Abstract:
A rubber composition containing 
     (A) a bismaleimide compound represented by the general formula (I) ##STR1## wherein R is a divalent acyclic aliphatic group, cyclic aliphatic group, aromatic group, or alkylaromatic group, these groups optionally containing a hetero atom selected from O, N and S in their chain or side substituent, 
     (B) a sulfenamide compound represented by the general formula (II) ##STR2## wherein R 1  and R 2  denote independently from each other a hydrogen atom, an acyclic aliphatic group, or cyclic aliphatic group, or R 1  and R 2  together denote a chain aliphatic group which optionally contains an oxygen atom, provided that R 1  and R 2  cannot simultaneously denote a hydrogen atom, 
     (C) a dithiophosphoric acid compound represented by the general formula (III) ##STR3## wherein R 3  and R 4  denote each an aliphatic group, and (D) sulfur; or 
     (A) a bismaleimide compound represented by the general formula (I) defined above, 
     (E) an aromatic carboxylic acid anhydride, 
     (F) sulfur and/or a sulfur donor, and 
     (G) vulcanization accelerators.

Description:
This is a division of application Ser. No. 020,227, filed Mar. 2, 1987, now U.S. Pat. No. 4,803,250, which in turn is a continuation of application Ser. No. 814,881, filed Dec. 30, 1985, now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to a rubber composition having improved rubber properties. More particularly, it relates to a rubber composition which is excellent in resistance to reversion in the vulcanization step and is excellent in such rubber properties as resistance to thermal degradation and resistance to deterioration due to flex cracking. 
     2. Description of the Prior Art 
     In recent years, increasingly higher levels of mechanical properties and heat resistance than before have come to be required for rubber goods such as tires and belts. 
     It has been known for a long time for improving the mechanical properties of rubber to use a large amount of sulfur as a cross-linking agent to increase the cross-linking density. However, the use of a large amount of sulfur has a serious defect in that it gives rise to a severe reversion in the vulcanization step and a marked decrease in resistance to heat and resistance to flex cracking in vulcanized rubbers, although it improves such mechanical properties of vulcanized rubber as hardness and tensile strength. 
     To ovbiate such a defect of sulfur cross-linking, there has been also proposed a method of adding a bismaleimide compound to a sulfur vulcanization system containing dibenzothiazyl disulfide (MBTS) or tetramethylthiuram disulfide (TMTD). However, though the use of this method can correct the above-mentioned defect to some extent, the improvement is not yet fully satisfactory. Moreover, the method have difficulties in that since it requires a large amount of costly bismaleimide compounds it leads to a marked increase in cost of rubber compounds and further that when a vulcanization accelerator of sulfenamide type, which is used chiefly for tires and the like in rubber industry, is used in place of MBTS or TMTD the effect of addition of bismaleimide compound is hardly observed, so that vulcanization accelerators which can be used in combination with bismaleimide compounds are limited to those giving a short scorch time such as MBTS and TMTD, and consequently it can be used only in a limited field such as the manufacture of footwears. 
     Thus, prior art rubber compositions are not simultaneously satisfactory in such properties as scorching stability, resistance to reversion, resistance to thermal degradation, and resistance to deterioration due to flex cracking. 
     In view of these circumstances, the present inventors have made an extensive study to obtain rubber compositions which, in all the sulfur vulcanization systems including those containing sulfenamide type accelerators, show an excellent resistance to reversion in vulcanization step and exhibit excellent rubber properties including resistance to thermal degradation and resistance to flex cracking. As a result, it has been found that a rubber composition comprising natural rubber and/or synthetic rubber compounded with a bismaleimide compound represented by the general formula (I), a sulfenamide compound represented by the general formula (II), a dithiophosphoric acid compound represented by the general formula (III), which are mentioned later, and sulfur, or a rubber composition comprising natural rubber and/or synthetic rubber compounded with a bismaleimide compound represented by the general formula (I) mentioned later, an aromatic carboxylic acid anhydride, sulfur and/or a sulfur donor and vulcanization accelerators can, for the first time in all the sulfur vulcanization systems including those containing sulfenamide type accelerators, give mechanical properties which are in no way inferior to those obtainable by using a large amount of sulfur and further show markedly improved properties including resistance to reversion, resistance to heat aging, and resistance to flex cracking, the insufficiency of which properties has been the defect of sulfur vulcanization. This invention has been achieved on the basis of above findings. 
