# Electrodeposition, Characterization, and Corrosion Stability of Nanostructured Anodic Oxides on New Ti-15Zr-5Nb Alloy Surface

Authors: Jose M. Calderon Moreno; Cora Vasilescu; Silviu Iulian Drob; Monica Popa; Paula Drob; Ecaterina Vasilescu
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

A new Ti-15Zr-5Nb alloy with suitable microstructure and mechanical properties was processed by galvanostatic anodization in 0.3 M H3PO4 solution and a continuous nanostructured layer of protective TiO2 oxide was electrodeposited. The obtained anatase oxide layer has a nanotubes-like porosity (SEM observations) and contains significant amount of phosphorus in phosphotitanate compound embedded in the oxide lattice (Raman, FT-IR, SEM, and EDX analysis). This layer composition can stimulate the formation of the bone and its porosity can offer a good scaffold for bone cell adhesion. The electrochemical behaviour, corrosion stability, and variations of the open circuit potentials, Eoc, and corresponding open circuit potential gradients, ΔEoc, for 1500 soaking hours in Ringer solutions of 3.21, 7.58, and 8.91 pH values were studied. The anodized layer was more resistant, stable (from EIS spectra), and was formed from an inner barrier insulating layer that assures the very good alloy corrosion resistance and an outer porous layer that provides the good conditions for cell development. The nanostructured alloy has higher corrosion stability, namely, a more reduced quantity of ions released and a lower toxicity than that of the bare one. The monitoring of Eoc and ΔEoc showed the enhancement and stabilizing of the long-term passive state of the anodized alloy and, respectively, no possibility at galvanic corrosion.


---

## Body

## 1. Introduction

Titanium and its alloys are used as orthopaedic and dental implants due to their good mechanical and anticorrosive properties and biocompatibility. However, it is an increasing necessity to obtain new alloys with a low elastic modulus, close to that of the human bone (10–40 GPa) [1], and based only on nontoxic, nonallergic, biocompatible elements as Zr, Nb, and Ta [2, 3]. Titanium alloys containing these biocompatible metals are relatively bioinert and the implant-bone integration is a longer process than that of the bone healing.The alloy bioactivity depends on its surface chemistry, topography, porosity, and roughness; a rough surface enhances the contact with the bone and improves the bioactive bone-binding activity. Thus, surface treatments that form thin or thick, uniform, resistant, porous, rough layers on the implant surface and also incorporate constituent elements of the human bone (calcium and phosphorus) or protective compounds (phosphates, hydroxyapatite) are applied in the last time [4–7]. Electrochemical anodic or cathodic deposition of the oxide layers is an important, cheap, efficient method to increase the protective and osseointegrative properties of the titanium alloys; oxide nanotubes are formed on the alloy surface being a good matrix for bone cell colonization [8].Electrochemical potentiostatic anodization technique was performed on Ti and its alloys in different solutions, and controlling the polarization parameters, the bioactive TiO2 nanotubes were obtained enhancing the alloy biocompatibility [9–14].Electrochemical galvanostatic anodization method was accomplished on Ti and some of its binary, ternary, and quaternary alloy surfaces using especially acidic solutions; varying solution composition, pH, temperature, and anodizing parameters, biofunctionalized surfaces were realized [15–17].To obtain a biocompatible surface is a complex problem because must be an alloy containing only nontoxic, nonallergic, biocompatible elements, having very good mechanical properties and then must be taken into consideration the most favorable method adapted for the improvement of its bioactivity.In this paper, a new Ti-15Zr-5Nb alloy was elaborated to satisfy the most important requirements of an implant material; this alloy (containing only nontoxic and nonallergic elements) has anα+β microstructure, type Widmanstatten, a low Young’s modulus (82.69 GPa), and a good correlation between its mechanical properties and corrosion resistance. Its biocompatibility and anticorrosive properties were enhanced by galvanostatic anodization in 0.3 M H3PO4 (orthophosphoric acid) solution assuring the formation of a continuous nanostructured layer of protective TiO2 oxide; this layer incorporated phosphorus as phosphotitanate (P2O52-) ions, increasing the alloy bioactivity.


## 2. Experimental Details

### 2.1. Materials

The new Ti-15Zr-5Nb alloy was obtained by vacuum, cold-crucible, semilevitation melting; alloy composition is (%wt.) 0.011% H2; 0.02% N2; 0.12% O2; 0.052% Mg; 0.00235% Ca; 0.00831% Cr; 0.02048% Fe; 0.0077% Ni; 0.0181% Ta; 14.97% Zr; 5.111% Nb; balance Ti. From as-cast ingots were cut cylindrical samples for experiments.


### 2.2. Electrodeposition of the Nanostructured Oxide Layer

Before the anodic galvanostatic processing, the samples were ground with metallographic paper till 2000 grade to eliminate any surface defects and then were ground with metallographic paper of 600 grades to assure the necessary roughness and were washed with bidistilled water. Then, the samples were ultrasonically degreased in acetone and bidistilled water (for 15 min), dried in air, and fixed in a Stern-Makrides mount system. The anodic galvanostatic polarization was applied by a DC power source (MATRIX, China) that supplied current densities of 5 mA/cm2 and 10 mA/cm2 between the working electrode (Ti-15Zr-5Nb alloy) and auxiliary electrode (Pt); these current densities were constantly maintained for different time periods of 15, 30, 45, and 60 min. The anodization solution was orthophosphoric acid (H3PO4) of 0.3 M and 1 M concentrations; three processing parameters were varied: the solution concentration, current density, and time; different oxide layers were obtained and the nanostructured surface with the most favorable structural and morphological properties was selected and its electrochemical behaviour, corrosion stability, and long-term behaviour in different simulated physiological solutions were studied.


### 2.3. Characterization of the Nanostructured Oxide Layer

Composition of the obtained layers was verified by Raman microscopy and Fourier transform infrared (FT-IR) analysis.Raman spectra were measured at room temperature using a LABRam Jobin Yvon (Japan) equipment. Acquisition time was 40 s; the green line (λ = 514.5 nm) of Ar+ laser was used to excite Raman spectra at a power of ~20 mW. Measurements were carried out under a microscope, with a 90x microscope objective; the laser spot size was around 1-2 μm. Raman measurements covered the range between 100 and 1100 cm−1.FT-IR spectra were registered as a resolution of 4 cm−1, over the frequency range from 1400 to 600 cm−1, using a spectrophotometer model Nicolet 6700 FTIR (USA). The spectra were taken from thin transparent (~20 mg/cm2) KBr pellets containing approximately 0.5% wt samples. Pellets were prepared by compacting and vacuum pressing of an intimate mixture obtained by grinding 1 mg of substance in 200 mg KBr.The morphology, microstructure, and elemental composition of the nanostructured electrodeposited layer were analyzed by scanning electron microscopy (SEM) using a Quanta 3D FEG apparatus (The Nederland) working at an accelerating voltage of 20 kV and equipped with an energy dispersive X-ray (EDX) spectrometer.


