# Preparation of Silica Aerogel and Its Adsorption Performance to Organic Molecule

Authors: Hong-xin Shi; Jing-tao Cui; Hai-min Shen; Hong-ke Wu
Journal: Advances in Materials Science and Engineering
 (2014)

---

## Abstract

Hydrophobic and lipophilic silica aerogel was prepared from water-glass by gelling, aging, silylation, and drying under atmospheric pressure and characterized by FT-IR and SEM. The effect of preparation process on aerogel density and the aerogel density on contact angle of water on it were investigated in detail. pH 6 is most beneficial to shorten gelling time and to obtain the lowest density of silica aerogel. Increasing TEOS concentration of aging solution to 25 v% could decrease aerogel density to 0.093 g/cm3. The silica aerogel exhibits good hydrophobicity even though its density is 0.30 g/cm3. There are few changes in their adsorption capacities after 3 cycles of adsorption-desorption. The adsorption performance of the silica aerogel to organic solvent in water is different from in pure solvents. The critical surface tension (γC) of the silica aerogel prepared here is about 30.8 mN/m. If the surface tension of aqueous solvent solution (γ) is greater than γC, it will wet the aerogel surface partially. If γ  ≤  γC, the solution will wet all aerogel surface and be adsorbed well. This work delivers us a method to adsorb solvents from their waste water by adjusting the surface tension of the waste water to lower than γC of the adsorbent.


---

## Body

## 1. Introduction

Silica aerogel [1–4] is a nanostructured material with open foam-like structures having very low density (as low as 3 kg/m3), high specific surface area (700–1000 m2/g), and extremely high porosity (98%-99%) [5]. These features lead to unique properties due to excellent accessibility of the inner surface through open porous network. The most interesting feature of silica aerogel is the controllability of the surface polarity between hydrophobicity and hydrophilicity. Various applications such as thermal super insulation, catalyst support, microfilters, controlled release of drugs, and inertial confinement fusion targets have already been investigated and reported [6, 7]. Because of their very high specific surface area and porosity as well as hydrophobicity, silica aerogel is an ideal adsorbent for organic compounds.Rao et al. investigated the adsorption and desorption of organic liquids on silica aerogel and found that the aerogel could adsorb the organic liquids and oils by nearly 15 times of its own mass [8]. Wang et al. studied the equilibrium and kinetics of sorption of generic vegetable cooking oil, motor oil, and crude oil from the liquid phase and from an oil-in-water emulsion on two different particle-size hydrophobic silica aerogels and found that the aerogels had a very high capacity (up to 15.1 g oil/g aerogel) and rate (uptake time of 25–1200 s) for adsorption of liquid oils; thus they regarded the aerogels as a very attractive adsorbent for oil spill clean-up [9]. Wang et al. investigated the adsorption of six volatile organic compounds in vapor, liquid, and aqueous solution on hydrophobic aerogels and found that the rate for adsorption are very different, with the uptake time in the order of about 100 min for vapor, 10 min for solution, and 10 s for liquid. The slowest rate of adsorption for vapor is due to the fact that the aerogel has an extremely low thermal conductivity [10]. Štandeker et al. synthesized some silica aerogels and used them to adsorb toxic organic compounds from water. They found that the adsorption capacity of both hydrophobic silica aerogel adsorbents M9 and E6 exceeded the capacity of comparable granular activated carbon, for all toxic organic compounds tested in ranges of factors from 15 to 400 [3]. Štandeker et al. assessed the ability of modified silica aerogel with mercapto group to remove Cu(II) and Hg(II) from aqueous solutions using batch adsorption technique under equilibrium conditions. They found the adsorbent exhibited very high adsorption potential for Cu(II) and Hg(II) and more than 99.0% removal was achieved in the pH range of 4–6 [11].The common preparation of silica aerogel includes supercritical drying and expensive raw materials like tetraethoxysilane which prohibit its commercialization. There are capillary forces in the gel pores which make the gel shrink and even lead to the gel collapse when aerogel is dried [12]. Supercritical drying process can avoid the shrinkage and the collapse of aerogel completely, but its high cost makes it difficult to prepare aerogel in large scale. Schwertfeger et al. used water-glass combined with silylation and drying of the lyogel under atmospheric pressure to produce durably hydrophobic aerogel [13]. Their new process makes the aerogel production become cost-effective and more commercial.Silica aerogel shows a very high uptake capacity for pure organic compounds. It adsorbs about 14.3 g benzene, 13.6 g toluene, or 14.4 gp-xylene per gram silica aerogel [10]. But its uptake capacity for organics from their aqueous solution cuts down sharply, for example, 87 mg benzene, 223 mg toluene, or 1064 mg p-xylene per gram silica aerogel, respectively [10]. It is the hydrophobicity of silica aerogel that prohibits the aqueous solution of organic compounds entering into the interior pores of silica aerogel, and only external space but not internal space of the aerogel adsorbs the organic compounds. This is the main cause of the decreased uptake capacity of organic compounds on silica aerogels. In the present study, we used water-glass as precursor, combined with silylation and drying of the lyogel under atmospheric pressure to prepare silica aerogel. The performances to adsorb organic compounds from their aqueous solutions on the aerogel were studied. The uptake capacity of these adsorbent will increase greatly in the presence of penetrating agent.


