Abstract:
Blends of a polyphenylene ether resin, optionally containing an impact modifier, are filled with finely divided particulate clay which is characterized by a very narrow size distribution, 98 percent or more of the particles being less than 2 microns in diameter, and a very small particle size, with the particles having mean equivalent spherical diameter of from 0.2 to 0.4 microns. This particular clay filler provides rigidity and stiffness, as expected, but with better retention of other physical properties which are normally adversely affected by other mineral fillers, such as larger particle size clay and titanium dioxide. Adhesion between this clay and the polymer, which is already good, is further enhanced by pre-cleaning the clay particles to remove surface dirt, chemicals and salts.

Description:
BACKGROUND OF THE INVENTION 
     The polyphenylene ether resins are a family of engineering thermoplastics known to be admixable with other polymeric materials, such as styrenic copolymeric impact modifiers, to form blends which can be molded into articles of various shapes and sizes. The polyphenylene ether resins and methods of their preparation are described in U.S. Pat. Nos. 3,306,874 and 3,306,875 (Hay), in U.S. Pat. Nos. 3,257,357 and 3,257,358 (Stamatoff), and elsewhere. Styrenic polymers suitable for admixture with the polyphenylene ether resins are described in U.S. Pat. No. 3,383,435 (Cizek), and elsewhere. 
     In general, mineral fillers, such as clay, titanium dioxide, silica, and the like, when incorporated into thermoplastic blends provide greater rigidity and stiffness in the molded or shaped article, as manifested by increases in the modulus, dimensional stability and heat distortion temperature. The use of various mineral fillers in polyphenylene ether resin compositions is described in the patent literature. For instance, mixtures of polyphenylene ether resin, rubber modified high impact polystyrene and aluminum silicate are disclosed in U.S. Pat. No. 4,166,812 (Lee, Jr.). The utility of small particle clay and of small particle titanium dioxide (in both cases, no greater than 0.6 micron in diameter) in plasticized compositions of a polyphenylene ether resin and an ABA block copolymer is disclosed by Abolins, in U.S. Pat. Nos. 4,317,761 and 4,318,836, respectively. 
     While the presence of mineral fillers confers the aforementioned benefits, in the typical case other important physical properties such as the impact strength, tensile elongation (ductility), optical properties and processability are adversely affected. These adverse effects are attributable to the fact that the polymer and mineral filler have poor compatibility and do not adhere well to one another. A result is that the amount of mineral filler which can be used is very limited if large increases in the melt viscosity are to be avoided, and even with smaller filler amounts the compositions must usually be processed at higher temperatures to compensate for the poorer melt flow. 
     INTRODUCTION TO THE INVENTION 
     It has now been discovered that certain grades of clay, having a very small particle size and a very narrow size distribution, as well as a clean surface, are more effective not only in providing the requisite rigidity and stiffness, but with smaller losses in other properties, in comparison with other mineral fillers such as titanium dioxide or larger particle clay. More specifically, this form of clay has the characteristics that 98 percent by weight or more of the particles are finer than 2 microns in diameter, the mean equivalent spherical diameter is in the range from 0.2 to 0.4 microns, and preferably the surface of the particles has been water washed three or more times, usually during manufacturing. 
     Clay fillers having these described features have now been found to be less detrimental than the more bulky fillers as a stress concentrator in the molded article. This is manifested by better properties when compared side by side with the other mineral filler types in blends which are otherwise identical, as shown in the accompanying examples. 
     DESCRIPTION OF THE INVENTION 
     In general, this invention comprises compositions which are admixtures of 
     (a) a polyphenylene ether resin, 
     (b) a plasticizer, and 
     (c) a finely divided particulate clay filler having the following characteristics: 
     (i) a mean equivalent spherical diameter of from 0.2 to 0.4 microns, 
     (ii) 98 percent by weight or more are finer than 2 microns, and optionally 
     (iii) the particles have been water washed three or more times. 
     The water washing of the clay particles is most conveniently carried out during the process of manufacture. Typically, the particles are suspended in water, followed by filtration, after which the procedure is repeated two or more times. The filtration is also useful to separate clay particles outside the prescribed 0.2-0.4 micron range and thus achieving a narrow size distribution, both of which are also essential features for this invention. 
     The washing treatment is believed to remove surface salts and chemicals from the clay particles deposited during manufacture and to result in enhanced adhesion, absorption and/or interpenetration between the clay particles and the polymer matrix in the composition. 
