# Krypton Gas for High Quality Single Wall Carbon Nanotubes Synthesis by KrF Excimer Laser Ablation

Authors: Jasim Al-Zanganawee; Adrian Katona; Calin Moise; Dionezie Bojin; Marius Enachescu
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

We report for the first time the production of  single wall carbon nanotubes (SWCNTs) by KrF excimer laser ablation method under the krypton gas atmosphere. For the ablation experiment 450 mJ energy and 30 Hz repetition rate KrF excimer laser was used, and the target was prepared with the following composition: 0.6% Ni, 0.6% Co, and 98.8% C (atomic percentage). The ablation product was characterized by confocal Raman microspectroscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM), and thermogravimetric analysis (TGA). The SWCNTs obtained are a mixture of semiconducting and metallic types with narrow diameters distribution of 1.26 to 1.49 nm, are micrometers long, and contain low amount of  graphite and amorphous carbon.


---

## Body

## 1. Introduction

Since Iijima discovered the multiwall carbon nanotubes in 1990 [1] and especially in 1993 when Iijima and Ichihashi discovered the single wall carbon nanotubes [2], they are still attracting the interests of great number of scientific research groups and industries around the world because of their exceptional electrical [3], mechanical [4], thermal [5], and magnetic [6] properties. The CNTs have been used in different types of applications such as biosensors [7], chemical sensors [8], scanning microscope tips [9], nanoelectronics [10], third generation solar cell [11], and hydrogen storage [12].Many different techniques have been used and developed for production of carbon nanotubes such as chemical vapour deposition (CVD) [13], arc discharge [14], and laser ablation techniques [15]. Pulse laser ablation method was observed to yield specifically high quality and high purity [16] and high yield [17] of single wall carbon nanotubes. Several types of lasers have been used to produce SWCNTs such as Nd:YAG laser [16, 18], CO2 laser [15], XeCl excimer laser [19], and KrF excimer laser [20–22]. Parameters such as laser wavelength, carrier gas, ablation temperature, or metal catalysts content of the target have been studied for the optimization of PLA method [22]. For example, the furnace temperature and the gas flow velocity can influence the diameter distribution of SWCNTs. By increasing the furnace temperature or the gas flow velocity, SWCNTs with larger diameter distribution can be produced [23].To the best of our knowledge, there are no reports in the literature of using krypton gas for the synthesis of single wall carbon nanotubes using KrF excimer laser ablation. In this work, we report the synthesis of single wall carbon nanotubes with narrow diameter distribution (1.26–1.49 nm) and few micrometers in length by using KrF excimer laser ablation with wavelength of 248 nm in krypton atmosphere as carrier gas.


## 2. Materials and Methods

The KrF excimer laser used for the ablation was produced by Coherent COMPex Pro 205 equipment, having the wavelength of 248 nm and the pulse period of 20 ns. In our study we used a laser energy of 450 mJ and 30 Hz repetition rate. The laser ablation experiment was carried out in a custom-designed installation depicted in Figure1 [22, 24].Figure 1
Ablation chamber design [22, 23].The ablation parameters like temperature, pressure, and laser repetition rate were selected based on the previous optimization studies done in our group [22]. The oven temperature, pressure, and ablation time of the experimental work were 1100°C, 500 Torr, and 60 minutes, respectively.The laser ablation starts by passing the laser beam through a UV transparent quartz window and enters into the quartz tube hitting the target, when the target material begins to be ablated. The target was rotated during ablation with constant speed to get uniform ablation. Then the inert gas, which enters from the left-up side of the reaction chamber, moves through the quartz tube to the heated area at 1100°C where the reaction takes place, transporting the ablation product toward a copper condenser called cold finger (CF), where it will be deposited as a black soot. The cold finger was cooled down using 12°C water supplied by a chiller. The quartz tube of the reaction chamber was 1260 mm long, with the internal diameter of 50 mm. The inert atmosphere and the transportation of the ablated material to the CF were maintained by using the krypton gas at 70 L/h flow rate.Our system has some special technical features:(i)
The length of the oven was doubled compared with previous designs [16, 25], to ensure a more uniform temperature in the ablation reactor, allowing the product to travel longer time in the constant heated zone favoring the growth of the SWCNTs.(ii)
The cold finger is longer (260 mm) with a higher surface than the previous one [22], reducing the temperature gradient over its length and improving the capture of the product.(iii)
The attached ALICAT flow meter controller allows controlling accurately the flow rate of the carrier gas over a wide range 0–10 NPLM with a resolution of 0.01.The target containing C, Co, and Ni was prepared by following a recipe developed by Professor Enachescu’s group. This recipe involves the mixing of graphite cement (GC 8010-B from Metal Forming Lubricants) with Co and Ni metal catalysts powder (Sigma Aldrich), with the following composition 0.6% Ni, 0.6% Co, and 98.8% C (atomic percentage). The mixture was transferred into a Teflon mold (20 mm diameter) and then cured 4 hours at 130°C in air to increase the mechanical strength. Further another heat treatment of the target was applied for one hour at 800°C in inert atmosphere to remove all the remaining organic compounds.After ablation, the raw product soot was collected from the copper cold finger. The abundance of single wall carbon nanotubes in the collected product was investigated using confocal micro-Raman spectroscopy, scanning electron microscopy (SEM) and TEM, and thermogravimetric analysis (TGA).


