# Experimental Research on Compression Properties of Cement Asphalt Mortar due to Drying and Wetting Cycle

Authors: Ping Wang; Hao Xu; Rong Chen; Jingmang Xu; Xiaohui Zeng
Journal: Advances in Materials Science and Engineering
 (2014)

---

## Abstract

Uniaxial compression test of cement asphalt (CA) mortar specimens, due to drying and wetting cycle of 0, 2, 4 and 8 times, is carried out by using the electronic universal test machine, with the strain rate ranging from 1 × 10−5 s−1 to 1 × 10−2 s−1. The effects of strain rate and drying and wetting cycle time on the compressive strength, elasticity modulus, and stress-strain full curve are investigated. Experimental results show that the strain-stress full curve of CA mortar is affected obviously by strain rate and drying and wetting cycle time. The compressive strength and elasticity modulus increase with the strain rate under the same drying and wetting cycle time. The compressive strength and elasticity modulus decrease with the increase of drying and wetting cycle time in the same strain rate. The lower the strain rate is, the greater the compressive strength and elasticity modulus of CA mortar decrease. When the strain rate is 1 × 10−5 s−1 and drying and wetting cycle time is 8, the largest reduction of average compressive strength of CA mortar is 40.48%, and the largest reduction of elasticity modulus of CA mortar is 35.51%, and the influence of drying and wetting cycle on the compressive strength of CA mortar is greater than its influence on the elasticity modulus.


---

## Body

## 1. Introduction

Slab ballastless track is a track structure, which is widely used in high speed railway (HSR). The cement emulsified asphalt mortar (CA mortar) layer as a filling layer between track slab and concrete supporting layer functions in support, load transfer, adjustment, reduction, and isolate vibration [1–5]. The long-term service performance of CA mortar is very important in the regularity and durability of track and the safety and comfort of the vehicle driving [6, 7].As the buffer, damping structure layer of slab ballastless track, CA mortar is mainly under the vertical load and in dynamic loading process [8, 9], so the influence of loading rate on the mechanical properties of CA mortar was researched in paper [10–13]. Wang et al. [10] explored the variation in compressive strength of CA mortar under different loading rates. Kong et al. [11] tested the compressive stress-strain of two CAMs at different displacement rates ranging from 0.3 mm/min to 30 mm/min. And the correlation between peak strength or elastic modulus and loading rates was acquired. Yongliang et al. [12] tested two typical CAMs at varied deformation rates over a range of 0.3 to 30 mm/min at room temperature, and the correlation between the mechanical properties and temperature or loading rates was acquired. Xie et al. [13] studied the single-axis compressive characteristic of CRTS I type slab tracks CA mortar under different strain rates. CA mortar is vulnerable in natural environmental conditions chronically under its service process. The rain and sun cycles will have a negative impact on the mechanical properties of CA mortar inevitably, but the variation law on mechanical properties of CA mortar under the drying and wetting cycle has not been reported in China or abroad. In this paper, the writer studied the deterioration laws of mechanical properties of CA mortar, using specimen of CA mortar made in laboratory on the basis of the drying and wetting cycle experiment, which can provide an experimental basis for the deterioration mechanism of CA mortar.


## 2. Experimental

### 2.1. Raw Materials

Cement emulsified asphalt mortar special dry ingredients are mainly mixed with cement, sand, and other additives. Its basic mixture ratio is cement : sand : expanders = 1 : 2 : 0.1. Pure Portland cement with a strength grade of 42.5, complying with the Chinese National Standard GB175-1999, was used. The 24 h volume expansion rate of this cement emulsified asphalt mortar special dry ingredients is 2.1%, whose 7 d line expansion rate is 0.1% and the 1-day compressive strength is 6.89 MPa.The asphalt emulsion is the special emulsified asphalt of CA mortar on CRTS I type slab ballastless track, whose solid mass fraction is 62.1%. And the viscosity, penetration, and ductility of asphalt emulsion can meet the requirements of the temporary technology criterion of cement and emulsified asphalt mortar in CRTS (China railway track system) I type slab track of passenger dedicated railway, whose main properties are listed in Table1.Table 1
Properties of emulsified asphalts.
Number
Item
Unit
Requesting
Value
1
Engler viscosity (25°C)
5~15
8.0
2
Ratioof screen residue (1.18 mm)
%
<0.1
0
3
Storage stability (1 d, 25°C)
%
<1.0
0.3
4
Storage stability (5 d, 25°C)
%
<5.0
3.2
5
Residue of mixing with cement
%
<1.0
0.3
6
Evaporated residue
Needle penetration (25°C, 100 g)
0.1 mm
60~120
78.5
7
Solubility(trichloroethylene)
%
>97
98.0
8
Ductility (5°C)
cm
⩾20
26.5
9
Ductility (15°C)
cm
⩾50
61.2The J-funnel flow time of fresh CA mortar is 24 s, and the resolution is 0.2%. The mix proportion of CA mortar is m(dry ingredients) : m(asphalt) : m(water) = 1100 : 515 : 50. Mixing water is the tap water.


