# Dynamic Wetting Behavior of Vibrated Droplets on a Micropillared Surface

Authors: Zhi-hai Jia; Wei Lei; Hui-nan Yang; Gang Wang
Journal: Advances in Materials Science and Engineering
 (2016)

---

## Abstract

The dynamical wetting behavior has been observed under vertical vibration of a water droplet placed on a micropillared surface. The wetting transition takes place under the different processes. In compression process, the droplet is transited from Cassie state to Wenzel state. The droplet undergoes a Wenzel-Cassie wetting transition in restoring process and the droplet bounces off from the surface in bouncing process. Meanwhile, the wetting and dewetting models during vibration are proposed. The wetting transition is confirmed by the model calculation. This study has potential to be used to control the wetting state.


---

## Body

## 1. Introduction

With the development of micro- and nanotechnology, superhydrophobic surface with a high static contact angle (CA) above 150° and low contact angle hysteresis plays an important role in technical applications, such as drag reduction in microfluidic devices and dropwise condensation [1–3]. In particular, achieving a high CA of these superhydrophobic surfaces is not crucial; the behavior of the droplet moving on these surfaces and the velocity of the liquid leaving from these surfaces are important in most of the applications. And superhydrophobic surfaces are not always water repellent, such as condensation [4, 5]. Therefore, restoring the characteristics of the superhydrophobic surfaces has gained widespread attention [6, 7].In the previous research, theoretical models for liquid droplets wetting on rough and chemically inhomogeneous surfaces have been investigated [8–11]. Wetting of these surfaces is governed by the Wenzel model, where the liquid wets both peaks and valleys of rough surfaces, as shown in Figure 1(a). An apparent contact angle θw of a liquid droplet on a rough surface is given by the classical Wenzel equation(1)cos⁡θw=rwcos⁡θE,where rw is roughness factor, defined as the ratio of the actual area of a rough surface to the geometric projected area. This factor is always larger than unity. And θE is an equilibrium contact angle of a liquid droplet on a corresponding flat surface.Figure 1
Wetting state of rough surfaces.
(a)
Wenzel state
(b)
Cassie stateChemically heterogeneous surface is characterized by the apparent CA, predicted by the Cassie-Baxter wetting model, as shown in Figure1(b). The apparent CA θCB is defined by the Cassie-Baxter equation(2)cos⁡θCB=fcos⁡θE+f-1,where f is the fraction of the projected area of the solid surface that is wetted by the liquid. Although these two well-established theoretical models, Wenzel model and Cassie model, are frequently employed in demonstrating different wetting phenomena, the wetting mechanisms on the rough surface are not fully investigated yet, especially in the transition region between the Wenzel and Cassie states.Recently, wetting transitions have been studied in a series of experimental and theoretical works [12–16]. It is shown that the wetting transitions are achieved by external stimuli, such as pressure [17, 18], vibration [19, 20], electric voltage [21, 22], evaporation or heat [23, 24], thermal chemical methods [25], solvent method [26], and magnetism [27]. Jung and Bhushan [12] found that the inertia force imposed on the droplet by vibration can overcome the adhesion force between the droplet and the rough surfaces; the droplet can bounce off from the surface and transit from Wenzel state to Cassie state. Bormashenko et al. [28] showed that the dynamic Cassie-Wenzel transition under vibration is more likely a 1D than a 2D affair. Meanwhile, the oscillations of droplets were widely studied on the hydrophobic or superhydrophobic surfaces [29–31]. However, most of them were focused on drop vibration models, and few experimental studies have been reported on the dynamic wetting behavior of vibrated droplets on patterned surfaces.In this paper, dynamic properties (such as the droplet contact diameter, the CA, and the liquid height) of a vibrated droplet on patterned surfaces at resonance frequency are studied. The influence of vibration on the dynamic wetting states of a water droplet is investigated. And the wetting and dewetting models during the vibration are presented.


