Abstract:
This invention is related to glasses for use as substrates in flat panel display devices; more specifically, for use as substrates in LCDs which utilize polycrystalline silicon thin film transistors. The compositions for the inventive glasses are essentially free from alkali metal oxides and consist essentially, in mole percent, of 
     
       ______________________________________ 
     
     SiO 2   64-70    Y 2  O 3      0-5Al 2  O 3   9.5-14   MgO                 0-5B 2  O 3    5-10    CaO                  3-13TiO 2   0-5      SrO                   0-5.5Ta 2  O 5   0-5      BaO                 2-7Nb 2  O 5   0-5      MgO + CaO + SrO + BaO                                10-20.______________________________________

Description:
This application is a continuation-in-part application of application Ser. No. 08/008,560, filed January 22, 1993, and now abandoned. 
    
    
     RELATED APPLICATION 
     U.S. application Ser. No. 08/8561, filed concurrently with application Ser. No. 08/008,560 under the title BARIUM ALUMINOSILICATE GLASSES and now abandoned, is directed to glasses particularly designed for use as substrates in liquid crystal display devices employing polysilicon thin film transistors as switches. Those glasses exhibit strain points of at least 660° C., liquidus temperatures no higher than 1175° C., viscosities at the liquidus temperature of at least 600,000 poises (60,000 Pa.s), and weight losses of less than 1 mg/cm 2  after immersion for 24 hours in an aqueous 5% by weight HCl solution at 95° C., the glasses being essentially free from alkali metal oxides and consisting essentially, expressed in terms of mole percent on the oxide basis, of 
     
         __________________________________________________________________________SiO.sub.2    65-78    Mgo        0-5                  ZrO.sub.2    0-2.5Al.sub.2 O.sub.37-11    CaO        0-10                  TiO.sub.2    0-3BaO 12-19    SrO        0-10                  Ta.sub.2 O.sub.5                               0-3B.sub.2 O.sub.3    0-5  MgO + CaO + SrO               0-15                  ZrO.sub.2 + TiO.sub.2 + Ta.sub.2 O.sub.5                               0-5__________________________________________________________________________ 
    
