Abstract:
A method of reinforcing an automobile structure includes: providing an elongated hollow automotive frame structure; providing an elongated carrier having a longitudinal axis; applying a reinforcing medium to the carrier for forming a sleeve wherein the reinforcing medium is a heat activated expandable material; and inserting the sleeve in the hollow frame structure.

Description:
This application is a continuation of application Ser. No. 10/216,944 filed on Aug. 12, 2002, now U.S. Pat. No. 6,641,208, which is a continuation of application Ser. No. 09/524,961 filed on Mar. 14,2000, now U.S. Pat. No. 6,482,486, and claims the benefit of the filing date of both applications. 
    
    
     FIELD OF THE INVENTION 
     This invention relates to a reinforced sleeve coupled to a frame assembly so as to increase the structural strength and stiffness of the frame at selected locations. More particularly, the invention relates to a sleeve coupled to the pillar portion of an automobile frame, wherein the sleeve supports a reinforcing medium that becomes chemically active and expands in response to a predetermined change in ambient conditions. 
     BACKGROUND OF THE INVENTION 
     For many years the automobile industry has been concerned with designing improved vehicle body structures that absorb or deflect impact loads imposed on the vehicle at or near the passenger compartment. While reinforcing the surfaces surrounding the vehicle passenger compartment has long been practiced in the automotive industry, often the structures used to reinforce the frame surrounding the passenger compartment include metal components. These metal reinforcement members tend to add unwanted weight to the automobile. In other instances, the reinforcing members include complex configurations that require welding or mechanical fasteners to affix the reinforcement member to the frame. 
     Consequently, there is needed a lightweight, easily installed apparatus for reinforcing the automobile frame structure, particularly in the area of the passenger compartment. 
     SUMMARY OF THE INVENTION 
     An object of the present invention is to define a reinforcing sleeve that enhances the capacity of an automobile frame assembly to dissipate energy from an impact load imposed on the vehicle frame to avoid deformation of the frame in special locations. 
     To accomplish this and other objects, there is provided a sleeve including a carrier and a reinforcing, medium supported by the carrier. The carrier is fabricated from a polymeric material, and includes an interior and exterior surface. 
     The reinforcing medium extends along at least a portion of the length of the exterior of the carrier. The reinforcing medium is an epoxy-based resin. Preferably the reinforcing medium is a heat-activated structural foam that expands upon heating, typically by a foaming reaction. The preferred reinforcing materials are structural foams available from L&amp;L Products of Romeo, Mich. under the designations L5206, L5207, L5208 and L5209. 
     The sleeve is formed by (1) providing a carrier; (2) reinforcing the carrier by applying a reinforcing medium thereto; and (3) heating the reinforcing medium to a temperature sufficient to cause the reinforcing medium to expand and adhere to adjacent surfaces, either via a bonding formulation in the reinforcing medium itself or via a separate adhesive layer. 
     A general method for installing the sleeve in a frame member includes (1) providing a carrier having a hollow portion; (2) coupling the sleeve to the carrier; and (3) heating the energy absorbing medium to a temperature sufficient to cause the reinforcing medium to expand, such as via activation of a blowing agent. 
     In one embodiment, the sleeve is coupled to a pillar portion of an automobile frame. The sleeve is received in the hollow portion of the pillar frame, wherein the sleeve includes a carrier and an reinforcing medium supported by the carrier. The reinforcing medium extends along at least a portion of the length of the carrier, and becomes chemically activated upon heating the foam to its thermal activation temperature. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The features and inventive aspects of the present invention will become more apparent upon reading the following detailed description, claims and drawings, of which the following is a brief description: 
         FIG. 1  is an elevational view of a typical automobile frame assembly. 
         FIG. 2  shows a perspective view of a reinforced sleeve formed in accordance with the teachings of the invention. 
         FIG. 3  shows a cross-sectional view of the sleeve of  FIG. 2  taken along the line  3 — 3 . 
         FIG. 4  shows the sleeve of  FIG. 2  in the uncured state installed in an automobile frame at the B-pillar portion of the frame. 
         FIG. 5  shows a cross-section view of the sleeve of  FIG. 2  in the cured state installed in an automobile frame at the B-pillar portion of the frame. 
     
    
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
       FIG. 2  shows a reinforced sleeve  20  formed in accordance with the teachings of this invention. The sleeve  20  includes a carrier  22  and a reinforcing medium  24  supported by the carrier  22 . 
     The carrier  22  is an elongated member having open end portions  26 ,  28 . At the end  26 , the carrier  22  includes a U-shaped notch  36  and an elongated opening  32 , each of which aligns with mating components on an automobile frame, or alternatively permits venting of the sleeve  20 . At the opposite end  28 , the carrier  22  defines an opening (not shown), which also aligns with mating components of an automobile frame or alternatively permits venting of sleeve  20 . The exterior surface of the carrier  22  supports an outwardly extending C-shaped bracket  30  between the end portions  26 ,  28 . 
