Abstract:
An improved process is disclosed for the selective disproportionation of toluene. The process preferably uses a disproportionation catalyst comprising MFI bound with alumina phosphate. Running the process at a hydrogen to hydrocarbon ratio between 0.2 to 0.5 improves the yield of para-xylene. Optional periodic rejuvenation by increasing the hydrogen to hydrocarbon ratio removes some carbon deposits and restores catalyst activity.

Description:
FIELD OF THE INVENTION 
     This invention relates to an improved process for the conversion of aromatic hydrocarbons, such as conversion of toluene into paraxylene. More specifically, the present invention concerns operating a disproportionation process at very low hydrogen to hydrocarbon level to promote favorable selectivity. 
     BACKGROUND OF THE INVENTION 
     The xylene isomers are produced in large volumes from petroleum as feedstocks for a variety of important industrial chemicals. The most important of the xylene isomers is para-xylene, the principal feedstock for polyester which continues to enjoy a high growth rate from large base demand. Orthoxylene is used to produce phthalic anhydride, which has high-volume but mature markets. Meta-xylene is used in lesser but growing volumes for such products as plasticizers, azo dyes and wood preservers. Ethylbenzene generally is present in xylene mixtures and is occasionally recovered for styrene production, but usually is considered a less-desirable component of C 8  aromatics. 
     Among the aromatic hydrocarbons, the overall importance of the xylenes rivals that of benzene as a feedstock for industrial chemicals. Neither the xylenes nor benzene are produced from petroleum by the reforming of naphtha in sufficient volume to meet demand, and conversion of other hydrocarbons is necessary to increase the yield of xylenes and benzene. Often toluene is selectively disproportionated to yield benzene and C 8  aromatics from which the individual xylene isomers are recovered. 
     A current objective of many petrochemical and aromatics complexes is to increase the yield of xylenes and to de-emphasize benzene production Demand is growing faster for xylene derivatives than for benzene derivatives. Refinery modifications are being effected to reduce the benzene content of gasoline in industrialized countries, which will increase the supply of benzene available to meet demand. A higher yield of xylenes at the expense of benzene thus is a favorable objective, and processes to transalkylate C 9  aromatics along with toluene have been commercialized to obtain high xylene yields. 
     U.S. Pat. No. 4,016,219 B1 (Kaeding) discloses a process for toluene disproportionation using a catalyst comprising a zeolite which has been modified by the addition of phosphorus in an amount of at least 0.5 mass-%. The crystals of the zeolite are contacted with a phosphorus compound to effect reaction of the zeolite and phosphorus compound. The modified zeolite then may be incorporated into indicated matrix materials. 
     U.S. Pat. No. 4,097,543 B1 (Haag et al.) teaches toluene disproportionation for the selective production of para-xylene using a zeolite which has undergone controlled precoking. The zeolite may be ion-exchanged with a variety of elements from Group IB to VIII, and composited with a variety of clays and other porous matrix materials. 
     U.S. Pat. No. 4,182,923 B1 (Chu) describes a process for toluene disproportionation with a high conversion of the toluene to benzene and paraxylene by use of an aluminosilicate zeolite of silica to alumina ratio above 12 and which has been modified by treatment with ammonium hydrogen phosphate to deposit phosphorus. 
     U.S. Pat. No. 4,629,717 B1 (Chao) discloses a phosphorus-modified alumina hydrogel formed by gelation of a homogeneous hydrosol. The composite has a high surface area of 140-450 m 2 /g and high activity and selectivity in 1-heptene conversion tests. 
     U.S. Pat. No. 6,114,592 B1 (Gajda et al.), which is incorporated herein by reference, teaches an improved process combination for the selective disproportionation of toluene. The combination comprises selective hydrogenation of a toluene feedstock followed by a zeolitic catalyst. 
     Workers in the field of aromatics disproportionation continue to seek processes and catalysts having exceptionally high selectivity for paraxylene from toluene combined with favorable activity and stability. 
