Abstract:
Sheathing panels are produced by methods which do not require natural resources such as wood and use significantly reduced embodied energy when compared with the energy used to fabricate gypsum sheathing panels. A novel binder, consisting in one embodiment of monopotassium phosphate and magnesium oxide, and combined with various fillers, is incorporated with hollow tubes or water soluble fibers to create a gypsum board-like core which can be formed into a suitable sheathing panel handled and installed in a typical manner. The panel is manufactured to have a desirable shear resistance and water vapor permeability, important performance elements in building envelope design. The manufacturing process results in a panel that does not require mature trees as source material, does not off gas, and involves much lower greenhouse gas emissions than the processes used to make traditional wood or gypsum-based sheathing panels.

Description:
FIELD OF INVENTION 
       [0001]    The present invention relates to new compositions and methods of manufacture for structural sheathing panels and in particular to panels and processes which reduce the energy required to manufacture such structural sheathing panels when compared to the energy required to manufacture traditional gypsum or wood-based structural sheathing panels. 
       BACKGROUND OF THE INVENTION 
       [0002]    In the field of building construction, structural sheathing is a crucial element in suitable building design. Structural sheathing may serve many functions associated with the purpose and integrity of the assembly, including strengthening the building to lateral forces; providing a base wall to which finish siding can be nailed; acting as thermal insulation; and, in some cases, acting as a base for further thermal insulation. Structural sheathing, in the form of thin, rigid panels, is nailed directly onto the framework of the building. Some common types of sheathing include wood boards or slats, oriented strand board (OSB) panels, plywood panels, and gypsum panels. 
         [0003]    Before the acceptance of performance-rated cellulose panels such as oriented strand board (OSB), plywood was the sheet product of choice for constructing wood shear walls. Plywood panels are very flexible and appropriate for a variety of building designs. The panel thickness, panel grade, nail type, and nail spacing could be combined in different ways to achieve a wall with the right design strength. In the 1970s, with the advent of performance-rated products based on waferboard technology, plywood was largely replaced with composite wood panels such as OSB. Today, all of the model building codes in the United States and Canada recognize OSB panels for the same uses as plywood on a thickness-by-thickness basis and they are used interchangeably, based on price and availability. 
         [0004]    More recently, gypsum sheathing panels have been used as structural sheathing panels. Gypsum sheathing is most commonly manufactured with a water-resistive treated core but may also be available in a non-treated core. Treated core gypsum sheathing is intended for use as a substrate sheathing under a variety of exterior wall claddings in any climate. Non-treated core gypsum sheathing is intended for use only in dry climates. As with their wood counterparts, both types of gypsum sheathing (i.e. treated core and non-treated core) are designed to be mechanically attached to the outside surface of exterior wall framing using either nails, or screws, or staples. Gypsum sheathing is manufactured in a range of lengths and widths similar to those of both plywood and OSB. 
         [0005]    The sheathing layer is designed with several system properties and requirements in mind. Of particular importance are the shear resistance imparted by the layer, the water vapor permeance of the layer, the weather resistance of the layer, and finally, the environmental impact (and associated greenhouse gases) involved with the manufacture of the sheathing layer. First, an appropriate structural building design requires that the panel reliably transfer shear forces (typically from wind shear or earthquake loads) from the body of the structure to its foundation. The performance of a panel in a building design is subject to many design elements including the material&#39;s Young&#39;s modulus, the panel thickness, the type and configuration of the structural framing and the type and spacing of the panel fasteners. All of these combine for a rated shear resistance in units of pounds per foot (lb/ft). Materials are tested via American Society of Testing and Materials (ASTM) test methods E2126 or E564. Further information may be found on the Internet at http://www.astm.org. 
