Abstract:
A method for forming and the structure of a vertical channel of a field effect transistor, a field effect transistor and CMOS circuitry are described incorporating a drain, body and source region on a sidewall of a vertical single crystal semiconductor structure wherein a hetero-junction is formed between the source and body of the transistor, wherein the source region and channel are independently lattice strained with respect the body region and wherein the drain region contains a carbon doped region to prevent the diffusion of dopants (i.e., B and P) into the body. The invention reduces the problem of short channel effects such as drain induced barrier lowering and the leakage current from the source to drain regions via the hetero-junction and while independently permitting lattice strain in the channel region for increased mobility via choice of the semiconductor materials. The problem of scalability of the gate length below 100 nm is overcome by the heterojunction between the source and body regions.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS  
       [0001]    This application is further cross referenced to U.S. patent application Ser. No. ______ (Attorney docket YOR920030140US1) by Q. Ouyang and Jack O. Chu, the inventors herein, filed herewith, entitled “Ultra Scalable High Speed Heterojunction Vertical N-channel MISFETs and Methods Thereof” which is directed to vertical N-channel MISFETs which is incorporated herein by reference and assigned to the assignee herein.  
         [0002]    This application is further cross referenced to U.S. patent application Ser. No. ______ (Attorney docket YOR920030141US1) by Q. Ouyang and Jack O. Chu, the inventors herein, filed herewith, entitled “High Speed Lateral Heterojunction MISFETs Realized by 2-dimensional Bandgap Engineering and Methods Thereof” which is directed to lateral Heterojunction MISFETs which is incorporated herein by reference and assigned to the assignee herein. 
     
    
     
       FIELD OF THE INVENTION  
         [0003]    This invention relates to semiconductor transistors and, more particularly, to a metal insulator semiconductor field effect transistor (MISFET) consisting of a conducting channel, which has no hetero-barrier in the current flow direction and a heterojunction between the source/drain and body (bulk) of the transistor.  
         BACKGROUND OF THE INVENTION  
         [0004]    Silicon MOSFET scaling has become a major challenge in the semiconductor industry. Traditional techniques start to fail in reducing certain undesirable physical effects as device dimensions shrink down to the nanometer regime. For example, anti-punchthrough (APT) or halo implantation is used to reduce the short-channel effects (SCE). However, the abrupt doping profiles are difficult to achieve due to temperature enhanced diffusion, and these highly doped channels or pocket implant regions increase junction capacitance and band-to-band tunneling. It has been shown by S. Thompson, et al., in “MOS scaling: transistor challenges for the 21st century,” Intel Technology Journal, Q3, 1998, that channel engineering can only decrease the circuit gate delay by ˜10% for a given technology, and it cannot provide channel length scaling for generation after generation that gate oxide and source/drain (S/D) junction depth scaling has provided.  
           [0005]    With bandgap engineering, an important degree of freedom can be provided in the device design. The growth of high-quality tensile strained Si/SiGe and compressively strained SiGe/Si heterostructures by molecular beam epitaxy (MBE), various types of chemical vapor deposition (CVD), and/or ion implantation allows incorporation of bandgap engineering concepts into a mature silicon technology.  
           [0006]    Bandgap engineering has been utilized to realize various types of heterojunction field effect transistors (HFETs). The most widely studied is the modulation doped field effect transistors (MODFET), in which a quantum well is used to confine the carriers in a lightly doped semiconductor (See K. Ismail, “Si/SiGe High-Speed Field-Effect Transistors”,  IEDM, Technology Digest,  p. 509-512, 1995). Higher carrier mobility can be achieved due to reduced impurity scattering, reduced surface roughness scattering in the buried channel, and strained-induced mobility enhancement, if any, depending on the hetero material system. Derived from the same concept, various types of heterostructure CMOS devices have also been proposed and studied (See M. A. Armstong, et al., “Design of Si/SiGe Heterojunction Complementary Metal-Oxide Semiconductor Transistors”,  IEDM Technology Digest,  p. 761-764, 1995; S. Imai et al., “Si—SiGe Semiconductor Device and Method of Fabricating the Same”, U.S. Pat. No. 5,847,419; and M. Kubo, et al., “Method of Forming HCMOS Devices with a Silicon-Germanium-Carbon compound Semiconductor Layer”, U.S. Pat. No. 6,190,975, Feb. 20, 2001.) The advantage of these devices is the high carrier mobility and hence high drive current and high speed. However, two prominent problems still remain in these planar devices: device scaling and control of short-channel effects.  
