Abstract:
Provided is a solid oxide fuel cell having a service life of approximately 90,000 hours, a level required to encourage the widespread use of SOFC. The solid oxide fuel cell according to the present invention comprises a solid electrolyte layer, an oxygen electrode layer provide to one side of the solid electrolyte layer, and a fuel electrode layer provide to the other side of the solid electrolyte layer. The oxygen electrode layer is made from a material including iron or manganese, the solid electrolyte layer is made from a scandia-stabilized zirconia electrolyte material containing alumina, and the solid electrolyte layer has a lanthanoid oxide and/or yttria dissolved therein.

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to a solid oxide fuel cell. 
       BACKGROUND ART 
       [0002]    Conventionally, solid electrolyte materials such as scandia doped zirconia (hereinafter, referred to as ScSZ) have been used in the applications of solid oxide fuel cells (hereinafter, abbreviated as SOFCs) and the like. SOFCs have higher electric power generation efficiencies and higher discharged thermal energy temperatures than other fuel cells, such as phosphoric acid-type fuel cells and molten carbonate-type fuel cells. Hence, SOFCs have attracted attention as a next-generation type energy-saving electric power generation system. 
         [0003]    A basic structure of an SOFC includes a solid electrolyte layer, a fuel electrode layer, and an oxygen electrode layer. When a fuel gas such as hydrogen (H 2 ) flows through and thereby comes into contact with the fuel electrode layer, which faces one surface of the solid electrolyte layer, and an oxidizing agent gas such as the air or oxygen (O 2 ) flows through and thereby comes into contact with the oxygen electrode layer, which faces an opposite surface of the solid electrolyte layer, oxygen ions (O 2− ) generated in the oxygen electrode layer move through the solid electrolyte layer to the fuel electrode layer, and the O 2−  react with H 2  in the fuel electrode layer. An electric output can be obtained by this electrochemical reaction. 
         [0004]    A solid electrolyte material for an SOFC based on such a reaction mechanism needs to have the following characteristics: (1) high oxygen ion conductivity; (2) excellent long-term durability; (3) high material strength; and the like. Among zirconia-based solid electrolyte materials, the most preferred material is ScSZ. 
         [0005]    As the oxygen electrode layer of an SOFC, strontium doped lanthanum manganite (hereinafter, referred to as LSM), strontium doped lanthanum ferrite (hereinafter, referred to as LSF), and strontium and iron doped lanthanum cobaltite (hereinafter, referred to as LSCF) are generally used. A cell is exposed to a high temperature during the production of the oxygen electrode layer by the sintering method using any of these materials and during the operation of the cell. Hence, manganese (Mn) in the case of LSM or iron (Fe) in the cases of LSF and LSCF diffuses to ScSZ, which is the solid electrolyte layer, and lowers the oxygen ion conductivity. To suppress the diffusion, a solid electrolyte layer of ScSZ containing alumina has been proposed (see Japanese Patent Application Publication No. Hei 8-250135). 
       SUMMARY OF THE INVENTION 
       [0006]    The inclusion of alumina in ScSZ makes it possible to suppress the doping and diffusion of Mn or Fe from the oxygen electrode to the inside of the ScSZ. However, the Mn doping and the Fe doping cannot be completely zero, and the ScSZ is doped with Mn or Fe and Mn or Fe is diffused near the interface of the ScSZ with the fuel electrode layer, although the amount is trace. 
         [0007]    A long-term durability test conducted for several hundred to several thousand hours on an SOFC using LSM as the oxygen electrode layer and having ScSZ as the solid electrolyte layer showed that powder formation in a portion of the solid electrolyte layer occurred near the fuel electrode. As a result of various examinations, it was found that Mn diffused to the ScSZ doped with Mn was extracted from the ScSZ upon exposure to a reducing atmosphere, and it was revealed that a stabilizer, scandia, was also extracted from crystals at the same time, so that crystal transformation (change from cubic crystals to tetragonal crystals) of the solid electrolyte layer occurred. 
         [0008]    It is conceivable that the Mn doping diffused near the interface with the fuel electrode varies depending on the atmosphere, and that when the SOFC is exposed to a reducing atmosphere, part of the Mn doped is extracted from the ScSZ to the fuel electrode side. Presumably, the same phenomenon as that of Mn occurs in the case of Fe. 
         [0009]    In the long-term durability test conducted for several thousand hours, no powder formation was observed in a portion of the solid electrolyte layer covered with the fuel electrode layer, but crystal transformation occurred in this portion as in the portion where the powder formation occurred. Hence, presumably, powder formation will occur during operation for several tens of thousands hours, and peeling (hereinafter, referred to as powder formation peeling) will occur between the solid electrolyte layer and the fuel electrode layer. If the powder formation peeling occurs, electricity cannot be extracted, and electric power generation is impossible. An SOFC is required to have a lifetime of about 40000 hours in the introduction period, and of about 90000 hours in the spread period. The powder formation peeling shown here is a technical problem which should be solved for introduction to the market. 
         [0010]    Results of a SEM observation on the powder formation portion showed that particles fell off at grain boundaries, so that the powder formation occurred. This is presumably because the change from the cubic crystals to the tetragonal crystals caused decrease in volume, so that fracture occurred at the grain boundaries (see  FIG. 1 ). 
         [0011]    The present inventors provide an SOFC comprising a solid electrolyte layer having an improved strength between particles, in order that, in an SOFC comprising a solid electrolyte layer of ScSZ to which Mn or Fe is diffused from an oxygen electrode layer, the extraction of the stabilizer, scandia, from the crystals caused at the time that Mn or Fe diffused to the ScSZ doped with Mn or Fe is extracted from the ScSZ upon exposure to a reducing atmosphere can be suppressed, and no intergranular fracture associated with the crystal transformation can be allowed even if the crystal transformation occurs. 
