# Design and Experiment Study of Ultrasonic Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

Authors: Xiangqiang Zhong; Benxue Zhang; Weiqing Huang; Zhimin Di; Huajie Fang
Journal: Shock and Vibration
 (2020)

---

## Abstract

In order to realize the connection for metal foil, a longitudinal-torsional compound consolidation vibration system is proposed, and relative experiments are carried out. Firstly, the structure of longitudinal-torsional compound consolidation vibration system was designed, detailed structural design of the compound piezoelectric transducer and the compound horn in the vibration system was carried out, and torsional vibration analysis of the compound horn with spiral grooves was carried out based on mechanical principle. Secondly, modal calculation and harmonic response analysis of longitudinal-torsional compound consolidation vibration system were carried out, and corresponding vibration mode and harmonic frequency were obtained. The effect of structural parameters for the compound horn on the frequency of the consolidation vibration system was analysed, and structural parameters of the compound horn were optimized. Finally, the prototype was made, and the experimental platform was built to test the amplitude. When the frequency is near 20000 Hz, the resonance is achieved in three directions at the same time, and the resonance frequency is 19800 Hz. Through the frequency-scanning test, the maximum longitudinal amplitude of the consolidation vibration system is 16μm, and the maximum torsional amplitudes of X and Y are 7.9 μm and 8.1 μm. The longitudinal-torsional compound consolidation vibration system can realize the connection of the same and different metal foils and has broad application prospects.


---

## Body

## 1. Introduction

Ultrasonic additive manufacturing for metal foil has the advantages of low forming temperature, small deformation, fast speed, and no pollution. A variety of metal foils and embed low melting point materials or electronic devices such as sensors, alloy fibres, and other temperature-sensitive materials can be connected and are widely used in the manufacturing of intelligent structures and materials [1–4]. To connect metal foils under certain pressure, it is usually achieved under one-dimensional longitudinal vibration mode by the traditional additive manufacturing equipment. The consolidation mechanism is clear but accompanied with some shortcomings; it cannot apply to thick and hard metal foil such as titanium alloy and stainless steel. Therefore, the research on two-dimensional compound ultrasonic consolidation vibration system for metal foil becomes a hot spot.A system for use in ultrasonic additive manufacturing processes was invented by Norfolk et al. [5], comprising the milling machine or the like and a welded assembly. Graff et al. [6] invented an ultrasonic welding apparatus that included a full-wave sonotrode that further included a first horn, a first nodal region, a welding surface, a second nodal region, and a second horn.Tsujino et al. [7–10] studied transverse and torsional complex vibration systems for ultrasonic seam welding of metal plate specimens, using a 27 kHz welding tip with complex vibration disk vibrating in transverse and torsional vibration modes. The complex vibration system can continuously weld multiple parts of metal plate specimens such as heat sinks with a large number of fins.An ultrasonic longitudinal-torsional vibration source which could be controlled was developed by Asami et al. [11]. It consisted of two transducers, a longitudinal transducer and a torsional transducer, attached to the ends of a uniform rod with a length of one wavelength of the propagating vibration.Al-Budairi et al. [12, 13] studied combining longitudinal and torsional vibration responses at the output face of a Langevin transducer. A mode degeneration method was adopted that converted the longitudinal response excited by the axially poled piezoceramic discs in the transducer into combined longitudinal-torsional vibration in the transducer front mass using geometric modifications of the wave path.Ultrasonic additive manufacturing system for longitudinal vibration and the design approach for longitudinal-torsional ultrasonic transducers have been studied in the above research work, but there are few studies on longitudinal-torsional compound consolidation vibration system for metal foil.In this paper, longitudinal-torsional compound consolidation vibration system for metal foil was designed, the structure and working principle were analysed, and the optimization design of the consolidation vibration system was carried out. The longitudinal and torsional amplitudes were tested. The experiment proved the feasibility of the longitudinal-torsional compound consolidation vibration system.


## 2. Structural Design of Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

In order to better explore the effect of ultrasonic vibration mode on the consolidation for metal foil, based on UG NX, a hybrid top-down and bottom-up assembly method was adopted to establish the overall structure, as shown in Figure1. The system mainly includes a piezoelectric transducer, the compound horn with spiral grooves, and consolidation sonotrode [14–16].Figure 1
The overall structure of longitudinal-torsional compound consolidation vibration system. 1: spiral groove; 2: front cover plate; 3: electrode slices; 4: rear cover plate; 5: fastening bolt; 6: piezoelectric ceramics; 7: flange; 8: consolidation sonotrode.The working principle of the consolidation vibration system is as follows. Flange 7 is used for positioning the whole consolidation vibration system; pretightening bolt 5 makes piezoelectric ceramic 6 fasten between the front cover plate and rear cover plate. When an ultrasonic signal is input, longitudinal vibration is generated by the piezoelectric transducer and then is transformed into longitudinal-torsional compound vibration through spiral grooves. Under a static pressure applied to consolidation sonotrode 8, friction heat is generated between metal foils, and then plastic deformation occurs, and the consolidation for metal foil is achieved.


### 2.1. Design of the Compound Piezoelectric Transducer

The piezoelectric transducer is the key component of longitudinal-torsional compound consolidation vibration system. Its vibration mode belongs to longitudinal vibration. It uses the reverse piezoelectric effect of piezoelectric ceramics to generate the vibration.


#### 2.1.1. Equivalent Circuit of the Piezoelectric Transducer

The equivalent circuit of the piezoelectric transducer mainly includes the front cover plate, piezoelectric ceramics and rear cover plate. As shown in Figure2, Z01, Za2, and Za3 are the impedance of the rear cover plate. Z01 and Z02 are the impedance of piezoelectric ceramics. Zb1, Zb2, and Zb3 are the impedance of the front cover plate. Zb is the load impedance of the rear cover plate. Zf is the load impedance of the front cover plate. I is the circuit current. V is the circuit voltage. C0 is the circuit capacitance. When the transducer is designed and calculated, the load impedance of Zb and Zf can be removed.Figure 2
The equivalent circuit of the transducer.


#### 2.1.2. Frequency Equation of the Piezoelectric Transducer

The frequency equation of the piezoelectric transducer is the key to the structural design of the transducer. The frequency equation is related to the structure, shape, and material characteristics of the transducer components. The nodal plane selection of the transducer affects the structural dimension, which is the basis of the transducer design. The piezoelectric transducer node designed in this paper is at the front cover plate, as shown in Figure3. l1, l2, l3, and l4 are different position sizes of the transducer, l4=λc/4. The frequency equation of the transducer node at the front cover plate is shown in the following equation:(1)Z3Z2tank2l2tank3l3+Z3Z1tank1l1tank3l3+Z2Z1tank1l1tank2l2=1,where k1=24.7m−1, k2=40.5m−1, and k3=23.9m−1.Figure 3
Nodal plane at the front cover plate.