     Internally, the carrier  22  is reinforced by an interior plate  40 , as best seen in FIG.  3 . The plate  40  is located approximately at the center portion of the carrier  22 , and includes two openings  42 ,  44  for permitting the passage of components through the carrier  22 . It will be appreciated that the openings  42 ,  44  may also permit ventilation of the carrier  22  if necessary. 
     The interior surface of the carrier  22  also supports reinforcing ribs  38 . The ribs  38  extend axially along the carrier  20  beginning at each end  26 ,  28  and extending inwardly toward the plate  40 . The ribs  38  terminate at the respective sides of the plate  40 . 
     Preferably, the carrier  22  is fabricated of a moldable material. A preferred polymeric material is glass-reinforced nylon. The carrier  22  can be formed using known techniques such as injection molding, insert injection molding, die casting or blow molding. One advantage of the carrier  22  being fabricated of a moldable material is the ability to mold the carrier  22  into a variety of configurations. Specifically, the carrier  22  can be fabricated using a mold having virtually the same configuration as the component to which the carrier  22  will be coupled or inserted. This facilitates assembling the carrier  22  with the mating component without the need for mechanical fasteners or welding. 
     Turning now to a discussion of the reinforcing medium  24 , as seen in  FIGS. 2 ,  4  and  5 , the carrier  22  supports the reinforcing medium  24  along at least a portion of its exterior surface. The primary purpose of the reinforcing medium  24  is to increase the structural strength and stiffness of the sleeve  20 . In the preferred embodiment, the reinforcing medium  24  is a structural foam. The structural foam  24  increases the compressive strength and structural stiffness of the sleeve  20  without adding significantly to the overall weight of the sleeve  20 . 
     Typically, the structural foam  24  is applied to the carrier  22  in the areas where bonding contact and load transfer is needed. It will be appreciated that the structural foam  24  may encapsulate the entire carrier  22  or may be applied only at preselected locations. The structural foam  24  substantially covers the entire carrier  22  shown in FIG.  2 . Note, however, that it is not necessary to substantially cover the entire surface of the carrier  22  in all applications in which the sleeve will be used. Instead, the structural foam  24  can be applied to selected areas on the carrier  22 , leaving other portions of the carrier  22  uncoated. In the example shown in  FIG. 2 , only the end portions  26 ,  28  and the area of the C-shaped bracket  30  remain uncoated. 
     The structural foam  24  is generally applied to the carrier  22  in a solid or semi-solid state. The structural foam  24  is applied to the outer perimeter of the carrier  22  in a semi-solid state using commonly known injection techniques. During the application process, the structural foam  24  is heated to a temperature that permits the structural foam  24  to flow slightly. However, the temperature is not sufficient to cause the foam  24  to expand or cure. Upon cooling, the structural foam  24  hardens and adheres to the outer surface of the carrier  22 . Where the carrier  22  is made of polymer, for example, it is possible to inject the structural foam  24  into the mold for the carrier  22  during the process of molding the carrier  22 . This arrangement permits the structural foam  24  to substantially encapsulate the outer periphery of the carrier  22 . 
     Alternatively, the structural foam  24  may be applied to the carrier  22  as precast pellets, which are heated slightly to permit the pellets to bond to the outer surface of the carrier  22 . At this stage, the structural foam  24  is heated just enough to cause the structural foam  22  to flow slightly, but not enough to cause the structural foam  24  to thermally expand. Note that other expandable materials can be used, such as, without limitation, an encapsulated mixture of materials that, when activated by temperature, pressure, chemically, or by other ambient conditions, will expand. 
     The structural foam  24  is an epoxy-based material that may include an ethylene copolymer or terpolymer. A copolymer or terpolymer, is composed of two or three different monomers, respectively, i.e., small molecules with high chemical reactivity that are capable of linking up with similar molecules to create a polymer. 
     A number of epoxy-based structural reinforcing foams are known in the art and may also be used as the structural foam  24 . A typical structural foam includes a polymeric base material, such as an epoxy resin or ethylene-based polymer which, when compounded with appropriate ingredients (typically a blowing agent, filler, curing agent, etc.), expands and cures in a reliable and predicable manner upon the application of heat or another activation stimulus. The resulting material has a density that is sufficient to impart desired rigidity to a supported article. From a chemical standpoint for a thermally-activated material, the structural foam  24  is usually initially processed as a thermoplastic material before curing. After curing, the structural foam  16  typically becomes a thermoset material. 
     An example of a preferred structural foam  24  formulation is an epoxy-based material that may include an ethylene copolymer or terpolymer commercially available from L&amp;L Products of Romeo, Mich., under the designations L5206, L5207, L5208 and L5209. One advantage of the preferred structural foam materials  24  over prior art materials is that the preferred materials can be processed in several ways. The preferred materials can be processed by injection molding, extrusion or with a mini-applicator type extruder. This enables the formulation and creation of part designs that exceed the capability of most prior art materials. 
