# A Novel Approach to Improve the Barrier Properties of PET/Clay Nanocomposites

Authors: Kazem Majdzadeh-Ardakani; Shahab Zekriardehani; Maria R. Coleman; Saleh A. Jabarin
Journal: International Journal of Polymer Science
 (2017)

---

## Abstract

An investigation of oleic acid-modified clay versus plain clay with regard to the physical and barrier properties of PET/clay nanocomposites was performed. Montmorillonite (MMT) and Cloisite 30B nanoclays were modified by long-chain oleic acid and identified as ol-MMT and ol-30B, respectively. Fourier Transformed Infrared Spectroscopy and X-ray diffraction (XRD) results revealed that the fatty acid was associated with the clay surface and that the gallery spacing of the layered silicates was expanded. In the case of ol-MMT, a disordered structure of layered silicates was achieved. TGA results indicated that ol-MMT showed thermal stability and could survive PET processing temperature. The degradation of ol-30B, however, increased after modification because of the presence of oleic acid. PET/clay nanocomposites were prepared with modified ol-MMT and modified ol-30B by using a twin screw extruder. XRD indicated that there was a significant improvement on the dispersion of nanoclays modified with long-chain oleic acid into the PET matrix, and an exfoliated structure was achieved. DSC data also revealed that crystallization behaviors of nanocomposites prepared with oleic acid-modified clays are similar to that of extruded PET. Significant improvements in the mechanical and barrier properties of stretched PET/clay nanocomposites were also achieved.


---

## Body

## 1. Introduction

Poly(ethylene terephthalate) (PET) is a semicrystalline thermoplastic which is widely used in the manufacture of fibers, films, and beverage containers. Along with its low cost, PET shows chemical and thermal resistance, good optical properties, and good processability [1]. One of the main applications of PET in the packaging industries is its usage in the manufacture of plastic bottles for carbonated soft drinks, water, and juice [2]. There are two common approaches for improving the barrier properties of PET to be used for highly oxygen-sensitive food packaging. These are passive barrier techniques achieved by adding fillers to the polymer matrix to create a tortuous pass for gas molecules [3, 4] and active barrier techniques that include oxygen scavengers in the polymer matrix [5, 6].Polymer/clay nanocomposites have attracted significant interest in recent years, because they provide advantages compared to conventional composites. Introducing small amounts of nanoclays into the polymer matrix is one of the passive barrier methods used to further improve thermal stability, barrier, and mechanical properties of PET [7–11]. These improvements, however, are greatly influenced by the degree of clay dispersion into the polymer matrix. Preparing nanocomposites with an exfoliated structure leads to better barrier and mechanical properties [12, 13]. Pristine montmorillonite (MMT) and commercially modified clays have been widely used in areas of nanocomposite research. The compatibility of pristine clay (MMT) with most engineering polymers is very low. It is essential to use clays modified with organic surfactants in order to make them compatible with the polymer matrix. Most of the recent efforts, therefore, have focused on modification of MMT with organic surfactants [7, 14–17]. Commercial nanoclays modified with quaternary ammonium surfactants have widely been used in the preparation of nanocomposites. These nanoclays, however, degrade at PET processing temperatures (270–300°C). Thermally stable surfactants such as imidazolium [7, 14, 15, 18], quinolinium [19], phosphonium [7, 8, 16], and pyridinium surfactants [17] have been used by some researchers. The results indicate that in most cases a combination of intercalated and exfoliated morphologies has been achieved and the uniform dispersion of nanoclays into the PET matrix has remained inaccessible. This is because of the lack of compatibility of modified clays with PET and difficulty in diffusing the long polymer chains into the gallery spacing of layered silicates. Consequently, there has been no significant improvement in the barrier properties of PET nanocomposites.In an active barrier approach, a component such as an oxygen scavenger is added to PET to react with any oxygen present and protect the packaged food against quality changes. Bio-based unsaturated fatty acids such as oleic acid (with a single double bond) can be used as oxygen scavengers to improve the barrier properties of PET [20, 21].In this work, the main objective has been to develop a new method for preparation of exfoliated PET/clay nanocomposites with superior barrier properties. The approach is to combine both passive barrier and active barrier techniques by modifying pristine clay and commercially modified clay (Cloisite 30B) with long-chain fatty acids and blending these nanoparticles with PET to make nanocomposites with superior barrier properties. This modification not only opens up the gallery spacing of layered silicates and makes them more accessible for PET to diffuse inside the galleries but also provides an oxygen scavenger that can react with oxygen and protect foods and beverages from oxidation. No published reports have been found describing the introduction of fatty acids as oxygen scavengers into nanoclays to improve the dispersion and barrier properties of PET/clay nanocomposites by using both active and passive barrier approaches.


## 2. Experimental

### 2.1. Materials

PET resin (grade HP806) with an intrinsic viscosity (IV) of 0.84 dL/g was obtained from Wellman Company (Bay St. Louis, MS). MMT and Cloisite 30B clays, with respective cation exchange capacities of 92.6 and 90 meq/100 g, were generously donated by Southern Clay Products (Gonzales, TX). Oleic acid (technical grade, 90%) was purchased from Sigma-Aldrich (Allentown, PA). Methanol was obtained from Fisher Scientific (Chicago, IL).


### 2.2. Modification of Nanoclays with Oleic Acid

The organically modified clays (ol-MMT and ol-30B) were synthesized by mixing MMT or Cloisite 30B with oleic acid. To prepare ol-MMT and ol-30B, mixtures of the clays and fatty acids (1 : 2 by mass) were prepared and blended in a Parr Reactor with a fixed rotor speed of 50 rpm and temperature of 60°C. These mixtures were stirred for 2 hours before being removed and washed repeatedly with methanol to remove unbounded fatty acids. Modified samples were vacuum-dried at 90°C for 24 hours and then ground into a fine powder.Water molecules encapsulate sodium in the interlayer of MMT and they can react with the C=O groups of the fatty acid. A bridge can also be formed between water molecules and metal ions present in the layer structure. Another possibility is the interaction between free OH groups at the surface of the clay particles and carboxyl group of fatty acid. The quaternary amines with long alkyl chain present in the interlayer space of Cloisite 30B, expanded the silicate layers, and facilitate the way for intercalation of long-chain fatty acids during mixing. Furthermore, the presence of the long alkyl chains in the interlayer of clay particles reduces the hydrophilic character of these particles and makes it easier for fatty acid alkyl chains to be drawn inside the clay interlayer space due to the strong van der Waals force of attraction. The possibility of interaction between the ammonium head groups of quaternary ammonium surfactants and the carboxylic acid of oleic acid via hydrogen bonding could also be speculated [22].


### 2.3. Preparation of Nanocomposites

PET and modified clays (2% wt.%) were melt blended with a corotating twin screw extruder at 280°C and 200 rpm. Before extrusion, PET samples were dried in a Conair dehumidifying air dryer at 140°C overnight and the modified clays were vacuum-dried at 100°C overnight. Before loading the mixture of PET and clay into the hopper of the extruder, PET and the dry modified clays were mixed in a sealed container for 3 min. Nanocomposite strands extruded from the die were quenched through a water bath and then cut into pellets with a pelletizer and vacuum-dried for further characterization.