     1. Field of the Invention 
     This invention is directed to the production of glass compositions exhibiting high viscosities at their liquidus temperatures. More particularly, this invention is directed to such glasses demonstrating chemical and physical characteristics rendering them especially suitable for use as substrates in flat panel display devices. 
     2. Background of the Invention 
     Liquid crystal displays (LCDs) are passive displays which depend upon external sources of light for illumination. They are manufactured as segmented displays or in one of two basic configurations. The substrate needs (other than being transparent and capable of withstanding the chemical conditions to which it is exposed during display processing) of the two matrix types vary. The first type is intrinsic matrix addressed, relying upon the threshold properties of the liquid crystal material. The second is extrinsic matrix or active matrix (AM) addressed, in which an array of diodes, metal-insulator-metal (MIM) devices, or thin film transistors (TFTs) supplies an electronic switch to each pixel. In both cases, two sheets of glass form the structure of the display. The separation between the two sheets is the critical gap dimension, of the order of 5-10 μm. 
     Intrinsically addressed LCDs are fabricated using thin film deposition techniques at temperatures ≦350° C., followed by photolithographic patterning. As a result, the substrate requirements therefor are often the same as those for segmented displays. Soda-lime-silica glass with a barrier layer has proven to be adequate for most needs. A high performance version of intrinsically addressed LCDs, the super twisted nematic (STN) type, has an added requirement of extremely precise flatness for the purpose of holding the gap dimensions uniform. Because of that requirement, soda-lime-silica glass used for those displays must be polished or, alternatively, a precision formed, barium aluminoborosilicate glass marketed by Corning Incorporated, Corning, New York, as Code 7059 may be used without polishing. 
     Extrinsically addressed LCDs can be further subdivided into two categories; viz., one based on MIM or amorphous silicon (a-Si) devices, and the other based on polycrystalline silicon (poly-Si) devices. The substrate requirements of the MIM or a-Si type are similar to the STN application. Corning Code 7059 sheet glass is the preferred substrate because of its very low sodium content, i.e., less than 0.1% Na 2  O by weight, its dimensional precision, and its commercial availability. Devices formed from poly-Si, however, are processed at higher temperatures than those that are employed with a-Si TFTs. Substrates capable of use temperatures (taken to be 25° C. below the strain point of the glass) of 600°-800° C. are demanded. The actual temperature required is mandated by the particular process utilized in fabricating the TFTs. Those TFTs with deposited gate dielectrics require 600°-650° C., while those with thermal oxides call for about 800° C. Both a-Si and poly-Si processes demand precise alignment of successive photolithographic patterns, thereby necessitating that the thermal shrinkage of the substrate be kept low. Those temperatures have mandated the use of glasses exhibiting higher strain points than soda-lime-silica glass and Corning Code 7059 glass in order to avoid thermal deformation of the sheet during processing. As can be appreciated, the lower the strain point, the greater this dimensional change. Thus, there has been considerable research to develop glasses demonstrating high strain points so that thermal deformation is minimized during device processing at temperatures greater than 600° C., and preferably, higher than 650° C. 
     U.S. Pat. No. 4,824,808 (Dumbaugh, Jr.) lists four properties which have been deemed mandatory for a glass to exhibit in order to fully satisfy the needs of a substrate for LCDs: 
     First, the glass must be essentially free of intentionally added alkali metal oxide to avoid the possibility that alkali metal from the substrate can migrate into the transistor matrix; 
     Second, the glass substrate must be sufficiently chemically durable to withstand the reagents used in the TFT matrix deposition process; 
     Third, the expansion mismatch between the glass and the silicon present in the TFT array must be maintained at a relatively low level even as processing temperatures for the substrates increase; and 
     Fourth, the glass must be capable of being produced in high quality thin sheet form at low cost; that is, it must not require extensive grinding and polishing to secure the necessary surface finish. 
     That last requirement is most difficult to achieve inasmuch as it demands a sheet glass production process capable of producing essentially finished glass sheet, such as the overflow downdraw sheet manufacturing process described in U.S. Pat. No. 3,338,696 (Dockerty) and U.S. Pat. No. 3,682,609 (Dockerty). That process requires a glass exhibiting a very high viscosity at the liquidus temperature plus long term stability, e.g., periods of 30 days, against devitrification at melting and forming temperatures. 
     Corning Code 7059 glass, supra, is currently employed in the fabrication of LCDs. That glass, consisting essentially, in weight percent, of about 50% SiO 2 , 15% B 2  O 3 , 10% Al 2  O 3 , and 24% BaO, is nominally free of alkali metal oxides, and exhibits a linear coefficient of thermal expansion (25°-300° C.) of about 46×10 -7  /° C. and a viscosity at the liquidus temperature in excess of 600,000 poises (6×10 4  Pa.s). The high liquidus viscosity of the glass enables it to be drawn into sheet via the overflow downdraw sheet processing technique, but its relatively low strain point (˜593° C.) is adequate only for processing a-Si devices and not for poly-Si devices. 
     The glasses of U.S. Pat. No. 4,824,808, supra, were designed to meet the requirements for use in fabricating poly-Si devices, including the capability of being formed into sheet by the overflow downdraw sheet processing technique, and linear coefficients of thermal expansion as low as about 36.5×10 -7  /° C. (25°-300° C.), such as to closely match that of silicon, thereby enabling a silicon chip to be sealed directly thereon, but their strain points were less than 650° C. 
     The glasses of U.S. Pat. No. 4,409,337 (Dumbaugh, Jr.) were also considered for LCD substrates, but their long term stability against devitrification was feared to be insufficient for their use in the overflow downdraw sheet processing technique. 
     The glasses of U.S. Pat. No. 5,116,787 (Dumbaugh, Jr.) are essentially free from alkali metal oxides and MgO and demonstrate strain points of 655° C. and higher, with viscosities at the liquidus greater than 1.5×10 5  poises (1.5×10 4  Pa.s). Although designed for use in the overflow downdraw sheet processing technique, their long term stability against devitrification was found to be marginal when employed in the process, some crystallization being formed in the glass during manufacture. Also, the linear coefficients of thermal expansion (25°-300° C.) generally ranged in the upper 40s to low 50s×10 -7  /° C., undesirably high for matching that of silicon (˜35×10 -7  /° C.). 
     U.S. Pat. No. 5,116,788 (Dumbaugh, Jr.) discloses other glasses exhibiting high strain points, i.e., greater than 675° C., but having such relatively low viscosities at the liquidus temperature, viz., 20,000-200,000 poises (2,000-20,000 Pa.s), as to be subject to devitrification when formed utilizing the overflow downdraw sheet processing technique. 
     Finally, U.S. Pat. No. 5,116,789 (Dumbaugh, Jr. et al.) describes other glass compositions demonstrating strain points higher than 675° C., but their linear coefficients of thermal expansion (25°-300° C.) range from 45-62×10 -7  /° C., too high to form a high temperature match with silicon. 
     A recent advance in liquid crystal technology termed &#34;chip-on-glass&#34; (COG) has further emphasized the need for the substrate glass to closely match silicon in thermal expansion. Thus, the initial LCD devices did not have their driver chips mounted on the substrate glass. Instead, the silicon chips were mounted remotely and were connected to the LCD substrate circuitry with compliant or flexible wiring. As LCD device technology improved and as the devices became larger, these flexible mountings became unacceptable, both because of cost and of uncertain reliability. This situation led to Tape Automatic Bonding (TAB) of the silicon chips. In that process the silicon chips and electrical connections to the chips were mounted on a carrier tape, that subassembly was mounted directly on the LCD substrate, and thereafter the connection to the LCD circuitry was completed. TAB decreased cost while improving reliability and increasing the permitted density of the conductors to a pitch of approximately 200 μm--all significant factors. COG, however, provides further improvement over TAB with respect to those three factors. Hence, as the size and quality requirements of LCD devices increase, COG is demanded for those devices dependent upon the use of integrated circuit silicon chips. For that reason, the substrate glass must demonstrate a linear coefficient of thermal expansion closely matching that of silicon; i.e., the glass must exhibit a linear coefficient of thermal expansion (0°-300° C.) between 32-46×10 -7  /° C., most preferably 32-40×10 -7  /° C. 
     SUMMARY OF THE INVENTION 
     The present invention is founded in the discovery of glass exhibiting linear coefficients of thermal expansion over the temperature range of 0°-300° C. between 32-46×10 -7  /° C., strain points higher than 650° C., liquidus temperatures no higher than 1200° C., liquidus viscosities greater than about 200,000 poises (20,000 Pa.s), a weight loss of less than 2 mg/cm 2  after immersion for 24 hours in an aqueous 5% by weight HCl solution at 95° C., long term stability against devitrification at melting and forming temperatures, and melting viscosities of about 200 poises (20 Pa.s) at less than 1675° C., the glasses being essentially free from alkali metal oxides and consisting essentially, expressed in terms of mole percent on the oxide basis, of 
     
