Abstract:
The present invention discloses an novel organic material containing indenotriphenylene derivatives and organic EL device using the indenotriphenylene derivatives as hole blocking layer (HBL), electron transport layer (ETL) and/or phosphorescent host can efficiently lower driving voltage, lower power consumption and increase the efficiency. The present invention further relates to the methods of preparation for the indenotriphenylene derivatives and organic EL device comprising these derivatives.

Description:
[0001]    This application is a Continuation-in-Part of U.S. patent Ser. No. 14/585,219, filed Dec. 30, 2014. 
     
    
     FIELD OF INVENTION 
       [0002]    The present invention generally relates to an organic material containing indenotriphenylene derivatives and organic electroluminescent (herein referred to as organic EL) device using the organic material. More specifically, the present invention relates to an organic material having general formula (I), an organic EL device employing the organic material as hole blocking layer (HBL), electron transport layer (ETL) and/or phosphorescent host can efficiently lower driving voltage, lower power consumption and increase the efficiency. 
       BACKGROUND OF THE INVENTION 
       [0003]    Organic electroluminescent (organic EL) is a light-emitting diode (LED) in which the emissive layer is a film made by organic compounds which emits light in response to an electric current. The emissive layer of organic compound is sandwiched between two electrodes. Organic EL is applied in flat panel displays due to their high illumination, low weight, ultra-thin profile, self-illumination without back light, low power consumption, wide viewing angle, high contrast, simple fabrication methods and rapid response time. 
         [0004]    The first observation of electroluminescence in organic materials were in the early 1950s by Andre Bernanose and co-workers at the Nancy-University in France. Martin Pope and his co-workers at New York University first observed direct current (DC) electroluminescence on a single pure crystal of anthracene and on anthracene crystals doped with tetracene under vacuum in 1963. 
         [0005]    The first diode device was reported by Ching W. Tang and Steven Van Slyke at Eastman Kodak in 1987. The device used a two-layer structure with separate hole transporting and electron transporting layers resulted in reduction in operating voltage and improvement of the efficiency, that led to the current era of organic EL research and device production. 
         [0006]    Typically organic EL is composed of layers of organic materials situated between two electrodes, which include a hole transporting layer (HTL), an emitting layer (EML), an electron transporting layer (ETL). The basic mechanism of organic electroluminescence involves the injection of the carrier, transport, recombination of carriers and exciton formed to emit light. When an external voltage is applied to an organic light-emitting device, electrons and holes are injected from a cathode and an anode, respectively, electrons will be injected from a cathode into a LUMO (lowest unoccupied molecular orbital) and holes will be injected from an anode into a HOMO (highest occupied molecular orbital). When the electrons recombine with holes in the emitting layer, excitons are formed and then emit light. When luminescent molecules absorb energy to achieve an excited state, an exciton may either be in a singlet state or a triplet state depending on how the spins of the electron and hole have been combined. 75% of the excitons form by recombination of electrons and holes to achieve a triplet excited state. Decay from triplet states is spin forbidden, Thus, a fluorescence electroluminescent device has only 25% internal quantum efficiency. In contrast to fluorescence electroluminescent device, phosphorescent organic light-emitting diodes make use of spin-orbit interactions to facilitate intersystem crossing between singlet and triplet states, thus obtaining emission from both singlet and triplet states and the internal quantum efficiency of electroluminescent devices from 25% to 100%. 
         [0007]    Recently, a new type of fluorescent organic EL device incorporating mechanism of thermally activated delayed fluorescence (TADF) has been developed by Adachi and coworkers is a promising way to obtain a high efficiency of exciton formation by converting spin-forbidden triplet excitons up to the siglet level by the mechanism of reverse intersystem crossing (RISC). 
         [0008]    The phosphorescent organic EL utilizes both triplet and singlet excitons. Cause of longer lifetime and the diffusion length of triplet excitons compared to those of singlet excitons, the phosphorescent organic EL generally need an additional hole blocking layer (HBL) between the emitting layer (EML) and the electron transporting layer (ETL) or the electron transporting layer with hole blocking ability instead of typical ETL. The purpose of the use of HBL or HBETL is to confine the recombination of injected holes and electrons and the relaxation of created excitons within the EML, hence the device&#39;s efficiency can be improved. To meet such roles, the hole blocking materials must have HOMO (highest occupied molecular orbital) and LUMO (lowest unoccupied molecular orbital) energy levels suitable to block hole transport from the EML to the ETL and to pass electrons from the ETL to the EML, in addition, lower power consumption, the good thermal and electrochemical stability of the materials are also needed. 
         [0009]    There continues to be a need for organic EL materials which is able to efficiently transport electrons and block holes, with lower power consumption, good thermal stability and high emitting efficiency. According to the reasons described above, the present invention has the objective of resolving such problems of the prior-art and offering an organic EL device which is excellent in its lower power consumption, thermal stability, high luminance and long half-life time. The present invention disclose a novel organic material containing indenotriphenylene derivatives having general formula (I), used as hole blocking layer (HBL), electron transport layer (ETL) and/or phosphorescent host have good charge carrier mobility and excellent operational durability can efficiently lower driving voltage and power consumption, increasing efficiency of organic EL device. 
       SUMMARY OF THE INVENTION 
       [0010]    In accordance with the present invention, the organic material for hole blocking material (herein referred to as HBM), electron transport material (herein referred to as ETM) and/or phosphorescent host and their use for organic EL device are provided. The organic material can overcome the drawbacks of the conventional materials like as lower efficiency and higher power consumption. 
         [0011]    An object of the present invention is to provide the organic material which can be used as hole blocking material (HBM), hole blocking electron transport material (HBETM) for organic EL device and can efficiently confine excitons to transfer to electron transport layer. 
         [0012]    An object of the present invention is to provide the organic material which can be used as electron transport material (ETM) for organic EL device. 
         [0013]    An object of the present invention is to provide the organic material which can be used as phosphorescent host material of emitting layer for organic EL device. 
         [0014]    Another object of the present invention is to apply the organic material for organic EL device and lower driving voltage, lower power consumption and increase the efficiency. 
         [0015]    The present invention has the economic advantages for industrial practice. Accordingly the present invention, the organic material which can be used for organic EL device is disclosed. The mentioned the organic material is represented by the following formula (I): 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein A ring represents a phenyl group and fused ring hydrocarbon units with two to four rings group, L represents a single bond, a substituted or unsubstituted divalent arylene group having 6 to 30 ring carbon atoms or a substituted or unsubstituted divalent heteroarylene group having 6 to 30 ring carbon atoms, R 1  to R 3  independently selected from the group consisting of a hydrogen atom, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, a substituted or unsubstituted aralkyl group having 6 to 30 carbon atoms and a substituted or unsubstituted heteroaryl group having 3 to 30 carbon atoms, Y 1  to Y 5  each independently represent nitrogen atom or CR 5 , R 5  independently represent a hydrogen atom, a substituted or unsubstituted phenylene group having 6 to 30 ring carbon atoms, or a bond linked to B; B stand for a group of following formula (II): 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein q represents an integer of 0 to 3, p represents an integer of 0 to 7, X represents O, S, NR 6 , R 6  independently represents a hydrogen atom, a substituted or unsubstituted phenyl group, a substituted or unsubstituted carbazole group, and a bond linked to formula (I), R 4  is the same definition as R 1 . 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0016]      FIG. 1  show one example of organic EL device in the present invention.  6  is transparent electrode,  13  is metal electrode,  7  is hole injection layer which is deposited onto  6 ,  8  is hole transporting layer which is deposited onto  7 ,  9  is fluorescent or phosphorescent emitting layer which is deposited onto  8 ,  10  is hole blocking layer which is deposited onto  9 ,  11  is electron transporting layer which is deposited onto  10 ,  12  is electron injection layer which is deposited on to  11 . 
       
