# One-Step Synthesis of Copper and Cupric Oxide Particles from the Liquid Phase by X-Ray Radiolysis Using Synchrotron Radiation

Authors: Akinobu Yamaguchi; Ikuo Okada; Takao Fukuoka; Mari Ishihara; Ikuya Sakurai; Yuichi Utsumi
Journal: Journal of Nanomaterials
 (2016)

---

## Abstract

The deposition of copper (Cu) and cupric oxide (Cu4O3, Cu2O, and CuO) particles in an aqueous copper sulfate (CuSO4) solution with additive alcohol such as methanol, ethanol, 2-propanol, and ethylene glycol has been studied by X-ray exposure from synchrotron radiation. An attenuated X-ray radiation time of 5 min allows for the synthesis of Cu, Cu4O3, Cu2O, and CuO nano/microscale particles and their aggregation into clusters. The morphology and composition of the synthesized Cu/cupric oxide particle clusters were characterized by scanning electron microscopy, scanning transmission electron microscopy, and high-resolution transmission electron microscopy with energy dispersive X-ray spectroscopy. Micro-Raman spectroscopy revealed that the clusters comprised cupric oxide core particles covered with Cu particles. Neither Cu/cupric oxide particles nor their clusters were formed without any alcohol additives. The effect of alcohol additives is attributed to the following sequential steps: photochemical reaction due to X-ray irradiation induces nucleation of the particles accompanying redox reaction and forms a cluster or aggregates by LaMer process and DLVO interactions. The procedure offers a novel route to synthesize the Cu/cupric oxide particles and aggregates. It also provides a novel additive manufacturing process or lithography of composite materials such as metal, oxide, and resin.


---

## Body

## 1. Introduction

Nanoparticles (NPs), of which sizes are in general below 100 nm, are potentially interesting for applications such as catalysis and optical devices, and the nucleation and fabrication of NPs are fundamental topics of scientific and engineering studies [1–5]. The optical properties of noble metal NPs have attracted considerable attention because these NPs exhibit extremely high absorption and scattering cross sections due to surface plasmon resonance. Metal NPs are currently synthesized by many methods such as sonochemical reaction [6–13], chemical aqueous reduction of metal ions [14–16], microwave-assisted synthesis [17], and UV-visible light or laser-induced photochemical reaction [18–23]. In these studies, the polyol reaction [24–28] plays a significant important role in NP synthesis. Recently, X-ray irradiation has also been used to generate NPs from liquid solution and tailor NP aggregation at desired locations [29–36]. To this end, noble metal NPs are typically used for surface enhanced Raman scattering spectroscopy (SERS) and plasmon-assisted photochemical reactions [1–4, 37]. Potential applications of NPs in a nanoscale material processing have been demonstrated in various fields such as catalysis, medicine, electronics, ceramics, pigments, and cosmetics [1–5].Recently, copper (Cu) and copper oxide-nanostructured materials have attracted considerable attention due to their fundamental importance and potential future applications [38–54]. Cupric oxide (Cu2O, CuO) NPs are p-type semiconductor materials with a low band-gap energies. Recently, Poizot et al. [40] used cupric oxide NPs as anodes for lithium ion cells. Izaki et al. [47] produced solar cell plates consisting of Cu2O and ZnO NPs. In addition, the cupric oxide NPs have sufficient space to absorb harmful gases. Zhang et al. demonstrated the application of copper oxide NPs as a gas sensor [51]. Thus, copper oxide NPs have additional noteworthy properties, such as nontoxicity, environmental friendliness, high stability, and recyclability. Many reports have provided methods to synthesize and characterize cupric oxide (Cu2O, CuO) NPs [38–54]. For example, CuO NPs were prepared by Brookshier et al. using a spin-coating technique to control SiO2 size [54] and Volanti et al. synthesized CuO flower-like nanostructures using a domestic hydrothermal microwave [38]. Clay and Cohen synthesized CuO nanoclusters within films of diblock copolymers [52], whereas Lisiecki and Pileni produced Cu and CuO NPs from inverse micelle solutions [53].Radiolysis using synchrotron radiation (SR) has recently been investigated as a radiation-assisted method for the synthesis of NPs [29–36]. Due to the higher brilliance and controllability of X-ray from SR, the X-ray radiolysis has attracted much attention. To date, the synchrotron X-ray synthesis of Au, Fe, Ni, and AuPt alloyed NPs has been reported [29–36]. Thus, the syntheses of various metallic NPs by X-ray irradiation have been investigated. A few studies have reported the synthesis of Cu, Cu2O, Cu4O3, and CuO materials using X-ray irradiation from SR. Recently, Oyanagi et al. [55] and Yamaguchi et al. [56] succeeded in producing Cu particles by exposing diverse copper solutions. Oyanagi et al. [55] used Cu(II) bis(1,1,1,5,5,5-hexafluoro-2,4,pentanedionate) solution with benzopinacol C26H22O2, octylamine C8H19N and diethylene glycol diethyl ether, while Yamaguchi et al. [56] succeeded in producing Cu NPs by exposing copper sulfate (CuSO4) liquid solution mixed with ethanol to X-rays. In the previous study, we simply demonstrated the synthesis of Cu NPs without any detailed analysis. Investigating the formation of Cu and cupric oxide NPs is required to understand the physical and chemical mechanisms and to develop engineering applications such as lithium ion cells [51], gas sensors [57], and solar cell plates [58].In this paper, synchrotron X-ray radiation is used to synthesize cupric oxide and Cu particles from cupric sulfate solutions containing methanol, ethanol, 2-propanol, and ethylene glycol. Here, we investigate additive alcohol type dependence of cupric particles synthesized by X-ray irradiation. High-resolution scanning electron microscope (SEM), scanning transmission electron microscope (STEM), and high-resolution transmission electron microscope (HRTEM) image with energy dispersive X-ray spectroscopy (EDX) are used to obtain a deeper understanding of the formation mechanism. We also employ microscopic Raman spectroscopy to characterize the cupric particles obtained by X-ray irradiation.


