Abstract:
The present invention relates to a rubber injection molding nozzle, and an injection molding machine and method using the nozzle, used mainly for the injection molding of rubber articles such as rubber vibration insulators for automobiles. It is aimed to increase the molding efficiency and productivity of rubber products and to reduce production cost. At least one portion of an injection channel extending through the injection molding nozzle is formed as an orifice having a non-circular flattend cross section, such that, at least at around major axial ends, a dimension measured orthogonal to its major axis gradually decreases as either of major axial ends is approached. For example, in the cross section, two opposed curved interior wall faces join together to form an acute-angled corner, at major axial ends. This construction enhances the effect of the internal heat generation of the rubber passing through the non-circular cross-sectional portion, facilitating the temperature rise even at center core portion of the rubber. Thus, curing time is shortened thanks to temperature rise of the whole rubber due to the internal heat generation.

Description:
TECHNICAL FIELD 
     The present invention relates to a rubber injection molding nozzle used mainly for injection molding of rubber products such as rubber vibration insulators for automobiles, and an injection molding machine and a molding method. 
     BACKGROUND OF THE INVENTION 
     Relatively small rubber products, such as rubber vibration insulators or the like for automobiles, are manufactured by injection molding in general. In most cases, a preplasticizing type of injection molding machine or inline screw injection molding machine is used. 
     A preplasticizing type of injection molding machine A, as shown in FIG. 14, comprises a plasticizing mechanism  70  for plasticizing a molding material, or rubber (unvulcanized rubber) and feeding it to the front portion of an injection cylinder  61 , and an injection device  60  for injecting rubber being fed into a mold  40  and pressing it, such machines being classified into the plunger preplasticizing type and the screw preplasticizing type according to how rubber is pressed in. 
     An injection molding machine B of the inline screw type, as shown in FIG. 15, which is also referred to as the reciprocating screw type, has an injection device  60  provided with a screw  62  for plasticizing and measuring a molding material, or rubber, said screw  62  also performing the function of a plunger to inject the rubber resided in the front portion of an injection cylinder  61  into a mold  40  to fill the latter therewith. 
     Each of these injection molding machines is provided with a rubber injection molding nozzle  51  at the front end of the injection cylinder  61  of the injection device  60 . 
     This nozzle  51 , as shown in FIG. 16, has an injection channel  55  extending, through the nozzle  51 , from the side of an attaching portion  52  at which the nozzle is attached to said injection cylinder  61 , to the front end  51   a.  The nozzle  51  also has an orifice  56  which is disposed somewhere between the inlet  53  at the attaching side  52  of said channel  55  and the outlet  54  at the front end or which is disposed at the front end. This orifice  56  serves to increase the flow velocity of the rubber by reducing the channel diameter. Thereby, the heated rubber extruded from the cylinder  61  flows through said channel  55 , having its flow velocity increased by the effect of constricting by said orifice  56 , so that it is injected at high speed from the outlet  54  at the front end into the sprue  41  of the mold  40 . 
     In this connection, in the industry using such rubber products produced by injection molding, particularly the automobile parts industry, cost reduction is urgent requirement and measures to meet this requirement are being investigated. As a means therefor, it could be contemplated to enhance internal heat generation of the rubber passing through the nozzle so as to increase the temperature of the rubber being injected, thus shortening the vulcanization time in the mold. 
     However, in the conventional nozzle  51  shown in FIG. 13 used in injection molding of rubber vibration insulator for automobile, the cross sectional shape of said orifice  56  is a simple circle, so that although more or less heat generation is brought about by passage of the rubber through said orifice  56 , the effect of the vulcanization time reduction due to such heat generation is small. 
     In particular, the peripheral portion of the rubber passing through the orifice  56  receives a force of friction against the interior wall face of the orifice and the shearing stress in the rubber thereby increases; thus, the temperature of generated heat, though increased to some extent, is not very high in the innermost portion, which means that there are differences in temperature within the rubber being injected. Therefore, in order to ensure thorough vulcanization within the rubber, it is necessary to set the vulcanization time on the basis of this low temperature rubber portion, presenting a problem that the vulcanization time is correspondingly prolonged. 
     SUMMARY OF THE INVENTION 
     The present invention provides a rubber injection molding nozzle which has an injection channel extending therethrough, characterized in that at least one portion of said injection channel constitutes an orifice having a non-circular cross section, said orifice having a flattened cross sectional shape such that it is elongate in one direction and such that at least at around major axial ends, a dimension measured orthogonal to its major axis gradually decreases as either of said major axial ends is approached. 
     When this injection molding nozzle is used to injection-mold a rubber article, a molding material, or rubber, passes through said injection channel, it being noted that at said orifice, the surface area is greater than at a circular cross section having the same cross sectional area. Therefore, the area of contact of the rubber passing through this portion is increased, thus increasing the frictional force acting on the rubber and the shearing stress produced in the rubber. As a result, the effect of the internal heat generation of the rubber itself is enhanced, thus achieving effective temperature rise due to the internal heat generation of the entire rubber. Thereby, the vulcanization time can be shortened. 