           [0007]    In planar FET devices, the channel length is limited by lithography. This problem can be solved if the devices are fabricated in a vertical fashion, in which the channel length is only determined by epitaxial techniques. And the diffusion of boron and phosphorus in the source/drain can be reduced by introducing thin SiGeC layers in the source/drain to achieve ultra scalable vertical transistors, as shown by Y. Ming, et al., in “25-nm p-Channel vertical MOSFET&#39;s with SiGeC source-drains”,  IEEE, Electron Device Letters,  vol. 20, no. 6, 1999, and by H. Rücker et al., in “Dopant diffusion in C-doped Si and SiGe: physical model and experimental verification,”  IEDM, Technical Digest,  p. 345-8, 1999.  
           [0008]    As for short-channel effects, other than ultra-steep retrograded channel profiles and ultra-shallow source/drain junctions, silicon-on-insulator (SOI) has been used to control short-channel effects. However, SOI does not remove short-channel effects completely, and an inherent problem with SOI is the floating body effect. Another way to reduce the short-channel effect is to have a built-in energy barrier at the source/body junction, and the height of the barrier does not depend on the applied bias. The band offset provided by a heterojunction is very suitable in this case. A heterojunction MOSFET (HJMOSFET) has been proposed and studied by S. Hareland, et al., in “New structural approach for reducing punchthrough current in deep submicrometer MOSFETs and extending MOSFET scaling,”  IEEE Electronics Letters,  vol. 29, no. 21, pp. 1894-1896, October 1993, and X. D. Chen, et al., in “Vertical P-MOSFETS with heterojunction between source/drain and channel,”  Device Research Conference,  Denver, June 2000.  
           [0009]    A p-channel/n-channel, complementary vertical MISFET device and a specific application of such devices in dynamic random access memory (DRAM) are described in U.S. Pat. Nos. 5,920,088, 6,207,977, 5,963,800, and 5,914,504. A heterojunction is utilized at the source/channel junction in the vertical devices. Even though very short channels may be achieved and short-channel effects may be reduced, there is still a big drawback with such device structures. At the off state (i.e., zero bias at the gate and high bias at the drain), the hetero-barrier is useful in reducing the drain-induced barrier lowering (DIBL), bulk punchthrough and therefore, off-state leakage current. However, at the on state (i.e., high bias at the gate and drain), the built-in hetero-barrier becomes harmful to the drive current. This is because the hetero-barrier at the source/channel junction severely blocks the thermal emission of the carriers from the source into the channel. The only way for carrier injection is the quantum mechanical tunneling across the barrier, which becomes the bottleneck of the transport in the channel. The so-called ballistic transport after crossing the barrier in the channel mentioned in these references will not occur due to strong surface roughness scattering. Therefore, the drive current in such devices is significantly reduced. Additionally, a part of the source (close to the channel) of such a device is undoped; therefore, the drive current will be further reduced by high series resistance in the source. A detailed study has been performed by Q. Ouyang, et al., in “Two-Dimensional Bandgap Engineering in Novel pMOSFETs,”  SISPAD,  Seattle September 2000, and by X. D. Chen, et al., in “Vertical P-MOSFETS with heterojunction between source/drain and channel”,  Device Research Conference,  Denver, June 2000.  
           [0010]    Recently, a lateral high mobility, buried, p-channel heterojunction transistor (HMHJT) has been described by Q. Ouyang, et al., in U.S. Pat. No. 6,319,799B1. A detailed simulation study has been performed by Q. Ouyang, et al., in “A Novel Si/SiGe Heterojunction pMOSFET with Reduced Short-Channel Effects and Enhanced Drive Current,”  IEEE Transactions on Electron Devices,  47 (10), 2000. In addition, the device has been realized using a vertical structure fabricated by Q. Ouyang, et al., in “Fabrication of a Novel Vertical pMOSFET with Enhanced Drive Current and Reduced Short-Channel Effects and Floating Body Effects”,  VLSI Symposium,  Kyoto, June 2001. In this case, compressively strained SiGe on Si is used to realize a high performance pMOSFET. However, the channel length scaling of such a device is still limited by boron diffusion from the source/drain into the channel. Furthermore, the transconductance for a buried channel may be reduced compared to a surface channel due to the reduced gate capacitance, despite the higher mobility in the buried channel. The present invention addresses these problems and provides a new structure for pMOSFETs. Ultimately, the present invention discloses a vertical high performance complementary MISFET.  
