# Experimental Study of Laser Cladding Methods on  Water Erosion Resistance to Low Pressure Blades Materials of  Steam Turbine

Authors: Di Zhang; Pengfei Zhao; Wei Zhao; Yaoyuan Luo; Yonghui Xie
Journal: Advances in Condensed Matter Physics
 (2014)

---

## Abstract

An experimental apparatus was built to study the effects of liquid-solid impact on laser cladding processing specimens of 17-4PH stainless steel material in the present investigation. Then the result of specimens without laser surface process was compared. The impact effect on the specimens was observed using the three-dimensional digital microscope. The depth of laser cladding and substrate material caused by liquid droplet impact was studied in detail and measured. The accuracy and reliability of the experimental system and computing methods were also verified. The depth of the impact area of laser cladding specimens was distributed in the range of 0.5–1.5μm while the 17-4PH group was distributed in the range of 2.5–3.5 μm. In contrast with specimens without laser surface processing, the material processed by laser cladding has significantly higher resistance to water erosion.


---

## Body

## 1. Introduction

In the condensing steam turbines of nuclear power plants and thermal power units, wet steam flow causes the erosion of the last stage blades and may cause considerable damage to the turbine. The reliability of turbines decreases over time and makes their lifetime shorter because of water erosion [1–3]. A number of experimental and theoretical investigations have been carried out to find a solution for controlling and curbing the bad effects of erosion. The antierosion measures can be divided into passive and objective methods. Varieties of dehumidification equipment have been adopted such as stator blade suction devices and humidity-removing stages to reduce the amount of droplets actively. Passive methods mainly include choosing the erosion resistance materials, strengthening the bucket exit edge, and using the protective coating to ensure the blades against eroding by water during normal working life, even after long-term water erosion from harming blade. Passive protection is the main method currently used by the world’s major companies [4–8].17-4PH material has been widely used in the manufacture of LP (low pressure) blades of steam turbine. And laser hardening of the last stage blades of steam turbine has been carried out to reduce the water erosion. As a passive protection technology, laser cladding surface treatment method is a relatively new technology [9–11]. In this paper, the dynamic stress response of laser cladding and ordinary 17-4PH specimens impacted by liquid droplet were investigated. The depth of pits caused by liquid droplet impact was measured, and the dimensions of damage area were recorded and analyzed statistically. It will provide the basis reference about surface treatment processing of last stage blades of steam turbine.


## 2. Experimental Test System

In this test system, a high speed impactor was developed. High pressure gas was employed to push piston and projectile supplied by detonating explosive in Type NS-603 Nail Ejector. Then a nylon rod is accelerated by the piston. The process of high speed impact between nylon rod and nylon plug results in high speed water droplets. The shape and location of water were obtained via high speed camera MEMRECAM FX-K3 with the speed of 104 frames/s.According to the droplets velocity calibration, the speed of droplets produced by the test system can reach up to 600 m/s or more. The dimension of explosive chamber varies with piston positions to obtain different velocity. Figures1 and 2 show the photo and the schematic diagram of the test system. Figure 3 is the specimen holder.Figure 1
Schematic diagram of the test system.Figure 2
The photo of the experimental setup.Figure 3
Specimen holder.During the test, the nylon rod was placed in the barrel, and the nylon plug was inserted in the nozzle inlet section. To ensure the sealing of the nozzle chamber, the nylon plug shall be applied with a certain number of Vaseline. The water was injected via a microsyringe from another side of the nozzle. Then the specimen was installed to the striking position together with the fixture. The ejector and its carriage were then fixed on the test bench by two bolts on both sides of the nail. The last step of the preparation work was covering the impact area with a bulletproof shield. After impact, the specimen should be cleaned and preserved before further analysis.In this paper, the base material of laser cladding is 17-4PH stainless steel, whose parameters are listed in Table1.Table 1
Material parameters of solid.
Material parameter
Value
Mass density
7820 kg/m3
Tensile strength
1000 MPa
Poisson’s ratio
0.272
Yield strength
945 MPa
Tangent modulus
7.74 GPaThe material samples were processed into cuboids with the dimension of 35 mm × 15 mm × 5 mm. Since the surface treatment layer on the specimen is relatively thin, only a slight degree of surface polishing has been carried out. Then the specimens with the cotton ball dipped in ethanol were cleaned before and after the impact test. Figure4 shows the specimens before the test. During the test, they were installed on the special fixture which fixed vertically 10 mm away from the nozzle.Figure 4
Photo of the specimens.