     SUMMARY OF THE INVENTION 
     It is an object of the present invention to provide an improved process for the disproportionation of aromatic hydrocarbons. A specific objective is to obtain a high yield of xylenes by selective toluene disproportionation. 
     This invention is based on the unexpected finding that operation at very low levels of hydrogen to hydrocarbon promotes favorable selectivity to paraxylene. Soft coke that is deposited upon a catalyst at such low ratio processing can also be periodically removed by conducting periodic rejuvenation at higher molar ratios of hydrogen to hydrocarbon. Further, low ratio processing also improves the selective precoking and conditioning of zeolitic catalysts. 
     The present invention is directed to a process for the production of xylene comprising a selective disproportionation zone at conditions comprising a hydrogen to hydrocarbon ratio of less than 0.5. In the disproportionation zone the stream is contacted with a disproportionation catalyst at disproportionation conditions. The disproportionation catalyst preferably comprises a pentasil zeolitic aluminosilicate, most preferably MFI. This catalyst is subjected to a precoking step prior to its use in the disproportionation zone in order to increase its selectivity to paraxylene in the product beyond its equilibrium concentration. 
     Mixed C 8  aromatics recovered from the disproportionation effluent are sent to a xylene-separation zone; preferably, para-xylene is recovered by adsorption and/or crystallization. The xylene-separation zone may also comprise a catalytic alkyl-aromatic zone for ethylbenzene conversion and dealkylation. 
     Periodic disproportionation catalyst rejuvenation can also be conducted by increasing the ratio of hydrogen to hydrocarbon above 0.5, preferably to somewhere in the range of about 1 to about 5. 
     These as well as other objects and embodiments will become apparent from the detailed description of the invention. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 shows the yields of xylenes versus process hydrogen to hydrocarbon ratio. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     A broad embodiment of the present invention is a selective toluene disproportionation process operating at low hydrogen to hydrocarbon ratio for increased selectivity to para-xylene. Accordingly, one necessary element of the process is a zeolitic catalyst which has been subjected to a precoking step, prior to its use for disproportionation, in order to deposit a controlled concentration of carbon on the catalyst and increase paraxylene selectivity. The paraxylene content of the paraxylene-rich product from disproportionation is in excess of its equilibrium concentration at disproportionation conditions. 
     The selective disproportionation process zone of the present invention comprises a molecular sieve and a refractory inorganic oxide. The preferred molecular sieves are zeolitic aluminosilicates, or zeolites, which may be any of those which have a SiO 2 /Al 2 O 3  ratio greater than about 10, preferably than 20, and a pore diameter of about 5 to 8 Angstroms (Å). Specific examples of zeolites which can be used are the MFI, MEL, EUO, FER, MFS, MTT, MTW, TON, MOR and FAU types of zeolites. Pentasil zeolites MFI, MEL, MTW and TON are preferred, and MFI-type zeolite, often designated ZSM-5, is especially preferred. 
     The preparation of the preferred MFI-type zeolite is well known in the art. The zeolite preferably is prepared by crystallizing a mixture containing an alumina source, a silica source, an alkali metal source, water and an alkyl ammonium compound or its precursor. 
     A refractory binder or matrix is utilized to facilitate fabrication of the disproportionation catalyst, provide strength and reduce fabrication costs. The binder should be uniform in composition and relatively refractory to the conditions used in the process. Suitable binders include inorganic oxides such as one or more of alumina, magnesia, zirconia, chromia, titania, boria, thoria, zinc oxide and silica. Alumina and/or silica are preferred binders. The amount of zeolite present in the bound catalyst can vary considerably but usually is present in an amount from about 30 to 90 mass percent and preferably from about 50 to 80 mass percent of the catalyst. 
