본 실험에서는 NIMAX재료를 3차원 측정기 및 백색광간섭계를 이용, 진원도 측정과 표면조도 측정을 하여 다음과 같은 결과를 얻었다. 절삭특성은 재료의 경도가 큰 관계로 2F의 조건보다 4F의 조건에서 낮게 나타났으며, 주축 회전수 및 공구 이송이 낮을수록 양호하게 나타났다. 3차원 측정기를 통한 진원도 측정은 절삭분력과 같은 4F 조건에서 양호하게 나타났으며, 주축회전수 1,700 rpm, 공구이송속도 85 mm/min의 조건에서 진원도는 양호한 결과를 보였다. 가공면의 표면거칠기는 2F 조건보다 4F의 조건에서 양호하게 나타났으며, 주축회전수 1,700 rpm, 공구이송속도 55 mm/min의 조건에서 Ra 값을 보였다.

In this study, NIMAX material has been processed using the three-dimensional measuring instrument and white light interferometer. they were tested to roundness and surface roughness and results are as follows: As for a cutting characteristic, it indicated that F4 showed a lower result than 2F showed due to the high hardness of the material and showed a good result when spindle rotation speed and tool feed were low. As for the measurement of roundness through 3-Dimensional measuring machine, it indicated that 4F showed a good result like the condition of cutting component and that roundness showed a good result when spindle rotation speed of 1,700 rpm and tool feed speed of 85 mm/min were applied. As for the surface roughness of processing surface, Surface roughness showed better 4F than 2F and conditions of spindle rotation speed 1,700 rpm, tool feed rate 55 mm/min showed good results in the Ra .

(게재일: 2013.02.28)
철강 생산 제품 중 강선 (steel wire rod)은 제조 과정 중 종방향으로 미세한 표면 결함이 매우 빈번하게 발생하는데 이중 깊이가 수 십 마이크로미터 이상인 결함들은 최종 생산품의 불량을 유발하는 심각한 원인이 되고 있다. 이와 같은 이유로 강선의 제조 단계에서 표면의 미세 결함의 깊이를 평가하는 방법의 개발이 절실히 요구된다. 표면 미세 결함을 평가할 수 있는 여러 가지 방법 중에서, 본 연구에서는, 전자기 음향공진법의 적용 가능성을 고찰하고자 한다. 전자기 음향 공진 (electromagnetic acoustic resonance, EMAR)은 전자기 음향 트랜스듀서 (electromagnetic acoustic transducer, EMAT)을 이용하여 시편의 공진 특성을 측정하는 방법으로서, 대상의 작은 변화에도 민감하게 반응하고 비접촉 측정이 가능하여 현장 적용에 용이하다는 장점이 있다. 전자기 음향 공진 실험을 통하여 표면 미세결함과 잔향특성의 변화를 관찰하여 깊이 약 100 마이크로미터 내외의 결함은 탐상 가능함을 확인하였다.

The surface microcrack over a few tens of micrometers is one of severe problems of a steel wire rod to lead to the failure of the final products, so the method to evaluate crack depth has been required to develop. This work investigates the feasibility of electromagnetic acoustic resonance (EMAR) for this problem. EMAR is the method for measurement of resonant features using electromagnetic acoustic transducer (EMAT). Generally, EMAR is sensitive to small variation of the structures and easy to apply it to the industrial field because of the feature of noncontact measurement. Through several EMAR experiments, the change of the resonant frequencies and attenuation in reverberation has been observed. The results confirms that the surface cracks of around 100 micrometer depth can be detected successfully with the present method.

(게재일: 2013.02.28)
열화 정도를 예측하기 위한 비파괴기법으로 초음파기법이 널리 적용되고 있다. 초음파 속도와 감쇠 특성은 일반적으로 금속재료의 물성 변화에 따라 변화하기 때문에 초음파 속도와 감쇠 특성을 이용하여 금속재료의 열화 정도를 간접적으로 예측할 수 있다. 따라서, 본 연구에서는 반복하중으로 인하여 피로파괴 발생 가능성이 높은 볼트, 리벳 접합의 구조용재 및 선박 차량에 사용되고 있는 Al6061-T6을 피로수명의 0%, 55%, 70%, 85%인 시험편을 제작하였고, 가공된 시험편의 감쇠 특성을 이용하여 측정된 열화 이미지로 Al6061-T6의 건전부와 열화부를 판단하였으며, 건전부와 열화부의 감쇠 특성 차이를 계산하여 Al6061-T6의 열화 진행 정도를 평가하였다.

