Abstract:
A catalyst for the production of synthesis gas or hydrogen from aqueous methanol by dissociation or steam reforming. The catalyst contains: 
     (A) a metal component of one or more elements of the VIIIb group of the periodic table on a carrier material on the basis: 
     (B 1 ) of TiO 2  or CeO 2 , singly or in admixture with other heat-resistant metal oxides and/or binders or 
     (B 2 ) of TiO 2 , which is introduced onto the surface of a preformed, heat-resistant carrier. 
     Processes utilizing this catalyst allow for the dissociation of methanol for production of synthesis gas, or for the production of hydrogen through steam reforming. 
     Thus, the concentration of hydrogen or of carbon monoxide may be controlled by monitoring the concentration of steam utilized in the inlet feed.

Description:
FIELD OF THE INVENTION 
     This invention pertains to the production of hydrogen-rich gas mixtures from methanol. More specifically, this invention relates to an improved catalyst which may be used in the production of synthesis gas through the dissociation of methanol or in the steam reforming reaction for production of hydrogen. 
     Still more specifically, this invention relates to a process in which one reaction may be guided to predominate over the other by adjusting the amount of steam admitted with the methanol into the reactor, but without changing the catalyst in the reactor. Still more specifically, this invention relates to a catalyst which does not promote the deposition of coke even at low steam concentrations. 
     BACKGROUND OF THE INVENTION 
     In the last few years, methanol dissociation has been devoted a growing attention. The synthesis gas, composed of about 33 vol.% CO and 66 vol.% H 2 , can be obtained according to equation (1). 
     
         CH.sub.3 OH⃡CO+2H.sub.2                        ( 1) 
    
     Reaction (1) is highly endothermic and can be carried out at temperatures over 200° C. under atmospheric or lower methanol pressure with the help of certain heterogeneous catalysts. Thus, Inui, et al, J. Japan Petrol., Inst. 25, 121 (1982), investigated the effect of Ni--, Rh--, or Ru-- on SiO 2  -- catalyst in comparison to the commercial ZnO--Cr 2  O 3  -- methanol synthesis catalysts. The best results were obtained with Ni--Ru-on-La 2  O 3  or on-SiO 2 . This catalyst was far superior to the commercial ZnO--Cr 2  O 3  -- catalyst. However, with an increase of methanol conversion (over 30%), coke was laid down on the catalyst according to equations (2) and (3). 
     
         2CH.sub.3 OH→C+CO.sub.2 +4H.sub.2                   ( 2) 
    
     
         CH.sub.3 OH→C+H.sub.2 +H.sub.2 O                    (3) 
    
     Another industrially interesting reaction is the methanol steam reforming reaction, which follows equation (4) and leads to a gas mixture of 25 vol.% CO 2  and 75 vol.% H 2 . 
     
         CH.sub.3 OH+H.sub.2 ⃡CO.sub.2 +3H.sub.2        ( 4) 
    
     This endothermic reaction can be considered as a combination of methanol dissociation (1) and CO-water gas shift according to equation 5. 
     
         CO+H.sub.2 O→CO.sub.2 +H.sub.2                      ( 5) 
    
