Abstract:
An interior finishing panel for a vehicle, comprising a first wall) and a second wall opposed to each other at an interval. The panel is formed in a hollow double wall structure having an inner rib formed between the first wall and the second wall. A skin sheet with an averaged thickness of 2.0 mm or thinner is integrally laminated on the first wall. The skin sheet is formed in a double layer structure in which a nonwoven cloth with a weight of 250 g/m&lt;2&gt; or less is stuck on a resin sheet, and its tensile elastic modulus at room temperature is 3500 kg/cm&lt;2&gt; or less. A parting line and a step part are formed on a peripheral wall within the range of 35% of the averaged thickness of the panel from the first wall side over roughly all the periphery thereof, and the end of the skin sheet is melt-bonded to the peripheral wall along the step part. A three-dimensional pattern is produced on the surface of the resin sheet forming the skin sheet.

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to a blow-molded panel with a skin or covering that is used as a vehicle interior panel, a method of producing the panel with skin, and a laminating blow molding method. 
       DESCRIPTION OF THE RELATED ART 
       [0002]    In a lid panel of the luggage compartment in an automobile such as the floor panel and the luggage board and similar structures, the panel with a cover material such as the non-woven fabric is laminated to the panel surface is used in order to improve touch sense of the panel surface and to impart a design effect (see Japanese Patent Laid-Open No. H1-347720 and Japanese Patent Laid-Open No. 2000-289095). However, recently utilization of the luggage compartment and the like of the automobile is diversified, accordingly demands for the panel formed by the integrally welding a resin sheet in which a three-dimensional pattern such as a grain pattern is formed and the like are grown besides the conventional panel in which the non-woven fabric is laminated. 
         [0003]    For example, Japanese Patent Laid-Open No. H9-39078 discloses a panel in which a decorative fabric having a three-layer structure of the cover material, a foam, and a fabric sheet, integrally laminated to a surface wall of a upholstered hollow molding component (panel) while blow molding and the fabric sheet is the non-woven fabric whose weight per area ranges from 50 to 250 g/m . Japanese Patent Laid-Open No. H9-39079 discloses one in which the cover material, which is formed by the bonding of a resin sheet and a fabric sheet, is integrally laminated to the surface wall of the upholstered hollow molding component (panel) while blow molding and the resin sheet is made of polypropylene or PET whose tensile modulus ranges from 3000 to 12000 kg/cm Japanese Patent Laid-Open No. S62-25117 discloses a molding method, in which a coating layer (cover material) is heated and integrally laminated while blow molding, the cover material is formed by bonding a non-woven fabric to a soft PVC, and a not-flat pattern of a mold is transferred. Japanese Patent Laid-Open No. H10-235720 discloses a panel with skin, to which a fabric having fuzzy hairs (non-woven fabric) is integrally laminated, used for a vehicle cargo floor panel and the like, and the panel with skin has an double-walled rib. Japanese Patent Laid-Open No. 2001-277342 and Japanese Patent Laid-Open No. 2004-74660 disclose that a part of a parison is compressed and thinned to form a hinge portion having a groove while blow molding and the non-woven fabric is placed between the cover material and the parison from the viewpoint of improving cover material bonding strength. 
         [0004]    In a panel with skin produced by the blow molding is formed by integrally laminating a cover material to a melted parison while molding. In the case where a resin sheet having no air permeability is used as the cover material, air remains between the resin sheet and parison arranged in the mold causing a problem. In order to prevent the above problem, usually a resin sheet in which the foam or the non-woven fabric is placed is used. 
         [0005]    In a vehicle interior panel and other such panels, it may be desired that textured or not-flat three-dimensional pattern such as the fine grain pattern or a regular embossing pattern emerges on the outer surface of the cover material. However, when the blow molding is performed with a resin sheet having a not-flat three-dimensional pattern, the not-flat three-dimensional pattern becomes flat or loses its texture by the pressure applied as part of the blow molding and heat from the parison, which results in deformation of the resin sheet. Further, particularly in an end portion of the resin sheet, the not-flat three-dimensional pattern is largely elongated by stretch of the resin sheet, and appearance is remarkably detracted. 
