# Fabrication of TiO2@Yeast-Carbon Hybrid Composites with the Raspberry-Like Structure and Their Synergistic Adsorption-Photocatalysis Performance

Authors: Dang Yu; Bai Bo; He Yunhua
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

In the present work, we report the preparation and photocatalytic properties of TiO2@yeast-carbon with raspberry-like structure using a pyrolysis method. The products are characterized by field emission scanning electron microscopy (FE-SEM), energy dispersive spectrometry (EDS), X-ray diffraction (XRD), thermal gravimetric and differential thermal analysis (TGA-DTA), Fourier transformed infrared spectroscopy (FT-IR), and ultraviolet visible spectroscopy (UV-VIS), respectively. The results show that the hybrid TiO2@yeast-carbon microspheres have ordered elliptic shapes of uniform size (length = 3.5±0.3 μm; width = 2.5±0.5 μm).  UV-VIS ascertains that the as-prepared microspheres possess an obvious light response in a wide range of 250–400 nm. In the decomposition of typical model pollutants including methylene blue and congo red, the hybrid composites exhibited excellent photocatalytic activity for the methylene blue due to the enhanced adsorption ability. Further investigation reveals that the combined effect of adsorption from the yeast-carbon core and photocatalytic degradation from the attached TiO2 nanoparticles were responsible for the improvement of the photocatalytic activities. Hereby, the raspberry-like TiO2@yeast-carbon has promising applications in water purification.


---

## Body

## 1. Introduction

In the past few years, raspberry-like composite particles with well-defined structures have become the subject of rapidly growing interest due to their high surface roughness and potential applications [1, 2]. The unique raspberry-like composites have combined excellent characteristics of host particles and guest particles, such as higher surface area, increased chemical and biological stability, rich surface chemical component, and different magnetic or optical properties [3].The high surface area, large pores (macroporosity), and the presence of surface hydroxyl groups make carbon substance an ideal catalyst support [4–6]. Like the titania photocatalysts supported on the carbon matrix by means of several strategies [7–9] appear to have various benefits and advantages for providing a cheap and effective wastewater treatment and remediation options [10, 11]. For example, Hu et al. [12] obtained TiO2 nanoparticles/carbon nanotubes particles with raspberry-like structure by combining sol-gel and electrospinning methods. Liu et al. [13] demonstrated the formation of TiO2/carbon fibers (ACFs) composite photocatalyst via sol-gel method and the TiO2/ACFs is especially helpful for the removal of low molecular weight organic pollutants in the contaminated water. Areerachakul et al. [14] prepared well-structured TiO2/granular-activated carbon (GAC) hybrid particles. The TiO2/GAC showed excellent capabilities in decomposing the herbicide of metsulfuron-methyl (MM) from waste water. In brief, using carbon materials above-mentioned as catalyst supports has increased the photodegradation rate by progressively allowing an increased quantity of substrate to come in contact with the TiO2 by means of adsorption. In this respect, carbon matrix has been proven to be an invaluable support in promoting the photocatalytic process [15–17] through providing a synergistic effect by creating a common interface between both the carbon phase and the TiO2 nanoparticle phase. Such synergistic effect can be explained as an enhanced adsorption of the target pollutant onto the carbon phase followed closely by a transfer through an interphase to the TiO2 phase, giving a complete photodegradation process [18].The yeast-carbon is a porous and amorphous solid carbon material, which is derived mainly from baker’s yeast. For instance, Nacoo and Aquarone [19] reported the fabrication of yeast-carbon by carbonizing in a gas-heated muffle. The obtained yeast-carbon possessed higher surface area. Similarly, Guan et al. [20] synthesized amphiphilic porous hollow carbonaceous materials via mild hydrothermal treatment of yeast cells. The resultant carbon material displayed effective adsorption of organic chemicals in wastewater treatment. Thus, in the present study, a novel TiO2@yeast-carbon microsphere with raspberry-like morphology was fabricated firstly by a single-step strategy based on the pyrolysis method. The obtained hybrid microspheres were characterized by FE-SEM, EDS, XRD, TGA-DTA, FT-IR, and UV-VIS, respectively. A possible mechanism for the formation of the composite microspheres was proposed. In addition, the synergistic effect of adsorption-photocatalysis performance in the TiO2@yeast-carbon microspheres was evaluated by examining the decolonization of methylene blue and congo red.


## 2. Materials and Methods

### 2.1. Materials

The powdered yeast was purchased from Angel Yeast Company. Photocatalyst was TiO2 from Degussa and was used without further purification. In all preparations, absolute ethanol and double-distilled water were used. Methylene blue (MB) and congo red (CR) were analytic grades and were used as the model pollutants in present work.


