Abstract:
It is an object of the present invention to provide a new method for production of zinc oxide particles which can control the particle diameter and particle shape of obtained zinc oxide particles by selecting suitable conditions, and can prepare zinc oxide applicable to various applications. A method for production of zinc oxide particles, comprising a step of aging a zinc oxide raw material in an aqueous zinc salt solution.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     This application is a Continuation-in-Part of Application No. PCT/JP2012/061280, filed on Apr. 26, 2012, which claims priority to Application No. 2011-101021, filed on Apr. 28, 2011; Application No. PCT/JP2012/061281, filed on Apr. 26, 2012, which claims priority to Application No. 2011-101022, filed on Apr. 28, 2011; and Application No. PCT/JP2012/061282, filed on Apr. 26, 2012, which claims priority to Application No. 2011-101023, filed on Apr. 28, 2011; for which priority is claimed. The entire contents of each of these applications is hereby incorporated by reference. 
    
    
     TECHNICAL FIELD 
     The present invention relates to a method for production of zinc oxide particles. 
     BACKGROUND OF THE DISCLOSURE 
     Zinc oxide particles have been known as a sunscreen ultraviolet blocking agent in cosmetic product applications. However, the applications of the zinc oxide fine particles, which have been used conventionally, are limited from various points of view. Therefore, a new production method which is able to control a particle diameter and particle shape for enhancing the homogeneity thereof has been desired. The following described about various conventional zinc oxides and methods for production of the zinc oxide. 
     The zinc oxide particles in Patent Document 1 are formed by aggregation of zinc oxide fine particles in a hexagonal plate shape, and therefore proper slippage cannot be achieved. Further, since the particle shape is not sufficiently controlled, physical properties tend to vary, so that it is difficult to obtain a cosmetic with stable quality. 
     Patent Document 2 describes flaky plate-shaped zinc oxide particles, and uses thereof in cosmetics and industrial applications. However, many of the flaky plate-shaped zinc oxide particles described in Patent Document 2 have a large particle diameter, and the particle shape is not controlled to be fine and uniform. In the production method, a basic zinc salt is generated, and therefore a thermal decomposition step such as that of calcinating is required to obtain zinc oxide. 
     Patent Document 3 describes hexagonal plate-shaped zinc oxide particles. However, the zinc oxide particles in Patent Document 3 significantly vary in particle diameter and shape, and are aggregated, so that problems such as those described above cannot be sufficiently rectified. 
     Patent Document 4 describes hexagonal prism- and hexagonal barrel-shaped zinc oxide particles which can be used as a cosmetic. However, in the described production method, hexagonal prism-shaped zinc oxide particles having a particle diameter of less than 0.5 μm cannot be obtained. 
     From such a point of view, zinc oxide particles which have a primary particle diameter of 0.1 μm or more and can exhibit higher transparency and higher ultraviolet blocking performance as compared to conventional zinc oxide particles are desired. However, such zinc oxide particles have not been developed. 
     Patent Document 5 discloses a production method in which a mixed liquid of a zinc compound, acetic acid and glycol is held at a temperature of 50 to 200° C. for 0.5 to 5 hours to generate zinc oxide fine particles having an average particle diameter of 200 nm or less. However, this production method is a method of obtaining a precipitate by heating a solution in which zinc oxide is fully dissolved, and zinc oxide particles obtained by this method are not preferable because particles having an aspect ratio of less than 2.5 cannot be obtained. Further, the production method is not suitable from an industrial point of view because expensive glycol is used. 
     In applications of heat releasing materials in electronic/electrical fields, aluminum oxide, aluminum nitride, boron nitride, zinc oxide and the like are often used as a heat releasing filler. It is generally known that two or more kinds of spherical particles having different particle diameters are filled, and a filler is filled in a resin or the like at a high rate for achieving high heat releasing performance. Meanwhile, it is considered to make use of anisotropy of thermal conduction by compounding particles of different shapes, such as plate-shaped particles and needle-shaped particles, for more effectively enhancing heat conductivity. However, the zinc oxide particles in Patent Document 1 are aggregates, and therefore influences of heat resistance between particles in plate-shaped particles are significant, so that anisotropy of thermal conduction specific to plate-shaped particles cannot be exhibited. 
     Usually, in production of zinc oxide particles, mostly a calcinating step is essential. In calcinating, however, equipment capable of performing a treatment at a high temperature is required, and there is the problem that the particle diameter and the particle shape which have been adjusted/controlled in the stage of a zinc oxide precursor are changed by calcinating, and so on. Therefore, it is very preferable to obtain zinc oxide particles without performing calcinating. 
     PRIOR TECHNICAL DOCUMENTS 
     Patent Documents 
     
         
         [Patent Document 1] Japanese Kokai Publication 2007-223874 
         [Patent Document 2] Japanese Kokai Publication Hei7-187673 
         [Patent Document 3] Japanese Kokai Publication Hei9-137152 
         [Patent Document 4] Japanese Kokai Publication 2008-254992 
         [Patent Document 5] Japanese Kokai Publication 2009-29698 
       
