# Gold/Chitosan Nanocomposites with Specific Near Infrared Absorption for Photothermal Therapy Applications

Authors: Guandong Zhang; Xinghua Sun; Jacek Jasinski; Dhruvin Patel; Andre M. Gobin
Journal: Journal of Nanomaterials
 (2012)

---

## Abstract

Gold/chitosan nanocomposites were synthesized and evaluated as a therapeutic agent for the photothermal therapy. Gold nanoparticles (Au NPs) with controllable optical absorption in the near infrared (NIR) region were prepared by the reaction of chloroauric acid and sodium thiosulfate. To apply these particles to cancer therapy, the bare Au NPs were coated with chitosan (CS), O-carboxymethyl chitosan (CMCS), and a blend of CS and CMCS for utilizations in physiologic conditions. The surface properties, optical stability, and photothermal ablation efficiency on hepatocellular carcinoma cells (HepG2) and human dermal fibroblast cells (HDF) demonstrate that these gold nanocomposites have great potential as a therapeutic agent inin vitro tests. The CS-coated nanocomposites show the highest efficiency for the photo-ablation on the HepG2 cells, and the CS and CMCS blended coated particles show the best discrimination between the cancer cell and normal cells. The well-controlled NIR absorption and the biocompatible surface of these nanocomposites allow low-power NIR laser activation and low-dosage particle injection for the cancer cell treatment.


---

## Body

## 1. Introduction

The use of nanoparticles (NPs) in biomedical field is one of the most important branches of nanobiotechnology. Many biomedical applications require nanoparticles with low toxicity, biocompatibility, and stability with high preferential accumulation in the target tissue or organ [1]. Polymer-nanoparticle composites may possess the unique property superior to that of either the polymer or nanoparticles. Metal nanoparticles with polymer coatings or dispersed in polymeric matrices display the increased stability, improved processability, recyclability, and solubility in a variety of solvents [2].Gold nanoparticles (Au NPs) are attracting enormous attentions in applications for immunoassay [3, 4], drug delivery [5], contrast enhancement, and thermal therapy for tumor treatment [6–8], due to their nanoscale size, oxide-free components, bioconjugation property,  biocompatibility, and unique optical properties.Thermal therapy, also termed as hyperthermia, has thousands years history as one of most important methods for the tumor treatment [9]. In this technique, moderate heating is generated in the target region, resulting in tumors selectively destroyed, due to their reduced heat tolerance compared to normal tissue [10]. In the past decades, because many new heating sources such as radiofrequency [11], microwave [12], magnetic field [13], and laser [9] were employed, there were remarkable progresses achieved in this area. Photothermal therapy (PT) is a promising field within thermal therapy, incorporating laser techniques and photoabsorbing agents. Light absorbing dyes, chemical photosensitizers, and solid optically responsive nanomaterials have been applied as the photoabsorbing agents in PT [9]. For small metal nanoparticles, their optical properties are dominated by collective oscillation of conduction electrons. An absorption band results when the incident photon frequency is resonant with the collective oscillation of the conduction band electrons, and this is known as the surface plasmon resonance (SPR) [14]. Au NPs possess strongly enhanced visible and near infrared light absorption, which is several orders of magnitude more intense compared to conventional chromophores. Various gold-based nanostructures with NIR absorption have been developed. Gold nanospheres [15], gold nanoshells [7], gold nanorods [16], and gold nanocages [17] are the popular nanostructures that have been demonstrated in photothermal therapeutics due to their strongly enhanced absorption in the visible and NIR regions on account of their SPR effects.In our work, Au NPs with NIR absorption were prepared by the one step reaction of chloroauric acid and sodium thiosulfate. Their NIR absorption wavelengths were well controlled by adjusting molar ratio of HAuCl4/Na2S2O3 [18]. These Au NPs were coated with chitosan- (CS)- based coatings and used as a therapeutic agent for the photothermal ablation of cancer cells. Chitosan is a biobased polysaccharide derived from shrimp and crab shells [19]. It is nontoxic, biodegradable and biocompatible, and has good processability [20, 21]. The cost associated with chitosan is much lower than that of other polymer coatings or chemical compounds, for example, polyethylene glycol (PEG) that are often used to protect and stabilize the nanoparticles by many researchers [5]. Hepatocellular carcinoma is the most common primary malignant tumor of the liver. It affects greater than half a million patients worldwide. US liver-related cancer deaths account for 4% of all cancers or about 20,000 deaths annually. Two anchorage-dependent cell lines, hepatocellular carcinoma cell line (HepG2), and control cell line of human dermal fibroblast (HDF) were selected for the estimation of laser ablation efficiency of these novel gold nanocomposites. The efficacy was evaluated by live/dead stain images following photothermal ablation. These gold nanocomposites show great ability for laser ablation, and the surface coating components plays a very important role for selectivity to certain cancer cells. In addition, this composite material offers new and desirable advantages for cancer treatment. Beside the optically tunable gold nanoparticle for efficient conversion of light to heat, chitosan-based coatings provide tunable surface charges for applications in a variety of physiological pH environments and also allow further modification with targeting molecules or drug molecules by chemical reaction or electrostatic interaction.