## 2. Experimental Section

### 2.1. Fabrication of Polydimethylsiloxane (PDMS) Rough Surfaces

Microstructured surfaces are fabricated using PDMS material by soft lithography, with pillars of 30μm in width, 30 μm in height, and 30 μm in pitch value. PDMS stamps were prepared in a replication molding process with a 6-inch silicon wafer, which was covered with one layer of microstructured photoresist as a master. For preparation of the master, a layer (30 μm thickness ) of photoresist (SU-8, formulation 25, and a new negative near-UV thick photoresist) is spin-coated on a hydrophilic silicon wafer. Subsequently, the photoresist is patterned with the desired features, utilizing a printed foil mask. The polymer is allowed to cure for one hour at 90°C and to be cooled to room temperature before being removed from the master.The surface morphology of the pillars, which is observed with a scanning electron microscope (SEM, QUANTA FEG 450), is shown in Figure2(a). Deionized water is used as the liquid and the volume of each droplet is kept at 4 μL. Droplets are gently deposited on the substrate using a CA meter for the static CA. The CA value is 148.5° ± 2.5°, which is the average value of ten independent points, so the fabricated surface is a superhydrophobic surface [32]. As shown in Figure 2(b), the water droplet penetration into the space between the pillars is relatively small and it could be easily seen that the initial wetting state for PDMS surface is the Cassie state. Wetting of rough surfaces is characterized by the apparent contact angle; the apparent CA value is 113.7° for PDMS surface in this work. According to the Wenzel and Cassie equations (1) and (2), the local apparent contact angles are 143.5° and 148.3°, respectively. Thus, the experimental results are in accordance with the theoretical analysis: the initial wetting state is the Cassie state here.Figure 2
(a) SEM image of pillar structures made of PDMS (a is the pillar spacing, H is the height of the pillars, and b is the width). (b) Wetting state and contact angle of droplet of 4 µL on the microstructured surface.
(a)
(b)


### 2.2. Experimental Apparatus and Procedure

The experimental setup is shown in Figure3. The droplet is rested on a microstructured surface and the surface is vertically vibrated with a loudspeaker (maximum peak-to-peak displacement 2 mm). It is linked to a power amplifier connected to a digital function generator. The frequency and amplitude of a sinusoidal wave from a function generator can be adjusted. The vibration frequency was controlled between 0 and 250 Hz for measurement of the resonance frequency of a droplet. The process of the dynamic behavior was obtained with a high speed camera (OLYMPUS i-SPEED 3) operated at 2000 frames/s for each experimental run, and the dynamic properties of the droplets were then determined as a function of time. All experiments were carried out at 20 ± 1°C and 50 ± 5% relative humidity (RH).Figure 3
Experimental setup.


## 2.1. Fabrication of Polydimethylsiloxane (PDMS) Rough Surfaces

Microstructured surfaces are fabricated using PDMS material by soft lithography, with pillars of 30μm in width, 30 μm in height, and 30 μm in pitch value. PDMS stamps were prepared in a replication molding process with a 6-inch silicon wafer, which was covered with one layer of microstructured photoresist as a master. For preparation of the master, a layer (30 μm thickness ) of photoresist (SU-8, formulation 25, and a new negative near-UV thick photoresist) is spin-coated on a hydrophilic silicon wafer. Subsequently, the photoresist is patterned with the desired features, utilizing a printed foil mask. The polymer is allowed to cure for one hour at 90°C and to be cooled to room temperature before being removed from the master.The surface morphology of the pillars, which is observed with a scanning electron microscope (SEM, QUANTA FEG 450), is shown in Figure2(a). Deionized water is used as the liquid and the volume of each droplet is kept at 4 μL. Droplets are gently deposited on the substrate using a CA meter for the static CA. The CA value is 148.5° ± 2.5°, which is the average value of ten independent points, so the fabricated surface is a superhydrophobic surface [32]. As shown in Figure 2(b), the water droplet penetration into the space between the pillars is relatively small and it could be easily seen that the initial wetting state for PDMS surface is the Cassie state. Wetting of rough surfaces is characterized by the apparent contact angle; the apparent CA value is 113.7° for PDMS surface in this work. According to the Wenzel and Cassie equations (1) and (2), the local apparent contact angles are 143.5° and 148.3°, respectively. Thus, the experimental results are in accordance with the theoretical analysis: the initial wetting state is the Cassie state here.Figure 2
(a) SEM image of pillar structures made of PDMS (a is the pillar spacing, H is the height of the pillars, and b is the width). (b) Wetting state and contact angle of droplet of 4 µL on the microstructured surface.
(a)
(b)


## 2.2. Experimental Apparatus and Procedure

The experimental setup is shown in Figure3. The droplet is rested on a microstructured surface and the surface is vertically vibrated with a loudspeaker (maximum peak-to-peak displacement 2 mm). It is linked to a power amplifier connected to a digital function generator. The frequency and amplitude of a sinusoidal wave from a function generator can be adjusted. The vibration frequency was controlled between 0 and 250 Hz for measurement of the resonance frequency of a droplet. The process of the dynamic behavior was obtained with a high speed camera (OLYMPUS i-SPEED 3) operated at 2000 frames/s for each experimental run, and the dynamic properties of the droplets were then determined as a function of time. All experiments were carried out at 20 ± 1°C and 50 ± 5% relative humidity (RH).Figure 3
Experimental setup.


