# CdSe Quantum Dots for Solar Cell Devices

Authors: A. B. Kashyout; Hesham M. A. Soliman; Marwa Fathy; E. A. Gomaa; Ali A. Zidan
Journal: International Journal of Photoenergy
 (2012)

---

## Abstract

CdSe quantum dots have been prepared with different sizes and exploited as inorganic dye to sensitize a wide bandgap TiO2 thin films for QDs solar cells. The synthesis is based on the pyrolysis of organometallic reagents by injection into a hot coordinating solvent. This provides temporally discrete nucleation and permits controlled growth of macroscopic quantities of nanocrystallites. XRD, HRTEM, UV-visible, and PL were used to characterize the synthesized quantum dots. The results showed CdSe quantum dots with sizes ranging from 3 nm to 6 nm which enabled the control of the optical properties and consequently the solar cell performance. Solar cell of 0.08% performance under solar irradiation with a light intensity of 100 mW/cm2 has been obtained. CdSe/TiO2 solar cells without and with using mercaptopropionic acid (MPA) as a linker between CdSe and TiO2 particles despite a Voc of 428 mV, Jsc of 0.184 mAcm−2, FF of 0.57, and η of 0.05% but with linker despite a Voc of 543 mV, Jsc of 0.318 mAcm−2 , FF of 0.48, and η of 0.08%, respectively.


---

## Body

## 1. Introduction

Nanocrystals or quantum dots (QDs) are currently a subject of intense research activity targeting a wide range of potential applications, including light-emitting diodes (LEDs) [1, 2], photovoltaics [3, 4], single-electron transistors [5], and fluorescent tags for biological imaging [6, 7]. The utility of nanocrystals lies in their unique size-dependent optical and electronic properties, chiefly a size-tunable optical absorption and emission spectra [8]. According to these unique properties, the recent interest in utilizing semiconductor nanocrystals (or quantum dots) for harvesting light energy has drawn great attention toward metal-chalcogenide-based system [4, 9]. Of particular interest are CdX and PbX (X = S, Se, and Te) QDs, which have relatively small bandgaps and thus are capable of harvesting photons in the visible and infrared region [10]. These materials have been employed in three different types of quantum dot solar cells [11]: (i) metal junction solar cells, (ii) polymer hybrid solar cells, and (iii) quantum dot-sensitized solar cells (QDSCs). In the metal junction solar cells, charge separation is achieved at metal semiconductor interface upon visible laser excitation. The polymer hybrid solar cells utilize blends of conducting polymers (e.g., poly(3-hexylthiophene)) and QDs to facilitate charge separation and charge transport. In the case of the QDSCs, excited electrons of semiconductor nanocrystals are injected into a large bandgap semiconductor such as TiO2 or ZnO, and holes are scavenged by a redox couple [4].Research on the preparation of the QDs concentrates on the syntheses and characterizations of the monodisperse QDs, especially the studies of nucleation and growth mechanisms as well as the improvement of the luminescence quantum yields (QY). The most popular route to synthesize CdSe quantum dots is the method using organometallic compounds [12]: dimethylcadmium ((CH3)2Cd) reacts with a selenium reagent in the presence of trioctylphosphine oxide (TOPO) surfactant at high temperature (300°C). Careful control of reaction conditions produces CdSe quantum dots that are quite homogeneous in size and tunable in size from 2 to 8 nm. However, ((CH3)2Cd) is extremely toxic, pyrophoric, unstable at room temperature, and explosive at elevated temperatures by releasing large amounts of gas. Because of these reasons, the (CH3)2Cd-related schemes require very restricted equipments and conditions and are not suitable for large-scale synthesis. In a recent development, Z. A. Peng and X. Peng [13] reported the use of less toxic and reactive cadmium oxide (CdO) with hexylphosphonic acid (HPA) or tetradecylphosphonic acid (TDPA), as an alternative to (CH3)2Cd in TOPO syntheses of CdX.In this paper, we chose different reagents as reaction media and low-toxic, air-stable inorganic reagents as precursors to synthesize CdSe QDs such as CdO instead of dimethyl cadmium and study the effect of solvent (TOPO & TOP) and the ratio of CdO to Se on the growth and the yield of QDs. Then use these CdSe QDs as sensitizer for TiO2 nanoparticles prepared by Kashyout et al. 2010 [14]. TiO2 films prepared by doctor-blade technique on ITO (14 Ω/□)/glass that prepared by Kashyout et al. 2011 [15] using sputtering technique. QDs linked to TiO2 film by using 3-mercaptopropionic acid as a linker [16].


## 2. Materials and Methods

### 2.1. Materials

Cadmium oxide CdO (99.5%, Alpha), selenium powder Se (99%, Alfa Aesar), trioctylphosphine (TOP) (99%, Aldrich), trioctylphosphine oxide (TOPO) (99%, Aldrich), hexadecylamine (HDA) (99%, Aldrich), Stearic acid (SA) (99.5%, Aldrich), and 3-mercaptopropionic acid (MPA) (99%, Alfa Aesar).


