# Inverse Slip Accompanying Twinning and Detwinning during Cyclic Loading of Magnesium Single Crystal

Authors: Qin Yu; Jian Wang; Yanyao Jiang
Journal: Journal of Materials
 (2013)

---

## Abstract

In situ, observation of twinning and detwinning in magnesium single crystals during tension-compression cyclic loading was made using optical microscopy. A quantitative analysis of plastic strain indicates that twinning and detwinning experience two stages, low and high work hardening de-twinning, and pure re-twinning and fresh twinning combined with retwinning. Slip is always activated. For the first time, inverse slip accompanying with pure retwinning and high work hardening detwinning was experimentally identified, which provides insights in better understanding of the activity of twining, detwinning, and slips.


---

## Body

## 1. Introduction

Plastic deformation in materials with hexagonal-close-packed (HCP) structure is accommodated by both slip and twinning (or detwinning) [1, 2]. For magnesium (Mg) alloys, twinning is mainly related to the extension twin  {101-2}〈101-1〉 with six variants that can be activated by an equivalent tension along the c-axis. Due to its polar nature, detwinning leads to the reorientation of the basal pole from the twin back to the matrix [1–4]. Under cyclic loading and strain path changes, twinning and detwinning appear alternately [5–9]. Experimental studies have been focusing on the role of twinning and detwinning in cyclic deformation and fatigue [5–9]. In addition to twinning, slips are necessary to accommodate arbitrary plastic deformation. However, the activity of twinning and slip is different in terms of nucleation and glide (or growth). For instance, nucleation of lattice glide dislocations is relatively easier than twins, but the mobility of a {101-2}  twinning dislocation is greater than that of a lattice dislocation [10–14]. As a consequence, the plastic deformation in the twinned crystal resulted from twinning shear can be greater than that in the matrix resulted from dislocation slip. The incompatibility of plastic deformation between the twin and the matrix can generate a change in the stress state in the matrix surrounding the growing twin.  To be specific, the shear stress in the matrix near the growing twin can have an opposite sign to the shear stress in the matrix far away from the twin.  The opposite signed stress surrounding the twin is often referred to as “backstress.”  The growth of twin can be slowed down and even stopped if the local backstress keeps increasing.  To sustain the growth of twin, the magnitude of the backstress must be reduced or the direction of the backstress should reorient to align with that of the external load.  Such changes can be achieved through either increasing the external load or initiating slips in the direction opposite to the twinning shear (or the external load).  Note that at any moment, the total plastic strain rate (ε˙P(ij)Exp) with respect to time is equal to the summation of the twinning-induced plastic strain rate (ε˙P(ij)Tw) and the slip-induced plastic strain rate (ε˙P(ij)S); that is, ε˙P(ij)Exp=ε˙P(ij)Tw+ε˙P(ij)S, where the subscripts i and j denote the coordinates. If a slip flows in the direction opposite to that of the twinning shear, we define such a slip as “inverse slip.”  To validate the existence of inverse slips, it is essential to experimentally and quantitatively separate the plastic deformation contributed by twinning/detwinning and slips.In the current study, a tension-compression cyclic loading experiment of a[0001]-orientated Mg single crystal was conducted at room temperature. In situ, optical microscopy was employed to directly observe the evolution of twins. Optical microscopy (OM) was chosen for the study due to the large observation area and high frame rate [5]. A large observation area is extremely crucial for the determination of macrostrain that is equal to the strain measured by using an extensometer in the tension-compression experiment of a single crystal. In addition, twins are generally larger than micrometers in size and grow very fast. Therefore, an optical microscope equipped with a fast digital camera can properly capture the twin growth. To this end, in situ high/low resolution transmission electron microscopy (TEM) or scanning electron microscope or electron backscatter diffraction is not suitable to study the cyclic tension-compression deformation due to the geometry limit of the testing samples and due to the small observation region and the low frame rate [15–19]. For example, the buckling could occur for a TEM sample that is subjected to a cyclic loading with a total strain magnitude of 0.5%.


