# Self-Passivation by Fluorine Plasma Treatment and Low-Temperature Annealing in SiGe Nanowires for Biochemical Sensors

Authors: Kow-Ming Chang; Chiung-Hui Lai; Chu-Feng Chen; Po-Shen Kuo; Yi-Ming Chen; Tai-Yuan Chang; Allen Jong-Woei Whang; Yi-Lung Lai; Huai-Yi Chen; Ing-Jar Hsieh
Journal: Journal of Nanoscience
 (2014)

---

## Abstract

Nanowires are widely used as highly sensitive sensors for electrical detection of biological and chemical species. Modifying the band structure of strained-Si metal-oxide-semiconductor field-effect transistors by applying the in-plane tensile strain reportedly improves electron and hole mobility. The oxidation-induced Ge condensation increases the Ge fraction in a SiGe-on-insulator (SGOI) and substantially increases hole mobility. However, oxidation increases the number of surface states, resulting in hole mobility degradation. In this work, 3-aminopropyltrimethoxysilane (APTMS) was used as a biochemical  reagent. The hydroxyl molecule on the oxide surface was replaced by the methoxy groups of the APTMS molecule. We proposed a surface plasma treatment to improve the electrical properties of SiGe nanowires. Fluorine plasma treatment can result in enhanced rates of thermal oxidation and speed up the formation of a self-passivation oxide layer. Like a capping oxide layer, the self-passivation oxide layer reduces the rate of follow-up oxidation. Preoxidation treatment also improved the sensitivity of SiGe nanowires because the Si-F binding was held at a more stable interface state compared to bare nanowire on the SiGe surface. Additionally, the sensitivity can be further improved by either the N2 plasma posttreatment or the low-temperature postannealing due to the suppression of outdiffusion of Ge and F atoms from the SiGe nanowire surface.


---

## Body

## 1. Introduction

One-dimensional (1D) nanostructures, such as Si nanowires and ZnO nanorods, have been demonstrated as good candidates for ultrasensitive, miniaturized molecule sensors in biological, chemical, and optical applications [1–7]. The physical properties of biosensor devices fabricated from silicon depend on biochemical/molecular sensitivity. Nanoscale semiconductor processes can be used to improve chemical detection sensitivity. A basic phenomenon associated with the planar semiconductor process that can be exploited in biological sensors is surface potential modification. An important feature of nanowires is their ultrahigh surface-to-volume ratio, which is essential for ultrasensitive detection of chemical or biomolecular species. Since the conductivity of nanowires depends on the surface charges around their surfaces, one way to improve the sensitivity of the nanowire sensor is to use various biomolecular coatings for detecting viruses, proteins, ions, and DNA [8–10]. Strained silicon MOSFETs can be used to increase their electron and hole mobility. To maximize hole mobility, the fractionx of Si1-xGex should be approximately 0.3 [11]. The SiGe-on-insulator (SGOI) process [12] has great potential for fabricating high-sensitivity nanowire sensors. Using Ge condensation to induce formation of SiGe-on-insulator (SGOI) nanowires, enhances conductance by increasing hole carrier mobility. During the Ge condensation process used to fabricate ultrathin SiGe-on-insulators with a high Ge fraction, Ge pile-up occurs at the SiO2/SiGe interface. However, oxidation increases the trap density at the SiO2/SiGe interfaces by approximately 1012 cm−2 [13]. At its free surface, Si generally has an interface state approximating 1015 cm−2 eV−1. The stability of this surface state can be increased by deposition of a thermal SiO2 passivation layer to reduce the interface state of the SGOI nanowire surface to less than 1011 cm−2 eV−1 [14]. Plasma fluorination process also reduces defects at the SiO2/Si interface during the VLSI process [15, 16]. Since fluorine atoms enhance the thermal oxidation rate [17], the enhanced thermal oxidation rate accelerates the formation of a thermal oxide layer, which, like a capping oxide layer, reduces the rate of follow-up oxidation. Otherwise, F atoms terminate Si dangling bonds and replace weak Si–H bonds to prevent the defects and dangling bonds from reducing the conductivity of transport carriers. This study compared the effects of surface state on biochemical detection sensitivity in boron-doped SiGe nanowires with and without surface treatment.


