Abstract:
A process and catalyst for reducing the nitrous oxide content in gas, which operates at relatively low temperatures, the activity of which is relatively insensitive to the presence of water vapour and which is highly resistant to hydrothermal degradation, is prepared from ferrierite exchanged with iron. Application to the treatment of gases with a low N 2 O content, such as gases resulting from plants for the manufacture of nitric acid, and of gases with a high N 2 O content, which are emitted during oxidations of organic compounds by nitric acid.

Description:
BACKGROUND OF THE INVENTION 
     (i) Field of the Invention 
     The invention comes within the general scope of the reduction of the content of greenhouse gases in gaseous effluents of industrial origin discharged to the atmosphere. It is a question here of lowering nitrous oxide N 2 O in gaseous discharges. 
     (ii) Description of Related Art 
     For a long time, concern was only felt about the discharge of nitric oxides (NOx), which easily combine with water to form nitrous or nitric acids, the most spectacular sign of which is without doubt acid rain, with subsequent destruction of forests and damage to exposed monuments, and the most insidious signs of which are contamination of breathable air and its effect on public health. Awareness has now arisen of the significant contribution of nitrous oxide to enhancing the greenhouse effect, with the risk of leading to climatic changes with uncontrolled effects, and perhaps also of its participation in the destruction of the ozone layer. Its removal has thus become a preoccupation of the authorities and of manufacturers. 
     While the most significant sources of N 2 O are the oceans, uncultivated soils, agriculture, the combustion of organic matter and the use of fossil fuels, the chemical industry contributes some 5 to 10% of emissions of this gas. Nitric acid plants, as well as plants for organic synthesis employing nitric oxidation processes (production of adipic acid, of glyoxal, and the like), are the source of most discharges of N 2 O by the chemical industry (see, in this respect, Freek Kapteijn et al., Heterogenous Catalytic Decomposition of Nitrous Oxide, in Applied Catalysis B, Environmental 9, 1996, 25-64). 
     For some years already, most nitric acid plants have been equipped with so-called DeNOx reactors, which operate satisfactorily in removing nitric oxides from their effluents. However, N 2 O, which is essentially produced during the oxidation of ammonia over the platinum gauzes of the burners, remains substantially constant between the outlet of the burners and the inlet of the DeNO x  reactor and is not lowered by passage of the gases through this reactor (sometimes, it is even slightly increased). 
     Provision has been made to reduce the N 2 O content of the gaseous effluents resulting from nitric oxidation processes in organic chemistry by catalytically destroying the nitrous oxide contained in the latter over a mordenite/iron catalyst (EP 0,625,369). However, on account of the large fall in its activity in the presence of steam in the temperature range 350-450° C., this catalyst is not well suited to functioning with respect to dilute gases and ages badly, due to a mediocre hydrothermal resistance. 
     It also turns out to be economically unsuited to the treatment of the tail gases from nitric acid plants, which, upstream of the expansion turbine, generally correspond to the following characteristics, 
     
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 temperature: 
                 &lt;400° C., 
               
               
                   
                 N 2 O content: 
                 between 500 and 1500 ppmv, 
               
               
                   
                 NOx content: 
                 between 50 and 2000 ppmv, 
               
               
                   
                 H 2 O content: 
                 between 0.5 and 5%. 
               
               
                   
                   
               
             
          
         
       
