Abstract:
A light emitting apparatus is provided that includes a light emitting device and luminous material thereon. Light output of the light emitting apparatus is measured. Some of the luminous material is selectively removed from the light emitting device based on the output of the light emitting apparatus that was measured, so that luminous material that remains on the light emitting device after the selective removing continues to be optically excited by light that is generated by the light emitting device. In measuring, a frequency spectrum of the light emitting apparatus may be measured, and the light emitting apparatus may emit white light after the selectively removing.

Description:
RELATED APPLICATIONS 
       [0001]    The present application is a continuation of U.S. patent application Ser. No. 10/267,093, filed Oct. 4, 2002, entitled Methods and Systems for Fabricating Broad Spectrum Light Emitting Devices, and is related to and claims priority from U.S. Provisional Application Ser. No. 60/335,649, filed Oct. 31, 2001, entitled “Broad Spectrum Light Emitting Devices and Methods and Systems For Fabricating the Same,” the disclosures of both of which are incorporated herein by reference as if set forth fully herein. 
     
    
     FIELD OF THE INVENTION 
       [0002]    The present invention relates to semiconductor devices, and more particularly to semiconductor devices for producing light. 
       BACKGROUND OF THE INVENTION 
       [0003]    Broad spectrum light emitting semiconductor devices have conventionally been fabricated by exciting a luminous substance with a relatively narrow spectrum light source. Conventionally, in such devices a light emitting diode (LED) or laser emits light in a narrow spectrum which is shifted and/or spread to provide a broader spectrum of light. Typically, it is desirable to provide white light from a narrow spectrum light source, such as an LED or laser. Such white light sources are described, for example, in U.S. Pat. No. 6,245,259, the disclosure of which is incorporated herein by reference as if set forth fully herein. 
         [0004]    One difficulty with the fabrication of white light devices is that, typically, the spectrum of light emitted by the devices is dependent on the spectrum of light emitted by the laser or LED and the amount of luminous substance on the device. On a single wafer or die there may be variations in the wavelength of light emitted by the particular devices on the wafer or die. Such deviations may, for example, be the result of defects in the devices or variations as a result of manufacturing tolerances. These deviations in the output wavelength of the underlying devices may result in variations in the white light emitted by the resulting devices after application and excitation of the luminous substance. 
       SUMMARY OF THE INVENTION 
       [0005]    Embodiments of the present invention provide broad spectrum light emitting devices and methods and systems for fabricating such devices. Such devices may include a light emitting element, such as a diode or laser, which emits light in a predefined range of frequencies, and an amount of luminous material on the light emitting diode. The amount of luminous material may be based on a measured output of the light emitting element and/or the light emitting device. 
         [0006]    In particular embodiments of the present invention, light emitting elements are coated with a first layer of luminous material and activated and the output frequency of the devices measured. A map of the variations of output frequency of the devices is generated based on the measurements and additional luminous material is selectively applied to the light emitting elements based on the map of variations so as to provide a plurality of broadband light emitting devices have a desired uniformity, such as a substantially uniform light output. Additionally, the measurement and application operations may be repeated multiple times until a desired uniformity of light output is achieved. 
         [0007]    Alternatively, the frequency of the output of the individual devices could be measured before the initial application of the luminous material and the initial application could be adjusted based on the measurement. The light emitting elements could be individually activated, activated in groups or all activated for measurement. 
         [0008]    In further embodiments of the present invention, the light emitting elements are gallium nitride based devices. Preferably, the light emitting elements are fabricated on a silicon carbide substrate such that the light is emitted through the silicon carbide substrate. The silicon carbide substrate may be patterned to enhance light emission of the light emitting elements. Furthermore, in some embodiments, the light emitting elements have two contacts accessible from a single side of the device. In such a case, the devices may be activated in parallel by placing the devices on a foil or other conductor and contacting the devices through the foil. 