## 2. Experimental Procedure

Strategies typically used to fabricate nanowires can be classified as bottom-up methods (e.g., thermal evaporation [18], laser ablation, and the vapor-liquid-solid methods (VLS) [19]) or top-down methods (e.g., advanced photoemission approaches, including EUV to X-ray [20], AFM [21], nanoimprinting [22], and methods that use side-wall spacers [23]). The side-wall spacer technique is the cheapest and easiest method of fabricating a nanowire sensor. Accordingly, the nanowire samples in this study were fabricated by a side-wall spacer process. A p-type (boron-doped) Si substrate (100) with a resistance of 8~10 ohm·cm was used. After an initial standard RCA cleaning, the 500 nm thick oxide was grown on the Si substrate by wet oxidation at 980°C for seven hours. Then, the oxide layer was patterned by optical lithography and dry etching. The thickness of the remaining oxide is around 300 nm. This 300 nm thick oxide layer served as the bottom oxide in side-wall spacer etching. A 20 nm thick amorphous Si (α-Si) layer was deposited by LPCVD at 650°C, and a 200 nm thick Si0.86Ge0.14 layer was deposited by UHV-CVD at 655°C after RCA cleaning of the wafer. The side-wall-spacer nanowires were formed by self-aligned etching. Figure 1 schematically depicts two SiGe nanowire samples with and without surface plasma treatment. Figure 1(a) shows a bare SiGe nanowire without surface treatment, and Figure 1(b) shows a SiGe nanowire after fluorine plasma treatment. After formation of the α-Si/SiGe layer, the samples were treated in a diluted O2 gas ambient environment for 3 min. The nanowires were then annealed for 180 s in N2 gas. After oxidation and N2 gas annealing, the nanowires were implanted with 3×1015 ions/cm2 of BF2 to form p-type nanowires. The final metallization process was deposition of a 500 nm thick layer of aluminum followed by Al sintering at 400°C. Finally, the electrodes were defined by mask process. The α-Si/SiGe nanowires were functionalized by using 3-aminopropyltrimethoxysilane (APTMS) to modify the silicon oxide surfaces surrounding the nanowires. A hydroxyl functional group on the oxide surface was replaced by methoxy groups of APTMS modules, and the nanowire surfaces were simultaneously terminated by amine groups. When the surface charges of the proposed SiGe nanowires were modified by APTMS, pronounced conductance changes were observed, leading to high sensitivity for chemical/biochemical sensing. The proposed SiGe nanowire was one-time usable and its response time after APTMS dripped on nanowire was around 10~30 s. A Hewlett Packard HP 4156A was used to measure the electrical characteristics of the nanowire sensor. The drain voltage (VD) was varied from −10 to 10 V in steps of 500 mV, and the back gate voltage was fixed at 0 V. The electrical characteristics were measured at each stage of the surface modification, and the average conductance was then extracted from the ID-VD characteristics for a VD = 3~6 V. The sensitivity (S) of a nanowire-based sensor was defined as the ratio of the magnitude of the change in conductance to the baseline conductance:
(1)S=|G-G0|G0=ΔGG0,
where G0 represents the conductance before capture of a molecule; G is the conductance after capture of a molecule, and ΔG is the difference between G and G0.The schematics of different SiGe nanowire surface treatment processes: (a) the “bare” SiGe nanowire without any plasma treatment and (b) the SiGe nanowire with fluorine plasma treatment.
(a)
(b)


