Abstract:
The present invention relates to a method for manufacturing a light-emitting diode package, and more specifically to a method for manufacturing a light-emitting diode package that does not need an additional colour conversion frit heat-treatment process and cutting process after bonding between the colour conversion frit and a light-emitting diode chip. To this end, the present invention provides a method for manufacturing a light-emitting diode package chatacterized in that the present invention comprises: a colour conversion frit formation step for forming a colour conversion frit in which phosphor is included on a substrate; a colour conversion frit transcription step for transcribing the colour conversion frit formed on the substrate from the substrate to a transcription film; and a colour conversion frit bonding step for bonding the colour conversion frit transcribed on the transcription film onto a light-emitting diode package.

Description:
BACKGROUND OF THE INVENTION 
       [0001]    Field of the Invention 
         [0002]    The present invention relates to a method of fabricating a light-emitting diode (LED) package. More particularly, the present invention relates to a method of fabricating an LED package that does not require an additional heat treatment or cutting process on a color conversion frit after bonding the color conversion frit to an LED chip. 
         [0003]    Description of Related Art 
         [0004]    A light emitting diode (LED) is a semiconductor device formed of a compound such as gallium arsenide (GaAs) to emit light in response to an electrical current applied thereto. The LED uses a p-n junction semiconductor structure into which minority carriers, such as electrons or holes, are injected, such that light is generated by the recombination of electrons and holes. 
         [0005]    The characteristics of LEDs include low power consumption, a relatively long lifespan, the ability to be mounted in cramped spaces, and strong resistance to vibrations. While LEDs are used in display devices and the backlight units of display devices, studies into applying LEDs to general lighting devices have been recently undertaken. In addition to monochromatic LEDs, such as red, blue, or green LEDs, white LEDs have also come onto the market. In particular, a sharp increase in demand for white LEDs is expected, since white LEDs can be applied to vehicle lighting devices and general lighting apparatuses. 
         [0006]    In the field of LED technology, white light is commonly generated using two main methods. The first method to generate white light includes disposing monochromatic LEDs, such as red, green, and blue LEDs, adjacently to each other such that various colors of light emitted by the monochromatic LEDs are mixed. However, color tones may change depending on the environment in which such devices are used, since individual monochromatic LEDs have different thermal or temporal characteristics. In particular, color stains may occur, making it difficult to uniformly mix different colors of light. The second method to generate white light includes applying a fluorescent material to surfaces of an LED and mixing a portion of light initially emitted by the LED and secondary light wavelength-converted by the fluorescent material. For example, a fluorescent material generating yellowish-green or yellow light may be used as a light excitation source on a blue LED, whereby white light can be produced by mixing blue light emitted by the blue LED and yellowish-green or yellow excitation light from the fluorescent material. At present, the second method of realizing white light utilizing a blue LED and a fluorescent material is generally used. 
         [0007]    The fluorescent material for producing white light in cooperation with the blue LED chip can be used mixed with a frit. In the related art, in order to directly bond the mixture of the frit and the fluorescent material to the LED chip, the mixture of the frit and the fluorescent material has been formed into a paste, followed by coating the LED chip with the mixture of the frit and the fluorescent material and subsequent sintering. However, the sintering temperature is commonly 500° C. or above, and the LED chip that is thermally stable at 200° C. or below cannot withstand such a sintering temperature. That is, sintering the mixture of the frit and the fluorescent material at such a temperature will degrade LED chips, which is problematic. In addition, a heat treatment, such as sintering, performed after the operation of coating the LED chip with the mixture of the frit and the fluorescent material may cause a problem. For example, a base substrate, i.e. a GaN substrate, on which a plurality of LEDs is formed, may be warped. When a GaN substrate is warped in this manner, none of the plurality of LED chips formed on the GaN substrate can be used. Although a fluorescent mixture able to be sintered at a low temperature may be used in order to overcome the degradation problem, other problems, such as peeling or fracturing, may occur in the process of cutting the plurality of LED chips. 
         [0008]    Related Art Document 
         [0009]    Patent Document 1: United States Patent Application Publication No. US2013/0026461 (Jan. 31, 2013) 
       BRIEF SUMMARY OF THE INVENTION 
       [0010]    Various aspects of the present invention provide a method of fabricating an LED package that does not require an additional heat treatment or cutting process on a color conversion frit after bonding the color conversion frit to a light-emitting diode (LED) chip. 
