Abstract:
A substrate for fixing an integrated circuit (IC) element comprises: a substrate for fixing an integrated circuit element includes: a plurality of metal posts that are aligned in a longitudinal direction and a lateral direction in plan view, each of the plurality of metal posts having a first surface and a second surface facing an opposite direction to the first surface, the plurality of metal posts being configured identically; and a joining section that joins each of the plurality of metal posts together at a portion of each of the plurality of metal posts between the first surface and the second surface.

Description:
The entire disclosure of Japanese Patent Application No, 2007-199566, filed Jul. 31, 2007 is expressly incorporated by reference herein. 
     BACKGROUND 
     1. Technical Field 
     The present invention relates to a substrate, a method for fabricating a substrate, a semiconductor device, and a method for fabricating a semiconductor device. 
     2. Related Art 
     Semiconductor packages are roughly classified into peripheral type packages and area type packages. A peripheral type package is a package in which the external terminals are arranged on the periphery of the package, and an area type package is a package in which the external terminals are arranged on the lower surface of the package.  FIGS. 20A through 20C  show typical peripheral type packages called a dual in-line package (DIP), a small out-line package (SOP), and a quad flat package (QFP). The peripheral type package, as shown in  FIG. 20D , includes an integrated circuit (IC) element  210  mounted on a chip-mounting section called a die pad  201 . Electrodes on the IC element  210  and leads  203  of a lead frame are coupled by e.g. gold wires. Then, these elements, not including peripheral portions of the leads  203 , are sealed with resin. Portions of the leads  203  inside the resin package are called internal terminals, and portions of the leads  203  outside the resin package are called external terminals. 
     The area type package, with reference to  FIGS. 21A and 21B  and  FIGS. 22A and 22B , is a package represented by a ball grid array (BGA) package which is fabricated by mounting the IC element  210  on a substrate  211 , electrically coupling the IC element  210  to the substrate  211  with either gold wires, solder, or gold bumps, and sealing the elements such as the IC element  210  with resin. Referring to  FIGS. 21A and 21B , the package in which the substrate  211  is coupled to the IC element  210  with gold wires  213  is called a gold wire BGA package. 
     Also, a package with reference to  FIGS. 22A and 22B  is called a bump BGA package in which the substrate  211  is coupled to the IC element  210  with bumps  223 .  FIGS. 22A and 22B , in particular, show a type of bump BGA that is not sealed with resin. As shown in  FIGS. 21A through 22B , the external terminals of the area type are not the leads but electrodes  225  (or solder balls  19 ) mounted on the rear surface of the substrate  211 . 
     Manufactured also in recent years is a package, with reference to  FIGS. 23A through 23I , which is fabricated by: electroplating columnar-shaped terminals  233  and an columnar-shaped die pad  235  on a metal plate  231 , mounting the IC element  210  on the die pad  235 , coupling the IC element  210  to the terminals  233  with the gold wires  213 , conducting resin sealing, peeling off the metal plate  231  from a resin-formed portion  236 , and dicing into each separate product. 
     More specifically, with reference to  FIGS. 23A and 2313 , a resist is first coated on the metal plate  231 , and the coated metal plate  231  is subjected to exposure and development to form a resist pattern  237 . Then, referring to  FIG. 23C , copper or the like is electroplated on the surface of the metal plate  231  that is exposed at the lower part of the resist pattern  237  so as to form the columnar shaped terminals  233  and die pad  235 . Thereafter, referring to  FIG. 23D , the resist pattern is removed. Then, with reference to  FIG. 23E , the IC element  210  is mounted on the die pad  235  through electroplating, followed by wire bonding. Then, with reference to  FIG. 23F , the IC element, gold wires  213 , etc. are sealed with resin. Referring to  FIG. 23G , the metal plate  231  is then peeled off from the resin-formed portion  236 . Thereafter, referring to  FIGS. 23H and 23I , the resin-formed portion  236  is diced into each separate product, and the package is thereby produced. 
     JP-A-2-240940 discloses a technique in which a peripheral type package is fabricated by: half-etching one surface of a support of a tabular lead frame, mounting an IC element on a die pad of the lead frame, conducting wire bonding and resin sealing, and thereafter removing the support by polishing the other surface of the support whose one surface has been half-etched, thereby fabricating the peripheral type package. Disclosed in JP-A-2004-281486 is a technique intended to enhance versatility of the area type package by radially arranging the wires from the center of the substrate to outside in plan view. 
     In the related art techniques, the peripheral type packages, the area type packages, the package referring  FIGS. 23A through 23I , and the package described in JP-A-2-240940 all require a die pad as an IC element-mounting plane or a substrate such as an interposer. Therefore, depending on the size of the IC element and the number of external outputs from the IC element (i.e., the number of leads or balls), these packages need specific lead frames or specific substrates, or specific photomasks (to form the columnar shapes). In particular, in order to produce large item small volume products, a large number of lead frames or substrates or photomasks need be secured, and this has been a setback in reducing the production costs. 
     Also, in JP-A-2004-281486, an area type package that accommodates all chip sizes is accomplished by radially arranging the wires from the center of the substrate to outside. However, in this technology, it is necessary to arrange the pad terminals of the IC element so as to always overlap planarly with the wires that extend radially from the substrate center. Therefore, there is less degree of freedom of design in laying out the pad terminals. In other words, although the versatility of the package improves, restrictions placed on the IC element increases as well. 
     SUMMARY 
     An advantage of some aspects of the invention is to provide a substrate, a substrate fabrication method, a semiconductor device, and a semiconductor device fabrication method which allow common application of a specification of a wiring board for mounting an IC element, without placing additional restrictions on the IC element. 
     According to a first aspect of the invention, a substrate for fixing an integrated circuit element includes: a plurality of metal posts that are aligned in a longitudinal direction and a lateral direction in plan view, each of the plurality of metal posts having a first surface and a second surface facing an opposite direction to the first surface, the plurality of metal posts being configured identically; and a joining section that joins each of the plurality of metal posts together at a portion of each of the plurality of metal posts between the first surface and the second surface. 
     In this case, the “first surface” of some aspects of the invention is a surface on a side to be coupled to a pad terminal of the IC element, for example, and the “second surface” is a surface on a side of each metal post to be coupled to a motherboard, for example. Also, the “portion” of some aspects of the invention may either be a middle portion between the first and second surfaces or a portion between the middle portion and the second surface, including the second surface. If the “portion” of some aspects of the invention includes the second surface, the “joining section” is formed between the middle portion and the second surface. For example, the joining section may be formed so that the lower surface of the joining section becomes the same surface as the second surface. 
     In a semiconductor device fabrication process, for example, the IC element may be fixed on the first surface of a first metal post, and the first surface of a second metal post may be coupled to the pad terminals of the IC element. Then, the IC element, conductive members, and portions on the side adjacent to the first surfaces of the metal posts may all together be sealed with resin. Then, the joining portions are etched from the side adjacent to the second surface of the substrate and removed so that the metal posts are electrically cut off from each other. 
     Because all of the metal posts of the substrate of the first aspect of the invention have an identical configuration, all of them may be used as die pads for mounting the IC element, or the plurality of them may be used as external terminals of the IC element. Depending on the configuration and size of an IC fixing region established as desired, the plurality of metal posts may be used either as the die pads or the external terminals. Accordingly, it is not necessary to prepare a specific die pad, a specific lead frame, or a specific substrate (e.g., interposer) per each kind of IC element when assembling a semiconductor device. It is possible to commonly apply the specification of the substrate used for element mounting and as the external terminals, without restricting the layout (arrangement position) of the pad terminals of each kind of IC element. As a result, the costs of producing substrates may be reduced. 
     It is preferable that, in the substrate of the first aspect of the invention, the joining section be made of a same material as that of the metal posts. 
     It is preferable that, in the substrate of the first aspect of the invention, the plurality of metal posts be in an identical size. 
     It is also preferable that, in the substrate of the first aspect of the invention, a side surface of each of the plurality of metal posts be cross-sectionally curved. Having such a structure, as compared to a structure in which the side surface of each metal post is not curved (i.e., the side surface of the metal post is perpendicular to both first and second surfaces), it is possible to increase the area of contact between the resin and the side surfaces of the metal posts and to enhance the bond between the resin and the metal posts at a time of, for example, resin-sealing the elements such as the IC element. Such a substrate may therefore contribute to prevention of falling of the metal posts after sealed with resin. 
     It is preferable that, in the substrate of the first aspect of the invention, each of the plurality of metal posts be cross-sectionally constricted. A term “constricted” here indicates a configuration that is narrowed down at the center. 
     In this case, when the portions of the metal posts on the side adjacent to the first surface and the like are sealed with resin, for example, the constricted configuration clutches the first resin, thereby producing an anchor effect. Such a substrate may therefore contribute to prevention of falling of the metal posts after sealed with resin. 
     It is preferable that the substrate according to the first aspect of the invention further include a first plated layer provided the first surface of each of the plurality of metal posts, in that the first plated layer protrudes outside the first surface. 
     In this case, the first plated layer and the metal post together form a shape that looks like the letter “T” in sectional view. When sealing the portions of the metal posts on the side adjacent to the first surface, this letter T catches the resin. Therefore, the anchor effect may be produced by the letter T, and the metal posts may be prevented from falling after sealed with resin. 
     According to a second aspect of the invention, a method for fabricating a substrate for fixing an integrated circuit element includes: providing a plurality of metal posts aligned in a longitudinal direction and a lateral direction in plan view, by partially etching a metal plate from at least a first surface of the metal plate which has a second surface facing an opposite direction to the first surface. In the method, the etching is conducted so that all the plurality of metal posts are configured identically and that the plurality of metal posts are joined together between the first and second surfaces. 
     The method according to the second aspect of the invention enables fabrication of the substrate of the first aspect of the invention. 
     It is preferable that the substrate fabrication method according to the second aspect of the invention further include: providing a first plated layer in a first region of the first surface prior to the forming of the plurality of the metal posts, and the plurality of metal posts are provided in the forming of the plurality of the metal postsby wet etching the metal plate from the first surface using the first plated layer as a mask. 
     In this case, the “first plated layer” and a “second plated layer” of some aspects of the invention may take a single layer structure or a multilayer structure. Also, the “first plated layer” and the “second plated layer” may have the same structure or different structures. To express the multilayer structure in the order of lower layer/middle layer/upper layer, each of the “first plated layer” and the “second plated layer” is Ni/Pd/Au, Ni/Au, or Ag, for example. 
