PATENT DOCUMENT

Publication Number: US-11549191-B2
Application Number: US-201916277072-A
Country: US
Kind Code: B2

Title: Corrosion resistance for anodized parts having convex surface features

Abstract:
Anodic oxide coatings that provide corrosion resistance to parts having protruding features, such as edges, corners and convex-shaped features, are described. According to some embodiments, the anodic oxide coatings include an inner porous layer and an outer porous layer. The inner layer is adjacent to an underlying metal substrate and is formed under compressive stress anodizing conditions that allow the inner porous layer to be formed generally crack-free. In this way, the inner porous layer acts as a barrier that prevents water or other corrosion-inducing agents from reaching the underlying metal substrate. The outer porous layer can be thicker and harder than the inner porous layer, thereby increasing the overall hardness of the anodic oxide coating.

Claims:
What is claimed is: 
     
       1. An enclosure for a portable electronic device, the enclosure comprising:
 a metal substrate having a surface that includes a surface feature; 
 a first metal oxide layer that overlays the surface of the metal substrate, wherein the first metal oxide layer includes:
 a first set of pores that extend from an external surface of the enclosure and towards the metal substrate, and 
 an interstice that is dependent upon the surface feature, wherein the interstice extends at least partially through the first oxide layer; and 
 
 a second metal oxide layer that is disposed between the metal substrate and the first metal oxide layer, the second metal oxide layer adhered directly to the metal substrate, wherein the second metal oxide layer includes a second set of pores having an average diameter that is less than and at least half of the average diameter of the first set of pores. 
 
     
     
       2. The enclosure of  claim 1 , wherein the second metal oxide layer has a thickness between 0.5 micrometer to 2 micrometers. 
     
     
       3. The enclosure of  claim 1 , wherein the first metal oxide layer has a thickness between 10 micrometers to 17 micrometers. 
     
     
       4. The enclosure of  claim 1 , wherein the first set of pores having an average diameter, and the average diameter of the second set of pores is between 10% to 25% less than the average diameter of the first set of pores. 
     
     
       5. The enclosure of  claim 1 , wherein the metal substrate includes at least one of magnesium or zinc. 
     
     
       6. The enclosure of  claim 1 , wherein the first and second set of pores are sealed with a sealant. 
     
     
       7. The enclosure of  claim 1 , wherein the interstice has a first width, and the sealant has a second width that is less than the first width such that the sealant is unable to fill the interstice. 
     
     
       8. The enclosure of  claim 1 , further comprising:
 dye particles that are disposed within the first set of pores. 
 
     
     
       9. An enclosure for a portable electronic device, the enclosure comprising:
 an aluminum alloy substrate including a convex surface feature; 
 an anodized layer that overlays the aluminum alloy substrate, wherein the anodized layer includes:
 a first anodized layer including an interstice having a geometry that is based on the convex surface feature, the first anodized layer having a first thickness and a first set of pores, and 
 a second anodized layer that is disposed between the aluminum alloy substrate and the first anodized layer, the second anodized layer adhered directly to the metal substrate, wherein the second anodized layer has a second thickness that is less than the first thickness and a second set of pores having an average diameter that is less than and at least half of the average diameter of the first set of pores. 
 
 
     
     
       10. The enclosure of  claim 9 , wherein the first thickness is between 10 micrometers to 17 micrometers. 
     
     
       11. The enclosure of  claim 10 , wherein the second thickness is between 0.2 micrometer to 2 micrometers. 
     
     
       12. The enclosure of  claim 9 , further comprising:
 dye particles that are disposed within the first set of pores. 
 
     
     
       13. The enclosure of  claim 9 , wherein the anodized layer has a Vickers hardness of at least 300 Hv 0.05  or greater. 
     
     
       14. A method for forming an enclosure for a portable electronic device, the enclosure including a metal substrate having a surface feature, the method comprising:
 converting a first amount of the metal substrate to a first metal oxide layer under a tensile strain condition that corresponds to a first electrical parameter, wherein the first metal oxide layer includes a first set of pores and an interstice that is based on a geometry of the surface feature; and 
 converting a second amount of the metal substrate to a second metal oxide layer under a compressive stress condition that corresponds to a second electrical parameter that is less than the first electrical parameter, wherein the second metal oxide layer is adhered directly to the metal substrate and overlaid by the first metal oxide layer, wherein the second metal oxide layer includes a second set of pores having an average diameter that is less than and at least half of the average diameter of the first set of pores. 
 
     
     
       15. The method of  claim 14 , wherein the first electrical parameter includes a current density greater than 1.0 A/dm 2 , and the second electrical parameter includes a current density of less than 0.8 A/dm 2 . 
     
     
       16. The method of  claim 14 , wherein the metal substrate is converted to the first and second metal oxide layers by exposing the metal substrate to a mixed electrolytic acid. 
     
     
       17. The method of  claim 16 , wherein the mixed electrolytic acid includes sulfuric acid and oxalic acid. 
     
     
       18. The method of  claim 14 , wherein a size of the interstice is based at least on an acuteness of the geometry of the surface feature.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     The present application claims the benefit of U.S. Provisional Application No. 62/729,346, entitled “CORROSION RESISTANCE FOR ANODIZED PARTS HAVING CONVEX SURFACE FEATURES,” filed Sep. 10, 2018, the content of which is incorporated herein by reference in its entirety for all purposes. 
     This patent application is related and incorporates by reference in their entirety the copending U.S. patent application Ser. No. 15/881,305, entitled “OXIDE COATINGS FOR PROVIDING CORROSION RESISTANCE ON PARTS WITH EDGES AND CONVEX FEATURES,” filed Jan. 26, 2018. 
     Any publications, patents, and patent applications referred to in the instant specification are herein incorporated by reference in their entireties for all purposes. To the extent that the publications, patents, or patent applications incorporated by reference contradict the disclosure contained in the instant specification, the instant specification is intended to supersede and/or take precedence over any such contradictory material. 
    
    
     FIELD 
     The described embodiments relate to oxide films and methods for forming the same. The oxide films can have layered structures that provide improved adhesion. 
     BACKGROUND 
     When a metal part having convex edges or protruding features is anodized, the resulting anodic oxide film can exhibit small cracks along the convex edges and protruding features. These cracks can compromise the protective nature of the oxide film by providing pathways for water or other corrosion-inducing agents to reach the underlying metal part, thereby leaving the metal part susceptible to corrosion. 
     Certain high-strength aluminum alloys suffer from poor oxide adhesion when anodized. Alloying elements such as zinc accumulate at the interface between the metal and the oxide, and when combined with sulfur from the anodizing electrolyte, the zinc weakens the adhesion of the oxide. Regions of the oxide coating thus chip off relatively easily when mechanical stress is applied through incidents such as surface impacts. These chips expose the substrate, compromising the protective nature of the oxide film by providing pathways for water or other corrosion-inducing agents to reach the underlying metal part, thereby leaving the metal part susceptible to corrosion. The chips also constitute obvious cosmetic defects. What are needed therefore are improved anodic oxide films and anodizing techniques. 
     SUMMARY 
     This paper describes various embodiments that relate to oxide coatings useful for coating and preventing corrosion of metal substrates, including substrates having convex surface features. In particular embodiments, the oxide coatings include a porous corrosion-prevention layer proximate to the substrate. 
     According to some embodiments, an enclosure for a portable electronic device is described. The enclosure includes a metal substrate having a surface that includes a surface feature, a first metal oxide layer that overlays the surface of the metal substrate, where the first metal oxide layer includes: a first set of pores that extend from an external surface of the enclosure and towards the metal substrate, and an interstice that is dependent upon the surface feature, where the interstice extends at least partially through the first oxide layer. The enclosure further includes a second metal oxide layer that is disposed between the metal substrate and the first metal oxide layer, where the second metal oxide layer includes a second set of pores having an average diameter that is less than the first set of pores. 
     According to some embodiments, an enclosure for a portable electronic device is described. The enclosure includes an aluminum alloy substrate including a convex surface feature, an anodized layer that overlays the aluminum alloy substrate. The anodized layer includes a first anodized layer including an interstice having a geometry that is based on the convex surface feature, the first anodized layer having a first thickness, and a second anodized layer that is disposed between the aluminum alloy substrate and the first anodized layer, where the second anodized layer has a second thickness that is less than the first thickness. 
     According to some embodiments, a method for forming an enclosure for a portable electronic device, the enclosure including a metal substrate having a surface feature, is described. The method includes converting a first amount of the metal substrate to a first metal oxide layer under a tensile strain condition that corresponds to a first electrical parameter, where the first metal oxide layer includes an interstice that is based on a geometry of the surface feature, and converting a second amount of the metal substrate to a second metal oxide layer under a compressive stress condition that corresponds to a second electrical parameter that is less than the first electrical parameter, where the second metal oxide layer is overlaid by the first metal oxide layer. 
     These and other embodiments will be described in detail below. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The disclosure will be readily understood by the following detailed description in conjunction with the accompanying drawings, wherein like reference numerals designate like structural elements. 
         FIG.  1    shows perspective views of devices having metal surfaces that can be treated with the coatings described herein. 
         FIGS.  2 A- 2 B and  3 A- 3 B  illustrate cross-section views of parts having geometric features that are prone to corrosion. 
         FIGS.  4 A and  4 B  illustrate cross-section views of enclosures having geometric features that are prone to corrosion. 
         FIGS.  5 A and  5 B  show cross-section views of a part undergoing anodizing processes for forming a corrosion-resisting oxide coating, in accordance with some embodiments. 
         FIGS.  6 A- 6 E  show cross-section views of portions of the part in  FIGS.  5 A- 5 B  having the corrosion-resisting oxide coating. 
         FIGS.  7 A and  7 B  show scanning electron microscope (SEM) images of cross-section views of a part having a corrosion-resisting oxide coating, in accordance with some embodiments. 
         FIG.  8    shows a flowchart indicating a process for forming a corrosion-resisting oxide coating, in accordance with some embodiments. 
         FIGS.  9 A- 9 C  show cross-section views of a part having a corrosion-resistant oxide coating, in accordance with some embodiments. 
         FIG.  10    show a cross-section view of a part having a corrosion-resistant oxide coating, in accordance with some embodiments. 
         FIG.  11    shows a flowchart for forming a corrosion-resistant oxide coating, in accordance with some embodiments. 
         FIGS.  12 A- 12 D  show comparisons between parts formed with conventional anodization and voltage step anodization, in accordance with some embodiments. 
         FIG.  13    illustrates an electron microscope image of the part as formed using the techniques described herein, in accordance with some embodiments. 
     