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0017]    What probed into the invention is the organic material and organic EL device using the organic material. Detailed descriptions of the production, structure and elements will be provided in the following to make the invention thoroughly understood. Obviously, the application of the invention is not confined to specific details familiar to those who are skilled in the art. On the other hand, the common elements and procedures that are known to everyone are not described in details to avoid unnecessary limits of the invention. Some preferred embodiments of the present invention will now be described in greater detail in the following. However, it should be recognized that the present invention can be practiced in a wide range of other embodiments besides those explicitly described, that is, this invention can also be applied extensively to other embodiments, and the scope of the present invention is expressly not limited except as specified in the accompanying claims. 
         [0018]    In a first embodiment of the present invention, the organic material which can be used as hole blocking material (herein referred to as HBM), electron transport material (herein referred to as ETM) and/or phosphorescent host for organic EL device are disclosed. The mentioned organic material are represented by the following formula (I) 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein A ring represents a phenyl group and fused ring hydrocarbon units with two to four rings group, L represents a single bond, a substituted or unsubstituted divalent arylene group having 6 to 30 ring carbon atoms or a substituted or unsubstituted divalent heteroarylene group having 6 to 30 ring carbon atoms, R 1  to R 3  independently selected from the group consisting of a hydrogen atom, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, a substituted or unsubstituted aralkyl group having 6 to 30 carbon atoms and a substituted or unsubstituted heteroaryl group having 3 to 30 carbon atoms, Y 1  to Y 5  each independently represent nitrogen atom or CR 5 , R 5  independently represent a hydrogen atom, a substituted or unsubstituted phenylene group having 6 to 30 ring carbon atoms, or a bond linked to B; B stand for a group of following formula (II): 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein q represents an integer of 0 to 3, p represents an integer of 0 to 7, X represents O, S, NR 6 , R 6  independently represents a hydrogen atom, a substituted or unsubstituted phenyl group, a substituted or unsubstituted carbazole group, and a bond linked to formula (I), R 4  is the same definition as R 1 . 
         [0019]    According to the above-mentioned formula (I) wherein L is represented the following formulas: 
         [0000]    
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
     
