Abstract:
Concretes containing Portland cement, fly ash and aggregate are disclosed which are capable of attaining high compressive strength and which contain relatively low proportions of Portland cement and relatively high proportions of a select fly ash component. The inventive concretes may be formulated as highly dense masses particularly suited for use in the manner of conventional structural concretes in buildings, bridges, dams, etc. Comparatively low density concrete masses may also be produced which are light in weight and have thermal insulation value rendering them particularly suited for use as thermal insulating components of roofs and as protective coatings for a variety of substrates.

Description:
BACKGROUND OF THE INVENTION 
     This invention relates to cementitious compositions containing Portland cement and fly ash. More particularly, this application concerns novel Portland cement concrete compositions containing relatively low proportions of cement together with relatively high proportions of a select fly ash component, which compositions when mixed with water and allowed to set harden into masses exhibiting unexpectedly high compressive strengths. 
     Of all the hydraulic cements, Portland cement enjoys the most widespread use for constructional purposes at the present time. Portland cement is produced by heating to fusion mixtures of argillaceous and calcareous materials and thereafter grinding the &#34;clinker&#34; produced, in the presence of up to about five percent gypsum, to a fine powder. Mixtures of Portland cement with a particulate aggregate such as limestone and sand form a &#34;structural&#34; concrete which is unsurpassed as a strong and durable building material. 
     Fly ash is a well known material generated as a by-product in the combustion of coal as a fuel in power plant boilers. The American Concrete Institute Publication &#34;SP-19&#34; defines fly ash as &#34;The finely divided residue resulting from the combustion of ground or powdered coal and which is transported from the firebox through the boiler by flue gas&#34;. The recent growth of coal fired power due to fuel oil shortage and price increases has resulted in an abundance of fly ash with consequent active promotion of uses for the rapidly accumulating solid waste material. 
     Being finely divided and highly siliceous, fly ash is a well known pozzolan which forms a slowly hardening cement with water and hydrated lime. A pozzolan is defined in the American Concrete Institute Publication &#34;SP-19&#34; as &#34;A siliceous or siliceous and aluminous material, which in itself possesses little or no cementitious value but will, in finely divided form and in the presence of moisture, chemically react with calcium hydroxide at ordinary temperatures to form compounds possessing cementitious properties&#34;. This chemical reaction between the pozzolan and the calcium hydroxide is often referred to as the &#34;pozzolanic reaction&#34;. While the &#34;pozzolanic reaction&#34; has been studied, the mechanisms involved are not completely understood. For instance in a report published in June, 1976 by the U.S. Department of Transportation, No. FHWA-IP-76-16 entitled &#34;FLY ASH AS A CONSTRUCTION MATERIAL FOR HIGHWAYS&#34;, it is stated that the pozzolanic reaction, although still not completely understood, involves the silica and alumina compounds in the fly ash, as well as any free lime which may be present. 
     The art has recognized that useful cementitious compositions can be prepared by combining in the presence of water Portland cement and pozzolans such as fly ash. For example, as detailed in the aforementioned published report of the Department of Transportation (DOT), Portland cement may be added to lime-fly ash-aggregate base and sub-base courses in rigid pavement systems as a substitute for all or part of the lime to accelerate the rate of strength gain of the mixtures. On the other hand it is well known to add fly ash and other pozzolans to Portland cement compositions. Commercial Portland cements containing appreciable amounts, 15 to 40 percent, of pozzolan such as fly ash are known in the art as &#34;Type 1P&#34; cements. Moreover, Portland cement concretes have been prepared containing fly ash to increase workability and pumpability, to control bleeding, reduce shrinkage, etc. The major objective however sought by the addition of fly ash to Portland cement concretes in the U. S. has been for the enhancement of compressive strength of the hardened concrete. In such concretes the fly ash has been added as a replacement for the cement and/or sand, the pozzolanic fly ash reacting with the lime produced as the result of the hydration reaction between the Portland cement component and water to give additional strength. Such &#34;pozzolanic reaction&#34; of the fly ash increases the strength of the concrete, especially at ages of 28 days or more. The cementitious compounds produced by the &#34;pozzolanic reaction&#34; are believed to fill the pores and capillaries that are normally present in concrete and as a result the concrete containing fly ash also becomes less permeable to water and salt solutions. 
     The amount of fly ash in practice added to Portland cement concrete has varied depending upon the desired end properties of the concrete. Generally, when a given Portland cement concrete is redesigned to include fly ash, between 10 and 30% of the Portland cement, by weight, is replaced by a volume of fly ash which ranges from that equal to that of the cement removed to that equal to two times that of the cement removed. One-hundred pounds of a typical Type I Portland cement will produce enough calcium hydroxide during its reaction with water to react with about 20 pounds of a typical fly ash. The amount of fly ash, therefore, over and above this 100 cement to 20 fly ash weight ratio acts essentially in a physical way to affect bleeding, workability and heat of hydration. When the amount of fly ash used in concrete is equal in volume to the amount removed and the cement substitution exceeds about 20%, the compressive strengths of the set concrete are lower as compared to a reference non-fly ash-containing concrete, at all ages, and for this reason substitution beyond the approximate 20% level in concrete has been avoided in practice. 
     Concretes however wherein fly ash has been substituted beyond the 20% level have been suggested in the art. For example, in U. S. Pat. No. 2,250,107 to John S. Nelles, assigned to the Detroit Edison Company, Detroit, Michigan, Portland cement concretes are described wherein fly ash is added in substitution for part or all of the fine aggregate such as sand conventionally used as the fine aggregate. The fly ash is said to be added in greater proportions than previously added, i.e., at least equal to the amount of cement by volume, with a range of from 1.5 to 2.5 times the amount of cement being preferred. The resulting concretes are said to be stronger than comparable concretes having identical Portland cement content, to be lighter in weight, and to possess better workability and flexibility. Also, in British Patent No. 940,692 to Fonbonne, Portland cement compositions comprised of mixtures of cement and fly ash are described, the proportion of fly ash constituting at least two thirds by weight of the cement. In contrast to prior art cement-fly ash compositions wherein the proportion of fly ash was limited, the hardened compositions of British 940,692 containing the large amounts of fly ash are said to have good compressive strengths after 7 and 28 days. According to the British patent, the prior art cement-fly ash compositions limited the amount of fly ash to 20 percent by weight, since it was found that increased proportions beyond this decreased the strength of the hardened cement. The high fly ash content cement compositions of British Pat. No. 940,692 are said to increase in strength at a greater rate than conventional cements having similar strength at 28 days after setting. According to the British patent it was found necessary to crush the fly ash as uncrushed ash would not produce an effective cement composition. 
     It is also known in the art that the chemical compositions of fly ashes from coals from differing geographical locations sometimes vary significantly as does their pozzolanic activity. According to the aforementioned DOT report No. FHWA-IP-76-16, the extent and rate of pozzolanic reaction involving fly ashes is a function of several factors including quantity of stabilizer (free lime or cement), total silica and alumina in the fly ash, etc. The DOT report also states that fly ashes having large amounts of free lime (as indicated by, although not equal to, the CaO content) tend to be very reactive and probably exhibit some degree of self-hardening. The report describes compositions stabilized through the pozzolanic reaction by the addition thereto of lime and/or cement, and/or aggregate, particularly useful in constructing pavements, stabilizing soil, embankments, structural backfill, and in forming grouting compositions. 
     In U. S. Pat. No. 3,634,115 to Leonard John Minnick, a new fly ash is described which is &#34;sulfopozzolanically&#34; reactive. The fly ash is said inter alia to have a high sulfate and a high calcium oxide content rendering it useful for preparing stabilized load-supporting compositions having superior qualities. The new fly ash is produced by injecting lime into the boiler under particular conditions during combustion of the coal. The novel fly ash according to the patent gives especially good results when combined with lime and aggregate, for example, to provide a sub-base or sub-roadway course, although other materials such as Portland cement and ordinary fly ash can be used with the inventive fly ash according to the patent. 
     SUMMARY OF THE INVENTION 
     It has been found that certain fly ashes when combined with Portland cement in weight ratios of 1 part cement to 1, preferably about 1.5 parts fly ash up to weight ratios of 1 part cement to about 15 parts fly ash produce surprisingly high strengths in concrete, mortar and pastes which it is believed, cannot be entirely accounted for by the conventional &#34;pozzolanic reaction&#34;. The fly ashes combined with Portland cement in these relatively high ratios to produce unexpectedly high strength mixtures according to the invention are those characterized as having a total analyzable calcium oxide greater than about 10, preferably greater than about 15, percent by weight and a combined silica (SiO 2 ), alumina (Al 2  O 3 ), and iron oxide (Fe 2  O 3 ) content of less than about 80, preferably less than about 75, percent by weight. Particularly valuable are high density mixtures of such cement/fly ash combinations with aggregate such as sand and/or stone to produce structural concretes where strength is most important. These &#34;structural&#34; concretes according to the invention exhibit high strength when measured at early as well as later stages of hydration with minimum cement content. A practical result of the invention is the ability to formulate high strength structural Portland cement concrete mixes containing less Portland cement than conventional Portland cement structural concrete mixtures. 
     The aformentioned discovery has also led to the preparation according to the invention of comparatively low density mixtures of such cement/fly ash combinations with lightweight aggregates, such as expanded vermiculite and perlite, and additionally air-entraining or foaming agents, which are valuable as lightweight thermal insulating masses in for example, roofs and roof decks, or as protective insulating coatings for a variety of substrates. Again, a lessening of the amount of Portland cement binder required in the mixture is afforded. 
     The &#34;structural&#34; concretes prepared herein may be characterized as &#34;heavy&#34;, that is having a hardened density of at least about 120 pounds per cubic foot (p.c.f.), or &#34;lightweight&#34; in which case the hardened density ranges from about 70 to about 120 p.c.f. The aggregates moreover in such structural concretes may be &#34;heavy&#34;, that is possess densities of at least about 80 p.c.f. or may be characterized as &#34;lightweight&#34; in which case their densities range between about 40 and 80 p.c.f. Low density &#34;insulating&#34; concretes prepared herein on the other hand generally have hardened densities less than about 70, typically less than about 60, p.c.f. and employ aggregates having a density less than about 15 p.c.f. 
     The fly ashes employed herein in high proportion to produce such valuable products are characterized as possessing a particular chemical composition defined below. In addition, the fly ashes used herein appear to be unique in their behavior in various tests described below. Moreover the fly ashes used herein are products of commerce being produced at various boiler facilities, and need not be first crushed or ground to promote activity. 
     DETAILED DESCRIPTION OF THE INVENTION 
     In investigations leading to the finding upon which the present invention is based, fly ashes from various sources throughout the United States were obtained and mixed with Portland cement, particularly with Portland cement-aggregate blends to form dry concrete mixes, and thereafter water added to hydrate the mixtures. The fly ashes were obtained from principally power companies operating in the States of Illinois, Pennsylvania, Minnesota, North Dakota, Michigan, Texas, Kansas, Ohio, Florida and Arizona. Because of the wide differences in coal sources and coal firing practices in the industry, the physical properties and chemical compositions of the fly ashes varied markedly. TABLE I below details the typical chemical analyses of fly ashes from sources A through K. TABLE I gives the appropriate percent by weight of SiO 2  ; Al 2  O 3  ; and Fe 2  O 3  ; combined SiO 2 , Al 2  O 3  and Fe 2  O 3  ; CaO; MgO; and SO 3  found as well as the loss on ignition (L.O.I.) for each of the fly ash samples A through K, as calculated according to ASTM C114-77. Also shown in Table I is the percentage of &#34; free lime&#34; as calculated according to ASTM C-25 Section 28.3 (1972). 
     