           [0011]    U.S. Pat. No. 5,285,088 describes a “High Electron Mobility Transistor”. This device has a pair of semiconductor layers for source/drain electrodes consisting of a poly SiGe layer and a poly Si layer so as to form a partially projected “overhanging-shape” over the active area. In this case, the source/drain and the gate are self-aligned. However, it is a planar structure and still suffers from the short-channel effects.  
         SUMMARY OF THE INVENTION  
         [0012]    The objective of this invention is to provide a device structure that has superb performance and scalability. By using 2-dimensional bandgap engineering, the tradeoffs in the conventional Si technology can be avoided, and the drive current and leakage current are optimized independently. Consequently, very high drive current and excellent turn-off characteristics can be achieved simultaneously. The suppression of short-channel effects in such a device also allows continuous and more aggressive scaling of the MOSFET technology.  
           [0013]    This invention describes a vertical p-channel and a vertical complementary MISFET structure having these advantages with various embodiments. Another aspect of this invention is the process integration for such devices. The devices described in this invention have at least a hetero-barrier between the source and the body of the transistor, however, no hetero-barrier in the channel along the current flow direction. Drain induced barrier lowering is substantially reduced due to the hetero-barrier at the source junction; hence, the subthreshold swing and off-state leakage are reduced. Meanwhile, the drive current is not limited by quantum mechanical tunneling since there is no hetero-barrier in the channel. Therefore, with these devices, very high on/off ratio can be achieved. Such devices are superb in high speed, low leakage and low power applications, such as DRAM, laptop computers, and wireless communications.  
           [0014]    Any hetero-material systems with the proper band offset may be used to realize the device concept such as silicon-based or III-V material systems. Since silicon technology is the most mature, silicon based materials are the most economically feasible and attractive. For pMISFETs, compressively strained SiGe or SiGeC on silicon has the suitable band offset for holes. In order to realize the complementary MISFETs, there are two options or two types of Si-based heterostructures that can be used for nMISFETs because they have the suitable band offset for electrons. One is compressively strained Si or SiGe on relaxed SiGe buffer layers, and the other is tensile strained Si 1-x-y Ge x C y  on Si. With each heterostructure design, the channel could be a surface channel or a buried quantum well channel.  
           [0015]    The carrier mobility depends not only on the strain in the crystal, but also on crystal orientation. A recent study showed that hole mobility is enhanced significantly on a (110) substrate along &lt;110&gt;direction, while the electron mobility remains highest on a (100) substrate along &lt;100&gt;direction for devices with a gate oxide less than 2 nm and a gate length less than 150 nm. While it is not practical to integrate a nMOSFET on a (100) plane and a pMOSFET on a (110) plane using conventional, planar silicon technology, it is relative easy to do so with vertical devices or FinFETs. Therefore, a high-hole-mobility channel and a high-electron-mobility channel can be realized simultaneously on the same wafer without introducing the strain in the channel by utilizing a heterostructure or any induced localized stress derived from the device fabrication process.  
           [0016]    In the present invention, two embodiments for a vertical p-channel transistor are illustrated. Then two embodiments for a vertical CMOS are described. The fabrication methods are also described. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0017]    These and other features, objects, and advantages of the present invention will become apparent upon consideration of the following detailed description of the invention when read in conjunction with the drawing in which:  
         [0018]    [0018]FIG. 1 is an energy band diagram of compressively strained SiGe or SiGe(C) on cubic Si.  
         [0019]    [0019]FIG. 2 is an energy band diagram of tensile strained SiC on cubic Si.  
         [0020]    [0020]FIG. 3 is an energy band diagram of tensile strained Si on relaxed SiGe buffer.  
         [0021]    [0021]FIG. 4 is a top view of a vertical channel MOSFET.  
         [0022]    [0022]FIG. 5 is a cross sectional schematic of a vertical compressively strained SiGe/Si or SiGeC/Si surface channel pMOSFET with a diffusion barrier layer containing carbon and a composite source region consisting of a relaxed silicon layer and a strained SiGeC layer.  
         [0023]    [0023]FIG. 6 is a cross sectional schematic of a vertical compressively strained SiGe/Si or SiGeC/Si buried channel pMOSFET with a diffusion barrier layer containing carbon and a composite source region consisting of a relaxed silicon layer and a strained SiGeC layer.  
