# Research on the Preparation of Microbial Capsules by Epoxy Resin-CoatedBacillus pasteurii

Authors: Yingying Hu; Weitao Liu; Xinlei Jia; Lanjuan Xu; Jianjun Shen; Xiangming Hu
Journal: Shock and Vibration
 (2021)

---

## Abstract

With the increasing number of underground engineering construction projects such as coal mining, tunnel, and subway, water inrush disasters occur more and more frequently. Inspired by the phenomenon of microbial mineralization and diagenesis, microbial-induced calcium carbonate precipitation (MICP) is used to repair cracks in cement-based materials, which provides a new idea to solve the problem of water inrush. To investigate the self-healing properties of microbial capsules, this paper selected epoxy resin E-51 cured by DMP-30 as the wall material andBacillus pasteurii as the core materials for experiments. In this paper, a single-factor method was adopted to determine the optimal preparation process of microbial capsules and the oil-phase separation method to prepare the microbial capsules. The effects of various factors on the experimental results under different core-wall ratios, reaction time, reaction temperatures, and agitation rates were analyzed. Microbial capsules were analyzed by Fourier transform infrared spectroscopy and optical microscopy to explore the functional groups and features of microbial capsules. The experimental results showed that the microbial capsules achieved the best performance with a core-to-wall ratio of 1 : 3, a reaction temperature of 50°C, a reaction time of 40 min, and a stirring rate of 300 rpm. Meanwhile, we determined the spore survival rate of microbial capsules and finally studied the waterproofness, storage stability, and rupture under the pressure of microbial capsules. We concluded that microbial capsules have high-efficiency and self-healing properties.


---

## Body

## 1. Introduction

In the underground engineering, microcracks often occur in concrete layer, which not only reduces the bearing capacity of the concrete structure but also affects its durability and waterproofness [1–8]. Currently, a more effective method for repairing concrete cracks is microcapsule technology. This technique involves coating the desired material with a suitable material to form a core-wall structure. The material used for coating is called a wall material, and the material to be coated is called a core material. The wall material is usually selected from organic polymer materials and inorganic materials, and the selection of the core material is determined according to the application of the microbial capsules. When microcapsule technology applies to the crack repair of concrete, its essence is the use of microorganisms to induce the formation of calcium carbonate. A specific microorganism is coated as a core material and embedded in concrete [9–13]. When the concrete cracks, the microbial capsule will break, and microbial metabolism will produce calcium carbonate, thereby repairing the crack.At present, microcapsule technology has made some progresses in concrete repair. To improve cemented coral sand’s self-healing efficiency, Xu et al. [14] fabricated the urea-formaldehyde (UF) microcapsule with in situ polymerization using controlled particles size distributions. They confirmed that the specimen’s crack or compression triggered the microcapsules, which then reacted with the contribution from the healing agent to self-heal the internal cracks. Singh et al. [15] found that the crack healing capacity of the calcium lactate-prepared samples significantly improved, in spite that the expanded clay aggregates-based samples featured a considerable decrease in strength. Also, the use of Bacillus sp. bacterial solution in the concrete mix enhances its mechanical properties. Wang et al. [16] studied the physical properties of microcapsules and the microstructure of self-healing concrete. They also analyzed the influence of microcapsules on the strength, permeability, and long-term shrinkage of self-healing concrete. Al-Tabbaa et al. [17] focused on microcapsules, which contain a healing agent. This healing agent will be released upon crack propagation. Han et al. [18] pointed out that bacteria with expanded clay (EC) are very active in generating CaCO3. Liu [19] prepared a kind of microcapsule and manufactured a new type of self-healing asphalt. To do so, he mixed asphalt, microcapsule, and curing agent with proper ratio. Mohamed et al. [20] found that efficient self-healing capacity not only requires sufficient healing compounds (e.g., calcium acetate) but also demands a minimal number of bacterial spores. Tripathi et al. [21] studied the effect of microcapsule shell material on the mechanical behavior of self-healing epoxy composites. They encapsulated the liquid epoxy healant in melamine-formaldehyde (MF) and urea-formaldehyde (UF), using the emulsion polymerization technique to prepare microcapsules of different shell walls. Singh and Gupta [22] produced self-healing mortar by using alkaline bacteria producing minerals. Shahid et al. [23] focused on the microcracks’ self-healing capability in concrete by using different Bacillus strains. They achieved a 16% increase in compressive strength in concrete and significant healing with Bacillus subtilis. Hu et al. [24–26] considered three novel types of healing agent encapsulation systems, namely, body-contact double capsule, parallel-style double capsule, and concentric-style capsule. They examined the compatibility of the PU healing agent with a dynamic crack using different accelerants. They also investigated the crack’s adhesion area for different healing systems in terms of the capsule type, capsule spacing, accelerant, and crack width. Al-Ansari et al. [27] characterized the average diameter and shell thickness of the produced microcapsules. Souza and Al-Tabbaa [28] found that the aqueous core microcapsules presented a thicker shell which precluded the rupture upon crack. Cheng [29] researched into the epoxy resin microcapsules which contain both solid particles and cured epoxy resin. He finally obtained the thickness of the shell coated with alkali-resistant Bacillus H4.Wang et al. [30, 31] used alginate as the wall material and successfully prepared microbial capsules by using Bacillus sphaericus fixed in hydrogel as the core material, thus effectively protecting the bacterial activity. Van Tittelboom et al. [32] adopted epoxy resin as the wall material and Bacillus coli as the core material to make spore bio-microbial capsules, which solved the problem of spore burial and dormancy in concrete. Cheng [33] prepared microbial capsules with ethyl cellulose and epoxy resin as the wall material, respectively, and Bacillus alkalisediminis H4 as the core material. The experimental results showed that microbial capsules have an excellent repair effect on concrete cracks [34, 35]. There are still some issues in the existing research that require further in-depth research. Among them, one of the critical issues is how to reduce the preparation cost and efficiently utilize the material to prepare microbial capsules with the best biocompatibility and mechanical triggering performance.This paper investigated the application of epoxy resin as a bacterial carrier in the self-repairing system ofBacillus pasteurii. First, we designed and successfully prepared Bacillus pasteurianum microcapsules, optimized the microcapsule preparation process through experiments, and obtained the process parameters such as the core-wall ratios, reaction temperatures, reaction time, and agitation rate required to achieve the best performance. Next, we characterized the performance of the prepared microcapsules and studied the biocompatibility of epoxy resin and Bacillus pasteurii by measuring the spore survival rate of the microcapsules. In addition, the strength test of the prefabricated cracks in this paper confirms that the prepared microbial capsules have high-efficiency self-healing properties. The research results of this paper provide new ideas for studying a wider range of self-repairing bacterial carriers and improving the repair activity and strength repair rate of bacteria in harsh environments such as mines.


## 2. Experiments and Materials

### 2.1. Selection of Wall Materials

In the preparation of microbial capsules, in order to achieve the best results, the wall material needs to meet specific requirements. First, to prevent the core material from oxidizing and volatilizing during storage, the wall material needs to have good airtightness. Meanwhile, the wall material must have a specific mechanical strength to ensure the isolation and protection of the core material. The wall material also needs to have suitable brittleness to guarantee that the core material can be released typically when the triggering condition is reached.On the other hand, in the preparation of microbial capsules, attention should be paid to the adverse effects of concrete conditions on microorganisms. In other words, we should prevent outside air, moisture, and oxygen from entering the microbial capsules to cause spores to germinate in advance. Furthermore, the wall material needs to be biocompatible and low in toxicity to maintain the activity of the core material.Epoxy resin is not only dense, waterproof, and mechanically robust and brittle but also nontoxic and has excellent biocompatibility. Therefore, in all aspects, this paper chooses epoxy resin E-51 as the wall material.Table1 shows the experimental instruments. This paper utilized the ultraclean workbench and Chinese medicine pellet machine for the preparation of bacterial core material. Meanwhile, we used a digital constant temperature water bath and drying box to complete the wall material to cover the core material. We observed the microbial capsule’s core-wall structure with an optical microscope and the absorption peak in the infrared spectrum of the microbial capsule by Fourier transform infrared spectroscopy. Additionally, a television microscope was used to explore the waterproofness, storage stability, and rupture ability under the pressure of the microbial capsules. The survival rate of the spores was measured using the biochemistry incubators.Table 1
Experimental instruments.
Experimental instrumentsModelManufacturerElectronic balanceBSA223SSartorius Instrument Co., LtdTelevision microscopeSA3300Beijing Tech Instrument Co., LtdDigital constant speed electric mixerJJ-1AJintan Hongye Experimental Instrument FactoryDigital constant temperature water bathHH-1Changzhou Jintan Kexing Instrument FactoryElectric blast drying boxModel 101Beijing Ever Bright Medical Treatment Instrument Co., LtdChinese medicine pellet machineHBZ-201Ruian Hanbo Electromechanical Co., LtdFourier transform infrared spectrometerNICOLET380Thermo Nicolet Co., LtdPowder tablet pressPC-24Tianjin JingTuo Instrument Technology Co., LtdBiochemical incubatorHPX-80Shanghai Hengyue Medical Equipment Co., Ltd


### 2.2. Selection of Core Materials

The microbial capsule core must be a microorganism with life activity and mineralization. Microbial mineralization types fall into two types: microbial-controlled mineralization and microbial-induced mineralization. Microbial-controlled mineralization depends on the physiological processes of microorganisms and has nothing to do with changes in the external environment, while microbial-induced mineralization is produced by activities such as cell metabolism.This research selectsBacillus pasteurii as the core microbe that adopts the microbially induced mineralization. More specifically, we make microbes into dry spore powder and mix the powder with the required nutrients and auxiliary materials such as microcrystalline cellulose to make core particles. Meanwhile, we induce calcium carbonate by cell metabolism to self-repair the concrete.


