# Improved Sensitization of Zinc Oxide Nanorods by Cadmium Telluride Quantum Dots through Charge Induced Hydrophilic Surface Generation

Authors: Karthik Laxman; Tanujjal Bora; Salim H. Al-Harthi; Joydeep Dutta
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

This paper reports on UV-mediated enhancement in the sensitization of semiconductor quantum dots (QDs) on zinc oxide (ZnO) nanorods, improving the charge transfer efficiency across the QD-ZnO interface. The improvement was primarily due to the reduction in the interfacial resistance achieved via the incorporation of UV light induced surface defects on zinc oxide nanorods. The photoinduced defects were characterized by XPS, FTIR, and water contact angle measurements, which demonstrated an increase in the surface defects (oxygen vacancies) in the ZnO crystal, leading to an increase in the active sites available for the QD attachment. As a proof of concept, a model cadmium telluride (CdTe) QD solar cell was fabricated using the defect engineered ZnO photoelectrodes, which showed ∼10% increase in photovoltage and ∼66% improvement in the photocurrent compared to the defect-free photoelectrodes. The improvement in the photocurrent was mainly attributed to the enhancement in the charge transfer efficiency across the defect rich QD-ZnO interface, which was indicated by the higher quenching of the CdTe QD photoluminescence upon sensitization.


---

## Body

## 1. Introduction

The interfacial chemistry between two semiconductors or a metal and a semiconductor is important in determining the charge transfer across the interface that dictates the performance in areas like catalysis [1], solar cells [2], and other schemes involving charge separation processes. In a structure comprising a semiconductor QD deposited on top of a high surface area semiconducting nanostructured oxide, like in the sensitized solar cells, the current flowing across the QD-oxide junction is directly proportional to the distance between the QDs and the oxide material [2, 3]. This is especially important in quantum dot (QD) sensitized solar cells (QDSSC), where the QDs are deposited on oxide supports with the use of linkers, which increases the distance between the two semiconductors and thus generates lower current densities as compared to linker-free or directly attached QDs [4]. On the flip side, QDs deposited without linker molecules are randomly sized which limits their use in wavelength specific applications like light emitting diodes (LEDs) and rainbow solar cells [5]. Additionally, energy band mismatches between the two semiconductors can further hinder electron hopping from the excited state of the QD to the supporting oxide [6–8].As a supporting oxide, ZnO nanostructures with their wide band gap (3.37 eV) and high electron mobility have been extensively used in sensitized solar cells [9, 10]. In particular, the well-defined morphology and the facile formation of single crystalline ZnO nanorods (NRs) have attracted attention as a suitable photoelectrode (PE) [11, 12]. ZnO crystal comprises a zinc rich polar plane (0001) together with mixed terminated planes (0110, 1010, and 1100), which are relatively nonpolar in nature [13]. Modification of the surface energy of these nonpolar crystal planes by ligand functionalization [14, 15] and nanoparticle coating [16] enhances the QD loading factor and hence NR usability in solar cells [17].In this work we have shown the modification of NR surface energy by the incorporation of defects using beyond band gap (UV-c) photoirradiation of its surface for prolonged periods [18], reducing ZnO crystal stoichiometry and rendering its surface hydrophilic [19, 20]. We use the ZnO crystal nonstoichiometry to uniformly enhance surface energy, without any chemical modification, and employ this technique to demonstrate an improvement in the interfacial charge transfer at the QD-ZnO interface in a model quantum dot sensitized solar cell.


## 2. Materials and Methods

### 2.1. Materials

Analytical grade zinc acetate dihydrate [Zn(CH3COO)2·2H2O], zinc nitrate hexahydrate [Zn(NO3)2·6H2O] from Merck, and hexamethylenetetramine (C6H12N4) from Aldrich were used for the synthesis of ZnO NRs. Chloroplatinic acid (H2PtCl6·H2O), sodium sulphide (Na2S) from Qualigens, sublimated sulphur from Panreac (PRS), potassium chloride (KCl) from Carlo Erba, and methanol from Emsure were obtained. Fluorine doped tin oxide (SnO2 : F) coated conducting glass substrates (FTO, 12 Ω/cm2) were sourced from Nippon Sheet Glass, Japan. Sodium tellurite (Na2TeO3) and 3-mercaptopropionic acid (HSCH2CH2CO2H) were procured from Aldrich Chemicals; cadmium chloride (CdCl2·5H2O), sodium borohydride (NaBH4), and trisodium citrate dihydrate (C6H5Na3O7·2H2O) were acquired from Merck. All chemicals were of analytical grade and were used without further purification processes.


