Silver oxide battery. A silver oxide battery (IEC code: S) is a primary cell using silver oxide as the cathode material and zinc for the anode. These cells maintain a nearly constant nominal voltage during discharge until fully depleted. They are available in small sizes as button cells, where the amount of silver used is minimal and not a prohibitively expensive contributor to the overall product cost.

Silver oxide primary batteries account for 30% of all primary battery sales in Japan (64 mil. out of 212 million in February 2020).

History 
A silver oxide cell was first constructed by Alessandro Volta in late 1800. This consisted of a circle of cups of a liquid saline electrolyte, containing alternating zinc and silver strips connected by wire. It is claimed that 20 such cups were sufficient for the hydrolysis of water.

Large silver oxide batteries were used on early ICBM's and satellites because of their high energy-to-weight ratio. For example the Corona reconnaissance satellites used them, as did the Agena-D rocket upper stage. Later, they were also used in the Apollo Lunar Module and lunar rover.

Specifications 

 Cell voltage
 Open circuit voltage = 1.6 V
 Working voltage = 1.2~1.5 V
 Energy density = 130 Wh/kg (60 Wh/lb)
 Service life of several thousand hours (continuous operation)
 Shelf stable over several years (retaining 90% of initial capacity)

Silver oxide cells are a primary battery and do not have a cycle life or a rate of charging and discharging.

Typical silver oxide cells are stable at temperatures below 100°C, at which point leakage can occur.

Chemistry
A silver oxide battery uses silver(I) oxide as the positive electrode (cathode), zinc as the negative electrode (anode), plus an alkaline electrolyte, usually sodium hydroxide (NaOH) or potassium hydroxide (KOH). The silver is reduced at the cathode from Ag(I) to Ag, and the zinc is oxidized from Zn to Zn(II). 

The half-cell reaction at the positive plate:
 Ag2O + H2O + 2e- ->  2Ag (v) + 2OH-, 

The half-cell reaction at the negative plate:
 {Zn} + 2OH^- -> \overset{Zinc~hydroxide}{Zn(OH)2} + 2e-,   

Overall reaction:  
 Zn + H2O + Ag2O -> Zn(OH)2 + 2Ag(v), 

Overall reaction (anhydrous form):
 Zn + Ag2O ->[\ce{KOH/NaOH}] ZnO + 2Ag (v)

Construction 

In order to reduce the cost of manufacture, most commercially available silver oxide cells take the form of button cells with relatively low silver content. These button cells generally follow the same compact design. The bottom portion of the cell is the cathode, which consists of a graphite infused silver oxide. A plastic membrane separates this from an anode of powdered zinc dissolved in an alkaline electrolyte. An insulating gasket keeps the two contacts apart, facilitating the discharge of the cell.

Mercury content

Until 2004, all silver oxide batteries contained up to 0.2% mercury, incorporated into the zinc anode to inhibit corrosion from the alkaline environment. This corrosion would occur regardless of whether or not the battery was providing power, making shelf life an important consideration with silver oxide batteries. Sony started producing the first mercury-free silver oxide batteries in 2004. Regulation in the European Union now dictates that all batteries be virtually mercury-free.

Other safety concerns with silver oxide cells stem from their small size, which often leads to accidental swallowing and poisoning, especially by young children.

See also
 Battery nomenclature
 Battery recycling
 Comparison of battery types
 Fuel cell
 History of the battery
 List of battery sizes
 List of battery types

References

External links

 SR (Silver Oxide Battery) from Maxell

Disposable batteries