Abstract:
A wafer-level package for semiconductor devices and a method for making the package. At least one dielectric layer is selectively printed on at least a portion of the semiconductor devices creating first recesses aligned with a plurality of electrical terminals on the semiconductor devices. A conductive material is printed in the first recesses to form contact members on the semiconductor devices. At least one dielectric layer is selectively printed to create a plurality of second recesses corresponding to a target circuit geometry. A conductive material is printed in at least a portion of the second recesses to create a circuit geometry. The circuit geometry includes a plurality of exposed terminals adapted to electrically couple to another circuit member. The wafer is diced to provide a plurality of discrete packaged semiconductor devices.

Description:
TECHNICAL FIELD 
       [0001]    The present application is directed to leveraging the capabilities of additive printing processes to provide a wafer level semiconductor package that results in a high performance packaged IC devices after wafer dicing. 
       BACKGROUND OF THE INVENTION 
       [0002]    Traditional semiconductors and IC devices are typically packaged in a variety of ways to provide redistribution from the terminals on the die to a spacing that is conducive to cost effective printed circuit board (“PCB”) fabrication techniques. In many cases, the size and distance between die terminals is so small that the device cannot be connected to the final PCB without some sort of fan out or routing. The packages also serve to protect the fragile silicon or provide additional functions such as thermal management or near device decoupling. In many cases, the size and distance between die terminals is so small that the IC device cannot be connected to the final PCB without some sort of re-routing interface. 
         [0003]    Most IC devices are produced with terminals in either a peripheral pattern that runs along the edges of the IC device or an area array pattern that spans across the surface of the IC device. A main method for attachment when the terminals are in an area array pattern is to connect the terminals with solder. Basically, the package has an array of terminals that correspond to the IC device terminals. Solder is applied the terminals on the IC device and/or the package and reflowed to create the mechanical and electrical connection in a process commonly called flip chip attachment. In a flip chip attachment the IC device is flipped over to mate the terminals on the die to the terminals on the IC package substrate. 
         [0004]    The IC devices in these types of packages are often under filled with an epoxy of some type to provide support and strength to the solder joints. The epoxy protects the solder joints during use from thermal expansion, miss-match and/or shock. In both cases, the connection of the IC device to the package is generally not reworkable once packaged and if there is a missing or broken connection it is difficult to repair. 
         [0005]    Once the IC devices are packaged, they are usually tested in a variety of ways to determine the reliability and performance of the IC devices in the package as they would be used in the final application. In many cases, the functional performance of the IC device is not known prior to placing it into the package and if the packaged IC device fails testing the cost of the package and processing is lost. 
         [0006]    A packaging method that has increased in popularity in recent years is called Wafer Level Packaging, where the packaging materials are applied to the IC devices directly while they are still in the wafer format prior to dicing. This method has shown to be effective for relatively small pin count devices and has some advantages over handling individual IC devices and packaging them in an offline operation. Wafer Level packages tend to have routing and termination that is within the footprint of the die and not fanned out due to the fact that the fan out would be cut when the wafer is diced. 
         [0007]    Area array packaging has been utilized for many years, and provides a method for interconnecting IC devices with larger terminal counts than peripheral lead packaging. In general, the area array packaging is more expensive due to the larger pin counts and more sophisticated substrates required. The main limitations for area array packaging are the terminal pitch, thermal management, cost, ability to rework faulty IC devices and reliability of the solder joints. 
       BRIEF SUMMARY OF THE INVENTION 
       [0008]    The present disclosure is directed to providing a wafer level semiconductor package. The present semiconductor package preferably permits the IC devices to be tested prior to, or after, dicing. 
         [0009]    The present wafer level semiconductor package resembles a traditional package in construction, but utilizes additive printing processes rather than conventional subtractive processes. The unique nature of the additive printing processes allows for a direct writing of circuitry and dielectrics, with the added benefit of stress decoupling at the terminal joints as well as embedded function not seen in traditional wafer-level packaging. 