         [0012]    To solve the above-described problem, an SOFC according to the present invention is a solid oxide fuel cell comprising: a solid electrolyte layer; an oxygen electrode layer provided on one surface of the solid electrolyte layer; and a fuel electrode layer provided on the other surface of the solid electrolyte layer, wherein the oxygen electrode layer is made of a material containing iron or manganese, the solid electrolyte layer is made of an ScSZ electrolyte material containing alumina, and doped with a lanthanoid oxide and/or yttria. Since the alumina is contained in the ScSZ, the Mn or Fe doping diffused to the inside of ScSZ is reduced. Hence, the amount of the stabilizer, scandia, simultaneously extracted from crystals at the extraction of Mn or Fe from the ScSZ is also reduced. However, since the Mn doping and the Fe doping cannot be reduced to 0 by this alone, the phenomenon in which a trace amount of Mn or Fe is extracted from the ScSZ cannot be eliminated. In this respect, the present invention makes it possible to suppress, even if Mn or Fe is extracted from the ScSZ, the phenomenon itself in which scandia is extracted from the ScSZ by the ScSZ containing alumina and also doped with a lanthanoid oxide and/or yttria. Furthermore, since the alumina is present at grain boundaries of ScSZ particles, and firmly connects the ScSZ particles to each other, the alumina also achieves an effect of suppressing the fracture at grain boundaries, even when the slight volume change associated with the crystal transformation occurs. As a result, no powder formation occurs. Hence, it is possible to provide an SOFC having a lifetime of 90000 hours, which is required in the spread period. In a further preferred mode, the lanthanoid oxide and/or the yttria doping at the fuel electrode side of the solid electrolyte layer is higher than the lanthanoid oxide and/or the yttria doping at the oxygen electrode side of the solid electrolyte layer. Examples thereof include one in which the lanthanoid oxide doping gradually decreases from the fuel electrode side to the oxygen electrode side, and the like. This makes it possible to minimize the decrease in oxygen ion conductivity of the solid oxide layer as a whole, while preventing the powder formation peeling on the fuel electrode layer side. 
         [0013]    In a preferred mode of the present invention, the zirconia is doped with 9 to 15 mol %, and more preferably 9 to 11 mol % of the scandia, and 2 to 5 mol %, and more preferably 3 to 5 mol % of the lanthanoid oxide and/or the yttria relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. In a further preferred mode of the present invention, the alumina is contained in an amount of more than 1 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. The amount of scandia is preferably 9 to 15 mol %, because an amount of less than 9 mol % may result in the formation of tetragonal crystals, and an amount exceeding 15 mol % may result in the formation of rhombohedral crystals, each of which lowers the oxygen ion conductivity. The lanthanoid oxide and/or the yttria doping is preferably 2 to 5 mol %, because an amount of less than 2 mol % results in a decreased effect of suppressing the extraction of scandia at the extraction of Mn or Fe from the ScSZ, and an amount exceeding 5 mol % increases the possibility of the crystal transformation, because of the formation of tetragonal crystals. The alumina is contained in an amount of more than 1 mol %, because an amount of 1 mol % or less results in a decreased effect of reducing the Mn doping or the Fe doping, and in a decreased effect of suppressing the intergranular fracture due to the volume change associated with the crystal transformation. In addition, the solid electrolyte material of the present invention preferably contains the alumina in an amount of 5 mol % or less. This is because an alumina amount of 5 mol % or less does not cause decrease in oxygen ion conductivity of the solid electrolyte material, or if some decrease is caused, the decrease can be minimized. 
         [0014]    In a preferred mode of the present invention, the lanthanoid oxide is ceria. Ceria is preferable because, not only the extraction of scandia can be suppressed at the extraction of Mn or Fe from the ScSZ, but also the oxygen ion conductivity of the solid electrolyte material can be improved. 
         [0015]    In a preferred mode of the present invention, the solid electrolyte layer consists of two layers of a first layer formed at the oxygen electrode layer side and a second layer formed at the fuel electrode layer side, the lanthanoid oxide and/or the yttria doping in the second layer is higher than the lanthanoid oxide and/or the yttria doping in the first layer, and the amount of the alumina in the second layer is higher than the amount of the alumina in the first layer. More preferably, the first layer is not doped with the lanthanoid oxide and/or the yttria, and the first layer does not contain the alumina. In addition, the first layer may use scandia stabilized zirconia or yttria stabilized zirconia. The SOFC comprising the solid electrolyte layer has a high efficiency, and a lifetime of 90000 hours, which is required in the spread period. This is because of the following reason. Specifically, in the second layer on the fuel electrode layer side, the powder formation peeling can be prevented, but the ion conductivity decreases because of the inclusion of alumina and the like. In contrast, in the first layer on the oxygen electrode layer side, the oxygen ion conductivity remains high, and the internal resistance remains small. Hence, the powder formation peeling can be prevented from occurring, while the decrease in oxygen ion conductivity of the solid oxide layer as a whole is minimized. 
         [0016]    In a preferred mode of the present invention, the first layer of the solid electrolyte layer is thicker than the second layer. An SOFC of the present invention comprising such a solid electrolyte layer has a high efficiency, and a lifetime of 90000 hours, which is required in the spread period. This is because, since the thickness of the second layer is minimum necessary for preventing the powder formation peeling, the contribution of the high oxygen ion conductivity of the first layer is increased, so that the electric power generation efficiency can be further increased. A minimum necessary thickness of the second layer for preventing the powder formation peeling is, for example, 1 μm or more, and preferably 3 μm or more. 
         [0017]    According to the present invention, a solid electrolyte layer having an improved strength between particles is provided in order that, in an SOFC comprising ScSZ to which Mn or Fe is diffused from an oxygen electrode layer, the extraction of the stabilizer, scandia, from the crystals caused at the time that Mn or Fe diffused to the ScSZ doped with Mn or Fe is extracted from the ScSZ upon exposure to a reducing atmosphere can be suppressed, and that even when the crystal transformation occurs, no intergranular fracture associated with the crystal transformation can be allowed. Hence, it is possible to suppress the powder formation associated with the crystal transformation of zirconia and the powder formation peeling which may occur several tens of thousands hours later between the fuel electrode layer and the solid electrolyte layer. Therefore, the present invention makes it possible to provide a solid oxide fuel cell which has a lifetime of about 90000 hours required in the spread period of SOFCs. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0018]      FIG. 1  is an SEM photograph showing a powder formation phenomenon of a solid electrolyte layer in the present invention. 
           [0019]      FIG. 2  is a diagram showing an example of an SOFC of the present invention. 
           [0020]      FIG. 3  is a diagram showing the difference in change associated with crystal transformation of a solid electrolyte layer between a conventional case and the present invention. 
           [0021]      FIG. 4  is a diagram showing the crystal state of ScSZ depending on the Sc 2 O 3  concentration and the temperature. 
           [0022]      FIG. 5  is a diagram showing a best mode of the SOFC of the present invention. 
           [0023]      FIG. 6  is a diagram showing a testing apparatus for demonstrating effects of the present invention. 
       