     DESCRIPTION OF THE PRIOR ART 
     Methanol reforming has, up till now, commanded a greater interest than the methanol dissociation. In order to accelerate the reaction of the methanol with steam, Cu-containing catalysts, preferably on Al 2  O 3 , SiO 2 , or Al 2  O 3  -- SiO 2 , were used (T. Inui, et al, J. Japan Petrol. Inst. 25, 63 (1982), K. Takahashi, et al, Appl. Catal. 2, 363 (1982)). 
     For the simultaneous methanol dissociation and methanol reforming, Co-, Ni-, Fe-, and precious metal catalysts on Al 2  O 3  are recommended as well as copper catalysts (J. Fuel Soc. Japan 59, 40 (1980)). These catalysts have, however, only a proportionally low thermal stability and tend to promote coke lay down, corresponding to equations (2) and (3), especially if the water content of the methanol is low. 
     SUMMARY OF THE INVENTION 
     The invention is based on the problem of creating a catalyst that is equally good under the conditions of the methanol dissociation (equation 1) and of the methanol steam reforming (equation 4), so that the process can be guided simply, by varying the steam content of the methanol used, either in the direction of synthesis gas production or in the direction of hydrogen production, without having to replace the catalyst. Such a catalyst should have a high stability under varying process conditions and also should not cause coke deposition if no steam is added or if the steam content is low, i.e., under the conditions of the methanol dissociation according to equation (1). 
     The object of the invention is, accordingly, a catalyst for the production of synthesis gas or hydrogen from aqueous methanol by dissociation or steam reforming, which is characterized by: 
     (A) a metal component of one or more elements of the eighth subgroup of the periodic table on a carrier material on the basis 
     (B 1 ) of TiO 2  or CeO 2 , if necessary in admixture with other refractory heat-resistant metal oxides, and/or hydraulic binders or cements or 
     (B 2 ) of TiO 2 , that is introduced onto the surface of refractories pre-formed from Al 2  O 3  or ceramic. 
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     The catalyst according to the invention makes it possible to carry out the process either under the conditions of the methanol dissociation (synthesis gas production) or under the conditions of methanol steam reforming (hydrogen production), whereby only the amount of added steam is varied. The catalyst according to the invention is stable under different process conditions and does not tend towards coking under the conditions of methanol dissociation. 
     Further, the catalyst according to the invention can also be used in the presence of oxygen, thus, under conditions under which the known copper catalysts are not stable. Since reactions (1) and (4) are endothermic, it is desirable in many cases to carry out the reactions in the presence of oxygen, so that an autothermic reaction process may be achieved. 
     For industrial use of the catalyst according to the invention, it is advantageous for the carrier material to be in shaped forms, such as tablets, spheres, rings, or honeycombs. 
     For the metal component, one or more precious metals from the eighth subgroup of the periodic table (group VIIIb) especially platinum, palladium, or rhodium may be used. Alloys of these metals can also be applied. 
     The precious metal concentration can be held proportionally low. Preferably the concentration is about 0.03-3 wgt.%, preferably 0.15-0.5 wgt.%, with reference to the total catalyst. 
     The concept &#34;heat-resistant metal oxide or refractory&#34; is to be taken in its broadest sense and includes mixed refractory metal oxides, spinels, metal aluminates and ceramics. Al 2  O 3  and Cr 2  O 3  are preferred heat-resistant metal oxides. 
     For increasing the stability of the catalyst, the TiO 2  or CeO 2  or a mixture of TiO 2  and CeO 2  and of other heat-resistant metal oxides can contain a hydraulic binder, such as calcium aluminate cement. The fraction of the calcium aluminate cement is in general 10-50 wgt.% preferably 25 wgt.% with reference to the total catalyst. 
     The catalysts according to the invention are generally produced as follows: 
     According to variant (B 1 ), shaped bodies, e.g. tablets, spheres on rings, are produced by pressing or extruding TiO 2  or CeO 2 , if necessary in admixture with other heat-resistant metal oxides. Preferably, a hydraulic cement is added to the titania, or to the mixture of titania and other heat-resistant metal oxides, before tableting. Finally, water is added to the mixture, in order to activate the hydraulic cement, whereupon the shaped bodies are produced by tableting. These are dried and, if necessary, hardened with steam, calcined and thereafter impregnated with the catalytically active metal component. 
     In order to facilitate the tableting, a lubricant, such as aluminum stearate and/or graphite, is added to the mass to be tableted. 
     According to variant (B 2 ), titanium dioxide is introduced onto the surface of a pre-formed, &#34;inert&#34; refractory or heat-resistant material, such as Al 2  O 3 , or ceramic, whereupon the so-treated shaped body is calcined and impregnated with the precious metal component. Pre-formed refractory ceramics include ceramic honeycombs in normal commercial usage, which excel in high stability. The ceramic material can be, for example, of cordierite or mullite. However, commercially available ceramic spheres and rings can also be used as pre-formed shaped bodies. 
     In order to incorporate the titanium dioxide onto the pre-formed shaped refractories, the shaped refractories are preferably impregnated with alkoxytitanates, such as tetraisopropyltitanate ((CH 3 ) 2  CHO) 4  Ti) or tetra-n-butyltitanate ((n-C 4  H 8  O) 4  Ti). The alkoxytitanates are thereafter hydrolyzed with steam and calcined. 
     According to both process variants, the impregnation of the carrier material with the metal component is carried out with the use of water-soluble precious metal salts, especially H 2  PtCl 6  or (NH 4 ) 2  PtCl 6  or the corresponding Pd- or Rh-salts. The so-produced catalyst precursor is then dried and calcined. The calcination of the impregnated carrier material is usually carried out at 450°-650° C., preferably at 550°-640° C. 
     In order to obtain the corresponding precious metals from the precious metal salts, the calcined catalyst precursor is activated by reduction with hydrogen. The reduction or activation can be done immediately after the calcination or in the reactor before start-up. 
     The subject of the invention is also the use of the previously described catalysts for the production of synthesis gas or hydrogen from aqueous methanol by dissociation or steam reforming. As is evident from equations (1) and (4), dissociation of methanol takes place in the abence of steam, while steam reforming according to equation (4) takes place in the presence of steam. Depending on the water content of the methanol, the process can be simply guided so that either one or the other reacton predominates. 
     If pure hydrogen, according to equation (4), or a synthesis gas with an excess of hydrogen is to be produced, the carbon dioxide formed according to equation (4) is removed from the gas mixture in a known manner. 
     In general, the conversion of the aqueous methanol takes place in the temperature range of about 300°-600° C., under atmospheric or lower pressure, whereby a space velocity of 0.05-20 liter/h.liter catalyst, with reference to the aqueous methanol, is used. Preferably, the conversion is carried out in the temperature range of 400°-500° C. at pressures of 0.1-1 bar, especially 0.75-1 bar, starting from methanol with a water content of 0.5-25 vol.%, preferably 2-10 vol.% at a space velocity of 2-8 liter/h.liter catalyst, with reference to the aqueous methanol. 
     The trials given in the following examples were carried out in a conventional metal tubular reactor (fixed bed flow system) with tabletted (4×4 mm) catalyst (50 ml) or with ceramic honeycombs (diameter 17 mm, length 150 mm) at atmospheric pressure in the temperature range of 300°-500° C. The methanol contained 1-68 vol.% steam. The space velocity was 1-10 liter/h.liter catalyst. The gases formed by the methanol dissociation were measured with the help of a gas meter and analyzed by gas chromatography. 
     The un-decomposed methanol or a mixture of methanol and water were condensed in a cooler, measured and analyzed by gas chromatography. 
    
