# Origin of the Difference in the Resistivity of As-Grown Focused-Ion- and Focused-Electron-Beam-Induced Pt Nanodeposits

Authors: J. M. De Teresa; R. Córdoba; A. Fernández-Pacheco; O. Montero; P. Strichovanec; M. R. Ibarra
Journal: Journal of Nanomaterials
 (2009)

---

## Abstract

We study the origin of the strong difference in the resistivity of focused-electron- and focused-Ga-ion-beam-induced deposition (FEBID and FIBID, resp.) of Pt performed in a dual beam equipment using(CH3)3Pt(CpCH3) as the precursor gas. We have performed in-situ and ex-situ resistance measurements in both types of nanodeposits, finding that the resistivity of Pt by FEBID is typically four orders of magnitude higher than Pt by FIBID. In the case of Pt by FEBID, the current-versus-voltage dependence is nonlinear and the resistance-versus-temperature behavior is strongly semiconducting, whereas Pt by FIBID shows linear current-versus-voltage dependence and only slight temperature dependence. The microstructure, as investigated by high-resolution transmission electron microscopy, consists in all cases of Pt single crystals with size about 3 nm embedded in an amorphous carbonaceous matrix. Due to the semiconducting character of the carbon matrix, which is the main component of the deposit, we propose that the transport results can be mapped onto those obtained in semiconducting materials with different degrees of doping. The different transport properties of Pt by FEBID and FIBID are attributed to the higher doping level in the case of FIBID, as given by composition measurements obtained with energy-dispersive X-ray microanalysis.


---

## Body

## 1. Introduction

Focused-electron- and focused-ion-beam-induced deposition (from now on, FEBID and FIBID, resp.) of metallic materials is one major application of “dual beam” systems, which integrate electron and ion columns. FEBID and FIBID allow local deposition in the targeted place with controllable lateral size (typical size from 15 nm to 10μm) and thickness (typically ranging from 10 nm to 10 μm). Amongst applications of FEBID and FIBID deposits, one can cite the reparation of optical masks and integrated circuits [1], fabrication of three-dimensional nanostructures [2, 3], deposition of protection layers for lamella preparation [4], creation of electronic nanodevices [5], fabrication of nanoelectrodes and nanocontacts [6], transport studies of nanowires [7, 8], and deposition of magnetic [9, 10] and superconducting materials [11–13].FEBID and FIBID involve a chemical vapor deposition process that is assisted by electron and ion beams, respectively (for recent review articles, see [14–16]). Roughly speaking, precursor gas molecules containing the material to be deposited flow from an injector toward the substrate and become adsorbed to it. The precursor gas molecules are decomposed by the electron or ion beams, and the material is locally deposited.  More in detail, this growth technique is based on three physical/chemical processes. The first one is the substrate-precursor molecule interactions, involving mechanisms such as diffusion, adsorption, and desorption. The second one is the electron/ion-substrate interaction. A primary beam of electrons/ions is focused onto the substrate. Some of these electrons collide and are deflected from their initial trajectory whereas other ones undergo inelastic collisions transferring the energy to other electrons/ions. The third one is the electron-precursor molecule interaction. The probability that an electron induces the scission of a bond in a precursor molecule depends on the electron energy and is generally expressed as a cross-section (cm2). It depends on the energy of the bonds within the molecule and, in general, electrons with energy of a few eV are able to produce the molecule dissociation. Besides, two clear deposition regimes have been identified. In the first regime, coined electron-limited regime, the growth is limited by the current density and is independent of the gas flux. In the second regime, coined precursor-limited regime, the growth is limited by the number of molecules arriving at the irradiated area [16].The physical phenomena involved in the deposition are thus complex, and models trying to explain the experimental results take into account factors such as the electron flux as well as their spatial and energy distribution, the cross-section of the precursor as a function of electron energy, the precursor residence time, the electron-beam-induced heating, etc. An important piece of information has been gained through Monte Carlo simulations [14]. Those simulations have highlighted the important role played by the generated secondary electrons in the deposition rate and also in the spatial distribution and resolution of the nanodeposits.When the precursor molecules are organic, in general they are not fully decomposed and, together with the metallic component, a carbonaceous matrix is also present, which is relevant for the physical and chemical properties exhibited by the deposit. One of the most used metallic materials in these deposits is Pt, which calls for detailed characterization of the process and the deposited material. In previous studies, the resistivity values of as-grown Pt nanowires grown with FEBID and FIBID were found to be strongly dependent on the deposition parameters but, in general, the FIBID deposits showed lower resistivity values [17–21]. Different conduction mechanisms have been proposed in these Pt nanodeposits but a clear picture is not established yet, mainly due to the important role played by the carbonaceous matrix. The low percentage of Pt in the deposits compared to the residual C is a handicap for their long-searched metallic behavior.In the present work, we study the transport properties of Pt by FEBID and FIBID with in-situ real-time control of the deposit resistance by means of electrical microprobes. One advantage of the in-situ electrical characterization compared to the ex-situ one is that spurious effects such as oxidation or contamination under ambient conditions will not play any role in the obtained results. These measurements are complemented with more standard ex-situ transport measurements in a cryostat. In order to give a satisfactory explanation of the observed transport behavior, detailed transmission-electron-microscopy (TEM) and energy-dispersive X-ray microanalisis (EDX) studies have been performed. The set of results allows us to propose a comprehensive explanation of the differences between Pt nanodeposits grown by FEBID and FIBID.


## 2. Experimental

For the present experiments, a commercial “dual beam” instrument (Nova 200 NanoLab from FEI) has been used. It integrates a 30 kV field-emission electron column and a Ga-based 30 kV ion column placed forming 52° with coincidence point at 5 mm away from the electron-column pole. For Pt deposition, an automatized gas-injection system (GIS) was used with (CH3)3Pt(CpCH3) as the precursor material. The GIS tip was positioned about 150 μm away from the region of interest in the z direction and about 50 μm away in the x/y direction. The GIS was heated to about 40°C for operation, and a 10-minute preheating period was realized before deposition. The real temperature in the GIS can be a bit lower (≈1 K) than the set point [12].For the investigation of the composition, growth of Pt by FEBID and FIBID was carried out in5×5μm2 areas on a Si substrate. After waiting for a few minutes in order to allow most of the adsorbed precursor molecules to leave the substrate surface, EDX microanalysis was performed by means of a commercial Oxford INCA 200 EDX setup whose detector is driven in the vicinity of the sample. Prior to each EDX experiment, energy calibration by means of a Co calibration sample was done. The volume per dose has been calculated after doing cross-section inspections of the deposits in order to measure the deposit thickness.For the electrical measurements of the Pt deposits, we designed experiments where the deposits close a 12μm gap between metal electrodes. The metal Al electrodes were micropatterned on a Si3N4 (300 nm)/Si substrate following these steps: (1) the Si3N4 layer was grown with a plasma-enhanced chemical-vapor-deposition equipment (from Sistec Company) on a Si wafer in order to ensure good electrical insulation from the substrate; (2) an optical lithography lift-off process was carried out via an image reversal photoresist and metal deposited with an electron-beam evaporator (from Edwards Company) and finally acetone immersion. The mask design was done so that contact pads for measurements of the electrical resistance in 2-probe as well as 4-probe were available.Electrical microprobes (from Kleindiek) were used for precise in-situ control of the deposit resistance [22]. These conductive microprobes are connected via a feedthrough to a Keithley 2000 multimeter located out of the dual beam chamber, which allows measuring the deposit resistance by two-probe measurements provided that its value is below 120 MΩ. A two-probe method is used to measure the resistance applying constant current of value 700 nA and continuous monitoring. The lead resistance was only about 13 Ω, which guarantees no significant influence on the measured resistance of the deposit, which is at least two orders of magnitude larger as will be shown later. In the current-versus-voltage characterization and in the measurements as a function of temperature, four-probe measurements were performed with a 6220 DC current source-2182A nanovoltmeter combined Keithley system, which warrants no influence of any contact resistance. For the measurements as a function of temperature, microcontacting to a chip carrier has been performed, and a closed-cycle refrigerator has been used to cool down the sample.The high-resolution TEM (HRTEM) study was carried out using a Jeol 2010F equipment operated at 200 kV (point-to-point resolution 0.19 nm) on Pt deposits either grown on Cu TEM grids with a supporting carbon membrane or by inspection of a typical thin lamella (<100 nm thick) prepared after deposit growth.


