Abstract:
The conventional free layer in a TMR read head has been replaced by a composite of two or more magnetic layers, one of which is iron rich The result is an improved device that has a higher MR ratio than prior art devices, while still maintaining free layer softness and acceptable magnetostriction. A process for manufacturing the device is also described.

Description:
RELATED PATENT APPLICATION  
       [0001]     The present application is related to application Ser. No. 10/999,826 which was filed on Nov. 30, 2004. 
     
    
     FIELD OF THE INVENTION  
       [0002]     The invention relates to the general field of CPP TMR read heads with particular reference to the free layer sub-structure.  
       BACKGROUND OF THE INVENTION  
       [0003]     The principle governing the operation of most magnetic read heads is the change of resistivity of certain materials in the presence of a magnetic field (magneto-resistance or MR). Magneto-resistance can be significantly increased by means of a structure known as a spin valve where the resistance increase (known as Giant Magneto-Resistance or GMR) derives from the fact that electrons in a magnetized solid are subject to significantly less scattering by the lattice when their own magnetization vectors (due to spin) are parallel (as opposed to anti-parallel) to the direction of magnetization of their environment.  
         [0004]     The key elements of a spin valve are illustrated in  FIG. 1 . They are seed layer  11  (lying on lower conductive lead  10 ) on which is antiferromagnetic layer  12  whose purpose is to act as a pinning agent for a magnetically pinned layer. The latter is a synthetic antiferromagnet formed by sandwiching antiferromagnetic coupling layer  14  between two antiparallel ferromagnetic layers  13  (AP2) and  15  (AP1).  
         [0005]     Next is a non-magnetic spacer layer  16  on which is low coercivity (free) ferromagnetic layer  17 . A contacting layer such as lead  18  lies atop free layer  17 . Not shown, but generally present, is a capping layer between  17  and  18 . When free layer  17  is exposed to an external magnetic field, the direction of its magnetization is free to rotate according to the direction of the external field. After the external field is removed, the magnetization of the free layer will stay at a direction, which is dictated by the minimum energy state, determined by the crystalline and shape anisotropy, current field, coupling field and demagnetization field.  
         [0006]     If the direction of the pinned field is parallel to the free layer, electrons passing between the free and pinned layers suffer less scattering. Thus, the resistance in this state is lower. If, however, the magnetization of the pinned layer is anti-parallel to that of the free layer, electrons moving from one layer into the other will suffer more scattering so the resistance of the structure will increase. The change in resistance of a spin valve is typically 8-20%.  
         [0007]     Earlier GMR devices were designed so as to measure the resistance of the free layer for current flowing parallel to its two surfaces. However, as the quest for ever greater densities has progressed, devices that measure current flowing perpendicular to the plane (CPP), as exemplified in  FIG. 1 , have also emerged. CPP GMR heads are considered to be promising candidates for the over 100 Gb/in 2  recording density domain (see references 1-3 below).  
         [0008]     A related effect to the GMR phenomenon described above is tunneling magnetic resistance (TMR) in which the layer that separates the free and pinned layers is a non-magnetic insulator, such as alumina or silica. Its thickness needs to be such that it will transmit a significant tunneling current. Typically, this is around 5-20 Angstroms.  
         [0009]     A MTJ (magnetic tunnel junction) is readily visualized by substituting a very thin dielectric layer for spacer layer  16  described above for the GMR device. The principle governing the operation of the MTJ in magnetic read sensors is the change of resistivity of the tunnel junction between two ferromagnetic layers when it is subjected to a bit field from magnetic media. When the magnetizations of the pinned and free layers are in opposite directions, the tunneling resistance increases due to a reduction in the tunneling probability. The change of resistance is typically 40%, which is much larger than for GMR devices.  
         [0010]     With the decrease of AlOx thickness in TMR sensor, MR ratio drops with areal resistance. The present invention discloses how a higher MR ratio can be obtained while still retaining the same R.A (resistance.area product) as before. Additionally, the invention allows several of the magnetic properties of the device to be adjusted.  
         [0011]     We note the following references to be of interest: 
    1. Hitoshi Kanai “Multilayer spin valve magneto-resistive effect magnetic head with free magnetic layer including two sublayers and magnetic disk drive including same”, U.S. Pat. No. 5,896,252 (Apr. 20, 1999).     2. Dian Song et al., “Demonstrating a Tunneling Magneto-Resistive Read Head”, IEEE Transactions On Magnetics, Vol. 36, No. 5, 2000, p 2545.     3. Ishiwata et al., “Tunneling magnetoresistance transducer and method for manufacturing the same”, U.S. Pat. No. 6,452,204 (Sep. 17, 2002).     4. Hitoshi Kanai “Multilayer spin valve magneto-resistive effect magnetic head with free magnetic layer including two sublayers and magnetic disk drive including same”, U.S. Pat. No. 5,896,252 (Apr. 20, 1999)     5. K. Ohashi et al. “Low-Resistance Tunnel Magnetoresistive Head” IEEE Transactions On Magnetics, Vol. 36, NO. 5, 2000, p 2549.     6. P. P. Freitas et al., “Spin-dependent Tunnel Junctions for Memory and Read-Head applications”, IEEE Transactions On Magnetics, Vol. 36, No. 5, 2000, p 2796.     7. Ishiwata et al., “Tunneling magnetoresistance transducer and method for manufacturing the same”, U.S. Pat. No. 6,452,204 (Sep. 17, 2002).    
 