    
     The invention is illustrated by the following examples, with reference to a comparison-catalyst, in a non-limiting fashion. 
     COMPARISON EXAMPLE 
     50 ml (58.6 g; 6.3×3.2 mm tablets) of a commercial, pre-reduced low-temperature water-gas shift catalyst (CC-1) (CuO about 35 wgt.%, ZnO about 65 wgt.%) were activated for three hours at 300° C. with hydrogen (50 liter/h) in a fixed bed flow reactor. The methanol dissociation (without H 2  O) is then carried out, with a liquid hourly space velocity of 2 liter methanol/h.liter catalyst, at 300°, 350° and 400° C. The methanol to be dissociated contained 2.2 vol.% H 2  O. The gas liberated by the catalytic reaction was measured and analyzed by gas chromatography (see Table II). 
     EXAMPLE 1 
     Commercial TiO 2  (BET surface area=45 m 2  /g) was formed into 4.5×4.5 mm tablets after the addition of 8 wgt.% Al-stearate as a lubricant or tableting aid. These tablets were heated up to 640° C. in air for 8 hours, then held at 640° C. for 1 hour and then cooled down again to room temperature. After impregnation with an aqueous H 2  PtCl 6  solution (at 25° C.), the Pt-containing tablets were dried (4 hours at 120° C.) and calcined at 400° C. (2 hours). The resulting catalyst (C-1) contained 0.3 wgt.% Pt, and its physical-mechanical data are given in Table I. 
     50 ml (75.3 g) of catalyst C-1 were heated for 3 hours at 400° C. in a stream of hydrogen (50 liter/h) in a fixed bed flow reactor. After cooling to 300° C., the methanol dissociation was begun in a way analogous to the comparison example. The results are given in Table II. 
     EXAMPLE 2 
     Commercial TiO 2  (BET surface area=45 m 2  /g) was first dry mixed with 25% calcium aluminate cement, then mix mulled after the addition of 60% H 2  O (with reference to the amount introduced). Shortly before the end of the mixing procedure, 3% of electro graphite was added. The wet mass was laid out in a thin layer and dried with air, until a loss due to drying (DL) at 120° C. of 8-12% was reached. Then this mass was pressed into cylindrical tablets of 4.5 mm diameter and 4.5 mm height. The tablets were cured in a closed container for 4 days and then steam-treated in an autoclave at 5.5 bar and 155° C. for 12 hours. Subsequently, the tablets were left lying out for a day and finally heated up to 640° C. within 3 hours and held at 640° C. for 1 hour. After cooling, the tablets were impregnated with an aqueous H 2  PtCl 6  solution, then dried at 120° C. (4 hours) and recalcined at 400° C. (2 hours). The catalyst (C-2) thus obtained contained 0.3 wgt.% Pt, and its physical-mechanical data are given in Table I. 50 ml (56.6 g) of catalyst C-2 were heated up to 400° C. by treatment for 3 hours in a stream of hydrogen (50 liter/h) in a fixed bed flow reactor. Ater cooling to 300° C., a methanol dissociation analogous to that of the comparison example was carried out. 
     The results are given in Table II. 
     EXAMPLE 2a 
     The production of the catalyst followed the procedure described in Example 2; however, instead of impregnating with Pt from the H 2  PtCl 6  solution, an aqueous solution of (NH 4 ) 2  PtCl 6 , with a pH of 10, was used. 
     The resulting catalyst (C-2a) contained 0.3 wgt.% Pt; its physical-mechanical data are given in Table I. 
     50 ml (59.0 g) of catalyst C-2a were activated by reduction with hydrogen as in Example 1 and a methanol dissociation carried out. 
     The results are given in Table III. 
     EXAMPLE 3 
     The production of the catalyst followed as described in Example 1. For the precious metal impregnating solution, however, a hydrochloric aqueous solution of PdCl 2  was used instead of the H 2  PtCl 6  solution. 
     The resulting catalyst (C-3) contained 0.3 wgt.% Pd; its physical-mechanical data are presented in Table I. 
     50 ml (76.3 g) of catalyst C-4 were reduced with hydrogen as in Example 1 and methanol dissociation carried out. 
     The results are given in Table IV. 
     EXAMPLE 4 
     The production of the catalyst followed the procedure described in Example 1. For the precious metal impregnating solution, however, a aqueous solution of H 2  RhCl 6  was used instead of the H 2  PtCl 6  solution. 
     The thus-obtained catalyst (C-4) contained 0.3 wgt.% Rh; its physical-mechanical data are given in Table I. 
     50 ml (71.2 g) of catalyst C-4 were reduced with hydrogen as in Example 1 and methanol dissociation carried out. 
     The results are given in Table IV. 
     EXAMPLE 5 
     The production of the catalyst followed the procedure described as in Example 1. For the platinum impregnating solution, however, an aqueous solution of H 2  PtCl 6  that was only half as concentrated as the one in Example 1 was used. The resulting catalyst (C-5) contained 0.15 wgt.% Pt; its physical-mechanical data are given in Table I. 
     50 ml (69.3 g) of catalyst C-6 were reduced with hydrogen as in Example 1 and methanol dissociation carried out. 
     The results are given in Table V. 
     EXAMPLE 6 
     The production of the catalyst followed the procedure described in Example 1. For the platinum impregnating solution, however, an aqueous solution of H 2  PtCl 6  that was only one-fourth as concentrated as that in Example 1 was used. 
     The resulting catalyst (C-6) contained 0.075 wgt.% Pt; its physical-mechanical data are given in Table I. 
     50 ml (70.5 g) of catalyst C-6 were reduced and activated with hydrogen as in Example 1 and methanol dissociation carried out. 
     The results are given in Table V. 
     EXAMPLE 7 
     Commercial CeO 2  (BET SA=43 m 2  /g) was formed into 4.5×4.5 mm tablets after the addition of 8 wgt.% Al-stearate. These tablets were heated to 640° C. for 1 hour, then cooled again to room temperature. After impregnation with an aqueous H 2  PtCl 6  solution (at 25° C.), the Pt-containing tablets were dried (120° C., 4 hours) and calcined at 400° C. (2 hours). The resulting catalyst (C-7) contained 0.3 wgt.% Pt. Its physical-mechanical data are given in Table I. 
     50 ml (92.5 g) of catalyst C-7 were heated to 400° C. and reduced for 3 hours in a stream of hydrogen (50 liter/hour) in a fixed bed flow reactor. After cooling to 300° C., methanol dissociation was begun as in the comparison example. The results are given in Table II. 
     EXAMPLE 8 
     A commercial ceramic honeycomb refractory with square openings of 1.5 mm side length was immersed at room temperature in tetraisopropyltitanate (TIPT) for 30 minutes. 
     The refractory carrier was then steam-treated in an autoclave at 5.5 bar and 155° C. for 12 hours for hydrolysis of the TIPT. It then was calcined in a muffle-furnace at 600° C. (2 hours); the ceramic honeycomb carrier contained 6 wgt.% TiO 2  after this treatment. 
     For impregnation with Pt, the TiO 2  -containing carrier was soaked with an aqueous solution of H 2  PtCl 6 , carefully dried, and recalcined at 400° C. (2 hours). 
     The resulting catalyst (C-8) contained 0.3% Pt; its physical-mechanical data are given in Table I. 
     50 ml (17.9 g) of catalyst C-8 were reduced with hydrogen as described in Example 1 and methanol dissociation was carried out. 
     The results are give in Table VI. 
     