         ______________________________________SiO.sub.2 64-70     Y.sub.2 O.sub.3    0-3Al.sub.2 O.sub.3 9.5-14    MgO                0-5B.sub.2 O.sub.3  5-10     CaO                 3-13TiO.sub.2 0-5       SrO                  0-5.5Ta.sub.2 O.sub.5 0-5       BaO                2-7Nb.sub.2 O.sub.5 0-5       MgO + CaO + SrO + BaO                              10-20______________________________________ 
    
     Because of their deleterious effect upon the electrical properties of the glasses, the alkali metal oxides will most preferably be totally absent therefrom. 
     Adherence to those composition intervals has been found to be vital in securing glasses demonstrating properties desired for LCD substrate glasses to be employed in poly-Si devices. To illustrate: 
     If the SiO 2  content is below 64%, the strain point will be too low and the resistance of the glass to attack by acid will be poor. On the other hand, when the concentration of SiO 2  exceeds 70%, the glass becomes difficult to melt at customary glass melting temperatures. 
     The level of Al 2  O 3  is critical to obtain a minimum liquidus temperature; that is, if the concentration of Al 2  O 3  falls below 9.5% or exceeds 14%, the liquidus temperature can exceed 1200° C. 
     B 2  O 3  tends to improve the viscosity character of the glass thereby making it easier to process. Where the level of B 2  O 3  is less than 5%, the liquidus temperature becomes too high. At contents above 10% B 2  O 3 , the resistance to attack by acid is sacrificed and the strain point becomes too low. 
     The alkaline earth metal oxides modify the melting and physical properties of the glass. If the total thereof exceeds 20%, however, the linear coefficient of thermal expansion becomes too high. SrO and BaO raise the thermal expansion more than either MgO or CaO and, hence, will individually not exceed 7%. Because CaO also raises the thermal expansion, but at a slower rate than SrO or BaO, the total thereof ought not to exceed 13%. MgO appears to exert a beneficial effect upon the liquidus temperature at low levels, but, at concentrations greater than 5%, the liquidus temperature appears to rise. 
     The inclusion of TiO 2  is useful in lowering the coefficient of thermal expansion of the glass. The presence of Ta 2  O 5  not only lowers the coefficient of thermal expansion of the glass but also raises the strain point of the glass and significantly improves the chemical durability thereof. Nb 2  O 5  and Y 2  O 3  appear to reduce the coefficient of thermal expansion of the glass and lower the liquidus temperature thereof. 
     In the preferred glasses the level of Al 2  O 3  will exceed that of B 2  O 3  and in the most preferred glasses the composition will consist essentially, expressed in terms of mole percent, of about 
     