         [0009]    The luminous material is preferably a phosphor, such as YAG:Ce. The luminous material may be applied by one or more of dusting a charged surface of the light emitting elements, suspending the phosphor in a fluid and applying the fluid to the devices, air brushing the phosphor on the devices and/or applying the phosphor with an ink or bubble jet. The same application technique may be used for the initial and subsequent application or differing techniques may be utilized. 
         [0010]    In particular embodiments of the present invention, a broad spectrum light emitting device is fabricated by measuring light output of the light emitting device and selectively applying luminous material to the light emitting device based on the measured light output of the light emitting device. The selective application of luminous material may be provided by selectively applying an amount of luminous material to the light emitting device, by selectively applying different compositions of luminous material to the light emitting device and/or by selectively applying differing doping levels of luminous material to the light emitting device based on the measured light output of the light emitting device. 
         [0011]    In further embodiments of the present invention, light output of the light emitting device is measured after applying a coating of luminous material to the light emitting device. The measurement of light output and the selective application of luminous material may also be repeated until the measured light output of the light emitting device meets a predefined criteria. 
         [0012]    Furthermore, the selective application of luminous material may be preceded by singulating the light emitting device from a wafer having a plurality of light emitting devices. If such is the case, the singulated light emitting devices may be grouped based on measured light output of respective ones of the singulated light emitting devices and different amounts of luminous material, differently doped luminous material and/or different composition luminous material applied to different groups of the singulated light emitting devices. 
         [0013]    In particular embodiments of the present invention, the selective application of luminous material is provided by selectively applying luminous material utilizing at least one of an inkjet application process, an air brush application process, a fluid application process, electrostatic deposition, electrophoretic deposition, screen printing, dipping, roll coating and/or vacuum deposition. 
         [0014]    In certain embodiments of the present invention, the light emitting device is a light emitting device on a wafer having a plurality of light emitting devices. 
         [0015]    In still further embodiments of the present invention, broad spectrum light emitting devices are fabricated by measuring light output of respective ones of a plurality of light emitting devices and selectively applying luminous material to the respective ones of the plurality of light emitting devices based on the measured light output of the respective ones of the light emitting devices. The light output of respective ones of the plurality of light emitting devices may be measured by activating respective ones of the plurality of light emitting devices and measuring light output of the respective ones of the plurality of light emitting devices when the respective ones of the light emitting devices are activated. The light emitting devices may be activated individually, in groups, sequentially and/or in parallel. 
         [0016]    In additional embodiment of the present invention, a map of the light output of the respective ones of the light emitting devices is generated and luminous material is selectively applied to respective ones of the plurality of light emitting devices based on the measured light output of the respective ones of the light emitting devices utilizing the generated map. Furthermore, the measurement of light output of the respective ones of the plurality of light emitting devices and the selective application of luminous material may be repeated until a predefined light output criteria is reached. The predefined light output criteria may be a substantially uniform light output of the plurality of light emitting devices. The predefined light output criteria could also be a threshold percentage of the plurality of light emitting devices having a predefined light output. The light output of respective ones of the plurality of light emitting devices may be measured after applying a coating of luminous material to the plurality of light emitting devices. The selective application of luminous material may include applying an amount of luminous material, applying different compositions of luminous material and/or applying differing doping levels of luminous material to the respective ones of the light emitting devices based on the measured light output of the respective ones of the light emitting devices. The luminous material may be selectively applied utilizing an inkjet application process, an air brush application process, a fluid application process, electrostatic deposition, electrophoretic deposition, screen printing, dipping, roll coating and/or vacuum deposition. 
         [0017]    In additional embodiments of the present invention, the respective ones of the plurality of light emitting devices are singulated light emitting devices. In such embodiments, the selective application of luminous material may be provided by sorting the singulating light emitting devices based on the measured light output of the light emitting devices so as to group singulated light emitting devices having common measured light output characteristics and selectively applying luminous material to the singulated light emitting devices so as to provide different luminous material characteristics to different groups of singulated light emitting devices. 
