Abstract:
A ceramic composition is herein disclosed, which is a lead-type perovskite compound capable of being subjected to low temperature-sintering among ceramic compositions for use in making capacitors, which has a high dielectric constant at room temperature of not less than 10000, a low temperature-dependency of the dielectric constant and a low decrease in capacitance upon application of a DC bias and which comprises, as a main constituent, a ternary system comprising lead magnesium niobate: [Pb(Mg 1/3  Nb 2/3 )O 3  ], lead nickel niobate: [Pb(Ni 1/3  Nb 2/3 )O 3  ] and lead titanate: [PbTiO 3  ] in which part of the Pb 2+   ions present in the ternary system are substituted with a desired amount of Sr 2+   ions, Ba 2+   ions or Ca 2+   ions.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a ceramic composition and in particular to a ceramic composition which has a high dielectric constant and insulation resistance, a low rate of variation in dielectric constant with temperature and a low decrease in dielectric constant upon application of a DC bias. 
     2. Description of the Prior Art 
     When a multilayer capacitor is produced from a ceramic composition, the ceramic composition should be selected so that it satisfies several requirements. The composition should have a dielectric constant and a specific resistivity as high as possible and that a rate of variation in dielectric constant with temperature, dielectric loss and drop in dielectric constant due to DC bias application should be as low as possible. Among ceramic compositions having high dielectric constants, those mainly comprising barium titanate (BaTiO 3 ) are well known. However, these compositions require a high sintering temperature. Accordingly, an additive such as calcium titanate (CaTiO 3 ) or lead titanate (PbTiO 3 ) is incorporated to improve temperature-dependent characteristics. However the sintering temperature thereof is still on the order of not less than 1300° C. For this reason, when the ceramic composition mainly comprising barium titanate is used in making a multilayer ceramic capacitor, materials for internal electrodes thereof are limited to, for example, noble metals (e.g., platinum and palladium) which can withstand such a high sintering temperature. Further, the dielectric constant achieved by these dielectric ceramic compositions is at highest about 8000. The dielectric constant thereof may be increased, but, at a cost of temperature stability. More specifically, these ceramic compositions simply satisfy Y5V characteristics (-30° to 85° C.; +22%, -82%) as defined in the EIA Standards. 
     Although a ceramic material showing a low rate of variation in dielectric constant with temperature can be produced from the conventional material, the dielectric constant of the resulting ceramic composition is too low (on the order of about 2000) to use as a material for capacitors. 
     To reduce the expenses for producing multilayer ceramic capacitors, it is necessary to develop a ceramic composition capable of being sintered at a low temperature on the order of not more than 1150° C., and which uses less expensive materials for internal electrodes of capacitors such as those mainly comprising silver or nickel. Recently, there have been proposed various lead-based composite perovskite type compounds having low sintering temperatures and high dielectric constants. For instance, a ternary composition comprising lead magnesium niobate [Pb(Mg1/3Nb2/3)O 3  ], lead nickel niobate [Pb(Ni1/3Nb2/3)O 3  ] and lead titanate (PbTiO 3 ) can achieve a dielectric constant at room temperature of not less than 10000 (see U.S. Pat. No. 4,712,156). However, this three-component system suffers from a problem of high temperature-dependency of the dielectric constant. Moreover, the capacitances thereof are greatly reduced upon application of a DC bias and correspondingly, the resulting capacitors are greatly limited in their practical applications. 
     SUMMARY OF THE INVENTION 
     Accordingly, an object of the present invention is to provide a ceramic composition which comprises the foregoing three-component system and exhibits a high dielectric constant on the order of not less than 10000, a substantially improved temperature-dependency thereof and a small drop in capacitance upon application of a DC bias. 
     The foregoing and other objects and features of the present invention will be apparent from the following description. 
     According to the present invention, there is provided a ceramic composition which comprises, as a main constituent, a ternary system essentially consisting of lead magnesium niobate [Pb(Mg 1/3  Nb 2/3 )O 3  ], lead nickel niobate, [Pb(Ni 1/3  Nb 2/3 )O 3  ] and lead titanate [PbTiO 3  ] and being expressed by the following general formula: [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  wherein the subscripts x, y and z satisfy the following relation: x+y+z=1.0 and fall within the range defined by and be on the line segments joining the following seven points (a) to (g) which are given by the coordinates: 
     
         ______________________________________(x = 0.10,  y = 0.70,    z = 0.20)   (a)(x = 0.10,  y = 0.475,   z = 0.425)  (b)(x = 0.625, y = 0.05,    z = 0.325)  (c)(x = 0.75,  y = 0.05,    z = 0.20)   (d)(x = 0.75   y = 0.15,    z = 0.10)   (e)(x = 0.50,  y = 0.40,    z = 0.10)   (f)(x = 0.15,  y = 0.70,    z = 0.15)   (g)______________________________________ 
    
     on the triangular ternary-system diagram; and wherein part of lead ions (Pb 2+ ) of the main constituent are substituted with 0.01 to 30 mole % of strontium ions (Sr 2+ ), 0.01 to 25 mole % of barium ions (Ba 2+ ) or 0.01 to 25 mole % of calcium ions (Ca 2+ ) 
    
