# Improvement of Mechanical Properties of Noil Hemp Fiber Reinforced Polypropylene Composites by Resin Modification and Fiber Treatment

Authors: Zili Yan; Jianchun Zhang; Hua Zhang; Hao Wang
Journal: Advances in Materials Science and Engineering
 (2013)

---

## Abstract

The present study aims to improve the reinforcement of hemp fibre to polypropylene (PP) by simple resin modification and fibre treatment. Maleic anhydride grafted polypropylene (MAPP) was used as resin modifier by direct mixing with PP, and hydrophobically modified hydroxyethyl cellulose (HMHEC) was used as fibre treatment reagent by immersing fibre into its aqueous solution. The influences of fibre content, resin modification, and fibre treatment on the mechanical properties (tensile, flexural, and impact strengths) of composites were investigated. The change of interfacial bonding between fibre and resin in composites caused by MAPP and HMHEC was studied by scanning electron microscopy and dynamic mechanical analysis. Resin modification and fibre treatment were effective to enhance the mechanical properties of the composites. The improvement in interfacial bonding is quantitatively evaluated with adhesion factor.


---

## Body

## 1. Introduction

Glass fibres are the most widely used reinforcement to plastics due to their low cost and satisfactory effectiveness. However, their drawbacks are also evident, including the health risk when handling and nonbiodegradability when disposed [1, 2]. Using natural fibres, especially plant fibres, as replacement of glass fibres can overcome the above-mentioned problems with additional advantages, including cost-effectiveness, low density, high specific strength, and their availability as renewable resources [3–5]. So far, natural fibres have been used to replace glass fibres in automotive industry but mostly in nonstructural components [6, 7]. The first and most important reason for the limited application of natural fibre composites is due to the poor interfacial bonding between the hydrophilic natural fibres and the hydrophobic resins, which means the poor shear stress transferring ability at microscale and the unsatisfactory mechanical properties at macroscale in the composites [8, 9]. Additional disadvantages arisen from this drawback are apparent fibre breakage and unavoidable thermal degradation when internal mixing or extruding is used to fabricate compound of natural fibre and plastic because strong shearing force and long compounding time are necessary to realize homogeneous fibre distribution [10–12].Many studies have been focused on resin modification and fibre treatment to improve interfacial bonding. For thermoplastic matrix composites, a lot of resin modifiers have been developed and shown positive effect on interfacial bonding and mechanical properties [13–15]. The most effective modifier is maleic grafted polymer in which the maleic anhydride can react with the hydroxygen group on natural fibre surface, and the main chain of modifier entangles with the matrix [15]. However, the overall mechanical properties of the composites are still lower than corresponding glass fibre reinforced composites [16]. Fibre surface treatment is another approach to achieve improved mechanical performance. Various fibre treatments have been developed using alkali, isocyanate, silane, and acrylic acids, permanganate, and so forth [17, 18]. Nevertheless, much water is consumed to wash the alkali treated fibre to neutral PH, and many of other treatments are undertaken in pure organic solvent or mixed solvent containing organic solvent, which have the problems of disposal of chemicals after treatment [19]. Caulfield et al. [20] used aqueous emulsion of paper sizing agents (alkyl ketene dimer and alkenyl succinic anhydride) to treat cellulose fibre. The treatment improved the hydrophobicity of the fibre and the compatibility between the fibre and the matrix but did not show any improvement in mechanical properties of the composites.This research is an attempt aiming to develop simple resin modification and fibre treatment route to improve mechanical properties of hemp fibre reinforced polypropylene composites. The fibre treatment was carried out simply by immersing fibre into aqueous solution of hydrophobically modified hydroxyethyl cellulose (HMHEC) followed by oven drying. Resin modification was achieved by applying maleic anhydride grafted polypropylene (MAPP) to Polypropylene (PP).


