Abstract:
The present invention relates to high transmission green dye for LCD, dye dispersion comprising the dye, coloring composite comprising the dye dispersion, color filter comprising the coloring composite, and synthetic method thereof.

Description:
RELATED APPLICATION 
       [0001]    This application claims the benefit of priority to Korean Patent Application No. 10 2012-0102943, filed on Sep. 17, 2012, which is hereby incorporated by reference for all purposes as if fully set forth herein. 
       BACKGROUND OF THE INVENTION 
       [0002]    1. Field of the Invention 
         [0003]    The present invention relates to high transmission green dye for LCD, dye dispersion comprising the dye, coloring composition comprising the dye dispersion, color filter comprising the coloring composition, and synthetic method thereof. 
         [0004]    2. Background of the Invention 
         [0005]    A color filter used in Liquid Crystal Display (LCD) is used for materialize color images in the Display, which can be prepared through a process consisting of coating pigments on a basic circuit board with various methods, and curing and patterning them. The color filter is one that each of 3 color pixel parts is formed on a transparent circuit board as like a glass. The color filter used in a display device or a solid state image sensor usually has a coloring pattern of the three primary colors comprising red®, green (G) and Blue (B) and play a role in coloring a light passing through or segregating it to the 3 primary colors. Dyes displaying red, green, and blue consist of fine particles, namely pigments, and these pigments display each of red, green, and blue color by mixing dyes representing similar colors rather than being used independently to obtain a color display property in a desired range. 
         [0006]    Recently, technology development of LDC toward larger screen and higher definition has been advanced and its usage has been expanded sharply from a display for laptop computer to a monitor for a desktop computer and television monitor. In these situations, the color filter used in LCD is required to have high color purity. Especially in high definition display making high definition image display possible, it becomes important to satisfy this requirement. A light passing through a color filter is to be colored with the color of each pixel and colors of the lights are synthesized to form a color image. Therefore, a color filter having very high purity pixel is required as certain 3 colors of RGB making it possible. 
         [0007]    Besides due to propagation of digital camera and camera equipped mobile phone, demand of solid state image sensors such as CCD image sensor has increased remarkably also. As the color filter is used as a key device of these displays or optical elements, demand on cost reduction as well as demand on high definition of the color filter increases. 
         [0008]    Dyes used in the color filter are required to have following properties: Having a desirable light absorption property in color reproduction; having no development of optical faults such as light scattering or color non-uniformity of solid state image sensor causing contrast lowering of LCD or optical density non-uniformity causing coarse sensation; having proper resisting properties such as thermal resistance, light resistance, and damp heat resistance; and being capable of preparation of thin film. 
         [0009]    Demands on LCD with high definition, namely improved contrast and color purity increase and it is required for improvement of contrast that the particle size of dyes (organic pigments) in photosensitive resin composition for formation of color filter is further smaller. In addition, it is important also to increase content of dyes (such as organic pigments) against solids of the photosensitive resin composition for improvement of color purity. 
         [0010]    Besides, in the recent color filter for solid state image sensors such as CCD, high definition is required further. Therefore, miniaturization of dye is desired to inhibit color non-uniformity by coarse particles of the dye. 
         [0011]    Currently, a metal halide phthalocyanine dye or a metal halide phthalocyanine pigment is used generally for forming green pixel. In concrete, dyes or pigments with metal halide phthalocyanine structure where at least 8 halogen atoms per phthalocyanine molecule are combined with benzene ring are used as a green dye constituting the green pixels of color filter. 