    
     BRIEF EXPLANATION OF THE DRAWINGS 
     FIG. 1 is the ternary-system diagram for Pb(Mg 1/3  Nb 2/3 )O 3  -Pb(Ni 1/3  Nb 2/3 )O 3  -PbTiO 3  showing the acceptable compositional range of the main constituent of the ceramic composition of the present invention; 
     FIG. 2 is a graph showing the temperature-dependency of the dielectric constant of an embodiment of the ceramic composition according to the present invention in which x, y and z are 0.50, 0.30 and 0.20 respectively and the amount of Sr 2+  -substitution is 0, 10 or 30 mole %; 
     FIG. 3 is a graph in which the rate of variation in capacitance observed when a DC bias is applied to a multilayer ceramic capacitor is plotted against the strength of DC electric field per layer of the capacitor (as determined in Example 2 and Comparative Example 1); 
     FIG. 4 is a graph showing the temperature-dependency of the dielectric constant of a further embodiment of the ceramic composition according to the present invention in which x, y and z are 0.50, 0.30 and 0.20 respectively and the amount of Ba 2+   substitution is 0, 10 or 25 mole %; 
     FIG. 5 is a graph in which the rate of variation in capacitance observed when a DC bias is applied to a multilayer ceramic capacitor is plotted against the strength of DC electric field per layer of the capacitor (as determined in Example 4 and Comparative Example 2); 
     FIG. 6 is a graph showing the temperature-dependency of the dielectric constant of a further embodiment of the ceramic composition according to the present invention in which x, y and z are 0.50, 0.30 and 0.20 respectively and the amount of Ca 2+  -substitution is 0, 10 or 25 mole %; and 
     FIG. 7 is a graph in which the rate of variation in capacitance observed when a DC bias is applied to a multilayer ceramic capacitor is plotted against the strength of DC electric field per layer of the capacitor (as determined in Example 6 and Comparative Example 3). 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The ternary-system diagram of the Pb(Mg 1/3  Nb 2/3 )O 3  -Pb(Ni 1/3  Nb 2/3 )O 3  -PbTiO 3  system, illustrating the compositional range of the main constituent of the ceramic composition of the present invention is shown in FIG. 1. In this figure (a) to (g) are coordinates in the ternary-system diagram and the acceptable compositional range is shown as the shadowed portion in the figure including the boundary lines. 
     In the ceramic composition of the present invention, the amount of Sr 2+   ions with which Pb 2+   ions in the main constituent are substituted ranges from 0.01 to 30 mole %, preferably 2 to 20 mole %; that of Ba 2+   ions ranges from 0.01 to 25 mole %, preferably 2 to 20 mole %; and that of Ca 2+   ions ranges from 0.01 to 25 mole %, preferably 2 to 20 mole %. 
     The present invention will hereinafter be described in more detail with reference to the following nonlimitative working Examples and the effects practically achieved by the present invention will also be discussed in detail in comparison with Comparative Examples. 
     EXAMPLE 1 
     In this Example, there were used, as starting materials, lead oxide (PbO), magnesium oxide (MgO), niobium oxide (Nb 2  O 5 ), nickel oxide (NiO), titanium oxide (TiO 2 ) and strontium carbonate (SrCO 3 ) and these starting materials were weighed so as to satisfy the compounding ratio as shown in Tables 1 to 3. 
     These weighed starting materials were subjected to wet-milling and mixing in a ball mill, calcined at 800° to 850° C., followed by re-milling of the resulting powder in a ball mill, filtration, drying, addition of an organic binder, sizing and pressing to give two disk-like samples having a diameter of about 16 mm and a thickness of about 2 mm as well as a cylindrical sample having a diameter of about 16 mm and a thickness of about 10 mm. The latter was used in the subsequent determination of sintering density. 
     Then the pressed disk-like samples were fired at a temperature ranging from 1100° to 1150° C. for one hour. Then silver electrodes were printed onto both faces of the fired disk-like samples at 600° C. and the capacitances and dielectric losses thereof were determined at a frequency of 1 kHz, a voltage of 1 V r.m.s. and room temperature using a digital LCR meter to obtain the dielectric losses and capacitances thereof. Moreover, an electric current upon application of a DC voltage of 50 V for one minute to the samples was determined by an insulation resistance tester to obtain the specific resistivity of each sample. The dielectric constant was obtained from the capacitance determined. In addition, capacitances were determined at -30° and 85° C. to obtain the variation in dielectric constant with temperature as a value relative to that observed at 20° C. 
     Tables 1 to 3 show the compounding ratio: x, y and z of the main constituent: [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z   of the resulting ceramic composition and the amount of Sr 2+   ions with which Pb 2+   ions in the main constituent were substituted, and Tables 4 to 6 show the dielectric constant as determined at room temperature, the dielectric loss, the specific resistivity and the variations of dielectric constants (relative to that observed at 20° C.) determined at -30° C. and 85° C. 
     In these table, the asterisk (*) means that the compounding ratio of the main constituent of the corresponding sample is beyond the range defined in the present invention and the double asterisk (**) means that the amount of Sr 2+  -substitution thereof is beyond the range defined in the present invention. 
     
                       TABLE 1______________________________________Compounding Ratios of Sample Nos. 1 to 20                                Amount                                of Sr.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________ 1*   80           0          20     10  2** 75          15          10     0 3    75          15          10     2 4    75          15          10     10  5** 75           5          20     0 6    75           5          20     10 7    75           5          20     30  8** 65          10          25     0 9    65          10          25     10 10** 62.5         5          32.5   011    62.5         5          32.5   30 12** 62.5         5          32.5   35 13** 60          20          20     014    60          20          20     1015    60          20          20     30 16*  50          40          10     0 17*  50          40          10     5 18** 50          30          20     019    50          30          20     0.0120    50          30          20     2______________________________________ 
    
     
                       TABLE 2______________________________________Compounding Ratios of Sample Nos. 21 to 40                                Amount                                of Sr.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________21    50          30          20     1022    50          30          20     30 23** 50          20          30     024    50          20          30     1025    50          20          30     30 26*  50          10          40     0 27*  50          10          40     30 28*  50          10          40     40 29** 40          40          20     030    40          40          20     0.0131    40          40          20     10 32** 40          30          30     033    40          30          30     1034    40          30          30     30 35** 30          40          30     036    30          40          30     1037    30          40          30     30 38** 20          50          30     039    20          50          30     1040    20          50          30     30______________________________________ 
    
