# Fracture of Parallel Strand Bamboo Composite under Mode I Loading: DCB Test Investigation

Authors: Yurong Shen; Dongsheng Huang; Ying Hei Chui; Chunping Dai
Journal: Advances in Materials Science and Engineering
 (2019)

---

## Abstract

This paper describes the experimental studies on Mode I fracture of parallel strand bamboo (PSB) by the double cantilever beam (DCB) test. R-curves based on the elementary beam theory and specimen compliance are proposed in order to overcome the difficulties to monitor the crack propagation during experiments. The results demonstrate that the energy release rate (ERR) is influenced by the specimen geometry, i.e., the specimen width and initial crack length. The ERR at the plateau level is similar for the range of the analyzed widths (B = 20, 40, and 60 mm), while it decreases with width increasing up to 80 mm and 100 mm. The energy release rate for PSB specimens would verge to a stable value with the width increasing up to a specific value, while the value of the energy release rate will be influenced by the initial crack length. Consequently, the DCB tests also show that the obtained R-curve in this study is not a material property.


---

## Body

## 1. Introduction

Parallel strand bamboo (PSB) is manufactured by parallelly gluing bamboo strands together under controlled temperature and pressure. Because bamboo strips are parallelly glued along the longitudinal direction and uniformly distributed over the transverse direction, PSB can be considered as a unidirectional and orthotropic fibrous composite, as shown in Figure1 [1]. More recently, PSB wins growing interests as an alternative of wood composites for construction engineering in China due to its fast-growing feature and excellent structural performance. Aimed at the structural use, the failure modes of combined compression and bending PSB members were studied by Huang et al. [2–4]. It was found that the fracture along the fiber interfaces was one of the major failure modes of PSB composites. Once a PSB member subjected to an increasing external load, the initial deflects, such as microvoids and microcracks, could be advancing or growing into macrocracks and consequently result in catastrophic failure of structures. Therefore, the fracture of PSB composite is one of the major concerns in PSB structural design.Figure 1
(a) Photograph of PSB. (b) Principal directions of PSB.
(a)
(b)The objective of the present study is to investigate the Mode I fracture properties and to measure the fracture toughness of the PSB composite through DCB experiments, which is one of the necessities for establishing design allowable values used in damage tolerance analysis of PSB structures.The double cantilever beam (DCB) test [5–7], a standard test procedure prescribed in ASTM D5528-13 [8], was employed as the test procedure in this study. The test uses a rectangular specimen with different widths, different initial crack lengths, and constant thickness. It contains a preimplanted, nonadhesive insert or crack as an initial delamination. The opening load is applied perpendicular to the initial crack surface to induce the Mode I crack. Such a test analysis is based on the beam theory, and the fracture toughness can be measured through the energy release rate (ERR) for orthotropic fibrous composites. The ERR can be obtained by various methods, including direct area integration of loading-unloading curves or by means of compliance measurements [9]. Since the data reduction of DCB test is easier than the other test approaches [10, 11], it is now the most popular method used to determine Mode I fracture toughness.Recommended by ASTM and ISO standards [9, 12, 13], the energy release rate can be estimated through the change of compliance. Theoretically, it can be obtained by differentiating the specimen compliance, C, with respect to the crack length a, i.e., G=P2/2B∂C/∂a [14–18], where P is the applied load and B the width of the specimen. In the frame of linear fracture mechanics, the root condition is supposed to be fully built-in; hence, the compliance equation can be given by simple beam theory, i.e., C=8a3/BEh3 [9]. Nevertheless, because of the fuzzy boundary conditions at the end of opening arms, the compliance equation C(a) cannot be determined without controversy. On the other hand, the crack length cannot be measured either with desired precision. Therefore, various data reduction methods were developed to overcome this disadvantage, such as the area method, in which the compliance equation was built through data fitting for tests [19, 20]. Hashemi et al. [21] compared the different data reduction methods for obtaining the energy release rate of fibrous composites. They proposed that the correction of crack length was necessary in the beam theory-based method because the end of opening arms was not perfectly clamped. They developed the corrected beam theory (CBT), providing a correction in the crack length based on a compliance calibration. However, the fracture mechanism of fibrous composite is much complicated than that of brittle materials. The major aspect is that the microvoids coalescing, fine cracks extending, and fiber bridging lead to a large fracture process zone (FPZ) in front of the crack tip, which makes the clear location of the crack tip impracticable [22–25]. Furthermore, the development of the large FPZ in the crack-tip front delays the fracture of specimen, which consequently makes the built-in assumption no longer valid. It has been well recognized that the use of elementary beam theory with the built-in assumption at the crack tip has a significant error for calculating the energy release rate of fibrous composites [26]. To date, there is no method available to exactly identify the crack tip for the DCB test of fibrous composites. For this reason, extensive researches have been carried out to avoid locating the crack tip [27–32]. Among these researches, the concept of equivalent linear elastic fracture mechanics (LEFM) was widely accepted to deal with the fracture with a large FPZ [31]. According to the concept of equivalent LEFM, the increasing of compliance, owing to the development of FPZ or main crack propagation with FPZ, is attributed to the elastic crack which equals to the actual crack with its FPZ [33]. Therefore, the crack length can be estimated according to the associated compliance obtained by experiments. Furthermore, the R-curve can also be measured using only a monotonic load-displacement record.In the present study, the data reduction method was based on the theory of equivalent LEFM. Compliance calibration was introduced to determine the crack length. The direct integral approach was adopted to calculate the energy release rate.


