# Synthesis of Platinum Nanoparticles by Gamma Co-60 Ray Irradiation Method Using Chitosan as Stabilizer

Authors: Thi Kim Lan Nguyen; Ngoc Duy Nguyen; Van Phu Dang; Dinh Tuan Phan; Thai Hoa Tran; Quoc Hien Nguyen
Journal: Advances in Materials Science and Engineering
 (2019)

---

## Abstract

Platinum nanoparticles were synthesized using the gamma-ray irradiation as a reducing factor and chitosan as a stabilizer. The prepared platinum nanoparticles were characterized using ultraviolet-visible spectroscopy (UV-Vis), transmission electron microscopy (TEM), and Fourier-transform infrared spectroscopy (FT-IR). The saturated conversion dose to reduce the Pt4+ to Pt0 was found to be about 14 kGy for initial Pt4+ concentration of 1 mM. The size of the platinum nanoparticles (1.4–1.6 nm) did almost not change with the increase of chitosan concentration from 0.5 to 2.0%. Thus, gamma Co-60 ray irradiation method is favorable for synthesizing PtNPs with the small sizes.


---

## Body

## 1. Introduction

Platinum nanoparticles (PtNPs) have attracted great attention in many fields due to their applications in catalysis [1–7], such as in fuel cell technology [1], exhaust purification [2], automobile [3], and energy storage and sensors [8]. However, the possible applications are related to the size and morphology of PtNPs [1, 3, 8, 9]. PtNPs with small sizes possess a large number of surface atoms that affect its surface activity [8]. So, it is essential to prepare small size of PtNPs. The synthesis of PtNPs has already been studied using different methods such as chemical reduction [8–13], electrochemical deposition [1, 8], hydrothermal reduction [1, 3], biological synthesis [14], gamma Co-60 ray irradiation [4, 6], and polyol method [1]. In comparison with other methods, the gamma Co-60 ray irradiation is considered as an effective method for the synthesis of metal nanoparticles due to several advantages such as (1) the reduction reaction of metal ions performed at ambient condition; (2) the rate of reduction reaction can be properly controlled; (3) the reducing agents uniformly distributed in the solution; and (4) large-scale production can be favorably set up and satisfied with requirements of the clean production process [6]. Stabilizers, such as dextran [3], polyvinyalcohol, polyacrylic acid, and polyacrylate [4], and chitosan [5], and others must be used for the protection of PtNPs from agglomeration. Among stabilizers studied, chitosan (CTS) is widely used in the synthesis of metallic nanoparticles such as gold, platinum, silver, and palladium [10]. The CTS is one of the environmentally friendly polymers that is particularly interesting in the synthesis of metal nanoparticles due to its interactions with metal nanoparticles through both steric and electrostatic effect. The polymer molecules bind with the nanoparticles to prevent leaching from the catalysts. These characteristics make CTS an ideal material as catalystic support [1, 5, 11]. To the best of our knowledge, there has been no research on the synthesis of PtNPs with small size (1-2 nm) and narrow particle size distribution by the radiolytic method. In this study, the synthesis of PtNPs by the gamma Co-60 ray irradiation using CTS as a stabilizer was carried out, and the effect of CTS concentration on the size of PtNPs was also investigated.


## 2. Materials and Methods

### 2.1. Materials and Chemicals

Potassium hexachloroplatinate (IV) (K2PtCl6) was purchased from Merck. CTS with the molecular weight of ∼95,000 g/mol and deacetylation degree of ∼90% were supplied by a factory in Vung Tau Province, Vietnam. Lactic acid was purchased from Shanghai Chemical Reagent Co., China. Distilled water was used in all experiments.


### 2.2. Preparation of Pt4+/CTS Solution and Gamma-Ray Irradiation

Three-gram CTS was dissolved in 100 ml lactic acid 1.5% (v/v) to prepare a 3% (w/v) CTS solution. K2PtCl6 was then dissolved in CTS solutions to prepare Pt4+/CTS solutions with 1 mM Pt4+ and different CTS concentrations of 0.5, 1.0, and 2.0% (w/v). Then, the solutions of Pt4+/CTS were poured into glass bottles with caper and irradiated on the gamma Co-60 irradiator, STSV Co-60/B (Hungary), at VINAGAMMA Center, Ho Chi Minh City, with doses up to 17.5 kGy (dose rate of 1.25 kGy/h) measured by the dichromate dosimetry system [15].


### 2.3. Characterization of Colloidal PtNPs/CTS Solution

The UV-Vis absorption spectra of PtNPs/CTS solutions were measured on a UV-Vis spectrophotometer model Jasco-V630, Japan. The size and size distribution of the PtNPs were determined from TEM images on a transmission electron microscope model JEM 1010, JEOL, Japan, operating at 80 kV and statistically calculated using Photoshop software [16]. The FT-IR spectra of samples were measured on a FT-IR spectrometer 8400S, Shimadzu, Japan. For FT-IR measurement, the PtNPs/CTS solutions were dried at 60°C in a forced air oven. The dried PtNPs/CTS samples were ground into fine powder. After that, the powder samples of PtNPs/CTS were mixed with KBr and compressed into pellets with a thickness of 0.5 mm.


