# Effects of Self-Assembled Monolayers with Different Chemical Groups on Ovarian Cancer Cell Line BehaviorIn Vitro

Authors: Jie Li; Ting Guan; Chenjun Hao; Lihua Li; Yu Zhang
Journal: Journal of Chemistry
 (2015)

---

## Abstract

In addition to serving as a physical support, the extracellular matrix (ECM) actively influences cell behavior. However, the definitive effects of different chemical structures present in the ECM on cell behavior remain obscure. The current study aimed to investigate the effects of different chemical structures present in the ECM on cellular physiology using the ovarian cancer cell line SKOV-3 as a model. Self-assembled monolayers (SAMs) with different chemical modifications, including methyl (-CH3), hydroxyl (-OH), amino (-NH2), carboxyl (-COOH), and mercapto (-SH) groups, were used as microenvironmental models to explore the effects of different structures on SKOV-3 cells. The cell morphology, cell adhesion, cytotoxicity, and functional alterations in cancer cells cultured on different SAMs were analyzed. The results showed that SKOV-3 cells cultured on -NH2 surfaces exhibited the largest contact area, whereas those on -CH3 surfaces exhibited the smallest contact area and mostly rounded morphologies. Additionally, -NH2 and -COOH promoted cell proliferation and adhesion, whereas CH3 inhibited adhesion, leading to G1 arrest during the cell cycle and resulting in cell apoptosis. This study may provide useful information for reconstruction of the ECM and for controlling cell behavior in related areas of study.


---

## Body

## 1. Introduction

The extracellular matrix (ECM) is a network of biological macromolecules that surrounds cells within tissues. In addition to serving as a physical support, the ECM actively influences cell behavior by providing sites for cell adhesion, establishing soluble factor gradients, and forming interfaces between different cell types within a tissue [1, 2]. Thus, the influence of different chemical structures in the ECM on cell behavior is an important aspect of cell biology.Self-assembled monolayers (SAMs) are stable, ordered, and closely packed ultrathin membranes that are formed by adsorption of an active surfactant onto a solid surface [3]. Many molecules can be assembled onto these substrates, forming SAMs with different functional groups that affect the integral properties of the SAM surfaces [4–6]. A unique feature of SAMs compared with traditional culture substrates, however, is the fact that functionalized alkane thiolates (terminated with a wide variety of chemical functionalities) can be readily synthesized and efficiently packed into SAMs on Au [7]. This chemical variability has provided a unique tool to probe the influence of biomaterial surface chemistry on protein adsorption and thus cell interactions with adsorbed proteins. SAMs are routinely used as cell culture substrates to study the influence of adsorbed proteins on cell function. However, studies have underscored the importance of surface chemistry as a key determinant of cell interactions with nonspecifically adsorbed biomolecules, a feature that may have been challenging to assess using traditional polystyrene substrates due to the inherent complexity associated with modifying the surface chemistry of polymeric materials. The observation that surface chemistry influences biomolecule adsorption and thus cell interactions with adsorbed biomolecules suggests that spatially patterned surfaces with different chemistries may be used to evaluate the interactions of cells with substrates [8].Previous studies have used SAMs to evaluate the effects of surface charge, wettability, and cellular behaviors, including the strength of cell adhesion, the spreading of human fibroblasts and human osteoblast-like cells, and the differentiation of mesenchymal stem cells [9–12]. MC3T3-E1 osteoblast behavior has been reported to be surface chemistry-dependent and to vary according to the individual functional groups present rather than to general surface properties, such as wettability [9]. Sung et al. have investigated the effects of a range of silane-modified surfaces on the differentiation of human mesenchymal stem cells and have found that changes in the surface chemistry of the glass alter the differentiation potentials of the cells [10]. However, considering that SAMs may be applied in the treatment of diseases, and particularly of malignant cancers, the effects of SAMs with different chemical structures warrant further systematic exploration.The present study was conducted to investigate cell behaviors in response to different chemical groups using the SAM technique. Our aim was to demonstrate the relationships between different chemical functional groups in the microenvironment and ovarian cancer cells. Our results are meaningful for reconstructing the ECMin vitro and for identifying interactions that occur between the ECM and ovarian cancer cells.


