Abstract:
The invention provides a novel highly refractory sintered body based on a tal diboride such as TiB 2  or Mo 2  B 5  and W 2  B 5  containing a binder ingredient. The high-temperature performance of the sintered body is further improved by including an auxiliary additive ingredient selected from several carbides, nitrides, silicides and oxides such as WC, TiC, TaN, TiN, MoSi 2 , TiO 2 , Al 2  O 3 , B 2  O 3  and the like in a limited amount.

Description:
BACKGROUND OF THE INVENTION 
     The present invention relates to a boride-based refractory material or, more particularly, to a boride-based refractory material having remarkably improved mechanical strengths and hardness at high temperatures as well as high heat resistance based on a metal diboride of the MB 2  type or an equivalent boride such as M 2  B 5  type boride as the base component. 
     Among various classes of highly refractory materials, metal diboride-based ones belong to one of the most promising classes owing to their high melting points and high hardness as well as sufficiently high mechanical strengths at high temperatures in general so that their application to cutting tools and building materials for internal combustion engines and rockets and the like is now under rapid development. On the contrary to the above mentioned excellent properties of the metal diboride-based refractory materials, they are rather defective of the brittleness and low bending strength, especially, when the refractory material is composed essentially of a metal diboride of the MB 2  type or a metal boride of the M 2  B 5  type which may be crystallographically equivalent to the MB 2  type diboride at elevated temperatures. 
     Extensive investigations have hitherto been undertaken to develop a metal diboride-based refractory material fully exhibiting the excellent properties inherent to the metal diborides and still free from the above mentioned defects of brittleness or low bending strength of the prior art materials. The investigations have been directed to the improvement of the material by the addition of a suitable binder component to a metal diboride and there have been proposed several kinds of binders which may be an alloy of nickel and phosphorus or a boride of nickel, iron, cobalt, manganese or titanium. There has further been disclosed that a metal boride of the M 2  B 5  type such as W 2  B 5  and Mo 2  B 5 , which has the same crystallographic structure at high temperatures as the metal diborides of the MB 2  type, is more advantageous in a sintered refractory material in respect of the mechanical strengths at high temperatures (see, for example, copending U.S. applications Ser. Nos. 89,487, 973,957 and 127,434 now U.S. Pat. Nos. 4,259,119; 4,246,027; and 4,292,081, respectively). 
     It is of course desirable to obtain a metal diboride-based refractory material having still higher strengths than those obtained in the above described impoved formulations and the inventors have continued their efforts to discover more preferable formulations for a high-strength refractory material on the base of a metal diboride. 
     SUMMARY OF THE INVENTION 
     As a result of the above mentioned continued efforts undertaken by the inventors, it has been unexpectedly discovered that the mechanical strengths of the metal diboride-based refractory materials can further be improved by the addition of a suitable amount of an additive ingredient which may be a carbide, oxide, silicide or nitride of specified elements as defined hereinafter. 
     The metal diboride-based refractory material of the invention comprises the components of 
     (a) at least one metal boride selected from the group consisting of the MB 2  type diborides of titanium, vanadium, niobium, tantalum, chromium, molybdenum, manganese, zirconium, hafnium and aluminum and M 2  B 5  type borides of molybdenum and tungsten, 
     (b) from 0.01 to 50% by weight of at least one binder ingredient selected from the group consisting of the borides of nickel, iron, cobalt, manganese and titanium other than the MB 2  type diborides and alloys of nickel and phosphorus, and 
     (c) from 0.1 to 50% by weight of at least one additive ingredient selected from the group consisting of 
     (c-1) carbides expressed by the formulas TiC, ZrC, HfC, VC, NbC, TaC, Ta 2  C, Mo 2  C, MoC, Cr 3  C 2 , B 4  C, W 2  C, WC and SiC; 
     (c-2) silicides expressed by the formulas MoSi 2 , WSi 2 , CrSi, CrSi 2 , Cr 3  Si, TaSi 2 , NbSi 2 , VSi 2 , ZrSi 2  and TiSi 2  ; 
     (c-3) nitrides expressed by the formulas TiN, TaN, Ta 2  N, ZrN, HfN, VN, V 3  N, NbN, Nb 2  N, CrN, Cr 2  N, Mo 2  N and MoN; and 
     (c-4) oxides expressed by the formulas Al 2  O 3 , B 2  O 3 , SiO 2 , Cr 2  O 3 , TaO, VO, NbO, BeO, TiO, TiO 2 , Ti 2  O 3 , ZrO 2 .SiO 2 , Al 2  O 3 .TiO 2 , MgO.Al 2  O 3 , ThO 2 .ZrO 2 , 3Al 2  O 3 .SiO 2  and (Mg,Fe) (Al,Cr) 2  O 4 , the balance being substantially the metal boride as the component (a). 