         ______________________________________SiO.sub.2 65-69      MgO               1-5Al.sub.2 O.sub.3 10-12      CaO               3-9B.sub.2 O.sub.3  7-10      SrO               1-3TiO.sub.2 0-3        BaO               2-5Ta.sub.2 O.sub.5 0-3        MgO + CaO + SrO + BaO                              11-16______________________________________ 
    
     wherein the ratio Al 2  O 3  :B 2  O 3  &gt;1. The glasses will exhibit a linear coefficient of thermal expansion (0°-300° C.) of 32-40×10 -7  /° C., a liquidus temperature no higher than 1125° C., and a viscosity at the liquidus temperature greater than 600,000 poises (60,000 Pa.s). 
    
    
     DESCRIPTION OF PREFERRED EMBODIMENTS 
     Table I records a number of glass compositions, expressed in terms of parts by weight on the oxide basis, illustrating the compositional parameters of the present invention. Inasmuch as the sum of the individual constituents totals or very closely approximates 100, for all practical purposes the reported values may be deemed to represent weight percent. The actual batch ingredients may comprise any materials, either oxides or other compounds, which, when melted together with the other batch components, will be converted into the desired oxide in the proper proportions. For example, SrCO 3  and CaCO 3  can provide the source of SrO and CaO, respectively. 
     The batch ingredients were compounded, tumble mixed together thoroughly to aid in producing a homogeneous melt, and charged into platinum crucibles. After placing lids thereon, the crucibles were moved into furnaces operating at temperatures of 1600°-1650° C. To assure the production of inclusion- and cord-free glasses a two step melting procedure was used. In the first step the batch was melted for about 16 hours, stirred and then poured as a fine stream into a water bath, a process termed &#34;drigaging&#34; in the glass art. In the second step the finely-divided glass particles from the drigaging were remelted at 1600°-1650° C. for about four hours, the melts stirred in both directions (clockwise and counterclockwise), the melts thereafter poured onto steel plates to make glass slabs having dimensions of about 18&#34;×6&#34;×0.5&#34; (˜45.7×15.2×1.3 cm), and those slabs transferred immediately to an annealer operating at about 730° C. 
     Whereas the above description reflects a laboratory melting procedure, it must be appreciated that the inventive glasses are capable of being melted and formed employing large scale, commercial glass melting and forming equipment. Thus, the glasses are specifically designed to be drawn into thin sheet utilizing the overflow downdraw sheet processing technique. For the experimental glasses described herein, arsenic and/or antimony in amounts of about 0-1% and 0-0.5%, respectively, were added to each batch to perform their customary function as a fining agent. The small residual remaining in the glass has no substantial effect upon the properties of the glass. 
     Table I also lists measurements of several chemical and physical properties determined on the glasses in accordance with techniques conventional in the glass art. Thus, the linear coefficient of thermal expansion (Exp.) over the temperature range 0°-300° C. expressed in terms of ×10 -7  /° C., and the softening point (S.P.), annealing point (A.P.), and strain point (St.P.) expressed in terms of ° C., were determined by fiber elongation. The durability (Dur.) in HCl was determined by measuring the weight loss (mg/cm 2 ) after immersion in a bath of aqueous 5% by weight HCl at 95° C. for 24 hours. 
     The liquidus temperatures of the glasses were measured via two different methods. The standard liquidus method (Liq.) involves placing crushed glass particles in a platinum boat, placing the boat in a furnace having a region of gradient temperatures, heating the boat in an appropriate temperature region for 24 hours, and determining by means of microscopic examination the highest temperature at which crystals appear in the interior of the glass. A second method termed the &#34;meltback liquidus&#34; (M.Liq.) contemplates placing a glass sample which has been precrystallized by holding at a temperature of 1000° C. for 24 hours in a platinum boat, heating the boat in an appropriate temperature region in a gradient furnace for 24 hours, and then determining by microscopic examination the lowest temperature at which crystals are not observed in the interior of the glass. Generally, the liquidus temperatures measured by these two techniques do not differ by more than 50° C., with the &#34;meltback liquidus&#34; typically being higher than the standard liquidus temperature. 
     Table IA records the same glass compositions expressed in terms of mole percent on the oxide basis, the content of the fining agents being omitted as their presence in the final glass is small and has no substantive effect upon the overall properties of the glass. 
     