     
                       TABLE 3______________________________________Compounding Ratios of Sample Nos. 41 to 52                                Amount                                of Sr.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________ 41** 10          67.5        22.5   042    10          67.5        22.5   0.0143    10          67.5        22.5   2 44** 10          47.5        42.5   045    10          47.5        42.5   30 46** 10          47.5        42.5   40 47*   5          60          35     0 48*   5          60          35     10 49** 10          70          20     050    10          70          20     2 51** 15          70          15     052    15          70          15     2______________________________________ 
    
     
                       TABLE 4______________________________________Properties of Samples Nos. 1 to 20     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________ 1*     5580    1.5      6.8 × 10.sup.10                            -60.2  -10.5  2**  22560    7.3      2.1 × 10.sup.11                            -63.7  -64.5 3     21770    3.8      8.2 × 10.sup.11                            -54.3  -59.1 4      8560    1.1      1.3 × 10.sup.12                            -35.2  -55.1  5**  13710    6.9      1.7 × 10.sup.11                            -64.1  +57.3 6     12840    2.1      9.8 × 10.sup.11                            -50.6  -33.1 7      5500    0.5      1.7 × 10.sup.13                            +2.3   -45.3  8**  10320    7.1      2.6 × 10.sup.11                            -54.1  +72.1 9     14560    2.3      1.1 × 10.sup.12                            -54.7  -27.6 10**   8310    7.6      2.9 × 10.sup.11                            - 52.6 +51.011      8680    2.1      2.6 × 10.sup.13                            -54.3  -47.2 12**   6100    2.5      7.8 × 10.sup.12                            -46.1  -58.5 13**  16720    6.5      3.1 × 10.sup.11                            -62.3  +13.714     12850    2.0      2.5 × 10.sup.12                            -54.1  -32.615      7240    0.7      2.9 × 10.sup.13                            -35.2  -15.6 16*   15200    3.1      3.0 × 10.sup.11                            -56.5  -70.3 17*    6800    0.5      1.9 × 10.sup.12                            +11.5  -61.5 18**  17080    6.9      3.9 × 10.sup.11                            -68.5  -5.219     19560    2.7      9.1 × 10.sup.11                            -57.1  -27.4 20*   20500    1.2      2.7 × 10.sup.12                            -54.5  -41.1______________________________________ 
    
     
                       TABLE 5______________________________________Properties of Samples Nos. 21 to 40     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________21     14100    0.4      6.1 × 10.sup.12                            -8.5   -54.822      7320    0.1      2.0 × 10.sup.13                            +15.8  -50.1 23**  10240    6.5      4.9 × 10.sup.11                            -21.5  +41.524     12180    3.2      6.7 × 10.sup.12                            -50.8  +2.325      8680    0.9      1.9 × 10.sup.13                            -52.6  -43.6 26*    6120    6.3      4.5 × 10.sup.11                            -20.3  +85.1 27*    6420    4.9      2.2 × 10.sup.13                            -37.6  +40.5 28*    4270    3.7      2.0 × 10.sup.13                            -48.3  -11.5 29*   18700    6.7      4.1 × 10.sup.11                            -62.6  -18.330     19150    3.9      8.2 × 10.sup.11                            -57.3  -25.831     10400    0.2      2.7 × 10.sup.12                            -15.8  -53.8 32**   8650    6.8      4.3 × 10.sup.11                            -29.8  +36.333     11300    3.6      3.6 × 10.sup.12                            -37.5  +11.234      8640    0.9      2.8 × 10.sup.13                            -49.7  -40.5 35**  12510    7.0      4.6 × 10.sup.11                            -41.7  +61.336     10800    4.1      3.4 × 10.sup.12                            -56.8  +20.637      9790    1.0      3.0 × 10.sup.13                            -47.3  -50.5 38**  13300    6.8      4.5 × 10.sup.11                            -50.7  +81.339     13850    4.6      3.1 × 10.sup.12                            -49.6  +19.640      9230    0.3      3.4 × 10.sup.13                            -40.6  -44.8______________________________________ 
    
     
                       TABLE 6______________________________________Properties of Samples Nos. 41 to 52     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________ 41**  24510    3.1      5.8 × 10.sup.11                            -71.4  -67.842     21400    2.9      8.6 × 10.sup.11                            -60.3  -61.243     18740    1.8      1.7 × 10.sup.12                            -48.1  -55.8 44**   7210    7.5      6.0 × 10.sup.11                            -36.5  +39.345     10800    2.1      2.2 × 10.sup.13                            -52.6  -45.5 46**   5320    1.2      8.6 × 10.sup.12                            -41.5  -57.2 47*    7220    6.5      5.7 × 10.sup.11                            -46.5  +42.6 48*    6830    4.7      9.3 × 10.sup.11                            -52.8  +3.7 49**   9500    4.2      6.5 × 10.sup.12                            -52.3  -43.250      7960    0.9      8.8 × 10.sup.12                            -30.9  -39.7  51** 16250    2.3      4.3 × 10.sup.12                            -53.8  -41.252     12240    1.0      7.3 × 10.sup.12                            -34.6  -38.8______________________________________ 
    
