# Influence of Bath Composition at Acidic pH on Electrodeposition of Nickel-Layered Silicate Nanocomposites for Corrosion Protection

Authors: Jeerapan Tientong; Casey R. Thurber; Nandika D’Souza; Adel Mohamed; Teresa D. Golden
Journal: International Journal of Electrochemistry
 (2013)

---

## Abstract

Nickel-layered silicates were electrochemically deposited from acidic bath solutions. Citrate was used as a ligand to stabilize nickel (II) ions in the plating solution. The silicate, montmorillonite, was exfoliated by stirring in aqueous solution over 24 hours. The plating solutions were analyzed for zeta-potential, particle size, viscosity, and conductivity to investigate the effects of the composition at various pHs. The solution particles at pH 2.5 (−22.2 mV) and pH 3.0 (−21.9 mV) were more stable than at pH 1.6 (−10.1 mV) as shown by zeta-potential analysis of the nickel-citrate-montmorillonite plating solution.Ecorr for the films ranged from −0.32 to −0.39 V with varying pH from 1.6 to 3.0. The films were immersed in 3.5% NaCl and the open circuit potential monitored for one month. The coatings deposited at pH 3.0 were stable 13 days longer in the salt solution than the other coatings. X-ray diffraction showed a change in the (111)/(200) ratio for the coatings at the various pHs. The scanning electron microscopy and hardness results also support that the electrodeposition of nickel-montmorillonite at pH 3.0 (234 GPa) had improved hardness and morphology compared to pH 2.5 (174 GPa) and pH 1.6 (147 GPa).


---

## Body

## 1. Introduction

A steady demand for enhanced coatings at a reduced cost has been the main focus in the area of corrosion for many years. Degradation of the coatings takes place because of unfavorable environmental conditions that lead to many types of corrosion [1–4]. Since it is difficult to completely stop corrosion, the best economical idea is to simply reduce the rate at which it occurs [5]. Low cost, convenience, and the ability to work at low temperatures have made electro-deposition one of the more favorable techniques to synthesize coatings [6]. The applied potential, pH, temperature, and current all play a role in determining the morphology, structure, and composition of the coatings [6–8].One metal commonly used to enhance corrosion resistance is nickel because of its high abundance and capability to protect against common corrosion [1–4]. Nevertheless, corrosion resistance from metal coatings tends to be unsuccessful because of reduced mechanical properties. Forming alloys, with metals such as zinc, seems to be the answer to increasing the corrosion resistance [7]. The alloyed coatings tend to enhance the corrosion resistance properties but possess mechanical properties that are comparable to the individual metals. Ceramic fortification into the metal coatings can improve mechanical properties. To increase the hardness and life of nickel coatings, different nanoparticles such as TiO2, CeO2, SiC, and Al2O3 have been integrated into the matrix of the coating [9–14].The ceramic compounds that are being investigated for this study are layered silicates, which possess many advantageous properties such as a high surface area, good chemical resistance, resistance to extreme temperatures, and resistance to pH. Incorporation of the layered silicates into polymers [15–17] and ceramics [18, 19] to form composites has enhanced the mechanical properties. In the case of conductive polymer composite coatings, scientists have shown that layered silicates increase the resistance to corrosion [20, 21]. The incorporation of the layered silicates into the metal matrix should prove to be fruitful for enhanced resistance to corrosion and hardness in the nanocomposite coating.In this work, nickel-layered silicate nanocomposite films were electrochemically deposited using pulsed potentiostatic conditions from an acidic plating bath containing exfoliated layered silicate to enhance adhesion to the substrate, corrosion resistance, and mechanical properties. Scanning electron microscopy (SEM) was chosen to analyze the morphology of the electrodeposited films. X-ray diffraction (XRD) was used to analyze the crystal structure of the films. The corrosion resistance and hardness of the nanocomposite films were compared with each bath condition using Tafel polarization, immersion tests, and nanoindentation. The pH of the plating solution was varied by adding different amounts of sodium citrate and citric acid. The citrate ligand was used to stabilize nickel ions in the plating solution. Viscosity, conductivity, zeta potential, and particle size were all measured for the addition of montmorillonite to the plating solution.


