GET IN TOUCH PROJECTS PRODUCTS ENHANCEMENTS ABOUT US LOGISTICS Heat Treatments HEAT TREATED GLASS… FOR SAFER BREAKING PATTERNS AND STRONGER GLASS TOP-TIER TECHNOLOGY Since 1972, Rochester Insulated glass has been providing heat-treated glass throughout the world. Both of our furnaces allow RIG to increase capacity in production and continually provide some of the largest glass in North America. LET US HELP YOU MEET YOUR SAFETY REQUIREMENTS THROUGH OUR EXPERTISE IN: HEAT STRENGTHENING FULLY TEMPERING HEAT SOAKING THIS IS HOW HEAT TEMPERING WORKS Once the glass heated to the required temperature, it is then quickly cooled on both sides, simultaneously. The quick cooling process creates a state of high compression at the glass surface while the core of the glass is in compensating tension. ANNEALED GLASS VS. HEAT TREATED GLASS Annealed Glass • Annealed is the purest form of float glass. • Used if you are seeking limited roller wave distortion. Ie. Air traffic towers. • If broken, annealed glass separates into large shards like a broken mirror. • Not considered safety glass. Heat Treated Glass • Fully tempered glass is 4X stronger than annealed. • Heat strengthened glass is 2X’s stronger than annealed. • The small, roughly cubical pieces created in breakage qualify tempered glass as a safety glazing material. • Fully tempered glass is considered safety glass. When used in a lamination application, both heat treated and annealed glass will remain within their structure if broken; therefore meeting a higher safety standard. Fully Tempered glass complies with safety glazing requirements as outlined by American National Standards Institute (ANSI) Z97.1 and the federal safety standard Consumer Products Safety Commission (CPSC) 16 CFR 1201. TOP QUALITY - IN EVERY LITE Heat-treating can cause slight wave distortion, bowing or warping. Therefore, to ensure each lite of glass meets our rigorous standards, glass goes directly from the tempering furnace through our state of the art LiteSentry distortion inspection scanner. HEAT SOAKING WHAT IS SPONTANEOUS BREAKAGE? There are instances, after installation, of tempered glass breaking due to no apparent cause. In relatively rare instances, breakage has been traced to the presence of nickel sulphide stones in the center tension zone of the tempered glass. RIG OFFERS A SOLUTION To prevent nickel sulphide inclusions, RIG utilizes a Jumbo European heat-soaking furnace to achieve a “break now, not later” result, based on the assumption that any glass lites with nickel sulphide inclusions will break during the heat soak process. HERE'S HOW IT WORKS Nickel sulphide stones can manifest in the production of float glass. Therefore, they can be present in annealed, heat strengthened and tempered glass. During the heat strengthening or heat tempering process, the stone size can increase 2-4% causing stress on the glass and increasing probability of future breakage. A typical heat soak process elevates the glass temperature to 550 degrees F (290oC) for two hours. [BS EN 14179-1 standard]. If there are nickel sulphide stones present, theoretically the glass should break in the heat-soaking furnace and not during installation or use. THE SPECIFICS WE HELP CREATE SOLUTIONS GET IN TOUCH ABOUT US PROJECTS PRODUCTS Monolithic Insulated Laminated Oversized ENHANCEMENTS Digital In-Glass Print Heat Treatments Interlayers Fabrication Spandrel Spacers RESOURCES Contact us FAQ Logistics Our Documents Careers We would love to hear from you! Contact us for sales requests, career information, or general questions. 800-732-0400 585-289-3611 Connect with us on social! RELENTLESS PURSUIT OF QUALITY AND INNOVATION © Copyright 2021 Rochester Insulated Glass, Inc. All Rights Reserved.