Abstract:
A semiconductor device having a laminated wiring layer composed of an Al or Al alloy layer and a high melting point conductive layer, wherein the laminated wiring layer has narrowed portions at which the stress tolerance of the Al or Al alloy is reduced. The controlled breakage of the Al or Al alloy layer at the narrowed portion results in a laminated wiring layer of a predetermined resistance component.

Description:
This application is a continuation of application Ser. No. 07/851,294, filed Mar. 12, 1992, and now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Industrial Field of the Invention 
     The present invention relates to a semiconductor device such as an LSI semiconductor device etc., particularly to a laminated wiring structure on the semiconductor device which is composed of an aluminium or aluminium alloy layer and a high melting point conductive layer. 
     2. Description of the Related Art 
     A single layer wiring structure using an Al, Al-Si alloy, Al-Si-Cu alloy, etc. has been employed in a wiring for a semiconductor integrated circuit device. 
     In order to realize the production of a high integration of semiconductor integrated circuit device, however, a laminated structure using an Al or Al alloy layer and a high melting point conductive layer (e.g. TiN, TiW, WNW, WSi 2 , MoSi 2  etc.) has recently been employed as a wiring layer. This is because the breakage of wire is liable to occur in the single layer wiring structure using an Al or Al alloy alone, due to stress-migration or electro-migration during heat treatment as the wiring layer employs finer wiring and thinner film. A laminated wiring structure composed of an Al or Al alloy layer and a high melting point conductive layer can prevent the failure of the whole semiconductor integrated circuit device, even if the Al or Al alloy layer is broken, since a high melting point conductive layer maintains its electrical conductivity. However, if the Al or Al alloy wirings are broken at uncertain places, irregular variations between the wiring resistance components affect the operating speed and operational timing of the internal circuits. As a result, the entire characteristics of the semiconductor integrated circuit device are deteriorated. 
     SUMMARY OF THE INVENTION 
     It is an object of the present invention to provide a semiconductor device having a wiring layer of a predetermined resistance component and capable of eliminating the variation of wiring resistance due to the breaking of an Al or Al alloy layer of a laminated layer at a predetermined position. 
     The semiconductor device according to the present invention comprises a laminated wiring structure composed of an Al or Al alloy low melting point conductive layer and a high melting point conductive layer, characterized in that the Al or Al alloy wiring layer has narrowed portions at predetermined intervals at which the stress-resistance of the Al or Al alloy is reduced. 
     A predetermined wiring resistance component is obtained and a variation in wiring resistance component can be restrained by intentionally breaking the Al or Al alloy wiring layers at the narrowed portions. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     FIG. 1(a) is a plan view showing a laminated wiring structure body which is used in a semiconductor integrated circuit device according to a preferred embodiment of the present invention; 
     FIG. 1(b) is a cross-sectional view of the laminated wiring structure in FIG. 1(a); 
     FIG. 2 is a cross-sectional view of the laminated wiring structure in FIG. 1(a) showing breaking of the wiring. 
     FIG. 3 is also a cross-sectional view of the laminated wiring structure in FIG. 1(a), except that the low melting temperature conductive layer comprising Al is located directly on the semiconductor substrate and the high melting point conductive layer is located on top of the low melting point conductive layer. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     A preferred embodiment of the present invention will be described with reference to FIGS. 1(a), 1(b) and 2, wherein FIG. 1(a) is a plan view and FIG. 1(b) is a cross-sectional view. A wiring 11 formed on a semiconductor substrate 10 comprises an upper layer of a low melting point conductive layer, e.g. an Al layer 12, and a lower layer of a high melting point conductive layer, e.g. a TiN layer 13. For example, the Al layer is 4000 Å thick, and the TiN layer is 1000 Å thick. Their widths are, e.g., about 1 μm. The wiring has narrowed portions 14 at intervals ranging from 50 to 500 μm. The width of the narrowed portions is at the most about one half of that of the other portions. The length of the narrowed portions 14 should be as short as possible, e.g. about 0.5 μm under current lithographic techniques. It is desirable to be as short as possible with the improvement of the lithographic technique. 
     The narrowed portions are of the Al layer are finally broken or electrically disconnected before the final wafer process is finished. The Al layer is sintered in hydrogen at a temperature of 350° to 400° C. after being subjected to patterning, and the wiring is broken at almost all the narrowed portions due to this heat treatment. The narrowed portions which were not broken in the foregoing processes are completely broken in the heat treatment (400° C. for about 30 min.) during the formation of a passivation film. 
     When the wiring 11 set forth above is used as the lowest layer wiring of a multi-layer wiring (e.g. 2-layer wiring), an insulating film is formed between the layers at the next step. When the wiring 11 is used as a single layer wiring or an uppermost layer wiring of the multi-layer wiring, a passivation film (last protective insulating film) is formed at the next step. When the wiring 11 is subjected to a heat treatment, e.g., at the time of forming the insulating film, the Al wiring layer is broken at its weak points since the coefficient of linear expansion of Al is 10 times greater than that of the base material such as Si, SiO 2 , etc. This is because Al increases its volume largely to thereby generate a plastic deformation at high temperature during heat treatment and reduces its volume largely in cooling to thereby generate a heat stress in the Al wiring layer. 
     As described in the preferred embodiment, the Al wiring 12 is broken at the narrowed portions 14 which are formed at predetermined intervals as shown in FIG. 2. This is because the strength of the wiring is reduced at the narrowed portions 14. Consequently, the breakage of Al wiring 12 can be localized at weak narrowed portions 14 so as to control the breaking points of the Al wiring 12. Furthermore, inasmuch as the breaking of the wiring at the narrowed portions 14 releases the stress of the wiring, the unintentional breakage of the Al wiring 12 caused by stress- or electro-migration can be restrained so as to always attain a uniform wiring resistance component. 
     FIG. 3 is similar to FIG. 1(b), except that the location of the low melting point conductive layer and the high temperature melting point layer is reversed as indicated therein. 
     Supposing that the specific resistance factors of Al 12 and TiN 13 are 3 μΩ.cm and 100 μΩ.cm respectively and the broken gap of the Al wiring is 1 μm in the case of the laminated wiring of Al/TiN, according to the preferred embodiment, the resistance component increasing rate per each breaking of Al wiring 12 is about 1.5% per each wire of 1 cm length. It is about 1% if the Al wiring 12 is 3000Å thick and about 2% if the Al wiring 12 is 6000Å thick. The increase of the resistance component caused by the wiring breakage can be estimated so that it is possible to design a circuit by incorporating variations in circuit parameters. 
     Although TiN was employed as the lower layer of the high melting point conductive layer in the preferred embodiment, other high melting point materials such as TiW, WN, W, WSi 2 , MoSi 2 , etc. can be employed too. The upper Al layer can be substituted by an Al-Si alloy, an Al-Si-Cu alloy, an Al-Si-Cu-Hf-B alloy, Al-Ti, Al-Pd, Al-Pd-Nb, Al-Sc, Al-Cr-Cu, Al-Cr, Al-Ti-Cu or the like, instead of pure Al. The present invention can be applied to other laminated wiring structures such as those having a high melting point conductive layer on the upper surface of an Al layer, those having high melting point conductive layers on the upper and lower surfaces of the Al layer and those having high melting point conductive layers interlaced with a plurality of Al layers.