### 2.4. Electrochemical Behaviour of Bare and Anodized Ti-15Zr-5Nb Alloys

The electrochemical behaviour of the anodized Ti-15Zr-5Nb alloy was examined in comparison with the bare alloy in Ringer solution of different pH values (acid pH = 3.21, obtained by HCl addition; neutral pH = 7.58, normal; alkaline pH = 8.91, obtained by KOH addition) that simulate the severe functional conditions from the human body: in the case of surgery, the pH decreases till 3-4 value [18, 19] and must long time to come back to 7.4 value; in the case of inflammations or infections, the pH can increase till 9 value [20]. Ringer solution composition was (g/L) NaCl—6.8; KCl—0.4; CaCl2—0.2; MgSO4·7H2O—0.2048; NaH2PO4·H2O—0.1438; NaHCO3—1.1; glucose—1. The working temperature was 37° ± 1°C.The electrochemical behaviour was studied by cyclic potentiodynamic polarization method and electrochemical impedance spectroscopy (EIS).The cyclic potentiodynamic measurements were applied beginning from −0.5 V till +2 V (versus saturated calomel electrode, SCE) at a scan rate of 1 mV/s. Voltalab 80 equipment (Radiometer, France) with its VoltaMaster 4 program was used. From voltammograms, the main electrochemical parameters that characterize the bare and anodized Ti-15Zr-5Nb alloy behaviour were determined:Ecorr—corrosion potential (like zero current potential); Ep—passivation potential (the potential value at which the current becomes constant); |Ecorr-Ep|—tendency to passivation (low values show a rapid, easy passivation); ΔEp—passive potential range (potential range for constant current, plateau range; larger potential range proves a more resistant material); ip—passive current density (lower values indicate a more protective passive layer).EIS measurements were carried out at open circuit potential-Eoc with the same VoltaLab 80 equipment; Nyquist and Bode spectra were recorded applying sine wave of 5 mHz in the frequency range from 100 mHz to 100 kHz, with 7 points per decade. The electric equivalent circuit was fitted using nonlinear least square ZVIEW program.


### 2.5. Corrosion Stability of Bare and Anodized Ti-15Zr-5Nb Alloys

Linear polarization measurements were performed for ±50 mV around the open circuit potential at a scan rate of 1 mV/s, using the same Voltalab 80 equipment. From Tafel representation, the VoltaMaster 4 program directly supplied the values of the corrosion current density—icorr, corrosion rate—Vcorr, and polarization resistance—Rp; the total quantity (ng/cm2) of ions released in biofluid was calculated [21, 22] as
(1)Ionrelease=1.016·Vcorr·105,
where Vcorr = corrosion rate in mm/year.


### 2.6. Long-Term Behaviour of Bare and Anodized Ti-15Zr-5Nb Alloys

The long-term behaviour of bare and anodized alloys was monitored by the measurements of the open circuit potentials—Eoc (with a performing Hewlett-Packard multimeter) at regular time periods, till 1500 soaking hours in Ringer solutions. The shift of Eoc to more positive values shows the increase of the thickness of oxide passive film and lower corrosion rate [23]. The decrease of Eoc value suggests dissolution processes at the interface and its subsequent increase, the formation of new oxide layer [23]. Also, taking into consideration that the human biofluid pH can vary from acid to alkaline values, different pH values can appear along the implant surface; thus, Eoc will have various values on different zones of the implant, producing potential gradients—ΔEoc—that can initiate galvanic cells and can accelerate the implant corrosion; simulating these conditions, the following gradients were calculated [24–26]:(2)ΔEoc1(pH)=EocpH=3.21-EocpH=7.58,ΔEoc2(pH)=EocpH=3.21-EocpH=8.91,ΔEoc3(pH)=EocpH=7.58-EocpH=8.91.Also, the time variations of ΔEoc values were registered with the aim of evaluating the possible susceptibility to galvanic or local corrosion.


## 2.1. Materials

The new Ti-15Zr-5Nb alloy was obtained by vacuum, cold-crucible, semilevitation melting; alloy composition is (%wt.) 0.011% H2; 0.02% N2; 0.12% O2; 0.052% Mg; 0.00235% Ca; 0.00831% Cr; 0.02048% Fe; 0.0077% Ni; 0.0181% Ta; 14.97% Zr; 5.111% Nb; balance Ti. From as-cast ingots were cut cylindrical samples for experiments.


## 2.2. Electrodeposition of the Nanostructured Oxide Layer

Before the anodic galvanostatic processing, the samples were ground with metallographic paper till 2000 grade to eliminate any surface defects and then were ground with metallographic paper of 600 grades to assure the necessary roughness and were washed with bidistilled water. Then, the samples were ultrasonically degreased in acetone and bidistilled water (for 15 min), dried in air, and fixed in a Stern-Makrides mount system. The anodic galvanostatic polarization was applied by a DC power source (MATRIX, China) that supplied current densities of 5 mA/cm2 and 10 mA/cm2 between the working electrode (Ti-15Zr-5Nb alloy) and auxiliary electrode (Pt); these current densities were constantly maintained for different time periods of 15, 30, 45, and 60 min. The anodization solution was orthophosphoric acid (H3PO4) of 0.3 M and 1 M concentrations; three processing parameters were varied: the solution concentration, current density, and time; different oxide layers were obtained and the nanostructured surface with the most favorable structural and morphological properties was selected and its electrochemical behaviour, corrosion stability, and long-term behaviour in different simulated physiological solutions were studied.


## 2.3. Characterization of the Nanostructured Oxide Layer

Composition of the obtained layers was verified by Raman microscopy and Fourier transform infrared (FT-IR) analysis.Raman spectra were measured at room temperature using a LABRam Jobin Yvon (Japan) equipment. Acquisition time was 40 s; the green line (λ = 514.5 nm) of Ar+ laser was used to excite Raman spectra at a power of ~20 mW. Measurements were carried out under a microscope, with a 90x microscope objective; the laser spot size was around 1-2 μm. Raman measurements covered the range between 100 and 1100 cm−1.FT-IR spectra were registered as a resolution of 4 cm−1, over the frequency range from 1400 to 600 cm−1, using a spectrophotometer model Nicolet 6700 FTIR (USA). The spectra were taken from thin transparent (~20 mg/cm2) KBr pellets containing approximately 0.5% wt samples. Pellets were prepared by compacting and vacuum pressing of an intimate mixture obtained by grinding 1 mg of substance in 200 mg KBr.The morphology, microstructure, and elemental composition of the nanostructured electrodeposited layer were analyzed by scanning electron microscopy (SEM) using a Quanta 3D FEG apparatus (The Nederland) working at an accelerating voltage of 20 kV and equipped with an energy dispersive X-ray (EDX) spectrometer.


## 2.4. Electrochemical Behaviour of Bare and Anodized Ti-15Zr-5Nb Alloys

The electrochemical behaviour of the anodized Ti-15Zr-5Nb alloy was examined in comparison with the bare alloy in Ringer solution of different pH values (acid pH = 3.21, obtained by HCl addition; neutral pH = 7.58, normal; alkaline pH = 8.91, obtained by KOH addition) that simulate the severe functional conditions from the human body: in the case of surgery, the pH decreases till 3-4 value [18, 19] and must long time to come back to 7.4 value; in the case of inflammations or infections, the pH can increase till 9 value [20]. Ringer solution composition was (g/L) NaCl—6.8; KCl—0.4; CaCl2—0.2; MgSO4·7H2O—0.2048; NaH2PO4·H2O—0.1438; NaHCO3—1.1; glucose—1. The working temperature was 37° ± 1°C.The electrochemical behaviour was studied by cyclic potentiodynamic polarization method and electrochemical impedance spectroscopy (EIS).The cyclic potentiodynamic measurements were applied beginning from −0.5 V till +2 V (versus saturated calomel electrode, SCE) at a scan rate of 1 mV/s. Voltalab 80 equipment (Radiometer, France) with its VoltaMaster 4 program was used. From voltammograms, the main electrochemical parameters that characterize the bare and anodized Ti-15Zr-5Nb alloy behaviour were determined:Ecorr—corrosion potential (like zero current potential); Ep—passivation potential (the potential value at which the current becomes constant); |Ecorr-Ep|—tendency to passivation (low values show a rapid, easy passivation); ΔEp—passive potential range (potential range for constant current, plateau range; larger potential range proves a more resistant material); ip—passive current density (lower values indicate a more protective passive layer).EIS measurements were carried out at open circuit potential-Eoc with the same VoltaLab 80 equipment; Nyquist and Bode spectra were recorded applying sine wave of 5 mHz in the frequency range from 100 mHz to 100 kHz, with 7 points per decade. The electric equivalent circuit was fitted using nonlinear least square ZVIEW program.