                                           TABLE I__________________________________________________________________________SOURCE      A  B  C  D  E  F  G  H  I  J  K__________________________________________________________________________Chemical Components% SiO.sub.2 31.4          43.1             37.6                24.1                   39.8                      48.9                         52.2                            47.1                               43.3                                  47.6                                     56.5Al.sub.2 O.sub.3       19.7          21.8             27.5                14.3                   16.8                      29.6                         31.0                            20.8                               18.5                                  23.3                                     24.7Fe.sub.2 O.sub.3       6.6          4.2             7.3                9.5                   6.8                      9.3                         8.3                            16.0                               29.9                                  16.0                                     5.6CaO         20.2          23.5             17.9                29.6                   16.8                      6.2                         4.9                            5.0                               4.3                                  7.6                                     7.7MgO         3.9          3.8             3.7                8.5                   5.3                      0.7                         0.7                            1.8                               0.9                                  1.4                                     2.0SO.sub.3    6.4          1.6             5.7                5.9                   2.8                      0.6                         0.3                            0.6                               1.2                                  0.7                                     0.5Loss on Ignition       1.4          0.5             0.5                0.6                   0.3                      2.3                         4.2                            2.8                               1.2                                  0.6                                     1.2SiO.sub.2 + Al.sub.2 O.sub.3 + Fe.sub.2 O.sub.3       57.7          69.1             72.4                47.9                   63.4                      87.8                         91.5                            83.9                               91.7                                  86.9                                     1.8Free Lime   1.35          1.91             0.93                3.63                   0.83                      0.44                         0.0                            0.63                               0.54                                  0.13                                     1.45__________________________________________________________________________ 
    
     The fly ashes from the differing sources A through E not only varied in composition, but also, it was discovered, in their performance as ingredients in the aforementioned Portland cement mixtures. In particular, it was discovered that the long term compressive strengths of Portland cement-fly ash compositions such as concrete mixes, formulated with the fly ashes A-E in weight proportions of cement to fly ash greater than 1 to about 1, preferably greater than 1 to about 1.5, were markedly higher than identical cementitious compositions prepared using fly ashes from sources F through K. This marked difference in strength performance between the fly ashes at the relatively high addition ratios of fly ash was surprising since such difference was not in evidence from previous strength measurements involving Portland cement-fly ash compositions wherein the cement to fly ash ratio is less than 1 to 1. The marked difference in strength contribution of the fly ashes A-E at the higher ratios was further unexpected since it could not have been predicted by a stoichiometric calculation based upon the conventionally theorized &#34;pozzolanic reaction&#34;. The fly ashes A-E had compositions falling in the approximate general ranges shown in Table II. 
     
                       TABLE II______________________________________           ApproximateComponent       Composition Range - Wt.%______________________________________SiO.sub.2       24.1-43.1Al.sub.2 O.sub.3           14.3-27.5Fe.sub.2 O.sub.3            4.2-9.5SiO.sub.2 + Al.sub.2 O.sub.3 +Fe.sub.2 O.sub.3           47.9-72.4CaO             16.8-29.6MgO              3.7-8.5SO.sub.3         1.6-6.4______________________________________ 
    
     In addition to the aforementioned compositional differences it was found that the strength-imparting fly ashes A-E differed from F-K in their response to various chemical treatments. These treatments are outlined as follows: 
     1. Reaction with tartaric acid 
     In this test, approximately 20 grams of fly ash are placed in a 250 ml. glass beaker containing 150 ml. of a 5% tartaric acid solution. The mixture is slowly brought to a boil and allowed to boil gently with constant stirring for 15 minutes. The beaker is then covered and its contents allowed to cool, unmolested, for about 3 hours. This procedure converts a fly ash from the A-E group to a voluminous gel whose height in the beaker will exceed 20 mm. Fly ashes F-K will settle to the bottom of the beaker and form a layer whose height is only 6 to 7 mm. 
     2. Reaction with triethanolamine 
     In this test, approximately 10 grams of fly ash are vigorously mixed with 50 ml. of a 10% triethanolamine solution in a stoppered bottle. After standing overnight, a 10 ml. portion of the clear, water white supernatant liquid is transferred (by pipet) to a second bottle which contains 10 ml. of a 10% hydrochloric acid solution. The triethanolamine/acid mixture involving a fly ash A-E will immediately develop a distinct canary yellow color. When this procedure is carried out with a fly ash F-K, the triethanolamine/acid mixture will remain colorless or take on only a very pale yellow color. 
     3. Reaction with Portland cement and water 
     The appearance of a hardened fly ash/Portland cement/water paste also distinguishes between the fly ash groups. The test procedure involves mixing, with a spoon or spatula, 20 grams of Portland cement, 50 grams of fly ash and sufficient water to produce a stiff paste in a cup or beaker. The paste is then rolled into a ball in the palms of the hands and allowed to harden in the laboratory atmosphere. After standing for a period of 5 to 6 hours, the paste formed from a fly ash A-E will begin to exhibit efflorescense and in 12 to 18 hours the test specimen will take on the appearance of a white &#34;snow-ball&#34;. The paste made from a fly ash F-K will exhibit slight or no efflorescence under these test condition. 
     4. Heat of solution in an acid medium 
     This test involves treating 3 grams of fly ash with a mixture of 2 N nitric acid and hydrofluoric acid in accordance with the method described in ASTM C186, Section 4.2 and 5.3. The treatment is carried out in an adiabatic calorimeter and the heat produced by the dissolving fly ash is measured in calories per gram. The heat of the solution of each of the five fly ashes A-E described in TABLE III is listed in TABLE III. 
     
