Abstract:
Dry emulsions comprising less than 20% wt water, at least 50% wt of a particulate, water-insoluble polysaccharide having a mean particle size of less than 3 microns and at least 30% wt of hydrophobic oil have improved properties including redispersibility.

Description:
TECHNICAL FIELD  
       [0001]     The present invention concerns improvements relating to emulsions, and in particular to dry emulsions which can be re-dispersed in water.  
       BACKGROUND OF THE INVENTION  
       [0002]     Emulsions are often thermodynamically unstable. They exhibit all classical behaviours of metastable colloids including reversible as well as irreversible transitions that can lead to their destruction. Given that many applications in industry involve the use of emulsions, efforts have been dedicated to avoid or at least minimise the destabilising forces mentioned above.  
         [0003]     Drying the emulsions is one of the alternatives available to extend their effective lifetime. For example in oil-in-water emulsions (‘o/w’ emulsions) the continuous water phase can be removed from the original emulsion by a suitable thermal and/or mechanical processes. Meanwhile, the other component of the emulsion, the dispersed oil phase, is usually encapsulated with a protecting shell or barrier that hampers their coalescence. The main requirement for a successful emulsion-drying operation is that the resulting material can be restored to the emulsified state on contact with water.  
         [0004]     Spray drying is a known process for drying o/w emulsions, although other drying processes are also available. It is known to protect the oil droplets in a dried emulsion with a shell composed of a water-soluble material that becomes insoluble once the water removal starts. Some examples of such materials are gelatine, glycine, casein, maltodextrin, sucrose, and water-soluble polymers such as polyvinyl alcohol and polyvinyl pyrrolidone. Examples of such processes can be found in Frensch et al. U.S. Pat. No. 4,244,836.  
         [0005]     Although effective, the use of only water-soluble compounds as the sole component of the shell limits the encapsulation process. For instance, some of the materials mentioned above are heat-sensitive and become unstable at the temperatures usually encountered in spray drying (e.g. inlet temperatures of 250-280° C.).  
         [0006]     Some authors have recognised this drawback and suggested applications involving the addition of insoluble materials to help form a matrix that encapsulates the oil droplets during and after the drying stage. In most cases the insoluble, matrix-forming component was colloidal silica. Mixtures of soluble polymer (e.g., polyvinyl alcohol) and insoluble particulate material selected from clays (e.g., attapulgite, kaolin, and montmorillonite) or silicas (precipitated or fumed) are mentioned in WO 96/01048 as a way to reinforce the encapsulating wall.  
         [0007]     In another example (WO 97/15617) high concentrations of a surfactant known to form a liquid crystal phase is used as a solid support in combination with a film-forming polymer.  
         [0008]     These materials are part of a parent emulsion, which after drying produces a water-redispersible polymer composition.  
       BRIEF DESCRIPTION OF THE INVENTION  
       [0009]     We have determined that improved emulsions can be manufactured by using specific ranges of water, oil and a water insoluble polysaccharide of a particular particle size range.  
         [0010]     Accordingly the present invention provides a dry emulsion comprising less than 20% wt water, at least 50% wt of a particulate, water-insoluble polysaccharide having a mean particle size of less than 3 microns and at least 30% wt of hydrophobic oil.  
         [0011]     Typically, emulsions according to the invention comprise:  
         [0000]     a) 5-15% wt water,  
         [0000]     b) 50-60% wt polysaccharide,  
         [0000]     c) 30-40% wt hydrophobic oil.  
         [0012]     Preferably, the polysaccharide is selected from the group comprising: amaranth starch, hydrolysed amaranth starch, waxy maize hydrolysate, nano-particulate native starch, and mixtures thereof.  
         [0013]     Some starches have a large particle size and contain soluble sugars such as amylose. They may be rendered suitable for use in the present invention by hydrolysis under suitable conditions of pH and temperature to reduce the particle size and remove amylose.  
         [0014]     Preferably, the hydrophobic oil is selected from the group comprising, hydrocarbons, silicone oils, lipids, and mixtures thereof. More preferably, the hydrophobic oil comprises a mono- or di-ester of a polyol. Most preferably, the hydrophobic oil comprises a glyceride, an ester of a dimethicone copolyol, or a mixture thereof. Preferably, the hydrophobic oil comprises a perfume ingredient.  
         [0015]     Oily components are of particular interest when the dried emulsion is incorporated in a washing, cleaning or laundering product, as many of the oily components discussed above have important functional properties in these classes of product.  
