Abstract:
An electrochromic display device comprising an electrolyte held between a pair of substrates, at least one of which being transparent, a plurality of electrodes coated with electro-chemical coloration material formed on at least one substrate, at least a part of the plurality of electrodes composing display picture elements, wherein the display is of uniform density and can be changed only by changing the display between the plurality of electrodes coated with the electro-chemical coloration material.

Description:
BACKGROUND OF THE INVENTION 
     The present invention relates to an electrochromic (referred to as an EC hereafter) display device in which a display image is changed between electrodes coated with an electrochemical coloration material. 
     A display method of a conventional EC display device will be described in conjunction with FIG. 1. 
     A transparent electrode 3 is formed on an upper transparent substrate 1. A tungsten trioxide (referred to as WO 3  hereafter) film 5 is formed on the transparent electrode 3. Electric charges are injected into the WO 3  film by applying a negative electric potential to the transparent electrode 3 and a positive electric potential to a counter electrode 9 via an electrolyte 7 and a white background plate 8, whereby the WO 3  film colors blue. The electrolyte 7 is a solution of lithium perchlorate (LiClO 4 ) and propylene carbonate, and the white background plate 8 comprises a multipolar ceramic plate. The counter electrode 9 is made of an inert material such as gold, platinum or sintered carbon. A counter substrate 2 defines a container for sealing the electrolyte 7 and the background plate 8 with a sealing agent 10. Reference numeral 11 denotes a mask plate of the display device. The following is the formula of reaction in case the WO 3  film is colored. ##STR1## 
     When a positive electric potential is applied to the transparent electrode and a negative electric potential is applied to the counter electrode, the electric charges inside the WO 3  film are extracted, and the WO 3  film is bleached as indicated by the above formula. 
     Thus the conventional EC display device displays images by applying a voltage between the transparent electrode on which the WO 3  film is formed and the counter electrode to color or bleach the WO 3  film. 
     This method, however, is disadvantageous in the following respects: 
     1. The display device is thickened by use of a particular insert material. 
     2. The cost is extremely high because the counter electrode is made of expensive materials such as gold, platinum and sintered carbon. 
     3. The panel structure is complicated and the reliability is low since the terminals of the counter electrode must be extracted to the outside of the panel structure. 
     Accordingly, the present invention aims to eliminate the above noted drawbacks, and therefore it is an object of the invention to facilitate the practical use of EC display devices. 
     An EC display device according to the present invention eliminates a counter electrode which, in the prior art, serves for coloring the EC material, and instead, applies a voltage between groups of bleached and colored display electrodes for displaying images. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a sectional view showing the structure of a conventional electrochromic display device, 
     FIG. 2 is a sectional view of an electrochromic display device showing an embodiment of a display device according to the present invention, 
     FIG. 3 is a plan view of a conventional display which constantly applies electric charges from a counter electrode, 
     FIG. 4 is a plan view of a display using the electric charge transfer method according to the present invention in which electric charges are exchanged between display electrodes by providing a dummy electrode, 
     FIG. 5 is a schematic illustration of a driving circuit for experiment, 
     FIG. 6 is a plot of experimental data using a display device according to the present invention, and 
     FIG. 7 is a graph showing a change in density when the display device according to the present invention is used in a timepiece. 
    
