# Efficient Tandem Organic Light Emitting Diode Using Organic Photovoltaic Charge Generation Layer

Authors: Akanksha Jetly; Rajesh Mehra
Journal: International Journal of Optics
 (2018)

---

## Abstract

Highly efficient tandem red OLED is proposed using planar organic heterojunction based charge generation layer (CGL) of C70 (Fullerene)/CoPc (Cobalt Phthalocyanine). The proposed charge generation layer generates charges and exhibits organic photovoltaic type (OPV) behavior in the red emitter zone which helps in slower efficiency roll-off at higher current densities. In addition an ultrathin layer of Al/LiF is used as electron injection layer (EIL) so as to enhance the injection of electrons from charge generation layer to emissive unit. It is found that the tandem red device can reach current efficiency and luminance of 26 cd/A and 26039 cd/m2 at 20 mA/cm2 and 100 mA/cm2, respectively, which is 1.663 times and 1.665 times higher than the corresponding single emitter device. Moreover, it is known that the tandem device requires double turn-on voltage than conventional devices. In this work, the turn-on voltage of red tandem device (5.85 V) is found to be less than twice the voltage of conventional device (3 V). Further with the introduction of Distributed Bragg Reflector (DBR), enhancement in current efficiency and brightness of tandem red device are observed due to high reflectance property of DBR. Thus, the effective charge generation and OPV function of proposed charge generation layer as well as remarkably high injection property of EIL layer lead to the high performance tandem OLED.


---

## Body

## 1. Introduction

Developed in 1987 and based on the electroluminescent phenomenon, organic light emitting diodes have turned out to be a blessing for both display and lightning applications because of their ability to produce more vibrant colors and amazing features like low operating voltage, wide viewing angle, low power consumption, flexibility, thin, light weight, high resolution, and many more. The basic OLED structure comprises of electroluminescent unit that contains anode and cathode and emitting and transport layers between these electrodes. The light is generated in the emitting layer upon the application of external supply because of the radiative recombination of electrons and holes injected by the electrodes. To make the conventional OLEDs more efficient, the theory of tandem OLED was demonstrated in the year 2003. Tandem OLED is an advancement of basic OLED structure that comprises of two or more electroluminescent units that are placed one over the other and are separated by the interconnecting or charge generation (CGL) layer. They have the potential to achieve higher efficiency and luminance at minuscule current density with the increase in the number of electroluminescent units. They have longer lifespan in contrast to the conventional OLEDs as they have the tendency to reduce efficiency roll-off caused by the higher current density.The enhanced performance of tandem OLED is attributed to the charge generation layer which serves exactly like the heart of tandem OLEDs. As a fundamental interconnector in tandem OLEDs, CGLs must have high transparency, low electrical resistance, matched HOMO LUMO levels with the adjacent transport layers, low power loss, etc. When the external voltage is supplied, charge carriers are generated in the CGL, which are then injected into the neighboring emitting unit via the transport layers, where they combine with the opposite charges injected by the electrodes to generate light.The CGL is typically a p-n junction that consists of metal/metal or metal oxide/metal oxide bilayer structure, organic doped n-type layer/p-type layer, or organic photovoltaic heterojunctions. Out of these, CGLs comprising metal layers or metal oxide layers are comparatively less transparent and electrically more resistant as they can easily react with dopants present in the adjacent transport layer to form complexes, thus enhancing the driving voltage and degrading the performance of the device. Further in OLEDs because of the waveguide modes, surface plasmon, and optical losses, the 75-80% of the total produced light is lost; only 20-25% of the persisting light can be efficiently drawn out of device. Thus, for enhancing the efficiency and performance of device, it becomes very necessary to utilize that lost part of light. To surpass all these limitations organic photovoltaic (OPV) type interconnectors formed of the organic materials with the low energy gap are mostly used [1, 2].They have the tendency to generate the charges called electrically generated charges upon the application of external voltage and they have the additional advantage of absorbing a fraction of wasted photons (packets of light energy) from the emissive layer to form the excitons and then at the interface of heterojunction separates them into free electrons and holes. These free electrons and holes are known as photo generated charges. Thus, due to their unique feature of producing photo as well as electric generated charges, this OPV heterojunctions are contemplated as very efficient interconnectors in tandem OLEDs. In this work, the conjunction of organic fullerene derivative C70 and CoPc (Cobalt Phthalocyanine) heterojunction is proposed as planar charge generation layer of tandem OLEDs, where C70 behaves as n-type semiconductor material that has high thermal stability with exceptionally high electrons mobility and CoPc acts as p-type semiconductor material that has high holes' mobility. Further, to boost up the injections of electrons from the CGL to the neighboring emitting unit, the combination of thin layers of Al (aluminium) along with LiF (Lithium Fluoride) is used as electron injection material. The advantage of using aluminium is that it helps in decreasing the work function of C70, thus increasing the device performance.