         [0016]     It is advantageous that compositions according to the invention comprise a soluble binder. Preferably, the binder is selected from the group comprising a peptide, a sugar and mixtures thereof.  
         [0017]     A preferred embodiment of the invention provides a dry emulsion, which comprises:  
         [0000]     a) 5-15% wt water,  
         [0000]     b) 50-60% wt of a starch having a particle size less than 2 micron, and  
         [0000]     c) 30-40% wt of a glyceride and/or an ester of a silicone polymer.  
         [0018]     Preferred compositions are those which, at water contents of 9% wt, have no glass transition temperature between 100-150 Celsius, more preferably 100-180 Celsius.  
         [0019]     The invention also provides a method for the manufacture of a dry emulsion, which comprises the steps of:  
         [0000]     a) providing a dispersion of the insoluble polysaccharide in water,  
         [0000]     b) forming an emulsion of said dispersion and the hydrophobic oil,  
         [0000]     c) drying said emulsion to a water level of less than 20% water.  
         [0020]     Preferably step (b) comprises use of a rotary mixer. A turbine-type impeller having a 2-4 cm rotor operating at 1200 to 1600 rpm is suitable for small scale manufacture.  
         [0021]     Preferably the emulsion formed in step (b) comprises 0.5-2% wt of insoluble ‘solids’ (i.e. oil and polysaccharide). The preferred weight ratio of oil to polysaccharide in this parent emulsion is such that 40-50% wt of the total solids is oil and 50-60% wt is polysaccharide.  
         [0022]     Preferably, step (c) comprises spray drying. Typical inlet temperatures for the spray head are 120 to 250 Celsius.  
         [0023]     The drying step preferably reduces the water content of the feed emulsion from greater than 95% to less than 20%, preferably less than 15% wt and most preferably 12% wt or less.  
         [0024]     In a further aspect, the invention provides an emulsion obtainable by dispersion of the dried emulsion described herein in water. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0025]     Various preferred and/or optional features of the product and method aspects of the present invention are described in further detail below. As used elsewhere in the specification all percentages are percentages by weight unless the context demands otherwise.  
         [0026]     Typically finished compositions, as well as the dried emulsion, will further comprise on or more of surfactant, builder, textile softener and/or conditioner and other optional components found in laundry compositions.  
         [0000]     Surfactants:  
         [0027]     The surfactant may be chosen from soap and non-soap anionic, cationic, nonionic, amphoteric and zwitterionic detergent active compounds, and mixtures thereof.  
         [0028]     Many suitable surfactants are available and are fully described in the literature, for example, in “Surface-Active Agents and Detergents”, Volumes I and II, by. Schwartz, Perry and Berch (published by Interscience).  
         [0029]     The preferred surfactants that can be used are soaps and synthetic non-soap anionic and nonionic compounds.  
         [0030]     Anionic surfactants are well-known to those skilled in the art. Examples include alkylbenzene sulphonates, particularly linear alkylbenzene sulphonates having an alkyl chain length of C 8 -C 15 ; primary and secondary alkylsulphates, particularly C 8 -C 15  primary alkyl sulphates; alkyl ether sulphates; olefin sulphonates; alkyl xylene sulphonates; dialkyl sulphosuccinates; and fatty acid ester sulphonates. Sodium salts are generally preferred.  
         [0031]     Nonionic surfactants that may be used include the primary and secondary alcohol ethoxylates, especially the C 8 -C 20  aliphatic alcohols ethoxylated with an average of from 1 to 20 moles of ethylene oxide per mole of alcohol, and more especially the C 10 -C 15  primary and secondary aliphatic alcohols ethoxylated with an average of from 1 to 10 moles of ethylene oxide per mole of alcohol. Suitable non-ethoxylated nonionic surfactants include alkylpolyglycosides, glycerol monoethers, and polyhydroxyamides (glucamide).  
         [0032]     Cationic surfactants that may be used include quaternary ammonium salts of the general formula R 1 R 2 R 3 R 4 N + X −  wherein the R groups are independently hydrocarbyl chains of C 1 -C 22  length, typically alkyl, hydroxyalkyl or ethoxylated alkyl groups, and X is a solubilising cation (for example, compounds in which R 1  is a C 8 -C 22  alkyl group, preferably a C 8 -C 10  or C 12 -C 14  alkyl group, R 2  is a methyl group, and R 3  and R 4 , which may be the same or different, are methyl or hydroxyethyl groups); and cationic esters (for example, choline esters) and pyridinium salts.  
