# Investigations on Engineering Properties of Solidified/Stabilized Pb-Contaminated Soil Based on Alkaline Residue

Authors: Fusheng Zha; Dongdong Pan; Long Xu; Bo Kang; Chengbin Yang; Chengfu Chu
Journal: Advances in Civil Engineering
 (2018)

---

## Abstract

Solidification/stabilization (S/S) has been considered as one of the most effective techniques for remediation of the heavy metal-contaminated sites. Among various binders adopted in S/S, alkaline residue (AR) could be considered as a new binder to treat heavy metal-contaminated soil due to its strong adsorptive capacity for heavy metal ions. So in this paper, the strength, leaching, and microstructure characteristics of the solidified/stabilized Pb-contaminated soil by using alkaline residue are systematically investigated. Test results present that the unconfined compressive strength (UCS) of the treated soil will increase, while the leached Pb2+ concentration will decrease, with the increase of the alkaline residue content in the specimen. The UCS increases significantly with the curing time increasing during the initial 28 days, after which the UCS of the specimen becomes stable. The leached Pb2+ concentration decreases significantly at the initial 28 days followed by a stable trend with curing time increasing. The UCS decreases and the leached Pb2+ concentration increases with the increase of the initial Pb2+ concentration in the specimen. The microstructural analysis performed by scanning electron microscope (SEM) showed that the increase of the alkaline residue content and curing time will result in more hydration products and densified microstructure, which could effectively improve the engineering properties of the specimen.


---

## Body

## 1. Introduction

Widespread contamination of soil with heavy metal is one of the most severe environmental problems that can seriously deteriorate the environmental quality and human health. Remediation techniques are massively proposed for remediation of the heavy metal-contaminated site [1, 2], in which the stabilization/solidification (S/S) technique is intensively accepted for its efficiency, convenience, and cost-effectiveness. According to the remediation mechanism (including adsorption, encapsulation, precipitation, and complexation), selection of the binder for improvement of the strength and leaching characteristics is of great importance to the application of the stabilization/solidification technique [3–10].Alkaline residue, the by-product generated from the manufacturing alkaline industry, attracts attentions in the S/S technique recently. The extremely fine particles consisted in alkaline residue would result in high specific surface area and strong adsorptive capacity, which are beneficial for removal of heavy metal ions in the contaminated site. In addition, hydration products could be generated from the complicated interactions between the alkaline residue and soil, which will improve the leaching characteristics of the treated soils due to the adsorption and encapsulation mechanisms. Components like calcium oxide and aluminum oxide contained in AR can be the framework alongside with the hydration products generated from the hydration reaction, which will enhance the strength of the specimen. Based on the experimental investigations, Yan et al. [11] reported that the addition of alkaline residue in the contaminated soils could significantly reduce the leachability of Pb2+ to an acceptable level and the removal efficiency strongly depended on the pH value in the soils. The adsorption characteristics of the alkaline residue on heavy metal ions were also investigated by Cao et al. [12], in which the adsorption capacity of alkaline residue was confirmed to be susceptible to the pH, temperature, and the initial concentration of heavy metal ions in the soils. Jin et al. [13] confirmed the remarkable adsorption characteristics of the alkaline residue and the important roles of the temperature and pH value played during the adsorption process. Additionally, Sun et al. [14] investigated the engineering properties of the expansive soil treated by using alkaline residue. Test results indicated remarkable improvement of the basic properties (including the relative density, liquid/plastic limit, and expansive potential) and strength characteristic of the treated soil, which was supported by the Wang et al. [15].As mentioned above, alkaline residue is normally regarded as an effective binder because of its significant absorption characteristic in previous researches. Comprehensive investigations on the basis of engineering and environmental characteristics, as well as the microcosmic mechanism, are rarely reported. In the present work, the UCS and leaching characteristics, as well as the microstructure analysis of the alkaline residue-treated contaminated soil, are experimentally investigated to reveal the remediation efficiency and mechanism.