## 2.5. Corrosion Stability of Bare and Anodized Ti-15Zr-5Nb Alloys

Linear polarization measurements were performed for ±50 mV around the open circuit potential at a scan rate of 1 mV/s, using the same Voltalab 80 equipment. From Tafel representation, the VoltaMaster 4 program directly supplied the values of the corrosion current density—icorr, corrosion rate—Vcorr, and polarization resistance—Rp; the total quantity (ng/cm2) of ions released in biofluid was calculated [21, 22] as
(1)Ionrelease=1.016·Vcorr·105,
where Vcorr = corrosion rate in mm/year.


## 2.6. Long-Term Behaviour of Bare and Anodized Ti-15Zr-5Nb Alloys

The long-term behaviour of bare and anodized alloys was monitored by the measurements of the open circuit potentials—Eoc (with a performing Hewlett-Packard multimeter) at regular time periods, till 1500 soaking hours in Ringer solutions. The shift of Eoc to more positive values shows the increase of the thickness of oxide passive film and lower corrosion rate [23]. The decrease of Eoc value suggests dissolution processes at the interface and its subsequent increase, the formation of new oxide layer [23]. Also, taking into consideration that the human biofluid pH can vary from acid to alkaline values, different pH values can appear along the implant surface; thus, Eoc will have various values on different zones of the implant, producing potential gradients—ΔEoc—that can initiate galvanic cells and can accelerate the implant corrosion; simulating these conditions, the following gradients were calculated [24–26]:(2)ΔEoc1(pH)=EocpH=3.21-EocpH=7.58,ΔEoc2(pH)=EocpH=3.21-EocpH=8.91,ΔEoc3(pH)=EocpH=7.58-EocpH=8.91.Also, the time variations of ΔEoc values were registered with the aim of evaluating the possible susceptibility to galvanic or local corrosion.


## 3. Results and Discussion

### 3.1. Characterization of the Alloy Nanostructured Surface

Composition of the electrodeposited layer was determined from Raman spectra and FT-IR analysis. The morphology, microstructure, and elemental composition of the surface layer were analyzed by SEM and EDX methods.


#### 3.1.1. Characterization of the Alloy Surface Galvanostatically Anodized in 0.3 M H3PO4 for 45 min. at a Current Density of 10 mA/cm2

SEM observations of the alloy surface after galvanostatic anodization (Figure1) revealed the formation of a layer showing two hierarchical features: hill-like protuberances with a typical width between 5 and 10 μm (Figure 1(a)), where the layer is locally thicker, and nanotube-like porosity with diameters in the one to a few hundred manometers (Figure 1(b)). The chemical analysis by EDX determined that the nanostructured layer contains significant amount of P and O, as well as the constituent alloy elements (Figure 2).SEM micrographs of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2: (a) hill-like protuberances; (b) nanotube-like porosity.
(a)
(b)Figure 2
EDX spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.Raman microspectroscopy is especially suitable for the analysis of the presence of oxides [27, 28] and/or phosphates, [29–31] even if present as nanocrystalline or secondary phases in surface layers, difficult to detect by other methods. Raman measurements (Figure 3) clearly showed the existence of titanium oxide with anatase-like structure, indicated by the existence of a strong band at 149 cm−1, coincident with the main Eg vibrational band of anatase. The significant shift from reported values at ~142–145 cm−1 [27, 28] of different anatase nanoparticles with dimensions between 12 and 30 nm and the width of the main band clearly indicate smaller dimensions of the anatase nanocrystallites nucleated in the anodized surface layer. Besides, the additional spectral features reveal a substantial modification of the crystalline structure of anatase during anodization in H3PO4: the wide bands centered at ~400 cm−1 and at ~600 cm−1 cannot be unambiguously matched with the secondary features of anatase at 395 cm−1 (B1g) and 638 cm−1 (Eg) [27, 28], while the (A1g) band at 515 cm−1 is not present and the Eg band at 195 cm−1 is masked by the wide main band. Different authors have reported similar wide Raman bands in titania modified layers containing phosphorus, either as phosphate (PO43-) or as pyrophosphate (P2O74-) groups, embedded in the O–Ti(Nb)–O oxidized surface layer [32, 33] and caused by modification of Ti–O–Ti bonds into P–O–Ti and P–O–P bonds in the oxide lattice. Raman analysis of the anodized surface, on the other hand, found no evidence of the presence of the PO43- group characteristic main vibrational band at ~1000 cm−1 [29–31].Figure 3
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.Because the sensitivity of Raman method for Ti–O bonding is significantly higher than that for phosphate bonds, we used FT-IR vibrational spectroscopy to investigate the presence of phosphate groups, in order to complete the compositional analysis of the electrodeposited films. The two wide bands, centered at ~800 cm−1 and 1100 cm−1, detected by FT-IR (Figure 4) can only be attributed to the ν3 bending mode of the P–O–P bonds in phosphotitanate glass oxide, due to the incorporation of P5+ ions [33, 34] into the oxide coating, promoted by the acidic conditions.Figure 4
FT-IR spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.We can conclude that the layer electrodeposited in 0.3 M H3PO4 solution is formed by anatase oxide that contains phosphorus as P2O74- ion in phosphotitanate compound, phosphorus being the main inorganic component of the human bone thus stimulating the formation of bone [35]. Also, this nanolayer has a nanotube-like porosity that can provide a good scaffold for the bone cell development [35].


#### 3.1.2. Characterization of the Alloy Surface Galvanostatically Anodized in 1 M H3PO4 for 45 min. at a Current Density of 10 mA/cm2

The analysis of the galvanostatic anodization Ti-15Zr-5Nb alloy surface by vibrational Raman (Figure5) and FT-IR (Figure 6) spectroscopies detected the same composition of the electrodeposited layer, namely, TiO2 anatase oxide, modified with phosphorus as pyrophosphate bonds in titania-based oxide.Figure 5
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.Figure 6
FT-IR spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.SEM micrographs (Figure7) of the sample processed electrochemically in 1 M H3PO4 showed the deposition of loose aggregates (Figure 7(b)) of submicron sized particles on top of the porous layer (Figure 7(a)). The additional features have the same composition of the continuous passivating layer, as determined from the EDX analysis (Figure 8). It results in the fact that in 1 M H3PO4 solution was obtained a nanolayer with lower microstructural properties.SEM micrographs of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.
(a)
(b)Figure 8
EDX spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min.From the previous experimental results, it appears that the most favorable properties of Ti-15Zr-5Nb alloy surface were obtained by the galvanostatic anodization in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2. The electrochemical behaviour, corrosion stability, and long-term behaviour of the alloy surface processed by this method will be studied later on (named anodized alloy).