#### 2.1.3. Size Calculation of the Piezoelectric Transducer

The material characteristic parameters for different components of the transducer are shown in Table1.Table 1
Material parameters of ultrasonic transducer.
MaterialDensityρ 103 (kg/m3)Elastic modulusE 1011 (N/m2)Poisson’s ratioμLongitudinal wave velocityC m/sPiezoelectric ceramic PZT-87.50.590.353100Electrode slices (copper strip)8.91.230.353718Front cover plate (aluminum alloy)2.70.700.345090Rear cover plate (45# steel)7.82.160.285262Prestressed screw (40 Cr)7.752.150.295267Horn (45# steel)7.82.160.285262Sonotrode (45# steel)7.82.160.285262Using the frequency equation (1) and the data in Table 1, the dimensions of different structures of the transducer can be calculated.Piezoelectric ceramic is PZT-8, the radius isR1=20mm, the thickness is 5 mm, four pieces are taken, the radius of electrode slices is the same as that of piezoelectric ceramic, the radius is also R2=20mm, the thickness is 1 mm, and l2=5×4+1×4=24mm.The rear cover plate is 45# steel, the radius isR3=20mm, and the length is 10 mm. l4=λc/4=c/4f=5262/4/20=65.8mm, the value is rounded to 66 mm.Takingl2, l3, and l4 and the data in Table 1 into equation (1), l1=4.5mm is calculated. Therefore, the length of front cover plate of the transducer is l1+l4=70.5mm and the radius is R4=20mm.


### 2.2. Design of Longitudinal-Torsional Compound Horn

In the longitudinal-torsional compound piezoelectric consolidation vibration system, the horn is the key component. The horn amplifies the vibration of the transducer and transmits it, and the consolidation requirement for metal foil is met [17–19].


#### 2.2.1. Frequency Equation of Conical Compound Horn

In order to meet the requirements of the consolidation vibration system, the design of stepped conical compound horn is adopted, which can not only ensure the amplitude magnification but also ensure the stability of vibration transmission by giving the need for big amplitude and high stability of longitudinal-torsional compound piezoelectric vibration system for metal foil. The structure and boundary conditions of stepped conical compound horn are shown in Figure4.Figure 4
Stepped conical compound horn.The frequency equation of the compound horn is shown in the following equation:(2)tank6l6=a2k5l5−a2+bk5l52tank5l5k5l5bk5l5−atank5l5,where, a=R5−R6/R6, b=R5/R6, and k5=k6=23.9m−1.The amplitude magnification of the compound horn is shown in the following equation:(3)Mp=R5R6cosk5l5−1k5l5R5−R6R6sink5l51cosk5l5.In order to match with the output end of the transducer, the radius of the big end conical part isR5=20mm, the length is l5=50mm, and the radius of the small end cylinder is R6=6.66mm.Takinga=2, b=3, and k5l5=1.195 into (2) and (3), l6=60mm and Mp=6.48 are calculated.


#### 2.2.2. Torsional Vibration Analysis of the Compound Horn with Spiral Grooves Based on Mechanical Principle

At present, there are two ways to generate longitudinal-torsional vibration in the ultrasonic vibration system. One is to use the axial and tangential polarization of piezoelectric ceramics, which is easy to make the polarization effect of piezoelectric ceramics poor. The other is to use the modal conversion method to transform the longitudinal vibration into the longitudinal-torsional compound vibration through a structure, which is relatively simple. The compound horn with spiral grooves is shown in Figure5. The inclination angle of spiral grooves is β. r1 is the small end radius of the compound horn, and r2 is the big end radius of the compound horn.Figure 5
Spiral groove structure.The spiral groove divides the vibration forceF into the axial force F1 and the tangential force F2, in which the tangential force F2 causes the torsional vibration of the compound horn and the axial force F1 causes the longitudinal vibration of the compound horn. The relationship between them is shown in the following equation:(4)F1=Fcosβ,F2=Fsinβ.The torqueMT generated by torsional vibration is shown in the following equation:(5)MT=∫SrfTdS,where r is the radius of the spiral groove at any section and fT=Fsinβ/S is the unit area tangential force of the spiral groove.The approximate calculation of the cross-sectional area of the spiral groove at any position is shown in the following equation:(6)S=πr2−2hsinβr1<r≤r2,where h is the depth of the spiral groove.Equation (7) can be obtained from the following equation:(7)dS=2πrdrThe following equation can be obtained from (5)–(7):(8)MT=2Fsinβr2−r1−2hsinβ/πarctanhr22hsinβ/π+2hsinβ/πarctanhr12hsinβ/π.From the moment expression, the transducer can generate both the longitudinal vibration and the torsional vibration by means of the effect of the spiral groove, which can realize the longitudinal-torsional compound vibration.In order to realize the consolidation for metal foil, a consolidation disk should be installed at the front end of the compound horn with spiral grooves.


## 2.1. Design of the Compound Piezoelectric Transducer

The piezoelectric transducer is the key component of longitudinal-torsional compound consolidation vibration system. Its vibration mode belongs to longitudinal vibration. It uses the reverse piezoelectric effect of piezoelectric ceramics to generate the vibration.


### 2.1.1. Equivalent Circuit of the Piezoelectric Transducer

The equivalent circuit of the piezoelectric transducer mainly includes the front cover plate, piezoelectric ceramics and rear cover plate. As shown in Figure2, Z01, Za2, and Za3 are the impedance of the rear cover plate. Z01 and Z02 are the impedance of piezoelectric ceramics. Zb1, Zb2, and Zb3 are the impedance of the front cover plate. Zb is the load impedance of the rear cover plate. Zf is the load impedance of the front cover plate. I is the circuit current. V is the circuit voltage. C0 is the circuit capacitance. When the transducer is designed and calculated, the load impedance of Zb and Zf can be removed.Figure 2
The equivalent circuit of the transducer.


### 2.1.2. Frequency Equation of the Piezoelectric Transducer

The frequency equation of the piezoelectric transducer is the key to the structural design of the transducer. The frequency equation is related to the structure, shape, and material characteristics of the transducer components. The nodal plane selection of the transducer affects the structural dimension, which is the basis of the transducer design. The piezoelectric transducer node designed in this paper is at the front cover plate, as shown in Figure3. l1, l2, l3, and l4 are different position sizes of the transducer, l4=λc/4. The frequency equation of the transducer node at the front cover plate is shown in the following equation:(1)Z3Z2tank2l2tank3l3+Z3Z1tank1l1tank3l3+Z2Z1tank1l1tank2l2=1,where k1=24.7m−1, k2=40.5m−1, and k3=23.9m−1.Figure 3
Nodal plane at the front cover plate.


