# Quantum-Dot and Polychalcone Mixed Nanocomposites for Polymer Light-Emitting Diodes

Authors: Vanaraj Ramkumar; Sanghyun Ju
Journal: Journal of Nanomaterials
 (2017)

---

## Abstract

The present work is aimed at improving the efficiency of light-emitting diodes (LEDs) through the amalgamation of polymeric materials and quantum dots (QDs) in nanocomposites. Herein, we report on the polytriphenylamine-based chalcone (PTpC) or polycarbazole-based chalcone- (PCzC-) QDs mixture nanocomposites as emissive layers for polymer LEDs (PLEDs). QDs were evenly dispersed in the polymer matrix and the synthesized PTpC-QDs and PCzC-QDs nanocomposites were able to form smooth thin films. The luminance characteristics of PTpC-QDs and PCzC-QDs nanocomposites were better than those of the pristine QD, PTpC, and PCzC materials, owing to the high charge-carrier transport ability of polymer-QDs nanocomposites. These results indicate that the proposed polymer-QDs nanocomposites could be potential candidates for application in PLEDs.


---

## Body

## 1. Introduction

Recently, significant efforts have been placed in developing high-performance polymeric materials in optoelectronic applications, including polymer light-emitting diodes (PLEDs) [1–3]. The PLEDs with multilayer structures (hole injection layer (HIL)/hole transfer layer (HTL)/emission layer (EML)/electron transfer layer (ETL)/electron injection layer (EIL)) should theoretically show better electrooptical characteristics compared to PLEDs with unilayer (EML only) and bilayer structures (HIL/EML) [4–6]. However, there are performance degradation issues during the formation of multilayers [6, 7]. In order to solve this issue, conjugated polymer-based LEDs have received particular attention because the conjugated polymer could provide a high carrier transport ability, which could play a multiple role as HTL, ETL, and EIL, in the EML [8–10]. As a result, conjugated polymer-based LEDs could provide high-performance properties in terms of high luminance, high efficiency, and low voltage operation, while allowing for inexpensive and easier fabrication process techniques [4–6]. Among conjugated polymers, several studies have been conducted on polymer-nanoparticle mixtures, especially polymer quantum dots (QDs) materials [11–14]. In polymer-nanoparticle composites, the uniform dispersion of nanoparticles offers advantages over those cases where nanoparticle aggregation dominates. In addition, polymers with different architectures, such as homo- and copolymers, hyperbranched polymers, and polymeric nanogels, have been employed to anchor and coat QDs for fabricating photonic polymer-QDs materials [14, 15].QDs materials have been widely used to fabricate display devices because of their unique physical properties, especially their tunable band gap energy derived by tuning the particle size, which generates the quantum confinement effect [7]. However, because of their charge immobility, indissolubility, and photoluminescence instability, QDs usually need to be modulated by a passivation process to increase the luminance efficiency of the device [8]. To achieve this goal, polymers with excellent charge mobility and high stability are widely employed to modify the QDs for display and photonic applications [9, 10]. The modification of QDs including surface functionalization could improve the photoluminescence quantum yield for organic or inorganic capped nanoparticles [10, 11]. On the other hand, inorganic nanoparticles, including QDs, generally produce poor film formation because they are based on powders, which results in the disconnection between nanoparticles. Therefore, the nanoparticles should be uniformly dispersed in conductive solution-based polymers, which could connect the inorganic nanoparticles by providing high charge-carrier mobility [11, 12].In this study, polymer-QDs (PTpC-QDs and PCzC-QDs) nanocomposites were synthesized, and their chemical structures and optical properties were investigated. The two polymers, PTpC and PCzC, were combined with QDs by surface functionalization. The synthesized PTpC-QDs and PCzC-QDs nanocomposites were used to fabricate PLED devices as an EML, and their luminescence characteristics were compared with those of the LEDs with the pristine PTpC, PCzC, and QDs.