                       TABLE III______________________________________             Heat of SolutionFly Ash           Cal./gram______________________________________A                 459.6B                 498.6C                 467.0D                 421.8E                 506.6______________________________________ 
    
     The remaining fly ashes from Table II have heat of solution values that are less than about 405 calories per gram. 
     While useful pastes and mortar compositions can be produced from Portland cement mixtures containing high proportions of the particular fly ashes of the invention, the present discovery, as aforementioned, is especially useful in preparing high strength concrete formulations for structural useage where high compressive strength is desired. 
     As is well known in the art, conventional structural concretes are mixtures essentially of Portland cement, coarse and fine aggregate and water. Such concretes use only sufficient water to make the mix placeable and when hardened have densities greater than 70 pounds per cubic foot and compressive strength values typically in excess of 2,000 psi after 28 days of preparation. &#34;Coarse&#34; aggregate conventionally are greater than about 3/8 inches in size, and include gravel, granite, limestone, shale, etc. The &#34;fine&#34; aggregate employed in Portland cement concretes is most often sand (silica), sometimes washed, comprised of particles less than about 3/8 inch, typically less than 3/16 of an inch in size. The total aggregate present in the set concrete is usually greater than 50 percent by volume. As aforementioned, aggregate used in dense structural concretes typically have bulk densities greater than about 80, more often greater than about 90, pounds per cubic foot. 
     As aforementioned, the inventive Portland cement/fly ash combinations are also useful in preparing lightweight, low density, thermal-insulating concretes. As opposed to structural concretes discussed above, such concretes have densities much less than about 100 pounds per cubic foot &#34;dry&#34;, that is after hardening, and typically less than about 70 pounds per cubic foot. Such concretes are rendered lightweight and porous by the substitution of lightweight, low-density aggregates for the heavier sand and stone aggregate used in &#34;structural&#34;concretes, and/or by the incorporation of foaming or air-entraining agents which cause air or gas bubbles to be formed in the wet mixtures which render the concretes porous upon hardening. Structural concretes sometimes have air entrained therein also, but only to the extent of about 6 percent which is substantially less than the amount of air in thermal insulating concretes. Typical lightweight aggregates are those having dry densities of less than about 15, preferably less than about 10, pounds per cubic foot. Exemplary lightweight aggregates include those aggregates having cells or pores therein such as expanded vermiculite, expanded perlite, cellular synthetic resin particles, e.g. foamed polystyrene beads or shreds, cellular glass beads, etc., or mixtures thereof. The amount of such aggregate used will depend upon, inter alia, the final density of the concrete desired, but typically at least 50% by volume of the hydrated composition is employed. 
     Suitable foaming or air entraining agents include surface active agents which act to entrain air in the composition as it is mixed with water and allowed to set, or as it is mixed, pumped and sprayed. The entrained air not only lowers density but also assists the pumpability and sprayability of the wet mixes. Any of the surface active agents heretofore found useful in the art for this purpose in low density cementitious compositions are useful herein. In general, the surface active sulfonates have found particular utilization by the art. Alpha olefin sulfonates as disclosed in U.S. Pat. No. 3,926,650 are preferred surface active foaming agents for use herein along with saponified or neutralized Vinsol resin. Vinsol resin is an extract of pinewood and a well known product of commerce. For use as a surface active agent the resin is neutralized typically with caustic alkali such as caustic soda. Another commercially popular surface active foaming agent for low density cementitious insulating compositions is sodium lauryl sulfate. A further illustrative surfactant is &#34;TRITON X-100&#34;, a condensate of octylphenol and ethylene oxide produced by Rohm &amp; Haas Co. A sufficient amount of the surface active agent is employed herein to give the desired low density and/or degree of pumpability and sprayability. In general an amount of surfactant ranging from about 0.001 to about 2, preferably 0.001 to 0.5, percent by weight of the total solids of the composition is employed. 
     In order to maintain the air which is entrained during mixing, particularly after pumping the wet air-entrained mixture, and in order to keep the lightweight aggregate in suspension and thus prevent segregation of the wet mix during pumping especially, a stabilizer such as a cellulose ether, starch or gum may be employed in the composition of the invention. Suitable cellulose ethers include methyl cellulose, hydroxethyl cellulose, methyl hydroxyethyl cellulose, hydroxypropyl methylcellulose and sodium carboxymethylcellulose. Illustrative stabilizing starches include for example hydrated corn starch and pregelantinized starch, while exemplary gums include natural gums such as guar gum, karaya gum and xanthum gum. Only a small amount, about 0.001 to 1.5, preferably 0.001 to about 0.5, percent by weight based on the total solids, of such stabilizer is typically needed. 
     Practical uses of the low density cement/fly ash concretes include use as insulating and fireproofing masses which may be pumped and thereafter poured or spray-applied. In the use for example of such lightweight concretes as a lightweight insulating layer in roof decks of commercial buildings, the material typically is mixed at ground level and thereafter pumped vertically to the roof deck. After placement in this fashion, the compositions after hydration must exhibit the desired low dry density, typically in the ranges of about 20 to 40 pounds per cubic foot. In simialar fashion, low density compositions for fireproofing for example steel structural beams of buildings are mixed, pumped and thereafter sprayed onto the exposed beams. Typical dry densities of hydrated cement/lightweight aggregate fireproofings applied in this manner lie in the range of about 10 to about 25 pounds per cubic foot. 
     In the detailed Examples 1-16 below, concrete formulations were prepared except where otherwise noted such as Example 9 (mortar) and 10 (paste). Where indicated, compressive strengths of the set concretes were tested according to ASTM No. C192 procedure. Usually the compressive strengths of specimens were measured after 1, 7 and 28 days, in accordance with ASTM No. C39. The concretes contained Portland cement or a mixture of Portland cement and fly ash in the proportions shown usually pounds per cubic yards of concrete produced. In all &#34;concrete&#34; formulations of Examples 1-16, a mixture of sand and crushed limestone was employed as the aggregate in a 45:45 ratio by weight unless otherwise noted. In the concrete mixes containing fly ash, the volume of sand and stone aggregate was reduced by an amount equal to the volume of fly ash added in order to maintain a constant yield. The Portland cement &#34;X&#34;, &#34;Y&#34; and &#34;Z&#34; employed in certain of the Examples had the chemical compositions shown in Table IV below. The structural concretes were prepared in accordance with ASTM C494 procedure. Determination of the amount of air entrained in the hydrated compositions of the Examples below was made according to ASTM test procedure No. C231. Also, the &#34;slump&#34; of the wet mixes produced in the Examples was determined according to ASTM test procedure No. C143. &#34;Slump&#34; is a measure of the relative consistency or plasticity of the wet mix. 
     
                       TABLE IV______________________________________Portland CementComposition     X         Y         Z______________________________________% SiO.sub.2     21.9      19.9      20.5Al.sub.2 O.sub.3           4.9       5.7       5.2Fe.sub.2 O.sub.3           2.7       2.6       2.5CaO             66.0      62.3      62.3MgO             1.2       3.1       3.6SO.sub.3        2.1       2.8       3.4Loss on Ignition           1.2       2.4       1.2Alk. as Na.sub.2 O           0.19      0.62      0.63C.sub.3 S       59.5      52.5      49.0C.sub.2 S       17.9      17.5      21.0C.sub.3 A       8.4       10.6      9.0C.sub.4 AF      8.2       8.0       7.0______________________________________ 
    
     The following Examples serve to illustrate the invention further and should not be construed as limiting the invention in any manner. 
    
