# Structural and Ferroic Properties of La, Nd, and Dy Doped BiFeO3 Ceramics

Authors: Ashwini Kumar; Poorva Sharma; Dinesh Varshney
Journal: Journal of Ceramics
 (2015)

---

## Abstract

Polycrystalline samples of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) have been synthesized by solid-state reaction route. X-ray diffraction (XRD) patterns of Bi0.8La0.2FeO3 and Bi0.8Nd0.2FeO3 were indexed in rhombohedral (R3c) and triclinic (P1) structure, respectively. Rietveld refined XRD pattern of Bi0.8Dy0.2FeO3 confirms the biphasic (Pnma + R3c space groups) nature. Raman spectroscopy reveals the change in BiFeO3 mode positions and supplements structural change with RE ion substitution. Ferroelectric and ferromagnetic loops have been observed in the Bi0.8RE0.2FeO3 ceramics at room temperature, indicating that ferroelectric and ferromagnetic ordering coexist in the ceramics at room temperature. The magnetic measurements at room temperature indicate that rare-earth substitution induces ferromagnetism and discerns large and nonzero remnant magnetization as compared to pristine BiFeO3.


---

## Body

## 1. Introduction

Multiferroic materials, such as BiFeO3 (BFO), have been a subject of unprecedented interest due to coexistence of simultaneous ferroelectric and antiferromagnetic/ferromagnetic ordering in the same phase [1]. These are studied extensively due to their wide range of potential applications, including information-storage device, spintronics, and sensors [2, 3]. The common exclusive nature of magnetism and electric polarization makes natural multiferroic materials rare [3, 4]. Needless to say, majority of compounds have low ordering temperatures; however room temperature achievement has yet to be noticed. BFO has a rhombohedrally distorted perovskite structure (space groupR3c) [5] with high Curie temperature (TC~1100 K) and antiferromagnetic Neel temperature (TN~675 K) with a spatially modulated spiral spin structure [6, 7].Efforts have been made to improve the ferroelectric and magnetic properties in antiferromagnetic BiFeO3 ceramic. Enhancing the magnetic moments by reducing particle size of BFO has been one of the important tasks [8]. Ion substitution in BFO is believed to be effective and the most convenient way to enhance the ferroelectric and magnetic properties. From the existing literature, it has been earlier observed that partial substitution of rare-earth (RE) elements like La [9], Pr [10], Nd [11, 12], Gd [13], Dy [14], and Ho [15] at Bi site can eliminate the impurity phase along with a structural phase transformation and improve ferroelectric properties and induced ferromagnetism in BFO ceramic. The relationship between the structural, evolution, and magnetic properties among these doped BFO ceramics still needs further investigations. With these priorities, we have synthesized RE ions doped (Bi site) BFO ceramics.A structural phase transition from rhombohedral to orthorhombic structure is observed inBi1-xLaxFeO3 near x=0.3 and enhances the magnetoelectric interaction [9]. For Nd doped BiFeO3 a rhombohedral structure at x=0, a triclinic structure between x=0.05 and 0.15, and a pseudotetragonal structure between x=0.175 and 0.2 have been reported [11]. A structural transformation from rhombohedral to monoclinic structure for Bi1-xNdxFeO3 (x=0.0–0.15) ceramic prepared by an improved rapid liquid phase sintering method is also reported [12]. On the other hand, 20% Dy substitution confirms the orthorhombic structure withPnma structural model [14]. Substitutional effect of Ho on BFO bulk ceramic infers that the remnant polarization (Pr) and switching characteristic were improved at low field by reducing the leakage current apart from enhanced ferromagnetic properties [15]. These improved properties obtained byRE doping demonstrate the possibility of enhancing multiferroic applicability of BFO.From this viewpoint, it is necessary to be aware of the crystal structure of compounds. Keeping the important features in mind and taking interesting crystallography of BiFeO3 into consideration, it is worth studying the properties of rare-earth doped Bi-ferrite. We have thus synthesized rare-earth substituted BiFeO3 abbreviated as Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) multiferroic samplesvia solid-state reaction route and reported the consistency of evolution of crystal structure, dielectric, electrical, and magnetic properties. The synthesized samples of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) are further designated as BLFO, BNFO, and BDFO, respectively.