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0024]    Hereinafter, embodiments of the present invention will be described with reference to the drawings.  FIG. 2  is an SOFC of an embodiment of the present invention. An oxygen electrode layer  101  is provided on one surface of a solid electrolyte layer  102 , and a fuel electrode layer  103  is provided on the other surface of the solid electrolyte layer  102 . Conventionally, ScSZ has been used as the solid electrolyte layer, from the viewpoint of high oxygen ion conductivity. However, a long-term durability test conducted for several hundred to several thousand hours showed that, in an SOFC having a solid electrolyte layer of the above-described composition, the stabilizer, scandia, was extracted from the crystals when Mn or Fe diffused from the oxygen electrode layer was extracted from the ScSZ upon exposure to a reducing atmosphere, so that crystal transformation (change from cubic crystals to tetragonal crystals) of the solid electrolyte layer  102  occurred. In addition, powder formation was observed in an uncovered portion of the solid electrolyte layer  102 . Hence, presumably, the crystal transformation occurred also in a portion of the solid electrolyte layer  102  covered with the fuel electrode layer  103  in the same manner, and the powder formation peeling will occur between the solid electrolyte layer  102  and the fuel electrode layer  103  during operation for several tens of thousands hours. 
         [0025]    The difference in change associated with the crystal transformation of the solid electrolyte layer between Comparative Example and the present invention is described based on  FIG. 3 . A solid electrolyte layer which has a 10Sc1CeSZ composition corresponding to that of Comparative Example 1 doped with several mol percent of Mn has a cubic crystal structure  110  at the production thereof. When the solid electrolyte layer is exposed to a reducing atmosphere, Mn is extracted in the form of MnO or Mn(OH) 2 , and scandia (Sc 2 O 3 ) is extracted from the crystal phase. Consequently, the crystal phase changes from the cubic crystals (c)  110  to tetragonal crystals (t)  111 , as shown in the phase diagram of  FIG. 4 . The change from the cubic crystals (c)  110  to the tetragonal crystals (t)  111  results in decrease in lattice constants and decrease in volume. Presumably as a result of this, intergranular fracture occurs, and the powder formation as shown in the SEM image of  FIG. 1  occurs. In the solid electrolyte material of the SOFC of the present invention, it is preferable to prevent the powder formation from occurring by increasing the lanthanoid oxide and/or the yttria doping in order to suppress the extraction of scandia (Sc 2 O 3 ) from the crystal phase, and by further containing alumina  112  in order to reinforce the grain boundaries for prevention of the intergranular fracture even in a case where the crystal transformation occurs due to the extraction of scandia from the crystal phase. 
         [0026]    A preferred composition of the solid electrolyte layer is such that the scandia doping is 9 to 15 mol %, and the lanthanoid oxide and/or the yttria doping is 2 to 5 mol %, relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. A further preferred composition of the solid electrolyte material of the present invention is such that the more than 1 mol % of alumina is contained relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. The amount of scandia is preferably 9 to 15 mol %, because an amount of less than 9 mol % may result in the formation of tetragonal crystals, and an amount exceeding 15 mol % may result in the formation of rhombohedral crystals, which lower the oxygen ion conductivity. The lanthanoid oxide and/or the yttria doping is preferably 2 to 5 mol %, because an amount of less than 2 mol % results in a decreased effect of suppressing the extraction of scandia at the extraction of Mn or Fe from the ScSZ, and an amount exceeding 5 mol % increases the possibility of the crystal transformation because of the formation of tetragonal crystals. The alumina is contained in an amount of more than 1 mol %, because an amount of 1 mol % or less results in a decreased effect of suppressing the intergranular fracture due to the volume change associated with the crystal transformation. 
         [0027]    A major object of the solid electrolyte layer of the SOFC of the present invention is to prevent degradation at the extraction of Mn or Fe, which is diffused from the oxygen electrode layer, from ScSZ in a reducing atmosphere. From the viewpoints of increasing the efficiency and of a high durability of the SOFC, the solid electrolyte layer preferably comprises two layers of a first layer  107  formed at the oxygen electrode layer  101  side and having a high oxygen ion conductivity, and a second layer  108  formed at the fuel electrode layer side  103  and formed of a solid electrolyte material comprising ScSZ doped with a lanthanoid oxide and/or yttria, and having a composition further containing alumina (see  FIG. 5 ). From the viewpoint of increasing the efficiency, the first layer is more preferably thicker than the second layer. 
         [0028]    The fuel electrode layer  103  in the SOFC of the present invention only needs to satisfy the following requirements: having a high electrical conductivity, which enables an electric output to be obtained by an electrochemical reaction in which O 2−  react with H 2 ; being chemically stable; and having a coefficient of thermal expansion close to that of the solid electrolyte layer  102 . Conventionally used fuel electrode layers can be employed without any particular limitation. Typical examples thereof include a cermet of Ni and ScSZ, a cermet of Ni and yttria stabilized zirconia (hereinafter, referred to as YSZ), a cermet of Ni and cerium oxide, and the like. 
         [0029]    The oxygen electrode layer  101  in the SOFC of the present invention only needs to satisfy the following requirements: having a high electrical conductivity and having a high catalytic activity for converting an oxidizing agent gas such as oxygen (O 2 ) into oxygen ions (O 2− ); being chemically stable; and having a coefficient of thermal expansion close to that of the solid electrolyte layer  102 . Conventionally used oxygen electrode layers can be employed without any particular limitation. Examples thereof include strontium doped lanthanum manganite (hereinafter, referred to as LSM), strontium doped lanthanum ferrite (hereinafter, referred to as LSF), strontium and iron doped lanthanum cobaltite (hereinafter, referred to as LSCF), and the like. 
         [0030]    In the production of the solid electrolyte material used in the SOFC of the present invention, any method generally employed in this technical field may be used without any particular limitation. For example, the solid electrolyte material of the present invention can be produced as follows, although the method is not limited to this one. Specifically, particles of zirconia, particles of scandia, and particles of the lanthanoid oxide and/or particles of yttria are mixed with each other at a given blending ratio; the mixture is ground in a grinding machine such as a ball mill, and then sintered; the sintered material is ground in a grinding machine such as a ball mill; then the ground material is mixed with alumina and a binder component; and the mixture is molded and sintered. 