## 2. Material, Experiment, and Analysis Method

Mg single crystal was grown by the Bridgman method [20].  Small plate dog-bone testing specimen is cut by chemical corrosion technique [5] and has a gage length of 5.0 mm and a square cross-section of 3.0 mm by 3.0 mm. The loading direction was aligned with the c-axis. The specimen surface, that is, the (101-0) prismatic plane, was carefully polished down to 1 μm using polycrystalline diamond suspension, followed by chemical polishing using a solution of 1 part of nitric acid, 2 parts of hydrochloric acid, and 7 parts of ethanol as described in [21]. The well-prepared specimen was characterized using OM, and no mechanical twins were detected before the testing. A servohydraulic load frame with a load capacity of ±25 kN was employed to perform the cyclic loading experiment. A grip system was specially designed to ensure the accurate alignment of the loading axis with the testing specimen.  A strain-gaged extensometer with a range of ±9.15% was attached to the specimen to directly measure the engineering strain within the gage length of the testing sample.  The load was measured by the load cell and recorded by a computer.  A long-distance optical microscope was employed to trace the twins in the middle of the specimen observation surface during testing.  The image frame covers an area of  1.4mm×1.0mm  on the specimen surface with a resolution of approximate 1 μm per pixel. The video recording rate was 42 frames per minute. Fully reversed strain-controlled tension-compression was applied at a total strain amplitude of 0.5% at a frequency of 0.01 Hz in ambient air.The plastic strain,εp(t), is determined by subtracting the elastic strain, εe(t), from the total applied strain εExp(t). The elastic strain εe(t) is calculated using the Hooke’s Law employing a constant Young’s modulus of 44.7 GPa. The plastic strain consists of two parts: twinning-induced and slip-induced plastic strains. The twinning-induced plastic strain,  εpTw(t), is determined according to the measured twin volume fraction that is identified in optical micrographs through an image analysis. With the given crystallography and the observation direction under investigation, there are six  {101-2}  extension twin variants that could be equally activated due to identical Schmid factors of the variants (Figure 1(a)). For each twin variant, the twin volume fraction is calculated from the twin area fraction by multiplying a geometrical factor βi (i = 1, 2, 3, …, 6, denoting the six variants) that accounts for the true twin thickness.  β  is equal to 0.73 for two variants and 0.94 for the other four variants. Due to a technique difficulty to numerically distinguish the type of twin variants, an average geometry factor  β-=(1/6)∑i=16βi  was adopted in this study (to avoid an overestimation of the contribution to the plastic deformation by twins, we also performed an analysis by using a low geometry factor of 0.73, in Figure S1. The results from both low and averaged geometry factors are similar). The total twin area fraction  A  is equal to the ratio of the total number of dark contrasted pixels (representing twins) over the total number of pixels within the observed region. The plastic strain accommodated by twinning/detwinning is calculated according to the volume average plastic strain [22],  εp(ij)Tw=(γtwβ-A/2)(m⊗n+n⊗m), where εp(ij)Tw is the plastic strain accommodated by twinning, γtw is the twinning shear defined as  3/(c/a)-(c/a)/3, which is equal to 0.129 as  c/a =1.624 for Mg, and m and n are the normal vectors of the twin plane and the twinning direction corresponding to the specimen’s coordinates, respectively. Slip-induced strain is the difference between the measured plastic strain and the twinning-induced plastic strain, that is,  εp(ij)S=εp(ij)Exp-εp(ij)Tw. The subscripts i and j represent the specimen coordinates x, y, and z. Since the experiment was conducted with the controlled strain along the z-axis (see Figure 1), only the strain components in the z direction (εp(zz)Exp,  εp(zz)Tw,  and  εp(zz)S) are analyzed and discussed. A parabolic curve is used to fit a successive set of five data points in the experimentally obtained relationship between the plastic strain (εp(zz)Exp, εp(zz)Tw, or εp(zz)S) and the time.  The first-order derivative of the obtained fitting curve at the middle point in the successive five-point data set is reported as the plastic strain rates (ε˙p(zz)Exp, ε˙p(zz)Tw, and ε˙p(zz)S).(a) Schematics showing six{101-2}  twin variants and their projections on the (101-0) prismatic plane.In situ optical micrographs showing twins at the tensile peak strain ((b)  and (c)) and compressive peak strain ((d) and (e)) at the first loading cycle and the tenth loading cycle.
(a)
(b)
(c)
(d)
(e)With the increasing number of loading cycles after the tenth loading cycle, residual twins are found to accumulate significantly.  Large amounts of crossing-like twin-twin junctions are developed severely at local areas, for example, as shown in the optical micrographs at the tensile peak strain and compressive peak strain in the 40th, 400th, and 1610th loading cycle in Figure2.  To ensure the reliability of the analysis, we only report the plastic strains (total, twinning induced, and slip induced) during the first ten loading cycles, where much fewer crossing-like twin-twin junctions were observed (see Figure 1 and Supplementary Material MOVIE available online at http://dx.doi.org/10.1155/2013/903786).Figure 2
Variation of twin volume fraction with respect to the loading cycles together with the optical micrographs showing twins at tensile and compressive peak strains in the 40th, 400th, and 1610th loading cycle.