## 2. Experimental

### 2.1. Preparation of Au Nanoparticles

Au NPs were prepared by the method we reported before [18, 22]. In which, 3 mM sodium thiosulfate (Na2S2O3·5H2O, Aldrich, 99.999%) solution was added into 1.71 mM chloroauric acid (HAuCl4·3H2O, Alfa Aesar, Au 49.68%) solutions with desired volume ratio at room temperature and vortexed for 20 seconds for uniform mixing. All the water used in the experiments was purified by a Thermo Scientific Easypure II system, with a resistivity of 18.2 MΩ cm.


### 2.2. Preparation of Carboxymethylated Chitosan

Low molecule weight chitosan (Sigma-Aldrich, MW 50–190 K) was used for the surface coating of the Au NPs. Based on this chitosan,O-carboxymethyl chitosan (CMCS) was synthesized as the reported method [23, 24]. Briefly, 15 g sodium hydroxide was dissolved in a 20 : 80 mixture of deionized water and isopropanol (100 mL) in a 500 mL flask. 10 g chitosan was added to the flask to swell and alkalize at 50°C for 1 h. 15 g monochloroacetic acid (ClCH2CO2H, 99%, Acros Organics) was dissolved in 20 mL isopropanol and added into the reaction mixture dropwisely in 30 min and reacted under vigorous agitation for 4 h at 55–60°C. Adding 200 mL 80% ethyl alcohol stopped the reaction. The product was filtered and repeatedly rinsed by 80% ethyl alcohol, to desalt and dewater, until the pH value of the washing solution was less than 8.0. Finally, the product was vacuum dried for 1 day at 40°C.


### 2.3. Preparation and Purification of Au NPs with Chitosan Based Coatings

Stock solution of chitosan was prepared by dispersing chitosan (1 g) in 0.7% acetic acid solution (100 mL). CMCS solution was prepared by directly dissolving CMCS (1 g) in 100 mL DI water. CS and CMCS solutions were purified by centrifuge at 1000 rpm for 10 min, to remove the little amount of insoluble residuals, and then were dialyzed (Spectrum Dialysis Membranes, MWCO 3 KDa) for 2 days. The chitosan-coated Au NPs (Au/CS), CMCS coated Au NPs (Au/CMCS), and CS and CMCS blended coated Au NPs (Au/(CS+CMCS))  were prepared by, respectively, adding CS solution, CMCS solution, or CS and CMCS blending solution (CS and CMCS solutions were premixed) dropwisely into the as-synthesized gold particle suspensions, with vigorous agitation. The ratio between CS or CMCS to Au NPs was controlled as 0.2 mg CS or CMCS per OD Au NP suspension and between CS and CMCS blending to Au NPs is (0.15 mg CS + 0.05 mg CMCS) per OD Au NP suspension (OD is the optical density). Then these samples were set on the rocking bed for 1 day. In the end the gold nanocomposite suspensions were concentrated and separated from the solution by centrifugation at 1000 g for 20 min. This step will remove the byproducts in solution and the extra chitosan. Then the centrifuged pellets were dispersed in sterilized DI water to a concentration of 25 OD/mL and stored at 4°C for the subsequent studies.


### 2.4. Characterization of Au NPs

The optical absorption of Au NPs was measured by a UV-Visible spectrophotometer (Cary-50Bio, Varian). A Zetasizer (Nano-ZS90, Malvern) was used to assess the surface charge of the nanoparticle suspensions. A FEI Tecnai F30 transmission electron microscope (TEM) operated at 200 KV was used to determine the morphology of Au NPs. Several Au NPs suspensions that have different NIR peak wavelength were carefully prepared for the photo-induced temperature rising measurement. 1 mL of the Au NP suspensions were added into the wells of tissue culture plate (Multiwell, Primaria 24 Well), with the concentration of 1 OD/mL. A laser with 817 nm centered wavelength generated by FAT-System (Coherent, CA) was shone on the gold suspension. The laser spot has the same area with the well, and the power of the laser was fixed as 1 W/cm2. An infrared thermometer (CSmicro, Optris GmbH, Germany) detecting the temperature of the Au NP suspension was fixed 10 cm above the media.


### 2.5. Photothermal Ablation Study

All cell lines were obtained from ATCC (Manassas, MA). Human dermal fibroblasts cell line (HDF, ATCC: PCS-201-012 male source) and hepatocellular carcinomas cell line (HepG2, ATCC: 59194) were seeded at monolayer confluence to allow for easier cell counting following staining (within 15 passages). All the cells were cultured at 37°C in a 5% CO2 environment in Dulbecco's modified eagle medium (DMEM) supplemented with 4 mM l-glutamine, 1% penicillin, and 10% fetal bovine serum. Prior to laser ablation experiments, cells were detached from culture flash with trypsin (0.25%) and resuspended in DMEM media and injected into the 24-well tissue culture plate (Multiwell, Primaria), cultured for 36–48 hours to achieve confluence. Laser ablation was performed based on methods described in [7]. Cells were incubated with 1 mL DMEM media which contains 1 OD Au NPs for 2 h to obtain the binding of the Au NPs on the cell. For this experiment, Au NPs and gold/chitosan nanocomposites were prepared with NIR absorption in the range of 820 nm to 850 nm, close to the wavelength of the laser source. Media were removed, and cells were rinsed with 0.5 mL PBS buffer, followed by addition of 0.5 mL fresh media to the culture wells. Next, the cells were exposed to 817 nm NIR laser at optimized conditions (5 W/cm2, 2 min). Well plates were incubated overnight after photothermal treatment, and a live/dead stain (Invitrogen, Carlsbad, CA) was performed, and fluorescent images were obtained and analyzed. Images were taken with a Nikon D90 camera on an Accu-Scope 3032 Microscope for green/red fluorescence, respectively, and cell numbers were counted manually.