## 3. Results

The results presented hereafter have been obtained in Pt-based nanodeposits grown either in the form of nanowires or in the form of square areas. In Figure1, we show typical cross-section SEM images of these nanodeposits. The standard cross-section method for the imaging of the place of interest involves: (1) the deposition of another material on top of it for protection and high image contrast, (2) FIB milling from the top and cleaning procedure at low current or voltage, (3) sample tilting and SEM imaging.SEM images taken after cross-section experiments performed in (a) a FIBID Pt nanowire and (b) a FIBID Pt square deposit. In both cases, a layer of FEBID Pt is deposited on top of the FIBID deposits before ion milling in order to protect the area to be investigated and to get higher image contrast for reliable thickness measurements.
(a)(b)As can be observed in Figure1(a), our nanowires are typically a few microns long, one micron wide, and a few tens or hundreds of nanometers thick. The square nanodeposits have typically  ≈5×5μm2 area as shown in Figure 1(b) and thickness of some hundreds of nanometers. The shown nanowire and nanodeposit correspond to Pt FIBID samples which have been covered with a protective Pt FEBID layer for the cross-section evaluation.


### 3.1. Volume per Dose of the Pt Nanodeposits

In order to compare the transport properties of FEBID and FIBID samples with similar thickness, the volume per dose (inμm3/nC) has been first investigated. The procedure to calculate the volume per dose consists in growing the nanodeposits in a  ≈5×5μm2 square area, measuring the thickness by standard cross-section experiments with the assistance of FIB milling and SEM inspection, and calculating the total amount of charge received by the sample. The ratio of the nanodeposit volume to the charge gives the volume per dose.Pt by FEBID at several incident electron beam energy in the range from 1 kV to 30 kV was performed. At each fixed beam energy, several depositions of size≈5×5μm2 have been carried out with five different beam currents in the range 0.4–9.5 nA. The electron beam current was found not to have any significant influence on the volume per dose. In Figure 2(a), the volume per dose is represented as a function of the beam energy. Thus, for a fixed beam energy, the average volume-per-dose value of all the investigated currents is represented together with the standard deviation (error bar). In every experiment, the nanodeposit thickness is evaluated by the standard cross-section method. It can be noticed that the volume per dose decreases as a function of the beam energy, as previously found for FEBID of Pt [23, 24]. The decrease is rather fast up to 5 kV and flattens above 15 kV as previously found. At 30 kV, the volume per dose is four times lower than at 1 kV. This dependence can be explained by the decrease in the amount of secondary electrons generated in the substrate and reaching the sample surface [14–16, 23, 24]. The deposition rate, R, is governed by the formula
(1)R=∫0E0f(E)σdiss(E)NdE where E0 is the energy of the primary electrons, f(E) and σdiss(E) are, respectively, the flux of electrons and the electron-impact dissociation cross-section at given energy, and N is the molecular density on the surface. σdiss(E) is experimentally found to show a maximum at a certain energy in the range of a few tens of eV (see the example of C2H5 in [14], with maximum in σdiss at 18 eV). On the other hand, the distribution of secondary electrons generated by the incident electron beam is maximum in the same range of energy, which favors that secondary electrons contribute largely to the molecule precursor dissociation. As the secondary electron yield decreases with the incident electron beam energy, the diminishment of deposition rate with increasing beam energy is naturally explained.(a) Average volume per dose versus incident electron beam energy in the investigated Pt deposits by FEBID; (b) average volume per dose versus incident electron beam energy in the investigated Pt deposits by FIBID. The inset shows the volume per dose versus ion beam current in the investigated FIBID deposits at fixed incident beam energy of 10 kV.
(a)
FEBID(b)
FIBIDPt by FIBID at several incident ion beam energies in the range from 5 kV to 30 kV was performed with beam currents from 44 pA to 2.6 nA. In sharp contrast with Pt by FEBID, in Pt by FIBID the beam current modifies the volume per dose at fixed incident beam energy. Figure2(b) indicates that the volume per dose slightly increases as a function of the beam energy. This fact can be explained by a higher amount of secondary electrons being generated at higher beam energy and being able to reach the sample surface. In contrast to electrons, the Ga ions, even at high energy of 30 kV, are stopped in about 50 nm below the sample surface [23], which allows the generated secondary electrons to reach more easily the sample surface. As shown in the inset of Figure 1(b) for deposits at 10 kV, the volume per dose decreases as a function of the beam current, which is explained by the lack of full refreshment of the precursor molecules adsorbed to the sample surface at high beam currents. Thus, a 50% higher volume per dose can be obtained at 50 pA compared to 2.6 nA. This decrease of the volume per dose with the beam current is also observed in deposits performed at different beam energies (from 5 kV to 30 kV, results not shown). As a further example, at 5 kV it is obtained that the volume per dose decreases from 0.52 μm3/nC to 0.39 μm3/nC with the increase of the ion beam current from 70 pA to 1 nA. These results show that with those large ion beam currents, the growth belongs to the precursor-limited regime, in sharp contrast to the case of FEBID of Pt described above.


