Abstract:
A method for creating a material sheet with fibers includes the steps of feeding a layer of loose fibers to a conveyor; applying adhesive to the loose fibers, the adhesive being capable of mechanically bonding to the loose fibers; conveying the loose fibers and adhesive to a mold; and allowing the adhesive applied to the loose fibers to expand while containing the adhesive applied with the loose fibers in the mold in a manner to cause the adhesive to permeate throughout the fibers and to harden in a desired thickness.

Description:
BACKGROUND OF THE INVENTION 
       [0001]    This invention is in the field of solid materials handling, and relates to using material (for example, recycled material from discarded carpet segments) to create structural materials of various shapes and sizes. Preferably, the material is highly resistant to infiltration or damage by water and various chemicals and solvents. 
         [0002]    Various methods are known for converting recycled waste products containing nylon and other polymers into relatively narrow planks. Those recycled planks typically resemble single boards, and typically have widths only up to about 15 cm (6 inches) wide. Most manufacturing processes used to create such planks from recycled wastes require a relatively high level of melting of the nylon or other plastic material in the recycled feedstock mixture. Accordingly, such manufacturing processes require large amounts of energy, primarily to heat the recycled materials to their melting points. 
         [0003]    By contrast, prior to this invention, there have been few successful or widely accepted methods of converting nylon or other waste material into sheets with high strength, durability, high but non-brittle levels of hardness and rigidity, etc. A number of important and previously insurmountable obstacles apparently have prevented any such efforts from succeeding. Some of those obstacles can be summarized as follows. 
         [0004]    Prodigious amounts of energy are required to heat the bulk and volume of material that would be involved in large-scale manufacturing of wood substitutes, to the high temperatures that would be necessary in a manufacturing operation that requires extensive melting of recycled plastic or synthetic feedstock material. 
         [0005]    Even if the necessary “average” temperatures could be reached, non-uniform heating would lead to unacceptable fault lines, fracture zones, weak spots, and other flaws, when large sheets of hard material are being manufactured. If wood-like sheets are being created, those flaws would result in uneven strength, poor quality, and unreliability in ways that do not occur when narrow planks are created using melt-and-mold processes as used in the prior art. 
         [0006]    The problem of uneven heating (and resulting poor quality) is aggravated by the fact that when matted layers of fibers are heated, they respond in a manner directly comparable to thick woolen blankets. Fibrous mats are thermal insulators, and the type of thermal insulation they provide will thwart and frustrate any effort to establish the type of uniform and consistent heating that is required for a melt-and-mold manufacturing operation. 
         [0007]    Serious problems arise when attempts are made to mix different types and grades of discarded nylon, and/or various other types of recycled plastics. As one example, in recycling operations used to create narrow planks of wood-like materials, care must be taken to avoid mixing a form of nylon called “nylon-6” with a slightly different form of nylon called “nylon-6,6.” 
         [0008]    For these and other reasons, most prior efforts to create large sheets of wood-like material from discarded carpet segments (or other recycled textiles) by melting apparently have failed. A comparable item that is available for sale is a synthetic waterproof sheet, made from highly expensive materials such as never-before-used spun fiberglass, held together with large quantities of expensive adhesives. Such sheets are sold as premium waterproof construction materials, by companies such as Coosa Composites LLC (Pelham, Ala.), at prices which average about $125.00 (wholesale price) for a single sheet which is ½ inch thick, and which is the same size as a standard sheet of plywood (4 ft.×8 ft., or about 1.2 m×2.4 m). Conventionally, low levels of filler are used, whereas the present invention uses an average of 33% to 50% filler by weight, as will be discussed more fully below. 
         [0009]    There are some known forms of making large sheets of material without melting the nylon fibers. As discussed in U.S. Patent Application Publication No. 2004/0224589 A1, which is incorporated herein by reference, in one embodiment a continuous sheet of matted fibers can be sent through a needle-punching machine in order to create a needle-punched mat. The mats can then be layered with adhesive. Multiple mats can be layered together. The mats are then pressed together and kept compressed until the adhesive has cured and hardened enough to establish the final thickness. In another disclosed embodiment, nylon fibers blended with polyolefins, such as polypropylene (which is commonly used in carpet backing), are heated to a certain temperature causing only the polyolefins to melt, which causes the polyolefins to act as an adhesive. 
         [0010]    The results eventually achieved have shown that discarded carpet segments can be processed to create inexpensive but very strong sheets of wood-like construction materials, which have strength, durability, and handling traits (including the ability to withstand nails or screws near an edge without splitting or fracturing), which are comparable to wood, and in some respects substantially better than wood. In addition, since this material is made from nylon and other hydrophobic synthetic fibers, it is much more resistant than normal plywood to infiltration or damage by water. However, previously, the plywood-like materials were incapable of being made without either needle-punched mats or melting the nylon fibers. 
         [0011]    Synthetic v. Natural Fibers 
         [0012]    Nylon is the primary type of synthetic fibers discussed herein, because nylon tufting material is used in a large majority of carpets that use synthetic fibers. However, any references herein to “nylon” should be regarded as being merely exemplary of synthetic fibers as a class. Other types of synthetic fibers (such as polyethylene terephthalate, sold under the trademark DACRON, and polyacrylonitrile, sold under the trademark ORLON) also can be used to make wood-like materials, using the procedures described herein. 
         [0013]    The manufacturing operations described herein can be performed most economically, on a large commercial scale, if all of the fibers used are synthetic (i.e., are derived from petrochemicals or similar chemical feedstocks). However, a primary factor in this preference relates to explosion and flammability risks that arise when natural fibers (such as cotton, linen, etc.) are used. Additional concerns with the use of natural fibers are the inherent tendency to wick moisture and provide a food source for insects, mold, spores, and fungal microbials. Recycling and manufacturing plants designed for use with natural fibers must use special venting, air handling, dust control, and similar equipment, to minimize the risks of explosions or fires. 
