# Sorbents Coupled to Solar Light TiO2-Based Photocatalysts for Olive Mill Wastewater Treatment

Authors: Andrea Speltini; Federica Maraschi; Michela Sturini; Valentina Caratto; Maurizio Ferretti; Antonella Profumo
Journal: International Journal of Photoenergy
 (2016)

---

## Abstract

The aim of this work was to couple physical-chemical approaches with photocatalysis to reduce by a simple, inexpensive way the organic load of olive mill wastewater (OMW), mandatorily prior to the final discharge. Before irradiation, different sorbents were tested to remove part of the organic fraction, monitored by measuring chemical oxygen demand (COD) and polyphenols (PP). Different low-cost, safe materials were tested, that is, Y zeolite (ZY), montmorillonite, and sepiolite. Considerable decrease of organic load was obtained, with the highest abatement (40%) provided by ZY (10 g L−1 in 1 : 10 OMW). Use of the three sorbents, in particular ZY, was convenient compared to commercial activated carbons. UV light photocatalytic tests, performed using P25 TiO2 on ZY-treated OMW, yielded quantitative remediation (ca. 90%). Also solar light provided significative results, PP being lowered by 74% and COD by 56%. Sol-gel anatase TiO2 and N-doped anatase TiO2 were also tested, obtaining good results, around -80% PP and -40% COD. Finally, an integrated approach was experimented by ZY-supported anatase TiO2 (TiO2@ZY). Thisphotoreactive sorbent allowedone-pot treatment of OMW significative abatements of PP (-77%) and COD (-39%) with only 1 g L−1 material, under solar light.


---

## Body

## 1. Introduction

Olive mill wastewater (OMW) is a highly toxic effluent obtained from the extraction process of the olive oil industry and is considered an undesired waste. OMW represents a serious problem in the Mediterranean basin [1], as over 95% of the world production, estimated at more than 30 million m3 [2], occurs in Mediterranean countries and about 80% in the European Union, mainly Spain, Italy, and Greece [3]. It has been calculated that the volume of OMW coming from milling activity ranges from 0.5 to 1.5 m3 per ton of olives [3].The OMW is a blackish liquid containing 80–83% of water (pH around 4.5), organic compounds ranging from 40 to 220 g L−1 [2]. As expectable, the composition is variable and depends on many factors, namely, olive cultivar, extraction process, and climatic conditions, but always includes oil and grease, sugars, polyalcohols, pectins, lipids, and polyphenols (PP) [4, 5]. Specifically, it has been reported that more than 30 phenolic compounds are present in OMW [6]. Beside lignin and tannins, the high content of phenolic species in a wide range of molecular weights is responsible for the typical black-brownish colour [4]. The dark colour of the OMW disturbs the sunlight absorption by photosynthetical organisms whereas the surface oil film prevents the oxygen absorption from air releasing an intense smell.OMW is indeed considered a source of environmental pollution, due to the high levels of PP, persistent phytotoxic and antibacterial compounds that inhibit biodegradation. Due to the high content of phenols and long-chain fatty acids, high values of chemical oxygen demand (COD), up to 200 g L−1, and biochemical oxygen demand (up to 100 g L−1) are expected [3, 5]. Since these values may be found as hundreds of times higher than those of typical municipal sewage [7], it is clear that a direct discharge in receiving waters or soils is not possible because it would involve severe effects, that is, ecotoxicity and eutrophication for natural water bodies.Although the complex organic composition of OMW has been recently exploited to obtain “clean energy,” such as hydrogen gas [1, 3, 8], the actual major issue is the development of efficient, simple, and low environmental impact treatments for OMW before the final discharge.Among the methods used for OMW treatment, physicochemical treatments (i.e., settling, centrifugation, and filtration) coupled with adsorption on activated carbon have been practiced [9]. On the other side, the biological treatments, mainly consisting of anaerobic digestion [10], require large dilution factors or mandatory dephenolization procedures [11]. Advanced oxidation processes (AOPs) by ozonization [12] or photo-Fenton [5, 13–16] have been experimented, and integrated approaches involving flocculation/coagulation and/or adsorption, enzymatic, and biological treatments and photocatalysis have been proposed [5, 13–15, 17]. However, an environmentally safe and cost-effective solution to OMW treatment is still lacking [18].Heterogeneous photocatalysis, requiring just a semiconductor and a light source, is a very promising, environmentally benign way to reduce the toxic organic load of OMW, as reported in some recent studies [14, 15, 17, 19, 20]. As for photo-Fenton applied to OMW [5], it seems convenient to design a sequential procedure combining pretreatment of the raw OMW, by adsorption onto high surface area sorbents, with a photocatalytic treatment and/or a biological step before the final discharge. As a matter of fact, photocatalysis is becoming increasingly attractive for environmental remediation [21], for instance, for abatement of emerging organic pollutants [22] or toxic metals [23], but also for OMW remediation [14, 15, 17, 19]. Owing to chemical stability, efficiency, low cost, and nontoxicity, titanium dioxide (TiO2) is the most used photocatalyst, recently applied also for OMW remediation, after immobilization onto sepiolite [19]. However, to the authors’ best knowledge, the application of N-doped TiO2 or ZY-supported TiO2 has not been reported in the literature for OMW treatment.Based on this background, the aim of this work was to find out a simple and efficient procedure for the abatement of the organic load of OMW, in particular COD and PP levels. These were the two key parameters for evaluating the efficiency of the various treatments tested, that is, flocculation/coagulation, adsorption, and photocatalysis. Different high surface area materials were employed in the adsorption step, namely, Y zeolite (ZY), sepiolite (SEP), and montmorillonite (MMT), in addition to two commercially available activated carbons. After adsorption, OMW was submitted to photocatalytic treatment, under both UV and solar light. Different semiconductors were investigated, namely, anatase TiO2 and N-doped anatase TiO2 prepared by sol-gel method and characterized before use and commercial P25 TiO2. Finally, a hybrid material consisting of ZY-supported anatase TiO2 combining sorption capacity and photocatalytic activity was prepared, characterized, and tested asphotoreactive sorbent for theone-pot treatment of OMW, under solar light.


