Abstract:
An SEM measurement standard for measuring linewidths of 0.1 microns and below utilizes two different conducting materials in order to prevent charging effects. The top material is selected to use grain morphology to focus secondary electrons, and to obtain improved image contrast. The inventive standard is comprised of materials which are commonly used in semiconductor manufacturing and which do not cause contamination of fabrication facilities.

Description:
FIELD OF THE INVENTION 
     This invention deals with metrology standards, and in particular with metrology standards as applied to Scanning Electron Microscopy used for measurement of Critical Dimensions (CD&#39;s) in integrated circuit manufacturing technology. 
     BACKGROUND OF THE INVENTION 
     As integrated circuits become smaller and faster, the critical dimensions (CD&#39;s) of the devices and interconnections also must decrease. As these CD&#39;s get closer to the resolution limits of optical lithography and microscopy measurement techniques, great care must be taken to eliminate all possible sources of measurement error in order to obtain accurate and reproducible critical dimensions. One nearly universally used measurement technique is Scanning Electron Microscopy (SEM), which utilizes highly focused energetic beams of electrons impinging on the sample and measures the yield of secondary emitted electrons. SEM is the most widely used tool for VLSI measurement and morphology analysis, due to its high resolution and relative ease of use. 
     FIG. 1 depicts an SEM system, showing the electron source and the acceleration, focusing, and detection electronics. FIG. 2 shows a typical electron emission energy spectrum resulting from the incident electron beam of an SEM. The highest energy peak  18  results from the backscattered electrons, which have energies close to that of the incident beam, and which have undergone only elastic collisions with the target atoms. Peaks  20  seen at intermediate energies are the Auger electrons emitted due to relaxation of electrons between atomic energy levels. The lowest energy emitted electrons  22 , produced by inelastic collisions between the primary beam and the inner shell electrons of the sample, are known as the secondary electrons and are generally the most useful for morphology studies in VLSI. This is due in part to the extremely short escape depth (less than about 50 Angstroms) of secondary electrons, which yields high surface sensitivity. In addition, since the incident electron beam undergoes beam broadening due to multiple collisions as it penetrates into the sample, the backscattered electrons originating from deeper into the sample reflect this broadening with degraded point-to-point resolution. The lower energy secondary electrons which escape the sample originate from the surface region above the penetration depth where beam broadening becomes influential, and therefore yield higher point-to-point resolution than evidenced by backscattered electrons. 
     The detected electron current, typically chosen to be the secondary electron current as described above, is used to intensity modulate the z-axis of a CRT. An image of the sample surface is produced by synchronously raster scanning the CRT screen and the electron beam of the SEM. 
     The contrast of the image depends on variations in the electron flux arriving at the detector, and is related to the yield of emitted electrons per incident electron. The yield is dependent on both the work function of the material and the surface curvature. These factors allow the SEM to distinguish between materials such as metal, oxide, and silicon, and also to distinguish surfaces which differ in slope. Thus, Critical Dimensions (CD&#39;s) of patterned and/or etched lines and gaps can be measured. 
     Two factors affecting the accuracy of SEM measurements are resolution and charging effects. The resolution of the SEM depends on the type of sample under inspection and on the incident beam diameter or “spot size”. The high voltages of the electron beam required to produce small scanning spot sizes were historically one source of charging when examining insulating surfaces. When incident beam energies exceeded the secondary electron crossover point, i.e., when the incident beam penetration depth was high enough that the number of emitted secondary electrons was less than the number of incident electrons, the surface in the region of the scanning beam would acquire excess negative charge, which would be retained in the case of exposed insulating surfaces. This would cause the incident beam trajectory to be disturbed, and would therefore degrade the image. Grounding schemes such as coating the surface with a conducting material, e.g., gold, and attaching a ground wire to the coating were used to reduce charging effects. These methods prohibited further processing following inspection of wafers. More recent SEM machines have eliminated high energy accelerating voltages, thus decreasing the corresponding charging effects. However, these low voltage SEM&#39;s have poorer resolution (approximately 40-50 A resolution for 600 V SEM) than the corresponding high-voltage SEM&#39;s (approximately 5-10 A for 20-50 KV SEM). Charging of insulating surfaces can result from factors other than the SEM electron beam, such as processing-induced charging. 
     Calibration standards are necessary when using SEM&#39;s, in order to assure that magnification factors are accurate and to thereby assure accurate sizes as measured by SEM photographs. Conductor-coated (generally gold-coated) standard samples with features measured to high accuracy are still used to calibrate, i.e., to verify CD&#39;s and spacings as measured in low-voltage SEM&#39;s. Although this method is one way of producing measurement standards, it has the disadvantage of degrading image contrast, since the underlying layers are partially obscured by the conducting coating. Additionally, gold-coated standards cannot be used in fabrication facilities since the presence of gold incurs the risk of drastically lowering the carrier lifetime in silicon. 
     If measurement standards having exposed insulating layers are used without a conducting coating in order to achieve maximum contrast, variations in charging will induce variations in measurement, and therefore the calibration standard will drift as a function of time. 
