Materials Testing Results - Case Construction Materials

==Case Construction Materials==
This table includes construction, packing, and storage materials.
Material Name 	Manufacturer 	Supplier 	Test Results 	Date tested yyyy/mm/dd	Tester 	Test(s) Used 	Description/ Composition 	Comments 	Material Type 	Results Image or Description
Styrofoam™ Brand Scoreboard XPS Foam Insulation 	Dupont 	LeNoble Lumber 	Temporary 	2022/06/30 	MMA 	Oddy Test (method: 20211201_OT ) 	Blue; extruded polystyrene foam insulation board that is scored longitudinally on 16 inch and 24 inch centers; high resistance to water and water vapor, high compressive strength and durability; contains: polystyrene; 2 inches thick, 4 x 8 foot boards, R-value: 10; purchased 2019 	 	-Polymer - foam - building insulation 	
Ethafoam® 220 	Sealed Air 	Valentine Packaging 	Temporary 	2022/06/30 	MMA 	Oddy Test (method: 20211201_OT ) 	White; Strong, resilient, medium-density, closed-cell polyethylene foam; 2 inches thick, 2.2 pounds per cubic foot; Purchased December 2021 	 	-Polymer - foam - non-building insulation 	
Variations 4 carpet tile, Linked 14199 	Mannington Mills, Inc 	Mannington Commercial 	FAIL 	2022/06/30 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey; non-patterened looped nylon carpet with solution dyed Antron® Lumena™ Type 6,6 Nylon fibers and Infinity® 2 Modular backing; contains nylon and pre-consumer recycled content; 60.96 x 60.96 cm squares, 2.54 mm pile thickness; Purchased May 2022 	 	-Carpet - Synthetic/plastic/polymeric 	
Variations 4 carpet tile, Wired 12202 	Mannington Mills, Inc 	Mannington Commercial 	FAIL 	2022/06/30 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey; non-patterened looped nylon carpet with solution dyed Antron® Lumena™ Type 6,6 Nylon fibers and Infinity® 2 Modular backing; contains nylon and pre-consumer recycled content; 60.96 x 60.96 cm squares, 2.54 mm pile thickness; Purchased May 2022 	 	-Carpet - Synthetic/plastic/polymeric 	
Variations 4 carpet tile, Disclose 13210 	Mannington Mills, Inc 	Manningon Commercial 	FAIL 	2022/06/30 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey; non-patterened looped nylon carpet with solution dyed Antron® Lumena™ Type 6,6 Nylon fibers and Infinity® 2 Modular backing; contains nylon and pre-consumer recycled content; 60.96 x 60.96 cm squares, 2.54 mm pile thickness; Purchased May 2022 	 	-Carpet - Synthetic/plastic/polymeric 	
CoLibri Cover System®, ECO Book Covers, 01-20 STD12-ECO (green print) 	CoLibri System S.p.A. 	CoLibri USA 	Temporary 	2022/06/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Transparent polymer membrane for book covers with green printing; made from green polyethylene produced from ethanol extracted from sugar cane; 49 x 32 cm, 3.5 mil; Purchased April 2022 	 	-Polymer - membrane (< 1mm thick) 	
CoLibri Cover System® Transparent Book Covers, Crystal Covers, 08-15 STD (blue print) 	CoLibri System S.p.A. 	CoLibri USA 	Temporary 	2022/06/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Transparent polymer membrane for book covers with blue printing; blend of polyester and polyethylene; 49 x 32 cm, 3.5 mil; Purchased April 2022 	 	-Polymer - membrane (< 1mm thick) 	
Ice Breaker 147002500 carpet tile, 105770 Concrete 	Interface 	Consolidated Carpet 	FAIL 	2022/06/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey, tufted textured loop carpet tile; 100% recycled content nylon yarn with Protekt(R) stain treatment, vinyl GlasBac(R) backing; 576 g/m^2 yarn weight, 1.8 mm pile thickness, 319,628 g/m³ pile density, 50 cm x 50 cm tile size; Purchased April 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Tred-Mor® 2568 Carpet Cushion 	Sponge Cushion, Inc 	Consolidated Carpet 	FAIL 	2022/05/13 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey, flat, synthetic carpet padding; contains: synthetic rubber, Poly-Tek backing; 68 oz/yd^2, 22 lbs/ft^3, 0.25 inches thick; Purchased March 2022 	 	-Flooring - non-carpet 	
Ice Breaker 147002500 carpet tile, 105771 Granite 	Interface 	Consolidated Carpet 	FAIL 	2022/05/13 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey, tufted textured loop carpet tile; 100% recycled content nylon yarn with Protekt® stain treatment, vinyl GlasBac® backing; 576 g/m^2 yarn weight, 1.8 mm pile thickness, 319,628 g/m³ pile density, 50 cm x 50 cm tile size; Purchased April 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Harmonize 138720AK00 carpet tile, 104043 Gravel 	Interface 	Consolidated Carpet 	FAIL 	2022/05/13 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey, tufted textured loop carpet tile; 100% recycled content nylon yarn with Protekt® stain treatment, vinyl GlasBac® backing; 542 g/m^2 yearn weight, 2.7 mm pile thickness, 201,492 g/m³ pile density, 25 cm x 1 m tile size; Purchased April 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
LVT Secoya C0009 vinyl floor tile, Benmore 123 	Mohawk Group 	Consolidated Carpet 	Temporary 	2022/04/29 	MMA 	Oddy Test (method: 20211201_OT ) 	Floating luxury vinyl tile with a wood grain pattern; contains: vinyl; 235 mm x 1505 mm, 5 mm thick; Purchased March 2022 	 	-Flooring - non-carpet 	
Attraction floor tile, Plaza 2745 	Gerflor 	Consolidated Carpet 	Temporary 	2022/04/29 	MMA 	Oddy Test (method: 20211201_OT ) 	Interlocking modular floor tiles; Protecsol® surface treatment, 1 mm colored wearlayer, 4 mm recycled backing with double fiberglass grid; contains: vinyl; Purchased March 2022 	 	-Flooring - non-carpet 	
Attraction floor tile, Recife 8735 	Gerflor 	Consolidated Carpet 	Temporary 	2022/04/29 	MMA 	Oddy Test (method: 20211201_OT ) 	Interlocking modular floor tiles; Protecsol® surface treatment, 1 mm colored wearlayer, 4 mm recycled backing with double fiberglass grid; contains: vinyl; Purchased March 2022 	 	-Flooring - non-carpet 	
GTI Max vinyl floor tile, Glear Grey 0234 	Geflor 	Consolidated Carpet 	Temporary 	2022/04/29 	MMA 	Oddy Test (method: 20211201_OT ) 	Multilayered, interlocking looselay vinyl tile; 2 mm thick colored wearlayer with oblong fibers reinforced with an interlayer and multiple fiberglass grids on both sides on a 2 mm vinyl sheet backing; contains vinyl, polyurethane; 6 mm total thickness; Purchased March 2022 	 	-Flooring - non-carpet 	
Natural Woodgrains LVT floor tile, Cedar A00212 	Interface 	Consolidated Carpet 	Temporary 	2022/04/29 	MMA 	Oddy Test (method: 20211201_OT ) 	High performance luxury vinyl plank with cedar wood pattern; contains: vinyl; 4.5mm thick; Purchased March 2022 	 	-Flooring - non-carpet 	
Structure Broadloom Carpet, 20100/1805 Joist 	J&J Flooring 	J&J Flooring 	Temporary 	2022/03/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey; Textured loop carpet; PremierBac® backing, Encore® SD Ultima® (with recycled content) nylon fibers; 678 g/m^2, 201.76 kg/m^3, 3.94 rows/cm, 3.66 m, 0.218 inch total thickness; purchased February 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Tempo Broadloom Carpet, 2023/1759 Major 	J&J Flooring 	J&J Flooring 	Temporary 	2022/03/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Black; textured patterned loop carpet; PremierBac® Plus backing, Encore® SD Ultima® (with recycled content) nylon fibers; 543 g/m^2, 208.10 kg/m^3 pile density, 4.72 rows/cm, 3.66 m standard width; purchased February 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Panache 287 Black carpet tile 	Masland 	Masland 	FAIL 	2022/03/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Black; cut pile carpet; woven polypropylene backing, 100% Antron® legacy nylon fibers; 12 feet width, 0.375 inch pile height; purchased February 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Color Study 30 broadloom carpet, 999 Tricon Black 	Mohawk 	Mohawk 	Temporary 	2022/03/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Black; Broadloom, tufted, cut pile nylon carpet; Colorstrand® nylon, weldlok® backing; 8.68 mm thick, 39.37 rows per 10 cm, 1,017 g/m^2; Purchased February 2022 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Krion® Porcelanosa Black Metal 6901 	Krion Solid Surfaces, S.A. 	Material Bank 	Temporary 	2022/03/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Black; solid block material that is highly fireproof and resistant to chemical agents, steam and outdoor conditions; 2/3 natural mineral (ATH aluminum trihydrate) and 1/3 acrylic resin (PMMA); purchased February 2022 	 	-Other (enter details in Type of Material) 	
Ballare Glossy Floor, Black 	Rosebrand 	Rosebrand 	FAIL 	2022/03/17 	MMA 	Oddy Test (method: 20211201_OT ) 	Black; Semi-permanent vinyl gloss flooring ordered in rolls; 100% vinyl; full roll is 59 inches x 82 feet, 121 lb roll; purchased February 2022 	 	-Flooring - non-carpet 	
Invision Passages Broadloom Carpet, 2051 trail 	J&J Flooring 	J&J Flooring 	Temporary 	2022/02/25 	MMA 	Oddy Test (method: 20211201_OT ) 	Grey; looped nylon fiber, broadloom carpet; Encore®SD Ultima® Nylon with recycled content and PremierBac® Plus backing; 678 g/m^2, 296.01 kg/m^3 density, 3.94 rows/cm, 3.15 stitches/cm, 3.66 m standard width; Purchased 2021 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Avila Oak Moroccan Sand, NA190 vinyl floor tile 	 	Armstrong Flooring 	Temporary 	2022/02/15 	MMA 	Oddy Test (method: 20211201_OT ) 	Imitation wooden planking; vinyl tiling; 101.6 mm x 914.4 mm x 3.2 mm tiles; Purchased December 2021 	 	-Flooring - non-carpet 	
Shaw Contract Classicbac® Squares carpet tile, 5B102 	Shaw Industries Group Inc 	Consolidated Carpet 	Temporary 	2022/02/15 	MMA 	Oddy Test (method: 20211201_OT ) 	Brown carpet tile with overlapping squares pattern and Classicbac® backing; nylon fibers, install with Direct Glue, Double Glue, Stretch-in; 1085 g/m^2; Purchased December 2021 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Grotto Trail™ 4GT260660T carpet tile, 4000827 	Bentley Mills, Inc 	Consolidated Carpet 	FAIL 	2022/02/15 	MMA 	Oddy Test (method: 20211201_OT ) 	Cushioned brown carpet tile; Antron® Legacy™ Type 6.6 nylon; 7.719 oz/yd^3 pile density, 9.5 mm thick, 3356.7 g/m^2; Purchased December 2021 	 	-Flooring - Carpet - Synthetic/plastic/polymeric 	
Wonderflex 	Dazian fabrics 	Dazian fabrics 	pass, but no direct contact with object 	2011/03/15 	NMAI 	Oddy Test 	 	coupons adhered to the sample, material adhered to the glass 	plastic 	Cu: no changes; Ag: no changes, the coupon is well adhered to the sample; Pb: darkening, comparable to control
Wonderflex 	Dazian fabrics 	Dazian fabrics 	pass, but no direct contact with object 	2011/03/15 	NMAI 	Oddy Test 	 	coupons adhered to the sample, material adhered to the glass 	plastic 	Cu: darkening of the copper on contact side, the coupon is well adhered to the sample; Ag: no changes, the coupon is well adhered to the sample; Pb: darkening, comparable to control
Aquaplast 	Sammons Preston 	Patterson Medical 	fail 	2011/03/15 	NMAI 	Oddy Test 	 	material melted and embedded metal coupons 	plastic 	Cu: green corrosion; Ag: no change; Pb: white bloom
Aquaplast 	Sammons Preston 	Patterson Medical 	fail 	2011/03/15 	NMAI 	Oddy Test 	 	material melted and embedded metal coupons 	plastic 	Cu: green corrosion; Ag: no change; Pb: white bloom
Fisherbrand* Solid Silicone Stoppers 	 	Fisher Scientific 	pass 	2011/03/15 	NMAI 	Oddy Test 	 	contact 	silicon rubber 	Cu: no change; Ag: no change; Pb: no change
Fisherbrand* Solid Silicone Stoppers 	 	Fisher Scientific 	pass 	2011/03/15 	NMAI 	Oddy Test 	 	non contact 	silicon rubber 	Cu: no change; Ag: no change; Pb: no change
Sealed Air Corp Ethafoam, 1"" 	Sealed Air 	Foam Air 	PASS 	2009/04/23 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Typical, No major changes ; Ag: Typical, No major changes ; Pb: Typical, No major changes
Sealed Air Corp Ethafoam, 1"" 	Sealed Air 	Foam Air 	PASS 	2009/04/23 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Typical, No major changes ; Ag: Slightly redened ; Pb: Color became slightly lighter
Sealed Air Corp Ethafoam, 2"" 	Sealed Air 	Foam Air 	PASS 	2009/04/23 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Typical, No major changes ; Ag: Typical, No major changes ; Pb: Typical, No major changes
Sealed Air Corp Ethafoam, 2"" 	Sealed Air 	Foam Air 	PASS 	2009/04/23 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Typical, No major changes ; Ag: Typical, No major changes ; Pb: Typical, No major changes
avery Graphics Etchmark films specialty cast vinyl 	Avery 	 	FAIL 	2009/04/23 	NMAI 	Oddy Test 	 	 	graphic 	Cu: Typical, No major changes ; Ag: Typical, No major changes ; Pb: Darkening and some crystal formation
avery Graphics Etchmark films specialty cast vinyl 	Avery 	 	FAIL 	2009/04/23 	NMAI 	Oddy Test 	 	 	graphic 	Cu: Typical, No major changes ; Ag: Lighter color, possibly green corrosion; Pb: Darkening and some crystal formation
high strength transparent sillicone rubber compound 	GE Momentive Permance Materials 	Hisco 	PASS 	2009/04/23 	NMAI 	Oddy Test 	 	 	 	Cu: Typical, No major changes ; Ag: Typical, No major changes ; Pb: Typical, No major changes
high strength transparent sillicone rubber compound 	GE Momentive Permance Materials 	Hisco 	PASS 	2009/04/23 	NMAI 	Oddy Test 	 	 	 	Cu: Typical, No major changes ; Ag: Typical, No major changes ; Pb: Typical, No major changes
Backer rod - gray, 3"" diameter 	 	Reilly foam 	pass 	2009/03/19 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Typical, No major changes; Ag: Typical, No major changes; Pb: Typical, slightly darkened
Backer rod - gray, 3"" diameter 	 	Reilly foam 	pass 	2009/03/19 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Typical, No major changes; Ag: Typical, No major changes; Pb: Typical, slightly darkened
backer rod - white, 3"" Diameter 	 	Foam Fair 	pass 	2009/03/19 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Slightly reddened; Ag: Slightly yellow, but not overall; Pb: Typical, slightly darkened, with a few white crystals
backer rod - white, 3"" Diameter 	 	Foam Fair 	pass 	2009/03/19 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Slightly reddened; Ag: Slightly yellow, but not overall; Pb: Typical, slightly darkened with a few white crystals
Sherwin-Williams Polane 28T plus 	Sherwin William Company 	 	FAIL 	2009/03/19 	NMAI 	Oddy Test 	 	Polyeurethane = No Pass 	graphic 	Cu: Reddened; Ag: Slight yellow; Pb: Typical, slightly darkened
Sherwin-Williams Polane 28T plus 	Sherwin William Company 	 	FAIL 	2009/03/19 	NMAI 	Oddy Test 	 	Polyeurethane = No Pass 	graphic 	Cu: Reddened; Ag: Slight yellow; Pb: Typical, slightly darkened
Acrylite FF Acrylic Sheet 	Evonik Cyro http://corporate.evonik.com http://www.cyro.com/methacrylates/us/ 	 	pass 	2008/01/08 	NMAI 	Oddy Test 	 	passed with data sheets, without testing. 	Construction plastic 	
Pemko SiliconSeal Adhesive Gasketing HSS2000X588 	Pemko www.pemko.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	Caulk/Gasket 	Cu: same as control; Ag: same as control; Pb: same as control
Pemko SiliconSeal Adhesive Gasketing HSS2000X589 	Pemko www.pemko.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	Caulk/Gasket 	Cu: same as control; Ag: same as control; Pb: same as control
Alucore Honeycomb Core Panel (silver coating) 	Alcan www.alucore.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	Construction/Plastic & Metal 	Cu: same as control; Ag: same as control; Pb: same as control
Alucore Honeycomb Core Panel (silver coating) 	Alcan www.alucore.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	Construction/Plastic & Metal 	Cu: same as control; Ag: same as control; Pb: same as control
Alucore Honeycomb Core Panel (white coating) 	Alcan www.alucore.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	Construction/Plastic & Metal 	Cu: same as control; Ag: same as control; Pb: same as control
Alucore Honeycomb Core Panel (white coating) 	Alcan www.alucore.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	Construction/Plastic & Metal 	Cu: same as control; Ag: same as control; Pb: same as control
Sof-Rod backer rod 	Nomaco.com 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	foam/padding 	Cu: same as control; Ag: same as control; Pb: same as control
Sof-Rod backer rod 	Nomaco.com 	 	pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	foam/padding 	Cu: same as control; Ag: same as control; Pb: same as control
Carpet: Bentley Prince St ""Which Way Now"" 8WY300630R 	Bentley Prince St 	 	Pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems 	other/carpet 	Cu: slightly darker than control; Ag: same as control; Pb: same as control
Carpet: Bentley Prince St ""Which Way Now"" 8WY300630R 	Bentley Prince St 	 	pass 	2008/04/16 	NMAI 	Oddy Test 	 	condensation problems, A-D strip test pass 	other/carpet 	Cu: same as control; Ag: same as control; Pb: same as control
Aqua Resin 	ADM Tronics Unlimited, Inc.; www.aquaresin.com 	 	pass 	2007/06/14 	NMAI 	Oddy Test 	 	photo on file, A-D strip test pass 	Construction/plastic 	Cu: dull, darkened brown along 1 edge, crimson along opposite edge; dark crimson interior side; Ag: no change; Pb: dull, darkened, slight white corrosion on edge and near fold (covering about 1/8 surface)
Aqua Resin 	ADM Tronics Unlimited, Inc.; www.aquaresin.com 	 	pass 	2007/06/14 	NMAI 	Oddy Test 	 	photo on file, A-D strip test pass 	Construction/plastic 	Cu: dull, dark brown along 1 edge, crimson irredescent patina interior; Ag: no change; Pb: dull, darkened, slight white corrosion on edges and near fold
Marine Boatyard Resin 	Bondo Corporation; www.bondo-online.com 	 	fail 	2007/06/14 	NMAI 	Oddy Test 	 	photo on file, A-D strip test: At level 2 after 3 weeks 	Construction/plastic 	Cu: dull, interior considerably darkened with crimson irredescent patina; Ag: no change; Pb: dull, surface covered with white powder
Marine Boatyard Resin 	Bondo Corporation; www.bondo-online.com 	 	fail 	2007/06/14 	NMAI 	Oddy Test 	 	photo on file, A-D strip test: At level 2 after 3 weeks 	Construction/plastic 	Cu: dull, interior darkened with crimson irredescent patina; Ag: no change; Pb: dull, white powdery surface with white spots and lt. brown spots
duoMatrix NEO 	Smooth-On; www.smooth-on.com 	 	pass 	2007/06/14 	NMAI 	Oddy Test 	 	photo on file, A-D strip test pass 	other - mold making material for mounts 	Cu: slightly dull; Ag: no change; Pb: dull, darkened, slight bluish irredescence
duoMatrix NEO 	Smooth-On; www.smooth-on.com 	 	pass 	2007/06/14 	NMAI 	Oddy Test 	 	photo on file, A-D strip test pass 	other - mold making material for mounts 	Cu: slightly dull; Ag: no change; Pb: dull, darkened, slight bluish irredescence
Ultra Mount - Sample from Company (retest) 	United Industries, Inc. www.ultraboard.com 	 	pass 	2007/06/04 	NMAI 	Oddy Test 	 	Spots on lead are probably due to condensation, A-D strip test pass 	Construction/plastic 	Cu: dull, darkened, irredescent violet patina (same as control); Ag: No change; Pb: dull, darkened, localized spot at fold with white/silvery powdery appearance
Ultra Mount - Sample from Company (retest) 	United Industries, Inc. www.ultraboard.com 	 	pass 	2007/06/04 	NMAI 	Oddy Test 	 	Spots on lead are probably due to condensation, A-D strip test pass 	Construction/plastic 	Cu: dull, darkened, irredescent violet patina (same as control); Ag: No change; Pb: dull, darkened, localized spot at side with white/silvery powdery appearance
Ultra Board 	United Industries, Inc. www.ultraboard.com 	 	pass 	2007/05/18 	NMAI 	Oddy Test 	 	 	Construction/plastic 	Cu: dull, blue and crimson irredescent patina, darkened; Ag: no change; Pb: dull, darkened, slightly irredescent
Ultra Board 	United Industries, Inc. www.ultraboard.com 	 	pass 	2007/05/18 	NMAI 	Oddy Test 	 	 	Construction/plastic 	Cu: dull, darkened brown, bluish patina; Ag: no change; Pb: dull, darkened, slight bluish irredescence
EcoResin - Atmosphere, Stone 2 	3-form.com 	 	pass 	2007/05/17 	NMAI 	Oddy Test 	 	 	Construction/plastic 	Cu: slightly dull, with crimson irredescence; Ag: no change; Pb: dull and darkened with slight blue irredescence at center of coupon
EcoResin - Atmosphere, Stone 2 	3-form.com 	 	pass 	2007/05/17 	NMAI 	Oddy Test 	 	 	Construction/plastic 	Cu: slightly dull, spotty crimson patina with gray/silver spots at edge and center; Ag: no change; Pb: dull, dark
EcoResin - Atmosphere, Thyme 2 	3-form.com 	 	pass 	2007/05/17 	NMAI 	Oddy Test 	 	 	Construction/plastic 	Cu: slightly dull with crimson irredescent patina; Ag: no change; Pb: dull and darkened
EcoResin - Atmosphere, Thyme 2 	3-form.com 	 	pass 	2007/05/17 	NMAI 	Oddy Test 	 	 	Construction/plastic 	Cu: slightly dull, with crimson irredescence and few black spots (appear to be from water droplets) ; Ag: no change; Pb: dull and darkened
Ambersil 1040N; clear 	Ambersil; www.siliconia.co.uk 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: dull, slightly darkened; Ag: no change; Pb: dulled, darkened
Ambersil 1040N; clear 	Ambersil; www.siliconia.co.uk 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: dull, slightly darkened; Ag: no change; Pb: dulled, slightly darkened
Dow Corning 7091 silicone - gray 	Dow Corning; http://www.dowcorning.com/ 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: dulled, darkened crimson/brown; Ag: no change; Pb: dulled, slightly darkened
Dow Corning 7091 silicone - gray 	Dow Corning; http://www.dowcorning.com/ 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: dulled, darkened crimson/brown; Ag: no change; Pb: dulled, slightly darkened
Dow Corning 993 silicone - black 	Dow Corning; http://www.dowcorning.com/ 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: slightly dulled; Ag: no change; Pb: dulled, slightly darkened
Dow Corning 993 silicone - black 	Dow Corning; http://www.dowcorning.com/ 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: slightly dulled, w/ crimson patina; consistent w/ control; Ag: no change; Pb: dulled, slightly darkened
Silex bubble seal D-shape; Black 	Silex 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	 	caulk/gasket 	Cu: dulled, one side darkened crimson; Ag: no change; Pb: dulled, slightly darkened
Silex bubble seal D-shape; Black 	Silex 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	 	caulk/gasket 	Cu: slightly dulled, w/ crimson patina; consistent w/ control; Ag: no change; Pb: dulled, slightly darkened
Silex bubble seal D-shape; Gray 	Silex 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	 	caulk/gasket 	Cu: dulled, slight crimson patina, interior of coupon blackened; black spots on exterior ; Ag: no change; Pb: dulled, slightly darkened
Silex bubble seal D-shape; Gray 	Silex 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	 	caulk/gasket 	Cu: slightly dulled ; Ag: no change; Pb: dulled, slightly darkened
Silex extruded bubble seal ""D"" shape clear 	Dow Corning; http://www.dowcorning.com/ 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: dulled, exterior side darkened w/ crimson patina; Ag: no change; Pb: dulled, slightly darkened
Silex extruded bubble seal ""D"" shape clear 	Dow Corning; http://www.dowcorning.com/ 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	caulk/gasket 	Cu: dulled, exterior side darkened w/ crimson patina; Ag: no change; Pb: dulled, slightly darkened
1/2 "" foam board 	Laird Plastics; 410-7807100 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	Construction/plastic 	Cu: dulled, slightly darkened; Ag: No change; Pb: dulled, slightly darkened
1/2 "" foam board 	Laird Plastics; 410-7807100 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	Construction/plastic 	Cu: dulled, slightly darkened; Ag: No change; Pb: dulled, slightly darkened
Tefor 	ABET, Inc; www.abetlaminati.com 	 	fail 	2007/04/27 	NMAI 	Oddy Test 	 	not for use inside cases, photo on file 	Construction/plastic 	Cu: dulled, slightly darkened; Ag: No change; Pb: significantly darkened, irredescent red & orange patina
Tefor 	ABET, Inc; www.abetlaminati.com 	 	fail 	2007/04/27 	NMAI 	Oddy Test 	 	not for use inside cases, photo on file 	Construction/plastic 	Cu: dulled, slightly darkened; Ag: No change; Pb: darkened, irredescent blue patina
Ultra Mount- Used by Artex 	United Industries, Inc. www.ultraboard.com 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	Construction/plastic 	Cu: dulled, crimson patina; Ag: No change; Pb: dulled, slightly darkened
Ultra Mount- Used by Artex 	United Industries, Inc. www.ultraboard.com 	 	pass 	2007/04/27 	NMAI 	Oddy Test 	 	photo on file 	Construction/plastic 	Cu: dulled, crimson patina; Ag: No change; Pb: dulled, slightly darkened
Shapelock 	Shapelock; www.shapelock.com 	 	Temporary 	2007/03/19 	NMAI 	Oddy Test 	 	Passed for use at temp.'s below 60 C. Approved for non-permanent (non-contact for metals) use. Note however material is designed to break down over time. 	other - mold making material for mounts 	Cu: no change; Ag: no change; Pb: dulled, slightly darkened
Shapelock 	Shapelock; www.shapelock.com 	 	Temporary 	2007/03/19 	NMAI 	Oddy Test 	 	Passed for use at temp.'s below 60 C. Approved for non-permanent (non-contact for metals) use. 	other - mold making material for mounts 	Cu: no change; Ag: no change; Pb: dulled, slightly darkened
Shapelock 	Shapelock; www.shapelock.com 	 	fail 	2007/02/08 	NMAI 	Oddy Test 	 	re-test at 40 C because 60 C is melting point of this material. Material was in molten state during test, A-D strip test pass 	other - mold making material for mounts 	Cu: darkened, dull, purply gray, slightly iridescent; Ag: no change; Pb: completely coverd with yellow-white corrosion
Shapelock 	Shapelock; www.shapelock.com 	 	fail 	2007/02/08 	NMAI 	Oddy Test 	 	re-test at 40 C because 60 C is melting point of this material. Material was in molten state during test, A-D strip test pass 	other - mold making material for mounts 	Cu: darkened, dull, purply gray, slightly iridescent; Ag: no change; Pb: completely coverd with yellow-white corrosion
Polyolefin Adhesive lined thin-wall heat shrink tubing 7861K series 	3M 	 	pass 	2006/05/11 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: brighter/less red than control; Ag: no change; Pb: darkened, less so than control
Polyolefin Adhesive lined thin-wall heat shrink tubing 7861K series 	3M 	 	pass 	2006/05/11 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: brighter/less red than control; Ag: no change; Pb: darkened, less so than control
Appleply covered with corrosion intercept 	Conservation By Design LimitedEmail: info@conservation-by-design.co.uk Tel: +44 (0)1234 853555Fax: +44 (0)1234 852334 	 	fail 	2006/03/22 	NMAI 	Oddy Test 	 	Not viable option for vapor barrier for Appleply. 	construction/wood product/barrier 	Cu: very dark red irridescence, dull brown areas; Ag: no change; Pb: darkened
Appleply covered with corrosion intercept 	Conservation By Design LimitedEmail: info@conservation-by-design.co.uk Tel: +44 (0)1234 853555 Fax: +44 (0)1234 852334 	 	fail 	2006/03/22 	NMAI 	Oddy Test 	 	Not viable option for vapor barrier for Appleply. 	construction/wood product/barrier 	Cu: bright metallic orange with irridescent red; Ag: no change; Pb: very thick white corrosion product all over
3M Thermal Transfer Polyester Label Material 7816 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/03/22 	NMAI 	Oddy Test 	 	 	graphics 	Cu: no change; Ag: no change; Pb: no change - comparable to control
3M Thermal Transfer Polyester Label Material 7817 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/03/22 	NMAI 	Oddy Test 	 	 	graphics 	Cu: no change; Ag: no change; Pb: no change - comparable to control
black silicone O-ring 	HELMUT GUENSCHEL, INC. (HGI) 10 Emala Avenue Baltimore, MD 21220 Tel: 410.686.5900 Fax: 410.687.9342 www.guenschel.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	proprietary product, supplied by Guenschel 	caulk/gasket 	Cu: no change; Ag: no change; Pb: no change
black silicone O-ring 	HELMUT GUENSCHEL, INC. (HGI) 10 Emala Avenue Baltimore, MD 21220 Tel: 410.686.5900 Fax: 410.687.9342 www.guenschel.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	proprietary product, supplied by Guenschel 	caulk/gasket 	Cu: no change; Ag: no change; Pb: no change
Cured Silicone glazing compound 	HELMUT GUENSCHEL, INC. (HGI) www.guenschel.com 	 	fail 	2006/02/13 	NMAI 	Oddy Test 	 	proprietary product, supplied by Guenschel, A-D strip test pass 	caulk/gasket 	Cu: dark orange; Ag: no change; Pb: white/yellow corrosion product all over
Cured Silicone glazing compound 	HELMUT GUENSCHEL, INC. (HGI) 10 Emala Avenue Baltimore, MD 21220 Tel: 410.686.5900 Fax: 410.687.9342 www.guenschel.com 	 	fail 	2006/02/13 	NMAI 	Oddy Test 	 	proprietary product, supplied by Guenschel, A-D strip test pass 	caulk/gasket 	Cu: dark brown ; Ag: no change; Pb: white corrosion product all over
white silicone O-ring 	HELMUT GUENSCHEL, INC. www.guenschel.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	proprietary product, supplied by Guenschel 	caulk/gasket 	Cu: dark orange; Ag: no change; Pb: slightly mottled surface; remains bright
white silicone O-ring 	HELMUT GUENSCHEL, INC. www.guenschel.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	proprietary product, supplied by Guenschel 	caulk/gasket 	Cu: no change; Ag: no change; Pb: slightly mottled surface; remains bright
Sintra (black) 	Alcan Composites USA Inc. 208 W. 5th Street, PO Box 507 Benton, KY 42025 270-527-4200 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	construction/plastic 	Cu: slightly dark orange; Ag: no change; Pb: no change
Sintra (black) 	Alcan Composites USA Inc. 208 W. 5th Street, PO Box 507 Benton, KY 42025 270-527-4201 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	construction/plastic 	Cu: slightly dark orange; Ag: no change; Pb: no change
3M Jet-I Dye sublimation ink on polyester fabric 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: no change; Ag: no change; Pb: no change
3M Jet-I Dye sublimation ink on polyester fabric 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	Condensation problems 	Graphic composite 	Cu: dark red; black spot due to condensation; Ag: no change; Pb: darkened; crystals on edge due to condensation
3M Scotchcal matte overlaminate 8520 on Sentinel polycarbonate 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	fail 	2006/02/13 	NMAI 	Oddy Test 	 	The ink transfers when wet 	Graphic composite 	Cu: dark red; Ag: no change; Pb: white and yellow powdery surface, buildup at edges
3M Scotchcal matte overlaminate 8520 on Sentinel polycarbonate 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	fail 	2006/02/13 	NMAI 	Oddy Test 	 	The ink transfers when wet 	Graphic composite 	Cu: dark red; Ag: no change; Pb: white powdery surface all over
3M Scotchcal matte overlaminate 8520, vinyl, media 7725-10, acrylic 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: dark red; Ag: no change; Pb: no change when compared to control
3M Scotchcal matte overlaminate 8520, vinyl, media 7725-10, acrylic 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: dark red; Ag: no change; Pb: no change when compared to control
3M Scothcal matte overlaminate, non-solvent based ink 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: dark red; Ag: no change; Pb: white crystal corrosion product on one edge, possible condensation problems
3M Scothcal matte overlaminate, non-solvent based ink 	3M Graphics Market Center Building 220-12E-04 PO Box 33220 St Paul MN 55144-3220 1-800-374-6772 www.scotchprint.com 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: slightly darker red; Ag: no change; Pb: no change
Bogod Easy Slide Silicone Compound in test jar 	Bogod Group Fortran Rd, St. Mellons, Cardiff CF3 0WJ tel:(029) 2079 2081 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	other 	Cu: very dark red iridescent; Ag: no change; Pb: dark iridescence
Bogod Easy Slide Silicone Compound in test jar 	Bogod Group Fortran Rd, St. Mellons, Cardiff CF3 0WJ tel:(029) 2079 2082 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	other 	Cu: very dark red iridescent; Ag: no change; Pb: slight iridescence
Bogod Easy Slide Silicone Compound on mylar 	Bogod Group Fortran Rd, St. Mellons, Cardiff CF3 0WJ tel:(029) 2079 2079 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	other 	Cu: dark red iridescent; Ag: no change; Pb: slightly darkened
Bogod Easy Slide Silicone Compound on mylar 	Bogod Group Fortran Rd, St. Mellons, Cardiff CF3 0WJ tel:(029) 2079 2080 	 	pass 	2006/02/13 	NMAI 	Oddy Test 	 	 	other 	Cu: darkened; Ag: no change; Pb: no change
Sorbothane with unknown adhesive 	SORBOTHANE, INCORPORATED 2144 State Route 59 Kent, OH 44240 t: 330.678.9444 800.838.3906 http://www.sorbothane.comTECHNICAL CONTACT Michael Zanin, Engineer Phone: 330.678.9444 ext. 151 Email: mike.zanin@sorbothane.com	 	pass 	2005/11/22 	NMAI 	Oddy Test 	 	A-D strip test pass 	foam/padding 	Cu: no change; Ag: no change; Pb: white corrosion due to condensation
Sorbothane with unknown adhesive 	SORBOTHANE, INCORPORATED 2144 State Route 59 Kent, OH 44240 t: 330.678.9444 800.838.3906 http://www.sorbothane.comTECHNICAL CONTACT Michael Zanin, Engineer Phone: 330.678.9444 ext. 151 Email: mike.zanin@sorbothane.com	 	pass 	2005/11/21 	NMAI 	Oddy Test 	 	A-D strip test pass 	foam/padding 	Cu: no change; Ag: no change; Pb: no change
Alumalite Aluminum panel 10mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19449 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark orange, slight iridescence; Ag: no change; Pb: darkened; blue tinge
Alumalite Aluminum panel 10mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19450 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: bright orange; Ag: no change; Pb: darkened; blue tinge
Alumalite Aluminum panel 6mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19447 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark orange; Ag: no change; Pb: darkened; comparable to control
Alumalite Aluminum panel 6mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19448 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: very dark brown iridescent; Ag: no change; Pb: darkened; comparable to control
D Lite Aluminum panel painted 1 side 3mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19441 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: iridescence splotchy, possible condensation problems; Ag: no change; Pb: white crystal corrosion product on one edge, possible condensation problems
D Lite Aluminum panel painted 1side 3mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19442 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark orange, no iridescence; Ag: no change; Pb: darkened; comparable to control
D Lite Aluminum panel painted 2 sides 3mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19439 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark; iridescent; Ag: no change; Pb: lightly dusted with white corrosion product; splotchy overall
D Lite Aluminum panel painted 2 sides 3mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19440 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: irridescent; Ag: no change; Pb: darkened; dusty toned; comparble to control
Econolite Aluminum panel 10mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19445 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark brown iridescent; Ag: no change; Pb: darkened; comparable to control
Econolite Aluminum panel 10mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19446 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark red-brown iridescent; Ag: no change; Pb: darkened; comparable to control
Econolite Aluminum panel 6mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19443 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: very dark, iridescent, black edges; Ag: no change; Pb: darkened; blue tinge
Econolite Aluminum panel 6mm 	LAMINATORS INC 3255 Penn Street Hatfield, PA 19444 	 	pass 	2005/11/11 	NMAI 	Oddy Test 	 	A-D strip test pass 	construction/plastic & metal 	Cu: dark red iridescent; Ag: no change; Pb: darkened, blue tinge, small corrosion product (condensation?)
Appleply uncoated 	made by States Industries, with a urea formaldehyde resin 	 	fail 	2005/10/05 	NMAI 	Oddy Test 	 	Control: Cu - darkened, Ag - no change, Pb - darkened, blue tinge; A-D strip test: 2 out of scale 0 (pass) to 3 (fail) 	construction/wood product 	Cu: very slightly darkened; Ag: no change; Pb: overall light white corrosion. Some condesation/ yellow corrosion
Appleply uncoated 	made by States Industries, with a urea formaldehyde resin 	 	fail 	2005/10/05 	NMAI 	Oddy Test 	 	A-D strip test: 3 out of scale 0 (pass) to 3 (fail); Control: Cu - darkened, Ag - no change, Pb - darkened, blue tinge. 	construction/wood product 	Cu: very slightly darkened; Ag: no change; Pb: overall light white corrosion.