         [0012]    Although Pigment Green 36 has been used mainly among them, its transmission degree is relatively low, so development of dye for improving that has been progressed. As a result of the development, Pigment Green 58 comprising zinc polyhalide phthalocyanine was developed as a dye for overcoming the demerit of Pigment Green 38 and suggested to be used as a dye for color filter. 
         [0013]    The dye or the pigment is required to contain following properties: Having a desirable absorption property in color reproduction; and having good fastness property in its application environment including light resistance, thermal resistance, and resistance to oxidative gas such as ozone. Additionally, when the dye is a pigment, it is substantially insoluble in water or organic solvent and it is necessary to contain following properties: having good fastness resisting chemical; and giving no damage to desirable absorption properties in molecular dispersion even in being used as particles. The requirements may be controlled with strength and weakness of intermolecular interaction and it is difficult to make both of them coexist because they are in trade off relationship. 
         [0014]    Under these situations, a technology using a dye instead of a pigment has been suggested. When using a dye instead of a pigment, accomplishment of high resolution is expected by solving problems such as color non-uniformity and coarse sensation in the color filter for solid state image sensor and improvement of optical properties such as contrast or haze is expected in LCD or Organic Light-Emitting Display (OLED). 
         [0015]    However, coloring curable composition containing dyes has following problems also: 
         [0016]    (1) The dyes in molecular dispersion state have insufficient light resistance and thermal resistance generally compared with the pigments forming molecular aggregates; especially, when forming ITO (Indium tin oxide) film used widely as an electrode of LCD, there is a problem that optical properties are changed by high temperature process. 
         [0017]    (2) The dyes in molecular dispersion state have insufficient solvent resistance generally compared with the pigments forming molecular aggregates; 
         [0018]    (3) As the pigment tends to inhibit radical polymerization reaction, there are some difficulties in designing coloring curable composition in a system using the radical polymerization as a mean of curing; 
         [0019]    (4) Conventional dyes have lower solubility in alkali aqueous solution or organic solvent, so it is difficult to obtain a coloring curable composition having a desired spectrum; 
         [0020]    (5) The dyes are likely to interact with other ingredients in the coloring curable composition, so it is difficult to control solubility of exposure and non-exposure part (developing property); 
         [0021]    (6) When molar extinction coefficient of the dye (ε) is low, it is needed to add large amount of the dye. Thus, it is required to reduce the amount of other ingredients such as polymeric chemical (monomer), binder, or photo-initiator in the coloring curable composition relatively; curing property, heat resistance after curing, and developing property of the composition are lowered. 
         [0022]    Therefore, it is required to develop an improved dye used for preparing a color filter for LCD able to overcome the above mentioned disadvantages. 
       SUMMARY OF THE INVENTION 
       [0023]    An object of the present invention is to provide high transmission green dye for LCD, dye dispersion comprising the dye, coloring composition comprising the dye dispersion, color filter comprising the coloring composition, and synthetic method thereof. 
         [0024]    In the present invention, it was intended to develop high transmission green dye of color filter for developing hybrid color photo resist proper to low electric power LED BLU light source substituting for CCFL, a conventional LCD color filter backlight (BLU) light source. For this, it is necessary to develop a high transmission major green dye and a high durability yellow compensation dye able to absorb short wavelength in the range of 400˜500 nm and it is intended to materialize transmission spectrum for optimal green color filter by mixing the high transmission green dye and the yellow dye appropriately. 
         [0025]    An example of the present invention to accomplish the objective is a dye of Formula 1. 
         [0000]    
       