     In said rubber injection molding nozzle, said orifice having a non-circular cross section may be disposed between the ends of said injection channel. 
     In this case, when the molding material, or rubber, passes through said orifice, shearing stresses are produced in the rubber to heat the rubber internally. In addition to this, because of this orifice having a non-circular cross section, the area of contact of the rubber increases as compared with an orifice of circular cross section having the same cross sectional area, so that the frictional force acting on the rubber is increased, thus further increasing the shearing stresses produced in the rubber. As a result, the effect of the internal heat generation of the rubber itself is further enhanced, so that the temperature rise due to the internal heat generation extends deep into the innermost portion, thus minimizing the difference in temperature within the rubber and maximizing the vulcanization time reduction effect. For example, even when the vulcanization time is set on the basis of the portion of lowest temperature so as to ensure thorough vulcanization of the entire rubber, the vulcanization time can be greatly reduced, thereby achieving the cost reduction of rubber products. 
     Also in the case where the orifice having a non-circular cross section constitutes the outlet end of said injection channel, the effect of the internal heat generation of the rubber itself, as in the case described above, is further enhanced, so that the temperature rise due to the internal heat generation extends deep into the innermost portion, thus greatly reducing the vulcanization time. 
     Further, said orifice of flattened shape may be such that the interior wall face of said orifice may form substantially an acute-angled corner at around the opposite major axial ends in the cross section. In otherwise, said orifice may have a flattened substantially elliptic cross section. 
     In the case of this shape, the passage of the molding material, or rubber, through said orifice results in a shearing stress being produced in the rubber, thus internally heating the rubber itself, of course, and since said orifice is of said flattened shape, for example, substantially elliptic, the peripheral length of the interior wall face is increased as compared with an orifice of circular cross section having the same cross sectional area, so that the area of contact between the rubber passing through the orifice and said interior wall face is increased and is the shearing force produced in the rubber. Further, because of the shape in which the opposed interior wall faces gradually approach each other at the opposite major axial ends, the frictional force produced in the rubber also increases, thus enhancing the effect of the internal heat generation of the rubber itself. Moreover, since the orifice is of flattened shape, the temperature rise due to the internal heat generation of the rubber extends deep into the middle portion, so that the temperature rise of the entire rubber is effectively achieved and moreover the difference in temperature between the innermost and peripheral portions is minimized. Therefore, the effect of the shortening of the vulcanization time is enhanced. 
     In said nozzle, the ratio of the minor axial diameter to the major axial diameter in the orifice of flattened substantially elliptic cross section, (minor axial diameter/major axial diameter), is set preferably in the range from 1/2 to 1/5. 
     That is, if the ratio of minor diameter to major diameter (i.e., flatness factor) is less than 1/5, the shape is excessively flattened, resulting in increased resistance to passage of rubber, thus requiring an increased injection pressure. Further, if said flatness factor is greater than 1/2, the effect of being flattened shape is decreased. From this viewpoint of effects, it is particularly preferable that the flatness factor be in the range from 1/3 to 1/5. 
     As for said orifice of flattened substantially elliptic cross section in said nozzle, it may be such that two curved interior wall faces are opposed to each other and join together to form a substantially acute-angled corner at the major axial ends in the cross section. For example, it may be such that two interior wall faces in the form of arcs of relatively large radius are opposed to each other and crosswise join together at opposite ends of the arcs, thereby forming a shape like an eye. 
     In this case, as in the above, the effect of the internal heat generation of the rubber itself is enhanced, so that the temperature rise due to the internal heat generation of the entire rubber is effectively achieved. Moreover, configurationally, at the opposite major axial ends, the opposed curved interior wall faces gradually approach each other, so that the friction between the rubber passing through the orifice and said interior wall faces increases the shearing stress produced in the rubber. Thus, the effect of the internal heat generation of the rubber itself is further enhanced, to provide an excellent vulcanization time reduction effect. 
     Particularly, when said opposite major axial ends are bent with a radius of not more than 1.0 mm, the shearing stress produced in the rubber increases, and so does the effect of the internal heat generation of the rubber. 
     Further, from the viewpoint of the effect of the internal heat generation of the rubber, said orifice is preferably such that the major axial diameter is not more than 8 mm and such that the opposed curved interior wall faces are arcuate with a radius of not more than 14 mm. 
     Further, in said orifice, at least one of the two interior wall faces opposed to each other across the major axis of the cross sectional shape may be provided with an inwardly extending projection. In this case also, the area of the interior wall face of the orifice increases and so does the area of contact with rubber, increasing the shearing stress produced in the rubber, enhancing the effect of internal heat generation of the rubber, thus providing a further enhanced vulcanization time reduction effect. 
     Further, in the case of said orifice of substantially elliptic cross section, a preferable arrangement is such that said orifice is in the range of 10-70 mm from the outlet at the front end and that said orifice joins to channel portions upstream (inlet side) and downstream (outlet side) of the orifice through taper portions, respectively. 
