본 연구는 순환골재의 품질을 개선시키기 위해 pH 10.2의 알칼리성을 띄고 있는 입경 5nm~60nm 정도의 40% 콜로이달 실리카 수용액을 사용하고, 4가지 표면처리방법을 적용하여 순환골재의 품질 향상 시험을 하였다. 순환골재의 품질시험은 비중, 흡수율, 기공률, 계면특성, 그리고 압축 및 인장시험을 하였다. 100kpa의 일정 압력하에서 콜로이달 실리카 수용액이 표면에 도포되고 에서 건조됨으로써 콜로이달 실리카 용액이 순환골재의 시멘트 모르타르의 표면을 일정한 두께로 효과적으로 코팅되었다. 4가지 표면처리 방법 중 Method C에 의한 표면처리방법이 순환골재의 품질을 효과적으로 개선시켰으며, 그로인해 순환골재콘크리트의 압축강도 및 인장강도 향상에 영향을 미친 것으로 판단된다.

The research, in order to enhance the quality of recycled aggregate, was carried out the quality characteristics test of the recycled aggregates by applying the four kinds of surface treatment using a colloidal suspension of approximately 5nm~60nm particle size with the alkalinity of pH 10.2. The quality tests of recycled aggregate have been processed by specific gravity, water absorption, porosity, surface properties, and the compression and tensile tests. The colloidal suspension was coated effectively the surface of the old cement mortars of recycled aggregate with a constant thickness by colloidal suspension is being applied to the recycled aggregate surface under constant pressure of 100kpa and then it was dried in at . The surface treatment method by the Method C out of 4 kinds of surface treatment improved effectively the quality of the recycled aggregates, whereby it obtained the best compressive strength and tensile strength of the recycled aggregate concrete.

(게재일: 2015.12.20)
고성능 시멘트 복합재료(HPFRCC)는 인장력 작용 하에 있어서 초기 균열이 발생한 이후에도 변형의 증가와 함께 응력이 증가하는 변형경화 특성과 다수의 미세 균열이 발생함으로써 균열 폭 제어 특성을 나타낸다. 그러나 국내의 HPFRCC의 연구는 단일섬유를 중심으로한 제조방법이나 경화전후의 재료적 성상에 관한 연구들이 진행되어지고 있으나 복합섬유인 HPFRCC를 실무에서 활용하기 위한 연구는 미미한 실정이다. 따라서 본 연구에서는 시공성 및 경제성을 고려하여 실무에서 효율적인 활용성을 검토하기 위한 방안으로 강섬유(이하 SL)와 유기섬유(이하 OL)를 조합한 복합섬유로 유동성 및 강도 등 제반 공학적 특성을 검토하고자 한다. 결과적으로 강섬유 장섬유(SL)과 유기섬유 장섬유(OL)의 복합섬유를 활용하는 HPFRCC의 제반 공학적 성능을 검토한 결과 복합섬유 혼입율 1.5%일 때 가장 우수한 것으로 판단되었다.

The high performance fiber reinforced cementitious composite (HPFRCC) controls the cracking development of the structure by inducing micro-cracking and strain hardening behavior after the initial cracking under the tensile conditions. Although, in Korea, the research about manufacturing the single-fiber reinforced cementitious composite or the mechanical properties of hardened status has been conducted, the research to apply the HPFRCC with multi-fiber is not sufficient. Hence, in this research, considering the workability and economic aspect for practical applications, the engineering properties of HPFRCC with combined long steel fiber (SL) and long organic fiber (OL) are evaluated such as workability and strength. As a result of evaluating the engineering properties of HPFRCC, the most favorable performance was obtained when the mixture contained 1.5% of combined SL and OL.