         __________________________________________________________________________1    2    3    4    5    6    7__________________________________________________________________________SiO.sub.257.0 57.3 56.8 59.3 55.0 59.2 55.8Al.sub.2 O.sub.315.1 14.7 15.3 15.7 14.5 15.6 17.3B.sub.2 O.sub.38.57 8.61 8.55 4.89 8.28 8.90 8.59MgO  0.70 0.70 0.70 0.73 0.68 0.73 0.702CaO  7.64 7.67 7.61 7.95 10.8 4.13 6.51SrO  1.80 1.81 1.80 1.87 1.74 1.87 1.81BaO  9.11 9.15 9.08 9.48 8.79 9.45 9.13As.sub.2 O.sub.30.3  0.3  0.3  0.3  0.3  0.3  0.3Sb.sub.2 O.sub.30.5  0.5  0.5  0.5  0.5  0.5  0.5Exp. 43.0 42.9 43.1 43.7 47.4 38.1 41.0S.P. 924  922  926  961  894  972  950A.P. 705  703  704  733  725  725  722St.P.656  653  656  680  669  668  671Dur. 1.12 --   --   --   1.94 1.88 --M.Liq.1075 1080 1085 1150 1080 1070 1115__________________________________________________________________________8    9    10   11   12   13   14   15__________________________________________________________________________SiO.sub.257.1 57.1 59.1 58.5 57.2 57.8 56.4 59.4Al.sub.2 O.sub.314.7 14.8 15.6 15.6 16.5 15.4 16.0 17.4B.sub.2 O.sub.36.22 7.0  8.31 8.3  9.53 8.2  7.48 10.0MgO  0.285     0.432          1.42 1.42 0.73 1.4  1.38 1.45CaO  9.72 9.01 4.13 4.13 3.18 4.08 4.01 6.05SrO  0.733     1.11 1.87 1.87 1.87 1.84 1.81 *0.09BaO  11.1 10.4 9.46 9.44 9.48 9.33 9.18 5.51TiO.sub.2--   --   --   0.69 1.38 --   --   --Ta.sub.2 O.sub.5--   --   --   --   --   1.87 3.68 --Exp. 45.9 44.8 37.7 37.4 35.0 38   36.5 34.6S.P. 925  924  969  964  971  969  973  966A.P. 713  711  723  721  725  728  739  730St.P.667  660  667  664  667  670  681  676Dur. 0.3  0.4  0.86 0.7  1.28 0.6  0.28 1.6M.Liq.1095 1110 --   --   --   --   --   --Liq. --   --   1065 1060 1090 1055 1055 1085__________________________________________________________________________ *Impurity in BaCO.sub.3 batch material. None purposely added. 
    
     
                                           TABLE IA__________________________________________________________________________1    2    3    4    5    6    7__________________________________________________________________________SiO.sub.265.4 65.6 65.3 68.0 62.7 68.5 64.8Al.sub.2 O.sub.310.2 9.9  10.4 10.6 9.8  10.7 11.8B.sub.2 O.sub.38.55 8.5  8.5  4.8  8.1  8.9  8.61MgO  1.2  1.2  1.2  1.2  1.1  1.2  1.22CaO  9.4  9.4  9.4  9.8  13.2 5.1  8.1SrO  1.2  1.2  1.2  1.2  1.1  1.2  1.22BaO  4.1  4.1  4.1  4.2  3.9  4.3  4.15__________________________________________________________________________8    9    10   11   12   13   14   15__________________________________________________________________________SiO.sub.265.8 65.7 68.1 67.5 66.5 67.7 67.3 66.7Al.sub.2 O.sub.310.0 10.0 10.6 10.6 11.3 10.6 11.2 11.5B.sub.2 O.sub.36.19 6.95 8.26 8.26 8.96 8.29 7.71 9.70MgO  0.49 0.74 1.25 1.25 1.26 1.25 1.26 2.42CaO  12.0 11.1 5.1  5.1  5.16 5.11 5.13 7.27SrO  0.49 0.74 1.25 1.25 1.26 1.25 1.26 --BaO  5.02 4.7  4.27 4.27 4.32 4.28 4.29 2.42TiO.sub.2--   --   --   0.59 1.2  --   --   --Ta.sub.2 O.sub.5--   --   --   --   --   0.3  0.6  --__________________________________________________________________________ 
    