## 2. Experimental Section

Synthesis of polymers (PTpC and PCzC) and polymer-QDs nanocomposites (PTpC-QDs and PCzC-QDs): Cyclohexanone, 4,4′-diformyltriphenylamine, 9-(2-ethylhexyl)carbazole-3,6-dicarboxaldehyde, sodium hydroxide, ethanol, and QDs (CdSeS@ZnS for red, CdZnSeS@ZnS for green, and CdZnS@ZnS for blue) were used to synthesize PTpC, PCzC, PTpC-QDs, and PCzC-QDs. The analogous chalcone polymers (PTpC and PCzC) were synthesized by using the standard Claisen–Schmidt condensation reaction from the respective aldehydes and ketone [15]. For PTpC, equimolar (0.009 mmol) of aldehyde (4,4′-diformyltriphenylamine) and ketone (cyclohexanone) were dissolved in absolute ethanol (60 mL) and the mixture was stirred at 10°C for 30 min. An aqueous solution of sodium hydroxide (5 mL, 10%) was slowly added to the reaction mixture. At the end of the reaction (6 h), the mixture was poured onto ice-cold water (500 mL) and set aside for 10 h. The precipitated crude solid was collected by filtration, dried in a hot air oven, and purified by repeated methanol [9]. A similar procedure was adopted to synthesize the polymer PCzC, from the respective aldehyde (9-(2-ethylhexyl)carbazole-3,6-dicarboxaldehyde) and ketone (cyclohexanone). The molecular weight of the polymers was obtained by gel permeation chromatography, and the molecular weights of PTpC and PCzC were 9750 and 7189, respectively. The polymer-QDs nanocomposites (PTpC-QDs and PCzC-QDs) were obtained as follows: 0.5 g of each polymer (PTpC or PCzC) was dissolved with 20 mL of chloroform, and 1 mL of each QD (R, G, and B) solution was added to them. The mixture was stirred for 3 h at room temperature. The stirred solution was allowed to settle as a precipitate for about 5 h. The mixture was filtered through Whatman filter paper, and the precipitate nanocomposite was collected for further analysis.Measurements of the synthesized polymers and polymer-QDs nanocomposites: The Fourier transform infrared (FT-IR) spectra of the polymers were recorded in the range of 600 to 4000 cm−1 using a Bruker IFS 66V Fourier transform spectrometer. High resolution 1H-NMR spectra were recorded on a 500 Hz AVANCE III spectrometer in CDCl3 with tetramethylsilane as an internal standard. Thermogravimetric analysis (TGA) was performed on a Mettler TA 3000 thermal analyzer under a nitrogen atmosphere at a heating rate of 5°C min−1 with a sample weight of 2–4 mg. Emission spectra were obtained from a Perkin–Elmer II fluorescence spectrophotometer.Fabrication and measurement of the PLED devices: PLED devices were fabricated by using pure polymers (PTpC and PCzC), QDs (CdSeS@ZnS for red, CdZnSeS@ZnS for green, and CdZnS@ZnS for blue), and the polymer-QDs nanocomposites as an EML. 100 nm thick ITO electrode was deposited on Corning glass by sputtering for use as an anode. The 40 nm thick poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) (PEDOT/PSS) as a HIL was coated on the ITO patterned substrates. The EMLs (PTpC, PCzC, QDs (R, G, and B), PTpC-QDs (R, G, and B), or PCzC-QDs (R, G, and B)) with the thickness of ~80 nm were spin-coated on HIL/ITO substrates. The 150 nm thick aluminum as a cathode electrode was then deposited onto the EML by using sputtering. The EL spectra and luminescence-current-voltage (LIV) characteristics of the fabricated PLED devices were recorded with a Konica-Minolta CS-1000 spectroradiometer coupled with a Keithley 2400 voltage and current source under ambient conditions.