     Moreover, to make clear the effect of Sr 2+  -substitution, there is shown, in FIG. 2, the temperature-dependency of the dielectric constant of a ceramic composition whose compounding ratio (x, y, z) was (0.50, 0.30, 0.20) and in which the amount of Sr 2+  -substitution was 0, 10 or 30 mole %. 
     As seen from the data shown in FIG. 2, there is observed a dielectric constant-depressing effect due to the Sr 2+  -substitution and accordingly the Curie point of the main constituent is shifted towards the lower temperature side. Further, as seen from the data listed in Tables 1 to 6, the composition of the present invention in which part of the Pb 2+   ions in the main constituent, a ternary system essentially consisting of [Pb(Mg 1/3  Nb 2/3 )O 3  ]-[Pb(Ni 1/3  Nb 2/3 )O 3  ]-[PbTiO 3  ], is substituted with Sr 2+   ions has high dielectric constant and specific resistivity at room temperature as well as a low variation in dielectric constant with temperature and thus can satisfy the Y5U characteristics (-30° to 85° C.; +22%, -56%) as defined in the EIA Standards. Furthermore, the composition of the present invention can be sintered at a relatively low temperature on the order of not more than 1150° C. and correspondingly a silver-palladium alloy can be used as a material for the internal electrodes of multilayer ceramic capacitors. 
     EXAMPLE 2 
     The same procedures used in Example 1 were repeated to give a dielectric powder except that lead oxide, magnesium oxide, titanium oxide, nickel oxide, niobium oxide and strontium carbonate were correctly dispensed so that the resulting dielectric powder had a compounding ratio: (x, y, z) in the main ingredient represented by [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ].sub. y [PbTiO 3  ] z  of (0.50, 0.30, 0.20) and 10 mole % of Pb 2+   ions were substituted with Sr 2+   ions. 
     The resulting dielectric powder was dispersed in an organic solvent, kneaded with an organic binder to give a slurry and the resulting slurry was formed into a film having a thickness of 40 μm according to the doctor blade technique currently used. Then a paste for an internal electrode was printed on the film in accordance with the usual screen printing method, followed by stamping out the film into a desired shape, lamination, hot-pressing to give a multilayer body which was then cut into pieces having a desired shape to obtain green chips for capacitors. The resulting green chips were heated to desired temperatures to remove the binder and to fire and then a silver paste was applied thereto to form external electrodes. 
     The capacitance of the capacitor was determined at room temperature by applying an alternating current having a frequency of 1 kHz and a voltage of 1 V r.m.s. using a digital LCR meter while a DC bias of 0 to 50 V was applied to the multilayer ceramic capacitor with a digital multi meter. The results thus obtained are plotted in FIG. 3. 
     COMPARATIVE EXAMPLE 1 
     The same procedures used in Example 2 were repeated except for using a composition having the compounding ratio (x, y, z) in the main constituent represented by [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  of (0.20, 0.60, 0.20) and free of Sr 2+  -substitution to give a capacitor and the capacitance thereof upon applying a DC bias was determined in the same manner described in Example 2. The results obtained are plotted in FIG. 3 together with the results obtained in Example 2. 
     The results shown in FIG. 3 clearly indicate that the capacitor obtained from the ceramic composition of the present invention in which part of Pb 2+   ions in the main constituent was substituted with Sr 2+  ions has the DC bias characteristics superior to those for the capacitor obtained using the compositions of Comparative Example 1, which was free of Sr 2+  -substitution. 
     EXAMPLE 3 
     In this example, there were used, as starting materials, lead oxide (PbO), magnesium oxide (MgO), niobium oxide (Nb 2  O 5 ), nickel oxide (NiO), titanium oxide (TiO 2 ) and barium carbonate (BaCO 3 ) and these starting materials were weighed so as to satisfy the compounding ratio as shown in Tables 7 to 9. 
     These weighed starting materials were subjected to wet-milling and mixing in a ball mill, calcined at 800° to 850° C., followed by re-milling of the resulting powder in a ball mill, filtration, drying, addition of an organic binder, sizing and pressing to give two disk-like samples having a diameter of about 16 mm and a thickness of about 2 mm and a cylindrical sample having a diameter of about 16 mm and a thickness of about 10 mm. The latter was used in the subsequent determination of sintering density. 
     Then the pressed disk-like samples were fired at a temperature ranging from 1100° to 1150° C. for one hour. Silver electrodes were printed onto both faces of the fired disk-like samples at 600° C. and the capacitances and dielectric losses thereof were determined at a frequency of 1 kHz, an AC voltage of 1 V r.m.s. and room temperature using a digital LCR meter. Then a current upon application of a DC voltage of 50 V to the samples for one minute was determined using an insulation resistance tester to determine specific resistivities of the samples. The dielectric constant was obtained from the capacitance determined above. Further, the capacitances at -30° and 85° C. were determined to obtain variations in dielectric constants in terms of values relative to that observed at 20° C. 
     Tables 7 to 9 show the compounding ratio: x, y and z of the main constituent: [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  of the resulting ceramic composition and the amount of Ba 2+  -substitution (mole %) and Tables 10 to 12 show the dielectric constant at room temperature, the dielectric loss, the specific resistivity and the variations of dielectric constants determined at -30° C. and 85° C. (in terms of values relative to that observed at 20° C.) which were determined in this Example. 
     In these tables, the asterisk (*) means that the compounding ratio of the main constituent of the corresponding sample is beyond the range defined in the present invention and double asterisk (**) means that the amount of Ba 2+  -substitution is beyond the range defined in the present invention. 
     
                       TABLE 7______________________________________Compounding Ratios of Sample Nos. 1 to 20                                Amount                                of Ba.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________ 1*   80           0          20     10  2** 75          15          10     0 3    75          15          10     1 4    75          15          10     5  5** 75           5          20     0 6    75           5          20     10 7    75           5          20     25  8** 65          10          25     0 9    65          10          25     10 10** 62.5         5          32.5   011    62.5         5          32.5   25 12** 62.5         5          32.5   30 13** 60          20          20     014    60          20          20     515    60          20          20     1016    60          20          20     25 17*  50          40          10     0 18*  50          40          10     2 19** 50          30          20     020    50          30          20     0.01______________________________________ 
    