         [0010]    The use of additive printing processes permits the material set in a given layer to vary. Traditional PCB and flex circuit fabrication methods take sheets of material and stack them up, laminate, and/or drill. The materials in each layer are limited to the materials in a particular sheet. Additive printing technologies permit a wide variety of materials to be applied on a layer with a registration relative to the features of the previous layer. Selective addition of conductive, non-conductive, or semi-conductive materials at precise locations to create a desired effect has the major advantages in tuning impedance or adding electrical function on a given layer. Tuning performance on a layer by layer basis relative to the previous layer greatly enhances electrical performance. 
         [0011]    One embodiment is directed to a wafer including a plurality of semiconductor devices. At least one dielectric layer is selectively printed on at least a portion of the wafer to create a plurality of first recesses aligned with a plurality of electrical terminals on the semiconductor devices. A conductive material is printed in the first recesses to form contact members on the semiconductor devices. At least one dielectric layer is selectively printed to create a plurality of second recesses corresponding to a target circuit geometry. A conductive material is printed in at least a portion of the second recesses to create a circuit geometry. The circuit geometry includes a plurality of exposed terminals adapted to electrically couple to another circuit member. The wafer is then diced to provide a plurality of discrete packaged semiconductor devices. 
         [0012]    Conductive plating is preferably added to one or more of the contact members and the circuit geometry. The conductive material can be sintered conductive particles or a conductive ink. In one embodiment, a compliant material is located between the exposed terminals and the semiconductor device. In another embodiment, at least one electrical device is printed on a dielectric layer and electrically coupled to at least a portion of the circuit geometry. In one embodiment, the exposed terminals extend above the package. 
         [0013]    The resulting circuit geometry preferably has conductive traces that have substantially rectangular cross-sectional shapes, corresponding to the second recesses. The use of additive printing processes permit conductive material, non-conductive material, and semi-conductive material to be located on a single layer. 
         [0014]    In one embodiment, pre-formed conductive trace materials are located in the second recesses. The second recesses are than plated to form conductive traces with substantially rectangular cross-sectional shapes. 
         [0015]    In another embodiment, a conductive foil is pressed into at least a portion of the second recesses. The conductive foil is sheared along edges of the second recesses. The excess conductive foil not located in the second recesses is removed and the second recesses are plated to form conductive traces with substantially rectangular cross-sectional shapes. 
         [0016]    In another embodiment, at least one external dielectric layer extends beyond the discrete packaged semiconductor devices. External routing is printed on the external dielectric layer and electrically coupled to a portion of the circuit geometry. 
         [0017]    The discrete packaged semiconductor devices can include a plurality of semiconductor devices. The circuit geometry may include at least one of an inter-die circuit path or an intra-die circuit paths. The plurality of semiconductor devices are optionally arranged in a stacked configuration. 
         [0018]    The present disclosure is also directed to an electrical assembly including a circuit member with a plurality of contact pads electrically coupled to the exposed terminals on the wafer-level semiconductor package. This coupling can be done before dicing of the wafer or on the discrete packaged semiconductor devices. The circuit member can be selected from one of a dielectric layer, a printed circuit board, a flexible circuit, a bare die device, an integrated circuit device, organic or inorganic substrates, or a rigid circuit. 
         [0019]    This present discrete packaged semiconductor devices provide internal and/or external compliance to enhance the mechanical performance. The present discrete packaged semiconductor devices can be produced digitally, without tooling or costly artwork. The wafer-level semiconductor package can be produced as a “Green” product, with dramatic reductions in environmental issues related to the production of conventional semiconductor packages. 
         [0020]    The present disclosure is also directed to a method of making a wafer-level semiconductor package. The method includes the step of printing at least one dielectric layer selectively on at least a portion of a wafer having a plurality of the semiconductor devices to create first recesses aligned with electrical terminals on the semiconductor devices. A conductive material is printed in a plurality of the first recesses to form contact members on the semiconductor devices. At least one dielectric layer is selectively printed on at least a portion of the wafer to create a plurality of second recesses corresponding to a target circuit geometry. A conductive material is printed in at least a portion of the second recesses to form a circuit geometry. The circuit geometry includes a plurality of exposed terminals electrically coupled to the semiconductor devices. The wafer is then diced into a plurality of discrete packaged semiconductor devices. 
