Abstract:
The present invention provides a method for forming interconnection structures, including the following steps: providing a semiconductor wafer with a dielectric layer; forming a first recessed area for forming the interconnection structures and a non-recessed area on the dielectric layer; forming a second recessed area for forming dummy structures on the dielectric layer; depositing a barrier layer to cover the first and second recessed areas and the non-recessed area; depositing a metal layer to fill the first and second recessed areas and cover the non-recessed area; removing the metal layer on the non-recessed area to expose the barrier layer; and removing the barrier layer on the non-recessed area to expose the dielectric layer.

Description:
BACKGROUND OF THE INVENTION 
       [0001]    1. Field of the Invention 
         [0002]    The present invention generally relates to the field of fabricating semiconductor devices, and more particularly to a method for forming interconnection structures in the semiconductor devices. 
         [0003]    2. The Related Art 
         [0004]    Semiconductor devices are generally manufactured or fabricated on semiconductor material such as wafers by using a number of processing steps. The wafers may undergo multiple masking, etching and deposition processing steps to form electronic circuitry of the semiconductor devices. With high integration of the semiconductor devices, metal interconnection structures have developed rapidly in the field of fabricating semiconductor devices. The multiple masking and etching processes can be used to form recessed areas in the wafer, such as trenches, vias, and the like. The deposition process can be used to deposit a metal layer onto both the recessed areas and non-recessed areas of the wafer. After deposition, the metal layer on the non-recessed areas of the wafer is removed and the metal left in the recessed areas of the wafer form the interconnection structures. Particularly, the metal layer is deposited on a dielectric layer formed on the wafer, so in order to prevent the diffusion or leaching of the metal layer into the dielectric layer, a barrier layer is deposited on the dielectric layer before depositing the metal layer and the metal layer is then deposited on the barrier layer. 
         [0005]    Conventional methods including, for example, chemical mechanical polishing (CMP) are adopted to remove the metal layer and the barrier layer on the non-recessed areas of the wafer. The CMP method is widely used in the semiconductor industry to polish and planarize the metal layer on the non-recessed areas of the wafer to form the interconnection structures. In a CMP process, the wafer is positioned on a CMP pad located on a platen. A force is then applied to press the wafer against the CMP pad. The CMP pad and the wafer are moved against and relative to one another while applying the force to polish and planarize the metal layer. A polishing solution, often referred to as polishing slurry, is dispensed on the CMP pad to facilitate the polishing However, the CMP method has several deleterious effects on the semiconductor structure formed on the wafer because of the involved relatively strong mechanical force applied on the metal layer and the barrier layer in the CMP process. 
         [0006]    Another method for removing the metal layer deposited on the non-recessed areas of the wafer is electropolishing The electropolishing method can remove the metal layer with high uniformity and have high selectivity to the barrier layer. It is a mechanical stress free process. However, during the electropolishing process, in order to remove all the metal layer on the non-recessed areas of the wafer, over polish is conducted. But it is found that at the areas, such as field area, wide space area between two adjacent metal lines, and space area at two sides of an isolated metal line, because there is no metal on the non-recessed areas and the barrier layer is exposed after the metal layer is removed at the over polishing stage, the current is conducted through the barrier layer. Then the surface of the barrier layer will be oxidized to form an oxidization film on the top surface of those areas. Or in other words, the oxidization film is thicker at the areas having lower interconnection structure density than at the areas having higher interconnection structure density. Since the metal layer, such as copper, has much lower resistance, the current will mostly go through the metal layer instead of going through the barrier layer. The oxidization film prevents the barrier layer being removed in the barrier layer removal step, and the barrier layer can not be uniformly removed, causing the semiconductor device failure. 
       SUMMARY 
       [0007]    Accordingly, an object of the present invention is to provide a method for forming interconnection structures, including the following steps: providing a semiconductor wafer with a dielectric layer; forming a first recessed area for forming the interconnection structures and a non-recessed area on the dielectric layer; forming a second recessed area for forming dummy structures on the dielectric layer; depositing a barrier layer to cover the first and second recessed areas and the non-recessed area; depositing a metal layer to fill the first and second recessed areas and cover the non-recessed area; removing the metal layer on the non-recessed area to expose the barrier layer; and removing the barrier layer on the non-recessed area to expose the dielectric layer. 
