# Piperidine-Substituted Perylene Sensitizer for  Dye-Sensitized Solar Cells

Authors: Joe  Otsuki; Yusho  Takaguchi; Daichi  Takahashi; Palanisamy  Kalimuthu; Surya Prakash Singh; Ashraful Islam; Liyuan Han
Journal: Advances in OptoElectronics
 (2011)

---

## Abstract

We have prepared a novel piperidine-donor-substituted perylene sensitizer,PK0002, and studied the photovoltaic performance in dye-sensitized solar cells (DSSCs). Physical properties and photovoltaic performance of this new perylene derivative PK0002 are reported and compared with those of unsubstituted perylene sensitizer, PK0003. PK0002, when anchored to nanocrystalline TiO2 films, achieves very efficient sensitization across the whole visible range extending up to 800 nm. The incident photon-to-current conversion efficiency (IPCE) spectrum was consistent with the absorption spectrum and resulted in a high short-circuit photocurrent density (Jsc) of 8.8 mA cm−2. PK0002 showed higher IPCE values than PK0003 in the 520–800 nm region. Under standard AM 1.5 irradiation (100 mW cm−2) and using an electrolyte consisting of 0.6 M dimethylpropyl-imidazolium iodide, 0.05 M I2, 0.1 M LiI, and 0.5 M tert-butylpyridine in acetonitrile, a solar cell containing sensitizer PK0002 yielded a short-circuit photocurrent density of 7.7 mA cm−2, an open-circuit photovoltage of 0.57 V, and a fill factor of 0.70, corresponding to an overall conversion efficiency of 3.1%.


---

## Body

## 1. Introduction

Dye-sensitized  solar cells (DSSCs) have been widely investigated because of their simple structure and potential for low-cost production    [1–3]. In this solar cell, a monolayer of dyes is attached to the surface of nanocrystalline TiO2 film to absorb solar light. The molecular design of dye-sensitizers that can absorb visible light of all colors for nanocrystalline oxide semiconductor solar cells is a challenging task as several requirements have to be fulfilled by the dye which are very difficult to be met simultaneously. Most of current research concerns development of panchromatic sensitizers based on organic dyes and transition metal complexes. Towards this goal, a number of transition metal complexes are used as effective sensitizers, due to their intense charge-transfer absorption over the whole visible range and highly efficient metal-to-ligand charge-transfer in a dye-sensitized solar cell device. DSSCs with dyes based on ruthenium complexes have achieved energy conversion efficiencies over 11% [4, 5]. In recent years, there has been much effort in replacing the ruthenium complexes with fully organic photosensitizers for environmental reasons, lower cost, and the possibility to obtain very high extinction coefficients, which could also allow application in thinner solar cells as demanded in, for example, solid-state DSSCs.Derivatives of perylene have been widely applied in various optical devices owing to their outstanding chemical, thermal, and photochemical stability and nontoxicity [6–12]. Several perylene dyes have been used as sensitizers in DSSCs, however, they exhibited very low overall power conversion efficiencies [13–16].  Li and Edvinsson reported diphenylamino-substituted perylene monoanhydrides as sensitizers with power conversion efficiency 3.9% [17], later on they reported 6.8% power conversion efficiency with new perylene sensitizer bearing two thiophenol groups [18]. As our research program in developing the new sensitizers [19], herein, we present a novel piperidine-donor-substituted perylene sensitizer (PK0002) and compare with unsubstituted perylene sensitizer (PK0003) as shown in Figure 1.Figure 1
Perylene derivatives.