         [0031]    In the production of the SOFC of the present invention, any method generally employed in this technical field may be used without any particular limitation. For example, the SOFC of the present invention can be produced by forming an oxygen electrode layer on one surface of the solid electrolyte material and a fuel electrode layer on the other surface thereof by the screen printing method or the like, followed by sintering. 
         [0032]    The SOFC of the present invention may be of any type such as the flat-plate vertical-stripe type, the flat-plate lateral-stripe type, the flat tubular type, the tubular vertical-stripe type, the tubular lateral-stripe type, or the microtube type. 
       EXAMPLES 
     Example 1 
       [0033]    A test conducted by fabricating a cell of the type shown in  FIG. 2  is described. A ZrO 2  raw material (average particle diameter 0.3 μm), a Sc 2 O 3  raw material (average particle diameter 0.3 μm), and a CeO 2  raw material (average particle diameter 0.3 μm) were weighed to give a 10Sc3CeSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ). These materials were wet blended in an ethanol solvent for 50 hr, and dried and ground. Then, the blend was sintered at 1200° C. The sintered material was ground into a powder. Then, to the powder, Al 2 O 3  (average particle diameter: 0.5 μm) was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material, and 2 wt % of MnO 2  (average particle diameter 0.5 μm) in terms of Mn content and 5 wt % of a binder PVA were added thereto, followed by mixing in a mortar. The powder containing the PVA was press molded at 50 MPa, and sintered at 1450° C. for 5 hr. Thus, a dense solid electrolyte layer having a 10Sc3CeSZ2Al composition was obtained. After the layer was polished to a thickness of about 200 μm, a film of LSM (average particle diameter: 2 μm) was formed as an oxygen electrode layer by screen printing so as to give a thickness of 20 μm after sintering, and a film of 40 wt % NiO-60 wt % YSZ (average particle diameter: 2 μm) was formed as a fuel electrode layer on an opposite surface by screen printing so as to form a cermet of Ni and YSZ and to give a thickness of 20 μm after sintering. Then, sintering was carried out at 1400° C. for 2 hr. 
       Example 2 
       [0034]    Example 2 was conducted in the same manner as in Example 1, except for the following points. Specifically, with a 10Sc3CeSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was mixed in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material, and 2 wt % of Fe 2 O 3  (average particle diameter: 0.5 μm) in terms of Fe content and 5 wt % of a binder PVA were added thereto. Thus, a dense solid electrolyte layer having a 10Sc3CeSZ2Al composition was obtained. In addition, LSF (average particle diameter: 2 μm) was used as the oxygen electrode layer. 
       Example 3 
       [0035]    Example 3 was conducted in the same manner as in Example 1, except for the following points. Specifically, with a 10Sc3CeSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was mixed in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material, and 1 wt % of MnO 2  (average particle diameter 0.5 μm) in terms of Mn content, 1 wt % of Fe 2 O 3  (average particle diameter: 0.5 μm) in terms of Fe content, and 5 wt % of a binder PVA were added thereto. Thus, a dense solid electrolyte layer having a 10Sc3CeSZ2Al composition was obtained. In addition, LSF (average particle diameter: 2 μm) was used as the oxygen electrode layer. 
       Comparative Example 1 
       [0036]    Comparative Example 1 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained by adding no Al 2 O 3  to a 10Sc1CeSZ composition represented by the general formula of 89 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-1 mol % (CeO 2 ). 
       Comparative Example 2 
       [0037]    Comparative Example 2 was conducted in the same manner as in Example 2, except that a dense solid electrolyte layer was obtained by adding no Al 2 O 3  to a 10Sc1CeSZ composition represented by the general formula of 89 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-1 mol % (CeO 2 ). 
       Comparative Example 3 
       [0038]    Comparative Example 3 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained by adding no Al 2 O 3  to a 10ScSZ composition represented by the general formula of 90 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 ). 
       Comparative Example 4 
       [0039]    Comparative Example 4 was conducted in the same manner as in Example 2, except that a dense solid electrolyte layer was obtained by adding no Al 2 O 3  to a 10ScSZ composition represented by the general formula of 90 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 ). 
       Comparative Example 5 
       [0040]    Comparative Example 5 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10ScSZ composition represented by the general formula of 90 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 ), Al 2 O 3  was added in an amount equivalent to 1 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Comparative Example 6 
       [0041]    Comparative Example 6 was conducted in the same manner as in Example 2, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10ScSZ composition represented by the general formula of 90 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 ), Al 2 O 3  was added in an amount equivalent to 1 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       (Testing Method) 
       [0042]      FIG. 6  schematically shows a testing apparatus. A glass seal (SiO 2 +B 2 O 3 )  104  was placed in an apparatus held by a zirconia tube  105 , and the fabricated SOFC  100  was placed on the glass seal  104 . Moreover, a zirconia tube  105  was placed on an upper surface of the SOFC  100 . While the air was passed on the upper surface of the SOFC of each of Examples 1 to 10 and Comparative Examples 1 to 3, and 97% N 2 +3% H 2  was passed on a lower surface thereof, the temperature of the electric furnace  106  was raised to 1000° C. While the air was passed on the upper surface of the SOFC, and a fuel gas (70% H 2 +30% H 2 O) was passed on the lower surface thereof, the temperature was kept at 1000° C. for 400 hr. Then, while the air was passed on the upper surface of the SOFC, and 97% N 2 +3% H 2  was passed on the lower surface thereof, the temperature was lowered to room temperature. 
       (Analysis 1) 
       [0043]    After the SOFC  100  was peeled off from the glass seal  104 , an exposed surface of the solid electrolyte layer  102  of the SOFC  100 , the exposed surface not having been in contact with the glass seal  104 , was analyzed by SEM and Raman spectroscopy, and the presence or absence of powder formation and the crystal phase were examined. In addition, the crystal phases of all the SOFCs were checked by Raman spectroscopy before the test. 
         [0044]    The SEM observation was carried out by using S-4100 of Hitachi High-Technologies Co., Japan at an acceleration voltage of 15 kV and at a 1000-fold magnification. In the Raman spectroscopy, mode of vibration of Zr—O on the surface of the electrolyte was analyzed by using NRS-2100 of JASCO Co., Japan. The measurement was conducted with a detector equipped with a triple monochromator at a wavenumber resolution of 1 cm −1  with an observation spot of 8 μm in diameter and an excitation wavelength of 523 nm. 
         [0000]    
       