### 2.3. Measurement of Curing Agent Effect

To explore the effect of the curing agent, the epoxy resin E-51 was precured separately in advance with three curing agents: 2,4,6-trisphenol (DMP-30), m-xylylenediamine (MXDA), and silane coupling agent (KH-151). The amount of the curing agent MXDA is usually calculated based on the active hydrogen equivalent of the amine curing agent. Figure1 illustrates the structural formula of MXDA.Figure 1
The structure formula of MXDA.The molecular weight of MXDA is 136.19, and the number of active hydrogens is four. Accordingly, its active hydrogen equivalent is 34.05. The epoxy value of epoxy resin E-51 is 0.51, and the theoretical amount of MXDA is 17.37 g per 100 g of epoxy resin E-51. Its calculation formula is shown as follows:(1)W=MN×E,where W is the amount of curing agent required per 100 g of epoxy resin E-51, M is the molecular weight of MXDA, N is the number of active hydrogens of MXDA, and E is the epoxy value of the epoxy resin.The amounts of curing agents DMP-30 and KH-151 were added according to empirical values. That is, the amount of DMP-30 is 10 g per 100 g of epoxy resin E-51, and the amount of KH-151 is 15 g.In order to determine the curing effect, we placed 20 g of epoxy resin E-51 in a 50°C water bath for 10 minutes, diluted, and added with a curing agent. The bubbles were uniformly discharged after we stirred it, and we then placed it in a water bath for heat preservation. Afterward, we placed it in a beaker and observed the curing phenomenon. Table2 shows the control experiments.Table 2
Control experiments.
NumberExperimental conditionsCuring agentsWater bath temperature °CDuration of heat preservation minCuring agent amount g1DMP-30501022MXDA50103.53KH-151501034DMP-30201025MXDA20103.56KH-15120103


### 2.4. Microbial Capsule Preparation

#### 2.4.1. Core Material Preparation

The microcapsule core material is prepared by mixing dry spore powder, auxiliary materials, and nutrients and then granulating by a granulation apparatus that is shown in Figure2. The specific preparation method is as follows:Step 1. Mixing stage: Weigh nutrients according to the proportion of the medium components of the optimized strains, i.e., weigh 1 g of urea, 0.25 g of soy peptone, 0.75 g of casein, and 0.25 g of sodium chloride. Add 50 g of microcrystalline cellulose for expanding the core volume and 1.5 g of hydroxypropyl methylcellulose to promote adhesion of microcrystalline cellulose to spores and nutrients.Step 2. Grouping stage: Weigh 0.5 g of dry spore powder in a beaker and add 150 g of distilled water to stir. Add the liquid solution to the mixture and stir to form a paste.Step 3. Granulation stage: Place the obtained paste from the previous step in the extrusion port of the Chinese medicine pelletizing machine and obtain a flat body after being extruded appropriately. Take out the flat body and place it at the mouth of the purlin to obtain a strip. The strips are separated into individual pieces and placed at the pellet opening to roll out the granules. Place the pellets in a rounder, take out, and dry in a low-temperature drying oven at 40°C for 24 hours. Finally, we obtain core particles with single-particle size.Figure 2
Core material granulation.The flowchart of preparing the core material is shown in Figure3. The nutrients contain urea, soy peptone, casein, and sodium chloride; and the auxiliary materials encompass microcrystalline cellulose and hydroxypropyl methylcellulose.Figure 3
The flowchart of preparing the core materials.


#### 2.4.2. Single-Factor Experiments Design

A variety of factors may affect the preparation of microbial capsules, such as reaction time, reaction temperature, core-wall ratio, and agitation rate. This experiment uses a single-factor experiment to determine the optimal preparation conditions for microbial capsules. Table3 lists the experimental parameters.Table 3
Single-factor experiment parameters.
NumberFactorsCore-wall ratioTemperature °CReaction timeAgitation rate11 : 1504030021 : 2504030031 : 3504030041 : 4504030051 : 3404030061 : 3504030071 : 3604030081 : 3503030091 : 35040300101 : 35050300111 : 35040250121 : 35040300131 : 35040350


#### 2.4.3. Preparing the Microbial Capsule

We use the oil-phase isolation method to prepare microbial capsules, thus avoiding the contact of the core material with water during the preparation process, thereby maintaining the stability of the spores. Epoxy resin E-51 is a hydrophobic substance, which guarantees the feasibility of the experiment. The prepared core material particles were coated with epoxy resin E-51, and the epoxy resin E-51 was solidified on the surface of the core material to form a microbial capsule under the condition of a double oil phase. The specific preparation method is as follows:Step 1. Mixing the wall and core materials: Weigh Epoxy resin E-51 and core particles according to a core-wall ratio. Place both in a beaker and mix to mix well. Place the mixture in a constant temperature water bath and keep for 10 min.Step 2. Precuring stage: After 10 min of incubation, add the curing agent to the mixture, stir well, and place in a water bath for precuring for 30 min.Step 3. Film-forming stage: Add the mixture slowly to a three-necked flask, and set the reaction temperature and stirring speed. After 5 minutes, open the stopper on one side, slowly pour in the polydimethylsiloxane oil, and continue to stir for 1 hour.After the curing was completed, take out the final product, filter with absolute ethanol, and wash the surface of the polydimethylsiloxane. Place the product in a Petri dish and transfer to a low-temperature drying oven at 40°C. As such, we obtain the microbial capsule. Figure4 demonstrates the flowchart of the preparation.Figure 4
The preparing flowchart.


### 2.5. Features of the Microbial Capsules

#### 2.5.1. Waterproofness

Randomly select a plurality of microbial capsules in a beaker, slowly add distilled water to thoroughly soak the microbial capsules, and record the soaking time of the microbial capsules. Take 5–7 microbial capsules every other day, blot the surface moisture with absorbent paper, and place them on a glass slide. Place the slide under a microscope and adjust the magnification of the microscope to observe the presence or absence of cracks.


#### 2.5.2. Storage Stability

Weigh specific amounts of microbial capsules in a Petri dish and place the Petri dish on a dry and ventilated bench. Record the initial weight of the microbial capsule and the weight of the microbial capsules on the 3rd, 6th, 9th, 12th, and 15th days. Observe the mass loss of the microbial capsules, and calculate the mass loss rate based on the following formula:(2)M=m0−mim0×100%,where m0 and mi are the last and the current weight (g).


#### 2.5.3. Rupture Ability under Trigger Condition

Randomly select plurality of microbial capsules, place them on a laboratory bench, and fracture them with tweezers. Place the fractured microbial capsules under a microscope, and fix the magnification to observe the rupture of the surface of the microbial capsule. In this way, we can judge whether the mechanical properties of the microbial capsules can be triggered and further germinate the microorganisms to conduct the self-repairing process when the concrete where they are buried ruptures.


#### 2.5.4. Spore Survival Rate

We employ the plate colony-counting method to determine the spore survival rate of microbial capsules. First, ground the microbial capsule into a powder, add to the liquid medium, and shake well. Then, use a pipette to extract 1 ml of the mixture, slowly inject into a tube containing 9 ml of the liquid medium along the tube wall, and shake the tube to mix well. Repeat the above procedure and replace the sterile pipette once every dilution until it is diluted to 1 × 108 times.Pipet 100μL of the diluted liquid, pour into a solid medium prepared in advance, and then uniformly distribute the colonies on the plate. After solidification, turn over the culture dish and place in an incubator for 24 hours. Observe the germination of the spores in the culture dish and count the number of colonies in the culture dish. It should be noted that at the dilution factor at this time, one colony represents one spore in the microbial capsule. The spore germination rate is obtained according to the number of colonies at the dilution factor and the number of spores in the core material.


### 2.6. Verification of Self-Healing Effect of Microbial Capsules

#### 2.6.1. Test Pieces Preparation

Table4 lists the specific mixing ratio of the experimental test pieces. Figure 5 shows the preparation of self-healing test piece. We designed three sets of control experiments. Specifically, Group A is a standard test piece without adding any repair agent. Group B only adds the core material part from the repair agent, that is, the bacterial body. Group C adds the complete microbial capsule. Meanwhile, the cement mortar has a water-cement ratio of 0.3. The amount of the repair agent is 3.0% of the amount of the cementing material. Besides, the mold uses a cylindrical test piece with φ of 50 mm and H of 100 mm.Table 4
Material ratios.
GroupsCement (g)Sand (g)Water (g)Repair agent1270810270N/A2270810270Bacterial body3270810270Microbial capsuleFigure 5
Preparation of self-healing testing pieces.The specific preparation steps are as follows:(1)
Weigh the required materials according to the required amount, add cement, sand, and water in sequence, mix well, and finally add the microcapsules and mix well.(2)
Brush a layer of grease on the inside of the mold, pour the evenly mixed mixture into the mold, and shake it up.(3)
After leaving the mixture at room temperature for one day, demold. Then, put it in a standard constant temperature and humidity curing box (temperature 25°C; air humidity 90%), and stay until a specific time.


#### 2.6.2. Prefabricating Crack for Test Pieces

This paper took the cement mortar test pieces within the curing period and manually prefabricated cracks. Based on a comprehensive analysis of various prefabricated cracking methods, this paper adopted a universal pressure testing machine to prefabricate cracks for cylindrical specimens, as shown in Figure6. The specific steps are as follows:(1)
Place the test piece in the center of the pressure-bearing plate of the testing machine, and adjust the bottom disc to a balanced state.(2)
Apply the axial stress at a displacement speed of 0.01 mm/min, and prefabricate the crack using a concentrated load in the center.(3)
When the obvious cracking sound occurs, stop the pressurization. By then, we can obtain a striped crack that diverges from the center of the test piece to the surroundings.(4)
Record the failure load and calculate the compressive strength according to the following formula:(3)f=FA,wheref is the compressive strength of cubes of similar rock text pieces (MPa); F is the failure load of the test piece (N); A is the pressure area of the test piece (mm2).(5)
Record the stress-strain curve and the test force-deformation curve, and analyze the uniaxial compression curve of the test piece.Figure 6
Microcomputer-controlled electro-hydraulic servo universal testing machine.


#### 2.6.3. Curing of Test Pieces

During the self-repair experiment, there is an exchange of substances and energy, which demands the participation of microorganisms embedded in the test piece in advance. This process requires an effective medium to assist in energy exchange and material transportation. This test used the water curing method. Specifically, the cracked test pieces were immersed in the tap water, the cracked surface and the liquid surface were kept vertical, and the water temperature was adjusted to 25°C.