## 2. Experimental Details

Polycrystalline samples with the composition Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) were prepared by conventional solid-state route and the typical synthesized process is described as follows. For the synthesis of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) ceramics Bi2O3 (Loba Chemie, 99.9% purity), Fe2O3 (Sigma-Aldrich, 99.99% purity), La2O3 (Sigma-Aldrich, 99.9% purity), Nd2O3 (Loba Chemie, 99.9% purity), and Dy2O3 (Loba Chemie, 99.9% purity) reagents were used as starting materials. All the chemicals were of GR grade and were used without any further purification. All the starting materials were weighed, mixed, and grounded thoroughly in an agate mortar for 6 hours using acetone and calcined for 6 hours at 650°C for the desired composition of Bi0.8RE0.2FeO3. All the calcined compositions were uniaxially dye-pressed into pellets of size 10 mm in diameter and 2 mm in thickness. Sintering was performed at 820°C for 3 hours, with intermediate grinding.X-ray diffraction was carried out with CuKα1 (1.5406 Å) radiation using Bruker D8 Advance X-ray diffractometer over the angular range 2θ (20°–80°) with a scanning rate of 2° per minute at room temperature working at 40 kV voltage and 40 mA current. The lattice parameters and other detailed structural information were obtained by the Rietveld refinement FullPROF program [16]. Raman measurements were carried out using LabRam HR800 micro-Raman spectrometer equipped with a 50x objective, an appropriate edge filter, and a Peltier-cooled charge coupled device detector. The spectra were excited with 488 nm radiations (2.53 eV) from an air-cooled Argon laser. Ferroelectric hysteresis (P-E) loop of the samples was measured using RT6000 (Radiant Technologies, USA) at frequency 50 Hz. The magnetization as a function of applied field (M-H) curve for BNFO sample at room temperatures was performed using a superconducting quantum interference device (SQUID) magnetometer (MPMS, Quantum Design). However, for BLFO and BDFO samples magnetic measurements were performed using vibrating sample magnetometer (VSM-lakeshore).


