# The High-Temperature Synthesis of the Nanoscaled White-Light Phosphors Applied in the White-Light LEDs

Authors: Hao-Ying Lu; Meng-Han Tsai
Journal: Advances in Materials Science and Engineering
 (2015)

---

## Abstract

The white-light phosphors consisting of Dy3+ doped YPO4 and Dy3+ doped YP1-XVXO4 were prepared by the chemical coprecipitation method. After the 1200°C thermal treatment in the air atmosphere, the white-light phosphors with particle sizes around 90 nm can be obtained. In order to reduce the average particle size of phosphors, the alkaline washing method was applied to the original synthesis process, which reduces the particle sizes to 65 nm. From the PLE spectra, four absorption peaks locating at 325, 352, 366, and 390 nm can be observed in the YPO4-based phosphors. These peaks appear due to  the following electron transitions: 6H15/2→4K15/2, 6H15/2→4M15/2+6P7/2, 6H15/2→4I11/2, and 6H15/2→4M19/2. Besides, the emission peaks of wavelengths 484 nm and 576 nm can be observed in the PL spectra. In order to obtain the white-light phosphors, the vanadium ions were applied to substitute the phosphorus ions to compose the YP1-XVXO4 phosphors. From the PL spectra, the strongest PL intensity can be obtained with 30% vanadium ions. As the concentration of vanadium ions increases to 40%, the phosphors with the CIE coordinates locating at the white-light area can be obtained.


---

## Body

## 1. Introduction

Due to the excellent luminescent properties and chemical stabilities, the phosphors using yttrium vanadate (YVO4) and yttrium phosphate (YPO4) as the host materials have been used in a broad range of daily life, such as the cathode ray tubes, electroluminescence devices, field emission displays, plasma display panels, projection displays, and ultraviolet light-emitting diodes (UV-LEDs) [1–4]. The europium (Eu3+) doped YVO4 phosphor especially is one of the excellent commercial red-light phosphors, which has been studied for many years [5–9]. In addition to the Eu3+ ions, the phosphor doped with dysprosium (Dy3+) ions is also a potential luminescent material. The active center Dy3+ can yield two emission bands: the yellow-light band and the blue-light band, and these two emission bands originate from the transition 4F9/2→6H15/2 and the transition 4F9/2→6H13/2, respectively.Through adjusting the relative intensities of yellow-light band and blue-light band, it is possible to obtain the white-light phosphors [8, 10–12]. Owing to the same crystal structure, similar lattice constants, and similar physical and chemical properties between YPO4 and YVO4 phosphors, the material Y(P,V)O4 has been paid much attention to in recent decades [13–15].In accordance with the above advantages, different synthesis methods were applied to produce the Y(P,V)O4 phosphors in recent years. Bao et al. synthesized the phosphors via the sol-gel method in 2008; the average particle size is around 80 nm with the 1000°C thermal treatment [16]. In 2009, Nguyen et al. applied the hydrothermal method to produce the Y(P,V)O4 phosphors, under the 1000°C synthesis temperature; the particle sizes are around 70 to 90 nm [17]. Additionally, the solid-state method is also a common method to synthesize the phosphors. Under the 1200°C thermal treatment for 6 hours, the phosphors with particle sizes around 2 to 4 μm can be obtained [18]. The methods above are either complicated or larger particle sizes. In this research, the chemical coprecipitation method with thermal treatments is adopted to synthesize the phosphors. In 2005, Su and Yanever used the similar processes to synthesize the Y(P,V)O4 phosphors at 1100°C, but the average particle sizes are around 0.5 to 2 μm [19]. In order to reduce the particle sizes, the alkaline-washing method was applied to the chemical coprecipitation method in this research and it can reduce the average particle size to 65 nm effectively.