## 2. Testing Materials and Procedures

### 2.1. Testing Materials

The tested soil was excavated from a construction site at depth of 3.0–4.5 m in Wuhu City, Anhui province, which is in the eastern part of China. The basic physical properties and the major chemical components determined by the X-ray fluorescence (XRF) technique are listed in Tables1 and 2, respectively. As can be seen, the tested soil is a kind of plastic clay with SiO2 and Al2O3 contents more than 80%. The maximum dry density and the optimal water content are 1.81 g/cm3 and 18.5%, respectively, according to the compaction test (Figure 1), which is conducted following the Test Methods of Soils for Highway Engineering (JTGE 40-2007) [16].Table 1
Basic physical properties of the tested soil.
Water content (%)
Specific gravity
Void ratio
Degree of saturation (%)
Liquid limit (%)
Plastic limit (%)
Plastic index
Cohesive strength (kPa)
Internal friction angle (°)
20.18
2.72
0.718
94
41.7
23.1
18.6
65
13.2Table 2
Major chemical components of the tested soil.
Component
CaO
MgO
SiO2
Al2O3
Fe2O3
P2O5
TiO2
Na2O
K2O
MnO
Content (%)
0.81
2.04
60.93
20.77
9.21
0.11
1.25
0.52
3.94
0.12Figure 1
Compaction curve of the tested soil.The alkaline residue adopted in the present work is collected from an ammonia alkali factory in Weifang, Shandong province, which is in the eastern part of China. The major chemical components determined by the XRF technique are presented in Table3. It is clear that CaO takes dominant proportion in the alkaline residue, while MgO, SiO2, and Al2O3 also take a relatively large amount. As shown in Figure 2, the particle size of AR is mainly in the range of 1–10 μm, which confirms the large specific surface area and strong adsorptive capacity of the alkaline residue adopted in the present work.Table 3
Major chemical components of the alkaline residue.
Component
CaO
MgO
SiO2
Al2O3
F
Fe2O3
P2O5
SO3
TiO2
Na2O
K2O
Cl
Content (%)
62.81
12.5
10.2
9.00
2.47
1.31
0.40
0.3
0.24
0.23
0.17
0.16Figure 2
Curves of particle size analysis of AR.In the present work, lead-contaminated soil is aimed for remediation due to its serious hazard and typical distribution in China. Analytical grade Pb(NO3)2 is selected as the heavy metal contaminants due to its high solubility, as well as the low interference of NO3− ions to the hydration process [17, 18].


### 2.2. Testing Procedures

#### 2.2.1. Specimen Preparation

In specimen preparation, the Pb2+ concentrations (mg/kg) of 0.1%, 0.5%, 1%, 2%, and 3% and alkaline residue contents of 0%, 10%, 20%, 30%, 40%, and 50% are designed in the present work. The contaminant concentrations of 0.1% indicates 1000 mg Pb2+ in the lead nitrate for 1 kg dry soil and is denoted as Pb0.1. The alkaline residue content of 10% is the mass ratio of alkaline residue to the dry soil and is denoted as AR10. After oven-drying at 105°C for 24 hours, the soil and alkaline residue were ground into powders and sized through 2 mm and 0.5 mm sieve, respectively. Then the soil and alkaline residue powders were mixed with the Pb(NO3)2 and deionized water at the designed proportions. After this, the mixtures were put into a compaction mould and statically compacted into targeted cylindrical specimens with a dimension of 100 mm in height, 50 mm in diameter, and a dry density of 1.72 mg/cm3, which equaled to the 95% of the maximum dry density. Finally, the prepared specimens were extruded from the mould and cured under standard curing conditions with temperature of 20 ± 1°C and relative humidity of 95% for 0 d, 1 d, 7 d, 14 d, 28 d, and 90 d.


#### 2.2.2. Unconfined Compressive Strength (UCS) Test

After the completion of the curing, the unconfined compressive strength tests were performed on the specimens following the Standard Test Method for Unconfined Compressive Strength of Cohesive Soil (ASTM D2166-06) [19]. The YHS-2 UCS testing apparatus at a vertical strain rate of 1%/min was adopted in the test, and three parallel specimens were tested in each test with the average value as the representative one.