         [0018]    In further embodiments, the plurality of light emitting devices are a plurality of light emitting devices on a wafer. 
         [0019]    In other embodiments of the present invention, a broad spectrum light emitting device includes a light emitting device having measurable optical characteristics and a coating of luminous material on the light emitting device. The coating of luminous material has at least one characteristic selected based on a measurement of the optical characteristics of the light emitting device to provide a predefined output characteristic of the light emitting device. 
         [0020]    The coating of luminous material may include a first coating of luminous material applied independent of the measured optical characteristics and a second coating of luminous material applied based on the measured optical characteristics. Furthermore, the first coating and the second coating may be of the same composition luminous material. In such a case, the thickness of the second coating may be selected based on the measured optical characteristics. The first coating and the second coating could also be of different composition luminous material and the composition of the second coating may be selected based on the measured optical characteristics. Furthermore, the doping of the second coating may be selected based on the measured optical characteristics. The measured optical characteristics may also be optical characteristics of the light emitting device with the first coating of luminous material applied. 
         [0021]    In still further embodiments of the present invention, the composition of the luminous material, the amount of luminous material and/or the doping of the luminous material are selected based on the measured optical characteristics. 
         [0022]    In additional embodiments of the present invention, a broad spectrum light emitting device includes a plurality of light emitting devices on at least a portion of a wafer and coatings of luminous material on respective ones of the plurality of light emitting devices, the coatings of luminous material on the respective ones of the plurality of light emitting devices having different characteristics. The different characteristics may be at least one of different amounts of luminous material, different dopings of a luminous material and/or different compositions of luminous material. 
         [0023]    Furthermore, the coatings of luminous material may include a first coating of luminous material on each of the respective ones of the plurality of light emitting devices and a second coating of luminous material applied based on a measured optical characteristic of respective ones of the plurality of light emitting devices. The first coating and the second coating may be of the same composition luminous material and the thickness of the second coating may be selected based on the measured optical characteristics. The first coating and the second coating could also be of different composition luminous material and the composition of the second coating may be selected based on the measured optical characteristics. Furthermore, the doping of the second coating may be selected based on the measured optical characteristics. Furthermore, the measured optical characteristics may be optical characteristics of respective ones of the light emitting devices with the first coating of luminous material applied. 
         [0024]    In other embodiments of the present invention, the composition of the coating of luminous material differs between the respective ones of the plurality of light emitting devices based on measured optical characteristics of the respective ones of the plurality of light emitting devices. Furthermore, the thickness of the coating of luminous material may differ between the respective ones of the plurality of light emitting devices based on measured optical characteristics of the respective ones of the plurality of light emitting devices. Also, the doping of the coating of luminous material may differ between the respective ones of the plurality of light emitting devices based on measured optical characteristics of the respective ones of the plurality of light emitting devices. 
         [0025]    In still further embodiments of the present invention, a system for fabricating broad spectrum light emitting devices includes a lighting element activation circuit configured to activate light emitting devices, an output measurement circuit configured to measure the light output by the activated light emitting devices, a luminous material application device configured to selectively applying luminous material to light emitting devices and a controller operably associated with the output measurement circuit and the luminous material application device and configured to control the luminous material application device to selectively apply luminous material to light emitting devices based on the measured light output of the activated light emitting devices. In certain embodiments, the luminous material application device is at least one of an inkjet application system, an air brush application system, a fluid application system, an electrostatic deposition system, an electrophoretic deposition system, a screen printing system, a dipping system, a roll coating system and/or vacuum deposition system. 
         [0026]    Furthermore, the controller may also be configured to control the luminous material application device to apply a coating of luminous material prior to measurement of the output of the activated light emitting devices. The luminous material application device may also be configured to selectively apply at least one of different amounts of luminous material, different dopings of luminous material and/or different compositions of luminous material. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0027]      FIG. 1  is a block diagram of a system for applying luminous materials suitable for use in carrying out operations according to embodiments of the present invention; 
           [0028]      FIG. 2  is a flowchart illustrating operations according to embodiments of the present invention; 
           [0029]      FIGS. 3A and 3B  are illustrations of wafers having selectively applied luminous materials according to embodiments of the present invention; and 
           [0030]      FIG. 4  is a flowchart illustrating operations according to further embodiments of the present invention. 
