# Hot Structure Flight Data of a Faceted Atmospheric Reentry Thermal Protection System

Authors: Hannah Boehrk; Hendrik Weihs; Henning Elsäßer
Journal: International Journal of Aerospace Engineering
 (2019)

---

## Abstract

The second sharp-edged flight experiment is a faceted suborbital reentry body that enables low-cost in-flight reentry research. Its faceted thermal protection system consisting of only flat radiation-cooled thermal protection panels is cost-efficient since it saves dies, manpower, and storage. The ceramic sharp leading edge has a 1 mm nose radius in order to achieve good aerodynamic behaviour of the vehicle. The maximum temperature measured during flight was 867°C just before transmission ended and was predicted with an accuracy of the order of 10%. The acreage thermal protection system is set up by 3 mm fiber-reinforced ceramic panels isolated by a 27 mm alumina felt from the substructure. The panel gaps are sealed by a ceramic seal. Part of the thermal protection system is an additional transpiration-cooling experiment in which nitrogen is exhausted through a permeable ceramic matrix composite to form a coolant film on the panel. The efficiencies at the maximum heat flux are 58% on the porous sample and 42% and 30% downstream of the sample in the wake. The transient load at each panel location is derived from the trajectory by oblique shock equations and subsequent use of a heat balance for both cooled and uncooled structures. The comparison to the heat balance HEATS reveals heat sinks in the attachment system while the concurrence with the measurement is good with only 8% deviation for the acreage thermal protection system. Aerodynamic control surfaces, i.e., canards, have been designed and made from a hybrid titanium and ceramic matrix composite structure.


---

## Body

## 1. Introduction

In 2001, Longo et al. and Eggers et al. have worked out a concept using sounding rockets for the purpose of establishing low-cost reentry flight opportunities for the investigation of in-flight aerothermodynamic phenomena [1, 2]. Although expensive and complex, structural artifice supports this endeavour. Longo proposed a faceted sharp-edged concept as an initial flight experiment. The approach was to estimate the cost for two different thermal protection systems (TPS) for the reference vehicle HOPPER [1, 3, 4]: a curved-panel TPS and a flat-panel TPS. Longo et al. compared the results and have found that 70% of the cost for the hot structure can be saved in dies, man hours, and storage [1]. For each curved part, a respective die is needed for each process step. Moreover, the panels have to be laid up individually by hand into the complexly curved die, adding to the man hours. Finally, the die must be stored in case of a need for a replacement or a need for a second mission. Flat panels, on the contrary, can be shaped from the identical basic shape and milled into the necessary geometry which reduces the storage cost for moulds and replacement panels. The study showed that from an aerothermodynamic point of view, problems are faced from these sharp leading edges, steps, and gaps. They promote local stagnation areas that experience very high temperatures that have not been withstood by any material before. On the other hand, sharp leading edges are known to have minimum drag, require relatively low thrust during ascent, and achieve a higher cross-range during reentry leading to larger reentry windows, as opposed to blunt bodies [5]. Therefore, during the 1990s, the development of ceramic composite and ultrahigh-temperature material systems for TPS applications has led to a renewed interest in sharp-edged configurations [1] such as the waverider concept F8 [6], the project JAPHAR [7], and the SHARP project [8]. The sharp-edged flight experiment presented here serves to investigate the practicability of the new materials for slender and controllable hypersonic flight vehicles. Although aspects like the aerodynamics at single flight points can be investigated in ground test facilities, the transient full scale qualification can be demonstrated only in flight.With SHEFEX I, this novel system approach with the combination of all of these assets, has flown a return flight from a 200 km apogee for the first time in 2005. It was proven by aerothermodynamic calculations and later validated against the SHEFEX I in-flight measurements that the thermal protection system can withstand the high temperatures that occur during return flight [9]. SHEFEX I performed successful reentry from 80 km at Mach 5.6 to 26 km at Mach 6.2 with the subsequent loss of the vehicle [10]. Lessons learned include the comparison of real flight data against numerical simulations and ground testing [9, 11].Taking into account all the experience and collected flight data obtained during the SHEFEX I mission, the test vehicle was redesigned to a similarly faceted, sharp-edged reentry body SHEFEX II and extended by an active control system, which allows for active aerodynamic control during the atmospheric flight segment [12, 13]. Unlike the nonsymmetric shape of SHEFEX I that provided natural lift during flight, SHEFEX II has an axis-symmetric shape in order to allow for only the control system to generate lift. Moreover, the axis-symmetric shape provides the possibility to take measurements during ascent since no fairing is needed. As depicted in Figure 1, SHEFEX II has an octagonal cross section over a forebody length of 1.5 m at a height and diameter of 0.5 m. It was launched by a two-stage sounding rocket system from Andøya, Norway, in spring 2012. The figure also shows the location nomenclature with the panel segments denominated in letters A though E.Figure 1
Sharp-edged flight experiment SHEFEX II.This paper gives an overview over the thermal protection system (TPS) of the SHEFEX II vehicle in heritage of SHEFEX I. At first, the predicted trajectory is given. After the introduction of the SHEFEX II TPS material, the design of the structural key elements will be explained in Section4. These comprise (a) the radiation-cooled faceted acreage panels and their attachment to the substructure; (b) the sharp leading edge, or vehicle tip; (c) the ceramic-based transpiration-cooled experiment AKTiV; and finally, (d) the aerodynamic control surfaces, i.e., canards, in which the twofold requirements of high-temperature resistance and load bearingness are realized in a hybrid structure. Their design is described in Sections 4.1–4.4. The instrumentation enables comparison of measurements to the load predicting heat balance tool HEATS and thus interpretation of ground testing and flight data. The impressive flight data are presented and interpreted in Section 5. The paper focuses on the TPS structure and design of the vehicle SHEFEX II and demonstration of the general viability of these structural solutions. Results are provided in terms of recorded and transmitted flight data.


## 2. The SHEFEX II Trajectory

SHEFEX II was launched from the Andøya Rocket Range in Norway on June 22nd 2012. It flew approximately 800 km far in a north-west direction where it fell into the arctic sea west of Svalbard, being decelerated by a parachute. Figure 2 shows the data measured by the Digital Miniature Attitude Reference System (DMARS) during the SHEFEX II flight [14, 15]. Black lines give in-flight measurement, and gray lines give the assumed subsequent flight path. The vehicle was launched by a two-stage Brazilian rocket configuration with an S-40 first stage and an S-44 second stage rocket motor. The rocket has delivered SHEFEX II, shown in the photograph of Figure 3, to an apogee of ∼180 km. The total flight time was roughly 500 s comprising 52 s of experimental time for the atmospheric reentry between 100 and 30 km.Figure 2
DMARS data of the SHEFEX II trajectory [14]. Black lines give in-flight measurement, and gray lines give the assumed subsequent flight path.Figure 3
Payload of the SHEFEX II reentry vehicle upon rollout to the launcher.All data were transmitted to a ground station at the Andøya Rocket Range. The connection lasted until SHEFEX II dove behind the horizon, corresponding to an altitude of 30 km. The subsequent flight path is assumed to have followed the trajectory down to approximately 13 km when the payload was split, translated to a subsonic flight, and the parachute was released. A flotation bag transmitted a position signal after splashdown, but due to harsh weather in the landing region the vehicle could not be recovered before it sank. Within the experiment time, the vehicle had accelerated from 2559 m/s and Mach 10.2 at 101 km altitude to 2791 m/s and Mach 9.3 at 30 km.During hypersonic reentry, a shock stands ahead of blunt shapes while it is attached to pointed shapes, since the shock distance decreases with leading-edge radius [16, 17]. Blunt bodies like Apollo or Soyuz are commonly used in order to increase the shock distance from the heat shield material to allow for the gas temperature close to the vehicle to be dissipated into the internal energy of the atmospheric gas, such as dissociation or vibration [16]. In the case of SHEFEX II, an oblique shock rises from the sharp pointed nose with very low shock distance. Downstream from the oblique shock, the air is expanded at the facet corners. Figure 4 illustrates the flow phenomena on the example of panels A and B of SHEFEX II. The TPS designer must account for the thermomechanical loads onto the vehicle. However, since access to space is costly, overdesign must be avoided. Therefore, the TPS designer needs to lay out the heat shield against transient loads, considering also the heat capacity of the heat shield material. The challenges addressed in SHEFEX II are the design of the sharp leading edge, the faceted acreage TPS, the active transpiration cooling, and the canard surfaces for controlled hypersonic flight and attitude. During heat shield design, it is necessary to estimate the heat flux from a fluid flow to a surface. Especially when the surface is actively cooled, such as with film, transpiration, or effusion cooling, the determination of the heat transfer coefficient is difficult to assess. The computer program HEATS (Heat Exchange Analysis for Transpiration Systems) is used to determine the transient wall temperature throughout the entire reentry trajectory or ground-testing experiment. It has been validated by comparison to experiments in both a steady-state arc-heated wind tunnel under laminar in-flow and short duration measurements in a shock tube [18, 19].Figure 4
SHEFEX II shock and expansion areas.


