Abstract:
A process for catalytically cracking deep cut vacuum gas oils, resids, or other reduced crudes containing metal contaminants to increase gasoline octane. Hydrocarbon feedstocks which include vanadium and sodium contaminants are introduced into the reaction zone of a catalytic cracking unit. Catalytic cracking catalysts which include a ZSM-5 type catalytic component are contacted in the reaction zone with the metals-containing hydrocarbon feedstock. The hydrocarbon feedstock is cracked at high temperature by the cracking catalysts, resulting in increased gasoline octane, and surprising tolerance of the ZSM-5 type catalytic component to poisoning from the usually expected synergistically destructive combination of sodium and vanadium on Y-type zeolites.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a process for cracking deep cut vacuum gas oils, resids or other reduced crudes for increased gasoline octane utilizing a catalytic cracking catalyst, which includes a ZSM-5 component that said ZSM-5 component exhibits a surprising tolerance to poisoning by sodium and vanadium. 
     2. Background of the Related Art 
     Current worldwide refinery trends indicate a continuing need to process heavier feedstocks. As a result, many refineries will be processing FCC feeds containing resids or deeper cut gas oils which have high metals content. The phaseout of lead additives for gasoline in both the U.S. and in Europe will require refiners to turn to other alternatives to increase gasoline octane, including octane catalysts. 
     Fluid catalytic cracking (FCC) is commercially practiced in a cycling mode in which a hydrocarbon feedstock is contacted with hot, active, solid particular catalyst without added hydrogen at rather low pressures of up to about 50 PSIG at temperatures sufficient to support the desired cracking. As the hydrocarbon feed is cracked to form more valuable and desirable products, in the presence of a cracking catalyst, carbonaceous residue known as &#34;coke&#34; is deposited on the catalyst. The coke contains carbon as well as metals which are present in the feedstock. 
     In fluid catalytic cracking (FCC), the catalyst is a fine powder of about 20-200 microns in size. The fine powder is propelled upwardly through a riser reaction zone, suspended and thoroughly mixed in the hydrocarbon feed. The hydrocarbon feed is cracked at high temperatures by the catalyst and separated into various hydrocarbon products. The coked catalyst particles are separated from the cracked hydrocarbon products, and after purging, are transferred into the regenerator where the coke is burned off to regenerate the catalyst. The regenerated catalyst then flows downward from the regenerator to the base of the riser. 
     Deposition of coke on the catalyst particles is generally considered undesirable for two reasons: first, it inevitably results in a decline in catalytic activity to a point where the catalyst is considered to have become &#34;spent&#34;; and second, coke generally forms on the catalyst at the expense of the more desired liquid products. To regenerate the catalytic activity, the hydrocarbon residues of the coke must be burnt off of the &#34;spent&#34; catalyst at elevated temperatures in the regenerator. Unlike the hydrocarbon residues, the metallic residues such as vanadium, sodium, nickel and the like, are not removed by high temperature regeneration. Rather, the catalytic cracking catalyst must be somehow protected from the deleterious effects of metallic residues. 
     There are substantial economic incentives for refineries to process reduced crudes due to factors such as the price and availability of heavy fuel oil (&#34;HFO&#34;), coal, the demand for asphalt and a particular refiner&#39;s ability to process the 650+ through 1150+ fractions. 
     Reduced crudes, however, are generally high in metals which poison the cracking catalyst and therefore require a high replacement rate of the catalyst in order to maintain catalyst selectivity and activity. In recent years, extensive research efforts have been directed towards developing improved catalysts and processes for reducing the deleterious effects caused by metals when cracking resids or deep cut vacuum gas oils. 
     The use of ZSM-5 type zeolites, such as ZSM-5, ZSM-11 and the like are known to result in improved gasoline octane and overall yields when used in conjunction with conventional cracking catalysts in cracking gas oils. The use of ZSM-5 in cracking is disclosed in U.S. Pat. Nos. 3,702,886; 3,758,403; 3,894,931; 3,894,933; 3,894,934; 4,309,279; 4,309,280; and 4,416,765. As understood, none of these patents specifically teach the use of ZSM-5 in resid cracking. While more recent patent, U.S. Pat. No. 4,552,648 includes examples which use ZSM-5 with hydrotreated Arab Light Resid, the chargestock contained less than 1 ppm Ni and V. In addition, this patent does not address the unexpected and exceptional metals tolerance of ZSM-5 catalysts to poisoning by these metals. 
     The deleterious effects of metals have been mentioned extensively in the patent literature, for example U.S. Pat. Nos. 4,376,696; 4,513,093 and 4,515,900, and are well known to those skilled in the art. Vanadium substantially deactivates cracking catalysts by irreversibly destroying the active zeolite, while other metals such as nickel promote dehydrogenation reactions which result in undesirable increases in coke and hydrogen yields. 