### 2.4. Preparation of Nanocomposite Films

An ALLROUNDER 320 s Arburg Injection Molding Machine (55-ton capacity) was used to prepare PET nanocomposite preforms. Before the injection molding process, the samples were dried in a Conair dehumidifying air dryer at 140°C overnight.The 2 wt.% PET nanocomposite preforms obtained by the injection molding process were stretched and blown into bottles using a lab-scale stretch-blow molding machine. In this process, infrared heaters provide an appropriate preform temperature profile. An axial stretch rod was used for stretching the preforms to a desirable length. Then, the final pressure or the full blow pressure was applied, which inflated the bottle to the desired volume (diameter and length of the bottles were 10.5 cm and 30 cm, resp.). This orientation process leads to the strain-induced crystallization and strain hardening of the stretched polymer [23, 24]. The bottles were solidified and cooled when they attained the shape of the mold. The sidewalls of the stretch blow molded bottles were used to investigate the tensile and oxygen barrier properties for nanocomposites and base PET.


## 2.1. Materials

PET resin (grade HP806) with an intrinsic viscosity (IV) of 0.84 dL/g was obtained from Wellman Company (Bay St. Louis, MS). MMT and Cloisite 30B clays, with respective cation exchange capacities of 92.6 and 90 meq/100 g, were generously donated by Southern Clay Products (Gonzales, TX). Oleic acid (technical grade, 90%) was purchased from Sigma-Aldrich (Allentown, PA). Methanol was obtained from Fisher Scientific (Chicago, IL).


## 2.2. Modification of Nanoclays with Oleic Acid

The organically modified clays (ol-MMT and ol-30B) were synthesized by mixing MMT or Cloisite 30B with oleic acid. To prepare ol-MMT and ol-30B, mixtures of the clays and fatty acids (1 : 2 by mass) were prepared and blended in a Parr Reactor with a fixed rotor speed of 50 rpm and temperature of 60°C. These mixtures were stirred for 2 hours before being removed and washed repeatedly with methanol to remove unbounded fatty acids. Modified samples were vacuum-dried at 90°C for 24 hours and then ground into a fine powder.Water molecules encapsulate sodium in the interlayer of MMT and they can react with the C=O groups of the fatty acid. A bridge can also be formed between water molecules and metal ions present in the layer structure. Another possibility is the interaction between free OH groups at the surface of the clay particles and carboxyl group of fatty acid. The quaternary amines with long alkyl chain present in the interlayer space of Cloisite 30B, expanded the silicate layers, and facilitate the way for intercalation of long-chain fatty acids during mixing. Furthermore, the presence of the long alkyl chains in the interlayer of clay particles reduces the hydrophilic character of these particles and makes it easier for fatty acid alkyl chains to be drawn inside the clay interlayer space due to the strong van der Waals force of attraction. The possibility of interaction between the ammonium head groups of quaternary ammonium surfactants and the carboxylic acid of oleic acid via hydrogen bonding could also be speculated [22].


## 2.3. Preparation of Nanocomposites

PET and modified clays (2% wt.%) were melt blended with a corotating twin screw extruder at 280°C and 200 rpm. Before extrusion, PET samples were dried in a Conair dehumidifying air dryer at 140°C overnight and the modified clays were vacuum-dried at 100°C overnight. Before loading the mixture of PET and clay into the hopper of the extruder, PET and the dry modified clays were mixed in a sealed container for 3 min. Nanocomposite strands extruded from the die were quenched through a water bath and then cut into pellets with a pelletizer and vacuum-dried for further characterization.


## 2.4. Preparation of Nanocomposite Films

An ALLROUNDER 320 s Arburg Injection Molding Machine (55-ton capacity) was used to prepare PET nanocomposite preforms. Before the injection molding process, the samples were dried in a Conair dehumidifying air dryer at 140°C overnight.The 2 wt.% PET nanocomposite preforms obtained by the injection molding process were stretched and blown into bottles using a lab-scale stretch-blow molding machine. In this process, infrared heaters provide an appropriate preform temperature profile. An axial stretch rod was used for stretching the preforms to a desirable length. Then, the final pressure or the full blow pressure was applied, which inflated the bottle to the desired volume (diameter and length of the bottles were 10.5 cm and 30 cm, resp.). This orientation process leads to the strain-induced crystallization and strain hardening of the stretched polymer [23, 24]. The bottles were solidified and cooled when they attained the shape of the mold. The sidewalls of the stretch blow molded bottles were used to investigate the tensile and oxygen barrier properties for nanocomposites and base PET.


## 3. Characterization

### 3.1. Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR)

Fourier Transformed Infrared (FTIR) spectra of modified clays were taken with a Perkin-Elmer 1600 spectrometer in the range of 700–4000 cm−1 to confirm that oleic acid was bonded to the clay surface after modification. Attenuated total reflection (ATR) is a sampling technique used in conjunction with infrared spectroscopy to examine the samples directly in the solid or liquid state without further preparation.


### 3.2. Wide Angle X-Ray Diffraction (WAXD)

A Rigaku Ultima X-ray diffractometer (The Woodlands, TX) with a Ni-filtered Cu Ka radiation (0.1541 nm wavelength) generated at 44 kV and 44 mA was used to determine the basal spacing of clays and their nanocomposites using the Bragg equation (λ=2dsin⁡θ), where θ is the diffraction angle, λ is the wavelength, and d is the basal spacing of clays. Samples were scanned at 0.5°/min in the range of 2θ = 1–8°.


### 3.3. Thermal Gravimetric Analysis (TGA)

Thermal Gravimetric Analysis (TGA) was conducted on a Q500 TGA instrument under nitrogen atmosphere. The samples of 5–10 mg were heated from room temperature to 700°C at a rate of 10°C/min.


### 3.4. Rheology and Melt Viscosity

Melt viscosity and rheological measurements of nanocomposites were determined using a parallel-plate Rheometric Scientific (RDA III) dynamic analyzer (Piscataway, NJ). Vacuum-dried samples were melted between parallel disks (diameter: 2.5 cm) at 270°C in the presence of nitrogen at 15% strain amplitude. Intrinsic viscosities (IV) of PET samples with different molecular weights were measured by dilute solution viscometry method [25] and the corresponding melt viscosity was measured by rheometer. Afterwards, a calibration curve was created by plotting IV versus ln⁡η∗ in order to determine the intrinsic viscosity from the corresponding melt viscosity.


### 3.5. Differential Scanning Calorimeter (DSC)

A Perkin-Elmer DSC 7 (Shelton, CT) was applied to measure the thermal characteristics of extruded PET and its nanocomposites in a nitrogen atmosphere. Dried samples (at 140°C for 12 hrs) of about 10 mg were heated at a rate of 10°C/min from 40 to 300°C.


### 3.6. Tensile Testing

An Instron 4400R tester was used to determine elastic modulus, stress, and strain at break of “dog-bone” shaped specimens (from the sidewalls of the PET bottles) according to ASTM D638 type IV. All the test samples were held for one week at 50% humidity and 23°C temperature before evaluation. Samples were stretched at a crosshead speed of 2 in/min during the test. Five specimens were measured for each evaluated sample type and averaged.


