# Au-Loaded Titanium Dioxide Nanoparticles Synthesized by Modified Sol-Gel/Impregnation Methods and Their Application to Dye-Sensitized Solar Cells

Authors: Hathaithip Ninsonti; Weerasak Chomkitichai; Akira Baba; Natda Wetchakun; Wiyong Kangwansupamonkon; Sukon Phanichphant; Kazunari Shinbo; Keizo Kato; Futao Kaneko
Journal: International Journal of Photoenergy
 (2014)

---

## Abstract

Au-loaded TiO2 nanoparticles were synthesized by the modified sol-gel method together with the impregnation method. Anatase phase of TiO2 was obtained in all samples with an average particle size of 20 nm. For the enhancement of DSSCs, the dye-sensitized solar cells composed of the ITO/Au-loaded TiO2/N-719/electrolyte/Pt were fabricated. Au-loaded TiO2 films were deposited by using squeegee method. Finally, the fabricated cells were studied upon an irradiation of solar light to study the performance. The fabricated cell with up to 1.0 mol% Au-loaded TiO2 could enhance the performance by localized surface plasmon effect and scattering property.


---

## Body

## 1. Introduction

Recently, an increase in energy demand has led to significant progress in environmental remediation and renewable energy technologies such as photocatalytic oxidation, adsorption/separation processing, solar cells, fuel cells, and biofuels. One of the various renewable energy options, solar cell, stands out as the most ultimately sustainable choice in terms of its availability and huge potential. The solar cell for renewable energy options is applied through catalyst materials. Titanium dioxide (TiO2) is one of the most efficient materials for dye-sensitized solar cells (DSSCs) due to its chemical stability, nontoxicity, good electrical properties, and inexpensiveness [1–4]. The phase structure of TiO2 exists in three polymorphs: anatase, rutile, and brookite. The anatase TiO2 is used as dye-sensitized solar cells material because it has band gap energy of 3.2 eV of which the absorption thresholds correspond to 380 nm, suggesting that it is easy for photon-electron transfer under solar light irradiation [3]. At the present time many studies on dye-sensitized solar cells (DSSCs) have been reported due to their high efficiency property and low cost of materials [1–4].In the active layer of DSSCs, a monolayer of organic dye molecules covered with covalent bond on anatase TiO2 film is generally used [5]. When the metal nanoparticles are incorporated in TiO2 film of DSSCs, localized surface plasmon or light scattering can enhance the electric field on the active dye layer which can increase the light absorption [6–8]. Moreover, metal nanoparticles can perform as an electron acceptor from the photo-excited semiconductors. Therefore, the electron transfer rate could be improved and the increase of photocurrent was obtained [6, 9]. Au has several advantages such as high conductivity and chemical and thermal stability [10]. For these reasons, Au nanoparticles were chosen to induce light scattering and localized surface plasmon excitation for the improvement of DSSCs performance.There are many ways to synthesize TiO2 such as precipitation method [11–13], solvothermal method [14–17], sol-gel method [18–22], spray pyrolysis [23–26], and microwave method [27–29]. Sol-gel process consists of 2 main reactions, hydrolysis and condensation [18–22, 30–33]. In our previous work, we reported the preparation of TiO2 by the modified sol-gel method using cellophane membrane to decrease the diffusion rates of reactants in hydrolysis and condensation steps. This synthesis method had many advantages such as good reproducibility, good ability to obtain TiO2 in nanosized scale, and good production for high purity products [30, 31].In this research, TiO2 and Au-loaded TiO2 nanoparticles were synthesized by the modified sol-gel method and coupling the modified sol-gel with impregnation methods, respectively. The as-prepared samples were characterized by X-ray diffractometry, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectrophotometry, and Brunauer-Emmett-Teller techniques. The obtained particles were used to enhance DSSCs performance.