## 2. Experimental

### 2.1. Materials

Nickel-layered silicates were electrochemically deposited from acidic plating baths at pH 1.6, 2.5, and 3.0 at 25°C. The montmorillonite (MMT) (5 g/L) aqueous solution from Southern Clay Products was mechanically agitated using a magnetic stirrer over 24 hours to obtain exfoliated layered silicate platelets. Citric acid anhydrous and/or sodium citrate dihydrate was utilized as a ligand to stabilize nickel (II) ions. The composition of nickel-citrate plating baths at different pHs was prepared from NiSO4 · 6H2O (Alfa Aesar) and Na3C6H5O7 · 6H2O (Fisher Scientific) or H3C6H5O7 (Fisher Scientific) as shown in Table 1.Table 1
Values of the acidic plating bath composition for nickel, citrate, and citric acid.
Chemical
pH 1.6
pH 2.5
pH 3.0
NiSO4·6H2O
77.8 g/L
77.8 g/L
77.8 g/L
Na3C6H5O7·6H2O
—
35.3 g/L
52.9 g/L
H3C6H5O7
57.6 g/L
34.6 g/L
23.0 g/LThe exfoliated MMT solution was added to the nickel and citrate salts and then stirred with a magnetic stirrer until dissolved. The pH of the plating solution was measured with a Corning pH meter and Pasco Scientific pH electrode. The electrochemical cell was comprised of three electrodes: chromel wire (counter electrode), saturated calomel (reference electrode), and stainless steel discs (working electrode). Stainless steel discs with a diameter of 1 cm2 were polished mechanically with 600, 800, and 1000 grit silicon carbide paper and then with 3 and 1 μm diamond solution on felt cloth. After the electrode was polished to a mirror-like finish, it was sonicated in deionized water for 10 minutes.


### 2.2. Electrodeposition

An EG&G PAR Potentiostat/Galvanostat Model 273A was used for all depositions, cyclic voltammetry, and corrosion studies. Pulsed electrodeposition of the film was carried out using a potential of −1.1 V for 10 seconds then steped to −0.58 V for 3 seconds until a total charge of 70 C.


### 2.3. Solution Studies

The solutions prepared for measurement of kinematic viscosity, zeta potential, particle size, and conductivity consisted of the exfoliated MMT solutions and the nickel-citrate plating solution. The zeta potential of the various plating solutions were measured using a Delsa Nano-C (Beckman-Coulter Instruments). The size of the particles in the solution was determined by photon correlation spectroscopy using the Delsa Nano-C. The samples were allowed to equilibrate at 25°C for 60 seconds using a peltier device in the instrument. The samples were measured for zeta potential three times to show reproducibility of the measurement. Kinematic viscosity (cSt) was measured with a Cannon Ubbelohde viscometer size 50. The viscometer with 20 mL of sample was placed into a Brinkmann RM6 water bath at 25°C and allowed to equilibrate for 20 minutes. The flow time was measured in seconds and multiplied by the kinematic viscosity constant (cSt/s). Each sample was measured five times to show reproducibility of the kinematic viscosity measurement. The conductivity was measured with a Thermo Orion 550 A conductivity meter.


### 2.4. Characterization Techniques

The surface morphology of the films was characterized with an Environmental FEI Quanta 200 scanning electron microscope (SEM). X-ray diffraction data was obtained on a Siemens D-500 Diffractometer using CuKα radiation (λ = 0.1541 nm) at 35 kV and 24 mA. The scans were run from 2–100° 2θ at a step size of 0.05 degrees and dwell time of 1 second.


### 2.5. Corrosion Measurements

Corrosion behavior was studied by electrochemical techniques. A four-electrode electrochemical cell was used as a corrosion testing system composed of the working electrode of the nanocomposite film, two graphite rods, and a saturated calomel electrode (SCE). Tafel plots were acquired in a 3.5% sodium chloride solution. A ±100 mV potential range was applied to the cell without stirring the solution; the resulting current density was then measured. In each scan, the run started at open circuit potentialEocp with a scan rate of 1 mV/s. Both cathodic and anodic scans were recorded starting from OCP. The nickel-layered silicate films were also immersed in a 3.5% sodium chloride solution for extended periods (30 days) while monitoring OCP.


## 2.1. Materials

Nickel-layered silicates were electrochemically deposited from acidic plating baths at pH 1.6, 2.5, and 3.0 at 25°C. The montmorillonite (MMT) (5 g/L) aqueous solution from Southern Clay Products was mechanically agitated using a magnetic stirrer over 24 hours to obtain exfoliated layered silicate platelets. Citric acid anhydrous and/or sodium citrate dihydrate was utilized as a ligand to stabilize nickel (II) ions. The composition of nickel-citrate plating baths at different pHs was prepared from NiSO4 · 6H2O (Alfa Aesar) and Na3C6H5O7 · 6H2O (Fisher Scientific) or H3C6H5O7 (Fisher Scientific) as shown in Table 1.Table 1
Values of the acidic plating bath composition for nickel, citrate, and citric acid.
Chemical
pH 1.6
pH 2.5
pH 3.0
NiSO4·6H2O
77.8 g/L
77.8 g/L
77.8 g/L
Na3C6H5O7·6H2O
—
35.3 g/L
52.9 g/L
H3C6H5O7
57.6 g/L
34.6 g/L
23.0 g/LThe exfoliated MMT solution was added to the nickel and citrate salts and then stirred with a magnetic stirrer until dissolved. The pH of the plating solution was measured with a Corning pH meter and Pasco Scientific pH electrode. The electrochemical cell was comprised of three electrodes: chromel wire (counter electrode), saturated calomel (reference electrode), and stainless steel discs (working electrode). Stainless steel discs with a diameter of 1 cm2 were polished mechanically with 600, 800, and 1000 grit silicon carbide paper and then with 3 and 1 μm diamond solution on felt cloth. After the electrode was polished to a mirror-like finish, it was sonicated in deionized water for 10 minutes.