         [0020]    According to the above-mentioned formula (I) wherein A ring represents a phenyl group and fused ring hydrocarbon units with two to four rings group including naphthyl group, anthracenyl group, phenanthrenyl group, pyrenyl group, chrysenyl group and triphenylene group. 
         [0021]    In this embodiment, some organic materials according formula (I) are shown below: 
         [0000]    
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
     
         [0022]    Detailed preparation for the organic material in the present invention could be clarified by exemplary embodiments, but the present invention is not limited to exemplary embodiments. EXAMPLE 1˜14 show the preparation for some EXAMPLES of the organic material in the present invention. EXAMPLE 15 and 16 show the fabrication of organic EL device and I-V-B, half-life time of organic EL device testing report. 
       Example 1 
     Synthesis of EX5 
     Synthesis of 2-bromo-5-nitrobiphenyl 
       [0023]    
       
                 
         
             
             
         
       
     
         [0024]    2.6 g (12.14 mmol) of 2-phenyl-4-nitroaniline was added to a mixture of 0.92 g (13.35 mmol) of sodium nitrite, 8 ml of sulfuric acid, 9 ml of acetic acid at 0-5° C. and stirred for 2 hr at 0-5° C. Water was added to this mixture and stirred for 1 hr at room temperature. 4.3 g (19.42 mmol) of copper(II) bromide dissolved in 9.3 ml 2M HCl solution was added and stirred for 20 min at room temperature, then heated to 60° C. for 1 hr. After finishing the reaction, the organic layer was extracted with ether and water, washed with brine, dried over magnesium sulfate and evaporated to dryness and the crude was purified by column chromatography on silica to give product (1.5 g, 5.39 mmol, 45.5%) as a white solid. 
       Synthesis of 9,9-dimethyl-2-(5-nitrobiphenyl-2-yl)-9H-fluorene 
       [0025]    
       
                 
         
             
             
         
       
     
         [0026]    A mixture of 40 g (14.38 mmol) of 2-bromo-5-nitrobiphenyl, 27.7 g (15.82 mmol) of 9,9-dimethyl-9H-fluoren-2-ylboronic acid, 1.8 g (0.16 mmol) of Pd(PPh 3 ) 4 , 119 ml of 2M Na 2 CO 3 , 150 ml of EtOH and 450 ml toluene was degassed and placed under nitrogen, and then heated at 100° C. overnight. After finishing the reaction, the mixture was allowed to cool to room temperature. The solution was extracted with dichloromethane and water. The organic layer was dried with anhydrous magnesium sulfate and the solvent was evaporated under reduced pressure. The residue was purified by column chromatography on silica to give product 43.1 g (110.1 mmol, 69.6%). 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 7.93 (s, 1H), 7.71 (d, 1H), 7.50 (d, 1H), 7.38˜7.21 (m, 6H), 7.16˜6.92 (m, 4H), 6.83˜6.65 (m, 2H), 1.15 (s, 6H) 
       Synthesis of 6-(9,9-dimethyl-9H-fluoren-2-yl)biphenyl-3-amine 
       [0027]    
       
                 
         
             
             
         
       
     
         [0028]    A mixture of 10.4 g (26.56 mmol) of 9,9-dimethyl-2-(5-nitrobiphenyl-2-yl)-9H-fluorene, 8.5 g (159.36 mmol) of iron powder and 10 ml of conc. HCl was refluxed in aqueous ethanol (100 mL of alcohol and 30 mL of water) at 85° C. for 2 h. The reaction mixture was filtered and the filtrate was extracted with ethyl acetate and water. The organic layer was dried with anhydrous magnesium sulfate and the solvent was evaporated under reduced pressure. Formed solid was washed with hexane to yield product 8.2 g (22.68 mmol, 85%). 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 7.71 (d, 1H), 7.64 (d, 1H), 7.42 (d, 1H), 7.29˜7.12 (m, 7H), 7.06 (d, 2H), 6.89 (s, 1H), 6.80 (d, 1H), 6.78 (s, 1H), 4.47 (s, 2H), 1.12 (s, 6H). 
       Synthesis of 2-(5-bromobiphenyl-2-yl)-9,9-dimethyl-9H-fluorene 
       [0029]    
       
                 
         
             
             
         
       