         [0006]    A second, important material property of the sheathing panel is the panel&#39;s role in the moisture management across the building envelope. The problems associated with excessive moisture in building wall cavities and the resulting mold growth, are well documented in the national outcry over unhealthy buildings and poor indoor air quality. As a result, building science has established best practices for minimizing the probability of mold growth in buildings. Walls between areas of differing temperature are the primary structures for these problems. Preventing condensation is of particular importance with regard to the exterior walls of homes or other buildings, where temperature extremes are likely to be greater than between interior walls. Wetting of exterior building surfaces and rainwater leaks are major causes of water infiltration, but so is excessive indoor moisture generation. Moisture may be present within a structure due to occupancy and use by humans, use of wet materials during construction, air leaks, or transfer from external wall materials. 
         [0007]    A figure of merit for the measurement of the transport of water vapor across a component such as a panel or a wall assembly, is its permeance, or “perms”. One perm is defined as the transport of one grain of water per square foot of exposed area per hour with a vapor pressure differential of 1-inch of mercury (Hg). Vapor pressure is a function of the temperature and relative humidity (RH) of the air to which a test structure is exposed, and may be found in many standard data tables. The vapor pressure at any certain RH is found by the product of the RH and the vapor pressure for saturated air at a certain temperature. For example, at 70 degrees Fahrenheit the saturated vapor pressure is 0.7392 Hg and the vapor pressure at fifty per cent RH is 0.3696. The testing methodology varies depending upon the subject material. Data presented for sheathing panel products is typically taken using the ASTM E96 “dry cup” method. Further information may be found on the Internet at http://www.astm.org. 
         [0008]    The Department of Energy (DOE) and the American Society of Heating, Refrigeration, and Air-Conditioning Engineers (ASHRAE) and other building science organizations have established recommended wall designs that specify the proper location of a vapor retarder within the wall. A vapor retarder is defined by the building codes as a material having a permeance rating of 1.0 or less. Wall designs are dependant upon the regional climate of the building. In cooling-dominated climates, it is recommended that a vapor retarder be installed on the exterior of the thermal insulation—at the typical location of the structural sheathing. In hot and humid climates, such as along the Gulf coast and in Florida, the vapor barrier should be placed in this exterior location in the wall. Conversely, in heating dominated climates it is recommended that a vapor retarder be installed on the interior side of the thermal insulation—against the interior wallboard. In mixed zones, climates with both significant heating and cooling requirements, design recommendations suggest the omission of the vapor retarder altogether. If these guidelines are not observed, the structure is at risk of allowing water vapor condensation within the wall cavity and eventual water damage and mold growth. To avoid such an outcome, one must know the permeability of the wall components and use only appropriate materials. 
         [0009]    For example, the rate of water vapor transmission of OSB is approximately two (2) perms. For sheathing grade plywood, of ½ to 1 inch thickness, the transmission rate is approximately ten (10) perms. Gypsum sheathing typically has an average vapor permeance of approximately twenty (20) perms. Therefore, plywood and gypsum are above the accepted minimum water vapor transmission rate of five (5) perms specified for a wall with a “U” value less than 0.25 and a vapor retarder not exceeding one (1) perm installed on the interior side of the framing. A double vapor retarder condition is avoided. However, OSB would be deemed unacceptable in the same assembly. 
         [0010]    A third important material feature is weather resistance. Gypsum sheathing is designed for use as a substrate that is covered by an exterior wall cladding. Local weather conditions will dictate the length of time gypsum sheathing may be left exposed; however, it should perform satisfactorily if exposed to the elements for one month or less. Treated core gypsum sheathing should be covered immediately with a weather-resistive barrier, such as building felt or equivalent, if exposure time will exceed one month or weather conditions will be severe. Plywood can typically endure a similar period of weather exposure, while OSB can not. Non-treated core gypsum sheathing should be covered immediately after installation with a weather-resistive barrier. Gypsum sheathing does not hold peel and stick water barrier well. 
         [0011]    Another final important consideration in the design and manufacture of construction materials is their potential negative environmental impact. Environmental impact can take many forms including the depletion of non-renewable natural resources (such as fossil fuels, for example), the generation of harmful chemicals or compounds, or the creation of greenhouse gasses. For a complete assessment as to the long term suitability of a construction material, the existing offering of sheathing materials should be considered in this context as well. 