         [0014]    Although such equipment can be installed in a recycling facility that handles both synthetic and natural materials, it is assumed for the present time that, at least in industrialized nations where large quantities of carpet are used and discarded, a shredding and manufacturing facility as described herein should limit its feedstock, so that it will only accept and work with synthetic fibers, such as discarded carpet segments, synthetic textiles, etc. In addition to helping reduce the risk of explosion or fire, this step can also help ensure that the wood-substitute materials manufactured in that facility will have high levels of resistance to water infiltration and damage, since cotton, linen, wool, rayon (which is derived from cellulose), and most other natural fibers tend to be more hydrophilic (water-attracting) than nylon, polypropylene, polyesters, and most other synthetic fibers. 
         [0015]    Since some natural fibers (such as wool and rayon) do not pose the same explosion and fire risks that are posed by cotton, the operators of any shredding and/or manufacturing facility can determine whether discarded materials made from any such material can be used safely as a suitable feedstock for that particular facility. 
         [0016]    Shredding Machines, Feedstocks, and Product Grades 
         [0017]    The process disclosed herein was initially developed and tested using carpet segments that had been shredded by a particular type of shredding system. That system, which uses a claw drum followed by two drums with abrading surfaces rotating at different speeds, is described in U.S. Pat. No. 5,897,066, which is incorporated herein by reference. 
         [0018]    The shredded material generated by that system provided excellent results in creating high-grade material sheets. However, it is anticipated that various other machines and/or methods for shredding discarded carpet segments (or other types of synthetic fibrous feedstocks) may also be suitable for use as described herein, for producing at least some grades of wood substitute materials. Many different types of processes are known for removing fibers from carpet backing, such as shaving, use of a hammermill machine, etc. 
         [0019]    Accordingly, specific methods of shredding or of post-shredding processing (such as the “opening” or “pulling” steps that are carried out by “Laroche” and garnett machines, described below) are not crucial to this invention. Any suitable shredding or opening machine or method can be used, if it will provide shredded and/or “opened” fibrous material that can be processed as described herein to generate a material sheet having acceptable quality for at least some types of uses. 
         [0020]    It also should be kept in mind that shredding operations that will be adequate for non-carpet textiles (such as clothing, drapes, bedsheets, etc.) are likely to be substantially easier (and less abrasive to the machinery involved) than carpet shredding operations. 
         [0021]    Accordingly, the output material from any type of shredding machine (or any other processing machine that is used after the initial shredding step, and before the needle-punching step), when performed on a particular type of carpet or other textile feedstock, can be evaluated as disclosed herein, using no more than routine experimentation, to determine whether that output material can be used to generate construction materials with acceptable consistency and reliability to satisfy the quality needs for a useful grade of construction material. 
         [0022]    If desired, carpet segments (or other recycled textiles) that are very dirty, greasy, or badly mildewed, or suffer from other problems can be processed by means of a washing process, using steam and/or other solvents; this can be followed by a drying process, if desired. 
         [0023]    It also should be noted that several types of feedstocks can be used, which are generated during carpet manufacturing operations but do not involve finished carpet. As one example, substantial quantities of “yarn waste” are generated by carpet manufacturers. This type of “yarn waste” is usually accumulated on large spools, for storage and handling. In a recycling facility, this yarn waste can be removed from the spools by an unwinding operation, or by a cutting operation. It can then be used as feedstock in the manufacturing operations described herein, using steps that can be adapted to the particular type and quality of the yarn waste being processed. As an example, yarn waste that has been removed from spools by a cutting operation, which will generate strands that typically range from about 1 to about 3 feet long, can be fed directly into the 3-cylinder shredder system described below; however, the material that emerges from that machine may not need to be passed through a “waste puller” machine (also called a “Laroche” machine) to further open up the fibers. 
         [0024]    Accordingly, the present invention can provide a practical and economical method of using discarded carpet segments or other textiles (preferably including only synthetic fibers) to make large sheets of material that are comparable to wood in terms of strength and weight, but which are more resistant than plywood or lumber to water infiltration and damage. 
         [0025]    The present invention can provide a more cost-effective way of producing sheets of material, by eliminating the preliminary step of needle-punching mats of fibers. 
         [0026]    The present invention can provide a practical and economical method of making a wood substitute of any desired size, from fibers, preferably from discarded carpet segments. 
         [0027]    The present invention can provide methods of making water-resistant wood substitutes in sheets which are highly resistant to cracking, and which will not lose strength if a crack forms on one side, or near an edge. 
         [0028]    The present invention can provide methods of making water-resistant wood substitutes in sheets of any desired size, with a range of density, hardness, insulating, and other traits, by controlling various manufacturing parameters that determine the final thickness, density, and hardness of the resulting material. 
         [0029]    The present invention can provide methods of making water-resistant wood substitutes in sheets which can be as large as desired, such as a single waterproof sheet large enough to form the entire deck of a large boat, or an entire roof or floor of a large truck trailer or recreational vehicle. 
         [0030]    The present invention can provide methods of making building materials which can substitute for wood, thereby eliminating the need to harvest trees to manufacture those materials. 
         [0031]    The present invention can provide a commercially feasible and economic method of reducing and even entirely eliminating the solid waste problem created by millions of tons of carpet segments and other discarded synthetic fabrics that are currently being sent to landfills every year. 
         [0032]    These and other features of the invention will become more apparent through the following summary, drawings, and description of the preferred embodiments. 
       SUMMARY OF THE INVENTION 
       [0033]    A method is disclosed for using discarded carpet segments or other recycled textiles (preferably made of nylon or other synthetic fibers) to make structural materials in large sheets that are comparable in some respects to, for example, plywood. The carpet segments or other recycled materials are shredded, and then layered transversely across a slow-moving conveyor system, to form a wide, thick, low-density belt of loose fibers. 
         [0034]    In one embodiment, loose fibers are fed to a conveyor belt and an adhesive capable of mechanically bonding to the loose fibers is poured onto the loose fibers. Then, the loose fibers mixed with the adhesive are conveyed to a mold. 
