Abstract:
[Problem] 
     To prepare a thin plate having excellent corrosion resistance, conductivity, and formability at low cost. 
     [Solution] 
     A thin plate is prepared by an ultraquenching transition control injector with a mixture of a metal powder having corrosion resistance to form a matrix and a powder having conductivity, as a raw material. An obtained thin plate has a conductive material component that exists, without dissolving, in a metal matrix exhibiting corrosion resistance by passivation, thereby having aforementioned characteristics.

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to a thin plate having excellent corrosion resistance, conductivity and formability as an industrial material, and the manufacturing method therefor. 
       BACKGROUND ART  
       [0002]    A polymer electrolyte fuel cell (PEFC) extracts energy as electric power from the reaction between hydrogen and oxygen to generate water, which is expected to be useful for future society as a clean power source with no CO2 emission. The use of PEFCs, such as for automobiles, household use fuel cells, and mobile phones, is well known. A component called a separator is used inside the PEFCs. This is mainly a component that forms a flow path for hydrogen and oxygen and allows electricity to flow between cells. 
         [0003]    For the material of PEFC separators, two kinds of material, carbon and metal, are generally used. On the basis of the reasoning that carbon is poor in workability and thick, thus increasing size, metallic separators are anticipated in automotive PEFCs. The development thereof has been underway not only at manufacturers but also at research institutions such as universities. 
         [0004]    In Non Patent Literature 1, formability, corrosion resistance, contact resistance, and power generation characteristics at a supercooled liquid temperature range are reported for the separator of a metallic glass material. 
         [0005]    Patent Literature 1 discloses a manufacturing method in which stainless steel is applied as a base, and in order to make the stainless steel conductive as well, a passive layer is passed through with a deposition, thereby increasing the conductivity between the stainless interior and its surface. A passive layer has high electric resistance, so that contact resistance increases (conductivity deteriorates) when the surface of a material is covered therewith. 
         [0006]    Also in Patent Literatures 2 and 3, the material, in which a passive layer is formed on a surface thereof to improve corrosion resistance, is selected, and similarly as described above, special treatment such as plating is performed on the surface in order to improve conductivity. 
         [0007]    In Patent Literature 4, the manufacturing apparatus for preparing an amorphous thin plate and the method therefor are disclosed, allowing for a thin plate in a size required for PEFC separators.  FIG. 1  shows the structure of an injection gun as a primary device. With this injection gun, a film is formed on a substrate surface while flying powder particles are quenched, finally followed by the release of the film from the substrate so as to obtain an amorphous thin plate. 
       CITATION LIST 
     Non Patent Literature 
       [0008]    [NPL 1] Masanori Yokoyama, Shinichi Yamamura, Hisamichi Kimura, Akihisa Inoue; “Hot Press Workability of Ni-based Metallic Glass in Supercooled Liquid State and Prototype of Fuel Cell Separators,”  Powder and Powder Metallurgy,  54 (2007), 773-777 
       Patent Literature 
       [0009]    [PTL 1] Japanese Unexamined Patent Application Publication No. 2003-193206 
         [0010]    [PTL 2] Japanese Unexamined Patent Application Publication No. 2006-210320 
         [0011]    [PTL 3] Japanese Unexamined Patent Application Publication No. H10-228914 
         [0012]    [PTL 4] Japanese Patent Publication No. 4579317 
       SUMMARY OF INVENTION 
     Technical Problem  
       [0013]    The practical use of metallic separators for PEFCs has been considered difficult because of problems in obtaining a material satisfying all corrosion resistance, conductivity, formability, and cost. In Non Patent Literature 1 and Patent Literature 1, it is said that non-conductive oxide grows on a material surface when applying current, so that power generation characteristics degrade. In Patent Literatures 2 and 3, there seems to be a cost issue for practical uses because special treatment is required for a surface and an expensive material is used. The present invention proposes a metallic separator for PEFCs that satisfies all corrosion resistance, conductivity and formability without requiring a complex procedure, or a thin plate applicable as a material for the separator and the like, and a manufacturing method therefor. 
       Solution to Problem 
       [0014]    In the present invention, the ultraquenching transition control injector as shown in  FIG. 1  or  FIG. 2  is used so as to prepare a metallic thin plate. These injectors are capable of forming, by using a powder raw material, a quenched coating of a melted powder material, on a substrate surface, and further preparing a quenched thin plate obtained by releasing the coating from the substrate. When a powder material having a composition which can easily become amorphous is used, the injector is capable of obtaining an amorphous coating and thin plate. Specifically, the powder material that was completely melted in flame during flying is quenched with refrigerant such as nitrogen gas and mist before reaching the substrate. As a result, the coating formed on the substrate surface will be amorphous. The difference between the ultraquenching transition control injectors in  FIG. 1  and  FIG. 2  is the width of coatings formed at a time. In  FIG. 1 , the width is 15 mm, and in  FIG. 2 , the width is 300 mm. With either ultraquenching transition control injector, coatings and thin plates of the same quality may be obtained. However, in considering production efficiency per ultraquenching transition control injector, the ultraquenching transition control injector in  FIG. 2  is more suitable, so that in the present invention, mainly this injector is used to prepare thin plates. 
         [0015]    In the present invention, for the powder material supplied to the above-mentioned ultraquenching transition control injector, conductive powder is mixed into the composition that tends to become amorphous, or the like. 
