Abstract:
This invention relates to a process of making high stretch elastic knitted fabrics from polytrimethylene terephthalate (PTT) which comprises:  
     (a) making a drawn textured yarn with an elongation to break of 30 to 60 percent by combining the steps of:  
     (i) spinning a polytrimethylene terephthalate polymer into a partially oriented yarn, and  
     (ii) draw texturing the yarn in a false-twisting texturing machine at a draw ratio of 1.05 to 2.0, and a yarn temperature of 50 to 200° C. using a either a contact heater or a non-contact heater, and  
     (b) knitting the yarn into a fabric composed of intermeshing loops of the yarn wherein the stitch length is from 22 cm/100 stitches to 26 cm/100 stitches, and  
     (c) scouring the knitted fabric, and  
     (d) drying the fabric on a belt, and  
     (e) dyeing the knitted fabric at atmospheric pressure by dispersing a dye and the fabric in water and increasing the temperature, and  
     (f) finishing the dyed knitted fabric according to the following procedure:  
     (i) cooling the dyed knitted fabric, and  
     (ii) adding reduction agent(s) for scouring, and  
     (iii) cooling the dyed knitted fabric, and  
     (iv) washing the dyed knitted fabric, and  
     (v) adding a solution of 0.25 to 0.75 weight percent weak organic acid, and  
     (vi) heating the dyed knitted fabric, and  
     (vii) washing the dyed knitted fabric, and  
     (viii) removing the fabric, and  
     (g) drying the fabric on a belt.

Description:
FIELD OF THE INVENTION  
         [0001]    This invention relates to a process for producing high stretch and elastic knitted fabrics from polytrimethylene terephthalate fibers. More particularly, the invention relates to a combination of novel fabric constructions, and dyeing and finishing processes and conditions for producing such high stretch and elastic knitted fabrics.  
         BACKGROUND OF THE INVENTION  
         [0002]    Polytrimethylene terephthalate (PTT) fibers are being developed for textile applications. It would be desirable to produce high stretch and elastic knitted fabrics from PTT. The conventional fabric construction and dyeing and finishing processes and conditions used for polyethylene terephthalate (PET) fibers and yarns do not, if used for PTT, produce a high stretch and elastic fabric. We have found that entirely different and more stringent knitted fabric constructions and dyeing and finishing conditions and processes are required in order to achieve high stretch and elastic fabrics made from PTT fibers or yarns.  
         SUMMARY OF THE INVENTION  
         [0003]    This invention relates to a process of making high stretch elastic knitted fabrics from polytrimethylene terephthalate (PTT) which comprises:  
           [0004]    (a) making a drawn textured yarn with an elongation to break of 30 to 60, preferably 35 to 55, percent by combining the steps of:  
           [0005]    (i) spinning a polytrimethylene terephthalate polymer into a partially oriented yarn, and  
           [0006]    (ii) draw texturing the yarn in a false-twisting texturing machine at a draw ratio of 1.05 to 2.0, preferably 1.15 to 1.5, and a yarn temperature of 50° C. to 200° C., preferably 130° C. to 180° C., using either a contact heater or a non-contact heater, and  
           [0007]    (b) knitting the yarn into a fabric composed of intermeshing loops of the yarn wherein the stitch length is from 22 cm/100 stitches to 26 cm/100 stitches, and  
           [0008]    (c) scouring the knitted fabric according to the following procedure:  
           [0009]    (i) load the fabric into a dryer with water at 30 to 40° C. for 12 to 15 minutes, and  
           [0010]    (ii) add 0.5 to 1.5% on weight of fabric of spin finish remover, and  
           [0011]    (iii) raise the temperature to 100° C. at a rate of 1.0 to 2.5° C., and  
           [0012]    (iv) hold for 5 to 10 minutes, and  
           [0013]    (d) drying the fabric:  
           [0014]    (i) on a belt at a speed 13 to 23 meter/minute through a forced air oven at a temperature of 88 to 98° C. with a residence time of 52 to 62 seconds, or  
           [0015]    (ii) on a belt at a speed 13 to 23 meter/minute through a tenter frame forced air oven at a temperature of 135 to 145° C. with a residence time of 52 to 62 seconds, and  
           [0016]    (e) dyeing the knitted fabric at atmospheric pressure by dispersing a dye and the fabric in water and increasing the temperature according to the following procedure:  
           [0017]    (i) preheating the fabric to a temperature of from 25° C. to an upper limit of 44 to 54° C. by increasing the temperature at a rate of 1.0° C. to 2.5° C. per minute, and  