    
     EXAMPLE I 
     To illustrate the effect of increasing the weight ratio of fly ash to cement on the compressive strength of concrete, a series of concretes were fabricated in which the weight ratio of cement to fly ash ranged from 1:0.0 to 1:2.5. The test data are summarized in Table V. The cement &#34;X&#34; was employed in the mixes. The fly ash used was &#34;B&#34; from Table I. Concretes No.&#39;s 1,2,3 and 4 were included in the series for reference purposes and contain no fly ash. Concretes No. 5 and 6 have approximately the same cementitious volume (volume of cement and fly ash) as No. 4 and exhibit a strength decrease in going from a cement to fly ash ratio of 1:0.0, in No. 4 to 1:0.5 in No. 6. Concrete No. 7 has a cementitious volume approximately the same as No. 3 and increasing the cement to fly ash weight ratio from 1:0.0 to 1:1.0 causes a decrease in compressive strength at all ages of test. Concretes No. 2 and 3 have about the same cementitious volume and increasing the cement to fly ash ratio from 1:0.0 to 1:1.5 results in a decrease to compressive strength at all ages of test. Concretes No. 1 and 9 have about the same cementitious volume but increasing the cement to fly ash ratio from 1:0.0 to 1:2.0 results in an increase in 56 and 90 day strengths and only a moderate decrease in the 1,7 and 28 day strengths. Concrete No. 10, which has a slightly larger cementitious volume than No. 1 and has a cement to fly ash weight ratio of 1:2.5, has compressive strengths that exceed those of No. 1 at all ages except 1 day. If one ignores the influence of cementitious volume, the data clearly indicates that at a fixed cement content (i.e., 194 to 198 lbs./yd 3 ) an increase in fly ash content from 99 lbs/yd 3  in No. 6 to 485 lbs./yd 3  in No. 10 causes an unexpected increase in strength and the magnitude of the increase, at all ages of test, is very significant when the cement to fly ash weight ratio exceeds 1:1.0. The increase in strength caused by the added increments of fly ash is not likely due to an increase in the normal &#34;pozzolanic reaction&#34;. The amount of cement in the concretes No. 6 through 10 will produce only enough calcium hydroxide to react with about 40 pounds of the fly ash. Therefore it might be concluded that the fly ash, because of its specified composition, is undergoing some kind of unique reaction which occurs when a fly ash of the invention is used with a minimum of Portland cement. 
     
                                           TABLE V__________________________________________________________________________Cement     Fly Ash          RatioConcrete(X)  (B)  Cement: Fly                    Slump                        Air                           Compressive Strength - P.S.I.No.  lbs/yd.sup.3     lbs/yd.sup.3          Ash-by wt.                 w/c                    in. %  1-Day                                7-Day                                     28-Day                                          56-Day                                               90-Day__________________________________________________________________________1    612  --   1:0.0  0.500                    31/2                        2.3                           1163 3963 5499 6288 72262    505  --   1:0.0  0.600                    31/4                        2.1                           910  3166 4706 5204 60343    404  --   1:0.0  0.750                    23/4                        1.9                           519  1980 3181 3905 44574    303  --   1:0.0  1.040                    21/2                        2.0                           218  940  1463 1786 19565    240   48  1:0.2  1.313                    21/4                        1.9                           192  779  1222 1541 17936    198   99  1:0.5  1.501                    21/2                        1.2                           168  738  1145 1493 16157    198  198  1:1.0  1.455                    5   0.9                           271  1257 1945 2841 32758    194  291  1:1.5  1.347                    61/4                        0.9                           441  2094 3282 4590 58279    194  388  1:2.0  1.102                    23/4                        2.1                           855  3460 5361 6964 739410   194  485  1:2.5  1.133                    23/4                        2.1                           1007 3974 6205 7082 7945__________________________________________________________________________ 
    
     EXAMPLE 2 
     The experiment described in Example 1 was repeated in part, using another fly ash that falls within the scope of this invention, &#34;A&#34;, in combination with two different cements. The test data are summarized in Table VI. At a fixed cement content (i.e. 202 to 213 lbs./yd 3  in Concretes No. 11 through No. 17) the added increments of fly ash A to cement X result in unusually large increases in compressive strength, at all ages of test, especially when the cement to fly ash weight ratio exceeds 1:1.0. The same observation is true for the combinations of cement Y and fly ash A in Concretes No. 19 through 23. 
     
                                           TABLE VI__________________________________________________________________________         Fly Ash              RatioConcreteCement   (A)  Cement:Fly                        Slump                             Air Compressive strength - P.S.I.No.  Source    Lbs/yd.sup.3         lbs/yd.sup.3              Ash-by Wt.                     w/c                        In.  %   1-Day                                      7-Day                                           28-Day                                                56-Day                                                     90-Day__________________________________________________________________________11   X   202  --   1:0.0  1.677                        2    2.1 99   499  722  849  95612   X   210  72   1:0.3  1.486                        2    1.8 149  848  1123 1402 161813   X   202  202  1:1.0  1.427                        13/4 2.0 294  1950 3062 3541 381714   X   204  306  1:1.5  1.396                        11/2 2.5 1104 3051 3938 4325 480915   X   206  412  1:2.0  1.370                        13/4 2.5 1838 3915 4864 5262 569516   X   208  521  1:2.5  1.484                        2    2.2 2144 4084 5258 5629 628417   X   213  638  1:3.0  1.565                        23/4 2.1 2443 3921 5058 5601 599418   Y   200  --   1:0.0  1.590                         3/4 1.4 108  419  730  796  80819   Y   202  202  1:1.0  1.383                        13/4 2.0 742  2067 3139 3527 379120   Y   204  306  1:1.5  1.340                        13/4 2.2 1525 3131 4023 4527 468621   Y   206  412  1:2.0  1.413                        13/4 2.3 1903 3658 4788 5411 570122   Y   208  515  1:2.5  1.455                        13/4 2.3 2295 4055 5345 6158 646123   Y   213  638  1:3.0  1.537                        13/4 2.3 2390 3882 5075 5862 6074__________________________________________________________________________ 
    
     EXAMPLE 3 
     To illustrate the difference between the strength producing properties of several typical fly ashes covered by the scope of this invention and those outside the scope of this invention, eleven batches of concrete were fabricated having approximately 200 lbs. of cement X and 500 lbs. of fly ash per cubic yard of concrete. The test data are summarized in Table VII. The concretes containing fly ashes A through E, which are within the scope of this invention have significantly higher compressive strengths, at all ages of test, than those concretes containing fly ashes F through K and which are not within the scope of this invention. The magnitude of the 1-day compressive strengths of concretes No. 24 through 28 are of particular importance because of restrictions often imposed on the time for stripping the concrete forms; that is, the concretes must reach a certain strength early in order to permit stripping of forms. The somewhat lower 1-day compressive strengths of concretes No. 25 and 28 are attributable to the lower surface area of the fly ashes B and E. These two ashes have surface areas in the range of 2700 to 3250 cm 2  /gram as measured by the Blaine permeability apparatus (ASTM C204). Fly ashes A, C and D have surface areas in the range of 3600 to 6025 cm 2  /gram. 
     
                                           TABLE VII__________________________________________________________________________CementConcrete(X)  Fly Ash     Slump                     Air                        Compressive Strength - P.S.I.No.  lbs/yd.sup.3     Source         lbs/yd.sup.3              w/c                 in. %  1-Day                             7-Day                                  28-Day                                      56-Day                                          90-Day__________________________________________________________________________24   204  A   510  1.369                 11/2                     2.5                        2570 4647 5720                                      5912                                          663125   200  B   500  1.219                 41/2                     1.6                        806  3496 5764                                      6846                                          729726   206  C   515  1.168                 31/4                     2.9                        2471 3575 4908                                      5669                                          627027   202  D   505  1.251                 2   2.5                        2715 5063 5633                                      6218                                          666628   204  E   510  1.180                 53/4                     2.5                        786  3291 4462                                      5023                                          552829   206  F   515  1.456                 41/4                     2.0                        307  1242 2080                                      2570                                          352330   206  G   515  1.658                 51/2                     1.7                        177  823  1387                                      1992                                          289731   204  H   510  1.267                 23/4                     2.1                        241  1637 2363                                      3075                                          394532   202  I   505  1.236                 23/4                     2.0                        300  1808 2943                                      3891                                          527833   202  J   505  1.265                 31/2                     1.9                        265  1342 2071                                      2902                                          402334   202  K   505  1.295                 31/2                     2.0                        310  1583 2577                                      3739                                          4855__________________________________________________________________________ 
    
     EXAMPLE 4 
     The possibility that the high strengths obtained with the low-cement high fly ash concrete compositions of the invention are due to volume changes was investigated. Quartz (SiO 2 ), which is chemically inert, was ball milled to a Blaine surface area of approximately 3000 cm 2  /gram. The ground quartz was used as a substitute for fly ash in the test concretes to evaluate the influence of volume without introducing any kind of reactive material. Two different cements were used in the test series. Measurements were made of slump, air and compressive strength after 1, 7, 28 56 and 90 days as in previous Examples. From the test data generated, it was apparent that the added increments of the inert ground quartz did increase the effectiveness of the Portland cement in developing additional compressive strength, but the increases are relatively minor when compared to those produced when cement and those fly ashes within the scope of this invention are combined in the same weight ratios. See Table VII A. 
     EXAMPLE 5 
     The effect of combining another fly ash within the scope of this invention, fly ash D from Table I with Portland cement X in various weight ratios was examined. The test data are summarized in Table VIII. Concretes no. 45, 46 and 47 contain no cement and the moderate strengths of these concretes indicate that fly ash D has some cementitious characteristics of its own. Within each of the four subseries each of which contains a fixed amount of cement, an increase in fly ash content results in a very significant increase in compressive strength at all ages of test. 
     
