Abstract:
Disclosed is a dry-cleaning method for removing a metal film adhered to a film-formation apparatus by using β-diketone, the dry-cleaning method being characterized by that a gas containing β-diketone and NOx (representing at least one of NO and N 2 O) is used as a cleaning gas and that the metal film within a temperature range of 200° C. to 400° C. is reacted with the cleaning gas, thereby removing the metal film. According to this method, it is possible to make etching progress even if there occurs a temperature difference depending on the position of the adhered metal film.

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to a dry-cleaning method in a film-formation apparatus. 
       BACKGROUND OF THE INVENTION 
       [0002]    In the production process of semiconductor elements, a metal film is formed as a metal gate material, an electrode material or a magnetic material on the substrate surface by a film-formation apparatus. Upon this, besides on the substrate surface, there occurs an adhesion of unnecessary metal films, etc. on the surfaces in the inside of the film-formation apparatus, such as a stage for holding and heating the substrate in a film-formation chamber of the apparatus, an electrode for generating plasma, or other jigs, and furthermore an inner wall of the chamber and as one connecting with this an inner wall of piping, etc. Therefore, it is necessary to remove this. There is known a dry-cleaning method using β-diketone, as a method for removing unnecessary metal films, etc. under a condition that the inside of the chamber is heated after the substrate has been taken out of the chamber. For example, there is known a dry-cleaning method of reacting and removing a metal oxide film as a metal coordination compound by bringing β-diketone, such as hexafluoroacetylacetone (in the following, abbreviated as HFAcAc), into contact with the metal oxide film (e.g., Patent Publication 1). However, when this method is conducted against a metal film, it is not possible to turn the metal into an oxidized condition, resulting in no progress in etching reaction. Thus, there is known a dry-cleaning method that makes it possible to react and remove a metal film as a metal coordination compound by using a combination of oxygen and β-diketone, such as HFAcAc (e.g., Patent Publications 2 and 3). 
       PRIOR ART PUBLICATIONS 
     Non-Patent Publications 
       [0003]    Patent Publication 1: Japanese Patent Application Publication 2001-176807. 
         [0004]    Patent Publication 2: Japanese Patent 4049423. 
         [0005]    Patent Publication 3: Japanese Patent Application Publication Heisei 6-101076. 
       SUMMARY OF THE INVENTION 
       [0006]    In general, when conducting a dry-cleaning of a metal film adhered to sites other than the substrate surface, after depositing the metal film on the surface of the substrate, there occur temperature differences among adhesion sites of the metal film, such as the inner wall of the chamber heated to high temperature, thereby causing a wide temperature distribution. Hitherto, in a dry-cleaning method of a metal film using β-diketone, in a method for removing a metal film as the removal target by etching using β-diketone and oxygen, in case that the temperature distribution of the metal film among adhesion sites ranges, for example, from 250° C. to 370° C., etching does not progress at all at a low temperature site of around 250° C., thereby causing a phenomenon that the temperature range in which the etching removal is possible gets narrower. Such phenomenon becomes conspicuous, particularly when the metal is nickel. 
         [0007]    Therefore, there is a demand for a dry-cleaning method capable of conducting an efficient cleaning, even in case that the temperature difference among adhesion sites of the metal film is large when conducting a cleaning of a chamber inner wall, etc. under a heated condition at high temperature without opening the chamber. 
         [0008]    It is an object of the present invention to solve the above-mentioned problem and to provide a dry-cleaning method capable of progressing etching, even if the temperature difference among sites of the adhered metal film occurs, when removing the metal film adhered in the inside of the film-formation apparatus. 
         [0009]    As a result of a repeated eager study the present inventors have found that, in a dry-cleaning method for removing a metal film adhered in the inside of a film-formation apparatus (for example, CVD apparatus, sputtering apparatus, vacuum deposition apparatus, etc.) using β-diketone, it becomes possible to progress etching of the adhered metal film in a wide temperature range in the film-formation apparatus by using a gas containing β-diketone and NOx (representing at least one of NO and N 2 O) as cleaning gas. 
         [0010]    That is, the present invention provides a dry-cleaning method for removing a metal film adhered in the inside of a film-formation apparatus by using β-diketone, the dry-cleaning method (first method) being characterized by that a gas containing β-diketone and NOx (representing at least one of NO and N 2 O) is used as a cleaning gas and that the metal film within a temperature range of 200° C. to 400° C. is reacted with the cleaning gas, thereby removing the metal film. 
         [0011]    The first method may be a dry-cleaning method (second method), which is characterized by that the β-diketone is hexafluoroacetylacetone or trifluoroacetylacetone. 
         [0012]    The first or second method may be a dry-cleaning method (third method), which is characterized by that the cleaning gas contains at least one gas selected from the group consisting of He, Ar, and N 2 . 
         [0013]    The first method may be a dry-cleaning method (fourth method), which is characterized by that the metal film is constituted of at least one element of from group 6 to group 11 of the periodic table. cl ADVANTAGEOUS EFFECT OF THE INVENTION 
         [0014]    By using the dry-cleaning method of the present invention, it becomes possible to efficiently conduct a cleaning of a metal film adhered in the inside of a film-formation apparatus, due to a wide temperature range in which the etching removal is possible. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0015]      FIG. 1  shows a schematic system diagram of an apparatus used in the test. 
       