## 3. Results and Discussion

### 3.1. Raman Spectroscopy Analysis

To identify the SWCNTs, the ablation product was analyzed by confocal Raman microspectroscopy using a Horiba Labram 800 instrument equipped with two laser wavelengths: 532 nm and 633 nm. The Raman spectra were recorded using both excitation wavelengths. The spectrum of the ablation product was compared with the commercial SWCNTs from Sigma as shown in Figure2. The Raman spectra present three main regions specific to SWCNTs: radial breathing mode (RBM) and D and G bands which are further analyzed.Figure 2
Raman spectra of the raw ablation product (a) and the commercial SWCNTs (b) recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)


#### 3.1.1. RBM Band Analysis

For the raw ablation product using the green laser (532 nm and 2.33 eV), two vibrational frequency peaks were found in the RBM band of the Raman spectra, each peak corresponding to a diameter distribution. Using red laser (633 nm and 1.96 eV), one vibrational frequency peak was found, corresponding to single diameter distribution (Figure3). Table 1 shows the calculated diameters of the synthesized SWCNTs.Table 1
Calculated diameter of the synthesized SWCNTs using (1).
Laser
Vibration frequency
SWCNTs diameter
[cm−1]
[nm]
Green 532 nm (2.33 eV)
162.2
1.49
184.6
1.29
Red 633 nm (1.96 eV)
188.8
1.26Figure 3
RBM band of the Raman spectra for the raw ablation product (a) and the commercial SWCNTs recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)For the commercial product using the green laser, one peak was found (Figure2) corresponding to a single diameter distribution, while using the red laser two peaks were found (Figure 2) corresponding to two diameters distribution, their values being listed in Table 2.Table 2
Calculated diameter of the commercial SWCNTs using (1).
Laser
Vibration frequency
SWCNTs diameter
[cm−1]
[nm]
Green 532 nm (2.33 eV)
158.4
1.53
Red 633 nm (1.96 eV)
143.9
1.71
159.9
1.52The vibrational frequency in the radial direction strongly depends on the diameter of the nanotubes, described by [26](1)d=c1ω-c2,where  ω is frequency of vibrations in the radial direction [cm−1]; c1 and c2 are constants [cm−1]: c1=215 [cm−1] and c2=18 [cm−1]; d is the diameter of the nanotubes [nm].Equation (1) was used to calculate the diameters of the SWCNTs and their values are summarized in Tables 1 and 2.The diameters of individual SWCNTs obtained in the laser ablation have been estimated to be between 1.26 nm and 1.49 nm, while for the commercial SWCNTs they were between 1.52 nm and 1.71 nm. Similar values have been reported by other authors for the SWCNTs obtained by laser ablation of targets with a similar composition [25].