      SUMMARY OF THE INVENTION 
     Thus, according to this invention, there is provided a rubber composition containing 
     (A) a bismaleimide compound represented by the general formula (I) ##STR4## wherein R is a divalent acyclic aliphatic group, cyclic aliphatic group, aromatic group, or alkylaromatic group, these groups optionally containing a hetero atom selected from O, N and S in their chain or side substituent, 
     (B) a sulfenamide compound represented by the general formula (II) ##STR5## wherein R 1  and R 2  denote independently from each other, a hydrogen atom, an acyclic aliphatic group, or cyclic aliphatic group; or R 1  and R 2  together denote a chain aliphatic group which optionally contains an oxygen atom, provided that R 1  and R 2  cannot simultaneously denote a hydrogen atom, 
     (C) a dithiophosphoric acid compound represented by the general formula (III) ##STR6## wherein R 3  and R 4  denote each an aliphatic group, and 
     (D) sulfur; or 
     (A) a bismaleimide compound represented by the general formula (I) defined above, 
     (E) an aromatic carboxylic acid anhydride, 
     (F) sulfur and/or a sulfur donor, and 
     (G) vulcanization accelerators. 
     These rubber compositions have a stable scorching property and are excellent in resistances to reversion, thermal degradation and flex cracking. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The bismaleimide compound represented by the general formula (I) used in this invention include, for example, 
     N,N&#39;-ethylenebismaleimide, 
     N,N&#39;-hexamethylenebismaleimide, 
     N,N&#39;-dodecamethylenebismaleimide, 
     N,N&#39;-(2,2,4-trimethylhexamethylene)bismaleimide, 
     N,N&#39;-(oxydipropylene)bismaleimide, 
     N,N&#39;-(aminodipropylene)bismaleimide, 
     N,N&#39;-(ethylenedioxydipropylene)bismaleimide, 
     N,N&#39;-(1,4-cyclohexylene)bismaleimide, 
     N,N&#39;-(1,3-cyclohexylene)bismaleimide, 
     N,N&#39;-(methylene-1,4-dicyclohexylene)bismaleimide, 
     N,N&#39;-(isopropylidene-1,4-dicyclohexylene)bismaleimide, 
     N,N&#39;-(oxy-1,4-dicyclohexylene)bismaleimide, 
     N,N&#39;-(m-phenylene)bismaleimide, 
     N,N&#39;-(p-phenylene)bismaleimide, 
     N,N&#39;-(o-phenylene)bismaleimide, 
     N,N&#39;-(1,3-naphthylene)bismaleimide, 
     N,N&#39;-(1,4-naphthylene)bismaleimide, 
     N,N&#39;-(1,5-naphthylene)bismaleimide, 
     N,N&#39;-(3,3&#39;-dimethyl-4,4&#39;-biphenylene)bismaleimide, 
     N,N&#39;-(3,3&#39;-dichloro-4,4&#39;-biphenylene)bismaleimide, 
     N,N&#39;-(2,4-pyridyl)bismaleimide, 
     N,N&#39;-(2,6-pyridyl)bismaleimide, 
     N,N&#39;-(4-methyl-2,6-pyridyl)bismaleimide, 
     N,N&#39;-(1,4-anthraquinonediyl)bismaleimide, 
     N,N&#39;-(m-tolylene)bismaleimide, 
     N,N&#39;-(p-tolylene)bismaleimide, 
     N,N&#39;-(4,6-dimethyl-1,3-phenylene)bismaleimide, 
     N,N&#39;-(2,3-dimethyl-1,4-phenylene)bismaleimide, 
     N,N&#39;-(4,6-dichloro-1,3-phenylene)bismaleimide, 
     N,N&#39;-(5-chloro-1,3-phenylene)bismaleimide, 
     N,N&#39;-(5-hydroxy-1,3-phenylene)bismaleimide, 
     N,N&#39;-(5-methoxy-1,3-phenylene)bismaleimide, 
     N,N&#39;-(m-xylylene)bismaleimide, 
     N,N&#39;-(p-xylylene)bismaleimide, 
     N,N&#39;-(methylenedi-p-phenylene)bismaleimide, 
     N,N&#39;-(isopropylidenedi-p-phenylene)bismaleimide, 
     N,N&#39;-(oxydi-p-phenylene)bismaleimide, 
     N,N&#39;-(thiodi-p-phenylene)bismaleimide, 
     N,N&#39;-(dithiodi-p-phenylene)bismaleimide, 
     N,N&#39;-(sulfodi-p-phenylene)bismaleimide, and 
     N,N&#39;-(carbonyldi-p-phenylene)bismaleimide. 
     The sulfenamide compounds represented by the general formula (II) used in this invention include, for example, 
     N-cyclohexyl-2-benzothiazylsulfenamide, 
     N-oxydiethylene-2-benzothiazylsulfenamide, 
     N-t-butyl-2-benzothiazylsulfenamide, 
     N,N-diisopropyl-2-benzothiazylsulfenamide, and 
     N,N-dicyclohexyl-2-benzothiazylsulfenamide. 
