Abstract:
A surface-coated blade member for cutting tools comprises a metal substrate of a super hard alloy and a coating on at least one surface of said substrate, said coating being composed of a layer of vapor deposited titanium on the surface of said metal substrate and at least one layer of vapor deposited titanium compound on said layer of titanium, and said layer of titanium compound being selected from the group consisting of titanium carbide, titanium nitride, titanium carbo-nitride, titanium oxy-carbide and titanium oxy-carbo-nitride, said layer of titanium being no larger than 2 μm thick and said layer of titanium compound being 0.5 to 10 μm thick.

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     This is a continuation of our earlier application Ser. No. 192,628 filed Sept. 30, 1980, now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to a surface-coated blade member or insert adapted to be secured to a body of a cutting tool by brazing or other suitable fastening means. The blade member comprises a metal substrate of a super hard alloy on which a hard coating is formed by vapor deposition. 
     2. Prior Art 
     It is known from Japanese Patent Application No. 52-130488 to provide a surface-coated blade member under consideration which comprises a metal substrate of a super hard alloy, and a hard coating on the surface of the substrate, said coating being composed of at least one layer of vapor deposited titanium compound on the surface of the substrate, and the titanium compound being selected from the group consisting of titanium carbide (TiC), titanium nitride (TiN), titanium carbo-nitride (TiCN), titanium oxy-carbide (TiCO), and titanium oxy-carbo-nitride (TiCNO). The layer of titanium compound is 0.5 to 10 μm thick. 
     This conventional blade member has been found not satisfactory in that the strength of bonding between the coating and the substrate is not so high that this titanium compound coating is susceptible to separation from the substrate surface when the blade member is used to carry out a cutting operation. This difficulty arises from the fact that atoms of the constituents of the substrate fail to positively combine with atoms of titanium contained in the coating since atoms of carbon, nitrogen and oxygen contained in the coating lower activity in the surface of the substrate. 
     If a titanium compound is deposited on the substrate to form a coating of the type described at elevated temperatures, the bonding between the coating and the substrate is enhanced since the diffusion of atoms between the substrate and the coating takes place sufficiently to promote the combination of the atoms. However, this procedure is not practical because the metal substrate becomes deteriorated by the high temperatures used. More specifically, the properties of the substrate becomes changed because the metal atoms of the substrate are diffused into the coating. Further, since the metal substrate is made of a super hard alloy, a brittle layer is formed on the surface of the substrate to lower its toughness. 
     U.S. Pat. No. 3,874,900 discloses a coating method in which a coating is applied to a metal substrate by chemical vapor deposition. The coating comprises a layer of titanium carbide and a layer of titanium nitride. In forming the titanium carbide layer, an interlayer of carbon, titanium, titanium carbide and metal of the substrate is formed between the substrate and the titanium carbide layer. This method has also been found not satisfactory in that the metal substrate is diffused into the coating because the chemical vapor deposition is carried out at high temperatures of 900° C. to 1200° C. As a result, the properties of the substrate become changed. 
     SUMMARY OF THE INVENTION 
     It is therefore an object of this invention to provide a surface-coated blade member for cutting tools in which the bonding of a hard coating to a substrate of a super hard alloy is highly enhanced to provide a high wear resistance. 
     Another object is to provide a process for producing such a blade member. 
     According to a first aspect of the present invention, there is provided a surface-coated blade member for cutting tools which comprises a metal substrate and a coating on at least one surface of said substrate, said coating being composed of a layer of vapor deposited titanium on the surface of said metal substrate and at least one layer of vapor deposited titanium compound on said layer of titanium, and said layer of titanium compound being selected from the group consisting of titanium carbide, titanium nitride, titanium carbo-nitride, titanium oxy-carbide and titanium oxy-carbo-nitride, said layer of titanium being no larger than 2 μm and said layer of titanium compound being 0.5 to 10 μm thick. 
     With this structure, the strength of bonding between the metal substrate and the layer of titanium is high, and also the strength of bonding between the layer of titanium and the layer of titanium compound is high. Thus, the bonding of the hard coating, i.e., the layer of titanium compound to the metal substrate is highly enhanced through the intermediary of the layer of titanium interposed therebetween. The reason why the strength of bonding between the metal substrate and the layer of titanium is high is that titanium atoms are quite active and that the substrate is not subjected at its surface to nonmetal atoms which lower the activity in the substrate surface, such nonmetal atoms being diffused and dissolved in the titanium layer. Therefore, the titanium atoms positively combine with the metal atoms of the substrate. Also, the reason why the strength of bonding between the layer of titanium and the layer of titanium compound is high is that the titanium atoms are quite active and that these two layers have common metal atoms, that is, titanium atoms. 
     The thickness of the layer of titanium is no larger than 2 μm. If the thickness exceeds this value, the overall coating becomes less hard and has a lowered wear resistance. This will shorten a service life of the blade member. Particularly, in the case of the titanium layer having a thickness not exceeding 0.9 μm, the blade member exhibits a marked wear resistance. The layer of titanium compound is 0.5 to 10 μm thick. If the thickness is less than 0.5 μm, the coating fails to have a desired wear resistance. On the other hand, if the thickness exceeds 10 μm, the coating become brittle and less tough. 
     Another advantage of the provision of the layer of titanium is that this layer is capable of absorbing the stresses exerted on the blade member during a cutting operation. During the cutting operation, the blade member is subjected to substantial stresses. In the absence of such titanium layer, the hard coating, i.e., the layer of titanium compound is susceptible to stress cracking and subsequent separation from the metal substrate during the cutting operation because the hard coating does not have deformability and therefore fails to follow the deformation of the substrate. The layer of titanium suitably absorbs such stresses and prevents the overall coating from being separated from the substrate. 
     According to a second aspect of the present invention, there is provided a process for producing a surface-coated blade member for cutting tools, which comprises the steps of: 
     placing a metal substrate in a vacuum chamber; vapor depositing no larger 2 μm thick layer of titanium on at least one surface of said substrate; and subsequently vapor depositing at least one layer of titanium compound on said layer of titanium to form a coating on said substrate, said layer of titanium compound being 0.5 to 10 μm thick, and said titanium compound being selected from the group consisting of titanium carbide, titanium nitride, titanium carbo-nitride, titanium oxy-carbide and titanium oxy-carbo-nitride. 
     With this method, the layer of titanium and the layer of titanium compound are successively formed by vapor deposition in the vacuum chamber. The layer of vapor deposited titanium should not be exposed to the atmosphere since the oxides of titanium are formed on this layer. This would adversely affect the strength of bonding between the layer of titanium and the subsequently vapor deposited layer of titanium compound. 
     During the vapor depositing operation, the metal substrate should preferably be maintained at temperatures of no less than 300° C. If the temperature of the substrate is below 300° C., the atoms of carbon, nitrogen and oxygen fail to be sufficiently diffused into the layer of titanium. As a result, residual such atoms lower the strength of bonding between the two layers. 
     The substrate made of a super hard alloy should preferably be maintained at temperatures below 800° C. Otherwise, a brittle layer would be formed on the surface of the substrate to lower its toughness. 
     Further, since the vapor deposition of the layers are carried out at relatively low temperatures, the metal atoms of the substrate will not be diffused into the coating so that the properties of the substrate are not changed. 
     The layer of titanium and the layer of titanium compound are formed either by a conventional physical vapor deposition process such as an ion plating process and a sputtering process or a chemical vapor deposition process such as one using a low temperature plasma. 
     Further, the super hard alloy constituting the metal substrate should contain 2 to 30% by weight at least one metal selected from the iron family. The titanium atoms of the layer of titanium combine positively with the atoms in the surface of the substrate and particularly with the metal atoms of the metal phase. For this reason, if the metal of the iron family is contained in the super hard alloy in an amount of less than 2% by weight, a sufficiently high bonding strength is not obtained. On the other hand, if the super hard alloy contains no less than 30% by weight of the metal of the iron family, the substrate is subjected to considerable deformation due to stresses during the cutting operation of the blade member so that the coating having a small deformability is susceptible to cracking and subsequent separation from the substrate even though the strength of bonding therebetween is high. 
    