         [0019]     Composite free layers, such as Co90Fe10/Ni80Fe20, are standard structures for giant magnetoresistive (GMR) sensors of magnetic recording heads. A composite free layer usually comprises two magnetic layers, namely first free layer (FL1) and second free layer (FL2), which are directly magnetic-coupled. FL1 (usually Co-rich alloys) provide strong spin dependent scattering for higher signal, while FL2 (usually Permalloy-type NiFe material) provides magnetic softness to suppress magnetic noise. This composite free layer structure has also been used in tunneling magnetoresistive (TMR) sensors, a typical TMR structure being as follows:  
         [0000]     Buffer layer/Antiferromagnetic layer/CoFe/Ru/CoFe/AlOx/CoFe/NiFe/Capping layer  
         [0020]     in which the Cu spacer layer of GMR structure is replaced by an AlOx layer. Compared to GMR, the advantage of TMR is higher MR ratio, which is usually larger than 20%. TMR sensors are operated in CPP (current perpendicular to plane of film) mode so that the sensor resistance will increase as the TMR sensor is scaled down in order to achieve higher recording density.  
         [0021]     To maintain a useful sensor resistance range, the AlOx thickness has to be reduced to less than 7 A to achieve low areal resistance, R.A, (of several ohm*μm 2 ). However, as a consequence, the MR ratio will also drop as R.A decreases. Thus, one of the major challenges facing the TMR sensor is how to improve the MR ratio while still keeping R.A low.  
         [0022]     Additionally, reference is made to HT04-015 (application Ser. No. 10,854,651 filed May 26, 2004) which deals with a similar problem towards which the present invention takes a different approach as well as to the following references that were found during a routine search:  
         [0023]     U.S. Pat. No. 6,529,353 (Shimazawa et al), U.S. Pat. No. 5,896,252 (Kanai), and U.S. Pat. No. 6,519,124 (Redon et al) disclose free layers comprising CoFe and NiFe. U.S. Patent Application 2004/0047190 (Odagawa et al) describes a Ni-rich free layer. U.S. Patent Application 2004/0184198 (Tetsukawa et al) discloses a free layer comprising FeNi with Fe 5-40%. U.S. Patent Application 2004/0109263 (Suds et al) teaches a free layer comprising FeNi and a Co alloy with no disclosure of the percentage of Fe.  
       SUMMARY OF THE INVENTION  
       [0024]     It has been an object of at least one embodiment of the present invention to provide a TMR magnetic read head having an improved MR ratio as well as a free layer that is magnetically soft  
         [0025]     Another object of at least one embodiment of the present invention has been to provide a process for manufacturing said read heads.  
         [0026]     Still another object of at least one embodiment of the present invention has been that said process be compatible with existing processes for the manufacture of TMR devices.  
         [0027]     These objects have been achieved by replacing the conventional free layer by a laminate comprising a layer that is iron rich with at least one other magnetic layer such as Permalloy. The result is an improved TMR device that has a higher GMR ratio than prior art devices, while still maintaining free layer softness and acceptable magnetostriction. A process for manufacturing the device is also described. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0028]      FIG. 1  shows a GMR/TMR stack of the prior art which has a conventional free layer.  
         [0029]      FIG. 2  shows a TMR stack having a modified free layer according to the teachings of the present invention.  
     