         [0035]    According to one aspect of the invention, a method for creating a material sheet with fibers comprises the steps of feeding a layer of loose fibers to a conveyor; applying adhesive to the loose fibers, the adhesive being capable of mechanically bonding to the loose fibers; conveying the loose fibers and adhesive to a mold; and allowing the adhesive applied to the loose fibers to expand while containing the adhesive applied with the loose fibers in the mold in a manner to cause the adhesive to permeate throughout the fibers and to harden in a desired thickness. 
         [0036]    According to another aspect of the invention, an article of manufacture suitable for use as a wood substitute comprises a sheet of composite material consisting essentially of an adhesive compound which has become bound to a layer of non-matted, loose fibers. 
         [0037]    According to another aspect of the invention, a system for creating a material sheet with fibers comprises a supplying system that supplies loose fibers; a conveyor system that conveys the loose fibers; an adhesive system that applies adhesive to the loose fibers; and a mold system that allows the adhesive applied to the loose fibers to expand while containing the adhesive applied with the loose fibers in the mold in a manner to cause the adhesive to permeate throughout the fibers and to harden in a desired thickness, wherein the supplying system supplies the loose fibers to the conveyor system to be conveyed to the adhesive system and then the mold system. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0038]      FIG. 1  illustrates the system of forming material sheets from loose fibers. 
           [0039]      FIG. 2  illustrates a side view of a supply hopper. 
           [0040]      FIG. 3  illustrates a gravity hopper with photoreceptive sensors. 
           [0041]      FIG. 4  is a flowchart for determining the level of the loose fibers in the gravity hopper. 
           [0042]      FIG. 5  illustrates an example bar conveyor. 
           [0043]      FIGS. 6   a  and  6   b  illustrate a front view and a side view, respectively, of a leveling rake assembly. 
           [0044]      FIGS. 7   a  and  7   b  illustrate a top view and a side view, respectively, of the static mix tube manifold for pouring adhesive. 
           [0045]      FIGS. 8   a  and  8   b  illustrate is a top view and a cross-sectional view, respectively, of the mold. 
           [0046]      FIG. 9  illustrates the controller system for controlling the various components of the entire system. 
           [0047]      FIGS. 10   a  and  10   b  are side views of the completed material sheet, with and without skins. 
       
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0048]    This invention relates to a method, apparatus and system of using shredded material from discarded carpet segments (or possibly other textiles) to make wood-like materials, in a variety of shapes and sizes. 
         [0049]    As used herein, terms such as “discarded” and “recycled” are used interchangeably. These terms refer to any type of fibrous material that is used as a feedstock in a manufacturing operation as described herein. Such materials include rolls or segments of carpet, as well as bales, piles, or any other aggregations of fabrics, textiles, or other fibrous materials. Such recycled material may be, or include, post-consumer material that has been discarded in a used and worn condition; alternately, it may be, or include, never-used material, such as material discarded because of imperfections, because it did not sell, because it became tailing or side-trim scrap, or for any other reason. Also, fibers may be made specifically for this application and need not come from any recycled material. 
         [0050]    The term “wood-like materials” describes output materials that are made from discarded or otherwise recycled carpet segments, or from other types of textiles, such as synthetic and natural fabrics, and include certain attributes of wood, such as rigidity, the ability to be machined, the ability to hold nails and screws, etc. 
         [0051]    As used herein, the term “sheet” is used to describe a manufactured item of any size. In this context, the term “sheet” implies that the manufactured item will be in a relatively flat, planar form, unless specific steps are taken to create a different shape. 
         [0052]    It should also be noted that in various settings, “oversized” sheets of seamless material can be very useful. As one example, various types of vans, recreational vehicles, buses, trucks and trailers, and other vehicles likely would be quieter, and less expensive to build, if the entire floor unit could be built on top of a single sheet of strong seamless material, especially if that material can provide an inherently high level of thermal and sound insulation. Additional advantages may arise from making the entire roof from a single sheet of seamless material, and/or from making one or more side or end walls from a single sheet of strong seamless material. 
         [0053]    As another example, various types of boats would be safer, stronger, and more seaworthy, if an entire deck or hull portion was made from a single sheet of seamless waterproof material. For example, complex shapes with multiple contours can be cast by a split mold, such as a clam shell concept, as long as either half of the mold does not prevent the ability to remove the casting from the mold. 
         [0054]    In addition, oversized sheets of material made as described herein could be highly useful in making “prefabricated” houses or other buildings. If an entire wall, or an entire floor segment, ceiling layer, or roof portion could be created from a single sheet of seamless material with inherent thermal and sound insulation, the cost savings and other benefits would be substantial. 
         [0055]    In discussing the potential advantages of the materials disclosed herein, it should also be noted that these materials are ideally suited for use with screws and nails, and with drills, saws, hammers, and other tools. Since they are made from a large number of strong fibers, rather than from a brittle, glass-like, or ceramic-type material, these materials will not shatter, crack, or split when a nail or screw is hammered or driven therethrough, even at a location very close to an edge. 
         [0056]    Indeed, in that respect, the materials disclosed herein can out-perform wood products in their ability to resist cracking and splitting. Due to the unique homogeneous closed cell construction, no laminations or grain patterns exist; therefore, damage inflicted on any particular area of the material is not transferred to surrounding areas by way of natural stress lines as would be experienced in wood or laminated products. 
         [0057]    In all of these respects, these materials appear to be able to far out-perform wood or plywood, in terms of strength and durability in response to high stress or other assaults. And, in addition to being highly tolerant of nails and screws, they offer good surfaces for painting, gluing, or other chemical coatings or bondings. Accordingly, in all respects, these materials appear to offer excellent and in many respects superior substitutes for wood, plywood, particleboard, planks, or other conventional construction materials. 
         [0058]    Material Composite Sheets Made with Adhesives 
         [0059]    In one preferred embodiment, material composite sheets can be made by using adhesives that will mechanically or chemically bond to loose synthetic fibers. In another embodiment, any type of loose fibers may be used. 