     The terminology &#34;mean equivalent spherical diameter&#34; is employed here in the conventional meaning, and in accordance with the explanation in the Handbook of Fillers and Reinforcement for Plastics, edited by H. J. Katz and J. V. Milewski, Van Nostrand Reinhold Co., New York (1978). The shapes of most filler materials are generally irregular. Kaolin clay, for instance, has the shape of hexagonal platelets. It is rare to find Kaolin clay particles that are true hexagonal platelets, however. The standard definition of the particle size in such cases is &#34;equivalent spherical diameter&#34; or &#34;esd&#34;, or stated another way, the diameter of a sphere having the same volume as that of the particle. 
     The actual particle size distributions of the exemplified clay samples reported herein were determined using a Micrometrics Sedigraph 5000 D Particle Size Analyzer. The results can be expressed graphically as the cumulative mass percent vs. the equivalent spherical diameter in μm. The mean equivalent spherical diameter is the esd at 50% cumulative mass. A more detailed explanation of this technique is found in the article &#34;Rapid, Automatic Particle Size Analysis in the Subsieve Range&#34;, by J. P. Oliver, G. K. Hickin and Clyde Orr, Jr., Powder Technology, 4 (1970/71), pp. 257-263, the disclosure of which is incorporated herein by reference. 
     Especially preferred for use in this invention are clay particles 98 percent by weight or more of which are finer than 1 micron. 
     Preferred polyphenylene ether resins are homopolymers or copolymers having units of the formula ##STR1## in which Q, Q&#39;, Q&#34; and Q&#34;&#39; are, independently, selected from the group consisting of hydrogen, halogen, hydrocarbon radicals, halohydrocarbon radicals, hydrocarbonoxy radicals, and halohydrocarbonoxy radicals; and n represents the total number of monomer units and is an integer of at least about 20, and more usually at least 50. 
     The polyphenylene ether resins are, in general, self-condensation products of monohydric, monocyclic phenols produced by reacting the phenols with oxygen in the presence of complex metal catalysts, with the molecular weight being controlled by the reaction time, longer times providing a higher average number of repeating units. Particular procedures are known to those skilled in the art and are described in the patent literature, including the Hay and Stamatoff patents mentioned above. 
     Suitable phenolic monomers include but are not limited to: 2,6-dimethylphenol; 2,6-diethylphenol; 2,6-dibutylphenol; 2,6-dilaurylphenol; 2,6-dipropylphenol; 2,6-diphenylphenol; 2-methyl-6-ethylphenol; 2-methyl-6-cyclohexylphenol; 2-methyl-6-tolylphenol; 2-methyl-6-methoxyphenol; 2-methyl-6-butylphenol; 2,6-dimethoxyphenol; 2,3,6-trimethylphenol; 2,3,5,6-tetramethylphenol; and 2,6-diethoxyphenol. 
     Some of the polymers which can be produced and which are within the above formula are: poly(2,6-dilauryl-1,4-phenylene)ether; poly(2,6-diphenyl-1,4-phenylene) ether; poly(2,6-dimethoxy-1,4-phenylene)ether; poly(2,6-diethoxy-1,4-phenylene)ether; poly(2-methoxy-6-ethoxy-1,4-phenylene)ether; poly(2-ethyl-6-stearyloxy-1,4-phenylene)ether; poly(2,6-dichloro-1,4-phenylene)ether; poly(2-methyl-6-phenyl-1,4-phenylene)ether; poly(2,6-dibenzyl-1,4-phenylene)ether; poly(2-ethoxy-1,4-phenylene) ether; poly(2-chloro-1,4-phenylene)ether; poly(2,6-dibromo-1,4-phenylene)ether; and the like. 
     Also included within the above formula are copolymers prepared from mixtures of phenolic monomers. Special mention is made of those based on the reaction of 2,6-dimethylphenol with other phenols, for example, with 2,3,6-trimethylphenol or 2-methyl-6-butylphenol, to produce the corresponding copolymer, for example, poly(2,6-dimethyl-co-2,3,6-trimethyl-1,4-phenylene)ether, poly(2,6dimethyl-co-2-methyl-6-butyl-1,4-phenylene)ether, and so forth. 
     Especially preferred for use in this invention are homopolymers having alkyl substituents in the two positions ortho to the oxygen ether atom, that is, those of the above formula in which Q and Q&#39; are alkyl, and particularly alkyl having from 1 to 4 carbon atoms. Most preferred is poly(2,6-dimethyl-1,4-phenylene ether). 
     In general, the plasticizer, component (b), will be a high boiling liquid or low melting solid which has a softening effect on the polyphenylene ether resin and reduces its glass transition temperature. The plasticizer can be selected from among materials known to exert these effects on polymers generally and on polyphenylene ether resins in particular. Suitable types include linear aliphatic esters based on dibasic acids, such as adipates, azelates and sebacates, or on phophorous, such as phosphates; as well as cyclic esters, such as phthalates, terephthalates, benzoates and trimellitates. 
     Preferably, component (b) is an organic phosphate and especially an aromatic phosphate compound of the formula ##STR2## in which R may be the same or different and are selected from the group consisting of alkyl, cycloalkyl, aryl, alkyl substituted aryl, aryl substituted alkyl, halogen, halogen substituted aryl, or a combination of any of the foregoing. 