     It has long been known to those in the petroleum refining art that the combination of sodium and vanadium in a crude feedstock, results in a synergistically destructive effect on the Y-containing cracking catalysts. For example, in the presence of about 0.5 wt % Na, a vanadium level of 5,000 ppm on the catalyst will have a substantially greater destructive effect on the Y-containing zeolite under hydrothermal conditions than when there is no sodium present. A priori, a similar synergistically destructive effect might also be expected by the combination of sodium and vanadium on ZSM-5 type catalysts. 
     It has been previously discovered that ZSM-5 type zeolites used in conjunction with conventional cracking catalysts, exhibit a high tolerance to metal poisoning by vanadium and nickel present in resids or other reduced crudes. The results of this work were disclosed at the fourth CCIC Technical Meeting, Tokyo, Japan on June 9, 1986 in a paper entitled ZSM-5 IN FCC, POTENTIAL IMPACT ON REFINERY OPERATIONS, by F. G. Dwyer, F. Gorra, J. Herbst, Mobil Research and Development Corporation, Paulsboro, N.J. 08066, U.S.A. Briefly, the paper disclosed the excellent tolerance of ZSM-5 to vanadium and nickel poisoning in metal-containing crudes and its resulting advantages and applications in processing resids or other reduced crudes. This publication, however, does not disclose the unexpected resistance of ZSM-5 to the synergistically destructive combination of sodium and vanadium. 
     Octane enhancement in FCC and the excellent metal tolerance by ZSM-5 was again the topic of a presentation at the NPRA ANNUAL MEETING held on Mar. 29-31, 1987, in San Antonio, Tex.. This presentation was published by F. G. Dwyer and P. H. Schipper of Mobil Research and Development Corporation, Paulsboro, New Jersey and F. Gorra of EniChem Anic SA, Milan, Italy, in a document entitled: Octane Enhancement in FCC Via ZSM-5, which is incorporated by reference herein. The document discusses the results of over 25 FCC and TCC operations in the United States and abroad, evaluating octane enhancement by ZSM-5, and contains an excellent background discussion of the use of ZMS-5 in FCC and TCC units. This document, at page 6, is the first to present results of laboratory tests conducted by the inventors herein, with ZSM-5 as an additive catalyst, poisoned by the combination of sodium and vanadium. The results of these tests, summarized in Table 7 of that document, show no change in the octane enhancing performance of the ZSM-5 catalyst. 
     Accordingly, the present invention sets forth a solution to a long felt need in the petroleum refining industry by providing a method for upgrading resids containing high concentrations of metals such as nickel, sodium and vanadium to increase gasoline octane by utilizing a catalytic cracking catalyst, which includes a ZSM-5 component. The ZSM-5 component of the catalyst not only exhibits surprising tolerance to metal poisoning due to nickel and vanadium, but also quite unexpectedly, exhibits tolerance to the normally synergistically destructive combination of sodium and vanadium on Y-type zeolites. 
     SUMMARY OF THE INVENTION 
     Accordingly, the present invention provides a process for catalytically cracking vacuum gas oils, resids, or other reduced crudes containing metal contaminants to increase gasoline octane. Hydrocarbon feedstocks which include vanadium and sodium contaminants are introduced into the reaction zone of a catalytic cracking unit. A catalytic cracking catalyst which includes a ZSM-5 type catalyst component is fluidized in the reaction zone in contact with the metals-containing hydrocarbon feedstock. The hydrocarbon feedstock is cracked at high temperatures by the cracking catalyst, resulting in increased gasoline octane of the hydrocarbon product, and surprising tolerance of the ZSM-5 type catalyst component to poisoning from the normally expected synergistically destructive combination of sodium and vanadium on Y-type zeolites. 
     In addition to the ZSM-5 type component, the cracking catalysts utilized in the process of the present invention also typically contain catalytically active cracking components having a pore size greater than about 7 angstroms. Such components include amorphous silica-alumina, and/or crystalline silicaalumina and/or large pore crystalline zeolites. 
     Representative crystalline zeolite constituents of these cracking catalysts include zeolite X described in U.S. Pat. 2,882,244, zeolite Y described in U.S. Pat. 3,130,007, synthetic mordenite and dealuminized synthetic mordenite, merely to name a few, as well as naturally occurring zeolites, including chabazite, faujasite, mordenite, and the like. Preferred crystalline zeolites include natural faujasite and the synthetic faujasite zeolites X and Y, with particular preference being accorded to zeolite Y. For the purposes of this invention, zeolite Y includes zeolite Y in its as-synthesized form, as well as its variant forms including framework dealuminated zeolite Y, e.g., ultrastable Y (USY) described in U.S. Pat. No. 3,293,192 and LZ-210 described in U.S. Pat. No. 4,503,023. 