## 2.1. Preparation of Au Nanoparticles

Au NPs were prepared by the method we reported before [18, 22]. In which, 3 mM sodium thiosulfate (Na2S2O3·5H2O, Aldrich, 99.999%) solution was added into 1.71 mM chloroauric acid (HAuCl4·3H2O, Alfa Aesar, Au 49.68%) solutions with desired volume ratio at room temperature and vortexed for 20 seconds for uniform mixing. All the water used in the experiments was purified by a Thermo Scientific Easypure II system, with a resistivity of 18.2 MΩ cm.


## 2.2. Preparation of Carboxymethylated Chitosan

Low molecule weight chitosan (Sigma-Aldrich, MW 50–190 K) was used for the surface coating of the Au NPs. Based on this chitosan,O-carboxymethyl chitosan (CMCS) was synthesized as the reported method [23, 24]. Briefly, 15 g sodium hydroxide was dissolved in a 20 : 80 mixture of deionized water and isopropanol (100 mL) in a 500 mL flask. 10 g chitosan was added to the flask to swell and alkalize at 50°C for 1 h. 15 g monochloroacetic acid (ClCH2CO2H, 99%, Acros Organics) was dissolved in 20 mL isopropanol and added into the reaction mixture dropwisely in 30 min and reacted under vigorous agitation for 4 h at 55–60°C. Adding 200 mL 80% ethyl alcohol stopped the reaction. The product was filtered and repeatedly rinsed by 80% ethyl alcohol, to desalt and dewater, until the pH value of the washing solution was less than 8.0. Finally, the product was vacuum dried for 1 day at 40°C.


## 2.3. Preparation and Purification of Au NPs with Chitosan Based Coatings

Stock solution of chitosan was prepared by dispersing chitosan (1 g) in 0.7% acetic acid solution (100 mL). CMCS solution was prepared by directly dissolving CMCS (1 g) in 100 mL DI water. CS and CMCS solutions were purified by centrifuge at 1000 rpm for 10 min, to remove the little amount of insoluble residuals, and then were dialyzed (Spectrum Dialysis Membranes, MWCO 3 KDa) for 2 days. The chitosan-coated Au NPs (Au/CS), CMCS coated Au NPs (Au/CMCS), and CS and CMCS blended coated Au NPs (Au/(CS+CMCS))  were prepared by, respectively, adding CS solution, CMCS solution, or CS and CMCS blending solution (CS and CMCS solutions were premixed) dropwisely into the as-synthesized gold particle suspensions, with vigorous agitation. The ratio between CS or CMCS to Au NPs was controlled as 0.2 mg CS or CMCS per OD Au NP suspension and between CS and CMCS blending to Au NPs is (0.15 mg CS + 0.05 mg CMCS) per OD Au NP suspension (OD is the optical density). Then these samples were set on the rocking bed for 1 day. In the end the gold nanocomposite suspensions were concentrated and separated from the solution by centrifugation at 1000 g for 20 min. This step will remove the byproducts in solution and the extra chitosan. Then the centrifuged pellets were dispersed in sterilized DI water to a concentration of 25 OD/mL and stored at 4°C for the subsequent studies.


## 2.4. Characterization of Au NPs

The optical absorption of Au NPs was measured by a UV-Visible spectrophotometer (Cary-50Bio, Varian). A Zetasizer (Nano-ZS90, Malvern) was used to assess the surface charge of the nanoparticle suspensions. A FEI Tecnai F30 transmission electron microscope (TEM) operated at 200 KV was used to determine the morphology of Au NPs. Several Au NPs suspensions that have different NIR peak wavelength were carefully prepared for the photo-induced temperature rising measurement. 1 mL of the Au NP suspensions were added into the wells of tissue culture plate (Multiwell, Primaria 24 Well), with the concentration of 1 OD/mL. A laser with 817 nm centered wavelength generated by FAT-System (Coherent, CA) was shone on the gold suspension. The laser spot has the same area with the well, and the power of the laser was fixed as 1 W/cm2. An infrared thermometer (CSmicro, Optris GmbH, Germany) detecting the temperature of the Au NP suspension was fixed 10 cm above the media.


## 2.5. Photothermal Ablation Study

All cell lines were obtained from ATCC (Manassas, MA). Human dermal fibroblasts cell line (HDF, ATCC: PCS-201-012 male source) and hepatocellular carcinomas cell line (HepG2, ATCC: 59194) were seeded at monolayer confluence to allow for easier cell counting following staining (within 15 passages). All the cells were cultured at 37°C in a 5% CO2 environment in Dulbecco's modified eagle medium (DMEM) supplemented with 4 mM l-glutamine, 1% penicillin, and 10% fetal bovine serum. Prior to laser ablation experiments, cells were detached from culture flash with trypsin (0.25%) and resuspended in DMEM media and injected into the 24-well tissue culture plate (Multiwell, Primaria), cultured for 36–48 hours to achieve confluence. Laser ablation was performed based on methods described in [7]. Cells were incubated with 1 mL DMEM media which contains 1 OD Au NPs for 2 h to obtain the binding of the Au NPs on the cell. For this experiment, Au NPs and gold/chitosan nanocomposites were prepared with NIR absorption in the range of 820 nm to 850 nm, close to the wavelength of the laser source. Media were removed, and cells were rinsed with 0.5 mL PBS buffer, followed by addition of 0.5 mL fresh media to the culture wells. Next, the cells were exposed to 817 nm NIR laser at optimized conditions (5 W/cm2, 2 min). Well plates were incubated overnight after photothermal treatment, and a live/dead stain (Invitrogen, Carlsbad, CA) was performed, and fluorescent images were obtained and analyzed. Images were taken with a Nikon D90 camera on an Accu-Scope 3032 Microscope for green/red fluorescence, respectively, and cell numbers were counted manually.