         [0021]    The present disclosure is also directed to several additive processes that combine the mechanical or structural properties of a polymer material, while adding metal materials in an unconventional fashion, to create electrical paths that are refined to provide electrical performance improvements. By adding or arranging metallic particles, conductive inks, plating, or portions of traditional alloys, the compliant printed semiconductor package reduces parasitic electrical effects and impedance mismatch, potentially increasing the current carrying capacity. 
         [0022]    The printing process permits the fabrication of functional structures, such as conductive paths and electrical devices, without the use of masks or resists. Features down to about 10 microns can be directly written in a wide variety of functional inks, including metals, ceramics, polymers and adhesives, on virtually any substrate—silicon, glass, polymers, metals and ceramics. The printing process is typically followed by a thermal treatment, such as in a furnace or with a laser, to achieve dense functionalized structures. 
         [0023]    The wafer-level semiconductor package can be configured with conductive traces that reduce or redistribute the terminal pitch, without the addition of an interposer or daughter substrate. Grounding schemes, shielding, electrical devices, and power planes can be added to the semiconductor package, reducing the number of connections to the PCB and relieving routing constraints while increasing performance. 
     
    
     
       BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING 
         [0024]      FIG. 1  is a cross-sectional view of a method of making a wafer level semiconductor package in accordance with an embodiment of the present disclosure. 
           [0025]      FIG. 2  illustrates a method of printing dielectric material on the semiconductor package of  FIG. 1 . 
           [0026]      FIG. 3  illustrates a method of printing contact members on the semiconductor package of  FIG. 1 . 
           [0027]      FIGS. 4 and 5  illustrate a method of printing circuit geometry on the semiconductor package of  FIG. 1 . 
           [0028]      FIG. 6  illustrates a wafer level semiconductor package before dicing in accordance with an embodiment of the present disclosure. 
           [0029]      FIG. 7  illustrates the semiconductor package of  FIG. 6  after dicing. 
           [0030]      FIG. 8  illustrates a plurality of discrete packaged semiconductor devices after dicing in accordance with an embodiment of the present disclosure. 
           [0031]      FIG. 9  illustrates an alternate packaged semiconductor with printed compliant circuit geometry in accordance with an embodiment of the present disclosure. 
           [0032]      FIG. 10  illustrates the packaged semiconductor of  FIG. 9  electrically coupled to another circuit member in accordance with an embodiment of the present disclosure. 
           [0033]      FIG. 11  illustrates an alternate packaged semiconductor with printed electrical devices in accordance with an embodiment of the present disclosure. 
           [0034]      FIG. 12  illustrates the packaged semiconductor of  FIG. 11  electrically coupled to another circuit member in accordance with an embodiment of the present disclosure. 
           [0035]      FIG. 13  illustrates a stacked multichip packaged semiconductor in accordance with an embodiment of the present disclosure. 
           [0036]      FIG. 14  illustrates a layered multichip packaged semiconductor in accordance with an embodiment of the present disclosure. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0037]      FIG. 1  is a side sectional view of semiconductor wafer  50  containing a plurality of IC devices  52 A,  52 B,  52 C (collectively “ 52 ”) located on substrate  54 . The IC terminals  56  are facing up. The substrate  54  may be a temporary work surface or may be a portion of the final semiconductor package. The substrate  54  can be constructed from a variety of rigid or flexible polymeric materials, such as for example, UV stabilized tetrafunctional epoxy resin systems referred to as Flame Retardant 4 (FR-4); bismaleimide-triazine thermoset epoxy resins referred to as BT-Epoxy or BT Resin; and liquid crystal polymers (LCPs), which are polyester polymers that are extremely unreactive, inert and resistant to fire. Other suitable plastics include phenolics, polyester (PET), polyimide (PI), polyethylene napthalate (PEN), Polyetherimide (PEI), along with various fluoropolymers (FEP) and copolymers, and Ryton® available from Phillips Petroleum Company. For some applications, the substrate  54  can be a polyimide film due to their advantageous electrical, mechanical, chemical, and thermal properties. 