     
         [0030]    To a refluxing mixture of 0.34 g (3.32 mmol) of tert-butyl nitrite, 0.6 g (2.76 mmol) of anhydrous copper(II) bromide and anhydrous acetonitrile (46 mL), 1 g (2.76 mmol) of the corresponding 6-(9,9-dimethyl-9H-fluoren-2-yl)-biphenyl-3-amine was added slowly over a period of 1 h giving rise to a reaction with vigorous foaming and evolution of nitrogen gas. After completion of the reaction, the mixture was cooled to room temperature and poured into an aqueous HCl solution. The crude which precipitated was purified by column chromatography on silica to give product 0.3 g (0.70 mmol, 25%). 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 7.81 (d, 1H), 7.68˜7.66 (m, 1H), 7.63˜7.61 (m, 1H), 7.37˜7.35 (m, 1H), 7.32˜7.24 (m, 4H), 7.22˜7.16 (m, 4H), 7.12˜7.09 (m, 2H), 6.93 (d, 1H), 1.20 (s, 6H). 
       Synthesis of 6-bromo-10,10-dimethyl-10H-indeno[2,1-b]triphenylene 
       [0031]    
       
                 
         
             
             
         
       
     
         [0032]    In a 100 ml three-necked flask that had been degassed and filled with nitrogen, 2.9 g (0.68 mmol) of 2-(5-bromobiphenyl-2-yl)-9,9-dimethyl-9H-fluorene was dissolved in anhydrous dichloromethane (180 ml), 5.5 g (3.40 mmol) of iron(III) chloride was then added, and the mixture was stirred one hour. The reaction was quenched with methanol and water and the organic layer was separated and the solvent was removed. The residue was purified by column chromatography on silica afforded a white solid (1.7 g, 0.81 mmol, 58.6%). 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 9.01 (s, 1H), 8.94 (d, 2H), 8.78 (s, 1H), 8.58 (s, 1H), 8.49 (s, 1H), 7.98 (d, 1H), 7.85˜7.78 (m, 2H), 7.63˜7.43 (m, 4H), 1.69 (s, 6H). 
       Synthesis of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane 
       [0033]    
       
                 
         
             
             
         
       
     
         [0034]    A mixture of 3 g (7 mmol) of 6-bromo-10,10-dimethyl-10H-indeno[2,1-b]triphenylene, 2.16 g (8.4 mmol) of 4,4,4′,4′,5,5,5′,5′-octamethyl-2,2′-bi(1,3,2-dioxaborolane), 0.16 g (0.14 mmol) of Pd(PPh 3 ) 4 , 50 ml 1,4-dioxane was degassed and placed under nitrogen, and then heated at 100° C. for 12 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with ethyl acetate and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product (2.27 g, 4.8 mmol, 69%) as a white solid. 
       Synthesis of 2-(4-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-4,6-diphenyl-1,3,5-triazine (EX5) 
       [0035]    
       
                 
         
             
             
         
       
     
         [0036]    A mixture of 3 g (6.38 mmol) of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane, 1.90 g (4.90 mmol) of 2-(4-bromophenyl)-4,6-diphenyl-1,3,5-triazine, 0.05 g (0.05 mmol) of Pd(PPh 3 ) 4 , 9.8 ml of 2M Na 2 CO 3 , 15 ml of EtOH and 45 ml toluene was degassed and placed under nitrogen, and then heated at 100° C. for 12 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product (1.75 g, 2.67 mmol, 55%) as a pale yellow solid. 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 9.03 (s, 1H), 8.97˜8.77 (m, 3H), 8.58 (s, 1H), 8.49˜8.31 (m, 7H), 7.98 (d, 1H), 7.85˜7.78 (m, 2H), 7.63˜7.43 (m, 12H), 1.69 (s, 6H). MS (m/z, FAB + ): 651.5 
       Example 2 
     Synthesis of EX9 
     Synthesis of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,6-diphenyl-1,3,5-triazine 
       [0037]    
       
                 
         
             
             
         
       
     
         [0038]    2-chloro-4,6-diphenyl-1,3,5-triazine instead of 2-(4-bromo phenyl)-4,6-diphenyl-1,3,5-triazine, except for using the same method as in synthesis Example 1, the desired compound of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,6-diphenyl-1,3,5-triazine (1.26 g, yield=45%) was obtained. MS (m/z, FAB + ): 575.6 
       Example 3 
     Synthesis of EX10 
     Synthesis of 2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-4,6-diphenylpyrimidine 
       [0039]    
       
                 
         
             
             
         
       
     
         [0040]    2-(3-bromophenyl)-4,6-diphenylpyrimidine instead of 2-(4-bromophenyl)-4,6-diphenyl-1,3,5-triazine, except for using the same method as in synthesis Example 1, the desired compound of 2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-4,6-diphenylpyrimidine (3.08 g, yield=63%) was obtained. MS (m/z, FAB + ): 650.8 
       Example 4 
     Synthesis of EX15 
     Synthesis of 2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-4,6-bis([1,1′:3′,1″-terphenyl]-5′-yl)-1,3,5-triazine 
       [0041]    
       