## 3. Results and Discussion

### 3.1. Preparation of Gold Nanoparticles with Desired Near Infrared Absorption

In our previous work [18, 25], a convenient method was developed to synthesize Au NPs with controllable NIR absorption. Au NPs were synthesized by one-step reaction of chloroauric acid and sodium thiosulfate, without assistance of additional templates, capping reagents, or seeds assembly. The synthesized products consist of nanoparticles with different shape and size including small spherical colloid gold particles (<5 nm) and nonspherical gold crystals. The nonspherical gold crystals are mainly the truncated octahedron, pentagons, and cuboctahedron, as well as the triangular-shaped plate structures [18]. Two absorption peaks due to the surface plasmon resonance are observed from these samples. The first SPR peak centered at around 530 nm is the characteristicSPR of the spherical colloid gold particles, and the second SPR component is higher at NIR band, which is attributed to the multipolar SPR band from the nonspherical Au NPs [18, 25]. Since the NIR absorption wavelengths increase with increasing molar ratio of HAuCl4/Na2S2O3, adjusting the molar ratio of HAuCl4/Na2S2O3 during the reaction controlled the absorption wavelength of the Au NPs. These products were further purified by the centrifugation to remove the spherical colloid gold particles, improving the NIR absorption. Figures 1(a) and 1(b) are the Z-contrast STEM images of the as-synthesized Au NPs and the same batch sample purified with centrifugation. The purified product possesses the NIR absorption wavelength at 820 nm. The temperature of the NIR absorbing Au NP suspension induced by the NIR laser radiation is affected by the concentration of nanoparticles, laser power, exposure time, and the absorbing wavelength of the Au NPs [26]. Figure 2 compares the heating effect of the Au NPs suspensions with NIR peak at 820 nm, 880 nm, 980 nm, and 1070 nm, respectively (showing in the insert figure) under the 817 nm wavelength diode laser (1 W/cm2) exposures. After 3 minutes, the temperature reaches to 50.8, 48.2, 46.4, and 41.2°C for the particles from low wavelength to high wavelength, respectively. The gold sample that has the NIR peak more close to the wavelength of laser source shows the best heating effect. The effective control of the NIR absorption of the gold nanoparticles for matching the wavelength of the laser source enhances the hyperthermia treatment. Meanwhile, the NIR wavelength is considered as the best light source for the photothermal therapy, because it is minimally absorbed by the normal tissues components of water and hemoglobin and can transmit deeply in the body.Z-contrast STEM images of the Au NPs synthesized from reaction of HAuCl4 and Na2S2O3 before and after centrifugation process. (a) As-synthesized Au NPs; (b) Au NPs after purification by centrifugation. The purified product has the NIR absorption peak at 820 nm.
(a)
(b)Figure 2
Heating effect of the gold nanoparticles with NIR absorption peaks at 820 nm, 880 nm, 980 nm, and 1070 nm, respectively, under the 817 nm wavelength laser exposures. The laser power is 1 W/cm2, and the Au NPs were dispersed in water at a concentration of 1 OD/mL. Inset shows the UV-visible-NIR spectra of the four Au NPs samples.