         [0006]    A not-flat or textured three-dimensional pattern along the cavity of the mold can be transferred as a method of causing the not-flat three-dimensional pattern to appear on the outer surface of the cover material. However, the resin sheet, in which the foam or the non-woven fabric is placed, is usually thick, three-dimensional pattern along the cavity of the mold cannot be transferred sufficiently. Particularly, in the case where the resin sheet is not previously softened by heating from the viewpoint of moldability, there is problem that the three-dimensional pattern has a poor appearance as the texture is inadequately transferred or imprinted on the cover material. 
         [0007]    In some such vehicle interior panels, a rib that protrudes from a backside wall and is integrally welded to the backside of the surface wall, is formed in order to enhance rigidity of a hollow double-walled structure, or a thin hinge portion, in which the surface wall and the backside wall are integrally welded, is formed in order to partially open and close divided floor boxes when the vehicle interior panel is used as a lid of the floor box. In this case, because the rib or the hinge portion is formed by integrally welding the surface wall and the backside wall, sink marks and unevenness of the transfer ability are generated in the three-dimensional pattern appearing on the surface of the resin sheet by a difference of molding condition between the welded portion and a portion corresponding to a hollow space where the surface wall and the backside wall are not welded. As a result, because the transfer is partially insufficient, there is the problem that the appearance is detracted by becoming dim or flatting of the three-dimensional pattern. 
         [0008]    In the panel with skin produced by the blow molding, there is a problem that peeling of the cover material is easy to occur at the end of the sheet and the hinge portion. Therefore, in order to prevent the peeling and uplift of the cover material, it is necessary to take such countermeasures such as molding the cover material integrally by winding the end of the cover material in the backside of the panel with a slide mold, and forming a wide recess from the cover material side in the hinge portion to broaden a bonding area. 
       SUMMARY OF THE INVENTION 
       [0009]    Therefore, according to one embodiment of the invention, in a vehicle interior panel having a hollow double-walled structure including a peripheral wall that forms a hollow space between a first wall and a second wall, a cover material laminated to the first wall is formed by at least a double-layer structure in which a non-woven fabric whose weight per area ranges from 80 to 250 g/m 2  is bonded to the resin sheet, an average thickness of the cover material is no more than 2.0 mm, tensile modulus of the cover material being no more than 3500 kg/cm 2  at room temperature, and an end of the cover material is fixed along a parting line formed over a substantially entire circumference of the peripheral wall. Accordingly, even when laminating the resin sheet that has a three-dimensional pattern with projections, recesses, or projections and recesses on a surface thereof integrally by blow molding, the three-dimensional pattern does not become flat nor is deformed by the pressure of the blow molding process and heat from the parison, and as a result, the deformation caused by largely elongating the three-dimensional pattern is not generated at the end of the resin sheet. Further, according to one embodiment of the invention, when a three-dimensional pattern including a fine grain pattern or a regular embossing shape is transferred from a cavity of a mold to a surface of a resin sheet while blow molding, the transfer ability is sufficiently high, and a three-dimensional pattern having good appearance can be disposed or imprinted on the surface of the cover material. 
         [0010]    In a vehicle interior panel having the hollow double-walled structure configured in accordance with one embodiment of the present invention, the parting line is formed at a position located within a 35% range of the average thickness of the panel from the surface of the first wall, a step portion is formed over the substantially entire circumference at a portion of the first wall side of the parting line of the peripheral wall, and the end of the cover material laminated to the surface of the first wall while blow molding is laminated along the step portion. Therefore, a three-dimensional pattern having a good or attractive appearance can be emerged, produced or imprinted , the excessive elongation of the end of the cover material laminated to the surface of the first wall of the panel is suppressed, and the cover material is strongly fixed to the surface of the first wall without generating wrinkles and breakage, which allows the detraction of appearance and the peeling of the end to be diminished or prevented. 