         [0008]    As described above, because of the dummy structures, when the metal layer is removed from the non-recessed area, the current is mostly conducted through the dummy structures and the surface of the barrier layer will not be oxidized, because the electrical conductivity of the metal layer is much higher than that of the barrier layer. The barrier layer on the non-recessed area can be removed easily, uniformly and completely, ensuring the quality of a semiconductor device having the interconnection structures. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0009]    The present invention will be apparent to those skilled in the art by reading the following description of preferred embodiments thereof, with reference to the attached drawings, in which: 
           [0010]      FIG. 1  is a flow chart showing an exemplary damascene process; 
           [0011]      FIG. 2  is a cross-sectional view showing the exemplary damascene process; 
           [0012]      FIG. 3  is a flow chart showing another exemplary damascene process; 
           [0013]      FIG. 4  is a top view showing an exemplary dummy structure formed at a field area of a wafer before a barrier layer removed; 
           [0014]      FIG. 4(   a ) is a cross-sectional view taken along line A-A of  FIG. 4 ; 
           [0015]      FIG. 4(   b ) is a cross-sectional view taken along line B-B of  FIG. 4 ; 
           [0016]      FIG. 5  is a top view showing the exemplary dummy structure formed at the field area of the wafer after the barrier layer removed; 
           [0017]      FIG. 5(   a ) is a cross-sectional view taken along line A-A of  FIG. 5 ; 
           [0018]      FIG. 5(   b ) is a cross-sectional view taken along line B-B of  FIG. 5 ; 
           [0019]      FIG. 6  is a top view showing an exemplary dummy structure formed at wide space areas between adjacent metal lines of a wafer after a barrier layer removed; 
           [0020]      FIG. 7  is a top view showing an exemplary dummy structure formed at space areas at two sides of an isolated metal line of a wafer after a barrier layer removed; 
           [0021]      FIGS. 8(   a )-( i ) show various exemplary shapes that can be used to form the dummy structure; 
           [0022]      FIG. 9(   a ) is a SEM top view showing a wafer having no dummy structures after a barrier layer removing process; and 
           [0023]      FIG. 9(   b ) is a SEM top view showing a wafer having the dummy structures after the barrier layer removing process. 
       
    
    
     DETAILED DESCRIPTION OF EMBODIMENTS 
       [0024]    Referring to  FIG. 1  and  FIG. 2 , an exemplary damascene process is depicted which can be used to form interconnection structures in a semiconductor device. In step  110 , a wafer  201  or other substrate is provided. The wafer  201  has an inter-metal dielectric (IMD) layer  202  formed thereon. The IMD layer  202  can include materials such as silicon dioxide and the like, or materials having dielectric constants lower than silicon dioxide, which can be used to lower the capacitance between the interconnection structures in the semiconductor device. In step  120 , first recessed areas, for example, trenches, vias, etc., are formed on the IMD layer  202  for forming the interconnection structures. In step  130 , a barrier layer  203  is deposited on the IMD layer  202  by any convenient deposition method, such as chemical vapor deposition (CVD), physical vapor deposition (PVD), atomic layer deposition (ALD), and the like, such that the barrier layer  203  covers both the first recessed areas and non-recessed areas of the IMD layer  202 . Because the IMD layer  202  can have a porous microstructure, the barrier layer  203  can include materials that can prevent the diffusion or leaching of a subsequently deposited metal layer  204  into the IMD layer  202 . Furthermore, the barrier layer  203  can be formed from a conductive material, which adheres to both the IMD layer  202  and the metal layer  204 . For instance, the barrier layer  203  can include materials such as titanium, tantalum, tungsten, titanium nitride, tantalum nitride, tungsten nitride, tantalum silicon nitride, tungsten silicon nitride, and the like. 
         [0025]    In step  140 , the metal layer  204  is deposited on the barrier layer  203  by any convenient method, such as PVD, CVD, ALD, electroplating and the like. Furthermore, in some applications, such as when plating is used to deposit the metal layer  204 , a seed layer can be deposited onto the barrier layer  203  before depositing the metal layer  204 . The seed layer can include the same material as the metal layer  204  in order to facilitate the deposition and bonding of the metal layer  204  onto the barrier layer  203 . The metal layer  204  fills the first recessed areas and covers the non-recessed areas of the IMD layer  202 . Besides, the metal layer  204  can include various electrically conductive materials, such as copper, aluminum, nickel, zinc, silver, gold, tin, chromium, superconductor materials, and the like. Preferably, the metal layer  204  can include copper. Furthermore, it should be recognized that the metal layer  204  can include an alloy of any of the various electrically conductive materials, or compound of superconductor. 