## 2. Experimental Procedure

### 2.1. Chemicals

AlCl3·6H2O (99%), Ca(OH)2 (≥95%), cetylpyridinium bromide (CPB, 98%), Folin-Ciocalteau’s phenol reagent (2 N), gallic acid (98%) and Y zeolite (ZY), titanium (IV) tetraisopropoxide (97% v/v), and 2-propanol (99.5% v/v) were obtained from Sigma-Aldrich (Milan, Italy). Na2CO3·10H2O (99.5%) was purchased from Carlo Erba Reagents (Milan, Italy) and Superfloc C 1598, a cationic emulsion polyacrylamide, from Kemira. AC20G (0.6–2.4 mm) and F-300 (0.8–1 mm) activated carbons were acquired from Purolite (Llantrisant, UK) and Chemviron Carbon Ltd. (Ashton-in-Makerfield, UK), respectively. SP-1 sepiolite (SEP, 50 grm/unit), Valdemoro, Spain (Miocene age, containing minor calcite), and Ca-montmorillonite STx-1 (MMT) were obtained from Clay Mineral Society; physical-chemical properties can be found at http://www.clays.org/Sourceclays.html. Evonik P25 TiO2 (80% anatase, 20% rutile, particle size 30 nm, and surface area 50 ± 15 m2 g−1) was purchased from Evonik Industries AG (Hanau, Germany). Distilled water was produced in laboratory.


### 2.2. Olive Mill Wastewater

OMW was collected at the outlet of an olive mill located in Recco, near Genova (Italy). Samples were taken using PET containers and stored in the dark (−20°C). Before use, aliquots of each sample were mixed to obtain a homogeneous representative sample, submitted to centrifugation (3 × 10 min at 4500 rpm, Sigma 2-16P Celbio Spa centrifuge) to remove suspended solids and oil residues [5]. The resulting matrix was then characterized having pH 5.1, conductivity at 20°C 8.21 mS cm−1, COD 52500 (1530) mg L−1 O2, and total PP content 3444 (114) mg L−1. These values, the mean of three replicates, are typical of OMW [5, 8, 14, 24]. The OMW sample was stored in the dark (4°C) and successively used to test the various chemical-physical and photocatalytic treatments.


### 2.3. Analytical Determinations

COD was determined before and after treatment according to the ISO 15705 protocol. The commercialized Hach Lange kit was used, working in the concentration interval 0–1000 mg L−1 O2. After incubation of the sample (2 h, 148°C, LT200 thermostat), COD quantification was performed by the standardized Hach Lange spectrophotometer (DR3900).Total PP were determined according to the Folin-Ciocalteau method. A proper sample aliquot was placed in a 10 mL volumetric flask, and 0.5 mL of the Folin-Ciocalteau reagent was added, followed by 1 mL of Na2CO3 (20%, w/v), and made up to 10 mL with distilled water. The control sample (no OMW) was prepared separately. The flasks were allowed to stand for 1 h; then, spectrophotometric measurements were performed at 700 nm (UVmini-1240 Shimadzu Corporation). Quantification was carried out by external calibration analyzing gallic acid standard solutions in the concentration range 2–8 mg L−1 (linearity r
2 > 0.9975, three independent calibration curves).


### 2.4. Pretreatment by Chemical Reagents

To test the potential effect of coagulant/flocculant agents, 30 mL of centrifuged OMW was spiked with 30μL of 1% w/v AlCl3 solution and then the sample was basified (pH 8) by addition of 5% w/v Ca(OH)2 solution. Alternatively, the OMW sample was enriched with 0.5 g L−1 cationic organic polyelectrolyte. In both cases, the sample was maintained under magnetic stirring overnight and then centrifuged (20 min, 4500 rpm) and filtered (nylon membrane, 0.45 μm) before COD and PP determination.


### 2.5. In-Batch Sorption Pretreatment

In the case of commercial granular activated carbons, batch sorption experiments were conducted on 30 mL OMW in the presence of 10/100 g L−1 of each sorbent. The suspensions were shaken on a rotating plate (150 rpm) in polypropylene tubes, at room temperature for 24 h. The same procedure was followed in the case of ZY (10–40 g L−1), SEP, and MMT (10 g L−1), using OMW (1 : 10). SEP was also tested after derivatization with CPB [25]. After equilibration, the suspensions were centrifuged (10 min, 4500 rpm) and then filtered by a nylon membrane (0.45 μm) before COD and PP determination.


### 2.6. Photocatalysts: Synthesis and Characterization

Beside the commercial P25 TiO2, other TiO2-based photocatalysts were tested. TiO2 and N-doped TiO2 have been synthesized by sol-gel process. According to previous work [26], titanium isopropoxide, isopropanol, and water have been used as precursors with the same concentrations reported changing the different solution to H2O for TiO2 and H2O-NH3 for TiO2 doped nanoparticles.TiO2@ZY has been synthesized according to Maraschi et al. [27]. The sample was obtained by magnetically stirring the resultant suspension of amorphous TiO2 mixed with H+ zeolite (2 : 1 w/w) in water. Powder was filtered, washed, and finally dried. Nominally, 1.5 g of the hybrid sample contains 1 g of nanometric TiO2.The synthesized samples have been finally treated in a muffle furnace (Carbolite RHF1400) at 350°C for 1 hour to promote amorphous to anatase phase conversion.The samples have been analyzed by X-ray powder diffraction (XRPD), scanning electron microscopy (SEM), diffuse reflectance spectroscopy (DRS), and Brunauer-Emmett-Teller analysis (BET). Phase identification was performed by XRPD analysis using a Philips PW1830 diffractometer (Bragg-Brentano geometry; Cu Kα; Ni filtered; range 20–80 2θ; step 0.025 2θ; sampling time 10 s). SEM was performed using a Tescan Vega 3 XMV microscope on powders coated with gold in low vacuum. DRS was performed using a Perkin Elmer UV-Vis spectrophotometer LAMBDA 35 equipped with an integrating sphere. BET analysis was carried out using an ASAP 2010 physisorption analyzer (Micromeritics Instrument Corp). Before measurements, the samples were pretreated at 200°C in vacuum. Ar was used for ZY, while N2 was used for all other materials.