### 2.1.3. Size Calculation of the Piezoelectric Transducer

The material characteristic parameters for different components of the transducer are shown in Table1.Table 1
Material parameters of ultrasonic transducer.
MaterialDensityρ 103 (kg/m3)Elastic modulusE 1011 (N/m2)Poisson’s ratioμLongitudinal wave velocityC m/sPiezoelectric ceramic PZT-87.50.590.353100Electrode slices (copper strip)8.91.230.353718Front cover plate (aluminum alloy)2.70.700.345090Rear cover plate (45# steel)7.82.160.285262Prestressed screw (40 Cr)7.752.150.295267Horn (45# steel)7.82.160.285262Sonotrode (45# steel)7.82.160.285262Using the frequency equation (1) and the data in Table 1, the dimensions of different structures of the transducer can be calculated.Piezoelectric ceramic is PZT-8, the radius isR1=20mm, the thickness is 5 mm, four pieces are taken, the radius of electrode slices is the same as that of piezoelectric ceramic, the radius is also R2=20mm, the thickness is 1 mm, and l2=5×4+1×4=24mm.The rear cover plate is 45# steel, the radius isR3=20mm, and the length is 10 mm. l4=λc/4=c/4f=5262/4/20=65.8mm, the value is rounded to 66 mm.Takingl2, l3, and l4 and the data in Table 1 into equation (1), l1=4.5mm is calculated. Therefore, the length of front cover plate of the transducer is l1+l4=70.5mm and the radius is R4=20mm.


## 2.1.1. Equivalent Circuit of the Piezoelectric Transducer

The equivalent circuit of the piezoelectric transducer mainly includes the front cover plate, piezoelectric ceramics and rear cover plate. As shown in Figure2, Z01, Za2, and Za3 are the impedance of the rear cover plate. Z01 and Z02 are the impedance of piezoelectric ceramics. Zb1, Zb2, and Zb3 are the impedance of the front cover plate. Zb is the load impedance of the rear cover plate. Zf is the load impedance of the front cover plate. I is the circuit current. V is the circuit voltage. C0 is the circuit capacitance. When the transducer is designed and calculated, the load impedance of Zb and Zf can be removed.Figure 2
The equivalent circuit of the transducer.


## 2.1.2. Frequency Equation of the Piezoelectric Transducer

The frequency equation of the piezoelectric transducer is the key to the structural design of the transducer. The frequency equation is related to the structure, shape, and material characteristics of the transducer components. The nodal plane selection of the transducer affects the structural dimension, which is the basis of the transducer design. The piezoelectric transducer node designed in this paper is at the front cover plate, as shown in Figure3. l1, l2, l3, and l4 are different position sizes of the transducer, l4=λc/4. The frequency equation of the transducer node at the front cover plate is shown in the following equation:(1)Z3Z2tank2l2tank3l3+Z3Z1tank1l1tank3l3+Z2Z1tank1l1tank2l2=1,where k1=24.7m−1, k2=40.5m−1, and k3=23.9m−1.Figure 3
Nodal plane at the front cover plate.


## 2.1.3. Size Calculation of the Piezoelectric Transducer

The material characteristic parameters for different components of the transducer are shown in Table1.Table 1
Material parameters of ultrasonic transducer.
MaterialDensityρ 103 (kg/m3)Elastic modulusE 1011 (N/m2)Poisson’s ratioμLongitudinal wave velocityC m/sPiezoelectric ceramic PZT-87.50.590.353100Electrode slices (copper strip)8.91.230.353718Front cover plate (aluminum alloy)2.70.700.345090Rear cover plate (45# steel)7.82.160.285262Prestressed screw (40 Cr)7.752.150.295267Horn (45# steel)7.82.160.285262Sonotrode (45# steel)7.82.160.285262Using the frequency equation (1) and the data in Table 1, the dimensions of different structures of the transducer can be calculated.Piezoelectric ceramic is PZT-8, the radius isR1=20mm, the thickness is 5 mm, four pieces are taken, the radius of electrode slices is the same as that of piezoelectric ceramic, the radius is also R2=20mm, the thickness is 1 mm, and l2=5×4+1×4=24mm.The rear cover plate is 45# steel, the radius isR3=20mm, and the length is 10 mm. l4=λc/4=c/4f=5262/4/20=65.8mm, the value is rounded to 66 mm.Takingl2, l3, and l4 and the data in Table 1 into equation (1), l1=4.5mm is calculated. Therefore, the length of front cover plate of the transducer is l1+l4=70.5mm and the radius is R4=20mm.


## 2.2. Design of Longitudinal-Torsional Compound Horn

In the longitudinal-torsional compound piezoelectric consolidation vibration system, the horn is the key component. The horn amplifies the vibration of the transducer and transmits it, and the consolidation requirement for metal foil is met [17–19].


### 2.2.1. Frequency Equation of Conical Compound Horn

In order to meet the requirements of the consolidation vibration system, the design of stepped conical compound horn is adopted, which can not only ensure the amplitude magnification but also ensure the stability of vibration transmission by giving the need for big amplitude and high stability of longitudinal-torsional compound piezoelectric vibration system for metal foil. The structure and boundary conditions of stepped conical compound horn are shown in Figure4.Figure 4
Stepped conical compound horn.The frequency equation of the compound horn is shown in the following equation:(2)tank6l6=a2k5l5−a2+bk5l52tank5l5k5l5bk5l5−atank5l5,where, a=R5−R6/R6, b=R5/R6, and k5=k6=23.9m−1.The amplitude magnification of the compound horn is shown in the following equation:(3)Mp=R5R6cosk5l5−1k5l5R5−R6R6sink5l51cosk5l5.In order to match with the output end of the transducer, the radius of the big end conical part isR5=20mm, the length is l5=50mm, and the radius of the small end cylinder is R6=6.66mm.Takinga=2, b=3, and k5l5=1.195 into (2) and (3), l6=60mm and Mp=6.48 are calculated.


### 2.2.2. Torsional Vibration Analysis of the Compound Horn with Spiral Grooves Based on Mechanical Principle

At present, there are two ways to generate longitudinal-torsional vibration in the ultrasonic vibration system. One is to use the axial and tangential polarization of piezoelectric ceramics, which is easy to make the polarization effect of piezoelectric ceramics poor. The other is to use the modal conversion method to transform the longitudinal vibration into the longitudinal-torsional compound vibration through a structure, which is relatively simple. The compound horn with spiral grooves is shown in Figure5. The inclination angle of spiral grooves is β. r1 is the small end radius of the compound horn, and r2 is the big end radius of the compound horn.Figure 5
Spiral groove structure.The spiral groove divides the vibration forceF into the axial force F1 and the tangential force F2, in which the tangential force F2 causes the torsional vibration of the compound horn and the axial force F1 causes the longitudinal vibration of the compound horn. The relationship between them is shown in the following equation:(4)F1=Fcosβ,F2=Fsinβ.The torqueMT generated by torsional vibration is shown in the following equation:(5)MT=∫SrfTdS,where r is the radius of the spiral groove at any section and fT=Fsinβ/S is the unit area tangential force of the spiral groove.The approximate calculation of the cross-sectional area of the spiral groove at any position is shown in the following equation:(6)S=πr2−2hsinβr1<r≤r2,where h is the depth of the spiral groove.Equation (7) can be obtained from the following equation:(7)dS=2πrdrThe following equation can be obtained from (5)–(7):(8)MT=2Fsinβr2−r1−2hsinβ/πarctanhr22hsinβ/π+2hsinβ/πarctanhr12hsinβ/π.From the moment expression, the transducer can generate both the longitudinal vibration and the torsional vibration by means of the effect of the spiral groove, which can realize the longitudinal-torsional compound vibration.In order to realize the consolidation for metal foil, a consolidation disk should be installed at the front end of the compound horn with spiral grooves.


