Abstract:
A method of reducing contamination caused by high intensity heating of metals is taught. Splatter, vapor droplets and particulate matter is collected to avoid return to the melt. An electric field is established in the heating zone to attract the vapor droplets and particles to charged plates.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     The present invention relates generally to the subject matter of Ser. No. 390052, filed 8-7-89, and to Ser. No. 376094, filed 7-6-89. The texts of these cross referenced applications are included herein by reference. 
     BACKGROUND OF THE INVENTION 
     The present invention relates generally to the melt processing of high temperature metals. More specifically, it relates to methods by which the contamination of high temperature melts can be reduced and/or avoided. 
     It is known that in the processing of lower temperature melts of metals contamination from atmospheric oxidation or from impurities introduced into the melt from the melt crucible, or from dust particles is at an exemplary low level. Ordinary procedures and practices permit melting and casting to be accomplished without exceeding the acceptable levels of impurities in such metals. Metals, such as lead, zinc, tin, bismuth, as well as alloys such as brasses, bronzes, and the like, have been usefully and successfully processed through a melt phase without impairment of the solid product metal through the introduction of an excessive level of impurities or contaminants due to the processing. Such metals are melted at lower melting temperatures of the order of a hundred to a few hundred degrees. Heat can be delivered to such melts through their containing crucible and such heating generates very little optically obscuring vaporous or particulate matter. 
     For metals which melt at higher temperatures, and particularly above about 1000° C., the techniques employed in the melting and the techniques for keeping the melt free from contamination, either from the atmosphere or from impurities, is of a different character. 
     In the first place, the means used for melting the metals which melt at much higher temperatures are different and, in the case of highly reactive metals such as titanium, may involve the use of a plasma flame or an electron beam or similar melting technique. The application of heat from such sources to the metal of the melt is directly onto the melt surface rather than through a crucible wall. In addition, because of the high reactivity of metals such as titanium, the metal must be protected from ordinary oxygen and nitrogen containing atmosphere. Further, because metal such as titanium is highly reactive with any crucible material, the metal is melted in a cold skull type of crucible in which a layer of solid titanium serves as the crucible for the liquid or molten titanium. Because of these unique circumstances, and because of the nature of the vaporous droplet and particulate material which is generated from the furnacing and melting of the high melting metal materials, special problems arise. 
     One such problem involves the deposit of vaporous and particulate material on the inside surfaces of enclosures provided to protect the molten metal from contact with ordinary atmospheres. The degree of vaporization and formation of particulate material is quite high for the high melting materials, at least partly because of the nature of heat delivery in the melting process itself. Heat is delivered from high temperature sources and is delivered at high intensity to a metal or melt surface. Plasma torch heat is delivered at temperatures in excess of 10000° C., for example. Thus, it has been found that there is a substantial amount of vaporous and particulate material generated from the use of plasma flames directed downward onto the top of a melt in a cold hearth crucible. Also, where electron beam heating is employed, a substantial amount of sputtering, spattering, and dissipation of the solid and liquid material occurs to the degree that there is a formation on the internal surfaces of the enclosing vessel of a deposit of the vaporized, and/or particulate material. 
     As the use of the vessel continues, there is a tendency for the surface deposited material to flake and to drop off in a manner which permits contamination of the melt. Where a tank or vessel is employed in the melting or melt processing of a number of different alloys, the danger is that the deposit formed during processing of one alloy will flake off and fall into the melt of a different alloy thereby contaminating the later processed alloy. 
     Efforts are made to avoid such contamination and may involve cleaning of the furnace interior between runs. However, another problem occurs during a single run and cannot be cured by cleaning between runs. This problem is that the condensate on a vessel interior has a much higher concentration of the more volatile elements, such as aluminium, than the melt from which the vapor is generated. The aluminum content of a titanium alloy containing 6% aluminum originally may be as high as 50%. When this condensate forms during a single run and drops into the melt just prior to casting, substantial property disparities can result in the casting. 
     Another type of processing of metals having high melting temperatures is the rapid solidification plasma deposition. In this process particles of the metal to be melted are entrained in a carrier gas and are passed through a plasma flame. The production of fine particulate solids and of metal vapors during plasma spray processing of a powder through a melt phase is similar to that which occurs during the high temperature melting processes described above. 
     BRIEF STATEMENT OF THE INVENTION 
     It is, accordingly, one object of the present invention to provide a method which limits the contamination of melts processed in high temperature melting apparatus. 