#### 2.2.3. The Toxicity Characteristic Leaching Procedure (TCLP)

The leachability of heavy metals from the stabilized soils was determined using the toxicity characteristic leaching procedure (TCLP) in accordance with the U.S EPA Method 1311 [20]. The prepared specimen was crushed into pieces with the size smaller than 9.5 mm. The leachant with pH value of 2.88 ± 0.05 was prepared by diluting 5.7 ml acetic acid (HAC) into 1 L deionized water. Then, 12.5 g crushed specimen and 250 ml leachant (solid-to-liquid ratio of 1 : 20) were mixed in a polythene bottle and vibrated at the rate of 180 rpm for 18 h. After this, the leachate was filtered through 0.45 μm filter membrane, and the pH value and Pb2+ concentration in the leachate were measured to analyze the leaching characteristic of the treated specimen.


#### 2.2.4. Microstructural Test

The prepared specimen was cut into small pieces with sizes around 5 mm × 5 mm × 3 mm. Surface of the samples should be cleaned and polished carefully before freeze-drying in vacuum condition. Then, conductive coating was done to prepare the standard samples for the scanning electron microscope (SEM) test with the help from a professional institution.


## 2.1. Testing Materials

The tested soil was excavated from a construction site at depth of 3.0–4.5 m in Wuhu City, Anhui province, which is in the eastern part of China. The basic physical properties and the major chemical components determined by the X-ray fluorescence (XRF) technique are listed in Tables1 and 2, respectively. As can be seen, the tested soil is a kind of plastic clay with SiO2 and Al2O3 contents more than 80%. The maximum dry density and the optimal water content are 1.81 g/cm3 and 18.5%, respectively, according to the compaction test (Figure 1), which is conducted following the Test Methods of Soils for Highway Engineering (JTGE 40-2007) [16].Table 1
Basic physical properties of the tested soil.
Water content (%)
Specific gravity
Void ratio
Degree of saturation (%)
Liquid limit (%)
Plastic limit (%)
Plastic index
Cohesive strength (kPa)
Internal friction angle (°)
20.18
2.72
0.718
94
41.7
23.1
18.6
65
13.2Table 2
Major chemical components of the tested soil.
Component
CaO
MgO
SiO2
Al2O3
Fe2O3
P2O5
TiO2
Na2O
K2O
MnO
Content (%)
0.81
2.04
60.93
20.77
9.21
0.11
1.25
0.52
3.94
0.12Figure 1
Compaction curve of the tested soil.The alkaline residue adopted in the present work is collected from an ammonia alkali factory in Weifang, Shandong province, which is in the eastern part of China. The major chemical components determined by the XRF technique are presented in Table3. It is clear that CaO takes dominant proportion in the alkaline residue, while MgO, SiO2, and Al2O3 also take a relatively large amount. As shown in Figure 2, the particle size of AR is mainly in the range of 1–10 μm, which confirms the large specific surface area and strong adsorptive capacity of the alkaline residue adopted in the present work.Table 3
Major chemical components of the alkaline residue.
Component
CaO
MgO
SiO2
Al2O3
F
Fe2O3
P2O5
SO3
TiO2
Na2O
K2O
Cl
Content (%)
62.81
12.5
10.2
9.00
2.47
1.31
0.40
0.3
0.24
0.23
0.17
0.16Figure 2
Curves of particle size analysis of AR.In the present work, lead-contaminated soil is aimed for remediation due to its serious hazard and typical distribution in China. Analytical grade Pb(NO3)2 is selected as the heavy metal contaminants due to its high solubility, as well as the low interference of NO3− ions to the hydration process [17, 18].


## 2.2. Testing Procedures

### 2.2.1. Specimen Preparation

In specimen preparation, the Pb2+ concentrations (mg/kg) of 0.1%, 0.5%, 1%, 2%, and 3% and alkaline residue contents of 0%, 10%, 20%, 30%, 40%, and 50% are designed in the present work. The contaminant concentrations of 0.1% indicates 1000 mg Pb2+ in the lead nitrate for 1 kg dry soil and is denoted as Pb0.1. The alkaline residue content of 10% is the mass ratio of alkaline residue to the dry soil and is denoted as AR10. After oven-drying at 105°C for 24 hours, the soil and alkaline residue were ground into powders and sized through 2 mm and 0.5 mm sieve, respectively. Then the soil and alkaline residue powders were mixed with the Pb(NO3)2 and deionized water at the designed proportions. After this, the mixtures were put into a compaction mould and statically compacted into targeted cylindrical specimens with a dimension of 100 mm in height, 50 mm in diameter, and a dry density of 1.72 mg/cm3, which equaled to the 95% of the maximum dry density. Finally, the prepared specimens were extruded from the mould and cured under standard curing conditions with temperature of 20 ± 1°C and relative humidity of 95% for 0 d, 1 d, 7 d, 14 d, 28 d, and 90 d.