         [0012]    Unfortunately, the structural integrity of plywood is dependent upon the inclusion of quality wood laminates harvested from mature, large diameter trees, at least 30 years old. Their manufacture puts stress on old growth forests and existing woodland areas. As a result, much of the U.S. softwood plywood industry has shifted from the Pacific Northwest to the South and Southeast, to pine plantations on private lands. These small pines produce a lower quality panel than from the previously abundant older trees. In addition, their costs have risen over the last decade, making them less desirable as a mainstay construction material. OSB has at least two distinct advantages over traditional plywood panels. First, they do not require old growth forests, or decades old trees for their manufacture. OSB is derived from younger aspen trees of a much smaller relative diameter. Although the aspen wood is not a rapidly renewable resource, it does lessen the OSB&#39;s impact of endangered woodlands. Second, OSB extends the use of potentially dangerous resins such as phenol formaldehydes listed by the International Agency for Research on Cancer (IARC) as a potential carcinogen that may be released as an undesirable volatile organic compound (VOC) during the OSB&#39;s service life. 
         [0013]    Gypsum sheathing panels do not require the use of wood and therefore do not share the concerns associated with tree harvesting. Instead, the manufacture of gypsum sheathing represents an astounding amount of embodied energy as a construction material. The term ‘embodied energy’ is defined as “the total energy required to produce a product from the raw materials stage through delivery” of finished product. Several of the steps (drying gypsum, calcining gypsum (dehumidification), mixing the slurry with hot water and drying the manufactured boards) involved in the manufacture of gypsum sheathing take considerable energy. Greenhouse gasses, particularly CO 2 , are produced from the burning of fossil fuels and the calcining of certain materials, such as gypsum. Thus the gypsum manufacturing process generates significant amounts of greenhouse gasses due to the requirements of the process. 
         [0014]    According to the National Institute of Standards and Technology (NIST—US Department of Commerce), specifically NISTIR 6916, the manufacture of gypsum sheathing panel requires 8,196 British Thermal Units (BTU) per pound. With an average ⅝′ gypsum sheathing board weighing approximately 75 pounds, this equates to over 600,000 BTU&#39;s per board total embodied energy. Other sources suggest that embodied energy is less than 600,000 BTU&#39;s per board, while others suggest it may be even more. It has been estimated that embodied energy constitutes over 50% of the cost of manufacture. As energy costs increase, and if carbon taxes are enacted, the cost of manufacturing sheathing panel from calcined gypsum will continue to go up directly with the cost of energy. Moreover, material producers carry the responsibility to find less-energy dependent alternatives for widely used products as part of a global initiative to combat climate change. 
         [0015]    For comparison, the same energy study (NISTIR 6916) found that a total of 18600 BTU&#39;s per panel are required for the wood harvesting and manufacture of plywood sheathing. OSB sheathing requires a similar amount of energy in its manufacture. Report NISTIR 6916 calculated 27100 BTU&#39;s per panel for OSB sheathing. 
         [0016]    In summary, a product&#39;s potential negative environmental impact can take many forms, including a depletion of natural resources such as trees, potable water and materials in short supply, or the negative impact may be in the form of a significant consumption of energy during the product&#39;s manufacture and the resulting generation of greenhouse gases from its production. 
         [0017]    Thus, it would be highly desirable to meet all of the performance requirements of a structural sheathing panel while reducing the environmental impact of its manufacture by reducing the harvesting of trees, reducing the use of harmful chemicals, and reducing the generation of dangerous greenhouse gases via a high embodied energy. 
       SUMMARY OF INVENTION 
       [0018]    In accordance with the present invention, new methods of manufacturing novel sheathing panels (defined herein as “EcoRock™” sheathing panels), are provided. The resulting novel EcoRock sheathing panels can replace plywood, OSB, and gypsum sheathing panels in most construction applications. Sheathing panels formulated and manufactured in accordance with this invention maintain the structural integrity, water vapor permeance, and weather resistance required for building applications. Water vapor permeance is enabled and controlled by the introduction of one or more of various filler fibers. These fibers may be hollow glass fibers and/or alternatively, water soluble fibers. These crucial performance features are maintained while significantly reducing the environmental impact associated with the other existing sheathing materials, thus substantially reducing future harm to the environment. 
         [0019]    This invention will be fully understood in light of the following detailed description taken together with the drawings. 
     
