Abstract:
A material for a base tube of a fuel battery, comprising a mixture of at least two components selected from the group consisting CaO, ZrO 2 , NiO, MgO, SrO, Al2O3, TiO2, and BaO. Such material suppresses cracks of an electrolyte and also suppress leakage after rapid temperature increase and decrease, thus providing a reliable fuel battery.

Description:
This is a division of Application Ser. No. 09/186,134 filed Nov. 4, 1998, now U.S. Pat. No.6,207,314. 
     This invention relates to a base material for a fuel battery. 
    
    
     FIELD OF THE INVENTION 
     BACKGROUND OF THE INVENTION 
     An example of a conventionally used technique is shown in FIG. 1. A base tube (base material portion)  1  according to prior art comprises a porous tube composed of 30.0 wt. % of CaO and 70.0 wt. % of ZrO 2 . On the surface of the base tube (base material portion)  1 , there are laminated a 100 μm thick fuel electrode-side electrode  2  comprising Ni-zirconia thermit, a 100 μm thick electrolyte  3  comprising yttrium-stabilized zirconia (“YSZ”), and a 100 μm thick air-side electrode  4  comprising LaMnO 3  doped with Sr in a proportion of 0.1. Further, a conductive connecting material  5  comprising LaCrO 3  is laminated for connecting the fuel electrode-side electrode  2  with the air-side electrode  4  to form a solid oxide fuel cell (“SOFC”); hereinafter referred to as “a fuel cell”; multiple fuel cells are connected to form a device hereinafter referred to as a “fuel battery”. 
     However, the base tube according to the earlier technology poses the problem of degrading markedly at a fast temperature raising and lowering rates during a heat cycle. In detail, with a temperature raising and lowering rate of not higher than 50° C./hour, the performance of the cell after the heat cycle does not differ from its performance before the heat cycle. At a temperature raising and lowering rate in excess of 50° C./hour, on the other hand, an output drop of about 10% may occur per heat cycle. When fuel cells are used as a gathering, a temperature raising and lowering rate, if not made very slow, exceeds 50° C./hour in a part of the fuel cell gathering, thereby damaging the cell. Thus, there is a demand for a cell which is not damaged even at a high temperature raising and lowering rate of about 200° C./hour. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     FIG. 1 is a sectional view of a base tube of a solid electrolyte fuel battery. 
    