         [0038]      FIG. 2  illustrates printed layer  58  printed to top surface  60  of the wafer  50  at locations  62  between IC terminal  56 . The printed layer  58  at locations  62  creates one or more recesses  64  corresponding to each of the IC terminals  56  that are used in subsequent steps of the process. 
         [0039]    As illustrated in  FIG. 3 , the recesses  64  for the IC terminals  56  are metalized to create contact members  70 . Metalizing can be performed by printing conductive particles followed by a sintering step, by printing conductive inks, or a variety of other techniques. The metalizing material is preferably of copper or similar metallic materials such as phosphor bronze or beryllium-copper. The resulting contact members  70  are optionally plated to improve conductive properties. The plating is preferably a corrosion resistant metallic material such as nickel, gold, silver, palladium, or multiple layers thereof. 
         [0040]    As illustrated in  FIG. 4 , dielectric layer  72  is printed on surface  74  with recesses or trenches  76  corresponding to a desired circuit geometry. Alternatively, the dielectric layer  72  is placed on surface  74 . The recesses  76  can be defined by printing, embossing, imprinting, chemical etching with a printed mask, or a variety of other techniques. As illustrated in  FIG. 5 , the recesses  76  are metalized as discussed above to create circuit geometry  78 . 
         [0041]    The printed dielectric layers  58 ,  72  may be constructed of any of a number of dielectric materials that provide electrostatic dissipation or to reduce cross-talk between the traces of the circuit geometry  78 . An efficient way to prevent electrostatic discharge (“ESD”) is to construct one of the layers from materials that are not too conductive but that will slowly conduct static charges away. These materials preferably have resistivity values in the range of 10 5  to 10 11  Ohm-meters. 
         [0042]    In one embodiment, the circuit geometry  78  is formed by depositing a conductive material in a first state in the recesses  76 , and then processed to create a second more permanent state. For example, the metallic powder is printed according to the circuit geometry and subsequently sintered, or the curable conductive material flows into the circuit geometry and is subsequently cured. As used herein “cure” and inflections thereof refers to a chemical-physical transformation that allows a material to progress from a first form (e.g., flowable form) to a more permanent second form. “Curable” refers to an uncured material having the potential to be cured, such as for example by the application of a suitable energy source. 
         [0043]    The recesses  64 ,  76  in the layers  58 ,  72  permit control of the location, cross section, material content, and aspect ratio of the contact members  70  and the conductive traces in the circuit geometry  78 . Maintaining the conductive traces with a cross-section of 1:1 or greater provides greater signal integrity than traditional subtractive trace forming technologies. For example, traditional methods take a sheet of a given thickness and etches the material between the traces away to have a resultant trace that is usually wider than it is thick. The etching process also removes more material at the top surface of the trace than at the bottom, leaving a trace with a trapezoidal cross-sectional shape, degrading signal integrity in some applications. Using the recesses  64 ,  76  to control the aspect ratio of the conductive traces results in a more rectangular or square cross-section of the conductive traces in the circuit geometry  78 , with the corresponding improvement in signal integrity. 
         [0044]    In another embodiment, pre-patterned or pre-etched thin conductive foil circuit traces are transferred to the recesses  64 ,  76 . For example, a pressure sensitive adhesive can be used to retain the copper foil circuit traces in the recesses  64 ,  76 . The trapezoidal cross-sections of the pre-formed conductive foil traces are then post-plated. The plating material fills the open spaces in the recesses  64 ,  76  not occupied by the foil circuit geometry, resulting in a substantially rectangular or square cross-sectional shape corresponding to the shape of the recesses  64 ,  76 . 
         [0045]    In another embodiment, a thin conductive foil is pressed into the recesses  64 ,  76 , and the edges of the recesses  64 ,  76  act to cut or shear the conductive foil. The process locates a portion of the conductive foil in the trenches  64 ,  76 , but leaves the negative pattern of the conductive foil not wanted outside and above the trenches  64 ,  76  for easy removal. Again, the foil in the trenches  64 ,  76  is preferably post plated to add material to increase the thickness of the conductive traces in the circuit geometry  78  and to fill any voids left between the conductive foil and the recesses  64 ,  76 . 