Ultrasonic methods are widely used to degradation assessment. Remaining-life cycle of metal can be estimated by ultrasonic parameters because ultrasonic velocity and attenuation are affected by change of material properties with accumulated fatigue in the metal. Therefore, in this study, we will estimate overall change of material properties by 2D C-scan image. Fatigued aluminum alloy 6061-T6 samples from 0 to 85% were prepared for evaluating fatigue life cycle. Also, degraded image of materials using attenuation is proposed to estimate degree of material degradation for determining degraded area of fatigued samples. Finally, we will predicts process pf degradation with measured attenuation of fatigued aluminum alloy 6061-T6 samples.

(게재일: 2013.02.28)
원자로 BMI 노즐은 원자력발전 설비의 운영을 위한 핵심요소 중 하나이며 하부헤드에 설치되어 있다. 상부헤드에 비해 비교적 저온영역에 있지만 최근 외국사례에 비추어 볼 때 PWSCC의 발생 가능성이 크기 때문에 가동중 비파괴검사가 반드시 필요하다. 그러나 BMI 노즐은 원자로 하부에 있기 때문에 고방사선 구역이며 원자로 내부는 붕산수로 채워져 있기 때문에 접근이 매우 어렵다. 본 연구에서 BMI 노즐 검사를 위하여 TOFD를 이용한 탐촉자를 개발하였고, 자동화검사를 위해 내방수 기능을 가진 스캐너를 개발하였다. 또한, BMI 노즐과 동일한 재질 및 형상으로 인공결함시험편을 제작하여 자동화 비파괴검사 시스템의 성능검증을 수행하였다.

BMI nozzles in bottom head of the nuclear vessel are one of major components in nuclear power plants. The BMI nozzles have high possibility to generate PWSCC(primary water stress corrosion crack) according to recent foreign case although operation temperature is lower then the upper head of the nuclear vessel. Thus, nondestructive inspection of the BMI nozzles is required. But, inspection of BMI nozzles is not easy since the BMI nozzles placed in high radiated area and inside the nozzles filled with boric acid. Thus, in this study, a TOFD transducer for inspection of BMI and automated scanner system with water were developed. Also, validation of performance of the developed transducer and system are performed using specimens with artificial defects.

(게재일: 2013.02.28)
선행 연구에서 적외선열화상기법을 이용하여 원전 배관의 감육 결함을 측정하기 위하여, 4 inch 배관에 인공결함을 가공하여 이에 대한 결함 검출을 도출하였다. 본 논문에서는 선행연구에서 도출된 조건을 이용하여 원전 소구경 배관의 결함 검출 조건에 관한 연구를 수행하였다. 결함의 가공은 감육 길이, 원주방향 각도, 감육 깊이를 변화시켜서 결함 조건을 가공하였다. 사용된 장비는 IR camera와 1 kW용량의 halogen lamp 2개를 사용하였으며, halogen lamp와 대상 배관과의 거리를 1 m, 1.5 m, 2 m 순으로 변화시켜 실험을 수행하였다. 실험 결과의 분석을 위하여 온도분포데이터를 확보하고, 이를 분석하여 결함 길이를 측정하였다. 4 inch 배관의 인공결함은 2 m에서 측정 결과의 신뢰도가 높았으나, 소구경 배관은 1.5 m에서 결함이 명확하게 검출되었다.

In the advanced research deducted infrared thermography (IRT) test using 4 inch pipe with artificial wall-thinning defect to measure on the wall-thinned nuclear pipe components. This study conducted for defect detection condition of nuclear small-bore pipe research using deducted condition in the advanced research. Defect process is processed by change for defect length, circumferential direction angle, wall-thinning depth. In the used equipment IR camera and two halogen lamps, whose full power capacitany is 1 kW, halogen lamps and Target pipe experiment performed to the distance of the changed 1 m, 1.5 m, 2 m. To analysis of the experimental results ensure for the temperature distribution data, by this data measure for defect length. artificial defect of 4 inch pipe is high reliability in the 2 m, but small-bore pipe is in the 1.5 m from the defect clearly was detected.