## 2. Experimental

### 2.1. Preparation of the Silica Hydrogel

The silica hydrogels were prepared through Shen’s process with water-glass as starting material [14, 15]. One L water-glass solution (SiO2 content 8 wt%, n(Na2O) : n(SiO2) = 1 : 3.1) was filtrated to remove solid impurities. 81 g water-glass solution was dropped into 4.5 g 35% hydrochloric acid with agitation at ambient temperature. After dropping, the mixture was continued agitation for 7 h to hydrolyze the water-glass. Then, some aqueous ammonia solution was added to adjust the pH value of the mixture. The hydrogel obtained was aged in distilled water for 2 h and in anhydrous alcohol for several hours at ambient temperature, respectively.


### 2.2. Silylation and Drying of the Silica Hydrogels

For the silylation, 5 g of the aged hydrogel sticks was placed together with 20 g hexamethyldisiloxane (HMDSO), 15 g trimethylchlorosilane (TMCS), and 50 mL hexane in a beaker at ambient temperature for 24 h. The resulted silylated lyogel sticks were dried at ambient temperature for 2 h, then elevated temperature at 1°C/min to 60°C, and stayed at 60°C for 2 h. After cooling to ambient temperature, the silica aerogel was obtained.


### 2.3. Characterization of the Silica Aerogels

The microstructure of the silica aerogel was observed by Hitachi S-4700 field emission scanning electron microscope (Hitachi). Specific surface and pore radius were measured by SP 1900 Physisorption Analyzers. Hydrophobicity was presented as water contact angle on the aerogel which was measured by OCA-20 optical contact angle measuring system (Dataphysics). Silylation efficiency was measured by NEXUS Fourier transform infrared spectroscopy (Thermo Nicolet). The bulk density (ρb) of the aerogel was measured using a known volume of the aerogel and its weight was measured with a microbalance, 10-5g accuracy.


### 2.4. Adsorption Capacity Determination

The aerogel sample was kept in an organic solvent until it was completely wetted by the liquid. A conventional batch equilibration procedure was used as isotherm testing [16]. To achieve accurate results, the adsorption measurements were accomplished under equilibrium conditions.


## 2.1. Preparation of the Silica Hydrogel

The silica hydrogels were prepared through Shen’s process with water-glass as starting material [14, 15]. One L water-glass solution (SiO2 content 8 wt%, n(Na2O) : n(SiO2) = 1 : 3.1) was filtrated to remove solid impurities. 81 g water-glass solution was dropped into 4.5 g 35% hydrochloric acid with agitation at ambient temperature. After dropping, the mixture was continued agitation for 7 h to hydrolyze the water-glass. Then, some aqueous ammonia solution was added to adjust the pH value of the mixture. The hydrogel obtained was aged in distilled water for 2 h and in anhydrous alcohol for several hours at ambient temperature, respectively.


## 2.2. Silylation and Drying of the Silica Hydrogels

For the silylation, 5 g of the aged hydrogel sticks was placed together with 20 g hexamethyldisiloxane (HMDSO), 15 g trimethylchlorosilane (TMCS), and 50 mL hexane in a beaker at ambient temperature for 24 h. The resulted silylated lyogel sticks were dried at ambient temperature for 2 h, then elevated temperature at 1°C/min to 60°C, and stayed at 60°C for 2 h. After cooling to ambient temperature, the silica aerogel was obtained.