(게재일: 2015.12.20)
본 연구에서는 국내의 석회암 광산에서 시멘트 제조를 위해 채굴되는 석회석을 시멘트 제조용으로 사용하지 못하는 저품위 석회암 폐석을 분쇄 및 체가름 등의 골재 생산설비를 통하여 제조한 석회암 굵은 골재를 고강도 콘크리트용 골재로의 활용성을 검토한 것이다. 즉, 석회암 굵은 골재를 사용한 고강도 콘크리트의 유동성, 공기량, 압축강도 등의 시공 특성을 화강암 굵은 골재에 대한 치환율로 변화시켜 그 성능을 검토하였다. 실험결과 굳지 않은 콘크리트 및 경화 콘크리트에서의 시공특성은 화강암 골재를 사용한 고강도 콘크리트와 동등 이상의 양호한 시공품질이 확보되는 것을 확인할 수 있었다.

The aim of this research is suggesting application method of the wasted rock obtained from the limestone quarry of raw material for cement as a coarse aggregate for high strength concrete after crushing and sieving processes. The wasted rock has been normally wasted because of its low quality as a material for cement production. In this research, the concrete using this wasted limestone coarse aggregate was evaluated the constructability based on the performances of workability, air content, and compressive strength. From the experiment, a favorable performance was achieved with a limestone coarse aggregate for high strength concrete comparing to the high strength concrete using granite coarse aggregate.

(게재일: 2015.12.20)
경수로 사용후핵연료 수송/저장용기의 핵임계 해석은 사용후핵연료내의 악티나이드핵종 및 핵분열생성물 함유량에 대한 불확실성을 이유로 신연료로 가정된 가상의 연료를 선정하여 평가해오고 있다. 그러나 이러한 평가방법은 용기 설계 시 과도한 임계여유도를 유도하여 경제적 손실을 유발할 수 있는 단점이있다. 이와 같은 단점을 극복하기 위하여 최근 연소도이득효과(burnup credit, BUC)를 반영한 수송저장용기의 설계 및 상용화를 위한 연구가 추진되었다. 이에 본 연구에서는 한국원자력환경공단에서 개발중인 금속겸용용기를 대상으로 연소도 이득효과적용 시 핵임계 안전성(criticality safety)에 영향을 미칠 것으로 예상되는 '노심 운전인자', '축방향 연소도 분포', '오장전 사고상황'에 대하여 핵임계 평가를 수행하였다. 그 결과 노심운전인자 중 저농축, 고연소도일 때 비출력에 따른 핵임계 변화가 크게 평가되었으며, 고연소도 사용후핵연료에서 End effect가 양의 값을 나타내었다. 특히 오장전에 의한 유효증배계수는 최대 0.18467증가하였으므로, 연소도이득효과를 적용 할 경우 필수고려사항임을 확인하였다. 본 연구결과는 국내모델(금속겸용용기)의 연소도 이득효과 적용기술 개발 및 사용 후핵연료 장전 시 일어날 수 있는 오장전 사고를 방지하기 위한 운영절차 개발에 참고자료로 활용될 수 있다.

In general, conventional criticality analysis for spent fuel transport/storage systems have been performed based on the assumption of fresh fuel concerning the potential uncertainties from number density calculations of actinide nuclides and fission products in spent fuel. However, these evaluation methods cause financial losses due to an excessive criticality margin. In order to overcome this disadvantage, many studies have recently been conducted to design and commercialize a transportation and storage cask applied to the Burnup Credit (BUC). This study conducted an assessment to ensure criticality safety for reactor operating parameters, axial burn-up profiles and misload accident conditions, which are the factors that are likely to affect criticality safety when the BUC is applied to the dual-purpose cask under development at the KOrea RADioactive waste agency (KORAD). As a result, it was found that criticality resulting from specific power, changed substantially and relied on conditions of low enrichment and high burn-up. Considering the end effect in the case of high burn-up produced a positive-definite result. In particular, the increment of maximum effective multiplication factors due to misloading was 0.18467, confirming that misload is a factor that must be taken into account when applying the BUC. The results of this study may therefore be utilized as references in developing technologies to apply the BUC to domestic models and operational procedures or preventing any misload accidents during the process of spent fuel loading.