#### 2.6.4. Assessment of Self-Healing Performance

To evaluate the self-healing performance, we first conducted a water absorption test. The water absorption rate of the test pieces can reflect the weathering resistance and frost resistance. The water absorption rate depends on the number, size, and degree of cracks contained in the test piece. Water absorption can effectively reflect the degree of development of cracks and voids in the text pieces, so it is an important indicator to evaluate the nature of the test pieces. The steps for testing the water absorption of cement mortar test pieces are as follows:(1)
Set the temperature of the drying box to 75°C, and after drying for 48 h, weigh its dry weight marking asm0(2)
Place the test piece into the sink, and the bottom is cushioned with a cuboid test block of 40 mm × 40 mm×160 mm(3)
Add water to the tank to 20 mm, and maintain a constant water temperature and 90% humidity(4)
Take the test piece out after immersion for 48 h, wipe the moisture on the surface with a wrung-out wet cloth, and weigh its wet weight marking asm1(5)
Calculate the water absorption rate of the test piece usingW = (m1 − m0)/m0Additionally, we conducted a uniaxial compression test. The compressive test is carried out on the test pieces after a specified time period, and the compressive strength of the specimens is obtained according to the following formula:(4)ηSTR=100×fhealedfinitial,where ηSTR is the strength repair rate (%); fhealed is the compressive strength after curing (Pa); and finitial is the compressive strength without curing (Pa).


## 2.1. Selection of Wall Materials

In the preparation of microbial capsules, in order to achieve the best results, the wall material needs to meet specific requirements. First, to prevent the core material from oxidizing and volatilizing during storage, the wall material needs to have good airtightness. Meanwhile, the wall material must have a specific mechanical strength to ensure the isolation and protection of the core material. The wall material also needs to have suitable brittleness to guarantee that the core material can be released typically when the triggering condition is reached.On the other hand, in the preparation of microbial capsules, attention should be paid to the adverse effects of concrete conditions on microorganisms. In other words, we should prevent outside air, moisture, and oxygen from entering the microbial capsules to cause spores to germinate in advance. Furthermore, the wall material needs to be biocompatible and low in toxicity to maintain the activity of the core material.Epoxy resin is not only dense, waterproof, and mechanically robust and brittle but also nontoxic and has excellent biocompatibility. Therefore, in all aspects, this paper chooses epoxy resin E-51 as the wall material.Table1 shows the experimental instruments. This paper utilized the ultraclean workbench and Chinese medicine pellet machine for the preparation of bacterial core material. Meanwhile, we used a digital constant temperature water bath and drying box to complete the wall material to cover the core material. We observed the microbial capsule’s core-wall structure with an optical microscope and the absorption peak in the infrared spectrum of the microbial capsule by Fourier transform infrared spectroscopy. Additionally, a television microscope was used to explore the waterproofness, storage stability, and rupture ability under the pressure of the microbial capsules. The survival rate of the spores was measured using the biochemistry incubators.Table 1
Experimental instruments.
Experimental instrumentsModelManufacturerElectronic balanceBSA223SSartorius Instrument Co., LtdTelevision microscopeSA3300Beijing Tech Instrument Co., LtdDigital constant speed electric mixerJJ-1AJintan Hongye Experimental Instrument FactoryDigital constant temperature water bathHH-1Changzhou Jintan Kexing Instrument FactoryElectric blast drying boxModel 101Beijing Ever Bright Medical Treatment Instrument Co., LtdChinese medicine pellet machineHBZ-201Ruian Hanbo Electromechanical Co., LtdFourier transform infrared spectrometerNICOLET380Thermo Nicolet Co., LtdPowder tablet pressPC-24Tianjin JingTuo Instrument Technology Co., LtdBiochemical incubatorHPX-80Shanghai Hengyue Medical Equipment Co., Ltd


## 2.2. Selection of Core Materials

The microbial capsule core must be a microorganism with life activity and mineralization. Microbial mineralization types fall into two types: microbial-controlled mineralization and microbial-induced mineralization. Microbial-controlled mineralization depends on the physiological processes of microorganisms and has nothing to do with changes in the external environment, while microbial-induced mineralization is produced by activities such as cell metabolism.This research selectsBacillus pasteurii as the core microbe that adopts the microbially induced mineralization. More specifically, we make microbes into dry spore powder and mix the powder with the required nutrients and auxiliary materials such as microcrystalline cellulose to make core particles. Meanwhile, we induce calcium carbonate by cell metabolism to self-repair the concrete.


## 2.3. Measurement of Curing Agent Effect

To explore the effect of the curing agent, the epoxy resin E-51 was precured separately in advance with three curing agents: 2,4,6-trisphenol (DMP-30), m-xylylenediamine (MXDA), and silane coupling agent (KH-151). The amount of the curing agent MXDA is usually calculated based on the active hydrogen equivalent of the amine curing agent. Figure1 illustrates the structural formula of MXDA.Figure 1
The structure formula of MXDA.The molecular weight of MXDA is 136.19, and the number of active hydrogens is four. Accordingly, its active hydrogen equivalent is 34.05. The epoxy value of epoxy resin E-51 is 0.51, and the theoretical amount of MXDA is 17.37 g per 100 g of epoxy resin E-51. Its calculation formula is shown as follows:(1)W=MN×E,where W is the amount of curing agent required per 100 g of epoxy resin E-51, M is the molecular weight of MXDA, N is the number of active hydrogens of MXDA, and E is the epoxy value of the epoxy resin.The amounts of curing agents DMP-30 and KH-151 were added according to empirical values. That is, the amount of DMP-30 is 10 g per 100 g of epoxy resin E-51, and the amount of KH-151 is 15 g.In order to determine the curing effect, we placed 20 g of epoxy resin E-51 in a 50°C water bath for 10 minutes, diluted, and added with a curing agent. The bubbles were uniformly discharged after we stirred it, and we then placed it in a water bath for heat preservation. Afterward, we placed it in a beaker and observed the curing phenomenon. Table2 shows the control experiments.Table 2
Control experiments.
NumberExperimental conditionsCuring agentsWater bath temperature °CDuration of heat preservation minCuring agent amount g1DMP-30501022MXDA50103.53KH-151501034DMP-30201025MXDA20103.56KH-15120103


## 2.4. Microbial Capsule Preparation

### 2.4.1. Core Material Preparation

The microcapsule core material is prepared by mixing dry spore powder, auxiliary materials, and nutrients and then granulating by a granulation apparatus that is shown in Figure2. The specific preparation method is as follows:Step 1. Mixing stage: Weigh nutrients according to the proportion of the medium components of the optimized strains, i.e., weigh 1 g of urea, 0.25 g of soy peptone, 0.75 g of casein, and 0.25 g of sodium chloride. Add 50 g of microcrystalline cellulose for expanding the core volume and 1.5 g of hydroxypropyl methylcellulose to promote adhesion of microcrystalline cellulose to spores and nutrients.Step 2. Grouping stage: Weigh 0.5 g of dry spore powder in a beaker and add 150 g of distilled water to stir. Add the liquid solution to the mixture and stir to form a paste.Step 3. Granulation stage: Place the obtained paste from the previous step in the extrusion port of the Chinese medicine pelletizing machine and obtain a flat body after being extruded appropriately. Take out the flat body and place it at the mouth of the purlin to obtain a strip. The strips are separated into individual pieces and placed at the pellet opening to roll out the granules. Place the pellets in a rounder, take out, and dry in a low-temperature drying oven at 40°C for 24 hours. Finally, we obtain core particles with single-particle size.Figure 2
Core material granulation.The flowchart of preparing the core material is shown in Figure3. The nutrients contain urea, soy peptone, casein, and sodium chloride; and the auxiliary materials encompass microcrystalline cellulose and hydroxypropyl methylcellulose.Figure 3
The flowchart of preparing the core materials.


### 2.4.2. Single-Factor Experiments Design

A variety of factors may affect the preparation of microbial capsules, such as reaction time, reaction temperature, core-wall ratio, and agitation rate. This experiment uses a single-factor experiment to determine the optimal preparation conditions for microbial capsules. Table3 lists the experimental parameters.Table 3
Single-factor experiment parameters.
NumberFactorsCore-wall ratioTemperature °CReaction timeAgitation rate11 : 1504030021 : 2504030031 : 3504030041 : 4504030051 : 3404030061 : 3504030071 : 3604030081 : 3503030091 : 35040300101 : 35050300111 : 35040250121 : 35040300131 : 35040350


### 2.4.3. Preparing the Microbial Capsule

We use the oil-phase isolation method to prepare microbial capsules, thus avoiding the contact of the core material with water during the preparation process, thereby maintaining the stability of the spores. Epoxy resin E-51 is a hydrophobic substance, which guarantees the feasibility of the experiment. The prepared core material particles were coated with epoxy resin E-51, and the epoxy resin E-51 was solidified on the surface of the core material to form a microbial capsule under the condition of a double oil phase. The specific preparation method is as follows:Step 1. Mixing the wall and core materials: Weigh Epoxy resin E-51 and core particles according to a core-wall ratio. Place both in a beaker and mix to mix well. Place the mixture in a constant temperature water bath and keep for 10 min.Step 2. Precuring stage: After 10 min of incubation, add the curing agent to the mixture, stir well, and place in a water bath for precuring for 30 min.Step 3. Film-forming stage: Add the mixture slowly to a three-necked flask, and set the reaction temperature and stirring speed. After 5 minutes, open the stopper on one side, slowly pour in the polydimethylsiloxane oil, and continue to stir for 1 hour.After the curing was completed, take out the final product, filter with absolute ethanol, and wash the surface of the polydimethylsiloxane. Place the product in a Petri dish and transfer to a low-temperature drying oven at 40°C. As such, we obtain the microbial capsule. Figure4 demonstrates the flowchart of the preparation.Figure 4
The preparing flowchart.


## 2.4.1. Core Material Preparation

The microcapsule core material is prepared by mixing dry spore powder, auxiliary materials, and nutrients and then granulating by a granulation apparatus that is shown in Figure2. The specific preparation method is as follows:Step 1. Mixing stage: Weigh nutrients according to the proportion of the medium components of the optimized strains, i.e., weigh 1 g of urea, 0.25 g of soy peptone, 0.75 g of casein, and 0.25 g of sodium chloride. Add 50 g of microcrystalline cellulose for expanding the core volume and 1.5 g of hydroxypropyl methylcellulose to promote adhesion of microcrystalline cellulose to spores and nutrients.Step 2. Grouping stage: Weigh 0.5 g of dry spore powder in a beaker and add 150 g of distilled water to stir. Add the liquid solution to the mixture and stir to form a paste.Step 3. Granulation stage: Place the obtained paste from the previous step in the extrusion port of the Chinese medicine pelletizing machine and obtain a flat body after being extruded appropriately. Take out the flat body and place it at the mouth of the purlin to obtain a strip. The strips are separated into individual pieces and placed at the pellet opening to roll out the granules. Place the pellets in a rounder, take out, and dry in a low-temperature drying oven at 40°C for 24 hours. Finally, we obtain core particles with single-particle size.Figure 2
Core material granulation.The flowchart of preparing the core material is shown in Figure3. The nutrients contain urea, soy peptone, casein, and sodium chloride; and the auxiliary materials encompass microcrystalline cellulose and hydroxypropyl methylcellulose.Figure 3
The flowchart of preparing the core materials.