                 
         
             
             
         
       
     
         [0026]    Wherein, M is Cu or Zn and R1 or R2 is selected from a group consisting of halogen, unsubstituted or substituted alkyl ether, and unsubstituted or substituted aryl ether independently. Provided, the case that the both R1 and R2 are halogen is excluded. 
         [0027]    In the present invention, phthalocyanine currently used as a pigment type was used as a main dye of green color filter. The phthalocyanine is clear blue and green, which has good durability (heat resistance, and light resistance) and very high molar extinction coefficient, and is being used as a major blue and green colored pigment type color filter. 
         [0000]    
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
     
         [0028]    In this study, reduction of durability was minimized and solubility was improved by introducing ether link and bulk sized alkyl/aryl substituent to non-peripheral (α) position and peripheral (β) position of isoindole part of phthalocyanine pigment with good durability and clear color. 
         [0000]    
       
                 
         
             
             
         
       
     
         [0029]    When a substituent is introduced to non-peripheral position of isoindole region of phthalocyanine, the wavelength is shifted toward longer wavelenghth region more than the case that a substituent is introduced to the peripheral position of isoindole region of phthalocyanine and the solubility is improved also from increase of steric hindrance. 
         [0030]    In addition, the wavelength is changed according to the central metal, where from the introduction of metal, the wavelength moves to shorter region than non-metal phthalocyanine and introduction of substituent to the isoindole region induces movement of wavelength toward longer region. Therefore, the color from blue to green is expressed according to proper combination of central metal and substituent. 
         [0031]    In a preceding study, when 4 substituents were introduced into the peripheral position of isoindole, the color was expresses as green, but its absorption and transmission spectrum features was insufficient somewhat. Accordingly, in this study, it was attempted to move the wavelength further toward longer region than the conventional dye where 4 substituents were introduced by introducing 8 substituents to the peripheral position of isoindole region. Another example of the present invention is to introduce 8 identical bulk-sized substituents to the isoindole region. 
         [0032]    Another example of the present invention is to raise the solubility and attempt to make the wavelength longer through hybrid structure of pigment and dye through mixing of them by introducing halogen atom to one side of isoindole and bulk sized substituent to the other side of isoindole. 
         [0033]    As substitution at non-peripheral position brings more shift toward longer wavelength than the substitution at peripheral position, it was attempted to improve solubility and bring proper shift toward longer wavelength to green color through introduction of 8 substituents with similar structure for compatibility with the solvent, PGMEA (Propylene Glycol Monomethyl Ether Acetate), minimizing shift toward longer wavelength by minimizing electron donating strength (EDS). 
         [0034]    The unsubstituted or substituted alkyl ether may have more than 6 carbon atoms and the unsubstituted or substituted aryl ether may have more than 6 carbon atoms. 
         [0035]    The R1 and R2 may be one selected from a group consisting of halogen, 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    independently. Provided, the case that the both R1 and R2 are halogen is excluded. 
         [0036]    In another example of the present invention, a mimetic diagram of dye synthesis reaction is as follows. 
         [0000]    
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
     
         [0037]    Another example of the present invention to accomplish the objective is a dye of Formula 2. 
         [0000]    
       
                 
         
             
             
         
       
     
         [0038]    Wherein, M is Cu or Zn and R3 or R4 is selected from a group consisting of hydrogen, unsubstituted or substituted alkyl ether, and unsubstituted or substituted aryl ether, independently. Provided, the case that the both R3 and R4 are hydrogen is excluded. 
         [0039]    The unsubstituted or substituted alkyl ether may have more than 6 carbon atoms and the unsubstituted or substituted aryl ether may have more than 6 carbon atoms. 
         [0040]    The R3 or R4 may be one selected from a group consisting of hydrogen, 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    independently. Provided, the case that the both R3 and R4 are hydrogen is excluded. 
         [0041]    In another example of the present invention, a mimetic diagram of dye synthesis reaction is as follows. 
         [0000]    
       
                 
         
             
             
         
       
     
         [0042]    Another example of the present invention to accomplish the objective is a dye dispersion comprising the said dye. 
         [0043]    Another example of the present invention to accomplish the objective is a coloring composition comprising the said dye dispersion. 
         [0044]    Another example of the present invention to accomplish the objective is a color filter formed by using the said coloring composition. 
         [0045]    Another example of the present invention to accomplish the objective is a synthetic method of the said dye comprising: a step to synthesize a phthalonitrile-induced precursor; and a step to synthesize the dye of Formula 1 using the phthalonitrile-induced precursor. 
         [0000]    
       
                 
         
             
             
         
       
     
         [0046]    Wherein, M is Cu or Zn and R1 or R2 is selected from a group consisting of halogen, unsubstituted or substituted alkyl ether, and unsubstituted or substituted aryl ether independently. Provided, the case that the both R1 and R2 are halogen is excluded. 
         [0047]    Another example of the present invention to accomplish the objective is a synthetic method of the said dye comprising: a step to synthesize a phthalonitrile-induced precursor; and a step to synthesize the dye of Formula 2 using the phthalonitrile-induced precursor. 
         [0000]    
       
                 
         
             
             
         
       