## 2. Materials and Methods

In this work, the CGL comprises the multilayers of Al/LiF/C70/CoPc. The coalition of C70/CoPc acts as the planar organic heterojunction at which the charges are generated whereas the Al/LiF works as the effective electron injection layer that helps in enhancing the injection of electrons from CGL to the adjacent emitting units. To exhibit the efficacy of the proposed CGL, various devices are designed and simulated. The detail device structures are given in Table1. The Schematic diagram of tandem device R is shown in Figure 1. In these devices ITO (Indium Tin Oxide) and Al/LiF act as anode and cathode, respectively, NPB (N,N0-bis-(3-naphthy)-N,N′-biphenyl-(1,1′-biphenyl)-4,4′-diamine) as the hole transport layer, and Bphen(4,7-diphenyl-1,10-phenanthroline) as electron transport layer in the two electroluminescent units. To prove the OPV behavior of the proposed CGL, red and blue devices are designed as given in Table 1 using α-NPD (N, N′-Bis(naphthalen-1-yl)-N,N′-bis(phenyl)-2,2-diMe) as host material for red emitter Irpiq3(Tris [1-phenylisoquinoline-C2,N] iridium(III)) and sDPVBi (4,4′-bis(2,2′-diphenylvinyl)-1,1′-spirobiphenyl as blue emitting material. The transport layers and electrodes optical constants are drawn from the [1]. The device emitting area is kept at 3 mm X 3 mm and the temperature is kept at 290K for this work. The Fluxim Setfos 4.6 is used to study the electrical and optical properties of the device.Table 1
The detail device structures of red and blue OLEDs.
Device Device Name Layer Structure Red conventional OLED A ITO/EL/LiF (2 nm)/Al (150 nm) Red Tandem OLED R ITO/EL/CGL/EL /LiF (2 nm)/Al (150 nm) Blue conventional OLED B1 ITO/EL 1/LiF (2 nm)/Al (150 nm) Blue Tandem OLED B2 ITO/EL 1/CGL/EL 1/LiF (2 nm)/Al (150 nm) EL: MoO3(3 nm)/NPB (40 nm)/α-NPD: Ir(piq)3 (30 nm, 20% by volume)/Bphen (30 nm). EL 1: MoO3(3 nm)/NPB (40 nm)/sDPVBi (30 nm) /Bphen (30 nm). CGL: Al (3 nm)/LiF (2 nm)/C70 (5 nm)/CoPc (5 nm).Figure 1
Structure of device R.To prove the efficacy of proposed OPV planar heterojunction and the ultrathin electron injection layer (Al/LiF), the conventional single emitter device structure is kept the same as used in [1] except that of the emitter that was CBP: Irpiq2acac (8% by volume). Due to the simulations environment limitation, the emitter used in this work is α-NPD: Ir(piq)3 (20% by volume). However, the emitting zone and the peak wavelength of α-NPD: Ir(piq)3 are the same as that of CBP: Irpiq2acac. Both the emitters emit in the red wavelength zone of 600-800 nm and have peak wavelength around 625 nm. The charge generation layer used in [1] comprised the multilayers of LiF/C60 (Fullerene Derivative 60) /CuPc (copper phthalocyanine) /MoO3, where C60/CuPc exhibits the organic photovoltaic type behavior and LiF and MoO3 are the interface layers that increase the injection of charge carriers from CGL to the emissive layer.