### 3.2. Electrochemical Behaviour of the Bare and Anodized Alloys in Ringer Solutions of Different pH Values

Electrochemical behaviour of the bare and anodized alloys in Ringer solutions of 3.21, 7.58, and 8.91 pH values was determined from cyclic potentiodynamic and EIS measurements.


#### 3.2.1. Electrochemical Behaviour from Cyclic Potentiodynamic Measurements

Cyclic potentiodynamic curves from Figure9 make evident a nobler behaviour of the anodized alloy than that of the bare one, because all the electrochemical parameters (Table 1) have more favorable values [10, 15]:(i)
corrosion,Ecorr and passivation, Ep potentials have more electropositive values and passive current densities, ip are lower, showing a more protective, more resistant nanostructured layer on the anodized alloy surface [23],(ii)
tendency to passivation,|Ecorr-Ep|, has lower values indicating that the processed alloy is more easily, more rapidly passivated, as a result of the existence of the electrodeposited nanolayer that improves the protective properties of the native passive layer by its thickening [23, 25].Table 1
Main electrochemical parameters for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
E
corr (mV)
E
p (mV)
Δ
E
p (mV)
|
E
corr
-
E
p
| (mV)
i
p (μA/cm2)
Ringer pH = 3.21
Bare
-
350
-
200
>2000
150
3.9
Anodized
-
250
-
150
>2000
100
1.9
Ringer pH = 7.58
Bare
-
200
0
>2000
200
1.0
Anodized
-
100
0
>2000
100
0.9
Ringer pH = 8.91
Bare
-
350
-
200
>2000
150
4.1
Anodized
-
200
-
100
>2000
100
2.0Figure 9
Cyclic potentiodynamic curves for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.In acid and alkaline Ringer solutions, the main electrochemical parameters presented slightly more unfavorable values both for the bare and the anodized alloys due to the slight higher aggressivity of these solutions; nevertheless, the anodized alloy revealed a very good passive behaviour.


#### 3.2.2. Electrochemical Behaviour from EIS Measurements

Nyquist spectra (Zreal versus Zimag) exhibited semicircles with large curvature radii (Figure10) that describe a capacitive behaviour, a resistant passive film [15, 36, 37]. Because the curvature radii have higher values for the anodized alloy, it results in the fact that its passive film is more resistant. The impedance values for the electrochemical anodized alloy exceed two times the values for the bare alloy; these results indicate a very protective nanostructured layer [15, 36, 37].Figure 10
Nyquist spectra for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.Bode spectra (phase angle versus logf) displayed both for bare and anodized alloys (Figure 11) phase angles around the value of −90° that represent a capacitive behaviour, a passive film like an electric insulator [16]. Same better behaviour of the anodized alloy than that of the bare one resulted:(i)
in Ringer solution of pH = 3.21; the bare alloy presents two phase angles at −81° and −79°, and the anodized one higher values at −83° and −81° that denote a better capacitive behaviour for the nanostructured alloy;(ii)
in Ringer solution of pH = 7.58; the phase angles have values of −84° and −80° for the bare alloy and of −86° and −82° for the anodized alloy, namely, a more insulating passive film existing on the nanostructured alloy surface;(iii)
in Ringer solution of pH = 8.91; values of −79° and −76° were registered for the bare alloy and of −81° and −78° for the anodized alloy.Figure 11
Bode spectra for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.Those two phase angles indicate a protective film formed by two layers: an inner barrier insulating layer characterized by the higher phase angle in the low frequency range and an outer porous layer represented by the lower phase angle in the intermediate frequency range; through this porous layer can penetrate the aggressive ions from the physiological solutions and can corrode the inner compact layer, but, in the same time, in these pores can be incorporated calcium and phosphorous ions from biofluid that can provide a good scaffold for the bone cell adhesion [38].According to the literature [39, 40], an electric equivalent circuit with two time constants (Figure 12) was modeled: the first time constant illustrates the inner barrier layer by its resistance, Rb, and capacitance, CPEb; the second time constant refers to the outer porous layer by its resistance, Rp, and capacitance, CPEp.Figure 12
Electric equivalent circuit with two time constants.The inner barrier layer resistances,Rb, and the porous layer resistances, Rp, of the anodized alloy are higher than those of the bare one (Table 2), showing that the galvanostatic processing generated a more resistant nanolayer; this fact is confirmed by the values of the frequency independent parameters n1 and n2 which are bigger for the processed alloy, indicating a better capacitor (n=1 represents an ideal capacitor), namely, superior protective properties [39]. Barrier layer resistances, Rb, for both bare and anodized alloys have values of about 100 times higher than those of the porous layer, Rp, proving that the barrier layer assures the alloy good resistance against the physiological solution aggressivity [41, 42]; on the other hand, lower values of Rp denote that the porous layer has inferior protective properties, permitting the diffusion and incorporation of the ions from the biofluid through and into this layer [36, 43]; thus, this porous layer provides the necessary conditions for the interactions of the alloy with human fluid, namely, the bioactivity of the surface layer [43].Table 2
Fitting parameters of the two time constants electric equivalent circuit.
Ti-15Zr-5Nb
R
sol (Ω·cm2)
R
b (Ω·cm2)
CP
E
b (S·sn·cm-2)
n
1
R
p (Ω·cm2)
CP
E
p (S·sn·cm-2)
n
2
Ringer pH = 3.21
Bare
14.2
7.3
×
10
6
2.2
×
10
-
6
0.96
1.2
×
10
4
2.5
×
10
-
5
0.90
Anodized
14.8
8.7
×
10
6
1.8
×
10
-
6
0.98
1.5
×
10
4
2.6
×
10
-
5
0.91
Ringer pH = 7.58
Bare
13.6
8.1
×
10
6
2.0
×
10
-
6
0.97
1.8
×
10
4
2.1
×
10
-
5
0.91
Anodized
15.1
9.9
×
10
6
1.6
×
10
-
6
0.99
1.9
×
10
4
2.3
×
10
-
5
0.93
Ringer pH = 8.91
Bare
14.5
6.2
×
10
6
2.3
×
10
-
6
0.95
1.6
×
10
4
2.6
×
10
-
5
0.90
Anodized
14.9
8.3
×
10
6
1.9
×
10
-
6
0.97
1.7
×
10
4
2.7
×
10
-
5
0.92


### 3.3. Corrosion Stability of the Bare and Anodized Alloys in Ringer Solutions of Different pH Values

The corrosion stability of the bare and anodized alloys was appreciated from the values of the corrosion current densities,icorr, corrosion, Vcorr, and ion release rates and polarization resistances, Rp (Table 3), obtained from Tafel representations. The main corrosion parameters have better values for the anodized alloy than those for the bare one:(i)
corrosion current densities,icorr, corrosion, Vcorr, and ion release rates have lower values that show a better resistance to corrosion and implicitly a more reduced quantity of ions released in biofluid, namely, a lower toxicity [21, 22];(ii)
polarization resistance,Rp, has higher values (of about 10 times, order MΩ·cm2) that prove a more resistant layer [23, 25].Table 3
Main corrosion parameters for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
i
corr (μA/cm2)
V
corr (μm/Y)
Resistance class
Ion release (ng/cm2)
R
p (kΩ·cm2)
Ringer pH = 3.21
Bare
0.081
0.751
PS
76.3
330
Anodized
0.029
0.269
PS
27.33
1295
Ringer pH = 7.58
Bare
0.039
0.358
PS
36.4
397
Anodized
0.0054
0.050
PS
5.08
3020
Ringer pH = 8.91
Bare
0.071
0.657
PS
66.75
305
Anodized
0.019
0.175
PS
17.78
1380
PS: perfect stable.Though, in acid and alkaline Ringer solutions, both the bare and the anodized alloys have a little higher corrosion rates, their values are placed in the “Perfect Stable” resistance class, indicating a very good anticorrosive resistance. The best corrosion resistance for the processed alloy resulted in neutral Ringer solution, normal conditions from the human body.