                                           TABLE VIIA__________________________________________________________________________          Ground               Ratio ofConcreteCement    Quartz               Cement:Quartz                           Slump                               Air                                  Compressive Strength - P.S.I.No.  Source     Lbs/yd..sup.3          Lbs/yd.sup.3               By wt.  w/c in. %  1-Day                                      7-Day                                          28-Day                                               56-Day                                                    90-Day__________________________________________________________________________35   X    202  --   1:0.0   1.677                           11/4                               2.0                                  80  360 520  670  71736   X    208  208  1:1.0   1.512                           21/4                               2.1                                  165 632 880  1117 115437   X    217  435  1:2.0   1.463                           21/2                               2.1                                  223 736 1078 1248 142838   X    222  555  1:2.5   1.511                           21/2                               2.0                                  179 686 929  1071 128639   X    227  682  1:3.0   1.569                           3   1.8                                  192 652 838  1023 118640   Y    202  --   1:0.0   1.707                           21/4                               2.1                                  65  455 600  633  60341   Y    198  198  1:1.0   1.531                           21/4                               3.0                                  157 773 1063 1137 120042   Y    198  396  1:2.0   1.471                           21/2                               2.0                                  219 914 1249 1299 132443   Y    198  495  1:2.5   1.501                           21/2                               1.9                                  262 951 1339 1473 148544   Y    198  594  1:3.0   1.591                           3   1.8                                  209 788 1160 1216 1238__________________________________________________________________________ 
    
     Some of the data in Table VIII are repeated in Table IX for discussion purposes. Concretes No. 46, 51, 54 and 62 contain approximately 500 pounds of fly ash per cubic yard, but different amounts of cement. The increased strengths which result from the addition of various levels of cement may be expressed as percentages of the strength of concrete No. 46, which contains no cement, and as percentages of the next lower cement addition level, which gives a measure of the incremental benefit of extra cement. Addition of approximately 50 lbs/yd cement increases strengths, averaged over all ages of test, to 498% of the concrete containing no cement (comparing No. 51 to 46). Addition of a further 50 lbs. of cement to a total of 100 lbs/yd, increases average strengths to 565% of that of the cement containing no cement (comparing No. 54 to 46) and to 113% of the concrete containing approximately 50 lbs cement per cubic yard. Another increase in cement, of 100 lbs/yd, to a total of 200 lbs/yd, increases average strength to 731% of that of the concrete containing no cement (comparing No. 62 to 46) and to 129% of that of the concrete containing approximately 100 lbs cement per cubic yard. Thus each increment of 50 lbs of cement increases strength roughly 15 percent above the strength of the concrete containing the lower increment, except that the first added approximately 50 pounds increases strength 565 percent, converting the concrete from a concrete that is not strong enough to allow stripping in actual concrete practice until 28 days or later to one that offers no stripping problem after 24 hours. 
     
                                           TABLE VIII__________________________________________________________________________Cement     Fly Ash          Cement toConcrete(X)  (D)  Fly Ash   Air                       Slump                           Compressive Strength - P.S.I.No.  lbs/yd.sup.3     lbs/yd.sup.3          ratio:by wt.                w/c %  in  1-Day                                7-Day                                     28-Day                                          56-Day                                               90-Day__________________________________________________________________________45   0    245        --  1.5                       21/2                           138  528  820  961  108546   0    495        --  1.5                       41/2                           379  599  781  837  112547   0    742        --  2.4                       2   1100 1735 2183 2429 280948   50   125  1:2.5 6.485                    1.3                       21/4                           24   233  332  419  46949   50   250  1:5.0 5.952                    1.4                       4   164  846  1394 1547 168950   49   371  1:7.5 5.288                    2.1                       3   813  2092 2738 3040 337751   49   495  1:10.0                4.867                    2.5                       21/4                           1747 3195 3997 4618 485152   49   742  1:15.0                5.288                    2.2                       11/2                           3064 4864 6116 6414 665353   100  250  1:2.5 2.795                    1.9                       21/4                           358  1542 2221 2490 279654   99   495  1:5.0 2.644                    2.1                       31/2                           2040 3749 4622 5012 529355   99   742  1:7.5 2.644                    2.3                       21/2                           3514 5232 6133 6407 710656   100  1000 1:10.0                2.974                    2.5                       11/2                           4022 5774 6029 6577 758457   151  151  1:1.0 2.002                    1.6                       13/4                           184  945  1414 1599 181458   151  379  1:2.5 1.806                    2.2                       3   1094 2922 3743 4084 442159   150  600  1:4.0 1.744                    2.4                       13/4                           3018 5105 5848 6417 666960   150  750  1:5.0 1.883                    2.2                       3   4110 6111 6704 7189 744961   200  400  1:2.0 1.382                    2.2                       3   2089 4072 5043 5392 575462   200  500  1:2.5 1.382                    2.1                       3   2661 5079 6023 6270 660563   202  758  1:3.75                1,457                    2.3                       21/2                           4019 6011 6880 7266 711464   198  990  1:5.0 1,681                    2.4                       21/4                           4616 6651 7057 7150 8006__________________________________________________________________________ 
    
     
                                           TABLE IX__________________________________________________________________________Cement     Fly Ash          Cement to                                  Ave. Inc.Concrete(X)  (D)  Fly Ash    Air                        Slump                            Compressive Strength PSI In. PSINo.  lbs/yd.sup.3     lbs/yd.sup.3          Ratio: by wt                 W/c %  In. 1-Day                                 7-Day                                      28-Day                                           56-Day                                                90-Day                                                     %__________________________________________________________________________46   0    495  --     --  1.5                        41/2                            379  599  781  837  112551   49   495  1:10.0 4.867                     2.5                        21/4                            1747 3195 3997 4618 4851Increase in strength of Concrete No. 51 over No. 46 -%                            461  533  512  552  431  49854   99   495  1:5.0  2,644                     2.1                        31/2                            2040 3749 4622 5012 5293Increase in strength of Concrete No. 54 over 46- %                            538  626  592  599  470  565Increase in strength of Concrete No. 54 over No. 51-%                            117  117  116  108  109  11362   200  500  1:2.5  1.382                     2.1                        3   2661 5079 6023 6270 6605Increase in strength of Concrete No. 62 over No. 54 -%                            130  135  130  125  125  129Increase in strength of Concrete No. 62 over No. 46 -%                            702  848  771  749  587  731__________________________________________________________________________ 
    
     EXAMPLE 6 
     It is of interest to establish, in a general way, the magnitude of the various strength producing processes that are in play in the low cement-high fly ash content compositions embodied by the scope of this invention. If it is assumed that three basic chemical processes take place in the system, (1) the reaction between cement and water; (2) the reaction between fly ash and water; and (3) an &#34;added reaction&#34;, then the strength contributed by each process can be estimated, using the data shown in Table X for concrete having approximately the same cementitious volume so as to eliminate volume as a minor factor. It is well known that the chemical reaction previously described as the &#34;pozzolanic reaction&#34; is a slow one because it depends on the rate at which cement reacts with water and liberates calcium hydroxide which in itself is a slow process. Since the magnitude of the strength contributed by the &#34;added reaction&#34; (Table X, Line 4) at 1, 7 and 28 days is much greater than that expected for such a reaction, a fourth chemical process must be occurring, a reaction that does not occur in conventional high cement-low fly ash content compositions. 
     