## 2.1. Materials and Chemicals

Potassium hexachloroplatinate (IV) (K2PtCl6) was purchased from Merck. CTS with the molecular weight of ∼95,000 g/mol and deacetylation degree of ∼90% were supplied by a factory in Vung Tau Province, Vietnam. Lactic acid was purchased from Shanghai Chemical Reagent Co., China. Distilled water was used in all experiments.


## 2.2. Preparation of Pt4+/CTS Solution and Gamma-Ray Irradiation

Three-gram CTS was dissolved in 100 ml lactic acid 1.5% (v/v) to prepare a 3% (w/v) CTS solution. K2PtCl6 was then dissolved in CTS solutions to prepare Pt4+/CTS solutions with 1 mM Pt4+ and different CTS concentrations of 0.5, 1.0, and 2.0% (w/v). Then, the solutions of Pt4+/CTS were poured into glass bottles with caper and irradiated on the gamma Co-60 irradiator, STSV Co-60/B (Hungary), at VINAGAMMA Center, Ho Chi Minh City, with doses up to 17.5 kGy (dose rate of 1.25 kGy/h) measured by the dichromate dosimetry system [15].


## 2.3. Characterization of Colloidal PtNPs/CTS Solution

The UV-Vis absorption spectra of PtNPs/CTS solutions were measured on a UV-Vis spectrophotometer model Jasco-V630, Japan. The size and size distribution of the PtNPs were determined from TEM images on a transmission electron microscope model JEM 1010, JEOL, Japan, operating at 80 kV and statistically calculated using Photoshop software [16]. The FT-IR spectra of samples were measured on a FT-IR spectrometer 8400S, Shimadzu, Japan. For FT-IR measurement, the PtNPs/CTS solutions were dried at 60°C in a forced air oven. The dried PtNPs/CTS samples were ground into fine powder. After that, the powder samples of PtNPs/CTS were mixed with KBr and compressed into pellets with a thickness of 0.5 mm.