         [0016]    Normally in the process of solidifying the metal having a composition that becomes amorphous, when there is a certain substance resulting in a core of crystallization, such as the conductive powder that is mixed this time, the metal is easily crystallized, instead of being amorphous, and then solidified. However, the use of the ultraquenching transition control injector as in  FIG. 1  and  FIG. 2  can prevent crystallization. This is because the metal powder having a composition that becomes amorphous and the conductive powder are not in a mixed state during flying, but these powders fly discretely and (the metal powder having a composition to be amorphous) solidify. That is, by using the ultraquenching transition control injector as in  FIG. 1  or  FIG. 2  with the powder material in which the metal powder having the composition that can become easily amorphous and the conductive powder are mixed, it is possible to prepare a thin plate having the conductive material mixed in a metal matrix which is amorphous or includes an amorphous structure. 
         [0017]    For this, in order to actually confirm this beforehand, Ni 65 Cr 15 P 16 B 4  as the metal powder having a composition that becomes amorphous and C, B4C as the conductive powder were selected, and an amorphous thin plate was prepared by the above-described method with the use of the ultraquenching transition control injector in  FIG. 1 . When an amorphous rate was calculated from the thermal energy of the thin plate measured by DSC (with the thermal energy of the amorphous Ni65Cr15P16B4 ribbon as 100%), the thin plates mixed with either C or B4C conductive powder had the amorphous rate of 89 to 95%. This result is the same as the Ni65Cr15P16B4 thin plate without mixed conductive powder. It was confirmed that the amorphization of Ni 65 Cr 15 P 16 B 4  was not affected by mixed conductive powder. It is noted that DSC stands for Differential Scanning Calorimetry, which measures a difference in amount of heat between a measurement sample and a reference material. With this measurement, it is possible to obtain a thermal energy value when a measurement sample is crystallized from the amorphous state. 
         [0018]    For a metal material having corrosion resistance as a base material (matrix), the use of amorphous and crystal-structure metal such as stainless steel can be considered. Metallic glass, though amorphous it is, has a temperature range in which to turn into a supercooled liquid, so that if the metallic glass is formed in this temperature range, it is possible to perform processing at excellent dimensional accuracy without generating cracks. Also, in the stainless steel, in a case where a plate-shaped product is produced with a general manufacturing method, when boron (B) or the like is added in large quantity to form a conductive deposition, boron (B) or the like dissolves in a matrix in a large amount to deteriorate workability (Solution Hardening). However, when the above-described manufacturing method using the ultraquenching transition control injector in  FIG. 1  or  FIG. 2  is used, the component of the conductive material powder to be mixed does not dissolve in a stainless matrix and exists solely in a thin plate, so that workability deterioration is not expected to be generated.  FIG. 4  shows a cross-sectional picture of a thin plate that was actually prepared. This is the cross-sectional picture of a thin plate that was formed from the powder material, which was the mixture of SUS316L powder and 2.5 wt % of B4C, with the ultraquenching transition control injector in  FIG. 2 . A dark gray area in a dotted circle is B 4 C. Furthermore,  FIG. 5  shows a result of an EDX analysis of SUS316L matrix points in this cross-sectional picture. It was actually confirmed that B did not dissolve in the stainless matrix as described above because the peak of B was not detected herein. EDX stands for Energy Dispersive X-ray Spectrometry. This is an element analysis method, which detects X-rays generated when a sample is irradiated with electron beams, with an energy dispersive detector, and examines substances that make up the sample and its concentrations on the basis of the energy and intensity of the X-rays. In  FIG. 5 , the horizontal axis corresponds to energy; and the vertical axis corresponds to intensity. 
         [0019]    The metal materials to be examined in the present invention form a passive layer to exhibit corrosion resistance, so that the contact resistance is considered large unless treated. Therefore, in order to reduce the contact resistance, it is required to mix a conductive material powder allowing electricity to flow in the passive layer. 
         [0020]    For the conductive powder material, the use of a non-metallic C-based powder was considered. The reason for this is that most of the non-metallic conductive powders remain stable at ph=3 and 80° C. as the driving environment of PEFC, and these powders are inexpensive; however, as long as cost and the effect of characteristics match, various components may be used for the conductive powder. That is because the ultraquenching transition control injector for use in the present invention melts a metal powder material at about 2000° C. with reducing flame with a reduced supply of oxygen, so that when the melting point of conductive powder is higher than that temperature, the conductive powder can remain in a thin plate without melting.  FIG. 4  shows a specific example of a thin plate that was actually prepared by the ultraquenching transition control injector. It is possible to find the remaining B4C (in a dotted circle) in the thin plate, and this B4C is also one of the components to be used as the conductive powder. 
       Advantageous Effects of Invention 
       [0021]    The present invention enables the production of metallic separators for PEFCs having excellent corrosion resistance, conductivity, and formability at low cost. As for the thickness of thin plates, in a case of using steel coils, an increase in rolling costs may be considered as the plates become thinner. However, in the manufacturing method of the present invention, a reduction in plate thickness can be easily adjusted by decreasing the feed rates of the material powder, decreasing the relative speeds between a substrate and an injection gun, etc. 
         [0022]    The thin plate of the present invention has high corrosion resistance at a matrix portion and has excellent conductivity because of having a conductive material. The plate is also advantageous in terms of formability and manufacturing costs, so that it is highly suitable as a metallic separator for PEFCs. 
     