## 2. Experimental Section

### 2.1. Raw Materials

Noil hemp fibre (NHF) was obtained from China-Hemp Industrial Investments and Holding Co., Ltd. (Yunnan Province, China). It is an overdegummed hemp fibre by-product in hemp fibre production for textile purpose, with a length shorter than the requirement for textile industry. The chemical composition and microstructure of NHF are shown in Table1 and Figure 1, respectively. It mainly consists of cellulose (91.9 wt%) and has low content of pectin, hemicellulose, and lignin. The fibre has smooth surface and an average diameter of 20–30 μm.Table 1
The chemical composition of NHF.
Components
Cellulose, wt%
Lignin, wt%
Hemicellulose, wt%
Pectin, wt%
Others, wt%
NHF
91.9
1.7
3.5
1.2
1.7
Note: the chemical composition test was based on dry hemp fibre.Photo and micrograph of NHF.
(a)
(b)Polypropylene (PP, M800E, Sinopec Shanghai petrochemical Co. Ltd., China) with melt flow index of8.0±1.5 g/10 min was chosen as a matrix. MAPP with MA content of 1.0 wt% (Bondyram 1001, Polyram Ram-On Industries, Israel) was used as a modifier to the resin. HMHEC (NATROSOL Plus 330, Hercules Chemicals Co. Ltd., China) was used as a fibre treatment reagent. Antioxidant and anti-UV agents were applied as additives to the composites.


### 2.2. Composites Preparation

HMHEC powder was added into stirred water and then kept for 24 h to get a semitransparent aqueous solution with 0.5 wt% of HMHEC. Then NHF was immersed in the solution for 0.5 h with a fibre/solution weight ratio of 1/5. After that, the treated NHF was taken out and heated to 60°C for 12 h and then to 105°C for 8 h to remove water/moisture before it was used for composite fabrication. When no fibre treatment was applied to NHF, it was heated to 105°C and kept for 8 h to remove moisture before mixing with PP.After the internal mixer was preheated to 170–180°C, PP, antioxidants (0.3%), and an anti-UV agent (0.3%) were added into it and mixed for 15 min to make the resin melt with a rotor speed of 50 rpm. Then NHF was added into the mixer to mix with resin melt for 10–15 min at the same temperature and rotor speed. After that, the composite melt was sheeted using an open mill. The cooled sheets were then crushed into granule of 3–7 mm in size by a crusher. The granules were finally moulded into specimens at 170–175°C for mechanical tests by an injection moulding machine. Composites with 10–40 wt% NHF were fabricated to evaluate the influence of fibre content on the mechanical properties of composites. Composites with MAPP modification to PP and HMHEC treatment to NHF were also fabricated. For those two composites, MAPP was added into the internal mixer together with PP, and the contents of MAPP and NHF were fixed at 5 wt% and 30 wt%, respectively.


### 2.3. Characterizations

In accordance with ISO 527-2-1993, the tensile strength test was performed on dumbbell-shaped specimens of Type 1A using a multifunctional machine (AG-2000A, Shimadzu Corp., Japan) with a loading rate of 10 mm/min and a 10 kN load cell at room temperature. The standard samples with nominal dimensions of 80 mm × 10 mm × 4 mm were used to measure the flexural strength using the above-mentioned MPa multifunctional machine according to ISO 178-2001 with a loading rate of 3 mm/min. The unnotched Charpy impact strength test was conducted on standard samples with nominal dimensions of 80 mm × 10 mm × 4 mm with an impact tester (XCJ24, Chengde Testing Machine Co., Ltd., China) in accordance with ISO 179-2000. All the results were based on average value of at least five specimens.A scanning electron microscopy (SEM, JSM-646-LV, Shimadzu Corp., Japan) was used to observe the microstructure of the fracture surface of tensile test specimens and fibre-matrix interface adhesion. The acceleration voltage is 20 kV. The fracture surface of the specimens was lightly sputter coated with carbon before SEM observation. Dynamic mechanical analyzer (DMA, Q-800, TA instrument, USA) was used to evaluate the damping coefficient and the adhesion factor of different composites. Rectangular specimens of 60 mm × 10 mm × 3.5 mm were used for this test, which were cut and sanded from injection moulded specimens for flexural/impact strength tests. The tests were carried out under a dual cantilever mode at a fixed frequency of 1 Hz in a temperature range of 30–145°C. The deflection amplitude was 15μm, and the heating ramp rate was 3°C/min.


