# Hydrothermal Growth and Hydrogen Selective Sensing of Nickel Oxide Nanowires

Authors: Thi Thanh Le Dang; Matteo Tonezzer; Van Hieu Nguyen
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Low cost synthesis of nanostructured metal oxides for gas sensing application at low temperature is nowadays of crucial importance in many fields. Herein, NiO p-type semiconducting nanowires with polycrystalline structure were prepared by a facile and scalable hydrothermal method. Morphology and crystal structure of the NiO nanowires were investigated by scan electron microscopy, X-ray diffraction, and transmission electron microscopy. The nanostructured material was then tested as hydrogen sensor showing very good performance in terms of sensor response, stability, absence of drifts, and speed of response and recovery. The selectivity of the NiO sensor to hydrogen towards other gases (ethanol, ammonia, and liquefied petroleum gas) was found to be good.


---

## Body

## 1. Introduction

Metal oxides are very good sensing materials. In the last decade, metal oxide nanostructures have been extensively studied in order to optimize them for several applications, including gas sensing. Semiconducting n-type metal oxides (mainly SnO2 and ZnO) have been investigated as gas sensing material very deeper than their p-type counterparts. Recently, also p-type metal oxides are being studied, and among them nickel oxide (NiO). Tuning the size and shape of nanostructured materials is a commonly employed strategy to optimize their performance due to their structure-dependent properties [1–3]. Nanowires, one of the quasi-monodimensional (1D) nanostructures, are perfect building blocks for functional nanodevices and represent the smallest dimension for efficient electron and hole transport [4]. As an important p-type semiconductor with wide band gap energy in the range of 3.6–4.0 eV [5], NiO has been considered as a promising material due to its excellent chemical stability and pronounced electrical properties with potential applications in a wide range of fields, including catalysis [6], electrode materials for lithium ion batteries [7], photovoltaic devices [8], fuel cell electrodes, electrochemical supercapacitors [9], electrochromic films [10], magnetic materials [11], and gas sensors [12–14]. To date, various NiO nanostructures have been grown, including nanoparticles [15], nanorods [16], nanotubes [17], and nanosheets [18].Many growth methods such as aqueous solution [19, 20], electrochemical deposition [21, 22], vapor-based metal etching oxidation method [23], and dehydration method [24] have been used to fabricate NiO nanowires. However, most of the deposition techniques used require strict parameters like high temperature, high vacuum, and complex reactions, leading to expensive processes and preventing a wide use of these materials. Compared to other methods, hydrothermal synthetic method has attracted the broadest attention for its simple operation and low power consumption.Herein, we report on the growth of nickel oxalate hydrate (NiC2O4 · 2H2O) nanowires by the hydrothermal method and their thermal decomposition during calcination at 500°C, obtaining polycrystalline NiO nanowires. Morphology and structure of the nickel oxide nanowires are characterized, and their gas sensing properties to detect hydrogen gas are investigated.


## 2. Materials and Methods

### 2.1. Synthesis of Nickel Oxide Nanowires

The NiO nanowires have been grown via a two-step deposition consisting in a hydrothermal method followed by an annealing at 500°C. All the chemicals used in our experiments were of analytical reagent grade and were directly used without further purification. In a typical procedure, 0.474 g of NiCl2 · 6H2O (Sigma-Aldrich, Germany) was dissolved into a mixture of 32 mL ethylene glycol (EG, Sigma-Aldrich) and 18 mL deionized water in a beaker under continuous magnetic stirring at room temperature. Then 0.1206 g of Na2C2O4 was added into the beaker. Half an hour of continuous magnetic stirring was carried out to ensure that Ni2+ ions were dispersed homogeneously in the solution. The clear solution was transferred into a Teflon-lined stainless steel autoclave of 100 mL capacity. The autoclave was sealed and heated at 200°C for 24 h. After the heating treatment, the autoclave was let cooling to room temperature naturally. The product was collected by centrifugation, washed three times with deionized water and absolute ethanol, respectively, and then dried naturally in air. As a result, a blue–green product was obtained.The polycrystalline NiO nanowires were obtained by the calcination of this blue-green precursor, consisting in nickel oxalate hydrate (NiC2O4 · 2H2O) short nanowires, at 500°C.The as-prepared material and the calcinated nanowires were characterized and analyzed by using X-ray diffraction (XRD), scanning electron microscopy (SEM). The XRD analysis was performed using a Bruker D5005 X-ray diffractometer withCuKα1 radiation (λ = 1.5406 Å) at 40 kV and 40 mA. SEM images were obtained using a JEOL7600 scanning electron microscope at an accelerating voltage of 20 kV. Transmission electron microscopy (TEM) and electron diffraction images of the calcinated material were obtained using a JEOL JEM-2100 transmission electron microscope at an accelerating voltage of 200 kV.