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         [0023]    [FIG. 1]  FIG. 1  is a side view showing the usage of an ultraquenching transition control injector. 
           [0024]    [FIG. 2]  FIG. 2A  is a side view and  FIG. 2B  is a bottom view each showing a large ultraquenching transition control injector. 
           [0025]    [FIG. 3]  FIG. 3  is a side view showing the overall production line of thin plates. 
           [0026]    [FIG. 4]  FIG. 4  is microscopic structure photography showing the cross section of a SUS316L thin plate mixed with B4C at 2.5 wt %. 
           [0027]    [FIG. 5]  FIG. 5  is a graph showing the EDX result of a SUS316L matrix of  FIG. 4 . 
           [0028]    [FIG. 6]  FIG. 6  is a side view showing upstream and downstream mist angles of the ultraquenching transition control injector of  FIG. 2 . 
           [0029]    [FIG. 7]  FIG. 7  is microscopic structure photography showing the cross section of a Ni65Cr15P16B4 thin plate mixed with C at 0.3 wt %. 
           [0030]    [FIG. 8]  FIG. 8  is a diagram illustrating a circuit 1 of measurement. 
           [0031]    [FIG. 9]  FIG. 9  is a diagram illustrating a circuit 2 of measurement. 
           [0032]    [FIG. 10]  FIG. 10  is a graph showing the result of contact resistance measurement. 
       