### 2.2. Preparation of Raspberry-Like TiO2@Yeast-Carbon Hybrid Microspheres

In a typical synthesis procedure, 125.0 mg yeast powder was washed with distilled water and absolute ethanol for three times, respectively. The yeast was dissolved in 20.0 mL of distilled water and stirred vigorously for 30 minutes. The pH was adjusted to approximately 3 by adding drop wise sulfuric acid. Further, 10.0 mg TiO2 was dispersed in 20.0 mL of distilled water, using ultrasonic vibration for 1.0 minute. The pH was adjusted to approximately 9-10 with sodium hydroxide and stirred for 30.0 min. Then the suspended TiO2 and yeast were gathered by centrifugation from their own suspensions and redistributed in 20.0 mL of distilled water. Afterwards, TiO2 and yeast suspensions were mixed and magnetically stirred for 1.5 h at room temperature and left for 3.0 h without further stirring or shaking to ensure the formation of TiO2@yeast particles. Thus, the mixture was centrifuged in three or more cycles to remove the undesired components and finally desiccated at 353 K for 1.0 h. Subsequently the TiO2@yeast particles were calcined at 573 K for 1.0 h in a nitrogen pipe furnace and cooled to room temperature. After that, the TiO2@yeast-carbon composite microspheres were obtained.


### 2.3. Sample Analysis

Philips XL-30 field emission scanning electron microscope (FE-SEM) was used to observe the morphology of samples. X-ray diffraction (XRD) patterns were collected on X. Pert Pro diffractometer using Cu Kα radiation (λ = 0.15418 nm) at a scanning rate of 10°/min. Thermal gravimetric analysis and differential thermal analysis (TGA-DTA) were carried out on an EXSTAR apparatus at a heating rate of 40°/min in flowing high purity N2. Fourier-transform infrared spectroscopy measurements (FT-IR) were recorded with a Bio-Rad FTS135 spectrometer in the rage of 370–4000 cm−1. UV-VIS diffuse reflectance spectra (UV-VIS) were measured on a HITACHI 340 UV-VIS spectrophotometer.


### 2.4. Photocatalytic Activity

The methylene blue (MB) dye and congo red (CR) are widely used in dye industry. Therefore, the elimination of these compounds is becoming an increasingly important environmental problem. Photocatalytic degradation of MB and CR was evaluated under UV irradiation in an aqueous media. The initial concentration of MB and CR was set as 2~3 mg/L, respectively. The amount of photocatalysts including yeast-carbon and TiO2@yeast-carbon were kept at 0.25 g/L. Before UV irradiation, the suspension containing photocatalyst, MB, and CR was deposited within 50.0 min to establish adsorption-desorption equilibrium. Then the suspension was irradiated under a UV lamp (the intensity of irradiation is 60 W). The concentration of MB and CR was traced by UV-VIS spectroscopy. The absorbance characteristic at bands 666.4 nm and 499.0 nm was taken to determine MB and CR concentration by using a calibration curve, respectively.


## 2.1. Materials

The powdered yeast was purchased from Angel Yeast Company. Photocatalyst was TiO2 from Degussa and was used without further purification. In all preparations, absolute ethanol and double-distilled water were used. Methylene blue (MB) and congo red (CR) were analytic grades and were used as the model pollutants in present work.


## 2.2. Preparation of Raspberry-Like TiO2@Yeast-Carbon Hybrid Microspheres

In a typical synthesis procedure, 125.0 mg yeast powder was washed with distilled water and absolute ethanol for three times, respectively. The yeast was dissolved in 20.0 mL of distilled water and stirred vigorously for 30 minutes. The pH was adjusted to approximately 3 by adding drop wise sulfuric acid. Further, 10.0 mg TiO2 was dispersed in 20.0 mL of distilled water, using ultrasonic vibration for 1.0 minute. The pH was adjusted to approximately 9-10 with sodium hydroxide and stirred for 30.0 min. Then the suspended TiO2 and yeast were gathered by centrifugation from their own suspensions and redistributed in 20.0 mL of distilled water. Afterwards, TiO2 and yeast suspensions were mixed and magnetically stirred for 1.5 h at room temperature and left for 3.0 h without further stirring or shaking to ensure the formation of TiO2@yeast particles. Thus, the mixture was centrifuged in three or more cycles to remove the undesired components and finally desiccated at 353 K for 1.0 h. Subsequently the TiO2@yeast particles were calcined at 573 K for 1.0 h in a nitrogen pipe furnace and cooled to room temperature. After that, the TiO2@yeast-carbon composite microspheres were obtained.


## 2.3. Sample Analysis

Philips XL-30 field emission scanning electron microscope (FE-SEM) was used to observe the morphology of samples. X-ray diffraction (XRD) patterns were collected on X. Pert Pro diffractometer using Cu Kα radiation (λ = 0.15418 nm) at a scanning rate of 10°/min. Thermal gravimetric analysis and differential thermal analysis (TGA-DTA) were carried out on an EXSTAR apparatus at a heating rate of 40°/min in flowing high purity N2. Fourier-transform infrared spectroscopy measurements (FT-IR) were recorded with a Bio-Rad FTS135 spectrometer in the rage of 370–4000 cm−1. UV-VIS diffuse reflectance spectra (UV-VIS) were measured on a HITACHI 340 UV-VIS spectrophotometer.


