Abstract:
A thermoplastic polymer alloy compositions including a blend of polymers that each contribute beneficial properties to the compositions. The compositions exhibit characteristics desirable for outdoor applications such as weatherability, impact resistance and durability, while offering excellent surface appearance. The compositions are particularly suitable for decking applications and as capstock materials.

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention relates to a thermoplastic polymer alloy compositions including a blend of polymers that each contribute beneficial properties to the compositions. The compositions exhibit characteristics desirable for outdoor applications such as weatherability, impact resistance and durability, while offering excellent surface appearance. The compositions are particularly suitable for decking applications and as capstock materials. 
       BACKGROUND OF THE INVENTION 
       [0002]    Many different materials, for example, polymers such as polyvinyl chloride (PVC), acrylonitrile/butadiene/styrene (ABS) and high impact polystyrene (HIPS) exhibit desirable structural or mechanical properties when formed into an article of manufacture. However, sometimes the surface properties of such materials are lacking in one or more areas, for example scratch resistance, impact resistance and weatherability. As a result, multi-layer compositions have been developed wherein an outer layer or capstock has been bonded to a base material and covers a previously exposed surface in order to provide sought-after performance. Such capstock layers are usually thinner than the base material. 
         [0003]    Various polymers and polymer blends have been used as capstocks, see for example U.S. Pat. Nos. 8,658,716, 8,034,441, 7,651,648, 7,338,706, 6,773,821, 6,696,513, 6,555,245, 6,534,592, 5,318,737; U.S. Publication Nos. 2013/0303644, 2013/0317139, 2012/0128967, 2010/0330272, 2009/0258208, 2008/0293837, 2007/0154689 2007/0092701; and International Application Nos. WO2014/018817. 
         [0004]    Some documents, such as U.S. 2009/0258208, U.S. Pat. No. 6,555,245, and U.S. Pat. No. 6,773,821 describe a problem when using PVC as a capstock layer. As stated in these documents, PVC sometimes cannot withstand demanding environmental and outdoor UV exposure. In view of this, problems of present invention were to provide compositions, especially capstock compositions, that are easily processable, readily bondable to a substrate, weatherable, durable, impact resistant, mar and scratch resistant, and flame retardant. 
       SUMMARY OF THE INVENTION 
       [0005]    The problems noted above and others are solved by the compositions of the present invention which comprise a blend of halogen-containing polymers such as polyvinyl chloride, thermoplastic polyurethane and one or more acrylic polymers. 
         [0006]    One object of the invention is to provide a composition that can be applied as a capstock material over a layer of a substrate material, often as a relatively thin layer, via melt processing, thereby forming a composite. 
         [0007]    Still another object of the present invention is to provide compositions that have excellent weatherability, impact resistance, durability, and/or desirable surface appearance. 
         [0008]    Another object of the present invention is to provide capstock compositions, that are easily processable and readily bondable to a substrate. 
         [0009]    An additional object of the present invention is to provide compositions, especially capstock compositions, that are mar and scratch resistant and/or flame retardant. 
         [0010]    A further object of the present invention is to provide compositions that can be coextruded, crosshead extruded, or otherwise bonded to a substrate with good bond strength. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0011]    The invention will be better understood and other features and advantages will become apparent by reading the detailed description of the invention, taken together with the drawings, wherein: 
           [0012]      FIG. 1  is a cross-sectional view of one embodiment of a composite comprising a capstock material over a layer of a substrate material. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0013]    The compositions of the present invention which are suitable, among other uses as capstock materials, comprise a blend of halogen-containing polymers, a thermoplastic polyurethane, and one or more, and preferably a plurality of different acrylic polymers. The compositions can also include other ingredients or additives, for example as described herein below. As utilized herein the term polymer encompasses both hompolymers and copolymers of two or more different monomers. 