    
    
     DETAILED DESCRIPTION 
       [0016]    The removal target by the dry-cleaning method of the present invention is a metal film. This metal film is constituted of at least one of elements of group 6 to group 11 of the periodic table. Specifically, it is possible to cite elements, such as Cr, Mo, W, Mn, Fe, Ru, Co, Ir, Ni, Pd, Pt, Cu, Ag, and Au. As the metal film constituted of the element, it is possible to cite, for example, a film made of any one of the elements. It may be a metal film constituted of a plurality of the elements. For example, it is possible to cite NiFe, CoFe, CoFeNi, NiFeCr, NiFeMo, CuNiFe, etc. On a metal film containing any of Cr, Mn, Fe, Ni, Co, and Pt as constituent elements, the advantageous effect of the present invention becomes conspicuous. 
         [0017]    In the dry-cleaning method of the present invention, a cleaning gas is introduced into a film-formation apparatus and brought into contact with a metal film adhered in the film-formation apparatus to generate a reaction to form a metal coordination compound, thereby removing the metal film by etching. Upon this, the cleaning gas must contain β-diketone and NOx (representing at least one of NO and N 2 O). The reason why the temperature range in which the metal film can be removed by etching becomes wider by using NOx as compared with O 2  used hitherto is not certain. We have not found a similar advantageous effect in NO 2 , which belongs to the same nitrogen oxides and has an oxidative action. Therefore, it is considered to be an action special to NO and N 2 O, in which reactivity of complexation of a metal oxide film generated by an oxidative action improves by not only the oxidative action of NO and/or N 2 O but also an interaction between NO or N 2 O and β-diketone. 
         [0018]    As β-diketone, it is possible to cite, for example, hexafluoroacetylacetone, trifluoroacetylacetone, acetylacetone, etc. It is possible to use not only one type, but also at least two types. In particular, in terms of etching capability at high rate, hexafluoroacetylacetone and trifluoroacetylacetone are preferable. Etching rate of the metal film increases with the increase of concentration of β-diketone contained in the cleaning gas. In case that vapor pressure of β-diketone is low to cause a risk of possibility of liquefaction in the film-formation apparatus, it is preferable to suitably adjust the concentration by a diluting gas. 
         [0019]    It is preferable that volume fraction of NOx contained in the cleaning gas relative to volume fraction of β-diketone contained in the cleaning gas, that is, NOx/β-diketone ratio, is from 0.02 to 0.60. If NOx/β-diketone ratio is less than 0.02 or exceeds 0.60, there is a risk of lowering of etching rate of the metal film. 
         [0020]    It is optional that NO and N 2 O are mixed together in the cleaning gas, and its ratio is not particularly limited. 
         [0021]    It is optional that at least one gas selected from inert gases, such as N 2 , He and Ar, is mixed in the cleaning gas, together with the above-mentioned β-diketone and NOx. Its concentration is not particularly limited. For example, it is usable by setting the concentration of inert gas in a range of 0 to 90 volume %. 
         [0022]    As to temperature during the cleaning, etching is possible as long as temperature of the metal film as the removal target is in a temperature range of 200° C. to 400° C. It is preferably from 250° C. to 370° C. In particular, it is desirable to be from 260° C. to 350° C. in order to obtain a higher etching rate. 
         [0023]    Pressure in the inside of the chamber during the cleaning is not particularly limited. In general, the pressure range in the film formation is from 0.1 kPa to 101.3 kPa. Etching is also possible in this pressure range. 
         [0024]    By conducting a dry-cleaning under the above-mentioned conditions, it becomes possible to efficiently remove the metal film adhered in the film-formation chamber or in the piping. This is the same, even if the inside of the film-formation chamber immediately after taking the substrate out of the chamber after forming a film on the substrate is in a heated condition or even if the chamber has been once cooled and then reheated. 
         [0025]    In particular, in the case of a CVD apparatus using a chemical vapor deposition method for forming a metal film, the temperature of the film-forming substrate of the film for ration process is as high as 300° C. or higher, as compared with that according to other film formation apparatuses. Therefore, there is a large temperature difference between that and a low-temperature section, which is lower than 300° C., in the film formation chamber. Thus, in view of the effect on the film formation process, it is preferable to conduct a cleaning for removing a metal film adhered in the film formation chamber, under a condition of a wide temperature distribution in the film formation apparatus. Therefore, it is particularly effective for a cleaning in a CVD apparatus. 
       EXAMPLES 