## 2.1. Raw Materials

Noil hemp fibre (NHF) was obtained from China-Hemp Industrial Investments and Holding Co., Ltd. (Yunnan Province, China). It is an overdegummed hemp fibre by-product in hemp fibre production for textile purpose, with a length shorter than the requirement for textile industry. The chemical composition and microstructure of NHF are shown in Table1 and Figure 1, respectively. It mainly consists of cellulose (91.9 wt%) and has low content of pectin, hemicellulose, and lignin. The fibre has smooth surface and an average diameter of 20–30 μm.Table 1
The chemical composition of NHF.
Components
Cellulose, wt%
Lignin, wt%
Hemicellulose, wt%
Pectin, wt%
Others, wt%
NHF
91.9
1.7
3.5
1.2
1.7
Note: the chemical composition test was based on dry hemp fibre.Photo and micrograph of NHF.
(a)
(b)Polypropylene (PP, M800E, Sinopec Shanghai petrochemical Co. Ltd., China) with melt flow index of8.0±1.5 g/10 min was chosen as a matrix. MAPP with MA content of 1.0 wt% (Bondyram 1001, Polyram Ram-On Industries, Israel) was used as a modifier to the resin. HMHEC (NATROSOL Plus 330, Hercules Chemicals Co. Ltd., China) was used as a fibre treatment reagent. Antioxidant and anti-UV agents were applied as additives to the composites.


## 2.2. Composites Preparation

HMHEC powder was added into stirred water and then kept for 24 h to get a semitransparent aqueous solution with 0.5 wt% of HMHEC. Then NHF was immersed in the solution for 0.5 h with a fibre/solution weight ratio of 1/5. After that, the treated NHF was taken out and heated to 60°C for 12 h and then to 105°C for 8 h to remove water/moisture before it was used for composite fabrication. When no fibre treatment was applied to NHF, it was heated to 105°C and kept for 8 h to remove moisture before mixing with PP.After the internal mixer was preheated to 170–180°C, PP, antioxidants (0.3%), and an anti-UV agent (0.3%) were added into it and mixed for 15 min to make the resin melt with a rotor speed of 50 rpm. Then NHF was added into the mixer to mix with resin melt for 10–15 min at the same temperature and rotor speed. After that, the composite melt was sheeted using an open mill. The cooled sheets were then crushed into granule of 3–7 mm in size by a crusher. The granules were finally moulded into specimens at 170–175°C for mechanical tests by an injection moulding machine. Composites with 10–40 wt% NHF were fabricated to evaluate the influence of fibre content on the mechanical properties of composites. Composites with MAPP modification to PP and HMHEC treatment to NHF were also fabricated. For those two composites, MAPP was added into the internal mixer together with PP, and the contents of MAPP and NHF were fixed at 5 wt% and 30 wt%, respectively.


## 2.3. Characterizations

In accordance with ISO 527-2-1993, the tensile strength test was performed on dumbbell-shaped specimens of Type 1A using a multifunctional machine (AG-2000A, Shimadzu Corp., Japan) with a loading rate of 10 mm/min and a 10 kN load cell at room temperature. The standard samples with nominal dimensions of 80 mm × 10 mm × 4 mm were used to measure the flexural strength using the above-mentioned MPa multifunctional machine according to ISO 178-2001 with a loading rate of 3 mm/min. The unnotched Charpy impact strength test was conducted on standard samples with nominal dimensions of 80 mm × 10 mm × 4 mm with an impact tester (XCJ24, Chengde Testing Machine Co., Ltd., China) in accordance with ISO 179-2000. All the results were based on average value of at least five specimens.A scanning electron microscopy (SEM, JSM-646-LV, Shimadzu Corp., Japan) was used to observe the microstructure of the fracture surface of tensile test specimens and fibre-matrix interface adhesion. The acceleration voltage is 20 kV. The fracture surface of the specimens was lightly sputter coated with carbon before SEM observation. Dynamic mechanical analyzer (DMA, Q-800, TA instrument, USA) was used to evaluate the damping coefficient and the adhesion factor of different composites. Rectangular specimens of 60 mm × 10 mm × 3.5 mm were used for this test, which were cut and sanded from injection moulded specimens for flexural/impact strength tests. The tests were carried out under a dual cantilever mode at a fixed frequency of 1 Hz in a temperature range of 30–145°C. The deflection amplitude was 15μm, and the heating ramp rate was 3°C/min.