## 2. Materials and Methods

In this study, yttrium nitrate hexahydrate Y(NO3)3·6H2O (99.9%, Alfa Aesar), dysprosium nitrate pentahydrate Dy(NO3)3·5H2O (99.9%, Alfa Aesar), phosphoric acid H3PO4 (85%, Panreac), and ammonium vanadate NH4VO3 (99.5%, Acros Organics) were used as the starting materials. At first, Y(NO3)3·6H2O, Dy(NO3)3·5H2O and H3PO4 were dissolved into distilled water by the stoichiometric ratio and the mixed solution was stirred for an hour at room temperature. Secondly, ammonia was used as the precipitant and added into the above solution. With the addition of ammonia, the pH value of mixed solution was adjusted to 8.0, and this solution was placed for 12 hours. After 12 hours, the white precipitation could be observed and separated directly by a centrifuge. Thirdly, the precipitation was washed by distilled water and ethanol for several times. Finally, the dried precipitation was used as the precursor to synthesize the YPO4:Dy3+ and YP1-XVXO4:Dy3+ phosphors by the suitable thermal treatment in the air atmosphere for 1 hour.Alkaline washing process: the precipitation was washed with ammonia and dried directly. Then, the dried powders can be used as the precursor.The X-ray diffraction patterns of phosphors were collected by Rigaku Miniflex II desktop X-ray diffractometer with Cu-Kα radiation. The particle morphology was studied by a field emission scanning electron microscope (FESEM, JEOL JSM-6500F). And the optical properties were studied with a fluorescence spectrophotometer (Hitachi F-2700PL).


## 3. Results and Discussion

Figure1 shows the XRD patterns of YPO4 phosphors with different thermal treatments. It can be seen from this figure that the three predominant peaks locating at 2θ = 25.9°, 35.0°, and 51.8° appear due to the following diffraction planes: (200), (112), and (312) of YPO4. Comparing with the JCPDS standard card (number 11-0254), the crystalline structures of all YPO4 phosphors prepared through the chemical coprecipitation method are confirmed as the tetragonal structures. No impurity phases resulting from the starting materials can be observed. As the thermal treatment temperature increases, the better crystallinity can be obtained.Figure 1
The XRD patterns of YPO4 phosphors with different thermal treatments.The scanning electron microscope (SEM) images are shown in Figure2. The irregular shape and agglomeration phenomenon of nanoparticles can be observed. The average particle size of phosphors is about 90 nm with the 1200°C thermal treatment and the agglomeration of phosphors is serious. From Figure 2(b), the particle size of phosphors reduces to 65 nm with the alkaline washing process and this process can also improve the agglomeration of phosphors.Figure 2
The SEM images of YPO4 phosphors with the 1200°C thermal treatment. (a) 1200°C. (b) 1200°C with the alkaline-washing process.
(a)
(b)Figure3 shows the XRD patterns of YPO4 phosphors with different dopant concentrations. In this figure, the lattice constants of phosphors change with the dopant concentrations, but all XRD patterns still exhibit the tetragonal structure. Small enlargement in the lattice constants of the YPO4:Dy3+ from YPO4 occurs due to the presence of Dy3+ (ionic radii of Dy3+ and Y3+ are 0.912 Å and 0.900 Å, resp.). The PLE spectra of YPO4:Dy3+ phosphors are revealed in Figure 4 with the emission wavelength (λem) 484 nm. Four absorption peaks can be observed from the PLE spectra. The 325 nm absorption peak originates from the f-f transition 6H15/2→4K15/2 within Dy3+. And the 352 nm, 366 nm, and 390 nm absorption peaks appear because of the following transitions: 6H15/2 →4M15/2 + 4P7/2, 6H15/2→4I11/2, and 6H15/2→4M19/2, respectively. Herein, the 352 nm peak is the strongest absorption peak of all peaks and is chosen as the excitation wavelength in the following PL measurements.Figure 3
The XRD patterns of YPO4 phosphors with different dopant concentrations.Figure 4
The PLE spectra of YPO4:Dy3+ phosphors with different dopant concentrations, λem = 484 nm.Figure5 demonstrates the PL spectra of YPO4:Dy3+ phosphors. Two emission peaks can be observed from the PL spectra. The 484 nm peak is the result from the transition 4F9/2→6H15/2 and the 576 nm peak occurs as the result of the transition 4F9/2→6H13/2. The PL intensity increases with the Dy3+ ion concentration. As the Dy3+ ion concentration increases to 0.8%, the phosphor can possess the strongest luminescent property. When the dopant concentration is above 0.8%, the concentration quench effect can be observed obviously.Figure 5
The PL spectra of YPO4:Dy3+ phosphors with different dopant concentrations, λexc = 352 nm.Figure6 shows the XRD patterns of Y0.992P1-XVXO4:0.008Dy3+ phosphors. The X means vanadium ion concentration and it starts from 0.1 to 0.5. As mentioned in [18], the cell parameters of YPO4 are a = b = 6.8817 Å; c = 6.0177 Å and those of YVO4 are a = b = 7.1183 Å; c = 6.2893 Å. When the concentration of vanadium ions increases, the angles of all diffraction peaks tend to be smaller (ionic radii of P5+ and V5+ are 0.34 Å and 0.59 Å, resp.). The lattice constant of Y0.992P1-XVXO4:0.008Dy3+ phosphor increases close to the lattice constant of YVO4 with vanadium quantity. Three predominant peaks locating at 25.4°, 34.2°, and 50.6° result from the diffraction planes (200), (112), and (312). The almost similar XRD patterns indicate that the presence of V5+ does not affect the crystal structure of the Y(P,V)O4 phosphors.Figure 6
The XRD patterns of Y0.992P1-XVXO4:0.008Dy3+ phosphors (X = 1 to 0.5).The PLE spectra of Y0.992P1-XVXO4:0.008Dy3+ phosphors are shown in Figure 7. With the emission wavelength 484 nm, 3 absorption peaks locating at 352, 366, and 390 nm can be observed. These peaks are the results of the following electron transitions: 6H15/2→4M15/2 + 6P7/2, 6H15/2→4I11/2 and 6H15/2→4M19/2, respectively. The 352 nm absorption peak is still the strongest absorption peak of all and is chosen as the excitation wavelength for the PL measurements. Figure 8 shows the PL spectra of Y0.992P1-XVXO4:0.008Dy3+ phosphors. These two emission peaks locating at 484 nm and 576 nm can be observed in the PL spectra. These two peaks originate from the electron transitions 4F9/2→6H15/2 and 4F9/2→6H13/2, respectively. As the concentration of vanadium ions increases, the PL intensity increases. When the vanadium concentration reaches 30%, the phosphor can possess the best emission property. According to the CIE coordinates in Figure 9, the phosphor Y0.992PO4:0.008Dy3+ can be used as a blue-white phosphor. With the addition of vanadium ions, the CIE coordinates can be adjusted to the white-light area. From Figure 9(b), the coordinates of phosphors with 40% and 50% vanadium concentration locate at (0.269, 0.317) and (0.279, 0.327).Figure 7
The PLE spectra of Y0.992P1-XVXO4:0.008Dy3+phosphors (X = 1 to 0.5), λem = 484 nm.Figure 8
The PL spectra of Y0.992P1-XVXO4:0.008Dy3+ phosphors (X = 1 to 0.5), λexc = 352 nm.Figure 9
The CIE coordinates of (a) YPO4:Dy3+ phosphor and (b) Y(P,V)O4:Dy3+ phosphors.
(a)
(b)


