# Morphological and Mechanical Properties of Poly (Butylene Terephthalate)/High-Density Polyethylene Blends

Authors: Nga Thi-Hong Pham; Van-Thuc Nguyen
Journal: Advances in Materials Science and Engineering
 (2020)

---

## Abstract

Poly (butylene terephthalate) (PBT) is a popular thermoplastic polyester resin but has low strength and low melting point. To improve its properties, PBT is often mixed with other resins, such as high-density polyethylene (HDPE). In this study, PBT/HDPE samples with 100% PBT, 5%, 10%, 15%, and 100% HDPE are generated and tested. The samples are analyzed by tensile strength, flexural strength, impact strength, and SEM tests. Adding HDPE will reduce tensile strength compared to pure PBT, in which 5%, 10%, and 15% PBT/HDPE samples obtain the values 40.23, 38.11, and 27.77 MPa, respectively. These values are lower than that of pure PBT but still higher than that of HDPE. Improving the HDPE portion mostly results in decreasing flexural strength. The flexural strengths of these samples are 87.79, 70.47, 55.3, 58.98, and 19.14 MPa corresponding to 100% PBT, 5%, 10%, 15%, and 100% HDPE samples, respectively. Moreover, the SEM microstructure of PBT and HDPE indicates a two-phase heterogeneous mixture with little or no adhesion between these phases.


---

## Body

## 1. Introduction

Poly (butylene terephthalate) (PBT) is an important thermoplastic with good properties of chemical resistance, insulation, lubrication, and processing and has been widely used in the automobile and construction industry. It exhibits high rates of crystallization, allowing short cycle times when pressing. However, its tensile strength and impact resistance is rather low. To improve its characteristics, PBT can be mixed with other polymers.Polymer blending is a popular and efficient method in which new materials can be produced to meet specific and diverse demands. Blended polymers are preferred over homogeneous types because they can perform the advantages of each component. For instance, semicrystalline polybutylene terephthalate (PBT) has some disadvantages such as low impact strength and low melting strength. Therefore, it can be mixed with a variety of polyethylene polymers, such as high-density polyethylene (HDPE), low-density polyethylene (LDPE), linear low-density polyethylene (LLDPE), and polypropylene (PP), to create thermoplastic materials that are commonly used in the packaging industry. The blended polymers also provide an alternative means of using recycled plastic waste by mixing one to another type of polymer.Toothbrush bristles are often made from polyamide (PA) and PBT fiber mixture. To recycle, this mixture must be classified into PA fiber and PBT fiber. After separation, PA is often reused due to its high cost [1, 2]. PBT is a widely used thermoplastic polyester resin, but it still has certain disadvantages such as low strength, low melting point, and low durability. PBT is often mixed with other resins to improve its characteristics. However, mixing two or more polymers together often leads to incompatibilities. In addition, Jubinville et al. [3] showed that the mixture can also be well dispersed by using a suitable compatibilizer. According to Greiner et al. [4], the mixture of PBT and PC can be sintering by a liquid-phase method by applying selective laser sintering (SLS). Wang et al. [5] investigated HDPE with a rigid PA-6/polybutylene terephthalate core. It was found that the strength of the sample of a mixture of three different substances, polyethylene PA-6/PBT (80/10/10), was 43.87 kJ/m2, two times higher than pure HDPE. Microstructure observations show that the addition of polybutylene terephthalate and PA-6 leads to the appearance of core-dispersed particles in an HDPE matrix, which is the main reason for HDPE hardening. In a study by Chalabi Tehran et al. [6], thermoplastic polyurethane (TPU) and clay nanoparticles have been integrated into PBT to improve impact properties and tensile strength. PBT/TPU samples (90/10, 80/20, and 70/30) were prepared by melt mixing using a coaxial twin-screw extruder, followed by injection molding. In the next stage, clay nanoparticles with different weight fractions were added to the PBT/TPU (80/20) mixture. SEM pictures illustrate good compatibility between TPU and PBT. The addition of TPU to PBT significantly increases impact strength but reduces tensile strength and elastic modulus. The incorporation of clay nanoparticles into a PBT/TPU mixture has greatly improved the tensile properties. A balance of tensile and impact characteristics has been found in the PBT/TPU/clay nanocomposite system (80/20/3). Salmoria et al. [7] investigated the structure and properties of blended samples PA-12 and PBT. Higher values for the bending modulus and tensile strength expressed by the specimen 90/10 PA-12/PBT show the hardening effect of the PBT particles in the PA-12 matrix. These results indicate the potential application in the manufacture of 90/10 PA-12/PBT with high stiffness and fatigue resistance. Yanping et al. [8] researched the PBT/TPU mixture prepared by melting their mixture. The flexibility, crystalline behavior, and hardening mechanism of PBT/TPU mixtures have been studied. The results have proved that adding TPU will help improve the toughness of the mixture.The development of microheterogeneous composites with a structural discontinuity is becoming one of the important trends in the production of new synthetic polymer materials. The mixture of two compatible polymers can increase the characteristics of the composite. A popular composite polymer-polymer system is PBT and polyolefin resins [9–11]. Studies of PBT and polyolefin-based composites have shown significant improvement in their physical and mechanical properties when adding 2–5wt% PBT. Differences in tensile values for PBT and PBT/polyolefin samples were explained by forming a loose-packed interfacial layer (LIL) between thermodynamically incompatible polymers, where crystal formation is not possible. Under high temperatures and deformation, the molecular weight distribution of polymers may change as certain low-molecular fractions can be formed, contributing to the plasticizer process [12, 13]. Mikitaev et al. [9] have proved that HDPE is one of the most promising materials that can improve the properties of PBT. However, PBT/HDPE is an incompatible mixture because of the lack of bonding on the surface of these two materials, thereby leading to its poor mechanical properties.