     
     The economic optimization of the lowering of N 2 O both in the gases emitted by organic plants and by nitric acid plants involves the development of a catalyst which retains a good activity for the destruction of N 2 O at a temperature below 400° C. in the presence of NOx and of steam, and which has a sufficient hydrothermal stability at 600° C to withstand the temperature peaks to which it may be subjected under certain circumstances in its use. 
     SUMMARY OF THE INVENTION 
     A solution corresponding to such specifications has just been found with a catalyst composed of agglomerates formed of 80 to 90% of a ferrierite/iron assaying from 1 to 6% of iron, and preferably from 2 to 4%, and of 20 to 10% by weight of an agglomeration binder (percentages by weight with respect to the weight of the granule). 
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
     The ferrierite/iron is the active component of the catalyst according to the invention. The structure of its crystal lattice is that of ferrierite [RN=12173-30-7], that is to say a zeolite traversed by two systems of channels, one parallel to the c axis of the structure, formed of channels with an elliptical cross-section (0.43 nm×0.55 nm) of approximately 0.18 nm 2  (18 Å 2 ), the other parallel to the b axis and the c axis of the structure, with channels formed of 8-membered rings, with 0.34×0.48 nm axes. There is no channel parallel to the a axis. Approximately spherical cavities, with an approximate diameter of 0.7 nm, lie on these channels and are accessible only through the 8-membered rings, i.e. via 0.43 nm×0.55 nm or 0.34 nm×0.48 nm pores. The ferrieritic structure is completely characterized by its X-ray diffraction diagram (for the interlattice distances, consult Breck “The Synthetic Zeolites”, 1974 Edition, Table 4.45, p. 358). 
     This ferrierite/iron is obtained by subjecting a commercial ferrierite, of sodium/potassium type, to exchange with an aqueous solution of an iron salt, so as to obtain the desired iron content. The operating procedures are well known to a person skilled in the art. It is possible, in particular, to carry out one or more exchanges by immersion in an iron salt solution or by column percolation, either of the ferrierite powder itself or with respect to granules. 
     This exchange can be carried out either using a ferric salt solution or using a ferrous salt solution. Use is advantageously made of ferrous sulphate, which is a very low cost product and which does not introduce chlorides, which are sources of corrosion, into the preparation. 
     Preference is given to the form exchanged with iron starting from the ammonium form of ferrierite, which is obtained by subjecting a commercial ferrierite, the electrical neutrality of the crystallographic lattice of which is essentially produced by sodium and potassium alkali metal ions, to an exchange with a solution of an ammonium salt. The ferrierite/iron obtained from the ammonium form of ferrierite exhibits, as characteristic, that of having a very low content of alkali metal ions in the exchange position. It is the low content of potassium ions (less than 0.5% by weight) which analytically indicates this preferred form of the catalyst of the invention. The ferrierites/iron according to the invention contain only 0.5 to 0.1% of potassium. 
     The catalysts according to the invention are shaped as agglomerates, a presentation which is necessary for reasons of minimization of the pressure drop as they pass through the catalyst bed. The agglomeration of zeolites is well known to a person skilled in the art. It is carried out by forming a paste of the zeolite powder with a binder, generally fluidified with water, often composed of a clay which is simultaneously sufficiently plastic to be able to form the agglomerate as balls, using a dish granulator, as pellets by moulding or as extrudates, using an extruder, and hardenable by calcination to give sufficient cohesion and hardness to the agglomerate. The clays used are kaolinites, attapulgites, bentonites, halloysite or mixtures of these clays. 
     It is also possible to use siliceous or aluminous binders. In particular, agglomeration with peptized aluminas gives very strong granules, this method of agglomeration being possible here because ferrierite is not degraded by the acidity of the binder. 
     After agglomeration, the granules are thermally activated. This means that they are subjected to a calcination carried out under air at a temperature of approximately 400° C., the role of which is both to harden the binder, to dehydrate it without hydrothermally degrading it and, in the case of ferrierites exchanged starting from an ammonium form, to remove a large part of the ammonium ions and to bring the zeolite to the H form. 
     It is also possible to start by agglomerating the sodium/potassium ferrierite, then to harden it by calcination and to carry out exchanges on the agglomerate. After drying, a second calcination makes it possible to bring the ferrierite/iron to the H form, if the ferrierite employed was taken in the ammonium form. 
     This catalyst is the improved catalytic means of a process for destroying N 2 O, contained in a gas mixture, according to the overall reaction: 
     