     Thereby, the injected rubber is passed through the orifice without encountering excessive resistance and then through the downstream channel portion without abrupt expansion and injected into a mold through the outlet; thus, the effect of said vulcanization time reduction can be satisfactorily retained. 
     In addition, if the position of said orifice comes closer to the outlet than it is mentioned above, the opening angle of the taper portion downstream of the orifice becomes larger or it becomes impossible to provide such taper portion in the downstream side, and if it is spaced further away from the outlet than it is mentioned above, the distance from the orifice to the outlet is too long, incurring a danger of the temperature of the rubber dropping before the rubber is injected into the mold. Therefore, it is preferable that the position of the orifice be within said range, more preferably in the range of 20-40 mm from the outlet. 
     Further, from the viewpoint of said effect, it is preferable that the opening angle of the taper portion located upstream of the orifice in said injection channel be 30°-90° and that the opening angle of the taper portion located downstream of the orifice be 15°-60°. 
     That is, if the opening angle of said upstream taper portion is smaller than it is mentioned above, the taper portion becomes longer, while if it is larger than it is mentioned above, the resistance to passage of the rubber through the orifice increases. Further, if the opening angle of the downstream taper portion is smaller than it is mentioned above, the taper portion becomes longer, resulting in an increased distance from the outlet to the orifice, while if it is larger than it is mentioned above, the effect to be obtained by the provision of the taper portion cannot be fully attained, incurring a danger of the rubber temperature going down. 
     Said orifice constituting one portion of said injection channel may be one having a plurality of openings. 
     In this case also, the passage of rubber through the plurality of openings in the orifice results in a high shearing stress is produced in each portion of rubber passing through each opening, and the effect of the internal heat generation of the rubber extends over the entire rubber being discharged from the nozzle, thus effectively realizing the temperature rise. 
     It is preferable that the cross sectional area of said orifice be not more than 20 mm 2  and that the percentage thereof to the cross sectional area of the channel portion located upstream of the orifice be not more than 20%, whereby the effect of constricting by the orifice and the effect of heat generation can be fully exerted. 
     From the viewpoints of the effect of constricting by the orifice and the effect of the internal heat generation of the rubber, it is particularly preferable that the cross sectional area of the orifice be not more than 5 mm 2  and that the percentage thereof to the cross sectional area of the channel portion located upstream of the orifice be not more than 5%. 
     A rubber injection molding machine having said injection molding nozzle is capable of reducing the rubber molding vulcanization time by the non-circular cross sectional shape of the orifice or the like in the injection channel of the nozzle. Further, by suitably selecting said cross sectional shape according to the kind of the rubber product to be molded, it is also possible to adjust the vulcanization time and hence the molding cycle time. 
     Thus, a plurality of said injection molding machines which differ in the kind of rubber products to be molded may be installed with their cycle times adjusted to each other, whereby it is possible to simultaneously mold a plurality of kinds of rubber products, thus improving the efficiency of small-lot production of a wide variety of rubber products. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a sectional view showing a rubber injection molding nozzle according to an embodiment of the present invention; 
     FIG. 2 is a front view taken from the outlet of said nozzle; 
     FIG. 3 is an enlarged explanatory view showing the cross sectional shape of the orifice of said nozzle; 
     FIG. 4 is an explanatory view showing another example of the cross sectional shape of the orifice; 
     FIG. 5 is an explanatory view showing still another example of the cross sectional shape of the orifice; 
     FIG. 6 is an explanatory view showing still another example of the cross sectional shape of the orifice; 
     FIG. 7 is an explanatory view showing still another example of the cross sectional shape of the orifice; 
     FIG. 8 is an explanatory view showing still another example of the cross sectional shape of the orifice; 
     FIG. 9 is an explanatory view showing still another example of the cross sectional shape of the orifice; 
     FIG. 10 is a sectional view of a rubber injection molding nozzle according to another embodiment; 
     FIG. 11 is a sectional view of a rubber injection molding nozzle according to still another embodiment; 
     FIG. 12 is a sectional view showing an example of a rubber product to be injection-molded; 
     FIG. 13 is a sectional view showing an another example of a rubber product to be injection-molded; 
     FIG. 14 is sectional view showing the outlines of an injection molding machine; 
     FIG. 15 is sectional view showing the outlines of another injection molding machine; 
     FIG. 16 is a sectional view of a conventional injection molding nozzle. 
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Embodiments of the present invention will now be described with reference to the accompanying drawings; however, the invention is not limited thereto. 
     FIGS. 1 through 3 show a rubber injection molding nozzle according to an embodiment of the present invention. 
     This injection molding nozzle  1  in this embodiment, as in a conventional nozzle, is attached to the front end of the injection cylinder  61  of an injection molding machine shown in FIG. 14 or  15 . The front end  1   a  of the nozzle is frusto-conical, adapted to be fitted to a filling port for a mold, while the rear end of the nozzle is an attachment  2  having on its outer periphery a screw thread  2   a  for attaching to said injection cylinder  61 . This nozzle  1  has, in its interior, an injection channel  5  extending therethrough to the front end  1   a  from an inlet  3  on the side associated with said attachment  2 . This injection channel  5  is internally provided with an orifice  6  disposed between the inlet  3  and the outlet  4  at the front end, for example, as shown, somewhere in the channel for reducing the channel diameter to increase the flow velocity of rubber, which is a molding material. 
