# Preparation of Dicalcium Phosphate Anhydrous (Monetite) Biological Coating on Titanium by Spray-Drying Method

Authors: Xingling Shi; Chao Zhao; Lingli Xu; Qingliang Wang
Journal: Advances in Materials Science and Engineering
 (2017)

---

## Abstract

Titanium and its alloys have been widely used in the manufacture of endosseous implants due to excellent biocompatibility, low elastic modulus, and good chemical stability. However, the titanium based metals are essentially bioinert materials. In order to improve their bioactivity, biological coatings are usually applied. Recent studies found that, compared with hydroxyapatite coating, dicalcium phosphate anhydrous (DCPA, Monetite) coating maybe more bioactive due to higher solubility and release of Ca and P ions. In this work, DCPA coating was prepared through a novel and simple method. Briefly, high concentration DCPA solution was sprayed onto superhydrophilic titanium and the specimens were dried fast in an air-circulating oven. After repeating the process over 100 times, a compact coating was fabricated. The microstructure, chemical composition, wettability, andin vitro bioactivity of the coating were analyzed and evaluated. Results showed that the coating fully covered the substrate and consisted of a large number of uniformly sized DCPA granules that packed together closely. The coating showed good wettability and could keep the property for a long time. After immersion in simulated body fluid for 2 weeks, a large amount of bone-like apatite with low crystallinity was induced implying a good bioactivity.


---

## Body

## 1. Introduction

Titanium (Ti) and its alloys are important metal materials for the manufacture of load bearing bone implants due to excellent corrosion resistance, biocompatibility, and lower elasticity modulus. However, the Ti based metals are essentially bioinert materials and are insufficient in osseointegration ability. Instead of biological fixation, their combination with human bones mainly depends on mechanical locking. Moreover, a fibrous capsule intervening at the interface of implant and bone is always formed after the implantation, especially when a relatively smooth implant was used [1, 2]. Such kind of fibrous capsule is fragile and its adhesion to both implant and surrounding bone cavity is quite low, and therefore it is easy to peel or form crush induced necrosis under stress and micromovement. In this case, a serious secondary infection is likely to happen and may lead to a premature loss of reconstruction function of the implants. In addition, the fibrous capsule is poorly differentiated and may undergo hyperplasia or transform into tumor tissue under sustained mechanical stimulation. Thus, a fast and strong bonding to the host bone without soft tissue intervention is a prerequisite for the long-term and stable performance of Ti implants.Bioactive coatings play an important role in improving the osseointegration of metal implant with bone and, among them, the hydroxyapatite (HA) coating is the most widely used [3–5]. However, HA is not osteoinductive and when the implantation site is poor in bone mass and density, such as osteoporosis, even HA coated implants cannot form a rapid biological integration with the host bone. With the increasing desire from patients for early loading and rapid healing, it is urgent to prepare new biological implant coatings with osteoinductivity. By contrast, acidic calcium phosphates, dicalcium phosphate anhydrous (CaHPO4, DCPA, Monetite) and dicalcium phosphate dehydrate (CaHPO4·H2O, DCPD, Brushite), are more degradable at physiologic pH than HA and will form a Ca2+ and PO43- supersaturated zone at the interface of implant and bone that may induce osteoblastic differentiation [6]. Among them, DCPA has gained great attention recently as it showed degradation and regeneration properties superior to DCPD. For instance,in vitro evaluation showed that DCPA ensured active osteoclast resorption and would also induce higher levels of osteogenic genes expression of bone marrow cells than DCPD [7, 8].In vivo studies are even more promising. Torres and coworkers grafted DCPA and autologous bone granules separately into critical sized bone defects in rabbit calvaria and after 8 weeks they found that the volumes of mineralized tissue formed by two kinds of granules were not significantly different [9, 10]. Oryan et al. compared the effectiveness of calcium phosphates/chitosan-gelatin-platelet gel scaffold on the healing of critical size radial bone defects in rats 8 weeks after implantation. They reported that DCPA filler accelerated bone regeneration and provided a much better balance between substitute resorption and new bone formation compared with β-TCP and HA [11]. DCPA degrades at a mild rate and, unlike β-TCP and DCPD, it will not undergo phase transition into HA in physiologic environment [12]. Such unique properties may bring about its superiority in terms of resorption and remodeling. Therefore, we think DCPA coatings are expected to be a new generation of bioactive coatings used on surface of metal endosseous implants.Several techniques have been developed for preparation of DCPA coating. Kuroda et al. heated the Ti substrate up to 150°C in a solution with calcium and phosphorus ions by large alternating current (up to 25 A). Water gasified vigorously on Ti surface and DCPA was formed. However, the coating grew in the form of lamellar and brick-like clusters and failed to completely cover the substrate [13]. Ortiz et al. prepared DCPD on metal substrate by electrochemical deposition and chemical deposition separately and then heated the specimens to get DCPA coating. In this procedure, Ca/P ratio was difficult to control as spontaneous grain growth happened during the formation of DCPD coating and therefore the final products might contain calcium pyrophosphate (CPPD) which to some extent weakens the biocompatibility of coatings [14, 15]. DCPA coating can also be prepared by sol-gel method. However, such method not only consumes time as always, but also induces calcium carbonate and other impurities [16]. Obviously, DCPA coatings by these methods can not meet the requirement of biomedical applications. Moreover, the current methods present several drawbacks such as complicated equipment, high safety standard, high current or temperature operation, complicated process, low efficiency, and high energy consumption. Besides, the DCPA granules by these methods usually scatter on substrate surface as clusters and could not cover the substrate completely. Nevertheless, the impurity phase generated during preparation may impair the properties of coating.In this work, a novel DCPA coating preparation method was proposed based on the dissolution characteristic of dicalcium phosphate. Briefly, high concentration DCPA aqueous solution was prepared and then a DCPA coating was prepared on superhydrophilic Ti substrate by repeated spray-drying treatment. The microstructure, chemical composition, wettability, andin vitro apatite inducing ability of the coating were analyzed and evaluated.