    
     DESCRIPTION OF THE INVENTION 
     The invention will now be illustrated by the following examples. 
     EXAMPLE 1 
     There was prepared, as a substrate, a throw-away blade member made of a super hard alloy or cemented carbide containing WC, 5% by weigh Co and 5% by weight TiC and conforming in shape to a blade member of JIS.SNP432 (ISO.SNGN120408). There was used an ion plating apparatus of the type in which an electron beam was applied to a titanium block supported on a support means mounted within a vacuum chamber so that the vapored titaniumand gases introduced into the vacuum chamber were allowed to pass through the plasma within the vacuum chamber. The above-mentioned blade member or substrate was first placed within the vacuum chamber. Then, 0.5 μm thick layer of titanium was vapor deposited on the surface of the substrate at a heat temperature of 750° C. in an argon atmosphere. Subsequently, 3.5 μm thick layer of titanium compound (TiCN) was vapor deposited on the layer of titanium by replacing the argon gas with a mixture gas of N 2 , C 2  H 2  and Ar to provide a surface coatedblade member of the super hard alloy (hereinafter referred to as &#34;the blademember of this invention&#34;). 
     For comparison purposes, a comparison blade member was prepared according to the above procedure except that the layer of titanium was not provided.Using the Rockwell hardness tester, a coating separation test was carried out in which a dent was applied under a load of 50 kg to the coateted surface of each of the two blade members, and the coating was observed to determine whether any separation of the coating from each substrate took place around the applied dent. The coating of the blade member of this invention was subjected to no separation and exhibited an excellent bonding strength. On the other hand, the coating of the comparison blade member was separated from the substrate around the applied dent. 
     A throw-away blade member of the super hard alloy identical to that of thisinvention but having no coating was also prepared. This blade member is hereinafter referred to as &#34;the non-coating blade member&#34;. 
     The blade member of this invention, the comparison blade member and the non-coating blade member were each attached to a holder of JIS.N11R-44 to provide a cutting tool. These three cutting tools were used to turn a workpiece to determine how long it took for the flank of each blade memberto be worn 0.3 mm. The cutting conditions for this turning test were as follows: 
     