     
         [0048]    Wherein, M is Cu or Zn and R3 or R4 is selected from a group consisting of hydrogen, unsubstituted or substituted alkyl ether, and unsubstituted or substituted aryl ether, independently. Provided, the case that the both R3 and R4 are hydrogen is excluded. 
       EFFECTS OF INVENTION 
       [0049]    The present invention can provide a green dye to cope with low electric power type LED BLU light source substitutable conventional CCFL BLU and a green dye with high transmission and high durability for substitution of major pigment. It is possible to an optimal green color filter by mixing with yellow compensation dye with high durability able to absorb the shorter wavelength range effectively. In addition, the dye synthesized in the present invention has high durability (high heat resistance and high thermal resistance) suitable to present LCD process as well as solubility proper to conventional pigment type solvent (PGMEA). In other words, the present invention provides an optimal synthetic method and mass synthesis technology as well as high transmission green dye for LCD. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0050]      FIG. 1  shows a diagram of the improved dye according to the present invention. 
           [0051]      FIG. 2A  shows UV-VIS absorption of the synthesized dyes. 
           [0052]      FIG. 2B  shows transmission spectrum of the synthesized dyes. 
           [0053]      FIGS. 3A-3H  are graphs showing thermal resistances of the synthesized dyes. 
           [0054]      FIG. 4  shows absorption and transmission spectrum of GD-1 and GD-3 by temperatures. 
           [0055]      FIG. 5A  is an absorption and transmission spectrum graph of GD-4˜6 after PB. 
           [0056]      FIG. 5B  is an absorption spectrum graph of GD-4 by temperatures. 
           [0057]      FIG. 5C  is an absorption spectrum graph of GD-5 by temperatures. 
           [0058]      FIG. 5D  is an absorption spectrum graph of GD-5-1 by temperatures. 
           [0059]      FIG. 5E  is an absorption spectrum graph of GD-6 by temperatures. 
           [0060]      FIG. 6A  is comparison of absorption spectrum between GD4 of the present invention and the conventional dye G58 and an absorption spectrum graph of GD-4 by temperatures. 
           [0061]      FIGS. 6B-6D  are transmission spectrum graphs of GD-4 by temperatures and number of PB. 
           [0062]      FIGS. 6E-6J  are graphs showing change of color coordinate values of GD-4 by temperatures and number of PB. 
           [0063]      FIG. 6K  and  FIG. 6L  are graphs showing change of color coordinate values of GD-4 by color mixing against the conventional G3. 
           [0064]      FIG. 6M  is a graph showing color mixing absorption of the dye GD-4. 
           [0065]      FIG. 6N  is a graph showing transmission spectrum of the dye GD-4. 
           [0066]      FIG. 6O  is a graph showing coloring of the dye GD-4. 
           [0067]      FIG. 7A  is a NMR ( 1 H) result confirming precursor synthesis of GD-1,2. 
           [0068]      FIG. 7B  is a NMR ( 1 H) result confirming precursor synthesis of GD-3.4. 
           [0069]      FIG. 7C  is a NMR ( 13 C) result confirming precursor synthesis of GD-3.4. 
           [0070]      FIG. 7D  is a NMR ( 1 H) result confirming precursor synthesis of GD-5.6. 
           [0071]      FIG. 7E  is a NMR ( 13 C) result confirming precursor synthesis of GD-5.6. 
           [0072]      FIG. 7F  is a NMR ( 1 H) result confirming precursor synthesis of GD-7.8. 
           [0073]      FIG. 7G  is a NMR ( 13 C) result confirming precursor synthesis of GD-7.8. 
           [0074]      FIG. 7H  is a NMR ( 1 H) result confirming precursor synthesis of GD-9.10. 
           [0075]      FIG. 71  is a NMR ( 13 C) result confirming precursor synthesis of GD-9.10. 
           [0076]      FIG. 8A  is a MALDI-TOF result confirming synthesis of GD-1. 
           [0077]      FIG. 8B  is a MALDI-TOF result confirming synthesis of GD-2. 
           [0078]      FIG. 8C  is a MALDI-TOF result confirming synthesis of GD-3. 