       [0026]    In the present test, in order to examine the etching behavior of a metal film depending on the temperature distribution in the chamber, a test was conducted by using a chamber equipped in the inside with five heater stages each carrying a sample of a metal film adhered. 
         [0027]      FIG. 1  is a schematic system diagram of an apparatus used in the present test. In the chamber  1 , heater stages  5 A to  5 E are provided. Outside of the chamber  1  and in the insides of the heater stages  5 A,  5 B,  5 C,  5 D and  5 E, heaters  61 ,  62 A,  62 B,  62 C,  62 D and  62 E are provided. It is possible to separately set each stage at a predetermined temperature. This heater stage  5 A,  5 B,  5 C,  5 D or  5 E carries thereon a sample  7 A,  7 B,  7 C,  7 D or  7 E. The sample  7 A,  7 B,  7 C,  7 D or  7 E is a metal foil (shape: 2 cm×2 cm, thickness: 0.1 mm). The metal foil is one assumed to be a metal film adhered in the film formation apparatus. 
         [0028]    To the chamber  1 , there are connected a gas pipe  41  for introducing gas and a gas pipe  42  for discharging gas. β-diketone supply system  21 , NOx gas supply system  22 , and diluting gas introducing system  23  are connected to the gas pipe  41  through valves  31 ,  32  and  33 . A vacuum pump  8  is connected to the gas pipe  42  through a valve  34 . Pressure of the inside of the chamber  1  is controlled by the valve  34 , based on the indicated value of a pressure gauge (omitted in the drawings) attached to the chamber  1 . 
         [0029]    Next, the operation method is explained. The insides of the chamber  1  and the gas pipes  41  and  42  were subjected to a vacuum displacement until less than 10 Pa. Then, the samples, which have been placed on the heater stages and of which weights have been measured, are heated at a predetermined temperature by the heaters  61 ,  62 A,  62 B,  62 C,  62 D and  62 E. After confirming that the heaters  61  and  62 A to  62 E have reached predetermined values, the valves  31 ,  32  and  33  are opened. While a cleaning gas is introduced into the chamber  1  by supplying β-diketone, NOx and the diluting gas from β-diketone supply system  21 , NOx gas supply system  22 , and diluting gas supply system  23  at predetermined flow rates, the inside of the chamber  1  is adjusted to a predetermined pressure. After the start of the introduction, after a lapse of a predetermined time (10 minutes), the introduction of the cleaning gas is stopped. The inside of the chamber  1  is subjected to a vacuum displacement. Then, the samples are taken out to measure their weights. The amount of etching is calculated from the weight change of the sample before and after the test. In this case, due to the measurement accuracy of a scale for measuring the weight, the quantitative lower limit of the amount of etching to be calculated is 20 nm. 
       Examples 1-21 
       [0030]    In the present test, the total flow rate of the cleaning gas to be introduced was 500 sccm. The diluting gas was N 2 . The samples  7 A,  7 B,  7 C,  7 D, and  7 E were respectively heated at 240° C., 275° C., 300° C., 325° C. and 370° C. 
         [0031]    Furthermore, the above test was conducted by adjusting the volume concentration of hexafluoroacetylacetone as β-diketone in the cleaning gas to 50%, changing volume concentration of NO as NOx in the cleaning gas to a concentration shown in Table 1, adjusting the pressure in the inside of the chamber to 13.3 kPa, and using a Ni foil as the metal foil (Examples 1-6). 
         [0032]    Furthermore, Example 1 was repeated except in that the pressure in the inside of the chamber was adjusted to 40 kPa (Example 7), 6.7 kPa (Example 8), 1.3 kPa (Example 9), and 80 kPa (Example 10). 
         [0033]    Furthermore, Example 1 was repeated except in that β-diketone was trifluoroacetylacetone (Example 11). 
         [0034]    Furthermore, Example 1 was repeated except in that N 2 O was used. as NOx (Example 12). 
         [0035]    Furthermore, Example 1 was repeated except in that the volume concentration of hexafluoroacetylacetone in the cleaning gas was adjusted to 25%, and that the volume concentration of NO in the cleaning gas was adjusted to 5% (Example 13). 
         [0036]    Furthermore, Example 1 was repeated except in that the volume concentration of hexafluoroacetylacetone in the cleaning gas was adjusted to 83%, and that the volume concentration of NO in the cleaning gas was adjusted to 17% (Example 14). 
         [0037]    Furthermore, Example 1 was repeated except that, as shown in Table 1, the metal foil was changed to Cr, Mn, Fe, Co Pt, or NiFe alloy (permalloy, an alloy of Fe:Ni=22:78) (Examples 15-20). 
         [0038]    Example 1 was repeated except in that the volume concentrations of NO and N 2 O in the cleaning gas were respectively adjusted to 5% and 5%, 10% in total (Example 21). 
         [0039]    Table 1 shows the gas, the pressure and the temperature condition of the test and the result of calculating the amount of etching. As a result, it as confirmed that all the samples with different temperatures were etched in all of Examples. 
         [0040]    It has been confirmed that the result is similar even if changing the diluting gas from N 2  to Ar or He. 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
             