     The injection channel  5  has the channel portions  5   a  and  5   b,  which are located upstream (inlet side) and downstream (outlet side) of the orifice respectively, and are circular in cross section. The diameter of the downstream channel portion  5   b  is set to about 1/2-1/3 of the diameter of the upstream channel portion  5   a.    
     The orifice  6  in the injection channel  5  has at least one non-circular cross section. In the cross sectional shape of this orifice  6 , one of the vertical and horizontal dimensions is larger than the other such that the cross sectional shape is flattened in the direction orthogonal to the longer dimension. It is preferred that at least at the opposite major axial ends, the dimension taken orthogonal to the major axis decreases as said opposite ends are approached. 
     For example, as shown enlarged in FIG. 3, it has a relatively flattened substantially elliptic cross sectional shape. Reference numerals  6   a,    6   a  designate the opposite major axial ends in the cross sectional shape. Meanwhile, reference numerals  6   b,    6   b  designate two curved inner wall faces opposed to each other across the major axis of the cross sectional shape. 
     The flattened substantially elliptic cross sectional shape of the orifice  6  may be a shape in which the opposite major axial ends  6   a,    6   a  are rounded with a predetermined radius as in a true or usual ellipse. However, in practice, the cross sectional shape is preferably a shape in which, as shown in FIG. 3, the two opposed curved interior wall faces  6   b,    6   b  join together in acute-angled bent form at said opposite ends  6   a,    6   a.  The cross sectional shape is more preferably a shape in which two arcuate interior wall faces  6   b,    6   b  of relatively large radius are opposed to each other and in which their arcuate opposite ends crosswise join together. That is a shape similar to, as it were, an eye or a biconvex lens. 
     As for the shape having acute-angled bent form at opposite major axial ends  6   a,    6   a,  the acute-angled bent form may be slightly rounded. However, in practice, it is preferable that the opposite ends  6   a,    6   a  are bent with a radius of not more than 1.0 mm. It is more preferable that the opposite ends  6   a,    6   a  are bent with a very small amount of roundness having a workable radius in the order of about 0.2 mm or with little roundness. 
     It is preferred that the major axial dimension W in the cross sectional shape of said orifice  6  is not more than 8 mm while the two opposed curved interior wall faces  6   b,    6   b  are arcuate with a radius of not more than 14 mm. It is particularly preferable that the major axial dimension W be 2.5-5.5 mm, the radius R of the curved interior wall faces  6   b,    6   b  be in the range of 4-8 mm, while the ratio of the minor diameter T, which is orthogonal to the major axis, to the major diameter W (T/W), namely the flatness factor, be in the range of 1/2-1/5. 
     As for the flattened substantially elliptic cross sectional shape of the orifice  6 , it is not limited to a shape in which the two opposed curved interior wall faces  6   b,    6   b  are arcs with a given radius. The cross sectional shape may be somewhat modified substantially elliptic forms. For example, the curved interior wall faces  6   b,    6   b  may have different radii of curvature at major axial middle portion and at major axial opposite end portions. In another example shown in FIG. 4, the middle portion is flat whereas the opposite end portions alone are curved with a predetermined radius of curvature or substantially linear to form a triangle-like shape at the opposite ends. 
     In each of these cases, towards the major axial opposite ends  6   a,    6   a,  the opposed curved interior wall faces  6   b,    6   b  gradually approach each other, thereby gradually increasing the shearing stress due to the friction between said interior wall faces  6   b,    6   b  and the rubber passing through the opposite end portions. 
     FIG. 5 shows an example in which in the orifice  6  of substantially elliptic cross section, the required region, such as the middle, of at least one of the opposed curved interior wall faces  6   b,    6   b  is provided with a slightly inwardly extending projection  9 . In this case, the peripheral lengths of the interior wall faces  6   b,    6   b  of the orifice  6  are increased, thus increasing the area of contact of said interior wall faces  6   b,    6   b  with the rubber passing through the orifice  6 . Though not illustrated, when recesses are formed in said interior wall faces  6   b,    6   b,  the area of contact of the interior wall faces with the rubber also increases. 
     FIG. 6 shows an example in which in the orifice  6  of substantially elliptic cross section, the interior wall face  6   c  being peripherally corrugated. In this case, the area of contact between the rubber passing through the orifice  6  and the interior wall face  6   c  increases, and the presence of the corrugation makes it easier for the shearing stress to be produced, so that the effect of internal heat generation due to the rubber passing through the orifice  6  is enhanced and the temperature rise due to heat generation easily extends deep into the rubber. 
     Further, the orifice having a non-circular cross section is not limited to those described above whose basic form is said substantially elliptic cross sectional shape. For example, as shown in FIG. 7, the cross section may have a flattened substantially rhombic shape in which the opposite major axial ends  6   a,    6   a  join together in a corner-forming manner. Besides this, the cross sectional shape may be a substantially rectangular shape, a shape in which the longitudinal opposite ends of such substantially rectangular shape are semi-circular, or other elongated integral shapes. However, from the viewpoint of the effect of internal heat generation at the opposite end portions, such cross sections are preferable as one in which the opposite major axial ends are in a corner-forming manner and continuous, as in the embodiment described above, and another which is provided with projections or corrugations. Cross sections of other shapes may also be employed. 