## 2. Materials and Methods

The experiment chose to use HDPE resins from SABIC-HDPE 4024, Saudi Arabia, which was provided by Thuan Thang Plastic Co., Ltd. PBT was taken from the brush hair scraps, and then PBT resins were created from the bristles. Samples of HDPE and PBT resins were mixed and pressed according to the proportions shown in Table1.Table 1
Composition of the testing sample.
SamplesComponent (wt.%)‐PBTHDPEH01000H5955H109010H158515H1000100


### 2.1. Plastic Drying

The samples are dried for 10 h at 80°C before pressing by the plastic injection molding machine.


### 2.2. Tensile Testing

The samples are tested following the ASTM D638 standard. The number of tensile test samples included 24 samples divided into 6 groups. The sample tested must be free of sharp edges, oil, grease, and other impurities. Before testing, the samples are stored in an environment with a temperature of 23 ± 2°C and a humidity of 50 ± 5%, for at least 40 hours.The dimensions of the samples are shown in Figure1. The sample is mounted on the testing machine as shown in Figure 2 and pulled at a speed of 50 mm/min at room temperature.Figure 1
Sample size of the tensile test.Figure 2
Sample mounted on the universal Shimadzu Autograph AG-X Plus machine.The test is performed on the universal Shimadzu Autograph AG-X Plus machine. The expansion meter is a high-resolution camera (1.8μm) that does not contact with the sample. The basic specifications of the testing machine are maximum test power of 20 kN, speed range of 0.001–1600 mm/min, speed accuracy of ± 0.1% of test speed, operating environment at 5–50°C, and data collection rate of 1000 Hz.


### 2.3. Flexural Testing

The samples are tested following the ISO 178 standard as shown in Figure3 and Figure 4. The number of samples is 30 divided into 6 groups.Figure 3
Sample size for bending strength testing.Figure 4
Sample mounted on the Instron 5566 machine.


### 2.4. Izod Impact Testing

The samples are tested following the ASTM D256 standard (Figure5). According to ASTM D256, we need to check at least 4 samples for each sample group to achieve high accuracy. However, to prevent the sample from being damaged during measurement, 7 samples are taken for each group of samples tested. Therefore, the total number of samples is 42. The test is performed on the impact tester Tinius Olsen IT504 (Figure 6).Figure 5
Sample size for Izod impact strength.Figure 6
Izod impact tester Tinius Olsen IT504.


### 2.5. Microstructure Examination

To observe the sample microstructure, the experiment uses a high-resolution scanning electron microscope (SEM) (HITACHI S-4800).


## 2.1. Plastic Drying

The samples are dried for 10 h at 80°C before pressing by the plastic injection molding machine.