### 2.2. ZnO Nanorod Synthesis

ZnO nanorods were grown hydrothermally on microscope glass substrates and fluorine doped tin oxide (FTO) substrates as per our previous reports [13, 21]. The substrates were precleaned by successive sonication in soap water, ethanol, acetone, and deionised (DI) water for 15 minutes each and dried in an oven until further use. A ZnO seed layer was deposited on the cleaned substrates by spraying 15 mL of 10 mM zinc acetate dihydrate [Zn(CH3COO)2·2H2O] solution in DI water at a rate of 1 mL/min (from a distance of 20 cm), where the cleaned substrates were preheated at 420°C on a hot plate. Seeded substrates were then allowed to cool naturally and were subsequently placed in a chemical bath containing equimolar (20 mM) concentration of zinc nitrate hexahydrate [Zn(NO3)2·6H2O] and hexamethylenetetramine (C6H12N4) solution in DI water at 95°C for 20 hours; the solution was replenished every 5 hours to obtain uniform nanorod growth [22]. The ZnO NR coated substrates were then removed from the chemical bath and rinsed thoroughly with DI water and some samples were annealed in air at 350°C for 60 minutes prior to further use.


### 2.3. CdTe Quantum Dot Synthesis

CdTe quantum dots were synthesized following a previous report [23] with minor modifications. In brief, 0.12 M of cadmium chloride (CdCl2) was dissolved in 8 mL of DI water and then diluted to 84 mL with constant stirring. To this solution 0.024 M trisodium citrate dihydrate, 0.03 M Na2TeO3 in 8 mL of DI water, 0.011 M 3-MPA, and 0.086 M NaBH4 were successively added with constant stirring to make the CdTe QD stock solution. This stock solution was refluxed for 20 minutes in a commercial microwave oven (in low power mode) to precipitate the CdTe QDs which were then washed several times in DI water and resuspended in DI water.


### 2.4. Ultraviolet (UV) Annealing of ZnO NRs in Ultrahigh Vacuum (UHV) and in Ambient Air

For UHV UV annealing, as-prepared and air-annealed ZnO NRs on glass substrates were subjected to high energy UV irradiation (21 eV) under 10−10mbar pressure for a period of 40 minutes. For ambient air UV annealing, as-prepared and air-annealed ZnO NRs were exposed to 12 Watts of 4.9 eV UV-c irradiation for 180 minutes, by keeping the substrates at a distance of 3 cm from the UV lamps (Philips TUV 6W germicidal lamps) in the ambient air.


### 2.5. Solar Cell Assembly and Characterization

Solar cells with an active area of 0.25 cm2 were fabricated by thermally fusing (using DuPont Surlyn 1702) ZnO-CdTe photoelectrode (PE) and platinized FTO (0.5 mM hexachloroplatinate) counterelectrode (CE). Two holes predrilled in the CE allowed filling of polysulfide electrolyte acting as the redox agent. The PE was fabricated by immersing air-annealed and UV-annealed (in the ambient air) ZnO NR coated FTO substrates into a concentrated CdTe QD colloidal solution (2.06 g/L). The substrates were kept immersed at 70°C for 3 hours to allow adsorption of QDs on the ZnO NR surface, followed by drying in air at 70°C. For UV-annealed samples, exposure to UV-c irradiation in the ambient air was carried out for 180 minutes prior to the QD deposition. The counterelectrode (CE) was prepared by dropping 7 μL of 5 mM hexachloroplatinate hydrate (H2Cl6Pt·H2O) solution dissolved in isopropanol on cleaned FTO substrates. The substrate was then left to dry at room temperature, followed by annealing in air at 385°C for 30 minutes. Electrolyte was prepared as per previous reports [24]. In brief, 2 M sublimated sulphur, 0.6 M Na2S, and 0.2 M KCl were dissolved in 50 mL solution mixture of DI water and methanol in the ratio of 3 : 7, respectively. The assembled cell was characterized using Sciencetech 150W Small Beam Solar Simulator (SF150) under AM1.5 G illumination (100 mW/cm2). Keithley 617 Programmable Electrometer was used as an input voltage source and a current meter, to measure the output current and record the current-voltage (I-V) characteristics of the devices.