(게재일: 2013.02.28)
위상잠금 적외선열화상기법을 이용하여 치과용 복합레진 수복재의 내부 홀 결함 크기에 따른 검출 가능성을 연구하였다 위상잠금 주파수 조건을 다르게 하며 진폭과 위상영상을 분석하였다. 진폭 이미지 분석을 통해 직경 2 mm 이상의 결함 검출이 가능함을 알았으며 0.05 Hz 부근에서 결함부의 구별이 뚜렷하고 선명한 이미지를 획득할 수 있었다. 진폭 대비차는 결함부의 직경 크기에 비례하였다. 위상 이미지 분석 결과 0.3-0.5 Hz 부근에서 최적의 대조 영상을 보였으며 0.006 Hz 에서는 반대 명암의 뚜렷한 이미지를 얻을 수 있었다. 진폭 분석보다 위상 분석에서 결함부 크기가 작은 시편의 검출 가능성이 더 높았다.

The purpose of this study was to detect the pin hole defect of dental composite restoration using lock-in thermography method. Amplitude and phase images of the composite resin specimens were analyzed according to the lock-in frequency and the diameter of defect area. Through the amplitude image analysis, at lock-in frequency of 0.05 Hz, defect diameters 2-5 mm exhibited the highest amplitude contrast value between defective area and sound area. The lock-in frequency range of 0.3-0.5 Hz provided good phase angle contrast for the defect area. At lock-in frequency range of 0.5 Hz, defect diameter of 5 mm exhibited the highest phase contrast value. It is concluded that the infrared lock-in thermography method verified the effectiveness for detecting the pin hole defect of dental composite restoration.

(게재일: 2013.02.28)
최근 고추재배에 있어 CMV-P1감염은 상품성 저하와 생산량 감수를 발생시키는 매우 심각한 문제이다. 본 실험에서는 역병 저항성 품종인 PR계통을 포함한 국내 시판 56품종과 미국에서 도입해 온 31품종 도입자원 및 농촌진흥청 유전자원센터(RDA Genebank)로부터 받은 112개의 고추 유전자원을 CMV-P1 저항성 검정에 사용하였다. 저항성 검정은 인공 접종 후 24일 후와 51일 후 ELISA를 실시하였다. 36개 시판품종 중 '무한질주' 품종이 CMV-P1에 저항성이었다. 모든 PR품종과 중도저항성인 'NuMex Twilight'와 'Chainese Giant'를 제외한 29개 외국 도입고추는 감수성이었다. RDA Genebank의 112계통의 고추 유전자원에서는 저항성 계통이 9, 중도저항성을 나타내는 계통이 17, 나머지 86계통은 모두 감수성으로 조사되었다. 국내 시판 고추품종은 거의 CMV-P1에 높은 감수성을 보이는 것으로 확인되는 반면, 외국 도입자원과 유전자원의 17.2%가 저항성이거나 중도저항성으로 확인되었다. 본 연구 결과로 확인된 저항성 고추는 CMV-P1 저항성 고추육종에 유용한 유전자원으로 이용될 수 있다.

Recently, Cucumber mosaic virus (CMV)-P1 infection in pepper cultivation is very serious problem, which causes low marketability and yield. In this research, 56 domestic pepper cultivars including 20 PR (Phytophthora resistance) cultivars, 31 foreign pepper lines collected from USA and 112 genetic pepper resources form RDA Genebank were used for CMV-P1 resistance evaluation. Resistance evaluation was performed at 24 days and 51 days after artificial inoculation of peppers by enzyme-linked immunosorbent assay (ELISA). Among the 36 domestic cultivars 'Muhanjilju' were resistant to CMV-P1. All 20 PR cultivars and 29 foreign peppers except 'NuMex Twilight' and 'Chainese Giant' were susceptible. Among 112 pepper lines from RDA Genebank, nine pepper lines were resistant, and 17 pepper lines were moderately resistant, and 86 pepper lines were susceptible. Almost all domestic peppers on the market were highly susceptible to CMV-P1, whereas 17.2% of foreign pepper cultivars and genetic pepper lines from RDA Genebank were resistant or moderately resistant. Resistant pepper lines selected in this study can be used as genetic sources for breeding CMV-P1 resistant pepper.

