Abstract:
A method of forming a metal trench pattern in a thin-film device includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a metal layer for filling spaces in the trench forming portion and for covering the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of planarizing at least a top surface of the formed metal layer until the trench forming portion of the resist pattern layer is at least exposed, and a step of removing the exposed trench forming portion of the resist pattern layer.

Description:
BACKGROUND OF THE INVENTION 
       [0001]    1. Field of the Invention 
         [0002]    The present invention relates to a method of forming a metal trench pattern in a thin-film device and to a manufacturing method of a thin-film device. 
         [0003]    2. Description of the Related Art 
         [0004]    When manufacturing a thin-film device with a metal trench pattern such as a trench capacitor for example, in general, recesses or trenches are first formed and then an adjacent space layer is deposited on top surfaces around the recesses in order to self-align a height of a top surface of opening edges of the recesses with a height of the top surfaces of the adjacent spaces around the recesses. U.S. Pat. No. 6,207,524 B1 discloses such method for manufacturing a semiconductor memory cell with a trench capacitor. 
         [0005]    However, if the deposition is done to form an adjacent space layer around recesses after forming these recesses, the layer will be also deposited in the recesses and the deposited layer once formed in the recesses will be difficult to completely remove. Particularly, in case that the trench is deep, it may be impossible to remove the deposited layer in the trench. If such unnecessary deposited layer is remained in the recesses, it may be impossible to keep a precise shape of the trench as desired. In such case, it will be difficult to fabricate, by utilizing the trench pattern, a trench capacitor with high precision and high quality. 
         [0006]    To solve such problem in the conventional art, the assignee of the present application has proposed a method of forming a recess pattern in Japanese Patent Application No. 2007-089644, filed on Mar. 29, 2007. According to the proposed method, openings of a metal trench pattern are covered by a dry resist film to prevent an adjacent space layer from being deposited in the recesses. It should be noted that this Japanese Patent Application No. 2007-089644 had not published when the present invention was invented and also when the present application was filed. 
         [0007]    However, according to this recess pattern forming method proposed by the assignee of the present application, since the dry resist film or resist pattern is removed just after the metal trench pattern is formed, the most part in the recesses is remained hollow during the following processes. This causes convex portions or pillars that form the trench there between to easily deform or to topple over, particularly when the trench is deep. 
       SUMMARY OF THE INVENTION 
       [0008]    It is therefore an object of the present invention to provide a method of forming a metal trench pattern in a thin-film device and a manufacturing method of a thin-film device, whereby unnecessary material can be prevented from being deposited in recesses of the trench pattern. 
         [0009]    Another object of the present invention is to provide a method of forming a metal trench pattern in a thin-film device and a manufacturing method of a thin-film device, whereby convex portions or pillars that form the trench pattern can be prevented from being deformed. 
         [0010]    According to the present invention, a method of forming a metal trench pattern in a thin-film device includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a metal layer for filling spaces in the trench forming portion and for covering the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of planarizing at least a top surface of the formed metal layer until the trench forming portion of the resist pattern layer is at least exposed, and a step of removing the exposed trench forming portion of the resist pattern layer. 
         [0011]    Since the concave portions or recesses in the trench pattern are filled with the resist layer until the planarization is finished, it is possible to prevent slurry used in planarization or lapped material from entering into the spaces or recesses of the trench pattern and also to prevent the convex portions or pillars that configure the trench pattern by sandwiching the spaces or recesses there between from being deformed or toppled over. 
         [0012]    It is preferred that the method further includes a step of removing a part of the resist pattern layer and a part of the electrode film, which are uncovered by the formed metal layer, and a step of depositing a peripheral area layer on the metal layer, and that the planarizing step includes planarizing top surfaces of the formed metal layer and the deposited peripheral area layer until the trench forming portion of the resist pattern layer is at least exposed. In this case, preferably, the step of depositing a peripheral area layer includes depositing an insulation layer. 
         [0013]    It is also preferred that the planarizing step includes planarizing a top surface of only the formed metal layer until the trench forming portion of the resist pattern layer is at least exposed. 
         [0014]    According to the present invention, also, a method of forming a metal trench pattern in a thin-film device, includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a first metal layer made of a first metal material for filling spaces in the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of forming a second metal layer made of a second metal material for covering at least the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, the second metal material having a higher chemical activity than that of the first metal material, a step of planarizing at least a top surface of the formed second metal layer just before the trench forming portion of the resist pattern layer is exposed, a step of removing the second metal layer to expose the trench forming portion of the resist pattern layer, and a step of removing the exposed trench forming portion of the resist pattern layer. 
         [0015]    Since the concave portions or recesses in the trench pattern are filled with the second metal layer and the resist layer until the planarization is finished, it is possible to prevent slurry used in planarization or lapped material from entering into the spaces or recesses of the trench pattern. Furthermore, since the concave portions or recesses in the trench pattern are filled with not only the resist layer but also the second metal layer until the planarization is finished, it is possible to securely support convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between so as to effectively prevent these convex portions or pillars from being deformed or toppled over. 
         [0016]    It is preferred that the method further includes a step of removing a part of the resist pattern layer and a part of the electrode film, which are uncovered by the formed first and second metal layers, and a step of depositing a peripheral area layer on the second metal layer, and that the planarizing step includes planarizing top surfaces of the formed second metal layer and the deposited peripheral area layer just before the trench forming portion of the resist pattern layer is exposed. In this case, preferably, the step of depositing a peripheral area layer includes depositing an insulation layer. 
         [0017]    It is also preferred that the planarizing step includes planarizing a top surface of only the formed second metal layer just before the trench forming portion of the resist pattern layer is exposed. 
         [0018]    According to the present invention, further, a method of forming a metal trench pattern in a thin-film device, includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a first metal layer made of a first metal material for filling spaces in the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of shaving by an ashing process a top surface of the formed resist pattern layer, a step of forming a second metal layer made of a second metal material for covering at least the trench forming portion, by performing plating through the shaved resist pattern layer using the deposited electrode film as an electrode, the second metal material having a higher chemical activity than that of the first metal material, a step of planarizing top surfaces of the formed first and second metal layers just before the trench forming portion of the resist pattern layer is exposed, a step of removing the second metal layer to expose the trench forming portion of the resist pattern layer, and a step of removing the exposed trench forming portion of the resist pattern layer. 
         [0019]    Since the concave portions or recesses in the trench pattern are filled with the second metal layer and the resist layer until the planarization is finished, it is possible to prevent slurry used in planarization or lapped material from entering into the spaces or recesses of the trench pattern. Furthermore, since the concave portions or recesses in the trench pattern are filled with not only the resist layer but also the second metal layer until the planarization is finished, it is possible to securely support convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between so as to effectively prevent these convex portions or pillars from being deformed or toppled over. 