     The dithiophosphoric acid compounds represented by the general formula (III) used in this invention include, for example, 
     diethyldithiophosphoric acid disulfide, 
     di-isopropyldithiophosphoric acid disulfide, 
     di-n-propyldithiophosphoric acid disulfide, 
     dibutyldithiophosphoric acid disulfide, 
     dihexyldithiophosphoric acid disulfide, 
     dicyclohexyldithiophosphoric acid disulfide, and 
     dioctyldithiophosphoric acid disulfide. 
     Examples of sulfur include various types of sulfur such as powdered sulfur, precipitated sulfur, and insoluble sulfur. 
     Examples of aromatic carboxylic acid anhydrides, another important constituent in this invention, include phthalic anhydride, pyromellitic anhydride, benzenehexacarboxylic trianhydride, 4-methylphthalic anhydride, trimellitic anhydride, and 4-chlorophthalic anhydride. 
     Phthalic anhydride and the like mentioned above have for long been known to the rubber industry as scorch retarders. However, other known scorch retarders than these, namely organic acids such as salicylic acid and benzoic acid, maleic anhydride, N-nitrosodiphenylamine, N-cyclohexylphthalimide and the like do not show such effect as is obtained in this invention even when combined with above-mentioned bismaleimide compounds (I). The latter compounds can give a remarkable effect only when used in combination with the above-mentioned aromatic acid anhydride. 
     The examples of sulfur donors include tetramethylthiuram disulfide, tetraethylthiuram disulfide, tetrabutylthiuram disulfide, and pentamethylthiuram hexasulfide. 
     The examples of vulcanization accelerators include dibenzothiazyl disulfide, tetramethylthiuram disulfide, N-cyclohexyl-2-benzothiazylsulfenamide, N-oxydiethylene-2-benzothiazylsulfenamide, N-t-butyl-2-benzothiazylsulfenamide, and N,N-dicyclohexyl-2-benzothiazylsulfenamide. 
     Examples of rubbers usable in this invention include natural rubber (NR), styrene-butadiene rubber (SBR), butadiene rubber (BR), isoprene rubber (IR), acrylonitrile-butadiene rubber (NBR), chloroprene rubber (CR), ethylene-propylene-diene terpolymer (EPDM), and isoprene-isobutylene rubber (IIR), used each alone or in combination of two or more thereof. 
     The amount of the bismaleimide compound (I), the sulfenamide compound (II), the dithiophosphoric acid compound (III), and sulfur to be compounded with rubber is, based on 100 parts by weight of rubber, usually 0.1 to 8 parts by weight, preferably 0.3 to 4 parts by weight, for bismaleimide compounds (I); usually 0.1 to 8 parts by weight, preferably 0.3 to 6 parts by weight, for sulfenamide compounds; usually 0.1 to 8 parts by weight, preferably 0.3 to 6 parts by weight, for dithiophosphoric acid compounds; and usually 0.1 to 14 parts by weight, preferably 0.5 to 8 parts by weight for sulfur. 
     Further, the amount of the bismaleimide compound (I), the aromatic carboxylic acid anhydride, the sulfur and/or the sulfur donor and the vulcanization accelerator to be compounded with rubber is, based on 100 parts by weight of rubber, usually 0.1 to 8 parts by weight, preferably 0.3 to 4 parts by weight for bismaleimide compounds (I); usually 0.1 to 4 parts by weight, preferably 0.3 to 3 parts by weight for aromatic carboxylic acid anhydrides; usually 0.1 to 14 parts by weight, preferably 0.5 to 8 parts by weight; for sulfur and/or sulfur donors, and usually 0.1 to 8 parts by weight, preferably 0.3 to 6 parts by weight for vulcanization accelerators. 
     These ingredients may be used as a mixture prepared beforehand or added separately together with, as required, other compounding ingredients at the time of compounding. 
     Other compounding ingredients include reinforcing agents, for example carbon black, such as HAF, ISAF and SRF, silica, and calcium carbonate; stearic acid, zinc white, process oil, tackifiers, waxes, antioxidants, etc. 
     The rubber composition of this invention thus obtained shows excellent scorch stability and resistance to reversion in processing and vulcanization and further, as to rubber properties after vulcanization, shows very excellent resistance to heat aging and to flex cracking. 
     This invention will be explained in detail below with reference to Examples, but it is not limited thereto. 
     In the Examples, &#34;parts&#34; means parts by weight. 