### 3.2. In-Situ Control of the Electrical Resistance during Deposition and Comparison of the Transport Properties

The possibility of in-situ control of the electrical resistance during deposition, which is demonstrated in Figure3, is very interesting and has been previously reported with different approaches in [12, 25]. In our case, by careful initial positioning of the electrical microprobes with respect to the contact electrodes and final adjustments with the help of the electron and ion beams imaging, it is possible to realize in-situ good electrical contacts between the probes and the contact electrodes [22]. Thus, if we locate the electrical microprobes on a metallic electrode, we measure 13 Ω, which is the specified lead resistance. In our targeted experiments, the electrodes are separated by a 12 μm gap, which is closed with the FEBID or FIBID deposits (with size 1×20μm2).  After certain time, the deposit resistance is below 120 MΩ, and we start to monitor continuously how the resistance decreases as the deposition time goes on.The image on the left top is a SEM picture of the electrical pads patterned by optical lithography together with the two microprobes contacted for in-situ control of the deposit resistance. The image on the right top is a SEM picture of one typical deposit closing the gap between the contact electrodes for the measurement of the resistance. The shown results of resistance versus time correspond to the comparison between several Pt samples grown by FEBID and FIBID. Resistance monitorization starts after 6.3 minutes in the case of the FEBID process and 1.5 minutes in the case of the FIBID process. The final deposit thickness is approximately the same (160 nm) in all cases (see text for details). For the sake of clarity, zero time is the starting point of the resistance monitorization in all cases.
(a)(b)In Figure3 we compare Pt samples by FEBID and FIBID with similar thickness in order to give evidence for the success in the application of the method as well as the strong difference in the resistance of the deposits. In all cases a multiscan (several beam passes) process is used. Three FEBID and FIBID deposits are shown to illustrate the reproducibility of the results. In the case of the shown FEBID deposits, we have used the conditions: beam current  = 0.54 nA, beam energy  = 10 kV,  and dwell time  = 1 μs. After 6.3 minutes, the resistance reaches 120 MΩ, and we start the resistance monitorization. After additional deposition time of 14.6 minutes, the final resistance is found to be 23.5 MΩ. In the case of the FIBID deposits shown, we have used the conditions: beam current  = 10 pA, beam energy  = 30 kV, and dwell time  = 200 ns. After 1.5 minutes, the resistance reaches 120 MΩ, and we start the resistance monitorization. After additional deposition time of 10.7 minutes, the final resistance is found to be 1 kΩ. Even though the final thickness of all the deposits is roughly the same (~160 nm), the resistance is four orders of magnitude lower for Pt by FIBID. For these nanodeposits of thickness 160 nm, the resistivity value in the case of the Pt by FEBID is about 107μΩcm whereas it is about 800 μΩcm in the case of Pt by FIBID, in any case much higher than for bulk Pt, 10.8 μΩcm.In a homogeneous system with a certain resitivity,ρ, one expects Ohm's law to hold
(2)R=ρlS∝1thicknessAssuming that the nanodeposit thickness is proportional to the deposition time, one can represent the resistance versus the inverse of the thickness in order to investigate if this behavior occurs in the FEBID and FIBID nanodeposits. This representation is shown in Figure4 for selected FEBID and FIBID nanodeposits. In the case of the FEBID nanodeposit, such scaling is not obtained but a slight decrease of the resistivity with thickness. In the case of the FIBID nanodeposit, the effects are dramatic. It is clearly observed that the scaling of the resistance with the inverse of thickness only occurs for thickness above ~100 nm. This means that the nanodeposit resistivity is changing rapidly during the first ~100 nm and finally stabilizes at about 800 μΩcm. A similar behavior has been observed by Spoddig et al. in Pd-based nanowires grown with FIBID [12]. It can be speculated that as the nanodeposition starts and proceeds, the nanodeposit composition changes as a function of the thickness due to the “changing substrate” seen by the incoming ions. As we have described in Section 1, the interactions between the precursor molecules and the substrate as well as the incoming ions with the substrate is crucial for the physical phenomena involved in the nanodeposition, and these interactions will change with thickness during the first tens of nanometers. A focused work on this interesting issue is currently in progress.Figure 4
Representation of the resistance as a function of the inverse of thickness for one selected FEBID Pt nanowire and one selected FIBID Pt nanowire, which illustrates that the constant value expected if the Ohm-law applies only occurs for the FIBID Pt deposits above≈100 nm.In Figure5, again in-situ, we compare the four-probe current-versus-voltage dependence after finishing the growth of one FEBID and one FIBID Pt deposit of similar thickness to those of Figure 3. As can be seen in the SEM image of Figure 5, it is possible to place the four electrical microprobes and the GIS in the area of interest. These measurements have the advantage that any lead resistance or contact resistance is eliminated, and the intrinsic resistance of the nanowire is measured. Whereas the FIBID deposit, with resistance about 1 kΩ (ρ≈800μΩcm), shows a linear dependence in the studied voltage range, the FEBID deposit, with resistance about 50 MΩ (ρ≈107μΩcm), shows a non-linear dependence. The differences between both types of behavior lie on the different content of the nanodeposits as will be demonstrated later. The linear behavior of the FIBID Pt is the expected response for a metallic or quasimetallic system. On the other hand, the non-linear behavior observed in the FEBID Pt deposit can be explained on the basis of the relevant role played by the semiconducting carbonaceous matrix. Interestingly, in the inset of Figure 5(b), the conductance of the FEBID Pt deposit is represented as a function of the applied voltage. It is observed that the conductance decreases up to ≈0.6 V and then starts to increase for higher voltages. We interpret this result within the theoretical framework developed  by Van Lien and Shklovskii [26], further studied with Monte Carlo simulations [27], and experimentally observed in doped silicon [28, 29]. Basically, in semiconducting systems with conduction via impurities the application of electrical field can block the hopping of electrons opposite to the electrical field direction, reducing first the conductivity up to a certain electric field value, where it starts increasing again due to hopping to the localized-states band tail or the unlocalized states band. A deeper discussion on this point will be elaborated in Section 4.In-situ four-probe current-versus-voltage measurements of FEBID and FIBID Pt deposits similar to those of Figure3. (a) The measurements in the FIBID Pt nanowire indicate linear dependence between current and applied voltage. The inset shows a SEM picture where the 4 electrical microprobes and the Pt-based gas injector can be located in the vicinity of the area of interest for the realization of the current-versus-voltage measurements. (b) whereas those in the FEBID Pt nanowire indicate non-linear dependence. The inset shows the anomalous dependence of conductance versus voltage, which is explained in the text.
(a)
FIBID Pt
300 K(b)
FEBID Pt
300 KWe have subsequently studied the ex-situ transport properties of the deposits by four-probe measurements in a cryostat. This characterization is useful for two reasons. First, it provides additional information on the conduction mechanism. Second, if these nanodeposits are going to be used at low temperatures, their transport properties must be known. In Figure6 the dependence of the resistance with temperature for the same FIBID and FEBID deposits as in Figure 5 is shown. Whereas the resistance of the FIBID deposit only increases very slightly with decreasing temperature (a factor of 1.1 at 150 K compared to 300 K), the FEBID deposit shows a strong semiconductor behavior, and at T=150 K the resistance is of the order of 1 GΩ, the maximum resistance that our experimental setup can measure (a factor of 5.5 compared to 300 K). Further understanding of the conduction mechanisms has been obtained by the performed data analysis.(a) Temperature variation of the resistance of a FIBID Pt nanowire showing a quite flat dependence. The inset shows the analysis of data in the form ofw versus T1/2. (b) Temperature variation of the resistance of a FEBID Pt nanowire, showing a semiconducting dependence. The inset shows the analysis of data in the form of ln(G) versus T−1/2 (see text for details).
(a)
FIBID Pt(b)
FEBID PtIn the case of the FIBID Pt deposit, and in order to study if the temperature dependence of the resistance is compatible with a metallic or an insulating material, we use the methodology proposed by Möbius et al. [30]. As shown in the inset of Figure 6(a), w=d(lnG)/d(lnT) is represented as a function of T1/2. According to  [30], if w tends to zero at low temperature, it means that the compound behaves as a metal. In fact this is the tendency observed in our measurements even though further measurements at very low temperatures would be required to fully determine this point. As a consequence, the FIBID Pt deposit has metallic (or quasimetallic) conduction as would be expected if a semiconductor matrix is highly doped so that an impurity band or a percolation network builds up.In the case of the FEBID Pt deposit, the temperature dependence of the resistance is compatible with hopping conduction in a band of localized states inside a semiconductor matrix [31]. In the inset of Figure 6(b), the representation of ln(G) versus T1/2 indicates that below 200 K the conduction mechanism fits the model of variable-range-hopping with Coulomb interaction developed by Efros and Shklovskii [32], where R∝R0exp(T0/T)1/2. The same temperature dependence has been previously found in FEBID Pt deposits by Tsukatani et al. [33]. Above 200 K, the thermal energy is high enough to allow other electronic processes to be involved such as hopping via thermal activation, leading to a deviation from the  T−1/2 law.These results stress the different transport behavior of Pt by FEBID and FIBID. By changing process parameters such as the beam energy or current within accessible ranges, we do not find significant differences in the transport results, the FEBID of Pt always being several orders of magnitude more resistive than the FIBID one. In order to investigate possible origins of such strong difference, we have carried out further experiments regarding the microstructure and composition of the nanodeposits.