         
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                   
                 Mn content 
                 Fe content 
                 Initial stage 
                 400 hr later 
                   
               
               
                   
                 Composition 
                 (wt %) 
                 (wt %) 
                 Crystal phase 
                 Powder formation 
                 Crystal phase 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 10Sc3CeSZ2Al 
                 2 
                   
                 C 
                 Absent 
                 C 
               
               
                 Example 2 
                 10Sc3CeSZ2Al 
                   
                 2 
                 C 
                 Absent 
                 C 
               
               
                 Example 3 
                 10Sc3CeSZ2Al 
                 1 
                 1 
                 C 
                 Absent 
                 C 
               
               
                 Comp. Ex. 1 
                 10Sc1CeSZ 
                 2 
                   
                 C 
                 Present 
                 t 
               
               
                 Comp. Ex. 2 
                 10Sc1CeSZ 
                   
                 2 
                 C 
                 Present 
                 t 
               
               
                 Comp. Ex. 3 
                 10ScSZ 
                 2 
                   
                 C 
                 Present 
                 t 
               
               
                 Comp. Ex. 4 
                 10ScSZ 
                   
                 2 
                 C 
                 Present 
                 t 
               
               
                 Comp. Ex. 5 
                 10ScSZ1Al 
                 2 
                   
                 C 
                 Present 
                 t 
               
               
                 Comp. Ex. 6 
                 10ScSZ1Al 
                   
                 2 
                 C 
                 Present 
                 t 
               
               
                   
               
             
          
         
       
     
         [0045]    Table 1 shows the test results. The notation is as follows: c: cubic crystals, and t: tetragonal crystals. Powder formation was observed in each of Comparative Examples 1 to 6. In contrast, no powder formation was observed in any of Examples 1 to 3. This demonstrated that the powder formation can be suppressed by employing the composition of the present invention. Moreover, it was also found that the crystal phase remained the c phase in each of Examples 1 to 3, and the crystal phase was transformed to the t phase in all of Comparative Examples 1 to 6. It was found that the composition of the present invention reduced the possibilities of the occurrences of the powder formation and the crystal transformation even when Mn or Fe was contained. 
       (Analysis 2) 
       [0046]    The SOFCs of Examples 1 and 2 and Comparative Examples 1 and 2 were analyzed as follows. Specifically, the fuel electrode layer  103  was peeled off, and the surface of the solid electrolyte layer  102  having been covered with the fuel electrode layer  103  was analyzed by SEM and Raman spectroscopy. 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                   
                 Powder 
                   
                 Crystal 
               
               
                   
                 Composition 
                 formation 
                 Cracks 
                 phase 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 10Sc3CeSZ2Al 
                 Absent 
                 Absent 
                 C 
               
               
                 Example 2 
                 10Sc3CeSZ2Al 
                 Absent 
                 Absent 
                 C 
               
               
                 Comp. Ex. 1 
                 10Sc1CeSZ 
                 Absent 
                 Present 
                 t 
               
               
                 Comp. Ex. 2 
                 10Sc1CeSZ 
                 Absent 
                 Present 
                 t 
               
               
                   
               
             
          
         
       
     