     EXAMPLE 1 
     In a conventional manner, 100 parts of natural rubber, 45 parts of HAF carbon, 5 parts of zinc white, 1  part of stearic acid, 1 part of process oil, 3 parts of wax, 2 parts of N-phenyl-N&#39;-1,3-dimethylbutyl-p-phenylenediamine (an antiozonant) and the compounding ingredients listed in Table 1 were compounded by using an open roll of 6 inches diameter to prepare various rubber compositions. 
     With each of the rubber compositions thus obtained, scorching property was determined according to JIS-K-6300, and the maximum cross-linking density (M H ) and the vulcanization-reverse property (the time required for torque to decrease by 1 kg.cm from its maximum value; Rt) were determined according to ASTM-D-2084 by using an oscillating disc rheometer at 170° C. 
     Further, each of the various rubber compositions was vulcanized at 170° C. for 20 minutes to prepare prescribed specimens and then subjected to a thermal aging test and a flex cracking test according to JIS-K-6301. The thermal aging test was conducted by subjecting the specimen to thermal aging at 100° C. for 48 hours in a Geer Oven and then measuring the percentage of retention of tensile strength. The flex cracking test was conducted by subjecting a specimen, on which a crack of 2 mm original length had been made, to 10,000 times of flexing and then measuring the length of the crack. 
     The results obtained by these tests are shown in Table 1. 
     EXAMPLE 2 
     In the same manner as in Example 1, 100 parts of styrene-butadiene rubber, 50 parts of HAF carbon, 5 parts of process oil, 5 parts of zinc white, 3 parts of stearic acid, 3 parts of wax, 2 parts of 2,2,4-trimethyl-1,2-dihydroquinoline polymer (an antioxidant) and the ingredients listed in Table 2 were compounded to prepare various rubber compositions and their properties were determined. The results are shown in Table 2. The thermal aging test in this Example was conducted at 110° C. for 48 hours. 
     EXAMPLE 3 
     In a conventional manner, 100 parts of natural rubber, 45 parts of HAF carbon, 5 parts of zinc white, 1 part of stearic acid, 1 part of process oil, 3 parts of wax, 2 parts of N-phenyl-N&#39;-1,3-dimethylbutyl-p-phenylenediamine (an antiozonant) and the ingredients listed in Table 3 were compounded by using an open roll of 6 inches diameter to prepare various rubber compositions. 
     With each of the rubber compositions thus obtained, the maximum cross-linking density (M H ) and the vulcanization-reverse property (the time required for torque to decrease by 1 kg.cm from its maximum value; Rt) were determined according to ASTM-D-2084 by using an oscillating disc rheometer at 170° C. 
     Further, each of the various rubber compositions was vulcanized at 170° C. for 20 minutes to prepare prescribed specimens and then subjected to a thermal aging test and a flex cracking test according to JIS-K-6301. The thermal aging test was conducted by subjecting a specimen to thermal aging at 100° C. for 48 hours in a Gear Over and then measuring the percentage of retention of tensile strength. The flex cracking test was conducted by subjecting a specimen, on which a cut of 2 mm original length has been made, to 10,000 times of flexing and then measuring the length of the cut. 
     The results obtained are shown in Table 3. 
     EXAMPLE 4 
     In the same manner as in Example 3, 100 parts of styrene-butadiene rubber, 50 parts of HAF carbon, 5 parts of process oil, 5 parts of zinc white, 3 parts of stearic acid, 3 parts of wax, 2 parts of 2,2,4-trimethyl-1,2-dihydroquinoline polymer (an antioxidant), and the ingredients listed in Table 4 were compounded to prepare various rubber compositions and their properties were determined. The results obtained are shown in Table 4. The thermal aging test in this Example was conducted at 110° C. for 48 hours. 
     EXAMPLE 5 
     In the same manner as in Example 3, 100 parts of acrylonitrile-butadiene rubber, 3 parts of stearic acid, 5 parts of zinc white, 10 parts of process oil, 40 parts of light calcium carbonate, 10 parts of titanium oxide, 30 parts of hydrated silica, 2 parts of 2,2&#39;-methylenebis(4-methyl-6-t-butylphenol) (an antioxidant) and the ingredients listed in Table 5 were compounded to prepare various rubber compositions and their properties were determined. The results obtained are shown in Table 5. The thermal aging test in this Example was conducted at 130° C. for 48 hours. 