## 2. Experimental

The stock solution was prepared by dissolving 18.6 g of CuSO4·5H2O (Wako Chemical, 99.99%) in 100 mL of doubly distilled water. A 100 mL aliquot of 10% CuSO4 aqueous solution (solution #1) was prepared by diluting the stock solution. We siphoned off 200 μL 10% CuSO4 aqueous solution into a microtube and added 10 μL ethanol to obtain the mixed solution (solution #3). In the similar way, other additives such as methanol (solution #2) and 2-propanol (solution #4) were also added into 10% CuSO4 aqueous solution. In the case of X-ray irradiation experiment with ethylene glycol, the mix ratio of CuSO4 solution and ethylene glycol is 500 μL to 0.5 μL (solution #5). We took off 18 μL of the mixed solution (including the CuSO4 and ethanol) and added it into the X-ray irradiation system. The prepared solutions for X-ray irradiation experiments are summarized in Table 1.Table 1
Summary of solutions prepared for X-ray irradiation experiments.
Prepared solution (18μL siphoned off from the mixed solution) Base solution & amount Additive material & amount Solution #1 10% CuSO4 solution200 μL — Solution #2 10% CuSO4 solution200 μL Methanol (CH3COH)10 μL Solution #3 10% CuSO4 solution200 μL Ethanol (CH3CH2OH)10 μL Solution #4 10% CuSO4 solution200 μL 2-Propanol (CH3CH(CH3)OH)10 μL Solution #5 10% CuSO4 solution500 μL Ethylene glycol(HOCH2CH2OH)0.5 μLThe particles deposition experiments using the SR were performed on BL8S1 at the Aichi Synchrotron Radiation Center (Aichi SRC). The experimental setup is schematically shown in Figure1 [36, 56]. The X-ray spectra evaluated by the calculation are also shown in the inset of Figure 1(a). As described in the previous work [36, 56], a silicon substrate (10 × 10 × 0.5 mm3) was dipped into the solution prepared as shown in Table 1 (total amount of 18 μL). The Si substrate dipped in the solution was sealed by a 2 μm thick SiN membrane and polytetrafluoroethylene (PTFE) plates as shown in Figure 1(a). The sealed package including Si substrate dipped in the solution was fixed by the special steel used stainless (SUS) holder as schematically illustrated in Figure 1(a). In addition, a filtered patterned X-ray mask made of SUS was attached on the SUS holder to obtain the contrast by X-ray irradiation. The use of the X-ray mask allows us to easily get more, about tenfold, difference of the photon number in an area directly irradiated by X-ray with respect to the area covered with the X-ray mask, as shown in the spectra of Figure 1(a). The X-ray mask has some hole-arrays with various size through-holes. We chose the hole-array consisting of through-hole with diameter of 300 μm. The specimen prepared for the X-ray irradiation was placed on the irradiation system. After exposure to synchrotron X-rays, we washed the specimen using deionization water to remove residual dross except particles. The particles synthesized onto the silicon substrate were observed by field emission scanning electron microscopy (FE-SEM; JEOL JSM-7001F) with EDX to perform the element analysis. To prepare the cross-sectional sample for transmission electron microscope (TEM) observation, we fixed the sample on TEM observation grid consisting of Al and Mo using a resin. A focused ion beam (FIB) was used to expose the cross-sectional surface of the sample to observe the TEM image. We obtained the cross-sectional images and elemental maps of the synthesized particles using TEM (JEOL JEM-2100F) with EDX (JEOL, JED-2300T & Gatan, GIF Quantum ER). Micro-Raman measurements (JASCO, NRS-5100) were performed using the 532 nm wavelength as the excitation source. The power was maintained at 3.2 mW, and a field lens with a magnification of 100x was used. The diameter of the laser spot is about 1 μm. All experiments were performed at room temperature and in the atmosphere.Figure 1
(a) Schematic of experimental setup for the X-ray irradiation of liquid solution. The inset shows X-ray spectra. The evaluated photon intensity obtained from (A): synchrotron radiation at BL8S1 of Aichi SRC, (B): Pt mirror (incident angle: 0.2°), (C): 400μm thick Be film, (D): 500 μm thick Al film, (E): metallic solution through air (1 m distance), and (F): 180 μm thick steel used stainless (SUS) mask. (b) Photograph of specimen with the SUS mask.
(a) (b)