## 2. Experimental

### 2.1. Preparation of TiO2 Nanoparticles

Titanium dioxide (TiO2) nanoparticles were synthesized by the modified sol-gel method [30, 31]. Titanium tetraisopropoxide (Ti[OCH(CH3)2]4 (TTIP), Aldrich, England), absolute ethanol (C2H5OH, Merck, Germany), and ammonia (NH3, Merck, Germany) were used as the starting materials for synthesizing TiO2 nanoparticles. Titanium tetraisopropoxide (20 mL) was dissolved in 250 mL absolute ethanol and mixed until a homogeneous solution was obtained. The mixture of TTIP and absolute ethanol was loaded into a cellophane membrane and suspended for 1 h in a clear solution containing 1 : 1 ratio of ethanol (95%) and deionized water and 7 mL of ammonia solution (25%) as shown in Figure 1. After the completion of the dialysis process, the suspension was centrifuged at 7500 rpm for 10 min, washed with deionized water, and then dried in an oven at 60°C for 24 h. The white powders were then calcined in a furnace at a temperature of 400°C for 3 h.Figure 1
Scheme of the modified sol-gel method.


### 2.2. Preparation of Au-Loaded TiO2 Nanoparticles

The nominal 0.50–3.0 mol% Au-loaded TiO2 powders were prepared by the impregnation method. The appropriate amounts of gold (III) chloride hydrate ((H(AuCl4)·H2O, Electron Microscopy Science) solution were added in TiO2 nanoparticles as described previously in Section 2.1. Then, the as-prepared samples were mixed until being homogeneous. Finally, the obtained powders were dried at 60°C for 24 h and calcined at 400°C for 3 h.


### 2.3. Characterization of TiO2 and Au-Loaded TiO2 Nanoparticles

The crystal structure and crystallinity of TiO2 and Au-loaded TiO2 nanoparticles were examined by X-ray diffractometry (JDX-3530, JEOL, Japan) using the Ni-filtered monochromatic with CuKα radiation. The detection range was 15–75° with the step size of 0.10° (2θ°/s). Morphologies and particle sizes of TiO2 and Au-loaded TiO2 nanoparticles were investigated by scanning electron microscopy (SEM, JSM5410-LV, JEOL, Japan) and transmission electron microscopy (TEM, JEM-2010, JEOL, Japan). The chemical composition of TiO2 and Au-loaded TiO2 nanoparticles was examined by energy dispersive X-ray spectrophotometry (EDXS, ISIS300, Oxford, England). Specific surface area (SS
A
BET) of the samples was investigated by the Brunauer-Emmett-Teller (BET, Micromeritics Tristar 3000). An average particle diameter (d
BET) of TiO2 and Au-loaded TiO2 nanoparticles was calculated using the following formula: d
BET = 6
/
[
(
ρ
TiO
2
×
SS
A
BET
×
wt
.
%
Ti
O
2
)
+
(
ρ
Au
×
SS
A
BET
×
wt
.
%
Au
)
], where ρ
TiO
2 and ρ
Au are the weight densities of TiO2 (3.84
g
cm
-
3) and Au (19.30
g
cm
-
3), respectively.