## 4. Conclusion

The white-light phosphors with average particle size 90 nm can be obtained through the chemical coprecipitation method with suitable thermal treatments in this study. The alkaline-washing process was applied to the original synthesis to reduce the average particle size. In this research, the particle size of phosphors can be reduced to 65 nm through the alkaline washing process and this process can also improve the agglomeration phenomenon. From the XRD patterns, the YPO4 phosphors with different thermal treatments all crystallize into the tetragonal structure. The lattice constant increases with the concentration of vanadium ions and tends to the lattice constant of YVO4. There are four absorption peaks observed in the PLE spectra, which are the results of the transitions 6H15/2→4K15/2, 6H15/2→4M15/2 + 4P7/2, 6H15/2→4I11/2, and 6H15/2→4M19/2. Additionally, two emission peaks locating at 484 nm and 576 nm can be observed in the PL spectra and they originate from the electron transitions, 4F9/2→6H15/2 and 4F9/2→6H13/2, respectively. By substituting the vanadium ions for the phosphorus ions in YPO4 phosphors, the relative intensities of these two emission peaks can be tuned to produce the white-light phosphor. The 40% vanadium concentration is the optimal condition to obtain the white-light phosphor Y0.992P0.6V0.4O4:0.008Dy3+ in our work. It is believed that the chemical coprecipitation method with thermal treatments is an effective way to obtain the white-light phosphors.



---