    
    
     DETAILED DESCRIPTION 
     Reference will now be made in detail to representative embodiments illustrated in the accompanying drawings. It should be understood that the following descriptions are not intended to limit the embodiments to one preferred embodiment. To the contrary, it is intended to cover alternatives, modifications, and equivalents as can be included within the spirit and scope of the described embodiments as defined by the appended claims. 
     Anodic oxide films that provide improved protection against corrosion for substrates having protruding features are described. The protruding features can include edges, corners, convex-shaped surfaces, and junction regions between non-parallel surfaces of a substrate. When a substrate having protruding features is anodized using conventional anodizing processes, the resulting oxide film can have cracks, interstices, gaps, or channels at areas covering the protruding features. This is because anodizing is a conversion process, whereby the oxide film is grown out of and into the substrate, resulting in an overall expansion of the outer surface of the oxide film. A protruding feature on the substrate generates an effective in-plane tensile strain in the oxide film during the anodizing process, which can cause cracks to form within the oxide film that compromise the protective nature of the oxide film. 
     The oxide films described herein include an inner oxide layer adjacent the substrate that is resistant to developing cracks, interstices, gaps, or channels during the anodizing process, even at high stress locations such as protruding features of the substrate. The inner oxide layer is formed under compressive stress conditions that counter the effective tensile strain induced by the protruding feature geometry. In this way, the inner oxide layer can form without cracks, interstices, gaps, or channels, thereby providing full coverage of the substrate and minimizing or eliminating corrosion. According to some embodiments, a thicker and harder outer oxide layer is formed over the inner oxide layer, thereby increasing the overall hardness of the oxide film. 
     According to some embodiments, methods for forming the oxide films include a two-phase anodizing process, with the second phase conducted using lower current density or lower voltage to generate the compressive stress conditions. For a feature having a given convex radius, the oxide films formed using the two-phase process show a far lower incidence of cracks, interstices, gaps, or channels compared to conventional oxide films. 
     As described herein, the term convex surface geometry can refer to a surface of a substrate (e.g., anodic oxide layer) that curves and extends outwards and away from a base portion of the same substrate. The convex surface geometry can include a radius of curvature, where cracks or convex surface geometry dependent interstices tend to form when the radius of curvature is greater than a threshold radius of curvature. In other words, the convex surface geometry can appear “more convex” when there is an increase in the radius of curvature and/or a greater change in the radius of curvature; thereby, increasing a tendency of the substrate to form cracks and channels. Additionally, these cracks and interstices are more likely to form in the surface of the substrate when the surface is subject to tensile strain, such as during an anodization process. For example, during the anodization process, the radius of curvature of a surface of the anodic oxide layer is necessarily greater than a radius of curvature of the underlying substrate that was oxidized, which can induce lateral expansion of the anodic oxide layer. In other examples, these cracks and interstices can tend to form when the radius of curvature is less than 0.5 mm. 
     In some examples, the convex surface geometry can include surfaces (e.g., planar surfaces) that meet at an edge, where the edge can represent an abrupt change in the radius of curvature and represent a focal point for the formation of the interstice or the crack. In such some examples, the convex surface geometry can include an angle associated with where the planar surfaces meet. Cracks, fissures, and interstices that are dependent upon the convex surface geometry may tend to form when the angle at which the planar surfaces meet is less than a threshold angle. In other words, there is a greater tendency to form cracks, interstices, and channels when the angle between the surfaces is more acute (i.e., less than 90 degrees). In some examples, an acute angle between multiple surfaces may correspond to a sharp edge or a sharp protruding feature, and where further decreasing the acute angle between these multiple surfaces can lead to a sharper edge or a sharper protruding feature. In some examples, the sharpness of the edge or protruding feature can be based on the acute angle and/or the thickness of the surfaces. 
     As described herein, the terms oxide, anodic oxide, metal oxide, etc. can be used interchangeably and can refer to suitable metal oxide materials, unless otherwise specified. Furthermore, the terms coating, layer, film, etc. can be used interchangeably and can refer to any suitable material that covers a surface of a substrate, part, etc. unless otherwise specified. For example, an oxide formed by anodizing an aluminum or aluminum alloy substrate can form a corresponding aluminum oxide film, layer or coating. 
     The oxide coatings described herein are well suited for providing cosmetically appealing and protective surfaces to consumer products. For example, the oxide coatings can be used to form durable and cosmetically appealing finishes for housing of computers, portable electronic devices, wearable electronic devices, and electronic device accessories, such as those manufactured by Apple Inc., based in Cupertino, Calif. 
     These and other embodiments are discussed below with reference to  FIGS.  1 - 13   . However, those skilled in the art will readily appreciate that the detailed description given herein with respect to these Figures is for explanatory purposes only and should not be construed as limiting. 
     The methods described herein can be used to form durable and cosmetically appealing coatings for metallic surfaces of consumer electronic products, such as computing devices shown in  FIG.  1   , which includes portable phone  102 , tablet computer  104 , smart watch  106  and portable computer  108 . It is well understood that the use of personally identifiable information that is capable of being transmitted, received, and/or managed by these consumer electronic devices should follow privacy policies and practices that are generally recognized as meeting or exceeding industry or governmental requirements for maintaining the privacy of users. In particular, personally identifiable information data should be managed and handled so as to minimize risks of unintentional or unauthorized access or use, and the nature of authorized use should be clearly indicated to users. Electronic devices  102 ,  104 ,  106  and  108  can each include housings that are made of metal or have metal sections. Aluminum alloys and other anodizable metals and their alloys can be used due to their ability to anodize and form a protective anodic oxide coating that protects the metal surfaces from scratches. Aluminum alloys, such as 5000 series, 6000 series or 7000 series aluminum alloys, may be choice metal materials due to their light weight and durability. 
     Products such as electronic devices  102 ,  104 ,  106  and  108  can include metal edges, corners and other geometric features that can be susceptible to corrosion and developing cosmetic defects when anodized using conventional techniques. This is, in part, because anodizing is a conversion process that consumes surface portions of a part. To illustrate,  FIGS.  2 A- 2 B and  3 A- 3 B  show cross-section views of parts, which are treated using a conventional anodizing process. 
       FIG.  2 A  shows part  200 , which includes metal substrate  202  having a square shape with corners  203  and side defined by length a.  FIG.  2 B  shows metal substrate  202  after a conventional anodizing process, where the metal substrate has a reduced length a′. Anodizing is a conversion process, whereby a portion of metal substrate  202  is consumed and converted to a corresponding oxide film  204  having thickness t. Dashed line  205  indicates the dimensions of the original surface of metal substrate  202  prior to the anodizing process. As shown, oxide film  204  grows into and out from the original surface of the metal substrate  202  by about t/2, and increases the length of part  300  to about a′+2t. This inherent expansion from the anodizing process induces tensile strain on oxide film  204 . Since anodizing converts metal substrate  202  to a lower density porous oxide film  204 , the inherent expansion which might be expected to accommodate some of this effective strain. However, this is balanced by mass loss (e.g., aluminum dissolving into the anodizing solution) and is largely expressed in an out-of-plane direction. Thus, those portions of oxide film  204  on corners  203  can experience significant in-plane tensile strain that causes channels  207  to form during the anodizing process. The likelihood of forming cracks or interstices and the width of channels  207  are functions of the angle of corners  203 , with more acute angles associated with a higher likelihood of forming channels  207  and wider channels  207 . In particular, the angle of corners can refer to convex surface geometrical features that refer to a portion of the oxide film  204  that protrudes or extends away from the oxide film  204 . In other words, every internal angle of the convex surface geometrical features is less than or equal to 180 degrees. The angle of corners can refer to multiple surfaces that intersect or meet at a point. As the angle of the corner decreases (i.e., becomes more acute), then the corner becomes sharper and the amount of tensile strain induced at the oxide film  204  is increased. Consequently, increasing the amount of tensile strain at the oxide film  204  can cause channels  207  to form at the focal point where the multiple surfaces intersect. The likelihood of forming channels  207  and the width of the channels  207  can also depend on the thickness t of oxide film  204 , with greater thicknesses associated with a higher likelihood of cracking or forming interstices, and with the width of channel  207  can be calculated at about t/√2. 
       FIG.  3 A  shows part  300 , which includes metal substrate  302  having a radius r and a round shape defined by diameter 2r and circumference 2πr.  FIG.  3 B  shows metal substrate  302  after a conventional anodizing process, whereby a portion of metal substrate  302  is consumed and converted to a corresponding oxide film  304  having thickness t. Subsequent to the anodization process, the metal substrate  302  has a reduced radius r′. Dashed line  305  indicates the dimensions of the original surface of metal substrate  302  prior to the anodizing process. Oxide film  304  grows into and out from original surface of the metal substrate  302  and expands the diameter of part  300  to about 2r′+2t and expands the outer circumference of part  300  to about a (r′+t), which induces tensile strain on oxide film  304  that causes channel  307  to form. The likelihood of cracking or forming channels and the width of channel  307  are functions of the radius of curvature of substrate  302 , with smaller radius of curvatures associated with a higher likelihood of cracking and forming channels, and forming a wider channel  307 . The likelihood of forming channels and the width of the channels  307  are functions of the radius of curvature. In particular, the radius of curvature of the oxide film  304  can refer to convex surface geometrical features (e.g., external surface features) that protrude or extend away from a base portion (e.g., inner surface) of the oxide film  304 . In other words, the inner surfaces of the oxide film  304  are convex because the distance between two or more points of the oxide film  304  is the length of the shortest arc connecting them. As the radius of curvature increases and/or there is a greater increase in the amount of change in the radius of curvature, can result in an increase the tendency of the oxide film  304  to form channels  307 . Additionally, during the anodization process, the oxide film  304  necessarily has a greater radius of curvature than the underlying substrate  302 . Therefore, the anodization process can lead to increased lateral expansion of the oxide film  304 , which can lead to formation of channels  307 . The likelihood of cracking and forming channels, and the width of channel  307  can also depend on the thickness t of oxide film  304 , with greater thicknesses associated with a higher likelihood of cracking and a wider channel  307 . 
       FIGS.  4 A and  4 B  illustrate cross-section views of enclosures having geometric features that, when anodized using convention processes, can cause channels to form within the resultant oxide film.  FIG.  4 A  shows enclosure  400 , which includes metal substrate  402  having edge  403 . The geometric constraints of edge  403  induce tensile stress within oxide coating  404  during the anodizing process, thereby causing channel  407  to form—similar to as described above with reference to  FIGS.  2 A- 2 B and  3 A- 3 B . The size (e.g., as measured by width w) of channel  407  will depend, in part, on the acuteness of edge  403  and thickness t of oxide coating  404 . In some cases, width w of channel can range between about 10 micrometers to about 800 micrometers. 
