# Role of Vanadium Pentoxide Hole-Extracting Nanolayer in Rubrene/C

Authors: Zhen Zhan; Jing Cao; Weiguang Xie; Lintao Hou; Qin Ye; Pengyi Liu
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

Vanadium pentoxideV
2
O
5 was inserted between the donor layer and the anode as a hole-extracting nanolayer. Compared with devices without a hole-extracting layer, short-circuit current density (J
SC), open-circuit voltage (V
OC), fill factor (FF), and power conversion efficiency (PCE) of rubrene/C70-based heterojunction solar cells with 3 nm V2O5 nanolayer are enhanced by 99%, 73%, 20%, and 310%, respectively. We found that V2O5 interlayer can effectively suppress the contact resistance and increase the hole transport capability. The dependence of the device performance on V2O5 layer thickness as well as fill factor on exciton dissociation and charge transport was also investigated in detail.


---

## Body

## 1. Introduction

Solar cells are presently considered as an important source of renewable and green energy to solve the energy crisis. Due to potential applications of compatibility with flexible substrates, low-manufacturing cost, and large-area fabrication [1–3], organic solar cells (OSCs) have received much attention as one kind of the most promising devices in energy harvesting area. Since the first discovery of donor-acceptor heterojunction cell by Tang [4], the performance of OSCs has greatly improved by the use of new materials [5], nanostructuring [6], and the modification of interfaces [7, 8].Improvements in the performance of OSCs are commonly achieved by inserting a hole-extracting layer between the indium tin oxide (ITO) transparent conducting electrode and the organic donor materials. The hole-extracting layer improves the efficiency of hole transport from the active layer into the ITO anode as its higher work function lowers the energy barrier at the interface of ITO/organic donor layer [9]. Poly(3, 4-ethylenedioxythiophene) : poly(styrenesulfonate) (PEDOT : PSS) is one of the most commonly used hole-extracting layers in OSCs. However, PEDOT : PSS is burdened with electrical inhomogeneity which limits electron blocking capability as well as acidic nature which limits the stability and the lifetime of the device [10, 11]. This has driven the vigorous development of better hole-extracting layers. Recent literatures have extensively focused on transition metal oxides (TMO) because of their favorable electronic properties, low optical absorption in the visible spectrum, and high level of technological compatibility in organic electronics [12]. For example, molybdenum trioxide (MoO3) [13], vanadium pentoxide (V2O5) [14], and tungsten trioxide (WO3) [15] have been shown to be promising alternatives to PEDOT : PSS.In our previous study, we had investigated the rubrene/C70-based OSCs, which provided an open-circuit voltage (V
OC) almost twice as high as that of devices based on CuPc/C60 [16, 17]. In this paper, we first demonstrate an improvement in rubrene/C70-based OSCs efficiency by inserting a transparent metal oxide V2O5 thin film as the hole-extracting layer. The effects of the morphology and the thickness of the V2O5 interlayer on the performance of OSC were investigated. The efficiency is improved in OSC with optimized thickness of V2O5 interlayer, which is higher than that with bare ITO by about 3 times. The mechanism is discussed from perspectives of change in resistance, the film transparency, and the charge transport behavior. Our findings contribute to our understanding of hole-extracting behavior in OSCs and may be helpful in fabricating an efficient conversion contact layer in tandem OSCs [18, 19].


## 2. Materials and Methods

Cells were fabricated on commercially available ITO thin film coated glass substrates (180 nm ITO thickness with a sheet resistance less than 10 Ω/□). After successive ultrasonic cleaning processes in acetone, ethanol, and deionized water for 15 minutes each, the ITO glass was then dried by high-purity nitrogen flow before deposition. The organic and metal oxide layers were grown by vacuum deposition in a vacuum thermal evaporation system with a base pressure of 6 × 10−6 mbar. The organic materials used in cells were rubrene (99%), C70 (99%), and 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (BCP) (99%) without further sublimation before deposition. The V2O5 (99%) was used as received. An aluminum thin film with the thickness of 150 nm was deposited in situ as the cathode electrode. The deposition rates of V2O5, rubrene, C70, BCP, and Al were 0.05–0.1/s, 0.06–0.15 nm/s, 0.8–1.5 Å/s, 0.01–0.04 nm/s, and 1.0–4.0 nm/s, respectively. The thickness of layers was monitored by an INFICON XTM/2 oscillating quartz thickness monitor. The schematics of cell structure and energy level are shown in Figures 1(a) and 1(b).(a) Device structure of rubrene/C70-based OSCs and (b) diagram of the energy level in OSCs.
(a)
(b)The active area of the device irradiated was 0.5 × 0.6 mm2. Current density-voltage (J-V) characteristics were measured with a Keithley 2400 sourcemeter under an illumination of 100 mW/cm2 with an AM 1.5G solar illumination from ABET Technologies, Sun 2000 Solar simulator. The solar cell was calibrated using a reference Si solar cell. The surface morphology of V2O5 interlayer was analyzed by atomic force microscope (AFM, CSPM 5500), and the transmission spectra of the V2O5 interlayer were measured by UV-Vis spectrophotometer (UV-2550). All measurements were carried out in ambient air without any encapsulation.