         [0020]    It is preferred that the method further includes a step of removing a part of the resist pattern layer and a part of the electrode film, which are uncovered by the formed first and second metal layers, and a step of depositing a peripheral area layer on the second metal layer, and that the planarizing step includes planarizing top surfaces of the formed first and second metal layers and of the deposited peripheral area layer just before the trench forming portion of the resist pattern layer is exposed. In this case, preferably, the step of depositing a peripheral area layer includes depositing an insulation layer. 
         [0021]    It is also preferred that the planarizing step includes planarizing top surfaces of only the formed first and second metal layers just before the trench forming portion of the resist pattern layer is exposed. 
         [0022]    According to the present invention, still further a manufacturing method of a thin-film device, includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a metal layer for filling spaces in the trench forming portion and for covering the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of planarizing at least a top surface of the formed metal layer until the trench forming portion of the resist pattern layer is at least exposed, and a step of removing the exposed trench forming portion of the resist pattern layer. 
         [0023]    It is preferred that the method further includes a step of depositing a dielectric film on the surface of the metal layer after the removing step of the resist pattern layer, and a step of depositing an upper electrode film on a surface of the dielectric film. 
         [0024]    It is also preferred that the method further includes a step of removing a part of the resist pattern layer and a part of the electrode film, which are uncovered by the formed metal layer, and a step of depositing a peripheral area layer on the metal layer, and that the planarizing step includes planarizing top surfaces of the formed metal layer and the deposited peripheral area layer until the trench forming portion of the resist pattern layer is at least exposed. In this case, preferably, the step of depositing a peripheral area layer includes depositing an insulation layer. 
         [0025]    It is further preferred that the planarizing step includes planarizing a top surface of only the formed metal layer until the trench forming portion of the resist pattern layer is at least exposed. 
         [0026]    According to the present invention, still further, a manufacturing method of a thin-film device, includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a first metal layer made of a first metal material for filling spaces in the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of forming a second metal layer made of a second metal material for covering at least the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, the second metal material having a higher chemical activity than that of the first metal material, a step of planarizing at least a top surface of the formed second metal layer just before the trench forming portion of the resist pattern layer is exposed, a step of removing the second metal layer to expose the trench forming portion of the resist pattern layer, and a step of removing the exposed trench forming portion of the resist pattern layer. 
         [0027]    It is preferred that the manufacturing method further includes a step of depositing a dielectric film on the surface of the first metal layer after the removing step of the resist pattern layer, and a step of depositing an upper electrode film on a surface of the dielectric film. 
         [0028]    It is also preferred that the manufacturing method further includes a step of removing a part of the resist pattern layer and a part of the electrode film, which are uncovered by the formed first and second metal layers, and a step of depositing a peripheral area layer on the second metal layer, and that the planarizing step includes planarizing top surfaces of the formed second metal layer and the deposited peripheral area layer just before the trench forming portion of the resist pattern layer is exposed. In this case, preferably, the step of depositing a peripheral area layer includes depositing an insulation layer. 
         [0029]    It is further preferred that the planarizing step includes planarizing a top surface of only the formed second metal layer just before the trench forming portion of the resist pattern layer is exposed. 
         [0030]    According to the present invention, a manufacturing method of a thin-film device, includes a step of depositing an electrode film on a substrate or on a base layer, a step of forming a resist pattern layer having a trench forming portion used to make a trench pattern, on the deposited electrode film, a step of forming a first metal layer made of a first metal material for filling spaces in the trench forming portion, by performing plating through the formed resist pattern layer using the deposited electrode film as an electrode, a step of shaving by an ashing process a top surface of the formed resist pattern layer, a step of forming a second metal layer made of a second metal material for covering at least the trench forming portion, by performing plating through the shaved resist pattern layer using the deposited electrode film as an electrode, the second metal material having a higher chemical activity than that of the first metal material, a step of planarizing top surfaces of the formed first and second metal layers just before the trench forming portion of the resist pattern layer is exposed, a step of removing the second metal layer to expose the trench forming portion of the resist pattern layer, and a step of removing the exposed trench forming portion of the resist pattern layer. 
         [0031]    It is preferred that the manufacturing method further includes a step of depositing a dielectric film on the surface of the first metal layer after the removing step of the resist pattern layer, and a step of depositing an upper electrode film on a surface of the dielectric film. 
         [0032]    It is also preferred that the manufacturing method further includes a step of removing a part of the resist pattern layer and a part of the electrode film, which are uncovered by the formed first and second metal layers, and a step of depositing a peripheral area layer on the second metal layer, and that the planarizing step includes planarizing top surfaces of the formed first and second metal layers and of the deposited peripheral area layer just before the trench forming portion of the resist pattern layer is exposed. In this case, preferably, the step of depositing a peripheral area layer includes depositing an insulation layer. 
         [0033]    It is further preferred that the planarizing step includes planarizing top surfaces of only the formed first and second metal layers just before the trench forming portion of the resist pattern layer is exposed. 
         [0034]    Further objects and advantages of the present invention will be apparent from the following description of the preferred embodiments of the invention as illustrated in the accompanying drawings. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS  
         [0035]      FIGS. 1   a  to  1   h  show sectional views schematically illustrating a part of processes in a first embodiment of a method of forming a metal trench pattern according to the present invention; 
           [0036]      FIGS. 2   a  to  2   j  show plane views schematically illustrating a part of processes in the first embodiment shown in  FIGS. 1   a  to  1   h;    
           [0037]      FIGS. 3   a  to  3   i  show sectional views schematically illustrating a part of processes in a second embodiment of a method of forming a metal trench pattern according to the present invention; 
           [0038]      FIGS. 4   a  to  4   l  show plane views schematically illustrating a part of processes in the second embodiment shown in  FIGS. 3   a  to  3   i;    
           [0039]      FIGS. 5   a  to  5   i  show sectional views schematically illustrating a part of processes in a third embodiment of a method of forming a metal trench pattern according to the present invention; 
           [0040]      FIGS. 6   a  to  6   l  show plane views schematically illustrating a part of processes in the third embodiment shown in  FIGS. 5   a  to  5   i;    
           [0041]      FIGS. 7   a  to  7   g  show sectional views schematically illustrating a part of processes in a fourth embodiment of a method of forming a metal trench pattern according to the present invention; 
           [0042]      FIGS. 8   a  to  8   i  show plane views schematically illustrating a part of processes in the fourth embodiment shown in  FIGS. 7   a  to  7   g;    
           [0043]      FIGS. 9   a  to  9   g  show sectional views schematically illustrating a part of processes in a fifth embodiment of a method of forming a metal trench pattern according to the present invention; 
           [0044]      FIGS. 10   a  to  10   i  show plane views schematically illustrating a part of processes in the fifth embodiment-shown in  FIGS. 9   a  to  9   g;    
           [0045]      FIGS. 11   a  to  11   e  show sectional views schematically illustrating a part of processes in a sixth embodiment of a method of forming a metal trench pattern according to the present invention; and 
           [0046]      FIGS. 12   a  to  12   g  show plane views schematically illustrating a part of processes in the sixth embodiment shown in  FIGS. 11   a  to  11   e.    