         ______________________________________Workpiece    a circular cross-section bar of alloyed        steel (JIS · SNCM-8; AISI · 4340;        Brinell hardness: 220)Cutting speed        120 m/minuteFeed rate    0.2 mm/revolutionDepth of cut 1 mmCoolant      used______________________________________ 
    
     The results obtained are given in Table 1 below. 
     
                       TABLE 1______________________________________Kind of blade Time of cutting                     Results ofmember        (min.)      separation test______________________________________Blade member of         100         No separationthis invention            developedComparison blade         30          Separationmember                    developedNon-coating blade         10          --member______________________________________ 
    
     As can be seen from Table 1, the blade member of this invention exhibited aquite high bonding strength of the coating by virtue of the provision of the layer of titanium interposed between the substrate and the layer of titanium compound, and was subjected to no separation of the coating. The cutting time of the present blade member was substantially longer than those of the other two blade members, that is to say, more than three times that of the comparison blade member and ten times that of the non-coating blade member. Thus, the present blade member turned out to have an excellent cutting performance. 
     EXAMPLE 2 
     There were prepared as substrates various blade members having different constituents as shown in Table 2 below. A coating was applied by conventional vapor deposition processes to each of these substrates to provide the coated blade members (a) to (l) of this invention and the coated comparison blade members (a) to (h), as shown in Table 4. With a sputtering apparatus used, a target of titanium accommodated within a vacuum chamber was subjected to sputtering in a predetermined atmosphere. For example, TiCNO, a layer of titanium compound, was vapor deposited in an atmosphere of Ar, N 2 , CO 2  and C 2  H 2 , TiC in an atmosphere of Ar and C 2  H 2 , and TiN in an atmosphere of Ar and N 2 . The comparison blade member (a) had no layer of titanium in the coating. The comparison blade member (b) had the layer of titanium the thickness of which was beyond the upper limit of this invention. The comparison blade member (c) had the layer of titanium compound the thickness of which was beyond the upper limit of this invention. The comparison blade member (d) had the substrate containing not less than 30%by weight Co, and the comparison blade member (e) had the substrate containing 1% by weight Co. The comparison blade member (f) had the coating composed of the layer of titanium and the layer of titanium compound which were not successively formed in the same deposition chamber. The comparison blade member (g) had the coating temperature (the temperature of the substrate) of less than 300° C. The comparison blade member (h) had the coating temperature of more than 800° C. 
     The coating separation test and turning test of the above blade members were carried out according to the procedure of Example 1. The results obtained are given in Table 3 below. 
     