     The hydrocarbon feedstock may also include the combination of nickel and sodium, or nickel and vanadium. Preferably, the reaction zone of a catalytic cracking unit is maintained at a temperature from about 900° F. to about 110° F. and the catalyst regenerator temperature is maintained at about 1200°-1400° F. The hydrocarbon feedstock which is introduced into the reaction zone of the catalytic cracking unit, typically contains from about 0.1 to about 25 lbs. sodium and from about 0.5 to about 250 lbs. vanadium per thousand barrels. The ZSM-5 type component of the catalytic cracking catalyst is replaced at a makeup rate of about 0.2 lbs. to about 500 lbs. ZSM-5 per thousand barrels of feedstock processed. Typically, the ZSM-5 type component is present in a range from about 0.5 to about 5% of the catalytic cracking catalyst inventory. 
    
    
     For a better understanding of the present invention, reference is made to the following description and examples, taken in conjunction with the accompanying tables, the scope of which is pointed out in the appended claims. 
     DETAILED DESCRIPTION OF THE INVENTION 
     In contrast to conventional cracking catalysts, the ZSM-5 type catalysts, and ZSM-5 in particular, exhibit significantly greater tolerance to metal poisoning and are therefore particularly applicable to resid upgrading processes. Especially unexpected i the tolerance of the ZSM-5 type component to poisoning from the synergistically destructive combination ofsodium and vanadium which are routinely observed on Y-containing cracking catalysts. This makes ZSM-5 particularly applicable to resid type applications. As discussed in U.S. Pat. No. 4,309,279, incorporated by reference herein, there is a significant improvement in the octane number of gasoline produced by a catalytic cracking unit utilizing ZSM-5 type catalytic components. In addition, as discussed therein, there is also in increase in the total yield of the combination of C 5   +   gasolineand alkylate produced by the catalytic cracking units and alkylation units,respectively, when ZSM-5 type catalytic cracking components are utilized. 
     The catalytic cracking process of the present invention generally operates with a cracking reaction zone temperature of from about 800° to about 1300° F., preferably from about 900° to about 1100° F., and with a catalyst regenerator temperature of from about1000° to about 1800° F., preferably from about 1200° to 1400° F. The deep cut vacuum gas oil or resid feedstock containsfrom about 0.1 to about 25 lbs. sodium and from about 0.5 to about 250 lbs.vanadium per thousand barrels of hydrocarbon feed. The ZSM-5 type componentof the catalytic cracking catalyst is replaced at a makeup rate of from about 0.2 to about 500 lbs. ZSM-5 per thousand barrels of feedstock processed. Typically, the ZSM-5 type component is present in the range from about 0.5 to about 5% of the catalytic cracking inventory. When operating within the aforementioned range of process and feed conditions, the effects of the ZSM-5 component are surprisingly pronounced. Namely, when processing a feedstock containing appreciable amounts of sodium and vanadium at these severe process conditions, very substantial deactivationof catalytic activity occurs on conventional cracking catalysts containing Y-type zeolites. The ZSM-5 type component utilized in the process of the present invention is significantly less affected at these conditions. 
     EXAMPLES 
     Examples 1A-1D 
     1A. A ZSM-5 additive catalyst was prepared by spray drying a mixture containing 20% ZSM-5 in an 87/13 (wt/wt) SiO 2  -Al 2  O 3  gel matrix. The spray dried catalyst was exchanged with a 1.0N NH 4  NO 3  solution and was then washed with 10 cc H 2  O/g catalyst and dried at 250° F. for about 16 hrs. The catalyst was analyzed chemically and found to contain (100% solids basis) 90.6 wt % SiO 2 , 9.4 wt % Al 2  O 3  and &lt;0.01 wt % sodium. 
     1B. A potion of the ZSM-5 additive described in Example 1A was steamed at 1450° F for 10 hours in a 45% steam/55% air, 0 psig atmosphere. Theresulting catalyst surface area was 84 m 2  /g. 
     1C. A portion of the ZSM-5 additive catalyst from Example 1A was blended with an amount of V 2  O 5  powder such that the overall vanadium content was 0.5 wt % in the mixture. This mixture was steamed at the same conditions as specified in Example 1B. The resulting catalyst had a surface area of 62 m 2  /g and a V content of 0.53 wt % based on physical/chemical analyses. 
     1D. A portion of the ZSM-5 additive catalyst from Example 1A was blended with an amount of V 2  O 5  powder such that the overall vanadium content was 1 wt % in the mixture. This mixture was steamed at the conditions specified in Example 1B. The resulting catalyst had a surface area of 46 m 2  /g and a vanadium content of 0.77 wt % based on physical/chemical analyses. 
     Examples 2A-2C 
     Three blends, each containing 2% steamed ZSM-5 in an equilibrium REY base catalyst, were prepared by combining 10 parts by weight of steamed ZSM-5 catalysts from Examples 1B, 1C, and 1D, respectively, with 90 parts by weight of an equilibrium REY cracking catalyst. The resulting catalyst blends were designated as the catalysts of Examples 2A, 2B and 2C, respectively. 