## 2.2. Tensile Testing

The samples are tested following the ASTM D638 standard. The number of tensile test samples included 24 samples divided into 6 groups. The sample tested must be free of sharp edges, oil, grease, and other impurities. Before testing, the samples are stored in an environment with a temperature of 23 ± 2°C and a humidity of 50 ± 5%, for at least 40 hours.The dimensions of the samples are shown in Figure1. The sample is mounted on the testing machine as shown in Figure 2 and pulled at a speed of 50 mm/min at room temperature.Figure 1
Sample size of the tensile test.Figure 2
Sample mounted on the universal Shimadzu Autograph AG-X Plus machine.The test is performed on the universal Shimadzu Autograph AG-X Plus machine. The expansion meter is a high-resolution camera (1.8μm) that does not contact with the sample. The basic specifications of the testing machine are maximum test power of 20 kN, speed range of 0.001–1600 mm/min, speed accuracy of ± 0.1% of test speed, operating environment at 5–50°C, and data collection rate of 1000 Hz.


## 2.3. Flexural Testing

The samples are tested following the ISO 178 standard as shown in Figure3 and Figure 4. The number of samples is 30 divided into 6 groups.Figure 3
Sample size for bending strength testing.Figure 4
Sample mounted on the Instron 5566 machine.


## 2.4. Izod Impact Testing

The samples are tested following the ASTM D256 standard (Figure5). According to ASTM D256, we need to check at least 4 samples for each sample group to achieve high accuracy. However, to prevent the sample from being damaged during measurement, 7 samples are taken for each group of samples tested. Therefore, the total number of samples is 42. The test is performed on the impact tester Tinius Olsen IT504 (Figure 6).Figure 5
Sample size for Izod impact strength.Figure 6
Izod impact tester Tinius Olsen IT504.


## 2.5. Microstructure Examination

To observe the sample microstructure, the experiment uses a high-resolution scanning electron microscope (SEM) (HITACHI S-4800).


## 3. Results and Discussion

### 3.1. Surface Morphology

Figure7 shows the specimen of the tensile test, flexural strength test, and Charpy impact test. Through the practice of injection molding, it can be seen that sample H0 is not easy to inject, while sample H100 has a high shrinkage rate. Samples H5, H10, and H15 have a good surface quality.Figure 7
Specimen of the tensile test, flexural strength test, and Charpy impact test: (a) flexural strength samples, (b) Charpy impact samples, and (c) tensile test samples.
(a)(b)(c)Figure8 presents the stress-strain curves of the samples. The pure PBT is very brittle with a very low value of elongation of about 2.5%. Adding HDPE to PBT will lead to a decrease in tensile strength. The tensile strength values of the composite samples are in the middle of pure PBT and HDPE. Generally, the fracture mechanism of these samples is also brittle fracture.Figure 8
Stress-strain curves of samples.Figure9 describes the effect of the HDPE content on the tensile strength of the PBT/HDPE mixture. Samples H5, H10, and H15 have the values 40.23, 38.11, and 27.77 MPa, respectively. These values are lower than the 51.00 MPa value of pure PBT but higher than that of HDPE which is 20.79 MPa. In general, adding HDPE will reduce tensile strength compared to pure PBT. Because, for incompatible blends such as PBT/HDPE, incompatibility between the two components can result in weaker bonding between the components, poorer mechanical properties, and other problems such as welding line failure in the injection molding process.Figure 9
Effect of HDPE percentage on the tensile strength of the PBT/HDPE blends.The average elongation values at break are shown in Figure10. The mixtures of 0–15% HDPE have a low value of elongation, vibrating about 2.5%. Therefore, by adding 0–15% HDPE to the mixture, the elongation of the sample does not cause appreciable change. The pure HDPE sample achieves the highest value of elongation of 24.09%. The HDPE particles are dispersed in the PBT/HDPE matrix. In this matrix, the two phases are almost co-continuous, creating higher barrier properties for toluene than pure PE [12].Figure 10
Effect of HDPE percentage on the break-strain value.Figure11 shows the stress curves of the flexural test of the PBT/HDPE mix. Similar to the tensile strength, initially, the flexural stress of these blended samples gradually increases, followed by a sudden decrease when the samples are destroyed. However, with a pure HDPE sample, the stress gradually increases and then gradually decreases as its ductility is much higher.Figure 11
The stress-strain curves of the flexural test of the PBT/HDPE blends: (a) 0% HDPE, (b) 5% HDPE, (c) 10% HDPE, (d) 15% HDPE, and (e) 100% HDPE.
(a)(b)(c)(d)(e)Figure12 exhibits the effect of HDPE percentage on the flexural strength of the PBT/HDPE blends. The flexural strength of these samples is 87.79, 70.47, 55.3, 58.98, and 19.14 MPa corresponding to 0%, 5%, 10%, 15%, and 100% HDPE, respectively. Increasing the HDPE mostly results in decreasing the flexural strength.Figure 12
Effect of HDPE percentage on the flexural strength of the PBT/HDPE blends.The effect of HDPE percentage on the max-strain value is demonstrated in Figure13. Overall, increasing the HDPE from 0 to 10% causes a minor change in max-strain values; the max-strain value slightly declines. This value obtains the lowest number of 4.50% at 15% HDPE, the same with 4.56% at 10% HDPE.Figure 13
Effects on max-strain in different compositions of HDPE.