     Although channel  407  may in some cases be too small to be visible, channel  407  can act as a pathway for water, other corrosion-inducing agents, or other contaminant to reach underlying substrate  402 , thereby compromising the protective nature of oxide coating  404 . In some products, smaller channel  407  may not lead to significant corrosion of the underlying substrate  402 . Furthermore, the product may not be exposed to moisture on a regular basis during normal use. However, some products, such as some portable electronic devices, may be exposed to more aggressively corrosive environments, such as exposure to sweat, humid conditions, and chlorides from chlorinated or ocean water, which can exacerbate the corrosion process and lead to significant corrosion of substrate  402 . 
     Furthermore, some types of metal substrates may be more susceptible to corrosion. For example, some aluminum alloys that include relatively high levels of zinc may be more susceptible to corrosion than other aluminum alloys under certain conditions. In general, zinc can be added as an alloying element to increase the strength and hardness of an aluminum alloy. For example, some 7000-series aluminum alloys (per The International Alloy Designation System), which are known for their high strength, can have relatively high levels of zinc. In some applications, the target yield strength for substrate  402  is at least about 330 MPa. In some cases, this corresponds to an aluminum alloy having a zinc concentration of at least about 4 weight %. In other cases, this corresponds to an aluminum alloy having a zinc concentration of at least about 2 weight %. It is believed that zinc combines with magnesium as another alloying element to form precipitates such as MgZn 2  (the η′ or “eta-prime” phase), which gives the aluminum alloy its high strength. Thus, the aluminum alloys having relatively high levels of zinc may also have relatively high levels of magnesium. Despite the advantage of increasing the strength of the substrate, higher levels of zinc can also be associated with increased vulnerability to corrosion. Thus, the presence of channel  407  can be especially detrimental to those substrates  402  composed of aluminum alloys having zinc concentrations of about 4 weight % or higher. 
     It should be noted that width w of channel  407  can be on the order of micrometers, and is therefore generally three to four orders of magnitude greater than diameters of the pores formed within oxide coating  404  during the anodizing process, which are typically in the scale of tens of nanometers. Thus, a subsequent hydrothermal sealing process would not be able to sufficiently close off channel  407 . 
     It should also be noted that a polymer coating applied over oxide coating  404  and into channel  407  used mitigate corrosion can detract from the tactile and visible cosmetics of oxide coating. In particular, a polymer coating may have a warm and sticky feeling compared to a cool and smooth feeling of an outer oxide coating. Furthermore, polymer coatings may introduce their own reliability limits, such as increased changes of discoloration under ultraviolet light exposure, or attack by certain everyday household chemicals. 
       FIG.  4 B  shows enclosure  420 , which includes metal substrate  422  having a curved surface  423 , which can correspond to a curved edge, a curved corner, or a curved protruding feature of enclosure  420 . Oxide coating  424  formed using a conventional anodizing process includes channel  427 . As described above with reference to  FIG.  4 A , channel  427  can act as a pathway for corrosion-inducing agents to reach metal substrate  422 . Width w of channel  427  will depend, in part, on the radius of curvature of curved surface  423  and thickness t of oxide coating  424 . For example, in some cases, radius of curvatures of about 0.5 mm or smaller for oxide coating  424  having thickness t of about 8 micrometers or greater can cause channel  427  to form. In some applications, thicknesses t of about 12 micrometers or greater may be preferred for adequate corrosion protection of some types of aluminum alloys. Thus, such oxide coatings would likely develop channels along convex geometrical surfaces or convex protruding features. 
     Described herein are anodizing methods for forming an oxide coating that provides improved corrosion resistance, especially useful on parts with edges, corners and convex features. Even a coarse blast texture, or a surface roughened through a laser marking or engraving procedure could result in such features.  FIGS.  5 A and  5 B  show cross-section views of part  500  undergoing an anodizing process in accordance with some embodiments. At  FIG.  5 A , metal substrate  502  of part  500  has undergone a first anodizing process, whereby a portion of substrate  502  is converted to first oxide layer  504 . In some embodiments, substrate  502  corresponds to a metal portion of an enclosure of an electronic device, such as device  102 ,  104 ,  106  or  108 , described above. Substrate  502  can be composed of any suitable anodizable material, including aluminum and aluminum alloys. In some embodiments, substrate  502  is composed of high-strength aluminum alloy, such as those having relatively high levels of zinc as an alloying element. As described above, higher concentrations of zinc and/or magnesium can be associated with greater yield strength and hardness. In some embodiments, substrate  502  is composed of an aluminum alloy having a zinc concentration of at least about 4 weight %. In some embodiments, substrate  502  is composed of an aluminum alloy having a zinc concentration of at least about 2 weight %. In some embodiments, substrate  502  is composed of an aluminum alloy having a magnesium concentration of at least about 2 weight %. In some embodiments, substrate  502  is composed of an aluminum alloy having a magnesium concentration of at least about 1 weight %. In some applications, substrate  502  has a yield strength of at least about 330 MPa. 
     Another consideration regarding substrate  502  relates to the cosmetics. Color and finish quality can be important aspects when manufacturing consumer products. Some alloying elements, such as iron, copper, and silver, within substrate  502  can discolor first oxide layer  504 . For example, copper can add a yellow color to the first oxide layer  504 , which can be noticeable even when copper is added in quantities as low as about 0.2 weight %. Thus, in some embodiments, where such yellowing in first oxide layer  504  is undesirable, substrate  502  is composed of an aluminum alloy having a copper concentration of no more than about 0.2 weight %—in some embodiments, a copper concentration of no more than about 0.1 weight %. These and other details as to how alloying elements can affect strength and coloration of substrate  502  are described in U.S. patent application Ser. Nos. 14/830,699 and 14/830,705, both filed on Aug. 19, 2015, and U.S. patent application Ser. No. 14/927,225, filed on Oct. 29, 2015, each of which is incorporated herein in its entirety for all purposes. 
     Any suitable anodizing process can be used to form first oxide layer  504 . In some embodiments, a “Type II anodizing” process (as defined by military specification MIL-A-8625 standards) is used, which involves anodizing in an aqueous sulfuric acid-based electrolyte. In some embodiments, the Type II anodizing process involves using an applied current density of between about 1 A/dm 2  and about 2 A/dm 2 . In a particular embodiment, the applied current density is no less than about 1.3 A/dm 2 . In some embodiments, the Type II anodizing involves using an electrolyte temperature of between about 15 degrees C. and about 25 degrees C. It should be noted that anodizing processes using other types of electrolytes might be used, including those using oxalic acid-based electrolytes or phosphoric acid-based electrolytes. However, sulfuric acid-based electrolytes can provide porous (and therefore dyeable), relatively colorless, and relatively durable coatings, which can be desirable characteristics for consumer products, such as electronic devices  102 ,  104 ,  106  and  108  described above. 
     First oxide layer  504  is porous in that it includes pores  505 , which are formed during the anodizing process and which can be filled with colorant in a subsequent anodic film coloring operation. The size of pores  505  within first oxide layer  504  will vary depending on the anodizing process conditions. In some embodiments, pores  505  have diameters ranging between about 10 nanometers and about 50 nanometers. The thickness  506  of first oxide layer  504  can vary, depending on application requirements. In some consumer electronic enclosure applications, thickness  506  should be sufficiently large to provide adequate protection to substrate  502  against denting and scratching under normal use, and sufficiently small such that first oxide layer  504  remains cosmetically appealing and relatively colorless. In some embodiments, this corresponds to thickness  506  ranging between about 10 micrometers and about 50 micrometers. In some embodiments, this corresponds to thickness  506  ranging between about 10 micrometers and about 20 micrometers 
       FIG.  5 B  shows part  500  after a second anodizing process is performed, whereby another portion of substrate  502  is converted to second oxide layer  508 , having a thickness  510 . Because of their relative positions, second oxide layer  508  can be referred to as an inner oxide layer and first oxide layer can be referred to as an outer oxide layer. Together, first oxide layer  504  and second oxide layer  508  can be referred to as oxide coating  511 , having a thickness  512  (thickness  506  plus thickness  510 ). 
     The second anodizing process is different than the first anodizing process used to form first oxide layer  504 , in that the second anodizing process involves growing second oxide layer  504  under compressive stress conditions compared to tensile stress conditions of the first anodizing process. As described above with reference to  FIGS.  2 A- 2 B,  3 A- 3 B and  4 A- 4 B , oxide films grown under tensile stress can form interstices, cracks or channels, especially in those regions of a substrate that include high strain regions such as edges, corners and convex-shaped features. The second anodizing process involves adjusting anodizing parameters such that second oxide layer  508  experiences a compressive stress during its formation, so that it can tolerate a higher level of strain during its formation. Thus, second oxide layer  508  is less likely to develop channels compared to first oxide layer  504 , even at high strain regions of a part, such as edges, corners, convex-shaped protrusions, or textured or roughened surfaces which exhibit sufficiently small radius of curvature or acute angles where different surfaces meet at an edge. This means that even if first oxide layer  504  has channels formed during the first anodizing process, second oxide layer  508  can remain crack-free or interstice-free and therefore protect substrate  502  from exposure to water, other corrosion-inducing agents, or other contaminant. These aspects will be described in detail below with reference to  FIGS.  6 A- 6 D . 
     Process conditions of the second anodizing process can vary. In some embodiments, the second anodizing process involves keeping part  500  in the same electrolyte as used during the first anodizing process, and reducing the current density compared to that used during the first anodizing process. One of the advantages of keeping part  500  in the same electrolyte during the first and second anodizing processes is that this simplifies manufacturing. In particular embodiments, the first and second anodizing processes are both performed in an aqueous sulfuric acid electrolyte (e.g., a 200 g/l solution at 25 degrees C.) and the current density is reduced by a factor of four (e.g., from about 1.6 A/dm 2  to about 0.4 A/dm 2 ), corresponding to a reduction in voltage of about one half (½). In some embodiments, the second anodizing process involves using a current density ranging less than about 0.8 A/dm 2 . In a particular embodiment, the second anodizing process involves using a current density ranging between about 0.2 A/dm 2  and about 0.9 A/dm 2 . In another embodiment, the second anodizing process involves using a voltage ranging between about 6 volts and about 10 volts. In some embodiments, using a higher electrolyte temperature drops the effective voltage, thereby inducing a compressive stress conditions during the second anodizing process. In another variation, the current density (or voltage) is dropped as a continuous gradient and ends at a target low current density (or voltage) rather than abruptly dropped in one step. 