           [0018]    (ii) preheating the fabric to a temperature of from 44 to 54° C. to 55 to 65° C. by increasing the temperature at a rate of 1.0° C. to 2.5° C. per minute, and  
           [0019]    (iii) preheating the fabric to a temperature of from 55 to 65° C. to 105 to 115° C. by increasing the temperature at a rate of 1 to 2° C. per minute, and  
           [0020]    (iv) maintaining the dyeing solution at this temperature for from 30 to 50 minutes, and  
           [0021]    (f) finishing the dyed knitted fabric according to the following procedure:  
           [0022]    (i) cooling the dyed knitted fabric to 88 to 98° C. at a cooling rate of 1° C. to 2° C. per minute, and  
           [0023]    (ii) adding reduction agent(s) for scouring which is carried out for from 3 to 7 minutes, and  
           [0024]    (iii) cooling the dyed knitted fabric to 55 to 65° C. at a cooling rate of 1.0° C. to 2.5° C. per minute, and  
           [0025]    (iv) washing the dyed knitted fabric with room temperature water for from 10 to 20 minutes, and  
           [0026]    (v) adding a solution of 0.25 to 0.75 weight percent weak organic acid, and  
           [0027]    (vi) heating the dyed knitted fabric to 44 to 54° C. at a rate of 1.0 to 2.5° C. per minute and holding it at that temperature for from 5 to 15 minutes, and  
           [0028]    (vii) washing the dyed knitted fabric at 34 to 44° C. for 5 to 10 minutes, and  
           [0029]    (viii) removing the fabric, and  
           [0030]    (g) drying the fabric:  
           [0031]    (i) on a belt at a speed of 13 to 23 meter/minute through a forced air oven at a temperature of 88 to 98° C. with a residence time of 52 to 62 seconds, or  
           [0032]    (ii) drying the fabric on a belt at a speed of 13 to 23 meter/minute through a tenter frame forced air oven at a temperature of 135 to 145° C. with a residence time of 52 to 62 seconds.  
         DETAILED DESCRIPTION OF THE INVENTION  
         [0033]    It is important that the PTT yarn by draw textured in a false-twisting draw texturing machine at a draw ratio of 1.05 to 2.0, preferably 1.15 to 1.5, and a yarn temperature of 50 to 200° C.; preferably 130 to 180° C. if using either a contact heater or a non-contact heater. Further, it is important that the yarn be knitted into a fabric composed of intermeshing loops of the yarn wherein the stitch length is from 22 centimeters/100 stitches to 26 centimeters/100 stitches.  
           [0034]    PTT can be knitted and woven into many different fabric constructions. The possibilities for PTT yarns and fibers are virtually identical to other fibers such as polyester and nylon.  
           [0035]    PTT can be used as both the fill (weft) yarn and/or the warp yarn. Fabric properties will depend on weaving tensions and finishing conditions, and are beyond the scope of this manual.  
           [0036]    PTT can be used in knitting applications. Fabric properties will depend on knitting tension and stitch length, as well as finishing conditions. An example for an interlock fabric described below.  
           [0037]    While each fabric will have its own set of unique properties from the way it was made, PTT should be able to impart softness, bulk and/or good feel (soft touch). A balance will come from the particular construction, and from the way the fabric was finished. In general, some of the considerations are:  
           [0038]    The fabric should be constructed in such a way that it accounts for shrinkage of the PTT yarn. A PTT draw textured yarn (DTY) will have 40% of more shrinkage at 100° C. (stretch yarn) and 0-40% shrinkage for a set yarn. This shrinkage will occur when the fabric is finished or dyed, and must be accounted for in the construction. Desired attributes in a fabric may not be obtained when the shrinkage is not taken into account. For example, if there is a 40% shrinkage in a knit, and the knit is finished with no decrease in width, the fabric will be stiff and lifeless.  
           [0039]    If knitting and weaving tensions are excessively high, this will cause excessive shrinkage in the fabric. In some constructions, the yarns will lock onto themselves, making stretch impossible.  
           [0040]    Temperatures in excess of 140° C. should be used cautiously. While the exact temperature a fabric sees is dependent on the nascent temperature and the amount of time that the fabric sees that temperature, temperatures greater than 140° C. can cause permanent loss of properties in the PTT yarn which makes up the fabric.  