         [0024]    [0024]FIG. 7 is a cross sectional schematic of a vertical compressively strained SiGe/Si or SiGeC/Si surface channel pMOSFET with a heterojunction at both source and drain junction.  
         [0025]    [0025]FIG. 8A and FIG. 8B are top views of the orientations of the mesa structures or vertical structures for a vertical CMOS inverter on a (100) substrate.  
         [0026]    [0026]FIG. 9 is a cross sectional schematic of a vertical CMOS with tensile strained SiC source/drain for the nMOSFET and compressively strained SiGeC source/drain for pMOSFET according to the present invention.  
         [0027]    [0027]FIG. 10 is a cross sectional schematic of a vertical CMOS with tensile strained Si source/drain for the nMOSFET and compressively strained SiGeC source/drain for pMOSFET according to the present invention.  
     
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0028]    The lattice spacing of carbon, silicon and germanium are 3.567 Å, 5.431 Å and 5.646 Å, respectively. Biaxial tensile strain exists in pseudomorphic SiC on relaxed Si, or in pseudomorphic Si on relaxed SiGe or Ge substrate, which means the larger lattice spacing in the growth plane (surface) and smaller lattice spacing in the growth direction (normal to the surface) in the pseudomorphic material. On the other hand, compressive strain exists in pseudomorphic SiGe on relaxed Si, or in pseudomorphic Ge on relaxed SiGe, which means the smaller lattice spacing in the growth plane (surface) and larger lattice spacing in the growth direction (normal to the surface) in the pseudomorphic material. Adding a small amount of carbon (&lt;1%) into compressively strained SiGe on relaxed Si can compensate and reduce the strain in SiGe. Strain changes the band structure of the strained material. Therefore, strain may affect the energy band offset, effective mass and density of states. Referring to the drawing, FIG. 1 shows the conduction band and valence band of compressively strained SiGe or SiGe(C) on relaxed silicon by curves  2  and  3 , respectively. Holes are confined in the compressively strained SiGe(C) which has high hole mobility, and this material system is suitable for pMOSFETs.  
         [0029]    [0029]FIG. 2 shows the conduction band and valence band of tensile strained Si 1-y C y  on relaxed Si buffer layer by curves  4  and  5 , respectively. In this case, electrons are confined in the tensile strained Si 1-y C y  which has high electron mobility, and this material system is suitable for nMOSFETs. Furthermore, FIG. 3 shows the conduction band and valence band of tensile strained silicon on silicon germanium by curves  6  and  7 , respectively. Electrons are confined in the tensile strained silicon which potentially has high electron mobility, and this material system may be suitable for nMOSFETs. With the three material systems, the channel could be a surface channel or a buried quantum well channel. In FIGS. 1-3, the ordinate represents energy and the abscissa represents depth.  
         [0030]    [0030]FIG. 4 shows the top view of a vertical device  160  (not to scale). FIG. 5 shows the cross sectional view of the first embodiment which is a compressively strained SiGeC vertical pMOSFET  160  comprising a vertical column  5000  comprising several layers or regions, such as a source layer or region  164 , a body layer or region  163 , and a drain layer or region  162 , with a channel layer or region  165 , an insulator layer or region  166 , and a gate electrode layer or region  167  on the sidewalls. Vertical column or mesa  6000  forms vertical device  160 . When SiGe layer or region  164  is highly strained, its critical thickness is rather small. The more strain in the layer, the thinner is the critical thickness at which the stained layer starts to relax. The critical thickness is understood in the art as a thickness where defects are generated within a layer or region to relieve its strain so that the layer or region relaxes towards its natural lattice spacing. The lattice spacing is determined by the composition of the layer. For example, Ge lattice is 1.04 times the lattice spacing of silicon. A 50% Ge composition in a SiGe layer would be expected to have a lattice spacing of 1.02 times the lattice spacing of silicon. In this embodiment, a relaxed silicon layer or region, poly silicon layer or region or poly SiGe layer or region  410  is formed on top of strained SiGe layer  164 , and together they form the composite source that has sufficient thickness for silicidation. Layer  410  can be as thick as desired while layer or region  164  has a thickness below or about the critical thickness.  
         [0031]    The device has the following structural characteristics:  
         [0032]    1) The drain is p + -type single crystal silicon  162  with a concentration level greater than 1×10 19  atom/cm 3 .  
