About us Products Contact You are here: Home Products Performance Materials Hydrogenated Petroleum Resin Hydrogenated Petroleum Resin - I-MARV I-MARV is Idemitsu's groundbreaking tackifier resin. It has proven excellent for hot-melt and pressure sensitive adhesives, and functions as a polyolefin resin modifier. I-MARV is extremely transparent, has excellent thermal stability and no odor. It also boasts excellent compatibility with base resins and elastomers. Exclusively created based on polymerization and hydrogenation technologies developed by Idemitsu over decades of research. I-MARV displays a balanced performance in terms of heat and cold resistance as well as adhesive properties as a tackifier when used as a hot-melt adhesive. Because is also compatible with polypropylene, its transparency, rigidity, and vapor barrier characteristics are improved when added to a bipolar oriented or BOPP film. We gathered the above information referring to CMC Publishing Co., Ltd. I-MARV is available in partially hydrogenated S-grades, fully hydrogenated P-grades and intermediate type Y-grades. Because they are so broadly applicable, a wide selection of specific S- and P-grades are available to suit individual customer needs and applications. Typical Properties S-100 S-110 P-100 P-125 P-140 Test method Softening point (°F) 212 230 212 257 284 JIS K2207 Average molecular weight 700 760 660 820 900 VPO Density (g/cm3 at 68 F) 1.05 1.05 1.03 1.03 1.03 JIS K0061 Color (Harzen) 25 25 10 20 20 JIS K6901 Bromine number (g/100 g) 5.0 6.0 2.5 2.5 2.0 JIS K2605 Compatibility After Melting and Mixing at Room Temperature Material/Grade S-100 S-110 P-100 25% 50% 75% 25% 50% 75% 25% 50% 75% Linseed oil - C - - C - - C - Soybean oil - C - - C - - C - Alkyd resin (short oil type) - C - - C - - C - Alkyd resin (medium oil type) - C - - C - - C - 100% phenol resin - C - - C - - C - Alkyd resin (medium oil type) - C - - C - - C - 100% phenol resin - C - - C - - C - Epoxy resin - I - - I - - I - Terpene resin - C - - C - - C - Rosin - C - - C - - C - Terpene phenol formamide resin - I - - I - - I - Vaseline - I - - I - - I - Fatty acids - C - - C - - C - Polyethylene* P P P P P P C C C Polypropylene* P P P P P P C C C Polybutene C C C C C C C C C Liquid polybutadiene I I I I I I I I I Material/Grade P-125 P-140 25% 50% 75% 25% 50% 75% Linseed oil - C - - C - Soybean oil - C - - C - Alkyd resin (short oil type) - C - - C - Alkyd resin (medium oil type) - C - - C - 100% phenol resin - C - - C - Epoxy resin - I - - I - Terpene resin - C - - C - Rosin - C - - C - Terpene phenol formamide resin - I - - I - Vaseline - I - - I - Fatty acids - C - - C - Polyethylene* C C C C C C Polypropylene* C C C C C C Polybutene C C C C C C Liquid polybutadiene I I I I I I C: Compatible; P: Partially compatible; I: Incompatible * Based on the level of transparency in a film state. Compatibility at 180°C After Melting and Mixing Material/Grade S-100 S-110 P-100 25% 50% 75% 25% 50% 75% 25% 50% 75% Vaseline - C - - C - - C - Fatty acids - C - - C - - C - Epoxy resin - I - - I - - I - Polybutene C C C C C C C C C Liquid polybutadiene C C C C C C C C C Paraffin wax C C C C C C C C C Microcrystalline wax C C C C C C C C C EVA C C C C C C C C C Material/Grade P-125 P-140 25% 50% 75% 25% 50% 75% Vaseline - C - - C - Fatty acids - C - - C - Epoxy resin - I - - I - Polybutene C C C C C C Liquid polybutadiene C C C C C C Paraffin wax C C C C C C Microcrystalline wax C C C C C C EVA C C C C C C C: Compatible; I: Incompatible Film State Compatibility*1 Material/Grade S-100 S-110 P-100 25% 50% 75% 25% 50% 75% 25% 50% 75% NR C C C C C C C C C BR C C C C C C C C C CR C C C C C C C C C