## 3. Results and Discussion

The SiGe nanowires were functionalized by using APTMS to modify their surrounding silicon oxide surfaces. The hydroxyl functional group on the oxide surface was replaced by the methoxy groups of the APTMS molecule, and the nanowire surface was simultaneously terminated by amine groups. Next, bis (3-sulfo-N-hydroxysuccinimide ester) sodium salt (BS3) was used to link the APTMS with the IgG antibody. Figure2 presents the conductance characteristics of a nanowire after APTMS and BS3 were dripped onto the nanowire surfaces. Conductance was decreased in nanowires treated by drip application of APTMS on their surfaces. The APTMS tended to become positively charged, as reflected in the decrease of the conductance when hole carriers were depleted from the surface of the p-type nanowire. The conductance of the APTMS-modified nanowire increased after drip application of BS3. These experimental results indicate that the BS3 reduced the surface potential and caused hole carriers to accumulate at the nanowire surface. The functionalization was consistent with the results of our previous experiments in n-type SiGe nanowire [24]. The hydroxyl molecules were replaced by the methoxy sides of the APTMS molecules, which caused the surface potential of the nanowire to become positive and deplete the hole carriers. As the BS3 molecules released sodium ions or broke the single bonds between the carbon atoms and the oxygen atoms, the accumulation of the hole carriers changed the surface potential from positive to negative. Figure 3 depicts the sensitivity of Si0.86Ge0.14 nanowires by different CF4 plasma treatment times. There were 8 tested samples for production of error bars. The results show that the sensitivity of the sample by plasma treatment time of 20 s is better. It can be speculated that the oxidation rate becomes slow because oxygen needs to diffuse through the capping layer. The oxidation rate in the samples capped with an oxidation layer is reduced, further suppressing the formation of surface defects. The free surface of a semiconductor is well known to have high surface state as a result of its dangling bonds. Accumulation of Ge at the nanowire surface during the Ge condensation process also causes interface defects. Thus, a SiGe nanowire without an oxide capping layer should have a lower conductance compared to one with an oxide-capped sample. The oxide cap was exploited to increase the biochemical sensitivity of SiGe nanowires [25]. Since fluorine atoms enhance thermal oxidation [17], the enhanced thermal oxidation rate assumedly causes a thermal oxide layer to form rapidly. Like a capping oxide layer, the thermal oxide layer reduces the rate of follow-up oxidation. This self-passivation effect was verified in a control sample of p-type wafers that had received varying durations of fluorine plasma treatment. The oxide thickness was measured with an ellipsometer. Figure 4 plots the oxide thickness after varying durations of CF4 plasma treatment. The sample by plasma treatment time of 20 s obtained the lowest passive oxide thickness. Although nanowire samples that received a longer treatment had a thicker oxide layer and a lower oxidation rate, fewer O2 atoms passed through their thick oxide layers, which minimized the Ge pile-up effect. The long duration of fluorine treatment also degraded sensitivity [26, 27]. Hanrath and Korgel reported that [28], in Ge nanowires with p-type behavior, Ge tends to accumulate holes at the nanowire surfaces owing to a trapped negative surface charge. Hence, the bare SiGe nanowire sample should have had a higher conductance compared to other SiGe nanowire samples. This difference resulted from enhanced surface doping; therefore, carrier scattering caused by ionized impurities and surface scattering are major concerns with respect to sensitivity variation [29, 30]. Several recent studies have used fluorine to improve the quality of the interfacial layer at a high-κ/Si interface. The strong Si–F bond (5.73 eV) replaces the weak Si–H bond (3.18 eV) [31, 32] which increases the sensitivity of the nanowire upon plasma fluorination by suppressing the formation of dangling bonds in Ge condensation process.Figure 2
The functionalization of the 20 nmα-Si/Si0.86Ge0.14 nanowire after APTMS and BS3 dripping.Figure 3
The sensitivity of Si0.86Ge0.14 nanowire with period of treatment by CF4 treatment.Figure 4