       
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0047]      FIGS. 1   a  to  1   h  and  FIGS. 2   a  to  2   j  schematically illustrate a part of processes in a first embodiment of a method of forming a metal trench pattern according to the present invention. In  FIGS. 1   a  to  1   h,  the structure of a trench-forming portion of a resist pattern layer is simplified for the sake of clarity. 
         [0048]    Hereinafter, in reference to these figures, a manufacturing process in this first embodiment will be described. Although a trench capacitor is fabricated as a thin-film device in this embodiment, the trench pattern forming method of this first embodiment can be utilized for fabricating another thin-film device such as Micro Electro Mechanical System (MEMS) for example. 
         [0049]    First, as shown in  FIG. 2   a,  a substrate  10  is provided. As for the substrate  10 , used is an alumina (Al 2 O 3 ) substrate with a diameter of 6 inches and a thickness of 2 mm in this embodiment. 
         [0050]    Then, as shown in  FIG. 2   b,  an electrode film  11 ′ that is a seed film for plating is deposited on the whole area of the substrate  10  or on a base layer formed on the substrate  10 . The deposition of the electrode film  11 ′ will be performed by sputtering or by vapor deposition of a metal material with a good conductivity such as nickel (Ni) or else to have a thickness of about 100 nm. 
         [0051]    Then, as shown in  FIGS. 1   a  and  2   c,  a resist pattern layer  12  is formed. This resist pattern layer  12  is constituted by a trench forming portion  12   a′  having a predetermined trench pattern and an outer frame portion  12   b.    
         [0052]    The resist pattern layer  12  will be formed as follows. First, a resist film having a thickness of about 21 μm is formed by performing spin-coat of a liquid resist material such as for example SIPR-7100 of Shin-Etsu Chemical Co., Ltd. Thereafter, the formed resist film is pre-baked, exposed and then developed with the following conditions. The pre-baking is 100° C.×60 seconds. As for a pattern exposure machine, for example NSR-i12TFH (λ=365 nm, NA=0.3, σ=0.3) of Nikon Corporation is used. Exposure amount is 350 mJ/cm 2 . PEB is 130° C.×360 seconds. As for a developer, an aqueous solution of 2.38% Tetramethylammonium hydroxide (TMAH) is used. The development is performed for 60 seconds×5 times. The shape of thus obtained resist pattern layer  12 , particularly that of the trench forming portion  12   a′,  is line and space (L/S) with a width of 5 μm. The outer frame portion  12   b  is formed around outer circumference of the trench forming portion  12   a′.    
         [0053]    Then, a metal layer  13 ′ with the trench pattern shown in  FIGS. 1   b  and  2   d  is formed by performing a flame plating using this resist pattern layer  12  and the electrode film  11 ′. The frame plating is conducted for a long period of time so that nickel (Ni) or other metal material for example is plated using a Ni-bath (Watt bath) for example to have a thickness of about 21 μm, and that not only spaces in the trench forming portion  12   a′  of the resist pattern layer  12  is filled with the metal layer  13 ′ but also the trench forming portion  12   a′  is completely covered by the metal layer  13 ′, in other words, the trench forming portion  12   a′  is buried in the metal layer  13 ′. Instead of a long time period of plating or with a long time period of plating, increased plating current and/or increased metal-ion density of plating solution may be employed. 
         [0054]    Then, as shown in  FIGS. 1   c  and  2   e,  the outer frame portion  12   b  of the resist pattern  12 , which is uncovered by the metal layer  13 ′ is removed. This removal may be performed by immersing the substrate into an organic solution such as for example propanol isopropyl alcohol (IPL) or N-methyl-2-pyrrolydone (NMP) and by rocking the immersed substrate. 
         [0055]    Then, as shown in  FIGS. 1   d  and  2   f,  an area of the electrode film  11 ′, which is uncovered by the metal layer  13 ′ is removed by ion milling to partially remain the electrode film  11  only under the metal layer  13 ′. In this embodiment, the ion milling may be performed using a milling device such as for example IML of Hitachi, Ltd. Argon (Ar) gas may be used as for the milling gas and a milling current of 300 mA may be used. Instead of ion milling, a reactive ion etching (RIE) or a wet etching may be performed. 
         [0056]    Then, as shown in  FIGS. 1   e  and  2   g,  an insulation layer  14 ′ is deposited as for a peripheral area layer, over the metal layer  13 ′. The insulation layer  14 ′ may be formed by performing sputtering of an insulation material such as for example Al 2 O 3  to have a thickness of about 25 μm. In this embodiment, the sputtering may be performed using a bias-sputtering device of for example Hitachi, Ltd. A target of Al 2 O 3  may be used and Ar gas may be used as for the sputtering gas. 
         [0057]    Thereafter, surfaces of the deposited insulation layer  14 ′, of the metal layer  13 ′, and of the trench forming portion  12   a′  of the resist pattern are planarized together by performing a chemical mechanical polishing (CMP). In this embodiment, the CMP may be performed using a CMP device such as for example MIRRA of Applied Materials Inc. In the CMP process, a urethane pad is used with aluminum slurry having a grain diameter of 250 nm. This planarization process will be continued until the trench forming portion  12   a′  of the resist pattern layer is exposed. As a result, as shown in  FIGS. 1   f  and  2   h,  an insulation layer  14 , a metal layer  13 , and a trench forming portion  12   a  of the resist pattern, with top surfaces planarized flat together in the same plane. 
         [0058]    Then, as shown in  FIGS. 1   g  and  2   i,  the trench forming portion  12   a  of the resist pattern is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0059]    According to the above-mentioned processes, the metal layer  13  having a trench pattern of a plurality of convex portions or pillars arranged to sandwich concave portions or recesses with a depth of about 20 μm, surrounded by the insulation layer  14  that is a peripheral area layer, can be obtained. The convex portions or pillars of the metal layer  13  are electrically conducted with each other through the electrode film  11 . Particularly, in this embodiment, since the concave portions or recesses are completely filled with the resist layer until the CMP planarization is finished, it is possible to prevent slurry used in CMP or lapped material from entering into the concave portions or recesses of the trench pattern and also to prevent the convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between from being deformed or toppled over. 
         [0060]    After forming such trench pattern, in this embodiment, a dielectric film  15  is formed on top surfaces of the metal layer  13  and the insulation layer  14  by depositing thereon, by sputtering, a dielectric material such as for example Al 2 O 3  to have a thickness of about 80 nm. Then, an upper electrode film  16  is formed by depositing thereon, by sputtering, two conductive materials such as for example chrome (Cr) and copper (Cu) to have a thickness of about 10 nm and a thickness of about 500 nm, respectively. Thereafter, electrode pads  17  and  18  that are electrically connected to the metal layer  13  constituting a lower electrode and to the upper electrode film  16 , respectively, are formed. As a result, as shown in  FIGS. 1   h  and  2   j,  a trench capacitor is fabricated. 
         [0061]    As described in detail, according to this embodiment, because the trench pattern is formed in a correct shape without deformation, a trench capacitor with high accuracy and high quality can be provided. 