### 2.4. Fabrication of DSSCs

DSSCs were fabricated by TiO2 and Au-loaded TiO2 nanoparticles for comparison of the efficiency performance. ITO glass substrate with a sheet resistance of 10 Ω/sq was used as an anode. Dish washing liquid solution, water, distilled water, and DI water were used for cleaning of ITO substrate. After cleaning process, squeegee technique was used to deposit TiO2 or Au-loaded TiO2 layers as follows: TiO2 or Au-loaded TiO2 nanoparticles were dispersed in ethanol with the concentration of 2, 3, 4, or 5 M in order to optimize the appropriate thickness. Then, TiO2 or Au-loaded TiO2 pastes were coated on ITO substrates by squeegee technique. TiO2 or Au-loaded TiO2 films were then calcined at 450°C for 90 min. To prevent the corrosion of Au particles by iodine electrolyte, Au-loaded TiO2 films were immersed in 0.001 M 1-octadecanethiol (CH3(CH2)17SH, Aldrich, England) for 15 h after calcination step. N-719 (di-tetrabutylammonium cis-bis (isothiocyanato) bis(2,2′-bipyridyl-4,4′-dicarboxylato) ruthenium (II), Sigma-Aldrich) was used as a photosensitized dye. TiO2 or Au-loaded TiO2 films were immersed in 0.5 mM N-719 dye for 12 h. DSSCs were fabricated as shown in Figure 2. 0.1 M LiI, 0.05 M I2, 0.6 M tBP, and 0.5 M tetrabutylammonium iodide in acetonitrile were used as electrolyte (for the optimization of the appropriate thickness, only 0.1 M LiI and 0.05 M I2 in acetonitrile were used as electrolyte). Pt film prepared by vacuum evaporation technique was used as the cathode.Figure 2
Scheme of fabricated dye-sensitized solar cells (DSSCs).


### 2.5. Characterization of the Fabricated DSSCs

The absorption of TiO2 and Au-loaded TiO2 films was observed by UV-vis spectroscopy technique (UV-vis spectrometer, V-650, JASCO). Photovoltaic properties were studied by irradiating a solar simulator (HAL-C100, 100 W compact xenon light source, ASAHI SPECTRA) to the fabricated DSSCs.


## 2.1. Preparation of TiO2 Nanoparticles

Titanium dioxide (TiO2) nanoparticles were synthesized by the modified sol-gel method [30, 31]. Titanium tetraisopropoxide (Ti[OCH(CH3)2]4 (TTIP), Aldrich, England), absolute ethanol (C2H5OH, Merck, Germany), and ammonia (NH3, Merck, Germany) were used as the starting materials for synthesizing TiO2 nanoparticles. Titanium tetraisopropoxide (20 mL) was dissolved in 250 mL absolute ethanol and mixed until a homogeneous solution was obtained. The mixture of TTIP and absolute ethanol was loaded into a cellophane membrane and suspended for 1 h in a clear solution containing 1 : 1 ratio of ethanol (95%) and deionized water and 7 mL of ammonia solution (25%) as shown in Figure 1. After the completion of the dialysis process, the suspension was centrifuged at 7500 rpm for 10 min, washed with deionized water, and then dried in an oven at 60°C for 24 h. The white powders were then calcined in a furnace at a temperature of 400°C for 3 h.Figure 1
Scheme of the modified sol-gel method.


## 2.2. Preparation of Au-Loaded TiO2 Nanoparticles

The nominal 0.50–3.0 mol% Au-loaded TiO2 powders were prepared by the impregnation method. The appropriate amounts of gold (III) chloride hydrate ((H(AuCl4)·H2O, Electron Microscopy Science) solution were added in TiO2 nanoparticles as described previously in Section 2.1. Then, the as-prepared samples were mixed until being homogeneous. Finally, the obtained powders were dried at 60°C for 24 h and calcined at 400°C for 3 h.


## 2.3. Characterization of TiO2 and Au-Loaded TiO2 Nanoparticles

The crystal structure and crystallinity of TiO2 and Au-loaded TiO2 nanoparticles were examined by X-ray diffractometry (JDX-3530, JEOL, Japan) using the Ni-filtered monochromatic with CuKα radiation. The detection range was 15–75° with the step size of 0.10° (2θ°/s). Morphologies and particle sizes of TiO2 and Au-loaded TiO2 nanoparticles were investigated by scanning electron microscopy (SEM, JSM5410-LV, JEOL, Japan) and transmission electron microscopy (TEM, JEM-2010, JEOL, Japan). The chemical composition of TiO2 and Au-loaded TiO2 nanoparticles was examined by energy dispersive X-ray spectrophotometry (EDXS, ISIS300, Oxford, England). Specific surface area (SS
A
BET) of the samples was investigated by the Brunauer-Emmett-Teller (BET, Micromeritics Tristar 3000). An average particle diameter (d
BET) of TiO2 and Au-loaded TiO2 nanoparticles was calculated using the following formula: d
BET = 6
/
[
(
ρ
TiO
2
×
SS
A
BET
×
wt
.
%
Ti
O
2
)
+
(
ρ
Au
×
SS
A
BET
×
wt
.
%
Au
)
], where ρ
TiO
2 and ρ
Au are the weight densities of TiO2 (3.84
g
cm
-
3) and Au (19.30
g
cm
-
3), respectively.