     Examples include cresyl diphenyl phosphate, 2-ethylhexyl diphenyl phosphate, triphenyl phosphate, triethyl phosphate, dibutyl phenyl phosphate, diethyl phosphate, cresyl diphenyl phosphate, isooctyl diphenyl phosphate, tributyl phosphate, 2-ethylhexyl diphenyl phosphate, isodecyl diphenyl phosphate, isodecyl dicresyl phosphate, didecyl cresyl phosphate, tri-n-hexyl phosphate, di-n-octyl phenyl phosphate, di-2- ethylhexyl phenyl and tri-2- ethylhexyl phosphate, tri(polychlorophenyl) phosphate or mixtures of any of the foregoing. 
     Preferably, at least one R is aryl. Especially preferred is triphenyl phosphate, as such or in one of its modified forms, such as isopropylated triphenyl phosphate. 
     Alternatively, the phosphate can be a di- or polyfunctional compound or polymer having the formula ##STR3## and mixtures thereof, wherein R 1 , R 3  and R 5  are, independently, hydrocarbon; R 2 , R 4 , R 6  and R 7  are, independently, hydrocarbon or hydrocarbonoxy; X 1 , X 2  and X 3  are halogen; m and r are 0 or integers from 1 to 4, and n and p are from 1 to 30. These are described in British Pat. No. 2,043,083, incorporated herein by reference. 
     The presence of component (b) in the compositions lowers the glass transition temperature of the polyphenylene ether resin to an extent proportional to its amount and, in general, increases the resilience, mechanical flexibility and impact strength of moldings made from the compositions. Particular amounts will vary, depending on specific requirements. In the preferred embodiments, however, component (b) is included in a concentration of from about 5 to about 50 parts by weight, for each 100 parts of the total composition. 
     The particulate clay filler, component (c), is preferably included in amounts ranging from about 5 to about 50 parts by weight, for each 100 parts by the total composition weight. 
     The impact modifier, the presence of which in the compositions is optional, but preferred, may be a copolymer or terpolymer of an alkenyl aromatic compound, and especially a compound of the formula ##STR4## in which R 1  and R 2  are selected from the group consisting of lower alkyl or alkenyl groups of from 1 to 6 carbon atoms and hydrogen; R 3  and R 4  are selected from the group consisting of chloro, bromo, hydrogen and lower alkyl of from 1 to 6 carbon atoms; and R 5  and R 6  are selected from the group consisting of hydrogen and lower alkyl and alkenyl groups of from 1 to 6 carbon atoms or R 5  and R 6  may be concatenated together with hydrocarbyl groups to form a naphtyl group. 
     Examples of compounds within the formula are styrene, as well as homologs and analogs thereof, such as alpha-methyl styrene, para-methyl styrene, bromostyrene, dibromostyrene, chlorostyrene, dichlorostyrene, vinyl xylene, divinylbenzene and vinyl naphthalene. 
     Preferred for use as the impact modifier are diblock-, triblock- or radial teleblock copolymers of styrene and a conjugated diene, for example, styrene-butadiene, styrene-isoprene, styrene-butadiene-styrene, styrene-isoprene-styrene, or the like, as well as hydrogenated derivatives thereof, for example, styrene-ethylene/butylene or styrene-ethylene/butylene-styrene. 
     These may be prepared using known processes, such as the sequential polymerization of the corresponding monomers in the presence of an organolithium catalyst, after which the polymer may be treated to reduce the aliphatic unsaturation by selective hydrogenation in the presence of, e.g., nickel (see, for instance, U.S. Patent No. 3,431,323). 
     Suitable impact modifiers are available commercially from Shell Oil Company, Chemicals Division, under the trade designations &#34;Kraton&#34; and &#34;Kraton G&#34;. 
     The impact modifier, if employed, is added to the compositions in amounts effective to enhance the impact strength of the moldings, and generally, from about 2 to about 20 parts by weight, based on 100 parts of the total composition weight. 
     The compositions can also contain supplementary ingredients which may function to modify the chemical and physical properties. These may be selected from among conventional additives such as coloring agents (for example, dyes and pigments), stabilizers, antioxidants, melt flow enhancers, mold release agents, and so forth. Conventional amounts may be employed, ranging from about 1 to about 10 parts by weight, based on 100 parts of the total composition. 
     Preparation of the compositions may be accomplished by dry mixing or solution blending the ingredients, compounding the mixture on a screw extruder at a temperature of from 280 to 330° C., cooling and pelletizing the extrudate, and injection molding the pellets at a temperature of from 260 to 310° C. (55 to 85° C. mold temperature). 
     The compositions can be shaped into a wide variety of articles, and, in general, they can be used for the same purposes for which polyphenylene ether resin blends have heretofore been employed. Thus, a broad spectrum of manufactured objects is possible, ranging from personal care products such as hair driers made of plastic component parts and plastic housings for computers and office business machines, to interior consoles and exterior body trim in automobiles. 
    