                                           TABLE X__________________________________________________________________________   Cement        Fly Ash             GroundLine   Concrete   (X)  (D)  Quartz                  Compressive Strength PSI Strength ProducingNo.   No.  Lbs/yd.sup.3        Lbs/yd.sup.3             Lbs/yd.sup.3                  1-Day                       7-Day                            28-Day                                 56-Day                                      90-Day                                           Process__________________________________________________________________________1  38   222  --   555  179  686  929  1071 1286 Reaction between                                           cement and water2  62   200  500  --   2661 5079 6023 6270 6605 Reaction between                                           cement and water                                           Reaction between                                           fly ash and water                                           Added reaction3  47   0    742  --   1100 1735 2183 2429 2809 Reaction between                                           fly ash and water4  Line 2-(Line 1 &amp; Line 3)                  1382 2658 2911 2770 2510  Added reaction__________________________________________________________________________ 
    
     EXAMPLE 7 
     Test concretes fabricated from three cements and four fly ashes that fall within the scope of this invention (A,B,C, and E) are described in Table XI. Weight ratios of cement to fly ash vary from a low of 1:1.0 (Concrete No. 80) to a high of 1:10.1 (Concrete No. 92). As is noted in Example 3, the concretes containing fly ashes B and E exhibit somewhat lower 1-day compressive strengths because of their lower surface areas, but rapidly gain strength between 1 and 7 days. The compressive strengths attained by Concrete No. 71 indicate that fly ash B (like D in Table VIII) has some cementitious properties in itself. 
     
                                           TABLE XI__________________________________________________________________________                    Cement to                    Fly AshConcreteCement    Fly Ash   Ratio by %  Slump                                    Compressive Strength PSINo.  Source     Lbs/yd.sup.3          Source               Lbs/yd.sup.3                    Weight                          W/C                             Air                                in. 1-Day                                         7-Day                                              28-Day                                                  56-Day                                                      90-Day__________________________________________________________________________65   X    50   A    500  1:10.0                          6.011                             2.5                                3/4 891  1531 1664                                                  1942                                                      198066   X    101  A    404  1:4.0 2.620                             2.5                                1   1301 2568 3858                                                  4250                                                      462167   X    101  A    758  1:7.5 3.358                             2.3                                21/4                                    1847 2365 2807                                                  3167                                                      380068   X    134  A    310  1:2.3 2.121                             2.1                                21/4                                    1377 2798 3872                                                  4282                                                      445369   X    153  A    357  1:2.3 1.865                             2.2                                2   1239 2688 3939                                                  4465                                                      488670   X    412  A    1031 1:2.5 1.184                             1.4                                71/2                                    2897 4795 5785                                                  6111                                                      688071   X    0    B    495  --    -- 1.3                                6   237  884  1536                                                  2317                                                      285972   X    48   B    347  1:7.2 4.944                             1.4                                4   315  1416 2637                                                  3652                                                      431873   X    49   B    490  1:10.0                          5.103                             1.4                                51/4                                    241  1056 1651                                                  2090                                                      279174   X    98   B    735  1:7.5 2.671                             1.7                                41/2                                    640  2451 3673                                                  4456                                                      541975   X    100  B    400  1:4.0 2.617                             1.1                                6   267  1179 1942                                                  2535                                                      339576   X    134  B    310  1:2.3 1.916                             1.4                                33/4                                    546  2385 3747                                                  5074                                                      548477   X    150  B    350  1:2.3 1.744                             1.2                                6   316  1506 2293                                                  3209                                                      439778   X    104  B    234  1:2.2 1.255                             1.7                                23/4                                    461  2121 3301                                                  4451                                                      505579   X    392  B    980  1:2.5 0.942                             0.4                                11  1039 4029 6577                                                  7183                                                      854780   Y    200  B    200  1:1.0 1.338                             1.5                                21/2                                    418  1439 2877                                                  3543                                                      413381   Y    200  B    300  1:1.5 1.278                             1.5                                33/4                                    572  1999 4015                                                  5122                                                      559382   Y    204  B    408  1:2.0 1.136                             1.9                                21/4                                    794  2905 5415                                                  6174                                                      653783   Y    204  B    510  1:2.5 1.165                             1.9                                21/4                                    953  3088 5732                                                  6432                                                      696384   X    50   C    500  1:10.0                          4.583                             3.0                                2   492  820  987 1050                                                      122585   X    99   C    742  1:7.5 2.766                             2.0                                51/4                                    1031 1786 2505                                                  2747                                                      301286   X    101  C    303  1:3.0 2.532                             2.4                                2   890  1734 2539                                                  3022                                                      328887   X    102  408  1:4.0                    2.215 2.4                             2  1747                                    2411 2874 3897                                                  449288   X    101  C    505  1:5.0 2.296                             2.4                                31/4                                    1056 2628 3639                                                  4368                                                      474789   X    133  C    333  1:2.5 1.782                             2.3                                23/4                                    1806 3115 4158                                                  4796                                                      494790   X    151  C    353  1:2.3 1.582                             2.3                                21/2                                    2027 3027 4072                                                  4888                                                      530291   Z    202  C    505  1:2.5 1.217                             3.0                                3   2383 4586 5688                                                  6395                                                      650092   X    49   E    495  1:10.1                          4.807                             2.5                                31/2                                    98   1064 1516                                                  1693                                                      185493   X    101  E    303  1:3.0 2.483                             2.2                                13/4                                    115  824  1596                                                  1944                                                      208994   X    101  E    404  1:4.0 2.444                             1.8                                3   204  1423 2337                                                  2684                                                      286395   X    99   E    495  1:5.0 2.524                             1.7                                61/4                                    156  1626 2445                                                  2815                                                      298796   X    153  E    357  1:2.3 1.612                             2.3                                2   279  1615 2632                                                  3394                                                      3538__________________________________________________________________________ 
    
     EXAMPLE 8 
     Concretes fabricated from Portland cement and four blends of five fly ashes within the scope of this invention are described in Table XII. The compressive strength, at any given age of test, of Concrete No. 97 should be approximately the same as the average of the strengths of Concrete No. 26 and 27 listed in Table VII. This is not the case. The strength of Concrete No. 97, at every age of test, is significantly higher than the corresponding average strength of Concretes No. 26 and 27 (Table VII). Of the twenty strength values cited in Table XII 65% are significantly higher than the corresponding average calculated from the strength data in Table VII, 20% are essentially the same, and only 15% are lower. This indicates that in the majority of instances, blending two or more of the fly ashes covered by the scope of this patent prior to their use in concrete will lead to a synergistic increase in compressive strength. 
     
                                           TABLE XII__________________________________________________________________________CementConcrete(X)  Fly Ash     Slump                     Air                        Compressive Strength PSINo.  Lbs/yd.sup.3     Source         Lbs/yd.sup.3              w/c                 in. %  1-Day                            7-Day                                28-Day                                    56-Day                                        90-Day__________________________________________________________________________97   202  C   252  1.206                 21/4                     2.4                        3450                            5130                                6052                                    6726                                        6851     D   25298   202  B   252  1.280                 21/2                     2.4                        1293                            4590                                6085                                    6520                                        6724     D   25299   200  A   250  1.352                 21/2                     2.2                        2775                            4908                                5901                                    6367                                        6748     D   250100  200  E   250  1.278                 3   2.2                        1354                            4448                                5728                                    6167                                        6670     D   250__________________________________________________________________________ 
    
     EXAMPLE 9 
     The strength producing properties of the low cement-high fly ash compositions of this invention are also observed when they are used in mortar. A description of the test mortars and their respective compressive strengths, at three ages of test, are listed in Table XIII. All of the test mortars contained 200 grams of cement, 500 grams of fly ash, 2052 grams of sand and 370 grams of water. The sand used in the mortars was natural silica sand, as described in ASTM C109, Section 4.1.1. The mortars were cast into 2&#34;×2&#34;×2&#34; cube molds after mixing. The compressive strengths of the mortars containing the fly ashes within the scope of this invention (Mortars No. 1, 2, 3, 7, 8, 12, 13 and 14) are significantly higher, at all ages of test, than those containing the fly ashes outside the scope of this invention. 
     