## 2.2. Electrodeposition

An EG&G PAR Potentiostat/Galvanostat Model 273A was used for all depositions, cyclic voltammetry, and corrosion studies. Pulsed electrodeposition of the film was carried out using a potential of −1.1 V for 10 seconds then steped to −0.58 V for 3 seconds until a total charge of 70 C.


## 2.3. Solution Studies

The solutions prepared for measurement of kinematic viscosity, zeta potential, particle size, and conductivity consisted of the exfoliated MMT solutions and the nickel-citrate plating solution. The zeta potential of the various plating solutions were measured using a Delsa Nano-C (Beckman-Coulter Instruments). The size of the particles in the solution was determined by photon correlation spectroscopy using the Delsa Nano-C. The samples were allowed to equilibrate at 25°C for 60 seconds using a peltier device in the instrument. The samples were measured for zeta potential three times to show reproducibility of the measurement. Kinematic viscosity (cSt) was measured with a Cannon Ubbelohde viscometer size 50. The viscometer with 20 mL of sample was placed into a Brinkmann RM6 water bath at 25°C and allowed to equilibrate for 20 minutes. The flow time was measured in seconds and multiplied by the kinematic viscosity constant (cSt/s). Each sample was measured five times to show reproducibility of the kinematic viscosity measurement. The conductivity was measured with a Thermo Orion 550 A conductivity meter.


## 2.4. Characterization Techniques

The surface morphology of the films was characterized with an Environmental FEI Quanta 200 scanning electron microscope (SEM). X-ray diffraction data was obtained on a Siemens D-500 Diffractometer using CuKα radiation (λ = 0.1541 nm) at 35 kV and 24 mA. The scans were run from 2–100° 2θ at a step size of 0.05 degrees and dwell time of 1 second.


## 2.5. Corrosion Measurements

Corrosion behavior was studied by electrochemical techniques. A four-electrode electrochemical cell was used as a corrosion testing system composed of the working electrode of the nanocomposite film, two graphite rods, and a saturated calomel electrode (SCE). Tafel plots were acquired in a 3.5% sodium chloride solution. A ±100 mV potential range was applied to the cell without stirring the solution; the resulting current density was then measured. In each scan, the run started at open circuit potentialEocp with a scan rate of 1 mV/s. Both cathodic and anodic scans were recorded starting from OCP. The nickel-layered silicate films were also immersed in a 3.5% sodium chloride solution for extended periods (30 days) while monitoring OCP.


## 3. Results and Discussion

### 3.1. Kinematic Viscosity

The layered silicate was stirred over 24 hours resulting in exfoliated montmorillonite (MMT) platelets. A certain amount of anionic exfoliated MMT was able to suspend in the aqueous solution forming an equilibrium of the individual particle repulsions. If the MMT concentration is too high, agglomeration and precipitation occur, resulting in an increase of viscosity. The optimum amount of MMT is chosen from viscosity based on the kinematic viscosity curve (Figure1). The exfoliated MMT are non-spherical particles; thus, the rotary Brownian motion may lead to non-Newtonian effect even in the diluted solution. The addition of more MMT particles changes the magnitude of the kinematic viscosity because of its platelet shape and charged surface, which results in a deviation of Newtonian behavior [22]. According to Figure 1(b), the viscosity of the MMT solution gradually increases until 0.5% MMT. Then the viscosity starts to dramatically increase when MMT is higher than 1% as seen from the steep increase of the slope. The viscosity increase is linear at very low concentration ranges. The kinematic viscosity values for the concentrations of 0.5% MMT was 1.33 cSt at 25°C. The MMT concentration of 0.5% is selected to be used in the nickel plating solution because the viscosity stays stable at about this concentration. When introducing an exfoliated MMT into the nickel solution, it becomes a thickened fluid because the opposite charge of nickel ion is electrostatically adsorbed onto the clay surface (negative-charged) leading to agglomeration of the particles. Once citrate ions are added into the nickel-MMT solution, the viscosity decreases because citrate ligands help stabilize nickel ions in the solution. However, the viscosity of Ni-citrate in MMT solution is still higher than that of only Ni-citrate solution because free nickel cations are able to be adsorbed onto the MMT surface.Figure 1
Kinematic viscosity of montmorillonite (MMT) solutions.