           [0079]      FIG. 8D  is a MALDI-TOF result confirming synthesis of GD-4. 
           [0080]      FIG. 8E  is a MALDI-TOF result confirming synthesis of GD-5. 
           [0081]      FIG. 8F  is a MALDI-TOF result confirming synthesis of GD-6. 
           [0082]      FIG. 8G  is a MALDI-TOF result confirming synthesis of GD-7. 
           [0083]      FIG. 8H  is a MALDI-TOF result confirming synthesis of GD-8. 
           [0084]      FIG. 8I  is a MALDI-TOF result confirming synthesis of GD-9. 
           [0085]      FIG. 9  is showing the condition under which the color filter application property assessment for GD-1 and GD-3 is performed. 
           [0086]      FIG. 10  is showing the condition under which the color filter application property assessment for GD-4, GD-5, GD-5-1, GD-6, GD-11, and GD-12 is performed. 
           [0087]      FIG. 11  is showing the condition under which the color filter application property assessment for GD-4 is performed. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0088]    Further scope of applicability of the present application will become more apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from the detailed description. 
         [0089]    1. Synthesis of Green Dye (GD) 
         [0090]    1-1. Synthesis of Green Dye Precursor 
         [0091]    (1) Precursor Synthesis of GD-1,2 
         [0092]    Dissolve 1.97 g (10 mmol) of 4,5-dichlorophthalonitrile, 7.31 g (25 mmol) of 4-methoxy-2,5-bis(2-methylpentan-2-yl)phenol, 9.67 g (70 mmol) of K 2 CO 3  in 70 ml of anhydrous DMF under nitrogen gas and circulate it at 80° C. for 8 hr. After completion of the reaction, drop the reacted solution slowly to ice water. Filter the white powder precipitated in the ice water and then dry it in the oven. The dried product was purified with column chromatography. 
         [0093]    (2) Precursor Synthesis of GD-3.4 
         [0094]    The precursor synthesis of GD-3,4 was performed using same method of the precursor synthesis of GD-1,2 other than dissolving 1.97 g (10 mmol) of 4,5-dichlorophthalonitrile, 2.92 g (10 mmol) of 4-methoxy-2,5-bis(2-methylpentan-2-yl)phenol, and 6.91 g (50 mmol) of K 2 CO 3  in 70 ml of anhydrous DMF. 
         [0095]    (3) Precursor Synthesis of GD-5.6 
         [0096]    The precursor synthesis of GD-5.6 was performed using same method of the precursor synthesis of GD-1,2 other than dissolving 1.64 g (10 mmol) of 4,5-difluorophthalonitrile, 2.92 g (10 mmol) of 4-methoxy-2,5-bis(2-methylpentan-2-yl)phenol, and 6.91 g (50 mmol) of K 2 CO 3  in 70 ml of anhydrous DMF. 
         [0097]    (4) Precursor Synthesis of GD-7.8 
         [0098]    Dissolve 3.20 g (20 mmol) of 2.3-dicyanohydroquinone, 11.82 g (60 mmol) of 2-bromo-1.1-diethoxyethanel, 11.82 g (60 mmol) of K 2 CO 3  in 70 ml of anhydrous DMF under nitrogen gas and circulate it at 100° C. for 8 hr. After completion of the reaction, drop the reacted solution slowly to ice water. Filter the white powder precipitated in the ice water and then dry it in the oven. The dried product was purified with column chromatography. 
         [0099]    (5) Precursor Synthesis of GD-9.10 
         [0100]    The precursor synthesis of GD-9.10 was performed using same method of the precursor synthesis of GD-7.8 other than dissolving 3.20 g (20 mmol) of 2.3-dicyanohydroquinone, 11.70 g (60 mmol) of 2-(2-bromoethyl)-1.3-dioxane and 13.82 g (100 mmol) of K 2 CO 3  in 70 ml of anhydrous DMF under nitrogen gas. 
         [0101]    (6) Precursor Synthesis of GD-11.12 
         [0102]    The precursor synthesis of GD-11.12 was performed using same method of the precursor synthesis of GD-1,2 other than dissolving 1.73 g (10 mmol) of 4-nitrophthalonitrile, 2.20 g (10 mmol) of 1-acetyl-4-(4-hydoxyphenyl)piperazine, and 6.91 g (50 mmol) of K 2 CO 3  in 70 ml of anhydrous DMF. 
         [0103]    The mimetic diagram of precursor synthesis of the GD-1˜12 is as follows. 
         [0000]    
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
       