### 2.7. Photocatalytic Irradiation

All the photocatalytic experiments were performed on 10 mL ZY-treated OMW (see Section2.5) in the presence of 1 g L−1 of P25 TiO2, anatase TiO2, and anatase N-TiO2. For ZY-supported TiO2, any previous adsorption was done. Suspensions were irradiated (8 h) under UV light or simulated solar light. For UV irradiation, samples were placed in quartz tubes and treated under continuous air insufflation at 254 nm (4 × 15 W lamps) or 310 nm (10 × 15 W lamps). In the case of solar light, samples were placed in Pyrex glass containers and irradiated under magnetic stirring. A solar Box  1500e (CO.FO.ME.GRA S.r.l., Milan, Italy) set at a power factor of 500 W m−2 and equipped with a UV outdoor filter of soda lime glass IR treated was used as the solar light simulator. After photocatalysis, each sample was filtered and COD and PP concentrations were checked.


## 2.1. Chemicals

AlCl3·6H2O (99%), Ca(OH)2 (≥95%), cetylpyridinium bromide (CPB, 98%), Folin-Ciocalteau’s phenol reagent (2 N), gallic acid (98%) and Y zeolite (ZY), titanium (IV) tetraisopropoxide (97% v/v), and 2-propanol (99.5% v/v) were obtained from Sigma-Aldrich (Milan, Italy). Na2CO3·10H2O (99.5%) was purchased from Carlo Erba Reagents (Milan, Italy) and Superfloc C 1598, a cationic emulsion polyacrylamide, from Kemira. AC20G (0.6–2.4 mm) and F-300 (0.8–1 mm) activated carbons were acquired from Purolite (Llantrisant, UK) and Chemviron Carbon Ltd. (Ashton-in-Makerfield, UK), respectively. SP-1 sepiolite (SEP, 50 grm/unit), Valdemoro, Spain (Miocene age, containing minor calcite), and Ca-montmorillonite STx-1 (MMT) were obtained from Clay Mineral Society; physical-chemical properties can be found at http://www.clays.org/Sourceclays.html. Evonik P25 TiO2 (80% anatase, 20% rutile, particle size 30 nm, and surface area 50 ± 15 m2 g−1) was purchased from Evonik Industries AG (Hanau, Germany). Distilled water was produced in laboratory.


## 2.2. Olive Mill Wastewater

OMW was collected at the outlet of an olive mill located in Recco, near Genova (Italy). Samples were taken using PET containers and stored in the dark (−20°C). Before use, aliquots of each sample were mixed to obtain a homogeneous representative sample, submitted to centrifugation (3 × 10 min at 4500 rpm, Sigma 2-16P Celbio Spa centrifuge) to remove suspended solids and oil residues [5]. The resulting matrix was then characterized having pH 5.1, conductivity at 20°C 8.21 mS cm−1, COD 52500 (1530) mg L−1 O2, and total PP content 3444 (114) mg L−1. These values, the mean of three replicates, are typical of OMW [5, 8, 14, 24]. The OMW sample was stored in the dark (4°C) and successively used to test the various chemical-physical and photocatalytic treatments.


## 2.3. Analytical Determinations

COD was determined before and after treatment according to the ISO 15705 protocol. The commercialized Hach Lange kit was used, working in the concentration interval 0–1000 mg L−1 O2. After incubation of the sample (2 h, 148°C, LT200 thermostat), COD quantification was performed by the standardized Hach Lange spectrophotometer (DR3900).Total PP were determined according to the Folin-Ciocalteau method. A proper sample aliquot was placed in a 10 mL volumetric flask, and 0.5 mL of the Folin-Ciocalteau reagent was added, followed by 1 mL of Na2CO3 (20%, w/v), and made up to 10 mL with distilled water. The control sample (no OMW) was prepared separately. The flasks were allowed to stand for 1 h; then, spectrophotometric measurements were performed at 700 nm (UVmini-1240 Shimadzu Corporation). Quantification was carried out by external calibration analyzing gallic acid standard solutions in the concentration range 2–8 mg L−1 (linearity r
2 > 0.9975, three independent calibration curves).


## 2.4. Pretreatment by Chemical Reagents

To test the potential effect of coagulant/flocculant agents, 30 mL of centrifuged OMW was spiked with 30μL of 1% w/v AlCl3 solution and then the sample was basified (pH 8) by addition of 5% w/v Ca(OH)2 solution. Alternatively, the OMW sample was enriched with 0.5 g L−1 cationic organic polyelectrolyte. In both cases, the sample was maintained under magnetic stirring overnight and then centrifuged (20 min, 4500 rpm) and filtered (nylon membrane, 0.45 μm) before COD and PP determination.


## 2.5. In-Batch Sorption Pretreatment

In the case of commercial granular activated carbons, batch sorption experiments were conducted on 30 mL OMW in the presence of 10/100 g L−1 of each sorbent. The suspensions were shaken on a rotating plate (150 rpm) in polypropylene tubes, at room temperature for 24 h. The same procedure was followed in the case of ZY (10–40 g L−1), SEP, and MMT (10 g L−1), using OMW (1 : 10). SEP was also tested after derivatization with CPB [25]. After equilibration, the suspensions were centrifuged (10 min, 4500 rpm) and then filtered by a nylon membrane (0.45 μm) before COD and PP determination.


