# Cyclic Strain Enhances Cellular Uptake of Nanoparticles

Authors: Jia Hu; Yaling Liu
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Nanoparticles (NPs) have gained increasing interest in recent years due to their potential use as drug carrier, imaging, and diagnostic agents in pharmaceutical and biomedical applications. While many cellsin vivo experience mechanical forces, little is known about the correlation of the mechanical stimulation and the internalization of NPs into cells. This paper investigates the effects of applied cyclic strain on NP uptake by cells. Bovine aortic endothelial cells (BAECs) were cultured on collagen-coated culture plates and placed under cyclic equal-axial strains. NPs of sizes ranging from 50 to 200 nm were loaded at a concentration of 0.02 mg/mL and cyclic strains from 5 to 15% were applied to the cells for one hour. The cyclic strain results in a significant enhancement in NP uptake, which increases almost linearly with strain level. The enhanced uptake also depends on size of the NPs with the highest uptake observed on 100 nm NP. The effect of enhanced NP uptake lasts around 13 hours after cyclic stretch. Such in vitro cell stretch systems mimic physiological conditions of the endothelial cells in vivo and could potentially serve as a biomimetic platform for drug therapeutic evaluation.


---

## Body

## 1. Introduction

In the past decades, rapid progress has been made in nanoparticle (NP) technologies for the development of disease diagnosis and therapy [1]. Significant efforts have been made in the design of surface functionalized and bioconjugated NPs [2]. It was found that cellular uptake of NP efficiency and quantity depends on various nanoparticle characteristics, including the NP concentration [3], size [4], shape [5], and surface chemical structures [6]. However, these discoveries have not yet been applied to effective targeted therapies due to the complexity of thein vivo environment that severely inhibits their efficiency. This must be overcome to fully exploit the potential of NPs to improve drug pharmacokinetics and pharmacodynamics.Endothelial cells (ECs) form the interior of the blood vessels and serve as a major barrier for therapeutic agents passing through the bloodstream to the target tissues [7]. Recent studies have focused on targeting the endothelium with NPs as therapeutic agents for a variety of targeted therapeutics because of the large population of ECs in the tissue and blood flow [8]. Nanoparticles (NPs) can serve as containers for the targeting of therapeutics to specific location and increasing the resistance time in the body [9]. NP entrance into cells depends on not only the size of the NP, but also the surface coating and charge [10]. For example, the efficiency of carboxydextran-coated superparamagnetic iron oxide nanoparticles (SPION) uptake was correlated to the amount of carboxyl groups on the NP surface [11]. Cationic D, L-polylactide- (PLA-) NP entered Hela cells in greater amounts than anionic PLA-NP [12]. In this study, we investigate the endothelial cell uptake of carboxylated polystyrene NPs (PS-COOH) with positive charge.ECsin vivo are constantly exposed to a variety of forces that generate mechanical stresses within the cell body including shear stress, hydrostatic pressure, and cyclic stretch caused by the pulsatile blood flow [13]. The study of endothelial response to biomechanical forces throughin vitro experiments assists in the understanding of endothelial function, mechanisms involved in endothelial damage, and therapeutic targeting. Researchers reported that cyclic stretch affects the mechanical properties of ECs, such as cell proliferation [14], cytoskeletal structure [15], signal transduction [16], and gene expression and transfer [17]. However very few researches have been done to quantify the effect of cyclic stretching on the cellular uptake of NPs [18]. The aim of this study is to investigate the effects of cyclic stretch on the cellular uptake of NPs and its dependence on NP size through controlled tests. The enhancement of NPs uptake by ECs under physiologically relevant mechanical stimulation might be useful for the development of targeted therapeutics.In this study, we cultured the bovine aortic endothelial cells (BAECs) on six-well plates and stretched the membrane with a cyclic stretcher to investigate the endothelial cell uptake of NPs. The goal of this study was to find out the correlation between cyclic strain and the uptake of NPs into endothelial cells. The results showed that cyclic stretch notably enhanced the cellular uptake of NPs. We further explored the stretch effect on the cellular uptake of NPs by changing the cyclic strain strength and particle size. The results indicated that the enhanced cellular uptake was size-dependent with an optimal particle size of 100 nm. In addition, the cellular uptake is strain-dependent and improves as the strain level increases.


