# Synthesis and Electrochemical Characterization of Mesoporous MnO2

Authors: Jia Chang Zhao; Jun Wang; Jing Li Xu
Journal: Journal of Chemistry
 (2015)

---

## Abstract

The pore, crystal structure, and electrochemical performance of mesoporous MnO2 prepared by silica sol template method as electrode material for supercapacitor were investigated in this work. It is found that the crystal structure of nonporous and mesoporous MnO2 is confirmed to be β-MnO2 and the crystallinity of mesoporous MnO2 decreases due to the formation of mesopore. The results of electrochemical performance show that the specific capacitances of the sample prepared by using 20 g of Mn(NO3)2 solution and 40 g of silica sol (named MMO-4) at the scan rate of 5 mV/s are the highest (163.2 F/g), in comparison with 19.3 F/g of that of the sample of blank, suggesting the important role of pore-forming using silica sol as template. As the potential scan rate is raised to 200 mV/s, the specific capacitances of the sample of blank and MMO-4 are 12.2 F/g and 21.6 F/g, respectively. The great improvement of specific capacitance is probably due to the enlarged activated surface area after template is added.


---

## Body

## 1. Introduction

MnO2 used as the key component of electrode for supercapacitor has been widely studied in recent years. MnO2 electrode material has been prepared by various methods, such as the sol-gel route [1], hydrothermal method [2], electrochemical deposition [3], microemulsion method [4], and sonochemistry method [5]. Recently, mesoporous MnO2 has been prepared by various methods and used as the electrode material for supercapacitor [6–10]. And the unique mesopore system and large surface area are expected to favor ion transfer in the pore system and increase the MnO2, electrolyte interfacial area, respectively, and thus can improve the electrochemical performance of the MnO2 electrode material. Silica sol as hard template has been widely used as the template for the synthesis of mesoporous polymer [11], mesoporous inorganic oxide [12], mesoporous carbon [13], and mesoporous metal [14]. In this paper, mesoporous MnO2 was synthesized by utilizing Mn(NO3)2 as manganese source and silica sol as template. And the electrochemical performance was investigated by cyclic voltammetry and chronopotentiometry.


## 2. Experimental

### 2.1. Reagents and Solutions

Mn(NO3)2 solution (50 wt.%) was purchased from Shanghai Chemical Reagent Co. Ltd. and silica sol (20 wt.%) with average particle size of 10 nm was purchased from Shanghai Debang Company.


### 2.2. Materials Preparation

Silica sol was added to Mn(NO3)2 solution and mixed thoroughly. The mixture was condensed to form precursor after the evaporation of water. And the precursor was heated up to 300°C at a rate of 5°C/min and maintained for 2 h. The obtained products were first washed by 3 M KOH solution for 10 h and then by deionized water until pH reached 7. The mass of manganese source (Mn(NO3)2) solution was fixed at 20 g, whereas that of silica sol was 10, 20, 30, 40, 50, and 60 g, respectively. The MnO2 prepared by the decomposition of Mn(NO3)2 without template was designated as blank. And those synthesized with silica sol were designated as MMO-1, MMO-2, MMO-3, MMO-4, MMO-5, and MMO-6 accordingly.


### 2.3. Instrumentation

The pore characteristics of the mesoporous MnO2 were measured on a Micromeritics (ASAP 2010) instrument, using nitrogen at 77 K. Mesopore size distributions were determined by BJH method. The micropore volume (V
mic) and the total pore volume (V
t) were calculated from the amount of N2 adsorbed at a relative pressure (P
r
=
P
/
P
0) of 0.1 and 0.95, respectively, and the mesopore volume (V
meso) was calculated by subtracting the micropore volume from the total pore volume. The XRD patterns of the MnO2 were characterized by means of Rigaku DMAX-2000 diffractometer using a Cu Kα source. The electrochemical measurements were tested by three-electrode electrochemical cell on CHI660C Instrument.


### 2.4. Electrochemical Measurements

The MnO2 electrode was used as the working electrode, Pt plate as the counter, and a saturated calomel electrode (SCE) as the reference electrode. 0.5 M Na2SO4 solution was used as electrolyte. The electrodes were obtained by pressing electrode slurry formed by MnO2 (75 wt%), PVdF (5 wt%), and SuperP (20 wt%) on Ti mesh at the pressure of 10 MPa.The capacitance of the electrode material was determined by cyclic voltammetry between 0 and 0.9 V. The mass specific capacitance was calculated according to the following formula:(1)
C
=
Q
(
Δ
V
·
m
)
,where the charge (Q) is half of the integrated area of the CV curve and m and Δ
V refer to the mass of the electrode and the potential window, respectively.