     To demonstrate the effect of vanadium on ZSM-5 performance, the catalysts from Examples 2A-2C along with the equilibrium REY base catalyst were eachcatalytically evaluated in a fixed-fluidized bed unit at 960° F. temperature and 1.0 minutes on-stream using Joliet Sour Heavy Gas Oil (JSHGO) as feed. The JSHGO feed utilized in these evaluations has the properties shown in Table 1. The cat/oil ratio was varied from 2.5-5.0 with a corresponding WHSV range of 15-30 hr -1  to cover a wide range of conversions. The resulting yields at 60 vol % conversion, given in Table 2, clearly demonstrate the excellent vanadium tolerance of the ZSM-5additive catalyst. As indicated by the octane gain and yield shifts, no significant loss of ZSM-5 activity was observed even for the ZSM-5 additive catalyst containing 0.77 wt % vanadium. 
     
                       TABLE 1______________________________________                         Arab Light                         Atmospheric            Joliet Sour Heavy                         ResidChargestock      Gas Oil (JSHGO)                         (ALAR)______________________________________Gravity, API     24.3         20.2Aniline Pt., °F.            171          --Hydrogen, wt. %  12.3         --Sulfur, wt .%    1.87         2.73Nitrogen, wt. %  0.10         --Basic Nitrogen, ppm            327          432Conradson Carbon, wt %            0.28         6.55Kinematic Viscosity at 210° F.            3.6          --Bromine No.      4.2          --R.I. at 70° F.            1.5080       --Molecular Weight 358          435Pour Point, °F.            85           --Paraffins, wt. % 23.5         22.5Naphthenes, wt. %            32.0         19.2Aromatics, wt. % 44.5         58.2Aromatic Carbon, wt. %            18.9         21.5Ni, ppm          0.3          6.0V, ppm           0.6          22.0______________________________________ 
    
     
                       TABLE 2______________________________________Effect of Vanadium on ZSM-5 Performance in FCC         Equil.               +2%      +2%     +2%         REY   ZSM-5    ZSM-5   ZSM-5______________________________________Example         --      2A       2B    2CV Content, ppmBase FCC Catalyst           950     950      950   950ZSM-5 Additive  --      0        5300  7700Conversion, % vol.           60      60       60    60Product Yields:C.sub.5.sup.+  Gasoline, % vol           49.3    46.0     44.7  46.9Total C.sub.4 &#39;s, % vol           11.3    13.2     14.5  12.8Dry Gas, % wt   6.6     8.2      7.9   7.2Coke, % wt      3.8     4.0      3.8   3.9H.sub.2, % wt   0.20    0.19     0.20  0.23LFO, % wt       32.8    32.5     32.6  32.5HFO, % wt       9.0     9.5      9.3   9.4G + D, % wt     73.3    69.8     69.4  71.3n-C.sub.4, % vol           0.9     0.9      1.1   0.9i-C.sub.4, % vol           4.1     4.8      4.9   4.6C.sub.4.sup.=, % vol           4.2     4.9      5.6   4.8C.sub.3, % vol  1.2     1.4      1.2   1.2C.sub.3.sup.=, % vol           6.0     8.6      8.8   7.3Potential Alkylate Yields:Alkylate, % vol 20.7    26.7     28.8  24.3C.sub.5.sup.+  Gasoline +Alkylate, % vol 70.0    72.7     73.5  71.2Additional i-C.sub.4Required, % vol 9.9     13.4     14.7  11.9Octane, RON + O:C.sub.5.sup.+  Gasoline           89.3    90.6     91.2  90.7C.sub.5.sup.+  Gasoline + Alkylate           90.8    91.9     92.3  91.9______________________________________ 
    
     As shown in Table 2, the addition of vanadium had no deleterious effect on ZSM-5 performance. The gasoline octane increased by about 1.3 RON+O due tothe addition of the ZSM-5 catalyst, and was not adversely affected by the presence of up to 0.77 wt % vanadium. In addition, the total C 4  &#39;s and potential alkylate yields, both indicative of ZSM-5 activity, were notsubstantially affected by the addition of vanadium. It was also noted that the addition of vanadium had no observable effect on coke yield. 
     Example 3A and 3B 
     3A. Additive &#34;O&#34;, commercially available ZSM-5 additive catalyst manufactured by the Davison Division of W.R. Grace, was steamed at the conditions specified in Example 1B. This catalyst contains 25% ZSM-5 (supplied by Mobil) and based on chemical analyses contains 74.0 wt % SiO 2 , 25.4 wt % Al 2  O 3  and 0.06 wt % Na. The surface areas of the fresh and steamed catalysts were 116 and 94 m 2  /g, respectively. 