                 
         
             
             
         
       
     
         [0042]    2-(4-bromophenyl)-4,6-bis([1,1′:3′,1″-terphenyl]-5′-yl)-1,3,5-triazine instead of 2-(4-bromophenyl)-4,6-diphenyl-1,3,5-triazine, except for using the same method as in synthesis Example 1, the desired compound of 2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-4,6-bis([1,1′:3′,1″-terphenyl]-5′-yl)-1,3,5-triazine (1.96 g, yield=42%) was obtained. MS (m/z, FAB + ): 957.2 
       Example 5 
     Synthesis of EX33 
     Synthesis of 9,9′-(6-(4-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-1,3,5-triazine-2,4-diyl)bis(9H-carbazole) 
       [0043]    
       
                 
         
             
             
         
       
     
         [0044]    A mixture of 2 g (4.25 mmol) of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane, 1.85 g (3.26 mmol) of 9,9′-(6-(4-bromophenyl)-1,3,5-triazine-2,4-diyl)bis(9H-carbazole), 0.04 g (0.03 mmol) of Pd(PPh 3 ) 4 , 3.25 ml of 2M Na 2 CO 3 , 10 ml of EtOH and 30 ml toluene was degassed and placed under nitrogen, and then heated at 100° C. for 12 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product (1.24 g, 1.50 mmol, 46%) as a pale yellow solid. 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 9.08 (s, 1H), 8.97˜8.77 (m, 3H), 8.53˜8.29 (m, 8H), 7.92˜7.78 (m, 7H), 7.63˜7.43 (m, 14H), 1.69 (s, 6H). MS (m/z, FAB + ): 831.0 
       Example 6 
     Synthesis of EX37 
     Synthesis of 9,9′-(2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)pyrimidine-4,6-diyl)bis(9H-carbazole) 
       [0045]    
       
                 
         
             
             
         
       
     
         [0046]    9,9′-(2-(3-bromophenyl)pyrimidine-4,6-diyl)bis(9H-carbazole) instead of 9,9′-(6-(4-bromophenyl)-1,3,5-triazine-2,4-diyl)bis(9H-carbazole), except for using the same method as in synthesis Example 5, the desired compound of 9,9′-(2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)pyrimidine-4,6-diyl)bis(9H-carbazole) (1.18 g, yield=44%) was obtained. MS (m/z, FAB + ): 829.8 
       Example 7 
     Synthesis of EX38 
     Synthesis of 9,9′-(2-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)pyrimidine-4,6-diyl)bis(9H-carbazole) 
       [0047]    
       
                 
         
             
             
         
       
     
         [0048]    9-(4-(4-bromophenyl)-6-phenyl-1,3,5-triazin-2-yl)-9H-carbazole instead of 9,9′-(6-(4-bromophenyl)-1,3,5-triazine-2,4-diyl)bis(9H-carbazole) except for using the same method as in synthesis Example 5, the desired compound of 9-(4-(4-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-6-phenyl-1,3,5-triazin-2-yl)-9H-carbazole (1.20 g, yield=50%) was obtained. MS (m/z, FAB + ): 741.5 
       Example 8 
     Synthesis of EX42 
     Synthesis of 9-(4-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-9H-carbazole 
       [0049]    
       
                 
         
             
             
         
       
     
         [0050]    A mixture of 2 g (4.25 mmol) of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane, 1.05 g (3.26 mmol) of 9-(4-bromophenyl)-9H-carbazole, 0.04 g (0.03 mmol) of Pd(PPh 3 ) 4 , 3.25 ml of 2M Na 2 CO 3 , 10 ml of EtOH and 30 ml toluene was degassed and placed under nitrogen, and then heated at 100° C. for 12 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product (1.43 g, 2.45 mmol, 75%) as a pale yellow solid. 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 9.01 (s, 1H), 8.82 (d, 2H), 8.77 (s, 1H), 8.55 (s, 1H), 8.49 (s, 1H), 7.98 (d, 1H), 7.85˜7.75 (m, 6H), 7.63˜7.33 (m, 12H), 1.69 (s, 6H). MS (m/z, FAB + ): 586.3 
       Example 9 
     Synthesis of EX44 
     Synthesis of 9,9′-(5-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-1,3-phenylene)bis(9H-carbazole) 
       [0051]    
       
                 
         
             
             
         
       