     A preferred binder or matrix component is a phosphorus-containing alumina (hereinafter referred to as aluminum phosphate) component. The phosphorus may be composited with the alumina in any acceptable manner known in the art. The zeolite and aluminum phosphate binder are mixed and formed into particles by means well known in the art such as gellation, pilling, nodulizing, marumerizing, spray drying, extrusion or any combination of these techniques. A preferred method of preparing the zeolite/aluminum phosphate support involves adding the zeolite either to an alumina sol or a phosphorus compound, forming a mixture of the alumina sol/zeolite/phosphorus compound into particles by employing an oil-drop method as described here-in-below and calcining the spherical particles. 
     The preferred oil-drop method of preparing the aluminum phosphate is described in U.S. Pat. No. 4,629,717 B1 which is incorporated by reference. The technique described in the &#39;717 patent involves the gellation of a hydrosol of alumina which contains a phosphorus compound using the well-known oil-drop method. Generally this technique involves preparing a hydrosol by digesting aluminum in aqueous hydrochloric acid at reflux temperatures of about 80° to 105° C. The ratio of aluminum to chloride in the sol ranges from about 0.7:1 to 1.5:1 mass ratio. A phosphorus compound is now added to the sol. Preferred phosphorus compounds are phosphoric acid, phosphorous acid and ammonium phosphate. The relative amount of phosphorus and aluminum expressed in molar ratios ranges from about 10:1 to 1:100, respectively, on an elemental basis. The zeolite is added to the aluminum phosphate hydrosol and the mixture is gelled. One method of gelling this mixture involves combining a gelling agent with the mixture and then dispersing the resultant combined into an oil bath or tower which has been heated to elevated temperatures such that gellation occurs with the formation of spheroidal particles. The gelling agents which may be used in this process are hexamethylene tetraamine, urea or mixtures thereof. The gelling agents release ammonia at the elevated temperatures which sets or converts the hydrosol spheres into hydrogel spheres. The combined mixture preferably is dispersed into the oil bath in the form of droplets from a nozzle, orifice or rotating disk. The spheres are then continuously withdrawn from the oil bath and typically subjected to specific aging and drying treatments in oil and in ammoniacal solution to further improve their physical characteristics. The resulting aged and gelled particles are then washed and dried at a relatively low temperature of about 100° to 150° C. and subjected to a calcination procedure at a temperature of about 450° to 700° C. for a period of about 1 to 20 hours. 
     Alternatively, the particles may be formed by spray-drying the mixture. In any event, conditions and equipment should be selected to obtain small spherical particles; the particles preferably should have an average diameter of less than about 1.0 mm, more preferably from about 0.2 to 0.8 mm, and optimally from about 0.3 to 0.8 mm. 
     The amount of phosphorus-containing alumina component present (as the oxide) in the catalyst can range from about 10 to 70 mass percent and preferably from about 20 to 50 mass percent. The aluminum phosphate binder/matrix optionally may contain lesser proportions of other inorganic oxides including, but not limited to, magnesia, beryllia, boria, silica, germania, tin oxide, zinc oxide, titania, zirconia, vanadia, iron oxide, chromia, cobalt oxide and the like which can be added to the hydrosol prior to dropping. 
     The aluminum-phosphate binder generally is amorphous, i.e., the binder material is essentially of amorphous character. Preferably less than about 10 mass-% of the binder pore volume is micropore volume, characteristic of crystalline material, and the micropore volume more preferably is less than 5% and optimally less than 2% of the pore volume. Crystalline aluminophosphate generally is an unsuitable binder material for preparing a strong, crush-resistant catalyst. Material that is not in an amorphous phase generally is present as gamma-alumina; as the phosphorus content of amorphous aluminum phosphate is decreased, therefore, the proportion of crystalline material is increased. The average bulk density of the spheres also varies with the phosphorus content, as a higher proportion of phosphorus decreases the average bulk density. Surface area also is controlled by phosphorus content: gamma-alumina oil-dropped spherical particles typically have surface areas up to about 250 m 2 /g, while spheroidal particles of aluminum phosphate may have surface areas of up to about 450 m 2 /g. Al/P atomic ratios of the binder/matrix generally range from about 1/10 to 100/1, more typically from about 1/5 to 20/1, and often between about 1:1 and 5:1. 