## 2. Experimental

### 2.1. General

Dehydrated DMF was purchased from Aldrich. The synthesis ofPK0003 [20] and compound 1 [20, 21] was performed as reported in the literature. 1H NMR was recorded using a JEOL JNM-ECX-400 spectrometer (400 MHz) and the chemical shifts are referenced to internal tetramethylsilane. Atmospheric pressure chemical ionization (APCI)–HRMS was obtained on an Agilent LC/MSD TOF spectrometer. Absorption and emission spectra were obtained using Shimadzu UV-2400PC and RF-5300PC spectrometers, respectively. Spectroscopic-grade CHCl3 was purchased from Kanto Chemical. DFT calculations were performed with a Gaussian03 package using B3LYP/6-31G.Synthesis of2
A mixture of compound1 (100 mg, 0.170 mmol) and piperidine (0.30 mL, 3.6 mmol) in DMF (10 mL) was refluxed under N2 for 3 h. The reaction mixture turned from bright scarlet to deep blue in color. The solvent was removed on a rotary evaporator. The resulting residue was column chromatographed with silica gel and chloroform, yielding a purple solid (69 mg, 61%). 1H NMR (CDCl3): δ (ppm) = 8.61 (2H, m), 8.47 (1H, m), 8.40 (2H, m), 8.33 (1H, m), 8.24 (1H, d, J = 8.7 Hz), 7.64 (1H, t, J = 8.1 Hz), 7.58 (1H, d, J = 8.7 Hz), 7.44 (1H, dd, J = 8.7, 2.2 Hz), 7.20 (1H, d, J = 8.3 Hz), 7.02 (1H, d, J = 2.3 Hz), 3.19 (4H, br), 1.90 (4H, m), 1.73 (2H, br), 1.33 (9H, s), 1.30 (9H, s). APCI-HRMS: calcd for C41H41N2O2 (MH+), 593.3163; found: 593.3008.Synthesis ofPK0002
Crushed KOH pellets (1.5 g) were added to a suspension of2 (60 mg, 0.11 mmol) in t-butanol (50 mL) and the mixture was vigrously refluxed with stirring for 2 hrs (Scheme 1). The blue solid slowly dissolved and the solution turned yellow. While hot, the reaction mixture was cautiously poured into glacial acetic acid (100 mL) with vigorous stirring. The deep blue color returned immediately and a solid precipitated. The suspension was cooled and chloroform was added to dissolve the solid. The organic layer was washed 3 times with water, dried over anhydrous sodium sulfate, stripped on a rotary evaporator and dried overnight in a dessicator. The crude product was column chromatographed on silica gel with chloroform, yielding a purple solid (69 mg, 45%). 1H NMR (CDCl3):  δ (ppm) = 8.24 (4H, m), 8.21 (1H, d, J = 8.2 Hz), 8.02 (1H, d, J = 7.8 Hz), 7.92 (1H, d, J = 8.2 Hz), 7.56 (1H, t, J = 7.8 Hz), 7.08 (1H, d, J = 8.2 Hz), 3.21 (4H, br), 1.91 (4H, m), 1.74 (2H, m). APCI-HRMS: calcd for C27H20NO3 (MH+), 406.1438; found: 406.1342.Scheme 1
Preparation ofPK0002.


### 2.2. Fabrication of Dye-Sensitized Solar Cell

A nanocrystalline TiO2 photoelectrodes of 20 μm thickness (area: 0.25 cm2) was prepared by screen-printing on conducting glass as previously described [22]. The films were further treated with 0.05 M TiCl4 and 0.1 M HCl aqueous solutions before examination [23]. Coating of the TiO2 film was carried out by immersing for 20 h in a sensitizer solution of 3×10-4 M dichlorobezene solution.  Deoxycholic acid (20 mM) was added to the dye solution as a coadsorbent to prevent aggregation of the dye molecules [24, 25]. Photovoltaic measurements were performed in a two-electrode sandwich cell configuration. The dye-deposited TiO2 film and a platinum-coated conducting glass were used as the working electrode and the counter electrode, respectively. The two electrodes were separated by a surlyn spacer (40 μm thick) and sealed by heating the polymer frame. The electrolytes were composed of 0.6 M dimethylpropyl-imidazolium iodide (DMPII), 0.05 M I2, and 0.1 M LiI in acetonitrile with (0.5 M) or without tert-butylpyridine (TBP).


### 2.3. Photovoltaic Characterization

The working electrode was illuminated through a conducting glass. The current-voltage characteristics were measured using a solar simulator (AM-1.5, 100 mW/cm2, WXS-155S-10: Wacom Denso Co. Japan). Monochromatic incident photon-to-current conversion efficiency (IPCE) for the solar cell, plotted as a function of excitation wavelength, was recorded on a CEP-2000 system (Bunkoh-Keiki Co. Ltd.). Incident photon-to-current conversion efficiency (IPCE) at each incident wavelength was calculated from (1), where Isc is the photocurrent density at short circuit in mA cm−2 under monochromatic irradiation, λ is the wavelength of incident radiation in nm, and ϕ is the incident radiative flux in mW cm−2(1)IPCE(λ)=1240(ISCλϕ).


