# Zinc Nanoparticles at Intercrystallite Sites of (Cu0.5Tl0.5)Ba2Ca3Cu4O12−δ Superconductor

Authors: Irfan Qasim; M. Mumtaz; K. Nadeem; S. Qamar Abbas
Journal: Journal of Nanomaterials
 (2016)

---

## Abstract

We synthesizedZnx/(Cu0.5Tl0.5)Ba2Ca3Cu4O12-δ  {Znx/CuTl-1234}(x = 0~3 wt.%) nanoparticles-superconductor composites by solid-state reaction technique and examined the effects of zinc (Zn) nanoparticles on structural and superconducting properties of CuTl-1234 phase. Unaltered crystal structure of host CuTl-1234 phase confirmed the existence of Zn nanoparticles at intercrystallite sites. We observed an improvement in grains size and intergrains connectivity by healing up the voids after incorporation of Zn nanoparticles in CuTl-1234 superconductor. Superconducting properties of Znx/CuTl-1234 composites were suppressed for all Zn nanoparticles concentrations. Suppression of zero resistivity critical temperature {Tc(0)} and variation in normal state resistivity {ρ300K (Ω-cm)} were attributed to reduction of superconducting volume fractions and enhanced scattering cross section of mobile carriers.


---

## Body

## 1. Introduction

Intergrains connectivity and pinning potential are very important parameters for the enhancement of superconducting properties of bulk high temperature superconductors (HTSCs) from application point of view. Thus, it is important to engineer additional efficient connectivity enhancers in HTSCs synthesized at ambient pressure. Diverse techniques have been exercised to address these issues but one of the most convenient and effective techniques is the addition of appropriate nanosized structures (i.e., nanoparticles, nanowires, and nanorods) at grain-boundaries of bulk HTSCs. A lot of research works by many research groups were carried out but the addition of most suitable nanosized structures is still preferred for the improvement of superconducting parameters as well as efficient pinning centers. The improvement of superconducting parameters (i.e.,Tc, Hc, and Jc) by the inclusion of ZrO2 and ZnO nanoparticles in Gd-123 bulk superconducting matrix was reported [1]. The addition of ZnO and Zn0.95Mn0.05O nanoparticles in polycrystalline YBa2Cu3Oy superconductor has increased the flux pinning strength which was attributed to magnetic interaction of pinning centers via vortices [2]. The inclusion of noble metals (Ag and Au) nanoparticles has enhanced the intergrains coupling, superconducting volume fraction, and superconducting properties of CuTl-1223 phase [3, 4]. Lower concentration of ZnO nanoparticles up to x=0.8 wt.% has increased Tc(0) and further increase of these nanoparticles concentration suppressed the superconductivity of (Cu0.5Tl0.25Pb0.25)Ba2Ca2Cu3O10−δ phase [5]. Reduction of porosity and improvement in microhardness were observed after addition of SnO2 nanoparticles in (Cu0.5Tl0.5)-1223 superconducting matrix [6].The suppression of superconducting properties was observed after addition of core shell Ni/NiO nanoparticles and ZnFe2O4 nanoparticles in CuTl-1223 matrix, which was attributed to scattering/pair-breaking of carriers across these magnetic nanoparticles due to spin-interaction [7, 8]. Metallic nanoparticles (i.e., Ag, Zn, and Sn) in MgB2 superconducting matrix have enhanced Jc, which was attributed to increased intergrains connectivity [9]. Mechanical and electrical properties of (Cu0.5Tl0.5)-1223 superconducting phase added with Fe2O3 nanoparticles were studied and increase in Tc was observed with low concentration of these nanoparticles (up to x = 0.2 wt.%) followed by systematic decrease with x > 0.2 wt.% [10]. Improvement in Jc had been observed after addition of Al2O3 and NiFe2O4 nanoparticles in (Bi, Pb)-2223 superconductors, which was attributed to these nanoparticles acting as effective pinning centers [11–13]. The enhancement in superconducting properties of CuTl-based family with the addition of CaO2, BaO, and CuO nanoparticles had been already reported [14, 15].We have selected one of the most prominent phases (Cu0.5Tl0.5)Ba2Ca3Cu4O12−δ (CuTl-1234) of (Cu0.5Tl0.5)Ba2Can-1CunO2n+4−δ (CuTl-12(n-1)n), n=2, 3, 4,…, superconducting family for further investigation. We have investigated the effects of addition of nonmagnetic 3d10 Zn metallic nanoparticles on superconducting properties of CuTl-1234 phase. We have successfully inserted Zn nanoparticles in CuTl-1234 matrix and characterized the resultant Znx/CuTl-1234 nanoparticles-superconductor composites by different experimental techniques. The addition of Zn nanoparticles has changed the superconducting properties of different HTSCs [16–19]. The suppression of zero resistivity critical temperature Tc(R=0) with the nano-Zn addition is pretty surprising but may be understood on the basis of their nonuniform dispersion, pair-breaking, and scattering of charge carriers at grain-boundaries of CuTl-1234 phase [20–30]. The reproducibility of Znx/CuTl-1234 nanoparticles-superconductor composites with various concentrations (i.e., x = 0~3 wt.%) was ensured by synthesizing and characterizing these composites again and again.


