# Reducing Water Vapor Permeability of Poly(lactic acid) Film and Bottle through Layer-by-Layer Deposition of Green-Processed Cellulose Nanocrystals and Chitosan

Authors: Katalin Halász; Yanin Hosakun; Levente Csóka
Journal: International Journal of Polymer Science
 (2015)

---

## Abstract

Layer-by-layer electrostatic self-assembly technique was applied to improve the barrier properties of poly(lactic acid) (PLA) films and bottles. The LbL process was carried out by the alternate adsorption of chitosan (CH) (polycation) and cellulose nanocrystals (CNC) produced via ultrasonic treatment. Four bilayers (on each side) of chitosan and cellulose nanocrystals caused 29 and 26% improvement in barrier properties in case of films and bottles, respectively. According to the results the LbL process with CH and CNC offered a transparent “green” barrier coating on PLA substrates.


---

## Body

## 1. Introduction

Poly(lactic acid) (PLA) is a biodegradable and compostable bioplastic, which can be used widely in the packaging industry due to its heat formability, injection, and blow moldability and due to its properties like excellent transparency, good oil, chemical and UV resistance, and satisfying mechanical and thermal properties. However, PLA is not suitable for liquid products where long shelf-life is demanded, for products which are sensitive to moisture or for carbonated beverages because of the high water vapor and gas permeability. To make PLA an appropriate packaging material for these kinds of products, improvement of its barrier properties is required.Layer-by-layer coating technique, which is based on the self-assembly of polyelectrolytes and/or nanoparticles on substrates, has many advantages compared to other coating methods like spin coating, thermal deposition, or solution casting. According to Jang et al. [1] LbL self-assembled nanostructured coatings provide both transparency and flexibility, making them good alternatives in packaging applications. The process is inexpensive, simple, and quick and it can be carried out in water media excluding using harmful and toxic solvents. It offers ultrathin film creation with desired composition and properties on several kinds of substrates with different sizes, irregular shapes, and 3D forms. A wide variety of materials can be used to perform the LbL deposition including inorganic or organic polycations, polyanions, and nanoparticles which have surface charges when solved or dispersed in water (or other processing media). LbL self-assembly is based on electrostatic attractions between the oppositely charged constituents, although hydrogen-bonding, van der Waals forces or charge-transfer interactions can also play a role in the thickness or in the stability of the self-assembled layers. With LbL deposition, ultrathin mono-, bi-, or multilayer coating can be achieved with more than 1 nm precision. The properties of the films can be fine-tuned by varying the process parameters like components, concentration, pH, ionic strength, and immersion time [2–6].Recent studies showed that montmorillonite (MMT) and poly(ethylene-imine) (PEI) bilayers can enhance the oxygen barrier properties of PET films [7, 8] and water vapor barrier properties of cellulose films [6] as well. Findenig et al. [6] also examined 2-hydroxy-3-trimethylammonium propyl chloride (HPMA) starch, PDDA, and chitosan as polyelectrolytes. It was concluded that it is possible to improve the water vapor barrier properties with hydrophilic components; they observed that PEI and HPMA starch are the most suitable for the preparation of transparent barrier coatings. Although chitosan was not as effective as PEI or starch in case of reducing the water vapor transmission rate with MMT, it was suitable for reducing oxygen transmission not only in case of PET but also in case of PLA reported by Svagan et al. [9] and Laufer et al. [10]. Svagan et al. [9] observed 95% reduction in oxygen permeability and 20% reduction in water vapor transmission after deposition of 70 MMT-CH bilayers. Laufer et al. [10] created 10 quadrat layers (CH-PAA-CH-MMT) on PLA and PET films which could significantly reduce the oxygen permeability of both packaging materials. Laufer et al. [11] also reported a high barrier effect with high transparency of 10 trilayers of CH-MMT-CR (carrageenan) and 10 quadrat layers of CH-CR-CH-MMT.According to the literature, the most extensively studied LbL barrier coating nanomaterial is the layered silicate montmorillonite [6–10]; however, other materials might be suitable for barrier improvers as well. Hagen et al. [12] recently showed that polyelectrolytes can be enough to reduce the oxygen transmission rate, and eight bilayers of PEI-PAA (poly(acrylic acid)) deposited onto PET film could lead to undetectable oxygen transmission rate. Hirvikorpi et al. [13] created ultrathin multilayer on PLA film substrate from sodium alginate, chitosan (deposited by LbL method), and Al2O3 nanoparticles (deposited by atomic layer deposition). In contrast to Hagen et al. [12], they observed that multilayer containing only polyelectrolytes enhanced the WVTR while coating with an extra Al2O3 layer the WVTR became significant (47%) lower.In this study, chitosan and “green-” processed cellulose nanocrystal were deposited on poly(lactic acid) film and bottle with the aim of reducing water vapor transmission rate.