### 2.6. Characterization

CdTe quantum dots were characterized using JOEL JEM 2010 high resolution transmission electron microscope working at 20 KV, while the ZnO nanorods were characterized using field emission scanning electron microscope (SEM, IE350FSG FESEM), working at 30 KV. X-ray diffraction measurements of ZnO NR thin films on glass substrates were carried out by Rigakuminiflex 600 XRD system with a Cu Kα X-ray source (wavelength ~1.54 angstrom). Water contact angle (WCA) measurements were made by dropping 5 μL of water on air-annealed ZnO NR coated glass substrates before and after exposing them to 4.9 eV UV-c irradiation for varying periods of time. Between each measurement, the NR substrates were annealed at 100°C in air for 30 minutes. WCA was recorded with a customized contact angle instrument equipped with Dino Lite Pro AM 413T digital microscope camera [19]. WCA values were determined using ImageJ Analysis software, following a method described previously [25]. Steady state absorption and emission of the QDs were characterized by Perkin Elmer Lambda 25 and Perkin Elmer LS-55 Fluorescence Spectrometer, respectively. Photoluminescence (PL) measurements on ZnO-CdTe PEs were made by sensitizing the ZnO NRs (with and without UV treatment) with a monolayer of CdTe QDs, followed by exciting the PEs with a wavelength of 450 nm and collecting the emission up to 700 nm, based on CdTe QD PL peak at 540 nm. X-ray photoelectron spectroscopy (XPS) measurements were carried out using Omicron Nanotechnology system using a monochromatic Al Kα radiation (hυ=1,486.6 eV) at 10−10mbar base pressure. The source voltage and emission current were 20 kV and 20 mA, respectively. Deconvolutions of the peaks were performed by Casa XPS software (Fairley, N. CASA XPS, version 2.0). Infrared spectroscopy measurements were made on Avatar 360 HATR (horizontal attenuated total reflection (HATR)) FTIR Spectrometer from Thermo Nicolet after detaching the ZnO NRs from the glass substrates. The spectrum was measured on air-annealed NRs in powder form before and after exposing them to 4.9 eV UV-c irradiation for 180 minutes in ambient air.


## 2.1. Materials

Analytical grade zinc acetate dihydrate [Zn(CH3COO)2·2H2O], zinc nitrate hexahydrate [Zn(NO3)2·6H2O] from Merck, and hexamethylenetetramine (C6H12N4) from Aldrich were used for the synthesis of ZnO NRs. Chloroplatinic acid (H2PtCl6·H2O), sodium sulphide (Na2S) from Qualigens, sublimated sulphur from Panreac (PRS), potassium chloride (KCl) from Carlo Erba, and methanol from Emsure were obtained. Fluorine doped tin oxide (SnO2 : F) coated conducting glass substrates (FTO, 12 Ω/cm2) were sourced from Nippon Sheet Glass, Japan. Sodium tellurite (Na2TeO3) and 3-mercaptopropionic acid (HSCH2CH2CO2H) were procured from Aldrich Chemicals; cadmium chloride (CdCl2·5H2O), sodium borohydride (NaBH4), and trisodium citrate dihydrate (C6H5Na3O7·2H2O) were acquired from Merck. All chemicals were of analytical grade and were used without further purification processes.


## 2.2. ZnO Nanorod Synthesis

ZnO nanorods were grown hydrothermally on microscope glass substrates and fluorine doped tin oxide (FTO) substrates as per our previous reports [13, 21]. The substrates were precleaned by successive sonication in soap water, ethanol, acetone, and deionised (DI) water for 15 minutes each and dried in an oven until further use. A ZnO seed layer was deposited on the cleaned substrates by spraying 15 mL of 10 mM zinc acetate dihydrate [Zn(CH3COO)2·2H2O] solution in DI water at a rate of 1 mL/min (from a distance of 20 cm), where the cleaned substrates were preheated at 420°C on a hot plate. Seeded substrates were then allowed to cool naturally and were subsequently placed in a chemical bath containing equimolar (20 mM) concentration of zinc nitrate hexahydrate [Zn(NO3)2·6H2O] and hexamethylenetetramine (C6H12N4) solution in DI water at 95°C for 20 hours; the solution was replenished every 5 hours to obtain uniform nanorod growth [22]. The ZnO NR coated substrates were then removed from the chemical bath and rinsed thoroughly with DI water and some samples were annealed in air at 350°C for 60 minutes prior to further use.