## 3. Results and Discussion

Cells with the architecture ITO/V2O5 (0 or 3 nm)/rubrene (30 nm)/C70 (30 nm)/BCP (6 nm)/Al (150 nm) (Figure 1(a)) were fabricated. Figure 2 shows J-V characteristics of the device with 0 and 3 nm thick V2O5 layer under 100 mW/cm2 white light illumination. In the absence of V2O5 interlayer, the simple device presents a power conversion efficiency of 0.42% with a low fill factor of 36.2%. The J
SC and V
OC are 2.3 mA/cm2 and 0.51 V, respectively. However, by inserting a 3 nm V2O5 interlayer between the donor layer and anode, the device exhibits a significant improvement in power conversion efficiency (PCE) to 1.74%, with short-circuit current density (J
SC) 4.58 mA/cm2, open-circuit voltage (V
OC) 0.88 V, and fill factor (FF) 43.3%.Figure 2
TheJ-V characteristics of devices under 100 mW/cm2 white light illumination in air: ITO/V2O5 (3 nm)/Rubrene/C70/BCP/Al (solid circle) and ITO/Rubrene/C70/BCP/Al (open circle).Figure1(b) shows the diagram of energy level in the rubrene/C70-based OSC [11, 20, 21]. Due to high work function, the thermally evaporated ultrathin film of V2O5 has a more favorable energy level alignment for hole extraction compared to bare ITO [22]. Figure 3 shows the surface morphology of ITO and ITO covered with a 3 nm V2O5 interlayer. The surface of ITO substrate shows a root-mean-square (RMS) roughness of 1.81 nm. After covering with a 3 nm thick V2O5 layer, the RMS roughness decreases to 1.46 nm. ITO with improved morphology will favor the contact between the anode layer and the donor layer [23]. Some small islands were observed on the surface of ITO covered with 3 nm V2O5, which were made of oxide molecules aggregated together on the surface. Minimization of the surface energy might play a role in the formation of such islands which occupy a very small amount of surface area, and the V2O5 layer below the islands should dominate the performance [24].Figure 3
The surface morphology of (a) ITO and (b) ITO coated with 3 nm of V2O5 interlayer. The area is 29 × 29 μm2.By introducing a 3 nm V2O5 hole-extracting layer, the device shows a remarkable increase in J
SC from 2.30 mA/cm2 to 4.58 mA/cm2. It is known that the resistance of the active materials and the contact resistance contribute to the series resistance. Theoretically, inserting a V2O5 layer will introduce two additional interfaces (rubrene/V2O5 and V2O5/ITO) which contribute to an increase in the contact resistance, therefore, increasing the series resistance. However, the series resistance (R
S, defined by the slope of the J-V curve at J
=
0 mA/cm2) is estimated to be 40 and 95.7 Ω cm2 for the device with and without V2O5 interlayer, respectively. Consequently, the decrease in series resistance of the device indicates that the insertion of V2O5 interlayer suppresses the contact resistance remarkably. Although most of the carriers are generated in the active layer, their collection is relative to the contact resistance at the organic/electrode interface [25]. Besides, the high work function of V2O5 (7.0 eV) [9] will enhance hole collection at the organic/ITO interface.It is observable that the cell without a V2O5 hole-extracting layer exhibits a low V
OC of 0.51 V, which leads to a lower PCE. However, by incorporating a hole-extracting layer, the V
OC has an obvious increase to 0.88 V. Providing a more favorable energy level alignment with the donor HOMO than ITO does, and decreasing the series resistance, the hole-extracting layer allows for an Ohmic contact and decreases the losses in the built-in field, leading to the increase in the V
OC since the V
OC is the voltage where the applied bias equals the built-in potential in an ideal diode [22, 26]. Similar to J
SC and V
OC, the FF also has an increase from 36.2% to 43.3%. The decrease in series resistance and the better transport property contribute to the increase in FF. As a consequence, the performance of the device with metal oxide is better as compared to the ITO-only device.For V2O5 placed between ITO and the donor layer, an overall increase in J