## 3. Material

The present paper gives an overview of the different parts of the SHEFEX II thermal protection system. The SHEFEX II acreage TPS is made from a ceramic matrix composite (CMC). The fiber ceramic C/C-SiC, used for the SHEFEX II TPS, is a composite consisting of carbon fibers with a matrix of carbon and silicon carbide. It was qualified in plasma wind tunnel testing in numerous campaigns since the 1980s and during real reentry flight, such as in the FOTON9, EXPRESS, FOTON-M2, and the SHEFEX I and II missions. The material is lightweight with a density of 1900 kg/m3. Up to temperatures as high as 2000 K, this material has stable properties with respect to Young’s modulus, strength, and tensile strain. Moreover, with large damage tolerance, it is resistant to thermoshock [20] at low thermal expansion in a ply direction of only 1.5×10−6K−1 [21]. The carbon fibers, however, are oxidation sensitive with <3 kg/m2 h specific mass loss below 1900 K and >10 kg/m2 h above 2100 K. When coated, the material withstands high-temperature loads up to 1970 K, being fully reusable with negligibly small specific mass loss rates below 0.1 kg/m2 h [22].The manufacturing of C/C-SiC has been widely reported [23]. The intermediate stage C/C (carbon-fiber-reinforced carbon) has intriguing permeable properties. The good permeability of the C/C produced during DLR’s pyrolysis step is used in transpiration cooling in which a cooling fluid is fed through the structure into the boundary layer, as will be introduced for the flight experiment AKTiV. The microcracks in the low-density carbon matrix serve as open pores for the fluid transfer. The pores distribute the coolant evenly over the hot facing surface to keep it cool and enable it to withstand exposure to high temperatures. The permeability of the C/C used for the hypersonic in-flight transpiration-cooling experiment AKTiV in 2012 is on the order of 10−13m2. The porosity is relatively high at 12%. A coolant film may also provide oxidation protection for the structure. Since material properties are adjustable by choice of rovings and stacking of plies, both conductivity and permeability can be optimized to the values necessary for the application. Table 1 compares the thermal properties of C/C and C/C-SiC.Table 1
Material properties of C/C, C/C-SiC, and titanium Ti6Al4V. C/C-SiC is given in its orthotropic properties which are comparably constant over temperature. Titanium properties are given with respect to room temperature (RT) and high temperature (HT) of approximately 800 K.
ρ(kg/m3)
ϵ—
λ‖(W/mK)
λ⊥(W/mK)
cp(J/kg K)
αTE,‖10−6K−1
αTE,⊥10−6K−1
σ(MPa)
C/C
1400
0.85
14
2
1650
C/C-SiC
1900
0.85
17
8
1350
1.5
5
160 (bending)
Ti6Al4V
4430
7.1
7.1
560
2.6 (RT)
900 (RT)
3 (HT)
550 (HT)C/C-SiC, as presented here, is the material used for the SHEFEX II thermal protection system. The majority of the key components of the TPS described in the following section are based on this material. Table1 additionally gives thermophysical properties of Ti6Al4V which is used in the hybrid design of the control surfaces, i.e., canards, described in Section 4.4.


## 4. Faceted Thermal Protection System

The primary structure of the forebody consists of an aluminum substructure created by stiff ribs and stringers. The open volume is then closed by flat aluminum panels which create an inner mould line. These aluminum panels are used for mounting the TPS facets and experiments. Inside the aluminum substructure, the in-flight measurement infrastructure is integrated. These are thermocouple connection and compensation, pressure transducers, a pyrometer system, and data processing boxes.As explained above, the forebody geometry is symmetrically divided into eight identical facets 1 through 8 in a circular direction and five lengthwise segments A through E, as marked in Figure1. All in all, the payload houses 40 single flat areas. The challenging parts are the attachment of the panels to the cold substructure, providing sufficient insulation to the aluminum and interpanel sealing. Before flight, the entire payload forebody has undergone vibration testing. The tests have shown that the SHEFEX II payload remains safe with an identical eigen frequency before and after the test.In this chapter, the overall faceted TPS will be described and its attachment to the substructure will be addressed. Subsequently, the set-up, attachment, and instrumentation of the sharp leading edge will be introduced. Finally, the transpiration-cooled experiment AKTiV, the world first transpiration-cooled flight experiment, will be described. Finally, the aerodynamic control surfaces, with their hybrid titanium and ceramic matrix composite structure are presented.