(게재일: 2015.08.31)
순수 베타 핵종인 Sr 분석은 화학적 거동이 유사한 알칼리 토금속(Ca, Ba, Ra)등 방해 원소를 제거할 분리 공정이 필요하다. 본 연구는 Sr을 추출/정제하기 위해 추출크로마토그래피법을 이용한 최적의 절차를 마련하는 것을 목적으로 한다. Sr resin 1.5 mL BV(Bed Volume)의 최대 Sr 흡착량은 6 mg이었다. 유량 1 mL min 과 Ca 200 mg 이하에서는 Sr resin 1.5 mL(BV)의 Sr 회수는 정량적이었으나, 유량을 5 mL min 으로 중가 시키면 Sr 회수율이 감소하였다. 같은 양(BV)의 Sr resin을 사용할 경우, 컬럼의 단면적이 작을수록 Sr resin의 분리능이 향상되었다.

For the analysis of Sr, which is a pure beta emitter, radiochemical separation from the main interfering elements such as Ca, Ba and Ra is required due to their similarity in chemical behavior to strontium. This study describes a radioanalytical procedure using extraction chromatography for separating Sr from interfering elements. The maximum capacity of the resin for Sr was approximately 6 mg per 1.5 mL of bed volume (BV). The recovery of Sr on the resin 1.5 mL (BV) was quantitative for the calcium level of 200 mg at the flow rate of 1 mL min . However the chemical yield declined by increasing the flow rate by up to 5 mL min even at the calcium level of 200 mg. When using the same BV of Sr resin, the performance of the resin was enhanced as the cross-sectional area of the Sr resin column is small.

(게재일: 2015.08.31)
본 연구에서는 고준위폐기물 처분시 완충재로 사용되는 벤토나이트의 열적 거동을 평가하기 위해 실내실험장치를 제작하였다. 그리고 실험 결과를 검증하기 위해 유한요소해석 프로그램인 ABAQUS를 이용한 열해석을 실시하였다. 그리고 실험기간 동안의 계절변화를 감안하여 외부대기 온도에 따른 벤토나이트의 열적거동을 평가하였다. 해석결과, 스테인리스스틸이 포함된 case3 해석모델의 결과가 실험결과와 1℃ 내외의 오차를 보이며 거의 일치함을 볼 수 있었다. 그리고 계절에 따른 벤토나이트 온도 해석을 수행한 결과, 시간에 따른 온도분포 경향이 일치함을 확인하였다. 이러한 열해석을 통해 완충재를 둘러싸고 있는 물질의 열전도도와 외부대기의 온도가 벤토나이트 완충재의 열적 거동에 큰 영향을 주는 요소임을 확인할 수 있었다. 향후 열원을 포함한 벤토나이트 완충재의 수분 포화 특성 실험이 실시 될 예정이므로, 실험에 대한 검증과 예측을 위해 보다 적합한 수치해석모델 개발에 대한 연구가 필요할 것이다.

In this study, laboratory test equipment was designed and installed to evaluate the thermal behavior of bentonite, which is used as a buffer in high-level waste disposal systems. The thermal analysis was conducted to verify the test results using ABAQUS, a finite element analysis code. In view of the seasonal changes seen during the test, the thermal behavior of bentonite with a temperature of outside air was evaluated. Of the cases examined, the results of the analysis model using stainless steel (Case 3) approximates to the test results, showing an error of about 1℃. The results of the thermal analysis into seasonal temperature distributions are consistent with trends seen in lab-test results. These analyses show that the effects of the thermal conductivity of the material surrounding the buffer and outside air temperature, are very important factors in the thermal behavior of bentonite. In the future, it is expected that a moisture saturation test of a bentonite buffer containing a heat source will be carried out. Therefore, the development of a numerical analysis model is required for the prediction and verification of the laboratory test results.