             
               
                   
                   
               
               
                   
                 Conc. (vol. %) 
                 NO x /β- 
                 Chamber 
                 Amount of etching (nm) 
               
             
          
           
               
                 Test 
                   
                 β- 
                   
                 β- 
                   
                 diketone 
                 pressure 
                 Sample A 
                 Sample B 
                 Sample C 
                 Sample D 
                 Sample E 
               
               
                 No. 
                 Metal 
                 diketone 
                 NO x   
                 diketone 
                 NO x   
                 vol. ratio 
                 kPa 
                 240 °  C. 
                 275 °  C. 
                 300 °  C. 
                 325 °  C. 
                 370 °  C. 
               
               
                   
               
             
          
           
               
                 Ex. 1 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 700 
                 nm 
                 1800 
                 nm 
                 1600 
                 nm 
                 1400 
                 nm 
                 1200 
                 nm 
               
               
                 Ex. 2 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                  5% 
                 0.10 
                 13.3 
                 kPa 
                 1000 
                 nm 
                 2000 
                 nm 
                 3200 
                 nm 
                 4000 
                 nm 
                 3900 
                 nm 
               
               
                 Ex. 3 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                  2% 
                 0.04 
                 13.3 
                 kPa 
                 700 
                 nm 
                 1500 
                 nm 
                 1800 
                 nm 
                 2000 
                 nm 
                 1900 
                 nm 
               
               
                 Ex. 4 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 0.5%  
                 0.01 
                 13.3 
                 kPa 
                 100 
                 nm 
                 150 
                 nm 
                 150 
                 nm 
                 100 
                 nm 
                 90 
                 nm 
               
               
                 Ex. 5 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 25% 
                 0.50 
                 13.3 
                 kPa 
                 900 
                 nm 
                 1100 
                 nm 
                 1300 
                 nm 
                 1500 
                 nm 
                 1300 
                 nm 
               