### 2.2.2. Unconfined Compressive Strength (UCS) Test

After the completion of the curing, the unconfined compressive strength tests were performed on the specimens following the Standard Test Method for Unconfined Compressive Strength of Cohesive Soil (ASTM D2166-06) [19]. The YHS-2 UCS testing apparatus at a vertical strain rate of 1%/min was adopted in the test, and three parallel specimens were tested in each test with the average value as the representative one.


### 2.2.3. The Toxicity Characteristic Leaching Procedure (TCLP)

The leachability of heavy metals from the stabilized soils was determined using the toxicity characteristic leaching procedure (TCLP) in accordance with the U.S EPA Method 1311 [20]. The prepared specimen was crushed into pieces with the size smaller than 9.5 mm. The leachant with pH value of 2.88 ± 0.05 was prepared by diluting 5.7 ml acetic acid (HAC) into 1 L deionized water. Then, 12.5 g crushed specimen and 250 ml leachant (solid-to-liquid ratio of 1 : 20) were mixed in a polythene bottle and vibrated at the rate of 180 rpm for 18 h. After this, the leachate was filtered through 0.45 μm filter membrane, and the pH value and Pb2+ concentration in the leachate were measured to analyze the leaching characteristic of the treated specimen.


### 2.2.4. Microstructural Test

The prepared specimen was cut into small pieces with sizes around 5 mm × 5 mm × 3 mm. Surface of the samples should be cleaned and polished carefully before freeze-drying in vacuum condition. Then, conductive coating was done to prepare the standard samples for the scanning electron microscope (SEM) test with the help from a professional institution.


## 2.2.1. Specimen Preparation

In specimen preparation, the Pb2+ concentrations (mg/kg) of 0.1%, 0.5%, 1%, 2%, and 3% and alkaline residue contents of 0%, 10%, 20%, 30%, 40%, and 50% are designed in the present work. The contaminant concentrations of 0.1% indicates 1000 mg Pb2+ in the lead nitrate for 1 kg dry soil and is denoted as Pb0.1. The alkaline residue content of 10% is the mass ratio of alkaline residue to the dry soil and is denoted as AR10. After oven-drying at 105°C for 24 hours, the soil and alkaline residue were ground into powders and sized through 2 mm and 0.5 mm sieve, respectively. Then the soil and alkaline residue powders were mixed with the Pb(NO3)2 and deionized water at the designed proportions. After this, the mixtures were put into a compaction mould and statically compacted into targeted cylindrical specimens with a dimension of 100 mm in height, 50 mm in diameter, and a dry density of 1.72 mg/cm3, which equaled to the 95% of the maximum dry density. Finally, the prepared specimens were extruded from the mould and cured under standard curing conditions with temperature of 20 ± 1°C and relative humidity of 95% for 0 d, 1 d, 7 d, 14 d, 28 d, and 90 d.


## 2.2.2. Unconfined Compressive Strength (UCS) Test

After the completion of the curing, the unconfined compressive strength tests were performed on the specimens following the Standard Test Method for Unconfined Compressive Strength of Cohesive Soil (ASTM D2166-06) [19]. The YHS-2 UCS testing apparatus at a vertical strain rate of 1%/min was adopted in the test, and three parallel specimens were tested in each test with the average value as the representative one.


