Abstract:
A process for removing nitrogen protoxide from gas mixtures which 5 contain it, comprising contacting with a catalyst which contains mixed oxides of copper, manganese and rare earth metals in an amount expressed as percentage by weight of CuO, MnO and rare earth metal oxide in the lowest state of valency of 20-45% CuO, 50-60% MnO, and 5-20% rare earth metal oxide.

Description:
[0001]    This application is a continuation-in-part of and claims priority to U.S. application Ser. No. 12/523,883, filed Jul. 25, 2009, which is a 371 of PCT/IB2008/000149, dated Jan. 23, 2008. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    The present invention relates to a process for catalytic decomposition of nitrogen protoxide (N 2 0) to nitrogen and oxygen and to its use for removing protoxide from gas mixtures which contain it, in particular for removal from the emissions of nitric acid and adipic acid plants. 
         [0003]    Nitrogen protoxide is a harmful greenhouse gas, much more powerful lthan carbon dioxide; moreover, it takes part in the stratosphere in the reactions which lead to destruction of the ozone layer. 
         [0004]    The main industrial sources of the generation of nitrogen protoxide are plants for producing nitric acid and adipic acid (a monomer used in the preparation of nylon 6,6 and 6,12). 
         [0005]    Nitrogen protoxide is present in the emissions from adipic acid plants in considerable amounts: a typical composition comprises, in percentage by volume: 30% N 2 0, 2% C0 2 , 2.5% H 2 0, 8-12% 0 2 , 50-150 ppm NOx. 
         [0006]    The emissions of nitric acid plants generally contain 300-1700 ppm N 2 0, 100-2000 ppm NOx, 1-4% 0 2 , the rest being nitrogen. 
         [0007]    The emission of N 2 0 from nitric acid and adipic acid plants is predicted to grow by approximately 16% over the period 2005-2020. 
         [0008]    Several catalysts are known which are used to decompose N 2 0. The main ones are constituted by noble metals supported on metallic oxides of different kinds, zeolites substituted with transition metal ions or on which metallic oxides and anionic clays are supported, such as for example hydrotalcites constituted by mixed hydroxides with a stratified structure in which exchangeable or non-exchangeable anions of different kinds and water molecules are inserted between two layers. 
         [0009]    All these catalysts have the drawback of not being thermally stable: the noble metals supported on metallic oxides because at high temperatures
       the particles of the metal tend to sinter, with consequent deactivation of the catalyst; the clays and the zeolites because their structure tends to collapse and thus loses its initial catalytic properties.       
 
         [0011]    Catalysts are known (U.S. Pat. No. 5,705,136) which are constituted by oxides such as MnO, CuO, NiO and CoO supported on MgO, CaO, ZnO Ti0 2 , Al 2 0 3 -Zn0, Al 2 0 3 -Ti0 2 , and the like. Preferably, the catalysts contain CoO supported on MgO. 
         [0012]    N 2 0 conversions are high. 
         [0013]    Structures such as hydrotalcite, such as for example Cu 3 Mg 5 Al 2 (OH) 20 CO 3  3H 2 0, Mn 3  Mg 5 Al 2 (OH) 2 oC0 3 H 2 0, can also be used. 
         [0014]    It has now been found unexpectedly that the catalysts specified hereafter have a high catalytic activity in the decomposition of N 2 0 to nitrogen and oxygen and a satisfactory thermal stability, and are able to keep their activity unchanged for long periods of time. 
         [0015]    The catalysts comprise mixed oxides of copper, manganese and rare earth metals, which are present in the following composition, expressed in percentage by weight of CuO, MnO and oxide of rare earth metals in which the metal is present in the lowest valency state: 50-60% MnO, 20-45% CuO, 5-20% rare earth metal oxide. 
         [0016]    Further the invention comprises a process for removing nitrogen protoxide from gas emission from adipic acid plants comprising contacting with a catalyst which comprises mixed oxides of copper, manganese and lanthanum having a composition expressed as percentage by weight of 55-60% MnO, 25-40% CuO, 9-14% La 2 O 3 .” In this process, the gas emissions released by the adipic acid plants may be made to pass over a fixed catalyst bed at temperatures from 600° C. to 700° C.” 