### 3.2. Izod Impact Test Results

PBT has good hydrocarbon barrier properties but has some obvious disadvantages such as low impact toughness [11]. Figure 14 indicates the effect of the HDPE content on the impact toughness of PBT/HDPE blends. The impact toughness of these samples is 2.70, 2.52, 2.65, 2.59, and 39.19 kJ/m2 corresponding to H0, H5, H10, H15, and pure HDPE samples, respectively. Overall, adding 5–15% HDPE does not cause much change in the impact toughness. Moreover, the impact toughness of the PBT/HDPE mixtures is lower than that of pure HDPE. These results are consistent with the tensile strength results discussed in the previous section. These results also showed that an increase in the spherulite size of HDPE results in no improvement in the impact strength [13]. Wang et al. [5] studied HDPE and HDPE/PBT 80/20, and the results of impact strength showed that HDPE hardly improves the toughness of these blends and the impact value of the HDPE/PBT mixture is 7.05 kJ/m2, lower than pure HDPE. Besides, similar to the break-strain value as shown in Figure 10, Figure 14 presents a big variation due to the sudden change in the percentage of the PBT/HDPE mixture. The HDPE percentage has a rapid change from 15% to 100% of the mixture; therefore, the structure and the mechanical properties have a great change.Figure 14
Effect of HDPE percentage on the impact toughness of the PBT/HDPE blends.


### 3.3. Microstructure Results

The properties of the polymer mixture are strongly influenced by its morphology. Figure15(a)–15(c) show the SEM images of the PBT/HDPE mixture with different HDPE contents at a magnification of 5000×. The pure PBT shows a relatively smooth surface, a characteristic of typical brittle fracture, as shown in Figure 15(a). By adding 5–15% HDPE to the mixtures, the surfaces show more surface evidence of small fibers, as shown in Figure 15(b)–15(d). Notably, Figure 15(b)–15(d) show that the spherical HDPE particles are scattered in the PBT matrix, representing a well-dispersed microstructure. Furthermore, there is no evidence of adhesion between the HDPE phase and substrate, as the surface of the HDPE particles is completely clear. This is the reason why the 5–15% HDPE samples do not present an improvement in the mechanical characteristics.Figure 15
SEM micrographs of the PBT/HDPE blend with different weight percents of HDPE (5000× magnification): (a) 0% HDPE (100% PBT), (b) 100% HDPE, (c) 5% HDPE, (d) 10% HDPE, and (e) 15% HDPE.
(a)(b)(c)(d)(e)PBT and HDPE have a clear spherical crystal structure [10, 12]. Figure 16(a)–16(c) show the dispersion of fine spherical particles of HDPE in a continuous matrix of PBT at a magnification of 30000×. Large cavities can be seen due to the removal of HDPE particles. Because the chemical structures of PE (nonpolar) and PBT (polar) are completely different, the two phases are seen directly on the microscope image. Incompatibility between PE and PBT can also be seen directly on the SEM image. Pesneau’s study showed HDPE/PBT incompatibility because the surface of the PBT particles was completely clean, and the fault was always present at the interface [12]. Due to the lack of interphase adhesion, the mechanical properties of these mixtures are relatively poor.Figure 16
SEM micrographs of the PBT/HDPE blend with different weight percents of HDPE (30000× magnification): (a) 5% HDPE, (b) 10% HDPE, and (c) 15% HDPE.
(a)(b)(c)An increase in HDPE content leads to a further increase in the mean particle size. For a mixture containing 0%, 10%, and 20% HDPE, two distinct zones are clearly visible due to PBT and HDPE. Joung Sook Hong’s study also demonstrated that the material with lower impact toughness forms a coating around the PBT core. This result also showed that a significant increase in the spherulite size of HDPE resulted in no improvement in the impact strength of HDPE/PBT [13].