     Example 5 illustrates how a glass with high CaO and low SiO 2  can result in high thermal expansion coefficients. 
     Table II records a second group of glass compositions which were characterized more in depth, again expressed in terms of parts by weight on the oxide basis. Again, because the sum of the individual constituents totals or very closely approximates 100, for all practical purposes the values recited may be considered to reflect weight percent. And, in like manner to the compositions recorded in Table I, the actual batch ingredients may comprise any materials, either oxides or other compounds, which, when melted together, will be converted into the desired oxide in the proper proportions. 
     The batch ingredients were compounded, mixed together, melted, and shaped into glass slabs in accordance with the laboratory procedure outlined above for the glasses of Table I. 
     Table II also lists the measurements of chemical and physical properties conducted on the several glasses along with two additional determinations not performed on the glasses of Table I. First, the melting temperature [Melt, in ° C.] (defined as the temperature at which the glass melt demonstrates a viscosity of 200 poises [20 Pa.s]) has been added, being calculated employing the Fulcher equation as fit to the high temperature viscosity data. Second, the liquidus viscosity (Visc), also calculated using the Fulcher equation coefficients, was added, expressed in terms of ×100,000 poises (10,000 Pa.s). The liquidus temperature reported was determined in accordance with the standard liquidus method (Liq.). Finally, in like manner to the glass compositions of Table I, fining of the glass was accomplished by including arsenic and/or antimony in the glass batch. 
     Table IIA reports the same glass compositions expressed in terms of mole percent on the oxide basis, the concentration of fining agent being omitted because the small residual therefrom has no substantive effect upon the overall properties of the glass. Example No. 16 is a laboratory remelt of Example No. 6. 
     