Sintra (expanded PVC sheet) 	 	 	pass 	2005/08/16 	NMAI 	Oddy Test 	 	retested Cu and Pb only 	construction: plastic 	Cu: no change; Pb: no change
Sintra (expanded PVC sheet) 	 	 	pass 	2005/08/16 	NMAI 	Oddy Test 	 	retested Cu and Pb only 	construction: plastic 	Cu: no change; Pb: no change
CleanSeal 2897H2-IM gasket 	Clean Seal Inc.www.cleanseal.com 	 	fail 	2005/08/12 	NMAI 	Oddy Test 	 	backing removed, adhesive exposed 	caulk/gasket 	Cu: turned silvery all over; Ag: no change; Pb: no change
CleanSeal 2897H2-IM gasket 	Clean Seal Inc. POB 2929-20900 West Ireland Rd. South Bend IN 46680. tel 574-299-1888. www.cleanseal.com 	 	Fail 	2005/08/12 	NMAI 	Oddy Test 	 	backing removed, adhesive exposed 	caulk/gasket 	Cu: silvery on exterior, red, iridescent on interior; Ag: no change; Pb: no change
Apleply encased in Sintra 	Sintra: Alcan Composites; Appleply: states Industries 	 	pass 	2005/08/12 	NMAI 	Oddy Test 	 	(Sintra as substrate and vapor barrier)Cube of appleply completely encased in Sintra, solvent welded seams. 	Construction/plastic 	Cu: no change; Ag: no change; Pb: darkened
Apleply encased in Sintra 	Sintra: Alcan Composites; Appleply: states Industries 	 	pass 	2005/08/12 	NMAI 	Oddy Test 	 	(Sintra as substrate and vapor barrier)Cube of appleply completely encased in Sintra, solvent welded seams 	Construction/plastic 	Cu: no change; Ag: no change; Pb: darkened
Komatex PVC sheet 	Total Plastics Inc. www.totalplastics.com; 5424 Pulaski Highway, Baltimore MD 21205. Tel 410-83-1122 Fax 410-483-1493. 	 	pass 	2005/08/12 	NMAI 	Oddy Test 	 	 	construction/plastic 	Cu: no change; Ag: no change; Pb: darkened
Komatex PVC sheet 	Total Plastics Inc. www.totalplastics.com; 5424 Pulaski Highway, Baltimore MD 21205. Tel 410-83-1122 Fax 410-483-1493. 	 	pass 	2005/08/12 	NMAI 	Oddy Test 	 	 	construction/plastic 	Cu: no change; Ag: no change; Pb: darkened
Appleply 	States Industries 	 	Fail 	2005/08/12 	NMAI 	Oddy Test 	 	A-D strip test: 0.6 ""fair to good"" 	construction: wood product 	Cu: no change; Ag: no change; Pb: voluminous yellow and white corrosion, heterogeneous
Appleply 	States Industries 	 	Fail 	2005/08/12 	NMAI 	Oddy Test 	 	A-D strip test: 0.5 ""fair to good"" 	construction: wood product/substrate 	Cu: no change; Ag: no change; Pb: uneven voluminous yellow and white corrosion, heterogeneous
Apleply encased in Sintra coated with Benjamin moore clear epoxy 	Sintra: Alcan Composites; Appleply: states Industries; Epoxy: Benjamin Moore 	 	pass 	2005/08/12 	NMAI 	Oddy Test 	 	Sintra and epoxy as vapor barriers.Cube of appleply completely encased in Sintra, solvent welded seams, then coated with BM clear epoxy 	construction?wood/plastic/coating 	Cu: no change; Ag: no change; Pb: darkened
Apleply encased in Sintra coated with Benjamin moore clear epoxy 	Sintra: Alcan Composites; Appleply: states Industries; Epoxy: Benjamin Moore 	 	pass 	2005/08/12 	NMAI 	Oddy Test 	 	Sintra and epoxy as vapor barriers.Cube of appleply completely encased in Sintra, solvent welded seams, then coated with BM clear epoxy 	construction?wood/plastic/coating 	Cu: no change; Ag: no change; Pb: darkened
Sintra (expanded PVC sheet) 	suppliers: Laird plastics 800-873-8405 Total plastics 800-492-4695 	 	pass 	2005/07/27 	NMAI 	Oddy Test 	 	retest: Pb coupons reacted differently. Note: this material passed by NARA. According to Craig Huzway (NMAI exhibits shop) ""you never know what brand of PVC sheet they have in stock. Yes there are many ""brands"" of sintra."" 	construction/plastic 	Cu: dulled; Ag: shiny; Pb: darkened
Sintra (expanded PVC sheet) 	 	 	pass 	2005/07/27 	NMAI 	Oddy Test 	 	retest: Pb coupons reacted differently. Note: this material passed by NARA. 	construction/plastic 	Cu: dulled; Ag: shiny; Pb: scattered white crystals
MDF Collection yellow WPMA 6019 	archsystems.com 	 	fail 	2005/03/12 	NMAI 	Oddy Test 	 	A-D strip test: level 2 	construction/wood product 	Cu: no change; Ag: no change; Pb: almost no metal left - all white corrosion
MDF Collection yellow WPMA 6019 - ASI solid and gouged 	archsystems.com 	 	fail 	2005/03/11 	NMAI 	Oddy Test 	 	A-D strip test: level 1 	construction/wood product 	Cu: no change; Ag: no change; Pb: almost no metal left - all white corrosion
Alaskan Yellow cedar veneer on appleply with unknown waterbase contact adhesive 	 	 	fail 	2005/03/10 	NMAI 	Oddy Test 	 	no product lit found, A-D strip test: level 1 	construction/wood product 	Cu: darkened; Ag: no change; Pb: no metal left, all white corrosion
Alaskan Yellow cedar veneer on appleply with unknown waterbase contact adhesive 	 	 	fail 	2005/03/10 	NMAI 	Oddy Test 	 	no product lit found, A-D strip test: level 2 	construction/wood product 	Cu: darkened; Ag: no change; Pb: trace of metal remaining, yellow/white corrosion
Alaskan Yellow cedar veneer 	Seiling&Jones 717-235-7931 	 	pass 	2005/03/01 	NMAI 	Oddy Test 	 	 	construction/wood product 	Cu: no change; Ag: no change; Pb: no change
Alaskan Yellow cedar veneer 	Seiling&Jones 717-235-7931 	 	Pass 	2005/03/01 	NMAI 	Oddy Test 	 	 	construction/wood product 	Cu: slightly reddish; Ag: no change; Pb: small white crystals on edge
Permaflex IP 6100 Lustex 10 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Tried MSC setup; lost all water 	Graphic composite 	Cu: shiny; Ag: shiny; Pb: shiny; barely darkened
Permaflex IP 6100 Lustex 10 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Condensation probs 	Graphic composite 	Cu: Slightly darkened; shiny; Ag: shiny; Pb: slightly darkened; blue tinge; some white corrosion inner end with outlines from water
Permagard PG 7034 Gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Tried MSC setup; lost all water 	Graphic composite 	Cu: slightly darkened; shiny; Ag: shiny; Pb: slightly darkened
Permagard PG 7034 Gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: slightly darkened; violet tinge; shiny; Ag: shiny; Pb: slightly darkened
Permagard PG 7282 semi-gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Tried MSC setup; lost all water; vinyl 	Graphic composite 	Cu: shiny; Ag: shiny; Pb: slightly darkened
Permagard PG 7282 semi-gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Condensation probs; vinyl 	Graphic composite 	Cu: Black spots & darkened areas with outlines from water; Ag: shiny; Pb: slightly darkened; blue tinge; some white corrosion inner end with outlines from water
Permagard PG 7285 Matte mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Tried MSC setup; lost all water; vinyl 	Graphic composite 	Cu: shiny; Ag: shiny; Pb: slightly darkened
Permagard PG 7285 Matte mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Condensation probs; vinyl 	Graphic composite 	Cu: slightly darkened; shiny; Ag: shiny; Pb: slightly darkened; blue tinge; some white corrosion both ends with outlines from water
Alpha Graphics Black 	Alpha Graphics; 1305 St Paul St.; Baltimore, MD 21202; 410-727-1400 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Tried MSC setup; lost all water 	Graphics 	Cu: Slightly darkened; shiny; Ag: shiny; Pb: slightly darkened
Alpha Graphics Black 	Alpha Graphics; 1305 St Paul St.; Baltimore, MD 21202; 410-727-1400 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	 	Graphics 	Cu: shiny; Ag: shiny; Pb: slightly darkened
Alpha Graphics Gray 	Alpha Graphics; 1305 St Paul St.; Baltimore, MD 21202; 410-727-1400 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Tried MSC setup; lost all water 	Graphics 	Cu: shiny; Ag: shiny; Pb: slightly darkened
Alpha Graphics Gray 	Alpha Graphics; 1305 St Paul St.; Baltimore, MD 21202; 410-727-1400 	 	Pass 	2004/02/20 	NMAI 	Oddy Test 	 	Condensation probs 	Graphics 	Cu: slightly darkened; violet tinge; shiny; black spots from water; Ag: shiny; Pb: slightly darkened; blue tinge; some white corrosion outer end with outlines from water
Permaflex PF 6000 Lustex 15 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: Shiny; Ag: Shiny; Pb: Slightly darkened
Permaflex PF 6000 Lustex 15 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	Unclear if Pb corrosion from condensation 	Graphic composite 	Cu: Overall darkening, like control # 1; Ag: Shiny; Pb: Slightly darkened; small amount white corrosion inside end
Permaflex PF 6300 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: Shiny; Ag: Shiny; Pb: Slightly darkened
Permaflex PF 6300 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: Black corrosion, due to condensation; Ag: Shiny; Pb: Slightly darkened; slight white corrosion under coupon from condensation
Permagard IP 7000 Gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Fail 	2004/02/09 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: Overall darkening, violet discolor; Ag: Shiny; Pb: Beginning even coverage of whitish corrosion on inner end
Permagard IP 7000 Gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Fail 	2004/02/09 	NMAI 	Oddy Test 	 	 	Graphic composite 	Cu: Shiny; Ag: Shiny; Pb: Beginning even coverage of whitish corrosion on inner end
Permagard PG 7284 semi-matte mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Fail 	2004/02/09 	NMAI 	Oddy Test 	 	Made of vinyl 	Graphic composite 	Cu: Overall violet discolor; Ag: Shiny; Pb: Velvety look overall no sheen, top & under; like #s 11 & 12
Permagard PG 7284 semi-matte mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Fail 	2004/02/09 	NMAI 	Oddy Test 	 	Made of vinyl 	Graphic composite 	Cu: Shiny; Ag: Shiny; Pb: Velvety look overall no sheen, top & under; like #s 11 & 12
Permaflex IP 6200 Lustex 5 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	graphics composite 	Cu: Shiny; Ag: Shiny; Pb: Slightly darkened
Permaflex IP 6200 Lustex 5 mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	graphics composite 	Cu: Shiny; Ag: Shiny; Pb: Slightly darkened
Permagard IP 7200 matte overlaminate mock graphic panel with 1/8"" acrylic, Polycarbonate print media 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	graphics composite 	Cu: Violet discolor, shiny ; Ag: Shiny ; Pb: Slightly darkened - ok
Permagard IP 7200 matte overlaminate mock graphic panel with 1/8"" acrylic, Polycarbonate print media 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	graphics composite 	Cu: Shiny; slight black corrosion outside end from condensation; Ag: Shiny ; Pb: Slightly darkened - ok
Permagard IP 7200 matte overlaminate mock graphic panel with 1/8"" acrylic, Tyvek print media 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	 	graphics composite 	Cu: Slight discolor: black and violet; still shiny; Ag: Shiny ; Pb: Slightly darkened - ok; white corrosion under bend from condensation
Permagard IP 7200 matte overlaminate mock graphic panel with 1/8"" acrylic, Tyvek print media 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Pass 	2004/02/09 	NMAI 	Oddy Test 	 	Passed despite Cu result - Black may be aberration, see Cu for # 1; also 3 other samples with similar material fine: #s 3,5,6 	graphics composite 	Cu: Black corrosion in inside end, even coverage; still shiny outside end; Ag: Shiny ; Pb: Slightly darkened - ok
Permagard PG 7281 PVC Gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Fail 	2004/02/09 	NMAI 	Oddy Test 	 	Made of vinyl 	graphics composite 	Cu: Shiny; Ag: Shiny; Pb: Velvety look overall no sheen, top & under
Permagard PG 7281 PVC Gloss mock graphic panel with 1/8"" acrylic 	MacTac North America, 4560 Darrow Rd. Stow, OH, 44224, 330-688-1111, www. mactac.com 	 	Fail 	2004/02/09 	NMAI 	Oddy Test 	 	Made of vinyl 	graphics composite 	Cu: Shiny; Ag: Shiny; Pb: Velvety look overall no sheen, top & under; inside end under overall white corrosion
Conformable PTFE Teflon tape on Supersoft silicone foam rubber strip 	 	McMasterCarr www.mcmaster.com 	Fail 	2004/01/22 	NMAI 	Oddy Test 	 	Lost all water 	caulk/gasket 	Cu: darkened, violet discolor, still shiny; Ag: shiny - ok; Pb: overall even white corrosion
Conformable PTFE Teflon tape on Supersoft silicone foam rubber strip 	 	McMasterCarr www.mcmaster.com 	Fail 	2004/01/22 	NMAI 	Oddy Test 	 	 	caulk/gasket 	Cu: darkened, violet discolor, still shiny; Ag: shiny - ok; Pb: overall even white corrosion
GG10 Gasket Seal 	 	 	Fail 	2004/01/22 	NMAI 	Oddy Test 	 	Lost all water 	caulk/gasket 	Cu: green tarnishing,light on top, darker underneath bend; Ag: shiny - ok; Pb: even white corrosion
GG10 Gasket Seal 	 	 	Fail 	2004/01/22 	NMAI 	Oddy Test 	 	 	caulk/gasket 	Cu: overall black green tarnishing; Ag: tarnishing & color change, slight reddish overall, esp at edges ; Pb: slightly dark
Velcro brand hook 088 Tape 0115 Black 330 	Velcro Brand 	 	Fail 	2004/01/22 	NMAI 	Oddy Test 	 	Lost all water 	fastener 	Cu: darkened, violet discolor, still shiny; Ag: shiny - ok; Pb: white corrosion at top of bend over matte dark gray color
Velcro brand hook 088 Tape 0115 Black 330 	Velcro Brand 	 	Fail 	2004/01/22 	NMAI 	Oddy Test 	 	 	fastener 	Cu: darkened, violet discolor, still shiny; Ag: shiny - ok; Pb: even white corrosion top of bend to inner end over matte dark gray color
Teflon sheet 	Plastomer Products www.plastomertech.com/plastomerproducts.htm 	 	Pass 	2004/01/22 	NMAI 	Oddy Test 	 	Lost all water 	other 	Cu: shiny - ok; Ag: shiny - ok; Pb: dark gray with blue tinge
Teflon sheet 	Plastomer Products www.plastomertech.com/plastomerproducts.htm 	 	Pass 	2004/01/22 	NMAI 	Oddy Test 	 	Coupons layered between sheets of test sample 	other 	Cu: Shiny, slight violet discolor; Ag: shiny - ok; Pb: slightly dark
Corrosion Intercept 	Engineered Materials, Inc. 	 	Pass 	2004/01/22 	NMAI 	Oddy Test 	 	Lost all water; coupons layered between sheets of test sample 	scavenger 	Cu: Shiny, slight violet discolor; Ag: shiny - ok; Pb: slightly dark
Corrosion Intercept 	Engineered Materials, Inc. 	 	Pass 	2004/01/22 	NMAI 	Oddy Test 	 	Coupons in pools of water;coupons layered between sheets of test sample 	scavenger 	Cu: black/green corrosion where sitting in water; Ag: shiny - ok; Pb: White corrosion where sitting in water
Dry Tac PSF Facemount UV adhesive in a mock graphic panel with 1/8"" acrylic, polycarbonate & print media 	 	 	Pass 	2003/12/23 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: slight white corrosion in inside end; slightly darkened, still shiny
Dry Tac PSF Facemount UV adhesive in a mock graphic panel with 1/8"" acrylic, polycarbonate & print media 	 	 	Pass 	2003/12/23 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: slightly darkened
Optima Liquid overlaminate 	 	 	Pass 	2003/12/23 	NMAI 	Oddy Test 	 	Mixed according to instructions & applied to Mylar; offgas time 5 days 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: dark gray
Optima Liquid overlaminate 	 	 	Pass 	2003/12/23 	NMAI 	Oddy Test 	 	Mixed according to instructions & applied to Mylar; offgas time 5 days 	graphics 	Cu: slight violet tarnishing on inner end; otherwise shiny; Ag: shiny - ok; Pb: dark gray
Optimount 60711 adhesive in a mock graphic panel with 1/8"" acrylic, polycarbonate & print media 	 	 	Pass 	2003/12/23 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny - ok; black corrosion on outer end from condensation; Ag: shiny - ok; Pb: white corrosion from condensation; slightly darkened
Optimount 60711 adhesive in a mock graphic panel with 1/8"" acrylic, polycarbonate & print media 	 	 	Pass 	2003/12/23 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: white corrosion from condensation; slightly darkened
Permacolor, PermaGard IP7300 	MACtac N.A. 4560 Darrow Rd, Stow, OH 44224; (330) 688-1111; www.MACTac.com 	 	Fail 	2003/12/23 	NMAI 	Oddy Test 	 	 	graphics 	Cu: slight violet tarnishing; otherwise shiny; Ag: shiny - ok; Pb: overall hazy white
Permacolor, PermaGard IP7300 	MACtac N.A. 4560 Darrow Rd, Stow, OH 44224; (330) 688-1111; www.MACTac.com 	 	Fail 	2003/12/23 	NMAI 	Oddy Test 	 	 	graphics 	Cu: tarnishing of surface, esp underside of bent coupon; Ag: shiny - ok; Pb: overall hazy white; white bubbly corrosion on outer end with red tinge
Decoupage Collage Gel + Lama Li Nepal Paper- thin natural + Kasuiri Paper 	 	 	Fail 	2003/11/26 	NMAI 	Oddy Test 	 	Prepared by Carol Reuter; double layer. 	graphics 	Cu: Darkened; violet discolor; still shiny; Ag: Shiny - ok; Pb: overall even white corrosion
Decoupage Collage Gel + Lama Li Nepal Paper- thin natural + Kasuiri Paper 	 	 	Fail 	2003/11/26 	NMAI 	Oddy Test 	 	Prepared by Carol Reuter; double layer. 	graphics 	Cu: Darkened; violet discolor; still shiny; Ag: Shiny - ok; Pb: overall even white corrosion
IP 7300 Permacolor Permafles, Lustre Vinyl 	MACtac. Phone: 1-866-2MACtac 	 	Pass 	2003/11/26 	NMAI 	Oddy Test 	 	 	graphics 	Cu: beginning to dull, slightly darkened, violet & green/blue tinge discolor; Ag: Shiny - ok; Pb: Slightly darkened - ok
IP 7300 Permacolor Permafles, Lustre Vinyl 	MACtac. Phone: 1-866-2MACtac 	 	Pass 	2003/11/26 	NMAI 	Oddy Test 	 	Corrosion from condensation 	graphics 	Cu: beginning to dull, slightly darkened, violet & green/blue tinge discolor; Ag: Shiny - ok; Pb: slightly darkened, white corrsion at ends, probably condensation problem
Kasuiri Paper 	 	 	Pass 	2003/11/26 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Shiny - ok; Ag: Shiny - ok; Pb: Slightly darkened - ok
Kasuiri Paper 	 	 	Pass 	2003/11/26 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Shiny - ok; Ag: Shiny - ok; Pb: Slightly darkened - ok
Lama Li Nepal Paper- thin natural 	 	 	Pass 	2003/11/26 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Shiny. Black corrosion on outer end from condensation; Ag: shiny- ok; Pb: Slightly darkened - ok
Lama Li Nepal Paper- thin natural 	 	 	Pass 	2003/11/26 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Shiny. Black corrosion on outer end from condensation; Ag: shiny- ok; Pb: Slightly darkened - ok
Ethafoam Trirod 	 	 	Pass 	2003/11/10 	NMAI 	Oddy Test 	 	Concerned that both samples showed some slight corrosion, close to dulling on Cu; didn't test as well as some other samples in batch 	construction/wood 	Cu: very slightly darkened -stil shiny; Ag: shiny - ok; Pb: Slightly darkened - ok
Ethafoam Trirod 	 	 	Pass 	2003/11/10 	NMAI 	Oddy Test 	 	Concerned that both samples showed some slight corrosion, close to dulling on Cu; didn't test as well as some other samples in batch; possible condensation prob; some water found under Cu coupon 	construction/wood 	Cu: slightly darkened, some black corrosion inner end; dulled in underside; Ag: shiny - ok; Pb: Slightly darkened - ok
Gudy 909 Neschen 	Neschen USA 	 	Fail 	2003/11/10 	NMAI 	Oddy Test 	 	 	graphics 	Cu: darkened and dulled; slight green color; some raised recording; Ag: shiny - ok; Pb: compact even coating of lead carbonate corrosion
Gudy 909 Neschen 	Neschen USA 9800 W. York, Wichita, KS 67215 Toll-Free 877.637.2436 Phone 316.522.9438 Fax 316.522.9486 www.neschenusa.com 	 	Fail 	2003/11/10 	NMAI 	Oddy Test 	 	 	graphics 	Cu: darkened and dulled; Ag: shiny - ok; Pb: compact even coating of lead carbonate corrosion
Macal 9700 etched vinyl color 	 	 	Pass 	2003/11/10 	NMAI 	Oddy Test 	 	tested better than controls 1 & 3 	graphics 	Cu: slight amount of black corrosion inside corner; Ag: shiny - ok; Pb: darkened - ok
Macal 9700 etched vinyl color 	 	 	Pass 	2003/11/10 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: darkened - ok
3M overlaminate 	 	 	Fail 	2003/09/15 	NMAI 	Oddy Test 	 	5 week test due to vacation; tested better than the failed control 	graphics 	Cu: still shiny, but beginning thin film of black corrosion; Ag: shiny - ok; Pb: darkened; even layer of white corrosion
3M overlaminate 	 	 	Fail 	2003/09/15 	NMAI 	Oddy Test 	 	5 week test due to vacation; tested better than the failed control 	graphics 	Cu: still shiny, but beginning thin film of black corrosion; Ag: shiny - ok; Pb: darkened; beginning thin layer of whtie corrosion
Permacolor, Permagard IP 7300 Lustre 	MacTac 	 	Fail 	2003/09/15 	NMAI 	Oddy Test 	 	5 week test due to vacation 	graphics 	Cu: surface dulled overall; Ag: shiny - ok; Pb: even white corrosion overall
Permacolor, Permagard IP 7300 Lustre 	MacTac 	 	Fail 	2003/09/15 	NMAI 	Oddy Test 	 	5 week test due to vacation 	graphics 	Cu: surface dulled overall; Ag: shiny - ok; Pb: even white corrosion overall; reddish spots, especially under bend in metal
Overlaminate GBC Octiva 	GBC 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - Lexan tested better than Octiva, A-D strip test: no change; pH indicator paper: no change 	graphics 	Cu: Darker than control, slightly dulled, violet discoloration; Ag: shiny - ok; Pb: thin layer of white corrosion
Overlaminate GBC Octiva 	GBC 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - Lexan tested better than Octiva, A-D strip test: no change; pH indicator paper: no change 	graphics 	Cu: Darker than control, slightly dulled, violet discoloration; Ag: shiny - ok; Pb: like # 3, but more white corrosion
Overlaminate Lexan 	Lexan 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - Lexan tested better than Octiva, A-D strip test: 0-1, pH indicator paper: no change 	graphics 	Cu: Darker than control, shiny, violet discoloration; Ag: shiny - ok; Pb: thin layer of white corrosion
Overlaminate Lexan 	Lexan 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - Lexan tested better than Octiva, A-D strip test: 0-1, pH indicator paper: no change 	graphics 	Cu: Darker than control, shiny, violet discoloration (more than #3); black spot on corner away from sample may be water drop; Ag: shiny - ok; Pb: like # 3, but more white corrosion
Marmorette Linoleum 19022 Caspian Blue 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 2, pH indicator paper: 4 	other/Flooring 	Cu: Uniform blackening & dulling; Ag: shiny - ok; Pb: Overall thick layer white corrosion; coupon broke
Marmorette Linoleum 19022 Caspian Blue 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 2, pH indicator paper: 4 	other/Flooring 	Cu: Darkened; still shiny; Ag: shiny - ok; Pb: Overall thick layer white corrosion; yellow color, bubbling
Marmorette Linoleum 19028 Midnight Blue 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 1, pH indicator paper: between 4 & 5 	other/Flooring 	Cu: Darkened; still shiny; Ag: shiny - ok; Pb: Overall layer white corrosion
Marmorette Linoleum 19028 Midnight Blue 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 1, pH indicator paper: between 4 & 5 	other/Flooring 	Cu: Darkened; still shiny; Ag: shiny - ok; Pb: Overall layer white corrosion
Marmorette Linoleum 19056 Terrazo Gray 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 1, pH indicator paper: 4 	other/Flooring 	Cu: Darkened; still shiny; Ag: shiny - ok; Pb: Overall thick layer white corrosion; bubbling
Marmorette Linoleum 19056 Terrazo Gray 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 1, pH indicator paper: 4 	other/Flooring 	Cu: Darkened; still shiny; Ag: shiny - ok; Pb: Overall thick layer white corrosion; yellow color, bubbling
Marmorette Linoleum 19063 Dusty Lilac 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 2, pH indicator paper: 4 	other/Flooring 	Cu: Uniform blackening & dulling; Ag: shiny - ok; Pb: Overall thick layer white corrosion
Marmorette Linoleum 19063 Dusty Lilac 	Armstrong 	 	Fail 	2003/09/02 	NMAI 	Oddy Test 	 	No Teflon holder - 19028 & 19056 tested slightly better than others, A-D strip test: 2, pH indicator paper: 4 	other/Flooring 	Cu: Darkened; still shiny; Ag: shiny - ok; Pb: Overall thick layer white corrosion; yellow color, bubbling
Foam Fair Minicel block 'skinned' 	 	 	Pass 	2003/08/27 	NMAI 	Oddy Test 	 	Used MSC oven - No Teflon holder used 	construction/wood 	Cu: Shiny- ok; Ag: shiny - ok; Pb: Darkened; blue tinge - ok
Foam Fair Minicel 'skin' 	 	 	Fail 	2003/08/27 	NMAI 	Oddy Test 	 	Used MSC oven - No Teflon holder used 	construction/wood 	Cu: slight beginnings of black film; slightly dulled; Ag: shiny - ok; Pb: Darkened - ok
Magnetic Strip adhesive backing 	 	 	Pass 	2003/08/27 	NMAI 	Oddy Test 	 	Used MSC oven - No Teflon holder used 	fastener 	Cu: Slightly darkened; still shiny; Ag: shiny - ok; Pb: Darkened; slightly dull
Polycarbonate display film DMBPC 12 	 	 	Fail 	2003/08/27 	NMAI 	Oddy Test 	 	Used MSC oven - No Teflon holder used 	graphics 	Cu: Darkened, still shiny but beginning to dull; Ag: shiny - ok; Pb: Darkened; very thin, even film of white corrosion
Thermaflex 	 	 	Fail 	2003/08/27 	NMAI 	Oddy Test 	 	Used MSC oven - No Teflon holder used 	graphics 	Cu: Dark gray spots (deposits?) on one end; dulling of metal ; Ag: shiny - ok; Pb: White & orange corrosion products
UV Display film DMBF5 	 	 	Fail 	2003/08/27 	NMAI 	Oddy Test 	 	Used MSC oven - No Teflon holder used 	graphics 	Cu: Darkened, still shiny but beginning to dull; Ag: shiny - ok; Pb: Darkened; very thin, even film of white corrosion
Thermaflex 	 	 	Fail 	2003/08/18 	NMAI 	Oddy Test 	 	possible condensation on Cu coupon - tested much better than previously, compare to other graphics to determine which is best to recommend, A-D testing: no change, pH indicator paper: no change 	graphics 	Cu: Shiny, but with small amount of spotting on bottom with black color - may be condensation problem; Ag: shiny - ok; Pb: Overall even white corrosion with reddish tint
Thermaflex 	 	 	Fail 	2003/08/18 	NMAI 	Oddy Test 	 	tested much better than previously, compare to other graphics to determine which is best to recommend, A-D testing: no change, pH indicator paper: no change 	graphics 	Cu: Shiny - ok; Ag: shiny - ok; Pb: Overall even white corrosion with reddish tint
Photo rag paper with ink print color 	Unkown 	 	Pass 	2003/08/18 	NMAI 	Oddy Test 	 	No water present - same appearance as #4, A-D testing: no change, pH indicator paper: no change 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: darker than control - brownish color
Photo rag paper with ink print color 	Unkown 	 	Pass 	2003/08/18 	NMAI 	Oddy Test 	 	A-D testing: no change, pH indicator paper: no change 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: darker than control - brownish color
Photo rag paper with ink print in B&W 	Unkown 	 	Pass 	2003/08/18 	NMAI 	Oddy Test 	 	No water present, A-D testing: no change, pH indicator paper: no change 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: darker than control - brown-violet color - less brown than # 3&4
Photo rag paper with ink print in B&W 	Unkown 	 	Pass 	2003/08/18 	NMAI 	Oddy Test 	 	A-D testing: no change, pH indicator paper: no change 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: darker than control - brown-violet color - less brown than # 3&4
FoamFair Minicel 	 	 	Fail 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door, A-D strip test: slight greenish tinge on block of foam tested. No change on the 'skin' tested, pH indicator paper: pH 6 on the block tested. pH between 5-6 for skin and control.	construction/wood 	Cu: surface dulled, beginning black corrosion bottom; Ag: shiny - ok; Pb: even spread of white corrosion on bottom, also under drop at top
FoamFair Minicel 	 	 	Fail 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door, A-D strip test: slight greenish tinge on block of foam tested. No change on the 'skin' tested, pH indicator paper: pH 6 on the block tested. pH between 5-6 for skin and control.	construction/wood 	Cu: Surface dulled more than 11, beginng black corrosion bottom; Ag: shiny - ok; Pb: darkened, violet color, white corrosion on bottom
3M low-profile dual lock 	 	 	Pass 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	fastener 	Cu: shiny - ok; Ag: shiny - ok; Pb: slightly darkened, violet tinge
Brillianized Vivak 	 	 	Pass 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: slightly darkened
Instashield UV lustre 	 	 	Fail 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	Graphics 	Cu: surface dulled on top; Ag: shiny - ok; Pb: Darkened, mat apppearance overall
Instashield UV lustre 	 	 	Fail 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	graphics 	Cu: surface dulled, black corrosion bottom, condensation problem; Ag: shiny - ok; Pb: white corrosion overall with orange crystals
Polycarbonate display film DMBPC 12 	 	 	Fail 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: darkened, white corrosion half way up, orange tinge to upper corrosion
Polycarbonate display film DMBPC 12 	 	 	Fail 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: evenly distributed white corrosion, yellow tinge, not dense
UV Display film DMBF5 	 	 	Pass 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: slightly darkened, violet tinge
UV Display film DMBF5 	 	 	Pass 	2003/07/18 	NMAI 	Oddy Test 	 	Condensation problems for about 1/2 of batch - mainly those nearest the oven door. 	graphics 	Cu: shiny - ok; Ag: shiny - ok; Pb: slightly darkened, white corrosion on bottom and under drop
Crystal Clear Surface protectors silicone self-adhesive stopper 	Master Caster http://www.mastermfgco.com/ 	staples office supplies 	pass 	2010/05/04 	NMAI 	Oddy Test 	 	condensation problems caused substantial corrosion on non-contact samples, A-D strip test pass 	foam/padding 	Cu: substantial blackening overall; Ag: minor scattered yellow; Pb: extensive white & yellow crystals
Crystal Clear Surface protectors silicone self-adhesive stopper 	Master Caster http://www.mastermfgco.com/ 	staples office supplies 	pass 	2010/05/04 	NMAI 	Oddy Test 	 	condensation problems caused substantial corrosion on non-contact samples, A-D strip test pass 	foam/padding 	Cu: reddened; Ag: minor scattered yellow; Pb: minor white & yellow crystals
Crystal Clear Surface protectors silicone self-adhesive stopper 	Master Caster http://www.mastermfgco.com/ 	staples office supplies 	pass 	2010/05/04 	NMAI 	Oddy Test 	 	condensation problems caused substantial corrosion on non-contact samples, A-D strip test pass 	foam/padding 	Cu: reddened; Ag: no change; Pb: no change
Crystal Clear Surface protectors silicone self-adhesive stopper 	Master Caster http://www.mastermfgco.com/ 	staples office supplies 	pass 	2010/05/04 	NMAI 	Oddy Test 	 	condensation problems caused substantial corrosion on non-contact samples, A-D strip test pass 	foam/padding 	Cu: reddened; Ag: no change; Pb: no change
Thermaflex 	 	 	Fail 	2003/07/08 	NMAI 	Oddy Test 	 	Condensation problems for the whole test batch. Shell vial not used for water. Coupons with localized corrosion like control passed. 	graphics 	Cu: Black corrosion under droplets. Shiny. Like control.; Ag: Shiny - ok; Pb: Even deposition of white and orange corrosion all over coupon.
Appleply - Aldur core - maple face 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Slightly darkened, off white corrosion, large crystal growth
Appleply - Aldur core - maple face 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Slightly darkened, off white corrosion, large crystal growth
Appleply - birch face 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shinyspot with slight corrosion around a drop mark - ok; Ag: shiny - ok; Pb: Slightly darkened, white corrosion, large crystal growth
Appleply - birch face 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Slightly darkened, white corrosion, large crystal growth
Appleply - Hardwood core - Maple face 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	This sample tested better than similar substrates in the same batch 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Covered in even layer of white corrosion
Appleply - Hardwood core - Maple face 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	This sample tested better than similar substrates in the same batch 	construction/wood 	Cu: Slightly darker, shinyspot with slight corrosion around a drop mark - ok; Ag: shiny - ok; Pb: Covered in even layer of white corrosion
Birch Ply 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: very darkened - ok
Birch Ply 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Slightly darkened, white corrosion, large crystal growth
Euroform - North American Plywood 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	This sample tested better than similar substrates in the same batch 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Slightly darkened, white corrosion
Euroform - North American Plywood 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	This sample tested better than similar substrates in the same batch 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Slightly darkened, white corrosion
Finland Birch - North American Plywood 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: slightly darkened, violet color, shiny; Ag: shiny - ok; Pb: Dense even coating of white corrosion
Finland Birch - North American Plywood 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: slightly darkened, violet color, shiny; Ag: shiny - ok; Pb: Dense even coating of white corrosion
Medex Medford 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: White corrosion with heavy crystal growth.
Medex Medford 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: White corrosion with heavy crystal growth.
Medex NC 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	Water present, A-D strip test: 1 green, pH indicator paper: 4 	construction/wood 	
Medex NC 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	No water present, A-D strip test: 1 green, pH indicator paper: 4 	construction/wood 	
Medex NC 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	Water present, A-D strip test: 1 green, pH indicator paper: 4 	construction/wood 	
Medex NC 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	No water present, A-D strip test: 1 green, pH indicator paper: 5 	construction/wood 	
Signal MDO 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Heavy white corrosion with loss of structure
Signal MDO 	 	 	Fail 	2003/06/25 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Heavy white corrosion with loss of structure
Unkown white foam 	Unkown 	 	Pass 	2003/06/25 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Darkened - ok
Unkown white foam 	Unkown 	 	Pass 	2003/06/25 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Darkened - ok
ScothCal 22 	3M made for Gerber Scientific Products 	 	Pass 	2003/06/25 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Darkened, lsight white haze on bottom - ok
ScothCal 22 	3M made for Gerber Scientific Products 	 	Pass 	2003/06/25 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Slightly darker, shiny - ok; Ag: shiny - ok; Pb: Darkened - ok
Painted & silk screened vinyl with pressure sensitive adhesive 	 	 	Fail 	2003/06/05 	NMAI 	Oddy Test 	 	very strong fresh paint smell when opened 	graphics 	Cu: very dark violet color, green streaks like oil slick; Ag: Not tested; Pb: very dark, white corrosion
Painted & silk screened vinyl with pressure sensitive adhesive 	 	 	Fail 	2003/06/05 	NMAI 	Oddy Test 	 	very strong fresh paint smell when opened 	graphics 	Cu: very dark violet color, green streaks, worse than Sample 10; violet waxy substance bottom; Ag: Not tested; Pb: very yellow raised corrosion on bottom; condensation probs
Printed paper from Exhibits 	 	 	Pass 	2003/06/05 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny; Ag: Not tested; Pb: darker than control
Printed paper from Exhibits 	 	 	Pass 	2003/06/05 	NMAI 	Oddy Test 	 	 	graphics 	Cu: shiny; Ag: Not tested; Pb: darker than control, some white corrosion bottom, may be condensation
Gudebrod Kevlar thread #1242BS Black size 1 	Gudebrod, Portstown, PA 	 	PASS 	2003/05/18 	NMAI 	Oddy Test 	 	 	fastener 	Cu: shiny - slightly darker than control - ok; Ag: shiny ; Pb: darkened - ok
Gudebrod Kevlar thread #1242BS Black size 1 	Gudebrod, Portstown, PA 	 	PASS 	2003/05/18 	NMAI 	Oddy Test 	 	 	fastener 	Cu: shiny - slightly darker than control - ok; Ag: shiny ; Pb: darkened - ok
Instashield matte pressure senstivie vinyl laminating film 	Quality Mounting & Laminating Systems, Inc. 	 	FAIL 	2003/05/18 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Surface darkened to gray, loss of shine; Ag: shiny; Pb: even coating of lead carbonate corrosion overall
Instashield matte pressure senstivie vinyl laminating film 	Quality Mounting & Laminating Systems, Inc. 	 	FAIL 	2003/05/18 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Surface darkened slightly, loss of shine; Ag: shiny; Pb: even coating of lead carbonate corrosion along center length of coupon
Instashield Velvet Polycarbonate pressure sensitive vinyl laminating film 	Quality Mounting & Laminating Systems, Inc. 	 	FAIL 	2003/05/18 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Surface cloudy, whitish; Ag: shiny; Pb: compact even coating of lead carbonate corrosion
Accuflex beading wire 1681 BS 	see above 	 	PASS 	2003/05/16 	NMAI 	Oddy Test 	 	Condensation problems.Left in oven 1 week longer than normal for T of 60 C 	fastener 	Cu: slightly darkened, shiny, slight dark-brown/black corrosion on bottom corner; Ag: lead carbonate on lower corner; Pb: shiny
Accuflex beading wire 1681 BS 	 	 	PASS 	2003/05/16 	NMAI 	Oddy Test 	 	Condensation problems.Left in oven 1 week longer than normal for T of 60 C 	fastener 	Cu: slightly darkened, shiny, slight black corrosion on bottom corner, slight haze on surface; Ag: lead carbonate on lower corner; Pb: shiny
Accuflex beading wire 9722/30 	 	 	PASS 	2003/05/16 	NMAI 	Oddy Test 	 	Condensation problems.Left in oven 1 week longer than normal for T of 60 C 	fastener 	Cu: slightly darkened, shiny, slight black corrosion on bottom corner, slight haze on surface; Ag: lead carbonate on lower corner; Pb: shiny
Accuflex beading wire 9722/30 	 	 	PASS 	2003/05/16 	NMAI 	Oddy Test 	 	Condensation problems.Left in oven 1 week longer than normal for T of 60 C 	fastener 	Cu: slightly darkened, shiny, slight black corrosion on bottom corner, slight haze on surface; Ag: lead darkened - ok; Pb: shiny
Parachute cord 1906 BS 	 	 	PASS 	2003/05/16 	NMAI 	Oddy Test 	 	Condensation problems.Left in oven 1 week longer than normal for T of 60 C 	fastener 	Cu: Mostly shiny, slight haze, darkened slightly; Ag: shiny; Pb: darkened
Parachute cord 1906 BS 	 	 	PASS 	2003/05/16 	NMAI 	Oddy Test 	 	Condensation problems.Left in oven 1 week longer than normal for T of 60 C 	fastener 	Cu: Mostly shiny, slight haze, darkened slightly; Ag: shiny; Pb: darkened, small spot of corrosion bottom corner -condensation probs
Magic display paper 	InteliCoat Technologies, LLC 700 Crestdale Street, Matthews, NC 28105 Phone: 800-688-9171 or 800-343-0818 Fax: 704-845-4307 or 800-861-4128 http://www.intelicoat.com 	 	Pass 	2003/05/07 	NMAI 	Oddy Test 	 	 	graphics 	Cu: Slight darkening, shiny; Ag: Shiny; Pb: darkened, blue/violet color
Antistat plastic 	 	 	Pass 	2003/05/07 	NMAI 	Oddy Test 	 	 	other 	Cu: Shiny, slightly darkened; Ag: Shiny; Pb: darkened
Antistat plastic 	 	 	Pass 	2003/05/07 	NMAI 	Oddy Test 	 	 	other 	Cu: Shiny, slightly darkened; Ag: Shiny; Pb: darkened
Blue board 	 	 	Pass 	2003/05/07 	NMAI 	Oddy Test 	 	 	other/construction paper board 	Cu: Shiny, slightly darkened; Ag: Shiny; Pb: Darkened, ok
Blue board 	 	 	Pass 	2003/05/07 	NMAI 	Oddy Test 	 	 	other/construction paper board 	Cu: Shiny, violet color; Ag: Shiny; Pb: Darkened, blu-violet color, ok
Volara black 	Voltek www.sekisuivoltek.com/products/volara.php 	 	Pass 	2003/04/07 	NMAI 	Oddy Test 	 	 	foam/padding 	Cu: shiny, violet color; Ag: shiny; Pb: bluish color
Dow Corning vacuum grease 	www.dowcorning.com 	 	Pass 	2003/04/07 	NMAI 	Oddy Test 	 	 	other 	Cu: Shiny; Ag: Shiny, darker where grease covers metal; Pb: darkened, especially where grease covers metal
nitrile glove 	 	 	Pass 	2003/04/07 	NMAI 	Oddy Test 	 	 	other 	Cu: Shiny; Ag: Shiny; Pb: darkened
Corrosion intercept stretch 	 	 	Pass 	2003/04/07 	NMAI 	Oddy Test 	 	 	scavenger 	Cu: shiny; Ag: shiny; Pb: darkened, violet color
Appleply Birch 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Appleply Birch 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Exterior Baltic Birch 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Exterior Baltic Birch 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Exterior Yellow Pine 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Exterior Yellow Pine 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Red Oak 	 	 	fail 	2003/04/03 	NMAI 	Oddy Test 	 	 	construction/wood 	
Hoover FRPI - Pyroguard 	likely to be yellow pine, with a phenol formaldehyde resin (from phone conversation with Steve Hill) 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Dark bue-green spots on the back of the coupon; Ag: none; Pb: White corrosion, crumbling
Hoover FRPI - Pyroguard 	likely to be yellow pine, with a phenol formaldehyde resin (from phone conversation with Steve Hill) 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: Black on contact edge; Ag: none; Pb: disintegrated
Medex NC 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: none; Ag: none; Pb: Covered in white corrosion, but intact
Medex NC 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood 	Cu: slight darkening on edges; Ag: none; Pb: Yellow- white corrosion, non-contact parts crumbling
Benwood Staysclear 423 on Medex NC 	Benjamin Moore 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Lighter in colour than control; Ag: none; Pb: white corrosion, crumbling
Benwood Staysclear 423 on Medex NC 	Benjamin Moore 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	a mess - the lead disintegrated over the copper and the silver 	construction/wood & barrier 	
Benwood Staysclear 423 on Medex NC with Crafton Paint 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Lighter in colour than control; Ag: none; Pb: white corrosion, crumbling
Benwood Staysclear 423 on Medex NC with Crafton Paint 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	cu and ag coupons covered in Pb corrosion 	construction/wood & barrier 	
Microchamber Emulsion on Hoover FRPI 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Turquiose and black areas; Ag: none; Pb: White corrosion, falling apart
Microchamber Emulsion on Hoover FRPI 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: turquoise-green irridesence; Ag: slight yellow cast; Pb: White corrosion, falling apart
Microchamber Emulsion on Medex NC 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Lighter in colour than control; Ag: none; Pb: white corrosion, crumbling
Microchamber Emulsion on Medex NC 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: pink, blue and black irridesence; Ag: brown marks; Pb: covered in white corrosion, crumbling
Microchamber emulsion on Medex NC with Crafton paint 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Brown cast over coupon; Ag: none; Pb: White corrosion, crumbling
Pyrologistix WoodSafe on Medex NC 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Lighter in colour than control; Ag: Duller than control; Pb: White corrosion, falling apart
Pyrologistix WoodSafe on Medex NC 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Darker, purple irridesence; Ag: black on edge; Pb: white corrosion, falling apart
Sancure 878 on Medex NC 	Sancure: Noveon, Inc, 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: lighter in colour than control; Ag: none; Pb: white corrosion, crumbling
Sancure 878 on Medex NC 	Sancure: Noveon, Inc, 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: irridesence, brown marks; Ag: brown marks; Pb: covered in white corrosion
Sancure 878 on Medex NC with Crafton 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	 	construction/wood & barrier 	Cu: Lighter in colour than control; Ag: none; Pb: Covered in white corrosion, still intact
Sancure 878 on Medex NC with Crafton 	 	 	FAIL 	2003/03/26 	NMAI 	Oddy Test 	 	lead corrosion ran onto copper and silver coupons 	construction/wood & barrier 	
Appleply -Birch 	made by States Industries, with a urea formaldehyde resin 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	better than any other wood product tested to date. Seal and monitor lead materials 	construction/wood 	Cu: none; Ag: none; Pb: white-yellow ""spikes"" growing from coupon, coupon intact
Appleply-Birch 	made by States Industries, with a urea formaldehyde resin 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	better than any other wood product tested to date. Seal and monitor leamaterials 	construction/wood 	Cu: none; Ag: none; Pb: white-yellow ""bubbles"" growing from coupon, coupon intact
Appleply-Birch 	made by States Industries, with a urea formaldehyde resin 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	better than any other wood product tested to date. Seal and monitor lead materials 	construction/wood 	Cu: none; Ag: none; Pb: thin layer of white-yellow corrosion, coupon intact
Appleply-Birch 	made by States Industries, with a urea formaldehyde resin 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	better than any other wood product tested to date. Seal and monitor lead materials 	construction/wood 	Cu: none; Ag: none; Pb: spots of white-yellow corrosion, coupon intact
Medex NC 	 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use with lead and possibly copper 	construction/wood 	; Pb: covered in white corrosion, falling apart
Medex NC 	 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use with lead and possibly copper 	construction/wood 	Cu: brownish cast; Pb: covered in white corrosion, falling apart
Medex NC 	 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use with lead and possibly copper 	construction/wood 	; Pb: white corrosion, falling apart
Medex NC 	 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use with lead and possibly copper 	construction/wood 	Cu: brownish cast; Pb: white corrosion, falling apart
Woodstalk 	made with a polyurethane binder 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use around any metals 	construction/wood 	Cu: brown/grey cast; Ag: blue/black cast; Pb: white corrosion, falling apart
Woodstalk 	made with a polyurethane binder 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use around any metals 	construction/wood 	Cu: brownish cast; Ag: blue/black cast - brown where the coupon contacted the woodstalk; Pb: white corrosion, falling apart
Woodstalk 	made with a polyurethane binder 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use around any metals 	construction/wood 	Cu: brownish cast; Ag: blue/black cast; Pb: white corrosion, falling apart
Woodstalk 	made with a polyurethane binder 	 	FAIL 	2003/03/15 	NMAI 	Oddy Test 	 	not for use around any metals 	construction/wood 	Cu: brownish cast; Ag: blue/black cast - brown where the coupon contacted the woodstalk; Pb: White corrosion, falling apart
Medex NC 	 	 	fail 	2003/02/24 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medex NC 	 	 	fail 	2003/02/24 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medex NC 	 	 	fail 	2003/02/24 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medite II 	 	 	fail 	2003/02/24 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medite II NC 	 	 	fail 	2003/02/24 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medex NC 	 	 	fail 	2003/01/20 	NMAI 	Oddy Test 	 	 	construction/wood 	