## 2.6. Photocatalysts: Synthesis and Characterization

Beside the commercial P25 TiO2, other TiO2-based photocatalysts were tested. TiO2 and N-doped TiO2 have been synthesized by sol-gel process. According to previous work [26], titanium isopropoxide, isopropanol, and water have been used as precursors with the same concentrations reported changing the different solution to H2O for TiO2 and H2O-NH3 for TiO2 doped nanoparticles.TiO2@ZY has been synthesized according to Maraschi et al. [27]. The sample was obtained by magnetically stirring the resultant suspension of amorphous TiO2 mixed with H+ zeolite (2 : 1 w/w) in water. Powder was filtered, washed, and finally dried. Nominally, 1.5 g of the hybrid sample contains 1 g of nanometric TiO2.The synthesized samples have been finally treated in a muffle furnace (Carbolite RHF1400) at 350°C for 1 hour to promote amorphous to anatase phase conversion.The samples have been analyzed by X-ray powder diffraction (XRPD), scanning electron microscopy (SEM), diffuse reflectance spectroscopy (DRS), and Brunauer-Emmett-Teller analysis (BET). Phase identification was performed by XRPD analysis using a Philips PW1830 diffractometer (Bragg-Brentano geometry; Cu Kα; Ni filtered; range 20–80 2θ; step 0.025 2θ; sampling time 10 s). SEM was performed using a Tescan Vega 3 XMV microscope on powders coated with gold in low vacuum. DRS was performed using a Perkin Elmer UV-Vis spectrophotometer LAMBDA 35 equipped with an integrating sphere. BET analysis was carried out using an ASAP 2010 physisorption analyzer (Micromeritics Instrument Corp). Before measurements, the samples were pretreated at 200°C in vacuum. Ar was used for ZY, while N2 was used for all other materials.


## 2.7. Photocatalytic Irradiation

All the photocatalytic experiments were performed on 10 mL ZY-treated OMW (see Section2.5) in the presence of 1 g L−1 of P25 TiO2, anatase TiO2, and anatase N-TiO2. For ZY-supported TiO2, any previous adsorption was done. Suspensions were irradiated (8 h) under UV light or simulated solar light. For UV irradiation, samples were placed in quartz tubes and treated under continuous air insufflation at 254 nm (4 × 15 W lamps) or 310 nm (10 × 15 W lamps). In the case of solar light, samples were placed in Pyrex glass containers and irradiated under magnetic stirring. A solar Box  1500e (CO.FO.ME.GRA S.r.l., Milan, Italy) set at a power factor of 500 W m−2 and equipped with a UV outdoor filter of soda lime glass IR treated was used as the solar light simulator. After photocatalysis, each sample was filtered and COD and PP concentrations were checked.


## 3. Results and Discussion

### 3.1. Characterization of the Prepared Photocatalysts

XRD spectra of TiO2, N-doped TiO2, and TiO2@ZY confirm the presence of anatase crystalline structure (Figure S1 in Supplementary Material available online at http://dx.doi.org/10.1155/2016/8793841). The SEM analysis shows the morphology of the samples. Undoped TiO2 grains have rounded shape and form sponge-like aggregates (Figure 1(a)), while the N-doped ones form lamellar isolated aggregates (Figure 1(b)), in accordance with literature [26].Figure 1
SEM images collected on anatase TiO2 (a) and N-doped anatase TiO2 (b).
(a)
(b)The TiO2 nanoparticles supported by the zeolite are round shaped (Figure 2) and the sample is homogenous, as previously reported by Maraschi et al. [27]. The values of absorption wavelength, energy gap, and surface area of each material are reported in Table 1. It is apparent that N-doping yields a narrower band gap compared to anatase TiO2, although the latter shows a twofold higher surface area. The DRS spectra of doped and undoped TiO2 are shown in the supplementary information (Figure S2). The E
g
a
p calculation was made according to literature [26, 28]. The composite material, TiO2@ZY, shows the highest surface area (>200 m2 g−1); the smaller energy gap and higher surface area compared to pristine ZY confirm the successful immobilization of the photocatalyst onto the zeolitic structure.Table 1
Values of absorption wavelength, energy gap, and BET surface area determined for each material.
Sample
Absorption wavelength (nm)
Energy gap (eV)
Surface area (m2 g−1)
Anatase TiO2
384
3.2
120
N-doped anatase TiO2
413
3.0
67
TiO2@ZY
384
3.2
216
ZY
188
3.7
175Figure 2
SEM image collected on the photoreactive sorbent anatase TiO2@ZY.BET analyses are in agreement with the literature data [27].