       
         2N 2 O→2N 2 +O 2   
       
     
     This process, which is also one of the subjects of the present invention, consists in passing the gases to be purified, in which the range of concentrations of N 2 O extends from 500 ppm to 50%, of H 2 O from 0.5 to 5% and of NO from 50 to 2000 ppm, through a catalyst bed placed in an axial or radial flow reactor maintained at a temperature of between 350 and 600° C. In the treatment of a gas with a high N 2 O content and with an initial temperature of less than 350° C., as is generally the case in processes for organic synthesis by nitric oxidation, the initiation of the reaction can be facilitated by preheating, during the start-up phase, the gas flow or the catalyst by an external means, the temperature of the catalytic bed subsequently being self-supporting because of the exothermicity of the reaction. In certain situations, in particular in the case of the treatment of gas with a high N 2 O concentration, heat exchangers or devices of quench type can advantageously be immersed in the catalytic bed in order to control the temperature of the latter, it optionally being possible to use part of the heat to preheat the gas to be treated. 
     Contrary to other zeolitic catalysts, the ferrierite/iron according to the invention retains a manifest activity with respect to N 2 O in the presence of water. This activity is very much enhanced in the presence of NO, which is a very favourable factor because this synergy becomes more significant for very low levels of NO, of the order of 50 ppm, and because the gases capable of such a treatment almost always contain such traces of NO. 
     The process according to the invention finds its application in particular in the treatment of tail gases from nitric acid plants, both before and after DeNOx treatment, which gases can have compositions within the following limits, 
     
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 N 2 O content: 
                 between 500 and 1500 ppmv, 
               
               
                   
                 NOx content: 
                 between 50 and 2000 ppmv, 
               
               
                   
                 H 2 O content: 
                 between 0.5 and 3%, 
               
               
                   
                 oxygen content: 
                 approximately 2%, 
               
               
                   
                   
               
             
          
         
       
     
     the remainder being essentially composed of nitrogen. 
     The process can also be applied to the treatment of gases resulting from plants for organic oxidation using nitric acid in organic chemistry, in particular in the manufacture of adipic acid, of glyoxal and of glyoxylic acid. These are gases with the approximate composition, before optional dilution with air, as follows: 
     
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 N 2 O content: 
                 between 20 and 50% 
               
               
                   
                 NOx content: 
                 between 50 and 5000 ppmv, 
               
               
                   
                 H 2 O content: 
                 between 0.5 and 5%, 
               
               
                   
                 oxygen content: 
                 between 1 and 4%, 
               
               
                   
                 CO 2  content: 
                 approximately 5%, 
               
               
                   
                   
               
             
          
         
       
     
     the remainder being essentially composed of nitrogen. 
    
    
     EXAMPLES 
     In the following examples, which are nonlimiting but intended to give a better understanding of the invention, the same catalytic test procedure has been followed, which procedure comprises the preparation of the sample and the catalytic test proper. 
     a) Preparation of the Catalyst 
     The exchanged zeolite powder is dried in an oven at 100° C. and then mixed with a silica sol, containing 40% by weight of SiO 2 , in an amount such that the silica SiO 2  content with respect to the SiO 2 +zeolite dry combination is 10%. The paste obtained is dried at 100° C. for 6 hours and then reduced to a powder in a mortar. The powder is pelletized to pellets with a diameter of 5 mm which are activated in an oven at 400° C. under air for 2 hours. After cooling, the pellets are crushed and sieved at 0.5-1 mm, this fraction constituting the catalyst. 
     b) Catalytic Test 
     It is carried out in a traversable stationary bed test unit (catatest) surrounded by heating shells regulated by PID, which brings the catalytic bed to a temperature approximately 25° C. below their set-point temperature. The reactor has a diameter of 15 mm. The catalyst volume employed is 10 cm 3 , i.e. a bed with a height of 57 mm. 
     The reaction gas is prepared from compressed air, from nitrogen and from standard gas, 2% N 2 O in N 2 , 2% NO in N 2 . The water vapour content is adjusted by an air humidifier, according to the laws of vapour pressure. 
     N 2 O analyses are carried out by infrared and NOx analyses by chemiluminescence. 
     The results are expressed as degrees of conversion of N 2 O to N 2 . 
     Example 1 
     Preparation of Various Ferrierite/iron Compositions 
     The ferrierite is supplied by Tosoh. Its Si/Al ratio is 8.85 and its Na and K contents, on a dry basis, after calcination at 1000° C. are 0.92% and 4.7% respectively. Taking into account its loss on ignition of 25% at 1000° C., its formula is 
     
