Abstract:
A method and apparatus used to calibrate high-resolution electron microscopes where a single standard provides multiple samples, each having a different atomic structure, permits rapid accurate calibration of the entire range of magnifications. The different atomic structure dimensions possess known reference measurement data. The S/TEM is adjusted to focus onto the crystal lattice structure of each sample in a selected sequence. Measurements of these lattice spacings are compared to known dimensions. If S/TEM measurements do not agree with the lattice spacing dimensions, the S/TEM magnification is adjusted to reflect known dimensions. Typical standard exchange and associated processing steps are eliminated by the use of the single standard comprising of a plurality of samples.

Description:
FIELD OF THE INVENTION  
         [0001]    This invention relates to a method and apparatus used to calibrate a measuring instrument. More particularly this invention relates calibration of Scanning Transmission Electron Microscopes (STEM) and Transmission Electron Microscopes (TEM).  
         BACKGROUND OF THE INVENTION  
         [0002]    Semiconductor manufacturing consists of a number of crucial processing steps performed on wafer lots where measurements of minimum feature sizes known as critical dimensions (CD) are made to ensure proper device fabrication. The high-degree of precision during this processing requires the utilization of Scanning Transmission Electron Microscopes and Transmission Electron Microscopes (S/TEM). These critical tools provide measurement capabilities in the low nanometer range. Accuracy of their measurements is essential since effective process controls depend on CDs they supply. S/TEMs require frequent calibration to ensure their accuracy since processing errors cause appreciable inconsistencies in CDs. Calibration procedures are very time consuming and have a negative impact on semiconductor fabrication workflow. Typical S/TEM magnification calibration approaches are also limited in accuracy.  
           [0003]    A conventional calibration approach utilizes a standard (e.g., TEM grid) that possesses one crystal lattice specimen to calibrate a S/TEM for a particular magnification. This approach requires that calibration for each magnification of a range of magnifications required to support semiconductor fabrication use a different standard. Thus, numerous specimen exchanges along with new orientations to achieve calibration over a range of magnifications are required. In addition, the beam conditions must be reset for each standard. Measurements obtained from the specimen&#39;s crystal lattice spacing are compared to known data to determine if the S/TEM requires adjustment or if the magnification results being calibrated are within tolerance. Calibration adjustments are made accordingly. This iterative process is conducted until calibration is achieved for the full range of magnification required in support of semiconductor fabrication.  
           [0004]    Another method using a scale with multiple crystal lattice specimens to calibrate a S/TEM is described in U.S. Pat. No. 6,231,668 to Loesch entitled “Method for Manufacturing a Calibrated Scale in the Nanometer Range for Technical Devices Used for the High Resolution or Ultrahigh-Resolution Imaging of Structures and Such Scale”. This patent discloses utilization and manufacturing of a layered scale. Depositions of at least two different crystalline or amorphous materials are used to create the scale. These materials are deposited on a substrate in alternate layers, one on top of the other. Even though a plurality of crystal lattice materials are used, this scale results in a single multi-layered specimen also known as sample on a substrate so the range of calibration of magnification is still limited very limited.  
           [0005]    A few other approaches allow calibration over a range of magnifications. However, these standards are limited and do not cover the entire range of S/TEM magnifications typically required to support current semiconductor fabrication requirements. Nor do these solutions provide the accuracy that can be achieved with known crystal lattice plane spacing. It would be very advantageous to utilize a standard that is comprised of a plurality of specimens each having or arranged to present a different lattice spacing or atomic spacing on a single TEM grid. Utilization of this standard would allow rapid accurate calibration of the S/TEM at all desired magnifications and conditions to overcome limitations of prior art. Then, fast thorough calibration can be performed streamlining workflow of a semiconductor processing line.  
         SUMMARY OF THE INVENTION  
         [0006]    An object of the present invention is to streamline semiconductor fabrication workflow, solve the need for greater accuracy, and induce process reliability/repeatability by enabling rapid, accurate calibration of high-resolution electron microscopes.  
           [0007]    Another object of the present invention is to provide a method and apparatus for rapid high-resolution electron microscopes calibration over the range of magnifications required utilizing a single standard that provides multiple specimens, each possessing different lattice spacing.  