### 4.1. Faceted Acreage TPS

The basic TPS system is based on the segmented FESTIP concept developed in the 1990s [24].It facilitates multiuse, low maintenance, and rapid turn-around time for the exchange of TPS panels and is shown in Figure5. The main element of the concept is the hot CMC panel, supported in all directions by a central post and flexible standoffs at the four corners, so that the panel’s thermal expansion is not suppressed [25]. Between the panel and the cold aluminum structure, an alumina felt insulation material is laid out. The SHEFEX standard C/C-SiC panel thickness is 3 mm, and the alumina insulation thickness is 27 mm. This results in an extremely thin overall TPS thickness of 33 mm, including the aluminum panel, making room for the payload and instrumentation. Each flat panel was instrumented with three thermocouples and a pressure port [26, 27].Figure 5
SHEFEX II thermal protection system set-ups [31].As mentioned, one key issue of the design concept is the hot connection of the panels to the CMC standoff by fasteners in the high-temperature regime of up to 1800 K. These fasteners must enable panel attachment and removal having only external access to the TPS. A rivet-type fastening bolt was therefore developed, tested, and optimized, combining the function of a screw and a rivet [28–30]. It is shown in Figure 6. A total of 180 screw rivets are necessary for assembly of the flight unit.Figure 6
Fastener side and top views [30].Another key element for the TPS is the interpanel seal [32]. Seals are used to protect the area where two panels are joined but not connected. For temperatures around 1700 K, a thermal expansion
(1)Δl=LpanelαTET,of up to 0.765 mm has to be taken into account lengthwise for the panels. Therefore, a gap has to be foreseen to allow for the panels to expand freely without conflicting with each other. In order to prevent hot gas from intruding into the vehicle or even into the insulation of the TPS, the gap needs to be covered. Alumina-based WHIPOX has a flexible intermediate state during the manufacturing process, in which it is possible to shape a component such as the SHEFEX rigid seal during forebody assembly. Using this property, it is possible to shape and cut all required seal components from one uniform WHIPOX tape as shown in Figure 7.Figure 7
WHIPOX® seal between facets [31].In segment C, every other panel is from a radiofrequency-transparent WHIPOX alumina ceramic matrix composite in order to transmit the signal from a patch antenna. WHIPOX is, thus, used as an oxidation-resistant alternative to carbon-based CMC. A special feature of these CMCs is their inherent transparency for electromagnetic waves, making them attractive as thermal protection for antennae. However, the emissivity of alumina is low and, consequently, the radiation cooling capability of alumina-based TPS panels is limited. In order to prevent thermal overload, the emissivity of CMC is improved by superficial impregnation and coating with an oxidation-resistant “black” CoFe-spinel [33]. It has been shown that CoFe-spinel surface modification reduces the CMC temperatures by more than 200 K in a Mach 6 hypersonic flow field [33]. Moreover, the large coefficient of thermal expansion of roughly 7×10−6K−1 (see Table 1 for comparison) causes a strong bending momentum within the flexible CMC standoffs. At the expected 1500 K at panel C, resulting in a thermal expansion of 2.7 mm, the momentum is too large for the standoffs. In order to account for these effects, the WHIPOX panels are split into two parts, thus bisecting the expansion on each half panel to 1.35 mm. The momentum in the standoffs is thus diminished and another gap is introduced between the half panels, in turn, sealed by a WHIPOX seal.The faceted set-up of SHEFEX II has been shown to be cost-efficient compared to curved parts. In contrary to flat panels, each curved part needs a respective die for each process step, i.e., tempering of the CFRP green body and pyrolysis, and has to be laid up individually by hand into the complexly curved die. SHEFEX II consists of 40 flat TPS panels in segments B through E, made from identical raw material plates. The set-up has the advantage of being able to integrate experiments from potential clients with one single interface specification [34–37].


### 4.2. Sharp Leading Edge

Figure8 shows the sharp leading-edge design. The octagonal pyramid shape was milled from solid material and has a mass of around 680 g. The radius of the sharp leading edge was investigated with a profile projector and determined to be 0.8 mm. The tip is attached to the vehicle by a mount from thin-walled C/C-SiC material, as shown at the very left of the side view in Figure 8. The mount is composed of two half shells, joined by joining elements, and an inlay. The inlay has four screw bores through which, by means of four C/C-SiC fasteners, the tip is attached to the mount [30]. The thin-walled mount, in turn, is attached to the aluminum substructure by Z-shaped CMC standoffs.Figure 8
SHEFEX II C/C-SiC sharp leading-edge design.The instrumentation of the sharp leading edge during reentry flight comprises bores for both pressure measurement and thermocouples. These measurements are used to reconstruct flight attitude [38]. The bores for the flush air data system have been electrical discharge machined into the material. Three sheathed type-S-thermocouples with 1 mm diameter and isolated hot junctions were located far upstream in the leading edge at approximately 5 mm beneath the surface as shown in Figure 9 in the bottom cut view. Additionally, the solid C/C-SiC tip contains pressure ports on its eight facets in the shape of slender bore holes leading to the aft side of the tip. The pressure bores must be connected to the pressure transducers by metallic tubing because mounting the transducer directly to the tip is not possible due to geometrical and thermal constraints. Therefore, eight Inconel tubes have been soldered into the ceramic matrix composite in order to make the connection, see Figure 10.Figure 9
Leading-edge instrumentation.Figure 10
SHEFEX II sharp leading edge with pressure routing.A duplicate was ground-tested in an arc-heated wind tunnel in a representative condition for the loads imposed by the flight trajectory [39]. Additionally, the surface temperature was measured by an infrared camera and pyrometers. The results of the ground testing show that the temperatures at the interior thermocouple positions are well predicted by the heat balance from HEATS with accuracies of 3 and 11% [39]. Also, the ground measurement with an IR camera is predicted with 6% accuracy.


### 4.3. Transpiration-Cooled Experiment AKTiV

The ceramic matrix composite C/C-SiC serves as a passive, radiatively cooled heat shield of the SHEFEX II thermal protection system. Lately, in the discussion of reusable space transportation, active cooling systems have gained special interest when it comes to severe thermal environments where the passive systems are insufficient. One experiment on SHEFEX II, AKTiV, was dedicated to this topic.Transpiration-cooled rocket engines fabricated from porous CMC material have been investigated for a couple of years [40]. This technology, in which a coolant is forced through a permeable wall component by a pressure gradient, has recently been transferred to reentry load cases. CMCs are candidate materials for transpiration cooling as they can be produced within a variety of open porosity and permeability characteristics. The described prestate of the TPS material C/C has a natural porosity and permeability and still withstands the mechanical and thermal loads as specified for TPS. However, it consists of carbon and is thus extremely prone to oxidation at temperatures above 700 K.Transpiration cooling, as referred to here, is effected by two physical phenomena. The first being convection-cooling of the wall material by the coolant as it is fed through the permeable structure. The other one is the lowering of the heat transfer from the high-enthalpy environment to the vehicle surface by forming a coolant layer or film on the outer—hot—surface as shown in Figure11. Moreover, a coolant film—for example of nitrogen—also provides oxidation protection for the structure which may be an important issue in the case of carbon-based materials.Figure 11
HEATS heat balance concept for transpiration cooling [18].AKTiV was located on panel C3, see Figure1. A nonpressurized reference set-up was mounted on the opposite panel C7 where—at zero sideslip angle—the same ambient flow conditions were expected. HEATS is a lay-up tool for the determination of transient wall heat flux to a transpiration-cooled parallel flat plate under laminar or turbulent flow conditions. It was developed for the lay-up of the experiment and later for the interpretation of the results. The method is based on heat balances between wall material, transpired coolant, and surrounding hot gas. The problem is approached in three steps, sketched in Figure 11. Step 1 includes the heat flux to the panels as in a parallel plate case. The heat balance for the surface in this case equals
(2)q̇HG−W=q̇rad+q̇cond,with index HG−W indicating heat transfer from the hot gas to the wall. Step 2, addressed in region #2 of Figure 11, additionally takes into account the thermal blocking by a coolant layer (film cooling) that in the case of the experiment presented here is injected through the porous material C/C. The heat balance for the surface remains
(3)q̇F‐W=q̇rad+q̇cond,with index F−W for the heat transfer from the film to the wall. Step 3 addresses all three effects, heat flux from the hot gas to the film q̇HG−F, from the film to the wall q̇F−W, and heat transfer from the hot wall to the transpired coolant as the coolant temperature increases according to the heat equation for the wall,
(4)ρmatcp,mat∂Tmat∂t=λx∂2Tmat∂x2+λy∂2Tmat∂y2−αVTmat−TF,and the one for the gas, accordingly,
(5)ρFcp,F∂TF∂t=∂ṁx,y/Acp,FTF∂x+αVTmat−TF.Figures12 and 13 show the set-up of the experiment on the SHEFEX II reentry vehicle. In the center of a 7 mm thick thermal protection panel, a porous C/C 5 mm thick sample of the dimensions 61×61mm2 is inserted. This porous sample is to be run through by the coolant and is flanged into the surrounding TPS panel by a pressure reservoir and riveted ceramic fasteners [29, 30]. The reservoir itself is made of stainless steel. The panel and sample are tightened against sneak flows by graphite SIGRAFLEX felt.Figure 12
AKTiV side view.Figure 13
AKTiV interior instrumentation.The system consists of a pressurized tank, a pressure regulator, and a valve on the vehicle side of the experiment, and another pressure regulator, a mass flow controller (sonic nozzle), sensors, and data acquisition on the payload side of the experiment. A photograph of the entire set-up is shown in Figures12 and 13. The hot panel of AKTiV is instrumented with thermocouples as shown in Figure 14. The picture also shows the groves where Z-shaped standoffs are attached to carry the hot panel.Figure 14
AKTiV panel instrumentation.Especially downstream of the porous sample, the thermocouples serve to monitor the effect of the film cooling redundantly, but also locally resolved, as shown in Figure15(a). The reference module on panel C7 has monitored the uncooled behaviour of the set-up, as shown in Figure 15(b). A direct comparison of cooled and uncooled wall temperature TW with reference to coolant temperature Tc allows for assessment of the cooling efficiency,
(6)η=TW,uncooled−TWTW,uncooled−Tc,of the transpiration cooling by AKTiV. Reservoir pressure is measured with a Kulite HKL/T-1-235 (M) combined pressure (p29) and temperature (pt6) sensor screwed at the bottom of the reservoir [41, 42].Figure 15
AKTiV thermocouple locations on the experiment (C3) and the reference (C7).
(a)
(b)