## 2. Data Reduction Scheme

Figure2 illustrates the principle of evaluating energy release rate based on the theory of equivalent LEFM. In the schematic load-displacement curve F,δ, two consecutive points M1δa1,Fa1 and M2δa2,Fa2 corresponding to two different crack lengths a1 and a2, respectively, are selected. Suppose that the crack extends from length a1 to a2 with a small amount of propagation increment Δa and that the load-displacement trajectory goes from M1 to M2; thus, the shadow area circulated by the dashed lines OM1, and OM2 and the segment of load-displacement M1M2 must be equal to the energy released as the crack growth of the extension Δa [19]. Therefore, the energy release rate can be calculated by(1)GR=1bΔa12Pa1δa2−12Pa2δa1,where P and δ stand for the applied load and associated displacement at loading position, respectively. The crack length aii=1,2 can be determined from the test compliance Cai=δai/Pai. According to the beam theory, the compliance can be calculated by [34](2)Ca=a3ELI+6a5GLTA,where EL is the longitudinal elastic modulus, GLT is the shear modulus in LT plane, i.e., the 12 or 13 plane as shown in Figure 1(b), I is the inertia moment of the cross section, and A is the area of cross section. Once the compliance Caiis obtained by experiment and the crack length can be determined by resolving equation (2) or by numerical iteration in terms of the following equation:(3)ai=3ELIλCai21+3ELh2/10GLTai−121/3,where λ=C¯0/C0 is the calibration parameter to eliminate the system error of the experiment, in which C0 is the test compliance corresponding to the initial crack length a0 and C¯0 stands for the theoretical compliance corresponding to the initial crack length calculated by equation (2).Figure 2
Schematic diagram of the evaluation of the resistance to crack growth (GR).


## 3. Experimental Investigation

### 3.1. Materials

The test PSB was provided by Feiyu Bamboo Products, Jianghxi, China. The material density was 1.26 g/cm3, and the moisture content was 11%. Mechanical properties in parallel-to-grain direction, which are involved in test analysis, were pretested following the method recommended in ASTM D143-14 [35], and the results are collected in Table 1, where the subscripts L and T are the parallel-to-grain direction and perpendicular-to-grain direction, respectively, and υ represents Poisson’s ratio of PSB.Table 1
Mechanical properties of PSB composites in parallel-to-grain direction.
Items
E
L (MPa)
G
LT (MPa)
υ
LT
υ
TL
Mean
15363
4890
0.32
0.05
CV (%)
9.575
12.31
12.3
25.6


