# Study Structure and Properties of Nanocomposite Material Based on Unsaturated Polyester with Clay Modified by Poly(ethylene oxide)

Authors: Tran Duy Thanh; Nguyen Dang Mao; Nguyen Thi Kim Ngan; Ha Thuc Chi Nhan; Ha Thuc Huy; Anne-Cecile Grillet
Journal: Journal of Nanomaterials
 (2012)

---

## Abstract

In recent years, polymer clay nanocomposites have been attracting considerable interests in polymers science because of their advantages. There are many scientists who researched about this kind of material and demonstrated that when polymer matrix was added to little weight of clay, properties were enhanced considerably. Because clay is a hydrophilic substance so it is difficult to use as filler in polymer matrix having hydrophobic nature, so clay needs to be modified to become compatible with polymer. In this study, poly(ethylene oxide) was used as a new modifier for clay to replace some traditional ionic surfactants such as primary, secondary, tertiary, and quaternary alkyl ammonium or alkylphosphonium cations having the following disadvantages: disintegrate at high temperature, catalyze polymer degradation, and make nanoproducts colorific, and so forth. In order to evaluate modifying effect of poly(ethylene oxide), modified clay products were characterize d by X-ray spectrum. Then organoclay was used to prepare nanocomposite based on unsaturated polyester. Morphology and properties of nanocomposites were measure d by X-ray diffraction, transmission electron microscopy, tensile strength, and thermal stability. The results showed that clay galleries changed to intercalated state in the nanocomposites. Properties of nanocomposites were improved a lot when the loading of the organoclay was used at 1 phr.


---

## Body

## 1. Introduction

Polymer clay nanocomposites (PCNs) are one of the ways for making new materials that frequently exhibit remarkable improvements of material properties to replace traditional products in many applications [1, 2]. The PCNs based on unsaturated polyester and nanoclay (MMT) also have been widely researched by scientists in the world for many years. The results showed that when clay dispersed in the form of exfoliated state or intercalated state, properties of PCNs such as tensile strength, flexural strength,  gas permeability and biodegradability were improved significantly [3–6]. In recent time, the trend using nonion modifiers demonstrated that they had many promising applications in nanocomposite material field [5, 7–12]. So in this study we have tried using poly(ethylene oxide) (PEO) as a new modifier to replace some traditional ionic surfactants such as primary, secondary, tertiary, and  quaternary alkyl ammonium or alkylphosphonium cations having, disadvantages: disintegrate at high temperature, catalyze polymer degradation, and make nanoproducts colorific [13]. Then nanocomposite materials based on Unsaturated Polyester resin (UP) with PEO modified clay were prepared by solution method. The morphology and properties of PCNs were tested through XRD, TEM, mechanical strength, and thermal behavior.


## 2. Experimental Methods

### 2.1. Materials

Poly(ethylene oxide) (PEO),Mn=100.000, used as a non-ion modifier, was provided by Alrich Co., Germany. Commercial unmodified clay under trade name of N757 was from Sud-Chemie Co., Germany. Unsaturated polyester (UP) SHCP 268 BQT having 32% wt of styrene is from Highpolymer Chemical Products Co., Singapore. Wax 8 was supplied by Meguiar Company, USA. And Ethyl Methyl Ketone Peroxide (MEKP) was obtained from AkzoNobel Company.


### 2.2. Experiment

#### 2.2.1. Modify MMT by Melting Method (Isothermal Annealing)

Clay and PEO were used according to two ratios 10 : 3 and 10 : 5. The suitable weights were mixed and grinded finely in one hour to enhance interface area between PEO and clay. Then mixture was annealed at 90°C in 8 hour. During this time, PEO was melted and adsorbed into interlayer structure of clay. The receipted organoclay was stored under vacuum condition in a desiccator.


#### 2.2.2. Modify Clay by Solution Method

Clay and PEO were  dissolved into solvent system water : ethanol and the weight ratio of clay and solvent were about 30 : 1. Solution was stirred at 40°C during 4 hours. After that it was centrifuged and wasted by ethanol. Receipted modified clay was dried at 40°C and then stored under vacuum condition in desiccator.