### 3.3. Microstructure Investigated by High-Resolution Transmission Electron Microscopy

HRTEM experiments of FEBID and FIBID Pt deposits grown at several energies and beam currents have been performed in order to investigate any difference in the microstructure. Two approaches have been followed. First, several lamellae were prepared out of the deposits grown on Si substrates. Second, the FEBID and FIBID Pt deposits (thickness in the range 20–50 nm) were directly grown on Cu TEM grids with a supporting carbon membrane. Whereas the first approach produces results representative of the samples studied in the transport experiments, the second approach gives more clear TEM images but are grown on a different substrate from the samples studied in transport experiments. Both studies are consequently shown in order to show that both types of results are compatible.From the EDX results to be shown in the next subsection, we know that the main constituents of the deposits are C and Pt. As Pt is a high-atomic-number element compared to C, in HRTEM images it is expected that the Pt-rich areas appear darker than the C-rich areas. However, the interpretation of the TEM images can be tricky because the obtained 2D image contains information of all the way traveled by the electrons along the sample thickness (50–100 nm). This is why it is not straightforward to reach conclusions just from the black/white contrast observed in the images, especially because the grains are small compared to the sample thickness, and the transmitted electrons can meet several grains in their path across the sample. The TEM images obtained in the lamellae fabricated from FIBID and FEBID Pt deposits are shown in Figure7. The observed black/white contrast is due to the inhomogeneous distribution of Pt, and C in the deposits as previously reported [17–21] and in principle can be roughly assigned to Pt nanoparticles with size below 5 nm immersed in the amorphous carbon matrix. However, the lack of clear observation of atomic planes is a drawback for the correct interpretation of the images. On the other hand, the observation of atomic planes in the deposits grown directly on the Cu grids permits an unambiguous interpretation of the images. As can be observed in Figure 8, the FEBID and FIBID Pt deposits consist of ellipsoidal crystalline Pt grains embedded in an amorphous carbonaceous matrix. The crystalline Pt grains are easily identified due to the clear observation of Pt atomic planes with the expected planar distances. Thus, fast-Fourier transforms of the images give as a result the presence of diffraction spots corresponding to the planar distances of 0.2263 nm, 0.1960 nm, 0.1386 nm, and 0.1132 nm, which correspond, respectively, to the (111), (200), (202), and (222) atomic planes of fcc Pt, with lattice parameter of 0.3924 nm. An average size of Pt crystallites has been obtained from the measurement of about 50 individual grains in each image through the counting of the number of atomic planes. It is found that no matter the used beam energy and current are, in all the FEBID and FIBID deposits the average Pt crystallite size is about 3.2±0.8 nm. In W nanodeposits by FEBID, it has been found that by using very high beam energies (>200 kV) it is possible to modify the nanocrystallite size [34]. To the best of our knowledge, such high beam energy has not been used to create Pt by FEBID.HRTEM images obtained out of lamellae fabricated respectively from a Pt nanodeposit by (a) FIBID and (b) FEBID, in both cases grown at 5 kV beam energy.
(a)
FIBID Pt deposit(b)
FEBID Pt depositHRTEM images of a Pt nanodeposit by (a) FIBID and (b) FEBID, in both cases grown at 30 kV beam energy on top of a TEM Cu grid covered with a thin supporting holey carbon membrane. One Pt grain has been selected in each case for magnification and clear observation of the corresponding atomic planes. The Fast-Fourier-Transform of the full image gives diffraction spots that correspond to the (200), (111), (222), and (202) atomic planes of fcc Pt.
(a)
FIBID Pt deposit(b)
FEBID Pt depositThus, from these HRTEM images, the microstructure of the FEBID and FIBID Pt deposits is similar. We would like to stress that the microstructures observed in both, the lamellae and the TEM grids, are qualitatively similar. However, for quantitative analysis only the deposits on the TEM grids can be reliably used.