     Due to the different anodizing conditions, second oxide layer  508  has different structural properties than first oxide layer  504 . The structural difference, which can be key to the present embodiments, is the stress during layer formation, with the second layer being formed under compressive stress. In particular, pores  518  within second oxide layer  508  are generally smaller in diameter compared to pores  505  of first oxide layer  504 . In some embodiments, the diameters of pores  518  of second oxide layer  508  are about half (½) the diameters of pores  505  of first oxide layer  504 . Thus, a first pore in the first oxide layer  504  can have a first diameter that is greater than that of a pore in the second oxide layer  508  (e.g., the second diameter can be at least half the first diameter). 
     An undesirable consequence of anodizing conditions selected to induce compressive stress in the second oxide layer  508  (namely lower current density, lower voltage or higher electrolyte temperature) can be that reductive dissolution is greater. It can be a relatively “soft” anodizing process, which results in softer oxide films. This softening particularly affects outer surface  516 , and the outer portion of the first oxide layer  504 , making the overall film less abrasion resistant. Thus, for those applications where the oxide coating hardness should be sufficiently high to resist scratching and denting, the relatively “hard” process used to grow the first oxide layer  504  should constitute as much of the overall processing time as possible. The corresponding layer thickness  506  of first oxide layer  504  will be much greater than the layer thickness  510  of the second oxide layer  508 . For example, in some consumer electronic enclosure applications where the oxide coating hardness should be sufficiently high to resist scratching and denting, the harder first oxide layer  504  should have a much greater thickness  506  compared to thickness  510  of the softer second oxide layer  508 . For example, in some consumer electronic enclosure applications, oxide coating  511  should have a hardness of at least about 250 HV 0.05  as measured in accordance with Vickers hardness testing standards—in some embodiments at least about 300 HV 0.05 . In some embodiments, thickness  510  of second oxide layer ranges between about 2% and about 15% of the thickness of oxide coating  511 . In some embodiments, second oxide layer  508  has a thickness no greater than about 2 micrometers. In some consumer product applications, thickness  512  of oxide coating  511  should be at least about 8 micrometers in order to provide adequate protection to substrate  502 , but not be so thick as to negatively affect the cosmetics of part  500 . In particular embodiments, thickness  512  ranges between about 8 micrometers and about 30 micrometers. In a particular embodiment, thickness  512  ranges between about 10 micrometers and about 15 micrometers. 
     In addition to being generally crack-free or interstice-free due to the compressive stress conditions of the second anodizing process, the presence of second oxide layer  508  can provide other advantages. For example, second oxide layer  508  can better adhere to substrate  502  compared to first oxide layer  504  due to the compressive stress conditions from which second oxide layer  508  was formed. This means that oxide coating  511  can be less susceptible to delamination compared to an oxide coating having only first oxide layer  504 . Thus, part  500  would be less susceptible to chipping or delamination that would cause cosmetic defects and also leave those chipped or delaminated areas of substrate  502  exposed and vulnerable to corrosion. 
     Another way in which second oxide layer  508  can provide structural advantages to oxide coating  511  relates to interface  514  between first oxide layer  504  and second oxide layer  508 . In particular, oxide coating  511  may be subjected to forces that impact outer surface  516  during use of part  500 , such as from scratching, gouging or drop events, which can cause damage in the form of channels within oxide coating  511 . If these post-anodizing channels occur, they may propagate through first oxide layer  504  and be deflected in a lateral direction (generally parallel to outer surface  516 ) by interface  514 , thereby preventing such channels from propagating through second layer oxide layer  508 . It should be noted that this type of channel occurs during the use of part  500  (i.e., after oxide coating  511  has already been formed), whereas channels  207  and  407  described above with reference to  FIGS.  2 A- 2 B,  3 A- 3 B and  4 A- 4 B  occur during the anodizing process. In this way, second oxide layer  508  can provide protection against post-anodizing channels. It should be noted that, in some embodiments, thickness  510  of second oxide layer  508  is at least a prescribed minimum thickness in order to prevent or reduce the likelihood of such post-anodizing channels. In some embodiments, this minimum thickness is about 0.5 micrometers. Thus, in some embodiments, thickness  510  ranges between about 0.5 micrometers and about 2 micrometers. 
     In particular, the presently described two-step anodizing process provides a means of improving the interfacial adhesion between an anodic oxide coating and relatively pure 7000-series aluminum alloys comprising zinc. For instance, specific types of aluminum alloys (e.g., aluminum-zinc alloys, aluminum-magnesium alloys, etc.) can be susceptible to delamination when anodized using a conventional Type II anodizing process. In particular, specific types of electrolytes, such as sulfuric acid, can include chemical species (e.g., sulfur) that preferentially combine with alloying agents (e.g., zinc) to form delamination compounds that can promote delamination between the oxide coating  511  and the substrate  502 . In order to minimize the possibility of delamination of these parts during the anodization process, other types of acids, such as oxalic acid and mixed acids can be generally used. However, these types of acids are associated with certain drawbacks, such as a higher probability of discoloring these parts with a yellow appearance during the anodization process. Consequently, the discoloration of these anodized parts is cosmetically unappealing. 
     Beneficially, the techniques described herein are able to improve interfacial adhesion between the oxide coating  511  and the substrate  502  relative to the conventional Type II anodizing process, such that these parts can be anodized using electrolytes, such as sulfuric acid, which were previously avoided due to their strong likelihood of inducing delamination. Additionally, by anodizing these parts using these types of electrolytes, discoloration of these parts can be generally avoided. 
     According to some embodiments, interfacial adhesion between the oxide coating  511  and the substrate  502  can be improved by subjecting the part  500  to a two-step anodizing process, where first and second steps for forming the first metal oxide coating  504  and the second metal oxide coating  508  are performed under different electrical parameter conditions (e.g., current density, voltage, etc.). Furthermore, in some embodiments, the first and second metal oxide coatings  504 ,  508  can be formed by exposing the part  500  to the same electrolytic solution during the first and second anodizing processes. For example, the second anodizing process can include exposing the part  500  to the same electrolytic solution that the part  500  was previously exposed to during the first anodizing process. In other words, the part  500  does not need to be removed from the electrolytic solution in-between the first and second anodizing processes. In other embodiments, the first and second metal oxide coatings  504 ,  508  can be formed by exposing the part  500  to a substantially similar electrolyte. According to some examples, the electrolytic solution that is used to anodize the part  500  during the first and second anodizing processes can include one of sulfuric acid, phosphoric acid, or chromic acid. 
     While the first anodizing process can be performed at a relatively high current density (or voltage), such as between about 1 A/dm 2  to about 2 A/dm 2 , the second anodizing process can be performed at a lower current density (or voltage), such as 1 A/dm 2  or less. In other examples, the second anodizing process can be performed at a current density between about 0.2 A/dm 2  to about 0.9 A/dm 2 . In particular, implementing a lower current density (or voltage) during the second anodizing process can impart compressive stress conditions against the part  500 . Beneficially, by imparting compressive stress conditions, the second metal oxide layer  508  that is formed as a result of the second anodizing process is able to tolerate a higher level of strain, thereby significantly minimizing and/or preventing the likelihood of delamination between the oxide coating  511  and the substrate  502 , as will be described in greater detail herein. 
     According to some embodiments, the minimized delamination and/or prevention of delamination as a result of performing the second anodizing process under reduced electrical parameter conditions (e.g., current density, voltage, etc.) can be attributed to the presence of fewer alloying agents, such as zinc, that aggregate and become enriched at an interface  520  between the substrate  502  and the second metal oxide layer  508  during the second anodizing process. Specifically, it has been found that particular alloying agents, such as zinc can combine with one or more chemical species included within the electrolytic solution to form delaminating compounds that can weaken the interfacial adhesion between the oxide coating  511  and the substrate  502  at the interface  520 . In particular, the formation of delamination compounds can cause the oxide coating  511  to be susceptible to delamination (e.g., chipping, spalling, peeling, etc.), such as when the part  500  is subject to a high-impact event. In some examples, the alloying agents, such as zinc from the aluminum alloy substrate can act as an interface-weakening agent when the zinc becomes enriched at the interface  520 . The zinc can aggregate at the interface  520  and form a thin layer of zinc. The enriched zinc layer can preferentially combine with sulfur-containing species, such as from a sulfuric acid electrolyte, thereby forming one or more zinc-sulfur species, such as zinc folate or a zinc sulfite. Consequently, these one or more zinc-sulfur species can act as delaminating compounds or interface-weakening agents that disrupt the interface adhesion between the oxide coating  511  and the substrate  502 . However, it has been found that the enrichment of zinc at the interface  520  can be minimized and/or prevented by lowering the current density (or voltage) of the second anodizing process relative to the first anodizing process, such as 0.6 A/dm 2  or less. Instead zinc can become more readily incorporated directly into the second metal oxide layer  508  so as to prevent zinc from aggregating at the interface  520 . 
     In some examples, traditionally, sulfur from the sulfuric acid electrolyte can also accumulate at the interface  520  and combine with the alloying agents so as to weaken the interface adhesion between the oxide coating  511  and the substrate  502  at the interface  520 . However, by performing the second anodizing process at a relatively low current density (or voltage) can also minimize the presence of sulfur elements at the interface  520 . In particular, the sulfur elements can be locked within the second metal oxide layer  508  and less driven towards the interface  520 . Beneficially, this reduction of sulfur elements at the interface  520  can prevent and/or minimize zinc-sulfur compounds from interacting with the alloying agents. 
     According to some embodiments, the second metal oxide layer  508  formed by the techniques described herein can be characterized as having different structural properties than the first metal oxide layer  504 . This difference in structural properties can be attributed to forming the second metal oxide layer  508  under compressive stress conditions while forming the first metal oxide layer  504  under tensile strain conditions. In some examples, the pores  518  within the second metal oxide layer  508  are generally smaller in diameter than pores  505  within the first metal oxide layer  504 . In some examples, the pores  518  of the second metal oxide layer  508  have pore diameters that are about half of the pore diameters of the pores  505  of the first metal oxide layer  504 . 
     The methods described herein may be used in combination with the afore-mentioned patent publications, to yield further improvement in interfacial adhesion by a factor of two or more, without additional discoloration. 
     Additionally, adhesion between the oxide coating  511  and the substrate  502  can be measured using a 5-by-5 pattern of corner-linked 10 kg Vickers indents (as described in U.S. Patent publication No. 2016/0290917 A1, entitled “PROCESS FOR EVALUATION OF DELAMINATION-RESISTANCE OF HARD COATINGS ON METAL SUBSTRATES,” published Oct. 6, 2016, which is incorporated by reference in its entirety for all purposes) yields fewer than 5 vertices of delamination—as compared to an unacceptable level of delamination (e.g., greater than 15 vertices of delamination) observed when the same alloy is anodized in the same electrolyte (e.g., 200 g/l sulfuric acid) without the presently described two-step process. 