     
                       TABLE 8______________________________________Compounding Ratios of Sample Nos. 21 to 40                                Amount                                of Ba.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________21    50          30          20     222    50          30          20     1023    50          30          20     25 24** 50          20          30     025    50          20          30     1026    50          20          30     25 27*  50          10          40     0 28*  50          10          40     25 29*  50          10          40     30 30** 40          40          20     031    40          40          20     0.0132    40          40          20     10 33** 40          30          30     034    40          30          30     1035    40          30          30     25 36** 30          40          30     037    30          40          30     1038    30          40          30     25 39** 20          50          30     040    20          50          30     10______________________________________ 
    
     
                       TABLE 9______________________________________Compounding Ratios of Sample Nos. 41 to 52                                Amount                                of Ba.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________41    20          50          30     25 42** 10          67.5        22.5   043    10          67.5        22.5   2 44** 10          47.5        42.5   045    10          47.5        42.5   25 46** 10          47.5        42.5   30 47*   5          60          35     0 48*   5          60          35     10 49** 10          70          20     050    10          70          20     2 51** 15          70          15     052    15          70          15     2______________________________________ 
    
     
                       TABLE 10______________________________________Properties of Samples Nos. 1 to 20     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________ 1*     7630    3.8      7.9 × 10.sup.10                            -59.3  -22.5  2**  22560    7.3      2.1 × 10.sup.11                            -63.7  -64.5 3     20810    4.1      6.3 × 10.sup.11                            -55.3  -58.1 4     12340    1.9      1.1 × 10.sup.12                            -52.6  -51.2  5**  13710    6.9      1.7 × 10.sup.11                            -64.1  +57.3 6     11530    2.3      7.7 × 10.sup.11                            -57.3  -21.7 7      8150    0.9      6.5 × 10.sup.12                            -38.1  -48.6  8**  10320    7.1      2.6 × 10.sup.11                            -54.1  +72.1 9     12800    2.6      9.0 × 10.sup.11                            -49.2  -7.6 10**   8310    7.6      2.9 × 10.sup.11                            - 52.6 +51.011      9560    2.7      1.3 × 10.sup.13                            -48.7  -26.3 12**   7630    3.1      7.2 × 10.sup.12                            -49.3  -53.6 13**  16720    6.5      3.1 × 10.sup.11                            -62.3  +13.714     12380    2.9      8.3 × 10.sup.11                            -45.6  -39.515      9710    2.2      1.6 × 10.sup.12                            -40.3  -32.116      7320    1.1      1.4 × 10.sup.13                            +16.4  -51.6 17*   15200    3.1      3.0 × 10.sup.11                            -56.5  -70.3 18*    8150    2.6      5.6 × 10.sup.11                            -27.5  -67.1 19**  17080    6.9      3.9 × 10.sup.11                            -68.5  -5.220     18320    3.2      7.7 × 10.sup.11                            -55.7  -31.7______________________________________ 
    
     
                       TABLE 11______________________________________Properties of Samples Nos. 21 to 40     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________21     20040    2.0      1.4 × 10.sup.12                            -58.3  -47.522     15300    1.1      3.8 × 10.sup.12                            -37.9  -55.823      7310    0.3      9.6 × 10.sup.12                            +20.5  -52.1 24**  10240    6.5      4.0 × 10.sup.11                            -21.5  +41.525     12070    3.9      2.1 × 10.sup.12                            -53.3  +32.626      7160    1.1      8.4 × 10.sup.12                            -44.4  -43.8 27*    6120    6.3      4.5 × 10.sup.11                            -20.3  +85.1 28*    5680    5.1      6.8 × 10.sup.12                            -43.9  +40.4 29*    5210    3.9      8.2 × 10.sup.12                            -46.2  +25.0 30**  18700    6.7      4.1 × 10.sup.11                            -62.6  -18.331     19620    4.2      7.4 × 10.sup.11                            -59.8  -24.532     11270    0.7      2.2 × 10.sup.12                            -42.5  -55.8 33**   8560    6.8      4.3 × 10.sup.11                            -29.8  +36.334     10890    3.9      2.7 × 10.sup.12                            -49.5  +14.735      8220    1.1      1.5 × 10.sup.13                            -51.2  -54.1 36**  12510    7.0      4.6 × 10.sup.11                            -41.7  +61.337     11980    4.7      2.1 × 10.sup.12                            -50.2  -11.638      7330    1.9      1.8 × 10.sup.13                            -34.2  -56.1 39**  13300    6.8      4.5 × 10.sup.11                            -50.7  +81.340     14550    4.8      2.1 × 10.sup.12                            -55.1  -20.7______________________________________ 
    
     
                       TABLE 12______________________________________Properties of Samples Nos. 41 to 52     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________41      6980    0.7      1.7 × 10.sup.13                            +3.3   -54.3 42**  24510    3.1      5.8 × 10.sup.11                            -71.4  -67.843     17630    1.9      9.6 × 10.sup.11                            -53.6  -54.5 44**   7210    7.5      6.0 × 10.sup.11                            -36.5  +39.345      8160    3.8      8.3 × 10.sup.12                            -51.2  -32.9 46**   6240    3.1      9.6 × 10.sup.12                            -44.8  -53.2 47*    7220    6.5      5.7 × 10.sup.11                            -46.5  +42.6 48*    8740    5.0      8.3 × 10.sup.11                            -58.6  +9.1 49**   8500    4.2      6.5 × 10.sup.12                            -52.3  -43.250      8410    1.7      8.1 × 10.sup.12                            -34.6  - 39.4 51**  16250    2.3      4.3 × 10.sup.12                            -53.8  -41.252     13060    1.3      6.5 × 10.sup.12                            -40.8  -37.2______________________________________ 
    