       
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0031]    The present invention now will be described more fully hereinafter with reference to the accompanying drawings, in which embodiments of the invention are shown. This invention, however, should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. In the drawings, the thickness of layers and regions are exaggerated for clarity. Like numbers refer to like elements throughout. 
         [0032]      FIG. 1  illustrates a system that may be utilized to fabricate broad spectrum light emitting devices according to embodiments of the present invention. As illustrated in  FIG. 1 , a plurality of light emitting elements  10  are provided. Preferably, the light emitting elements comprise LEDs or lasers and are provided on a wafer and/or die such that the light emitting elements may be activated either individually or collectively. The LEDs and/or lasers may have contacts on opposite sides of the device or may have two contacts on a single side of the device. 
         [0033]    For example, the light emitting elements may be gallium nitride based LEDs or lasers fabricated on a silicon carbide substrate such as those devices manufactured and sold by Cree, Inc. of Durham, N.C. For example, the present invention may be suitable for use with LEDs and/or lasers as described in U.S. Pat. Nos. 6,201,262, 6,187,606, 6,120,600, 5,912,477, 5,739,554, 5,631,190, 5,604,135, 5,523,589, 5,416,342, 5,393,993, 5,338,944, 5,210,051, 5,027,168, 5,027,168, 4,966,862 and/or 4,918,497, the disclosures of which are incorporated herein by reference as if set forth fully herein. Other suitable LEDs and/or lasers are described in U.S. Provisional Patent Application Ser. No. 60,294,378, entitled “LIGHT EMITTING DIDODE STRUCTURE WITH MULTI-QUANTUM WELL AND SUPERLATTICE STRUCTURE”, U.S. Provisional Patent Application Ser. No. 60/294,445, entitled “MULTI-QUANTUM LIGHT EMITTING DIODE STRUCTURE” and U.S. Provisional Patent Application Ser. No. 60,294,308, entitled “LIGHT EMITTING DIDODE STRUCTURE WITH SUPERLATTICE STRUCTURE”, each filed May 30, 2001, U.S. patent application Ser. No. 10/140,796, entitled “GROUP III NITRIDE BASED LIGHT EMITTING DIODE STRUCTURES WITH A QUANTUM WELL AND SUPERLATTICE, GROUP III NITRIDE BASED QUANTUM WELL STRUCTURES AND GROUP III NITRIDE BASED SUPERLATTICE STRUCTURES”, filed May 7, 2002, as well as United States Provisional patent application Ser. No. 10/057,82, entitled “LIGHT EMITTING DIODES INCLUDING SUBSTRATE MODIFICATIONS FOR LIGHT EXTRACTION AND MANUFACTURING METHODS THEREFOR” filed Jul. 23, 2001 and U.S. patent application Ser. No. 10/057,82, filed Jan. 25, 2002 entitled “LIGHT EMITTING DIODES INCLUDING SUBSTRATE MODIFICATIONS FOR LIGHT EXTRACTION AND MANUFACTURING METHODS THEREFOR.” the disclosures of which are incorporated herein as if set forth fully. Furthermore, phosphor coated LEDs, such as those described in U.S. Provisional application Ser. No. ______ (Attorney Docket No. 5308-245PR) entitled “PHOSPHOR-COATED LIGHT EMITTING DIODES INCLUDING TAPERED SIDEWALLS, AND FABRICATION METHODS THEREFOR,” filed Sep. 19, 2002, the disclosure of which is incorporated by reference herein as if set forth full, may also be suitable for use in embodiments of the present invention. 