    
     SUMMARY OF THE INVENTION 
     In order to meet such demand for a fuel cell, the material for constructing the porous base tube of the fuel cell has been changed from the prior art material comprising 30.0 wt. % CaO and 70.0 wt. % ZrO 2 . 
     It has been found that porous base tubes comprised of the materials described below will permit the fuel cell to operate at heat cycles entailing rapid rates of temperature increase and decrease without any significant reduction in output. 
     DETAILS OF THE INVENTION 
     In its broadest sense, the material employed for the porous base tube of a fuel battery comprising a mixture of at least two components selected from the group consisting of CaO, ZrO 2 , NiO, MgO, SrO, Al 2 O 3 , TiO 2  and BaO. 
     A first aspect of the invention based on the above finding is a material for a base tube of a fuel battery, comprising a three-component mixture composed of CaO≦26.1 wt. %, ZrO 2 ≦60.9 wt. % and 13.0 wt. %≦NiO. 
     A second aspect of the invention is the material for a base tube of a fuel battery of the first aspect, wherein the NiO is present in the form of particles having a particle size of 5 μm or less. 
     A third aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of CaO≦27.2 wt. %, ZrO 2 ≦63.6 wt. % and 9.2 wt. %≦MgO. 
     A fourth aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of CaO≦27.4 wt. %, ZrO 2 ≦63.9 wt. % and 8.7 wt. %≦SrO. 
     A fifth aspect of the invention is a material for a base tube of a fuel battery, comprising a two-component mixture composed of 47.9 wt. %≦MgO and Al 2 O 3 ≦52.1 wt. %. 
     A sixth aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of 22.8 wt. %≦CaO, MgO≦21.9 wt. % and Al 2 O 3 ≦55.3 wt. %. 
     A seventh aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of MgO≦20.9 wt. %, 26.3 wt. %≦SrO and Al 2 O 3 ≦52.8 wt. %. 
     An eighth aspect of the invention is a material for a base tube of a fuel battery, comprising a four-component mixture composed of 17.7 wt. %≦CaO, MgO≦16.2 wt. %, Al 2 O 3 ≦40.9 wt. % and 25.2 wt. %≦TiO 2 . 
     A ninth aspect of the invention is a material for a base tube of a fuel battery, comprising a four-component mixture composed of MgO≦13.3 wt. %, 30.1 wt. %≦SrO, Al 2 O 3 ≦33.4 wt. % and 23.2 wt. %≦TiO 2 . 
     A tenth aspect of the invention is a material for a base tube of a fuel battery, comprising a four-component mixture composed of MgO≦14.2 wt. %, Al 2 O 3 23 36.2 wt. %, 17.0 wt. %≦TiO 2  and 32.6 wt. %≦BaO. 
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     (1) The first aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of CaO≦26.1 wt. %, ZrO 2 ≦60.9 wt. % and 13.0 wt. %≦NiO. 
     Preferably, as shown in Examples to be offered later on, the three-component mixture is selected from the ranges 26.1 wt. %≦CaO≧9.1 wt. %, 60.9 wt. %≧ZrO 2 ≧20.9 wt. %, and 13.0 wt. %≦NiO≦70.0 wt. %, more preferably, the ranges 21.0 wt. %≧CaO≧9.1 wt. %, 49.0 wt. %≧ZrO 2 ≧20.9 wt. %, and 30.0 wt. %≦NiO≦70.0 wt. %, and most preferably, the ranges 14.9 wt. %≧CaO≧9.1 wt. %, 34.8 wt. %≧ZrO 2 ≧20.9 wt. %, and 50.3 wt. %≦NiO≦70.0 wt. %. If the three-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be changed to a rapid rate. With a higher content of the Ni component, electrical conductivity occurs, and performance of a fuel battery is not obtained. Here, the change in the temperature raising and lowering rate to a rapid rate refers to a change to a temperature raising and lowering rate exceeding 50° C./hour (the same will hold true hereinbelow). 
     (2) The second aspect of the invention is the constitution of the first aspect, wherein the NiO is present in the form of particles having a particle size of 5 μm or less. If the particle size of NiO exceeds 5 μm, the amount of steam added when natural gas is used as a fuel cannot be decreased. This is not preferred for improvement of efficiency. 
     (3) The third aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of CaO≦27.2 wt. %, ZrO 2 ≦63.6 wt. % and 9.2 wt. %≦MgO. 
     Preferably, as shown in the Examples to be offered later on, the three-component mixture is selected from the ranges 27.2 wt. %≧CaO≧0.5 wt. %, 63.6 wt. %≧ZrO 2 ≧0.5 wt. %, and 9.2 wt. %≦MgO≦99 wt. %, more preferably, the ranges 22.9 wt. %≧CaO≧0.5 wt. %, 53.5 wt. %≧ZrO 2 ≧0.5 wt. %, and 23.6 wt. %≦MgO≦99 wt. %, and most preferably, the ranges 16.2 wt. %≧CaO≧0.5 wt. %, 37.9 wt. %≧ZrO 2 ≧0.5 wt. %, and 43.9 wt. %≦MgO≦99 wt. %. If the three-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. 
     (4) The fourth aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of CaO≦27.4 wt. %, ZrO 2 ≦63.9 wt. % and 8.7 wt. %≦SrO. 
     Preferably, as shown in the Examples to be offered later on, the three-component mixture is selected from the ranges 27.4 wt. %≧CaO≧0.5 wt. %, 63.9 wt. %≧ZrO 2 ≧0.5 wt. %, and 8.7 wt. %≦SrO≦99 wt. %, more preferably, the ranges 23.6 wt. %≧CaO≧0.5 wt. %, 55.1 wt. %≧ZrO 2 ≧0.5 wt. %, and 21.3 wt. %≦SrO≦99 wt. %, and most preferably, the ranges 18.6 wt. %≧CaO≧0.5 wt. %, 43.4 wt. %≧ZrO 2 ≧0.5 wt. %, and 38.0 wt. %≦SrO≦99 wt. %. If the three-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     (5) The fifth aspect of the invention is a material for a base tube of a fuel battery, comprising a two-component mixture composed of 47.9 wt. %≦MgO and Al 2 O 3 ≦52.1 wt. %. 