                                           TABLE II__________________________________________________________________________16   17   18   19   20   21   22   23__________________________________________________________________________SiO.sub.259.2 57.7 59.9 58.8 59.6 58.3 58.2 57.8Al.sub.2 O.sub.315.6 15.2 15.8 15.5 15.8 16.5 16.5 17.0B.sub.2 O.sub.38.90 8.67 9.01 8.84 8.96 8.94 8.32 8.94MgO  0.73 0.71 0.74 --   --   0.73 1.42 0.73CaO  4.13 6.57 2.99 5.45 4.18 4.15 4.14 4.15SrO  1.87 1.82 1.89 1.86 1.88 1.87 1.87 1.87BaO  9.45 9.21 9.57 9.39 9.52 9.49 9.47 9.49Exp. 37.5 42.0 36.2 39.5 37.2 38.1 37.1 37.2S.P. 973  937  992  972  989  980  972  979A.P. 721  707  730  722  732  731  730  735St.P.662  656  669  666  672  673  673  677Dur. 0.62 1.04 0.52 0.63 0.52 0.72 1.1  1.12Liq. 1065 1050 1085 1105 1070 1035 1020 1030Melt 1645 1560 1670 1644 1670 1632 1619 --Visc 21   8.8  22   6.7  32   58   79   --__________________________________________________________________________24   25   26   27   28   29   30   31__________________________________________________________________________SiO.sub.261.3 58.4 58.1 57.3 57.5 55.4 54.5 48.0Al.sub.2 O.sub.314.4 17.1 16.5 16.5 12.5 16.0 16.3 12.8B.sub.2 O.sub.39.8  9.85 7.11 8.35 7.5  7.07 7.22 6.73MgO  1.42 1.43 2.8  2.12 --   4.43 3.13 --CaO  3.95 3.97 4.13 4.15 2.5  2.37 8.23 10.8SrO  3.65 3.67 1.87 1.88 --   7.01 --   8.58BaO  5.4  5.42 9.45 9.5  20.0 7.78 10.6 10.7Exp. 37.2 35.8 39.1 38.6 43.9 41.3 44.5 59.4S.P. 970  969  953  957  917  --   908  --A.P. 719  730  722  726  702  719  703  670St.P.664  674  670  676  653  674  657  627Dur. --   1.8  0.62 0.88 0.39 0.9  2.69 2.9Liq. --   1050 1075 1055 1080 1242 1086 1042Melt --   1610 1585 1595 1758 --   1475 --Visc --   29   8.0  17   14.8 --   1.0  --__________________________________________________________________________32   33   34   35   36   37   38__________________________________________________________________________SiO.sub.257.5 57.2 58.2 57.1 55.69                         57.3 57.3Al.sub.2 O.sub.318.2 18.6 18.4 17.6 19.6 19.0 17.9B.sub.2 O.sub.37.41 7.08 8.14 7.65 7.75 6.79 7.38MgO  1.42 1.76 1.44 1.41 1.43 1.42 1.41CaO  4.13 4.11 4.18 4.1  4.14 4.11 4.11SrO  1.87 1.86 --   --   1.88 1.86 1.86BaO  9.45 9.41 9.57 12.1 9.49 9.43 10.1Exp. 36.9 37.2 34.9 38.1 37.6 36.6 37.8S.P. 987  983  988  981  982  990  983A.P. 740  740  738  734  741  749  743St.P.682  682  678  674  684  693  690Dur. 0.7  0.78 0.83 0.77 1.84 0.66 0.64Liq. 1080 1100 1090 1035 1145 1155 1090Melt 1600 1582 1607 1597 1581 1589 1593Visc 14   8    12   &gt;40  2.2  2.4  11__________________________________________________________________________39   40   41   42   43   44   45   46__________________________________________________________________________SiO.sub.256.3 56.8 57.2 55.8 56.4 55.3 55.5 55.7Al.sub.2 O.sub.318.3 18.4 18.6 17.7 17.9 16.6 16.6 16.7B.sub.2 O.sub.36.38 6.43 6.48 6.32 6.98 7.55 7.58 7.61MgO  1.39 1.4  1.41 1.38 1.39 2.07 2.08 2.08CaO  4.04 4.07 5.06 4.0  4.05 4.04 4.06 4.07SrO  1.83 3.6  1.86 1.81 --   1.83 1.84 1.84BaO  11.83     9.33 9.4  13.0 13.4 9.26 9.3  9.33Ta.sub.2 O.sub.5--   --   --   --   --   2.79 1.87 0.94Nb.sub.2 O.sub.5--   --   --   --   --   0.56 1.12 1.69Exp. 40.1 39.1 38.4 41.2 38.6 38.4 38.4 38.1S.P. 985  986  982  978  985  957  956  951A.P. 746  737  742  740  744  729  728  724St.P.690  681  688  687  690  676  674  671Dur. 0.63 0.57 0.57 0.53 0.59 0.56 0.65 0.7Liq. 1130 1060 1120 1140 1080 1070 1065 1070Melt 1587 1597 1583 1586 1601 --   --   --Visc 4    30   4.5  2.6  14   --   --   --__________________________________________________________________________47   48   49   50   51__________________________________________________________________________SiO.sub.255.9 55.4 55.6 55.9 56.0Al.sub.2 O.sub.316.8 16.6 16.6 16.7 16.8B.sub.2 O.sub.37.64 7.56 7.6  7.63 7.65MgO  2.09 2.07 2.08 2.09 2.1CaO  4.09 4.05 4.06 4.08 4.1SrO  1.85 1.83 1.84 1.85 1.85BaO  9.37 9.27 9.31 9.35 9.38Ta.sub.2 O.sub.5--   2.79 1.87 0.94 --Nb.sub.2 O.sub.52.26 --   --   --   1.13Y.sub.2 O.sub.3--   0.48 0.96 1.44 0.96Exp. 38.3 38.3 38.5 39.2 37.8S.P. 949  961  959  958  955A.P. 724  733  731  733  728St.P.671  680  679  681  676Dur. 0.86 0.64 0.74 0.99 0.97Liq. 1065 1055 1065 1090 1090__________________________________________________________________________ 
    