## 2. Materials and Methods

All reagents and equipment, unless otherwise indicated, were purchased from Sigma-Aldrich USA.


### 2.1. Cell Culture

The bovine aortic endothelial cells (BAECs) which were provided by Cell Applications (San Diego, CA) were cultured in 25 cm2 cell culture flasks using a medium containing Dulbecco’s modified Eagle’s medium (DMEM), 10% heat-inactivated fetal bovine serum, and 1% Penicillin/Streptomycin inside a humidified incubator at 5% CO2 and 37°C [19, 20]. The cells were passaged in a split ratio of 1 : 2. All experiments were performed with cells between passages 10 and 15.


### 2.2. Seeding of BAECs for Cyclic Stretch Study

Cell culture medium was aspirated from the flask and the cell monolayer was washed with sterile phosphate buffered saline (PBS, pH 7.4). After removing the PBS, 3 mL trypsin was added to the flask. The flask was placed in the incubator (Thermo Scientific, USA) at 37°C for 3 min to allow for cell detachment. Fresh cell culture medium was added to the flask and flushed with a 10 mL pipette several times to ensure that all the cells were in suspension. Afterwards the cell suspension was transferred to a 15 mL tube. The cells were centrifuged at 1500 rpm for 5 min in order to pellet the cells. The supernatant was discarded and cells were resuspended in fresh cell culture medium. For the cyclic stretch study, BAECs were seeded into six-well, collagen type I coated Bioflex plates (Flexcell International Corp., NC, USA) at 6 × 105 cells/well, determined by a hemocytometer count.


### 2.3. NP Uptake Assay and Cyclic Stretch

Carboxylate-modified fluorescent polystyrene NPs (50 nm, 100 nm, 200 nm) were sonicated for 15 min to break apart possible aggregations and diluted to the final concentration of 0.02 mg/mL in fresh culture medium [21]. This concentration is nontoxic and can be applied without overloading the cells with nanoparticles. After cells reached 80% confluence in the six-well plates, the media were discarded and replaced with NP medium, and BAECs from the test group were subjected to cyclic stretch with frequency of 1 Hz and cyclic strain (5%, 10%, and 15%) for 1 h. A Flexcell tension system (Flexcell International Corp., NC, USA) was used to apply physiological equibiaxial cyclic strain for a wide range of durations, amplitudes, and frequencies [22, 23]. The control group was not subjected to the cyclic stretch while kept in the same condition as the test group.


### 2.4. Analysis of Cellular Uptake

After loading the NP for 1 h, the cells were rinsed with DPBS to eliminate free particles that were not taken up by the cells. Phase contrast and fluorescence images were acquired with a Nikon phase contrast microscope using a 20x lens (Olympus, JP). For quantitative analysis of cellular uptake, 0.5% Triton X-100 in a 0.2 M NaOH solution was added to destroy the cell membrane [4]. The cell medium was transferred to a 96-well plate. Quantitative measurement was then performed by the definite quantitative determination of each cell lysate with a fluorescence Infinite M200 Pro microplate reader (Tecan, Männedorf, Switzerland).


### 2.5. NP Localization and Cell Viability Assay

After cyclic stretch for 1 h, cells were washed three times with PBS, fixed in 4% paraformaldehyde for 30 mins, and then washed three times with PBS. Afterwards, cells were permeabilized in 0.3% Triton X-100 for 5 mins at room temperature. Cells were washed three times with PBS and then incubated with DAPI to visualize nuclei. Cells viability was determined by staining the cells with Calcein AM.


### 2.6. Statistical Analysis

The cellular uptake of nanoparticles (%) was calculated as the fluorescence of the NPs taken up by the cells relative to the total fluorescence of the NPs in the solution. Results are expressed as means ± standard error of the mean (SEM). Statistical analysis was conducted by using Student’st-test, with P<0.05 as the significant difference. Each data point was performed with a minimum of three independent experiments (n=3).


## 2.1. Cell Culture

The bovine aortic endothelial cells (BAECs) which were provided by Cell Applications (San Diego, CA) were cultured in 25 cm2 cell culture flasks using a medium containing Dulbecco’s modified Eagle’s medium (DMEM), 10% heat-inactivated fetal bovine serum, and 1% Penicillin/Streptomycin inside a humidified incubator at 5% CO2 and 37°C [19, 20]. The cells were passaged in a split ratio of 1 : 2. All experiments were performed with cells between passages 10 and 15.