### 2.2. Methods

#### 2.2.1. Preparation of CdSe QDs

This reaction procedure was originally reported by Z. A. Peng and X. Peng [13]. Figure 1 shows scheme for the preparation reaction of CdSe QDs. Se injection solution was prepared under nitrogen by mixing Se powder and TOP in a scintillation vial, which was capped by a rubber septum and fixed with two turns of Cu wire. After ~30 min of heating (~150°C, on a hot plate) and vigorously stirring with a PTFE stir bar, the suspended Se became soluble to afford a light-yellow solution. The Se solution is allowed to cool to room temperature in the presence of nitrogen gas instead of air before injection into a heated Cd solution.Figure 1
Scheme for the preparation  reaction of CdSe QDs.In a laminar flow hood, CdO and SA were loaded into a 3-neck round-bottom flask. The reaction flask is heated to 150°C in air with a round bottom heating mantle. After ~30 min, the reddish-brown slurry became optically clear indicating formation of cadmium stearate. To the hot reaction vessel, HDA and TOPO were added. The reaction flask was backfilled with N2 and heated to 320°C. At this temperature, the selenium solution was swiftly injected into the reaction flask.Upon injection, the solution temperature dropped to 280°C. The solution was maintained at 280°C for the desired amount of time to reach the desired NC size. The round-bottom flask was then removed from the heating mantle and quickly cooled to ~70°C. CdSe QDs washed more than three times by using ethanol and acetone.Table1 illustrates the different preparation parameters, which are used for the preparation of CdSe QDs.Table 1
Different preparation parameters used for the preparation of CdSe QDs.
Sample no.CdO (gm)Se (gm)TOPO (gm)TOP (mL)HAD (gm)SA (gm)Reaction time (sec.)S10.08290.0519.836.259.730.897460S20.08290.0519.836.259.730.897440S30.08290.0519.836.259.730.897420S40.08290.0519.836.259.730.897410S50.08290.05110109.730.897460S60.08290.05115109.730.897460S70.08290.0515109.730.897460S80.08290.10210109.730.897460S90.08290.15310109.730.897460S100.08290.25510109.730.897460S110.08290.35710109.730.897460


#### 2.2.2. Preparation of TiO2 Thin Films

The ITO/glass which is used as current collector (14 Ω/□) [15] was first cleaned in water and then acetone using an ultrasonic bath for 15 min. A layer of TiO2 paste was coated on the ITO glass plates by spinner coating method (wafer spinner machine (100 rpm, 2 min)), then allowed to dry in air and followed by heat treatment at 450°C for 30 min. This procedure with TiO2 paste (coating, drying, and heat treatment) was repeated to get the appropriate thickness of about 10 μm for the working electrode.


#### 2.2.3. Preparation of CdSe QDs/TiO2 Films

TiO2 thin films were dipped into a solution of N2 purged acetonitrile containing carboxyalkanethiol such as 3-mercaptopropionic acid (1 : 10 ratio) for 24 hrs. Resulting TiO2 films, functionalized with these bifunctional surface modifiers, were washed with both acetonitrile and toluene and then immersed in a suspension of CdSe solution for 24 hrs [17].


#### 2.2.4. Fabrication of QDs/TiO2 Solar Cells

The counter electrode was placed directly on the top of the QDs/TiO2 film, supported by the conducting glass sheet. Both electrodes were clamped tightly together. Drops of electrolyte (0.5 M LiI/50 mM I2 in solvent of 3-methoxypropionitrile) and 0.5 M 4-tert-butylpyridine were added to the standard electrolyte solution in order to increase the stability of the electrolyte. The QDs/TiO2 film was illuminated through the conducting glass substrate to measure the cell performance.


#### 2.2.5. Characterization of CdSe QDs

The structural properties of these organic species were confirmed by the powder X-ray diffraction (XRD) using (Shimadzu 7000, Japan) diffractometer, operating with Cu Kα radiation (λ = 0.15406 nm) generated at 30 kV and 30 mA. Scans were done at 4° min−1 for 2θ values between 20 and 60°. The morphologies and the crystallite size of TiO2 nanoparticles were observed by high-resolution transmission electron microscopy (HRTEM) (JEOLJEM-2100F, Japan). To identify and characterize the organic species on the surfaces, the Fourier transform infrared spectroscopy (FT-IR) spectra were obtained using a Shimadzu FTIR-8400 S, Japan. The absorption spectra and their photoluminescence properties were characterized by means of LABOMED double-beam UV-Vis spectrophotometer with spectrum range from 190 to 1100 nm and using a Varian Cary Eclipse spectrofluorometer.


#### 2.2.6. Characterization of QDs/TiO2 Solar Cells

The QDs/TiO2 solar cell performance was measured using solar simulator device (PET Photo Emission Tech., Inc., USA). The solar simulator simulates the AM1.5 spectrum by using xenon lamp, and the light intensity could be controlled from 0.1 Sun to 1.25 Sun. The cell ambient temperature was controlled at 25°C using a control system attached to the solar simulator.


