Abstract:
A metal layer cleaning composition including a first component that is an acid; and a different second component that is a chelating agent, wherein the composition is in a form suitable for use in effectively removing undesirable constituents from a wafer surface following a polishing operation.

Description:
RELATED APPLICATION  
       [0001]     The present application is a divisional application of U.S. patent application Ser. No. 10/429,989, filed May 6, 2003, which is a divisional of U.S. patent application Ser. No. 09/476,977, filed Dec. 31, 1999, issued as U.S. Pat. No. 6,592,433. 
     
    
     BACKGROUND  
       [0002]     1. Field of the Invention  
         [0003]     The invention relates generally to removal of particles from a substrate and more particularly to removal of at least one particle from a metal layer deposited on a substrate using an acid.  
         [0004]     2. Description of Related Art  
         [0005]     Integrated circuits are made up of literally millions of active devices formed in or on a silicon substrate or well. The active devices that are initially isolated from one another are later connected together to form functional circuits and components. The devices are interconnected together through the use of well known multilevel interconnections. A cross-sectional illustration of a typical multilevel interconnection structure  10  is shown in  FIG. 1 . Interconnection structures normally have a first layer of metallization, an interconnection layer  12  (typically aluminum alloys with up to 3% copper), a second level of metallization  14 , and sometimes a third or even fourth level of metallization. Interlevel dielectrics  16  (ILDs), such as doped and undoped silicon dioxide (SiO 2 ), are used to electrically isolate the different levels of metallization in silicon substrate or well  18 . The electrical connections between different interconnection levels are made through the use of metallized vias  11  formed in ILD  16 . In a similar manner, metal contacts  22  are used to form electrical connections between interconnection levels and devices formed in well  18 . The metal vias  11  and contacts  22 , hereinafter being collectively referred to as “vias” or “plugs”, are generally filled with tungsten  14  and generally employ an adhesion layer  16  such as TiN. Adhesion layer  16  acts as an adhesion layer for the tungsten metal layer  14  which is known to adhere poorly to SiO 2 . At the contact level, the adhesion layer acts as a diffusion barrier to prevent W and Si from reacting.  
         [0006]     In one process, metallized vias or contacts are formed by a blanket tungsten deposition and a chemical mechanical polish (CMP) process. In a typical process, via holes  23  are etched through an ILD  24  to interconnection lines or a semiconductor substrate  26  formed below. Next, a thin adhesion layer  28 , such as TiN, is generally formed over ILD  24  and into via hole  23 , as shown in  FIG. 2B . Next, a conformal tungsten film  29  is blanket deposited over the adhesion layer and into the via hole  23 . The deposition is continued until the via hole  23  is completely filled with tungsten. Next, the metal films formed on the top surface of ILD  24  are removed by CMP, thereby forming metal vias or plugs  28 .  
         [0007]     In a typical CMP process as shown in  FIG. 2C , the substrate or wafer  30  is placed face-down on a polishing pad  32  which is fixedly attached to a rotatable platen  34 . In this way, the thin film of a metal layer to be polished (i.e., tungsten film  29 ) is placed in direct contact with pad  32 . A carrier  36  is used to apply a downward pressure F 1  against the backside of substrate  30 . During the polishing process, pad  32  and platen  34  are rotated while a downward force is placed on substrate  30  by carrier  36 . An abrasive and chemically reactive solution, commonly referred to as “slurry”  35  is introduced onto pad  32  during polishing. Slurries generally include an abrasive material such as alumina or silica. The slurry initiates the polishing process by chemically reacting with the film being polished. The polishing process is facilitated by the rotational movement of pad  32  relative to wafer  30  as slurry is provided to the wafer/pad interface. Polishing is continued in this manner until all of the film on the insulator is removed.  
         [0008]     After the polishing process, the substrate is then rinsed with a solution such as deionized water. By rinsing the substrate, particles from the slurry are removed from the metallized layer.  
         [0009]     Conventional rinsing methods include using a double sided scrubber using deionized water for removing particles present from the CMP from a metallized layer. However, using deionized water generally does not remove all of the particles. Another conventional method is a “magasonic” bath which involves high frequency vibration in which particles are shaken off the substrate. This method also leaves particles on the metal layer.  
         [0010]     Removing foreign particles from a substrate that is used in integrated circuits is known in the art. One known method involves introducing a slurry over a substrate and polishing the substrate. The substrate is then rinsed with deionized water. A scrubber then cleans the substrate. However, this method is problematic because it is unable to remove the particles to a nondetectable level.  FIG. 8  shows that a substrate using a conventional method such as that which is described above leaves a large quantity of defects on the substrate. Particles on a substrate may affect the electrical conductivity between the various layers of the interconnect within an integrated circuit and cause catastrophic failures upon further processing. Accordingly, it is desirable to have a method and an apparatus wherein particles are removed from a substrate to a nondetectable level of particles without affecting adhesion or the integrity of the post-polish metal layer surface. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0011]      FIG. 1  is a cross-sectional illustration showing a portion of a standard multilevel integrated circuit.  