#### 3.1.2. D and G Bands Analysis

In the range of 1300–1600 cm−1 two bands were identified for both products, respectively, D and G bands, which are specific for SWCNTs (Figure 4) and help in the SWCNTs identification. Their values are shown in Tables 3 and 4. D band is characteristic for scattering on sp3 type carbon atoms; therefore, this signal is assigned to the amorphous carbon content in the sample and the defects in the nanotubes structure [27], while G band is due to the presence of sp2 carbon in the nanotubes structure. Hence, the ratio of the integrated intensity of D and G bands, ID/IG, is a measure of the quality of SWCNTs which shows the purity and the defects [28]. This ratio has a very low value for both products indicating the presence of the high quality SWCNTs (Tables 3 and 4), while the laser wavelength has no significant influence on this ratio. G band is divided into two bands G− and G+: the G− is characteristic for vibrations in the circumferential direction and G+ is characteristic for vibrations along the nanotubes axis. Their ratio IG-/IG+ gives information about the conducting character of the SWCNTs [29]. Using the 532 nm laser, for our ablation product and for the commercial one, this ratio is lower than 1 indicating the presence of semiconducting type, while when the 633 nm laser was used this ratio became higher than 1 indicating the presence of metallic type (Tables 3 and 4).Table 3
Raman shift,ID/IG and IG-/IG+ values for the ablation product.
Laser
D band
G band[cm−1]
I
D
/
I
G
I
G
-
/
I
G
+
[cm−1]
G−
G+
Green 532 nm (2.33 eV)
1334
1559
1581
0.004
0.43
Red 633 nm (1.96 eV)
1316
1526
1579
0.004
2.11Table 4
Raman shift,ID/IG and IG-/IG+ values for the commercial SWCNTs.
Laser
D band
G band [cm−1]
I
D
/
I
G
I
G
-
/
I
G
+
[cm−1]
G−
G+
Green 532 nm (2.33 eV)
1321
1552
1577
0.008
0.29
Red 633 nm (1.96 eV)
1312
1551
1579
0.004
1.23Figure 4
D and G bands of the Raman spectra of the raw ablation product (a) and the commercial SWCNTs (b) recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)


#### 3.1.3. Kataura Plot Analysis

Kataura plot is a graph correlating the band gaps energy of the carbon nanotubes with their diameters [30]. A carbon nanotube can be metallic or semiconducting depending on its diameter. Rao et al. have shown that the Raman spectrum at a given wavelength is strongly influenced by the resonance Raman effect [31]. Raman scattering in SWCNTs is resonant, only when the band gap of the nanotubes is equal to the exciting laser energy [32, 33]. However, this resonance effect in nanotubes is influenced by the conducting character; thus, we can identify the conducting character of the SWCNTs obtained during ablation by performing an interpolation in the Kataura plot of the estimated diameters with the laser excitation energies for our product and for the commercial one.According to Kataura plot the commercial product contains semiconducting SWCNTs, while our ablation product indicates the presence of both types: semiconducting and metallic SWCNTs (Figure5). By modifying the diameter of the SWCNTs we could move from a zone of semiconducting nanotubes to a zone of metallic ones; therefore, the conducting character of the SWCNTs could be changed.Figure 5
Kataura plot with black points indicating semiconductor nanotubes and red circles indicating metallic nanotubes. The horizontal green line indicates the excitation energy of the green laser (2.33 eV), while the red line indicates the excitation energy of the red laser (1.96 eV). The vertical green lines indicate the diameter distribution of the nanotubes of our ablation product obtained with the green laser and the red line with the red laser (a) and the commercial nanotubes from Sigma obtained with the green laser and the red line with the red laser (b) [33].
(a)
(b)


### 3.2. Scanning Electron Microscopy and Transmission Electron Microscopy Analysis

The SEM image of the raw product soot (Figure6) shows the presence of the SWCNTs bundles surrounded by the metal catalyst and amorphous carbon particles. For TEM imaging, the raw ablation product was dispersed in dimethylformamide (DMF) (Sigma-Aldrich), using an ultrasonic bath for 8 hours to get good dispersion. The TEM images were obtained with Philips-EM 410 TEM instrument (Figure 7) showing that the SWCNTs in the raw ablation product were grouped in micrometer-long bundles of different diameters, along the metal catalysts particles, graphite, and amorphous carbon, also present in the product.Figure 6
Scanning electron microscopy (SEM) image of the raw product synthesized by a KrF excimer laser ablation of the target.Figure 7
Transmission electron microscopy (TEM) images of the ablation product.The SEM and TEM micrographs support the Raman analysis data confirming the presence of the SWCNTs and low content of amorphous carbon.