           [0041]    Dyeing temperatures should not exceed 140° C. In general, 110° C. is the most that is needed. PET blends with PTT may need somewhat higher temperatures.  
           [0042]    Care must be taken during the dyeing procedure not to excessively stretch the fabric. Jet dyers tend to give a less destructive drying cycle.  
           [0043]    The interlock construction is a good way to see the stretch and soft touch of PTT in a fabric. An interlock fabric was constructed using a 70/34 DTY. The DTY had about 44% boiling water shrinkage. Tenacity was 3.0 g/denier, and 35% elongation.  
           [0044]    Several different knitting machines were used. A 32 cut, a 28 cut, and a 24 cut. The 28 cut, with normal knitting tensions gave the softest of the fabrics. Special attention was given to the length that the needle penetrated the fabric. By increasing this (but not the stitch length), a softer (to the hand) fabric was obtained.  
           [0045]    There are very few knitting parameters (other than stitch length) which can be varied. Getting the correct DTY for the process will eventually determine the fabric properties.  
           [0046]    PTT uses disperse dyes like PET. The carriers necessary to get good dye penetration into PET are not necessary for PTT. Neither is excessive temperature and pressure.  
           [0047]    The dyeing rate of PTT will disperse dyes is very similar to that of PET, although the dyeing temperature of PTT is only 100° C. compared to 130-140° C. for PET.  
           [0048]    There are different sizes of dye molecules. The larger the molecule, the more energy is necessary to get the molecule to penetrate the fiber. Above, we have discussed conditions for a low energy dye. A medium energy or high energy dye may need an additional 10° C. to get better penetration into the PTT fiber.  
           [0049]    Disperse dyes are used at owf (on the weight of fabric) necessary to give good color shade. A temperature of 100-110° C. is recommended. Temperatures above 110° C. will not give more exhaustive dyeing. Higher temperature will also not give faster dye penetration. Two inflection points exist, one at 80° C., the other at 95° C.  
           [0050]    Dyeing can be started at ambient temperature and raised to the dyeing temperature at a rate of 3° C./min and hold at the dyeing temperature for 20-40 minutes. After dyeing, the fabrics are rinsed until no further dye bleeds from the fabric. Reduction scouring can be important (see below), especially for dyes whose interaction with PTT is unknown.  
           [0051]    A pH of 7 can be used for all disperse dyes. If pH adjustment due to dye stability at a different pH, then the following chemicals can be used to adjust pHs:  
           [0052]    acetic acid/sodium acetate for the acidic pHs  
           [0053]    sodium carbonate/sodium bicarbonate for the weak alkaline solutions  
           [0054]    sodium hydroxide for pHs above 11.  
           [0055]    The recommended temperature profile is 5-10° C./min when temperatures are below 70° C.; 3-5° C./min for temperatures between 70-80° C.; and 1-2° C./min from 80-100° C. (low energy dye) and 80-110° C. (medium to high energy dye).  
           [0056]    The recommended dyeing temperature for PTT with low energy disperse dyes is 100° C., and 110° C. with medium and high energy disperse dyes. Temperatures below 100° C. will result in less dye exhaustion; temperature above 110° C. will not increase the dye exhaustion. There were two temperature ranges which affected the equilibrium dye sorption considerably. They are 70-80° C., and 95-100° C. Below 60° C., there is little dye sorption.  
           [0057]    The recommended dyeing pH for PTT with disperse dyes is 7. Due to the stability of most disperse dyes in a broad pH range, e.g., from 4 to 9, no pH adjustment is required for PTT dyeing. Even those with poor pH stability under high temperature dyeing conditions require no pH adjustment. This is due to the low temperature dyeability of PTT. Therefore, the pH stability of the disperse dyes is considerably increased. It is, however, often desirable for dye and or fabric properties to alter the pH. This can be done as above under control of pH.  
           [0058]    Possible auxiliary chemicals include the following:  
           [0059]    dispersant  
           [0060]    lubricant  
           [0061]    chelating agent  
           [0062]    defoamer/deaerator  
           [0063]    leveling agent  
           [0064]    The use of these chemicals depends on the dyeing machines, the quality of water being used, the dye properties, and the end-product requirement. Use only if they are necessary.  