## 2.3. Characterization of the Silica Aerogels

The microstructure of the silica aerogel was observed by Hitachi S-4700 field emission scanning electron microscope (Hitachi). Specific surface and pore radius were measured by SP 1900 Physisorption Analyzers. Hydrophobicity was presented as water contact angle on the aerogel which was measured by OCA-20 optical contact angle measuring system (Dataphysics). Silylation efficiency was measured by NEXUS Fourier transform infrared spectroscopy (Thermo Nicolet). The bulk density (ρb) of the aerogel was measured using a known volume of the aerogel and its weight was measured with a microbalance, 10-5g accuracy.


## 2.4. Adsorption Capacity Determination

The aerogel sample was kept in an organic solvent until it was completely wetted by the liquid. A conventional batch equilibration procedure was used as isotherm testing [16]. To achieve accurate results, the adsorption measurements were accomplished under equilibrium conditions.


## 3. Results and Discussion

Using low-cost industrial water-glass as silicon source to produce silicon aerogel, complete ionic exchange and water washing are necessary steps. But the process using water-glass with the two steps of acid-base catalysts (HNO3-NaOH), without ionic exchange, and possessing surface modification under atmospheric condition to produce nanoporous silica aerogels was reported [14]. We used hydrochloric acid and aqueous ammonia solution (HCl-NH4OH) to substitute HNO3-NaOH. The hydrolyzation is presented as the reactions (1)~(3). Reactions (2) and (3) are the same as reaction (4):
(1)Na2O+2HCl⟶2NaCl+H2O(2)SiO2+6HCl⟶H2[SiCl6]+2H2O(3)H2[SiCl6]+4H2O⟶H4SiO4+6HCl(4)(2)+(3)⟶SiO2+2H2O=H4SiO4After neutralizing with NH4OH, the mixture gelled and polycondensed to three-dimension molecules (5).(5)The relation of gelling time to the pH value of the mixture was shown in Figure1. When the mixture was acidic, for example, pH 4, hydrolization was fast, and the polycondensation of the orthosilicic acid (H4SiO4) was slow, the mixture gelled slowly and took about 260 min. The gelling time declined sharply with increased pH value and was 20 min at pH 6. When the pH value increased from pH 6 to pH 8, the gelling time declined very slowly, but white floccule appeared at pH 7 and white deposit occurred quickly at pH 8. The polycondensation rate increased with the increase of the pH value of the mixture, and when pH value is greater than 6, H4SiO4 condenses so quickly that it was easy to form gel particles, gathered to form white floccules (pH 7) and even a dense white deposit (pH 8). So, pH 6 is most proper for gelling. Good aerogel generally has very high porosity which produces its low density and high specific surface area. Shen has found that two steps of HNO3-NaOH catalysts with water-glass could result in lower aerogel density (0.068~0.096 g/cm3) than that of quick step of HF (0.327~0.354 g/cm3). We found that adding NH4OH to the mixture could influence the aerogel density obtained. The effect of the pH value of the mixture on the aerogel density was shown in Figure 2. Figure 2 shows that gelling at pH 6 could prepare aerogel with the smallest density. Elevating or decreasing the pH value of the mixture made the aerogel density increase. It is clear that pH 6 is the best pH value in gelling. The hydrolization rate may be equal to the polycondensation rate at pH 6; the aerogel grew properly in three dimensions and formed some internal pores which made the aerogel density decline. If the pH value was smaller than 6, the hydrolization rate may be greater than the polycondensation rate; many aerogel particles appeared and grew at the same time which made aerogel particle become smaller and made internal pores reduce, so that the aerogel density increased. If the pH value was great than 6, for example, pH 8, the hydrolization rate may be smaller than the polycondensation rate, H4SiO4 polycondensed very quickly as soon as it produced from hydrolyzation, precipitation but not aerogel growth took place, and few pores formed so that the aerogel density also increased.Figure 1
The relation of gelling time to the pH value of the mixture.Figure 2
The relation of aerogel density to the pH value of the mixture.Aging of hydrogel is very important operation for preparing silica aerogel. The polycondensation inside hydrogel does not finish completely without aging; then the hydrogel network will be not strong enough to endure the capillary force added by the surface tension of solvent during drying stage, which makes the aerogel shrink and dilapidate. Aging of hydrogel is a necessary step for aerogel to avoid shrinkage and dilapidation. In aging operation, hydrogel, were dipped into 0%, 5%, 15%, 25%, 35%, and 40% tetraethoxysilane (CTEOS v%) solution in ethanol, respectively. The effect of CTEOS v% of aging solution on the aerogel density was shown in Figure 3.Figure 3