         [0034]    The LEDs and/or lasers may be configured to operate in a “flip-chip” configuration such that light emission occurs through the substrate. In such embodiments, the substrate may be patterned so as to enhance light output of the devices as is described, for example, in U.S. Provisional Patent Application Ser. No. 60/307,235 filed Jul. 23, 2001 entitled “LIGHT EMITTING DIODES INCLUDING SUBSTRATE MODIFICATIONS FOR LIGHT EXTRACTION AND MANUFACTURING METHODS THEREFOR” or as described in U.S. patent application Ser. No. 10/057,821, filed Jan. 25, 2002, entitled “LIGHT EMITTING DIODES INCLUDING SUBSTRATE MODIFICATIONS FOR LIGHT EXTRACTION AND MANUFACTURING METHODS THEREFOR,” the disclosures of which are incorporated herein by reference as if set forth fully herein. As is further illustrated in  FIG. 1 , a light emitting element activation circuit  12  is also provided. The light emitting element activation circuit  12  activates the light emitting elements  10  so that the light emitting elements  10  emit light. Such activation may be performed individually in a sequential fashion or simultaneously activating some or all of the light emitting elements  10 . Similarly, subsets of the plurality of light emitting elements  10  could be activated. The particular technique for activating the light emitting elements  10  may depend on the configuration of the electrodes for the light emitting elements  10 , the nature of the output measurement circuit  14  which measures the output of the light emitting elements  10  and/or the manner in which the luminous material is applied to the light emitting elements  10 . For example, in embodiments where the light emitting elements have two contacts accessible from a single side of the device, the devices may be activated in parallel by placing the devices on a foil or other conductor and contacting the devices through the foil. 
         [0035]    The output measurement circuit  14  measures the light output of one or more of the light emitting elements  10  and provides this information to a controller  18 . The controller  18  utilizes the light output information to control the luminous material application device  16  that selectively applies luminous material to the light emitting elements  10  based on the measured light output of the light emitting elements  10 . The output measurement circuit  14  may be a spectrum analyzer or other such device for analyzing the frequency and/or power of light output of the light emitting elements  10 . Such devices are known to those of skill in the art and, therefore, need not be described further herein. 
         [0036]    The luminous material application device  16  provides means for selectively applying a luminous material, including phosphors such as YAG:Ce or the like. Such means  16  for selectively applying a luminous material may be provided by, for example, an inkjet application system, an air brush application system, a fluid application system, a dust application system utilizing charged particles which are attracted to light emitting elements having an opposite charge (electrostatic deposition), electrophoretic deposition, screen printing, dipping, roll coating and/or vacuum deposition and/or other suitable techniques known to those of skill in the art. The selective application of luminous material may be provided before or after singulation of the devices. Differing amounts of luminous material may be applied to differing devices before or after singulation utilizing application techniques that provide for the selective application of luminous materials to individual devices or groups of devices. For example, if selective application is provided before singulation, an inkjet or other such selective application system may provide differing amounts of luminous material to individual or groups of devices while the devices remain on a wafer. After singulation, individual devices could have specific amounts of luminous material applied by, for example, an inkjet process, electrostatic deposition or the like. For example, differing charges could be applied to singulated or non-singulated devices in an electrostatic process such that differing amounts of luminous material would be attracted to different devices based on the charge of the device. Alternatively, if selective application is provided after singulation, the singulated devices (dies) may be grouped based on common measured output characteristics and a common amount of luminous material applied to each of the devices in the group. Furthermore, application of the luminous material may occur before or after a device or devices are mounted to a submount. 
         [0037]    Finally, the controller  18  may be any suitable controller capable of coordinating the operations as described herein for selectively applying luminous material to light emitting elements. For example, the controller  18  may be a programmable microcontroller, a personal computer or other data processing system. 