## 3. Results and Discussion

### 3.1. Structural Analysis

Figure1 shows the XRD pattern of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) ceramic samples. From the measured XRD pattern it has been observed that all the samples exhibit different crystal structures. BLFO sample was indexed in rhombohedral structure with space groupR3c where all the diffraction peaks match closely with the JCPDS file number 86-1518. A minor low level impurity phase (marked with *) was detected around 2θ≈28° associated with Bi2Fe4O9 [17]. This impurity peak matches well with the JCPDS file number 72-1832. The diffraction peaks change in both intensity and 2θ values with different dopant ionic radii as a result of change in crystal structure [18]. The values of lattice constants were manually calculated using different forms of crystal structures as defined earlier [19].Figure 1
Room temperature XRD pattern of the Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples designated as BLFO, BNFO, and BDFO, respectively.In order to further analyze the crystal structure the Rietveld refinement of measured XRD pattern was performed for all the samples as shown in Figures2(a), 2(b), and 2(c). La doped BFO compound holds the polar rhombohedralR3c structure similar to pure bismuth ferrite (BFO). The XRD pattern of BLFO sample was indexed in rhombohedral (R3c) system with lattice parameters a=b=5.5604(5) Å and c=13.7596(6) Å as shown in Figure 2(a). Earlier study reports a substitutional induced structural phase transition (R3c → C222) for BLFO compound [9, 21]. It is worth noting that our attempt to fit the XRD pattern of present BLFO sample withC222 structural model was completely failed. Indeed, the reflection conditions derived from indexed reflection for BLFO cell were l=2n forhhl, k=2n forhkh, h=2n forhkk, h=2n forh00, k=2n for 0k0, and l=2n for 00l which are compatible with the space groupR3c.Rietveld refined X-ray diffraction pattern of the Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples. The figure shows observed intensity (Yobs), calculated intensity (Ycalc), and difference in observed and calculated intensities (Yobs-Ycalc) and peak positions of different phases are shown at the base line as small ticks (|).
(a)
(b)
(c)The XRD pattern of BNFO sample was indexed in triclinic structure (P1 space group) with cell parameters a=3.9074(5) Å, b=3.9112(6) Å, and c=3.9002(5) Å. The X-ray diffraction pattern shows that all the X-ray peaks of the BLFO and BNFO samples are well matching with the earlier reported data [17]. Nd addition at Bi site is helpful in suppressing the secondary phase in BFO. Therefore present samples have a single phase triclinic perovskite structure with all constituent components forming a solid solution rather than a mixture of Bi2O3, Fe2O3, Nd2O3, or any other impurity phase except Bi2Fe4O9 observed in pure BFO.Similarly, for BDFO compound, the refinement was performed withPnma +R3c structural model. The Rietveld refined XRD pattern of BDFO is shown in Figure 2(c). The dominant contribution is related to orthorhombic phase (Pnma, 80.62%) with lattice parameters a=5.4014(5) Å, b=7.7842(4) Å, and c=5.5904(5) Å. The other component is related to rhombohedral phase (R3c, 19.38%). Reflection conditions obtained forPnma model are found to be almost similar forPn21a model except h=2n forh0l. The best iteration gives χ2≈4.32 forR3c, χ2≈10.08 forPnma, and χ2≈1.84 forR3c +Pnma model attributing to the fact that crystal structure of BDFO compound is characterized by coexistence of two phases with a minimum χ2 value. The obtained result is consistent with the earlier reported work [14]. Rietveld refined structural parameters of the Bi0.8RE0.2FeO3 (La, Nd and Dy) samples simulated based on the measured XRD patterns are documented in Table 1.Table 1
Rietveld refined structural parameters of the Bi0.8RE0.2FeO3 samples simulated based on the measured XRD patterns. The error values are presented in the parentheses.
Structure
Cell
Atoms
x
y
z
R-factors (%)
Bi0.8La0.2FeO3
R3c (100%)
a = 5.5604 (5)
Bi/La
0.0000
0.0000
0.2724
R
Bragg = 4.89
b = 5.5604 (5)
Fe
0.0000
0.0000
0.0000
R
p = 5.36
c = 13.7596 (6)
O
0.6679
0.7647
0.5489
R
wp = 7.15
V = 368.43 (2)
χ
2 = 2.91
GoF = 1.7
Bi0.8Nd0.2FeO3
P1 (100%)
a = 3.9074 (5)
Bi/Nd
0.0000
0.0000
0.0000
R
Bragg = 10.0
b = 3.9112 (6)
Fe
0.5689
0.4362
0.5467
R
p = 7.79
c = 3.9002 (5)
O1
−0.0815
0.4542
0.6774
R
wp = 11.2
V = 59.60 (2)
O2
0.4538
−0.0722
0.6835
χ
2  = 1.85
O3
0.4541
0.4756
0.0176
GOF = 1.16
Bi0.8Dy0.2FeO3
Pnma (80.62%)
a = 5.4014 (5)
Bi/Dy
0.0472
0.2500
0.9933
R
B
1 = 10.7
b = 7.7822 (4)
Fe
0.0000
0.0000
0.5000
R
B
2 = 6.96
c = 5.5904 (5)
O1
0.3832
0.2500
0.0818
R
p = 5.62
V = 234.99 (1)
O2
0.2076
0.5414
0.2044
R
wp = 7.2
χ
2 = 1.85
R3c (19.38%)
a = 5.5504 (2)
Bi/Dy
0.0000
0.0000
0.2676
GOF = 1.4
b = 5.5504 (2)
Fe
0.0000
0.0000
0.0000
c = 13.7888 (5)
O
0.6794
0.7801
0.5544
V = 367.88 (2)It is well known that ferroic order and spontaneous polarization in BFO mainly result from the Bi3+ stereochemical 6s2 lone pair electron. Thus it is expected that systematic doping of rare-earth ions will distort the cation spacing between the oxygen octahedra and alter the long-range ferroelectric order. The ferroelectric properties have a close relation with the Fe–O bond length. The interatomic bond lengths of all the four samples were calculated by using Bond_Str program and are tabulated in Table 2. In BLFO compound with rhombohedral (R3c) crystal structure the octahedra bond environment is composed of three long degenerate Fe–O bond lengths and three short degenerate Fe–O bond lengths. The FeO6 octahedron gets distorted due to Nd and Dy substitution, resulting in change in bond lengths as mentioned in Table 2.Table 2
Important bond lengths of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples. The error values are presented in the parentheses.
Compounds
Bond type
Bond length (Å)
BLFO
Fe–O (3)
1.7775
Fe–O (3)
2.3165
BNFO
Fe–O (1)
1.4653
Fe–O (1)
1.9015
Fe–O (1)
2.0505
Fe–O (1)
2.1114
Fe–O (1)
2.1248
Fe–O (1)
2.5882
BDFO
Fe–O (2)
1.9760
Fe–O (2)
2.0226
Fe–O (2)
2.0958