#### 2.2.3. Preparation of Nanocomposite Materials

Nancomposite materials were prepared based on unsaturated polyester and organoclay at three clay contents 1, 3, and 5 phr (phr: parts per hundred resins). Firstly, UP and organoclay were mixed together in a closed container at 80°C in 6 hour. Then mixture was cooled down to room temperature. 1 phr of MEKP was added into mixture and stirred in one minute. After that solution was poured into the mould placed in a stove at 60°C in 24 hour. Continuously, achieved nanocomposites were taken out and gone through the post-cure process at room temperature in 24 hours to define shape of the samples. Finally, PCNs were processed into suitable size to test structure and properties.


## 2.1. Materials

Poly(ethylene oxide) (PEO),Mn=100.000, used as a non-ion modifier, was provided by Alrich Co., Germany. Commercial unmodified clay under trade name of N757 was from Sud-Chemie Co., Germany. Unsaturated polyester (UP) SHCP 268 BQT having 32% wt of styrene is from Highpolymer Chemical Products Co., Singapore. Wax 8 was supplied by Meguiar Company, USA. And Ethyl Methyl Ketone Peroxide (MEKP) was obtained from AkzoNobel Company.


## 2.2. Experiment

### 2.2.1. Modify MMT by Melting Method (Isothermal Annealing)

Clay and PEO were used according to two ratios 10 : 3 and 10 : 5. The suitable weights were mixed and grinded finely in one hour to enhance interface area between PEO and clay. Then mixture was annealed at 90°C in 8 hour. During this time, PEO was melted and adsorbed into interlayer structure of clay. The receipted organoclay was stored under vacuum condition in a desiccator.


### 2.2.2. Modify Clay by Solution Method

Clay and PEO were  dissolved into solvent system water : ethanol and the weight ratio of clay and solvent were about 30 : 1. Solution was stirred at 40°C during 4 hours. After that it was centrifuged and wasted by ethanol. Receipted modified clay was dried at 40°C and then stored under vacuum condition in desiccator.


### 2.2.3. Preparation of Nanocomposite Materials

Nancomposite materials were prepared based on unsaturated polyester and organoclay at three clay contents 1, 3, and 5 phr (phr: parts per hundred resins). Firstly, UP and organoclay were mixed together in a closed container at 80°C in 6 hour. Then mixture was cooled down to room temperature. 1 phr of MEKP was added into mixture and stirred in one minute. After that solution was poured into the mould placed in a stove at 60°C in 24 hour. Continuously, achieved nanocomposites were taken out and gone through the post-cure process at room temperature in 24 hours to define shape of the samples. Finally, PCNs were processed into suitable size to test structure and properties.


## 2.2.1. Modify MMT by Melting Method (Isothermal Annealing)

Clay and PEO were used according to two ratios 10 : 3 and 10 : 5. The suitable weights were mixed and grinded finely in one hour to enhance interface area between PEO and clay. Then mixture was annealed at 90°C in 8 hour. During this time, PEO was melted and adsorbed into interlayer structure of clay. The receipted organoclay was stored under vacuum condition in a desiccator.


## 2.2.2. Modify Clay by Solution Method

Clay and PEO were  dissolved into solvent system water : ethanol and the weight ratio of clay and solvent were about 30 : 1. Solution was stirred at 40°C during 4 hours. After that it was centrifuged and wasted by ethanol. Receipted modified clay was dried at 40°C and then stored under vacuum condition in desiccator.


## 2.2.3. Preparation of Nanocomposite Materials

Nancomposite materials were prepared based on unsaturated polyester and organoclay at three clay contents 1, 3, and 5 phr (phr: parts per hundred resins). Firstly, UP and organoclay were mixed together in a closed container at 80°C in 6 hour. Then mixture was cooled down to room temperature. 1 phr of MEKP was added into mixture and stirred in one minute. After that solution was poured into the mould placed in a stove at 60°C in 24 hour. Continuously, achieved nanocomposites were taken out and gone through the post-cure process at room temperature in 24 hours to define shape of the samples. Finally, PCNs were processed into suitable size to test structure and properties.


