Abstract:
A novel high-performance biodegradable plastic material based on biodegradable polyester and starch applying LDI(L-Lysine Diisocyanate) as coupling agent.

Description:
BACKGROUND OF THE INVENTION 
       [0001]    1. Field of the Invention 
         [0002]    The present invention relates carbon reduction eco-friendly materials and more particularly, to a biodegradable plastic material. 
         [0003]    2. Description of the Related Art 
         [0004]    Many biodegradable plastic materials are commercially available. These biodegradable plastic materials are eco-friendly, however, they still have some drawbacks. For example, some commercial biodegradable plastic materials are not 100-percent biodegradable; some other commercial biodegradable plastic material are highly biodegradable but with a low level of structural strength. These drawbacks limit the applications of the conventional biodegradable plastic materials. Therefore, there is a strong demand for optimal biodegradable plastic materials that eliminate the aforesaid drawbacks. 
       SUMMARY OF THE INVENTION 
       [0005]    The present invention has been accomplished under the circumstances in view. It is the main object of the present invention to provide a biodegradable plastic material, which is highly degradable and has a high level of structural strength. 
         [0006]    To achieve this and other objects of the present invention, a biodegradable plastic material comprises 50 wt %˜70 wt % biodegradable polyester, 25 wt %˜50 wt % starch, and 0.5 wt %˜2 wt % LDI (L-Lysine Diisocyanate). 
     
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0007]    The advantages and features of the present invention will be fully understood by way of examples in conjunction with the related test results. A biodegradable plastic material in accordance with the present invention comprises 50 wt %˜70 wt % biodegradable polyester selected from the group of PBS (Poly Butylenes Succinate), PCL (Poly Capro Lactone), PLA (Poly Lactic Acid), PBSA (Poly Butylene Succinate-co-Adipate), PBAT (Poly Butylene Adipate-co-Terephthalate), PGA(Poly Glycolic Acid) and PVA (Poly Vinyl Alcohol), 25 wt %˜50 wt % starch selected from the cereal starch group of α starch, corn starch, potato starch, manioc starch, rice starch and wheat starch, and 0.5 wt %˜20 wt % LDI (L-Lysine Diisocyanate). 
         [0008]    The biodegradable plastic material can be used as a base material, or mixed with other plastic materials in a proper percentage for making a biodegradable plastic product having excellent structural strength. 
         [0009]    The following Table I and Table II are material strength test results from examples of group A prepared according to the present invention, wherein the percentage in Table I is a percentage by weight; the percentage by weight of biodegradable polyester in examples of group A is 60%. 
         [0000]    
       
         
               
               
               
               
               
               
             
           
               
                 TABLE I 
               
               
                   
               
               
                   
                 A-1 
                 A-2 
                 A-3 
                 A-4 
                 A-5 
               
               
                   
               
             
             
               
                 PBS (Poly Butylene Succinate) 
                 100% 
                 60% 
                   60% 
                 60% 
                 60% 
               
               
                 60% 
                   
                   
                   
                   
                   
               
               
                 α starch 40% 
                 — 
                 40% 
                 39.5% 
                 39% 
                 38% 
               
               
                 LDI (L-Lysine Diisocyanate) 
                 — 
                 — 
                  0.5% 
                  1% 
                  2% 
               
               
                 0.5%~2% 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                 TABLE II 
               
               
                   
               
               
                   
                 Test 
                   
                   
                   
                   
                   
                   
               
               
                 Properties 
                 method 
                 Unit 
                 A-1 
                 A-2 
                 A-3 
                 A-4 
                 A-5 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 Elongation 
                 ASTM 
                 % 
                 600 
                 80 
                 60 
                 50 
                 20 
               
               
                 at Break 
                 D638 
               
               
                 Melt flow 
                 ASTM 
                 g/10 min 
                 12 
                 5.5 
                 2.8 
                 1.6 
                 0.4 
               
               
                 index@ 
                 D1238 
               
               
                 2.16 kg/ 
               
               
                 150° C. 
               