## 3.1. Surface Morphology

Figure7 shows the specimen of the tensile test, flexural strength test, and Charpy impact test. Through the practice of injection molding, it can be seen that sample H0 is not easy to inject, while sample H100 has a high shrinkage rate. Samples H5, H10, and H15 have a good surface quality.Figure 7
Specimen of the tensile test, flexural strength test, and Charpy impact test: (a) flexural strength samples, (b) Charpy impact samples, and (c) tensile test samples.
(a)(b)(c)Figure8 presents the stress-strain curves of the samples. The pure PBT is very brittle with a very low value of elongation of about 2.5%. Adding HDPE to PBT will lead to a decrease in tensile strength. The tensile strength values of the composite samples are in the middle of pure PBT and HDPE. Generally, the fracture mechanism of these samples is also brittle fracture.Figure 8
Stress-strain curves of samples.Figure9 describes the effect of the HDPE content on the tensile strength of the PBT/HDPE mixture. Samples H5, H10, and H15 have the values 40.23, 38.11, and 27.77 MPa, respectively. These values are lower than the 51.00 MPa value of pure PBT but higher than that of HDPE which is 20.79 MPa. In general, adding HDPE will reduce tensile strength compared to pure PBT. Because, for incompatible blends such as PBT/HDPE, incompatibility between the two components can result in weaker bonding between the components, poorer mechanical properties, and other problems such as welding line failure in the injection molding process.Figure 9
Effect of HDPE percentage on the tensile strength of the PBT/HDPE blends.The average elongation values at break are shown in Figure10. The mixtures of 0–15% HDPE have a low value of elongation, vibrating about 2.5%. Therefore, by adding 0–15% HDPE to the mixture, the elongation of the sample does not cause appreciable change. The pure HDPE sample achieves the highest value of elongation of 24.09%. The HDPE particles are dispersed in the PBT/HDPE matrix. In this matrix, the two phases are almost co-continuous, creating higher barrier properties for toluene than pure PE [12].Figure 10
Effect of HDPE percentage on the break-strain value.Figure11 shows the stress curves of the flexural test of the PBT/HDPE mix. Similar to the tensile strength, initially, the flexural stress of these blended samples gradually increases, followed by a sudden decrease when the samples are destroyed. However, with a pure HDPE sample, the stress gradually increases and then gradually decreases as its ductility is much higher.Figure 11
The stress-strain curves of the flexural test of the PBT/HDPE blends: (a) 0% HDPE, (b) 5% HDPE, (c) 10% HDPE, (d) 15% HDPE, and (e) 100% HDPE.
(a)(b)(c)(d)(e)Figure12 exhibits the effect of HDPE percentage on the flexural strength of the PBT/HDPE blends. The flexural strength of these samples is 87.79, 70.47, 55.3, 58.98, and 19.14 MPa corresponding to 0%, 5%, 10%, 15%, and 100% HDPE, respectively. Increasing the HDPE mostly results in decreasing the flexural strength.Figure 12
Effect of HDPE percentage on the flexural strength of the PBT/HDPE blends.The effect of HDPE percentage on the max-strain value is demonstrated in Figure13. Overall, increasing the HDPE from 0 to 10% causes a minor change in max-strain values; the max-strain value slightly declines. This value obtains the lowest number of 4.50% at 15% HDPE, the same with 4.56% at 10% HDPE.Figure 13
Effects on max-strain in different compositions of HDPE.