     The fabrication method according the second aspect of the invention allows fabrication of the substrate such that the side surface of the metal post is cross-sectionally curved. Additionally, the wet etching of the metal plate may be done by spray type wet etching. The spray type etching promotes etching in the depth direction if the spraying angle of an etchant is set perpendicular to the surface of the metal plate, and promotes etching in the lateral direction (i.e., side etching) if the spraying angle is set diagonal to the surface of the metal plate. Moreover, by increasing the spraying pressure of the etchant, the etching speed may increase. Therefore, it is possible to form the side surface of each metal post into the sectionally constricted configuration (i.e., narrowed down at the center) by, for example, spray etching the metal plate while adjusting the spraying angle and pressure against the surface of the metal plate. As a consequence, the method also allows fabrication of the substrate such that the metal post is sectionally constricted. 
     It is preferable that the substrate fabrication method according to the second aspect of the invention further include: providing a second plated layer in a second region of the second surface prior to the forming of the plurality of metal posts, and the plurality of metal posts are provided in the forming of the plurality of metal posts by wet etching the metal plate from the first surface using the first plated layer as the mask and from the second surface using the second plated layer as a mask. 
     It is preferable that, in the substrate fabrication method according to the second aspect of the invention, the metal plate is wet etched, in the forming of the plurality of metal posts, from the first surface under a condition that the metal plate is more readily etched than the first plated layer In this case, if the “first plated layer” of some aspects of the invention is composed of e.g. Ni/Pd/Au, Ni/Au, or Ag, and if the “metal plate” is made from a copper plate, the wet etching using a ferric chloride solution or an alkaline solution (hereunder referred to as alkaline etchant) may be employed as an example of “a condition in which the first plated layer is more readily etched than the metal plate.” 
     By this method, it is possible to subject the metal plate to isotropic etching using the first plated layer as a mask and to narrow down each metal post located directly under the first plated layer. That is, because the first plated layer may protrude outside the first surface of the metal post, it is possible to produce the substrate of the first aspect of the invention. 
     According to a third aspect of the invention, a semiconductor device includes: a plurality of metal posts that are aligned in a longitudinal direction and a lateral direction in plan view, each of the plurality of metal posts having a first surface and a second surface facing an opposite direction to the first surface, the plurality of metal posts having a first metal post and a second metal post; an integrated circuit element that is fixed on the first surface of the first metal post; a first conductive member that couples the first surface of the second metal post to a pad terminal of the integrated circuit element; and a first resin that seals the integrated circuit element, the first conductive member, and a part of the plurality of metal posts. The second surface of the plurality of metal posts is exposed from the first resin, and a side surface of each of the plurality of metal posts is cross-sectionally curved. 
     If the “pad terminal” and the “second metal post” of some aspects of the invention are electrically coupled by wire bonding, the “first conductive member” is a gold wire, for example. If this coupling is conducted by face-down bonding, the “first conductive member” is a stud bump made of e.g. gold. The layout interval (pitch) between the stud bumps is, for example, an integral multiplication of the pitch between the metal posts. 
     With the semiconductor device of the third aspect of the invention, it is possible to use the plurality of metal posts as the die pads for mounting the IC elements or the external elements of the IC elements and to use the plurality of metal posts either as the die pads or the external terminals depending the configuration and the size of the IC fixation region that are established as desired. Therefore, it is not necessary to prepare a specific die pad, a specific lead frame, or a specific substrate (e.g., interposer) per each kind of the IC element when assembling the semiconductor device. It is possible to commonly apply the specification of the substrate used for element mounting and as the external terminals, without restricting the layout (arrangement position) of the pad terminals of each kind of IC element. As a result, the costs of producing the semiconductor device may be reduced. 
     Also, with the semiconductor device of the third aspect of the invention, metals are not gathered at one place unlike the die pads of the related art. Because the metal posts functioning as the die pads or the external terminals are distributed within the resin package, it is possible to decentralize the locations of moisture aggregation and to reduce concentration of water vapor pressure. Therefore, it is possible to suppress cracking of the resin package during a reliability test associated with moisture absorption and heating, and to thereby enhance the reliability of the semiconductor device. 
     Moreover, with the semiconductor device of the third aspect of the invention, the side surfaces of the plurality of metal posts are cross-sectionally curved. This may increase the area of contact between the first resin and the side surfaces of the metal posts, as compared to when the side surfaces are not curved (that is, the side surfaces of the metal posts are perpendicular to the first and second surfaces) and, thus, increase the bond between the first resin and the metal posts. As a result, falling of the metal posts from the first resin may be prevented. 
     It is preferable that, with the semiconductor device of the third aspect of the invention, each of the plurality of metal posts is cross-sectionally constricted. In this case, because the constricted configuration clutches the first resin, the anchor effect may be produced, and the metal posts may be prevented from falling from the first resin. 
     It is preferable that the semiconductor device of the third aspect of the invention further includes a first plated layer that is provided on the first surface of each of the plurality of metal posts. 
     In this case, the first plated layer and the metal posts together form a shape that looks like the letter “T” in sectional view, and it is this letter T that catches the first resin. Therefore, the anchor effect may be produced by the letter T, and the metal posts may be prevented from falling from the first resin. 
     It is preferable that the semiconductor device of the third aspect of the invention further includes a second resin that seals a portion of the plurality of metal posts, the portion being exposed from the first resin. Each of the plurality of metal posts includes, between the first and second surfaces, a first portion having a first width and a second portion having a second width that is cross-sectionally wider than the first width, and the second portion is cross-sectionally interposed between the first and second resins. 
     In this case, because the second portion is interposed and fixed between the first and second resins, the metal posts may be prevented from falling from the first resin. 
     It is preferable that semiconductor device of the third aspect of the invention further include: a second plated layer that is provided on the second surface of each of the plurality of metal posts; and a second conductive member that is provided over part of the second plated layer. The second resin covers a periphery of the second plated layer, and the second conductive member covers a portion of the second resin covering the periphery of the second plated layer. 
     In this case, because the metal posts having the second plated layers formed thereon may be held by the second resin, and because this second resin may be held by the second conductive member, it is possible to prevent the metal posts from falling from the first resin. 
     It is preferable that semiconductor device of the third aspect of the invention further include: a motherboard that is coupled to each of the plurality of metal posts; and a third resin sealing, between the first resin and the motherboard, the portion of each of the plurality of metal posts that is exposed from the first resin. In this case, the “substrate” of some aspects of the invention is a substrate for primary packaging, and the “motherboard” is a substrate for secondary packaging. 
     With the semiconductor device of the third aspect of the invention, it is possible to increase the reliability of connection between the IC elements and the motherboard. 
     It is preferable that semiconductor device of the third aspect of the invention further include: a third metal post and a fourth metal post that are included in the plurality of metal posts; a passive component that is fixed on the first surface of the third metal post; and a third conductive member that coupls the fourth metal post on the first surface to a terminal section of the passive component. The first resin seals the passive component and the third conductive member. 
     In this case, similarly to the first and second metal posts, the third and fourth metal posts may also be prevented from falling. 
     According to a fourth aspect of the invention, a method for fabricating a semiconductor device includes: (a) providing a plurality of metal posts aligned in a longitudinal direction and a lateral direction in plan view, by partially etching a metal plate from at least a first surface of a metal plate having a second surface facing an opposite direction to the first surface, and the etching is conducted so that the plurality of metal posts are configured identically and joined together between the first and second surfaces by joining sections; (b) fixing an integrated circuit element on the first surface of a first metal post of the plurality of metal posts; (c) coupling a second metal post of the plurality of metal posts to a pad terminal of the integrated circuit element using a first conductive member; (d) sealing the integrated circuit element, the first conductive member, and a portion of the plurality of metal posts on a side adjacent to the first surface with a first resin; and (e) removing the joining sections by etching from the second surface after the sealing of the integrated circuit element. 
     In this case, if the IC element is to be fixed to the substrate by face-down bonding, in particular, the IC element should be designed so that the pitch between the pad terminals (e.g., gold stud bumps or solder bumps) of the IC element becomes the integral multiplication of the pitch of the metal posts. 
     The fabrication method of the fourth aspect of the invention enables fabrication of the semiconductor device of the third aspect of the invention. 
     The term “first resin” of some aspects of the invention is a mold resin, for example, and the “second resin” is a solder resist, for example. Also, the “third resin” is an underfill. If the expansion rates of the mold resin, the solder resin, and the underfill are α 1 , α 2 , and α 3 , respectively, the magnitude relation among them is α 1 &lt;α 3 &lt;α 2 , for example. The smaller the expansion rate is, the more expandable the resin is. In other words, the mold resin is not as expandable than the solder resist or the underfill. Additionally, if the elasticity modulus of the mold resin, the solder resist, and the underfill are 1β, 2β, and 3β, respectively, the magnitude relation among them is 1β&gt;3β&gt;2β, for example. The smaller the elasticity modulus is, the more elastic the resin is, and the larger the elasticity modulus is, the harder the resin is. In other words, the mold resin is harder than the solder resist or the underfill. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The invention will be described with reference to the accompanying drawings, wherein like numbers reference like elements. 
         FIGS. 1A through 1F  are diagrams showing a method for fabricating a substrate  10  according to a first embodiment. 
         FIGS. 2A through 2G  are diagrams showing the method for fabricating the substrate  10  according to the first embodiment. 
         FIGS. 3A through 3E  are diagrams showing a method for fabricating a semiconductor device  100  according to the first embodiment. 
         FIGS. 4A and 4B  are diagrams showing a dicing step according to the first embodiment. 
         FIG. 5  is a diagram exemplarily showing the configuration of the substrate  10 . 
         FIG. 6  is a diagram exemplarily showing the positions for forming recognition marks  8  of the substrate  10 . 
         FIG. 7  is a diagram exemplarily showing the sectional configuration of the semiconductor device  100 . 
         FIGS. 8A through 8C  are diagrams showing a method for fabricating a semiconductor device  110  according to a second embodiment. 
         FIGS. 9A through 9C  are diagrams showing a method for fabricating a semiconductor device  120  according to a third embodiment. 
         FIG. 10  is a diagram exemplarily showing the sectional configuration of the semiconductor device  120 . 
         FIG. 11  is a diagram exemplarily showing the composition of a semiconductor device  130  according to a fourth embodiment. 
         FIGS. 12A through 12C  are diagrams showing a method for fabricating a semiconductor device  140  according to a fifth embodiment. 
         FIGS. 13A through 13D  are diagrams showing the method for fabricating the semiconductor device  140  according to the fifth embodiment. 