         [0038]      FIG. 2  illustrates operations according to certain embodiments of the present invention. The operations of  FIG. 2  will be described with reference to  FIGS. 3A and 3B .  FIG. 3A  is an illustration of a wafer  300  having several regions  310  containing a plurality of light emitting elements  320  prior to processing according to embodiments of the present invention. As seen in  FIG. 2 , optionally, an initial coating of the luminous material is applied to the light emitting elements  320  (block  40 ). This initial coating may be applied by the techniques described above, for example, by flowing a fluid containing the luminous material onto the wafer  300  to cover the regions  310 , by inkjet application of the luminous material, by air brush application of the material and/or by dusting the wafer  300  when the surface of the wafer is charged or other such techniques for application of a luminous material to a light emitting element as will be understood by those of skill in the art. Such an application may, for example, be provided by the luminous material application device  16  under control of the controller  18 . 
         [0039]    As is further seen in  FIG. 2 , the light emitting elements  320  are activated (block  42 ) and the output of the light emitting elements  320  is measured (block  44 ). Such activation, for example, may be provided by the light emitting element activation circuit  12  contacting electrodes of the light emitting elements, either in parallel, in groups, and/or individually, such that a forward electrical bias may be applied to the light emitting elements  320  when the light emitting element activation circuit  12  is instructed to do so by the controller  18 . Such activation of the light emitting elements  320  may be performed simultaneously, sequentially by individual elements and/or sequentially by groups of elements. For example, the entire wafer  300  could be activated and the output of the light emitting elements  320  measured, each region  310  could be individually activated and its output measured and/or each element  320  could be individually activated and its output measured. 
         [0040]    Furthermore, the output of the light emitting elements  320  may be measured at differing resolutions. For example, the output of each individual light emitting element could be measured or the output of groups of light emitting elements  320  could be measured. In certain embodiments of the present invention, the resolution of the light output measurement as well as the resolution to which luminous material may be applied correspond to the size of an individual light emitting element  320 . However, in other embodiments of the present invention, the resolution of the light output measurement may be at least the resolution to which luminous material may be applied to the light emitting elements  320  if such is coarser than an individual light emitting element  320 . 
         [0041]    As is further seen in  FIG. 2 , optionally, a map of the output of the light emitting elements  320  may be developed (block  46 ) to indicate which of the light emitting elements may need additional application(s) of luminous material or the thickness of an initial application of luminous material. The map relates the location of a light emitting element with its output such that a subsequent application of luminous material may be based on the measured output. Such a map may only need to be generated if the measurement of the output of light emitting elements is carried out for multiple light emitting elements prior to the selective application of luminous material in block  48 . 
         [0042]    In any event, luminous material is selectively applied to the light emitting elements  320  based on the measured output of the light emitting elements  320  such that different ones of the light emitting elements in the same wafer and/or die may receive differing amounts of luminous material (block  48 ). For example, as illustrated in  FIG. 3B , the output of the light emitting elements  320  may be measured as described above and it is determined that a first subset of light emitting elements  325  (indicated by the right to left diagonal cross-hatch in  FIG. 3B ) have an output which requires more luminous material be applied to these light emitting elements  325  than the remaining ones of the light emitting elements  320  and a second subset of light emitting elements  330  (indicated by the left to right diagonal cross-hatch in  FIG. 3B ) have an output which requires less luminous material be applied to these elements  330  than the remaining ones of the light emitting elements  320 . The second subset of light emitting elements  330  may then have a first amount of luminous material applied to them, the remaining ones of the light emitting elements  320  may have a second amount of luminous material, greater than the first amount, applied to them and the first subset of light emitting elements  325  may have a third amount of luminous material applied to them, which is greater than the first and the second amounts. 