         [0012]      FIG. 2A  is a cross-sectional illustration showing the formation of a via hole through an insulating layer formed on a conductive layer of a semiconductor substrate.  
         [0013]      FIG. 2B  is a cross-sectional illustration showing the formation of an adhesion layer and a tungsten layer on the substrate of  FIG. 2A .  
         [0014]      FIG. 2C  is a cross-sectional illustration of a chemical mechanical polishing apparatus used to polish the films formed on the substrate of  FIG. 2B .  
         [0015]      FIG. 3  illustrates an assembly wherein a barrier layer is formed over an oxide layer of a substrate.  
         [0016]      FIG. 4  illustrates the assembly of  FIG. 3  after the assembly has undergone a first polishing operation.  
         [0017]      FIG. 5  illustrates the assembly of  FIG. 4  after the assembly has undergone a second polishing operation.  
         [0018]      FIG. 6  illustrates the assembly of  FIG. 5  after it has been rinsed.  
         [0019]      FIG. 7  provides a graphic comparison of defect density on a wafer using a conventional method compared to one embodiment of the invention.  
         [0020]      FIG. 8  provides a graphic comparison of defect events on a wafer using a conventional method compared to one embodiment of the invention.  
         [0021]      FIG. 9  illustrates a schematic view of the process that may be used in accordance with an embodiment of the invention.  
         [0022]      FIG. 10  illustrates a polisher that may be used in one embodiment of the invention.  
         [0023]      FIG. 11  illustrates a scrubber that may be used in one embodiment of the invention.  
         [0024]      FIGS. 12A and 12B  illustrate a flow diagram in accordance with an embodiment of the invention. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0025]     A method and a composition is disclosed for reducing defects in an electronic device such as in an integrated circuit by using a buffered solution comprising an acid. The following detailed description and the accompanying drawings are provided for the purpose of describing and illustrating presently preferred embodiments of the invention only, and are not intended to limit the scope of the invention.  
         [0026]     One embodiment of the invention relates to a method of removing at least one particle by polishing a metal layer over a substrate using a slurry and introducing a solution that includes an acid. Another embodiment of the invention relates to the same process described above except the solution comprises an acid and a chelating agent. The solution may also be buffered.  
         [0027]     Another embodiment of the invention relates to a method of using a first solution that is deposited onto the substrate and a polisher that has an abrasive material at the surface of a polishing pad of the polisher that contacts the substrate and removing the particle from the substrate using a second solution containing an acid.  
         [0028]     In another embodiment of the invention, a chelating agent is used in the solution. In yet another embodiment of the invention, the solution is buffered to allow the pH to remain constant.  
         [0029]      FIGS. 3 through 7  show one embodiment of a fabrication process (e.g., an integrated circuit fabrication process) incorporating the method of the invention wherein a solution containing an acid is used to remove particles from the surface of a substrate.  FIG. 3  shows wafer  38  wherein oxide layer  40  is disposed over a substrate. Adhesion layer  42  comprising of, for example, tantalum is formed over oxide layer  40 . Metal layer  44  comprising an adhesion material such as copper, or any other suitable conductive material is blanket deposited over adhesion layer  42  and has formed a via or contact. Preferably, copper is used.  FIG. 4  shows the substrate of  FIG. 3  after the metal layer has been polished using a conventional polishing technique. One conventional polishing technique for polishing a metal layer of copper involves introducing a slurry (also referred to herein as a first agent) of alumina or silica onto a polishing pad and the polishing pad then contacts the metal layer. As illustrated in  FIG. 4 , fabrication techniques such as chemical mechanical polishing (“CMP”) generate undesired particles on the surface of the substrate. Particles  50  that may have been generated from the first polishing operation or from some other source remain on barrier layer  42  and metal layer  44 . Such particles can disrupt the integrity of electrical signals utilizing the via and metal layer.  
         [0030]      FIG. 5  shows wafer  38  after a second polishing operation is performed in which barrier layer  42  is polished such that barrier layer  42  has been substantially removed from the surface of oxide layer  46 . CMP with an abrasive material such as silica is used to perform the second polishing operation. The rate of removal of barrier layer  42  is approximately in the range of 100 Å/minute to 1000 Å/minute. Even after polishing barrier layer  42 , particles  50  remain on the surface of oxide layer  46  and the metal layer  44 .  