## 2. Materials and Methods

### 2.1. Preparation of Substrates

Glass wafers (Corning Cat. number 2865-18; 18 × 18 mm) were coated with Au (40 nm) after formation of a Ti layer (40 nm) using an ANELVA L-400EK electron beam evaporator (Canon Anelva Corporation, Kanagawa, Japan). Next, the wafers were cut into 1.0 cm × 0.5 cm chips, rinsed with ethyl alcohol and triple-distilled water, and cleaned with piranha solution (formed from concentrated H2SO4 and 30% H2O2) for 10 min at room temperature. The wafers were then washed with triple-distilled water in an ultrasonic bath. Finally, the Au substrates were immersed in an ethanol solution containing 1 mM 1-dodecanethiol (-CH3; Sigma, USA), 11-hydroxy-1-undecanethiol (-OH; Sigma, USA), 12-mercaptododecanoic acid (-COOH; Sigma, USA), 11-amino-1-undecanethiol hydrochloride (-NH2; Sigma, USA), and 11-undecanedithiol (-SH) for 12 h. Following overnight assembly, the substrates were thoroughly rinsed with triple-distilled water and dried with nitrogen.


### 2.2. Characterization of the Surfaces

To confirm the presence of the surface modifications, the substrates with different chemical groups were characterized by water contact angle measurement (DataPhysics, Germany). The measurements (4 mL of ultrapure H2O) were performed with an OCA20 contact angle system fitted with a digital camera and were analyzed using in-house image analysis software [8, 9].


### 2.3. Cell Culture

Serous ovarian cancer is the most common ovarian cancer type, accounting for approximately 45% of all ovarian cancers, and SKOV-3 is one of its representative cell lines [10]. The SKOV-3 cell line was purchased from the American Type Culture Collection (Maryland, USA) and was grown in McCoy’s 5A medium (Gibco, Life Technologies, Carlsbad, CA, USA) containing 10% fetal bovine serum (FBS; HyClone, Thermo, Fremont, CA, USA), 100 U/mL penicillin, and 100 mg/mL streptomycin in a humidified 5% CO2 atmosphere at 37°C. The medium was changed every 2 days. To investigate the influences of different surfaces on cell growth, modified glass wafers were placed at the bottom of a 24-well plate after ultraviolet disinfection for cell inoculation and culture.Cells were harvested at 75–85% confluence after 5 days of culture and were then seeded onto SAM surfaces that were modified with -OH, -COOH, -NH2, -CH3, or -SH chemical functional groups. As a control, an equivalent volume of cells was inoculated into a Corning culture dish.


### 2.4. Morphological Observations of Cells

The morphologies of cells cultured on the modified SAM surfaces were observed by scanning electron microscopy (SEM; S-3700, HITACHI). After 24 h of culture, the samples were fixed with 3% glutaraldehyde for 5 h, rinsed with PBS, and dehydrated in a graded ethanol series (50%, 70%, 95%, and 100%). Next, the samples were allowed to air-dry and were observed by SEM. Cellular growth was assessed by comparing the morphology of these cells with that of control cells.


### 2.5. Cell Adhesion Assay

4,6-Diamidino-2-phenylindole (DAPI) staining was performed to examine the early-stage adhesion of SKOV-3 cells. Cells were cultured on modified Au surfaces for 30 min, 60 min, or 90 min, fixed with 4% paraformaldehyde for 15 min at 4°C, and then washed three times with PBS. Next, they were stained with 300μL DAPI (10 μg/mL) (Roche, Germany) for 30 min and were photographed using a fluorescence microscope (BX51, Olympus). Five randomly selected fields were counted for each sample. Cell counting was performed by counting the number of nuclei in a certain region, which was selected after comparison between groups.


### 2.6. Focal Adhesion Assembly

SKOV-3 cells were seeded onto the surfaces with different chemical groups. After culturing for 24 h, cells were fixed with 3.7% formaldehyde for 10 min and washed twice with PBS. They were then permeabilized with 0.1% Triton X-100 in PBS for 3 min, and blocking solution was applied for 10 min. Focal adhesion kinase was stained for 20 min using ActinRed (Keygentec, China) according to the manufacturer’s protocol. DAPI was diluted in deionized water to 0.1μg/mL, and staining was carried out for 5 min at room temperature. The samples were then washed and observed using a fluorescence microscope (BX51, Olympus). Cell adhesion was assessed by observing kinase expression.


### 2.7. Cytotoxicity Test

Cytotoxicity was examined by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. SKOV-3 cells were cultured in 48-well plates on the surfaces modified with the five different chemical groups in a 5% CO2 incubator at 37°C. At the indicated time points (1 d, 3 d, and 5 d), 30 μL of a 5 mg/mL solution of MTT (Sigma, USA) was added to 300 μL culture medium and was incubated for 4 h at 37°C. The formazan reaction products were then dissolved in 300 μL dimethyl sulfoxide (DMSO) for 20 min. Optical density was determined using an ELISA plate reader (Thermo, Multiskan GO) at 570 nm.Cell viability was assessed by performing live/dead staining with calcein-AM and PI (Sigma, USA) at 37°C for 24 h. Next, cells attached to the SAMs were washed three times with PBS. Images were obtained using a fluorescence microscope (BX51, Olympus), and red-stained and green-stained cells were counted in five randomly selected fields.