## 2.4. Photocatalytic Activity

The methylene blue (MB) dye and congo red (CR) are widely used in dye industry. Therefore, the elimination of these compounds is becoming an increasingly important environmental problem. Photocatalytic degradation of MB and CR was evaluated under UV irradiation in an aqueous media. The initial concentration of MB and CR was set as 2~3 mg/L, respectively. The amount of photocatalysts including yeast-carbon and TiO2@yeast-carbon were kept at 0.25 g/L. Before UV irradiation, the suspension containing photocatalyst, MB, and CR was deposited within 50.0 min to establish adsorption-desorption equilibrium. Then the suspension was irradiated under a UV lamp (the intensity of irradiation is 60 W). The concentration of MB and CR was traced by UV-VIS spectroscopy. The absorbance characteristic at bands 666.4 nm and 499.0 nm was taken to determine MB and CR concentration by using a calibration curve, respectively.


## 3. Results and Discussion

### 3.1. Materials Characterization

The shape and structure of the samples are shown in Figure1. The SEM image in Figure 1(a) shows that the prime yeast cells have a regular ellipsoidal shape with a diameter varying between 2.6 and 3.7 μm. Figure 1(b) shows an image of the precursor of TiO2@yeast-carbon. Compared with the bared yeast, the size of the TiO2@yeast (length=3.7±0.4μm; width=2.6±0.5μm) was gently increased due to the attachment of TiO2 nanoparticles. The picture in Figure 1(d) shows an overall image of the TiO2@yeast-carbon microspheres. The particles maintained the shape of the original precursor and had the average diameter (length=3.7±0.3μm; width=2.5±0.5μm). Further, higher resolution image in Figure 1(f) shows that the nano-sized TiO2 particles randomly decorated the surface of yeast spheres, which have the morphology of raspberry-like composites. Similar morphology has been reported for the synthesis of the raspberry-like PMMA/SiO2 hybrid microspheres [21]. Moreover, the nanoparticles TiO2 were relatively dispersed on the yeast-carbon in comparison with the agglomerated TiO2 in the TiO2/spherical activated carbons composed by Oh et al. [22]. In addition, the raspberry-like morphology of the TiO2@yeast-carbon microspheres can be confirmed through the EDS analysis. In the insert image in Figure 1(f), the sample contained Ti, C, O, S, and P; no other impurity element is detected, confirming that the TiO2 particles were coated on the surface of the yeast-carbon. By comparing the TiO2@yeast precursor with the TiO2@yeast-carbon product, it can be seen that the color of particles changed from pure white to ash black. Thus, it can be inferred that the carbonization of the yeast occurred in the pyrolysis process. In this respect, the control experiments of the yeast-carbon without the attachment of nanoparticles TiO2 have been conducted under the same conditions. The image of yeast-carbon in Figure 1(c) indicates that the yeast-carbon with an average diameter (length=3.5±0.4μm;  width=2.3±0.50μm) has smooth surface morphology and rich pore structure, which contrasts with the morphology of yeast-carbon synthesized by Shen et al. [23] in which a relatively high distribution of broken shells was observed.SEM images of (a) the naked yeast, (b) general observation of the raspberry-like TiO2@yeast precursor, (c) the yeast-carbon, (d) the overall view of the raspberry-like TiO2@yeast-carbon microspheres, (e) the selected raspberry-like TiO2@yeast-carbon microspheres, and (f) typical raspberry-like TiO2@yeast-carbon microspheres observed under high magnification.
(a)
(b)
(c)
(d)
(e)
(f)XRD patterns of yeast, yeast-carbon, TiO2@yeast-carbon, and TiO2 are displayed in Figure 2. The broad peak around 2θ = 20° indicates that the yeast carbon (in Figure 2(a)) and the yeast (in Figure 2(b)) can be assigned to amorphous species. In Figures 2(c) and 2(d) display the XRD patterns of the hybrid TiO2@yeast-carbon. The broad peaks centering at 2θ = 25°, 37°, 48°, 55°, and 63° are assigned to anatase-type TiO2 (JCPDS. No: 21-1272) [24]. Other diffraction peaks are in good agreement with diffraction peaks of rutile-type TiO2 (JCPDS. No: 21-1276) [25]. The relative intensity of diffraction peaks of TiO2@yeast carbon is approximately identical with the original components of the TiO2 as guest particles (P25TiO2: 78% anatase-type TiO2 and 22% rutile-type TiO2). The broad peaks at 2θ = 20° in the Figures 2(c) and 2(d) are mainly caused by the amorphous structure of yeast-carbon.Figure 2