         [0011]    In one embodiment, where a thin hinge portion is integrally formed, the first wall can be substantially formed in flat by forming the parting line with a substantially linear portion and a portion close to the first wall side in the vicinity of the hinge portion (parting surfaces of the mold halves forming the parting line are formed at the positions close to the cavity surface on the cover material arrangement side by winding the parting line of the mold at the position corresponding to the hinge portion). Therefore, the sheet peeling caused by motion of the hinge portion is prevented, and the unevenness of the transfer ability is not generated even if the three-dimensional pattern is transferred to the surface of the cover material. 
         [0012]    Further, double-walled ribs having plate-like structures are formed as a reinforcement rib in which a part of the second wall being protruded toward the first wall to be integrally welded to the backside of the first wall. Therefore, detraction of the appearance caused by the sink marks or the like is not generated, and the unevenness is not generated in the surface of the cover material, and the three-dimensional pattern with a good appearance can be emerged. 
         [0013]    According to one embodiment of the invention, the vehicle interior panel having a hollow double-walled structure in which the three-dimensional pattern is emerged, deposited, transferred or imprinted, on the surface of the cover material can be obtained by using the thin, soft sheet having at least the double-layer structure in which the non-woven fabric whose weight per area ranges from 80 to 250 g/m 2  is placed as the cover material between the resin sheet and the first wall. 
         [0014]    A step portion in one embodiment of the present invention, an double-walled rib, and a parting line are provided, and a three-dimensional pattern including the projections, the recesses, or the projections and recesses emerge is formed on the surface of the resin sheet by the three-dimensional shape transfer surface provided in the cavity of the mold. The step portion is formed over the substantially entire circumference at a portion on the first wall side of the parting line formed on the peripheral wall, the double-walled rib is formed between the first wall and the second wall, a part of the second wall is protruded toward the first wall to be integrally welded to the backside of the first wall and the protruded portions is integrally welded to each other, and the parting line is formed by the substantially linear portion and the portion close to the first wall side in the vicinity of the hinge portion the peripheral wall of the hollow double-walled structure. Therefore, there are effects that the excessive elongation of the end of the cover material is suppressed, the cover material is strongly fixed without generating the wrinkle and breakage, the three-dimensional pattern having the fine grain pattern or the regular embossing shape cab preferably is emerged, the unevenness of the transfer ability caused by the sink marks of the like is not generated, and the detraction of the appearance can be prevented. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS  
         [0015]      FIG. 1  is a perspective view of a vehicle interior panel according to one embodiment of the invention; 
           [0016]      FIG. 2  is a sectional view taken on line A-A of  FIG. 1 ; 
           [0017]      FIG. 3  is a partially perspective view of the vehicle interior panel of  FIG. 1  when viewed from backside; 
           [0018]      FIG. 4  is a partially enlarged sectional view showing the vehicle interior panel; 
           [0019]      FIG. 5  is a perspective view of a vehicle interior panel according to another embodiment of the invention; 
           [0020]      FIG. 6  is a partially detail perspective view of  FIG. 5 ; 
           [0021]      FIG. 7  is a sectional view taken on line B-B of  FIG. 6 ; 
           [0022]      FIG. 8  is a perspective view showing a mode in which an automobile is equipped with a floor panel which is of an example of the vehicle interior panel according to the invention; 
           [0023]      FIG. 9  is a sectional view showing a blow molding mode of the vehicle interior panel; 
           [0024]      FIG. 10  is a partially enlarged sectional view of  FIG. 9 ; 
           [0025]      FIG. 11  is a partially enlarged sectional view showing a mode in which blow molding is finished after clamping; and 
           [0026]      FIG. 12  is a sectional view showing a blow molding mode of a vehicle interior panel according to another embodiment of the invention. 
       
    
    
     DETAILED DESCRIPTION  
       [0027]    The panel of one embodiment of the present invention is provided with a skin and is a vehicle interior panel used for a lid panel, a shelf board, and the like of a luggage compartment in an automobile such as a floor panel, a luggage board, and a shelf panel. The panel is also the panel having a hollow double-walled structure in which a cover material is integrally laminated by the blow molding. The cover material is one in which a non-woven fabric is laminated to a resin sheet. The resin sheet is made of a thermoplastic resin, and a three-dimensional pattern is formed on the resin sheet. 