    
     SUMMARY OF INVENTION 
     Problems to be Solved by the Invention 
     In view of the situations described above, it is an object of the present invention to provide a new method for production of zinc oxide particles which can control the particle diameter and particle shape of obtained zinc oxide particles by selecting suitable conditions, and can prepare zinc oxide applicable to various applications. 
     Means for Solving Object 
     The present invention relates to a method for production of zinc oxide particles, comprising a step of aging a zinc oxide raw material in an aqueous zinc salt solution. 
     Preferably, a zinc salt concentration in the aqueous zinc salt solution is 0.005 mol/l or more and 4.00 mol/l or less. 
     Preferably, the zinc oxide raw material has particle diameter of 0.005 μm or more and 0.5 μm or less. 
     The method for production of zinc oxide particles may comprises a step of surface treating the obtained zinc oxide particles. 
     Effects of the Invention 
     The method for production of zinc oxide particles of the present invention can obtain zinc oxide particles having various particle shapes and produce zinc oxide particles having high homogeneity in particle diameter and particle shape. Furthermore, by this production method, zinc oxide particles can be obtained directly without passing through a thermal decomposition step such as that of calcinating. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a scanning electron microscope photograph of zinc oxide particles of the present invention obtained in Example 1. 
         FIG. 2  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 1. 
         FIG. 3  is a scanning electron microscope photograph of zinc oxide particles of the present invention obtained in Example 2. 
         FIG. 4  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 2. 
         FIG. 5  is an X-ray diffraction spectrum of zinc oxide particles of the present invention obtained in Example 2. 
         FIG. 6  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 3. 
         FIG. 7  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 3 which are observed with a higher magnification. 
         FIG. 8  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 4. 
         FIG. 9  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 4 which are observed with a higher magnification. 
         FIG. 10  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 5. 
         FIG. 11  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 5 which are observed with a higher magnification. 
         FIG. 12  is an X-ray diffraction spectrum of zinc oxide particles of the present invention obtained in Example 5. 
         FIG. 13  is a transmission electron microscope photograph of zinc oxide particles (Fine zinc oxide manufactured by Sakai Chemical Industry Co., Ltd.) used in Comparative Example 1. 
         FIG. 14  is a transmission electron microscope photograph of zinc oxide particles obtained in Comparative Example 2. 
         FIG. 15  is a transmission electron microscope photograph of zinc oxide particles (FINEX-50 manufactured by Sakai Chemical Industry Co., Ltd.) used in Comparative Example 4. 
         FIG. 16  is a transmission electron microscope photograph of zinc oxide particles (FINEX-30 manufactured by Sakai Chemical Industry Co., Ltd.) used in Comparative Example 5. 
         FIG. 17  is a schematic view illustrating a method for measurement of a primary particle diameter of zinc oxide particles obtained in Examples 1 to 5, and in Comparative examples 1 to 5. 
         FIG. 18  is a schematic view illustrating a method for measurement of an aspect ratio of hexagonal plate-shaped zinc oxide particles obtained by the method for production of the present invention. 
         FIG. 19  is a schematic view illustrating a method for measurement of an aspect ratio of hexagonal prism-shaped zinc oxide particles obtained by the method for production of the present invention. 
         FIG. 20  is a schematic view illustrating a method for measurement of an aspect ratio of indefinite-shaped zinc oxide particles obtained in Examples 11 to 13, and in Comparative examples 1 to 7. 
         FIG. 21  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 6. 
         FIG. 22  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 6 which are observed with a higher magnification. 
         FIG. 23  is an X-ray diffraction spectrum of zinc oxide particles of the present invention obtained in Example 6. 
         FIG. 24  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 7. 
         FIG. 25  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 7 which are observed with a higher magnification. 
         FIG. 26  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 8. 
         FIG. 27  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 8 which are observed with a higher magnification. 
         FIG. 28  is a scanning electron microscope photograph of zinc oxide particles of the present invention obtained in Example 8. 
         FIG. 29  is an X-ray diffraction spectrum of zinc oxide particles of the present invention obtained in Example 8. 
         FIG. 30  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 9. 
         FIG. 31  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 9 which are observed with a higher magnification. 
         FIG. 32  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 10. 
         FIG. 33  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 10 which are observed with a higher magnification. 
         FIG. 34  is a transmission electron microscope photograph of zinc oxide particles obtained in Comparative Example 6. 
         FIG. 35  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 11. 
         FIG. 36  is an X-ray diffraction spectrum of zinc oxide particles of the present invention obtained in Example 11. 
         FIG. 37  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 12. 
         FIG. 38  is a transmission electron microscope photograph of zinc oxide particles of the present invention obtained in Example 13. 
         FIG. 39  is a transmission electron microscope photograph of zinc oxide particles obtained in Comparative Example 7. 
     
    
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
     The present invention will be described in detail hereinafter. 
     The present invention relates to a method for production of zinc oxide particles, comprising a step of aging a source of zinc oxide in an aqueous zinc salt solution. 
     In this production method, unlike a method of performing aging after forming particles by neutralization of a zinc salt compound as described in the cited documents, zinc oxide raw material is added as a seed, and therefore particles are grown as the surface layers thereof are repeatedly dissolved and precipitated while zinc oxide raw material as a seed serves as cores. Thus, the particle diameters of zinc oxide particles obtained after aging using, as a base, zinc oxide raw material as cores are determined, and particle shapes and particle diameters are established in a uniform state, so that the particle size distribution can be further sharpened. Therefore, the above-mentioned production method is preferable in that the particle diameter and the particle size distribution are more precisely controlled. The production method is also preferable in that owing to zinc oxide raw material as a seed, zinc oxide particles having a sharp particle size distribution can be selectively obtained. 
     By adjusting an aging temperature, an aging time, a zinc salt concentration, a zinc oxide raw material concentration and so on as necessary, the particle diameter and shape, and the like can be adjusted. 
     In production of zinc oxide particles as described above, zinc oxide raw material is used. The zinc oxide raw material is not particularly limited, but its particle diameter is preferably 0.005 μm or more and 0.5 μm or less. The particle diameter of the zinc oxide raw material corresponds to a diameter of a sphere having the same surface area as a specific surface area determined by a BET method. That is, the particle diameter is a value determined by the following calculation formula from a specific surface area: Sg determined by making a measurement using a fully automatic BET specific surface area measuring device Macsorb (manufactured by Mountech Co., Ltd.), and a true specific gravity of zinc oxide: ρ.
 
particle diameter(μm)=[6/( Sg ×ρ)]
 