         [0043]    The application of luminous material may be provided by successive passes including a first pass that applies the first amount to all the light emitting elements, a second pass that applies an additional amount to the remaining light emitting elements  320  and the first subset of light emitting elements  325  and a third pass that applies an additional amount of luminous material to only the first subset of light emitting elements  325 . Alternatively, a single pass that applies differing amounts of luminous material to the differing subsets of light emitting elements may be carried out. Furthermore, if an initial application of luminous material is provided, then an additional pass or passes applying luminous material may be provided such that the relative amount of luminous material applied to the various light emitting elements provides the second subset of light emitting elements  330  with the least luminous material, the first subset of light emitting elements  325  with the most luminous material and the remaining ones of the light emitting elements  320  with an amount between the amounts of the first subset  325  and the second subset  330 . As described above, the application of luminous material may be carried out by one or more of the above described techniques, including inkjet, air brush, or other such techniques. 
         [0044]    As is further illustrated in  FIG. 2 , after application of the luminous material is carried out, the output of the light emitting elements  320  could again be measured and it determined if the output of the light emitting elements  320  has a desired uniformity, such as being substantially uniform (block  50 ). Such light output may be substantially uniform if it is within acceptable manufacturing tolerances and provides an acceptable yield for the devices. For example, if a 75% yield is considered acceptable for a wafer, then the output may be considered substantially uniform when 75% of the light emitting elements are within the acceptable manufacturing tolerances for light output. In any event, if such substantial uniformity is not achieved (block  50 ), the operations at blocks  42 - 50  may be repeated until such uniformity is achieved (block  50 ). 
         [0045]      FIG. 4  illustrates operations according to further embodiments of the present invention. As seen in  FIG. 4 , optionally, an initial coating of the luminous material is applied to light emitting elements on a wafer (block  440 ). This initial coating may be applied by the techniques described above, for example, by flowing a fluid containing the luminous material onto the wafer, by inkjet application of the luminous material, by air brush application of the material, by dusting the wafer when the surface of the wafer is charged (electrostatic application) or other such techniques for application of a luminous material to a light emitting element as will be understood by those of skill in the art. Such an application may, for example, be provided by the luminous material application device  16  under control of the controller  18 . 
         [0046]    As is further seen in  FIG. 4 , the light emitting elements are singulated from the wafer to provide individual or groups of individual light emitting devices (block  442 ). Such singulation techniques may include sawing, breaking, etching and/or other such techniques known to those of skill in the art. The light emitting devices or groups of devices are activated (block  444 ) and the output of the light emitting devices is measured (block  446 ). Such activation, for example, may be provided by the light emitting element activation circuit  12  contacting electrodes of the light emitting elements, either in parallel, in groups, or individually, such that a forward electrical bias may be applied to the light emitting devices when the light emitting element activation circuit  12  is instructed to do so by the controller  18 . Such activation of the light emitting elements  320  may be performed simultaneously, sequentially by individual elements or sequentially by groups of elements. Furthermore, in certain embodiments of the present invention, the activation and measurement of light output may be performed prior to singulation. Furthermore, as discussed above, the output of the light emitting devices may be measured at differing resolutions. 
         [0047]    Luminous material is selectively applied to the light emitting devices based on the measured output of the light emitting devices such that different ones of the light emitting elements in the same wafer and/or die may receive differing amounts of luminous material (block  448 ). The application of luminous material may be provided by successive passes or a single pass that applies differing amounts of luminous material to the differing light emitting devices may be carried out. 
         [0048]    As is further illustrated in  FIG. 4 , after application of the luminous material is carried out, the output of the light emitting devices could again be measured and it determined if the output of the light emitting devices or a device has an acceptable output, such as being within a predefined range for the device, for example, the acceptable manufacturing tolerances for light output (block  450 ). In any event, if acceptable light output is not achieved (block  450 ), the operations at blocks  444 - 450  may be repeated until such output is achieved (block  450 ). 