### 3.2. Specimen Preparation

The geometry of DCB specimen is shown in Figure3. The dimensions of DCB specimen were determined referring to the standard test procedure addressed in ASTM D5528-13 [8]. In this method, the DCB dimension was designed to ensure the damage zone or nonlinear deformation developed along the delamination front and the stable crack growth can be achieved.Figure 3
The configurations of DCB specimens.Totally four groups of specimens with different initial crack lengths and different widths were prepared, as illustrated in Table2, in which each group consists of the same initial crack length and 5 types of specimens with different widths. A label system was designed to identify the specimen. In this system, the latter A, B, C, and D correspond to the initial crack length of 34 mm, 67 mm, 100 mm, and 134 mm, respectively. The number prior to the letter of the group name stands for the width of the specimen, as shown in Table 2. The initial crack was firstly introduced by a 1.5 mm thick saw kerf; afterwards, precrack with length about 1 mm was extended by using a cutting blade [10]. At the end of the DCB test, two bolt holes of 8 mm in diameter were drilled for the sake of joining DCB specimen to the actuator of the test machine, as illustrated in Figure 3.Table 2
Dimensions of DCB specimens.
Group
Label
a
0 (mm)
L (mm)
B (mm)
H (mm)
a
0 (L)
Number
A
20-A
34
350
20
50
0.097
3
40-A
40
60-A
60
80-A
80
100-A
100
B
20-B
67
350
20
50
0.191
3
40-B
40
60-B
60
80-B
80
100-B
100
C
20-C
100
350
20
50
0.286
3
40-C
40
60-C
60
80-C
80
100-C
100
D
20-D
134
350
20
50
0.383
3
40-D
40
60-D
60
80-D
80
100-D
100


### 3.3. Test Procedure

The fracture tests were performed on a servo-hydraulic universal test machine of 20 kN capacity in room ambient circumstance. The test setup is illustrated in Figure4(a). The specimen was joined to the load actuator through two steel rods of 7.5 mm diameter, as shown in Figure 4(b). Loading was controlled by the displacement of a moveable actuator at the speed of 1.0 mm/min. A microscope digital camera was mounted in front of the specimen to monitor the crack propagation and take the images of the crack tip. The applied load and the displacement at loading position were simultaneously recorded at a frequency of 10 Hz. The opening displacement at the initial crack tip was measured by using a clip-on gauge (COD gauge) symmetrically fixed at the two sides of the crack tip through embedded aluminum flakes (Figure 4(b)). The crack length during propagation can be observed by using the microscopic camera, as shown in Figure 4(b).Figure 4
(a) Experimental setup of the DCB test. (b) Schematic diagram of the DCB test.
(a)
(b)


## 3.1. Materials

The test PSB was provided by Feiyu Bamboo Products, Jianghxi, China. The material density was 1.26 g/cm3, and the moisture content was 11%. Mechanical properties in parallel-to-grain direction, which are involved in test analysis, were pretested following the method recommended in ASTM D143-14 [35], and the results are collected in Table 1, where the subscripts L and T are the parallel-to-grain direction and perpendicular-to-grain direction, respectively, and υ represents Poisson’s ratio of PSB.Table 1
Mechanical properties of PSB composites in parallel-to-grain direction.
Items
E
L (MPa)
G
LT (MPa)
υ
LT
υ
TL
Mean
15363
4890
0.32
0.05
CV (%)
9.575
12.31
12.3
25.6