     Further, the orifice  6  having a non-circular cross section in the injection channel  5  may also be embodied in a form having a plurality of openings  6   d,  as shown in FIG.  8 . In this case, as compared with an orifice having the same cross sectional area, the area of contact of the wall face with the rubber passing through the openings  6   d  in the orifice  6  is increased. Further, passing through the narrow openings results in an increased shearing stress within the rubber, enhancing the effect of the internal heat generation of the rubber, so that the temperature of the rubber being injected from the nozzle uniformly rises throughout. 
     In addition, the plurality of openings  6   d  are not limited to circular ones as shown, and various forms may be used; for example, as shown in FIG. 9, a circular orifice  6  may be internally provided with a crisscross member  6   e  to divide the orifice  6  into a plurality of sectorial openings  6   d.    
     In each embodiment described above, the length of the orifice  6  is preferably about 2-5 mm, though differing according to configurational factors including the cross sectional shape and area and the major axial dimension. And it is possible to decrease or increase the above-mentioned value of the length, and the greater the length, the higher the constricting effect and the heat generating effect, but the injection resistance correspondingly increases. 
     As shown in FIG. 10, the orifice  6  might be connected to the upstream and downstream channel portions  5   a  and  5   b  through respective ledges. However, in usual cases, as shown in FIG. 1, there are taper portions  7   a  and  7   b  which, preferably, gradually increase in diameter from the orifice  6  and lead to the upstream and downstream channel portions  5   a  and  5   b.  This construction allows the rubber to smoothly pass through the orifice  6  from the channel portion  5   a  via the taper portion  7   a  and to flow into the channel portion  5   b  while gradually expanding at the downstream taper portion  7   b.    
     Particularly, in the case of a sharp increase in diameter starting from the orifice  6  toward the channel portion  5   b  downstream of the orifice  6 , the rubber passing through the orifice  6  sharply expands to be deprived of heat, so that its temperature undesirably drops. 
     Further, it is preferable that the opening angle α 1  of the taper portion  7   a  upstream of the orifice  6  of said channel  5  be 30-90° and that the opening angle α 2  of the taper portion  7   b  downstream of the orifice  6  of said channel  5  be 15-60°. Usually, the opening angle α 2  of the downstream taper portion  7   b  should be smaller than the opening angle α 1  of the upstream taper portion  7   a.  For example, in the case of the embodiment shown in FIG. 1, the opening angle α 1  of the taper portion  7   a  is 60° and the opening angle α 2  of the taper portion  7   b  is 30°. 
     Further, the position of the orifice  6  may be anywhere between the inlet  3  and the outlet  4  of the injection channel  5  in the nozzle; for example, the orifice may be positioned so as to constitute an outlet  4 . In practice, however, it is located in the range preferably from 10 to 70 mm, more preferably from 20 to 40 mm, from the outlet  4 . 
     On one hand, in order to inhibit the sharp expansion of the rubber passing through the orifice  6 , the taper portion  7   b  leading to the channel portion  5   b  associated with the outlet is required. On the other hand, the longer the time taken for the rubber passing through the orifice  6  to be injected into the mold, the greater the tendency of the temperature of the rubber to decrease, which means that the effect of vulcanization time reduction cannot be obtained. Therefore, it is preferable that it be positioned within the aforesaid range. 
     It is preferable that the cross sectional area of said orifice  6  be not more than 20.0 mm 2  and its percentage to the cross sectional area of the upstream channel portion  5   a  be not more than 20%. If the cross sectional area and its percentage exceed said values, the constricting effect due to the provision of the orifice  6  cannot be obtained, nor can it be expected to achieve an increased injection velocity or the effect of heat generation. From the viewpoints of said constricting effect and said effect of heat generation, it is particularly preferable that the cross sectional area of said orifice  6  be not more than 5 mm 2  and be not more than 5% of the cross sectional area of the upstream channel portion  5   a.  If the cross sectional area is too small, the resistance to the flow becomes excessively high, influencing the injection speed; thus, it is preferable to set it to not less than 2.5 mm 2 . 
     FIGS. 10 and 11 respectively show other embodiments of rubber injection molding nozzles according to the present invention, each of which embodiments has the same basic arrangement as in the above embodiment, and like reference characters are affixed to like parts. A detailed description thereof is omitted. 
     In the nozzle  1  of the embodiment shown in FIG. 10, the orifice  6  in the injection channel  5  is disposed more remote from the outlet  4  than in the preceding embodiment. Further, the upstream end of said orifice  6  is linked with the upstream channel portion  5   a  through a taper portion  7   a  having a ledge  8   a  around the orifice opening, particularly through a taper portion  7   a  forming an opening angle α 1  of about 90°. Further, the downstream end of the orifice  6  is linked with the downstream channel portion  5   b  through a ledge  8   b  slightly inclined from the orifice opening end. 
     The nozzle  1  of the embodiment in FIG. 11 is the same in the basic arrangement of the orifice  6  in the injection channel  5  in the above embodiment. However, the upstream end of the orifice  6  is linked with the upstream channel portion  5   a  through a taper portion  7   a  having an opening angle α 1  of 60° as in the embodiment shown in FIG.  1 . Further, the downstream end of the orifice  6  is linked with the downstream channel portion  5   b  through a ledge  8   b  which is slightly inclined as in the above. 
     In addition, the portion having at least one non-circular cross section in the injection channel  5  within the nozzle  1  is not limited to an orifice disposed at an intermediate position between ends of the channel or an orifice disposed on the front-end outlet, as in the illustrated embodiments. Though not illustrated, the injection channel  5  other than the orifice may be formed to have above-described non-circular cross section. Further, a plurality of portions having a non-circular cross section may be formed. 