### 4.4. Sharp Leading Edges in Canards

Another experiment onboard is dedicated to the attitude and roll control during reentry by means of the so-called canards, also shown in Figure1. The canards are to stabilize the forebody during reentry by damping out rolling, pitching, or coning [12, 13]. They are mounted onto the flat surfaces of the canard module that transfers the octagonal forebody shape to the cylindrical rocket modules. Four independent actuators, mechanically guarded within a secure maximum deflection of 15°, drive the canards. For transportation reasons, the canards have to be able to be mounted and secured from external access only.Control surfaces are load bearing, and this issue requires additional consideration during their design. Like any structural part in flight experimentation, the canards have to withstand all thermal and mechanical loads while being lightweight. However, in order to reach the sufficient efficiency of the canards at altitudes above 60 km with low static air pressure, they are oversized for the lower altitudes. Consequently, extreme thermomechanical loads are encountered at low altitudes of 20 km, which defines the end of the SHEFEX II experiment. The major challenge of the canard design is thus to withstand the resulting high mechanical load at the canard pivot in combination with the high thermal loads at the leading edges.The design point is a worst case scenario as in the case of a malfunction in the canard actuators in which the canard would keep a constant maximum canard deflection of 15° throughout the entire experiment phase, where the maximum mechanical canard load isFcanard=10kN [43]. This is equivalent to a pressure difference of 1.8 bar on the canard surfaces. The load in the outer fiber of a potential C/C-SiC pivot is deduced as follows. The load reduction to the pressure point of the canard and the pressure point approximated in the area focus of the triangular canard, i.e., with a lever arm of l=75mm, the momentum in the pivot yields 750 Nm with
(7)Mpivot=lFcanard.With pivot diameterd=40mm and area moment of inertia of an approximate circular cross section I=πr4/4, the load in the outer fiber,
(8)σof=MpivotId2,results in approximately 375 MPa. Table 1 gives strength, thermal expansion coefficient, and failure temperature for C/C-SiC, indicating that the ceramic cannot endure the stress resulting from the equation above. A hybrid canard design was therefore chosen using a metallic main structure at the pivot and a CMC as the leading edge.The sharp leading edge of the hybrid canard is made from C/C-SiC, and the main structure including the pivot is made from titanium. This choice of material combination accounts for similar coefficients of thermal expansion, given in Table1. Titanium, moreover, has a high strength and low density. For joining of the two structural parts from CMC and titanium, a dovetail principle is applied as shown in Figure 16. To secure the CMC at the titanium, it is locked with a CMC pin. The dovetail compensates for the remaining difference in thermal expansion by permitting displacement of the components in length direction. The leading edge’s laminae lay-up is also indicated in Figure 16. In thickness, i.e., out of plane of the C/C-SiC, the thermal expansion coefficients of both materials are comparable, as shown in Table 1, guaranteeing a tight conjunction throughout the whole flight. Due to the higher coefficients of the thermal expansion in ply direction, the titanium is expected to elongate beyond the C/C-SiC edges and pull the C/C-SiC by frictional effects. The maximum but uncritical load of 45 MPa resulting from this effect is located at the CMC safety pin from Figure 17.Figure 16
Dovetail principle.Figure 17
Mounting order for the CMC-titanium hybrid canard structure.As mentioned above, for transportation reasons, the hybrid structure must allow for mounting from external access only. The titanium part can be slipped onto the canard module at first, followed by sliding in the CMC leading edge and securing it with a pin. The mounting procedure is depicted in Figure17.The sharp leading edge is not coated, so oxidation is expected to a certain extent. This is however tolerated, since erosion is expected to take only a few millimeters of the leading edge. The main titanium structure is also expected to locally overheat.Both structural parts are mechanically loaded under their limits by factors of 1.5. In the titanium structure, the maximum stress appears at the pivot and in the C/C-SiC at the dovetail inner radius.


## 4.1. Faceted Acreage TPS

The basic TPS system is based on the segmented FESTIP concept developed in the 1990s [24].It facilitates multiuse, low maintenance, and rapid turn-around time for the exchange of TPS panels and is shown in Figure5. The main element of the concept is the hot CMC panel, supported in all directions by a central post and flexible standoffs at the four corners, so that the panel’s thermal expansion is not suppressed [25]. Between the panel and the cold aluminum structure, an alumina felt insulation material is laid out. The SHEFEX standard C/C-SiC panel thickness is 3 mm, and the alumina insulation thickness is 27 mm. This results in an extremely thin overall TPS thickness of 33 mm, including the aluminum panel, making room for the payload and instrumentation. Each flat panel was instrumented with three thermocouples and a pressure port [26, 27].Figure 5
SHEFEX II thermal protection system set-ups [31].As mentioned, one key issue of the design concept is the hot connection of the panels to the CMC standoff by fasteners in the high-temperature regime of up to 1800 K. These fasteners must enable panel attachment and removal having only external access to the TPS. A rivet-type fastening bolt was therefore developed, tested, and optimized, combining the function of a screw and a rivet [28–30]. It is shown in Figure 6. A total of 180 screw rivets are necessary for assembly of the flight unit.Figure 6
Fastener side and top views [30].Another key element for the TPS is the interpanel seal [32]. Seals are used to protect the area where two panels are joined but not connected. For temperatures around 1700 K, a thermal expansion
(1)Δl=LpanelαTET,of up to 0.765 mm has to be taken into account lengthwise for the panels. Therefore, a gap has to be foreseen to allow for the panels to expand freely without conflicting with each other. In order to prevent hot gas from intruding into the vehicle or even into the insulation of the TPS, the gap needs to be covered. Alumina-based WHIPOX has a flexible intermediate state during the manufacturing process, in which it is possible to shape a component such as the SHEFEX rigid seal during forebody assembly. Using this property, it is possible to shape and cut all required seal components from one uniform WHIPOX tape as shown in Figure 7.Figure 7
WHIPOX® seal between facets [31].In segment C, every other panel is from a radiofrequency-transparent WHIPOX alumina ceramic matrix composite in order to transmit the signal from a patch antenna. WHIPOX is, thus, used as an oxidation-resistant alternative to carbon-based CMC. A special feature of these CMCs is their inherent transparency for electromagnetic waves, making them attractive as thermal protection for antennae. However, the emissivity of alumina is low and, consequently, the radiation cooling capability of alumina-based TPS panels is limited. In order to prevent thermal overload, the emissivity of CMC is improved by superficial impregnation and coating with an oxidation-resistant “black” CoFe-spinel [33]. It has been shown that CoFe-spinel surface modification reduces the CMC temperatures by more than 200 K in a Mach 6 hypersonic flow field [33]. Moreover, the large coefficient of thermal expansion of roughly 7×10−6K−1 (see Table 1 for comparison) causes a strong bending momentum within the flexible CMC standoffs. At the expected 1500 K at panel C, resulting in a thermal expansion of 2.7 mm, the momentum is too large for the standoffs. In order to account for these effects, the WHIPOX panels are split into two parts, thus bisecting the expansion on each half panel to 1.35 mm. The momentum in the standoffs is thus diminished and another gap is introduced between the half panels, in turn, sealed by a WHIPOX seal.The faceted set-up of SHEFEX II has been shown to be cost-efficient compared to curved parts. In contrary to flat panels, each curved part needs a respective die for each process step, i.e., tempering of the CFRP green body and pyrolysis, and has to be laid up individually by hand into the complexly curved die. SHEFEX II consists of 40 flat TPS panels in segments B through E, made from identical raw material plates. The set-up has the advantage of being able to integrate experiments from potential clients with one single interface specification [34–37].