### 2.2. Sensing Devices Fabrication

The fabrication of sensing devices consists of a 2-step procedure. First, 1 mg of as-prepared nickel oxide nanowires was dispersed in ethanol solution under ultrasonic vibration for 3 min. The solution was then dropped onto interdigitated comb Pt/Ti electrodes on thermally oxidized silicon substrate. The interdigitated Pt/Ti contacts were previously deposited onto the SiO2/Si substrates by sputtering and conventional optical lithography technique. The whole device is 2 mm × 6 mm, while the two electrodes consisted in 18 pairs of fingers, each 800 μm long and 20 μm wide. The gap between two contiguous fingers is 50 μm. After the deposition of nickel oxide nanowires, the sensor was heated to 500°C at a rate of 1.0°C min−1 in a furnace and then maintained for 2 h in order to increase stability and adhesion between active material and metal electrodes.


### 2.3. Gas Sensing Measurements

The NiO nanowires sensing properties were measured in dynamic conditions, in which the dilution (dry air) and the tested gas were flowing continuously through the sensing chamber at a total flow rate of 500 sccm. The apparatus was home-built and included a test chamber, a sensor holder which can be heated up to 500°C, and mass flow controllers (connected to high purity calibrated bottles).The sensors resistance was measured using a Keithley 2400 multimeter connected to a data acquisition system (LabView, National Instruments). The samples, biased with a voltage of 5 V and operated in air, showed a good ohmic behaviour, with a negligible metal-semiconductor junction resistance. The sensor responseS was defined as S=(Rgas-Rair)/Rair·100, where Rgas and Rair are the resistance of the device in the presence of analyte gas (reducing) or without it, respectively. Response and recovery times are defined as the time needed to reach 90% of the response value at its maximum and to get down to 10% of it, respectively.


## 2.1. Synthesis of Nickel Oxide Nanowires

The NiO nanowires have been grown via a two-step deposition consisting in a hydrothermal method followed by an annealing at 500°C. All the chemicals used in our experiments were of analytical reagent grade and were directly used without further purification. In a typical procedure, 0.474 g of NiCl2 · 6H2O (Sigma-Aldrich, Germany) was dissolved into a mixture of 32 mL ethylene glycol (EG, Sigma-Aldrich) and 18 mL deionized water in a beaker under continuous magnetic stirring at room temperature. Then 0.1206 g of Na2C2O4 was added into the beaker. Half an hour of continuous magnetic stirring was carried out to ensure that Ni2+ ions were dispersed homogeneously in the solution. The clear solution was transferred into a Teflon-lined stainless steel autoclave of 100 mL capacity. The autoclave was sealed and heated at 200°C for 24 h. After the heating treatment, the autoclave was let cooling to room temperature naturally. The product was collected by centrifugation, washed three times with deionized water and absolute ethanol, respectively, and then dried naturally in air. As a result, a blue–green product was obtained.The polycrystalline NiO nanowires were obtained by the calcination of this blue-green precursor, consisting in nickel oxalate hydrate (NiC2O4 · 2H2O) short nanowires, at 500°C.The as-prepared material and the calcinated nanowires were characterized and analyzed by using X-ray diffraction (XRD), scanning electron microscopy (SEM). The XRD analysis was performed using a Bruker D5005 X-ray diffractometer withCuKα1 radiation (λ = 1.5406 Å) at 40 kV and 40 mA. SEM images were obtained using a JEOL7600 scanning electron microscope at an accelerating voltage of 20 kV. Transmission electron microscopy (TEM) and electron diffraction images of the calcinated material were obtained using a JEOL JEM-2100 transmission electron microscope at an accelerating voltage of 200 kV.