## 2.1. General

Dehydrated DMF was purchased from Aldrich. The synthesis ofPK0003 [20] and compound 1 [20, 21] was performed as reported in the literature. 1H NMR was recorded using a JEOL JNM-ECX-400 spectrometer (400 MHz) and the chemical shifts are referenced to internal tetramethylsilane. Atmospheric pressure chemical ionization (APCI)–HRMS was obtained on an Agilent LC/MSD TOF spectrometer. Absorption and emission spectra were obtained using Shimadzu UV-2400PC and RF-5300PC spectrometers, respectively. Spectroscopic-grade CHCl3 was purchased from Kanto Chemical. DFT calculations were performed with a Gaussian03 package using B3LYP/6-31G.Synthesis of2
A mixture of compound1 (100 mg, 0.170 mmol) and piperidine (0.30 mL, 3.6 mmol) in DMF (10 mL) was refluxed under N2 for 3 h. The reaction mixture turned from bright scarlet to deep blue in color. The solvent was removed on a rotary evaporator. The resulting residue was column chromatographed with silica gel and chloroform, yielding a purple solid (69 mg, 61%). 1H NMR (CDCl3): δ (ppm) = 8.61 (2H, m), 8.47 (1H, m), 8.40 (2H, m), 8.33 (1H, m), 8.24 (1H, d, J = 8.7 Hz), 7.64 (1H, t, J = 8.1 Hz), 7.58 (1H, d, J = 8.7 Hz), 7.44 (1H, dd, J = 8.7, 2.2 Hz), 7.20 (1H, d, J = 8.3 Hz), 7.02 (1H, d, J = 2.3 Hz), 3.19 (4H, br), 1.90 (4H, m), 1.73 (2H, br), 1.33 (9H, s), 1.30 (9H, s). APCI-HRMS: calcd for C41H41N2O2 (MH+), 593.3163; found: 593.3008.Synthesis ofPK0002
Crushed KOH pellets (1.5 g) were added to a suspension of2 (60 mg, 0.11 mmol) in t-butanol (50 mL) and the mixture was vigrously refluxed with stirring for 2 hrs (Scheme 1). The blue solid slowly dissolved and the solution turned yellow. While hot, the reaction mixture was cautiously poured into glacial acetic acid (100 mL) with vigorous stirring. The deep blue color returned immediately and a solid precipitated. The suspension was cooled and chloroform was added to dissolve the solid. The organic layer was washed 3 times with water, dried over anhydrous sodium sulfate, stripped on a rotary evaporator and dried overnight in a dessicator. The crude product was column chromatographed on silica gel with chloroform, yielding a purple solid (69 mg, 45%). 1H NMR (CDCl3):  δ (ppm) = 8.24 (4H, m), 8.21 (1H, d, J = 8.2 Hz), 8.02 (1H, d, J = 7.8 Hz), 7.92 (1H, d, J = 8.2 Hz), 7.56 (1H, t, J = 7.8 Hz), 7.08 (1H, d, J = 8.2 Hz), 3.21 (4H, br), 1.91 (4H, m), 1.74 (2H, m). APCI-HRMS: calcd for C27H20NO3 (MH+), 406.1438; found: 406.1342.Scheme 1
Preparation ofPK0002.


## 2.2. Fabrication of Dye-Sensitized Solar Cell

A nanocrystalline TiO2 photoelectrodes of 20 μm thickness (area: 0.25 cm2) was prepared by screen-printing on conducting glass as previously described [22]. The films were further treated with 0.05 M TiCl4 and 0.1 M HCl aqueous solutions before examination [23]. Coating of the TiO2 film was carried out by immersing for 20 h in a sensitizer solution of 3×10-4 M dichlorobezene solution.  Deoxycholic acid (20 mM) was added to the dye solution as a coadsorbent to prevent aggregation of the dye molecules [24, 25]. Photovoltaic measurements were performed in a two-electrode sandwich cell configuration. The dye-deposited TiO2 film and a platinum-coated conducting glass were used as the working electrode and the counter electrode, respectively. The two electrodes were separated by a surlyn spacer (40 μm thick) and sealed by heating the polymer frame. The electrolytes were composed of 0.6 M dimethylpropyl-imidazolium iodide (DMPII), 0.05 M I2, and 0.1 M LiI in acetonitrile with (0.5 M) or without tert-butylpyridine (TBP).