     (Sg (m 2 /g): specific surface area, ρ (g/cm 3 ): true specific gravity of particle) 
     As the true specific gravity of particle: ρ, a value of the true specific gravity of zinc oxide, i.e. 5.6, was used for the above calculation. 
     Zinc oxide raw material that can be used as a raw material is not particularly limited, and zinc oxide produced by a known method can be used. Examples of those that are commercially available may include FINEX-75, FINEX-50, FINEX-30, Fine zinc oxide, SF-15, and ZINC OXIDE NO. 1 manufactured by Sakai Chemical Industry Co., Ltd. 
     In the method for production of zinc oxide particles according to the present invention, the zinc oxide raw material described above is aged in an aqueous zinc salt solution. That is, the zinc oxide raw material is dispersed in an aqueous zinc salt solution, and heated in this state to be crystal-grown. 
     The solvent to be used in the present invention is water. Water is inexpensive and safe in terms of handling, and is therefore most preferable from the viewpoint of production control and costs. 
     The aqueous zinc salt solution to be used is not particularly limited, and examples thereof may include aqueous solutions of zinc acetate, zinc nitrate, zinc sulfate, zinc chloride and zinc formate. Particularly when an aqueous zinc acetate solution, among the aqueous zinc salt solutions, is used, specific zinc oxide particles of the present invention can be suitably obtained. 
     These aqueous zinc salt solutions may be those prepared by mixing zinc oxide, an acid and water to acid-hydrolyze zinc oxide. The particle shape and particle size of zinc oxide to be used when the aqueous zinc salt solution is prepared with zinc oxide, an acid and water are not particularly limited, but the Zn purity of zinc oxide is preferably 95% or more for reducing impurities as much as possible. Examples of the acid include acetic acid, nitric acid, sulfuric acid, hydrochloric acid, formic acid, citric acid, oxalic acid, propionic acid, malonic acid, lactic acid, tartaric acid, gluconic acid and succinic acid, and particularly when acetic acid is used, specific zinc oxide particles of the present invention can be suitably obtained. Two of these aqueous zinc salt solutions may be used in combination. 
     The zinc salt concentration in the aqueous zinc salt solution is preferably 0.005 mol/l or more and 4.00 mol/l or less, and particularly the zinc salt concentration in the aqueous zinc acetate solution is preferably more than 0.05 mol/l and 2.00 mol/l or less. 
     The zinc salt concentration in the aqueous zinc salt solution is preferably set according to the shape of the desired zinc oxide particles because the zinc salt concentration influences the shape of the zinc oxide particles to be obtained. For example, when the concentration is more than 0.45 mol/l and 4.00 mol/l or less, the zinc oxide particle to be obtained tends to be hexagonal plate-shaped particles. When the concentration is 0.30 mol/l or more and 0.45 mol/l or less, the zinc oxide particles to be obtained tend to be hexagonal prism-shaped particles. When the concentration is less than 0.30 mol/l, the zinc oxide particles to be obtained tend to be zinc oxide ultra fine particles having well-ordered particle diameter and particle shape. 
     When zinc oxide raw material is added in the aqueous zinc salt solution to form a slurry, the concentration of zinc oxide raw material is preferably 10 to 500 g/l based on the total amount of the slurry. 
     The method for preparation of a slurry is not particularly limited, and for example, a homogeneous slurry having a zinc oxide raw material concentration of 10 to 500 g/l can be formed by adding the above-described components to water, and dispersing the components at 5 to 30° C. for 10 to 30 minutes. 
     In the aging described above, components other than zinc oxide raw material, a zinc salt and water may be added in a small amount within the bounds of not impairing the effect of the present invention. For example, a dispersant and the like may be added. 
     Preferably, aging is performed at 45 to 110° C. The aging time may be 0.5 to 24 hours. The particle diameter can be adjusted by conditions such as an aging temperature, an aging time, a zinc oxide raw material concentration and a zinc salt concentration. Therefore, by adjusting these conditions, the method for production of zinc oxide particles according to the present invention can obtain zinc oxide particles having various shapes and particle diameters, on the other hand, having a high homogeneity in a particle diameter and a particle shape as well as a high purity. 
     Zinc oxide particles thus obtained may be subjected to post-treatments such as filtration, water washing and drying as necessary. 
     Zinc oxide particles produced by the above-described method may be classified by sieving as necessary. Examples of methods for classification by sieving may include wet classification and dry classification. Further, a treatment such as wet crushing or dry crushing may be performed. 
     As described above, the method for production of zinc oxide particles according to the present invention is capable of obtaining zinc oxide particles without performing a calcinating treatment, but zinc oxide particles obtained by the above-described method may be subjected to a calcinating treatment. For calcinating, mention may be made of a known method using an arbitrary device, and treatment conditions and the like are not particularly limited. 
     The method for production of zinc oxide particles may further comprise a surface treatment step as necessary. The surface treatment is not particularly limited, and examples thereof may include known treatment methods such as inorganic surface treatments to form an inorganic oxide layer such as a silica layer, an alumina layer, a zirconia layer or a titania layer, and various kinds of other surface treatments. Two or more kinds of surface treatments may be sequentially performed. 
     More specific examples of the surface treatment may include surface treatments with a surface treatment agent selected from an organic silicon compound, an organic aluminum compound, an organic titanium compound, a higher fatty acid, a higher fatty acid ester, a metallic soap, a polyhydric alcohol and an alkanolamine. For the surface treatment agent described above, a treatment amount can be appropriately set according to the particle diameter of the zinc oxide particle. 
     Examples of the organic silicon compound may include organopolysiloxanes such as methyl hydrogen polysiloxane and dimethyl polysiloxane, and silane coupling agents such as triethoxyvinylsilane and diphenyldimethoxysilane. 
     Examples of the higher fatty acid may include higher fatty acids having 10 to 30 carbon atoms, such as lauric acid, stearic acid and palmitic acid. 
     Examples of the higher fatty acid ester may include alkyl esters of the above-described higher fatty acids, such as octyl palmitate. 
     Examples of the metallic soap may include metal salts of the above-described higher fatty acids, such as aluminum stearate and aluminum laurate. The metal species that forms the metallic soap is not particularly limited, and examples thereof may include aluminum, lithium, magnesium, calcium, strontium, barium, zinc and tin. 
     Examples of the polyhydric alcohol may include trimethylolethane, trimethylolpropane and pentaerythritol. 
     Examples of the alkanolamine may include diethanolamine, dipropanolamine, triethanolamine and tripropanolamine. 
     The treatment with the surface treatment agent can be achieved by mixing a predetermined amount of the surface treatment agent with the zinc oxide particles. Further, the treatment can be achieved by adding the zinc oxide particles to an appropriate medium, for example, water, an alcohol, an ether or the like to be suspended, adding a surface treatment agent to the suspension, followed by stirring, separating, drying and crushing the suspension, or solidifying by evaporation and crushing the suspension. 
     Since zinc oxide particles subjected to the surface treatment described above have various kinds of coating layers such as those of zinc silicate on the surfaces thereof, the physiological activity and chemical activity thereof are suppressed when the zinc oxide particles are compounded in a cosmetic, and therefore a particularly excellent cosmetic product can be provided. 
     The zinc oxide particles obtained by the method for production of zinc oxide particles of the present invention are not particularly limited for applications thereof, and can be suitably used in, for example, applications of raw materials of cosmetics and heat releasing fillers. 
     Further, the zinc oxide particles of the present invention can be used in the fields of vulcanization accelerators for rubber, pigments for coatings/inks, electronic components such as ferrites and varistors, pharmaceuticals and so on in addition to the cosmetics and heat releasing fillers described above. 
     EXAMPLES 
     Hereinafter, the present invention will be explained with reference to examples. However, the present invention is not limited to these examples. 
     The measurement methods for each evaluation item in the examples are described in detail, prior to examples. 
     (Composition of Obtained Particles) 
     The X-ray diffraction spectra shown in Figs and the compositions of the obtained particles in Table show results of performing analysis using an X-ray diffractometer UltimaIII (manufactured by Rigaku Corporation) having an X-ray tube with copper. From these results, it is evident that zinc oxide was obtained in the examples. 
     (Primary Particle Diameter) 
     The primary particle diameter, in Table 1 of this specification, is a particle diameter (μm) defined by a unidirectional particle diameter in a visual field of 2000 to 50000 magnification in a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.) photograph (distance between two parallel lines in a fixed direction with a particle held therebetween; measurements are made in a fixed direction regardless of shapes of particles on the image), and is a geometric particle diameter obtained by measuring the unidirectional diameters of 250 primary particles in the TEM photograph and determining an average value of a cumulative distribution thereof. For the method for measurement of a primary particle diameter,  FIG. 17  is attached. 
     (Aspect Ratio) 