FRPI stud 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
FRPI stud 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
FRPI stud 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
FRPI stud 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medex NC 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medex NC 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Medex NC 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Red oak 	 	 	Fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Red oak 	 	 	Fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Red oak 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Red oak 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	construction/wood 	
Dye sublimated vinyl 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	graphics 	
Dye sublimated vinyl 	 	 	fail 	2003/01/10 	NMAI 	Oddy Test 	 	 	graphics 	
Pemko Silicon seal S77C25 	Pemko pemko.com 	 	pass 	2008/04/01 	NMAI 	Oddy Test 	 	adhesive backed, adhesive unknown 	caulk/gasket 	
Pemko Silicon seal S77C26 	pemko.com 	 	pass 	2008/04/01 	NMAI 	Oddy Test 	 	adhesive backed, adhesive unknown 	caulk/gasket 	
FlexFoam-It 25 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/03 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	foam/padding 	
FlexFoam-It X 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/03 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	foam/padding 	
Foam-It 10 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/03 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	foam/padding 	
Foam-It 3 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/03 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	foam/padding 	
Foam-It 8 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/03 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	foam/padding 	
Color Match Series 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/19 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	other - mold making material for mounts 	
Crystal Clear Series 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/19 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	other - mold making material for mounts 	
Shell Shock - Brushable Urethane Plastic 	Smooth-On; www.smooth-on.com 	 	fail 	2007/06/19 	NMAI 	Oddy Test 	 	Material not tested due to urethane in chemical composition - urethane will fail 	other - mold making material for mounts 	
Chemcast® Cell Cast Acrylic Sheet 	Plastiglas de Mexico http://www.plastiglas.com.mx/ 	 	Pass 	2017/08/25 	NMAI 	Oddy Test 	 	A-D strip test: no change 	graphics 	
Foamed Ridgid Polyvinyl Chloride sheet PALIGHT®, PALIGHT®,Trimboard, PALFOAM™, PALTOP™ 	PALRAM Industries Ltd. http://www.palram.com/ 	 	Pass 	2017/08/25 	NMAI 	Oddy Test 	 	A-D strip test: no change 	graphics 	
DigiMag® Vinyl Solvent Inkjet Printable Magnetic Sheet 	magnummagnetics.com 	 	Fail 	2017/10/01 	NMAI 	Oddy Test 	 	A-D strip test: change, fail 	Construction 	
W&W FrothPak 650 Spray foam 	DuPont 	Service Partners 	Fail 	2021/12/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Yellow; Polyurethane insulating spray foam; tack-free in 30 seconds; HFC free, low gwp, no ozone depleting chemicals; sample prepared by supplier; Purchased August 2021 	 	-Polymer - foam - building insulation 	
Unbuffered Interleaving Tissue 741-2436 	Unknown 	University Products 	Fail 	2021/12/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Thin, translucent, unbuffered, acid-free tissue; 16 gm^2; Lot No. 081072; Purchased September 2021 	 	-Paper-based (eg.: folders, cardboard, sheets) 	
Ethafoam 220 	Sealed Air 	Valentine 	Fail 	2021/12/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	White; Strong, resilient, medium-density, closed-cell polyethylene foam; 2.2 pounds per cubic foot; Purchased July 2021 	 	-Polymer - foam - non-building insulation 	
Red Label NS binder board 	WestRock 	LBS 	Fail 	2021/11/12 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	High density binders board made from 100% recycled fiber; 0.098 caliper; purchased September 2021 	 	-Board - Natural (eg: wood, cotton) 	
PrimerOne® binder board 0.098 caliper 	Westrock 	LBS 	Fail 	2021/11/12 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	100% recycled paper from defined sources; paper is different types and lengths of fiber; no heavily dyed fiber included, pulp and water only; 0.098 caliper; purchased September 2021 	 	-Board - Natural (eg: wood, cotton) 	
Sylodamp® SP 10 	Getzner 	Getzner 	Pass 	2021/10/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Yellow; Elastic mixed-cell pore structure foamed polyurethane material for high impact insulation; 12.5 mm thick; purchased August 2021 	 	-Polymer - foam - non-building insulation 	
Sylodamp® SP 30 	Getzner 	Getzner 	Pass 	2021/10/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Green; Elastic mixed-cell pore structure foamed polyurethane material for high impact insulation; 12.5 mm thick; purchased August 2021 	 	-Polymer - foam - non-building insulation 	
Gatorfoam board 	3A Composites 	Pathe Shipping Supplies Company, inc 	Fail 	2021/10/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	White; Rigid foam board, extruded polystyrene foam core bonded between two layers of wood-fiber veneer; 0.5 mm thick; Purchased August 2021 	 	-Board - Plastic/polymeric/synthetic 	
Sylomer® SR 28 	Getzner 	Getzner 	Temporary 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Blue; Elastic polyurethane foam with mixed-cell pore structure for vibration isolation; 12.5mm thick, Purchased 2021 	 	-Polymer - foam - non-building insulation 	
Sylomer® SR 18 	Getzner 	Getzner 	Temporary 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Orange; Elastic polyurethane foam with mixed-cell pore structure for vibration isolation; 12.5mm thick, Purchased 2021 	 	-Polymer - foam - non-building insulation 	
Sylomer® SR 11 	Getzner 	Getzner 	Temporary 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Yellow; Elastic polyurethane foam with mixed-cell pore structure for vibration isolation; 12.5mm thick, Purchased 2021 	 	-Polymer - foam - non-building insulation 	
PolyPlank® LAM, 4.0 PCF density 	Pregis 	Pathe Shipping Supplies Company, inc 	Fail 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	White; Non-abrasive and water-resistant closed-cell polyethylene foam; 2 inches thick, 4.0 pcf density; Purchased August 2021 	 	-Polymer - foam - non-building insulation 	
PolyPlank® LAM, 2.2 PCF density 	Pregis 	Pathe Shipping Supplies Company, inc 	Temporary 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	White; Non-abrasive and water-resistant closed-cell polyethylene foam; 2 inches thick, 2.2 pcf density; Purchased August 2021 	 	-Polymer - foam - non-building insulation 	
Styrofoam™ Brand Extruded Polystyrene (XPS) with reduced GWP 	Dupont 	Lenoble 	Temporary 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Grey; Extruded polystyrene foam; 1 inch thick, R-value 5.0/inch; Purchased July 2021 	 	-Polymer - foam - non-building insulation 	
S82N Polyester Polyurethane 	William T. Burnett & Co. 	Pathe Shipping Supplies Company, inc 	Temporary 	2021/10/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Highly compressible, grey polyester polyurethane foam; 2 inches thick, 32kg/m^3 density; Purchased August 2021 	 	-Polymer - foam - non-building insulation 	
Masa Paper Roll 	Unknown 	Talas 	Temporary 	2021/07/23 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Machine made 100% sulphite paper with a neutral pH and lightly sized, smooth on one side and textured on the other; SKU: TPB062002; 70g/m^2, 43 inch wide by 30 yard roll size; Purchased February 202 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Softwrap(r) Tyvek(r), #2-52 	DuPont 	Masterpak 	Temporary 	2021/07/23 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Non-woven, acid free spunbonded olefin made from high density polyethylene fibers; pH of 7.0 or higher; 1.74 oz/yd^2, 6.6 mils thick; Purchased June 2018 	 	Polymer - membrane (< 1mm thick) 	
Expona Commercial 5056, Light Gray Concrete floor tile 	Polyflor 	Spartan Flooring 	Fail 	2021/07/13 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Grey vinyl tile flooring with a clear PVC wear layer; 2.5mm thick, 203.2 by 1524mm tiles; PVC; Purchased May 2021 	 	Flooring - non-carpet 	
Au Natural, Tuscany TS1 Rustica floor tile 	Allied Tile 	Spartan Flooring 	Temporary 	2021/07/13 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Visually textured, imitation stone vinyl floor tile with clear PVC wear surface; 3mm thick, 305mm by 305mm tiles; Purchased May 2021 	 	Flooring - non-carpet 	
Tyvek® 1443R 	DuPont 	Material Concepts Inc 	Temporary 	2021/07/13 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Uncoated, 6.1 mil, 43gsm, 3" core, soft and fabric-like. Sample received April 2021 	 	Polymer - membrane (< 1mm thick) 	
Expona Commercial 5055, Raw Cement 	Polyflor 	Spartan Flooring 	Temporary 	2021/07/09 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Grey vinyl tile flooring with a clear PVC wear layer; 2.5mm thick, 203.2 by 1524mm tiles; Purchased May 2021 	 	Flooring - non-carpet 	
MRGE Erie DI001 	AVA Flor 	Spartan Flooring 	Temporary 	2021/07/09 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Durable grey vinyl tile flooring; 2.5mm thick; Purchased May 2021 	 	Flooring - non-carpet 	
MRGE Ontario DI004 	AVA Flor 	Spartan Flooring 	Temporary 	2021/07/09 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Durable brown vinyl tile flooring; 2.5mm thick; Purchased May 2021 	 	Flooring - non-carpet 	
Standard Excelon Imperial Texture, 51899031, R338E, cool white 	Armstrong Flooring 	Consolidated Carpet 	Temporary 	2021/06/10 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Visually textured, white vinyl composition tile; 1/8 inch thick, 12 inch by 12 inch tiles; ortho-phthalate and heavy metal free; Purchased December 2017 	 	Flooring - non-carpet 	
Marmoleum Concrete, 3704 Satellite 	Forbo Flooring Systems 	RoundSquare/Beyer Blinder Belle 	Fail 	2021/06/10 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Grey flooring sheet, created from natural, renewable materials; floor covering based on a binder composed of vegetable drying oil (linseed) and natural rosin, mixed with wood flour and limestone pressed on a jute backing, lacquered with waterborne UV cured urethane acrylate hybrid dispersion; 0.1 inch thick, 79 inches wide; Purchased April 2021 	 	Flooring - non-carpet 	
MedinPure (with Diamond 10(r) Technology), H6008 Dolphin 	Armstrong Flooring 	RoundSquare/Beyer Blinder Belle 	Temporary 	2021/06/10 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Grey, PVC-free flooring; 6 feet 7 inch wide rolls up to 98.4 feet long, 1/8 inch thick; plasticizer, ortho-phthalate, halogen, and isocyanate free; Purchased April 2021 	 	Flooring - non-carpet 	
Colorplan White Frost, 350 Gsm 	 	Talas 	Temporary 	2021/05/14 	MMA 	Oddy Test (method: 20191213_B_OT ) 	Acid-free paper with a subtle vellum texture; 100% ECF virgin fiber; 25"x38" sheet size, 350 g/m^2; Purchased 2021 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Colorplan Pristine White, 350 Gsm 	 	Talas 	Temporary 	2021/05/14 	MMA 	Oddy Test (method: 20191213_B_OT ) 	Acid-free paper with a subtle vellum texture; 100% ECF virgin fiber; 25"x38" sheet size, 350 g/m^2; Purchased 2021 	 	Paper-based (eg.: folders, cardboard, sheets) 	
CADPAK HD100, MIL-PRF-131K CLass1 	 	Heritage Packaging 	Temporary 	2021/05/14 	MMA 	Oddy Test (method: 20190130_OT ) 	Heavy duty heat sealable metalized barrier film. silver with writing on outside and green on inside: 60ga biax nylon / 15# LDPE / 30ga foil / 6 mil Polyethylene co-extruded with heavy-duty green Sealant; Chemical Components: nylon, metal foil, polythylene 	 	Polymer - membrane (< 1mm thick) 	
Sintra expanded PVC 	SINTRA 	3A Composites 	Temporary 	2021/05/14 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	White, expanded PVC board; 6mm thick; Purchased April 2021 	 	-Board - Plastic/polymeric/synthetic 	
Mushroom Packaging 	Paradise Packaging Company 	Paradise Packaging Company 	Fail 	2021/01/12 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Replacement for Styrofoam made from hemp hurd and mycelium; 100% compostable; 1 inch thick form; Purchased November 2020 	 	Foam Replacement - Natural (eg: wood, cotton) 	
Usuyo Japanese Paper 	Unknown 	Yoshida Shoten, Co., Ltd. 	Temporary 	2021/01/12 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Machine made, mass produced, Japanese, extremely thin, highly calendared paper; used for interleaving; imported from Kyoto, Japan; Purchased March 2012 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Dartek-Cast Nylon Film, C-917NA 	TC Transcontinental Packaging 	Masterpak 	Temporary 	2021/01/12 	MMA 	Oddy Test (method: 20191213_B_OT ) 	A cast film made from nylon 6,6 and modified with a heat stabilizing additive for use as a carrier, barrier and release film in extreme prolonged high temperature applications; absorbs up to 10% of its weight in moisture, no surface coatings or plasticizers; 3/4 mil thick; Purchased September 2020 	 	Polymer - membrane (< 1mm thick) 	
Strong and Flexible Nylon 12, PA12 	Shapeways 	Shapeways 	Pass 	2020/11/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Strong and flexible nylon 12 plastic, PA12, polyamide, PA2200; 3D printed nylon in custom shape; Purchased September 2020 	 	Polymer - block/bulk/pellet - 3D printed 	
Spaceloft Insulation 	Aspen Aerogels 	Aspen Aerogels 	Fail 	2020/11/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Flexible, nanoporous aerogel blanket insulation; combines silica gel with reinforcing fiber. Comes in 0.2 inch and 0.4 inch thicknesses. Maximum temperature of 390°F. 0.15 g/cc density. R-value of 10.3 per inch. Received January 2020 	 	Polymer - foam - building insulation 	
Grey Silicone SPG w/ Silicone PSA 	Netherland Rubber Company 	Netherland Rubber Company 	Temporary 	2020/11/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Platinum cured silicone foam, reactive foaming process, 1/4" thick, gray silicone sponge w/ silicone PSA and clear release liner. Purchased 2017 	 	Polymer - gasket 	
Cafco Board Foil-Faced 	Isolatek International 	Isolatek International 	Temporary 	2020/11/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	A rigid mineral wool board which combines fire protection, thermal insulation and acoustical control all in one product. R-value of 4.2 R/inch, 0.144 g/mL density. Contains mineral wool, phenolic resin, and urea. Received July 2020 	 	Polymer - foam - building insulation 	
TPU F70D-035TR UV, 3D Print Material 	Keene Village Plastics 	Keene Village Plastics 	Pass 	2020/10/28 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Thermoplastic polyurethane 3D printing material. 6 grams of material was printed prior to printing an addition 6 grams for the Oddy test. Print bed has white glue stick on it for adhesion. This layer was NOT used for the Oddy test. 235°C print temp on 50°C bed with Kapton tape on bed surface on top of the white glue. Received November 2018, printed on 9/11/2020 	 	Polymer - block/bulk/pellet 	
PETG, 3D Print Material 	Keene Village Plastics 	Keene Village Plastics 	Pass 	2020/10/22 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Polyethylene Terephthalate Glycol Modified (PETG) filament 3D printing material. 6 grams of material was printed prior to printing an addition 6 grams for the Oddy test. Print bed has white glue stick on it for adhesion. This layer was NOT used for the Oddy test. 250°C print temp. 85°C bed temp. Received November 2018, printed on 9/11/2020. 	 	Polymer - block/bulk/pellet 	
Vivak Thermoplastic PTEG, Glossy 	Plaskolite, Inc. 	Laird Plastics 	Temporary 	2020/10/16 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Clear thermoplastic sheet, polyethylene terephthalate glycol (PETG); 2mm thick; sample received with protective plastic covering on either side, which was removed before testing; Purchased September 2020 	 	Board - Plastic/polymeric/synthetic 	
HM-43 Akaso Kozo 	Tatsuyuki Kitaoka 	Hiromi Paper 	Fail 	2020/10/02 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	100% Akaso Kozo paper from Tosa Kozo family, handmade in Japan, no coloration added, cooked with lime, board dried. 10.5 g/m^2. Purchased January 2020 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Tyvek 1622E 	Dow 	Material Concepts Inc. 	Temporary 	2020/09/18 	MMA 	Oddy Test (method: 20191213_B_OT ) 	Uncoated, 6.1 mil, 44gsm, 3" core, pin perforated with .025mm - .038mm holes throughout, highly air and moisture permeable, soft and fabric-like. Received June 2020 	 	Polymer - membrane (< 1mm thick) 	
Cafco Board 	Isolatek International 	Isolatek International 	Temporary 	2020/09/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	A rigid mineral wool board which combines fire protection, thermal insulation and acoustical control all in one product. R-value of 4.2 R/inch, 0.144 g/mL density. Contains mineral wool, phenolic resin, and urea. Received July 2020 	 	Board - Composite (eg: drywall) 	
Migrations BBT Diamond 10 Technology Coating, Z3543 	Armstrong Flooring 	Armstrong Flooring 	Temporary 	2020/09/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Biobased non-pvc floor tile, 1.8 inch thickness, 12 inch x 12 inch tiles, Diamond 10 Technology coating, scratch and stain resistant. Received December 2019 	 	Flooring - non-carpet 	
Migrations BBT Diamond 10 Technology Coating, Z3503 	Armstrong Flooring 	Armstrong Flooring 	Temporary 	2020/09/04 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Biobased non-pvc floor tile, 1.8 inch thickness, 12 inch x 12 inch tiles, Diamond 10 Technology coating, scratch and stain resistant. Received December 2019 	 	Flooring - non-carpet 	
Silicone Parchment Release Paper, #2-23 	Unknown 	Masterpak 	Temporary 	2020/08/27 	MMA 	Oddy Test (method: 20191213_B_OT ) 	Non-stick thin parchment release paper, vegetable parchment, silicone-treated on two sides; pH value of 5.5 to 6.5; 100 sheets of 24 inches x 36 inches, 2 mil thick 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Formglas GFRG, Glass Fiber Reinforced Gypsum 	Formglas Products 	Formglas(R) Products 	Temporary 	2020/08/27 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Glass fiber reinforced gypsum board, 'thin cast' alpha gypsum, 1675 kg/m^3; calcium sulfate hemihydrate, glass fiber, portland cement, crystalline silica; oxides of sulfur released when burned; Purchased January 2020 	 	Board- Composite (eg: drywall) 	
Obomodulan 500 	OBO- Werke 	McCausey Specialty Products 	Pass 	2020/04/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Stiff, foamed polyurethane board; density is 500 kg/m3; pink colored; Purchased December 2017 	 	Board - Plastic/polymeric/synthetic 	
Komatex White Matte 	Unknown 	Harbor Sales Inc. 	Temporary 	2020/04/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Rigid foam PVC sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; Prepared on 1/27/2020, cut into strips on table saw and broken/cut into large pieces; Purchased May 2019 	 	Board - Plastic/polymeric/synthetic 	
Komacel White Gloss 4813MCK 	Unknown 	Harbor Sales Inc. 	Pass 	2020/04/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Rigid foam PVC sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; Prepared 1/27/2020, cut into strips on table saw and broken into large pieces; Purchased May 2019 	 	Board - Plastic/polymeric/synthetic 	
Heritage Archival Corrugated Board, E-Flute TPB567017 	Unknown 	Talas 	Temporary 	2020/04/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Acid-free corrugated cardboard; single ply construction; 100% bleached alpha cellulose, potato starch, alkaline reserve (buffer) > 3% calcium carbonate; 1/16" x 8" x 10" sheets; Prepared on 1/27/2020; cut with Exacto knives; Purchased May 2019 	 	Board - Natural (eg: wood, cotton) 	
Davey Board Red Label, #18 	Unknown 	Colophon Book Arts Supply 	Fail 	2020/04/03 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Single ply book board; acid neutral with a pH of 7-8; 20.625" x 30"; Prepared on 1/27/2020, cut with cleaned scissors; Purchased May 2019 	 	Board - Natural (eg: wood, cotton) 	
Neopor GPS Type II Insulation 	BASF 	BASF 	Temporary 	2020/03/27 	MMA 	Oddy Test (method: 20190226_OT_1) 	Graphite polystyrene (GPS) rigid foam insulation, comprised of many small pockets of air within a polymer matrix containing graphite. R-value of 5.0 @ 75°F and 5.2 @ 40°F. ~1 inch thick. Density of 21.6 kg/m3. 1 g of material in each jar. Sample received February 2020 	Color: Gray 	Polymer - foam - building insulation 	
WALLTITE Spray Foam 	BASF 	BASF 	Fail 	2020/03/27 	MMA 	Oddy Test (method: 20190226_OT_1) 	Two-component closed-cell spray polyurethane foam system, zero ozone-depleting blowing agent. Density of 2.0-2.3 pcf, maximum temperature of 180°F. Sample received February 2020. Only 1.5 g of material in each jar. 	Color: Green 	Polymer - foam - building insulation 	
Sponge Aero Rubber Closed Cell EVA Sponge 	Aero Rubber Company Inc 	Spacesaver Corporation 	Fail 	2020/03/26 	MMA 	Oddy Test (method: 20190226_OT_1) 	Black closed cell EVA foam; 1/4 inches thick, 4lb density; tested without adhesive; ethyl vinyl acetate cross-linked polyethylene; Purchased February 2020 	Color: Black 	Polymer - foam - non-building insulation 	
Polyvinyl Print Media, Prime 75CT - Clear 	BILD 	Varidirect 	Fail 	2020/03/26 	MMA 	Oddy Test (method: 20190226_OT_1) 	Flexible PVC floor coating; ceramic(TM) textured surface with satin top coat finish, 100% polyvinyl wear layer, and reverse printing surface - sample with printed green grass; 8 oz/sq ft, 75mil thick; extruded PVC; Purchased January 2020 	Color: Green 	Coating - Floor (eg.: anti-wear, anti-slip) 	
Sequel Rubber Cork, Ebony SQ5013 	Capri Collections 	Capri Collections 	Fail 	2020/03/26 	MMA 	Oddy Test (method: 20190226_OT_1) 	Vulcanized rubber with homogeneous cork content, abrasion resistance; 3 mm thick tiles; Purchased January 2020 	Color: Ebony 	Coating - Floor (eg.: anti-wear, anti-slip) 	
Lens Tissue, J51-Lens 	Unknown 	Legion Paper 	Fail 	2020/03/19 	MMA 	Oddy Test (method: 20190226_OT_1) 	100% rayon, machine made in Japan, neutral pH, no deckles, 12 gsm, sold as 24 inch x 36 inch sheets. Sample received February 2020 	Color: White 	Paper-based (eg.: folders, cardboard, sheets) 	
Sekishu Mare HP-07 	So Kubota 	Hiromi Paper 	Temporary 	2020/03/19 	MMA 	Oddy Test (method: 20180821_B_OT) 	100% Japanese kozo paper, cooked with soda ash, dried on wooden boards, 21.4g/m^2, pH 7.0, unbuffered, no sizing, handmade, hand beaten, inner green and white layer of bark. Purchased January 2020. 	Color: Natural 	Paper-based (eg.: folders, cardboard, sheets) 	
Tek Wipe 	Unknown 	Polistini 	Temporary 	2020/03/19 	MMA 	Oddy Test (method: 20180821_B_OT) 	Non-woven fabric, a blend of 45% polyester and 55% cellulose hydrospun with high tensile strength and without the use of any binders, starches, or thermal binding techniques. Sample received February 2020. 	Color: White 	Polymer - membrane (< 1mm thick) 	
ComfortTherm Fiberglass Insulation R-30 	Johns Manville 	Johns Manville 	Fail 	2020/03/19 	MMA 	Oddy Test (method: 20190226_OT_1) 	Formaldehyde-free plastic wrapped fiberglass batt. Available in either vapor retarder or non-vapor retarder poly-encapsulated plastic casing. 10.25 inch thickness. 30 maximum r-value. Sample received January 2020. 	Color: White 	Building insulation 	
Softwrap Nomex 	DuPont 	Masterpak 	Temporary 	2020/03/19 	MMA 	Oddy Test (method: 20180821_B_OT) 	Synthetic aromatic polyamide polymer wrap permeable to air and water, chemically inert, complete temperature stability, nondusting, flame resistant. 5 mil thickness, 2.0 oz/yd^2. Sample received February 2020. 	Color: White 	Polymer - membrane (< 1mm thick) 	
Ceiling Mirror 	MirrorLite 	MirrorLite 	Fail 	2020/03/05 	MMA 	Oddy Test (method: 20190226_OT_1) 	Lightweight glassless mirror, reflective polyester film metalized with vacuum deposited aluminum stretched over internal foam and adhesive; Purchased January 2020 	Silver mirror 	Board - Composite (eg: drywall) 	
Thermax Xarmor CI Insulation 	Dow 	Dow 	Fail 	2020/03/04 	MMA 	Oddy Test (method: 20190226_OT_1) 	Glass-fiber-reinforced polyisocyanurate foam core with aluminum facing. 4.0 mil embossed exterior foil facer. Maximum use temperature of 250°F, R-value of 6.5 per inch. 2-inch thick sample received January 2020 	Color: Silver 	Polymer - building insulation 	
Thermafiber Ultrabatt FF Insulation 	Owens Corning 	Owens Corning 	Fail 	2020/03/04 	MMA 	Oddy Test (method: 20190226_OT_1) 	Formaldehyde-free mineral wool insulation, non-combustible, moisture-resistant, non-corrosive, non-deteriorating, and mold resistant. 3.0 inch thick sample. Sample received January 2020 	Color: Brown 	Building insulation 	
Thermafiber Ultrabatt Insulation 	Owens Corning 	Owens Corning 	Temporary 	2020/03/04 	MMA 	Oddy Test (method: 20190226_OT_1) 	Mineral wool insulation, non-combustible, moisture-resistant, non-corrosive, non-deteriorating, and mold resistant. 3.5 inch thick sample, R-15. Sample Received January 2020 	Color: Yellow 	Building insulation 	
AP Foil Faced Foam Sheathing 	Johns Manville 	Johns Manville 	Fail 	2020/03/04 	MMA 	Oddy Test (method: 20190226_OT_1) 	Uniform closed-cell polyisocyanurate foam core bonded on each side to a foil facer; one side has a reflective foil facer and the other side a white non-reflective foil facer. Produced with hydrocarbon blowing agent with zero ozone depletion potential and virtually no global warming potential. Free of CFC and HCFC. Service temperature of -100 to 250°F. R-value of 6.0 per inch. Sample received January 2020 	Color: Silver 	Polymer - foam - building insulation 	
Non-Perforated Silverboard Type I 	Amvic System 	Amvic System 	Fail 	2020/03/04 	MMA 	Oddy Test (method: 20190226_OT_1) 	Expanded polystyrene (EPS) covered with a layer of polypropylene reflective lamination on both sides. No off-gassing and does not contain HFCs, CFCs, or HCFCs. R-value of 4.1 @ 75°F and 5.2 @ 0°F. 158°F maximum use temperature. Density of 16 kg/m^3. Sampled received January 2020 	Color: White 	Polymer - foam - building insulation 	
Sintra 	Alusuise Composites 	 	Pass, Permanent 	2011/03/04 	BKM 	Oddy Test 	Moderately expanded closed-cell polyvinyl acetate (PVC) 	 	Board - plastic/polymeric/synthetic 	Copper: Very slightly tarnished, same as control and zinsser shieldz coated sample Lead: Consistent with Control Silver: Consistent with Control
Sintra Coated with 3x Zinsser Shieldz 	Alusuise Composites 	 	Pass, Permanent 	2011/03/04 	BKM 	Oddy Test 	Moderately expanded closed-cell polyvinyl acetate (PVC) 	 	Board - plastic/polymeric/synthetic 	Copper: Slightly tarnished, consistent with control and non-coated sample Lead: Consistent with Control Silver: Consistent with Control
Sintra 	Alusuise Composites 	 	Pass, Permanent 	2011/03/04 	BKM 	Oddy Test 	Moderately expanded closed-cell polyvinyl acetate (PVC) 	 	Fabric - exhibition/woven 	Copper: Slightly tarnished, consistent with control and zionsser shieldz coated sample Lead: Consistent with Control Silver: Consistent with Control
Sintra Coated with 3x Zinsser shieldz 	Alusuise Composites 	 	Pass, Permanent 	2011/03/04 	BKM 	Oddy Test 	moderately expanded closed-cell polyvinyl acetate (PVC) 	 	Fabric - exhibition/woven 	Copper: Slightly tarnished, consistent with control and non-coated sample Lead: Consistent with Control Silver: Consistent with Control
Abatron, Wood Epoxy 	Abatron 	 	Temporary 	2007/08/28 	BKM 	Oddy Test 	Epoxy wood replacement compound; permanent, high strength, parts A and B 	9/26/07 - 64F in chamber 	Paste - filler/binder mixture (non-paint) 	Copper: Slightly red Lead: Marginally more corroded Silver: No data
Abatron, Wood Epoxy 	Abatron 	 	Temporary 	2008/05/08 	BKM 	Oddy Test 	 	9 month cure time ok; would recommend 2 week and cure before inside case; ok for outside of case 	Paste - filler/binder mixture (non-paint) 	Copper: Tarnished Lead: No data Silver: No data
Benchmark Sueded Polyethylene 	Benchmark 	Benchmark 	Pass, Permanent 	2017/06/23 	BKM 	Oddy Test 	Acrylic-adhesive backed sueded polyethylene 	 	Fabric - batting & padding 	Copper: Red, consistent with control Lead: Consistent with Control Silver: Consistent with Control
Clean Seal Gasket EPDM 105 	Clean Seal, Inc. 	Clean Seal, Inc. 	Pass, Permanent 	2017/06/23 	BKM 	Oddy Test 	.438 x .375 Ethylene propylene diene monomer (M-class) rubber, no adhesive 	 	Polymer - gasket 	Copper: Minor darkening with some silver patches of discoloration Lead: Slight white spots of control, otherwise consistent with control Silver: Consistent with Control
Clean Seal Gasket Silicone 8490 	Clean Seal, Inc. 	Clean Seal, Inc. 	Pass, Permanent 	2017/06/23 	BKM 	Oddy Test 	.3125 x .1875 ""D"" plain silicone no adhesive 	Only 1 out of 2 samples opened, inconclusive 	Polymer - gasket 	Copper: Red with some patches of silver discoloration Lead: Slight white spots of corrosion Silver: Consistent with Control
Cleanseal 1153B EPDM 	Clean Seal, Inc. 	Clean Seal, Inc. 	Fail, Unsuitable 	2018/10/05 	BKM 	Oddy Test 	Gasketing 	extended Oddy test - 52 days 	Polymer - gasket 	Copper: Darkened compared to controls and Cleanseal 8598 Lead: Some corrosion Silver: Black tarnish localized at bottom of coupon
Cleanseal 8598P silicone 	Clean Seal, Inc. 	Clean Seal, Inc. 	Pass, Permanent 	2018/10/05 	BKM 	Oddy Test 	Gasketing 	extended Oddy test - 52 days 	Polymer - gasket 	Copper: Darkened slightly compared to control Lead: Consistent with Control Silver: Consistent with Control
Dibond Panel Assembly / Anodized Aluminum Facing 	3A Composites 	 	Pass, Permanent 	2016/08/04 	BKM 	Oddy Test 	Dibond panel 	Copper corrosion appeared the same as on both controls 	Board - plastic/polymeric/synthetic 	Copper: Slightly red but otherwise consistent with control Lead: Consistent with Control Silver: Consistent with Control
Dow Corning 3145 RTV MIL-A-46146 Transparent / Structural Sealant and Adhesive 	Dow Corning 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	Sealant and Adhesive 	Copper corrosion appeared the same as on both controls 	Polymer - adhesive caulk 	Copper: Very minor darkening Lead: Consistent with Control Silver: Consistent with Control
Dow Corning 7091 Black / Structural Adhesive / Sealant 	Dow Corning 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	Sealant and Adhesive 	Copper corrosion appeared the same as on both controls 	Polymer - adhesive caulk 	Copper: Minor darkening Lead: Consistent with Control Silver: Consistent with Control
DOW Corning RTV Sealant 737 Neutral Cure Sealant, 100% Silicone Rubber 	Dow Corning 	 	Fail, Unsuitable 	2018/10/05 	BKM 	Oddy Test 	Sealing casework (SmallCorp cases on the 2nd floor) 	extended Oddy test - 52 days 	Polymer - adhesive caulk 	Copper: Multicolored corrosion Lead: Significantly darker than controls Silver: Consistent with Control
DOW Corning RTV Sealant 737 Neutral Cure Sealant, 100% Silicone Rubber 	Dow Corning 	 	Pass, Permanent 	2018/12/17 	BKM 	Oddy Test 	sealing casework (SmallCorp cases on the 2nd floor) 	 	Polymer - adhesive caulk 	Copper: Darkened slightly compared to control Lead: Consistent with Control Silver: Consistent with Control
coating EuroPolveri RAL 9005 /Powdercoat (Textured) on Steel 	EuroPolveri 	 	Pass, Permanent 	2016/08/04 	BKM 	Oddy Test 	Powdercoated steel 	Copper corrosion appeared the same as on both controls 	Coating - paint & primer 	Copper: Very minor darkening Lead: Consistent with Control Silver:Consistent with Control
Hyflex Foam Gloves by Ansell 911-800 	Ansell 	 	Pass, Permanent 	2009/03/16 	BKM 	Oddy Test 	 	4/13/09: Gloves themselves discolored significantly on foam pads but metals not tarnished. 	Polymer - glove 	Copper: No data Lead: No data Silver: No data
Hyflex Foam Gloves by Ansell 911-800 CE 	Ansell 	 	Pass, Permanent 	2008/12/30 	BKM 	Oddy Test 	Gloves washed 	No change in coupons but color change in glove material, should retest with glove in contact with coupons 	Polymer - glove 	Copper: No data Lead: No data Silver: No data
ILPEA Magnetic Gasket Assembly 	Industrie ILPEA 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	Magnetic gasket for case doors 	Copper corrosion appeared the same as on both controls 	Polymer - gasket 	Copper: Slighty red but otherwise consistent with control Lead: Consistent with Control Silver: Consistent with Control
ILPEA Magnetic Gasket Assembly + 3M VHB / Acrylic Foam Tape 	Industrie ILPEA and 3M 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	2 Materials: Gasket tested in combination w/ Adhesive 	Copper corrosion appeared the same as on both controls 	Polymer - gasket 	Copper: Minor darkening Lead: Consistent with Control Silver: Consistent with Control
ILPEA Magnetic Gasket Assembly + Dow Corning 3145 RTV MIL-A-46146 Transparent / Structural Sealant and Adhesive 	Industrie ILPEA and Dow Corning 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	2 Materials: Gasket tested in combination w/ Adhesive 	Copper corrosion appeared the same as on both controls 	Polymer - gasket 	Copper: Minor darkening Lead: Consistent with Control Silver: Consistent with Control
Kraftmark Pro-Create Professional Sculptors Putty 	Kraftmark 	 	Pass, Permanent 	2008/12/30 	BKM 	Oddy Test 	2 part epoxy putty 	Ok to use if allowed to cure for two weeks. Better to use outside case. 	Paste - filler/binder mixture (non-paint) 	Copper: Date unknown, corroded Lead: No data Silver: No data
Kraftmark Pro-Create Professional Sculptors Putty 	Kraftmark 	 	Pass, Permanent 	2008/12/30 	BKM 	Oddy Test 	2 part epoxy putty (white and grey), similar to pliacre, 60hr air time, 50/50 mix ratio 	Pass if allowed to cure for 2+ weeks. Oddy tested 5/8/08, new Oddy test requested 	Paste - filler/binder mixture (non-paint) 	Copper: No data Lead: No data Silver: No data
Kraftmark Pro-Create Terrain Putty 	Kraftmark 	 	Pass, Permanent 	2008/12/30 	BKM 	Oddy Test 	2 part epoxy putty 	Ok to use with at least two week cure time. Better to use outside case. 	Paste - filler/binder mixture (non-paint) 	Copper: Date unknown, corroded Lead: No data Silver: No data
Kraftmark Pro-Create Terrain Putty 	Kraftmark 	 	Pass, Permanent 	2008/12/30 	BKM 	Oddy Test 	2 part epoxy putty (white and beige), lightweight, 60 hr air time, 50/50 mix 	PASS if allowed to cure for 2 weeks. Oddy tested 5/8/08- new Oddy test requested 	Paste - filler/binder mixture (non-paint) 	Copper: No data Lead: No data Silver: No data
Magic Sculpt 2 Part Epoxy Putty 	Wesco 	 	Pass, Permanent 	2009/03/27 	BKM 	Oddy Test 	Cured for two weeks 	Considered for use in mountmaking 	Paste - filler/binder mixture (non-paint) 	Copper: 4/17/09 was oxidized Lead: No data Silver: No data
Magic Sculpt White 	Wesco 	 	Pass, Permanent 	2009/03/27 	BKM 	Oddy Test 	2 part epoxy putty cured 2 weeks 	Considered for use in mountmaking 	Paste - filler/binder mixture (non-paint) 	Copper: 4/17/09 was oxidized Lead: No data Silver: No data
Medex 	Roseburg 	 	Fail, Unsuitable 	2009/03/27 	BKM 	Oddy Test 	 	 	Board - plastic/polymeric/synthetic 	Copper: No data Lead: 4/17/09 covered in white corrosion products Silver: No data
Neoprene Spring Rubber Sheet 	 	 	Pass, Permanent 	2018/12/17 	BKM 	Oddy Test 	Neoprene rubber sheet, 1/4"" thick, 70A, 200% elongation, plain backing 	One anomaly Lead coupon that corroded very heavily, likely an issue with test conditions 	Polymer - block/bulk/pellet 	Copper: Darkened slightly compared to control Lead: Almost no corrosion Silver: Consistent with Control
OECE 414-9001 / White Back Paint for Glass 	OECE [Organizzazione Economica Commercio Emiliano (Emilia Commerce Economic Organization)] 	 	Pass, Permanent 	2016/08/04 	BKM 	Oddy Test 	White back paint for glass - case material for Goppion cases 	Copper corrosion appeared the same as on both controls 	Coating - paint & primer 	Copper: Very minor darkening Lead: Consistent with Control Silver: Consistent with Control
OECE 414-9001 / White Back Paint for Glass + Dow Corning 7091 Black / Structural Adhesive / Sealant 	OECE [Organizzazione Economica Commercio Emiliano (Emilia Commerce Economic Organization)] and Dow Corning 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	2 Materials: Glass tested in combination w/ Adhesive 	Copper corrosion appeared the same as on both controls 	Other - composite 	Copper: Slightly red but ok Lead: Consistent with Control Silver: Consistent with Control
Pro-Create Terrain Putty (2 part) 	Kraftmark 	 	Pass, Permanent 	2009/03/27 	BKM 	Oddy Test 	2 part epoxy putty cured 2 weeks 	Considered for use in mountmaking 	Paste - filler/binder mixture (non-paint) 	Copper: 4/17/09 oxidized Lead: No data Silver: No data
Promante MC Bond 2K Transparent / Structural Adhesive 	Promanté 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	Structural adhesive 	Cu corrosion appeared the same as on both controls 	Polymer - adhesive caulk 	Pb: No corrosion; 
Cu: minor darkening; 
Ag: no corrosion
SE2040 - 40 Durometer Silicone 	Stockwell Elastomerics 	 	Fail, Unsuitable 	2018/12/17 	BKM 	Oddy Test 	Silicone 	 	Polymer - gasket 	Pb: some white corrosion spots overall, discrete areas of brown corrosion; 
Cu: darkened slightly compared to control; 
Ag: no corosion
Technical Rubber/Viton Tubular Gasket 	Technical Rubber S.R.L 	 	Pass, Permanent 	2016/08/04 	BKM 	Oddy Test 	Gasket 	Cu corrosion appeared the same as on both controls 	Polymer - gasket 	Pb: No corrosion; 
Cu: minor darkening; 
Ag: very slightly yellowed
Technical Rubber / Viton Tubular Gasket + 3M VHB / Acrylic Foam Tape 	Technical Rubber S.R.L and 3M 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	2 Materials: Gasket tested in combination w/ Adhesive 	Cu corrosion appeared the same as on both controls 	Polymer - gasket 	Pb: No corrosion; 
Cu: minor darkening; 
Ag: no corrosion
Technical Rubber / Viton Tubular Gasket + Dow Corning 7091 Black / Structural Adhesive / Sealant 	Technical Rubber S.R.L and Dow Corning 	 	Pass, Permanent 	2016/09/21 	BKM 	Oddy Test 	2 Materials: Gasket tested in combination w/ Adhesive 	Cu corrosion appeared the same as on both controls 	Polymer - gasket 	Pb: No corrosion; 
Cu: slightly red, but okay; 
Ag: no corrosion
Tempur-Pedic 	Tempur-Pedic 	 	Pass, Permanent 	2007/02/14 	BKM 	Oddy Test 	Pressure-relieving swedish mattresses and pillows; Phone: 888-225-7984; lab sample - G0403M 	Great - no tarnish, BUT needs more research for use 	Polymer - foam - non building insulation 	Pb: ; 
Cu: ; 
Ag:
USA Sealing 3/16"" neoprene sponge cord 	USA Sealing 	 	Fail, Unsuitable 	2019/01/25 	BKM 	Oddy Test 	neoprene sponge cord, 3/16"" 	Control lead FAIL 	Polymer - gasket 	Pb: Control lead FAIL; 
Cu: very dark (purple) compared to control; 
Ag: same as control
White Photomount 	Rising - Legion Paper 	 	Pass, Permanent 	2019/09/04 	BKM 	Oddy Test 	4-ply non-buffered 100% cotton rag board 	 	Paper-based (eg. folder, cardboard, sheet) 	Pb: same as control; 
Cu: same as control; 
Ag: same as control
Wilsonart Laminate 	Wilsonart 	 	Pass, Permanent 	2008/12/30 	BKM 	Oddy Test 	decorative surface paper impregnated with melamine resins over Kraft paper core sheets impregnated with phenolic resin 	 	Board - natural (eg. wood, cotton) 	Pb: Date Unknown: no change; 
Cu: Date Unknown: no change; 
Ag: Date Unknown: no change
[http://cameo.mfa.org/wiki/Thermoplastic Wonderflex 	Wonderflex 	 	Fail, Unsuitable 	2019/01/31 	BKM 	Oddy Test 	thermoplastic composite 	inconclusive - re-test recommended before use 	Fabric - batting & padding 	Pb: yellowish corrosion; 
Cu: darkened red/purple slightly more than control; 
Ag: same as control
Wonderflex Fosshape (black) heated with steam from iron 	Wonderflex 	 	Pass, Permanent 	2018/10/05 	BKM 	Oddy Test 	non woven thermoplastic polyester fabric 	extended Oddy test - 52 days. One sample's lid popped off and moisture escaped 	Fabric - batting & padding 	Pb: no corrosion; 
Cu: no corrosion; 
Ag: no corrosion
Wonderflex Fosshape (black) unheated 	Wonderflex 	 	Pass, Permanent 	2018/10/05 	BKM 	Oddy Test 	non woven thermoplastic polyester fabric 	extended Oddy test - 52 days 	Fabric - batting & padding 	Pb: no corrosion; 
Cu: no corrosion; 
Ag: no corrosion
Wonderflex Pro 	Wonderflex Pro 	 	Fail, Unsuitable 	2019/01/31 	BKM 	Oddy Test 	thermoplastic composite 	 	Fabric - batting & padding 	Pb: yellowish corrosion - more than Wonderflex above; 
Cu: darkened red/purple slightly more than control and more than Wonderflex above; 
Ag: same as control
Plexiglas G 	Altuglas International by Arkema Group 	 	PASS, Permanent 	2019/08/06 	FMNH 	Oddy Test 	Cell-cast acrylic sheet: Polymethyl methacrylate copolymer 	Five samples run 	Polymer - sheet (>1mm thick) 	--Copper: Consistent with Control
--Lead: Consistent with Control
--Silver: Consistent with Control
ABS (3D printing filament) 	 	imaterialise 	Pass, Permanent 	2019/04/22 	FMNH 	Oddy Test 	ABS 3D printing material (opaque white) acrylonitrile butadiene styrene 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Consistent with Control
--Silver: Consistent with Control
[http://cameo.mfa.org/wiki/Filament ABS 	 	imaterialise 	Pass, Permanent 	2019/04/22 	FMNH 	Oddy Test 	Aluminum and polyamide 3D printing material (metallic gray) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Consistent with Control
--Silver: Consistent with Control
High-Detail Resin (3D printing filament) 	 	imaterialise 	Fail, Unsuitable 	2019/04/22 	FMNH 	Oddy Test 	Resin 3D printing material (transparent) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Heavy white crystal growth
--Silver: Consistent with Control
High-Detail Resin (3D printing filament) 	 	imaterialise 	Temporary 	2019/04/22 	FMNH 	Oddy Test 	Resin 3D printing material (opaque white) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Yellow/gray haze
--Silver: Consistent with Control
High-Detail Resin (paintable 3D printing filament) 	 	imaterialise 	Fail, Unsuitable 	2019/04/22 	FMNH 	Oddy test 	Resin 3D printing material (paintable) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Heavy white crystal growth
--Silver: Consistent with Control
Multicolor (3D printing filament) 	 	imaterialise 	Fail, Unsuitable 	2019/04/22 	FMNH 	Oddy Test 	Resin 3D printing material (multicolor) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Heavy white crystal formation, complete delamination of coupon
--Silver: Consistent with Control
Polyamide MJP (3D printing filament) 	 	imaterialise 	Pass, Permanent 	2019/04/22 	FMNH 	Oddy Test 	Polyamide 3D printing material (gray) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Consistent with Control
--Silver: Consistent with Control
Polyamide SLS (3D printing filament) 	 	imaterialise 	Temporary 	2019/04/22 	FMNH 	Oddy Test 	Polyamide 3D printing material 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Yellow/gray haze
--Silver: Consistent with Control
Prime Gray (3D printing filament) 	 	imaterialise 	Fail, Unsuitable 	2019/04/22 	FMNH 	Oddy Test 	Resin 3D printing material (gray) 	 	Polymer - block/bulk/pellet 	Copper: Consistent with Control
Lead: Heavy white crystal growth
Silver: Consistent with Control
Standard Resin (3D printing filament) 	 	imaterialise 	Fail, Unsuitable 	2019/04/22 	FMNH 	Oddy Test 	Resin 3D printing material (translucent yellow) 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: White crystal growth and haze
--Silver: Consistent with Control
Versatile Plastic (neutral white 3D printing filament) 	 	Shapeways 	Temporary 	2019/04/22 	FMNH 	Oddy Test 	White nylon plastic for 3D printing applications 	 	Polymer - block/bulk/pellet 	--Copper: Consistent with Control
--Lead: Consistent with Control
--Silver: Consistent with Control
Gaylord Archival 10 pt. Folder Stock Artifact Tags (100-Pack) 	Gaylord Archival 	Gaylord 	PASS 	2020/02/14 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Folder stock artifact tags; acid-free, lignin-free, pH 8.0-8.5, buffered; Purchased 2018 	Color: Cream 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
Rigilene Polyester Sewing Boning, 4336920980 	Item4ever 	Amazon 	Temporary 	2020/02/14 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	See through, flat type polyester plastic boning; Polypropylene sewn/woven inside; Washable, can be dry cleaned; Purchased November 2019 	Color: White 	Polymer - Other 	
B-flute Corrugated Board Sheets, CB810 	Gaylord Archival 	Gaylord Archival 	Temporary In contact: PASS 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Corrugated board made with two outer sheets and a fluted inner sheet; 1/8" thick with a larger flute profile for vertical compression strength and cushioning; Buffered, acid-free, lignin-free, pH 8.0-9.5; 1/8 in. thick; Purchased November 2019 	Blue Tested hanging and in contact 	Paper-based (eg.: folders, cardboard, sheets) 	
Unbuffered Acid-Free Interleaving Tissue, 741-0810 	Unknown 	University Products 	Temporary In contact: Temporary 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Unbuffered, acid-free, thin, translucent 16 g/m^2 tissue; 8 inch x 10 inch sheets; Purchased November 2019 	Color: White Tested hanging and in contact 	Paper-based (eg.: folders, cardboard, sheets) 	
Acid-Free Buffered Tissue Paper, TPB001008 	Unknown 	Talas 	PASS In contact: PASS 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Interleaving tissue; acid-free, lignin-free, pH 9-10, and buffered with approximately 3% calcium carbonate; 24 g/m^2; 10 inch x 20 inch sheets; Purchased November 2019 	Color: White Tested hanging and in contact 	Paper-based (eg.: folders, cardboard, sheets) 	
Archivart® Unbuffered PhotoTex Tissue 	Archivart 	Nielsen Bainbridge Group 	Temporary In contact: Temporary 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	PhotoTex tissue; 10.5 lb. 100% cotton rag, sulfur-free, acid-free, lignin-free, pH 6.8-7.2, unbuffered, naturally white, sold as 24" x 36" sheets; Purchased November 2019 	Color: White Tested hanging and in contact 	Paper-based (eg.: folders, cardboard, sheets) 	
Abaca.sa Paper Hinging Tape, 533-0754 	Lineco, Holyoke 	Lineco 	Temporary In contact: FAIL 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Self-hinging tape made of Abaca paper (manila hemp) with very strong, permanent, and non-yellowing, water-activated acrylic adhesive; Purchased November 2019 	Color: White Tested hanging and in contact 	Paper-based (eg.: folders, cardboard, sheets) 	
InsulBloc® Spray Foam System, 11-017 	NCFI Polyurethanes 	NCFI Polyurethanes 	Temporary 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Spray foam insulation; Two component, self-adhering, seamless, closed cell, spray applied polyurethane foam system; Formulated with highly insulating HFC-245fa as the blowing agent; Maximum service temperature: 180°F; Foam sprayed onto wooden boards by manufacturer, tested without wood, test sample taken from area farthest from the boards; Acquired November 2019 	Color: White 	Polymer - foam - building insulation 	