         FIGS. 14A through 14F  are diagrams showing a method for fabricating a substrate  20  according to a sixth embodiment. 
         FIGS. 15A through 15G  are diagrams showing the method for fabricating the substrate  20  according to the sixth embodiment. 
         FIGS. 16A through 16D  are diagrams showing a method for fabricating a semiconductor device  150  according to the sixth embodiment. 
         FIGS. 17A through 17C  are diagrams exemplarily showing the compositions of semiconductor devices  160 ,  170 , and  180  according to a seventh embodiment. 
         FIGS. 18A through 18E  are diagrams showing a method for fabricating a semiconductor device  190  according to an eighth embodiment. 
         FIGS. 19A through 19E  are diagrams showing another example of the side surface configuration of a post  5 . 
         FIGS. 20A through 20D  are diagrams showing examples of the related art. 
         FIGS. 21A and 21B  are diagrams showing examples of the related art. 
         FIGS. 22A and 22B  are diagrams showing examples of the related art. 
         FIGS. 23A through 23I  are diagrams showing examples of the related art. 
     
    
    
     DESCRIPTION OF EXEMPLARY EMBODIMENTS 
     Embodiments of the invention will now be described with reference to the accompanying drawings. 
     1. First Embodiment 
     In the first embodiment, a substrate fabrication method will be described first. Then, a method for fabricating a semiconductor device by mounting an integrated circuit (IC) element onto this substrate will be described. In the first embodiment, two fabrication techniques will be described with reference to  FIGS. 1A through 1F  and  2 A through  2 G to exemplify the substrate fabrication method.  FIGS. 1A through 1F  illustrate the fabrication method employing a semi-additive technique, and  FIGS. 2A  through  2 G illustrate the fabrication method employing a subtractive technique. Description of these two techniques is followed by descriptions of processes of mounting the IC element and resin sealing with reference to  FIGS. 3A through 3E  and of a dicing process with reference to  FIGS. 4A and 4B . 
       FIGS. 1A through 1F  are sectional diagrams showing the method (semi-additive technique) for fabricating a substrate  10  according to the first embodiment of the invention. First, a copper plate  1  with reference to  FIG. 1A  is prepared. The vertical and horizontal sizes of the copper plate  1  in plan view may be any sizes larger than the dimensional outline of a package of the semiconductor device made from the copper plate  1 . The thickness of the copper plate  1  is about 0.10 to 0.30 mm, for example. Then, referring to  FIG. 1B , photoresists  2   a  and  2   b  are coated on a front surface and a rear surface of the copper plate  1 , respectively. The photoresists  2   a  and  2   b  may be of positive type or negative type, for example. 
     Then, referring to  FIG. 1C , the photoresists are subjected to exposure and development so as to expose regions for forming a plurality of cylindrical electrodes (hereunder referred to as posts) and to form resist patterns  2   a ′ and  2   b ′ over the remaining regions. In this case, the resist patterns  2   a ′ is formed on the front surface of the copper plate  1 , while the resist pattern  2   b ′ is formed on the rear surface of the copper plate  1 . 
     Then, referring to  FIG. 1D , plated layers  3   a  and  3   b  are provided by e.g. electrolytic plating in the regions exposed from the resist patterns  2   a ′ and  2   b ′ (i.e., the regions for forming the posts). In this case, the plated layer  3   a  is formed on the front surface of the copper plate  1 , while the plated layer  3   b  is formed on the rear surface of the copper plate  1 . 
     Referring to  FIG. 1D , both of the plated layers  3   a  and  3   b  have a double layer structure. However, the plated layers  3   a  and  3   b  may have a multilayer structure with more than two layers or a single layer structure. For example, the plated layers  3   a  and  3   b  may employ either a triple layer structure composed of Ni (lower layer)/Pd (middle layer)/Au (upper layer), a double layer structure composed of Ni (lower layer)/Au (upper layer), or a single structure made of Ag. If the plated layers  3   a  and  3   b  employ any of these structures, it is preferable that the Ni layer or the Ag layer be made into a thick layer. 
     Thereafter, referring to  FIG. 1E , the resist patterns are removed from the front and rear surfaces of the copper plate  1 . Then, referring to  FIG. 1F , the copper plate  1  is etched from the side adjacent to the front surface using the plated layer  3   a  as a mask to provide recesses  4   a , while it is also etched from the side adjacent to the rear surface using the plated layer  3   b  as a mask to provide recesses  4   b . In this case, the copper plate  1  is half-etched from both the front and rear surfaces to form a plurality of posts  5 , while simultaneously forming joining sections  6  for horizontally joining these posts  5  together in sectional view. That is, the etching is stopped before the copper plate  1  between the plurality of posts  5  is completely etched and disappeared (i.e., before penetrated). Produced by this half etching is the substrate  10  having the posts that are joined to each other at portions between the front surface and the rear surface of the copper plate  1 . 
     Referring to  FIG. 1F , the half etching of the copper plate  1  is conducted by dip type or spray type wet etching. The etchant used is a ferric chloride solution or an alkaline etchant (hereunder referred to as alkaline solution), for example. 
     If the plated layers  3   a  and  3   b  are composed of, e.g., Ni/Pd/Au or Ni/Au, it is preferred to use the alkaline solution as the etchant. Since Ni is not readily dissolved in alkaline solution, the plated layers  3   a  and  3   b  are left unetched and protrude outside from both front and rear surfaces of the posts  5 , with reference to  FIG. 1F . Similarly, if the plated layers  3   a  and  3   b  are made of e.g. Ag, it is preferred to use the ferric chloride solution as the etchant. Since Ag is not readily dissolved in ferric chloride solution, the plated layers  3   a  and  3   b  are left unetched and protrude outside from both front and rear surfaces of the posts  5 , with reference to  FIG. 1F . 
     The recesses  4   a  and  4   b  to be provided on the respective front and rear surfaces of the copper plate  1  may be formed in an identical depth or different depths. For example, if the recesses  4   a  and  4   b  are to be formed by the spray type wet etching, the time for etching the front surface is set twice the time for etching the rear surface. As a consequence, the recesses  4   a  are formed in a depth of e.g. 0.1 mm on the front surface, and the recesses  4   b  are formed in a depth of e.g. 0.05 mm on the rear surface. 
     In the half etching process with reference to  FIG. 1F , there is a case in which the surface of the copper plate  1  exposed by use of the etchant is darkened from oxidation. Thus, after the half etching, the substrate  10  may be rinsed to remove the oxidized and darkened layer. By this rinsing treatment, the oxidized layer is removed from the exposed surface of the copper plate  1 , and the copper plate  1  restores gloss. Additionally, after the rinsing treatment, the exposed surface of the copper plate  1  may be coated with an antioxidant. This prevents oxidation of the copper plate  1  in assembling processes that follow hereafter. 
     Before etching the copper plate  1 , referring to  FIG. 1E , a plate-protecting photoresist (not shown) may be additionally provided on the front and rear surfaces of the copper plate  1 . Because the copper plate  1  is etched using, as a mask, the plated layers  3   a  and  3   b  covered by this photoresist, the plated layers  3   a  and  3   b  is protected from the etchant. 
     The plate-protecting photoresist may be left unremoved even after the recesses  4   a  and  4   b  have been provided. Thus, in the subsequent assembling processes, also, the plated layers  3   a  and  3   b  stay protected. The plate-protecting photoresist may be left unremoved on both of the plated layers  3   a  and  3   b  or only on the plated layer  3   b . If the photoresist remains only on the plated layer  3   b , the layer  3   b  can stay protected in the subsequent assembling process. 
     Also, this plate-protecting photoresist may be provided not before but after etching the copper plate  1 . With such a composition, also, the plated layers  3   a  and  3   b  are kept protected even in the subsequent assembling processes. 
     The other technique for fabricating the substrate will be described with reference to  FIGS. 2A through 2G . 
       FIGS. 2A through 2G  are sectional diagrams showing the method (subtractive technique) for fabricating the substrate  10  according to the first embodiment of the invention. The constituting elements of  FIGS. 2A through 2G  that are identical to those of  FIGS. 1A through 1F  are allotted the same reference numbers, and explanations thereof will not be repeated. 
     At first, referring to  FIG. 2A , the copper plate  1  is prepared. Then, referring to  FIG. 2B , plated layers  3   a ′ and  3   b ′ are provided by e.g. electrolytic plating on the front and rear surfaces of the copper plate  1 , respectively. In  FIG. 2B , similarly to  FIGS. 1A through 1F  both of the plated layers  3   a ′ and  3   b ′ also have the double layer structures. However, the plated layers  3   a ′ and  3   b ′ may have the multilayer structure with more than two layers or the single layer structure. For example, the plated layers  3   a ′ and  3   b ′ may employ either a multilayer structure composed of Ni (lower layer)/Pd (middle layer)/Au (upper layer), a double layer structure composed of Ni (lower layer)/Au (upper layer), or a single structure made of Ag. If the plated layers  3   a ′ and  3   b ′ take any of these structures, it is preferable that the Ni layer or the Ag layer be made into a thick layer. 
     Next, with reference to  FIG. 2C , the front and rear surfaces of the copper plate  1  are coated with photoresists  7   a  and  7   b , respectively. Then, referring to  FIG. 2D , the photoresists  7   a  and  7   b  are subjected to exposure and development so as to expose the regions for forming the posts, and resist patterns  7   a ′ and  7   b ′ are formed to cover the other regions. Thereafter, the plated layers  3   a ′ and  3   b ′ are etched using the resist patterns  7   a ′ and  7   b ′ as a mask and removed. As a result, referring to  FIG. 2E , the patterned plated layers  3   a  and  3   b  are formed on the respective front and rear surfaces of the copper plate  1 . 
     If the plated layers  3   a  and  3   b  are composed of Ni/Pd/Au or Ni/Au, aqua rigia is used for example as an etchant for etching the plated layers. If the plated layers  3   a  and  3   b  are made of Ag, nitric acid solution is used as the etchant, for example. After etching the plated layers, the copper plate  1  is etched, with reference to  FIG. 2F , from both front and rear surfaces using, as a mask, the resist patterns  7   a ′ and  7   b ′ and the plated layers  3   a  and  3   b  covered by these resist patterns  7   a ′ and  7   b ′, respectively. As a result, the recesses  4   a  are formed on the front surface, and the recesses  4   b  are formed on the rear surface of the copper plate  1 . 