           [0065]    The color fastness to laundering of a PTT fabric can be greatly affected by reduction scouring, as shown below. In general, reduction scouring represents a safety step to make sure that dye is not bled to other fabrics and fibers. Work has been done to assure that the lower dyeing temperature of PTT does not mean “easy in-easy out.” However, many dyes will exhibit different solubility and equilibrium behavior at 100° C. vs. 130° C. The reduction scour represents a good way to insure that small particles of dye are not left adhering to the surface of the PTT fibers.  
           [0066]    Chemical commonly used for reduction scour include:  
           [0067]    Caustic (sodium hydroxide) and hydro (sodium hydrosulfite) or  
           [0068]    Soda ash (sodium carbonate) and Thiox (formamidine sulfinic acid)  
           [0069]    The negative attribute of reduction scouring is that some reduction in color intensity can be seen.  
           [0070]    Laundering Fastness of a Black Woven Fabric Before Reduction Scouring  
                                                             Color Stain on #10 Multifiber*            Color Change   Acetate   Cotton   Nylon   Polyester   Acrylic   Wool               4-5   3   5   2-3   4-5   5   4                          
 
           [0071]    [0071]                                                             Color Stain on #10 Multifiber*            Color Change   Acetate   Cotton   Nylon   Polyester   Acrylic   Wool               5   4   5   4   5   5   5                                                            
           [0072]    Pre-scour before dyeing may be considered if the fabric is not pretreated. The choice of chemicals used depends on how aggressively the fabric (or fabrics) will be cleaned. A good general purpose cleaner would be 0.5% Actisol. A more aggressive choice would be 0.05% Jeffsol (propylene carbonate).  
           [0073]    The following dyeing and finishing procedure is a sample dyeing procedure used for an interlock stretch fabric. The dyer used was a “tube” or “cigar” type jet dryer. All % and weights based on owf.  
           [0074]    Step Action  
           [0075]    1 Fill dyer with water at 38° C.  
           [0076]    2 Load fabric into dyer  
           [0077]    3 Add 0.5% Actisol (to wash fabric)  
           [0078]    4 Run dyer for 20 minutes  
           [0079]    5 Wash with water in dyer for 15 minutes  
           [0080]    6 Heat to 49° C. at 1.7 degrees per minute  
           [0081]    7 Add dye bath chemicals. This would include 1% of a buffer (to maintain pH 7) and 3% Dyol 2447 (Boehme-Filatex) leveling/disperse agent. (Approximately 5 minutes)  
           [0082]    8 Add dyes by backwashing dyes into dyer. In this case, 0.092% Foron Blue S-BGL, 0.004% Foron Red RD-BR, and 0.06% Intrasin Orange 2 GR was used. (Approximately 5 minutes)  
           [0083]    9 Heat to 60° C. at 1.7 degrees per minute  
           [0084]    10 Heat to 110° C. at 1 degree per minute  
           [0085]    11 Run at 110° C. for 40 minutes  
           [0086]    12 Cool to 82° C. at 1 degree per minute  
           [0087]    13 Add chemicals for reduction scour. These were 2% soda ash (sodium carbonate), 1% Thiox (foramidine sulfinic acid).  
           [0088]    14 Run at 82° C. for 5 minutes  
           [0089]    15 Cool to 60° C. at 1.7 degrees per minute  
           [0090]    16 Wash for 15 minutes. Wash clear.  
           [0091]    17 Add 0.5% acetic acid  
           [0092]    18 Heat to 50° C. at 1.7 degrees per minute  
           [0093]    19 Run at 50° C. for 10 minutes  
           [0094]    20 Wash at 38° C. for 10 minutes  
           [0095]    21 Unload the fabric  
       
    
    
     EXAMPLES  
     Example 1  
       [0096]    A 32 gauge fabric, interlock knit, with about 8 oz. fabric weight were dyed, using the conditions below. Stretch was lost during the dyeing step at 110° C. The fabric was split into two parts to compare the two procedures, with about ½ the fabric from each style on each procedure.  
         [0097]    1. Procedure 1 and 2. Scour. The fabric was loaded into the Future jet dryer. A cold water wash (35° C., about 95° F.) was done for 10-15 minutes to remove most of the spin finish. The water was flushed, 1% owf Milease T was added to help scouring and lubrication, and the temperature profile ramped to 212° F. (100° C.). The temperature was held at 212° F. (100° C.) for ten minutes, then cooled back down to room temperature. The heating and cooling steps each took about 20 minutes. See detailed procedure below.  
