Abstract:
Magnetoresistive devices with increased response sensitivity to external magnetic fields and an increased magnetoresistive ratio (MR ratio) to cope with rapid advances made in a high-density magnetic recording device. A patterned dielectric layer is laminated in a flat shape on a substrate capable of being doped with carriers (holes) in an electric field, and an FET structure with gate electrodes is then fabricated on that dielectric layer, and the substrate spatially modulated by applying a non-uniform electrical field to induce a first ferromagnetic domain, a nonmagnetic domain and a second ferromagnetic domain.

Description:
CLAIM OF PRIORITY  
         [0001]    The present application claims priority from a Japanese application JP 2003-176293 filed on Jun. 20, 2003, the content of which is hereby incorporated by reference into this application.  
         FIELD OF THE INVENTION  
         [0002]    The present invention relates to laminated magnetoresistance devices containing a ferromagnetic layer, nonmagnetic layer, ferromagnetic layer and to electronic devices using these magnetoresistance devices.  
         BACKGROUND OF THE INVENTION  
         [0003]    The magnetoresistance effect is generally a physical phenomenon wherein a magnetic field is applied to a magnetic material to vary the electrical resistance. The GMR device that utilizes the giant magnetoresistance (GMR) effect discovered in metallic multilayer film structures comprised of laminations of ferromagnetic metal layers/nonmagnetic metal layers/ferromagnetic metal layers is already utilized in magnetic read-out heads. In recent years, the application of magnetic random access memory (MRAM) devices as nonvolatile memories is under study. However, due to the tremendous advances made in magnetic recording density, utilizing magnetoresistance devices in next generation magnetic heads and large capacity MRAM requires making the magnetoresistance ratio (MR ratio) even larger, and making further increases in the sensitivity response to external magnetic fields.  
           [0004]    In recent years, magnetoresistance devices (tunneling magneto-resistance devices: TMR devices) that utilize the tunnel current flowing between both ferromagnetic layers have been discovered. In other words, these TMR devices use the tunnel current that flows when a tunnel junction with an insulating layer is inserted between two ferromagnetic layers namely, a ferromagnetic tunnel junction. The magnetoresistance ratio in these ferromagnetic tunnel junction devices exceeds 20 percent (Non-patent Document 1) so there is increasing potential for applications in magnetic heads and magnetoresistance effect memories. The magnetoresistance ratio at room temperature is approximately 40 percent; however an even larger magnetoresistance ratio is needed in order to obtain the output voltage needed for magnetic read-out heads of high density magnetic recording medium.  
           [0005]    In MRAM applications using TMR devices, an external magnetic field (an electromagnetic field) is applied to ferromagnetic layer without a fixed magnetic direction (freely magnetized layer) by making an electrical current flow in the external wiring to reverse the magnetic direction of the free layer of magnetization. However, the constantly shrinking size of the memory cell brings about an increase in the magnetic field (magnetic switching field) required for magnetic reversal of the freely magnetized layer that causes an unavoidable increase in the wiring current for writing. Therefore, increasing the capacity of the MRAM causes an unavoidable increase in electrical power consumption. The increased electrical current in the wiring brings the potential problem of the wiring melting. One method for resolving this problem is to cause a magnetic reversal by injecting a spin-polarized spin current (Non-patent Document 2). However, this method for inducing a magnetic reversal by injecting a spin current, increases the electrical current density flowing in the TMR device. This increase in electrical current density might possibly cause the wiring to deteriorate or induce a ferroelectric breakdown in the tunnel insulation (dielectric) due to electro-migration.  
           [0006]    In recent years, on the other hand, much attention has been focused on new magnetic material capable of being utilized in magnetoresistive devices. These are diluted magnetic semiconductors such as type III-IV semiconductors typically of GaAs, InAs or type IV semiconductors of germanium, substituted in part with the magnetic atom manganese. In particular, structures of field effect transistors (FET) fabricated using a magnetic semiconductor as the substrate are capable of inducing a magnetic phase transition from a non-magnetic phase to a ferromagnetic phase by applying an external voltage from the gate electrode to the internal portion of the magnetic semiconductor substrate (Non-patent Document 3).  