### 3.2. OMW Treatment: Adsorption Coupled to Photocatalysis

A first series of experiments was carried out to further reduce the suspended particles of the centrifuged OMW prior to the photocatalytic step, which is more efficient in limpid solution due to higher light penetration and lower scattering phenomena [14]. Since use of chitosan (0.4 g L−1) before Fenton and photo-Fenton oxidation was reported [15], some experiments were performed in the presence of less expensive agents, either AlCl3 (0.001%, v/v) under alkaline conditions (pH 8) or cationic organic polyelectrolyte (0.5 g L−1), in order to test the potential effects of coagulation/flocculation in removing colloids (<1 μm). Results showed that both treatments yielded a COD abatement lower than 10%, whereas a 36% decrease of PP was observed using AlCl3, indicating that the sole centrifugation is convenient for removing suspended organic matter.To reduce the organic load of OMW, in-batch sorption was therefore exploited as a possible more efficient approach, investigated in the recent years for OMW treatment [5, 24, 29]. ZY, MMT, and SEP, largely available and low-cost materials characterized by high surface area, were selected as in principle they can operate in very complex matrices like OMW [5, 24, 29].ZY (surface area 175 m2 g−1) was tested in the concentration range 10–40 g L−1, working at the sample native pH, and results are shown in Table 2.Table 2
PP and COD values in OMW before and after adsorption onto ZY and activated carbons (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
OMW
3444 (114)
—
52500 (1530)
—
OMW + ZY (10 g L−1)
2431 (170)
30 (5)
35900 (1424)
32 (3)
OMW + ZY (20 g L−1)
2189 (152)
37 (4)
32846 (1462)
37 (4)
OMW + ZY (40 g L−1)
1877 (150)
46 (4)
29300 (1568)
44 (3)
OMW + AC20G (100 g L−1)
617 (76)
82 (2)
18800 (1945)
64 (4)
OMW + F-300 (100 g L−1)
1130 (114)
67 (3)
22200 (2054)
58 (4)COD and PP levels were substantially lowered after contact with ZY, indicating a strong affinity for the organic constituents of OMW. This is in accordance with literature data reporting on the use of zeolites for wastewater treatment [4, 29]. No significative improvement was seen in going from the lowest to the highest ZY concentration; thus, 10 g L−1 seemed convenient.Despite the good results obtained, 1 : 10 diluted OMW was used for further experiments (see Table3), in order to dispose of a final solution suitable for the photocatalytic treatment [15, 20]. Indeed, photocatalysis cannot operate satisfactorily in not diluted OMW, as later described and in agreement with literature [14]. The efficiency of ZY was then compared to clay powders, namely, SEP (surface area 213 m2 g−1) and MMT (surface area 84 m2 g−1), under the above reported conditions. These were tested because clays proved to be effective for purification of urban and industrial wastewater and have been recently employed also in the case of OMW [5, 29, 30].Table 3
PP and COD values in 1 : 10 OMW before and after adsorption onto 10 g L−1 ZY, CPB/ZY, SEP, MMT, and activated carbons (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
1 : 10 OMW
335 (25)
—
5226 (330)
—
1 : 10 OMW + ZY (10 g L−1)
186 (21)
44 (6)
2640 (258)
36 (3)
1 : 10 OMW + CPB/ZY (10 g L−1)
194 (19)
42 (5)
2637 (247)
49 (4)
1 : 10 OMW + SEP (10 g L−1)
210 (17)
37 (5)
3685 (147)
29 (3)
1 : 10 OMW + MMT (10 g L−1)
209 (13)
38 (4)
3220 (161)
38 (3)
1 : 10 OMW + F-300 (10 g L−1)
111 (9)
77 (6)
2561 (237)
51 (5)
1 : 10 OMW + AC20G (10 g L−1)
121 (11)
74 (6)
2770 (232)
47 (4)As reported in Table3, PP level dropped down by ca. 40% after adsorption onto SEP and MMT, similar to the case of ZY, and COD by ca. 30%.With the aim of further improving ZY efficiency, the crude powder was derivatized with CPB, a cationic surfactant that could favour sorption of polyphenolic species [25]. However, no significative improvement in PP removal was observed using the CPB-derivatized material; thus, it was preferred to use the raw ZY.Since activated carbon is the most used sorbent for water and wastewater purification, two types of granular activated carbon, specifically AC20G and F-300, were tested for comparison. Due to the large surface area (>1000 m2 g−1) and strong binding affinity of these materials for organic compounds, experiments were performed on not diluted OMW, using 100 g L−1 sorbent, and on 1 : 10 OMW with 10 g L−1 sorbent obtaining comparable results (see Tables 2 and 3).Nevertheless, considering the results obtained by using the alternative sorbents (10 g L−1, 1 : 10 OMW, Table 3) and their low cost compared to activated carbon, ZY proved to be a valid sorbent for OMW remediation and was therefore selected as the convenient adsorbent phase to treat OMW prior to the photocatalytic irradiation. Indeed, after ZY-contact, a biological step followed by an AOP treatment would be required to reach remediation of OMW, or as in this case, the treated OMW can be directly submitted to photocatalysis. This was investigated under either UV or solar simulated light, using commercial P25 TiO2 and sol-gel anatase TiO2 and N-doped anatase TiO2, the two latter not being previously investigated for OMW.Irradiation in presence of the former semiconductor led to quantitative abatements, around 90%, working under UV light. Interesting data were found also under solar simulated irradiation, with COD and PP decrease of 56% and 74%, correspondingly (see Table4).Table 4
PP and COD values in 1 : 10 OMW before and after photocatalytic treatment under UV and solar simulated light using P25 TiO2 (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
1 : 10 OMW
335 (25)
—
5226 (330)
—
1 : 10 OMW + ZY (10 g L−1)
186 (21)
44 (6)
2640 (258)
36 (3)
1 : 10 OMW + ZY (10 g L−1) + P25 TiO2 (254 nm)a
21 (3)
94 (1)
490 (39)
91 (1)
1 : 10 OMW + ZY (10 g L−1) + P25 TiO2 (310 nm)a
31 (4)
91 (1)
775 (54)
85 (1)
1 : 10 OMW + ZY (10 g L−1) + P25 TiO2 (solar box)a
87 (7)
74 (5)
1585 (127)
56 (2)
a1 g L−1 photocatalyst, 8 h irradiation.Notice that the adsorption step prior to photocatalysis is of great importance in allowing a successful remediation of OMW. Indeed, direct photocatalytic treatment on 1:10 OMW (not contacted with ZY) led to a COD abatement of just 20% even under drastic conditions (254 nm, 8 h radiation). On the other hand, irradiation of not diluted OMW after ZY-adsorption was as well unsuccessful. As shown in UV-Vis spectra of OMW samples (see Figure S3, Supplementary Materials), the sorption step on ZY is convenient not only for PP/COD abatement, but also to favour light penetration by decreasing the sample absorbance (ca. 20%).These findings support the actual reports on TiO2 photocatalytic treatment of OMW, requiring a diluted sample [14, 15, 17]. Nevertheless, dilution can be avoided in the case of photo-Fenton, but the additional costs due to the use of oxidizing reagents and necessity to adjust pH have to be taken into account [13, 14, 16]. Besides, since photo-Fenton was shown to preserve or even increase the OMW effluent toxicity, a successive biotreatment that would be required to further reduce COD and phenols could be hampered [16].The adsorption-photocatalysis combined treatment on 1 : 10 OMW presented here is convenient and efficient, as the PP content was reduced to ca. 20 mg L−1, and COD was lowered below the limit (500 mg L−1) indicated by the actual Italian legislation for wastewater discharge. The above results were substantiated by control experiments performed to evaluate the role of direct photolysis that is in the absence of catalyst, under the same conditions. COD and PP reduction being lower than 10%, except in the case of 254 nm for PP (−29%), these findings absolutely attest the great contribution of the photocatalyst in degrading OMW organics.In the framework of the photochemical step, a part of the work was undertaken to strengthen the possibility of working under solar light and, with this aim, N-doped anatase TiO2 was tested, compared to anatase TiO2 as the control sample. Indeed, the absorption edge of P25 TiO2 is around 390 nm, in relation to its band gap of 3–3.2 eV; thus, just the 5% of the solar light spectrum can be exploited for the activation of the semiconductor. Differently, a red-shift absorption of TiO2 can be achieved after derivatization or doping [31]. Despite the narrower band gap obtained after N-doping (3.0 eV), the efficiency in degrading OMW organics was comparable to anatase TiO2 (band gap 3.2 eV), as shown in Table 5.Table 5
PP and COD values in 1 : 10 OMW before and after photocatalytic treatment under solar simulated light using different TiO2-based photocatalysts (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
1 : 10 OMW
335 (25)
—
5226 (330)
—
1 : 10 OMW + ZY (10 g L−1)
186 (21)
44 (6)
2640 (258)
36 (3)
1 : 10 OMW + ZY (10 g L−1) + P25 T
i
O
2
a
87 (7)
74 (5)
1585 (127)
56 (2)
1 : 10 OMW + ZY (10 g L−1) + anatase T
i
O
2
a
54 (5)
84 (6)
3031
42 (3)
1 : 10 OMW + ZY (10 g L−1) + N-doped anatase T
i
O
2
a
74 (6)
78 (4)
3188
39 (3)
1 : 10 OMW + TiO2@ZYa
77 (6)
77 (3)
3170 (224)
39 (3)
a1 g L−1 photocatalyst, 8 h irradiation.This is reasonably attributable to the lower surface area of the N-doped particles that could be improved with further optimization of the synthesis. Anyway, as apparent from Table5, both sol-gel semiconductors are attractive under solar light compared to commercial P25 TiO2.Further experiments were planned using a hybrid material able to join sorption capability and photocatalytic activity, that is, TiO2@ZY. As shown in Table 5, TiO2@ZY proved to be greatly advantageous because it allowed the same efficiency in terms of PP/COD abatement, compared to the sequential treatment entailing adsorption on ZY and photocatalytic steps. Use of this sorbent/photoreactive material provides those similar satisfying results by one-pot treatment and tenfold lower amount of material.The overall abatement is indeed due to the sorption capacity of this composite (49% PP and 29% COD) combined with the photocatalytic properties (further abatement 28% PP and 10% COD). This behavior can be certainly explained by considering the physical-chemical properties of the composite. Indeed, among the many factors that may influence the photocatalytic activity, namely, crystal structure, energy gap, and surface area, TiO2@ZY presents as well greater surface area with respect to pristine zeolite, anatase TiO2, and N-doped TiO2, due to the smaller regular dimension of grains combined with the high surface area of ZY.