    
     
       DRAWINGS 
         [0020]      FIG. 1  is a perspective view of a sheathing panel according to a preferred embodiment of the invention. 
           [0021]      FIG. 2  shows an EcoRock sheathing slurry tank  202  with fibers  206  oriented in a preferential direction to allow for optimal water vapor transmission following manufacture. 
           [0022]      FIG. 2A  shows a cured EcoRock sheathing brick  212  being cut into slices to create a series of panels with optimal water vapor transmission. 
           [0023]      FIGS. 3 and 3A  show an EcoRock sheathing panel  304  molded as a continuous slab designed for further fabrication steps to allow for optimal water vapor transmission and a cross-section of this panel, respectively. 
           [0024]      FIG. 4  shows an EcoRock molded sheathing panel  406  lowered into a liquid bath to dissolve the embedded liquid soluble fibers. 
           [0025]      FIG. 5  shows the EcoRock sheathing panel manufacturing steps which require little energy. 
           [0026]      FIG. 6  shows the EcoRock sheathing panels  100  installed to framed structure. 
       
    
    
     DETAILED DESCRIPTION 
       [0027]    The following detailed description of embodiments of the invention is illustrative only and not limiting. Other embodiments will be obvious to those skilled in the art in view of this description. The example embodiments are in such detail as to clearly communicate the invention. However, the amount of detail offered is not intended to limit the anticipated variations of embodiments; but, on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the present invention as defined by the appended claims. Various changes in the details may be made without departing from the spirit, or sacrificing any of the advantages of the present invention. The detailed descriptions below are designed to make such embodiments obvious to a person of ordinary skill in the art. 
         [0028]    The novel processes and materials described herein for manufacturing a low embodied energy sheathing panel lessen the environmental impact created by traditional processes and materials. In comparison to wood products (such as plywood and OSB) there is no depletion of trees as a natural resource. As an alternative to gypsum, the disclosed processes eliminate the most energy intensive prior art processes in the manufacture of current gypsum sheathing panels such as gypsum drying, gypsum calcining, the generation of hot water, and board drying. The new processes allow a sheathing panel to be formed from non-calcined materials which are plentiful and safe and which can react naturally to form a strong, shear resistant board that is also weather hardy and with acceptable water vapor permeability. 
         [0029]    The new EcoRock sheathing panel contains a binder of one or more of magnesium oxide (MgO), calcium oxide, calcium hydroxide, iron oxide (Hematite or Magnetite) and a solution of alkali phosphate salt (sodium phosphate, potassium phosphate, monopotassium phosphate, tripotassium phosphate, triple super phosphate, calicium dihydrogen phosphate, dipotassium phosphate or phosphoric acid). The selected binder materials, often in conjunction with fillers, are mixed together at the start of the particular EcoRock manufacturing process or processes selected to be used to form the EcoRock sheathing panel or sheathing panels. Prior to the addition of liquids, such as water, this mix of binder and filler powders is termed a “dry mix.” The MgO may be calcined or uncalcined. However uncalcined MgO may be less expensive and provide significant energy savings over calcined MgO. Thus there is no need to use calcined MgO, even though calcined MgO can be used in the EcoRock sheathing panel processes. 
         [0030]    In U.S. patent application Ser. No. 11/652,991 Surace et al. describe novel interior gypsum wallboard replacements using such an EcoRock formulation. While there are many binder ingredients in the Surace et al. panels similar to the binder ingredients used in the present EcoRock sheathing panel, the present sheathing panel as intended for use in building construction has features which optimize the water vapor transmission of the panel, a property which is an important characteristic of sheathing panels. This water vapor transmission capability is not present in the Surace et al. panels. 