## 2.2.3. The Toxicity Characteristic Leaching Procedure (TCLP)

The leachability of heavy metals from the stabilized soils was determined using the toxicity characteristic leaching procedure (TCLP) in accordance with the U.S EPA Method 1311 [20]. The prepared specimen was crushed into pieces with the size smaller than 9.5 mm. The leachant with pH value of 2.88 ± 0.05 was prepared by diluting 5.7 ml acetic acid (HAC) into 1 L deionized water. Then, 12.5 g crushed specimen and 250 ml leachant (solid-to-liquid ratio of 1 : 20) were mixed in a polythene bottle and vibrated at the rate of 180 rpm for 18 h. After this, the leachate was filtered through 0.45 μm filter membrane, and the pH value and Pb2+ concentration in the leachate were measured to analyze the leaching characteristic of the treated specimen.


## 2.2.4. Microstructural Test

The prepared specimen was cut into small pieces with sizes around 5 mm × 5 mm × 3 mm. Surface of the samples should be cleaned and polished carefully before freeze-drying in vacuum condition. Then, conductive coating was done to prepare the standard samples for the scanning electron microscope (SEM) test with the help from a professional institution.


## 3. Results and Discussion

### 3.1. Effects on the UCS of the Solidified/Stabilized Specimen

The UCS of the solidified/stabilized specimen is investigated with consideration of different influencing factors. The evolutions of the UCS with the alkaline residue contents are typically shown in Figure3.Figure 3
Evolutions of the UCS with the alkaline residue content of the specimen. Curing times of (a) 0 d and (b) 28 d.
(a)
(b)Curves in Figure3 showed significant increase of the UCS with incorporation of the alkaline residue into the specimen. Such improvement of the strength characteristic by adding alkaline residue is attributed to the formation of hydration products like CaO·SiO2·nH2O (C-S-H) and CaSiO3·CaCO3·Ca(OH)2·nH2O arising from the reactions between the CaCO3, Ca(OH)2, and SiO2 [14, 15]. Furthermore, the alkaline environment created by the alkaline residue could promote the hydration reaction and produce more hydration products. Existence of these hydration products decreases the porosity and increases the density and integrity of the specimen, which lead to the increase of the UCS. Additionally, calcium compounds like CaCO3 contained in alkaline residue could form framework in the soil resulting in the improvement of the strength as well [14, 15].As shown in Figure3, the significant effect of the curing time on the UCS can be preliminarily observed after the comparison of diagrams (a) and (b). In further analysis, the evolutions of the UCS with the curing time are presented in Figure 4.Figure 4
Evolutions of the UCS with the curing time of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)Results in Figure4 show that the UCS of the solidified/stabilized specimen increases with the curing time increasing. A notable increasing magnitude of 38%–47% can be observed before 28-day curing. After this, the evolution of the UCS becomes stable with a slight increase in magnitude until 90-day curing is reached. As described in previous research, the improved strength of the specimen with curing time is attributed to the continuous formation of the hydration products during the hydration process. The pore space in the specimen can be filled, and the solid particles can be encapsulated by these hydration products, which contribute to the improvement of the strength. However, during the later period of the curing (after 28 days in the present work), hydration is fully developed and pores in the specimen are filled by the hydration products at a large proportion. Then the microstructural variation of the specimen becomes limited resulting in relatively stable growth trend of the strength during this stage.Results in Figure4 also implied a significant effect of the initial Pb2+ concentration on the UCS of the specimen. For analysis in details, evolutions of the UCS with the initial Pb2+ concentration are depicted in Figure 5.Figure 5
Evolutions of the UCS with the initial Pb2+ concentrations of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)As shown in Figure5, the increase of the initial Pb2+ concentration in the specimen leads to a notable decrease of the UCS. This is because the reactions between the alkaline residue and the soil particles can be retarded owing to the existence of Pb2+, and then the generation of the hydration products will be decelerated [9, 21–23]. Additionally, due to the alkaline environment created by the alkaline residue, Pb2+ will be involved in the hydration reactions resulting in generation of Pb complex and reduction of the hydration products. The Pb-precipitation will also form in this alkaline environment and encapsulate the alkaline residue and soil particles, which prevent the further hydration reaction [5, 23].