## 4.2. Sharp Leading Edge

Figure8 shows the sharp leading-edge design. The octagonal pyramid shape was milled from solid material and has a mass of around 680 g. The radius of the sharp leading edge was investigated with a profile projector and determined to be 0.8 mm. The tip is attached to the vehicle by a mount from thin-walled C/C-SiC material, as shown at the very left of the side view in Figure 8. The mount is composed of two half shells, joined by joining elements, and an inlay. The inlay has four screw bores through which, by means of four C/C-SiC fasteners, the tip is attached to the mount [30]. The thin-walled mount, in turn, is attached to the aluminum substructure by Z-shaped CMC standoffs.Figure 8
SHEFEX II C/C-SiC sharp leading-edge design.The instrumentation of the sharp leading edge during reentry flight comprises bores for both pressure measurement and thermocouples. These measurements are used to reconstruct flight attitude [38]. The bores for the flush air data system have been electrical discharge machined into the material. Three sheathed type-S-thermocouples with 1 mm diameter and isolated hot junctions were located far upstream in the leading edge at approximately 5 mm beneath the surface as shown in Figure 9 in the bottom cut view. Additionally, the solid C/C-SiC tip contains pressure ports on its eight facets in the shape of slender bore holes leading to the aft side of the tip. The pressure bores must be connected to the pressure transducers by metallic tubing because mounting the transducer directly to the tip is not possible due to geometrical and thermal constraints. Therefore, eight Inconel tubes have been soldered into the ceramic matrix composite in order to make the connection, see Figure 10.Figure 9
Leading-edge instrumentation.Figure 10
SHEFEX II sharp leading edge with pressure routing.A duplicate was ground-tested in an arc-heated wind tunnel in a representative condition for the loads imposed by the flight trajectory [39]. Additionally, the surface temperature was measured by an infrared camera and pyrometers. The results of the ground testing show that the temperatures at the interior thermocouple positions are well predicted by the heat balance from HEATS with accuracies of 3 and 11% [39]. Also, the ground measurement with an IR camera is predicted with 6% accuracy.


## 4.3. Transpiration-Cooled Experiment AKTiV

The ceramic matrix composite C/C-SiC serves as a passive, radiatively cooled heat shield of the SHEFEX II thermal protection system. Lately, in the discussion of reusable space transportation, active cooling systems have gained special interest when it comes to severe thermal environments where the passive systems are insufficient. One experiment on SHEFEX II, AKTiV, was dedicated to this topic.Transpiration-cooled rocket engines fabricated from porous CMC material have been investigated for a couple of years [40]. This technology, in which a coolant is forced through a permeable wall component by a pressure gradient, has recently been transferred to reentry load cases. CMCs are candidate materials for transpiration cooling as they can be produced within a variety of open porosity and permeability characteristics. The described prestate of the TPS material C/C has a natural porosity and permeability and still withstands the mechanical and thermal loads as specified for TPS. However, it consists of carbon and is thus extremely prone to oxidation at temperatures above 700 K.Transpiration cooling, as referred to here, is effected by two physical phenomena. The first being convection-cooling of the wall material by the coolant as it is fed through the permeable structure. The other one is the lowering of the heat transfer from the high-enthalpy environment to the vehicle surface by forming a coolant layer or film on the outer—hot—surface as shown in Figure11. Moreover, a coolant film—for example of nitrogen—also provides oxidation protection for the structure which may be an important issue in the case of carbon-based materials.Figure 11
HEATS heat balance concept for transpiration cooling [18].AKTiV was located on panel C3, see Figure1. A nonpressurized reference set-up was mounted on the opposite panel C7 where—at zero sideslip angle—the same ambient flow conditions were expected. HEATS is a lay-up tool for the determination of transient wall heat flux to a transpiration-cooled parallel flat plate under laminar or turbulent flow conditions. It was developed for the lay-up of the experiment and later for the interpretation of the results. The method is based on heat balances between wall material, transpired coolant, and surrounding hot gas. The problem is approached in three steps, sketched in Figure 11. Step 1 includes the heat flux to the panels as in a parallel plate case. The heat balance for the surface in this case equals
(2)q̇HG−W=q̇rad+q̇cond,with index HG−W indicating heat transfer from the hot gas to the wall. Step 2, addressed in region #2 of Figure 11, additionally takes into account the thermal blocking by a coolant layer (film cooling) that in the case of the experiment presented here is injected through the porous material C/C. The heat balance for the surface remains
(3)q̇F‐W=q̇rad+q̇cond,with index F−W for the heat transfer from the film to the wall. Step 3 addresses all three effects, heat flux from the hot gas to the film q̇HG−F, from the film to the wall q̇F−W, and heat transfer from the hot wall to the transpired coolant as the coolant temperature increases according to the heat equation for the wall,
(4)ρmatcp,mat∂Tmat∂t=λx∂2Tmat∂x2+λy∂2Tmat∂y2−αVTmat−TF,and the one for the gas, accordingly,
(5)ρFcp,F∂TF∂t=∂ṁx,y/Acp,FTF∂x+αVTmat−TF.Figures12 and 13 show the set-up of the experiment on the SHEFEX II reentry vehicle. In the center of a 7 mm thick thermal protection panel, a porous C/C 5 mm thick sample of the dimensions 61×61mm2 is inserted. This porous sample is to be run through by the coolant and is flanged into the surrounding TPS panel by a pressure reservoir and riveted ceramic fasteners [29, 30]. The reservoir itself is made of stainless steel. The panel and sample are tightened against sneak flows by graphite SIGRAFLEX felt.Figure 12
AKTiV side view.Figure 13
AKTiV interior instrumentation.The system consists of a pressurized tank, a pressure regulator, and a valve on the vehicle side of the experiment, and another pressure regulator, a mass flow controller (sonic nozzle), sensors, and data acquisition on the payload side of the experiment. A photograph of the entire set-up is shown in Figures12 and 13. The hot panel of AKTiV is instrumented with thermocouples as shown in Figure 14. The picture also shows the groves where Z-shaped standoffs are attached to carry the hot panel.Figure 14
AKTiV panel instrumentation.Especially downstream of the porous sample, the thermocouples serve to monitor the effect of the film cooling redundantly, but also locally resolved, as shown in Figure15(a). The reference module on panel C7 has monitored the uncooled behaviour of the set-up, as shown in Figure 15(b). A direct comparison of cooled and uncooled wall temperature TW with reference to coolant temperature Tc allows for assessment of the cooling efficiency,
(6)η=TW,uncooled−TWTW,uncooled−Tc,of the transpiration cooling by AKTiV. Reservoir pressure is measured with a Kulite HKL/T-1-235 (M) combined pressure (p29) and temperature (pt6) sensor screwed at the bottom of the reservoir [41, 42].Figure 15
AKTiV thermocouple locations on the experiment (C3) and the reference (C7).
(a)
(b)