## 3. Results and Discussion

### 3.1. Structure of N757 Modified by PEO

#### 3.1.1. Effect of PEO Contents on Structure of N757

Structure of clays was characterized from X-ray diffractograms of a D8 Advance (Bruker Germany) with Ni-filtered CuKα radiation of wavelength 1.54 Å at 40 kV and 40 mA. Figure 1 shows the XRD pattern of unmodified and modified clay. The original MMT had basal spacing of 12.4 Å. After it was modified by PEO, the peak corresponding to the basal spacing of MMT disappeared and new peaks appeared with d-spacing of 17.9 and 18.2 Å in samples having clay: PEO ratios 10 : 3 and 10 : 5, respectively. However, d-spacing of MMT was not enhanced considerably as the clay: PEO ratios were increased from 10 : 3 to 10 : 5. It is concluded that PEO dispersed into structure of MMT and adsorption gained the saturated value at ratio 10 : 3. That was completely suitable to results researched by author Shen et al. [9].Figure 1
XRD diffraction of N757: (a) virgin N757; N757 modified by PEO at ratios (b) 10/3 and (c) 10/5.


#### 3.1.2. Effect of Modifying Method on Structure of Clay

Figures2(a) and 2(b) show  the XRD patterns of modified clay synthesized by solution and melting method, respectively.Figure 2
XRD diffraction of N757 modified by PEO at ratio 10/3 according two methods: (a) solution method and (b) melting method.At the modified clay: PEO ratio 10 : 3, results display that the melting method was better than solution method. For example, the d-spacing of organoclay modified by isothermal annealing method had stronger intensity and appeared at d-spacing higher than sample from solution method. Besides, melting method (isothermal annealing) was more simple, economic, and easy to process than solution method. So it was a good method to be chosen for modifying MMT by PEO.


### 3.2. Structure and Properties of Nanocomposites Based on UP and Organoclay Modified by PEO

#### 3.2.1. Characterization Structure of Nanocomposite Materials

Figure3 shows that when clay concentration reached 1 phr, peaks d001 moved to 41.39 Å. The original structure of MMT has been broken down to intercalated state in polymer matrix, suggesting that a great amount of polymer has dispersed into the interlayer space and expanded the MMT structure widely. At higher filler content such as 3 and 5 phr, only a part of clay was extended to intercalated structure and the remains still kept under original structure of organoclay. Specific peaks of clay contents 3 and 5 phr low intensity appeared at d-spacing =18.7Ǻand18.4Å, respectively. That means crystal structure of MMT was not destroyed and the nanocomposites exhibited partially intercalated structures.Figure 3
XRD diffraction of nanocomposite samples with three various contents of organoclay (a) 1 phr, (b) 3 phr, and (c) 5 phr.Even though XRD spectrum was a useful technique to investigate interlayer d-spacing of clay, it was not enough to characterize   internal   structure of nanocomposites. Therefore, TEM images were essential to observe a direct evidence of what structure exists in the PCNs as shown in Figure4 for 1 phr (a), 3 phr (b), and 5 phr (c). From Figure 4(a), the MMT layers were dispersed well into UP to gain intercalated structure at 1 phr clay loading. These results could possibly  due   to poly(ethylene oxide) existing in structure was as a bridge to connect between the UP chains and MMT layers to help UP enter into and expand widely structure of clay to make intercalated state. Meanwhile, the agglomerates were found in the samples containing 3 and 5 phr clay and quantity of the agglomerates was highest at the samples containing 5 phr clay (Figures 4(a) and 4(b)). That means that although MMT was modified to become more compatible with  polymer matrix, hydrophilic nature did not change remarkably. When clay content increased, the dispersion of clay was limited and kept the agglomerates in polymer matrix.TEM of nanocomposite samples with three various contents of organoclay (a) 1 phr, (b) 3 phr, and (c) 5 phr.
(a)(b)(c)