         [0046]    In the embodiment of  FIG. 6 , solder balls  80  are deposited on the contact members  70  and/or the circuit geometry  78  to create packaged semiconductors  82 A,  82 B,  82 C (collectively “ 82 ”). The packaged semiconductor devices  82  can be tested while still part of the wafer  50 . As illustrated in  FIG. 7 , the packaged semiconductor devices  82  are then singulated or cut from the wafer  50  at locations  84  using traditional methods and removed from the substrate  52 . 
         [0047]      FIG. 8  illustrates an alternate embodiment in which metalized terminals  90  are printed on the circuit geometry  78  to create posts or pillars as an alternative to the solder balls  80  or bumps. The shape of the metalized terminals  90  can be altered to promote electrical coupling to another circuit member. 
         [0048]      FIG. 9  illustrates an alternate packaged semiconductor device  100  with modified terminals  102 ,  104  in accordance with an embodiment of the present disclosure. Resilient material  106  is preferably printed during the creation of layers  108  and the circuit geometry  109 . In the preferred embodiment, dielectric material is printed to leave a recess into which the resilient material  106  is deposited. The resilient material  106  permit the terminals  102 ,  104  to move in all six degrees of freedom (X-Y-Z-Pitch-Roll-Yaw) to facilitate electrical coupling with another circuit member  116  (see  FIG. 10 ). In one embodiment, solder ball  110  is located on terminal  102 . In another embodiment, conductive material  112  is printed on the terminal so it extends above surface  114  of the packaged semiconductor device  100 . 
         [0049]    The circuit geometry  109  re-routes the terminal  102 ,  104  relative to the terminals  122  on the IC device  118 . The size and pitch of exposed terminals  102 ,  104  are printed to electrically couple the IC device  118  to another circuit member  116 , such as a printed circuit board or a socket. The packaged semiconductor device  100  permits fine contact-to-contact spacing (pitch) on the order of less than 1.0 mm pitch, and more preferably a pitch of less than about 0.7 millimeter, and most preferably a pitch of less than about 0.4 millimeter. 
         [0050]    The resilient material  106  increases the compliance of the terminals  102 ,  104  to permit electrical coupling by compression, without the need to solder the packaged semiconductor device  100 . As illustrated in  FIG. 10 , the packaged semiconductor device  100  permits IC device  118  to be tested prior to final packaging by pressing against pads  120  on a circuit member  116  and powered without the need for a socket, such as printed circuit board (PCB), or by insertion into a LGA or BGA socket. The present packaged semiconductor device  100  also permits the performance of the IC device  118  to be evaluated before being incorporated into a multi-chip module, permitting an individual die to be replaced if necessary. Alternatively, the packaged semiconductor device  100  can be soldered to a circuit member, such as a PCB, to provide a more reliable stress-decoupled solder joint. As used herein, the term “circuit members” refers to, for example, a packaged integrated circuit device, an unpackaged integrated circuit device, a printed circuit board, a flexible circuit, a bare-die device, an organic or inorganic substrate, a rigid circuit, or any other device capable of carrying electrical current. 
         [0051]      FIG. 11  illustrates an alternate packaged semiconductor device  140  formed on wafer  142 , with printed electrical devices  144  in accordance with an embodiment of the present disclosure. The electrical devices  144  can include passive or active functional elements. Passive structure refers to a structure having a desired electrical, magnetic, or other property, including but not limited to a conductor, resistor, capacitor, inductor, insulator, dielectric, suppressor, filter, varistor, ferromagnet, and the like. 
         [0052]      FIG. 12  illustrates the packaged semiconductor device  140  after the wafer  142  is singulated. The circuit geometry  148  includes external contact pads  152  that can electrically couple with contact pads  154  on circuit member  156 . 