         [0047]    Table 2 shows the results of the analysis. No powder formation was observed in the solid electrolyte layers having been covered with the fuel electrode layers. However, in Comparative Examples 1 and 2, the crystal phase had already changed to the t phase, and cracks were observed at grain boundaries. On the other hand, in Examples 1 and 2, no powder formation was observed, the crystal phase was unchanged, and no cracks were observed at grain boundaries. In the cases of Comparative Examples 1 and 2, it is suggested that the powder formation may occur during a further long time operation, and the powder formation peeling may occur between the fuel electrode layer  103  and the solid electrolyte layer  102 . 
       Optimization of Composition 
     Example 4 
       [0048]    Example 4 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10Sc1CeSZ composition represented by the general formula of 89 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-1 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 1 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 5 
       [0049]    Example 5 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10Sc1CeSZ composition represented by the general formula of 89 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-1 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 6 
       [0050]    Example 6 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10Sc3CeSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 5 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 7 
       [0051]    Example 7 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10Sc5CeSZ composition represented by the general formula of 85 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-5 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 8 
       [0052]    Example 8 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 10Sc6CeSZ composition represented by the general formula of 84 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-6 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 9 
       [0053]    Example 9 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to an 8Sc3CeSZ composition represented by the general formula of 89 mol % (ZrO 2 )-8 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 10 
       [0054]    Example 10 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 9Sc3CeSZ composition represented by the general formula of 88 mol % (ZrO 2 )-9 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 11 
       [0055]    Example 11 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 15Sc3CeSZ composition represented by the general formula of 82 mol % (ZrO 2 )-15 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 12 
       [0056]    Example 12 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer was obtained as follows. Specifically, to a 16Sc3CeSZ composition represented by the general formula of 81 mol % (ZrO 2 )-16 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ), Al 2 O 3  was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
         [0057]    While the air was passed on the upper surface of the SOFC of each of Examples 1, and 4 to 12, and 97% N 2 +3% H 2  was passed on a lower surface thereof by using the testing apparatus shown in  FIG. 6 , the temperature of the electric furnace  106  was raised to 1000° C. While the air was passed on the upper surface of the SOFC, and a fuel gas (70% H 2 +30% H 2 O) was passed on the lower surface thereof, the temperature was kept at 1000° C. for 400 hr. Then, while the air was passed on the upper surface of the SOFC, and 97% N 2 +3% H 2  was passed on the lower surface thereof, the temperature was lowered to room temperature. An exposed surface of the solid electrolyte layer  102  of the SOFC  100 , the exposed surface not having been in contact with the glass seal  104 , was analyzed by SEM and Raman spectroscopy in the same manner, and the presence or absence of powder formation and the crystal phase were examined. 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 3 
               
               
                   
                   
               
               
                   
                   
                   
                 400 hr later 
                   
               
               
                   
                   
                 Initial stage 
                 Powder 
                 Crystal 
               
               
                   
                 Composition 
                 Crystal phase 
                 formation 
                 phase 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 10Sc3CeSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 4 
                 10Sc1CeSZ1Al 
                   
                 Absent 
                 t 
               
               
                 Example 5 
                 10Sc1CeSZ2Al 
                 C 
                 Absent 
                 t 
               
               
                 Example 6 
                 10Sc3CeSZ5Al 
                 C 
                 Absent 
               
               
                 Example 7 
                 10Sc5CeSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 8 
                 10Sc6CeSZ2Al 
                 C 
                 Absent 
                 t 
               
               
                 Example 9 
                 8Sc3CeSZ2Al 
                 C + t 
                 Absent 
                 t 
               
               
                 Example 10 
                 9Sc3CeSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 11 
                 15Sc3CeSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 12 
                 16Sc3CeSZ2Al 
                 C + r 
                 Absent 
                 C + r 
               
               
                   
               
             
          
         
       
     
         [0058]    Table 3 shows the test results. The notation is as follows: c: cubic crystals, t: tetragonal crystals, and r: rhombohedral crystals. No powder formation was observed in any of Examples 1, and 4 to 12. This demonstrated that the powder formation can be suppressed by employing the composition of the present invention. In addition, the crystal phase was transformed to the t phase in each of Examples 4, 5, 8, and 9, and the r phase, which causes phase transformation at around 630° C., partially remained in Example 12. In contrast, the crystal phase remained the c phase in each of Examples 1, 6, 7, 10, and 11. From these results, more preferred compositions are those shown in Examples 1, 6, 7, 10, and 11, where 9 to 15 mol % of scandia and 2 to 5 mol % of the lanthanoid oxide are doped, and more than 1 mol % of alumina is further contained. 
       Regarding Lanthanoid Oxide other than CeO 2 , and Yttria 
     Example 13 
       [0059]    Example 13 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer having a 10Sc3SmSZ2Al composition was obtained as follows. Specifically, with a 10Sc3SmSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (Sm 2 O 3 ), Al 2 O 3  was mixed in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 14 
       [0060]    Example 14 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer having a 10Sc3YbSZ2Al composition was obtained as follows. Specifically, with a 10Sc3YbSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (Yb 2 O 3 ), Al 2 O 3  was mixed in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 15 
       [0061]    Example 15 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer having a 10Sc3LaSZ2Al composition was obtained as follows. Specifically, with a 10Sc3LaSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (La 2 O 3 ), Al 2 O 3  was mixed in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
       Example 16 
       [0062]    Example 16 was conducted in the same manner as in Example 1, except that a dense solid electrolyte layer having a 10Sc3YSZ2Al composition was obtained as follows. Specifically, with a 10Sc3YSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (Y 2 O 3 ), Al 2 O 3  was mixed in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the solid electrolyte material. 
         [0063]    While the air was passed on the upper surface of the SOFC of each of Examples 1, and 13 to 16, and 97% N 2 +3% H 2  was passed on a lower surface thereof by using the testing apparatus shown in  FIG. 6 , the temperature of the electric furnace  106  was raised to 1000° C. While the air was passed on the upper surface of the SOFC, and a fuel gas (70% H 2 +30% H 2 O) was passed on the lower surface thereof, the temperature was kept at 1000° C. for 400 hr. Then, while the air was passed on the upper surface of the SOFC, and 97% N 2 +3% H 2  was passed on the lower surface thereof, the temperature was lowered to room temperature. A surface of the solid electrolyte layer  102  of the SOFC  100 , the surface having been in contact with the glass seal  104 , was analyzed by SEM and Raman spectroscopy in the same manner, and the presence or absence of powder formation and the crystal phase were examined. 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 4 
               