     As in the fabrication method shown with reference to  FIGS. 1A to 1F , in the fabrication method referring to  FIGS. 2A through 2G , also, the copper plate  1  is half-etched from the front and rear surfaces so as to form the plurality of posts  5  while simultaneously forming the joining sections  6  for horizontally joining these posts  5  in sectional view. Specifically, the etching is stopped before the copper plate  1  between the plurality of posts  5  is completely etched and disappeared (i.e., before penetrated). Produced by this half etching is the substrate  10  having the posts that are joined to each other at the portions between the front surface and the rear surface of the copper plate  1 , for example. The half etching of the copper plate  1 , with reference to  FIG. 2F , is conducted by dip type or spray type wet etching. The etchant used is a ferric chloride solution or an alkaline solution, for example. 
     If the plated layers  3   a  and  3   b  are composed of, e.g., Ni/Pd/Au or Ni/Au, it is preferable to use the alkaline solution as the etchant. If the plated layers  3   a  and  3   b  are made of e.g. Ag, it is preferable to use the ferric chloride solution as the etchant. By choosing the etchant, the plated layers  3   a  and  3   b  can be left unetched and protrude outside from the front and rear surfaces of the posts  5 , with reference to  FIG. 2F . 
     The recesses  4   a  and  4   b  provided on the respective front and rear surfaces of the copper plate  1  may have an identical depth or different depths. For example, if the recesses  4   a  and  4   b  are to be formed by the spray type wet etching as in the fabrication method with reference to  FIGS. 1A through 1F , the time required for the wet etching may be adjusted in order to produce the recesses having a depth of e.g. 0.1 mm on the front surface, and the recesses having a depth of e.g. 0.05 mm on the rear surface. As in the method with reference to  FIGS. 1A through 1F , after providing these recesses  4   a  and  4   b , the oxidized and darkened layer may be removed by rinsing the substrate  10 . This restores gloss of the copper plate  1 . Additionally, after the rinsing treatment, the exposed surface of the copper plate  1  may be coated with an antioxidant. This prevents oxidation of the copper plate  1 . 
     Thereafter, with reference to  FIG. 2G , the resist patterns are removed from the substrate  10 . 
     The resist removal process with reference to  FIG. 2G  is not an essential process in this embodiment. In this embodiment, the resist patterns may be left unremoved on both surfaces of the substrate  10 . Also, referring to  FIG. 2G , the resist pattern only on the front surface of the substrate  10  may be removed, leaving the resist pattern on the rear surface. Accordingly, the resist pattern may be used as a film for protecting both the plated layer  3   a  and the plated layer  3   b , or the plated layer  3   b  alone, in the subsequent assembling processes. 
     In the fabrication method with reference to  FIGS. 2A through 2G , the process of  FIGS. 2C through 2E  may be conducted not by a chemical process but by a physical process. For example, it is also possible to remove part of the plated layers  3   a  and  3   b  by sandblasting or by using a cutting instrument. In a sandblasting process, glass particles, for example, are blasted to abrade part of the plated layers  3   a  and  3   b . By adjusting the blasting conditions, such as the amount of glass particles and blasting pressure, it is possible to process the plated layers  3   a  and  3   b  as shown in  FIG. 2E . 
       FIG. 5  is a diagram exemplarily showing the configuration of the substrate  10 . The structure of the substrate  10  provided by the method referring to  FIGS. 1A through 1F  is identical to the structure of the substrate  10  provided by the method referring to  FIGS. 2A through 2G . The sterical configuration of the substrate  10  is illustrated in  FIG. 5 . Specifically, the substrate  10  includes the plurality of posts  5  which are arranged vertically and horizontally and joined together at the portions between the front surface and the rear surface (e.g., intermediate portions in the thickness direction). The side surface of each post  5  is curved (i.e., bowl-shaped) such that the diameter of the post  5  gradually increases from the front surface, or from the rear surface, to the intermediate portion. 
     The method for fabricating the semiconductor device by mounting the IC element in a bare state onto the substrate  10  will now be described. 
       FIGS. 3A through 3E  are sectional diagrams showing the method for fabricating a semiconductor device  100  (from a recognition mark forming step to a resin sealing step) according to the first embodiment of the invention. Referring to  FIG. 3A , a recognition mark  8  is first provided on the surface of the substrate  10 . In this case, the plurality of posts  5  of the substrate  10  have the same configuration, size, and color. Also, the distance between all adjacent posts  5  (the distance between the centers of all adjacent posts  5 ) in the vertical direction are identical in plan view, for example, and the distance between all adjacent posts  5  (distance between the centers of all adjacent posts  5 ) in the horizontal direction are identical in plan view. Therefore, the IC fixation region may not be recognized when mounting (fixing) the IC element onto the substrate  10 , and the IC element may not be aligned to the IC fixation region with precision. In this case, the distances between the adjacent posts  5  in the vertical direction may all be equal to the distances between the adjacent posts  5  in the horizontal direction. 
     Therefore, in this embodiment, the recognition mark  8  is provided by coloring the surface (upper surface) of each post  5  located at a desired position using an inkjet technique or a laser marking technique. To provide the recognition mark  8  by the inkjet technique, a thermo-resistive multicolor ink or a multicolor plate or the like may be employed as the coloring material. 
     If the multicolor plate is employed, a plating process using a mask may be performed instead of performing the inkjet technique. However, because the plating process using the mask requires various mask original plates in accordance with the recognition marks  8  to be formed in desired positions, the production costs may increase. Therefore, in the process of providing the recognition marks  8 , it is desirable to use the inkjet technique or the laser marking technique rather than the plating process using the mask. 
       FIG. 6  is a diagram exemplarily showing the alignment positions of the recognition marks  8 . The alignment positions of the recognition marks  8  may be located inside or outside the regions for fixing the IC element (i.e., IC fixing regions) or may be located both inside and outside the regions.  FIG. 6  shows a case in which the recognition marks  8  are aligned outside an IC fixing region. Each recognition mark  8  keeps a certain distance from the IC fixing region on an extension of a diagonal line of this IC fixing region (e.g., planarly rectangular in shape). The layout interval (pitch) between the recognition marks  8  is fixed, for example. The recognition marks  8  are colored just so that they are recognizable through a camera or the like when mounting the IC element onto the substrate  10 .  FIG. 6  shows an example of providing black recognition marks  8 . 
     In  FIG. 6 , two recognition marks  8  correspond to one IC fixing region, for example. However, if the product is such that has some degree of freedom in precision-aligning the IC element on the substrate  10  (i.e., the precision required is not very high), one recognition mark  8  may correspond to one IC fixing region. Often, products that employ wire bonding for connection of the IC element with the posts  5  have some freedom in precision aligning (i.e., not very high precision is required). For such products, it is possible to reduce the number of the recognition marks  8  that correspond to one IC fixing region. For example, a single recognition mark  8  may be provided on a point at the intersection of the diagonal lines of the IC fixing region or on a point at the intersection of the diagonal lines of dicing lines. 
     Also, products that employ the face-down bonding to couple the IC element to the posts  5  often do not have much freedom in precision aligning (i.e., high alignment precision is required). For such products, it is possible to increase the number of the recognition marks  8  corresponding to one IC fixing region. For example, three recognition marks  8  may correspond to one IC fixing region. Thus, in the embodiment, a desired number of the recognition marks  8  are provided with respect to the kind (model) of the semiconductor device, packaging method, precision required in the alignment, and so forth. 
     Referring now to  FIG. 3B , the IC fixing region is recognized using the recognition mark  8 . For example, a region having a certain distance in a certain direction (in the right direction of  FIG. 3B  in sectional view) from the recognition mark  8  is recognized as the IC fixing region. Then, an IC element  11  is aligned to the recognized IC fixing region, and, while in this aligned state, the IC element  11  is mounted onto the plurality of posts  5  in the IC fixing region. By this technique, the IC element  11  is aligned to the IC fixing region with precision, and the IC element  11  is mounted onto the substrate  10  with minor misalignment. In this die attaching process, an adhesive  12  is used to mount the IC element  11  onto the posts  5 . The adhesive  12  used is a thermo-curing agent in a form of paste or sheet, for example. 
     Then, referring to  FIG. 3C , the upper surfaces of the posts  5  in the region other than the IC fixing region (i.e., the region not directly under the IC element) are coupled to the pad terminals provided on the active surface of the IC element  11  with gold wires  13 , for example. In this case, the posts  5  that become the external terminals are recognized using the recognition mark  8  as a marker, and the recognized posts  5  may be coupled to ends of the gold wires  13 . By this technique, it is possible to correctly recognize the posts  5  that become the external terminals, out of the plurality of posts  5 , and to connect the gold wires  13  to the recognized posts  5  with precision. If the recognition mark  8  is conductive as are the posts  5  or as is the plated layer  3   a , the posts  5  with the recognition mark  8  formed thereon may be coupled to the gold wires  13 , and these posts  5  may be used as the external terminals. 
     Referring now to  FIG. 3D , the entire upper part of the substrate  10  that includes the IC element  11 , gold wires  13 , and the posts  5  are sealed with a mold resin  14 . The mold resin  14  is a thermo-curing epoxy resin, for example. In this resin-sealing process, for example, the side adjacent to the front surface of the substrate  10  including the IC element  11  is covered by the cavity, and pressure inside the cavity is reduced. The mold resin  14  is then supplied into the depressurized cavity. By this supply of resin under reduced pressure, the mold resin  14  is satisfactorily supplied and filled in the cavity, and, with reference to  FIG. 3D , the recesses  4   a  is filled with the mold resin  14  without creating voids. 
     Thereafter, the joining sections  6  joining the posts  5  together are removed by etching from the side adjacent to the rear surface. The joining sections  6  are etched using the same solution as used when forming the recesses  4   a  and  4   b , such as the ferric chloride solution or the alkaline solution, for example. As a result, with reference to  FIG. 3E , the adjacent posts  5  are electrically disconnected from each other, and the posts  5  connected to the gold wires  13  can be used as electrically independent external terminals. Also, because an upper surface side portion of each post  5  is fixed with the mold resin  14 , the position of the posts  5  are maintained even after removing the joining sections. 
     If the photoresist (not shown) remains on the rear surface of the plated layer  3   b  as a film for protecting the layer  3   b , this photoresist is removed after etching the joining sections. 
     If the plated layer  3   b  is an Ag plate, the Ag plate may be removed, and another plating process may be conducted. That is, the Ag plate may be removed, and, thereafter, a different kind of plate may be reapplied as the plated layer  3   b . An example of such a different kind of plate is Ni/Pd/Au, Ni/Au, or solder. Such reapplication of the plated layer  3   b  may be conducted after removing the photoresist if the photoresist is formed on the rear surface, or after removing the joining sections if the photoresist is not formed on the rear surface. 