STYROFOAM™ Brand PlazaMATE™ 	Dow Chemical Company 	Dow Chemical Company 	Temporary 	2020/01/08 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Rigid extruded polystyrene board, foam insulation, hydrochlorofluorocarbon (HCFC) free with zero ozone-depletion potential; Maximum use temperature: 165°F; 2 inches thick; Acquired November 2019; Only 1.5 g of sample in each jar 	Color: Blue 	Polymer - foam - building insulation 	
kSil & suraSil GP series silicone elastomer 	Silicone Engineering ltd 	Silicone Engineering ltd 	FAIL 	2020/01/02 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Extruded silicone gasket, circular profile with an arm that branches off (♇); chemical components: Polydimethylsiloxane with vinyl groups plus fillers and pigments where required; Purchased November 2019 	Color: Grey 	Polymer - gasket 	
Plastazote LD 15 BK 	Zotefoams 	Zotefoams 	Temporary 	2020/01/02 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Low density polyethylene foam; closed-cell, cross-linked polyethylene block foam; maximum recommended operating temperature: 85 degrees C 	Color: Black 	Polymer - foam - non-building insulation 	
Obomodulan 500 	OBO- werke 	McCausey Specialty Products 	PASS 	2019/12/12 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Foamed polyurethane; density is 500 kg/m3; pink colored; Purchased: December 2017 	Color: Pink 	Board - Plastic/polymeric/synthetic 	
Roxul Safe insulation 	Rockwool 	Rockwool 	Temporary 	2019/11/27 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Fire resistant mineral wool insulation with resin binder; 3 inches thick; 72 kg/m³ density; Received October 2019 	Color: Green 	Polymer - foam - building insulation 	
Foamular 250 SE 2" insulation 	Owens Corning 	Owens Corning 	Temporary 	2019/11/27 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Extruded polystyrene; moisture-resistant rigid foam board; 2 inches thick; New polystyrene 65-75%, Recycled polystyrene <30%, Flame retardant <1%, Colorant <1%, Blowing Agent 5-15%, Additives <1%; Received October 2019 	Color: Pink 	Polymer - foam - non-building insulation 	
Commercial SAFB FF Formaldehyde Free Mineral Wool Insulation 	Owens Corning/Thermafiber 	Owens Corning 	FAIL 	2019/11/27 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Formaldehyde-free mineral wool sound attenuation fire blanket; semi-rigid, non-structural insulation; 3 in thick; Mineral Wool, dextrose binder: Mineral Wool 93-98%, Dextrose 1-10%, proprietary material <1%; Received October 2019 	Color: Brown 	Polymer - foam - building insulation 	
Commercial SAFB Mineral Wool Insulation 	Owens Corning/Thermafiber 	Owens Corning 	Temporary 	2019/11/27 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Semi-rigid non structural mineral wool insulation; sound attenuation and fire blanket; 3 in thick; Mineral wool/fiber glass, Formaldehyde urea binder: 67-70% slag, 6-9% feldspar, 20-23% trap rock, 1-4% formic resin, 1-3% urea, <1% proprietary material; Received October 2019 	Color: Green 	Polymer - foam - building insulation 	
Obomodulan 500 	OBO- werke 	McCausey Specialty Products 	PASS 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Foamed polyurethane; density is 500 kg/m3; pink colored; Purchased: December 2017 	Color: Pink 	Board - Plastic/polymeric/synthetic 	
Corafoam U280 	DUNA 	DUNA 	Temporary 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	High density polyurethane rigid foam; carbon dioxide blowing agent; density: 450 kg/m^3; Received August 2019 	Color: Peach/Salmon 	Board - Plastic/polymeric/synthetic 	
Corafoam U310 	DUNA 	DUNA 	FAIL 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	High density polyurethane rigid foam; HFCs/CFCs/HCFCs-free blowing agent; density: 490 kg/m^3; Received August 2019 	Color: Brown/Mauve 	Board - Plastic/polymeric/synthetic 	
Plastazote LD18WE 	Zotefoams 	Zotefoams 	Temporary 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Closed cell, cross-linked polyethylene block foam; 18 kg/m3 density; 0.8 mm cell size; Only 1.6g of sample added to each jar; Purchased May 2019 	Color: White 	Polymer - foam - non-building insulation 	
Artifact Identification Tags 	Unknown 	Talas 	Temporary 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	10 pt. manilla acid free and lignin free stock with 6 in looped cotton string; string included in testing; SKU: TAS046002; 1.5 inches x 3 inches 	Color: Natural 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
Artifact Identification Tags, 613-1530 	Unknown 	University Products 	PASS 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Artifact ID tags; 1.5 inches x 3 inches; buffered 10 pt. off-white lignin-free and acid-free; 6 in cotton string; string included in testing 	Color: Natural 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
Silicone Sheet SS-.020X36-64904 	Acme Rubber Co. 	AAA-ACME Rubber Co. 	PASS 	2019/11/20 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Silicone sheet .020" thick x 36" wide roll, 40 + OR -5 durometer, clear; General purpose silicone sheet with operating temperature of -65 to 400°F 	Color: Clear 	Polymer - membrane (< 1mm thick) 	
Kodak Professional Endura Premier Paper 	Kodak Alaris 	ColorEdge 	Temporary 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Resin-coated multilayers paper for making color prints; white medium weight paper with one glossy side - White - Cut to weight 	AMNH Test #62 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK - Lead: Thin Yellow/green compacted corrosion
Lexjet Premium Archival Matte Paper 	LexJet 	ColorEdge 	Permanent 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Matte white paper for inkjet printing, pH neutral, acid-free, 9.5 mil - White - Cut to weight 	AMNH Test #70 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK - Lead: Very slight darkening
Epson Presentation Matte Paper 	Epson 	ColorEdge 	Permanent 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	White paper medium weight for inkjet printable media; 7.20 mil - White - Cut to weight 	AMNH Test #71 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK - Lead: light blue tarnish on coupon B
Crescent Select 4-Ply (1607) 	Crescent 	Dick Blick 	Permanent 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	4-ply alpha-cellulose mat board; acid and lignin-free - Brite White - Cut to weight 	AMNH Test #91 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK - Lead: OK
Bainbridge Alphamat Artcare Matboard 4-Ply 	Nielsen and Bainbridge 	Dick Blick 	Permanent 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Conservation-quality mat board with alkaline pH - Matte White (8464CR) - Cut to weight 	AMNH Test #92 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK - Lead: Very slight darkening on coupon B
Entrada Rag Bright 300 	Moab 	Duggal 	Temporary 	2019/07/29 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	100% cotton, acid-free, pH 8, buffered with calcium carbonate, 22.5mil, 300gsm, matte - White - Cut to weight 	AMNH Test #175 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK - Lead: Slight darkening, Light white compacted corrosion
Somerset Enhanced Velvet 225 	Moab 	Duggal 	Permanent 	2019/07/29 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	100% cotton mould made, acid-free, pH neutral, buffered with calcium carbonate, 18mil, 225gsm, matte - White - Cut to weight 	AMNH Test #176 	Board - cellulosic (eg.: paper, cardboard) 	Copper: OK - Silver: OK (slight darkening on edges) - Lead: OK
Dibond (6mm thickness) 	Alcan Composite 	 	Temporary 	2019/03/25 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Aluminum composite panel: AlMg1 alloy with black polyethylene (LDPE type) core with modified polyester system lacquer - Silver/Black - Cut to weight using circular saw 	AMNH Test #29 	Board - composite 	Copper: very slight red tarnish - Silver: OK - Lead: thin yellow/green compacted corrosion
ExhibitShield UV Laminate (5 mil); Kodak Ektacolor RA Chemicals; Kodak Professional Endura Premier Paper; Ultimate Optical Mount Removable (4-0167); Scratch-Resistant Acrylic Sheet (Optix E-series)	Plaskolite, Ritrama Inc., Kodak, Quality Media and Laminating Solutions 	ColorEdge 	Temporary 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Fully assembled "Digital C" sandwich (2019 copy label from AMNH exhibit) - Multicolor - Cut to weight 	AMNH Test #89 	Board - composite 	Copper: OK - Silver: OK - Lead: Darkening
Ethafoam (220 or 2.2 pcf) 	Dow Chemicals 	From Conservation lab 	Temporary 	2020/03/13 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Polyethylene foam, density: 2.2 lbs per cubic foot - White - Cut to weight 	AMNH Test #290 	Board - foam 	Copper: Very slight red tarnish - Silver: OK - Lead: Slight blue tarnish, Very slight darkening
Polyethylene foam (S-12857) (1.7 pcf) 	U-Line 	U-Line 	Temporary 	2020/03/13 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Polyethylene foam, density: 1.7 lbs per cubic foot - White - Cut to weight 	AMNH Test #291 	Board - foam 	Copper: Very slight red tarnish - Silver: OK - Lead: Slight blue tarnish, Very slight darkening
Scratch-Resistant Acrylic Sheet (Optix E-series) 	Plaskolite, LLC 	ColorEdge 	Temporary 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Clear acrylic sheet; contains olymethyl methacrylate (PMMA) and coating (proprietary) - Clear - Cut to weight with circular saw 	AMNH Test #63 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Light blue tarnish on coupon B, Very slight darkening
AcryStar 0001 Clear P95 Matte Acrylic Sheet P48 (0.125") 	AcryStar 	ePlastics 	Permanent 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Cast acrylic sheet; acrylic polymer based on methyl methacrylate - 0001 frosted - Cut to weight with circular saw 	AMNH Test #64 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: OK, very light blue tarnish on coupon B
Optix 0001 Non-Glare Acrylic Sheet (0.125") 	Plaskolite 	ePlastics 	Temporary 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Acrylic sheet based on polymethyl methacryalte (PMMA) (99.5%) and methyl methacrylate (MMA) (0.5%) - 0001 clear - Cut to weight with circular saw. 	AMNH Test #65 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Very slight darkening, light blue tarnish on coupon A
Acrylite UV/ Non-Glare acrylic sheet (1/10") 	Acrylite 	FrameDestination 	Temporary 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Extruded thermoplastic acrylic sheet (proprietary) with UV filtering (OP3) - Clear - Cut to weight with circular saw 	AMNH Test #66 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Very slight darkening, very light blue tarnish on coupon A
Acrylite Standard Acrylic Sheet (1/10") 	Acrylite 	FrameDestination 	Temporary 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Extruded thermoplastic acrylic sheet (proprietary) - Clear - Cut to weight with circular saw 	AMNH Test #67 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Very slight darkening, light blue tarnish on coupon A
Acrylite P95 frosted acrylic sheet (1/2") 	Evonik Industries 	LeNoble Lumber 	Temporary 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Acrylic copolymer (proprietary) - Frosted - Cut to weight with circular saw 	AMNH Test #68 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Very slight darkening, light blue tarnish on coupon A
HDPE (white, 1/2") 	 	Goppion 	Permanent 	2019/07/10 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Hard dense material - White - Cut in small strips; cut to weight 	AMNH Test #169 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Very slight darkening
Vivak (grade 0.220) 	Plaskolite LLC 	Plaskolite 	Temporary 	2019/12/19 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	PETG (polyethylene terephthalate glycol-modified) copolyester sheet - Transparent - Cut to weight with circular saw 	AMNH Test #262 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Slight darkening, very light white compacted corrosion at bottom
HDPE (black, 1/2") 	INDAT Plastics (Milan) 	Goppion 	Temporary 	2019/12/19 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	High density polyethylene - Black - Cut to weight with circular saw 	AMNH Test #263 	Board - plastic/polymeric/synthetic 	Copper: OK - Silver: OK - Lead: Slight darkening, Thin Yellow/green compacted corrosion
Vutek Inks on HIPS Filament (1/4") ("Lexan") 	SABIC; Electronic for Imaging 	 	Permanent 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	HIPS (High Impact Polystyrene Dissolvable Filament) with Vutek Inks (GSLX and GSR series) for inkjet/UV direct process printing - Color inks on clear substrate - Cut to weight with circular saw 	AMNH Test #69 	Board - plastic/polymeric/synthetic (and inks) 	Copper: OK - Silver: OK - Lead: OK
coupon B: Very slight darkening (P/T)
Compound FPM 75 (rubber ring) 	 	(Italian supplier) 	Temporary 	2019/03/25 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Fluorinated carbon-based polymers (also known as Viton O-Ring); contains hexafluoropropylene and vindylidenefluoride - Black - Cut to weight 	AMNH Test #30 	Gasket 	Copper: - Silver: - Lead: slight darkening, thin yellow green compact corrosion
Magnetic rubber strip (NdFeB) with adhesive backing (3M 9448) 	Magnet Over Bros (Italy) 	 	Temporary 	2019/03/25 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Plasto-ferrite strip (nedodymium magnet made from an alloy of neodymium, iron and boron) with adhesive back 3M 9448 (acrylate); attraction force: 1349 g/cm2 - Grey - Cut to weight; liner removed; tested on Mylar 	AMNH Test #31 	Gasket 	Copper: slight red tarnish on coupon B - Silver: OK - Lead: darkening, rainbow tarnish
TPE transparent compound (ShA 70)/ Plastoferrite 	Industrie ILPEA (Italy) 	 	Temporary 	2019/03/25 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Transparent TPE (thermoplastic elastomer) on plastoferrite magnetic strip - Clear/Black - Cut to weight 	AMNH Test #32 	Gasket 	Copper: very slight red tarnish - Silver: OK - Lead: very slight darkening
Viton Fluoroelastomer (VTR-9193) 	Dupont Performance Elastomers 	Rainbow Rubber 	Temporary 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Dark grey rubber; contains polyvinyllidenefluoride/hexafluoropropene and barium sulfate - Black - Cut to weight 	AMNH Test #94 	Gasket 	Copper: Very slight red tarnish - Silver: OK - Lead: Slight darkening
Flexible Hose A8G16 	ATAG 	Goppion 	Temporary 	2020/01/07 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Ether based PU wall with crushproof PVC helix - Transparent and yellow ribs - Cut to weight 	AMNH Test #279 	Gasket 	Copper: OK - Silver: OK - Lead: Slight darkening (darker at center); blue tarnish on coupon B
ExhibitShield UV Laminate (5 mil) ("Lexan Lam") 	Quality Media and Laminating Solutions (QMLS) 	ColorEdge 	Unsuitable 	2019/05/14 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Textured and rigid co-polymer film (PET) lined with pressure sensitive acrylic - Non-glare finish - Liner removed; cut to weight; sample folded on itself 	AMNH Test #61 	MPolymer - membrane (<1mm thick) 	Copper: Black corrosion spots - Silver: Light purple tarnish, very light blue/blue-green tarnish on coupon B - Lead: Fluffy white crystals
ExhibitShield UV Laminate (5 mil) ("Lexan Lam") 	Quality Media and Laminating Solutions (QMLS) 	ColorEdge 	Temporary 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Textured and rigid co-polymer film (PET) lined with pressure sensitive acrylic - Non-glare finish - Liner removed; sample cut to weight and laminated onto itself with bone folder 	AMNH Test #90 	Polymer - membrane (<1mm thick) 	Copper: OK - Silver: Blue/blue-green tarnish, Heavy purple tarnish - Lead: Slight darkening, Light white compacted corrosion
Computer Grafix Matte Film for Inkjet 	Grafix 	 	Unsuitable 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Polyester base film - Translucent - Cut to weight 	AMNH Test #139 	Polymer - membrane (<1mm thick) 	Copper: Very slight red tarnish - Silver: OK - Lead: Fluffy white crystals
Dura-Lar Film (.005, Matte, 2 sides) 	Grafix 	 	Temporary 	2019/06/20 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Bi-axially oriented polyester film (PET) - Translucent (matte 2 sides) - Cut to weight 	AMNH Test #140 	Polymer - membrane (<1mm thick) 	Copper: Red tarnish - Silver: OK - Lead: Slight darkening, Light white compacted corrosion
Dura Clear 	Kodak Endura Media 	 	Temporary 	2019/07/10 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Polyethylene teraphtalate and misc. additives - Transparent - Cut to weight 	AMNH Test #162 	Polymer - membrane (<1mm thick) 	Copper: tiny lighter spots - Silver: OK - Lead: Thin Yellow/green compacted corrosion
Photo Tex 	 	 	Temporary 	2019/07/10 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Inkjet printing media made of polyester textile (40-45%), cellulose pulp (40-45%), silicon dioxide (3-7%), polyacrylic acid ester (3-7%), additives (3-7%) - White - Cut to weight 	AMNH Test #163 	Polymer - membrane (<1mm thick) 	Copper: OK - Silver: OK - Lead: Very slight darkening, very slight blue tinge on coupon A
Fasson Rapid-Roll 1079 Tyvek 	Dupont 	 	Temporary 	2019/09/26 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Spunbound polyethylene, 8.3 mils - White - Cut to weight 	AMNH Test #221 	Polymer - membrane (<1mm thick) 	Copper: OK - Silver: OK - Lead: Slight darkening
Fasson Rapid-Roll 1085D Tyvek 	Dupont 	 	Temporary 	2019/09/26 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Spunbound polyethylene, 10.3 mils - White - Cut to weight 	AMNH Test #222 	Polymer - membrane (<1mm thick) 	Copper: OK - Silver: OK - Lead: Slight darkening, Thin Yellow/green compacted corrosion
Viton gasket, 11mm diameter 	Rainbow Rubber 	Rainbow Rubber 	Permanent 	2019/07/10 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Viton, soft and flexible tube gasket - Grey - Cut to weight 	AMNH Test #168 	Gasket 	Copper: OK - Silver: OK - Lead: Very slight darkening
Plastazote LD 70 Black polyethylene foam 	UFP Technologies 	Zotefoams 	Temporary 	2019/11/06 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Low density closed cell, cross-linked polyethylene block foam; recommended maximum operating temperature 105 degrees C; water absorption less than 2%; received May 2019 	Black 	Polymer - foam - non-building insulation 	
Acoustic Textile Felt, Cotton board 	Really 	Kvadrat 	Temporary 	2019/10/24 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Sound absorbing acoustic felt board; 70% cotton, 30% thermoplastic binder; 10 mm thick, 100 kg/m^3, 305 x 118 cm boards; purchased August 2019 	White 	Fabric - batting or padding 	
Abaca Tissue, MM-52 Lens Tissue 	Unknown 	Hiromi Paper Co. 	Temporary 	2019/10/23 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	100% Abaca tissue, pH neutral, cooked with caustic soda and dried on stainless steel; 9g/m^2; purchased August 2019 	Natural 	Paper-based (eg.: folders, cardboard, sheets) 	
Obomodulan 500 	OBO- werke 	McCausey Specialty Products 	PASS 	2019/10/17 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Foamed polyurethane board; density is 500 kg/m^3; pink colored; purchased December 2017 	Color: Pink; Comment: lead coupons are better than controls. 	Board - Plastic/polymeric/synthetic 	
Solid Textile Board 	Really 	Kvadrat 	Temporary 	2019/10/11 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Recycled cotton board, 70% textile 30% thermoplastic binder; 300 cm x 110 cm, 7.8mm thick; designed to replace wood board in furniture and architecture construction; purchased August 2019 	Cotton White 	Board - Composite (eg: drywall) 	
Flutecorr, corrugated polypropylene board 	Laminacorr 	LaminaCorr 	Temporary 	2019/10/10 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Extruded polypropylene corrugated board 10mm 1800 g/m^2; batch #2-0090907, extruded 1/6/17, cut 8/22/19; purchased August 2019 	Natural 	Board - Plastic/polymeric/synthetic 	
Cast Polymethylmethacrylate (PMMA), PMMA GS 	iNDAT 	Unknown 	PASS 	2019/10/10 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	About 1" thick cast PMMA for use as display case plexi glass; purchased June 2019 	Colorless 	Polymer - sheet (> 1mm thick) 	
Obomodulan 500 	OBO- werke 	McCausey Specialty Products 	PASS 	2019/09/24 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Foamed polyurethane board; density is 500 kg/m^3; pink colored; purchased December 2017 	Color Pink; Comment: lead coupons are better than controls. 	Board - Plastic/polymeric/synthetic 	
Komatex White Matte 4812MKTW, rigid PVC board 	Unknown 	Harbor Sales, Inc 	FAIL 	2019/09/24 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Rigid foam PVC sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; purchased May 2019 	White 	Board - Plastic/polymeric/synthetic 	
Komacel White Gloss 4813MKC, rigid PVC board 	Unknown 	Harbor Sales, Inc 	PASS 	2019/09/24 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Rigid Foam PVC Sheet; polyvinyl chloride and minor components; 4' x 8' (1/2" thick) sheets; purchased May 2019; 	White 	Board - Plastic/polymeric/synthetic 	
Heritage Archival Corrugated Board, E-Flute TPB67017 	Unknown 	Talas 	Temporary 	2019/09/24 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Acid-free corrugated cardboard; single ply construction; 100% bleached alpha cellulose, potato starch, alkaline reserve (buffer) > 3% calcium carbonate; 1/16" x 8" x 10" sheets; purchased May 2019 	Blue/gray, white 	Paper-based (eg.: folders, cardboard, sheets) 	
Davey Board Red Label, #18 	Unknown 	Colophon Book Arts Supply 	FAIL 	2019/09/24 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Single ply book board; acid neutral with a pH of 7-8; 20.625" x 30"; purchased May 2019 	Brown 	Paper-based (eg.: folders, cardboard, sheets) 	
Multi-use Bi-Corr Cross Direction Corrugated Board 613-4001 	Unknown 	University Products 	Temporary 	2019/08/16 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	1/4" Thick laminated corrugated board running perpendicular to each other; buffered with 3% calcium carbonate; lignin-free, acid-free; received May 2019 	Blue/grey 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
Moisture Resistant Corrugated Board 156-1114 	Unknown 	University Products 	Temporary 	2019/08/16 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	200 lb. Test B-flute corrugated paper board, 1/8 in thick; Acrylic water-resistant coating; acid-free lignin-free; buffered with 3% calcium carbonate; received May 2019 	Grey 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
SS-.047x36-65019 Silicone Sheet 	Acme Rubber Co. 	AAA-ACME Rubber Co. 	Temporary 	2019/08/16 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	General purpose Silicone Sheet; 0.47" thick x 36" wide +/- 5 durometer black color; Operating temperature of -65 to 400°F. Excellent electrical insulator. Resistance to oxygen & ozone 	Black 	Polymer - sheet (> 1mm thick) 	
P-565 Silicone Rubber Clear 	Silicone Inc. 	Anglers Artistry 	Temporary 	2019/07/17 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Silicone cast into large ~10 cm diam petri dish, about 8 mm thick; P-565 is not designed as a mold-making rubber; rather, it is used as the article.; cured 7 days before testing; Details: two-component, addition reaction, platinum catalyzed silicone rubber. It is designed to remain water-clear even after extended exposure to the sun. Chemical components: silicone. Mixing Instructions: Mix 100 parts by weight of P-565 Base with 10 parts by weight of P-565 Activator thoroughly. After mixing, place the material in a vacuum chamber capable of 28 to 29 inches of mercury vacuum. The material will expand to approximately quadruple its original volume and then collapse. Maintain the vacuum for an additional 2 to 3 minutes and then remove; purchased May 2018	Colorless, transparent 	Polymer - block/bulk/pellet 	
Spiders Wet Strength Tarantula Tissue Sheet, PASWTT7651 	Unknown 	Conservation by Design (CXD) 	Temporary 	2019/07/17 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Unbuffered, low-opacity, long-fiber tissue. Application: repair work, lining, wrapping, interleaving; Chemical Components: 100% Manilla fiber; purchased September 2018 	Cream 	Paper-based (eg.: folders, cardboard, sheets) 	
Archival Corrugated multi-use board, #2-130, 2-131, 2-133, 2-148 	Unknown 	Masterpak 	Temporary 	2019/07/17 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Masterpak E Flute 1/16 inch single wall. 100% bleached alpha cellulose. No recycled or wooden fibers. No optical brighteners. Kappa level: 1-2 = lignin-free (TAPPI T 23 om-99). pH cold extraction: 8.0-9.5 (TAPPI T 509 om-02). Alkaline reserve (buffered) >3% calcium carbonate. Adhesive: potato starch, pH 7.0, moisture proof. 	Grey/White 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
Teflon Relic Wrap Packaging Film, Part #51001 	Technetics 	Gaylord 	Temporary 	2019/07/17 	MMA 	Oddy Test (method: 20190226_OT_1 ) 	Teflon PTFE film, pliable, chemically inert, nontoxic, and non-adsorbent; 3 mil thick, 10 in wide, 100 ft roll; Lot number 3161603004 	White 	Polymer - membrane (< 1mm thick) 	
Corobuff Roll, three-dimensional paper, P0011301 	Unknown 	Pacon Creative Products 	PASS 	2019/07/05 	MMA 	Oddy Test (method: 20190226_OT ) 	Three dimensional paper with black corrugation on one side, smooth and white on the opposite, 1/4" thick, 8"x8" sample; Product Number: P0011301; Chemical Components: Paper and recyclable substrate, glue (the Pacon website is vague on these materials); purchased September 2018 	White and black 	Polymer - sheet (> 1mm thick) 	
Viton™ tubing 5mm ID 10mm OD 	Rainbow Rubber 	Rainbow Rubber 	Temporary 	2019/01/11 	MMA 	Oddy Test (method: 20180821_OT ) 	Round black Viton™ gasket; model #1571806; black tubing, 5mm ID, 10mm OD; certified Viton rubber; purchased November 2018 	Black 	Polymer - gasket 	
HEYCo-molded™ Liquid Tight Break-Thru Plugs; C2062-P, LTBP 625-250 black 	Heyco 	Unknown 	Temporary 	2018/08/01 	MMA 	Oddy Test (method: 20180704_OT ) 	Model/Catalog Number: part #: C2062-P; LTBP 625-250 black; Details: mounting hole diameter: 15.9 mm; cable diameter range: 3.3-9.5 mm; part no. C2062; A head diameter: 26.2 mm; Chemical Components: Nylon 6/6 and TPE; purchased June 2018 	Black 	Polymer - block/bulk/pellet 	
#5 mt AWG jacketed electric cable; 28171A multi-conductor 600V type TC-ER cable 	Belden 	Unknown 	Temporary 	2018/06/08 	MMA 	Oddy Test (method: 20171116_OT ) 	Jacketed Wire: 2/0 AWG multi-conductor stranded (19 x 11) bare copper conductors, 6 AWG bare copper ground wire, PVC/nylon insulation, PVC jacket; received 2018 	Glack 	Other: composite 	
#1 mt Air conduit tube; A8G16 	ATAG 	Unknown 	Temporary 	2018/06/08 	MMA 	Oddy Test (method: 20171116_OT ) 	Flexible tubing: ether based PU wall, food grade, with crushproof PVC helix; 1.1" diameter; received 2018 	Clear with an ivory spiral 	Polymer - membrane (< 1mm thick) 	
D-Seal Gasket, Elastosil R 401/70 	Wacker Silicones 	 	Temporary 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	D-profile gasket; peroxide-cured high consistency silicone rubber (HCR) - Grey - Cut to weight 	AMNH Test #1 	Polymer - gasket 	Copper: ok - Silver: ok - Lead: rainbow tarnish, darkening
Bubble-Seal Gasket, Elastosil R 401/60 	Wacker Silicones 	 	Temporary 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	gasket; peroxide-cured high consistency silicone rubber (HCR) - Grey - Cut to weight 	AMNH Test #2 	Polymer - gasket 	Copper: red tarnish - Silver: ok - Lead: rainbow tarnish, darkening
D-Seal Gasket, Elastosil R 401/70 	Wacker Silicones 	 	Temporary 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	D-profile gasket; peroxide-cured high consistency silicone rubber (HCR) - Black - Cut to weight 	AMNH Test #3 	Polymer - gasket 	Copper: very slight red tarnish (light streaks) - Silver: ok - Lead: rainbow, darkening
Bubble-Seal Gasket, Elastosil R 401/60 	Wacker Silicones 	 	Temporary 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	gasket; peroxide-cured high consistency silicone rubber (HCR) - Black - Cut to weight 	AMNH Test #4 	Polymer - gasket 	Copper: red tarnish - Silver: ok - Lead: rainbow tarnish, darkening
Silifoam seal, Adhesive backed HT603A 	NewMet Silicones 	 	Unsuitable 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Rectangular profile silicone gasket with pressure-sensitive adhesive; low density, low compression set, fire retardant silicone foam - White - Cut, release paper removed 	AMNH Test #5 	Polymer - gasket 	Copper: ok - Silver: ok; localized white spot - Lead: thick white and yellow compact corrosion; with fluffy spots
Interpon 610, RAL 7012 	Interpon Powder Coatings 	 	Temporary 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	polyester-based powder coating on steel panel - Grey - Cut into small blocks using bandsaw 	AMNH Test #15 	Board - plastic/polymeric/synthetic 	Copper: ok - Silver: ok - Lead: slight darkening
Arreis MDF with Dacrylate Clear Acrylic Emulsion varnish applied 	Roseburg Forest Products, Dacrylate Paints Ltd. 	 	Unsuitable 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Medium density fiberboard panel coated in Dacrylate Clear Acrylic Emulsion varnish (2-butoxyethanol) - Brown, Transparent - Cut into small blocks using bandsaw - cut edges are uncoated. 	AMNH Test #16 	Board - plastic/polymeric/synthetic 	Copper: red tarnish - Silver: ok - Lead: Thick yellow/white compact corrosion
Obomodulan 500 	OBO-Werke 	McCausey Lumber 	Permanent 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Rigid fine-cell polyurethane foam panel - Pink - Cut into small blocks using bandsaw 	AMNH Test #19 	Board - plastic/polymeric/synthetic 	Copper: ok - Silver: ok - Lead: ok (better than control)
Alucore 	3A Composites 	 	Permanent 	2019/02/08 	AMNH 	Oddy Test (method: MMA 20190130_OT) 	Aluminum honeycomb composite panel; core of AlMn alloys, cover sheets of corrosion-resistant Peraluman alloys (AlMg1/5005A) - Grey - Cut into small blocks using bandsaw 	AMNH Test #14 	Board - plastic/polymeric/synthetic 	Copper: ok - Silver: ok - Lead: very slight darkening (looks like control)
Cor-X polypropylene 4 mm corrugated board 	Primex Plastics 	Primex 	Temporary 	2019/05/29 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Corrugated polypropylene board; May 2018; 4 mm thickness. Purchased in May 2018. Reference Oddy 2199. 	White 	Board - Plastic/polymeric/synthetic 	
Masterpak B-Flute 1/8 inch single wall. Model #2-130, 2-131, 2-133 	Masterpak 	Unknown 	Temporary 	2019/05/29 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Single-wall B Flute (1/8" thick). 100% bleached alpha cellulose. No recycled or wooden fibers. No optical brighteners. Kappa level: 1 - 2 = lignin-free (TAPPI T 23 om-99). pH cold extraction: 8.0 - 9.5 (TAPPI T 509 om-02). Alkaline reserve (buffered) >3% calcium carbonate. Adhesive: Potato starch, pH 7.0, moisture proof. 	Grey, white 	Board - Natural (eg: wood, cotton) 	
Backer rod, #860-1020 	Unknown 	University Products 	Temporary 	2019/05/29 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	1-Inch trapezoid backer rods, closed cell polyethylene foam. Purchased in January 2019. 	White 	Polymer - foam - non-building insulation 	
Silicone Cabinet gasket 	Unknown 	Delta Designs 	Temporary 	2019/05/23 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Cabinet gasket. Delta Designs. Month/Year Purchased: 2019. Silicone. 1cm diameter. 	Black 	Polymer - gasket 	
Insite ® Acid Free Foamcore #136 	The Gillman Brothers Company 	The Gilman Brothers Company 	Temporary 	2019/05/23 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Extruded polystyerene foamboard; acid free 100% High Alpha Cellulose paper faces; pH 7.5-9.5 buffered with 3-5% Calcium Carbonate. Standard thickness is 3/16″ and sizes range from 24″x 36″ to 48″x 96″. Month/Year Purchased: Unknown. 	White 	Board - Plastic/polymeric/synthetic 	
Insite ® Reveal® Colors 	The Gillman Brothers Company 	The Gilman Brothers Company 	Temporary 	2019/05/23 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Paper faced foamboard. Acquired in 2018. GAUGES: Min: 1/8” Max: 1/2” SIZES: Min: 24″x 36″ Max: 60” x 192”. . 	White 	Board - Plastic/polymeric/synthetic 	
Binders Board 	Unknown 	Hollanders 	FAIL 	2019/03/26 	MMA 	Oddy Test (method: 20190226_OT ) 	Binders Board; Purchased: Feb 2016 	Grey 	Paper-based (eg.: folders, cardboard, sheets) 	
Unbuffered Glassine Sheets, UIG810 	Unknown 	Gaylord Archival 	Temporary 	2019/03/26 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Interleaving paper; Catalog Number: UIG810; Purchased: December 2018 	White 	Paper-based (eg.: folders, cardboard, sheets) 	
Davey Board Red Label #18 	Unknown 	Colophon Book Arts Supply 	FAIL 	2019/03/26 	MMA 	Oddy Test (method: 20190226_OT ) 	Brown, 0.082" thick paper board; Catalog Number: Davey Board Red Label #18; Purchased: 12/2018 	Brown 	Paper-based (eg.: folders, cardboard, sheets) 	
Black proof box, 114-104 	Unknown 	Archival Methods 	FAIL 	2019/03/26 	MMA 	Oddy Test (method: 20190226_OT ) 	1/16" thick black colored cardboard; Catalog Number: 114-104; Purchased: December 2018 	Black 	Paper-based (eg.: folders, cardboard, sheets) 	
File folder with antimicrobial product protection, 10338 	Smead 	Amazon 	FAIL 	2019/03/26 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Smead File Folder with Antimicrobial Product Protection, 1/3-Cut Tab, Letter Size, Manila, 100 per Box; Catalog Number: 10338; Month/Year Purchased: November 2018 	Beige 	Paper-based (eg.: folders, cardboard, sheets) 	
Permalife 20 lb. Bond Paper, 132-A4 	Unknown 	Archival Methods 	PASS 	2019/03/26 	MMA 	Oddy Test (method: 20190226_OT ), SPME GCMS 	Lignin-free; Chemical Components: 25% cotton + 75% pure cellulose fiber + 3% calcium carbonate alkaline reserve; Catalog Number: 132-A4; Purchased: December 2018 	White 	Paper-based (eg.: folders, cardboard, sheets) 	
Cerex spunbond nylon, 23150/23200 	Cerex Advanced Fabrics, Inc. 	Cerex Advanced Fabrics, Inc. 	Temporary 	2019/03/14 	MMA 	Oddy Test (method: 20190214_OT_a ), SPME GCMS	"Gas bonded" continuous filament nylon fabric; white; Model/Catalog Number: 23150/23200 (same composition; last three numbers refer to thickness); Chemical Components: nylon 6,6 and nylon 6; Purchased: 01/2019 	White 	Polymer - membrane (< 1mm thick) 	
Item #A-PP2B, polypropylene pellets 	Unknown 	Fairfield 	PASS 	2019/02/27 	MMA 	Oddy Test (method: 20180821_OT ) 	Polypropylene pellets for pillow filling; colorless; Model/Catalog Number: Item #A-PP2B; Purchased: 10/18 	Colorless 	Polymer - block/bulk/pellet 	
1/32" FDA Clear silicone sheet, colorless 	Unknown 	Canal Rubber 	Temporary 	2019/02/27 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	1/32" Thick food safe silicone sheet; colorless; Purchased: January 2019 from Canal; washed with distilled water and wiped dry 	Colorless; tarnish on the copper is very slight red tarnish boarding on Permanent 	Polymer - membrane (< 1mm thick) 	
Extruded Ilpea Thermoplastic Elastomer (TPE) 	Ilpea - Malgesso, Italy 	Ilpea 	PASS 	2019/02/27 	MMA 	Oddy Test (method: 20180821_OT ) 	Ilpea TPE gasket; colorless; Model/Catalog Number: TPE-S Transparent Compound ShA 70; Purchased: 1/2019; Details: 1mm x 14 mm x 285 mm strips of TPE were extruded, stapled to printer paper, and shipped from Italy for testing. Extrusion details unknown. Shore A 70 durometer; Chemical Components: Material is Teknor's Medalis(r) MD-53273. 	Colorless; Oddy results note: Haze on copper is due to copper not the gasket material 	Polymer - gasket 	
HP-PBN7 Metalized barrier film 	Unknown 	Heritage Packaging 	Temporary 	2019/02/27 	MMA 	Oddy Test (method: 20190130_OT ), SPME GCMS 	Heat Sealable barrier film; Details: heat sealable barrier film silver on outside, grey inside. 48ga. PET/Ink/Adhesive/35ga./Foil/Adhesive/60ga. oriented nylon/Adhesive/5.0mil Sealant; Chemical Components: PET, unknown adhesive, metal foil, and nylon; Purchased: 4/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	Silver 	Polymer - membrane (< 1mm thick) 	
S411757 or NFE-016 Metalized barrier film 	Unknown 	Heritage Packaging 	Temporary 	2019/02/27 	MMA 	Oddy Test (method: 20190130_OT ), SPME GCMS 	Heat Sealable Barrier film; Details: metallized barrier film, silver on outside: 15 um BON/16g LDPE Coextrusion/9 um Aluminum foil/16g LDPE coextrusion/76 um LLDPE; purchased 11/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	 	Polymer - membrane (< 1mm thick) 	
Cad Pak N (CPN) Barrier Film 	Unknown 	Protective Packaging Corp. 	Temporary 	2019/02/27 	MMA 	Oddy Test (method: 20190130_OT ), SPME GCMS 	Heat Sealable Barrier film; Details: metallized barrier film, silver on outside: Nylon/polyethylene/aluminum foil/polyethylene. adheres to MIL-PRF-131K Type I Class I; Chemical Components: nylon, polyethylene, aluminum; purchased 10/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	 	Polymer - membrane (< 1mm thick) 	
Marvelseal 470, MFS470 Metalized Barrier film 	Unknown 	Protective Packaging 	Temporary 	2019/02/27 	MMA 	Oddy Test (method: 20190130_OT ), SPME GCMS 	Heat Sealable Barrier film; Details: metalized barrier film, silver with red lettering on outside, grey on inside: Oriented Polypropylene (0.9 mil) / polyethylene (0.65 mil) / Aluminum foil (0.000285 mil) / linear low-density polyethylene (2.9 mil); Chemical Components: polyethylene, aluminum; purchased 10/2018; TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	 	Polymer - membrane (< 1mm thick) 	
Peterboro Museum Board Traditional White, M902-4 	Peterboro 	Talas 	FAIL 	2019/02/13 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Museum board; off-white; thickness 4-ply; 100% cotton; Purchased: 09/2018 	Off-white, traditional white 	Board - Natural (eg: wood, cotton) 	
Peterboro Museum Board Warm White, M901-4 	Peterboro 	Talas 	FAIL 	2019/02/13 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Museum board; off-white; thickness: 4-ply; 100% cotton; Purchased: 09/2018 	Off-white, warm white 	Board - Natural (eg: wood, cotton) 	
Peterboro Museum Board Black, M905-4 	Peterboro 	Talas 	Temporary 	2019/02/13 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Museum Board; thickness: 4-ply; black; 100% cotton; Purchased: 09/2018 	Black 	Board - Natural (eg: wood, cotton) 	
Polyurethane flexible foam wedges 	SoundAssured 	Butera Brands 	Temporary 	2019/02/13 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Acoustic foam wedges; black flexible solid foam with cellular structure; 3" base; Chemical Components:polyether and polyester based urethane polymers; purchased 12/2018 	Black 	Polymer - foam - non-building insulation 	
Marvelseal 360; Film Foil MIL PRF-131-K CL1 Type I 	Midsouth Packaging 	edcosupply.com 	Temporary 	2018/12/31 	MMA 	Oddy Test (method: 20180305_OT ) 	Barrier film; Details: heat sealable barrier film, silver with writing on outside and grey on inside: biaxially oriented nylon (0.6mil) / polyethylene (1.4mil) / aluminum foil (0.0003mil) / polyethylene (1.2mil) / linear LDPE(1.5mil); Chemical Components: nylon, polyethylene, and aluminum; Purchased: 4/2018. TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	Silver 	Polymer - membrane (< 1mm thick) 	
CADPAK HD100, MIL-PRF-131K CLass1 Barrier Film 	Unknown 	Heritage Packaging 	Temporary 	2018/12/31 	MMA 	Oddy Test (method: 20180305_OT ) 	Barrier film; Details: heavy duty heat sealable barrier film. silver with writing on outside and green on inside: 60ga biax nylon / 15# LDPE / 30ga foil / 6 mil Polyethylene co-extruded with heavy-duty green Sealant; Chemical Components: nylon, metal foil, polythylene; Purchased: 4/2018. TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	Silver 	Polymer - membrane (< 1mm thick) 	
CADPAK HD200, QPL MIL-PRF-131K Barrier Film 	Unknown 	Heritage Packaging 	Temporary 	2018/12/31 	MMA 	Oddy Test (method: 20180305_OT ) 	Barrier film; Details: super heavy duty heat sealable barrier film. silver with writing on outside and green on inside: Biax Nylon/PE/Cross-Lam PE/PE/Foil/Heavy Duty Coextrusion; Chemical Components: nylon, polyethylene, metal foil; purchase date unknown. TESTED AS SEALED POUCH NOT IN GLASS JARS, so inside of material only tested. 	White 	Polymer - membrane (< 1mm thick) 	
Food-Grade High-Temperature Silicone Rubber Sheet, catalog # 5827t21 	J. A. Bar 	McMaster-Carr 	Temporary 	2018/12/19 	MMA 	Oddy Test (method: 20180821_OT ) 	Colorless silicone rubber sheet; 1/32" thickness; purchased 11/2018; Temperature Range: -80° to 400° F Tensile Strength: 1,000 psi; 50A durometer 	Colorless 	Polymer - sheet (> 1mm thick) 	
Kobracast Art 	Worbla 	cosplaysupplies.com 	Temporary 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	Open-weave polyester with a thermoplastic backing 	 	Polymer - sheet (>1mm thick) 	Copper: slight reddening, yellowing, or rainbow-like color change; Formation of up to 20 black spots (Temporary) Silver: similar to control; slight yellowing, purpling, or darkening. (Temporary) Lead: darkening; spots of corrosion where in direct contact with sample material (Temporary)
Finest Art 	Worbla 	cosplaysupplies.com 	Fail, Unsuitable 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	Thermoplastic resin and wood flour filler 	 	Polymer - sheet (>1mm thick) 	Copper: slight reddening, yellowing, or rainbow-like color change (Temporary) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: significant darkening and purple, red, green discoloration; white fluffy crystal formation; coupon eaten away where in direct contact with sample material. (Fail)
Mesh Art 	Worbla 	cosplaysupplies.com 	Fail, Unsuitable 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	Thermoplastic resin and filler partially made from recycled rice husks 	 	Polymer - sheet (>1mm thick) 	Copper: slight reddening, yellowing, or rainbow-like color change (Temporary) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: yellow/olive tarnish (Temporary); white fluffy crystal formation. (Fail)
TranspArt 	Worbla 	cosplaysupplies.com 	Pass, Permanent 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	Transparent polymer thermoplastic, ionomer resin 	 	Polymer - sheet (>1mm thick) 	Coupons look similar to the controls. (Pass/Permanent)
WonderFlex 	WonderFlex 	cosplaysupplies.com 	Fail, Unsuitable 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	Thermoplastic film, with a layer of polyester open weave scrim 	 	Polymer - sheet (>1mm thick) 	Copper: slight reddening, yellowing, or rainbow-like color change; Formation of up to 20 black spots (Temporary) Silver: Coupons look similar to the controls. (Pass/Permanent) Lead: heavy, overall white fluffy crystal formation; coupon eaten away where in contact with sample material (Fail)
VaraForm 	 	cosplaysupplies.com 	Fail, Unsuitable 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	Natural cotton fabric impregnated by a thermoplastic polymer 	 	Polymer - sheet (>1mm thick) 	Copper: Inconsistent;reddening, yellowing, or darkening (Fail) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: heavy, overall white fluffy crystal formation; coupon eaten away where in contact with sample material (Fail)
Polly Plastics moldable plastic pellets 	Polly Plastics 	Amazon 	Fail, Unsuitable 	2019/01/31 	Penn 	Oddy Test, A-D Strips 	polycaprolactone pellets 	 	Polymer - pellet 	Copper: severe blackening (Fail) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: heavy, overall white fluffy crystal formation; coupon eaten away where in contact with sample material (Fail)
Instamorph 	Instamorph 	Amazon 	Fail, Unsuitable 	2019/03/30 	Penn 	Oddy Test, A-D Strips 	polycaprolactone pellets 	 	Polymer - pellet 	Copper: severe blackening; more alteration where in contact with sample material (Fail) Silver: slight yellowing, purpling, or darkening. (Temporary) Lead: heavy, overall white fluffy crystal formation; coupon eaten away where in contact with sample material (Fail)
BON 100 Clear 	Cadillac Products Packaging Company 	Heritage packaging (Victor, NY) 	Unsuitable 	2018/05/23 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Heat sealable thin flexible transparent film; Biaxially oriented nylon/PE/EVOH/coextrusion; barrier material; nylon, polyethylene, ethylene vinyl alcohol; Quasi -repeat of Oddy 2084, where only the interior component was oddy tested (coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material); FOR THIS TEST, the material in its totality was cut into pieces and placed in the Oddy jars; sample provided 8/20/2017 - barrier film 	 	Polymer - membrane (< 1mm thick) 	
48 ga Alox PET/adhesive/2.5 mil LLDPE 	Unknown 	Heritage Packaging, Victor, NY 	Temporary 	2018/05/23 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Heat sealable ~0.1 mm thick barrier film; transparent, flexible, heat-sealable film with medium water and oxygen transmission rates (0.13 g/100 in^2/day and 0.13 cc/100 in^2/day; quasi-repeat of Oddy 2087, where coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material; FOR THIS TES, the material was cut into pieces and placed into the oddy test jars; Supplier: Heritage Packaging, Victor NY; purchased 8/2017 - barrier film 	 	Polymer - membrane (< 1mm thick) 	
BON 100 Clear 	Cadillac Products Packaging Company 	Heritage packaging (Victor, NY) 	Unsuitable 	2018/05/23 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Heat sealable thin flexible transparent film; Biaxially oriented nylon/PE/EVOH/coextrusion; barrier material; nylon, polyethylene, ethylene vinyl alcohol; Quasi -repeat of Oddy 2084, where only the interior component was oddy tested (coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material); FOR THIS TEST, the material in its totality was cut into pieces and placed in the Oddy jars; sample provided 8/20/2017 - barrier film 	 	Polymer - membrane (< 1mm thick) 	
48 ga Alox PET/adhesive/2.5 mil LLDPE 	Unknown 	Heritage Packaging, Victor, NY 	Temporary 	2018/05/23 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Heat sealable ~0.1 mm thick barrier film; transparent, flexible, heat-sealable film with medium water and oxygen transmission rates (0.13 g/100 in^2/day and 0.13 cc/100 in^2/day; quasi-repeat of Oddy 2087, where coupons, holder, and water went into a heat-sealed pouch produced from 8.5" square of material; FOR THIS TES, the material was cut into pieces and placed into the oddy test jars; Supplier: Heritage Packaging, Victor NY; purchased 8/2017 - barrier film 	 	Polymer - membrane (< 1mm thick) 	
All purpose joint compound (spackle) 	USG, Sheetrock brand 	Unknown 	Unsuitable 	2018/07/05 	MMA 	Oddy Test (method: 20180525_OT ), SPME GCMS 	Drywall joint compound: premixed with water, 4.5 gallons (17 L) purchased (green label on container), which finishes 450 ft2 (42m2)of drywall. Allow 1/16” thick film to dry 24 hours; Chemical Components: Limestone, water, (may contain talc), ethylene vinyl acetate polymer, polyvinyl acetate, and may contain perlite. Contains 1.7 g/L of VOC. Received Spring 2018. 	 	Other - inorganic filler 	