## 3. Results and Discussion

Figure3(a) illustrates a typical stress-plastic strain hysteresis loop for the ith loading cycle with four featured segments divided by critical points from Ai, Bi, Ci, Di, Ei, and  Ai+1. These four featured segments are related to slips and three distinctive twinning mechanisms: fresh twinning, detwinning, and retwinning. Fresh twinning refers to the nucleation and propagation of new twins from the virgin, material and retwinning corresponds to the repeated growth of a residual twin that is not fully detwinned [5].  Ai  and  Ci  are defined as points at the tensile and compressive peak strain, respectively. Stage from  Ai  and  Ci  refers to the unloading including the tensile unloading and the compressive reloading. We introduced a critical point  Bi, from  Ai to  Bi, and plastic deformation is mainly accommodated by the easy detwinning (corresponding to a low work hardening). From  Bi  to  Ci, detwinning and slips both accommodate plastic deformation, causing a high work hardening. Due to the dislocation-twin interaction, detwinning becomes difficult, thus referred to as the high work hardening detwinning. The critical point Bi is defined as the point where the plastic strain rate induced by slip inverses its sign from negative to positive in Figure 3(c). The critical point  Di is defined as the end of the elastic segment following the compressive strain peak  Ci  in Figure 3(d), during which no plastic flow exists.  Similar to the case of  Bi, the transition point  Ei  from pure retwinning to re- and fresh-twinning is defined as the point at which the slip-induced plastic strain rate inverses its sign from negative to positive in Figure 3(c).Figure 3
Stress-plastic strain hysteresis loop with critical points (Ai  to  Ai+1) for the ith loading cycle (a) and variation of plastic strain rates (b) with the focused areas near critical point  Bi (c), Di  (d), and  Ei  (e).Figure4(a) presents the stress-plastic strain hysteresis loops for the first and second loading cycles.  Six snapshots from in situ optical micrographs show morphology change of twins at critical points (A1,  B1,  C1,  D1,  E1,  and  A2).  The variations of plastic strain, plastic strain rates, and the absolute activities of twinning and slip with respect to the time are also quantified, as shown in Figure 4(b)–Figure 4(e). The activity of twin or slip is a normalized factor that is used to indicate the percentage of plastic deformation in association with twinning or slip during a deformation segment. For example,  fTwAiBi=(Δεp(zz)Tw)AiBi/(Δεp(zz)Tw+Δεp(zz)S)AiBi  is for twin activity during deformation from  Ai  to  Bi, and  fSAiBi=(Δεp(zz)Tw)AiBi/(Δεp(zz)Tw+Δεp(zz)S)AiBi  corresponds to the slip activity, where Δ denotes the plastic strain (twinning or slip) range between Ai and Bi. In Figure 4(d), the absolute value of the normalized activity factor is shown.Figure 4
(a) Stress-plastic strain hysteresis loops at the critical points of the first and second loading cycles.In situ, optical micrographs at critical points (A1,  B1,  C1,  D1,  E1, and  A2) show the morphology change of twins. from (b) to (e) illustrate the variations of (b) plastic strains, (c) plastic strain rates, (d) absolute activity of twinning and slip which indicates the percentage of plastic deformation by twinning or slip during a deformation segment in the stress-plastic strain hysteresis loop, and (e) the stress with respect to the time for the first and second loading cycles.During initial tension (O  to  A1), the six variants of  {101-2}  tensile twins are easily activated due to the same Schmid factor of 0.499 (see Figure 1). As observed in in situ optical microscopy (see Supplementary MOVIE), deformation twins nucleate instantaneously and grow very rapidly, forming fresh twins [5]. In Figures 4(c) and 4(d), it is noticed that the twin-induced strain rate has the same sign as the applied total strain rate, but the slip-induced strain rate has an opposite sign once twinning is activated. At the tensile peak strain (A1), all the deformation twins are fully expanded (see micrograph A1 in Figure 4(a)).  