         [0014]    Halogen Containing Polymers 
         [0015]    The polymer compositions of the invention incorporate a halogen-containing polymer therein. Examples of suitable halogen containing polymers include, but are not limited to, polyvinyl chloride, polyvinyl fluoride, polyvinyl bromide, polyvinylidene chloride, chlorinated polyvinyl chloride, polyvinylidene fluoride and polyvinylidene bromide. Chlorine containing vinyl polymers are preferred in one embodiment. Polyvinyl chloride is preferred in various embodiments. 
         [0016]    Halogen-containing polymers, offer the benefit of being inherently flame retardant due to polymer containing relatively high halogen content, such as 57 weight % chlorine in the case of PVC. Various halogen-containing polymers, such as PVC are also polar in nature with the ionic bonds providing good chemical resistance against certain solvents. 
         [0017]    Halogen-containing polymers are available from many commercial sources under various designations including, but not limited to, Oxyvinyl, as OXY 200, OXY 216S, OXY 500F, and as Oxy 225, Shintech as SE 800A, SE 950A, SE 1100A, Formosa, Formolon 616K, Formolon 622R, and Formolon 622F. 
         [0018]    The halogen containing polymers can be present in compositions of the invention in amounts which range generally from about 15 to about 60, desirably from about 20 to about 40 and preferably from about 25 to about 35 parts by weight based on 100 total parts by weight of the composition. 
         [0019]    Thermoplastic Polyurethane (TPU) 
         [0020]    Thermoplastic polyurethanes are another polymer present in the blend compositions of the present invention. Polyurethanes are generally prepared by combining and reacting a polyol, generally a polyol component of at least one hydroxyl terminated intermediate such as a hydroxyl terminated polyether, polyester, polycarbonate or polycaprolactone, with a polyisocyanate. Polyamines are sometimes included in the reaction. The reaction can additionally include chain extenders and catalysts. Polyisocyanates include two or more isocyanate groups per molecule. Likewise, polyols include two or more hydroxyl groups per molecule. 
         [0021]    In various embodiments, generally any type of TPU can be utilized and blends thereof, such as but not limited to ether and ester TPU grades. The thermoplastic polyurethanes used in the invention may be aliphatic or aromatic, or combinations thereof. In one preferred embodiment, polyurethanes prepared utilizing polyether polyols are preferred. Polyether TPU grades have the advantage of providing improved hydrolysis resistance, mildew resistance, and anti-microbial properties over polyester TPU resin grades. 
         [0022]    Thermoplastic Polyurethanes provide the benefit of achieving exceptional abrasion resistance and chemical resistance. Thermoplastic polyurethanes also are known to reduce the modulus of PVC without incorporating plasticizers. 
         [0023]    Polyurethanes are available from many commercial sources including, but not limited to, A. Shulman, Bayer, BASF, Huntsman, Lubrizol, RTP, and Techmer and COIM under various designations. Suitable TPU grades are from BASF as Elastollan A1154D, Elastollan 1195A, and Elastollan 1190A, Bayer as Texin DP7-3041, Texin DP7-3018, Texin DP7-3006, Texin DP7-3007, Texin DP7-SUN 3006, and from Lubrizol as Estane 58213. 
         [0024]    The polyurethanes can be present in compositions of the invention in amounts which range generally from about 1 to about 50, desirably from about 1 to about 40 and preferably from about 1 to about 25 parts by weight based on 100 total parts by weight of the composition. 
         [0025]    Acrylic Polymers 
         [0026]    The compositions of the present invention include at least one and preferably a plurality of different acrylic polymers. Various different acrylic polymers can be utilized including, but not limited to, polyacrylate-styrene-acrylonitrile, styrene-acrylonitrile, cross-linked acrylonitrile and high molecular weight or ultra-high-molecular weight styrene-acrylonitrile copolymer. 
         [0027]    Polyacrylate-styrene-acrylonitrile (ASA) Copolymer 
         [0028]    The compositions of the present invention also include a polyacrylate-styrene-acrylonitrile copolymer. ASA is typically classified as a terpolymer which can be made by various methods as known to those of ordinary skill in the art. For example, ASA can be made by grafting SAN to an acrylate, for example a polybutylacrylate rubber, to form a SAN-soluble polybutylacrylate rubber. 