## 2.4.2. Single-Factor Experiments Design

A variety of factors may affect the preparation of microbial capsules, such as reaction time, reaction temperature, core-wall ratio, and agitation rate. This experiment uses a single-factor experiment to determine the optimal preparation conditions for microbial capsules. Table3 lists the experimental parameters.Table 3
Single-factor experiment parameters.
NumberFactorsCore-wall ratioTemperature °CReaction timeAgitation rate11 : 1504030021 : 2504030031 : 3504030041 : 4504030051 : 3404030061 : 3504030071 : 3604030081 : 3503030091 : 35040300101 : 35050300111 : 35040250121 : 35040300131 : 35040350


## 2.4.3. Preparing the Microbial Capsule

We use the oil-phase isolation method to prepare microbial capsules, thus avoiding the contact of the core material with water during the preparation process, thereby maintaining the stability of the spores. Epoxy resin E-51 is a hydrophobic substance, which guarantees the feasibility of the experiment. The prepared core material particles were coated with epoxy resin E-51, and the epoxy resin E-51 was solidified on the surface of the core material to form a microbial capsule under the condition of a double oil phase. The specific preparation method is as follows:Step 1. Mixing the wall and core materials: Weigh Epoxy resin E-51 and core particles according to a core-wall ratio. Place both in a beaker and mix to mix well. Place the mixture in a constant temperature water bath and keep for 10 min.Step 2. Precuring stage: After 10 min of incubation, add the curing agent to the mixture, stir well, and place in a water bath for precuring for 30 min.Step 3. Film-forming stage: Add the mixture slowly to a three-necked flask, and set the reaction temperature and stirring speed. After 5 minutes, open the stopper on one side, slowly pour in the polydimethylsiloxane oil, and continue to stir for 1 hour.After the curing was completed, take out the final product, filter with absolute ethanol, and wash the surface of the polydimethylsiloxane. Place the product in a Petri dish and transfer to a low-temperature drying oven at 40°C. As such, we obtain the microbial capsule. Figure4 demonstrates the flowchart of the preparation.Figure 4
The preparing flowchart.


## 2.5. Features of the Microbial Capsules

### 2.5.1. Waterproofness

Randomly select a plurality of microbial capsules in a beaker, slowly add distilled water to thoroughly soak the microbial capsules, and record the soaking time of the microbial capsules. Take 5–7 microbial capsules every other day, blot the surface moisture with absorbent paper, and place them on a glass slide. Place the slide under a microscope and adjust the magnification of the microscope to observe the presence or absence of cracks.


### 2.5.2. Storage Stability

Weigh specific amounts of microbial capsules in a Petri dish and place the Petri dish on a dry and ventilated bench. Record the initial weight of the microbial capsule and the weight of the microbial capsules on the 3rd, 6th, 9th, 12th, and 15th days. Observe the mass loss of the microbial capsules, and calculate the mass loss rate based on the following formula:(2)M=m0−mim0×100%,where m0 and mi are the last and the current weight (g).


### 2.5.3. Rupture Ability under Trigger Condition

Randomly select plurality of microbial capsules, place them on a laboratory bench, and fracture them with tweezers. Place the fractured microbial capsules under a microscope, and fix the magnification to observe the rupture of the surface of the microbial capsule. In this way, we can judge whether the mechanical properties of the microbial capsules can be triggered and further germinate the microorganisms to conduct the self-repairing process when the concrete where they are buried ruptures.


### 2.5.4. Spore Survival Rate

We employ the plate colony-counting method to determine the spore survival rate of microbial capsules. First, ground the microbial capsule into a powder, add to the liquid medium, and shake well. Then, use a pipette to extract 1 ml of the mixture, slowly inject into a tube containing 9 ml of the liquid medium along the tube wall, and shake the tube to mix well. Repeat the above procedure and replace the sterile pipette once every dilution until it is diluted to 1 × 108 times.Pipet 100μL of the diluted liquid, pour into a solid medium prepared in advance, and then uniformly distribute the colonies on the plate. After solidification, turn over the culture dish and place in an incubator for 24 hours. Observe the germination of the spores in the culture dish and count the number of colonies in the culture dish. It should be noted that at the dilution factor at this time, one colony represents one spore in the microbial capsule. The spore germination rate is obtained according to the number of colonies at the dilution factor and the number of spores in the core material.


## 2.5.1. Waterproofness

Randomly select a plurality of microbial capsules in a beaker, slowly add distilled water to thoroughly soak the microbial capsules, and record the soaking time of the microbial capsules. Take 5–7 microbial capsules every other day, blot the surface moisture with absorbent paper, and place them on a glass slide. Place the slide under a microscope and adjust the magnification of the microscope to observe the presence or absence of cracks.


## 2.5.2. Storage Stability

Weigh specific amounts of microbial capsules in a Petri dish and place the Petri dish on a dry and ventilated bench. Record the initial weight of the microbial capsule and the weight of the microbial capsules on the 3rd, 6th, 9th, 12th, and 15th days. Observe the mass loss of the microbial capsules, and calculate the mass loss rate based on the following formula:(2)M=m0−mim0×100%,where m0 and mi are the last and the current weight (g).


## 2.5.3. Rupture Ability under Trigger Condition

Randomly select plurality of microbial capsules, place them on a laboratory bench, and fracture them with tweezers. Place the fractured microbial capsules under a microscope, and fix the magnification to observe the rupture of the surface of the microbial capsule. In this way, we can judge whether the mechanical properties of the microbial capsules can be triggered and further germinate the microorganisms to conduct the self-repairing process when the concrete where they are buried ruptures.


## 2.5.4. Spore Survival Rate

We employ the plate colony-counting method to determine the spore survival rate of microbial capsules. First, ground the microbial capsule into a powder, add to the liquid medium, and shake well. Then, use a pipette to extract 1 ml of the mixture, slowly inject into a tube containing 9 ml of the liquid medium along the tube wall, and shake the tube to mix well. Repeat the above procedure and replace the sterile pipette once every dilution until it is diluted to 1 × 108 times.Pipet 100μL of the diluted liquid, pour into a solid medium prepared in advance, and then uniformly distribute the colonies on the plate. After solidification, turn over the culture dish and place in an incubator for 24 hours. Observe the germination of the spores in the culture dish and count the number of colonies in the culture dish. It should be noted that at the dilution factor at this time, one colony represents one spore in the microbial capsule. The spore germination rate is obtained according to the number of colonies at the dilution factor and the number of spores in the core material.


## 2.6. Verification of Self-Healing Effect of Microbial Capsules

### 2.6.1. Test Pieces Preparation

Table4 lists the specific mixing ratio of the experimental test pieces. Figure 5 shows the preparation of self-healing test piece. We designed three sets of control experiments. Specifically, Group A is a standard test piece without adding any repair agent. Group B only adds the core material part from the repair agent, that is, the bacterial body. Group C adds the complete microbial capsule. Meanwhile, the cement mortar has a water-cement ratio of 0.3. The amount of the repair agent is 3.0% of the amount of the cementing material. Besides, the mold uses a cylindrical test piece with φ of 50 mm and H of 100 mm.Table 4
Material ratios.
GroupsCement (g)Sand (g)Water (g)Repair agent1270810270N/A2270810270Bacterial body3270810270Microbial capsuleFigure 5
Preparation of self-healing testing pieces.The specific preparation steps are as follows:(1)
Weigh the required materials according to the required amount, add cement, sand, and water in sequence, mix well, and finally add the microcapsules and mix well.(2)
Brush a layer of grease on the inside of the mold, pour the evenly mixed mixture into the mold, and shake it up.(3)
After leaving the mixture at room temperature for one day, demold. Then, put it in a standard constant temperature and humidity curing box (temperature 25°C; air humidity 90%), and stay until a specific time.


### 2.6.2. Prefabricating Crack for Test Pieces

This paper took the cement mortar test pieces within the curing period and manually prefabricated cracks. Based on a comprehensive analysis of various prefabricated cracking methods, this paper adopted a universal pressure testing machine to prefabricate cracks for cylindrical specimens, as shown in Figure6. The specific steps are as follows:(1)
Place the test piece in the center of the pressure-bearing plate of the testing machine, and adjust the bottom disc to a balanced state.(2)
Apply the axial stress at a displacement speed of 0.01 mm/min, and prefabricate the crack using a concentrated load in the center.(3)
When the obvious cracking sound occurs, stop the pressurization. By then, we can obtain a striped crack that diverges from the center of the test piece to the surroundings.(4)
Record the failure load and calculate the compressive strength according to the following formula:(3)f=FA,wheref is the compressive strength of cubes of similar rock text pieces (MPa); F is the failure load of the test piece (N); A is the pressure area of the test piece (mm2).(5)
Record the stress-strain curve and the test force-deformation curve, and analyze the uniaxial compression curve of the test piece.Figure 6
Microcomputer-controlled electro-hydraulic servo universal testing machine.


### 2.6.3. Curing of Test Pieces

During the self-repair experiment, there is an exchange of substances and energy, which demands the participation of microorganisms embedded in the test piece in advance. This process requires an effective medium to assist in energy exchange and material transportation. This test used the water curing method. Specifically, the cracked test pieces were immersed in the tap water, the cracked surface and the liquid surface were kept vertical, and the water temperature was adjusted to 25°C.


### 2.6.4. Assessment of Self-Healing Performance

To evaluate the self-healing performance, we first conducted a water absorption test. The water absorption rate of the test pieces can reflect the weathering resistance and frost resistance. The water absorption rate depends on the number, size, and degree of cracks contained in the test piece. Water absorption can effectively reflect the degree of development of cracks and voids in the text pieces, so it is an important indicator to evaluate the nature of the test pieces. The steps for testing the water absorption of cement mortar test pieces are as follows:(1)
Set the temperature of the drying box to 75°C, and after drying for 48 h, weigh its dry weight marking asm0(2)
Place the test piece into the sink, and the bottom is cushioned with a cuboid test block of 40 mm × 40 mm×160 mm(3)
Add water to the tank to 20 mm, and maintain a constant water temperature and 90% humidity(4)
Take the test piece out after immersion for 48 h, wipe the moisture on the surface with a wrung-out wet cloth, and weigh its wet weight marking asm1(5)
Calculate the water absorption rate of the test piece usingW = (m1 − m0)/m0Additionally, we conducted a uniaxial compression test. The compressive test is carried out on the test pieces after a specified time period, and the compressive strength of the specimens is obtained according to the following formula:(4)ηSTR=100×fhealedfinitial,where ηSTR is the strength repair rate (%); fhealed is the compressive strength after curing (Pa); and finitial is the compressive strength without curing (Pa).