## 2.2. Sensing Devices Fabrication

The fabrication of sensing devices consists of a 2-step procedure. First, 1 mg of as-prepared nickel oxide nanowires was dispersed in ethanol solution under ultrasonic vibration for 3 min. The solution was then dropped onto interdigitated comb Pt/Ti electrodes on thermally oxidized silicon substrate. The interdigitated Pt/Ti contacts were previously deposited onto the SiO2/Si substrates by sputtering and conventional optical lithography technique. The whole device is 2 mm × 6 mm, while the two electrodes consisted in 18 pairs of fingers, each 800 μm long and 20 μm wide. The gap between two contiguous fingers is 50 μm. After the deposition of nickel oxide nanowires, the sensor was heated to 500°C at a rate of 1.0°C min−1 in a furnace and then maintained for 2 h in order to increase stability and adhesion between active material and metal electrodes.


## 2.3. Gas Sensing Measurements

The NiO nanowires sensing properties were measured in dynamic conditions, in which the dilution (dry air) and the tested gas were flowing continuously through the sensing chamber at a total flow rate of 500 sccm. The apparatus was home-built and included a test chamber, a sensor holder which can be heated up to 500°C, and mass flow controllers (connected to high purity calibrated bottles).The sensors resistance was measured using a Keithley 2400 multimeter connected to a data acquisition system (LabView, National Instruments). The samples, biased with a voltage of 5 V and operated in air, showed a good ohmic behaviour, with a negligible metal-semiconductor junction resistance. The sensor responseS was defined as S=(Rgas-Rair)/Rair·100, where Rgas and Rair are the resistance of the device in the presence of analyte gas (reducing) or without it, respectively. Response and recovery times are defined as the time needed to reach 90% of the response value at its maximum and to get down to 10% of it, respectively.


## 3. Results and Discussion

### 3.1. Nanowires Characterization

The hydrothermal growth produces thin nanowires with a diameter of about 60 nm. Figure1(a) shows a SEM image of the grown material: the nanostructures are thin and straight with a constant diameter and smooth surfaces. Their aspect ratio (ratio between length and diameter) depends on the process temperature, increasing while the temperature augments. Once the material (nickel oxalate hydrate nanowires) is calcinated at 500°C for 2 hours, the nanowires morphology greatly changes, as shown in Figure 1(b).Figure 1
SEM images of the nanowires (a) before and (b) after the calcination at 500°C.
(a)
(b)It is clear that, after the higher temperature annealing, the nanowires material conglomerates in a series of nanoparticles which still resemble the former nanowires. The nanoparticles are roundish with a diameter in the range of 20–50 nm. A confirmation about the composition of the nanowires before and after the calcination is given by the X-ray diffraction spectra shown in Figure2. In Figure 2(a), relative to the nanowires before calcination, all the numerous diffraction peaks can be assigned to reflections of monoclinic NiC2O4 · 2H2O (JCPDS 25-0581). Figure 2(b), relative to nanowires after the calcination process, shows instead a well crystallized cubic NiO phase (JCPDS 47-1049). The three intense diffraction peaks at 37.3, 43.4, and 62.9° can be indexed to its cubic unit cell, with a lattice parameter of 4.1667 Å. The absence of peaks for any impurity phase in both spectra of Figure 2 confirms that the nanostructures are pure crystals and that the NiC2O4 · 2H2O precursor was completely converted to NiO during calcination.Figure 2
XRD spectra of nanowires (a) before and (b) after the calcination at 500°C.
(a)
(b)The crystal structure of the NiO nanowires was further characterized by TEM and high-resolution TEM analysis. Figure3(a) shows a TEM image of a bundle of NiO nanowires with diameters ranging from 40 to 70 nm; the whole bundle has a diameter of 600 nm. The high magnification TEM image reported in Figure 3(b) reveals that the nanowires are assembled from NiO nanoparticles with the diameters of 20–80 nm, with interspaces between the nanoparticles.Figure 3
(a) TEM, (b) HRTEM, and (c) SAED images of the nanowires once calcinated. The inset in (b) shows a magnification of the lattice fringes of a nanograin.
(a)
(b)
(c)The spacing between lattice fringes in Figure3(b) measures about 0.20 nm, which corresponds to the interplanar distance of (200) lattice planes of cubic NiO. The selected area electron diffraction (SAED) pattern corresponding to the nanogranular NiO nanowires is reported in Figure 3(c), displaying three diffused rings. These rings are assigned to (111), (200), and (220) diffraction lines of cubic NiO phase, respectively. These investigations reveal that the NiO nanowires are made of polycrystalline NiO with cubic structure.