### 3.2. Raman Analysis

Raman spectroscopy is a powerful tool to probe the structural and vibrational property of a material and also provide valuable information about ionic substitution and electric polarization. Raman spectra of BLFO, BNFO, and BDFO samples with excitation wavelength of 488 nm at room temperature are shown in Figure3. It has been reported that undoped BiFeO3with distorted rhombohedral structure,R3c space group, and ten atoms in a unit cell of this structure yields 18 optical phonon modes that can be summarized using the following irreducible representation: Γopt=4A1+5A2+9E; according to group theory 13 observed modes (ΓRaman,R3c=4A1+9E) are Raman active, whereas 5A2 are Raman inactive modes [22, 23]. The dependence of mode positions on BLFO, BNFO, and BDFO samples is summarized in Table 3.Table 3
Raman modes (cm−1) for Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples and the bulk BiFeO3 (Kothari et al. [20]).
Raman modes (cm−1)
BFO bulk [20]
BLFO
BNFO
BDFO
A
1
-1
135.15
135.95
139.06
142.33
A
1
-2
167.08
174.52
—
176.88
A
1
-3
218.11
—
—
—
A
1
-4
430.95
434.14
—
—
E
-1
71.39
67.44
68.24
—
E
-2
98.36
—
97.91
—
E
-3
255.38
—
—
234.32
E
-4
283.0
273.93
298.01
278.77
E
-5
321.47
—
—
326.52
E
-6
351.55
373.35
—
386.31
E
-7
467.60
475.53
488.53
475.47
E
-8
526.22
527.78
—
531.89
E
-9
598.84
627.47
619.53
585.45Figure 3
Raman spectra for Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples at room temperature with excitation wavelength of 488 nm.In the present study, for BLFO ceramicA1 andE-symmetry normal modes forR3c symmetry includingA1-1,A1-2,A1-3,A1-4,E-1,E-4,E-6,E-7,E-8, andE-9 at around 138, 174, 191, 434, 67, 273, 373, 475, 527, and 627 cm−1 are clearly observed. These results are matched well with the Raman active vibration modes identified for BFO (R3c) [20, 24]. The ferroelectricity of BFO generally originates from the stereochemical activity of the Bi3+ 6s2 lone pair electron that is mainly responsible for the change in both Bi–O covalent bonds. The low frequency characteristic modes below 200 cm−1 may be responsible for the ferroelectric nature of the bismuth ferrite samples. As evident from the X-ray diffraction the changes in crystal symmetries are attributed to theA-site disorder created by Nd and Dy substitution, which leads to the shifting of Raman modes with sudden disappearance of some modes. TheA1-2,A1-3, andA1-4 were decomposed completely in BNFO and BDFO samples.The normal modes related to the Bi–O covalent bonds (i.e.,E-1,A1-1,A1-2,A1-3, andE-2 modes) shift gradually toward higher frequencies and are attributed to the substitution of relatively light (mass) La3+ (138.90 g), Nd3+ (144.24 g), and Dy3+ (162.50 g) ion for Bi3+ (208.98 g) ion in the BiFeO3.


### 3.3. Ferroelectric (P-E) Measurement

We have also made attempts to measure ferroelectric hysteresis loop at room temperature for BLFO, BNFO, and BDFO compounds (Figure4). It has been observed from the graph that BLFO and BDFO sample represent ferroelectric (FE) behaviour whereas BNFO sample represents paraelectric (PE) nature. The BLFO compound represents ferroelectric loop without any saturation value. This is attributed to the fact that BLFO sample is highly conductive at room temperature which results in the partial reversal of the polarization. For BDFO the spontaneous polarization (2Ps), remnant polarization (2Pr), and coercive field (Ec) are about ~0.23 μc/cm2, 0.16 μc/cm2, and 1.50 kV/cm, respectively, under the electric field of ~3 kV/cm, whereas for BNFO compound the obtained values of 2Ps and 2Pr are found to be ~2.6 μc/cm2 and ~0.0 μc/cm2, respectively, under the electric field of ~100 kV/cm.Figure 4
Room temperature ferroelectric (P-E) loop measurement of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples.It has been reported that Dy substitution is very much supportive in decreasing the leakage behavior of BiFeO3. Moreover, too much Dy substitution will degrade ferroelectric nature [25]. This is attributed to the fact that higher Dy substitution will transform the crystal structure from rhombohedral to orthorhombic symmetry. The orthorhombic structure is more centrosymmetric, which in turn suppresses the ferroelectricity [26]. Furthermore, the origin of ferroelectricity in BiFeO3 is generally due to Bi3+ (6s2) lone pair electron. The substitution of Bi3+ with Dy3+ ion will weaken the stereochemical activity of lone pair and weaken the ferroelectricity. In present study, despite 20% Dy substitution, BDFO compound is ferroelectric in nature with a small leakage current. This might be because of the coexistence of two phases (Pnma +R3c) in present BDFO compound.Furthermore, for paraelectric BNFO sample the obtained values of2Ps (~2.6 μc/cm2) and 2Pr (~0 μc/cm2) are found to be much lower even at a high field of 100 kV/cm. The lower Pr value of BNFO despite its higher applied electric field indicates that Nd doping degrades the ferroelectric nature. In the present case of BNFO, the Bi3+ lone pair electron hybridizes with empty p orbital of Bi3+ or an O2− ion to form Bi–O covalent bonds ensuing the noncentrosymmetric distortion and ferroelectricity. Substitution of Nd3+ ion weakens the stereochemical activity and results in FE-PE transition.