         [0031]    Many different configurations of materials are possible in accordance with this invention, resulting in improved strength, hardness, score/snap capability, paper adhesion, thermal resistance, weight, and fire resistance. The binder is compatible with many different fillers including calcium carbonate (CaCO 3 ), wolastinite (calcium silicate,) cornstarch, ceramic microspheres, perlite, flyash, waste products and other low-embodied energy materials. Uncalcined gypsum may also be used as a filler material. By carefully choosing low-energy, plentiful, biodegradable materials as fillers, such as those listed above, the sheathing panel begins to take on the best characteristics of wood-based and gypsum sheathing panels. These characteristics (structural strength, acceptable weight so as to be able to be carried, water vapor permeability, and the ability to be nailed or otherwise attached to other materials such as studs) are important to the marketplace and may be required to make the product a commercial success as a traditional sheathing panel replacement. 
         [0032]    Calcium carbonate (CaCO 3 ), an acceptable alternate filler material, is plentiful and represents an environmentally favorable choice. Cornstarch, made from corn, is plentiful and non toxic. In addition, ceramic microspheres are a waste product of coal-fired power plants, and can reduce the weight of materials as well as increase thermal and fire resistance of the sheathing panels that incorporate these materials. The dry mix can include up to 60% by weight of ceramic microspheres. Such a dry mix may be successfully incorporated in EcoRock sheathing panels. Concentrations of greater than sixty percent (60%) by weight of ceramic microspheres in the dry mix increase cost and can reduce strength below acceptable levels. Fly ash is also a waste product of coal-fired power plants which can be effectively utilized in the dry mix. The dry mix can include up to 80% by weight of fly ash. Such a dry mix has been successfully incorporated into EcoRock sheathing panels; however very high concentrations of fly ash can increase weight, darken the core color, and harden the core beyond a level that may be desirable. Biofibers (i.e. biodegradable plant-based fibers) are used for tensile and flexural strengthening in this embodiment; however other fibers, such as cellulose or borosilicate glass fibers, may also be used. The use of specialized fibers in cement boards is disclosed in U.S. Pat. No. 6,676,744 and is well known to those practicing the art. 
         [0033]    In a preferred embodiment of the present invention, a dry mix of powders plus water is created using the materials listed in TABLE 1 by both volume and weight: 
         [0000]    
       
         
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
               
                 Material 
                 % Volume 
                 % Weight 
                 Notes 
               
               
                   
               
             
             
               
                 Oxide 
                  7.0% 
                  5.4% 
                 Magnesium Oxide 
               
               
                 Phosphate 
                 13.0% 
                 16.0% 
                 Monopotassium Phosphate 
               
               
                 Filler 
                  11.% 
                 12.0% 
                 Calcium Silicate 
               
               
                 Fibers 
                  2.0% 
                 0.50% 
                 Biofibers 
               
               
                 Lightener 
                 32.0% 
                 30.0% 
                 Microspheres 
               
               
                 Retarder 
                 0.20% 
                 0.20% 
                 Boric Acid 
               
               
                 Water 
                 34.8% 
                 35.9% 
                 Water 
               
               
                   
               
             
          
         
       
     