         [0033]    2) The body is n-type silicon  163 , and the doping level is adjusted to achieve the desirable threshold voltage;  
         [0034]    3) The p-type SiGeC layer  210  over layer  162  is used to reduce boron diffusion from drain  162  into the body  163 ; layer  210  has a p-type concentration level greater than 1×10 19  atoms/cm 3 .  
         [0035]    4) The source is p + -type compressively strained Ge, GeC or SiGeC  164  and relaxed silicon or poly silicon or poly SiGe  410  both having a p-type concentration level greater than 1×10 19  atom/cm 3 ;  
         [0036]    5) The channel  165  is compressively strained SiGeC or silicon, and there is no hetero-barrier along the current flow direction shown by arrow  104 ;  
         [0037]    6) A strained SiGeC/Si heterojunction is formed between the source  164  and the body  163  at the interface  570 , and preferably, aligned with the source/body metallurgical p/n junction;  
         [0038]    7) The gate is a conducting layer  167  overlapping the entire channel  165  over body  163  from the source  164  and to the drain  162  with an insulator  166  in between.  
         [0039]    8) The drain, source, and gate electrodes  169 ,  170  and  171  are coupled to the drain  162 , the composite source  164  plus  410  and the gate  167 , respectively.  
         [0040]    9) Layer  161  may be bulk silicon or SOI substrate or SiGe-on-insulator.  
         [0041]    Gate dielectric layer or region  166  may be an oxide, nitride, oxynitride of silicon, and oxides and silicates of Hf, Al, Zr, La, Y, Ta alone or in combination.  
         [0042]    Conducting region  167  may be a metal, metal silicide, doped poly silicon, or doped poly SiGe.  
         [0043]    Layer  210  is doped p-type in the range from 1×10 19  to 1×10 21  atoms/cm 3 .  
         [0044]    Layer or region  410  is doped p-type in the range from 1×10 19  to 1×10 21  atoms/cm 3 .  
         [0045]    Vertical structure or column  5000  may have a sidewall in the crystalline plane (100) and be perpendicular to the substrate plane or major surface of the substrate.  
         [0046]    For low noise applications, a buried channel may be preferred. A vertical buried channel pMOSFET is shown in FIG. 6. A silicon cap layer or region  175  is formed before the gate oxidation. In this case, the strained SiGe quantum well channel  165  will be able to maintain its high hole mobility because there is no surface roughness scattering. Except for silicon cap layer or region  175 , FIG. 6 is the same as FIG. 5.  
         [0047]    Note that the above embodiment is an asymmetric device, which has a heterojunction only between the source and the body i.e. interface  570 . For certain circuit applications, such as transmission gate circuits, the devices are preferred to be symmetric.  
         [0048]    The fourth embodiment of the present invention, shown in FIG. 7, is a surface channel pMOSFET  901 . It has a similar structure to the first embodiment, but with a surface channel and a composite drain which comprises a thin compressively strained SiGeC layer  900  and silicon layer or region  162 . In this structure, the SiGeC layers or regions  164  and  900  may or can have the same amount of strain. Region  900  may be p-type having a concentration level greater than 1×10 19  atoms/cm 3  carbon doped region  900  may be doped p-type in the range from 1×10 19  to 1×10 21  atoms/cm 3 . Therefore, the hetero-barriers at the source and the drain junctions have the same height; hence the device is close to a symmetric device.  
         [0049]    [0049]FIGS. 8A and 8B show the top view schematic of orientations of the mesa structures or vertical structures for a vertical NMOSFET and a vertical pMOSFET on a (100) silicon substrate. Both n- and p-channels in FIG. 8A are in the planes of the (110) family. Even though hole mobility in the (110) plane is higher than that of the (100) plane, the electron mobility is degraded compared to the (100) plane. However, when the mesa structure or vertical structure of the nMOSFET is rotated 45 degrees from the wafer notch line then the n-channels on the four sidewalls of the mesa structure or vertical structure are in the (001), (010), (001) and (010) planes, as shown in FIG. 8B. Meanwhile, in FIG. 8B, the mesa structure or vertical structure of the pMOSFET has a sidewall aligned with the wafer notch line, and the p-channels on the sidewalls of the mesa structure or vertical structure are in the (011), (011), (011) and (011) planes. Consequently, the layout for a vertical CMOS shown in FIG. 8B can achieve the high hole-mobility and high electron-mobility simultaneously. It should be noted that the orientation scheme shown in FIG. 8B can be used for any vertical MOSFETs, such as Si vertical MOSFETs with or without a replacement gate and the heterojunction MOSFETs described in this specification.  