         [0031]     In order to remove undesired particles  50  after both polishing steps discussed above, an aspect of the invention includes introducing a solution (also referred to herein as a second agent) comprising an acid over the substrate.  FIG. 6  shows that particles  50  from the device shown in  FIG. 5  have been removed from oxide layer  46  and metal layer  44  when a solution comprising an acid is used to rinse the device of  FIG. 5 . Preferably organic acids are used such as carboxylic acids including acetic acid, citric acid, gluconic acid, glucoronic acid, oxalic acid, and tartaric acid. It is to be appreciated that the list of suitable organic acids is not exhaustive and that other organic acids may be used particularly those having such as multivalent carboxylic acids similar to those listed. The concentration of acid to be used depends upon the acid selected. Preferably, citric acid is used at a concentration of 50 mM.  
         [0032]     Inorganic acids may also be used such as sulfuric acid, nitric acid, and phosphoric acid. However, these inorganic acids generally must be substantially diluted to reduce their corrosivity to prevent the surface of the metal layer from becoming too rough. A sulfuric acid having a concentration on the order of less than five percent acid is an example of such a dilution. A rougher metal layer surface may affect adhesion of subsequent layers and the electrical conduction of the fabricated device.  
         [0033]     In one embodiment of the invention, the solution comprising the acid is buffered and comprises an organic acid and a chelating agent. Examples of chelating agents include aliphatic amines, hydroxy alkyl amines, aminocarboxylic acids, cyanides, organosulphides, ammonia ethylyenediaminetetraacetic acid (EDTA), ethlyenediamine (EN), nitrilotriacetic acid (NTA), glycin, diethlyene triamine, and triethanol amine. It is generally believed that chelating agents form bonds with metals atoms of the metal layer. It will be appreciated that other chelating agents may be used provided that the chelating agent is capable of forming a bond with a metal that is used in the metal layer. In the case of a copper metal layer, a chelating agent is added to bind free (dissolved) copper ions in solution and to prevent the copper ions from adsorbing on the surface of the substrate. The composition of this solution substantially reduces particles on the surface of a substrate.  
         [0034]     In one embodiment, the solution comprises, for example, 50 mM citric acid and 20 mM potassium citrate (or ammonium citrate as an alternative to potassium citrate), and 100 ppm of EDTA. The solution is diluted with deionized water. Suitable pH ranges are from 3 to 4 but the pH may range from 3 to 5. The pH range from 3 to 4 increases the copper solubility and the copper adsorption of ions on SiO 2  is minimized. This solution provides approximately in the range of two to one hundred times improvement in frontside defects. This solution also reduces backside metal levels such as copper to less than 10 −12  atoms/cm 2  thereby eliminating the need to have a dedicated copper processing equipment. It should be noted that although one embodiment of the invention describes a metallized layer being polished prior to the rinsing solution being introduced onto the metallized layer, the metallized layer may be cleaned by introducing the rinsing solution onto the metallized layer without first polishing the metallized layer.  
         [0035]     Table 1 compares the effectiveness of embodiments of the invention when a chelating agent is used and is not used in the process. As shown in Table 1, total reflection x-ray fluorescence (“TXRF”) is one method used for determining small amounts of copper that are readsorbed onto a substrate. When citric acid scrub is used without a chelating agent, the average TXRF is 4×10 10  to atoms/cm 2 . In comparison, when a chelating agent is combined with citric acid, the TXRF is nondetectable at a detection limit of 10 10  atoms/cm 2 . Conventional methods (i.e., a process using a double sided scrubber and deionized water) and control with no polish provide 9×10 10  atoms/cm 2  and 289×10 10  atoms/cm 2 , respectively.  
                                                   TABLE 1                           Comparison of Copper Levels on the Backside       of a Substrate Having Copper Contamination                    TXRF           Process Used to Clean       x 10 10     Average of       a Substrate   Coordinate   atoms/cm 2     TXRF Data                    Citric Acid Scrub   (0, 0)   nd   4            (0, 40)   nd               (63.6, 63.6)   4.4           (−63.6, −63.6)   nd       Citric Acid Scrub   (0, 0)   nd   nd       Wherein the Citric    (0, 40)   nd       Acid is Combined   (63.6, 63.6)   nd       With EDTA   (−63.6, −63.6)   nd       Conventional Method   (0, 0)   nd   9       Using    (0, 40)   nd       Deionized Water   (63.6, 63.6)   5.6           (−63.6, −63.6)   13       Control Process   (0, 0)   52   289       Wherein    (0, 40)   75       No Polish Is Used   (63.6, 63.6)   313       (Post-electroplate)   (−63.6, −63.6)   716                  
 
         [0036]      FIGS. 7 and 8  compare the amount of defects between the conventional process of using deionized water compared to a buffered citric acid solution. For example,  FIG. 7  shows that POR leaves 0.8 defects/cm 2  compared to approximately 0.06 defects/cm 2  of the buffered organic acid.  FIG. 8  further shows the defects between a POR clean which is generally greater than 140 defects on a wafer compared to the much lower defects of about 40 defects or lower for a buffered citric acid process.  