         [0049]    With regard to the particular amount of luminous material to be applied to a particular light emitting element, such amounts may depend on the light emitting element and, the luminous material being utilized. Furthermore, the amount of material to be applied in a particular application may vary depending on the measured output of the light emitting element and the luminous material being applied. Techniques for determining the amount of luminous material to be applied based on a particular output of a light emitting element are known to those of skill in the art and, therefore, need not be described further herein. However, according to particular embodiments of the present invention, such a specific determination need not be made as a small incremental amount of material could be added in successive passes to light emitting elements that do not provide the desired output until a desired uniformity is achieved in the light emitting elements. Thus, for example, an initial increment of luminous material could be applied to all, or substantially all, of the light emitting elements and then the light output may be measured. Subsequent increments of luminous material would then only be applied to ones of the light emitting elements which do not meet a predefined light output criteria. The selective incremental application of luminous material could then be continued until either a predefined number of applications had been reached and/or a predefined yield threshold had been achieved. 
         [0050]    As is described above, embodiments of the present invention may provide a broad spectrum light emitting device through selective application of a luminous material, such as a phosphor. In particular embodiments of the present invention, a white light emission device is provided by selective application of an amount of a phosphor based on the output characteristics of the individual device. Furthermore, while the present invention has been described with reference to the selective application of an amount of phosphor, in other embodiments of the present invention, the type of phosphor or the doping of the phosphor could be altered based on the measured characteristics of a light emitting device. Thus, for example, a first application of a first phosphor could be followed by a selective application of a second phosphor so as to provide the desired broad spectrum device. Similarly, the particular doping or phosphor applied to a device could be adjusted based on the measured output of the device. Accordingly, embodiments of the present invention should not be construed as limited to varying the amount of a light emitting material but may also be utilized to vary the light emitting material and/or to apply multiple types of light emitting material so as to provide light emitting devices with a desired output spectrum. 
         [0051]    Embodiments of the present invention have been described with reference to individual light emitting devices. However, embodiments of the present invention may also be applicable to groups of light emitting elements into a single device, such as described in U.S. patent application Ser. No. 10/058,369 entitled “CLUSTER PACKAGING OF LIGHT EMITTING DIODES,” filed Jan. 28, 2002, the disclosure of which is incorporated herein as if set forth fully. Thus, as used herein, the term individual light emitting device is used to refer to devices having a single or multiple light emitting elements. 
         [0052]    Additionally, embodiments of the present invention have been described with reference to the selective application of luminous material. However, embodiments of the present invention could also selectively remove luminous material based on a measured light output of a light emitting device. For example, a coating of luminous material could be applied having a thickness corresponding to the maximum thickness required by a light emitting device in a group of devices and then luminous material removed from individual ones of the group based on measured output of the individual light emitting devices. Such a removal may, for example, be provided by laser etching or other such selective removal techniques known to those of skill in the art. Thus, certain embodiments of the present invention may provide for tailoring the characteristics of the luminous material, for example, by selective application or removal, based on a measured light output of an individual light emitting device. 
         [0053]    In the drawings, certain operations/acts and or blocks which have been indicated as optional are shown in dashed lines. The presence or lack of such a dashed line shall not, however, be construed as requiring any of the elements of the figures to carry, out particular embodiments of the present invention. Furthermore, while a particular breakdown or division of functions has been illustrated in  FIGS. 1 and 2 , as will be appreciated by those of skill in the art in light of the present disclosure, other divisions of functions may be provided while still benefiting from the teachings of the present invention. Thus, for example, blocks in the block diagram of  FIG. 1  may be combined, or additional blocks added, while still falling under the teachings of the present invention. Similarly, additional blocks may be added, blocks combined or operations may be performed in a different sequence than that illustrated in the flowchart illustration of  FIG. 2 . For example, blocks for illustrating when the light emitting elements  320  are deactivated are not illustrated in  FIG. 2  but could be added in various locations such that the light emitting elements  320  were activated during output measurement and deactivated when output is not measured. Thus, the present invention should not be construed as limited to the particular illustrations provided herewith but is intended to cover any such methods, systems or devices utilizing the selective application of luminous materials as described herein. 
         [0054]    In the drawings and specification, there have been disclosed typical preferred embodiments of the invention and, although specific terms are employed, they are used in a generic and descriptive sense only and not for purposes of limitation.