         [0050]    [0050]FIG. 9 shows an embodiment of a vertical CMOS inverter  262 , comprising a vertical nMOSFET  74 , and a vertical pMOSFET  260 . The mesa orientation is shown in FIG. 8B, where the p-channel mesa  5000  sidewall is in the plane (110) and the n-channel mesa  3001  sidewall is in the plane (100). The device isolation is provided by insulator regions or blanket dielectric layers  168 ,  148  and  68 . The nMOSFET  74  has a tensile strained SiGeC source  64 , and a carbon-doped layer  300  in the drain to reduce phosphorus diffusion if the drain  62  is doped with phosphorus; the pMOSFET has a compressively strained SiGeC source  164 , a carbon-doped layer  210  in the drain to reduce boron diffusion if the drain  162  is doped with boron. Both devices have a silicon surface channel  65 ,  165 . The gate insulator layer or region  66 ,  166  can be oxide, oxynitride, other high-permittivity dielectrics, or a combination thereof. The gate electrode  67 ,  167  can be the same kind of metal with a mid-gap work function, or two different types of metal with suitable work function, or n-type poly silicon or poly SiGe for nMOSFET and p-type poly silicon or poly SiGe for pMOSFET. Vertical column  6000  forms pMOSFET  260 . Vertical column  4001  forms nMOSFET  74 .  
         [0051]    A method of preparing an inverter made of the vertical field effect CMOS transistors shown in FIG. 9 is described comprising the steps of:  
         [0052]    forming a silicon epitaxial layer or region  62  on a first single crystalline substrate  61 , doping the silicon epitaxial layer or region  62  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0053]    forming a Si 1-i-j Ge i C j  epitaxial layer or region  300  over the n-type silicon layer or region  62 ,  
         [0054]    forming a silicon epitaxial layer or region  63  over the Si 1-i-j Ge i C j  layer or region  300 , doping the silicon epitaxial layer or region  63  p-type,  
         [0055]    forming a strained Si 1-y C y  epitaxial layer or region  64  over the p-type silicon layer or region  63 , doping the strained Si 1-y C y  layer or region  64  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0056]    forming a silicon layer or region  450  over the n-type strained Si 1-y C y  layer or region  64 , doping the silicon layer or region  450  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0057]    forming a vertical column structure  3001  comprising at least one sidewall extending from the silicon layer or region  62 , over the second layer of strained Si 1-x C x  layer or region  300 , over third layer or region of p-type silicon  63 , over the fourth layer or region of strained Si 1-y C y    64 , to the silicon layer or region  450 ,  
         [0058]    forming a silicon layer or region  65  over a region of the at least one sidewall of the vertical structure  3001 ,  
         [0059]    forming a dielectric layer or region  66  over the silicon layer or region  65 ,  
         [0060]    forming a conducting layer or region  67  over the dielectric layer or region  66 ,  
         [0061]    masking and etching a nearby region to expose the single crystalline substrate  61 ,  
         [0062]    forming a p-type silicon  162  layer or region with a concentration level greater than 1×10 19  atoms/cm 3  on a first single crystalline substrate  161 ,  
         [0063]    forming a carbon-doped epitaxial layer or region  210  over the layer or region  162 , doping the layer or region  210  p-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0064]    forming a silicon epitaxial layer or region  163  over the layer or region  210 , doping the layer or region  163  n-type,  
         [0065]    forming a compressively strained Si 1-w-q Ge w C q  epitaxial layer or region  164  over the layer or region  163 , doping the Si 1-w-q Ge w C q  layer or region  164  p-type to a concentration level greater than 1×10 19  atom/cm 3 ,  
         [0066]    forming a silicon epitaxial layer or region  410  over the Si 1-w-q Ge w C q  layer or region  164 , doping the silicon layer or region  410  p-type to a concentration level greater than 1E19 cm −3 ,  
         [0067]    forming a vertical column structure  5000  comprising the first layer or region of silicon  162 , second layer of carbon-doped layer or region  210 , third layer of silicon layer or region  163 , fourth layer or region of Si 1-w-q Ge w C q    164 , and fifth layer or region of silicon  410 ,  
         [0068]    forming a strained Si 1-s Ge s  layer or region  165  over the outer perimeter of the above vertical column structure  5000 ,  
         [0069]    forming a dielectric layer or region  166  over the outer perimeter of above layer or region  165 , and  
         [0070]    forming a conducting layer or region  167  over the outer perimeter of above dielectric layer or region  166 .  
