# Sonication Enhanced Removal of Nickel and Cobalt Ions from Polluted Water Using an Iron Based Sorbent

Authors: Zari Hooshyar; Ghasem Rezanejade Bardajee; Yousef Ghayeb
Journal: Journal of Chemistry
 (2013)

---

## Abstract

The effect of sonication time on removal efficiency of Ni2+ and Co2+ from wastewater in the presence of zero valence iron (ZVI) nanoparticles is described. The results showed that the presence of cobalt ions in the solution enhances the removal efficiency of nickel by ZVI nanoparticles to about 64% which is one of the advantages of this protocol.


---

## Body

## 1. Introduction

Zero valence materials are important for the PRB (permeable reactive barrier) facilities. Over the past decades, PRBs have been developed and used to treat contaminated ground water by different contaminants [1–8]. In these barriers, zero valence iron (ZVI) can be used as a reactive material to reduce and stabilize different types of ions. Compared to powder or granular ZVI, nanoscale ZVI can largely increase the uptake capacity due to the high surface to volume ratio [9]. This reactivity can be improved about 30 times relative to iron powders [10]. High surface reactivity of ZVI nanoparticles have been used for in situ remediation of several kinds of contaminants. Most investigations have been originally focused on the remediation of chlorinated hydrocarbons such as tetrachloroethene (PCE), trichloroethene (TCE), carbon tetrachloride (CT), organochlorine pesticides (like DDT and lindane), and nitro aromatic compounds in aqueous streams [11–20]. Recent investigations have shown that heavy metals including arsenic, lead, chromium, cadmium, uranium, molybdenum, and mercury also can be reduced by ZVI nanoparticles as well [21–29]. ZVI nanoparticles remove chlorinated contaminants of aqueous media by reductive dechlorination and eliminate aqueous metal ions by their reduction to an insoluble form. A layer of ferrous hydroxide is formed in aqueous solution and hydrogen gas is liberated. As a result, ZVI particles typically have a core-shell structure with the core being zero valence iron (Fe0) and the shell being iron oxides/hydroxides due to the iron oxidation. This structure presents the ZVI nanoparticles with high surface and unique redox potential properties for removal and transformation of contaminants [25, 27, 28]. The removal efficiency is related to the surface area or the size of used ZVI nanoparticles, the pH, and composition of the solution. Acoustic cavitations can increase the surface area of the reactive solids by rupture of the particles. Sonication in the presence of Fe0 has been explored for the dechlorination of carbon tetrachloride. Results showed that the coupled ultrasound and iron systems compare to the degradation by direct reaction with Fe0 enhanced the overall degradation rate about 40%. The enhancement was attributed to the continuous cleaning and chemical activation of the Fe0 surfaces by the combined chemical and physical effects of acoustic cavitations, to shatter the particles, and accelerate mass transport of reacting substances to the Fe0 surfaces [28].Herein, we describe the treatment of common ground water heavy metals pollutants such as Ni2+ and Co2+ by ZVI nanoparticles in separate as well as mixture batch experiments, respectively. Nickel and cobalt were selected as target substances, because they have been listed in the priority pollutants by the United States Environmental Protection Agency as a persistent inorganic pollutant. While the removal of Ni(II) from wastewater by ZVI nanoparticles has been widely investigated, very little works have been performed on the removal of Co(II), Ni(II), and their mixtures from wastewater. In addition, there is no report on the application of sonication in these systems. In this regard, particular attention is devoted to the effect of sonication on the removal of nickel and cobalt pollutants by ZVI nanoparticles near neutral pH value.


## 2. Experiments

### 2.1. Materials and Instruments

All chemicals, including nickel nitrate (Ni(NO3)2  · 6H2O, 99%, Merck), cobalt nitrate (Co(NO3)2  · 6H2O, 99%, Merck), and iron nanoparticles (Fe0, 97%, 12 nm diameter, spherical, Research Institute of Petroleum Industry, Iran), were used as received. Sonications were performed in a Sonopuls-HD3200 (Bandelin, Germany) consisting of microtip MS 73, 3 mm diameter at 70% amplitude with a frequency of 20 kHz and a nominal power 200 W.