## 2. Materials and Methods

### 2.1. Pretreatment of Specimens

Annealed commercially pure Ti pieces (Grade 2, Baoji Titanium Industry Company Ltd., China), cut into 10 mm × 10 mm × 2.5 mm, were used as substrates. The specimens were wet-polished with 280#, 400#, and 800# SiC abrasive paper successively and then ultrasonically washed in acetone and distilled water for 10 min, respectively. After being dried in air, these specimens were pretreated by acid etching to get superhydrophilic surface. Briefly, the Ti specimens were submerged in a mixture of 98% (wt) H2SO4, 37% (wt) HCl, and distilled water with the volume ratio of 5 : 2 : 3 and etched for 30 min. After that, the specimens were sufficiently washed with tap water, neutralized by diluted NaHCO3 solution, and then ultrasonically washed for 10 min in distilled water. The pretreated specimens were placed in distilled water before use.


### 2.2. Solution Preparation and Coating Fabrication

High concentration DCPA aqueous solutions, 11.5 g/L (unsaturated), were prepared by dissolving analytically pure DCPA powder (Sinopharm Chemical Reagent Co. Ltd., China) into diluted HCl solution of 0.15 mol/L with the assistance of ultrasonicator. Pretreated Ti specimens were taken out of distilled water, placed into an air-circulating oven set at 60°C. Immediately after drying, the specimens were repeatedly sprayed with DCPA solution for certain times by a programmable automatic electric sprayer (TS-T, Shanghai Kezhe Biochemical Technology Co., Ltd., China). The spraying distance was 3 cm, the spray radius was 4 cm, and the spray volume was 0.1 ml per time. A interval of 2 min was set between two successive sprays to ensure complete drying of the specimen surface. The experiment setup is illustrated in Figure1. After the final spray and drying, specimen were washed thoroughly with distilled water and then were finally dried in the oven for 30 min.Figure 1
Illustration of coating preparation progress.