         [0062]      FIGS. 3   a  to  3   i  and  FIGS. 4   a  to  4   l  schematically illustrate a part of processes in a second embodiment of a method of forming a metal trench pattern according to the present invention. In  FIGS. 3   a  to  3   i,  the structure of a trench-forming portion of a resist pattern layer is simplified for the sake of clarity. In this embodiment, the similar components as these in the first embodiment are represented with the same reference numerals. 
         [0063]    Hereinafter, in reference to these figures, a manufacturing process in this second embodiment will be described. Although a trench capacitor is fabricated as a thin-film device in this embodiment, the trench pattern forming method of this second embodiment can be utilized for fabricating another thin-film device such as MEMS for example. 
         [0064]    First, as shown in  FIG. 4   a,  a substrate  10  is provided. As for the substrate  10 , used is an Al 2 O 3  substrate with a diameter of 6 inches and a thickness of 2 mm in this embodiment. 
         [0065]    Then, as shown in  FIG. 4   b,  an electrode film  11 ′ that is a seed film for plating is deposited on the whole area of the substrate  10  or on a base layer formed on the substrate  10 . The deposition of the electrode film  11 ′ will be performed by sputtering or by vapor deposition of a metal material with a good conductivity such as Ni or else to have a thickness of about 100 nm. 
         [0066]    Then, as shown in  FIGS. 3   a  and  4   c,  a resist pattern layer  12  is formed. This resist pattern layer  12  is constituted by a trench forming portion  12   a  having a predetermined trench pattern and an outer frame portion  12   b.    
         [0067]    The resist pattern layer  12  will be formed as follows. First, a resist film having a thickness of about 21 μm is formed by performing spin-coat of a liquid resist material such as for example SIPR-7100 of Shin-Etsu Chemical Co., Ltd. Thereafter, the formed resist film is pre-baked, exposed and then developed with the following conditions. The pre-baking is 100° C.×60 seconds. As for a pattern exposure machine, for example NSR-i12TFH (λ=365 nm, NA=0.3, σ=0.3) of Nikon Corporation is used. Exposure amount is 350 mJ/cm 2 . PEB is 130° C.×360 seconds. As for a developer, an aqueous solution of 2.38% TMAH is used. The development is performed for 60 seconds×5 times. The shape of thus obtained resist pattern layer  12 , particularly that of the trench forming portion  12   a,  is line and space (L/S) with a width of 5 μm. The outer frame portion  12   b  is formed around outer circumference of the trench forming portion  12   a.    
         [0068]    Then, a first metal layer  33  with the trench pattern shown in  FIGS. 3   b  and  4   d  is formed by performing a flame plating using this resist pattern layer  12  and the electrode film  11 ′. This frame plating is performed so that Ni or other metal material for example is plated using a Watt bath for example to have a thickness of about 20 μm, and that spaces in the trench forming portion  12   a  of the resist pattern layer  12  are partially filled with the first metal layer  33  but top surfaces of the first metal layer  33  are lower than a top of the trench forming portion  12   a,  in other words, the top end of the trench forming portion  12   a  is exposed. 
         [0069]    Then, a second metal layer or sacrifice layer  39 ′ shown in  FIGS. 3   c  and  4   e  is formed by performing a flame plating using the same electrode film  11 ′ used in the flame plating of the first metal layer  33  and the resist pattern layer  12 . This frame plating is performed so that Cu or other metal material for example is plated using a copper sulfate plating-bath for example. Also, this plating is performed so that the first metal layer  33  and the trench forming portion  12   a′  of the resist pattern layer are completely covered by the second metal layer  39 ′. It is necessary to select for the second metal layer  39 ′ a metal material with a higher chemical activity or a higher ionization tendency than that of the first metal layer  33 . This is because to prevent the first metal layer  33  from dissolving when the second metal layer  39 ′ is dissolved and removed by a wet etching. 
         [0070]    Then, as shown in  FIG. 4   f,  the outer frame portion  12   b  of the resist pattern  12 , which is uncovered by the second metal layer  39 ′ is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0071]    Then, as shown in  FIGS. 3   d  and  4   g,  an area of the electrode film  11 ′, which is uncovered by the second metal layer  39 ′ is removed by ion milling to partially remain the electrode film  11  only under the first metal layer  33  and the second metal layer  39 ′. In this embodiment, the ion milling may be performed using a milling device such as for example IML of Hitachi, Ltd. Ar gas may be used as for the milling gas and a milling current of 300 mA may be used. Instead of ion milling, an RIE or a wet etching may be performed. 
         [0072]    Then, as shown in  FIGS. 3   e  and  4   h,  an insulation layer  14 ′ is deposited as for a peripheral area layer, over the second metal layer  39 ′. The insulation layer  14 ′ may be formed by performing sputtering of an insulation material such as for example Al 2 O 3  to have a thickness of about 25 μm. In this embodiment, the sputtering may be performed using a bias-sputtering device of for example Hitachi, Ltd. A target of Al 2 O 3  may be used and Ar gas may be used as for the sputtering gas. 
         [0073]    Thereafter, surfaces of the deposited insulation layer  14 ′ and of the second metal layer  39 ′ are planarized together by performing a CMP. In this embodiment, the CMP may be performed using a CMP device such as for example MIRRA of Applied Materials Inc. In the CMP process, a urethane pad is used with aluminum slurry having a grain diameter of 250 nm. This planarization process will be finished just before the trench forming portion  12   a′  of the resist pattern layer is exposed. As a result, as shown in  FIGS. 3   f  and  4   i,  an insulation layer  14  and a second metal layer  39 , with top surfaces planarized flat together in the same plane. 
         [0074]    Then, as shown in  FIGS. 3   g  and  4   j,  only the second metal layer  39  is dissolved and removed by a wet etching. This removal process may be performed by using an etching solution of aqueous ammonia and an ammonium persulfate so that the first metal layer  33  is not dissolved. 
         [0075]    Then, as shown in  FIGS. 3   h  and  4   k,  the trench forming portion  12   a  of the resist pattern is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0076]    According to the above-mentioned processes, the first metal layer  33  having a trench pattern of a plurality of convex portions or pillars arranged to sandwich concave portions or recesses with a depth of about 20 μm, surrounded by the insulation layer  14  that is a peripheral area layer, can be obtained. The convex portions or pillars of the first metal layer  33  are electrically conducted with each other through the electrode film  11 . Particularly, in this embodiment, since the concave portions or recesses are filled with the second metal layer and the resist layer until the CMP planarization is finished, it is possible to prevent slurry used in CMP or lapped material from entering into the concave portions or recesses of the trench pattern and also to securely support the convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between so as to effectively prevent these convex portions or pillars from being deformed or toppled over. According to this embodiment, however, the top surfaces of the first metal layer  33  and the insulation layer  14  that is the peripheral area layer are uneven as shown  FIG. 3   h.    