### 3.2. Gas Sensing Properties

A voltage ranging from −5 V to +5 V was applied to the sensors to check the electrical contact between the active material and the metal electrodes. A very good ohmic behaviour was observed, which is important for the sensing properties since the sensor response of a conductometric device can be maximized when the metal-semiconductor connection has a negligible junction resistance. The resistance of the sensors ranged from 27 kΩ to 3 MΩ in air while the temperature increases from 200 to 400°C. The sensing performance of the NiO devices was studied at a voltage of 5 V between the electrodes while flowing different gas concentrations into the apparatus.Figure4 shows the dynamic resistance of a sensor to different hydrogen concentrations (50, 100, 250, 500, and 1000 ppm) at different working temperatures (200, 250, 300, 350, and 400°C). All the plots show that the resistance of the NiO nanowires is stable in air and increases when hydrogen gas is injected into the system. When the H2 flow is interrupted and replaced with air, the sensor resistance decreases to its previous value. This behavior well agrees with that of p-type semiconductor sensors. It is indeed well known that NiO is usually a p-type semiconductor when grown in “normal” conditions. When the NiO nanowires are exposed to air, oxygen molecules will be absorbed on their surface in the form of O− and O2−. This high coverage with adsorbed oxygen particles drains electrons from the nanostructure, increasing the number of electrical holes and thus enlarging its conductivity in these base conditions. Once hydrogen is flown on the devices, its molecules interact with the adsorbed oxygen releasing the electrons used in the chemical bonds back to the nanowires bulk. This results in a decrease of holes and a rise in the sensor resistance.Figure 4
Dynamic resistance of a sensor to the injection and evacuation of different hydrogen concentrations at different sensors working temperatures. Please notice that thex-axis presents a different time scale for each plot.As can be seen in Figure4, the response magnitude of the sensors improves with increasing hydrogen concentration at all working temperatures. At all temperature values, the sensor response is sharp and clear, and the recovery is very good with negligible drifts.The response values calculated from Figure4 are reported in Figure 5(a) as a function of H2 concentration. At all temperatures, the sensor response improves with the increasing gas concentration, with a slope (sensitivity) that slowly decreases at high concentrations, indicating the beginning of saturation.Figure 5
Sensor percentage response as a function of (a) hydrogen concentration and (b) working temperature.
(a)
(b)All the curves show a similar trend, with 200 and 250°C plots showing the highest response values. A plot of the response values towards the working temperature is indeed reported in Figure5(b), showing that the best response is always obtained at 200°C (50 ppm H2) or 250°C (all other hydrogen concentrations). This is a good property of NiO material compared to other metal oxides, because their sensing properties are usually best at higher temperatures [32, 33]. The lowest sensor response of NiO nanowires based sensors goes from 30.4% to 81.6% at 400°C. The best values go from 56.8% (200°C) to 106.9% (at 250°C). These values are good when compared with literature, as will be shown in Table 1.Table 1
Percentage response, response time, and recovery time values of sensors presented in this paper, compared with recent literature.
Note
WorkT.[°C]
Concentration[ppm]
Percentage response[%]
Response time[s]
Recovery time[s]
Reference (year)
n-type
Thin film
125
30000
14
600
540
[25] (2008)
76
900
600
p-type
Nanoparticle
150
1000
10.8
[26] (2012)
Thin film
300
3000
29.6
404
[27] (2013)
6000
45
Nanoparticle
150
3000
42.5
328
450
[28] (2013)
175
68
328
1017
200
62.7
200
774
225
49.4
243
243
175
1000
30
Thin film
160
1000
3.65
[29] (2015)
180
1000
9.1
2000
9.5
1980
144
Nanoparticle
175
1000
22.25
1164
810
[30] (2012)
Nanoparticle
175
1000
32.4
134
406
[31] (2012)
Nanowire
200
1000
103
659
900
Present work
250
1000
107
266
111
300
1000
91
88
39The speed of the response and the recovery of the sensors at different gas concentrations and working temperatures, calculated from Figure4, are presented in Figure 6.Figure 6
(a) Response time and (b) recovery time values as a function of working temperature for different hydrogen concentrations.
(a)
(b)Figure6(a) shows response times, while Figure 6(b) shows recovery times. It is clear that both response and recovery times decrease while increasing the working temperature. There is no evident dependency on the hydrogen concentration. The response time goes from hundreds of seconds at 200°C to few tens of seconds at 300–400°C. Similarly, the plot in Figure 6(b) shows an even steeper decrease: the recovery times go from some hundreds of seconds at 200°C down to few tens of seconds much more quickly. As can be seen in Table 1, the speed of the sensors presented in this work is good when compared with the present literature.Selectivity of the NiO polycrystalline nanowires has been studied towards ethanol, ammonia (NH3), and liquefied petroleum gas (LPG). All these gases behaved as reducing gases, increasing the devices resistance upon their injection. Figure 7 reports the response value of the NiO nanogranular sensors to 100 ppm of different gases while working at 200°C. It is apparent that hydrogen gives rise to a very high response while compared to ethanol, NH3, and LPG.Figure 7
Percentage response of a sensor to 100 ppm of ethanol, ammonia, hydrogen, and liquefied petroleum gas at a working temperature of 200°C.At a low temperature of 200°C, the NiO sensor gives a response of around 65% to H2, while the response to ethanol and NH3 is lower than 20% and that to LPG is lower than 10%. This proves that the NiO polycrystalline nanowires can be used as selective hydrogen sensors.