         [0033]     The total quantity of detergent surfactant in the composition is suitably from 0.1 to 60 wt % e.g. 0.5-55 wt %, such as 5-50 wt %.  
         [0034]     Preferably, the quantity of anionic surfactant (when present) is in the range of from 1 to 50% by weight of the total composition. More preferably, the quantity of anionic surfactant is in the range of from 3 to 35% by weight, e.g. 5 to 30% by weight.  
         [0035]     Preferably, the quantity of nonionic surfactant when present is in the range of from 2 to 25% by weight, more preferably from 5 to 20% by weight.  
         [0036]     Amphoteric surfactants may also be used, for example amine oxides or betaines.  
         [0000]     Builders:  
         [0037]     The compositions may suitably contain from 10 to 70%, preferably from 15 to 70% by weight, of detergency builder. Preferably, the quantity of builder is in the range of from 15 to 50% by weight.  
         [0038]     The detergent composition may contain as builder a crystalline aluminosilicate, preferably an alkali metal aluminosilicate, more preferably a sodium aluminosilicate.  
         [0039]     The aluminosilicate may generally be incorporated in amounts of from 10 to 70% by weight (anhydrous basis), preferably from 25 to 50%. Aluminosilicates are materials having the general formula: 
 
0.8-1.5 M 2 O. Al 2 O 3 . 0.8-6 SiO 2  
 
 where M is a monovalent cation, preferably sodium. These materials contain some bound water and are required to have a calcium ion exchange capacity of at least 50 mg CaO/g. The preferred sodium aluminosilicates contain 1.5-3.5 SiO 2  units in the formula above. They can be prepared readily by reaction between sodium silicate and sodium aluminate, as amply described in the literature. 
 
         [0040]     Alternatively, or additionally to the aluminosilicate builders, phosphate builders may be used.  
         [0000]     Textile Softening and/or Conditioner Compounds:  
         [0041]     If the composition of the present invention is in the form of a textile conditioner composition, the surfactant will be a textile softening and/or conditioning compound (hereinafter referred to as “textile softening compound”), which may be a cationic or nonionic compound.  
         [0042]     The softening and/or conditioning compounds may be water insoluble quaternary ammonium compounds. The compounds may be present in amounts of up to 8% by weight (based on the total amount of the composition) in which case the compositions are considered dilute, or at levels from 8% to about 50% by weight, in which case the compositions are considered concentrates.  
         [0043]     Compositions suitable for delivery during the rinse cycle may also be delivered to the textile in the tumble dryer if used in a suitable form. Thus, another product form is a composition (for example, a paste) suitable for coating onto, and delivery from, a substrate e.g. a flexible sheet or sponge or a suitable dispenser during a tumble dryer cycle.  
         [0044]     Suitable cationic textile softening compounds are substantially water-insoluble quaternary ammonium materials comprising a single alkyl or alkenyl long chain having an average chain length greater than or equal to C 20 . More preferably, softening compounds comprise a polar head group and two alkyl or alkenyl chains having an average chain length greater than or equal to C 14 . Preferably the textile softening compounds have two, long-chain, alkyl or alkenyl chains each having an average chain length greater than or equal to C 16 .  
         [0045]     Most preferably at least 50% of the long chain alkyl or alkenyl groups have a chain length of C 18  or above. It is preferred if the long chain alkyl or alkenyl groups of the textile softening compound are predominantly linear.  
         [0046]     Quaternary ammonium compounds having two long-chain aliphatic groups, for example, distearyldimethyl ammonium chloride and di(hardened tallow alkyl) dimethyl ammonium chloride, are widely used in commercially available rinse conditioner compositions. Other examples of these cationic compounds are to be found in “Surface-Active Agents and Detergents”, Volumes I and II, by Schwartz, Perry and Berch. Any of the conventional types of such compounds may be used in the compositions of the present invention.  
         [0047]     The textile softening compounds are preferably compounds that provide excellent softening, and are characterised by a chain melting Lβ to Lα transition temperature greater than 25° C., preferably greater than 35° C., most preferably greater than 45° C. This Lβ to Lα transition can be measured by DSC as defined in “Handbook of Lipid Bilayers”, D Marsh, CRC Press, Boca Raton, Fla., 1990 (pages 137 and 337).  