### 3.2. Zeta Potential and Particle Size

As shown previously, typically the surface forces can be the key factor for incorporation of particles into a metal matrix during electrodeposition [23]. The zeta potential of layered silicate nanoparticles were measured at three different pHs (1.6, 2.5, and 3.0). In order to investigate the influence of the bath composition and pH, the zeta potential of each condition was analyzed for particle stability (Table 2). The zeta potential of the charged particles helps predict colloidal stability and electrostatic interaction of the particles. The zeta potential represents the repulsive forces between particles. Because most aqueous colloidal systems are stabilized by electrostatic repulsion, the larger repulsive forces between particles result in the particles being stabilized in solution, which reduces the possibility for the particles to aggregate. The exfoliated MMT is known to have a negative charge on its surface [24]. The exfoliated MMT (0.5%) solution has a zeta potential of −43.2 mV. It is stable and able to suspend in the aqueous solution while the nonexfoliated MMT precipitates. Based on the results from the zeta-potential analysis of the nickel-citrate-MMT plating solution, pH 2.5 (−22.2 mV) and pH 3.0 (−21.9 mV) solutions are more stable than pH 1.6 (−10.1 mV) solution (Table 2). The adsorption of the nickel and citrate at the MMT surface shifted the zeta potential toward positive values dropping the electrostatic stabilization of the dispersion. However, the particles at pH 2.5, and pH 3.0 are much more stable than that at pH 1.6. This was also confirmed by allowing the solution to sit stagnant for 24 hours in which time the pH 1.6 solution precipitated out, whereas the pH 2.5 and 3.0 stayed stable in solution for 3-4 more days.Table 2
Plating solution measurements of conductivity, viscosity, zeta potential, and particle size for various pHs (1.6, 2.5, 3.0) of the plating bath.
Plating solution pH
Conductivity(n=3) (mS/cm)
Viscosity (n=3) (cSt)
Particle size (nm)
Zeta potential (n=3)  (mV)
pH 1.6
24.3 ± 0.1
2.86 ± 0.03
3120
−10.1 ± 0.3
pH 2.5
28.1 ± 0.2
2.64 ± 0.01
2756
−22.2 ± 0.9
pH 3.0
33.7 ± 0.3
2.21 ± 0.01
2517
−21.9 ± 0.4
0.5% MMT
0.502 ± 0.008
1.33 ± 0.01
591
−43.2 ± 0.8In addition, the particle’s size decreased as pH increased with changing citrate concentration (Table2). The particle size of 0.5% MMT in water is 591 nm. When the MMT concentration is introduced to the nickel plating bath, the particle size becomes larger than the native MMT particles. A slight change was observed from 3120 to 2517 nm as the pH increased, which follows the decrease in viscosity as pH increases (Table 2). At pH 1.6, mostly free Ni2+ ions are present to adsorb to the surface of the MMT, whereas at the higher pH values of 2.5 and 3.0 a nickel-citrate complex (NiHCit) is formed removing some of the free Ni2+ ions that could bind to MMT [25]. This follows the result where the particle size and viscosity decrease as the pH is increased from 1.6 to 3.0.


### 3.3. Cyclic Voltammetry

Cyclic voltammetry (CV) was run for the nickel-layer silicate plating solutions at pHs of 1.6, 2.5, and 3.0 and shown in Figure2. The pH influences the electrodeposition of Ni-MMT. The reduction peak for Ni-MMT at pH 3.0 is shifted to a more negative potential (−0.6 V). Also the working window of the electrodeposition was expanded at pH 3.0, pushing the hydrogen evolution further cathodic and resulting in smoother films (Figure 2) [26]. The nickel-citrate species varied with respect to pH values [26]. For a nickel-citrate bath at pH less than 4, the predominant species is NiCitH with trace amount of NiH2Cit+ (less than 2%). At pH lower than 2, most of the nickel exists as free nickel ions; as the pH increases from 2 to 3, the nickel-citrate species are mostly represented as NiCitH and NiH2Cit+, with less free nickel ions [26–28]. MMT improves adhesion and provides for a smoother film because the nonelectroactive platelets slow down the reduction reaction and push hydrogen evolution more cathodic (as seen in cyclic voltammetry). Also the nickel films without MMT at these pHs tended to have poor adhesion. The pH 3 nanocomposite film was the optimal coating giving the best results of overall properties for adhesion, corrosion protection and mechanical properties.Figure 2
Cyclic voltammograms of nickel-layered silicate (0.5% MMT) plating solution for various pHs (1.6, 2.5, 3.0).