         [0098]    2. Procedure 1 and 2. Dyeing. The fabric was dyed at 110° C. (230° F.) in a jet dyer (Futura, Gaston County) machine. (Same machine as used for scouring). See detailed procedure below.  
         [0099]    3. Procedure 1 and 2. Dry. The fabric was dried on a belt, forced air oven. A temperature of 200° F. (about 93° C.) was used, and the machine speed was 18 yards (16.5 meters) per minute.  
         [0100]    4. Procedure 1 and 2. The fabric was run through a tenter frame, with a heat set of 140° C. (284° F.) at 18 yards per minutes.  
                                                         Actual scouring    1. Fill at 100° F. (37.8° C.)       procedure    2. Load at 100° F. (37.8° C.)            3. Wash at 100° F. (37.8° C.) for 15 minutes            4. Add chemical scouring agent, 1 Milease T            5. Heat to 212° F. (100° C.) at 3° F. (1.7° C.) per           minute            6. Run at 212° F. (100° C.) for 10 minutes       Actual dyeing    1. Load fabric       procedure    2. Wash at 100° F. (37.8° C.) for 10 minutes            3. Heat to 120° F. (66.7° C.), at 3° F. (1.7° C.)/minute            4. Add dye to bath at 120° F. (66.7° C.)            5. Add dyes at 120° F. (66.7° C.) in two parts.           Back wash slowly.            6. Heat to 140° F. (60° C.) at 3° F. (1.7° C.) per           minute            7. Heat to 230° F. (110° C.) at 2° F. (1.1° C.) per           minute            8. Run at 230° F. (110° C.) for 40 minutes            9. Cool to 180° F. (82° C.) at 2° F. (1.1° C.) per minute           10. No sample           11. Add after clear-Soda ash and Thiox           12. Run at 180° F. (82° C.) for 5 minutes           13. Cool at 140° F. (60° C.) at 3° F. (1.7° C.) per minute           14. Wash clear, and neutralize           15. Add acetic acid, ½%           16. Heat to 120° F. (66.7° C.) at 3° F. (1.7° C.) per           minute           17. Run at 120° F. (66.7° C.) for 10 minutes           18. Wash at 100° F. (37.8° C.) for 10 minutes until clear           19. Unload       Dye   The dye was composed of the following:           1.00% Lydcol-Rdn Liq, -Lubrication, leveling           agent, and dispersing aid           0.25% Hydroquest 444-chelating agent (like           EDTA)           1.00% Buffer pH-7           6.00% Foron Black S-K Paste           1.20% Sodyecron Navy AR 100%           0.50% Intrasil Orange 2 GR           All 3 medium to high energy dyes           After dyeing, step 11 above adds 2.0% soda ash and           1.0% Thiox (foramidine sulfinic acid reducing agent).           To clear this up, step 15 uses 0.5% acetic acid.           All percentages are owf            Results on   Fabric   Width before   Width after       scouring       scour   scour           From M-700*   68.5″   51.5-52.5″               (1.74 m)   (1.31-1.33 m)           From AFK*   68.5-71″   47.75               (1.74 m-1.80 m)%                          
 
         [0101]    [0101]                                                                   TABLE 1                           Dyeing/Finishing Procedure 1 Fabrics                        Style   Width           Yarn   Lot   Piece   Number   After       I.D.   Number   Number   Pounds   Dyeing   Comments                    A   L11   P1   19.9   36.1″   Stretch &amp; power                       (1.0 m)           L12       20.6       Stretch &amp; power       B   L13   P2   22.0   49.1″   Poor power                       (1.36 m)           L14       27.7       Not tested       C   L15   P3   19.8   43.35″   Stretch &amp; power                       (1.20 m)           L16       18.9       Not tested           L17       6.1       Not tested       D   L18   P4   21.5   51.22″   Not tested                       (1.42 m)           L19       22       Stretch &amp; power                    
         [0102]    [0102]                                             TABLE 2                           Dyeing/Finishing Procedure 2 Fabrics                                Width           Yarn   Lot   Piece   Style   Fabric   After       I.D.   Number   Number   Number   Weight   Dyeing   Comments               A   L21   P1   S1   43.5 lb   52″   Poor                       (20.0 kg)   (1.44 m)   stretch           L22           10.0 lb   52″   Stretch                       (4.5 kg)   (1.44 m)   and power       B   L23   P2   S2   43.5 lb   52″   Poor                       (20.0 kg)   (1.44 m)   power       C   L24   P3   S3   19.7 lb   47″   Stretch &amp;                       (8.96 kg)   (1.31 m)   power           L25           20.8 lb   47″   Poor                       (9.46 kg)   (1.31 m)   power       D   L26   P4   S4   21.9 lb   47″   Stretch &amp;                       (9.96 kg)   (1.31 m)   power           L27           20.9 lb   47″   Poor                       (9.5 kg)   (1.31 m)   power                                    