               
                 Ex. 6 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 35% 
                 0.70 
                 13.3 
                 kPa 
                 80 
                 nm 
                 200 
                 nm 
                 300 
                 nm 
                 300 
                 nm 
                 280 
                 nm 
               
               
                 Ex. 7 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 40 
                 kPa 
                 1500 
                 nm 
                 2100 
                 nm 
                 3500 
                 nm 
                 3100 
                 nm 
                 2500 
                 nm 
               
               
                 Ex. 8 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 6.7 
                 kPa 
                 600 
                 nm 
                 1500 
                 nm 
                 1400 
                 nm 
                 1400 
                 nm 
                 1300 
                 nm 
               
               
                 Ex. 9 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 1.3 
                 kPa 
                 200 
                 nm 
                 500 
                 nm 
                 500 
                 nm 
                 400 
                 nm 
                 350 
                 nm 
               
               
                 Ex. 10 
                 Ni 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 80 
                 kPa 
                 1400 
                 nm 
                 2000 
                 nm 
                 3200 
                 nm 
                 3000 
                 nm 
                 2000 
                 nm 
               
               
                 Ex. 11 
                 Ni 
                 TFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 500 
                 nm 
                 1300 
                 nm 
                 1100 
                 nm 
                 1000 
                 nm 
                 900 
                 nm 
               
               
                 Ex. 12 
                 Ni 
                 HFAcAc 
                 N2O 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 200 
                 nm 
                 400 
                 nm 
                 500 
                 nm 
                 600 
                 nm 
                 500 
                 nm 
               
               
                 Ex. 13 
                 Ni 
                 HFAcAc 
                 NO 
                 25% 
                  5% 
                 0.20 
                 13.3 
                 kPa 
                 400 
                 nm 
                 800 
                 nm 
                 800 
                 nm 
                 700 
                 nm 
                 600 
                 nm 
               
               
                 Ex. 14 
                 Ni 
                 HFAcAc 
                 NO 
                 83% 
                 17% 
                 0.20 
                 13.3 
                 kPa 
                 800 
                 nm 
                 1900 
                 nm 
                 1700 
                 nm 
                 1500 
                 nm 
                 1400 
                 nm 
               
               
                 Ex. 15 
                 Cr 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 600 
                 nm 
                 1500 
                 nm 
                 1300 
                 nm 
                 1000 
                 nm 
                 900 
                 nm 
               
               
                 Ex. 16 
                 Mn 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 700 
                 nm 
                 1700 
                 nm 
                 1600 
                 nm 
                 1400 
                 nm 
                 1300 
                 nm 
               
               
                 Ex. 17 
                 Fe 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 900 
                 nm 
                 2200 
                 nm 
                 2000 
                 nm 
                 2000 
                 nm 
                 1900 
                 nm 
               
               
                 Ex. 18 
                 Co 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 800 
                 nm 
                 2000 
                 nm 
                 1800 
                 nm 
                 1600 
                 nm 
                 1500 
                 nm 
               
               
                 Ex. 19 
                 Pt 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 400 
                 nm 
                 900 
                 nm 
                 900 
                 nm 
                 800 
                 nm 
                 600 
                 nm 
               
               
                 Ex. 20 
                 NiFe 
                 HFAcAc 
                 NO 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 800 
                 nm 
                 1600 
                 nm 
                 1600 
                 nm 
                 1500 
                 nm 
                 1500 
                 nm 
               
               
                 Ex. 21 
                 Ni 
                 HFAcAc 
                 NO + 
                 50% 
                      5% + 
                 0.20 
                 13.3 
                 kPa 
                 600 
                 nm 
                 1600 
                 nm 
                 1600 
                 nm 
                 1500 
                 nm 
                 1200 
                 nm 
               
               
                   
                   
                   
                 N2O 
                   
                  5% 
               
               
                   
               
               
                 *HFAcAc: hexafluoroacetylacetone, TFAcAc: trifluoroacetylacetone 
               
             
          
         
       
