# Fabrication and Characterization of Nickel Chloride Doped PMMA Films

Authors: Wasan A. Al-Taa’y; Saad F. Oboudi; Emad Yousif; Mohammed Abdul Nabi; Rahimi M. Yusop; Darfizzi Derawi
Journal: Advances in Materials Science and Engineering
 (2015)

---

## Abstract

Films of PMMA and PMMA doped with NiCl2 with different contents were prepared using the casting technique. The optical properties of all films were investigated using spectrophotometric measurements of absorbance and transmittance in the wavelength range 200–800 nm. The change of the calculated values of the optical energy gaps with increasing NiCl2 content has been interpreted in terms of the structural modifications of the PMMA matrix. The optical energy gap decreased from 3.6 to 3.05 eV with increasing the NiCl2 concentration to 0.4%. The effect of doping on the optical constants of films such as refractive index, extinction coefficient, real and imaginary parts of dielectric constant, optical conductivity, and skin depth has been reported. All these constants were increased with increasing NiCl2 concentration with the exception of skin depth which is different result.


---

## Body

## 1. Introduction

Optical properties of polymer films are very important for many technological applications [1], ranging from protective coatings to paintings, microelectronic, semiconductors, and optoelectronic devices depending on the reflectance and transmittance properties of the films during their preparation [2, 3]. PMMA as a polymeric waveguide has attracted much attention for use as optical components and in optoelectronics devices due to their low cost and volume productivity. Recently, some researchers reported optical components such as an optical switch, a coupler, a splitter, and a transceiver [4, 5].PMMA is considered as an excellent host material for doping due to their good transparency (the transmission for visible light is very high), resistivity, mechanical strength, and optical homogeneity which can play an important role in building up advanced optical materials [6]. It is one of the earliest and best known polymers. PMMA was seen as a replacement for glass in a variety of applications and is currently used extensively in glazing applications. The material is one of the hardest polymers and is rigid, glass-clear with glossy finish and good weather resistance [7].Owing to the influence of doping on the properties of polymeric materials, the controlled preparation of PMMA of different doping materials and concentrations is always the researcher’s purpose; these doping processes cause a remarkable change in their properties [8, 9]. The present work is a part of a systematic study of the effect of doping of NiCl2 on PMMA on improving their physical properties. Therefore, we study the effect of the doping level (W) using both the optical absorption measurements and the determination of the optical constants and energy gap. The accurate determination of the optical constants of these materials is important, in order not only to know the basic mechanisms underlying these phenomena but also to exploit and develop their interesting technological applications.


## 2. Experimental Details

Films of poly(methyl methacrylate) PMMA doped with different weight concentration of nickel chloride (NiCl2) salt (0.1, 0.2, 0.3, and 0.4%) have been prepared by the dispersed polymer and NiCl2 dissolve in 100 mL chloroform with stirring the solution, using a magnetic stirrer for about 30 min at room temperature for complete dissolving. Different polymer solutions (volumetric solutions) were casted as a layer, dried at room temperature for 24 hours. Layer thickness was measured using indicating micrometer 0.25 μm; all layers were found to be in the range of 20 ± 1 μm; these layers were clear, transparent, and free from any noticeable defect showing light bluish color.Optical transmittance and absorbance were recorded in the wavelength range of 200–800 nm using computerized UV-VIS spectrophotometer (Shimadzu UV-1601 PC). Optical transmittance and absorbance were reported in order to study the effect of doping on the parameters under investigation.