(게재일: 2013.12.31)
냉매의 비등이나 응축같은 열전달 향상을 위하여 금속 표면위에 탄소나노튜브(CNT)를 코팅하는 것을 연구하였다. 다중벽 탄소나노튜브/구리 복합소재는 어트리션 볼밀에 의해서 제작되었으며, 정전 도장 장치로 복합 분말을 구리 기판위에 코팅한 후 전기로에서 소결하였다. 본 논문에서는 CNT/Cu 코팅 표면의 분석 및 소결전후의 탄소나노튜브의 변화를 파악하기 위하여 샘플들을 주사전자현미경, EDAX, 라만분광법에 의해 분석하였다. 아울러 열전달 촉진은 비등열전달로 확인하였다.

The coating of metal surface with carbon nanotubes (CNTs) has been studied for the heat transfer enhancement of the boiling and condensation of refrigerant. The MWCNT/copper composite powder was made by the attrition ball milling, which has been coated on the copper wafer by electrostatic powder coating and sintered with electric furnace. In this paper, experiments were performed to assess the characterization and comparison of CNT before and after sinterning and the morphology changes of the CNT/Cu-coated surface. The samples were examined by the scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDAX) and raman spectroscopy. To verify the heat transfer enhancement, boiling heat transfer tests were performed.

(게재일: 2013.12.31)
나노입자를 이용하여 강화 효과를 높이기 위해서는 고분자 기지 내부의 균일한 분산 상태를 확보하여야 한다. 또한 균일분산 조건 확보 후 균일 분산상태를 증명할 평가자료가 필요하다. 본 연구는 에폭시 수지와 SiC 나노입자를 혼합한 SiC/에폭시 복합 수지를 제조할 경우 커패시턴스 측정법을 이용한 강화재 분산도 예측 연구를 진행하였다. 커패시턴스는 전기용량을 의미하며 측정 재료의 내부 전하량과 비례한다. 기존 에폭시 수지에 비해 나노 SiC 입자를 함유할 경우 전하량이 증가되는 이론을 바탕으로 구간별 커패시턴스 측정에 따른 분산도 평가를 진행하고, 커패시턴스 분산도 예측방법에 대한 타당성을 FE-SEM과 물리적 강도 증가 방법으로 평가하였다. 소니케이션 분산 방법과 교반기 분산 방법을 이용하여 분산 방법에 따른 SiC 나노입자 분산도 상태를 비교하였다. 인장강도와 커패시턴스 간의 상관관계가 있었으며, 파단면에 대한 비교를 할 때 분산성 향상에 대한 차이를 확인할 수 있었다.

The good dispersion of nano-materials in epoxy matrix was important parameter for the reinforcement effect, and the evaluation of dispersion degree was to prove it. This work was studied to predict the dispersion condition of nano-SiC powders in SiC/epoxy composites using capacitance measurement. Capacitance was defined to be the electric capacity in proportional to electron charge of the measuring section. In case of nano-SiC powders, the electron charge of SiC/epoxy composites was higher than that of neat epoxy resin. Capacitance was evaluated for each section of SiC/epoxy composites. The prediction of dispersion condition was verified by using capacitance measurement. Dispersion condition of nano-SiC powders in epoxy matrix was evaluated with two different dispersion methods, i.e., sonication and stirring methods. The dispersion degree was also verified with the tensile strength correlating to capacitance.

(게재일: 2013.12.31)
조류 발생이 문제시 되는 정체수역이나 호소에서 현장적용에 적합한 응집제를 선정하고 응집제별 적정 주입농도를 찾기 위하여 황토와 개량된 토양기반 무기응집제 세 가지(AC-A, AC-B, AC-C)를 주입하며 응집 침전실험을 실시하였다. 남조류가 주종이고 조류밀도가 2,950 cells/mL인 원수에 대한 황토(50 mg/L 주입)에 의한 조류밀도 제거율은 10분 침전후 49%, 30분 침전후 85%로 나타났고, 다른 세 가지 무기응집제(20 mg/L 주입)의 경우 10분 침전 후 80-90% 제거율, 30분 침전 후에는 89-94%의 조류 제거율을 나타냈다. 조류 제거와 탁도, pH 등의 수질인자 특성을 종합적으로 고려할 때 본 연구에서 고려된 천연 무기응집제 중 AC-A가 가장 적합한 것으로 판단된다. 원수의 조류밀도가 높을수록 같은 제거효율을 얻기 위한 응집제 주입량이 증가하는 경향을 나타냈으나 선형적인 상관관계는 찾을 수 없었다. 황토를 비롯한 천연 무기응집제는 원수의 유기물 제거 및 pH 변화에는 큰 영향을 미치지 않는 것으로 나타났고, 인산염의 경우 주입량을 늘임에 따라 제거율이 높아져 최대 70%까지 제거되었다.