## 2. Materials and Methods

Poly(lactic acid) film was extruded with the thickness of 30 microns using Esun AI1031 transparent PLA granulates (Shenzhen Bright China Industrial Co.). PLA bottles with wall thickness of 680 microns and inner volume of 150 mL were kindly provided by Biopackpro Ltd. Microcrystalline cellulose (particle size < 20μm) and chitosan were obtained from Sigma Aldrich.To create cellulose nanocrystal colloid ultrasonic treatment of the MMC in distilled water was applied. The concentration of the suspension was set to 1.0 wt% and the sonication was carried out using ultrasonic horn with 20 kHz (35 W/cm2) for 80 min. After sonication of the sediment, larger cellulose particles were removed, dried, and weighted in order to define the final concentration of the CNC colloid which was given to be 0.7 wt%. To prove that the treated cellulose is nanosized, solvent exchange was carried out with acetone. The resulting material which was a nanocellulose gel can be seen in Figure 1. Although the appearance of the cellulose nanocrystals has not been examined in this research, according to our previous study, we can assume that the ultrasonically produced, above described, cellulose nanocrystal might have spherical form rather than whisker, which can be obtained through the acidic hydrolysis [14, 15].Figure 1
Nanocellulose gel formed after sonication and solvent exchange.The positively charged chitosan polyelectrolyte solution was prepared by dissolving CH (0.1 wt%) in 0.1 M lactic acid. To achieve less expanded polymer coil, thus obtaining thicker chitosan layers in the multilayer, the pH was adjusted to 6 by adding 1 M NaOH to the polyelectrolyte solution.Layer-by-layer method was carried out as follows: the PLA films and bottles were immersed into the positively charged chitosan solution; after rinsing the packaging objects with distilled water they were immersed into the negatively charged CNC colloid until reaching the adsorption equilibrium. After alternate adsorption of CH and CNC, 4 and 8 bilayers were built up on each side of the substrates.


## 3. Characterization

To monitor the formation of the deposited layers, to make gravimetric and thickness analysis Quartz Crystal Microbalance (QCM) measurement was carried out. Since the deposition of mass onto the quartz crystal surface causes a measurable frequency shift, the adsorbed mass and the layer thickness were calculated with the Sauerbrey equation. To prevent measuring failure, which comes from the density and pressure of the liquids after the immersions, before the measurement, drying was applied. The surface modifying effects of the resulted coatings on the PLA substrates were tested by contact angle measurement with PGX goniometer. The microstructure of the surface was characterized by scanning electron microscopy (SEM) (Hitachi S-3400N), where the acceleration voltage was 20 kV. UV-VIS spectrophotometry was used to evaluate the transmittance of the coated PLA films in the visible range (400–800 nm). Transmittance of the films was measured in three different sites. Water vapor transmission rate tests were done in a climate chamber at 23°C and 85 RH% for 7 days in the case of both films and bottles. During the tests, three samples of each of modified PLA films and bottles and control samples were tested.