     Other methods identified for overcoming such interfacial adhesion problems include micro-alloying with elements such as copper and silver (as described in U.S. Patent publication No. 2017/0051426 A1, entitled “PROCESSES TO AVOID ANODIC OXIDE DELAMINATION OF ANODIZED HIGH STRENGTH ALUMINUM ALLOYS,” published Feb. 23, 2017, which is incorporated by reference in its entirety for all purposes), anodizing in electrolytes comprising organic acids (such as described in U.S. Patent publication No. 2016/0060783 A1, entitled “PROCESS TO MITIGATE SPALLATION OF ANODIC OXIDE COATINGS FROM HIGH STRENGTH SUBSTRATE ALLOYS,” published Mar. 3, 2016, and U.S. Patent publication No. 2016/0289858 A1, entitled “PROCESS TO MITIGATE GRAIN TEXTURE DIFFERENTIAL GROWTH RATES IN MIRROR-FINISH ANODIZED ALUMINUM,” published Oct. 6, 2016, which are incorporated by reference in their entireties for all purposes). However, these methods can result in some degree of discoloration (e.g., yellowness) in the resulting oxide film. 
     As described above, discoloration of part  500  can be an important factor for consumer product applications. The degree of discoloration can be measured using colorimetry spectrophotometer techniques and quantified according to color space standards, such as CIE 1976 L*a*b* by the International Commission on Illumination. The CIE 1976 L*a*b* color space model is used to characterize colors of an object according to color opponents L* corresponding to an amount of lightness, a* corresponding to amounts of green and magenta, and b* corresponding to amounts of blue and yellow. By convention, higher L* values correspond to greater amounts of lightness and lower L* values correspond to lesser amounts of lightness. Negative b* values indicate a blue color, with more negative b* values indicating a bluer color, and positive b* values indicate a yellow color, with more positive b* values indicating a yellower color. 
     Anodic oxide coatings characterized as having b* values greater than about 1 will generally have a perceptibly yellow color. The presence of too much copper or other certain types of alloying elements within a substrate and cause part  500  to have b* values greater than 1 when oxide coating  511  is more than about five micrometers in thickness. Since a yellow color is undesirable in some applications, in some embodiments, oxide coating  511  is characterized having a b* value of less than 1. In some embodiments, oxide coating  511  is characterized having a b* value between about 1 and −1 and a* value between about 1 and −1, corresponding to a substantially colorless oxide coating  511  when undyed. 
     After the second anodizing process is complete, any suitable post-anodizing process can be implemented, such as an anodic film dyeing process, hydrothermal sealing process, and/or anodic film buffing/polishing process. In some applications, oxide coating  511  is left undyed and substantially colorless and hydrothermally sealed. In other applications, oxide coating  511  is colorized by depositing dye and/or metal within pores  505 , and then hydrothermally sealed. 
       FIGS.  6 A- 6 B  show cross-section views of different portions of part  500 . Part  500  can correspond to a consumer electronic device, such as device  102 ,  104 ,  106  or  108 .  FIG.  6 A  shows a portion of part  500  having a convex feature  602 , such as a radius of curvature, convex edges, corner or protruding feature.  FIG.  6 B  shows a portion of part  500  having a convex-shaped rounded feature  604 , such as a rounded edge (i.e., having a curved profile), corner or protruding feature. The convex feature  602  or convex-shaped rounded feature  604  may also be small features within a textured surface, such as a blast-textured finish, a chemically etched surface, a laser-textured or laser marked finish, which exhibit roughness with features having convex radii. For simplicity, the porous structure of oxide coating  511  is not shown. 
       FIG.  6 A  shows first oxide layer  504  has channel  607  in the region over convex feature  602 . Anodizing conditions of the first anodizing process combined with the tensile strain at convex feature  602  to form channel  607 . As described above, the likelihood of channel  607  being formed, as well as width  608  of channel  607 , will depend on conditions of the first anodizing process and the acuteness or sharpness of convex feature  602 . In some embodiments, channel  607  has width  608  ranging between about 1 micrometer and about 5 micrometers. In some cases, channel  607  extends lengthwise from outer surface  516  to interface  514  between first oxide layer  504  and second oxide layer  508 —i.e., through the entire thickness  506  of first oxide layer  504 . In other cases, channel  607  only extends partially through the thickness  506  of first oxide layer  504 . 
       FIG.  6 B  shows first oxide layer  504  has channel  617  in the region over rounded feature  604 . In some embodiments, surface  601  corresponds to a bottom and generally planar surface of a bottom region of an enclosure for an electronic device, and surface  603  corresponds to a curved lateral surface (having a curved profile) of a side portion of the electronic device. Like channel  607 , channel  617  was formed during the first anodizing process due, in part, to tensile strain at rounded feature  604 . The likelihood of channel  617 , and width  618  of channel  617 , will depend on conditions of the first anodizing process and the radius of curvature of rounded feature  604 . In some case, channel  617  is likely to occur when thickness  506  of first oxide layer  504  is at least 8 micrometers and the radius of curvature of rounded feature  604  is smaller than about 0.5 millimeters. In some embodiments, channel  617  has width  618  ranging between about 1 micrometer and about 5 micrometers. In some cases, channel  617  extends lengthwise from outer surface  516  to interface  514  between first oxide layer  504  and second oxide layer  508 —i.e., through the entire thickness  506  of first oxide layer  504 . In other cases, channel  617  only extends partially through the thickness  506  of first oxide layer  504 . 
     Although channels  607  and  617  extend at least partially through first oxide layer  504 , they do not penetrate through second oxide layer  508 . This is because second oxide layer  508  was formed using the second anodizing process under conditions which generate compressive stresses in the oxide film, counteracting and resisting the effective lateral growth strain induced by film growth on convex feature  602  and rounded feature  604 . In some cases, channels  607  and  617  only partially enter the second oxide layer  508 . In other cases, channels  607  and  617  terminate at interface  514  between first oxide layer  504  and second oxide layer  508 . For example, in some embodiments, second oxide layer  508  has an outer surface (defined by interface  514 ) that generally conforms to the curvature of curved lateral surface  603 , while first an outer surface  516  of first oxide layer  504  has channel  617 , and therefore does not conform to the curvature of the curved lateral surface  603 . In other words, interface  514  can be characterized as having a generally constant and smooth curvature without any interruptions. In contrast, outer surface  516  of first oxide layer  504  includes channel  617 , which corresponds to an abrupt discontinuity in the curved profile of outer surface  516 . As described herein, the abrupt discontinuity in the curved profile can refer to a convex surface feature that extends from a base portion of the first oxide layer  504 . 
     In other cases, channels  607  and  617  penetrate through first oxide layer  504  and partially through second oxide layer  508 . In any case, channels  607  and  617  do not penetrate all the way through thickness  510  of second oxide layer  508 . In this way, second oxide layer  508  prevents channels  607  and  617  from extending to substrate  502 , thereby preventing substrate  502  from being exposed to any of a number of corrosion-inducing agents and contaminants from various environmental factors such as humidity, high temperatures, or chemicals such as salt, sweat or chlorine. These environmental exposures can be replicated and tested at accelerated rates in controlled lab environments, with salt spray testing or cycles of immersion in artificial sweat. In some cases, part  500  withstands corrosion after about 9 days of continuous salt spray testing at 65 degrees C. and 90% relative humidity (correlating to about 5 years of service in a humid marine environment). 
       FIG.  6 C  shows a cross-section view of a greater portion of part  500 . As shown, part  500  includes metal substrate  502  that is shaped and sized to form cavity  620 , which is suitable for carrying electronic components of part  500 . In this way, metal substrate  502  can serve as an enclosure. In a particular embodiment, part  500  corresponds to smart watch  106 , described above with reference to  FIG.  1   . Metal substrate (also referred to as an enclosure or housing)  502  includes recesses  626 , which can accept correspondingly shaped portions of a wristband so that part  500  can be worn on a user&#39;s wrist. Part  500  also includes cover  622  and component  624 , which cooperate with metal substrate  502  to complete the enclosure. In particular embodiments, cover  622  can correspond to a visibly transparent cover for a touch display assembly (not shown) that is configured to accept touch input from a user. Component  624  can include one more light sensors configured to accept input from a user. For example, component  624  can be configured to contact a user&#39;s wrist and collect light input related to the user&#39;s heart rate. Cover  622  and component  624  can be positioned within respective openings of metal substrate  502  (i.e., within openings of metal enclosure  502 ). 
     Oxide coating  511  covers and protects metal substrate  502  from abrasion and exposure to chemical contaminants. Oxide coating  511  can fully cover and follow the contours of metal substrate  502 , including over generally planar surface  601  of a bottom region of substrate  502  and curved lateral surface  603  of side region of substrate  502 . In some embodiments, curved lateral surface  603  has a spline-shaped curvature. For simplicity, first oxide layer  504  and second oxide layer  508  of oxide coating  511  are not depicted in  FIG.  6 C . The first oxide layer  504  of oxide coating  511  provides a cosmetically appealing and abrasion resistant outer surface for part  500 . The second oxide layer  508  of oxide coating  511  can act as a interstice-free barrier or crack-free barrier, even where portions of outer first oxide layer  504  that may have channels (e.g.,  607  or  617  shown in  FIGS.  6 A and  6 B ). For example, the first oxide layer  504  portion of oxide coating  511  formed over curved side surfaces  603  and convex edges  609  may have channels from the first anodizing process. Other types of outwardly projecting features of metal substrate  502  that may have oxide coating  511  with channels can include curved regions  611  proximate to recesses  626 , and bezel regions  612  proximate to cover  622 . In general, those portions of substrate  502  that are junction regions between two non-parallel sides of substrate  502  (e.g., corners, curved or convex edges, protrusions, etc.) may have an oxide coating  511  with channels. The second oxide layer  508  of oxide coating  511  prevents encroachment of corrosion-inducing contaminants from reaching substrate  502  through such channels. 
     The corrosion-resisting oxide coatings described herein can also be used to protect features having very small dimensions. For example,  FIGS.  6 D and  6 E  show cross-section views of such small features on a textured surface  628  of part  500 , according to some embodiments. In  FIG.  6 D , shows part  500  after oxide coating  511  is formed on textured surface  628  of substrate  502 , and  FIG.  6 E  shows part  500  after an optional oxide polishing operation is performed to smooth outer surface  516  of oxide coating  511 . 
     Textured surface  628  is formed by treating substrate  502  with one or more surface roughening operations prior to performing the first and second anodizing processes. Suitable roughing operations can include one or more abrasive material blasting, chemical etching, laser processing, or laser-marking (e.g., if textured surface  628  corresponds to the surface of a laser-marked logo, text or other feature). Textured surface  628  is characterized as having a series of peaks  630  and valleys  632  that capture and reflect light in a way that can create matte or sparkling appearance to substrate  502 . Since peaks  630  are protrusions (i.e., have convex radii), they can cause localized in-plane tensile strain within first oxide layer  504  during the first anodizing process, and therefore can cause channel  634  to form. Of course, more than one channel  634  can be formed within first oxide layer  504 , the prevalence of which will depend on the size of peaks  630 , as well as the conditions of the first anodizing process. In some embodiments, peaks  630  having heights  636  of about 5 micrometers or more may cause channel  634  to form using some Type II anodizing processes. In any case, second oxide layer  508 , formed using the compressive stress second anodizing process, prevents channel  634  from extending to substrate  502  and thereby protects substrate  502  from exposure to corrosion-inducing agents or other contaminants. 