     The injection molding nozzle  1  for rubber in the embodiments described above is used as in the prior art; the nozzle  1  is attached to the front end of the injection cylinder  61  of the injection device  60  in an injection molding machine A in FIG. 14 or B in  15 . 
     For example, in injection molding using the nozzle  1  of the embodiment shown in FIGS. 1 through 3, unvulcanized rubber, which is a molding material, plasticized in the injection device  60  and extruded from the injection cylinder  61  in a predetermined heated state passes through the injection channel  5  in the nozzle and then through the orifice  6  disposed somewhere in the channel  5 , so that the flow velocity is increased by the constricting effect of the orifice  6 , so that the rubber is injected from the outlet  4  at the front end into the sprue  41  of the mold  40  at high speed to fill the cavity  43  of the mold  40  through a runner  42 . 
     In this case, the rubber to be injected passes through the orifice  6 , whereby shearing stress is produced within the rubber to internally heat the rubber, so that the temperature of the rubber rises. Said orifice  6  has a flattened substantially elliptic cross section, for example, a special substantially elliptic cross section such that two curved interior wall faces  6   b,    6   b  join together to form an acute-angled corner form at the major axial ends  6   a,    6   a  in the cross section. Thus, the area of contact between the rubber passing through said orifice  6  and the interior wall faces of the orifice increases, increasing the frictional force on the rubber and the shearing stress produced in the rubber. 
     Particularly, the nearer to the opposite major axial ends in the orifice  6 , the smaller the distance between the two opposed curved interior wall faces  6   b,    6   b.  For this reason, the rubber in the orifice  6  has its shearing stress further increased in the vicinity of said opposite major axial ends  6   a,    6   a.  And the effect of internal heat generation of the rubber further increases. Furthermore, the temperature rise due to this internal heat generation is effected even at innermost portion in the cross section of the rubber, with the result that the temperature of the entire rubber effectively rises to the extent of minimizing the difference in temperature between the innermost and peripheral portions. 
     A combination of the effect of the temperature rise due to the internal heat generation of the rubber injected into the mold  40  and the effect of the decrease in the difference in temperature in the rubber makes it possible to greatly decrease the vulcanization time, even if the vulcanization time is set on the basis of the portion with the lowest temperature so as to ensure complete vulcanization of the entire rubber. Further, the vulcanization time and hence the molding cycle time can be suitably adjusted and set according to the kind of the rubber product to be molded. 
     Thus, a plurality of said injection molding machines which differ in the kind of rubber products to be molded may be installed with their molding cycle times adjusted to each other, whereby it is possible to simultaneously produce a plurality of kinds of products by injection molding, facilitating the control of molding operation, rationalizing the small-lot injection molding of a wide variety of rubber products, thus increasing the productivity. 
     The effect obtained by the injection molding nozzle of the invention described above is clear from a comparison of vulcanization time in the following injection molding tests on rubber products shown in FIGS. 12 and 13. 
     The table 1 below shows the results of injection molding tests on a rubber product  10  shown in FIG. 12, the injection molding being effected using a rubber material having a rubber compound (a) shown in the table 3 below, at a mold temperature of 160° C. and a controlled screw temperature of 90° C. The hardness of the rubber used was 55 degrees (measured as defined by JIS-A using a hardness tester). 
     In addition, the rubber product  10  in FIG. 12 is a vibration insulator (with a diameter of 50 mm, and a height of 25 mm) for automobiles, comprising two attaching metal parts  11  and  12 , and a rubber body  13  integrally interposed therebetween by vulcanization molding. 
     The table 2 below shows the results of injection molding tests on a rubber product  20  shown in FIG. 13, the injection molding being effected using a rubber material having a rubber compound (b) shown in the table 3 below, at a mold temperature of 170° C. and a controlled screw temperature of 95° C. The hardness of the rubber used was 64 degrees (measured as defined by JIS-A using a hardness tester). 
     The rubber product  20  shown in FIG. 13 is a hollow spring which comprises a plate-like attaching base metal  21  and a hollow rubber body  22  integrally joined thereto by vulcanization molding. The rubber product  20  is used as an auxiliary implement for spring that is installed, for example, in a rear wheel of an automobile to prevent a metal spring from flexing beyond the limit or abutting against the frame. 
     In the tables 1 and 2 below, the injection molding machine B is an inline type of injection molding machine B shown in FIG.  15 . 
     Further, in the tables 1 and 2, (I) in the column titled “Nozzle shape” refers to the nozzle shape in the embodiment shown in FIG. 1, (II) refers to the nozzle shape in the embodiment shown in FIG. 10, (III) refers to the nozzle shape in the embodiment shown in FIG. 11, and (IV) refers to a conventional type of nozzle shown in FIG. 16, the sizes and shapes of the orifice and other portions being as entered in the tables. Further, the initial rubber temperature in the mold shown in the tables is obtained by measuring the temperature of the rubber injected into the mold, and the free shot rubber temperature is obtained by measuring the temperature of the rubber free-injected from the nozzle. 
     Further, in critical cure (vulcanization) time shown in the tables 1 and 2, uncured NG refers to a case (or a case of insufficient vulcanization) in which an unvulcanized portion remains in the rubber of the molded product. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                   
                   