         [0028]    The invention is described in detail with reference to the accompanying drawings. 
         [0029]      FIG. 1  is a perspective view of a vehicle interior panel according to the invention,  FIG. 2  is a sectional view taken on line A-A of  FIG. 1 ,  FIG. 3  is a partially perspective view of the vehicle interior panel of  FIG. 1  when viewed from backside, and  FIG. 4  is a partially enlarged sectional view showing the vehicle interior panel. 
         [0030]    In  FIGS. 1 to 4 , the reference numeral  1  designates a vehicle interior panel. The vehicle interior panel  1  has a hollow double-walled structure made of a thermoplastic resin by blow molding, and the vehicle interior panel  1  has a first wall  2  and a second wall  3  which face each other with some intervals. The vehicle interior panel  1  has a peripheral wall  5  between the first wall  2  and the second wall  3 , and the peripheral wall  5  forms a hollow space  4 . Double-walled ribs  6  having plate-like structures are formed between the first wall  2  and the second wall  3 . The double-walled rib  6  is formed as follows, a part of the second wall  3  is protruded toward the first wall  2  to be integrally welded to the backside of the first wall  2 , a wall surface of the protruded portion is folded into two wall surfaces, and the two wall surfaces are integrally welded. 
         [0031]    A cover material  7  whose average thickness ranges from 0.5 to 3.0 mm is integrally laminated to the first wall  2 . In one embodiment the cover material  7  has a double-layer structure in which non-woven fabric whose weight per area is no more than 250 g/m 2  is bonded to the resin sheet. A three-dimensional pattern  8  emerges on the surface of the resin sheet. The thickness of the resin sheet itself ranges from about 0.2 to 0.6 mm. 
         [0032]    The resin sheet forming the cover material  7  is, in one embodiment, made of a thermoplastic resin including thermoplastic elastomer (TPE) such as polyvinyl chloride (PVC), thermoplastic polyurethane elastomer (TPU), and thermoplastic polyolefin elastomer (TPO) and a polyolefin resin such as a polyethylene resin and a polypropylene resin. The resin sheet in which a fabric sheet such as a non-woven fabric is laminated to the backside is used for the purpose of adhesive properties and prevention of an air pool. Olefin elastomer (TPO), urethane elastomer (TPU), styrene elastomer (SBC), polyvinyl chloride (TPVC), polyester elastomer (TPEE), polyamide elastomer (TPAE) and the like can appropriately be selected as thermoplastic elastomer. Among them, from the viewpoint of transfer ability for forming the three-dimensional pattern, thermoplastic polyurethane elastomer (TPU) or thermoplastic polyolefin elastomer (TPO) are preferable for the resin sheet. 
         [0033]    In one embodiment, a through hole or perforation is not made in the resin sheet. The resin sheet is made of the thermoplastic resin. For the thermoplastic resin, tensile modulus is no more than 3500 kg/cm 2  at room temperature and more preferably tensile modulus is 2000 kg/cm 2 , tensile modulus is lower than 500 kg/cm 2  at 100° C. and more preferably tensile modulus is lower than 300 kg/cm 2 , and a tensile strength at yield point is no more than 50 kg/cm 2  at 100° C. In this case, tensile modulus and the tensile strength at yield point (tensile yield strength) are measured pursuant to JIS-K-7113. No. 2 specimens are used as a specimen, and the measurement is performed at a test speed of 50 mm/min. However, an environmental temperature is set at room temperature (23° C.) or 100° C., and the measurement is performed after the temperature of the specimen is stabilized. 
         [0034]    To provide the three-dimensional pattern  8 , in one embodiment, a pattern of the cavity surface is transferred to the surface of the resin sheet by pressing the cover material  7  against the mold while blow molding. Further, the cover material  7  in which a design or pattern improving appearance or touch sense, or a grain pattern is previously formed on the surface of the resin sheet can be used. 