### 3.4. Composition of the Pt Nanodeposits

First, we checked that the EDX results obtained on nanowires was equivalent to those obtained on square nanodeposits of size≈5×5μm2, which are preferred for the EDX experiments. First, we analyzed a FEBID Pt nanodeposit carried out at 10 kV incident beam energy. The nanowire composition found by EDX was C(%)  = 87.81±0.21, Pt(%)  = 12.19±0.21 whereas the square area composition was found to be C(%)  = 85.46±0.69, Pt(%)  = 13.47±0.40. Afterwards, a FIBID Pt nanodeposit carried out at 30 kV incident beam energy was analyzed. The nanowire composition found by EDX was C(%)  = 71.80±0.22, Pt(%)  = 17.40±0.22, and Ga(%)  = 10.80±0.21, whereas the square area composition was found to be C(%)  = 72.84±0.52, Pt(%)  = 16.67±0.26, and Ga(%)  = 10.50±0.12. Thus, we concluded that the composition could be extracted reliably from the EDX results on the square samples.In Figure9(a) the average Pt content of FEBID of Pt, as obtained with EDX measurements, is shown as a function of the beam energy used for the growth of the nanodeposit. The nanodeposit thickness is about the same as that of the nanowires (≈160 nm). The incident electron beam energy for the EDX measurement was always 10 kV. As the growth beam energy increases, the Pt content is found to decrease from 17% down to 11%. Thus, the C content in the deposit (the main remaining part, more than 80%) will be dominant. We did not find any significant change of the deposition content as a function of the beam current. The decrease of Pt content with the beam energy can be due to the lower amount of secondary electrons produced in the substrate reaching the sample surface and being available for precursor gas molecule decomposition. However, the interplay among primary electrons, secondary electrons, and backscattered electrons in the dissociation of the precursor molecules brings about a complex scenario that calls for focused experiments and simulations to provide a more complete picture [14–16]. Regarding the transport properties, it becomes clear that the carbonaceous matrix (more than 80% in any case) will play a crucial role in the FEBID of Pt.Average Pt atomic content (measured by EDX) versus the incident beam energy used for the growth in the investigated (a) FEBID deposits and (b) FIBID deposits. In this last case the Ga content is also shown. An incident electron beam energy of 10 kV was always used for the EDX experiments.
(a)
FEBID(b)
FIBIDIn Figure9(b) the obtained average Pt and Ga content in FIBID of Pt is shown as a function of the growth beam energy. Whereas the Ga content is roughly constant around 10%, the Pt content is found to decrease from 27% down to 17%. The C content in the deposit is still significant (more than 60%) but the amount of  Pt plus Ga is now relatively high, which, as discussed in the next section, can be responsible for the observed transport properties.


## 3.1. Volume per Dose of the Pt Nanodeposits

In order to compare the transport properties of FEBID and FIBID samples with similar thickness, the volume per dose (inμm3/nC) has been first investigated. The procedure to calculate the volume per dose consists in growing the nanodeposits in a  ≈5×5μm2 square area, measuring the thickness by standard cross-section experiments with the assistance of FIB milling and SEM inspection, and calculating the total amount of charge received by the sample. The ratio of the nanodeposit volume to the charge gives the volume per dose.Pt by FEBID at several incident electron beam energy in the range from 1 kV to 30 kV was performed. At each fixed beam energy, several depositions of size≈5×5μm2 have been carried out with five different beam currents in the range 0.4–9.5 nA. The electron beam current was found not to have any significant influence on the volume per dose. In Figure 2(a), the volume per dose is represented as a function of the beam energy. Thus, for a fixed beam energy, the average volume-per-dose value of all the investigated currents is represented together with the standard deviation (error bar). In every experiment, the nanodeposit thickness is evaluated by the standard cross-section method. It can be noticed that the volume per dose decreases as a function of the beam energy, as previously found for FEBID of Pt [23, 24]. The decrease is rather fast up to 5 kV and flattens above 15 kV as previously found. At 30 kV, the volume per dose is four times lower than at 1 kV. This dependence can be explained by the decrease in the amount of secondary electrons generated in the substrate and reaching the sample surface [14–16, 23, 24]. The deposition rate, R, is governed by the formula
(1)R=∫0E0f(E)σdiss(E)NdE where E0 is the energy of the primary electrons, f(E) and σdiss(E) are, respectively, the flux of electrons and the electron-impact dissociation cross-section at given energy, and N is the molecular density on the surface. σdiss(E) is experimentally found to show a maximum at a certain energy in the range of a few tens of eV (see the example of C2H5 in [14], with maximum in σdiss at 18 eV). On the other hand, the distribution of secondary electrons generated by the incident electron beam is maximum in the same range of energy, which favors that secondary electrons contribute largely to the molecule precursor dissociation. As the secondary electron yield decreases with the incident electron beam energy, the diminishment of deposition rate with increasing beam energy is naturally explained.(a) Average volume per dose versus incident electron beam energy in the investigated Pt deposits by FEBID; (b) average volume per dose versus incident electron beam energy in the investigated Pt deposits by FIBID. The inset shows the volume per dose versus ion beam current in the investigated FIBID deposits at fixed incident beam energy of 10 kV.
(a)
FEBID(b)
FIBIDPt by FIBID at several incident ion beam energies in the range from 5 kV to 30 kV was performed with beam currents from 44 pA to 2.6 nA. In sharp contrast with Pt by FEBID, in Pt by FIBID the beam current modifies the volume per dose at fixed incident beam energy. Figure2(b) indicates that the volume per dose slightly increases as a function of the beam energy. This fact can be explained by a higher amount of secondary electrons being generated at higher beam energy and being able to reach the sample surface. In contrast to electrons, the Ga ions, even at high energy of 30 kV, are stopped in about 50 nm below the sample surface [23], which allows the generated secondary electrons to reach more easily the sample surface. As shown in the inset of Figure 1(b) for deposits at 10 kV, the volume per dose decreases as a function of the beam current, which is explained by the lack of full refreshment of the precursor molecules adsorbed to the sample surface at high beam currents. Thus, a 50% higher volume per dose can be obtained at 50 pA compared to 2.6 nA. This decrease of the volume per dose with the beam current is also observed in deposits performed at different beam energies (from 5 kV to 30 kV, results not shown). As a further example, at 5 kV it is obtained that the volume per dose decreases from 0.52 μm3/nC to 0.39 μm3/nC with the increase of the ion beam current from 70 pA to 1 nA. These results show that with those large ion beam currents, the growth belongs to the precursor-limited regime, in sharp contrast to the case of FEBID of Pt described above.