XRD patterns of (a) the prepared yeast-carbon, (b) the premier yeast, (c) the  80% of TiO2@yeast-carbon, (d) the 40% of TiO2@yeast-carbon, and (e) the pure TiO2.In Figure3, the distinct decrease in weight of the bare yeast is shown during a wide temperature range of 280–600°C. The rapid weight loss of approximately 50.0% at the temperature range of 280–370°C may be associated with the split of the polysaccharide chains in the yeast [26, 27], which is accompanied by a broad exothermal peak at about 370°C in the DTA curve. The ultimate weight loss from 400 to 600°C can be resulted from the cross-linking of oligosaccharides [28] in the yeast, which is accompanied by the endothermic peak at 500°C in the DTA curve. The total weight loss reaches to about 30.0% and the last weight of the residual ashes is approximately 70.0% of the original yeast biomass. In comparison with the naked yeast, the carbonization reaction of the TiO2@yeast precursor was started at temperatures about 250°C. The broad exothermal peak at around 200–300°C may be related to the carbonized decomposition of organic substrate in the yeast along with the rapid weight loss of 50.0%. It is worth noting that the broader exothermal peak appeared at around 300–450°C. This may be caused by the release of constitution water and further crystallization of TiO2 [29]. The wider exothermal peak at 450–600°C can be ascribed to the crystal shift from anatase to rutile phase.Figure 3
TGA-DTA curves of the yeast and the TiO2@yeast-carbon.After pyrolysis entirely, the raspberry-like TiO2@yeast-carbon microspheres can be attained, which has been proved by SEM analysis. The connection between the guest particles TiO2 and the host particles of the yeast-carbon can be elaborated further by FT-IR analysis. FT-IR spectra of the yeast, yeast-carbon, TiO2@yeast precursor, TiO2 and TiO2@yeast-carbon composites are presented in Figure 4, respectively. For the yeast-carbon, the band around 1570 cm−1 can be ascribed to –C=C– stretching bond originated from the inherent structure of yeast, and the bands at 1704 and 1210 cm−1 correspond to C=O, C–O stretching of carboxyl groups, respectively [30]. As for TiO2@yeast-carbon composites, the broad and intense peak at 3500–3200 cm−1 can be assigned to the stretching of –OH group due to the bound water in the TiO2@yeast-carbon composites [31, 32]. The stretching bond corresponding to skeletal Ti–O–Ti is clearly represented in the region of 509 cm−1. The band at 1171 cm−1 suggests the presence of C–O bond [33].  The band at around 620 cm−1 can be attributed to the Ti–O–C vibration, which indicates that TiO2 nanoparticles were chemically bonded with yeast-carbon in hybrid particles [34]. Moreover, the band at 3350 cm−1 is more prominent in TiO2@yeast-carbon composites than that of TiO2, indicating that there were more hydroxyl groups in the TiO2@yeast-carbon hybrid particles. Generally, more hydroxyl groups lead to generation of more •OH radicals in photocatalysis, which can enhance the photocatalytic activity of TiO2 [35].Figure 4
FT-IR spectrum of (a) the original yeast, (b) the TiO2 nanoparticle, (c) the TiO2@yeast precursor, (d) the yeast-carbon, (e) the 80% TiO2@yeast-carbon, and (f) the 40% TiO2@yeast-carbon.Based on the characterization discussed above, the following mechanism that appeared in Scheme1 is proposed to account for the formation procedure of the raspberry-like TiO2@yeast-carbon hybrid microspheres. In Scheme 1, the opposite zeta potentials of yeast cells with a positive charge (H+) and the nanoparticles TiO2 with a negative charge (OH−) were adjusted previously by tuning the pH of their own aqueous suspensions. Then the TiO2@yeast hybrid precursor with raspberry-like morphology was obtained once the aforementioned aqueous suspensions were mixed [36]. In the obtained raspberry-like TiO2@yeast precursor, the yeast acted as the host cores and TiO2 as the guest particles. Afterwards, the carbonization of yeast core in the precursors of raspberry-like TiO2@yeast can be fulfilled by a gradual temperature-rise procedure, which can obtain the hybrid TiO2@yeast-carbon composites. TGA-DTA results showed that the final weight loss is approximately 50.0% in the process of carbonization. In the obtained raspberry-like TiO2@yeast-carbon, TiO2 nanoparticles were chemically bonded with yeast-carbon through FT-IR analysis.Scheme 1
Schematic illustration for the formation of the raspberry-like TiO2@yeast-carbon and their synergistic effect in the removal of dyes aqueous solutions.Figure5 shows the UV-VIS diffuse reflectance spectra of the yeast-carbon, TiO2 nanoparticles, and the TiO2@yeast-carbon hybrid particles. In Figure 5(a), the yeast-carbon showed a strong absorption in the range from the UV to the visible light, which was similar to the commercial activated carbon [37]. In Figure 5(b), the band gap energy (Eg) of nanoparticles TiO2 is estimated about 3.2 ev [38], corresponding to a threshold wavelength of 376 nm. In comparison with the nanoparticles TiO2, in Figure 5(c), TiO2@yeast-carbon composites remain optical response in a wide range of 250–400 nm. Besides, in the insert images of Figure 5, the color of the TiO2@yeast-carbon sample was ash black in comparison with the pure white TiO2@yeast precursor, which was consistent with its adsorption spectrum.Figure 5
UV-VIS diffuses reflectance spectra of the yeast-carbon, TiO2 nanoparticles, and the obtained raspberry-like TiO2@yeast-carbon samples ((a) the yeast-carbon, (b) the TiO2 nanoparticles, and (c) the hybrid TiO2@yeast-carbon).