## 3. Results and Discussion

The 1 mM Pt4+/1% CTS solution was irradiated with the different doses of 3.5, 7.0, 10.5, 14.0, and 17.5 kGy did almost not have clearly maximum absorption peak (λmax) in the wavelength range of the measured UV-Vis spectrum, but the absorbance was increased with the increase of dose up to 14 kGy (Figure 1). After irradiation, the color of the initial colorless Pt4+/CTS solutions was converted to brown color, and the higher the absorption dose, the darker the color of PtNPs/CTS solutions obtained. The same pattern of UV-Vis spectrum of PtNPs with no λmax was also reported by Yang et al. [3] using the chemical reduction, and by Remita et al. [4] and Choi et al. [6] using the gamma Co-60 ray irradiation method. However, Gharibshahi et al. [17] recently have reported that the PtNPs (2.8–4.4 nm) synthesized by the gamma-ray irradiation of 3.4 mM Pt4+ solution appeared two λmax in the UV-Vis spectrum, particularly the first peak in the range of 209–214 nm and the second one in the range of 257–262 nm. Furthermore, Cele et al. [18] reported that the PtNPs solutions prepared by the gamma-ray radiolytic method with the concentrations from 1 to 10 mM also had two λmax as in the study of Gharibshahi et al. [17] except for the sample of 1 mM PtNPs without λmax in the UV region due to less Pt atoms interacting with the light.Figure 1
UV-Vis spectra of CTS and Pt4+/CTS solutions irradiated with different doses.Figure1 shows that the CTS solution has a weak peak at ∼300 nm. All spectra of PtNPs/CTS solutions also manifested a weak peak at 260–300 nm with increased absorbance corresponding to the increase of the absorbed dose. This may be due to the formation of carbonyl groups from CTS by chain scission during irradiation [19]. Besides, the absorbance was increased with the increase of dose and reached a stable level at 14 kGy. So, it could be inferred that the absorbed dose of 14 kGy could be selected as the saturated conversion dose to completely reduce Pt4+ with the concentration of 1 mM to Pt0. The mechanism of PtNPs formation from Pt4+ ion solution by the gamma Co-60 ray irradiation was described in detail by Choi et al. [6] and Cele et al. [18]. Briefly, Pt4+ ions were reduced to Pt0 mainly by hydrated electrons (e−aq), hydrogen radicals (H˙), and hydroxyl radicals (˙OH). For ˙OH radicals, they were converted into secondary radicals by hydrogen abstraction from free radical scavengers (alcohol, polysaccharides, etc.) for reducing Pt4+ ions.The effect of CTS concentration was studied for the initial Pt4+ concentration of 1 mM. Figure 2 indicates that there was almost no difference among UV-Vis spectra of PtNPs/CTS samples with different CTS concentrations. In addition, the size of the radiolytic synthesized PtNPs in Figure 3 was virtually not affected by the CTS concentrations from 0.5 to 2.0%.Figure 2
UV-Vis spectra of PtNPs/CTS solutions with different CTS concentrations.Figure 3
TEM images and size distribution of PtNPs from 1 mM PtNPs in 0.5% CTS (a), 1.0% CTS (b), and 2.0% CTS (c).
(a)
(b)
(c)The synthesized PtNPs have a rather small size and narrow size distribution in the range of 1.4–1.6 nm (Figure3). The size of resultant PtNPs with the concentration of 1 mM in this study was smaller than the size of 4.4 and 7.4 nm for the PtNPs concentrations of 3.4 and 10 mM, respectively [17, 18]. Furthermore, the size of the synthesized PtNPs (1.4–1.6 nm) was also smaller than that of the PtNPs (3.4 nm) that were synthesized by the chemical method using NaBH4 as a reducing agent with the same initial concentration of 1 mM Pt4+ and 1% CTS as a stabilizer [5]. Moreover, the study on the synthesis of Ag and Au nanoparticles by the gamma Co-60 ray irradiation method using CTS as a stabilizer revealed that the size of Ag and Au nanoparticles was 4.6 and 9.8 nm for 1 mM Ag+ and Au3+ ions, respectively [16, 20]. Thus, it is obvious that the size of PtNPs synthesized by the gamma Co-60 ray irradiation method is smaller than that of Ag and Au nanoparticles at the same initial concentration of metal ions. The reason for this phenomenon is still not clear. Furthermore, it is interesting to note that, according to Choi et al. [6], the size of PtNPs which was synthesized by the gamma Co-60 ray irradiation using polyvinyl pyrrolidone as a stabilizer and the Pt4+ ions concentration of 0.2 mM could not be predicted from TEM images due to the morphology of particles was not clear. Therefore, further study of the effect of stabilizers on the morphology and size of PtNPs synthesized by the gamma-ray irradiation method should be carried out.The FT-IR spectra of CTS and PtNPs/CTS are shown in Figure4. The FT-IR spectrum of the CTS possesses the main characteristic peaks that appear at 3448 cm−1 for O-H and N-H stretch; 2937 cm−1 and 2981 cm−1 for C-H stretch [21]; 1641 cm−1 for C=O stretching vibration in amide I; 1591 cm−1 for N-H deformation vibration in amide II; 1413 cm−1 and 1380 cm−1 for acetamide stretching and C-CH3 deformation vibration of amide groups; 1126 cm−1 for antisymmetric stretch C-O-C and C-N stretch; and 1089 cm−1 and 1031 cm−1 for skeletal vibration of C-O stretch [21, 22]. The FT-IR spectra of PtNPs/CTS samples with different concentrations of CTS in Figure 4 are almost similar to that of CTS. However, the main difference was that the peak at 3448 cm−1 of CTS shifted to lower wavenumbers, particularly at 3382, 3269, and 3236 cm−1 for PtNPs/CTS samples with CTS concentration of 2.0, 1.0, and 0.5%, respectively. Thus, on the basis of the FT-IR spectra of PtNPs/CTS in Figure 4, it presumed that the interaction between CTS molecules and PtNPs has occurred. The obtained FT-IR spectra in this study were also consistent with that in the study of Geng et al. [21] using chitosan as a stabilizer for the synthesis of Fe nanoparticles.Figure 4
FT-IR spectra of CTS and PtNPs/CTS samples with different CTS concentrations.Chitosan, hyaluronan, and alginate with oxygen-rich structures lead to binding them to metal nanoparticles tightly via steric and electrostatic interactions [23]. On the basis of the stabilizing interaction of polysaccharides to metal nanoparticles, a schematic diagram of chitosan capped PtNPs which were synthesized using the gamma Co-60 ray irradiation was proposed as in Figure 5. Furthermore, the spherical PtNPs with the small size (1-2 nm) were favorably synthesized using the gamma Co-60 ray irradiation. And this method has been considered as a green production method with favorable large-scale production [24, 25].Figure 5
Schematic diagram of chitosan capped PtNPs synthesized by the gamma Co-60 ray irradiation.


## 4. Conclusions

The gamma Co-60 ray irradiation has been as an effective method for synthesizing PtNPs dispersed in the CTS solution. The saturated conversion dose (Pt4+ ⟶ Pt0) for the initial Pt4+ concentration of 1 mM was found out to be ∼14 kGy. The resultant PtNPs with the small size (1.4–1.6 nm) could be potentially applied in catalyst materials and other purposes of applications as well.



---

*Source: 9624374-2019-04-18.xml*