## 2.6.1. Test Pieces Preparation

Table4 lists the specific mixing ratio of the experimental test pieces. Figure 5 shows the preparation of self-healing test piece. We designed three sets of control experiments. Specifically, Group A is a standard test piece without adding any repair agent. Group B only adds the core material part from the repair agent, that is, the bacterial body. Group C adds the complete microbial capsule. Meanwhile, the cement mortar has a water-cement ratio of 0.3. The amount of the repair agent is 3.0% of the amount of the cementing material. Besides, the mold uses a cylindrical test piece with φ of 50 mm and H of 100 mm.Table 4
Material ratios.
GroupsCement (g)Sand (g)Water (g)Repair agent1270810270N/A2270810270Bacterial body3270810270Microbial capsuleFigure 5
Preparation of self-healing testing pieces.The specific preparation steps are as follows:(1)
Weigh the required materials according to the required amount, add cement, sand, and water in sequence, mix well, and finally add the microcapsules and mix well.(2)
Brush a layer of grease on the inside of the mold, pour the evenly mixed mixture into the mold, and shake it up.(3)
After leaving the mixture at room temperature for one day, demold. Then, put it in a standard constant temperature and humidity curing box (temperature 25°C; air humidity 90%), and stay until a specific time.


## 2.6.2. Prefabricating Crack for Test Pieces

This paper took the cement mortar test pieces within the curing period and manually prefabricated cracks. Based on a comprehensive analysis of various prefabricated cracking methods, this paper adopted a universal pressure testing machine to prefabricate cracks for cylindrical specimens, as shown in Figure6. The specific steps are as follows:(1)
Place the test piece in the center of the pressure-bearing plate of the testing machine, and adjust the bottom disc to a balanced state.(2)
Apply the axial stress at a displacement speed of 0.01 mm/min, and prefabricate the crack using a concentrated load in the center.(3)
When the obvious cracking sound occurs, stop the pressurization. By then, we can obtain a striped crack that diverges from the center of the test piece to the surroundings.(4)
Record the failure load and calculate the compressive strength according to the following formula:(3)f=FA,wheref is the compressive strength of cubes of similar rock text pieces (MPa); F is the failure load of the test piece (N); A is the pressure area of the test piece (mm2).(5)
Record the stress-strain curve and the test force-deformation curve, and analyze the uniaxial compression curve of the test piece.Figure 6
Microcomputer-controlled electro-hydraulic servo universal testing machine.


## 2.6.3. Curing of Test Pieces

During the self-repair experiment, there is an exchange of substances and energy, which demands the participation of microorganisms embedded in the test piece in advance. This process requires an effective medium to assist in energy exchange and material transportation. This test used the water curing method. Specifically, the cracked test pieces were immersed in the tap water, the cracked surface and the liquid surface were kept vertical, and the water temperature was adjusted to 25°C.


## 2.6.4. Assessment of Self-Healing Performance

To evaluate the self-healing performance, we first conducted a water absorption test. The water absorption rate of the test pieces can reflect the weathering resistance and frost resistance. The water absorption rate depends on the number, size, and degree of cracks contained in the test piece. Water absorption can effectively reflect the degree of development of cracks and voids in the text pieces, so it is an important indicator to evaluate the nature of the test pieces. The steps for testing the water absorption of cement mortar test pieces are as follows:(1)
Set the temperature of the drying box to 75°C, and after drying for 48 h, weigh its dry weight marking asm0(2)
Place the test piece into the sink, and the bottom is cushioned with a cuboid test block of 40 mm × 40 mm×160 mm(3)
Add water to the tank to 20 mm, and maintain a constant water temperature and 90% humidity(4)
Take the test piece out after immersion for 48 h, wipe the moisture on the surface with a wrung-out wet cloth, and weigh its wet weight marking asm1(5)
Calculate the water absorption rate of the test piece usingW = (m1 − m0)/m0Additionally, we conducted a uniaxial compression test. The compressive test is carried out on the test pieces after a specified time period, and the compressive strength of the specimens is obtained according to the following formula:(4)ηSTR=100×fhealedfinitial,where ηSTR is the strength repair rate (%); fhealed is the compressive strength after curing (Pa); and finitial is the compressive strength without curing (Pa).


## 3. Results and Discussion

### 3.1. Curing Effects of the Wall Material

Precuring of epoxy resin E-51 was carried out according to a control experiment (Table3). The experiment shows that the curing reaction accelerates with the increase in the temperature of the water bath; and when the temperature of the water bath reaches 50°C, the curing reaction is the fastest.Under the same conditions, changing the curing agent, we found that the curing agent DMP-30 can completely cure the epoxy resin E-51 after 30 minutes. In contrast, the time required for the curing agent MXDA to fully cure the epoxy resin E-51 was about two hours, while the KH-151 did not have a curing effect on the epoxy resin E-51. Table5 shows the properties of the cured product.Table 5
The properties of the cured products under various curing agents.
NumberCuring agentAmount of curing agent (g)Curing products properties1DMP-302Orange, fragile2MXDA3.5Light yellow, a little fragile3KH-1513Transparent, no curing effectFrom the comparison of the physical properties of the cured products and the curing reaction time, it is concluded that the curing agent DMP-30 has the best curing effect. Moreover, the spore survival rate and mechanical triggering performance of DMP-30 prepared microbial capsules are the best.


### 3.2. Preparation of the Core Material

The spore dry powder, auxiliary materials, and nutrients are uniformly mixed, and the core material particles required for the experiment are obtained by stripping, extruding, pelletizing, and rounding, as shown in Figure7. Figure 7(a) shows that the prepared core material particles are pure white before dried, have a large particle size, and are easily crushed by pressing. Figure 7(b) shows that the particle size of the prepared core material is significantly reduced after drying. This is because the added microcrystalline cellulose and HPMC have good water swell ability.Figure 7
Particles of the core material: (a) particles before dried; (b) particles after dried.The color of the core material particles changes from white to pale yellow due to the residual suspension in the added spore dry powder (as shown in Figure8). Currently, the texture of the core material particles is hard, and the pressing does not break, which ensures the integrity of the core material particles in the process of preparing the microbial capsule.Figure 8
Dried spore powder after centrifugation and drying.


### 3.3. Impact of Single Factor on Microbial Capsule Preparation

#### 3.3.1. Reaction Temperature

The temperature can change the viscosity of Epoxy E-51. Specifically, as the reaction temperature increases, the viscosity gradually decreases. At the same time, different curing agents require different curing temperatures, and the properties of the cured products formed are also different. Epoxy resins cure at low temperature, and it has the best overall performance.The results of single-factor experiments showed that the epoxy resin coated on the surface of the microbial capsule became more slippery, and the wall became thicker as the reaction temperature increased. However, when the experimental temperature reached 60°C, the precured mixture appeared to unite in the three-necked flask, and the microbial capsules showed agglomeration. Since the activity of theBacillus pasteurii used in the core material is not suitable for excessively high temperature, the optimum temperature for the experiment is 50°C.


#### 3.3.2. Reaction Time

In order to explore the effect of reaction time on the experiment, we keep the other factors unchanged and only change the reaction time to experiment. The experimental results show that the influence of reaction time on the preparation of microbial capsules is like the reaction temperature. That is, when the reaction time gradually increases, the coating effect on the surface of the core material is getting better and better, and the thickness of the wall material also gradually increases. Similarly, the precured mixture also exhibits agglomeration. The experimental results reveal that the optimal reaction time is 40 min.


#### 3.3.3. Core-Wall Ratio

Among the influencing factors of microbial capsules, the influence of core-wall ratio is the most significant. The core-wall plays an essential role in the wall thickness and particle size of the microbial capsule, thereby affecting its waterproof performance. This is because the difference in core-wall content directly affects the content of the wall material coated on the surface of the core material. In this experiment, the core-to-wall ratio was set to 1 : 1, 1 : 2, 1 : 3, and 1 : 4, respectively, to explore the effect of this factor on the experimental results.In the experiment, we prepared microbial capsules according to different core-wall ratios to observe changes in wall thickness values. The experimental results are shown in Figure9. The thickness of the wall material gradually increases as the core-wall ratio decreases, but when the core-wall ratio is greater than 1 : 3, the thickness increase of the wall material begins to decrease. This is because, at the lower core-wall ratio, the wall material content is higher than the core material content, the more the wall material can be coated by the core material, the thicker the wall material thickness. However, when the core-wall ratio reaches a specific value, the increase in the thickness of the wall material will slow down. In other words, the wall material content has begun to generate a residual amount concerning the core material content, and the utilization rate of the wall material starts to decrease. Considering the thickness of the wall material and its utilization, we set the optimum wall-core ratio as 3 : 1.Figure 9
The trend of wall thickness with respect to various wall-core ratios.


#### 3.3.4. Agitation Rate

We prepared microbial capsules at an agitation rate of 250 rpm, 300 rpm, and 350 rpm, respectively. From the prepared microbial capsules, we found that the thickness of the microbial capsule wall material decreased with the gradual increase in the rotational speed until it approached the particle size of the core material particles. This is because as the rotational speed increases, the shear stress of the agitator is higher than the viscous force of the epoxy resin so that the epoxy resin coated on the surface of the core material is peeled off under high-speed rotation. Meanwhile, under high-speed rotation, some core material particles are broken, which is not conducive to the survival ofBacillus pasteurii. Taken together, we set the best experimental speed as 300 rpm.