## 3. Results and discussion

### 3.1. Effect of Fibre Content on Mechanical Properties of the Composites

Fibre content has important influence on the overall performance of composites. Figure2 shows the effect of NHF content on mechanical properties of the composites without resin modification and fibre treatment. Tensile strength is decreased to 26.7 MPa, when fibre content is 10 wt% compared with neat PP (31.1 MPa). Further increasing fibre content to 40 wt% has negligible effect on tensile strength of the composites. Flexural strength in NHF/PP almost keeps constant with increasing the NHF from 0 to 40 wt%. Comparing to the tensile strength of composites, the standard deviation of flexural strength is so small that it is invisible. The impact strength of PP/NHF decreases with increasing the fibre from 56 KJ/m2 in neat PP to 16.8 KJ/m2 in PP/NHF (40 wt%). The overall mechanical properties of the composites are lower than neat PP. As has been stated in the pieces of literature [21, 22], the low adhesion between the hydrophilic natural fibre and hydrophobic PP is the reason why direct compounding of fibre and PP cannot exhibit fibre reinforcement.The influence of fibre content on mechanical properties of NHF/PP composites.
(a)
(b)


### 3.2. Effect of Resin Modification and Fibre Treatment

Fibre treatment and resin modification are necessary to achieve the benefit from fibre to reinforce plastics [15, 23]. Figure 3 shows the influence of resin modification with MAPP and fibre treatment with HMHEC on the mechanical properties of the composites with 30 wt% fibre. Tensile, flexural, and impact strengths of the composites with MAPP (NHF/PP/MAPP) are 39.3 MPa, 62.6 MPa, and 33 KJ/m2, respectively. Compared to the composites without MAPP (NHF/PP), the improvements by MAPP addition are 40%, 47%, and 44%, respectively. The combination of fibre treatment and resin modification (HMHEC/NHF/PP/MAPP) leads to further improvement in tensile strength and impact strength but shows minimal effect on flexural strength. The finial composites show a tensile strength of 44.5 MPa (13% improvement compared to resin modified composites), a flexural strength of 60.9 MPa (3% decrease), and an impact strength of 39.3 kJ/m2 (19% improvement).Figure 3
Influence of resin modification with MAPP and fibre treatment with HMHEC on the mechanical properties of the composites.


### 3.3. Fracture Surface of Composites

Figure4 shows fracture surfaces of the three composites, unmodified, resin modified, and resin modified plus fibre treated. There is a visible difference in fracture surface between the three composites. When no resin modification and no fibre treatment were conducted to the composites (NHF/PP), fibre has a tendency to be pulled out from the matrix, and the extracted fibre length is long (Figure 4(a)). For the composites with 5 wt% MAPP resin modification (NHF/PP/MAPP) (Figure 4(b)), fibre breakage is the main fracture mechanism, and the extracted fibre is shorter than that in NHF/PP. The fracture surface of composites with both resin modification and fibre treatment (HMHEC/NHF/PP/MAPP) shows similar appearance with NHF/PP/MAPP but less fibre pullout (Figure 4(c)).SEM images of fracture surface of (a) NHF/PP; (b) NHF/PP/MAPP; (c) HMHEC/NHF/PP/MAPP.
(a)
(b)
(c)The previous difference demonstrates the enhanced interfacial bonding in composites by resin modification and fibre treatment. MAPP has been used as modifier in wood plastic composites to improve interfacial bonding because of the reaction between maleic anhydride of MAPP and hydrogen on fibre surface, together with the entanglement of the PP chain between MAPP and the matrix [24–26]. HMHEC for fibre treatment has hydroxyethylcellulose (HEC) as hydrophilic main chain and long-chain alkyl group as hydrophobic graft chain (Figure 5) [27]. The similar structure between HEC and cellulose in NHF allows Van der Waals forces and hydrogen bond between the modifier and NHF. The olefinic structure of the graft chain is miscible with polypropylene. Both the graft chain and the main chain of HMHEC contributed to the improvement of the interfacial bonding of the composites.Figure 5
Illustration of HMHEC in aqueous solution.