               
                 Tensile 
                 ASTM 
                 Kgf/cm 2   
                 343 
                 127.4 
                 294 
                 341 
                 352.8 
               
               
                 Strength 
                 D638 
               
               
                 Izod notched 
                 ASTM 
                 Kgf/cm 2   
                 4 
                 1.2 
                 3.2 
                 3.72 
                 2.8 
               
               
                 impact 
                 D256 
               
               
                 strength 
               
               
                   
               
             
          
         
       
     
         [0010]    From the above listed test results, it can be known that the modified material compositions still maintain a high level of material strength. 
         [0011]    The following Table III and Table IV are material strength test results from examples of group B prepared according to the present invention, wherein the percentage by weight of biodegradable polyester in examples of group B is 50%. 
         [0000]    
       
         
               
               
               
               
               
             
           
               
                 TABLE III 
               
               
                   
               
               
                   
                   
                 B-1 
                 B-2 
                 B-3 
               
               
                   
               
             
             
               
                 PBS(Poly Butylene Succinate)  
                 50% 
                   50% 
                 50% 
                 50% 
               
               
                 α starch  
                 50% 
                 49.5% 
                 49% 
                 48% 
               
               
                 LDI (L-Lysine Diisocyanste)  
                 0.5%~2% 
                  0.5% 
                  1% 
                  2% 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE IV 
               
               
                   
               
               
                 Properties 
                 Test method 
                 Unit 
                 B-1 
                 B-2 
                 B-3 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 Elongation at Break 
                 ASTM D638 
                 % 
                 50 
                 42 
                 15 
               
               
                 Melt flow  
                 ASTM  
                 g/10 min 
                 1.11 
                 0.36 
                 0.05 
               
               
                 index@2.16 
                 D1238 
                   
                   
                   
                   
               
               
                 kg/150° C. 
                   
                   
                   
                   
                   
               
               
                 Tensile Strength 
                 ASTM D638 
                 Kgf/cm 2   
                 343.5 
                 362 
                 358 
               
               
                 Izod notched  
                 ASTM D256 
                 Kgf/cm 2   
                 2.12 
                 3.07 
                 1.75 
               
               
                 impact strength 
               
               
                   
               
             
          
         
       
     
         [0012]    The following Table V and Table VI are material strength test results from examples of group C prepared according to the present invention, wherein the percentage by weight of biodegradable polyester in examples of group C is 70%. 
         [0000]    
       
         
               
               
               
               
               
             
           
               
                 TABLE V 
               
               
                   
               
               
                   
                   
                 C-1 
                 C-2 
                 C-3 
               
               
                   
               
             
             
               
                 PBS(Poly Butylene Succinate)  
                 70% 
                   70% 
                 70% 
                 70% 
               
               
                 α starch  
                 30% 
                 29.5% 
                 29% 
                 28% 
               
               
                 LDI (L-Lysine Diisocyanste)  
                 0.5%~2% 
                  0.5% 
                  1% 
                  2% 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE VI 
               
               
                   
               
               
                 Properties 
                 Test method 
                 Unit 
                 C-1 
                 C-2 
                 C-3 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 Elongation at Break 
                 ASTM D638 
                 % 
                 95 
                 73 
                 45 
               
               
                 Melt flow 
                 ASTM D1238 
                 g/10 min 
                 2.77 
                 0.75 
                 0.15 
               
               
                 index@2.16 kg/150° C. 
                   
                   
                   
                   
                   
               
               
                 Tensile Strength 
                 ASTM D638 
                 Kgf/cm 2   
                 340 
                 356 
                 335 
               
               
                 Izod notched impact  
                 ASTM D256 
                 Kgf/cm 2   
                 3.85 
                 4.01 
                 2.74 
               
               
                 strength 
               
               
                   
               
             
          
         
       
     
         [0013]    From the test results of the above-mentioned various groups of samples prove that the biodegradable plastic material of the present invention provides a high level of structural strength. More particularly, the biodegradable plastic material gives the best tensile strength when containing biodegradable polyester 50 wt %, starch 49 wt % and LDI (L-Lysine Diisocyanate) 1 wt %, or the best impact strength when containing biodegradable polyester 70 wt %, starch 29 wt % and LDI (L-Lysine Diisocyanate) 1 wt %. 
         [0014]    The samples received ISO14855-1 biodegradability evaluation test in Plastics Industry Development Center, and the test result is also listed in the attached Annex I. The test result indicates 50% degradability after 59 days, or 99% degradability after 113 days, as shown in Annex I. 
         [0015]    From the above-mentioned test results, the biodegradable plastic material of the invention is highly biodegradable compound material that provides a high level of structural strength. 
         [0016]    Although particular embodiments of the invention have been described in detail for purposes of illustration, various modifications and enhancements may be made without departing from the spirit and scope of the invention. Accordingly, the invention is not to be limited except as by the appended claims.