## 2.2. Seeding of BAECs for Cyclic Stretch Study

Cell culture medium was aspirated from the flask and the cell monolayer was washed with sterile phosphate buffered saline (PBS, pH 7.4). After removing the PBS, 3 mL trypsin was added to the flask. The flask was placed in the incubator (Thermo Scientific, USA) at 37°C for 3 min to allow for cell detachment. Fresh cell culture medium was added to the flask and flushed with a 10 mL pipette several times to ensure that all the cells were in suspension. Afterwards the cell suspension was transferred to a 15 mL tube. The cells were centrifuged at 1500 rpm for 5 min in order to pellet the cells. The supernatant was discarded and cells were resuspended in fresh cell culture medium. For the cyclic stretch study, BAECs were seeded into six-well, collagen type I coated Bioflex plates (Flexcell International Corp., NC, USA) at 6 × 105 cells/well, determined by a hemocytometer count.


## 2.3. NP Uptake Assay and Cyclic Stretch

Carboxylate-modified fluorescent polystyrene NPs (50 nm, 100 nm, 200 nm) were sonicated for 15 min to break apart possible aggregations and diluted to the final concentration of 0.02 mg/mL in fresh culture medium [21]. This concentration is nontoxic and can be applied without overloading the cells with nanoparticles. After cells reached 80% confluence in the six-well plates, the media were discarded and replaced with NP medium, and BAECs from the test group were subjected to cyclic stretch with frequency of 1 Hz and cyclic strain (5%, 10%, and 15%) for 1 h. A Flexcell tension system (Flexcell International Corp., NC, USA) was used to apply physiological equibiaxial cyclic strain for a wide range of durations, amplitudes, and frequencies [22, 23]. The control group was not subjected to the cyclic stretch while kept in the same condition as the test group.


## 2.4. Analysis of Cellular Uptake

After loading the NP for 1 h, the cells were rinsed with DPBS to eliminate free particles that were not taken up by the cells. Phase contrast and fluorescence images were acquired with a Nikon phase contrast microscope using a 20x lens (Olympus, JP). For quantitative analysis of cellular uptake, 0.5% Triton X-100 in a 0.2 M NaOH solution was added to destroy the cell membrane [4]. The cell medium was transferred to a 96-well plate. Quantitative measurement was then performed by the definite quantitative determination of each cell lysate with a fluorescence Infinite M200 Pro microplate reader (Tecan, Männedorf, Switzerland).


## 2.5. NP Localization and Cell Viability Assay

After cyclic stretch for 1 h, cells were washed three times with PBS, fixed in 4% paraformaldehyde for 30 mins, and then washed three times with PBS. Afterwards, cells were permeabilized in 0.3% Triton X-100 for 5 mins at room temperature. Cells were washed three times with PBS and then incubated with DAPI to visualize nuclei. Cells viability was determined by staining the cells with Calcein AM.


## 2.6. Statistical Analysis

The cellular uptake of nanoparticles (%) was calculated as the fluorescence of the NPs taken up by the cells relative to the total fluorescence of the NPs in the solution. Results are expressed as means ± standard error of the mean (SEM). Statistical analysis was conducted by using Student’st-test, with P<0.05 as the significant difference. Each data point was performed with a minimum of three independent experiments (n=3).