Self-adhesive drywall joint mesh, FiFlexMesh FM2300 	FiFlexMesh 	Jaydee Group 	Unsuitable 	2018/07/05 	MMA 	Oddy Test (method: 20180525_OT ), SPME GCMS 	Self-adhesive drywall joint mesh: 1-7/8” x 300’ roll; Chemical Components: Fiberglass and unknown adhesive. no SDS or chemical info available; unknown purchase date. 	 	polymer other 	
Paper drywall joint tape, 2 1/16" paper joint tape 	Proform Brand 	unknown 	Temporary 	2018/07/05 	MMA 	Oddy Test (method: 20180525_OT ), SPME GCMS 	Paper drywall joint tape, purchased sometime between 1/2018-5/2018; Details: 2 1/6” wide by 500’; Chemical Components: Paper, no other details available. Unknown purchase date. 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Invision Transit Carpet Tile (style 7029) 	Unknown 	J & J Flooring 	Temporary 	2018/07/17 	MMA 	Oddy Test (method: 20171106_OT ), SPME GCMS 	Carpet tile; Details: Closed loop, solution dyed, Encore(r) SD Ultima Nylon fiber with Nexus(r) Modulus PVC backing. Fiber and Backing include 49% recycled material in unknown ratio. Fibers heat treated with ProTex(r) fluorochemical anti-soiling treatment. Heat used to bond the fluorochemical to the fiber; Chemical Components: Nylon, PVC, Fluorochemical; purchased 6/2018 	 	Carpet - Synthetic/plastic/polymeric 	
Self Adhesive Natural Cork, 04F-C6421-06 	Con-tact brand 	Kittrich Corporation 	Unsuitable 	2018/08/01 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	Cork roll with self-adhesive; natural lignocellulosic plant material, unknown adhesive; Purchased: 2017 	 	Other - natural 	
Natural cork roll, UPC 034138103005 	Quartet 	ACCO Brands 	Unsuitable 	2018/08/01 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	Natural cork roll (no adhesive); 2mm thickness x 2.23 cm wide; Material Class: natural lignocellulosic plant material; Purchased: February 2018 	 	Other - natural 	
Tyvek® Envelopes with 2" Gusset & 4" Flap (50-Pack), #3970 	DuPont 	Gaylord Archival 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Tyvek envelopes; Part# 3970; Chemical Components: Polyethylene; Tyvek antistatic coating; Purchased: July 2018 	 	Polymer - membrane (< 1mm thick) 	
Overspray Protective Sheeting, 3M No. 06728 	3M 	Zoro.com 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Overspray protective sheeting; Details: Paintable, high-density, tear-resistant, translucent film designed for use in automotive painting industry for edge masking; Chemical Components: High Density Polyethylene film; Purchased: 1/2018 	 	Polymer - membrane (< 1mm thick) 	
Pro-Form Splint Material, 9615000 	Keystone Industries 	Keystone Industries 	Temporary 	2018/09/27 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Transparent Pro-form formed plastic; thickness: 0.020" (0.5 mm); co-polyester; purchased August 2018; formed one week prior to testing 	 	Polymer - block/bulk/pellet 	
PVC crystal clear glossy binding covers 	Oregon Laminations Company 	Oregon Laminations Company 	Temporary 	2018/09/27 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Formable polyvinylchloride plastic; purchased August 2018; formed 1 week before testing 	 	Polymer - block/bulk/pellet 	
Soft EVA .040 (1mm), #9596980 	ProForm 	Keystone Industries 	Temporary 	2018/09/27 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Pro-form formable plastic; Ethyl vinyl acetate; thickness: 0.040" (1mm); August 2018; formed 2 days before testing; there is some residual plaster from the mould on the plastic (test with plaster side down) 	 	Polymer - block/bulk/pellet 	
Sorbothane 0212012-40-10 	Sorbothane, Inc 	unknown 	Temporary 	2018/10/09 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Flexible polymeric sheet; 40 durometer sheet, 12" x 12" x 1/8"; purchased more than 2 years ago 	 	Polymer - sheet (> 1mm thick) 	
AND/OR rubber cork; Skylight AD1007 	Capri Collections 	Capri Collections 	Temporary 	2018/11/28 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Cork & rubber flooring; white rubber & natural cork flecks; Purchased: September 2018 	 	Polymer - sheet (> 1mm thick) 	
AND/OR rubber cork; Gold AD2004 	Capri Collections 	Capri Collections 	Unsuitable 	2018/11/28 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Cork & rubber flooring; yellow & natural cork flecks; Purchased: September 2018 	 	Polymer - sheet (> 1mm thick) 	
Rubber Cork Hybrid; Zonkey 	Siena USA 	Siena USA 	Unsuitable 	2018/11/28 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Grey rubber & cork flooring; purchased september 2018 	 	Polymer - sheet (> 1mm thick) 	
Norseal sponge silicone rubber, R10470 	Saint-Gobain 	Stockwell Elastomerics 	Temporary 	2018/12/19 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Silicone Sheet of textured black foamed silicone 0.032 or 1/32 inch thick; purchased ~2015 	 	Polymer - sheet (> 1mm thick) 	
Norseal sponge silicone rubber, 0.032 R10470M Sil Sponge Plain 	Saint-Gobain 	Stockwell Elastomerics 	Temporary 	2018/12/19 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Sheet of textured orange foamed silicone 1/32 inch thick; Chemical Components: silicone; purchased 10/2018 	 	Polymer - sheet (> 1mm thick) 	
Norseal sponge silicone rubber, 0.062 R10470M Sil Sponge Plain 	Saint-Gobain 	Stockwell Elastomerics 	Temporary 	2018/12/19 	MMA 	Oddy Test (method: 20180821_B_OT ), SPME GCMS	Sheet of textured orange foamed silicone 1/16 inch thick; Chemical Components: silicone; purchased 10/2018 	 	Polymer - sheet (> 1mm thick) 	
Clear acrylic emulsion varnish 	Dacrylate 	Dacrylate 	Temporary 	2019/01/11 	MMA 	Oddy Test (method: 20181031_OT ), SPME GCMS 	Emulsion varnish; cured 2 weeks before testing; batch # 6801210318; date of manufacture: March 16, 2018 	 	Coating - protective (eg.: anti-UV, anti-abrasion, anti-tarnish)	
Expanded polyethylene foam; 1.3 lb/ft^3; EPE 1.3# 	New England Foam 	Unknown 	Temporary 	2018/01/04 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Expanded polyethylene foam; produced as bun; Chemical Components: polyethylene. Others unknown; PURCHASED 11/2017 	 	Polymer - foam - non-building insulation 	
Plastazote LD33 	UFP Technologies 	Zote Foams 	Temporary 	2018/01/10 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	White closed cell crosslinked PE foam; purchased 3/2017 	 	Polymer - foam - non-building insulation 	
Azote Evazote 30 	UFP Technologies 	Zote Foams 	Temporary 	2018/01/10 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	White foam; purchased 3/2017 	 	Polymer - foam - non-building insulation 	
Cabinet gasket material; black 	Unknown 	Delta Designs 	Permanent 	2018/02/16 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	From Delta case manufacturers; Gasket manufactured by Delta; unknown material type 	 	Polymer - gasket 	
Silicone (VMQ) Black Gasket 	BSP Silikon Profile GmbH 	Unknown 	Temporary 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Black silicone gasket; SIPRO; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Ω profile with a 7mm wide base and 5mm diameter circle 	 	Polymer - gasket 	
Silicone (VMQ) geometrical shaped white gasket 	BSP Silikon - Profile GmbH 	Unknown 	Unsuitable 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	White silicone gasket; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Ω profile with a 7mm wide base and 5mm diameter circle 	 	Polymer - gasket 	
Silicone SIPRO black gasket 	BSP Silikon - profile GmbH 	Unknown 	Temporary 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Artificially aged black silicone gasket; baked at 80°C for 8 hours; 5mm diameter; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Received April 2018; Ω profile with a 7mm wide base and 5mm diameter circle 	 	Polymer - gasket 	
Silicone (VMQ) white gasket 	BSP Silikon - profile GmbH 	Unknown 	Unsuitable 	2018/05/31 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Artificially aged white silicone gasket; sample was baked at 80°C for 8 hours; Chemical Components: Cured compound of polysiliaxanes and pyrogenic silica; Received April 2018; Ω profile with a 7mm wide base and 5mm diameter circle 	 	Polymer - gasket 	
Expanded white silicone tubular gasket, 411/PLT 	Technical Rubber SRL 	Technical Rubber SRL 	Temporary 	2018/08/27 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	Foamed round gasket; expanded white silicone tubular gasket. 10 mm O.D., 3 mm I.D.; Purchased: 7/2018 	 	Polymer - gasket 	
Expanded black viton-like tubular gasket, FKM17514/ESP 	Technical Rubber SRL 	Technical Rubber SRL 	Temporary 	2018/08/27 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	Expanded black viton-like tubular gasket. 7 mm O.D., 2 mm I.D. Purchased: 7/2018 	 	Polymer - gasket 	
Heatlok XT insulating expanding foam 	Airseal Insulation Systems 	Demilec, Inc. 	Unsuitable 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	3" thick expanded green urethane foam; sample taken from center of cured block; Month/Year Purchased: 7/2018; Sample sprayed onto cardboard July 19th 2018;Chemical Components: Polyurethane 	 	Polymer - foam - building insulation 	
Viton™ o-rings 	Unknown 	ACE Glass 	Temporary 	2018/10/09 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Viton™ o-rings; comprised of linear co-polymer of vinylidine fluoride and hexafluoropropylene, florine content is between 66 and 70%; Production reference: Z156485- Batch 3110; dimensions: OD: 0.58", ID: 0.38", width: 0.1"; Purchased: August 2018 	 	Polymer - gasket 	
Extruded polystyrene blue board 	Dow Corning 	LeNoble 	Temporary 	2018/10/25 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Extruded polystyrene; 1" thick board; blue; R value = 5; material to be used for crate and box insulation; possible direct contact with larger objects; purchased September 2018 	 	Polymer - foam - building insulation 	
White Celtec® expanded PVC 	Vycom 	Vycom 	Unsuitable 	2018/12/19 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Expanded PVC board, white, thickness: 12 mm thick; this is a repeat of Oddy 2301; Month/Year Purchased: 6/2018, tested after sitting in open air for ~5 months before testing 	 	Board - Plastic/polymeric/synthetic 	
Sintra™ 6 mm white PVC board 	3A Composites 	3A Composites 	Temporary 	2018/12/19 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Expanded PVC board; white; thickness 6 mm; purchased 11/2017 	 	Board - Plastic/polymeric/synthetic 	
Museum Board Black 	Rising 	Talas 	Temporary 	2019/01/11 	MMA 	Oddy Test (method: 20181031_OT ), SPME GCMS 	100% cotton mat board; black; thickness 4-ply; purchased 9/2018; catalog #R45-405820 	 	Board - Natural (eg: wood, cotton) 	
Museum Board Antique 	Rising 	Talas 	Temporary 	2019/01/11 	MMA 	Oddy Test (method: 20181031_OT ), SPME GCMS 	100% cotton mat board; off-white; thickness 4-ply; purchased 9/2018; catalog #R45-405602 	 	Board - Natural (eg: wood, cotton) 	
Museum Board Warm White 	Rising 	Talas 	Temporary 	2019/01/11 	MMA 	Oddy Test (method: 20181031_OT ), SPME GCMS 	100% cotton mat board; off-white; thickness 4-ply; purchased 9/2018; catalog #R45-402447 	 	Board - Natural (eg: wood, cotton) 	
PhotoMount mat board 	Rising 	Talas 	Temporary 	2019/01/11 	MMA 	Oddy Test (method: 20181031_OT ), SPME GCMS 	100% cotton mat board; white; thickness 4-ply; purchased 9/2018; catalog #R45-RPHO4WH3240 	 	Board - Natural (eg: wood, cotton) 	
White natural versatile plastic, laser sintered nylon, printed as custom #3631036 	Shapeways 	Shapeways.com 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Test of Shapeways nylon (white natural versatile plastic) Total weight of nylon in bottom of jar + nylon coupon holders is 2g. 	 	Polymer - block/bulk/pellet 	
3D printed Nylforce Glass Fiber 	Unknown 	Printed Solid Fiber Force Italy 	Temporary 	2018/05/14 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Printed at 245°C; nylon and glass filled; required corrosion resistant print head; purchased 3/2018 	 	Polymer - block/bulk/pellet 	
3D printed Primalloy 99026 or 55500 	Verbatim (possibly) 	Verbatim 	Temporary 	2018/05/14 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed plastic; printed at 215°C; polyester based thermoplastic elastomer; recommended for use with direct drive extruder models; use < 30 mm/sec. Turn retraction off; purchased 02/2018; 	 	Polymer - block/bulk/pellet 	
3D printed PET 	Verbatim 	Verbatim 	Temporary 	2018/04/13 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed plastic; Printed at 215C; catalog #55751; polyethylene terephthalate; hygroscopic so drying filament could be useful to avoid water bubbles in the print; purchased 02/2018 	 	Polymer - block/bulk/pellet 	
3D printed Polypropylene; 0555951-812 	Verbatim 	Verbatim 	Permanent 	2018/04/13 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed plastic; verbatim polypropylene 0555951-812; Printed at 205C; polypropylene purchased 02/2018; "material by nature is non-polar; use packing tape with PP or double sided adhesive on print bed" - per Verbatim 	 	Polymer - block/bulk/pellet 	
3D printed Colorfabb HT clear 	Eastman Chemical 	Printedsolid.com 	Temporary 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed plastic; print T 250-280C; extruded at 250C; build plate temp 100-110C; Tg = 100C; clear; Chemical Components: Eastman Amphora 3D(TM) Co-polyester; purchased 11/2017 	 	Polymer - block/bulk/pellet 	
3D printed CPE+ material, transparent 	Ultimaker 	Printedsolid.com 	Temporary 	2018/03/26 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed plastic; printed filament same day as test; details: 2.85mm diameter; print temp 250 degrees C; plate temp 107 C; flow of 101; speed 45 mm/sec; fan at 5%; no brim or support; supplier: printedsolid.com; purchased 9/2017 	 	Polymer - block/bulk/pellet 	
3D printed Nylon, material 1785 	Ultimaker 	Printedsolid.com 	Temporary 	2017/09/25 	MMA 	Oddy Test (method: 20170918_OT ), SPME GCMS 	3D printed plastic; polypropylene printed with glue for adhesion to plate 2 days before testing; Details: 2.85mm diameter, print temp: 220-240 degrees C; Month/Year Purchased: Sept. 2017 	 	Polymer - block/bulk/pellet 	
3D printed transparent nylon, material 1647 	Ultimaker 	Printedsolid.com 	Permanent 	2017/09/13 	MMA 	Oddy Test (method: 20170918_OT ), SPME GCMS 	3D printed plastic; printed WITHOUT platform adhesive; printed 1 day before testing; 120% speed; 2.85mm diameter; 215° C print temp.; month/year purchased: sept. 2017 	Note: Caprolactam (an amide) was identified as a VOC for this material using SPME-GCMS at 60 degrees C, though it does not appear to adversly affect the metals in the Oddy test. 	Polymer - block/bulk/pellet 	
3D printed transparent nylon, material 1647 	Ultimaker 	Printedsolid.com 	Permanent 	2017/09/13 	MMA 	Oddy Test (method: 20170918_OT ), SPME GCMS 	3D printed plastic; printed WITH platform adhesive; printed 4 days before testing; Details: 2.85mm diameter, print temp: 240-260 degrees C; month/year purchased: sept. 2017 	Note: Caprolactam (an amide) was identified as a VOC for this material using SPME-GCMS at 60 degrees C, though it does not appear to adversly affect the metals in the Oddy test. 	Polymer - block/bulk/pellet 	
Volara 040A 0250WH 	Sekisui Voltek 	Sekisui Voltek 	Unsuitable 	2018/01/10 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Volara type A foam; white; 4 pcf density; 0.25" thick; cross-linked polyolefin foam; purchased 11/2017 	 	Polymer - foam - non-building insulation 	
Ethafoam Cellu-cushion; product 120 	Sealed Air 	Sealed Air 	Temporary 	2018/01/10 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Roll-form polyethylene foam, non-cross-linked; white; purchased 11/2017 	 	Polymer - foam - non-building insulation 	
Ethafoam Synergy; product 1000 	Sealed Air 	Sealed Air 	Temporary 	2018/01/10 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	2" thickness foam block; polyethylene foam; white; purchased 11/2017 	 	Polymer - foam - non-building insulation 	
Biodegradable Packing peanuts; Catalog # S-156; 	Unknown 	Uline 	Temporary 	2018/05/15 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	White cylindrical packing peanuts; foamed cylinder; ~0.5x2 inches; made of starch; decomposes in water; purchased 3/2018. 	 	Polymer - foam - non-building insulation 	
Cellulose wadding; S-656 	Unknown 	Uline 	Unsuitable 	2018/05/15 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Dimpled paper wadding; Made of recycled materials; kraft pulp; purchased 3/2018. 	 	Paper-based - filled (eg.: silica gel, zeolites, alumina) 	
Komatex® 2210 	Kommerling (Huntsville, Alabama plant) 	Kommerling 	Unsuitable 	2018/08/03 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	White matte board, 10 mm thickness; Chemical Components: PVC, limestone, titanium dioxide, Paraffin waxes, and Hydrocarbon waxes; Month/Year Purchased: 6/2018. 	 	Board - Plastic/polymeric/synthetic 	
HDPE Sheet 12" x 12" x 1/8"; #8619K441 	King Plastic Corp 	McMaster-Carr 	Permanent 	2018/08/27 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	1/8" thick HDPE plastic sheet; white; high density polyethylene; durometer 60D; density 0.034 lbs./cu. in.; purchased 5/2018 	 	Board - Plastic/polymeric/synthetic 	
Round Backer Rod 	Alcot Plastics Ltd. 	Weatherall Company Inc. 	Temporary 	2018/08/27 	MMA 	Oddy Test (method: 20180614_OT ), SPME GCMS 	Grey foamed polyethylene round backer rod; diameter 5/8"; Chemical Components: closed cell polyethylene, residual blowing agent: isobutane; Purchased: 5/2018 	 	Polymer - foam - non-building insulation 	
ArmaFORM® PET GR 150 	Armacell Canada Inc, Brampton ON, Canada 	Armacell 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Foamed PET board; density 150 kg/m^3; Chemical Components: 100% post-consumer polyethylene terephthalate; Purchased 7/2018 	 	Board - Plastic/polymeric/synthetic 	
Alpharag Artcare Museum, M8634 	Nielson Bainbridge 	unknown 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	white alpharag board; Supplier: purchased April 2018; thickness: 1.5 mm; Chemical Components: 100% cotton, zeolites, buffering agents (calcium carbonate) 	 	Board - Natural (eg: wood, cotton) 	
Alpharag Artcare Museum, M8644 	Nielson Bainbridge 	unknown 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	black alpharag board; Purchased: April 2018; ; thickness: 1.5 mm; Chemical Components: 100% cotton, zeolites, buffering agents (calcium carbonate) 	 	Board - Natural (eg: wood, cotton) 	
Alpharag Artcare Museum, M8667 	Nielson Bainbridge 	unknown 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Natural alpharag board; Month/Year Purchased: April 2018; Details: thickness: 1.5 mm; Chemical Components: 100% cotton, zeolites, buffering agents (calcium carbonate) 	 	Board - Natural (eg: wood, cotton) 	
27310810 OA 3mm (Optium Acrylic®) 	Tru Vue (plants in McCook, IL and Faribault, MN) 	Tru-Vue 	Temporary 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Acrylic plexi glass with optical coating; Abrasion resistant, anti-static, anti-reflective, 3mm thick acrylic sheet, washed with 1% Micro 90 and rinsed with 18.2 MOhm water prior to testing; filters 98% UV Rays; Chemical Components: acrylic & optical coatings; purchased 5/2018; From manufacturer: For removal of all traces of P-tape residue: Mix a couple drops of dish detergent with distilled water. Use on micro-fiber cloth to clean surface of glazing. Sourced from https://tru-vue.com/solution/optium-acrylic 	 	Board - Plastic/polymeric/synthetic 	
Celtec® expanded PVC 	Vycom 	Vycom 	Unsuitable 	2018/09/27 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Expanded PVC board, white, thickness: 12 mm thick; Month/Year Purchased: 6/2018 	 	Board - Plastic/polymeric/synthetic 	
Dibond® 483MDBWW 	3A Composites 	Harbor Sales 	Temporary 	2018/10/09 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	Aluminum composite sheet; white paint over aluminum with polyethylene core; 2 mm thickness; purchased 8/2018 	 	Board - Plastic/polymeric/synthetic 	
0.031" black silicone rubber sheeting 	Acme Rubber Co. 	Acme Rubber Co 	P 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	thin silicone rubber sheet; durometer: 20; thickness: 0.031"; manufacturer can dye-cut this sheeting if they are supplied drawings. However, their extruded silicone is a different compound and should not be confused with their sheeting; purchased August 2018 	 	Polymer - membrane (< 1mm thick) 	
0.020" black silicone rubber sheeting 	Acme Rubber Co. 	Acme Rubber Co 	P 	2018/09/18 	MMA 	Oddy Test (method: 20180821_OT ), SPME GCMS 	thin silicone rubber sheet; durometer: 20; thickness: 0.020"; manufacturer can dye-cut this sheeting if they are supplied drawings. However, their extruded silicone is a different compound and should not be confused with the sheeting; purchased August 2018 	 	Polymer - membrane (< 1mm thick) 	
Komacel 	Kommerling (Huntsville, Alabama plant) 	Kommerling 	P 	2018/08/03 	MMA 	Oddy Test (method: 20180704_OT ), SPME GCMS 	white PVC sheet/board; Details: white glossy, 10 mm thickness; Chemical Components: PVC, limestone, titanium dioxide. Month/Year Purchased: June/2018 	 	Board - Plastic/polymeric/synthetic 	
Perma/Cor E-Flute corrugated board; 612-0810E 	Unknown 	University Products 	P 	2018/05/31 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Blue/gray corrugated board; Thickness: .0625; Acid-free, lignin-free, and buffered with 3% calcium carbonate; purchased April 2018 	 	Paper-based (eg.: folders, cardboard, sheets) 	
3D printed PP; 0555951-812 	Verbatim 	 	P 	2018/04/13 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D Printed polypropylene; printed at 205C; used U-line brown S-118 packing tape with PP carrier on print bed for adhesion; 2.85 diameter filament, opaque; purchased 02/2018 	 	Polymer - block/bulk/pellet 	
Colorfabb XT clear 	Eastman Chemical 	Printed Solid, Inc. 	P 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Eastman Amphora 3D amorphous copolyester; extruded at 250C; Details: print temperature 230-260C, 2.85mm diameter filament, transparent, Tg is 75C.; purchased 11/2017 	 	Polymer - block/bulk/pellet 	
Colorfabb ngen clear 	Eastman Chemical 	Printed Solid, Inc. 	P 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed copolyester; transparent; unknown extrusion temperature; Details: print temperature 220-240C, advised heat bed temp 60-80C, 2.85mm diameter filament; Purchased 11/2017 	 	Polymer - block/bulk/pellet 	
3D printed nylon filament, Bridge Nylon - Natural 	Taulman Bridge 	Printed Solid, Inc. 	P 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed nylon; extruded at 245-250C; Details: print temperature 250-255C, 2.85mm diameter filament, transparent; nylon; purchased 02/2018 	 	Polymer - block/bulk/pellet 	
expanded polyethylene (EPE) foam; 1.9 lb/ft^3; EPE 1.9# 	Unknown 	New England Foam 	P 	2018/01/04 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Expanded polyethylene foam (EPE); white; produced as bun; purchased 11/2017 	 	Polymer - foam - non-building insulation 	
3D printed Copolyester plus (CPE+), ultimaker material 9725 	Ultimaker 	Printed Solid, Inc. 	P 	2017/12/14 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	3D printed copolyester; printed 11/14/2017; Details: 2.85mm diameter, print temp: 250 degrees C; Purchased Sept. 2017 	 	Polymer - block/bulk/pellet 	
10344-2130 Drawing Paper 	Strathmore Artagain 	Dick Blick 	P 	2017/10/16 	MMA 	Oddy Test (method: 20170918_OT ), SPME GCMS 	Drawing paper; coal black; acid free; 30% post consumer material; catalog# 10344-2130; Coal Black, 19"x15”, 160gsm; Purchased: 08/2017 	 	Paper-based (eg.: folders, cardboard, sheets) 	
TPB052016 Endleaf Bugra Paper 	Hahnemuhle 	TALAS 	P 	2017/10/16 	MMA 	Oddy Test (method: 20170918_OT ), SPME GCMS 	antique endleaf Bugra paper; #313 black; 33" x 41"; 130 gsm; 100% alpha cellulose; acid free and age resistant; purchased aug. 2017 	 	Paper-based (eg.: folders, cardboard, sheets) 	
TPB007014 Antique Endleaf Ppaer 	 	TALAS 	P 	2017/10/16 	MMA 	Oddy Test (method: 20170918_OT ), SPME GCMS 	Antique endleaf paper; black, acid free and lignin free with a minimum of 2% alkaline reserve; purchased: august 2017 	 	Paper-based (eg.: folders, cardboard, sheets) 	
Mylar Film rolls 	unknown 	TALAS 	P 	2017/09/20 	MMA 	Oddy Test (method: 20170913_OT ), SPME GCMS 	Archival Mylar polyester film; transparent; thickness: 0.5 mm; unknown purchase date 	 	Polymer - membrane (< 1mm thick) 	
thermoplastic vinyl traditional wall base/trim 	Johnsonite 	 	P 	2017/03/23 	MMA 	Oddy Test (method: 20170223_OT ), SPME GCMS 	wall base/trim in snow white; dimensions: 3mm thick x ~100mm tall; chemical components: PVC, and other proprietary ingredients; purchased 2017 	 	Polymer - sheet (> 1mm thick) 	
Renshape 460 foamed medium-high density board 	Huntsman Chemical 	 	P 	2016/11/28 	MMA 	Oddy Test (method: 20161007_OT ), SPME GCMS 	medium-high density polyurethane board; density: 48 lb./ft^3; light brown color; Purchased 2016 	 	Board 	
2# VIZION STD BLACK 	Palziv North America 	Rubberlite Incorporated 	T 	2018/08/03 	MMA 	Oddy Test (method: 20180704_OT), SPME GCMS 	Black polyethylene foam; Details: 2 lb/cubic foot density black cross-linked polyethylene foam, purchased as 3"x12"x12" block; Month/Year Purchased: 12/2017; Chemical Components: cross-linked polyethylene 	 	Polymer - foam - non-building insulation 	
Obomodulan® polyurethane board, Obomodulan 500 	OBO- werke 	McCausey Specialty Products 	P 	2018/08/01 	MMA 	Oddy Test (method: 20180704_OT), SPME GCMS 	Obomodulan board; Month/Year Purchased: 5/2018; Details: density is 500 kg/m3; pink colored; foamed polyurethane; Chemical Components: polyurethane 	 	Board - Plastic/polymeric/synthetic 	
Plascore aluminum honeycomb core panel; AA3.6-80 	Plascore Inc. 	Plascore Inc. 	T 	2018/07/24 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Aluminum honeycomb; Chemical Components: 0.020” aluminum, epoxy primer finish, aluminum honeycomb Core 3.6 pcf; Purchased: 3/27/2018; 	 	Board - Plastic/polymeric/synthetic 	
Archival Coroplast 	Coroplast 	Talas 	T 	2018/07/24 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Polypropylene corrugated board; Details: Extruded twin wall fluted plastic sheet; Chemical Components: Polypropylene copolymer; Purchased: 4/2018; 	 	Board - Plastic/polymeric/synthetic 	
non-archival Coroplast 	Coroplast 	Van Owners 	T 	2018/07/24 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Polypropylene corrugated board; Non-archival. Extruded twin wall fluted plastic sheet. Chemical Components: Polypropylene copolymer; Purchased: 4/2018; 	 	Board - Plastic/polymeric/synthetic 	
Neoprene EPDM foam tape, 4311N 	Jacobs and Thompson 	Jacobs and Thompson 	T 	2018/07/24 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Neoprene EPDM foam tape, black, closed cell foam with acrylic adhesive on one side; Chemical Components: EPDM foam, acrylic adhesive; www.foamparts.com; Purchased: 5/2017; 	 	Polymer - gasket 	
Rising Museum Rag Matboard Antique; R405602 	Unknown 	Omega Moulings Co. 	T 	2018/07/24 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	100% cotton rag board, 4 ply, acid-free, neutral pH, buffered with calcium carbonate; received from the Walt Disney museum June 2018 	 	Board - Natural (eg: wood, cotton) 	
Microfoam MF500 1/2 	Pregis 	Pregis 	T 	2018/07/24 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Polypropylene foam in roll; 1/2" thickness; multilayer sheet foam; purchased april 2018 	 	Polymer - foam - non-building insulation 	
King Starboard Marine grade HDPE polymer sheet, KSBBLAKMM.75006.0006.00 	King Plastic Corporation 	McMaster Carr 	P 	2018/07/17 	MMA 	Oddy Test (method: 20171106_OT), SPME GCMS 	Black HDPE board; Purchased May 2018; Chemical Components: black polyethylene 	 	Board - Plastic/polymeric/synthetic 	
MF-S1 Compression Seal 	Manfred Frank 	Manfred Frank 	T 	2018/07/17 	MMA 	Oddy Test (method: 20171106_OT), SPME GCMS 	Silicone S-shaped compression Seal used for butt joints; purchased june 2017 	 	Polymer - gasket 	
Better Backer polyethylene foam 	Robert Holmes Construction Inc. 	Weatherall Company Inc. 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	White trapezoidal foamed polyethylene backer rod; thickness bottom: 1 3/4", top: 7/8"; purchased May 2018 	 	Polymer - foam - non-building insulation 	
Grip Strip foam backing material polyethylene foam 	Timeless Wood Care Products, LLC 	Weatherall Company Inc. 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	White trapezoidal backer rod foam, Top: 1.5"; bottom: 1 7/8"; Chemical Components: (see percentages in SDS) polyethylene foam, dichlorodifluoromethane, dichlorotetrafluoroethane; chlorodifluoroethane; stearyl stearamide; color concentrate in polyethylene; purchased May 2018 	 	Polymer - foam - non-building insulation 	
Optium Museum Acrylic 	Tru Vue (plants in McCook, IL and Faribault, MN) 	Tru Vue 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Anti-reflective, abrasion resistant, and anti-static, 3mm acrylic sheet. Washed with tap water and 1% Micro 90 solution; rinsed with tap water then rinsed with 18.2 Mohm water. 99% UV protective; Chemical Components: acrylic, optical coating; acquired 5/2018; 	 	Board - Plastic/polymeric/synthetic 	
10 mm polypropylene flutecorr, "natural" color 	Laminacorr (Canada) 	Laminacorr (canada) 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Extruded polypropylene corrugated board, 10mm thick; polypropylene; acquired 5/2018 	 	Board - Plastic/polymeric/synthetic 	
Astro-Foam (R); AF-500 1/2"; 	Pregis 	Pregis 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	White polyethylene foam sheet, 1/2" thick, non-abrasive; polyethylene; purchased March 2018 	 	Polymer - foam - non-building insulation 	
Cor-X polypropylene 4 mm corrugated board 	Primex 	Primex Plastics 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Corrugated polypropylene board; 4 mm thickness; Purchased May 2018 	 	Board - Plastic/polymeric/synthetic 	
Proflex Profiles 2" Solid Rounds structural foam (polyethylene foam); 49486 	Unknown 	New England Foam 	T 	2018/07/17 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Round foamed backer rod; Polyethylene CAS No. 9002-88-4; Isobutane CAS No.75-28-5; Details: 1.7-1.9 PCF Extruded, white, 2" x 72" 	 	Polymer - foam - non-building insulation 	
Foam Core Board - 48 x 96" , Black, 3⁄16" thick, S-12861 	Unknown 	Uline 	T 	2018/07/05 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Details: white; 3/16" thick clay coated foam board; https://www.uline.com/BL_870/Uline-Foam-Core-Board?keywords=Foam+Board; Chemical Components: clay coating, extruded polystyrene core; purchased May 2018. 	 	Board - Plastic/polymeric/synthetic 	
LJ Acid-free, LAF40 	Unknown 	Larson Juhl 	T 	2018/07/05 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	Details: white; 3/16" thick acid free foam board; purchased May 2018 	 	Board - Plastic/polymeric/synthetic 	
Nylon material 1647 	Ultimaker 	Ultimaker 	T 	2018/07/05 	MMA 	Oddy Test (method: 20180525_OT), SPME GCMS 	3D printed nylon: 3D printed at 250°C; Industrial-grade impact and abrasion resistance; Durable, High strength-to-weight ratio, Low friction coefficient, Good corrosion resistance to alkalis and organic chemicals; Reduced humidity absorption when compared to other Nylon filaments; purchased September 2017. 	 	Polymer - block/bulk/pellet 	
Poron polyurethane 4701-40 black 	Rogers Corporation 	 	T 	2017/11/27 	MMA 	Oddy Test (method: 20171030_OT), SPME GCMS 	Black polyurethane foam; purchased March 2017 	 	Polymer - foam - non-building insulation 	
Supamag white matt magnetic sheet 	supamag magnetic sheet 	Anchor Magnet 	T 	2017/11/21 	MMA 	Oddy Test (method: 20171024_OT), SPME GCMS 	Printable magnetic sheet with white matte thermoplastic binder on one side (often used for retail graphics); flexible in nature; thickness: 0.6 mm; purchased 9/2017; 	 	Polymer - membrane (< 1mm thick) 	
Supamag white glass magnetic sheet 	Supamag® 	Anchor Magnets 	P 	2017/10/16 	MMA 	Oddy Test (method: 20170918_OT), SPME GCMS 	Printable magnetic sheet with white glossy thermoplastic binder surface on one side; thickness: 0.75 mm; uses: large format retail graphics; Purchased: 9/2017 	 	Polymer - sheet (> 1mm thick) 	
Platinum 2000 silicone tubing 	 	McMaster-Carr 	Temporary 	2017/12/28 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	white silicone tubing; 0.040 ID x 0.085 OD; 60-411-44-10 ft; purchased april 2016 	 	Polymer - block/bulk/pellet 	
PL Premium polyurethane construction adhesive; "PL3X" 	unknown 	Loctite 	Permanent 	2017/12/21 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	polyurethane construction adhesive; this sample was cured 19 days before testing; purchased october 2017 	 	Polymer - adhesive - caulk or sealant 	
OPTIX extruded acrylic sheet 	Plaskolite 	AIN Plastics 	Permanent 	2018/05/17 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	extruded polymethyl methacrylate; Crystal clear, impact- and weather-resistant, OPTIX is a continuously processed acrylic sheet; contains UV stabilization; sourced from The Met's Plexi shop 	 	Polymer - sheet (> 1mm thick) 	
Astariglas GP cast acrylic sheet 	Plaskolite 	AIN Plastics 	Permanent 	2018/05/17 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	ASTARIGLAS® GP cast acrylic sheets are made from 100% virgin MMA (methyl methacrylate monomer); sourced from The Met's Plexi shop 	 	Polymer - sheet (> 1mm thick) 	
clear glass joint strips 180 degree joint 	CR Laurence 	CR Laurence 	Temporary 	2018/05/17 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Hard plastic I-beam for edge-joining sheets of glass; 1/2" tall 1/8" wide; copolyester plastic with unknown adhesive; Contains removable adhesive liner. Tested without red adhesive liner 	 	Polymer - gasket 	
Volara 040A 125WH closed cell foam 	Sekisui Voltek 	Sekisui - US 	Temporary 	2018/04/05 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	white polyethylene foam; 12"x12"x0.25"; density = 4 lb/ft^3; Grade A; Chemical Components: polyethylene; purchased 11/2017 	 	Polymer - foam - non-building insulation 	
Polystone G polyethylene board 	Rochling 	AIN Plastics 	P 	2018/05/17 	MMA 	Oddy Test (method: 20171116_OT) 	white polyethylene board, HDPE, 3/16" thick 	 	Board - Plastic/polymeric/synthetic 	
Komacel Plus, striated PVC board 	Kömmerling 	Kömmerling 	P 	2016/12/19 	MMA 	Oddy Test (method: 20162116_OT ) 	Striated; PVC board 	 	Board - Plastic/polymeric/synthetic 	
BPE-T50 / Polyethyene tubing 0.023" ID x 0.038" OD 	Soloman Scientific 	unknown 	P 	2016/08/04 	MMA 	Oddy Test (method: 20160705_OT ), SPME GCMS 	non-sterile polyethylene tubing 	 	Polymer - block/bulk/pellet 	
TPB004003 (tissue paper) 	Green's 	Talas 	P 	2018/05/14 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	unbuffered lens tissue; Month/Year Purchased: March/2018; Details: An unbuffered, neutral pH tissue made of a select blend of abaca fibers, softer than the acid-free tissues. Paper weight: 10 gsm, 60 microns thick; 	 	Paper-based (eg.: folders, cardboard, sheets) 	
CRL EZ glaze soundstrip 	CR Laurence 	unknown 	T 	2018/05/14 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	Hollow core, square shaped; flexible; 1/4" x 1/4"; extruded silicone 	 	Polymer - gasket 	
black SIL-B silicone foam with acrylic 3M Brand PSA backing adhesive 	Netherland Rubber Company 	Netherland Rubber Co. 	T 	2018/01/10 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	black SIL-B silicone foam gasket with acrylic 3M Brand PSA backing adhesive 	 	Polymer - gasket 	
ETHAFOAM® 900 	Sealed Air Plant in Kentucky 	Hibco Plastics 	P 	2018/01/04 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	9.0 pounds per cubic ft. closed cell Polyethylene foam 	 	Polymer - foam - non-building insulation 	
ETHAFOAM® 220 	Sealed Air Plant in Kentucky 	Hibco Plastics 	T 	2018/01/04 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	2.2 pounds per cubic ft. closed cell Polyethylene foam 	 	Polymer - foam - non-building insulation 	
Alucobond 	3A Composites GmbH 	unknown 	P 	2017/12/21 	MMA 	Oddy Test (method: 20171116_OT ), SPME GCMS 	unpainted silver with (seeming) black core 	 	Board - Plastic/polymeric/synthetic 	
translucent, food grade 1/32" thick silicone rubber sheet 	Unknown 	Canal Rubber Supply Co. 	P 	2017/11/27 	MMA 	Oddy Test (method: 20171030_OT ), SPME GCMS 	(purchased off the shelf 8/2016) 	 	Polymer - sheet (> 1mm thick) 	
SHAPEWAYS stainless STEEL (infiltrated with bronze) 60/40 	Unknown 	Shapeways.com 	T 	2017/11/27 	MMA 	Oddy Test (method: 20171030_OT ), SPME GCMS 	HIGH COPPER CONTENT; Chemical Components: Shapeways’ 3D printed steel is Stainless Steel Alloy 420 infiltrated with Bronze (90% Cu/10% Sn). It is a matrix material composed of 60% stainless steel and 40% bronze; Details: manufactured via additive manufacturing process; purchased 10/2017; NOTE: observe the sample material before and after test. 	 	Metal (eg.: mechanical fastener) 	
Raw Aluminum 	Unknown 	Shapeways.com 	P 	2017/11/27 	MMA 	Oddy Test (method: 20171030_OT ), SPME GCMS 	3D printed by Shapeways 10/2017; manufactured via selective laser melting. Aluminum is fused and melted using a laser from a bed of metallic powder. This process fully melts the powder rather than just sintering it, creating a solid, homogenous aluminum alloy; note: sample jars contained less than 2g of sample. jar A contained 1.845 g & Jar B contained 1.516 g sample 	 	Metal (eg.: mechanical fastener) 	
Food-Grade SuperCushioning Polyethylene Foam Sheets w/ Ultra-Smooth Texture 	Pres-on Corporation 	McMasterCarr 	Unsuitable 	2018/03/06 	MMA 	Oddy Test (method: 20180206_OT), SPME GCMS 	Polyethylene foam sheet, catalogue #8722K11; 3/8" thick 	 	Polymer - foam - non-building insulation 	
transparent extruded D-seal rubber 	Elastostar Rubber 	Elastostar Rubber 	Unsuitable 	2018/03/06 	MMA 	Oddy Test (method: 20180206_OT), SPME GCMS 	transparent silicone D gasket; Clear 50-60 Durometer; FDA Silicone; 21-22mm Wide X 13-15mm high X 5mm wide X 2mm; FDA extruded silicone; purchased Januray 2018 	 	Polymer - gasket 	
Food-Grade SuperCushioning Polyethylene Foam Sheets w/ Ultra-Smooth Texture 	Pres On Corporation 	McMasterCarr 	Unsuitable 	2018/03/06 	MMA 	Oddy Test (method: 20180206_OT), SPME GCMS 	3/8" thick black polyethylene foam sheet; catalogue #8722K11; purchased 10/2017 	 	Polymer - foam - non-building insulation 	
Bisco BF 1000 White 	Rogers Corporation 	Elastomeric Material Solutions, Carol Stream, IL	Temporary 	2018/02/26 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	White silicone foam with pressure sensitive adhesive on one side; purchased januray 2018 	 	Polymer - foam - non-building insulation 	
Bisco BF-2000 black 	Rogers Corporation 	Elastomeric Material Solutions, Carol Stream, IL	Temporary 	2018/02/26 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	black silicone foam with pressure sensitive adhesive on one side; purchased January 2018; 	 	Polymer - foam - non-building insulation 	
Renshape 440 	Huntsman Chemical 	Freeman Manufacturing and Supply Co 	Pass 	2018/02/26 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	foamed polyurethane board (dense) 	 	Board - Plastic/polymeric/synthetic 	
Black gasket 	BSP silikone Profile GmBH 	 	Temporary 	2018/02/26 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	Chemical Components: HTV-silicone, polysiliaxanes and pyrogenic silica; received January 2018 	 	Polymer - gasket 	
0.125" clear silicone rubber sheeting 	Acme Rubber 	Acme Rubber 	Pass 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	Clear silicone rubber sheet; durometer: 40; manufacturer may dyeCut this sheeting if drawings are supplied. Their extruded silicone can be a different compound than the tested sheeting. 	 	Polymer - gasket 	
Intramedic non-radiopaque polyethylene tubing, model #427411 	Clay Adams Brand 	Beckton Dickenson 	Pass 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	non-sterile polyethylene tubing; 0.023" ID, 0.038" OD; purchased January 2018 	 	Polymer - block/bulk/pellet 	
Colorsil N in color RAL 7022 (gray) 	Kawo Karl Wolpers 	 	Temporary 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	Colored one component silicone sealant; cured 24 hours 	 	Polymer - adhesive - caulk or sealant 	
PE60 Flesh - model P60FLXL8 	Ultralon Foam Group 	Ultralon 	Unsuitable 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	Polyethylene foam board; 34mm thick, 2ft x 3ft. Produced in Ho chi minh, Vietnam - only manufacture site for Ultralon. Batch made with pellets sourced from Germany. Ultralon chemically cross-linked polyethylene foam using azo carbamide foaming agent, claim high 90% cross-linking. Can laminate with heat or glue. available in 24-44mm thickness. purchased 12/2017 	 	Polymer - foam - non-building insulation 	
PE30 White; model #PE30WHS3 	Ultralon Foam Group 	Ultralon 	Temporary 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	Polyethylene foam board; 41mm thick, 2ft x 3 ft. Produced in Ho chi minh, Vietnam - only manufacture site for Ultralon. Batch made with pellets sourced from Germany. Ultralon chemically cross-linked polyethylene foam using azo carbamide foaming agent, claim high 90% cross-linking. Can laminate with heat or glue. available in 24-44mm thickness. purchased: 12/2017 	 	Polymer - foam - non-building insulation 	
Ultralon PE140 White; model #PE140UVBWHXLHD 	Ultralon Foam Group 	Ultralon 	Unsuitable 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	Polyethylene foam board; Details: 39.5mm thick, 2ft x 3ft, Produced in Ho chi minh, Vietnam - only manufacture site for Ultralon. Batch made with pellets sourced from Germany. Ultralon chemically cross-linked polyethylene foam using azo carbamide foaming agent, claim high 90% cross-linking. Can laminate with heat or glue. available in 24-44mm thickness. purchased: 12/2017 	 	Polymer - foam - non-building insulation 	
EPU40 	Carbon3D 	Carbon3D 	Temporary 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	3D printed elastomeric polyurethane; Black, dog bone shaped samples printed on M2 Printer. ~4 inches long, 1 inch wide with 8mm width at narrow portion of 'bone'. Testing as possible customizable 'foam' or cushioning structure for shipping art. purchased december 2017 	 	Polymer - block/bulk/pellet 	
Viton® 60 	Rainbow Rubber 	Rainbow Rubber 	Pass 	2018/02/21 	MMA 	Oddy Test (method: 20171116_OT), SPME GCMS 	black Viton® 60 1/8" thick y 3/4" wide black gasketing; must be trademarked product 	 	Polymer - gasket 	
MDF + 3 coats Resene Lumbersider White 	Resene Paints, Newmarket 	 	Fail, Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood plus paint/varnish 	 	Board - composite (eg. Corian, drywall) 	
MDF + 3 coats Resene Polythane moisture cured polyurethane, Clear Gloss 	Resene Paints, Newmarket 	 	Pass, suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood plus paint/varnish 	In vitrine or case 	Board - composite (eg. Corian, drywall) 	
MDF 	 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood 	 	Board - composite (eg. Corian, drywall) 	
Medite ZF 	Andy Jorritsma 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood 	 	Board - composite (eg. Corian, drywall) 	
Medite ZF + 3 coats Resene Lumbersider White 	Andy Jorritsma + Resene Paints, Newmarket 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood plus paint/varnish 	 	Board - composite (eg. Corian, drywall) 	
Medite ZF + 3 coats Resene Polythane Moisture Cured Polyurethane, Clear Gloss 	Andy Jorritsma + Resene Paints, Newmarket 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood plus paint/varnish 	 	Board - composite (eg. Corian, drywall) 	
Hoop Pine + 3 coats Resene Lumbersider White 	Andy Jorritsma + Resene Paints, Newmarket 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood 	 	Board - composite (eg. Corian, drywall) 	
Hoop Pine + 3 coats Resene Polythane Moisture Cured Polyurethane, Clear Gloss 	Andy Jorritsma + Resene Paints, Newmarket 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood 	Outside vitrine or case 	Board - composite (eg. Corian, drywall) 	
Cedar, sample from old seasoned shelving plank 	 	 	Suitable for permanent use 	1999/12/21 	AWMM 	Oddy test 	Wood 	Outside vitrine or case 	Board - natural (eg. wood, cotton) 	Change in patina of copper coupon, (lightened) but no obvious corrosion.
Pine 	 	 	Suitable for temporary use 	1999/12/21 	AWMM 	Oddy test 	Wood 	Outside vitrine or case. Temporary use only. 	Board - natural (eg. wood, cotton) 	Slight clouding of the lead coupon, and change in patina of copper, as above.
Hoop Pine 	Andy Jorritsma 	 	Not suitable for use 	2006/05/16 	AWMM 	Oddy test 	Wood 	 	Board - natural (eg. wood, cotton) 	
Pine wood with pink surface (treated?) 	? 	 	Not suitable for use 	2009/01/12 	AWMM 	Oddy test 	Wood 	 	Board - natural (eg. wood, cotton) 	
Colourfield card, KSA25A3PW-10 	Gordon Harris 	Gordon Harris 	Suitable for permanent use 	2017/05/18 	AWMM 	Oddy test 	Paper, board 	In vitrine or case 	Board - natural (eg. wood, cotton) 	
Orfit Eco 	Orfit industries, Vosweld 	 	Suitable for temporary use 	2003/02/18 	AWMM 	Oddy test 	Paper, board 	Outside vitrine or case. Suitable for use in controlled situations. 	Paper-based (eg. folder, cardboard, sheet) 	Few white spots on lead coupon.
Elastomer Products Ltd. clear gasket/bulb seal 	Elastomer Products Ltd. 	 	Suitable for temporary use 	1998/09/28 	AWMM 	Oddy test 	Gasket materials 	Outside vitrine or case 	Polymer - adhesive - caulk or sealant 	Lead and copper coupons slightly changed: small specks of white corrosion products on lead with uneven patina, and slight discolouration of copper.
Compression Seal, permanent elastic silicone, Clear 	Frank Europe GmbH 	 	Suitable for temporary use 	2007/11/29 	AWMM 	Oddy test 	Gasket materials 	Outside vitrine or case 	Polymer - adhesive - caulk or sealant 	
Foam PVC 	 	 	Not suitable for use 	2016/05/02 	AWMM 	Oddy test 	 	 	Polymer - foam - non building insulation 	
Woods Glass gasket materials 	 	 	Suitable for temporary use 	2003/09/16 	AWMM 	Oddy test 	Gasket materials 	Outside vitrine or case. Suitable for temporary use in display cases and storage units. 	Polymer - gasket 	Slight tarnish on silver coupon, moderate corrosion on lead coupon. Tarnishing on copper coupon in keeping with control copper coupon.
Manfred Frank gasket materials 	 	 	Suitable for permanent use 	2003/09/16 	AWMM 	Oddy test 	Gasket materials 	Outside vitrine or case 	Polymer - gasket 	
Netherfield Case Gasket 	Andy Jorritsma 	 	Suitable for temporary use 	2006/05/16 	AWMM 	Oddy test 	Gasket materials 	Outside vitrine or case 	Polymer - gasket 	
Brush seal, panel connection system, permanent elastic silicone, Clear 	Frank Europe GmbH 	 	Not suitable for use 	2007/11/29 	AWMM 	Oddy test 	Gasket materials 	 	Polymer - gasket 	
Compression Seal, permanent elastic silicone, Clear 	Frank Europa GmbH 	 	Suitable for temporary use 	2008/02/28 	AWMM 	Oddy test 	Gasket materials 	In vitrine or case 	Polymer - gasket 	Slight darkening of lead coupon. Suitable for permanent use to seal butt joints in showcases.