### 3.4. Magnetic Hysteresis Analysis

The magnetization-magnetic field (M-H) curve recorded at room temperature for BLFO and BDFO samples with a maximum applied field 10 kOe has been illustrated in Figure 5. Similarly, for BNFO sample, the maximum applied magnetic field (Hm) up to 50 kOe has been also shown in Figure 5. It is well known that pristine BFO hasG-type antiferromagnetic order with a long period of ~62 nm of canted spins between two successive ferromagnetically coupled (111) planes and zero net magnetization [27]. There are sharp and noticeable changes in magnetization observed for Bi0.8RE0.2FeO3 (RE = Nd and Dy) samples at room temperature. Magnetization increases presentably with doping content as shown in the inset of Figure 5.Magnetization versus magnetic field (M-H) loops of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples recorded at room temperature. The inset shows the enlarged data.
(a)
(b)
(c)In Figure5(a)M-H curve of BLFO sample shows a very narrow magnetic hysteresis loop, no saturation magnetization, with a small but nonzero remnant magnetization (Mr) of ~0.005 emu/g and coercive field (Hc) of ~454.6 Oe. From Figure 5(b), it is clearly seen that BDFO sample exhibits typical ferromagnetic hysteresis loop. The saturation magnetization (Ms), Mr, and Hc values were found to be 1.36 emu/g, 0.05 emu/g, and 4.71 Oe, respectively. A weak ferromagnetic behaviour was observed for BLFO and BDFO sample due to the suppression of space modulated spin structure [28, 29]. Doping by La at Bi site in BFO leads to distortion in rhombohedral structure. However, doping of Dy further enhances the distortion in rhombohedral structure leading to coexistence of orthorhombic phase (Pnma, 80.62%) + rhombohedral phase (R3c, 19.38%). We thus make a note that apart from the suppression of space modulated spin structure mismatch of ionic radii of La and Dy ion leading to different structures is also plausible for weak ferromagnetic behaviour. This can be probed by neutron diffraction and we shall study this problem in near future.Figure5(c) represents the room temperatureM-H curve for BNFO sample with a maximum applied magnetic field (Hm) 50 kOe. The magnetic field dependent magnetization of BNFO showed similar behaviour. In case of ceramic BNFO, it exhibits a deviation from linear loop at 300 K as documented in Figure 5(c). Interestingly, the peculiar double hysteresis loop likeM-H curve in both BNFO samples with a low coercive field (Hc) has been observed; however this implies that additional factors contribute to enhanced magnetization. Similar behaviour was earlier observed in Ho doped BFO and is attributed to ferromagnetic interaction between Fe3+ and Ho3+ [15].The magnetization appears in all the samples due to suppression of spiral magnetic spin structures in Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy). As the substituting ions effectively disturb the crystal structure differently reasons for each rare-earth dopant in this report are different for destruction of spiral magnetic spin structure [29]. In other words, theRE ion as (RE = La, Nd, and Dy) doping in BFO can only suppress but cannot destroy the spin cycloid structure completely at 20% substitution in BFO. Similar behavior is also observed in previously rare-earth doped BiFeO3 [10–15, 30]. Henceforth, partial substitution should be considered as one of the most effective ways for improving the multiferroic characteristic of antiferromagnetic BFO.