### 2.2. Sample Preparation

According to the given mixture of CA mortar, put the emulsified asphalt and water into the pot and stir slowly, and add the dry ingredients into the spot slowly in the slowly stir condition. After the dry ingredients were added, stir rapidly for 3 min and then stir for 1 min. The fluidity, apparent density, gas content, and other properties of fresh CA mortar were measured according to the method in [10]. The fluidity of CA mortar was 24 s. The apparent density was 1610 kg·m−3 and the gas content was 8.2%. Then fresh CA mortar was placed into cylindrical plastics moulds with size Ф 50 mm × 50 mm, forming 90 specimens. After being cured in the constant temperature (23±2)°C and constant humidity (65±5)% for 24 hours, the samples were removed from the moulds, transferred into the standard room, and cured for 120 days, and then we did the drying and wetting cycle experiment and compression test.


### 2.3. Testing Method

In order to simulate the condition of CA mortar layer under drying and wetting cycle, CA mortar specimens were immersed in water for 7 days and then put them in outdoor for natural withering 7 days. The environment temperature was kept at 20°C, and the drying and wetting cycle times were 0, 2, 4, and 8. And then, at the regulation age, the mechanical property of CA mortar specimens was tested. The CA mortar specimens and the specimens which were immersed in water were given in Figure1.CA mortar specimens.
(a)
Standard specimen of CA mortar
(b)
CA mortar specimens immersed in waterThe mechanical property test of CA mortar, uniaxial compressive test of CA mortar specimens in different immersion time, was carried out by using the universal electronic test machine (Figure2) according to the method in paper [6], keeping the environment temperature at 20°C when testing. Considering the loading ability of the experimental system, loading rates of 0.03 mm/min, 0.3 mm/min, 3 mm/min, and 30 mm/min were set for testing the CA mortar specimens. Strain rates were 1 × 10−5 s−1, 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1, which were obtained according to the size of CA mortar specimens, taking 1 × 10−5 s−1 as a quasistatic strain rate. Two loading surfaces were coated with French chalk to reduce the surface restraint effect and three samples were used for each test as duplication. If the test results are discrete, the number of specimens should be increased in order to ensure the validity of test data. Specimens should be preloaded three times with loading rate of 0.5 mm/min and strength of 0.05 MPa before the formal loading in order to prevent the error because of the surface unevenness of CA mortar samples.Figure 2
The schematic of universal testing machine in the loading direction.