Brush seal, panel connection system, permanent elastic silicone, Clear 	Frank Europa GmbH 	 	Suitable for temporary use 	2008/02/28 	AWMM 	Oddy test 	Gasket materials 	In vitrine or case. Suitable for permanent use to apply to leading edges of doors and opposing edges. 	Polymer - gasket 	Slight overall darkening of lead coupon.
PTFE (Polytetrafluoroethylene, Teflon), white 	 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - sheet (>1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
SOMOS 9210 	DSM Desotech 	 	Not suitable for use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - sheet (>1mm thick) 	
SOMOS NeXt 	DSM Desotech 	 	Not suitable for use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - sheet (>1mm thick) 	
SOMOS Watershed XC11122 	DSM Desotech 	 	Not suitable for use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - sheet (>1mm thick) 	
PA 3200 GF 	EOS GmbH - Electro Optical Systems 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - sheet (>1mm thick) 	
PA 2200 	EOS GmbH - Electro Optical Systems 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - sheet (>1mm thick) 	
Benchmark Sueded polyethylene with adhesive , Black 	Benchmark 	 	PASS 	1999/07/13 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Fabric - batting & padding and adhesive 	
Benchmark Sueded polyethylene with adhesive , Grey 	Benchmark 	 	Suitable for temporary use 	1999/07/13 	AWMM 	 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Fabric - batting & padding and adhesive 	
Benchmark Sueded polyethylene with adhesive , Black 	Benchmark 	 	Suitable for temporary use 	1999/09/14 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Fabric - batting & padding and adhesive 	
Clear Electrical Heat Shrink Tubing 41 Series 	Dick Smith Electronics 	Dick Smith Electronics 	Suitable for permanent use 	2003/01/12 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	
3M Window Film, Scotchfield, polyester film plus acrylate adhesive liner, S40 (previous SH4CLARL) 	3M New Zealand Ltd. 	3M New Zealand Ltd. 	Not suitable for use 	2008/02/28 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
rubber mat, black 	 	 	Not suitable for use 	2013/11/26 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
rubber mat, black 	 	 	Not suitable for use 	2013/11/26 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
Anoxic chamber film, CEPAC ® HD100 Super Heavy Duty Barrier, MIL-PRF-131K, class 1, Green/silver 	Cadillac Products Packaging Company 	 	Suitable for permanent use 	2015/07/22 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	Pretty much the same as the control.
UHMWPE (ultra high molecular weight polyethylene), black 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
HMPE (High molecular weight polyethylene?), white 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
Polypropylene, white 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
Tapco Chamber tool, firearms safety lock, ZTOOLCST01, yellow 	TAPCO 	 	Suitable for temporary use 	2016/03/24 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - block/bulk/pellet 	The tests all exploded (stopper blew off) during testing, so results may not be accurate. Only slight reaction with lead, so could probably be used for permanent storage so long as not direct contact with metal, and well ventilated.
ABS, white 	MakerBot Industries LLC 	 	Suitable for permanent use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - block/bulk/pellet 	
ABS, Dark Saguine Red 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
PLA, natural 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
PLA, Pearly White 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
PLA, black, UP FILA C-12-02 PLA-BLACK 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
SLA Perform 	 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - block/bulk/pellet 	
Procell Foam non cross linked, closed cell, LDP 	Dunlop Flexible Foams 	 	Suitable for permanent use 	1999/08/15 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	Dark patina on lead coupon acceptable; other coupons unchanged. Suitable for permanent use.
Ethafoam 220, Dow Chemicals 	Dunlop Flexible Foams 	 	Suitable for permanent use 	2002/03/25 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Plastazote with adhesive backing LD 45 	 	 	Suitable for permanent use 	2002/03/25 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Evazote, Black EV 50 	Dunlop Flexible Foams 	 	Suitable for permanent use 	2006/05/16 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Heat-bonded Polyethylene Foam, Black 	A&E Karsten 	A&E Karsten 	Suitable for permanent use 	2006/05/16 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Cross-Linked Expanded PE Foam (black) 	A & E Karsten 	A & E Karsten 	Suitable for permanent use 	2012/06/20 	AWMM 	Oddy test 	Plastics, foams 	In vitrine or case 	Polymer - foam - non building insulation 	
Clear Electrical Heat Shrink Tubing 41 Series 	Dick Smith Electronics 	Dick Smith Electronics 	Suitable for permanent use 	2003/01/12 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	
3M Window Film, Scotchfield, polyester film plus acrylate adhesive liner, S40 (previous SH4CLARL) 	3M New Zealand Ltd. 	3M New Zealand Ltd. 	Not suitable for use 	2008/02/28 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
rubber mat, black 	 	 	Not suitable for use 	2013/11/26 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
rubber mat, black 	 	 	Not suitable for use 	2013/11/26 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
Anoxic chamber film, CEPAC ® HD100 Super Heavy Duty Barrier, MIL-PRF-131K, class 1, Green/silver 	Cadillac Products Packaging Company 	 	Suitable for permanent use 	2015/07/22 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	Pretty much the same as the control.
UHMWPE (ultra high molecular weight polyethylene), black 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
HMPE (High molecular weight polyethylene?), white 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
Polyproylene, white 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
DWP 125, ES1000 thin wall heat shrink, DWP 125 unheated 	transnet 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contaminaton of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distingished. Some change in the lead, but the yellow coating appeared on the control too, so I suspect it is contamination on the stoppers.
DWP 125, ES1000 thin wall heat shrink, DWP 125 pre-shrunk 	transnet 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
RNF100 general purpose low voltage heat shrink, RNF 100 unheated 	tyco electronics 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
RNF100 general purpose low voltage heat shrink, RNF 100 pre-shrunk 	tyco electronics 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
ezishrink EZHSWH2/1, HS WH 2/1 unheated 	transnet 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
ezishrink EZHSWH2/1, HS WH 2/1pre-shrunk 	transnet 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
ezishrink EZHSBK3/1.5, HS BK 3/1.5 unheated 	transnet 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
ezishrink EZHSBK3/1.5, HS BK 3/1.5 pre-shrunk 	transnet 	 	Suitable for permanent use 	2014/06/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer -tubing 	Some contamination of the coupons, but most tests had better results than the controls, and none were worse than the controls. The duplicate nature of the tests allowed contamination to be distinguished.
Medical grade silicone LSR-4305 Platinum liquid silicone (set solid) 	 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Other - silicone moulding compound 	
Mouldfast Fix-All silicone, neutral cure 	 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Other - silicone moulding compound 	
Tygon tube, S-50-HL Class VI 	Saint-Gobain Performance Plastics? 	 	Suitable for permanent use 	2009/01/12 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Other - tygon tubing 	
Tapco Chamber tool, firearms safety lock, ZTOOLCST01, yellow 	TAPCO 	 	Suitable for temporary use 	2016/03/24 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - block/bulk/pellet 	The tests all exploded (stopper blew off) during testing, so results may not be accurate. Only slight reaction with lead, so could probably be used for permanent storage so long as not direct contact with metal, and well ventilated.
ABS, white 	MakerBot Industries LLC 	 	Suitable for permanent use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - block/bulk/pellet 	
ABS, Dark Saguine Red 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
PLA, natural 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
PLA, Pearly White 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
PLA, black, UP FILA C-12-02 PLA-BLACK 	MakerBot Industries LLC 	 	Not suitable for use 	2017/02/17 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Polymer - block/bulk/pellet 	
SLA Perform 	 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - block/bulk/pellet 	
Procell Foam non cross linked, closed cell, LDP 	Dunlop Flexible Foams 	 	Suitable for permanent use 	1999/08/15 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	Dark patina on lead coupon acceptable; other coupons unchanged. Suitable for permanent use.
Ethafoam 220, Dow Chemicals 	Dunlop Flexible Foams 	 	Suitable for permanent use 	2002/03/25 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Plastazote with adhesive backing LD 45 	 	 	Suitable for permanent use 	2002/03/25 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Evazote, Black EV 50 	Dunlop Flexible Foams 	 	Suitable for permanent use 	2006/05/16 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Heat-bonded Polyethylene Foam, Black 	A&E Karsten 	A&E Karsten 	Suitable for permanent use 	2006/05/16 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - foam - non building insulation 	
Cross-Linked Expanded PE Foam (black) 	A & E Karsten 	A & E Karsten 	Suitable for permanent use 	2012/06/20 	AWMM 	Oddy test 	Plastics, foams 	In vitrine or case 	Polymer - foam - non building insulation 	
Clear Electrical Heat Shrink Tubing 41 Series 	Dick Smith Electronics 	Dick Smith Electronics 	Suitable for permanent use 	2003/01/12 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	
3M Window Film, Scotchfield, polyester film plus acrylate adhesive liner, S40 (previous SH4CLARL) 	3M New Zealand Ltd. 	3M New Zealand Ltd. 	Not suitable for use 	2008/02/28 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
rubber mat, black 	 	 	Not suitable for use 	2013/11/26 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
rubber mat, black 	 	 	Not suitable for use 	2013/11/26 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Polymer - membrane (<1mm thick) 	
Anoxic chamber film, CEPAC ® HD100 Super Heavy Duty Barrier, MIL-PRF-131K, class 1, Green/silver 	Cadillac Products Packaging Company 	 	Suitable for permanent use 	2015/07/22 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	Pretty much the same as the control.
UHMWPE (ultra high molecular weight polyethylene), black 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
HMPE (High molecular weight polyethylene?), white 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
Polypropylene, white 	LEP engineering plastics 	 	Suitable for permanent use 	2016/04/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Polymer - membrane (<1mm thick) 	The tests all exploded (stopper blew off) during testing, so results may not be accurate.
Neoprene strip 	Howard King and Assoc. Mt. Roskill 	Howard King and Assoc. Mt. Roskill 	Suitable for temporary use 	1998/05/07 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Neoprene strip 	Pb and Ag unchanged, Cu coupon changed colour. Suitable for temporary use or permanent use with selected collections only.
6040 Sellotape Anti Skid Dots, clear 	Sellotape Products (NZ) Limited 	 	Not suitable for use 	2008/03/04 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Other - dots 	
Actifoam, black/blue-grey 	Beele Engineering BV 	 	Suitable for temporary use 	2014/03/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Other - fire barrier 	
Rise multicable transits:rapid sealing system, 	Beele Engineering BV 	 	Suitable for temporary use 	2014/03/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Other - fire barrier 	A building requirement, so it has to be used. Just ensure that objects are not located closet to fire intrusions, and no fire intrusion are present in display cases against walls.
Nofirno firestop, sealant, red 	Beele Engineering BV 	 	Not suitable for use 	2014/03/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Other - fire barrier 	A building requirement, so it has to be used. Just ensure that objects are not located cloaset to fire intrusions, and no fire instrusion are present in display cases against walls.
Rise/Ultra Crusher, black 	Beele Engineering BV 	 	Suitable for temporary use 	2014/03/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Other - fire barrier 	A building requirement, so it has to be used. Just ensure that objects are not located cloaset to fire intrusions, and no fire instrusion are present in display cases against walls.
3M Ultra plastic pipe liner material, black 	3M 	 	Not suitable for use 	2014/03/06 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	 	Other - fire barrier 	A building requirement, so it has to be used. Just ensure that objects are not located cloaset to fire intrusions, and no fire instrusion are present in display cases against walls.
Avery Dennison HP DOL 2080, vinyl laminate, HP DOL 2080, matte 	3M New Zealand 	Big Colour 	Suitable for permanent use 	2017/05/18 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Board - plastic/polymeric/synthetic 	
3M Controltac, 180C-10, white 	3M New Zealand 	Big Colour 	Suitable for permanent use 	2017/05/18 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Board - plastic/polymeric/synthetic 	
Clear strip 	Glass Relate, Kelston 	Glass Relate, Kelston 	Suitable for temporary use 	1998/05/07 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Clear strip 	Formation of corrosion on Pb beginning, Cu and Ag coupons have changed colour.
Parafilm M 	 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	Outside vitrine or case 	Coating - grease, oil, wax 	
TC-857 PART A, polyurethane resin 	BJB Enterprises, Inc. 	 	Suitable for permanent use 	2017/03/23 	AWMM 	Oddy test 	Plastics, films, foams, plastic sheeting 	In vitrine or case 	Coating - paint & primer 	
Kingspan KS1100CS, insulated panel, metal surface only 	Kingspan. New Zealand:Kingspan Ltd. 	Kingspan. New Zealand:Kingspan Ltd. 	Suitable for permanent use 	2016/06/20 	AWMM 	Oddy test 	Misc. 	In vitrine or case 	Board - composite (eg. Corian, drywall) 	
Kingspan KS1100CS, insulated panel, foam core only 	Kingspan. New Zealand:Kingspan Ltd. 	Kingspan. New Zealand:Kingspan Ltd. 	Suitable for permanent use 	2016/06/20 	AWMM 	Oddy test 	Misc. 	In vitrine or case 	Board - composite (eg. Corian, drywall) 	
Kingspan KS1100CS, insulated panel 	Kingspan. New Zealand:Kingspan Ltd. 	Kingspan. New Zealand:Kingspan Ltd. 	Suitable for permanent use 	2016/06/20 	AWMM 	Oddy test 	Misc. 	In vitrine or case 	Board - composite (eg. Corian, drywall) 	
Alabaster-white with grey 	3form 	3form 	Pass 	2008/12/19 	CAM 	Oddy 	White Alabaster with grey for exhibit cases 	for use non-contact; test run at 60 degrees C for 4 weeks 	Inorganic, stone 	Description: Cu- slight tarnish; Ag- slight yellowing around edges; Pb- dark gray
Chroma-Ghost Applied 	3form 	3form 	Pass 	2008/12/19 	CAM 	Oddy 	polymer resin substrate for exhibit cases- decks 	test run at 60 degrees C for 4 weeks 	Board - plastic/polymeric/synthetic 	Description: Cu- no change; Ag- no change; Pb- no change
Apoxie sculpt 	AVES Studio 	 	P 	2015/07/28 	CAM 	Oddy 	epoxy paste for mounts and conservation treatment 	for use non-contact; test run at 65 degrees C for 4 weeks 	Polymer- block/bulk 	Description: Cu- almost no change; Ag- no change; Pb- hazy grey appearance
Pure bond 	Columbia Forest Products 	Nisbet Brower, Cincinnati 	Ok, with coating 	2007/01/31 	CAM 	Oddy 	plywood 	for use non-contact; test run at 60 degrees C for 4 weeks 	Board- natural composite 	Description: Cu- slight darkening; Ag- good; Pb- slight traces of white
PureBond birch faced plywood 	Columbia Forest Products 	Nisbet Brower, Cincinnati 	Retest 	2006/09/29 	CAM 	Oddy 	plywood 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- natural composite 	Description: Cu- slight darkening/ iridescence around edges; Ag- shiny-ok; Pb- thin layer white corrosion
PureBond birch faced plywood 	Columbia Forest Products 	Nisbet Brower, Cincinnati 	Retest 	2006/09/29 	CAM 	Oddy 	plywood 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- natural composite 	Description: Cu- shiny- OK; Ag- slightly dull at edges; Pb- white/yellow corrosion on both sides
Plastic Tubing 	 	Dunbar 	Pass 	2016/06/01 	CAM 	Oddy 	Clear Tubing, for mounts 	for use non-contact; test run at 60 degrees C for 4 weeks 	Polymer- sheet/tube (>1 mm thick) 	Description: Cu- Even darkening ; Ag- Even darkening; Pb- Slight haziness
Birch Plywood 	 	Nisbet Brower, Cincinnati 	fail 	2016/06/01 	CAM 	Oddy 	plywood 	for use non-contact; test run at 60 degrees C for 4 weeks 	Board- natural composite 	Description: Cu- Red with slight black; Ag- no change; Pb- grey discoloration
Dow MDF 	 	Nisbet Brower, Cincinnati 	FAIL 	2006/09/29 	CAM 	Oddy 	medium density fiberboard 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- natural composite 	Description: Cu- darkened overall; Ag- darkened overall; Pb- thick white corrosion
Dow MDF 	 	Nisbet Brower, Cincinnati 	FAIL 	2006/09/29 	CAM 	Oddy 	medium density fiberboard 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- natural composite 	Description: Cu- darkened overall; Ag- darkened overall; Pb- thick white corrosion
MDF 	Uniboard Canada 	Nisbet Brower, Cincinnati 	Retest 	2006/09/29 	CAM 	Oddy 	medium density fiberboard 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- natural composite 	Description: Cu- slight darkening/ iridescence around edges; Ag- shiny-ok; Pb- white/yellow corrosion on both sides
MDF 	Uniboard Canada 	Nisbet Brower, Cincinnati 	Retest 	2006/09/29 	CAM 	Oddy 	medium density fiberboard 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- natural composite 	Description: Cu- slight darkening/ iridescence around edges; Ag- shiny-ok; Pb- white/yellow corrosion on both sides
Closed cell neoprene sponge SNC-1 with adhesive backing 	 	Netherland Rubber 	Pass 	2007/06/11 	CAM 	Oddy 	closed cell neoprene sponge SNC with adhesive backing 	for use non-contact; test run at 60 degrees C for 4 weeks 	Polymer- gasket 	Description: Cu- slight tarnish; Ag- great; Pb- slight darkening
Gasket (thick) 	 	Netherland Rubber 	Short-term 	2016/05/25 	CAM 	Oddy 	black gasket, thick 	for use non-contact; test run at 60 degrees C for 4 weeks 	Polymer- gasket 	Description: Cu- spotted tarnish; Ag- no change; Pb- slight tarnish
Gasket (thin) 	 	Netherland Rubber 	Retest 	2016/06/01 	CAM 	Oddy 	black gasket, thin 	for use non-contact; test run at 60 degrees C for 4 weeks 	Polymer- gasket 	Description: Cu- Uneven tarnish; Ag- Slight yellow; Pb- non change
Gasket (thin) 	 	Netherland Rubber 	Fail 	2016/07/01 	CAM 	Oddy 	black gasket, thin 	for use non-contact; test run at 60 degrees C for 4 weeks 	Polymer- gasket 	Description: Cu- Uneven darkening; Ag- no change; Pb- Unenven whitening
Poplar 	 	Nisbet Brower, Cincinnati 	Fail 	2016/06/01 	CAM 	Oddy 	wood 	for use non-contact; test run at 60 degrees C for 4 weeks 	Board- natural (wood) 	Description: Cu- Mostly Black; Ag- Uneven corrosion; Pb- Uneven haziness
Poplar Plywood 	 	Nisbet Brower, Cincinnati 	Pass 	2016/05/25 	CAM 	Oddy 	plywood 	; test run at 60 degrees C for 4 weeks 	Board- natural composite 	Description: Cu- Purple ; Ag- no change; Pb- Slight lightening
Volara 	Voltek 	Voltek 	Retest 	2016/06/01 	CAM 	Oddy 	polyethylene, closed cell foam sheet 	for use non-contact; test run at 60 degrees C for 4 weeks 	Polymer- foam 	Description: Cu- Uneven tarnish; Ag- slight change; Pb- Slight haziness
Extira 	Jeld-Wen 	 	FAIL 	2006/09/29 	CAM 	Oddy 	alternative to MDF 	for use in contact; test run at 60 degrees C for 3 weeks 	Board- composite 	Description: Cu- slight darkening/ iridescence around edges; Ag- shiny-OK; Pb- dull white haze overall
Extira 	Jeld-Wen 	 	FAIL 	2006/09/29 	CAM 	Oddy 	alternative to MDF 	for use in contact; test run at 60 degrees C for 3 weeks 	substrate with paint/coating 	Description: Cu- slight darkening/ iridescence around edges; Ag- shiny-ok; Pb- dull white haze overall
Fosshape-all grades (dry shaped) 	 	 	Pass 	2009/11/04 	CAM 	Oddy 	mounts for textiles 	test run at60 for 2 weeks 	Fabric- nonwoven synthetic 	Description: Cu- spotted tarnish; Ag- no change; Pb- even darkening
Fosshape-all grades (raw) 	 	 	Pass 	2009/11/04 	CAM 	Oddy 	mounts for textiles 	test run at60 for 2 weeks 	Fabric- nonwoven synthetic 	Description: Cu- minor tarnish; Ag- no change; Pb- even darkening
Fosshape-all grades (wet-heat shaped) 	 	 	Pass 	2009/11/04 	CAM 	Oddy 	mounts for textiles 	test run at60 for 2 weeks 	Fabric- nonwoven synthetic 	Description: Cu- spotted tarnish; Ag- no change; Pb- even darkening
Polyethylene foam 	 	 	Pass 	2010/04/12 	CAM 	Oddy 	black polyethylene foam 	test run at 60 degrees C for 3 weeks 	Polymer- foam - non building insulation 	Description: Cu- slight darkening; Ag- no change; Pb- even darkening
Perma/Dur tan unbuffered barrier board 	unknown 	University Products 	T 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	Acid-free, lignin-free, non-buffered 40 pt. board 	none 	BOARD 	
Perma/Dur tan buffered barrier board 	unknown 	University Products 	F 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	Acid-free, lignin-free, buffered (3% CaCO3) pH 8.5 40 and 60 pt. board 	none 	BOARD 	
Bainbridge Alpharag Artcare black buffered 	Nielsen Bainbridge 	unknown 	F 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	100% virgin alpha-cellulose fiber with zeolites, 3-5% buffer to pH 8.9 	none 	BOARD 	
Rising Photomount board white unbuffered 	Rising 	unknown 	P 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	non-buffered 100% cotton board, acid and lignin free 	none 	BOARD 	
Rising Museum board antique buffered 	Rising 	unknown 	F 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	acid-free, neutral pH, buffered with calcium carbonate 	none 	BOARD 	
Bainbridge Alpharag Artcare colonial cream 	Nielsen Bainbridge 	unknown 	F 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	100% virgin alpha-cellulose fiber with zeolites, 3-5% buffer to pH 8.9 	none 	BOARD 	
black volara 	Volara 	unknown 	P 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	closed cell foam sheet 	none 	FOAM 	
white volara 	Volara 	unknown 	P 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	closed cell foam sheet 	none 	FOAM 	
white volara, 10 years old 	Volara 	unknown 	P 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	closed cell foam sheet 	10 year old sample 	FOAM 	
Mylar, 0.0005 mm 	unknown 	unknown 	P 	2013 	Hodgkins et. al.	Oddy Test, silver nanofilm 	clear polyester film 	none 	FILM, Plastic 	
Expanded PVC foam sheet 19 mm thick Celtec 	Vycom 	OCIP 	F 	2015 June 	Autry 	Oddy Test 	PVC, White 	none 	BOARD 	none
Expanded PVC foam sheet 12 mm thick Celtec 	Vycom 	OCIP 	T 	2015 June 	Autry 	Oddy Test 	PVC, White 	Temp use, no contact with objects 	BOARD 	none
Celtec 	Vycom 	OCIP 	F 	2014 Dec 	Autry 	Oddy Test 	PVC, White 	Bought December 2013. 	BOARD 	none
Sintra or Celtec 	3AComposites or Vycom 	OCIP 	F 	2014 Dec 	Autry 	Oddy Test 	PVC, White 	Bought April 2013. 	BOARD 	none
Freefoam PVC 10 mm ordered in 2013 	Jain Americas 	Laird Plastics 	F 	2014 Dec 	Autry 	Oddy Test 	PVC , White, 48"x96" 	Test 3 of 3 	BOARD 	none
Freefoam PVC 10 mm ordered in 2013 	Jain Americas 	Laird Plastics 	F 	2014 Mar-Apr 	Autry 	Oddy Test 	PVC , White, 48"x96" 	The pH of water in control: 5.5-6, in test material: 8.5. Test 2 of 3 	BOARD 	none
Freefoam PVC 10 mm ordered in 2013 	Jain Americas 	Laird Plastics 	F 	2014 Oct-Nov 	Autry 	Oddy Test 	PVC , White 	The pH of water in control: 8, in test material: 9. Test 1 of 3 	BOARD 	none
Freefoam PVC 13 mm ordered in 2013 	Jain Americas 	Laird Plastics 	F 	2014 Dec 	Autry 	Oddy Test 	PVC , White, 48"x96" 	Test 3 of 3 	BOARD 	none
Freefoam PVC 13 mm ordered in 2013 	Jain Americas 	Laird Plastics 	F 	2014 Mar-Apr 	Autry 	Oddy Test 	PVC , White, 48"x96" 	The pH of water in control: 5.5-6, in test material: 8.5. Test 2 of 3 	BOARD 	none
Freefoam PVC 13 mm ordered in 2013 	Jain Americas 	Laird Plastics 	F 	2014 Oct-Nov 	Autry 	Oddy Test 	PVC , White 	material absorbed all the water. Test 1 of 3 	BOARD 	none
Expanded closed-cell polyvinyl chloride ( PVC) material similar to Sintra 	unknown 	Laird Plastics 	P 	2009 Apr-May 	Autry 	Oddy Test 	PVC , White 	Test periodically 	BOARD 	none
6 mm"Sintra" 	unknown 	Laird Plastics 	P no contact 	2011 Feb-Mar 	Autry 	Oddy Test 	PVC, White 	Test periodically. The pH of water before test: 5.5-6, after test: 7.5-8 	BOARD 	
ALUCORE, PLATINUM WHITE 	3A COMPOSITES 	3A COMPOSITES 	T 	2013/06/26 	BM 	Oddy Test 	POWDER COATED ALUMINIUM HONEYCOMB BOARD WITH PVDF LACQUER, WHITE, 	PREP/Drying time: N/A, test #7889 	BOARD 	none
FOREX CLASSIC, 5MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , WHITE, 	PREP/Drying time: N/A, test #8019 	BOARD 	none
FOREX COLOR, BLACK 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , BLACK, 	PREP/Drying time: N/A, test #8018 	BOARD 	none
FOREX COLOR, BLUE 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , BLUE, 	PREP/Drying time: N/A, test #8015 	BOARD 	none
FOREX COLOR, DARK BLUE 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , BLUE, DARK, 	PREP/Drying time: N/A, test #8016 	BOARD 	none
FOREX COLOR, DARK YELLOW 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , YELLOW, DARK, 	PREP/Drying time: N/A, test #8011 	BOARD 	none
FOREX COLOR, GREEN 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , GREEN, 	PREP/Drying time: N/A, test #8014 	BOARD 	none
FOREX COLOR, GREY 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , GREY, 	PREP/Drying time: N/A, test #8017 	BOARD 	none
FOREX COLOR, ORANGE 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , ORANGE, 	PREP/Drying time: N/A, test #8012 	BOARD 	none
FOREX COLOR, RED 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , RED, 	PREP/Drying time: N/A, test #8013 	BOARD 	none
FOREX COLOR, YELLOW 3MM 	3A COMPOSITES 	3A COMPOSITES 	P 	2013/09/16 	BM 	Oddy Test 	PVC , YELLOW, 	PREP/Drying time: N/A, test #8010 	BOARD 	none
FOREX PRINT, 	3A COMPOSITES (M) 	BAF GRAPHICS (S) 	P 	2010/09/16 	BM 	Oddy Test 	POLYSTYRENE, WHITE, 	PREP/Drying time: N/A, test #6988 	BOARD 	none
DIBOND, BRITISH GREEN 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, GREEN, 	PREP/Drying time: N/A, test #6577 	BOARD 	none
DIBOND, BUTLERFINISH 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER, 	PREP/Drying time: N/A, test #6581 	BOARD 	none
DIBOND, BUTLERFINISH COPPER 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	P 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, COPPER, 	PREP/Drying time: N/A, test #6583 	BOARD 	none
DIBOND, BUTLERFINISH GOLD 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, GOLD, 	PREP/Drying time: N/A, test #6582 	BOARD 	none
DIBOND, BUTLERFINISH STEEL 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	P 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER, 	PREP/Drying time: N/A, test #6571 	BOARD 	none
DIBOND, MAYAN GOLD METALLIC 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	P 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, GOLD, 	PREP/Drying time: N/A, test #6580 	BOARD 	none
DIBOND, MIRROR 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER, 	PREP/Drying time: N/A, test #6584 	BOARD 	none
DIBOND, RAL 1015 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, YELLOW, 	PREP/Drying time: N/A, test #6574 	BOARD 	none
DIBOND, RAL 1023 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, RED, 	PREP/Drying time: N/A, test #6573 	BOARD 	none
DIBOND, RAL 3020 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, WHITE, 	PREP/Drying time: N/A, test #6572 	BOARD 	none
DIBOND, RAL 5002 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	P 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, CREAM, 	PREP/Drying time: N/A, test #6575 	BOARD 	none
DIBOND, RAL 5002 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, BLUE, 	PREP/Drying time: N/A, test #6576 	BOARD 	none
DIBOND, RAL 9005 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	T 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, BLACK, 	PREP/Drying time: N/A, test #6578 	BOARD 	none
DIBOND, RAL 9006 	3A COMPOSITES (M) 	SELECTAPLAS LIMITED (S) 	P 	2009/08/05 	BM 	Oddy Test 	POLYETHYLENE CORE, ALUMINIUM SKIN, POLYESTER LACQUER, SILVER, SAMPLE MELTED, MAY ACCOUNT FOR TEMPORARY RATING 	PREP/Drying time: N/A, test #6579 	BOARD 	none
ALUCORE, 1-TYPE POLYESTER LACQUER 	3A COMPOSITES (M) 	UNKNOWN 	T 	2009/08/05 	BM 	Oddy Test 	ALUMINIUM, POLYESTER LACQUER, SILVER, 	PREP/Drying time: N/A, test #6587 	BOARD 	none
ALUCORE BASE, MILL FINISH 	3A COMPOSITES (M) 	UNKNOWN 	P 	2009/08/05 	BM 	Oddy Test 	ALUMINIUM, SILVER, 	PREP/Drying time: N/A, test #6586 	BOARD 	none
FOAM-X, 	3A COMPOSITES (M) 	UNKNOWN 	F 	2010/06/08 	BM 	Oddy Test 	POLYSTYRENE CORE WITH COATED MULTY-LAYERED PAPER LINERS, WHITE, 	PREP/Drying time: N/A, test #6850 	BOARD 	none
FOREX CLASSIC, 	3A COMPOSITES (M) 	UNKNOWN 	P 	2009/08/25 	BM 	Oddy Test 	PVC, BLACK, 	PREP/Drying time: N/A, test #6593 	BOARD 	none
FOREX SMART, 	3A COMPOSITES (M) 	UNKNOWN 	P 	2009/08/25 	BM 	Oddy Test 	UV RESISTANT POLYSTYRENE SUFACE AND POLYSTYRENE CORE, WHITE, 	PREP/Drying time: N/A, test #6591 	BOARD 	none
GATORFOAM, 	3A COMPOSITES (M) 	UNKNOWN 	F 	2009/08/25 	BM 	Oddy Test 	POLYSTYRENE CORE, UREA RESIN SURFACE, WHITE, 	PREP/Drying time: N/A, test #6595 	BOARD 	none
GATORFOAM, 	3A COMPOSITES (M) 	UNKNOWN 	F 	2009/08/25 	BM 	Oddy Test 	POLYSTYRENE CORE WITH RESIN INPREGNATED LINERS, BLACK, 	PREP/Drying time: N/A, test #6602 	BOARD 	none
HYLITE, 	3A COMPOSITES (M) 	UNKNOWN 	T 	2009/08/05 	BM 	Oddy Test 	POLYPROPYLENE CORE, ALUMINIUM SKIN, SILVER, SLIGHT YELLOWISH HUE 	PREP/Drying time: N/A, test #6585 	BOARD 	none
KAPA COLOUR, 	3A COMPOSITES (M) 	UNKNOWN 	T 	2009/08/25 	BM 	Oddy Test 	POLYSTYRENE CORE WITH COLOURED PLASTIC COATED LINERS, BLACK, 	PREP/Drying time: N/A, test #6601 	BOARD 	none
KAPA FIX, 	3A COMPOSITES (M) 	UNKNOWN 	F 	2009/08/25 	BM 	Oddy Test 	POLYSTYRENE CORE WITH ALUMINIUM REINFORCED LINERS, WHITE, 	PREP/Drying time: N/A, test #6596 	BOARD 	none
KAPA LINE, 	3A COMPOSITES (M) 	UNKNOWN 	F 	2009/08/25 	BM 	Oddy Test 	POLYSTYRENE CORE WITH CROMA-SUBSITUTE LINERS, WHITE, 	PREP/Drying time: N/A, test #6599 	BOARD 	none
KAPA MOUNT, 	3A COMPOSITES (M) 	UNKNOWN 	F 	2009/08/25 	BM 	Oddy Test 	POLYSTYRENE CORE WITH ALUMINIUM REINFORCED LINERS, WHITE, 	PREP/Drying time: N/A, test #6597 	BOARD 	none
KAPA PLAST, 	3A COMPOSITES (M) 	UNKNOWN 	P 	2009/09/25 	BM 	Oddy Test 	POLYSTYRENE CORE WITH PLASTIC COATED CELLUCARTLON LINERS, WHITE, 	PREP/Drying time: N/A, test #6611 	BOARD 	none
KAPA PREMIUM POLY BOARD, 	3A COMPOSITES (M) 	UNKNOWN 	P 	2009/07/06 	BM 	Oddy Test 	POLYURETHANE AND PAPER, WHITE, 	PREP/Drying time: N/A, test #6545 	BOARD 	none
Sintra 	3A Composites 	unknown 	Pass 	2012/09/26 	NHM 	Oddy test 	Expanded PVC Bodard 	None 	wood alternative 	n/a
BUMPONS, 	3M 	3M 	F 	2011/03/16 	BM 	Oddy Test 	POLYURETHANE, CLEAR, 	PREP/Drying time: STUCK TO ITSELF, test #7206 	ANTISLIP/ ANTIVIBRATION 	none
BUMPONS (SMALL), SJ530209 (W7.9 H2.2) 	3M 	3M 	F 	2011/08/25 	BM 	Oddy Test 	POLYURETHANE, CLEAR, 	PREP/Drying time: STUCK TO THEMSELVES, test #7286 	MOUNT/ MOUNT MAKING 	none
Bumpon self adhesive bumpers 	3M 	Home Depot 	fail 	2012/01/10 	CMA 	Oddy Test 	Plasticizer-free urethane, A-20 Acrylic adhesive 	none 	support, mount 	none
Oxidation arrest paper 	3M 	unknown 	Pass w/ reservations 	1996/01/24 	GCI 	Oddy test 	None 	None 	pollutant scavenger? 	n/a
Sparkfast lightweight filler 	3M 	unknown 	Pass w/ reservations 	2005/08/22 	GCI 	Oddy test 	None 	None 	Spackle 	n/a
Sparkfast lightweight filler 	3M 	unknown 	Pass w/ reservations 	2005/08/22 	GCI 	Oddy test 	None 	None 	filler, spackle 	n/a
PTFE TUBING, TW18 1.14 X 0.31mm 	ADTECH 	ADTECH 	P 	2009/04/13 	BM 	Oddy Test 	PTFE, CLEAR, 	PREP/Drying time: N/A, test #6420 	SLEEVING/ TUBING 	none
PTFE TUBING (THICK), TW SERIES 	ADTECH 	ADTECH 	P 	2009/03/20 	BM 	Oddy Test 	POLYETRAFLUOROETHYLENE, CLEAR, 	PREP/Drying time: N/A, test #6329 	SLEEVING/ TUBING 	none
Aeroflex EPDM (ethylene propylene diene monomer) closed cell elastometric thermal insulation 	Aeroflex 	Airefrig Australia 	PASS 	2006 	NAA 	PAT 	7 mm thick 	none 	foam, closed cell insulation 	n/a
Polypropylene 35 mm negative page 	Albox Australia 	Albox Australia 	PASS 	1996 	NAA 	PAT 	6 strip 	none 	protective plastic sheet, polypropylene 	n/a
Polypropylene box 	Albox Australia 	Albox Australia 	PASS 	1996 	NAA 	PAT 	none 	none 	box, polypropylene 	n/a
Polypropylene box 	Albox Australia 	Albox Australia 	PASS 	2006 	NAA 	PAT 	none 	none 	box, polypropylene 	n/a
Polypropylene photo album cover 	Albox Australia 	Albox Australia 	PASS 	2004 	NAA 	PAT 	polypropylene 	none 	album, cover 	n/a
AIREX RIGID FOAM, R82.60 	ALCAN AIREX AG 	ALCAN AIREX AG 	F 	2009/08/25 	BM 	Oddy Test 	RIGID POLYMER FOAM , CREAM, 	PREP/Drying time: N/A, test #6604 	FOAM 	none
Archivart interleaving paper 	Archivart® 	Zetta Florence 	PASS 	1996 	NAA 	PAT 	none 	none 	paper 	n/a
Archivart library board 	Archivart® 	Zetta Florence 	PASS 	1996 	NAA 	PAT 	grey, light 	none 	board, paper 	n/a
Archivart photographic storage paper 	Archivart® 	Zetta Florence 	PASS 	1996 	NAA 	PAT 	none 	none 	paper 	n/a
Archivart Photo-Tex Tissue 	Archivart® 	Zetta Florence 	PASS 	1997 	NAA 	PAT 	none 	none 	paper, tissue 	n/a
ANTIQUE RANGE THICKNESS 2800, 64934 	ARQUADIA (M) 	CXD (S) 	P 	2014/03/12 	BM 	Oddy Test 	MOUNTBOARD, BROWN, 	PREP/Drying time: N/A, test #8159 	BOARD 	none
Optix offset Milli Vanilla 	Australian Paper 	Australian Paper 	PASS 	2000 	NAA 	PAT 	none 	none 	paper, 110 gsm 	n/a
Reflex archival (copypaper) 	Australian Paper 	AustralianPaper 	PASS 	2004 	NAA 	PAT 	none 	none 	paper, copy 	n/a
Saxton Chardonnay paper 140 gsm 	Australian Paper 	Spicers 	PASS 	2012 	NAA 	PAT 	140 gsm 	none 	paper 	n/a
Archival folder board(white) 	Australian Paper 	Zetta Florence 	PASS 	2006 	NAA 	PAT 	320 gsm 	none 	board, folder 	n/a
Cotton linter paper 	AustralianPaper 	AustralianPaper 	PASS 	2004 	NAA 	PAT 	cotton linter 	none 	paper 	n/a
Fixit 	Aves Studio 	Aves Studio 	Pass 	2012/02/01 	CMA 	Oddy Test 	Aluminum/ two-part epoxy putty 	used for custom contoured mounts, not in direct contact with artwork 	filler, epoxy putty 	none