### 3.7. Oxygen Permeability

The oxygen permeability test was carried out on the sidewalls of the PET and nanocomposite bottles. This test was done by a MOCON OX-TRAN 1050 tester according to ASTM D3985. The experiment conditions were 23°C and 45% relative humidity. The exposed area and the thickness of the films were 50 cm2 and 10–13 mil, respectively. A mixture of 98% N2 and 2% H2 was used as a carrier gas. The instrument was calibrated with a standard Mylar polyester film before sample measurements.


## 3.1. Attenuated Total Reflection-Fourier Transform Infrared Spectroscopy (ATR-FTIR)

Fourier Transformed Infrared (FTIR) spectra of modified clays were taken with a Perkin-Elmer 1600 spectrometer in the range of 700–4000 cm−1 to confirm that oleic acid was bonded to the clay surface after modification. Attenuated total reflection (ATR) is a sampling technique used in conjunction with infrared spectroscopy to examine the samples directly in the solid or liquid state without further preparation.


## 3.2. Wide Angle X-Ray Diffraction (WAXD)

A Rigaku Ultima X-ray diffractometer (The Woodlands, TX) with a Ni-filtered Cu Ka radiation (0.1541 nm wavelength) generated at 44 kV and 44 mA was used to determine the basal spacing of clays and their nanocomposites using the Bragg equation (λ=2dsin⁡θ), where θ is the diffraction angle, λ is the wavelength, and d is the basal spacing of clays. Samples were scanned at 0.5°/min in the range of 2θ = 1–8°.


## 3.3. Thermal Gravimetric Analysis (TGA)

Thermal Gravimetric Analysis (TGA) was conducted on a Q500 TGA instrument under nitrogen atmosphere. The samples of 5–10 mg were heated from room temperature to 700°C at a rate of 10°C/min.


## 3.4. Rheology and Melt Viscosity

Melt viscosity and rheological measurements of nanocomposites were determined using a parallel-plate Rheometric Scientific (RDA III) dynamic analyzer (Piscataway, NJ). Vacuum-dried samples were melted between parallel disks (diameter: 2.5 cm) at 270°C in the presence of nitrogen at 15% strain amplitude. Intrinsic viscosities (IV) of PET samples with different molecular weights were measured by dilute solution viscometry method [25] and the corresponding melt viscosity was measured by rheometer. Afterwards, a calibration curve was created by plotting IV versus ln⁡η∗ in order to determine the intrinsic viscosity from the corresponding melt viscosity.


## 3.5. Differential Scanning Calorimeter (DSC)

A Perkin-Elmer DSC 7 (Shelton, CT) was applied to measure the thermal characteristics of extruded PET and its nanocomposites in a nitrogen atmosphere. Dried samples (at 140°C for 12 hrs) of about 10 mg were heated at a rate of 10°C/min from 40 to 300°C.


## 3.6. Tensile Testing

An Instron 4400R tester was used to determine elastic modulus, stress, and strain at break of “dog-bone” shaped specimens (from the sidewalls of the PET bottles) according to ASTM D638 type IV. All the test samples were held for one week at 50% humidity and 23°C temperature before evaluation. Samples were stretched at a crosshead speed of 2 in/min during the test. Five specimens were measured for each evaluated sample type and averaged.


## 3.7. Oxygen Permeability

The oxygen permeability test was carried out on the sidewalls of the PET and nanocomposite bottles. This test was done by a MOCON OX-TRAN 1050 tester according to ASTM D3985. The experiment conditions were 23°C and 45% relative humidity. The exposed area and the thickness of the films were 50 cm2 and 10–13 mil, respectively. A mixture of 98% N2 and 2% H2 was used as a carrier gas. The instrument was calibrated with a standard Mylar polyester film before sample measurements.


## 4. Results and Discussion

### 4.1. ATR-FTIR Results

FTIR spectra of oleic acid, MMT, and MMT modified with oleic acid (ol-MMT) are shown in Figure1. In the spectrum of MMT, the peak at 3619 cm−1 is related to O–H stretching. The Si–O out-of-plane and in-plane stretching bonds are observed at 1110 cm−1 and 996 cm−1, respectively. The Al–O and Mg–O stretching bonds are assigned to the peaks between 836 and 910 cm−1. The strong peak at 1630 cm−1 is assigned to the bending mode of absorbed water [26, 27].Figure 1
FTIR spectra of oleic acid, MMT, and modified clay (ol-MMT).The spectrum of oleic acid shows a peak at 1710 cm−1 which is related to the vibrations of C=O groups. Two peaks at 2932 cm−1 and 2856 cm−1 are related to the symmetric and asymmetric vibrations of methylene (–CH2) groups present in the fatty acid [26]. Characteristic peaks of the oleic acid are included in the spectra of the modified clay, indicating the presence of oleic acid in the gallery spacing of the nanoclays. These peaks are indicative of surfactant associated with the clay surface because the unbounded fatty acids were removed by washing with methanol. Since the vibrations of C=O groups remain the same (1710 cm−1) for oleic acid and ol-MMT samples, the possibility of the interaction between water molecules and metal ion present in the layer structure via a water bridge is speculated. The absence of O–H bending peak in the modified clay spectrum suggests that, with surfactant loading, MMT was transformed into an entirely hydrophobic material.FTIR spectra of oleic acid, Cloisite 30B, and Cloisite 30B modified with oleic acid (ol-30B) are shown in Figure2. Most of the peaks are the same in these components because of the organic surfactant present in the interlayer of 30B. In the spectrum of oleic acid, the peak at 3016 cm−1 is related to the double bond (C=C). This peak appeared in the spectrum of ol-30B. It can also be observed that the peak related to the C=O of the oleic acid has shifted to the higher wavenumbers (1738 cm−1), indicating the strong interaction between the C=O group and quaternary ammonium surfactant present in the interlayer of Cloisite 30B [28]. This shift could be an indicative of changing the carboxylic acid group to an ester group. The possibility of interaction between either the ammonium head groups or OH groups of quaternary ammonium surfactants and the carboxylic acid group of oleic acid via hydrogen bonding could be speculated.Figure 2
FTIR spectra of oleic acid, 30B, and modified clay (ol-30B).Table1 summarizes the IR bands of oleic acid, MMT, 30B, and the modified clays.Table 1
IR bands of oleic acid, MMT, 30B, ol-MMT, and ol-30B.
Wavenumber (cm−1)
Vibration
Oleic acid
MMT
Ol-MMT
30B
Ol-30B
3500–3800
3619
3619
3619
3619
O–H stretching
3016
—
—
—
3016
C–H stretching in C=C–H
2856, 2932
—
2856, 2932
2856, 2932
2856, 2932
Aliphatic C–H
1710
—
1710
—
1738
C=O stretching
—
1630
—
1630
—
O–H bending
1460
1460
1460
1460
1460
In-plane O–H band
1412
—
1412
—
1412
Methyl (–CH3) group
—
—
—
1457
1457
CH2 bending
1284
—
—
—
1312
C–O stretching
—
1110, 996
1110, 996
1110, 996
1110, 996
Si–O out-of-plane and in-plane stretching
937
—
—
—
—
Out-of-plane O–H stretching
—
910, 836
910, 836
910, 836
910, 836
Al–O and Mg–O stretching