         [0037]      FIG. 9  shows one embodiment of the invention wherein a substrate is advanced to a polishing operation  70  in which a slurry is put onto the polishing pad and the polishing pad contacts the substrate and is used during the polishing operation. Chemical mechanical polishing (CMP) may be used in this process. However, it will be appreciated that other suitable methods such as orbital polishing may be used to practice the invention. In CMP, a portion of a metal layer comprising a metal such as copper may be removed from the substrate using a slurry that is dispensed or deposited onto the metal layer. The slurry includes an abrasive material such as aluminum, silica, or other suitable material.  
         [0038]     A polisher  100  shown in  FIG. 10  generally comprises a carrier  140  and three platens ( 130 , second and third platens are not shown). Each platen has a polish pad  120 . Two of the three platens may be used to remove a portion of the copper using a slurry. The slurry may contain an abrasive material such as alumina, silica, etc. Each platen further has four polishing heads  170 . The polishing heads rotate on a turret.  
         [0039]     The substrate is polished in series such that platen one  140  removes a portion of a metallized layer such as copper by polishing for a certain amount of time such as less than two minutes and the substrate is then moved to the second platen where another portion of the copper is removed using a slurry. The substrate then moves to a third platen where a portion of the tantalum is removed. At the third platen  130 , the pressure is lowered to approximately 2 psi. The polish time of this operation is approximately 125 seconds or less.  
         [0040]     The substrate is then advanced to scrubber  30  wherein a solution is introduced through the polisher and is deposited over the substrate and the substrate is scrubbed. The solution that is introduced onto the substrate contains an acid and preferably a chelating agent. The solution may also be buffered. Finally, the substrate undergoes a spin/rinse/dry cycle until it reaches a dried state. The substrate is dried for approximately 2 minutes or less at a temperature of approximately 22° C.  
         [0041]     Scrubber  90  shown in  FIG. 11  may be a double-sided scrubber that has four submodules ( 300 ,  310 ,  320 ,  330 ). In the first submodule  300 , deionized water is sprayed onto the substrate. The substrate is then advanced to a second submodule  310  wherein a buffered solution comprising an acid and a chelating agent is applied to the substrate. The solution may be fed to the substrate through a chemical dispense arm  340  onto a brush  350 . The substrate is then advanced to a third submodule  320  wherein the substrate enters a second brush box. In this operation, the chemical solution may be dripped onto the top box or the hardware of the scrubber  30  is used to spray the chemical solution onto the backside of the substrate to reduce the copper contamination on the back side of the substrate. The wet substrate is then advanced to the spin/rinse/dry module  330  where the wafer is wet and is rinsed with deionized water is introduced while it rotates at 2,000 rpm until the wafer is dry.  
         [0042]     The chemical solution is added to the substrate at a rate of approximately 300 milliliters/minute. While in scrubber  90 , the substrate is scrubbed with at least one or more soft poly vinyl alcohol brushes  380 . The brush rotates generally at 100 revolutions per minute (rpm). Waste water exits from the scrubber at a flow rate of approximately 2 gallons per minute.  
         [0043]      FIGS. 12A and 12B  are a flow chart of one embodiment of the invention used to remove at least one or more particles from a substrate. At operation  400 , the substrate is advanced to a position such that the substrate is adjacent to a polisher. The polisher performs a first polishing operation wherein a portion of the metal layer such as copper is removed. At operation  410 , a slurry is introduced over a substrate. The slurry includes an abrasive material such as silica or alumina. At operation  420 , the polisher uses the slurry to perform a first polish of the surface of the substrate in order to remove a portion of a metallized layer comprising a metal such as copper on the substrate. At operation  430 , the surface of the substrate is polished in a second polishing operation using a polisher to remove a portion of the metal layer comprising a metal such as tantalum. At operation  440 , the substrate is rinsed with a solution comprising an acid and preferably a chelating agent. A weak organic acid is preferable such as acetic acid, citric acid, gluconic acid, glucoronic acid, oxalic acid, and tartaric acid. At least one particle is removed from the surface of a substrate using a scrubber and the solution containing an acid such as a weak organic acid at operation  450 . The chelating agent is added to the solution in order to prevent metals such as copper from adsorbing to the surface of the substrate. At operation  460 , the substrate is advanced to a spin/rinse/dry module. At operation  470 , the substrate is dried in less than two minutes at a temperature approximately in the range of 20° C. to 25° C. Other temperatures may be used.  
         [0044]     In the preceding detailed description, the invention is described with reference to specific embodiments thereof. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of the invention as set forth in the claims. The specification and drawings are, accordingly, to be regarded in an illustrative rather than a restrictive sense.