(게재일: 2015.08.31)
방사성폐기물 심지층 처분시스템의 안전성평가에서는 일반적으로 정상 시나리오 이외에 심지층 처분시스템이 외부 요인에 의해서 영향을 받는 비정상 시나리오를 추가적으로 고려하게 된다. 본 연구에서는 방사성폐기물 심지층 처분시스템의 비정상 시나리오를 포함하는 복합피폭 시나리오에 대한 안전성평가를 위하여 비정상 시나리오를 구성하는 비정상 사건으로 지진의 국내 발생 특성을 조사하였다. 이를 위하여, 국내(한반도)의 지진 자료에 대한 통계·확률적인 접근법으로 발생 특성을 조사하고, 이를 통해 미래의 지진 발생 특성을 예측하는 방법론과 함께 계산 예를 소개하였다. 그 결과, 국내 연간 지진 발생빈도는 자료의 종류에 따라 그리고 최소 유효 지진규모에 따라 0.4 /yr에서 36.2 /yr까지 넓게 분포되었다. 최종적으로, 처분시스템 안전성평가의 보수성 측면에서 위의 범위 내 최대값인 36.2 /yr가 국내 연간 지진 발생 빈도로써 제안되었고, 처분시스템의 면적비를 고려하여 처분시스템 영향 반경 내 연간 지진 발생 빈도는 5.4×10 /yr로 계산되었다. 그리고, 이때의 최소 유효 지진 규모는 2.3이었다. 본 연구는 앞으로 비정상 사건들이 처분시스템에 미치는 영향에 대한 추가 연구와 함께 향후 복합피폭 시나리오를 고려한 심지층 처분시스템의 안전성평가 신뢰도 향상에 크게 기여할 것으로 판단된다.

Safety assessments of geological radioactive waste disposal systems, need to consider the abnormal scenario in which a system is impacted by external events in addition to a reference scenario. In this study, the characterization and prediction of an earthquake as an external event which will impact disposal systems were conducted probabilistically and statistically for the safety assessment. The domestic earthquake data were analyzed, and the prediction methodologies of the earthquake were suggested with a computational example. From the results, the earthquake occurrence rates in Korea ranged from 0.4 /yr to 36.2 /yr depending on the data set and the completeness magnitude. From a conservative point of view, the earthquake occurrence rate in the disposal system was suggested as 5.4×10 /yr considering the area of the disposal system. At that time, the completeness magnitude of an earthquake was 2.3. This study will be followed by an appraisal of impacts associated with external events on the geological disposal system, and it will contribute to improvements in reliability of the safety assessment.

(게재일: 2015.08.31)
국내 원자력발전소에서는 사용후핵연료 저장용량의 확대를 위해 사용후핵연료저장조에 조밀저장대를 설치하고 있지만 한빛원전은 2024년에 포화가 예상된다. 또한 10개의 원자력발전소가 2029년까지 설계수명에 도달하게 된다. 하지만 원전운영과 해체를 위한 국내 사용후핵연료 관리정책은 아직 결정되지 않은 상황이다. 미국의 경우 원전해체시 사용후핵연료를 중간 저장시설 또는 영구처분장으로 이송하기 전까지 임시적으로 독립된 사용후연료저장조(이하 'SFPI') 방식을 운영하는 사례가 있다. SFPI는 원전해체시 운전정지 후 사용후핵연료를 저장하는데 있어서 방사선 노출 저감, 운영비용 절감, 안전성 보강 등의 효과를 기대할 수 있다. 따라서 이 논문에서는 미국의 SFPI 운영경험, 시스템, 적용규정 등에 대한 사례연구를 수행하였다. 결론적으로 SFPI 국내 적용을 위해서는 사용후핵연료저장 계통의 설계변경 범위 및 예상 소요비용 확정, 원전 해체계획에 설비개선 계획 반영제출, 주기적안전성평가(PSR) 방법 등을 활용한 안전성 평가(운영기간 10 년), 설계변경을 위한 운영 변경허가 신청, 규제기관 심사 및 허가 취득, 설계변경 수행, 규제기관의 확인점검, SFPI 운영을 위한 교육 및 시운전, SFPI 운영 및 정기검사, SFPI 해체 등의 절차가 필요하다.