## 2.4. Fabrication of DSSCs

DSSCs were fabricated by TiO2 and Au-loaded TiO2 nanoparticles for comparison of the efficiency performance. ITO glass substrate with a sheet resistance of 10 Ω/sq was used as an anode. Dish washing liquid solution, water, distilled water, and DI water were used for cleaning of ITO substrate. After cleaning process, squeegee technique was used to deposit TiO2 or Au-loaded TiO2 layers as follows: TiO2 or Au-loaded TiO2 nanoparticles were dispersed in ethanol with the concentration of 2, 3, 4, or 5 M in order to optimize the appropriate thickness. Then, TiO2 or Au-loaded TiO2 pastes were coated on ITO substrates by squeegee technique. TiO2 or Au-loaded TiO2 films were then calcined at 450°C for 90 min. To prevent the corrosion of Au particles by iodine electrolyte, Au-loaded TiO2 films were immersed in 0.001 M 1-octadecanethiol (CH3(CH2)17SH, Aldrich, England) for 15 h after calcination step. N-719 (di-tetrabutylammonium cis-bis (isothiocyanato) bis(2,2′-bipyridyl-4,4′-dicarboxylato) ruthenium (II), Sigma-Aldrich) was used as a photosensitized dye. TiO2 or Au-loaded TiO2 films were immersed in 0.5 mM N-719 dye for 12 h. DSSCs were fabricated as shown in Figure 2. 0.1 M LiI, 0.05 M I2, 0.6 M tBP, and 0.5 M tetrabutylammonium iodide in acetonitrile were used as electrolyte (for the optimization of the appropriate thickness, only 0.1 M LiI and 0.05 M I2 in acetonitrile were used as electrolyte). Pt film prepared by vacuum evaporation technique was used as the cathode.Figure 2
Scheme of fabricated dye-sensitized solar cells (DSSCs).


## 2.5. Characterization of the Fabricated DSSCs

The absorption of TiO2 and Au-loaded TiO2 films was observed by UV-vis spectroscopy technique (UV-vis spectrometer, V-650, JASCO). Photovoltaic properties were studied by irradiating a solar simulator (HAL-C100, 100 W compact xenon light source, ASAHI SPECTRA) to the fabricated DSSCs.