     
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0017]    The preferred rare earth metal oxides are lanthanum and cerium oxides. 
         [0018]    A preferred composition comprises lanthanum oxide in an amount of 8-16% by weight expressed as La 2 0 3 . 
         [0019]    The mixed oxides which constitute the active components of the catalysts have the characteristic of being p-type semiconductors, in which conductivity increases exponentially with the temperature according to an Arrhenius-type rule and in which the charge vectors are constituted by electron vacancies. In these oxides, the lattice oxygen takes part in the oxidation reactions. 
         [0020]    The mixed oxides axe used on porous metallic supports such as alumina, silica-alumina, titanium dioxide, magnesium oxide. Gamma alumina, in the form of microspheroidal particles with a diameter of 30-80 pm, is the preferred support for reactions performed in particular in a fluid bed. The surface area (BET) of the catalyst supported in gamma alumina ranges generally from 80 to 150 m 2 /g. The oxides are preferably present in the support in an amount of 10-30% by weight. 
         [0021]    In the fixed-bed reactions used in the removal of nitrogen protoxide from the emissions of nitric acid and adipic acid plants, it is preferred to use supports which have a definite geometric shape, such as perforated cylindrical granules or three-lobed granules provided with through holes at the lobes. The size of the granules is 3-10 mm in height and their circumference ranges from 3 to 10 mm. 
         [0022]    The catalysts used in the process according to the present invention are disclosed in EP 1 197 259 B1, in which they are used to oxidize volatile organic substances and in which the use for decomposition of N 2 O to nitrogen and oxygen is not provided or mentioned at all. 
         [0023]    In order to prepare the catalysts, the support is first impregnated with an aqueous solution of a salt of lanthanum or cerium or other rare earth metal or mixtures thereof, followed by drying of the support and then calcining at temperatures preferably from 450 to 600° C. The support thus treated is then impregnated with a solution of a salt of copper and manganese, subsequently dried and then calcined at temperatures from 300 to 500° C. 
         [0024]    Any salt of the metals mentioned above which is soluble in water can be used; preference is given to nitrates, formates and acetates. 
         [0025]    The preferred impregnation method is provided in dry conditions, i.e., by using a volume of salt solution which is equal to, or smaller than, the volume of the pores of the support. 
         [0026]    The decomposition of N 2 0 is performed at temperatures from 400 up to 900° C. The higher temperatures are used as the N 2 0 content increases. In the case of emission from nitric acid plants, the preferred temperature is from 600° to 800° C. 
         [0027]    The spatial velocities range from 3000 to 60,000 h −1 . The N 2 0 content in the mixtures varies from ppm to percentages by volume of more than 20%. When working in the conditions indicated above, any NOx oxides that are present remain unchanged. 
         [0028]    The following examples are provided merely by way of non-limiting illustration of the invention. 
       Examples 1-4 
       [0029]    The catalyst used in the following examples had the following composition, expressed as a percentage by weight of: 
         [0030]    La 2 0 3 =9.2 
         [0031]    MnO=53.4 
         [0032]    CuO=37.4 
         [0033]    Preparation was performed by impregnating gamma alumina with an aqueous solution of lanthanum nitrate La(N0 3 ) 3 . 
         [0034]    The support was then dried at 110° C. and then calcined at 600° C. The calcined support was impregnated with an aqueous solution of manganese nitrate (Mn(N0 3 ) 3 ) and copper nitrate (Cu(N0 3 ) 2 ) and then dried at 120-200° C. and calcined at 450° C. 
         [0035]    A volume of solution equal to 100% of the volume of the pores of the alumina was used for impregnation. 
         [0036]    The oxides were present in the support in an amount of 26% by weight. The surface area of the catalyst (BET) was 110 m 2 /g and the porosity was 0.40 cm 3 /g. 
         [0037]    Before the test, the catalyst was appropriately milled and screened. 