         [0029]    Other acrylates can be utilized, such as alkyl (meth)acrylates having generally from about 1 to about 8 carbon atoms, such as methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, or ethylhexyl (meth)acrylate. When utilized herein, the term “(meth)” means that methyl group may be present or absent. Butyl (meth)acrylate is preferred in one embodiment. 
         [0030]    Styrene in the ASA refers to any vinyl aromatic monomer, including, but not limited to styrene; alkyl styrene, such as alpha-methylstyrene; and ring-alkylated styrenes, for example p-methylstyrene. 
         [0031]    Acrylonitrile monomers include acrylonitrile and methacrylonitrile. 
         [0032]    The acrylate content of the ASA ranges generally from about 10 to about 60, desirably from about 30 to about 50 and preferably from about 35 to about 45 parts per 100 parts by weight of the ASA. Further, the ASA typically has a styrene content of from generally about 20 to about 50, desirably from about 25 to about 40 and preferably from about 25 to about 30 parts per 100 parts by weight of the ASA. The ASA has an acrylonitrile content of from generally about 5 to about 35, desirably from about 5 to about 30 and preferably from about 10 to about 20 parts per 100 parts by weight of the ASA. 
         [0033]    Various grades of ASA are commercially available from sources such as BASF as LURAN™ SSE, Sabic as Geloy™ CR3020, and Galata Chemicals as Royaltuf® 960A which is stated to include 60 percent polybutylacrylate and Royaltuf® 945A which is stated to include 45 percent polybutylacrylate. 
         [0034]    ASA provide the benefit of offering exceptional weathering and UV resistance particularly of dark colored articles. 
         [0035]    The ASA can be present in compositions of the invention in amounts which range generally from about 10 to about 50, desirably from about 15 to about 50 and preferably from about 15 to about 35 parts by weight based on 100 total parts by weight of the composition. 
       Styrene Acrylonitrile (SAN) Copolymer 
       [0036]    At least one styrene acrylonitrile copolymer is also present in the compositions of the present invention. In some embodiments, two or more, three or more, etc., different types of SAN are present. SAN is typically classified as a copolymer, which is made by reacting acrylonitrile monomers and styrene monomers, see for example the acrylonitrile and styrene monomers defined hereinabove. 
         [0037]    In one embodiment of the present invention, a so-called standard type of SAN is utilized. SAN provides the benefit of a fusion promoter and process aid for PVC. SAN also provides the ability for dilution with ASA to control the rubber wt % content of the ASA. In a further embodiment of the present invention, the compositions include cross-linked SAN. The cross-linked SAN is useful as a matting agent in various embodiments of the invention. The cross-linked SAN is a matting agent and is a mixture of polystyrene and acrylonitrile-styrene copolymer, including a styrene-based matrix and cross-linked acrylonitrile-styrene copolymer wherein the mixture can include polystyrene in an amount of 20-30 weight % and acrylonitrile-styrene copolymer in an amount of about 70-80 weight %. In yet a further embodiment of the present invention, a relatively high molecular weight styrene-acrylonitrile copolymer is utilized in compositions of the present invention. By high molecular weight it is meant that the end copolymer has a molecular weight greater than 1 million, desirably greater than 2 million, preferably greater than 3 million weight average as measured by Gel Permeation Chromotography (GPC) using a suitable solvent and compared against Polystyrene standards. By comparison, the standard grades of SAN include molecular weights below the lowest range of the high molecular weight SAN, i.e. 1 million weight average or less and preferably below 500,000 weight average. High-molecular weight SAN can adjust the melt strength during extrusion. 
         [0038]    The SAN generally has an acrylonitrile content of preferably from about 10 to about 50 parts by weight based on 100 parts by weight of the SAN. That said, the SAN styrene content ranges preferably from about 50 to about 90 parts by weight based on 100 parts by weight of the SAN. 