     3B. A portion of the fresh Additive &#34;O&#34; sample was blended with an amount of V 2  O 5  such that the overall vanadium content was 0.5 wt % in the mixture. This mixture was steamed at the conditions specified in Example 1B. The resulting catalyst had a surface area of 63 m 2  /g andwas analyzed by atomic absorption to contain 0.55 wt % vanadium. Examples 4A and 4B 
     Two blends, each containing 2% steamed ZSM-5 in an equilibrium REY base catalyst, were prepared by combining 8 parts by weight of steamed ZSM-5 catalysts from Examples 8 and 9, respectively, with 92 parts by weight of an equilibrium REY cracking catalyst. The resulting blends were designatedas the catalysts of Examples 4A and 4B, respectively. 
     The catalysts of Examples 4A and 4B were evaluated along with the equilibrium REY base catalyst in a fixed-fluidized bed unit in an identical manner to that described in Examples 2A-2C. The results, given in Table 3 for 60 vol % conversion of JSHGO, demonstrate the excellent vanadium tolerance of the ZSM-5 containing Additive &#34;O&#34;. The octane enhancement capability and yield shifts of ZSM-5 are not deleteriously effected by the presence of vanadium. 
     
                       TABLE 3______________________________________Effect of Vanadium on ZSM-5 CatalystPerformance In FCC        Equil.   +2%     +2%        REY      ZSM-5   ZSM-5______________________________________Example        --         4A      4BV Content, ppmBase FCC Catalyst          950        950     950ZSM-5 Additive --         0       5500Conversion, % vol          60         60      60Product Yields:C.sub.5 + Gasoline, % vol          49.3       45.7    43.1Total C.sub.4 &#39;s, % vol          11.3       13.9    14.8Dry Gas, % wt. 6.6        7.4     9.0Coke, % wt.    3.8        3.9     3.9H.sub.2, % wt. 0.20       0.19    0.23LFO, % wt.     32.8       32.5    32.4HFO, % wt.     9.0        9.4     9.6G + D, % wt.   73.3       70.3    68.0n-C.sub.4, % vol          0.9        1.0     0.9i-C.sub.4, % vol          4.1        4.9     4.8C.sub.4.sup.=, % vol          6.4        8.1     9.1C.sub.3, % vol 1.2        1.3     1.2C.sub.3.sup.=, % vol          6.0        7.0     10.4Potential Alkylate Yields:Alkylate, % vol          20.7       26.6    32.4C.sub.5 + Gasoline+ Alkylate, % vol          70.0       72.3    75.5Additional i-C.sub.4 Required,% vol          9.9        13.2    17.2Octane, RON + O:C.sub.5 + Gasoline          89.3       90.7    91.3C.sub.5 + Gasoline + Alkylate          90.8       91.9    92.5______________________________________ 
    
     As shown in Table 3, the addition of vanadium had no deleterious effect on ZSM-5 performance. The gasoline octane increased by about 1.4 RON+O due tothe addition of the ZSM-5  catalyst, and was not adversely affected by the presence of up to 0.55 wt % vanadium. In addition, the total C 4  &#39;s and potential alkylate yields, both indicative of ZSM-5 activity, were notadversely affected by the addition of vanadium. It was also noted that the addition of vanadium had no observable effect on coke yield. 
     The foregoing Examples 1-4 illustrated the excellent vanadium tolerance of ZSM-5. Examples 5 and 6 which follow, are included to compare the vanadiumtolerance of a commercial REY catalyst to the vanadium tolerance of the ZSM-5 catalysts. 
     Examples 5A and 5B 
     5A. The commercial REY catalyst used in this study, Super D, was manufactured by the Davision Division of W.R. Grace. This catalyst was chemically analyzed and found to obtain (100% solids basis) 63.7 wt % SiO 2 , 32.3 wt % Al 2  O 3 , 3.0 wt % RE 2  O 3  and 0.57 wt % Na. X-ray analysis indicates an REY content of about 14 wt %. The surface area of the as-received catalyst was 151 m 2  /g. 
     5B. The commercial REY catalyst of Example 5A was steamed at the conditionsspecified in Example 1B. The resulting surface area was 114 m 2  /g. 
     Example 6A-6C 
     Three portions of the catalyst from Example 5A were each blended with an amount of V 2  O 5  such that the overall vanadium contents in the mixtures were 0.2, 0.5 and 0.75 wt % V, respectively. The three resulting mixtures were individually steamed at the same conditions as specified in Example 1B. The resulting catalysts (designated Examples 6A-6C) contained,based on atomic absorption analyses, 0.23, 0.52 and 0.84 wt % V, respectively with corresponding surface areas of 75, 31 and 22 m 2  /g. 
     To determine the effect of the vanadium on the commercial REY catalyst, thecatalysts from Examples 5B and 6A-6C were evaluated in a fixed-fluidized bed unit at 960° F. temperature, 3.0 cat/oil (15 WHSV), 1.0 minute on-stream using the JSHGO chargestock described in Table 1. The results are summarized in Table 4. 