### 3.4. Film Characterization

The pH also affects nickel crystalline growth as shown by SEM (Figure3) and XRD (Figure 4). At very low pH there is more hydrogen formation and the plating rate is faster resulting in a non-uniform film and larger grain size. At pH of 2.5 and 3.0 the rate of electrodeposition is slower and hydrogen evolution decreases resulting in smoother uniform films and longer deposition time for the same accumulated charges. Pulse electrodeposition is applied for depositing the nickel-MMT films at low pH (1.6–3.0). Through experiments, it was determined that the electrodeposition of nickel at pH values greater than 3.5 tended to have poor adhesion that required other pretreatment of the stainless steel substrate or a different plating bath for adhesion of the coating. By pulsing, there is an increase in the replenishment of nickel cations in the diffusion layer and diffusion of hydrogen away from the electrode surface [7, 29]. Also, the pulse deposition method provided a uniform, smooth film with good adhesion. A direct potential method was attempted but it was found that the films deposited in a non-uniform manner and had poor adhesion. SEM micrographs of the deposits show microstructures with grain sizes in the micrometer range. However, it is clear from Figure 3 that at pH 3.0 there is a progressive change in the crystal orientation from an almost random texture to a stronger (200) texture. This may be due to the stronger nickel-citrate chelate NiHCit formation at pH 3.0, which stabilizes the nickel in solution and allows for slower dissolution at the electrode surface. This truncation of the pyramidal grains (observed for pH 1.6 and 2.5) occurs for pH 3.0 (Figure 3) which would support the enhanced (200) texture of the pH 3.0 deposits.Figure 3
Scanning electron microscopy (SEM) images of Ni-MMT (0.5%) films electrodeposited from plating baths at pHs 1.6 ((a) and (a′)), 2.5 ((b) and (b′)), and 3.0 ((c) and (c′)).X-ray diffraction (XRD) patterns of Ni-MMT (0.5%) films electrodeposited at various pHs (a) 1.6, (b) 2.5 and (c) 3.0 (SS: substrate stainless steel peaks).
(a)
(b)
(c)The Ni-MMT films fabricated at pH 1.6 are crystalline and give a random XRD pattern that matches the PDF no. 00-004-0850 for nickel (Figure4). When pH of the plating bath is increased to 2.5 and 3.0, Ni-MMT films start to show an orientation preference for (200) growth. An electrostatic stabilization of dispersion of the nickel-citrate-MMT particles benefits insertion of MMT into the nickel electrodeposited films. The nanoindentation results also support that the hardness is highest for coatings deposited at pH 3.0 (234 GPa) over that of coatings deposited at pH 1.6 and 2.5 (Table 3).Table 3
Nanoindentation hardness and young modulus of the Ni-MMT (0.5%) nanocomposite films electrodeposited at various pHs (1.6, 2.5, 3.0).
Ni-MMT coatings pHs
Young modulus(GPa ± SD, n=25)
Nanoindentation hardness(GPa ± SD, n=25)
pH 1.6
147 ± 50
4.1 ± 1.5
pH 2.5
174 ± 52
3.3 ± 1.2
pH 3.0
234 ± 57
5.3 ± 1.6


### 3.5. Corrosion Studies

The electrochemical corrosion parameters from the Tafel data (Figure5) are summarized in Table 4. Rp is the polarization resistance experimentally observed between the applied electrochemical current density and potential for the corroding electrode within a few millivolts of the polarization from the corrosion potential (Ecorr). The corrosion current density (icorr) is approximately calculated from a simplified rearranged Stern and Geary equation with respect to the two anodic and cathodic Tafel slopes. The corrosion rate is inversely proportional to the polarization resistance. However, the film fabricated from pH 3 exhibited a passive region (plateau region) with a higher anodic potential of the polarization (Figure 5). The corrosion parameters, (Rp, Ecorr, and  icorr), are all within the same range for pH 1.6, 2.5, and 3.0 (Table 4). The corrosion potential of the films decreases from −0.32, −0.34, and −0.39 V for different pHs of 1.6, 2.5, and 3.0, respectively, while the corrosion rate improves for the pH 3.0 coating. The immersion corrosion tests were conducted at ambient temperature to monitor OCP values for one month (Figure 6). The films deposited at pH 3 show the greatest improvement in corrosion protection taking 13 days to reach the OCP of the stainless steel. The coatings deposited at pH 1.6 began to corrode within a day based on the immersion OCP values matching stainless steel. The immersion test was run three times for each of the pHs and the average was taken to create Figure 6 with an overall standard deviation of ±0.02. Figure 7 shows the coatings at pH 1.6, 2.5, and 3.0 before and after 30 days of immersion in 3.5% NaCl. At pH 1.6, corrosion is visible for the coating (Figure 7(d)), whereas pH 2.5 just starts to show corrosion effects at the edges of the substrate (Figure 7(e)). The coating at pH 3.0 still shows no visible corrosion at 30 days and is the most stable of the coatings.Table 4
E
corr, icorr and polarization resistance (Rp) of the Ni-MMT (0.5%) nanocomposite film electrodeposited at various pHs (1.6, 2.5, 3.0) of the plating bath.
Ni-MMT coating deposited at
E
corr (V)± SD (n=3)
i
corr (A·cm−2)± SD (n=3)
Rp (Ω·cm2)± SD (n=3)
pH 1.6
−0.32 ± 0.02
9.02 ± 3 × 10−7
1.47 ± 0.5 × 105
pH 2.5
−0.34 ± 0.02
9.48 ± 3 × 10−7
1.84 ± 0.4 × 105
pH 3.0
−0.39 ± 0.02
7.34 ± 2 × 10−7
1.16 ± 0.2 × 105Figure 5
Tafel plot of Ni-MMT (0.5%) films measured in 3.5% NaCl solution at 25°C. Coatings were electrodeposited from a plating solution at various pHs (1.6, 2.5, and 3.0) onto stainless steel substrates.Figure 6
Open circuit potential (OCP) versus immersion time in 3.5% NaCl for nickel-layered silicate films electrodeposited from various pHs (1.6, 2.5, 3.0). Values are an average of three runs with a standard deviation of ±0.02.Sample images of Ni-MMT coatings electrodeposited from plating baths at various pHs of 1.6, 2.5, and 3.0 before immersion in 3.5% NaCl (a)–(c), and after (d)-(f), respectively.
(a)
(b)
(c)
(d)
(e)
(f)