### 4.2. XRD Results

XRD results obtained for pristine MMT and ol-MMT are shown in Figure3. The unmodified clay shows a characteristic peak at 2θ = 7.0°, indicatingd-spacing of 1.27 nm. The characteristic peak disappeared after modification of clay with the fatty acid. This indicates that oleic acid molecules could diffuse into the gallery spacing of pristine clay and interact with Na+ contained inside its interlayer via hydrogen bonding. This modification, therefore, could change the arrangement of layered silicates and make them disordered. This is an important achievement since the polymer chains should be able to more easily diffuse into the gallery spacing of the nanoclay during preparation of PET nanocomposites. Few studies have been reported with regard to achieving a disordered arrangement of nanoclays after the modification process.Figure 3
XRD results of MMT and ol-MMT.XRD results of Cloisite 30B and ol-30B are shown in Figure4. Commercial 30B (clay modified with methyl tallow bis-2-hydroxyethyl ammonium cations) hasd-spacing of 1.88 nm. Modification of clay with oleic acid resulted in a shift in the (001) peak by 2.6°. This corresponds to an increase ind-spacing of about 2.36 nm, indicating that the oleic acid molecules are intercalated into the clay galleries. This is also a large increase of the gallery spacing of nanoclays. Because of this large gallery spacing and compatibility of ol-30B with PET, good dispersion of these nanoparticles into the PET matrix is expected during the process of preparing nanocomposites.Figure 4
XRD results of 30B and ol-30B.


### 4.3. TGA Results

The percentage mass loss with temperature plots for oleic acid, MMT, and, ol-MMT is shown in Figure5. There was no significant mass loss for unmodified clay up to 570°C. Evaporation of free water in clay, which is hydrophilic, results in an initial mass loss below 200°C. Evaporation of structural water under dehydroxylation causes a mass loss between 570 and 700°C in the unmodified clay [16, 29].Figure 5
TGA results of oleic acid, MMT, and ol-MMT.Since the boiling point of oleic acid is about 250°C, the percentage mass loss increased from 0 to 100% very quickly. MMT modified with oleic acid showed no significant mass loss up to 250°C. This may indicate that the fatty acid had penetrated inside the gallery spacing of layered silicates and made them more hydrophobic (the initial degradation, below 100°C, for ol-MMT is much less than that of MMT). The onset of decomposition temperature (T0) value of ol-MMT is 250°C, which corresponds with the boiling point of oleic acid. Therefore, the thermal stability of modified MMT decreased in the presence of oleic acid. The degradation of modified clay is, however, a slow process because of the strong bonds between clay particles and fatty acid molecules. From the results, it can be concluded that the modification process was successful and clays modified with oleic acid could survive PET processing temperatures of ~300°C.In the case of Cloisite 30B organoclays shown in Figure6, the major mass loss occurred in the temperature range of 180–420°C. Quaternary ammonium ions present in 30B clays started to degrade at the onset of decomposition temperature (T0 = 180°C).Figure 6
TGA results of oleic acid, 30B, and ol-30B.Modification of Cloisite 30B with oleic acid reducedT0 value of ol-30B to 160°C. Faster and more degradation of modifiers, therefore, occurred in the case of ol-30B. This indicated that fatty acid was intercalated inside the gallery spacing of the layered silicates. Although the decomposition temperature of the modifiers is below the PET processing temperature, the very large gallery spacing of 30B modified with fatty acid along with high affinity between organic modifiers and PET should facilitate the diffusion of polymer chains into the interlayers of modified clays.


### 4.4. Morphology of Nanocomposites

XRD data for 2 wt.% PET/MMT, PET/ol-MMT, and PET/ol-30B nanocomposites are shown in Figure7. PET/ol-MMT is nanocomposite prepared with pristine clay modified with oleic acid, while PET/ol-30B is nanocomposite prepared with Cloisite 30B modified with oleic acid. A characteristic diffraction peak appeared at 2θ = 6.1° withd-spacing of about 1.4 nm for 2 wt.% PET/MMT nanocomposites, indicating the agglomeration of nanoparticles in the PET. The presence of flat curves for both PET/ol-MMT and PET/ol-30B samples indicates that exfoliated structures may have been obtained. Modification of nanoclays by fatty acid, therefore, appears to have resulted in an exfoliated structure for these PET/clay nanocomposites. In fact, the quaternary amines and fatty acids with long alkyl chain present in the interlayer space of 30B facilitated the intercalation of PET chains during the melt compounding process. Moreover, according to the FTIR results, the presence of the long alkyl chains in the interlayer space reduced the hydrophilic character of the clay and because of the interaction between PET and fatty acid molecules, guest polymer chains were drawn inside the clay interlayer space.Figure 7
XRD results of 2 wt.% PET/ol-MMT and PET/ol-30B nanocomposites.TEM was used to verify the results obtained from XRD data. Micrographs of 2 wt.% PET/ol-MMT and PET/ol-30B nanocomposites are shown in Figures8 and 9. Since the original micrographs (left side) are vague, a program was used to make a better contrast between clay particles and polymer matrix. The processed micrographs are shown in the right side. It can be seen that the particles were well dispersed into the PET matrix. There are, however, some agglomerations of clay particles, especially in the case of 2% PET/ol-MMT sample. These TEM results indicate that modification of clays with fatty acids provides a combination of exfoliated/intercalated morphologies for PET/clay nanocomposites.Figure 8
TEM micrographs of 2 wt.% PET/ol-MMT nanocomposite.Figure 9
TEM micrographs of 2 wt.% PET/ol-30B nanocomposite.