         [0011]    According to an aspect of the present invention, a method of fabricating an LED package includes: forming a color conversion frit containing a fluorescent material on a substrate; transferring the color conversion frit formed on the substrate to a transfer film; and bonding the color conversion frit on the transfer film to an LED chip. 
         [0012]    According to an embodiment of the present invention, the process of forming the color conversion frit may include: coating the substrate with the color conversion frit; and sintering the color conversion frit coating the substrate. 
         [0013]    The process of coating the substrate may coat the substrate with the color conversion frit in a size corresponding to the size of the LED chip. 
         [0014]    The process of coating the substrate may pattern the color conversion frit in a shape corresponding to the shape of a plurality of the LEDs. 
         [0015]    The substrate may be implemented as a boron nitride substrate or a graphite substrate. 
         [0016]    At the process of transferring the color conversion frit, the transfer film may be implemented as a pressure sensitive adhesive film. 
         [0017]    The process of bonding the color conversion frit may bond the color conversion frit and the LED chip by means of an adhesive. 
         [0018]    The LED chip may be implemented as a blue LED chip, and the fluorescent material may convert a portion of light emitted by the blue LED chip into yellow light. 
         [0019]    In addition, the method may further include removing the transfer film from the color conversion frit after the process of bonding the color conversion frit to the LED chip. 
         [0020]    Furthermore, the method may further include mounting the LED chip onto a package substrate after the process of removing the transfer film. 
         [0021]    According to the present invention as set forth above, a substrate is coated with an intended pattern of a color conversion frit that generates white light from an LED, and the color conversion frit is sintered. Afterwards, the color conversion frit is transferred to a transfer film, and subsequently is bonded to an LED chip. Accordingly, after the color conversion frit is bonded to the LED chip, an additional heat treatment or cutting process on the color conversion frit is not required. 
         [0022]    In other words, according to the present invention, since the process of forming the color conversion frit on the LED chips is completed with the bonding of the color conversion frit to the LED chips, it is possible to fundamentally prevent a base substrate on which the LED chips are formed from being warped by a heat treatment of the related art or cracks from occurring in the color conversion frit during a cutting operation of dividing the color conversion frit according to the LED chips. Accordingly, it is possible to simplify the process of fabricating an LED package while minimizing the occurrence of defects. 
         [0023]    In addition, according to the present invention, it is possible to form a color conversion frit in an intended size without restriction on the size of LED chips by patterning the color conversion frit according to the size of LEDs by screen printing or spraying before bonding the color conversion frit to the LED chips. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0024]      FIG. 1  is a flowchart illustrating a method of fabricating an LED package according to an exemplary embodiment of the present invention; and 
           [0025]      FIG. 2  to  FIG. 8  are schematic views sequentially illustrating the operations in the method of fabricating an LED package according to the exemplary embodiment of the present invention. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0026]    Reference will now be made in detail to a method of fabricating a light-emitting diode (LED) package according to the present invention, examples of which are illustrated in the accompanying drawings and described below, so that a person skilled in the art to which the present invention relates could easily put the present invention into practice. 
         [0027]    Throughout this document, reference should be made to the drawings, in which the same reference numerals and symbols will be used throughout the different drawings to designate the same or like components. In the following description of the present invention, detailed descriptions of known functions and components incorporated herein will be omitted in the case that the subject matter of the present invention is rendered unclear. 
         [0028]    Referring to  FIG. 1 , a method of fabricating an LED package according to an exemplary embodiment of the present invention is a method of fabricating a white LED package ( 200  in  FIG. 8 ). The method of fabricating an LED package includes color conversion frit forming step S 1 , color conversion frit transfer step S 2 , and color conversion frit bonding step S 3 . 