## 3. Results

### 3.1. Size-Dependent Uptake of NPs

In this study, nanoparticles of different sizes 50 nm, 100 nm, and 200 nm were used to evaluate the correlation between particle sizes and the internalization of NPs into endothelial cells. The fluorescent dye embedded inside the NPs allows us to quantify cellular uptake through fluorescence images. Assuming that the fluorescence intensity is proportional to the number of fluorescent NPs, the average fluorescence yielded within individual cells indicates the cellular uptake of NPs. It should be mentioned that, in extracting the fluorescence intensity, the seeded cells were extensively washed using DPBS to remove any NPs adhered to the cell surface. Therefore, the fluorescence intensity accounts only for the internalized NPs. The cells were cultured in six-well plates for 24 h before loading the NPs for 1 h. We further quantify the cellular uptake of NPs with a fluorescence Infinite M200 Pro microplate reader (Tecan, Männedorf, Switzerland,λex 488 nm, λem 644 nm). As shown in Figure 1(a), BAECs uptake more 100 nm NPs than 50 nm and 200 nm NPs. The result indicates that cellular uptake exhibited size-dependence for the NPs in BAECs, and the optimal size was around 100 nm. This result is consistent with other investigations that cells uptake more 100 nm than other sizes [4, 24].Figure 1
BAECs incubated with NPs under static and 15% strain condition for 1 h. (a) Cellular uptake efficiency of 50 nm, 100 nm, and 200 nm particles. The uptake of 100 nm nanoparticles has significant enhancement after stretching compared to static condition. (b) Cell viability after incubation with NPs of different sizes and without NPs (control). Bars represent mean ± SEM (n=3). ∗ denotes significant differences (p<0.05).
(a)
(b)


### 3.2. Comparison on the Stretch-Enhanced Uptake of the Different Sized NPs

We compared the cyclic stretch effect on 50 nm, 100 nm, and 200 nm particles uptake separately. We found that, after stretching with 15% strain for 1 h, the uptake enhancement of 100 nm particles was much higher than those of 50 nm and 200 nm particles (Figure1(a)). While 50 nm and 200 nm particles show around 20% higher cellular uptake after stretching for 1 h, 100 nm particles show more than twofold enhancement.We also investigated the viability of cells with Calcein AM staining after incubation with 50 nm, 100 nm, and 200 nm NPs. Comparing with cells without NP exposure, no significant differences were found as shown in Figure1(b). This indicates that incubation with NPs from 50 to 200 nm does not have apparent effect on cell viability.


### 3.3. Stretch Effect on Cellular Uptake of NPs

Since it was found that 100 nm NPs have the highest uptake in cells compared to 50 nm and 200 nm NPs, we used carboxylate polystyrene NPs (PS-COOH) with diameters of 100 nm to study the dependence of strain level on cellular uptake. BAECs were cultured on six-well plates for 24 h before loading NPs into the culture media. Fluorescence and phase contrast images were taken after loading NPs for 1 h at different strain levels (Figure2). The images show that the stretch influences the cellular NP uptake quantity. A microplate reader was used to quantify the uptake of NPs in each plate. For each sample, the negative control of cells without NPs was also determined. We found that the application of cyclic stretch significantly promotes the cellular uptake of 100 nm polystyrene nanoparticles relative to static cells, as depicted in Figure 3. This qualitative observation agrees with that reported by Huh et al. [25]. We further compared the cellular uptake of NPs with different cyclic strains: 5%, 10%, and 15%. Results in Figure 3(a) indicate that the cellular uptake of NPs is strain-dependent, and higher strain leads to more NP uptake. The endothelial cellsin vivo are exposed to shear stress and cyclic stretch induced by the pulsatile blood flow. The levels of applied uniform strain (5 to 15%) cover the range of strain experienced by endothelial cellsin vivo. This result indicates that mechanical strain influences NP uptake, which is not considered in the static culture dish work. NP uptake observed in such a cyclic strain system is closer to one that might be observed in animal studies for drug targeting and toxicology applications.Figure 2
Cellular uptake of fluorescent NPs by the cells on plates with different strain ratio (0%, 5%, 10%, and 15%) (scale bar: 20μm). Cells were cultured on substrates for 24 h before loading the NPs. Images were taken after loading the NPs for 1 h.Figure 3
Cell incubation with nanoparticles after stretching for 1 h with cyclic strain (5%, 10%, 15%) and at static condition (control group). (a) Cellular uptake efficiency of nanoparticles. (b) Percentage of detached cells indicates no significant detachment difference. Bars represent mean ± SEM (n=3). p∗<0.05 versus static cells.
(a)
(b)To make sure cyclic stretch does not get cells detached, we also examined the detachment of cells after incubation with 100 nm NPs under cyclic strain (5%, 10%, and 15%) for 1 h. No significant difference of cell detachment was found compared to static cells as shown in Figure3(b), partially because the plates were coated with collagen type I which can help cell adhesion on the surface. The result indicates that the strain level from 5 to 15% will not apparently lead to the detachment of cells.