     
       Comparative Examples 1-6  
       [0041]    In the present test, the total flow rate of the cleaning gas to be introduced was 500 sccm. The diluting gas was N 2 . The samples  7 A,  7 B,  7 C,  7 D, and  7 E were respectively heated at 240° C., 275° C., 300° C., 325° C. and 370° C. 
         [0042]    Furthermore, Examples 1, 2 and 3 were repeated except in that O 2  was used as the additive gas, in place of NOx (Comparative Examples 1, 2 and 3). 
         [0043]    Furthermore, Example 14 was repeated except in that O 2 , was used as the additive gas, in place of NOx (Comparative Example 4). 
         [0044]    Furthermore, Example 1 was repeated except in that NO 2  was used as the additive gas, in place of NOx (Comparative Example 5). 
         [0045]    Furthermore, Example 1 was repeated except in that NOx was not introduced into the cleaning gas (Comparative Example 6). 
         [0046]    Table 2 shows the gas, the pressure and the temperature condition of the test and the result of calculating the amount of etching. As a result, it was confirmed that, in case that O 2  was used as the additive gas in place of NOx, the nickel foil sample was almost not etched at every sample temperature or etched at particular sample temperatures, not all sample temperatures. 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
             
             
               
                   
                   
               
               
                   
                 Conc. (vol. %) 
                   
                   
               
             
          
           
               
                   
                 Addi- 
                 Addi- 
                 NO x /β- 
                 Chamber 
                 Amount of etching (nm) 
               
             
          
           
               
                 Test 
                   
                 β- 
                 tive 
                 β- 
                 tive 
                 diketone 
                 pressure 
                 Sample A 
                 Sample B 
                 Sample C 
                 Sample D 
                 Sample E 
               
               
                 No. 
                 Metal 
                 diketone 
                 gas 
                 diketone 
                 gas 
                 vol. ratio 
                 kPa 
                 240 °  C. 
                 275 °  C. 
                 300 °  C. 
                 325 °  C. 
                 370 °  C. 
               
               
                   
               
             
          
           
               
                 Com. Ex. 1 
                 Ni 
                 HFAcAc 
                 O2 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 &lt;20 nm 
                 &lt;20 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
                 60 
                 nm 
               
               
                 Com. Ex. 2 
                 Ni 
                 HFAcAc 
                 O2 
                 50% 
                  5% 
                 0.10 
                 13.3 
                 kPa 
                 &lt;20 nm 
                 &lt;20 nm 
                 &lt;20 
                 nm 
                 400 
                 nm 
                 700 
                 nm 
               
               
                 Com. Ex. 3 
                 Ni 
                 HFAcAc 
                 O2 
                 50% 
                  2% 
                 0.04 
                 13.3 
                 kPa 
                 &lt;20 nm 
                 &lt;20 nm 
                 1500 
                 nm 
                 5000 
                 nm 
                 4500 
                 nm 
               
               
                 Com. Ex. 4 
                 Ni 
                 HFAcAc 
                 O2 
                 83% 
                 17% 
                 0.20 
                 13.3 
                 kPa 
                 &lt;20 nm 
                 &lt;20 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
               
               
                 Com. Ex. 5 
                 Ni 
                 HFAcAc 
                 NO2 
                 50% 
                 10% 
                 0.20 
                 13.3 
                 kPa 
                 &lt;20 nm 
                 &lt;20 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
               
               
                 Com. Ex. 6 
                 Ni 
                 HFAcAc 
                 — 
                 50% 
                 — 
                 — 
                 13.3 
                 kPa 
                 &lt;20 nm 
                 &lt;20 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
                 &lt;20 
                 nm 
               
               
                   
               
               
                 *HFAcAc: hexafluoroacetylacetone 
               
             
          
         
       
     
       INDUSTRIAL APPLICABILITY 
       [0047]    The present invention becomes effective for the removal of a metal film adhered in the inside of a film-formation chamber, particularly for the cleaning in case that the temperature difference among adhesion sites of the metal film is large. 
       EXPLANATION OF SYMBOLS 
       [0000]    
       
           1 : a chamber 
           21 : a β-diketone supply system 
           22 : a NOx supply system 
           23 : a diluting gas supply system 
           31 ,  32 ,  33  and  34 : valves 
           41  and  42 : gas pipes 
           5 A,  5 B,  5 C,  5 D and  5 E: heater stages 
           61 ,  62 A,  62 B,  62 C,  62 D and  62 E: heaters 
           7 A,  7 B,  7 C,  7 D and  7 E: samples 
           8 : a vacuum pump