### 2.3. Characterizations

Product phases and crystallinity were investigated by X-ray diffraction (XRD, D/MAX-3B, Rigaku Co., USA). The surface morphologies of the specimens were observed with scanning electronic microscope (SEM, S-3000, Hitachi Co., Japan). Surface roughness of specimens was analyzed by laser scanning confocal microscopy (VKX100, Keyence Co., Japan). The contact angle of distilled water on DCPA coating was measured by the static contact angle measuring instrument (JC2000A, Shanghai Zhongchen Digital Technic Apparatus Co., Ltd., China). Bioactivity of DCPA coating was evaluated through the simulated body fluid (SBF) immersion test. The main ion concentrations of the SBF were nearly equal to that of human plasma and the pH was adjusted to 7.4 by trihydroxymethyl aminomethane (Tris) and 1.0 mol/L HCl solution [17]. DCPA coated specimens were immersed in 1.0 mol/L NaOH solution at 60°C for 1 h and after thorough rinse they were immersed in SBF for 14 days in an incubator set at 37°C. After that, specimens were taken out, rinsed with distilled water, and dried in air at room temperature. And then the immersed specimens were analyzed by SEM and XRD.


## 2.1. Pretreatment of Specimens

Annealed commercially pure Ti pieces (Grade 2, Baoji Titanium Industry Company Ltd., China), cut into 10 mm × 10 mm × 2.5 mm, were used as substrates. The specimens were wet-polished with 280#, 400#, and 800# SiC abrasive paper successively and then ultrasonically washed in acetone and distilled water for 10 min, respectively. After being dried in air, these specimens were pretreated by acid etching to get superhydrophilic surface. Briefly, the Ti specimens were submerged in a mixture of 98% (wt) H2SO4, 37% (wt) HCl, and distilled water with the volume ratio of 5 : 2 : 3 and etched for 30 min. After that, the specimens were sufficiently washed with tap water, neutralized by diluted NaHCO3 solution, and then ultrasonically washed for 10 min in distilled water. The pretreated specimens were placed in distilled water before use.


## 2.2. Solution Preparation and Coating Fabrication

High concentration DCPA aqueous solutions, 11.5 g/L (unsaturated), were prepared by dissolving analytically pure DCPA powder (Sinopharm Chemical Reagent Co. Ltd., China) into diluted HCl solution of 0.15 mol/L with the assistance of ultrasonicator. Pretreated Ti specimens were taken out of distilled water, placed into an air-circulating oven set at 60°C. Immediately after drying, the specimens were repeatedly sprayed with DCPA solution for certain times by a programmable automatic electric sprayer (TS-T, Shanghai Kezhe Biochemical Technology Co., Ltd., China). The spraying distance was 3 cm, the spray radius was 4 cm, and the spray volume was 0.1 ml per time. A interval of 2 min was set between two successive sprays to ensure complete drying of the specimen surface. The experiment setup is illustrated in Figure1. After the final spray and drying, specimen were washed thoroughly with distilled water and then were finally dried in the oven for 30 min.Figure 1
Illustration of coating preparation progress.


## 2.3. Characterizations

Product phases and crystallinity were investigated by X-ray diffraction (XRD, D/MAX-3B, Rigaku Co., USA). The surface morphologies of the specimens were observed with scanning electronic microscope (SEM, S-3000, Hitachi Co., Japan). Surface roughness of specimens was analyzed by laser scanning confocal microscopy (VKX100, Keyence Co., Japan). The contact angle of distilled water on DCPA coating was measured by the static contact angle measuring instrument (JC2000A, Shanghai Zhongchen Digital Technic Apparatus Co., Ltd., China). Bioactivity of DCPA coating was evaluated through the simulated body fluid (SBF) immersion test. The main ion concentrations of the SBF were nearly equal to that of human plasma and the pH was adjusted to 7.4 by trihydroxymethyl aminomethane (Tris) and 1.0 mol/L HCl solution [17]. DCPA coated specimens were immersed in 1.0 mol/L NaOH solution at 60°C for 1 h and after thorough rinse they were immersed in SBF for 14 days in an incubator set at 37°C. After that, specimens were taken out, rinsed with distilled water, and dried in air at room temperature. And then the immersed specimens were analyzed by SEM and XRD.