           [0007]    This electric field-induced magnetic phase transition is caused by the fact that the ferromagnetic transition temperature of the magnetic semiconductor is strongly dependent on the carrier (hole) concentration. The above FET device is an innovative device that utilizes this physical effect to cause shifts in the bulk magnetic state (ferromagnetic state/non-magnetic state) even under fixed temperature conditions, by effectively injecting (doping) carriers the semiconductor internally by applying an electrical field externally. Besides diluted magnetic semiconductors, another material known to be capable of this type of electric field-induced magnetic phase transition is manganese oxides having a perovskite crystalline structure. However, the internal magnetic semiconductor substrate of this FET is not comprised of a ferromagnetic/nonmagnetic/ferromagnetic junction structure, and so no improvement in the MR ratio can be expected even in the vicinity of the magnetic phase transition. This FET structure is therefore not suited for use as a magnetoresistive device.  
           [0008]    The diluted magnetic semiconductors are predicted to be a half metal (spin polarization of the fermi surface equals 100%) by an elaborate calculation of electronic states. Based on this prediction, the laminated magnetoresistive device with a nonmagnetic semiconductor layer inserted between the magnetic semiconductor layers is expected to have an MR ratio in excess of 100%. Even though, trial fabrication of ferromagnetic junction type magnetoresistive devices using magnetic semiconductor has also begun very recently, a magnetoresistive device having an MR ratio in excess of 40 percent at room temperature has not been achieved.  
           [0009]    [Non-patent Document 1] 
           [0010]    J. Appl. Phys.79, 4724 (1996)  
           [0011]    [Non-patent Document 2] 
           [0012]    Appl. Phys. Lett. 78, 3663 (2001)  
           [0013]    [Non-patent Document 3] 
           [0014]    Nature 408, 944 (2000), Science 295, 651 (2002)  
           [0015]    The magnetoresistive device of the related art typically contains a three-layer laminated heterogeneous junction structure comprised of a ferromagnetic layer, nonmagnetic layer, and ferromagnetic layer. However fabricating a satisfactory heterogeneous interface/junction and a uniformly thin intermediate layer is extremely difficult. Microscopic irregularities at the crystal boundaries of the heterogeneous junction and the effects of microscopic pin holes formed unintentionally in the nonmagnetic intermediate layer create the problem that the MR ratio of the magnetoresistance device drastically deteriorates from the theoretically expected value. Further, the MR ratio in the magnetoresistive device, varies according to the film thickness of the nonmagnetic intermediate layer so that obtaining a large improvement in the MR ratio and optimizing with the peripheral circuits could only be achieved by experimentally fabricating large numbers of devices with nonmagnetic layers of different film thickness.  
         SUMMARY OF THE INVENTION  
         [0016]    In order to resolve the above problems with the related art, a first object of the present invention is to provide an optimized, electrically-controlled magnetoresistance device, further having an improved MR ratio only by using the field effect in FET structures using magnetic materials (for example, diluted magnetic semiconductor) capable of electric-field type of carrier-doping of the substrate, and further provide magnetic sensors of different types or high sensitivity magnetic heads for high density magnetic recording medium utilizing these magnetoresistive devices. A second object of the present invention is to provide an MRAM device having low power consumption and an adequate output signal by utilizing a field effect magnetoresistive device as the means for writing the MRAM memory cells.  
           [0017]    The magnetoresistance device utilizing the field effect of the present invention is a device containing a substrate capable of being doped with carriers (holes) in an electric field, wherein a patterned dielectric (insulating) layer is laminated in a flat shape on this substrate and by forming an FET structure with gate electrodes on that dielectric layer, a non-uniform spatially modulated electrical field is applied to the substrate. This field effect is essentially characterized by inducing a strongly electric-doped domain (first ferromagnetic domain), a weakly doped domain (nonmagnetic domain), and a strongly doped electrical field domain (second ferromagnetic domain).  
           [0018]    The present invention further provides a magnetoresistive device with an MR ratio equal to or higher than the three-layer laminated heterogeneous junction device of the related art and is characterized by containing a means to control the magnetoresistive value or MR ratio accompanying the electrical current flowing between the first and the second ferromagnetic domains magnetically coupled via a nonmagnetic domain, by applying an external voltage to the gate electrodes.  
           [0019]    The field effect spin-controlled device of the present invention is characterized essentially in actively controlling the direction of magnetization of the first through the second ferromagnetic domains in magnetoresistive devices with the above described structure by utilizing the electric field effect. Here, the magnetic exchange interaction between both ferromagnetic domains inducing positive and negative oscillations as a function of the particular voltage, is utilized based on the RKKY (Ruderman-Kittel-Kasuya-Yosida) mechanism or quantum well mechanism functioning via the intermediate nonmagnetic domain in both the ferromagnetic domains. The present invention therefore provides a technology for magnetic reversals by electric field carrier doping.  