## 3. Results and Discussion

The capacitance versus voltage plot as known from the former studies is the most suitable method to designate that the free positive and negative charge pairs are produced at the interface of the proposed organic heterojunction [3–5].For this purpose, three devices D1-D3 is designed and simulated. The detail structure of the all the three devices is summarized in Table 2. To block the injection of holes and electrons from electrodes thick layers of LiF (50 nm) and MoO3(50 nm) are used alongside anode and cathode, respectively. As can be seen from Figure 2 that, with the increase in the external voltage, the capacitance also increases for device D1 whereas for the devices D2 and D3, the capacitance remains invariable with the voltage.The rise in capacitance with voltage of device D1 should be attributed to the production of free charges at the interface of the proposed organic heterojunction of C70/CoPc because charge carriers from the electrodes are blocked by the thick insulating layers of LiF and MoO3.Table 2
C-V characteristics of three devices D1, D2, and D3.
Device Layer Structure D1 ITO/LiF (50 nm)/C70(5 nm)/CoPc (5 nm)/MoO3(50 nm)/Al(150 nm) D2 ITO/LiF (50 nm)/C70(5 nm)/NPB(5 nm)/MoO3(50 nm)/Al(150 nm) D3 ITO/LiF (50 nm)/Bphen(5 nm)/CoPc (5 nm)/MoO3(50 nm)/Al(150 nm)Figure 2
CV characteristics of devices D1, D2, and D3.To show further the charge generation capability of C70/ CoPc based planar heterojunction, a current limited device is fabricated. The detail structure of device C is summarized as follows: ITO (100 nm)/LiF (50 nm)/C70 (5 nm)/CoPc (5 nm)/MoO3(50 nm)/Al (150 nm). Here the 50 nm thick layers of LiF and MoO3 act as the holes and electrons blocking layers, respectively, that blocks the injection of holes and electrons from the two electrodes. It means that, as shown in Figure 3, the current in the current limited device is only because of the production of charge carriers at the C70/CoPc interface because the injection of charge carriers from the two electrodes are blocked by the thick blocking layers. The whole operating process of the device is shown in Figure 4. On application of voltage, the large amount of charges are produced at the C70/CoPc interface, which moves towards the electrodes from the interface, which are then collected by the electrodes, exhibiting unique diode behavior in the device. So, JV characteristics is one of the most appropriate methods to depict the charge generation ability of the charge generation layer.Figure 3
JV plot of device C.Figure 4
Operating process of device C.The energy level alignment of CGL with the adjacent transport layers is depicted in Figure1. It can be seen that the HOMO (highest occupied molecular orbit) level difference between NPB (5.4 eV) and CoPc (5.2 eV) is only 0.2 eV and LUMO (lowest unoccupied molecular orbit) level difference between C70 (3.9 eV) and Bphen (3.1 eV) is 0.8 eV. Due to the small energy level difference between CGL and the neighboring transport layers, free charge carriers are produced at the interface of C70/CoPc planar heterojunction and transfer to the adjacent emitting layers i.e., holes can easily transfer from HOMO of CoPc to that of NPB while electrons can easily jump from LUMO of C70 to that of Bphen. Then from HOMO of NPB and LUMO of Bphen, the holes and electrons can move easily to the adjacent emitting units where they combine with the opposite charge carriers injected by the electrodes to form photons.The optical and electrical properties are used to study the effect of thickness variation of CGL on the behavior of the device. The effect of thickness variation of CGL on the optical properties is studied by calculating the transmittance for different thickness of C70/CoPc from the absorption spectra as shown in Figure5 by using the formula Transmittance= antilog (2-absorption). Thus, transmittance is calculated to be 94.5 %, 84.62%, and 71.56 %, respectively, for 5 nm, 10 nm, and 15 nm thickness of both C70 and CoPc while for 5 nm thickness of C70 and 10 nm thickness of CoPc, transmittance is 90.28 % and for 10 nm thickness of C70 and 5 nm thickness of CoPc, transmittance is 84.62 % at 625 nm. Thus, the planar organic heterojunction displays the highest transmittance for 5 nm thickness of both C70 and CoPc.Figure 5
Absorbance plot of CGL at various thicknesses.The effect of thickness variation of CGL on the electrical properties is studied by observing the current density versus voltage plot of different thickness of C70/CoPc. A test device T with the structure of ITO/Bphen (30 nm)/Al (3 nm)/LiF (2 nm)/C70 (x nm)/CoPc (y nm)/NPB (40 nm)/Al is designed and simulated for this purpose. The voltages at 200 mA/cm2 are noted for different thickness sets of x and y (x, y). From Figure 6, it is found that voltages are 12.45 V, 13.3 V, 13.4 V, 14.4 V, and 16.46 V, respectively, for thickness sets (5nm, 5 nm), (5nm, 10 nm), (10nm, 5 nm), (10 nm, 10 nm), and (15nm, 15 nm). Thus the minimum voltage is found for 5 nm thickness of both C70 and CoPc for the same current density. Thus, it can be noted that increasing the thickness of CGL causes the difficulty in electron extraction from CGL. That is why, more voltage is required to extract the electrons at same current density with the increasing thickness [6, 7]. Therefore, the optimized thickness of both C70 and CoPc is found to be 5 nm from both the electrical and optical properties.Figure 6