In many nuclear power plant sites in Korea, high density storage racks were installed in the spent fuel pool to expand the spent fuel storage capacity. Nevertheless, the capability of the Hanbit nuclear site will be saturated by 2024. Also, 10 NPPs will reach their design life expiration date by 2029. In the case of the US, SFPI (Spent Fuel Pool Island) operated temporarily as a spent fuel storage option before spent nuclear fuels were transported to an interim storage facility or a final disposal facility. As a spent fuel storage option after shutdown during decommissioning, the SFPI concept can be expected to have the following effects: reduced occupational exposure, lower cost of operation, strengthened safety, and so on. This paper presents a case study associated with the regulations, operating experiences, and systems of SFPI in the US. In conclusion, the following steps are recommended for applying SFPI during decommissioning in Korea: confirmation of design change scope of SFPI and expected final cost, the submission of a decommissioning plan which is reflected in SFPI improvement plans, safety assessment using PSR, application of an operating license change for design change, regulatory body review and approval, design change, inspection by the regulatory body, education and commissioning for SFPI, SFPI operation and periodic inspection, and dismantling of SFPI.

(게재일: 2015.08.31)
본 연구에서는 저장볼트(storage vault)의 실험을 위하여 1/4 축소모델 내 튜브의 적정 발열량을 선정하고자 상사해석을 수행하였다. 저장볼트에 대한 열 및 유동 해석을 우선적으로 수행하였고, 크기를 1/4로 축소한 저장볼트에 대하여 동일한 전산해석을 수행하였다. 전산해석 결과를 바탕으로, 제안된 무차원수를 비교하여 원형모델과 온도분포와 유동분포가 유사하게 되는 발열량을 선정하였다. 1/4 축소 저장볼트 내 튜브의 열유속이 1.3배일 때, 원형 저장볼트와 1/4 축소 저장볼트의 온도장 및 유동장이 상사되었다. 이 때, 1/4 축소 저장볼트 내 발열량은 약 190 W이다.

This research studied a scaling analysis for the selection of proper heat generation at tube for 1/4-scale storage vaults. First of all, the temperature field and velocity distribution of an original scale storage vault were analyzed and then numerical analysis of a 1/4-scale storage vault was performed to compare each model. The proper heat generation for a 1/4-scale storage vault, at which the temperature and velocity field of a 1/4-scale storage vault showed the best agreement with that of the original storage vault, was evaluated with proposed dimensionless parameters. The behavior of temperature and velocity of fluid in the 1/4-scale case were most similar to those of the original scale, using a heat flux 1.3 times higher than that seen in the original scale, which was approximately 190 W.

(게재일: 2015.08.31)
Rhodamine염료는 높은 흡광계수와 함께 넓은 가시광선 영역에서 고효율과 안정성을 나타내는 형광을 제공함으로써 형광표지 물질로 널리 사용되고 있다. Rhodamine 화합물을 형광표지 물질로 이용하기 위해서는 rhodamine골격을 (생체)분자나 표면에 공유결합 시키는 화학적 과정이 필수적이기 때문에 이에 관련하여 다양한 rhodamine유도체를 합성해내는 효율적이고 실제적인 방법의 개발은 큰 관심을 끌어왔다. Sulforhodamine B는 반응성이 큰 두 개의 sulfoxy작용기를 포함하고 있는데 이를 이용하여 여러 재료에 공유결합 시킴으로써 널리 활용될 수 있는 유용한 화합물이다. 본 연구에서는 4-formyl-1, 3-benzenedisulfonic acid의 disodium염과 3-diethylaminophenol으로부터 3단계에 걸쳐 sulforhodamine B를 합성하는 과정을 연구하였다. 이 과정에서 dihydroxytriarylmethane 중간체를 xanthene 골격으로 전환하는 두 번째 단계를 획기적으로 개선하는 방법에 대해 기술하였다. 이는 반응 중에 생성되는 물분자가 역반응에 참여하는 것을 억제하도록 메탄올을 가함으로써 이루어졌다. 그 결과, 반응온도는 낮아지고(135에서 80 ℃), 수율은 크게 증가되었다(20% 미만에서 84%). 이로써, 기존의 3단계에 걸친 sulforhodamine B의 제법은 에너지 절감 및 자원효율 면에서 개선된 방법으로 이루어지게 되었다.