         [0035]    The three-dimensional pattern  8  emerging on the surface of the resin sheet is formed in plural not-flat shapes having height at least 200 μm, preferably ranging from 500 to 2500 μm. Examples of the three-dimensional pattern  8 , in one embodiment, include the grain pattern such as satin-like finish, tanned skin-like or leather finish, a geometrical pattern, a wood-grain pattern, and a marble-grain pattern and an embossing pattern protruded in a hemispherical shape, a tubular shape, a conical shape, a cylindrical shape, a square-pole shape, and a trapezoidal shape. 
         [0036]    As shown in  FIG. 4 , the vehicle interior panel  1  is formed with an average thickness (a) of the vehicle interior panel  1  ranges from 20.0 to 40.0 mm. On the peripheral wall  5  connecting the first wall  2  and the second wall  3 , a parting line  9  is formed at a position located within a 35% range (b) of the average thickness of the panel from the surface of the first wall  2 , or the parting line  9  is formed within the range in which the thickness is no more than 8.0 mm from the surface of the first wall  2 . The parting line  9  is formed over the entire circumference of the peripheral wall  5 . When the parting line  9  is formed at the position far away from the surface of the first wall  2  to which the cover material  7  is laminated integrally, an edge of the cover material is prolonged. Therefore, it is necessary that the parting-line forming position is close to the surface of the first wall  2  to an extent so that the edge of the cover material is not prolonged. A step portion  10  having a width c is substantially formed over the circumference on the side of the first wall  2  of the parting line  9 , and the edge of the cover material  7  is laminated along the step portion  10 . The width c of the step portion  10  is at least 1.0 mm, and preferably the width c is at least 1.5 mm. Although the width c of the step portion  10  is set at least 1.0 mm, the width c can appropriately be adjusted according to the thickness of the cover material  7 . When the width c of the step portion  10  is lower than 1.0 mm, welding strength is not sufficient at the edge of the cover material  7 , peeling is easy to occur at the edge of the cover material  7 , and workability of flash removal is worsened. 
         [0037]    A boundary portion between the first wall  2  and the step portion  10  is formed on a loose curved surface, and elongation is hardly generated in the edge portion of the cover material  7  while the edge portion of the cover material  7  is welded to the step portion  10 . Therefore, even if the grain pattern is formed in the surface of the cover material  7 , not only the appearance of the cover material  7  is not detracted, but also the peeling is hardly generated in the welded portion because the elongation is hardly generated in the edge portion of the cover material  7  while the edge portion of the cover material  7  is welded to the step portion  10 . 
         [0038]    The double-walled rib  6 , may in one embodiment, have a plate-like structure, in which a part of the second wall  3  is protruded toward the first wall  2  and be integrally welded to the inner surface of the first wall  2 , the protruded wall surface is folded into two wall surfaces, and the two wall surfaces are integrally welded. A shape such as a recess caused by the double-walled rib  6  never emerges on the appearance of the vehicle interior panel  1 . In the case where the double-walled rib  6  is formed, only one stripe emerges on the surface of the second wall  3  by a fold thickness generated in the portion where the two wall surfaces is folded and welded. Form the viewpoint of causing the stripe generated by the double-walled rib  6  to be inconspicuous in appearance, and from the viewpoint of preventing the micro protrusion generated by the stripe from projecting to the surface of the second wall  3 , a groove  11  which is shallower than the thickness of the wall surface of the second wall  3  is formed on the surface of the second wall  3  such that the stripe corresponding to the region where the double-walled rib  6  is formed is concaved from the surface of the second wall  3 . In the vehicle interior panel  1 , a series of weld ribs  12  is provided at an end portion in a longitudinal direction of the double-walled rib  6 . In the weld rib  12 , a part of the second wall  3  is protruded toward the first wall  2  to be integrally welded to the backside of the first wall  2 , and the protruded portion is formed in the concave shape. 