         [0060]    If certain types of adhesives discussed below are used, the combination of the loose fibers and the adhesive can create premium grade (or even super-premium) sheets which are highly resistant to water, salt water, and most solvents and other chemicals. These sheets can also be made with very high levels of hardness, durability, and other traits. Alternately, if different adhesives are used, they can create wood-like sheets that have different physical and/or performance traits, but which can nevertheless be useful and valuable as building materials. 
         [0061]    In one embodiment, a supply system  100  provides loose fibers to a conveyor system  200 , which conveys the loose fibers to an area where adhesive is poured on the loose fibers. The conveyor system  200  then continues to convey the loose fibers to a mold system  300  to form a sheet of material. The overview of the system is shown in  FIG. 1 . 
         [0062]    Supply System 
         [0063]    In the supply system  100 , shown in  FIG. 1 , fibers are stored in a conventional supply hopper  102 , blown via ducts  106  to a gravitational hopper  110 , and fed to a conveyor system  200  to have adhesive poured on the loose fibers. The supply hopper  102 , also known as a bale beater, may be a conventional mixing chamber provided by OBR Belmatex. Supply hoppers are known in the art; therefore, only a brief description thereof will be given. In a preferred embodiment, the loose fibers are provided from discarded carpet segments; however, the loose fibers may be any other synthetic or natural fibers. A side view of a simplified supply hopper  102  is shown in  FIG. 2 . The supply hopper  102  may include one or more rods  118  that rotate to create a more manageable loose material from bales of fibers placed in the supply hopper  102 . The rods  118  are placed horizontally through the supply hopper  102 . Bales of fibers are fed to a conveyor belt  103  in the supply hopper  102 . The conveyor belt  103  is shown merely as a flat surface for simplicity. The bales of fiber are then conveyed toward the one or more rods  118 . Even more preferably, rods  118  turn in opposite directions. The rods  118  generally have a row of six or more bars  119 . By the movement of the one or more rods  118  and the attached bars  119 , the bales of fibers are beat into loose fibers that are a manageable loose material to allow the loose fibers to more easily be blown by the blowers  104 . That is, the bars  119  act as an impact surface or stirring stick to break the compacted baled fiber into loose fibers. At least one armature motor  602  (not shown in  FIG. 2 ) is used to drive and rotate the one or more rods  118  in a circular manner. The armature motor  602  is controlled by a controller  600 , as will be discussed below. 
         [0064]    The supply hopper  102  contains a gate  112 , as shown in  FIG. 2 . At least one motor  604  is attached to the gate  112  to open and close it, depending on a signal sent from the controller  600 . The gate  112  is closed to keep the loose fibers in the supply hopper  102  or opened to allow the loose fibers to proceed to ducts  106 . The gate  112  is closed and the ducts  106  are cleared prior to shutting down the whole assembly so as to prevent stalling during a restart of the assembly. The gate  112  may consist of a conveyor system with moving rollers to move the fibers to an exit  116  to pneumatic blowers  104 , as shown in  FIG. 2 . As shown in  FIG. 2 , the loose fibers, once beaten by the rods  118 , are conveyed to the gate  112 . The fibers are conveyed up a conveyor belt which has attached bars, or an equivalent structure (not shown), to grasp and lift the fibers up through the rollers of the gate  112  and down to the exit  116 . 
         [0065]    Attached to the supply hopper  102  is a transportation system to transport the loose fibers from the supply hopper  102  to the gravitational hopper  110 . The transportation system consists of the gate  112 , at least one but preferably two or more ducts  106 , and pneumatic blowers  104 . Plural ducts  106  allow the loose fibers to be more evenly distributed in the gravitational hopper  110 , which will, in turn, help the flow of the system. The loose fibers are fed directly into the pneumatic blowers  104 , which may be squirrel cages, or centrifugal blowers, for example. However, any type of blowers  104  may be used to transport the loose fibers from the supply hopper  102  to the gravitational hopper  110  via ducts  106 . When the loose fibers pass through the blowers  104 , the blowers  104  move the loose fibers in an air stream through the ducts  106  to the gravitational hopper  110 . The blowers  104  are controlled by a signal sent from a controller  600 , as will be discussed more fully below. 
         [0066]    Referring to  FIG. 1 , the gravitational hopper  110  acts as a vertical hold station for the loose fibers blown by the blowers  104 . An exhaust stack  108  is provided at the top of the gravitational hopper  110  to allow gravitational separation of air and the loose fibers. This allows the air stream to exhaust and the loose fibers to accumulate at the bottom of the gravitational hopper  110 . The air is filtered and ducted harmlessly away from the process line while the loose fibers, with the assistance of both air pressure from the ducts  106  and gravitational force, drop into the gravitational hopper  110  to be further processed. In one embodiment, the gravitational hopper  110  is 8.2 feet wide, 1 foot across and 12 feet high. However, the gravitational hopper  110  may be any size necessary to store the loose fibers and provide a steady supply of loose fibers during the manufacturing process. The gravitational hopper  110  also may contain photoreceptive sensors  114 , as shown in  FIG. 3 , in order to sense the level of the loose fibers in the gravitational hopper  110 . The photoreceptive sensors  114  may be installed in several locations in the gravitational hopper  110 , as shown in  FIG. 3 . 
         [0067]    As shown in the flowchart in  FIG. 4 , if the photoreceptive sensors  114  indicate that the amount of loose fibers in the gravitational hopper  110  is below a minimal level, the controller  600  will then open the gate  112  in supply hopper  102  and turn on the pneumatic blowers  104  so that the loose fibers will be blown by the pneumatic blowers  104  through the ducts  106  to the gravitational hopper  110 . If the photoreceptive sensors  114  indicate that the amount of loose fiber in the gravitational hopper  110  is at a mid-level, the controller  600  will close the gate  112 . Once the photoreceptive sensors  114  indicate that the amount of material in the gravitational hopper  110  has reached the maximum level, the controller  600  will then turn off the pneumatic blowers  104 . By delaying the shut off of the blowers  104  after the gate  112  is closed, most of the loose fibers can be cleared from the ducts  106  to prevent clogging during the next start up. 