           [0020]    The above described device utilizes the same material in the substrate and therefore has the advantages of no crystal irregularities or defects in the magnetic junction boundary effective in inducing the field effect. In the device structure of the present invention, the MR ratio can be controlled and optimized just by applying a voltage from the gate electrode. Another advantage is that the power consumption required for device operation can be significantly lowered by utilizing the electrical field effect. Further, utilizing a magnetic semiconductor in the substrate will provide good compatibility with conventional semiconductor manufacturing process technology and make integration with peripheral semiconductor circuits simpler.  
           [0021]    The magnetic read-out head and magnetic sensor of the present invention are characterized in containing a field effect magnetoresistive device. The magnetic random access memory of the present invention is characterized in containing a field effect spin-controlled device. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0022]    [0022]FIG. 1A is a cross sectional view showing the FET structure of the field effect magnetoresistive device of the first embodiment;  
         [0023]    [0023]FIG. 1B is a cross sectional view of a typical junction structure for the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain patterned in a flat shape;  
         [0024]    [0024]FIG. 2A is a cross sectional view showing the FET structure of the field effect magnetoresistive device of the second embodiment;  
         [0025]    [0025]FIG. 2B is a cross sectional view of a typical junction structure for the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain patterned in a flat shape;  
         [0026]    [0026]FIG. 3 is a graph showing the magnetoresistance (reluctance) characteristics of the magnetoresistance device of the first embodiment or second embodiment;  
         [0027]    [0027]FIG. 4A is a cross sectional view showing the multi-joint structure of the FET structure of the first embodiment;  
         [0028]    [0028]FIG. 4B is a cross sectional view of an example of the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain multi-junction structure;  
         [0029]    [0029]FIG. 5 is a cross sectional view of the field effect spin-controlled device of the fourth embodiment;  
         [0030]    [0030]FIG. 6 is a graph showing positive and negative oscillations as a function of the gate voltage Vg in the magnetic exchange interaction between the first ferromagnetic domain and the second ferromagnetic domain;  
         [0031]    [0031]FIG. 7 is a drawing showing the operating principle and the basic structure of the electrically-driven MRAM utilizing the field effect spin-controlled device described in the fourth embodiment;  
         [0032]    [0032]FIG. 8 is a diagram showing the circuit configuration of the fixed memory when the electrically-driven MRAM cells shown in FIG. 7 are arrayed in a 2-row vertical and 2-row horizontal X-Y matrix;  
         [0033]    [0033]FIG. 9 is a concept drawing showing an example of one memory device mounted on the silicon substrate of the fixed memory when the electrically-driven MRAM cells shown in FIG. 8 are arrayed in a 2-row vertical and 2-row horizontal X-Y matrix; and  
         [0034]    [0034]FIG. 10 is a cross sectional view showing another FET structure of the gate electrode  13  in the field effect magnetoresistance device of the first embodiment shown in FIG. 1A.  
     
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0035]    First Embodiment  
         [0036]    [0036]FIG. 1A is a cross sectional view showing the FET structure of the field effect magnetoresistance device of the first embodiment. An electrical insulating layer  12  whose structure is patterned in a convex shape is formed on the upper part of the nonmagnetic substrate  11  capable of being doped with electric field carriers. A first metallic electrode (gate electrode)  13  is formed on the insulating (film) layer  12 . When an external section applies a positive voltage of Vg&gt;0 to the gate electrode  13  from the power supply  17 , a strong electrical field is applied locally to the substrate directly below the region where the insulating film layer is thin and that part of the substrate can be doped with a high concentration of hole carriers (doped region with high concentration of carriers is formed). On the other hand, when a weak electrical field is applied to the region on the substrate directly below region where the insulating film is thick, then that part of the substrate can be doped with a low concentration of hole carriers (doped region with a low concentration of carriers is formed).  
         [0037]    [0037]FIG. 1B is a cross sectional view of a typical junction structure for the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain patterned in a flat shape (on the substrate). Setting the voltage Vg as needed in this structure, allows a transition in the nonmagnetic substrate  11  to a highly concentrated doped region in ferromagnetic domain  111  and  113 , and into the low concentrated doped region of nonmagnetic domain  112 . The electrical field has no actual effect here on both ends  110  so this is a nonmagnetic domain which is the original nonmagnetic substrate  11 .  