## 3. Results and Discussion

When the silicon substrate with only CuSO4 solution with no additives (solution #1) was exposed to X-rays, no particles were synthesized; particles and clusters were only generated in the presence of ethanol (solution #3). Figure 2 shows the SEM image after a 10% CuSO4 containing ethanol (solution #3) was irradiated with X-rays for 5 min. Here, the X-ray was attenuated by 500 μm thick Al foil as shown in Figure 1 [36, 56]. As shown in Figure 2(a), a slit pattern is well defined. When magnified, the slit patterns were found to contain particles. The magnified SEM images of small particles and aggregates are represented in Figures 2(b)–2(d), showing that they are not detached from the Si substrate even after washing because of strong van der Waals interaction.Figure 2
(a) SEM image of a well-patterned CuSO4 solution with ethanol (solution #3) after X-ray irradiation for 5 min. The dashed circle and arrows correspond to the slit patterned areas. (b) Magnified SEM image of Cu particles nucleated from the mixed solution under X-ray irradiation. ((c) and (d)) High-resolution SEM images of the nucleated particles. The arrow in (c) points out a cuboctahedral like particle.
(a) (b) (c) (d)To confirm the composition of the synthesized particles, elementary analysis was carried out by EDX. The inset of the magnified SEM image in Figure3(a) represents that the positions at which EDX are measured. The red squares correspond to the areas measured by EDX. Signals of elements C, Cu, and Si are observed in the spectra in Figures 3(a) and 3(c), while an enlarged signal of O is seen in Figure 3(b). The Cu/O ratios in Figures 3(a)–3(c) are roughly estimated to be about 9/0.5, 7/2, and 9/0.5, respectively. Here, the EDX peak of Si is derived from the silicon substrate because the synthesized particles are small enough to pick up the Si elementary information as the background signal. As a result, these spectra suggest that the core particle is different from the additional particles which attach on it. Carbon (C) is in the all particles, while sulfur (S) is not included in them. C is considered to be derived from contamination or the additive ethanol. C from ethanol is expected to play an important role in the nucleation process, in which the added ethanol facilitates the redox reaction and nucleates the Cu and cupric oxide particles [38].Figure 3
In the inset of (a), three red squared frames (i), (ii), and (iii) on the high-resolution SEM image of the particle depict the EDX measurement positions. EDX spectra measured from the positions (i), (ii), and (iii) are shown in (a), (b), and (c), respectively. The position (ii) corresponds to the surface of the core particle, while the positions (i) and (iii) are the surfaces of attached particles.To investigate the morphology and composition, STEM was performed and elemental maps were collected using EDX. Figure4(a) shows the EDX spectrum of the cross-sectional area of a cluster generated by X-ray irradiation in the liquid solution shown in Figure 4(b), which is the STEM image. The spectra includes necessary elemental information along with nonessential signals derived from the TEM grid mount materials (C, Al, Si, and Mo) and a Ga signal from the focused ion beam (FIB) milling process. In this manuscript, except the carbon C, elementary maps of Al, Mo, and Ga are not shown to avoid cumbersome maps of which provide nonessential phenomena. Figures 4(c)–4(f) show the elementary maps of Cu, O, Si, and C, respectively; the bright and dark contrasts correspond to high and low elemental abundance, respectively. Note that the elements Si and C remained from the polishing agent slurry and mold resin, respectively, after FIB milling. Thus, both elements reside around the particles near the TEM grid frame, as shown in Figures 4(e) and 4(f). This cross-sectional TEM elementary mapping indicates that all synthesized particles are at least including Cu as shown in Figure 4(c) and the element C does not play an important role in the ripping process of the particles. By comparison with Figures 4(c) and 4(d), the amount of oxygen (O) is higher included in the core particle, while oxygen distribution is barely visible in the small particles attached on the core particle (Figure 4(d)). One can see the single crystalline-like structure in all synthesized particles, because we recognized the several facets in morphology observation using TEM and SEM.Figure 4
(a) EDX spectrum of the observed cross-sectional area shown in secondary-electron topographical TEM image of (b). (c)–(f) Elemental mappings of Cu, O, Si, and C, respectively.