## 2.2.1. Frequency Equation of Conical Compound Horn

In order to meet the requirements of the consolidation vibration system, the design of stepped conical compound horn is adopted, which can not only ensure the amplitude magnification but also ensure the stability of vibration transmission by giving the need for big amplitude and high stability of longitudinal-torsional compound piezoelectric vibration system for metal foil. The structure and boundary conditions of stepped conical compound horn are shown in Figure4.Figure 4
Stepped conical compound horn.The frequency equation of the compound horn is shown in the following equation:(2)tank6l6=a2k5l5−a2+bk5l52tank5l5k5l5bk5l5−atank5l5,where, a=R5−R6/R6, b=R5/R6, and k5=k6=23.9m−1.The amplitude magnification of the compound horn is shown in the following equation:(3)Mp=R5R6cosk5l5−1k5l5R5−R6R6sink5l51cosk5l5.In order to match with the output end of the transducer, the radius of the big end conical part isR5=20mm, the length is l5=50mm, and the radius of the small end cylinder is R6=6.66mm.Takinga=2, b=3, and k5l5=1.195 into (2) and (3), l6=60mm and Mp=6.48 are calculated.


## 2.2.2. Torsional Vibration Analysis of the Compound Horn with Spiral Grooves Based on Mechanical Principle

At present, there are two ways to generate longitudinal-torsional vibration in the ultrasonic vibration system. One is to use the axial and tangential polarization of piezoelectric ceramics, which is easy to make the polarization effect of piezoelectric ceramics poor. The other is to use the modal conversion method to transform the longitudinal vibration into the longitudinal-torsional compound vibration through a structure, which is relatively simple. The compound horn with spiral grooves is shown in Figure5. The inclination angle of spiral grooves is β. r1 is the small end radius of the compound horn, and r2 is the big end radius of the compound horn.Figure 5
Spiral groove structure.The spiral groove divides the vibration forceF into the axial force F1 and the tangential force F2, in which the tangential force F2 causes the torsional vibration of the compound horn and the axial force F1 causes the longitudinal vibration of the compound horn. The relationship between them is shown in the following equation:(4)F1=Fcosβ,F2=Fsinβ.The torqueMT generated by torsional vibration is shown in the following equation:(5)MT=∫SrfTdS,where r is the radius of the spiral groove at any section and fT=Fsinβ/S is the unit area tangential force of the spiral groove.The approximate calculation of the cross-sectional area of the spiral groove at any position is shown in the following equation:(6)S=πr2−2hsinβr1<r≤r2,where h is the depth of the spiral groove.Equation (7) can be obtained from the following equation:(7)dS=2πrdrThe following equation can be obtained from (5)–(7):(8)MT=2Fsinβr2−r1−2hsinβ/πarctanhr22hsinβ/π+2hsinβ/πarctanhr12hsinβ/π.From the moment expression, the transducer can generate both the longitudinal vibration and the torsional vibration by means of the effect of the spiral groove, which can realize the longitudinal-torsional compound vibration.In order to realize the consolidation for metal foil, a consolidation disk should be installed at the front end of the compound horn with spiral grooves.


## 3. Optimization Design of Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

In order to realize the consolidation for metal foil, the calculation and analysis of the longitudinal-torsional compound consolidation vibration system are carried out, then the harmonic response analysis is carried out, the effect of structural parameters of the compound horn on the frequency of the consolidation vibration system is studied, and structural parameters of the compound horn are optimized [20–24].


### 3.1. Modal Analysis of Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

Through modal analysis, the vibration mode and frequency of the structure can be observed intuitively, and then the correct modal order can be selected to lay the foundation for the structural optimization.


#### 3.1.1. Modal Analysis of the Transducer

Modal analysis flow of the transducer is as follows. Firstly, NX and ANSYS are connected bidirectionally. Secondly, material properties of each component are defined for the transducer model, the contact type is defined, the mesh is generated, the number of modes is set to 6, and the frequency range is set between 15000 Hz and 21000 Hz. The transducer has no external load and belongs to free modal analysis. The simulation results show that the transducer belongs to the longitudinal vibration, the maximum amplitude is at the front of the front cover plate, the node position is on the left side of the front cover plate, the vibration frequency is 19801 Hz, the difference from the design frequency of 20 kHz is 199 Hz, and the error is 1% and less than 5%, which meets the engineering requirements.


#### 3.1.2. Modal Analysis of the Compound Horn

According to different spiral grooves of the compound horn, the modal analysis is carried out based on ANSYS, and the effect of the number of spiral grooves on modal frequency of the compound horn is shown in Figure6.Figure 6
The effect of the number of spiral grooves on frequency of the compound horn.It can be seen from Figure6 that the vibration frequency of the compound horn decreases with the increase of the number of spiral grooves. When the number of spiral grooves is 6, the vibration frequency of the compound horn is the closest to the design frequency of 20 kHz. As the number of spiral grooves increases, processing becomes more difficult, the strength and rigidity of the compound horn will decrease, and the stress concentration will appear, the damage is easy to occur. According to the simulation results, the number of spiral grooves can be 4, the vibration frequency of the compound horn is 21037 Hz, which is quite different from the theoretical design frequency, and the structural parameters need to be optimized further.


#### 3.1.3. Modal Analysis of Longitudinal-Torsional Compound Vibration System

According to the simulation results, the vibration frequency of the longitudinal-torsional compound vibration system without flange is 20576 Hz, the difference from theoretical design frequency of 20 kHz is 576 Hz, and the error is 2.88% and less than 5%, which meets the design requirements. The vibration frequency with flange is 20355 Hz, the solution result is shown in Figure7, the difference from theoretical design frequency of 20 kHz is 355 Hz, and the error is 1.78% and less than 5%, which meets the design requirements. The purpose of adding flange is to facilitate the positioning and clamping of longitudinal-torsional compound vibration system. Through the finite element modal calculation, all of them are within the allowable error range and meet the engineering requirements.Figure 7
Modal analysis of the longitudinal-torsional compound vibration system with flange.


### 3.2. Harmonic Response Analysis of Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

Harmonic response analysis belongs to frequency response analysis, also known as frequency-scanning analysis, which is the amplitude response of the system under the frequency excitation.Before harmonic response analysis of longitudinal-torsional compound consolidation vibration system, modal analysis is carried out firstly, the longitudinal-torsional frequency of compound consolidation vibration system is 20335 Hz, and the frequency response range can be set to 19000–21000 Hz. A point on the sonotrode is selected as the harmonic response point. After the harmonic response calculation, the amplitudes ofX, Y, and Z at the end of longitudinal-torsional compound consolidation vibration system are 9.31 μm, 9.22 μm, and 18.8 μm. The simulated longitudinal amplitude of the transducer is 3 μm, the theoretical amplitudes of the compound horn are 19.45 μm, and the error is 3.3%, which meets the design requirements.