     
                                           TABLE 1__________________________________________________________________________                                              Comparative                        Example               Example                        Run No.Item                         1  2  3   4   5   6   7   8   9__________________________________________________________________________Compounding  Sulfur                1  1  1   1   1   1   1   2   1ingredients  Soxinol ® NBS*.sup.1                        1  1  1   1           2.5 2.5  Soxinol ® NS*.sup.2             1               2.5  Soxinol ® DZ*.sup.3                 1  Diethyldithiophosphoric acid disulfide                        1.5  Di-iso-propyldithiophosphoric acid disulfide                           1.5                              1.5 1.5 1.5 1.5  N,N&#39;-Ethylenebismaleimide                           1.5  N,N&#39;-m-phenylenebismaleimide                              1.5 2.5 1.5  N,N&#39;-(methylene-di-p-phenylene)bismaleimide                                          1.5  Soxinol ® DM*.sup.4Properties  Scorching property (minute)                        56.0                           56.5                              57.0                                  58.5                                      51.5                                          38.5                                              45.0                                                  38.0                                                      42.0  MH (kg · cm) 98 97 97  106 97  96  72  90  70  Rt (minute)           &gt;15                           &gt;15                              &gt;15 &gt;15 &gt;15 &gt;15 1.8 1.0 1.8  Thermal resistance (%)                        75 76 77  78  77  76  50  39  49  Resistance to flex cracking (mm)                        9.2                           9.1                              9.1 9.1 9.1 9.1 9.0 13.0                                                      9.1__________________________________________________________________________                        Comparative Example                        Run No.Item                         10  11  12  13 14 15 16 17 18 19__________________________________________________________________________Compounding  Sulfur                1   1   1   1  1  1  1  1  1  1ingredients  Soxinol ® NBS*.sup.1          2.5  Soxinol ® NS*.sup.2              2.5  Soxinol ® DZ*.sup.3                        2.5               2.5  Diethyldithiophosphoric acid disulfide                            2.5              2.5  Di-iso-propyldithiophosphoric acid disulfide                                2.5             2.5  N,N&#39;-Ethylenebismaleimide         1.5      1.5      1.5  N,N&#39;-m-phenylenebismaleimide         1.5      1.5  N,N&#39;-(methylene-di-p-phenylene)bismaleimide                                          1.5  Soxinol ® DM*.sup.4                          2.5                                                      2.5Properties  Scorching property (minute)                        46.0                            54.0                                54.0                                    46.0                                       44.0                                          50.5                                             56.0                                                56.5                                                   18.5                                                      19.0  MH (kg · cm) 68  53  55  74 78 70 82 88 54 84  Rt (minute)           1.4 2.2 2.2 3.1                                       3.2                                          3.1                                             3.2                                                3.3                                                   1.5                                                      4.0  Thermal resistance (%)                        53  55  56  52 53 52 55 57 39 55  Resistance to flex cracking (mm)                        9.5 9.1 9.3 9.0                                       9.1                                          9.1                                             9.2                                                9.3                                                   8.6                                                      11.5__________________________________________________________________________ Note: *.sup.1 Soxinol ® NBS: NOxydiethylene-z-benzothiazylsulfenamide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.2 Soxinol ® NS: Nt-Butyl-2-benzothiazylsulfenamide (mfd. by Sumitom Chemical Co., Ltd.) *.sup.3 Soxinol ® DZ: N,NDicyclohexyl-2-benzothiazylsulfenamide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.4 Soxinol ® DM: Dibenzothiazyl disulfide (mfd. by Sumitomo Chemical Co., Ltd.) 
    
     
                                           TABLE 2__________________________________________________________________________                                         Comparative                       Example           Example                       Run No.Item                        1   2   3   4  5  6  7  8__________________________________________________________________________Compounding  Sulfur               2   2   2   2  2  2  3  2ingredients  Soxinol ® CZ*.sup.1                       1   1   1         2  2  2  Soxinol ® NBS*.sup.2         1  1  Soxinol ® DM*.sup.3  Di-iso-propyldithiophosphoric acid disulfide                       1   1       1  Dibutyldithiophosphoric acid disulfide                               1      1  N,N&#39;-p-Phenylenebismaleimide                       1.5            1.5      1.5  N,N&#39;-m-Phenylenebismaleimide                           1.5     1.5  N,N&#39;-(Oxy-p-phenylene)bismaleimide                               1.5Properties  MH (kg · cm)                       126 127 127 130                                      128                                         103                                            128                                               104  Thermal resistance (%)                       78  78  79  78 79 61 53 63  Resistance to flex cracking (mm)                       13.1                           13.2                               13.0                                   13.1                                      13.0                                         12.3                                            19.5                                               12.7__________________________________________________________________________                       Comparative Example                       Run No.Item                        9  10 11 12 13 14 15 16 17__________________________________________________________________________Compounding  Sulfur               2  2  2  2  2  2  2  2  2ingredients  Soxinol ® CZ*.sup.1                       2  2  Soxinol ® NBS*.sup.2   2  2  Soxinol ® DM*.sup.3                   2  2  Di-iso-propyldithiophosphoric acid disulfide                                   2  2  Dibutyldithiophosphoric acid disulfide 2  N,N&#39;-p-Phenylenebismaleimide  1.5                                   1.5         1.5  N,N&#39;-m-Phenylenebismaleimide                       1.5   1.5      1.5  N,N&#39;-(Oxy-p-phenylene)bismaleimide                          1.5            1.5Properties  MH (kg · cm)                       105                          104                             100                                101                                   85 86 86 98 119  Thermal resistance (%)                       62 64 62 63 67 67 66 61 51  Resistance to flex cracking (mm)                       12.8                          12.7                             12.2                                12.3                                   11.4                                      11.5                                         11.3                                            12.0                                               18.6 Note: *.sup.1 Soxinol ® CZ: NCyclohexyl-2-benzothiazylsulfenamide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.2 Soxinol ® NBS: NOxydiethylene-2-benzothiazylsulfenamide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.3 Soxinol ® DM: Dibenzothiazyl disulfide (mfd. by Sumitomo Chemical Co., Ltd.) 