## 2.3. Photovoltaic Characterization

The working electrode was illuminated through a conducting glass. The current-voltage characteristics were measured using a solar simulator (AM-1.5, 100 mW/cm2, WXS-155S-10: Wacom Denso Co. Japan). Monochromatic incident photon-to-current conversion efficiency (IPCE) for the solar cell, plotted as a function of excitation wavelength, was recorded on a CEP-2000 system (Bunkoh-Keiki Co. Ltd.). Incident photon-to-current conversion efficiency (IPCE) at each incident wavelength was calculated from (1), where Isc is the photocurrent density at short circuit in mA cm−2 under monochromatic irradiation, λ is the wavelength of incident radiation in nm, and ϕ is the incident radiative flux in mW cm−2(1)IPCE(λ)=1240(ISCλϕ).


## 3. Results and Discussion

### 3.1. Photophysical Properties

The absorption, excitation, and fluorescence spectra forPK0003 and PK0002 are shown in Figure 2, and the numerical data are summarized in Table 1. The absorption maxima (λmax) ofPK0003 and PK0002 were observed at 489 nm and 544 nm, respectively. Their molar absorption coefficients (ε) were calculated to be 1.0–1.6×104 M−1 cm−1. The fluorescence emission maxima (λflur) of PK0003 and PK0002 were observed at 543 nm and 655 nm, respectively. It is noticed that on going from PK0003 without a donor group to PK0002 with the donor group, the structured absorption and fluorescence bands become broader and are shifted to longer wavelengths, and the Stokes shift becomes larger. These observations imply that the more charge-transfer character is involved in the π-π* transition of the donor-substituted PK0002. PK0003 and PK0002 show a blue-shifted absorption when adsorbed onto TiO2 (Figure 3). This effect is attributed to the ring opening of the anhydride group on perylene to form two carboxylates, providing interactions with the oxide surface.Table 1
Physical properties ofPK0003 and PK0002.
CompoundAbsorption(a)Fluorescence(a)Absorption on TiO2 filmIPE0-0(c)LUMO(d)λmax/nmε×10-4/M-1cm-1λex/nm(b)λfluor/nm(b)λmax/nm(eV)(eV)(eV)PK00034891.0516543450−5.882.07−3.81PK00025441.6580655500−5.601.77−3.83(a)In CHCl3.(b)At emission maximum.(c)E0-0 values were estimated from the 5% intensity level of the absorption spectra on TiO2.(d)Calculated from E*(LUMO)=E(IP)-E0-0.Absorption, fluorescence, and excitation spectra ofPK0003 (a) and PK0002 (b) in CHCl3.
(a)(b)Figure 3
Absorption spectra ofPK0003- and PK0002-adsorbed TiO2 film.To obtain an insight into the electron distribution and relative energy level ofPK0003andPK0002 for better understanding of the charge injection and dye regeneration process, the highest occupied molecular orbital (HOMO) and the lowest unoccupied molecular orbital (LUMO) of PK0003andPK0002 were calculated with B3LYP/6-31G implemented in a Gaussian-03 program package (Figure 4). The HOMO and LUMO energies are –5.88 eV and –3.18 eV, respectively, for PK0003. The corresponding energies for PK0002 are –5.31 eV and –2.88 eV, respectively. These values are positively shifted due to the introduction of the donor moiety, piperidine, at the 9th position. The influence of the introduction of the donor group is larger on the HOMO, which is shifted by +0.57 eV, than on the LUMO, which is shifted by +0.30 eV. Upon adsorption on the TiO2 surface, the carboxylic anhydride group is believed to be cleaved to become dicarboxylate. Therefore, the DFT calculations were also conducted for disodium salts of the dicarboxylate as models for the adsorbed molecules. The HOMO and LUMO energies for PK0002 are –4.33 eV and –1.63 eV, respectively [20]. The major effect is rise in energy of both of the HOMO and LUMO. The effect is more pronounced for the LUMO, resulting in an increase in the HOMO–LUMO gap from 2.43 eV for the anhydride to 2.70 eV for the dicarboxylate. This result agrees with the blue-shifted absorption spectra of PK0003 and PK0002 when adsorbed onto TiO2 (Figure 3).Figure 4
Frontier orbitals ofPK0003 and PK0002.The ionization potential (IP) ofPK0003 and PK0002 bound to nanocrystalline TiO2 film was determined using a photoemission yield spectrometer (Riken Keiki AC-3E). The ground-state oxidation potential (IP) values of -5.88 eV and -5.60 eV obtained for sensitizer PK0003 and PK0002, respectively, were low enough for efficient regeneration of the oxidized dye through reaction with iodide [26]. The excited-state oxidation potential, LUMO, of sensitizers PK0003and PK0002 was estimated at −3.81 eV and −3.83 eV, respectively, which lies above the conduction band edge (-4.2 eV) [2] of nanocrystalline TiO2. Efficient electron injection into the conduction band of TiO2 is therefore expected to occur with both sensitizers PK0003 and PK0002.