SC, V
OC, and FF is obtained, which offers a substantial improvement in PCE. However, introducing a thinner layer of V2O5 will generally lead to a low V
OC and a high leakage current, while a thicker layer will result in an increased series resistance, consequently reducing the J
SC and FF. To find out the optimum thickness, the effect of V2O5 interlayer thickness on device performance is investigated and showed in Figure 4. The detailed result is summarized in Table 1.Table 1
Characteristics (η
P, J
SC, V
OC, FF, and R
S) of OSCs with V2O5 as the hole-extracting layer (varied thickness). The optimum V2O5 thickness is 3 nm (bold values).
Hole-extracting layer (nm)
PCE (%)
J
SC (mA/cm2)
V
OC (V)
FF (%)
R
S (Ω cm2)
0
0.425
2.304
±
0.2
0.51
±
0.05
36.2
±
0.6
95.7
2
1.557
4.289
±
0.2
0.88
±
0.01
41.2
±
0.7
43.0
3
1.745
4.583
±
0.2
0.88
±
0.01
43.3
±
0.1
40.0
6
1.651
4.606
±
0.3
0.88
±
0.01
40.8
±
0.4
41.2
10
1.390
3.711
±
0.1
0.90
±
0.02
41.6
±
0.8
68.0
15
1.320
3.642
±
0.06
0.88
±
0.01
41.2
±
0.3
59.5
20
1.238
3.563
±
0.1
0.86
±
0.02
40.4
±
1.0
63.2
25
1.110
3.128
±
0.2
0.88
±
0.02
40.3
±
1.0
71.5
30
0.731
2.742
±
0.1
0.88
±
0.01
30.3
±
1.0
365Figure 4
TheJ-V characteristics of devices with variable V2O5 interlayer under 100 mW/cm2 white light illumination in air.There is a pronounced dependency of device performance on the thickness of V2O5 interlayer and the optimum V2O5 thickness for our device is 3 nm (bold values in Table 1). When the thickness is 2 nm, the ITO will not be fully covered by V2O5 and two interfaces (V2O5/ITO and organic/ITO) are formed. Therefore, the J-V curve of the cell with 2 nm thick V2O5 interlayer can be considered as the overlapping of two independent J-V curves of cells with 3 nm of V2O5 interlayer and without V2O5. Due to the bad performance of a cell without V2O5, the overlapping curve will result in a worse performance than that of a cell with 3 nm thick V2O5 layer, as is shown in Figure 4.With the thickness of V2O5 increasing from 3 nm to 30 nm, the V
OC and FF changed slightly. On the contrary, the J
SC of a cell with 3 nm thick V2O5 layer is approximately higher than that of a cell with 30 nm V2O5 interlayer by one time. The deterioration of characteristics for devices with V2O5 interlayer thickness larger than 3 nm may be due to the reduction in the quality of both electrical conductivity and optical transmissivity of the V2O5 interlayer [11]. Firstly, we estimated the series resistance of cells with different thickness of V2O5 shown in Table 1. Figure 5 shows the R
S/R
S
0-V2O5 interlayer thickness curve (R
S
0, defined as the series resistance of a device with 0 nm thick V2O5 layer). As compared to that of the optimum cell, the series resistance of cells with thicker V2O5 film increases, which indicates that the electrical conductivity becomes worse with the increase of the V2O5 thickness from 3 nm to 30 nm. The series resistance of the cell with 30 nm V2O5 interlayer is almost 10 times higher than of that with 3 nm thick V2O5 layer.Figure 5
The curve of series resistance-thickness of V2O5 interlayer.We also investigated the optical properties of V2O5 films shown in Figure 6. With a thickness of 30 nm interlayer, the V2O5 film shows significant optical absorption in the visible band and wavelengths below 400 nm. Based on the transmittance data, we propose that a V2O5 layer with the thickness of 3 nm almost transmits 100% of light intensity at wavelength higher than 390 nm whilst a 30 nm V2O5 interlayer absorbs 23% of light intensity at 390 nm (the maximum of the spectral absorption of C70). At 350 nm wavelength, a 3 nm thick layer transmits 96% of the photons while a 30 nm thick layer only transmits 58% of light intensity, which is similar to the result reported by Zilberberg et al. [11]. Thus, it appears reasonable that the deterioration of cell performance with thicker V2O5 (>3 nm) interlayer is related to the lower electrical conductivity and optical transmissivity of the V2O5.Figure 6