## 2. Experimental Details for Sample Preparation and Characterization

We prepared Cu0.5Ba2Ca3Cu4O12−δ precursor material from Ba(NO3)2 (99.50%, UNI-Chem), Ca(NO3)2·4H2O (99%, Appli Chem), and Cu2(CN)2·H2O (99%, BDH) compounds. These compounds were mixed in appropriate ratios and were ground in mortar and pestle for 2 hours. The ground mixture was put into quartz boat and placed in furnace for 24 hours firing at 880°C. The precursor material was cooled down in furnace to room temperature after 24 hours firing at 880°C. The fired material was again ground for 1 hour and kept in furnace for second time firing under the same conditions to obtain Cu0.5Ba2Ca3Cu4O12−δ precursor material. Zn nanoparticles were synthesized by sol-gel method. Initially, one solution of Zn(NO)3 and ethanol was prepared and mixed drop by drop with second solution of citric acid and distilled water in a glass beaker with constant stirring. During the process, ammonia (NH3) was added to the final solution to raise the pH value up to 5. The solution was then heated at 80°C till gel formation. The gel was placed in oven at 110°C for 12 hours to dry, which was then ground and annealed at 700°C for 4 hours to get the final Zn nanoparticles. Thallium oxide (TI2O3) (99%, BDH) and Zn nanoparticles of 100 nm in appropriate ratios were mixed in Cu0.5Ba2Ca3Cu4O12−δ precursor material. The precursor material with Tl2O3 and Zn nanoparticles was ground for 1 hour and then pelletized under 3.8 tons/cm2 pressure. The pellets were enclosed in gold capsules and sintered at 880°C for nearly 10 minutes in preheated chamber furnace followed by quenching to room temperature to get the required Znx/(Cu0.5Tl0.5)Ba2Ca3Cu4O12−δ  {Znx/CuTl-1234}, x = 0, 0.6, 1.2, 1.8, 2.4, and 3.0 wt.%, nanoparticles-superconductor composites.Nanoparticles-superconductorZnx/CuTl-1234 composites samples were characterized thoroughly with different available experimental techniques. The structure and phase purity of the material were determined by XRD scans D/Max IIIC Rigaku with a CuKα source of wavelength (1.54056 Å). We measured dc-resistivity and ac-susceptibility of these samples. Scanning electron microscopy (SEM) was carried out for morphology. The phonon modes related to the vibrations of various oxygen atoms in the unit cell were determined by FTIR absorption spectroscopy in wave number range from 400 to 700 cm−1.