     Best results are achieved when the catalyst has an X-ray diffraction pattern showing characteristic intensities of peaks at specified Bragg angle positions. Specifically, the preferred catalyst has an X-ray powder diffraction pattern such that the ratio of peak intensities at respective two-⊖ Bragg angle positions of about 48.5:46.5 is at least about 1.1 and the ratio of peak intensities at respective two-⊖ Bragg angle values of about 48.5:47.5 is at least about 1.0. The X-ray pattern may be obtained by standard X-ray powder diffraction techniques, of which a suitable example is described hereinbelow. Typically, the radiation source is a high-intensity, copper-target, X-ray tube operated at 45 KV and 35 mA. Flat compressed powder samples illustratively are scanned in a continuous mode with a step size of 0.030° and a dwell time of 9.0 seconds on a computer-controller diffractometer. The diffraction pattern from the copper K radiation may be recorded with a Peltier effect cooled solid-state detector. The data suitably are stored in digital format in the controlling computer. The peak heights and peak positions are read from the computer plot as a function of two times theta (two-⊖), where theta is the Bragg angle. 
     It is within the scope of the invention that the catalyst contains a metal component, preferably selected from components of the group consisting of gallium, rhenium and bismuth. Preferably, however, the catalyst consists essentially of a zeolitic aluminosilicate having a pore diameter from about 5 to 8 Å and an aluminum phosphate binder. 
     The zeolitic catalyst is subjected to selective precoking to increase the proportion of paraxylene in the paraxylene-rich product above equilibrium levels at disproportionation conditions. Precoking of the present catalyst effects a proportion of paraxylene in the product above equilibrium levels at disproportionation conditions, preferably at least about 80 mass-% and optimally about 90 mass-% or more of the C 8  aromatics. Precoking is effected on a fresh or regenerated catalyst, prior to its use for disproportionation, for a time ranging from about 0.5 hours to 10 days. 
     The precoking is effected at conditions relative to the subsequent disproportionation step comprising one or more of a higher temperature, lower pressure, higher space velocity, and higher hydrogen to hydrocarbon ratio. Such precoking conditions comprise a pressure of from about 100 kPa to 4 MPa absolute, and a liquid hourly space velocity of from about 0.2 to 10 hr −1 . The conditions comprise one or more of an inlet temperature at least about 50° C. higher; a pressure at least about 100 kPa lower, or preferably no more than about half of the pressure utilized in the subsequent disproportionation step. Preferably the molar ratio of free hydrogen to feedstock coke-forming hydrocarbons is no more than about half of that utilized in the subsequent disproportionation step. Lower pressure and/or a lower hydrogen/hydrocarbon ratio will lower the proportion of exothermic aromatic-saturation reactions, and thus restrict the temperature rise; the result thus should be a relatively flatter temperature profile. Thus a typical temperature range would be from about 300° C. to about 700° C. and a typical hydrogen to coke-forming feed range would be about 0.01 to about 5. 
     It is believed that the temperature profile affects the coking rate in various parts of the catalyst bed. A steep temperature gradient therefore will effect non-uniform coke deposition, and different parts of the catalyst bed thus will be selectivated to a different extent causing poorer performance in the subsequent disproportionation step. Thus a typical temperature differential across the bed of catalyst during selective precoking would be between about a 3° C. increase and about a 4° C. decrease. 