     
                                           TABLE IIA__________________________________________________________________________16   17   18   19   20   21   22   23__________________________________________________________________________SiO.sub.268.5 66.4 69.5 68.2 69.4 67.7 67.3 67.3Al.sub.2 O.sub.310.7 10.3 10.8 10.6 10.8 11.3 11.2 11.6B.sub.2 O.sub.38.9  8.6  9.0  8.8  9.0  9.0  8.3  8.99MgO  1.2  1.2  1.3  --   ---  1.3  2.5  1.27CaO  5.1  8.1  3.7  6.8  5.2  5.2  5.1  5.18SrO  1.2  1.2  1.3  1.2  1.3  1.3  1.3  1.27BaO  4.3  4.1  4.4  4.3  4.4  4.3  4.5  4.33__________________________________________________________________________24   25   26   27   28   29   30   31__________________________________________________________________________SiO.sub.269.0 66.7 66.5 66.1 70.2 63.6 62.0 57.9Al.sub.2 O.sub.39.52 11.5 11.1 11.2 9.0  10.8 11.0 9.1B.sub.2 O.sub.39.52 9.7  7.03 8.31 7.9  7.0  7.0  7.0MgO  2.38 2.42 4.79 3.65 --   7.58 5.3  --CaO  4.76 4.85 5.07 5.13 3.27 2.91 10.0 14.0Sro  2.38 2.42 1.24 1.26 --   4.66 --   6.0BaO  2.38 2.42 4.24 4.29 9.57 3.49 4.7  6.0__________________________________________________________________________32   33   34   35   36   37__________________________________________________________________________SiO.sub.266.9 66.5 67.4 66.9 65.3 66.9Al.sub.2 O.sub.312.5 12.7 12.6 12.2 13.5 13.1B.sub.2 O.sub.37.44 7.09 8.12 7.74 7.83 6.84MgO  2.46 3.04 2.47 2.46 2.49 2.46CaO  5.15 5.11 5.18 5.15 5.21 5.15SrO  1.26 1.25 --   --   1.27 1.26BaO  4.31 4.28 4.33 5.56 4.36 4.31__________________________________________________________________________38   39   40   41   42   43__________________________________________________________________________SiO.sub.266.8 66.5 66.5 66.5 66.3 66.7Al.sub.2 O.sub.312.3 12.7 12.7 12.7 12.4 12.4B.sub.2 O.sub.37.42 6.5  6.5  6.5  6.48 7.11MgO  2.45 2.44 2.44 2.44 2.44 2.44CaO  5.14 5.11 5.11 6.31 5.1  5.13SrO  1.26 1.25 2.44 1.25 1.25 --BaO  4.6  5.47 4.28 4.28 6.05 6.14__________________________________________________________________________44   45   46   47   48   29   50   51__________________________________________________________________________SiO.sub.265.7 65.7 65.7 65.7 65.7 65.7 65.7 65.7Al.sub.2 O.sub.311.6 11.6 11.6 11.6 11.6 11.6 11.6 11.6B.sub.2 O.sub.37.74 7.74 7.74 7.74 7.74 7.74 7.74 7.74MgO  3.66 3.66 3.66 3.66 3.66 3.66 3.66 3.66CaO  5.15 5.15 5.15 5.15 5.15 5.15 5.15 5.15SrO  1.26 1.26 1.26 1.26 1.26 1.26 1.26 1.26BaO  4.31 4.31 4.31 4.31 4.31 4.31 4.31 4.31Ta.sub.2 O.sub.50.45 0.3  0.15 --   0.45 0.3  0.15 --Nb.sub.2 O.sub.50.15 0.3  0.45 0.6  --   --   --Y.sub.2 O.sub.3--   --   --   --   0.15 0.3  0.45 0.3__________________________________________________________________________ 
    
     Examples 28-31 illustrate glasses having compositions close to, but somewhat outside of, the inventive ranges. Thus, the SiO 2  and BaO concentrations are too high in Example 28; the level of SiO 2  is low and that of MgO too high in Example 29; the content of SiO 2  is low in Example 30; and the amount of SiO 2  is low and that of CaO too high in Example 31. 
     Examples 16, 21, 22, 25, 26, and 27 constitute preferred compositions with Example 21 being the most preferred based upon its overall combination of chemical, physical, and melting properties.