### 3.2. Combined Adsorption and Photocatalytic Degradation of Methylene Blue and Congo Red

The raspberry-like TiO2@yeast-carbon microspheres containing an incompletely covered surface of yeast-carbon may possess unique properties for getting rid of water pollutants. The rich pore structure of yeast-carbon might promote adsorption of organic dyes, while the outer TiO2 nanoparticles can be in charge of the photocatalytic degradation of the dyes [39]. That is to say that immobilizing TiO2 nanoparticles on adsorbent-like yeast-carbon can result in a synergistic effect on the efficient degradation of dye in the photocatalytic process. Specially, yeast-carbon core has the capability to extend the separation lifetime of photogenerated e−/h+ from outer TiO2 nanoparticles [40] and thus increasing the quantum efficiency of TiO2. In turn, TiO2 nanoparticles can destroy dyes by photocatalytic oxidation, thus regenerating the yeast-carbon in situ. In order to test the activity of the composite TiO2@yeast-carbon catalysts, the photocatalytic experiments were carried out for the degradation of MB and CR aqueous solution widely used as model compound for photocatalytic nanomaterial standardization.From the results shown in Figure6, the MB and CR aqueous solution is barely photolyzed by UV light irradiation in Figure 6(a). In Figure 6(b) the adsorption-desorption equilibrium was set up within 50.0 min dark environment. The adsorption capacity of the TiO2@yeast-carbon microspheres for MB was higher than that for CR, which can be assigned to the negatively charged surface of the catalyst. Hereafter, the experiments of the removal of dyes in aqueous solution were preceded for about 120.0 min under UV light irradiation. During 50.0~140.0 minutes, only the adsorption procedures of MB and CR dyes onto the yeast-carbon continuously occurred in the yeast-carbon suspension in Figure 6(b). In the presence of the TiO2@yeast-carbon catalysts, the adsorption and photocatalysis occurred simultaneously in Figure 6(c). Thus, the degradation rate of the dye in the TiO2@yeast-carbon catalyst suspension was significantly higher than that in the yeast-carbon suspension. After 140.0 minutes, the adsorption of dyes onto the yeast-carbon tended to reach the adsorption equilibrium. However, the photocatalytic reactions under UV irradiation still proceeded constantly by TiO2@yeast-carbon catalysts. Finally, approximately 87.0% degradation rate of MB was achieved, whereas only around 30.0% CR was removed from the suspension. The distinct disparity of degradation rate between MB and CR dye aqueous solution can be attributed to their own adsorption performance onto the TiO2@yeast-carbon catalyst.Figure 6
Photocatalytic activities of yeast-carbon and TiO2@yeast-carbon under UV irradiation.The adsorption constant for MB and CRwas listed in Table1. From the results in Table 1, the maximum adsorption amount of the hybrid TiO2@yeast-carbon catalysts for cationic MB was significantly higher than that for anionic CR. In addition, the Langmuir model for MB and CR yields a somewhat better fit than the Freundlich model. The value of 1/n is equal to 0.94 (MB) and (0.13), respectively, which indicates that the adsorption may belong to the favorable adsorption [41]. This prior adsorption of MB than CR dyes on the surface of the TiO2@yeast-carbon microspheres may be assigned to the negatively charged properties of composite catalyst. The discriminatory adsorption for the MB and CR dyes by the TiO2@yeast-carbon composite catalyst inevitably leads to the disparity of above-mentioned photocatalytic degradation rate. Therefore, the adsorption behavior on the surface of the TiO2@yeast-carbon microspheres has a direct impact on the photocatalytic degradation of the MB and CR dyes.Table 1
Comparison of the adsorption constant for MB and CR.
Dyes
C
0 (mg/L)
q
e  (mg/g)
Langmuir isotherm
Freundlich isotherm
C
e
/
q
e
=
(
1
/
Q
0
b
)
+
(
1
/
Q
0
)
C
e
ln
q
e
=
ln
K
F
+
(
1
/
n
)
ln
C
e
Q
0 (mg/g)
b (1/mg)
R
2
K
F
[
(
mg
/
g
)
(
(
1
/
mg
)
1
/
n
)
]
1/n
R
2
MB
1.00
0.23
1.53
1.25
0.99
0.78
0.94
0.83
2.00
0.56
3.00
0.87
4.00
1.17
5.00
1.18
CR
3.00
0.12
1.15
0.33
0.98
0.39
0.13
0.82
5.00
0.34
7.00
0.59
9.00
0.74
11.00
0.75