         [0071]    The above method may further comprise the steps of:  
         [0072]    forming a blanket dielectric  68  layer over and above the entire vertical column structure  4001 ,  
         [0073]    forming a conducting layer or region  69  through the above blanket dielectric layer  68  in contact to said n-type silicon layer  62 ,  
         [0074]    forming a conducting layer or region  70  through the above blanket dielectric layer  68  in contact to said silicon layer or region  450  at the top of the above vertical column structure  4001 ,  
         [0075]    forming a conducting layer or region  71  through the above blanket dielectric layer  68  in contact to the conducting layer or region  67  on the outer perimeter of the vertical column structure  4001 ,  
         [0076]    forming a blanket dielectric layer  168  over and above the entire vertical column structure  6000 ,  
         [0077]    forming a conducting layer or region  169  through the above blanket dielectric layer  168  in contact to the p-type silicon layer or region  162 ,  
         [0078]    forming a conducting layer or region  170  through the above blanket dielectric layer  168  in contact to the p-type silicon layer or region  410  at the top of the above vertical column structure  5000 ,  
         [0079]    forming a conducting layer or region  171  through the above blanket dielectric layer  168  in contact to the conducting layer or region  167  on the outer perimeter of the vertical column structure  5000 , and  
         [0080]    forming a dielectric region  148  on layer  61  in between the two vertical column structures  4001  and  6000  to serve as the device isolation.  
         [0081]    The sidewall of the vertical column  3001  is preferred to be in the plane (100), and be perpendicular to the substrate plane.  
         [0082]    The sidewall of the vertical column  5000  is preferred to be in the plane (110), and be perpendicular to the substrate plane.  
         [0083]    [0083]FIG. 10 shows the second embodiment of the vertical CMOS  362 , similar to FIG. 9 except for the nMOSFET  374 . The nMOSFET  374  has a tensile-strained silicon channel  65  built on a relaxed SiGe body  63 . Body  63  is relaxed with respect to virtual substrate  62 . The advantage of having tensile-strained silicon as the channel is the higher electron mobility. The mesa  3001  orientation is shown in FIG. 8B, where the p-channel is in the plane (110) and the n-channel is in the plane (100) for higher hole and electron mobilities.  
         [0084]    A method of preparing an inverter made of the vertical field effect CMOS transistors is described comprising the steps of:  
         [0085]    forming a relaxed Si 1-i Ge i  epitaxial layer or region  62  on a first single crystalline substrate  61 , doping the Si 1-i Ge i  epitaxial layer or region  62  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0086]    forming a carbon-doped SiGe epitaxial layer or region  300  over the n-type Si 1-i Ge i  layer or region  62 , doping the silicon epitaxial layer or region  300  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0087]    forming a relaxed Si 1-i Ge i  epitaxial layer or region  63  over the carbon-doped SiGe layer  300 , doping the silicon epitaxial layer  63  p-type,  
         [0088]    forming a tensile strained silicon epitaxial layer or region  64  over the p-type Si 1-i Ge i  layer  63 , doping the strained silicon layer  64  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0089]    forming a relaxed Si 1-i Ge i  layer or region  450  over the n-type strained silicon layer  64 , doping the Si 1-i Ge i  layer  450  n-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0090]    forming a vertical column structure  3001  comprising at least one sidewall extending from the relaxed Si 1-i Ge i  layer  62 , over the second layer of carbon-doped SiGe layer  300 , over third layer of p-type relaxed Si 1-i Ge i    63 , over fourth layer of strained silicon  64 , to the SiGe layer  450 ,  
         [0091]    forming a strained silicon layer or region  65  over a region of the at least one sidewall of the vertical structure  3001 ,  
         [0092]    forming a dielectric layer or region  66  over the silicon layer or region  65 ,  
         [0093]    forming a conducting layer or region  67  over the dielectric layer or region  66 ,  
         [0094]    masking and etching a nearby region to expose the single crystalline substrate  161 ,  
         [0095]    forming a p-type silicon layer or region  162  with a concentration level greater than 1×10 19  atoms/cm 3  on a first single crystalline substrate  161 ,  
         [0096]    forming a carbon-doped epitaxial layer or region  210  over the layer or region  162 , doping the layer  210  p-type to a concentration level greater than 1×10 19  atoms/cm 3 ,  
         [0097]    forming a silicon epitaxial layer or region  163  over the layer  210 , doping the layer  163  n-type,  
         [0098]    forming a compressively strained S 1-w-q Ge w C q  epitaxial layer or region  164  over the layer  163 , doping the Si 1-w-q Ge w C q  layer  164  p-type to a concentration level greater than 1×10 19  atom/cm 3 ,  
         [0099]    forming a silicon epitaxial layer or region  410  over the Si 1-w-q Ge w C q  layer  164 , doping the silicon layer  410  p-type to a concentration level greater than 1×10 19  cm −3 ,  
         [0100]    forming a vertical column structure  5000  comprising the first layer of silicon  162 , second layer of carbon-doped layer  210 , third layer of silicon layer  163 , fourth layer of Si 1-w-q Ge w C q    164 , and fifth layer of silicon  410 ,  
         [0101]    forming a strained S 1-s Ge s  layer or region  165  over the other perimeter of the above vertical column structure  5000 ,  
         [0102]    forming a dielectric layer or region  166  over the outer perimeter of the above layer  165 , and  
         [0103]    forming a conducting layer or region  167  over the outer perimeter of above dielectric layer  166 .  