## 3. Results and Discussions

### 3.1. Pretreatment

Surface morphologies of specimens before and after pretreatment were shown in Figure2. After acid etching, texture of scratches generated during the wet abrasion had disappeared and submicron sized etch pits were found distributing all over the surface. The surface roughness was found increased, from 0.26 μm to 1.61 μm, after acid etching treatment. Surface wettability of specimens was obviously improved as shown in Figure 3. The contact angle on polished surface was about 37°, whereas the water drop spread on acid etched surface fast and the contact angle became 0°. It meant that acid etching had imposed superhydrophilicity to the Ti specimens. However, such excellent wettability gradually degraded when specimens were kept in ambient air. As shown in Figure 4, the contact angle (CA) increased with the increase of storage time. After 14 days storage it was over 100°. In order to preserve the superhydrophilicity, specimens were submersed in distilled water in a sealed glass bottle. As it could be seen, the CA was still 0° after 14 days immersion in distilled water.Figure 2
Surface morphology of specimens before and after pretreatment: (a) sandpaper polished; (b) acid etched specimens.
(a)
(b)Figure 3
Contact angles of specimens before and after pretreatment: (a) sandpaper polished; (b) acid etched specimens.
(a)
(b)Figure 4
The changes of contact angles with increasing storage duration.


### 3.2. Characterizations of DCPA Coating

#### 3.2.1. Surface Morphology

Figure5 showed the SEM observation results of acid etched Ti specimens after spray-drying treatment with different repeating times. At the beginning, when the number of repetitions was low, round shaped clumps were formed on the surface, as shown in Figure 5(a). They were separated, occupying one or more etch pits, but closely attached to the specimens surface. However, the acid etched surface was still visible, because of the limited numbers of these particles. As the spray-drying operation repeated, more round clumps were formed, and they started to pile up and contact each other, as shown in Figure 5(b). When the repeating times increase to 100, the whole specimens surface was covered with numerous cubic granules of about 1.5 μm in diameter and the acid etched pits disappeared. These granules stacked up tightly with each other and had formed a compact layer, Figure 5(c). The later XRD result confirmed that these are DCPA particles. However, further increase in repeating times, up to 140, induced a less compact coating with particles showing a hairy surface, as shown in Figure 5(d).Figure 5
Surface morphology changes with increasing spray-drying repetition number: (a) 20 times; (b) 60 times; (c) 100 times; (d) 140 times.
(a)
(b)
(c)
(d)


#### 3.2.2. Coating Phase Analysis

Figure6 showed the XRD patterns of acid etched Ti after 100 times of spray-drying treatment. It could be seen that several diffraction peaks appeared besides those from pure Ti substrate and all these new peaks could be ascribed to DCPA (PDF #01-077-0128). Among them, the three most intense ones, located at 2θ=26.4°, 30.2°, and 32.8°, could be assigned to the (220), (112), and (102) planes, respectively. The diffraction results have excluded existence of by-products in the coating as peaks from other crystalized Ca-P compound and amorphous phases were not found. Besides, all the diffraction peaks were sharp in shape which indicated well crystallized structures and an atomic ratio that was close to the ideal stoichiometry. According to calculations using Scherrer formula, the crystal in the cubic granules was 40.59 nm in average. Thermodynamically, the product of Ca-P precipitation from solution could be predicted based on the diagram of Ca-P compounds solubility versus pH. When the pH was less than 4.0, DCPA crystals could preferentially be precipitated from the liquid if the ions were supersaturated [6, 18]. Thus, in this method, low solution pH was the controlling factor for the pure DCPA product.Figure 6
XRD patterns of specimens after 100 times of spray-drying treatment.It could be inferred that, after each spraying, the former precipitated granules on substrate would be dissolved and precipitated again during the following drying stage. With the increase of repeating times and the accumulation of solute, a compact DCPA coating would be formed gradually. Compared with that by Kuroda et al., the DCPA coating prepared by this spray-drying method could cover the acid etched surface completely and the granules in the coating were uniform in size, contacted with each other more closely according to SEM observation [13, 19]. The superhydrophilic surface facilitated even and fast evaporation of water once a thin liquid layer was formed by spraying and was thought to be an important precondition for the homogenous precipitation of DCPA granules. However, as water evaporated quickly, once a compact coating had been formed, the following sprays would only induce partial dissolution of these granules and thus the top surface of the coating became hairy as the spray-drying repeating times reached 140.