### 2.8. Cell Apoptosis/Necrosis Detection

Apoptosis of SKOV-3 cells was measured using Guava Nexin Reagent (Millipore, USA) according to the manufacturer’s protocol. Briefly, cells cultured for 24 h were collected and resuspended in 100μL of medium supplemented with 1% FBS. The cells were then incubated with 100 μL annexin V-PE and 7-AAD labeling solution (Millipore) for 20 min at room temperature in the dark. The resultant stained cells were analyzed using a Guava easyCyte 5HT flow cytometer. Simultaneously, the proportion of necrotic cells was synchronously analyzed by flow cytometry based on the amount of cell debris present. Data were analyzed using Guava Nexin Software v2.2.2.


### 2.9. Cell Cycle Phase Assay

After being cultured for 24 h, SKOV-3 cells were centrifuged at 1000 rpm for 5 min and were then washed twice with PBS and fixed with 70% ethanol overnight at 4°C. Next, the cells were recentrifuged and washed with PBS. Harvested cells were incubated with PI and RNase A at 37°C for 30 min. The cell cycle phases were analyzed using a Guava easyCyte 5HT flow cytometer (Millipore, USA).


### 2.10. Statistical Analysis

All experiments were repeated three times. All statistical computations were performed with GraphPad Prism 5 software. The data were analyzed using ANOVA, with values considered significantly different atp<0.05.


## 2.1. Preparation of Substrates

Glass wafers (Corning Cat. number 2865-18; 18 × 18 mm) were coated with Au (40 nm) after formation of a Ti layer (40 nm) using an ANELVA L-400EK electron beam evaporator (Canon Anelva Corporation, Kanagawa, Japan). Next, the wafers were cut into 1.0 cm × 0.5 cm chips, rinsed with ethyl alcohol and triple-distilled water, and cleaned with piranha solution (formed from concentrated H2SO4 and 30% H2O2) for 10 min at room temperature. The wafers were then washed with triple-distilled water in an ultrasonic bath. Finally, the Au substrates were immersed in an ethanol solution containing 1 mM 1-dodecanethiol (-CH3; Sigma, USA), 11-hydroxy-1-undecanethiol (-OH; Sigma, USA), 12-mercaptododecanoic acid (-COOH; Sigma, USA), 11-amino-1-undecanethiol hydrochloride (-NH2; Sigma, USA), and 11-undecanedithiol (-SH) for 12 h. Following overnight assembly, the substrates were thoroughly rinsed with triple-distilled water and dried with nitrogen.


## 2.2. Characterization of the Surfaces

To confirm the presence of the surface modifications, the substrates with different chemical groups were characterized by water contact angle measurement (DataPhysics, Germany). The measurements (4 mL of ultrapure H2O) were performed with an OCA20 contact angle system fitted with a digital camera and were analyzed using in-house image analysis software [8, 9].


## 2.3. Cell Culture

Serous ovarian cancer is the most common ovarian cancer type, accounting for approximately 45% of all ovarian cancers, and SKOV-3 is one of its representative cell lines [10]. The SKOV-3 cell line was purchased from the American Type Culture Collection (Maryland, USA) and was grown in McCoy’s 5A medium (Gibco, Life Technologies, Carlsbad, CA, USA) containing 10% fetal bovine serum (FBS; HyClone, Thermo, Fremont, CA, USA), 100 U/mL penicillin, and 100 mg/mL streptomycin in a humidified 5% CO2 atmosphere at 37°C. The medium was changed every 2 days. To investigate the influences of different surfaces on cell growth, modified glass wafers were placed at the bottom of a 24-well plate after ultraviolet disinfection for cell inoculation and culture.Cells were harvested at 75–85% confluence after 5 days of culture and were then seeded onto SAM surfaces that were modified with -OH, -COOH, -NH2, -CH3, or -SH chemical functional groups. As a control, an equivalent volume of cells was inoculated into a Corning culture dish.


## 2.4. Morphological Observations of Cells

The morphologies of cells cultured on the modified SAM surfaces were observed by scanning electron microscopy (SEM; S-3700, HITACHI). After 24 h of culture, the samples were fixed with 3% glutaraldehyde for 5 h, rinsed with PBS, and dehydrated in a graded ethanol series (50%, 70%, 95%, and 100%). Next, the samples were allowed to air-dry and were observed by SEM. Cellular growth was assessed by comparing the morphology of these cells with that of control cells.