EPDM C C C C C C C C C EVA C C C C C C C C C SBS C C C C C C C C P SIS C C C C C C C C C SEBS C C C C C C C C P Material/Grade P-125 P-140 25% 50% 75% 25% 50% 75% NR C C C C C C BR C C C C C C CR C C P C C P EPDM C C C C C C EVA C C C C C C SBS C C P C C P SIS C C C C C C SEBS C C P C C P C: Compatible; P: Partially Compatible; I: Incompatible *1 EPDM rubber blend samples were dissolved for 1 hour at 90°C. After dissolving both substances in toluene, the solution was applied on a PET film and the solvent was evaporated at room temperature. The transparency was then observed visually using a bar coater. Solubility*1 Solvent/Grade S-100 S-110 P-100 20% 50% 20% 50% 20% 50% Hydrocarbons - - - - - - Benzene S S S S S S Toluene S S S S S S Xylene S S S S S S n-hexane S S S S S S Cyclohexane S S S S S S Mineral spirits S S S S S S Alcohols - - - - - - Ethanol I I I I I I Isopropyl alcohol I I I I I I 1-butanol I I I I I I 1-octanol I I I I I I Ketones - - - - - - Acetones I I I I I I Methyl ethyl ketone I I I I I I Chlorine compounds - - - - - - Carbon tetrachloride S S S S S S Ethers - - - - - - Ethyl ether S S S S S S Dioxane S S S S S S Esters - - - - - - Ethyl acetate I I I I I I Nitrogen compounds - - - - - - n,n-dimethylformamide I I I I I I Pyridine S S S S I I Aniline I I I I I I Solvent/Grade P-125 P-140 20% 50% 20% 50% Hydrocarbons - - - - Benzene S S S S Toluene S S S S Xylene S S S S n-hexane S S S S Cyclohexane S S S S Mineral spirits S S S S Alcohols - - - - Ethanol I I I I Isopropyl alcohol I I I I 1-butanol I I I I 1-octanol I I I I Ketones - - - - Acetones I I I I Methyl ethyl ketone I I I I Chlorine compounds - - - - Carbon tetrachloride S S S S Ethers - - - - Ethyl ether S S S S Dioxane S S S S Esters - - - - Ethyl acetate I I I I Nitrogen compounds - - - - n,n-dimethylformamide I I I I Pyridine I I I I Aniline I I I I S: Soluble; I: Insoluble *1 The transparency at room temperature was measured after preparing the solution at the above percentages. Molten Viscosity Toluene Solution Viscosity Heat Resistance Aging Color Grade/Aging Time 0 hr 12 hr 24 hr 48 hr 72 hr 96 hr S-100 G1> G1> G1> G2 G4 G5 P-100 H10 H50 H120 H200 G3 G4 P-125 H20 H80 H130 H240 G3 G4 G: Gardner color, H: Harzen color * Test conditions: A sample of 1.5 g was placed in an aluminum foil container was used 10 mm in diameter and 20 mm high. Testing was carried out at 180°C in an open cup exposed to the air. Heating loss Sample applications Tackifier for hot melt adhesives Tackifier for pressure sensitive adhesives Polyolefin resin modifier Rubber compounding ingredient Packaging Net 25-kg paper bag Net 500-kg flexible container For more Information, please visit our website: http://www.idemitsu.com/products/petrochemicals/chemicals/index.html * N.B. The data shown above was measured under specific conditions and has been verified for accuracy. Nevertheless, results in applications may differ depending on use and products may not perform for all recommended uses depending on use conditions. The content above is subject to change without notice. Figures of physical characteristics of other resins than the products have been referred from other catalogues and sources thereof. * I-MARV is trademarks registerd in Japan under the name of Idemitsu Kosan Co.,Ltd. I-MARV Data Sheets - I-MARV P-100 - english deutsch I-MARV P-125 - english deutsch I-MARV P-140 - english deutsch I-MARV S-100 - english deutsch Related Links Performance Materials L-MODU Alfa Olefin Hydrogenated Petroleum Resin Isoparaffin Solvents Engineering Plastics Contact Us © 2018 Idemitsu Chemicals Europe GmbH. All rights reserved. About usImprintPrivacy PolicySitemapContact Top