     It should be noted that the surface features that can cause sufficient in-plane tensile strain to cause cracks or channels to form during anodizing are not limited to the examples described above. That is, any protruding, outwardly curved, convex-shaped, convex edges or corner surface features may be associated with forming a channel within the first oxide layer. Other examples may include metal surfaces of buttons (e.g., watch crown), switches, bezels, frames, brackets other suitable components of electronic devices. The channels within the first oxide layer may be positioned proximate to the surface features, such as above the surface feature (with the second oxide layer positioned between the first oxide layer and a metal surface of the underlying substrate). 
       FIGS.  7 A and  7 B  show scanning electron microscope (SEM) images of cross-sections views of a part having a corrosion-resisting oxide coating, with  FIG.  7 B  showing a higher magnification SEM image. The part in  FIGS.  7 A and  7 B  includes aluminum alloy substrate  702  having edge  703 , which has an oxide coating with first oxide layer  704  (also referred to as an outer oxide layer) formed using a first anodizing process and second oxide layer  708  (also referred to as an inner oxide layer) formed using a compressive stress second anodizing process, as described above. As show, channel  707  formed during the first anodizing process extends at least partially through the thickness of first oxide layer  704  but does not extend through second oxide layer  708 , thereby preventing contaminant from reaching substrate  702 . This is because second oxide layer  708  is formed under compressive stress conditions that prevent channel  707  from forming within or extending through second oxide layer  708 . 
       FIG.  8    illustrates flowchart  800 , indicating a process for forming a corrosion-resisting oxide coating on a part, in accordance with some embodiments. At  802 , a protruding feature is formed on a substrate, such as an aluminum or an aluminum alloy substrate. The protruding feature can correspond to an edge, corner or other outwardly extending feature. The protruding feature can have a curved profile or an angular profile. In a particular embodiment, protruding feature corresponds to a curved edge or corner of an enclosure for an electronic device. The feature can be formed using any suitable technique, including a machining operation, etching operation, molding operation, or suitable combination thereof. It may even be formed by a surface texturing operation such as blasting, chemical etching, laser processing, or laser-marking of a logo or text. 
     At  804 , the substrate is optionally treated prior to an anodizing process. Suitable pretreatments can include etching, polishing and/or abrasive blasting the surface of the substrate that is to be anodized. In some cases the surface of the substrate is polished to achieve a target gloss value. At  806 , a first oxide layer of an oxide coating is formed on the substrate using a first anodizing process. In some applications, the first anodizing process is a Type II anodizing process using an aqueous sulfuric acid electrolyte. The first anodizing process can form a relatively hard first oxide layer (e.g., having a hardness value of at least 350 HV 0.05 ); however, these conditions can cause one or more cracks or channels to form within the first oxide layer over the protruding feature. 
     At  808 , a second oxide layer of the oxide coating is formed adjacent the substrate using a second anodizing process. The second anodizing process is performed under compressive stress conditions, which can involve anodizing using a low current density (e.g., 0.8 A/dm −2 ), low voltage, or high electrolyte temperature. The compressive stress conditions result in the second oxide layer to be softer than the first oxide layer, but also less likely to develop a channel, even over the protruding feature. Thus, the second oxide layer acts as a barrier between the outer environment and the substrate, thereby protecting the substrate from exposure to corrosion-inducing agents. The thickness of the second oxide layer is thin (e.g., between about 0.5 and 2 micrometers) such that the majority thickness of the oxide coating is formed under process conditions which yield a relatively hard coating. 
     At  810 , the oxide coating is optionally colored using one or more coloring processes. In some embodiments, this involves depositing a dye and/or metal material within pores of the oxide coating. In other embodiments, the coloring process is skipped such that the oxide coating is substantially colorless. At  812 , the oxide coating is optionally sealed using, for example, a hydrothermal sealing process that closes the pores within the oxide coating, thereby further increasing the corrosion-resisting properties of the oxide coating. At  814 , the oxide coating is optionally polished using, for example, one or more buffing, lapping or other polishing operations to provide a shine to an exterior surface to the oxide coating. 
       FIGS.  9 A- 9 D  illustrate cross-section views of parts having corrosion-resistant metal oxide coatings, in accordance with some embodiments.  FIG.  9 A  illustrates a cross-section view of a part  900  that includes a metal substrate  902  that is overlaid by a metal oxide coating  910 . As illustrated in  FIG.  9 A , the metal substrate  902  includes a surface feature  906  having a convex geometry. As described herein, the surface feature  906  may protrude from a boundary of the metal substrate  902 . Additionally, due to the surface feature  906 , the metal substrate  902  may be characterized as having a convex polygon shape in which no line segment between two points of a boundary of the polygon shape extends past the polygon shape. Furthermore, all interior angles of the convex polygon shape are less than or equal to 180 degrees. 
     The metal oxide coating  910  includes a first metal oxide coating  904  and a second metal oxide coating  908 . In some embodiments, a portion of the metal substrate  902  is converted to the first metal oxide coating  904  in conjunction with exposing the metal substrate  902  to a first set of electrical parameters. In some embodiments, a portion of the metal substrate  902  is converted to the second metal oxide coating  908  in conjunction with exposing the metal substrate  902  to a second set of electrical parameters that are different than the first set of electrical parameters. In some examples, the first and second set of electrical parameters include at least one of voltage or current density (A/dm 2 ).  FIG.  9 A  further illustrates that the first metal oxide coating  904  includes an interstice  920  that extends at least partially through the first metal oxide coating  904 . As described herein, the interstice  920  is formed by the surface feature  906  generating an effective in-plane tensile strain in the metal oxide coating  910  during the anodizing process. 
       FIG.  9 B  illustrates a magnified cross-sectional view of the part  900 , in accordance with some embodiments. As illustrated in  FIG.  9 B , the part  900  includes a metal oxide coating  910  having a thickness  912  of between about 12 μm to about 20 μm. The metal oxide coating  910  includes a first metal oxide coating  904  and a second metal oxide coating  908 . 
     In some examples, the first metal oxide coating  904  is characterized as having a thickness  914  that is between about 10 μm to about 18 μm. In some examples, the first metal oxide coating  904  has a thickness  914  that is between about 12 μm to about 14 μm. In some examples, the first metal oxide coating  904  is formed under an anodizing process by exposing the metal substrate  902  to an electrolytic solution using a current density of &gt;1.0 A/dm 2 . In some examples, the current density is 2 A/dm 2 &gt;x&gt;1.6 A/dm 2 . In some examples, the electrolytic solution includes at least one of oxalic acid or sulfuric acid. In some examples, the electrolytic solution includes a mixed acid electrolytic solution, where the mixed acid electrolytic solution includes a combination of oxalic acid and sulfuric acid. More particularly, the mixed acid electrolytic solution may include anywhere from ˜10 g/L to ˜60 g/L oxalic acid and ˜5 g/L to ˜40 g/L of sulfuric acid at a temperature range between about 25° C. to about 35° C. In some examples, the mixed acid electrolytic solution includes between about 35-45 g/l oxalic acid and about 15-25 g/l sulfuric acid where a dye is to be subsequently incorporated within the metal oxide coating  910  to impart the metal oxide coating  910  with a color. In some examples, the mixed acid electrolytic solution includes between about 40-60 g/l sulfuric acid and about 10-30 g/l sulfuric acid where the metal oxide coating  910  has a non-transparent color. 
     In some embodiments, the first metal oxide coating  904  is formed under an in-plane tensile stress condition that results in the formation of the interstice  920  that extends at least partially through the first metal oxide coating  904 . It should be noted that the interstice  920  is generally too large to be filled with a sealant. Thus, there is a risk that the interstice  920  will extend into the metal substrate  902  if the part  900  is exposed to additional external contaminants. 
     In some examples, the second metal oxide coating  908  is characterized as having a thickness  918  that is between about 0.2 μm to about 2 μm. In some examples, the second metal oxide coating  908  has a thickness  918  of about 2 μm. In some examples, the second metal oxide coating  908  is formed under an anodizing process by exposing the metal substrate  902  to an electrolytic solution using a current density of &lt;1.0 A/dm 2 . More particularly, the metal substrate  902  may be exposed to the electrolytic solution at a current density of &lt;0.7 A/dm 2  for a duration between about ˜25 minutes to ˜35 minutes. As described herein, the first and second metal oxide coatings  904 ,  908  may be formed using an anodizing bath that includes a single electrolytic solution. In other words, the electrolytic solution is not replaced in conjunction with forming the first and second metal oxide coatings  904 ,  908 . Accordingly, the second metal oxide coating  908  may also be formed using a mixed acid electrolytic solution that includes a combination of oxalic acid and sulfuric acid. 
     In some embodiments, the second metal oxide coating  908  is formed under a compressive stress condition that is linked to reducing the current density for forming the second metal oxide coating  908  relative to the current density for forming the first metal oxide coating  904 . By forming the second metal oxide coating  908  under a compressive stress condition, the second metal oxide coating  908  may cause portions of the interstice  920  to close by pushing metal oxide material (e.g., aluminum oxide, etc.) to fill in portions of the interstice  920 . However, one of ordinary skill in the art would appreciate that the entire metal oxide coating  910  cannot be formed using a low current density (i.e., &lt;0.7 A/dm 2 ) because the low current density results in slow growth of the metal oxide coating. Additionally, the resulting metal oxide coating would have a softness that is not suitable for providing sufficient hardness for protecting operational components that are carried within the enclosure, such as display, circuit boards, etc. Indeed, the formation of the second metal oxide coating  908  is a relatively slow process (e.g., ˜7 minutes to ˜14 minutes, etc.) when one of ordinary skill in the art considers the thickness  918  of the second metal oxide coating  908  relative to a thickness  914  of the first metal oxide coating  904 . Additionally, if the metal oxide coating  910  is grown at too slow of a rate, then the metal oxide coating  910  may suffer from erosion during the anodizing process. Thus, to compensate for the slow growth of the second metal oxide coating  908 , the rate at which the first metal oxide coating  908  is formed may be increased to prevent erosion. As a result, the metal oxide coating  910  has a Vickers hardness of at least about 300 Hv 0.05  or greater. 
     According to some embodiments, voltage control for forming the first and second metal oxide coatings  904 ,  908  is between about 15 volts to about 25 volts, respectively. In other embodiments, the voltage control is about 17 to 23 volts, respectively for the first and second metal oxide coatings  904 ,  908 . It should be noted that voltage control can be substituted for current density control. 
     In some embodiments, the metal substrate  902  includes titanium. In using a mixed acid electrolyte, a significant allowance must be made for titanium fixtures as these will draw ˜20%-30% of the applied current. 