### 3.2. Effects on the Leaching Characteristic of the Solidified/Stabilized Specimen

The leaching characteristics of the solidified/stabilized specimen are investigated with consideration of different influencing factors. The effects of the alkaline residue content on the leaching characteristics are typically shown in Figure6.Figure 6
Evolutions of the leached Pb2+ concentration with the alkaline residue content of the specimen. Curing times of (a) 1 d and (b) 28 d.
(a)
(b)As shown in Figure6, the leached Pb2+ concentrations are extremely high when alkaline residue contents are at low ranges and will decrease with the increase of the alkaline residue content. Notable decreasing magnitude of 94%–98% can be observed at the alkaline residue content of 30% and curing time of 28 d, which is of great importance to the engineering practice. This significant improvement of the leaching characteristic of the specimen is mainly attributed to the adsorption of Pb2+ by the generated hydration products [14]. Besides, Pb2+ could react with OH− and CO32+ in such alkaline environment leading to the formation of precipitates with Pb2+ adsorbing on the particle surface. Moreover, Pb2+ can partially replace Ca2+ in CaO·SiO2·nH2O (C-S-H) and then be fixed in the reticular structure of silicate represented as C-Pb-S-H [21, 22, 24, 25].The effects of the curing time on the leaching characteristics of the solidified/stabilized specimen are presented in Figure7.Figure 7
Evolutions of the leached Pb2+ concentration with the curing time of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)In Figure7, the leached Pb2+ concentration decreases with the curing time increasing. Notable decreasing magnitude of 89%–98% can be observed before 28-day curing at the alkaline content of 30%. After this, the evolution of the leached Pb2+ concentration becomes stable until 90-day curing is reached. This is because the hydration process will be improved and fully developed with the curing time increasing. The hydration products like CSH will be generated and effectively immobile the Pb2+ in such high alkaline environment provided by alkaline residue, which contributes to the improvement of the leaching characteristics of the specimen. Based on this result, it can be concluded that the leaching characteristics of the specimen can be improved in a short time due to the existence of the alkaline residue.One point should be paid attention in Figures6 and 7 is that the leaching characteristics of the specimen are strongly dependent on the initial Pb2+ concentration in the specimen. For further analysis, the evolutions of the leached Pb2+ concentration with the initial Pb2+ concentration in the specimen are shown in Figure 8.Figure 8
Evolutions of the leached Pb2+ concentration with the initial Pb2+ concentration of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)Results in Figure8 suggest that the leached Pb2+ concentration is extremely high for the specimen with higher initial Pb2+ concentration and will increase with the increase of the initial Pb2+ concentration in the specimen, which is attributed to the retardation of the hydration process, as well as the limitation of the immobilized capacity, due to the existence of the Pb2+ in the specimen [24, 25].


### 3.3. Microstructure Analysis

For explanation of the strength and leaching characteristics of the solidified/stabilized specimens under different conditions (alkaline residue content, curing time, and initial Pb2+ concentration), the SEM technique is adopted to perform the microstructural analysis as shown in Figure 9.Figure 9
Microstructural characteristics of the specimens tested under different conditions. (a) AR10 + Pb1 (28 d). (b) AR30 + Pb1 (28 d). (c) AR30 + Pb3 (28 d). (d) AR30 + Pb1 (90 d).
(a)
(b)
(c)
(d)As shown in Figure9, hydration products like cotton-like C-S-H, calcite drusy, and portlandite are presented in the solidified/stabilized specimen due to the physical-chemical reactions between the alkaline residue and soil [26]. Pb2+ will be immobilized in C-S-H through physical adsorption/encapsulation and chemical single displacement reactions. Ca2+ contained in C-S-H will be substituted by Pb2+ resulting in the decrease of the strength and increase of the chemical connection between Pb2+ and hydration products. Pb-CSH gel could be observed on the surface of the soil particles, which implies the effective immobilization of Pb2+ in the specimen [27, 28]. Additionally, densification of the microstructure is clearly presented due to the massive formation of the hydration products. With the increase of alkaline residue content and curing time, the hydration process will be promoted resulting in more hydration products. Based on these complicated physical-chemical reactions in the specimen, the strength and leaching characteristics will be effectively improved.