     Preferably, as shown in the Examples to be offered later on, the two-component mixture is selected from the ranges 47.9 wt. %≦MgO≦99.5 wt. % and 52.1 wt. %≧Al 2 O 3 ≧0.5 wt. %, more preferably, the ranges 59.3 wt. %≦MgO≦99.5 wt. % and 40.7 wt. %≧Al 2 O 3 ≧0.5 wt. %, most preferably, the ranges 73.9 wt. %≦MgO≦99.5 wt. % and 26.1 wt. %≧Al 2 O 3 ≧0.5 wt. %. If the two-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     (6) The sixth aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of 22.8 wt. %≦CaO, MgO≦21.9 wt. % and Al 2 O 3 ≦55.3 wt. %. 
     Preferably, the three-component mixture is selected from the ranges 22.8 wt. %≦CaO≦99.0 wt. %, 21.9 wt. %≧MgO≧0.5 wt. %, and 55.3 wt. %≧Al 2 O 3 ≧0.5 wt. %, more preferably, the ranges 36.5 wt. %≦CaO≦99.0 wt. %, 18.0 wt. %≧MgO≧0.5 wt. %, and 45.5 wt. %≧Al 2 O 3 ≧0.5 wt. %, and most preferably, the ranges 54.4 wt. %≦CaO≦99.0 wt. %, 12.9 wt. %≧MgO≧0.5 wt. %, and 32.7 wt. %≧Al 2 O 3 ≧0.5 wt. %. If the three-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     (7) The seventh aspect of the invention is a material for a base tube of a fuel battery, comprising a three-component mixture composed of MgO≦20.9 wt. %, 26.3 wt. %≦SrO and Al 2 O 3 ≦52.8 wt. %. 
     Preferably, the three-component mixture is selected from the ranges 20.9 wt. %≧MgO≧0.5 wt. %, 26.3 wt. %≦SrO≦99.0 wt. %, and 52.8 wt. %≧Al 2 O 3 ≧0.5 wt. %, more preferably, the ranges 17.0 wt. %≧MgO≧0.5 wt. %, 39.9 wt. %≦SrO≦99.0 wt. %, and 43.1 wt. %≧Al 2 O 3 ≧0.5 wt. %, and most preferably, the ranges 12.5 wt. %≧MgO≧0.5 wt. %, 55.8 wt. %≦SrO≦99.0 wt. %, and 31.7 wt. %≧Al 2 O 3 ≧0.5 wt. %. If the three-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     (8) The eighth aspect of the invention is a material for a base tube of a fuel battery, comprising a four-component mixture composed of 17.7 wt. %≦CaO, MgO≦16.2 wt. %, Al 2 O 3 ≦40.9 wt. % and 25.2 wt. %≦TiO 2 . 
     Preferably, the four-component mixture is selected from the ranges 17.7 wt. %≦CaO≦40.8 wt. %, 16.2 wt. %≧MgO≧0.5 wt. %, 40.9 wt. %≧Al 2 O 3 ≧0.5 wt. % and 25.2 wt. %≦TiO 2 ≦58.2 wt. %, more preferably, the ranges 27.3 wt. %≦CaO≦40.8 wt. %, 9.6 wt. %≧MgO≧0.5 wt. %, 24.3 wt. %≧Al 2 O 3 ≧0.5 wt. % and 38.8 wt. %≦TiO 2 ≦58.2 wt. %, and most preferably, the ranges 38.8 wt. %≦CaO≦40.8 wt. %, 1.6 wt. %≧MgO≧0.5 wt. %, 4.3 wt. %≧Al 2 O 3 ≧0.5 wt. % and 55.3 wt. %≦TiO 2 ≦58.2 wt. %. If the four-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     (9) The ninth aspect of the invention is a material for a base tube of a fuel battery, comprising a four-component mixture composed of MgO≦13.3 wt. %, 30.1 wt. %≦SrO, Al 2 O 3 ≦33.4 wt. % and 23.2 wt. %≦TiO 2 . 
     Preferably, the four-component mixture is selected from the ranges 13.3 wt. %≧MgO≧0.5 wt. %, 30.1 wt. %≦SrO≦55.9 wt. %, 33.4 wt. %≧Al 2 O 3 ≧0.5 wt. % and 23.2 wt. %≦TiO 2 ≦43.1 wt. %, more preferably, the ranges 6.5 wt. %≧MgO≧0.5 wt. %, 43.6 wt. %≦SrO≦55.9 wt. %, 16.3 wt. %≧Al 2 O 3 ≧0.5 wt. % and 33.6 wt. %≦TiO 2 ≦43.1 wt. %. If the four-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     (10) The tenth aspect of the invention is a material for a base tube of a fuel battery, comprising a four-component mixture composed of MgO≦14.2 wt. %, Al 2 O 3 ≦36.2 wt. %, 17.0 wt. %≦TiO 2  and 32.6 wt. %≦BaO. 
     Preferably, the four-component mixture is selected from the ranges 14.2 wt. %≧MgO≧0.5 wt. %, 36.2 wt. %≧Al 2 O 3 ≧0.5 wt. %, 17.0 wt. %≦TiO 2 ≦65.8 wt. % and 32.6 wt. %≦BaO≦33.2 wt. %, more preferably, the ranges 8.3 wt. %≧MgO≧0.5 wt. %, 21.1 wt. %≧Al 2 O 3 ≧0.5 wt. %, 24.2 wt. %≦TiO 2 ≦65.8 wt. % and 46.4 wt. %≧BaO≧33.2 wt. %, and most preferably, the ranges 2.2 wt. %≧MgO≧0.5 wt. %, 5.8 wt. %≧Al 2 O 3 ≧0.5 wt. %, 31.5 wt. %≦TiO 2 ≦65.8 wt. % and 60.5 wt. %≧BaO≧33.2 wt. %. If the four-component mixture exceeds these ranges, the temperature raising and lowering rate cannot be made rapid. Increased purity also leads to a higher cost, making production of an inexpensive fuel battery impossible. 
     The present invention will be described in detail with reference to Examples, which in no way limit the invention. 
     EXAMPLE 1 
     A Base Tube Comprising a Composite Material Having a CaO—ZrO 2 —NiO Three-component Mixture 
     EXAMPLE 1-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (1) indicated in Table 1. 
     On the surface of the base tube  1 , there were laminated a 100 μm thick fuel electrode-side electrode  2  comprising Ni-zirconia thermit, a 100 μm thick electrolyte  3  comprising YSZ, and a 100 μm thick air-side electrode  4  comprising LaMnO 3  doped with Sr in a proportion of 0.1. Further, a conductive connecting material  5  comprising LaCrO 3  was laminated for connecting the fuel electrode-side electrode  2  with the air-side electrode  4  to form a fuel cell, and the fuel cells were connected together to make a fuel battery. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 1. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     In this Example, the repetition of rapid temperature raising and lowering refers concretely to raising and lowering the temperature repeatedly from room temperature to 1,000° C. and vice versa at a rate of 200° C./hour (the same will hold true for the following Examples). 
     The results given in Table 1 show that the composition (1) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 
                   