### 3.3. Thermogravimetric Analysis

The thermogravimetric analysis (TGA) of the ablation product was carried out in synthetic air with a temperature rate of 5°C/min using an STA-8000 Perkin Elmer instrument (Figure8). TGA curves were recorded for the ablation product and ablated and nonablated sides of the target (Figure 8(a, b, and c)). The TGA curve of the ablation product shows a burning slope centered around 400°C, while nonablated target shows a slope centered around 700°C proving that a new product was formed during the laser ablation. The same residual mass resulted from the ablation product as for the ablated side of the target (17.6%), showing that the product preserves the same stoechiometry of the metal catalyst as the target from where it comes from. Also the residual mass of the ablated side of the target is higher than that of the nonablated side, showing that during ablation an increase of the metal content at the surface of the target has occurred.Figure 8
TGA curve recorded in air: (a) the ablation product, (b) ablated side of the target, and (c) nonablated target, respectively.The TGA curve in Figure8(a) indicates that most of the weight loss occurred in the temperature range of 350–450°C, where the SWCNTs burning took place. The 70% weight loss indicates a 70% SWCNTs production yield. Also multiple products are present in the ablation product like fullerenes (7-8%) which burn between 500 and 600°C, followed by the metal catalyst particles. TGA analysis confirms the presence of very low amount of amorphous carbon, fact revealed by the other analysis methods, Raman and TEM.


## 3.1. Raman Spectroscopy Analysis

To identify the SWCNTs, the ablation product was analyzed by confocal Raman microspectroscopy using a Horiba Labram 800 instrument equipped with two laser wavelengths: 532 nm and 633 nm. The Raman spectra were recorded using both excitation wavelengths. The spectrum of the ablation product was compared with the commercial SWCNTs from Sigma as shown in Figure2. The Raman spectra present three main regions specific to SWCNTs: radial breathing mode (RBM) and D and G bands which are further analyzed.Figure 2
Raman spectra of the raw ablation product (a) and the commercial SWCNTs (b) recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)


### 3.1.1. RBM Band Analysis

For the raw ablation product using the green laser (532 nm and 2.33 eV), two vibrational frequency peaks were found in the RBM band of the Raman spectra, each peak corresponding to a diameter distribution. Using red laser (633 nm and 1.96 eV), one vibrational frequency peak was found, corresponding to single diameter distribution (Figure3). Table 1 shows the calculated diameters of the synthesized SWCNTs.Table 1
Calculated diameter of the synthesized SWCNTs using (1).
Laser
Vibration frequency
SWCNTs diameter
[cm−1]
[nm]
Green 532 nm (2.33 eV)
162.2
1.49
184.6
1.29
Red 633 nm (1.96 eV)
188.8
1.26Figure 3
RBM band of the Raman spectra for the raw ablation product (a) and the commercial SWCNTs recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)For the commercial product using the green laser, one peak was found (Figure2) corresponding to a single diameter distribution, while using the red laser two peaks were found (Figure 2) corresponding to two diameters distribution, their values being listed in Table 2.Table 2
Calculated diameter of the commercial SWCNTs using (1).
Laser
Vibration frequency
SWCNTs diameter
[cm−1]
[nm]
Green 532 nm (2.33 eV)
158.4
1.53
Red 633 nm (1.96 eV)
143.9
1.71
159.9
1.52The vibrational frequency in the radial direction strongly depends on the diameter of the nanotubes, described by [26](1)d=c1ω-c2,where  ω is frequency of vibrations in the radial direction [cm−1]; c1 and c2 are constants [cm−1]: c1=215 [cm−1] and c2=18 [cm−1]; d is the diameter of the nanotubes [nm].Equation (1) was used to calculate the diameters of the SWCNTs and their values are summarized in Tables 1 and 2.The diameters of individual SWCNTs obtained in the laser ablation have been estimated to be between 1.26 nm and 1.49 nm, while for the commercial SWCNTs they were between 1.52 nm and 1.71 nm. Similar values have been reported by other authors for the SWCNTs obtained by laser ablation of targets with a similar composition [25].