## 2.1. Raw Materials

Cement emulsified asphalt mortar special dry ingredients are mainly mixed with cement, sand, and other additives. Its basic mixture ratio is cement : sand : expanders = 1 : 2 : 0.1. Pure Portland cement with a strength grade of 42.5, complying with the Chinese National Standard GB175-1999, was used. The 24 h volume expansion rate of this cement emulsified asphalt mortar special dry ingredients is 2.1%, whose 7 d line expansion rate is 0.1% and the 1-day compressive strength is 6.89 MPa.The asphalt emulsion is the special emulsified asphalt of CA mortar on CRTS I type slab ballastless track, whose solid mass fraction is 62.1%. And the viscosity, penetration, and ductility of asphalt emulsion can meet the requirements of the temporary technology criterion of cement and emulsified asphalt mortar in CRTS (China railway track system) I type slab track of passenger dedicated railway, whose main properties are listed in Table1.Table 1
Properties of emulsified asphalts.
Number
Item
Unit
Requesting
Value
1
Engler viscosity (25°C)
5~15
8.0
2
Ratioof screen residue (1.18 mm)
%
<0.1
0
3
Storage stability (1 d, 25°C)
%
<1.0
0.3
4
Storage stability (5 d, 25°C)
%
<5.0
3.2
5
Residue of mixing with cement
%
<1.0
0.3
6
Evaporated residue
Needle penetration (25°C, 100 g)
0.1 mm
60~120
78.5
7
Solubility(trichloroethylene)
%
>97
98.0
8
Ductility (5°C)
cm
⩾20
26.5
9
Ductility (15°C)
cm
⩾50
61.2The J-funnel flow time of fresh CA mortar is 24 s, and the resolution is 0.2%. The mix proportion of CA mortar is m(dry ingredients) : m(asphalt) : m(water) = 1100 : 515 : 50. Mixing water is the tap water.


## 2.2. Sample Preparation

According to the given mixture of CA mortar, put the emulsified asphalt and water into the pot and stir slowly, and add the dry ingredients into the spot slowly in the slowly stir condition. After the dry ingredients were added, stir rapidly for 3 min and then stir for 1 min. The fluidity, apparent density, gas content, and other properties of fresh CA mortar were measured according to the method in [10]. The fluidity of CA mortar was 24 s. The apparent density was 1610 kg·m−3 and the gas content was 8.2%. Then fresh CA mortar was placed into cylindrical plastics moulds with size Ф 50 mm × 50 mm, forming 90 specimens. After being cured in the constant temperature (23±2)°C and constant humidity (65±5)% for 24 hours, the samples were removed from the moulds, transferred into the standard room, and cured for 120 days, and then we did the drying and wetting cycle experiment and compression test.


## 2.3. Testing Method

In order to simulate the condition of CA mortar layer under drying and wetting cycle, CA mortar specimens were immersed in water for 7 days and then put them in outdoor for natural withering 7 days. The environment temperature was kept at 20°C, and the drying and wetting cycle times were 0, 2, 4, and 8. And then, at the regulation age, the mechanical property of CA mortar specimens was tested. The CA mortar specimens and the specimens which were immersed in water were given in Figure1.CA mortar specimens.
(a)
Standard specimen of CA mortar
(b)
CA mortar specimens immersed in waterThe mechanical property test of CA mortar, uniaxial compressive test of CA mortar specimens in different immersion time, was carried out by using the universal electronic test machine (Figure2) according to the method in paper [6], keeping the environment temperature at 20°C when testing. Considering the loading ability of the experimental system, loading rates of 0.03 mm/min, 0.3 mm/min, 3 mm/min, and 30 mm/min were set for testing the CA mortar specimens. Strain rates were 1 × 10−5 s−1, 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1, which were obtained according to the size of CA mortar specimens, taking 1 × 10−5 s−1 as a quasistatic strain rate. Two loading surfaces were coated with French chalk to reduce the surface restraint effect and three samples were used for each test as duplication. If the test results are discrete, the number of specimens should be increased in order to ensure the validity of test data. Specimens should be preloaded three times with loading rate of 0.5 mm/min and strength of 0.05 MPa before the formal loading in order to prevent the error because of the surface unevenness of CA mortar samples.Figure 2
The schematic of universal testing machine in the loading direction.


## 3. Results and Discussion

### 3.1. Stress-Strain Curve of CA Mortar

The mechanical property of CA mortar was fully reflected by the stress-strain full curve of CA mortar. The stress-strain full curves of CA mortar of CRTS I slab ballastless track are shown in Figure3. Figure 3(a) shows the stress-strain full curves of CA mortar under different strain rates, without drying and wetting cycle. As shown in Figure 3(a), the stress-strain curves of CA mortar change obviously under different strain rates, and the ultimate compressive strength of CA mortar increases with the strain rate. Figure 3(b) shows the stress-strain full curves of CA mortar under different drying and wetting cycle times when the strain rate is 1 × 10−4 s−1. As shown in Figure 3(b), the ultimate compressive strength of CA mortar decreases with the increase of drying and wetting cycle time. The strength of CA mortar decreases slowly when the strength of CA mortar reaches the peak strength. The existence of asphalt improves the fracture toughness of CA mortar, and the CA mortar still has enough bearing capacity when the strain reaches 10%, which indicates that the CA mortar has good toughness and ductility.Stress-strain full curves of CA mortar.
(a)
Different strain rates
(b)
Strain rate is 1 × 10−4 s−1


