Abstract:
A process for rejuvenating a turbine disk having a plurality of slots includes the steps of determining a depth of a damaged layer containing M23C6 carbide dissolution; and removing the damaged layer from the slots in accordance with the determined depth.

Description:
BACKGROUND 
       [0001]    The present disclosure is directed to a process for rejuvenating turbine disks. 
         [0002]    Turbine disks can be fatigue limited in high temperature dwell environments due to initiation of fatigue cracks at the oxide surface. Turbine disks are typically made from nickel-based superalloys. One cause of fatigue life debit is microstructural dissolution near the oxide layer. Dissolution of M23C6 carbides near the surface is a prime driver in the fatigue failures. 
         [0003]    It is desirable to find a way to recover the life of these turbine disks. 
       SUMMARY 
       [0004]    In accordance with the present disclosure, there is provided a process for rejuvenating a turbine disk having a plurality of slots which broadly comprises the steps of determining a depth of a damaged layer containing M23C6 carbide dissolution; and removing the damaged layer from the slots in accordance with the determined depth. 
         [0005]    In another and alternative embodiment, the determining step comprises creating a model showing the depth of M23C6 carbide dissolution vs. time and temperature. 
         [0006]    In another and alternative embodiment, the process further comprises removing blades/buckets having an original size from the slots. 
         [0007]    In another and alternative embodiment, the removing step comprises remachining the slots. 
         [0008]    In another and alternative embodiment, the remachining step comprises using one of super abrasive machining, wire EDM, broaching, grinding, and milling. 
         [0009]    In another and alternative embodiment, the remachining step further comprises remachining other high temperature exposed surfaces. 
         [0010]    In another and alternative embodiment, the process further comprises installing new blades/buckets into the remachined slots having a size larger than a size of removed blades/buckets. 
         [0011]    Other details of the turbine disk fatigue rejuvenation are set forth in the following detailed description and the following drawings in which like reference numerals depict like elements. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0012]      FIG. 1  is a schematic representation of a turbine disk; 
           [0013]      FIG. 2  is a flow chart showing the process for rejuvenating a turbine disk. 
       
    
    
     DETAILED DESCRIPTION 
       [0014]    Referring now to  FIG. 1 , there is shown a turbine disk  10  forming one of the disks of a gas or steam turbine. The turbine disk  10  may be formed from a nickel-based superalloy or an iron based alloy. The turbine disk  10  has a plurality of generally dovetail-shaped slots  12  spaced circumferentially one form the other about the periphery of the margin of the turbine disk  10 . As illustrated, each slot  12  includes a slot bottom  14  and a plurality of ribs  16  along opposite slides of the slot  12  and progressively spaced greater distances from one another from the bottom of the slot  14  radially outward to its outermost opening. 
         [0015]    A blade or bucket  18  having a generally corresponding dovetail shaped configuration at its root as the dovetail configuration of the slot  12  is disposed in each slot  12  about the rotor. It will be appreciated that when the rotor rotates, the outermost surfaces of the ribs  16  of the dovetail slot and those of the surfaces of the ribs  16  of the dovetail slot and those of the blade or bucket dovetails constitute active surfaces  20  and  22 , respectively which tightly bear against one another. The opposing surfaces  24  and  26  of the slot and blade/bucket root, respectively, generally only lightly engage or are spaced relative to one another during operation of the turbine. Over time, the active surfaces wear and the disk requires refurbishment or overhaul. 
         [0016]    Referring now to  FIG. 2 , there is shown a flowchart showing a process for rejuvenating the turbine disk. In step  102 , a model is first developed which shows the depth of M23C6 carbide dissolution versus time and temperature for the nickel-based superalloy or iron based alloy forming the turbine disk. The model allows an understanding of the amount of material that must be removed to eliminate any region of M23C6 carbide dissolution. The model may be created using a pre-programmed computer which shows the depth of M23C6 carbide dissolution versus time and temperature for the material forming the turbine disk. 
         [0017]    In step  104 , prior to remachining the turbine disk  10 , the blades/buckets  18  are removed, leaving the bare slots  12 . 
         [0018]    In step  106 , once it is understood how much material must be removed from the turbine disk  10  to eliminate any region of M23C6 carbide dissolution, the disk slots  12 , as well as other high temperature exposed surfaces, are remachined to eliminate the unwanted regions of M23C6 carbide dissolution. The other high temperature exposed surfaces could be the outer rim or front face of the turbine disk  12 . The remachining step may be performed using super abrasive machining, wire EDM, broaching, grinding, milling, etc. to remove the damaged layer. During the remachining, the surfaces of the slots  12  are transformed by removing the determined damaged layer while retaining the dovetail configuration. 
         [0019]    Removal of the damaged layer increases the size of the slots  12 . Thus, the replacement blades/buckets  18  must be larger in size than the original blades/buckets. For example, the replacement blades/buckets may have a larger root portion than the root portion of the original blades/buckets. Additionally, the replacement blades/buckets may be larger from tip  30  to tip  32  of each dovetail than the original blades/buckets. In step  108 , the replacement blades/buckets  18  are installed. 
         [0020]    The method described herein causes a substantial increase in dwell fatigue life, thereby increasing the service life of a turbine disk. Depending on the conditions, the fatigue debit associated with oxidation can be as much or more than two times the non-oxidized life. 
         [0021]    There has been provided a turbine disk fatigue rejuvenation. While the turbine disk fatigue rejuvenation has been described in the context of specific embodiments thereof, other unforeseen alternatives, modifications, and variations may become apparent to those skilled in the art having read the foregoing description. Accordingly, it is intended to embrace those alternatives, modifications, and variations as fall within the broad scope of the appended claims.