         [0103]    [0103]                           TABLE 3                       Lot   Fabric   Fabric           number   Stretch,* %   Recovery,** %   Comments                   L23   100   60   No power       LiS   100   75   Stretch &amp; power       L19   110   75   Str. &amp; pwr.       L13   100   60   Seems to pull out       L11    95   80   Str. &amp; pwr.       L27   120   50   No power       L24   100   70   Str. &amp; pwr       L21    80   70   Poor stretch       L22   100   90   Greige***, scoured, heat set       L26   120   85   Greige, scoured, heat set       Unknown   130   100    Greige, scoured, not heat set                                            
         [0104]    As indicated in the column of comments of Table 3 fabrics with lot numbers, L15, L19, L11 and L24 has both good (high) stretch and high recovery after stretch.  
         [0105]    A Monarch LIL Size 30 (30 inches [0.83 m] diameter) Circular Interlock Knitting Machine was used. This is a 84 feed machine, run at 24 rpm. It is Contempora machine #25. It is a 32 cut (32 gauge, i.e., 32 needles per inch [12.6 per cm]) machine, and it uses 3096 needles. (Calculated would be 3016 needles).  
         [0106]    The following draw-textured yarns were made for the different fabrics for the studies of stretch and recovery in this application.  
                                       TABLE 4                                   Lot Number   A   B   C   D                           Denier, g   77.47   85.8   79.67   86.0           Tenacity, g/d   2.75   2.39   2.88           Elongation, %   36.1   49.2   43.25   51.0           Skein   46.1   41.6   44.59           Shrinkage,* %           Machine   M-700   M-700   AFK   AFK           Speed (M/m)   500   275   450   425           Draw Ratio   1.367   1.23   1.3365   1.23           Discs lay-out   1-6-1   1-5-1   1-3-1   1-3-1           Disc   6 mm   6 mm   9 mm   9 mm           thickness   Kyocera   Kyocera   Kyocera   Kyocera           material           Spacing, mm   0.5   0.5   0.5   0.5           D/y ratio   2.49   2.35   2.10   2.10           Heater Temp   160   160   220/220   220/220           (° C.)           Tube Color   Black   Blue   Red   Green                                              
 
         [0107]    [0107]                                                                                             TABLE 5                               Calcu&#39;d*                                       Fabric   stitch   Greige                   Boil off           length   length,   fabric   Greige   Greige   Boil off   Boil off   fabric           feed,   cm/100   width,   fabric %   fabric %   fabric %   fabric %   width,       Run #   meters   stitch   cm   stretch   recovery   stretch   recovery   cm   Remark                                1   8.69   25.65       60   98   61   96       No power       2   7.94   23.45       60   97   60   98   81.3   stretch &amp;                                       pwr       3   7.29   21.52       40   90   32   97   79.4   poor str.       4**   3.125   24.64   90.2   60   98   62   98   81.9   str. &amp; pwr.       5**   8.125   24.64   87.0   68   97   63   97   82.6   str. &amp; pwr.       6   7.11   21   87.0   50   100   42   99   75.6   poor str.       7   7.85   23.17   88.3   75   95   66   97   75.6   str. &amp;                                       pwr.       8   8.59   25.38   88.3   85   98   70   98   78.1   str. &amp; pwr.       9**   8.125   24.64   87.0   70   99   70   98   74.6   str. &amp; pwr.       10**   8.125   24.64   87.0   78   100   82   100   75.3   str. &amp; pwr.                                    
         [0108]    Conclusion: As indicated in Table 5, to obtain good stretch and power, the stitch length should be from 23 to 25.5 cm/100 stitches in order to obtain power and good stretch (% stretch≧60% and % recovery≧97%)