         [0068]    Conveyor System 
         [0069]    The loose fibers in the gravitational hopper  110  are fed to the conveyor system  200  by gravity. The conveyor system  200  conveys the loose fibers from the gravitational hopper  110  to a mold system  300 . The conveyor system  200  helps maintain the continuous flow of the loose fibers from the gravitational hopper  110  to the mold system  300 . 
         [0070]    The conveyor system  200  includes, at the bottom of the gravitational hopper  110 , a short length, full width bar conveyor  202 , as shown in  FIG. 1  and in more detail in  FIG. 5 . The bar conveyor  202  is a conveyor belt  204  with a variety of bars  205  attached perpendicular to the transport direction of the belt. The bars  205  can be made from any material. For example, the bars  205  can be made out of the sheets produced as disclosed in this application. The height of the bars  205  on the bar conveyor  202  may be adjusted according to the desired density of the loose fibers to be supplied to a pour table  208 . The higher the desired density of the loose fibers, the more loose fibers that must be conveyed onto the pour table  208  per a given area. Therefore, the bar height of the bar conveyor  202  will be higher. The height of the bars  205  is changed by replacing the current set of bars  205  on the bar conveyor  202  with a different set of bars of a different height. The bars  205  may be slideably removed and inserted onto the bar conveyor  202 . 
         [0071]    As shown in  FIG. 5 , the bars  205  of the bar conveyor  202  are formed in an “L” shape. One portion of the “L” sits on the conveyor belt  204  and the other portion is perpendicular to the conveyor belt  204 . This “L” shape creates a tray for the fibers to be received from the gravitational hopper  110 . The smaller the height of the bars  205 , the less space there is available for the loose fibers in the tray. Therefore, the density of the loose fibers conveyed to the pour table  208  will be less. As the conveyor belt  204  rotates, via gears  203   a  and  203   b , the trays dump the loose fibers stored in the trays on to the pour table  208 . 
         [0072]    The speed of the bar conveyor  202  is also adjusted according to the bar  205  height and the required density of the loose fibers on the pour table  208  at a given area. At least one motor  606  is attached to the gears  203   a  and  203   b  to rotate the bar conveyor  202 . The controller  600 , as will be discussed more fully below, controls the speed of the bar conveyor  202 . The higher the density of the loose fibers needed, the slower the bar conveyor  202  will rotate to accommodate filling the more voluminous trays created by the bars  205  of the bar conveyor  202 . 
         [0073]    The bar conveyor  202  conveys the loose fibers to the pour table  208 . The pour table  208  is a conveyor belt, driven by at least one motor  608 , to convey the loose fibers to an area where adhesive is poured on the loose fibers and further to the mold system  300 . After the loose fibers are conveyed to the pour table  208 , a leveling rake  206 , shown in  FIGS. 6   a  and  6   b , levels the loose fibers before entering the mold. The leveling rake  206  may be a two bar reciprocating rake. At least one motor  610  is attached to drive the leveling rake  206 . The two bars  207 ,  209  of the two bar reciprocating rake  206  are connected to linear bearings and move in a linear motion back and forth relative to each other via motor  610 . This causes the blades  211  attached to the two bars  207 ,  209  of the two bar reciprocating rake  206  to drag across the loose fibers on the pour table  208  in order to level the loose fibers. The speed of the pour table motor  608  and the leveling rake motor  610  are coordinated. The controller  600  will control the speed of both motors so that the speed of the pour table  208  is tied to the speed of the leveling rake  206 . The height of the leveling rake  206  can be adjusted by hand or automatically, for example, to accommodate different densities of fibers needed on the pour table  208 . If done automatically, the controller  600  will determine the necessary height of the leveling rake  206  and a motor  611  will be attached to adjust the height of the leveling rake  206  based on a signal from the controller  600 . If the density of the loose fibers is to be higher, then the height of the leveling rake  206  can be raised to level the loose fibers. If the density of the loose fibers is to be lower, then the leveling rake  206  can be lowered to level the loose fibers. Although the leveling rake  206  has been described as a two bar reciprocrating rake, the leveling rake  206  is not limited to this configuration. The leveling rake  206  may be any device, such as a rotational device, for metering the loose fibers. 
         [0074]    Adhesive Application System 
         [0075]    Once the loose fibers have been leveled by the leveling rake  206 , the loose fibers continue to be conveyed by the pour table  208  toward the mold system  300 . Prior to entering the mold system  300 , an adhesive is added to the loose fibers. 
         [0076]    In a preferred embodiment, the adhesive is poured on the loose fibers via static mix tube manifold  212  shown in  FIGS. 7   a  and  7   b . The adhesive is stored in a storage container and is poured onto the loose fibers by at least one nozzle  210 . The static mix tube manifold  212  preferably includes a plurality of nozzles  210 , as shown in  FIG. 7   b , and is preferably formed into a “V” shape to create a “V” pattern for pouring the adhesive onto the loose fibers, as shown in  FIG. 7   a . The adhesive is poured onto the loose fibers located on the pour table  208  at a rate to create a defined level of the adhesive as it is poured. Therefore, the layer of adhesive poured will have a certain height. Calculating the necessary height of the adhesive will be discussed later. 
         [0077]    The “V” pattern allows the adhesive to be contacted in the middle of the loose fibers on the pour table  208  first before entering the mold. This also allows the adhesive to be poured onto the center of the loose fibers at a different time from when the adhesive is poured on either side of the center. Preferably, the wide portion of the “V” pattern would be poured closest to the mold, when moving in the process direction, as shown in  FIG. 7   a . This allows the point of the “V” to begin pouring adhesive on the loose fiber first. 
         [0078]    When the center of the “V” pattern is upstream in the conveying direction of the fibers, the adhesive is poured in the center of the loose fibers first, so the adhesive in the center will begin to react within the central loose fibers before the adhesive immediately adjacent the center. This allows the adhesive to foam and expand from the center of the loose fibers and push the air from the middle of the loose fibers toward the outside of the loose fibers as the adhesive begins to react away from the center. This creates a timing difference between when the adhesive at the center of the loose fibers will be cured compared to the outside. The removal of the air from the center outward as the material is forming helps eliminate voids caused by air or gases between the exteriors of the material sheet. However, any pour shape may be used to pour the adhesive onto the loose fibers. For example, the point of the “V” pattern may also be poured closest to the mold, or the nozzles may be laid out in a straight line rather than a “V” pattern. 