                   
                   
                 Compara- 
               
               
                   
                   
                   
                   
                   
                 tive 
               
               
                   
                 Embodi- 
                 Embodi- 
                 Embodi- 
                 Embodi- 
                 Embodi- 
               
               
                   
                 ment 1 
                 ment 2 
                 ment 3 
                 ment 4 
                 ment 1 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Injection 
                 Molding 
                 Molding 
                 Molding 
                 Molding 
                 Molding 
               
               
                 molding 
                 machine B 
                 machine B 
                 machine B 
                 machine B 
                 machine B 
               
               
                 machine 
               
               
                 Nozzle shape 
                 (I) 
                 (II) 
                 (III) 
                 (III) 
                 (IV) 
               
               
                 Orifice cross 
                 Substan- 
                 Substan- 
                 Substan- 
                 Substan- 
                 Circular 
               
               
                 sectional 
                 tially 
                 tially 
                 tially 
                 tially 
               
               
                 shape 
                 elliptic 
                 elliptic 
                 elliptic 
                 elliptic 
               
               
                 Major axis × 
                 5.5 × 1.3 
                 5.5 × 1.3 
                 5.6 × 1.4 
                 5.6 × 1.4 
                 φ 2.5 
               
               
                 minor axis or 
               
               
                 diameter 
               
               
                 (mm) 
               
               
                 Orifice 
                 2 
                 2 
                 5 
                 5 
                 15 
               
               
                 length (mm) 
               
               
                 Orifice cross 
                 About 5 
                 About 5 
                 About 5 
                 About 5 
                 About 5 
               
               
                 sectional 
               
               
                 area (mm 2 ) 
               
               
                 Taper around 
                 Inlet 60°/ 
                 None 
                 Inlet 60° 
                 Inlet 60° 
                 None 
               
               
                 orifice 
                 outlet 30° 
               
               
                 Inlet channel 
                 12 
                 12 
                 15 
                 15 
                 15 
               
               
                 diameter 
               
               
                 (mm) 
               
               
                 Outlet chan- 
                 6 
                 6 
                 7.5 
                 5.5 
                 5.5 
               
               
                 nel diameter 
               
               
                 (mm) 
               
               
                 Rubber 
                 14-15″ 
                 12-15″ 
                 9-10″ 
                 7-9″ 
                 18-23″ 
               
               
                 injection 
               
               
                 time (sec) 
               
               
                 The initial 
                 148° C. 
                 150° C. 
                 144° C. 
                 146° C. 
                 144° C. 
               
               
                 rubber 
               
               
                 temperature 
               
               
                 in Mold 
               
               
                 The rubber 
                 Not 
                 Not 
                 Not 
                 142° C. 
                 138° C. 
               
               
                 temperature 
                 measured 
                 measured 
                 measured 
               
               
                 on Free shot 
               
               
                 Amount of 
                 240 cc 
                 240 cc 
                 240 cc 
                 240 cc 
                 240 cc 
               
               
                 charge 
               
             
          
           
               
                 Criti- 
                 3 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
               
               
                 cal 
                 min. 
                 NG 
                 NG 
                 NG 
                 NG 
                 NG 
               
               
                 cure 
                 4 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
               
               
                 time 
                 min. 
                 NG 
                 NG 
                 NG 
                 NG 
                 NG 
               
               
                   
                 4.5 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
               
               
                   
                 min. 
                 NG 
                 NG 
                 NG 
                 NG 
                 NG 
               
               
                   
                 5 
                 Cured OK 
                 Uncured 
                 Uncured 
                 Uncured 
                 Uncured 
               
               
                   
                 min. 
                   
                 NG 
                 NG 
                 NG 
                 NG 
               
               
                   
                 6 
                 Cured OK 
                 Cured OK 
                 Cured OK 
                 Cured OK 
                 Uncured 
               
               
                   
                 min. 
                   