         [0053]    The electrical devices  144  are preferably printed during construction of the dielectric layers  146  and the circuit geometry  148 . The electrical devices  144  can be ground planes, power planes, electrical connections to other circuit members, dielectric layers, conductive traces, transistors, capacitors, resistors, RF antennae, shielding, filters, signal or power altering and enhancing devices, memory devices, embedded IC, and the like. For example, the electrical devices  144  can be formed using printing technology, adding intelligence to the packaged semiconductor device  140 . Features that are typically located on the IC device  150  can be incorporated into the packaged semiconductor device  140  in accordance with an embodiment of the present disclosure. 
         [0054]    The availability of printable silicon inks provides the ability to print electrical devices  144 , such as disclosed in U.S. Pat. Nos. 7,485,345 (Renn et al.); 7,382,363 (Albert et al.); 7,148,128 (Jacobson); 6,967,640 (Albert et al.); 6,825,829 (Albert et al.); 6,750,473 (Amundson et al.); 6,652,075 (Jacobson); 6,639,578 (Comiskey et al.); 6,545,291 (Amundson et al.); 6,521,489 (Duthaler et al.); 6,459,418 (Comiskey et al.); 6,422,687 (Jacobson); 6,413,790 (Duthaler et al.); 6,312,971 (Amundson et al.); 6,252,564 (Albert et al.); 6,177,921 (Comiskey et al.); 6,120,588 (Jacobson); 6,118,426 (Albert et al.); and U.S. Pat. Publication No. 2008/0008822 (Kowalski et al.), which are hereby incorporated by reference. In particular, U.S. Pat. Nos. 6,506,438 (Duthaler et al.) and 6,750,473 (Amundson et al.), which are incorporated by reference, teach using ink-jet printing to make various electrical devices, such as, resistors, capacitors, diodes, inductors (or elements which may be used in radio applications or magnetic or electric field transmission of power or data), semiconductor logic elements, electro-optical elements, transistor (including, light emitting, light sensing or solar cell elements, field effect transistor, top gate structures), and the like. 
         [0055]    The electrical devices  202  can also be created by aerosol printing, such as disclosed in U.S. Pat. Nos. 7,674,671 (Renn et al.); 7,658,163 (Renn et al.); 7,485,345 (Renn et al.); 7,045,015 (Renn et al.); and 6,823,124 (Renn et al.), which are hereby incorporated by reference. 
         [0056]    Printing processes are preferably used to fabricate various functional structures, such as conductive paths and electrical devices, without the use of masks or resists. Features down to about 10 microns can be directly written in a wide variety of functional inks, including metals, ceramics, polymers and adhesives, on virtually any substrate—silicon, glass, polymers, metals and ceramics. The substrates can be planar and non-planar surfaces. The printing process is typically followed by a thermal treatment, such as in a furnace or with a laser, to achieve dense functionalized structures. 
         [0057]    Ink jet printing of electronically active inks can be done on a large class of substrates, without the requirements of standard vacuum processing or etching. The inks may incorporate mechanical, electrical or other properties, such as, conducting, insulating, resistive, magnetic, semi conductive, light modulating, piezoelectric, spin, optoelectronic, thermoelectric or radio frequency. 
         [0058]    In one embodiment, a plurality of ink drops are dispensed from the print head directly to a substrate or on an intermediate transfer member. The transfer member can be a planar or non-planar structure, such as a drum. The surface of the transfer member can be coated with a non-sticking layer, such as silicone, silicone rubber, or Teflon. 
         [0059]    The ink (also referred to as function inks) can include conductive materials, semi-conductive materials (e.g., p-type and n-type semiconducting materials), metallic material, insulating materials, and/or release materials. The ink pattern can be deposited in precise locations on a substrate to create fine lines having a width smaller than 10 microns, with precisely controlled spaces between the lines. For example, the ink drops form an ink pattern corresponding to portions of a transistor, such as a source electrode, a drain electrode, a dielectric layer, a semiconductor layer, or a gate electrode. 
         [0060]    The substrate can be an insulating polymer, such as polyethylene terephthalate (PET), polyester, polyethersulphone (PES), polyimide film (e.g. Kapton, available from DuPont located in Wilmington, Del.; Upilex available from Ube Corporation located in Japan), or polycarbonate. Alternatively, the substrate can be made of an insulator such as undoped silicon, glass, or a plastic material. The substrate can also be patterned to serve as an electrode. The substrate can further be a metal foil insulated from the gate electrode by a non-conducting material. The substrate can also be a woven material or paper, planarized or otherwise modified on at least one surface by a polymeric or other coating to accept the other structures. 