                                           TABLE 2__________________________________________________________________________                                  Coating                                        Thick-Kind                                   tempera-                                        ness of                                             Constituents andof coated                              ture (Tem-                                        titanium-                                             thickness of layerblade  Constituents of substrate                        Coating forming                                  perature of                                        layer                                             of titaniummember (% by weight)         process   substrate)                                        (μm)                                             compound__________________________________________________________________________                                             (μm)Bladea WC--10% Tic--10% Tac--5% Co                        Ion plating                                  700° C.                                        0.3  TiCN: 3 μmmembers                      processof thisb &#34;                     Ion plating                                  &#34;     1.0  TiN: 2 μm--TiCNO: 5                                             μminvention                    processc &#34;                     Ion plating                                  &#34;     1.5  TiCO: 1 μm--TiC: 6                                             μm                        processd &#34;                     Plasma chemical                                  &#34;     1.9  TiN: 3 μm--TiC: 3                                             μm                        vapor deposition                        processe TiCN--10% Mo--10% Ni  Sputtering process                                  &#34;     1.0  TiNo 5 μmf WC--10% HfC--10% ZrC--10% Co                        &#34;         &#34;     0.9  TiCN: 5 μmg WC--10% NbC--10% TaC--10% Co                        &#34;         &#34;     0.9  &#34;g&#39;  &#34;                     &#34;         &#34;     0.7  &#34;g&#34;  &#34;                     &#34;         &#34;     0.3  &#34;g&#39;&#34;  &#34;                     &#34;         &#34;     1.0  &#34;h WC--10% TiCN--10% TaN--5% Co--5% Ni                        &#34;         &#34;     0.9  &#34;i WC--10% TiC--10% Tac--30% Co                        Plasma chemical                                  &#34;     0.9  &#34;                        vapor deposition                        processj WC--10% TiC--10% TaC--2% Co                        Plasma chemical                                  &#34;     0.9  &#34;                        vapor deposition                        processk WC--10% TiC--10% TaC--5% Co                        Ion plating process                                  350° C.                                        0.9  &#34;l &#34;                     &#34;         750° C.                                        0.9  &#34;Com- a WC--10% TiC--10% TaC--5% Co                        Ion plating process                                  700° C.                                        --   TiCN: 3 μmparisonb &#34;                     &#34;         &#34;     3.0  &#34;bladec &#34;                     &#34;         &#34;     1.5  TiCN: 12 μmmembersd WC--10% TiC--10% TaC--32% Co                        &#34;         &#34;     0.9  TiCN: 5 μme WC--10% TiC--10% TaC--1% Co                        &#34;         &#34;     0.9  &#34;f WC--10% TiC--10% TaC--5% Co                        Ion plating process*                                  &#34;     0.9  &#34;g &#34;                     &#34;         250° C.                                        0.9  &#34;h &#34;                     &#34;         850° C.                                        0.9  &#34;__________________________________________________________________________*The layer of vapor deposited titanium was exposed to the atmosphere, and then the layer of titanium compound was formed thereon. 
    
     
                       TABLE 3______________________________________                     Results of turningKind of coated        Results of coating                     test (Time of cutting)blade member separation test                     (min.)______________________________________Blade members      a     no separation                         100of this invention            developed      b     no separation                         120            developed      c     no separation                         120            developed      d     no separation                         110            developed      e     no separation                         110            developed      f     no separation                         120            developed      g     no separation                         150            developed      g&#39;    no separation                         170            developed      g&#34;    no separation                         200            developed      g&#39;&#34;   no separation                         100            developed      h     no separation                         110            developed      i     no separation                          90            developed      j     no separation                         120            developed      k     no separation                         100            developed      l     no separation                         100            developedComparison blade      a     substantial   30members          separation            developed      b     no separation                          20            developed      c     no separation                         chipping developed            developed    in ten minutes      d     separation    20            developed      e     separation    35            developed      f     separation    30            developed      g     separation    30            developed      h     separation    30            developed______________________________________ 
    
     As shown in Table 3, the comparison blade member (a) had no layer of titanium in the coating and hence exhibited a poor bonding strength of thecoating. The comparison blade member (b) had the layer of titanium which was too thick, so that the overall coating became soft to exhibit a poor wear resistance. The comparison blade member (c) had the layer of titaniumcompound which was too thick, so that the coating became brittle, thereby giving rise to chipping in the blade member. The compariosn blade member (d) had the substrate which contained too much Co, so that the coating wassubjected to separation from the substrate. The comparison blade member (e)had the substrate which contained an excessively small proportion of Co, sothat the coating was also subjected to separation from the substrate. As described above, the comparison blade member (f) had the coating composed of the titanium layer and the layer of titanium compound which were not successively formed in the same deposition chamber. More specificallly, the layer of vapor deposited titanium was exposed to the atmosphere, and then the layer of titanium compound was formed thereon. This comparison blade member (f) was subjected to separation of the coating from the substrate. The comparison blade members (g) and (h) were also subjected toseparation of the coating. The cutting time of each of these comparison blade members was short while the cutting time of each of the blade members of this invention was substantially longer. Further, the thinner the titanium layer was, the higher wear resistance the blade members of this invention exhibited. This is clearly seen from the data of the blade members (g) to (g&#34;&#39;) in Table 3. Particularly the blade members, having the titanium layer thickness not exceeding 0.9 μm, exhibited a marked wear resistance.