## 3.1. Characterization of the Prepared Photocatalysts

XRD spectra of TiO2, N-doped TiO2, and TiO2@ZY confirm the presence of anatase crystalline structure (Figure S1 in Supplementary Material available online at http://dx.doi.org/10.1155/2016/8793841). The SEM analysis shows the morphology of the samples. Undoped TiO2 grains have rounded shape and form sponge-like aggregates (Figure 1(a)), while the N-doped ones form lamellar isolated aggregates (Figure 1(b)), in accordance with literature [26].Figure 1
SEM images collected on anatase TiO2 (a) and N-doped anatase TiO2 (b).
(a)
(b)The TiO2 nanoparticles supported by the zeolite are round shaped (Figure 2) and the sample is homogenous, as previously reported by Maraschi et al. [27]. The values of absorption wavelength, energy gap, and surface area of each material are reported in Table 1. It is apparent that N-doping yields a narrower band gap compared to anatase TiO2, although the latter shows a twofold higher surface area. The DRS spectra of doped and undoped TiO2 are shown in the supplementary information (Figure S2). The E
g
a
p calculation was made according to literature [26, 28]. The composite material, TiO2@ZY, shows the highest surface area (>200 m2 g−1); the smaller energy gap and higher surface area compared to pristine ZY confirm the successful immobilization of the photocatalyst onto the zeolitic structure.Table 1
Values of absorption wavelength, energy gap, and BET surface area determined for each material.
Sample
Absorption wavelength (nm)
Energy gap (eV)
Surface area (m2 g−1)
Anatase TiO2
384
3.2
120
N-doped anatase TiO2
413
3.0
67
TiO2@ZY
384
3.2
216
ZY
188
3.7
175Figure 2
SEM image collected on the photoreactive sorbent anatase TiO2@ZY.BET analyses are in agreement with the literature data [27].