           [0008]    In accordance with the present invention, the disclosed method and apparatus enables a calibration process of an electron microscope to be performed where only one standard is required for calibration of the entire range of magnifications. The enabling apparatus consists of different atomic structures such as crystal lattice spacing samples also known as specimens that are resident on the single standard. These samples are arranged in a grid pattern. Lattice spacing dimensions of the samples are known reference data. The S/TEM is adjusted to establish viewing of a single sample from a plurality of samples by bring fringes of the lattice space into focus. Measurements of these lattice spacings are compared to known reference measurement data. If S/TEM measurements do not agree with the lattice spacing dimensions then, the S/TEM magnification is adjusted (i.e., the input current to the lens is adjusted) to reflect known reference data. Sequentially viewing one sample at a time and performing S/TEM adjustments for the particular sample accomplishes calibration. All samples required to support magnification calibration of a range of magnification are used. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0009]    The features of the invention believed to be novel are specifically set forth in the appended claims. However, the invention itself, both as to its structure and method of operation, may best be understood by referring to the following description and accompanying drawings.  
         [0010]    [0010]FIG. 1 is a diagram representing a prior art S/TEM system.  
         [0011]    [0011]FIG. 2 is a flow diagram of a typical prior art calibration process.  
         [0012]    [0012]FIG. 3 is a block diagram of a calibration standard with multiple samples.  
         [0013]    [0013]FIG. 4 provides S/TEM imagery of a plurality of crystal lattice samples on one standard.  
         [0014]    [0014]FIG. 5 is a flow diagram of the preferred embodiment optimized calibration process.  
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0015]    During fabrication, semiconductor products are analyzed using high-resolution electron microscopy such as Scanning Transmission Electron Microscopes (STEM) and Transmission Electron Microscopes (TEM), sometimes referred to collectively as S/TEM system. A block diagram representing a S/TEM system  100  is provided in FIG. 1 where the energy source represents an electron gun  101  that produces a stream of monochromatic electrons. This stream is focused onto a small, thin, coherent beam by the use of condenser lenses  102 ,  103 . The first lens  102  largely determines the “spot size”; the general size range of the final spot that strikes a sample  105 . A “spot size knob” usually controls this condenser lens. The second condenser lens  103  changes the spot size on a sample also known as a specimen  105 , adjusting the beam from a dispersed spot to a pinpoint beam. An “intensity or brightness knob” controls this lens. The user selected condenser aperture  104  constricts the resulting beam. This condenser aperture  104  blocks high angle electrons, those far from the optic axis (i.e., the dotted line  112  down the center). The beam strikes a sample  105  and parts of it are transmitted through the sample. The transmitted portion is focused by the objective lens  106  into an image. The optional objective lens  107  and selected area  108  apertures can restrict the beam. The objective aperture  107  enhances contrast by blocking out high-angle diffracted electrons. The selected area aperture  108  enables a user to examine the periodic diffraction of electrons by ordered arrangements of atoms in the sample. The resulting image is enlarged as it passes through the intermediate lenses  109 ,  110  and projector  111  lens. This image strikes the phosphor image screen and light is generated, resulting in an image for the user to see. The darker areas of an image represent areas of the sample that fewer electrons were transmitted through (they are thicker or denser). The lighter areas of the image represent those areas of the sample that more electrons were transmitted through (they are thinner or less dense).  
         [0016]    Semiconductor fabrication routinely requires S/TEM magnification ranging from 10,000 to 5 million times a sample size. Accuracy of S/TEM results at these magnification levels is critical to fabrication processing. Therefore, routine periodic S/TEM calibration must be performed. S/TEMs can be calibrated by measuring known lattice spacing of various materials. S/TEM calibration is typically an iterative process as indicated in the simplified prior art process flow diagram of FIG. 2. The process begins by starting the S/TEM system  100  along with setting operational parameters and S/TEM conditions  200  for a particular magnification. Beam alignment/optimization  201  is established for this desired magnification. The sample to be used for a particular magnification calibration is exchanged  202  (i.e., located and prepared for use in the S/TEM). The sample is orientated perpendicular to the beam and the beam optimized under the desired condition, in order to image the sample lattice or atomic structure. Liquid nitrogen is injected  203  to preclude contamination. Adjustments are made to focus the beam, block  204 , onto the sample. Then, the S/TEM is calibrated appropriately, block  205 , where measurements are obtained and compared with known values from reference data. S/TEM adjustments are made for any differences that are out of tolerance. Upon requiring calibration for another magnification  206 , the process is repeated,  208 . Standard samples are exchanged to calibrate a S/TEM at each of a range of magnifications required. Each time a sample is exchanged, S/TEM operational conditions and orientation must be reset, which is iterative and very time consuming. Once calibration is achieved for the complete magnification range required, the calibration procedure is considered complete, block  207 . This process has a significant negative impact on fabrication cycle time (i.e., the S/TEM is not available for fabrication support while being calibrated).  