    
     DETAILED DESCRIPTION OF INVENTION 
     FIG. 1 shows a conventional electrochromic display device according to the present invention. FIG. 2 shows an embodiment of an electrochromic display device according to the present invention, in which the counter electrode 9 and an insulating film 4 which are required in the FIG. 1 construction are eliminated. FIG. 3 shows a plan view of a conventional 7-segments display pattern and FIG. 4 shows a plan view of a 7-segments display pattern acoording to the present invention. Reference numerals 5a-5g denote display segment WO 3  films and 6a-6c are dummy segment WO 3  films. 
     A conventional display method and the present display method will be illustrated in conjunction with the drawings. In a conventional display method, the EC display device is displayed by applying a voltage between a counter electrode and a transparent electrode coated with a WO 3  film (referred to as WO 3  electrode hereafter) as heretofore described. The change of the display state will be illustrated. For displaying a numeral 1, WO 3  electrodes 5b and 5c are connected to a negative electric potential and the counter electrode is connected to a positive electric potential to color the WO 3  film. When the numeral 1 changes to numeral 2, the electrode 5c is connected to the positive electric potential and the counter electrode is connected to the negative electric potential to bleach 5c. After this, the WO 3  film, once colored, holds its coloration state even if the voltage is off. This feature is what is called a memory characteristic. The coloration state of the electrode 5b is maintained without applying a voltage, taking advantage of the memory characteristic, whereby numeral 2 is displayed. Another changing method of numerals is to bleach all the colored WO 3  films and then freshly color the next numeral. 
     A display method according to the present invention will now be illustrated. Initially, the principle of coloration according to the present invention will be illustrated in conjunction with FIG. 5. In the prior art, the coloration and bleaching of EC display devices was carried out by a counter electrode. It has been found, however, that the WO 3  films are gradually colored by changing a positive electric potential and a negative electric potential between two WO 3  electrodes alternately at a certain cycle as shown schematically in FIG. 5. This phenomena may be occur because the WO 3  electrodes serve as a counter electrode when bleaching. Therefore, an insulation film is not formed in this structure to use the bleached electrodes effectively. This method of changing the display state between plural WO 3  electrodes alternately is called the &#34;electric charge transfer&#34; method since electric charges are transferred through the electrolyte directly between the WO 3  films. It has been found, through a number of basic experiments, that the density of the WO 3  films colored by the electric charge transfer method is controlled by factors such as the thickness of the WO 3  film and drive voltage. The following experiment is made on the basis of the data of the basic experiment. The WO 3  film thicknesses are 3 KÅ, 5 KÅ and 7 KÅ and the drive voltages are 1.5 V, 1.75 V and 2.0 V. The following conclusions are found by the resultant data shown in FIG. 6. 
     1. The density of the WO 3  film is higher as the voltage is higher. 
     2. The density of the WO 3  film is higher as the thickness of the WO 3  film is increased. 
     The coloration density in this experiment is defined as follows. The reflection factor of the white background plate is defined as 100%, while the relative reflection factor of the colored portion to that of the white background is defined as the coloration density. When the white background plate is measured by a color difference meter, the data of X:77, Y:80 and Z:95 is obtained. 
     Generally, a vivid display is realized if the coloration density is more than 40%. The coloration density in FIG. 6 is checked by the following method. 
     The number of charge transfer cycles to stabilize the density is around 100 cycles by the basic experiment. The density after 200 transfering cycles is plotted in the experimental data. One cycle consists of a positive electric potential applied for 1 second and a negative electric potential applied for 1 second. Two hundred cycles are applied to the segments 5a and 5d. 
     The structure of the EC display device according to the present invention will now be illustrated in detail. An upper transparent substrate 1 is of a glass, on which is formed a transparent electrode film. The transparent electrode film is an indium oxide (In 2  O 3 ) film or a tin oxide (SnO 2 ) film formed by the spraying method. The transparent electrode film is patterned at the desired forms by the photo technique and etching technique. WO 3  films in given patterns or forms are coated on patterned transparent electrodes 3 by the vaccum evaporation method. In their embodiment the WO 3  films are: display segment WO 3  films 5a, 5b, 5c, 5d, 5e, 5f and 5g; and dummy segment WO 3  films 6a, 6b and 6c. Numeral 7 denotes an electrolyte consisting of lithium perchlorate (LiC O 4 ) and propylene carbonate solution. The electrolyte 7 colors the WO 3  films since Li +  is injected into them together with electrons when a voltage is applied. A white background plate 8 is provided to show up the blue WO 3  films vividly. The white background plate is of multi-polar shape having a certain porosity to fill the electrolyte sufficiently and to pass through electric charges (electrons and Li + ) easily. The counter substrate 2 serves as a container to seal the white background plate and the electrolyte by the sealing agent 10. The counter substrate is made of glass or ceramic. The mask plate 11 is configured to mask and conceal the dummy electrodes, sealing agent portion and the like and the mask plate has an opening therethrough for exposing the display electrodes. An experiment on driving a watch display is further made with reference to the experimental data in FIG. 6, using the EC display device. 
     A method of changing the display state of the 7-segments according to the present invention will be illustrated in conjunction with FIG. 4. In FIG. 4 the dummy electrodes 6a, 6b and 6c are positioned to always balance the total area of the colored WO 3  electrodes and the total area of the bleached WO 3  electrodes. FIG. 4 shows that the same quantity of electric charges are always transferred between the WO 3  coated electrodes, i.e., the display changing method according to the present invention is the same as that of the basic experiment. The display changing method will now be illustrated. Each area of the 7-segments WO 3  electrodes 5a, 5b, 5c, 5d, 5e, 5f and 5g is 1 unit, the area of the dummy WO 3  electrode 6a is 1 unit, and that of the electrodes 6b and 6c is 2 units. As shown in FIG. 4, the dummy electrodes 6b and 6 c are disposed in a line in end-to-end relationship. 
     
                       TABLE 1______________________________________                   dummydisplay segment         segment(5)                     (6)a       b      c      d   e    f   g    a    b    c______________________________________0                           o        x1    x                  x   x    x             o    o2    o             x    o   o        o    x    x3                  o        x4    x                  x        o        o5    o      x           o                 x6                           o             o         x7           o           x   x    x   x    x    o    o8                       o   o    o   o         x    x9                           x             o______________________________________ 
    
     Table 1 shows the display changing method. The mark O indicates that the negative electric potential (colored state) is held, the mark X indicates that the positive electric potential (bleached state) is held, and the blank space indicates that the display state just before changing the display is held. The Table 1 is an example wherein the display of numerals 0 to 9 are changed in turn. 
     The specifications and structure of an EC display device used as a time display will be illustrated. The electrodes comprise indium oxide film, no insulating film between the electrodes is needed, the WO 3  film thickness is 5 KÅ, the time display content comprises 4 digits (an hour-minute display) with each digit being a 7 segments system, and the cell area is 10 mm×20 mm. The transfer time in this experiment is also 2 sec/cycle (the same as the basic experiment), the display of the time is changed in the same way as in timepieces, the coloration density was plotted each cycle, and the cycle is replaced by the actual hour-minute display to check the life in actual use. As a result of driving the time display in this way, the experimental data as shown in FIG. 7 is obtained. In this experiment no changes in the display density and appearance are found even by changing display of 4×10 6  cycles. If the 2 sec./cycle-display change is replaced by 1 min. (60 sec.)/cycle-display change, the display change is maintained for more than 7 years. 
     This invention has the above noted structure and achieves an EC display device with stable display density as shown by experimental data and long-term tests. 
     The following advantages are achieved by the present invention. 
     (1) Characters and numerals are displayed by simple driving circuits since the function of the counter electrode is not needed. 
     (2) The cell structure can be made thinner since the counter electrode is not needed. An extreme reduction in cost is realized by the reduction in the number of the manufacturing processes since expensive and special materials are not used. 
     (3) By this system a new, stable display density is achieved. 
     Thus, a remarkable improvement is achieved and a practical and excellent EC display device is realized.