     The aspect ratio of the hexagonal plate-shaped zinc oxide particles is a value determined as a ratio of L/T where L is an average value of measured particle diameters (μm) of 250 particles, the particle diameter defined by a unidirectional diameter for particles in which the hexagonal-shaped surface of the hexagonal plate-shaped zinc oxide particle faces frontward (distance between two parallel lines in a fixed direction with a particle held therebetween; measurements are made in a fixed direction for particles in which the hexagonal-shaped surface on the image faces frontward), and T is an average value of measured thicknesses (μm) (length of the shorter side of rectangle) of 250 particles for particles in which the side surface of the hexagonal plate-shaped zinc oxide particle faces frontward (particles that appear rectangular), in a visual field of 2000 to 50000 magnification in a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.) photograph or a scanning electron microscope (SEM, JSM-5600, manufactured by JEOL Ltd.) photograph. For the method for measurement of an aspect ratio,  FIG. 18  is attached. 
     For the aspect ratio of the zinc oxide particles having an indefinite particle shape, a major axis of the indefinite-shaped zinc oxide particle and a minor axis passing through the center of the major axis are measured in a visual field of 2000 to 50000 magnification in a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.) photograph, and a ratio between the lengths of the major axis and the minor axis: major axis/minor axis is determined. The ratio of major axis/minor axis is measured in the manner described above for 250 indefinite-shaped zinc oxide particles in the TEM photograph, and an average value of a cumulative distribution thereof is determined as an aspect ratio. The method for measurement of an aspect ratio of indefinite-shaped zinc oxide particles is shown in  FIG. 20 . 
     The aspect ratio of the zinc oxide particles having a hexagonal prism particle shape in the comparative example is determined in the following manner. For the aspect ratio of the hexagonal prism-shaped zinc oxide particles, a major axis and a minor axis are measured for particles in which the side surface of the hexagonal prism-shaped zinc oxide particle faces frontward (particles observed as a rectangular or square shape) in a visual field of 2000 to 50000 magnification in a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.) photograph, and a ratio between the lengths of the major axis and the minor axis: major axis/minor axis is determined. The ratio of major axis/minor axis is measured in the manner described above for 250 hexagonal prism-shaped zinc oxide particles in the TEM photograph, and an average value of a cumulative distribution thereof is determined as an aspect ratio. Hexagonal prism-shaped zinc oxide particles in which the hexagonal-shaped surface faces frontward were excluded from measurement objects because it was difficult to determine the thickness. The method for measurement of an aspect ratio of hexagonal prism-shaped zinc oxide particles is shown in  FIG. 19 . 
     (Crystallite Diameter) 
     For the crystallite diameter (μm) in Table 1 of this specification, results of performing analysis using an X-ray diffractometer UltimaIII (manufactured by Rigaku Corporation) having an X-ray tube with copper are shown. The crystallite usually means a small single crystal in a microscopic level, which forms a crystalline substance. In Table 1 of this specification, the crystallite diameter (μm) is a value determined from a half width of a diffraction peak of the plate-shaped surface: (002) plane of zinc oxide in the X-ray diffraction pattern of a hexagonal wurtzite-type zinc oxide particle. 
     (Crystallite Diameter/Primary Particle Diameter) 
     A value shown as crystallite diameter/primary particle diameter in Table 1 of this specification is a value as an indicator of a level of independency of primary particles that form a powder. As described previously, the primary particle diameter is a particle diameter (μm) defined by a unidirectional particle diameter in a visual field of 2000 to 50000 magnification in a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.) photograph (distance between two parallel lines in a fixed direction with a particle held therebetween; measurements are made in a fixed direction regardless of shapes of particles on the image), and is a geometric particle diameter obtained by measuring the unidirectional diameters of 250 primary particles in the TEM photograph and determining an average value of a cumulative distribution thereof. On the other hand, the crystallite diameter is a value determined from a half width of a diffraction peak of the plate-shaped surface: (002) plane of zinc oxide in the X-ray diffraction pattern as described previously. Therefore, as the value of crystallite diameter/primary particle diameter becomes closer to 1, a difference between the geometric particle diameter and the single crystal size decreases, which means that primary particles are not aggregated particles, but exist independently as single crystal particles. The values of crystallite diameter/primary particle diameter of the hexagonal plate-shaped zinc oxide particles obtained in Examples 4 and 5 are both 0.64, and therefore primary particles are not aggregated particles but rather single crystals. 
     (Powder Touch) 
     The powder touch herein is an indicator showing slippage and roughness in a touch felt when a small amount of a powder is placed on the skin and the powder is drawn by a finger. Herein, score evaluations are performed in five grades with score 5 given when slippage is very good and no roughness is felt, score 4 given when slippage is good and almost no roughness is felt, score 3 given when both slippage and roughness are moderate, score 2 given when slippage is poor and roughness is felt, and score 1 given when slippage is very poor and roughness is felt. The results are shown in Table 1. A higher score means a better powder touch, and particles having a better powder touch can be more suitably used in applications of foundations and other makeup cosmetics. 
     (Preparation of Coating Film) 
     In a mayonnaise bottle having a volume of 75 ml, 2 g of zinc oxide particles obtained in each of examples and comparative examples, 10 g of varnish (ACRYDIC A-801-P manufactured by DIC Corporation), 5 g of butyl acetate (special grade reagent, manufactured by Wako Pure Chemical Industries, Ltd.), 5 g of xylene (genuine special grade, manufactured by JUNSEI CHEMICAL CO., LTD.) and 38 g of glass beads (1.5 mm, manufactured by Potters-Ballotini Co., Ltd.) were put and sufficiently mixed, then fixed in a paint conditioner Model 5410 (manufactured by RED DEVIL, Inc.), and subjected to a dispersion treatment by giving vibrations for 90 minutes, thereby preparing a coating. Next, a small amount of the prepared coating was added dropwise onto a slide glass (length/width/thickness=76 mm/26 mm/0.8 to 1.0 mm, manufactured by Matsunami Glass Ind., Ltd.), and a coating film was prepared using a bar coater (No. 579 ROD No. 6, manufactured by YASUDA SEIKI SEISAKUSHO, LTD.). The prepared coating film was dried at 20° C. for 12 hours, and then used for measurement of total light transmittance 1, total light transmittance 2, total light transmittance 3, total light transmittance 4(%), parallel light transmittance 1, parallel light transmittance 2, haze, and sharpened gloss (20° gloss). 
     (Total Light Transmittance 1, Total Light Transmittance 2, Total Light Transmittance 3, Parallel Light Transmittance 1 and Parallel Light Transmittance 2) 
     Herein, total light transmittance 1(%), total light transmittance 2(%), total light transmittance 3(%), parallel light transmittance 1(%) and parallel light transmittance 2(%) are values obtained by measuring the prepared coating film using a spectrophotometer V-570 (manufactured by JASCO Corporation). The value of total light transmittance 1(%) is a value of total light transmittance at a wavelength of 310 nm, the value of total light transmittance 2(%) is a value of total light transmittance at a wavelength of 350 nm, the value of total light transmittance 3(%) is a value of total light transmittance at a wavelength of 375 nm, the value of parallel light transmittance 1(%) is a value of parallel light transmittance at a wavelength of 500 nm, and the value of parallel light transmittance 2(%) is a value of parallel light transmittance at a wavelength of 700 nm. An ultraviolet blocking effect to ultraviolet rays having a wavelength of UVB is enhanced as the value of total light transmittance 1(%) becomes smaller, and an ultraviolet blocking effect to ultraviolet rays having a wavelength of UVA is enhanced as the values of total light transmittance 2(%) and total light transmittance 3(%) become smaller. Particularly, when the value of total light transmittance 3(%) is small, a blocking region to ultraviolet rays having a wavelength of UVA extends over a wider range. Visible light transparency is enhanced as the values of parallel light transmittance 1(%) and parallel light transmittance 2(%) become larger. 
     (Total Light Transmittance 4 and Haze) 
     The total light transmittance 4(%) and haze (%) in Table 1 are values obtained by measuring the prepared coating film using a haze meter HM-150 (manufactured by MURAKAMI COLOR RESEARCH LABORATORY CO., Ltd.). When coating films having comparable values of total light transmittance 4(%) are compared, those having a higher haze (%) have a higher effect of blurring a base (a so called soft focus effect). 
     (D50, D90, D10, D90/D10) 
     Herein, D50 (μm), D90 (μm) and D10 (μm) are values measured by a dynamic light scattering particle diameter distribution measuring device Nanotrack UPA-UT (manufactured by Nikkiso Co., Ltd.). The zinc oxide particles of each of examples and comparative examples were dispersed in water, and the dispersion was measured with the refractive index of zinc oxide set at 1.95 and the refractive index of water set at 1.309. D50 (μm) denotes a 50% cumulative particle diameter on the volume basis, D90 (μm) denotes a 90% cumulative particle diameter on the volume basis, and D10 (μm) denotes a 10% cumulative particle diameter on the volume basis. A ratio of D90/D10 is calculated as an indicator of sharpness of the particle size distribution. The particle size distribution broadens as the value becomes larger, while the particle size distribution sharpens as the value becomes smaller. 
     (Primary Particle Diameter) 
     The primary particle diameter in Tables 2 and 3 corresponds to a diameter of a sphere having the same surface area as a specific surface area determined by a BET method. That is, the primary particle diameter is a value determined according to the relational expression:
 