## 3. Results and Discussion

In this work, the droplet is exposed to a vertical vibration. The amplitude increases during the experiment until the droplet first bounces off from the solid surface. The droplet oscillation gets vigorous with its shape and the triple line is moving. Figure4 shows the images of droplets from the pillars PDMS surface at external forcing vibration frequency of 70 Hz and vibration amplitude of 0.31 mm.Figure 4
High speed images of the droplet bouncing-off from a vibrating plane (f=70Hz, A=0.31mm). The value of t for each image indicates a time relative to the moment (t=0) the drop bounces off from the surface.It reveals that the instantaneous dynamic characteristics of the vibrated droplets, such as the droplet contact diameterD(t), CA θ(t), and the droplet height H(t), are different at various time points. Meanwhile, the input waveform is sinusoidal signal, and the amplitude A is a function of time t, A(t)=A0sin⁡(2πft), where f is the frequency and A0 is the half of the peak-to-peak amplitude of vibration.Figure5 shows the transient evolution of the droplet and amplitude A(t) prior to the droplet bouncing-off. In one hand, H(t), D(t), and θ(t) increase or decrease with the speaker vibration amplitude (A), indicating that the droplet motion and external forcing are harmonious. It is in a resonance mode, which had been discussed in detail in our recent work [33]. Meanwhile, because of fluid elastic deformation, there is a time interval Δt between the amplitude and the instantaneous dynamic characteristics of vibrated droplets, as shown in Figure 5(a). On the other hand, with the amplitude increasing and decreasing, the dynamic behaviors of a droplet can generally be classified into three different categories: compression process, restoring process, and bouncing process.Figure 5
The transient evolution of the droplet and amplitudeA(t) prior to the droplet bouncing-off. (a) The droplet height H(t), (b) the droplet contact diameter D(t), and (c) the CA θ(t). The characteristics of the vibrated droplet on the pillared surface can generally be classified into three different categories: compression process (A)–(C), restoring process (C)–(E), and bouncing process (E)–(G).
(a)
(b)
(c)The compression process corresponds to the case where the vibrated droplet is continuously compressed as the top portion of the droplet is moving at a lower velocity in the positivey-direction than the bottom portion of the droplet. This behavior results in considerable decreasing of the liquid height during its vibration in the y-direction, as shown in Figures 4(a)–4(c) and 5(a). Also, the contact diameter between the droplet and the substrate is increasing (see Figure 5(b)) and the CA is decreasing (see Figure 5(c)). Such a situation occurs because of the partial filling of pillars with water and that results in a wetting transition. Generally, there are two main scenarios of wetting transitions, 1D and 2D, as shown in Figure 6 [34]. In this case, as shown in Figure 6, the triple line and contact angle are continuously slowly changing and the triple line is not pinned. Thus, the dynamic Cassie-Wenzel transition is more likely a 1D than a 2D affair. Also, it has been established that the transition occurs under the constant force per unit length of the triple contact line. It is not necessary to fill all surface intrusions but only those adjacent to the triple line [28].Figure 6
Scheme illustrating 1D and 2D scenarios of wetting transitions [28].On the rough substrate manufactured from strongly hydrophobic material, the Cassie wetting state corresponds to a higher free energy of the droplet/substrate system than the Wenzel wetting state. Vibrations provide the droplet with the necessary energy for penetration into pillars on the surface. The energy required when one “cell” is wetting is(3)ΔEcell=4bhγSL-γSA=-4bhγLAcos⁡θE,where γLA, γSL, and γSA are surface tensions on the liquid-air, solid-liquid, and solid-air interfaces, respectively. θE is the Young contact angle of a flat surface. The number of such cells depends on the scenarios of wetting transition. As mentioned above, the transition corresponds to the 1D scenario of wetting transitions. Figure 7 shows the wetting behavior models. As it is shown in Figure 6, the number of “cells” is(4)N=πRmax2-πR02a+b2.Thus, the necessary energy for wetting the surface in this process is(5)E=NΔEcell=-4bhγLAπRmax2-R02cos⁡θEa+b2,where Rmax and R0 are the maximum and the initial contact diameters between the droplet and substrate, respectively. a is the pillar spacing, h is the wetting height of pillars, and b is the width, respectively.Figure 7