### 3.2. Photovoltaic Performance

The photovoltaic properties of the solar cells fabricated with these organic dyes were measured under simulated AM 1.5G irradiation (100 mW cm−2). The open-circuit photovoltage (Voc), short-circuit photocurrent density (Jsc), fill factor (ff), and solar energy-to-electricity conversion efficiencies (η) were listed in Table 2. Figure 5 shows the photocurrent action spectra for the cells with sensitizers PK0003 and PK0002where the incident photons-to-current conversion efficiency (IPCE) values are plotted as a function of wavelength. PK0003achieved efficient sensitization of nanocrystalline TiO2 across the whole visible range and displayed the highest IPCE value of 80% at around 450 nm. Under similar conditions, PK0002 showed higher IPCE values than PK0003 in the 520–800 nm region. This result is consistent with the absorption spectra of the sensitizers on the TiO2 surface (Figure 3). PK0002shows the highest IPCE value of 70% at around 470 nm. One possible explanation for this low IPCE value of sensitizer PK0002 is the aggregation of sensitizer molecules on the TiO2 surface, which could not be completely suppressed by addition of deoxycholic acid (DCA) as a coadsorbent.Table 2
The photovoltaic data of DSSCs based onPK0003 and PK0002.
DyeTBPJsc[mAcm-2]Voc[V]F.F.Eff. [%]PK000307.60.450.632.2PK00030.5 M4.10.560.691.6PK000208.80.410.592.1PK00020.5 M7.70.570.703.1Figure 5
Photocurrent action spectra (IPCE) of nanocrystalline TiO2 film sensitized by PK0003(blue line) andPK0002(red line). The redox electrolyte solution was a mixture of 0.6 M DMPII, 0.05 M I2, and 0.1 M LiI in acetonitrile.Figure6 shows photocurrent voltage curves of a sandwich-type sealed solar cell based on PK0003andPK0002at standard AM 1.5 irradiation with using an electrolyte of 0.6 M dimethylpropyl-imidazolium iodide (DMPII), 0.05 M I2 and 0.1 M LiI in acetonitrile with (0.5 M) or without tert-butylpyridine (TBP). PK0003 and PK0002-sensitized cell gave a short-circuit photocurrent density (Jsc) of 7.6 mA cm−2 and 8.8 mA cm−2, and an overall conversion efficiency (η) of 2.2% and 2.1%, respectively, using electrolytes with no TBP. The short-circuit photocurrent density decreased by adding TBP in the electrolyte. In contrast, the open-circuit voltage and the fill factor increased significantly with the presence of TBP. TBP probably adsorbed on the bare TiO2 surface and suppress the recombination between the injected electrons and I3- ions [27]. As shown in Table 2, the solar cell sensitized with PK0002showed a photocurrent density of 7.7 mA cm−2, an open-circuit potential of 0.57 V, and a fill factor of 0.70, corresponding to an overall conversion efficiency (η) of 3.1% with the electrolyte containing 0.5 M TBP under standard AM 1.5 irradiation (100 mW cm−2). Thus, this class of piperidine-substituted perylene sensitizer serves as a basis for further design of new potential sensitizers by introducing suitable substituents on the perylene to improve the light harvesting efficiency of the sensitizer.Figure 6
Photocurrent voltage characteristics of a nanocrystalline photoelectrochemical cell sensitized with the dyePK0003andPK0002at AM 1.5 illuminations (light intensity: 100 mW cm−2).