primary particle diameter(μm)=[6/( Sg ×ρ)]
 
     (Sg (m 2 /g): specific surface area, ρ (g/cm 3 ): true specific gravity of particle. 
     The specific surface area: Sg by the BET method was measured using a fully automatic BET specific surface area measuring device Macsorb (manufactured by Mountech Co., Ltd.), and the measurement value was used for the calculation described above. As the true specific gravity of particle: p, a value of the true specific gravity of zinc oxide, i.e.  5 . 6 , was used for the above calculation. 
     (Crystallite Diameter) 
     For the crystallite diameter (μm) in Tables 3, results of performing analysis using an X-ray diffractometer UltimaIII (manufactured by Rigaku Corporation) having an X-ray tube with copper are shown. The crystallite usually means a small single crystal in a microscopic level, which forms a crystalline substance. Herein, the crystallite diameter (m) is a value determined from a half width of a diffraction peak of the (101) plane of zinc oxide in the X-ray diffraction pattern of a hexagonal wurtzite-type zinc oxide particle. 
     (Crystallite Diameter/Primary Particle Diameter) 
     A value shown as crystallite diameter/primary particle diameter in Tables 3 is a value as an indicator of a level of independency of primary particles that form a powder. The primary particle diameter is a geometric particle diameter corresponding to a diameter of a sphere having the same surface area as a specific surface area determined by a BET method as described previously. On the other hand, the crystallite diameter is a value determined from a half width of a diffraction peak of the (101) plane of zinc oxide in the X-ray diffraction pattern as described previously. Therefore, as the value of crystallite diameter/primary particle diameter becomes closer to 1, a difference between the geometric particle diameter and the single crystal size decreases, which means that primary particles are not aggregated particles, but exist independently as single crystal particles. 
     (Oil Absorption) 
     The oil absorption was measured by the method described in Pigment Test Method-Oil Absorption in JIS K 5101-13-2. As an oil, isopropyl myristate (EXCEPARL IPM manufactured by Kao Corporation) was used in place of boiled linseed oil. 
     (BET Specific Surface Area) 
     The BET specific surface area (m 2 /g) is a value measured using a fully automatic BET specific area measuring device Macsorb (manufactured by Mountech Co., Ltd.), and corresponds to a specific surface area: Sg used for calculation of the primary particle diameter. 
     (Oil Absorption/BET Specific Surface Area) 
     The oil absorption/BET specific surface area (ml/100 m 2 ) is a value obtained by dividing the value of the oil absorption (ml/100 g) by the value of the BET specific surface area (m 2 /g), and as this value becomes smaller, the oil absorption per unit area of the particle surface is low, leading to reduced aggregation of particles and enhanced dispersibility of particles. 
     (Apparent Density) 
     The apparent density is a value measured by the method described in Pigment Test Method-Apparent Density or Apparent Specific Volume (Standing Method) in JIS K 5101-12-1. The volume of the powder decreases as the apparent density increases. 
     (Sharpened gloss (20° Gloss)) 
     Herein, the sharpened gloss (20° gloss) of the coating film is a value obtained by measuring the coating film using GLOSS METER GM-26D (manufactured by MURAKAMI COLOR RESEARCH LABORATORY CO., Ltd.), and is a value of glossiness at an incidence angle of 20°. A larger value of sharpened gloss (20° gloss) corresponds to reduced aggregation and enhanced dispersibility of zinc oxide particles in the prepared coating film. 
     Example 1 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 266.07 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 1 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 100° C. over 60 minutes with stirring, and aged at 100° C. for 7 hours with stirring. After aging, the slurry was quenched immediately, then filtered and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to forma slurry, and the slurry was heated to 100° C. over 60 minutes with stirring, and heated and washed at 100° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal plate-shaped zinc oxide particles having a primary particle diameter of 1.12 μm. The size and form of the obtained particles were observed with a scanning electron microscope (SEM, JSM-5600, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 1 . Further, an observation was made with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 2 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Example 2 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 266.07 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 1 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 100° C. over 60 minutes with stirring, and aged at 100° C. for 3 hours with stirring. After aging, the slurry was quenched immediately, then filtered and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to forma slurry, and the slurry was heated to 100° C. over 60 minutes with stirring, and heated and washed at 100° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal plate-shaped zinc oxide particles having a primary particle diameter of 0.53 μm. The size and form of the obtained particles were observed with a scanning electron microscope (SEM, JSM-5600, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 3 . Further, an observation was made with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 4 . Further, the X-ray diffraction spectrum of the obtained particles is shown in  FIG. 5 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Example 3 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 266.07 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 1 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 100° C. over 60 minutes with stirring, and aged at 100° C. for 1 hour with stirring. After aging, the slurry was quenched immediately, then filtered and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to forma slurry, and the slurry was heated to 100° C. over 60 minutes with stirring, and heated and washed at 100° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal plate-shaped zinc oxide particles having a primary particle diameter of 0.30 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 6 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 7 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Example 4 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 133.02 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.5 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 100° C. over 60 minutes with stirring, and aged at 100° C. for 3 hours with stirring. After aging, the slurry was quenched immediately, then filtered and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to forma slurry, and the slurry was heated to 100° C. over 60 minutes with stirring, and heated and washed at 100° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal plate-shaped zinc oxide particles having a primary particle diameter of 0.11 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 8 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 9 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. The crystallite diameter of the plate-shaped surface; (002) plane is 0.07 μm. 
     Example 5 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 133.02 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.5 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 70° C. over 42 minutes with stirring, and aged at 70° C. for 3 hours with stirring. After aging, the slurry was quenched immediately, then filtered and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 70° C. over 42 minutes with stirring, and heated and washed at 70° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal plate-shaped zinc oxide particles having a primary particle diameter of 0.11 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 10 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 11 . Further, the X-ray diffraction spectrum of the obtained particles is shown in  FIG. 12 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. The crystallite diameter of the plate-shaped surface; (002) plane is 0.07 μm. 
     Comparative Example 1 
     Fine zinc oxide (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.11 μm) was evaluated in the same manner as in the examples. The electron microscope photograph is shown in  FIG. 13 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Comparative Example 2 
     In 1200 ml of water, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped to form a slurry. Subsequently, the slurry was heated to 100° C. over 60 minutes with stirring, and aged at 100° C. for 3 hours with stirring. After aging, the slurry was quenched immediately, then filtered, washed with water, and dried at 110° C. for 12 hours to obtain indefinite-shaped zinc oxide particles having a primary particle diameter of 0.02 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 14 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Comparative Example 3 
     In an alumina crucible (length/width/height=100 mm/100 mm/35 mm) was put 10 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm), and left standing and calcinated at 675° C. for 2 hours in an electric muffle furnace (manufactured by TOYO ENGINEERING WORKS, LTD.) to obtain indefinite-shaped zinc oxide particles having a primary particle diameter of 0.30 μm. The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Comparative Example 4 
     FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was evaluated in the same manner as in the examples. The electron microscope photograph is shown in  FIG. 15 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     Comparative Example 5 
     FINEX-30 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.04 μm) was evaluated in the same manner as in the examples. The electron microscope photograph is shown in  FIG. 16 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 1. 
     