## 3. Results and Discussions

XRD pattern exhibits prominent diffraction peaks indexed with hexagonal closed pack (HCP) structure of Zn nanoparticles as shown in Figure1. The distinct diffraction peaks at 36.34°, 39.06°, 43.28°, 54.36°, 70.1°, 70.68°, and 77.04° diffraction angles correspond to (002), (100), (101), (102), (103), (110), and (004) planes of HCP structure, respectively. HCP structure of Zn nanoparticles matched with the data base of Joint Committee on Powder Diffraction Standards (JCPDS number 00-004-0784). The size of Zn nanoparticles was calculated by Debye Sherrer’s formula and the average size of these Zn nanoparticles was about 100 nm. The representative XRD spectra of Znx/CuTI-1234 nanoparticles-superconductor composites with x = 0 and 3.0 wt.% are shown in Figure 2. These composites have shown the tetragonal structure following P4/mmm symmetry with almost the same lattice parameters a = 4.21 Å and c = 18.25 Å. Majority of the diffraction peaks correspond to CuTl-1234 phase. XRD analysis reveals that the Zn nanoparticles addition has not affected the crystal structure of CuTl-1234 phase. The nonmagnetic Zn nanoparticles of 100 nm size dispersed themselves on the surface of CuTl-1234 grains occupying intercrystallite sites. The slight variation in lattice parameters by the addition of Zn nanoparticles in CuTl-1234 superconducting matrix is mainly due to variation of oxygen contents. Some unindexed peaks of very low intensity are possibly due to presence of impurities and some other superconducting phases. The diffraction peaks were indexed using the computer software MDI-Jade and matched with international center for diffraction data (ICDD) record.Figure 1
XRD pattern of zinc (Zn) nanoparticles.Figure 2
XRD patterns ofZnx/CuTl-1234 composites with x = 0 and 3.0 wt.%.The morphology was examined by SEM micrographs ofZnx/CuTI-1234 (x = 0~3.0 wt.%) nanoparticles-superconductor composites as shown in Figure 3. The granular nature and porosity of these samples are obvious from these micrographs. There is an improvement in the intergrains connectivity as well as in grains size after the addition of Zn nanoparticles in CuTI-1234 superconducting matrix. The main issue being faced is the nonuniform distribution of Zn nanoparticles within the entire bulk CuTI-1234 matrix.Figure 3
SEMs ofZnx/CuTl-1234 composites with (a) x = 0, (b) x = 0.6, and (c) x = 1.8 wt.%.FTIR absorption spectra ofZnx/CuTI-1234, x = 0, 0.6, 1.2, 1.8, 2.4, and 3.0 wt.%, nanoparticles-superconductor composites are shown in Figure 4. Considering our previous studies to understand the mechanism of superconductivity in HTSCs, the possibility of electron-phonon interaction cannot be ignored. Oxygen related phonon modes are of special interest, since these modes most likely cause such interactions. We have taken FTIR spectra in the range of 400–700 cm−1 in which the bands from 400 to 540 cm−1 are associated with the apical oxygen atoms and from 541 to 600 cm−1 are associated with CuO2 planar oxygen atoms. The bands from 670 to 700 cm−1 are associated with Oδ atoms in the charge reservoir layer [31–34]. But in the pure Cu0.5Tl0.5Ba2Ca3Cu4O12−δ samples, the apical oxygen modes of types Tl–OA–Cu(2) and Cu(1)–OA–Cu(2) are observed around 415 cm−1 and 444~456 cm−1 and CuO2 planner modes are around 541 cm−1. The apical oxygen mode of type Tl-OA-Cu(2) is slightly hardened to 421 cm−1 and Cu(1)-OA-Cu(2) is softened to 518 cm−1 in nano-Zn particles added samples, which may be due to stresses and strains produced in the material after the addition of these nanoparticles. Almost the positions of all the oxygen vibrational phonon modes remained unaltered after nano-Zn particles addition in CuTl-1234 matrix. This gives us a clue that Zn did not substitute any atom in the unit cell and remained at the grain-boundaries of CuTI-1234 matrix.Figure 4