    
     
                                           TABLE 3__________________________________________________________________________                         Example                         Run No.Item                          1   2   3   4  5  6  7  8  9  10__________________________________________________________________________Compounding  Sulfur                 1.0 1.0 1.0 1.0                                        1.0                                           1.0                                              0.5                                                 0.5                                                    0.5                                                       0.5ingredients  Soxinol ® DM*.sup.1                         1.5 1.5 1.5 1.5                                        1.5                                           1.5  Soxinol ® NBS*.sup.2                    2.5                                                 2.5                                                    2.5                                                       2.5  N,N&#39;-Hexamethylenebismaleimide                         1.5  N,N&#39;-p-Phenylenebismaleimide                             1.5  N,N&#39;-m-Phenylenebismaleimide   0.5 1.5                                        2.5                                           1.5                                              1.5                                                 1.5  N,N&#39;-(methylene-di-p-phenylene)bismaleimide       1.5  N,N&#39;-(Oxy-di-p-phenylene)bismaleimide                1.5  Phthalic anhydride     1   1   1   1  1     1  2  1  Trimellitic anhydride                    1           1  Maleic anhydride  Phthalic acid  N-NitrosodiphenylamineProperties  MH (kg · cm)  113 115 92  116                                        128                                           112                                              98 107                                                    96 96  Rt (minute)            &gt;15 &gt;15 &gt;15 &gt;15                                        &gt;15                                           &gt;15                                              &gt;15                                                 &gt;15                                                    &gt;15                                                       &gt; 15  Thermal resistance (%) 63  62  59  64 69 62 71 71 70 70  Resistance to flex cracking (mm)                         9.3 9.3 9.1 9.3                                        9.3                                           9.2                                              9.2                                                 9.2                                                    9.2                                                       9.2__________________________________________________________________________                         Comparative Example                         Run No.Item                          11 12 13 14 15 16 17 18 19 20 21__________________________________________________________________________Compounding  Sulfur                 1.0                            2.0                               1.0                                  1.0                                     1.0                                        1.0                                           1.0                                              1.0                                                 1.0                                                    0.5                                                       0.5ingredients  Soxinol ® DM*.sup.1                         1.5                            1.5                               1.5                                  1.5                                     1.5                                        1.5                                           1.5                                              1.5                                                 1.5  Soxinol ® NBS*.sup.2                          2.5                                                       2.5  N,N&#39;-Hexamethylenebismaleimide     1.5   1.5  N,N&#39;-p-Phenylenebismaleimide                1.5  N,N&#39;-m-Phenylenebismaleimide          1.5      1.5  N,N&#39;-(methylene-di-p-phenylene)bismaleimide  N,N&#39;-(Oxy-di-p-phenylene)bismaleimide  Phthalic anhydride           1                       1  Trimellitic anhydride           1  Maleic anhydride                   1  Phthallic acid  N-Nitrosodiphenylamine                1Properties  MH (kg · cm)  68 87 66 63 80 81 78 79 80 58 72  Rt (minute)            1.5                            0.7                               1.5                                  1.5                                     3.4                                        3.4                                           3.4                                              3.4                                                 3.4                                                    1.8                                                       0.3  Thermal resistance (%) 40 32 40 39 54 53 53 52 53 48 39  Resistance to flex cracking (mm)                         7.5                            11.5                               7.6                                  7.5                                     9.1                                        9.2                                           9.2                                              9.2                                                 9.1                                                    8.8                                                       12.0__________________________________________________________________________                                        Comparative Example                                        Run No.Item                                         22                                          23                                            24                                              25                                                26                                                  27                                                    28                                                      29                                                        30__________________________________________________________________________          Compounding                 Sulfur                 0.5                                          0.5                                            0.5                                              0.5                                                0.5                                                  0.5                                                    0.5          ingredients                 Soxinol ® DM.sup.*1                 Soxinol ® NBS.sup.