## 2.1. Materials

Cadmium oxide CdO (99.5%, Alpha), selenium powder Se (99%, Alfa Aesar), trioctylphosphine (TOP) (99%, Aldrich), trioctylphosphine oxide (TOPO) (99%, Aldrich), hexadecylamine (HDA) (99%, Aldrich), Stearic acid (SA) (99.5%, Aldrich), and 3-mercaptopropionic acid (MPA) (99%, Alfa Aesar).


## 2.2. Methods

### 2.2.1. Preparation of CdSe QDs

This reaction procedure was originally reported by Z. A. Peng and X. Peng [13]. Figure 1 shows scheme for the preparation reaction of CdSe QDs. Se injection solution was prepared under nitrogen by mixing Se powder and TOP in a scintillation vial, which was capped by a rubber septum and fixed with two turns of Cu wire. After ~30 min of heating (~150°C, on a hot plate) and vigorously stirring with a PTFE stir bar, the suspended Se became soluble to afford a light-yellow solution. The Se solution is allowed to cool to room temperature in the presence of nitrogen gas instead of air before injection into a heated Cd solution.Figure 1
Scheme for the preparation  reaction of CdSe QDs.In a laminar flow hood, CdO and SA were loaded into a 3-neck round-bottom flask. The reaction flask is heated to 150°C in air with a round bottom heating mantle. After ~30 min, the reddish-brown slurry became optically clear indicating formation of cadmium stearate. To the hot reaction vessel, HDA and TOPO were added. The reaction flask was backfilled with N2 and heated to 320°C. At this temperature, the selenium solution was swiftly injected into the reaction flask.Upon injection, the solution temperature dropped to 280°C. The solution was maintained at 280°C for the desired amount of time to reach the desired NC size. The round-bottom flask was then removed from the heating mantle and quickly cooled to ~70°C. CdSe QDs washed more than three times by using ethanol and acetone.Table1 illustrates the different preparation parameters, which are used for the preparation of CdSe QDs.Table 1
Different preparation parameters used for the preparation of CdSe QDs.
Sample no.CdO (gm)Se (gm)TOPO (gm)TOP (mL)HAD (gm)SA (gm)Reaction time (sec.)S10.08290.0519.836.259.730.897460S20.08290.0519.836.259.730.897440S30.08290.0519.836.259.730.897420S40.08290.0519.836.259.730.897410S50.08290.05110109.730.897460S60.08290.05115109.730.897460S70.08290.0515109.730.897460S80.08290.10210109.730.897460S90.08290.15310109.730.897460S100.08290.25510109.730.897460S110.08290.35710109.730.897460


### 2.2.2. Preparation of TiO2 Thin Films

The ITO/glass which is used as current collector (14 Ω/□) [15] was first cleaned in water and then acetone using an ultrasonic bath for 15 min. A layer of TiO2 paste was coated on the ITO glass plates by spinner coating method (wafer spinner machine (100 rpm, 2 min)), then allowed to dry in air and followed by heat treatment at 450°C for 30 min. This procedure with TiO2 paste (coating, drying, and heat treatment) was repeated to get the appropriate thickness of about 10 μm for the working electrode.


### 2.2.3. Preparation of CdSe QDs/TiO2 Films

TiO2 thin films were dipped into a solution of N2 purged acetonitrile containing carboxyalkanethiol such as 3-mercaptopropionic acid (1 : 10 ratio) for 24 hrs. Resulting TiO2 films, functionalized with these bifunctional surface modifiers, were washed with both acetonitrile and toluene and then immersed in a suspension of CdSe solution for 24 hrs [17].


### 2.2.4. Fabrication of QDs/TiO2 Solar Cells

The counter electrode was placed directly on the top of the QDs/TiO2 film, supported by the conducting glass sheet. Both electrodes were clamped tightly together. Drops of electrolyte (0.5 M LiI/50 mM I2 in solvent of 3-methoxypropionitrile) and 0.5 M 4-tert-butylpyridine were added to the standard electrolyte solution in order to increase the stability of the electrolyte. The QDs/TiO2 film was illuminated through the conducting glass substrate to measure the cell performance.


### 2.2.5. Characterization of CdSe QDs

The structural properties of these organic species were confirmed by the powder X-ray diffraction (XRD) using (Shimadzu 7000, Japan) diffractometer, operating with Cu Kα radiation (λ = 0.15406 nm) generated at 30 kV and 30 mA. Scans were done at 4° min−1 for 2θ values between 20 and 60°. The morphologies and the crystallite size of TiO2 nanoparticles were observed by high-resolution transmission electron microscopy (HRTEM) (JEOLJEM-2100F, Japan). To identify and characterize the organic species on the surfaces, the Fourier transform infrared spectroscopy (FT-IR) spectra were obtained using a Shimadzu FTIR-8400 S, Japan. The absorption spectra and their photoluminescence properties were characterized by means of LABOMED double-beam UV-Vis spectrophotometer with spectrum range from 190 to 1100 nm and using a Varian Cary Eclipse spectrofluorometer.