(a) (b) (c) (d) (e) (f)To understand the details of the elementary distributions in the synthesized particles, the magnified STEM images and EDX mappings are shown in Figure5. Figure 5(a) shows the topographical STEM image of the cross section of the aggregate. Figures 5(b) and 5(c) show the EDX elementary mappings of Cu (red-colored) and O (orange-colored), respectively. The elemental mappings clearly show anisotropic distributions of Cu and O. O is almost detected in the original single crystalline core region, whereas Cu is mainly found in all particles, similarly to the results shown in Figures 4 and 5.Figure 5
(a) High-resolution TEM topographical image of the aggregate cross section. ((b) and (c)) Elementary mappings of Cu and O, respectively.
(a) (b) (c)Furthermore, we collected the micro-Raman spectra in order to reveal crystallographic information. The photograph insets of Figure6 show the respective aggregates consisting some particles. The labels (A), (C), and (D) correspond to the measurement positions of micro-Raman spectroscopies. The bright green positions correspond to the areas irradiated by the excitation laser. Figures 6(a)–6(d) show the micro-Raman spectra of (a) surface of metallic particle, (b) silicon substrate, (c) surface of core particle, and (d) particle on the core particle, respectively. The micro-Raman spectrometer is so sensitive that it can pick up the information at focal depth of about 500 nm. As shown in Figures 6(a) and 6(d), the broad spectra are observed, indicating that the particles attaching on core particle are metal and are deduced that the nucleation, growth, or aggregate of Cu particles occurred.Figure 6
(a) Micro-Raman spectrum of the particle attached on the core particle. The optical image of a typical aggregate is shown in the inset of (b). The green portion of the inset photograph shown in (B) shows the position irradiated by the green laser (wavelength = 532 nm). Micro-Raman spectra of (b) the Si substrate, (c) core and particle attached on the core particle, and (d) other particles, respectively. Indexes were taken from the following Raman spectrum patterns: Cu2O, CuO, and Cu4O3 [38, 39].
(a) (b) (c) (d)Next, we focus on the spectrum of Figure6(c). The peaks at 277, 324, 520, and 613 cm−1 appeared clearly in Figure 6(c). These peaks are possibly attributed to summation of three cupric oxides: Cu2O, CuO, and Cu4O3 [38, 39]. Although a comparison of Raman spectra shown in Figures 6(a), 6(c), and 6(d) with that of the Si substrate in Figure 6(b) indicates that the peak at 520 cm−1 is attributed to the Si substrate, there remains the undeniable possibility that the peak at 520 cm−1 is derived from A1g mode of Cu4O3 because the particle volume is thick enough to shade the excitation laser reaching Si substrate. Accordingly to the previous studies of Debbichi et al. [39] and Volanti et al. [38], our observed Raman signals at 277, 324, and 613 cm−1 from the core particle correspond to Raman signals from Ag (283.8 cm−1) and Bg (333.5 and 622.5 cm−1) modes of CuO, respectively [38, 39]. In this study, the corresponding Raman shifts are a little bit lower than those reported in [40, 41]. As shown in the inset photograph of Figure 6(d) after the measurement of Raman spectra, the particles that the laser had been focused on were slightly melted. It is attributed that a red shift was induced by the heating effect from laser excitation. In addition, we understand the potential of the broad Raman peak structure ranging from 500 to 630 cm−1 being originated from Cu2O [38, 39]. The result may be explainable for Cu/O (at %) ratios of the aggregates by comparing with EDX measurements; however, in the present stage, it allows us to deduce that the synthesized particle is expected to be a composited cupric oxide consisting of CuO, Cu2O, and Cu4O3, while some particles attached to the core particle were deduced to be Cu particles. Thus, in either case, we demonstrated one-step synthesis of Cu/cupric oxide and the aggregates induced from the liquid solution by direct X-ray irradiation.Various investigations were performed to understand the mechanism of particle formation based on the interaction of sonochemical preparation [6–13], laser light [18–23], microwave irradiation [14–17, 38, 39, 41–51], and X-ray and γ-ray irradiation (radiolysis) [29–36, 55, 56]. For photochemical reactions, both thermal and electronic excitation effects were considered and discussed. To our knowledge, no report has discussed the particle formation mechanism from CuSO4 solution under X-ray irradiation. Therefore, we have attempted to understand the phenomenological chemical reaction process.In our experiment, hydrated electrons, hydroxyl radicals, and hydrogen atoms were the reactive intermediates in the X-ray