### 3.2. Chitosan-Based Coatings on the Gold Nanoparticles

Chitosan is a cationic polysaccharide of D-glucosamine and N-acetyl-D-glucosamine and has been shown to be a highly biocompatible material and have antibiotic properties. To improve its solubility or achieve new functionality, chemical modifications of chitosan were conducted and many derivatives have been synthesized. For example, modifications can be synthesized by carboxylation of the hydroxyl or amine groups in chitosan structure [20], resulting in the O-carboxymethyl chitosan or N-carboxymethyl chitosan respectively. O-carboxymethyl chitosan is achieved by substituting parts of the –OH at C-6 position of glucosamine units with –CH2COOH. Therefore, the reactive ligands such as –COOH and –NH2 groups are amenable to chemical functions. Others have reported the stabilization of GNPs with chitosan. As chitosan in solution is protonated and positively charged, it can be adsorbed onto the surfaces of gold nanoparticles, stabilizing and protecting the nanoparticles [27–29]. As-synthesized Au NPs present strongly negative surface charge (around −40 mV) allowing the positive charged chitosan tightly coated onto gold surface via electrostatic interaction.Figures3(a), 3(b), 3(c), and 3(d) show the high-resolution TEM images of the Au NPs without coating, Au/CS, Au/CMCS, and Au/(CS+CMCS) nanocomposites, respectively. The as-synthesized bare Au NPs have a 1-2 nm thin layer on their surface. Comparing to the bare Au NPs, Figures 3(b)–3(d) show the chitosan-based coatings effectively cover the gold NPs uniformly, forming a 2–5 nm thick layer on the gold surface.High-resolution TEM images of the Au NPs: (a) Au NPs without coating, (b) Au/CS nanocomposite, (c) Au/CMCS nanocomposite, and (d) Au/(CS+CMCS) nanocomposite.
(a)
Au Bare
(b)
Au/CS
(c)
Au/CMCS
(d)
Au/(CS+CMCS)Table1 lists the hydrodynamic diameter and the surface charge of the gold nanoparticles with different chitosan-based coatings in water. The chitosan-based coating significantly changed the surface property of the gold nanoparticles. The average particle size of the bare gold nanoparticles is 36 nm; after being coated with polymer, the hydrodynamic diameter of Au/CS, Au/CMCS, and Au/(CS+CMCS) reaches 290, 236, and 262 nm, respectively. Meanwhile, their surface charge changes from −43.5 mV to +43.8, +20.2 and +24.3 mV, respectively.Table 1
Surface property of the gold nanoparticles with different chitosan-based coatings. Particles are dispersed in DI water with a concentration of 1 OD/mL.
Nanoparticles
Coating components
Hydrodynamic diameter(nm, mean ± STD)
Zeta Potential(mV, mean ± STD)
Au Bare
None
36.0 ± 1.78
−43.5 ± 2.92
Au/CS
CS
290.4 ± 52.7
+43.8 ± 4.36
Au/CMCS
CMCS
235.5 ± 9.05
+20.2 ± 0.68
Au/(CS + CMCMS)
75 wt.% CS+25 wt.% CMCS
262.3 ± 58.9
+24.3 ± 0.80Figure4 shows the optical stability of the Au NPs with different coatings in PBS and 1 wt% NaCl solution. Since the physiologic salinity is near 1%, optical properties of Au NPs were simulated in these solutions. The optical stabilities were measured by monitoring the optical absorbance of the Au NPs at their NIR peak wavelength as function of time. These nanoparticles have similar behavior in the PBS and NaCl solution. CMCS-coated particles show the highest stability, and there is no obvious decrease in its optical absorption in 3h. The CS and CMCS blended coated particles also show good stability, with a decrease in its absorbance less than 10%. The most unstable particles are the bare Au NPs. Its absorbance decreases more than 70% in saline environment. The Au/CS nanocomposites are more stable than the bare particles, but less stable than the Au NPs with CMCS component in the coating. The decrease of NIR absorption of the bare Au NPs results from interparticle coupling effect [30, 31], in which its stabilized surface layer was disturbed due to the high ion strength, causing the particle aggregation (irreversible coalescence). This behavior may greatly decrease the efficiency of photothermal ablation. Chitosan-based coatings greatly improve the optical stability of the Au NPs. The instability of the Au/CS NPs mainly results from the sedimentation of particles caused by the agglomeration (reversible coalescence) of chitosan coating. At the pH value above 6, the solubility of chitosan becomes worse. CMCS has the best solubility in all pH ranges except its isoelectrical point [23]. The good solubility and the increased chain flexibility [32] of CMCS may prevent the coupling effect and the sedimentation of the particles.Optical stability of the Au NPs with different chitosan coatings in (a) PBS solution and in (b) 1 wt.% NaCl solution.
(a)
(b)By adjusting the surface components, the surface charge of the Au NPs can be modified. Figure5 shows the zeta potential of Au NPs with different chitosan coatings as function of the pH value. The isoelectric points (IEPs) of Au/CMCS, Au/(CS+CMCS), and Au/CS nanocomposites are 6.1, 7.1, and 7.7, respectively. IEP of CMCS is close to value (5.5) reported by Zhao et al. [33]. CMCS presents amine and carboxylic acid groups in its structure. In solution, the groups turn to the ion state, -NH3+ and –COO−, respectively, which improves the solubility of CMCS. Only at its IEP, the number of -NH3+ is equal to that of –COO−, resulting in the deceasing of solubility. Au/CS particle shows much higher IEP value than that of the Au/CMCS particles, since the CS only presents the positively charged groups (-NH3+). The IEP of the Au/(CS+CMCS) particle is 7.1, between the those of Au/CMCS and Au/CS. This shows that the surface charge of Au NPs can be tuned by the chitosan components on their surface, since CMCS possesses more negatively charged characteristic than CS.Figure 5
Effect of pH on Zeta potential of Au NPs with different coatings. Square point: Au/CMCS NPs, Triangle point: Au/CS NPs, Sphere point: Au/(CS+CMCS) NPs.