         [0061]    Electrodes can be printed with metals, such as aluminum or gold, or conductive polymers, such as polythiophene or polyaniline. The electrodes may also include a printed conductor, such as a polymer film comprising metal particles, such as silver or nickel, a printed conductor comprising a polymer film containing graphite or some other conductive carbon material, or a conductive oxide such as tin oxide or indium tin oxide. 
         [0062]    Dielectric layers can be printed with a silicon dioxide layer, an insulating polymer, such as polyimide and its derivatives, poly-vinyl phenol, polymethylmethacrylate, polyvinyldenedifluoride, an inorganic oxide, such as metal oxide, an inorganic nitride such as silicon nitride, or an inorganic/organic composite material such as an organic-substituted silicon oxide, or a sol-gel organosilicon glass. Dielectric layers can also include a bicylcobutene derivative (BCB) available from Dow Chemical (Midland, Mich.), spin-on glass, or dispersions of dielectric colloid materials in a binder or solvent. 
         [0063]    Semiconductor layers can be printed with polymeric semiconductors, such as, polythiophene, poly(3-alkyl)thiophenes, alkyl-substituted oligothiophene, polythienylenevinylene, poly(para-phenylenevinylene) and doped versions of these polymers. An example of suitable oligomeric semiconductor is alpha-hexathienylene. Horowitz, Organic Field-Effect Transistors, Adv. Mater., 10, No. 5, p. 365 (1998) describes the use of unsubstituted and alkyl-substituted oligothiophenes in transistors. A field effect transistor made with regioregular poly(3-hexylthiophene) as the semiconductor layer is described in Bao et al., Soluble and Processable Regioregular Poly(3-hexylthiophene) for Thin Film Field-Effect Transistor Applications with High Mobility, Appl. Phys. Lett. 69 (26), p. 4108 (December 1996). A field effect transistor made with a-hexathienylene is described in U.S. Pat. No. 5,659,181, which is incorporated herein by reference. 
         [0064]    A protective layer can optionally be printed onto the electrical devices. The protective layer can be an aluminum film, a metal oxide coating, a substrate, or a combination thereof. 
         [0065]    Organic semiconductors can be printed using suitable carbon-based compounds, such as, pentacene, phthalocyanine, benzodithiophene, buckminsterfullerene or other fullerene derivatives, tetracyanonaphthoquinone, and tetrakisimethylanimoethylene. The materials provided above for forming the substrate, the dielectric layer, the electrodes, or the semiconductor layer are exemplary only. Other suitable materials known to those skilled in the art having properties similar to those described above can be used in accordance with the present disclosure. 
         [0066]    The ink-jet print head preferably includes a plurality of orifices for dispensing one or more fluids onto a desired media, such as for example, a conducting fluid solution, a semiconducting fluid solution, an insulating fluid solution, and a precursor material to facilitate subsequent deposition. The precursor material can be surface active agents, such as octadecyltrichlorosilane (OTS). 
         [0067]    Alternatively, a separate print head is used for each fluid solution. The print head nozzles can be held at different potentials to aid in atomization and imparting a charge to the droplets, such as disclosed in U.S. Pat. No. 7,148,128 (Jacobson), which is hereby incorporated by reference. Alternate print heads are disclosed in U.S. Pat. No. 6,626,526 (Ueki et al.), and U.S. Pat. Publication Nos. 2006/0044357 (Andersen et al.) and 2009/0061089 (King et al.), which are hereby incorporated by reference. 
         [0068]    The print head preferably uses a pulse-on-demand method, and can employ one of the following methods to dispense the ink drops: piezoelectric, magnetostrictive, electromechanical, electro pneumatic, electrostatic, rapid ink heating, magneto hydrodynamic, or any other technique well known to those skilled in the art. The deposited ink patterns typically undergo a curing step or another processing step before subsequent layers are applied. 
