# Semi-Biosynthesis of Magnetite-Gold Composite Nanoparticles Using an Ethanol Extract ofEucalyptus camaldulensis and Study of the Surface Chemistry

Authors: Emad al din Haratifar; Hamid Reza Shahverdi; Mojtaba Shakibaie; Kamyar Mollazadeh Moghaddam; Mohsen Amini; Hojatollah Montazeri; Ahmad Reza Shahverdi
Journal: Journal of Nanomaterials
 (2009)

---

## Abstract

Green synthesis of metal nanoparticles, such as silver or gold nanoparticles, has been attracting increasing attention in recent years. Functionalized magnetite nanoparticles have many uses in various applications, including nanoelectronic devices, molecular recognition, biomedical applications, drug delivery targeting, and optical devices. In this investigation, magnetic cores (Fe3O4) were synthesized using a fabrication method involving coprecipitation of Fe2+ and Fe3+. In the next step, magnetite-gold composite nanoparticles were synthesized with size ranging from 6–20 nm, using an ethanol extract of Eucalyptus camaldulensis as a natural reducing agent. Transmission electron microscopy, energy-dispersive spectroscopy, X-ray diffraction spectroscopy, and visible absorption spectroscopy confirmed the fabrication of magnetite-gold composite nanoparticles. In the UV spectra diagram, a red-shift of the surface plasmon of the Au was evidence that contact between gold and Fe3O4 had occurred. The surface chemistry of the as-prepared magnetite-gold nanoparticles was studied using infrared spectroscopy. The presence of organic compounds with a carboxyl moiety was confirmed on the surface of the magnetite-gold nanoparticles fabricated by this combined chemical and biological reducing process, which we have designated as a semi-biosynthesis method.


---

## Body

## 1. Introduction

Composite nanoparticles that contain two or more different nanoscale materials are of increasing interest in present day research because of their unique properties. These nanoparticles, have many applications in a number of fields, including use in nanoelectronic devices, molecular recognition, biomedical applications, and optical devices [1]. Recently, different nanocomposite materials, such as SiO2-coated Fe nanocapsules, cobalt ferrite core/shell nanoparticles, silver/polystyrene nanospheres, Au-Cu2O core-shell nanocubes, and Al2O3-Co nanocapsules have been synthesized by different fabrication methods [2–5]. One of the prevalent nanostructures that has many uses in biomedicine is the magnetic nanoparticle. Magnetic nanoparticles, for instance those composed of magnetite (Fe3O4) or maghemite (γ-Fe2O3), have unique thermal, chemical, and magnetic properties that make them particularly well suited for medical applications [6].However, materials that are used in medical diagnoses or as therapeutic agents require specific characteristics, such as colloidal stability [7], biocompatibility [8], resistance against environmental degradation [2], and nontoxicity [6]. For these applications, nanoparticles must be passivated with an external inert shell in order to protect the magnetic core against oxidation. Moreover, the surfaces of these particles should be functionalized with organic molecules in order to allow them to chemically bind with biomolecules like DNA, proteins, amino acids, and so forth [9].At present, a number of different methods have been reported for coating magnetic nanoparticles. Protective layers include polymeric molecules such as polyethylene glycol and dextran or inorganic compounds like silica [8]. Although some of these methods have been recently commercialized, most have substantial deficiencies. For example, hydrophobic surfaces arising from polymeric chains can result in improper protein bonding [10]. A nonmetallic coating also potentially decreases the magnetic properties of iron-oxide nanoparticles, thus limiting the applications of these particles [11].Among the different techniques available for surface modifications, gold-coated magnetic nanoparticles have lately attracted significant attention. Since gold is an inert element from the viewpoint of chemical reactivity, it is very useful as a coating for protecting magnetic nanoparticles. Kinoshita et al. synthesized a gold-iron nanocomposite powder by a reverse micelle method [12]. Similar structures of Fe/Au nanoparticles have been successfully synthesized and the particles used as a magnetic resonance (MR) contrast agent [13]. According to Yu et al. and Au-Fe3O4 nanoparticles with dumbbell-like shapes could be prepared via decomposition of iron pentacarbonyl, FeCO5, onto the surface of gold nanoparticles [14]. In other work, gold and magnetite composite nanoparticles have been prepared by a laser process in water [15]. Gold-coated ferric oxide nanoparticles have been obtained using sodium citrate as the reducing agent, yielding particles with an average size of 25 nm, as reported by Pham et al [6]. Amino acids have also been adsorbed onto the Au/γ-Fe2O3composite nanoparticles synthesized by gamma-ray irradiation [9].A number of these methods for synthesizing gold-iron oxide nanocomposites may not be suitable for biological application because they use harmful surfactants or organic solvents. In addition, maintaining the magnetic nanoparticles in liquid media and preventing aggregation are difficult in practice. In the current study, Au-Fe3O4composite nanoparticles were prepared with a combined chemical and biological reducing process, designated here as a semi-biosynthesis method. Magnetic cores (Fe3O4) were primarily synthesized using a fabrication method consisting of coprecipitation of Fe2+ and Fe3+. An ethanol extract of Eucalyptus camaldulensis[16] was used for the reduction of Au+3 on the surface of the Fe3O4magnetic nanoparticles and for the functionalization of the Au-Fe3O4 nanocomposite particles.