### 2.2.6. Characterization of QDs/TiO2 Solar Cells

The QDs/TiO2 solar cell performance was measured using solar simulator device (PET Photo Emission Tech., Inc., USA). The solar simulator simulates the AM1.5 spectrum by using xenon lamp, and the light intensity could be controlled from 0.1 Sun to 1.25 Sun. The cell ambient temperature was controlled at 25°C using a control system attached to the solar simulator.


## 2.2.1. Preparation of CdSe QDs

This reaction procedure was originally reported by Z. A. Peng and X. Peng [13]. Figure 1 shows scheme for the preparation reaction of CdSe QDs. Se injection solution was prepared under nitrogen by mixing Se powder and TOP in a scintillation vial, which was capped by a rubber septum and fixed with two turns of Cu wire. After ~30 min of heating (~150°C, on a hot plate) and vigorously stirring with a PTFE stir bar, the suspended Se became soluble to afford a light-yellow solution. The Se solution is allowed to cool to room temperature in the presence of nitrogen gas instead of air before injection into a heated Cd solution.Figure 1
Scheme for the preparation  reaction of CdSe QDs.In a laminar flow hood, CdO and SA were loaded into a 3-neck round-bottom flask. The reaction flask is heated to 150°C in air with a round bottom heating mantle. After ~30 min, the reddish-brown slurry became optically clear indicating formation of cadmium stearate. To the hot reaction vessel, HDA and TOPO were added. The reaction flask was backfilled with N2 and heated to 320°C. At this temperature, the selenium solution was swiftly injected into the reaction flask.Upon injection, the solution temperature dropped to 280°C. The solution was maintained at 280°C for the desired amount of time to reach the desired NC size. The round-bottom flask was then removed from the heating mantle and quickly cooled to ~70°C. CdSe QDs washed more than three times by using ethanol and acetone.Table1 illustrates the different preparation parameters, which are used for the preparation of CdSe QDs.Table 1
Different preparation parameters used for the preparation of CdSe QDs.
Sample no.CdO (gm)Se (gm)TOPO (gm)TOP (mL)HAD (gm)SA (gm)Reaction time (sec.)S10.08290.0519.836.259.730.897460S20.08290.0519.836.259.730.897440S30.08290.0519.836.259.730.897420S40.08290.0519.836.259.730.897410S50.08290.05110109.730.897460S60.08290.05115109.730.897460S70.08290.0515109.730.897460S80.08290.10210109.730.897460S90.08290.15310109.730.897460S100.08290.25510109.730.897460S110.08290.35710109.730.897460


## 2.2.2. Preparation of TiO2 Thin Films

The ITO/glass which is used as current collector (14 Ω/□) [15] was first cleaned in water and then acetone using an ultrasonic bath for 15 min. A layer of TiO2 paste was coated on the ITO glass plates by spinner coating method (wafer spinner machine (100 rpm, 2 min)), then allowed to dry in air and followed by heat treatment at 450°C for 30 min. This procedure with TiO2 paste (coating, drying, and heat treatment) was repeated to get the appropriate thickness of about 10 μm for the working electrode.


## 2.2.3. Preparation of CdSe QDs/TiO2 Films

TiO2 thin films were dipped into a solution of N2 purged acetonitrile containing carboxyalkanethiol such as 3-mercaptopropionic acid (1 : 10 ratio) for 24 hrs. Resulting TiO2 films, functionalized with these bifunctional surface modifiers, were washed with both acetonitrile and toluene and then immersed in a suspension of CdSe solution for 24 hrs [17].


## 2.2.4. Fabrication of QDs/TiO2 Solar Cells

The counter electrode was placed directly on the top of the QDs/TiO2 film, supported by the conducting glass sheet. Both electrodes were clamped tightly together. Drops of electrolyte (0.5 M LiI/50 mM I2 in solvent of 3-methoxypropionitrile) and 0.5 M 4-tert-butylpyridine were added to the standard electrolyte solution in order to increase the stability of the electrolyte. The QDs/TiO2 film was illuminated through the conducting glass substrate to measure the cell performance.


## 2.2.5. Characterization of CdSe QDs

The structural properties of these organic species were confirmed by the powder X-ray diffraction (XRD) using (Shimadzu 7000, Japan) diffractometer, operating with Cu Kα radiation (λ = 0.15406 nm) generated at 30 kV and 30 mA. Scans were done at 4° min−1 for 2θ values between 20 and 60°. The morphologies and the crystallite size of TiO2 nanoparticles were observed by high-resolution transmission electron microscopy (HRTEM) (JEOLJEM-2100F, Japan). To identify and characterize the organic species on the surfaces, the Fourier transform infrared spectroscopy (FT-IR) spectra were obtained using a Shimadzu FTIR-8400 S, Japan. The absorption spectra and their photoluminescence properties were characterized by means of LABOMED double-beam UV-Vis spectrophotometer with spectrum range from 190 to 1100 nm and using a Varian Cary Eclipse spectrofluorometer.