    
    
     DESCRIPTION OF EMBODIMENTS 
       [0033]    1. Preparation of Thin Plate and Test Specimen (Corrosion Resistance, Contact Resistance) 
         [0034]    For a metal material for use in an injection gun (ultraquenching transition control injector), a gas atomized powder having the composition of Ni65Cr15P16B4 (at %) and being classified as +38/−63 μm in diameter was used. This is a composition that solidifies as metallic glass when quenched, and this composition was selected also in the present invention in order to achieve the formation in a supercooled liquid range. 
         [0035]    For a conductive powder to be mixed in the metal material mentioned above, artificial graphite (AGB-5 from Ito Graphite Co., Ltd.) having the average particle size of 5 μm was used (hereinafter, referred to as carbon). This powder is obtained by pulverizing artificial graphite electrodes, and is available at low cost. 
         [0036]    Ni 65 Cr 15 P 16 B 4  and 0.3wt % of carbon powder were mixed and stirred to obtain a material for injection. After mixing, water was removed by keeping the material warm in a drying oven under the condition of 80° C. for two hours. This is performed for a purpose of achieving stable powder supply without clogging or the like inside a supply path during the injection of the powder material. 
         [0037]    For the injection gun, the ultraquenching transition control injector shown in  FIG. 2  was used. Mixed gas of oxygen and propane is used for fuel, and combustion flame is ejected from flame vents  5  outside of powder ejection ports  6 , which are arranged at equal intervals in the widthwise direction. The powder material ejected from the powder ejection ports  6  is completely melted once in the combustion flame. The material is deposited on the surface of a substrate while being quenched, right after being melted, with a refrigerant mist ejected from a mist ejection port  3  arranged outside the powder ejection ports  6 , thereby forming a film. This injection gun injects the material uniformly in the widthwise direction, and thus, it is possible to prepare a thin plate having a uniform thickness in the widthwise direction. 
         [0038]    The above-described ultraquenching transition control injector was installed in the thin plate production line shown in  FIG. 3 . A pickled steel coil of 2 mm in thickness×300 mm in width is set between a payoff reel  7  and a coil winder  13 , and the coil is moved toward the coil winder  13 . First, the coil is heated with propane flame by a preheater  8 . Then, after the coil shape was corrected by a leveler  9 , the coil was heated up to the target temperature of 250° C. by a thin plate substrate heating and heat-equalizing device  10 . 
         [0039]    On the surface of the coil that was heated up to the target temperature of 250° C., a film was formed with the mixed powder by an ultraquenching transition control injector  11 . Immediately after the film formation, 10% reduction was applied thereon with a rolling mill  12 . Before being wound on the coil winder  13 , the film was released from the coil, thus obtaining a thin plate  14 . At this time, the film temperature is 220 to 280° C. right after the reduction applied with the rolling mill  12 . It is noted that in a series of operations, a coil speed was constant at 5.7 m/min. The above-described condition for manufacturing thin plates is shown in Table 1. An upstream mist angle and a downstream mist angle in Table 1 show a positional relationship, relative to the coil movement direction, of a mist ejection nozzle  2  and an inclination from the direction at right angles to the plane of the coil. The conditions are illustrated in  FIG. 6 . 
         [0000]    
       
         
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
             
             
               
                   
                 Feed Rate of Alloy Powder (g/s) 
                 30 
               
               
                   
                 Flow Rate of Propane Gas (m 3 /h) 
                 34 
               
               
                   
                 Oxygen Flow Rate (m 3 /h) 
                 120 
               
               
                   
                 Rectified Nitrogen Flow Rate (m 3 /h) 
                 400 
               
               
                   
                 Injection Distance to Coil (mm) 
                 600 
               
               
                   
                 Upstream Mist Angle (°) 
                 9 
               
               
                   
                 Upstream Mist Flow Rate (liter/min) 
                 4 
               
               
                   
                 Downstream Mist Angle (°) 
                 9 
               
               
                   
                 Downstream Mist Flow Rate (liter/min) 
                 4 
               
               
                   
                 Coil Surface Temperature Before 
                 250 
               
               
                   
                 Injection 
               
               
                   
                 Rolling Speed (m/min) 
                 5.7 
               
               
                   
                   
               
             
          
         
       
     
         [0040]    The thin plate obtained thereby had a size of 300 μm in thickness×300 mm in width. The thin plate was confirmed by DSC to have 85% amorphous rate in comparison with an amorphous ribbon material which has 100% amorphous rate.  FIG. 7  is a cross-sectional picture of the thin plate obtained thereby. It is observed that C (in a dotted circle) remains in the Ni65Cr15P16B4 matrix. 
         [0041]    Further, in order to confirm a difference in contact resistance between the cases with or without the conductive powder, an amorphous thin plate was also prepared from Ni65Cr15P16B4 powder having no mixed carbon powder, in the same procedures as described above. Finally, the following two types of thin plates were prepared. 
         [0000]    
       