## 2.3. CdTe Quantum Dot Synthesis

CdTe quantum dots were synthesized following a previous report [23] with minor modifications. In brief, 0.12 M of cadmium chloride (CdCl2) was dissolved in 8 mL of DI water and then diluted to 84 mL with constant stirring. To this solution 0.024 M trisodium citrate dihydrate, 0.03 M Na2TeO3 in 8 mL of DI water, 0.011 M 3-MPA, and 0.086 M NaBH4 were successively added with constant stirring to make the CdTe QD stock solution. This stock solution was refluxed for 20 minutes in a commercial microwave oven (in low power mode) to precipitate the CdTe QDs which were then washed several times in DI water and resuspended in DI water.


## 2.4. Ultraviolet (UV) Annealing of ZnO NRs in Ultrahigh Vacuum (UHV) and in Ambient Air

For UHV UV annealing, as-prepared and air-annealed ZnO NRs on glass substrates were subjected to high energy UV irradiation (21 eV) under 10−10mbar pressure for a period of 40 minutes. For ambient air UV annealing, as-prepared and air-annealed ZnO NRs were exposed to 12 Watts of 4.9 eV UV-c irradiation for 180 minutes, by keeping the substrates at a distance of 3 cm from the UV lamps (Philips TUV 6W germicidal lamps) in the ambient air.


## 2.5. Solar Cell Assembly and Characterization

Solar cells with an active area of 0.25 cm2 were fabricated by thermally fusing (using DuPont Surlyn 1702) ZnO-CdTe photoelectrode (PE) and platinized FTO (0.5 mM hexachloroplatinate) counterelectrode (CE). Two holes predrilled in the CE allowed filling of polysulfide electrolyte acting as the redox agent. The PE was fabricated by immersing air-annealed and UV-annealed (in the ambient air) ZnO NR coated FTO substrates into a concentrated CdTe QD colloidal solution (2.06 g/L). The substrates were kept immersed at 70°C for 3 hours to allow adsorption of QDs on the ZnO NR surface, followed by drying in air at 70°C. For UV-annealed samples, exposure to UV-c irradiation in the ambient air was carried out for 180 minutes prior to the QD deposition. The counterelectrode (CE) was prepared by dropping 7 μL of 5 mM hexachloroplatinate hydrate (H2Cl6Pt·H2O) solution dissolved in isopropanol on cleaned FTO substrates. The substrate was then left to dry at room temperature, followed by annealing in air at 385°C for 30 minutes. Electrolyte was prepared as per previous reports [24]. In brief, 2 M sublimated sulphur, 0.6 M Na2S, and 0.2 M KCl were dissolved in 50 mL solution mixture of DI water and methanol in the ratio of 3 : 7, respectively. The assembled cell was characterized using Sciencetech 150W Small Beam Solar Simulator (SF150) under AM1.5 G illumination (100 mW/cm2). Keithley 617 Programmable Electrometer was used as an input voltage source and a current meter, to measure the output current and record the current-voltage (I-V) characteristics of the devices.


## 2.6. Characterization

CdTe quantum dots were characterized using JOEL JEM 2010 high resolution transmission electron microscope working at 20 KV, while the ZnO nanorods were characterized using field emission scanning electron microscope (SEM, IE350FSG FESEM), working at 30 KV. X-ray diffraction measurements of ZnO NR thin films on glass substrates were carried out by Rigakuminiflex 600 XRD system with a Cu Kα X-ray source (wavelength ~1.54 angstrom). Water contact angle (WCA) measurements were made by dropping 5 μL of water on air-annealed ZnO NR coated glass substrates before and after exposing them to 4.9 eV UV-c irradiation for varying periods of time. Between each measurement, the NR substrates were annealed at 100°C in air for 30 minutes. WCA was recorded with a customized contact angle instrument equipped with Dino Lite Pro AM 413T digital microscope camera [19]. WCA values were determined using ImageJ Analysis software, following a method described previously [25]. Steady state absorption and emission of the QDs were characterized by Perkin Elmer Lambda 25 and Perkin Elmer LS-55 Fluorescence Spectrometer, respectively. Photoluminescence (PL) measurements on ZnO-CdTe PEs were made by sensitizing the ZnO NRs (with and without UV treatment) with a monolayer of CdTe QDs, followed by exciting the PEs with a wavelength of 450 nm and collecting the emission up to 700 nm, based on CdTe QD PL peak at 540 nm. X-ray photoelectron spectroscopy (XPS) measurements were carried out using Omicron Nanotechnology system using a monochromatic Al Kα radiation (hυ=1,486.6 eV) at 10−10mbar base pressure. The source voltage and emission current were 20 kV and 20 mA, respectively. Deconvolutions of the peaks were performed by Casa XPS software (Fairley, N. CASA XPS, version 2.0). Infrared spectroscopy measurements were made on Avatar 360 HATR (horizontal attenuated total reflection (HATR)) FTIR Spectrometer from Thermo Nicolet after detaching the ZnO NRs from the glass substrates. The spectrum was measured on air-annealed NRs in powder form before and after exposing them to 4.9 eV UV-c irradiation for 180 minutes in ambient air.