Rhodamine dyes are widely used as fluorescent probes because of their excellent photophysical properties, such as high extinction coefficients, excellent quantum yields, great photostability, relatively long emission wavelengths. A great synthetic effort has been focused on developing efficient and practical procedures to prepare rhodamine derivatives, because for most applications the probe must be covalently linked to another (bio)molecule or surface. Sulforhodamine B is one of the most used rhodamine dyes for this purpose, because it carries two sulfoxy functions which can be easily utilized for binding with other molecules. Recently, we needed an expedient, practical synthesis of sulforhodamine derivatives. We found the existing procedure for obtaining those compounds unsatisfactory, particularly, with the cyclization process of the dihydroxytriarylmethane (1) to produce the corresponding xanthene derivative (2). We report here our findings, which represent modification of the existing literature procedure and provide access to the corresponding xanthene derivative (2) in a high yield. Use of methanol as a co-solvent was found quite effective to prohibit the water molecule produced during the cyclization reaction from retro-cyclizing back to the starting dihydroxytriarylmethane and the yield of the cyclization was increased (up to 84% from less than 20%). The reaction temperature was significantly lowered (80 vs. 135 ℃). Thus, the reaction proceeds in a higher yield and energy-saving manner where the use of reactants and the production of chemical wastes is minimized.

(게재일: 2015.06.30)
황화수소와 암모니아는 많은 하수처리장과 산업 플랜트로부터의 배출가스에서 발견되어질 수 있는 가장 흔한 악취성분이다. 이들 유해물질들은 인간에게 건강 문제를 일으키고 촉매에 악영향을 미치기 때문에 생활환경과 산업 현장에서의 제거는 매우 중요하다. 본 연구에서는 황화수소와 암모니아에 대한 우수한 흡착능력을 가지는 흡착제를 개발하기 위하여 폐타이어의 열분해 생성물인 카본블랙을 이용하였다. 카본블랙, 금속산화물과 산 또는 염기를 혼합하여 펠렛형 흡착제를 제조하였고, 상온상압에서 고정층 흡착탑의 파과곡선을 이용하여 황화수소와 암모니아에 대한 흡착성능을 평가하였다. 카본블랙, 산화철(III)과 수산화나트륨 혼합물로 제조된 흡착제가 황화수소에 대한 가장 우수한 작업능력을 나타내었다. 암모니아에 대해서는 카본블랙, 산화구리(II), 염산의 혼합물로 제조된 흡착제가 우수한 작업능력을 보였다.

Hydrogen sulfide and ammonia are one of the common malodorous compounds that can be found in emissions from many sewages treatment plants and industrial plants. Therefore, removing these harmful gases from emissions is of significance in both life and industry because they can cause health problems to human and detrimental effects on the catalysts. In this work, pyrolytic carbon blacks from waste tires were used to develop adsorbent with good adsorption capacity for removal of hydrogen and ammonia. Pellet-type adsorbents were prepared by a mixture of carbon black, metal oxide and sodium hydroxide or hydrochloric acid, and their adsorption capacities were estimated by using breakthrough curve of a continuous fixed bed adsorption column at ambient condition. The adsorbent manufactured with a mixture of carbon black, iron oxide(III) and sodium hydroxide showed the maximum working capacity of hydrogen sulfide. For ammonia, maximum working capacity was obtained by the adsorbent manufactured with a mixture of carbon black, copper oxide(II) and hydrochloric acid.