## 3.1. Photophysical Properties

The absorption, excitation, and fluorescence spectra forPK0003 and PK0002 are shown in Figure 2, and the numerical data are summarized in Table 1. The absorption maxima (λmax) ofPK0003 and PK0002 were observed at 489 nm and 544 nm, respectively. Their molar absorption coefficients (ε) were calculated to be 1.0–1.6×104 M−1 cm−1. The fluorescence emission maxima (λflur) of PK0003 and PK0002 were observed at 543 nm and 655 nm, respectively. It is noticed that on going from PK0003 without a donor group to PK0002 with the donor group, the structured absorption and fluorescence bands become broader and are shifted to longer wavelengths, and the Stokes shift becomes larger. These observations imply that the more charge-transfer character is involved in the π-π* transition of the donor-substituted PK0002. PK0003 and PK0002 show a blue-shifted absorption when adsorbed onto TiO2 (Figure 3). This effect is attributed to the ring opening of the anhydride group on perylene to form two carboxylates, providing interactions with the oxide surface.Table 1
Physical properties ofPK0003 and PK0002.
CompoundAbsorption(a)Fluorescence(a)Absorption on TiO2 filmIPE0-0(c)LUMO(d)λmax/nmε×10-4/M-1cm-1λex/nm(b)λfluor/nm(b)λmax/nm(eV)(eV)(eV)PK00034891.0516543450−5.882.07−3.81PK00025441.6580655500−5.601.77−3.83(a)In CHCl3.(b)At emission maximum.(c)E0-0 values were estimated from the 5% intensity level of the absorption spectra on TiO2.(d)Calculated from E*(LUMO)=E(IP)-E0-0.Absorption, fluorescence, and excitation spectra ofPK0003 (a) and PK0002 (b) in CHCl3.
(a)(b)Figure 3
Absorption spectra ofPK0003- and PK0002-adsorbed TiO2 film.To obtain an insight into the electron distribution and relative energy level ofPK0003andPK0002 for better understanding of the charge injection and dye regeneration process, the highest occupied molecular orbital (HOMO) and the lowest unoccupied molecular orbital (LUMO) of PK0003andPK0002 were calculated with B3LYP/6-31G implemented in a Gaussian-03 program package (Figure 4). The HOMO and LUMO energies are –5.88 eV and –3.18 eV, respectively, for PK0003. The corresponding energies for PK0002 are –5.31 eV and –2.88 eV, respectively. These values are positively shifted due to the introduction of the donor moiety, piperidine, at the 9th position. The influence of the introduction of the donor group is larger on the HOMO, which is shifted by +0.57 eV, than on the LUMO, which is shifted by +0.30 eV. Upon adsorption on the TiO2 surface, the carboxylic anhydride group is believed to be cleaved to become dicarboxylate. Therefore, the DFT calculations were also conducted for disodium salts of the dicarboxylate as models for the adsorbed molecules. The HOMO and LUMO energies for PK0002 are –4.33 eV and –1.63 eV, respectively [20]. The major effect is rise in energy of both of the HOMO and LUMO. The effect is more pronounced for the LUMO, resulting in an increase in the HOMO–LUMO gap from 2.43 eV for the anhydride to 2.70 eV for the dicarboxylate. This result agrees with the blue-shifted absorption spectra of PK0003 and PK0002 when adsorbed onto TiO2 (Figure 3).Figure 4
Frontier orbitals ofPK0003 and PK0002.The ionization potential (IP) ofPK0003 and PK0002 bound to nanocrystalline TiO2 film was determined using a photoemission yield spectrometer (Riken Keiki AC-3E). The ground-state oxidation potential (IP) values of -5.88 eV and -5.60 eV obtained for sensitizer PK0003 and PK0002, respectively, were low enough for efficient regeneration of the oxidized dye through reaction with iodide [26]. The excited-state oxidation potential, LUMO, of sensitizers PK0003and PK0002 was estimated at −3.81 eV and −3.83 eV, respectively, which lies above the conduction band edge (-4.2 eV) [2] of nanocrystalline TiO2. Efficient electron injection into the conduction band of TiO2 is therefore expected to occur with both sensitizers PK0003 and PK0002.