         [0039]    Another embodiment of the invention is described with reference to  FIGS. 5 to 7 . However, the same mode as  FIGS. 1 to 4  is designated by the same reference numeral, and the description of the same mode will not be repeated.  FIG. 5  is a perspective view of a vehicle interior panel according to another embodiment of the invention,  FIG. 6  is a partially detail perspective view of  FIG. 5 , and  FIG. 7  is a sectional view taken on line B-B of  FIG. 6 . 
         [0040]    A linear hinge portion  24  separating hollow spaces  4  can be formed in the vehicle interior panel  1 . In the hinge portion  24 , a part of the second wall  3  is protruded toward the first wall  2  and integrally welded to the backside of the first wall  2 . The parting line  9  is formed on the peripheral wall  5  connecting the first wall  2  and the second wall  3 . The hinge portion  24  has a linear thin single-wall structure in which the first wall  2  and the second wall  3  are welded to each other, and a part of the panel can be opened and closed through the hinge portion  24 . The parting line  9  includes a substantially linear portion  9   a  and a portion  9   b . The portion  9   b  is located close to the side of the first wall  2  in the vicinity of the hinge portion  24 . The first wall  2  is substantially formed in flat, and the hinge portion  24  is formed in the substantially same surface as the first wall  2 . Therefore, there is no recess such as the groove in the first wall  2  at the position corresponding to the hinge portion  24 , and rattle or catching is not generated when a baggage and the like are placed on the vehicle interior panel  1 . Further, when the three-dimensional pattern is transferred by the mold, the vehicle interior panel  1  having the good appearance can be obtained while deformation such as elongation and surface irregularity is not generated in the three-dimensional pattern. 
         [0041]    The plural double-walled ribs  6  are formed in parallel with the hinge portion  24 , and both ends of the double-walled rib  6  extending in parallel with the hinge portion  24  are formed while spaced from the peripheral wall  5 . The hollow space  4  is not separated by the double-walled rib  6 , but the hollow space  4  is separated only by the hinge portion  24 . Therefore, because the hollow spaces  4  communicating one another are filled with a pressurized fluid while blow molding since the pressurized fluid is not obstructed by the double-walled ribs  6 , the provision of at least two blow nozzles is enough to introduce the pressurized fluid into a parison. Further, the double-walled ribs  6  can intermittently be formed in order to fill the parison with the pressurized fluid. That is, the double-walled rib  6 , linearly formed from one end of the peripheral wall  5  toward the other end, can be formed by dividing the double-walled rib  6 , so that the pressurized fluid can flow through gaps between the double-walled ribs  6 . 
         [0042]      FIG. 8  is a perspective view showing a mode in which the automobile is equipped with a floor panel which is of an example of the vehicle interior panel according to the invention. The vehicle interior panel  1  illustrated in  FIGS. 1 to 7  is an automobile floor panel  13 , and the floor panel  13  is furnished in a luggage compartment  15  of an automobile  14  as shown in  FIG. 8 . 
         [0043]    Any thermoplastic resin in which the blow molding can be performed is used as the thermoplastic resin of which the vehicle interior panel  1  is made. Examples of the thermoplastic resin include, but are not limited to, polyolefin resins such as a polyethylene resin, and a polypropylene resin, a polyvinyl chloride resin, an ABS resin (acrylonitrile-butadiene-styrene resin), a polyamide resin, a polystyrene resin, a polyester resin, polycarbonate resins engineering plastics such as modified polyphenylene ether and a mixture thereof. In some embodiments, fillers such as glass fiber, carbon fiber, calcium carbonate, talc, and mica can be added as appropriate. 
         [0044]    The vehicle interior panel  1  according to the invention is blow-molded by the laminating blow molding method shown in  FIGS. 9 to 11 .  FIG. 9  is a sectional view showing a blow molding mode of a blow molded component with skin,  FIG. 10  is a partially enlarged sectional view of  FIG. 9 , and  FIG. 11  is a partially enlarged sectional view showing a mode in which the blow molding is finished after clamping. 