     As illustrated in  FIG.  9 B , the first metal oxide coating  904  includes a first set of pores  924 . The second metal oxide coating  908  is distinct from and generally thinner than the first metal oxide coating  904 , and the second metal oxide coating  908  includes a second set of pores  928 . The second set of pores  928  are finer (e.g., shorter, narrower diameter, etc.) than the first set of pores  924  due to processing the second metal oxide coating  908  at a lower current density and under compressive stress conditions. As a result, the second metal oxide coating  908  has a higher density of pores than the first metal oxide coating  904 . In some examples, the difference in average diameters between the first set of pores  924  and the second set of pores  928  is between about 10% to about 20%. For example, the first set of pores  924  may have average diameters between about 45-55 nm and the second set of pores  928  may have average diameters between about 35-45 nm. In some examples, For example, the first set of pores  924  may have average diameters between about 45-50 nm and the second set of pores  928  may have average diameters between about 38-42 nm. 
     In some embodiments, one or more pores of the second set of pores  928  branch into one or more pores of the first set of pores  924  as a result of significantly reducing the current density while forming the second metal oxide coating  908 . As illustrated in  FIG.  9 B , the second set of pores  928  may extend from the first set of pores  924  at branched regions  926 . In some examples, the ratio of the number of the second set of pores  928  to the number of the first set of pores  924  is about 1:1. However, because the second metal oxide coating  908  is thinner than the first metal oxide coating  904 , the second metal oxide coating  908  exhibits a greater density of pores than the first metal oxide coating  904 , as further described with reference to  FIG.  12   . Thus, there is an abrupt shift between the first and second metal oxide coatings  904 ,  908  due to the branching between the first and second set of pores  924 ,  928 . 
       FIG.  9 C  illustrates a cross-sectional view of the part  900 , in accordance with some embodiments. As illustrated in  FIG.  9 C , in some examples, the interstice  920  may extend entirely through the thickness  914  of the first metal oxide coating  904 . As a result, a crack  930  may be formed within the second metal oxide coating  908 . The thickness of the second metal oxide coating  908  prevents the crack  930  from extending into the metal substrate  902 . As a result, the second metal oxide coating  908  imparts up to a 50% improvement in preventing corrosion relative to conventional techniques. Additionally, it should be noted that the crack  930  is so small (e.g., &lt;0.1 μm) such that external contaminants cannot reach the metal substrate  902 . 
       FIG.  10    illustrates a cross-section view of a part having a corrosion-resistant oxide coating, in accordance with some embodiments. In some examples, the part  1000  may correspond to a consumer electronic device, such as device  102 ,  104 ,  106  or  108 .  FIG.  10    shows a portion of part  1000  having a convex-shaped rounded feature  1006 , such as a rounded edge (i.e., having a curved profile), corner or protruding feature. The convex-shaped rounded feature  1006  may also be small features within a textured surface, such as a blast-textured finish, a chemically etched surface, a laser-textured or laser marked finish, which exhibit roughness with features having convex radii. 
       FIG.  10    shows a first oxide layer  1004  that overlays a metal substrate  1002  having a rounded feature  1006 . Additionally, a second oxide layer  1008  is disposed between the metal substrate  1002  and the first oxide layer  1004 . The first oxide layer  1004  includes an external surface  1034  that corresponds to an exterior surface of an enclosure.  FIG.  10    shows first oxide layer  1004  has an interstice  1020 -A and interstice  1020 -B that extend through the first oxide layer  1004  and reach a surface  1038  of a second oxide layer  1008 . The interstices  1020 -A, B may be formed in the first oxide layer  1004  during the first anodizing process due, in part, to tensile strain at rounded feature  1006 . The width (X 1 ) of the interstice  1020 -A and the width (X 2 ) of the interstice  1020 -B will depend on conditions of the first anodizing process and the radius of curvature of rounded feature  1006 . 
     In some examples, the widths (X 1 ) and (X 2 ) of the interstices  1020 -A, B are different from each other. In some examples, the widths (X 1 ) and (X 2 ) of the interstices  1020 -A, B are between about 1 micrometer to about 5 micrometers. In some examples, the interstices  1020 -A, B extend through partially or the entire thickness (W 1 ) of the first oxide layer  1004 . However, the interstices  1020 -A, B are not illustrated as penetrating the thickness (W 2 ) of the second oxide layer  1008 . This is because second oxide layer  1008  was formed using the second anodizing process under conditions which generate compressive stresses in the oxide film, counteracting and resisting the effective lateral growth strain induced by film growth on the rounded feature  1006 . In some cases, interstices  1020 -A, B only partially enter the second oxide layer  1008 , but these interstices  1020 -A, B are so small (e.g., &lt;1 micrometer) such that external contaminants are generally unable to reach the underlying metal substrate  1002 . 
     In some examples, the thickness (W 1 ) of the first oxide layer  1004  is about 12±3 micrometers. In other examples, the thickness (W 1 ) of the first oxide layer  1004  is 12 micrometers. In other examples, the thickness (W 2 ) of the second oxide layer  1008  is about 2±1 micrometers. In other examples, the thickness (W 2 ) of the second oxide layer  1008  is 2 micrometers. 
       FIG.  11    illustrates a flowchart  1100  for forming a corrosion-resistant oxide coating on a part, in accordance with some embodiments. At step  1102 , a surface feature  906  is formed on the metal substrate  902 , such as an aluminum or an aluminum alloy substrate. The surface feature  906  can correspond to an edge, corner or other outwardly extending feature. The surface feature  906  can have a curved profile or an angular profile. The surface feature  906  may be formed using any suitable technique, including a machining operation, etching operation, molding operation, or suitable combination thereof. It may even be formed by a surface texturing operation such as blasting, chemical etching, laser processing, or laser-marking of a logo or text. 
     At step  1104 , the metal substrate  902  is optionally treated prior to an anodizing process. Suitable pretreatments can include etching, polishing and/or abrasive blasting the surface of the metal substrate  902  that is to be anodized. In some cases the surface of the metal substrate  902  is polished to achieve a target gloss value. 
     At step  1106 , a first metal oxide coating  904  is formed from the metal substrate  902  by exposing the metal substrate  902  to an electrolytic acid solution using a first electrical parameter. In some examples, the first electrical parameter is a voltage or a current density. In particular, the voltage is between about 18-22 volts, whereas the current density is &gt;1.0 A/dm 2 . Additionally, the first metal oxide coating  904  is formed under a tensile stress condition. The electrolytic acid solution may be a mixed acid electrolyte that includes a combination of oxalic acid and sulfuric acid. The metal oxide coating  904  (e.g., having a hardness value of at least 350 HV 0.05 ); however, these conditions can cause one or more cracks or interstice  920  to form within the first metal oxide coating  904  over the surface feature  906 . 
     At step  1108 , a second metal oxide coating  908  of the metal oxide coating  910  is formed between the metal substrate  902  and the first metal oxide coating  904 . The second metal oxide coating  908  is performed under compressive stress conditions while anodizing using a low current density (e.g., &lt;0.7 A/dm 2 ), low voltage, or high electrolyte temperature. In some embodiments, the first and second metal oxide coatings  904 ,  908  are anodized under a voltage step anodization process. The voltage step anodization refers to reducing the current density or voltage control in conjunction with forming the second metal oxide coating  908 . In some embodiments, the second metal oxide coating  908  is anodized using a mixed acid electrolyte. In some examples, the same mixed acid electrolyte is used to form the first and second metal oxide coatings  904 ,  908 . In some embodiments, a programmable rectifier controller, capable of multiple process segments and timed ramps is used. The current and voltage specification of the rectifier must be suitable for processing the load under the conditions described herein. 
     The compressive stress conditions result in the second metal oxide coating  908  to be softer than the first metal oxide coating  904 , but also less likely to develop an interstice—e.g., the interstice  920 . Thus, the second metal oxide coating  908  acts as a barrier between the outer environment and the substrate, thereby protecting the metal substrate  902  from exposure to corrosion-inducing agents. 
     At step  1110 , the metal oxide coating  910  is optionally colored using one or more coloring processes. In some embodiments, this involves depositing a dye and/or metal material within at least one of the first or second set of pores  914 ,  918  of the metal oxide coating  910 . 
     At  1112 , the metal oxide coating  910  is optionally sealed using, for example, a hydrothermal sealing process that closes the first and second set of pores  914 ,  918  within the metal oxide coating  910 , thereby further increasing the corrosion-resisting properties of the oxide coating. At step  1014 , the metal oxide coating  910  is optionally polished using, for example, one or more buffing, lapping or other polishing operations to provide a shine to an exterior surface to the metal oxide coating  910 . 
       FIGS.  12 A- 12 D  illustrate comparisons between parts formed with conventional anodization and voltage step anodization, in accordance with some embodiments. As described herein, the voltage step anodization refers to forming the first metal oxide coating—e.g., the first metal oxide coating  904  at a current density &gt;1.0 A/dm 2 , and forming the second metal oxide coating—e.g., the second metal oxide coating  908  at a reduced current density &lt;0.7 A/dm 2 . 
     As illustrated in  FIGS.  12 A- 12 D , different parts were tested for corrosion resistance based on immersion to sweat. In particular, the parts were compared to a threshold value for one or more structural and/or cosmetic characteristics (e.g., surface finish, structural rigidity, hardness, color, etc.). The parts anodized using the voltage step process exhibited significant improvement in corrosion resistance ˜up to 50% improvement in preventing corrosion relative to conventional anodizing processes. The parts were tested under simulated accelerated aging tests as indicated by Time 0, Time 1, Time 2, Time 3, and Time 4.  FIGS.  12 A- 12 D  illustrate the (a) percentage of parts that were anodized using voltage step anodization that did not satisfy a threshold level for the one or more structural and/or cosmetic characteristics, and (b) percentage of parts that were anodized using conventional anodization processes that did not satisfy a threshold level for the one or more structural and/or cosmetic characteristics. As illustrated in  FIGS.  12 A- 12 D , a significant percentage of the parts anodized using the voltage step process satisfies the threshold. 
       FIG.  13    illustrates an electron microscope image of the part as formed using the techniques described herein, in accordance with some embodiments. As illustrated in  FIG.  13   , the second metal oxide coating  1308  exhibits a greater density of pores than the first metal oxide coating  1304 , which is indicated by the second metal oxide coating  1308  imaging darker than the first metal oxide coating  1304 . In some examples, first metal oxide coating  1304  has a thickness (W 1 ), the second metal oxide coating  1308  has a thickness (W 2 ), and the part has an overall thickness (W t ). 
     In some examples, the thickness (W 1 ) of the first oxide coating  1304  is about 12±3 micrometers. In some examples, the thickness (W 2 ) of the second oxide coating  1308  is about 2±1 micrometers. In some examples, the thickness (W t ) of the oxide coating that includes the first and second oxide coatings is 15±3 micrometers. 
     The foregoing description, for purposes of explanation, uses specific nomenclature to provide a thorough understanding of the described embodiments. However, it will be apparent to one skilled in the art that the specific details are not required in order to practice the described embodiments. Thus, the foregoing descriptions of the specific embodiments described herein are presented for purposes of illustration and description. They are not intended to be exhaustive or to limit the embodiments to the precise forms disclosed. It will be apparent to one of ordinary skill in the art that many modifications and variations are possible in view of the above teachings.