## 3. Results and Discussion

The hydrothermally synthesized ZnO nanorods (NRs) which were used as the supporting oxide have a length and diameter of ~3.5μm and ~70 nm, respectively, as observed from the scanning electron micrographs with a preferential orientation in the 002 axis, as observed from the XRD pattern (Figure 1). Absorption and emission spectra of aqueous cadmium telluride quantum dots (CdTe QDs) used as a model QD show peaks at 500 nm and 550 nm, respectively (Figure 2(a)). From the corresponding selected area electron diffraction (SAED) pattern and HRTEM images (Figure 2(b)), it can be observed that the QDs are nearly monocrystalline in nature with a diameter of ~5 nm (Figure 2(b)), which was confirmed by dynamic light scattering based particle size measurement (Supplementary Information Figure S1 in Supplementary Material available online at http://dx.doi.org/10.1155/2014/919163). The effect of UV light induced defects on the interfacial charge transfer efficiency was examined by fabricating model solar cells by depositing a monolayer of CdTe QDs on top of the ZnO nanorods with and without exposure to UV-c light (see experimental section) and measuring the current density across the CdTe-ZnO interface.Figure 1
X-ray diffraction (XRD) peaks of hydrothermally synthesized wurtzite ZnO nanorods using equimolar (20 mM) solution mixture of zinc nitrate (Zn(NO3)2) and hexamethylenetetramine at 90°C showing preferential orientation along the 002 axis and field emission scanning electron microscopy (FESEM) images of ZnO nanorods (inset).(a) Absorption and emission of cadmium telluride quantum dots (CdTe QDs) samples used for the preparation of photoelectrodes of solar cells. The emission was triggered by exciting the QDs at 445 nm; (b) high resolution transmission electron microscope (HRTEM) of as-synthesized CdTe QDs showing single-crystalline nature of QDs (inset) small area electron diffraction (SAED) pattern of CdTe QDs.
(a)
(b)The measuredI-V response of three individual solar cells (Supplementary Information Figure S3) shows an average increase of 66% in the short circuit current density along with a 10% increase in open circuit voltage for UV-c light exposed photoelectrodes (UVPEs) as compared to non-UV-exposed or air-annealed ZnO-CdTe photoelectrodes (PPEs) (Table 1). It is to be noted that the current density can be increased by increasing the QD deposition layers (Supplementary Information Table S1) but was limited to a monolayer for better comparison of the interfacial processes. SEM images of two PEs point to increased and more uniform distribution of CdTe QDs on the ZnO NRs exposed to UV-c irradiation as compared to air-annealed ZnO nanorods, where moderate agglomeration and nonuniform surface coverage of the QDs could be observed (Figure 3).Table 1
Voltage and current magnitudes for a monolayer of CdTe QD’s on ZnO NR’s w/wo UVA in ambient air.
Samples
Short circuit current density
Open circuit voltage
(μA/cm2)
(mV)
Defect-free ZnO nanorods based CdTe QD-ZnO solar cell photoelectrodes
150 (+/−8)
37.5
UV defect induced ZnO nanorods based CdTe QD-ZnO solar cell photoelectrodes
250 (+/−12)
41.0Field emission scanning electron microscope (FESEM) images of CdTe QDs decorated on ZnO NRs showing a comparison of (a) bare air-annealed ZnO NRs; (b) CdTe QD decorated air-annealed ZnO NRs, and (c) CdTe QD decorated ultraviolet (UV) light annealed ZnO NRs; (d), (e), and (f) show close-up of the (a), (b), and (c) images while the insets in (d), (e), and (f) show top view of the same samples at different areas. UV-annealed defect engineered ZnO NRs show well distributed CdTe QDs along the cross section and tips of the NRs compared to annealed ZnO NRs.
(a)
(b)
(c)
(d)
(e)