                   
                   
                   
                 NG 
               
               
                   
                 7 
                 Cured OK 
                 Cured OK 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                 min. 
               
               
                   
                 8 
                 Cured OK 
                 Cured OK 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                 min. 
               
               
                   
               
             
          
         
       
     
     
       
         
               
               
               
               
             
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                   
                   
                 Comparative 
               
               
                   
                 Embodiment 5 
                 Embodiment 6 
                 Embodiment 2 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Injection molding 
                 Molding 
                 Molding 
                 Molding 
               
               
                 machine 
                 machine B 
                 machine B 
                 machine B 
               
               
                 Nozzle shape 
                 (III) 
                 (III) 
                 (IV) 
               
               
                 Orifice cross sectional 
                 Substantially 
                 Substantially 
                 Circular 
               
               
                 shape 
                 elliptic 
                 elliptic 
               
               
                 Major axis × minor 
                 5.6 × 1.4 
                 5.6 × 1.4 
                 φ 2.5 
               
               
                 axis or diameter (mm) 
               
               
                 Orifice length (mm) 
                 2 
                 2 
                 20 
               
               
                 Orifice cross sectional 
                 About 5 
                 About 5 
                 About 5 
               
               
                 area (mm 2 ) 
               
               
                 Taper around orifice 
                 None 
                 Inlet 60°/ 
                 None 
               
               
                   
                   
                 outlet 30° 
               
               
                 Inlet channel diameter 
                 12 
                 12 
                 15 
               
               
                 (mm) 
               
               
                 Outlet channel 
                 6 
                 6 
                 5.5 
               
               
                 diameter (mm) 
               
               
                 Rubber injection time 
                 24-33″ 
                 24-33″ 
                 17″ 
               
               
                 (sec) 
               
               
                 The initial rubber 
                 Not measured 
                 Not measured 
                 Not measured 
               
               
                 temperature in Mold 
               
               
                 The rubber tempera- 
                 155° C. 
                 155° C. 
                 149° C. 
               
               
                 ture on Free shot 
               
               
                 Amount of charge 
                 About 900 cc 
                 About 900 cc 
                 About 900 cc 
               
             
          
           
               
                 Critical 
                   3 min. 
                 Cured OK 
                 Cured OK 
                 Uncured NG 
               
               
                 cure time 
                   4 min. 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                 4.5 min. 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                   5 min. 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                   6 min. 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                   7 min. 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
                   8 min. 
                 Cured OK 
                 Cured OK 
                 Cured OK 
               
               
                   
               
             
          
         
       
     
     
       
         
               
               
             
               
               
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                 Compound (a) 
                   
               
             
          
           
               
                   
                 Parts 
                 Compound (b) 
               
             
          
           
               
                 component 
                 by weight 
                 component 
                 Parts by weight 
               
               
                   
               
             
          
           
               
                 Natural rubber (NR) 
                 100 
                 Natural rubber (NR) 
                 100 
               
               
                 HAF carbon 
                 38 
                 HAF carbon 
                 58 
               
               
                 Aroma oil 
                 5 
                 Aroma oil 
                 5 
               
               
                 Zinc oxide 
                 5 
                 Zinc oxide 
                 5 
               
               
                 Stearic acid 
                 2 
                 Stearic acid 
                 2 
               
               
                 Wax 
                 1 
                 Wax 
                 1 
               
               
                 Antiaging agent 3C 
                 1 
                 Antiaging agent 3C 
                 1 
               
               
                 Antiaging agent RD 
                 1 
                 Antiaging agent RD 
                 1 
               
               
                 Vulcanization 
                 1 
                 Vulcanization 
                 1 
               
               
                 accelerator CZ 
                   
                 accelerator CZ 
               
               
                 Sulfur 
                 3 
                 Sulfur 
                 3 
               
               
                   
               
               
                 Antiaging agent 3C: N-phenyl-N′-isopropyl-P-phenylenediamine  
               
               
                 Antiaging agent RD: 2,2,4-trimethyl-1,2-dihydroquinoline polymer  
               
               
                 Vulcanization accelerator: N-cyclohexyl-2-benzothiazole sulfeneamide  
               
             
          
         
       
     
     According to the comparative tests for vulcanization time in the above table 1, in the molding of the rubber product shown in FIG. 12, a vulcanization time of 7-8 minutes was required when the conventional nozzle was used, whereas the vulcanization was completed in 5-6 minutes when the present inventive nozzle was used. Further, in the molding of the rubber product shown in FIG. 13, a vulcanization time of 4-8 minutes was required when the conventional nozzle was used, whereas the vulcanization was completed within 3 minutes when the present inventive nozzle was used. 
     Thus, according to the present inventive injection molding nozzle, the effect of temperature rise due to the internal heat generation of the rubber injected into a mold is enhanced, and the difference in temperature in the rubber due to the internal heat generation of the rubber is reduced, thereby greatly reducing the vulcanization time, increasing the efficiency of injection molding of rubber products, improving the productivity, and contributing to the promotion of cost reduction.