## 3.1. Structural Analysis

Figure1 shows the XRD pattern of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) ceramic samples. From the measured XRD pattern it has been observed that all the samples exhibit different crystal structures. BLFO sample was indexed in rhombohedral structure with space groupR3c where all the diffraction peaks match closely with the JCPDS file number 86-1518. A minor low level impurity phase (marked with *) was detected around 2θ≈28° associated with Bi2Fe4O9 [17]. This impurity peak matches well with the JCPDS file number 72-1832. The diffraction peaks change in both intensity and 2θ values with different dopant ionic radii as a result of change in crystal structure [18]. The values of lattice constants were manually calculated using different forms of crystal structures as defined earlier [19].Figure 1
Room temperature XRD pattern of the Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples designated as BLFO, BNFO, and BDFO, respectively.In order to further analyze the crystal structure the Rietveld refinement of measured XRD pattern was performed for all the samples as shown in Figures2(a), 2(b), and 2(c). La doped BFO compound holds the polar rhombohedralR3c structure similar to pure bismuth ferrite (BFO). The XRD pattern of BLFO sample was indexed in rhombohedral (R3c) system with lattice parameters a=b=5.5604(5) Å and c=13.7596(6) Å as shown in Figure 2(a). Earlier study reports a substitutional induced structural phase transition (R3c → C222) for BLFO compound [9, 21]. It is worth noting that our attempt to fit the XRD pattern of present BLFO sample withC222 structural model was completely failed. Indeed, the reflection conditions derived from indexed reflection for BLFO cell were l=2n forhhl, k=2n forhkh, h=2n forhkk, h=2n forh00, k=2n for 0k0, and l=2n for 00l which are compatible with the space groupR3c.Rietveld refined X-ray diffraction pattern of the Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples. The figure shows observed intensity (Yobs), calculated intensity (Ycalc), and difference in observed and calculated intensities (Yobs-Ycalc) and peak positions of different phases are shown at the base line as small ticks (|).
(a)
(b)
(c)The XRD pattern of BNFO sample was indexed in triclinic structure (P1 space group) with cell parameters a=3.9074(5) Å, b=3.9112(6) Å, and c=3.9002(5) Å. The X-ray diffraction pattern shows that all the X-ray peaks of the BLFO and BNFO samples are well matching with the earlier reported data [17]. Nd addition at Bi site is helpful in suppressing the secondary phase in BFO. Therefore present samples have a single phase triclinic perovskite structure with all constituent components forming a solid solution rather than a mixture of Bi2O3, Fe2O3, Nd2O3, or any other impurity phase except Bi2Fe4O9 observed in pure BFO.Similarly, for BDFO compound, the refinement was performed withPnma +R3c structural model. The Rietveld refined XRD pattern of BDFO is shown in Figure 2(c). The dominant contribution is related to orthorhombic phase (Pnma, 80.62%) with lattice parameters a=5.4014(5) Å, b=7.7842(4) Å, and c=5.5904(5) Å. The other component is related to rhombohedral phase (R3c, 19.38%). Reflection conditions obtained forPnma model are found to be almost similar forPn21a model except h=2n forh0l. The best iteration gives χ2≈4.32 forR3c, χ2≈10.08 forPnma, and χ2≈1.84 forR3c +Pnma model attributing to the fact that crystal structure of BDFO compound is characterized by coexistence of two phases with a minimum χ2 value. The obtained result is consistent with the earlier reported work [14]. Rietveld refined structural parameters of the Bi0.8RE0.2FeO3 (La, Nd and Dy) samples simulated based on the measured XRD patterns are documented in Table 1.Table 1
Rietveld refined structural parameters of the Bi0.8RE0.2FeO3 samples simulated based on the measured XRD patterns. The error values are presented in the parentheses.
Structure
Cell
Atoms
x
y
z
R-factors (%)
Bi0.8La0.2FeO3
R3c (100%)
a = 5.5604 (5)
Bi/La
0.0000
0.0000
0.2724
R
Bragg = 4.89
b = 5.5604 (5)
Fe
0.0000
0.0000
0.0000
R
p = 5.36
c = 13.7596 (6)
O
0.6679
0.7647
0.5489
R
wp = 7.15
V = 368.43 (2)
χ
2 = 2.91
GoF = 1.7
Bi0.8Nd0.2FeO3
P1 (100%)
a = 3.9074 (5)
Bi/Nd
0.0000
0.0000
0.0000
R
Bragg = 10.0
b = 3.9112 (6)
Fe
0.5689
0.4362
0.5467
R
p = 7.79
c = 3.9002 (5)
O1
−0.0815
0.4542
0.6774
R
wp = 11.2
V = 59.60 (2)
O2
0.4538
−0.0722
0.6835
χ
2  = 1.85
O3
0.4541
0.4756
0.0176
GOF = 1.16
Bi0.8Dy0.2FeO3
Pnma (80.62%)
a = 5.4014 (5)
Bi/Dy
0.0472
0.2500
0.9933
R
B
1 = 10.7
b = 7.7822 (4)
Fe
0.0000
0.0000
0.5000
R
B
2 = 6.96
c = 5.5904 (5)
O1
0.3832
0.2500
0.0818
R
p = 5.62
V = 234.99 (1)
O2
0.2076
0.5414
0.2044
R
wp = 7.2
χ
2 = 1.85
R3c (19.38%)
a = 5.5504 (2)
Bi/Dy
0.0000
0.0000
0.2676
GOF = 1.4
b = 5.5504 (2)
Fe
0.0000
0.0000
0.0000
c = 13.7888 (5)
O
0.6794
0.7801
0.5544
V = 367.88 (2)It is well known that ferroic order and spontaneous polarization in BFO mainly result from the Bi3+ stereochemical 6s2 lone pair electron. Thus it is expected that systematic doping of rare-earth ions will distort the cation spacing between the oxygen octahedra and alter the long-range ferroelectric order. The ferroelectric properties have a close relation with the Fe–O bond length. The interatomic bond lengths of all the four samples were calculated by using Bond_Str program and are tabulated in Table 2. In BLFO compound with rhombohedral (R3c) crystal structure the octahedra bond environment is composed of three long degenerate Fe–O bond lengths and three short degenerate Fe–O bond lengths. The FeO6 octahedron gets distorted due to Nd and Dy substitution, resulting in change in bond lengths as mentioned in Table 2.Table 2
Important bond lengths of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples. The error values are presented in the parentheses.
Compounds
Bond type
Bond length (Å)
BLFO
Fe–O (3)
1.7775
Fe–O (3)
2.3165
BNFO
Fe–O (1)
1.4653
Fe–O (1)
1.9015
Fe–O (1)
2.0505
Fe–O (1)
2.1114
Fe–O (1)
2.1248
Fe–O (1)
2.5882
BDFO
Fe–O (2)
1.9760
Fe–O (2)
2.0226
Fe–O (2)
2.0958