Coagulation and sedimentation tests were conducted with clay and three different coagulants of soil origin (AC-A, AC-B, AC-C) to determine optimal coagulant types and doses to remove algae in stagnant water bodies such as reservoirs. Raw water had an algal density of 2,950 cells/mL and was dominated by Cyanobacteria. Removal rates of algal density by clay (50 mg/L) were 49% and 85% after 10 and 30 minutes sedimentation, respectively. Other natural coagulants achieved 80-90% removal in 10 minutes and 89-94% removal in 30 minutes of sedimentation after adding 20 mg/L each. AC-A was the optimal coagulant from this study considering algal removal rates and other water quality parameters such as turbidity and pH. For the same removal rates of algae, raw waters with higher algal densities required higher coagulant doses although no strong corelation was observed. The coagulants of soil origin did not impact orgnic contents and pH of raw water, but remove phosphate up to 70%.

(게재일: 2013.12.30)
담수생태계에서 갈수기가 지속되면 다양한 물리적 장애가 발생한다. 이 시기는 어류의 생태 유지용수가 부족하여, 이동이 일어남에 따라 새로운 피난처 및 서식처가 요구된다. 이러한 문제를 해결하기 위해 본 연구에서는 실증규모의 실험시설을 구축하였으며, 수위변화와 어류 피난처의 관계를 분석하였다. ADP (artificial deep pool)는 본 연구에서 제안된 인공적인 깊은 웅덩이이다. 본 시설을 실증규모의 test-bed 실험구에 적용하여 모니터링 한 결과, 수위변화에 따른 어류 개체수는 실험연못의 수심 0.5 m에서 가장 높게 나타났다. 하지만 ADP에서는 낮은 외부 수위 조건(<0.3 m)에서 단위면적당 어류 개체수가 증가하였고, 실험구의 총 어류 군집을 보존하는데 기여하였다. 또한, ADP 내부의 수온과 DO는 외부보다 낮게 조성되었지만, 어류는 지속적으로 서식하였다. 이 결과와 관련하여, ADP 내부는 WCS, OS, SS, TS 등이 높은 효율적인 정수생태계임을 나타내었다. 더욱이, ADP 내부의 종풍부도는 Acheilognathus koreensis (A. koreensis), Carassius carassius (C. carassius)와 같은 WCS가 높은 비율로 측정되었다. 결국, 수위가 낮게 형성되는 동안 어류는 서식환경의 교란에 의해 수심이 깊은 곳으로 피난하였고, 본 연구 결과를 종합하여 볼 때, ADP는 정수생태계에 적합한 어류 피난 및 서식처로 활용이 가능함을 시사하였다.

Physical disturbance, which induces a lack of flow rate, frequently occurs in freshwater ecosystem. Due to this, it is required to provide a new fish shelter to resolve. We installed a pilot scale test-bed to scrutinize the relationship between water level and the influence of fish shelter. The proposed ADP (artificial deep pool) is a fish shelter which composed of concrete materials. From the monitoring results in test-bed, it was observed that the population of fish was the highest at the 0.5 m in depth from the water level of experimental pond. But it was more appropriate for shallow water level (<0.3 m) to conserve the total number of fish by increasing the number per unit area despite of lower inner temperature and DO than outer environment. Therefore, inner of ADP was more efficient lentic system for fish to live due to higher WCS, OS, SS, and TS. In addition, there was a relative abundance of WCS fish species such as Acheilognathus koreensis (A. koreensis), Carassius carassius (C. carassius). Considered these results, it is suggested that ADP is appropriate to use for fish shelter and habitat for the fishes in lentic ecosystem.