     While the preferred materials for fabricating the structural foam  24  have been disclosed, the structural foam  24  can be formed from other materials provided that the material selected is heat-activated or otherwise activated by an ambient condition (e.g. moisture, pressure, time or the like) and expands in a predictable and reliable manner under appropriate conditions for the selected application. One such material is the epoxy based resin disclosed in U.S. patent application Ser. No. 09/460,322, the teachings of which are incorporated herein by reference, filed with the United States Patent and Trademark Office on Mar. 8, 1999 by the assignee of this application. Some other possible materials include, but are not limited to, polyolefin materials, copolymers and terpolymers with at least one monomer type an alpha-olefin, phenol/formaldehyde materials, phenoxy materials, and polyurethane materials with high glass transition temperatures. In general, the desired characteristics of the structural foam  24  include high stiffness, high strength, high glass transition temperature (typically greater than 70 degrees Celsius), and good corrosion resistance properties. 
     In applications where a heat activated, thermally expanding material is employed, an important consideration involved with the selection and formulation of the material comprising the structural foam  24  is the temperature at which a material reaction or expansion, and possibly curing, will take place. For instance, in most applications, it is undesirable for the material to be active at room temperature or otherwise at the ambient temperature in a production line environment. More typically, the structural foam  24  becomes reactive at higher processing temperatures, such as those encountered in an automobile assembly plant, when the foam  16  is processed along with the automobile components at elevated temperatures or at higher applied energy levels. While temperatures encountered in an automobile assembly operation may be in the range of 148.89° C. to 204.44° C. (300° F. to 400° F.), body and paint shop applications are commonly about 121° C. (250° F.) or slightly lower. If needed, blowing agents can be altered by activation to cause expansion at different temperatures outside the above ranges. 
     Generally, prior art expandable foams have a range of expansion ranging from approximately 0 to over 1000 percent. The level of expansion of the structural foam  24  may be increased to as high as 1500 percent or more. 
     Installation 
       FIG. 1  shows an automobile  1  having a front door aperture  2 , a roof portion  3 , an A-pillar  4  and a B-pillar  5 . The front door aperture  2  is bounded in the longitudinal direction of the vehicle by the front or A-pillar  4 , and the rear or B-pillar  5 . At the bottom, the door aperture  2  is bounded by a sill  6 , and at the top by the roof portion  3 . The A-pillar  4 , B-pillar  5 , roof portion  2  and the sill  6  form a frame  7  that surrounds the passenger compartment, which is internally adjacent the door aperture  2 . 
     Conventionally, the pillars  4 ,  5  are hollow beams having a closed profile. According to the present invention, the hollow center of the pillars  4 ,  5  each receive the sleeve  20  as best seen in  FIGS. 1 ,  2 ,  4  and  5 . The sleeve  20  is configured such that the C-bracket  30 , the opening  32  as well as other openings not shown in the figures and the U-shaped portion  36  align with mating components formed or supported by the pillars  4 ,  5 . 
     As seen in  FIG. 4 , when the sleeve  20  is installed in the pillar  5 , there is a slight clearance between the interior of the B-pillar  5  and the sleeve  20 . This is so because the structural foam  24  is in the uncured state and enables the structural foam  24  to bond to electrocoat-primed metal rather than non-primed metal. More particularly, the clearance permits electrocoat drainage, thereby allowing the primer to cover all of the metal surfaces to facilitate bonding of the structural foam and prevent corrosion of the metal. 
       FIG. 5  illustrates the position of the structural foam  24  in the automobile frame assembly after the curing cycle. As shown, the structural foam  24  adheres to the inner surface of the automobile frame assembly, substantially filling the gap between the inner surface of the pillar  5  and the sleeve  20 . 
     The structural foam  24  is fully cured by subjecting the structural foam  24  to temperatures in the range of those generated by a paint oven of the type used to cure automobile body paint or primer. It will be appreciated that paint ovens are known to reach temperatures of 121° C. (250° F.) or greater. Thus, it will be appreciated that the structural foam may be cured by simply heating the sleeve to a temperature of 121° C. (250° F.) or greater. 
     The high temperatures used to cure the structural foam  24  also cause activation of the thermal expansion properties of the structural foam  24 . The application of the structural foam  24  to the carrier  22  increases the structural strength and stiffness of the carrier  22 . As a result, the overall structural strength and stiffness of the sleeve  20  is increased. 
     It should be understood that various alternatives to the embodiments of the invention described herein may be employed in practicing the invention. It is intended that the following claims define the scope of the invention and that the method and apparatus within the scope of these claims and their equivalents be covered thereby.