     Moreover, to make clear the effect of Ba 2+  -substitution, there is shown, in FIG. 4, the temperature-dependency of the dielectric constant of a ceramic composition whose compounding ratio (x, y, z) was (0.50, 0.30, 0.20) and in which the amount of Ba 2+  -substitution was 0, 10 or 25 mole %. 
     As seen from the data shown in FIG. 4, there is observed a dielectric constant-depressing effect of the Ba 2+  -substitution and accordingly the Curie point of the main constituent is shifted towards the lower temperature side. Further, as seen from the data listed in Tables 7 to 12, the composition of the present invention in which part of Pb 2+   in the main constituent, a ternary system essentially consisting of [Pb(Mg 1/3  Nb 2/3 )O 3  ]-[Pb(Ni 1/3  Nb 2/3 )O 3  ]-[PbTiO 3  ], is substituted with Ba 2+   ions has a high dielectric constant and specific resistivity at room temperature as well as a low variation in dielectric constant with temperature and thus can satisfy the Y5U characteristics (-30° to 85° C.; +22%, -56%) as defined in the EIA Standards. Furthermore, the composition of the present invention can be sintered at a relatively low temperature in the order of not more than 1150° C. and correspondingly a silver-palladium alloy can be used as a material for the internal electrodes of multilayer ceramic capacitors. 
     EXAMPLE 4 
     The same procedures used in Example 3 were repeated to give a dielectric powder except that lead oxide, magnesium oxide, titanium oxide, nickel oxide, niobium oxide and barium carbonate were correctly weighed so that the resulting dielectric powder had a compounding ratio: (x, y, z) in the main constituent represented by [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  of (0.50, 0.30, 0.20) and 10 mole % of Pb 2+   ions were substituted with Ba 2+   ions. 
     The resulting dielectric powder was dispersed in an organic solvent, kneaded with an organic binder to give a slurry and the resulting slurry was formed into a film having a thickness of 40 μm according to the doctor blade technique currently used. Then a paste for an internal electrode was printed on the film in accordance with the usual screen printing method, followed by stamping out the film into a desired shape, lamination, hot-pressing to give a multilayer body which was then cut into pieces having a desired shape to obtain green chips for capacitors. The resulting green chips were heated to desired temperatures to remove the binder and to fire and then silver paste was applied thereto to form external electrodes. 
     The capacitance of the capacitor was determined at room temperature by applying an alternating current having a frequency of 1 kHz and a voltage of 1 V r.m.s. using a digital LCR meter while a DC bias of 0 to 50 V was applied to the multilayer ceramic capacitor with a digital multi meter. The results thus obtained are plotted in FIG. 5. 
     COMPARATOR EXAMPLE 2 
     The same procedures used in Example 4 were repeated except for using a composition having the compounding ratio (x, y, z) in the main constituent represented by Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  of (0.20, 0.60, 0.20) and free of Ba 2+  -substitution to give a capacitor and the capacitance thereof upon applying a DC bias was determined in the same manner described in Example 4. The results obtained are plotted in FIG. 5 together with the results obtained in Example 4. 
     The results shown in FIG. 5 clearly indicate that the capacitor obtained from the ceramic composition of the present invention in which part of the Pb 2+   ions in the main constituent was substituted with Ba 2+  ions shows the behavior upon application of a DC bias superior to that for the capacitor obtained using the composition of Comparative Example 2, which is free of Ba 2+  -substitution. 
     EXAMPLE 5 
     In this Example, there were used, as starting materials, lead oxide (PbO), magnesium oxide (MgO), niobium oxide (Nb 2  O 5 ), nickel oxide (NiO), titanium oxide (TiO 2 ) and calcium carbonate (CaCO 3 ) and these starting materials were weighed so as to satisfy the compounding ratio as shown in Tables 13 to 15. 
     These dispensed starting materials were subjected to wet-milling and mixing in a ball mill, calcined at 800° to 850° C., followed by re-milling of the resulting powder in a ball mill, filtration, drying, addition of an organic binder, sizing and pressing to give two disk-like samples having a diameter of about 16 mm and a thickness of about 2 mm and a cylindrical sample having a diameter of about 16 mm and a thickness of about 10 mm. The latter was used in the subsequent determination of sintering density. 
     Then the pressed disk-like samples were fired at a temperature ranging from 1100° to 1150° C. for one hour. Silver electrodes were printed onto both faces of the fired disk-like samples at 600° C. and the capacitances and dielectric losses thereof were determined at a frequency of 1 kHz, a voltage of 1 V r.m.s. and room temperature using a digital LCR meter. Then a current upon application of a DC voltage of 50 V to the samples for one minute was determined using an insulation resistance tester to determine specific resistivity of the samples. The dielectric constant was obtained from the capacitance determined above. Further, the capacitances at -30° and 85° C. were determined to obtain variations in dielectric constants in terms of values relative to that observed at 20° C. 
     Tables 13 to 15 show the compounding ratio: x, y and z of the main constituent: [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  of the resulting ceramic composition, and the amount of Ca 2+  -substitution (mole %) and Tables 16 to 18 show the dielectric constant at room temperature, the dielectric loss, the specific resistivity and the variations of dielectric constants determined at -30° C. and 85° C. (in terms of values relative to that observed at 20° C.) which were determined in this example. 
     In these tables, the asterisk (*) means that the compounding ratio of the main constituent of the corresponding sample is beyond the range defined in the present invention and double asterisk (**) means that the amount of Ca 2+  -substitution is beyond the range defined in the present invention. 
     