## 3. Results and Discussion

The optical properties of films by means of optical absorption in the UV-VIS region of 200–800 nm have been investigated. Figure1 shows the dependence of absorbance (A) on wavelength (λ) of all films before and after being doped by NiCl2 salt with different concentrations (0.1, 0.2, 0.3, and 0.4%). It is observed that in the visible region all films have very low transparent; then absorbance is rapidly decreased with increasing wavelength. This behavior may be attributed to perfection and stoichiometry of the films. Also it can be observed from the figure that the absorbance increased with increasing the doping concentration of NiCl2 to 0.4%; this result agrees with the previous work [10]. It has been observed that the absorption peaks appear at wavelengths 240, 242, 248, 249, and 251 nm as the concentration of dopant varies from 0 to 0.4 mol/L in PMMA matrix, respectively. The shifting occurring in the spectra may be due to the polarity of solvent used in the synthesis or may be due to the dispersion of rare earth oxide particles in the PMMA matrix [11].Figure 1
The variation of absorbance with wavelength for pure and doped PMMA films.From the transmittance(T) data and according to Tauc [12] relation, the most satisfactory representation is obtained by plotting the quantity αhυ2 as a function of (hυ). The plot of αhυ2 versus hυ for different dopant percentage in polymer samples is shown in Figure 2. The observed behavior suggests allowed direct transition for amorphous material [13]. The values of optical energy gap Eopt obtained from the extrapolation of the linear region are found to be decrease for all samples 3.6, 3.5, 3.29, 3.19, and 3.05 eV with increasing the doping percentage of NiCl2 0.1, 0.2, 0.3, and 0.4%, respectively. The decrease in Eopt with increasing NiCl2 concentration can be understood by considering the mobility gap variation in the doped polymer [14]. The figure shows a linear dependence for pure PMMA in one region representing one optical absorption edge as mentioned before in previous work [9, 15–17]. The value obtained in this work is close to others previously reported for the allowed direct transition.Figure 2
Theαhυ2 versus photon energy for pure and doped PMMA films.The refractive index(n) is an important parameter for optical materials and applications. Thus, it is important to determine optical constants of the films. The refractive index of the films was determined from the following relation [18]:
(1)n=1+R1-R+4R1-R2-K2,
where R represent the reflectance and k is the extinction coefficient (k=αλ/4π) where α is the absorption coefficient. The n and k values of dependence of wavelength are shown in Figures 3 and 4, respectively, for all samples before and after being doped. As seen in these figures, the n and k values increase with increasing the doping concentration of NiCl2; this result agrees with the previous work [19]. Such behavior corresponds to the density of absorbing centers such as impurities absorption, excitation transition, and other defects in the crystal lattice dependent on the conditions of sample preparation.Figure 3
The variation of refractive index with wavelength for pure and doped PMMA films.Figure 4
The extinction coefficient versus wavelength for pure and doped PMMA films.The dielectric constant is defined asε(ω)=ε1(ω)+iε2(ω); real (ε1) and imaginary (ε2) parts of the dielectric constant are related to the n and k values. The ε1 and ε2 values were calculated using the following formulas [20]
(2)ε1=n2-k2,ε2=2nk.Theε1 and ε2 values of dependence of wavelength are, respectively, shown in Figures 5 and 6 for pure and doped films. The ε1 values are higher than ε2 values. It is seen that the ε1 and ε2 values increase with increasing wavelength and with the doping concentration of NiCl2. The values of dielectric constant at 400 nm for 0, 0.1, 0.2, 0.3, and 0.4% NiCl2 content were 1.75, 3.08, 3.71, 4.45, and 4.60, respectively, for real part and 0.000035, 0.000123, 0.000177, 0.000285, and 0.000342, respectively, for imaginary part. Moreover, this increase by the variation of ε1  mainly depends on n2 because of small values of k2 while ε2 mainly depends on k value which is related to the variation of absorption coefficients [21].Figure 5
The variation of real part of dielectric constant with wavelength for pure and doped PMMA films.Figure 6
The variation of imaginary part of dielectric constant with wavelength for pure and doped PMMA films.The optical conductivity (σ) was calculated using the following relation [22]:
(3)σ=αnc4π,
where c is the velocity of light.Figure7 shows the variation of optical conductivity with the wavelength. It was observed that the optical conductivity increases as the doping percentage of NiCl2 in the PMMA increases to 0.4%. It can be noticed from the figure that the optical conductivity for all films increased in the low wavelengths region and decreased in the high wavelength region; this decrease is due to the low absorbance of the films in that region.Figure 7
The optical conductivity versus wavelength for pure and doped PMMA films.The skin depth(x) could be calculated using the following relation [23]:
(4)x=λ2πk.Figure8 shows the variation of skin depth as a function of wavelength for all films. It is clear from the figure that the skin depth increases as the wavelength increases; this behavior could be seen for all samples, but the skin depth decreases as the doping concentration increases, so the skin depth is a transmittance related.Figure 8
The skin depth versus wavelength for pure and doped PMMA films.


## 4. Conclusion

PMMA and NiCl2 doped PMMA films were prepared by using casting technique. Both pure and doped samples were characterized. Results indicate that the optical band gap and the optical parameters are strongly dependent on doping with NiCl2. The optical band gap decreased from 3.6 to 3.05 eV with increasing the doping concentration to 0.4%. The refractive index, extinction coefficient, the real and imaginary parts of dielectric constant, and the optical conductivity were calculated and they are tending to increase with increasing the doping concentration of NiCl2; on the other hand, the skin depth decreases with increasing the doping concentration. These present observations can help improve the understanding of the optical parameters of NiCl2 films.



---

*Source: 913260-2015-01-01.xml*