*2                                        2.5                                          2.5                                            2.5                                              2.5                                                2.5                                                  2.5                                                    2.5                 N,N&#39;-Hexamethylenebismaleimide                 N,N&#39;-p-Phenylenebismaleimide                 N,N&#39;-m-Phenylenebismaleimide 1.5   1.5                 N,N&#39;-(methylene-di-p-phenylene)bismaleimide                                                1.5   1.5                 N,N&#39;-(Oxy-di-p-phenylene)bismaleimide                                                  1.5   1.5                 Phthalic anhydride                 Trimellitic anhydride  1                 Maleic anhydride             1                 Phthalic acid            1     1                 N-Nitrosodiphenylamine     1     1          Properties                 MH (kg · cm)  58                                          57                                            56                                              61                                                62                                                  61                                                    62                                                      61                                                        61                 Rt (minute)            1.8                                          1.8                                            1.7                                              2.0                                                2.0                                                  2.0                                                    2.0                                                      2.0                                                        2.0                 Thermal resistance (%) 48                                          47                                            47                                              49                                                50                                                  49                                                    50                                                      49                                                        49                 Resistance to flex cracking (mm)                                        8.9                                          8.8                                            8.8                                              9.0                                                9.0                                                  9.0                                                    9.1                                                      9.1                                                        9.1__________________________________________________________________________ Note: *.sup.1 Soxinol ® DM: Dibenzothiazyl disulfide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.2 Soxinol ® NBS: NOxydiethylene-2-benzothiazylsulfenamide (mfd. by Sumitomo Chemical Co., Ltd.) 
    
     
                                           TABLE 4__________________________________________________________________________                                       Comparative                  Example              Example                  Run No.Item                   1  2  3  4  5  6  7  8  9__________________________________________________________________________Compounding  Sulfur          1.5                     1.5                        1.5                           1.5                              1.5                                 1.5                                    1.5                                       1.5                                          2.5ingredients  Soxinol ® CZ*.sup.1                  2  2  2  2           2  2  Soxinol ® DM*.sup.2     2  2  2  N,N-Ethylenebismaleimide 1.5  N,N&#39;-p-Phenylenebismaleimide                     1.5  N,N&#39;-m-Phenylenebismaleimide                        1.5                           1.5                              1.5  N,N&#39;-(methylene-di-p-          1.5  phenylene)bismaleimide  N,N&#39;-(Oxydi-p-phenylene)-         1.5  bismaleimide  Phthalic anhydride                  1  1  1     1  1  Pyromellitic anhydride   1        1  Phthalic acid  N-Cyclohexylthiophthalimide  Benzoic acidProperties  MH (kg · cm)                  131                     132                        132                           130                              121                                 119                                    119                                       98 121  Thermal resistance (%)                  78 78 79 74 73 73 73 68 54  Resistance to flex cracking                  14.2                     14.3                        14.5                           14.3                              14.0                                 14.1                                    14.0                                       11.4                                          18.0  (mm)__________________________________________________________________________                  Comparative Example                  Run No.Item                   10 11 12 13 14 15 16 17 18__________________________________________________________________________Compounding  Sulfur          1.5                     1.5                        1.5                           1.5                              1.5                                 1.5                                    1.5                                       1.5                                          1.5ingredients  Soxinol ® CZ*.sup.1                  2  2  2  2  2  2  2  2  Soxinol ® DM*.sup.2              2  2  N,N-Ethylenebismaleimide  N,N&#39;-p-Phenylenebismaleimide                        1.5      1.5  N,N&#39;-m-Phenylenebismaleimide                           1.5      1.5  N,N&#39;-(methylene-di-p-       1.5      1.5  phenylene)bismaleimide  N,N&#39;-(Oxydi-p-phenylene)-  bismaleimide  Phthalic anhydride                  1  Pyromellitic anhydride                     1  Phthalic acid         1  N-Cyclohexylthiophthalimide 1  Benzoic acidProperties  MH (kg · cm)                  98 98 102                           101                              102                                 102                                    101                                       102                                          84  Thermal resistance (%)                  72 73 69 69 69 69 70 70 61  Resistance to flex cracking                  11.5                     11.4                        11.6                           11.7                              11.7                                 11.6                                    11.7                                       11.7                                          11.2  (mm)__________________________________________________________________________                  Comparative Example                  Run No.Item                   19 20 21  22                              23 24 25 26 27__________________________________________________________________________Compounding  