## 3. Method of Calculating Droplets Velocity

The MEMRECAM FX K3 high speed camera was used to capture the motion state of the droplets. The boundary of droplets captured by the camera is not very clear. However, knowing the position of jet frontier in two pictures is the only way to obtain the droplets velocity. So it is necessary to process the high speed photographs.Firstly, the background of two adjacent pictures is almost the same. The only difference is the shape and the position of the jet.On test data with 104 frames, the resolving power of the instrument is640×96. For each processed picture, the obtained RGB image is actually a M×N×3 matrix. Each point (x,y) in the two-dimensional picture and its color can be expressed as a color vector composed of RGB components:
(1)C(x,y)=(r,g,b).
From the difference between the pixels coding of the binary image of the block of present frame and that of previous frame, the following can be obtained:
(2)ΔC(x,y)={C(x,y)(n+1)-C(x,y)(n),C(x,y)(n+1)-C(x,y)(n)>0,0,C(x,y)(n+1)-C(x,y)(n)≤0.
Thus an image formed by color difference of the two pictures emerges. Figure 6 shows the two pictures taken at intervals of 10-4 s.This paper performed image sharpening to the differential chart. Figure6 is the difference between Figures 5(a) and 5(b) after 30 times sharpening. It is clear that a region emerges where white color centered.Two pictures taken at intervals of10-4 s.
(a)
(b)Figure 6
30 times sharpening of the differential chart.To get the velocity, the picture at next frame of Figure5(b) should be introduced, which is shown in Figure 7(b). For better comparison, frame of Figure 5(b) is also shown in Figure 7, that is, Figure 7(a).Two pictures taken at intervals of10-4 s.
(a)
(b)In order to reduce the noise signal, a figure of the difference of their absolute values is obtained by using the following methods:(3)|Δ|C(x,y)=|C(x,y)(n+1)-C(x,y)(n)|.
A vector R(x,y) generated by the subtraction of ΔC(x,y) and |Δ|C(x,y) will reduce the noise in the environment to its minimum level.And the differential chart (see Figure9) generated from Figure 8 can be in almost perfect profile.Effects of 30 times sharpening in Figure7.
(a)
(b)Figure 9
Picture for statistical results of jet frontier.In order to obtain the position of the jet frontier, further statistical processing of the image is needed. A real matrixR is generated from the 2-norm of three elements of the R(x,y) vector by taking x as the column and y as the row. Figure 10 can be obtained by summing each column of the matrix and normalizing the results.Figure 10
Distribution of the filteredR with the horizontal position of the image.In order to obtain the relationship between the pixel and the actual size, we also require a conversion unit of length. For this reason, a ruler placed in the same position with the jet was photographed with the same resolution.From Figures5–9, we learn that the actual 1 mm occupies 3.6 pixels length. Thus the velocity of the jet can be calculated easily. Taking Figure 11(a) and the adjacent frame of Figure 11(b) as example, their lateral attitudes are, respectively, 433 and 219.Distribution of the filteredR with the horizontal position of the image.
(a)
(b)According to the “3.6 pixels = 1 mm” conclusion, the initial droplets velocity used in this experiment is(4)vjet=433-2193.6×10-310-4=594m/s.
The liquid droplets velocity in the air is gradually reduced with the distance and the designed distance between the specimen and the export is only 10 mm, so it is reliable to estimate 600 m/s as the droplets velocity.