## 3. Results and Discussion

### 3.1. Synthesis and Characterization of Au-Loaded TiO2 Nanoparticles

In this research, the TiO2 and Au-loaded TiO2 nanoparticles were prepared by the modified sol-gel method and the modified sol-gel method together with the impregnation method, respectively. The preparation of the TiO2 was followed from our previously reported research [30, 31]. The sol-gel method consists of hydrolysis and condensation of titanium alkoxides, Ti (OR)n, to form oxopolymers, which are converted to an oxide complex as equation mentioned in our previous report [30].The rates of hydrolysis and condensation are important factors that might affect characteristic of Au-loaded TiO2. Smaller particle sizes were obtained from hydrolysis and condensation rates which are controlled by basic solution [34–37]. Consequently, cellophane membrane was used to control the hydrolysis and condensation rates in the reaction to acquire the nanosized particles [30, 31]. Moreover, TiO2 loading with Au was produced by the impregnation method which is a very simple technique and does not require expensive equipment. The homogeneous powders of TiO2 show white color, while increase of Au ions changed the color to grayish purple.The structure confirmation of TiO2 and Au-loaded TiO2 nanoparticles was obtained by comparison with the Joint Committee on Powder Diffraction Standards (JCPDS) Card Files numbers 21-1272 and 04-0784. Figure 3 shows the XRD patterns of the TiO2 and 1.0 mol% Au-loaded TiO2 nanoparticles. The results of the TiO2 and 1.0 mol% Au-loaded TiO2 nanoparticles confirmed anatase structures according to JCPDS file number 21-1272 [30, 31]. The Au-loading might not affect the phase of TiO2 nanoparticles. The diffraction peaks of Au were found on Au-loaded TiO2 nanoparticles at 2θ value of 38.2°and 44.4° according to JCPDS file number 04-0784. The high intensity value of the XRD peaks shows that all of the samples have well crystalline structure and the broad peaks at 2θ value of 25.2° show that the particles have a small average crystallite size.Figure 3
XRD patterns of the TiO2 and 1.0 mol% Au-loaded TiO2 nanoparticles.The specific surface area (SS
A
BET) of the TiO2 and Au-loaded TiO2 nanoparticles was found to be in the range of 69–109 m2g−1 with the particle diameter in the range of 14–21 nm, corresponding well with the XRD results. It was reported that high surface area of TiO2 active layer has many advantages such as large amount of dye adsorption, high light-harvesting efficiency, rapid electron transport, and low electron recombination [38–40]. Therefore, high photoefficiency could be expected.Morphologies, particle sizes, and element chemical compositions were investigated by scanning electron microscopy (SEM) as shown in Figure4(a). The SEM result shows the rough morphology and the presence of agglomerated nanoparticles with an average diameter of 50–100 nm. From the EDS spectra as shown in Figure 4(e), the chemical compositions of 1.0 mol% Au-loaded TiO2 showed the characteristic X-ray energy level of titanium, oxygen. The characteristic peaks of Au were observed to confirm the presence of Au corresponding to the XRD results. Furthermore, element composition of Au-loaded TiO2 was investigated by EDS mapping mode. Figures 4(b), 4(c), and 4(d) show element composition of Ti, O, and Au in 1.0 mol% Au-loaded TiO2 nanoparticles. The presence of Au in the sample was confirmed. Further analysis for the accurate sizes and morphology of the nanoparticles was carried out by TEM observation. The average particle diameter of TiO2 and Au-loaded TiO2 nanoparticles was in the range of 15–20 nm as shown in Figure 5.(a) SEM micrographs and EDS mapping mode of (b) Ti, (c) O, (d) Au, and (e) EDS spectra of 1.0 mol% Au-loaded TiO2 nanoparticles.
(a)
(b)
(c)
(d)
(e)Figure 5
TEM micrograph of 1.0 mol% Au-loaded TiO2 nanoparticles.


### 3.2. Characterization and Optimization of Au-Loaded TiO2 Films

Figure6 shows the UV-vis absorption spectra of TiO2 and 0.50–3.0 mol% Au-loaded TiO2 films deposited on ITO substrate. A broad peak of Au appeared in the wavelength of 530–580 nm and increased intensity with increasing the Au loading amount on the TiO2 nanoparticles. This result indicated that the localized surface plasmon resonance could be excited on Au-loaded TiO2 nanoparticles [41]. As mentioned in the previously reported research by many groups, the film thickness is one of the most important factor effects on the performance of DSSCs [42, 43]. The film thickness was optimized by varying the concentration of 3.0 mol% Au-loaded TiO2 paste in the squeegee process. The thickness of 3.0% Au-loaded TiO2 films was increased with increasing the concentration of Au-loaded TiO2 paste, as shown in Figure 7(a). Figure 7(b) shows the effect of 3.0% Au-loaded TiO2 film thickness on short-circuit photocurrent properties of DSSCs. It was found that the short-circuit photocurrent increased with increasing film thickness up to 8 μm (Figure 7(c)). However, the photocurrent decreased with the film thickness more than 8 μm.Figure 6
UV-vis absorption spectra of TiO2 and 0.50–3.0 mol% Au-loaded TiO2 films deposited on ITO substrate.(a) Molar concentration of TiO2 paste versus film thickness of 3.0 mol% Au-TiO2 film. (b) Film thickness versus short-circuit photocurrent of 3.0 mol% Au-TiO2 film. (c) SEM image of 3.0 mol% Au-TiO2 film prepared by squeegee method with using 3 M TiO2 paste.
(a)
(b)
(c)