     Further improvement in the mechanical strengths of the metal diboride-based refractory materials of the above defined formulation is obtained when the composition additionally contains (d) up to 40% by weight, based on the total amount of the sintered material, of a MB type boride of a metal selected from the group consisting of tantalum, niobium, tungsten, zirconium, hafnium, molybdenum and vanadium. 
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     As is described above, the inventive metal diboride-based refractory material is basically composed of the base boride as the component (a), the binder ingredient as the component (b) and the auxiliary additive ingredient as the component (c) in the above specified proportion, optionally, with addition of the MB type boride as the component (d) partially substituting for the base component (a). The addition of this component (d) is preferable when further increased strength of the refractory material is desired and such an additional improvement is obtained by adding 0.1% by weight or more of the component (d) while an amount in excess of 40% by weight is undesirable due to the increased difficulty in sintering the composition into refractory bodies. 
     The amount of this base component constitutes the balance of the other components but it is preferable that the amount of the MB 2  and/or M 2  B 5  type boride or borides is at least 30% by weight of the total formulation. Among the above named 10 kinds of the metal diborides, titanium diboride is preferred solely for the reason of less expensiveness than the other diborides which also can give equally excellent refractory bodies. 
     The base component, i.e. the component (a) with optional admixture of the component (d), is used as a fine powder having a particle size distribution of 5 μm or smaller in the average particle diameter. 
     The binder ingredient as the component (b) is essential to facilitate sintering of the composition so that it should be used in an amount of at least 0.01% by weight based on the total amount of the composition to be sintered while an amount in excess of 50% by weight of the binder ingredient is undesirable due to the decreased heat resistance of the resultant sintered refractory bodies. The amount of this binder ingredient is preferably in the range from 0.1 to 20% by weight when the refractory body is prepared by the techniques of so-called hot pressing and in the range from 15 to 40% by weight when the refractory body is prepared by the method of sintering a green body shaped by compression molding in cold or by the method of so-called infiltration. 
     The binder ingredient as the component (b) is, as is described above, selected from the borides of nickel, cobalt, iron, manganese and titanium as well as alloys of nickel and phosphorus. Suitable borides of nickel are exemplified by NiB, Ni 4  B 3 , Ni 2  B and Ni 3  B, cobalt borides are exemplified by CoB, Co 2  B and Co 3  B, iron borides are exemplified by FeB and Fe 2  B, manganese borides are exemplified by MnB, Mn 3  B 4 , Mn 2  B and Mn 4  B, and titanium borides are exemplified by TiB, Ti 2  B and Ti 2  B 5 . These borides may be used either singly or as a mixture of two kinds or more. Particularly suitable metal borides among them are NiB, Ni 4  B 3 , CoB, FeB, TiB and MnB. The alloy of nickel and phosphorus used as the component (b) is obtained by adding from 3 to 25% by weight of phosphorus to nickel. It is of course optional that the binder ingredient as the component (b) is a combination of one or more of the metal borides as defined above and the nickel-phosphorus alloy. Among the above named borides suitable as the binder ingredient, MnB, TiB, NiB, Ni 4  B, CoB and FeB are more preferable. 
     It should be noted that the above defined binder ingredient is not necessarily added in the form described above as such but may be a mixture of the components from which the above mentioned borides or the alloys can be formed during the sintering procedure. For example, a metal such as nickel, cobalt, iron, manganese and titanium may be added as combined with elementary boron so as that the desired metal boride is formed by the reaction between the metal and the boron during sintering. 