     Next, the mold resin  14  is diced into separate pieces. In this dicing process, the mold resin  14  is diced into separate resin packages along the dicing lines, while an excess portion of the resin unusable as products is cut off and removed. The dicing of the mold resin  14  is conducted using, for example, the exposed portions on the rear surfaces of the posts  5  as the mark. In this dicing process, referring to  FIG. 4A , the terminal sections (i.e., posts  5 ) may be diced with blades  15  having the same size or larger than the terminals. Alternatively, referring to  FIG. 4B , the cutting may be conducted between the terminals (i.e., between one post  5  and its adjacent post  5 ) using the blades  15  having the same as or narrower than the half etching width. Alternatively, referring to  FIG. 4A , the posts  5  having the recognition mark  8  formed thereon may be cut off. The semiconductor device  100  is thereby produced. 
     If the posts  5  having the recognition mark  8  formed thereon are diced (i.e., if the dicing lines overlap with the recognition mark  8 ), the recognition mark  8  naturally does not remain within the semiconductor device  100 . Also, if the recognition mark  8  is inside the dicing lines, the recognition mark  8  remains within the device  100  even after the dicing, while, if the recognition mark  8  is outside the dicing lines, the recognition mark  8  does not remain within the device  100  after the dicing. Depending on the positional relation between the dicing lines and the recognition mark  8 , the recognition mark  8  may or may not remain in the device  100 . 
     As described, according to the first embodiment of the invention, the plurality of posts  5  may be used as the die pads of the IC element  11  or as external terminals of the IC element  11 , and, depending on the configuration and size of the IC fixing region that are established as desired, it is possible to use the plurality of posts  5  either as the die pads or the external terminals. Accordingly, it is not necessary to prepare a specific die pad, a specific lead frame, or a specific substrate (e.g., interposer) per each kind of IC element  11  when assembling the semiconductor device  100 . It is possible to commonly apply the specification of the substrate used for element mounting and as the external terminals, without restricting the layout (arrangement position) of the pad terminals of each kind of IC element  11 . As a result, the costs of producing the semiconductor device may be reduced. 
     Additionally, the metal is not gathered in one place unlike the die pads of the related art. Because the posts  5  that function as the die pads or the external terminals are distributed within the resin package, it is possible to spread the positions of moisture aggregation and to reduce concentration of water vapor pressure. As a result, it is possible to suppress cracking of the resin package during a reliability test associated with moisture absorption and heating (a test to examine whether or not malfunction occurs to the resin package made from the mold resin  14  when the resin package is heated while left under a high moisture atmosphere) and to thereby enhance the reliability of the semiconductor device  100 . 
     Moreover, only a desired number of recognition marks  8  are provided with respect to the kind (model) of the semiconductor device, packaging method, precision required in the alignment, and so forth. By the die attaching process, the IC fixing region is recognized using the recognition marks  8  as a marker. Through such a process, the IC fixing region is correctly recognized. As a result, the IC element  11  is aligned to the IC fixing region with precision, and the IC element  11  is mounted onto the posts  5  in the IC fixing region with minor misalignment. 
     Also, with reference to  FIG. 7 , the side surface of each post  5  is sectionally curved, and the recesses  4   a  and  4   b  between the adjacent posts  5  are sectionally bowl-shaped. Accordingly, it is possible to increase the area of contact between the mold resin  14  and the side surface of the post  5 , as compared to when the side surface of the post  5  is not curved (that is, the side surface of the post  5  is perpendicular to the front and rear surfaces of the same) and to increase the bond between the first resin and the post  5 . 
     Furthermore, the plated layer  3   a  formed on the surface of each post  5  protrudes from the surface to outside, and the sectional configurations of the plated layer  3   a  and the post  5  together form the letter “T” shape as expressed in dotted lines in  FIG. 7 . This protrusion of the plated layer  3   a  catches the mold resin  14 , and the plated layer  3   a  thereby produces the anchor effect. 
     As described, in the first embodiment of the invention, the posts  5  are pressed toward the mold resin  14  and prevented from falling from the mold resin  14  because of the following two countermeasures against falling: (a) curved configuration of the side surface of each post  5 , and (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T. 
     In the first embodiment, the copper plate  1  corresponds to the “metal plate” of the embodiments of the invention, and the front surface of the copper plate  1  corresponds to the “first surface” of the embodiments of the invention, and the rear surface of the copper plate  1  corresponds to the “second surface” of the embodiments of the invention. Also, the post  5  corresponds to the “metal post” of the embodiments of the invention, and the post  5  having the IC element  11  mounted thereon corresponds to the “first metal post” of the embodiments of the invention, and the post  5  coupled to the gold wire  13  via the plated layer  3   a  corresponds to the “second metal post” of the embodiments of the invention. Further, the gold wire  13  corresponds to the “first conductive member” of the embodiments of the invention, and the mold resin  14  corresponds to the “first resin” of the embodiments of the invention. Furthermore, the plated layer  3   a  corresponds to the “first plated layer” of the embodiments of the invention, and the plated layer  3   b  corresponds to the “second plated layer” of the embodiments of the invention. 
     2. Second Embodiment 
       FIGS. 8A through 8C  are sectional diagrams showing the method for fabricating a semiconductor device  110  according to the second embodiment of the invention. Explained in this embodiment are cases in which the recesses  4   b  on the side adjacent to the rear surface of the substrate  10  are filled with a resist after penetrating the rear surface (i.e., removing the joining sections  6 ) as shown in  FIG. 3E , and in which Ni/Pb/Au or Ni/Au is used as the solder plate  3   b  on the side adjacent to the rear surface or in which a solder plate is additionally provided on the plated layer  3   b  on the side adjacent to the rear surface. The constituting elements of  FIGS. 8A through 8C  that are identical to those of the first embodiment are allotted the same reference numbers, and explanations thereof will not be repeated. 
     Referring to  FIG. 8A , the processes up to the rear surface penetration step are the same as those in the first embodiment. In this second embodiment, after the rear surface penetration step, a solder resist  16  is coated on the side adjacent to the rear surface of the substrate  10  so as to fill the recesses  4   b . Then, the solder resist  16  is subjected to exposure and development so as to partially remove the solder resist  16 . Referring to  FIG. 8B , the plated layer  3   b  is exposed, while leaving the solder resist  16  in the recesses  4   b.    
     If the solder resist  16  is a positive type, the solder resist  16  is exposed using a photomask (not shown) that shields only regions of the solder resist  16  with the recesses  4   b  formed thereon. If the solder resist  16  is a negative type, the solder resist  16  is exposed using a photomask (not shown) that shields only regions of the solder resist  16  with the posts  5  formed thereon. As a result, the solder resist  16  remains in the recesses  4   b.    
     Then, referring to  FIG. 8C , a terminal section  17  such as the solder plate is provided on the surface of the exposed plated layer  3   b . The mold resin  14  is then diced into separate pieces. In this dicing process, as shown with reference to  FIG. 4A , the posts  5  may be diced with the blades  15  having the same size as or larger than the terminals. Alternatively, as shown with reference to  FIG. 4B , the cutting may be conducted between the posts  5  using the blades  15  having the same width as or narrower than the half etching width. Depending on the positional relation between the dicing lines and the recognition mark  8 , the recognition mark  8  may or may not remain within the semiconductor device  110 . The semiconductor device  110  is thereby produced. 
     As described, according to the second embodiment, because the solder resist  16  is filled in the recesses  4   b , the connection between the adjacent posts  5  is stronger compared to that in the first embodiment. In addition, each post  5  has a saucer-like protrusion  18  at a middle portion of the thickness direction of the port  5 . This protrusion  18  is fixed on the side adjacent to the mold resin  14  using the solder resist  16 . The protrusion  18  is a boundary for wet etching that proceeds from both front and rear surfaces. It can be said that the protrusion  18  is, for example, a section having a width sectionally wider than those of the other portions of the post  5 . 
     According to the second embodiment of the invention, it is possible to press the posts toward the mold resin  14  and to prevent the posts  5  from falling from the mold resin  14  because of the following three countermeasures against falling: (a) curved configuration of the side surface of each post  5 , (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T, and (c) suppression of falling by use of the solder resist  16  (including fixation of the protrusion  18 ). 
     In the second embodiment, the solder resist  16  corresponds to the “second resin” of the embodiments of the invention. The other corresponding relations are the same as those in the first to third embodiments. 
     3. Third Embodiment 
       FIGS. 9A through 9C  are sectional diagrams showing the method for fabricating a semiconductor device  120  according to the third embodiment of the invention. Explained herein is a case in which the recesses  4   b  on the side adjacent to the rear surface of the substrate are filled with the solder resist  16  after penetrating the rear surface (i.e., removing the joining sections  6 ) shown in  FIG. 3E  and, also, in which solder balls  19  are mounted on the plated layer  3   b . The constituting elements of  FIGS. 9A through 9C  that are identical to those of the first and second embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     Referring to  FIG. 9A , the processes up to the rear surface penetration step are the same as those in the first embodiment. In the third embodiment, after the rear surface penetration step, the solder resist  16  is coated on the rear surface of the substrate  10  so as to fill the recesses  4   b . In this embodiment, the solder resist  16  is coated more thickly than in the second embodiment. Then, the solder resist  16  is subjected to exposure and development so that the solder resist  16  is partially removed. Referring to  FIG. 9B , the plated layer  3   b  is exposed, while the solder resist  16  remains in the recesses  4   b . In this embodiment, with reference to  FIG. 9B , apertures (to expose the plated layer  3   b ) of the solder resist  16  are made smaller than in the first embodiment so that the solder resist  16  overhangs the side adjacent to each post  5 . 
     Then, referring to  FIG. 9C , the solder balls  19  are mounted on the plated layer  3   b  that is exposed from the solder resist  16 . In this case, because the exposed surface of the plated layer  3   b  becomes small (i.e., is narrowed down) by the solder resist  16 , it is possible to mound up the solder balls  19  to sectionally take the shapes of mushrooms. With these solder balls  19 , stable terminal-mounting area and height (coplanarity) are acquired, which is a property advantageous to the secondary packaging. 
     Thereafter, the mold resin  14  is diced into separate pieces. This dicing process is the same as that shown with reference to  FIG. 4A  or  FIG. 4B . That is, as shown in  FIG. 4A , the posts  5  may be diced with the blades  15  having the same size as or larger than the terminals, or, as shown to  FIG. 4B , the cutting may be conducted between the posts  5  using the blades  15  having the same width as or narrower than the half etching width. Alternatively, referring to  FIG. 4A , the posts  5  having the recognition mark  8  formed thereon may be cut off. Depending on the positional relation between the dicing lines and the recognition mark  8 , the recognition mark  8  may or may not remain within the semiconductor device  110 . The semiconductor device  110  is thereby produced. 