## 3.1. Nanowires Characterization

The hydrothermal growth produces thin nanowires with a diameter of about 60 nm. Figure1(a) shows a SEM image of the grown material: the nanostructures are thin and straight with a constant diameter and smooth surfaces. Their aspect ratio (ratio between length and diameter) depends on the process temperature, increasing while the temperature augments. Once the material (nickel oxalate hydrate nanowires) is calcinated at 500°C for 2 hours, the nanowires morphology greatly changes, as shown in Figure 1(b).Figure 1
SEM images of the nanowires (a) before and (b) after the calcination at 500°C.
(a)
(b)It is clear that, after the higher temperature annealing, the nanowires material conglomerates in a series of nanoparticles which still resemble the former nanowires. The nanoparticles are roundish with a diameter in the range of 20–50 nm. A confirmation about the composition of the nanowires before and after the calcination is given by the X-ray diffraction spectra shown in Figure2. In Figure 2(a), relative to the nanowires before calcination, all the numerous diffraction peaks can be assigned to reflections of monoclinic NiC2O4 · 2H2O (JCPDS 25-0581). Figure 2(b), relative to nanowires after the calcination process, shows instead a well crystallized cubic NiO phase (JCPDS 47-1049). The three intense diffraction peaks at 37.3, 43.4, and 62.9° can be indexed to its cubic unit cell, with a lattice parameter of 4.1667 Å. The absence of peaks for any impurity phase in both spectra of Figure 2 confirms that the nanostructures are pure crystals and that the NiC2O4 · 2H2O precursor was completely converted to NiO during calcination.Figure 2
XRD spectra of nanowires (a) before and (b) after the calcination at 500°C.
(a)
(b)The crystal structure of the NiO nanowires was further characterized by TEM and high-resolution TEM analysis. Figure3(a) shows a TEM image of a bundle of NiO nanowires with diameters ranging from 40 to 70 nm; the whole bundle has a diameter of 600 nm. The high magnification TEM image reported in Figure 3(b) reveals that the nanowires are assembled from NiO nanoparticles with the diameters of 20–80 nm, with interspaces between the nanoparticles.Figure 3
(a) TEM, (b) HRTEM, and (c) SAED images of the nanowires once calcinated. The inset in (b) shows a magnification of the lattice fringes of a nanograin.
(a)
(b)
(c)The spacing between lattice fringes in Figure3(b) measures about 0.20 nm, which corresponds to the interplanar distance of (200) lattice planes of cubic NiO. The selected area electron diffraction (SAED) pattern corresponding to the nanogranular NiO nanowires is reported in Figure 3(c), displaying three diffused rings. These rings are assigned to (111), (200), and (220) diffraction lines of cubic NiO phase, respectively. These investigations reveal that the NiO nanowires are made of polycrystalline NiO with cubic structure.