## 3. Results and Discussion

A summary of the synthetic scheme of the target polymers, PTpC and PCzC, is presented in Figure1(a). The synthesized polymers (PTpC and PCzC) were confirmed by using FT-IR and 1H-NMR analysis. The FT-IR spectra of the polymers (PTpC and PCzC) revealed the vibration frequencies of the materials (Figure 1(b)). The stretching vibration at 3083 cm−1 indicated the presence of aromatic C=C. The characteristic peak of the C–H group appeared at 800–1200 cm−1. The characteristic carbonyl (C=O) band is assigned at 1707 cm−1 [12]. An intense sharp band at 1071 cm−1 was observed because of C–H stretching vibration, and –CH2 ring stretching was also observed at 2857 cm−1. As shown in Figure 1(c), the 1H-NMR spectra of the polymeric compounds show multiplet peaks for each aliphatic –CH and –CH2 proton between 1.25 and 6.25 ppm. The multiplet peaks at 7–9 ppm were due to the presence of aromatic protons in PTpC and PCzC [10].Figure 1
(a)
(b)
(c)
(d)Thermal stability is a significant factor in PLED device, because a material with poor thermal stability causes rapid degradation of EML and leads to decomposition of materials at high temperature. The thermogravimetric analysis (TGA) was used to determine thermal stability of the synthesized polymers. Figure1(d) shows the TGA results of the synthesized polymers PTpC and PCzC. The initial weight loss (Ti) occurred at ~290 and 295°C for PTpC and PCzC, respectively, because of the first decomposition of the polymers. The second weight loss of PTpC and PCzC was obtained at ~550 and 560°C, respectively. Both polymers, PTpC and PCzC, were thermally stable up to 290 and 295°C, respectively. These high Ti values indicate that the thermal stability of polymers makes them suitable for the fabrication of PLED devices.Figures2(a) and 2(b) show the fluorescence spectra of PTpC and PCzC in power, solution, and thin film. The PTpC possessed a broad peak from ~400 to 650 nm in powder and the maximum emission peak at 540 nm in solution and 560 nm in thin film. On the other hand, the PCzC exhibited a broad peak from 450 to 720 nm in powder and a maximum emission peak at 520 nm in solution and at 600 nm in thin film. The powders of PTpC and PCzC showed reddish yellow and yellow emission with a broad bandwidth. The emission peak of PTpC was red-shifted compared to that of PCzC because of the different substitution group of the polymers. Because PTpC has a more planar structure than PCzC, the molecules in PTpC are better aligned and possess higher molecular weight than in PCzC. As the molecular weight increases, the number of repeating units also increases. It leads to the π-conjugation extension of the polymer. The different maximum emission peaks of the PTpC and PCzC between thin film and solution were due to the well-aligned molecules and no interaction with solvent. The different bandwidth was due to the molecular arrangement of the polymers [16–18]. Since the molecular alignment in powder is much closer than that in solution and thin film, PTpC and PCzC in powder exhibit broad peaks. On the other hand, the PTpC and PCzC in solution show the narrow peak because the molecules were divided by the solvent interaction.Figure 2
(a)
(b)
(c)
(d)Figures2(c) and 2(d) show the photo images of the PTpC and PCzC in powder, solution, and thin film states under UV light (365 nm) exposure. As shown in the figures, PTpC and PCzC in powder, solution, and thin film showed different colors under UV light exposure.In order to secure an efficient charge transfer between the QDs and the polymer, it is important to control the dispersibility of the QDs in the polymer and the improvement of the interface between polymer and QDs. The dispersibility of the QDs in the polymer is directly related to the physisorption of polymers on the surface of QDs. The electroactive surfactants, such as the conjugated polymers, PTpC and PCzC, could improve the transfer of charges between the QDs and the polymers. The polymer, which passivated the surface of QDs, could improve the interface between the polymer and QDs providing an efficient charge injection into the QDs. The interface between QD and polymer plays an important role in the determination of the luminescent properties of the PLED devices, because of the carrier transfer efficiency.In order to observe the dispersibility of QDs in the polymer, the surface morphology of the two polymers (PTpC and PCzC), three QDs (CdSeS@ZnS for red, CdZnSeS@ZnS for green, and CdZnS@ZnS for blue), and six polymer-QDs nanocomposites were observed through the FE-SEM. The FE-SEM images of PTpC and PCzC in Figures3(a) and 3(b) exhibited plain uniform morphology. In general, the polymer has the ability to form a smooth and plain morphology, because of its repeating units and high molecular weight. The triphenyl and carbazole group induced aggregation of the polymer molecules and π–π stacking interaction between the molecules, resulting in a uniform surface morphology. Figures 3(c) and 3(e) illustrate the FE-SEM morphology of the three QDs before and after combining with PTpC or PCzC. As depicted in the figures, the QDs were binding well with the polymers, showing uniform spherical structure. This result indicates that polymer-QDs nanocomposites could provide uniform dispersion of the QDs phase throughout the host polymer matrix on the microscopic level.Figure 3