               
               
                   
                   
                 cycle of rapid 
                 Leak after 15 cycles 
               
               
                   
                   
                 temperature rais- 
                 of rapid temperature 
               
               
                   
                 Base tube 
                 ing and lowering 
                 raising and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 26.1 wt. % 
                 3% 
                  3% 
               
               
                 (1) 
                 ZrO 2 : 60.9 wt. % 
               
               
                   
                 NiO: 13.0 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 1-1 
     The composition of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, can reduce the leak after temperature raising and lowering, and can thus provide a reliable fuel battery. 
     As noted above, this composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 1-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (2) indicated in Table 2. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 . Potentials obtained during the test were compared. The results are shown in Table 2. A fuel battery having the aforementioned base tube composition (1) was used as a reference. 
     The results given in Table 2 show that the composition (2) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (1). 
     
       
         
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 26.1 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                 0.7 
                 V 
               
               
                 (1) 
                 ZrO 2 : 60.9 wt. % 
               
               
                   
                 NiO: 13.0 wt. % 
               
               
                 Composition 
                 CaO: 21.0 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.75 
                 V 
               
               
                 (2) 
                 ZrO 2 : 49.0 wt. % 
               
               
                   
                 NiO: 30.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 1-2 
     The composition (2) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (1). 
     In addition to exhibiting the effects of the composition (1), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.05 V. 
     EXAMPLE 1-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (3) indicated in Table 3. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     A comparison of the cost of the base tube was made. The results are shown in Table 3. A fuel battery having the aforementioned base tube composition (2) was used as a reference for the relative value of the cost of the base tube. 
     The results given in Table 3 show that the composition (3) of the invention not only has the characteristics of the composition (2), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 3 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 CaO: 21.0 wt. % 
                 100 
               
               
                   
                 (2) 
                 ZrO 2 : 49.0 wt. % 
               
               
                   
                   
                 NiO: 30.0 wt. % 
               
               
                   
                 Composition 
                 CaO: 14.9 wt. % 
                 80 
               
               
                   
                 (3) 
                 ZrO 2 : 34.8 wt. % 
               
               
                   
                   
                 NiO: 50.3 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 1-3 
     The composition (3) of the invention not only has the actions of the composition (2), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the base tube materials, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (2), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 2 
     A Base Tube Comprising a Composite Material Having a CaO—ZrO 2 —NiO Three-component Mixture (Particle Size of NiO: 5 μm or Less.) 
     EXAMPLE 2-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (4) indicated in Table 4. Composition (4) was similar to composition(1) in its content, except that the NiO employed in composition(4) consisted of particles having a maximum particle size of 5 μm. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then its leaks before and after this test were compared. Fuel compositions capable of power generation using natural gas as a fuel were also compared. 
     The results are shown in Table 4. A fuel battery having the aforementioned base tube composition (1) (particle diameter: 10 μm), and a fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology were used as controls. 
     The results given in Table 4 show that the composition (4) causes no changes in the leak after rapid temperature raising and lowering, and can reduce the amount of steam added (S/C=steam/carbon) during use of natural gas. 
     
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 4 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 
                 Leak after 
                 Fuel 
               
               
                   
                   
                 cycle of 
                 15 cycles of 
                 compo- 
               
               
                   
                   
                 rapid 
                 rapid 
                 sition 
               
               
                   
                   
                 temperature 
                 temperature 
                 capable of 
               
               
                   
                   
                 raising and 
                 raising and 
                 power 
               
               
                   
                 Base tube 
                 lowering 
                 lowering 
                 generation 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 26.1 wt. % 
                 3% 
                 3% 
                 S/C = 1.5 
               
               
                 (4) 
                 ZrO 2 : 60.9 wt. % 
               
               
                   
                 NiO: 13.0 wt. % 
               
               
                   
                 NiO particle 
               
               
                   
                 size: 5 μm 
               
               
                 Composition 
                 CaO: 26.1 wt. % 
                 3% 
                 3% 
                 S/C = 2.0 
               
               
                 (1) 
                 ZrO 2 : 60.9 wt. % 
               
               
                   
                 NiO: 13.0 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28%  
                 S/C = 2.0 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 2-1 
     The composition of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. It can also decrease the amount of steam added when natural gas is used as a fuel. 
     As noted above, the composition (4) can suppress the increase of the leak after rapid temperature raising and lowering. It can also decrease the amount of steam added when natural gas is used as a fuel. 
     EXAMPLE 2-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (5) indicated in Table 5. 
     On the surface of the base tube  1 , there were laminated a 100 μm thick fuel electrode-side electrode  2  comprising Ni-zirconia thermit, a 100 μm thick electrolyte  3  comprising YSZ, and a 100 μm thick air-side electrode  4  comprising LaMnO 3  doped with Sr in a proportion of 0.4. Further, a conductive connecting material  5  comprising LaCrO 3  was laminated for connecting the fuel electrode-side electrode  2  with the air-side electrode  4  to form a fuel cell, and the fuel cells were connected together to make a fuel battery. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 . Potentials obtained during the test were compared. Fuel compositions capable of power generation using natural gas as a fuel were also compared. 
     The results are shown in Table 5. A fuel battery having the aforementioned base tube composition (4) was used as a reference. 
     The results given in Table 5 show that the composition (5) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the mean potential, in addition to having the characteristics of the composition (4). 
     
       
         
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                   
                 TABLE 5 
               
               
                   
                   
               
               
                   
                   
                   
                   
                 Fuel 
               
               
                   
                   
                   
                 Mean 
                 compo- 
               
               
                   
                   
                   
                 potential 
                 sition 
               
               
                   
                   
                 Material for 
                 obtained 
                 capable of 
               
               
                   
                   
                 air-side 
                 (at 200 
                 power 
               
               
                   
                 Base tube 
                 electrode 
                 mA/cm 2 ) 
                 generation 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 26.1 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                 0.7 
                 V 
                 S/C = 1.5 
               
               
                 (4) 
                 ZrO 2 : 60.9 wt. % 
               
               
                   
                 NiO: 13.0 wt. % 
               
               
                   
                 NiO particle 
               
               
                   
                 size: 5 μm or less 
               
               
                 Composition 
                 CaO: 21.0 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.75 
                 V 
                 S/C = 1.5 
               
               
                 (5) 
                 ZrO 2 : 49.0 wt. % 
               
               
                   