FTIR spectra ofZnx/CuTl-1234 composites with x = 0, 0.6, 1.2, 1.8, 2.4, and 3.0 wt.%.The dc-resistivity versus temperature measurements ofZnx/CuTI-1234, x = 0, 0.6, 1.2, 1.8, 2.4, and 3.0 wt.%, nanoparticles-superconductor composites are shown in Figure 5. All the samples exhibit metallic like behavior in variations of dc-resistivity above superconducting transition temperatures. The four-probe method was used for dc-resistivity measurements. Systematic and consistent reduction in Tc values from 105 K for x = 0 to 93 K for x = 3.0 wt.% was observed. The decrease in Tc(0) with increasing content of Zn nanoparticles has been observed as shown in the inset of Figure 5. Gradual decrease in Tc(0) with increasing nano-Zn particles content can be either due to oxygen vacancy disorder or due to mobile carriers trapping, or due to diminishment of oxygen content in CuO2 conducting planes. Nonmonotonic variation in normal state resistivity {ρ290K (Ω-cm)} is mainly due to nonuniform distribution of Zn nanoparticles and irregular scattering of carriers at the grain-boundaries of Znx/CuTl-1234 composite [35–39].Figure 5
Temperature dependence of dc-resistivity measurements ofZnx/CuTl-1234 composites with x = 0, 0.6, 1.2, 1.8, 2.4, and 3.0 wt.%.Magnetic ac-susceptibility measurements ofZnx/CuTI-1234 composites are shown in Figure 6. We used SR530 lock-in amplifier working at frequency of 270 Hz with HAC = 0.07 Oe of primary coil. There is one peak for all samples above the transition temperatures in all ac-susceptibility measurements for different concentrations of nano-Zn particles in CuTl-1234 superconducting matrix. The magnitude of diamagnetism of the superconducting materials is represented by the real part (χ′) of ac-susceptibility and the ac-losses corresponding to the flux penetration in the superconducting samples are represented by imaginary part (χ′′). The imaginary part of the ac-susceptibility provides the intergranular contribution, which gives information about the nature of intergrains weak-links and pinning strength [40, 41]. The suppression of superconductivity within the grains decreases the magnitude of χ′. It is observed that onset temperature as well as magnitude of diamagnetism has overall been decreased with increased Zn nanoparticles content. The peak position in χ′′ is clearly shifted to lower temperature values with increased Zn nanoparticles.Figure 6
AC susceptibility measurements ofZnx/CuTl-1234 composites with x = 0, 0.6, 1.2, 1.8, 2.4, and 3.0 wt.%.The regular decreasing trend in superconducting properties can be expected due to reduction of superconducting volume fraction with increasing content of Zn nanoparticles at the grains-boundaries of CuTI-1234 superconductor. The second possible reason may be due to enhanced scattering cross section of carriers after addition of nanoparticles of nonmagnetic 3d10 Zn element.


## 4. Conclusion

The effects of Zn nanoparticles addition on superconducting properties as well as phase formation of CuTl-1234 superconductor were studied. We synthesizedZnx/CuTI-1234 composites successfully by well established solid-state reaction. The tetragonal structure of CuTl-1234 phase was determined by XRD, which remained unaltered and uninterrupted after nano-Zn particles addition. Unaltered crystal structure of host CuTl-1234 phase confirmed the existence of Zn nanoparticles at the intercrystallite sites. The SEM micrographs have shown the enhanced grain sizes after nano-Zn particles addition. The suppression of superconducting properties of CuTl-1234 phase after addition of nonmagnetic 3d10 Zn element nanoparticles can be attributed to reduction of superconducting volume fractions and enhanced scattering cross section of mobile carriers.



---

*Source: 9781790-2016-03-15.xml*