       
         0.75K.025Na.AlO 2 .8.85SiO 2 .116H 2 O 
       
     
     The direct ferric exchange is carried out as follows. 100 g of zeolite powder are suspended, in a 1 litre round-bottomed glass flask, with 0.5 l of molar aqueous ferric chloride (FeCl 3 ) solution (i.e. 8.1 g of FeCl 3  per litre), namely with a volume of liquid/weight of dry solid ratio of 5. The system is kept stirred at 60° C. for 4 hours. The exchanged zeolite is recovered by filtration on a filter funnel, washed by percolation with 2 litres of demineralized water at ambient temperature and then dried on a tray in a ventilated oven overnight. 
     The iron, potassium and sodium contents with respect to the dry product (1000° C.) are 2.7%, 2.8% and 0.16% respectively. These quantities can be varied by adjusting the temperature, the duration of the exchanges and their number. 
     
       
         
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
               
               
                   
                   
                 Time 
                 Fe 3+   
                   
                   
                   
               
               
                 Ref. 
                 T° 
                 (h) 
                 exchanges 
                 Fe % 
                 Na % 
                 K % 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.1 
                 60 
                 4 
                 1 
                 2.7 
                 0.16 
                 2.8 
               
               
                 1.2 
                 60 
                 4 
                 1 
                 3.8 
                 0.1 
                 2.7 
               
               
                 1.3 
                 80 
                 4 
                 3 
                 7.7 
                 &lt;0.05 
                 0.16 
               
               
                   
               
             
          
         
       
     
     These products are subsequently named FERFe 3+ , Na, K form. 
     The ferric exchange on ferrierite exchanged beforehand with ammonium ions is carried out as follows. 
     A first exchange is carried out, on 100 g of the same zeolite as above, with 0.5 litre of an 800 g/l ammonium nitrate solution at a temperature of 80° C. for 4 hours. The exchanged product is recovered, washed and dried as above. Its sodium content is less than 0.1% and its potassium content less than 0.15%. 
     The ferric exchange is subsequently carried out as above but with two successive exchanges. The continuation of the operation is the same as in Example 1. A ferrierite/iron is obtained for which the iron, potassium and sodium contents are 2.2%, 0.15% and less than 0.1% respectively. These quantities can be varied by adjusting the temperature, the duration of the exchanges and their number. The following were thus obtained 
     
       
         
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
               
               
                   
                   
                 Time 
                 Number of 
                   
                   
                   
               
               
                 Ref. 
                 T° 
                 (h) 
                 Fe 3+  exchanges 
                 Fe % 
                 Na % 
                 K % 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 2.1 
                 60 
                 5 
                 1 
                 1.26 
                   
                   
               
               
                 2.2 
                 60 
                 4 
                 2 
                 2.2 
                 &lt;0.05 
                 0.15 
               
               
                 2.3 
                 80 
                 4 
                 1 
                 3.2 
                 &lt;0.05 
                 0.12 
               
               
                 2.4 
                 80 
                 4 
                 2 
                 7 
                 &lt;0.05 
                 &lt;0.05 
               
               
                   
               
             
          
         
       
     
     These products are subsequently named FERFe 3+ , NH 4  form. 
     Example 2 
     Power of Conversion of N 2 O of Ferrierites/iron 3+  in gases with a low N 2 O content 
     The test is carried out, according to the experimental procedure explained above, on nitrogen enriched with 
     
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 N 2 O 
                 1000 ppm 
               
               
                   
                 O 2   
                 2% 
               
               
                   
                   
               
             
          
         
       
     
     at an hourly volumetric rate or HVR of 10,000 h 31 1 . 
     In addition, the gas may or may not contain nitrogen oxide NO or water. The specific conditions of the test are as follows 
     
       
         
               
               
             
           
               
                   
               
             
             
               
                 1: 
                 375° C., NO = O, H 2 O = 0 
               
               
                 2: 
                 375° C., NO = 1000 ppm, H 2 O = 0 
               
               
                 3: 
                 375° C., NO = 1000 ppm, H 2 O = 3% 
               
               
                 4: 
                 400° C., NO = 1000 ppm, H 2 O = 3% 
               
               
                   
               
             
          
         
       
     
     The following % conversion results are obtained 
     
       
         
               
             