### 3.3. Photovoltaic Properties of the Fabricated DSSCs Using TiO2 and Au-Loaded TiO2 Nanoparticles

Photovoltaic properties of the fabricated DSSCs using TiO2 and different nominal 0.50–3.0 mol% of Au-loaded TiO2 nanoparticles were studied to compare the enhancement of photovoltaic performance of DSSCs. Figure 8 shows current density versus voltage (
J
-
V
) curves of fabricated DSSCs using TiO2 and 0.50–3.0 mol% Au-loaded TiO2 nanoparticles. Photovoltaic performances were calculated from these J
-
V curves as shown in Table 1. The open circuit voltage (V
oc) is almost constant value with Au-loading amount. This indicates that the Au-loading to TiO2 does not affect the Fermi level because the V
oc is originated from the energy difference between Fermi level of TiO2 layer and the oxidation/reduction potential of the electrolyte [44]. The results show that the short-circuit current densities (
J
sc
) of the fabricated DSSCs with TiO2, 0.50, 1.0, 2.0, and 3.0 mol% Au-loaded TiO2 nanoparticles were 10.04, 12.48, 13.06, 8.27, and 7.02 mA/cm2, corresponding to the efficiency (
η
) of 4.34, 5.40, 5.52, 4.13, and 3.33%, respectively. These results confirmed that Au-loading could enhance the performances of DSSCs with the loading amount up to 1.0 mol%. However, the short-circuit current density and the efficiency of the fabricated DSSCs were decreased upon the increasing amount of 2.0 mol% Au loading. These effects might be possibly due to the fact that the active site was shielded by the large amount of Au loading or rougher morphology of the Au-loaded TiO2 layers.Table 1
Photovoltaic performances of fabricated DSSCs using TiO2 and 0.50–3.0 mol% Au-loaded TiO2 nanoparticles.
V
oc (V)
J
sc (mA/cm2)
η (%)
FF
TiO2
0.75
10.04
4.34
0.43
0.50 mol% Au-TiO2
0.78
12.48
5.40
0.42
1.0 mol% Au-TiO2
0.78
13.06
5.52
0.44
2.0 mol% Au-TiO2
0.77
8.27
4.13
0.56
3.0 mol% Au-TiO2
0.77
7.02
3.33
0.39Figure 8
Current density versus voltage (J
-
V) curves of fabricated DSSCs using TiO2 and 0.50–3.0 mol% Au-loaded TiO2 nanoparticles.