### 3.4. The Structure Feature of the Microbial Capsule

#### 3.4.1. Structure Feature

Figure10 illustrates a microbial capsule under an optical microscope. Figure 10(a) is a full picture of the microbial capsule. The core is oval in the center, and the core material is epoxy E-51. Figure 10(b) is a partial view of the microbial capsule, i.e., the core-wall structure of the microbial capsule. As can be seen from the picture, the surface of the core material particles is rough, entirely covered by the solidified epoxy resin of the wall material. Meanwhile, the inside is crystallized, and the surface of the wall material of the microbial capsule is slightly smooth and flat.Figure 10
A microbial capsule under an optical microscope: (a) full picture of the microbial capsule; (b) partial view of the microbial capsule.
(a)(b)


#### 3.4.2. Fourier Transform Infrared Spectroscopy

Use the Fourier transform infrared spectrometer to characterize the chemical structure of the microbial capsules. Mix the dried microbial capsule sample with potassium bromide in proportion and uniformly place it in a mortar. Slowly ground until it is ground into a powder and place it in a tableting machine for tableting. Place the sheet in an experimental apparatus for scan and analysis.The epoxy resin E-51 selected in this experiment belongs to bisphenol A type epoxy resin. This type of epoxy resin has an aromatic hydrocarbon structure, which produces a richer infrared spectrum. Figure11 illustrates the FTIR spectrum of the microbial capsule. At 830 cm−1 and 915 cm−1, they are characteristic absorption peaks of epoxy resin E-51. Specifically, at 830 cm−1, it is the absorption band of two adjacent hydrogen atoms on the benzene ring; and at 915 cm−1, it belongs to the characteristic absorption band of the epoxy group. The characteristic peak produced by absorption of the aliphatic ether bond C-O-C appears at 1040 cm−1. The characteristic peak of phenyl ether occurs at 1250 cm−1.Figure 11
The FTIR spectrum of the microbial capsule.


### 3.5. The Performance of Microbial Capsules

#### 3.5.1. Waterproofness

In the experiment, we chose microcrystalline cellulose to expand the volume of the core material and used hydroxypropyl methylcellulose as a binder to promote the fusion of dry spore powder, nutrients, and microcrystalline cellulose. These two substances are insoluble in water and have good water swell ability, and the volume of the core material expands after water absorption, thereby causing the wall material to rupture. Therefore, we can judge the waterproofness of the wall material according to this feature. We adopted an optical microscope to observe the surface of the microbial capsule, as shown in Figure12. The figure clearly shows that the surface of the microbial capsule has no cracks, so the moisture does not penetrate the inside of the core material. In other words, the wall epoxy resin E-51 has excellent water resistance.Figure 12
The waterproofness of microbial capsule.


#### 3.5.2. Storage Stability

Obtain 20 g of microbial capsules with single-particle size and weigh the mass on day 3, 6, 9, 12, 15, and 18. The results are shown in Table6.Table 6
The measurement of stability of microbial capsule.
Mass and lossDaysDay 0Day 3Day 6Day 9Day 12Day 15Day 18Mass20 g19.884 g19.797 g19.762 g19.753 g19.747 g19.740 gMass loss—0.6%0.4%0.17%0.04%0.03%0.03%Figure13 shows the quality of microbial capsules over time. As can be seen from the figure, the mass loss of the microbial capsule was significant in the first six days. As time goes by, the reduction of microbial capsule quality gradually stabilized, and the quality of microbial capsules did not decrease significantly in the later stage. This indicates that the microbial capsule will not drop after losing a small amount of mass, i.e., the microbial capsule has excellent storage stability.Figure 13
The mass trend of the microbial capsule.


#### 3.5.3. Rupture Ability under Trigger Condition

Slowly fracture the microbial capsule with forceps and place it under an optical microscope for observation. Figure14 displays an image of the ruptured portion under an optical microscope after the microcapsule breaks. Figure 14(a) shows the broken wall material after the microbial capsules are fractured, showing that the cracked part is smooth and transparent. Figure 14(b) reveals the core material after fracturing, showing an opaque black state, and the surface is not covered with a transparent ring. As can be seen from the figure, the core material and the wall material can be separated under pressure.Figure 14
The fracture figure of the microbial capsule under pressure: (a) broken wall material; (b) core material.
(a)(b)As described above, after the microcapsule capsule breaks, the core material and the wall material will separate. When the microbial capsule is buried in the concrete and the concrete cracks, the pressure is generated inside to cause the microcapsule to rupture and expose the core material. The core material is then in contact with moisture and oxygen to initiate germination, initiate cell metabolism, and produce calcium carbonate for self-healing.


#### 3.5.4. Spore Survival Rate

Figure15 illustrates the rupture of the microbial capsule under pressure after 24 h of incubation.Figure 15
The rupture figure of the microbial capsule under pressure.As can be seen from the figure, round white colony spots appear on the surface of the culture dish, and the number of colonies and diameters vary. After statistics, the average number of colonies per dish was 40. That is, after 1 × 108 times dilution, the survival spores in the microbial capsule were 4 × 109 cfu/ml.According to the core-wall ratio, 4 × 109 cfu/ml was converted to 5.33 × 109 cfu/ml of the spore survival per gram of core material in the microbial capsule. The spore survival per gram of the core material before preparation of the microbial capsule was 8 × 109 cfu/ml. Thus, the spore survival rate in the microbial capsule was 66.7%.After the preparation of the core material and the microbial capsule, theBacillus pasteurii remains active. The selected wall material has excellent biocompatibility with the spores, thus ensuring that the microbial capsule can be self-repaired when being embedded in the concrete.


### 3.6. Experimental Analysis of Self-Healing Performance

#### 3.6.1. Analysis of Water Absorption Test

In the mortar test piece, the calcium carbonate precipitate generated by microbial mineralization binds the sand particles and effectively fills the pores of the mortar test piece. Consequently, the porosity is reduced to a certain extent, and the water absorption of the test piece reduces accordingly. The change trend of water absorption of the test piece with time is shown in Figure16.Figure 16
Water absorption ratio of test pieces under various microbial capsule amounts.As shown in the figure, with a fixed water-to-binder ratio, the water absorption rate of the cement mortar test pieces showed a downward trend with the extension of the curing age. This is due to the continuous increase in hydration products caused by microbial reactions, resulting in a tighter internal structure of the mortar. In addition, the addition of microbial capsules increased the water absorption of the mortar test piece, and the water absorption rate of the test piece showed an upward trend as the number of microbial capsules increased. Since the density of the microcapsules is relatively low, the density of the cement mortar test pieces also decreases with the increase in the microcapsule content, resulting in an increase in the internal porosity of the test pieces.


#### 3.6.2. Analysis of Uniaxial Compression Test

Table7 shows the compressive strength of the three groups of test pieces. The compressive strength of group A increased with the extension of maintenance age (48 days). The compressive strength of Group B was higher than that of standard test pieces in the initial stage of curing, but there was no significant change in the overall situation. When bacteria were added, the CO2 hydration reaction in the crack area was accelerated. However, because the cement-based material is more alkaline and the bacteria have poor tolerance, the survival time inside the test pieces became shorter. With the increase in the curing time, few bacteria survived. To sum up, the compression resistance of Group C is significantly improved compared with that of the other two groups. Using epoxy resin as the wall material can achieve long-term survival of bacteria in cement-based materials.Table 7
Comparison of compression strength under various curing ages.
Repair agentStrength (MPa)3(d)5(d)7(d)N/A2.3112.4322.517Bacterial body2.4362.3172.336Microbial capsule2.3162.4252.618


## 3.1. Curing Effects of the Wall Material

Precuring of epoxy resin E-51 was carried out according to a control experiment (Table3). The experiment shows that the curing reaction accelerates with the increase in the temperature of the water bath; and when the temperature of the water bath reaches 50°C, the curing reaction is the fastest.Under the same conditions, changing the curing agent, we found that the curing agent DMP-30 can completely cure the epoxy resin E-51 after 30 minutes. In contrast, the time required for the curing agent MXDA to fully cure the epoxy resin E-51 was about two hours, while the KH-151 did not have a curing effect on the epoxy resin E-51. Table5 shows the properties of the cured product.Table 5
The properties of the cured products under various curing agents.
NumberCuring agentAmount of curing agent (g)Curing products properties1DMP-302Orange, fragile2MXDA3.5Light yellow, a little fragile3KH-1513Transparent, no curing effectFrom the comparison of the physical properties of the cured products and the curing reaction time, it is concluded that the curing agent DMP-30 has the best curing effect. Moreover, the spore survival rate and mechanical triggering performance of DMP-30 prepared microbial capsules are the best.


## 3.2. Preparation of the Core Material

The spore dry powder, auxiliary materials, and nutrients are uniformly mixed, and the core material particles required for the experiment are obtained by stripping, extruding, pelletizing, and rounding, as shown in Figure7. Figure 7(a) shows that the prepared core material particles are pure white before dried, have a large particle size, and are easily crushed by pressing. Figure 7(b) shows that the particle size of the prepared core material is significantly reduced after drying. This is because the added microcrystalline cellulose and HPMC have good water swell ability.Figure 7
Particles of the core material: (a) particles before dried; (b) particles after dried.The color of the core material particles changes from white to pale yellow due to the residual suspension in the added spore dry powder (as shown in Figure8). Currently, the texture of the core material particles is hard, and the pressing does not break, which ensures the integrity of the core material particles in the process of preparing the microbial capsule.Figure 8
Dried spore powder after centrifugation and drying.


## 3.3. Impact of Single Factor on Microbial Capsule Preparation

### 3.3.1. Reaction Temperature

The temperature can change the viscosity of Epoxy E-51. Specifically, as the reaction temperature increases, the viscosity gradually decreases. At the same time, different curing agents require different curing temperatures, and the properties of the cured products formed are also different. Epoxy resins cure at low temperature, and it has the best overall performance.The results of single-factor experiments showed that the epoxy resin coated on the surface of the microbial capsule became more slippery, and the wall became thicker as the reaction temperature increased. However, when the experimental temperature reached 60°C, the precured mixture appeared to unite in the three-necked flask, and the microbial capsules showed agglomeration. Since the activity of theBacillus pasteurii used in the core material is not suitable for excessively high temperature, the optimum temperature for the experiment is 50°C.


### 3.3.2. Reaction Time

In order to explore the effect of reaction time on the experiment, we keep the other factors unchanged and only change the reaction time to experiment. The experimental results show that the influence of reaction time on the preparation of microbial capsules is like the reaction temperature. That is, when the reaction time gradually increases, the coating effect on the surface of the core material is getting better and better, and the thickness of the wall material also gradually increases. Similarly, the precured mixture also exhibits agglomeration. The experimental results reveal that the optimal reaction time is 40 min.