## 3.2. OMW Treatment: Adsorption Coupled to Photocatalysis

A first series of experiments was carried out to further reduce the suspended particles of the centrifuged OMW prior to the photocatalytic step, which is more efficient in limpid solution due to higher light penetration and lower scattering phenomena [14]. Since use of chitosan (0.4 g L−1) before Fenton and photo-Fenton oxidation was reported [15], some experiments were performed in the presence of less expensive agents, either AlCl3 (0.001%, v/v) under alkaline conditions (pH 8) or cationic organic polyelectrolyte (0.5 g L−1), in order to test the potential effects of coagulation/flocculation in removing colloids (<1 μm). Results showed that both treatments yielded a COD abatement lower than 10%, whereas a 36% decrease of PP was observed using AlCl3, indicating that the sole centrifugation is convenient for removing suspended organic matter.To reduce the organic load of OMW, in-batch sorption was therefore exploited as a possible more efficient approach, investigated in the recent years for OMW treatment [5, 24, 29]. ZY, MMT, and SEP, largely available and low-cost materials characterized by high surface area, were selected as in principle they can operate in very complex matrices like OMW [5, 24, 29].ZY (surface area 175 m2 g−1) was tested in the concentration range 10–40 g L−1, working at the sample native pH, and results are shown in Table 2.Table 2
PP and COD values in OMW before and after adsorption onto ZY and activated carbons (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
OMW
3444 (114)
—
52500 (1530)
—
OMW + ZY (10 g L−1)
2431 (170)
30 (5)
35900 (1424)
32 (3)
OMW + ZY (20 g L−1)
2189 (152)
37 (4)
32846 (1462)
37 (4)
OMW + ZY (40 g L−1)
1877 (150)
46 (4)
29300 (1568)
44 (3)
OMW + AC20G (100 g L−1)
617 (76)
82 (2)
18800 (1945)
64 (4)
OMW + F-300 (100 g L−1)
1130 (114)
67 (3)
22200 (2054)
58 (4)COD and PP levels were substantially lowered after contact with ZY, indicating a strong affinity for the organic constituents of OMW. This is in accordance with literature data reporting on the use of zeolites for wastewater treatment [4, 29]. No significative improvement was seen in going from the lowest to the highest ZY concentration; thus, 10 g L−1 seemed convenient.Despite the good results obtained, 1 : 10 diluted OMW was used for further experiments (see Table3), in order to dispose of a final solution suitable for the photocatalytic treatment [15, 20]. Indeed, photocatalysis cannot operate satisfactorily in not diluted OMW, as later described and in agreement with literature [14]. The efficiency of ZY was then compared to clay powders, namely, SEP (surface area 213 m2 g−1) and MMT (surface area 84 m2 g−1), under the above reported conditions. These were tested because clays proved to be effective for purification of urban and industrial wastewater and have been recently employed also in the case of OMW [5, 29, 30].Table 3
PP and COD values in 1 : 10 OMW before and after adsorption onto 10 g L−1 ZY, CPB/ZY, SEP, MMT, and activated carbons (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
1 : 10 OMW
335 (25)
—
5226 (330)
—
1 : 10 OMW + ZY (10 g L−1)
186 (21)
44 (6)
2640 (258)
36 (3)
1 : 10 OMW + CPB/ZY (10 g L−1)
194 (19)
42 (5)
2637 (247)
49 (4)
1 : 10 OMW + SEP (10 g L−1)
210 (17)
37 (5)
3685 (147)
29 (3)
1 : 10 OMW + MMT (10 g L−1)
209 (13)
38 (4)
3220 (161)
38 (3)
1 : 10 OMW + F-300 (10 g L−1)
111 (9)
77 (6)
2561 (237)
51 (5)
1 : 10 OMW + AC20G (10 g L−1)
121 (11)
74 (6)
2770 (232)
47 (4)As reported in Table3, PP level dropped down by ca. 40% after adsorption onto SEP and MMT, similar to the case of ZY, and COD by ca. 30%.With the aim of further improving ZY efficiency, the crude powder was derivatized with CPB, a cationic surfactant that could favour sorption of polyphenolic species [25]. However, no significative improvement in PP removal was observed using the CPB-derivatized material; thus, it was preferred to use the raw ZY.Since activated carbon is the most used sorbent for water and wastewater purification, two types of granular activated carbon, specifically AC20G and F-300, were tested for comparison. Due to the large surface area (>1000 m2 g−1) and strong binding affinity of these materials for organic compounds, experiments were performed on not diluted OMW, using 100 g L−1 sorbent, and on 1 : 10 OMW with 10 g L−1 sorbent obtaining comparable results (see Tables 2 and 3).Nevertheless, considering the results obtained by using the alternative sorbents (10 g L−1, 1 : 10 OMW, Table 3) and their low cost compared to activated carbon, ZY proved to be a valid sorbent for OMW remediation and was therefore selected as the convenient adsorbent phase to treat OMW prior to the photocatalytic irradiation. Indeed, after ZY-contact, a biological step followed by an AOP treatment would be required to reach remediation of OMW, or as in this case, the treated OMW can be directly submitted to photocatalysis. This was investigated under either UV or solar simulated light, using commercial P25 TiO2 and sol-gel anatase TiO2 and N-doped anatase TiO2, the two latter not being previously investigated for OMW.Irradiation in presence of the former semiconductor led to quantitative abatements, around 90%, working under UV light. Interesting data were found also under solar simulated irradiation, with COD and PP decrease of 56% and 74%, correspondingly (see Table4).Table 4
PP and COD values in 1 : 10 OMW before and after photocatalytic treatment under UV and solar simulated light using P25 TiO2 (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
1 : 10 OMW
335 (25)
—
5226 (330)
—
1 : 10 OMW + ZY (10 g L−1)
186 (21)
44 (6)
2640 (258)
36 (3)
1 : 10 OMW + ZY (10 g L−1) + P25 TiO2 (254 nm)a
21 (3)
94 (1)
490 (39)
91 (1)
1 : 10 OMW + ZY (10 g L−1) + P25 TiO2 (310 nm)a
31 (4)
91 (1)