irradiation of the mixed aqueous solution. As described in previous studies, the X-ray irradiation from SR provides the proton radical and hydroxyl radical as the following [59–65]:(1)H2O→X-rayeaq-,H∙,OH∙,H2O2,H2As described above, in this study, the X-ray irradiation of only CuSO4 solution (without ethanol) did not result in the formation of any particles. This is because the proton and hydroxyl radicals provided by X-ray irradiation are not sufficient to form copper particles via reduction due to the hydration.Upon the addition of an alcohol (e.g., methanol and ethanol), theOH∙ and H∙ radicals are scavenged to yield reducing organic radicals. In the case where ethanol is added to the solution, proton and hydroxyl radicals react as follows [59–65]:(2a)OH∙H∙+CH3CH2OH⟶H2OH2+CH2OH∙(2b)CH3CH2OH→X-rayCH3CHO+2e-+2H+(2c)CH3CH2OHn→X-rayCH3CH2OHn+∗+e-(2d)CH3CH2OHn→X-rayCH3CH2OHn-1H++CH3CHO+e-The several candidates of associated reactions are taking place in the mixed solution under the X-ray irradiation, as follows [58, 63–65]:(3a)Cu2++2e-⟶Cu0(3b)Cu2++2CH3CHO+2OH-⟶Cu0+2CH3COOH+H2(3c)Cu2++2OH-⟶CuOH2(3d)CuOH2⟶CuO+H2O(3e)CuOH2+Cu⟶Cu2O+H2O(3f)2CuO+Cu2O⟶Cu4O3Here, the CuO, Cu2O, Cu4O3, and Cu particles are finally reduced and deposited onto the silicon substrate and SiN membrane.Here, we can obtain cubic, cuboctahedral, and octahedral particles as shown in Figure2. The nucleation and growth process can be basically explained by LaMer model [66] and the aggregation mechanism derived from the Derjaguin, Landau, Verwey, and Overbeek (DLVO) model [67, 68]. In addition, for the silicon substrate, the H-terminated Si substrate produced during the X-ray irradiation may play an important role in particle synthesis, as described in [46].To investigate the functional group dependence of particle synthesis initiated by X-ray radiolysis, we added methanol, 2-propanol, or ethylene glycol to 10% CuSO4 solution. The concentration of the additives of methanol and 2-propanol was the same as the case of X-ray irradiation with ethanol. The mixture ratio of the 10% CuSO4 solution and ethylene glycol was 500 μL to 0.5 μL (solution #5), while the ratio of the others (methanol, ethanol, and 2-propanol) was 200 μL to 10 μL. As a result, the synthesis of particles is confirmed. The SEM images and EDX spectra and micro-Raman spectra of morphologies of particles and surface of Si substrate after X-ray irradiation of CuSO4 solution with methanol, 2-propanol, and ethylene glycol are shown in Figures 7–9, 10–12, and 13–15, respectively. We found that the single crystalline like particles and their aggregates are also formed in the cases of additive methanol, 2-propanol, and ethylene glycol, respectively. In addition, the dappling surfaces, where the bright and dark contrasts are randomly distributed in Figures 10 and 13, on irradiated area appear in the both cases of X-ray irradiation under the application of 2-propanol and ethylene glycol. According to the EDX analysis (not shown here), the dappled shade area is consisting of Si. This result indicates that dips are formed in the dappled shade area by etching process of Si due to X-ray radiolysis with 2-propanol and ethylene glycol.Figure 7
(a) SEM image of a well-patterned CuSO4 solution with added methanol (solution #2) after X-ray irradiation for 5 min. (b) Magnified SEM image of Cu NPs nucleated from the mixed solution under X-ray irradiation. ((c) and (d)) High-resolution SEM images of the synthesized particles.
(a) (b) (c) (d)Figure 8
EDX spectra of the red squared areas (a) and (b) in the synthesized particles observed in Figures7(c) and 7(d), respectively.
(a) (b)Figure 9
Micro-Raman spectra of the measurement positions (a), (b), and (c) on the particle aggregate synthesized from CuSO4 solution mixed with 2-propanol (solution #4) and Si substrate. The inset photographs display the green laser position on the measurement area. Indexes were taken from the following Raman spectrum patterns: Cu2O, CuO, and Cu4O3 [38, 39].
(a) (b) (c) (d)Figure 10
(a) SEM image of a well-patterned CuSO4 solution mixed with 2-propanol (solution #4) after X-ray irradiation for 5 min. (b) Magnified SEM image of Cu particles nucleated from the mixed solution under X-ray irradiation. ((c) and (d)) High-resolution SEM images of the synthesized particles.
(a) (b) (c) (d)Figure 11
EDX spectrum of the red squared area in the synthesized particles observed in Figure10(d).Figure 12
Micro-Raman spectra of the measurement position on the synthesized particle aggregate. The inset photograph displays the laser spot position on the aggregate. Indexes were taken from the Raman spectrum patterns: Cu2O, CuO, and Cu4O3 [38, 39].Figure 13