The oxide thickness after varying durations of CF4 plasma treatment time.The effects of the posttreatment were also examined. Figure5 schematically depicts two SiGe nanowire samples that received different plasma posttreatment after fluorine plasma pretreatment. Figure 5(a) shows a SiGe nanowire that received the N2 plasma posttreatment, and Figure 5(b) shows a SiGe nanowire that received the NH3 plasma posttreatment. Figure 6 displays the effect of the posttreatment of SiGe nanowire after fluorine plasma treatment. The sensitivity of the nanowire sample posttreated with N2 is higher than those of nanowire samples posttreated with NH3 and those that did not receive treatment. Several studies have reported the successful incorporation of nitrogen into the interfacial layer (IL) and dielectric layer of high-κ material [33–36]. Hence, plasma treatment was effective for incorporating nitrogen on the SiGe nanowire surface. Compared to the NH3-treated sample, the N2-treated sample has a higher conductance because it incorporates more N atoms. Weak Si–H bonds are easily broken in the following annealing process at high temperature, which causes dangling bonds to reappear. In the NH3-treated sample, because of these dangling bond traps the conduction carriers are trapped in n-type traps [37–40], reducing its sensitivity. Figure 7 shows the sensitivity of SiGe nanowire samples with and without plasma treatment under different annealing temperatures. The change in the sensitivity of the plasma-treated nanowire is opposite that of the bare nanowire in the temperature region 800~950°C. At 1000°C, the sensitivity of the bare nanowire sample decreases. According to the literature, temperature has an important effect on the SGOI structure [41–43]. It is observed that the raise of the sensitivity of “bare” SiGe nanowire is more obvious at temperature of 950°C due to better concentration and enough energy to recrystallize. A suitable thermal budget can recrystallize the interface between the oxide and SiGe, which reduces the number of dislocations and interior defects. Therefore, sensitivity decreased as annealing temperature increased to 1000°C owing to the diffusion of the Ge, which had originally piled up at the nanowire surface, into the SiGe/SiO2 interface. The sensitivity was reduced because Ge diffusion decreased the Ge fraction at the surface. In preoxidation treatment, fluorine atoms eliminated most of the defects in the plasma-treated nanowire sample. Furthermore, Ge atoms did not diffuse into the amorphous Si/buried oxide interface. Hence, the average sensitivity of plasma-treated SiGe nanowires exceeded that of bare samples after annealing at various temperatures and increased as annealing temperature decreased. Figure 8 summarizes the sensitivity of the SiGe nanowire after fluorine/nitrogen plasma treatment for different postannealing conditions. The rate of increase in conductance of the plasma-treated samples declined with increasing temperature. It can be attributed to the fact that the SiGe nanowire surface lost fluorine atoms when annealing temperature exceeded 700°C. According to the literature [43, 44], most fluorine is retained at an annealing temperature of 600°C. When annealing temperature reaches 700°C, the retained dose substantially decreases. In preoxidation treatment, fluorine atoms eliminated most of the defects in the plasma-treated nanowire sample. Hence, the reduced sensitivity of the SiGe nanowire resulting from defects was reproduced by the loss of fluorine atoms in SiGe nanowire surfaces exposed to higher postannealing temperature.The schematics of different post-plasma treatment processes: (a) the N2 plasma posttreatment and (b) the NH3 plasma posttreatment.
(a)
(b)Figure 6
The effect of the plasma posttreatment of SiGe nanowire after fluorine plasma treatment.Figure 7
The sensitivity of SiGe nanowire samples (w/i and w/o plasma treatment) is in different annealing temperature conditions.Figure 8
The effect of the postannealing of SiGe nanowire after fluorine/nitrogen plasma treatment.


## 4. Conclusion

This study examined the use of self-passivation and dual plasma methods for increasing the sensitivity of SiGe nanowires in the Ge condensation process. A self-passivation capping oxide layer formed on SiGe nanowire by fluorine enhanced-oxidation reduced the oxidation rate, which suppressed defect formation during the Ge condensation process. Fluorine plasma treatment also efficiently enhanced the sensitivity of SiGe nanowires by increasing the strength of Si–F bonds, which then increased the stability of the interface state on SiGe surface. Accordingly, F atoms can eliminate the dangling bonds in the Ge condensation process in a SiGe nanowire with a high fraction of Ge, which improves its conductance. Plasma posttreatment in N2 ambient is better than that in NH3 because the H atoms are more easily dissolved by subsequent annealing at high temperature. Sensitivity can also be improved by adjusting postannealing temperature. A suitable thermal budge not only prevents Ge redistribution, but also retains the highest fluorine dose at the SiGe nanowire surface, which provides a high sensitivity and conductance.



---

*Source: 961720-2014-06-11.xml*