## 2.2.6. Characterization of QDs/TiO2 Solar Cells

The QDs/TiO2 solar cell performance was measured using solar simulator device (PET Photo Emission Tech., Inc., USA). The solar simulator simulates the AM1.5 spectrum by using xenon lamp, and the light intensity could be controlled from 0.1 Sun to 1.25 Sun. The cell ambient temperature was controlled at 25°C using a control system attached to the solar simulator.


## 3. Results and Discussion

### 3.1. Structural Analysis

Figure2 (S1, S2, S3, and S4) shows the XRD of CdSe quantum dots with different growth rates as shown in Table 1. The XRD spectra of S1 and S2 exhibit clear peaks that confirm the wurtzite structure with (100), (002), (101), (102), (110), (112), (202), and (104) planes according to the JCPD no. 08-0456, but, for S3 and S4, it gives amorphous structure, which mean that, when the particle size became small, the sample loses its crystalline structure and transfers into amorphous structure.Figure 2
XRD spectra of CdSe samples using different growth rate.The crystallite size of different samples can be determined from the broadening of corresponding X-ray spectral peaks by the Scherrer formula:(1)L=Kλ(βcos⁡θ),
where L is the crystallite size, λ is the wavelength of the X-ray radiation (Cu Kaα=0.15418 nm), K is usually taken as 0.89, and β is the line width at half-maximum height, after subtraction of equipment broadening. It was found that the crystallite size value of S1 and S2, is 4.5 and 4, respectively.Table2 illustrates the effect of using different TOPO/TOP (wt/vol) ratio on the growth rate of the CdSe QDs. It was found that the growth rate of particles was decreased as the ratio of TOPO/TOP increases. Figure 3 shows the absorbance curve of different CdSe samples (S5, S6, and S7) prepared using different TOPO/TOP ratio. It was found that the absorbance peak for samples S5, S6, and S7 was shifted to lower value of wavelength with decrease of the particle growth rate.Table 2
Effect of TOPO/TOP ratio on the CdSe QDs yield.
SampleTOP (mL)TOPO (gm)Yield (gm)Yield (%)S510100.1429S615100.1327S75100.1225Figure 3
Absorbance spectra of CdS QDs prepared using different TOPO/TOP ratio.Table3 illustrates the effect of using different CdO/Se molar ratios on the stoichiometry of CdSe QDs using the TOPO/TOP ratio value of 1 : 1. It is found that the atomic ratio of Cd/Se is 1.27, 1.42, and 1.32 for CdO/Se ratios of 1 : 1, 1 : 3, and 1 : 5, respectively. When increasing the CdO/Se ratio to 1 : 7, no reaction was occurred. This result indicates that controlling the Cd/Se ratio in the precursors affects the quantum dot chemicals properties with a small effect on their yield.Table 3
Effect of CdO/Se molar ratio on the CdSe stoichiometry and QDs yield.
SamplesCdO : Se ratioCd : Se atomic ratioYield (gm)Yield (%)S81 : 11.270.1225S91 : 31.420.1327S101 : 51.320.1327S111 : 7—No reactionNo reactionEnergy dispersive X-ray analysis (EDX) indicates that the quantum dots are nonstoichiometric, showing a molar ratio of Cd/Se about 1.27 (sample S8) in Table2. This result is similar to the data previously reported by other authors such as Moreels et al. [18] and Taylor et al. [19] who found similar ratios between the metal M (Cd) and the counterion X (Se) in analogous systems for the PbSe QDs. Owen et al. [20] proposed a sphere-like structure for these materials, in which Cd2+ ions are present on the QDs surface, which justifies the nonstoichiometry so that metal ions can easily interact with the molecules of a ligand shell by coordination [21].


### 3.2. Morphological Analysis

HRTEM reveals information about the particle size and shape. Figure4 shows the HRTEM images of the S1 example for of CdSe quantum dots before purification from the excess of ligands. CdSe quantum dots are collected on the surface of large chain ligands.Figure 4
HRTEM images of CdSe QDs without purification.The concentration of the nanocrystals in samples were determined by the number of cadmium atoms contained in the samples and the size of the nearly monodisperse particles. Therefore, it was critical to remove any unreacted cadmium precursors in the sample. The extraction method is based on the fact that the solubilities of the un-reacted cadmium precursors used in the synthesis and the resulting nanocrystals were significantly different in a two-phase system, ethanol and octadecane.Figure5 shows the HRTEM images of CdSe powder after purification. The particle size was determined to have value of 2–4 nm. These are consistent with the result of X-ray diffraction spectrum. Also, the nanocrystals were dispersed well, and no aggregation was detected.HRTEM images of CdSe QDs after purification.
(a)(b)Figure6 shows the FT-IR spectra of S1, S2, S3, and S4. CdSe QDs are soluble in toluene after purification. On the basis of the FT-IR data, the surface of the CdSe QDs is mainly coated with alkyl ligands. Flexible organic molecule such as phosphine alkyl ligands provides repulsive interactions between the QDs in toluene, thus preventing aggregation. Others show 3417 cm−1 at OH, 2360 cm−1 at PH3, 1464 cm−1 at CH2, 1155 cm−1 at P=O functional group [22].Figure 6
FT-IR spectra of CdSe QDs soluble in toluene.