## 2.5. Cell Adhesion Assay

4,6-Diamidino-2-phenylindole (DAPI) staining was performed to examine the early-stage adhesion of SKOV-3 cells. Cells were cultured on modified Au surfaces for 30 min, 60 min, or 90 min, fixed with 4% paraformaldehyde for 15 min at 4°C, and then washed three times with PBS. Next, they were stained with 300μL DAPI (10 μg/mL) (Roche, Germany) for 30 min and were photographed using a fluorescence microscope (BX51, Olympus). Five randomly selected fields were counted for each sample. Cell counting was performed by counting the number of nuclei in a certain region, which was selected after comparison between groups.


## 2.6. Focal Adhesion Assembly

SKOV-3 cells were seeded onto the surfaces with different chemical groups. After culturing for 24 h, cells were fixed with 3.7% formaldehyde for 10 min and washed twice with PBS. They were then permeabilized with 0.1% Triton X-100 in PBS for 3 min, and blocking solution was applied for 10 min. Focal adhesion kinase was stained for 20 min using ActinRed (Keygentec, China) according to the manufacturer’s protocol. DAPI was diluted in deionized water to 0.1μg/mL, and staining was carried out for 5 min at room temperature. The samples were then washed and observed using a fluorescence microscope (BX51, Olympus). Cell adhesion was assessed by observing kinase expression.


## 2.7. Cytotoxicity Test

Cytotoxicity was examined by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. SKOV-3 cells were cultured in 48-well plates on the surfaces modified with the five different chemical groups in a 5% CO2 incubator at 37°C. At the indicated time points (1 d, 3 d, and 5 d), 30 μL of a 5 mg/mL solution of MTT (Sigma, USA) was added to 300 μL culture medium and was incubated for 4 h at 37°C. The formazan reaction products were then dissolved in 300 μL dimethyl sulfoxide (DMSO) for 20 min. Optical density was determined using an ELISA plate reader (Thermo, Multiskan GO) at 570 nm.Cell viability was assessed by performing live/dead staining with calcein-AM and PI (Sigma, USA) at 37°C for 24 h. Next, cells attached to the SAMs were washed three times with PBS. Images were obtained using a fluorescence microscope (BX51, Olympus), and red-stained and green-stained cells were counted in five randomly selected fields.


## 2.8. Cell Apoptosis/Necrosis Detection

Apoptosis of SKOV-3 cells was measured using Guava Nexin Reagent (Millipore, USA) according to the manufacturer’s protocol. Briefly, cells cultured for 24 h were collected and resuspended in 100μL of medium supplemented with 1% FBS. The cells were then incubated with 100 μL annexin V-PE and 7-AAD labeling solution (Millipore) for 20 min at room temperature in the dark. The resultant stained cells were analyzed using a Guava easyCyte 5HT flow cytometer. Simultaneously, the proportion of necrotic cells was synchronously analyzed by flow cytometry based on the amount of cell debris present. Data were analyzed using Guava Nexin Software v2.2.2.


## 2.9. Cell Cycle Phase Assay

After being cultured for 24 h, SKOV-3 cells were centrifuged at 1000 rpm for 5 min and were then washed twice with PBS and fixed with 70% ethanol overnight at 4°C. Next, the cells were recentrifuged and washed with PBS. Harvested cells were incubated with PI and RNase A at 37°C for 30 min. The cell cycle phases were analyzed using a Guava easyCyte 5HT flow cytometer (Millipore, USA).


## 2.10. Statistical Analysis

All experiments were repeated three times. All statistical computations were performed with GraphPad Prism 5 software. The data were analyzed using ANOVA, with values considered significantly different atp<0.05.


## 3. Results

### 3.1. Physicochemical Characterization of the SAMs

Characterization of the modified SAM surfaces used in this study via water contact angle measurements has been reported previously [11, 12]. The -CH3 surface was the most hydrophobic among the tested substrates, with a contact angle of 102.78° ± 2.66°. The SAMs terminated with -SH demonstrated a contact angle of 88.33° ± 1.98°, whereas -COOH and -NH2 formed moderately wettable surfaces, with contact angles of 50.13° ± 1.69° and 68.88° ± 3.64°, respectively. The -OH surface was the most hydrophilic, with a contact angle of 41.17° ± 5.97° (Table 1).Table 1
Effects of SAMs with different chemical groups on the water contact angle (x-±s).
Sample
Control
CH3
OH
COOH
NH2
SH
x
-
±
s
91 ± 1.63
102.78 ± 2.66
41.17 ± 5.97
50.13 ± 1.69
68.88 ± 3.64
88.33 ± 1.98
F
321.5
p
<0.001