### 4.5. Rheology and Melt Viscosity

Melt viscosity results and corresponding PET equivalent IV values for extruded PET and 2 wt.% nanocomposites are shown in Figure10 and Table 2. The complex viscosity decreased with increasing angular frequency for all the samples. The maximum value of complex viscosity was observed for extruded PET sample. The 2 wt.% PET/MMT nanocomposite exhibited lower complex viscosity and IV values compared to the 2 wt.% PET/ol-MMT nanocomposite. The modification of nanoclays with oleic acid improved the dispersion of nanoparticles into the PET matrix. These well-dispersed nanoparticles can present a shielding effect which reduces the mass transport rates during the degradation process in the polymer matrix [30]. The complex viscosity of PET/ol-MMT is, therefore, very close to that of extruded PET. PET/ol-30B nanocomposites exhibited lower complex viscosity and IV values compared to the PET/ol-MMT. As shown in Figure 6, presence of fatty acids in Cloisite 30B causes thermal instability in ol-30B. As a result, degradation of the polymer matrix was accelerated by the degradation of organic modifier present in ol-30B nanoparticles. The complex viscosity and IV values of PET/ol-30B were higher than those of the PET/30B samples. This confirms the improvement in the dispersion of 30B nanoparticles and their shielding effect after modification with oleic acid. PET/MMT and PET/30B, however, exhibited the same behavior and IV values. In fact, the degradation of polymer matrix was accelerated by the agglomerations of unmodified MMT and 30B nanoparticles. These agglomerations increased the mass transport rate during the degradation process in the polymer. This, therefore, causes a reduction in the complex viscosity values of composites. It can be concluded that although 30B shows better compatibility with PET, its thermal degradation causes it to behave like an unmodified clay.Table 2
IV values of PET and nanocomposites.
Sample
IV (dl/g)
Pure PET
0.81
±
0.01
Extruded PET
0.64
±
0.01
2.0 wt.% PET/MMT
0.50
±
0.01
2.0 wt.% PET/ol-MMT
0.62
±
0.02
2.0 wt.% PET/30B
0.51
±
0.03
2.0 wt.% PET/ol-30B
0.57
±
0.02Figure 10
Melt viscosity of PET and nanocomposites.The storage modulus (G′) and loss modulus (G′′) versus frequency for all samples are shown in Figures 11 and 12. Samples prepared with unmodified nanoclays showed lower storage modulus because of the lower level of clay dispersion. On the other hand, extruded PET, PET/ol-MMT, and PET/ol-30B nanocomposites exhibited higher storage moduli as a result of more interconnected structure and geometric constraints. The storage modulus of PET/ol-MMT is very close to that of extruded PET. Poorer dispersion of MMT and 30B particles accelerated the degradation process in the PET matrix; hence the storage modulus of PET/MMT and PET/30B nanocomposites is lower than that of PET/ol-MMT and PET/ol-30B. Although the storage modulus of PET/30B is higher than that of PET/MMT at lower frequencies because of better affinity with PET, their G′ values would be similar at higher frequencies, where the behavior of the matrix is dominant.Figure 11
Storage modulus of PET and nanocomposites.Figure 12
Loss modulus of PET and nanocomposites.


### 4.6. Thermal Analysis of Nanocomposites

Thermal characteristics of extruded PET and its nanocomposites are presented in Table3. Results show that the glass transition temperature (Tg) and melting temperature (Tm) of all nanocomposites samples are very close to those of extruded PET. The enthalpy of melting (ΔHm) values of nanocomposites is slightly higher than that of extruded PET. According to Table 3, in the case of PET nanocomposites, crystallization occurred during the quenching step and ΔHcm was low compared to that of PET.Table 3
DSC results of 2 wt.% PET/MMT, PET/ol-MMT, PET/30B, and PET/ol-30B nanocomposites.
Sample
Reheating at 10°C/min
Cooling at 10°C/min
T
g (°C)
Δ
H
c
m (J/g)
T
m (°C)
Δ
H
m (J/g)
T
c
c (°C)
T
o
n
c (°C)
t
1
/
2 (min)
Δ
H
c
c (J/g)
Extruded PET
79.1
20.7
244.1
32.8
186.2
195.3
0.91
34.4
2 wt.% PET/MMT
79.8
5.9
245.4
37.0
192.7
199.9
0.72
38.5
2 wt.% PET/ol-MMT
79.1
10.5
244.1
33.6
193.1
200.8
0.77
35.1
2 wt.% PET/30B
78.2
13.3
244.8
35.2
193.7
201.1
0.74
36.7
2 wt.% PET/ol-30B
77.6
11.2
245.1
32.8
188.8
196.6
0.78
34.0As shown by the cooling process data given in Table3, the crystallization peak temperature (Tcc) and the onset of crystallization temperature (Tonc) of nanocomposites are slightly higher than those of PET, indicating that crystallization in nanocomposites occurs a little bit faster. Half time of crystallization (t1/2), which is also an indicator of the overall crystallization rate corresponding to the effects of both nucleation and crystal growth, can be measured by using the following equation [31]:(1)t1/2=Tonc-Tccχ,where Tonc is the onset of crystallization temperature, Tcc is the crystallization temperature at the exothermic peak, and χ is the cooling rate (°C/min). According to Table 3, t1/2 values of the nanocomposites are lower than those of extruded PET. t1/2 values of PET/ol-MMT and PET/ol-30B nanocomposites, however, are higher than those of PET/MMT and PET/30B and closer to those of extruded PET. From these results, it can be concluded that unmodified clay has a significant influence on the crystallization of PET because of the low level of dispersion of these particles into the PET. Cloisite 30B also showed higher rate of crystallization because of the thermal degradation of organic modifier. Modification of MMT and Cloisite 30B with oleic acid, however, has a smaller effect on the crystallization of polymer because of the improvement in the dispersion of nanoparticles into the polymer matrix and less amount of agglomeration.


### 4.7. Mechanical Properties

The strength results obtained for sidewalls of PET and nanocomposite bottles are shown in Figure13. It can be seen that the PET nanocomposites prepared with both modified clays exhibited higher strength values than those of the PET because of the reinforcing effect of the stiff clay particles (8% and 16% improvement for 2 wt.% PET/ol-MMT and 2 wt.% PET/ol-30B, resp.). The nanocomposites prepared with unmodified clay (2 wt.% PET/MMT), however, showed mechanical property improvement of only 5%.Figure 13
Strength of the sidewall of stretched blown PET and nanocomposite bottles.Young’s modulus results for sidewalls of PET and nanocomposite bottles are also presented in Figure13. PET nanocomposites prepared with both modified clays exhibited higher Young’s modulus values than the PET (7% and 25% improvement for 2 wt.% PET/ol-MMT and 2 wt.% PET/ol-30B, resp.). The nanocomposites prepared with unmodified clay (2 wt.% PET/MMT), however, showed only 2% improvement in their Young’s modulus values.


### 4.8. Barrier Properties

Oxygen permeability results recorded for the sidewalls of PET and nanocomposite bottles are shown in Figure14. It can be seen that there are 53% and 74% improvements in oxygen permeability for 2 wt.% PET/ol-MMT and 2 wt.% PET/ol-30B nanocomposites, respectively. In fact, the well-dispersed modified clays created a tortuous path for gas molecules and reduced the permeability of the samples. Although phase separation upon stretching of the samples is one of the challenges that researchers faced [32], the good adhesion between the clay particles and PET matrix, in this study, resulted in a significant improvement in the barrier properties of stretched blown bottles, even upon stretching of the samples.Figure 14
Barrier properties of the sidewalls of stretched blown PET and nanocomposite bottles.Beside the passive barrier effect of modified nanoparticles, fatty acid, intercalated into the interlayer of layered silicates, might act as an oxygen scavenger and reduce the amount of oxygen which passes through the films. In fact, oleic acid includes one double bond which can react with oxygen molecules to reduce the permeability of the samples.In order to investigate the role of passive and active barrier mechanisms on the permeability of the samples, a measure of cumulative amount of oxygen passing through the films with time was used. The idea of adding active oxygen scavenger into the PET matrix is that the scavenger could delay the induction time period of oxygen transmitted into the PET container and then after some time achieve a steady state similar to that of pure PET. Cumulative plots for PET and PET nanocomposites are shown in Figure15. The data were collected for 38 days. The slopes of Qt versus time are still changing and they did not achieve a steady state. Therefore, the exact values of induction time are not known yet. However, calculating the slope of Qt versus time between 20 and 38 days gives an indication of the transmission rates. The extrapolated slopes to zero Qt give the values of apparent induction time as shown in Table 4.Table 4
Slope and intercepts of cumulative plots.
Sample
Slope (cc/m2·mil·day)
Intercept (days)
PET
8.6
13
2.0 wt.% PET/MMT
3.1
13
2.0 wt.% PET/30B
2.4
13
2.0 wt.% PET/ol-MMT
2.9
14
2.0 wt.% PET/ol-30B
2.0
14Figure 15
Cumulative permeability data for sidewall of stretched blown PET and nanocomposite bottles.In relationship to the unmodified PET, significant reductions in the slopes of the other cumulative plots occurred. These reductions for samples prepared with modified clays are because of the improved compatibility between the clay particles and PET matrix and the good dispersion of these particles into the PET. This also confirmed that the well-dispersed modified clays acted as passive barriers and reduced the permeability of the samples. There was, however, no significant change in the intercepts or apparent induction periods of the samples. While it was expected that PET/fatty acid-modified clay nanocomposite may act as an active barrier as well, the data were not carried out to a longer time to confirm the presence of active barrier mechanism. More research is ongoing to confirm the barrier mechanisms in these systems.