## 2.1. Reagents and Solutions

Mn(NO3)2 solution (50 wt.%) was purchased from Shanghai Chemical Reagent Co. Ltd. and silica sol (20 wt.%) with average particle size of 10 nm was purchased from Shanghai Debang Company.


## 2.2. Materials Preparation

Silica sol was added to Mn(NO3)2 solution and mixed thoroughly. The mixture was condensed to form precursor after the evaporation of water. And the precursor was heated up to 300°C at a rate of 5°C/min and maintained for 2 h. The obtained products were first washed by 3 M KOH solution for 10 h and then by deionized water until pH reached 7. The mass of manganese source (Mn(NO3)2) solution was fixed at 20 g, whereas that of silica sol was 10, 20, 30, 40, 50, and 60 g, respectively. The MnO2 prepared by the decomposition of Mn(NO3)2 without template was designated as blank. And those synthesized with silica sol were designated as MMO-1, MMO-2, MMO-3, MMO-4, MMO-5, and MMO-6 accordingly.


## 2.3. Instrumentation

The pore characteristics of the mesoporous MnO2 were measured on a Micromeritics (ASAP 2010) instrument, using nitrogen at 77 K. Mesopore size distributions were determined by BJH method. The micropore volume (V
mic) and the total pore volume (V
t) were calculated from the amount of N2 adsorbed at a relative pressure (P
r
=
P
/
P
0) of 0.1 and 0.95, respectively, and the mesopore volume (V
meso) was calculated by subtracting the micropore volume from the total pore volume. The XRD patterns of the MnO2 were characterized by means of Rigaku DMAX-2000 diffractometer using a Cu Kα source. The electrochemical measurements were tested by three-electrode electrochemical cell on CHI660C Instrument.


## 2.4. Electrochemical Measurements

The MnO2 electrode was used as the working electrode, Pt plate as the counter, and a saturated calomel electrode (SCE) as the reference electrode. 0.5 M Na2SO4 solution was used as electrolyte. The electrodes were obtained by pressing electrode slurry formed by MnO2 (75 wt%), PVdF (5 wt%), and SuperP (20 wt%) on Ti mesh at the pressure of 10 MPa.The capacitance of the electrode material was determined by cyclic voltammetry between 0 and 0.9 V. The mass specific capacitance was calculated according to the following formula:(1)
C
=
Q
(
Δ
V
·
m
)
,where the charge (Q) is half of the integrated area of the CV curve and m and Δ
V refer to the mass of the electrode and the potential window, respectively.


## 3. Results and Discussion

### 3.1. XRD

Figure1 shows the XRD pattern of the sample of blank prepared by the decomposition of Mn(NO3)2 directly without the addition of silica sol template. The reflections of the sample are found to be sharp, indicating the good crystallinity of the sample. And the crystal form is confirmed to be β-MnO2 corresponding to JCPDS number 72-1984.Figure 1
XRD pattern of the sample of blank.Figure2 shows the XRD patterns of the samples of MMO-x (x = 1–6). The reflections of the samples are found to be consistent with those of the sample of blank, indicating the remains of the crystal structure of the samples. And the broader and weaker reflections of the samples suggest the decrease of the crystallinity of the samples.Figure 2
XRD patterns of the samples of MMO-x (x = 1–6).


### 3.2. Adsorption and Desorption Isotherms

Adsorption and desorption isotherms of the samples of blank and MMO-x (x = 1–6) are shown in Figure 3. We can see that there exist notable changes on the adsorption and desorption isotherms between the samples of blank and MMO-x (x = 1–6). The nitrogen uptake of the sample of blank was nearly zero, indicating the nonporous nature of this material. The isotherms of MMO-x (x = 1–6) belong to type IV according to the IUPAC classification. The hysteresis loop on the isotherms suggests the capillary condensation occurring in mesopores and the limiting uptake occurring at high relative pressure. And the volume adsorbed of N2 of mesoporous MnO2 increases with the increase of the mass ratio of silica sol to Mn(NO3)2.Figure 3
Adsorption and desorption isotherms of the samples of blank and MMO-x (x = 1–6). The isotherms of MMO-4, MMO-5, and MMO-6 were offset vertically by 25, 35, and 55 cm3 g−1 STP.The pore characteristics, namely, BET surface area, total pore volume, and mean pore size determined from the N2 adsorption and desorption isotherms are shown in Table 1. The BET surface area and total pore volume increases with the increase of the mass ratio of silica sol to manganese source. We can safely draw a conclusion that, in the silica sol/Mn(NO3)2 ratio studied, the porosity of the mesoporous MnO2 is improved greatly with the increase of silica sol/Mn(NO3)2 ratio, demonstrating that silica particle effectively functions as template and pore-generators.Table 1
Pore characteristics of the mesoporous MnO2.
Samples
S
BET (m2 g−1)
V
t
(cm3 g−1)
Mean pore size (nm)
Blank
0.55
—
—
MMO-1
22.65
0.0663
11.71
MMO-2
39.84
0.1168
11.73
MMO-3
63.86
0.1726
10.81
MMO-4
61.30
0.2062
13.46
MMO-5
81.81
0.2467
12.06
MMO-6
89.73
0.2655
11.83Figure4 shows the pore size distributions of the sample of blank and MMO-x (x = 1–6). The results show that the samples are mesoporous except the sample of blank, which is consistent with that of the result of adsorption and desorption isotherms. The predominant pore size of the samples is found to be in the range of 6~8 nm, suggesting some shrinkage for the mean 10 nm of the particle size of the silica particle used as template. Furthermore, the predominant pore size of the samples increases with the increase of the amount of silica sol added.Figure 4
Mesopore size distributions of the samples of blank and MMO-x (x = 1–6).