### 3.2. Morphology and Early Adhesion of SKOV-3 Cells

SEM revealed that cell morphology was altered in response to the surfaces with different chemical functional groups (Figure1). A sparse cell population and spherical cell bodies in a small area were observed for the surfaces with -CH3 terminal groups compared with the other surfaces. In contrast, on the -NH2 surfaces, cells appeared polygonal in shape and were spread out across a large area, with many processes in contact with each other and the surfaces.Figure 1
SEM photographs of SKOV-3 cells cultured on surfaces with different chemical functional groups for 24 h. Scale bar = 50μm.Cell adhesion is the first stage of cell-material interaction, and the quality of this stage influences the subsequent proliferation and growth of cells [13]. The numbers of adherent cells are shown in Figure 2. At 60 and 90 min time points, there were fewer adherent cells on the -CH3 surfaces than on the control surfaces (significant at p<0.01) or on the surfaces with the other terminal chemical groups. There were fewer cells on the -OH and -SH surfaces than on the control surfaces, but no obvious differences were observed at 90 min. At 90 min, the number of cells seeded on the -COOH surfaces was obviously increased (p<0.01). In addition, the number of SKOV-3 cells cultured on the -NH2 surfaces was higher during the incubation period compared with the number of cells cultured on the control (p<0.01). Among the surfaces modified with the five chemical groups, adhesion of SKOV-3 cells appeared to be greatly inhibited on the -CH3-modified surfaces.Figure 2
Cell counts for adherent SKOV-3 cells cultured on substrates containing different chemical groups. Cells were stained with DAPI and observed by fluorescence microscopy after 30 min, 60 min, or 90 min. Scale bar = 100μm. One symbol, p<0.05; 2 symbols, p<0.01; ∗compared with the control at the same time point; #compared with the same substrate at 60 min.The differences in initial cell spreading modulated by the different chemical functional groups were confirmed by analysis of focal adhesion (Figure3). Actin in the focal adhesion plaques was indicated by a red color. Both focal adhesion formation and cell size differed among SKOV-3 cells cultured on the surfaces modified with the different chemical functional groups. Cells on the -OH-modified surfaces had similar diameters as those on the control surfaces (without modification) (between 30 μm and 50 μm). On the -CH3-modified surfaces, the formation of cellular focal adhesions was significantly inhibited. Cell nuclei were not clearly visible, and few focal adhesions and actin stress fibers were observed. Cells on the -CH3 and -SH surfaces were rounded, with sizes of approximately 20–30 μm, whereas those on the surfaces modified with -COOH or -NH2 were polygonal and approximately 40–60 μm wide.Figure 3
Focal adhesions of SKOV-3 cells cultured on surfaces with different chemical functional groups for 24 h. Scale bar = 50μm.


### 3.3. Cytotoxicity Test

The results of MTT assay of SKOV-3 cells cultured on surfaces modified with the different chemical groups for 1 d, 3 d, or 5 d are shown in Figure4. From day 1 to day 3, there was a nonsignificant difference in the proliferation of SKOV-3 cells on the different surfaces. On day 5, cells on the -CH3 surfaces showed the lowest proliferation rate among all of the groups (versus the control, p<0.01). However, the number of cells on the -NH2 surfaces significantly increased compared with that of cells on the control surfaces. The -OH, -COOH, -NH2, and -SH modifications appeared to promote cell proliferation over a longer culture period, but their proliferation rates did not significantly differ compared with that of the control. The proliferation capacities of SKOV-3 cells on the SAMs with the different chemical groups can be ordered as follows: -NH2 > -COOH > -OH > -SH > -CH3.Figure 4
MTT reduction by SKOV-3 cells cultured on surfaces modified with different chemical groups for 1 d, 3 d, or 5 d. The error bars represent the mean + SD forn=3. One symbol, p<0.05; 2 symbols, p<0.01; ∗compared with the control on the same day; #compared with the same substrate on day 3.


### 3.4. Live/Dead Assay

The effects of the different chemical groups on cytotoxicity were also evaluated by live/dead viability/cytotoxicity staining. Representative fluorescence micrographs were chosen for visualization of live (green) and dead (red) cells, as shown in Figure5. In the control group (without modification), no nonviable (red) cells were observed. Rare viable (green) cells and several nonviable (red) cells were observed on the surfaces with -CH3 groups after incubation for 24 h. No nonviable cells and denser populations of viable cells were observed on the -OH, -COOH, and -NH2 surfaces. There were only two nonviable cells on the -SH surface. These observations indicated that the -CH3 functional group induced cell toxicity, whereas the -NH2 and -COOH groups produced little cell toxicity.Figure 5
Fluorescence micrographs of live/dead dye-stained SKOV-3 cells cultured on substrates modified with different chemical groups for 24 h. Scale bar = 50μm. Green cells are viable, and red cells are nonviable.