## 4.1. ATR-FTIR Results

FTIR spectra of oleic acid, MMT, and MMT modified with oleic acid (ol-MMT) are shown in Figure1. In the spectrum of MMT, the peak at 3619 cm−1 is related to O–H stretching. The Si–O out-of-plane and in-plane stretching bonds are observed at 1110 cm−1 and 996 cm−1, respectively. The Al–O and Mg–O stretching bonds are assigned to the peaks between 836 and 910 cm−1. The strong peak at 1630 cm−1 is assigned to the bending mode of absorbed water [26, 27].Figure 1
FTIR spectra of oleic acid, MMT, and modified clay (ol-MMT).The spectrum of oleic acid shows a peak at 1710 cm−1 which is related to the vibrations of C=O groups. Two peaks at 2932 cm−1 and 2856 cm−1 are related to the symmetric and asymmetric vibrations of methylene (–CH2) groups present in the fatty acid [26]. Characteristic peaks of the oleic acid are included in the spectra of the modified clay, indicating the presence of oleic acid in the gallery spacing of the nanoclays. These peaks are indicative of surfactant associated with the clay surface because the unbounded fatty acids were removed by washing with methanol. Since the vibrations of C=O groups remain the same (1710 cm−1) for oleic acid and ol-MMT samples, the possibility of the interaction between water molecules and metal ion present in the layer structure via a water bridge is speculated. The absence of O–H bending peak in the modified clay spectrum suggests that, with surfactant loading, MMT was transformed into an entirely hydrophobic material.FTIR spectra of oleic acid, Cloisite 30B, and Cloisite 30B modified with oleic acid (ol-30B) are shown in Figure2. Most of the peaks are the same in these components because of the organic surfactant present in the interlayer of 30B. In the spectrum of oleic acid, the peak at 3016 cm−1 is related to the double bond (C=C). This peak appeared in the spectrum of ol-30B. It can also be observed that the peak related to the C=O of the oleic acid has shifted to the higher wavenumbers (1738 cm−1), indicating the strong interaction between the C=O group and quaternary ammonium surfactant present in the interlayer of Cloisite 30B [28]. This shift could be an indicative of changing the carboxylic acid group to an ester group. The possibility of interaction between either the ammonium head groups or OH groups of quaternary ammonium surfactants and the carboxylic acid group of oleic acid via hydrogen bonding could be speculated.Figure 2
FTIR spectra of oleic acid, 30B, and modified clay (ol-30B).Table1 summarizes the IR bands of oleic acid, MMT, 30B, and the modified clays.Table 1
IR bands of oleic acid, MMT, 30B, ol-MMT, and ol-30B.
Wavenumber (cm−1)
Vibration
Oleic acid
MMT
Ol-MMT
30B
Ol-30B
3500–3800
3619
3619
3619
3619
O–H stretching
3016
—
—
—
3016
C–H stretching in C=C–H
2856, 2932
—
2856, 2932
2856, 2932
2856, 2932
Aliphatic C–H
1710
—
1710
—
1738
C=O stretching
—
1630
—
1630
—
O–H bending
1460
1460
1460
1460
1460
In-plane O–H band
1412
—
1412
—
1412
Methyl (–CH3) group
—
—
—
1457
1457
CH2 bending
1284
—
—
—
1312
C–O stretching
—
1110, 996
1110, 996
1110, 996
1110, 996
Si–O out-of-plane and in-plane stretching
937
—
—
—
—
Out-of-plane O–H stretching
—
910, 836
910, 836
910, 836
910, 836
Al–O and Mg–O stretching


## 4.2. XRD Results

XRD results obtained for pristine MMT and ol-MMT are shown in Figure3. The unmodified clay shows a characteristic peak at 2θ = 7.0°, indicatingd-spacing of 1.27 nm. The characteristic peak disappeared after modification of clay with the fatty acid. This indicates that oleic acid molecules could diffuse into the gallery spacing of pristine clay and interact with Na+ contained inside its interlayer via hydrogen bonding. This modification, therefore, could change the arrangement of layered silicates and make them disordered. This is an important achievement since the polymer chains should be able to more easily diffuse into the gallery spacing of the nanoclay during preparation of PET nanocomposites. Few studies have been reported with regard to achieving a disordered arrangement of nanoclays after the modification process.Figure 3
XRD results of MMT and ol-MMT.XRD results of Cloisite 30B and ol-30B are shown in Figure4. Commercial 30B (clay modified with methyl tallow bis-2-hydroxyethyl ammonium cations) hasd-spacing of 1.88 nm. Modification of clay with oleic acid resulted in a shift in the (001) peak by 2.6°. This corresponds to an increase ind-spacing of about 2.36 nm, indicating that the oleic acid molecules are intercalated into the clay galleries. This is also a large increase of the gallery spacing of nanoclays. Because of this large gallery spacing and compatibility of ol-30B with PET, good dispersion of these nanoparticles into the PET matrix is expected during the process of preparing nanocomposites.Figure 4
XRD results of 30B and ol-30B.