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0030]     In the present invention, Ni-rich NiFe is replaced with Fe-rich FeNi for FL2 in the composite free layer structure in order to obtain higher MR ratio in a TMR sensor while maintaining low R.A.  
         [0031]     The process begins with the formation of lower lead  10  onto which is deposited seed layer  11  followed by pinning layer  12 . Layer  12  comprises a suitable antiferromagnetic material such as IrMn and it is deposited to a thickness between 45 and 80 Angstroms. Layer  13  (AP2), the first of the two antiparallel layers that will form the synthetic AFM pinned layer, is then deposited onto layer  12 . This is followed by layer of AFM coupling material  14  and then AP1 layer is deposited thereon.  
         [0032]     Next, tunneling, non-magnetic, insulating layer  16  is deposited on AP1 layer  15 . For the TMR design, layer  16  would be a dielectric layer of a material such as alumina between about 5 and 10 Angstroms thick.  
         [0033]     Now follows a key feature of the invention by which the free layer  17   a  is made up of three sub-layers  21 - 23 :  
         [0034]     Layer  21 , referred to as FL1, comprises one or more elements selected from the group consisting of Co, Fe, and Ni. FL2 (layer  22 ) is Fe x Ni 1-x , where x is between 0.6 and 0.8. Free layer  17   a  may be constituted from layers  21  and  22  or, optionally, additional layers (such as layer  23 ) could also be added. If FL2 is made up of multiple magnetic layers, one of these must contain at least 50 atomic percent of iron and be between about 2 and 80 Angstroms thick.  
         [0035]     The process concludes with the deposition of capping layer  24  followed by upper lead layer  18 , the completed structure being now ready to serve as a TMR read head.  
         [0000]     Confirmation of the Effectiveness of the Invention:  
         [0036]     TABLE I below compares the properties of reference TMR sample A, having a Ni 82 Fe 18  free layer, with those of samples B and C which are GMR stacks having a Fe 66 Ni 34  free layer. Except for FL2, the other parts of the full GMR stack have been kept the same.  
                                   TABLE I                       Sample   FL1   FL2   Bs   R.A   dR/R                   A   10 Å CoFe(10%   30 Å NiFe(18%)   0.349   2.4   17%       B   10 Å CoFe(10%)   17 Å FeNi(34%)   0.272   2.3   21%       C   10 Å CoFe(10%   25 Å FeNi(34%)   0.419   2.4   20%                  
 
         [0037]     In TABLE I, 0.6 μm circle devices were used. These had a TMR structure of Seed layer\Antiferromagnetic layer\CoFe\Ru\CoFe\AlOx\FL1\FL2\Capping layer. FL2 was permalloy (Ni82Fe18) for sample A and FeNi(34 at %) for samples B and C. R.A is given in units of ohm·μm 2 . Bs values were measured on full film samples.  
         [0038]     It can be seen that MR ratio is significantly enhanced with the new composite free layer structure. Since the MR ratio is usually determined by the spin polarization of magnetic layers interfacing with barrier layer, the enhancement MR with new FL2 material indicates that FL2 material can affect spin polarization of FL1 through inter-diffusion or modification of band structure.  
         [0039]     Another example of new composite free layer structure is: FL1\FeNi(34%)\NiFe(18%). By varying the relative thicknesses of FeNi(34%) and NiFe(18%), we can obtain high MR ratio, (low) adjustable magnetic softness, and suitable magnetostriction. Some examples are shown in TABLE II below:  
                                             TABLE II                       FL2   Bs   Hc   lambda                                12CoFe(10%)/25NiFe 66%)   0.46   12.47   8.5E−06       10CoFe(10%)/10NiFe(66%)/25NiFe(18%)   0.47   4.3   9.0E−06       5CoFe(10%)/10NiFe(66%)/40NiFe(18%)   0.54   2.9   7.0E−06                  
 
         [0040]     The implementation of the invention requires only a target of new material to replace current NiFe targets for GMR stack sputtering. The annealing process can be kept the same. Therefore, there is no change of the process flow and related process compared to current practice.