## 3.2. Izod Impact Test Results

PBT has good hydrocarbon barrier properties but has some obvious disadvantages such as low impact toughness [11]. Figure 14 indicates the effect of the HDPE content on the impact toughness of PBT/HDPE blends. The impact toughness of these samples is 2.70, 2.52, 2.65, 2.59, and 39.19 kJ/m2 corresponding to H0, H5, H10, H15, and pure HDPE samples, respectively. Overall, adding 5–15% HDPE does not cause much change in the impact toughness. Moreover, the impact toughness of the PBT/HDPE mixtures is lower than that of pure HDPE. These results are consistent with the tensile strength results discussed in the previous section. These results also showed that an increase in the spherulite size of HDPE results in no improvement in the impact strength [13]. Wang et al. [5] studied HDPE and HDPE/PBT 80/20, and the results of impact strength showed that HDPE hardly improves the toughness of these blends and the impact value of the HDPE/PBT mixture is 7.05 kJ/m2, lower than pure HDPE. Besides, similar to the break-strain value as shown in Figure 10, Figure 14 presents a big variation due to the sudden change in the percentage of the PBT/HDPE mixture. The HDPE percentage has a rapid change from 15% to 100% of the mixture; therefore, the structure and the mechanical properties have a great change.Figure 14
Effect of HDPE percentage on the impact toughness of the PBT/HDPE blends.


## 3.3. Microstructure Results

The properties of the polymer mixture are strongly influenced by its morphology. Figure15(a)–15(c) show the SEM images of the PBT/HDPE mixture with different HDPE contents at a magnification of 5000×. The pure PBT shows a relatively smooth surface, a characteristic of typical brittle fracture, as shown in Figure 15(a). By adding 5–15% HDPE to the mixtures, the surfaces show more surface evidence of small fibers, as shown in Figure 15(b)–15(d). Notably, Figure 15(b)–15(d) show that the spherical HDPE particles are scattered in the PBT matrix, representing a well-dispersed microstructure. Furthermore, there is no evidence of adhesion between the HDPE phase and substrate, as the surface of the HDPE particles is completely clear. This is the reason why the 5–15% HDPE samples do not present an improvement in the mechanical characteristics.Figure 15
SEM micrographs of the PBT/HDPE blend with different weight percents of HDPE (5000× magnification): (a) 0% HDPE (100% PBT), (b) 100% HDPE, (c) 5% HDPE, (d) 10% HDPE, and (e) 15% HDPE.
(a)(b)(c)(d)(e)PBT and HDPE have a clear spherical crystal structure [10, 12]. Figure 16(a)–16(c) show the dispersion of fine spherical particles of HDPE in a continuous matrix of PBT at a magnification of 30000×. Large cavities can be seen due to the removal of HDPE particles. Because the chemical structures of PE (nonpolar) and PBT (polar) are completely different, the two phases are seen directly on the microscope image. Incompatibility between PE and PBT can also be seen directly on the SEM image. Pesneau’s study showed HDPE/PBT incompatibility because the surface of the PBT particles was completely clean, and the fault was always present at the interface [12]. Due to the lack of interphase adhesion, the mechanical properties of these mixtures are relatively poor.Figure 16
SEM micrographs of the PBT/HDPE blend with different weight percents of HDPE (30000× magnification): (a) 5% HDPE, (b) 10% HDPE, and (c) 15% HDPE.
(a)(b)(c)An increase in HDPE content leads to a further increase in the mean particle size. For a mixture containing 0%, 10%, and 20% HDPE, two distinct zones are clearly visible due to PBT and HDPE. Joung Sook Hong’s study also demonstrated that the material with lower impact toughness forms a coating around the PBT core. This result also showed that a significant increase in the spherulite size of HDPE resulted in no improvement in the impact strength of HDPE/PBT [13].


## 4. Conclusions

(i)
The tensile strength results show that the PBT/HDPE mixture can present plastic damage. Adding HDPE will reduce tensile strength compared to pure PBT. 5%, 10%, and 15% HDPE/PBT samples have the values 40.23, 38.11, and 27.77 MPa, respectively. These values are lower than that of pure PBT but still higher than that of HDPE.(ii)
Increasing the HDPE mostly results in a decrease in flexural strength. The flexural strength of these samples is 87.79, 70.47, 55.3, 58.98, and 19.14 MPa corresponding to 0%, 5%, 10%, 15%, and 100% HDPE, respectively.(iii)
Adding 5–15% HDPE does not cause much change in the impact toughness. The impact toughness of the PBT/HDPE mixtures is lower than that of pure HDPE. The impact toughness of these samples is 2.70, 2.52, 2.65, 2.59, and 39.19 kJ/m2 corresponding to 100% PBT, 5%, 10%, 15% HDPE/PBT, and pure HDPE samples, respectively.(iv)
The SEM microstructure of PBT and HDPE indicates a two-phase heterogeneous mixture with little or no adhesion between these phases.(v)
Further studies should be conducted to identify these morphological changes to the properties and also to correlate the morphology.



---