     
                       TABLE 4______________________________________Vanadium Deactivation of a Commercial REY CatalystCatalysts Stmd: 1450° F., 10 hours, 45/55 Steam/AirExample       5B      6A       6B     6C______________________________________V on Catalyst, ppm         0       2300     5200   8400Conversion at 3 cat/oil,% vol         70.3    62.4     30.8   25.7Surface Area, m.sup.2 /g         114     75       31     22% REY by X-ray         11      8        2      2______________________________________ 
    
     In contrast to the excellent vanadium tolerance of ZSM-5, the results for the REY catalyst, shown in Table 4, indicate a dramatic loss of cracking activity even at 2300 ppm V. At greater than 5000 ppm V the conversion, surface area and X-ray crystallinity data indicate essentially complete destruction of the REY. 
     Examples 7A-7G show the effects of the addition of Ni to both commercial FCC and ZSM-5 additive catalysts. The results of Examples 7 and 8, which follow, indicate that ZSM-5 is substantially less affected by the additionof Ni than conventional REY catalysts, based upon both hydrogen factor and coke yield. 
     Example 7 
     7A. The base catalyst used in this part of the study, MRZ-204S, was manufactured by Catalysts and Chemicals Industries Co., LTD. (CCIC) of Japan. This catalyst was steam deactivated by the procedure specified in Example 1B. The resulting catalyst was designated as the catalyst of Example 7A. The surface areas of the fresh and steamed catalysts are 187 and 121 m 2  /g, respectively. Based on chemical analyses, this catalyst contains (100% solids basis) 60.2 wt % SiO 2 , 37.7 wt % Al 2  O 3 , 0.52 wt % RE 2  O 3  and 0.10 wt % Na. 
     7B. MC-7, a ZSM-5 additive catalyst prepared by CCIC, was steamed at the conditions specified in Example 1B. The resulting catalyst was designated as the catalyst of Example 7B. This catalyst contains 25% ZSM-5 (supplied by Mobil) and based on chemical analyses contains (100% solids basis) 72.0wt % SiO 2 , 27.5 wt % Al 2  O 3  and 0.03 wt % Na. The surface areas of the fresh and steamed catalysts were 153 and 92 M 2  /g, respectively. 
     Examples 7C and 7D 
     The catalysts of Examples 7A and 7B were impregnated at ambient temperaturewith a Wide-Cut Mid-Continental Gas Oil (WCMCGO) chargestock containing about 10,000 ppm Ni as naphthenate diluted with xylene to a total volume sufficient to just fill the catalyst pores. The ratio of catalyst-to-chargestock was 5 wt/wt.; the impregnated catalysts each contained about 2000 ppm Ni. After evaporation of the xylene at 250° F., the impregnated samples were heated to 980° F. in astream of nitrogen in a fixed-fluidized bed, then held at 980° F. for 10 minutes, allowing the impregnated chargestock to crack and deposit the metals and coke on the catalyst. The coke was then removed by combustion in air at 1200° F. The resulting catalysts were designated as the catalysts of Examples 7C and 7D, respectively. 
     7E. A blend which contained 2% ZSM-5 in the base FCC catalyst was prepared by combining 8 parts by weight of the catalyst from Example 7B with 92 parts by weight of the catalyst from Example 7A. 
     7F. A blend which contained 2% Ni-impregnated ZSM-5 in the base FCC catalyst was prepared by combining 8 parts by weight of the catalyst from Example 7D with 92 parts by weight of the catalyst from Example 7A. 
     7G. A blend which contained 2% Ni-impregnated ZSM-5 in the Ni-impregnated base FCC catalyst was prepared by combining 8 parts by weight of the catalyst from Example 7D with 92 parts by weight of the catalyst from Example 7C. 
     Examples 8A and 8B 
     A portion of the Ni-containing catalyst blends from Examples 7F and 7G wereeach steamed at 1250° F. for 4 hrs in 100% steam and 0 psig atmosphere. The resulting catalysts were designated as the catalysts of Examples 8A and 8B, respectively. 
     The catalysts of Examples 7A, 7E-7G and Examples 8A and 8B were evaluated in a fixed-fluidized bed unit in an identical manner to that described in Examples 2A-2C. The results are summarized in Table 5 for 50 vol % conversion of JSHGO. 