### 3.3. Optical Analysis of CdSe QDs

Figure7 shows the absorption and photoluminescence (PL) spectra (410 nm excitation) for different size of CdSe QDs (S1, S2, S3, and S4). For the absorption spectra, all CdSe samples clearly show the effect of quantum confinement. These particles exhibit absorption in the visible region with an onset corresponding to the particle size. The shift of the onset absorption peaks to higher wavelengths (506, 530, 543, and 577 nm) with increasing the particle size represents size quantization effects in these particles.UV-Vis and photoluminescence spectra of the representative nanocrystalline samples.
(a)(b)According to the literature, Yu et al., 2003, developed a theoretical method to calculate the QDs size using the position of first excitonic peak. The particle size of the different samples was determined using(2)D=(1.6122*10-9)λ4-(2.6575*10-6)λ3+(1.6242*10-3)λ2-(0.4277)λ+(41.57),
where D (nm) is the size of a given sample and λ (nm) is the wavelength of the first excitonic absorption peak of the corresponding sample. The calculated particle size crossponding to the wavelength of the excitonic peaks was 2.3, 2.9, 3, and 3.7 nm for samples S1, S2, S3, and S4, respectively.For photoluminescence spectra, CdSe samples with particle size of 2.3, 2.9, 3, and 3.7 nm were given emission peaks at 505, 547, 577, and 600 nm; respectively, it means that the peaks move toward the red end of visible region with the growth temperature which expected according to the literature.Figure8 shows the calculated Eg of S1, S2, S3, and S4 of CdSe QDs with different particle size. The band gap was decreased by 2.38, 2.28, 2.18, and 2.08 eV with the particle size increase of 2.3, 2.9, 3, and 3.7 nm, respectively.Figure 8
Bandgap of CdSe samples.The calculated diameter was used to determine the molar absorption (extinction) coefficient (ε) using (3)ε=5857(D)2.65.If the extinction coefficient of those nanocrystals was calculated, it would be easy to obtain the concentrations of the nanocrystals by simply taking an absorption spectrum of the sample and using Lambert-Beer’s law(4)A=εCL,
where A is the absorbance at the peak position of the first exciton absorption peak for a given sample. C is the molar concentration (mol/L) of the nanocrystals of the sample. L is the path length (cm) of the radiation beam used for recording the absorption spectrum.Unlike conventional organic and inorganic compounds, the concentration of colloidal nanocrystals is difficult to determine by gravimetric methods. Because the number of ligands on the surface of nanocrystals is quite difficult to identify and may also vary significantly under different conditions, measurements solely based on gravimetric methods using ligands-coated nanocrystals are accurate only when the interactions between nanocrystals and ligands are sufficiently strong to withstand necessary purification procedures [23]. Therefore, the absorption spectrum method in many cases is the most practical and convenient way to determine the particle concentrations, if it is not the only possible way as shown in Table 4.Table 4
Absorbance, particle size, extinction, and the molar concentration of CdSe DQs.
Sample no.First excitonic peak (nm)Abs.Size (nm)Extinction coeff. (mol−1cm−1 L)Conc. (mol/L) (10−6)S15770.63.781150.439923.14S25430.92.9190860.45846.16S35300.52.6999040.019719.08S45050.42.3959194.805596.75


### 3.4.I-V Curve of CdSe/TiO2 Solar Cell

For the fabricated solar cell using S1 CdSe QD, the efficiency (η) is calculated as η=JscVoc FF/I0, where I0 is the incident irradiation power, Jsc is the short-circuit current density (current density corresponding to V=0), Voc is the open circuit voltage (voltage corresponding to Jsc=0), and FF is the fill factor.Figures9(a) and 9(b) show the I-V curve of two CdSe QDs/TiO2 solar cells without and with using of MPA as a linker between two semiconductors (TiO2 and CdSe) is used to enhance the adsorption of CdSe QDs on the surface of TiO2 particles and facilitate the charge transfer process from CdSe QDs to TiO2 which enhances the solar cell efficiency [17]. Simulated AM1.5G solar irradiation with a light intensity of 100 mW/cm2 was obtained. It was found, QD solar cell without using linker despite a Voc of 428 mV, Jsc of 0.184 mAcm−2, FF of 0.57, and η of 0.05% but with linker despite a Voc of 543 mV, Jsc of 0.318 mAcm−2, FF of 0.48, and η of 0.08%.I-V curves of CdSe/TiO2 solar cell, (a) without and (b) with using MPA as a linker between CdSe and TiO2 particles.
(a)(b)