#### 3.2.3. Wettability

The wettability of DCPA coating was evaluated by measuring the contact angle, as shown in Figure7. Same as acid etched specimens, the freshly prepared DCPA coated ones also showed superhydrophilicity. Moreover, after being stored in ambient air for 4 weeks, it still kept an excellent hydrophilicity with the contact angle only rising about 15°. These results showed that, the DCPA coating not only inherited superhydrophilicity of acid etched surface but also preserved a good wettability after a long storing duration.Figure 7
Contact angles of DCPA coatings: (a) freshly prepared; (b) after 4 weeks storage in air.
(a)
(b)Currently, surface of Ti implants designed for osseointegration are usually roughened by sandblast and/or acid etching. Submicron scaled pits generated on the Ti surface mimic the microstructure of natural bone and facilitate osteogenic differentiation of stem cells. Besides, such roughening could impose superhydrophilicity to surface of implant which greatly improves the bioactivity of Ti. For instance, the protein in the body fluid could be rapidly adsorbed to the implant surface at the implantation moment and show conformation favorable for cell attachment, proliferation, and osteogenic differentiation [20]. However, a fresh acid etched surface also possesses high surface energy, and therefore carbon containing molecules in the ambient air or packages will easily be adsorbed onto its surface and keep accumulating as storage time increases. Such contamination impairs the excellent wettability and degrades osteoconductivity of rough implants and has become a universal problem that challenges both the producer and surgeons [21–24]. This study demonstrated that hydrophilicity of the bone implants with rough surface could be preserved by slightly soluble bioactive coatings and hence the bioactivity degradation will be overcome.


#### 3.2.4.In Vivo Apatite Induction

The surface morphology observation and XRD results of DCPA coated specimens (spray-drying 100 times) after immersion in SBF for 2 weeks were shown in Figures8 and 9. As could be seen from the SEM image, the whole surface of specimens was covered by spherical crystal clusters after immersion. It was the typical surface morphology of bioactive materials after SBF immersion test [25, 26]. In the XRD pattern peaks ascribed to apatite could be observed. Meanwhile, it should be noticed that apatite was of low crystallinity and signals of amorphous phase were found at the diffraction angles from 20° to 40°. In addition, the diffraction peaks of DCPA remained clearly and their relative intensities versus those of Ti substrate did not seem to decrease. It indicated that the DCPA coating did not undergo obvious degradation during the immersion. The SBF immersion experiment tallies within vivo animal experiment very well and is reproducible and easy to be operated, so it is widely used to evaluate the bioactivity of materials. The spontaneous deposition of apatite from SBF within 2 weeks indicated that the DCPA coating fabricated by this method has good bioactivity and it is hopeful of inducing new bone to grow rapidly on the surface of implants and increasing the initial stability of implants.Figure 8
Surface morphology of coated specimens after being immersed in SBF for 2 weeks.Figure 9
Phase analysis of coated specimens after being immersed in SBF for 2 weeks.


## 3.1. Pretreatment

Surface morphologies of specimens before and after pretreatment were shown in Figure2. After acid etching, texture of scratches generated during the wet abrasion had disappeared and submicron sized etch pits were found distributing all over the surface. The surface roughness was found increased, from 0.26 μm to 1.61 μm, after acid etching treatment. Surface wettability of specimens was obviously improved as shown in Figure 3. The contact angle on polished surface was about 37°, whereas the water drop spread on acid etched surface fast and the contact angle became 0°. It meant that acid etching had imposed superhydrophilicity to the Ti specimens. However, such excellent wettability gradually degraded when specimens were kept in ambient air. As shown in Figure 4, the contact angle (CA) increased with the increase of storage time. After 14 days storage it was over 100°. In order to preserve the superhydrophilicity, specimens were submersed in distilled water in a sealed glass bottle. As it could be seen, the CA was still 0° after 14 days immersion in distilled water.Figure 2
Surface morphology of specimens before and after pretreatment: (a) sandpaper polished; (b) acid etched specimens.
(a)
(b)Figure 3
Contact angles of specimens before and after pretreatment: (a) sandpaper polished; (b) acid etched specimens.
(a)
(b)Figure 4
The changes of contact angles with increasing storage duration.