### 3.3. Photothermal Ablation of the HepG2 Cells

Figures6 and 7 show the live/dead stain images of the HDF and HepG2 cells after being exposed to the 817 nm NIR laser at 5 W/cm2, 2 min. The live/dead stain provides a two-color fluorescence assay of cell viability based on plasma membrane permeability, for reliably and quantitatively distinguishing live and dead cells. The live cells show the green color and dead cells show the red color. The statistical cell death ratio of HDF cells and HepG2 cells counted from the live/dead stain images are shown in Figure 8.Live/dead stain images of the HDF cells treated with different Au NPs after the laser ablation (5 W/cm2, 2 min). (a) control cells with no laser exposure, (b) cells without NPs, (c) cells treated with bare Au NPs, (d) cells treated with Au/CS NPs, (e) cells treated with Au/CMCS NPs, and (f) cells treated with Au/(CS+CMCS) NPs.
(a)
control
(b)
without Au NP
(c)
bare Au NP
(d)
Au/CS NP
(e)
Au/CMCS NP
(f)
Au/(CS+CMCS) NPLive/dead stain images of the HepG2 cells treated with different Au NPs after the laser ablation (5 W/cm2, 2 min). (a) control cells with no laser exposure, (b) cells without NPs, (c) cells treated with bare Au NPs, (d) cells treated with Au/CMCS NPs, (e) cells treated with Au/CS NPs, and (f) cells treated with Au/(CS+CMCS) NPs.
(a)
control
(b)
without Au NP
(c)
bare Au NP
(d)
Au/CS NP
(e)
Au/CMCS NP
(f)
Au/(CS+CMCS) NPFigure 8
Death percentage of HDF cell and HepG2 cell cells treated with different Au NPs after the laser ablation at 5 W/cm2, 2 min. (Average ± STD, n=3).Without incubation with Au NPs, cells do not exhibit obvious ablation after the laser irradiation at 5 W/cm2, 2 min, as shown in Figures 6(b) and 7(b). The bare Au NPs do not show significant photo-destruction on either cell lines (Figures 6(c) and 7(c)), due to the interparticle coupling effect [31]. The relatively low photothermal ablation efficiency of Au/CMCS NPs is probably due to their less adsorption on the cell membrane (Figures 6(e) and 7(e)). The highest efficiency of the photothermal ablation is observed from the cells treated with Au/CS NPs. There are almost 100% HepG2 cells, and 90% HDF cells were killed after the laser treatment (Figures 6(d) and 7(d)). The CS and CMCS blended coated gold NPs present the promising result: around 96% HepG2 cancer cells were ablated and less than 30% HDF normal cells died (Figures 6(f) and 7(f)). The differences of the Au NPs in the photothermal ablation result from the density of the Au NPs adsorbed on the cell surface. The negatively charged cell surface allows Au/CS NPs to highly accumulate on the cell surface, and high density particles generate extraordinary heat, damaging the HepG2 cells as well as the HDF cells under the laser radiation. Au/(CS+CMCS) particles bind to the cell surface uniformly and generate suitable heat, which was high enough to kill the cancer cells but not enough to damage all the normal cells. This consists with laser ablation results by using gold nanorod [16]. It was reported that after exposure to continuous red laser, malignant cells require about half the laser energy to be photothermally destroyed than the nonmalignant cells [16].


## 3.1. Preparation of Gold Nanoparticles with Desired Near Infrared Absorption

In our previous work [18, 25], a convenient method was developed to synthesize Au NPs with controllable NIR absorption. Au NPs were synthesized by one-step reaction of chloroauric acid and sodium thiosulfate, without assistance of additional templates, capping reagents, or seeds assembly. The synthesized products consist of nanoparticles with different shape and size including small spherical colloid gold particles (<5 nm) and nonspherical gold crystals. The nonspherical gold crystals are mainly the truncated octahedron, pentagons, and cuboctahedron, as well as the triangular-shaped plate structures [18]. Two absorption peaks due to the surface plasmon resonance are observed from these samples. The first SPR peak centered at around 530 nm is the characteristicSPR of the spherical colloid gold particles, and the second SPR component is higher at NIR band, which is attributed to the multipolar SPR band from the nonspherical Au NPs [18, 25]. Since the NIR absorption wavelengths increase with increasing molar ratio of HAuCl4/Na2S2O3, adjusting the molar ratio of HAuCl4/Na2S2O3 during the reaction controlled the absorption wavelength of the Au NPs. These products were further purified by the centrifugation to remove the spherical colloid gold particles, improving the NIR absorption. Figures 1(a) and 1(b) are the Z-contrast STEM images of the as-synthesized Au NPs and the same batch sample purified with centrifugation. The purified product possesses the NIR absorption wavelength at 820 nm. The temperature of the NIR absorbing Au NP suspension induced by the NIR laser radiation is affected by the concentration of nanoparticles, laser power, exposure time, and the absorbing wavelength of the Au NPs [26]. Figure 2 compares the heating effect of the Au NPs suspensions with NIR peak at 820 nm, 880 nm, 980 nm, and 1070 nm, respectively (showing in the insert figure) under the 817 nm wavelength diode laser (1 W/cm2) exposures. After 3 minutes, the temperature reaches to 50.8, 48.2, 46.4, and 41.2°C for the particles from low wavelength to high wavelength, respectively. The gold sample that has the NIR peak more close to the wavelength of laser source shows the best heating effect. The effective control of the NIR absorption of the gold nanoparticles for matching the wavelength of the laser source enhances the hyperthermia treatment. Meanwhile, the NIR wavelength is considered as the best light source for the photothermal therapy, because it is minimally absorbed by the normal tissues components of water and hemoglobin and can transmit deeply in the body.Z-contrast STEM images of the Au NPs synthesized from reaction of HAuCl4 and Na2S2O3 before and after centrifugation process. (a) As-synthesized Au NPs; (b) Au NPs after purification by centrifugation. The purified product has the NIR absorption peak at 820 nm.
(a)
(b)Figure 2
Heating effect of the gold nanoparticles with NIR absorption peaks at 820 nm, 880 nm, 980 nm, and 1070 nm, respectively, under the 817 nm wavelength laser exposures. The laser power is 1 W/cm2, and the Au NPs were dispersed in water at a concentration of 1 OD/mL. Inset shows the UV-visible-NIR spectra of the four Au NPs samples.