         [0045]    In  FIGS. 9 to 11 , the reference numerals  16  and  17  designate a pair of mold halves, a cavity of the mold  16  has a three-dimensional transfer surface  18  which transfers the three-dimensional pattern  8  formed on the surface of the cover material  7 . Slide cores  19  which form the double-walled ribs  6  are provided on the mold  17 . The reference numeral  20  designates an extruding head, and the reference numeral  21  designates a parison. 
         [0046]    When the blow molding of the vehicle interior panel  1  is performed, the mold halves  16  and  17  are opened, and the cover material  7  is placed between the parison  21  and the cavity of the mold  16  while the parison  21  is arranged or disposed between the mold halves  16  and  17 . In the cover material  7  arranged between the mold halves  16  and  17 , a non-woven fabric is placed on the surface facing the parison  21 . 
         [0047]    The cover material  7 , arranged between the parison  21  and the cavity of the mold  16  having the three-dimensional transfer surface in the pair of mold halves  16  and  17 , has a double-layer structure in which the non-woven fabric is bonded to the resin sheet. In one embodiment, the resin sheet is made of the thermoplastic resin has no through hole, and the resin sheet does not substantially have air permeability. In the thermoplastic resin, the average thickness is no more than 2.0 mm, tensile modulus is 500 kg/cm 2  at 100° C., and the tensile strength at yield point is no more than 50 kg/cm 2  at 100° C. In the non-woven fabric, the weight per area is no more than 250 g/cm 3 . 
         [0048]    The slide cores  19  provided on the mold  17  intrude while the mold halves  16  and  17  are clamped, parts of the parison  21  pushed out by the slide cores  19  are welded by coming into contact with each other. Then, the pressurized fluid is introduced into the parison  21  while the slide cores  19  are retracted to the cavity of the mold  17 , the cover material  7  is pressed against the cavity of the mold  16  to transfer the three-dimensional pattern  8  corresponding to the three-dimensional transfer surface to the surface of the cover material  7  by expanding the parison. In the portions protruded by the slide cores  19 , the wall surfaces are welded to each other to form the double-walled rib  6  having the integral plate-like structure between the first wall  2  and the second wall  3 . 
         [0049]    That is, in the vehicle interior panel  1 , the flat resin sheet having no substantial not-flat pattern or texture in which the non-woven fabrics whose weight per areas are no more than 250 g/m 2  are laminated is arranged between the parison  21  and the mold halves  16  and  17 , the parison  21  and the cover material  7  which are in the melting state are integrally laminated by the blow molding, and the integrally laminated parison  21  and cover material  7  are pressed against the mold half  16  on which the three-dimensional transfer surface  18  is formed on the cavity, which transfers three-dimensional pattern  8  including the hemispherical protrusion, the projection, the recess, the projection and recess, or the embossing shape to the surface of the resin sheet. Therefore, the vehicle interior panel  1  in which the protruding three-dimensional pattern having the height ranging from 200 to 2500 μm is preferably formed by the three-dimensional transfer surface  18  provided in the cavity of the mold half  16  can be obtained, even if the resin sheet  7  is prolonged while blow molding. 
         [0050]    Three-dimensional transfer surface  18  formed in the cavity of the mold half  16  is one in which the recesses are formed by machining or etching the cavity surface. While blow molding, the resin sheet is integrally laminated to the parison  21 , and the shape corresponding to the recesses is transferred to the surface of the resin sheet by pressing the resin sheet against the cavity surface. Therefore, the blow molding component  1  with skin having the protruding three-dimensional pattern can be obtained. At this point, the three-dimensional transfer surface  18  is formed in at least a part of the cavity, however, it is preferable that the regularly arrayed recesses are provided in the whole surface of the cavity. 
         [0051]    The cavity of the mold  16  in the pair of mold halves  16  and  17  has a step forming portion  23  on the whole circumference along a pinch-off forming portion  23 . In the pinch-off forming portion  23 , the end of the cover material  7  is integrally fixed to the parison  21  by pressing the end of the cover material  7  against the parison  21 . 