## 3.1. Kinematic Viscosity

The layered silicate was stirred over 24 hours resulting in exfoliated montmorillonite (MMT) platelets. A certain amount of anionic exfoliated MMT was able to suspend in the aqueous solution forming an equilibrium of the individual particle repulsions. If the MMT concentration is too high, agglomeration and precipitation occur, resulting in an increase of viscosity. The optimum amount of MMT is chosen from viscosity based on the kinematic viscosity curve (Figure1). The exfoliated MMT are non-spherical particles; thus, the rotary Brownian motion may lead to non-Newtonian effect even in the diluted solution. The addition of more MMT particles changes the magnitude of the kinematic viscosity because of its platelet shape and charged surface, which results in a deviation of Newtonian behavior [22]. According to Figure 1(b), the viscosity of the MMT solution gradually increases until 0.5% MMT. Then the viscosity starts to dramatically increase when MMT is higher than 1% as seen from the steep increase of the slope. The viscosity increase is linear at very low concentration ranges. The kinematic viscosity values for the concentrations of 0.5% MMT was 1.33 cSt at 25°C. The MMT concentration of 0.5% is selected to be used in the nickel plating solution because the viscosity stays stable at about this concentration. When introducing an exfoliated MMT into the nickel solution, it becomes a thickened fluid because the opposite charge of nickel ion is electrostatically adsorbed onto the clay surface (negative-charged) leading to agglomeration of the particles. Once citrate ions are added into the nickel-MMT solution, the viscosity decreases because citrate ligands help stabilize nickel ions in the solution. However, the viscosity of Ni-citrate in MMT solution is still higher than that of only Ni-citrate solution because free nickel cations are able to be adsorbed onto the MMT surface.Figure 1
Kinematic viscosity of montmorillonite (MMT) solutions.


## 3.2. Zeta Potential and Particle Size

As shown previously, typically the surface forces can be the key factor for incorporation of particles into a metal matrix during electrodeposition [23]. The zeta potential of layered silicate nanoparticles were measured at three different pHs (1.6, 2.5, and 3.0). In order to investigate the influence of the bath composition and pH, the zeta potential of each condition was analyzed for particle stability (Table 2). The zeta potential of the charged particles helps predict colloidal stability and electrostatic interaction of the particles. The zeta potential represents the repulsive forces between particles. Because most aqueous colloidal systems are stabilized by electrostatic repulsion, the larger repulsive forces between particles result in the particles being stabilized in solution, which reduces the possibility for the particles to aggregate. The exfoliated MMT is known to have a negative charge on its surface [24]. The exfoliated MMT (0.5%) solution has a zeta potential of −43.2 mV. It is stable and able to suspend in the aqueous solution while the nonexfoliated MMT precipitates. Based on the results from the zeta-potential analysis of the nickel-citrate-MMT plating solution, pH 2.5 (−22.2 mV) and pH 3.0 (−21.9 mV) solutions are more stable than pH 1.6 (−10.1 mV) solution (Table 2). The adsorption of the nickel and citrate at the MMT surface shifted the zeta potential toward positive values dropping the electrostatic stabilization of the dispersion. However, the particles at pH 2.5, and pH 3.0 are much more stable than that at pH 1.6. This was also confirmed by allowing the solution to sit stagnant for 24 hours in which time the pH 1.6 solution precipitated out, whereas the pH 2.5 and 3.0 stayed stable in solution for 3-4 more days.Table 2
Plating solution measurements of conductivity, viscosity, zeta potential, and particle size for various pHs (1.6, 2.5, 3.0) of the plating bath.
Plating solution pH
Conductivity(n=3) (mS/cm)
Viscosity (n=3) (cSt)
Particle size (nm)
Zeta potential (n=3)  (mV)
pH 1.6
24.3 ± 0.1
2.86 ± 0.03
3120
−10.1 ± 0.3
pH 2.5
28.1 ± 0.2
2.64 ± 0.01
2756
−22.2 ± 0.9
pH 3.0
33.7 ± 0.3
2.21 ± 0.01
2517
−21.9 ± 0.4
0.5% MMT
0.502 ± 0.008
1.33 ± 0.01
591
−43.2 ± 0.8In addition, the particle’s size decreased as pH increased with changing citrate concentration (Table2). The particle size of 0.5% MMT in water is 591 nm. When the MMT concentration is introduced to the nickel plating bath, the particle size becomes larger than the native MMT particles. A slight change was observed from 3120 to 2517 nm as the pH increased, which follows the decrease in viscosity as pH increases (Table 2). At pH 1.6, mostly free Ni2+ ions are present to adsorb to the surface of the MMT, whereas at the higher pH values of 2.5 and 3.0 a nickel-citrate complex (NiHCit) is formed removing some of the free Ni2+ ions that could bind to MMT [25]. This follows the result where the particle size and viscosity decrease as the pH is increased from 1.6 to 3.0.


