MyPaulo Careers Contact Us Locations Search for: CAPABILITIES MARKETS + PROJECTS DATAGINEERING LEARNING CENTER ABOUT US GET A QUOTE CAPABILITIES > HEAT TREATING > AUSTEMPERING AUSTEMPERING Achieve superior toughness while minimizing distortion. Related View All White Paper Heat treating: Best Handled In-House or Outsourced? White Paper Heat Treating 101: An Introduction to Heat Treating Procedures Case Study Case study: Unconventional treatment improves quality of constant tension bands We Help Your Parts Withstand the Toughest Applications When workpieces require added hardness, higher impact and fatigue strength, increased ductility, resistance to embrittlement, and higher wear resistance, Paulo’s state-of-the-art austempering process ensures your parts are finished to specification with minimal distortion. How Austempering Works In austempering, parts are first heated in continuous belt furnaces or salt baths to temperatures as high as 1,650°F, depending on the material. The carbon atoms that add hardness to a part cannot dissolve into it unless a part is austenitized, causing a transformation of the part’s crystal structure. After heating, parts are quenched in a bath of molten salt. While this temperature varies depending on the part’s makeup and its desired finished hardness, it is generally done at around 600°F. This delivers added strength and ductility to the part. The part is held at this temperature until bainite forms. Bainite refers to the microstructure that is created by the austempering process. Austempering can take as little as ten minutes or as long as an hour and a half depending on how a part’s makeup affects bainite formation. The quench-and-hold at higher temperatures for the hardening in austempering greatly minimizes the risk that parts will distort compared to quenching in oil. That’s because cooling parts at elevated temperatures rather than at lower temperatures significantly slows cooling. Slower cooling means parts encounter less stress due to thermal expansion and contraction and less stress from transformation. The process concludes by final cooling of the part in open air at room temperature. Final tempering of austempered parts is usually not required because the part’s desired hardness can be achieved via the temperature of the salt bath quench that follows heating. However, some austempered parts, do require subsequent tempering because parts emerge from quenches harder than the specification calls for. Benefits of Austempering Pieces treated by austempering are ideal for use as components of systems under frequent stress, such as springs, clips and seat belt loops in cars, agricultural components, lawn mower blades, mining, oil, and gas components, and other applications where toughness is a chief concern. Parts that are austempered feature: Greater ductility Uniform hardness Higher impact and fatigue strengths Wear resistance Resistance to hydrogen embrittlement Materials for Austempering Austempering delivers the highest ductility available for steels in the mid- to upper-40s on the HRC hardness scale. Steels with medium amounts of carbon and higher alloy levels, including thicker parts made of steels like 4140, 4150, 5160 and 6150 and thinner parts made of steels from between 1050 and 1095, usually respond best to austempering. Austempering Capabilities Our multi-furnace capabilities offer both continuous belt and vertical bath setups to accommodate a broad range of parts and volumes. Because our facilities have redundant capabilities and capacity, we’ll meet any order on deadline, no matter what. The continuous mesh belt austemper in our Murfreesboro Division is capable of treating 3,000 pounds of parts per hour with a maximum temperature of 1,650 degrees Fahrenheit. Murfreesboro’s salt quench bath temperature ranges from 585 to 680 degrees. The salt bath and salt quench in our Kansas City Division has dimensions of 16” x 32” x 58” with maximum temperature of 1,650 degrees and a quenching range of 300 to 900 degrees. Computer-controlled loading, processing and tracking systems are used at all Paulo facilities. Markets ATV Automotive Construction Firearms Hand Tools Mining Recreational Vehicle Equipment Continuous Austemper Furnace (Salt Quench) Salt Pot Furnace Methods of Manufacturing Casting Forging Stamping Materials High Carbon Steels Iron Medium Carbon Steels Locations Kansas City Division Murfreesboro Division Trust Your Parts to Paulo Need austempering services for your next project? We can provide precise, accurate results. Bring us your challenges, and let’s solve them together. START YOUR QUOTE Subscribe to our emails to receive updates on new content, promotions, and more. Email Address 5711 West Park Ave St. Louis, MO 63110 Phone: (314) 647-7500 Fax: (314) 647-7518 About Paulo Contact Us Locations Careers Certifications & Approvals News Services Heat Treating Brazing Metal Finishing Resources Request A Quote © Paulo 2021 Terms & Conditions Privacy Policy Site Map Notice We and selected third parties use cookies or similar technologies for technical purposes and, with your consent, for other purposes as specified in the cookie policy. You can consent to the use of such technologies by closing this notice, by scrolling this page, by interacting with any link or button outside of this notice or by continuing to browse otherwise. Learn more and customize Accept ×