## 3.1. Effects on the UCS of the Solidified/Stabilized Specimen

The UCS of the solidified/stabilized specimen is investigated with consideration of different influencing factors. The evolutions of the UCS with the alkaline residue contents are typically shown in Figure3.Figure 3
Evolutions of the UCS with the alkaline residue content of the specimen. Curing times of (a) 0 d and (b) 28 d.
(a)
(b)Curves in Figure3 showed significant increase of the UCS with incorporation of the alkaline residue into the specimen. Such improvement of the strength characteristic by adding alkaline residue is attributed to the formation of hydration products like CaO·SiO2·nH2O (C-S-H) and CaSiO3·CaCO3·Ca(OH)2·nH2O arising from the reactions between the CaCO3, Ca(OH)2, and SiO2 [14, 15]. Furthermore, the alkaline environment created by the alkaline residue could promote the hydration reaction and produce more hydration products. Existence of these hydration products decreases the porosity and increases the density and integrity of the specimen, which lead to the increase of the UCS. Additionally, calcium compounds like CaCO3 contained in alkaline residue could form framework in the soil resulting in the improvement of the strength as well [14, 15].As shown in Figure3, the significant effect of the curing time on the UCS can be preliminarily observed after the comparison of diagrams (a) and (b). In further analysis, the evolutions of the UCS with the curing time are presented in Figure 4.Figure 4
Evolutions of the UCS with the curing time of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)Results in Figure4 show that the UCS of the solidified/stabilized specimen increases with the curing time increasing. A notable increasing magnitude of 38%–47% can be observed before 28-day curing. After this, the evolution of the UCS becomes stable with a slight increase in magnitude until 90-day curing is reached. As described in previous research, the improved strength of the specimen with curing time is attributed to the continuous formation of the hydration products during the hydration process. The pore space in the specimen can be filled, and the solid particles can be encapsulated by these hydration products, which contribute to the improvement of the strength. However, during the later period of the curing (after 28 days in the present work), hydration is fully developed and pores in the specimen are filled by the hydration products at a large proportion. Then the microstructural variation of the specimen becomes limited resulting in relatively stable growth trend of the strength during this stage.Results in Figure4 also implied a significant effect of the initial Pb2+ concentration on the UCS of the specimen. For analysis in details, evolutions of the UCS with the initial Pb2+ concentration are depicted in Figure 5.Figure 5
Evolutions of the UCS with the initial Pb2+ concentrations of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)As shown in Figure5, the increase of the initial Pb2+ concentration in the specimen leads to a notable decrease of the UCS. This is because the reactions between the alkaline residue and the soil particles can be retarded owing to the existence of Pb2+, and then the generation of the hydration products will be decelerated [9, 21–23]. Additionally, due to the alkaline environment created by the alkaline residue, Pb2+ will be involved in the hydration reactions resulting in generation of Pb complex and reduction of the hydration products. The Pb-precipitation will also form in this alkaline environment and encapsulate the alkaline residue and soil particles, which prevent the further hydration reaction [5, 23].