JV plot of CGL at various thicknesses.Further, tandem devices T1-T4 made with distinct interconnectors are designed and simulated to prove the effectiveness of proposed CGL consisting of multilayers of Al/LiF/C70/CoPc and also the advantage of using C70 over C60. The detail design structure of devices T1-T4 is given in Table3. It can be shown from the current efficiency and luminance plots of devices T1-T4 and device A and R as given in Figures 7 and 8, respectively, that, out of all the devices given in Table 3, the red tandem device R with CGL layer consisting of Al/LiF/C70/CoPc shows the best performance in terms of current efficiency and luminance with respect to single emitter device A. The current efficiencies of device T1-T4 and device R, respectively, are found to be 16.97, 17.21, 25.65, 25.37, and 26 cd/A at 20 mA/cm2 and luminance is 16970, 17217, 25660, 25378, and 26039 cd/m2 at 100 mA/cm2. It can be observed that the device R exhibits almost two times enhanced current efficiency and luminance in contrast to device A (15.63 cd/A and 15,630 cd/m2).Table 3
Detailed layer structures of red tandem OLED with different interconnectors.
Device Layer Structure T1 ITO/EL/IC 1/EL/LiF(2 nm)/Al(150 nm) T2 ITO/EL/IC 2/EL/LiF(2 nm)/Al(150 nm) T3 ITO/EL/IC 3/EL/LiF(2 nm)/Al(150 nm) T4 ITO/EL/IC 4/EL/LiF(2 nm)/Al(150 nm) EL: MoO3 (3 nm)/NPB (40 nm)/α-NPD: Ir(piq)3 (30 nm, 20% by volume)/Bphen (30 nm). IC 1: C70 (5nm)/CoPc (5 nm). IC 2: LiF (2 nm)/C70 (5 nm)/CoPc (5 nm). IC 3: Al (3 nm)/C70 (5nm)/Pentacene (5 nm). IC 4: Al(3 nm)/LiF (2 nm)/C60 (5 nm)/CoPc (5 nm).Figure 7
Current efficiency plot of various devices.Figure 8
Luminance plot of various devices.This enhanced performance can be attributed to the interface layer or injection layer used with CGL which are crucial because of their functional efficacy and excellent charge injection property which eventually causes carrier recombination and balance in the emitting layer and also to the large energy level alignment between CoPc and C70 as well as good transport ability of C70 than that of C60. The HOMO of CoPc is 5.2 eV and LUMO of C60 is 3.7 eV whereas that of C70 is 3.9 eV. Therefore electrons have to cross a large energy barrier of 1.5 eV to jump to LUMO of C60 from the HOMO of CoPc in contrast to C70/CoPc where the energy barrier is 1.3 eV. Thus C70/CoPc heterojunction is highly efficient than the C60/CoPc heterojunction [8].The EL spectra of both the structures A and R are shown in Figure9. It can be noticed that the two spectra almost coincide over each other; i.e., there is very minuscule difference between the two spectra. Both the devices show peak wavelength located in red emitter zone at 628 nm. Thus, the proposed CGL has negligible impact on EL spectra relative to red single emitter device. From Luminance versus current density plot studied at 1000 cd/m2 (Figure 8) it is found that current density of structure A is 6.39 mA/cm2 which is 1.6 times higher than device R having current density of 3.84 mA/cm2. Thus device R requires less current density than the device A to reach the same luminance. Therefore there is slow efficiency roll-off in device R than device A which increases with the current density. Thus, tandem devices are more efficient than conventional devices.Figure 9
EL spectra of devices A and R.Normally it has been known that the turn-on voltage of tandem OLED is over two times greater in contrast to conventional OLED, as in tandem device two EL units are used [9–11]. But from the current density versus voltage graph as shown in Figure 10, the turn-on voltage of device A is found to be 3 V and device R is found to be 5.85 V which is less than two times the turn-on voltage of device A. It should be because of less voltage drop across the proposed CGL, thus showing its effectiveness. From Figure 8, the luminance of the tandem device R is 26,039 cd/m2 that is 1.66 times the luminance of device A (15,630 cd/m2) at 100 mA/cm2. In addition, the current efficiency of device R is 26 cd/A which is almost twice as compared to device A (15.63 cd/A). Further enhancement in EQE of device R is also observed in contrast to device A. The detail EL performances of the device R and A are concluded in Table 4.Table 4
Comparison of proposed devices with the corresponding devices used in [1].
Parameters Red Single Emitter Device A Red Single Emitter Device [1] Red Tandem Device R Red Tandem Device [1] Current Efficiency (cd/A) @ 20 mA/cm2 15.63 8 26 17 Luminance (cd/m2) @ 100 mA/cm2 15630 7593 26039 16061 EQE @ 1000 cd/m2 17.9 8.8 29.3 14.1Figure 10
JV plot of devices A and R.The difference in the performance of tandem device and single emitter unit device is because of the microcavity effect, interference from light, and many more. The enhancement in performance of tandem devices is because of the CGL that produced almost the same number of free charges as are inoculated by the anode and cathode, thus causing charge carriers balance which leads to reduction in quenching and the plasmonic losses and also increases the microcavity effect. Also, the emission quenching caused by relaxed CoPc molecules is reduced because of the large distance between emitting unit and CGL. Further, the electric field intensity of tandem device is found to be less in contrast to the single emitter device, thereby reducing the quenching effect caused by electric field in tandem device in contrast to single emitter device. In addition, in tandem devices both the emitting layers are located at the two antinodes so as to take the benefit of increased light output from the microcavity effect [12–15].To observe the OPV behavior of proposed heterojunction, the UV-vis absorption spectra of C70/CoPc and the photoluminescent spectra ofα-NPD: Ir(piq)3 are studied. As shown in Figure 11 both spectra overlap each other in the red emitter zone of 600-800 nm. So it can be presumed that the red wasted photons due to surface plasmon and waveguide modes in the emitter can be easily absorbed by C70/CoPc heterojunction to form excitons and further dissociate them into free charges, thus enhancing the efficiency. A blue tandem device B2 as shown in Table 1 is further designed and simulated to show the organic photovoltaic behavior of the C70/CoPc heterojunction. From the UV-vis absorption spectra of C70/CoPc and that of the blue emitter used as shown in Figure 12, it can be seen that two spectra do not coincide; i.e., the peak of the emitter does not fall in the main absorbing area of the C70/CoPc. So, it can be concluded that the proposed CGL is not able to observe the blue photons generated in the emitter.Figure 11