                                           TABLE I__________________________________________________________________________Physical-Mechanical Data           BET-SA                BD CS PV  CompositionCat. No.Form       (m.sup.2 /g)                (g/l)                   (kg)                      (ml/g)                          (Weight %)__________________________________________________________________________CC-1 6 × mm Tabl.           49   1146                    8.1                      0.24                          CuO (35) ZnO (65)C-1  4.5 × 4.5 mm Tabl.           40   1426                   17.3                      0.13                          TiO.sub.2C-2  4.5 × 4.5 mm Tabl.           15   1131                   39.0                      0.22                          TiO.sub.2 (75) Ca--Al--CementC-2a 4.5 × 4.5 mm Tabl.           48   1180                   34.5                      0.20                          TiO.sub.2 (75) Ca--Al--CementC-3  4.5 × 4.5 mm Tabl.           19   1525                   24.6                      0.13                          TiO.sub.2C-4  4.5 × 4.5 mm Tabl.           21   1423                   15.1                      0.16                          TiO.sub.2C-5  4.5 × 4.5 mm Tabl.           20   1385                   20.4                      0.19                          TiO.sub.2C-6  4.5 × 4.5 mm Tabl.           20   1410                   20.3                      0.15                          TiO.sub.2C-7  4.5 × 4.5 mm Tabl.           47   1850                   12.5                      0.12                          CeO.sub.2C-8  Ceramic Honeycombs            8    358                   -- 0.14                          TiO.sub.2 (6.1)__________________________________________________________________________ Notes: BETSA = Specific surface area according to BET method BD =  Specific weight CS = Crush strength PV = Pore volume measured by Hg porosimeter 
    