## 2. Experimental

Magnetite (Fe3O4) nanoparticles were prepared at room temperature by a previously reported method [17]. Briefly, deionized water (200 ml) was deoxygenated by bubbling nitrogen gas for 1.5 hour, then 50 ml of NH4OH (1 M) was added, and the mixture was stirred with mechanical agitation at 1000 rpm. Next, 6.76 g FeCl3.6H2O (2.5 mmol) and 4.97 g FeCl2.4H2O (2.5 mmol) were separately dissolved in 50 ml distilled water to make 0.5 M solutions. Subsequently, 10 ml of the ferrous chloride and 20 ml of the ferric chloride solutions were added to the mentioned ammonium hydroxide solution and the reaction mixture was stirred for 2.5 minutes at 1000 rpm. At this stage, a black precipitate formed and it was washed four times with deionized water. The prepared magnetite (Fe3O4) nanoparticles were separated from the solution with a magnet.The reduction of theAu3+ onto the surface of magnetite (Fe3O4) nanoparticles was carried out using an ethanol extract prepared from E.camaldulensiswhole plant [16]. Chloroauric acid was purchased from Merck, Germany. Magnetic nanoparticles (200 mg) were dispersed in 100 mL of aqueous HAuCl4 (chloroauric acid) solution (1 mM) and mixed with 10 mL of an ethanol extract of E.camaldulensis (10 mg/mL). The resulting mixture was allowed to stand for 15 minutes at room temperature, then the prepared magnetite-gold nanocomposites were separated from the colloid by a magnet. Finally, the nanoparticles were washed three times with distilled water for use in further experiments.The UV–visible spectra of the magnetite nanoparticles and magnetite-gold nanocomposites samples, before and after separation with the magnet, were measured on a Labomed Model UVD-2950 UV-VIS Double Beam PC Scanning spectrophotometer, operated at a resolution of 2 nm. All samples were characterized by transmission electron microscopy (model EM 208 Philips), energy-dispersive spectroscopy (EDS), and X-ray diffraction spectroscopy. The surface chemistry of the separated magnetite-gold nanocomposites was further studied with Fourier transform infrared spectroscopy (Nicolet Magna 550).