         [0034]    Monopotassium phosphate and magnesium oxide together form a binder in the slurry and thus in the to-be-formed core of the EcoRock sheathing panel. Calcium carbonate, cornstarch and ceramic microspheres form a filler in the slurry while the biofibers strengthen the core, when the slurry has hardened. Boric acid is a retardant to slow the exothermic reaction and thus slow down the setting of the slurry. 
         [0035]    In terms of manufacturing steps, the water, equivalent to about thirty six (36%) of the dry mix by weight, is added to the dry mix to form a slurry. The wet mix (termed the “initial slurry”) is mixed by the mixer in one embodiment for three (3) minutes. Mixers of many varieties may be used, such as a pin mixer, provided the mix can be quickly removed from the mixer prior to hardening. 
         [0036]    In order to meet all of the sheathing material requirements, the bulk EcoRock may not have a water vapor permeability acceptable for all wall designs. For this reason, several embodiments of the invention involve fibers or tubes that allow for transmission of water vapor from one surface of the panel to the opposite surface. The tubes can be observed as a number of pores across the panel from one surface to the other surface. A representation of such a porous surface is shown in  FIG. 1  in a perspective view. 
         [0037]      FIG. 1  shows a proposed embodiment of the present invention whereby the novel cement mixture is formed into water vapor permeable panels. Panel  100  is of typical construction panel dimensions of approximately 4 feet by 8 feet by ⅝ inch thick, or 4 feet by 12 feet by 1 inch thick, or another set of dimensions typical to the construction industry. The panel  100  features an array of through penetrations (pores)  102  with a prescribed hole diameter and spacing to ensure the proper water vapor transmission while maintaining the structural integrity of panel  100 . Example hole counts are from 50 to 5000 per 4 foot by 8 foot panel. The diameter of the holes ranges from 0.2 mm to 2 mm. 
         [0038]      FIG. 2  shows a proposed embodiment of a manufacturing step for production of panel  100 . A cement slurry  204  is poured into a forming tank  202 . The slurry  204  contains a prescribed number or amount of hollow or soluble fibers  206 . The liquid cement mixture is allowed to cure in the forming tank  202 . The dimensions of the tank are chosen to optimize the manufacturing efficiency and yield of construction panels of typical dimensions from approximately 2 feet by 8 feet to approximately 4 feet by 12 feet. In one embodiment, the tank dimensions could be a height  208  of 26 inches by a width  210  of 97 inches, by tens of feet long, depending only on the total weight constraints. The fibers  206  may be of various lengths and diameters. They may also be straight or bent or curled along their length. In one embodiment, the fibers  206  consist of hollow glass tubes approximately 60 mm long with an inside diameter of 200 microns. Such tubes are available from Accu-Glass of St. Louis, Mo. In another embodiment, the fibers  206  are glass tubes about 150 mm long with an inside diameter of about 1 mm. These tubes are also available from Accu-Glass of St. Louis, Mo. In another embodiment, the fibers  206  may consist of a soluble polymer 60 mm long and 200 microns in diameter. Soluble Polymer fibers are disclosed in U.S. Pat. Nos. 3,066,999, 3,689,469, 4,942,089, 5,181,966, 5,187,226, 6,780,832 and 7,001,976 and U.S. published application No. WO/2003/097703. In another embodiment, the fibers  206  are approximately 150 mm long and approximately 1 mm in diameter. In another embodiment, the fibers  206  may consist of a material such as paraffin with a melting point below 200 degrees Celsius, approximately 60 mm long and approximately 200 microns in diameter. In another embodiment, the fibers are made from another soluble material such as starch as disclosed in U.S. Pat. No. 4,853,168. The low melting point fiber material may be paraffin, olefin, PVA, or another similar material. Many different fiber lengths and fiber diameters are possible in accordance with this invention. 
         [0039]      FIG. 2A  shows the cured cement mixture as a single large ingot  212  following extraction from the forming tank. Individual sheathing panels  214  are created by slicing the ingot at prescribed intervals  216 . The interval distance is selected according to the desired panel thickness. It is important to note that the panels  214  have fibers  218  oriented in parallel with the thickness dimension (i.e. the fibers extend through each panel from one surface to the other surface). This allows for transport of water vapor. 
         [0040]    One resulting panel is shown in  FIG. 3 . The extended surfaces of sheathing panel  300  show a large number of pores  304 . These are the exposed ends of the filler hollow tubes or soluble fibers  306 . The holes are again of a number and diameter according to the preferred panel permeance of 10-20 perms without allowing the transmission of liquid water. Practical hole diameters range from 0.2 to 2 mm. The panel is shown in cross section in  FIG. 3A  where the holes  304  and traversing fibers  306  are visible. 