     
                                           TABLE 5__________________________________________________________________________Effect of 2000 ppm Ni on ZSM-5 Additive andFCC Base Catalysts at 50 Vol % Conversion of JSHGO.          Base FCC          Catalyst                +2% ZSM-5Example        7A    7E   7F  7G   8A   8B__________________________________________________________________________Ni Content, ppmBase FCC Catalyst          0     0   0    2000 0    2000ZSM-5 Additive --    0   2000 2000 2000 2000Product Yields:C.sub.5 + Gasoline, % vol          42.0  38.9                    36.8 30.3 36.5 32.5Total C.sub.4 &#39;s, % vol          9.4   11.3                    12.2 10.5 12.3 11.6Dry Gas, % wt  5.6   6.8 7.5  7.5  7.4  7.5Coke, % wt     2.4   2.6 2.7  8.8  2.7  6.2H.sub.2, % wt  0.14  0.16                    0.16 0.94 0.19 0.69LFO, % wt      36.5  37.2                    38.1 37.2 37.9 38.2HFO, % wt      14.8  14.2                    13.6 14.5 13.6 13.8G + D, % wt    71.0  69.0                    68.4 62.4 68.2 64.4n-C.sub.4, % vol          0.8   0.8 0.5  0.3  0.8  1.1i-C.sub.4, % vol          3.0   3.5 4.3  2.9  3.7  2.1C.sub.4.sup.=, % vol          5.7   7.0 7.4  7.3  7.8  8.4C.sub.3, % vol 1.2   1.4 1.6  1.1  1.3  0.7C.sub.3.sup.=, % vol          5.2   7.1 8.0  7.8  8.1  7.1RON + O, C.sub.5.sup.+  Gasoline          89.9  91.1                    91.7 93.5 91.5 92.5ΔRON + O --    1.2 1.8  3.6  1.6  2.6ΔC.sub.5.sup.+  Gasoline, % vol          --    -3.1                    -5.2 -11.7                              -5.5 -9.5ΔCoke, % wt          --    0.2 0.3  6.4  0.3  3.8Hydrogen Factor          138   158 157  989  173  564(H.sub.2 /C.sub.1 + C.sub.2 + C.sub.2.sup.=)) × 100__________________________________________________________________________ 
    
     These results, shown in Table 5, demonstrate that 2000 ppm Ni on the ZSM-5 additive caused only slight increases in the dehydrogenation activity as measured by the hydrogen factor and coke yields. In contrast, the additionof 2000 ppm Ni to the base FCC catalyst dramatically increased both the hydrogen factor and coke yields, even following a 1250° F. steamingof the Ni-containing catalyst (Example 8B). 
     It is well known to those skilled in the art that the destructive effect ofvanadium of Zeolite-Y containing cracking catalysts is substantially enhanced by the presence of high sodium levels. In order to determine the effects of added vanadium and/or sodium on the performance of ZSM-5 catalysts, the following Examples 9A-9C were carried out. 
     Examples 9A-9C 
     9A. A portion of the ZSM-5 additive catalyst from Example 1A was impregnated with sufficient NaNO 3  solution to produce a catalyst containing 5000 ppm sodium. The resulting catalyst was dried at 110 ° C. and subsequently steamed at the same conditions under the conditions specified in Example 1B. Ten parts by weight of this steamed ZSM-5 catalyst was then combined with 90 parts of an equilibrium REY cracking catalyst to yield a blend containing 2% steamed ZSM-5 in the equilibrium REY based catalyst. 
     9B. A portion of the fresh ZSM-5 additive catalyst from Example 1A was blended with an amount of V 2  O 5  such that the overall vanadium content in the mixture was 10,000 ppm. This mixture was then steamed underthe conditions specified in Example 1B. Ten parts by weight of this steamedZSM-5  catalyst was then combined with 90 parts of an equilibrium REY cracking catalyst to yield a blend containing 2% steamed ZSM-5 in the equilibrium REY based cracking catalyst. 
     9C. A portion of the fresh ZSM-5 additive catalyst from Example 1A was impregnated with sufficient NaNO 3  solution to produce a catalyst containing 5,000 ppm sodium. This catalyst was then dried at 110 ° C. and blended with an amount of V 2  O 5  such that the overall vanadium content in the mixture was 10,000 ppm. This mixture was then steamed under the conditions specified in Example 1B. Ten parts by weight of this steamed ZSM-5 catalyst was then combined with 90 parts of an equilibrium REY cracking catalyst to yield a blend containing 2% steamed ZSM-5 in the equilibrium REY based cracking catalyst. 
     The catalysts of Examples 9A-9C were evaluated in a fixed-fluidized bed unit in an identical manner to that described in Examples 2A-2C. The results for 60 Volume % conversion of JSHGO are given in Table 6 along with those for both the equilibrium REY based catalyst and the catalyst ofExample 2A. 