       
         
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                   
                   
                   
                   
                   
                 Compar- 
                 Compar- 
                 Compar- 
                 Compar- 
                 Compar- 
               
               
                   
                   
                   
                   
                   
                   
                 ative 
                 ative 
                 ative 
                 ative 
                 ative 
               
               
                   
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
               
               
                   
                 ple 1 
                 ple 2 
                 ple 3 
                 ple 4 
                 ple 5 
                 ple 1 
                 ple 2 
                 ple 3 
                 ple 4 
                 ple 5 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Prepara- 
                 Zinc oxide fine 
                 FINEX- 
                 FINEX- 
                 FINEX- 
                 FINEX- 
                 FINEX- 
                 Fine zinc 
                 FINEX- 
                 FINEX- 
                 FINEX- 
                 FINEX- 
               
               
                 tion 
                 particles 
                 50 
                 50 
                 50 
                 50 
                 50 
                 oxide 
                 50 
                 50 
                 50 
                 30 
               
               
                 condi- 
                 as raw material 
               
               
                 tions 
                 Particle diameter of 
                 0.02 
                 0.02 
                 0.02 
                 0.02 
                 0.02 
                 0.11 
                 0.02 
                 0.02 
                 0.02 
                 0.04 
               
               
                   
                 raw material (μm) 
               
               
                   
                 Amount of raw material 
                 80 
                 80 
                 80 
                 80 
                 80 
                   
                 80 
                 10 
               
               
                   
                 used in preparation (g) 
               
               
                   
                 Zinc salt used in 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
               
               
                   
                 preparation 
                 acetate 
                 acetate 
                 acetate 
                 acetate 
                 acetate 
               
               
                   
                   
                 dihy- 
                 dihy- 
                 dihy- 
                 dihy- 
                 dihy- 
               
               
                   
                   
                 drate 
                 drate 
                 drate 
                 drate 
                 drate 
               
               
                   
                 Amount of zinc salt (g) 
                 266.07 
                 266.07 
                 266.07 
                 133.02 
                 133.02 
               
               
                   
                 Solvent used in 
                 Water 
                 Water 
                 Water 
                 Water 
                 Water 
                   
                 Water 
               
               
                   
                 preparation 
               
               
                   
                 Amount of aqueous zinc 
                 1200 
                 1200 
                 1200 
                 1200 
                 1200 
                   
                 1200 
               
               
                   
                 salt solution (ml) 
               
               
                   
                 Concentration of aqueous 
                 1 
                 1 
                 1 
                 0.5 
                 0.5 
               
               
                   
                 zinc salt solution (mol/l) 
               
               
                   
                 Aging temperature (° C.) 
                 100 
                 100 
                 100 
                 100 
                 70 
                   
                 100 
               
               
                   
                 Aging time (Hr) 
                 7 
                 3 
                 1 
                 3 
                 3 
                   
                 3 
               
               
                   
                 Calcinating temperature/ 
                   
                   
                   
                   
                   
                   
                   
                 675° 
               
               
                   
                 calcinating time 
                   
                   
                   
                   
                   
                   
                   
                 C./2 Hr 
               
               
                 Phys- 
                 Composition of obtained 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
               
               
                 ical 
                 particles 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
               
               
                 proper- 
                 Particle shape 
                 Hexag- 
                 Hexag- 
                 Hexag- 
                 Hexag- 
                 Hexag- 
                 Indefinite 
                 Indefinite 
                 Indefinite 
                 Indefinite 
                 Indefinite 
               
               
                 ties of 
                   
                 onal 
                 onal 
                 onal 
                 onal 
                 onal 
                 shape 
                 shape 
                 shape 
                 shape 
                 shape 
               
               
                 par- 
                   
                 plate 
                 plate 
                 plate 
                 plate 
                 plate 
               
               
                 ticles 
                   
                 shape 
                 shape 
                 shape 
                 shape 
                 shape 
               
               
                   
                 Primary particle 
                 1.12 
                 0.53 
                 0.30 
                 0.11 
                 0.11 
                 0.11 
                 0.02 
                 0.30 
                 0.02 
                 0.04 
               
               
                   
                 diameter (μm) 
               
               
                   
                 Crystallite diameter 
                   
                   
                   
                 0.07 
                 0.07 
               
               
                   
                 (μm) 
               
               
                   
                 Crystalllite diameter/ 
                   
                   
                   
                 0.64 
                 0.64 
               
               
                   
                 primary particle diameter 
               
               
                   
                 Aspect ratio 
                 3.4 
                 3.6 
                 3.7 
                 3.4 
                 3.5 
                   
                   
                   
                 1.8 
                 2.0 
               
               
                   
                 Powder touch 
                 5 
                 4 
                 3 
                 3 
                 3 
                 2 
                   
                 2 
                 1 
                 1 
               
               
                 Phys- 
                 Total light 
                   
                 43 
                 19 
                 12 
                 13 
                 20 
                   
                 41 
                 15 
                 13 
               
               
                 ical 
                 transmittance 1 (%) 
               
               
                 proper- 
                 Total light 
                   
                 41 
                 16 
                 9 
                 10 
                 17 
                   
                 37 
                 16 
                 13 
               
               
                 ties of 
                 transmittance 2 (%) 
               
               
                 coating 
                 Total light 
                   
                 43 
                 18 
                 10 
                 11 
                 15 
                   
                 32 
                 54 
                 24 
               
               
                 film 
                 transmittance 3 (%) 
               
               
                   
                 Parallel light 
                   
                 20 
                 17 
                 54 
                 55 
                 53 
                   
                 37 
                 85 
                 78 
               
               
                   
                 transmittance 1 (%) 
               
               
                   
                 Parallel light 
                   
                 47 
                 49 
                 81 
                 83 
                 79 
                   
                 63 
                 93 
                 90 
               
               
                   
                 transmittance 2 (%) 
               
               
                   
                 Total light 
                 85 
                 83 
                 77 
                 80 
                 80 
                 81 
                   
                 78 
               
               
                   
                 transmittance 4 (%) 
               
               
                   
                 Haze (%) 
                 61 
                 63 
                 63 
                 27 
                 27 
                 26 
                   
                 58 
               
               
                   
               
             
          
         
       
     