                 
         
             
             
         
       
     
         [0104]    1-2. Synthesis of Green Dye 
         [0105]    (1) Synthesis of GD-1 
         [0106]    Dissolve 1.42 g (2 mmol) of the GD-1 precursor synthesized in the example 1-1, 1.50 ml (10 mmol) of DBU (1,8-diazabicycle[5.4.0]-7-undecene), and 0.27 g (2 mmol) of CuCl 2  in 50 ml of 1-pentanol under nitrogen gas and circulate at 150° C. for 12 hr. After completion of the reaction, the solvent was removed under reduced pressure. Dissolve the remaining product in MC (methylene chloride) and extract it with water several times. After removing MC under reduced pressure, the product was filtered through methanol recycling. Dry the green powder remained on the filter paper in the oven and purity it with column chromatography. 
         [0107]    (2) Synthesis of GD-2 
         [0108]    Dissolve 1.42 g (2 mmol) of the GD-2 precursor synthesized in the example 1-1, 1.50 ml (10 mmol) of DBU (1,8-diazabicycle[5.4.0]-7-undecene), and 0.27 g (2 mmol) of ZnCl 2  in 50 ml of 1-pentanol under nitrogen gas and circulate at 150° C. for 12 hr. After completion of the reaction, the solvent was removed under reduced pressure. Dissolve the remaining product in MC (methylene chloride) and extract it with water several times. After removing MC under reduced pressure, the product was filtered through methanol recycling. Dry the green powder remained on the filter paper in the oven and purity it with column chromatography. 
         [0109]    (3) Synthesis of GD-3 
         [0110]    GD-3 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-3 precursor synthesized in the example 1-1 as precursor. 
         [0111]    (4) Synthesis of GD-4 
         [0112]    GD-4 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-4 precursor synthesized in the example 1-1 as precursor. 
         [0113]    (5) Synthesis of GD-5 
         [0114]    GD-5 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-5 precursor synthesized in the example 1-1 as precursor. 
         [0115]    (6) Synthesis of GD-6 
         [0116]    GD-6 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-6 precursor synthesized in the example 1-1 as precursor. 
         [0117]    (7) Synthesis of GD-7 
         [0118]    GD-7 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-7 precursor synthesized in the example 1-1 as precursor. 
         [0119]    (8) Synthesis of GD-8 
         [0120]    GD-8 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-8 precursor synthesized in the example 1-1 as precursor. 
         [0121]    (9) Synthesis of GD-9 
         [0122]    GD-9 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-9 precursor synthesized in the example 1-1 as precursor. 
         [0123]    (10) Synthesis of GD-10 
         [0124]    GD-10 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-10 precursor synthesized in the example 1-1 as precursor. 
         [0125]    (11) Synthesis of GD-11 
         [0126]    GD-11 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-11 precursor synthesized in the example 1-1 as precursor. 
         [0127]    (12) Synthesis of GD-12 
         [0128]    GD-12 was synthesized and purified with same method and same molar equivalent to the synthesis of GD-1 excluding using GD-12 precursor synthesized in the example 1-2 as precursor. 
         [0129]    2. Spectroscopic Analysis of Dye 
         [0130]    For GD-1˜6, absorption and transmission spectrum in PGEA were analyzed ( FIG. 2A  and 2B). It was shown that GD-5,6 where the substituent was introduced to non-peripheral position had wavelength in absorption range adjacent to Near-IR and had about 120,000 of molar extinct coefficient and GD-1˜4 where the substituent was introduced to peripheral position showed at least 200,000 of excellent molar extinct coefficient and proper wavelength as green color. These differences are considered that GD-5,6 where the substituent was introduced to non-peripheral position were made its wavelength further longer. 
         [0131]    It was found that their transmission degree was excellent in the range of 500 nm˜540 nm and GD-1,4 showed the most similar spectrum to Green 58 (G58). 
         [0132]    3. Thermal Resistance Analysis of Dye 
         [0133]    Through Thermo Gravimetric Analyzer (TGA), Thermogravimetric Analyzer 2050 (TA instruments), thermal resistance of the synthesized dye was measured (FIG.  3 A-3H). For the thermal resistance test, change of mass reduction rate (w %) was measured by passing through isothermal zone at 220° C. for 30 min, raising the temperature to 30° C.˜400° C. in 10° C./min. It was found that the synthesized dye having Cu as its central metal had better thermal resistance in general than the dye having Zn. This result seems to be caused by change of phthalocyanine crystal form depending on the metal. It was found that GD-1,5 showed almost no change of mass even at over 300° C. as well as in the isothermal zone and was most stable. For GD-3,4, it was shown than they were stable also to heat and showed only 1˜2% of mass reduction in the isothermal zone. GD-6 showed less than 5% of mass reduction in the isothermal zone. It is considered that this mass reduction of the dyes may be affected by small amount of impurities. 
         [0134]    4. Solubility Analysis of Dye 
         [0135]    For organic solvents and process solvents, solubility of the synthesized dyes was assessed. The results were assessed qualitatively and shown in below Table 1. As shown in the Table 1, it was found that overall solubility to the organic solvent (CH 2 Cl 2 ) was better than that to the process solvent (PGMEA). It was found that GD-3˜6 with dye-pigment hybrid structure showed excellent solubility to PGMEA, from structural diversity from existence of isomers and the results of proper steric hindrance by substituents. As in general, a dye has a physical property that its solubility is better than that of a pigment and in case of the present invention, when granting steric hindrance to green pigment to make it have a certain solubility, the pigment becomes a dye, the above mentioned term of dye-pigment hybrid structure means that the solubility was improved by granting steric hindrance from introducing bulk-sized substituents to common pigment. These results show that it is possible to accomplish excellent solubility through control on the introduction of substituents able to induce proper steric hindrance to prevent aggregation between dyes and crystallization of the dye. 
         [0000]    
       