     
                                           TABLE II__________________________________________________________________________Methanol Dissociation      Gas Amount             Composition (Vol. %)                         CondensateCatalyst T °C.      1/h (25° C.)             CO H.sub.2                   CO.sub.2                      CH.sub.4                         ml/h__________________________________________________________________________CC-1  300  72     20.1                73.1                   6.6                       0.20                         59 350  125    27.1                68.4                   4.1                       0.34                         30 400  167    29.0                67.1                   3.4                       0.50                          7C-1   300  85     26.7                66.4                   4.4                      2.5                         52 350  156    28.6                65.4                   3.5                      2.5                         12 400  181    28.5                65.1                   3.4                      3.0                          0C-2   300  46     29.9                66.2                   2.9                      1.0                         73 350  95     30.0                66.6                   2.4                      1.0                         46 400  150    30.0                66.8                   2.1                      1.1                         16C-3   300  84     18.1                72.9                   7.2                      1.8                         52 400  162    27.9                65.1                   3.5                      3.5                          9C-7   300  64     25.6                71.0                   3.0                      0.4                         63 350  137    28.4                68.2                   3.0                      0.4                         20 400  182    29.1                67.8                   2.6                      0.5                          0For 100% conversion      181.2  31.2                67.2                   1.6                      -- --__________________________________________________________________________ Cat: 50 ml, 4.5 × 4.5 mm Tablets, Feed: Methanol with 2.2 Vol. % H.sub.2 O, 100 ml/h 
    