         [0041]    If the fibers consist of a soluble material such as a water soluble polymer, the panel must be dipped in a liquid bath for a selected time to dissolve the fibers. In one embodiment, the fibers are water soluble and the solvent liquid is water. This process is shown in  FIG. 4  where a liquid bath  402 , a dissolving liquid (water)  404  and the sheathing panel to be treated  406  are shown in relationship to each other. The panel may be dipped for a time range from seconds to days depending upon the soluble polymer, the solvent liquid, and the physical arrangement (e.g. number and diameter) of the fibers. Alternately, the panels may pass horizontally through a liquid shower or mist as necessary. The panels are fabricated of such materials that dipping the panels in water does not degrade the structural integity of the panels after the water soluble polymer has been dissolved. A suitable fiber that is currently commercially available is one made from polyvinyl alcohol (PVA). These fibers are available from multiple suppliers of polyvinyl alcohol (PVA) including Sinopec Shanghai Petrochemical Company Limited of Shanghai, China, Nantong Yimian Textile Co., Ltd. of Jiangsu, China, Texchem Materials of Subang Jaya, Malaysia, Kuraray Co., Ltd. of Osaka, Japan and others. PVA fibers are in common use in carpets and textiles. Their typical water dissolution temperature is from 20 to 90 degrees Celsius with a dissolving time of several minutes to several hours, depending on their particular chemistry and geometry. 
         [0042]    The processing of the slurry may occur using several different techniques depending on a number of factors such as quantity of boards required, manufacturing space and familiarity with the process by the engineering staff. An example of such a process is given in  FIG. 5 . 
         [0043]    In the processes of this invention, an exothermic reaction between the binder components starts naturally once water is added to the dry mix to form a slurry and the exothermic reaction heats the slurry. The reaction time can be controlled by many factors including total composition of slurry, percent (%) binder by weight in the slurry, the fillers in the slurry, the amount of water or other liquids in the slurry and the addition of a retarder such as boric acid to the slurry. Retarders slow down the reaction. Alternate retardants can include borax, sodium tripolyphosphate, sodium sulfonate, citric acid and many other commercial retardants common to the industry. 
         [0044]      FIG. 5  shows the simplicity of the two-step process of this invention: namely mixing the slurry with unheated water and then forming the wallboards from the slurry. An optional third step is shown in  FIG. 5  wherein the third step involves dipping the wallboard produced in the second step into a liquid (water if the soluble fibers are water soluble) to remove the soluble fibers thereby to create the desired perm value for the sheathing panel. The actual perm value of the sheathing is a function of the number of soluble fibers, the lengths and diameters of the soluble fibers and the number of the soluble fibers which extend across the complete thickness of the panel. Only a fraction of the total number of soluble fibers will extend across the panel from one surface to the other surface and thereby affect the vapor transmission through the panel. When the soluble fibers which extend from one surface to the other surface of the panel are dissolved, the volume occupied by these fibers then is available to allow the transmission of vapor from one side to the other side of the panel. It should be recognized that even fibers which extend to only one surface of the panel will also be dissolved by the liquid. Some moisture will pass along the channels previously occupied by these fibers and will ultimately diffuse through the remaining portions of the panel to the opposite surface. However, the effect on the vapor transmissivity of the panel is small because the perm rating of the panel is basically controlled by the number of soluble fibers which extend from one surface to the other surface of the panel, for the number of soluble fibers in the slurry used to form the panel being in excess of ten thousand fibers per panel. 
         [0045]    The third step in  FIG. 5  can be avoided if the fibers added to the panel are hollow. 
         [0046]    The wallboards can either be formed in molds or formed using a conveyor system of the type used to form gypsum wallboards and then cut to the desired size. 
         [0047]    In the process of  FIG. 5 , the slurry starts thickening quickly, the exothermic reaction proceeds to heat the slurry and eventually the slurry sets into a hard mass. Typically maximum temperatures of 40° C. to 90° C. have been observed depending on filler content and size of mix. The hardness can also be controlled by fillers, and can vary from extremely hard and strong to soft (but dry) and easy to break. A range of suitable formulations with varied filler content is given in Table 2. Set time, the time necessary to achieve a slurry strength sufficient to remove the cured slurry (i.e.“cement”) from forming tanks, can be designed from twenty (20) seconds to days, depending on the additives or fillers. For instance, boric acid can extend the set time from seconds to hours where powdered boric acid is added to the binder in a range by weight of 0% (seconds) to 4% (hours). While a set time of twenty (20) seconds leads to extreme productivity, the slurry may begin to set too soon for high quality manufacturing, and thus the set time should be adjusted to a longer period of time typically by adding boric acid. The use of one and two tenths percent (1.2%) by weight of boric acid gives approximately a four minute set time. 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                   
                   