### 3.3. Effect of Structural Parameters of the Compound Horn on the Frequency of the Consolidation Vibration System

Structural parameters of the compound horn include the lengthL1 of the small end cylinder, the length L2 of the big end conical part, the diameter D1 of the small end cylinder, the inner diameter D2 of the big end conical part, and the sector angle β of the big end conical part, as shown in Figure 6. Based on the parametric design function of NX, the parametric model of the compound horn was established and imported into ANSYS, and the bidirectional parameter transmission between them was established. The simulation analysis used single factor experiment method, the search frequency range was 18000–22000 Hz, and one parameter was changed each time to analyse the effect of structural parameters on the longitudinal-torsional frequency of the consolidation vibration system.The lengthL1 of the small end cylinder of the compound horn is 54–66 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 8. It can be seen that the frequency of the consolidation vibration system decreases with the increase of the length of the small end cylinder; that is to say, the length of the small end cylinder is inversely proportional to the frequency of the consolidation vibration system. When the length of the small end cylinder of the compound horn is about 63 mm, it is close to the design frequency of 20 kHz.Figure 8
The effect of the lengthL1 of the small end cylinder of the compound horn on vibration frequency.The diameterD1 of the small end cylinder of the compound horn is 9–15 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 9. It can be seen that the frequency of the consolidation vibration system increases first and then decreases with the increase of the diameter of the small end cylinder. When the diameter of the small end cylinder of the compound horn is 13–14 mm, it is close to the design frequency of 20 kHz.Figure 9
The effect of the diameterD1 of the small end cylinder of the compound horn on vibration frequency.The lengthL2 of the big end conical part of the compound horn is 44–56 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 10. It can be seen that the frequency of the consolidation vibration system decreases with the increase of the length of the big end conical part; that is, the length of the big end conical part is inversely proportional to the frequency of the consolidation vibration system. When the length of the big end conical part of the compound horn is about 53 mm, it is close to the design frequency of 20 kHz.Figure 10
The effect of the lengthL2 of the big end conical part of the compound horn on vibration frequency.The inner diameterD2 of the big end conical part of the compound horn is 27–33 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 11. It can be seen that the frequency of the consolidation vibration system decreases with the increase of the inner diameter of the big end conical part; that is to say, the inner diameter of the big end conical part is inversely proportional to the frequency of the consolidation vibration system. When the inner diameter of the big end conical part of the compound horn is about 31 mm, it is close to the design frequency of 20 kHz.Figure 11
The effect of the inner diameterD2 of the big end conical part of the compound horn on vibration frequency.The sector angleβ of the big end conical part of the compound horn is 30–60°, and the effect on the frequency of the consolidation vibration system is shown in Figure 12. It can be seen that the frequency of consolidation vibration system first decreases with the increase of the sector angle of the big end conical part, and when the sector angle is greater than 50°, the frequency of the consolidation vibration system increases.Figure 12
The effect of the sector angleβ of the big end conical part of the compound horn on vibration frequency.Through the effect of structural parameters of the compound horn on vibration frequency, it can be seen that the change of the lengthL1 of the small end cylinder, the length L2 of the big end conical part, the diameter D1 of the small end cylinder, the inner diameter D2, and the sector angle β of the big end conical part will affect vibration frequency, and the design size of the compound horn can be obtained from the analysis. Furthermore, the modal analysis can be carried out by establishing four factors and four levels orthogonal parameters to judge the effect of each parameter on the vibration frequency.


### 3.4. Optimization of Structural Parameters of the Compound Horn

Based on Design Exploration in ANSYS, structural parameters of the compound horn are optimized by response surface optimization. Design variablesP1, P2, P3, and P4 are the diameter D1 and the length L1 of the small end cylinder, the inner diameter D2, and sector angle β of the big end conical part; the variation range of design variables is ±10%; and the design variable P5 is the longitudinal-torsional frequency of the consolidation vibration system, which is the optimization objective. The mathematical model is shown in the following equation:(9)fiχ=fx1+x2+⋯⋯xngiχ=gix1+x2+⋯⋯xni=1,2⋯⋯nhiχ=hix1+x2+⋯⋯xni=1,2⋯⋯nwhere χ is the design variable and the value is taken according to the actual situation, fiχ is the objective function, giχ is the constraint function, and hiχ is the structural response function.Through optimization analysis, the effects ofP1, P2, P3, and P4 on the sensitivity of longitudinal-torsional frequency of the consolidation vibration system are obtained. The simulation results show that the length L1 (P2) of the small end cylinder and the inner diameter D2 (P3) of the big end conical part have an effect on the longitudinal-torsional frequency of the consolidation vibration system, which are important parameters to be considered in the optimization process.The data in the early stage and optimization data of longitudinal-torsional frequency of the consolidation vibration system in the after stage are shown in Table2. It can be seen that the optimization percentages of three groups of data are 1.8%, 1%, and 2%, respectively, which are less than 5% and meet the optimization requirements. Initial and correction values for design variables P1, P2, P3, and P4 are obtained.Table 2
Longitudinal-torsional vibration frequency before and after optimization.
Objective functionBefore optimizationAfter optimizationOptimization percentage (%)Longitudinal-torsional vibration frequency (Hz)20335199431.93200871.22198872.20After optimization, the amplitudes ofX, Y, and Z directions at the end of longitudinal-torsional compound consolidation vibration system are 9.55 μm, 9.44 μm, and 18.9 μm, respectively. The amplitudes before and after optimization are shown in Table 3. It can be seen that the optimization percentages of amplitudes in X, Y, and Z directions are 2.6%, 2.4%, and 0.5%.Table 3
Amplitudes before and after optimization.
Before optimization (μm)After optimization (μm)Optimization percentage (%)Z direction18.818.90.5X direction9.319.552.6Y direction9.229.442.4


### 3.5. The Relationship between the Structure of Spiral Groove and the Amplitude of Torsional Vibration

The structure of spiral groove is most key factor to torsional vibration of compound horn. The displacement in modal analysis is not an absolute value. Torsional-longitudinal ratioi can be used to measure the ratio between the longitudinal and torsional vibration component. Using the single factor variable analysis method, the curve of torsional-longitudinal ratio i with the sector angle β of spiral groove is shown in Figure 13; the curve of groove width w and groove depth s is shown in Figure 14.Figure 13
The effect of sector angleβ of spiral groove on torsional-longitudinal ratio i.Figure 14
The effect of groove widthw and groove depth s on torsional-longitudinal ratio i.It can be seen from Figure13 that torsional-longitudinal ratio i increases first, then decreases with the increase of sector angle β, and reaches the peak value at about sector angle 40°. It can be seen from Figure 14 that torsional-longitudinal ratio i increases with the increase of groove depth s, when groove width w increases, torsional-longitudinal ratio i is basically unchanged.


## 3.1. Modal Analysis of Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

Through modal analysis, the vibration mode and frequency of the structure can be observed intuitively, and then the correct modal order can be selected to lay the foundation for the structural optimization.