## 3.2. Raman Analysis

Raman spectroscopy is a powerful tool to probe the structural and vibrational property of a material and also provide valuable information about ionic substitution and electric polarization. Raman spectra of BLFO, BNFO, and BDFO samples with excitation wavelength of 488 nm at room temperature are shown in Figure3. It has been reported that undoped BiFeO3with distorted rhombohedral structure,R3c space group, and ten atoms in a unit cell of this structure yields 18 optical phonon modes that can be summarized using the following irreducible representation: Γopt=4A1+5A2+9E; according to group theory 13 observed modes (ΓRaman,R3c=4A1+9E) are Raman active, whereas 5A2 are Raman inactive modes [22, 23]. The dependence of mode positions on BLFO, BNFO, and BDFO samples is summarized in Table 3.Table 3
Raman modes (cm−1) for Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples and the bulk BiFeO3 (Kothari et al. [20]).
Raman modes (cm−1)
BFO bulk [20]
BLFO
BNFO
BDFO
A
1
-1
135.15
135.95
139.06
142.33
A
1
-2
167.08
174.52
—
176.88
A
1
-3
218.11
—
—
—
A
1
-4
430.95
434.14
—
—
E
-1
71.39
67.44
68.24
—
E
-2
98.36
—
97.91
—
E
-3
255.38
—
—
234.32
E
-4
283.0
273.93
298.01
278.77
E
-5
321.47
—
—
326.52
E
-6
351.55
373.35
—
386.31
E
-7
467.60
475.53
488.53
475.47
E
-8
526.22
527.78
—
531.89
E
-9
598.84
627.47
619.53
585.45Figure 3
Raman spectra for Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples at room temperature with excitation wavelength of 488 nm.In the present study, for BLFO ceramicA1 andE-symmetry normal modes forR3c symmetry includingA1-1,A1-2,A1-3,A1-4,E-1,E-4,E-6,E-7,E-8, andE-9 at around 138, 174, 191, 434, 67, 273, 373, 475, 527, and 627 cm−1 are clearly observed. These results are matched well with the Raman active vibration modes identified for BFO (R3c) [20, 24]. The ferroelectricity of BFO generally originates from the stereochemical activity of the Bi3+ 6s2 lone pair electron that is mainly responsible for the change in both Bi–O covalent bonds. The low frequency characteristic modes below 200 cm−1 may be responsible for the ferroelectric nature of the bismuth ferrite samples. As evident from the X-ray diffraction the changes in crystal symmetries are attributed to theA-site disorder created by Nd and Dy substitution, which leads to the shifting of Raman modes with sudden disappearance of some modes. TheA1-2,A1-3, andA1-4 were decomposed completely in BNFO and BDFO samples.The normal modes related to the Bi–O covalent bonds (i.e.,E-1,A1-1,A1-2,A1-3, andE-2 modes) shift gradually toward higher frequencies and are attributed to the substitution of relatively light (mass) La3+ (138.90 g), Nd3+ (144.24 g), and Dy3+ (162.50 g) ion for Bi3+ (208.98 g) ion in the BiFeO3.


## 3.3. Ferroelectric (P-E) Measurement

We have also made attempts to measure ferroelectric hysteresis loop at room temperature for BLFO, BNFO, and BDFO compounds (Figure4). It has been observed from the graph that BLFO and BDFO sample represent ferroelectric (FE) behaviour whereas BNFO sample represents paraelectric (PE) nature. The BLFO compound represents ferroelectric loop without any saturation value. This is attributed to the fact that BLFO sample is highly conductive at room temperature which results in the partial reversal of the polarization. For BDFO the spontaneous polarization (2Ps), remnant polarization (2Pr), and coercive field (Ec) are about ~0.23 μc/cm2, 0.16 μc/cm2, and 1.50 kV/cm, respectively, under the electric field of ~3 kV/cm, whereas for BNFO compound the obtained values of 2Ps and 2Pr are found to be ~2.6 μc/cm2 and ~0.0 μc/cm2, respectively, under the electric field of ~100 kV/cm.Figure 4
Room temperature ferroelectric (P-E) loop measurement of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples.It has been reported that Dy substitution is very much supportive in decreasing the leakage behavior of BiFeO3. Moreover, too much Dy substitution will degrade ferroelectric nature [25]. This is attributed to the fact that higher Dy substitution will transform the crystal structure from rhombohedral to orthorhombic symmetry. The orthorhombic structure is more centrosymmetric, which in turn suppresses the ferroelectricity [26]. Furthermore, the origin of ferroelectricity in BiFeO3 is generally due to Bi3+ (6s2) lone pair electron. The substitution of Bi3+ with Dy3+ ion will weaken the stereochemical activity of lone pair and weaken the ferroelectricity. In present study, despite 20% Dy substitution, BDFO compound is ferroelectric in nature with a small leakage current. This might be because of the coexistence of two phases (Pnma +R3c) in present BDFO compound.Furthermore, for paraelectric BNFO sample the obtained values of2Ps (~2.6 μc/cm2) and 2Pr (~0 μc/cm2) are found to be much lower even at a high field of 100 kV/cm. The lower Pr value of BNFO despite its higher applied electric field indicates that Nd doping degrades the ferroelectric nature. In the present case of BNFO, the Bi3+ lone pair electron hybridizes with empty p orbital of Bi3+ or an O2− ion to form Bi–O covalent bonds ensuing the noncentrosymmetric distortion and ferroelectricity. Substitution of Nd3+ ion weakens the stereochemical activity and results in FE-PE transition.