         [0017]    The invention disclosed streamlines the calibration procedure by alleviating the process iteration indicated in FIG. 2. A preferred embodiment utilizes a single standard for calibration over the range of magnifications required. A plurality of samples or specimens having different atomic structures is provided on the single standard as indicated in the block diagram representation of FIG. 3. Since the objective of having different samples is to have different lattice dimensions for calibration, it is recognized that some samples may be of the same material but oriented to present a different lattice or atomic structure to the electron beam. Multiple samples with different lattice spacing are provided on this single standard to calibrate the S/TEM. The block diagram is a representation of multiple, varying calibration specimens or samples  301  on a single substrate  300 . In the preferred embodiment, each unique sample  301 , has a known crystal lattice structure. with crystal lattice spacings that are very accurately known for each sample used. Each sample supports a specific S/TEM calibration magnification so that the entire range of magnifications required is accommodated with the one standard. Each sample is positioned independently in a respective defined region of the standard such that each sample can be selected for imaging.  
         [0018]    A preferred embodiment of the calibration standard is comprised of a standard possessing multiple calibration samples having different crystal lattice planes where the interference fringes of each of the samples range from approximately 0.3 nanometers to 9.0 nanometers. The standard utilizes a carbon sheet sample support with a copper grid structure supporting the carbon sheet. Each grid section may be 10 by 10 nanometers and each sample may be 5×5 nanometers. Focused ion beam lift-out may be used to create a sample that is to be placed on the grid. Focused Ion Beam (FIB) lift-out allows multiple thinned samples to be obtained rapidly and to be placed on the grid. The carbon sheet support structure thickness is less than about 500 nanometers with a preference of less than about 100 nanometers. The thickness of each sample may be about 0.5 micrometers.  
         [0019]    [0019]FIG. 4 provides actual S/TEM imagery of two adjacent crystal lattice samples. These images are of S/TEM lattice fringes possessing high-resolution cross-fringes. In order to image lattice spacings in S/TEM, a very thin section of crystalline material is placed in the tool. The electron beam scans over the crystalline sample, and the electrons create interference fringes as they pass through the evenly spaced atomic planes. The pitch of the interference fringes will vary depending on the distance between the crystalline lattice planes. The pitch of the interference fringes is uniform and constant over time and differing beam conditions. The fringes are imaged, and their pitch is measured. Measurements on the sample of interest are compared with values from the known reference data, and the differences monitored. Any significant deviation is corrected during calibration.  
         [0020]    This invention establishes S/TEM calibration that can be performed accurately and quickly over the range of magnifications of the S/TEM, without the necessity of iterative standard exchanges and multiple sample/beam alignments. FIG. 5 depicts an optimized calibration process flow diagram leveraging the use of the single standard  300  of FIG. 3. By placing samples with a range of lattice or atomic spacings on the same sample (i.e., grid), sample exchange  202  along with nitrogen purge  203  are only performed once. By focusing, block  500 , from sample to sample on the grid  300 , various pitches can be observed at the appropriate magnifications. This ensures beam conditions remain the same from sample to sample and eliminates sample and beam alignment between samples. Viewing a sample can be accomplished by moving the ion beam or by moving the sample. Since the actual lattice spacing is known for each sample, the operator can move rapidly between samples to make the necessary calibration adjustments  501  and the calibration is then complete  207 . The ease and speed of this calibration method affects not only the throughput of the S/TEM, but the frequency with which tests can be reasonably conducted. This process also speeds up turnaround time of samples for critical dimension measurements on features too small to be measured accurately in the clean room and for checks on in-line tools.  
         [0021]    While only certain preferred features of the invention have been shown by way of illustration, many modifications and changes will occur to those skilled in the art. It is, therefore, to be understood that the present claims are intended to cover all such modifications and changes, which fall within the true spirit of the invention.