         [0039]    The SAN can be present in compositions of the invention in amounts which range generally from about 10 to about 50, desirably from about 10 to about 40 and preferably from about 10 to 30 parts by weight based on 100 total parts by weight of the composition. The cross-linked SAN can be present in compositions of the invention in amounts which range generally from 0.25 to about 4.0, desirably from about 0.50 to about 2.5, and preferably from about 0.75 to about 2.0 parts by weight based on 100 total parts by weight of the composition. High molecular weight SAN can be present in compositions of the invention in amounts which range generally from about 0.1 to about 20, desirably from about 0.1 to about 10 and preferably from about 0.1 to 8 parts by weight based on 100 total parts by weight of the composition. 
         [0040]    Suitable grades of SAN are commercially available from sources such Styrolution as LURAN® 358N, LURAN®-VLN, and LURAN®-VLR and Galata Chemicals as Blendex® 869, Blendex® 5215, Blendex® 5233, and Blendex® BMAT. 
         [0041]    In one preferred embodiment, the compositions of the present invention include two or more, three or more, four more different grades or types of SAN. In one preferred embodiment, the compositions include SAN, cross-linked SAN, and high molecular weight SAN. 
         [0042]    Optional Additives 
         [0043]    The compositions of the present invention can also include additives, each in a sufficient amount to obtain alone or in combination with other components, a desired property of the composition. Such additives are well known to those of ordinary skill in the art and are described in various references regarding polymeric materials, e.g. Modern Plastics Handbook and Additives for Plastic Handbook. Examples of various additives that can be included in compositions of the present invention include, but are not limited to, colorants, pigments, plasticizers, lubricants, UV stabilizers, light stabilizers, thermal stabilizers, antioxidants, antistatic agents, flame retardants, fillers, fibers, processing aids, biocides, surfactants, blowing agents, foaming agents, waxes and combinations thereof. 
         [0044]    The additives can be utilized in various amounts to impart a desired property to the composition. Thus, ranges of individual additives within a composition can vary. 
         [0045]    Composition Form and Processing 
         [0046]    The compositions of the present invention are generally prepared by compounding or blending the desired components in one or more steps, preferably by mixing. The composition is preferably heated to obtain a melted composition, preferably with mixing, to substantially disperse the components thereof, as desired. The blending is preferably performed at a temperature below the decomposition temperatures of the components and generally from about 140° C. to about 200° C. The compositions can be prepared for example in a Banbury, on a two roll mill, in a continuous mixer such as single screw or twin screw extruder, a kneader, or any other mixing machine as known to those of ordinary skill in the art. After preparation of the compositions, they can be processed into any desired form. For example, the compositions can be of a form, such as, but not limited to, a powder, pellet, strand, bead, etc., of various shapes and sizes. Alternatively, the compositions can be directly molded, or shaped as desired, for example using an extruder, injection molder, compression molder, calender, or the like. 
         [0047]    Composition Features for capstock material are high abrasion resistance, excellent outdoor UV protection, high LOI, and good chemical stain resistance. 
         [0048]    Uses/Composites 
         [0049]    In some embodiments, the compositions of the present invention can be formed into a useful article, such as any of the articles mentioned herein. 
         [0050]    Various composites can also be formed including at least one layer of a composition of the present invention and at least a second layer. The composite can be manufactured as articles including, but not limited to, decking, siding, fencing, frames, gutters, appliance housings, appliance liners, building materials, countertops, bathtubs, shower surround materials, railings, shutters, and extruded profiles. 
         [0051]    As illustrated in  FIG. 1 , one suitable use for the compositions of the present invention is as a capstock.  FIG. 1  illustrates an article  10  in the form of an article that can be used for wood-replacement applications, for example decking, fencing, railing, siding, and the like. Article  10  includes a substrate or core  12  and a capstock layer  14 . The core  12  can comprise any desired material, such as, but not limited to, a polymeric material, cellulosic material, metallic material, ceramic material or any combination thereof. 