## 3.2. Chitosan-Based Coatings on the Gold Nanoparticles

Chitosan is a cationic polysaccharide of D-glucosamine and N-acetyl-D-glucosamine and has been shown to be a highly biocompatible material and have antibiotic properties. To improve its solubility or achieve new functionality, chemical modifications of chitosan were conducted and many derivatives have been synthesized. For example, modifications can be synthesized by carboxylation of the hydroxyl or amine groups in chitosan structure [20], resulting in the O-carboxymethyl chitosan or N-carboxymethyl chitosan respectively. O-carboxymethyl chitosan is achieved by substituting parts of the –OH at C-6 position of glucosamine units with –CH2COOH. Therefore, the reactive ligands such as –COOH and –NH2 groups are amenable to chemical functions. Others have reported the stabilization of GNPs with chitosan. As chitosan in solution is protonated and positively charged, it can be adsorbed onto the surfaces of gold nanoparticles, stabilizing and protecting the nanoparticles [27–29]. As-synthesized Au NPs present strongly negative surface charge (around −40 mV) allowing the positive charged chitosan tightly coated onto gold surface via electrostatic interaction.Figures3(a), 3(b), 3(c), and 3(d) show the high-resolution TEM images of the Au NPs without coating, Au/CS, Au/CMCS, and Au/(CS+CMCS) nanocomposites, respectively. The as-synthesized bare Au NPs have a 1-2 nm thin layer on their surface. Comparing to the bare Au NPs, Figures 3(b)–3(d) show the chitosan-based coatings effectively cover the gold NPs uniformly, forming a 2–5 nm thick layer on the gold surface.High-resolution TEM images of the Au NPs: (a) Au NPs without coating, (b) Au/CS nanocomposite, (c) Au/CMCS nanocomposite, and (d) Au/(CS+CMCS) nanocomposite.
(a)
Au Bare
(b)
Au/CS
(c)
Au/CMCS
(d)
Au/(CS+CMCS)Table1 lists the hydrodynamic diameter and the surface charge of the gold nanoparticles with different chitosan-based coatings in water. The chitosan-based coating significantly changed the surface property of the gold nanoparticles. The average particle size of the bare gold nanoparticles is 36 nm; after being coated with polymer, the hydrodynamic diameter of Au/CS, Au/CMCS, and Au/(CS+CMCS) reaches 290, 236, and 262 nm, respectively. Meanwhile, their surface charge changes from −43.5 mV to +43.8, +20.2 and +24.3 mV, respectively.Table 1
Surface property of the gold nanoparticles with different chitosan-based coatings. Particles are dispersed in DI water with a concentration of 1 OD/mL.
Nanoparticles
Coating components
Hydrodynamic diameter(nm, mean ± STD)
Zeta Potential(mV, mean ± STD)
Au Bare
None
36.0 ± 1.78
−43.5 ± 2.92
Au/CS
CS
290.4 ± 52.7
+43.8 ± 4.36
Au/CMCS
CMCS
235.5 ± 9.05
+20.2 ± 0.68
Au/(CS + CMCMS)
75 wt.% CS+25 wt.% CMCS
262.3 ± 58.9
+24.3 ± 0.80Figure4 shows the optical stability of the Au NPs with different coatings in PBS and 1 wt% NaCl solution. Since the physiologic salinity is near 1%, optical properties of Au NPs were simulated in these solutions. The optical stabilities were measured by monitoring the optical absorbance of the Au NPs at their NIR peak wavelength as function of time. These nanoparticles have similar behavior in the PBS and NaCl solution. CMCS-coated particles show the highest stability, and there is no obvious decrease in its optical absorption in 3h. The CS and CMCS blended coated particles also show good stability, with a decrease in its absorbance less than 10%. The most unstable particles are the bare Au NPs. Its absorbance decreases more than 70% in saline environment. The Au/CS nanocomposites are more stable than the bare particles, but less stable than the Au NPs with CMCS component in the coating. The decrease of NIR absorption of the bare Au NPs results from interparticle coupling effect [30, 31], in which its stabilized surface layer was disturbed due to the high ion strength, causing the particle aggregation (irreversible coalescence). This behavior may greatly decrease the efficiency of photothermal ablation. Chitosan-based coatings greatly improve the optical stability of the Au NPs. The instability of the Au/CS NPs mainly results from the sedimentation of particles caused by the agglomeration (reversible coalescence) of chitosan coating. At the pH value above 6, the solubility of chitosan becomes worse. CMCS has the best solubility in all pH ranges except its isoelectrical point [23]. The good solubility and the increased chain flexibility [32] of CMCS may prevent the coupling effect and the sedimentation of the particles.Optical stability of the Au NPs with different chitosan coatings in (a) PBS solution and in (b) 1 wt.% NaCl solution.
(a)
(b)By adjusting the surface components, the surface charge of the Au NPs can be modified. Figure5 shows the zeta potential of Au NPs with different chitosan coatings as function of the pH value. The isoelectric points (IEPs) of Au/CMCS, Au/(CS+CMCS), and Au/CS nanocomposites are 6.1, 7.1, and 7.7, respectively. IEP of CMCS is close to value (5.5) reported by Zhao et al. [33]. CMCS presents amine and carboxylic acid groups in its structure. In solution, the groups turn to the ion state, -NH3+ and –COO−, respectively, which improves the solubility of CMCS. Only at its IEP, the number of -NH3+ is equal to that of –COO−, resulting in the deceasing of solubility. Au/CS particle shows much higher IEP value than that of the Au/CMCS particles, since the CS only presents the positively charged groups (-NH3+). The IEP of the Au/(CS+CMCS) particle is 7.1, between the those of Au/CMCS and Au/CS. This shows that the surface charge of Au NPs can be tuned by the chitosan components on their surface, since CMCS possesses more negatively charged characteristic than CS.Figure 5
Effect of pH on Zeta potential of Au NPs with different coatings. Square point: Au/CMCS NPs, Triangle point: Au/CS NPs, Sphere point: Au/(CS+CMCS) NPs.