                 NiO: 30.0 wt. % 
               
               
                   
                 NiO particle 
               
               
                   
                 size: 5 μm or less 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 2-2 
     The composition (5) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (4). 
     In addition to exhibiting the effects of the composition (4), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the mean potential. 
     EXAMPLE 2-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (6) indicated in Table 6. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The costs of the base tube were compared. The results are shown in Table 6. A fuel battery having the aforementioned base tube composition (5) was used as a reference for the relative value of the cost of the base tube. 
     The results given in Table 6 show that the composition (6) of the invention not only has the characteristics of the composition (5), but can reduce the cost of the base tube. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 6 
               
               
                   
                   
               
               
                   
                   
                   
                 Fuel composition 
               
               
                   
                   
                 Cost of base tube 
                 capable of power 
               
               
                   
                 Base tube 
                 (relative value) 
                 generation 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 21.0 wt. % 
                 100 
                 S/C = 1.5 
               
               
                 (5) 
                 ZrO 2 : 49.0 wt. % 
               
               
                   
                 NiO: 30.0 wt. % 
               
               
                   
                 NiO particle 
               
               
                   
                 size: 5 μm or less 
               
               
                 Composition 
                 CaO: 14.9 wt. % 
                 80 
                 S/C = 1.5 
               
               
                 (6) 
                 ZrO 2 : 50.3 wt. % 
               
               
                   
                 NiO particle 
               
               
                   
                 size: 5 μm or less 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 2-3 
     The composition (6) of the invention not only has the actions of the composition (5), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (5), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 3 
     A Base Tube Comprising a Composite Material Having a CaO—ZrO 2 —MgO Three-component Mixture 
     EXAMPLE 3-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (7) indicated in Table 7. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 7. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 7 show that the composition (7) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 7 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                   
               
               
                   
                   
                 of rapid 
                 Leak after 15 cycles 
               
               
                   
                   
                 temperature rais- 
                 of rapid temperature 
               
               
                   
                 Base tube 
                 ing and lowering 
                 raising and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 27.2 wt. % 
                 2% 
                  2% 
               
               
                 (7) 
                 ZrO 2 : 63.6 wt. % 
               
               
                   
                 MgO: 9.2 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 3-1 
     The composition (7) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     As noted above, this composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 3-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (8) indicated in Table 8. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 8. A fuel battery having the aforementioned composition (7) was used as a reference. 
     The results given in Table 8 show that the composition (8) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (7). 
     
       
         
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 8 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 27.2 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                 0.7 
                 V 
               
               
                 (7) 
                 ZrO 2 : 63.6 wt. % 
               
               
                   
                 MgO: 9.2 wt. % 
               
               
                 Composition 
                 CaO: 22.9 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.74 
                 V 
               
               
                 (6) 
                 ZrO 2 : 53.5 wt. % 
               
               
                   
                 MgO: 23.6 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 3-2 
     The composition (8) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (7). 
     In addition to exhibiting the effects of the composition (7), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.04 V. 
     EXAMPLE 3-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (9) indicated in Table 9. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (8), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 9. 
     The results given in Table 9 show that the composition (9) of the invention not only has the characteristics of the composition (8), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 9 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 CaO: 22.9 wt. % 
                 100 
               
               
                   
                 (8) 
                 ZrO 2 : 53.5 wt. % 
               
               
                   
                   
                 MgO: 23.6 wt. % 
               
               
                   
                 Composition 
                 CaO: 16.2 wt. % 
                 60 
               
               
                   
                 (9) 
                 ZrO 2 : 37.9 wt. % 
               
               
                   
                   
                 MgO: 45.9 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 3-3 
     The composition (9) of the invention not only has the actions of the composition (8), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (8), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 4 
     A Base Tube Comprising a Composite Material Having a CaO—ZrO 2 —SrO Three-component Mixture 
     EXAMPLE 4-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (10) indicated in Table 10. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 10. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 10 show that the composition (10) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 10 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid 
                 cycles of rapid 
               
               
                   
                   
                 temperature 
                 temperature 
               
               
                   
                   
                 raising and 
                 raising and 
               
               
                   
                 Base tube 
                 lowering 
                 lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 27.4 wt. % 
                 3% 
                  3% 
               
               
                 (10) 
                 ZrO 2 : 63.9 wt. % 
               
               
                   
                 SrO: 8.7 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 4-1 
     The composition (10) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, and suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 4-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (11) indicated in Table 11. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 11. A fuel battery having the aforementioned base tube composition (10) was used as a reference. 
     The results given in Table 11 show that the composition (11) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (10). 
     
       
         
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 11 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 CaO: 27.4 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                 0.7 
                 V 
               
               
                 (10) 
                 ZrO 2 : 63.9 wt. % 
               
               
                   
                 SrO: 8.7 wt. % 
               
               
                 Composition 
                 CaO: 23.6 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.74 
                 V 
               
               
                 (11) 
                 ZrO 2 : 55.1 wt. % 
               
               
                   
                 SrO: 21.3 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 4-2 
     The composition (11) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (10). 
     In addition to exhibiting the effects of the composition (10), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.04 V. 
     EXAMPLE 4-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (12) indicated in Table 12. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (11), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 12. 
     The results given in Table 12 show that the composition (12) of the invention not only has the characteristics of the composition (11), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 12 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 CaO: 23.6 wt. % 
                 100 
               
               
                   
                 (11) 
                 ZrO 2 : 55.1 wt. % 
               
               
                   
                   
                 SrO: 21.3 wt. % 
               
               
                   