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                   
               
               
                 Conversion of N 2 O to N 2 , different conditions 
               
             
          
           
               
                   
                 Test conditions 
                   
               
             
          
           
               
                   
                 Ref. 
                 Fe % 
                 1 
                 2 
                 3 
                 4 
               
               
                   
                   
               
             
          
           
               
                   
                 Na, K 
                 1.1 
                 2.7 
                  10% 
                  50% 
                  30% 
                  42% 
               
               
                   
                 form 
                 1.2 
                 3.8 
                 14 
                 50 
                 20 
                 45 
               
               
                   
                   
                 1.3 
                 7.7 
                 35 
                 75 
                 34 
                 72 
               
               
                   
                 H form 
                 2.1 
                 1.26 
                 49 
                 88 
                 44 
                 72 
               
               
                   
                   
                 2.2 
                 2.2 
                 46 
                 97 
                 48 
                 77 
               
               
                   
                   
                 2.3 
                 3.2 
                 24 
                 79 
                 35 
                 66 
               
               
                   
                   
                 2.4 
                 7 
                 33 
                 84 
                 52 
                 85 
               
               
                   
                   
               
             
          
         
       
     
     An excellent activity of the ferrierite/iron, H form, is observed. 
     Example 3 
     Power of Conversion of N 2 O of Ferrierites/iron in Gases with a Low N 2 O Content 
     The preceding operations are repeated but, instead of ferric chloride, the exchange is carried out with a ferrous salt, ferrous sulphate FeSO 4 .7H 2 O. The procedures are carried out equally in Na, K form and in NH4 form. The products of the FERFe 2+ , Na, K form, series: 
     
       
         
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
               
               
                   
                   
                 Time 
                 Number of 
                   
                   
                   
               
               
                 Ref. 
                 T° 
                 (h) 
                 Fe 2+  exchanges 
                 Fe % 
                 Na % 
                 K % 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 3.1.1 
                 80 
                 4 
                 1 
                 1.8 
                 0.25 
                 3.2 
               
               
                 3.1.2 
                 80 
                 4 
                 3 
                 4.1 
                 0.2 
                 1.8 
               
               
                   
               
             
          
         
       
     
     and the products of the FERFe 2+ , NH 4  form, series: 
     
       
         
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
               
               
                   
                   
                 Time 
                 Number of 
                   
                   
                   
               
               
                 Ref. 
                 T° 
                 (h) 
                 Fe 2+  exchanges 
                 Fe % 
                 Na % 
                 K % 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 3.2.1 
                 80 
                 4 
                 1 
                 1.7 
                 &lt;0.05 
                 0.15 
               
               
                 3.2.2 
                 80 
                 4 
                 3 
                 5.46 
                 &lt;0.05 
                 0.15 
               
               
                   
               
             
          
         
       
     
     are thus obtained. 
     The results of the catalytic test are as follows, the conditions being those in the preceding example: 
     
       
         
               
             
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                   
               
               
                 Conversion of N 2 O to N 2 , different conditions 
               
             
          
           
               
                   
                 Test conditions 
                   
               
             
          
           
               
                   
                 Ref. 
                 Fe % 
                 1 
                 2 
                 3 
                 4 
               
               
                   
                   
               
             
          
           
               
                   
                 Na, K 
                 3.1.1 
                 1.8 
                  12% 
                  90% 
                  22% 
                  43% 
               
               
                   
                 form 
               
               
                   
                 H form 
                 3.2.1 
                 1.7 
                 31 
                 93 
                 48 
                 78 
               
               
                   
                   
                 3.2.2 
                 5.46 
                 29 
                 98 
                 50 
                 78 
               
               
                   
                   
               
             
          
         
       
     
     An excellent activity of the ferrierite/iron, form H, is observed. There is no substantial difference between the ferric and ferrous series. 
     Example III 
     Conversion of N 2 O—Comparison of Various Zeolites/iron 
     Various zeolites/iron, all exchanged in their NH 4  form starting from ferrous sulphate, are now compared with a ferrierite/iron 2+ , at iron assays in the region of 2%. The zeolite Y is a Y with an Si/Al ratio of 20 and assays, after exchange, 1.8% of iron and &lt;0.1% of sodium; the pentasil has an SI/Al of 13.5 and assays, after exchange, 1.6% of iron and &lt;0.05% of sodium; the beta has an Si/Al of 12.5 and assays, after exchange, 1.9% of iron and &lt;0.05% of sodium; the mordenite has an Si/Al of 5.5 and assays, after exchange, 1.9% of iron and &lt;0.05% of sodium. The ferrierite is the ferrierite with the reference 2.2 in Example 2. 
     