Absorption, PL spectra of CGL, and red emitter.Figure 12
Absorption, PL spectra of CGL, and blue emitter.Also, from Figures13 and 14, it can be seen that current efficiency and luminance of tandem device B2 (42.25 cd/A and 42250 cd/m2) at 20 mA/cm2 and 100 mA/cm2, respectively, is only 1.42 times the current efficiency and luminance of device B1 (29.67 cd/A and 29670 cd/m2) whereas because of the OPV type behavior of device R which is the absorption of red wasted photons by the proposed heterojunction, the current efficiency of device R at the same current density is 1.6 times the efficiency of device A. The JV characteristics of device B1 and B2 are shown in Figures 15 and 16, respectively. It can be observed that the turn-on voltage of device B2 is about 4.2 V which is 2.3 times greater than that of device B1 having turn-on voltage of 1.8 V. On the other hand, from Figure 10, it can be observed that the turn-on voltage of device R is only 1.9 times greater than that of device A. It is because in device B2, the CGL does not exhibit OPV type behavior, so the excitons are not present in the CoPc layer. So, the charge generation at the low current density is due to the transfer of electrons from HOMO of CoPc to the LUMO of C70 and because of the large energy barrier between the C70 and CoPc interface as depicted in Figure 1, greater value of electric field is needed for the charge carriers transfer, thereby reducing the efficiency and requiring high turn-on voltage.Figure 13
Current efficiency plot of devices B1 and B2.Figure 14
Luminance plot of device B1 and B2.Figure 15
JV plot of of device B1.Figure 16
JV plot of device B2.The basic requirement in CGL is the generation of charges at the CGL interface. Many models have been proposed till date to show the charge generation capability of CGL like Kroger et al. who in [16] have suggested that the charge production capability of interconnector does not depend on temperature. Sun et al. in [17] have demonstrated through JV characteristics the charge production ability of interconnector under reverse bias. In this work, the charge generation capability of CGL is explained through J-V and C-V plot of tandem device R as shown in Figures 17 and 18, respectively. It can be seen that, at about 1.1 V forward voltage, the current begins to increase; on the other hand correspondingly there is a drastic decrease in the capacitance which can be attributed to the large injection and recombination of charge carriers. Also, at about 1V reverse voltage there is critical decrease in capacitance as well as current breakdown which can be attributed to large generation of charge carriers at C70/CoPc heterojunction [16]. This is because under the reverse voltage, hole and electron transport layers should stop the transport of electrons and holes, respectively. So, the large reverse current in the device R should be because of the charge carriers production rather than because of the injection by anode and cathode under the reverse bias. The entire working process of tandem device can be concluded as follows. At small current density, due to the generation of charges at heterojunction, current efficiency increases rapidly with the increase in luminance of device. Then, the current efficiency becomes invariable, after attaining the maximum height. This is because of the recombination of these generated charges at CGL with the charges inoculated by electrodes in the emissive layer to produce photons. Due to the OPV type behavior, CGL fetches a part of wasted photons from emissive layer to generate more charges and again the whole process repeats causing the slower efficiency roll-off. Thus, this OPV type CGL is very effective and results in longer lifespan of the device.Figure 17
JV plot of device R at various temperatures.Figure 18
Mott-Schottky plot of device R at 282K.Further to improve the performance of device R in terms of efficiency, longer lifespan, and low power consumption and to elucidate microcavity effect for red emitter, DBR substrates consisting of quarter wavelength stack two layers of high refractive index Zirconium Dioxide (ZrO2) and low refractive index Silicon Dioxide (SiO2) is used. The reflectance of Distributed Bragg Reflector (DBR) structure depends upon variation in the refractive index of layers and number of layer pairs used in the structure. The more the gap and number of pairs are, the greater the reflectance will be. The DBR structures with high reflectance help in achieving highly effective cavity structures and thus help in improving brightness of the device. The optimized quarter wavelength thickness of ZrO2is found to be 64 nm by using the formula (λ/4nZrO2 = 64nm, where nZrO2 = 2.45, λ = 628 nm) and that of SiO2 is found to be 107 nm (λ/4nSiO2 = 107nm, where nSiO2 = 1.4575, λ = 628 nm). Here λ = 628 nm is the peak wavelength of device R. The reflectance (Figure 19) of single pair of ZrO2 and SiO2 is found to be approximately 56% at 625-628 nm wavelength. Further enhancement in current efficiency and luminance (Figure 20) at 20 mA/cm2 and 100 mA/cm2, respectively, of device R is observed with the DBR structure which is found to be 31.80 cd/A and 31,800 cd/m2 respectively. This enhancement is due to the constructive interference of light because of DBR structure.Figure 19
Reflectance of DBR structure.Figure 20
Current Efficiency and Luminance plot of DBR structure.