         [0029]    Referring to  FIG. 2  and  FIG. 3 , the color conversion frit forming step S 1  is the step of forming a color conversion frit  100  containing a fluorescent material on a substrate  110 . Here, the fluorescent material is a material that generates wavelength-converted light, i.e. fluorescent light, by converting the wavelength of light emitted by an LED chip (i.e. an LED chip of a plurality of LED chips  130  illustrated in  FIG. 6 ). According to the present embodiment, the LED chip is implemented as a blue LED. In order to generate white light by light mixing with blue light emitted by the blue LED, a fluorescent material that converts the wavelength of a portion of light emitted by the blue LED may be mixed with frit powder to form the color conversion frit  100 . The fluorescent material is mixed with the frit powder, and the mixture is dispersed in a solvent, thereby forming a paste of the color conversion frit  100 . It is preferable that the fluorescent material be formed of a material having superior dispersibility. In addition, it is more preferable that the fluorescent material be formed of a material having superior long-term reliability. 
         [0030]    In order to form the color conversion frit  100  containing the fluorescent material on the substrate  110 , the color conversion frit forming step S 1  may include coating and sintering processes. 
         [0031]    First, in the coating process, the substrate  110  is coated with the paste of the color conversion frit  100 . In the coating process, the substrate  110  is coated with the color conversion frit  100  in a size corresponding to the size of the plurality of LED chips ( 130  in  FIG. 6 ). Specifically, the substrate  110  is coated with the color conversion frit  100  in an area and shape corresponding to the top surfaces of the plurality of LED chips  130 , i.e. the bonding surfaces of the plurality of LED chips  130  to which the color conversion frit  100  will be bonded in a subsequent process. 
         [0032]    As illustrated in  FIG. 6 , according to the present invention, the plurality of LED chips  130  is provided on a base substrate  130   a . In the coating process, the color conversion frit  100  is patterned on the substrate  110  in the shape corresponding to the shape of the plurality of LED chips  130 . For example, the coating process may include preparing a mask having a pattern corresponding to the plurality of LED chips  130  and coating the substrate  110  with an intended pattern of the color conversion frit  100  using the mask. The coating may be screen printing, or may include spraying the color conversion frit  100  onto the substrate  110  after placing the mask on the substrate  110 . When the color conversion frit  100  is patterned in the shape corresponding to the shape of the plurality of LED chips  130 , the operation of cutting the color conversion frit  100  into unit pieces is not required in the process of cutting the plurality of LED chips  130  into individual LED chips, since the color conversion frit  100  is patterned, i.e. divided, according to each of the plurality of LED chips  130 . It is therefore possible to prevent the problem of peeling or fracturing that would otherwise occur in the process of cutting a color conversion frit in the related art. In addition, since the mask can be fabricated according to the size of the plurality of LED chips  130  without restriction on the size of the LED chips  130 , it is possible to form the color conversion frit  100  in an intended size. 
         [0033]    The substrate  110  used in the formation of the color conversion frit  100  is a backing that supports the color conversion frit  100  coating the substrate  110  during the subsequent process of sintering the color conversion frit  100 . According to the present embodiment, the substrate  110  may be implemented as a boron nitride (BN) substrate or a graphite substrate. 
         [0034]    Afterwards, in the sintering process, the color conversion frit  100  coating the substrate  110  is sintered. When the manufacture of the color conversion frit  100  in the shape of a thin film or substrate is completed before the color conversion frit bonding step S 3  that will proceed as a subsequent process, no heat treatment follows after the color conversion frit bonding step S 3 . This can consequently prevent a problem, such as degradation of the LED chips  130  or warping of the base substrate  130   a  on which the plurality of LED chips  130  is formed, which would otherwise be caused by the sintering heat treatment of the color conversion frit  100 . 
         [0035]    After that, referring to  FIG. 4  and  FIG. 5 , the color conversion frit transfer step S 2  is the step of transferring the color conversion frit  100  formed on the substrate  110  to a transfer film  120 . Specifically, at the color conversion frit transfer step S 2 , the transfer film  120  is placed above the color conversion frit  100  formed on the substrate  110 , is moved downwardly such that the transfer film  120  comes into contact with the color conversion frit  100 , and subsequently the transfer film  120  is moved upwardly. In order to improve the ratio of the transfer of the color conversion frit  100  to the transfer film  120 , the transfer film  120  may be heated or rubbed with a roller while the transfer film  120  is kept in contact with the color conversion frit  100 . 