### 3.3.3. Core-Wall Ratio

Among the influencing factors of microbial capsules, the influence of core-wall ratio is the most significant. The core-wall plays an essential role in the wall thickness and particle size of the microbial capsule, thereby affecting its waterproof performance. This is because the difference in core-wall content directly affects the content of the wall material coated on the surface of the core material. In this experiment, the core-to-wall ratio was set to 1 : 1, 1 : 2, 1 : 3, and 1 : 4, respectively, to explore the effect of this factor on the experimental results.In the experiment, we prepared microbial capsules according to different core-wall ratios to observe changes in wall thickness values. The experimental results are shown in Figure9. The thickness of the wall material gradually increases as the core-wall ratio decreases, but when the core-wall ratio is greater than 1 : 3, the thickness increase of the wall material begins to decrease. This is because, at the lower core-wall ratio, the wall material content is higher than the core material content, the more the wall material can be coated by the core material, the thicker the wall material thickness. However, when the core-wall ratio reaches a specific value, the increase in the thickness of the wall material will slow down. In other words, the wall material content has begun to generate a residual amount concerning the core material content, and the utilization rate of the wall material starts to decrease. Considering the thickness of the wall material and its utilization, we set the optimum wall-core ratio as 3 : 1.Figure 9
The trend of wall thickness with respect to various wall-core ratios.


### 3.3.4. Agitation Rate

We prepared microbial capsules at an agitation rate of 250 rpm, 300 rpm, and 350 rpm, respectively. From the prepared microbial capsules, we found that the thickness of the microbial capsule wall material decreased with the gradual increase in the rotational speed until it approached the particle size of the core material particles. This is because as the rotational speed increases, the shear stress of the agitator is higher than the viscous force of the epoxy resin so that the epoxy resin coated on the surface of the core material is peeled off under high-speed rotation. Meanwhile, under high-speed rotation, some core material particles are broken, which is not conducive to the survival ofBacillus pasteurii. Taken together, we set the best experimental speed as 300 rpm.


## 3.3.1. Reaction Temperature

The temperature can change the viscosity of Epoxy E-51. Specifically, as the reaction temperature increases, the viscosity gradually decreases. At the same time, different curing agents require different curing temperatures, and the properties of the cured products formed are also different. Epoxy resins cure at low temperature, and it has the best overall performance.The results of single-factor experiments showed that the epoxy resin coated on the surface of the microbial capsule became more slippery, and the wall became thicker as the reaction temperature increased. However, when the experimental temperature reached 60°C, the precured mixture appeared to unite in the three-necked flask, and the microbial capsules showed agglomeration. Since the activity of theBacillus pasteurii used in the core material is not suitable for excessively high temperature, the optimum temperature for the experiment is 50°C.


## 3.3.2. Reaction Time

In order to explore the effect of reaction time on the experiment, we keep the other factors unchanged and only change the reaction time to experiment. The experimental results show that the influence of reaction time on the preparation of microbial capsules is like the reaction temperature. That is, when the reaction time gradually increases, the coating effect on the surface of the core material is getting better and better, and the thickness of the wall material also gradually increases. Similarly, the precured mixture also exhibits agglomeration. The experimental results reveal that the optimal reaction time is 40 min.


## 3.3.3. Core-Wall Ratio

Among the influencing factors of microbial capsules, the influence of core-wall ratio is the most significant. The core-wall plays an essential role in the wall thickness and particle size of the microbial capsule, thereby affecting its waterproof performance. This is because the difference in core-wall content directly affects the content of the wall material coated on the surface of the core material. In this experiment, the core-to-wall ratio was set to 1 : 1, 1 : 2, 1 : 3, and 1 : 4, respectively, to explore the effect of this factor on the experimental results.In the experiment, we prepared microbial capsules according to different core-wall ratios to observe changes in wall thickness values. The experimental results are shown in Figure9. The thickness of the wall material gradually increases as the core-wall ratio decreases, but when the core-wall ratio is greater than 1 : 3, the thickness increase of the wall material begins to decrease. This is because, at the lower core-wall ratio, the wall material content is higher than the core material content, the more the wall material can be coated by the core material, the thicker the wall material thickness. However, when the core-wall ratio reaches a specific value, the increase in the thickness of the wall material will slow down. In other words, the wall material content has begun to generate a residual amount concerning the core material content, and the utilization rate of the wall material starts to decrease. Considering the thickness of the wall material and its utilization, we set the optimum wall-core ratio as 3 : 1.Figure 9
The trend of wall thickness with respect to various wall-core ratios.


## 3.3.4. Agitation Rate

We prepared microbial capsules at an agitation rate of 250 rpm, 300 rpm, and 350 rpm, respectively. From the prepared microbial capsules, we found that the thickness of the microbial capsule wall material decreased with the gradual increase in the rotational speed until it approached the particle size of the core material particles. This is because as the rotational speed increases, the shear stress of the agitator is higher than the viscous force of the epoxy resin so that the epoxy resin coated on the surface of the core material is peeled off under high-speed rotation. Meanwhile, under high-speed rotation, some core material particles are broken, which is not conducive to the survival ofBacillus pasteurii. Taken together, we set the best experimental speed as 300 rpm.


## 3.4. The Structure Feature of the Microbial Capsule

### 3.4.1. Structure Feature

Figure10 illustrates a microbial capsule under an optical microscope. Figure 10(a) is a full picture of the microbial capsule. The core is oval in the center, and the core material is epoxy E-51. Figure 10(b) is a partial view of the microbial capsule, i.e., the core-wall structure of the microbial capsule. As can be seen from the picture, the surface of the core material particles is rough, entirely covered by the solidified epoxy resin of the wall material. Meanwhile, the inside is crystallized, and the surface of the wall material of the microbial capsule is slightly smooth and flat.Figure 10
A microbial capsule under an optical microscope: (a) full picture of the microbial capsule; (b) partial view of the microbial capsule.
(a)(b)


### 3.4.2. Fourier Transform Infrared Spectroscopy

Use the Fourier transform infrared spectrometer to characterize the chemical structure of the microbial capsules. Mix the dried microbial capsule sample with potassium bromide in proportion and uniformly place it in a mortar. Slowly ground until it is ground into a powder and place it in a tableting machine for tableting. Place the sheet in an experimental apparatus for scan and analysis.The epoxy resin E-51 selected in this experiment belongs to bisphenol A type epoxy resin. This type of epoxy resin has an aromatic hydrocarbon structure, which produces a richer infrared spectrum. Figure11 illustrates the FTIR spectrum of the microbial capsule. At 830 cm−1 and 915 cm−1, they are characteristic absorption peaks of epoxy resin E-51. Specifically, at 830 cm−1, it is the absorption band of two adjacent hydrogen atoms on the benzene ring; and at 915 cm−1, it belongs to the characteristic absorption band of the epoxy group. The characteristic peak produced by absorption of the aliphatic ether bond C-O-C appears at 1040 cm−1. The characteristic peak of phenyl ether occurs at 1250 cm−1.Figure 11
The FTIR spectrum of the microbial capsule.


## 3.4.1. Structure Feature

Figure10 illustrates a microbial capsule under an optical microscope. Figure 10(a) is a full picture of the microbial capsule. The core is oval in the center, and the core material is epoxy E-51. Figure 10(b) is a partial view of the microbial capsule, i.e., the core-wall structure of the microbial capsule. As can be seen from the picture, the surface of the core material particles is rough, entirely covered by the solidified epoxy resin of the wall material. Meanwhile, the inside is crystallized, and the surface of the wall material of the microbial capsule is slightly smooth and flat.Figure 10
A microbial capsule under an optical microscope: (a) full picture of the microbial capsule; (b) partial view of the microbial capsule.
(a)(b)


## 3.4.2. Fourier Transform Infrared Spectroscopy

Use the Fourier transform infrared spectrometer to characterize the chemical structure of the microbial capsules. Mix the dried microbial capsule sample with potassium bromide in proportion and uniformly place it in a mortar. Slowly ground until it is ground into a powder and place it in a tableting machine for tableting. Place the sheet in an experimental apparatus for scan and analysis.The epoxy resin E-51 selected in this experiment belongs to bisphenol A type epoxy resin. This type of epoxy resin has an aromatic hydrocarbon structure, which produces a richer infrared spectrum. Figure11 illustrates the FTIR spectrum of the microbial capsule. At 830 cm−1 and 915 cm−1, they are characteristic absorption peaks of epoxy resin E-51. Specifically, at 830 cm−1, it is the absorption band of two adjacent hydrogen atoms on the benzene ring; and at 915 cm−1, it belongs to the characteristic absorption band of the epoxy group. The characteristic peak produced by absorption of the aliphatic ether bond C-O-C appears at 1040 cm−1. The characteristic peak of phenyl ether occurs at 1250 cm−1.Figure 11
The FTIR spectrum of the microbial capsule.


## 3.5. The Performance of Microbial Capsules

### 3.5.1. Waterproofness

In the experiment, we chose microcrystalline cellulose to expand the volume of the core material and used hydroxypropyl methylcellulose as a binder to promote the fusion of dry spore powder, nutrients, and microcrystalline cellulose. These two substances are insoluble in water and have good water swell ability, and the volume of the core material expands after water absorption, thereby causing the wall material to rupture. Therefore, we can judge the waterproofness of the wall material according to this feature. We adopted an optical microscope to observe the surface of the microbial capsule, as shown in Figure12. The figure clearly shows that the surface of the microbial capsule has no cracks, so the moisture does not penetrate the inside of the core material. In other words, the wall epoxy resin E-51 has excellent water resistance.Figure 12
The waterproofness of microbial capsule.


### 3.5.2. Storage Stability

Obtain 20 g of microbial capsules with single-particle size and weigh the mass on day 3, 6, 9, 12, 15, and 18. The results are shown in Table6.Table 6
The measurement of stability of microbial capsule.
Mass and lossDaysDay 0Day 3Day 6Day 9Day 12Day 15Day 18Mass20 g19.884 g19.797 g19.762 g19.753 g19.747 g19.740 gMass loss—0.6%0.4%0.17%0.04%0.03%0.03%Figure13 shows the quality of microbial capsules over time. As can be seen from the figure, the mass loss of the microbial capsule was significant in the first six days. As time goes by, the reduction of microbial capsule quality gradually stabilized, and the quality of microbial capsules did not decrease significantly in the later stage. This indicates that the microbial capsule will not drop after losing a small amount of mass, i.e., the microbial capsule has excellent storage stability.Figure 13
The mass trend of the microbial capsule.