## 3.2. In-Situ Control of the Electrical Resistance during Deposition and Comparison of the Transport Properties

The possibility of in-situ control of the electrical resistance during deposition, which is demonstrated in Figure3, is very interesting and has been previously reported with different approaches in [12, 25]. In our case, by careful initial positioning of the electrical microprobes with respect to the contact electrodes and final adjustments with the help of the electron and ion beams imaging, it is possible to realize in-situ good electrical contacts between the probes and the contact electrodes [22]. Thus, if we locate the electrical microprobes on a metallic electrode, we measure 13 Ω, which is the specified lead resistance. In our targeted experiments, the electrodes are separated by a 12 μm gap, which is closed with the FEBID or FIBID deposits (with size 1×20μm2).  After certain time, the deposit resistance is below 120 MΩ, and we start to monitor continuously how the resistance decreases as the deposition time goes on.The image on the left top is a SEM picture of the electrical pads patterned by optical lithography together with the two microprobes contacted for in-situ control of the deposit resistance. The image on the right top is a SEM picture of one typical deposit closing the gap between the contact electrodes for the measurement of the resistance. The shown results of resistance versus time correspond to the comparison between several Pt samples grown by FEBID and FIBID. Resistance monitorization starts after 6.3 minutes in the case of the FEBID process and 1.5 minutes in the case of the FIBID process. The final deposit thickness is approximately the same (160 nm) in all cases (see text for details). For the sake of clarity, zero time is the starting point of the resistance monitorization in all cases.
(a)(b)In Figure3 we compare Pt samples by FEBID and FIBID with similar thickness in order to give evidence for the success in the application of the method as well as the strong difference in the resistance of the deposits. In all cases a multiscan (several beam passes) process is used. Three FEBID and FIBID deposits are shown to illustrate the reproducibility of the results. In the case of the shown FEBID deposits, we have used the conditions: beam current  = 0.54 nA, beam energy  = 10 kV,  and dwell time  = 1 μs. After 6.3 minutes, the resistance reaches 120 MΩ, and we start the resistance monitorization. After additional deposition time of 14.6 minutes, the final resistance is found to be 23.5 MΩ. In the case of the FIBID deposits shown, we have used the conditions: beam current  = 10 pA, beam energy  = 30 kV, and dwell time  = 200 ns. After 1.5 minutes, the resistance reaches 120 MΩ, and we start the resistance monitorization. After additional deposition time of 10.7 minutes, the final resistance is found to be 1 kΩ. Even though the final thickness of all the deposits is roughly the same (~160 nm), the resistance is four orders of magnitude lower for Pt by FIBID. For these nanodeposits of thickness 160 nm, the resistivity value in the case of the Pt by FEBID is about 107μΩcm whereas it is about 800 μΩcm in the case of Pt by FIBID, in any case much higher than for bulk Pt, 10.8 μΩcm.In a homogeneous system with a certain resitivity,ρ, one expects Ohm's law to hold
(2)R=ρlS∝1thicknessAssuming that the nanodeposit thickness is proportional to the deposition time, one can represent the resistance versus the inverse of the thickness in order to investigate if this behavior occurs in the FEBID and FIBID nanodeposits. This representation is shown in Figure4 for selected FEBID and FIBID nanodeposits. In the case of the FEBID nanodeposit, such scaling is not obtained but a slight decrease of the resistivity with thickness. In the case of the FIBID nanodeposit, the effects are dramatic. It is clearly observed that the scaling of the resistance with the inverse of thickness only occurs for thickness above ~100 nm. This means that the nanodeposit resistivity is changing rapidly during the first ~100 nm and finally stabilizes at about 800 μΩcm. A similar behavior has been observed by Spoddig et al. in Pd-based nanowires grown with FIBID [12]. It can be speculated that as the nanodeposition starts and proceeds, the nanodeposit composition changes as a function of the thickness due to the “changing substrate” seen by the incoming ions. As we have described in Section 1, the interactions between the precursor molecules and the substrate as well as the incoming ions with the substrate is crucial for the physical phenomena involved in the nanodeposition, and these interactions will change with thickness during the first tens of nanometers. A focused work on this interesting issue is currently in progress.Figure 4
Representation of the resistance as a function of the inverse of thickness for one selected FEBID Pt nanowire and one selected FIBID Pt nanowire, which illustrates that the constant value expected if the Ohm-law applies only occurs for the FIBID Pt deposits above≈100 nm.In Figure5, again in-situ, we compare the four-probe current-versus-voltage dependence after finishing the growth of one FEBID and one FIBID Pt deposit of similar thickness to those of Figure 3. As can be seen in the SEM image of Figure 5, it is possible to place the four electrical microprobes and the GIS in the area of interest. These measurements have the advantage that any lead resistance or contact resistance is eliminated, and the intrinsic resistance of the nanowire is measured. Whereas the FIBID deposit, with resistance about 1 kΩ (ρ≈800μΩcm), shows a linear dependence in the studied voltage range, the FEBID deposit, with resistance about 50 MΩ (ρ≈107μΩcm), shows a non-linear dependence. The differences between both types of behavior lie on the different content of the nanodeposits as will be demonstrated later. The linear behavior of the FIBID Pt is the expected response for a metallic or quasimetallic system. On the other hand, the non-linear behavior observed in the FEBID Pt deposit can be explained on the basis of the relevant role played by the semiconducting carbonaceous matrix. Interestingly, in the inset of Figure 5(b), the conductance of the FEBID Pt deposit is represented as a function of the applied voltage. It is observed that the conductance decreases up to ≈0.6 V and then starts to increase for higher voltages. We interpret this result within the theoretical framework developed  by Van Lien and Shklovskii [26], further studied with Monte Carlo simulations [27], and experimentally observed in doped silicon [28, 29]. Basically, in semiconducting systems with conduction via impurities the application of electrical field can block the hopping of electrons opposite to the electrical field direction, reducing first the conductivity up to a certain electric field value, where it starts increasing again due to hopping to the localized-states band tail or the unlocalized states band. A deeper discussion on this point will be elaborated in Section 4.In-situ four-probe current-versus-voltage measurements of FEBID and FIBID Pt deposits similar to those of Figure3. (a) The measurements in the FIBID Pt nanowire indicate linear dependence between current and applied voltage. The inset shows a SEM picture where the 4 electrical microprobes and the Pt-based gas injector can be located in the vicinity of the area of interest for the realization of the current-versus-voltage measurements. (b) whereas those in the FEBID Pt nanowire indicate non-linear dependence. The inset shows the anomalous dependence of conductance versus voltage, which is explained in the text.
(a)
FIBID Pt
300 K(b)
FEBID Pt
300 KWe have subsequently studied the ex-situ transport properties of the deposits by four-probe measurements in a cryostat. This characterization is useful for two reasons. First, it provides additional information on the conduction mechanism. Second, if these nanodeposits are going to be used at low temperatures, their transport properties must be known. In Figure6 the dependence of the resistance with temperature for the same FIBID and FEBID deposits as in Figure 5 is shown. Whereas the resistance of the FIBID deposit only increases very slightly with decreasing temperature (a factor of 1.1 at 150 K compared to 300 K), the FEBID deposit shows a strong semiconductor behavior, and at T=150 K the resistance is of the order of 1 GΩ, the maximum resistance that our experimental setup can measure (a factor of 5.5 compared to 300 K). Further understanding of the conduction mechanisms has been obtained by the performed data analysis.(a) Temperature variation of the resistance of a FIBID Pt nanowire showing a quite flat dependence. The inset shows the analysis of data in the form ofw versus T1/2. (b) Temperature variation of the resistance of a FEBID Pt nanowire, showing a semiconducting dependence. The inset shows the analysis of data in the form of ln(G) versus T−1/2 (see text for details).
(a)
FIBID Pt(b)
FEBID PtIn the case of the FIBID Pt deposit, and in order to study if the temperature dependence of the resistance is compatible with a metallic or an insulating material, we use the methodology proposed by Möbius et al. [30]. As shown in the inset of Figure 6(a), w=d(lnG)/d(lnT) is represented as a function of T1/2. According to  [30], if w tends to zero at low temperature, it means that the compound behaves as a metal. In fact this is the tendency observed in our measurements even though further measurements at very low temperatures would be required to fully determine this point. As a consequence, the FIBID Pt deposit has metallic (or quasimetallic) conduction as would be expected if a semiconductor matrix is highly doped so that an impurity band or a percolation network builds up.In the case of the FEBID Pt deposit, the temperature dependence of the resistance is compatible with hopping conduction in a band of localized states inside a semiconductor matrix [31]. In the inset of Figure 6(b), the representation of ln(G) versus T1/2 indicates that below 200 K the conduction mechanism fits the model of variable-range-hopping with Coulomb interaction developed by Efros and Shklovskii [32], where R∝R0exp(T0/T)1/2. The same temperature dependence has been previously found in FEBID Pt deposits by Tsukatani et al. [33]. Above 200 K, the thermal energy is high enough to allow other electronic processes to be involved such as hopping via thermal activation, leading to a deviation from the  T−1/2 law.These results stress the different transport behavior of Pt by FEBID and FIBID. By changing process parameters such as the beam energy or current within accessible ranges, we do not find significant differences in the transport results, the FEBID of Pt always being several orders of magnitude more resistive than the FIBID one. In order to investigate possible origins of such strong difference, we have carried out further experiments regarding the microstructure and composition of the nanodeposits.