         
               
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
               
                   
                 GD-1 
                 GD-2 
                 GD-3 
                 GD-4 
                 GD-5 
                 GD-6 
                 GD-7 
                 GD-8 
                 GD-9 
                 GD-10 
                 GD-11 
                 GD-12 
               
               
                   
               
             
             
               
                 CH 2 Cl 2   
                 +++ 
                 +++ 
                 +++ 
                 +++ 
                 +++ 
                 +++ 
                 + 
                 + 
                 + 
                 + 
                 ++ 
                 ++ 
               
               
                 PGMEA 
                 ++ 
                 ++ 
                 +++ 
                 +++ 
                 +++ 
                 +++ 
                 + 
                 + 
                 + 
                 + 
                 + 
                 + 
               
               
                   
               
               
                 +++: &gt;5.0 * 10 4  mg litre −1   
               
               
                 ++: &gt;5.0 * 10 3  mg litre −1   
               
               
                 +: &gt;5.0 * 10 2  mg litre −1   
               
             
          
         
       
     
         [0136]    5. Color Filter Application Property Assessment 
         [0137]    Property assessment of GD-1 and GD-3 
         [0138]    Prior to color mixing assessment, spectrum changes were observed after preparing a simple paste containing 1 wt % of dye, coating and then PB(post baking) it by temperatures. Using the observed spectrum, color simulation was performed. The assessment was performed under the condition described in  FIG. 9 . 
         [0139]    The results were shown in  FIG. 4 . Because GD-3 had better solubility to PGMEA than GD-1, only GD-3 was fixed as 1% against the content of G58 and the spectrum was compared. It was suggested that Q-band decreased a little after PB at 180/200/230° C., but its thermal resistance was excellent. 
         [0140]    Property Assessment of GD-4, GD-5, GD-5-1, GD-6, GD-11, and GD-12 
         [0141]    Using the same method in 5.(1), color filter application properties of GD-4, GD-5, GD-5-1, GD-6, GD-11, and GD-12 were analyzed. Wherein, GD-5-1 is an isomer of GD-5. The assessment was performed under the condition described in  FIG. 10 . 
         [0142]    The results were shown in  FIG. 5 .  FIG. 5A  is absorption and transmission spectrum of GD-4˜6 after PB. It was suggested that GD-4 showed the most similar spectrum to G58.  FIGS. 5B-5E  are absorption spectrum graphs of GD-4˜6 by temperatures after PB. The absorption peaks of GD-4 and GD-6 decrease around 600 nm after PB and increase around 630 nm. The accurate reason that the above mentioned results are developed has not been identified, but it is considered that it may be caused by complex reasons such as peak change from re-crystallization of dye after PB, degradation of substituents from heat energy, or effect of phthalocyanine isomer. 
         [0143]    (3) Secondary Color Filter Application Property Assessment—GD-4 
         [0144]    For GD-4 showing the best physical property in assessment of 5.(1) and 5.(2), independent PR and color mixing assessment were performed. The assessment was performed under the condition described in  FIG. 11 . 
         [0145]    The results were shown in  FIG. 6 .  FIG. 6A  shows comparison of absorption spectrum with G58 and absorption spectrum by temperature of GD-4. In case of GD-4 single color assessment, it was found that compared with G58, the absorption was formed somewhat high (blue circle), the absorption spectrum after PB decreased somewhat around 600 nm, and the absorption increased again around 630 nm. As mentioned in the above, it is considered that these results occurred from diverse and complex causes by peak change from recrystalization of dye after PB, degradation of substituent from heat energy, or phthalocyanine isomers. 
         [0146]      FIGS. 6B-6D  show transmission spectrums of GD-4 by temperature and number of PB. It was found that the solubility of GD-4 to PGMEA was excellent, as more than 5%. Its spectroscopic change showed satisfactory level in treatment at 180/200° C. 
         [0147]    As shown in below Table 2, it was found that in spectroscopic changes of GD-4 by number of PB, the spectroscopic change at each temperature after the first PB showed satisfactory physical property as values of ΔEab≦3, but the spectroscopic change after the second and third PB increased gradually. Especially, the larges spectroscopic change at high temperature, 230° C., means that thermal resistance of the dye is somewhat insufficient at high temperature, 230° C. In addition, it was shown that increase values by number of PB were not saturated and increased continuously. It seems that it is because of absorbance reduction of the dye by degradation of the dye. 
         [0000]    
       