### 2.2. Experiment Procedure

Solutions of nickel and cobalt with the same initial concentrations (50 mg/L) were prepared separately in glass reactor and ZVI nanoparticles (0.03 gr) were added to each one at ambient temperature (22–25°C). The nanoparticles were dispersed by sonications from 0 to 40 minutes with 5 minutes intervals to obtain the optimum sonication time for the highest removal efficiency (Figure1). Then, the absorbed metals on the surface of ZVI nanoparticles were separated by magnetic field (0.5 Tesla) and lastly the suspension was centrifuged for one hour at 3600 rpm. The concentration of the residual metal ions in the solution was measured with an atomic absorption (AA) spectrometer (Perkin-Elmer AA 2380) using standard absorption conditions (Figure 1).Figure 1
The effect of sonication times on the removal of Ni2+ (50 mg/L) in the presence of ZVI nanoparticles (0.03 gr/L).To investigate the effect of Co2+ on the removal of Ni+2 and to determine the optimum sonication time, six solutions containing, the same concentration of Ni+2 (50 mg/L) and various concentrations of Co+2 (5, 15, 25, 35, 50, and 75 mg/L) were prepared (Figure 2).Figure 2
The effect of sonication times on the removal of Co2+ (50 mg/L) in the presence of ZVI nanoparticles (0.03 gr/L).


## 2.1. Materials and Instruments

All chemicals, including nickel nitrate (Ni(NO3)2  · 6H2O, 99%, Merck), cobalt nitrate (Co(NO3)2  · 6H2O, 99%, Merck), and iron nanoparticles (Fe0, 97%, 12 nm diameter, spherical, Research Institute of Petroleum Industry, Iran), were used as received. Sonications were performed in a Sonopuls-HD3200 (Bandelin, Germany) consisting of microtip MS 73, 3 mm diameter at 70% amplitude with a frequency of 20 kHz and a nominal power 200 W.


## 2.2. Experiment Procedure

Solutions of nickel and cobalt with the same initial concentrations (50 mg/L) were prepared separately in glass reactor and ZVI nanoparticles (0.03 gr) were added to each one at ambient temperature (22–25°C). The nanoparticles were dispersed by sonications from 0 to 40 minutes with 5 minutes intervals to obtain the optimum sonication time for the highest removal efficiency (Figure1). Then, the absorbed metals on the surface of ZVI nanoparticles were separated by magnetic field (0.5 Tesla) and lastly the suspension was centrifuged for one hour at 3600 rpm. The concentration of the residual metal ions in the solution was measured with an atomic absorption (AA) spectrometer (Perkin-Elmer AA 2380) using standard absorption conditions (Figure 1).Figure 1
The effect of sonication times on the removal of Ni2+ (50 mg/L) in the presence of ZVI nanoparticles (0.03 gr/L).To investigate the effect of Co2+ on the removal of Ni+2 and to determine the optimum sonication time, six solutions containing, the same concentration of Ni+2 (50 mg/L) and various concentrations of Co+2 (5, 15, 25, 35, 50, and 75 mg/L) were prepared (Figure 2).Figure 2
The effect of sonication times on the removal of Co2+ (50 mg/L) in the presence of ZVI nanoparticles (0.03 gr/L).