(게재일: 2015.06.30)
본 연구는 LNT (lean NOx trap)용 DeNOx 촉매를 개발하기 위해 시도하였다. 이를 위해서 예비실험을 통해 Pt등 귀금속류등의 PGM (platinum group metal)을 사용하지 않는 4개의 촉매, Al/Co/Mn, Al/Co/Ni/Mn, Al/Co/Mn/Ca, Al/Co/Ni 혼합 금속 산화물을 선정하였다. 또한, 이들의 물리화학적인 성질을 평가하기 위해 XRD, EDS, SEM, BET 및 TPD test를 실시하였다. 이러한 평가를 실시한 결과, 4종의 촉매들은 스피넬(spinel)구조를 가지는 결정으로 이루어졌으며 NOx 기체들의 산화-환원 반응이 이루어지기에는 충분한 기공부피와 기공크기를 갖고 있음을 알 수 있었다. 또한, TPD test를 통해서는 산화-환원이 일어날 수 있는 산점을 4종의 촉매가 모두 가지고 있음을 확인하였다. 더욱이 ramp test를 통해서는 상용(commercial) 촉매와 비슷한 NO 산화 능력을 가지고 있는 것도 확인할 수 있었다. 이상의 결과들을 바탕으로, 본 연구에서 선정된 촉매들을 기본으로 하여 조성성분의 변화 및 활성 성분 첨가 등을 한다면, 보다 개선된 LNT용 DeNOx 촉매를 얻을 수 있을 것이라 기대할 수 있었다.

This inquiry was conducted to develop DeNOx catalyst for LNT. In order to develop appropriate catalysts, four catalysts, which do not use PGM (Platinum Group Metal), were carefully selected : Al/Co/Mn, Al/Co/Ni/Mn, Al/Co/Mn/Ca, Al/Co/Ni mixed metal oxides during preliminary experiments. Also, XRD, EDS, SEM, BET and TPD tests were carried as well to evaluate both physicochemical properties of such four catalysts. As a result of the experiment, four catalysts were composed of spinel-shaped crystals and had more than enough pore volume and size to have oxidation-reduction reaction of NOx gases. Additionally, through TPD test, all four types of catalysts were proved to possibly have an oxidation-reduction acid site and NO oxidation activities similar to commercial catalysts. Based on the results above, if we have further change in the composition components and active ingredients according to the catalysts that were chosen in this investigation, then we are more welcomed to expect to have an enhanced DeNox catalyst for LNT.

(게재일: 2015.06.30)
본 연구에서는 5~30 bar의 이산화탄소에 대한 DMPEG250 (dimethyl ether of polyethylene glycol), DEC (diethyl carbonate), DMC (dimethyl carbonate), 그리고 TAT (triacetin)의 용해도를 측정하기 위해 일정 부피법에 따른 용해도 측정 장치를 사용하였다. 이들에 대한 이산화탄소 용해도는 측정된 부피와 압력을 Peng-Robinson 방정식에 대입하여 얻은 이산화탄소의 몰수로부터 얻어졌다. 이산화탄소에 대한 물리 흡수제의 용해도는 같은 온도에 대해 DMPEG250 > TAT > DEC > DMC 순으로 나타났다. DMPEG250에 DEC를 혼합한 물리 흡수제를 사용할 경우 이산화탄소에 대한 용해도는 DMPEG250 단독에 의한 경우보다 높은 값을 가지는 것으로 확인되었다. 그러므로 DEC가 혼합된 DMPEG250/DEC 혼합 물리 흡수제는 기존의 DMPEG250이 가지는 높은 비용을 절감할 수 있을 뿐 아니라 용해도 향상까지 거둘 수 있어 향후 연소 후 이산화탄소 포집 공정에 효과적인 적용을 기대할 수 있다.

The constant-volume method was used to determine the solubility of CO in various physical absorbents such as DMPEG (dimethyl ether of polyethylene glycol), DEC (diethyl carbonate), DMC (dimethyl carbonate), and TAT (triacetin) in the total pressure range from 5 to 30 bar. The Peng-Robinson equation of state has been used to describe the equilibrium behavior of these mixtures. It was found that the solubility of absorbents was in the of DMPEG250 > TAT > DEC > DMC at the same temperature. Futhermore, the solubiity of blended absorbent of DMPEG250 and DEC is higher than that of DMPEG 250 alone. Therefore, blended absorbent of DMPEG250 and DEC is expected to be an effective and low cost absorbent for physical absorption in precombustion CO capture.