         
               
               
             
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Spectroscopic change 
               
               
                   
                 by # of PB (ΔEab) 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 180° C. 
                 1.46 → 2.14 → 3.14 
               
               
                   
                 200° C. 
                 2.19 → 3.13 → 4.36 
               
               
                   
                 230° C. 
                 2.99 → 5.03 → 7.78 
               
               
                   
                   
               
             
          
         
       
     
         [0148]      FIGS. 6E-6J  show changes of color coordinate of GD-4 depending on PB repetition and changes of luminance value in state that the y coordinate is fixed. It was found that at 180° C., there was a tendency that the values came to be saturated to some extent but at 200° C./230° C., the degree of color change increased gradually with washing-out depending on the number of repetition. Considering the above color coordinate change graph, it is identified that GD-4 is more suitable to low temperature process at 180° C. than high temperature process at over 200° C. and shows a trend that in the high temperature process over 200° C., the color change from degradation of the dye becomes more severe. 
         [0149]      FIGS. 6K and 6L  and below Table 3 show change of color coordinate values according to color mixing of GD-4 dye against G3 by making K-binder (dye dispersion improvement type) PR, which is considered to be suitable to the dye form. 
         [0000]    
       
         
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 3 
               
               
                   
               
               
                   
                 G58 
                   
                   
                   
                   
                   
                   
               
               
                            Gx 0.283/ 
                 replace- 
                 G58/Y138/GD4 
                   
                   
                   
                 modified 
                            GY 
               
               
                 Gy 0.556 
                 ment 
                 (%) 
                 Binder 
                 Gx 
                 GY 
                 GY 
                 vs. G3 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 G3_180PB 
                  0% 
                 72/28/0  
                 K 
                 0.2834 
                 64.12 
                 64.12 
                 — 
               
               
                 GGD4-7_180PB1 
                 100%  
                  0/47/53 
                 K 
                 0.285 
                 61.4 
                 61.0 
                 ▾3.12 
               
               
                 GGD4-8_180PB2 
                 15% 
                 58/32/10 
                 K 
                 0.2847 
                 64.2 
                 63.86 
                 ▾0.26 
               
               
                   
               
               
                             indicates data missing or illegible when filed 
               
             
          
         
       
     
         [0150]    It was found that when substituting 15% of GD-4 dye, there was almost no luminance reduction compared with the pigment type. 
         [0151]      FIGS. 6M-6O  are color mixing absorption, transmission spectrum, and coloring graphs of GD-4, which show correlation of absorption and transmission spectrum and color filter coating thickness depending on luminance in mixing color compared with G3. 
         [0152]    As the present features may be embodied in several forms without departing from the characteristics thereof, it should also be understood that the above-described embodiments are not limited by any of the details of the foregoing description, unless otherwise specified, but rather should be construed broadly within its scope as defined in the appended claims, and therefore all changes and modifications that fall within the metes and bounds of the claims, or equivalents of such metes and bounds are therefore intended to be embraced by the appended claims.