         [0077]    After forming such trench pattern, in this embodiment, a dielectric film  15  is formed on the top surfaces of the first metal layer  33  and the insulation layer  14  by depositing thereon, by sputtering, a dielectric material such as for example Al 2 O 3  to have a thickness of about 80 nm. Then, an upper electrode film  16  is formed by depositing thereon, by sputtering, two conductive materials such as for example Cr and Cu to have a thickness of about 10 nm and a thickness of about 500 nm, respectively. Thereafter, electrode pads  17  and  18  that are electrically connected to the first metal layer  33  constituting a lower electrode and to the upper electrode film  16 , respectively, are formed. As a result, as shown in  FIGS. 3   i  and  4   l,  a trench capacitor is fabricated. 
         [0078]    As described in detail, according to this embodiment, because the trench pattern is formed in a correct shape without deformation, a trench capacitor with high accuracy and high quality can be provided. 
         [0079]      FIGS. 5   a  to  5   i  and  FIGS. 6   a  to  6   l  schematically illustrate a part of processes in a third embodiment of a method of forming a metal trench pattern according to the present invention. In  FIGS. 5   a  to  5   i,  the structure of a trench-forming portion of a resist pattern layer is simplified for the sake of clarity. In this embodiment, the similar components as these in the first embodiment are represented with the same reference numerals. 
         [0080]    Hereinafter, in reference to these figures, a manufacturing process in this third embodiment will be described. Although a trench capacitor is fabricated as a thin-film device in this embodiment, the trench pattern forming method of this second embodiment can be utilized for fabricating another thin-film device such as MEMS for example. 
         [0081]    First, as shown in  FIG. 6   a,  a substrate  10  is provided. As for the substrate  10 , used is an Al 2 O 3  substrate with a diameter of 6 inches and a thickness of 2 mm in this embodiment. 
         [0082]    Then, as shown in  FIG. 6   b,  an electrode film  11 ′ that is a seed film for plating is deposited on the whole area of the substrate  10  or on a base layer formed on the substrate  10 . The deposition of the electrode film  11 ′ will be performed by sputtering or by vapor deposition of a metal material with a good conductivity such as Ni or else to have a thickness of about 100 nm. 
         [0083]    Then, as shown in  FIGS. 5   a  and  6   c,  a resist pattern layer  12  is formed. This resist pattern layer  12  is constituted by a trench forming portion  12   a′  having a predetermined trench pattern and an outer frame portion  12   b′.    
         [0084]    The resist pattern layer  12  will be formed as follows. First, a resist film having a thickness of about 21 μm is formed by performing spin-coat of a liquid resist material such as for example SIPR-7100 of Shin-Etsu Chemical Co., Ltd. Thereafter, the formed resist film is pre-baked, exposed and then developed with the following conditions. The pre-baking is 100° C.×60 seconds. As for a pattern exposure machine, for example NSR-i12TFH (λ=365 nm, NA=0.3, σ=0.3) of Nikon Corporation is used. Exposure amount is 350 mJ/cm 2 . PEB is 130° C.×360 seconds. As for a developer, an aqueous solution of 2.38% TMAH is used. The development is performed for 60 seconds×5 times. The shape of thus obtained resist pattern layer  12 , particularly that of the trench forming portion  12   a,  is line and space (L/S) with a width of 5 μm. The outer frame portion  12   b′  is formed around outer circumference of the trench forming portion  12   a′.    
         [0085]    Then, a first metal layer  33  with the trench pattern shown in  FIGS. 5   b  and  6   d  is formed by performing a flame plating using this resist pattern layer  12  and the electrode film  11 ′. This frame plating is performed so that Ni or other metal material for example is plated using a Watt bath for example to have a thickness of about 20 μm, and that spaces in the trench forming portion  12   a′  of the resist pattern layer  12  are partially filled with the first metal layer  33  but top surfaces of the first metal layer  33  are lower than a top of the trench forming portion  12   a′,  in other words, the top end of the trench forming portion  12   a′  is exposed. 
         [0086]    Then, as shown in  FIG. 5   c,  a trench forming portion  12   a  and an outer frame portion  12   b  are obtained by performing an ashing process to reduce the thickness of the resist pattern layer  12  such that a top surface of the resist pattern layer  12  becomes lower than the top surfaces of the first metal layer  33 . This ashing process is executed using for example an ashing device such as MAS of Alcantech Co., Inc. Oxygen (O 2 ) gas may be used as for the ashing gas. 
         [0087]    Then, a second metal layer or sacrifice layer  39 ′ shown in  FIGS. 5   d  and  6   e  is formed by performing a flame plating using the same electrode film  11 ′ used in the flame plating of the first metal layer  33  and the resist pattern layer  12 . This frame plating is performed so that Cu or other metal material for example is plated using a copper sulfate plating-bath for example. Also, this plating is performed so that the first metal layer  33  and the trench forming portion  12   a  of the resist pattern layer are completely covered by the second metal layer  39 ′. It is necessary to select for the second metal layer  39 ′ a metal material with a higher chemical activity or a higher ionization tendency than that of the first metal layer  33 . This is because to prevent the first metal layer  33  from dissolving when the second metal layer  39 ′ is dissolved and removed by a wet etching. 
         [0088]    Then, as shown in  FIG. 6   f,  the outer frame portion  12   b  of the resist pattern  12 , which is uncovered by the second metal layer  39 ′ is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0089]    Then, as shown in  FIGS. 5   e  and  6   g,  an area of the electrode film  11 ′, which is uncovered by the second metal layer  39 ′ is removed by ion milling to partially remain the electrode film  11  only under the first metal layer  33  and the second metal layer  39 ′. In this embodiment, the ion milling may be performed using a milling device such as for example IML of Hitachi, Ltd. Ar gas may be used as for the milling gas and a milling current of 300 mA may be used. Instead of ion milling, an RIE or a wet etching may be performed. 
         [0090]    Then, as shown in  FIGS. 5   f  and  6   h,  an insulation layer  14 ′ is deposited as for a peripheral area layer, over the second metal layer  39 ′. The insulation layer  14 ′ may be formed by performing sputtering of an insulation material such as for example Al 2 O 3  to have a thickness of about 25 μm. In this embodiment, the sputtering may be performed using a bias-sputtering device of for example Hitachi, Ltd. A target of Al 2 O 3  may be used and Ar gas may be used as for the sputtering gas. 
         [0091]    Thereafter, surfaces of the deposited insulation layer  14 ′ and of the second metal layer  39 ′ are planarized together by performing a CMP. In this embodiment, the CMP may be performed using a CMP device such as for example MIRRA of Applied Materials Inc. In the CMP process, a urethane pad is used with aluminum slurry having a grain diameter of 250 nm. This planarization process will be continued until the first metal layer  33  is exposed. As a result, as shown in  FIGS. 5   g  and  6   i,  an insulation layer  14 , a first metal layer  33  and a second metal layer  39 , with top surfaces planarized flat together in the same plane. 