## 3. Results and Discussion

Figures1 and 2 show the effect of sonication times on the removal efficiency of Ni2+ and CO2+ in solutions with concentration of 50 mg/L by ZVI nanoparticles, respectively. As one can see, the maximum removal efficiency of Ni2+ is about 38% at 20 minutes of sonication while this value for Co+2 is about 59% at 30 minutes. With increasing the sonication time, the nanoclusters break down and subsequently their size decreases to reach a minimum value (optimum time). At higher sonication times, the size of nanoparticles increases again due to the aggregation of nanoparticles. This behavior was previously reported by Kwak and Kim [31] for nanoclusters of CuO at different sonication times. In other words, the ratio of surface to volume of the nanoclusters enhances as the ZVI nanoclusters break down.Another feature in Figures1 and 2 is the difference between the maximum removal efficiencies of Co2+ (59%) and Ni2+ (38%). This discrepancy may be attributed to three parameters that effect on the removal efficiency of metal ions. First, according to Table 1, the standard reduction potential of Co2+ is lower than Ni2+. Therefore, one can expect that nickel ions have more reduction to cobalt ions.Table 1
Standard reduction potentials at 25°C [31].
Element
Half-cell reaction
E
0 (V)
Iron (Fe)
Fe2+ + 2e−→ Fe
−0.44
Nickel (Ni)
Ni2+ + 2e−→ Ni
−0.23
Cobalt (Co)
Co2+ + 2e−→ Co
−0.28Secondly, the adsorption of smaller cation will be more effective than the larger one, on the same surface. Comparing the radius of nickel and cobalt ions (55 and 69 ppm for Ni2+ at coordination number (CN) of IV and VI, 58 and 74 pm for Co2+ at CN of IV and VI, resp.) shows that the radius of these ions has not any role in this enhancement. Finally, due to the more magnetism of Co2+ than Ni2+ (μCo2+=15 BM, μNi2+=8 BM), the more adsorption of Co2+ on the surface of iron ZVI nanoparticles is expected. Since the ZVI nanoparticles have permanent magnetism, more magnetism of Co2+ plays an important role on the removal efficiency of these ions in their solutions.Furthermore, there is dissimilarity in optimum sonication times for Ni2+and CO2+, which are about 20 and 30 minutes, respectively (Figures 1 and 2). The more optimum sonication time for CO2+ can be attributed to the kinetic mechanism of electron transfer from ZVI nanoparticles to Co2+ ions.In the next step, the amount of ZVI nanoparticles was increased from 0.03 to 0.8 gr/L while the concentrations of nickel and cobalt solutions were kept constant (50 mg/L). By increasing the amount of ZVI nanoparticles, the removal efficiency was increased so that 0.8 gr ZVI nanoparticles can remove all of the cobalt and nickel ions from their solutions (Table2).Table 2
Comparative applicability of ZVI nanoparticles for removal of nickel and cobalt ions.
Surface area of nanoparticles (m2/g)
Initial concentration  of ions (mg/L)
Ion
Removal percentage
Amount ofnanoparticle (g/L)
Reference
55–75
50
Ni2+
100
0.8
Present work
55–75
50
Co2+
100
0.8
Present work
35
100
Ni2+
100
5
[28]
—
100
Ni2+
71
5
[25]
14.2
50
Co2+
96
1.25
[31]We have compared some previously reported data and ours for the removal of nickel and cobalt ions in terms of the surface area, initial concentrations, size, and amounts of ZVI nanoparticles (Table2). As one can see, our system shows a wide applicability and a very good comparability with previously reported data. The improved performance may be attributed to the smaller size and the higher surface to volume ratio of our ZVI nanoparticles and the use of sonication.In continue, the effect of Co2+ on the removal of Ni2+ was investigated. Six samples containing constant concentrations of Ni2+ (50 mg/L) and different concentrations of Co2+ (15 to 75 mg/L) were prepared and sonicated at different times (5–40 minutes). Figure 3 presents the effect of sonication time on the adsorption of Ni2+ (50 mg/L) and Co2+ (15 mg/L) in the same solution in the presence of ZVI nanoparticles (0.03 gr/L).Figure 3
The effect of sonication times on the removal of Ni2+ (50 mg/L) and Co2+ (15 mg/L) in solutions containing both ions by ZVI nanoparticles (0.03 gr/L).The removal efficiency of these ions along with the optimum sonication times are summarized in Table3. As one can see, the Ni2+ adsorption was increased at initial Co2+ concentrations and then became constant at around 25 mg/L. The maximum removal efficiency of Ni2+ is as high as its amount in Figure 1. Increasing the amount of cobalt ions had less effect on the removal efficiency of nickel (Figures 1 and 3), and the optimum sonication time was changed from 20 minutes to 30 minutes. Although the overall removal efficiency (regarding to both Ni2+ and Co2+ ions) is increased, but the level of cobalt adsorption is less than when we have only cobalt ions in the solution (Table 3). It seems that the adsorption mechanism of Co2+ and Ni2+ from Co2+ and Ni2+ solution is different from the adsorption mechanism of Co2+ and Ni2+ from pure Co2+or Ni2+ solution. In the Co2+ and Ni2+ solution, Co2+ rapidly surround the ZVI nanoparticles and redox reactions occurred. In this state, a lot of Co0 tend again to do redox reactions with Ni2+. Therefore, removal efficiency of Ni2+ is more than removal efficiency of Co2+. In other words, initial layer of cobalt around ZVI nanoparticles increases the removal efficiency of Ni2+ at the specific time. The above results clearly indicated that Ni2+ and Co2+ removal by ZVI nanoparticles was significantly influenced by the ions in the reacting solution.Table 3
The removal efficiency of nickel and cobalt ions in solutions containing both ions by applying sonication in optimum times.
Entry
Initial concentration of Ni2+ (mg/L)
Initial concentration of Co2+(mg/L)
Optimum sonication time (min)
Removed Ni2+(mg/L)
Removed Co2+(mg/L)
1
50
5
30
25
5
2
50
15
30
30
10
3
50
25
30
30
14
4
50
35
30
30
13
5
50
50
30
31
14
6
50
75
30
32
13


## 4. Conclusions

In summary, the nickel and cobalt ions were removed effectively by sonicating the aqueous solutions containing one of the entitled ions in the presence of ZVI nanoparticles. The procedure was simple, quick, and economical and removal efficiency was comparable with previously reported methods. Optimum sonication times for removal of nickel and cobalt ions were 20 and 30 minutes, respectively. Compared to Ni2+, Co2+ removal is favored probably due to its more magnetism. In the presence of cobalt ions, the highest removal efficiency of nickel ions by ZVI nanoparticles was observed to about 64% which is one of the advantages of this methodology. It should be noted that the presence of both metals in the solution affects on the adsorption efficiency, depending on the initial ion concentrations. For example, removal efficiency of cobalt ions in solutions containing both cobalt and nickel ions decreased significantly.



---

*Source: 786954-2012-10-16.xml*