### 3.4. Long-Term Behaviour of the Bare and Anodized Alloys in Ringer Solutions of Different pH Values

The long-term behaviour of the bare and anodized alloys was determined from the monitoring of the open circuit potentials,Eoc, and corresponding open circuit potential gradients, ΔEoc, for 1500 soaking hours in Ringer solutions of acid (3.21), neutral (7.58), and alkaline (8.91) pH values (Figure 13).Figure 13
Monitoring of the open circuit potentials for bare and anodized Ti-15Zr-5Nb alloy in Ringer solutions at 37°C.The open circuit potentials for the anodized alloy shifted to more positive values in time, showing the increase of its protective nanolayer thickness [23]. Eoc had more electropositive values for the anodized alloy than those for the bare one, which reveal more protective nanolayers [15, 16, 23]. Also, these potentials reached almost constant values after about 700 h, demonstrating more resistant, stable state [23].The open circuit potential gradients, ΔEoc, have very low values (Table 4) that cannot generate galvanic corrosion. Many authors [44, 45] showed that only differences of 600–700 mV can initiate and maintain galvanic cells; therefore, both the bare and the anodized alloys cannot corrode by galvanic corrosion, even in the case of large differences in the biofluid pH values between 3.21 and 8.91 (ΔEoc2) that could appear on the alloy surface in its long-term “working life” as implant.Table 4
Potential gradients for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
Time (h)
Δ
E
oc1 (mV)
Δ
E
oc2 (mV)
Δ
E
oc3 (mV)
Bare
24
-
98
+10
+108
500
-
80
+10
+81
1000
-
72
+8
+80
1500
-
70
+10
+80
Anodized
24
-
89
+20
+20
500
-
75
+10
+41
1000
-
70
+10
+80
1500
-
70
+10
+80


## 3.1. Characterization of the Alloy Nanostructured Surface

Composition of the electrodeposited layer was determined from Raman spectra and FT-IR analysis. The morphology, microstructure, and elemental composition of the surface layer were analyzed by SEM and EDX methods.


### 3.1.1. Characterization of the Alloy Surface Galvanostatically Anodized in 0.3 M H3PO4 for 45 min. at a Current Density of 10 mA/cm2

SEM observations of the alloy surface after galvanostatic anodization (Figure1) revealed the formation of a layer showing two hierarchical features: hill-like protuberances with a typical width between 5 and 10 μm (Figure 1(a)), where the layer is locally thicker, and nanotube-like porosity with diameters in the one to a few hundred manometers (Figure 1(b)). The chemical analysis by EDX determined that the nanostructured layer contains significant amount of P and O, as well as the constituent alloy elements (Figure 2).SEM micrographs of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2: (a) hill-like protuberances; (b) nanotube-like porosity.
(a)
(b)Figure 2
EDX spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.Raman microspectroscopy is especially suitable for the analysis of the presence of oxides [27, 28] and/or phosphates, [29–31] even if present as nanocrystalline or secondary phases in surface layers, difficult to detect by other methods. Raman measurements (Figure 3) clearly showed the existence of titanium oxide with anatase-like structure, indicated by the existence of a strong band at 149 cm−1, coincident with the main Eg vibrational band of anatase. The significant shift from reported values at ~142–145 cm−1 [27, 28] of different anatase nanoparticles with dimensions between 12 and 30 nm and the width of the main band clearly indicate smaller dimensions of the anatase nanocrystallites nucleated in the anodized surface layer. Besides, the additional spectral features reveal a substantial modification of the crystalline structure of anatase during anodization in H3PO4: the wide bands centered at ~400 cm−1 and at ~600 cm−1 cannot be unambiguously matched with the secondary features of anatase at 395 cm−1 (B1g) and 638 cm−1 (Eg) [27, 28], while the (A1g) band at 515 cm−1 is not present and the Eg band at 195 cm−1 is masked by the wide main band. Different authors have reported similar wide Raman bands in titania modified layers containing phosphorus, either as phosphate (PO43-) or as pyrophosphate (P2O74-) groups, embedded in the O–Ti(Nb)–O oxidized surface layer [32, 33] and caused by modification of Ti–O–Ti bonds into P–O–Ti and P–O–P bonds in the oxide lattice. Raman analysis of the anodized surface, on the other hand, found no evidence of the presence of the PO43- group characteristic main vibrational band at ~1000 cm−1 [29–31].Figure 3
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.Because the sensitivity of Raman method for Ti–O bonding is significantly higher than that for phosphate bonds, we used FT-IR vibrational spectroscopy to investigate the presence of phosphate groups, in order to complete the compositional analysis of the electrodeposited films. The two wide bands, centered at ~800 cm−1 and 1100 cm−1, detected by FT-IR (Figure 4) can only be attributed to the ν3 bending mode of the P–O–P bonds in phosphotitanate glass oxide, due to the incorporation of P5+ ions [33, 34] into the oxide coating, promoted by the acidic conditions.Figure 4
FT-IR spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.We can conclude that the layer electrodeposited in 0.3 M H3PO4 solution is formed by anatase oxide that contains phosphorus as P2O74- ion in phosphotitanate compound, phosphorus being the main inorganic component of the human bone thus stimulating the formation of bone [35]. Also, this nanolayer has a nanotube-like porosity that can provide a good scaffold for the bone cell development [35].


### 3.1.2. Characterization of the Alloy Surface Galvanostatically Anodized in 1 M H3PO4 for 45 min. at a Current Density of 10 mA/cm2

The analysis of the galvanostatic anodization Ti-15Zr-5Nb alloy surface by vibrational Raman (Figure5) and FT-IR (Figure 6) spectroscopies detected the same composition of the electrodeposited layer, namely, TiO2 anatase oxide, modified with phosphorus as pyrophosphate bonds in titania-based oxide.Figure 5
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.Figure 6
FT-IR spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.SEM micrographs (Figure7) of the sample processed electrochemically in 1 M H3PO4 showed the deposition of loose aggregates (Figure 7(b)) of submicron sized particles on top of the porous layer (Figure 7(a)). The additional features have the same composition of the continuous passivating layer, as determined from the EDX analysis (Figure 8). It results in the fact that in 1 M H3PO4 solution was obtained a nanolayer with lower microstructural properties.SEM micrographs of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.
(a)
(b)Figure 8
EDX spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min.From the previous experimental results, it appears that the most favorable properties of Ti-15Zr-5Nb alloy surface were obtained by the galvanostatic anodization in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2. The electrochemical behaviour, corrosion stability, and long-term behaviour of the alloy surface processed by this method will be studied later on (named anodized alloy).