     The auxiliary additive ingredient as the component (c), which is formulated in an amount from 0.1 to 50% by weight or, preferably, from 1 to 30% by weight, is selected from the above named carbides, silicides, nitrides and oxides. Among the above named ones, WC, TiC, TaC, NbC, VC and ZrO 2  are more preferable and the nitrides such as TiN, ZrN, TaN and VN are effective to improve the impact strength of the sintered refractory body. MoSi 2 , ZrSi 2 , B 2  O 3  and Al 2  O 3  are less preferable. These auxiliary additive ingredients should have a particle diameter not to exceed 5 μm. These ingredients may be added either alone or as a combination of two kinds or more. 
     The sintered refractory body of the invention is manufactured as follows. The individual components are taken in calculated amounts and uniformly blended to give a powdery composition. A mold made of, for example, graphite is filled with the powder composition and sintering of the composition is carried out by heating the composition in the mold at a temperature of 1000° C. or higher or, preferably, from 1700° to 1800° C. under a pressure of at least 50 kg/cm 2  or preferably, at least 200 kg/cm 2  in vacuum or in an inert or reducing atmosphere of argon or hydrogen for about 10 minutes or longer. Instead of the above described so-called hot-pressing, it is of course possible that a green body is first shaped by compression molding a room temperature with the powder composition and the green body of the desired form is then subjected to sintering under atmospheric pressure otherwise with the above described conditions into a sintered body. 
     Further alternatively, the techniques of the so-called infiltration are applicable in this case. That is, the metal diboride and/or the M 2  B 5  type boride with optional admixture of MB type borides are blended with the auxiliary additive ingredient of the carbides, nitrides, silicides or oxides and the powder blend is first shaped and sintered without the binder ingredient followed by dipping of the thus sintered body in a melt of the binder ingredient so as that the molten binder is soaked in the sintered body resulting in the desired sintered body. 
     In any way, the sintered refractory body of the invention always has a relative density of approximately 100% and is excellent in the mechanical strengths, hardness and heat resistance and advantageously utilized for the manufacture of cutting tools or as a structural material of internal combustion engines, rockets and the like. 
    
    
     Following are the examples to illustrate the present invention in further detail. 
     EXAMPLE (EXPERIMENTS NO. 1 to NO. 43) 
     One or two kinds of the base borides selected from the MB 2  type and M 2  B 5  type borides always including titanium diboride TiB 2  were admixed with a binder boride, i.e. CoB, NiB, FeB or TiB, and one to three kinds of the auxiliary additive ingredients selected from the carbides, nitrides, silicides and oxides. The kinds of the admixed ingredients in each of the experiments excepting titanium diboride are shown in the accompanying table with the amount of each of the ingredients indicated in brackets in % by weight, the balance being the amount of titanium diboride. In Experiment No. 22, tantalum boride TaB was used to partially substitute for the MB 2  or M 2  B 5  type borides. 
     A graphite mold was filled with the thus well blended powder mixture which was sintered under compression with a pressure of 200 kg/cm 2  for 30 minutes. The heating temperature was 1700° C. in all of the Experiments excepting No. 2 in which the sintering was carried out at 1800° C. The atmosphere of sintering was evacuated to vacuum in all of the Experiments excepting No. 21 in which the sintering was carried out in an atmosphere of argon. 
     All of the sintered bodies obtained in this manner had a relative density of almost 100% of the theoretical value. The sintered bodies were subjected to the measurements of the bending strength and the Vickers hardness both at room temperature and at 1000° C. to give the results shown in the table. 