## 3.2. Characterizations of DCPA Coating

### 3.2.1. Surface Morphology

Figure5 showed the SEM observation results of acid etched Ti specimens after spray-drying treatment with different repeating times. At the beginning, when the number of repetitions was low, round shaped clumps were formed on the surface, as shown in Figure 5(a). They were separated, occupying one or more etch pits, but closely attached to the specimens surface. However, the acid etched surface was still visible, because of the limited numbers of these particles. As the spray-drying operation repeated, more round clumps were formed, and they started to pile up and contact each other, as shown in Figure 5(b). When the repeating times increase to 100, the whole specimens surface was covered with numerous cubic granules of about 1.5 μm in diameter and the acid etched pits disappeared. These granules stacked up tightly with each other and had formed a compact layer, Figure 5(c). The later XRD result confirmed that these are DCPA particles. However, further increase in repeating times, up to 140, induced a less compact coating with particles showing a hairy surface, as shown in Figure 5(d).Figure 5
Surface morphology changes with increasing spray-drying repetition number: (a) 20 times; (b) 60 times; (c) 100 times; (d) 140 times.
(a)
(b)
(c)
(d)


### 3.2.2. Coating Phase Analysis

Figure6 showed the XRD patterns of acid etched Ti after 100 times of spray-drying treatment. It could be seen that several diffraction peaks appeared besides those from pure Ti substrate and all these new peaks could be ascribed to DCPA (PDF #01-077-0128). Among them, the three most intense ones, located at 2θ=26.4°, 30.2°, and 32.8°, could be assigned to the (220), (112), and (102) planes, respectively. The diffraction results have excluded existence of by-products in the coating as peaks from other crystalized Ca-P compound and amorphous phases were not found. Besides, all the diffraction peaks were sharp in shape which indicated well crystallized structures and an atomic ratio that was close to the ideal stoichiometry. According to calculations using Scherrer formula, the crystal in the cubic granules was 40.59 nm in average. Thermodynamically, the product of Ca-P precipitation from solution could be predicted based on the diagram of Ca-P compounds solubility versus pH. When the pH was less than 4.0, DCPA crystals could preferentially be precipitated from the liquid if the ions were supersaturated [6, 18]. Thus, in this method, low solution pH was the controlling factor for the pure DCPA product.Figure 6
XRD patterns of specimens after 100 times of spray-drying treatment.It could be inferred that, after each spraying, the former precipitated granules on substrate would be dissolved and precipitated again during the following drying stage. With the increase of repeating times and the accumulation of solute, a compact DCPA coating would be formed gradually. Compared with that by Kuroda et al., the DCPA coating prepared by this spray-drying method could cover the acid etched surface completely and the granules in the coating were uniform in size, contacted with each other more closely according to SEM observation [13, 19]. The superhydrophilic surface facilitated even and fast evaporation of water once a thin liquid layer was formed by spraying and was thought to be an important precondition for the homogenous precipitation of DCPA granules. However, as water evaporated quickly, once a compact coating had been formed, the following sprays would only induce partial dissolution of these granules and thus the top surface of the coating became hairy as the spray-drying repeating times reached 140.


### 3.2.3. Wettability

The wettability of DCPA coating was evaluated by measuring the contact angle, as shown in Figure7. Same as acid etched specimens, the freshly prepared DCPA coated ones also showed superhydrophilicity. Moreover, after being stored in ambient air for 4 weeks, it still kept an excellent hydrophilicity with the contact angle only rising about 15°. These results showed that, the DCPA coating not only inherited superhydrophilicity of acid etched surface but also preserved a good wettability after a long storing duration.Figure 7
Contact angles of DCPA coatings: (a) freshly prepared; (b) after 4 weeks storage in air.
(a)
(b)Currently, surface of Ti implants designed for osseointegration are usually roughened by sandblast and/or acid etching. Submicron scaled pits generated on the Ti surface mimic the microstructure of natural bone and facilitate osteogenic differentiation of stem cells. Besides, such roughening could impose superhydrophilicity to surface of implant which greatly improves the bioactivity of Ti. For instance, the protein in the body fluid could be rapidly adsorbed to the implant surface at the implantation moment and show conformation favorable for cell attachment, proliferation, and osteogenic differentiation [20]. However, a fresh acid etched surface also possesses high surface energy, and therefore carbon containing molecules in the ambient air or packages will easily be adsorbed onto its surface and keep accumulating as storage time increases. Such contamination impairs the excellent wettability and degrades osteoconductivity of rough implants and has become a universal problem that challenges both the producer and surgeons [21–24]. This study demonstrated that hydrophilicity of the bone implants with rough surface could be preserved by slightly soluble bioactive coatings and hence the bioactivity degradation will be overcome.