       
         
               
             
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
               
               
                 Conversion of N 2 O 
               
             
          
           
               
                   
                 Test conditions 
                   
               
             
          
           
               
                   
                 Zeolite 
                 Iron % 
                 1 
                 2 
                 3 
                 4 
               
               
                   
                   
               
             
          
           
               
                   
                 Y 
                 1.8 
                 28 
                 45 
                 22 
                 38 
               
               
                   
                 Pentasil 
                 1.6 
                 7 
                 62 
                 14 
                 30 
               
               
                   
                 Beta 
                 1.9 
                 47 
                 98 
                 21 
                 44 
               
               
                   
                 Mordenite 
                 2.4 
                 8 
                 91 
                 22 
                 42 
               
               
                   
                 Ferrierite 
                 2.2 
                 46 
                 97 
                 48 
                 77 
               
               
                   
                   
               
             
          
         
       
     
     It is found that only the ferrierite retains a significant activity in conversion of N 2 O in the presence of water vapour. 
     Example IV 
     Comparative Activities of a Mordenite/iron and of a Ferrierite/iron in Gases with a High N 2 O Content 
     The reduction in the N 2 O content obtained with the preceding mordenite/iron containing 2.4% of iron is compared with that of two ferrierites, one containing 1.46% of iron and the other containing 3.37% of iron. 
     The conditions of the test are 
     
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 N 2 O 
                 5% 
               
               
                   
                 O 2   
                 5% 
               
               
                   
                 HVR 
                 10,000 h −1   
               
               
                   
                 5: 
                 325° C., NO = 0 
               
               
                   
                 6: 
                 325° C., NO = 1000 ppm 
               
               
                   
                 7: 
                 375° C., NO = 0 
               
               
                   
                 8: 
                 375° C., NO = 1000 ppm 
               
               
                   
                 9: 
                 425° C., NO = 0 
               
               
                   
                 10: 
                 425° C., NO = 1000 ppm 
               
               
                   
                 11: 
                 475° C., NO = 0 
               
               
                   
                 12: 
                 475° C., NO = 1000 ppm 
               
               
                   
                   
               
             
          
         
       
     
     The degrees of decomposition below are recorded. 
     
       
         
               
             
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
               
               
                 Conversion of N 2 O to N 2   
               
             
          
           
               
                   
                 Test conditions 
               
             
          
           
               
                   
                 Fe % 
                 5 
                 6 
                 7 
                 8 
                 9 
                 10 
                 11 
                 12 
               
               
                   
                   
               
             
          
           
               
                 Mordenite/ 
                 2.4 
                 0.1 
                 0 
                 0.8 
                 14.3 
                 6.8 
                 21.6 
                 35.2 
                 65.8 
               
               
                 iron 
               
               
                 Ferrierite/ 
                 1.46 
                 1.6 
                 1.2 
                 5.3 
                 11.6 
                 12.3 
                 36.7 
                 42.1 
                  8.7 
               
               
                 iron 
               
               
                 Ferrierite/ 
                 3.37 
                 0.8 
                 3.2 
                 1.1 
                 13.2 
                 5 
                 93.4 
                 49.3 
                 99.9 
               
               
                 iron 
               
               
                   
               
             
          
         
       
     
     These results exhibit a higher level of conversion of N 2 O with the ferrierite. 
     Example V 
     Ageing 
     The result of a comparative hydrothermal stability test between a mordenite/iron with an Si/Al ratio of 5.5, H form, exchanged with iron to the level of 2.4% by weight, and a ferrierite/iron according to the invention, an H form, exchanged with iron to the level of 2.2% (reference 2.2 in Example 1), is reported here. 
     The ageing was carried out by exposure of the catalysts to an air/water vapour mixture in a dried bed at 650° C. for 3 hours. The air is saturated with water vapour at 90° C. 
     The two catalysts are tested as above with respect to conversion of N 2 O, the operating conditions being 
     
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 N 2 O 
                 1000 ppm 
               
               
                   
                 NO 
                 1000 ppm 
               
               
                   
                 O 2   
                 10% 
               
               
                   
                 Temperature: 
                 375° C. 
               