### 3.2. Compressive Strength of CA Mortar

The uniaxial compressive strength of CA mortar under different drying and wetting cycle times and strain rates are shown in Table2.Table 2
Compressive strengths of CA mortar under different drying and wetting cycle times.
Strain rates/s−1
Test
Compressive strength/MPa
0 times
2 times
4 times
8 times
1 × 10−5
1
3.301
2.872
2.051
1.915
2
3.277
2.882
2.058
2.017
3
3.367
2.981
2.129
1.987
Average
3.315
2.912
2.079
1.973
1 × 10−4
1
3.858
3.594
2.871
2.456
2
3.781
3.448
2.764
2.537
3
3.954
3.501
2.765
2.412
Average
3.864
3.514
2.800
2.468
1 × 10−3
1
5.283
4.285
3.684
3.299
2
5.232
4.221
3.739
3.403
3
5.192
4.084
3.619
3.255
Average
5.235
4.196
3.680
3.319
1 × 10−2
1
7.121
6.349
5.040
4.622
2
7.184
6.261
4.903
4.508
3
7.102
6.183
4.917
4.587
Average
7.135
6.264
4.953
4.572As shown in Table2, the ultimate compressive strength increases with the strain rate under the same drying and wetting cycle time. After drying and wetting cycle for 0, 2,4, and 8 times, the average strength of CA mortar in the strain rates of 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1 increases by 16.56%, 20.67%, 34.68%, and 25.09%, 57.92%, 44.09%, 77.01%, and 68.22%, and 115.23%, 115.11%, 138.24%, and 131.72% comparing with that in the strain rate of 1 × 10−5 s−1. The strength of CA mortar comes from the hydration of cement and demulsification of asphalt emulsion, and the skeleton structure of CA mortar is formed by the asphalt being coated with hydration product of cement and sand [14]. The strength of CA mortar is provided by the connection between cement hydration products and asphalt or connection between sand and asphalt. Damage of CA mortar is mainly caused by the internal crack of its skeleton. With the increase of strain rate, the microcrack of CA mortar could not extend timely, and the lateral inertia confinement effect of asphalt’s network structure will prevent the development of microcrack, which results in the compressive strength improvement of CA mortar.Influences of strain rate on the compressive strength of CA mortar under different drying and wetting cycle times are shown in Figure4.Figure 4
Compressive strength of CA mortar at different strain rates and drying and wetting cycle times.As shown in Table2 and Figure 4, the ultimate compressive strength of CA mortar decreases with the increase of drying and wetting cycle time under the same strain rate. When the strain rates are 1 × 10−5 s−1, 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1, the drying and wetting cycle times are 2, 4, and 8, and the average compressive strength of CA mortar decreases by 12.15%, 9.06%, 19.84%, and 12.21%, 37.28%, 27.53%, 29.70%, and 30.58%, and 40.48%, 36.12%, 36.59%, and 35.92% compared with that without drying and wetting cycle. The stress generated by dry shrinkage and wet expansion deformation of CA mortar will damage the CA mortar with the developing of drying and wetting. The stress concentration zoon, which is formatted in the weak interfaces between network of asphalt and cement hydration products and between network structure and sand, results in micropore and cracks. The internal damage of CA mortar accumulates continually, and the strength of CA mortar reduces gradually. When the microcracks extend to a regular degree, the stress generated by dry shrinkage and wet expansion will decrease continuously. In the macroscopic level, the decrease of compressive strength of CA mortar trends to stability.