The relation of aerogel density to the TEOS concentration in aging solution.When pure ethanol was used,CTEOS=0 v%, the density was 0.15 g/cm3; adding TEOS gradually, the density declined firstly and then increased; when CTEOS=25 v%, the density reached the smallest value, 0.093 g/cm3; when CTEOS>25 v%, the density turned to increase. This is because there was water in hydrogel which made TEOS hydrolyze to ≡Si–OH, =Si(OH)2, and –Si(OH)3; they reacted with the hydroxy groups of hydrogel to strengthen hydrogel network, so that to delimit the aerogel shrinkage during drying. Before aging, there were many interpores full of water in the hydrogel. During aging, the water in the pores could be substituted by ethanol. This substitution should be finished enough so that the aerogel could avoid shrinkage and collapse; then smaller density of aerogel could be obtained. When CTEOS was lower, the water was substituted completely. When CTEOS was higher, or Cethanol was lower, the water could not be substituted completely. The higher the CTEOS, the more the water remained in the pores and the more shrinkage and collapse of aerogel, then the greater the aerogel density.The silica aerogel prepared is Cambridge blue solid with BET surface area of 838.6 m2/g, pore volume of 1.072 cm3/g, and average pore width of 5.11 nm. SEM image of the silica aerogel was shown in Figure 4. It is very clear that the silica aerogel is multiporous nanomaterial with concatenate network structure. Because the external and internal surfaces of the aerogel were treated with hexamethyldisiloxane (HMDSO) and trimethylchlorosilane (TMCS), it exhibited hydrophobicity. The image of water on the silica aerogel prepared was shown in Figure 5. The water contact angle on the aerogel was about 138°.Figure 4
SEM micrograph of silica aerogel.Figure 5
Image of water on the silica aerogel.The water contact angle on aerogel is related to the preparation process containing silicon source, gelling, aging, silylation, and drying; all of that can influence the aerogel density, which determines the water contact angle on the aerogel and its hydrophobicity. We selected some silica aerogels with different densities ranged from 0.093 g/cm3 to 0.30 g/cm3 and measured their water contact angles which ranging from 138° to 110°. The relation of the water contact angle to aerogel density was shown in Figure 6. It is very clear that the water contact angle on the silica aerogel declines gradually with the increase of its density. The lower the aerogel density, the greater the water contact angle. The silica aerogel presents good hydrophobicity even though its density is 0.30 g/cm3. This result tells us that controlling silica aerogel density can adjust its hydrophobicity.Figure 6
Water contact angle versus aerogel density.Hydrophobic silica aerogel is lipophilic and can adsorb organic compounds. One g powdery active carbon, silica gel, and silica aerogel (0.084 g/cm3) prepared were added into pure toluene, xylene, chlorobenzene, DMSO, and MeOH at ambient temperature for 1 h, respectively. After filtration in vacuum, the wet solid adsorbents were weighted and the adsorption capacities of each adsorbents were calculated, which were shown in Figure 7. For adsorbates, the adsorption capacity order is silica aerogel ≫ silica gel > active carbon except for MeOH. Active carbon is a common adsorbent for organic adsorbates; its adsorption capacity is smaller than 1 g/g for organic compounds tested. But the corresponding adsorption capacity of silica aerogel is equal to or greater than 7 g/g. The aerogel can especially adsorb about 10 times of chlorobenzene compared to 0.4 time for active carbon. Silica aerogel exhibits excellent adsorption performance.Figure 7
Adsorption capacities of various adsorbents.After adsorption, organic adsorbates were desorbed from silica aerogel at ambient temperature. Elevated temperature will quicken desorption. For example, it takes about 220 min (at 25°C) and 10 min (at 100°C) for toluene desorption, respectively. The images of silica aerogel in different states of adsorbing and desorbing toluene were shown in Figure8. After absorbing toluene, the volume of aerogel became a little bigger and its color looked gloomy. After desorption, the appearance of aerogel seemed to return to its original state.Figure 8
Images of aerogel adsorbing and desorbing toluene.After desorption, the silica aerogel was applied to adsorb organic compounds again and their adsorption capacities were listed in Table1. There are few changes in their adsorption capacities among the first, the second, and the third cycles.Table 1
The adsorption capacities of silica aerogel.
No
Adsorbate
Adsorption capacities (g/g)
First cycle
Second cycle
Third cycle
1
Chlorobenzene
10.12
10.06
10.01
2
DMSO
9.60
9.51
9.44
3
Xylene
8.92
8.89
8.82
4
Methanol
7.24
7.19
7.11
5
Toluene
7.00
6.94
6.95Various aqueous solutions of THF, DMF, acetone, CH3CN, ethanol, AcOH, and MeOH were prepared. 0.05 g silica aerogel was added into 20 mL solutions at ambient temperature for sufficient time, respectively, and the adsorption capacities were calculated. The capacities of silica aerogel to adsorb solvent from their aqueous solution in different volume concentrations (CSolvent) were recorded in Figure 9. It is shown that when CSolvent is lower than 30 v%, the adsorption capacities are similar and smaller than 1 g/g. Increasing CSolvent, especially from 30 v% to 50 v%, the adsorption capacities increase sharply. If CSolvent continues to increase, the adsorption capacities continue to increase slowly. The performances of aerogel in adsorbing pure solvents and aqueous solvent solutions are very different. In adsorption equilibrium, the adsorbing capacities in aqueous solvent solutions are very lower than those of corresponding pure solvents. For example, the capacity to adsorb 30 v% ethanol solution is about 0.85 g/g, but 7.00 g/g for pure ethanol. The adsorbing performance of aerogel to DMF solution is very interesting. When CDMF<75 v%, little adsorption takes place, but when CDMF increases a little, the adsorption capacity increases sharply. When CDMF=80 v%, the adsorption capacity reaches to 5.0 g/g. The differences of adsorption capacities of aerogel between pure solvents and aqueous solvent solutions may be caused by surface hydrophobicity and lipophilicity of silica aerogel.Figure 9