         [0038]    The light-off activity of the catalyst, i.e., the temperature of the gas stream at which the catalyst decomposes 50% of the nitrogen protoxide that is present, and the temperature of total decomposition of the protoxide were to 900° C. The higher temperatures are used as the N 2 O content increases. In the case of emission from nitric acid plants, the preferred temperature is from 600° to 800° C. 
         [0039]    The spatial velocities range from 3000 to 60,000 h −1 . The N 2 O content in the mixtures varies from ppm to percentages by volume of more than 20%. When working in the conditions indicated above, any NOx oxides that are present remain unchanged. 
       Example 5 
       [0040]    The catalyst used in this example had the following composition, expressed as a percentage by weight of: 
         [0041]    La 2 0 3 =10% 
         [0042]    MnO=53% 
         [0043]    CuO=38% 
         [0044]    Preparation was performed as in Examples 1-4 and tested accordingly. 
       Example 6 
       [0045]    The catalyst used in example 6, a comparative example, had the following composition, expressed as a percentage by weight of: 
         [0046]    La 2 0 3 =10% 
         [0047]    MnO=45% 
         [0048]    CuO=45% 
         [0049]    Preparation was performed as in Example 1-4 and tested accordingly. The results obtained are given in the table. 
         [0000]                                                                                  TABLE               Operating                                   conditions   Unit   Example 1   Example 2   Example 3   Example 4   Example 5   Example 6                                N 2 0   % volume   30   13   8.5   1200   13   13                           ppmv               Oxygen   % volume       5   5   1   5   5       Helium       remainder   remainder   remainder   remainder   remainder   remainder       Reaction start   ° C.   445°   430°   430°   300°   300°   450°       temperatures                                    50% conversion   ° C.   503°   520°   520°   500°   490°   550°       100% conversion   ° C.   576°   620°    60°    56°   590°   650°       GHSV   h −1     10,000   12,500   10,000   10,000   1250   1250       Total flow-rate   Ncc/min   200   200   200   200   200   200                    
(a) 8000 ppmv of NO were present in the reaction mix
 
         [0050]    Example 5 illustrates a specific combination of manganese, copper and lanthanum oxides in defined ranges, namely, 55-60 wt % MnO, 25-40 wt % CuO, 9-14 wt % La 2 0 3 . These specific ranges represent a critical feature of the catalyst. 
         [0051]    By comparing the catalyst efficiency of a catalyst according to the subject invention and the catalyst efficiency of a catalyst which comprises the same oxides but in percentage ranges falling—even by a very little amount—outside the specific limits indicated, it results that the efficiency of the first catalyst is very high, while the efficiency of the second catalyst is remarkably lower. 
         [0052]    The composition of the high performance catalysts is 55-60 wt % MnO, 25-40 wt % CuO, 9-14 wt % La 2 0 3 . The low performance catalysts differ from the high performance catalysts in view of their CuO and MnO content, which is few percentage points higher than the upper limit and/or few percentage points lower than the lower limit. 
         [0053]    For example, catalysts with low performance have the same La 2 0 3  composition as the high performance catalysts but comprise 45 wt % CuO (the upper limit for the high performance catalysts being 40 wt %) and 45 wt % MnO (the lower limit for the high performance catalysts being 55 wt %). 
         [0054]    It follows that the CuO and MnO ranges of the high performance catalysts are actually critical because they result in a high catalytic efficiency, while catalysts whose CuO and MnO contents are even a little outside those CuO and MnO ranges show a very poor performance. 
         [0055]    The catalysts of the subject invention use only one fixed catalyst bed, while the catalyst used in the prior art requires at least two fixed catalyst beds to control the high exothermia of the N 2 O decomposition reaction. The difference in the subject invention with the prior art is a consequence of the critical narrow range of the catalysts. 
         [0056]    Although the foregoing invention has been described in some detail by way of illustration and example for purposes of clarity of understanding, it is readily apparent to those of ordinary skill in the art in light of the teachings of this invention that certain changes and modifications may be made thereto without departing from the spirit or scope of the appended claims.