#### 3.2.2. Characterization Mechanical Properties of Nanocomposite Materials

All samples were prepared according to standard ASTM D638 and tested by a Cotech Machine (Taiwan). Generally, tensile strength of PCNs tended to increase with an increasing clay loading. Tensile modulus of PCNs had the best values with MMT content up to 1 phr as shown in Figure5. Tensile stress also increased according to contents of modified MMT 1 phr, 3 phr and then decreased at 5 phr. These results were due to modified MMT compatible with UP dispersed very well in PCNs to create intercalated structure at clay content 1 phr, so that it significantly improved mechanical properties of nanomaterials. At high loading levels, such as 3 and 5 phr of clay, polymer-clay interactions were lower, so MMT could not disperse well into polymer matrix. That resulted in agglomeration of the clay particles. The cross-link density could also be decreased at high clay contents, leading to tensile strength of PCNs being not improved, especially at loading of MMT 5 phr.Tensile strength of nanocomposite materials according to various clay contents.
(a)(b)Figure6 shows that the flexural strength also depended on the nanoclay content. The flexural strength increased from the unsaturated polyester to 1 phr MMT and after that it decreased. The flexural strength behavior confirmed that clay dispersed well at 1 phr. At 3 and 5 phr of clay contents, the creation of agglomerates caused intercalation poor, so it made a decrease of strength.Flexural strength of nanocomposite materials according to various clay contents.
(a)(b)


#### 3.2.3. Characterization Thermal Property of Nanocomposite Materials

The thermal stability of the samples was evaluated at the heating rate of 20°C/min from room temperature to 800°C by using TA Instruments (USA) with TGA-Q500. The thermal property of 0, 1, 3, and 5 phr organoclay-loaded UP is shown in Table1. UP has the onset degradation temperature at 373°C and gained maximum degradation temperature at 411°C. All nanocomposites indicated that there was also a single-step thermal  degradation like  UP. The Thermogravimetric analysis demonstrated   that   the filling of MMT in the UP affected thermal stability. The presence of organoclay made PCNs have relatively higher thermal stability than UP. These results may be clay existing in structure of nanocomposites acts as a heat barrier. The improvement of thermal property  was mainly effected by the degree of dispersion of clay in polymer matrix. From the table, it can be concluded that the thermal property of UP/clay nanocomposites was slightly enhanced as the clay content increased.Table 1
Thermal data of UP/clay nanocomposites according to various clay contents.
Clay content (phr)Onset deg. temperature (°C)Max. deg. temperature (°C)0373412137441933584245370423


## 3.1. Structure of N757 Modified by PEO

### 3.1.1. Effect of PEO Contents on Structure of N757

Structure of clays was characterized from X-ray diffractograms of a D8 Advance (Bruker Germany) with Ni-filtered CuKα radiation of wavelength 1.54 Å at 40 kV and 40 mA. Figure 1 shows the XRD pattern of unmodified and modified clay. The original MMT had basal spacing of 12.4 Å. After it was modified by PEO, the peak corresponding to the basal spacing of MMT disappeared and new peaks appeared with d-spacing of 17.9 and 18.2 Å in samples having clay: PEO ratios 10 : 3 and 10 : 5, respectively. However, d-spacing of MMT was not enhanced considerably as the clay: PEO ratios were increased from 10 : 3 to 10 : 5. It is concluded that PEO dispersed into structure of MMT and adsorption gained the saturated value at ratio 10 : 3. That was completely suitable to results researched by author Shen et al. [9].Figure 1
XRD diffraction of N757: (a) virgin N757; N757 modified by PEO at ratios (b) 10/3 and (c) 10/5.


### 3.1.2. Effect of Modifying Method on Structure of Clay

Figures2(a) and 2(b) show  the XRD patterns of modified clay synthesized by solution and melting method, respectively.Figure 2
XRD diffraction of N757 modified by PEO at ratio 10/3 according two methods: (a) solution method and (b) melting method.At the modified clay: PEO ratio 10 : 3, results display that the melting method was better than solution method. For example, the d-spacing of organoclay modified by isothermal annealing method had stronger intensity and appeared at d-spacing higher than sample from solution method. Besides, melting method (isothermal annealing) was more simple, economic, and easy to process than solution method. So it was a good method to be chosen for modifying MMT by PEO.