(게재일: 2013.09.30)
물속의 색도 측정방법에는 비색법과 분광학적방법이 있다. 비색법은 농도가 알려진 백금-코발트 표준용액과 시료의 색을 비교하여 색도를 측정하는 방법이며 분광학적 색도 측정방법은 단일 또는 다중파장을 선택하여 색도를 측정하는 방법이다. 그러나 비색법의 경우, 분석자의 시력에 의한 단순 비교를 통해 색도를 측정하는 방법으로 측정결과의 신뢰성과 재현성이 우수하지 못할 뿐만 아니라 5 TCU 이하의 색도 측정이 불가능하다. 분광학적 색도 측정방법 중 단일파장법은 주로 색도 성분이 천연유기물질(휴믹물질)인 지표수나 지하수에만 적용이 가능한 것으로 나타났으며 하수와 같이 인위적인 화학적 색도 성분이 함유될 경우 색도 측정이 불가능하였다. 다중파장법은 지표수, 하수 등 다양한 시료에 대해 우수한 색도 측정결과를 나타냈으나 1개의 시료에 대해 수십 번의 측정과 복잡한 계산으로 실제 현장 적용에 어려움이 있었다. 따라서 본 연구에서는 지표수, 정수, 하수 등 다양한 시료에 대해 신속하고 정확한 색도 측정방법을 비교하였다. 그 결과, 다중파장 프로그램이 내장되어 3~4초 이내에 지표수, 하수 등 다양한 시료에 대해 신속하고 정확하게 색도 측정이 가능한 색도계 색도 측정방법이 가장 적합한 것으로 나타났다.

There are two approaches in measuring colors (or chromaticity) in water, i.e., visual comparison method and spectrophotometric method. The color of sample was determined by comparing with that of platinum-cobalt standard solution in the visual comparison method. Single or multiple wavelengths are used for the spectrophotometric method. As the accuracy and precision of visual comparison method depend on the eye sight of the analyzer, the results are not so reliable and representative. In addition, it is hard to measure chromaticity less than 5 TCU. Single wavelength approach in spectrophotometric method, can be applied for groundwater or surface water with natural organic matter (i.e., humic substances) while it's hard to measure the color of wastewater which includes anthropogenic chemical compounds. The measurements with multiple wavelengths approach resulted in reliable data regardless of the source of sample water, i.e., surface water and wastewater. As dozens of measurements and complicated calculations for one sample were required for the multiple wavelengths approach, the approach could not be applied for field measurement. In the present study, the authors tested efficient method which could measure the color of water sample accurately and precisely regardless of the source of water. With the colorimeter with multiple wavelengths and calculation program, the colors of water samples could be measured within 3~4 seconds with accuracy and precision.

(게재일: 2013.06.30)
소규모 하수처리시스템에 다양한 반송비와 고정식 담체를 적용하여 합성폐수에서 질소, 인의 제거를 검토하였다. 담체를 첨가 시 질소의 제거율은 40.1%에서 65.1%로 증가하였으나 COD와 인의 제거에는 영향이 없었다(<5%). 반송을 통해 유량을 2배(2Q)로 증가시킨 경우 질소의 제거율은 7% 정도가 증가하였으나, 인 제거율은 반송비가 증가됨에 따라 31.8에서 26.6%로 감소하였다. 무산소조에서 담체에 부착된 미생물은 약 73.4 로 존재하였으며, FISH분석 결과 탈질 미생물인 Pseudomonas aeruginosa 존재 (약 58%)를 확인하였다.

The effect of recycling ratio and fixed media on nitrate and phosphate removal was investigated in a pilot-scale wastewater treatment unit using synthetic wastewater. Addition of fixed media increased nitrate removal from 45 to 58% while no noticeable change was observed for Chemical Oxygen Demand (COD) and phosphate removal (<5%). Nitrate removal efficiency also enhanced (Ca 7%) when the influent wastewater flow was doubled (2Q), however phosphate removal was decreased from 40.9 to 26.6% with the increasing recycling rate. The attached biomass analysis showed the presence of bacteria (73.4 ) on the surface of added media in anoxic reactor. Pseudomonas aeruginosa a common denitrifying bacterium dominated the bacterial growth (58%) in the anoxic reactor which was determined using Fluorescence In Situ Hybridization (FISH) analysis.