                       TABLE XIII______________________________________Mortar Cement   Fly Ash   Compressive Strength - PSINo.    Source   Source    3-Days 7-Days 28-Days______________________________________1      X        A         2000   3200   46002      X        B         850    1700   29003      X        C         1820   2800   43004      X        F         280    550    7005      X        G         290    450    7006      X        I         465    750    12507      Y        D         1660   2400   29508      Y        E         590    1300   22509      Y        H         300    550    70010     Y        J         295    475    87511     Y        K         310    540    90012     Z        D         1810   2850   442513     Z        E         1345   2100   368514     Z        A         2500   2850   451015     Z        H         215    550    110016     Z        J         270    550    115017     Z        K         265    600    1260______________________________________ 
    
     EXAMPLE 10 
     The magnitude of the compressive strengths gained by the low cement-high fly ash mixtures of this invention is further dramatized when they are combined with water (no aggregate) to fabricate pastes. A description of six typical pastes, along with their compressive strengths at three ages of test, are summarized in Table XIV. Each paste was cast into 2&#34;×2&#34;×2&#34; molds immediately after fabrication and moist cured until tested for compressive strength. The compressive strengths of the pastes made from two fly ashes whose composition is outside the scope of this invention. (Pastes No. P-3 and P-6) are significantly lower than those of the other pastes at all ages of test. 
     
                                           TABLE XIV__________________________________________________________________________            Ratio of            CompressivePaste   Cement(Y)    Fly Ash Cement to                    Water       Strength - PSINo.   Grams Source        Grams            Fly Ash-by wt.                    Grams                        w/c 3-Days                                7 Days                                    28-Days__________________________________________________________________________P-1   400   B   1200            1:3.0   350 0.875                            5550                                9050                                     10950P-2   400   C   1200            1:3.0   350 0.875                            2900                                3150                                    8625P-3   400   I   1200            1.3.0   390 0.975                            1900                                2400                                    4200P-4   300   B   1200            1:4.0   350 1.167                            4050                                6100                                    9600P-5   400   A   1200            1:3.0   410 1.025                            4800                                5650                                    8950P-6   400   K   1200            1:3.0   400 1.000                            1700                                2300                                    3350__________________________________________________________________________ 
    
     EXAMPLE 11 
     Concrete fabricated from the low cement-high fly ash mixtures within the scope of this invention responds in an unusual, and to some extent unpredictable, way to the chemical admixtures commonly used in non-fly ash concrete and/or conventional fly ash concretes containing low amounts of fly ash. In a number of experiments, conventional set accelerating agents for Portland cement concretes including calcium chloride, calcium formate and triethanolamine, were added to concretes of this invention containing fly ashes A, B, C and D in greater than 1 to 2, cement to fly ash, ratios. Calcium chloride when added to a mixture of cement X and fly ash A (1 to 2.5 ratio) at its typical rate of 2% (1) based upon the cement, (2) based upon the fly ash, and (3) based upon cement plus fly ash, surprisingly was found to either retard or have no effect upon the initial setting time of the concretes. In similar experiments, calcium formate was found surprisingly to act as a retarder, that is the initial setting times of the concretes were delayed. At addition rates of 0.04 and 0.06 percent on the weight of cement and fly ash, triethanolamine had very little effect on the setting time of concretes within the scope of this invention containing cement &#34;X&#34; and fly ash &#34;A&#34; in a 1 to 2.5 ratio. When the addition rates were increased to 0.08 and 0.20 percent in concretes of the invention prepared using cement &#34;X&#34; and fly ash &#34;B&#34; (1 to 2.5 ratio), the setting times were actually significantly delayed, a result quite the opposite to that to be expected. The effect of the three chemical admixtures (calcium chloride, calcium formate and triethanolamine) on the compressive strengths of the test concretes was in the majority of cases, a positive one. For example, of 30 compressive strength-values measured for the concretes treated with a chemical admixture, 23 or approximately 77%, are higher than the strengths of the reference, non-admixed concretes at three ages of test (1, 7 and 28 days). For the sake of brevity, the detailed data is not given herein. 
     EXAMPLE 12 
     The effect of adding calcium chloride (and calcium formate) on the setting time of the low cement-high fly ash compositions of the invention was further investigated using a modification of the ASTM C403 method. In the ASTM C403 procedure, the coarse aggregate is removed from the test concrete by screening prior to setting time measurement. In the modified C403 method, mortar having a composition similar to that of the C403 screened mortar is fabricated and its setting time determined by the standard penetration technique. The effect of calcium chloride and calcium formate on the setting time of cement &#34;Y&#34; and fly ash &#34;D&#34;, 1:2.5 weight ratio mixtures was found to be essentially the same as that reported in Example 11 for 1:2.5 weight ratio mixtures of cement &#34;X&#34; fly ash &#34;A&#34; and &#34;B&#34;. The same can be said for the 1:2.5 as well as the 1:2.0; 1:3.0 and 1:4.0 weight ratio mixtures of cement &#34;Y&#34; and fly ash &#34;C&#34; when treated with calcium chloride. However, all four of the combinations of cement &#34;Y&#34; and fly ash &#34;B&#34; that were tested exhibit a dramatic acceleration in initial setting time when admixed with calcium chloride, which illustrates the unpredictability of the response of the low cement-high fly ash compositions of the invention to the set accelerating admixtures commonly used with non-fly ash concretes and/or conventional fly ash concrete. Again, for the sake of brevity, the detailed data is not given herein. 
     EXAMPLE 13 
     A set retarding admixture is a chemical additive for concrete, mortar or paste that reduces the rate of hardening or setting, thus increasing the time required to reach initial and final set. Three set retarding admixtures commonly used with non-fly ash concrete and/or conventional fly ash concrete are (1) salts of lignosulfonic acid, (2) salts of hydroxylated carboxylic acids such as gluconic acid and heptogluconic acid and (3) carbohydrates, usually in the form of high molecular weight glucose polymers such as corn syrup. In order to obtain approximately two hours set retardation at room temperature, the first is conventionally added at the rate of about 0.25% and the second and third at the rate at about 0.06% on the weight of cement in the concrete. The results of adding representatives of these three chemical admixtures to low cement-high fly ash concretes of the invention were investigated. The setting times were measured in accordance with the ASTM C403 procedure and the weight ratio of cement to fly ash in all of the mixtures was 1:2.5. When the three admixtures are added at a rate comparable to that used in conventional concrete, i.e., the rate is based on the weight of cement, the setting time is either unaltered or accelerated. When the addition rate is based on the weight of fly ash or the weight of cement plus fly ash, the initial set is retarded. For example, an addition rate of 0.25% based on the total weight of cement and fly ash represents 0.875% calcium lignosulfonate on weight of cement only. If the admixture is delaying the hydration of the cement only and if the initial set is due to the cement, as it is in conventional concrete, then the delay in initial set would be on the order of 18 to 24 hours. This is another strong indication that some process is at work in the low cement-high fly ash system of the invention that cannot be explained by existing technology. Again, for the sake of brevity, the detailed data is not given herein. 
     EXAMPLE 14 
     In this example, the effect of common set retarding admixtures on the initial setting time of the low cement-high fly ash mixtures of the invention was further investigated using the modified ASTM C403 method. When mixtures of cement &#34;Y&#34; and fly ash &#34;B&#34; having weight ratios of 1:2.0; 1:2.5; 1:3.0 and 1:4.0 are tested with the three retarders of Example 13 at the normal rate but based on the total weight of cement and fly ash, the initial set is retarded and the degree of retardation is greater than that reported in Example 13 for mixtures of cement &#34;X&#34; and fly ash &#34;A&#34; and &#34;B&#34;. However, when mixtures of cement &#34;Y&#34; and fly ash &#34;C&#34;, in weight ratios of 1:2.0; 1:2.5; 1:3.0 and 1:4.0, are treated with sodium gluconate at the same addition rate based on the weight of cement and fly ash, the initial set is accelerated. This is an unexpected phenomenon which demonstrates a novel chemistry in connection with the low cement-high fly ash systems of the invention. Again, for the sake of brevity, the detailed data is not given herein. 
     EXAMPLE 15 
     In this Example, a fly ash having a composition outside of those within the invention (Table II) was blended with various chemical compounds in an attempt to bring its overall composition within that of Table II. In one experiment, approximately 35 lbs. of calcium sulfate, 18 lbs. of magnesium oxide and 115 lbs. of calcium hydroxide were thoroughly blended with 350 lbs. of fly ash G (Blend #1). A second blend was made from approximately 35 lbs. of sodium sulfate, 131 lbs. of calcium hydroxide, 17 lbs. of magnesium oxide and 327 lbs. of fly ash G (Blend #2). Both blends were then evaluated in concrete having a cement to blend ratio of 1:2.5 by weight. The composition of the two blends is listed in Table XV and the concrete data are summarized in Table XVI. The data in Table XVI clearly indicates that the composition range covered by the scope of this patent must be produced within the ash itself during the burning of the coal and that such composition cannot be synthesized by simple blending of chemical ingredients in order to get the exceptionally high compressive strength. In Table XVI, the strengths of the blends were improved by the attempt at synthesization, but were not as great as is obtained with compositions of the invention. 
     