         [0026]    In step  150 , after the metal layer  204  is deposited, the metal layer  204  then should be removed from the non-recessed areas by any convenient method, such as electropolishing and the like. It should be recognized that polishing the metal layer  204  from the non-recessed areas can include removing the metal layer  204  from the non-recessed areas of the barrier layer  203  deposited on the IMD layer  202 . For a description of electropolishing, please see U.S. patent application Ser. No. 09/497,894, filed on Feb. 4, 2000, which is incorporated in its entirety herein by reference. 
         [0027]    Subsequently, in step  160 , after removing the metal layer  204  from the non-recessed areas, the barrier layer  203  is removed from the non-recessed areas by any convenient method, such as wet etching, dry chemical etching, dry plasma etching, and the like. Preferably, the barrier layer  203  is removed by using XeF 2  gas phase etching As shown in  FIG. 2 , in order to remove all the metal layer  204  on the non-recessed areas, when the metal layer  204  is removed from the non-recessed areas, over polish is conducted. Because there is no metal layer  204  on the non-recessed areas and the barrier layer  203  is exposed after the metal layer  204  is removed at the over polishing process, the current is conducted through the barrier layer  203 , causing the surface of the areas, such as field area, wide space area between two adjacent metal lines, and space area at two sides of an isolated metal line, of the barrier layer  203  to be oxidized to form an oxidization film  205  thereon. Before removing the barrier layer  203 , the oxidization film  205  must be removed in advance. Besides, the oxidization film  205  thickness is associated with the interconnection structure density. In other words, the oxidization film  205  is thicker at the areas having lower interconnection structure density than at the areas having higher interconnection structure density. Since the metal layer  204 , such as copper, has much lower resistance, the current will mostly go through the metal layer  204  instead of going through the barrier layer  203 . The oxidization film  205  can prevent the barrier layer  203  being removed in the barrier layer  203  removal step, and the barrier layer  203  can not be uniformly removed, causing the semiconductor device failure. 
         [0028]    Accordingly, referring to  FIG. 3  to  FIG. 5(   b ), depicting another exemplary damascene process that can be used to form interconnection structures in a semiconductor device, compared to the above damascene process, this damascene process can include dummy structures  200  at the field area to avoid producing the oxidization film  205  on the barrier layer  203  when over polishing the metal layer  204 . This damascene process is similar in many respects to the above damascene process, except that the dummy structures  200  are included at the field area. This damascene process will be briefly described hereinafter. 
         [0029]    In step  210 , a wafer  201  or other substrate is provided. The wafer  201  has an inter-metal dielectric (IMD) layer  202  formed thereon. The IMD layer  202  can include materials such as silicon dioxide and the like, or materials having dielectric constants lower than silicon dioxide, which can be used to lower the capacitance between the interconnection structures in the semiconductor device. 
         [0030]    In step  220 , first recessed areas, for example, trenches, vias, etc., are formed on the IMD layer  202  for forming the interconnection structures. 
         [0031]    In step  230 , second recessed areas, for example, trenches, vias, etc., are formed at the predetermined field area of the IMD layer  202  for forming the dummy structures  200 . The dummy structures  200  can be formed at the same time that the interconnection structures are formed, and the depth and width of the dummy structures  200  are the same as the interconnection structures. It should be recognized that the dummy structures  200  can be formed independently and the depth and width of the dummy structures  200  can be not the same as the interconnection structures. 
         [0032]    In step  240 , a barrier layer  203  is deposited on the IMD layer  202  by any convenient deposition method, such as chemical vapor deposition (CVD), physical vapor deposition (PVD), atomic layer deposition (ALD), and the like, such that the barrier layer  203  covers both the recessed areas, including the first and second recessed areas and non-recessed areas of the IMD layer  202 . 
         [0033]    In step  250 , a metal layer  204  is deposited on the barrier layer  203  by any convenient method, such as PVD, CVD, ALD, electroplating and the like. Furthermore, in some applications, such as when plating is used to deposit the metal layer  204 , a seed layer can be deposited onto the barrier layer  203  before depositing the metal layer  204 . The seed layer can include the same material as the metal layer  204  in order to facilitate the deposition and bonding of the metal layer  204  onto the barrier layer  203 . The metal layer  204  fills the recessed areas, including the first and second recessed areas and covers the non-recessed areas of the IMD layer  202 . 
         [0034]    In step  260 , after the metal layer  204  is deposited, the metal layer  204  then should be removed from the non-recessed areas by any convenient method, such as electropolishing and the like. It should be recognized that polishing the metal layer  204  from the non-recessed areas can include removing the metal layer  204  from the non-recessed areas of the barrier layer  203  deposited on the IMD layer  202 . Preferably, the metal layer  204  removing process can include two steps. The first step is that a partial metal layer  204  is removed by using the CMP method to achieve better surface planarity, and the subsequent step is that the rest metal layer  204  is removed by using the electropolishing method, avoiding damaging the semiconductor device. 