     
                                           TABLE III__________________________________________________________________________Methanol Dissociation(Comparison Between Catalysts Produced withH.sub.2 PtCl.sub.6 or Pt-ammine Complex)      Gas Amount             Composition (Vol %)                         CondensateCatalyst T °C.      1/h (25° C.)             CO H.sub.2                   CO.sub.2                      CH.sub.4                         ml/h__________________________________________________________________________C-2   300  46     29.9                66.2                   2.9                      1.0                         73 350  95     30.0                66.6                   2.4                      1.0                         46 400  150    30.0                66.8                   2.1                      1.1                         16C-2a  300  45     31.0                65.7                   2.2                      1.1                         74 350  85     31.0                65.7                   2.1                      1.2                         51 400  154    29.8                66.7                   2.0                      1.5                         13C-3   300  84     18.1                72.9                   7.2                      1.8                         52 350  128    23.3                68.9                   5.5                      2.3                         28 400  162    27.9                65.1                   3.5                      3.5                          9C-3a  300  100    17.1                72.3                   8.8                      1.8                         43 350  149    22.1                69.2                   6.5                      2.2                         16 400  181    27.0                64.8                   4.8                      3.4                          0For 100% conversion      181.2  31.2                67.2                   1.6                      -- --__________________________________________________________________________ Cat: 50 ml, 4.5 × 4.5 mm Tablets, Feed: Methanol with 2.2 Vol. % H.sub.2 O, 100 ml/h 
    
     
                                           TABLE IV__________________________________________________________________________Methanol Dissociation(Comparison Between Pt-, Pd- and Rh-containing Catalysts)      Gas Amount             Composition (Vol. %)                         CondensateCatalyst T °C.      1/h (25° C.)             CO H.sub.2                   CO.sub.2                      CH.sub.4                         ml/h__________________________________________________________________________C-1   300  85     26.7                66.4                   4.4                      2.5                         52 350  156    28.6                65.4                   3.5                      2.5                         12 400  181    28.5                65.1                   3.4                      3.0                          0C-3   300  36     23.6                59.2                   5.7                      11.5                         79 350  102    24.9                57.0                   6.0                      12.1                         42 .sup. 400.sup.1      71     23.3                60.7                   3.7                      12.3                         59 .sup. 400.sup.2      40     18.7                65.6                   2.2                      13.5                         76C-4   300  58     24.1                66.1                   6.1                      3.7                         66 350  136    25.2                64.1                   5.7                      5.0                         23 400  181    24.2                63.6                   6.5                      5.7                          0For 100% conversion      181.2  31.2                67.2                   1.6                      -- --__________________________________________________________________________ .sup.1 2h running time .sup.2 31/2 h running time, instable Cat: 50 ml, 4.5 × 4.5 mm tablets, Feed: Methanol with 2.2 Vol. % H.sub.2 O, 100 ml/h 
    
     
                                           TABLE V__________________________________________________________________________Methanol Dissociation(Effect of the Pt- Concentration)      Gas Amount             Composition (Vol. %)                         CondensateCatalyst T °C.      1/h (25° C.)             CO H.sub.2                   CO.sub.2                      CH.sub.4                         ml/h__________________________________________________________________________C-1   300  85     26.7                66.4                   4.4                      2.5                         52 350  156    28.6                65.4                   3.5                      2.5                         12 400  181    28.5                65.1                   3.4                      3.0                          0C-5   300  85     27.3                66.5                   4.0                      2.2                         51 350  155    29.5                65.6                   2.7                      2.2                         13 400  181    29.2                65.5                   2.9                      2.4                          0C-6   300  61     28.7                65.6                   3.7                      2.0                         65 350  128    30.6                65.2                   2.3                      1.9                         28 400  181    30.7                64.9                   2.2                      2.2                          0For 100% conversion      181.2  31.2                67.2                   1.6                      -- --__________________________________________________________________________ Cat.: 50 ml, 4.5 × 4.5 mm tablets, Feed: Methanol with 2.2 Vol. % H.sub.2 O, 100 ml/h 
    