                 Composition 
                 CaO: 18.6 wt. % 
                 75 
               
               
                   
                 (12) 
                 ZrO 2 : 43.4 wt. % 
               
               
                   
                   
                 SrO: 38.O wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 4-3 
     The composition (12) of the invention not only has the actions of the composition (11), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (11), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 5 
     A Base Tube Comprising a Composite Material Having an Al 2 O 3 —MgO Two-component Mixture 
     EXAMPLE 5-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (13) indicated in Table 13. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 13. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 13 show that the composition (13) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 13 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid temp- 
                 cycles of rapid 
               
               
                   
                   
                 erature raising 
                 temperature rais- 
               
               
                   
                 Base tube 
                 and lowering 
                 ing and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 Al 2 O 3 : 52.1 wt. % 
                 3% 
                  3% 
               
               
                 (13) 
                 MgO: 47.9 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 5-1 
     The composition (13) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     As noted above, this composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 5-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (14) indicated in Table 14. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/Cm 2 , and potentials obtained during the test were compared. The results are shown in Table 14. A fuel battery having the aforementioned base tube composition (13) was used as a reference. 
     The results given in Table 14 show that the composition (14) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (13). 
     
       
         
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 14 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 Al 2 O 3 : 52.1 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                 0.7 
                 V 
               
               
                 (13) 
                 MgO: 47.9 wt. % 
               
               
                 Composition 
                 Al 2 O 3 : 40.7 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.75 
                 V 
               
               
                 (14) 
                 MgO: 59.3 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 5-2 
     The composition (14) of the invention can broaden the range of selection of the material for the air-side electrode in addition to having the actions of the composition (13), increase the potential, and contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (13), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.05 V. 
     EXAMPLE 5-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (15) indicated in Table 15. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (14), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 15. 
     The results given in Table 15 show that the composition (15) of the invention not only has the characteristics of the composition (14), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 15 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 Al 2 O 3 : 40.7 wt. % 
                 100 
               
               
                   
                 (14) 
                 MgO: 59.3 wt. % 
               
               
                   
                 Composition 
                 Al 2 O 3 : 26.1 wt. % 
                 80 
               
               
                   
                 (15) 
                 MgO: 73.9 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 5-3 
     The composition (15) of the invention not only has the actions of the composition (14), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (14), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 6 
     A Base Tube Comprising a Composite Material Having an Al 2 O 3 —MgO—CaO Three-component Mixture 
     EXAMPLE 6-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (16) indicated in Table 16. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 16. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 16 show that the composition (16) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 16 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid tem- 
                 cycles of rapid 
               
               
                   
                   
                 perature raising 
                 temperature rais- 
               
               
                   
                 Base tube 
                 and lowering 
                 ing and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 Al 2 O 3 : 55.3 wt. % 
                 2% 
                  2% 
               
               
                 (16) 
                 MgO: 21.9 wt. % 
               
               
                   
                 CaO: 22.8 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 6-1 
     The composition (16) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     As noted above, this composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 6-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (17) indicated in Table 17. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 17. A fuel battery having the aforementioned base tube composition (16) was used as a reference. 
     The results given in Table 17 show that the composition (17) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (16). 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 17 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 Al 2 O 3 : 55.3 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                  0.7 V 
               
               
                 (16) 
                 MgO: 21.9 wt. % 
               
               
                   
                 CaO: 22.8 wt. % 
               
               
                 Composition 
                 Al 2 O 3 : 45.5 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.73 V 
               
               
                 (17) 
                 MgO: 18.0 wt. % 
               
               
                   
                 CaO: 36.5 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 6-2 
     The composition (17) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (16). 
     In addition to exhibiting the effects of the composition (16), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.03 V. 
     EXAMPLE 6-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (18) indicated in Table 18. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (17), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 18. 
     The results given in Table 18 show that the composition (18) of the invention not only has the characteristics of the composition (17), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 18 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 Al 2 O 3 : 45.5 wt. % 
                 100 
               
               
                   
                 (17) 
                 MgO: 18.0 wt. % 
               
               
                   
                   
                 CaO: 36.5 wt. % 
               
               
                   
                 Composition 
                 Al 2 O 3 : 32.7 wt. % 
                 85 
               
               
                   
                 (18) 
                 MgO: 12.9 wt. % 
               
               
                   
                   
                 CaO: 54.4 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 6-3 
     The composition (18) of the invention not only has the actions of the composition (17), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (17), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 7 
     A Base Tube Comprising a Composite Material Having an Al 2 O 3 —MgO—SrO Three-component Mixture 
     EXAMPLE 7-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (19) indicated in Table 19. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 19. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 19 show that the composition (19) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 19 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid tem- 
                 cycles of rapid 
               
               
                   
                   
                 perature raising 
                 temperature rais- 
               
               
                   
                 Base tube 
                 and lowering 
                 ing and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 Al 2 O 3 : 52.8 wt. % 
                 3% 
                  2% 
               
               
                 (19) 
                 MgO: 20.9 wt. % 
               
               
                   
                 SrO: 26.3 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 7-1 
     The composition (19) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     As noted above, this composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 7-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (20) indicated in Table 20. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 20. A fuel battery having the aforementioned base tube composition (19) was used as a reference. 
     The results given in Table 20 show that the composition (20) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (19). 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 20 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 Al 2 O 3 : 52.8 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                  0.7 V 
               
               
                 (16) 
                 MgO: 20.9 wt. % 
               
               
                   
                 CaO: 26.3 wt. % 
               
               
                 Composition 
                 Al 2 O 3 : 43.1 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.76 V 
               