         [0048]     Substantially water-insoluble textile softening compounds are defined as textile softening compounds having a solubility of less than 1×10 −3  wt % in demineralised water at 20° C. Preferably the textile softening compounds have a solubility of less than 1×10 −4  wt %, more preferably less than 1×10 −8  to 1×10 −6  wt %.  
         [0049]     Especially preferred are cationic textile softening compounds that are water-insoluble quaternary ammonium materials having two C 12-22  alkyl or alkenyl groups connected to the molecule via at least one ester link, preferably two ester links. Di(tallowoxyloxyethyl) dimethyl ammonium chloride and/or its hardened tallow analogue are especially preferred of the compounds of this type. Other preferred materials include 1,2-bis(hardened tallowoyloxy)-3-trimethylammonium propane chloride. Their methods of preparation are, for example, described in U.S. Pat. No. 4,137,180 (Lever Brothers Co). Preferably these materials comprise small amounts of the corresponding monoester as described in U.S. Pat. No. 4,137,180, for example, 1-hardened tallowoyloxy-2-hydroxy-3-trimethylammonium propane chloride.  
         [0050]     Other useful cationic softening agents are alkyl pyridinium salts and substituted imidazoline species. Also useful are primary, secondary and tertiary amines and the condensation products of fatty acids with alkylpolyamines.  
         [0051]     The compositions may alternatively or additionally contain water-soluble cationic textile softeners, as described in GB 2 039 556B (Unilever).  
         [0052]     The compositions may comprise a cationic textile softening compound and an oil, for example as disclosed in EP-A-0829531.  
         [0053]     Nonionic softeners include Lβ phase forming sugar esters (as described in M Hato et al Langmuir 12, 1659, 1666, (1996)) and related materials such as glycerol monostearate or sorbitan esters. Often these materials are used in conjunction with cationic materials to assist deposition (see, for example, GB 2 202 244). Silicones are used in a similar way as a co-softener with a cationic softener in rinse treatments (see, for example, GB 1 549 180).  
         [0054]     The compositions may also suitably contain a nonionic stabilising agent. Suitable nonionic stabilising agents are linear C 8  to C 22  alcohols alkoxylated with 10 to 20 moles of alkylene oxide, C 10  to C 20  alcohols, or mixtures thereof.  
         [0055]     Advantageously the nonionic stabilising agent is a linear C 8  to C 22  alcohol alkoxylated with 10 to 20 moles of alkylene oxide. Preferably, the level of nonionic stabiliser is within the range from 0.1 to 10% by weight, more preferably from 0.5 to 5% by weight, most preferably from 1 to 4% by weight. The mole ratio of the quaternary ammonium compound and/or other cationic softening agent to the nonionic stabilising agent is suitably within the range from 40:1 to about 1:1, preferably within the range from 18:1 to about 3:1.  
         [0056]     The composition can also contain fatty acids, for example C 8  to C 24  alkyl or alkenyl monocarboxylic acids or polymers thereof. Preferably saturated fatty acids are used, in particular, hardened tallow C 16  to C 18  fatty acids. Preferably the fatty acid is non-saponified, more preferably the fatty acid is free, for example oleic acid, lauric acid or tallow fatty acid. The level of fatty acid material is preferably more than 0.1% by weight, more preferably more than 0.2% by weight. Concentrated compositions may comprise from 0.5 to 20% by weight of fatty acid, more preferably 1% to 10% by weight. The weight ratio of quaternary ammonium material or other cationic softening agent to fatty acid material is preferably from 10:1 to 1:10.  
         [0000]     Other Components  
         [0057]     Compositions according to the invention may comprise soil release polymers such as block copolymers of polyethylene oxide and terephthalate.  
         [0058]     Other optional ingredients include emulsifiers, electrolytes (for example, sodium chloride or calcium chloride) preferably in the range from 0.01 to 5% by weight, pH buffering agents, and perfumes (preferably from 0.1 to 5% by weight).  
         [0059]     Further optional ingredients include non-aqueous solvents, fluorescers, colourants, hydrotropes, antifoaming agents, enzymes, optical brightening agents, and opacifiers.  
         [0060]     Suitable bleaches include peroxygen bleaches. Inorganic peroxygen bleaching agents, such as perborates and percarbonates are preferably combined with bleach activators. Where inorganic peroxygen bleaching agents are present the nonanoyloxybenzene sulphonate (NOBS) and tetra-acetyl ethylene diamine (TAED) activators are typical and preferred.  