         [0038]    When the intermediate nonmagnetic domain  112  within the junction structure comprised of the ferromagnetic domain  111 /nonmagnetic domain  112 /ferromagnetic domain  113  and patterned in a flat shape, conducts like a metal, then it effectively functions as a GMR (giant magnetoresistance) device. When the intermediate nonmagnetic domain  112  conducts like a dielectric or a semiconductor, then it effectively functions as a TMR (tunneling magnetoresistance) device. The electromagnetic resistance R(H) of the field effect magnetoresistance device of the present invention can by obtained by measuring the electrical resistance as a function of the external magnetic field H, when a power supply  16  is connected across a second metal electrode (source electrode)  14  and a third electrode (drain electrode)  15  formed on the upper part of both ends of substrate  11  and an electrical current made to flow.  
         [0039]    An overview of the process for fabricating the three-terminal FET structure of the first embodiment is described next. The three-terminal FET structure of the first embodiment was fabricated by a process identical to that in semiconductor processing technology used for manufacturing MOS-FET devices.  
         [0040]    A support substrate for forming the three-terminal FET structure is first of all prepared. This support substrate is for example a silicon substrate of a specified thickness. A magnetic semiconductor piece Mn x Ge 1−x  (X=0.04) capable of being doped with electric field carriers is used as the substrate  11 . The substrate  11  is formed on this support substrate. An insulating alumina layer (Al 2 O 3 ) is then deposited by sputtering or molecular beam epitaxy (MBE) to a uniform film thickness of 5 nanometers on the upper surface of the substrate  11  to form an electrical insulating film  12 . The alumina layer here is formed by the natural oxidation method or plasma oxidization method after first forming an aluminum-atom layer by evaporation deposition. Further, a convex structure (convex portion width of 20 nm) is then formed by removing a film thickness of 3 nanometers from both sides of the insulating film  12  by a chemical etching method. Next a gate electrode (Au)  13 , a source electrode (Au)  14  and a drain electrode (Au)  15  are evaporation deposited. An insulating layer is then formed as a protective layer and connections made to each electrode after forming the required wiring.  
         [0041]    The substrate  11  may be comprised not just by the Mn x Ge 1−x , but by other materials capable of switching the magnetic—nonmagnetic states by typical carrier doping. Diluted magnetic semiconductor may for example be type III-V semiconductors such as GaAs, InAs atoms, or type IV semiconductors such as silicon or germanium with a portion of their atoms substituted by magnetic atoms such as manganese. Magnetic semiconductors doped with manganese atoms may be utilized in wide gap semiconductors such as GaN and ZnO. Besides magnetic semiconductors, perovskite crystal structures made up of manganese oxides or GaAs/MnSb granular structures may also be used. The insulating material need not only be alumina, and any material may be used as the insulating material if it has a high ferroelectric constant and does not cause destruction of the insulation when a gate voltage Vg is applied during device operation. Such insulating materials include Si 3 N 4 , SiO, and MgO.  
         [0042]    The process described here may also be applied in the same way to the second embodiment and the third embodiment.  
         [0043]    Second Embodiment  
         [0044]    The FET structure of the field effect magnetoresistance device of the first embodiment can also be achieved with a ferromagnetic substrate capable of being electric carrier doped rather than by a non-magnetic substrate capable of being doped with electrical field carriers. In other words, a ferromagnetic domain/nonmagnetic domain/ferromagnetic domain junction structure possessing functions identical to the first embodiment can be achieved even by a ferromagnetic substrate capable of being doped with electric field carriers.  
         [0045]    [0045]FIG. 2A is a cross sectional view showing the FET structure of the field effect magnetoresistance device of the second embodiment. Sections identical to the first embodiment of FIG. 1A are assigned the same reference numerals. Comparing FIG. 2A with FIG. 1A clearly shows that an electric field carrier dopable ferromagnetic substrate  21  is utilized instead of the electric field carrier dopable nonmagnetic substrate  11 . This comparison also shows that a concave shape has been substituted for the convex shape of the electrical insulating film  12  pattern formed on the field carrier dopable ferromagnetic substrate  21 . Further, a reverse bias voltage (negative voltage) Vg&lt;0, has been applied to the gate electrode  13  instead of the positive voltage Vg&gt;0.  
         [0046]    [0046]FIG. 2B is a cross sectional view of a junction structure for the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain patterned in a flat shape. Applying a suitable voltage value Vg in this junction structure shifts transitions just the intermediate region of the carrier doped ferromagnetic substrate  21  to a nonmagnetic domain  212  and transitions the ferromagnetic substrate  21  to the highly concentrated doped ferromagnetic domains  211  and  213 . The electrical field has no actual effect here on both ends  210  so this is a ferromagnetic domain of the original ferromagnetic substrate  21 .  