         
               
               
               
               
             
           
               
                 TABLE 2 
               
               
                   
               
               
                   
                   
                   
                 Mixing Rate of 
               
               
                   
                 Composition of Metal 
                 Conductive 
                 Conductive Powder 
               
               
                 Sample No. 
                 Matrix (at %) 
                 Powder 
                 (wt %) 
               
               
                   
               
             
             
               
                 1 
                 Ni 65 Cr 15 P 16 B 4   
                 None 
                 — 
               
               
                 2 
                 Ni 65 Cr 15 P 16 B 4   
                 C 
                 0.3 
               
               
                   
               
             
          
         
       
     
         [0042]    2. Contact Resistance Test 
         [0043]    The prepared thin plates were cut out in the size of 35-mm square with a micro cutter. The amorphous thin plates were treated by a router to have a flat and smooth surface on the side opposite to the coil (having had a surface roughness of about Ra 10 μm since they remained as they were after injection). 
         [0044]    In order to passivate the material surface, the plates were immersed for two hours in sulfuric acid of ph=3 at 80° C. and then experimented on. 
         [0045]    A constant current of 1A was applied to a circuit shown in  FIG. 8  to measure a potential difference between gold layers (Au-1-Au-2), and a resistance value was calculated on the basis of Ohm&#39;s law. This resistance value, being a contact resistance of Au—Carbon (C) paper existing at two locations in the circuit, was divided by 2 to give Rc (contact resistance of Au—C paper). To determine Rc per 1 kgf/cm 2 , contact pressure was changed from 1 to 7 kgf/cm 2 . 
         [0046]    Then, a constant current of 1A was similarly applied to a circuit shown in  FIG. 9  to measure a potential difference between Au-1 and the test specimen, and a resistance value Ra was calculated on the basis of Ohm&#39;s law. Similar to the above description, to determine Ra per 1 kgf/cm 2 , contact pressure was changed from 1 to 7 kgf/cm 2 . Finally, according to the formula below, a contact resistance value Rs between the test specimen and the C paper was calculated, and conductivity was evaluated on the basis of this value. 
         [0000]    
       
      
       Rs=Ra−Rc  
      
     
         [0047]      FIG. 10  shows the measurement result of contact resistance. The amorphous material of Ni65Cr15P16B4 exhibits corrosion resistance by passivation on its surface. On the surface of both test specimens, a passive layer is formed during the sulfuric acid immersing process before the test. A reason why the contact resistance value of the C admixture is low at any contact pressure may be that C, a conductor, is present also in the passive layer. Accordingly, it is possible to say that the contact resistance that increases with passivation may be reduced by preparing a metallic thin plate with a powder material mixed with C by using an ultraquenching transition control injector. 
         [0048]    3. Corrosion Resistance Test 
         [0049]    The prepared No. 2 thin plate (with mixed C) was cut out in the size of 20-mm square with a micro cutter, and was then experimented. As an immersion solution, sulfuric acid of ph=3 (80° C.) was prepared, and immersion was performed for 24 hours. The weight of the test specimen was measured before and after immersion, and corrosion rate (pm/year) was calculated from weight changes and specific gravity. 
         [0050]    The result was 3 μm/year, confirming that it had sufficient corrosion resistance as a separator for PEFCs. 
         [0051]    As described above, it was confirmed that a thin plate with a mixed conductive powder of the present invention can satisfy conductivity and corrosion resistance necessary for a separator for PEFCs. 
       REFERENCE SIGNS LIST  
       [0000]    
       
           1  Powder Supply Pipe 
           2  Mist Ejection Nozzle 
           3  Mist Ejection Port 
           4  Inert Gas Ejection Port 
           5  Flame Vent 
           6  Powder Ejection Port 
           7  Payoff Reel 
           8  Preheater 
           9  Leveler 
           10  Thin plate substrate heating and heat-equalizing device 
           11  Ultraquenching Transition Control Injector 
           12  Rolling Mill 
           13  Coil Winder 
           14  Released Thin Plate