     As described, according to the third embodiment, because the solder resist  16  is filled in the recesses  4   b  as is in the second embodiment, the connection between the adjacent posts  5  is stronger compared to the first embodiment. In addition, referring to  FIG. 10 , at the middle portion in the thickness direction of each post  5 , there is the saucer-like protrusion  18  which is formed by wet etching from both front and rear surfaces. The protrusion  18  is fixed with the solder resist  16  on the side adjacent to the mold resin  14 . 
     Moreover, the solder resist  16  filled in the recesses  4   b  overhangs the side adjacent to each of the post  5 , and the overhung portions hold peripheries of the plated layer  3   b . Also, these portions of the solder resist  16  overhanging the posts  5  are held by the solder balls  19 . Having such a structure, it is possible to hold the posts  5  having the plated layer  3   b  formed thereon with the solder resist  16  and to hold the solder resist  16  with the solder balls  19 . 
     According to the third embodiment of the invention, it is possible to press the posts  5  toward the mold resin  14  and prevent the posts  5  from falling from the mold resin  14  because of the following four countermeasures against falling: (a) curved configuration of the side surface of each post  5 , (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T, (c) holding by use of the solder resist  16  (including both fixing the protrusion  18  and holding by the overhang structure from under), and (d) pressing using the mushroom-shaped solder balls. 
     In the third embodiment, the solder ball  19  corresponds to the “second conductive member” of the embodiments of the invention. The other corresponding relations are the same as those in the first and second embodiments. 
     4. Fourth Embodiment 
       FIG. 11  is a sectional diagram exemplarily showing the composition of a semiconductor device  130  according to the fourth embodiment. The constituting elements of  FIG. 11  that are identical to those of the drawings explained in the first to third embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     The semiconductor device  130  with reference to  FIG. 11  is a device produced by mounting, onto a motherboard  21 , the semiconductor device  100  (see  FIG. 7 ) that has been diced in the first embodiment and by filling an underfill  22  between the mold resin  14  and the motherboard  21 . Specifically, with the semiconductor device  130 , the plated layer  3   b  provided on the rear surface of each post  5  is joined to a wiring layer  23  provided on the surface of the motherboard  21 . Also, the exposed portion of the post  5  exposed from the mold resin  14 , the plated layer  3   b , and the wiring layer  23  are sealed with the underfill  22  between the mold resin  14  and the motherboard  21 . Thus, by filling the underfill  22  after the secondary packaging, it is possible to improve reliability in coupling the IC element  11  to the motherboard  21 . 
     In the fourth embodiment, the underfill  22  corresponds to the “third resin” of the embodiments of the invention. The other corresponding relations are the same as those in the first embodiment. 
     5. Fifth Embodiment 
     Explained in the previous first embodiment is a case in which the joining sections  6  are etched and removed after mounting the IC element  11  onto the substrate  10 . However, in the embodiments of the present invention, the joining sections  6  may be etched before mounting the IC element  11 . In the fifth embodiment, such a method will be described. 
       FIGS. 12A through 12C  and  13 A through  13 D are sectional diagrams showing the method for fabricating a semiconductor device  140  according to the fifth embodiment of the invention. The constituting elements of  FIGS. 12A through 13D  that are identical to those of the drawings explained in the first to fourth embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     Referring to  FIG. 12A , the substrate  10  is fabricated by the method described with reference to  FIGS. 1A through 1F  or  FIGS. 2A through 2G . The solder resist  16  is coated on the rear surface of the substrate  10  so as to fill the recesses  4   b . In this case, as in the third embodiment, for example, the solder resist  16  is coated thickly. 
     Then, the joining sections  6  joining the posts  5  together are removed by etching from the side adjacent to the front surface. In etching the joining sections  6 , the ferric chloride solution or the alkaline solution is used, for example. As a result, with reference to  FIG. 12B , the adjacent posts  5  are electrically disconnected from each other. Also, in this fifth embodiment, the solder resist  16  is filled in the recesses  4   b  when etching the joining sections. Thus, even after the joining sections are removed, the joined state of the adjacent posts  5  is maintained because of the solder resist  16 . 
     Then, with reference to  FIG. 12C , the solder resist  16  is subjected to exposure and development so as to partially remove the solder resist  16  and expose the plated layer  3   b  while keeping the solder resist  16  remained in the recesses  4   b . In this embodiment, as is in e.g. the third embodiment, the solder resist  16  is made to overhang the side adjacent to each post  5 . 
     Then, the recognition mark  8  is provided by coloring the surface (upper surface) of the post  5  in a desired position of the substrate  10  by use of the inkjet technique or the laser marking technique. To provide the recognition mark  8  by the inkjet technique, the thermo-resistive multicolor ink or the multicolor plate or the like may be applied as the coloring material. The process of providing the recognition mark  8  may be conducted prior to the process of partially removing the solder resist  16 . However, it is desirable to provide the recognition mark  8  after the process of removing the solder resist  16  or just before a die attaching process which will be described hereafter, in order to avoid the risks of damaging or eliminating the mark  8  in the process of removing the solder resist  16  and in processes conducted after having provided the mark  8 . 
     Thereafter, with reference to  FIG. 13A , each IC element  11  is mounted onto the plurality of posts  5  in the IC fixing region with the adhesive  12 . In this die attaching process, the IC fixing region is recognized using the recognition mark  8  as a marker, and the IC element  11  is aligned to the recognized IC fixing region. While keeping the IC element aligned to the IC fixing region, the IC element  11  is mounted onto the plurality of posts  5  in the IC fixing region. By this process, the IC element  11  is aligned to the IC fixing region with precision, and the IC element  11  is mounted onto the substrate  10  with minor misalignment. 
     Then, referring to  FIG. 13B , the surfaces of the posts  5  in the region outside the IC fixing region (i.e., the region not directly under the IC element) are coupled with e.g. the gold wires  13  to the pad terminals provided on the active surface of the IC element  11 . In this case, using the recognition mark  8  as a marker, the posts  5  that become the external terminals are recognized, and the recognized posts  5  may be coupled to ends of the gold wires  13 . By this method, it is possible to correctly recognize the posts  5  that become the external terminals, out of the plurality of posts  5 , and to connect the gold wires  13  to the recognized posts  5  with precision. 
     Thereafter, referring to  FIG. 3C , the entire upper part of the substrate  10  which includes the IC element  11 , gold wires  13 , and posts  5  are sealed with the mold resin  14 . The mold resin  14  is a thermo-curing epoxy resin, for example. As in the first embodiment, in this resin-sealing process, also, the front surface side of the substrate  10  including the IC element  11  is covered by the cavity, for example. Then, the pressure inside the cavity is reduced, and the mold resin  14  is supplied into the depressurized cavity. By this supply of resin under reduced pressure, the mold resin  14  is satisfactorily supplied and filled in the recesses  4   a  without the voids, with reference to  FIG. 13C . 
     Then, referring to  FIG. 13D , the solder balls  19  are mounted on the plated layer  3   b  which is exposed from the solder resist  16 . In this case, as in the third embodiment, because the exposed surface of the plated layer  3   b  becomes small (i.e., narrowed down) by the solder resist  16 , the solder balls  19  can be formed into mushroom shapes in sectional view. Thereafter, the mold resin  14  is diced into separate pieces. This dicing process is the same as shown with reference to  FIG. 4A  or  4 B, and the post  5  with the recognition mark  8  formed thereon may be cut off. Depending on the positional relation between the dicing lines and the recognition mark  8 , the recognition mark  8  may or may not remain within the semiconductor device  140 . The semiconductor device  140  is thereby produced. 
     As described, according to the fifth embodiment of the invention, the IC fixing region is recognized using the recognition mark  8  as a marker, and the IC element  11  is aligned to the recognized IC fixing region, as is in the first embodiment. It is therefore possible to align the IC element  11  to the IC fixing region with precision and to mount the IC element  11  onto the posts  5  in the IC fixing region with minor misalignment. Also, according to the fifth embodiment of the invention, it is possible to press the posts  5  toward the mold resin  14  and prevent the posts  5  from falling from the mold resin  14  because of the following four countermeasures against falling: (a) curved configuration of the side surface of each post  5 , (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T, (c) suppression of falling by use of the solder resist  16  (including fixation of the protrusion  18  and the overhung structure), and d) suppression of falling using the mushroom-shaped solder balls. 
     Moreover, according to the fifth embodiment of the invention, the joined state of the adjacent posts  5  is maintained because of the solder resist  16  even after removing the joining sections  6  made from the copper plate. Therefore, it is possible, for example, to distribute the substrate  10  in the state as shown in  FIG. 12C  and to assemble the semiconductor device  140  even in an assembling process (or facility) that does not use (have) apparatuses for etching the copper plate, coating the solder resist, and performing the exposure and development. 
     In the fifth embodiment, the joining section  6  and the solder resist  16  correspond to the “joining section” of the embodiments of the invention. The other corresponding relations are the same as those in the third embodiment. 
     6. Sixth Embodiment 
     Explained in the first embodiment with reference to  FIGS. 1A to 1F  and  2 A to  2 G is the method for fabricating the substrate  10  by half etching the copper plate  1  from the front and rear surfaces. However, the substrate fabrication method according to the invention is not limited to such a method. For example, the substrate may be fabricated by half etching only the front surface of the copper plate  1 . This process will be described in the sixth embodiment. In the sixth embodiment, two fabrication methods will be described with reference to  FIGS. 14A through 14F  and  FIGS. 15A through 15G  to exemplify the substrate fabrication method.  FIGS. 14A through 14F  show the fabrication method applying the semi additive technique, and  FIGS. 15A through 15G  show the fabrication method applying the subtractive technique. After the two fabrication methods are described, processes of mounting the IC element and resin sealing will be described with reference to  FIGS. 16A through 16D . 
