Patent EA-001790-B1 (EA)
Title: Drawing stock usable as reinforcing element
Inventor: ARNAUD JEAN-CLAUDE
IPC: C21D8/06
Filed: 1997-01-08
Abstract: 1. A method for forming tungsten carbide comprising the steps of: (a) heating the tungsten-containing material in the presence of an inorganic alkali metal compound and in the substantial absence of halide salt at a temperature sufficient to melt said tungsten-containing material and for a time sufficient for the formation of a high density phase and a low density phase wherein the majority of said tungsten reports to said high density phase in the form of tungstate salt; (b) allowing said high density phase and said low density phase to separate by gravity wherein said high density phase settles to the bottom; (c) concentrating said tungsten by separating said high density phase from said low density phase; (d) producing tungsten carbide by subjecting said high density phase to sparging with a carbon-containing gas at an elevated temperature in order to form tungsten carbide; and (e) recycling a portion of a salt-containing material from the sparged high density phase of step (d) to a melt comprising tungsten-containing material in the presence of an alkali metal compound as described in step (a). 2. The method of claim 1, wherein said tungsten-containing material is selected from the group consisting of huebnerite (MnWO4), scheelite (CaWO4), ferberite (FeWO4), wolframite ((Fe,Mn)WO4) and mixtures thereof. 3. The method of claim 1, wherein said tungsten-containing material is selected from the group consisting of flue dusts, slags, scrap and mixtures thereof. 4. The method of claim 1, wherein said alkali metal compound is selected from the group consisting of sodium compounds and potassium compounds. 5. The method of claim 1, wherein said alkali metal compound is selected from the group consisting of sodium silicate, sodium carbonate, sodium hydroxide and mixtures thereof. 6. The method of claim 1, wherein said heating step (a) takes place at a temperature from about 900 degree C. to about 1,200 degree C. 7. The method of claim 1, wherein said heating step (a) takes place at a temperature from about 1,050 degree C. to about 1,150 degree C. 8. The method of claim 1, wherein said sparging step (d) takes place at a temperature from about 1,050 degree C. to about 1,200 degree C. 9. The method of claim 1, wherein said sparging step (d) takes place at a temperature from about 1,050 degree C. to about 1,150 degree C. 10. The method of claim 1, wherein said carbon-containing gas is a hydrocarbon gas. 11. The method of claim 1, wherein said carbon-containing gas is selected from the group consisting of methane, ethylene, propane and mixtures thereof. 12. The method of claim 1, wherein said high density phase is separated from said low density phase by pouring said high density phase from a crucible. 13. The method of claim 1, wherein said high density phase is removed through an outlet in a crucible containing said high density phase and said low density phase. 14. The method of claim 1, wherein said tungsten carbide formed in step (d) is separated from the remainder of materials and purified. 15. The method of claim 14, wherein said tungsten carbide is at least 90 percent pure after it is purified. 16. . A method for forming tungsten carbide comprising the steps of: (a) heating a tungsten mineral concentrate in the presence of a sodium or potassium compound to a temperature from about 900 degree C. to about 1,200 degree C. in order to obtain a first melt; (b) maintaining said first melt at a temperature of from about 900 degree C. to about 1,200 degree C. until said melt separates into a higher density tungsten-containing phase and lower density slag phase, wherein in at least 80% of the tungsten in said tungsten mineral concentrate reports to said higher density tungsten-containing phase; (c) separating said higher density tungsten-containing phase from said lower density slag phase; (d) heating said higher density tungsten-containing phase to a temperature of from about 1,050 degree C. to about 1,200 degree C. to obtain a second melt; (e) sparging methane gas through said second melt to form a sparged second melt comprising tungsten carbide; (f) separating a tungsten carbide enriched portion from said sparged second melt; and (g) purifying said tungsten carbide enriched portion in order to obtain purified tungsten carbide. 17. The method of claim 16, wherein a portion of a salt-containing material is recycled from the second melt to a first melt as described in step (a) in order to aid in the separation of said higher density tungsten-containing phase from said lower density slag phase. 18. The method of claim 16, wherein said higher density tungsten-containing phase comprises a tungsten oxide salt. 19. The method of claim 16, wherein said higher density tungsten-containing phase comprises sodium tungstate salt. 20. The method of claim 16, wherein said lower density slag phase comprises a silicate. 21. The method of claim 16, wherein said lower density slag phase comprises manganese silicate, iron silicate or aluminum-calcium silicates. 22. The method of claim 16, wherein said tungsten carbide is produced in a fine size with at least 90 percent of said tungsten carbide having an average diameter of less then 10 microns. 23. The method of claim 16, wherein at least 95 percent of the tungsten in said tungsten mineral concentrate reports to said higher density tungsten-containing phase. 24. The method of claim 16, wherein at least 97 percent of the tungsten in said tungsten mineral concentrate reports to said higher density tungsten-containing phase. 25. The method of claim 16, wherein at least a portion of said sodium compound is in a form selected from the group consisting of: (i) sodium silicate (Na2SiO3); or (ii) sodium carbonate (Na2CO3) in the presence of silica (SiO2). 26. The method of claim 19, wherein said purifying step (g) comprises: (a) dry grinding, air elutriation and dry separation of melt from tungsten carbide; (b) water leaching said dry purified material; (c) subjecting said water leached material to solid/liquid separation to form crude tungsten carbide crystals; (d) comminuting and acid leaching said crude tungsten carbide crystals; and (e) subjecting said comminuted and acid leached crude tungsten carbide crystals to solid/liquid separation to obtain high purity tungsten carbide. 27. The method of claim 16, wherein said purified tungsten carbide is at least 90 percent tungsten carbide. 28. A method for forming tungsten carbide comprising the steps of: (a) heating a tungstate salt to a temperature greater than its melting temperature to form a melt in the substantial absence of any halide salt such that the melt separates into a high density phase and a low density phase wherein the majority of the tungsten reports to said high density phase; (b) sparging a hydrocarbon gas through said high density phase to form tungsten carbide; and (c) separating said tungsten carbide from the remainder of said high density phase. 29. The method of claim 28, wherein said tungstate salt comprises sodium tungstate. 30. A method for forming tungsten carbide comprising the steps of: (a) heating a tungsten mineral concentrate in the presence of a sodium or potassium compound and in the substantial absence of sodium chloride to a temperature from about 900 degree C. to about 1,200 degree C. in order to obtain a first melt; (b) maintaining said first melt at a temperature of from about 900 degree C. to about 1,200 degree C. until said melt separates into a higher density tungsten-containing phase and lower density slag phase; (c) separating said higher density tungsten-containing phase from said lower density slag phase; (d) heating said higher density tungsten-containing phase to a temperature of from about 1,050 degree C. to about 1,200 degree C. to obtain a second melt; (e) sparging methane gas through said second melt to form a sparged second melt comprising tungsten carbide; (f) separating a tungsten carbide enriched portion from said sparged second melt; and (g) purifying said tungsten carbide enriched portion in order to obtain purified tungsten carbide. 31. The method of claim 5, wherein said salt-containing material which is recycled comprises materials selected from the group consisting of sodium tungstate, Na2O and mixtures thereof. 32. The method of claim 17, wherein said salt-containing material which is recycled comprises materials selected from the group consisting of sodium tungstate, Na2 O and mixtures thereof. 33. The method of claim 29 wherein a portion of said remainder of said high density phase of step (e) is recycled to a melt as set forth in step (a). 34. The method of claim 26 wherein liquid which is separated in step (c) is fed to a crystallizer and the crystals are recycled to said second melt.