(게재일: 2015.06.30)
다양한 전자부품에 활용되는 금속 잉크 기술은 전자부품산업의 주요 기술로 자리매김하였으며 이에 대한 연구 개발이 점차 증가하고 있다. 그 중에서 실버 잉크는 뛰어난 전도성과 안정성을 가지고 있어서 전자부품산업에 오랫동안 이용되어 왔으며 최근에는 입자 크기를 나노 크기로 분산시킨 실버 나노 잉크를 개발하여 디스플레이, 전자태그, 반도체와 연성회로 기판 등에 사용되는 전자소재로써 각광받고 있다. 그러나 이러한 전자산업기기의 첨단화는 제품의 생산량과 소비량을 증가시켜 제조 공정 중에 발생되는 환경오염 물질과 사용하고 버려지는 제품들에 의해 심각한 환경 문제를 가져올 것으로 예상된다. 따라서 본 연구에서는 습식환원법에 의해 제조된 실버나노 잉크의 제조 공정이 환경에 미치는 영향을 전과정평가(life cycle assessment, LCA) 기법을 이용하여 평가하였다. 전과정 평가 소프트웨어로는 GaBi 6를 사용하였고, 유관기관으로부터 받은 실버 나노 잉크의 제조 공정 데이터를 참고하여, 인벤토리를 구축하였으며 전과정목록분석(international organization for standardization, ISO) 14040, 14044 규격의 4단계에 걸쳐 LCA를 수행하였다.

Utilized in a variety of electronic components, electronic components industry with metallic ink technology was established itself as a major technology research and development was gradually increasing, silver ink that is excellent in conductivity and stability, have long been used in the industry of electronic components in recent years and silver ink has been the size of nanoscale particles dispersed by developing display, an electronic tag, a flexible circuit board or the like used in the semiconductor and electronics as has been highlighted in, however industry modernization of equipment by increasing the production and consumption of products generated during the production process and environmental pollutants by use of waste products is expected to bring a serious environmental problem. In this study, prepared by a wet reduction method, the manufacturing process of the silver nano-ink to the entire process of the environmental impact assessment (LCA) was evaluated using the techniques. Life cycle assessment software GaBi 6 was used as received from the relevant agencies of the silver nano-ink data with reference to the manufacturing process, building inventory was international organization for standardization (ISO) 14040, 14044 compliant LCA conducted over four stages.

(게재일: 2015.06.30)
디지털 미세유체 전기천공 시스템을 활용하여 미세녹조류에 대한 형질전환 실험을 통해 기존 상용화 장치 대비 높은 유전자 전달 효율과 세포 생존도를 확인하였다. 전기천공의 주요 파라미터인 인가전압 및 인가시간 변화를 주며 세포벽이 존재하는 세포종과 세포벽이 없는 세포종에 대한 비교 실험을 수행하였다. 이를 통해 식물 세포의 전기천공에서 세포벽의 역할은 단순히 유전체의 전달을 방해하는 부정적 요소로만 작용하지 않는 다는 사실을 확인하였다. 병렬화 및 온 칩 세포 배양 등을 통해 제안된 디지털 전기천공 기술이 향후 새로운 청정 형질전환 방법으로써의 가능성도 확인하였다.

Digital microfluidic electroporation system was used for the transformation of microalgae and we have obtained higher transformation efficiency and viability than that of conventional method. Key parameters of electroporation such as pulse voltage, number, and duration time were systematically investigated for two different microalgal strains with and without cell wall. We have found that cell wall does not always have negative effects on the gene transformation of microalgae. Parallel processing of proposed digital microfluidic electroporation was demonstrated together with on chip culture of microalgae.

(게재일: 2015.06.30)