### 3.5.3. Rupture Ability under Trigger Condition

Slowly fracture the microbial capsule with forceps and place it under an optical microscope for observation. Figure14 displays an image of the ruptured portion under an optical microscope after the microcapsule breaks. Figure 14(a) shows the broken wall material after the microbial capsules are fractured, showing that the cracked part is smooth and transparent. Figure 14(b) reveals the core material after fracturing, showing an opaque black state, and the surface is not covered with a transparent ring. As can be seen from the figure, the core material and the wall material can be separated under pressure.Figure 14
The fracture figure of the microbial capsule under pressure: (a) broken wall material; (b) core material.
(a)(b)As described above, after the microcapsule capsule breaks, the core material and the wall material will separate. When the microbial capsule is buried in the concrete and the concrete cracks, the pressure is generated inside to cause the microcapsule to rupture and expose the core material. The core material is then in contact with moisture and oxygen to initiate germination, initiate cell metabolism, and produce calcium carbonate for self-healing.


### 3.5.4. Spore Survival Rate

Figure15 illustrates the rupture of the microbial capsule under pressure after 24 h of incubation.Figure 15
The rupture figure of the microbial capsule under pressure.As can be seen from the figure, round white colony spots appear on the surface of the culture dish, and the number of colonies and diameters vary. After statistics, the average number of colonies per dish was 40. That is, after 1 × 108 times dilution, the survival spores in the microbial capsule were 4 × 109 cfu/ml.According to the core-wall ratio, 4 × 109 cfu/ml was converted to 5.33 × 109 cfu/ml of the spore survival per gram of core material in the microbial capsule. The spore survival per gram of the core material before preparation of the microbial capsule was 8 × 109 cfu/ml. Thus, the spore survival rate in the microbial capsule was 66.7%.After the preparation of the core material and the microbial capsule, theBacillus pasteurii remains active. The selected wall material has excellent biocompatibility with the spores, thus ensuring that the microbial capsule can be self-repaired when being embedded in the concrete.


## 3.5.1. Waterproofness

In the experiment, we chose microcrystalline cellulose to expand the volume of the core material and used hydroxypropyl methylcellulose as a binder to promote the fusion of dry spore powder, nutrients, and microcrystalline cellulose. These two substances are insoluble in water and have good water swell ability, and the volume of the core material expands after water absorption, thereby causing the wall material to rupture. Therefore, we can judge the waterproofness of the wall material according to this feature. We adopted an optical microscope to observe the surface of the microbial capsule, as shown in Figure12. The figure clearly shows that the surface of the microbial capsule has no cracks, so the moisture does not penetrate the inside of the core material. In other words, the wall epoxy resin E-51 has excellent water resistance.Figure 12
The waterproofness of microbial capsule.


## 3.5.2. Storage Stability

Obtain 20 g of microbial capsules with single-particle size and weigh the mass on day 3, 6, 9, 12, 15, and 18. The results are shown in Table6.Table 6
The measurement of stability of microbial capsule.
Mass and lossDaysDay 0Day 3Day 6Day 9Day 12Day 15Day 18Mass20 g19.884 g19.797 g19.762 g19.753 g19.747 g19.740 gMass loss—0.6%0.4%0.17%0.04%0.03%0.03%Figure13 shows the quality of microbial capsules over time. As can be seen from the figure, the mass loss of the microbial capsule was significant in the first six days. As time goes by, the reduction of microbial capsule quality gradually stabilized, and the quality of microbial capsules did not decrease significantly in the later stage. This indicates that the microbial capsule will not drop after losing a small amount of mass, i.e., the microbial capsule has excellent storage stability.Figure 13
The mass trend of the microbial capsule.


## 3.5.3. Rupture Ability under Trigger Condition

Slowly fracture the microbial capsule with forceps and place it under an optical microscope for observation. Figure14 displays an image of the ruptured portion under an optical microscope after the microcapsule breaks. Figure 14(a) shows the broken wall material after the microbial capsules are fractured, showing that the cracked part is smooth and transparent. Figure 14(b) reveals the core material after fracturing, showing an opaque black state, and the surface is not covered with a transparent ring. As can be seen from the figure, the core material and the wall material can be separated under pressure.Figure 14
The fracture figure of the microbial capsule under pressure: (a) broken wall material; (b) core material.
(a)(b)As described above, after the microcapsule capsule breaks, the core material and the wall material will separate. When the microbial capsule is buried in the concrete and the concrete cracks, the pressure is generated inside to cause the microcapsule to rupture and expose the core material. The core material is then in contact with moisture and oxygen to initiate germination, initiate cell metabolism, and produce calcium carbonate for self-healing.


## 3.5.4. Spore Survival Rate

Figure15 illustrates the rupture of the microbial capsule under pressure after 24 h of incubation.Figure 15
The rupture figure of the microbial capsule under pressure.As can be seen from the figure, round white colony spots appear on the surface of the culture dish, and the number of colonies and diameters vary. After statistics, the average number of colonies per dish was 40. That is, after 1 × 108 times dilution, the survival spores in the microbial capsule were 4 × 109 cfu/ml.According to the core-wall ratio, 4 × 109 cfu/ml was converted to 5.33 × 109 cfu/ml of the spore survival per gram of core material in the microbial capsule. The spore survival per gram of the core material before preparation of the microbial capsule was 8 × 109 cfu/ml. Thus, the spore survival rate in the microbial capsule was 66.7%.After the preparation of the core material and the microbial capsule, theBacillus pasteurii remains active. The selected wall material has excellent biocompatibility with the spores, thus ensuring that the microbial capsule can be self-repaired when being embedded in the concrete.


## 3.6. Experimental Analysis of Self-Healing Performance

### 3.6.1. Analysis of Water Absorption Test

In the mortar test piece, the calcium carbonate precipitate generated by microbial mineralization binds the sand particles and effectively fills the pores of the mortar test piece. Consequently, the porosity is reduced to a certain extent, and the water absorption of the test piece reduces accordingly. The change trend of water absorption of the test piece with time is shown in Figure16.Figure 16
Water absorption ratio of test pieces under various microbial capsule amounts.As shown in the figure, with a fixed water-to-binder ratio, the water absorption rate of the cement mortar test pieces showed a downward trend with the extension of the curing age. This is due to the continuous increase in hydration products caused by microbial reactions, resulting in a tighter internal structure of the mortar. In addition, the addition of microbial capsules increased the water absorption of the mortar test piece, and the water absorption rate of the test piece showed an upward trend as the number of microbial capsules increased. Since the density of the microcapsules is relatively low, the density of the cement mortar test pieces also decreases with the increase in the microcapsule content, resulting in an increase in the internal porosity of the test pieces.


### 3.6.2. Analysis of Uniaxial Compression Test

Table7 shows the compressive strength of the three groups of test pieces. The compressive strength of group A increased with the extension of maintenance age (48 days). The compressive strength of Group B was higher than that of standard test pieces in the initial stage of curing, but there was no significant change in the overall situation. When bacteria were added, the CO2 hydration reaction in the crack area was accelerated. However, because the cement-based material is more alkaline and the bacteria have poor tolerance, the survival time inside the test pieces became shorter. With the increase in the curing time, few bacteria survived. To sum up, the compression resistance of Group C is significantly improved compared with that of the other two groups. Using epoxy resin as the wall material can achieve long-term survival of bacteria in cement-based materials.Table 7
Comparison of compression strength under various curing ages.
Repair agentStrength (MPa)3(d)5(d)7(d)N/A2.3112.4322.517Bacterial body2.4362.3172.336Microbial capsule2.3162.4252.618


## 3.6.1. Analysis of Water Absorption Test

In the mortar test piece, the calcium carbonate precipitate generated by microbial mineralization binds the sand particles and effectively fills the pores of the mortar test piece. Consequently, the porosity is reduced to a certain extent, and the water absorption of the test piece reduces accordingly. The change trend of water absorption of the test piece with time is shown in Figure16.Figure 16
Water absorption ratio of test pieces under various microbial capsule amounts.As shown in the figure, with a fixed water-to-binder ratio, the water absorption rate of the cement mortar test pieces showed a downward trend with the extension of the curing age. This is due to the continuous increase in hydration products caused by microbial reactions, resulting in a tighter internal structure of the mortar. In addition, the addition of microbial capsules increased the water absorption of the mortar test piece, and the water absorption rate of the test piece showed an upward trend as the number of microbial capsules increased. Since the density of the microcapsules is relatively low, the density of the cement mortar test pieces also decreases with the increase in the microcapsule content, resulting in an increase in the internal porosity of the test pieces.


## 3.6.2. Analysis of Uniaxial Compression Test

Table7 shows the compressive strength of the three groups of test pieces. The compressive strength of group A increased with the extension of maintenance age (48 days). The compressive strength of Group B was higher than that of standard test pieces in the initial stage of curing, but there was no significant change in the overall situation. When bacteria were added, the CO2 hydration reaction in the crack area was accelerated. However, because the cement-based material is more alkaline and the bacteria have poor tolerance, the survival time inside the test pieces became shorter. With the increase in the curing time, few bacteria survived. To sum up, the compression resistance of Group C is significantly improved compared with that of the other two groups. Using epoxy resin as the wall material can achieve long-term survival of bacteria in cement-based materials.Table 7
Comparison of compression strength under various curing ages.
Repair agentStrength (MPa)3(d)5(d)7(d)N/A2.3112.4322.517Bacterial body2.4362.3172.336Microbial capsule2.3162.4252.618


## 4. Conclusion

In this paper, microbial capsules were prepared by usingBacillus pasteurii coated with epoxy resin E-51, and the optimal conditions for preparing microbial capsules were determined according to single-factor experiments. We conclude that(1)
The optimum process conditions for microbial capsules are 1 : 3 in the core-wall ratio, 50°C in the reaction temperature, 40 min in the reaction time, and a stirring rate of 300 rpm.(2)
Epoxy resin E-51 was coated on the surface of the core material particles to form an epoxy resin E-51 coated microbial capsule. The test piece mixed with microbial capsules was cured for a certain period after predamage. Its compressive strength was enhanced, indicating that the microbial capsules played a repairing role.(3)
Microbial capsules have excellent waterproofness and high storage stability. The microbial capsules are embedded in the concrete to achieve mechanical triggering properties and thus rupture. The spore survival rate in the microbial capsules is 66.7%. The wall material is biocompatible with the core material.



---