Capacities of silica aerogel adsorbing solvents from their aqueous solution.Figure10 presents the balance of forces at the solid-vapor, solid-liquid, and liquid-vapor interface. If the contact angle is above 90°, there is no spreading of the liquid and the aerogel is said to be impervious. When the contact angle is less than 90°, the liquid spreads on the aerogel surface and when the liquid is completely adsorbed by the aerogel, the contact angle is equal to zero. The imper-viousness of the aerogels against solvents in water observed in various concentrations was researched by the contact angle measurements. Table 2 shows the contact angle (θ) of aqueous solution with different percentage of solvents (CSolvent, v%). It is very clear from Table 2 that, with the increase of CSolvent, the contact angle decreases. The aerogel is impervious against the solvents in water, the concentrations of which are up to 37 v% (THF), 48 v% (acetone), 34 v% (CH3CN), 74 v% (DMF), 35 v% (ethanol), 26 v% (acetic acid), and 39 v% (methanol), respectively.Table 2
Contact angle measurements for silica aerogel with different solvents in water.
Solvent
C
Solvent (v%)
Contact angle (°)
THF
0
153
10
150
30
137
37
90
40
82
48
Adsorption
Acetone
10
147
30
145
40
137
48
90
50
85
65
Adsorption
CH3OH
10
147
30
126
39
90
40
86
50
69
70
34
73
Adsorption
CH3CN
10
150
30
130
34
90
40
69
50
Adsorption
C2H5OH
10
148
30
110
35
90
40
70
50
40
53
Adsorption
DMF
10
148
50
141
70
138
74
90
75
80
90
Adsorption
CH3COOH
10
143
26
90
30
82
40
63
50
41
70
21
78
AdsorptionFigure 10
Balance of forces at the contact line solid-liquid-vapor system.The mass of the organic liquid adsorbed by aerogel depends upon the surface tension(γ) of the corresponding liquid. From Young’s equation [17],
(6)γsv=γsl+γlvcos⁡θ,
where γsv, γsl, and γlv are solid-vapor, solid-liquid, and liquid-vapor interfacial energies, respectively (Figure 10). If the material has a low energy surface(γsv<γsl), the contact angle (θ) will be >90° and the liquid cannot spread on the surface but remain in the form of a drop. This phenomenon is observed when CSolvent is low, for example, 10 v%. If the material has a high energy surface (γsv>γsl), the contact angle (θ) will be less than 90° and the liquid can spread on the surface. For example, when CMethanol=70 v%, the aqueous methanol solution spreads on the aerogel. If the material has a very high energy surface (γsv≫γsl), the contact angle (θ) will be zero and the liquid is fully adsorbed by the material. For example, when CMethanol=73 v%, methanol was adsorbed completely by the aerogel.Table3 shows the lowest concentrations of ethanol, methanol, THF, and acetone in water in which the solvent solutions can be adsorbed by the silica aerogel (i.e., θ=0). We measured the surface tensions of these aqueous solutions and listed these results in Table 3. From the data, we found that the average surface tension is about 30.9 mN/m which equals the critical surface tension (γC) of the silica aerogel according to Zisman’s rule [18]. If the surface tension of aqueous solvent solution γ>γC, the solution will wet the aerogel surface partially. If γ≤γC, the solution will wet all of the aerogel surface. If γ≫γC, the solution hardly enters inside aerogel and wets few aerogel surface, and the contact angel of the solution drop is greater than 90°, so aerogel adsorbs little solvent from the solvent solution in water. We prepared 20 v% solvent solutions in water, using penetrating agent A (delivered by Taizu New Materials Co., Ltd) to adjust the surface tensions of these solutions and measured the capacities of aerogel adsorbing the solvents in water before and after adjustment, respectively. The results were listed in Table 4 and show that the surface tensions of aqueous 20 v% solvent solutions are greater than γC, so their adsorption capacities are very small; once adding penetrating agent A in the solvent solutions, the surface tensions decline sharply to much smaller than γC, and the adsorption capacities are increased sharply. This deliver us a process to adsorb solvents from their waste water by adjusting the surface tension of the waste water to much lower than γC of the adsorbent. This will be very useful and practical to deal with the waste water containing some organic compounds.Table 3
The lowest concentration of solvents solution in whichθ=0 and their surface tensions.
Solvent
Ethanol
Methanol
THF
Acetone
C (v%)
53
73
48
65
γ (mN/m)
29.6
31.0
31.9
30.9Table 4
The adsorption capacities of 20 v% solvent solutions in water in different surface tensions.
Solutions
20 v% solvent
20 v% solvent—6 g/L penetrating agent
γ (mN/m)
Adsorption capacity (g/g)
γ (mN/m)
Adsorption capacity (g/g)
CH3CN
33.67
0.3
20.14
4.0
Acetone
35.54
0.2
21.22
6.2
THF
32.21
0.7
19.94
7.4
DMF
48.98
0
23.20
5.2
Ethanol
38.65
0.5
22.12
6.3
CH3COOH
41.72
0.8
22.47
6.4
Methanol
45.83
0.3
23.11
5.8