## 3.1. Materials Characterization

The shape and structure of the samples are shown in Figure1. The SEM image in Figure 1(a) shows that the prime yeast cells have a regular ellipsoidal shape with a diameter varying between 2.6 and 3.7 μm. Figure 1(b) shows an image of the precursor of TiO2@yeast-carbon. Compared with the bared yeast, the size of the TiO2@yeast (length=3.7±0.4μm; width=2.6±0.5μm) was gently increased due to the attachment of TiO2 nanoparticles. The picture in Figure 1(d) shows an overall image of the TiO2@yeast-carbon microspheres. The particles maintained the shape of the original precursor and had the average diameter (length=3.7±0.3μm; width=2.5±0.5μm). Further, higher resolution image in Figure 1(f) shows that the nano-sized TiO2 particles randomly decorated the surface of yeast spheres, which have the morphology of raspberry-like composites. Similar morphology has been reported for the synthesis of the raspberry-like PMMA/SiO2 hybrid microspheres [21]. Moreover, the nanoparticles TiO2 were relatively dispersed on the yeast-carbon in comparison with the agglomerated TiO2 in the TiO2/spherical activated carbons composed by Oh et al. [22]. In addition, the raspberry-like morphology of the TiO2@yeast-carbon microspheres can be confirmed through the EDS analysis. In the insert image in Figure 1(f), the sample contained Ti, C, O, S, and P; no other impurity element is detected, confirming that the TiO2 particles were coated on the surface of the yeast-carbon. By comparing the TiO2@yeast precursor with the TiO2@yeast-carbon product, it can be seen that the color of particles changed from pure white to ash black. Thus, it can be inferred that the carbonization of the yeast occurred in the pyrolysis process. In this respect, the control experiments of the yeast-carbon without the attachment of nanoparticles TiO2 have been conducted under the same conditions. The image of yeast-carbon in Figure 1(c) indicates that the yeast-carbon with an average diameter (length=3.5±0.4μm;  width=2.3±0.50μm) has smooth surface morphology and rich pore structure, which contrasts with the morphology of yeast-carbon synthesized by Shen et al. [23] in which a relatively high distribution of broken shells was observed.SEM images of (a) the naked yeast, (b) general observation of the raspberry-like TiO2@yeast precursor, (c) the yeast-carbon, (d) the overall view of the raspberry-like TiO2@yeast-carbon microspheres, (e) the selected raspberry-like TiO2@yeast-carbon microspheres, and (f) typical raspberry-like TiO2@yeast-carbon microspheres observed under high magnification.
(a)
(b)
(c)
(d)
(e)
(f)XRD patterns of yeast, yeast-carbon, TiO2@yeast-carbon, and TiO2 are displayed in Figure 2. The broad peak around 2θ = 20° indicates that the yeast carbon (in Figure 2(a)) and the yeast (in Figure 2(b)) can be assigned to amorphous species. In Figures 2(c) and 2(d) display the XRD patterns of the hybrid TiO2@yeast-carbon. The broad peaks centering at 2θ = 25°, 37°, 48°, 55°, and 63° are assigned to anatase-type TiO2 (JCPDS. No: 21-1272) [24]. Other diffraction peaks are in good agreement with diffraction peaks of rutile-type TiO2 (JCPDS. No: 21-1276) [25]. The relative intensity of diffraction peaks of TiO2@yeast carbon is approximately identical with the original components of the TiO2 as guest particles (P25TiO2: 78% anatase-type TiO2 and 22% rutile-type TiO2). The broad peaks at 2θ = 20° in the Figures 2(c) and 2(d) are mainly caused by the amorphous structure of yeast-carbon.Figure 2
XRD patterns of (a) the prepared yeast-carbon, (b) the premier yeast, (c) the  80% of TiO2@yeast-carbon, (d) the 40% of TiO2@yeast-carbon, and (e) the pure TiO2.In Figure3, the distinct decrease in weight of the bare yeast is shown during a wide temperature range of 280–600°C. The rapid weight loss of approximately 50.0% at the temperature range of 280–370°C may be associated with the split of the polysaccharide chains in the yeast [26, 27], which is accompanied by a broad exothermal peak at about 370°C in the DTA curve. The ultimate weight loss from 400 to 600°C can be resulted from the cross-linking of oligosaccharides [28] in the yeast, which is accompanied by the endothermic peak at 500°C in the DTA curve. The total weight loss reaches to about 30.0% and the last weight of the residual ashes is approximately 70.0% of the original yeast biomass. In comparison with the naked yeast, the carbonization reaction of the TiO2@yeast precursor was started at temperatures about 250°C. The broad exothermal peak at around 200–300°C may be related to the carbonized decomposition of organic substrate in the yeast along with the rapid weight loss of 50.0%. It is worth noting that the broader exothermal peak appeared at around 300–450°C. This may be caused by the release of constitution water and further crystallization of TiO2 [29]. The wider exothermal peak at 450–600°C can be ascribed to the crystal shift from anatase to rutile phase.Figure 3