         [0047]    [0047]FIG. 3 is a graph showing the magnetoresistance (reluctance) characteristics of the magnetoresistance device fabricated as previously described. The MR ratio obtained from the electrical resistance by applying a gate voltage (Vg) of approximately three volts across the source electrode  14  and the drain electrode  15  was an extremely large value of approximately 120 percent.  
         [0048]    Third Embodiment  
         [0049]    A multijunction GMR device or TMR device and its multiple circuits can easily be formed on the substrate by combining the detailed patterning of the insulating layer  12  of the first embodiment or the second embodiment and the MR ratio can be further improved. FIG. 4A is a cross sectional view showing the multi-joint structure of the FET structure of the first embodiment. FIG. 4B is a cross sectional view of the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain multi-junction structure. In FIG. 4B, the reference numerals  111  and  113  should be assigned to the ferromagnetic domains between two nonmagnetic domains  112 ; however, to avoid complexity, one number was assigned.  
         [0050]    When comparing the magnetoresistance of the magnetoresistance device comprising the above described multijunction GMR device or TMR device with the simple device shown in FIG. 3, the multijunction quantity is set as n, and the total series-connected magnetoresistance is found to be improved n times.  
         [0051]    (Applications of the First, Second and Third Embodiments)  
         [0052]    The three-terminal FET structure shown in FIG. 1, 2 and FIG. 4 can easily be incorporated into a magnetic read-out head and magnetic sensor. The present field effect magnetoresistance device operates by sensing the magnetoresistance across the source and drain electrodes of the FET structure, the same as with a typical magnetic head and magnetic sensor. The most significant feature of the device of the present invention is that the MR ratio and the write sensitivity are optimized by setting an optimal gate voltage Vg value. Also clearly apparent is that the power consumption accompanying the field effect does not occur as the leak current from the gate electrode can be ignored. Also, even if an electrical field leakage occurs from the FET structure, the present device has the benefit that the electrical field leakage itself will not alter the magnetism of the section used for magnetic sensing.  
         [0053]    Fourth Embodiment  
         [0054]    The basic structure and the operating principle of the field effect spin-controlled device of the fourth embodiment is described next while referring to FIG. 5.  
         [0055]    [0055]FIG. 5 is a cross sectional view of the field effect spin-controlled device of the fourth embodiment. Here, the structure of the substrate  11 , insulating layer  12 , gate electrode  13  and the gate electrode  14  for applying a gate voltage Vg is the same structure as the field effect magnetoresistance device of the first embodiment. In the fourth embodiment, the antiferromagnetic layer  34  is formed on the surface opposite the surface formed by the gate electrode  13  of substrate  11  at a position matching the left half of the gate electrode  13 . The presence of the antiferromagnetic layer  34  fixes (pins) the magnetic orientation (spin) of the first ferromagnetic domain (left side of substrate  11  in drawing) induced when the gate voltage Vg is applied to the gate electrode  13 . The first ferromagnetic domain therefore becomes a fixed magnetized layer. This fixed magnetized layer is indicated in FIG. 5 by the thick black arrow on the left side of the substrate  11 . However, the magnetism (spin) of the second ferromagnetic domain (right side of substrate  11  in drawing) is not fixed, and the second ferromagnetic domain layer becomes a freely magnetized layer. This freely magnetized layer is indicated in FIG. 5 by the thick arrows with the solid line and or broken lines on the right side of the substrate  11 .  
         [0056]    The effective width of the nonmagnetic domain narrows as the gate voltage Vg increases so the magnetic exchange interaction J between the first ferromagnetic domain and the second ferromagnetic domain as a function of the gate voltage Vg is expressed by the positive and negative swings (oscillation) with a shape such as shown in FIG. 6. In the conventional GMR device comprised of laminations of a ferromagnetic metal layer/nonmagnetic layer/ferromagnetic metal layers, the magnetic exchange interaction J that acts across both ferromagnetic layers is known to have positive/negative swings (oscillations) that are a function of the increasing film thickness of the nonmagnetic layer. This same effect of this phenomenon can be achieved in the field effect spin-controlled device of the fourth embodiment by controlling the gate voltage Vg. This phenomenon is physically explained by the interaction effect of the RKKY mechanism or the quantum well mechanism.  
         [0057]    From the above description, with a gate voltage Vg value (3 volts in the example in FIG. 6) for the magnetic exchange interaction J&gt;0, the freely magnetized layer has a spin position parallel to the magnetic direction of the fixed magnetic layer (solid line arrow in FIG. 5). On the other hand, with a gate voltage Vg for the magnetic exchange interaction J&lt;0, (5 volts in the example in FIG. 6) the freely magnetized layer has a spin position that is antiparallel to the magnetization (arrow with broken line in FIG. 5) of the fixed magnetized layer. Therefore the magnetization of the second ferromagnetic domain can be set as needed by controlling the gate voltage Vg.  