## 3.2. Effects on the Leaching Characteristic of the Solidified/Stabilized Specimen

The leaching characteristics of the solidified/stabilized specimen are investigated with consideration of different influencing factors. The effects of the alkaline residue content on the leaching characteristics are typically shown in Figure6.Figure 6
Evolutions of the leached Pb2+ concentration with the alkaline residue content of the specimen. Curing times of (a) 1 d and (b) 28 d.
(a)
(b)As shown in Figure6, the leached Pb2+ concentrations are extremely high when alkaline residue contents are at low ranges and will decrease with the increase of the alkaline residue content. Notable decreasing magnitude of 94%–98% can be observed at the alkaline residue content of 30% and curing time of 28 d, which is of great importance to the engineering practice. This significant improvement of the leaching characteristic of the specimen is mainly attributed to the adsorption of Pb2+ by the generated hydration products [14]. Besides, Pb2+ could react with OH− and CO32+ in such alkaline environment leading to the formation of precipitates with Pb2+ adsorbing on the particle surface. Moreover, Pb2+ can partially replace Ca2+ in CaO·SiO2·nH2O (C-S-H) and then be fixed in the reticular structure of silicate represented as C-Pb-S-H [21, 22, 24, 25].The effects of the curing time on the leaching characteristics of the solidified/stabilized specimen are presented in Figure7.Figure 7
Evolutions of the leached Pb2+ concentration with the curing time of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)In Figure7, the leached Pb2+ concentration decreases with the curing time increasing. Notable decreasing magnitude of 89%–98% can be observed before 28-day curing at the alkaline content of 30%. After this, the evolution of the leached Pb2+ concentration becomes stable until 90-day curing is reached. This is because the hydration process will be improved and fully developed with the curing time increasing. The hydration products like CSH will be generated and effectively immobile the Pb2+ in such high alkaline environment provided by alkaline residue, which contributes to the improvement of the leaching characteristics of the specimen. Based on this result, it can be concluded that the leaching characteristics of the specimen can be improved in a short time due to the existence of the alkaline residue.One point should be paid attention in Figures6 and 7 is that the leaching characteristics of the specimen are strongly dependent on the initial Pb2+ concentration in the specimen. For further analysis, the evolutions of the leached Pb2+ concentration with the initial Pb2+ concentration in the specimen are shown in Figure 8.Figure 8
Evolutions of the leached Pb2+ concentration with the initial Pb2+ concentration of the specimen. Alkaline residue contents of (a) 10% and (b) 30%.
(a)
(b)Results in Figure8 suggest that the leached Pb2+ concentration is extremely high for the specimen with higher initial Pb2+ concentration and will increase with the increase of the initial Pb2+ concentration in the specimen, which is attributed to the retardation of the hydration process, as well as the limitation of the immobilized capacity, due to the existence of the Pb2+ in the specimen [24, 25].


## 3.3. Microstructure Analysis

For explanation of the strength and leaching characteristics of the solidified/stabilized specimens under different conditions (alkaline residue content, curing time, and initial Pb2+ concentration), the SEM technique is adopted to perform the microstructural analysis as shown in Figure 9.Figure 9
Microstructural characteristics of the specimens tested under different conditions. (a) AR10 + Pb1 (28 d). (b) AR30 + Pb1 (28 d). (c) AR30 + Pb3 (28 d). (d) AR30 + Pb1 (90 d).
(a)
(b)
(c)
(d)As shown in Figure9, hydration products like cotton-like C-S-H, calcite drusy, and portlandite are presented in the solidified/stabilized specimen due to the physical-chemical reactions between the alkaline residue and soil [26]. Pb2+ will be immobilized in C-S-H through physical adsorption/encapsulation and chemical single displacement reactions. Ca2+ contained in C-S-H will be substituted by Pb2+ resulting in the decrease of the strength and increase of the chemical connection between Pb2+ and hydration products. Pb-CSH gel could be observed on the surface of the soil particles, which implies the effective immobilization of Pb2+ in the specimen [27, 28]. Additionally, densification of the microstructure is clearly presented due to the massive formation of the hydration products. With the increase of alkaline residue content and curing time, the hydration process will be promoted resulting in more hydration products. Based on these complicated physical-chemical reactions in the specimen, the strength and leaching characteristics will be effectively improved.


## 4. Conclusions

The strength and leaching characteristics, as well as the microstructural characteristic of the alkaline residue solidified/stabilized Pb-contaminated soil, were experimentally investigated in the present work. Some main conclusions can be summarized as follows:(1)
The UCS of the treated specimen increased with the increase of the alkaline residue content. The UCS of the treated specimen increased with the curing time increasing. Notable increasing magnitude was observed at the early period of curing followed by a slight increase in the long curing period. The increase of the initial Pb2+ concentration in the specimen resulted in a notable decrease of the UCS.(2)
Leached Pb2+ concentration after the TCLP test decreased with the increase of the alkaline residue content and curing time, while increased with the increase of the initial Pb2+ concentration in the specimen. The higher initial Pb2+ concentration in the specimen will result in more notable increase of the leached Pb2+ concentration.(3)
Microstructural analysis performed by the SEM technique confirmed the existence of CSH, calcite, portlandite, and other hydration products in the solidified/stabilized specimen. The amount of the hydration products, as well as the density and integrity of the specimen, increased with the increase of alkaline residue content and curing time.



---