               
                   
                   
               
               
                   
                   
                   
                 400 hr 
                   
               
               
                   
                   
                 Initial stage 
                 later Powder 
                 Crystal 
               
               
                   
                 Composition 
                 Crystal phase 
                 formation 
                 phase 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 10Sc3CeSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 13 
                 10Sc3SmSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 14 
                 10Sc3YbSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 15 
                 10Sc3LaSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                 Example 16 
                 10Sc3YSZ2Al 
                 C 
                 Absent 
                 C 
               
               
                   
               
             
          
         
       
     
         [0064]    Table 4 shows the results of the analysis after the test. No powder formation was observed in any of Examples 13 to 16, and the crystal phase remained the c phase therein. These results are the same as those of Example 1, indicating that the same effect as that achieved in the case where CeO 2  is doped can be achieved, also when a lanthanoid oxides other than CeO 2  or yttria is doped. 
         [0065]    The electric conductivities of the solid electrolyte materials of Examples 1, 13, 14, 15, and 16 were measured. Each solid electrolyte material was press molded, and sintered at 1450° C. for 5 hr. Then, platinum electrodes were attached onto both surfaces thereof, and a reference electrode was attached onto a side surface thereof. The impedance was measured at 1000° C. under atmospheric atmosphere. 
         [0000]    
       
         
               
               
               
             
               
               
               
             
           
               
                   
                 TABLE 5 
               
               
                   
                   
               
               
                   
                   
                 Electric conductivity at 1000° C. 
               
               
                   
                 Composition 
                 (S/cm) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 10Sc3CeSZ2Al 
                 0.21 
               
               
                 Example 13 
                 10Sc3SmSZ2Al 
                 0.19 
               
               
                 Example 14 
                 10Sc3YbSZ2Al 
                 0.18 
               
               
                 Example 15 
                 10Sc3LaSZ2Al 
                 0.18 
               
               
                 Example 16 
                 10Sc3YSZ2Al 
                 0.19 
               
               
                   
               
             
          
         
       
     
         [0066]    Table 5 shows the results of the electric conductivities. The electric conductivity of Example 1 was the highest, indicating that ceria is the most preferable as the lanthanoid oxide doped. 
       Regarding Two-Layer Structure of Solid Electrolyte Layer 
     Example 17 
     (1) Fabrication of First Layer 
       [0067]    A ZrO 2  raw material (average particle diameter 0.3 μm), a Sc 2 O 3  raw material (average particle diameter 0.3 μm), and a CeO 2  raw material (average particle diameter 0.3 μm) were weighed to give a 10ScSZ composition represented by the general formula of 90 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 ). These materials were wet blended in an ethanol solvent for 50 hr, and dried and ground. Then, the blend was sintered at 1200° C. The sintered material was ground into a powder. Then, to the powder, 2 wt % of MnO 2  (average particle diameter 0.5 μm) in terms of Mn content and 5 wt % of a binder PVA were added, followed by mixing in a mortar. The powder containing the PVA was press molded at 50 MPa. Thus, a molded article having a 10Sc1CeSZ1Al composition was fabricated. 
       (2) Fabrication of Second Layer 
       [0068]    A ZrO 2  raw material (average particle diameter 0.3 μm), a Sc 2 O 3  raw material (average particle diameter 0.3 μm), and a CeO 2  raw material (average particle diameter 0.3 μm) were weighed to give a 10Sc3CeSZ composition represented by the general formula of 87 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-3 mol % (CeO 2 ). These materials were wet blended in an ethanol solvent for 50 hr, and dried and ground. Then, the blend was sintered at 1200° C. The sintered material was ground into a powder. Then, to the powder, Al 2 O 3  (average particle diameter: 0.5 μm) was added in an amount equivalent to 2 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the second layer, and 2 wt % of MnO 2  (average particle diameter 0.5 μm) in terms of Mn content and 5 wt % of a binder PVA were added thereto, followed by mixing in a mortar. The powder containing the PVA was press molded at 50 MPa. Thus, a molded article having a 10Sc3CeSZ2Al composition was fabricated. 
       (3) Fabrication of Cell 
       [0069]    The molded article having the 10Sc1CeSZ1Al composition and serving as the first layer and the molded article having the 10Sc3CeSZ2Al composition and serving as the second layer were stacked on each other, thermally adhered to each other under pressure, and then sintered at 1450° C. for 5 hr. The first layer was polished to a thickness of about 190 μm, and the second layer was polished to a thickness of about 10 μm. Then, a film of LSM (average particle diameter: 2 μm) was formed as an oxygen electrode layer on the surface of the first layer by screen printing so as to give a thickness of 20 μm after sintering, and a film of 40 wt % NiO-60 wt % YSZ (average particle diameter: 2 μm) was formed as a fuel electrode layer on the surface of the second layer by screen printing so as to form a cermet of Ni and YSZ and to give a thickness of 20 μm after sintering. Then, sintering was carried out at 1400° C. for 2 hr. 
       Example 18 
       [0070]    Example 18 was conducted in the same manner as in Example 17, except that the composition of the first layer was changed to a composition obtained by adding, to a 10Sc1CeSZ composition represented by the general formula of 89 mol % (ZrO 2 )-10 mol % (Sc 2 O 3 )-1 mol % (CeO 2 ), Al 2 O 3  (average particle diameter: 0.5 μm) in an amount equivalent to 1 mol % relative to the total amount of substances (total molar amount) of the zirconia, the scandia, and the lanthanoid oxide and/or the yttria in the first layer. 
         [0071]    While the air was passed on the upper surface (on the first layer side) of the SOFC of each of Examples 17 and 18, and 97% N 2 +3% H 2  was passed on the lower surface (on the second layer side) thereof by using the testing apparatus shown in  FIG. 6 , the temperature of the electric furnace  106  was raised to 1000° C. While the air was passed on the upper surface (on the first layer side) of the SOFC, and a fuel gas (70% H 2 +30% H 2 O) was passed on the lower surface thereof, the temperature was kept at 1000° C. for 400 hr. Then, while the air was passed on the upper surface (on the first layer side) of the SOFC, and 97% N 2 +3% H 2  was passed on the lower surface thereof, the temperature was lowered to room temperature. An exposed surface of the solid electrolyte layer  102  of the SOFC  100 , the exposed surface not having been in contact with the glass seal  104 , was analyzed by SEM and Raman spectroscopy in the same manner. Thus, the presence or absence of powder formation and the crystal phase were examined, and a comparison with Example 1 was made. 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 6 
               