         [0058]    This magnetic reversal phenomenon of the fourth embodiment can be easily confirmed by an observation means such as spin SEM (spin-polarized scanning electron microscopy) and MFM (magnetic force microscopy).  
         [0059]    An overview of the process for fabricating the field effect spin-controlled device of the fourth embodiment is described next. The spin-controlled device is fabricated by a process identical to that in the first embodiment in semiconductor processing technology used for manufacturing MOS-FET devices.  
         [0060]    A support substrate for forming the three-terminal FET structure is first of all prepared. This support substrate is for example a silicon substrate of a specified thickness. The substrate  11  uses a magnetic semiconductor piece Mn x Ge 1−x  (X=0.04) capable of being doped with electric field carriers. In the fourth embodiment, both surfaces of the substrate  11  must be processed. To perform this processing, a gate electrode (Au)  13  is first of all formed on this support substrate. A concave structure (recessed section width is 20 nanometers) is formed by stripping away three nanometers in the center structure. An insulating alumina layer (Al 2 O 3 ) is then deposited by sputtering or molecular beam epitaxy (MBE) to a uniform film thickness of 5 nanometers on the upper surface of the substrate  11  to form an electrical insulating film  12 . The alumina layer here is formed by first depositing aluminum atoms and then using the natural oxidation method or plasma oxidization method. An electrode (gold)  14  is then formed on one side of the insulating film  12 . Then, after forming the substrate  11 , an antiferromagnetic layer  34  for example of MnIr alloy is formed on the upper surface of the substrate  11  at a position corresponding to the left half of the gate electrode  13 . An insulating layer is then formed as a protective layer, and the required wiring formed and connections made to each electrode  
         [0061]    The substrate  11  the same as in the first embodiment, may be comprised not only by Mn x Ge 1−x , but by any materials capable of switching the magnetic—nonmagnetic states by typical carrier doping.  
         [0062]    Fifth Embodiment  
         [0063]    The basic structure and operating principle of the electrically-driven MRAM using the field effect spin-controlled device as described for the fourth embodiment is described next while referring to FIG. 7. Sections in FIG. 7 identical to FIG. 5 are assigned the same reference numerals. After forming the structure shown in FIG. 5, a nonvolatile memory unit  500  is formed on the side opposite the side of substrate  11  where the gate electrode  13  is formed. The nonvolatile memory unit  500  position corresponds to the position of the right half of the gate electrode  13  matching the region formed by the freely magnetized layer of substrate  11 . This nonvolatile memory unit  500  is a CPP-GMR memory cell utilizing laminated films comprised from the substrate  11  side, of a nonmagnetic layer  51 , a ferromagnetic metal layer  52  (freely magnetized layer)/nonmagnetic metal layer  53 /ferromagnetic metal layer  54  (fixed magnetized layer). This nonvolatile memory unit  500  may also be a TMR memory cell utilizing laminated films comprised of a nonmagnetic layer  51 , a ferromagnetic metal layer  52  (freely magnetized layer)/nonmagnetic metal layer  53 /ferromagnetic metal layer  54  (fixed magnetized layer). The ferromagnetic metal layer  54  has a sufficient thickness versus the ferromagnetic metal layer  52  and so the ferromagnetic metal layer  54  functions as a fixed magnetized layer. The external electrodes  15  and  55  are formed to detect the storage information of the nonvolatile memory unit  500 . Even when the gate voltage is off (Vg=0), the nonvolatile memory unit  500  retains the magnetic recording information formed on the freely magnetized layer of the substrate  11 .  
         [0064]    The write operation (program mode) on the field effect MRAM cell of the fifth embodiment, applies a gate voltage Vg corresponding to the magnetic exchange interaction J&gt;0 to the gate electrode  13 , or applies a gate voltage Vg to the gate electrode  13  corresponding to the magnetic exchange interaction J&lt;0 as the data for storage. The magnetization direction (position where nonvolatile memory unit  500  is installed) of the second ferromagnetic region of the substrate  11  is consequently parallel or antiparallel to the magnetization direction at the position where the antiferromagnetic layer  34  is formed within the substrate  11 . The magnetization direction of the second ferromagnetic region of the substrate  11  is transferred by way of the magnetic coupling force of the nonmagnetic layer  51  to the ferromagnetic metal layer  52  which is a freely magnetized layer of the nonvolatile memory unit  500 . Writing on the GMR or the TMR memory cell is performed in this way.  