## 3.1. Synthesis and Characterization of Au-Loaded TiO2 Nanoparticles

In this research, the TiO2 and Au-loaded TiO2 nanoparticles were prepared by the modified sol-gel method and the modified sol-gel method together with the impregnation method, respectively. The preparation of the TiO2 was followed from our previously reported research [30, 31]. The sol-gel method consists of hydrolysis and condensation of titanium alkoxides, Ti (OR)n, to form oxopolymers, which are converted to an oxide complex as equation mentioned in our previous report [30].The rates of hydrolysis and condensation are important factors that might affect characteristic of Au-loaded TiO2. Smaller particle sizes were obtained from hydrolysis and condensation rates which are controlled by basic solution [34–37]. Consequently, cellophane membrane was used to control the hydrolysis and condensation rates in the reaction to acquire the nanosized particles [30, 31]. Moreover, TiO2 loading with Au was produced by the impregnation method which is a very simple technique and does not require expensive equipment. The homogeneous powders of TiO2 show white color, while increase of Au ions changed the color to grayish purple.The structure confirmation of TiO2 and Au-loaded TiO2 nanoparticles was obtained by comparison with the Joint Committee on Powder Diffraction Standards (JCPDS) Card Files numbers 21-1272 and 04-0784. Figure 3 shows the XRD patterns of the TiO2 and 1.0 mol% Au-loaded TiO2 nanoparticles. The results of the TiO2 and 1.0 mol% Au-loaded TiO2 nanoparticles confirmed anatase structures according to JCPDS file number 21-1272 [30, 31]. The Au-loading might not affect the phase of TiO2 nanoparticles. The diffraction peaks of Au were found on Au-loaded TiO2 nanoparticles at 2θ value of 38.2°and 44.4° according to JCPDS file number 04-0784. The high intensity value of the XRD peaks shows that all of the samples have well crystalline structure and the broad peaks at 2θ value of 25.2° show that the particles have a small average crystallite size.Figure 3
XRD patterns of the TiO2 and 1.0 mol% Au-loaded TiO2 nanoparticles.The specific surface area (SS
A
BET) of the TiO2 and Au-loaded TiO2 nanoparticles was found to be in the range of 69–109 m2g−1 with the particle diameter in the range of 14–21 nm, corresponding well with the XRD results. It was reported that high surface area of TiO2 active layer has many advantages such as large amount of dye adsorption, high light-harvesting efficiency, rapid electron transport, and low electron recombination [38–40]. Therefore, high photoefficiency could be expected.Morphologies, particle sizes, and element chemical compositions were investigated by scanning electron microscopy (SEM) as shown in Figure4(a). The SEM result shows the rough morphology and the presence of agglomerated nanoparticles with an average diameter of 50–100 nm. From the EDS spectra as shown in Figure 4(e), the chemical compositions of 1.0 mol% Au-loaded TiO2 showed the characteristic X-ray energy level of titanium, oxygen. The characteristic peaks of Au were observed to confirm the presence of Au corresponding to the XRD results. Furthermore, element composition of Au-loaded TiO2 was investigated by EDS mapping mode. Figures 4(b), 4(c), and 4(d) show element composition of Ti, O, and Au in 1.0 mol% Au-loaded TiO2 nanoparticles. The presence of Au in the sample was confirmed. Further analysis for the accurate sizes and morphology of the nanoparticles was carried out by TEM observation. The average particle diameter of TiO2 and Au-loaded TiO2 nanoparticles was in the range of 15–20 nm as shown in Figure 5.(a) SEM micrographs and EDS mapping mode of (b) Ti, (c) O, (d) Au, and (e) EDS spectra of 1.0 mol% Au-loaded TiO2 nanoparticles.
(a)
(b)
(c)
(d)
(e)Figure 5
TEM micrograph of 1.0 mol% Au-loaded TiO2 nanoparticles.