(f)Previous reports have suggested that ZnO exposure under UV light can lead to the formation of surface defects, specifically oxygen vacancies [18], which can increase surface hydrophilicity. This is advantageous for the deposition of aqueous QDs on ZnO, as it increases the interaction of water media with the ZnO surface, leading to increase in the surface area available for QD deposition. We were able to confirm the change in hydrophilicity by water contact angle (WCA) measurements made on ZnO nanorod surfaces before and after UV-c exposure, where UV-exposed ZnO showed a dramatic WCA reduction from 100° to ~12° after 180 minutes of UV-c irradiation (Figure 4(a)), indicating a substantial change in the surface energy of the nanorods [19]. The increased surface energy results from the donation of photogenerated electrons to surface adsorbed O2 and H2O, leading to the creation of surface adsorbed superoxide anions (O2-) and hydroxyl radicals. The photogenerated holes in turn migrate to the surface providing a site for dissociative adsorption of atmospheric moisture [18, 19, 26], which was evident in the infrared spectroscopy (FTIR) spectra, which showed a considerable increase in surface hydroxyl adsorption and a distinct broadening and bathochromic shift of the hydroxyl peaks (Figure 4(b)). The hydroxyl peaks were identified at a lower energy (3400 cm−1) in UV-exposed rods, which is characteristic of intermolecular strongly hydrogen bonded O–H [27]. Broadening of the O–H peaks was also observed, which shows that the hydroxyl ions are bonded to ZnO surface with varying energies, where the higher energy O–H stretch peaks (3790 cm−1) are attributed to weakly hydrogen bonded and free O–H [27]. Additionally CO2, which have been known to adsorb on surface oxygen vacancies, were also detected on the surface (Supplementary Information Figure S2).(a) Water contact angle measurements made on 350°C air-annealed ZnO NRs before and after UV-c exposure for varying times showing surface saturation after ~180 minutes. The insets show images of the water droplet (5μL) on the ZnO NR surface for different UV exposure times and (b) infrared absorption spectra of air-annealed ZnO NRs before and after UV annealing in ambient air. The spectra show the increase in surface OH concentration, organic impurity degradation, and attachment of CO2 on the NR surfaces after UV annealing in air.
(a)
(b)To better understand and quantify the formation of oxygen vacancies, air-annealed ZnO nanorods were exposed to UV irradiation in ultrahigh vacuum (UHV), followed by XPS measurements (Figure5). Deconvolution of O1s peak shows that it could be fitted with 2 component peaks centred at 529.93 eV and 530.88 eV (Figure 5(b)), which are characteristic of ZnO lattice oxygen and surface adsorbed hydroxyls and moisture [18, 28]. Integration of the area under the O1s spectra indicates the formation of surface oxygen vacancies upon UHV UV irradiation, manifesting in a reduction of surface oxygen content (Table 2 and Figure 5(a)). This confirms that UV annealing tends to release lattice and adsorbed oxygen, disturbing the equilibrium between creation and annihilation of photogenerated charges leading to the creation of localized defects on the stoichiometric ZnO surface [18].Table 2
XPS quantitative ratios of O2− and OH peaks in air-annealed and as-prepared ZnO NRs before and after UV annealing (UVA) in ultrahigh vacuum. “A” stands for air-annealed NRs and as-grown NRs before UV annealing in their respective rows.
Samples
Ratio before and after UV annealing in UHV
O1s[UVA]/O1s[A]
O2−UVA/O2−[A]
OH[UVA]/OH[A]
Annealed ZnO
0.98
0.95
1.02
As-grown ZnO
1.06
1.02
1.12(a) X-ray photoelectron spectroscopy (XPS) of oxygen O1s spectra of 350°C air-annealed ZnO NRs before and after UV annealing in ultrahigh vacuum (UHV) environment. The peaks show an increase in oxygen content for as-prepared NRs while decreasing the oxygen in annealed NRs and (b) deconvolution of the O1s peaks showing a decrease in the lattice oxygen and surface hydroxyl content (red triangles) after UV annealing in UHV.
(a)
(b)The defects which are uniformly distributed on the ZnO nanorod surfaces act as QD bonding sites, improving the QD distribution as evident in the SEM images. Further, since the transfer of electrons from excited state of QDs to ZnO is a function of ZnO-QD binding [29, 30], UV annealing induced change in ZnO surface energy may be the vital component which enhances the charge transfer efficiency across the CdTe-ZnO junction. For semiconductors, the electron transfer rate from a single donating state (QD) to a continuum of accepting states like those in ZnO can been represented as [31]
(1)KET=2πħ∫-∞∞ρEH^E214πλKbTexp⁡λ+ΔG+E24λKbT,