### 3.3. Electrochemical Measurements

Figure5 presents CVs of the samples of blank and MMO-x (x = 1–6) at the scan rate of 5 mV s−1. The steady-state voltammograms of all the samples exhibit a rectangular image with broad peaks observed, corresponding to a typical pseudocapacitive behavior where the current flow is independent of the electrode potential.Figure 5
CVs of the samples of blank and MMO-x (x = 1–6) at the scan rate of 5 mV/s.Figure6 illustrates the effect of scan rate on the cyclic voltammetry behavior of the sample of MMO-4 electrode in the 0.5 M Na2SO4 electrolyte. The rectangular shape of the voltammogram at lower scan rate suggests the ideal pseudocapacitive behavior of the electrode. However, at higher scan rate the voltammograms of the electrode deviate from this shape due to slow diffusion within the material particles [15].Figure 6
CVs of the sample of MMO-4 at different scan rates.Figure7 shows the influence of scan rate on the capacitance recorded with scan rates from 5 to 200 mV/s for the samples of blank and MMO-x (x = 1–6). The specific capacitances at the scan rate of 5 mV/s calculated from the CV curve of the sample of MMO-4 are the highest (163.2 F/g), in comparison with 19.3 F/g of that of the sample of blank, suggesting the important role of pore-forming using silica sol as template. As shown in the figure, the specific capacitances of the samples decrease as the scan rate increases. As the potential scan rate is raised to 200 mV/s, the specific capacitances of the sample of blank and MMO-4 are 12.2 F/g and 21.6 F/g, respectively. The great improvement of specific capacitance is probably due to the enlarged activated surface area after template is added.Figure 7
Specific capacitance of the samples of blank and MMO-x (x = 1–6) at different scan rates.The charge-discharge behavior of the sample of MMO-4 was examined by chronopotentiometry. Figure8 shows the charge/discharge behavior of the electrode of MMO-4. The linear and symmetric charge/discharge curves indicate good capacitive and revisable behavior.Figure 8
Charge-discharge curve of the sample of MMO-4 at the current density of 0.5 mA cm−2.


## 3.1. XRD

Figure1 shows the XRD pattern of the sample of blank prepared by the decomposition of Mn(NO3)2 directly without the addition of silica sol template. The reflections of the sample are found to be sharp, indicating the good crystallinity of the sample. And the crystal form is confirmed to be β-MnO2 corresponding to JCPDS number 72-1984.Figure 1
XRD pattern of the sample of blank.Figure2 shows the XRD patterns of the samples of MMO-x (x = 1–6). The reflections of the samples are found to be consistent with those of the sample of blank, indicating the remains of the crystal structure of the samples. And the broader and weaker reflections of the samples suggest the decrease of the crystallinity of the samples.Figure 2
XRD patterns of the samples of MMO-x (x = 1–6).