## 3.4. Magnetic Hysteresis Analysis

The magnetization-magnetic field (M-H) curve recorded at room temperature for BLFO and BDFO samples with a maximum applied field 10 kOe has been illustrated in Figure 5. Similarly, for BNFO sample, the maximum applied magnetic field (Hm) up to 50 kOe has been also shown in Figure 5. It is well known that pristine BFO hasG-type antiferromagnetic order with a long period of ~62 nm of canted spins between two successive ferromagnetically coupled (111) planes and zero net magnetization [27]. There are sharp and noticeable changes in magnetization observed for Bi0.8RE0.2FeO3 (RE = Nd and Dy) samples at room temperature. Magnetization increases presentably with doping content as shown in the inset of Figure 5.Magnetization versus magnetic field (M-H) loops of Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples recorded at room temperature. The inset shows the enlarged data.
(a)
(b)
(c)In Figure5(a)M-H curve of BLFO sample shows a very narrow magnetic hysteresis loop, no saturation magnetization, with a small but nonzero remnant magnetization (Mr) of ~0.005 emu/g and coercive field (Hc) of ~454.6 Oe. From Figure 5(b), it is clearly seen that BDFO sample exhibits typical ferromagnetic hysteresis loop. The saturation magnetization (Ms), Mr, and Hc values were found to be 1.36 emu/g, 0.05 emu/g, and 4.71 Oe, respectively. A weak ferromagnetic behaviour was observed for BLFO and BDFO sample due to the suppression of space modulated spin structure [28, 29]. Doping by La at Bi site in BFO leads to distortion in rhombohedral structure. However, doping of Dy further enhances the distortion in rhombohedral structure leading to coexistence of orthorhombic phase (Pnma, 80.62%) + rhombohedral phase (R3c, 19.38%). We thus make a note that apart from the suppression of space modulated spin structure mismatch of ionic radii of La and Dy ion leading to different structures is also plausible for weak ferromagnetic behaviour. This can be probed by neutron diffraction and we shall study this problem in near future.Figure5(c) represents the room temperatureM-H curve for BNFO sample with a maximum applied magnetic field (Hm) 50 kOe. The magnetic field dependent magnetization of BNFO showed similar behaviour. In case of ceramic BNFO, it exhibits a deviation from linear loop at 300 K as documented in Figure 5(c). Interestingly, the peculiar double hysteresis loop likeM-H curve in both BNFO samples with a low coercive field (Hc) has been observed; however this implies that additional factors contribute to enhanced magnetization. Similar behaviour was earlier observed in Ho doped BFO and is attributed to ferromagnetic interaction between Fe3+ and Ho3+ [15].The magnetization appears in all the samples due to suppression of spiral magnetic spin structures in Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy). As the substituting ions effectively disturb the crystal structure differently reasons for each rare-earth dopant in this report are different for destruction of spiral magnetic spin structure [29]. In other words, theRE ion as (RE = La, Nd, and Dy) doping in BFO can only suppress but cannot destroy the spin cycloid structure completely at 20% substitution in BFO. Similar behavior is also observed in previously rare-earth doped BiFeO3 [10–15, 30]. Henceforth, partial substitution should be considered as one of the most effective ways for improving the multiferroic characteristic of antiferromagnetic BFO.


## 4. Conclusion

Conclusively, polycrystalline Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples were successfully prepared through solid-state reaction route and were further investigated by XRD, Raman spectroscopy, and ferroelectric and magnetic measurements. All the samples fitted with Rietveld refinement using FullPROF program revealed the existence of rhombohedral structure with space groupR3c for BLFO (La3+ doped BiFeO3) and also revealed the substitutional induced structural transformationR3c →P1 (BNFO) andR3c →Pnma (BDFO) systems. The changes in crystal structure are attributed to theA-site disorder created by Nd and Dy substitution, which leads to the shifting of Raman modes with sudden disappearance of some modes asA1-2,A1-3, andA1-4 decomposed completely in BNFO and BDFO samples.Ferroelectric and ferromagnetic loops have been observed in the Bi0.8RE0.2FeO3 ceramics at room temperature, indicating that ferroelectric and ferromagnetic ordering coexist in the ceramics at room temperature. A significant enhancement in magnetization with enhanced remnant magnetization and coercive field is inferred in rare-earth doped Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples. These results validate the doping induced destruction of the cycloidal structure in Bi0.8RE0.2FeO3 (RE = La, Nd, and Dy) samples.



---

*Source: 869071-2015-02-04.xml*