### 3.4. Fibre Matrix Adhesion Factor

Dynamic mechanical analysis (DMA) is a powerful technique to characterize transition and relaxation process of matrix resin and the effect from fibre [28]. tanδ, damping coefficient from DMA test, is to characterize the energy dissipation of polymers and their composites. It has been commonly employed to determine the interfacial characteristics of composites because interfacial bonding is one of the most significant sources of damping in composites [29]. In general, a perfect interface will transfer the entire load from matrix to fibre and does not therefore contribute to the damping characteristics. Based on previous research with DMA, an adhesion factor (A) is adopted to evaluate the interfacial bonding of composites [30], which can be expressed as
(1)A=11-Vftanδctanδm-1,
in which Vf is fibre volume fraction and tanδc and tanδm represent the damping coefficients of the composite and the matrix, respectively. A low value of adhesion factor is an indication of good interfacial bonding between the fibre and the matrix.The damping coefficients of neat PP and three composites are shown in Figure6. tanδ of neat PP and its composites increases with the rising of temperature. However, there is an apparent difference between them. Compared with neat PP, NHF/PP has lower tanδ at low temperature but higher tanδ at high temperature, whereas the composites with resin modification and fibre treatment, NHF/PP/MAPP and HMHEC/NHF/PP/MAPP, have lower tanδ in the whole temperature range of the DMA test, which means that the resin modification and the fibre treatment improve the interfacial bonding in composites. Furthermore, the fibre treatment leads to even lower tanδ of the composites (HMHEC/NHF/PP/MAPP) at high temperature. Figure 7shows the calculated adhesion factors of three composites. Unmodified composites (NHF/PP) have higher adhesion factor in the whole temperature range. The MAPP resin modification brings about a significant decrease in adhesion factor. When the fibre treatment is combined with resin modification, the adhesion factor is slightly increased at low temperature but noticeably decreased at high temperature.Figure 6
Plots oftanδ versus temperature of neat PP and its composites.Figure 7
Adhesion factor of different composites.The results are consistent with the molecular movement theory and the previous research on the dynamic mechanical analysis of composites [31, 32]. Different from single phase of neat resin, the composite is consists of three phases: matrix, fibre, and interfacial phases. Therefore, besides the matrix, both the fibre and the interface affect the comprehensive properties of the composites, including the damping behavior. The fibre behaves more elastically than the matrix resin [31], which leads to the reduced energy dissipation of composites in the whole temperature range of the DMA test. The interfacial bonding in composites affects tanδ by restricting the molecular movement of the resin on the fibre surface. In NHF/PP, the poor interfacial bonding between NHF and PP shows limited restriction to the molecular movement of matrix, especially at high temperature. Due to the combined influence by fibre and the interfacial bonding, NHF/PP has lower tanδ at low temperature and higher tanδ at low temperature than PP. The effect of MAPP in enhancing interfacial bonding has been repeatedly testified in this study and leads to the lower tanδ of NHF/PP/MAPP than that of NHF/PP. The further decreased tanδ in HMHEC/NHF/PP/MAPP at high temperature suggests the effectiveness of fibre treatment in improving the interfacial bonding. Based on the previous discussion, it suggests that tanδ of composites at high temperature is more related with interfacial bonding. Figure 7 shows an adhesion factor sequence of NHF/PP > NHF/PP/MAPP > HMHEC/NHF/PP/MAPP at high temperature, which means increased interfacial bonding by resin modification and fibre treatment. Slightly high adhesion factor of HMHEC/NHF/PP/MAPP at low temperature (less than 65°C) compared to NHF/PP/MAPP is also observed Figure 7. Similar result was reported in the research of glass sphere/polyethylene composites [32]. It could be attributed to high molecular mobility of HMHEC due to its small molecular weight compared with PP. It is also noticed that MAPP addition results in more significant reduction of adhesion factor, which indicates that resin modification is more effective in improving the mechanical properties of the hemp/PP composites.