         [0079]    It is believed that a foaming reaction of the adhesive, which occurs when a layer of the adhesive is poured on the loose fibers, will substantially increase two very useful processes: (i) permeation and penetration of the adhesive into the loose fibers, and (ii) intimate contact and tight mechanical or chemical bonding between the adhesive and the loose fibers. Accordingly, foaming adhesives can enable and promote the manufacture of large sheets that have high levels of uniformity, consistency, and strength, in which any weak spots or fracture zones will be minimized or eliminated, to an extent that cannot be achieved in the absence of a foaming reaction, even when high pressure is applied. 
         [0080]    In a preferred embodiment, a foaming mixture of isocyanate and polyol (hereinafter polyurethane foam) is used as the adhesive. Polyurethane foam has an inherent bonding affinity for nylon. This allows for materials that are exceptionally hard, strong, and durable. 
         [0081]    Mold System 
         [0082]    After the adhesive has been poured on the loose fibers, the pour table  208  conveys the loose fibers mixed with the adhesive to the mold system  300 . Prior to entering the mold, a mechanical assist  304  may be provided to assist with pre-compression of the loose fibers mixed with the adhesive. As discussed above, the adhesive is added immediately prior to entering the mechanical assist  304 . The mechanical assist  304  is designed to provide 100% compression of the loose fibers and adhesive, substantially eliminating air in the mixture prior to entering the mold, as further described below. The mechanical assist  304  will compress the loose fibers mixed with the adhesive to a desired thickness of the material sheet so that the loose fibers mixed with adhesive maintain their shape in the mold  316  as the adhesive is cured to the desired hardness. The mechanical assist  304  may comprise a belt  304   c , as shown in  FIG. 1 , or a release film, discussed more fully below, may act as the belt for the mechanical assist  304 . The mechanical assist  304  also comprises rollers  304   a  and  304   b  to guide the belt  304   c . The mechanical assist  304  may also contain additional guide rollers  304   d  shown in  FIG. 1 . 
         [0083]    The gauge of the mechanical assist  304  is adjustable to produce a variety of sizes of the material. The gauge may be calculated by the total volumetric mass cross-section of all the solids and liquids entering the mechanical assist  304 . Depending on the calculations, the gauge is adjusted through the mold  316 , discussed more fully below, by either lifting the mechanical assist  304  to accommodate a higher gauge or by lowering the mechanical assist  304  to accommodate a lower gauge. Alternatively, the loose fibers poured with adhesive may enter the mold  316  without first going through a mechanical assist  304 . 
         [0084]    Typically, boards are produced with a pound per cubic foot (PCF) density in the range of 20 PCF to 50 PCF, for example. Then, it must be determined what thickness is desired for the board (generally ¼″, ⅜″, ½″, ⅞″, 1″ and 1¼″). Further, as discussed below, skins may be added to meet other structural requirements of the boards. Pounds per square foot of the board is determined by taking the PCF and dividing it by the desired thickness. The height of the total of the loose fibers, skins and adhesive can be determined from the weight per cubic foot and the rate of application. Then, the mechanical assist  304  will be set to this height to allow only the loose fibers, skins and adhesive to pass under the mechanical assist  304  to remove air. The percent of loose fibers by weight is averaged between 33% to 50%, for example. 
         [0085]    The mold  316  comprises a set of steel belts  302 ,  303 , as shown in  FIG. 1 . Each steel belt  302 ,  303  is fitted around at least two rollers  314   a ,  314   b . Each steel belt  302 ,  303  is moved by the rollers  314   a ,  314   b , which are driven by at least one motor  612  and controlled by the controller  600 . 
         [0086]    A set of containment belts  318   a ,  318   b  are fitted around steel belt  302 . The containment belts fit around the length of the steel belt, but also incorporate part of the mechanical assist  304 , as shown in  FIGS. 1 ,  8   a , and  8   b .  FIGS. 8   a  and  8   b  are not drawn to scale for simplicity purposes. One containment belt  318   a  is fitted at one outer edge of the steel belt  302  and the other containment belt  318   b  is fitted at the other outer edge of the steel belt  302 . If a mechanical assist  304  is provided, each containment belt is also fitted around part of the mechanical assist  304 . As discussed above, the mechanical assist  304  helps provide compression of the loose fibers poured with adhesive prior to entering the mold. The containment belts  318  are preferably made of hybrid polyurea.  FIG. 8   a  shows a top view of the steel belt  302  with the containment belts  318   a ,  318   b . As can be seen in  FIG. 8   a , a containment belt  318   a ,  318   b  is located on each of the outer edges of the steel belt  302 . Further, the front end portions of the containment belts  318   a ,  318   b  wrap around the roller  304   a , with the mechanical assist belt  304   c  in between the containment belts  318   a ,  318   b . The containment belts  318   a ,  318   b , however, are not limited to being located around steel belt  302 . In an alternative arrangement, the containment belts  318   a ,  318   b  may be located around steel belt  303 . 
         [0087]    The loose fibers poured with adhesive are conveyed through the mold  316 . As the loose fibers are conveyed through the mold  316 , the adhesive chemically reacts and expands within the loose fibers, forming the material sheet. The steel belts  302 ,  303  of the mold  316  convey the loose fibers mixed with the adhesive through the mold  316  while the adhesive is cured. The steel belts  302 ,  303  limit the expansion of the adhesive in the vertical direction, while the containment belts  318  limit the expansion of the adhesive in the horizontal direction, thereby creating pressure within the mold  316 . This can be seen in  FIG. 8   b , which is cross-section at section line B-B of  FIG. 8   a  of the mold  316 .  FIG. 8   b  shows the steel belts  302 ,  303  and the containment belts  318   a ,  318   b . The containment belts  318   a ,  318   b  encase the sides of the loose fibers poured with adhesive  319 , while the steel belts  302 ,  303  encase the top portion of the loose fibers poured with adhesive  319 . 