## 3.3. Photothermal Ablation of the HepG2 Cells

Figures6 and 7 show the live/dead stain images of the HDF and HepG2 cells after being exposed to the 817 nm NIR laser at 5 W/cm2, 2 min. The live/dead stain provides a two-color fluorescence assay of cell viability based on plasma membrane permeability, for reliably and quantitatively distinguishing live and dead cells. The live cells show the green color and dead cells show the red color. The statistical cell death ratio of HDF cells and HepG2 cells counted from the live/dead stain images are shown in Figure 8.Live/dead stain images of the HDF cells treated with different Au NPs after the laser ablation (5 W/cm2, 2 min). (a) control cells with no laser exposure, (b) cells without NPs, (c) cells treated with bare Au NPs, (d) cells treated with Au/CS NPs, (e) cells treated with Au/CMCS NPs, and (f) cells treated with Au/(CS+CMCS) NPs.
(a)
control
(b)
without Au NP
(c)
bare Au NP
(d)
Au/CS NP
(e)
Au/CMCS NP
(f)
Au/(CS+CMCS) NPLive/dead stain images of the HepG2 cells treated with different Au NPs after the laser ablation (5 W/cm2, 2 min). (a) control cells with no laser exposure, (b) cells without NPs, (c) cells treated with bare Au NPs, (d) cells treated with Au/CMCS NPs, (e) cells treated with Au/CS NPs, and (f) cells treated with Au/(CS+CMCS) NPs.
(a)
control
(b)
without Au NP
(c)
bare Au NP
(d)
Au/CS NP
(e)
Au/CMCS NP
(f)
Au/(CS+CMCS) NPFigure 8
Death percentage of HDF cell and HepG2 cell cells treated with different Au NPs after the laser ablation at 5 W/cm2, 2 min. (Average ± STD, n=3).Without incubation with Au NPs, cells do not exhibit obvious ablation after the laser irradiation at 5 W/cm2, 2 min, as shown in Figures 6(b) and 7(b). The bare Au NPs do not show significant photo-destruction on either cell lines (Figures 6(c) and 7(c)), due to the interparticle coupling effect [31]. The relatively low photothermal ablation efficiency of Au/CMCS NPs is probably due to their less adsorption on the cell membrane (Figures 6(e) and 7(e)). The highest efficiency of the photothermal ablation is observed from the cells treated with Au/CS NPs. There are almost 100% HepG2 cells, and 90% HDF cells were killed after the laser treatment (Figures 6(d) and 7(d)). The CS and CMCS blended coated gold NPs present the promising result: around 96% HepG2 cancer cells were ablated and less than 30% HDF normal cells died (Figures 6(f) and 7(f)). The differences of the Au NPs in the photothermal ablation result from the density of the Au NPs adsorbed on the cell surface. The negatively charged cell surface allows Au/CS NPs to highly accumulate on the cell surface, and high density particles generate extraordinary heat, damaging the HepG2 cells as well as the HDF cells under the laser radiation. Au/(CS+CMCS) particles bind to the cell surface uniformly and generate suitable heat, which was high enough to kill the cancer cells but not enough to damage all the normal cells. This consists with laser ablation results by using gold nanorod [16]. It was reported that after exposure to continuous red laser, malignant cells require about half the laser energy to be photothermally destroyed than the nonmalignant cells [16].


## 4. Conclusions

Gold/chitosan nanocomposites were synthesized for the photothermal therapy applications. Au NPs were prepared by the reaction of chloroauric acid with sodium thiosulfate, and they have specific NIR absorption matching the wavelength of laser source. These Au NPs were coated with chitosan or O-carboxymethyl chitosan as well as a blending. These chitosan coatings protect the gold nanoparticles, avoiding irreversible coalescence of the bare Au NPs and improving their optical stability, making photothermal ablation possible. The surface charge of the Au/chitosan nanocomposites can be modified by adjusting the CS and CMCS components on the gold surface to achieve suitable binding of the Au NPs on the cell surface. The Au/CS nanocomposites show high accumulation on the cell surface and present the highest laser ablation efficiency. The CS and CMCS blended coatings allow Au NPs uniformly binding to the cells, showing higher selectivity between the cancer cells and normal cells during the photothermal ablation. These novel gold/polymer nanocomposites have great potential for photothermal therapy, due to low-dosage particle injection, low-power NIR laser radiation, and quick ablation. More broad clinical relevance can be envisioned, such as the breast cancer treatment, skin cancer treatment, esophageal cancer treatment, and laryngocarcinoma cancer treatment.



---