     Example 6 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 66.51 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.25 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 100° C. over 60 minutes with stirring, and aged at 100° C. for 7 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 100° C. over 60 minutes with stirring, and heated and washed at 100° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal prism-shaped zinc oxide particles having a primary particle diameter of 0.10 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 21 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 22 . Further, the X-ray diffraction spectrum of the obtained particles is shown in  FIG. 23 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Example 7 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 133.02 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.5 mol/l in terms of zinc acetate dihydrate, 80 g of SF-15 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.08 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 70° C. over 42 minutes with stirring, and aged at 70° C. for 3 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 70° C. over 42 minutes with stirring, and heated and washed at 70° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal prism-shaped zinc oxide particles having a primary particle diameter of 0.19 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 24 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 25 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Example 8 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 106.42 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.4 mol/l in terms of zinc acetate dihydrate, 80 g of SF-15 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.08 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 70° C. over 42 minutes with stirring, and aged at 70° C. for 5 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 70° C. over 42 minutes with stirring, and heated and washed at 70° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal prism-shaped zinc oxide particles having a primary particle diameter of 0.13 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 26 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 27 . The size and form of the obtained particles were observed with a scanning electron microscope (SEM, JSM-7000F, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 28 . Further, the X-ray diffraction spectrum of the obtained particles is shown in  FIG. 29 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Example 9 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 106.42 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.4 mol/l in terms of zinc acetate dihydrate, 80 g of SF-15 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.08 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 90° C. over 54 minutes with stirring, and aged at 90° C. for 7 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 90° C. over 54 minutes with stirring, and heated and washed at 90° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal prism-shaped zinc oxide particles having a primary particle diameter of 0.15 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 30 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 31 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Example 10 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 106.42 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.4 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-30 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.04 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 70° C. over 42 minutes with stirring, and aged at 70° C. for 3 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 70° C. over 42 minutes with stirring, and heated and washed at 70° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain hexagonal prism-shaped zinc oxide particles having a primary particle diameter of 0.11 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 32 . Further, an electron microscope photograph with a higher magnification is shown in  FIG. 33 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Comparative Example 1 
     Fine zinc oxide (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.11 μm) was evaluated in the same manner as in examples. The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Comparative Example 6 
     In an alumina crucible (length/width/height=100 mm/100 mm/35 mm) was put 10 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm), and left standing and calcinated at 525° C. for 2 hours in an electric muffle furnace (manufactured by TOYO ENGINEERING WORKS, LTD.) to obtain indefinite-shaped zinc oxide particles having a primary particle diameter of 0.10 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 34 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     Comparative Example 4 
     FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm) was evaluated in the same manner as in the examples. The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 2. 
     
       
         
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Exam- 
                 Compar. 
                 Compar. 
                 Compar. 
               
               
                   
                 ple 6 
                 ple 7 
                 ple 8 
                 ple 9 
                 ple 10 
                 Ex. 1 
                 Ex. 6 
                 Ex. 4 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Preparation 
                 Zinc oxide fine 
                 FINEX-50 
                 SF-15 
                 SF-15 
                 SF-15 
                 FINEX-30 
                 Fine zinc 
                 FINEX-50 
                 FINEX-50 
               
               
                 conditions 
                 particles 
                   
                   
                   
                   
                   
                 oxide 
               
               
                   
                 as raw material 
               
               
                   
                 Particle diameter of 
                 0.02 
                 0.08 
                 0.08 
                 0.08 
                 0.04 
                 0.11 
                 0.02 
                 0.02 
               
               
                   
                 raw material (μm) 
               
               
                   
                 Amount of raw 
                 80 
                 80 
                 80 
                 80 
                 80 
               
               
                   
                 material used in 
               
               
                   
                 preparation (g) 
               
               
                   
                 Zinc salt used in 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
               
               
                   
                 preparation 
                 acetate 
                 acetate 
                 acetate 
                 acetate 
                 acetate 
               
               
                   
                   
                 dihydrate 
                 dihydrate 
                 dihydrate 
                 dihydrate 
                 dihydrate 
               
               
                   
                 Amount of zinc salt 
                 66.51 
                 133.02 
                 106.42 
                 106.42 
                 106.42 
               
               
                   
                 (g) 
               
               
                   
                 Solvent used in 
                 Water 
                 Water 
                 Water 
                 Water 
                 Water 
               
               
                   
                 preparation 
               
               
                   
                 Amount of zinc salt 
                 1200 
                 1200 
                 1200 
                 1200 
                 1200 
               
               
                   
                 solution (ml) 
               
               
                   
                 Concentration of 
                 0.25 
                 0.5 
                 0.4 
                 0.4 
                 0.4 
               
               
                   
                 zinc salt solution 
               
               
                   
                 (mol/l) 
               
               
                   
                 Aging temperature 
                 100 
                 70 
                 70 
                 90 
                 70 
               
               
                   
                 (° C.) 
               
               
                   
                 Aging time (Hr) 
                 7 
                 3 
                 5 
                 7 
                 3 
               
               
                   
                 Calcinating 
                   
                   
                   
                   
                   
                   
                 525° C./2 Hr 
               
               
                   
                 temperature/calcinat- 
               
               
                   
                 ing time 
               
               
                 Physical 
                 Composition of 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
               
               
                 properties 
                 obtained particles 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
               
               
                 of particles 
                 Particle shape 
                 Hexagonal 
                 Hexagonal 
                 Hexagonal 
                 Hexagonal 
                 Hexagonal 
                 Indefinite 
                 Indefinite 
                 Indefinite 
               
               
                   
                   
                 prism 
                 prism 
                 prism 
                 prism 
                 prism 
                 shape 
                 shape 
                 shape 
               
               
                   
                   
                 shape 
                 shape 
                 shape 
                 shape 
                 shape 
               
               
                   
                 Primary particle 
                 0.10 
                 0.19 
                 0.13 
                 0.15 
                 0.11 
                 0.11 
                 0.10 
                 0.02 
               
               
                   
                 diameter (μm) 
               
               
                   
                 D50 (μm) 
                 0.18 
                 0.40 
                 0.20 
                 0.19 
                 0.15 
                 0.23 
                 0.17 
                 0.14 
               
               
                   
                 D90 (μm) 
                 0.24 
                 0.54 
                 0.25 
                 0.27 
                 0.21 
                 0.41 
                 0.37 
                 0.41 
               
               
                   
                 D10 (μm) 
                 0.13 
                 0.25 
                 0.15 
                 0.13 
                 0.10 
                 0.17 
                 0.09 
                 0.05 
               
               
                   
                 D90/D10 
                 1.92 
                 2.16 
                 1.67 
                 2.09 
                 2.09 
                 2.47 
                 4.05 
                 7.39 
               
               
                   
                 Aspect ratio 
                 1.4 
                 1.6 
                 1.2 
                 1.4 
                 1.3 
                 2.1 
                 1.9 
                 1.8 
               
               
                 Physical 
                 Total light 
                 14 
                 20 
                 12 
                 16 
                 15 
                 20 
                 15 
                 15 
               
               
                 properties of 
                 transmittance 1 (%) 
               
               
                 coating film 
                 Total light 
                 12 
                 18 
                 10 
                 14 
                 15 
                 17 
                 14 
                 16 
               
               
                   
                 transmittance 2 (%) 
               
               
                   
                 Total light 
                 15 
                 23 
                 10 
                 11 
                 15 
                 19 
                 18 
                 54 
               
               
                   
                 transmittance 3 (%) 
               
               
                   
                 Parallel light 
                 71 
                 63 
                 56 
                 55 
                 65 
                 53 
                 57 
                 85 
               
               
                   
                 transmittance 1 (%) 
               
               
                   