(게재일: 2013.06.30)
낙동강 하류 물금지역의 장기적인 부영양화 경향을 평가하기 위해 1995년부터 2012년까지 수질인자들 및 식물 플랑크톤 생체량(클로로필-a 농도)들의 변화경향을 조사하였다. 18년간의 장기적인 연평균 수질인자들 농도 및 식물 플랑크톤 생체량 변화에서 연평균 수질인자들 농도 및 식물 플랑크톤 생체량은 점차 감소하는 추세였다. 연중 식물 플랑크톤의 농도변화에서는 매년 12월부터 3월까지 높은 식물 플랑크톤의 농도를 나타내었다. Aizaki의 부영양화 지수(Trophic State Index, TSI) 평가에서 낙동강 하류 물금지역의 경우 1995년부터 2012년까지 매년 그리고 연중 부영양화 상태인 것으로 나타났다. 각각의 수질인자들과 식물 플랑크톤 생체량과의 단순 상관관계 분석에서 BOD와 식물 플랑크톤 생체량과의 상관성( = 0.82)이 가장 높게 나타났다.

Long-term (from 1995 to 2012) data of phytoplankton biomass (chlorophyll-a, Chl-a) and water quality were analyzed to investigate trends of eutrophication in downstream of Nakdong River (Mulgum). Long-term annual average concentration of water quality parameters and phytoplankton biomass at Mulgum showed an decreasing trends for 18 years. Phytoplankton biomass was high from annually December to March. Trophic state was evaluated as the eutrophic state annually from 1995 to 2012 by TSI (trophic state index) by Aizaki. From the results of simple regression analysis, correlation coefficient between Chl-a concentration and BOD concentration was high ( = 0.82).

(게재일: 2013.04.30)
대청호의 추동과 문의수역에 설치된 수중폭기시설의 수질 개선 및 조류저감 효과를 평가하기 위하여, 폭기시설의 영향지점과 대조지점에서 시설의 가동 전 후 수질을 분석하였다. 분석 결과, 폭기지점과 대조지점에서 수심에 따른 수온 및 용존산소의 농도 차이는 거의 없었으며, 조류의 주요 성장인자인 총인과 총질소의 농도도 거의 차이가 없었다. 이러한 결과로부터 추동과 문의수역에서 폭기시설에 의한 수체 순환 및 영양염류 저감 효과가 크지 않은 것으로 판단되었다. 하절기에 심층의 총인 농도가 매우 높았으며, 이는 오염된 퇴적물로부터 용출되었거나 강우에 의해 외부로부터 유입된 것으로 판단되었다. 이 시기에 폭기시설을 가동할 경우 총인이 확산되어 조류의 성장을 촉진시킬 수 있으므로, 폭기시설의 가동 시기를 결정할 때 이를 고려하여야 한다.

To evaluate the effects of submerged aerators installed at Chudong and Muneui areas in Daechung Reservoir on improvement of water quality and reduction of algal bloom, the water quality was monitored at the effected and control areas at the time of operation. The water temperature and concentrations of dissolved oxygen, total phosphorus, and total nitrogen in depth at the effected and control areas were not different each other, indicating the submerged aerators at these areas are not effective for circulation of water body and reduction of nutrients. In warmer season, the concentrations of total phosphorus in deep water, which was probably released from contaminated sediment or inflowed from watershed, was high. To decide the operation of aerators in this season, the concentration of total phosphorus in water should be considered because the dispersed phosphorus by operation of aerators can enhance the algal growth.

(게재일: 2013.04.30)
본 연구에서는 고상 미세추출법(HS-SPME)을 적용하여 대기환경시료 중 VOCs 분석을 위한 응용성을 평가하고자 하였다. 광범위한 VOCs 검출을 위한 최적 HS-SPME 분석 조건(CAR/PDMS fiber, 30분 시료노출, 도출된 분석조건)에서 VOCs의 검출 한계 농도는 저분자량 화합물인 경우 1~3 ppbv 내외였고, BTEXs 계열 화합물들의 경우에는 0.0005 ppbv 이하의 매우 낮은 농도까지 검출 가능하였다. 다만 fiber들 간의 흡착효율 재현성 평가결과, 동일 fiber에 대하여 1~9.2% (n = 3), 서로 다른 fiber들에 대하여서는 5.9~13.5% (n = 5)의 오차를 보였다. 도출된 분석조건을 이용하여 매립지 가스 중 BTEX를 포함한 35여종의 VOCs를 성공적으로 정량분석하였다.