## 3.1. Structural Analysis

Figure2 (S1, S2, S3, and S4) shows the XRD of CdSe quantum dots with different growth rates as shown in Table 1. The XRD spectra of S1 and S2 exhibit clear peaks that confirm the wurtzite structure with (100), (002), (101), (102), (110), (112), (202), and (104) planes according to the JCPD no. 08-0456, but, for S3 and S4, it gives amorphous structure, which mean that, when the particle size became small, the sample loses its crystalline structure and transfers into amorphous structure.Figure 2
XRD spectra of CdSe samples using different growth rate.The crystallite size of different samples can be determined from the broadening of corresponding X-ray spectral peaks by the Scherrer formula:(1)L=Kλ(βcos⁡θ),
where L is the crystallite size, λ is the wavelength of the X-ray radiation (Cu Kaα=0.15418 nm), K is usually taken as 0.89, and β is the line width at half-maximum height, after subtraction of equipment broadening. It was found that the crystallite size value of S1 and S2, is 4.5 and 4, respectively.Table2 illustrates the effect of using different TOPO/TOP (wt/vol) ratio on the growth rate of the CdSe QDs. It was found that the growth rate of particles was decreased as the ratio of TOPO/TOP increases. Figure 3 shows the absorbance curve of different CdSe samples (S5, S6, and S7) prepared using different TOPO/TOP ratio. It was found that the absorbance peak for samples S5, S6, and S7 was shifted to lower value of wavelength with decrease of the particle growth rate.Table 2
Effect of TOPO/TOP ratio on the CdSe QDs yield.
SampleTOP (mL)TOPO (gm)Yield (gm)Yield (%)S510100.1429S615100.1327S75100.1225Figure 3
Absorbance spectra of CdS QDs prepared using different TOPO/TOP ratio.Table3 illustrates the effect of using different CdO/Se molar ratios on the stoichiometry of CdSe QDs using the TOPO/TOP ratio value of 1 : 1. It is found that the atomic ratio of Cd/Se is 1.27, 1.42, and 1.32 for CdO/Se ratios of 1 : 1, 1 : 3, and 1 : 5, respectively. When increasing the CdO/Se ratio to 1 : 7, no reaction was occurred. This result indicates that controlling the Cd/Se ratio in the precursors affects the quantum dot chemicals properties with a small effect on their yield.Table 3
Effect of CdO/Se molar ratio on the CdSe stoichiometry and QDs yield.
SamplesCdO : Se ratioCd : Se atomic ratioYield (gm)Yield (%)S81 : 11.270.1225S91 : 31.420.1327S101 : 51.320.1327S111 : 7—No reactionNo reactionEnergy dispersive X-ray analysis (EDX) indicates that the quantum dots are nonstoichiometric, showing a molar ratio of Cd/Se about 1.27 (sample S8) in Table2. This result is similar to the data previously reported by other authors such as Moreels et al. [18] and Taylor et al. [19] who found similar ratios between the metal M (Cd) and the counterion X (Se) in analogous systems for the PbSe QDs. Owen et al. [20] proposed a sphere-like structure for these materials, in which Cd2+ ions are present on the QDs surface, which justifies the nonstoichiometry so that metal ions can easily interact with the molecules of a ligand shell by coordination [21].


## 3.2. Morphological Analysis

HRTEM reveals information about the particle size and shape. Figure4 shows the HRTEM images of the S1 example for of CdSe quantum dots before purification from the excess of ligands. CdSe quantum dots are collected on the surface of large chain ligands.Figure 4
HRTEM images of CdSe QDs without purification.The concentration of the nanocrystals in samples were determined by the number of cadmium atoms contained in the samples and the size of the nearly monodisperse particles. Therefore, it was critical to remove any unreacted cadmium precursors in the sample. The extraction method is based on the fact that the solubilities of the un-reacted cadmium precursors used in the synthesis and the resulting nanocrystals were significantly different in a two-phase system, ethanol and octadecane.Figure5 shows the HRTEM images of CdSe powder after purification. The particle size was determined to have value of 2–4 nm. These are consistent with the result of X-ray diffraction spectrum. Also, the nanocrystals were dispersed well, and no aggregation was detected.HRTEM images of CdSe QDs after purification.
(a)(b)Figure6 shows the FT-IR spectra of S1, S2, S3, and S4. CdSe QDs are soluble in toluene after purification. On the basis of the FT-IR data, the surface of the CdSe QDs is mainly coated with alkyl ligands. Flexible organic molecule such as phosphine alkyl ligands provides repulsive interactions between the QDs in toluene, thus preventing aggregation. Others show 3417 cm−1 at OH, 2360 cm−1 at PH3, 1464 cm−1 at CH2, 1155 cm−1 at P=O functional group [22].Figure 6
FT-IR spectra of CdSe QDs soluble in toluene.