               
                 (17) 
                 MgO: 17.0 wt. % 
               
               
                   
                 SrO: 39.9 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 7-2 
     The composition (20) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (19). 
     In addition to exhibiting the effects of the composition (19), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.06 V. 
     EXAMPLE 7-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (21) indicated in Table 21. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (20), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 21. 
     The results given in Table 21 show that the composition (21) of the invention not only has the characteristics of the composition (20), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 21 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 Al 2 O 3 : 43.1 wt. % 
                 100 
               
               
                   
                 (20) 
                 MgO: 17.0 wt. % 
               
               
                   
                   
                 SrO: 39.9 wt. % 
               
               
                   
                 Composition 
                 Al 2 O 3 : 31.7 wt. % 
                 85 
               
               
                   
                 (21) 
                 MgO: 12.5 wt. % 
               
               
                   
                   
                 SrO: 55.8 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 7-3 
     The composition (21) of the invention not only has the actions of the composition (20), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (20), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 8 
     A Base Tube Comprising a Composite Material Having an MgO—Al 2 O 3 —CaO—TiO 2  Four-component Mixture 
     EXAMPLE 8-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (22) indicated in Table 22. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 22. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 22 show that the composition (22) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 22 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid tem- 
                 cycles of rapid 
               
               
                   
                   
                 perature raising 
                 temperature rais- 
               
               
                   
                 Base tube 
                 and lowering 
                 ing and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 MgO: 16.2 wt. % 
                 2% 
                  2% 
               
               
                 (22) 
                 Al 2 O 3 : 40.9 wt. % 
               
               
                   
                 CaO: 17.7 wt. % 
               
               
                   
                 TiO 2 : 25.2 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 8-1 
     The composition (22) of the invention can suppress the increase of the leak after rapid temperature raising and lowering. 
     This composition can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     EXAMPLE 8-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (23) indicated in Table 23. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 23. A fuel battery having the aforementioned base tube composition (22) was used as a reference. 
     The results given in Table 23 show that the composition (23) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (22). 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 23 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 MgO: 40.9 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                  0.7 V 
               
               
                 (22) 
                 Al 2 O 3 : 16.2 wt. % 
               
               
                   
                 CaO: 17.7 wt. % 
               
               
                   
                 TiO 2 : 25.2 wt. % 
               
               
                 Composition 
                 MgO: 9.6 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.75 V 
               
               
                 (23) 
                 Al 2 O 3 : 24.3 wt. % 
               
               
                   
                 CaO: 27.3 wt. % 
               
               
                   
                 TiO 2 : 38.8 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 8-2 
     The composition (23) of the invention can broaden the range of selection of the material for the air-side electrode in addition to having the actions of the composition (22), increase the potential, and contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (22), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.05 V. 
     EXAMPLE 8-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (24) indicated in Table 24. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (23), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 24. 
     The results given in Table 24 show that the composition (24) of the invention not only has the characteristics of the composition (23), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 24 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 MgO: 9.6 wt. % 
                 100 
               
               
                   
                 (23) 
                 Al 2 O 3 : 24.3 wt. % 
               
               
                   
                   
                 CaO: 27.3 wt. % 
               
               
                   
                   
                 TiO 2 : 38.8 wt. % 
               
               
                   
                 Composition 
                 MgO: 1.6 wt. % 
                 85 
               
               
                   
                 (24) 
                 Al 2 O 3 : 4.3 wt. % 
               
               
                   
                   
                 CaO: 38.8 wt. % 
               
               
                   
                   
                 TiO 2 : 55.3 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 8-3 
     The composition (24) of the invention not only has the actions of the composition (23), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (23), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     EXAMPLE 9 
     A Base Tube Comprising a Composite Material Having an MgO—Al 2 O 3 —SrO—TiO 2  Four-component Mixture 
     EXAMPLE 9-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (25) indicated in Table 25. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 25. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 25 show that the composition (25) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 25 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid tem- 
                 cycles of rapid 
               
               
                   
                   
                 perature raising 
                 temperature rais- 
               
               
                   
                 Base tube 
                 and lowering 
                 ing and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 MgO: 13.3 wt. % 
                 3% 
                  1% 
               
               
                 (25) 
                 Al 2 O 3 : 33.4 wt. % 
               
               
                   
                 SrO: 30.1 wt. % 
               
               
                   
                 TiO 2 : 23.2 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 9-1 
     The composition (25) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     As noted above, this composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 9-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (26) indicated in Table 25. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 26. A fuel battery having the aforementioned base tube composition (25) was used as a reference. 
     The results given in Table 26 show that the composition (26) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (25) . 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 26 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 MgO: 13.3 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                  0.7 V 
               
               
                 (25) 
                 Al 2 O 3 : 33.4 wt. % 
               
               
                   
                 SrO: 30.1 wt. % 
               
               
                   
                 TiO 2 : 23.2 wt. % 
               
               
                 Composition 
                 Al 2 O 3 : 6.5 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.74 V 
               
               
                 (26) 
                 MgO: 16.3 wt. % 
               
               
                   
                 SrO: 43.6 wt. % 
               
               
                   