### 3.3. Relationship between Elasticity Modulus and Cycle Time

The elasticity modulus of materials reflects the recovery capacity of deformation; the higher the elasticity modulus, the stronger the recovery capacity of deformation. Use the secant modulus of compressive strength of 0~1/3 as the elastic modulus of CA mortar [13], which is the following formula:
(1)Ed=σ1/3-σ0ε1/3-ε0,
in which Ed is the elasticity modulus of CA mortar and σ1/3 is the 1/3 of ultimate compressive strength. σ0 is the initial stress. In this experiment, σ0 is 0. ε1/3 is the strain corresponding to σ1/3. ε0 is the initial strain value, which is 0. Through the analysis of stress-strain curve, the elasticity moduli of CA mortar at different drying and wetting cycle times are shown in Table 3.Table 3
Elasticity modulus of CA mortar under different drying and wetting cycle times.
Strain rates/s−1
Test
Elastic modulusE/MPa
0 times
2 times
4 times
8 times
1 × 10−5
1
88.400
72.509
65.867
56.372
2
84.466
76.698
60.604
55.212
3
79.382
84.585
54.641
51.005
Average
84.082
77.931
60.370
54.196
1 × 10−4
1
94.824
87.467
75.179
62.379
2
88.195
85.362
61.631
59.477
3
95.666
77.999
71.060
67.446
Average
92.895
83.609
69.290
63.101
1 × 10−3
1
124.793
109.343
90.576
80.792
2
110.982
100.494
89.461
77.084
3
115.053
104.158
95.169
82.562
Average
116.942
104.664
91.736
80.146
1 × 10−2
1
150.201
142.525
115.953
107.252
2
162.436
152.803
123.504
107.602
3
161.260
146.402
127.761
113.613
Average
157.966
147.243
122.406
109.489Table3 demonstrates that the elasticity modulus of CA mortar increases with the strain rate under the same drying and wetting cycle time. After drying and wetting cycle for 0, 2, 4, and 8 times, the elasticity modulus of CA mortar in the strain rates of 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1 increases by 10.48%, 7.28%, 14.77%, and 16.43%, 39.08%, 34.30%, 51.95%, and 47.88%, and 87.87%, 88.94%, 102.76%, and 102.02% compared with that in the strain rate of 1 × 10−5 s−1. The elasticity modulus of CA mortar reflects the recovery capacity of deformation, so the sensibility of strain rate on the elasticity modulus of CA mortar can improve the stability of train driving.Influences of strain rate on the average elastic modulus of CA mortar under different drying and wetting cycle times are shown in Figure5.Figure 5
Elastic modulus of CA mortar.As shown in Table3 and Figure 5, elasticity modulus of CA mortar decreases with the increase of drying and wetting cycle time under the same strain rate. When the strain rates are 1 × 10−5 s−1, 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1, the drying and wetting cycle times are 2, 4, and 8; the average elastic modulus of CA mortar decreases by 7.31%, 9.99%, 10.49%, and 6.79%, 28.20%, 25.41%, 21.55%, and 22.51%, and 35.51%, 32.07%, 31.46%, and 30.69% comparing with that without drying and wetting cycle. With the continuation of drying and wetting cycle, the internal structure of CA mortar will be damaged, the recovery capacity of deformation will be weakened, and the elasticity modulus of CA mortar decreases gradually. The reason is similar to the change of CA mortar’s compressive strength. The attenuation rate of elasticity modulus of CA mortar decreases slowly.


## 3.1. Stress-Strain Curve of CA Mortar

The mechanical property of CA mortar was fully reflected by the stress-strain full curve of CA mortar. The stress-strain full curves of CA mortar of CRTS I slab ballastless track are shown in Figure3. Figure 3(a) shows the stress-strain full curves of CA mortar under different strain rates, without drying and wetting cycle. As shown in Figure 3(a), the stress-strain curves of CA mortar change obviously under different strain rates, and the ultimate compressive strength of CA mortar increases with the strain rate. Figure 3(b) shows the stress-strain full curves of CA mortar under different drying and wetting cycle times when the strain rate is 1 × 10−4 s−1. As shown in Figure 3(b), the ultimate compressive strength of CA mortar decreases with the increase of drying and wetting cycle time. The strength of CA mortar decreases slowly when the strength of CA mortar reaches the peak strength. The existence of asphalt improves the fracture toughness of CA mortar, and the CA mortar still has enough bearing capacity when the strain reaches 10%, which indicates that the CA mortar has good toughness and ductility.Stress-strain full curves of CA mortar.
(a)
Different strain rates
(b)
Strain rate is 1 × 10−4 s−1