### 3.5. Cell Apoptosis Assay

Abnormal cell apoptosis and cell death are the characteristics of cancer cells evaluated using annexin V-PE and 7-ADD. As shown in Figure6, approximately 7.5% of cells cultured on the -CH3-modified surfaces were apoptotic (p<0.01) as were approximately 10% of those cultured on the -OH-modified surfaces (p<0.01). Both of these proportions were significantly greater than that of the control (3%). The rate of death of cells cultured on the -SH-modified surfaces did not significantly differ from that of cells cultured on the control surfaces. The -NH2 group clearly decreased SKOV-3 cell necrosis, with 8% dead cells compared with 12.5% dead control cells (p<0.05).Figure 6
SKOV-3 cells were cultured on substrates with different chemical groups for 24 h. The percentage of annexinV(+)/PI(-) cells indicates apoptosis. The percentage of annexin V(+)/PI(+) cells indicates necrosis. One symbol, p<0.05; 2 symbols, p<0.01; ∗compared with the control.


### 3.6. Cell Cycle Assay

The results of cell cycle analysis of SKOV-3 cells cultured on the surfaces modified with the different chemical groups are shown in Figure7. The percentages of SKOV-3 cells in the mitotic phase (G2/M) during culturing on the -CH3- and -OH-modified surfaces were 11.94% and 13.50%, respectively, which were significantly lower than that for cells cultured on the control surfaces (15.99%) (both p<0.01). These findings indicated that the -CH3 chemical group inhibited the S-to-G2 phase cell cycle transition, leading to G1 arrest. Compared with cells on the control surfaces, those on the surfaces modified with -OH, -NH2, and -COOH groups did not significantly differ in the proportions of cells in the mitotic phase (G2/M), which were 15.11%, 14.89%, and 15.43%, respectively (all p>0.05).Figure 7
Cell cycle assay of asynchronous SKOV-3 cells cultured on substrates with different chemical groups for 24 h and analyzed by flow cytometry.p∗<0.05.


## 3.1. Physicochemical Characterization of the SAMs

Characterization of the modified SAM surfaces used in this study via water contact angle measurements has been reported previously [11, 12]. The -CH3 surface was the most hydrophobic among the tested substrates, with a contact angle of 102.78° ± 2.66°. The SAMs terminated with -SH demonstrated a contact angle of 88.33° ± 1.98°, whereas -COOH and -NH2 formed moderately wettable surfaces, with contact angles of 50.13° ± 1.69° and 68.88° ± 3.64°, respectively. The -OH surface was the most hydrophilic, with a contact angle of 41.17° ± 5.97° (Table 1).Table 1
Effects of SAMs with different chemical groups on the water contact angle (x-±s).
Sample
Control
CH3
OH
COOH
NH2
SH
x
-
±
s
91 ± 1.63
102.78 ± 2.66
41.17 ± 5.97
50.13 ± 1.69
68.88 ± 3.64
88.33 ± 1.98
F
321.5
p
<0.001


## 3.2. Morphology and Early Adhesion of SKOV-3 Cells

SEM revealed that cell morphology was altered in response to the surfaces with different chemical functional groups (Figure1). A sparse cell population and spherical cell bodies in a small area were observed for the surfaces with -CH3 terminal groups compared with the other surfaces. In contrast, on the -NH2 surfaces, cells appeared polygonal in shape and were spread out across a large area, with many processes in contact with each other and the surfaces.Figure 1
SEM photographs of SKOV-3 cells cultured on surfaces with different chemical functional groups for 24 h. Scale bar = 50μm.Cell adhesion is the first stage of cell-material interaction, and the quality of this stage influences the subsequent proliferation and growth of cells [13]. The numbers of adherent cells are shown in Figure 2. At 60 and 90 min time points, there were fewer adherent cells on the -CH3 surfaces than on the control surfaces (significant at p<0.01) or on the surfaces with the other terminal chemical groups. There were fewer cells on the -OH and -SH surfaces than on the control surfaces, but no obvious differences were observed at 90 min. At 90 min, the number of cells seeded on the -COOH surfaces was obviously increased (p<0.01). In addition, the number of SKOV-3 cells cultured on the -NH2 surfaces was higher during the incubation period compared with the number of cells cultured on the control (p<0.01). Among the surfaces modified with the five chemical groups, adhesion of SKOV-3 cells appeared to be greatly inhibited on the -CH3-modified surfaces.Figure 2
Cell counts for adherent SKOV-3 cells cultured on substrates containing different chemical groups. Cells were stained with DAPI and observed by fluorescence microscopy after 30 min, 60 min, or 90 min. Scale bar = 100μm. One symbol, p<0.05; 2 symbols, p<0.01; ∗compared with the control at the same time point; #compared with the same substrate at 60 min.The differences in initial cell spreading modulated by the different chemical functional groups were confirmed by analysis of focal adhesion (Figure3). Actin in the focal adhesion plaques was indicated by a red color. Both focal adhesion formation and cell size differed among SKOV-3 cells cultured on the surfaces modified with the different chemical functional groups. Cells on the -OH-modified surfaces had similar diameters as those on the control surfaces (without modification) (between 30 μm and 50 μm). On the -CH3-modified surfaces, the formation of cellular focal adhesions was significantly inhibited. Cell nuclei were not clearly visible, and few focal adhesions and actin stress fibers were observed. Cells on the -CH3 and -SH surfaces were rounded, with sizes of approximately 20–30 μm, whereas those on the surfaces modified with -COOH or -NH2 were polygonal and approximately 40–60 μm wide.Figure 3
Focal adhesions of SKOV-3 cells cultured on surfaces with different chemical functional groups for 24 h. Scale bar = 50μm.