    
     DESCRIPTION OF THE SPECIFIC EMBODIMENTS 
     The invention is illustrated in the following examples, which are presented to show preferred or best embodiments but are not intended in any way to be limiting. 
     In the Examples, the various forms of clay filler employed have the following respective characteristics: 
     
         ______________________________________    Wt. %       Wt. %     Mean Equiv.Type of  Finer than  Finer than                          SphericalClay     2 microns   1 micron  Diam., microns______________________________________ASP-100  92          73        0.55HG       94          90        0.29HG-90    97          94        0.29Fine     98.5        98        0.23Particle HGTriple   100         98        0.32FilteredHG-90______________________________________ 
    
     ASP-100 is manufactured by Englehard Minerals and Chemicals Corporation. Each of the &#34;HG&#34; (Hydragloss) clays is a product of the Huber Chemical Company. 
     EXAMPLE 1 
     Compositions were prepared into test specimens by dry mixing 63.5 parts by weight of poly(2,6-dimethyl-1,4-phenylene ether)resin (PPO®, General Electric Company), 4.0 parts by weight of styrene-ethylene/butylene-styrene block copolymer (Kraton G 1651, Shell Chemicals), 14.0 parts by weight of isopropylated triphenyl phosphate plasticizer-flame retardant agent (Kronitex-50, FMC Corp.), 1.0 part by weight of polyethylene, 0.5 part by weight of diphenyl decyl phosphite, 0.15 part by weight of zinc sulfide, 0.15 part by weight of zinc oxide and 17.5 parts by weight of clay (as noted in Table 1). The mixture was compounded by passage through a 28 mm. Werner-Pfleiderer twin screw extruder at a feed temperature of 300° F., and a die temperature of 590° F. (screw speed 300 rpm) under a vacuum equivalent to 10 inches of mercury. The extrudate was pelletized, and the pellets were injection molded on a 3-ounce Newbury injection molding machine, injection temperature 580° F., mold temperature 180°  F. The results are shown in the Table. 
     
                                           TABLE 1__________________________________________________________________________                              Triple Washed                       Fine Particle                              and FilteredCLAY FILLER  ASP-100*              HG* HG-90*                       HG     HG-90__________________________________________________________________________PropertiesNotched Izod impact str.,        1.6   2.4 2.4  3.2    3.6ft. lbs./in. of notchGardner impact str., in.-lb.        204   258 292  274    295Surface gloss, at 45°        47    49  51   56     52Heat distortion temp.        252   252 251  252    245under load at 264 psi,in °F.Injection channel flow        14.8  14.9                  14.5 14.8   15.6length, in.Melt viscosity, poises        3300  3100                  3300 3200   2950Tensile strength, psi        9600  10,000                  10,200                       9900   10,100Tensile yield, psi        11,500              11,700                  11,600                       11,800 11,600Tensile elongation, %        33    34  41   42     45Flexural strength, psi        17,900              18,800                  17,800                       17,500 17,200Flexural modulus, psi        544,000              569,000                  546,000                       477,000                              509,000__________________________________________________________________________ *comparison experiment 
    