## 3.1. Effect of Fibre Content on Mechanical Properties of the Composites

Fibre content has important influence on the overall performance of composites. Figure2 shows the effect of NHF content on mechanical properties of the composites without resin modification and fibre treatment. Tensile strength is decreased to 26.7 MPa, when fibre content is 10 wt% compared with neat PP (31.1 MPa). Further increasing fibre content to 40 wt% has negligible effect on tensile strength of the composites. Flexural strength in NHF/PP almost keeps constant with increasing the NHF from 0 to 40 wt%. Comparing to the tensile strength of composites, the standard deviation of flexural strength is so small that it is invisible. The impact strength of PP/NHF decreases with increasing the fibre from 56 KJ/m2 in neat PP to 16.8 KJ/m2 in PP/NHF (40 wt%). The overall mechanical properties of the composites are lower than neat PP. As has been stated in the pieces of literature [21, 22], the low adhesion between the hydrophilic natural fibre and hydrophobic PP is the reason why direct compounding of fibre and PP cannot exhibit fibre reinforcement.The influence of fibre content on mechanical properties of NHF/PP composites.
(a)
(b)


## 3.2. Effect of Resin Modification and Fibre Treatment

Fibre treatment and resin modification are necessary to achieve the benefit from fibre to reinforce plastics [15, 23]. Figure 3 shows the influence of resin modification with MAPP and fibre treatment with HMHEC on the mechanical properties of the composites with 30 wt% fibre. Tensile, flexural, and impact strengths of the composites with MAPP (NHF/PP/MAPP) are 39.3 MPa, 62.6 MPa, and 33 KJ/m2, respectively. Compared to the composites without MAPP (NHF/PP), the improvements by MAPP addition are 40%, 47%, and 44%, respectively. The combination of fibre treatment and resin modification (HMHEC/NHF/PP/MAPP) leads to further improvement in tensile strength and impact strength but shows minimal effect on flexural strength. The finial composites show a tensile strength of 44.5 MPa (13% improvement compared to resin modified composites), a flexural strength of 60.9 MPa (3% decrease), and an impact strength of 39.3 kJ/m2 (19% improvement).Figure 3
Influence of resin modification with MAPP and fibre treatment with HMHEC on the mechanical properties of the composites.


## 3.3. Fracture Surface of Composites

Figure4 shows fracture surfaces of the three composites, unmodified, resin modified, and resin modified plus fibre treated. There is a visible difference in fracture surface between the three composites. When no resin modification and no fibre treatment were conducted to the composites (NHF/PP), fibre has a tendency to be pulled out from the matrix, and the extracted fibre length is long (Figure 4(a)). For the composites with 5 wt% MAPP resin modification (NHF/PP/MAPP) (Figure 4(b)), fibre breakage is the main fracture mechanism, and the extracted fibre is shorter than that in NHF/PP. The fracture surface of composites with both resin modification and fibre treatment (HMHEC/NHF/PP/MAPP) shows similar appearance with NHF/PP/MAPP but less fibre pullout (Figure 4(c)).SEM images of fracture surface of (a) NHF/PP; (b) NHF/PP/MAPP; (c) HMHEC/NHF/PP/MAPP.
(a)
(b)
(c)The previous difference demonstrates the enhanced interfacial bonding in composites by resin modification and fibre treatment. MAPP has been used as modifier in wood plastic composites to improve interfacial bonding because of the reaction between maleic anhydride of MAPP and hydrogen on fibre surface, together with the entanglement of the PP chain between MAPP and the matrix [24–26]. HMHEC for fibre treatment has hydroxyethylcellulose (HEC) as hydrophilic main chain and long-chain alkyl group as hydrophobic graft chain (Figure 5) [27]. The similar structure between HEC and cellulose in NHF allows Van der Waals forces and hydrogen bond between the modifier and NHF. The olefinic structure of the graft chain is miscible with polypropylene. Both the graft chain and the main chain of HMHEC contributed to the improvement of the interfacial bonding of the composites.Figure 5
Illustration of HMHEC in aqueous solution.