## 4. Conclusions

In this paper, the novel planar organic heterojunction of C70/CoPc is proposed as planar charge generation layer which shows organic photovoltaic type behavior in red wavelength range from 600 to 800 nm. The advantage of using organic photovoltaic CGL is that they can generate charges and can absorb the wasted photons from emitter to form excitons and dissociate them into free electrons and holes. As a result, there is rather slower efficiency roll-off as compared to other devices. The tandem device exhibits 1.63 and 1.65 times enhanced current efficiency and luminance in contrast to conventional device. Also, remarkable reduction in turn-on voltage of the proposed tandem device as compared to other tandem device is observed. The turn-on voltage of tandem device is found to be only 1.9 times greater than that of the single emitter unit device. This remarkable improvement in performance can be attributed to the excellent charge generation, separation ability of interconnector, and excellent transport capability of Al/LiF electron injection layer which can be seen from the great rise of capacitance and current density with voltage. Also, from -J-V and C-V curves it can be confirmed further that the produced carriers are due to the reverse bias current. Further, by inculcating DBR structure of high refractive index ZrO2and low refractive index SiO2, the performance of tandem device in terms of current efficiency and luminance got enhanced by almost two times in contrast to conventional OLED. Thus, the doping free planar organic heterojunction yields high performance tandem OLED with the low fabrication cost. Also, the proposed work opens the path to explore the behavior of organic photovoltaic heterojunctions for fabricating highly efficient OLEDs.



---

*Source: 9458530-2018-09-26.xml*