                 TiO 2 : 33.6 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 9-2 
     The composition (26) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (25). 
     In addition to exhibiting the effects of the composition (25), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.04 V. 
     EXAMPLE 10 
     A Base Tube Comprising a Composite Material Having an MgO—Al 2 O 3 —BaO—TiO 2  Four-component Mixture 
     EXAMPLE 10-1 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (27) indicated in Table 27. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The rapid temperature raising and lowering of the fuel battery was repeated, and then changes in its leak were compared. The results are shown in Table 27. A fuel battery having the base tube composition CaO:30.0 wt. %/ZrO 2 :70.0 wt. % according to the earlier technology was used as a control. 
     The results given in Table 27 show that the composition (27) can suppress the increase of the leak. 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 27 
               
               
                   
                   
               
               
                   
                   
                 Leak after 1 cycle 
                 Leak after 15 
               
               
                   
                   
                 of rapid tem- 
                 cycles of rapid 
               
               
                   
                   
                 perature raising 
                 temperature rais- 
               
               
                   
                 Base tube 
                 and lowering 
                 ing and lowering 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 MgO: 14.2 wt. % 
                 3% 
                  2% 
               
               
                 (27) 
                 Al 2 O 3 : 36.2 wt. % 
               
               
                   
                 BaO: 32.6 wt. % 
               
               
                   
                 TiO 2 : 17.0 wt. % 
               
               
                 Prior Art 
                 CaO: 30.0 wt. % 
                 3% 
                 28% 
               
               
                   
                 ZrO 2 : 70.0 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 10-1 
     The composition (27) of the invention can suppress cracks of an electrolyte during rapid raising and lowering of the temperature of a fuel battery, reduce the leak after temperature raising and lowering, and thus provide a reliable fuel battery. 
     This composition can suppress the increase of the leak after rapid temperature raising and lowering. 
     EXAMPLE 10-2 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (28) indicated in Table 28. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The fuel battery was subjected to a power generation test under the conditions 200 mA/cm 2 , and potentials obtained during the test were compared. The results are shown in Table 28. A fuel battery having the aforementioned composition (27) was used as a reference. 
     The results given in Table 28 show that the composition (28) of the invention can broaden the range of selection of the material for the air-side electrode, and improve the potential, in addition to having the characteristics of the composition (27). 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 28 
               
               
                   
                   
               
               
                   
                   
                 Material for 
                 Mean potential 
               
               
                   
                   
                 air-side 
                 obtained 
               
               
                   
                 Base tube 
                 electrode 
                 (at 200 mA/cm 2 ) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Composition 
                 MgO: 14.2 wt. % 
                 La 0.9 Sr 0.1 MnO 3   
                  0.7 V 
               
               
                 (27) 
                 Al 2 O 3 : 36.2 wt. % 
               
               
                   
                 BaO: 32.6 wt. % 
               
               
                   
                 TiO 2 : 17.0 wt. % 
               
               
                 Composition 
                 MgO: 8.3 wt. % 
                 La 0.6 Sr 0.4 MnO 3   
                 0.74 V 
               
               
                 (28) 
                 Al 2 O 3 : 21.1 wt. % 
               
               
                   
                 BaO: 46.4 wt. % 
               
               
                   
                 TiO 2 : 24.2 wt. % 
               
               
                   
               
             
          
         
       
     
     Actions and Effects of Example 10-2 
     The composition (28) of the invention can broaden the range of selection of the material for the air-side electrode, increase the potential, and contribute to a lowered cost, in addition to having the actions of the composition (27). 
     In addition to exhibiting the effects of the composition (27), this composition can widen the range of selection of the material for the air-side electrode, and decrease the resistance on the air-side electrode side, thus increasing the resulting mean potential by 0.04 V. 
     EXAMPLE 10-3 
     FIG. 1 shows an example in which a base tube (base material portion)  1  was formed from a porous tube comprising a composite material having a composition (29) indicated in Table 29. 
     On the surface of the base tube  1 , a fuel electrode-side electrode  2 , an electrolyte  3 , and an air-side electrode  4  were laminated, and a conductive connecting material  5  was further laminated. The compositions of these materials and the procedure used were the same as in Example 1-1. In this manner, a fuel battery was produced. 
     The cost of the base tube of the fuel battery was compared with that of a fuel battery having the aforementioned base tube composition (28), which was used as a reference for the relative value of the cost of the base tube. The results are shown in Table 29. 
     The results given in Table 29 show that the composition (29) of the invention not only has the characteristics of the composition (28), but can reduce the cost of the base tube. 
     
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 29 
               
               
                   
                   
               
               
                   
                   
                 Cost of base tube 
               
               
                   
                 Base tube 
                 (relative value) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Composition 
                 MgO: 8.3 wt. % 
                 100 
               
               
                   
                 (28) 
                 Al 2 O 3 : 21.1 wt. % 
               
               
                   
                   
                 BaO: 46.4 wt. % 
               
               
                   
                   
                 TiO 2 : 24.2 wt. % 
               
               
                   
                 Composition 
                 MgO: 2.2 wt. % 
                 85 
               
               
                   
                 (29) 
                 Al 2 O 3 : 5.8 wt. % 
               
               
                   
                   
                 BaO: 60.5 wt. % 
               
               
                   
                   
                 TiO 2 : 31.5 wt. % 
               
               
                   
                   
               
             
          
         
       
     
     Actions and Effects of Example 10-3 
     The composition (29) of the invention not only has the actions of the composition (28), but has a larger content of an inexpensive component. Thus, it can reduce the cost of the materials for the base tube, and consequently contribute to a lowered cost. 
     In addition to exhibiting the effects of the composition (28), this composition increases in the content of an inexpensive component, thus decreasing the materials cost of the base tube. 
     While the invention has been described with reference to the preferred embodiments, it is to be understood that various changes and modifications may be made without departing from the spirit and scope of the invention. All such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.