     In order to achieve a calibration standard which will be effective for measuring linewidths less than 0.1 microns, for polysilicon by way of example, it is beneficial that the standard have a grainy structure at the top surface of the features (which provides focus improvement for the e-beam) while not being grainy on the feature sidewalls (which would result in measurement variations along the line), that the standard has a vertical and smooth sidewall profile, that it can be patterned as finely as the linewidths being measured, that it is not susceptible to charging effects, and that it yields good image contrast. Currently available SEM standards do not fulfill these requirements, and in particular are generally subject to significant charging effects. 
     SUMMARY OF THE INVENTION 
     It is therefore an object of this invention to provide an improved SEM measurement standard which is not subject to surface charging. 
     It is a further object of this invention to provide an improved SEM measurement standard which improves image contrast and e-beam focus. 
     It is a further object of this invention to provide an improved SEM measurement standard which can be patterned to linewidths of 0.1 microns or less, with vertical and smooth sidewall profile. 
     These objects are met by creating an SEM measurement standard having two different conducting layers comprised of materials used in semiconductor fabrication. 
    
    
     BRIEF DESCRIPTION OF THE FIGURES 
     FIG. 1 depicts an SEM system, showing the electron source and the acceleration, focusing, and detection electronics. 
     FIG. 2 is a typical electron emission energy spectrum resulting from the incident electron beam of an SEM. 
     FIG. 3 shows the inventive structure for an SEM measurement standard. 
     FIG. 4 a  illustrates an isolated line according to a second embodiment of the invention. 
     FIG. 4 b  illustrates dense lines according to the second embodiment of the invention. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     FIG. 1 is a schematic diagram of an SEM system, showing incident electron beam  2  impinging on sample  4 . The secondary electrons are collected and detected at detector  6 . Electron beam source  8 , accelerating and focusing electrodes  10 , lens apparatus  12 , scan control  14 , and monitor  16  are also shown. 
     FIG. 2 shows a representative spectrum of emitted electrons, including backscattering peak  18  at near the incident beam energy, Auger peaks  20 , and secondary electron emission peak  22  at lower energy. In general, secondary electrons  22  are those detected for the SEM&#39;s. 
     The inventive SEM measurement standard structure is comprised of two different conducting layers having different conductivity and/or density and thereby having different appearance in SEM photographs. As a result, good image contrast is achieved while the problem of surface charging is solved. The conducting layers are preferably composed of materials which are already used and accepted within fabrication areas. This would allow fabs to build their own verification standards using their existing processing equipment and mask sets, thereby eliminating cross contamination risk which would occur from commercially produced standards. 
     In a preferred embodiment of the invention a tungsten silicide (WSi x ) feature is patterned on a titanium or titanium nitride layer on a silicon wafer according to the following process flow: 
     Step  24  Provide a silicon substrate 
     Step  26  Deposit or grow a silicon dioxide layer thereon (by industry standard processes such as thermal oxidation, LPCVD, or PECVD by way of example), preferably of thickness greater than 500 A, to promote adhesion of titanium and to prevent a chemical reaction between titanium and silicon. The silicon dioxide layer must have a thickness of sufficient magnitude to prevent titanium-silicon reduction reactions from penetrating through the silicon dioxide. The minimum thickness depends on the thickness of the Ti layer. 
     Step  28  Deposit by sputtering or chemical vapor deposition a Ti or TiN layer of sufficient thickness to serve as an etch stop for WSi x  etch, preferably between 500 and 5000 A thickness 
     Step  30  Deposit by chemical vapor deposition a WSi x  film which can be patterned with high fidelity, preferably between 500 and 3000 A thickness 
     Step  32  Pattern and etch the WSi x  film, stopping on the underlying Ti or TiN film, using standard deep-UV photoresist lithography and plasma etch techniques. 
     The resulting structure is shown in cross section in FIG.  3 . Patterned and etched WSi x  feature  34  is shown atop Ti or TiN film  35 , with oxide layer  36  underlying, and silicon substrate  38 . 
     Structures included on the SEM standard include but are not restricted to: 1) L-shaped patterns; 2) equal lines/spaces; 3) isolated lines; 4) isolated spaces; 5) dense spaces; 6) dense and isolated contact holes. 
     A second embodiment of the invention further decreases charging effects by connecting all metal features to dissipate any local charge buildup. FIG. 4 a  shows an example of an isolated line feature according to this embodiment. Isolated WSi x  line  40  is connected at one end to interconnection lines  42  (also formed of WSi x ) traverse the standard and which are also connected to the other features on the standard. FIG. 4 b  similarly shows dense WSi x  lines  44  connected to interconnection lines  42 . 
     WSi x  features atop Ti or TiN nitride provide good image contrast, good grain morphology for focusing the e-beam at the best imaging conditions, and are not subject to surface charging, therefore exhibiting stability over time. The inventive SEM WSi x /Ti[N] standard structure is comprised of materials commonly used in semiconductor processing, with well developed deposition and etch processes already in place in the art to permit patterning of features equivalent in width and critical dimension to polysilicon gate dimensions. 
     Although the inventive structure is described herein according to the preferred embodiment, it will be clear to those skilled in the art that variations of the described structure and process flow may be used without departing from the inventive concept. For example, Ta or TaN x  might be used in place of Ti and TiN. WSi x  might be replaced by W or heavily doped polysilicon. Other possible materials commonly used in fabrication facilities which might be utilized include nickel, aluminum, cobalt, platinum, and their suicides. 
     The scope of the invention should be construed in view of the claims.