### 3.1.2. D and G Bands Analysis

In the range of 1300–1600 cm−1 two bands were identified for both products, respectively, D and G bands, which are specific for SWCNTs (Figure 4) and help in the SWCNTs identification. Their values are shown in Tables 3 and 4. D band is characteristic for scattering on sp3 type carbon atoms; therefore, this signal is assigned to the amorphous carbon content in the sample and the defects in the nanotubes structure [27], while G band is due to the presence of sp2 carbon in the nanotubes structure. Hence, the ratio of the integrated intensity of D and G bands, ID/IG, is a measure of the quality of SWCNTs which shows the purity and the defects [28]. This ratio has a very low value for both products indicating the presence of the high quality SWCNTs (Tables 3 and 4), while the laser wavelength has no significant influence on this ratio. G band is divided into two bands G− and G+: the G− is characteristic for vibrations in the circumferential direction and G+ is characteristic for vibrations along the nanotubes axis. Their ratio IG-/IG+ gives information about the conducting character of the SWCNTs [29]. Using the 532 nm laser, for our ablation product and for the commercial one, this ratio is lower than 1 indicating the presence of semiconducting type, while when the 633 nm laser was used this ratio became higher than 1 indicating the presence of metallic type (Tables 3 and 4).Table 3
Raman shift,ID/IG and IG-/IG+ values for the ablation product.
Laser
D band
G band[cm−1]
I
D
/
I
G
I
G
-
/
I
G
+
[cm−1]
G−
G+
Green 532 nm (2.33 eV)
1334
1559
1581
0.004
0.43
Red 633 nm (1.96 eV)
1316
1526
1579
0.004
2.11Table 4
Raman shift,ID/IG and IG-/IG+ values for the commercial SWCNTs.
Laser
D band
G band [cm−1]
I
D
/
I
G
I
G
-
/
I
G
+
[cm−1]
G−
G+
Green 532 nm (2.33 eV)
1321
1552
1577
0.008
0.29
Red 633 nm (1.96 eV)
1312
1551
1579
0.004
1.23Figure 4
D and G bands of the Raman spectra of the raw ablation product (a) and the commercial SWCNTs (b) recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)


### 3.1.3. Kataura Plot Analysis

Kataura plot is a graph correlating the band gaps energy of the carbon nanotubes with their diameters [30]. A carbon nanotube can be metallic or semiconducting depending on its diameter. Rao et al. have shown that the Raman spectrum at a given wavelength is strongly influenced by the resonance Raman effect [31]. Raman scattering in SWCNTs is resonant, only when the band gap of the nanotubes is equal to the exciting laser energy [32, 33]. However, this resonance effect in nanotubes is influenced by the conducting character; thus, we can identify the conducting character of the SWCNTs obtained during ablation by performing an interpolation in the Kataura plot of the estimated diameters with the laser excitation energies for our product and for the commercial one.According to Kataura plot the commercial product contains semiconducting SWCNTs, while our ablation product indicates the presence of both types: semiconducting and metallic SWCNTs (Figure5). By modifying the diameter of the SWCNTs we could move from a zone of semiconducting nanotubes to a zone of metallic ones; therefore, the conducting character of the SWCNTs could be changed.Figure 5
Kataura plot with black points indicating semiconductor nanotubes and red circles indicating metallic nanotubes. The horizontal green line indicates the excitation energy of the green laser (2.33 eV), while the red line indicates the excitation energy of the red laser (1.96 eV). The vertical green lines indicate the diameter distribution of the nanotubes of our ablation product obtained with the green laser and the red line with the red laser (a) and the commercial nanotubes from Sigma obtained with the green laser and the red line with the red laser (b) [33].
(a)
(b)