         [0052]    The substrate or core to which a composition of the present invention can be attached to form a composite is formed from any suitable material. Various thermoplastic resins are especially useful for making building products, but would benefit from a protective or capstock layer of the present invention, with examples including a halogen-containing polymers such as PVC and chlorinated PVC; acrylonitrile-butadiene-styrene (ABS), polyolefins such as polyethylene and polypropylene; polystyrene such as high impact polystyrene; polycarbonate, nylon; polyester; and combinations thereof. In various embodiments the substrate may be foamed, for example foamed PVC, foamed ABS, and other polymeric material. 
         [0053]    Cellulosic materials include any plant matter, for example wood and various plant fibers, such as flax fiber. 
         [0054]    The capstock layer  14  comprises a composition of the present invention. The core  12  can have dimensions that vary according to the end use. Typical dimensions are those such as of wood boards utilized for decking, fencing, siding, railing or the like. The capstock layer  14  is a relatively thin coating layer than may have a thickness generally between about 0.38 to about 1.27 mm, desirably from about 0.51 to about 1.14 mm and preferably from about 0.64 to about 1.02 mm. The capstock layer is present on at least one surface of the article  10 . As illustrated in  FIG. 1 , the capstock layer  14  covers three sides of the core  12  in one embodiment. If desired, all four sides could be coated with a capstock layer. Likewise, the core in some embodiments may have more than six sides that are coated in some embodiments. 
         [0055]    The composition of the present invention can be bonded to a substrate or core layer to form a composite by various methods. For example, a capstock layer can be bonded to the substrate with an adhesive. In other embodiments the capstock layer and substrate layer are laminated or co-extruded to bond the capstock and substrate layers together. It is to be understood that the present invention is not limited to any particular method of making the composite article or product. 
         [0056]    In a preferred embodiment, a composition of the present and a substrate layer adhere to each other and are materials which are compatible and/or miscible with one another. If desired, various surface treatments can be utilized to promote adhesion. Alternatively or in concert therewith, an adhesive can be utilized to adhere various layers of materials utilized to form a composite including or having a layer comprising a composition of the present invention. 
         [0057]    For the avoidance of doubt, the compositions of the present invention encompass all possible combinations of the components, including various ranges of said components, disclosed herein. It is further noted that the term ‘comprising’ does not exclude the presence of other elements. However, it is also to be understood that a description on a product comprising certain components also discloses a product consisting of these components. Similarly, it is also to be understood that a description on a process comprising certain steps also discloses a process consisting of these steps. 
       EXAMPLES 
       [0058]    The examples set forth below are provided to illustrate the compositions of the present invention. These examples are not intended to limit the scope of the invention. 
         [0059]    All of the materials before melt mixing were pre-mixed to a substantially free flowing state and were melt mixed with a Farrel Corp banbury batch mixer. The fluxed batch was dropped and probed with an internal batch temperature between 166° C.-188° C. The fluxed batch was then placed through a two roll which was annealed and prepared into a mill sheet. The mill sheet was cut into strips and run through a dicer. The diced pellets were then run through a two roll mill where another mill sheet was prepared. A portion of this mill sheet was then used for the chemical stain testing. The remainder of the mill sheets were then used to compression mold test plaques using a steam heated press for hardness, oxygen index, and abrasion testing. 
         [0060]    The following raw materials were utilized for the examples. 
         [0000]    
       