BAREX RESINS BARRIER, 4261 0.05 MM 	BAREX RESINS 	BAREX RESINS 	P 	2010/04/09 	BM 	Oddy Test 	ACRYLONITRILE METHYL ACRYLATE COPOLYMER, CLEAR, 	PREP/Drying time: N/A, test #6793 	BARRIER 	none
BEAD ALONG, 19 strand 	BEAD ALONG 	BEAD ALONG 	P 	2009/10/08 	BM 	Oddy Test 	STEEL WIRE COATED IN NYLON, , 	PREP/Drying time: N/A, test #6619 	FASTENER 	none
BEAD ALONG, 49 strand 	BEAD ALONG 	BEAD ALONG 	T 	2009/10/08 	BM 	Oddy Test 	STEEL WIRE COATED IN NYLON, , 	PREP/Drying time: N/A, test #6620 	FASTENER 	none
BEAD ALONG, 7 strand 	BEAD ALONG 	BEAD ALONG 	P 	2009/10/08 	BM 	Oddy Test 	STEEL WIRE COATED IN NYLON, , 	PREP/Drying time: N/A, test #6618 	FASTENER 	none
STICKY WAX, 09-100 	BENCHMARK 	BENCHMARK 	F 	2009/02/19 	BM 	Oddy Test 	WAX, CLEAR, 	PREP/Drying time: 48 HOURS, test #6235 	MOULDING MATERIAL 	none
MAKROLON UV CLEAR SHEET, 2099 	BEYER (M) 	AMARI PLASTICS (S) 	P 	2013/12/30 	BM 	Oddy Test 	POLYCARBONATE, CLEAR, SAMPLE MELTED, MAY ACCOUNT FOR TEMPORARY RATING 	PREP/Drying time: N/A, test #8132 	BOARD 	none
FOAMALUX, GSM9100, MIC1300 	BRETT MARTIN 	BRETT MARTIN 	P 	2010/08/27 	BM 	Oddy Test 	PVC, WHITE, 	PREP/Drying time: N/A, test #6924 	BOARD 	none
MASTER FLEX, 460 	BSFA 	BSFA 	F 	2012/03/20 	BM 	Oddy Test 	POLYURETHANE, GREY, 	PREP/Drying time: 4 WEEKS, test #7422 	FLOORING 	none
MASTERTOP 1324, 1324 	BSFA 	BSFA 	F 	2012/03/20 	BM 	Oddy Test 	POLYURETHANE WITH EPOXY PRIMER, GREY, 	PREP/Drying time: 4 WEEKS, test #7423 	FLOORING 	none
MASTERTOP TC441P, TC441P 	BSFA 	BSFA 	P 	2012/03/20 	BM 	Oddy Test 	POLYURETHANE, GREY, STICKY DEPOSIT ON LEAD COUPON BUT NO CORROSION VISIBLE 	PREP/Drying time: 8 WEEKS , test #7426 	FLOORING 	none
UCRETE MFA, MFA 	BSFA 	BSFA 	P 	2012/03/20 	BM 	Oddy Test 	HYBRID POLYURETHANE, GREY, 	PREP/Drying time: 4 WEEKS, test #7425 	FLOORING 	none
UCRETE MFAS, MFAS 	BSFA 	BSFA 	P 	2012/03/20 	BM 	Oddy Test 	HYBRID POLYURETHANE ANTISTATIC, GREY, 	PREP/Drying time: 4 WEEKS, test #7424 	FLOORING 	none
WEDI BOARD, 6MM BA6 	CAESAR CERAMICS 	CAESAR CERAMICS 	P 	2009/07/29 	BM 	Oddy Test 	POLYSTYRENE CORE, POLYMER MODIFIED CEMENT AND GLASS FIBER, GREY, 	PREP/Drying time: N/A, test #6551 	BOARD 	none
Barrier paper 	Canson Australia (Arjo Wiggins) 	Canson Australia (Arjo Wiggins) 	PASS 	1996 	NAA 	PAT 	none 	none 	paper 	n/a
Library board, light weight 	Canson Australia (Arjo Wiggins) 	Canson Australia (Arjo Wiggins) 	PASS 	2003 	NAA 	PAT 	lightweight 	none 	board 	n/a
Canson conservation board 	Canson Australia (Arjo Wiggins) 	The Heirloom BoxCompany 	PASS 	2003 	NAA 	PAT 	none 	none 	board 	n/a
Slide sleeves 	Champion Plastics 	Champion Plastics 	PASS 	1996 	NAA 	PAT 	none 	none 	sleeve, slide 	n/a
CHEMODEX L.Q.G. MOLY LIQUID GREASE AEROSOL, 	CHEMODEX LTD. (M) 	UNKNOWN 	P 	2013/12/12 	BM 	Oddy Test 	BUTANE, MINERAL OIL, MOLYBDENUM DISULPHIDE, GELLED WITH CALCIUM LANOLATE, PROPELLANTS, BLACK, USED TO REPAIR FLOORS 	PREP/Drying time: 1 WEEK, test #8079 	MISC 	none
PEEL WALLCOVERING RELEASE COAT, DILUTED 	CLAM-BRUMMER LTD 	CLAM-BRUMMER LTD 	T 	2013/09/10 	BM 	Oddy Test 	 	PREP/Drying time: 24 HOURS, test #7938 	BARRIER 	none
Gasket 8325 	Clean Seal, Inc. 	Clean Seal 	Pass, not to be used in direct contact with artwork.	2011/07/07 	CMA 	Oddy Test 	black Silicone with 3m double-stick tape 	8490, 8543, 8556, 8598, 8531 	gasket 	none
Gasket 8325 	Clean Seal, Inc. 	Clean Seal 	Pass 	2012/05/15 	CMA 	Oddy Test 	black Silicone gasket with 3m double-stick tape 	other profiles of same material 8490, 8543, 8556, 8598, 8531 	gasket, silicone 	none
Archival Plus polypropylene storage bag 	Clear File 	Clear File 	PASS 	1996 	NAA 	PAT 	none 	none 	bag, polypropylene 	n/a
COATED FABRIC TAPE, 7995C, 25MM, ECRU 	COLE FABRICS 	COLE FABRICS 	T 	2013/05/30 	BM 	Oddy Test 	POLYURETHAN COATED COTTON, CREAM, 	PREP/Drying time: N/A, test #7857 	MISC 	none
TEXTILE RIBBON, 73969 	COLE FABRICS 	COLE FABRICS 	T 	2013/11/14 	BM 	Oddy Test 	POLYESTER TAFFETA, POLTURETHANE COATING, WHITE, 	PREP/Drying time: N/A, test #8056 	FASTENER 	none
acid-free tissue paper 	Conservation by Design 	unknown 	PASS 	2009/01/20 	BM 	Oddy test 	white paper 	test 6175 	paper, tissue 	n/a
Corrosion Intercept Coin bag 	Conservation by Design(s) 	Unknown 	Pass 	2009/01/20 	BM 	Oddy 	polymer film with copper 	orange/dark brown in color 	bag, pollutants scavenger/filter 	n/a
POLYESTER POCKET, 115 x 158 MM PYSPOL 0006 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2013/12/12 	BM 	Oddy Test 	POLYESTER, CLEAR 	PREP/Drying time: N/A, test #8081 	CONTAINER 	none
PREMIER ARCHIVAL BOX BOARD, 1300 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2012/01/20 	BM 	Oddy Test 	CARD, GREY, 	PREP/Drying time: N/A, test #7367 	BOARD 	none
PREMIER FLUTED BOX BOARD, EB FLUTE 4.4MM 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2012/01/20 	BM 	Oddy Test 	CARD, GREY, 	PREP/Drying time: N/A, test #7368 	BOARD 	none
TIMECARE HERITAGE MUSEUM BOARD, UNBUFFERED, 4 PLY, 1650 MICRONS, DULL WHITE, BDTHMC3304 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2013/05/09 	BM 	Oddy Test 	PAPER, WHITE, 	PREP/Drying time: N/A, test #7850 	BOARD 	none
TIMECARE RANGE MUSEUM BOARD , C3311, 1650 MICRONS 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2014/03/12 	BM 	Oddy Test 	PAPER, BLACK, 	PREP/Drying time: N/A, test #8161 	BOARD 	none
TYCORE BOARD, 12MM 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2014/01/16 	BM 	Oddy Test 	BUFFERED ARCHIVAL PAPER, WHITE, 	PREP/Drying time: N/A, test #8138 	BOARD 	none
WHISPER TISSUE REMOISTENABLE STARCH COATED JAPANESE PAPER, PAJAPL7910 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2013/12/12 	BM 	Oddy Test 	TOSA KOZO PAPER COATED WITH TAPIOCA STARCH ADHESIVE, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #8082 	PAPER 	none
ACID FREE TISSUE PAPER 	CONSERVATION BY DESIGN 	CONSERVATION BY DESIGN 	P 	2009/01/20 	BM 	Oddy Test 	TISSUE PAPER, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #6175 	PAPER 	none
ECOPHANT SUPER MILL BOARD LYDAMORE, BDSMBE1171 1.1 mm 	CONSERVATION-BY-DESIGN 	CONSERVATION-BY-DESIGN 	P 	2010/05/28 	BM 	Oddy Test 	ACID-FREE BOARD, GREEN, 	PREP/Drying time: N/A, test #6819 	BOARD 	none
ECOPHANT SUPER MILL BOARD LYDAMORE, BDSMBE1571 1.5 mm 	CONSERVATION-BY-DESIGN 	CONSERVATION-BY-DESIGN 	P 	2010/05/28 	BM 	Oddy Test 	ACID-FREE BOARD, GREEN, 	PREP/Drying time: N/A, test #6820 	BOARD 	none
HERITAGE MUSEUM BOARD, A3311 550 MICRONS 	CONSERVATION-BY-DESIGN 	CONSERVATION-BY-DESIGN 	P 	2009/06/09 	BM 	Oddy Test 	, BLACK, 	PREP/Drying time: N/A, test #6480 	BOARD 	none
HERITAGE MUSEUM BOARD, D4711 2200 MICRONS 	CONSERVATION-BY-DESIGN 	CONSERVATION-BY-DESIGN 	P 	2009/06/09 	BM 	Oddy Test 	, BLACK, 	PREP/Drying time: N/A, test #6479 	BOARD 	none
SILICONE VEGETABLE PARCHMENT RELEASE PAPER, 	CONSERVATION-BY-DESIGN 	CONSERVATION-BY-DESIGN 	P 	2010/05/28 	BM 	Oddy Test 	SILICONE ON PAPER, WHITE, WHITE LINING 	PREP/Drying time: N/A, test #6821 	FILM 	none
Corrosion Intercept Foam 	Conservation by Design(s) 	Unknown 	Pass 	2009/01/20 	BM 	Oddy 	polymer foam with copper particles 	orange/dark brown color 	foam, pollutant scavenger/filter 	n/a
Corrosion Intercept Foam 	Conservation by Design(s) 	Unknown 	Pass 	2009/01/20 	BM 	Oddy 	polymer foam with copper particles 	orange/dark brown color 	foam, pollutant scavenger/filter 	n/a
Tycore Board 	Conservation by Design 	unknown 	PASS 	2014/01/16 	BM 	Oddy test 	12 mm, 2G, white buffered archival paper 	none 	Board, paper reinforced 	n/a
Corex polypropylene fluteboard (grey) 	Corex Plastics 	Corex Plastics 	PASS 	1996 	NAA 	PAT 	grey 	none 	board, fluted polypropylene 	n/a
NEEDLED POLYESTER, 	COWENS LTD 	COWENS LTD 	T 	2009/01/22 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #6140 	PADDING 	none
POLYESTER WADDING, 202 	COWENS LTD 	COWENS LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #7469 	PADDING 	none
POLYESTER WADDING, 402 	COWENS LTD 	COWENS LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #7467 	PADDING 	none
POLYESTER WADDING, ULTRASOFT 	COWENS LTD 	COWENS LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #7468 	PADDING 	none
HONEYCOMBED POLYPROPYLENE T2 CASES, 	CP CASES LIMITED 	CP CASES LIMITED 	P 	2009/07/06 	BM 	Oddy Test 	POLYPROPYLENE, BLACK, 	PREP/Drying time: N/A, test #6548 	CONTAINER 	none
HONEYCOMBED POLYPROPYLENE T2 CASES, 	CP CASES LIMITED 	CP CASES LIMITED 	P 	2009/07/06 	BM 	Oddy Test 	POLYPROPYLENE, BLUE, 	PREP/Drying time: N/A, test #6549 	CONTAINER 	none
HONEYCOMBED POLYPROPYLENE T2 CASES, 	CP CASES LIMITED 	CP CASES LIMITED 	P 	2009/07/06 	BM 	Oddy Test 	POLYPROPYLENE, RED, 	PREP/Drying time: N/A, test #6550 	CONTAINER 	none
WONDERFLEX, 	DAZAN FABRICS 	DAZAN FABRICS 	P 	2013/07/08 	BM 	Oddy Test 	POLYCAPROL ACETATE, POLYSTYRENE, EVA FILM POLYESTER FIBRE, CREAM, 	PREP/Drying time: N/A, test #7902 	MOUNT/ MOUNT MAKING 	none
Silicone gasket 	Delta Design 	unknown 	Pass 	2000/09/19 	GCI 	Oddy test 	None 	None 	gasket 	n/a
Depron 	Depron Foam 	unknown 	PASS 	2009/01/20 	BM 	Oddy test 	white polystyrene foam 	test 6171 	foam 	n/a
ETHAFOAM, 900 	DOW CHEMINCAL CO. 	DOW CHEMINCAL CO. 	P 	2009/02/09 	BM 	Oddy Test 	HDPE, WHITE, 	PREP/Drying time: N/A, test #6280 	FOAM 	none
SILASTIC P1 CASTING SILICONE, P-1 	DOW CORNING 	DOW CORNING 	P 	2010/12/07 	BM 	Oddy Test 	SILICONE, WHITE, 	PREP/Drying time: 12 HOUR CURE, test #7064 	ANTISLIP/ ANTIVIBRATION 	none
SILASTIC P1 CASTING SILICONE, P-1 	DOW CORNING 	DOW CORNING 	P 	2010/12/07 	BM 	Oddy Test 	SILICONE, BLACK, 	PREP/Drying time: 12 HOUR CURE, test #7065 	ANTISLIP/ ANTIVIBRATION 	none
Ethafoam 220, polyethylene foam, closed cell 	Dunlop Foams 	Dunlop Foams 	PASS 	2006 	NAA 	PAT 	100 mm thick 	none 	foam, closed cell polyethylene 	n/a
EVA 30 	Dunlop Foams 	Dunlop Foams 	PASS 	2006 	NAA 	PAT 	15 mm thick (Code Q86454) 	none 	foam, ethylene vinyl acetate 	n/a
EVA 45 	Dunlop Foams 	Dunlop Foams 	PASS 	2006 	NAA 	PAT 	11 mm thick, cream 	none 	foam, ethylene vinyl acetate 	n/a
3 panels 	DuPont 	unknown 	FAIL 	1991/03/12 	GCI 	Oddy test 	None 	None 	panel 	n/a
PTFE SHEET 'RELIC WRAP', 	DUPONT (M) 	SCREWFIX DIRECT (S) 	P 	2012/03/30 	BM 	Oddy Test 	PTFE, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7473 	MOUNT/ MOUNT MAKING 	none
CORIAN, 	DUPONT (M) 	UNKNOWN 	P 	2009/04/13 	BM 	Oddy Test 	ACRYLIC RESIN WITH FILLERS, WHITE, 	PREP/Drying time: N/A, test #6402 	BOARD 	none
PTFE THREAD SEAL TAPE, 12MM X 0.075MM 	DUPONT SCREW FIX DIRECT 	DUPONT SCREW FIX DIRECT 	P 	2012/03/30 	BM 	Oddy Test 	PTFE, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7472 	MOUNT/ MOUNT MAKING 	none
POLYLIGHT, 	EARLSMANN 	EARLSMANN 	P 	2010/06/08 	BM 	Oddy Test 	ACRYLIC, CLEAR, 	PREP/Drying time: N/A, test #6844 	BOARD 	none
FINGEBLOBBS, PD2010 	FINGEBLOBBS 	FINGEBLOBBS 	T 	2009/04/14 	BM 	Oddy Test 	POLYURETHANE, CLEAR, 	PREP/Drying time: STUCK TO ITSELF, test #6401 	ANTISLIP/ ANTIVIBRATION 	none
SHOWCASE SEAL 'D' , 	FLOREA D.SIGN WWW.FLOREADSIGN.DE 	FLOREA D.SIGN WWW.FLOREADSIGN.DE 	P 	2012/12/04 	BM 	Oddy Test 	SILICON RUBBER, BLACK, SAMPLE DID NOT DRY (DESIGNED NOT TO) 	PREP/Drying time: N/A, test #7659 	SEAL 	none
SHOWCASE SEAL 'D' WITH FLANGE, 	FLOREA D.SIGN WWW.FLOREADSIGN.DE 	FLOREA D.SIGN WWW.FLOREADSIGN.DE 	P 	2012/12/04 	BM 	Oddy Test 	SILICON RUBBER, BLACK, SAMPLE DID NOT DRY (DESIGNED NOT TO) 	PREP/Drying time: N/A, test #7660 	SEAL 	none
FLUGGER, 	FLÜGGER 	UNKNOWN 	P 	2011/08/11 	BM 	Oddy Test 	, WHITE, GREY WITH BLUE SWIRLS 	PREP/Drying time: 2 WEEKS, test #7302 	MOULDING MATERIAL 	none
FOAM, FT-S170/30 	FOAM TECHNIQUES LTD (M) 	UNKNOWN 	P 	2012/01/20 	BM 	Oddy Test 	, GREY, 	PREP/Drying time: N/A, test #7374 	FOAM 	none
FOAM, FT-S180/30 UV 	FOAM TECHNIQUES LTD (M) 	UNKNOWN 	P 	2012/01/20 	BM 	Oddy Test 	, WHITE, 	PREP/Drying time: N/A, test #7373 	FOAM 	none
FOAM, FTS-HLB 	FOAM TECHNIQUES LTD (M) 	UNKNOWN 	F 	2012/01/20 	BM 	Oddy Test 	POLY URETHANE FOAM, GREY, 	PREP/Drying time: N/A, test #7384 	FOAM 	none
WESTBOND CARPET, N9733 	FORBO (M) 	UNKNOWN 	T 	2013/11/14 	BM 	Oddy Test 	POLYAMIDE PILE, RECYCLED VINYL BACKING, PURPLE, DARK, 	PREP/Drying time: N/A, test #8057 	FLOORING 	none
FORMICA, OCEAN GREY F7853 MAT 	FORMICA 	UNKNOWN 	P 	2013/04/18 	BM 	Oddy Test 	RESIN IMPREGNATED PAPER, GREY, 	PREP/Drying time: N/A, test #7788 	BOARD 	none
Fuji Xerox – 'Gold' 	Fuji Xerox Australia 	Fuji Xerox Australia 	PASS 	1999 	NAA 	PAT 	none 	none 	paper, copy 	n/a
Fuji Xerox – 'X' 	Fuji Xerox Australia 	Fuji Xerox Australia 	PASS 	1999 	NAA 	PAT 	none 	none 	paper, copy 	n/a
8mm double wall polycarbonate panel 	Gallina USA, LLC 	unknown 	Pass 	2009/12/09 	CMA 	Oddy Test 	Polycarbonate panel 	none 	board, corrugated 	none
Polycarbonate channel 	Gallina USA, LLC 	unknown 	Pass 	2009/12/09 	CMA 	Oddy Test 	Polycarbonate 	none 	board, channeled 	none
Garfilm EMCL (polyethylene terephthalate film) 	Garware Polyester 	Multapex 	PASS 	2006 	NAA 	PAT 	none 	none 	film, polyethylene terephtalate 	n/a
Garfilm EMSC PT077 	Garware Polyester 	Multapex 	PASS 	2006 	NAA 	PAT 	none 	none 	film, polyester 	n/a
CLICK NETHERFIELD EVOLUTION CASE SEAL, SEA 210 	GE BAYER SILICONES 	GE BAYER SILICONES 	P 	2013/02/01 	BM 	Oddy Test 	SILICONE SEAL, CLEAR, 	PREP/Drying time: N/A, test #7704 	SEAL 	none
SYLODYN, 	GETZNER 	GETZNER 	P 	2009/04/28 	BM 	Oddy Test 	POLYURETHANE FOAM, PURPLE, 	PREP/Drying time: N/A, test #6424 	FOAM 	none
SYLODYN, 	GETZNER 	GETZNER 	P 	2009/04/28 	BM 	Oddy Test 	POLYURETHANE FOAM, GREEN, 	PREP/Drying time: N/A, test #6425 	FOAM 	none
SYLODYN, 	GETZNER 	GETZNER 	P 	2009/04/28 	BM 	Oddy Test 	POLYURETHANE FOAM, PINK, 	PREP/Drying time: N/A, test #6426 	FOAM 	none
SYLOMER , 	GETZNER 	GETZNER 	P 	2009/04/28 	BM 	Oddy Test 	POLYURETHANE FOAM, BLACK, 	PREP/Drying time: N/A, test #6429 	FOAM 	none
SYLOMER HD, 	GETZNER 	GETZNER 	P 	2009/04/03 	BM 	Oddy Test 	POLYURETHANE FOAM, GREEN, DARK, 	PREP/Drying time: N/A, test #6354 	FOAM 	none
SYLOMER HD, 	GETZNER 	GETZNER 	P 	2009/04/03 	BM 	Oddy Test 	POLYURETHANE FOAM, GREEN, 	PREP/Drying time: N/A, test #6355 	FOAM 	none
SYLOMER HD, 	GETZNER 	GETZNER 	P 	2009/04/28 	BM 	Oddy Test 	POLYURETHANE FOAM, BLUE, LIGHT, 	PREP/Drying time: N/A, test #6423 	FOAM 	none
GEKO TAPE NANOPLAST, 7014-00 (3098) 140711-1G1 	GOTTLIEB BINDER GMBH 	GOTTLIEB BINDER GMBH 	P 	2012/10/02 	BM 	Oddy Test 	SILICON, CLEAR, 	PREP/Drying time: WASHED, test #7642 	FASTENER 	none
GRATNELLS LIDDED TRAY, NO F1T 	GRATNELLS 	GRATNELLS 	P 	2013/03/29 	BM 	Oddy Test 	POLYPROPYLENE, CLEAR, 	PREP/Drying time: N/A, test #7748 	CONTAINER 	none
ANTI - STATIC CLEANER, SCVA 	HAMMOND CHEMICALS LTD 	HAMMOND CHEMICALS LTD 	P 	2009/11/30 	BM 	Oddy Test 	, CLEAR, 	PREP/Drying time: SPRAYED ON, DRIED 24 HOURS, test #6690 	CLEANING 	none
HARLEQUIN HIGH SHINE FLOORING, 	HARLEQUIN 	HARLEQUIN 	T 	2010/05/28 	BM 	Oddy Test 	LAMINATED PVS WITH POLYETHELYNE TEREPHTHALATE SURFACE, BLACK, 	PREP/Drying time: BACK AND SIDES SEALED WITH AL TAPE, test #6813 	FLOORING 	none
MANNEQUIN, 6270-10-6273-10 	HINDSGUAL 	HINDSGUAL 	T 	2012/01/20 	BM 	Oddy Test 	PLASTIC AND PAINT, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7376 	MOUNT/ MOUNT MAKING 	none
HOMASOTE, 440 	HOMASOTE 	HOMASOTE 	F 	2009/01/20 	BM 	Oddy Test 	RECYCLED NEWSPAPER, BROWN, 	PREP/Drying time: N/A, test #6166 	BOARD 	none
INTECEL, 	INTEPLAST GROUP (m) 	UNKNOWN 	P 	2012/06/29 	BM 	Oddy Test 	EXTRUDED PVC FOAM BOARD, WHITE, 	PREP/Drying time: N/A, test #7580 	BOARD 	none
500 year Archival photocopy paper 	International Paper 	Jackaroo 	PASS 	2006 	NAA 	PAT 	watermarked,A4; 120 and 150 gsm 	none 	paper, copy 	n/a
Archival folder 	International Paper 	Jackaroo 	PASS 	2006 	NAA 	PAT 	(codes UFF701, UDW704, ULW705) 	none 	folder 	n/a
Hi-yield manila file folder board (white) 	International Paper 	Jackaroo 	PASS 	2006 	NAA 	PAT 	293 gsm(#180), 374 gsm (#180) 	none 	folder, file folder white 	n/a
Hi-yield manila file folder board(buff) 	International Paper 	Jackaroo 	PASS 	2006 	NAA 	PAT 	163gsm (#100), 202 gsm (#124), 293 gsm (#180), 374 gsm (#180) 	none 	board, file folder manila 	n/a
Manila (Buff) Filefolder 	InternationalPaper 	Jackaroo 	PASS 	2003 	NAA 	PAT 	179, 244,293, 285, 325, 375 gsm 	none 	folder, file 	n/a
White File folder 	InternationalPaper 	Jackaroo 	PASS 	2003 	NAA 	PAT 	179, 244,285, 325, 375 gsm 	none 	folder, file 	n/a
SNAP RIVET, SNR027-CLR 	JET PRESS 	JET PRESS 	P 	2010/12/07 	BM 	Oddy Test 	POLYCARBONATE, CLEAR, 	PREP/Drying time: N/A, test #7066 	FASTENER 	none
ARCHIVAL COVER PAPER, 300 GSM 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/12/12 	BM 	Oddy Test 	, GREY, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #8086 	PAPER 	none
ARCHIVE FOLDING BOX BOARD, BLUE GREY 1300 MICRON 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/12/12 	BM 	Oddy Test 	, GREY, 	PREP/Drying time: N/A, test #8083 	BOARD 	none
CANSON CONSERVATION BOARD, 6 PLY, 2400 MICRONS, ANTIQUE WHITE, CANA2X 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/05/09 	BM 	Oddy Test 	, CREAM, 	PREP/Drying time: N/A, test #7853 	BOARD 	none
CANSON CONSERVATION BOARD, 8 PLY, 3000 MICRONS, WHITE, CANW30 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/05/09 	BM 	Oddy Test 	, WHITE, 	PREP/Drying time: N/A, test #7854 	BOARD 	none
HERITAGE CONSERVATION BOARD, BUFFERED, 3 PLY, 1380 MICRONS, IVORY, HECIV2 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/05/09 	BM 	Oddy Test 	, CREAM, 	PREP/Drying time: N/A, test #7851 	BOARD 	none
HERITAGE CONSERVATION BOARD, BUFFERED, 3 PLY, 1380 MICRONS, WHITE, HECW2 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/05/09 	BM 	Oddy Test 	, WHITE, 	PREP/Drying time: N/A, test #7852 	BOARD 	none
HERITAGE MUSEUM BOARD, BUFFERED, 2200 MICRONS 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/05/09 	BM 	Oddy Test 	100% COTTON, WHITE, 	PREP/Drying time: N/A, test #7856 	BOARD 	none
HERITAGE MUSEUM BOARD, BUFFERED, 6 PLY, 2200 MICRONS, CREAM, HEMC5 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/05/09 	BM 	Oddy Test 	100% COTTON, CREAM, 	PREP/Drying time: N/A, test #7855 	BOARD 	none
HERITAGE WOOD-FREE PAPER, BOOK WHITE 160 GSM 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/12/12 	BM 	Oddy Test 	, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #8085 	PAPER 	none
MERIDIAN HIGH DENSITY BOARD, 2800 MICRON 	JOHN PURCELL PAPER 	JOHN PURCELL PAPER 	P 	2013/12/12 	BM 	Oddy Test 	, BROWN, LIGHT, 	PREP/Drying time: N/A, test #8084 	BOARD 	none
SUPERZOTE, EM26 	KEWELL VONVERTERS LTD. 	KEWELL VONVERTERS LTD. 	P 	2009/04/03 	BM 	Oddy Test 	FOAM, BLACK, 	PREP/Drying time: N/A, test #6353 	FOAM 	none
KILNER JAR SEAL, 	KILNER 	KILNER 	P 	2013/05/30 	BM 	Oddy Test 	RUBBER , ORANGE, TO BE APPLIED ON A LAYER OF PARALOID B72 	PREP/Drying time: N/A, test #7866 	SEAL 	none
Purple Nitrile gloves 	Kimberly-Clark 	Starnes 	fail 	2013/05/10 	CMA 	Oddy Test 	nitrile 	none 	barrier, glove 	
KOMACEL, 	KOMMERLING (M) 	UNKNOWN 	P 	2012/06/29 	BM 	Oddy Test 	EXTRUDED PVC FOAM BOARD, WHITE, 	PREP/Drying time: N/A, test #7579 	BOARD 	none
Le PARFAIT RUBBER SEALS KILNER JARS, 85MM 	Le Parfait 	UNKNOWN 	P 	2013/04/18 	BM 	Oddy Test 	RUBBER?, RED, 	PREP/Drying time: N/A, test #7789 	SEAL 	none
CLEAR SAV SELF ADHESIVE FILM, 	LEACH GRAPHICS/ AVERY DENNISON 	LEACH GRAPHICS/ AVERY DENNISON 	T 	2009/12/16 	BM 	Oddy Test 	VINYL AND PVC WITH ACRYLIC ADHESIVE, CLEAR, 	PREP/Drying time: STUCK TO ITSELF, test #6760 	FILM 	none
POLYFILLA, 	LePage Products 	UNKNOWN 	F 	2011/08/11 	BM 	Oddy Test 	, WHITE, 	PREP/Drying time: 2 WEEKS, test #7307 	MOULDING MATERIAL 	none
BRISTLE STRIP, 6.7 EC SS 	LISTA UK LTD 	LISTA UK LTD 	P 	2013/03/11 	BM 	Oddy Test 	BRISTLES, ADHESIVE AND SILICON GASKET, BROWN, 	PREP/Drying time: ADHESIVE STUCK TO MELINEX, test #7732 	SEAL 	none
RAM FOAM, LD33 	LISTA UK/ RAMPLAST LTD 	LISTA UK/ RAMPLAST LTD 	P 	2009/12/23 	BM 	Oddy Test 	POLYETHELENE, WHITE, 	PREP/Drying time: N/A, test #6749 	FOAM 	none
WEST FOAM BOARD, 	LONDON GRAPHICS 	LONDON GRAPHICS 	P 	2009/07/06 	BM 	Oddy Test 	POLYURETHANE AND PAPER, WHITE, 	PREP/Drying time: N/A, test #6546 	BOARD 	none
SOMERSET TEXTURED PAPER, RADIANT WHITE 225 G/M2 	LONDON GRAPHICS CENTRE? 	LONDON GRAPHICS CENTRE? 	P 	2014/01/16 	BM 	Oddy Test 	100% COTTON, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #8137 	PAPER 	none
CORROSION INTERCEPT FOIL, 	LUCENT TECHNOLOGIES 	LUCENT TECHNOLOGIES 	P 	2009/02/12 	BM 	Oddy Test 	POLYETHYLENE WITH COPPER, ORANGE, DARK, SAMPLE DID NOT DRY (DESIGNED NOT TO) 	PREP/Drying time: N/A, test #6200 	POLLUTION CONTROL 	none
PERSPEX COLOURS, OPAQUE, 4494, 5MM 	LUCITE INTERNATIONAL (M) 	UNKNOWN 	P 	2013/09/10 	BM 	Oddy Test 	ACRYLIC (POLYMETHYLMETHACRYLATE), RED, DARK, 	PREP/Drying time: N/A, test #8006 	BOARD 	none
PERSPEX COLOURS, OPAQUE, 744, 3MM 	LUCITE INTERNATIONAL (M) 	UNKNOWN 	T 	2013/09/10 	BM 	Oddy Test 	ACRYLIC (POLYMETHYLMETHACRYLATE), BLUE, DARK, 	PREP/Drying time: N/A, test #8005 	BOARD 	none
PERSPEX, 9T30 3MM 	LUCITE SOLUTIONS 	LUCITE SOLUTIONS 	P 	2013/07/08 	BM 	Oddy Test 	ACRYLIC, EXTRUDED , CLEAR, 	PREP/Drying time: N/A, test #7901 	BOARD 	none
METALLIC' CAST ACRYLIC SHEET, 4260 ANTIQUE GOLD 	MADREPERLA S.P.A. (M) 	UNKNOWN 	P 	2013/09/10 	BM 	Oddy Test 	ACRYLIC (POLYMETHYLMETHACRYLATE), GOLD, 	PREP/Drying time: N/A, test #8004 	BOARD 	none
MEADOWS & PASSMORE MAINSPRING GREASE, 0604 012015 	MEADOWS & PASSMORE (M) 	UNKNOWN 	P 	2013/12/12 	BM 	Oddy Test 	, CLEAR, BEIGE WITH RED SWIRLS 	PREP/Drying time: 1 WEEK, test #8078 	MISC 	none
BLUNDER PEST TRAP, 	MITIE 	MITIE 	P 	2013/02/25 	BM 	Oddy Test 	PAPER AND ADHESIVE, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7712 	PEST CONTROL 	none
MOEBIUS NATURAL GREASE, 8201 	MOEBIUS (M) 	UNKNOWN 	P 	2013/12/12 	BM 	Oddy Test 	MINERAL OILS, VASELINE GREASE, NEATSFOOT OIL, MOLYBDANE DISULPHIDE, BLACK, 	PREP/Drying time: 1 WEEK, test #8076 	MISC 	none
MOEBIUS NATURAL GREASE, 8301 	MOEBIUS (M) 	UNKNOWN 	P 	2013/12/12 	BM 	Oddy Test 	MINERAL OILS, VASELINE GREASE, NEATSFOOT OIL, MOLYBDANE DISULPHIDE, BLACK, 	PREP/Drying time: 1 WEEK, test #8077 	MISC 	none
MUSION EYLINER FOIL, 	MUSION EVENTS LIMITED 	MUSION EVENTS LIMITED 	P 	2010/03/01 	BM 	Oddy Test 	, CLEAR, 	PREP/Drying time: N/A, test #6775 	FILM 	none
WINDOW FILM, C-171 	NAKAGAWA CHEM. LTD. 	NAKAGAWA CHEM. LTD. 	F 	2011/01/18 	BM 	Oddy Test 	, CLEAR, 	PREP/Drying time: N/A, test #7112 	FILM 	none
WINDOW FILM, C-181 	NAKAGAWA CHEM. LTD. 	NAKAGAWA CHEM. LTD. 	F 	2011/01/18 	BM 	Oddy Test 	, CLEAR, North American version of Forex Classic board 	PREP/Drying time: N/A, test #7113 	FILM 	none
WALLPAPER, SC622 	NiP CORPORATION 	NiP CORPORATION 	P 	2011/01/18 	BM 	Oddy Test 	CELLULOSE, GREY, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7115 	PAPER 	none
WALLPAPER, SC626 	NiP CORPORATION 	NiP CORPORATION 	P 	2011/01/18 	BM 	Oddy Test 	CELLULOSE, BLACK, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7114 	PAPER 	none
WALLPAPER, SC665 	NiP CORPORATION 	NiP CORPORATION 	P 	2011/01/18 	BM 	Oddy Test 	CELLULOSE, BLUE, LIGHT, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7116 	PAPER 	none
Nomapack Foam 	NMC 	Britestar 	PASS 	2012 	NAA 	PAT 	grey, blue (PAD Profile), bright yellow (WS ee*264 Edge Pad) 	none 	foam 	n/a
Walnut 	none 	Frame supplier 	Fail 	2012/01/10 	CMA 	Oddy Test 	wood 	none 	wood 	none
Walnut wood 	none 	Frame supplier 	fail 	2012/01/10 	CMA 	Oddy Test 	wood 	for comparison to coated Walnut 	wood 	none
Silicone Novabond 2, S29306000 	Novabond 	Unknown 	Fail (on Pb) 	2009/01/20 	BM 	Oddy 	black silicone sealant 	2 part silicone 	sealant, caulk or adhesive 	n/a
Nu-Alum 	Nudo 	unknown 	Fail 	2011/07/07 	CMA 	Oddy Test 	.13" aluminum bonded to plywood substrate 	barrier to cover wood products or as alternative to wood 	barrier, structural 	none
Nu-Alum (with fabric covering) 	Nudo 	unknown 	Fail 	2011/07/07 	CMA 	Oddy Test 	.13" aluminum bonded to plywood substrate 	barrier to cover wood products or as alternative to wood 	barrier, structural 	none
Obomodulan Tooling Board 500 Magma 	OBO-Werke GmbH & Co. 	McCausey Lumber 	Pass 	2011/01/20 	CMA 	Oddy Test 	Polyurethane, medium density/pink 	alternative to wood for risers/blocks, backboards and decks 	board, wood alternative 	none
OFREXS OHP PERMANENT PEN, 	OFREXS 	OFREXS 	P 	2010/04/09 	BM 	Oddy Test 	, RED, 	PREP/Drying time: 2 HOURS, SUBSTRATE FULLY COVERED, test #6800 	MISC 	none
CRIOS BAG, 	ORLA SOLUTIONS 	ORLA SOLUTIONS 	P 	2009/07/06 	BM 	Oddy Test 	COPPER IMPREGNATED POLYMER, CLEAR, TO BE APPLIED ON A LAYER OF PARALOID B72 	PREP/Drying time: N/A, test #6544 	POLLUTION CONTROL 	none
CRIOS FOAM, 	ORLA SOLUTIONS 	ORLA SOLUTIONS 	P 	2010/02/11 	BM 	Oddy Test 	COPPER IMPREGNATED POLYMER, PURPLE, DARK, SAMPLE DID NOT DRY (DESIGNED NOT TO) 	PREP/Drying time: N/A, test #6766 	POLLUTION CONTROL 	none
PALIGHT, ST-10 	PALRAM (S)(M) 	PALRAM (S)(M) 	P 	2014/04/04 	BM 	Oddy Test 	FOAMED PVC SHEET, WHITE, 	PREP/Drying time: N/A, test #8179 	BOARD 	none
Clear LDPE continuous roll 	Pinpak–Grayson Packaging 	Pinpak–Grayson Packaging 	PASS 	2007 	NAA 	PAT 	50 mm wide x 100 micron thick 	none 	film, Low Density Polyethylene 	n/a
Plascoat VitroGuard 12 	Plascoat Corp 	Plascoat Corp 	Pass 	2011/01/11 	CMA 	Oddy Test 	modified polyolefins 	barrier coating for brass mounts 	barrier/padding 	none
MODOSTUC, INTERIOR 	Plasveroi International 	UNKNOWN 	F 	2011/08/11 	BM 	Oddy Test 	, WHITE, 	PREP/Drying time: 2 WEEKS, test #7306 	MOULDING MATERIAL 	none
POLYFLEX PLUS PU, 7350 LAKELAND BLUE 	POLYFLOR 	POLYFLOR 	T 	2012/01/20 	BM 	Oddy Test 	PVC WITH POLYURETHANE COATING, BLUE, 	PREP/Drying time: N/A, test #7383 	FLOORING 	none
POLYFLOR 2000 PUR, 8500 LACE BLUE 	POLYFLOR LTD (M) 	U 	P 	2013/08/27 	BM 	Oddy Test 	POLYURETHANE, GREY, LIGHT, 	PREP/Drying time: N/A, test #7922 	FLOORING 	none
POLYFLOR 2000 PUR, 8650 WILD LILAC 	POLYFLOR LTD (M) 	U 	P 	2013/08/27 	BM 	Oddy Test 	POLYURETHANE, BLUE, LIGHT, 	PREP/Drying time: N/A, test #7923 	FLOORING 	none
POLYFLOR 2000 PUR, 8850 BUCKWHEAT 	POLYFLOR LTD (M) 	U 	P 	2013/08/27 	BM 	Oddy Test 	POLYURETHANE, BEIGE, 	PREP/Drying time: N/A, test #7924 	FLOORING 	none
POLYFLOR 2000 PUR, 8150 SHADOW 	POLYFLOR LTD (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	POLYURETHANE, GREY, DARK, 	PREP/Drying time: N/A, test #7920 	FLOORING 	none
POLYFLOR 2000 PUR, 8300 OAK 	POLYFLOR LTD (M) 	UNKNOWN 	T 	2013/08/27 	BM 	Oddy Test 	POLYURETHANE, BEIGE, 	PREP/Drying time: N/A, test #7921 	FLOORING 	none
PORTEX TUBING, 800/100/260 	PORTEX (M) 	CONSUMABLES.COM (S) 	P 	2013/11/28 	BM 	Oddy Test 	POLYETHYLENE, CLEAR, 	PREP/Drying time: N/A, test #8073 	SLEEVING/ TUBING 	none
POSA SR-70/T, SR-70/T 	POSA SpA 	POSA SpA 	P 	2012/09/08 	BM 	Oddy Test 	SILICONE RUBBER, BLACK, 	PREP/Drying time: N/A, test #7602 	SEAL 	none
POSA SR-70/T, SR-70T 	POSA SpA 	POSA SpA 	P 	2012/10/28 	BM 	Oddy Test 	SILICONE RUBBER, CLEAR, 	PREP/Drying time: N/A, test #7646 	SEAL 	none
Cellair (closed cell foam) 	Precision Foam Manufacturing 	Metro Foam Products 	PASS 	1996 	NAA 	PAT 	none 	none 	foam, closed cell 	n/a
ARCHIVAL CLOTH TAPE, 	PRESERVATION EQUIPMENT LTD 	PRESERVATION EQUIPMENT LTD 	T 	2010/04/09 	BM 	Oddy Test 	COTTON, BEIGE, 	PREP/Drying time: N/A, test #6804 	FASTENER 	none
ALU-KRAFT PAPER BARRIER, 70545 20 	PURE NATURE 	PURE NATURE 	T 	2009/02/09 	BM 	Oddy Test 	ALUMINIUM FOIL WITH PAPER BACKING, SILVER, 	PREP/Drying time: N/A, test #6277 	BARRIER 	none
PURE ALUMINIUM BARRIER FOIL, 70542 20 	PURE NATURE 	PURE NATURE 	P 	2009/02/09 	BM 	Oddy Test 	ALUMINIUM, SILVER, 	PREP/Drying time: N/A, test #6278 	BARRIER 	none
Foam core board 	Quill Stationery Manufacturers 	Quill Stationery Manufacturers 	PASS 	2006 	NAA 	PAT 	5 mm Gold OW (J) 	none 	board, foam core 	n/a
Mohawk digital paper 	RaleighPaper 	Rolls FilingSystem 	PASS 	2005 	NAA 	PAT 	none 	none 	paper 	n/a
REALLY USEFUL BOX - 1.6 LITRE, 1.6 LITRE 	REALLY USEFUL BOX UK 	REALLY USEFUL BOX UK 	P 	2013/03/29 	BM 	Oddy Test 	POLYPROPYLENE, CLEAR, 	PREP/Drying time: N/A, test #7747 	CONTAINER 	none
REALLY USEFUL BOX - 9 LITRE, MODEL NO.287048 	REALLY USEFUL BOX UK 	REALLY USEFUL BOX UK 	P 	2013/03/29 	BM 	Oddy Test 	POLYPROPYLENE, CLEAR, 	PREP/Drying time: N/A, test #7746 	CONTAINER 	none
POLYESTER BONING, 4224 	RIGILENE 	RIGILENE 	F 	2009/01/22 	BM 	Oddy Test 	POLYESTER, BLACK, 	PREP/Drying time: N/A, test #6138 	MOUNT/ MOUNT MAKING 	none
POLYESTER BONING, 4224 	RIGILENE 	RIGILENE 	F 	2009/01/22 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #6139 	MOUNT/ MOUNT MAKING 	none
FOAMALUX ULTRA FOAM, GSM:2100 MIC:3000 	ROBERT HORNE GROUP 	ROBERT HORNE GROUP 	P 	2013/06/26 	BM 	Oddy Test 	PVC, PE FOAM, BLACK, 	PREP/Drying time: N/A, test #7892 	FOAM 	none
SKYBOND COMPOSITE ACM BOARD, JH-9185 	ROBERT HORNE GROUP 	ROBERT HORNE GROUP 	T 	2013/06/26 	BM 	Oddy Test 	COATED AL SKIN WITH PLASTIC CORE, BLACK, 	PREP/Drying time: N/A, test #7888 	BOARD 	none
FLOWCRETE FLOWFRESH SL ANTI SLIP, RAL 7012 REF A8447 	RPM FLOWCRETE 	RPM FLOWCRETE 	P 	2012/11/02 	BM 	Oddy Test 	SUPER PU ANTI SLIP (SILICA) FLOORING WITH PRIMER AND SELF SMOOTHING BASE LAYER, GREY, 	PREP/Drying time: EDGES SEALED WITH ALUMINIUM TAPE, test #7648 	FLOORING 	none
Lexan polycarbonate Film 	SABIC Innovative Plastics 	Mulford Plastics 	PASS 	1996 	NAA 	PAT 	none 	none 	film, polycarbonate 	n/a
SHATTERPROOF FILM, CLM-2HC-R 	SANSHO LTD. 	SANSHO LTD. 	F 	2011/01/18 	BM 	Oddy Test 	, CLEAR, 	PREP/Drying time: N/A, test #7111 	FILM 	none
POLYFELT PADDING, T500 TSL 	SEVERNSIDE FABRICS 	SEVERNSIDE FABRICS 	T 	2009/01/22 	BM 	Oddy Test 	POLYFELT, WHITE, 	PREP/Drying time: N/A, test #6141 	PADDING 	none
POLYFELT PADDING, T600 TSL 	SEVERNSIDE FABRICS 	SEVERNSIDE FABRICS 	T 	2009/01/22 	BM 	Oddy Test 	POLYFELT, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #6142 	PADDING 	none
POLYFELT PADDING, T700 TSL 	SEVERNSIDE FABRICS 	SEVERNSIDE FABRICS 	T 	2009/01/22 	BM 	Oddy Test 	POLYFELT, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #6143 	PADDING 	none
POLYFELT PADDING, T900 TSL 	SEVERNSIDE FABRICS 	SEVERNSIDE FABRICS 	T 	2009/01/22 	BM 	Oddy Test 	POLYFELT, WHITE, 	PREP/Drying time: N/A, test #6144 	PADDING 	none
COTTON KNIT PAD, C/1180/KCP 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	T 	2012/03/30 	BM 	Oddy Test 	COTTON, CREAM, 	PREP/Drying time: N/A, test #7474 	PADDING 	none
POLYFELT, NT/1200/TXL 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7476 	PADDING 	none
POLYFELT, T/4000/T51 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #7475 	PADDING 	none
POLYFELT, T/500/TCL 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7480 	PADDING 	none
POLYFELT, T/600/TCL 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7479 	PADDING 	none
POLYFELT, T/700/TCL 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, 	PREP/Drying time: N/A, test #7478 	PADDING 	none
POLYFELT, T/900/TCL 	SEVERNSIDE FABRID LTD 	SEVERNSIDE FABRID LTD 	P 	2012/03/30 	BM 	Oddy Test 	POLYESTER, WHITE, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #7477 	PADDING 	none
FLAME RETARDANT CUSHION WRAP, 	SFSL (M) 	CONSERVATION RESOURCES (S) 	P 	2013/01/18 	BM 	Oddy Test 	, WHITE, 	PREP/Drying time: N/A, test #7677 	PADDING 	none
Archival liner board, blue/grey 	Shoalhaven Mill 	Australian Paper 	PASS 	2009 	NAA 	PAT 	blue/grey 	none 	board 	n/a
Archival liner board 	Shoalhaven Paper Mills 	AustralianPaper 	PASS 	2009 	NAA 	PAT 	none 	none 	board 	n/a
DIM OUT 7000 RANGE BLIND, 41 	SILENT GLISS (M) 	CONISTON (S) 	P 	2011/08/16 	BM 	Oddy Test 	PES, FLOCKED, GREY, 	PREP/Drying time: N/A, test #7314 	ENVIRONMENTAL CONTROL 	none
MIDNIGHT RANGE BLIND, 608 	SILENT GLISS (M) 	CONISTON (S) 	F 	2011/08/16 	BM 	Oddy Test 	GLASS FIBRE COATED AND FLOCKED, GREY, 	PREP/Drying time: N/A, test #7313 	ENVIRONMENTAL CONTROL 	none
SUPER CLEAR SHEET 0.8MM, 	SILEX 	SILEX 	F 	2010/03/26 	BM 	Oddy Test 	SILICONE, CLEAR, 	PREP/Drying time: N/A, test #6788 	FILM 	none
SUPER CLEAR SHEET 0.8MM, 	SILEX 	SILEX 	P 	2010/05/28 	BM 	Oddy Test 	SILICONE, WHITE, 	PREP/Drying time: N/A, test #6824 	FILM 	none
Sintra 	SINTRA 	SINTRA 	P 	2012/09/21 	BM 	Oddy Test 	PVC, WHITE, 	PREP/Drying time: N/A, test #7621 	BOARD 	none
SIROFLEX TRADE STRENGTH GLASS CELANER, SX GLASS CLEANER 	SIROFLEX (M) 	UNKNOWN 	P 	2013/02/25 	BM 	Oddy Test 	PROPANOL AND BUTOXYETHANOL, BLUE, 	PREP/Drying time: BUFFED TO REMOVE RESIDUE, test #7708 	CLEANING 	none
SORBOTHANE, 30 DURO 0204050-30-10 	SORBOTHANE INC (M) 	UNKNOWN 	T 	2013/04/18 	BM 	Oddy Test 	POLUYURATHANE, BLACK, 	PREP/Drying time: N/A, test #7774 	ANTISLIP/ ANTIVIBRATION 	none
SORBOTHANE, 50 DURO 0204062-50-10 	SORBOTHANE INC (M) 	UNKNOWN 	P 	2013/04/18 	BM 	Oddy Test 	POLUYURATHANE, BLACK, 	PREP/Drying time: N/A, test #7775 	ANTISLIP/ ANTIVIBRATION 	none
SORBOTHANE, 70 DURO 0204050-70-10 	SORBOTHANE INC (M) 	UNKNOWN 	T 	2013/04/18 	BM 	Oddy Test 	POLUYURATHANE, BLACK, 	PREP/Drying time: N/A, test #7776 	ANTISLIP/ ANTIVIBRATION 	none
LUMICOLOUR PERMANENT 'S', ART. NO.: 313-9, EAN 4007817 308820 	STAEDTLER 	STAEDTLER 	P 	2011/08/11 	BM 	Oddy Test 	, BLACK, TOP LAYER FOR MASTERTOP 1324 STILL SMELLED AFTER 4 WEEKS 	PREP/Drying time: 2 HOURS, FULLY COLOURED SUBSTRATE, test #7311 	MISC 	none
LUMICOLOUR SPECIAL 'F', ART. NO.: 319 f-9, EAN 4007817 319079 	STAEDTLER 	STAEDTLER 	F 	2011/08/11 	BM 	Oddy Test 	, BLACK, 	PREP/Drying time: 2 HOURS, FULLY COLOURED SUBSTRATE, test #7312 	MISC 	none
PLASTIC BOX (WITH TOP), 6147008 	STEWART 	STEWART 	P 	2009/02/09 	BM 	Oddy Test 	POLYSTYRENE, CLEAR, 	PREP/Drying time: N/A, test #6281 	CONTAINER 	none
STOP G-P, 	STOPGAP 	STOPGAP 	P 	2009/03/20 	BM 	Oddy Test 	POLYCARBONATE WITH PLASTISIZERS , CLEAR, 	PREP/Drying time: N/A, test #6328 	SEAL 	none
SUGRU, F.03 	SUGRU, FORMFORMFORM (M) 	UNKNOWN 	T 	2011/02/17 	BM 	Oddy Test 	SILICONE, RED, 	PREP/Drying time: 48 HOURS, test #7137 	MOULDING MATERIAL 	none
DECORATIVE FILM, PS-948 	SUMITOMO 	SUMITOMO 	P 	2011/01/18 	BM 	Oddy Test 	PVC, CLEAR, 	PREP/Drying time: N/A, test #7127 	FILM 	none
DEPRON, 	TECHNISCHES MERBLATT - GLUTOLIN 	TECHNISCHES MERBLATT - GLUTOLIN 	P 	2009/01/20 	BM 	Oddy Test 	POLYSTYRENE, WHITE, 	PREP/Drying time: N/A, test #6171 	FOAM 	none
GEL PAC MEMBRANE BOX (OUTER CASE), MB-15OT/100 	TELTEC 	TELTEC 	P 	2013/02/01 	BM 	Oddy Test 	, CLEAR, 	PREP/Drying time: N/A, test #7702 	CONTAINER 	none
GELPACK MEMBRANE BOX (MEMBRANE), MB-15OT/101 	TELTEC 	TELTEC 	P 	2013/02/01 	BM 	Oddy Test 	, CLEAR, 	PREP/Drying time: N/A, test #7703 	CONTAINER 	none
LEXAN, 10MM 	THE PLASTIC SHOP 	THE PLASTIC SHOP 	T 	2012/01/20 	BM 	Oddy Test 	POLYCARBONATE SHEET, WHITE, 	PREP/Drying time: N/A, test #7370 	BOARD 	none
LEXAN, 5MM 	THE PLASTIC SHOP 	THE PLASTIC SHOP 	T 	2012/01/20 	BM 	Oddy Test 	POLYCARBONATE SHEET, CLEAR, 	PREP/Drying time: N/A, test #7371 	BOARD 	none
ANTIQUE RANGE THICKNESS 2800, 64858 	TIMECASE (M) 	CXD (S) 	P 	2014/03/12 	BM 	Oddy Test 	MOUNTBOARD, BLACK, 	PREP/Drying time: N/A, test #8160 	BOARD 	none
Film canister 	Tuscan Industries 	Tuscan Industries 	PASS 	1997 	NAA 	PAT 	(blue) fire retardant 	none 	film canister 	n/a
Film canister 	Tuscan Industries 	Tuscan Industries 	PASS 	1997 	NAA 	PAT 	polypropylene (grey):MB 91603A, MB 91603B, MB 91603C, MB 91603D, MB 91603E, MB 91603F 	none 	film canister 	n/a