## 3.1.1. Characterization of the Alloy Surface Galvanostatically Anodized in 0.3 M H3PO4 for 45 min. at a Current Density of 10 mA/cm2

SEM observations of the alloy surface after galvanostatic anodization (Figure1) revealed the formation of a layer showing two hierarchical features: hill-like protuberances with a typical width between 5 and 10 μm (Figure 1(a)), where the layer is locally thicker, and nanotube-like porosity with diameters in the one to a few hundred manometers (Figure 1(b)). The chemical analysis by EDX determined that the nanostructured layer contains significant amount of P and O, as well as the constituent alloy elements (Figure 2).SEM micrographs of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2: (a) hill-like protuberances; (b) nanotube-like porosity.
(a)
(b)Figure 2
EDX spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.Raman microspectroscopy is especially suitable for the analysis of the presence of oxides [27, 28] and/or phosphates, [29–31] even if present as nanocrystalline or secondary phases in surface layers, difficult to detect by other methods. Raman measurements (Figure 3) clearly showed the existence of titanium oxide with anatase-like structure, indicated by the existence of a strong band at 149 cm−1, coincident with the main Eg vibrational band of anatase. The significant shift from reported values at ~142–145 cm−1 [27, 28] of different anatase nanoparticles with dimensions between 12 and 30 nm and the width of the main band clearly indicate smaller dimensions of the anatase nanocrystallites nucleated in the anodized surface layer. Besides, the additional spectral features reveal a substantial modification of the crystalline structure of anatase during anodization in H3PO4: the wide bands centered at ~400 cm−1 and at ~600 cm−1 cannot be unambiguously matched with the secondary features of anatase at 395 cm−1 (B1g) and 638 cm−1 (Eg) [27, 28], while the (A1g) band at 515 cm−1 is not present and the Eg band at 195 cm−1 is masked by the wide main band. Different authors have reported similar wide Raman bands in titania modified layers containing phosphorus, either as phosphate (PO43-) or as pyrophosphate (P2O74-) groups, embedded in the O–Ti(Nb)–O oxidized surface layer [32, 33] and caused by modification of Ti–O–Ti bonds into P–O–Ti and P–O–P bonds in the oxide lattice. Raman analysis of the anodized surface, on the other hand, found no evidence of the presence of the PO43- group characteristic main vibrational band at ~1000 cm−1 [29–31].Figure 3
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.Because the sensitivity of Raman method for Ti–O bonding is significantly higher than that for phosphate bonds, we used FT-IR vibrational spectroscopy to investigate the presence of phosphate groups, in order to complete the compositional analysis of the electrodeposited films. The two wide bands, centered at ~800 cm−1 and 1100 cm−1, detected by FT-IR (Figure 4) can only be attributed to the ν3 bending mode of the P–O–P bonds in phosphotitanate glass oxide, due to the incorporation of P5+ ions [33, 34] into the oxide coating, promoted by the acidic conditions.Figure 4
FT-IR spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2.We can conclude that the layer electrodeposited in 0.3 M H3PO4 solution is formed by anatase oxide that contains phosphorus as P2O74- ion in phosphotitanate compound, phosphorus being the main inorganic component of the human bone thus stimulating the formation of bone [35]. Also, this nanolayer has a nanotube-like porosity that can provide a good scaffold for the bone cell development [35].


## 3.1.2. Characterization of the Alloy Surface Galvanostatically Anodized in 1 M H3PO4 for 45 min. at a Current Density of 10 mA/cm2

The analysis of the galvanostatic anodization Ti-15Zr-5Nb alloy surface by vibrational Raman (Figure5) and FT-IR (Figure 6) spectroscopies detected the same composition of the electrodeposited layer, namely, TiO2 anatase oxide, modified with phosphorus as pyrophosphate bonds in titania-based oxide.Figure 5
Raman spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.Figure 6
FT-IR spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.SEM micrographs (Figure7) of the sample processed electrochemically in 1 M H3PO4 showed the deposition of loose aggregates (Figure 7(b)) of submicron sized particles on top of the porous layer (Figure 7(a)). The additional features have the same composition of the continuous passivating layer, as determined from the EDX analysis (Figure 8). It results in the fact that in 1 M H3PO4 solution was obtained a nanolayer with lower microstructural properties.SEM micrographs of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min. at 10 mA/cm2.
(a)
(b)Figure 8
EDX spectrum of Ti-15Zr-5Nb alloy surface galvanostatically anodized in 1 M H3PO4 solution for 45 min.From the previous experimental results, it appears that the most favorable properties of Ti-15Zr-5Nb alloy surface were obtained by the galvanostatic anodization in 0.3 M H3PO4 solution for 45 min. at 10 mA/cm2. The electrochemical behaviour, corrosion stability, and long-term behaviour of the alloy surface processed by this method will be studied later on (named anodized alloy).


## 3.2. Electrochemical Behaviour of the Bare and Anodized Alloys in Ringer Solutions of Different pH Values

Electrochemical behaviour of the bare and anodized alloys in Ringer solutions of 3.21, 7.58, and 8.91 pH values was determined from cyclic potentiodynamic and EIS measurements.


### 3.2.1. Electrochemical Behaviour from Cyclic Potentiodynamic Measurements

Cyclic potentiodynamic curves from Figure9 make evident a nobler behaviour of the anodized alloy than that of the bare one, because all the electrochemical parameters (Table 1) have more favorable values [10, 15]:(i)
corrosion,Ecorr and passivation, Ep potentials have more electropositive values and passive current densities, ip are lower, showing a more protective, more resistant nanostructured layer on the anodized alloy surface [23],(ii)
tendency to passivation,|Ecorr-Ep|, has lower values indicating that the processed alloy is more easily, more rapidly passivated, as a result of the existence of the electrodeposited nanolayer that improves the protective properties of the native passive layer by its thickening [23, 25].Table 1
Main electrochemical parameters for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
E
corr (mV)
E
p (mV)
Δ
E
p (mV)
|
E
corr
-
E
p
| (mV)
i
p (μA/cm2)
Ringer pH = 3.21
Bare
-
350
-
200
>2000
150
3.9
Anodized
-
250
-
150
>2000
100
1.9
Ringer pH = 7.58
Bare
-
200
0
>2000
200
1.0
Anodized
-
100
0
>2000
100
0.9
Ringer pH = 8.91
Bare
-
350
-
200
>2000
150
4.1
Anodized
-
200
-
100
>2000
100
2.0Figure 9
Cyclic potentiodynamic curves for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.In acid and alkaline Ringer solutions, the main electrochemical parameters presented slightly more unfavorable values both for the bare and the anodized alloys due to the slight higher aggressivity of these solutions; nevertheless, the anodized alloy revealed a very good passive behaviour.


