PRODUCTS SECTORS PROFILE CAREER NEWS Heat-to-coat process from Wuppermann saves 31 % CO2 The Wuppermann Group has commissioned the Fraunhofer Institute for Environmental, Safety and Energy Technology (UMSICHT) to investigate the environmental impact of the Wuppermann Group's "Heat to coat" strip galvanizing process and compare it with the conventional cold-rolled galvanizing process. The result makes it clear that whereever applications for galvanized hot strip and galvanized cold strip overlap, the Wuppermann process has an advantage in terms of CO2 balance. Fraunhofer Umsicht has drawn up a life cycle assessment in accordance with DIN EN ISO 14040 and evaluated the environmental effects as climate effectiveness in CO2 equivalents per kg (CO2-eq./kg ) of hot-dip galvanized steel strip. The following picture emerges when the Wuppermann production sites for the flat products segment are considered in detail: The galvanizing processes including after-treatment cause 31% lower CO2 emissions at the Moerdijk (NL) site (0.126 kg CO2 eq/kg) and 43 % lower CO2 emissions at the Judenburg (AT) site (0.105 kg CO2 eq/kg) than the reference process with 0.183 kg CO2 eq/kg. The CO2 emissions for pickling due to the integrated process at Wuppermann have already been taken into account. Not included in this so-called gate-to-gate consideration is the environmental impact of the starting material hot strip. Wuppermann Process at the Moerdijk and Judenburg sites saves around 40,000 tons of CO2 per year With an annual galvanizing volume of approximately 600,000 tons, this results in CO2 savings of 34,200 tons at the Moerdijk site. In Judenburg, the savings are 4,680 tons with a galvanizing capacity of approximately 60,000 tons. The largest value driver in the CO2 balance is energy consumption. The energy source is therefore of great importance. This is also shown by the comparison of the two sites. The WSN calculations are based primarily on electricity generated from fossil fuels in the Netherlands. The WA calculation is primarily based on ecologically generated Austrian electricity. This is also the reason for the significantly better environmental balance of the galvanized steel strip from Judenburg compared to Moerdijk. Why is the galvanizing process from Wuppermann more CO2-friendly than the market standard? The galvanizing process used at Wuppermann offers process-related advantages with regard to the ecological balance. The usual cold strip galvanizing process requires the steel strip to be annealed to a temperature of 750° C in a large annealing furnace, which is fired with natural gas or metallurgical gas. Its combustion product is CO2, which is released into the atmosphere. The strip must then be cooled down to the galvanizing temperature. The Wuppermann heat-to-coat process uses a small, inductively (electrically) heated strip heating furnace which heats the steel strip to the galvanizing temperature of 460 - 480° C in seconds. The energy-intensive recrystallization annealing at approx. 750° C is no longer necessary. Methodology of the study "Environmental impact of the strip galvanizing process Heat to coat of the Wuppermann Group” The Fraunhofer UMSICHT Institute was commissioned to draw up a greenhouse gas balance for the strip galvanizing process of the Wuppermann Group and to compare it with the cold strip galvanizing process commonly used on the market. The investigation was based on a life cycle assessment or life cycle analysis according to DIN EN ISO 14040. This provides the framework for assessing the potential environmental impact of a product system over its entire life cycle. The process is divided into four phases: Definition of the objective and scope of the study, Life Cycle Inventory, impact assessment and evaluation. It provides an opportunity to record all relevant potential impacts (with a focus on greenhouse gas emissions) on the environmental media. This climate impact is expressed in kg CO2 equivalents per kg (CO2-eq./kg) of hot-dip galvanized steel strip. The environmental impact of all other greenhouse gas emissions, e.g. methane, is converted via a standardized value into a value comparable to CO2. In order to be able to assess the total environmental impact caused by the production of one kilogram of hot-dip galvanized steel strip with ø Z214 (zinc coating 214 g/m2) or ø Z558 (zinc coating 558 g/m2), a system room extension is required. The concrete life cycle assessment therefore includes not only the primary data of the galvanizing process itself, but also secondary data of downstream or upstream processes. These primarily include the production of zinc, the provision of electricity and the transport of raw materials to the plants. For the reference process, publicly available data records were used for the production of hot strip, for the production of cold-rolled steel strip, and for the production of galvanized sheet by means of cold-rolled galvanizing. The latter refers to material with a zinc coating thickness of 275 g/m2. In order to be able to reference against the zinc layer thickness Z275 in the cold strip galvanizing process, the average zinc layer thickness for WSN (Z214) and WA (Z558) was corrected accordingly in the comparative calculation. The present LCA is primarily a so-called gate-to-gate consideration. The system boundary is quasi defined by the "factory gate". The focus is on the environmental impact caused by the galvanizing process. Only the minor CO2 input caused by the hot strip transport to the plants is included in the calculation. Since the heat-to-coat process at Wuppermann runs via a combined pickling & galvanizing plant, pickling is also included in the LCA. This is not the case with the reference process, as pickling takes place in a separate step before cold rolling. In a direct comparison of processes, the LCA of Wuppermann is thus additionally burdened by the environmental impact of pickling, i.e. it is presented somewhat too negative. If the system boundary of the reference process is extended to all process steps that take place between the completion of the hot strip and the finished galvanized steel strip, the advantage of the Wuppermann process even increases to 48 % in the case of the Dutch site and to 56 % in the case of production in Judenburg, Austria. More information you can find here. The complete study can be found here. The Wuppermann AG press release on the study can be found here. Contact Wuppermann AG Ottostraße 5 51381 Leverkusen Germany +49 (0) 21 71 50 00 800 +49 (0) 21 71 50 00 802 info(at)wuppermann.com General Information Imprint Data Protection Legal Sitemap Print page Downloads Annual Reports Product Portfolio Brochures Certificates GTCs