         [0088]    In one embodiment, the steel belt  302  has vents located at set distances, for example, approximately every six inches. However, the vents may be any desired distance apart. The vents allow the air or gas that is pushed out from the loose fibers, as discussed above, to exhaust as the material sheet is being formed. 
         [0089]    In one embodiment, the containment belts  318   a ,  318   b  are belt segments attached end to end by a chain-like joint. Therefore, each containment belt is formed of a plurality of belt segments. These belt segments allow for easy placement of the mechanical assist  304  gauge. During a gauge adjustment, the mold can be stopped and the nearest belt segment of the containment belts  318   a ,  318   b  may be opened so that the gauge of the mechanical assist  304  can be adjusted. Further, the mold is set to be at a height to allow the fibers to expand slightly beyond the desired thickness of the board. This will allow the board to be sanded down to the desired thickness, as will be discussed more fully below in the example. 
         [0090]    In a preferred embodiment, the containment belts  318   a ,  318   b  should be separated by a distance slightly greater than the desired width of the material sheet being produced so as to contain the material, but not unduly restrict the mold space. The use of belt segments, discussed above, allow for easy replacement of the containment belts  318  if the size needs to be changed. Therefore, the containment belts  318  can easily be changed segment by segment, rather than having to replace the containment belts  318  as a whole. 
         [0091]    As shown in  FIG. 1 , the mold system  300  further includes at least one roller, preferably two,  307   a ,  307   b , which store release film and/or paper (hereinafter referred to as release film  306 ). The rollers  307   a ,  307   b  that store the release film  306  have at least one motor  614  attached to rotate the roller. The release film  306  is preferably made of polyethylene. The release film  306  protects the material sheet from potentially sticking to the steel belts  302  after being formed. Preferably, the release film  306  is provided on a roller  307   a  below the loose fibers and on a roller  307   b  above the loose fibers poured with adhesive. This will allow the release film  306  to be located on both sides of the loose fiber. As shown in  FIG. 1 , the release film  306  is wound around the pour table  208  so that the fibers are conveyed directly onto the release film  306  on the pour table  208  (unless a lower skin is used, as discussed below.) Further, if release film  306  is provided on a roller  307   b  above the loose fibers, the release film  306  is wound around the mechanical assist  304  and is provided above the loose fibers after they have been poured with adhesive. The release film allows the product to cleanly release from the belts  302 . 
         [0092]    The release film  306  is preferably a reusable type of release film. After the release film  306  is fed through and exits the mold, the release film  306  originally fed from roller  307   a  will be wound around roller  310   a , and the release file  306  originally fed from roller  307   b  will be wound around roller  310   b , as shown in  FIG. 1 , to be used again. The rollers  310   a ,  310   b  will be provided with at least one motor  618  to help with the rewinding of the release paper. The release film  306 , for example, is preferably a film of high density polyethylene. 
         [0093]    Further, as shown in  FIG. 1 , the mold system  300  may also include at least one roller, preferably two,  309   a ,  309   b  which may store a skin  308 . As shown in  FIG. 1 , one roller  309   a  will feed the skin  308  so that the release film  306  is below the skin, and the loose fibers are poured onto the skin  308 . The other roller  309   b  will feed the skin  308  around the release film  306 , which is wound around the mechanical assist  304 , to be located on top of the loose fibers and below the release film  306 . The skins  308  provide further structural support for the material sheets and will be chosen based on the desired properties of the material sheet. Each of the rollers  309   a ,  309   b  will be controlled by a motor  616  connected to the controller  600 . 
         [0094]    As will be understood by one of ordinary skill in the art, a single skin  308  may be provided below the fibers with release film  306  provided above the fibers. Further, multiple skins  308  may be provided on a variety of rollers. As will be understood by one of ordinary skill in the art, a variety of combinations may be made between the release film  306  and the skins  308  provided to form the material sheet. 
         [0095]    The skins  308  can be a porous technical fabric. After the skin is laid on or below the loose fibers, the adhesive will expand through the pores of the skin  308 . The skin  308  is then embedded in the adhesive on top of the loose fibers. If multiple skins  308  are used, the adhesive will expand through the pores of all of the skins  308 . The skins  308  will then be embedded in the adhesive, layered on top of the loose fibers. Refer, for example, to  FIGS. 10   a  and  10   b , which show the layers of various types of boards.  FIG. 10   a  shows a sheet formed with loose fibers and adhesive, without a skin.  FIG. 10   b  shows a material sheet formed with multiple layers of skins  308  and loose fibers embedded in the adhesive. 
         [0096]    The skins  308  may include, but are not limited to, for example, E-glass veil skin, woven E-glass roven skin, carbon fiber technical skins, Kevlar, Nomex fire retardant skin, non-woven E-glass roven skin, embossed wood grain skin, polyester cloth, cotton cloth, polypropylene veil mesh, aluminum screen, nylon mesh, paper, tissue paper, blast resilient skin, and fragmentation resistant skin. Any skin may be used that is formed of an inert, fibrous and porous material, for example. 
         [0097]    For example,  FIG. 10   a  shows a material sheet formed out of loose fibers mixed with adhesive  902 .  FIG. 10   b  shows a material sheet formed with loose fibers mixed with adhesive  902 , with a layer of non-woven E-glass Roven  904  in the adhesive and a layer of E-glass veil  906  in the adhesive. 
         [0098]    Controller System 
         [0099]    As discussed above, the system is provided with at least one controller  600 ; however, as understood by one of ordinary of skill in the art, multiple controllers  600  that interact with each other may be provided. As shown in  FIG. 9 , the controller  600  controls the various aspects of the system as a whole. The controller can be a suitably programmed microprocessor. 
         [0100]    For example, the controller  600  receives signals from the photosensitive sensors  114  located in the gravitational hopper  110 . Depending on the signals received, the controller  600  controls the gate  112  of the supply hopper  102  and blowers  104 . The controller also controls the speed of the rods  118  to beat the material into manageable loose fibers. 