       FIGS. 14A through 14F  are sectional diagrams showing the method (semi additive technique) for fabricating a substrate  20  according to the sixth embodiment if the invention. The constituting elements of  FIGS. 14A to 14F  that are identical to those of the drawings of the first to fifth embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     At first, referring to  FIG. 14A , the copper plate  1  is prepared. Thereafter, referring to  FIG. 14B , the photoresists  2   a  and  2   b  are coated on the respective front and rear surfaces of the copper plate  1 . Then, referring to  FIG. 14C , the photoresists  2   a  and  2   b  are subjected to exposure and development so as to expose the regions for forming the posts  5  and to form the resist patterns  2   a ′ and  2   b ′ over the other regions. In this case, the resist pattern  2   a ′ is formed on the front surface of the copper plate  1 , while the resist pattern  2   b ′ is formed on the rear surface of the copper plate  1 . 
     Then, referring to  FIG. 14D , the plated layers  3   a  and  3   b  are provided by e.g. electrolytic plating in the regions on the copper plate  1  that are exposed from the resist patterns  2   a ′ and  2   b ′ (i.e., the regions for forming the posts  5 ). After the plated layers  3   a  and  3   b  are provided, the resist patterns are removed the both front and rear surfaces of the copper plate  1 , with reference to  FIG. 14E . Then, referring to  FIG. 14F , the copper plate  1  is half-etched from the front surface side using the plated layer  3   a  as a mask so as to form the recesses  4   a . In this step of  FIG. 14F , the copper plate  1  is etched only from the side adjacent to the front surface, leaving the side adjacent to the rear surface unetched. Such one-surface etching is possible by the spray type wet etching. The etchant used is the ferric chloride solution or the alkaline solution, for example, and the etchant is sprayed toward the front surface of the copper plate  1  to thereby form the recesses  4   a.    
     The depth of the recesses  4   a  may be half, or more or less than half, the thickness of the thickness of the copper plate  1 . For the same reason as mentioned in the first embodiment, the substrate  20  may be rinsed after the half etching. Alternatively, after the rinsing treatment, the front and rear surfaces of the copper plate  1  (including the inner surfaces of the recesses) may be coated with an antioxidant. 
     Also, referring to  FIG. 14E , a plate-protecting photoresist (not shown) may be additionally provided on the front and rear surfaces of the copper plate  1  before etching the copper plate  1 . In the process of etching the copper plate  1 , the copper plate  1  is etched from the side adjacent to the front surface using the plated layer  3  covered by this photoresist as a mask. Accordingly, the plated layers  3   a  and  3   b  are protected from the etchant. 
     The plate-protecting photoresist may be left unremoved even after the recesses  4   a  and  4   b  are provided. It is thereby possible to continuously protect the plated layers  3   a  and  3   b  even in the subsequent assembling processes. The plate-protecting photoresist may be formed on both of the plated layers  3   a  and  3   b  and left unremoved, or formed on both layers  3   a  and  3   b  but left unremoved only on the plated layer  3   b.    
     Alternatively, such a plate-protecting photoresist may be provided not before but after etching the copper plate  1 . With such a composition, it is also possible to continuously protect the plated layers  3   a  and  3   b  even in the subsequent assembling processes. 
     The other fabrication method will now be described with reference to  FIGS. 15A through 15G . 
       FIGS. 15A through 15G  are sectional diagrams showing the method (subtractive technique) for fabricating the substrate  20  according to the sixth embodiment of the invention. The constituting elements of  FIGS. 15A to 15F  that are identical to those of the drawings in the first to fifth embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     At first, referring to  FIG. 15A , the copper plate  1  is prepared. Then, referring to  FIG. 15B , the plated layers  5   a  and  3   b ′ are provided by e.g. electrolytic plating on the respective front and rear surfaces of the copper plate  1 . Then, referring to  FIG. 15C , the front and rear surfaces of the copper plate  1  are coated with photoresists  7   a  and  7   b , respectively. Thereafter, referring to  FIG. 15D , the photoresists  7   a  and  7   b  are subjected to exposure and development so as to expose the regions for forming the posts, and the resist patterns  7   a ′ and  7   b ′ are formed on the respective front and rear surfaces of the copper plate  1  covering the other regions. Then, referring to  FIG. 15E , the plated layers  3   a ′ and  5   b ′ are etched using the resist patterns  7   a ′ and  7   b ′ as a mask and removed. As a result, with reference to  FIG. 15E , the patterned plated layers  3   a  and  3   b  are provided on the respective front and rear surfaces of the copper plate  1 . 
     Then, referring to  FIG. 15F , the copper plate  1  is half-etched from the side adjacent to the front surface using the plated layer  3   a  as a mask so as to form the recesses  4   a  on the side adjacent to front surface of the copper plate  1 . In this step of  FIG. 15F , the copper plate  1  is etched only from the side adjacent to the front surface, leaving the rear surface unetched. Such etching from only the side adjacent to the front surface is possible by e.g. the spray type wet etching. The etchant used in this case is the ferric chloride solution or the alkaline solution, for example, and the etchant is sprayed toward the front surface of the copper plate  1  to thereby form the recesses  4   a.    
     The depth of the recesses provided on the surface of the copper plate  1  may be half, or more or less than half, the thickness of the thickness of, the copper plate  1 . For the same reason as mentioned in the first embodiment, the substrate  20  may be rinsed after the half etching. Alternatively, after the rinsing treatment, the front and rear surfaces of the copper plate  1  (including the inner surfaces of the recesses) may be coated with an antioxidant. 
     Thereafter, with reference to  FIG. 15G , the resist patterns are removed from the substrate  20 . This resist removal process referring to  FIG. 15G  is shown as an example and not essential in this embodiment. In this embodiment, the resist patterns may be left unremoved on both surfaces of the substrate  20 . Alternatively, referring to  FIG. 15G , the resist pattern only on the side adjacent to the front surface of the substrate  20  may be removed, and the resist pattern on the side adjacent to the rear surface may be left unremoved. Accordingly, the resist pattern can be used as a film for protecting the plated layer  3   b  in the subsequent assembling processes. 
     In the fabrication method referring to  FIGS. 15A through 15G , the process of  FIGS. 15C through 15E  may be conducted by a physical process and not a chemical process. As in the first embodiment, the plated layers may be partially removed by sandblasting or by using a cutting instrument. 
       FIGS. 16A through 16D  are sectional diagrams showing the method for fabricating a semiconductor device  150  (from the recognition mark processing step to the resin sealing step) according to the sixth embodiment. The constituting elements of  FIGS. 16A through 16D  that are identical to those of the drawings in the first to fifth embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     Referring to  FIG. 16A , the substrate  20  produced in the method of  FIGS. 14A to 14F  or  FIGS. 15A to 15G  is first prepared, and the recognition mark  8  is provided on the surface of the substrate  20 . In this case, as in the first embodiment, the recognition mark  8  is also provided by coloring the upper surface of the post  5  in a desired position by use of e.g. the inkjet technique or the laser marking technique. Then, the IC fixing region is recognized using the recognition mark  8  as a marker and the IC element  11  is aligned to the recognized IC fixing region. Then, the IC element  11  is mounted onto the plurality of posts  5  in the IC fixing region using the adhesive  12 . 
     Then, referring to  FIG. 16B , the upper surfaces of the posts  5  in the region other than the IC fixing region (i.e., the region not directly under the IC element) are coupled to the active surface of the IC element  11  with e.g. the gold wires  13 . In this case, using the recognition mark  8  as a marker, the posts  5  that become the external terminals are recognized, and the recognized posts  5  may be coupled to ends of the gold wires  13 . By this method, it is possible to correctly recognize the posts  5  that become the external terminals, out of the plurality of posts  5 , and to connect the gold wires  13  to the recognized posts  5  with precision. 
     Referring to  FIG. 16C , the entire upper part of the substrate  20  that includes the IC element  11 , the gold wires  13 , and the posts  5  are sealed with the mold resin  14 . The mold resin  14  is a thermo-curing epoxy resin, for example. In this resin-sealing process, for example, the front surface of the substrate  20  including the IC element  11  is covered by a cavity, and pressure inside the cavity is reduced. The mold resin  14  is then supplied into the depressurized cavity. By this supply of resin under reduced pressure, the mold resin  14  is satisfactorily supplied and filled in the recesses  4   a  without the voids, with reference to  FIG. 16C . 
     Thereafter, the joining sections  6  are removed by etching from the side adjacent to the rear surface of the substrate  20  using the plated layer  3   b  as a mask. Referring to  FIG. 16D , the adjacent posts  5  are electrically disconnected from each other. To etch the substrate  20 , the ferric chloride solution or the alkaline solution is used, for example. As a result, the posts  5  connected to the gold wires  13  can be used as the electrically independent external terminals. 
     If the photoresist (not shown) that is the layer for protecting the plated layer  3   b  is left unremoved on the rear surface of the layer  3   b , this photoresist is removed after etching the joining sections. 
     If the plated layer  3   b  is an Ag plate, the Ag plate may be removed, and another plating process may be performed. That is, the Ag plate is removed, and then a different kind of plate may be reapplied as the plated layer  3   b . An example of the different kind of plate is Ni/Pd/Au, Ni/Au, or solder. Such reapplication of the plated layer  3   b  may be conducted after the removal of the photoresist if the photoresist is formed on the rear surface of the layer  3   b , or after the removal of the joining sections if the photoresist is not formed on the rear surface of the layer  3   b.    
     Thereafter, the mold resin  14  is diced into separate pieces. This dicing process is as shown with reference to  FIG. 4A  or  FIG. 4B , and the post  5  with the recognition mark  8  formed thereon may be cut off. Depending on the positional relation between the dicing lines and the recognition mark  8 , the recognition mark  8  may or may not remain within the device  150 . The semiconductor device  150  is thereby produced. 
     As described, according to the sixth embodiment of the invention, it is possible to use the plurality of posts  5  as the die pads or as the external terminals, as is in the first embodiment. Also, it is possible to use the plurality of posts  5  either as the die pads or the external terminals depending on the configuration and size of an IC fixing region established as desired. Accordingly, as is in the first embodiment, it is possible to commonly apply the specification of the substrate used for element mounting and as the external terminals and to reduce the costs of producing the semiconductor device. 
     Also, according to the sixth embodiment of the invention, the IC element  11  is recognized using the recognition mark  8  as a marker, and the IC element  11  is aligned to the recognized IC fixing region, as is in the first embodiment. Therefore, it is possible to align the IC element  11  to the IC fixing region with precision and to mount the IC element  11  onto the posts  5  in the IC fixing region with minor misalignment. 
     Moreover, according to the sixth embodiment of the invention, the posts  5  are pressed toward the mold resin  14  and prevented from falling from the mold resin  14  because of the following two countermeasures against falling: (a) curved configuration of the side surface of each post  5 , and (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T. 
     The corresponding relations in the sixth embodiment are the same as those in the first embodiment. 