### 3.2.2. Electrochemical Behaviour from EIS Measurements

Nyquist spectra (Zreal versus Zimag) exhibited semicircles with large curvature radii (Figure10) that describe a capacitive behaviour, a resistant passive film [15, 36, 37]. Because the curvature radii have higher values for the anodized alloy, it results in the fact that its passive film is more resistant. The impedance values for the electrochemical anodized alloy exceed two times the values for the bare alloy; these results indicate a very protective nanostructured layer [15, 36, 37].Figure 10
Nyquist spectra for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.Bode spectra (phase angle versus logf) displayed both for bare and anodized alloys (Figure 11) phase angles around the value of −90° that represent a capacitive behaviour, a passive film like an electric insulator [16]. Same better behaviour of the anodized alloy than that of the bare one resulted:(i)
in Ringer solution of pH = 3.21; the bare alloy presents two phase angles at −81° and −79°, and the anodized one higher values at −83° and −81° that denote a better capacitive behaviour for the nanostructured alloy;(ii)
in Ringer solution of pH = 7.58; the phase angles have values of −84° and −80° for the bare alloy and of −86° and −82° for the anodized alloy, namely, a more insulating passive film existing on the nanostructured alloy surface;(iii)
in Ringer solution of pH = 8.91; values of −79° and −76° were registered for the bare alloy and of −81° and −78° for the anodized alloy.Figure 11
Bode spectra for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.Those two phase angles indicate a protective film formed by two layers: an inner barrier insulating layer characterized by the higher phase angle in the low frequency range and an outer porous layer represented by the lower phase angle in the intermediate frequency range; through this porous layer can penetrate the aggressive ions from the physiological solutions and can corrode the inner compact layer, but, in the same time, in these pores can be incorporated calcium and phosphorous ions from biofluid that can provide a good scaffold for the bone cell adhesion [38].According to the literature [39, 40], an electric equivalent circuit with two time constants (Figure 12) was modeled: the first time constant illustrates the inner barrier layer by its resistance, Rb, and capacitance, CPEb; the second time constant refers to the outer porous layer by its resistance, Rp, and capacitance, CPEp.Figure 12
Electric equivalent circuit with two time constants.The inner barrier layer resistances,Rb, and the porous layer resistances, Rp, of the anodized alloy are higher than those of the bare one (Table 2), showing that the galvanostatic processing generated a more resistant nanolayer; this fact is confirmed by the values of the frequency independent parameters n1 and n2 which are bigger for the processed alloy, indicating a better capacitor (n=1 represents an ideal capacitor), namely, superior protective properties [39]. Barrier layer resistances, Rb, for both bare and anodized alloys have values of about 100 times higher than those of the porous layer, Rp, proving that the barrier layer assures the alloy good resistance against the physiological solution aggressivity [41, 42]; on the other hand, lower values of Rp denote that the porous layer has inferior protective properties, permitting the diffusion and incorporation of the ions from the biofluid through and into this layer [36, 43]; thus, this porous layer provides the necessary conditions for the interactions of the alloy with human fluid, namely, the bioactivity of the surface layer [43].Table 2
Fitting parameters of the two time constants electric equivalent circuit.
Ti-15Zr-5Nb
R
sol (Ω·cm2)
R
b (Ω·cm2)
CP
E
b (S·sn·cm-2)
n
1
R
p (Ω·cm2)
CP
E
p (S·sn·cm-2)
n
2
Ringer pH = 3.21
Bare
14.2
7.3
×
10
6
2.2
×
10
-
6
0.96
1.2
×
10
4
2.5
×
10
-
5
0.90
Anodized
14.8
8.7
×
10
6
1.8
×
10
-
6
0.98
1.5
×
10
4
2.6
×
10
-
5
0.91
Ringer pH = 7.58
Bare
13.6
8.1
×
10
6
2.0
×
10
-
6
0.97
1.8
×
10
4
2.1
×
10
-
5
0.91
Anodized
15.1
9.9
×
10
6
1.6
×
10
-
6
0.99
1.9
×
10
4
2.3
×
10
-
5
0.93
Ringer pH = 8.91
Bare
14.5
6.2
×
10
6
2.3
×
10
-
6
0.95
1.6
×
10
4
2.6
×
10
-
5
0.90
Anodized
14.9
8.3
×
10
6
1.9
×
10
-
6
0.97
1.7
×
10
4
2.7
×
10
-
5
0.92


## 3.2.1. Electrochemical Behaviour from Cyclic Potentiodynamic Measurements

Cyclic potentiodynamic curves from Figure9 make evident a nobler behaviour of the anodized alloy than that of the bare one, because all the electrochemical parameters (Table 1) have more favorable values [10, 15]:(i)
corrosion,Ecorr and passivation, Ep potentials have more electropositive values and passive current densities, ip are lower, showing a more protective, more resistant nanostructured layer on the anodized alloy surface [23],(ii)
tendency to passivation,|Ecorr-Ep|, has lower values indicating that the processed alloy is more easily, more rapidly passivated, as a result of the existence of the electrodeposited nanolayer that improves the protective properties of the native passive layer by its thickening [23, 25].Table 1
Main electrochemical parameters for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
E
corr (mV)
E
p (mV)
Δ
E
p (mV)
|
E
corr
-
E
p
| (mV)
i
p (μA/cm2)
Ringer pH = 3.21
Bare
-
350
-
200
>2000
150
3.9
Anodized
-
250
-
150
>2000
100
1.9
Ringer pH = 7.58
Bare
-
200
0
>2000
200
1.0
Anodized
-
100
0
>2000
100
0.9
Ringer pH = 8.91
Bare
-
350
-
200
>2000
150
4.1
Anodized
-
200
-
100
>2000
100
2.0Figure 9
Cyclic potentiodynamic curves for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.In acid and alkaline Ringer solutions, the main electrochemical parameters presented slightly more unfavorable values both for the bare and the anodized alloys due to the slight higher aggressivity of these solutions; nevertheless, the anodized alloy revealed a very good passive behaviour.