(a) SEM image of a well-patterned CuSO4 solution mixed with ethylene glycol (solution #5) after X-ray irradiation for 5 min. (b) Magnified SEM image of Cu particles nucleated from the mixed solution under X-ray irradiation. ((c) and (d)) High-resolution SEM images of the synthesized particles.
(a) (b) (c) (d)Figure 14
EDX spectra of the red squared areas (a) and (b) on the synthesized particles observed in Figure13(d).Figure 15
Micro-Raman spectrum of the particle aggregate synthesized from CuSO4 solution mixed with ethylene glycol (solution #5). The inset photographs display the green laser position on the measurement area. Indexes were taken from the following Raman spectrum patterns: Cu2O, CuO, and Cu4O3 [38, 39].To confirm the composition of the synthesized cupric particles with methanol and 2-propanol, we analyzed the synthesized particles or clusters by EDX spectroscopy, as shown in Figures8 and 11, respectively. By comparison with these spectra, the EDX spectra indicate that the synthesized particles consisted mostly of Cu. Next, the micro-Raman spectra of the aggregate of these particles are shown in Figures 9 and 12. Comparing the spectrum in Figure 9(c) with that in Figure 12, we found the two spectra are almost the same and are educed to be derived from Cu4O3. The spectra shown in Figures 9(a) and 9(b) are similar with Figure 6(c) of the case of particles synthesized from CuSO4 solution with additive ethanol (solution #2). These results indicate that the composition of the particles is almost the same and is expected to be consisting of CuO and Cu2O. The particles attached on the core particles are expected to be Cu particles.Next, we analyzed urchin-like NPs synthesized by X-ray radiolysis with ethylene glycol (solution #5) by EDX spectroscopy. Figure14 indicates that both the outshoot and core consisted of cupric oxide. The outshoot seems to contain a higher proportion of carbon C than the core. The micro-Raman spectra of these particles synthesized from solution with ethylene glycol (solution #5) are shown in Figure 15. Unfortunately, the particles were burned after the micro-Raman spectroscopy was measured as shown in the inset of Figure 15. Comparing the spectrum in Figure 15 with the other spectra depicted in Figures 6, 9, and 12, we found that the obtained spectrum is expected to be derived from the composite consisting of CuO and Cu2O.We investigate the dependence of the deposited particle size on the kinds of additive alcohol. Here, to simplify the estimation of particle size, we evaluated the maximum length of the synthesized particles because their shapes were various and diversified. The probability densities of the particles synthesized from X-ray radiolysis with (a) methanol, (b) ethanol, (c) 2-propanol, and (d) ethylene glycol are plotted on a function of particle length in Figures16(a)–16(d), respectively. The synthesized particles under the X-ray irradiation time of 5 min with various additives are similar in size. The result indicates that the irradiation time of 5 min is long enough to complete the series of nucleation, growth, and aggregation of particles which began and proceeded under the competition of LaMer process [66] and DLVO interaction [67, 68]. Figure 17 shows the dependence of the synthesized particle length on the kinds of alcohol. It seems that the particle length increases with the order: methanol, ethanol, 2-propanol, and ethylene glycol. The trend of synthesis of particles is derived from the radical activity of alcohol, being consistent with the previous studies [65]. On the basis of the high-resolution SEM, TEM, and micro-Raman spectroscopy, we confirmed the synthesis of not only Cu particles but also higher-order aggregates consisting of cupric oxide and copper particles from liquid solution under X-ray irradiation.Figure 16
Probability densities of the particles synthesized CuSO4 mixed with (a) methanol, (b) ethanol, (c) 2-propanol, and (d) ethylene glycol, respectively, revealing the particle length distributions.
(a) (b) (c) (d)Figure 17
Additive alcohol dependence of synthesized particle length. Met., Eth., 2-Pro., and Et.-gly. correspond to methanol, ethanol, 2-propanol, and ethylene glycol, respectively.As cupric oxide and cupper particles are receiving considerable interest due to potential uses as anodes lithium ion cells, gas sensors, and p-type semiconductor materials, this X-ray irradiation method can provide a novel additive manufacturing process [69–71] for the devices and systems such as solar cells and plasmonic sensor in μTAS. In addition, this study sheds light on developing a three-dimensional printing with both metal and resin as a novel Lithographie Galvanoformung Abformung (LIGA) process [72].