                 Parallel light 
                 90 
                 85 
                 81 
                 80 
                 86 
                 79 
                 81 
                 93 
               
               
                   
                 transmittance 2 (%) 
               
               
                   
               
             
          
         
       
     
     Example 11 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 66.51 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.25 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., primary particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 70° C. over 42 minutes with stirring, and aged at 70° C. for 3 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 70° C. over 42 minutes with stirring, and heated and washed at 70° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain zinc oxide particles having a primary particle diameter of 0.046 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 35 . Further, the X-ray diffraction spectrum of the obtained particles is shown in  FIG. 36 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 3. 
     Example 12 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 93.12 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.35 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., primary particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 90° C. over 54 minutes with stirring, and aged at 90° C. for 3 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 90° C. over 54 minutes with stirring, and heated and washed at 90° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain zinc oxide particles having a primary particle diameter of 0.074 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 37 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 3. 
     Example 13 
     In 1200 ml of an aqueous zinc acetate solution prepared by dissolving 26.61 g of zinc acetate dihydrate (zinc acetate manufactured by Hosoi Chemical Industry Co., Ltd.) in water so as to have a concentration of 0.10 mol/l in terms of zinc acetate dihydrate, 80 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., primary particle diameter: 0.02 μm) was repulped, thereby forming a slurry. Subsequently, the slurry was heated to 70° C. over 84 minutes with stirring, and aged at 70° C. for 3 hours with stirring. After aging, the slurry was filtered, and washed with water. Subsequently, the obtained solid was repulped in 3 liters of water to form a slurry, and the slurry was heated to 70° C. over 84 minutes with stirring, and heated and washed at 70° C. for 30 minutes with stirring. After heating and washing, the slurry was filtered, washed with water, and dried at 110° C. for 12 hours to obtain zinc oxide particles having a primary particle diameter of 0.045 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 38 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 3. 
     Comparative Example 5 
     FINEX-30 (manufactured by Sakai Chemical Industry Co., Ltd., primary particle diameter: 0.04 μm) was evaluated in the same manner as in the examples. The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 3. 
     Comparative Example 7 
     In an alumina crucible (length/width/height=100 mm/100 mm/35 mm) was put 10 g of FINEX-50 (manufactured by Sakai Chemical Industry Co., Ltd., particle diameter: 0.02 μm), and left standing and calcinated at 500° C. for 2 hours in an electric muffle furnace (manufactured by TOYO ENGINEERING WORKS, LTD.) to obtain zinc oxide particles having a primary particle diameter of 0.083 μm. The size and form of the obtained particles were observed with a transmission electron microscope (TEM, JEM-1200EX II, manufactured by JEOL Ltd.). The obtained electron microscope photograph is shown in  FIG. 39 . The results of evaluating the physical properties of the obtained particles and the physical properties of the coating film are shown in Table 3. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 3 
               
               
                   
                   
               
               
                   
                 Exam- 
                 Exam- 
                 Exam- 
                 Comparative 
                 Comparative 
               
               
                   
                 ple 11 
                 ple 12 
                 ple 13 
                 Example 5 
                 Example 7 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Preparation 
                 Zinc oxide fine particles 
                 FINEX-50 
                 FINEX-50 
                 FINEX-50 
                 FINEX-30 
                 FINEX-50 
               
               
                 conditions 
                 as raw material 
               
               
                   
                 Particle diameter of 
                 0.02 
                 0.02 
                 0.02 
                 0.04 
                 0.02 
               
               
                   
                 raw material (μm) 
               
               
                   
                 Amount of raw material 
                 80 
                 80 
                 80 
               
               
                   
                 used in preparation (g) 
               
               
                   
                 Zinc salt used in 
                 Zinc 
                 Zinc 
                 Zinc 
               
               
                   
                 preparation 
                 acetate 
                 acetate 
                 acetate 
               
               
                   
                   
                 dihydrate 
                 dihydrate 
                 dihydrate 
               
               
                   
                 Amount of zinc salt (g) 
                 66.51 
                 93.12 
                 26.61 
               
               
                   
                 Solvent used in 
                 Water 
                 Water 
                 Water 
               
               
                   
                 preparation 
               
               
                   
                 Amount of zinc salt 
                 1200 
                 1200 
                 1200 
               
               
                   
                 solution (ml) 
               
               
                   
                 Concentration of zinc 
                 0.25 
                 0.35 
                 0.10 
               
               
                   
                 salt solution (mol/l) 
               
               
                   
                 Aging temperature (° C.) 
                 70 
                 90 
                 70 
               
               
                   
                 Aging time (Hr) 
                 3 
                 3 
                 3 
               
               
                   
                 Calcinating temperature/ 
                   
                   
                   
                   
                 500° C./2 Hr 
               
               
                   
                 calcinating time 
               
               
                 Physical 
                 Composition of 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
                 Zinc 
               
               
                 properties 
                 obtained particles 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
                 oxide 
               
               
                 of particles 
                 Primary particle diameter 
                 0.046 
                 0.074 
                 0.045 
                 0.044 
                 0.083 
               
               
                   
                 (μm) 
               
               
                   
                 Crystallite diameter (μm) 
                 0.036 
                 0.057 
                 0.032 
                 0.031 
                 0.054 
               
               
                   
                 Crystallite diameter/ 
                 0.78 
                 0.77 
                 0.71 
                 0.70 
                 0.65 
               
               
                   
                 primary particle diameter 
               
               
                   
                 Aspect ratio 
                 1.3 
                 1.4 
                 1.4 
                 2.0 
                 1.8 
               
               
                   
                 BET specific 
                 23.1 
                 14.5 
                 23.6 
                 24.3 
                 12.9 
               
               
                   
                 surface area (m 2 /g) 
               
               
                   
                 Oil absorption (ml/100 g) 
                 26 
                 18 
                 27 
                 43 
                 34 
               
               
                   
                 Oil absorption/BET 
                 1.13 
                 1.24 
                 1.14 
                 1.77 
                 2.63 
               
               
                   
                 specific surface area 
               
               
                   
                 (ml/100 m 2 ) 
               
               
                   
                 Apparent density (g/ml) 
                 0.53 
                 0.66 
                 0.49 
                 0.13 
                 0.16 
               
               
                 Physical 
                 Total light 
                 14 
                 16 
                 10 
                 13 
                 16 
               
               
                 properties of 
                 transmittance 1 (%) 
               
               
                 coating film 
                 Total light 
                 13 
                 15 
                 11 
                 13 
                 15 
               
               
                   
                 transmittance 2 (%) 
               
               
                   
                 Parallel light 
                 84 
                 78 
                 89 
                 78 
                 76 
               
               
                   
                 transmittance 1 (%) 
               
               
                   
                 Parallel light 
                 93 
                 92 
                 97 
                 90 
                 87 
               
               
                   
                 transmittance 2 (%) 
               
               
                   
                 Sharpened gloss 
                 148 
                 143 
                 151 
                 109 
                 99 
               
               
                   
                 (20° gloss) 
               
               
                   
               
             
          
         
       
     
     INDUSTRIAL APPLICABILITY 
     The method for production of zinc oxide particles of the present invention can be used as a production method of zinc oxide particles which can be used for various applications such as a cosmetic, a heat releasing filler, and so on.