### 3.1.1. Modal Analysis of the Transducer

Modal analysis flow of the transducer is as follows. Firstly, NX and ANSYS are connected bidirectionally. Secondly, material properties of each component are defined for the transducer model, the contact type is defined, the mesh is generated, the number of modes is set to 6, and the frequency range is set between 15000 Hz and 21000 Hz. The transducer has no external load and belongs to free modal analysis. The simulation results show that the transducer belongs to the longitudinal vibration, the maximum amplitude is at the front of the front cover plate, the node position is on the left side of the front cover plate, the vibration frequency is 19801 Hz, the difference from the design frequency of 20 kHz is 199 Hz, and the error is 1% and less than 5%, which meets the engineering requirements.


### 3.1.2. Modal Analysis of the Compound Horn

According to different spiral grooves of the compound horn, the modal analysis is carried out based on ANSYS, and the effect of the number of spiral grooves on modal frequency of the compound horn is shown in Figure6.Figure 6
The effect of the number of spiral grooves on frequency of the compound horn.It can be seen from Figure6 that the vibration frequency of the compound horn decreases with the increase of the number of spiral grooves. When the number of spiral grooves is 6, the vibration frequency of the compound horn is the closest to the design frequency of 20 kHz. As the number of spiral grooves increases, processing becomes more difficult, the strength and rigidity of the compound horn will decrease, and the stress concentration will appear, the damage is easy to occur. According to the simulation results, the number of spiral grooves can be 4, the vibration frequency of the compound horn is 21037 Hz, which is quite different from the theoretical design frequency, and the structural parameters need to be optimized further.


### 3.1.3. Modal Analysis of Longitudinal-Torsional Compound Vibration System

According to the simulation results, the vibration frequency of the longitudinal-torsional compound vibration system without flange is 20576 Hz, the difference from theoretical design frequency of 20 kHz is 576 Hz, and the error is 2.88% and less than 5%, which meets the design requirements. The vibration frequency with flange is 20355 Hz, the solution result is shown in Figure7, the difference from theoretical design frequency of 20 kHz is 355 Hz, and the error is 1.78% and less than 5%, which meets the design requirements. The purpose of adding flange is to facilitate the positioning and clamping of longitudinal-torsional compound vibration system. Through the finite element modal calculation, all of them are within the allowable error range and meet the engineering requirements.Figure 7
Modal analysis of the longitudinal-torsional compound vibration system with flange.


## 3.1.1. Modal Analysis of the Transducer

Modal analysis flow of the transducer is as follows. Firstly, NX and ANSYS are connected bidirectionally. Secondly, material properties of each component are defined for the transducer model, the contact type is defined, the mesh is generated, the number of modes is set to 6, and the frequency range is set between 15000 Hz and 21000 Hz. The transducer has no external load and belongs to free modal analysis. The simulation results show that the transducer belongs to the longitudinal vibration, the maximum amplitude is at the front of the front cover plate, the node position is on the left side of the front cover plate, the vibration frequency is 19801 Hz, the difference from the design frequency of 20 kHz is 199 Hz, and the error is 1% and less than 5%, which meets the engineering requirements.


## 3.1.2. Modal Analysis of the Compound Horn

According to different spiral grooves of the compound horn, the modal analysis is carried out based on ANSYS, and the effect of the number of spiral grooves on modal frequency of the compound horn is shown in Figure6.Figure 6
The effect of the number of spiral grooves on frequency of the compound horn.It can be seen from Figure6 that the vibration frequency of the compound horn decreases with the increase of the number of spiral grooves. When the number of spiral grooves is 6, the vibration frequency of the compound horn is the closest to the design frequency of 20 kHz. As the number of spiral grooves increases, processing becomes more difficult, the strength and rigidity of the compound horn will decrease, and the stress concentration will appear, the damage is easy to occur. According to the simulation results, the number of spiral grooves can be 4, the vibration frequency of the compound horn is 21037 Hz, which is quite different from the theoretical design frequency, and the structural parameters need to be optimized further.


## 3.1.3. Modal Analysis of Longitudinal-Torsional Compound Vibration System

According to the simulation results, the vibration frequency of the longitudinal-torsional compound vibration system without flange is 20576 Hz, the difference from theoretical design frequency of 20 kHz is 576 Hz, and the error is 2.88% and less than 5%, which meets the design requirements. The vibration frequency with flange is 20355 Hz, the solution result is shown in Figure7, the difference from theoretical design frequency of 20 kHz is 355 Hz, and the error is 1.78% and less than 5%, which meets the design requirements. The purpose of adding flange is to facilitate the positioning and clamping of longitudinal-torsional compound vibration system. Through the finite element modal calculation, all of them are within the allowable error range and meet the engineering requirements.Figure 7
Modal analysis of the longitudinal-torsional compound vibration system with flange.


## 3.2. Harmonic Response Analysis of Longitudinal-Torsional Compound Consolidation Vibration System for Metal Foil

Harmonic response analysis belongs to frequency response analysis, also known as frequency-scanning analysis, which is the amplitude response of the system under the frequency excitation.Before harmonic response analysis of longitudinal-torsional compound consolidation vibration system, modal analysis is carried out firstly, the longitudinal-torsional frequency of compound consolidation vibration system is 20335 Hz, and the frequency response range can be set to 19000–21000 Hz. A point on the sonotrode is selected as the harmonic response point. After the harmonic response calculation, the amplitudes ofX, Y, and Z at the end of longitudinal-torsional compound consolidation vibration system are 9.31 μm, 9.22 μm, and 18.8 μm. The simulated longitudinal amplitude of the transducer is 3 μm, the theoretical amplitudes of the compound horn are 19.45 μm, and the error is 3.3%, which meets the design requirements.