Metadata:
Filing Date: 20190215
Publication Date: 20230110
Grant Date: 20230110
Priority Date: 20180910
Inventors: CURRAN, JAMES A.
FEINBERG, ZECHARIAH D.
POSTAK, Sonja R.
Assignee: APPLE INC
CPC Classifications: [{"code": "C25D11/12", "inventive": true, "first": true, "tree": "[]"}, {"code": "C25D11/02", "inventive": true, "first": true, "tree": "[]"}, {"code": "C25D11/18", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/08", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/02", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/02", "inventive": true, "first": true, "tree": "[]"}, {"code": "H04M1/0202", "inventive": true, "first": false, "tree": "[]"}, {"code": "H04M1/0283", "inventive": false, "first": false, "tree": "[]"}, {"code": "C25D11/243", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/16", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/10", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/12", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/08", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/18", "inventive": true, "first": false, "tree": "[]"}, {"code": "H04M1/18", "inventive": false, "first": false, "tree": "[]"}, {"code": "C25D11/246", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/18", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/08", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/12", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/02", "inventive": true, "first": true, "tree": "[]"}, {"code": "C25D11/16", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/246", "inventive": true, "first": false, "tree": "[]"}, {"code": "C25D11/243", "inventive": true, "first": false, "tree": "[]"}]
Family ID: 67902358