### 3.4. NPs Localization within the Cells

To figure out the distribution of NPs within the cell, position of the nuclei in each cell was labeled with DAPI staining. The intracellular localization of the NPs was recorded after 1 h using fluorescence microscopy. As shown in Figure4, most of the NPs were located outside of the nucleus and within the cell cytosol. This result is consistent with that reported in literature [2, 3]. Additionally, cyclic stretch did not change the localization of NPs within the cells as shown in Figure 4(a). NPs are still localized in the cell cytosol after stretching.Figure 4
Phase contrast and fluorescence images of BAECs after nanoparticles uptake for 1 h (scale bar: 10μm). The nucleus in each cell was labeled with DAPI staining (blue color). (a-b) Representing uptake of 100 nm nanoparticles by BAECs with 15% stretching for 1 h. (c-d) Representing uptake of 100 nm NPs by BAECs incubated for 1 h without stretching. Nanoparticles (green color) are seen outside of the nucleus. (e-f) Control experiment without nanoparticle incubation.


### 3.5. Time Duration of NP Uptake Enhancement Effect

We further explore how long this stretch-enhanced NPs uptake effect lasts. To investigate the effect duration time, we first stretched the cells for 1 h without loading the NPs. We then loaded the NPs into each plate after waiting for 0, 2, 4, 6, 9, 11, 13, and 22 h separately. Fluorescence signals were quantified by a microplate reader for each sample. The cells exposed to cyclic stretching uptake more NPs than the control group of cells. The NP uptake enhancement effect after stretching decreases nonlinearly with time and disappears after 13 h compared to the cells without stretching, as shown in Figure5. The cellular uptake of NPs did not obviously change even 4 h after stretching and began to decrease 6 h after stretching. This result indicates that the effect of cyclic stretch on cellular NP uptake can last for as long as 13 h.Figure 5
The cellular nanoparticle uptake after stretching 1 h and waiting for 0 h, 2 h, 4 h, 6 h, 9 h, 11 h, 13 h, and 22 h. Control group shows the cells without stretching. The uptake of nanoparticles decreased after 4 h and recovered to static condition after 13 h. Bars represent mean ± SEM (n=3). p∗<0.05 versus control group.


## 3.1. Size-Dependent Uptake of NPs

In this study, nanoparticles of different sizes 50 nm, 100 nm, and 200 nm were used to evaluate the correlation between particle sizes and the internalization of NPs into endothelial cells. The fluorescent dye embedded inside the NPs allows us to quantify cellular uptake through fluorescence images. Assuming that the fluorescence intensity is proportional to the number of fluorescent NPs, the average fluorescence yielded within individual cells indicates the cellular uptake of NPs. It should be mentioned that, in extracting the fluorescence intensity, the seeded cells were extensively washed using DPBS to remove any NPs adhered to the cell surface. Therefore, the fluorescence intensity accounts only for the internalized NPs. The cells were cultured in six-well plates for 24 h before loading the NPs for 1 h. We further quantify the cellular uptake of NPs with a fluorescence Infinite M200 Pro microplate reader (Tecan, Männedorf, Switzerland,λex 488 nm, λem 644 nm). As shown in Figure 1(a), BAECs uptake more 100 nm NPs than 50 nm and 200 nm NPs. The result indicates that cellular uptake exhibited size-dependence for the NPs in BAECs, and the optimal size was around 100 nm. This result is consistent with other investigations that cells uptake more 100 nm than other sizes [4, 24].Figure 1
BAECs incubated with NPs under static and 15% strain condition for 1 h. (a) Cellular uptake efficiency of 50 nm, 100 nm, and 200 nm particles. The uptake of 100 nm nanoparticles has significant enhancement after stretching compared to static condition. (b) Cell viability after incubation with NPs of different sizes and without NPs (control). Bars represent mean ± SEM (n=3). ∗ denotes significant differences (p<0.05).
(a)
(b)


## 3.2. Comparison on the Stretch-Enhanced Uptake of the Different Sized NPs

We compared the cyclic stretch effect on 50 nm, 100 nm, and 200 nm particles uptake separately. We found that, after stretching with 15% strain for 1 h, the uptake enhancement of 100 nm particles was much higher than those of 50 nm and 200 nm particles (Figure1(a)). While 50 nm and 200 nm particles show around 20% higher cellular uptake after stretching for 1 h, 100 nm particles show more than twofold enhancement.We also investigated the viability of cells with Calcein AM staining after incubation with 50 nm, 100 nm, and 200 nm NPs. Comparing with cells without NP exposure, no significant differences were found as shown in Figure1(b). This indicates that incubation with NPs from 50 to 200 nm does not have apparent effect on cell viability.