     
                                           TABLE 6__________________________________________________________________________SODIUM AND VANADIUM EFFECT ON ZSM-5FCC ADDITIVE CATALYST          Equil.               +2%  +2%  +2%  +2%          REY  ZSM-5                    ZSM-5                         ZSM-5                              ZSM-5__________________________________________________________________________Example        --   2A   9A   9B   9CSodium, ppm    5,000               100  5,000                         100  5,000Vanadium, ppm  950  0    0    10,000                              10,00060 Vol % Conversion          Base Δ                    Δ                         Δ                              ΔC.sub.5 + Gasoline, Vol %          49.3 -3.3 -3.7 -2.4 -3.1RON + O        89.3 +1.3 +1.5 +1.4 +1.5G + D, Vol %   82.1 -3.6 -4.0 -2.7 -2.9C.sub.3.sup.=  + C.sub.4.sup.=  + i-C.sub.4, Vol %          16.5 +4.0 +4.9 +2.7 +3.1__________________________________________________________________________ 
    
     The results, as shown in Table 6, clearly demonstrate that ZSM-5, is highlyresistant to deactivation by sodium, vanadium and the normally expected synergistically destructive combination of sodium and vanadium. Even afterthe addition of 10,000 ppm vanadium and/or 5,000 ppm sodium, the performance of the ZSM-5 containing catalyst was shown to be comparable tothe performance of a ZSM-5 containing catalyst with no added sodium and/or vanadium based upon measurement of octane gain (RON+O). 
     Thus far all the examples have been with a JSHGO feed. Examples 10A and 10Bwere performed to demonstrate the capability of ZSM-5 to enhance gasoline octane and increase the C 3  =+C 4  =yields when cracking Arab LightAtmospheric Resid (ALAR). 
     Examples 10A and 10B 
     10A. The base FCC catalyst used in this Example was obtained by steaming Super D, described in Example 5A, at 1400° F. for 4 hrs in 100% steam and 0 psig atmosphere. 
     10B. The ZSM-5 additive was prepared by spray drying a mixture containing 25% ZSM-5 in a freshly prepared silica-alumina-clay matrix. The silica-alumina-clay matrix was base exchanged with a solution of (NH 4 ) 2  SO 4  followed by RECl 3  exchange prior to addition of the ZSM-5. Chemical analyses results for the spray dried catalyst indicate 72.7 wt % SiO 2 , 12.1 wt % Al 2  O 3  and 0.01wt % Na. This catalyst was then thermally treated at 1200° F. for 0.5 hrs in flowing N 2  at 0 psig and combined with the steamed Super Dof Example 10A in proportions to give a catalyst belnd containing 0.25 wt %ZSM-5. The resulting blend was designated the catalyst of Example 10B. 
     Both the base Super D catalyst of Example 10A and the ZSM-5 containing catalyst blend of Example 10B were evaluated in a fixed-fluidized bed unitat the conditions specified in Examples 2A-2C. A series of runs was made with each catalyst using both the JSHGO and the ALAR chargestocks. The results for 72 vol % conversion of the hydrocarbon chargestocks JSHGO and ALAR, respectively, are shown in Table 7. 
     
                       TABLE 7______________________________________Comparison of ZSM-5 Performance With JSHGOAnd Arab Light Atmospheric Resid Chargestocks         JSHGO     ALAR           REY    +.25%    REY   +.25%Chargestock     Base   ZSM-5    Base  ZSM-5______________________________________Example         10A    10B      10A   10BConversion, % vol.           72     72       72    72Product Yields:C.sub.5.sup.+  Gasoline, % vol           55.9   50.9     44.7  41.9Total C.sub.4 &#39;s, % vol           16.7   19.5     21.8  23.2Dry Gas, % wt   8.5    10.5     9.9   11.2Coke, % wt      3.7    4.1      10.7  10.6n-C.sub.4, % vol           1.8    1.7      2.7   2.6i-C.sub.4, % vol           8.5    10.0     11.6  12.8C.sub.4.sup.=, % vol           6.4    7.7      7.5   7.8C.sub.3, % vol  3.2    3.6      4.4   5.0C.sub.3.sup.=, % vol           7.0    10.0     7.6   9.1Potential Alkylate Yields:Alkylate, % vol 22.4   29.5     25.1  28.2C.sub.5.sup.+  Gasoline+ Alkylate, % vol           78.3   80.4     69.8  70.1Additional i-C.sub.4Required, % vol 6.8    10.2     5.6   6.6Octane, RON + O:C.sub.5.sup.+  Gasoline           88.7   91.4     89.0  90.5C.sub.5.sup.+  Gasoline+ Alkylate      90.2   92.3     90.8  91.9______________________________________ 
    
     The results summarized in TAble 7, show significant octane gains and yield shifts due to ZSM-5 addition with both the atmospheric resid (ALAR) and conventional gas oil (JSHGO) feeds. Therefore, the excellent metals tolerance of ZSM-5 and its capability to enhance gasoline octane when cracking resid make it an ideal octane catalyst for processing reduced crudes. 
     Thus, while there have been described what are presently the preferred embodiments of the present invention, other and further changes and modifications could be made thereto without departing from the scope of the invention, and it is intended to claim all such changes and modifications.