         [0052]    The cover material  7  is arranged between the parison  21  and the cavity of the mold  16  in the pair of mold halves  16  and  17 , and it is desirable that the clamping is performed without softening the cover material  7  by the heating process from the viewpoint of shortening the molding cycle. After the parison  21  drops vertically between the mold halves, it is preferable that a pre-pressurized fluid is introduced into the parison by pre-blow before the clamping from the viewpoint of molding. 
         [0053]    The vehicle interior panel  1  is produced by the so-called direct blow molding, in which the tubular parison  21  extruded by the extruding head  20  is used, as an example of the method of producing the vehicle interior panel  1 . Alternatively, the vehicle interior panel  1  can also preferably be molded by the so-called sheet blow molding in which a previously molded olefin resin sheet is arranged between the molds and the blow molding is performed by heating and melting the resin sheet, and the vehicle inner panel  1  can also be preferably molded by the method in which the melt-extruded sheet-like parison is used. In the case where the vehicle interior panel  1  is formed by the sheet blow molding, the cover material can previously be laminated to the olefin resin sheet or the like. 
         [0054]    A method of producing the vehicle interior panel shown in  FIGS. 5 to 7  according to another embodiment of the invention will be described below with reference to  FIG. 12 . However, the same mode as  FIGS. 9 to 11  is designated by the same reference numeral, and the description of the same mode will not be repeated. 
         [0055]      FIG. 12  is a sectional view showing a vehicle interior panel blow molding mode according to another embodiment of the invention. 
         [0056]    A hinge forming portion  27  is provided in the cavity of the mold  17 , and the cavity of the mold  17  has a parting surface including a substantially linear pinch-off forming portion  25   a  and a pinch-off forming portion  26   a  projected from the cavity surface near the hinge forming portion. On the other hand, the cavity of the mold  16  has the parting surface including a substantially linear pinch-off forming portion  25   b  and a pinch-off forming portion  26   b  corresponding to the projected pinch-off forming portion. 
         [0057]    When the blow molding of the vehicle interior panel  1  is performed, the cover material  7  is arranged between the parison  21  and the mold  16 , and the mold halves  16  and  17  are clamped to form the parting line  9  corresponding to the parting surface. Then, parts of the parison are welded to each other by the hinge forming portion  27  provided in the mold  17 , and the pressurized fluid is introduced into the parison to form the hinge portion  24  separating the hollow spaces in the substantially same surface as the first wall  2  by the blow pressure. 
         [0058]    According to this embodiment, on the peripheral wall  5  connecting the first wall  2  and the second wall  3  of the panel having the hollow double-walled structure, the parting line  9  including the portion  9   b  close to the side of the first wall  2  is formed near the substantially linear portion  9   a  and the hinge portion  24 , and the end of the cover material  7  is laminated along the parting line  9  formed on the peripheral wall  5 . Therefore, the substantially flat surface can be obtained on the first wall  2  while the unnecessary recesses are not formed on the first wall  2 , and the peeling is not generated because the end of the cover material is strongly fixed. The step portion  10  is provided in the parting line  9 , which allows the cover material  7  to be strongly fixed without generating wrinkle or breakage caused by the excessive elongation at the end of the cover material  7 . Because the parting surfaces of the mold half forming the parting line  9  is formed at the positions close to the side of the first wall  2  by winding the parting line of the mold at the position corresponding to the hinge portion  24 , the end of the cover material  7  is strongly fixed, and the sheet peeling caused by the motion of the hinge portion is prevented. Further, since the first wall  2  is substantially formed in flat, even if the three-dimensional pattern  8  is transferred to the surface of the cover material  7 , the transfer unevenness produced by other methods is not generated, and the vehicle interior panel  1  having the good appearance can be obtained. 
         [0059]    The invention relates to the blow-molded panel with skin that is used as the vehicle interior panel, the method of producing the panel with skin, and the laminating blow molding method. The panel with skin is the vehicle interior panel used for the lid panel and shelf board of the luggage compartment of the automobile such as the floor panel, the luggage board, and the shelf panel, and the panel with skin is the panel having the hollow double-walled structure in which the cover material is integrally laminated by the blow molding.