## 3.2. Compressive Strength of CA Mortar

The uniaxial compressive strength of CA mortar under different drying and wetting cycle times and strain rates are shown in Table2.Table 2
Compressive strengths of CA mortar under different drying and wetting cycle times.
Strain rates/s−1
Test
Compressive strength/MPa
0 times
2 times
4 times
8 times
1 × 10−5
1
3.301
2.872
2.051
1.915
2
3.277
2.882
2.058
2.017
3
3.367
2.981
2.129
1.987
Average
3.315
2.912
2.079
1.973
1 × 10−4
1
3.858
3.594
2.871
2.456
2
3.781
3.448
2.764
2.537
3
3.954
3.501
2.765
2.412
Average
3.864
3.514
2.800
2.468
1 × 10−3
1
5.283
4.285
3.684
3.299
2
5.232
4.221
3.739
3.403
3
5.192
4.084
3.619
3.255
Average
5.235
4.196
3.680
3.319
1 × 10−2
1
7.121
6.349
5.040
4.622
2
7.184
6.261
4.903
4.508
3
7.102
6.183
4.917
4.587
Average
7.135
6.264
4.953
4.572As shown in Table2, the ultimate compressive strength increases with the strain rate under the same drying and wetting cycle time. After drying and wetting cycle for 0, 2,4, and 8 times, the average strength of CA mortar in the strain rates of 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1 increases by 16.56%, 20.67%, 34.68%, and 25.09%, 57.92%, 44.09%, 77.01%, and 68.22%, and 115.23%, 115.11%, 138.24%, and 131.72% comparing with that in the strain rate of 1 × 10−5 s−1. The strength of CA mortar comes from the hydration of cement and demulsification of asphalt emulsion, and the skeleton structure of CA mortar is formed by the asphalt being coated with hydration product of cement and sand [14]. The strength of CA mortar is provided by the connection between cement hydration products and asphalt or connection between sand and asphalt. Damage of CA mortar is mainly caused by the internal crack of its skeleton. With the increase of strain rate, the microcrack of CA mortar could not extend timely, and the lateral inertia confinement effect of asphalt’s network structure will prevent the development of microcrack, which results in the compressive strength improvement of CA mortar.Influences of strain rate on the compressive strength of CA mortar under different drying and wetting cycle times are shown in Figure4.Figure 4
Compressive strength of CA mortar at different strain rates and drying and wetting cycle times.As shown in Table2 and Figure 4, the ultimate compressive strength of CA mortar decreases with the increase of drying and wetting cycle time under the same strain rate. When the strain rates are 1 × 10−5 s−1, 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1, the drying and wetting cycle times are 2, 4, and 8, and the average compressive strength of CA mortar decreases by 12.15%, 9.06%, 19.84%, and 12.21%, 37.28%, 27.53%, 29.70%, and 30.58%, and 40.48%, 36.12%, 36.59%, and 35.92% compared with that without drying and wetting cycle. The stress generated by dry shrinkage and wet expansion deformation of CA mortar will damage the CA mortar with the developing of drying and wetting. The stress concentration zoon, which is formatted in the weak interfaces between network of asphalt and cement hydration products and between network structure and sand, results in micropore and cracks. The internal damage of CA mortar accumulates continually, and the strength of CA mortar reduces gradually. When the microcracks extend to a regular degree, the stress generated by dry shrinkage and wet expansion will decrease continuously. In the macroscopic level, the decrease of compressive strength of CA mortar trends to stability.