     Another object is to provide an apparatus which permits the level of contaminants to be limited or reduced. 
     Another object is to provide a method for melt and/or plasma processing of high temperature melts, such as nickel based superalloys with reduced contamination. 
     Another object is to provide a method for melt processing of highly reactive metals such as titanium alloys with lowered contamination resulting from the processing. 
     Other objects will be in part apparent and in part pointed out in the description which follows. 
     In one of its broader aspects, objects of the present invention can be achieved by providing a furnace enclosure in which the heating of a metal at a very high rate and to a very high temperature is accomplished. The application of heat to the metal is preferably done at the upper surface of the melt by a high intensity heat source such as a plasma torch or an electron beam or similar high intensity source. A melt may be contained within a skull of the same metal to avoid its contamination by reaction with a containing vessel. Also the highly intense application of heat occurs at a particle surface during plasma heating of a stream of particles such as occurs during melt processing of the particles in forming a plasma spray deposit of metals onto a receiving surface. The high intensity heating causes a cloud-like fog of vaporous and/or particulate matter to form within the furnace chamber. Such matter is formed by the application of high intensity heating in a heating zone at the surface of the metal. To reduce the particulate cloud and the surface deposit on the walls of the enclosure, at least one metal surface is provided within the chamber adjacent to the heating zone. At least one electric charge is applied to the metal surfaces to cause an electric field to be established within the zone. This electric field causes deposition of vaporous and/or particulate matter from the heating zone onto the changed surface and reduces deposit of such material on portions of the enclosure. This reduction in de posit occurs on surfaces from which they the deposits might fall into the melt to contaminate the melt or to contaminate a plasma deposited molten metal layer. 
     By vaporous, as used herein, is meant material which leaves the heated metal surface as a vapor. It is realized, however, that such material quickly forms droplets as it leaves the high intensity heat zone where it is formed. Also, it is realized that such droplets quickly freeze to particles if they enter a zone where the ambient temperature is below their freezing point. 
     Alternatively, material which remains a vapor may condense on the walls of the enclosing vessel. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The description of the invention which follows will be understood with greater clarity if reference is made to the accompanying drawings in which: 
     FIG. 1 is a schematic view of a enclosure as of a furnace in which high intensity surface heating of a metal may be carried out. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     We have found that when a furnace is operated continuously by Plasma Arc Melting (PAM) or by Electron Beam Melting (EBM) processes, or when Rapid Solidification Plasma Deposition (RSPD) is carried out, particulate matter which is generated from these processes deposits on interior surfaces of the enclosure. These deposits occur on essentially all internal surfaces of the enclosure including on internal surfaces located over RSPD deposited surface layers as well as over molten metal pools. In time the deposits become thick enough to break loose and flake off and to drop into the metal pool. Some of these deposits are rich in oxygen. Others have disproportionate concentrations of ingredients as explained above. The finely divided material formed by the plasma arc melting or electron beam melting processes absorbs or reacts with oxygen readily and the oxide bearing deposit is rarely, if ever, identical in composition to the composition of the final alloy or deposit to be produced by the processing and in this sense represent an unwanted and potentially harmful addition to the alloy pool or to an RSPD receiving surface. Efforts have been made heretofore to reduce or eliminate such &#34;fall back&#34; contamination. 
     In a number of PAM furnaces, constant flowthrough of gas removes a portion of the particulate matter formed but such gas throughput would have to be increased many times in order to eliminate such deposits. In the EBM processing, a grate has been positioned over the melt in order to capture particulate matter and to provide a more reliable bond of the deposited particulate to the surfaces over the melt pool. The idea is that if the particulate matter adheres more strongly to the grate surface as it has a larger collection surface and, there is therefore a reduced chance that it will break loose and fall into the melt pool. These passive techniques such as grate over the melt pool or large volume gas purging has met with limited success and improvements in the processing and in the apparatus used for these techniques are needed. 
     In the RSPD processing, the danger is that surface deposits will flake off the enclosure interior and will fall onto the receiving surface and be embedded in the RSPD surface deposit thus creating an inclusion or defect in the surface structure or alloy composition. 