## 3.3. Cytotoxicity Test

The results of MTT assay of SKOV-3 cells cultured on surfaces modified with the different chemical groups for 1 d, 3 d, or 5 d are shown in Figure4. From day 1 to day 3, there was a nonsignificant difference in the proliferation of SKOV-3 cells on the different surfaces. On day 5, cells on the -CH3 surfaces showed the lowest proliferation rate among all of the groups (versus the control, p<0.01). However, the number of cells on the -NH2 surfaces significantly increased compared with that of cells on the control surfaces. The -OH, -COOH, -NH2, and -SH modifications appeared to promote cell proliferation over a longer culture period, but their proliferation rates did not significantly differ compared with that of the control. The proliferation capacities of SKOV-3 cells on the SAMs with the different chemical groups can be ordered as follows: -NH2 > -COOH > -OH > -SH > -CH3.Figure 4
MTT reduction by SKOV-3 cells cultured on surfaces modified with different chemical groups for 1 d, 3 d, or 5 d. The error bars represent the mean + SD forn=3. One symbol, p<0.05; 2 symbols, p<0.01; ∗compared with the control on the same day; #compared with the same substrate on day 3.


## 3.4. Live/Dead Assay

The effects of the different chemical groups on cytotoxicity were also evaluated by live/dead viability/cytotoxicity staining. Representative fluorescence micrographs were chosen for visualization of live (green) and dead (red) cells, as shown in Figure5. In the control group (without modification), no nonviable (red) cells were observed. Rare viable (green) cells and several nonviable (red) cells were observed on the surfaces with -CH3 groups after incubation for 24 h. No nonviable cells and denser populations of viable cells were observed on the -OH, -COOH, and -NH2 surfaces. There were only two nonviable cells on the -SH surface. These observations indicated that the -CH3 functional group induced cell toxicity, whereas the -NH2 and -COOH groups produced little cell toxicity.Figure 5
Fluorescence micrographs of live/dead dye-stained SKOV-3 cells cultured on substrates modified with different chemical groups for 24 h. Scale bar = 50μm. Green cells are viable, and red cells are nonviable.


## 3.5. Cell Apoptosis Assay

Abnormal cell apoptosis and cell death are the characteristics of cancer cells evaluated using annexin V-PE and 7-ADD. As shown in Figure6, approximately 7.5% of cells cultured on the -CH3-modified surfaces were apoptotic (p<0.01) as were approximately 10% of those cultured on the -OH-modified surfaces (p<0.01). Both of these proportions were significantly greater than that of the control (3%). The rate of death of cells cultured on the -SH-modified surfaces did not significantly differ from that of cells cultured on the control surfaces. The -NH2 group clearly decreased SKOV-3 cell necrosis, with 8% dead cells compared with 12.5% dead control cells (p<0.05).Figure 6
SKOV-3 cells were cultured on substrates with different chemical groups for 24 h. The percentage of annexinV(+)/PI(-) cells indicates apoptosis. The percentage of annexin V(+)/PI(+) cells indicates necrosis. One symbol, p<0.05; 2 symbols, p<0.01; ∗compared with the control.


## 3.6. Cell Cycle Assay

The results of cell cycle analysis of SKOV-3 cells cultured on the surfaces modified with the different chemical groups are shown in Figure7. The percentages of SKOV-3 cells in the mitotic phase (G2/M) during culturing on the -CH3- and -OH-modified surfaces were 11.94% and 13.50%, respectively, which were significantly lower than that for cells cultured on the control surfaces (15.99%) (both p<0.01). These findings indicated that the -CH3 chemical group inhibited the S-to-G2 phase cell cycle transition, leading to G1 arrest. Compared with cells on the control surfaces, those on the surfaces modified with -OH, -NH2, and -COOH groups did not significantly differ in the proportions of cells in the mitotic phase (G2/M), which were 15.11%, 14.89%, and 15.43%, respectively (all p>0.05).Figure 7
Cell cycle assay of asynchronous SKOV-3 cells cultured on substrates with different chemical groups for 24 h and analyzed by flow cytometry.p∗<0.05.