         [0092]    Then, as shown in  FIG. 6   j,  only the second metal layer  39  is dissolved and removed by a wet etching. This removal process may be performed by using an etching solution of aqueous ammonia and an ammonium persulfate so that the first metal layer  33  is not dissolved. 
         [0093]    Then, as shown in  FIGS. 5   h  and  5   k,  the trench forming portion  12   a  of the resist pattern is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0094]    According to the above-mentioned processes, the first metal layer  33  having a trench pattern of a plurality of convex portions or pillars arranged to sandwich concave portions or recesses with a depth of about 20 μm, surrounded by the insulation layer  14  that is a peripheral area layer, can be obtained. The convex portions or pillars of the first metal layer  33  are electrically conducted with each other through the electrode film  11 . Particularly, in this embodiment, since the concave portions or recesses are filled with the second metal layer and the resist layer until the CMP planarization is finished, it is possible to prevent slurry used in CMP or lapped material from entering into the concave portions or recesses of the trench pattern and also to securely support the convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between so as to effectively prevent these convex portions or pillars from being deformed or toppled over. According to this embodiment, the top surfaces of the first metal layer  33  and the insulation layer  14  that is the peripheral area layer are even as shown  FIG. 5   h.    
         [0095]    After forming such trench pattern, in this embodiment, a dielectric film  15  is formed on the top surfaces of the first metal layer  33  and the insulation layer  14  by depositing thereon, by sputtering, a dielectric material such as for example Al 2 O 3  to have a thickness of about 80 nm. Then, an upper electrode film  16  is formed by depositing thereon, by sputtering, two conductive materials such as for example Cr and Cu to have a thickness of about 10 nm and a thickness of about 500 nm, respectively. Thereafter, electrode pads  17  and  18  that are electrically connected to the first metal layer  33  constituting a lower electrode and to the upper electrode film  16 , respectively, are formed. As a result, as shown in  FIGS. 5   i  and  6   l,  a trench capacitor is fabricated. 
         [0096]    As described in detail, according to this embodiment, because the trench pattern is formed in a correct shape without deformation, a trench capacitor with high accuracy and high quality can be provided. 
         [0097]      FIGS. 7   a  to  7   g  and  FIGS. 8   a  to  8   i  schematically illustrate a part of processes in a fourth embodiment of a method of forming a metal trench pattern according to the present invention. In  FIGS. 7   a  to  7   g,  the structure of a trench-forming portion of a resist pattern layer is simplified for the sake of clarity. In this embodiment, the similar components as these in the first embodiment are represented with the same reference numerals. 
         [0098]    Hereinafter, in reference to these figures, a manufacturing process in this fourth embodiment will be described. Although a trench capacitor is fabricated as a thin-film device in this embodiment, the trench pattern forming method of this second embodiment can be utilized for fabricating another thin-film device such as MEMS for example. 
         [0099]    First, as shown in  FIG. 8   a,  a substrate  10  is provided. As for the substrate  10 , used is an Al 2 O 3  substrate with a diameter of 6 inches and a thickness of 2 mm in this embodiment. 
         [0100]    Then, as shown in  FIG. 8   b,  an electrode film  11  that is a seed film for plating is deposited on the whole area of the substrate  10  or on a base layer formed on the substrate  10 . The deposition of the electrode film  11  will be performed by sputtering or by vapor deposition of a metal material with a good conductivity such as Ni or else to have a thickness of about 100 nm. 
         [0101]    Then, as shown in  FIGS. 7   a  and  8   c,  a resist pattern layer  12  is formed. This resist pattern layer  12  is constituted by only a trench forming portion  12   a  having a predetermined trench pattern. 
         [0102]    The resist pattern layer  12  will be formed as follows. First, a resist film having a thickness of about 21 μm is formed by performing spin-coat of a liquid resist material such as for example SIPR-7100 of Shin-Etsu Chemical Co., Ltd. Thereafter, the formed resist film is pre-baked, exposed and then developed with the following conditions. The pre-baking is 100° C.×60 seconds. As for a pattern exposure machine, for example NSR-i12TFH (λ=365 nm, NA=0.3, σ=0.3) of Nikon Corporation is used. Exposure amount is 350 mJ/cm 2 . PEB is 130° C.×360 seconds. As for a developer, an aqueous solution of 2.38% TMAH is used. The development is performed for 60 seconds×5 times. The shape of thus obtained trench forming portion  12   a  of the resist pattern layer  12  is line and space (L/S) with a width of 5 μm. 
         [0103]    Then, a first metal layer  73  having the trench pattern shown in  FIGS. 7   b  and  8   d  and extending to its peripheral area is formed by performing a flame plating using this resist pattern layer  12  and the electrode film  11 . This frame plating is performed so that Ni or other metal material for example is plated using a Watt bath for example to have a thickness of about 20 μm, and that spaces in the trench forming portion  12   a  of the resist pattern layer  12  are partially filled with the first metal layer  73  but top surfaces of the first metal layer  73  are lower than a top of the trench forming portion  12   a,  in other words, the top end of the trench forming portion  12   a  is exposed. 
         [0104]    Then, a second metal layer or sacrifice layer  79 ′ shown in  FIGS. 7   c  and  8   e  is formed by performing a flame plating using the same electrode film  11 ′ used in the flame plating of the first metal layer  73  and the resist pattern layer  12 . This frame plating is performed so that Cu or other metal material for example is plated using a copper sulfate plating-bath for example. Also, this plating is performed so that the first metal layer  73  and the trench forming portion  12   a  of the resist pattern layer are completely covered by the second metal layer  79 ′. It is necessary to select for the second metal layer  79 ′ a metal material with a higher chemical activity or a higher ionization tendency than that of the first metal layer  73 . This is because to prevent the first metal layer  73  from dissolving when the second metal layer  79 ′ is dissolved and removed by a wet etching. 
         [0105]    Then, a surface of the second metal layer  79 ′ is planarized by performing a CMP. In this embodiment, the CMP may be performed using a CMP device such as for example MIRRA of Applied Materials Inc. In the CMP process, a urethane pad is used with aluminum slurry having a grain diameter of 250 nm. This planarization process will be finished just before the trench forming portion  12   a  of the resist pattern layer is exposed. As a result, as shown in  FIGS. 7   d  and  8   f,  a second metal layer  79 , with a flat top surface. 
         [0106]    Then, as shown in  FIGS. 7   e  and  8   g,  only the second metal layer  79  is dissolved and removed by a wet etching. This removal process may be performed by using an etching solution of aqueous ammonia and an ammonium persulfate so that the first metal layer  73  is not dissolved. 