         
               
               
             
           
               
                   
               
             
             
               
                 PVC 
                 Oxy 216S from OXY VINYLS LP 
               
               
                 TPU 
                 Texin DP7-3041 from Bayer Material Science LLC 
               
               
                 ASA 
                 Royaltuf 960A from Galata Chemicals LLC 
               
               
                 SAN #1 
                 Blendex 5215 from Galata Chemicals LLC 
               
               
                 SAN #2 
                 Blendex BMAT from Galata Chemicals LLC 
               
               
                 SAN #3 
                 Blendex 869 from Galata Chemicals LLC 
               
               
                 Antimony Oxide 
                 BRIGHTSUN HB from Albermarle Corporation 
               
               
                 Calcium Stearate 
                 COAD 10 from HM ROYAL INC 
               
               
                 PE Wax 
                 Polyethylene AC 629A from Honeywell INC NJ 
               
               
                 EBS Wax 
                 Advawax 280 from PMC Biogenix, INC 
               
               
                 Stearyl Stearate 
                 Struktol VSSE from Struktol Co. 
               
               
                 Ester 
               
               
                 AO/UV 
                 Package from Teknor Apex Co. 
               
               
                 Stabilizer 
                 REATINOR RT4472 from Reagens USA INC 
               
               
                 Pigment 
                 CI Yellow 164 from The Shepherd Color Company 
               
               
                   
               
             
          
         
       
     
         [0061]    Following test protocols were used for testing: 
         [0000]    
       
         
               
               
               
             
           
               
                   
               
             
             
               
                 Hardness 
                 Shore D 
                 ASTM D-2240 
               
               
                 Oxygen Index 
                 % 
                 ASTM D-2863 
               
               
                 Taber Abrasion - H18 
                 Weight loss (g) 
                 ASTM D-1044 
               
               
                 Chemical Staining 
                 SPF Spray 
                 Subject specimen to each 
               
               
                   
                 Gasoline 
                 chemical for 15 minutes and 
               
               
                   
                 Goof Off 
                 subjectively rate as chemical 
               
               
                   
                 Denatured 
                 staining (whitening) occurs 
               
               
                   
                 Alcohol 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
             
               
               
             
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                 Comparative Examples Based on Individual Polymer Components 
               
             
          
           
               
                   
                 Example 
               
             
          
           
               
                   
                 Comparative 
                 Comparative 
                 Comparative 
               
               
                   
                 Example 1 
                 Example 2 
                 Example 3 
               
               
                   
                   
               
             
          
           
               
                 PVC 
                   
                 97.51 
                   
                   
               
               
                 TPU 
                   
                   
                 97.51 
               
               
                 ASA 
                   
                   
                   
                 56.19 
               
               
                 SAN#1 
                   
                   
                   
                 41.32 
               
               
                 SAN#2 
                   
                 1.50 
                 1.50 
                 1.50 
               
               
                 SAN#3 
                   
                 4.00 
                 4.00 
                 4.00 
               
               
                 Antimyony Oxide 
                   
                 3.00 
                 3.00 
                 3.00 
               
               
                 Calcium Stearate 
                   
                 0.30 
                 0.30 
                 0.30 
               
               
                 PE Wax 
                   
                 0.05 
                 0.05 
                 0.05 
               
               
                 EBS Wax 
                   
                 0.40 
                 0.40 
                 0.40 
               
               
                 Stearyl Stearate 
                   
                 0.30 
                 0.30 
                 0.30 
               
               
                 Ester 
               
               
                 AO/UV 
                   
                 0.85 
                 0.85 
                 0.85 
               
               
                 Stabilizer 
                   
                 0.60 
                 0.60 
                 0.60 
               
               
                 Pigment 
                   
                 6.00 
                 6.00 
                 6.00 
               
               
                 Total Parts (weight) 
                   
                 114.51 
                 114.51 
                 114.51 
               
               
                 Hardness Hand 
                 D 
                 83 
                 50 
                 68 
               
               
                 (10 second delay) 
               
               
                 Oxygen Index 
                 % 
                 47.0% 
                 19.5% 
                 20.0% 
               
               
                 Taber Abrasion - 
                 Grams 
                 0.13 
                 0.11 
                 0.24 
               
               
                 H18 after 
                 lost 
               
               
                 1,000 hours 
               
               
                 Chemical Staining 
                   
                 None 
                 Moderate 
                 Slight 
               
               
                 after SPF Spray 
               
               
                 Chemical Staining 
                   
                 None 
                 V. Slight 
                 Slight 
               
               
                 after Gasoline 
               
               
                 Chemical Staining 
                   
                 Slight 
                 Moderate 
                 Severe 
               
               
                 after Goof Off 
               
               
                 Chemical Staining 
                   
                 None 
                 Slight 
                 None 
               
               
                 after Denatured 
               
               
                 Alcohol 
               
               
                   
               
             
          
         
       
     
         [0062]    Table 1 presents three comparative examples utilizing a single polymer. Comparative example 1 utilizes PVC which exhibits a high limiting oxygen index and very good chemical stain resistance, but a high hardness and known poor outdoor UV weather and environmental resistance exists. Comparative example 2 utilizes TPU which has a reduced hardness and improved taber abrasion resistance over PVC but exhibits very poor chemical resistance. Comparative example 3 utilizes ASA which is known to provide superior outdoor UV weather and environmental resistance exhibits moderate chemical resistance but has a poor limiting oxygen index and poor abrasion resistance. 
         [0000]    
       
         
               
             
               
               
             
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                 Comparative Examples Based on Polymer Blends and Inventive Example 
               