## 3.2. Specimen Preparation

The geometry of DCB specimen is shown in Figure3. The dimensions of DCB specimen were determined referring to the standard test procedure addressed in ASTM D5528-13 [8]. In this method, the DCB dimension was designed to ensure the damage zone or nonlinear deformation developed along the delamination front and the stable crack growth can be achieved.Figure 3
The configurations of DCB specimens.Totally four groups of specimens with different initial crack lengths and different widths were prepared, as illustrated in Table2, in which each group consists of the same initial crack length and 5 types of specimens with different widths. A label system was designed to identify the specimen. In this system, the latter A, B, C, and D correspond to the initial crack length of 34 mm, 67 mm, 100 mm, and 134 mm, respectively. The number prior to the letter of the group name stands for the width of the specimen, as shown in Table 2. The initial crack was firstly introduced by a 1.5 mm thick saw kerf; afterwards, precrack with length about 1 mm was extended by using a cutting blade [10]. At the end of the DCB test, two bolt holes of 8 mm in diameter were drilled for the sake of joining DCB specimen to the actuator of the test machine, as illustrated in Figure 3.Table 2
Dimensions of DCB specimens.
Group
Label
a
0 (mm)
L (mm)
B (mm)
H (mm)
a
0 (L)
Number
A
20-A
34
350
20
50
0.097
3
40-A
40
60-A
60
80-A
80
100-A
100
B
20-B
67
350
20
50
0.191
3
40-B
40
60-B
60
80-B
80
100-B
100
C
20-C
100
350
20
50
0.286
3
40-C
40
60-C
60
80-C
80
100-C
100
D
20-D
134
350
20
50
0.383
3
40-D
40
60-D
60
80-D
80
100-D
100


## 3.3. Test Procedure

The fracture tests were performed on a servo-hydraulic universal test machine of 20 kN capacity in room ambient circumstance. The test setup is illustrated in Figure4(a). The specimen was joined to the load actuator through two steel rods of 7.5 mm diameter, as shown in Figure 4(b). Loading was controlled by the displacement of a moveable actuator at the speed of 1.0 mm/min. A microscope digital camera was mounted in front of the specimen to monitor the crack propagation and take the images of the crack tip. The applied load and the displacement at loading position were simultaneously recorded at a frequency of 10 Hz. The opening displacement at the initial crack tip was measured by using a clip-on gauge (COD gauge) symmetrically fixed at the two sides of the crack tip through embedded aluminum flakes (Figure 4(b)). The crack length during propagation can be observed by using the microscopic camera, as shown in Figure 4(b).Figure 4
(a) Experimental setup of the DCB test. (b) Schematic diagram of the DCB test.
(a)
(b)


## 4. Test Results

### 4.1. Load-Displacement Curve

Figure5 illustrates a typical load-displacement curve. Roughly three stages can be observed. The first one (stage I) is no-damage stage from origin to the proportional limit point where the curve deviates from its original direction. The load-displacement curve exhibits perfect linearity in this stage. Once the load exceeds the point of proportional limit (stage II), damage onset extends and coalesces to form the fracture process zone (FPZ) and consequently leads to the compliance augment and the curve continuously deviates from its original direction as the load increases. Hence, this stage can be understood as the stage of FPZ development. When the FPZ fully developed, the load-displacement curve would reach its critical point, where the load reached its maximum value and the crack propagation began. Hence, the third stage (stage III) is the crack propagation stage.Figure 5
A typical load-displacement curve.Figure6 presents the load-displacement profiles of the specimens. For the specimens of Group A, the load-displacement curve sharply declines once the load reaches the maximum value, which indicates that the crack propagation is unstable. For the specimens in Groups B, C, and D with longer initial crack length, the load-displacement profile slowly declines in post-summit segments. Furthermore, the load-displacement profile declined more slowly with longer initial crack length, which indicated that the stability of crack propagation is sensitive to the initial crack length. Therefore, enough initial crack length is needed for obtaining stable crack propagation. In the present study, the ratios of initial crack length to ligament length of Groups B, C, and D are 0.191, 0.286, and 0.383, respectively, and their crack propagates in a stable and ductile manner, which means specimens with the ratio of Groups B, C, and D can be used to determine the fracture properties.Figure 6
Load-displacement curves of all tested DCB specimens with different initial crack lengths in the same width: (a) widthB = 20 mm; (b) width B = 40 mm; (c) width B = 80 mm; and (d) width B = 100 mm.
(a)
(b)
(c)
(d)The second factor is the width scaling which has a significant influence on fiber bridging in the wake of the crack, consequently affecting the delamination behavior. As shown in Figure7, the load-displacement curves for partial specimens are presented with the same initial crack length but different widths. It can be concluded that the crack grows in a “thumbnail” shape [36] under constant or decreasing load, while the overall displacement is increased. The “thumbnail” theory means that the crack extends mainly from the center of the thickness of specimens, while the edge regions are plastically deformed. Therefore, with the width increasing, the energy release rate of DCB specimens for PSB composite would converge to a stable value.Figure 7
Load-displacement curves of DCB specimens with different widths in the same initial crack length: (a) initial crack lengtha0 = 100 mm; (b) initial crack length a0 = 134 mm.
(a)
(b)It is worth mentioning that only partial specimens exhibit their load-displacement curves or R-curves in later analysis due to the similar tendency of these curves. Moreover, because of the manufacturing defects for some PSB specimens, the data cannot be used to analyze the energy release rate in the DCB test. Therefore, some specimens present two lines in partial load-displacement curves or R-curves.