     
                                           TABLE VI__________________________________________________________________________Methanol Dissociation(Comparison Between Different Catalyst Forms)      Gas Amount             Composition (Vol. %)                         CondensateCatalyst  T °C.      1/h (25° C.)             CO H.sub.2                   CO.sub.2                      CH.sub.4                         ml/h__________________________________________________________________________C-1    300 85     26.7                66.4                   4.4                      2.5                         52(Tablets)  350 156    28.6                65.4                   3.5                      2.5                         12  400 181    28.5                65.1                   3.4                      3.0                          0C-8    300 33     33.0                65.3                   0.6                      1.1                         80(Ceramic  350 73     32.9                65.2                   0.6                      1.3                         58Honeycombs)  400 120    32.7                65.1                   0.7                      1.5                         32C-10   300 46     26.1                72.2                   0.6                      1.1                         73(Spheres)  350 92     27.3                70.6                   0.9                      1.2                         48  400 133    29.3                68.1                   1.0                      1.6                         25C-11   300 59     31.2                66.3                   0.7                      1.8                         66(Spheres)  350 125    30.9                66.2                   1.0                      1.9                         29  400 169    31.2                65.1                   1.5                      2.2                          5For 100% conversion      181.2  31.2                67.2                   1.6                      -- --__________________________________________________________________________ Catalyst: 50 ml Feed: Methanol with 2.2 Vol. % H.sub.2 O, 100 ml/h 
    
     
                                           TABLE VII__________________________________________________________________________Methanol Dissociation(Effect of the Methanol Space Velocity)      Gas Amount             Composition (Vol. %)                         CondensateLHSV  T °C.      1/h (25° C.)             CO H.sub.2                   CO.sub.2                      CH.sub.4                         ml/h__________________________________________________________________________2     300  85     27.3                66.5                   4.0                      2.2                         512     350  155    29.5                65.6                   2.7                      2.2                         132     400  181    29.2                65.5                   2.9                      2.4                          0100% conversion      181.2  31.2                67.2                   1.6                      -- --4     400  283    31.3                64.7                   1.9                      2.1                         20For 100% conversion      362.4  31.2                67.2                   1.6                      -- --__________________________________________________________________________ Catalyst: C6, 50 ml, 4.5 × 4.5 mm tablets, Feed: Methanol with 2.2 Vol. % H.sub.2 O, 100 ml/h 
    
     
                                           TABLE VIII__________________________________________________________________________Methanol Dissociation and Reforming(Effect of the Water Content in the Methanolon the Gas Composition and the Gas Amount Obtained)H.sub.2 O Content               CondensateIn Methanol  Gas Amount               Composition (Vol. %)                              H.sub.2 O content(Vol. %) T °C.        1/h (25° C.)               CO H.sub.2                     CO.sub.2                        CH.sub.4                           ml/h                              (%)__________________________________________________________________________2.0      350 156    28.6                  65.4                      3.5                        2.5                           12 23.0(H.sub.2 O/CH.sub.3 OH    400 181    28.5                  65.1                      3.4                        3.0                           -- --mol. ratio = 0.04)41.3     350 131    9.4                  72.0                     17.5                        1.1                           25 86.0(H.sub.2 O/CH.sub.3 OH    400 145    7.4                  73.2                     18.4                        1.0                           22 98.0mol. ratio = 1.56)68.0     350 78.0   1.8                  75.4                     22.5                        0.3                           53 99.9(H.sub.2 O/CH.sub.3 OH    400 78.2   1.5                  75.1                     22.8                        0.6                           54 100.0mol. ratio = 4.73)__________________________________________________________________________ Catalyst: C1, 50 ml, 4.5 × 4.5 mm tablets, LHSV = 2 (CH.sub.3 OH + H.sub. 2 O)