## 3.1.1. Effect of PEO Contents on Structure of N757

Structure of clays was characterized from X-ray diffractograms of a D8 Advance (Bruker Germany) with Ni-filtered CuKα radiation of wavelength 1.54 Å at 40 kV and 40 mA. Figure 1 shows the XRD pattern of unmodified and modified clay. The original MMT had basal spacing of 12.4 Å. After it was modified by PEO, the peak corresponding to the basal spacing of MMT disappeared and new peaks appeared with d-spacing of 17.9 and 18.2 Å in samples having clay: PEO ratios 10 : 3 and 10 : 5, respectively. However, d-spacing of MMT was not enhanced considerably as the clay: PEO ratios were increased from 10 : 3 to 10 : 5. It is concluded that PEO dispersed into structure of MMT and adsorption gained the saturated value at ratio 10 : 3. That was completely suitable to results researched by author Shen et al. [9].Figure 1
XRD diffraction of N757: (a) virgin N757; N757 modified by PEO at ratios (b) 10/3 and (c) 10/5.


## 3.1.2. Effect of Modifying Method on Structure of Clay

Figures2(a) and 2(b) show  the XRD patterns of modified clay synthesized by solution and melting method, respectively.Figure 2
XRD diffraction of N757 modified by PEO at ratio 10/3 according two methods: (a) solution method and (b) melting method.At the modified clay: PEO ratio 10 : 3, results display that the melting method was better than solution method. For example, the d-spacing of organoclay modified by isothermal annealing method had stronger intensity and appeared at d-spacing higher than sample from solution method. Besides, melting method (isothermal annealing) was more simple, economic, and easy to process than solution method. So it was a good method to be chosen for modifying MMT by PEO.


## 3.2. Structure and Properties of Nanocomposites Based on UP and Organoclay Modified by PEO

### 3.2.1. Characterization Structure of Nanocomposite Materials

Figure3 shows that when clay concentration reached 1 phr, peaks d001 moved to 41.39 Å. The original structure of MMT has been broken down to intercalated state in polymer matrix, suggesting that a great amount of polymer has dispersed into the interlayer space and expanded the MMT structure widely. At higher filler content such as 3 and 5 phr, only a part of clay was extended to intercalated structure and the remains still kept under original structure of organoclay. Specific peaks of clay contents 3 and 5 phr low intensity appeared at d-spacing =18.7Ǻand18.4Å, respectively. That means crystal structure of MMT was not destroyed and the nanocomposites exhibited partially intercalated structures.Figure 3
XRD diffraction of nanocomposite samples with three various contents of organoclay (a) 1 phr, (b) 3 phr, and (c) 5 phr.Even though XRD spectrum was a useful technique to investigate interlayer d-spacing of clay, it was not enough to characterize   internal   structure of nanocomposites. Therefore, TEM images were essential to observe a direct evidence of what structure exists in the PCNs as shown in Figure4 for 1 phr (a), 3 phr (b), and 5 phr (c). From Figure 4(a), the MMT layers were dispersed well into UP to gain intercalated structure at 1 phr clay loading. These results could possibly  due   to poly(ethylene oxide) existing in structure was as a bridge to connect between the UP chains and MMT layers to help UP enter into and expand widely structure of clay to make intercalated state. Meanwhile, the agglomerates were found in the samples containing 3 and 5 phr clay and quantity of the agglomerates was highest at the samples containing 5 phr clay (Figures 4(a) and 4(b)). That means that although MMT was modified to become more compatible with  polymer matrix, hydrophilic nature did not change remarkably. When clay content increased, the dispersion of clay was limited and kept the agglomerates in polymer matrix.TEM of nanocomposite samples with three various contents of organoclay (a) 1 phr, (b) 3 phr, and (c) 5 phr.
(a)(b)(c)