     EXAMPLE 2 
     Using the same procedure described in Example 1, additional compositions were prepared for testing from 68 parts by weight of poly(2,6-dimethyl-1,4-phenylene ether)resin (PPO), 4 parts by weight of rubbery styrene-ethylene/butylene-styrene block copolymer (KG 651), 10 parts by weight of isopropylated triphenyl phosphate (K-50), 1.0 part by weight of polyethylene, 0.5 part by weight of diphenyl decyl phosphite, 0.15 part by weight of zinc sulfide, 0.15 part by weight of zinc oxide and 17 parts by weight of clay filler (as noted in Table 2, below. The results are shown in the Table. 
     
                                           TABLE 2__________________________________________________________________________                          Fine Triple Washed      Control             Particle                               and FilteredClay Filler      (none)           ASP-100*                 HG* HG-90*                          HG   HG-90__________________________________________________________________________PropertiesNotched Izod impact      1.3  1.6   1.9 2.0  2.3  2.4str., ft. lbs./in.of notchGardner impact str.,      375  234   232 232  238  258in. lbs.Heat distortion temp.      280  288   291 287  289  297under load at 264psi, °F.Injection channel flow      13.9 12.1  12.0                     12.5 11.7 11.1length, in.Surface gloss, at 45°      58   41    46  46   50   40Tensile strength, psi      10,640           1,400 12,000                     12,000                          11,800                               12,600Tensile yield, psi      13,400           13,600                 13,500                     13,700                          13,600                               13,500Tensile elongation, %      62   36    47  44   38   55Flexural Modulus, psi      350,600           517,100                 509,700                     496,700                          489,600                               508,000Flexural strength, psi      16,600           18,000                 17,800                     17,700                          17,600                               18,000__________________________________________________________________________ *comparison experiment 
    
     EXAMPLE 3 
     The procedure was repeated to prepare molded compositions comprising 65 parts by weight of poly(2,6-dimethyl-1,4-phenylene ether)resin (PPO), 18.5 parts by weight of crystal polystyrene, 8.5 parts by weight of styrene-ethylene/butylene-styrene block copolymer (KG-1651), 0.15 part by weight of zinc sulfide, 0.15 part by weight of zinc oxide and 8 parts by weight of mineral filler (titanium dioxide or various clays, as shown in Table 3). The results are reported below. 
     
                                           TABLE 3__________________________________________________________________________                        Fine Triple Washed      Control           Particle                             and FilteredFiller     (none)           TiO.sub.2 *               HG* HG-90*                        HG   HG-90__________________________________________________________________________PropertiesNotched Izod impact      1.1  1.2 1.7 1.5  1.3  1.8str., ft. lbs./in.of notchGardner impact str.,      188  112 197 179  221  215in. lbs.Heat distortion temp.      306  313 321 310  310  317under load at 264psi, °F.Injection channel flow      14.5 13.5               11.8                   12.6 13.0 12.2length, in.Surface gloss, at 45°      63   60  53  58   58   57Tensile strength, psi      10,100           10,200               10,900                   10,900                        10,800                             10,900Tensile yield, psi      12,900           13,000               13,300                   13,400                        13,500                             13,400Tensile elongation, %      43   29  32  32   21   21Flexural str., psi      16,150           16,100               16,400                   16,900                        16,900                             16,400Flexural modulus, psi      390,700           364,700               387,300                   413,600                        415,900                             404,900__________________________________________________________________________ *comparison experiment 
    
     All of the above mentioned patents are incorporated herein by reference. 
     Other modifications and variations of the invention are possible in the light of the present disclosure. For instance, instead of poly(2,6-dimethyl-1,4-phenylene ether)resin, a copolymer such as poly(2,6-dimethyl-co-2,3,6-trimethyl-1,4-phenylene ether) can be used. Triphenyl phosphate (a solid) can be substituted for K-50 (a liquid). In place of, or in addition to KG 1651, a nonhydrogenated counterpart such as styrene-butadiene-styrene block copolymer, or a radial teleblock copolymer of styrene and butadiene, either hydrogenated or non-hydrogenated (Phillips&#39; Solprene® materials) may be employed as an impact modifier. It is to be understood, therefore, that changes may be made in the specific embodiments shown which are still within the scope of the invention defined in the appended claims.