Sulfur          2.5                     1.5                        1.5                           1.5                              1.5                                 1.5                                    1.5                                       1.5                                          1.5ingredients  Soxinol ® CZ*.sup.1  Soxinol ® DM*.sup.2                  2  2  2  2  2  2  2  2  2  N,N&#39;-Ethylenebismaleimide  N,N&#39;-p-Phenylenebismaleimide  N,N&#39;-m-Phenylenebismaleimide                           1.5      1.5  N,N&#39;-(methylene-di-p-       1.5      1.5  phenylene)bismaleimide  N,N&#39;-(Oxydi-p-phenylene)-      1.5      1.5  bismaleimide  Phthalic anhydride 1  Pyromellitic anhydride                        1  Phthalic acid            1  N-Cyclohexylthiophthalimide    1  Benzoic acid                1Properties  MH (kg · cm)                  109                     84 83 103                              108                                 107                                    109                                       108                                          108  Thermal resistance (%)                  54 60 59 66 67 67 68 67 68  Resistance to flex cracking                  16.9                     11.2                        11.3                           13.8                              13.9                                 14.0                                    13.8                                       13.8                                          13.9  (mm)__________________________________________________________________________ Note: *.sup.1 Soxinol ® CZ: NCyclohexyl-2-benzothiazylsulfenamide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.2 Soxinol ® DM: Dibenzothiazyl disulfide (mfd. by Sumitomo Chemical Co., Ltd.) 
    
     
                                           TABLE 5__________________________________________________________________________                          Example                          Run No.Item                           1    2   3    4   5    6__________________________________________________________________________Compounding   Sulfur                 1.5  1.5 1.5ingredients   Soxinol ® DM*.sup.1                          1    1   1    1   1    1   Soxinol ® TT*.sup.2                          1    1   1    2   2    2   N,N&#39;-Hexamethylenebismaleimide                          1.5           1.5   N,N&#39;-m-Phenylenebismaleimide                               1.5          1.5   N,N&#39;-(methylenedi-p-phenylene)bismaleimide                                   1.5           1.5   Phthalic anhydride     1    1   1    1   1    1   N-Cyclohexylthiophthalimide   Salicylic acidProperties   MH (kg · cm)  104  105 103  82  84   88   Rt (minute)            &gt;10  &gt;10 &gt;10  &gt;10 &gt;10  &gt;10   Thermal resistance (%) 84   84  83   89  89   88   Resistance to flex cracking (mm)                          5.1  5.1 5.1  4.4 4.3  4.2__________________________________________________________________________                        Comparative Example                        Run No.Item                         7 8  9 10                                 11                                   12                                     13                                       14                                         15                                           16                                             17                                               18                                                 19                                                   20__________________________________________________________________________Compounding  Sulfur                1.5                          3  1.5                                1.5                                 1.5                                   1.5                                     1.5                                       1.5ingredients  Soxinol ® DM*.sup.1                        1 1  1 1 1 1 1 1 1 1 1 1 1 1  Soxinol ® TT*.sup.2                        1 1  1 1 1 1 1 1 2 4 2 2 2 2  N,N&#39;-Hexamethylenebismaleimide                               1.5 1.5         1.5  N,N&#39;-m-Phenylenebismaleimide   1.5 1.5         1.5  N,N&#39;-(methylenedi-p-phenylene)bismaleimide                                       1.5         1.5  Phthalic anhydride         1               1  N-Cyclohexylthiophthalimide  1  Salicylic acid                 1Properties  MH (kg · cm) 80                          104                             80                               91                                 92                                   91                                     93                                       91                                         52                                           64                                             51                                               68                                                 69                                                   68  Rt (minute)           2.0                          1.1                             2.0                               7.0                                 7.0                                   7.2                                     7.1                                       7.2                                         4.0                                           3.1                                             4.0                                               8.7                                                 8.3                                                   8.7  Thermal resistance (%)                        75                          64 75                               80                                 81                                   81                                     80                                       81                                         80                                           72                                             79                                               84                                                 88                                                   84  Resistance to flex cracking (mm)                        4.9                          8.2                             5.3                               5.4                                 5.4                                   5.3                                     5.4                                       5.4                                         4.3                                           5.0                                             4.3                                               5.5                                                 5.6                                                   5.7__________________________________________________________________________ Note: *.sup.1 Soxinol ® DM: Dibenzothiazyl disulfide (mfd. by Sumitomo Chemical Co., Ltd.) *.sup.2 Soxinol ® TT: Tetramethylthiuram disulfide (mfd. by Sumitomo Chemical Co., Ltd.)