## 4.4. Sharp Leading Edges in Canards

Another experiment onboard is dedicated to the attitude and roll control during reentry by means of the so-called canards, also shown in Figure1. The canards are to stabilize the forebody during reentry by damping out rolling, pitching, or coning [12, 13]. They are mounted onto the flat surfaces of the canard module that transfers the octagonal forebody shape to the cylindrical rocket modules. Four independent actuators, mechanically guarded within a secure maximum deflection of 15°, drive the canards. For transportation reasons, the canards have to be able to be mounted and secured from external access only.Control surfaces are load bearing, and this issue requires additional consideration during their design. Like any structural part in flight experimentation, the canards have to withstand all thermal and mechanical loads while being lightweight. However, in order to reach the sufficient efficiency of the canards at altitudes above 60 km with low static air pressure, they are oversized for the lower altitudes. Consequently, extreme thermomechanical loads are encountered at low altitudes of 20 km, which defines the end of the SHEFEX II experiment. The major challenge of the canard design is thus to withstand the resulting high mechanical load at the canard pivot in combination with the high thermal loads at the leading edges.The design point is a worst case scenario as in the case of a malfunction in the canard actuators in which the canard would keep a constant maximum canard deflection of 15° throughout the entire experiment phase, where the maximum mechanical canard load isFcanard=10kN [43]. This is equivalent to a pressure difference of 1.8 bar on the canard surfaces. The load in the outer fiber of a potential C/C-SiC pivot is deduced as follows. The load reduction to the pressure point of the canard and the pressure point approximated in the area focus of the triangular canard, i.e., with a lever arm of l=75mm, the momentum in the pivot yields 750 Nm with
(7)Mpivot=lFcanard.With pivot diameterd=40mm and area moment of inertia of an approximate circular cross section I=πr4/4, the load in the outer fiber,
(8)σof=MpivotId2,results in approximately 375 MPa. Table 1 gives strength, thermal expansion coefficient, and failure temperature for C/C-SiC, indicating that the ceramic cannot endure the stress resulting from the equation above. A hybrid canard design was therefore chosen using a metallic main structure at the pivot and a CMC as the leading edge.The sharp leading edge of the hybrid canard is made from C/C-SiC, and the main structure including the pivot is made from titanium. This choice of material combination accounts for similar coefficients of thermal expansion, given in Table1. Titanium, moreover, has a high strength and low density. For joining of the two structural parts from CMC and titanium, a dovetail principle is applied as shown in Figure 16. To secure the CMC at the titanium, it is locked with a CMC pin. The dovetail compensates for the remaining difference in thermal expansion by permitting displacement of the components in length direction. The leading edge’s laminae lay-up is also indicated in Figure 16. In thickness, i.e., out of plane of the C/C-SiC, the thermal expansion coefficients of both materials are comparable, as shown in Table 1, guaranteeing a tight conjunction throughout the whole flight. Due to the higher coefficients of the thermal expansion in ply direction, the titanium is expected to elongate beyond the C/C-SiC edges and pull the C/C-SiC by frictional effects. The maximum but uncritical load of 45 MPa resulting from this effect is located at the CMC safety pin from Figure 17.Figure 16
Dovetail principle.Figure 17
Mounting order for the CMC-titanium hybrid canard structure.As mentioned above, for transportation reasons, the hybrid structure must allow for mounting from external access only. The titanium part can be slipped onto the canard module at first, followed by sliding in the CMC leading edge and securing it with a pin. The mounting procedure is depicted in Figure17.The sharp leading edge is not coated, so oxidation is expected to a certain extent. This is however tolerated, since erosion is expected to take only a few millimeters of the leading edge. The main titanium structure is also expected to locally overheat.Both structural parts are mechanically loaded under their limits by factors of 1.5. In the titanium structure, the maximum stress appears at the pivot and in the C/C-SiC at the dovetail inner radius.


## 5. SHEFEX II Flight Data from the TPS

Flight measurements have been transmitted to a ground station during the SHEFEX II flight. The data were transferred from the launch until the vehicle disappeared behind the horizon att=485.12s and h=29.2km. It is not known how far down the vehicle has withstood the thermal and aerodynamic load beyond this point. However, temporary reception of the parachute signal in the foreseen impact area indicates that the rest of the flight has passed according to plan. It can thus be concluded that the leading edge has successfully passed the aerothermal loads of the SHEFEX II flight. The data interpreted here for the TPS address mainly thermocouple measurements. The model HEATS serves to interpret the data and to reconstruct q̇ onto the wall.


### 5.1. Faceted TPS

Since the payload was rotationally symmetric and no payload fairing was necessary, atmospheric and payload response data could be recorded even during ascent. Each panel of the four instrumented quadrants 1, 3, 5, and 7 (see Figure1 for nomenclature) was equipped with three thermocouples along its lengthwise axis of symmetry [26, 27, 44].Figure18 shows the measured temperatures at the foremost thermocouple position along panel row 5 over the entire flight time. The figure shows that all panels faced a peak heating during ascent, with a maximum at h=32km altitude and u=1490m/s after approximately 49 s flight time but before first stage burnout. After ascent peak heating, the temperatures decrease due to the decreasing air density. The heat at the surface is transferred into the structure and vicinity by conduction and radiation until a state is reached at which the temperatures remain almost constant. This state holds on during the coast phase and flight past the apogee until reentry. First then, reincreasing convection surface heat flux leads to increasing temperatures.Figure 18
Measured temperatures at row 5.Figure18 shows that the shock and expansion fans, as expected, leads to the highest temperatures at the foremost segment A. At a decreasing panel deflection angle with respect to the flow, the temperatures decrease since the ambient temperatures behind the respective expansion fans decrease. Segment A, as shown in Figure 8, consists not of single panels as in the segments behind, but instead of two half shells, joined by joining elements, and an inlay in order to carry the solid sharp leading edge. The thin-walled mount, in turn, is attached to the aluminum substructure by Z-shaped CMC standoffs [39]. All of these elements act as heat sinks. This is why during ascent, the temperatures at panel A remain below those of panel B.Figure19 shows the measurement at panels B and D averaged over the four instrumented circumferential panels for the respective x-position over reentry flight time. The scatter of the values with respect to the angle of attack is represented by the scatter bars based on the standard deviation of the measurement. It can be seen that a prediction with HEATS, which takes into account a laminar-turbulent transition, overestimates the measurement by up to 23%, while the laminar consideration meets the measurement with a maximum deviation of 8.4% at panel D. Although a continuous laminar flow seems unrealistic, this indicates that the flow remains laminar longer than anticipated. This effect might originate from the reattachment of the flow after the Prandtl-Meyer-expansion at the vehicle facet corners. For classification, the Reynolds number is also plotted in Figure 19.Figure 19
Comparison of HEATS results to SHEFEX II measurement of panels B and D.When comparing the laminar prediction from HEATS, which neglects attachment, the deviation is small with 5.5–8.5% att=485.12s, but the measurement is systematically below the predicted temperatures. This suggests that heat is conducted away from the panel center by the central post, giving good contact to the substructure and serving as a heat sink. Overall, the flight data coincide well with the expected thermal response of the faceted acreage TPS with only small deviations.