### 4.2. Fracture Process Zone

Damage begins when the external load exceeds its proportional limit, which is characterized by local microcracks at the crack tip front zone. This damaged zone is comprised of microcracks between the grains or through the grains. The microcracks are consequently extended and coalesced to form macrocracks and local microcracks at the advancing crack tip front as the external load increases. This fracture process and damaged zone can be called fracture process zone (FPZ). Before the load reaches its maximum value, the crack interfaces are bonded by fiber bridges which either rupture or peel off from the crack surfaces. This fracture mechanism leads to a large FPZ which can be observed at the crack tip front before crack propagation, as shown in Figure8. Due to the restriction of fiber bridges, the strain energy is smoothly consumed through the fibrous rupture or pull-off, which leads to stable crack propagation and a rising R-curve.Figure 8
The fiber bridging phenomenon of DCB specimens.Several micrographs were taken from the tested specimens at the fracture surfaces using the scanning electron microscope (SEM), as shown in Figure9. Figure 9(a) exhibits the typical fracture surface with a limited amount of fiber pull-out in the debonding plies, which is presented with higher magnitude in Figure 9(b). The pull-out process could have created a fibre-bridged zone in the wake of the advancing crack tip. During the whole experiment, the growth and eventual stabilization of this fibre-bridged zone could account for the tendency observed in later R-curves.Figure 9
(a) SEM micrograph of the DCB specimens’ fracture surface for PSB composite. (b) Fiber pull-out with higher magnitude.


### 4.3. R-Curve Measurement

Energy release rate for each test specimen was measured by the method addressed in Section2. The R-curves of partial DCB specimens with different widths and different initial crack lengths corresponding to specific thickness are presented in Figures 10 and 11. It was observed that the energy release rate increases up to a steady-state toughness after the initiation of delamination. As illustrated in Section 4.2, the fiber bridging effect during the whole crack propagation led to eventual stabilization of crack growths for all tested specimens. Meanwhile, the results also implied that the R-curve obtained in this study was not a material property, i.e., it depended on specimen geometry. Consequently, when the crack starts to propagate, the bridging zone is created. By developing the bridging zone length, the strain energy release rate increases up to the steady-state fracture toughness. The length between the initial crack length and crack length corresponding to the steady-state fracture toughness is called as the steady-state bridging zone length. From Figure 10, the value of the energy release rate was always affected by the initial crack length. The major reason may be that the steady-state bridging zone of PSB specimens was always influenced by the preimbedded crack.Figure 10
R-curves of DCB specimens with different initial crack lengths on the same width: (a) widthB = 20 mm; (b) width B = 40 mm.
(a)
(b)Figure 11
R-curves of DCB specimens with different widths in the same initial crack lengths. (a) Initial crack lengtha0 = 100 mm. (b) Initial crack length a0 = 134 mm.
(a)
(b)From Figure11, it can also be concluded that the energy release rate of DCB specimens for the PSB composite would verge to a stable value with the width increasing up to a specific value, which will be identified in the future DCB tests for PSB specimens. As illustrated in the abovementioned “thumbnail” theory, the width scaling has a significant effect on fiber bridging in the wake of the crack, which make the crack grow in a “thumbnail” shape, i.e., the crack extends mainly from the center of specimens, while the edge regions are plastically deformed. Therefore, the energy release rate of DCB specimens for the PSB composite would converge to a stable value with the increasing width. Table 3 gives the average fracture toughness for partial test samples.Table 3
The average fracture toughness for partial test samples (H = 50 mm).
Specimens
a
0 (mm)
B (mm)
L (mm)
P (N)
G
R (J/m2)
DCB-C
100
20
350
839
1740
40
1535
1505
60
2364
1550
80
2149
630
100
2952
820
DCB-D
134
20
350
745
2600
40
1332
2570
60
2081
1960
80
2009
950
100
2233
870