Transmission spectra of the V2O5 layer with a thickness of 3 nm (solid circle) and 30 nm (open circle) on ITO.The typical FF of OSCs based on small molecules is typically between 0.5 and 0.65 [5]. But as-prepared rubrene/C70-based OSCs have the highest FF of 43.3%, which is much lower than the typical value. The reverse bias photocurrent J
ph (J
ph
=
J
L
-
J
D, J
L, and J
D are defined as the current density of the device under illumination with 100 mW/cm2 white light and in the dark) of a device with FF > 50% saturates at the high reverse bias, indicating the fact that almost all the photogenerated free charge carriers are extracted [27]. However, in Figure 7(a), the J
ph in the reserve bias shows strong field dependence. In other words, the exciton dissociation rate of a device with 3 nm interlayer is moderately dependent on voltage.(a) TheJ-V characteristics of the device with a 3 nm thick V2O5 layer in the dark (open square) and under white light illumination of 100 mW/cm2 (solid square). (b) The photocurrent J
ph-effective applied bias voltage (V
0
-
V) curve of device with a 3 nm V2O5 interlayer.
(a)
(b)Besides the field-dependent exciton dissociation rate, unbalanced transports of charge carriers also play a role in reducing the FF. Figure7(b) shows the J
ph-(
V
0
-
V
) curve of optimum device (V
0 is the compensation voltage, defined as the voltage at J
ph
=
0, here V
0 is equal to 0.96 V). At low effective field (
V
0
-
V
≤
0.1
), J
ph shows linear dependence on the voltage, due to the competition between drift and diffusion of photogenerated free charges to the electrodes [28]. However, at high effective field (V
0
-
V
≥
0.1), J
ph clearly illustrates a square-root dependence on the voltage, especially, at the field range from 0.2 V to 1 V, which can be clearly seen from the inset of Figure 7(b). During this field region, in case of mobility-lifetime limit, the J
ph is given by
(1)
J
ph
=
q
G
[
(
μ
τ
)
slow
carrier
]
0.5
V
0.5
,
where q is the electric charge, G is the generation rate, μ is the charge carrier mobility, and τ is the charge carrier lifetime. While in case of space charge limit, the J
ph can be described by
(2)
J
ph
=
q
(
q
ε
0
ε
r
μ
slow
carrier
8
q
)
0.25
G
0.75
V
0.5
.
where ε
0
ε
r is the dielectric permittivity. Therefore, the J
ph is influenced by the unbalanced transport in the case of space charge limit or mobility-lifetime limit. For a photocurrent varying with a square-root dependence on the applied voltage, the FF amounts to 42% [27, 28]. It appears from Figure 7(b) that J
ph does not saturate with effective voltages exceeding 1 V but gradually increases for larger effective voltage. That is mainly because not all the photogenerated bound e-h pairs dissociate into free charge at the field lower than 1 V and the dissociation of a fraction of bound e-h pairs is dependent on field [29]. Hence, to some extent, the lower FF in rubrene/C70-based OSC is due to the field-dependent J
ph as well as unbalanced transport.


## 4. Conclusions

We have explored the role of V2O5 hole-extracting layer in rubrene/C70-based OSCs. Due to the favorable electronic properties, V2O5 interlayer effectively extracts holes and suppresses the contact resistance. Because of the thickness-dependent electrical conductivity and the optical transmissivity of the V2O5 layers, the performance of OSCs changes differently with the thickness of V2O5 layer. The highest PCE of 1.745% is achieved for the device with a 3 nm thick V2O5 interlayer and a high V
OC of 0.88 V is also obtained. As V2O5 interlayer can be used as the conversion contact layer in the tandem device, this work may contribute to further development of tandem solar cells.



---

*Source: 964548-2014-02-27.xml*