         [0101]    The controller  600  will control the speed of the bar conveyor  202  depending on the speed needed for the bar conveyor  202  to produce the desired density. The controller  600  will also control the speed of the leveling rake  206  to be tied to the speed of the pour table  208 . 
         [0102]    As shown in  FIG. 9  the controller  600  will provide signals to the motors associated with the various rollers, to move the rollers in a way to allow smooth operation of the loose fibers moving through the mold and applying the skin  308  and/or release film  306  to the loose fibers. The controller  600  will operate the various components of the system to run in unison. 
         [0103]    All of the components of the system, including, for example, motors, conveyor belts, chemical flow rate valves, etc., are program controlled based on sensor and/or operator inputs. This level of automation allows the sequencing of events to avoid process stalls as well as product consistency. The controller  600  is connected to a control panel for an operator to input the desired commands for running the entire system. 
       Example 
       [0104]    In one example, to make a ½ in. thick material sheet, the desired total weight of the board, which is identified as pounds per cubic foot (PCF), must first be determined. To make a 40 PCF, ½ in. material sheet with fiberglass technical fabric for a skin, 1.2948 pounds of adhesive per square foot must be added to the loose fibers and skin to meet the necessary design criteria. This is determined by calculating the total weight per square foot of solid materials and subtracting the total from the desired total weight of the board, which would be 1.667 pounds per square foot (which is determined by converting 40 PCF for a ½ in. material sheet to pounds per square foot). If the fiberglass technical fabric weighs 24 ounces per square yard, the loose fibers weigh 26 ounces per square yard, and an exterior E-glass veil weighs 3.6 ounces per square yard, adding to 53.6 ounces per square yard, or 0.3722 pounds per square foot, this leaves the abovementioned 1.2948 pounds of adhesive per square foot out of the total 1.667 pounds per square foot of the desired weight of the board. 
         [0105]    In one example, to make a ½ in. material sheet, fibers will be fed from the gravitational hopper  110  to the bars on the bar conveyor  202 . The bars on the bar conveyor  202  will be set to an appropriate height. The speed of the bar conveyor  202  will be set by the controller  600  to allow the area between the bars to fill with loose fibers. The bar conveyor  202  will then convey the loose fibers onto the release film  306  located on the pour table  208 . 
         [0106]    To determine the height of the bar conveyor  202 , during the design of a particular board the required weight per square foot of recycled material must be determined. For an example, 100 ounces per square yard converted to 0.6944 pounds per square foot of process board is used. Since each supplier or run of recycled material may be different in its specific gravity or volumetric density, lab tests should be run on raw material samples to determine volumetric density. In this example, loosely packed raw fiber has a density of four pounds per cubic foot. Therefore, the required height of the application of fiber would be 0.1736 feet or 2.0832 inches. At a mold  316  speed set for 10 feet per minute and a board width of 8.5 feet, the bar conveyor speed is set to 10 feet per minute as well. The height of the bar conveyor  202  would then be set for 2.0832 inches. However, if the bar conveyor  202  speed is set to 20 feet per minute, and the mold  316  speed remains at 10 feet per minute, the bar conveyor  202  height would be adjusted to be 1.0416 inches. Further, adjustments to metering can be made by slight adjustments to the bar conveyor speed by adjusting the motor  606 . 
         [0107]    Then, the leveling rake  206  will be adjusted to level the top of the loose fibers as the loose fibers are conveyed onto the release film  306  on the pour table  208 . The loose fibers will be leveled to be 0.1805 pounds per square foot. The necessary height of the mechanical assist  304  is calculated by determining the height of the loose fibers, skins and adhesives entering the mold  316 . In this example, E-Glass weighs 153.9 lbs per cubic foot applied at a rate of 27.6 ounces per yard (27.6 ounces per yard=0.19167 pounds per square foot). The area is then divided by the weight to determine the height, which is 0.0012454 feet, which equals 0.014945 inches. The same calculation is done for the recycled carpet fiber weighing 73.9 lbs per cubic foot applied at a rate of 26 ounces per yard, which result in a height of 0.029309 inches. 
         [0108]    To calculate the height of the layer of adhesive, a specific gravity of the polyurethane foam is used, with a standard formulation of 1.1. A specific gravity of any element is referenced from the specific gravity of water (1.0 at standard temperature and pressure). A specific gravity of 1.0 equates to 62.38737 pounds per cubic food (8.34 pounds per gallon), and accordingly, a specific gravity of 1.1 equates to 68.627 pounds per cubic foot. The weight of the adhesive, 1.2898 pounds, calculated above, is divided by 68.627 pounds per cubic foot for a layer height of 0.22548 inches. Accordingly, the mechanical assist  304  is set at a height of approximately 0.269734 inches, which is determined by adding the height of the loose fibers (0.029309 inches), the E-glass (0.014945 inches), and the adhesive (0.22548 inches). 
         [0109]    In the mold, the adhesive saturates throughout the loose fibers and the applied skin. The height of the mold  316  can be set to be slightly greater than the desired ½ inch material sheet, for example 0.533 inches, to allow for excess material to be sanded, making the material sheet a desired thickness. The adhesive will then expand beyond the loose fibers and the skin as it cures. In this example, the thickness of the adhesive above the skin material averages 0.030 of an inch per side. This allows the adhesive to provide a clear area to sand without sanding into the structural composite. 
         [0110]    Once the material sheets are formed in the mold, they are conveyed to an output  312 . The material sheet is then preferably cured for a minimum of 24 hours prior to a sanding or finishing of the surfaces of the material sheet. The material sheets can then be sanded to the desired thickness and ripped with appropriate sawing equipment to desired shapes and sizes. 
         [0111]    Thus, there has been shown and described a new and useful system for creating material sheets, using loose fibers from carpet or other textiles. Although this invention has been exemplified for purposes of illustration and description by reference to certain specific embodiments, it will be apparent to those skilled in the art that various modifications, alterations, and equivalents of the illustrated examples are possible.