             
          
           
               
                   
                 Example 
               
             
          
           
               
                   
                 Comparative 
                 Comparative 
                 Comparative 
                 Inventive 
               
               
                   
                 Example 4 
                 Example 5 
                 Example 6 
                 Example 
               
               
                   
                   
               
             
          
           
               
                 PVC 
                   
                 30.00 
                 30.00 
                   
                 30.00 
               
               
                 TPU 
                   
                 67.51 
                   
                 30.00 
                 20.00 
               
               
                 ASA 
                   
                   
                 38.91 
                 38.91 
                 27.38 
               
               
                 SAN#1 
                   
                   
                 28.60 
                 28.60 
                 20.13 
               
               
                 SAN#2 
                   
                 1.50 
                 1.50 
                 1.50 
                 1.50 
               
               
                 SAN#3 
                   
                 4.00 
                 4.00 
                 4.00 
                 4.00 
               
               
                 Antimyony Oxide 
                   
                 3.00 
                 3.00 
                 3.00 
                 3.00 
               
               
                 Calcium Stearate 
                   
                 0.30 
                 0.30 
                 0.30 
                 0.30 
               
               
                 PE Wax 
                   
                 0.05 
                 0.05 
                 0.05 
                 0.05 
               
               
                 EBS Wax 
                   
                 0.40 
                 0.40 
                 0.40 
                 0.40 
               
               
                 Stearyl Stearate Ester 
                   
                 0.30 
                 0.30 
                 0.30 
                 0.30 
               
               
                 AO/UV 
                   
                 0.85 
                 0.85 
                 0.85 
                 0.85 
               
               
                 Stabilizer 
                   
                 0.60 
                 0.60 
                 0.60 
                 0.60 
               
               
                 Pigment 
                   
                 6.00 
                 6.00 
                 6.00 
                 6.00 
               
               
                 Total Parts (Weight) 
                   
                 114.51 
                 114.51 
                 114.51 
                 114.51 
               
               
                 Hardness Hand (10 
                 D 
                 68 
                 74 
                 60 
                 70 
               
               
                 second delay) 
               
               
                 Oxygen Index 
                 % 
                 21.5% 
                 25.0% 
                 21.0% 
                 24.5% 
               
               
                 Taber Abrasion 
                 Grams 
                 0.13 
                 0.15 
                 0.36 
                 0.21 
               
               
                   
                 lost 
               
               
                 Chemical Staining after 
                   
                 Moderate 
                 None 
                 Moderate 
                 None 
               
               
                 SPF Spray 
               
               
                 Chemical Staining after 
                   
                 None 
                 Slight 
                 Severe 
                 V. Slight 
               
               
                 Gasoline 
               
               
                 Chemical Staining after 
                   
                 Slight 
                 Severe 
                 Severe 
                 Slight 
               
               
                 Goof Off 
               
               
                 Chemical Staining after 
                   
                 V. Slight 
                 None 
                 Moderate 
                 None 
               
               
                 Denatured Alcohol 
               
               
                   
               
             
          
         
       
     
         [0063]    Table 2 presents three comparative examples utilizing polymer blends with either PVC/TPU, PVC/ASA, or ASA/TPU. Comparative example 4 utilizes PVC/TPU which exhibits a relatively low hardness, very low abrasion resistance, but a low LOI and poor chemical stain resistance. Comparative example 5 utilizes a PVC/ASA blend which has a higher LOI and low abrasion resistance, but has a relatively high hardness and suffers severe staining after Goof Off chemical exposure. Comparative example 6 utilizes an ASA/TPU blend which provides improved hardness, but has poor chemical stain resistance, low LOI, and poor abrasion resistance. The inventive example utilizes a ternary blend comprising PVC/ASA/TPU which has an overall balance of properties that are desirable for capstock decking applications as well as other plastic parts. This inventive sample achieves desirable chemical stain resistance, higher LOI, good abrasion resistance, reduced hardness, and good outdoor UV resistance. 
         [0064]    While in accordance with the patent statutes the best mode and preferred embodiment have been set forth, the scope of the invention is not limited thereto, but rather by the scope of the attached claims.