     Precoking effects a catalyst coke or carbon content of between about 5 and 40 mass-% carbon, and preferably between about 10 and 30 mass-% carbon. A coke-forming feed for precoking may comprise the feedstock to the disproportionation step as described hereinbelow, such as toluene, or other specific hydrocarbons or mixtures known in the art preferably comprising aromatics may be used. Further details relative to precoking are disclosed in U.S. Pat. No. 4,097,543 B1 and U.S. Pat. No. 6,191,331 B1, incorporated herein by reference. 
     The feedstock to the present process comprises alkylaromatic hydrocarbons of the general formula C 6 H (6−n) R n , where n varies from 0 to 5 and R is CH 3 , C 2 H 5 , C 3 H 7 , or C 4 H 9 , in any combination to obtain more-valuable alkylaromatics. Suitable alkylaromatic hydrocarbons include, for example but without so limiting the invention, benzene, toluene, xylenes, ethylbenzene, trimethylbenzenes, ethyltoluenes, propylbenzenes, tetramethylbenzenes, ethyldimethylbenzenes, diethylbenzenes, methylpropylbenzenes, ethylpropylbenzenes, triethylbenzenes, di-isopropylbenzenes, and mixtures thereof. 
     The feedstock preferably comprises toluene, optionally in combination with C 9  aromatics, and suitably is derived from one or a variety of sources. Feedstock may be produced synthetically, for example, from naphtha by catalytic reforming or by pyrolysis followed by hydrotreating to yield an aromatics-rich product. The feedstock may be derived from such product with suitable purity by extraction of aromatic hydrocarbons from a mixture of aromatic and nonaromatic hydrocarbons and fractionation of the extract. For instance, aromatics may be recovered from a reformate. The reformate may be produced by any of the processes known in the art, with a process based on platinum containing L-zeolite being especially preferred for light aromatic production. The aromatics then may be recovered from the reformate through the use of a selective solvent, such as one of the sulfolane type, in a liquid-liquid extraction zone. The recovered aromatics may then be separated into streams having the desired carbon number range by fractionation. The feedstock should contain no more than about 10 mass-% non-aromatics; the content of benzene and C 8  aromatics is principally an economic decision relating to the dilution of toluene from these aromatics. When the severity of reforming or pyrolysis is sufficiently high, extraction may be unnecessary and fractionation may be sufficient to prepare the feedstock. 
     A preferred component of the feedstock is a heavy-aromatics stream comprising C 9  aromatics, thereby effecting transalkylation of toluene and C 9  aromatics to yield additional Xylenes. Benzene may also be transalkylated to yield additional toluene. Indane may be present in the heavy-aromatics stream although it is not a desirable component to effect high yields of C 8 -aromatics product. C 10 +aromatics also may be present, preferably in an amount of 30% or less of the feed. The heavy-aromatics stream preferably comprises at least about 90 mass-% aromatics, and may be derived from the same or different known refinery and petrochemical processes as the benzene and toluene feedstock and/or may be recycled from the separation of the product from transalkylation. 
     Within the disproportionation process the feed usually is first heated by indirect heat exchange against the effluent of the reaction zone and is then further heated in a fired heater. The resulting vaporous stream is then passed through a reaction zone which may comprise one or more individual reactors. The use of a single reaction vessel having a fixed cylindrical bed of catalyst is preferred, but other reaction configurations utilizing moving beds of catalyst or radial-flow reactors may be employed if desired. Passage of the combined feed through the reaction zone effects the production of a vaporous effluent stream comprising hydrogen and both product and unconverted feed hydrocarbons. This effluent is normally cooled by indirect heat exchange against the stream entering the reaction zone and then further cooled through the use of air or cooling water. The temperature of the effluent stream generally is lowered by heat exchange sufficiently to effect the condensation of substantially all of the feed and product hydrocarbons having six or more carbon atoms per molecule. The resultant mixed-phase stream is passed into a vapor-liquid separator wherein the two phases are separated and from which the hydrogen-rich vapor is recycled to the reaction zone. The condensate from the separator is passed into a stripping column in which substantially all C 5  and lighter hydrocarbons present in the effluent are concentrated into an overhead stream and removed from the process. An aromatics-rich stream which is referred to herein as the disproportionation effluent stream is recovered as net stripper bottoms. 