         [0104]    The above method may further comprise the steps of:  
         [0105]    forming a blanket dielectric  68  layer over and above the entire vertical column structure  4001 ,  
         [0106]    forming a conducting layer or region  69  through the above blanket dielectric layer  68  in contact to said n-type silicon layer or region  62 ,  
         [0107]    forming a conducting layer or region  70  through the above blanket dielectric layer  68  in contact to said silicon layer  450  at the top of the above vertical column structure  4001 ,  
         [0108]    forming a conducting layer or region  71  through the above blanket dielectric layer  68  in contact to the conducting layer or region  67  on the outer perimeter of the vertical column structure  4001 ,  
         [0109]    forming a blanket dielectric layer  168  over and above the entire vertical column structure  6000 ,  
         [0110]    forming a conducting layer or region  169  through the above blanket dielectric layer  168  in contact to the p-type silicon layer or region  162 ,  
         [0111]    forming a conducting layer or region  170  through the above blanket dielectric layer  168  in contact to the p-type silicon  410  at the top of the above vertical column structure  2001 ,  
         [0112]    forming a conducting layer or region  171  through the above blanket dielectric layer  168  in contact to the conducting layer  167  on the outer perimeter of the vertical column structure  5000 , and  
         [0113]    forming a dielectric region  148  on layer  61  in between the two vertical column structures  4001  and  6000  to serve as the device isolation.  
         [0114]    The sidewall of the vertical column  3001  is preferred to be in the plane (100), and be perpendicular to the substrate plane.  
         [0115]    The sidewall of the vertical column  5000  is preferred to be in the plane (110), and be perpendicular to the substrate plane.  
         [0116]    According to the preferred embodiment, this invention further comprises the scheme for process integration for a vertical high mobility heterojunction pMISFET:  
         [0117]    Epitaxial growth of a stack of several layers for the drain, body, and the source with or without in-situ doping;  
         [0118]    patterning/etching to form a mesa  5000 , or pedestal, or pillow, or column, or fin;  
         [0119]    epitaxial growth of the channel layer  165 , the cap layer if desired, on the sidewall of the mesa, pedestal, pillow, column or fin;  
         [0120]    growth or deposition of the insulator layer, which may be an oxide, oxynitride, other high-permittivity dielectrics, or a combination thereof;  
         [0121]    growth or deposition of the gate electrode layer, which may be poly silicon, poly SiGe or metal, on the sidewall of the mesa, or pedestal, or pillow, or column, or fin;  
         [0122]    patterning/etching gate electrode, forming the final vertical structure  6000 ;  
         [0123]    ion implant and annealing if the source, drain, body, or the poly Si or poly SiGe gate electrode is not in-situ doped;  
         [0124]    gate patterning and etching;  
         [0125]    field oxide deposition;  
         [0126]    contact opening;  
         [0127]    source/drain silicidation; and  
         [0128]    metallization and metal sintering.  
         [0129]    It should be noted that in the drawing like elements or components are referred to by like and corresponding reference numerals.  
         [0130]    While there has been described and illustrated a semiconductor device containing a high mobility channel and a heterojunction which preferably coincides with the junction of source and/or drain, it will be apparent to those skilled in the art that modifications and variations are possible without deviating from the broad scope of the invention which shall be limited solely by the scope of the claims appended hereto.