From A1 to B1 in Figure 4(c), the slip-induced plastic strain rate is initially greater than the detwinning-induced plastic strain rate, but later approximately equals to zero, implying that detwinning mainly accommodates the applied strain. Comparing the optical micrographs  A1  and  B1  in Figure 4(a), detwinning of the fully expanded twins at  A1  is clearly observed.  As revealed in Figures 4(d) and 4(e), both detwinning and slip-induced strain rates have the same sign as the applied strain rate. During tensile unloading and the early stage of compressive reloading, slip has a higher activity than detwinning (Figure 4(d)) and the magnitude of the stress quickly decreases, indicating recovery of slips (or reversible slip). Subsequently until point  B1, the stress-plastic strain curve shows slight strain hardening where detwinning has the higher activity than slip (Figure 4(d)).  From B1 to C1 in Figure 4(c), detwinning-induced strain rate has the same sign as the applied strain rate, but slip-induced strain rate has an opposite sign, clearly showing the occurrence of inverse slip. Detwinning during this segment has a higher activity than the slip activity (Figure 4(d)). Differing from detwinning from  A1  to  B1, the magnitude of the stress quickly increases from  B1  to  C1. It is noted that  B1  in Figure 4 is a critical point corresponding to the transition from low work hardening detwinning to high work hardening detwinning, at which the plastic strain rate induced by slip inverses its sign from negative to positive (Figure 3(c)). From  C1  to  D1, deformation is elastic, and  D1  corresponds to the yield point. No morphology change is observed by comparing optical micrographs at  C1  and D1.  From  D1  to  A2, retwinning occurs at a compressive stress of  −50 MPa at the early stage (D1  to  E1) of reversed loading. As revealed in optical micrograph  E1, pure retwinning is terminated at  E1  with the appearance of two fresh twins (see Arrows  P1  and P2  in Figure 4).  During pure retwinning from  D1  to  E1, the slip-induced strain rate has an opposite sign to the applied plastic strain rate, indicating that inverse slip appears. After  E1, twinning during  E1  to  A2  is mainly associated with fresh twinning combined with retwinning, and the stress magnitude is approximately constant.  As observed in optical micrograph  A2, several new twins are nucleated.The second loading cycle (A2  to  A3) experiences a similar deformation process as the first loading cycle (A1  to  A2, see Figure 4). Deformation mechanism corresponding to the segment from  A2  to B2 is the same as that from  A1  to  B1. The slip-induced plastic strain rate is initially greater than that associated with detwinning but later approaches approximately zero where detwinning mainly accommodates plastic deformation.  From  B2  to  C2, detwinning-induced strain has the same sign as that of the applied strain, but slip-induced strain rate has an opposite sign. Deformation from  C2  to  D2  is elastic. From  D2  to  A3, the single crystal initially experiences re-twinning and subsequently fresh twinning. Inverse slip only accompanies with retwining and ends up at  E2, at which the sign of slip-induced rate changes from negative to positive.Similar features were observed for the subsequent loading cycles (Figure5) with typical four featured segments: (i) twinning from  Di-1 to  Ai, including pure retwinning (Di-1  to  Ei-1) and fresh twinning combined with retwinning (Ei-1  to  Ai),  (ii) low work hardening detwinning from Ai to  Bi, (iii) high work