(a)
(b)
(c)
(d)
(e)Figure4 shows the normalized electroluminescence spectra of the pristine QDs and polymer-QDs nanocomposites in thin films. The pristine QDs (R, G, and B) exhibited emission peaks at 615, 525, and 445 nm, respectively. The EL spectra of PTpC-QDs (R, G, and B) nanocomposites exhibited three peaks, 617, 529, and 450 nm, while the PCzC-QDs (R, G, and B) nanocomposites possess peaks at 620, 528, and 452 nm, respectively. The relative peaks of the PCzC-QDs (R, G, and B) nanocomposite devices were ~2–5 nm red-shifted to PTpC-QDs (R, G, and B) nanocomposite devices, indicating that the recombination zone of electrons and holes in the carbazole is higher than that of the triphenylamine based nanocomposite. Figure 4(c) presents different blue, green, and red emission images of the polymer-QDs nanocomposites on the plastic substrates under UV (365 nm) illumination. The strong blue, green, and red emissions were obtained for both the pristine QDs and polymer-QDs nanocomposites. The emission behaviors of the polymer-QDs nanocomposites are based on the charge transfer of the molecule, which occurs between the C=O parts of the chalcone group. The conjugation part of the polymer acts as an electron transfer and linking group between the triphenyl amine and carbonyl group (C=O) of the polymer.Figure 4
(a)
(b)
(c)Figure5(a) shows the schematic of the device structure of ITO (100 nm)/PEDOT:PSS (40 nm)/EML (80 nm)/Al (150 nm). Figures 5(b)–5(d) show the LIV characteristics of the three types of devices by using the pristine QDs (R, G, and B), PTpC-QDs (R, G, and B) nanocomposites, and PCzC-QDs (R, G, and B) nanocomposites as an EML. The turn-on voltages of the devices of the pristine QDs (R, G, and B), PTpC-QDs (R, G, and B) nanocomposites, and PCzC-QDs (R, G, and B) nanocomposites were 4.6, 7.5, 7.0, 4, 5.1, 6.4, 4.1, 5.3, and 6.2 V, respectively. The PTpC-QDs or PCzC-QDs nanocomposites showed a low turn-on voltage compared to those of the pristine polymer and the pristine QDs, owing to the high charge transporting ability of the polymers. The triphenylene and carbazole groups are usually considered as electron donors, and they have an excellent hole transporting property as well. The maximum luminance values of the devices with the pristine QDs (R, G, and B), PTpC-QDs (R, G, and B) nanocomposites, and PCzC-QDs (R, G, and B) nanocomposites were observed as 107, 11, 27, 265, 170, 89, 256, 160, and 90 cd/m2, respectively. The fabrication part involves the bilayer efficiency analysis of the raw QDs, polymers, and polymer nanocomposites (PTpC-QDs and PCzC-QDs). The devices with the pristine QDs as an EML showed very low luminance values due to the lack of the other layers (HTL, ETL, and EIL), which made it difficult to apply the hole injection to EML and resulted in an unbalanced number of electrons and holes in the EML. On the other hand, PTpC-QDs and PCzC-QDs nanocomposites showed higher luminance properties due to the charge transfer between the QDs and the polymer. The insets in Figure 5 show current density of the pristine QDs (R, G, and B), PTpC-QDs (R, G, and B) nanocomposites, and PCzC-QDs (R, G, and B) nanocomposites.Figure 5
(a)
(b)
(c)
(d)Since the physicochemical properties of the PTpC-QDs and PCzC-QDs nanocomposites differed from those in the parent materials, PTpC and PCzC, the charge mobility and the emission properties of the nanocomposites were different from those in the pristine polymer and the pristine QDs. The presence of QDs in the polymer enhances the photoinduced charge generation efficiency, while the polymer can be responsible for the charge transport to the electrodes. The energy levels of the polymeric host and the QDs can be tuned by a different polymeric backbone and by mixing the QDs with the polymer. These modifications increase the charge transport and luminance of the PELD devices. As a result, a polymer-QD nanocomposite device could provide enhanced hole/electron injection and luminance efficiency compared to polymer-only and QDs-only devices.


## 4. Conclusion

In summary, we reported on two polymer (PTpC and PCzC)-QDs nanocomposites for PLEDs. The two polymers were used as grafting agents on core-shell QD nanoparticles. Electron transfer processes between the QDs and the surrounding polymer matrix are essential in a range of optoelectronic devices including PLEDs. Functionalization of the QD surface with electroactive polymers was therefore explored with the aim of facilitating the charge transfer across the interface between polymer and QDs. These hybrid polymer-QDs nanocomposites possess versatile properties, providing luminescence enhancement based on the increase of conductivity and the uniform formation of thin film. The fabricated PLED devices with polymer-QDs nanocomposites as an EML showed better luminescent characteristics compared to those of PLED devices with the pristine polymer or the pristine QDs as EML. The charge transfer between the QDs and the polymer played a key role for the increase of luminescence and efficiency of the PLED devices with polymer-QDs nanocomposites. The proposed polymer-QDs nanocomposite materials could be significant candidates for application in PLEDs.



---

*Source: 8739193-2017-10-23.xml*