                       TABLE 13______________________________________Compounding Ratios of Sample Nos. 1 to 20                                Amount                                of Ca.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________ 1*   80           0          20     10  2** 75          15          10     0 3    75          15          10     1 4    75          15          10     5  5** 75           5          20     0 6    75           5          20     10 7    75           5          20     25  8** 65          10          25     0 9    65          10          25     10 10** 62.5         5          32.5   011    62.5         5          32.5   25 12** 62.5         5          32.5   30 13** 60          20          20     014    60          20          20     515    60          20          20     1016    60          20          20     25 17*  50          40          10     0 18*  50          40          10     2 19** 50          30          20     020    50          30          20     0.01______________________________________ 
    
     
                       TABLE 14______________________________________Compounding Ratios of Sample Nos. 21 to 40                                Amount                                of Ca.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________21    50          30          20     222    50          30          20     1023    50          30          20     25 24** 50          20          30     025    50          20          30     1026    50          20          30     25 27*  50          10          40     0 28*  50          10          40     25 29*  50          10          40     30 30** 40          40          20     031    40          40          20     0.0132    40          40          20     10 33** 40          30          30     034    40          30          30     1035    40          30          30     25 36** 30          40          30     037    30          40          30     1038    30          40          30     25 39** 20          50          30     040    20          50          30     10______________________________________ 
    
     
                       TABLE 15______________________________________Compounding Ratios of Sample Nos. 41 to 52                                Amount                                of Ca.sup.2+ -Sample Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3             Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3                         PbTiO.sub.3                                SubstitutionNo.   (mole %)    (mole %)    (mole %)                                (mole %)______________________________________41    20          50          30     25 42** 10          67.5        22.5   043    10          67.5        22.5   2 44** 10          47.5        42.5   045    10          47.5        42.5   25 46** 10          47.5        42.5   30 47*   5          60          35     0 48*   5          60          35     10 49** 10          70          20     050    10          70          20     2 51** 15          70          15     052    15          70          15     2______________________________________ 
    
     
                       TABLE 15______________________________________Properties of Samples Nos. 1 to 20     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________ 1*     8600    4.1      9.8 × 10.sup.13                            -57.2  -25.6  2**  22560    7.3      2.1 × 10.sup.11                            -63.7  -64.5 3     25350    5.6      3.1 × 10.sup.11                            -64.8  -66.4 4     16400    1.6      8.5 × 10.sup.11                            -41.6  -55.8  5**  13710    6.9      1.7 × 10.sup.11                            -64.1  +57.3 6     10560    3.1      6.5 × 10.sup.11                            -43.1  -39.6 7      6540    1.2      2.1 × 10.sup.12                            -41.6  -53.9  8**  10320    7.1      2.6 × 10.sup.11                            -54.1  +72.1 9     12650    5.1      8.1 × 10.sup.11                            -56.1  -35.6 10**   8310    7.6      2.9 × 10.sup.11                            -52.6  +51.011      6140    4.3      3.6 × 10.sup.12                            -55.1  +5.8 12**   7520    4.4      1.8 × 10.sup.12                            -50.8  -21.5 13**  16720    6.5      3.1 × 10.sup.11                            -62.3  +13.714     13500    4.2      6.4 × 10.sup.11                            -57.0  -37.115     10650    1.6      9.6 × 10.sup.11                            -48.1  -40.516      7140    1.1      3.5 × 10.sup.12                            -11.3  -47.3 17*   15200    3.1      3.0 × 10.sup.11                            -56.5  -70.3 18*   16340    2.1      5.1 × 10.sup.11                            -32.5  -61.5 19**  17080    6.9      3.9 × 10.sup.11                            -68.5  -5.220     19160    6.1      4.5 × 10.sup.11                            -66.7  -12.3______________________________________ 
    
     
                       TABLE 17______________________________________Properties of Samples Nos. 21 to 40     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________21     21380    5.6      5.8 × 10.sup.11                            -61.3  -35.422     16550    2.1      9.6 × 10.sup.11                            -41.5  -57.323      6860    0.9      2.6 × 10.sup.12                            +21.5  -45.3 24**  10240    6.5      4.0 × 10.sup.11                            -21.5  +41.525     15320    4.5      1.1 × 10.sup.12                            -58.0  -5.526      9560    1.3      3.3 × 10.sup.12                            -47.3  -50.6 27*    6120    6.3      4.5 × 10.sup.11                            -20.3  +85.1 28*    6830    5.5      3.9 × 10.sup.12                            -43.4  +47.6 29*    5660    4.9      3.1 × 10.sup.12                            -49.7  +27.9 30**  18700    6.7      4.1 × 10.sup.11                            -62.6  -18.331     20020    5.3      5.6 × 10.sup.12                            -59.8  -24.632     12850    2.0      1.6 × 10.sup.12                            -31.3  -53.4 33**   8560    6.8      4.3 × 10.sup.11                            -29.8  +36.334     11570    4.2      9.4 × 10.sup.11                            -51.6  +3.635      7960    1.5      5.7 × 10.sup.12                            -41.5  -53.9 36**  12510    7.0      4.6 × 10.sup.11                            -41.7  +61.337     13810    5.1      9.2 × 10.sup.11                            -46.6  +8.338      8850    2.1      5.8 × 10.sup.12                            -39.6  -55.0 39**  13300    6.8      4.5 × 10.sup.11                            -50.7  +81.340     15140    5.0      9.6 × 10.sup.11                            -56.2  -12.4______________________________________ 
    
     
                       TABLE 18______________________________________Properties of Samples Nos. 41 to 52     tan δ            Specific  Δε/ε (20° C.)Sample ε           (20° C.)                    Resistivity                            -30° C.                                   85° C.No.    (20° C.)           (%)      (Ω · cm)                            (%)    (%)______________________________________41      7140    0.8      6.1 × 10.sup.12                            +8.0   -57.2 42**  24510    3.1      5.8 × 10.sup.11                            -71.4  -67.843     26500    1.6      8.4 × 10.sup.12                            -68.2  -70.5 44**   7210    7.5      6.0 × 10.sup.11                            -36.5  +39.345     10960    4.9      5.8 × 10.sup.12                            -52.9  -28.4 46**   8710    5.1      4.2 × 10.sup.12                            -48.3  -40.1 47*    7220    6.5      5.7 × 10.sup.11                            -46.5  +42.6 48*    9130    5.2      7.3 × 10.sup.11                            -60.2  +1.5 49**   8500    4.2      6.5 × 10.sup.12                            -52.3  -43.250      9340    1.2      7.8 × 10.sup.12                            -31.4  -41.3 51**  16250    2.3      4.3 × 10.sup.12                            -53.8  -41.252     13850    1.1      5.7 × 10.sup.12                            -37.9  -40.7______________________________________ 
    