## 4.1. Load-Displacement Curve

Figure5 illustrates a typical load-displacement curve. Roughly three stages can be observed. The first one (stage I) is no-damage stage from origin to the proportional limit point where the curve deviates from its original direction. The load-displacement curve exhibits perfect linearity in this stage. Once the load exceeds the point of proportional limit (stage II), damage onset extends and coalesces to form the fracture process zone (FPZ) and consequently leads to the compliance augment and the curve continuously deviates from its original direction as the load increases. Hence, this stage can be understood as the stage of FPZ development. When the FPZ fully developed, the load-displacement curve would reach its critical point, where the load reached its maximum value and the crack propagation began. Hence, the third stage (stage III) is the crack propagation stage.Figure 5
A typical load-displacement curve.Figure6 presents the load-displacement profiles of the specimens. For the specimens of Group A, the load-displacement curve sharply declines once the load reaches the maximum value, which indicates that the crack propagation is unstable. For the specimens in Groups B, C, and D with longer initial crack length, the load-displacement profile slowly declines in post-summit segments. Furthermore, the load-displacement profile declined more slowly with longer initial crack length, which indicated that the stability of crack propagation is sensitive to the initial crack length. Therefore, enough initial crack length is needed for obtaining stable crack propagation. In the present study, the ratios of initial crack length to ligament length of Groups B, C, and D are 0.191, 0.286, and 0.383, respectively, and their crack propagates in a stable and ductile manner, which means specimens with the ratio of Groups B, C, and D can be used to determine the fracture properties.Figure 6
Load-displacement curves of all tested DCB specimens with different initial crack lengths in the same width: (a) widthB = 20 mm; (b) width B = 40 mm; (c) width B = 80 mm; and (d) width B = 100 mm.
(a)
(b)
(c)
(d)The second factor is the width scaling which has a significant influence on fiber bridging in the wake of the crack, consequently affecting the delamination behavior. As shown in Figure7, the load-displacement curves for partial specimens are presented with the same initial crack length but different widths. It can be concluded that the crack grows in a “thumbnail” shape [36] under constant or decreasing load, while the overall displacement is increased. The “thumbnail” theory means that the crack extends mainly from the center of the thickness of specimens, while the edge regions are plastically deformed. Therefore, with the width increasing, the energy release rate of DCB specimens for PSB composite would converge to a stable value.Figure 7
Load-displacement curves of DCB specimens with different widths in the same initial crack length: (a) initial crack lengtha0 = 100 mm; (b) initial crack length a0 = 134 mm.
(a)
(b)It is worth mentioning that only partial specimens exhibit their load-displacement curves or R-curves in later analysis due to the similar tendency of these curves. Moreover, because of the manufacturing defects for some PSB specimens, the data cannot be used to analyze the energy release rate in the DCB test. Therefore, some specimens present two lines in partial load-displacement curves or R-curves.