Polypropylene film canister, round 	Tuscan Industries 	Tuscan Industries 	PASS 	1996 	NAA 	PAT 	polypropylene, (grey, blue) 	none 	film canister 	n/a
Polypropylene film canister, square 	Tuscan Industries 	Tuscan Industries 	PASS 	1996 	NAA 	PAT 	polypropylene (blue) 	none 	film canister 	n/a
SYSTEM BOXES, 	ULTRAPLAST-HOFSTATTER & EBBESEN A/S 	ULTRAPLAST-HOFSTATTER & EBBESEN A/S 	P 	2009/02/12 	BM 	Oddy Test 	POLYSTYRENE, CLEAR, needs label 	PREP/Drying time: N/A, test #6198 	CONTAINER 	none
PERSPEX, 1.5MM 	UNKNOWN 	AMARI PLASTICS (S) 	P 	2011/08/11 	BM 	Oddy Test 	ACRYLIC, EXTRUDED , CLEAR, 	PREP/Drying time: N/A, test #7310 	BOARD 	none
CORROSION INTERCEPT COIN BAG, 	UNKNOWN 	CONSERVATION BY DESIGN (S) 	P 	2009/01/20 	BM 	Oddy Test 	POLYMER FILM WITH COPPER , ORANGE, DARK, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #6159 	POLLUTION CONTROL 	none
CORROSION INTERCEPT FOAM, 	UNKNOWN 	CONSERVATION BY DESIGN (S) 	P 	2009/01/20 	BM 	Oddy Test 	POLYMER FOAM WITH COPPER PARTICLES, ORANGE, DARK, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #6160 	POLLUTION CONTROL 	none
JAC SERIALASS SELF ADHESIVE VINYL SHEET, 7000D 	UNKNOWN 	DISPLAY WAYS (S) 	P 	2014/02/12 	BM 	Oddy Test 	VINYL ADHESIVE, CLEAR, WHITE LINING 	PREP/Drying time: STUCK TO ITSELF, test #8148 	FILM 	none
MACAL GLASS DÉCOR, 798-01 	UNKNOWN 	DISPLAY WAYS (S) 	T 	2014/02/12 	BM 	Oddy Test 	VINYL WITH ADHESIVE, GREY, LIGHT, WHITE LINING 	PREP/Drying time: STUCK TO ITSELF, test #8147 	FILM 	none
METAMARK SIGN VINYL 4 SERIES, M4-OF FROST 	UNKNOWN 	DISPLAY WAYS (S) 	P 	2014/02/12 	BM 	Oddy Test 	VINYL WITH ADHESIVE, CLEAR, WHITE LINING 	PREP/Drying time: STUCK TO ITSELF, test #8149 	FILM 	none
RITRAMA - PICS SUPREME SERIES SELF ADHESIVE VINYL SHEET, CAST SILVER 	UNKNOWN 	DISPLAY WAYS (S) 	T 	2014/02/12 	BM 	Oddy Test 	VINYL ADHESIVE, GREY, LIGHT, WHITE LINING 	PREP/Drying time: STUCK TO ITSELF, test #8146 	FILM 	none
CORREX BOARD, 	UNKNOWN 	EUROPOINT DISPLAY (S) 	P 	2009/12/23 	BM 	Oddy Test 	POLYPROPYLENE, WHITE, 	PREP/Drying time: N/A, test #6742 	BOARD 	none
EXCEL FREE FOAM (FF), 	UNKNOWN 	HOLBOURNE INDUSTRIAL PLASTICS LTD (S) 	T 	2013/01/18 	BM 	Oddy Test 	PVC FOAM BOARD, WHITE, 	PREP/Drying time: N/A, test #7678 	BOARD 	none
EXCEL INTEGRAL FOAM (IF), 	UNKNOWN 	HOLBOURNE INDUSTRIAL PLASTICS LTD (S) 	P 	2013/01/18 	BM 	Oddy Test 	PVC FOAM BOARD, WHITE, 	PREP/Drying time: N/A, test #7679 	BOARD 	none
CORRUGATED BOARD, BC, 0314107, 6.4 MM LIGHT GREY /NATURAL WHITE 	UNKNOWN 	KLUG (S) 	P 	2013/11/28 	BM 	Oddy Test 	CALCIUM CARBONATE BUFFERED BOARD, GREY, LIGHT, 	PREP/Drying time: N/A, test #8068 	BOARD 	none
CORRUGATED BOARD, QUALITY 021, E FLUTE, 02110X, 1.6 MM, 560 G/M2, LIGHT GREY/ NATURAL WHITE 	UNKNOWN 	KLUG (S) 	P 	2013/11/28 	BM 	Oddy Test 	CALCIUM CARBONATE BUFFERED BOARD, GREY, LIGHT, 	PREP/Drying time: N/A, test #8070 	BOARD 	none
CORRUGATED BOARD, QUALITY 021, E FLUTE, 021147, 1.7 MM, 680 G/M2, GREY BLUE/ WHITE 	UNKNOWN 	KLUG (S) 	P 	2013/11/28 	BM 	Oddy Test 	100% BLEACHED CELLULOSE, GREY, DARK, 	PREP/Drying time: N/A, test #8067 	BOARD 	none
CORRUGATED BOARD, QUALITY 031, B FLUTE, 03110X, 3 MM, 570 G/M2, LIGHT GREY/ NATURAL WHITE 	UNKNOWN 	KLUG (S) 	P 	2013/11/28 	BM 	Oddy Test 	CALCIUM CARBONATE BUFFERED BOARD, GREY, LIGHT, 	PREP/Drying time: N/A, test #8069 	BOARD 	none
CORRUGATED BOARD, QUALITY 031, B FLUTE, 03147107, 3.1 MM, 680 G/M2, GREY BLUE/ NATURAL WHITE 	UNKNOWN 	KLUG (S) 	P 	2013/11/28 	BM 	Oddy Test 	CALCIUM CARBONATE BUFFERED BOARD, GREY, DARK, 	PREP/Drying time: N/A, test #8071 	BOARD 	none
VINYL-MACAL SHEETING, 	UNKNOWN 	MACTAC/BAF GRAPHICS (S) 	P 	2010/06/08 	BM 	Oddy Test 	VINYL WITH ACRYLIC ADHESIVE, WHITE, 	PREP/Drying time: N/A, test #6845 	FILM 	none
VINYL-MACAL SHEETING, 	UNKNOWN 	MACTAC/BAF GRAPHICS (S) 	P 	2010/06/08 	BM 	Oddy Test 	VINYL WITH ACRYLIC ADHESIVE, GREY, 	PREP/Drying time: N/A, test #6846 	FILM 	none
VINYL-MACAL SHEETING, 	UNKNOWN 	MACTAC/BAF GRAPHICS (S) 	P 	2010/06/08 	BM 	Oddy Test 	VINYL WITH ACRYLIC ADHESIVE, CREAM, 	PREP/Drying time: N/A, test #6847 	FILM 	none
VINYL-MACAL SHEETING, 	UNKNOWN 	MACTAC/BAF GRAPHICS (S) 	P 	2010/06/08 	BM 	Oddy Test 	VINYL WITH ACRYLIC ADHESIVE, SILVER, 	PREP/Drying time: N/A, test #6848 	FILM 	none
VINYL-MACAL SHEETING, 	UNKNOWN 	MACTAC/BAF GRAPHICS (S) 	F 	2010/06/08 	BM 	Oddy Test 	VINYL WITH ACRYLIC ADHESIVE, BLACK, 	PREP/Drying time: N/A, test #6849 	FILM 	none
FOAM , F104 	UNKNOWN 	PENTONVILLE LTD. (S) 	P 	2011/01/18 	BM 	Oddy Test 	POLYURETHANE, GREY, 	PREP/Drying time: N/A, test #7107 	FOAM 	none
VANGUARD CARD, Vanguard, celestial blue, 380mic 	UNKNOWN 	SS GRAPHICS/ELLIOT BAXTER (S) 	P 	2010/10/01 	BM 	Oddy Test 	CELLULOSE, BLUE, LIGHT, LIGHTWEIGHT SAMPLE 	PREP/Drying time: N/A, test #6993 	PAPER 	none
CELLITE PANEL, 840 	UNKNOWN 	UNKNOWN 	F 	2013/11/28 	BM 	Oddy Test 	HONEYCOMB PANEL WITH PHENOLIC SKIN, BEIGE, 	PREP/Drying time: EDGES TAPED WITH AL FOIL, test #8074 	BOARD 	none
CELLITE PANEL, 920 	UNKNOWN 	UNKNOWN 	P 	2013/11/28 	BM 	Oddy Test 	NOMEX HONEYCOMB PANEL WITH CARBON SKIN, BLACK, 	PREP/Drying time: EDGES TAPED WITH AL FOIL, test #8075 	BOARD 	none
CONTRACT 2600 SERIES BLACKOUT BLIND, 2603 LIGHT GREY 	UNKNOWN 	UNKNOWN 	T 	2013/11/14 	BM 	Oddy Test 	100% POLYESTER, GREY, LIGHT, 	PREP/Drying time: N/A, test #8058 	ENVIRONMENTAL CONTROL 	none
Dry mount photo album 	unknown 	Abbey Plastics Products 	PASS 	2004 	NAA 	PAT 	none 	black page and interleaf 	page, photo album 	n/a
Semi-rigid polypropylene 	unknown 	Abbey Plastics Products 	PASS 	2003 	NAA 	PAT 	none 	none 	sheet, polypropylene 	n/a
Photo corners 	unknown 	Albox Australia 	PASS 	2004 	NAA 	PAT 	250, LERO 81/03 	none 	photo corners 	n/a
Paperboard inserts 	unknown 	Albox Australia 	PASS 	2003 	NAA 	PAT 	cream, black, white 	none 	board 	n/a
Paperboard inserts 	unknown 	Albox Australia 	PASS 	2003 	NAA 	PAT 	cream, black, white 	none 	board 	n/a
Archival corrugated (blue/grey) board 	unknown 	Archival Survival 	PASS 	2006 	NAA 	PAT 	single and double wall 	none 	board, corrugated 	n/a
Archival Corrugated Board, blue/grey, double wall 	unknown 	Archival Survival Pty Ltd 	PASS 	2012 	NAA 	PAT 	(code BRDMUB) 	none 	board, corrugated archival 	n/a
Archival Corrugated Board, blue/grey, single wall 	unknown 	Archival Survival Pty Ltd 	PASS 	2012 	NAA 	PAT 	(code BRDMUB) 	none 	board, corrugated archival 	n/a
Archival folder board (white) 	unknown 	Archival Survival 	PASS 	2006 	NAA 	PAT 	320 gsm 	none 	board, folder 	n/a
Archival folder 	unknown 	Archival Survival Pty Ltd 	PASS 	2012 	NAA 	PAT 	260 and 320 gsm, (code FLDMAN) 	none 	folder, archival 	n/a
Buffered Seamless Envelope 	unknown 	Archival Survival Pty Ltd 	PASS 	2012 	NAA 	PAT 	90 gsm 	none 	envelope, buffered seamless 	n/a
Buffered seamless envelope 	unknown 	Archival Survival 	PASS 	2006 	NAA 	PAT 	90 gsm (code ENCSEAM 85X110) 	none 	envelope, buffered seamless 	n/a
Green grey library board 	unknown 	Archival Survival 	PASS 	2006 	NAA 	PAT 	240 gsm (10 point) 	none 	board, library 	n/a
Green grey library board 	unknown 	Archival Survival 	PASS 	2006 	NAA 	PAT 	490 gsm (20 point) 	none 	board, library 	n/a
Library Board 	unknown 	Archival Survival Pty Ltd 	PASS 	2012 	NAA 	PAT 	240 and 490 gsm, (code BRDLIB) 	none 	board, library 	n/a
Perpetuum Wove paper, 120 gsm 	unknown 	Archival Survival Pty Ltd 	PASS 	2012 	NAA 	PAT 	120 gsm 	none 	paper, wove 	n/a
Perpetuum Wove 	unknown 	Archival Survival 	PASS 	2003 	NAA 	PAT 	90 gsm (code PAPA4-90) 	none 	paper 	n/a
Perpetuum Wove 	unknown 	Archival Survival 	PASS 	2006 	NAA 	PAT 	90 gsm (code PAPA4-90) 	none 	paper 	n/a
Ever Fast file pin holder 	unknown 	Avery Dennison Office Products 	PASS 	2004 	NAA 	PAT 	Code 81996 	none 	holder 	n/a
Cellaire, polyethylene foam cushioning material 	unknown 	Bunzl/Sealed Air Australia 	PASS 	2006 	NAA 	PAT 	2 mm thick (Code RH0210), 6 mm thick (Code RH06D) 	none 	foam, polyethylene 	n/a
Sintra 	unknown 	Byrne Sign in Cleveland 	Pass 	2012/09/26 	CMA 	Oddy test 	3/4" white Expanded PVC Board 	on coupons spotty iridescent areas overall, concentrated at edges 	wood alternative 	n/a
Archive Text 	unknown 	Conservation Resources 	PASS 	1996 	NAA 	PAT 	none 	none 	paper, copy 	n/a
ProLong 500 year archival document wallet (white) 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	270gsm 	none 	envelope, buffered 	n/a
ProLong 500 year archival document wallet (white) 	unknown 	Conservation Resources 	PASS 	2006 	NAA 	PAT 	270gsm 	none 	envelope, buffered 	n/a
ProLong 500 year archival folder (white) 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	270gsm 	none 	envelope, buffered 	n/a
ProLong 500 year archival folder (white) 	unknown 	Conservation Resources 	PASS 	2006 	NAA 	PAT 	270gsm 	none 	envelope, buffered 	
ProLong 500 year archival folder board(white) 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	white,270 gsm 	none 	board, folder 	n/a
ProLong 500 year archival folder board(white) 	unknown 	Conservation Resources 	PASS 	2006 	NAA 	PAT 	white,270 gsm 	none 	board, folder 	n/a
ProLong 500 year archival corrugated(blue/grey) board 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	single and double wall 	none 	board, corrugated 	n/a
ProLong 500 year archival folder board 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	270gsm 	none 	board, folder 	n/a
ProLong 500 year archival, four flap folder 	unknown 	Conservation Resources 	PASS 	2006 	NAA 	PAT 	270gsm; retest 	none 	folder, four flap, 15 mm expansion 	n/a
ProLong 500 year watermarked archival laser/copy paper 	unknown 	Conservation Resources 	PASS 	2001 	NAA 	PAT 	watermarked archival 	none 	paper, copy/laser 	n/a
ProLong 500 year watermarked archival laser/copy paper 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	watermarked,archival, 80 gsm 	none 	paper, copy/laser 	n/a
ProLong 500 year archival envelope 	unknown 	Conservation Resources 	PASS 	2003 	NAA 	PAT 	watermarked, 80gsm, buffered, ungummed 	none 	envelope, buffered 	n/a
ProLong 500 year archival envelope 	unknown 	Conservation Resources 	PASS 	2006 	NAA 	PAT 	watermarked, 80gsm, buffered, ungummed 	none 	envelope, buffered 	n/a
Negative preservers, Print File 	unknown 	Get Smart Products 	PASS 	1996 	NAA 	PAT 	Code 35–6HB 	none 	sleeve, negative 	n/a
Magnetic photograph album page 	unknown 	Grant Studio 	PASS 	2003 	NAA 	PAT 	none 	paper, plastic, and adhesive elements 	page, photo album 	n/a
Memory scrapbook page 	unknown 	Grant Studio 	PASS 	2003 	NAA 	PAT 	none 	paper and plastic elements 	page, scrapbook 	n/a
Photo album page 	unknown 	Grant Studio 	PASS 	2003 	NAA 	PAT 	white 	paper and plastic elements 	page, photo album 	n/a
Pocket page photo album page 	unknown 	Grant Studio 	PASS 	2003 	NAA 	PAT 	none 	paper and plastic elements 	page, photo album 	n/a
Acid Free White Paper 	unknown 	GuisePak 	PASS 	2009 	NAA 	PAT 	400 µm 	none 	paper 	n/a
Archival (grey, blue/white) corrugated board 	unknown 	GuisePak 	PASS 	2010 	NAA 	PAT 	(Code GPO31B) 	none 	board, corrugated archival grey, blue/white 	n/a
Archival liner 	unknown 	GuisePak 	PASS 	2009 	NAA 	PAT 	blue/grey 	none 	board 	n/a
Archival liner (blue/grey) 	unknown 	GuisePak 	PASS 	2009 	NAA 	PAT 	220gsm 	none 	board 	n/a
Conservation board 	unknown 	GuisePak 	PASS 	2008 	NAA 	PAT 	300 gsm, 1000 µm 	none 	board 	n/a
E Flute corrugated board (grey/natural white) 	unknown 	GuisePak 	PASS 	2009 	NAA 	PAT 	1.60mm, grey/natural white 	none 	board, corrugated 	n/a
Klug corrugated board (Ref KCB BF) 	unknown 	GuisePak 	PASS 	2009 	NAA 	PAT 	1600µm, 560 gsm, Ref KCB BF 	none 	board, corrugated 	n/a
Klug Karton Board 	unknown 	GuisePak 	PASS 	2009 	NAA 	PAT 	350µm, 330 gsm- 277 µm, 240 gsm- 1600 µm, 560 gsm 	none 	paper 	n/a
Renaissance tissue 	unknown 	Light Impressions 	PASS 	1996 	NAA 	PAT 	unbuffered 	none 	paper, tissue 	n/a
Slide Guard polypropylene sleeve 	unknown 	Light Impressions 	PASS 	1996 	NAA 	PAT 	none 	none 	sleeve, slide 	n/a
Somerset textured paper 	unknown 	London Graphics Centre? 	PASS 	2014/01/16 	BM 	Oddy test 	Radiant White 225 G/M2, 100% cotton paper 	showcase graphics 	paper 	n/a
Mylar 	unknown 	Maria Anttems 	PASS 	2011 	NAA 	PAT 	100 micron thickness, A4 size 	none 	film, polyester 	n/a
Manila file folder 	unknown 	McDonald Printing Group 	PASS 	2005 	NAA 	PAT 	285 gsm 	none 	Folder, file manila 	n/a
Polyolefin Heat-Shrink Tubing 8098K323 	unknown 	McMaster-Carr 	Pass 	2011/01/11 	CMA 	Oddy Test 	Standard polyolefin 	barrier/coating material for brass mounts 	barrier/padding 	none
Polyolefin Heat-Shrink Tubing 8098K323 	unknown 	McMaster-Carr 	Pass 	2011/01/20 	CMA 	Oddy Test 	Standard polyolefin 	barrier/coating material for brass mounts 	barrier/padding 	none
Rising museum mount board 	unknown 	Neenah Paper (formerly Rising Paper 	PASS 	1996 	NAA 	PAT 	none 	none 	board, paper 	n/a
Millenium manila board (buff) 	unknown 	Rolls Filing System 	PASS 	2003 	NAA 	PAT 	244, 285, 326, 374 gsm 	none 	board 	n/a
Millenium manila board (buff) 	unknown 	Rolls Filing System 	PASS 	2007 	NAA 	PAT 	244,285, 326, 374 gsm 	none 	board 	n/a
Millenium manila board (white) 	unknown 	Rolls Filing System 	PASS 	2007 	NAA 	PAT 	285,326, 374 gsm 	none 	board 	n/a
Millenium manila board (white) 	unknown 	Rolls FilingSystem 	PASS 	2003 	NAA 	PAT 	285, 326, 374 gsm 	none 	board 	n/a
Ultimate archive 	unknown 	Rolls FilingSystem 	PASS 	2009 	NAA 	PAT 	none 	none 	unknown 	n/a
Ultimate Archive Paper 	unknown 	Rolls FilingSystem 	PASS 	2009 	NAA 	PAT 	none 	none 	paper 	n/a
Heritage photo album, Tomahawk 	unknown 	Salmat (formerly Hermes Precisa Australia) 	PASS 	1996 	NAA 	PAT 	Creme and Black leaf paper 	none 	album, photo 	n/a
Marbig folder sleeve and refill sleeve 	Unknown 	The Q Store/ Webshops 	PASS 	1997 	NAA 	PAT 	none 	none 	Folder, plastic sleeve 	n/a
Polyethylene storage bag 	Unknown 	Univeristy Products 	PASS 	1997 	NAA 	PAT 	polyethylene 	none 	Bag, storage 	n/a
black rabbet tape 	unknown 	University Products 	fail 	2013/08/22 	CMA 	Oddy test 	acrylic adhesive backed volara 1/16" thickness 	none 	gasket 	
Fosshape Thin 	unknown 	University Products 	Pass 	2011/02/24 	CMA 	Oddy Test 	white Polyester 	custom shapeable mount support 	support 	none
Mohawk digital paper 	unknown 	University Products 	PASS 	1996 	NAA 	PAT 	none 	none 	paper 	n/a
Fosshape Thick 	Unknown 	University Products 	Pass 	2011/03/03 	CMA 	Oddy Test 	white/ Polyester 	sets with heat 	support, mount 	none
Fosshape Thin 	Unknown 	University Products 	Pass 	2011/02/24 	CMA 	Oddy Test 	white/ Polyester 	sets with heat 	support, mount 	none
bending plywood or Wigglewood 	unknown 	unknown 	Fail 	2000/03/21 	GCI 	Oddy test 	None 	None 	plywood 	n/a
Book binding board 	unknown 	X-Press Graph-X 	PASS 	2000 	NAA 	PAT 	double sided, smooth/textured 	none 	board, paper 	n/a
Multimat 	unknown 	X-Press Graph-X 	PASS 	2000 	NAA 	PAT 	none 	none 	matboard 	n/a
White core board 	unknown 	X-Press Graph-X 	PASS 	2000 	NAA 	PAT 	1 mm 	none 	board, paper 	n/a
500 YearTM 	unknown 	Zetta Florence 	PASS 	2003 	NAA 	PAT 	watermarked; 90, 120, 150 gsm 	none 	paper, archival barrier 	n/a
500 Year™ archival photocopy paper, watermarked 	unknown 	Zetta Florence 	PASS 	2006 	NAA 	PAT 	watermarked;90, 120, 150 gsm 	none 	paper, copy 	n/a
500 Year™ corrugated archival board, blue/grey 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	double wall and single wall 	none 	board, corrugated blue/grey single and double wall 	n/a
500 Year™ Corrugated Archival Board, double wall, blue/grey 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	(code MUB) 	none 	board, corrugated archival double wall blue/grey 	n/a
500 Year™ Corrugated Archival Board, single wall, blue/grey 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	(code MUB) 	none 	board, corrugated archival single wall blue/grey 	n/a
Acid-free library board 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	665 x 970 mm, 280 gsm, code (ZFLIB180P) 	none 	board, library 	n/a
Acid-free library board 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	505 x 735 mm, 280 gsm, code (ZFLIB190P) 	none 	board, library 	n/a
Barrier paper APP/ZFBP (off white) 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	90 & 120 gsm 	none 	paper, barrier off white 	n/a
Brilliant Enclosures, 5 x 7" M415X7-A-5 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	5 x 7" M415X7-A-5 	none 	envelope 	n/a
Copy Paper, 80 gsm 	unknown 	Zetta Florence 	PASS 	2011 	NAA 	PAT 	80 gsm 	none 	paper, copy 	n/a
Mylar film 	unknown 	Zetta Florence 	PASS 	2006 	NAA 	PAT 	75 µm and 100 µm 	none 	Film, polyester 	n/a
PAPENV7RECORD, 18.3 x 18.3 cm envelope 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	18.3 cm square 	none 	envelope 	n/a
Polyethylene Envelope 	unknown 	Zetta Florence 	PASS 	1996 	NAA 	PAT 	none 	none 	envelope, polyethylene 	n/a
Seamless envelope, off white 	unknown 	Zetta Florence 	PASS 	2010 	NAA 	PAT 	90 gsm (code PAPSEA) 	none 	envelope, seamless 	n/a
500 YearTMbuffered envelopes 	unknown 	ZettaFlorence 	PASS 	2003 	NAA 	PAT 	seamless and standard style; 90 and 120 gsm 	none 	envelope, buffered 	n/a
500 Year™ archival folder 	unknown 	ZettaFlorence 	PASS 	2003 	NAA 	PAT 	none 	none 	folder 	n/a
500 Year™ archival folder 	unknown 	ZettaFlorence 	PASS 	2006 	NAA 	PAT 	none 	none 	folder 	n/a
500 Year™ folder board 	unknown 	ZettaFlorence 	PASS 	2003 	NAA 	PAT 	white; 260 and 330gsm 	none 	board, folder 	n/a
Green/grey library board 	unknown 	ZettaFlorence 	PASS 	2003 	NAA 	PAT 	240 and 490gsm 	none 	board, library 	n/a
Green/grey libraryboard 	unknown 	ZettaFlorence 	PASS 	2006 	NAA 	PAT 	240 and 490gsm 	none 	board, library 	n/a
500 YearTM archival corrugated (blue/grey) board 	Visy 	Zetta Florence 	PASS 	2002 	NAA 	PAT 	single and double wall 	none 	board, corrugated 	n/a
Volara 	Volara 	unknown 	Pass 	2008 	CMA 	Oddy Test 	white, closed cell polyethylene foam 	none 	foam, closed cell 	none
VIROC BRUT, C0801000100010101 	VIROC, PORTUGAL 	VIROC, PORTUGAL 	P 	2010/06/18 	BM 	Oddy Test 	CEMENT BONDED PARTICLE BOARD, GREY, 	PREP/Drying time: N/A, test #6862 	BOARD 	none
VIROC BRUT, C0801000100010102 	VIROC, PORTUGAL 	VIROC, PORTUGAL 	P 	2010/06/18 	BM 	Oddy Test 	CEMENT BONDED PARTICLE BOARD, BLACK, 	PREP/Drying time: N/A, test #6861 	BOARD 	none
VIROC BRUT, C1001000100010105 	VIROC, PORTUGAL 	VIROC, PORTUGAL 	P 	2010/06/18 	BM 	Oddy Test 	CEMENT BONDED PARTICLE BOARD, WHITE, 	PREP/Drying time: N/A, test #6860 	BOARD 	none
ALUMINIUM KITCHEN FOIL, 	WAITROSE 	WAITROSE 	P 	2009/09/25 	BM 	Oddy Test 	ALUMINIUM, SILVER, 	PREP/Drying time: N/A, test #6614 	BARRIER 	none
ARCHIVAL BOX, 	WALTER NEWBURYT 	WALTER NEWBURYT 	F 	2009/03/20 	BM 	Oddy Test 	ARCHIVAL BUCKRAM, RED, 	PREP/Drying time: N/A, test #6318 	CONTAINER 	none
WHATMAN FILTER PAPER , GRADE 1 1001-150 	WHATMAN (M) 	VWR (S) 	P 	2013/06/26 	BM 	Oddy Test 	PAPER, WHITE, 	PREP/Drying time: N/A, test #7891 	PAPER 	none
FOSSHAPE, 300 (3MM) OR 600 (6.5MM) 	WONDERFLEX WORLD (M) 	PRESERVATION EQUIPMENT LTD (S) 	T 	2013/11/28 	BM 	Oddy Test 	LOW MELT POLYESTER, WHITE, 	PREP/Drying time: N/A, test #8072 	MOUNT/ MOUNT MAKING 	none
Glad zip-lock bag 	Woolworths 	The Dow Chemical Company 	PASS 	1997 	NAA 	PAT 	none 	none 	Bag, resealable 	n/a
ECHO PANEL, WOVEN IMAGE ECHO PANEL 	WOVEN IMAGE 	WOVEN IMAGE 	P 	2013/03/22 	BM 	Oddy Test 	POLYETHYLENE TEREPHTHALATE (PET), BLACK, 	PREP/Drying time: N/A, test #7739 	BOARD 	none
Book binding board, double sided (smooth/textured) 	X-Press Graph-X 	X-PressGraph-X 	PASS 	2008 	NAA 	PAT 	double-sided,smooth/textured 	none 	board, binding 	n/a
PLASTAZOTE, LD45 	ZOTEFOAMS 	ZOTEFOAMS 	P 	2009/02/12 	BM 	Oddy Test 	POLYETHYLENE, WHITE, 	PREP/Drying time: N/A, test #6199 	FOAM 	none
EVAZOTE, EV 30 WE 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/20 	BM 	Oddy Test 	CROSS-LINKED ETHYLENE COPOLYMER, WHITE, 	PREP/Drying time: N/A, test #7917 	FOAM 	none
EVAZOTE, EV50 BE 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	CROSS-LINKED ETHYLENE COPOLYMER, BLUE, 	PREP/Drying time: N/A, test #7932 	FOAM 	none
EVAZOTE, EV50 RGY 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	CROSS-LINKED ETHYLENE COPOLYMER, GREY, WITH SILVER METALLIC FLECKS 	PREP/Drying time: N/A, test #7931 	FOAM 	none
PLASTAZOTE, HL 34 WE 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/20 	BM 	Oddy Test 	POLYETHYLENE, WHITE, 	PREP/Drying time: N/A, test #7918 	FOAM 	none
PLASTAZOTE, HL47 BK 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	POLYETHYLENE, BLACK, 	PREP/Drying time: N/A, test #7928 	FOAM 	none
PLASTAZOTE, HIGH DENSITY, HD 115 WE 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/20 	BM 	Oddy Test 	POLYETHYLENE, WHITE, 	PREP/Drying time: N/A, test #7919 	FOAM 	none
PLASTAZOTE, HIGH DRUABILITY, MP15 BK 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/08 	BM 	Oddy Test 	METALLOCENE POLYETHYLENE, BLACK, 	PREP/Drying time: N/A, test #7912 	FOAM 	none
PLASTAZOTE, HIGH DURABILITY, FLAME RETARDANT, MP15 FR PGY 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/08 	BM 	Oddy Test 	METALLOCENE POLYETHYLENE, FLAME RETARDANT, GREY, 	PREP/Drying time: N/A, test #7911 	FOAM 	none
PLASTAZOTE, LOW DENSITY, LD24 LC BK 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	LOW DENSITY POLYETHYLENE, BLACK, 	PREP/Drying time: N/A, test #7929 	FOAM 	none
PLASTAZOTE, LOW DENSITY, LD45 RD 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/09/10 	BM 	Oddy Test 	LOW DENSITY POLYETHYLENE, RED, 	PREP/Drying time: N/A, test #7940 	FOAM 	none
PLASTAZOTE, LOW DENSITY, LD45 WT 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/09/10 	BM 	Oddy Test 	LOW DENSITY POLYETHYLENE, WHITE, 	PREP/Drying time: N/A, test #7941 	FOAM 	none
PLASTAZOTE, SEMI RIGID, PK33 MGY 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/08 	BM 	Oddy Test 	POLYETHYLENE, GREY, 	PREP/Drying time: N/A, test #7910 	FOAM 	none
PLASTAZOTE, SEMI RIGID, PK80 SGY 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/08 	BM 	Oddy Test 	POLYETHYLENE, GREY, LIGHT, 	PREP/Drying time: N/A, test #7913 	FOAM 	none
PLASTAZOTE, STANDARD, LD45 GY 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/08 	BM 	Oddy Test 	LOW DENSITY POLYETHYLENE, GREY, WITH SILVER METALLIC FLECKS 	PREP/Drying time: N/A, test #7909 	FOAM 	none
PLASTAZOTE, STANDARD FLAME RETARDANT, LD45 FR 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/08 	BM 	Oddy Test 	POLYETHYLENE, FLAME RETARDANT, BLUE, LIGHT, 	PREP/Drying time: N/A, test #7914 	FOAM 	none
ZOTEK, HIGH TEMPERATURE, N A 30KG/M3 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	POLYAMIDE (NYLON), BLACK, 	PREP/Drying time: N/A, test #7927 	FOAM 	none
ZOTEK, HIGH TEMPERATURE, N B50 50KG/M3 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	POLYAMIDE (NYLON), BLACK, 	PREP/Drying time: N/A, test #7926 	FOAM 	none
ZOTEK, LOW FLAME, SMOKE TOXICITY, F35 30KG/M3 1.9 PCF 	ZOTEFOAMS PLC (M) 	UNKNOWN 	P 	2013/08/27 	BM 	Oddy Test 	KYNAR PVDF, WHITE, 	PREP/Drying time: N/A, test #7925 	FOAM 	none
Evazote EV50 	Zotefoams 	Sekisui Pilon 	PASS 	2006 	NAA 	PAT 	10 mm thick (white) 	none 	foam, EVA copolymer 	n/a
Plastazote LD45 	Zotefoams 	Sekisui Pilon 	PASS 	2006 	NAA 	PAT 	10 mm thick 	none 	foam, closed cell, cross-linked polythene 	n/a
Ethafoam® 220 	Sealed Air 	Sealed Air 	PASS 	2012/06/06 	CH 	Oddy Test 	Polyethylene, white 	Lab sample purchased 2011 	Foam 	x
Ethafoam® MRC® 	Sealed Air 	Sealed Air 	PASS 	2012/06/06 	CH 	Oddy Test 	100% recycled content polyethylene, black, 2" thick 	Sample received Feb 2012 	Foam 	x
Ethafoam® HRC® 	Sealed Air 	Sealed Air 	PASS 	2012/03/10 	CH 	Oddy Test 	min. 65% recycled content polyethylene, black, 2" thick 	Sample received Feb 2012 	Foam 	x
Stratocell® RC® 	Sealed Air 	Sealed Air 	PASS 	2012/03/10 	CH 	Oddy Test 	min. 65% recycled content polyethylene, black, 2" thick 	Sample received Feb 2012 	Foam 	x
Coroplast® Archival 	Coroplast. Inc. 	Talas 	PASS 	2012/06/06 	CH 	Oddy Test 	Polypropylene, translucent 	Lab sample purchased 2011 	Plastic Board 	x
Corogreen™ 	Coroplast. Inc. 	Coroplast. Inc. 	PASS 	2012/06/06 	CH 	Oddy Test 	Polypropylene with recycled content, 4 mm, white faces with black core 	Sample Received Feb 2012 	Plastic Board 	x
Heritage Corrugated Board 	NA 	Talas 	PASS 	2012/03/10 	CH 	Oddy Test 	Light blue-grey face with white flutes and white face 	Lab sample. Purchased 2011 	Cellulose Board 	x
Archivart® Multiuse Board 	Archivart® 	Archivart® 	PASS 	2012/03/10 	CH 	Oddy Test 	Light blue-grey, single wall 	Lab sample. Purchased 2011 	Cellulose Board 	x
Superior Millboard Sample#1 	Conservation By Design 	Conservation By Design/Larson-Juhl 	FAIL 	2012/06/06 	CH 	Oddy Test 	Dark green pressed millboard made from pre-consumer recycled waste 	Sample Received Feb 2012 	Cellulose Board 	x
Superior Millboard Sample#2 	Conservation By Design 	Conservation By Design/Larson-Juhl 	PASS 	2012/06/06 	CH 	Oddy Test 	Light green pressed millboard made from pre-consumer recycled waste 	Sample Received May 2012 	Cellulose Board 	x
EVA FOAM, SEV 035 	none 	Keng Huat Rubber Products 	TEMP 	2017/02/16 	HCC 	Oddy Test 	Black Ethylene-Vinyl Acetate foam 	none 	Polymer foam 	
EVA FOAM 	none 	Fagerdala Singapore Pte Ltd 	FAIL 	2017/02/16 	HCC 	Oddy Test 	White Ethylene-Vinyl Acetate foam 	none 	Polymer foam 	
MESH FABRIC 07-64/45 	none 	Sefar Petex 	FAIL 	2017/08/16 	HCC 	Oddy Test 	Off-White Plastic mesh 	none 	Polymer mesh 	
MESH FABRIC 07-425/46 	none 	Sefar Petex 	PASS 	2017/08/16 	HCC 	Oddy Test 	Off-White Plastic mesh 	none 	Polymer mesh 	
MESH FABRIC 07-102/44 	none 	Sefar Petex 	PASS 	2017/08/16 	HCC 	Oddy Test 	Off-White Plastic mesh 	none 	Polymer mesh 	
MESH FABRIC 07-285/55 	none 	Sefar Petex 	PASS 	2017/08/16 	HCC 	Oddy Test 	Off-White Plastic mesh 	none 	Polymer mesh 	
MESH FABRIC 07-120/50 	none 	Sefar Petex 	PASS 	2017/08/16 	HCC 	Oddy Test 	Off-White Plastic mesh 	none 	Polymer mesh 	
Carbon Fibre Fabric 	none 	Polymer Technologies Pte. Ltd 	PASS 	2017/08/16 	HCC 	Oddy Test 	BLACK 	none 	Carbon fibre 	
BARRIKADE EP TERRAZZO 	Hesselberg Bygg AS/Norway, Company of Sto SE & Co KG aA, Germany 	Sto SEA Pte. Ltd. Singapore 	PASS 	2018/03/20 	HCC 	Oddy Test 	Epoxy terrazzo coating system for floors 	none 	Epoxy 	100px
Non-archival roller 	Sonoco 	Sonoco Singapore 	FAIL 	2018/06/28 	HCC 	Oddy Test 	none 	none 	paper board 	100px
Card board roller 	Talas 	Talas online 	FAIL 	2018/06/28 	HCC 	Oddy Test 	none 	none 	paper board 	100px
Artcare Archival Foam White Board 	 	University Products 	PASS 	2018/06/28 	HCC 	Oddy Test 	none 	none 	paper board, foam 	100px
Archival Roller 	 	University Products 	PASS 	2018/06/28 	HCC 	Oddy Test 	none 	none 	paper 	100px
MG Interleaving KRAFT paper 	Sonoco 	Sonoco Singapore 	FAIL 	2018/06/28 	HCC 	Oddy Test 	none 	none 	paper 	100px
Marveal Seal equivalent 	Sonoco 	Sonoco Singapore 	PASS 	2018/06/28 	HCC 	Oddy Test 	none 	none 	aluminium foil 	100px
Glassine 	Sonoco 	Sonoco Singapore 	PASS 	2018/06/28 	HCC 	Oddy Test 	none 	none 	coated paper 	100px
StoSilent Board 	Sto SE & Co KGaA 	Sto SEA Pte. Ltd. Singapore 	PASS 	2018/08/23 	HCC 	Oddy Test 	Acoustic panel made of expanded glass granulate 	none 	glass granulate 	
Polyester Wadding 	--- 	AE Model Singapore 	PASS 	2019/02/14 	HCC 	Oddy Test 	 	none 	Fabric - batting & padding 	100px
Polystyrene beads 	--- 	Spotlight Singapore 	PASS 	2019/02/14 	HCC 	Oddy Test 	--- 	none 	Polymer - block/bulk/pellet 	100px
ProSorb Humidity Stabiliser 	ProSorb 	Preservation Equipment Ltd 	PASS 	2019/02/14 	HCC 	Oddy Test 	--- 	only beads were tested 	Polymer - block/bulk/pellet 	100px
Sintra 3A 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	PVC 	none 	Board - plastic/polymeric/synthetic 	
6 Plywood 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	
12 Plywood 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	
Ash Hardwood 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	
Blueboard 	 	 	PASS 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Jute Fiber 	none 	Paper-based (eg. folder, cardboard, sheet) 	
Delrin 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Polyacetal 	none 	Polymer - block/bulk/pellet 	
Flame Retardant Plywood 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Polymer - block/bulk/pellet 	
Gatorboard 	 	 	Temporary to FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Polystyrene 	none 	Board - composite (eg. Corian, drywall) 	
Komatex 	 	 	PASS to Temporary 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	PVC 	none 	Board - plastic/polymeric/synthetic 	
Medex MDF Wood 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	
Oak Hardwood (Aged 50 years) 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	
Paulownia Wood 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	File:AIC-Upload-Paulownia.pdfpdf
Plexi Glass 	 	 	PASS 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Polymethyl methacrylate 	none 	polymer - sheet (>1mm thick) 	
Oak Hardwood (Aged 1 year) 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	 	none 	Board - natural (eg. wood, cotton) 	
Fome-Cor with Zeolites 	 	 	PASS 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Polystrene with a Jute Fiber Face 	none 	Board - composite (eg. Corian, drywall) 	
Volara Foam 	 	 	PASS to Temporary 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Polyethylene 	none 	Polymer - foam - non building insulation 	
PUR (ester) Foam 	 	 	FAIL 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Polyester Urethane Resin 	none 	Polymer - foam - non building insulation 	
Purple Nitrile Gloves 	Kimberly Clark 	 	PASS to Temporary 	2016/7 	IMA 	Oddy Test, Microchemical, and EGA 	Acrylonitrile-butadiene Copolymer 	none 	Polymer - glove 	
Marmoleum Piano 	Forbo Flooring Systems 	Forbo Flooring UK Ltd 	Fail, Unsuitable 	2018/12/11 	NYUL 	Oddy Test 	Linseed oil, inorganic fillers, rosin, jute, wood flour 	Color is grey dusk 	Other - Flooring 	Link to Control Coupons ‎
Marmoleum Piano 	Forbo Flooring Systems 	Forbo Flooring UK Ltd 	Fail, Unsuitable 	2018/12/11 	NYUL 	Oddy Test 	Linseed oil, inorganic fillers, rosin, jute, wood flour 	Color is mellow yellow 	Other - Flooring 	Link to Control Coupons ‎
Gerflor Mipolam Symbioz 	Gerflor The Flooring Group 	Gerflor USA 	Fail, Unsuitable 	2018/12/11 	NYUL 	Oddy Test 	PVC, Plasticizer 	Color is black diamond 	Other - Flooring 	‎Link to Control Coupons
Gerflor Mipolam Symbioz 	Gerflor The Flooring Group 	Gerflor USA 	Fail, Unsuitable 	2018/12/11 	NYUL 	Oddy Test 	PVC, Plasticizer 	Color is sunshine 	Other - Flooring 	Link to Control Coupons ‎
PE #2.2 New England Foam 	N/A 	New England Foams 	Pass, Permanent 	2019/1/30 	NYUL 	Oddy Test 	Polyethylene 	none 	Polymer - foam - non building insulation 	Link to Control Coupons ‎
EPE #1.3 Arplank 	Arplank 	New England Foams 	Pass, Permanent 	2019/1/30 	NYUL 	Oddy Test 	Expanded polyethylene 	none 	Polymer - foam - non building insulation 	Link to Control Coupons ‎
EPE #1.9 Arplank 	Arplank 	New England Foams 	Pass, Permanent 	2019/1/30 	NYUL 	Oddy Test 	Expanded polyethylene 	none 	Polymer - foam - non building insulation 	‎Link to Control Coupons
XPLE #4 Microcell 	Microcell 	New England Foams 	Temporary 	2019/1/30 	NYUL 	Oddy Test 	Crosslinked polyethylene 	Color is black 	Polymer - foam - non building insulation 	Link to Control Coupons ‎
XPLE #2 Microcell 	Microcell 	New England Foams 	Temporary 	2019/1/30 	NYUL 	Oddy Test 	Crosslinked polyethylene 	Color is blue 	Polymer - foam - non building insulation 	Link to Control Coupons ‎
PE #4 New England Foams 	N/A 	New England Foams 	Pass, Permanent 	2019/1/30 	NYUL 	Oddy Test 	Polyethylene 	Color is white 	Polymer - foam - non building insulation 	‎Link to Control Coupons
Neoprene UChannel 	Trim Lok Incorporated 	McMaster Carr 	Pass, Permanent 	2019/1/30 	NYUL 	Oddy Test 	Neoprene rubber 	Color is black, 8507K15 (Line Item #4) 	U-Channel 	Link to Control Coupons ‎
Neoprene UChannel 	Trim Lok Incorporated 	McMaster Carr 	Fail, Unsuitable 	2019/1/30 	NYUL 	Oddy Test 	Neoprene rubber 	Color is black, 8507K52 (Line Item #2) 	U-Channel 	‎Link to Control Coupons
Neoprene foam with pressure sensitive adhesive (1/2" T x 1/2" W x 10ft) 	N/A 	McMaster Carr 	Fail, Unsuitable 	2019/4/2 	NYUL 	Oddy Test 	N/A 	Color is black 	Gasketing 	‎
Premium neoprene sponge with pressure sensitive adhesive (1/8" x 3/4" x 10 ft) 	N/A 	McMaster Carr 	Fail, Unsuitable 	2019/4/2 	NYUL 	Oddy Test 	N/A 	Color is black 	Gasketing 	‎
4311-N with SN PSA one side (0.125"TH x 12" x 12") 	N/A 	Jacobs & Thompson 	Temporary 	2019/4/2 	NYUL 	Oddy Test 	SN PSA is rubber adhesive 	Color is black 	Gasketing 	‎
0.125" thick clear silicone rubber sheeting 	N/A 	Acme Rubber 	Pass, Permanent 	2019/4/2 	NYUL 	Oddy Test 	Silicone 	Color is clear 	Gasketing 	‎
[http://cameo.mfa.org/wiki/Neoprene Neoprene U-channel 	N/A 	Acme Rubber 	Pass, Permanent 	2019/4/8 	NYUL 	Oddy Test 	Neoprene rubber 	Color is black, product number 8507K43 	U-channel for glass panes 	Link to Control Coupons ‎
==Links for Manufacturers/ Suppliers==
 Back to top of table
* 3A Composites
* 3M
* Abatron Inc.
* Abbey Plastics Products 
* Aeroflex International
* Airefrig Australia 
* Albox Australia 
* Amvic Building System
* Ansell
* Archival Survival 
* Archivart® Products for Conservation and Restoration
* Armstrong Flooring
* Aspen Aeorgels
* Australian Paper
* Avery Dennison Office Products 
* Aves Studio
* Britestar Australia Pty Ltd
* Bunzl/Sealed Air Australia
* Byrne Sign Supply
* Canson Australia (Arjo Wiggins)
* Capri Collections
* Champion Plastics (USA) 
* Clean Seal, Inc.
* Clear File 
* Colophon Book Arts
* Conservation by Design
* Conservation Resources
* Corex Plastics
* Delta Designs
* Depron Foam
* The Dow Chemical Company USA
* Dunlop Foams
* DuPont
* Fuji Xerox Australia
* Gallina USA
* Garware Polyester (India)
* Get Smart Products
* Grant Studios
* GuisePak
* Harbor Sales Inc.
* The Heirloom Shadow Box Company
* Hesselberg Bygg
* Hiromi Paper
* Homasote
* Home Depot
* ILPEA Industries Inc.
* International Paper
* Isolatek International
* Jackaroo 
* Johns Manville
* Keene Village Plastics
* Kimberly-Clark Health Care (now Halyard Health)
* Legion Paper
* Light Impressions USA
* Maria Anttems: (03)9799 9073 
* McCausey Specialty Products
* McDonald Printing Group 
* McMaster-Carr
* Metro Foam Products
* Mulford Plastics
* Multapex 
* Neenah Paper (formerly Rising Paper) (USA)
* Netherland Rubber Co.
* Nielsen Bainbridge 
* Novabond
* Nudo
* OBO-Werke GmbH & Co.
* Owens Corning
* Paradise Packaging Co.
* Pinpak–Grayson Packaging 
* Plascoat
* Precision Foam Manufacturing
* Polistini Conservation Material
* The Q Store/ Webshops 
* Raleigh Paper
* Rising
* Rolls Filing System
* SABIC Innovative Plastics
* Salmat (formerly Hermes Precisa Australia) 
* Sekisui Pilon 
* Shapeways
* Shoalhaven Mill
* Spacesaver
* Spicers
* StoCretec
* StoSEA
* Talas
* Transcontinental Packaging
* Tuscan Industries
* University Products
* Visy
* Volara
* Woolworths 
* X-Press Graph-X
* Zetta Florence
* Zotefoams (England)