     
                                           TABLE__________________________________________________________________________                       Vickers hardness,                 Bending                       kg/mm.sup.2Exp.    Component         strength,                       at room                             atNo. a* (%)     b (%) c (%) kg/mm.sup.2                       temp. 1000° C.__________________________________________________________________________(Part I)1   Mo.sub.2 B.sub.5 (3)     CoB (1)           Mo.sub.2 C (3)                 220   3000  20002   W.sub.2 B.sub.5 (5)     CoB (1)           WC (5)                 200   2800  --3   TaB.sub.2 (5)     CoB (1)           WC (5)                 186   --    --4   Mo.sub.2 B.sub.5 (3)     CoB (1)           TiC (5)                 226   2900  20005   TaB.sub.2 (5)     CoB (1)           TiC (1.7)                 230   3000  21006   TaB.sub.2 (5)     CoB (1)           TiC (3)                 230   --    --7   TaB.sub.2 (5)     CoB (1)           Mo.sub.2 C (3)                 210   2900  20008   TaB.sub.2 (5)     CoB (1)           TaN (5)                 198   --    --9   TaB.sub.2 (5)     CoB (1)           TaN (10)                 228   2910  200010  TaB.sub.2 (5)     CoB (1)           TaN (20)                 182   --    --11  TaB.sub.2 (5)     CoB (1)           TaN (30)                 178   --    --12  TaB.sub.2 (5)     CoB (1)           TiN (6)                 188   --    --13  TaB.sub.2 (5)     CoB (1)           TiN (2)                 185   --    --14  TaB.sub.2 (5)     CoB (1)           TiC (3)                 200   --    --           TaN (10)(Part II)15  TaB.sub.2 (5)     CoB (1)           TiC (3)                 204   --    --           TaN (20)16  TaB.sub.2 (5)     CoB (1)           TiC (1.7)                 250   3000  2100           TaN (5)17  TaB.sub.2 (5)     CoB (1)           TiC (1.7)                 250   --    --           TaN (10)18  TaB.sub.2 (5)     CoB (1)           TiC (1.7)                 196   --    --           TaN (20)19  TaB.sub.2 (5)     CoB (1)           MoSi.sub.2 (5)                 194   --    --20  Mo.sub.2 B.sub.5 (3)     CoB (1)           MoSi.sub.2 (3)                 172   --    --21    --  NiB (1)           MoSi.sub.2 (5)                 164   --    --22  TaB** (5)     TiB (1)           TiC (3)                 200   2900  2000           TaN (5)           MoSi.sub.2 (3)23  TaB.sub.2 (5)     CoB (1)           TiO.sub.2 (5)                 190   3000  200024  VB.sub.2 (5)     FeB (1)           Ti.sub.2 O.sub.3 (5)                 180   --    --25  CrB.sub.2 (5)     CoB (1)           TiO (5)                 174   --    --26  TaB.sub.2 (5)     CoB (1)           TiC (1.7)                 230   3200  2100           TaN (5)           TiO.sub.2 (5)27  TaB.sub.2 (5)     CoB (1)           B.sub.2 O.sub.3 (5)                 180   --    --28  TaB.sub.2 (5)     CoB (1)           WC (1)                 160   --    --29  TaB.sub.2 (5)     CoB (1)           WC (2.5)                 144   --    --(Part III)30  TaB.sub.2 (1)     CoB (1)           WC (10)                 160   3100  220031    --  CoB (1)           WC (2.5)                 200   2800  200032    --  CoB (1)           WC (5)                 200   --    --33    --  CoB (1)           WC (10)                 200   --    --34    --  CoB (1)           TiC (10)                 140   2800  200035    --  CoB (1)           TiC (20)                 140   --    --36  Mo.sub.2 B.sub.5 (3)     CoB (1)           Mo.sub.2 C (3)                 210   2910  200037  TaB.sub.2 (5)     CoB (3)           B.sub.4 C (5)                 150   2800  --38  TaB.sub.2 (5)     CoB (1)           TaC (5)                 200   3000  220039  TaB.sub.2 (5)     CoB (1)           NbC (5)                 200   3000  220040  TaB.sub.2 (5)     CoB (1)           VC (5)                 200   3000  220041  TaB.sub.2 (5)     CoB (1)           VN (5)                 180   2800  --42  TaB.sub.2 (5)     CoB (1)           ZrO.sub.2 (2)                 230   3000  210043  TaB.sub.2 (5)     CoB (1)           ZrO.sub.2 (2)                 230   3100  2100           WC (2)           TaN (5)__________________________________________________________________________ *Other than titanium diboride. **TaB was used in place of part of the component (a).