               
                   
                 HVR 
                 10,000 h −1   
               
               
                   
                 13: 
                 H 2 O = 0 
               
               
                   
                 14: 
                 H 2 O = 3% 
               
               
                   
                   
               
             
          
         
       
     
     The following results are obtained: 
     
       
         
               
             
               
               
               
             
               
               
               
             
               
               
               
               
               
             
           
               
                   
               
               
                 Conversion of N 2 O to N 2   
               
             
          
           
               
                   
                 Test conditions 
                   
               
             
          
           
               
                   
                 13 
                 14 
               
               
                   
                   
               
             
          
           
               
                   
                 Mordenite 
                 Before ageing 
                 91 
                 22 
               
               
                   
                 Mordenite 
                 After ageing 
                 32 
                 10 
               
               
                   
                 Ferrierite 
                 Before ageing 
                 88 
                 40 
               
               
                   
                 Ferrierite 
                 After ageing 
                 83 
                 39 
               
               
                   
                   
               
             
          
         
       
     
     which results confirm the remarkable stability of the ferrierite/iron to water vapour. 
     Example VI 
     Granules with an Aluminous Binder 
     In a first step, extrudates containing 20% of aluminous binder are formed as follows. An alumina of NG type, supplied by the company Condea, is used for the manufacture of the agglomerated catalyst. In a first step, it is peptized by continuously introducing, into a mixer, alumina at the rate of 15 kg/h and 5% by weight nitric acid with a flow rate of 0.16 l/min. 5 kg of the peptized alumina gel thus obtained are mixed with 10 kg of ferrierite powder, in the Na,K form, as supplied by Tosoh (see Example 1), in a conventional powder mixer. The resulting mixture is fed to a mixer/extruder at the same time as 3 litres of water. The extruder is a device of Redco type from the company Aoustin, with a diameter of 5 cm, equipped at the outlet with a die forming extrudates with a diameter of 3.8 mm which are cut into elements with a length of 5 to 10 mm. The extrudates are subsequently transferred, with a thickness of approximately 15 mm, to a muffle furnace, through which air passes, at 100° C. for 4 hours and then at 450° C. for 3 hours, in order to confer a satisfactory mechanical strength on them. 
     200 g of these ferrierite extrudates are now introduced into a stainless steel basket in order to steep them in 1 litre of an 800 g/l ammonium nitrate solution at a temperature of 80° C. for 3 hours, then to wash them by successive steepings (3) in 1 litre of demineralized water, and then to dry them at 100° C. 
     Their sodium and potassium content on a dry basis (1000° C.) is 0.1% (Na) and 0.15% (K). 
     Exchange with iron is then carried out according to the same principle with 1 litre of iron (Fe 2+ ) sulphate solution containing 280 g/l of FeSO 4 .7H 2 O at 80° C. for 3 hours, followed by washing by successive steepings in 1 litre of demineralized water and by drying. The iron content on a dry basis (1000° C.) is 1.6%. 
     The catalyst thus prepared is subjected to the catalytic test described above in a reactor with a diameter of 25 mm. The catalyst volume is 25 cm 3 , i.e. a height of approximately 5 cm. The catalytic test is applied under the conditions 1 to 4 of Example 2. 
     
       
         
               
             
               
               
               
             
               
               
               
               
               
               
             
           
               
                   
               
               
                 Conversion of N 2 O to N 2   
               
             
          
           
               
                   
                 Test conditions 
                   
               
             
          
           
               
                   
                 Catalyst 
                 1 
                 2 
                 3 
                 4 
               
               
                   
                   
               
               
                   
                 Aluminous granules 
                 30% 
                 89% 
                 43% 
                 72% 
               
               
                   
                   
               
             
          
         
       
     
     which are results highly comparable with those of Example 2.1.