## 3.3. Cyclic Voltammetry

Cyclic voltammetry (CV) was run for the nickel-layer silicate plating solutions at pHs of 1.6, 2.5, and 3.0 and shown in Figure2. The pH influences the electrodeposition of Ni-MMT. The reduction peak for Ni-MMT at pH 3.0 is shifted to a more negative potential (−0.6 V). Also the working window of the electrodeposition was expanded at pH 3.0, pushing the hydrogen evolution further cathodic and resulting in smoother films (Figure 2) [26]. The nickel-citrate species varied with respect to pH values [26]. For a nickel-citrate bath at pH less than 4, the predominant species is NiCitH with trace amount of NiH2Cit+ (less than 2%). At pH lower than 2, most of the nickel exists as free nickel ions; as the pH increases from 2 to 3, the nickel-citrate species are mostly represented as NiCitH and NiH2Cit+, with less free nickel ions [26–28]. MMT improves adhesion and provides for a smoother film because the nonelectroactive platelets slow down the reduction reaction and push hydrogen evolution more cathodic (as seen in cyclic voltammetry). Also the nickel films without MMT at these pHs tended to have poor adhesion. The pH 3 nanocomposite film was the optimal coating giving the best results of overall properties for adhesion, corrosion protection and mechanical properties.Figure 2
Cyclic voltammograms of nickel-layered silicate (0.5% MMT) plating solution for various pHs (1.6, 2.5, 3.0).


## 3.4. Film Characterization

The pH also affects nickel crystalline growth as shown by SEM (Figure3) and XRD (Figure 4). At very low pH there is more hydrogen formation and the plating rate is faster resulting in a non-uniform film and larger grain size. At pH of 2.5 and 3.0 the rate of electrodeposition is slower and hydrogen evolution decreases resulting in smoother uniform films and longer deposition time for the same accumulated charges. Pulse electrodeposition is applied for depositing the nickel-MMT films at low pH (1.6–3.0). Through experiments, it was determined that the electrodeposition of nickel at pH values greater than 3.5 tended to have poor adhesion that required other pretreatment of the stainless steel substrate or a different plating bath for adhesion of the coating. By pulsing, there is an increase in the replenishment of nickel cations in the diffusion layer and diffusion of hydrogen away from the electrode surface [7, 29]. Also, the pulse deposition method provided a uniform, smooth film with good adhesion. A direct potential method was attempted but it was found that the films deposited in a non-uniform manner and had poor adhesion. SEM micrographs of the deposits show microstructures with grain sizes in the micrometer range. However, it is clear from Figure 3 that at pH 3.0 there is a progressive change in the crystal orientation from an almost random texture to a stronger (200) texture. This may be due to the stronger nickel-citrate chelate NiHCit formation at pH 3.0, which stabilizes the nickel in solution and allows for slower dissolution at the electrode surface. This truncation of the pyramidal grains (observed for pH 1.6 and 2.5) occurs for pH 3.0 (Figure 3) which would support the enhanced (200) texture of the pH 3.0 deposits.Figure 3
Scanning electron microscopy (SEM) images of Ni-MMT (0.5%) films electrodeposited from plating baths at pHs 1.6 ((a) and (a′)), 2.5 ((b) and (b′)), and 3.0 ((c) and (c′)).X-ray diffraction (XRD) patterns of Ni-MMT (0.5%) films electrodeposited at various pHs (a) 1.6, (b) 2.5 and (c) 3.0 (SS: substrate stainless steel peaks).
(a)
(b)
(c)The Ni-MMT films fabricated at pH 1.6 are crystalline and give a random XRD pattern that matches the PDF no. 00-004-0850 for nickel (Figure4). When pH of the plating bath is increased to 2.5 and 3.0, Ni-MMT films start to show an orientation preference for (200) growth. An electrostatic stabilization of dispersion of the nickel-citrate-MMT particles benefits insertion of MMT into the nickel electrodeposited films. The nanoindentation results also support that the hardness is highest for coatings deposited at pH 3.0 (234 GPa) over that of coatings deposited at pH 1.6 and 2.5 (Table 3).Table 3
Nanoindentation hardness and young modulus of the Ni-MMT (0.5%) nanocomposite films electrodeposited at various pHs (1.6, 2.5, 3.0).
Ni-MMT coatings pHs
Young modulus(GPa ± SD, n=25)
Nanoindentation hardness(GPa ± SD, n=25)
pH 1.6
147 ± 50
4.1 ± 1.5
pH 2.5
174 ± 52
3.3 ± 1.2
pH 3.0
234 ± 57
5.3 ± 1.6