TGA-DTA curves of the yeast and the TiO2@yeast-carbon.After pyrolysis entirely, the raspberry-like TiO2@yeast-carbon microspheres can be attained, which has been proved by SEM analysis. The connection between the guest particles TiO2 and the host particles of the yeast-carbon can be elaborated further by FT-IR analysis. FT-IR spectra of the yeast, yeast-carbon, TiO2@yeast precursor, TiO2 and TiO2@yeast-carbon composites are presented in Figure 4, respectively. For the yeast-carbon, the band around 1570 cm−1 can be ascribed to –C=C– stretching bond originated from the inherent structure of yeast, and the bands at 1704 and 1210 cm−1 correspond to C=O, C–O stretching of carboxyl groups, respectively [30]. As for TiO2@yeast-carbon composites, the broad and intense peak at 3500–3200 cm−1 can be assigned to the stretching of –OH group due to the bound water in the TiO2@yeast-carbon composites [31, 32]. The stretching bond corresponding to skeletal Ti–O–Ti is clearly represented in the region of 509 cm−1. The band at 1171 cm−1 suggests the presence of C–O bond [33].  The band at around 620 cm−1 can be attributed to the Ti–O–C vibration, which indicates that TiO2 nanoparticles were chemically bonded with yeast-carbon in hybrid particles [34]. Moreover, the band at 3350 cm−1 is more prominent in TiO2@yeast-carbon composites than that of TiO2, indicating that there were more hydroxyl groups in the TiO2@yeast-carbon hybrid particles. Generally, more hydroxyl groups lead to generation of more •OH radicals in photocatalysis, which can enhance the photocatalytic activity of TiO2 [35].Figure 4
FT-IR spectrum of (a) the original yeast, (b) the TiO2 nanoparticle, (c) the TiO2@yeast precursor, (d) the yeast-carbon, (e) the 80% TiO2@yeast-carbon, and (f) the 40% TiO2@yeast-carbon.Based on the characterization discussed above, the following mechanism that appeared in Scheme1 is proposed to account for the formation procedure of the raspberry-like TiO2@yeast-carbon hybrid microspheres. In Scheme 1, the opposite zeta potentials of yeast cells with a positive charge (H+) and the nanoparticles TiO2 with a negative charge (OH−) were adjusted previously by tuning the pH of their own aqueous suspensions. Then the TiO2@yeast hybrid precursor with raspberry-like morphology was obtained once the aforementioned aqueous suspensions were mixed [36]. In the obtained raspberry-like TiO2@yeast precursor, the yeast acted as the host cores and TiO2 as the guest particles. Afterwards, the carbonization of yeast core in the precursors of raspberry-like TiO2@yeast can be fulfilled by a gradual temperature-rise procedure, which can obtain the hybrid TiO2@yeast-carbon composites. TGA-DTA results showed that the final weight loss is approximately 50.0% in the process of carbonization. In the obtained raspberry-like TiO2@yeast-carbon, TiO2 nanoparticles were chemically bonded with yeast-carbon through FT-IR analysis.Scheme 1
Schematic illustration for the formation of the raspberry-like TiO2@yeast-carbon and their synergistic effect in the removal of dyes aqueous solutions.Figure5 shows the UV-VIS diffuse reflectance spectra of the yeast-carbon, TiO2 nanoparticles, and the TiO2@yeast-carbon hybrid particles. In Figure 5(a), the yeast-carbon showed a strong absorption in the range from the UV to the visible light, which was similar to the commercial activated carbon [37]. In Figure 5(b), the band gap energy (Eg) of nanoparticles TiO2 is estimated about 3.2 ev [38], corresponding to a threshold wavelength of 376 nm. In comparison with the nanoparticles TiO2, in Figure 5(c), TiO2@yeast-carbon composites remain optical response in a wide range of 250–400 nm. Besides, in the insert images of Figure 5, the color of the TiO2@yeast-carbon sample was ash black in comparison with the pure white TiO2@yeast precursor, which was consistent with its adsorption spectrum.Figure 5
UV-VIS diffuses reflectance spectra of the yeast-carbon, TiO2 nanoparticles, and the obtained raspberry-like TiO2@yeast-carbon samples ((a) the yeast-carbon, (b) the TiO2 nanoparticles, and (c) the hybrid TiO2@yeast-carbon).