     
         [0052]    9,9′-(5-bromo-1,3-phenylene)bis(9H-carbazole) instead of 9-(4-bromophenyl)-9H-carbazole, except for using the same method as in synthesis Example 8, the desired compound of 9,9′-(5-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-1,3-phenylene)bis(9H-carbazole) (1.46 g, yield=60%) was obtained. MS (m/z, FAB + ): 751.4 
       Example 10 
     Synthesis of EX50 
     Synthesis of 9-(4-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-9′-phenyl-9H,9′H-3,3′-bicarbazole 
       [0053]    
       
                 
         
             
             
         
       
     
         [0054]    9-(4-bromophenyl)-9′-phenyl-9H,9′H-3,3′-bicarbazole instead of 9-(4-bromophenyl)-9H-carbazole, except for using the same method as in synthesis Example 8, the desired compound of 9-(4-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-9′-phenyl-9H,9′H-3,3′-bicarbazole (1.28 g, yield=48%) was obtained. MS (m/z, FAB + ): 827.9 
       Example 11 
     Synthesis of EX51 
     Synthesis of 3-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-9-phenyl-9H-carbazole 
       [0055]    
       
                 
         
             
             
         
       
     
         [0056]    3-(3-bromophenyl)-9-phenyl-9H-carbazole instead of 9-(4-bromophenyl)-9H-carbazole, except for using the same method as in synthesis Example 8, the desired compound of 3-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)-9-phenyl-9H-carbazole (1.28 g, yield=48%) was obtained. MS (m/z, FAB + ): 662.7 
       Example 12 
     Synthesis of EX55 
     Synthesis of 4-(3-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)phenyl)dibenzo[b,d]thiophene 
       [0057]    
       
                 
         
             
             
         
       
     
         [0058]    A mixture of 2 g (4.25 mmol) of 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-4,4,5,5-tetramethyl-1,3,2-dioxaborolane, 1.10 g (3.26 mmol) of 4-(3-bromophenyl)dibenzo[b,d]thiophene, 0.04 g (0.03 mmol) of Pd(PPh 3 ) 4 , 3.25 ml of 2M Na 2 CO 3 , 10 ml of EtOH and 30 ml toluene was degassed and placed under nitrogen, and then heated at 100° C. for 12 h. After finishing the reaction, the mixture was allowed to cool to room temperature. The organic layer was extracted with dichloromethane and water, dried with anhydrous magnesium sulfate, the solvent was removed and the residue was purified by column chromatography on silica to give product (1.62 g, 2.6 mmol, 80%) as a pale yellow solid. 1H NMR (CDCl3, 400 MHz): chemical shift (ppm) 9.03 (s, 1H), 8.86 (d, 2H), 8.70 (s, 1H), 8.49 (s, 1H), 8.46 (s, 1H), 7.96 (d, 1H), 7.85˜7.76 (m, 2H), 7.68˜7.25 (m, 15H), 1.69 (s, 6H). MS (m/z, FAB + ): 603.5 
       Example 13 
     Synthesis of EX56 
     Synthesis of 2,2′-(5-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-1,3-phenylene)didibenzo[b,d]furan 
       [0059]    
       
                 
         
             
             
         
       
     
         [0060]    2,2′-(5-bromo-1,3-phenylene)didibenzo[b,d]furan instead of 4-(3-bromophenyl)dibenzo[b,d]thiophene, except for using the same method as in synthesis Example 12, the desired compound of 2,2′-(5-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)-1,3-phenylene)didibenzo[b,d]furan (1.30 g, yield=53%) was obtained. MS (m/z, FAB + ): 752.9 
       Example 14 
     Synthesis of EX57 
     Synthesis of 4-(3′-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)biphenyl-3-yl)dibenzo[b,d]thiophene 
       [0061]    
       
                 
         
             
             
         
       