## 3.3. Stretch Effect on Cellular Uptake of NPs

Since it was found that 100 nm NPs have the highest uptake in cells compared to 50 nm and 200 nm NPs, we used carboxylate polystyrene NPs (PS-COOH) with diameters of 100 nm to study the dependence of strain level on cellular uptake. BAECs were cultured on six-well plates for 24 h before loading NPs into the culture media. Fluorescence and phase contrast images were taken after loading NPs for 1 h at different strain levels (Figure2). The images show that the stretch influences the cellular NP uptake quantity. A microplate reader was used to quantify the uptake of NPs in each plate. For each sample, the negative control of cells without NPs was also determined. We found that the application of cyclic stretch significantly promotes the cellular uptake of 100 nm polystyrene nanoparticles relative to static cells, as depicted in Figure 3. This qualitative observation agrees with that reported by Huh et al. [25]. We further compared the cellular uptake of NPs with different cyclic strains: 5%, 10%, and 15%. Results in Figure 3(a) indicate that the cellular uptake of NPs is strain-dependent, and higher strain leads to more NP uptake. The endothelial cellsin vivo are exposed to shear stress and cyclic stretch induced by the pulsatile blood flow. The levels of applied uniform strain (5 to 15%) cover the range of strain experienced by endothelial cellsin vivo. This result indicates that mechanical strain influences NP uptake, which is not considered in the static culture dish work. NP uptake observed in such a cyclic strain system is closer to one that might be observed in animal studies for drug targeting and toxicology applications.Figure 2
Cellular uptake of fluorescent NPs by the cells on plates with different strain ratio (0%, 5%, 10%, and 15%) (scale bar: 20μm). Cells were cultured on substrates for 24 h before loading the NPs. Images were taken after loading the NPs for 1 h.Figure 3
Cell incubation with nanoparticles after stretching for 1 h with cyclic strain (5%, 10%, 15%) and at static condition (control group). (a) Cellular uptake efficiency of nanoparticles. (b) Percentage of detached cells indicates no significant detachment difference. Bars represent mean ± SEM (n=3). p∗<0.05 versus static cells.
(a)
(b)To make sure cyclic stretch does not get cells detached, we also examined the detachment of cells after incubation with 100 nm NPs under cyclic strain (5%, 10%, and 15%) for 1 h. No significant difference of cell detachment was found compared to static cells as shown in Figure3(b), partially because the plates were coated with collagen type I which can help cell adhesion on the surface. The result indicates that the strain level from 5 to 15% will not apparently lead to the detachment of cells.


## 3.4. NPs Localization within the Cells

To figure out the distribution of NPs within the cell, position of the nuclei in each cell was labeled with DAPI staining. The intracellular localization of the NPs was recorded after 1 h using fluorescence microscopy. As shown in Figure4, most of the NPs were located outside of the nucleus and within the cell cytosol. This result is consistent with that reported in literature [2, 3]. Additionally, cyclic stretch did not change the localization of NPs within the cells as shown in Figure 4(a). NPs are still localized in the cell cytosol after stretching.Figure 4
Phase contrast and fluorescence images of BAECs after nanoparticles uptake for 1 h (scale bar: 10μm). The nucleus in each cell was labeled with DAPI staining (blue color). (a-b) Representing uptake of 100 nm nanoparticles by BAECs with 15% stretching for 1 h. (c-d) Representing uptake of 100 nm NPs by BAECs incubated for 1 h without stretching. Nanoparticles (green color) are seen outside of the nucleus. (e-f) Control experiment without nanoparticle incubation.