### 3.2.4.In Vivo Apatite Induction

The surface morphology observation and XRD results of DCPA coated specimens (spray-drying 100 times) after immersion in SBF for 2 weeks were shown in Figures8 and 9. As could be seen from the SEM image, the whole surface of specimens was covered by spherical crystal clusters after immersion. It was the typical surface morphology of bioactive materials after SBF immersion test [25, 26]. In the XRD pattern peaks ascribed to apatite could be observed. Meanwhile, it should be noticed that apatite was of low crystallinity and signals of amorphous phase were found at the diffraction angles from 20° to 40°. In addition, the diffraction peaks of DCPA remained clearly and their relative intensities versus those of Ti substrate did not seem to decrease. It indicated that the DCPA coating did not undergo obvious degradation during the immersion. The SBF immersion experiment tallies within vivo animal experiment very well and is reproducible and easy to be operated, so it is widely used to evaluate the bioactivity of materials. The spontaneous deposition of apatite from SBF within 2 weeks indicated that the DCPA coating fabricated by this method has good bioactivity and it is hopeful of inducing new bone to grow rapidly on the surface of implants and increasing the initial stability of implants.Figure 8
Surface morphology of coated specimens after being immersed in SBF for 2 weeks.Figure 9
Phase analysis of coated specimens after being immersed in SBF for 2 weeks.


## 3.2.1. Surface Morphology

Figure5 showed the SEM observation results of acid etched Ti specimens after spray-drying treatment with different repeating times. At the beginning, when the number of repetitions was low, round shaped clumps were formed on the surface, as shown in Figure 5(a). They were separated, occupying one or more etch pits, but closely attached to the specimens surface. However, the acid etched surface was still visible, because of the limited numbers of these particles. As the spray-drying operation repeated, more round clumps were formed, and they started to pile up and contact each other, as shown in Figure 5(b). When the repeating times increase to 100, the whole specimens surface was covered with numerous cubic granules of about 1.5 μm in diameter and the acid etched pits disappeared. These granules stacked up tightly with each other and had formed a compact layer, Figure 5(c). The later XRD result confirmed that these are DCPA particles. However, further increase in repeating times, up to 140, induced a less compact coating with particles showing a hairy surface, as shown in Figure 5(d).Figure 5
Surface morphology changes with increasing spray-drying repetition number: (a) 20 times; (b) 60 times; (c) 100 times; (d) 140 times.
(a)
(b)
(c)
(d)


## 3.2.2. Coating Phase Analysis

Figure6 showed the XRD patterns of acid etched Ti after 100 times of spray-drying treatment. It could be seen that several diffraction peaks appeared besides those from pure Ti substrate and all these new peaks could be ascribed to DCPA (PDF #01-077-0128). Among them, the three most intense ones, located at 2θ=26.4°, 30.2°, and 32.8°, could be assigned to the (220), (112), and (102) planes, respectively. The diffraction results have excluded existence of by-products in the coating as peaks from other crystalized Ca-P compound and amorphous phases were not found. Besides, all the diffraction peaks were sharp in shape which indicated well crystallized structures and an atomic ratio that was close to the ideal stoichiometry. According to calculations using Scherrer formula, the crystal in the cubic granules was 40.59 nm in average. Thermodynamically, the product of Ca-P precipitation from solution could be predicted based on the diagram of Ca-P compounds solubility versus pH. When the pH was less than 4.0, DCPA crystals could preferentially be precipitated from the liquid if the ions were supersaturated [6, 18]. Thus, in this method, low solution pH was the controlling factor for the pure DCPA product.Figure 6
XRD patterns of specimens after 100 times of spray-drying treatment.It could be inferred that, after each spraying, the former precipitated granules on substrate would be dissolved and precipitated again during the following drying stage. With the increase of repeating times and the accumulation of solute, a compact DCPA coating would be formed gradually. Compared with that by Kuroda et al., the DCPA coating prepared by this spray-drying method could cover the acid etched surface completely and the granules in the coating were uniform in size, contacted with each other more closely according to SEM observation [13, 19]. The superhydrophilic surface facilitated even and fast evaporation of water once a thin liquid layer was formed by spraying and was thought to be an important precondition for the homogenous precipitation of DCPA granules. However, as water evaporated quickly, once a compact coating had been formed, the following sprays would only induce partial dissolution of these granules and thus the top surface of the coating became hairy as the spray-drying repeating times reached 140.