where KET is the electron transfer rate, ħ is the reduced Planck constant, Kb is Boltzmann’s constant, λ is system reorganization energy, ΔG is the change in system free energy, ρ(E) is the density of accepting states which is also dependent on depth of defect states, and H^(E) is the overlap matrix element. Faster electron injection rates result when there is a better match between the system free energy (ΔG) and the system reorganization energy (λ) [31]. In the region where ΔG~λ as in ZnO, small changes in ΔG can cause steep changes in KET, which might explain the faster injection dynamics after UV annealing. On a physical level, reactive surface species formed by the dissociative adsorption of water molecules on ZnO defect sites [32] can change the surface free energy, possibly leading to sporadic degradation of some 3-MPA ligands on the CdTe QDs. This will reduce the ZnO-CdTe interfacial separation due to electrostatic attraction between the semiconductor surfaces [29], which in turn reduces the charge injection barrier, increasing the distance dependent electron tunnelling rate [30] as illustrated in Figures 6(a) and 6(b). This phenomenon was clearly evident in the CdTe QD photoluminescence (PL) quenching measurements conducted on UV-exposed and air-annealed ZnO PEs. UV-exposed PEs showed better PL quenching, suggesting a lower resistance to the charge injection phenomenon and a more intimate interface between the ZnO nanorods and CdTe QDs (Figure 7). It is to be noted that the excitation wavelength used for the PL characterization was 450 nm, where ZnO is inactive, while CdTe QD is highly active. This negates the interference of ZnO emission with CdTe QD emission, enabling measurement of only CdTe emission for better characterization.Schematic of change in attachment scheme and charge transfer efficiency of CdTe QDs on UV-annealed and air-annealed ZnO NR PE surfaces illustrating (a) CdTe attachment sites concentrated mainly on the upper surface of annealed ZnO NRs showing binding through the carboxylic end of 3-MPA; (b) change in charge transfer efficiency after UV annealing in ambient air as a result of uniform distribution of defect sites leading to an increase in the active surface area for the NRs, along with enhanced exposure of CdTe QD core to ZnO NR surface.
(a)
(b)Figure 7
Normalized photoluminescence (PL) measurements on CdTe QD decorated ZnO NR substrates showing lower luminescence (improved charge transfer from QD to ZnO) in UV treated ZnO substrates as compared to air-annealed ZnO substrates. The excitation was carried out at 450 nm, where ZnO is inactive to avoid interference by ZnO emission peaks.We thus propose a scheme where photoinduced surface defects on ZnO nanorods can transform a moderately active planar ZnO surface into a high energy reactive surface, which enhances the QD loading while simultaneously decreasing the interfacial charge transfer resistance due to direct electrostatic attachment of the QDs on the ZnO supports. Utilization of such a facile surface modification technique is independent of the type of QD used and can be useful in various surface related phenomena making it an effective tool for enhancing surface chemistry of semiconductor nanostructures.


## 4. Conclusion

We have introduced a controlled photomediated approach to create uniformly distributed surface charges on ZnO, leading to increase in ZnO surface energy. The increased surface energy showed greater hydrophilicity with water contact angle (WCA) changing from 1000 before UV exposure to 120 after UV exposure and was characterized by XPS and was partly found to be oxygen vacancies. The hydrophilic surfaces were shown to have better affinity towards QD loading while simultaneously increasing the efficiency of charge transfer across the ZnO-QD interface. Model solar cells made from the hydrophilic surfaces show 10% and 66% increase in voltage and current, respectively, opening a new approach for incorporating narrow band absorption control of sensitized cells along with the advantage of enhanced sensitization and better interfacial characteristics. Such surfaces can improve charge separation at the interface and can be utilized in diverse applications involving surface dominated reactions.



---

*Source: 919163-2014-12-10.xml*