## 3.1.1. RBM Band Analysis

For the raw ablation product using the green laser (532 nm and 2.33 eV), two vibrational frequency peaks were found in the RBM band of the Raman spectra, each peak corresponding to a diameter distribution. Using red laser (633 nm and 1.96 eV), one vibrational frequency peak was found, corresponding to single diameter distribution (Figure3). Table 1 shows the calculated diameters of the synthesized SWCNTs.Table 1
Calculated diameter of the synthesized SWCNTs using (1).
Laser
Vibration frequency
SWCNTs diameter
[cm−1]
[nm]
Green 532 nm (2.33 eV)
162.2
1.49
184.6
1.29
Red 633 nm (1.96 eV)
188.8
1.26Figure 3
RBM band of the Raman spectra for the raw ablation product (a) and the commercial SWCNTs recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)For the commercial product using the green laser, one peak was found (Figure2) corresponding to a single diameter distribution, while using the red laser two peaks were found (Figure 2) corresponding to two diameters distribution, their values being listed in Table 2.Table 2
Calculated diameter of the commercial SWCNTs using (1).
Laser
Vibration frequency
SWCNTs diameter
[cm−1]
[nm]
Green 532 nm (2.33 eV)
158.4
1.53
Red 633 nm (1.96 eV)
143.9
1.71
159.9
1.52The vibrational frequency in the radial direction strongly depends on the diameter of the nanotubes, described by [26](1)d=c1ω-c2,where  ω is frequency of vibrations in the radial direction [cm−1]; c1 and c2 are constants [cm−1]: c1=215 [cm−1] and c2=18 [cm−1]; d is the diameter of the nanotubes [nm].Equation (1) was used to calculate the diameters of the SWCNTs and their values are summarized in Tables 1 and 2.The diameters of individual SWCNTs obtained in the laser ablation have been estimated to be between 1.26 nm and 1.49 nm, while for the commercial SWCNTs they were between 1.52 nm and 1.71 nm. Similar values have been reported by other authors for the SWCNTs obtained by laser ablation of targets with a similar composition [25].


## 3.1.2. D and G Bands Analysis

In the range of 1300–1600 cm−1 two bands were identified for both products, respectively, D and G bands, which are specific for SWCNTs (Figure 4) and help in the SWCNTs identification. Their values are shown in Tables 3 and 4. D band is characteristic for scattering on sp3 type carbon atoms; therefore, this signal is assigned to the amorphous carbon content in the sample and the defects in the nanotubes structure [27], while G band is due to the presence of sp2 carbon in the nanotubes structure. Hence, the ratio of the integrated intensity of D and G bands, ID/IG, is a measure of the quality of SWCNTs which shows the purity and the defects [28]. This ratio has a very low value for both products indicating the presence of the high quality SWCNTs (Tables 3 and 4), while the laser wavelength has no significant influence on this ratio. G band is divided into two bands G− and G+: the G− is characteristic for vibrations in the circumferential direction and G+ is characteristic for vibrations along the nanotubes axis. Their ratio IG-/IG+ gives information about the conducting character of the SWCNTs [29]. Using the 532 nm laser, for our ablation product and for the commercial one, this ratio is lower than 1 indicating the presence of semiconducting type, while when the 633 nm laser was used this ratio became higher than 1 indicating the presence of metallic type (Tables 3 and 4).Table 3
Raman shift,ID/IG and IG-/IG+ values for the ablation product.
Laser
D band
G band[cm−1]
I
D
/
I
G
I
G
-
/
I
G
+
[cm−1]
G−
G+
Green 532 nm (2.33 eV)
1334
1559
1581
0.004
0.43
Red 633 nm (1.96 eV)
1316
1526
1579
0.004
2.11Table 4
Raman shift,ID/IG and IG-/IG+ values for the commercial SWCNTs.
Laser
D band
G band [cm−1]
I
D
/
I
G
I
G
-
/
I
G
+
[cm−1]
G−
G+
Green 532 nm (2.33 eV)
1321
1552
1577
0.008
0.29
Red 633 nm (1.96 eV)
1312
1551
1579
0.004
1.23Figure 4
D and G bands of the Raman spectra of the raw ablation product (a) and the commercial SWCNTs (b) recorded with green laser (532 nm, top spectrum) and red laser (633 nm, bottom spectrum).
(a)
(b)