         [0036]    Through this process, the color conversion frit  100  formed on the substrate  110  is removed from the surface of the substrate  110 , and is transferred to the surface of the transfer film  120  in the shape formed on the substrate  110 . According to the present embodiment, the transfer film  120  for transferring the color conversion frit  100  may be implemented as a pressure sensitive adhesive (PSA) film. 
         [0037]    Thereafter, the color conversion frit bonding step S 3  is the step of bonding the color conversion frit  100  transferred to the transfer film  120  to the plurality LED chips  130 . At the color conversion frit bonding step S 3 , the color conversion frit  100  is bonded to the plurality LED chips  130  by means of an adhesive. Specifically, after the adhesive is applied to the bonding surfaces of the plurality LED chips  130 , the color conversion frit  100  is bonded to the applied adhesive. 
         [0038]    As illustrated in  FIG. 6 , the plurality LED chips  130  provided according to the present embodiment may be formed on the base substrate  130   a  formed as a GaN substrate. Each of the plurality LED chips  130  is a light source emitting light in response to current applied thereto, formed as a forward junction of an n-semiconductor layer that provides electrons and a p-semiconductor layer that provides holes. In addition, the LED chip  130  provided according to the present embodiment is implemented as a blue LED to emit blue light. A portion of the emitted blue light is wavelength-converted into yellow light by the fluorescent material contained in the color conversion frit  100  disposed on a path along which the light radiates outward. That is, an LED package ( 200  in  FIG. 8 ) fabricated according to the present embodiment generates white light by mixing the blue light emitted by the blue LED chip  130  with the yellow light wavelength-converted by the fluorescent material contained in the color conversion frit  100 . In addition, the LED chip  130  provided according to the present embodiment may be implemented as a flip chip. Accordingly, the LED chip  130  may have electrodes ( 131  in  FIG. 8 ) or an electrode pattern formed on the bottom thereof. The electrodes ( 131  in  FIG. 8 ) or an electrode pattern will be fused to a package substrate ( 140  in  FIG. 8 ) implemented as a printed circuit board (PCB) to electrically connect the LED chip  130  to the package substrate ( 140  in  FIG. 8 ). 
         [0039]    Referring to  FIG. 7 , after the color conversion frit  100  is bonded to the plurality of LED chips  130  through the color conversion frit bonding step S 3 , the process of removing the transfer film from the color conversion frit  100  may be performed. 
         [0040]    Finally, referring to  FIG. 8 , after the transfer film  120  is removed from the color conversion frit  100 , the plurality of LED chips  130  is cut into a plurality of unit cells each of which is based on a single LED chip  130 . Subsequently, the LED chip  130  is mounted onto the package substrate  140  by fusing the electrodes  131  formed on the bottom of the LED chip  130  to electrode portions of the package substrate  140 . Consequently, the fabrication of an LED package  200  according to the present embodiment is completed. 
         [0041]    According to the method of fabricating an LED package according to present embodiment as set forth above, the substrate  110  is coated with the color conversion frit  100  in an intended pattern, the coated color conversion frit  100  is sintered, the color conversion frit  100  is transferred to the transfer film  120 , and subsequently the color conversion frit  100  transferred to the transfer film  120  is bonded to the LED chip  130 . After these processes, an additional heat treatment or cutting process is not performed on the color conversion frit  100 . It is therefore possible to prevent the heat treatment from degrading the LED chip  130  or the cutting from causing cracks in the color conversion frit  100 . Accordingly, the method of fabricating an LED package according to the present invention can simplify the fabrication of the LED package  200  and minimize the occurrence of defects. 
         [0042]    The foregoing descriptions of specific exemplary embodiments of the present invention have been presented with respect to the drawings. They are not intended to be exhaustive or to limit the present invention to the precise forms disclosed, and obviously many modifications and variations are possible for a person having ordinary skill in the art in light of the above teachings. 
         [0043]    It is intended therefore that the scope of the present invention not be limited to the foregoing embodiments, but be defined by the Claims appended hereto and their equivalents. 
       EXPLANATION OF REFERENCE NUMERALS 
       [0044]      100 : color conversion frit,  111 ; substrate 
         [0045]      120 : transfer film,  130 : LED chip 
         [0046]      131 : electrode,  130   a : base substrate 
         [0047]      140 : package substrate,  200 : LED package