## 4.2. Fracture Process Zone

Damage begins when the external load exceeds its proportional limit, which is characterized by local microcracks at the crack tip front zone. This damaged zone is comprised of microcracks between the grains or through the grains. The microcracks are consequently extended and coalesced to form macrocracks and local microcracks at the advancing crack tip front as the external load increases. This fracture process and damaged zone can be called fracture process zone (FPZ). Before the load reaches its maximum value, the crack interfaces are bonded by fiber bridges which either rupture or peel off from the crack surfaces. This fracture mechanism leads to a large FPZ which can be observed at the crack tip front before crack propagation, as shown in Figure8. Due to the restriction of fiber bridges, the strain energy is smoothly consumed through the fibrous rupture or pull-off, which leads to stable crack propagation and a rising R-curve.Figure 8
The fiber bridging phenomenon of DCB specimens.Several micrographs were taken from the tested specimens at the fracture surfaces using the scanning electron microscope (SEM), as shown in Figure9. Figure 9(a) exhibits the typical fracture surface with a limited amount of fiber pull-out in the debonding plies, which is presented with higher magnitude in Figure 9(b). The pull-out process could have created a fibre-bridged zone in the wake of the advancing crack tip. During the whole experiment, the growth and eventual stabilization of this fibre-bridged zone could account for the tendency observed in later R-curves.Figure 9
(a) SEM micrograph of the DCB specimens’ fracture surface for PSB composite. (b) Fiber pull-out with higher magnitude.


## 4.3. R-Curve Measurement

Energy release rate for each test specimen was measured by the method addressed in Section2. The R-curves of partial DCB specimens with different widths and different initial crack lengths corresponding to specific thickness are presented in Figures 10 and 11. It was observed that the energy release rate increases up to a steady-state toughness after the initiation of delamination. As illustrated in Section 4.2, the fiber bridging effect during the whole crack propagation led to eventual stabilization of crack growths for all tested specimens. Meanwhile, the results also implied that the R-curve obtained in this study was not a material property, i.e., it depended on specimen geometry. Consequently, when the crack starts to propagate, the bridging zone is created. By developing the bridging zone length, the strain energy release rate increases up to the steady-state fracture toughness. The length between the initial crack length and crack length corresponding to the steady-state fracture toughness is called as the steady-state bridging zone length. From Figure 10, the value of the energy release rate was always affected by the initial crack length. The major reason may be that the steady-state bridging zone of PSB specimens was always influenced by the preimbedded crack.Figure 10
R-curves of DCB specimens with different initial crack lengths on the same width: (a) widthB = 20 mm; (b) width B = 40 mm.
(a)
(b)Figure 11
R-curves of DCB specimens with different widths in the same initial crack lengths. (a) Initial crack lengtha0 = 100 mm. (b) Initial crack length a0 = 134 mm.
(a)
(b)From Figure11, it can also be concluded that the energy release rate of DCB specimens for the PSB composite would verge to a stable value with the width increasing up to a specific value, which will be identified in the future DCB tests for PSB specimens. As illustrated in the abovementioned “thumbnail” theory, the width scaling has a significant effect on fiber bridging in the wake of the crack, which make the crack grow in a “thumbnail” shape, i.e., the crack extends mainly from the center of specimens, while the edge regions are plastically deformed. Therefore, the energy release rate of DCB specimens for the PSB composite would converge to a stable value with the increasing width. Table 3 gives the average fracture toughness for partial test samples.Table 3
The average fracture toughness for partial test samples (H = 50 mm).
Specimens
a
0 (mm)
B (mm)
L (mm)
P (N)
G
R (J/m2)
DCB-C
100
20
350
839
1740
40
1535
1505
60
2364
1550
80
2149
630
100
2952
820
DCB-D
134
20
350
745
2600
40
1332
2570
60
2081
1960
80
2009
950
100
2233
870


## 5. Conclusion

This paper has investigated an experimental procedure to obtain the energy release rate (ERR) using DCB tests for parallel strand bamboo (PSB) composites. The effects of specimen width and initial crack length on large-scale fiber bridging in Mode I fracture of unidirectional PSB composites were investigated. The R-curve measurements, for the range of the analyzed widths (B = 20, 40, 60, 80, and 100 mm) and initial crack lengths (a0 = 34, 67, 100, and 134 mm), show that the energy release rate is influenced by both the width and initial crack length of specimens, in that the ERR at the plateau level decreased with an increasing width and initial crack length. Consequently, the DCB tests imply that the R-curve obtained in the present study is not a material property because it depends on the specimen geometry. However, the ERR at the plateau level is decreased to similar values as the width increases up to 80 mm and 100 mm. It may be concluded that the energy release rate would verge to a stable value with the width increasing up to more than a specific value, which can be clarified in the future DCB tests for PSB composites.



---