### 3.2.2. Characterization Mechanical Properties of Nanocomposite Materials

All samples were prepared according to standard ASTM D638 and tested by a Cotech Machine (Taiwan). Generally, tensile strength of PCNs tended to increase with an increasing clay loading. Tensile modulus of PCNs had the best values with MMT content up to 1 phr as shown in Figure5. Tensile stress also increased according to contents of modified MMT 1 phr, 3 phr and then decreased at 5 phr. These results were due to modified MMT compatible with UP dispersed very well in PCNs to create intercalated structure at clay content 1 phr, so that it significantly improved mechanical properties of nanomaterials. At high loading levels, such as 3 and 5 phr of clay, polymer-clay interactions were lower, so MMT could not disperse well into polymer matrix. That resulted in agglomeration of the clay particles. The cross-link density could also be decreased at high clay contents, leading to tensile strength of PCNs being not improved, especially at loading of MMT 5 phr.Tensile strength of nanocomposite materials according to various clay contents.
(a)(b)Figure6 shows that the flexural strength also depended on the nanoclay content. The flexural strength increased from the unsaturated polyester to 1 phr MMT and after that it decreased. The flexural strength behavior confirmed that clay dispersed well at 1 phr. At 3 and 5 phr of clay contents, the creation of agglomerates caused intercalation poor, so it made a decrease of strength.Flexural strength of nanocomposite materials according to various clay contents.
(a)(b)


### 3.2.3. Characterization Thermal Property of Nanocomposite Materials

The thermal stability of the samples was evaluated at the heating rate of 20°C/min from room temperature to 800°C by using TA Instruments (USA) with TGA-Q500. The thermal property of 0, 1, 3, and 5 phr organoclay-loaded UP is shown in Table1. UP has the onset degradation temperature at 373°C and gained maximum degradation temperature at 411°C. All nanocomposites indicated that there was also a single-step thermal  degradation like  UP. The Thermogravimetric analysis demonstrated   that   the filling of MMT in the UP affected thermal stability. The presence of organoclay made PCNs have relatively higher thermal stability than UP. These results may be clay existing in structure of nanocomposites acts as a heat barrier. The improvement of thermal property  was mainly effected by the degree of dispersion of clay in polymer matrix. From the table, it can be concluded that the thermal property of UP/clay nanocomposites was slightly enhanced as the clay content increased.Table 1
Thermal data of UP/clay nanocomposites according to various clay contents.
Clay content (phr)Onset deg. temperature (°C)Max. deg. temperature (°C)0373412137441933584245370423


## 3.2.1. Characterization Structure of Nanocomposite Materials

Figure3 shows that when clay concentration reached 1 phr, peaks d001 moved to 41.39 Å. The original structure of MMT has been broken down to intercalated state in polymer matrix, suggesting that a great amount of polymer has dispersed into the interlayer space and expanded the MMT structure widely. At higher filler content such as 3 and 5 phr, only a part of clay was extended to intercalated structure and the remains still kept under original structure of organoclay. Specific peaks of clay contents 3 and 5 phr low intensity appeared at d-spacing =18.7Ǻand18.4Å, respectively. That means crystal structure of MMT was not destroyed and the nanocomposites exhibited partially intercalated structures.Figure 3
XRD diffraction of nanocomposite samples with three various contents of organoclay (a) 1 phr, (b) 3 phr, and (c) 5 phr.Even though XRD spectrum was a useful technique to investigate interlayer d-spacing of clay, it was not enough to characterize   internal   structure of nanocomposites. Therefore, TEM images were essential to observe a direct evidence of what structure exists in the PCNs as shown in Figure4 for 1 phr (a), 3 phr (b), and 5 phr (c). From Figure 4(a), the MMT layers were dispersed well into UP to gain intercalated structure at 1 phr clay loading. These results could possibly  due   to poly(ethylene oxide) existing in structure was as a bridge to connect between the UP chains and MMT layers to help UP enter into and expand widely structure of clay to make intercalated state. Meanwhile, the agglomerates were found in the samples containing 3 and 5 phr clay and quantity of the agglomerates was highest at the samples containing 5 phr clay (Figures 4(a) and 4(b)). That means that although MMT was modified to become more compatible with  polymer matrix, hydrophilic nature did not change remarkably. When clay content increased, the dispersion of clay was limited and kept the agglomerates in polymer matrix.TEM of nanocomposite samples with three various contents of organoclay (a) 1 phr, (b) 3 phr, and (c) 5 phr.
(a)(b)(c)