## 3.3. Relationship between Elasticity Modulus and Cycle Time

The elasticity modulus of materials reflects the recovery capacity of deformation; the higher the elasticity modulus, the stronger the recovery capacity of deformation. Use the secant modulus of compressive strength of 0~1/3 as the elastic modulus of CA mortar [13], which is the following formula:
(1)Ed=σ1/3-σ0ε1/3-ε0,
in which Ed is the elasticity modulus of CA mortar and σ1/3 is the 1/3 of ultimate compressive strength. σ0 is the initial stress. In this experiment, σ0 is 0. ε1/3 is the strain corresponding to σ1/3. ε0 is the initial strain value, which is 0. Through the analysis of stress-strain curve, the elasticity moduli of CA mortar at different drying and wetting cycle times are shown in Table 3.Table 3
Elasticity modulus of CA mortar under different drying and wetting cycle times.
Strain rates/s−1
Test
Elastic modulusE/MPa
0 times
2 times
4 times
8 times
1 × 10−5
1
88.400
72.509
65.867
56.372
2
84.466
76.698
60.604
55.212
3
79.382
84.585
54.641
51.005
Average
84.082
77.931
60.370
54.196
1 × 10−4
1
94.824
87.467
75.179
62.379
2
88.195
85.362
61.631
59.477
3
95.666
77.999
71.060
67.446
Average
92.895
83.609
69.290
63.101
1 × 10−3
1
124.793
109.343
90.576
80.792
2
110.982
100.494
89.461
77.084
3
115.053
104.158
95.169
82.562
Average
116.942
104.664
91.736
80.146
1 × 10−2
1
150.201
142.525
115.953
107.252
2
162.436
152.803
123.504
107.602
3
161.260
146.402
127.761
113.613
Average
157.966
147.243
122.406
109.489Table3 demonstrates that the elasticity modulus of CA mortar increases with the strain rate under the same drying and wetting cycle time. After drying and wetting cycle for 0, 2, 4, and 8 times, the elasticity modulus of CA mortar in the strain rates of 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1 increases by 10.48%, 7.28%, 14.77%, and 16.43%, 39.08%, 34.30%, 51.95%, and 47.88%, and 87.87%, 88.94%, 102.76%, and 102.02% compared with that in the strain rate of 1 × 10−5 s−1. The elasticity modulus of CA mortar reflects the recovery capacity of deformation, so the sensibility of strain rate on the elasticity modulus of CA mortar can improve the stability of train driving.Influences of strain rate on the average elastic modulus of CA mortar under different drying and wetting cycle times are shown in Figure5.Figure 5
Elastic modulus of CA mortar.As shown in Table3 and Figure 5, elasticity modulus of CA mortar decreases with the increase of drying and wetting cycle time under the same strain rate. When the strain rates are 1 × 10−5 s−1, 1 × 10−4 s−1, 1 × 10−3 s−1, and 1 × 10−2 s−1, the drying and wetting cycle times are 2, 4, and 8; the average elastic modulus of CA mortar decreases by 7.31%, 9.99%, 10.49%, and 6.79%, 28.20%, 25.41%, 21.55%, and 22.51%, and 35.51%, 32.07%, 31.46%, and 30.69% comparing with that without drying and wetting cycle. With the continuation of drying and wetting cycle, the internal structure of CA mortar will be damaged, the recovery capacity of deformation will be weakened, and the elasticity modulus of CA mortar decreases gradually. The reason is similar to the change of CA mortar’s compressive strength. The attenuation rate of elasticity modulus of CA mortar decreases slowly.


## 4. Conclusions

The stress-strain relationship of CA mortar under different strain rates and drying and wetting cycle times has been got through the uniaxial compression experiment, and the change rule of related mechanics index has also been analyzed. The following conclusions can be drawn.(1)
The mechanical property of CA mortar is influenced obviously by strain rates and drying and wetting cycle times.(2)
Because the stress generated by dry shrinkage and wet expansion deformation of CA mortar will damage the CA mortar, the compressive strength and elasticity modulus decrease with the increase of drying and wetting cycle times in the same strain rate. When the strain rate is 1 × 10−5 s−1 and the drying and wetting cycle time is 8, the largest reduction of average compressive strength of CA mortar is 40.48%, and the largest reduction of elasticity modulus of CA mortar is 35.51%.(3)
Under the same drying and wetting cycle time, since microcracks inside the CA mortar can not develop in time, the ultimate compressive strength and elastic modulus will increase with the strain rate. The maximum increase of compressive strength is 138.24%, and the largest increase of elasticity modulus is 102.76%.(4)
The influence of drying and wetting cycle on the compressive strength of CA mortar is greater than its impact on the elasticity modulus.



---