## 3.3. Effect of Structural Parameters of the Compound Horn on the Frequency of the Consolidation Vibration System

Structural parameters of the compound horn include the lengthL1 of the small end cylinder, the length L2 of the big end conical part, the diameter D1 of the small end cylinder, the inner diameter D2 of the big end conical part, and the sector angle β of the big end conical part, as shown in Figure 6. Based on the parametric design function of NX, the parametric model of the compound horn was established and imported into ANSYS, and the bidirectional parameter transmission between them was established. The simulation analysis used single factor experiment method, the search frequency range was 18000–22000 Hz, and one parameter was changed each time to analyse the effect of structural parameters on the longitudinal-torsional frequency of the consolidation vibration system.The lengthL1 of the small end cylinder of the compound horn is 54–66 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 8. It can be seen that the frequency of the consolidation vibration system decreases with the increase of the length of the small end cylinder; that is to say, the length of the small end cylinder is inversely proportional to the frequency of the consolidation vibration system. When the length of the small end cylinder of the compound horn is about 63 mm, it is close to the design frequency of 20 kHz.Figure 8
The effect of the lengthL1 of the small end cylinder of the compound horn on vibration frequency.The diameterD1 of the small end cylinder of the compound horn is 9–15 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 9. It can be seen that the frequency of the consolidation vibration system increases first and then decreases with the increase of the diameter of the small end cylinder. When the diameter of the small end cylinder of the compound horn is 13–14 mm, it is close to the design frequency of 20 kHz.Figure 9
The effect of the diameterD1 of the small end cylinder of the compound horn on vibration frequency.The lengthL2 of the big end conical part of the compound horn is 44–56 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 10. It can be seen that the frequency of the consolidation vibration system decreases with the increase of the length of the big end conical part; that is, the length of the big end conical part is inversely proportional to the frequency of the consolidation vibration system. When the length of the big end conical part of the compound horn is about 53 mm, it is close to the design frequency of 20 kHz.Figure 10
The effect of the lengthL2 of the big end conical part of the compound horn on vibration frequency.The inner diameterD2 of the big end conical part of the compound horn is 27–33 mm, and the effect on the frequency of the consolidation vibration system is shown in Figure 11. It can be seen that the frequency of the consolidation vibration system decreases with the increase of the inner diameter of the big end conical part; that is to say, the inner diameter of the big end conical part is inversely proportional to the frequency of the consolidation vibration system. When the inner diameter of the big end conical part of the compound horn is about 31 mm, it is close to the design frequency of 20 kHz.Figure 11
The effect of the inner diameterD2 of the big end conical part of the compound horn on vibration frequency.The sector angleβ of the big end conical part of the compound horn is 30–60°, and the effect on the frequency of the consolidation vibration system is shown in Figure 12. It can be seen that the frequency of consolidation vibration system first decreases with the increase of the sector angle of the big end conical part, and when the sector angle is greater than 50°, the frequency of the consolidation vibration system increases.Figure 12
The effect of the sector angleβ of the big end conical part of the compound horn on vibration frequency.Through the effect of structural parameters of the compound horn on vibration frequency, it can be seen that the change of the lengthL1 of the small end cylinder, the length L2 of the big end conical part, the diameter D1 of the small end cylinder, the inner diameter D2, and the sector angle β of the big end conical part will affect vibration frequency, and the design size of the compound horn can be obtained from the analysis. Furthermore, the modal analysis can be carried out by establishing four factors and four levels orthogonal parameters to judge the effect of each parameter on the vibration frequency.


## 3.4. Optimization of Structural Parameters of the Compound Horn

Based on Design Exploration in ANSYS, structural parameters of the compound horn are optimized by response surface optimization. Design variablesP1, P2, P3, and P4 are the diameter D1 and the length L1 of the small end cylinder, the inner diameter D2, and sector angle β of the big end conical part; the variation range of design variables is ±10%; and the design variable P5 is the longitudinal-torsional frequency of the consolidation vibration system, which is the optimization objective. The mathematical model is shown in the following equation:(9)fiχ=fx1+x2+⋯⋯xngiχ=gix1+x2+⋯⋯xni=1,2⋯⋯nhiχ=hix1+x2+⋯⋯xni=1,2⋯⋯nwhere χ is the design variable and the value is taken according to the actual situation, fiχ is the objective function, giχ is the constraint function, and hiχ is the structural response function.Through optimization analysis, the effects ofP1, P2, P3, and P4 on the sensitivity of longitudinal-torsional frequency of the consolidation vibration system are obtained. The simulation results show that the length L1 (P2) of the small end cylinder and the inner diameter D2 (P3) of the big end conical part have an effect on the longitudinal-torsional frequency of the consolidation vibration system, which are important parameters to be considered in the optimization process.The data in the early stage and optimization data of longitudinal-torsional frequency of the consolidation vibration system in the after stage are shown in Table2. It can be seen that the optimization percentages of three groups of data are 1.8%, 1%, and 2%, respectively, which are less than 5% and meet the optimization requirements. Initial and correction values for design variables P1, P2, P3, and P4 are obtained.Table 2
Longitudinal-torsional vibration frequency before and after optimization.
Objective functionBefore optimizationAfter optimizationOptimization percentage (%)Longitudinal-torsional vibration frequency (Hz)20335199431.93200871.22198872.20After optimization, the amplitudes ofX, Y, and Z directions at the end of longitudinal-torsional compound consolidation vibration system are 9.55 μm, 9.44 μm, and 18.9 μm, respectively. The amplitudes before and after optimization are shown in Table 3. It can be seen that the optimization percentages of amplitudes in X, Y, and Z directions are 2.6%, 2.4%, and 0.5%.Table 3
Amplitudes before and after optimization.
Before optimization (μm)After optimization (μm)Optimization percentage (%)Z direction18.818.90.5X direction9.319.552.6Y direction9.229.442.4


## 3.5. The Relationship between the Structure of Spiral Groove and the Amplitude of Torsional Vibration

The structure of spiral groove is most key factor to torsional vibration of compound horn. The displacement in modal analysis is not an absolute value. Torsional-longitudinal ratioi can be used to measure the ratio between the longitudinal and torsional vibration component. Using the single factor variable analysis method, the curve of torsional-longitudinal ratio i with the sector angle β of spiral groove is shown in Figure 13; the curve of groove width w and groove depth s is shown in Figure 14.Figure 13
The effect of sector angleβ of spiral groove on torsional-longitudinal ratio i.Figure 14
The effect of groove widthw and groove depth s on torsional-longitudinal ratio i.It can be seen from Figure13 that torsional-longitudinal ratio i increases first, then decreases with the increase of sector angle β, and reaches the peak value at about sector angle 40°. It can be seen from Figure 14 that torsional-longitudinal ratio i increases with the increase of groove depth s, when groove width w increases, torsional-longitudinal ratio i is basically unchanged.


## 4. Experiments on the Longitudinal-Torsional Compound Piezoelectric Consolidation Vibration System for Metal Foil

Based on theoretical calculation and optimal design, the prototype of the longitudinal-torsional compound piezoelectric consolidation vibration system for metal foil was made.


### 4.1. The Test Platform for Longitudinal-Torsional Compound Consolidation Vibration System

The amplitude test platform for longitudinal-torsional compound consolidation vibration system is shown in Figure15. The test platform consists of laser vibrometer, signal generator, power amplifier, oscilloscope, and so forth. According to the principle of amplitude test, the amplitude test is carried out.Figure 15
The amplitude experiment platform.