         [0107]    Then, as shown in  FIGS. 7   f  and  8   h,  the trench forming portion  12   a  of the resist pattern is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0108]    According to the above-mentioned processes, the first metal layer  73  having a trench pattern of a plurality of convex portions or pillars arranged to sandwich concave portions or recesses with a depth of about 20 μm, surrounded by its peripheral area part, can be obtained. The convex portions or pillars of the first metal layer  73  are electrically conducted with each other through the electrode film  11 . Particularly, in this embodiment, since the concave portions or recesses are filled with the resist pattern layer until the CMP planarization is finished, it is possible to prevent slurry used in CMP or lapped material from entering into the concave portions or recesses of the trench pattern. Also, since the second metal layer is formed on the resist pattern layer and the first metal layer, it is possible to securely support the convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between so as to effectively prevent these convex portions or pillars from being deformed or toppled over. According to this embodiment, the top surfaces of the convex portions or pillars and the peripheral area part of the first metal layer  73  are even as shown  FIG. 7   f.    
         [0109]    After forming such trench pattern, in this embodiment, a dielectric film  15  is formed on the top surface of the first metal layer  73  by depositing thereon, by sputtering, a dielectric material such as for example Al 2 O 3  to have a thickness of about 80 nm. Then, an upper electrode film  16  is formed by depositing thereon, by sputtering, two conductive materials such as for example Cr and Cu to have a thickness of about 10 nm and a thickness of about 500 nm, respectively. Thereafter, electrode pads  17  and  18  that are electrically connected to the first metal layer  73  constituting a lower electrode and to the upper electrode film  16 , respectively, are formed. As a result, as shown in  FIGS. 7   g  and  8   i,  a trench capacitor is fabricated. 
         [0110]    As described in detail, according to this embodiment, because the trench pattern is formed in a correct shape without deformation, a trench capacitor with high accuracy and high quality can be provided. 
         [0111]      FIGS. 9   a  to  9   g  and  FIGS. 10   a  to  10   i  schematically illustrate a part of processes in a fifth embodiment of a method of forming a metal trench pattern according to the present invention. In  FIGS. 9   a  to  9   g,  the structure of a trench-forming portion of a resist pattern layer is simplified for the sake of clarity. In this embodiment, the similar components as these in the first embodiment are represented with the same reference numerals. 
         [0112]    Hereinafter, in reference to these figures, a manufacturing process in this fifth embodiment will be described. Although a trench capacitor is fabricated as a thin-film device in this embodiment, the trench pattern forming method of this second embodiment can be utilized for fabricating another thin-film device such as MEMS for example. 
         [0113]    First, as shown in  FIG. 10   a,  a substrate  10  is provided. As for the substrate  10 , used is an Al 2 O 3  substrate with a diameter of 6 inches and a thickness of 2 mm in this embodiment. 
         [0114]    Then, as shown in  FIG. 10   b,  an electrode film  11  that is a seed film for plating is deposited on the whole area of the substrate  10  or on a base layer formed on the substrate  10 . The deposition of the electrode film  11  will be performed by sputtering or by vapor deposition of a metal material with a good conductivity such as Ni or else to have a thickness of about 100 nm. 
         [0115]    Then, as shown in  FIGS. 9   a  and  10   c,  a resist pattern layer  12  is formed. This resist pattern layer  12  is constituted by only a trench forming portion  12   a′  having a predetermined trench pattern. 
         [0116]    The resist pattern layer  12  will be formed as follows. First, a resist film having a thickness of about 21 μm is formed by performing spin-coat of a liquid resist material such as for example SIPR-7100 of Shin-Etsu Chemical Co., Ltd. Thereafter, the formed resist film is pre-baked, exposed and then developed with the following conditions. The pre-baking is 100° C.×60 seconds. As for a pattern exposure machine, for example NSR-i12TFH (λ=365 nm, NA=0.3, σ=0.3) of Nikon Corporation is used. Exposure amount is 350 mJ/cm 2 . PEB is 130° C.×360 seconds. As for a developer, an aqueous solution of 2.38% TMAH is used. The development is performed for 60 seconds×5 times. The shape of thus obtained trench forming portion  12   a′  of the resist pattern layer  12  is line and space (L/S) with a width of 5 μm. 
         [0117]    Then, a first metal layer  73  having the trench pattern shown in  FIGS. 9   b  and  10   d  and extending to its peripheral area is formed by performing a flame plating using this resist pattern layer  12  and the electrode film  11 . This frame plating is performed so that Ni or other metal material for example is plated using a Watt bath for example to have a thickness of about 20 μm, and that spaces in the trench forming portion  12   a′  of the resist pattern layer  12  are partially filled with the first metal layer  73  but top surfaces of the first metal layer  73  are lower than a top of the trench forming portion  12   a′,  in other words, the top end of the trench forming portion  12   a′  is exposed. 
         [0118]    Then, as shown in  FIG. 9   c,  a trench forming portion  12   a  is obtained by performing an ashing process to reduce the thickness of the resist pattern layer  12  such that a top surface of trench forming portion of the resist pattern layer  12  becomes lower than the top surfaces of the first metal layer  33 . This ashing process is executed using for example an ashing device such as MAS of Alcantech Co., Inc. O 2  gas may be used as for the ashing gas. 
         [0119]    Then, a second metal layer or sacrifice layer  79 ′ shown in  FIGS. 9   c  and  10   e  is formed by performing a flame plating using the same electrode film  11  used in the flame plating of the first metal layer  73  and the resist pattern layer  12 . This frame plating is performed so that Cu or other metal material for example is plated using a copper sulfate plating-bath for example. Also, this plating is performed so that the first metal layer  73  and the trench forming portion  12   a  of the resist pattern layer are completely covered by the second metal layer  79 ′. It is necessary to select for the second metal layer  79 ′ a metal material with a higher chemical activity or a higher ionization tendency than that of the first metal layer  73 . This is because to prevent the first metal layer  73  from dissolving when the second metal layer  79 ′ is dissolved and removed by a wet etching. 
         [0120]    Then, a surface of the second metal layer  79 ′ is planarized by performing a CMP. In this embodiment, the CMP may be performed using a CMP device such as for example MIRRA of Applied Materials Inc. In the CMP process, a urethane pad is used with aluminum slurry having a grain diameter of 250 nm. This planarization process will be continued until the first metal layer  73  is exposed. As a result, as shown in  FIGS. 9   e  and  10   f,  a first metal layer  73  and a second metal layer  79 , with top surfaces planarized flat together in the same plane. 
         [0121]    Then, as shown in  FIG. 10   g,  only the second metal layer  79  is dissolved and removed by a wet etching. This removal process may be performed by using an etching solution of aqueous ammonia and an ammonium persulfate so that the first metal layer  73  is not dissolved. 
         [0122]    Then, as shown in  FIGS. 9   f  and  10   h,  the trench forming portion  12   a  of the resist pattern is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0123]    According to the above-mentioned processes, the first metal layer  73  having a trench pattern of a plurality of convex portions or pillars arranged to sandwich concave portions or recesses with a depth of about 20 μm, surrounded by its peripheral area part, can be obtained. The convex portions or pillars of the first metal layer  73  are electrically conducted with each other through the electrode film  11 . Particularly, in this embodiment, since the concave portions or recesses are filled with the second metal layer and the resist pattern layer until the CMP planarization is finished, it is possible to prevent slurry used in CMP or lapped material from entering into the concave portions or recesses of the trench pattern. Since not only the resist layer but also the second metal layer is filled in the concave portions or recesses, it is possible to securely support the convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between so as to effectively prevent these convex portions or pillars from being deformed or toppled over. According to this embodiment, the top surfaces of the convex portions or pillars and the peripheral area part of the first metal layer  73  are even as shown  FIG. 9   f.    