         [0061]     Suitable enzymes include proteases, amylases, lipases, cellulases, peroxidases and mixtures thereof.  
         [0062]     In addition, compositions may comprise one or more of anti-shrinking agents, anti-wrinkle agents, anti-spotting agents, germicides, fungicides, anti-oxidants, UV absorbers (sunscreens), heavy metal sequestrants, chlorine scavengers, dye fixatives, anti-corrosion agents, drape imparting agents, antistatic agents and ironing aids. The lists of optional components are not intended to be exhaustive.  
         [0063]     Lubricants and other ‘wrinkle release’ agents are a particularly preferred optional component of compositions according to the invention.  
         [0064]     In order that the invention may be further and better understood it will be described below with reference to several non-limiting examples.  
       EXAMPLES  
     Example 1  
     Preparation of Hydrolysed Amaranth Starch  
       [0065]     Hydrolytic treatment of amaranth starch was carried out to improve dispersibility and enhance colloidal properties of the native amaranth starch.  
         [0066]     In a Nalgene® container 30 g of food-grade organic amaranth starch (Nu-World Amaranth Inc., Earlville, Iowa, USA) was mixed with 500 ml of diluted hydrochloric acid, 2.2 N. The whole mixture was shaken vigorously to disperse the starch, and subsequently set in a controlled-temperature bath at 36° C. for five hours. The acid-starch mixture was redispersed from time to time by gently shaking the container manually to promote further acid attack on the soluble materials within the starch.  
         [0067]     To stop the hydrolytic treatment, an equal volume of distilled water (i.e., 500 ml) was added to the reaction container after the five-hours period. The neutralisation of the starch was carried out by successive steps of redispersion in distilled water followed by centrifugation at 4500 rpm until the pH of the supernatant was over 5. Finally, the neutralised product was dried in a freeze-dryer for a period of 3-5 days. The humidity content of the dried hydrolysed starch prepared in this way was 9.0%.  
       Example 2  
     Preparation of an Emulsion  
       [0068]     28 g of glycerol monoisostearate (Prisorine™ 2040, Uniquema, Wirral, UK) is thoroughly mixed with 12 g of polydimethylsiloxane PEG isostearate blend (Silwax™ DMC-IS, Siltech, Ontario, Canada). This mix is completely transparent; has a viscosity of 300 mPa·s at room temperature; has an interfacial tension with water of 0.3 mN/m also at room temperature; and under the microscope shows as a single phase.  
         [0069]     4 g of amaranth starch treated according to the procedure described in example 1 is dispersed in 1000 ml of distilled water with the aid of a electric mixer (Silverson SL2, Silverson Machines; Chesham, UK). 30 ml of dispersion containing 0.004 g/l of starch is poured in a 50 ml glass vial. 0.5 ml of polyol-in-silicone is added dropwise to the 30 ml amaranth dispersion. During the dropwise addition, the whole content is stirred at ca. 500 rpm with the aid of a universal electronic stirrer (Heidolph RZR 2051, Heidolph Instruments GmbH &amp; Co. KG, Schwabach, Germany).  
         [0070]     Once the total oil system is added, the speed of the mixer is increased to ca. 1500 rpm and maintained at this lever for 10 min. This same procedure was repeated seven times as to obtain 7 different particle-containing emulsions with 0.5 ml of oil each. All seven containers were then added to the original amaranth dispersion (790 ml) to form a parent emulsion consisting of 1000 ml of water, 4 g of amaranth starch and 3.5 ml of polyol-in-silicone (oil).  
         [0071]     Microscopy analysis of the parent emulsion showed individual amaranth colloidal particles freely suspended and not interacting with the emulsified oil droplets. The oil droplets were polydispersed in size and had diameters ranging between 5-10 microns. No interactions between droplets, such as coalescence, was evidenced from the microscopic analysis for up to two weeks after the emulsions were prepared.  
       Example 3  
     Spray Drying of the Emulsion  
       [0072]     Spray-drying of the model polyol-in-silicone/starch particles emulsion was carried out in a laboratory scale spray drier (Lab-plant SD-04, LabPlant Laboratory Equipment, Huddersfield, UK). Standard operating procedures for this equipment are well known to those skilled in the art. Further details can be found in the operation manual of the equipment.  
         [0073]     A parent emulsion with the same characteristics as the one described in example 2 was mixed with 50 ml of soluble amylopectin solution (concentration=4 g/l). A magnetic stirrer was operated at all times to avoid concentration gradients within the parent emulsion/amylopectin mix. The whole mixture was then fed to the top nozzle with the aid of a rotary pump.  