## 4.3. TGA Results

The percentage mass loss with temperature plots for oleic acid, MMT, and, ol-MMT is shown in Figure5. There was no significant mass loss for unmodified clay up to 570°C. Evaporation of free water in clay, which is hydrophilic, results in an initial mass loss below 200°C. Evaporation of structural water under dehydroxylation causes a mass loss between 570 and 700°C in the unmodified clay [16, 29].Figure 5
TGA results of oleic acid, MMT, and ol-MMT.Since the boiling point of oleic acid is about 250°C, the percentage mass loss increased from 0 to 100% very quickly. MMT modified with oleic acid showed no significant mass loss up to 250°C. This may indicate that the fatty acid had penetrated inside the gallery spacing of layered silicates and made them more hydrophobic (the initial degradation, below 100°C, for ol-MMT is much less than that of MMT). The onset of decomposition temperature (T0) value of ol-MMT is 250°C, which corresponds with the boiling point of oleic acid. Therefore, the thermal stability of modified MMT decreased in the presence of oleic acid. The degradation of modified clay is, however, a slow process because of the strong bonds between clay particles and fatty acid molecules. From the results, it can be concluded that the modification process was successful and clays modified with oleic acid could survive PET processing temperatures of ~300°C.In the case of Cloisite 30B organoclays shown in Figure6, the major mass loss occurred in the temperature range of 180–420°C. Quaternary ammonium ions present in 30B clays started to degrade at the onset of decomposition temperature (T0 = 180°C).Figure 6
TGA results of oleic acid, 30B, and ol-30B.Modification of Cloisite 30B with oleic acid reducedT0 value of ol-30B to 160°C. Faster and more degradation of modifiers, therefore, occurred in the case of ol-30B. This indicated that fatty acid was intercalated inside the gallery spacing of the layered silicates. Although the decomposition temperature of the modifiers is below the PET processing temperature, the very large gallery spacing of 30B modified with fatty acid along with high affinity between organic modifiers and PET should facilitate the diffusion of polymer chains into the interlayers of modified clays.


## 4.4. Morphology of Nanocomposites

XRD data for 2 wt.% PET/MMT, PET/ol-MMT, and PET/ol-30B nanocomposites are shown in Figure7. PET/ol-MMT is nanocomposite prepared with pristine clay modified with oleic acid, while PET/ol-30B is nanocomposite prepared with Cloisite 30B modified with oleic acid. A characteristic diffraction peak appeared at 2θ = 6.1° withd-spacing of about 1.4 nm for 2 wt.% PET/MMT nanocomposites, indicating the agglomeration of nanoparticles in the PET. The presence of flat curves for both PET/ol-MMT and PET/ol-30B samples indicates that exfoliated structures may have been obtained. Modification of nanoclays by fatty acid, therefore, appears to have resulted in an exfoliated structure for these PET/clay nanocomposites. In fact, the quaternary amines and fatty acids with long alkyl chain present in the interlayer space of 30B facilitated the intercalation of PET chains during the melt compounding process. Moreover, according to the FTIR results, the presence of the long alkyl chains in the interlayer space reduced the hydrophilic character of the clay and because of the interaction between PET and fatty acid molecules, guest polymer chains were drawn inside the clay interlayer space.Figure 7
XRD results of 2 wt.% PET/ol-MMT and PET/ol-30B nanocomposites.TEM was used to verify the results obtained from XRD data. Micrographs of 2 wt.% PET/ol-MMT and PET/ol-30B nanocomposites are shown in Figures8 and 9. Since the original micrographs (left side) are vague, a program was used to make a better contrast between clay particles and polymer matrix. The processed micrographs are shown in the right side. It can be seen that the particles were well dispersed into the PET matrix. There are, however, some agglomerations of clay particles, especially in the case of 2% PET/ol-MMT sample. These TEM results indicate that modification of clays with fatty acids provides a combination of exfoliated/intercalated morphologies for PET/clay nanocomposites.Figure 8
TEM micrographs of 2 wt.% PET/ol-MMT nanocomposite.Figure 9
TEM micrographs of 2 wt.% PET/ol-30B nanocomposite.


## 4.5. Rheology and Melt Viscosity

Melt viscosity results and corresponding PET equivalent IV values for extruded PET and 2 wt.% nanocomposites are shown in Figure10 and Table 2. The complex viscosity decreased with increasing angular frequency for all the samples. The maximum value of complex viscosity was observed for extruded PET sample. The 2 wt.% PET/MMT nanocomposite exhibited lower complex viscosity and IV values compared to the 2 wt.% PET/ol-MMT nanocomposite. The modification of nanoclays with oleic acid improved the dispersion of nanoparticles into the PET matrix. These well-dispersed nanoparticles can present a shielding effect which reduces the mass transport rates during the degradation process in the polymer matrix [30]. The complex viscosity of PET/ol-MMT is, therefore, very close to that of extruded PET. PET/ol-30B nanocomposites exhibited lower complex viscosity and IV values compared to the PET/ol-MMT. As shown in Figure 6, presence of fatty acids in Cloisite 30B causes thermal instability in ol-30B. As a result, degradation of the polymer matrix was accelerated by the degradation of organic modifier present in ol-30B nanoparticles. The complex viscosity and IV values of PET/ol-30B were higher than those of the PET/30B samples. This confirms the improvement in the dispersion of 30B nanoparticles and their shielding effect after modification with oleic acid. PET/MMT and PET/30B, however, exhibited the same behavior and IV values. In fact, the degradation of polymer matrix was accelerated by the agglomerations of unmodified MMT and 30B nanoparticles. These agglomerations increased the mass transport rate during the degradation process in the polymer. This, therefore, causes a reduction in the complex viscosity values of composites. It can be concluded that although 30B shows better compatibility with PET, its thermal degradation causes it to behave like an unmodified clay.Table 2
IV values of PET and nanocomposites.
Sample
IV (dl/g)
Pure PET
0.81
±
0.01
Extruded PET
0.64
±
0.01
2.0 wt.% PET/MMT
0.50
±
0.01
2.0 wt.% PET/ol-MMT
0.62
±
0.02
2.0 wt.% PET/30B
0.51
±
0.03
2.0 wt.% PET/ol-30B
0.57
±
0.02Figure 10
Melt viscosity of PET and nanocomposites.The storage modulus (G′) and loss modulus (G′′) versus frequency for all samples are shown in Figures 11 and 12. Samples prepared with unmodified nanoclays showed lower storage modulus because of the lower level of clay dispersion. On the other hand, extruded PET, PET/ol-MMT, and PET/ol-30B nanocomposites exhibited higher storage moduli as a result of more interconnected structure and geometric constraints. The storage modulus of PET/ol-MMT is very close to that of extruded PET. Poorer dispersion of MMT and 30B particles accelerated the degradation process in the PET matrix; hence the storage modulus of PET/MMT and PET/30B nanocomposites is lower than that of PET/ol-MMT and PET/ol-30B. Although the storage modulus of PET/30B is higher than that of PET/MMT at lower frequencies because of better affinity with PET, their G′ values would be similar at higher frequencies, where the behavior of the matrix is dominant.Figure 11
Storage modulus of PET and nanocomposites.Figure 12
Loss modulus of PET and nanocomposites.