         [0124]    After forming such trench pattern, in this embodiment, a dielectric film  15  is formed on the top surface of the first metal layer  73  by depositing thereon, by sputtering, a dielectric material such as for example Al 2 O 3  to have a thickness of about 80 nm. Then, an upper electrode film  16  is formed by depositing thereon, by sputtering, two conductive materials such as for example Cr and Cu to have a thickness of about 10 nm and a thickness of about 500 nm, respectively. Thereafter, electrode pads  17  and  18  that are electrically connected to the first metal layer  73  constituting a lower electrode and to the upper electrode film  16 , respectively, are formed. As a result, as shown in  FIGS. 9   g  and  10   i,  a trench capacitor is fabricated. 
         [0125]    As described in detail, according to this embodiment, because the trench pattern is formed in a correct shape without deformation, a trench capacitor with high accuracy and high quality can be provided. 
         [0126]      FIGS. 11   a  to  11   e  and  FIGS. 12   a  to  12   g  schematically illustrate a part of processes in a sixth embodiment of a method of forming a metal trench pattern according to the present invention. In  FIGS. 11   a  to  11   e,  the structure of a trench-forming portion of a resist pattern layer is simplified for the sake of clarity. In this embodiment, the similar components as these in the first embodiment are represented with the same reference numerals. 
         [0127]    Hereinafter, in reference to these figures, a manufacturing process in this sixth embodiment will be described. Although a trench capacitor is fabricated as a thin-film device in this embodiment, the trench pattern forming method of this second embodiment can be utilized for fabricating another thin-film device such as MEMS for example. 
         [0128]    First, as shown in  FIG. 12   a,  a substrate  10  is provided. As for the substrate  10 , used is an Al 2 O 3  substrate with a diameter of 6 inches and a thickness of 2 mm in this embodiment. 
         [0129]    Then, as shown in  FIG. 12   b,  an electrode film  11  that is a seed film for plating is deposited on the whole area of the substrate  10  or on a base layer formed on the substrate  10 . The deposition of the electrode film  11  will be performed by sputtering or by vapor deposition of a metal material with a good conductivity such as Ni or else to have a thickness of about 100 nm. 
         [0130]    Then, as shown in  FIGS. 11   a  and  12   c,  a resist pattern layer  12  is formed. This resist pattern layer  12  is constituted by only a trench forming portion  12   a′  having a predetermined trench pattern. 
         [0131]    The resist pattern layer  12  will be formed as follows. First, a resist film having a thickness of about 21 μm is formed by performing spin-coat of a liquid resist material such as for example SIPR-7100 of Shin-Etsu Chemical Co., Ltd. Thereafter, the formed resist film is pre-baked, exposed and then developed with the following conditions. The pre-baking is 100° C.×60 seconds. As for a pattern exposure machine, for example NSR-i12TFH (λ=365 nm, NA=0.3, σ=0.3) of Nikon Corporation is used. Exposure amount is 350 mJ/cm 2 . PEB is 130° C.×360 seconds. As for a developer, an aqueous solution of 2.38% TMAH is used. The development is performed for 60 seconds×5 times. The shape of thus obtained trench forming portion  12   a′  of the resist pattern layer  12  is line and space (L/S) with a width of 5 μm. 
         [0132]    Then, a metal layer  113 ′ having the trench pattern shown in  FIGS. 11   b  and  12   d  and extending to its peripheral area is formed by performing a flame plating using this resist pattern layer  12  and the electrode film  11 . This frame plating is conducted for a long period of time so that Ni or other metal material for example is plated using a Watt bath for example to have a thickness of about 21 μm, and that not only spaces in the trench forming portion  12   a′  of the resist pattern layer  12  is filled with the metal layer  113 ′ but also the trench forming portion  12   a′  is completely covered by the metal layer  113 ′, in other words, the trench forming portion  12   a′  is buried in the metal layer  113 ′. Instead of a long time period of plating or with a long time period of plating, increased plating current and/or increased metal-ion density of plating solution may be employed. 
         [0133]    Then, a surface of the metal layer  113 ′ is planarized by performing a CMP. In this embodiment, the CMP may be performed using a CMP device such as for example MIRRA of Applied Materials Inc. In the CMP process, a urethane pad is used with aluminum slurry having a grain diameter of 250 nm. This planarization process will be continued until the trench forming portion  12   a′  of the resist pattern layer  12  is exposed. As a result, as shown in  FIGS. 11   c  and  12   e,  a metal layer  113  and a trench forming portion  12   a  of the resist pattern layer, with top surfaces planarized flat together in the same plane. 
         [0134]    Then, as shown in  FIGS. 11   d  and  12   f,  the trench forming portion  12   a  of the resist pattern is removed. This removal may be performed by immersing the substrate into an organic solution such as for example IPL or NMP and by rocking the immersed substrate. 
         [0135]    According to the above-mentioned processes, the metal layer  113  having a trench pattern of a plurality of convex portions or pillars arranged to sandwich concave portions or recesses with a depth of about 20 μm, surrounded by its peripheral area part, can be obtained. The convex portions or pillars of the metal layer  113  are electrically conducted with each other through the electrode film  11 . Particularly, in this embodiment, since the concave portions or recesses are filled with the resist pattern layer until the CMP planarization is finished, it is possible to prevent slurry used in CMP or lapped material from entering into the concave portions or recesses of the trench pattern, and to prevent the convex portions or pillars that configure the trench pattern by sandwiching the concave portions or recesses there between from being deformed or toppled over. According to this embodiment, the top surfaces of the convex portions or pillars and the peripheral area part of the metal layer  113  are even as shown  FIG. 11   d.    
         [0136]    After forming such trench pattern, in this embodiment, a dielectric film  15  is formed on the top surface of the metal layer  113  by depositing thereon, by sputtering, a dielectric material such as for example Al 2 O 3  to have a thickness of about 80 nm. Then, an upper electrode film  16  is formed by depositing thereon, by sputtering, two conductive materials such as for example Cr and Cu to have a thickness of about 10 nm and a thickness of about 500 nm, respectively. Thereafter, electrode pads  17  and  18  that are electrically connected to the metal layer  113  constituting a lower electrode and to the upper electrode film  16 , respectively, are formed. As a result, as shown in  FIGS. 11   e  and  11   g,  a trench capacitor is fabricated. 
         [0137]    As described in detail, according to this embodiment, because the trench pattern is formed in a correct shape without deformation, a trench capacitor with high accuracy and high quality can be provided. 
         [0138]    Many widely different embodiments of the present invention may be constructed without departing from the spirit and scope of the present invention. It should be understood that the present invention is not limited to the specific embodiments described in the specification, except as defined in the appended claims.