## 3.2.2. Electrochemical Behaviour from EIS Measurements

Nyquist spectra (Zreal versus Zimag) exhibited semicircles with large curvature radii (Figure10) that describe a capacitive behaviour, a resistant passive film [15, 36, 37]. Because the curvature radii have higher values for the anodized alloy, it results in the fact that its passive film is more resistant. The impedance values for the electrochemical anodized alloy exceed two times the values for the bare alloy; these results indicate a very protective nanostructured layer [15, 36, 37].Figure 10
Nyquist spectra for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.Bode spectra (phase angle versus logf) displayed both for bare and anodized alloys (Figure 11) phase angles around the value of −90° that represent a capacitive behaviour, a passive film like an electric insulator [16]. Same better behaviour of the anodized alloy than that of the bare one resulted:(i)
in Ringer solution of pH = 3.21; the bare alloy presents two phase angles at −81° and −79°, and the anodized one higher values at −83° and −81° that denote a better capacitive behaviour for the nanostructured alloy;(ii)
in Ringer solution of pH = 7.58; the phase angles have values of −84° and −80° for the bare alloy and of −86° and −82° for the anodized alloy, namely, a more insulating passive film existing on the nanostructured alloy surface;(iii)
in Ringer solution of pH = 8.91; values of −79° and −76° were registered for the bare alloy and of −81° and −78° for the anodized alloy.Figure 11
Bode spectra for bare and anodized Ti-15Zr-5Nb alloys recorded in Ringer solutions at 37°C.Those two phase angles indicate a protective film formed by two layers: an inner barrier insulating layer characterized by the higher phase angle in the low frequency range and an outer porous layer represented by the lower phase angle in the intermediate frequency range; through this porous layer can penetrate the aggressive ions from the physiological solutions and can corrode the inner compact layer, but, in the same time, in these pores can be incorporated calcium and phosphorous ions from biofluid that can provide a good scaffold for the bone cell adhesion [38].According to the literature [39, 40], an electric equivalent circuit with two time constants (Figure 12) was modeled: the first time constant illustrates the inner barrier layer by its resistance, Rb, and capacitance, CPEb; the second time constant refers to the outer porous layer by its resistance, Rp, and capacitance, CPEp.Figure 12
Electric equivalent circuit with two time constants.The inner barrier layer resistances,Rb, and the porous layer resistances, Rp, of the anodized alloy are higher than those of the bare one (Table 2), showing that the galvanostatic processing generated a more resistant nanolayer; this fact is confirmed by the values of the frequency independent parameters n1 and n2 which are bigger for the processed alloy, indicating a better capacitor (n=1 represents an ideal capacitor), namely, superior protective properties [39]. Barrier layer resistances, Rb, for both bare and anodized alloys have values of about 100 times higher than those of the porous layer, Rp, proving that the barrier layer assures the alloy good resistance against the physiological solution aggressivity [41, 42]; on the other hand, lower values of Rp denote that the porous layer has inferior protective properties, permitting the diffusion and incorporation of the ions from the biofluid through and into this layer [36, 43]; thus, this porous layer provides the necessary conditions for the interactions of the alloy with human fluid, namely, the bioactivity of the surface layer [43].Table 2
Fitting parameters of the two time constants electric equivalent circuit.
Ti-15Zr-5Nb
R
sol (Ω·cm2)
R
b (Ω·cm2)
CP
E
b (S·sn·cm-2)
n
1
R
p (Ω·cm2)
CP
E
p (S·sn·cm-2)
n
2
Ringer pH = 3.21
Bare
14.2
7.3
×
10
6
2.2
×
10
-
6
0.96
1.2
×
10
4
2.5
×
10
-
5
0.90
Anodized
14.8
8.7
×
10
6
1.8
×
10
-
6
0.98
1.5
×
10
4
2.6
×
10
-
5
0.91
Ringer pH = 7.58
Bare
13.6
8.1
×
10
6
2.0
×
10
-
6
0.97
1.8
×
10
4
2.1
×
10
-
5
0.91
Anodized
15.1
9.9
×
10
6
1.6
×
10
-
6
0.99
1.9
×
10
4
2.3
×
10
-
5
0.93
Ringer pH = 8.91
Bare
14.5
6.2
×
10
6
2.3
×
10
-
6
0.95
1.6
×
10
4
2.6
×
10
-
5
0.90
Anodized
14.9
8.3
×
10
6
1.9
×
10
-
6
0.97
1.7
×
10
4
2.7
×
10
-
5
0.92


## 3.3. Corrosion Stability of the Bare and Anodized Alloys in Ringer Solutions of Different pH Values

The corrosion stability of the bare and anodized alloys was appreciated from the values of the corrosion current densities,icorr, corrosion, Vcorr, and ion release rates and polarization resistances, Rp (Table 3), obtained from Tafel representations. The main corrosion parameters have better values for the anodized alloy than those for the bare one:(i)
corrosion current densities,icorr, corrosion, Vcorr, and ion release rates have lower values that show a better resistance to corrosion and implicitly a more reduced quantity of ions released in biofluid, namely, a lower toxicity [21, 22];(ii)
polarization resistance,Rp, has higher values (of about 10 times, order MΩ·cm2) that prove a more resistant layer [23, 25].Table 3
Main corrosion parameters for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
i
corr (μA/cm2)
V
corr (μm/Y)
Resistance class
Ion release (ng/cm2)
R
p (kΩ·cm2)
Ringer pH = 3.21
Bare
0.081
0.751
PS
76.3
330
Anodized
0.029
0.269
PS
27.33
1295
Ringer pH = 7.58
Bare
0.039
0.358
PS
36.4
397
Anodized
0.0054
0.050
PS
5.08
3020
Ringer pH = 8.91
Bare
0.071
0.657
PS
66.75
305
Anodized
0.019
0.175
PS
17.78
1380
PS: perfect stable.Though, in acid and alkaline Ringer solutions, both the bare and the anodized alloys have a little higher corrosion rates, their values are placed in the “Perfect Stable” resistance class, indicating a very good anticorrosive resistance. The best corrosion resistance for the processed alloy resulted in neutral Ringer solution, normal conditions from the human body.


## 3.4. Long-Term Behaviour of the Bare and Anodized Alloys in Ringer Solutions of Different pH Values

The long-term behaviour of the bare and anodized alloys was determined from the monitoring of the open circuit potentials,Eoc, and corresponding open circuit potential gradients, ΔEoc, for 1500 soaking hours in Ringer solutions of acid (3.21), neutral (7.58), and alkaline (8.91) pH values (Figure 13).Figure 13
Monitoring of the open circuit potentials for bare and anodized Ti-15Zr-5Nb alloy in Ringer solutions at 37°C.The open circuit potentials for the anodized alloy shifted to more positive values in time, showing the increase of its protective nanolayer thickness [23]. Eoc had more electropositive values for the anodized alloy than those for the bare one, which reveal more protective nanolayers [15, 16, 23]. Also, these potentials reached almost constant values after about 700 h, demonstrating more resistant, stable state [23].The open circuit potential gradients, ΔEoc, have very low values (Table 4) that cannot generate galvanic corrosion. Many authors [44, 45] showed that only differences of 600–700 mV can initiate and maintain galvanic cells; therefore, both the bare and the anodized alloys cannot corrode by galvanic corrosion, even in the case of large differences in the biofluid pH values between 3.21 and 8.91 (ΔEoc2) that could appear on the alloy surface in its long-term “working life” as implant.Table 4
Potential gradients for bare and anodized Ti-15Zr-5Nb alloys obtained in Ringer solutions at 37°C.
Ti-15Zr-5Nb
Time (h)
Δ
E
oc1 (mV)
Δ
E
oc2 (mV)
Δ
E
oc3 (mV)
Bare
24
-
98
+10
+108
500
-
80
+10
+81
1000
-
72
+8
+80
1500
-
70
+10
+80
Anodized
24
-
89
+20
+20
500
-
75
+10
+41
1000
-
70
+10
+80
1500
-
70
+10
+80


## 4. Conclusions

The new Ti-15Zr-5Nb alloy surface was nanostructured by galvanostatic anodization in 0.3 M H3PO4 solution. The obtained layer has a nanotube-like porosity, revealed by SEM, and it is formed of anatase-like small crystallites, with added phosphorus as phosphotitanate, determined by Raman spectroscopy, FT-IR, and EDX analyses; this composition can stimulate the formation of the bone and the porosity can offer a good scaffold for the bone cell attachment. Cyclic potentiodynamic curves make evident a nobler behaviour of the anodized alloy than that of the bare one, as a result of the existence of the nanostructured layer that improves the protective properties of the native passive film by its thickening. EIS spectra revealed a better capacitive behaviour, a more insulating protective film electrodeposited on the alloy surface; the nanostructured film is formed by two layers: an inner barrier layer that assures the alloy very good anticorrosive resistance and an outer porous layer that can provide the good conditions for the bone cell adhesion. Corrosion and ion release rates have lower values showing a better resistance to corrosion and implicitly a more reduced quantity of ions released in biofluid, namely, a lower toxicity of the anodized alloy. The open circuit potentials for the nanostructured alloy shifted to more positive values in time, indicating the increase of its protective layer thickness. The open circuit potential gradients have very low values that cannot generate galvanic corrosion.



---

*Source: 858935-2013-04-11.xml*