         [0069]    While ink jet printing is preferred, the term “printing” is intended to include all forms of printing and coating, including: pre-metered coating such as patch die coating, slot or extrusion coating, slide or cascade coating, and curtain coating; roll coating such as knife over roll coating, forward and reverse roll coating; gravure coating; dip coating; spray coating; meniscus coating; spin coating; brush coating; air knife coating; screen printing processes; electrostatic printing processes; thermal printing processes; and other similar techniques. 
         [0070]      FIG. 13  illustrates a packaged semiconductor  170  with stacked IC devices  172 ,  174  in accordance with an embodiment of the present disclosure. Through silicon vias  176  permit contact pads  178  on IC device  172  to electrically couple with circuit geometry  180  and/or IC device  174 . The circuit geometry  180  permits the IC devices  172 , 174  to be routed discretely to circuit member  182 , inter-die or die-to-die. The through silicon vias  176  eliminate edge wiring and permit a shorter vertical stack. The through silicon vias  176  can be formed using the printing processes discussed herein or other methods. In the illustrated embodiment, the packaged semiconductor  170  is located on base wafer  184 . 
         [0071]      FIG. 14  illustrates an alternate packaged semiconductor  200  in accordance with an embodiment of the present disclosure. RF shielding  202  is optionally printed in recess  204  of substrate  206 . In one embodiment, substrate  206  is optimized for thermal management. In another embodiment, IC device  208  is retained to substrate  206  by overmolding or encapsulation  210 . 
         [0072]    Dielectric layers  212  and circuit geometry  214  are preferably printed as discussed above. In the embodiment of  FIG. 14 , the circuit geometry  214  is configured to add additional IC device  216  in a double sided configuration. Alternatively, the packaged semiconductor  200  can be mated with another circuit member  218  to create a complex system in package or multichip module. 
         [0073]    Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that stated range is encompassed within the embodiments of the disclosure. The upper and lower limits of these smaller ranges which may independently be included in the smaller ranges is also encompassed within the embodiments of the disclosure, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either both of those included limits are also included in the embodiments of the present disclosure. 
         [0074]    Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the embodiments of the present disclosure belong. Although any methods and materials similar or equivalent to those described herein can also be used in the practice or testing of the embodiments of the present disclosure, the preferred methods and materials are now described. All patents and publications mentioned herein, including those cited in the Background of the application, are hereby incorporated by reference to disclose and described the methods and/or materials in connection with which the publications are cited. 
         [0075]    The publications discussed herein are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the present disclosure is not entitled to antedate such publication by virtue of prior invention. Further, the dates of publication provided may be different from the actual publication dates which may need to be independently confirmed. 
         [0076]    Other embodiments of the disclosure are possible. Although the description above contains much specificity, these should not be construed as limiting the scope of the disclosure, but as merely providing illustrations of some of the presently preferred embodiments of this disclosure. It is also contemplated that various combinations or sub-combinations of the specific features and aspects of the embodiments may be made and still fall within the scope of the present disclosure. It should be understood that various features and aspects of the disclosed embodiments can be combined with or substituted for one another in order to form varying modes of the disclosed embodiments of the disclosure. Thus, it is intended that the scope of the present disclosure herein disclosed should not be limited by the particular disclosed embodiments described above. 
         [0077]    Thus the scope of this disclosure should be determined by the appended claims and their legal equivalents. Therefore, it will be appreciated that the scope of the present disclosure fully encompasses other embodiments which may become obvious to those skilled in the art, and that the scope of the present disclosure is accordingly to be limited by nothing other than the appended claims, in which reference to an element in the singular is not intended to mean “one and only one” unless explicitly so stated, but rather “one or more.” All structural, chemical, and functional equivalents to the elements of the above-described preferred embodiment(s) that are known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the present claims. Moreover, it is not necessary for a device or method to address each and every problem sought to be solved by the present disclosure, for it to be encompassed by the present claims. Furthermore, no element, component, or method step in the present disclosure is intended to be dedicated to the public regardless of whether the element, component, or method step is explicitly recited in the claims.