         [0065]    In the read-out operation (read mode), the gate voltage Vg applied to the gate electrode  13  is off. The substrate  11  is therefore in a nonmagnetic state at this time; however the magnetic recording information (magnetized direction) formed on the substrate by the gate voltage Vg, is still retained in the nonvolatile memory unit  500 . Here, sensing current flowing across the electrode  15  and electrode  55 , allows performing read-out by detecting the 0 and 1 record (write) bits from changes in the resistance across the electrodes  15 - 55  the same as in a typical MRAM device.  
         [0066]    An overview of the process for fabricating the electrically driven MRAM cell of the fifth embodiment is described next. Here also, the electrically driven MRAM cell is fabricated by a process identical to that in the first embodiment for manufacturing MOS-FET devices.  
         [0067]    The structure shown in FIG. 5 is fabricated using the process for manufacturing the field effect spin-controlled device of the fourth embodiment. In this case, the external electrode  15  is formed along with the forming of the electrode  14 . Next, the nonmagnetic layer  51  (Cu: copper) is formed to a thickness of two nanometers at a position on the substrate  11  where there is no antiferromagnetic layer  34 . A laminated structure made up of the freely magnetized layer  52  (CoFe:  661 alloy of cobalt and iron) in a thickness of five nanometers, a nonmagnetic metal layer  53  (Al 2 O 3 ) in a thickness of two nanometers, a fixed magnetic layer  54  (CoFe) in a thickness of 10 nanometers and further an electrode  55  (gold) are formed as the TMR device memory cell of the related art. An insulating layer is then formed as a protective layer, and the required wiring formed and connections made to each electrode.  
         [0068]    Writing is performed by setting the gate voltage to on and changing the Vg from 3 volts to a Vg of 5 volts and inverting the magnetic direction of the freely magnetized layer  506  that is the magnetic recording (write) unit. Read is performed by setting the gate voltage to off (Vg=0 volts) and fixing the magnetic direction of the write bit  0  (equivalent to a low resistance value) and 1 bit (equivalent to high resistance value) by detecting the resistance value across the electrode  505  through  509 . The resistance value can also be detected by utilizing a CMOS transistor to select the memory cell position the same as with the MRAM of the related art.  
         [0069]    The size of the TMR device memory cell can be made to approximately 100 by 100 nanometers, attaining a highly integrated memory device. A GMR memory cell of the related art may be utilized instead of this TMR memory cell.  
         [0070]    [0070]FIG. 8 is a diagram showing the circuit configuration of the fixed memory when the electrically-driven MRAM cells shown in FIG. 7 are arrayed in a 2-row vertical and 2-row horizontal X-Y matrix. To write data on the electrically-driven MRAM cells, two types of voltages must be selected according to the data and then applied across the gate electrode  13  and electrode  14 . To read data, a voltage applied across the electrode  15  and the electrode  55  must be applied and the current flow then detected. Since the write power supply and the read power supply should be separate, two word lines  82   11 ,  82   12  and  82   21 ,  82   22  are provided for each cell as clearly shown by referring to FIG. 7. These word line pairs are selected are each simultaneously selected by the word decoder  88 . The word decoder  88  is connected by the switches  81   11 ,  81   12  and  81   21 ,  81   22  to the separate wires  86   1 ,  86   2 . Two bit lines are connected to each electrically-driven MRAM cell. In other words, the MRAM cells are connected to the bit lines  80   11 ,  80   12  and  80   21 ,  80   22 . Besides the switches  83   11  and  83   21  connecting to the bit lines  80   11  and  80   21 , bit lines also respectively connect to the parallel circuit formed by the switches  84   11  and  84   12  as well as the parallel circuit formed by the switches  84   12  and  84   22 . The power supply lines  85   1 ,  85   2  respectively connect to other end of the switches  84   11  and  84   21 , and the other end of the switches  84   12  and  84   22 . The voltages of the power supply lines  85   1 ,  85   2 , are 3 volts, 5 volts on the line  86   2  according to the characteristics of FIG. 6. Along with the switches  83   12  and  83   22  connected to the bit lines  80   12 ,  80   22 , the data line  85   3  connects to the other end of the switches  83   12  and  83   22 . This data line  85   3  is set to a readout voltage by the line  86   1 . The bit lines are respectively selected by the write bit decoder  87   1  and the read-out bit decoder  87   2 . However when the switches  83   11  and  83   21  are turned on by the write bit decoder  87   1 , either the switches  84   11  and  84   12 , and either or the switches  84   12  and  84   21  simultaneously turns on according to the write data.  