## 3.2. Gas Sensing Properties

A voltage ranging from −5 V to +5 V was applied to the sensors to check the electrical contact between the active material and the metal electrodes. A very good ohmic behaviour was observed, which is important for the sensing properties since the sensor response of a conductometric device can be maximized when the metal-semiconductor connection has a negligible junction resistance. The resistance of the sensors ranged from 27 kΩ to 3 MΩ in air while the temperature increases from 200 to 400°C. The sensing performance of the NiO devices was studied at a voltage of 5 V between the electrodes while flowing different gas concentrations into the apparatus.Figure4 shows the dynamic resistance of a sensor to different hydrogen concentrations (50, 100, 250, 500, and 1000 ppm) at different working temperatures (200, 250, 300, 350, and 400°C). All the plots show that the resistance of the NiO nanowires is stable in air and increases when hydrogen gas is injected into the system. When the H2 flow is interrupted and replaced with air, the sensor resistance decreases to its previous value. This behavior well agrees with that of p-type semiconductor sensors. It is indeed well known that NiO is usually a p-type semiconductor when grown in “normal” conditions. When the NiO nanowires are exposed to air, oxygen molecules will be absorbed on their surface in the form of O− and O2−. This high coverage with adsorbed oxygen particles drains electrons from the nanostructure, increasing the number of electrical holes and thus enlarging its conductivity in these base conditions. Once hydrogen is flown on the devices, its molecules interact with the adsorbed oxygen releasing the electrons used in the chemical bonds back to the nanowires bulk. This results in a decrease of holes and a rise in the sensor resistance.Figure 4
Dynamic resistance of a sensor to the injection and evacuation of different hydrogen concentrations at different sensors working temperatures. Please notice that thex-axis presents a different time scale for each plot.As can be seen in Figure4, the response magnitude of the sensors improves with increasing hydrogen concentration at all working temperatures. At all temperature values, the sensor response is sharp and clear, and the recovery is very good with negligible drifts.The response values calculated from Figure4 are reported in Figure 5(a) as a function of H2 concentration. At all temperatures, the sensor response improves with the increasing gas concentration, with a slope (sensitivity) that slowly decreases at high concentrations, indicating the beginning of saturation.Figure 5
Sensor percentage response as a function of (a) hydrogen concentration and (b) working temperature.
(a)
(b)All the curves show a similar trend, with 200 and 250°C plots showing the highest response values. A plot of the response values towards the working temperature is indeed reported in Figure5(b), showing that the best response is always obtained at 200°C (50 ppm H2) or 250°C (all other hydrogen concentrations). This is a good property of NiO material compared to other metal oxides, because their sensing properties are usually best at higher temperatures [32, 33]. The lowest sensor response of NiO nanowires based sensors goes from 30.4% to 81.6% at 400°C. The best values go from 56.8% (200°C) to 106.9% (at 250°C). These values are good when compared with literature, as will be shown in Table 1.Table 1