## 3.5. Time Duration of NP Uptake Enhancement Effect

We further explore how long this stretch-enhanced NPs uptake effect lasts. To investigate the effect duration time, we first stretched the cells for 1 h without loading the NPs. We then loaded the NPs into each plate after waiting for 0, 2, 4, 6, 9, 11, 13, and 22 h separately. Fluorescence signals were quantified by a microplate reader for each sample. The cells exposed to cyclic stretching uptake more NPs than the control group of cells. The NP uptake enhancement effect after stretching decreases nonlinearly with time and disappears after 13 h compared to the cells without stretching, as shown in Figure5. The cellular uptake of NPs did not obviously change even 4 h after stretching and began to decrease 6 h after stretching. This result indicates that the effect of cyclic stretch on cellular NP uptake can last for as long as 13 h.Figure 5
The cellular nanoparticle uptake after stretching 1 h and waiting for 0 h, 2 h, 4 h, 6 h, 9 h, 11 h, 13 h, and 22 h. Control group shows the cells without stretching. The uptake of nanoparticles decreased after 4 h and recovered to static condition after 13 h. Bars represent mean ± SEM (n=3). p∗<0.05 versus control group.


## 4. Discussion

Nanoparticles as drug delivery carriers or imaging tools may play a pivotal role in improving biomedical therapies [26].In vitro experiments were usually executed to investigate the transport, binding, and uptake behaviors of nanoparticles. The development ofin vitromodels that mimic thein vivo environment is highly desirable. For example, Huh et al. develop a biomimetic microsystem that reconstitutes the critical functional alveolar capillary interface of the human lung to investigate cell reactions such as toxicity or the formation of reactive oxygen species [25]. Compared to static culture dish, the addition of cyclic stretching provides physiological conditions closer to thatin vivo.The main outcome of our study was that, under cyclic stretch conditions, more carboxylate polystyrene NPs were internalized by BAECs compared to static cell culture conditions and such enhancement is NP size and strain level dependent. To our understanding, few investigations were previously reported about the correlation between cyclic stretch and internalization of NPs into endothelial cells. Rouse et al. examined the cell viability, quantum dots (QD) uptake, and cytokine production under 10% cyclic strain condition [27]. Their results indicate that the addition of stain results in an increase in QD uptake by human epidermal keratinocytes (HEK). They mentioned that application of physiological load conditions can increase cell membrane permeability, thereby increasing the concentration of QD nanoparticles in cells. Other research further demonstrated that cyclic stretch leads to the generation of reactive oxygen species, which increase monolayer permeability via activation of NF-κB and extracellular signal-regulated kinase (ERK) [28].Based on the experimental results in this study, the enhanced NP uptake behavior will disappear after 13 h. This may be related to the response of cell to mechanical strains. Other studies also reported that repeated stretches resulted in the trafficking and remodeling of caveolin-3-rich membrane domains and accelerated turnover of membrane glycosphingolipids [29]. The mechanical strain effects on the cytoskeleton also play an important role in mechanotransduction [30, 31]. The changes in the arrangement of the cytoskeleton and the stretch-induced unfolding of caveolae might reflect the mechanisms of the cellular adaptation to mechanical strains which may affect endocytosis events [32]. This may lead to a changed uptake rate of NPs in BAECs in a strain-dependent manner. When the mechanical strains disappear, the cellular uptake of NPs recovers to normal condition after 13 h.The results of thisin vitro study demonstrate that mechanical strain influences the BAEC’s ability to internalize NPs. This study has also shown that differences occur with different cyclic strains and particles sizes. More testing in the future, such as using a different endothelial cell type, strain frequency, stretch time, particle type, chemical structure, and NP concentration, can be performed to better understand how mechanical strain affects the uptake of NPs into endothelial cells.


## 5. Conclusions

Mechanical strain is shown to enhance cellular uptake of nanoparticles. The cell internalization of nanoparticles is size-dependent and has an optimal size of about 100 nm. Additionally, the cell internalization of nanoparticles is strain-dependent and shows more internalization with higher strain levels. This enhanced nanoparticle uptake behavior can last for 13 h and disappears afterwards. Future research is needed to investigate the intercellular processes and activities affected by cyclic stretch to further understand the uptake mechanism. The strain level used in this study is similar to that in physiological systems; thus it may be helpful to understand targeted nanoparticle drug deliveryin vivo.



---

*Source: 953584-2015-08-17.xml*