     
         [0062]    4-(3′-bromobiphenyl-3-yl)dibenzo[b,d]thiophene instead of 4-(3-bromophenyl)dibenzo[b,d]thiophene, except for using the same method as in synthesis Example 12, the desired compound of 4-(3′-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-6-yl)biphenyl-3-yl)dibenzo[b,d]thiophene (1.30 g, yield=53%) was obtained. MS (m/z, FAB + ): 679.5 
       General Method of Producing Organic El Device 
       [0063]    ITO-coated glasses with 9˜12 ohm/square in resistance and 120˜160 nm in thickness are provided (hereinafter ITO substrate) and cleaned in a number of cleaning steps in an ultrasonic bath (e.g. detergent, deionized water). Before vapor deposition of the organic layers, cleaned ITO substrates are further treated by UV and ozone. All pre-treatment processes for ITO substrate are under clean room (class 100). 
         [0064]    These organic layers are applied onto the ITO substrate in order by vapor deposition in a high-vacuum unit (10 −7  Torr), such as: resistively heated quartz boats. The thickness of the respective layer and the vapor deposition rate (0.1˜0.3 nm/sec) are precisely monitored or set with the aid of a quartz-crystal monitor. It is also possible, as described above, for individual layers to consist of more than one compound, i.e. in general a host material doped with a dopant material. This is achieved by co-vaporization from two or more sources. 
         [0065]    Dipyrazino[2,3-f:2,3-]quinoxaline-2,3,6,7,10,11-hexacarbonitrile (HAT-CN) is used as hole injection layer in this organic EL device, N,N-Bis(naphthalene-1-yl)-N,N-bis(phenyl)-benzidine (NPB) is most widely used as the hole transporting layer. 10,10-dimethyl-12-(10-(naphthalen-2-yl)anthracen-9-yl)-10H-indeno[2,1-b]triphenylene (H1) is used as blue emitting host and N1,N1,N6,N6-tetram-tolylpyrene-1,6-diamine (D1) is used as blue guest. 2-(10,10-dimethyl-10H-indeno[2,1-b]triphenylen-13-yl)-4,6-diphenyl pyrimidine (HB1) is used as hole blocking material (HBM) and 4,7-Diphenyl-2,9-bis(4-(1-phenyl-1H-benzo[d]imidazole-2-yl)phenyl)-1,10-phenanthroline (LT-N8001, U.S. Pat. No. 7,754,348) is used as electron transporting material (ETM) to co-deposit with 8-hydroxyquinolato-lithium (LiQ) in organic EL device. Bis(2-methyl-8-quinolinolate)-4-(phenylphenolato)aluminium (BAlq) is used as hole blocking material (HBM) or phosphorescent host for phosphorescent system, Bis(2-phenylpyridinato) (2,4-diphenylpyridinato)iridium(III) (D2) is used as phosphorescent dopant. The prior art of OLED materials for producing standard organic EL device control and comparable material in this invention shown its chemical structure as following formulas: 
         [0000]    
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
     
         [0066]    A typical organic EL device consists of low work function metals, such as Al, Mg, Ca, Li and K, as the cathode by thermal evaporation, and the low work function metals can help electrons injecting the electron transporting layer from cathode. In addition, for reducing the electron injection barrier and improving the organic EL device performance, a thin-film electron injecting layer is introduced between the cathode and the electron transporting layer. Conventional materials of electron injecting layer are metal halide or metal oxide with low work function, such as: LiF, LiQ, MgO, or Li 2 O. On the other hand, after the organic EL device fabrication, EL spectra and CIE coordination are measured by using a PR650 spectra scan spectrometer. Furthermore, the current/voltage, luminescence/voltage and yield/voltage characteristics are taken with a Keithley 2400 programmable voltage-current source. The above-mentioned apparatuses are operated at room temperature (about 25° C.) and under atmospheric pressure. 
       Example 15 
       [0067]    Using a procedure analogous to the above mentioned general method, fluorescent blue emitting organic EL device having the following device structure were produced (See  FIG. 1 ): ITO/HAT-CN (20 nm)/NPB (130 nm)/H1 doped 5% D1 (30 nm)/HBM (10 nm)/ETM co-deposit LiQ (ETM:LiQ, ratio=1:1 (40 nm)/LiQ (1 nm)/Al (160 nm). The I-V-B (at 1000 nits) and half-life time of fluorescent blue-emitting organic EL device testing report as Table 1, The half-life time is defined that the initial luminance of 1000 cd/m 2  has dropped to half. 
         [0000]    
       
         
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
               
                   
                   
                 Voltage 
                 Efficiency 
                 CIE 
                 Half-lifetime 
               
               
                 HBM 
                 ETM 
                 (V) 
                 (cd/A) 
                 (y) 
                 (hour) 
               
               
                   
               
             
             
               
                 HB1 
                 LT-N8001 
                 6.5 
                 4.3 
                 0.174 
                 340 
               
               
                 BAlq 
                 LT-N8001 
                 7.2 
                 3.9 
                 0.174 
                 220 
               
               
                 HB1 
                 EX5 
                 5.5 
                 6.7 
                 0.180 
                 350 
               
               
                 HB1 
                 EX9 
                 5.8 
                 5.5 
                 0.183 
                 180 
               
               
                 HB1 
                 EX10 
                 5.4 
                 6.5 
                 0.180 
                 450 
               
               
                 HB1 
                 EX15 
                 5.6 
                 6.0 
                 0.181 
                 320 
               
               
                 BAlq 
                 EX10 
                 7.5 
                 5.3 
                 0.174 
                 250 
               
               
                 — 
                 EX10 
                 5.1 
                 6.8 
                 0.183 
                 390 
               
               
                 BAlq 
                 EX5 
                 7.7 
                 6.4 
                 0.177 
                 230 
               
               
                   
               
             
          
         
       
     