     Based on the experimental work we have done we deem it possible to considerably reduce or potentially to substantially avoid the formation of particulate deposits on the walls of a furnace which employs RSPD, PAM and/or EBM in the melt processing of high temperature metals. This reduction in the deposit of vaporous and particulate material on surfaces of a processing enclosure from which such deposit may fall onto and/or into and contaminate the melt or plasma deposit may be accomplished by placing at least one electrode in the enclosure at a position which is effective in attracting a large fraction of the particulate matter in the processing cavity. 
     We found the particulate in the furnace chamber to be charged. We inferred the existence of the charge from the fact that the particulate matter is attracted to an oppositely charged plate. Accordingly, we concluded that we would be able to influence the disposition of the particulate matter by inducing an electric field within the chamber to apply attractive and/or repulsive force to the particulate matter. 
     Based on our experiments, we have found that the particulate matter in the processing furnaces is very fine and that, to a large degree, the fine particles carry a charge. Our experiments have demonstrated that in certain processing apparatus the particulate material is almost exclusively negatively charged and the application is described in terms of a negatively changed particulate material. However, the principal experimental finding is that the particles are predominantly of a single charge, and the particulate matter may be dealt with effectively because it bears a single charge. The particle size of the particulate matter is to a large degree smaller than one micron. Based on the combination of particle size and charges which are carried by the particles, we have succeeded in attracting a significant fraction of the particles to a charge plate. To our knowledge, no effort has been made heretofore to clean particulate matter from the processing atmosphere of the RSPD, EBM or PAM process equipment through use of active precipitation, although such PAM melting, RSPD melt processing and EBM melting have been used for many years. 
     In order to accomplish or to influence the particle deposition and removal, at least one conductive surface must be located within the furnace enclosure proximate heating zone where the heat is applied to the specimen to be melted. At least one such conductive surface is so positioned although more than one may be used. The conductive surface is charged with relatively high voltage, of the range of 1030 kilovolts, in an experimental apparatus, and a power supply is provided capable of delivering relatively small currents of the order of milliamps to the conductive surface. The charge on the conductive surface is opposite to that on the particles. The higher the voltage employed the higher the rate of particle collection but the voltage should not be so high as to cause undesirable side effects such as arcing or the like. Such arcing or breakdown is a function of the type of atmosphere, the pressure, the temperature and other factors as well as the particle density, particle tape and other like factors. Care must also be exercised in the use of magnetic or electric fields in connection with electron beam heating to avoid redirecting the beam from the intended target. 
     We have found that the negatively charged conductive surface, such as the surface of a plate in our experiments, remained very clean. However, a substantial fraction of the particles in the enclosure appeared to be deposited on a positively charged plate. Although this deposit could not be observed directly to result in a decrease of the fog or cloud of particles in the chamber, in an overall such a decrease is believed to be at least partially the result that can be achieved. 
     Further, we were not able to observe directly, but were able to conclude based on the observations made, that through the use of at least one of these charged surfaces or charged plates we are able to limit and reduce the deposit of the particulate matter on the interior surfaces. Based on the deposit of negatively charged particles on the positively charged plate, we have concluded that with a collar of such plates extending around the exposed melt surface, the incidence of such deposits flaking off chamber surfaces and dropping into the melt to contaminate the melt or RSPD deposit can be effectively reduced. 
     For convenience of reference as used herein the term furnace enclosure designates an enclosure in which high intensity heating of metal specimens takes place. The high intensity heating can be by PAM, by EBM, by RSPD or by any other method which delivers high temperature heat rapidly to a metal surface, whether liquid, solid or solid particulate. 
     High intensity heating by a plasma flame occurs because the plasma flame involves high temperature ionization of gas and the operating temperature of a plasma is usually over 10,000° C. and contact of such a flame with a metal specimen delivers heat to the metal specimen at high temperature and accordingly at a high rate. The same high rate of heating occurs when the heating is done by transferred arc. 
     The method by which the invention is carried out may be described by referring to the accompanying FIG. 1. The Figure is schematic in that the relation of various parts of an apparatus are depicted but the details of mechanical support of the various mechanical parts are not included as they are readily apparent to those skilled in the art and are not essential to practice of the invention. 
     Referring now to the Figure an enclosure 10 houses an apparatus for the high intensity heating of a metal specimen. The metal 12 to be heated is contained within a hearth 14. The hearth is made up of a copper crucible 16 having cooling tubes 18 embedded in the base 20 and positioned about the sides 16 to cool the copper body of the hearth 14. The cooling results in the formation of a skull 22 surrounding the melt 12 and thereby avoiding contamination of the melt by material of the hearth. The hearth 14 is supported on a frame 24, the frame 24 is grounded by ground wire 26, and also the hearth 14 is grounded by ground wire 28. 