hardening detwinning from  Bi  to  Ci, and (iv) elastic deformation from  Ci  to  Di. To visualize the dependence of the deformation characteristics on loading cycle, Figure 5(a) plots the variations of twin-induced strain and slip-induced strain for the first ten loading cycles. A comprehensive analysis was performed for all loading cycles, and the results indicate that inverse slip always accompanies with pure retwinning (Di  to  Ei) and high work hardening detwinning (Bi  to  Ci).Dependence of plastic strains and other physical quantities associated with deformation mechanisms on the loading cycles. (a) Variations of twin-induced and slip-induced strains, (b) stress-plastic strain hysteresis loops, (c) the stresses atAi  and  Bi and the stress range between  Di  and  Ci. (d)–(g) Variation of twin-induced and slip-induced strains during (d) low work hardening detwinning, (e) high work hardening detwinning, (f) pure retwinning, and (g) retwinning and fresh twinning together.
(a)
(b)
(c)
(d)
(e)
(f)
(g)The variation of the stresses atAi  and  Bi  and the stress range between  Di  and  Ci  are plotted in Figure 5(c) with respect to the loading cycles. The stress magnitude  Bi    increases with loading cycles, which can be ascribed to strain hardening due to the dislocation-twin boundary interactions [23, 24]. Accompanying with cyclic loading, more slips are activated and interact with the twin boundaries. Atomistic simulations combining with dislocation theory show that lattice glide dislocations can transmit across twin boundary or dissociate on twin boundary while the residual and sessile dislocations are left at twin boundary and further pin the twin boundaries [10, 23–26].  However, the elastic stress range between  Di  and  Ci  decreases with increasing loading cycles, which could be mainly due to the accumulation of residual twins and the increase in the backstress resulted from detwinning. The peak stress at Ai increases with loading cycles, indicating that strain hardening is the result of both dislocation-dislocation and dislocation-twin interactions [24]. The variation of twin activity and slip activity with respect to the four segments during cyclic loading are plotted in Figures 5(d)–5(g). The ratio of detwinning-induced strain over slip-induced strain is approximately 1.60 during low work hardening detwinning and is 1.20 during fresh twinning, while both accommodate the applied strain. However, during high work hardening detwinning and pure retwinning, the ratio is approximately  −1.80 in average where inverse slips take place.In summary, plastic deformation of[0001]-oriented Mg single crystals during cyclic loading can be featured with four segments that correspond to distinctive deformation mechanisms.  Both slip and twin are always activated during plastic deformation, but twinning (or detwinning) is more active and contributes more to the total plastic strain. For the first time, inverse slip is found to be always accompanying with pure retwinning and high work hardening detwinning. This implies that twinning dislocation experiences a smaller Peierls stress than the lattice glide dislocation, which is in agreement with atomistic simulations [11].  In addition, retwinning can take place at macroscale compression accompanying with inverse slip, indicating that the local stress (which can be ascribed to the backstress resulted from the detwinning) has a significant effect on deformation mechanisms. The observed high work hardening detwinning associated with inverse slip and the increase of stress magnitude might be an indicator of strain hardening aroused from the dislocation-twin interaction. The current findings provide a new insight in understanding plastic deformation and will benefit the development of polycrystalline plastic models for hexagonal-close-packed crystals [27–29].



---