Scheme illustrating the droplet wetting behaviors.
(a)
The compression process
(b)
The restoring process
(c)
The bouncing processThe kinetic energy imparted to the dropEK scales as [15](6)EK∝12ρV2πfA2,where ρ and V are the density and volume of the droplet, f is the external forcing frequency, A is half of the peak-to-peak amplitude of vibration, and 2πfA is the maximum speed of the speaker.Meanwhile, the external forcing frequencyf=70Hz is consistent with the resonant frequency of the droplet [33]. At resonance, the droplet picks up the kinetic energy at the highest efficiency. Assuming that the highest efficiency is 100%, therefore, the kinetic energy imparted to the droplet Eko is(7)Eko=12ρV2πfA2.Vibrations provide the droplet with the necessary energy for penetration into pillars:(8)Eko=E.In this paper, 2Rmax=Dmax=1.71mm, 2R0=D0=1.05mm, A=0.31mm, f=70Hz, V=4μL, γLA=72×10-3J/m, ρ=1000kg/m3, and θE = 113.7°. When substituted into (1)–(8), the wetting height h can be deduced:(9)h=-ρV2πfA2a+b28bγLAπRmax2-R02cos⁡θE≈27μm.Obviously, the droplet comes close to the Wenzel state (the height of the pillars H=30μm). Therefore, in the compression process, the droplet achieves a Cassie to Wenzel transition, and the transition corresponds to the 1D scenario of wetting transitions, which verify the analysis before.The restoring process consists of water droplets that are considerably restored during their motion on the solid surface from the maximum positive amplitude to the equilibrium position, as shown in Figure7(b). In the presence of the adhesion force and inertia force, the top portion of the droplet is moving towards the positive y-direction, but the bottom portion of the droplet is moving in the opposite direction; the droplet is stretched in the y-direction. Meanwhile, it results in the increasing of the liquid height and decreasing of the contact diameter between the droplet and substrate (see Figure 5), and the wetting state changed. Comparing the time points t=-10.5ms (Figure 4(a)) and t=-3.5ms (Figure 4(e)), the contact diameter is nearly the same and the droplet is restored to Cassie state. However, because the droplet is stretched in the y-direction, the liquid-air line is moving and we can observe that the CAs for the two moments are very different. Namely, the CAs for the Cassie state are different and the Cassie equation is not applied to this situation. The restoring process is approximately a reversible process of the compression process, and the droplet transits from Wenzel state to Cassie state.The bouncing process corresponds to the case where the amplitude is increased in the negativey-direction and the water droplet is continuously stretched as the top portion of the droplet is moving slower than the bottom portion of the droplet. In this case, the contact diameter between the droplet and substrate is decreasing until the droplet bouncing-off from the surface, as shown in Figure 7(c). Meanwhile, droplets bouncing from the superhydrophobic patterned surface only at a certain frequency and amplitude were observed. It is reasonable to suggest that only when the imparted kinetic energy is greater than the adhesion energy, the droplet can bounce from the surface.


## 4. Conclusions

The dynamic behaviors of a vibrated droplet at resonance frequency on a micropillared surface were investigated in this paper. We considered the effect of vibration on the droplet contact diameter, the CA, and the droplet height during its movement along a micropillared surface. As the amplitude of vibration increases and decreases, the dynamic behavior of a water droplet can generally be classified into three different categories: compression process, restoring process, and bouncing process. In compression process, the contact diameter between the droplet and the substrate is increasing and the liquid height and contact angle are continuously slowly decreasing. The droplet is transited from Cassie state to Wenzel state and the transition corresponds to the 1D scenario of wetting transitions. The restoring is an inverse process of the compression, and a Wenzel-Cassie wetting transition is observed. In the bouncing process, the contact diameter is decreasing until the droplet bouncing-off from the surface and the bouncing only happened at certain amplitude. For the micropillared surfaces, the wetting regime could be controlled with vibration. The possibility of controlling the wetting regime with vibration may be of the utmost importance in the context of the rapid development of the applications of superhydrophobic surfaces.



---

*Source: 8409683-2016-01-26.xml*