## 4. Results and Discussions

Figure2 shows the results of the Quartz Crystal Microbalance and contact angle, surface energy (γsd) measurements. According to the QCM CH and CNC required approximately 2 and 4 minutes, respectively, to achieve the adsorption equilibrium. The layer growth was linear and each layer contained around 2–2.4 μg/cm2 chitosan and cellulose. As QCM showed the thickness of the deposited chitosan layer was around 50 nm and the thickness of the CNC layer was approximately 20 nm which indicates also that the maximal size of the ultrasonically produced CNC is around 20 nm if we assume that a monolayer was formed on the substrate. Thickness of the LbL deposited multilayer film (consisting of 4 bilayers of CH and CNC) formed on the quartz crystal surface was 196 nm. The 4 bilayers deposited on PLA films caused surface energy shift from 39.5 mN/m to 41.8 mN/m. In case of 8 bilayers, the thickness of the multilayer increased to 452 nm and the surface energy of the PLA increased from 39.5 to 44.3 mN/m. During the LbL process, uniform layer deposition and reproducible film growth were achieved.Figure 2
Thickness of the deposited CH and CNC layers and surface energy change in a function of deposition cycles.According to the SEM images (Figure3) of the neat and coated PLA films, either under 130x or under 1600x magnification, well-packed, dense multilayers without aggregation of the CNC particles were deposited onto the PLA substrate. Before the scanning electron microscopy the films were bent, but as the SEM images show it had no visible effect on the coatings, no microcracking could be observed.Figure 3
SEM images of the neat and coated PLA films.UV-VIS spectrophotometry revealed that, in the range of visible radiation, the transmittance of the coated PLA films slightly, but not remarkably, decreased. The neat PLA film has 89% (σ=3) transmittance and the coated PLA films, 4∗CH-CNC and 8∗(CH-CNC), have 85 (σ=2) and 82% (σ=3), respectively. Figure 4 shows the transparency of the modified and unmodified samples. The coating caused only slight little scattering in the visible range so it can be concluded that the deposited films are thin, uniform, and homogenous (in accordance with the observations during scanning electron microscopy). The negligible decrease in transmittance shows also that the cellulose particles, formed during the ultrasonic treatment, are in the nanometer range.Figure 4
Neat (A) and coated PLA films ((B)4∗CH-CNC and (C) 8∗(CH-CNC)).According to the water vapor transmission rate tests, whose results are presented in Figure5, in case of 4∗CH-CNC films 29% less water vapor was permeated through the material compared to in case of the neat PLA films. However, the 8∗(CH-CNC) films showed almost as high WVTR as the neat PLA. Although chitosan is a hydrophobic polymer the high water content of the environment might have a plasticizing effect on the chitosan as Svagan et al. [9] reported. Analogue to Svagan et al.’s [9] observation, in case of CH and MMT, the presence of water could interfere with the molecular interaction between CH and CNC with increased mobility of CH (which increases free volume) in the interfacial areas, which could modify the structure of the coating thus reducing the barrier effect. In case of bottles, the same phenomenon was observed. Presumably at the outmost layer there is an extensive interpenetration of deposited layers. Such phenomenon was observed by Fu et al. (2005) [16]. Many chitosan chains from the underlying layer can penetrate into the surface of the outmost CNC layer. The penetration perhaps can enhance the plasticizing effect of moisture on chitosan and hence reduce the water vapor barrier property. Figure 6 shows the assumed water vapor transmission rate reducing mechanism of the CH-CNC nanocoating. The barrier effect presumably can be attributed to the cellulose nanocrystals rather than to the chitosan. It has been shown that cellulose nanocrystals can significantly decrease the WVTR if it is used as reinforcement even in small ratios in PLA matrix [17, 18]. Though the barrier effect of the polymer is might be not as negligible either it rather acts as a binder and the nanoparticles as nanoshield. If the nanoparticles are tightly packed and impermeable to water vapor (which can occur if the cellulose is highly crystalline) these can cause an extreme tortuous path to water vapor molecules, thus reducing the rate of their passage through the material.Figure 5
The water vapor transmission rate of neat and coated PLA films (a) and bottles (b).
(a)
(b)Figure 6
Schematic illustration of water vapor transmission rate reducing mechanism of CH-CNC nanocoating.


## 5. Conclusions

Multilayer built up with chitosan and ultrasonically green-produced cellulose nanocrystals form a dense, well-packed, well-adsorbed biocoating was carried out, which can improve the barrier properties of the PLA films and bottles up to 4 bilayers on each side. Due to the high water vapor transmission, PLA is mostly applied for short shelf-life products. In case of LbL-coated4∗CH-CNC PLA films or bottles the shelf-life can be extended with almost 1/3 times. The CH-CNC coating could be suitable for food packaging applications since chitosan is already applied in the food industry and cellulose nanomaterials are also proven to be noncytotoxic [19–21]. Furthermore CH and CNC suit the PLA as well because of the biodegradability and compostability of both materials.Layer-by-layer electrostatic deposition can be an effective method in creating barrier coatings on PLA with choosing the suitable components; furthermore besides barrier properties, other functionalities can be provided to the material with chitosan and cellulose nanocrystals like antimicrobility or wear resistance [16, 17, 22–24]. However, to validate the usability of such coatings, to prove that there is no migration of the constituents into the contained liquid, further investigation is required.



---

*Source: 954290-2015-04-08.xml*