## 3.2. Combined Adsorption and Photocatalytic Degradation of Methylene Blue and Congo Red

The raspberry-like TiO2@yeast-carbon microspheres containing an incompletely covered surface of yeast-carbon may possess unique properties for getting rid of water pollutants. The rich pore structure of yeast-carbon might promote adsorption of organic dyes, while the outer TiO2 nanoparticles can be in charge of the photocatalytic degradation of the dyes [39]. That is to say that immobilizing TiO2 nanoparticles on adsorbent-like yeast-carbon can result in a synergistic effect on the efficient degradation of dye in the photocatalytic process. Specially, yeast-carbon core has the capability to extend the separation lifetime of photogenerated e−/h+ from outer TiO2 nanoparticles [40] and thus increasing the quantum efficiency of TiO2. In turn, TiO2 nanoparticles can destroy dyes by photocatalytic oxidation, thus regenerating the yeast-carbon in situ. In order to test the activity of the composite TiO2@yeast-carbon catalysts, the photocatalytic experiments were carried out for the degradation of MB and CR aqueous solution widely used as model compound for photocatalytic nanomaterial standardization.From the results shown in Figure6, the MB and CR aqueous solution is barely photolyzed by UV light irradiation in Figure 6(a). In Figure 6(b) the adsorption-desorption equilibrium was set up within 50.0 min dark environment. The adsorption capacity of the TiO2@yeast-carbon microspheres for MB was higher than that for CR, which can be assigned to the negatively charged surface of the catalyst. Hereafter, the experiments of the removal of dyes in aqueous solution were preceded for about 120.0 min under UV light irradiation. During 50.0~140.0 minutes, only the adsorption procedures of MB and CR dyes onto the yeast-carbon continuously occurred in the yeast-carbon suspension in Figure 6(b). In the presence of the TiO2@yeast-carbon catalysts, the adsorption and photocatalysis occurred simultaneously in Figure 6(c). Thus, the degradation rate of the dye in the TiO2@yeast-carbon catalyst suspension was significantly higher than that in the yeast-carbon suspension. After 140.0 minutes, the adsorption of dyes onto the yeast-carbon tended to reach the adsorption equilibrium. However, the photocatalytic reactions under UV irradiation still proceeded constantly by TiO2@yeast-carbon catalysts. Finally, approximately 87.0% degradation rate of MB was achieved, whereas only around 30.0% CR was removed from the suspension. The distinct disparity of degradation rate between MB and CR dye aqueous solution can be attributed to their own adsorption performance onto the TiO2@yeast-carbon catalyst.Figure 6
Photocatalytic activities of yeast-carbon and TiO2@yeast-carbon under UV irradiation.The adsorption constant for MB and CRwas listed in Table1. From the results in Table 1, the maximum adsorption amount of the hybrid TiO2@yeast-carbon catalysts for cationic MB was significantly higher than that for anionic CR. In addition, the Langmuir model for MB and CR yields a somewhat better fit than the Freundlich model. The value of 1/n is equal to 0.94 (MB) and (0.13), respectively, which indicates that the adsorption may belong to the favorable adsorption [41]. This prior adsorption of MB than CR dyes on the surface of the TiO2@yeast-carbon microspheres may be assigned to the negatively charged properties of composite catalyst. The discriminatory adsorption for the MB and CR dyes by the TiO2@yeast-carbon composite catalyst inevitably leads to the disparity of above-mentioned photocatalytic degradation rate. Therefore, the adsorption behavior on the surface of the TiO2@yeast-carbon microspheres has a direct impact on the photocatalytic degradation of the MB and CR dyes.Table 1
Comparison of the adsorption constant for MB and CR.
Dyes
C
0 (mg/L)
q
e  (mg/g)
Langmuir isotherm
Freundlich isotherm
C
e
/
q
e
=
(
1
/
Q
0
b
)
+
(
1
/
Q
0
)
C
e
ln
q
e
=
ln
K
F
+
(
1
/
n
)
ln
C
e
Q
0 (mg/g)
b (1/mg)
R
2
K
F
[
(
mg
/
g
)
(
(
1
/
mg
)
1
/
n
)
]
1/n
R
2
MB
1.00
0.23
1.53
1.25
0.99
0.78
0.94
0.83
2.00
0.56
3.00
0.87
4.00
1.17
5.00
1.18
CR
3.00
0.12
1.15
0.33
0.98
0.39
0.13
0.82
5.00
0.34
7.00
0.59
9.00
0.74
11.00
0.75


## 4. Conclusions

In summary, we prepared hybrid raspberry-like TiO2@yeast-carbon utilizing pyrolysis method. The as-synthesized hybrid TiO2@yeast-carbon had ordered elliptic shapes of uniform size (length=3.7±0.3μm;width=2.5±0.5μm). The potential applications of these novel composites for the removal of contaminants were ascertained for the removal of MB and CR. The results showed that the hybrid composites exhibited excellent photocatalytic activity for the MB due to its enhanced adsorption ability. The novel TiO2@yeast-carbon hybrid microspheres have potential applications not only in polluted water treatment but also in other areas such as sensors devices and dye sensitized solar cells.



---

*Source: 851417-2013-10-10.xml*