### 4.2. The Amplitude Test Analysis of Longitudinal-Torsional Compound Consolidation Vibration System

The amplitude test of longitudinal-torsional compound consolidation vibration system includes frequency-scanning and fixed-frequency experiments. The purpose of frequency-scanning is to determine the resonance frequency of the consolidation vibration system; the purpose of fixed-frequency is to determine the amplitude of the consolidation vibration system at a given resonance frequency. The three-dimensional laser vibrometer is aligned with the end face of consolidation disk, the end-face data for meshing is collected by the host computer, and the meshing point is used as the test point. The end-face normal directionZ of consolidation disk is the longitudinal vibration direction, and the other two directions X and Y are the torsional vibration directions, which can be easily recognized by the host computer. The frequency-scanning test results are shown in Figure 16. It can be seen that the scanning range is 0–50000 Hz, X and Y are the torsional vibrations of the consolidation vibration system, Z is the longitudinal vibration. When the frequency is near 20000 Hz, the resonance is achieved in three directions at the same time, the resonance frequency is 19800 Hz, which is 200 Hz different from the design frequency of 20000 Hz, and the error is 1% and less than 5%. It meets the engineering requirements and proves that the structural design is reasonable.Figure 16
Frequency-scanning results of the consolidation vibration system.When the input frequency is 19800 Hz, the longitudinal amplitude change through the frequency-scanning test is shown in Figure17. It can be seen that the maximum longitudinal amplitude of the system is 16 μm, the longitudinal amplitude after optimization is 18.9 μm, and the error is 2.9 μm. The main reasons for the errors are as follows. The theoretical calculation ignores the error and is ideal. There are some errors in the processing and assembly of the prototype. There may be some human factors during the test, which have some random errors.Figure 17
Fixed-frequency longitudinal amplitude.When the input frequency is 19800 Hz, the change of torsional amplitude through the frequency-scanning test is shown in Figure18. It can be seen that maximum torsional amplitudes in X and Y directions of the system are 7.9 μm and 8.1 μm, the torsional amplitudes after optimization are 9.55 μm and 9.44 μm, and errors are 1.65 μm and 1.34 μm.Figure 18
Fixed-frequency torsional amplitude. (a)X direction and (b) Y direction.
(a)(b)


### 4.3. The Effect of Voltage on Amplitude in the Longitudinal-Torsional Compound Consolidation Vibration System

The amplitude of longitudinal-torsional compound consolidation vibration system is directly related to the input voltage; the relationship between the output amplitude of sonotrode and the input voltage is shown in Figure19. It can be seen that when the input voltage is 60–100 V, the output amplitude is 3–25 μm. The output amplitude increases gradually with the increase of the input voltage, and there is almost a linear change between them. When the input voltage is 60 V, the output longitudinal amplitude of sonotrode is 5.2 μm, the torsional amplitude in the X direction is 2.5 μm, and the torsional amplitude in the Y direction is 2.6 μm. When the input voltage is 100 V, the output longitudinal amplitude of sonotrode is 25.2 μm, the torsional amplitude in the X direction is 12.6 μm, and the torsional amplitude in the Y direction is 13.3 μm. The test data show that the output amplitude of sonotrode meets the consolidation requirements.Figure 19
The relation between the output amplitude and input voltage.


## 4.1. The Test Platform for Longitudinal-Torsional Compound Consolidation Vibration System

The amplitude test platform for longitudinal-torsional compound consolidation vibration system is shown in Figure15. The test platform consists of laser vibrometer, signal generator, power amplifier, oscilloscope, and so forth. According to the principle of amplitude test, the amplitude test is carried out.Figure 15
The amplitude experiment platform.


## 4.2. The Amplitude Test Analysis of Longitudinal-Torsional Compound Consolidation Vibration System

The amplitude test of longitudinal-torsional compound consolidation vibration system includes frequency-scanning and fixed-frequency experiments. The purpose of frequency-scanning is to determine the resonance frequency of the consolidation vibration system; the purpose of fixed-frequency is to determine the amplitude of the consolidation vibration system at a given resonance frequency. The three-dimensional laser vibrometer is aligned with the end face of consolidation disk, the end-face data for meshing is collected by the host computer, and the meshing point is used as the test point. The end-face normal directionZ of consolidation disk is the longitudinal vibration direction, and the other two directions X and Y are the torsional vibration directions, which can be easily recognized by the host computer. The frequency-scanning test results are shown in Figure 16. It can be seen that the scanning range is 0–50000 Hz, X and Y are the torsional vibrations of the consolidation vibration system, Z is the longitudinal vibration. When the frequency is near 20000 Hz, the resonance is achieved in three directions at the same time, the resonance frequency is 19800 Hz, which is 200 Hz different from the design frequency of 20000 Hz, and the error is 1% and less than 5%. It meets the engineering requirements and proves that the structural design is reasonable.Figure 16
Frequency-scanning results of the consolidation vibration system.When the input frequency is 19800 Hz, the longitudinal amplitude change through the frequency-scanning test is shown in Figure17. It can be seen that the maximum longitudinal amplitude of the system is 16 μm, the longitudinal amplitude after optimization is 18.9 μm, and the error is 2.9 μm. The main reasons for the errors are as follows. The theoretical calculation ignores the error and is ideal. There are some errors in the processing and assembly of the prototype. There may be some human factors during the test, which have some random errors.Figure 17
Fixed-frequency longitudinal amplitude.When the input frequency is 19800 Hz, the change of torsional amplitude through the frequency-scanning test is shown in Figure18. It can be seen that maximum torsional amplitudes in X and Y directions of the system are 7.9 μm and 8.1 μm, the torsional amplitudes after optimization are 9.55 μm and 9.44 μm, and errors are 1.65 μm and 1.34 μm.Figure 18
Fixed-frequency torsional amplitude. (a)X direction and (b) Y direction.
(a)(b)


## 4.3. The Effect of Voltage on Amplitude in the Longitudinal-Torsional Compound Consolidation Vibration System

The amplitude of longitudinal-torsional compound consolidation vibration system is directly related to the input voltage; the relationship between the output amplitude of sonotrode and the input voltage is shown in Figure19. It can be seen that when the input voltage is 60–100 V, the output amplitude is 3–25 μm. The output amplitude increases gradually with the increase of the input voltage, and there is almost a linear change between them. When the input voltage is 60 V, the output longitudinal amplitude of sonotrode is 5.2 μm, the torsional amplitude in the X direction is 2.5 μm, and the torsional amplitude in the Y direction is 2.6 μm. When the input voltage is 100 V, the output longitudinal amplitude of sonotrode is 25.2 μm, the torsional amplitude in the X direction is 12.6 μm, and the torsional amplitude in the Y direction is 13.3 μm. The test data show that the output amplitude of sonotrode meets the consolidation requirements.Figure 19
The relation between the output amplitude and input voltage.


## 5. Conclusion

(1)
During modal analysis, the longitudinal vibration frequency of the compound piezoelectric transducer was 19801 Hz. The vibration frequency of the compound horn decreased with the increase in the number of spiral grooves. The vibration frequency of longitudinal-torsional compound vibration system without flange was 20576 Hz and the vibration frequency with flange was 20335 Hz, which could meet the engineering requirements.(2)
During harmonic response analysis, the amplitudes ofX, Y, and Z directions at the end were 9.31 μm, 9.22 μm, and 18.8 μm. After optimization, the amplitudes of X, Y, and Z directions at the end were 9.55 μm, 9.44 μm, and 18.9 μm, respectively, which could meet the needs of engineering design.(3)
During the frequency-scanning and fixed-frequency test, the resonance frequency was 19800 Hz, the maximum longitudinal amplitude was 16μm, and the maximum torsional amplitudes in X and Y directions were 7.9 μm and 8.1 μm. When the input voltage was 60–100 V, the output amplitude of sonotrode was 3–25 μm. Relevant consolidation tests for metal foil will be carried out subsequently.



---