## 3.3. Microstructure Investigated by High-Resolution Transmission Electron Microscopy

HRTEM experiments of FEBID and FIBID Pt deposits grown at several energies and beam currents have been performed in order to investigate any difference in the microstructure. Two approaches have been followed. First, several lamellae were prepared out of the deposits grown on Si substrates. Second, the FEBID and FIBID Pt deposits (thickness in the range 20–50 nm) were directly grown on Cu TEM grids with a supporting carbon membrane. Whereas the first approach produces results representative of the samples studied in the transport experiments, the second approach gives more clear TEM images but are grown on a different substrate from the samples studied in transport experiments. Both studies are consequently shown in order to show that both types of results are compatible.From the EDX results to be shown in the next subsection, we know that the main constituents of the deposits are C and Pt. As Pt is a high-atomic-number element compared to C, in HRTEM images it is expected that the Pt-rich areas appear darker than the C-rich areas. However, the interpretation of the TEM images can be tricky because the obtained 2D image contains information of all the way traveled by the electrons along the sample thickness (50–100 nm). This is why it is not straightforward to reach conclusions just from the black/white contrast observed in the images, especially because the grains are small compared to the sample thickness, and the transmitted electrons can meet several grains in their path across the sample. The TEM images obtained in the lamellae fabricated from FIBID and FEBID Pt deposits are shown in Figure7. The observed black/white contrast is due to the inhomogeneous distribution of Pt, and C in the deposits as previously reported [17–21] and in principle can be roughly assigned to Pt nanoparticles with size below 5 nm immersed in the amorphous carbon matrix. However, the lack of clear observation of atomic planes is a drawback for the correct interpretation of the images. On the other hand, the observation of atomic planes in the deposits grown directly on the Cu grids permits an unambiguous interpretation of the images. As can be observed in Figure 8, the FEBID and FIBID Pt deposits consist of ellipsoidal crystalline Pt grains embedded in an amorphous carbonaceous matrix. The crystalline Pt grains are easily identified due to the clear observation of Pt atomic planes with the expected planar distances. Thus, fast-Fourier transforms of the images give as a result the presence of diffraction spots corresponding to the planar distances of 0.2263 nm, 0.1960 nm, 0.1386 nm, and 0.1132 nm, which correspond, respectively, to the (111), (200), (202), and (222) atomic planes of fcc Pt, with lattice parameter of 0.3924 nm. An average size of Pt crystallites has been obtained from the measurement of about 50 individual grains in each image through the counting of the number of atomic planes. It is found that no matter the used beam energy and current are, in all the FEBID and FIBID deposits the average Pt crystallite size is about 3.2±0.8 nm. In W nanodeposits by FEBID, it has been found that by using very high beam energies (>200 kV) it is possible to modify the nanocrystallite size [34]. To the best of our knowledge, such high beam energy has not been used to create Pt by FEBID.HRTEM images obtained out of lamellae fabricated respectively from a Pt nanodeposit by (a) FIBID and (b) FEBID, in both cases grown at 5 kV beam energy.
(a)
FIBID Pt deposit(b)
FEBID Pt depositHRTEM images of a Pt nanodeposit by (a) FIBID and (b) FEBID, in both cases grown at 30 kV beam energy on top of a TEM Cu grid covered with a thin supporting holey carbon membrane. One Pt grain has been selected in each case for magnification and clear observation of the corresponding atomic planes. The Fast-Fourier-Transform of the full image gives diffraction spots that correspond to the (200), (111), (222), and (202) atomic planes of fcc Pt.
(a)
FIBID Pt deposit(b)
FEBID Pt depositThus, from these HRTEM images, the microstructure of the FEBID and FIBID Pt deposits is similar. We would like to stress that the microstructures observed in both, the lamellae and the TEM grids, are qualitatively similar. However, for quantitative analysis only the deposits on the TEM grids can be reliably used.


## 3.4. Composition of the Pt Nanodeposits

First, we checked that the EDX results obtained on nanowires was equivalent to those obtained on square nanodeposits of size≈5×5μm2, which are preferred for the EDX experiments. First, we analyzed a FEBID Pt nanodeposit carried out at 10 kV incident beam energy. The nanowire composition found by EDX was C(%)  = 87.81±0.21, Pt(%)  = 12.19±0.21 whereas the square area composition was found to be C(%)  = 85.46±0.69, Pt(%)  = 13.47±0.40. Afterwards, a FIBID Pt nanodeposit carried out at 30 kV incident beam energy was analyzed. The nanowire composition found by EDX was C(%)  = 71.80±0.22, Pt(%)  = 17.40±0.22, and Ga(%)  = 10.80±0.21, whereas the square area composition was found to be C(%)  = 72.84±0.52, Pt(%)  = 16.67±0.26, and Ga(%)  = 10.50±0.12. Thus, we concluded that the composition could be extracted reliably from the EDX results on the square samples.In Figure9(a) the average Pt content of FEBID of Pt, as obtained with EDX measurements, is shown as a function of the beam energy used for the growth of the nanodeposit. The nanodeposit thickness is about the same as that of the nanowires (≈160 nm). The incident electron beam energy for the EDX measurement was always 10 kV. As the growth beam energy increases, the Pt content is found to decrease from 17% down to 11%. Thus, the C content in the deposit (the main remaining part, more than 80%) will be dominant. We did not find any significant change of the deposition content as a function of the beam current. The decrease of Pt content with the beam energy can be due to the lower amount of secondary electrons produced in the substrate reaching the sample surface and being available for precursor gas molecule decomposition. However, the interplay among primary electrons, secondary electrons, and backscattered electrons in the dissociation of the precursor molecules brings about a complex scenario that calls for focused experiments and simulations to provide a more complete picture [14–16]. Regarding the transport properties, it becomes clear that the carbonaceous matrix (more than 80% in any case) will play a crucial role in the FEBID of Pt.Average Pt atomic content (measured by EDX) versus the incident beam energy used for the growth in the investigated (a) FEBID deposits and (b) FIBID deposits. In this last case the Ga content is also shown. An incident electron beam energy of 10 kV was always used for the EDX experiments.
(a)
FEBID(b)
FIBIDIn Figure9(b) the obtained average Pt and Ga content in FIBID of Pt is shown as a function of the growth beam energy. Whereas the Ga content is roughly constant around 10%, the Pt content is found to decrease from 27% down to 17%. The C content in the deposit is still significant (more than 60%) but the amount of  Pt plus Ga is now relatively high, which, as discussed in the next section, can be responsible for the observed transport properties.