### 5.2. Sharp Leading Edge

Thermocouple data from the positions shown in Figure9 are shown in dashed lines in Figure 20 and a detailed view is shown in Figure 21. Thin lines indicate the assumed flight path after the data transmission ended. Their maximum recorded temperature is 849°C, a temperature well below the material limit of C/C-SiC, at the altitude 30 km just before telemetry connection ended.Figure 20
In-flight thermocouple data for the SHEFEX II trajectory (Figure2) compared to prediction by HEATS.Figure 21
Detailed view of the atmospheric return flight phase of the SHEFEX II trajectory compared to prediction by HEATS.Applying the heat balance HEATS to the SHEFEX II return flight trajectory (Figure2) results in the simulated temperature response shown as solid lines in Figure 21. The in-flight measurements are in good concurrence with the expectation. Differences between simulation and measurement are attributed to uncertainties in the atmosphere model and the assumption of constant material properties [39].The subsequent flight path after telemetry ended is not exactly known. The heat balance gives the thermal response of the sharp leading edge as expected for the remaining descent as assumed in Figure2. The temperature of the leading edge at thermocouple position TC S02 is derived as 1817°C. The corresponding surface temperature with a maximum of 2344°C would have been above the material limit.


### 5.3. Transpiration-Cooled Experiment AKTiV

Figure22 shows the measurement of two temperature sensors on the porous sample of the cooled experiment and the uncooled reference set-up. For thermocouple locations, see Figure 15. Cooling with 0.4 g/s nitrogen was switched on via telecommand at 431 s. Before that, the structure was only subject to the ambient flow and shows the typical temperature maximum at ascent peak heating [42, 45].Figure 22
Comparison of sample temperatures on AKTiV and the reference set-up.It can be seen in Figures23 and 24 that upon the start of the coolant flow, i.e., from 431 s, the temperatures of the panel decrease, showing that transpiration cooling is effective. This is demonstrated by measurement on the porous sample itself, but also in the film cooling region downstream of the sample. The temperature difference with respect to the uncooled reference set-up is biggest for measurement location K38 with 87 K, which, according to equation (6), corresponds to a cooling efficiency of 58%. Downstream from the sample, the temperature is effectively reduced by 74.5 K at K33, resulting in a cooling efficiency of 42%.Figure 23
Temperatures on AKTiV and the reference set-up. Solid curves indicate thermocouple signals K29-K38 of the cooled experiment AKTiV while dashed curves represent signals K39-K46 of the uncooled reference with an identical set-up [42].Figure 24
More temperatures on AKTiV and the reference set-up. Solid curves indicate thermocouple signals K29-K38 of the cooled experiment AKTiV while dashed curves represent signals K39-K46 of the uncooled reference with an identical set-up [42].Figures22–24 also show the interesting effect that the temperatures reincrease after being cooled down from the timepoint of coolant switch-on. From this point, the cooling cannot compensate the increasing heat flux anymore; however, the temperatures are strongly reduced in comparison to the uncooled reference. This shows that the structure is not overcooled and still reacts to increasing heat flux. The same behaviour is predicted by the heat balances with HEATS. Figure 25 shows that the cooling is well reproduced by HEATS with only small deviations on the porous sample.Figure 25
Comparison of HEATS with up- and downstream measurements [42].Additionally, the results of AKTiV att=485.12s are plotted over distance x from the panel edge in Figure 26. Comparison to HEATS shows thermal response as expected on the impermeable C/C-SiC panel, while the steel reservoir is identified as a major heat sink on the cooled C/C sample. The sample temperatures had been expected to exceed those of the panel because of the lower heat conductivity of C/C and a thinner sample thickness than that of the panel. This is, however, compensated for by the set-up with the reservoir.Figure 26
AKTiV temperatures along the panel att=485.12 [42].However, Figure26 shows that the temperature is reduced by the coolant as shown by the graph for C3. The simulation with HEATS shows good agreement with the measurement values upstream and on the sample itself. The deviation from the measurement values on the sample is below 8%. Also the deviation of less than 6% from the measurement downstream the sample, i.e., in the film cooling region, shows that the heat balance well estimates the thermal response of the structure.Cooling efficiencies according to equation (6) are shown in Figure 27 for a reference coolant temperature of Tc=300K. Figures 23 and 24 had shown that upon return from the apogee, the sensor data of AKTiV deviated from that of the reference set-up on the opposite vehicle side by an average of 8.5 K. This deviation is not yet explained but cannot be accounted to aerodynamic effects since it originates at altitudes higher than those influenced by the atmosphere. This is only an apparent cooling efficiency with an average ηini=8.7% and has to be subtracted from the efficiencies displayed in Figure 27. The corrected cooling efficiency ηcorr=η−ηini, thus, is 51% and 58% up- and downstream on the porous sample, respectively. Downstream of the porous sample, it decreases with sensor distance from the sample with 42% and 30%. A cooling effect of the order of 11% can even be noticed upstream of the sample and it is assumed that heat conduction causes this cooling effect.Figure 27
AKTiV cooling efficiency forTc=300K [42].


## 5.1. Faceted TPS

Since the payload was rotationally symmetric and no payload fairing was necessary, atmospheric and payload response data could be recorded even during ascent. Each panel of the four instrumented quadrants 1, 3, 5, and 7 (see Figure1 for nomenclature) was equipped with three thermocouples along its lengthwise axis of symmetry [26, 27, 44].Figure18 shows the measured temperatures at the foremost thermocouple position along panel row 5 over the entire flight time. The figure shows that all panels faced a peak heating during ascent, with a maximum at h=32km altitude and u=1490m/s after approximately 49 s flight time but before first stage burnout. After ascent peak heating, the temperatures decrease due to the decreasing air density. The heat at the surface is transferred into the structure and vicinity by conduction and radiation until a state is reached at which the temperatures remain almost constant. This state holds on during the coast phase and flight past the apogee until reentry. First then, reincreasing convection surface heat flux leads to increasing temperatures.Figure 18
Measured temperatures at row 5.Figure18 shows that the shock and expansion fans, as expected, leads to the highest temperatures at the foremost segment A. At a decreasing panel deflection angle with respect to the flow, the temperatures decrease since the ambient temperatures behind the respective expansion fans decrease. Segment A, as shown in Figure 8, consists not of single panels as in the segments behind, but instead of two half shells, joined by joining elements, and an inlay in order to carry the solid sharp leading edge. The thin-walled mount, in turn, is attached to the aluminum substructure by Z-shaped CMC standoffs [39]. All of these elements act as heat sinks. This is why during ascent, the temperatures at panel A remain below those of panel B.Figure19 shows the measurement at panels B and D averaged over the four instrumented circumferential panels for the respective x-position over reentry flight time. The scatter of the values with respect to the angle of attack is represented by the scatter bars based on the standard deviation of the measurement. It can be seen that a prediction with HEATS, which takes into account a laminar-turbulent transition, overestimates the measurement by up to 23%, while the laminar consideration meets the measurement with a maximum deviation of 8.4% at panel D. Although a continuous laminar flow seems unrealistic, this indicates that the flow remains laminar longer than anticipated. This effect might originate from the reattachment of the flow after the Prandtl-Meyer-expansion at the vehicle facet corners. For classification, the Reynolds number is also plotted in Figure 19.Figure 19
Comparison of HEATS results to SHEFEX II measurement of panels B and D.When comparing the laminar prediction from HEATS, which neglects attachment, the deviation is small with 5.5–8.5% att=485.12s, but the measurement is systematically below the predicted temperatures. This suggests that heat is conducted away from the panel center by the central post, giving good contact to the substructure and serving as a heat sink. Overall, the flight data coincide well with the expected thermal response of the faceted acreage TPS with only small deviations.