## 3.5. Corrosion Studies

The electrochemical corrosion parameters from the Tafel data (Figure5) are summarized in Table 4. Rp is the polarization resistance experimentally observed between the applied electrochemical current density and potential for the corroding electrode within a few millivolts of the polarization from the corrosion potential (Ecorr). The corrosion current density (icorr) is approximately calculated from a simplified rearranged Stern and Geary equation with respect to the two anodic and cathodic Tafel slopes. The corrosion rate is inversely proportional to the polarization resistance. However, the film fabricated from pH 3 exhibited a passive region (plateau region) with a higher anodic potential of the polarization (Figure 5). The corrosion parameters, (Rp, Ecorr, and  icorr), are all within the same range for pH 1.6, 2.5, and 3.0 (Table 4). The corrosion potential of the films decreases from −0.32, −0.34, and −0.39 V for different pHs of 1.6, 2.5, and 3.0, respectively, while the corrosion rate improves for the pH 3.0 coating. The immersion corrosion tests were conducted at ambient temperature to monitor OCP values for one month (Figure 6). The films deposited at pH 3 show the greatest improvement in corrosion protection taking 13 days to reach the OCP of the stainless steel. The coatings deposited at pH 1.6 began to corrode within a day based on the immersion OCP values matching stainless steel. The immersion test was run three times for each of the pHs and the average was taken to create Figure 6 with an overall standard deviation of ±0.02. Figure 7 shows the coatings at pH 1.6, 2.5, and 3.0 before and after 30 days of immersion in 3.5% NaCl. At pH 1.6, corrosion is visible for the coating (Figure 7(d)), whereas pH 2.5 just starts to show corrosion effects at the edges of the substrate (Figure 7(e)). The coating at pH 3.0 still shows no visible corrosion at 30 days and is the most stable of the coatings.Table 4
E
corr, icorr and polarization resistance (Rp) of the Ni-MMT (0.5%) nanocomposite film electrodeposited at various pHs (1.6, 2.5, 3.0) of the plating bath.
Ni-MMT coating deposited at
E
corr (V)± SD (n=3)
i
corr (A·cm−2)± SD (n=3)
Rp (Ω·cm2)± SD (n=3)
pH 1.6
−0.32 ± 0.02
9.02 ± 3 × 10−7
1.47 ± 0.5 × 105
pH 2.5
−0.34 ± 0.02
9.48 ± 3 × 10−7
1.84 ± 0.4 × 105
pH 3.0
−0.39 ± 0.02
7.34 ± 2 × 10−7
1.16 ± 0.2 × 105Figure 5
Tafel plot of Ni-MMT (0.5%) films measured in 3.5% NaCl solution at 25°C. Coatings were electrodeposited from a plating solution at various pHs (1.6, 2.5, and 3.0) onto stainless steel substrates.Figure 6
Open circuit potential (OCP) versus immersion time in 3.5% NaCl for nickel-layered silicate films electrodeposited from various pHs (1.6, 2.5, 3.0). Values are an average of three runs with a standard deviation of ±0.02.Sample images of Ni-MMT coatings electrodeposited from plating baths at various pHs of 1.6, 2.5, and 3.0 before immersion in 3.5% NaCl (a)–(c), and after (d)-(f), respectively.
(a)
(b)
(c)
(d)
(e)
(f)


## 4. Conclusion

The optimal bath composition was developed to improve film adhesion to stainless steel, corrosion protection, and mechanical properties. To obtain the stable layered silicate particles for the codeposition with nickel, the viscosity, conductivity, zetapotential, and particle size were analyzed. The particles at pH 2.5 (−22.2 mV) and pH 3.0 (−21.9 mV) were more stable than that at pH 1.6 (−10.1 mV). Corrosion was investigated by Tafel polarization and open circuit potential measurement versus time. XRD determined that the (111)/(200) ratio changed with deposition pH. The SEM and hardness results also supported that the nickel-MMT nanocomposites at pH 2.5 (174 GPa) and 3.0 (234 GPa) were better than at pH 1.6 (147 GPa). From all the combined data, the pH 3.0 coating with incorporated MMT gave the best adherence, hardness, and corrosion protection for the nanocomposite coatings.



---