## 4. Conclusion

Hydrophobic and lipophilic silica aerogel was prepared from water-glass by gelling, aging, silylation and drying at atmospheric pressure. The pH value influence the gelling time of water-glass mixture. pH 6 is the best value to shorten gelling time and to obtain the lowest density of silica aerogel. Increasing TEOS concentration of aging solution to 25 v% could decrease aerogel density to 0.093 g/cm3. The preparation process will influence the aerogel density which determins the water contact angle on the aerogel, that is, its hydrophobisity. The water contact angle on the silica aerogel declines gradually with the increase of its density. The silica aerogel exhibits good hydrophobicity even though its density is 0.30 g/cm3. The adsorption capacities of silica aerogel are equal to or greater than 7 g organics tested/g adsorbent. There are few changes in their adsorption capacities after 3 cycles of adsorption-desorption. The performances of aerogel adsorbing to solvent solutions in water are different from those in the pure solvents. When CSolvent is lower than 30 v%, the adsorption capacities are similar and smaller than 1 g solvent/g adsorbent. The critical surface tension (γC) of the silica aerogel prepared is about 30.8 mN/m. If the surface tension of aqueous solvent solution (γ) is greater than γC, it will wet the aerogel surface partially. If γ≤γC, the solution will wet all the aerogel surface. Adjusting surface tension of the solvent solution in water to much smaller than γC of aerogel, the aerogel will adsorb solvent efficiently from its aqueous solution.



---