## 3.1.3. Kataura Plot Analysis

Kataura plot is a graph correlating the band gaps energy of the carbon nanotubes with their diameters [30]. A carbon nanotube can be metallic or semiconducting depending on its diameter. Rao et al. have shown that the Raman spectrum at a given wavelength is strongly influenced by the resonance Raman effect [31]. Raman scattering in SWCNTs is resonant, only when the band gap of the nanotubes is equal to the exciting laser energy [32, 33]. However, this resonance effect in nanotubes is influenced by the conducting character; thus, we can identify the conducting character of the SWCNTs obtained during ablation by performing an interpolation in the Kataura plot of the estimated diameters with the laser excitation energies for our product and for the commercial one.According to Kataura plot the commercial product contains semiconducting SWCNTs, while our ablation product indicates the presence of both types: semiconducting and metallic SWCNTs (Figure5). By modifying the diameter of the SWCNTs we could move from a zone of semiconducting nanotubes to a zone of metallic ones; therefore, the conducting character of the SWCNTs could be changed.Figure 5
Kataura plot with black points indicating semiconductor nanotubes and red circles indicating metallic nanotubes. The horizontal green line indicates the excitation energy of the green laser (2.33 eV), while the red line indicates the excitation energy of the red laser (1.96 eV). The vertical green lines indicate the diameter distribution of the nanotubes of our ablation product obtained with the green laser and the red line with the red laser (a) and the commercial nanotubes from Sigma obtained with the green laser and the red line with the red laser (b) [33].
(a)
(b)


## 3.2. Scanning Electron Microscopy and Transmission Electron Microscopy Analysis

The SEM image of the raw product soot (Figure6) shows the presence of the SWCNTs bundles surrounded by the metal catalyst and amorphous carbon particles. For TEM imaging, the raw ablation product was dispersed in dimethylformamide (DMF) (Sigma-Aldrich), using an ultrasonic bath for 8 hours to get good dispersion. The TEM images were obtained with Philips-EM 410 TEM instrument (Figure 7) showing that the SWCNTs in the raw ablation product were grouped in micrometer-long bundles of different diameters, along the metal catalysts particles, graphite, and amorphous carbon, also present in the product.Figure 6
Scanning electron microscopy (SEM) image of the raw product synthesized by a KrF excimer laser ablation of the target.Figure 7
Transmission electron microscopy (TEM) images of the ablation product.The SEM and TEM micrographs support the Raman analysis data confirming the presence of the SWCNTs and low content of amorphous carbon.


## 3.3. Thermogravimetric Analysis

The thermogravimetric analysis (TGA) of the ablation product was carried out in synthetic air with a temperature rate of 5°C/min using an STA-8000 Perkin Elmer instrument (Figure8). TGA curves were recorded for the ablation product and ablated and nonablated sides of the target (Figure 8(a, b, and c)). The TGA curve of the ablation product shows a burning slope centered around 400°C, while nonablated target shows a slope centered around 700°C proving that a new product was formed during the laser ablation. The same residual mass resulted from the ablation product as for the ablated side of the target (17.6%), showing that the product preserves the same stoechiometry of the metal catalyst as the target from where it comes from. Also the residual mass of the ablated side of the target is higher than that of the nonablated side, showing that during ablation an increase of the metal content at the surface of the target has occurred.Figure 8
TGA curve recorded in air: (a) the ablation product, (b) ablated side of the target, and (c) nonablated target, respectively.The TGA curve in Figure8(a) indicates that most of the weight loss occurred in the temperature range of 350–450°C, where the SWCNTs burning took place. The 70% weight loss indicates a 70% SWCNTs production yield. Also multiple products are present in the ablation product like fullerenes (7-8%) which burn between 500 and 600°C, followed by the metal catalyst particles. TGA analysis confirms the presence of very low amount of amorphous carbon, fact revealed by the other analysis methods, Raman and TEM.


## 4. Conclusion

In the present work we have shown the production of high quality SWCNTs using krypton atmosphere by KrF excimer laser ablation. The SWCNTs were obtained with a high yield of 70%. The obtained SWCNTs are a mixture of semiconducting and metallic types; also they are micrometers long with diameters distribution of 1.26 and 1.49 nm. The ablation product preserves the same stoechiometry of metal catalyst as the target from where it comes. The quality of our product is comparable with the top quality of commercial SWCNTs. The quality of the produced SWCNTs by this method was confirmed by Raman, TGA, and TEM analysis showing very low content of amorphous carbon and defects in the structure of the nanotubes. Also TGA curve indicated low content of amorphous carbon and fullerenes.



---