775 (54)
85 (1)
1 : 10 OMW + ZY (10 g L−1) + P25 TiO2 (solar box)a
87 (7)
74 (5)
1585 (127)
56 (2)
a1 g L−1 photocatalyst, 8 h irradiation.Notice that the adsorption step prior to photocatalysis is of great importance in allowing a successful remediation of OMW. Indeed, direct photocatalytic treatment on 1:10 OMW (not contacted with ZY) led to a COD abatement of just 20% even under drastic conditions (254 nm, 8 h radiation). On the other hand, irradiation of not diluted OMW after ZY-adsorption was as well unsuccessful. As shown in UV-Vis spectra of OMW samples (see Figure S3, Supplementary Materials), the sorption step on ZY is convenient not only for PP/COD abatement, but also to favour light penetration by decreasing the sample absorbance (ca. 20%).These findings support the actual reports on TiO2 photocatalytic treatment of OMW, requiring a diluted sample [14, 15, 17]. Nevertheless, dilution can be avoided in the case of photo-Fenton, but the additional costs due to the use of oxidizing reagents and necessity to adjust pH have to be taken into account [13, 14, 16]. Besides, since photo-Fenton was shown to preserve or even increase the OMW effluent toxicity, a successive biotreatment that would be required to further reduce COD and phenols could be hampered [16].The adsorption-photocatalysis combined treatment on 1 : 10 OMW presented here is convenient and efficient, as the PP content was reduced to ca. 20 mg L−1, and COD was lowered below the limit (500 mg L−1) indicated by the actual Italian legislation for wastewater discharge. The above results were substantiated by control experiments performed to evaluate the role of direct photolysis that is in the absence of catalyst, under the same conditions. COD and PP reduction being lower than 10%, except in the case of 254 nm for PP (−29%), these findings absolutely attest the great contribution of the photocatalyst in degrading OMW organics.In the framework of the photochemical step, a part of the work was undertaken to strengthen the possibility of working under solar light and, with this aim, N-doped anatase TiO2 was tested, compared to anatase TiO2 as the control sample. Indeed, the absorption edge of P25 TiO2 is around 390 nm, in relation to its band gap of 3–3.2 eV; thus, just the 5% of the solar light spectrum can be exploited for the activation of the semiconductor. Differently, a red-shift absorption of TiO2 can be achieved after derivatization or doping [31]. Despite the narrower band gap obtained after N-doping (3.0 eV), the efficiency in degrading OMW organics was comparable to anatase TiO2 (band gap 3.2 eV), as shown in Table 5.Table 5
PP and COD values in 1 : 10 OMW before and after photocatalytic treatment under solar simulated light using different TiO2-based photocatalysts (n
=
3).
Sample
PP (mg L−1)
Abatement (%)
COD (mg L−1 O2)
Abatement (%)
1 : 10 OMW
335 (25)
—
5226 (330)
—
1 : 10 OMW + ZY (10 g L−1)
186 (21)
44 (6)
2640 (258)
36 (3)
1 : 10 OMW + ZY (10 g L−1) + P25 T
i
O
2
a
87 (7)
74 (5)
1585 (127)
56 (2)
1 : 10 OMW + ZY (10 g L−1) + anatase T
i
O
2
a
54 (5)
84 (6)
3031
42 (3)
1 : 10 OMW + ZY (10 g L−1) + N-doped anatase T
i
O
2
a
74 (6)
78 (4)
3188
39 (3)
1 : 10 OMW + TiO2@ZYa
77 (6)
77 (3)
3170 (224)
39 (3)
a1 g L−1 photocatalyst, 8 h irradiation.This is reasonably attributable to the lower surface area of the N-doped particles that could be improved with further optimization of the synthesis. Anyway, as apparent from Table5, both sol-gel semiconductors are attractive under solar light compared to commercial P25 TiO2.Further experiments were planned using a hybrid material able to join sorption capability and photocatalytic activity, that is, TiO2@ZY. As shown in Table 5, TiO2@ZY proved to be greatly advantageous because it allowed the same efficiency in terms of PP/COD abatement, compared to the sequential treatment entailing adsorption on ZY and photocatalytic steps. Use of this sorbent/photoreactive material provides those similar satisfying results by one-pot treatment and tenfold lower amount of material.The overall abatement is indeed due to the sorption capacity of this composite (49% PP and 29% COD) combined with the photocatalytic properties (further abatement 28% PP and 10% COD). This behavior can be certainly explained by considering the physical-chemical properties of the composite. Indeed, among the many factors that may influence the photocatalytic activity, namely, crystal structure, energy gap, and surface area, TiO2@ZY presents as well greater surface area with respect to pristine zeolite, anatase TiO2, and N-doped TiO2, due to the smaller regular dimension of grains combined with the high surface area of ZY.


## 4. Conclusions

A simple, working procedure for OMW treatment prior to final discharge, entailing adsorption onto Y zeolite followed by TiO2 photocatalysis, is described here. The first step allowed relevant abatement of the organic load of OMW due to adsorption onto ZY, a largely available and costless material, providing an intermediated sample suitable to be submitted to photocatalytic treatment. This was studied under both UV and simulated solar light, in presence of various TiO2-based photocatalysts, namely, commercial P25, sol-gel anatase, and sol-gel N-doped anatase TiO2. Photocatalysis proved to degrade substantially OMW organic constituents, leading to a COD < 500 mg L−1 and PP around 20 mg L−1 in the final water. Considerable remediation was gained also under simulated sunlight. As a remarkable advantage, a hybrid material made of ZY-supported anatase TiO2 was for the first time applied for theone-pot treatment of OMW, under solar light. This material, combining solar light photocatalytic activity with sorption capacity, proved to be greatly advantageous in terms of efficiency, cost, ease of separation after use, and time-consumption.



---