       Example 16 
       [0068]    Using a procedure analogous to the above mentioned general method, phosphorescent emitting organic EL device having the following device structures are produced (See  FIG. 1 ): ITO/HAT-CN (20 nm)/NPB (130 nm)/phosphorescent host (PHhost)+15% D2 (30 nm)/HBM (15 nm)/EX5 co-deposit LiQ (EX5: LiQ, ratio=1:1) (40 nm)/LiQ (1 nm)/Al (160 nm). The I-V-B (at 1000 nits) and half-life time of phosphorescent emitting organic EL device testing report as Table 2. The half-life time is defined that the initial luminance of 3000 cd/m 2  has dropped to half. 
         [0000]    
       
         
               
               
               
               
               
               
             
           
               
                 TABLE 2 
               
               
                   
               
               
                   
                   
                   
                   
                   
                 Half- 
               
               
                 PHhost(H1 + H2) 
                   
                 Voltage 
                 Efficiency 
                 CIE 
                 life time 
               
               
                 H1:H2 = 1:1 
                 HBM 
                 (V) 
                 (lm/w) 
                 (x, y) 
                 (hour) 
               
               
                   
               
             
             
               
                 BAlq 
                 BAlq 
                 6.8 
                 16 
                 0.44, 0.56 
                 380 
               
               
                 EX37 + EX50 
                 BAlq 
                 5.3 
                 28 
                 0.44, 0.56 
                 450 
               
               
                 EX37 + EX50 
                 HB1 
                 2.8 
                 45 
                 0.41, 0.54 
                 650 
               
               
                 EX37 + EX55 
                 HB1 
                 2.5 
                 48 
                 0.41, 0.54 
                 650 
               
               
                 EX37 + EX56 
                 HB1 
                 2.5 
                 40 
                 0.41, 0.53 
                 600 
               
               
                 EX37 + EX57 
                 HB1 
                 2.5 
                 42 
                 0.41, 0.54 
                 650 
               
               
                 EX37 + EX42 
                 HB1 
                 3.0 
                 38 
                 0.41, 0.53 
                 660 
               
               
                 EX37 + EX44 
                 HB1 
                 2.8 
                 34 
                 0.40, 0.53 
                 550 
               
               
                 EX37 + EX51 
                 HB1 
                 3.2 
                 32 
                 0.41, 0.54 
                 560 
               
               
                 EX33 + EX50 
                 HB1 
                 2.5 
                 46 
                 0.41, 0.55 
                 600 
               
               
                 EX38 + EX50 
                 HB1 
                 2.8 
                 49 
                 0.41, 0.55 
                 720 
               
               
                 EX33 
                 HB1 
                 2.5 
                 36 
                 0.42, 0.56 
                 480 
               
               
                 EX37 
                 HB1 
                 2.6 
                 31 
                 0.43, 0.55 
                 500 
               
               
                 EX55 
                 HB1 
                 3.2 
                 40 
                 0.43, 0.54 
                 460 
               
               
                 EX57 
                 HB1 
                 3.0 
                 42 
                 0.42, 0.54 
                 550 
               
               
                   
               
             
          
         
       
     
         [0069]    In the above preferred embodiments for organic EL device test report (see Table 1 and Table 2), we show that the organic material formula (I) in the present invention used as hole blocking material, electron transport material and/or phosphorescent host display good performance than the prior art of organic EL materials. 
         [0070]    To sum up, the present invention discloses a novel organic material which can be used for organic EL device is disclosed. The mentioned organic material are represented by the following formula (I): 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein A ring represents a phenyl group and fused ring hydrocarbon units with two to four rings group, L represents a single bond, a substituted or unsubstituted divalent arylene group having 6 to 30 ring carbon atoms or a substituted or unsubstituted divalent heteroarylene group having 6 to 30 ring carbon atoms, R 1  to R 3  independently selected from the group consisting of a hydrogen atom, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, a substituted or unsubstituted aralkyl group having 6 to 30 carbon atoms and a substituted or unsubstituted heteroaryl group having 3 to 30 carbon atoms, Y 1  to Y 5  each independently represent nitrogen atom or CR 5 , R 5  independently represent a hydrogen atom, a substituted or unsubstituted phenylene group having 6 to 30 ring carbon atoms, or a bond linked to B; B stand for a group of following formula (II): 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein q represents an integer of 0 to 3, p represents an integer of 0 to 7, X represents O, S, NR 6 , R 6  independently represents a hydrogen atom, a substituted or unsubstituted phenyl group, a substituted or unsubstituted carbazole group, and a bond linked to formula (I), R 4  is the same definition as R 1 . 
         [0071]    Obvious many modifications and variations are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims the present invention can be practiced otherwise than as specifically described herein. Although specific embodiments have been illustrated and described herein, it is obvious to those skilled in the art that many modifications of the present invention may be made without departing from what is intended to be limited solely by the appended claims.