## 3. Results and Discussion

This study reports a new method for preparation of functionalized magnetite-gold nanocomposites that used a combined chemical and biological procedure. In the first stage,Fe3O4 magnetite nanoparticles were chemically synthesized and their shape and size were studied by transmission electron microscopy. Figures 1(a) and 1(b) show different representative TEM images recorded from the drop-coated film of the magnetite nanoparticles synthesized by this method [17]. The particle size histogram of the synthesized Fe3O4 nanoparticles shows that the particles ranged in size from 6 to 20 nm, with an average size of 10 nm (Figure 1(c)). As can be seen in Figures 1(a) and 1(b), the broad surface area of the nanoparticles and the magnetic forces between them could cause a considerable agglomeration between the fabricated Fe3O4magnetite nanoparticles [18]. The histogram of magnetite nanoparticle size dispersion obtained from TEM images showed diameter ranges between 6–20 nm with an average of 10 nm (Figure 1(c)).TEM images of magnetic nanoparticles with low (a) and high (b) magnifications, (c) Particle size distribution histogram ofFe3O4nanoparticles, (d) EDS spectrum of magnetite particles.
(a)(b)(c)(d)Analysis of theFe3O4nanoparticles by energy dispersive spectroscopy (EDS) confirmed the presence of Fe and O element signals (Figure 1(d)). The peaks shown in Figure 1(d) were attributed to Fe and O elements, which confirmed the existence of iron-oxide nanoparticles (copper and carbon peaks existed due to the grid used for TEM imaging). In the second stage, the magnetite-gold nanocomposite was fabricated in the presence of Au3+ by adding an ethanol extract of E. camaldulensis as a reducing agent. The TEM images of the magnetite-gold nanocomposite illustrated in Figure 2 show gold nanoparticles as dark spots. In contrast, Fe3O4magnetite nanoparticles are observed as a gray color because elemental gold (Au) has a higher electron density than Fe3O4and subsequently more electrons are transmitted in bright field imaging [14].TEM images of magnetic-gold composite nanoparticles with low (a) and high (b) magnifications. Dark particles represent gold, and gray particles are magnetite.
(a)(b)The EDS pattern of the separatedFe3O4magnetite-gold nanocomposite indicated the presence of gold, iron, and oxygen, as illustrated in Figure 3. The EDS experiment was repeated for different nanoparticles and the obtained EDS spectra confirmed that the formed nanoparticles were comprised of both elemental gold and Fe3O4magnetite ingredients. The UV–Visible spectra were examined before and after separation of the magnetic nanoparticles from the gold nanoparticles (Figure 4). Plasmon resonance peaks detected after removing the magnetic nanoparticles from the reaction mixture established the formation of magnetite-gold nanocomposites. It should be noted that pure iron-oxide did not show a significant plasmon resonance peak in the absence of gold nanoparticles. As seen in Figure 4, the highest absorbance was observed for gold nanoparticles located at 530 nm (solid line curve), whereas Au-Fe3O4composite nanoparticles showed a maximum peak at 608 nm (dotted line) which agreed with other previous reports [2, 9, 14, 19]. This wavelength shift in the gold surface plasmon, known as red-shift, is a probable occurrence and has been reported previously [9, 12, 14, 19].Figure 3
EDS pattern of magnetite-gold composite nanoparticles.Figure 4
Absorbance spectra of gold nanoparticles (solid line) and magnetite-gold composite nanoparticles (dotted line).The XRD method was further used to determine the chemical composition of the nanocomposites (Figure5). The Fe3O4and Au peaks were observed and again verified the connection of magnetite nanoparticles with elemental gold. The pattern of gold nanoparticles was face-centered cubic, and the dominant crystal plane for these particles was (111). The surface chemistry of the prepared magnetite-gold nanocomposites was studied using infrared (IR) spectroscopy and the IR peaks centered at 3426 cm-1 and 1675 cm-1 confirmed the presence of a carboxyl group on the surface of the semi-biosynthesized magnetite-gold nanocomposites (spectrum not shown).Figure 5
X-ray diffraction pattern of Au-Fe3O4 composite nanoparticles.


## 4. Conclusion

In this study, the green synthesis and functionalization of a Au-Fe3O4nanocomposite  (from Fe3O4magnetic nanoparticles) were performed using an ethanol extract of E. camaldulensis. As one advantage, a carboxyl group was detected on the surface of the prepared Au-Fe3O4nanocomposite, which would make these particles suitable for rapid separation and purification of biomolecules by magnetic field and drug delivery. It should be noted that the importance of the external inert shell in protecting the magnetic core against oxidation is well established but however, in this study we prepared the Au-Fe3O4nanocomposites that may have contained some portions of Au-Fe3O4 core-shell nanoparticles. Further treatments such as acid washing can be used for separation of the Au-Fe3O4 core-shell fraction and merit further investigation. Moreover, since surfactant has not been used for functionalization of these nanocomposites, this makes these nanoparticles also potentially useful for biomedical applications.



---

*Source: 962021-2010-02-14.xml*