                       TABLE XV______________________________________Composition of Blends            #1       #2______________________________________% SiO.sub.2        35.3       33.5Al.sub.2 O.sub.3   20.9       19.9Fe.sub.2 O.sub.3   5.6        5.3% SiO.sub.2 + Al.sub.2 O.sub.3 + Fe.sub.2 O.sub.3              61.8       58.7CaO                22.9       22.6MgO                3.9        3.8SO.sub.3           4.2        4.1______________________________________ 
    
     
                                           TABLE XVI__________________________________________________________________________ConcreteCement  Fly Ash    Slump                       Air                          Compressive Strength PSINo.  Source    lbs/yd.sup.3        Source            lbs/yd.sup.3                w/c                   In. %  1-Day                              7-Day                                  28-Day                                      56-Day                                          90-Day__________________________________________________________________________123  X   200 G   500 1.620                   3   2.1                          262 871 1511                                      2022                                          3010124  X   200 Blend 1            500 1.873                   4   1.7                          173 597 1744                                      2687                                          3674125  Y   196 G   490 1.683                   4   1.7                          201 869 1627                                      2520                                          NM*126  Y   200 Blend 2            500 1.814                   41/4                       2.0                          326 873 2010                                      2841                                          NM__________________________________________________________________________ *Not measured 
    
     EXAMPLE 16 
     A blend of two or more fly ashes which in combination has a composition that falls within Table II also produces concrete of unusually high compressive strength when combined with relatively small amounts of Portland cement. For example, fly ash &#34;D&#34; and fly ash &#34;G&#34; were thoroughly blended in a weight ratio of 3 parts &#34;D&#34; and 1 part &#34;G&#34; and the blend was evaluated in concrete. Concretes containing only fly ash &#34;D&#34; and only fly ash &#34;G&#34; were used as reference mixes. Cement &#34;Y&#34; was used in all three test concretes and the cement to fly ash weight ratio was 1:2.5. The test data are summarized in Table XVII. If one calculates weighted averages of Concrete Nos. 127 and 129 and compares these with No. 128, the combination produces greater strength than expected from the weighted averages for strengths obtained after 7 days, particularly after 90 days. 
     
                                           TABLE XVII__________________________________________________________________________ConcreteCement(a)      Fly Ash    Slump                     Air                        Compressive Strength PSINo.  lbs/yd.sup.3      Source          lbs/yd.sup.3              w/c                 In. %  1-Day                            7-Day                                28-Day                                    56-Day                                        90-Day__________________________________________________________________________127  200   D   500 1.264                 21/4                     1.9                        3342                            6139                                6959                                    7519                                        7836128  198   D   371      G   124 1.381                 3   1.7                        2219                            4556                                5763                                    6593                                        7130129  198   G   495 1.652                 4   1.4                         306                            1018                                1740                                    2231                                        2959__________________________________________________________________________  (a)Cement-Brand Y 
    
     EXAMPLE 17 
     In this Example, the dimensional stability of the low cement-high fly ash compositions of the invention were tested when subjected to autoclave curing conditions. Several cement/fly ash/water pastes were prepared and tested for their autoclave soundness in accordance with the method described in ASTM C151. The soundness requirement for Portland cement (ASTM C150) allows a maximum expansion of 0.80% when tested in accordance with ASTM C151. None of the pastes tested exceeded this limit; in fact, two of the pastes exhibited some shrinkage. For the sake of brevity, the detailed data is not given herein. 
     EXAMPLE 18 
     A series of eight ASTM C109 mortars was prepared in an effort to better understand the cause of the unexpectedly high compressive strengths developed by the low cement-high fly ash systems of the invention. Descriptions of the mortars along with the 7-day compressive strength developed by each are summarized in Table XVIII. Powdered silica, SiO 2 , which is chemically inert, was added to six of the test mortars so as to maintain a reasonable constant volume of mortar throughout the series. In Mortar No. 18, the 300 grams of cement generated 5200 P.S.I. (at 7 days) or 17.3 P.S.I./gram of cement (5200 P.S.I.÷300 g.). If this latter value can be assigned to Mortar No. 19, the cement in the mortar should have contributed 1491 P.S.I. (86 g. cement×17.3 P.S.I./gram). The difference between the measured strength of 3250 P.S.I. and the 1491 P.S.I., or 1759 P.S.I., must have been produced by a reaction of the fly ash. The strength produced by Mortar No. 21, which contained an amount of Ca(OH) 2  equivalent to that which would be produced if the cement in Mortar No. 19 were to completely hydrate is strictly due to the pozzolanic reaction i.e., the reaction between the calcium hydroxide and the fly ash. Substracting the 450 P.S.I. generated by this reaction from the 1759 P.S.I. leaves 1309 P.S.I. unaccounted for and can only be attributed to some other interaction between the fly ash and the cement. The amount of synthetic tricalcium silicate (C 3  S) employed in Mortar No. 20 is equivalent to that added to Mortar 19 by way of the cement. The fact that the strengths produced by Mortars No. 19 and 20 are essentially identical, indicates that the other components of Portland cement are not important to the 7-day compressive strengths of the low cement-high fly ash system of the invention. Mortar No. 22 is a duplicate of No. 20 and No. 25 is a duplicate of No. 21, but prepared in a different day. There is excellent agreement in the measured 7-day compressive strengths. The close similarity in the strengths of Mortars No. 23 and 24 indicates that the added calcium hydroxide (in No. 24) does very little to enhance the strength and that the C 3  S-fly ash combination is the principal contributor to strength at 7-days. 
     
                       TABLE XVIII______________________________________  Mortar No.  18   19     20     21   22   23   24   25______________________________________Cement-  300     86    --   --   --   --   --   --GramsFly Ash C-    --     214    214  214  214  214  214  214GramsASTM C109Sand -   825    825    825  825  825  825  825  825GramsWater -  145    145    145  145  145  145  145  145GramsC.sub.3 S - Grams    --     --      51  --    51   40   40  --Ca(OH).sub.2 -    --     --     --    25  --   --    9    25GramsPowderedSiO.sub.2(inert - --     --      35   61   35   44   35   61Grams)7-DayCompressiveStrength -    5200   3250   3100 450  3050 2550 2600 500PSI______________________________________ 
    
     EXAMPLE 19 
     In this Example, a low-density, lightweight porous mass having utility e.g. as a thermal insulating protective coating was prepared having the following composition: 
     
         ______________________________________          Grams______________________________________Portland cement  171Fly Ash &#34;D&#34;      429Expanded perlite 400Water            1025______________________________________ 
    
     A small amount of alpha olefin sulfonate surfactant as described in U.S. Pat. No. 3,926,650 was added to entrain air and give a hydrated mass having a density of 30.6 pounds per cubic ft. The expanded perlite used had a bulk density of approximately 6 pounds per cubic foot. 
     A similar composition substituting expanded vermiculite for perlite could be prepared from 6 cubic feet of expanded vermiculite (7 pounds p.c.f. density), 47 pounds of Portland cement, 117 pounds of fly ash, water and air-entraining, surface active agent. Such lightweight mixtures produce valuable low density, thermal insulating mixtures for use, inter alia, in roofs, etc. In such cases, sufficient surfactant is used to give a homogenous, non-segrated mixture and the desired density, typically less than about 40 pounds per cubic foot. A typical addition rate for the surface active agent is approximately 0.10 percent by weight of the cement and fly ash. 
     While the invention has been described herein using cements particularly characterized by the art as Portland cements as the reactive components with the high proportions of select fly ash according to the invention, it will be obvious to one skilled in the art that any cement similar to Portland having a significant amount of tricalcium silicate (3CaO. SiO 2 ) and hydratable with water can likewise be employed in the compositions of the invention, and all such similar cements are intended to be included within the term &#34;Portland cement&#34; as used herein and in the following claims.