               
                   
                   
               
               
                   
                 Initial stage 
                 400 hr later 
                   
               
               
                   
                 Crystal phase 
                 Powder formation 
                 Crystal phase 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 C 
                 Absent 
                 C 
               
               
                 Example 17 
                 C 
                 Absent 
                 C 
               
               
                 Example 18 
                 C 
                 Absent 
                 C 
               
               
                   
               
             
          
         
       
     
         [0072]    Table 6 shows the results of the analysis after the test. No powder formation was observed in any of Examples 17 and 18, and the crystal phase remained the c phase therein. It was found that the powder formation and the crystal transformation were successfully suppressed by employing the electrolyte two-layer structure, in which the first layer had the composition of any one of Comparative Examples 1 or 3 and the second layer had the composition of Example 1. 
         [0073]    The electric conductivities of the solid electrolyte materials of Examples 1, 17, and 18 were measured. Each solid electrolyte material was press molded and sintered at 1450° C. for 5 hr. Platinum electrodes were attached onto both surfaces thereof, and a reference electrode was attached onto a side surface thereof. The impedance was measured at 1000° C. under atmospheric atmosphere. 
         [0000]    
       
         
               
               
             
               
               
               
             
           
               
                   
                 TABLE 7 
               
               
                   
                   
               
               
                   
                 Electric conductivity at 1000° C. 
               
               
                   
                 (S/cm) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Example 1 
                 0.21 
               
               
                   
                 Example 17 
                 0.26 
               
               
                   
                 Example 18 
                 0.23 
               
               
                   
                   
               
             
          
         
       
     
         [0074]    Table 7 shows the results of the electric conductivities. It was found that the provision of the layer having a high oxygen ion conductivity to the first layer resulted in a higher electric conductivity than that of Example 1, so that the electric power generation efficiency was increased. From these results, it has been found that it is more effective to form the second layer in a thickness minimum necessary for preventing the powder formation peeling. 
       Example 19 
       [0075]    Example 19 was conducted in the same manner as in Example 17, except that the composition of the first layer was changed to a 10YSZ composition to which no Al 2 O 3  was added, and which is represented by the general formula of 90 mol % (ZrO 2 )-10 mol % (Y 2 O 3 ). 
         [0076]    While the air was passed on the upper surface (on the first layer side) of the SOFC of Example 19, and 97% N 2 +3% H 2  was passed on the lower surface (on the second layer side) thereof by using the testing apparatus shown in  FIG. 6 , the temperature of the electric furnace  106  was raised to 1000° C. While the air was passed on the upper surface (on the first layer side) of the SOFC, and a fuel gas (70% H 2 +30% H 2 O) was passed on the lower surface thereof, the temperature was kept at 1000° C. for 400 hr. Then, while the air was passed on the upper surface (on the first layer side) of the SOFC, and 97% N 2 +3% H 2  was passed on the lower surface thereof, the temperature was lowered to room temperature. An exposed surface of the solid electrolyte layer  102  of the SOFC  100 , the exposed surface not having been in contact with the glass seal  104 , was analyzed by SEM and Raman spectroscopy in the same manner. Thus, the presence or absence of powder formation and the crystal phase were examined, and a comparison with Example 1 was made. 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 8 
               
               
                   
                   
               
               
                   
                 Initial stage 
                 400 hr later 
                   
               
               
                   
                 Crystal phase 
                 Powder formation 
                 Crystal phase 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 C 
                 Absent 
                 C 
               
               
                 Example 19 
                 C 
                 Absent 
                 C 
               
               
                   
               
             
          
         
       
     
         [0077]    Table 8 shows the results of the analysis after the test. No powder formation was observed in Example 19, and the crystal phase remained the c phase therein. It was found that the SOFC having the electrolyte two-layer structure and using yttria as the stabilizer of the first layer also achieved the same effect, when the second layer had the composition of the solid electrolyte layer in the SOFC of the present invention. 
         [0078]    Effects of the present invention are described based on the SOFC of the type using the solid electrolyte layer as a support. However, the same effects are obtained also in SOFCs using an oxygen electrode layer or a fuel electrode layer as a support. 
         [0079]    Regarding the design of the SOFC, the description is made based on the flat plate type. However, the same effects are obtained in the case of any type such as the flat tubular type, the tubular vertical-stripe type, and the microtube type. 
         [0080]    In Examples shown above, the cases in each of which the ScSZ electrolyte material doped with only one lanthanoid oxide or yttria were tested. However, it is conceivable that the same effects as those in Examples shown above can be obtained also in a case where the ScSZ electrolyte material doped with a combination of two or more lanthanoid oxides or a combination of a lanthanoid oxide and yttria. 
       REFERENCE SIGNS LIST 
       [0000]    
       
         
           
               100  SOFC 
               101  oxygen electrode layer 
               102  solid electrolyte layer 
               103  fuel electrode layer 
               104  glass seal (SiO 2 +B 2 O 3 ) 
               105  zirconia tube 
               106  electric furnace 
               107  solid electrolyte layer (first layer) 
               108  solid electrolyte layer (second layer) 
               110  10Sc1CeSZ (cubic crystals) 
               111  10Sc1CeSZ (tetragonal crystals) 
               112  alumina (Al 2 O 3 )