         [0074]     The inlet temperature to the top spraying chamber was set in all experiments at 250±1° C. By controlling the inlet liquid flow rate it was possible to maintain an optimum cyclone outlet temperature in the range 110±1° C.  
         [0075]     Once the equipment reached a steady state operation, off-white powdery material started to form and was discharged out the cyclone into a collection sample bottle.  
       Example 4  
     Matrix/Encapsulate Ratio  
       [0076]     Several trials were run according to procedures described in examples 2 and 3. Different ratios of insoluble starch to oil were used. A description of the variables, types of products obtained and their redispersibility characteristics are listed in Table 1.  
                                             TABLE 1                           Description of spray-drying variables and product       characteristics                Solids   Oil   Starch   Powder       Encap. oil       Sample   (% W)   (% W)   (% W)   Quality   Redisp   (%)               1   0.36   48.80   51.20   ++   ++   N/A       2   0.53   65.60   34.40   −−   −−   N/A       3   0.44   58.90   41.10   −   −   N/A       4   0.40   54.40   45.60   −   −   N/A       5   0.30   43.30   56.70   +   +   N/A       6   1.30   45.50   54.50   +++   +++   32.50       7   1.30   45.50   54.50   +++   +++   32.80       8   1.30   45.50   54.50   +++   +++   37.10       Blank   N/A   N/A   N/A   +++   +++    0.90       (example 1)                  
 
         [0077]     In the table ‘solids’ is the w/w % total solids (oil+starch) in the emulsion before drying. ‘Oil’ is the w/w % of oil in solids fraction of the parent emulsion (i.e. oil as weight % of oil plus starch). ‘Starch’ is the w/w % of starch in the solids fraction of the emulsion prior to drying. The ‘Oil’ and ‘Starch’ % W add to 100%. Encapsulated oil is measured in triplicate by accelerated solvent extraction (ASE) technique using 0.5 g spray dried sample.  
         [0078]     For the powder quality the following notation is used:  
         [0000]     + flowing powder yet with big aggregates  
         [0000]     ++ flowing powder, smaller aggregates  
         [0000]     +++ flowing powder, optimum properties  
         [0000]     − sticky powder, troublesome spray-drying  
         [0000]     −− very sticky powder, unstable spray-drying  
       Example 5  
     Product Characterisation  
       [0079]     True density and thermogravimetric behaviour were assessed for the dry emulsion powder containing the encapsulated polyol-in-silicone system.  
         [0080]     The true density of the powder was measured by helium pycnometry. The equipment used was a Quantachrome Ultrapycnometer (Quantachrome Instruments, Boyton Beach, Fla., USA); which is designed to measure the volume and true density of solids by using Archimedes&#39; principle of fluid displacement, combined with Boyle&#39;s law to determine volume.  
         [0081]     Table 2 summarises the true density results. As inferred from the data in the table, there is a strong relationship between the level of encapsulated oil and the true density of the matrix/oil composite.  
                                           TABLE 2                           True density measurement of dry emulsions                Encapsulated oil level (%)   True density (g/cm 3 )                            0   1.542 ± 0.0016           32.8   1.8053 ± 0.2201            37.1   2.115 ± 0.1236                      
 
         [0082]     Thermogravimetric analysis was carried out in a Perkin Elmer Thermogravimetric Analyser TGA7 (Perkin Elmer, Wellesley, Mass., USA) under the following experimental conditions: sample weight, 10 mg; temperature range, 20-400° C.; heating rate, 5° C./min; flowing nitrogen atmosphere.  
         [0083]     A typical thermogram for a sample containing 37.1% weight of encapsulated oil shows the presence of two distinct weight-loss events. The first transition, which is due to the release of physically adsorbed water (i.e., moisture) and extents up to about 80° C. Total weight loss in this first transition is typically ca. 9%, a value comparable to the humidity levels found in the hydrolysed starch from example 1.  
         [0084]     The second transition typically occurs at a temperature of 180-200 Celsius and corresponds to the thermal decomposition of both encapsulated oil and the matrix. It is clear that the second transition is not a single event, as in the case of the first transition, and therefore it is impossible to distinguish the onset for the degradation of each individual component from the data in the thermogram. However, it is remarkable that the matrix/oil composite remains stable (i.e., no weight loss) when the temperature is raised up to ca. 200° C.