     7. Seventh Embodiment 
     Explained in the previous first to sixth embodiments is a case in which the IC element  11  is mounted on the substrate  10  or  20  having the plurality of posts  5 . However, in the embodiments of the invention, the elements to be mounted on the substrate  10  or  20  are not limited to the IC element  11  but may be passive components such as resistive elements and capacitive elements. 
       FIGS. 17A through 17C  are sectional diagrams exemplarily showing the compositions of semiconductor devices  160 ,  170 , and  180  according to the seventh embodiment of the invention. The constituting elements of  FIGS. 17A through 17C  that are identical to those of the first to sixth embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     The semiconductor device  160  with reference to  FIG. 17A  is a type of device that a passive component  31  is fixed to the surfaces of the posts  5  with solders  32  and that the electrical coupling (i.e., wire connection) of the passive component  31  to the IC element  11  is conducted on the side adjacent to the motherboard (not shown). Referring to  FIG. 17A , the portions on the side adjacent to the rear surfaces of the posts  5  of the semiconductor device  160  are exposed from the mold resin  14 , and the side surfaces of the posts  5  are sectionally curved. A solder ( 32 ) layer is provided, for example, by coating a cream solder  32  on the surfaces of the posts  5  before mounting the passive component  31  and by subjecting the cream solder  32  to a reflow process at a time of mounting the passive component  31 . 
     The semiconductor device  170  with reference to  FIG. 17B  is a type of device that the passive component  31  is fixed to the posts  5  with the solders  32  and that the electrical coupling of the passive component  31  to the IC element  11  is conducted using e.g. gold wires  33 . With the semiconductor device  170 , also, the portions on the side adjacent to the rear surfaces of the posts  5  are exposed from the mold resin  14 , and that the side surfaces of the posts  5  are sectionally curved. Also, the surface of a terminal section  34  of the passive component  31  is plated with Au or Ag, and the terminal section  34  and the surfaces of the posts  5  are coupled with the gold wires  33 . Further, some gold wires  13  connected to the IC element  11  and some gold wires  33  connected to the passive component  31  are coupled to the surface of the same post  5 , and the IC element  11  and the passive component  31  are electrically coupled via the gold wires  13 , the post  5 , and the gold wires  33 . 
     The semiconductor device  180  with reference to  FIG. 17C  is a type of device that the passive component  31  is fixed to the posts  5  with an insulating resin  35  and that the passive component  31  is electrically coupled to the IC element  11  with e.g. the gold wires  33 . The only difference from the semiconductor device  170  of  FIG. 17B  is that a bonding member bonding the passive component  31  to the posts  5  is not the solder but the insulating resin  35 . The rest of the composition is the same. 
     As described, with the semiconductor devices  160 ,  170 , and  180  according to the seventh embodiment of the invention, the plurality of posts  5  may be used as the die pads for mounting the IC elements  11  and the passive components  31  or as the external terminals of the IC elements  11  and the passive components  31 . Also, depending on the configuration and size of the IC fixing region established as desired and on the configuration and size of a region for fixing the passive component  31 , it is possible to use the plurality of posts  5  either as the die pads or the external terminals. Accordingly, as is in the first embodiment, it is also possible to commonly apply the specification of the substrate  10  and to reduce the costs of producing the semiconductor device. 
     Also, with the seventh embodiment of the invention, in the die attaching process, a region on which the passive component  31  should be mounted using the recognition mark  8  as a marker (hereunder referred to as predetermined region) may be recognized using the recognition mark  8  as a marker, and the passive component  31  may be aligned to the recognized predetermined region. By this method, it is possible to align the passive component  31  in the predetermined region with precision and to mount the component  31  onto the plurality of posts  5  in the predetermined region with minor misalignment. Also, in the wire bonding process, the posts that become the external terminals are recognized using the recognition mark  8  as a marker, and ends of the gold wires  13 ,  33  are coupled to the recognized posts  5 . By such a method, it is possible to correctly recognize the posts  5 , out of the plurality of posts  5 , that become the external terminals and to connect the gold wires  13  and  33  to the recognized posts  5  with precision. 
     Moreover, according to the seventh embodiment of the invention, the posts  5  are pressed toward the mold resin  14  and prevented from falling from the mold resin  14  because of the following two countermeasures against falling: (a) curved configuration of the side surface of each post  5 , and (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T. 
     In the seventh embodiment, the post  5  on which the passive component  31  is mounted corresponds to the “third metal post” of the embodiments of the invention, and the post  5  electrically coupled to the passive component  31  corresponds to the “fourth conductive member” of the embodiments of the invention. Also, the solder  32  or the gold wire  33  corresponds to the “third conductive member” of the embodiments of the invention. The other corresponding relations are the same as those in the first embodiment. 
     8. Eighth Embodiment 
     Explained in the first to seventh embodiments was a case in which the plurality of the posts  5  and the IC element  11  are electrically coupled using the gold wires  13  (i.e., by wire bonding). However, the embodiments of the invention may employ a technique other than the wire bonding technique, such as the face-down bonding. In the eighth embodiment, this process will be specifically described. 
       FIGS. 18A through 18E  are sectional diagrams showing the method for fabricating a semiconductor device  190  according to the eighth embodiment of the invention The constituting elements of  FIGS. 18A through 18E  that are identical to those of the drawings explained in the first to seventh embodiments are allotted the same reference numbers, and explanations thereof will not be repeated. 
     At first, referring to  FIG. 18A , the substrate  10  produced by the method of  FIGS. 1A to 1F  or  2 A to  2 G is prepared, and the recognition marks  8  are provided on the surface of the substrate  10 . In this embodiment, as in the first embodiment, the recognition marks  8  are provided also by coloring the upper surfaces of the posts  5  in desired positions using the inkjet technique or the laser marking technique. Compared to the wire bonding technique, the face-down bonding technique requires higher precision in the alignment of an IC element  41  on the substrate  10 . Therefore, it is suggested, for example, that two or more recognition marks  8  be provided per each IC fixing region. 
     Then, referring to  FIG. 18B , the IC fixing region is recognized using the recognition marks  8  as a marker in a state that the active surface of the IC element  41  is facing the substrate  10 , and the IC element  41  is aligned to the recognized IC fixing region. Then, referring to  FIG. 18C , while aligned to the IC fixing region, the IC element  41  is pressed toward the substrate  10 , and a plurality of electrodes  42  provided on the active surface of the IC element  41  are bonded to the upper surfaces of the plurality of corresponding posts  5 . The electrodes  42  are stud bumps made of gold, for example, and the layout interval (pitch) between the stud bumps is designed to become an integral multiplication of the pitch between the posts  5 . Accordingly, the IC element  41  is mounted onto the substrate  10 , and the electrodes  42  of the IC element  41  and the posts  5  are electrically coupled. The electrodes  42  may be electrolytically-plated gold bumps or solder bumps. 
     Then, referring to  FIG. 16D , the entire upper part of the substrate  10  containing the IC element  41  is sealed with the mold resin  14 . The mold resin  14  is a thermo-curing epoxy resin, for example. In this resin-sealing process, for example, the side adjacent to the front surface of the substrate  10  containing the IC element  11  is covered by a cavity. Then, pressure inside the cavity is reduced, and the mold resin  14  is supplied into the depressurized cavity. As a result, the mold resin  14  is satisfactorily supplied and filled in the cavity, and the recesses  4   a  are filled with the mold resin  14  without the voids. 
     As described, the joining sections  6  joining the posts  5  together are removed by etching from the side adjacent to the rear surface of the substrate  10 . Thus, referring to  FIG. 16E , the adjacent posts  5  are electrically disconnected from each other, and the posts  5  can be used as the electrically independent external terminals. Thereafter, the mold resin  14  is diced into separate pieces. This dicing process is the same as shown with reference to  FIG. 4A  or  4 B, and the posts  5  with the recognition mark  8  formed thereon may be cut off. The semiconductor device  190  is thereby produced. 
     Therefore, according to the eighth embodiment of the invention, it is possible, as is by the wire bonding technique, to use the plurality of posts  5  as the die pads or as the external terminals depending on the configuration and size of an IC fixing region established as desired. Accordingly, it is possible to commonly apply the specification of the substrate  10  used for element mounting and as the external terminals and to reduce the costs of producing the semiconductor device, as is in the first embodiment. 
     Also, in the eighth embodiment of the invention, the IC fixing region is recognized using the recognition marks  8  as a marker, and the IC element  41  is aligned to the recognized IC fixing region, as is in the first embodiment. Therefore, it is possible to align the IC element  41  to the IC fixing region with precision and to mount the IC element  41  onto the posts  5  in the IC fixing region with minor misalignment. 
     Moreover, according to the eighth embodiment of the invention, the posts  5  are pressed toward the mold resin  14  and prevented from falling from the mold resin  14  because of the following two countermeasures against falling: (a) curved configuration of the side surface of each post  5 , and (b) anchor effect by the plated layer  3   a  and the post  5  forming the letter T. 
     In the eighth embodiment, each electrode  42  corresponds to the “first conductive member” of the embodiments of the invention. The other corresponding relations are the same as those in the first embodiment. 
     Explained in the first to eighth embodiments is a case in which the configuration in sectional view (hereunder referred to as sectional configuration) of each of the recesses  4   a  and  4   b  provided on the substrate  10  is bowl shaped. However, the recesses  4   a  and  4   b  may take other sectional configurations. For example, referring to  FIGS. 19A through 19E , each of the recesses  4   a  and  4   b  may take the form of an ellipse that lies flat. In this case, the side surface of each post  5  facing each of the recesses  4   a  and  4   b  has a constricted configuration. 
     Having such a structure, with reference to  FIG. 19D , the constricted configuration catches the mold resin  14  when resin-sealing the IC element  11  and portions on the side adjacent to the surface of the substrate  10 . Therefore, in the process of  FIG. 10D  and processes thereafter, the anchor effect is produced due to the constriction, and the posts  5  are more firmly prevented from falling from the mold resin  14 . 
     Moreover, it is possible to form the constricted configuration shown in  FIGS. 19A to 19E  by e.g. the spray type wet etching. The spraying process promotes the etching in the depth direction by setting the spraying angle of the etchant perpendicular to the surface of the copper plate, and in the lateral direction (i.e., side etching) by setting the angle diagonal to the surface of the copper plate. Furthermore, by increasing the spraying pressure of the etchant, the etching speed may increase. Therefore, it is possible to form the side surface of each post  5  into the sectionally constricted configuration by, for example, spray etching the copper plate and by varying the spraying pressure during the etching when necessary.