     Heat is supplied by a plasma torch 30 positioned above the melt so as to direct the heat of the torch onto the upper surface of melt 12. The current supply and gas supplied to torch 30 are not illustrated as they are not essential and play no part in the subject invention. 
     When ignited the torch has an arc extending between elements internal to the torch. The torch flame extends from the gun due to the flow of gas through the arc. However, after ignition the arc may extend from the cathode of the gun to the surface of the melt by a transfer arc operation to continue the high intensity heating at the upper surface of the metal. This high intensity heating occurs because the temperature of the plasma from the torch is at 10,000° C. or higher and there is accordingly an application of high intensity heating to the surface of the melt because of the very high temperature at which heat is delivered to the melt surface. What attends the high intensity heating of the melt surface is a generation of vapor and particulate material of very fine particle size. Similar generation of vapors and particulate material accompanies other forms of high intensity heating such as heating with electron beam or other means. In addition, the same type of vapors and particulate matter is generated when a plasma arc is operated to plasma spray deposit particles of a material which are passed through the plasma flame onto a receiving surface. For each of these melt processing operations which involve the application of high intensity heat to a metal surface there is an accompanying production of vapors and particulate material for which the subject invention provides some advantages. 
     In order to reduce the concentration of particulate and vaporous material which emanates from the hearth 14 at least one conductive metal surface such as the surface 32 of electrode 34 may be provided. The electric surface may be charged with a positive voltage from the power supply 36 through the electrical conductor 38 when the charge on the particles is found to be negative. When the particle charge is positive the electrode 34 may be negatively charged to attract particle precipitation on the electrode. The conductor is insulated from the wall of enclosure 10 by insulator 40. By applying a voltage of 5 to 30 kilovolts on the plate 34 it is possible to induce the deposit of particulate matter from hearth 14 onto the surface of the plate. The upper limit of this voltage impressed on an electrode is determined by the capability of the apparatus. Our experimental apparatus could handle 30 kV. An industrial apparatus could beneficially employ higher voltages of 50 or 80 kV or higher. 
     One way in which the deposit of particulate material on the conductive surface can be studied is by placing a foil 42 on the conductive surface of plate 34 to serve as a collecting surface for particulate deposit. After a deposit has been accumulated the foil 42 may be removed from plate 34 and studied for the deposit which is found thereon. In this way we discovered that a substantial deposit of particulate material occurs on the foil 42 when the plate 34 has a positive voltage charge impressed thereon from power source 36. Also by a similar study of the plate 44, and particularly of a foil 46 on plate 44, we discovered that essentially no particulate deposit occurs on plate 44 where the charge on plate 44 is negative with the charge on plate 34 being positive. A charge is impressed on plate 44 from power source 36 through conductor 48. The conductor 48 is insulated from the wall of enclosure 10 by insulator 50. The brick insulating support 52 supports plate 32 in place and the brick insulating support 54 supports the plate 44 in place for these experiments. 
     From the experimental work which was carried out, it was concluded that it is feasible to collect a substantial amount of the particulate matter generated from a high intensity heating of a metal sample by a furnacing operation such as described above by including a conductive surface such as 32 in proximity to the hearth 14 to thereby impress an electric field in the heating zone of the hearth. The formation of vaporous and particulate matter during the high intensity furnacing operation is evidently an inescapable result of the furnacing with high intensity heat itself. However from the experimental observations which were made it is our conclusion that it is possible to collect a very substantial amount of the particulate matter from such a furnacing operation on a positively charged, or otherwise oppositely charged, conductive surface which surface is one element of an electric field impressed on the heating zone of the furnace. 
     Because the furnace and the support of the furnace is grounded, it is possible to have a charged plate or a conductive surface impress an electric field on a heating zone without having a second conductive plate. Such an arrangement is illustrated in the Figure where only a single plate 32 is provided and no second plate such as 44 is present. 
     A preferred form and arrangement of the electric field is one in which the single positively charged plate extends fully around the hearth 14 in the form of a positively charged collar. Such an arrangement would, for example, be present if one considers the plate 34 and the plate 44 to be sectional views of a charged collar extending all the way around the hearth 14.