## 4. Conclusion

The present work demonstrates that Cu/cupric oxide particles can be obtained by irradiating a CuSO4 solution containing alcohol with SR. The synthesized cubic, cuboctahedral, and octahedral NPs aggregate to form higher-order nano/microstructures. High-resolution SEM, TEM, and micro-Raman spectroscopy analyses demonstrated that the core particles consisted of Cu2O, CuO, and Cu4O3, while the particles attached to the core particles were copper. The additive alcohol helps the copper ions to reduce the copper colloids, cupric oxide particles, and Cu/cupric oxide aggregates. Two potential issues have arisen: (a) the synthetic process including the nucleation and formation of particles from the liquid solution by X-ray irradiation with/without ethanol or other alcohols and (b) the coagulation of the Cu/cupric oxide particles. These issues are worthy of further investigation.The direct X-ray irradiation using an SR source can provide an alternative route to explore the novel physical mechanism of liquid/solid interlayer reaction process from the liquid phase. The higher-order nano/microstructure consisting of metallic particles and metal oxides particles offer an opportunity to conveniently and directly induce catalysis and probe surface enhanced Raman scattering. Particularly, cupric oxide particles have attracted much attention for application of gas sensor and solar cell. This one-step direct deposition process can be used in new devices such as “Lab-on-a-chip” and “μTAS: micron-Total-Analysis-System” applications for chemical and environmental analyses. In addition, the development of this technique combined with the microfluidic chip enables integrating three-dimensional printing which can fabricate micro- or nanoscale structure consisting of metal and resin.



---

*Source: 8584304-2016-12-27.xml*