     Conditions employed in the disproportionation process zone normally include a temperature of from about 200° to 600° C., and preferably from about 350° C. to about 575° C. The temperature required to maintain the desired degree of conversion will increase as the catalyst gradually loses activity during processing. Normal end-of-run temperatures may therefore exceed start-of-run temperatures by 65° C. or more. 
     The disproportionation zone is generally operated at hydrogen to hydrocarbon ranges about 0.2 to about 0.5. The ratio of hydrogen to hydrocarbon is calculated based on the molar ratio of free hydrogen compared against the feedstock hydrocarbon. Periodic increases in hydrogen to hydrocarbon above 0.5, and preferably in the range of 1 to 5 permit catalyst rejuvenation by hydrogenation of soft coke. 
     The disproportionation zone is operated at moderately elevated pressures broadly ranging from about 100 kPa to 6 MPa absolute. A preferred pressure range is from 2 to 3.5 MPa. The disproportionation reaction can be effected over a wide range of space velocities, with higher space velocities effecting a higher ratio of paraxylene at the expense of conversion. Liquid hourly space velocity generally is in the range of from about 0.2 to 20 hr −1 . 
     The disproportionation effluent stream is separated into a light recycle stream, a paraxylene-rich mixed-C 8 -aromatics product and a heavy-aromatics stream. The paraxylene-rich product may be sent to a xylene separation zone for recovery of pure paraxylene; optionally, other xylenes and ethylbenzene also may be recovered as pure products. The paraxylene-rich stream preferably contains paraxylene in proportion to total xylenes in excess of its equilibrium concentration at disproportionation conditions, more preferably at least 80 mass-% paraxylene, and most preferably at least about 85 mass-% paraxylene. The light recycle stream may be diverted to other uses such as to benzene and toluene recovery, but optionally a portion is recycled since it contains not only benzene and toluene but also amounts of non-aromatics which would remain with the benzene and reduce its commercial value. The heavy recycle stream contains substantially all of the C 9  and heavier aromatics and may be either withdrawn as a product of the process or partially or totally recycled to the feedstock. 
     The xylene-separation zone may utilize one or more different separation techniques such as fractionation, crystallization or selective adsorption to recover pure paraxylene from the paraxylene-rich stream in the xylene-separation zone. Conventional crystallization is disclosed in U.S. Pat. No. 3,177,255 B1, U.S. Pat. No. 3,467,724 B1 and U.S. Pat. No. 3,662,013 B1. Various other crystallization alternatives are discussed in U.S. Pat. No. 5,329,061 B1, incorporated by reference. In an embodiment in which the paraxylene-rich product has a paraxylene content substantially in excess of the equilibrium concentration, recovery of pure paraxylene may be effected using only a single stage of crystallization corresponding to the higher-temperature purification stage of conventional crystallization. 
     An alternative separation zone comprises a bed of molecular sieves operated in accordance with the teaching of U.S. Pat. No. 3,201,491 B1 to simulate the use of a continuously moving bed of molecular sieves. Subsequent improvements to the process are described in U.S. Pat. No. 3,696,107 B1 and U.S. Pat. No. 3,626,020 B1. Details on the operation of the xylene-separation zone may be obtained from U.S. Pat. No. 4,039,599 B1 and U.S. Pat. No. 4,184,943. The xylene-separation zone may also incorporate a catalytic alkyl-aromatic isomerization zone within the separation loop, in order to shift the isomers of ortho- and meta-xylene towards para-xylene, as well as to isomerize ethyl benzene to xylene or else to dealkylate it to benzene. The benzene produced here may also be sent to the transalkylation zone. The xylene separation zone may also employ a simulated concurrent adsorptive separation process of U.S. Pat. No. 4,402,832 B1. The extract and raffinate streams may be handled as described in these references or as described in U.S. Pat. Nos. 4,381,410 and 5,495,061 B1. 