The purpose of this study is to quantify volatile organic compounds (VOCs) in gas sample using headspace solid-phase microextraction (HS-SPME) coupled to GC analysis. The optimal HS-SPME conditions was CAR/PDMS fiber and 30 min absorprion time for the analysis of various VOCs. In optimal conditions, 80 VOCs could be detected within 1 ppbv and even less than 0.0005 ppbv especially in the case of BTEX. However, fiber reproducibility on adsorption efficiency was 1~9.2% (between the same fiber) and 5.9~13.5% (between the other fiber). We successfully determined 35 VOCs in landfill gas with this method and found that VOCs of high concentration are emitting from vent pipe of closed/open landfill site under the HS-SPME conditions. This method may apply to VOCs/odor determination from various atmospheric environmental samples as well as landfills.

(게재일: 2013.12.30)
본 연구에서는 발포 폴리프로필렌(Expanded polypropylene)과 발포 폴리스티렌(Expanded polystyrene)의 준정적 시험(Quasi-static test) 및 계장화 충격 시험(Instrumented impact test)을 수행하였다. EPP와 EPS는 4가지의 다른 밀도에 대해 원통형 시편이 준비되었다. 준정적 시험에는 MTS 858을 사용하여 0.001 과 0.1 두 가지 변형률속도 조건으로 진행되어 결과를 분석하였다. 계장화 충격 시험에서는 Instron dynatup 9250HV를 사용하여, 각각 100 J, 200 J, 300 J의 서로 다른 충격에너지를 가했을 때의 응력-변형률 선도 결과를 비교 분석하였다.

In the present study, quasi-static tests and impact tests were performed for investigating the mechanical behaviour of EPP (Expanded polypropylene) and EPS (Expanded polystyrene). Four different density cylindrical type specimens were prepared for EPP and EPS and 0.001 and 0.1 of strain rate conditions for quasi-static tests and 100 J, 200 J and 300 J of incident energy conditions for the instrumented impact tests were considered.

(게재일: 2013.12.31)
본 논문에서는 Carbon/Epoxy 복합재 적층판에 대하여 실사격 실험을 수행하였으며, 복합재 적층판의 흡수에너지를 예측하기 위한 개선된 방법을 제시하였다. 고속충격실험 과정에서 충격체의 질량손실을 고속카메라를 통하여 거시적으로 확인하였으며, 따라서 이를 고려하여 복합재 적층판의 흡수에너지를 계산하였다. 고속충격을 받는 복합재 적층판의 흡수에너지를 예측하기 위한 모델을 제시하였으며, 복합재 적층판의 흡수에너지는 크게 정적에너지와 동적에너지로 분류하였다. 정적에너지 계산은 섬유의 파손과 정적 탄성에너지와 관련 있는 준정적 관통실험식을 통해 구한 관통에너지를 사용하였다. 동적에너지는 변형되는 시편의 운동에너지와 손실된 파편 질량들의 운동에너지로 나뉠 수 있다. 최종적으로 충격체 질량손실을 고려하여 예측된 흡수에너지와 실험결과를 비교/분석하였다.

In this paper, we conducted high velocity impact test for Carbon/Epoxy composite laminates and proposed advanced method for predicting the absorbed energy of composite laminates. During high-velocity impact test, we discovered loss of projectile mass macroscopically using high speed camera, thus we calculated the absorbed energy of composite laminates by taking loss of projectile mass into account. We proposed a model for predicting the absorbed energy of composite laminates subjected to high-velocity impact, the absorbed energy was classified into static energy and dynamic energy. The static energy was calculated by the quasi-static perforation equation that is related to the fiber breakage and static elastic energy. The dynamic energy can be divided by the kinetic energy of deformed specimen and fragment mass. Finally, the predicted absorbed energy considering loss of projectile mass was compared with experimental results.

(게재일: 2013.12.31)