## 3.2.3. Wettability

The wettability of DCPA coating was evaluated by measuring the contact angle, as shown in Figure7. Same as acid etched specimens, the freshly prepared DCPA coated ones also showed superhydrophilicity. Moreover, after being stored in ambient air for 4 weeks, it still kept an excellent hydrophilicity with the contact angle only rising about 15°. These results showed that, the DCPA coating not only inherited superhydrophilicity of acid etched surface but also preserved a good wettability after a long storing duration.Figure 7
Contact angles of DCPA coatings: (a) freshly prepared; (b) after 4 weeks storage in air.
(a)
(b)Currently, surface of Ti implants designed for osseointegration are usually roughened by sandblast and/or acid etching. Submicron scaled pits generated on the Ti surface mimic the microstructure of natural bone and facilitate osteogenic differentiation of stem cells. Besides, such roughening could impose superhydrophilicity to surface of implant which greatly improves the bioactivity of Ti. For instance, the protein in the body fluid could be rapidly adsorbed to the implant surface at the implantation moment and show conformation favorable for cell attachment, proliferation, and osteogenic differentiation [20]. However, a fresh acid etched surface also possesses high surface energy, and therefore carbon containing molecules in the ambient air or packages will easily be adsorbed onto its surface and keep accumulating as storage time increases. Such contamination impairs the excellent wettability and degrades osteoconductivity of rough implants and has become a universal problem that challenges both the producer and surgeons [21–24]. This study demonstrated that hydrophilicity of the bone implants with rough surface could be preserved by slightly soluble bioactive coatings and hence the bioactivity degradation will be overcome.


## 3.2.4.In Vivo Apatite Induction

The surface morphology observation and XRD results of DCPA coated specimens (spray-drying 100 times) after immersion in SBF for 2 weeks were shown in Figures8 and 9. As could be seen from the SEM image, the whole surface of specimens was covered by spherical crystal clusters after immersion. It was the typical surface morphology of bioactive materials after SBF immersion test [25, 26]. In the XRD pattern peaks ascribed to apatite could be observed. Meanwhile, it should be noticed that apatite was of low crystallinity and signals of amorphous phase were found at the diffraction angles from 20° to 40°. In addition, the diffraction peaks of DCPA remained clearly and their relative intensities versus those of Ti substrate did not seem to decrease. It indicated that the DCPA coating did not undergo obvious degradation during the immersion. The SBF immersion experiment tallies within vivo animal experiment very well and is reproducible and easy to be operated, so it is widely used to evaluate the bioactivity of materials. The spontaneous deposition of apatite from SBF within 2 weeks indicated that the DCPA coating fabricated by this method has good bioactivity and it is hopeful of inducing new bone to grow rapidly on the surface of implants and increasing the initial stability of implants.Figure 8
Surface morphology of coated specimens after being immersed in SBF for 2 weeks.Figure 9
Phase analysis of coated specimens after being immersed in SBF for 2 weeks.


## 4. Conclusion

DCPA coating was fabricated on titanium substrate through a novel and simple spray-drying method. The coating was compact, fully covered substrate and was consist of uniform sized DCPA granules that packed together closely. The coating showed good wettability and could keep the property for a long time. After immersion in simulated body fluid for 2 weeks, a large amount of bone-like apatite with low crystallinity was induced on the coating surface, which implied good bioactivity. This method is feasible and efficient, and it is expected to be used for other substrates as long as the surface showed good hydrophilicity.



---

*Source: 8281523-2017-11-02.xml*