## 3.2.2. Characterization Mechanical Properties of Nanocomposite Materials

All samples were prepared according to standard ASTM D638 and tested by a Cotech Machine (Taiwan). Generally, tensile strength of PCNs tended to increase with an increasing clay loading. Tensile modulus of PCNs had the best values with MMT content up to 1 phr as shown in Figure5. Tensile stress also increased according to contents of modified MMT 1 phr, 3 phr and then decreased at 5 phr. These results were due to modified MMT compatible with UP dispersed very well in PCNs to create intercalated structure at clay content 1 phr, so that it significantly improved mechanical properties of nanomaterials. At high loading levels, such as 3 and 5 phr of clay, polymer-clay interactions were lower, so MMT could not disperse well into polymer matrix. That resulted in agglomeration of the clay particles. The cross-link density could also be decreased at high clay contents, leading to tensile strength of PCNs being not improved, especially at loading of MMT 5 phr.Tensile strength of nanocomposite materials according to various clay contents.
(a)(b)Figure6 shows that the flexural strength also depended on the nanoclay content. The flexural strength increased from the unsaturated polyester to 1 phr MMT and after that it decreased. The flexural strength behavior confirmed that clay dispersed well at 1 phr. At 3 and 5 phr of clay contents, the creation of agglomerates caused intercalation poor, so it made a decrease of strength.Flexural strength of nanocomposite materials according to various clay contents.
(a)(b)


## 3.2.3. Characterization Thermal Property of Nanocomposite Materials

The thermal stability of the samples was evaluated at the heating rate of 20°C/min from room temperature to 800°C by using TA Instruments (USA) with TGA-Q500. The thermal property of 0, 1, 3, and 5 phr organoclay-loaded UP is shown in Table1. UP has the onset degradation temperature at 373°C and gained maximum degradation temperature at 411°C. All nanocomposites indicated that there was also a single-step thermal  degradation like  UP. The Thermogravimetric analysis demonstrated   that   the filling of MMT in the UP affected thermal stability. The presence of organoclay made PCNs have relatively higher thermal stability than UP. These results may be clay existing in structure of nanocomposites acts as a heat barrier. The improvement of thermal property  was mainly effected by the degree of dispersion of clay in polymer matrix. From the table, it can be concluded that the thermal property of UP/clay nanocomposites was slightly enhanced as the clay content increased.Table 1
Thermal data of UP/clay nanocomposites according to various clay contents.
Clay content (phr)Onset deg. temperature (°C)Max. deg. temperature (°C)0373412137441933584245370423


## 4. Conclusion

Addition of organoclay in relatively low weight to unsaturated polyester resin resulted in intercalated nanocomposites. From XRD patterns, the d-spacing of the organoclay expanded from 17.94 Å to 41.30 Å to make intercalated structure in PCNs at 1phr of modified MMT loading. TEM images of the PCNs showed presence of organoclay with nanosized dispersion in the polymer matrix. MMT dispersed well in matrix polymer to form exfoliated state or intercalated state. Degradation temperature values of the PCNs were enhanced when clay contents increased from 1 to 5 phr. Besides, mechanical properties of PCNs were also improved better than virgin unsaturated polyester. Mechanical properties showed improvement noticeably and express the best results at loading of modified MMT 1 phr. Though results were achieved from studying properties by using testing techniques, we have succeeded to prepare nanomaterials based on UP resin with PEO-modified MMT. Initial results prove that MMT could be modified by PEO and they also opened up a new trend to modify clay  to  apply  for  preparing  polymer nanomaterials in future.



---

*Source: 841813-2012-04-12.xml*