         [0035]    In step  270 , after removing the metal layer  204  from the non-recessed areas, the barrier layer  203  is removed from the non-recessed areas by any convenient method, such as wet etching, dry chemical etching, dry plasma etching, and the like. Preferably, the barrier layer  203  is removed by using XeF 2  gas phase etching The metal layer  204  remained in the first recessed areas which are used for forming the interconnection structures is formed the interconnection structures. The metal layer  204  remained in the second recessed areas which are used for forming the dummy structures  200  is used to form the dummy structures  200 . It should be recognized that the material of the dummy structures  200  can be not the same as the interconnection structures. As shown in  FIG. 5  to  FIG. 5(   b ), because the field area includes the dummy structures  200 , even the metal layer  204  is over polished, for the resistance of the dummy structures  200  is much lower than that of the barrier layer  203 , the current is mostly conducted through the dummy structures  200  and the surface of the barrier layer  203  will not be oxidized. The barrier layer  203  on the non-recessed areas of the IMD layer  202  can be removed easily and uniformly. 
         [0036]    As shown in  FIGS. 3 to 5(   b ), the density of the dummy structures  200  formed at the field area can be chosen in the range of 50% to 100% of that of the interconnection structure. The distance W 1  between the adjacent interconnection structure and the dummy structure  200  can be chosen in the range of 20 nm to 5000 nm. The size of the dummy structures  200  can be chosen in the range of 20 nm to 5000 nm, and more specifically, the width D 1  of the dummy structure  200  can vary from 20 nm to 5000 nm, the length Dw of the dummy structure  200  can vary from 20 nm to 5000 nm. 
         [0037]    In some applications, if the space between metal lines also referred to as the interconnection structures is too wide, the oxidization of the barrier layer  203  will be happened too when over polishing the metal layer  204 . So at the wide space areas between adjacent metal lines, there can be included dummy structures  300 , as shown in  FIG. 6 . The width W 3  of the wide space area can be 60 nm or wider. The size of the dummy structures  300  can be as same as the dummy structures  200 . 
         [0038]    In some applications, if two sides of an isolated metal line are too wide, the oxidization of the barrier layer  203  will be happened too when over polishing the metal layer  204 . So at the space areas of the two sides of the isolated metal line, there can be included dummy structures  400 , as shown in  FIG. 7 . The density of the dummy structures  400  can be chosen in the range of 20% to 80%. The size of the dummy structures  400  can be as same as the dummy structures  200 . 
         [0039]    With reference to  FIGS. 8(   a )˜( i ), various exemplary shapes that can be used to form the dummy structures  200 ,  300 ,  400  are shown, such as square, vertical rectangle, horizontal rectangle, round shape, oval shape, cross shape, elliptical shape, triangle shape, arc shape and the like. It should be recognized that although particular exemplary shapes are depicted in  FIGS. 8(   a )˜( i ), any shape can be used to form the dummy structures  200 ,  300 ,  400  depending on the particular application and the dummy structures  200 ,  300 ,  400  can include one or more different shapes. 
         [0040]    Please refer to  FIG. 9(   a ) and  FIG. 9(   b ).  FIG. 9(   a ) is a SEM top view showing a wafer  201  having no dummy structures  200  at the field area after a barrier layer  203  removing process. It can be seen that the barrier layer  203  around the interconnection structures is removed completely, but at the field area, the barrier layer  203  isn&#39;t removed completely. There is some residual barrier layer  203 . Comparatively,  FIG. 9(   b ) is a SEM top view showing a wafer  201  having the dummy structures  200  at the field area after the barrier layer  203  removing process. It can be seen that the barrier layer  203  is removed completely at the field area. 
         [0041]    As described above, the present invention utilizes the dummy structures  200 ,  300 ,  400  formed at the field area, the wide space area between two adjacent metal lines and the space area at two sides of an isolated metal line to avoid the barrier layer  203  being oxidized when over polishing the metal layer  204 , so the barrier layer  203  can be removed easily, completely and uniformly, ensuring the quality of the semiconductor device. It should be recognized that the dummy structures  200 ,  300 ,  400  can also be formed at the area which has less pattern density than other area. 
         [0042]    The foregoing description of the present invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and obviously many modifications and variations are possible in light of the above teaching Such modifications and variations that may be apparent to those skilled in the art are intended to be included within the scope of this invention as defined by the accompanying claims.