## 4. Experimental Results and Analysis

The VHX-600 digital microscope (see Figure12) is used to measure the three-dimensional profile of the sample before and after high speed liquid impact. Through an advanced zoom lens design and integrated setup, the microscopes are able to achieve a 20-time greater depth-of-field comparing with a typical optical microscope. This allows specimens with large variations in surface topography to be focused and accurately observed in a single image.Figure 12
The VHX-600 digital microscope.During the observation, vertical movement of the microscope lens is controlled by a computer. Current image captured by the lens after a tiny step length is transferred into the computer through high resolution CCD to process. The scene is identified from the focal length plane of the image by a program. When the lens driven by the step motor moves to a preset height, the focal length plane of the microscope just fall the scope of the field with certain depth to observe. The images obtained on the focal length plane of all steps are composted to get the three-dimensional surface of the corresponding area.Figure13 shows 500-time magnification of two specimens after impact. Three-dimensional scanning of the impact area is shown in Figure 15. In order to prevent the surface treatment layer from wearing away, the specimens were polished slightly. Therefore, it is difficult to distinguish the impact area visually. However, the phenomenon in the depth cloud map of specimens (see Figure 15) appears to be very obvious. The damage pattern observed after liquid impact on the specimen is typically a series of discrete cracks around or deviates from the central zone.500 times magnification of two specimens after impact.
(a)
(b)The presence of surface roughness cannot be ignored whatever the extent of polishing. Thus the surface roughness must be considered when calculating the pit depth. Figure14 is the schematic diagram of principle of measuring the impact pits. It describes the changes in the surface morphology of the sample before and after impact intuitively. Before the test, the surface profile from top to the bottom in the height direction of each specimen is measured for 3 times. Then we obtain their integral mean values and make them as average height (Ha) of materials before impact.Figure 14
Schematic diagram of principle of measuring the impact pits.Depth cloud map of laser cladding specimens impacted by high speed droplets: (a) case 1, (b) case 2, (c) case 3, (d) case 4, (e) case 5, and (f) case 6.
(a)
(b)
(c)
(d)
(e)
(f)UseHd which represents the height difference of the impact zone. Considering that the impact of droplets is a region rather than a point, we need to obtain the average height of the impact zone (Hd2). Then Hd can be obtained by subtracting Hd2 from the overall maximum height difference (Hd1) as shown in
(5)Hd=Hd1-Hd2.At last, the average pit depth can be obtained by subtractingHa from Hd:
(6)D=Hd-Ha=Hd1-Hd2-Ha.Ha is introduced to avoid the effects of surface roughness and has already been obtained before the test. Hd1 is the maximum value in the depth cloud map of specimens impacted by high speed droplets. Hd2 can be obtained by calculating the mean value of selected numbers from the surface elevation curves of specimens after impact. Thus, the relative accurate impact pit depth can be obtained by the above-mentioned equations.The impact region is relatively small and impurities exist in the steel itself, which may affect the results. In order to make the results more convincing, each group includes 6 specimens.The region of impact can be distinguished by observing the three-dimensional scanning area. For the laser cladding specimens, the maximum relative depth of the specimens after being impacted is 6.4μm with the minimum depth being 4.1 μm. Since the surface is not polished to a mirror effect and the droplets are distracted before impact, the maximum depth value is not worth too much. In order to prove our judgment, amplitude distribution curves of visual field after impact should be obtained before comparing the effect of impact. Figure 16 is surface elevation curves plotted from the data acquired from left to right along the depth cloud map. The black, red, and blue lines are in order drawn from the upper, middle, and lower portions of the data in Figure 15.Surface elevation curves of laser cladding specimens after impact: (a) case 1, (b) case 2, (c) case 3, (d) case 4, (e) case 5, and (f) case 6.
(a)
(b)
(c)
(d)
(e)
(f)For laser cladding specimen, it is obvious that the red and black curves are significantly lower in the left part than in the right part. Meanwhile it is seen that regions in deep color are relatively deeper from the charts of Figure15. This result is consistent with the observation, and therefore we can select data corresponding to the region to calculate the average depth of the surface after impact. Based on the calculation methods in this paper, we get the results of laser specimens. The depth of the impact area of laser cladding distribute in 0.5–1.5 μm. This material shows strong resistance to water erosion in such high speed droplet impact case.As seen from Figure17, the maximum relative depth of the 17-4PH specimens after being impacted is 10.6 μm with the minimum depth being 7.6 μm. Despite the fact that the impact marks in the depth cloud map are not obvious, they have relatively large impact depth than that of laser cladding specimens. As the 17-4PH surface is not coated, the extent of surface polishing is relatively high. The impact regions appear to be more dispersing. Through more detailed selection from the curves, the average depth of the surface after impact is obtained.Depth cloud map of 17-4PH specimens impacted by high speed water droplets: (a) case 1, (b) case 2, (c) case 3, (d) case 4, (e) case 5, and (f) case 6.
(a)
(b)
(c)
(d)
(e)
(f)Based on the calculating methods and Figure18, the calculated depth of the impact area of 17-4PH distributes in 2.5–3.5 μm. By comparing the depth cloud map and the surface elevation curves of these two specimens, it can be concluded that both the depth cloud map and the surface elevation curves show that the impact depth of laser cladding specimen is much shallower.Surface elevation curves of 17-4PH specimens after impact: (a) case 1, (b) case 2, (c) case 3, (d) case 4, (e) case 5, and (f) case 6.
(a)
(b)
(c)
(d)
(e)
(f)A frequency distribution diagram that contained all results of the specimens is shown in Figure19. The frequency distribution diagram is clearly indicating that the surface property of the material becomes more stable after laser cladding surface treatment. Therefore, a conclusion is reached that the laser cladding surface processing method is much better than ordinary blade material in terms of improving the blade material resistant to water erosion.Figure 19
Frequency distribution diagram of impact depth.


## 5. Conclusions

This paper compared and discussed the performance of erosion resistance between laser cladding and ordinary 17-4PH materials through high speed liquid-solid impact experiment. The result of the experiment showed that the average depth of the impact area for the laser cladding specimen is shallower than that of 17-4PH specimen, which indicates that laser cladding surface processing method is much better in terms of improving the blade material resistant to water erosion.The accuracy and reliability of the self-designed experimental systems and computing solutions are demonstrated by carrying this test. The research method and results have realistic and guiding significance to the selection of water erosion resistant method for the final stage blade of steam turbine.



---

*Source: 765064-2014-05-25.xml*