## 4. Discussion

We argue hereafter that the obtained results can be explained taking into account the important role played by the carbonaceous matrix together with the Pt inclusions, and Ga-ion implantation in the case of the FIBID. Strong similarities exist between these results and those obtained previously in doped amorphous semiconductors [31]. In those studies, it is typically observed that as the doping level and disorder increase, there appear impurity states in the vicinity of the Fermi level as well as a band tail of localized states separated from the band of unlocalized states at the mobility edge. If the doping level is low, the conduction mechanism at low temperature is carried out via hopping amongst impurity states and in the band tail of localized states, the compound remaining insulating at the lowest temperatures. If the doping level and disorder are high enough, the impurity states can form a band at low temperature allowing metallic (or quasimetallic) conduction, and the situation can be mapped onto a problem of percolation theory of conducting networks [35].In these Pt nanodeposits, the matrix is amorphous carbon, which is known to behave as a semiconductor with a bandgap of about 2 eV [36, 37]. Disorder and impurity states arise from the Pt grains (with random position and a certain size distribution), from Ga implantation, and from defects created in the carbonaceous matrix. Pure metallic behavior as a function of temperature is only expected in systems with percolation of the metallic inclusions, which will occur in nanodeposits with high metallic concentration, as in the FIBID Pt deposits. This is first supported by the room-temperature conductivity value found in our FIBID Pt deposits, σ=1250Ω−1cm−1, which is around the minimum metallic conductivity value reported by Mott and Davis [31].  The linear current-versus-voltage dependence, the quite flat temperature dependence of the resistivity, and the observed tendency of w to zero at low temperature further support this hypothesis. Similar behavior has been observed, for example, in the doping of amorphous semiconducting Ge with Fe [31, 38] and in the doping of amorphous carbon films with I [39]. The nonlinearity observed in [15] in Pt FIBID nanowires with room-temperature resistance of about 20 kΩ is not inconsistent with our results. A detailed study devoted to explain the temperature dependence of resistance and the current-versus-voltage behavior for FIBID Pt deposits as a function of thickness is in progress and will be published elsewhere.By contrast, the FEBID Pt deposits will have lower disorder and impurity states due to the smaller amount of Pt grains, the absence of Ga implantation, and the lower degree of disorder caused by electrons compared to ions. Thus, the conduction mechanism in such compounds is the typical one of a low-doped amorphous semiconductor, with a low value of room-temperature conductance,σ=0.1Ω−1cm−1, conduction via hopping, and strong increase of resistance at low temperatures. Specially interesting is the observed non-linear current-versus-voltage dependence. In general, in the hopping conduction in semiconductors, an increase in the conductance with the voltage occurs [40]. However, in certain cases, as those reported in [26–29], a negative differential conductivity is observed. It was reported in situations with doping level in the order of 1016–1017 cm-3, where conduction takes place at low voltage via the localized impurity states. The initial decrease in the conductivity is ascribed to the charge trapping in “dead ends” of the hopping network because the electrons cannot hop in opposite direction to that of the applied electric field. With further increase of applied voltage, the band tail of localized states and the band of unlocalized states above the mobility edge start to be involved in the conduction mechanism and the conductivity increases. This scenario can explain the behavior shown in the inset of Figure 5(b).


## 5. Conclusions and Outlook

We have accomplished a study of the growth of Pt by FEBID and FIBID in a dual-beam equipment, focusing on the difference in the transport properties of the as-grown materials. Owing to the real-time control of the electrical resistance of the growing deposits by means of electrical microprobes contacting metallic pads in a circuit prepatterned by optical lithography, the resistivity of such deposits has been determined without any influence of extrinsic effects such as undesired oxidation or contamination. In the range of deposit thickness studied, these measurements indicate that Pt by FIBID is four orders of magnitude more conductive than the FEBID ones. Even in the case of the FIBID of Pt, the resistivity is significantly higher than in bulk Pt (around a factor of 100). In-situ current-versus-voltage measurements on deposits with thickness in the range of 160 nm indicate that whereas the FEBID Pt ones show non-linear behavior, the FIBID Pt ones show linear behavior at room temperature. Moreover, the resistance of FEBID deposits increases strongly with decreasing temperature in sharp contrast to a smooth dependence in the case of the FIBID ones. These results have been explained within the well-established theoretical framework developed for doped amorphous semiconductors.As determined by means of HRTEM experiments, the microstructure of both, the FIBID and FEBID deposits, consists of small crystalline Pt grains (average size about 3 nm) embedded in an amorphous carbonaceous matrix. A scenario has been proposed where the amorphous carbonaceous matrix is semiconducting and the Pt inclusions (and Ga ions in the case of FIBID) act as impurities and give rise to disorder, providing available states inside the gap either as impurity states or a band tail of localized states. As measured by means of EDX, the amount of dopants in the case of the FIBID nanodeposits is significantly larger than in the case of the FEBID ones (roughly 30–40% versus 10–20%, resp.), which would explain the difference in the resistivity of both types of deposit.The obtained results clarify the reason for the difference of resistivity of as-grown FEBID and FIBID of Pt. It is suggested that the conduction is governed by the carbonaceous matrix modulated by the presence of Pt and Ga. In the case of FIBID of Pt, the nanodeposit is in the verge of metallic percolation showing metallic (or quasimetallic) conduction. However, the FEBID Pt deposits are far from metallic conduction, showing features typical of doped amorphous semiconductors.Some positive side effects of the presented methodology can be advanced. First, it will be possible to study the deposit growth mechanisms by tracking the time dependence of the electrical resistance of the deposits. Second, the correlation between the measured in-situ and ex-situ electrical resistance of the deposits can be tackled. Our methodology also allows fast studies of how the deposit resistance depends on some deposition parameter (energy, current, gas flow, substrate temperature, etc.), which can be useful for optimized resistance values in a wide range of applications. Besides, Pt nanodeposits have been used to contact nanowires and nanoparticles in order to study locally the electrical transport of such nanostructures [7, 8]. The results of our work indicate that Pt by FIBID seems a better choice for getting lower contact resistance and, as a consequence, less noisy and more reliable transport measurements. We hope that our work will foster further studies aiming to understand the fascinating properties of metallic deposits induced by ion and electron beams, with application in several domains in nanotechnology.



---

*Source: 936863-2009-04-26.xml*