         [0071]    The electrically-driven MRAM cell is positioned at the cross point of the word line and bit line as shown in FIG. 7. To avoid complexity, reference numerals are only assigned to the electrodes  13 ,  14 ,  15  and  55  for one cell, and the others are omitted. The electrodes  14  and  15  are shown in a shape protruding from the other layers to make the wiring easy to view. The electrode  55  of the electrically-driven MRAM cell is connected to the first word lines  82   11  and  82   12 . The gate electrode  14  of the electrically-driven MRAM cell is connected to second word lines  82   12  and  82   22 . The gate electrode  13  of the electrically-driven MRAM cell is connected to the first bit lines  80   11  and  80   21 . The gate electrode  15  of the electrically-driven MRAM cell is connected to the second bit lines  80   12  and  80   22 .  
         [0072]    Read and write can in this way be performed on the cell selected by the decoder.  
         [0073]    [0073]FIG. 9 is a drawing showing an example of one solid-state memory device mounted on the silicon substrate wherein the electrically-driven MRAM cells shown in FIG. 8 are arrayed in a 2-row vertical and 2-row horizontal X-Y matrix.  
         [0074]    A bottom layer is formed uniformly over the surface of the silicon substrate  230 . Patterning in a direction parallel to the paper surface is then performed for the second word line  210  (word line shown in FIG. 8 by reference numerals  82   12  and  82   22 ) according to the specified density of the memory device array. The electrically-driven MRAM cells shown in FIG. 8 are next sequentially laminated and a detailed description is omitted. In this process, the first bit line  207  connecting to the gate electrode  13  (bit line shown by reference numeral  80   11  in FIG. 8) is patterned in a direction perpendicular to the paper surface. Next, besides connecting the source electrode  14  to the second word line  210 , the second bit line  208  connecting to the drain electrode  15  (bit line shown by the reference numeral  80   12  in FIG. 8) is patterned in a direction perpendicular to the paper surface. The first word line  209  connecting to the electrode  55  is patterned in a direction perpendicular to the paper surface (word line shown in FIG. 8 by reference numerals  82   11  and  82   21 ). Each line and each element are covered by an insulating film  215  between layers.  
         [0075]    The MRAM of the related art has the unavoidable problem of large power consumption as the memory cells become more miniaturized, caused by the electrical current flowing along the wiring layer to write on the miniaturized memory cells. However, the electrically-driven MRAM cell of the present invention performs writing by selecting a gate voltage Vg so an electrically-driven MRAM cell with low power consumption can be fabricated. There is also no increase in power consumption as the cells become more miniaturized so the present invention is also ideal for large capacity MRAM.  
         [0076]    Other Embodiments  
         [0077]    [0077]FIG. 10 is across sectional view showing another FET structure of the gate electrode  13  in the field effect magnetoresistance device of the first embodiment shown in FIG. 1A. An electrical insulating layer  12  whose structure is patterned in a convex shape is formed on the upper part of the nonmagnetic substrate  11  capable of being doped with electric field carriers. A first metallic electrode (gate electrode)  13  is formed on the insulating (film) layer  12 . The other embodiments are the same as the first embodiment with the exception that the gate electrode  13  is divided into  13   1  and  13   2 . An external section applies a positive voltage of Vg&gt;0 to the gate electrode  13  from the power supply  17 . A strong electrical field is applied locally to the substrate directly below the region below the gate electrodes  13   1  and  13   2 . This region can be doped with a high concentration of hole carriers (forms a doped region with high carrier concentration). On the other hand, the substrate directly below the substrate  11  in sections where there are no gate electrodes  13   1  and  13   2  is indirectly affected only by a weak electrical field and that portion of the substrate can be doped with a low concentration of hole carriers (forms a doped region with a low carrier concentration).  
         [0078]    The nonmagnetic substrate  11  shown for the field effect magnetoresistance device of the first embodiment can therefore be formed with the junction structure of the ferromagnetic domain/nonmagnetic domain/ferromagnetic domain patterned in a flat shape shown in FIG. 1B. This magnetoresistance device possesses substantially the same characteristics of the field effect magnetoresistance device of the first embodiment.  
         [0079]    The field effect magnetoresistance device of the present invention outputs a sufficiently strong output signal with an MR ratio larger than the TMR device of the related art and so can therefore be used with different types of magnetic sensors and read/write heads of high density magnetic recording media. A field effect spin-controlled device is also provided that performs magnetic reversal with low electrical power consumption. By utilizing this electrically-driven magnetic reversal technology, the present invention can provide an electrically-driven MRAM with a large storage capacity and low power consumption.