## 3.2. Photovoltaic Performance

The photovoltaic properties of the solar cells fabricated with these organic dyes were measured under simulated AM 1.5G irradiation (100 mW cm−2). The open-circuit photovoltage (Voc), short-circuit photocurrent density (Jsc), fill factor (ff), and solar energy-to-electricity conversion efficiencies (η) were listed in Table 2. Figure 5 shows the photocurrent action spectra for the cells with sensitizers PK0003 and PK0002where the incident photons-to-current conversion efficiency (IPCE) values are plotted as a function of wavelength. PK0003achieved efficient sensitization of nanocrystalline TiO2 across the whole visible range and displayed the highest IPCE value of 80% at around 450 nm. Under similar conditions, PK0002 showed higher IPCE values than PK0003 in the 520–800 nm region. This result is consistent with the absorption spectra of the sensitizers on the TiO2 surface (Figure 3). PK0002shows the highest IPCE value of 70% at around 470 nm. One possible explanation for this low IPCE value of sensitizer PK0002 is the aggregation of sensitizer molecules on the TiO2 surface, which could not be completely suppressed by addition of deoxycholic acid (DCA) as a coadsorbent.Table 2
The photovoltaic data of DSSCs based onPK0003 and PK0002.
DyeTBPJsc[mAcm-2]Voc[V]F.F.Eff. [%]PK000307.60.450.632.2PK00030.5 M4.10.560.691.6PK000208.80.410.592.1PK00020.5 M7.70.570.703.1Figure 5
Photocurrent action spectra (IPCE) of nanocrystalline TiO2 film sensitized by PK0003(blue line) andPK0002(red line). The redox electrolyte solution was a mixture of 0.6 M DMPII, 0.05 M I2, and 0.1 M LiI in acetonitrile.Figure6 shows photocurrent voltage curves of a sandwich-type sealed solar cell based on PK0003andPK0002at standard AM 1.5 irradiation with using an electrolyte of 0.6 M dimethylpropyl-imidazolium iodide (DMPII), 0.05 M I2 and 0.1 M LiI in acetonitrile with (0.5 M) or without tert-butylpyridine (TBP). PK0003 and PK0002-sensitized cell gave a short-circuit photocurrent density (Jsc) of 7.6 mA cm−2 and 8.8 mA cm−2, and an overall conversion efficiency (η) of 2.2% and 2.1%, respectively, using electrolytes with no TBP. The short-circuit photocurrent density decreased by adding TBP in the electrolyte. In contrast, the open-circuit voltage and the fill factor increased significantly with the presence of TBP. TBP probably adsorbed on the bare TiO2 surface and suppress the recombination between the injected electrons and I3- ions [27]. As shown in Table 2, the solar cell sensitized with PK0002showed a photocurrent density of 7.7 mA cm−2, an open-circuit potential of 0.57 V, and a fill factor of 0.70, corresponding to an overall conversion efficiency (η) of 3.1% with the electrolyte containing 0.5 M TBP under standard AM 1.5 irradiation (100 mW cm−2). Thus, this class of piperidine-substituted perylene sensitizer serves as a basis for further design of new potential sensitizers by introducing suitable substituents on the perylene to improve the light harvesting efficiency of the sensitizer.Figure 6
Photocurrent voltage characteristics of a nanocrystalline photoelectrochemical cell sensitized with the dyePK0003andPK0002at AM 1.5 illuminations (light intensity: 100 mW cm−2).


## 4. Conclusion

We have synthesized a novel perylene derivative with a piperidine donor substituent,PK0002, for dye-sensitized solar cells. PK0002 achieved very efficient sensitization of nanocrystalline TiO2 over the whole visible range extending into the near-IR region (ca. 800 nm). The photovoltaic data of this new sensitizer show 3.1% power conversion efficiency under standard AM 1.5 irradiation (100 mW cm−2). Further study will target the development of a high-performance solar cell through modification of the electronic and steric environments of the sensitizers on the basis of alteration of the substituent on the perylene moiety.



---