## 4. Discussion

This study revealed that the morphology, adhesion, proliferation, and apoptosis of SKOV-3 cells differed in response to different chemical groups.Surface wettability was shown to be an important factor in protein adhesion to biomaterial surfaces. The best surfaces for cell adhesion and growth have the most suitable hydrophilic/hydrophobic balance. The optimal value varies for different types of cells. Excessively hydrophilic surfaces are not conducive to protein adsorption. In this paper, the water contact angle measurements revealed that -CH3 groups cause surfaces to be hydrophobic and that -NH2 and -COOH cause them to be moderately wettable, whereas -OH-modified surfaces are the most hydrophilic. SKOV-3 cells assumed a polygonal shape when cultured on surfaces with -NH2 terminal functional groups, and the cells expanded to larger areas and extended more processes on these surfaces than on the other surfaces. Our results showed that both -COOH and -NH2 terminal functional groups promoted adhesion of SKOV-3 cells, which is consistent with the findings of Jal et al. [14].It has been well established that the behavior of adherent cells is related to their shapes [15–20]. Cells with nonflattened and round shapes are likely to become apoptotic, and under these conditions cell proliferation is usually negatively affected [19, 21]. In contrast, healthy cells have well-spread and polygonal shapes [16, 20]. In the current study, the proliferative capacities of SKOV-3 cells on the SAMs with the different chemical groups can be ordered as follows: -NH2 > -COOH > -OH > -SH > -CH3. The -NH2- and -COOH-functionalized surfaces promoted SKOV-3 cell proliferation, whereas the -CH3- and -SH-functionalized surfaces inhibited proliferation. Viability/cytotoxicity staining also indicated that the -CH3 group was somewhat toxic to cells. In addition, all of the surfaces except for the -SH-coated surfaces caused an increase in the proportion of necrotic SKOV-3 cells. This phenomenon has been previously reported in the literature, and the underlying mechanism warrants further exploration in the future.Our results indicated that the -CH3 group may have caused apoptosis by inhibiting the S-to-G2 phase transition of the cell cycle, leading to G1 arrest, whereas the -NH2 group caused an obvious decrease in SKOV-3 cell necrosis. These results are consistent with the relationship between cell morphology and cell behavior discussed above.Chemical groups play an important role in intercellular communication [5, 22]. Previous studies have elucidated the different effects of chemical functional groups on tumor cells [23]. The -OH group has been reported to have positive effects on macrophage adhesion [13]. Further, human osteoblastoma cells show much better adhesion and spreading across larger areas on surfaces terminated with -COOH, -OH, or -NH2 than on hydrophobic surfaces. Yan et al. have shown that MCF-7 cells cultured on -SH- or -OH-modified substrates have the lowest viability and migratory capacity [24]. The different interactions of chemical functional groups with cells should play vital roles in this respect. In addition, there may be communication between -CH3 groups and ovarian cancer cells.The results of our study suggest that -CH3 inhibits proliferation and adhesion of cells and promotes apoptosis and necrosis of tumor cells, whereas -NH2 and -COOH promote cell adhesion. However, how cells identify the physical and chemical characteristics of the ECM has not been reported to the best of our knowledge. Presumably, adhesion and migration of cells primarily depend upon interactions between the molecules on their surfaces (particularly integrin) and those on the surfaces of vectors (the Arg-Gly-Asp (RGD) repeat sequence of fibronectin in the ECM predominatesin vivo) [25]. Arginine contains NH residues, and aspartate contains COOH residues. Nevertheless, further studies are needed to understand the signaling pathways by which cell behavior is affected by the chemical groups present on a substrate.This study has some limitations. First, because it was a preliminary study and the surfaces used are not produced and distributed on a large scale, we did not perform strict verification of the uniformity of the glass wafers (although they were from the same batch). Second, we did not use synchronous cells due to a lack of a sufficient number of synchronized cells, which may have influenced the outcomes of this study. Third, the experiments in the present study were performed using the ovarian cancer cell line SKOV-3. Whether our findings are applicable to other cell lines requires further exploration.This study investigated how the fate of SKOV-3 cells, including their morphology, adhesion, proliferation, and apoptosis, was affected by the presence of the -CH3, -OH, -COOH, -NH2, and -SH groups on culture substrates. -NH2-terminated surfaces may support preferential binding of actin to increase cell adhesion because cells cultured on -NH2 grew across a larger area than those on the other surfaces. Further, the -CH3-terminated surfaces significantly inhibited cell proliferation due to poor cell adhesion, high cytotoxicity, and promotion of apoptosis. These results highlight the important effects of the chemical groups present on substrates on the fate of cancer cells and suggest that cell culture substrate modifications are useful for controlling cell behaviorin vitro.



---

*Source: 784626-2015-09-03.xml*