## 3.4. Fibre Matrix Adhesion Factor

Dynamic mechanical analysis (DMA) is a powerful technique to characterize transition and relaxation process of matrix resin and the effect from fibre [28]. tanδ, damping coefficient from DMA test, is to characterize the energy dissipation of polymers and their composites. It has been commonly employed to determine the interfacial characteristics of composites because interfacial bonding is one of the most significant sources of damping in composites [29]. In general, a perfect interface will transfer the entire load from matrix to fibre and does not therefore contribute to the damping characteristics. Based on previous research with DMA, an adhesion factor (A) is adopted to evaluate the interfacial bonding of composites [30], which can be expressed as
(1)A=11-Vftanδctanδm-1,
in which Vf is fibre volume fraction and tanδc and tanδm represent the damping coefficients of the composite and the matrix, respectively. A low value of adhesion factor is an indication of good interfacial bonding between the fibre and the matrix.The damping coefficients of neat PP and three composites are shown in Figure6. tanδ of neat PP and its composites increases with the rising of temperature. However, there is an apparent difference between them. Compared with neat PP, NHF/PP has lower tanδ at low temperature but higher tanδ at high temperature, whereas the composites with resin modification and fibre treatment, NHF/PP/MAPP and HMHEC/NHF/PP/MAPP, have lower tanδ in the whole temperature range of the DMA test, which means that the resin modification and the fibre treatment improve the interfacial bonding in composites. Furthermore, the fibre treatment leads to even lower tanδ of the composites (HMHEC/NHF/PP/MAPP) at high temperature. Figure 7shows the calculated adhesion factors of three composites. Unmodified composites (NHF/PP) have higher adhesion factor in the whole temperature range. The MAPP resin modification brings about a significant decrease in adhesion factor. When the fibre treatment is combined with resin modification, the adhesion factor is slightly increased at low temperature but noticeably decreased at high temperature.Figure 6
Plots oftanδ versus temperature of neat PP and its composites.Figure 7
Adhesion factor of different composites.The results are consistent with the molecular movement theory and the previous research on the dynamic mechanical analysis of composites [31, 32]. Different from single phase of neat resin, the composite is consists of three phases: matrix, fibre, and interfacial phases. Therefore, besides the matrix, both the fibre and the interface affect the comprehensive properties of the composites, including the damping behavior. The fibre behaves more elastically than the matrix resin [31], which leads to the reduced energy dissipation of composites in the whole temperature range of the DMA test. The interfacial bonding in composites affects tanδ by restricting the molecular movement of the resin on the fibre surface. In NHF/PP, the poor interfacial bonding between NHF and PP shows limited restriction to the molecular movement of matrix, especially at high temperature. Due to the combined influence by fibre and the interfacial bonding, NHF/PP has lower tanδ at low temperature and higher tanδ at low temperature than PP. The effect of MAPP in enhancing interfacial bonding has been repeatedly testified in this study and leads to the lower tanδ of NHF/PP/MAPP than that of NHF/PP. The further decreased tanδ in HMHEC/NHF/PP/MAPP at high temperature suggests the effectiveness of fibre treatment in improving the interfacial bonding. Based on the previous discussion, it suggests that tanδ of composites at high temperature is more related with interfacial bonding. Figure 7 shows an adhesion factor sequence of NHF/PP > NHF/PP/MAPP > HMHEC/NHF/PP/MAPP at high temperature, which means increased interfacial bonding by resin modification and fibre treatment. Slightly high adhesion factor of HMHEC/NHF/PP/MAPP at low temperature (less than 65°C) compared to NHF/PP/MAPP is also observed Figure 7. Similar result was reported in the research of glass sphere/polyethylene composites [32]. It could be attributed to high molecular mobility of HMHEC due to its small molecular weight compared with PP. It is also noticed that MAPP addition results in more significant reduction of adhesion factor, which indicates that resin modification is more effective in improving the mechanical properties of the hemp/PP composites.


## 4. Conclusions

The incompatibility of hydrophilic hemp fibre and hydrophobic polypropylene leads to poor interfacial bonding between the fibre and the matrix. Resin modification and fibre treatment are effective in improving the interfacial bonding, which results in improved mechanical properties. MAPP resin modification leads to 40% improvement in tensile strength, 47% in flexural strength, and 44% in impact strength. When combining fibre treatment with resin modification, the mechanical properties are further improved, and the resulted hemp/PP composites achieved a tensile strength of 44.5 MPa, a flexural strength of 60.9 MPa, and an impact strength of 39.3 KJ/m2. The fracture surface observation indicates that the fracture mechanism is changed from fibre pullout to fibre breakage after the resin modification and fibre treatment. The improvement of interfacial bonding can be quantitatively evaluated by fibre matrix adhesion.



---