Percentage response, response time, and recovery time values of sensors presented in this paper, compared with recent literature.
Note
WorkT.[°C]
Concentration[ppm]
Percentage response[%]
Response time[s]
Recovery time[s]
Reference (year)
n-type
Thin film
125
30000
14
600
540
[25] (2008)
76
900
600
p-type
Nanoparticle
150
1000
10.8
[26] (2012)
Thin film
300
3000
29.6
404
[27] (2013)
6000
45
Nanoparticle
150
3000
42.5
328
450
[28] (2013)
175
68
328
1017
200
62.7
200
774
225
49.4
243
243
175
1000
30
Thin film
160
1000
3.65
[29] (2015)
180
1000
9.1
2000
9.5
1980
144
Nanoparticle
175
1000
22.25
1164
810
[30] (2012)
Nanoparticle
175
1000
32.4
134
406
[31] (2012)
Nanowire
200
1000
103
659
900
Present work
250
1000
107
266
111
300
1000
91
88
39The speed of the response and the recovery of the sensors at different gas concentrations and working temperatures, calculated from Figure4, are presented in Figure 6.Figure 6
(a) Response time and (b) recovery time values as a function of working temperature for different hydrogen concentrations.
(a)
(b)Figure6(a) shows response times, while Figure 6(b) shows recovery times. It is clear that both response and recovery times decrease while increasing the working temperature. There is no evident dependency on the hydrogen concentration. The response time goes from hundreds of seconds at 200°C to few tens of seconds at 300–400°C. Similarly, the plot in Figure 6(b) shows an even steeper decrease: the recovery times go from some hundreds of seconds at 200°C down to few tens of seconds much more quickly. As can be seen in Table 1, the speed of the sensors presented in this work is good when compared with the present literature.Selectivity of the NiO polycrystalline nanowires has been studied towards ethanol, ammonia (NH3), and liquefied petroleum gas (LPG). All these gases behaved as reducing gases, increasing the devices resistance upon their injection. Figure 7 reports the response value of the NiO nanogranular sensors to 100 ppm of different gases while working at 200°C. It is apparent that hydrogen gives rise to a very high response while compared to ethanol, NH3, and LPG.Figure 7
Percentage response of a sensor to 100 ppm of ethanol, ammonia, hydrogen, and liquefied petroleum gas at a working temperature of 200°C.At a low temperature of 200°C, the NiO sensor gives a response of around 65% to H2, while the response to ethanol and NH3 is lower than 20% and that to LPG is lower than 10%. This proves that the NiO polycrystalline nanowires can be used as selective hydrogen sensors.


## 4. Conclusions

We have grown NiO polycrystalline nanowires via a simple and cheap process consisting in hydrothermal growth followed by high temperature calcination. The thin polycrystalline nanowires, composed by NiO nanoparticles, show very good hydrogen sensing properties with response values that exceed 100%, quick response and recovery times (down to tens of seconds at 400°C), and good selectivity to hydrogen against ammonia, ethanol, and liquefied petroleum gas.



---

*Source: 785856-2015-10-11.xml*