## 5.2. Sharp Leading Edge

Thermocouple data from the positions shown in Figure9 are shown in dashed lines in Figure 20 and a detailed view is shown in Figure 21. Thin lines indicate the assumed flight path after the data transmission ended. Their maximum recorded temperature is 849°C, a temperature well below the material limit of C/C-SiC, at the altitude 30 km just before telemetry connection ended.Figure 20
In-flight thermocouple data for the SHEFEX II trajectory (Figure2) compared to prediction by HEATS.Figure 21
Detailed view of the atmospheric return flight phase of the SHEFEX II trajectory compared to prediction by HEATS.Applying the heat balance HEATS to the SHEFEX II return flight trajectory (Figure2) results in the simulated temperature response shown as solid lines in Figure 21. The in-flight measurements are in good concurrence with the expectation. Differences between simulation and measurement are attributed to uncertainties in the atmosphere model and the assumption of constant material properties [39].The subsequent flight path after telemetry ended is not exactly known. The heat balance gives the thermal response of the sharp leading edge as expected for the remaining descent as assumed in Figure2. The temperature of the leading edge at thermocouple position TC S02 is derived as 1817°C. The corresponding surface temperature with a maximum of 2344°C would have been above the material limit.


## 5.3. Transpiration-Cooled Experiment AKTiV

Figure22 shows the measurement of two temperature sensors on the porous sample of the cooled experiment and the uncooled reference set-up. For thermocouple locations, see Figure 15. Cooling with 0.4 g/s nitrogen was switched on via telecommand at 431 s. Before that, the structure was only subject to the ambient flow and shows the typical temperature maximum at ascent peak heating [42, 45].Figure 22
Comparison of sample temperatures on AKTiV and the reference set-up.It can be seen in Figures23 and 24 that upon the start of the coolant flow, i.e., from 431 s, the temperatures of the panel decrease, showing that transpiration cooling is effective. This is demonstrated by measurement on the porous sample itself, but also in the film cooling region downstream of the sample. The temperature difference with respect to the uncooled reference set-up is biggest for measurement location K38 with 87 K, which, according to equation (6), corresponds to a cooling efficiency of 58%. Downstream from the sample, the temperature is effectively reduced by 74.5 K at K33, resulting in a cooling efficiency of 42%.Figure 23
Temperatures on AKTiV and the reference set-up. Solid curves indicate thermocouple signals K29-K38 of the cooled experiment AKTiV while dashed curves represent signals K39-K46 of the uncooled reference with an identical set-up [42].Figure 24
More temperatures on AKTiV and the reference set-up. Solid curves indicate thermocouple signals K29-K38 of the cooled experiment AKTiV while dashed curves represent signals K39-K46 of the uncooled reference with an identical set-up [42].Figures22–24 also show the interesting effect that the temperatures reincrease after being cooled down from the timepoint of coolant switch-on. From this point, the cooling cannot compensate the increasing heat flux anymore; however, the temperatures are strongly reduced in comparison to the uncooled reference. This shows that the structure is not overcooled and still reacts to increasing heat flux. The same behaviour is predicted by the heat balances with HEATS. Figure 25 shows that the cooling is well reproduced by HEATS with only small deviations on the porous sample.Figure 25
Comparison of HEATS with up- and downstream measurements [42].Additionally, the results of AKTiV att=485.12s are plotted over distance x from the panel edge in Figure 26. Comparison to HEATS shows thermal response as expected on the impermeable C/C-SiC panel, while the steel reservoir is identified as a major heat sink on the cooled C/C sample. The sample temperatures had been expected to exceed those of the panel because of the lower heat conductivity of C/C and a thinner sample thickness than that of the panel. This is, however, compensated for by the set-up with the reservoir.Figure 26
AKTiV temperatures along the panel att=485.12 [42].However, Figure26 shows that the temperature is reduced by the coolant as shown by the graph for C3. The simulation with HEATS shows good agreement with the measurement values upstream and on the sample itself. The deviation from the measurement values on the sample is below 8%. Also the deviation of less than 6% from the measurement downstream the sample, i.e., in the film cooling region, shows that the heat balance well estimates the thermal response of the structure.Cooling efficiencies according to equation (6) are shown in Figure 27 for a reference coolant temperature of Tc=300K. Figures 23 and 24 had shown that upon return from the apogee, the sensor data of AKTiV deviated from that of the reference set-up on the opposite vehicle side by an average of 8.5 K. This deviation is not yet explained but cannot be accounted to aerodynamic effects since it originates at altitudes higher than those influenced by the atmosphere. This is only an apparent cooling efficiency with an average ηini=8.7% and has to be subtracted from the efficiencies displayed in Figure 27. The corrected cooling efficiency ηcorr=η−ηini, thus, is 51% and 58% up- and downstream on the porous sample, respectively. Downstream of the porous sample, it decreases with sensor distance from the sample with 42% and 30%. A cooling effect of the order of 11% can even be noticed upstream of the sample and it is assumed that heat conduction causes this cooling effect.Figure 27
AKTiV cooling efficiency forTc=300K [42].


## 6. Summary and Conclusion

The recent progress in material development and the improvement of lay-up and design calculation methods allow for a reconsideration of sharp leading-edge concepts for hypersonic flight. The faceted sharp-edged flight experiment served to investigate the applicability of CMCs for (a) slender and faceted, (b) sharp-leading-edged, (c) actively cooled, and (d) controllable hypersonic vehicles. SHEFEX II has flown from the Andøya Rocket Range in Norway on June 22nd 2012. It reached an approximately 180 km altitude and returned at Mach 10.2. All data were transmitted from the uncovered forebody from launch, throughout the ascent, apogee, and reentry until SHEFEX II dove behind the horizon and the transmission ended at an altitude of just below 30 km.Each flat TPS panel was instrumented with three thermocouples. As expected, the thermocouple readings show the highest temperatures at the foremost segment A. At a decreasing panel deflection angle with respect to the flow, the temperatures decrease since the ambient temperatures behind the respective expansion fans decrease. The comparison to expected temperatures predicted by a heat balance HEATS reveals heat sinks in the attachment system while the concurrence with the measurement is good with only 8% deviation.The octagonal sharp leading edge of SHEFEX II is made from a C/C-SiC-fiber-reinforced ceramic and has a leading-edge radius of <1 mm. It is instrumented by three thermocouples and eight pressure ports. The maximum temperature measured during flight was 867°C just before transmission ended and were predicted with an accuracy of the order of 10%. In conclusion, this shows that HEATS is a reliable tool for the prediction of the thermal response of a sharp leading edge. Although the SHEFEX II signal was lost, HEATS predicts for the anticipated subsequent flight segment that the temperature reached at the thermocouple position must have increased up to 1800°C. In turn, the leading-edge tip is determined to have reached more than 2300°C just before payload split.For the short flight time, these temperatures are considered as uncritical for the leading edge. For future entry or hypersonic flight missions, however, at higher velocity, the temperatures exceed the material limit and cooling methods have to be considered. A transpiration-cooling experiment AKTiV was therefore flown on SHEFEX II for the first time and has proven high efficiency for the cooling of a side panel. A reference set-up was located on the opposite panel. Upon start of the coolant flow, the panel temperatures are drastically reduced on the sample and in the coolant wake. As the heat flux increases, the cooled structure’s temperatures also increase at their lower level. This shows that the structure is not overcooled. The efficiencies at the maximum heating are 58% on the porous sample and 42% and 30% downstream of the sample in the wake. Future investigations address the application of this technology to a sharp leading edge which is subject to severe temperature and pressure gradients.Temporary reception of the parachute signal in the foreseen impact area indicates that the rest of the flight has passed according to plan. It can thus be concluded that the SHEFEX II has successfully withstood the aerothermal loads of the SHEFEX II flight. All structural challenges have thus been successfully solved, the flight data are within the expectation before the flight experiment, and the present TPS technologies were proven to be ready for practical use in future hypersonic flight.



---

*Source: 9754739-2019-11-18.xml*