## 3.3. Optical Analysis of CdSe QDs

Figure7 shows the absorption and photoluminescence (PL) spectra (410 nm excitation) for different size of CdSe QDs (S1, S2, S3, and S4). For the absorption spectra, all CdSe samples clearly show the effect of quantum confinement. These particles exhibit absorption in the visible region with an onset corresponding to the particle size. The shift of the onset absorption peaks to higher wavelengths (506, 530, 543, and 577 nm) with increasing the particle size represents size quantization effects in these particles.UV-Vis and photoluminescence spectra of the representative nanocrystalline samples.
(a)(b)According to the literature, Yu et al., 2003, developed a theoretical method to calculate the QDs size using the position of first excitonic peak. The particle size of the different samples was determined using(2)D=(1.6122*10-9)λ4-(2.6575*10-6)λ3+(1.6242*10-3)λ2-(0.4277)λ+(41.57),
where D (nm) is the size of a given sample and λ (nm) is the wavelength of the first excitonic absorption peak of the corresponding sample. The calculated particle size crossponding to the wavelength of the excitonic peaks was 2.3, 2.9, 3, and 3.7 nm for samples S1, S2, S3, and S4, respectively.For photoluminescence spectra, CdSe samples with particle size of 2.3, 2.9, 3, and 3.7 nm were given emission peaks at 505, 547, 577, and 600 nm; respectively, it means that the peaks move toward the red end of visible region with the growth temperature which expected according to the literature.Figure8 shows the calculated Eg of S1, S2, S3, and S4 of CdSe QDs with different particle size. The band gap was decreased by 2.38, 2.28, 2.18, and 2.08 eV with the particle size increase of 2.3, 2.9, 3, and 3.7 nm, respectively.Figure 8
Bandgap of CdSe samples.The calculated diameter was used to determine the molar absorption (extinction) coefficient (ε) using (3)ε=5857(D)2.65.If the extinction coefficient of those nanocrystals was calculated, it would be easy to obtain the concentrations of the nanocrystals by simply taking an absorption spectrum of the sample and using Lambert-Beer’s law(4)A=εCL,
where A is the absorbance at the peak position of the first exciton absorption peak for a given sample. C is the molar concentration (mol/L) of the nanocrystals of the sample. L is the path length (cm) of the radiation beam used for recording the absorption spectrum.Unlike conventional organic and inorganic compounds, the concentration of colloidal nanocrystals is difficult to determine by gravimetric methods. Because the number of ligands on the surface of nanocrystals is quite difficult to identify and may also vary significantly under different conditions, measurements solely based on gravimetric methods using ligands-coated nanocrystals are accurate only when the interactions between nanocrystals and ligands are sufficiently strong to withstand necessary purification procedures [23]. Therefore, the absorption spectrum method in many cases is the most practical and convenient way to determine the particle concentrations, if it is not the only possible way as shown in Table 4.Table 4
Absorbance, particle size, extinction, and the molar concentration of CdSe DQs.
Sample no.First excitonic peak (nm)Abs.Size (nm)Extinction coeff. (mol−1cm−1 L)Conc. (mol/L) (10−6)S15770.63.781150.439923.14S25430.92.9190860.45846.16S35300.52.6999040.019719.08S45050.42.3959194.805596.75


## 3.4.I-V Curve of CdSe/TiO2 Solar Cell

For the fabricated solar cell using S1 CdSe QD, the efficiency (η) is calculated as η=JscVoc FF/I0, where I0 is the incident irradiation power, Jsc is the short-circuit current density (current density corresponding to V=0), Voc is the open circuit voltage (voltage corresponding to Jsc=0), and FF is the fill factor.Figures9(a) and 9(b) show the I-V curve of two CdSe QDs/TiO2 solar cells without and with using of MPA as a linker between two semiconductors (TiO2 and CdSe) is used to enhance the adsorption of CdSe QDs on the surface of TiO2 particles and facilitate the charge transfer process from CdSe QDs to TiO2 which enhances the solar cell efficiency [17]. Simulated AM1.5G solar irradiation with a light intensity of 100 mW/cm2 was obtained. It was found, QD solar cell without using linker despite a Voc of 428 mV, Jsc of 0.184 mAcm−2, FF of 0.57, and η of 0.05% but with linker despite a Voc of 543 mV, Jsc of 0.318 mAcm−2, FF of 0.48, and η of 0.08%.I-V curves of CdSe/TiO2 solar cell, (a) without and (b) with using MPA as a linker between CdSe and TiO2 particles.
(a)(b)


## 4. Conclusions

Our results indicate that CdSe nanocrystals prepared by the common pyrolysis method have an average Cd/Se stoichiometry about 1.27 and the stoichiometry is independent on the initial Cd/Se ratio in the starting material. The results also showed CdSe quantum dots with sizes ranging from 3 nm to 6 nm which enabled the control of the optical properties and consequently the solar cell performance. Open-circuit voltage of 0.54 V, short-circuit current density of about 0.5 mA/cm2, and high fill factor of 0.57 are obtained, which are good results that should be improved through.



---

*Source: 952610-2012-04-17.xml*