## 3.2. Adsorption and Desorption Isotherms

Adsorption and desorption isotherms of the samples of blank and MMO-x (x = 1–6) are shown in Figure 3. We can see that there exist notable changes on the adsorption and desorption isotherms between the samples of blank and MMO-x (x = 1–6). The nitrogen uptake of the sample of blank was nearly zero, indicating the nonporous nature of this material. The isotherms of MMO-x (x = 1–6) belong to type IV according to the IUPAC classification. The hysteresis loop on the isotherms suggests the capillary condensation occurring in mesopores and the limiting uptake occurring at high relative pressure. And the volume adsorbed of N2 of mesoporous MnO2 increases with the increase of the mass ratio of silica sol to Mn(NO3)2.Figure 3
Adsorption and desorption isotherms of the samples of blank and MMO-x (x = 1–6). The isotherms of MMO-4, MMO-5, and MMO-6 were offset vertically by 25, 35, and 55 cm3 g−1 STP.The pore characteristics, namely, BET surface area, total pore volume, and mean pore size determined from the N2 adsorption and desorption isotherms are shown in Table 1. The BET surface area and total pore volume increases with the increase of the mass ratio of silica sol to manganese source. We can safely draw a conclusion that, in the silica sol/Mn(NO3)2 ratio studied, the porosity of the mesoporous MnO2 is improved greatly with the increase of silica sol/Mn(NO3)2 ratio, demonstrating that silica particle effectively functions as template and pore-generators.Table 1
Pore characteristics of the mesoporous MnO2.
Samples
S
BET (m2 g−1)
V
t
(cm3 g−1)
Mean pore size (nm)
Blank
0.55
—
—
MMO-1
22.65
0.0663
11.71
MMO-2
39.84
0.1168
11.73
MMO-3
63.86
0.1726
10.81
MMO-4
61.30
0.2062
13.46
MMO-5
81.81
0.2467
12.06
MMO-6
89.73
0.2655
11.83Figure4 shows the pore size distributions of the sample of blank and MMO-x (x = 1–6). The results show that the samples are mesoporous except the sample of blank, which is consistent with that of the result of adsorption and desorption isotherms. The predominant pore size of the samples is found to be in the range of 6~8 nm, suggesting some shrinkage for the mean 10 nm of the particle size of the silica particle used as template. Furthermore, the predominant pore size of the samples increases with the increase of the amount of silica sol added.Figure 4
Mesopore size distributions of the samples of blank and MMO-x (x = 1–6).


## 3.3. Electrochemical Measurements

Figure5 presents CVs of the samples of blank and MMO-x (x = 1–6) at the scan rate of 5 mV s−1. The steady-state voltammograms of all the samples exhibit a rectangular image with broad peaks observed, corresponding to a typical pseudocapacitive behavior where the current flow is independent of the electrode potential.Figure 5
CVs of the samples of blank and MMO-x (x = 1–6) at the scan rate of 5 mV/s.Figure6 illustrates the effect of scan rate on the cyclic voltammetry behavior of the sample of MMO-4 electrode in the 0.5 M Na2SO4 electrolyte. The rectangular shape of the voltammogram at lower scan rate suggests the ideal pseudocapacitive behavior of the electrode. However, at higher scan rate the voltammograms of the electrode deviate from this shape due to slow diffusion within the material particles [15].Figure 6
CVs of the sample of MMO-4 at different scan rates.Figure7 shows the influence of scan rate on the capacitance recorded with scan rates from 5 to 200 mV/s for the samples of blank and MMO-x (x = 1–6). The specific capacitances at the scan rate of 5 mV/s calculated from the CV curve of the sample of MMO-4 are the highest (163.2 F/g), in comparison with 19.3 F/g of that of the sample of blank, suggesting the important role of pore-forming using silica sol as template. As shown in the figure, the specific capacitances of the samples decrease as the scan rate increases. As the potential scan rate is raised to 200 mV/s, the specific capacitances of the sample of blank and MMO-4 are 12.2 F/g and 21.6 F/g, respectively. The great improvement of specific capacitance is probably due to the enlarged activated surface area after template is added.Figure 7
Specific capacitance of the samples of blank and MMO-x (x = 1–6) at different scan rates.The charge-discharge behavior of the sample of MMO-4 was examined by chronopotentiometry. Figure8 shows the charge/discharge behavior of the electrode of MMO-4. The linear and symmetric charge/discharge curves indicate good capacitive and revisable behavior.Figure 8
Charge-discharge curve of the sample of MMO-4 at the current density of 0.5 mA cm−2.


## 4. Conclusions

A series of mesoporous MnO2 with different surface areas (from 22.65 to 89.73 m2/g) have been synthesized by silica sol template method by utilizing silica sol as template and Mn(NO3)2 as manganese source. The results of XRD characterization show that the crystal type of the samples of blank and MMO-x (x = 1–6) is confirmed to be β-MnO2 and crystallinity of MMO-x (x = 1–6) decreases due to the formation of mesopore. It is found that the BET surface area and total pore volume increase with the increase of the mass ratio of silica sol to manganese source. And silica particle effectively functions as template and pore-generators.The results of electrochemical performance show that the specific capacitances of the sample of MMO-4 at the scan rate of 5 mV/s are the highest (163.2 F/g), in comparison with 19.3 F/g of that of the sample of blank, suggesting the important role of pore-forming using silica sol as template. As the potential scan rate is raised to 200 mV/s, the specific capacitances of the sample of blank and MMO-4 are 12.2 F/g and 21.6 F/g, respectively. The great improvement of specific capacitance is probably due to the enlarged activated surface area after template is added.



---

*Source: 768023-2015-01-27.xml*