     The skilled routineer will recognize variations in the process combination described above which are within the scope of the invention. For example, benzene as well as toluene may be charged to the disproportionation zone as a supplementary feedstock. The xylene-separation zone may use one or more of several known separation techniques such as adsorption, crystallization and fractionation. Orthoxylene and/or metaxylene may be recovered by one or more of such techniques as pure products from the xylene-separation zone. 
     The catalyst may be subjected to precoking either in-situ or ex-situ in order to increase the proportion of paraxylene in the C 8  aromatics product. 
     The process of disproportionation may be carried out until the catalyst conversion is no longer economically favorable due to catalyst decline, deterioration, or deactivation. A typical economic target occurs when the initial conversion of the catalyst has decreased by 2% or greater, at which point the catalyst is rejuvenated by increasing the molar ratio of free hydrogen to feedstock hydrocarbons to greater than 0.5. Preferred rejuvenation conditions include free hydrogen present in a molar ratio to feedstock hydrocarbons of about 1 to about 5, an inlet temperature from about 200 to about 600° C., a pressure of from about 100 kPa to about 6 MPa absolute, and a liquid hourly space velocity of about 0.2 to about 10 hr −1 . Moreover, the optimum initial conversion level for low levels of hydrogen to hydrocarbon ratio such as 0.2, may vary from about 26% to about 36%, more preferably from about 30% to about 34%. 
     EXAMPLES 
     The following examples are presented to demonstrate the present invention and to illustrate certain specific embodiments thereof. These examples should not be construed to limit the scope of the invention as set forth in the claims. There are many possible other variations, as those of ordinary skill in the art will recognize, which are with the spirit of the invention. 
     Example I 
     An alumina-phosphate-bound MFI catalyst was prepared to evaluate the invention. A first solution was prepared by adding phosphoric acid to an aqueous solution of hexamethylenetetraamine (HMT) in an amount to yield a phosphorus content of the finished catalyst equal to about 3.8 mass-% and an aluminum: phosphorus atomic ratio in the binder of about 1:1. A second solution was prepared by adding an MFI-type zeolite having a Si/Al 2  ratio of about 39 to enough alumina sol, prepared by digesting metallic aluminum in hydrochloric acid, to yield a zeolite content in the finished catalyst equal to about 70 mass-%. These two solutions were commingled to achieve a homogeneous admixture of HMT, phosphorus, alumina sol, and zeolite. The admixture was dispersed as droplets into an oil bath maintained at about 93° C. The droplets remained in the oil bath until they set and formed hydrogel spheres having a diameter of about 1.6 mm. The spheres were removed from the oil bath, water washed, air dried, and calcined at a temperature of about 650° C. This disproportionation catalyst was utilized in the precoking and disproportionation tests described hereinafter. 
     Example II 
     The catalyst was then precoked at conditions comprising a temperature of about 560° C., a pressure of 0.72 MPa and 4 weight hourly space velocity (WHSV) in the presence of a 1:0.5 hydrogen:hydrocarbon molar ratio for a period of time sufficient to effect approximately 90 mole-% paraxylene in total xylenes. Disproportionation of pure toluene then was carried out at 2.45 MPa and 4 WHSV in the presence of pure hydrogen at varying temperatures as red to achieve 30% conversion of toluene. Data-points were recorded at hydrogen to hydrocarbon ratios 3.0, 2.0, 1.0, 0.5 and 0.2 in order to illustrate the ion. Results then were normalized based on pilot-plant correlations to de comparative yields of benzene and xylenes in the product at 30% conversion. FIG. 1 indicates the increased para-xylene yield obtained with disportionation at ratios of hydrogen to hydrocarbon below 0.5.