                 Final 
               
               
                   
                   
                   
                 mixture 
               
               
                   
                   
                 Percentage 
                 strength (psi) 
               
               
                   
                   
                 filler by 
                 per ASTM 
               
               
                   
                 Filler Material 
                 volume (%) 
                 C109 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Dualite Microspheres 
                 0% 
                 7000 
               
               
                   
                   
                 1% 
                 3000 
               
               
                   
                   
                 2% 
                 1625 
               
               
                   
                   
                 3% 
                 1000 
               
               
                   
                   
                 5% 
                 450 
               
               
                   
                 Fillite 500 Microspheres 
                 0% 
                 7000 
               
               
                   
                   
                 10% 
                 4500 
               
               
                   
                   
                 20% 
                 2750 
               
               
                   
                   
                 30% 
                 2000 
               
               
                   
                   
                 40% 
                 900 
               
               
                   
                 Perlite 
                 0% 
                 7000 
               
               
                   
                   
                 3% 
                 3500 
               
               
                   
                   
                 6% 
                 2000 
               
               
                   
                   
                 9% 
                 1050 
               
               
                   
                   
                 12% 
                 750 
               
               
                   
                   
               
             
          
         
       
     
         [0048]    An exothermic reaction will begin almost immediately after removal of the slurry from the mixer and continue for several hours, absorbing most of the water in the slurry into the reaction. Boards can be cut and removed in less than 30 minutes, depending on handling equipment available. All of the water has not yet been used in the reaction, and some absorption of the water will continue for many hours. Within 24-48 hours, the majority of water has been absorbed, with some evaporation occurring as well. This can be accomplished on racks at room temperature with no heat required. Drying time will be faster at higher temperatures and slower at lower temperatures above freezing. Residual drying will continue to increase at higher temperatures, however it is not beneficial to apply heat (above room temperature) due to the need of the exothermic reaction to utilize the water that would thus be evaporated too quickly. 
         [0049]    The resulting boards (the “finished product”) have strength characteristics similar to or greater than the strength characteristics of gypsum sheathing panels, and can be easily installed in the field. 
         [0050]    As a feature of this invention, the ratio of one binder component to the other binder component by weight can be varied to minimize the cost of materials. A combination of 10% of one binder ingredient to 90% of the other has been mixed demonstrating an acceptable exothermic reaction. 
         [0051]    As illustrated in  FIG. 6 , the EcoReock sheathing panel  100  is mounted is mounted to the building&#39;s structural framing  604 . A typical concrete foundation  602  supports the framing  604 , both constructed in a manner prescribed by the local or national building code. The EcoRock sheathing panel  100  is placed across the exterior face of the framing members  604  and fastened with mechanical fasteners  606  such as nails or screws. The specific type and spacing is determined by local or national building codes. For the purposes of clarity, the array of very small through pore or penetrations  102  across the face of the panel  100  are not shown in this figure. 
         [0052]    Other embodiments of this invention will be obvious in view of the above disclosure.