## 3.2. Characterization and Optimization of Au-Loaded TiO2 Films

Figure6 shows the UV-vis absorption spectra of TiO2 and 0.50–3.0 mol% Au-loaded TiO2 films deposited on ITO substrate. A broad peak of Au appeared in the wavelength of 530–580 nm and increased intensity with increasing the Au loading amount on the TiO2 nanoparticles. This result indicated that the localized surface plasmon resonance could be excited on Au-loaded TiO2 nanoparticles [41]. As mentioned in the previously reported research by many groups, the film thickness is one of the most important factor effects on the performance of DSSCs [42, 43]. The film thickness was optimized by varying the concentration of 3.0 mol% Au-loaded TiO2 paste in the squeegee process. The thickness of 3.0% Au-loaded TiO2 films was increased with increasing the concentration of Au-loaded TiO2 paste, as shown in Figure 7(a). Figure 7(b) shows the effect of 3.0% Au-loaded TiO2 film thickness on short-circuit photocurrent properties of DSSCs. It was found that the short-circuit photocurrent increased with increasing film thickness up to 8 μm (Figure 7(c)). However, the photocurrent decreased with the film thickness more than 8 μm.Figure 6
UV-vis absorption spectra of TiO2 and 0.50–3.0 mol% Au-loaded TiO2 films deposited on ITO substrate.(a) Molar concentration of TiO2 paste versus film thickness of 3.0 mol% Au-TiO2 film. (b) Film thickness versus short-circuit photocurrent of 3.0 mol% Au-TiO2 film. (c) SEM image of 3.0 mol% Au-TiO2 film prepared by squeegee method with using 3 M TiO2 paste.
(a)
(b)
(c)


## 3.3. Photovoltaic Properties of the Fabricated DSSCs Using TiO2 and Au-Loaded TiO2 Nanoparticles

Photovoltaic properties of the fabricated DSSCs using TiO2 and different nominal 0.50–3.0 mol% of Au-loaded TiO2 nanoparticles were studied to compare the enhancement of photovoltaic performance of DSSCs. Figure 8 shows current density versus voltage (
J
-
V
) curves of fabricated DSSCs using TiO2 and 0.50–3.0 mol% Au-loaded TiO2 nanoparticles. Photovoltaic performances were calculated from these J
-
V curves as shown in Table 1. The open circuit voltage (V
oc) is almost constant value with Au-loading amount. This indicates that the Au-loading to TiO2 does not affect the Fermi level because the V
oc is originated from the energy difference between Fermi level of TiO2 layer and the oxidation/reduction potential of the electrolyte [44]. The results show that the short-circuit current densities (
J
sc
) of the fabricated DSSCs with TiO2, 0.50, 1.0, 2.0, and 3.0 mol% Au-loaded TiO2 nanoparticles were 10.04, 12.48, 13.06, 8.27, and 7.02 mA/cm2, corresponding to the efficiency (
η
) of 4.34, 5.40, 5.52, 4.13, and 3.33%, respectively. These results confirmed that Au-loading could enhance the performances of DSSCs with the loading amount up to 1.0 mol%. However, the short-circuit current density and the efficiency of the fabricated DSSCs were decreased upon the increasing amount of 2.0 mol% Au loading. These effects might be possibly due to the fact that the active site was shielded by the large amount of Au loading or rougher morphology of the Au-loaded TiO2 layers.Table 1
Photovoltaic performances of fabricated DSSCs using TiO2 and 0.50–3.0 mol% Au-loaded TiO2 nanoparticles.
V
oc (V)
J
sc (mA/cm2)
η (%)
FF
TiO2
0.75
10.04
4.34
0.43
0.50 mol% Au-TiO2
0.78
12.48
5.40
0.42
1.0 mol% Au-TiO2
0.78
13.06
5.52
0.44
2.0 mol% Au-TiO2
0.77
8.27
4.13
0.56
3.0 mol% Au-TiO2
0.77
7.02
3.33
0.39Figure 8
Current density versus voltage (J
-
V) curves of fabricated DSSCs using TiO2 and 0.50–3.0 mol% Au-loaded TiO2 nanoparticles.


## 4. Conclusion

In this research, the Au-loaded TiO2 nanoparticles were successfully synthesized by the modified sol-gel method together with the impregnation method. Anatase phase of TiO2 was obtained in all samples with an average particle size of 20 nm. The DSSC was improved by an effect of the Au-loaded titanium dioxide (Au-loaded TiO2). For the enhancement of DSSCs, the fabricated cell with up to 1.0 mol% Au-loaded TiO2 could enhance the performance by localized surface plasmon effect and scattering property.



---