     Moreover, to make clear the effect of Ca 2+  -substitution, there is shown, in FIG. 6, the temperature-dependency of the dielectric constant of a ceramic composition whose compounding ratio (x, y, z) was (0.50, 0.30, 0.20) and in which the amount of Ca 2+  -substitution was 0, 10 or 25 mole %. 
     As seen from the data shown in FIG. 6, there is observed a dielectric constant-depressing effect of the Ca 2+  -substitution and accordingly the Curie point of the main constituent is shifted towards the lower temperature side. Further, as seen from the data listed in Tables 13 to 18, the composition of the present invention in which part of the Pb 2+   ions in the main constituent, a ternary system essentially consisting of [Pb(Mg 1/3  Nb 2/3 )O 3  ]-[Pb(Ni 1/3  Nb 2/3 )O 3  ]-[PbTiO 3  ], is substituted with Ca 2+   ions have a high dielectric constant and specific resistivity at room temperature as well as a low variation in dielectric constant with temperature and thus can satisfy the Y5U characteristics (-30° to 85° C.; +22%, -56%) as defined in the EIA Standards. Furthermore, the composition of the present invention can be sintered at a relatively low temperature in the order of not more than 1150° C. and correspondingly a silver-palladium alloy can be used as a material for the internal electrodes of multilayer ceramic capacitors. 
     EXAMPLE 6 
     The same procedures used in Example 5 were repeated to give a dielectric powder except that lead oxide, magnesium oxide, titanium oxide, nickel oxide, niobium oxide and calcium carbonate were correctly weighed so that the resulting dielectric powder had a compounding ratio: (x, y, z) in the main constituent represented by [Pb(Mg 1/3  Nb 2/3 )O 3 ) x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3   z  of (0.50, 0.30, 0.20) and 10 mole % of Pb 2+   ions were substituted with Ca 2+   ions. 
     The resulting dielectric powder was dispersed in an organic solvent, kneaded with an organic binder to give a slurry and the resulting slurry was formed into a film having a thickness of 40 μm according to the doctor blade technique currently used. Then a paste for an internal electrode was printed on the film in accordance with the usual screen printing method, followed by stamping out the film into a desired shape, lamination, hot-pressing to give a multilayer body which was then cut into pieces having a desired shape to obtain green chips for capacitors. The resulting green chips were heated to desired temperatures to remove the binder and to fire and then a silver paste was applied thereto to form external electrodes. 
     The capacitance of the capacitor was determined at room temperature by applying an alternating current having a frequency of 1 kHz and a voltage of 1 V r.m.s. using a digital LCR meter while a DC bias of 0 to 50 V was applied to the multilayer ceramic capacitor with a digital multi meter. The results thus obtained are plotted in FIG. 7. 
     COMPARATIVE EXAMPLE 3 
     The same procedures used in Example 6 were repeated except for using a composition having the compounding ratio (x, y, z) in the main constituent represented by [Pb(Mg 1/3  Nb 2/3 )O 3  ] x  [Pb(Ni 1/3  Nb 2/3 )O 3  ] y  [PbTiO 3  ] z  of (0.20, 0.60, 0.20) and free of Ca 2+  -substitution to give a capacitor and the capacitance thereof upon applying a DC bias was determined in the same manner described in Example 6. The results obtained are plotted in FIG. 7 together with the results obtained in Example 6. 
     The results shown in FIG. 7 clearly indicate that the capacitor obtained from the ceramic composition of the present invention in which part of Pb 2+   ions in the main constituent was substituted with Ca 2+  ions shows the behavior upon application of a DC bias superior to that for the capacitor obtained using the composition of Comparative Example 3, which was free of Ca 2+  -substitution. 
     Incidentally, the Curie points of ceramic compositions whose main constituents are beyond the range defined in the present invention are deviated from room temperature to the temperature side much higher or lower than room temperature and, therefore, such compositions suffer from such a problem that the dielectric constants thereof at room temperature are very low, that the temperature-dependency of the dielectric constant is high within the practical temperature range or that the specific resistivities thereof are low. Moreover, if the amount of Sr 2+  -, Ba 2+  - or Ca 2+  -substitution is beyond each corresponding range defined in the present invention, the resulting composition is not applicable as a material for use in making capacitors since it suffers from such a problem that the capacitance is too low or that the Curie point thereof is greatly deviated from room temperature. 
     The ceramic composition of the present invention has a high dielectric constant at room temperature and a low temperature-dependency of dielectric constant, which can be achieved through the substitution of Pb 2+   ions in the main constituent with a predetermined amount of Sr 2+ , Ba 2+   or Ca 2+   ions since such ion-substitution permits the shift of the Curie point of the main constituent towards the low temperature side and the depression of the temperature-dependency of dielectric constant. Further, the ceramic composition of the invention shows a low decrease in the capacitance upon application of a DC bias and has a specific resistivity higher than that of the composition free of the substitution of Pb 2+   ions. Thus, the ceramic composition makes it possible to provide a multilayer ceramic capacitor having excellent temperature-dependency of dielectric constant and high reliability. Further, the firing temperature thereof is not more than 1150° C. and this allows the use of silver-palladium alloys as a material for internal electrodes of capacitors. The composition is likewise applicable to such a multilayer ceramic capacitor as a switching power source which is used while applying a DC bias since the decrease in the capacitance upon application of a DC bias is relatively small as has already been discussed above.