## 4.6. Thermal Analysis of Nanocomposites

Thermal characteristics of extruded PET and its nanocomposites are presented in Table3. Results show that the glass transition temperature (Tg) and melting temperature (Tm) of all nanocomposites samples are very close to those of extruded PET. The enthalpy of melting (ΔHm) values of nanocomposites is slightly higher than that of extruded PET. According to Table 3, in the case of PET nanocomposites, crystallization occurred during the quenching step and ΔHcm was low compared to that of PET.Table 3
DSC results of 2 wt.% PET/MMT, PET/ol-MMT, PET/30B, and PET/ol-30B nanocomposites.
Sample
Reheating at 10°C/min
Cooling at 10°C/min
T
g (°C)
Δ
H
c
m (J/g)
T
m (°C)
Δ
H
m (J/g)
T
c
c (°C)
T
o
n
c (°C)
t
1
/
2 (min)
Δ
H
c
c (J/g)
Extruded PET
79.1
20.7
244.1
32.8
186.2
195.3
0.91
34.4
2 wt.% PET/MMT
79.8
5.9
245.4
37.0
192.7
199.9
0.72
38.5
2 wt.% PET/ol-MMT
79.1
10.5
244.1
33.6
193.1
200.8
0.77
35.1
2 wt.% PET/30B
78.2
13.3
244.8
35.2
193.7
201.1
0.74
36.7
2 wt.% PET/ol-30B
77.6
11.2
245.1
32.8
188.8
196.6
0.78
34.0As shown by the cooling process data given in Table3, the crystallization peak temperature (Tcc) and the onset of crystallization temperature (Tonc) of nanocomposites are slightly higher than those of PET, indicating that crystallization in nanocomposites occurs a little bit faster. Half time of crystallization (t1/2), which is also an indicator of the overall crystallization rate corresponding to the effects of both nucleation and crystal growth, can be measured by using the following equation [31]:(1)t1/2=Tonc-Tccχ,where Tonc is the onset of crystallization temperature, Tcc is the crystallization temperature at the exothermic peak, and χ is the cooling rate (°C/min). According to Table 3, t1/2 values of the nanocomposites are lower than those of extruded PET. t1/2 values of PET/ol-MMT and PET/ol-30B nanocomposites, however, are higher than those of PET/MMT and PET/30B and closer to those of extruded PET. From these results, it can be concluded that unmodified clay has a significant influence on the crystallization of PET because of the low level of dispersion of these particles into the PET. Cloisite 30B also showed higher rate of crystallization because of the thermal degradation of organic modifier. Modification of MMT and Cloisite 30B with oleic acid, however, has a smaller effect on the crystallization of polymer because of the improvement in the dispersion of nanoparticles into the polymer matrix and less amount of agglomeration.


## 4.7. Mechanical Properties

The strength results obtained for sidewalls of PET and nanocomposite bottles are shown in Figure13. It can be seen that the PET nanocomposites prepared with both modified clays exhibited higher strength values than those of the PET because of the reinforcing effect of the stiff clay particles (8% and 16% improvement for 2 wt.% PET/ol-MMT and 2 wt.% PET/ol-30B, resp.). The nanocomposites prepared with unmodified clay (2 wt.% PET/MMT), however, showed mechanical property improvement of only 5%.Figure 13
Strength of the sidewall of stretched blown PET and nanocomposite bottles.Young’s modulus results for sidewalls of PET and nanocomposite bottles are also presented in Figure13. PET nanocomposites prepared with both modified clays exhibited higher Young’s modulus values than the PET (7% and 25% improvement for 2 wt.% PET/ol-MMT and 2 wt.% PET/ol-30B, resp.). The nanocomposites prepared with unmodified clay (2 wt.% PET/MMT), however, showed only 2% improvement in their Young’s modulus values.


## 4.8. Barrier Properties

Oxygen permeability results recorded for the sidewalls of PET and nanocomposite bottles are shown in Figure14. It can be seen that there are 53% and 74% improvements in oxygen permeability for 2 wt.% PET/ol-MMT and 2 wt.% PET/ol-30B nanocomposites, respectively. In fact, the well-dispersed modified clays created a tortuous path for gas molecules and reduced the permeability of the samples. Although phase separation upon stretching of the samples is one of the challenges that researchers faced [32], the good adhesion between the clay particles and PET matrix, in this study, resulted in a significant improvement in the barrier properties of stretched blown bottles, even upon stretching of the samples.Figure 14
Barrier properties of the sidewalls of stretched blown PET and nanocomposite bottles.Beside the passive barrier effect of modified nanoparticles, fatty acid, intercalated into the interlayer of layered silicates, might act as an oxygen scavenger and reduce the amount of oxygen which passes through the films. In fact, oleic acid includes one double bond which can react with oxygen molecules to reduce the permeability of the samples.In order to investigate the role of passive and active barrier mechanisms on the permeability of the samples, a measure of cumulative amount of oxygen passing through the films with time was used. The idea of adding active oxygen scavenger into the PET matrix is that the scavenger could delay the induction time period of oxygen transmitted into the PET container and then after some time achieve a steady state similar to that of pure PET. Cumulative plots for PET and PET nanocomposites are shown in Figure15. The data were collected for 38 days. The slopes of Qt versus time are still changing and they did not achieve a steady state. Therefore, the exact values of induction time are not known yet. However, calculating the slope of Qt versus time between 20 and 38 days gives an indication of the transmission rates. The extrapolated slopes to zero Qt give the values of apparent induction time as shown in Table 4.Table 4
Slope and intercepts of cumulative plots.
Sample
Slope (cc/m2·mil·day)
Intercept (days)
PET
8.6
13
2.0 wt.% PET/MMT
3.1
13
2.0 wt.% PET/30B
2.4
13
2.0 wt.% PET/ol-MMT
2.9
14
2.0 wt.% PET/ol-30B
2.0
14Figure 15
Cumulative permeability data for sidewall of stretched blown PET and nanocomposite bottles.In relationship to the unmodified PET, significant reductions in the slopes of the other cumulative plots occurred. These reductions for samples prepared with modified clays are because of the improved compatibility between the clay particles and PET matrix and the good dispersion of these particles into the PET. This also confirmed that the well-dispersed modified clays acted as passive barriers and reduced the permeability of the samples. There was, however, no significant change in the intercepts or apparent induction periods of the samples. While it was expected that PET/fatty acid-modified clay nanocomposite may act as an active barrier as well, the data were not carried out to a longer time to confirm the presence of active barrier mechanism. More research is ongoing to confirm the barrier mechanisms in these systems.


## 5. Conclusions

Pristine clay and Cloisite 30B were modified with a long-chain fatty acid. FTIR and XRD results revealed that oleic acid could interact with the surface of pristine clay (MMT) and commercially modified clays (Cloisite 30B) to open up their gallery spacing and make them more compatible with PET. This modification increased the gallery spacing of the layered silicates significantly. In the case of MMT modified with oleic acid (ol-MMT), a disordered structure was achieved. TGA results indicated that ol-MMT is thermally stable and can survive PET processing temperatures. There is, however, more degradation in the case of Cloisite 30B modified with oleic acid (ol-30B). XRD indicated that there is a significant improvement on the dispersion of nanoclays modified with long-chain oleic acid into the PET matrix, and an exfoliated structure was achieved. DSC data also revealed that crystallization behaviors of nanocomposites prepared with oleic acid-modified clays are similar to those of extruded PET. Significant improvements in the mechanical and barrier properties of oriented PET/clay nanocomposites were also achieved. Well-dispersed modified clays acted as a passive barrier and improved the barrier properties of the films significantly. This improvement might be also a result of the reaction between the scavenger present in the gallery spacing of nanoparticles and oxygen.



---

*Source: 7625906-2017-05-11.xml*