# Size-Dependent Indirect Excitation of Trivalent Er Ions via Si Nanocrystals Embedded in a Silicon-Rich Silicon Oxide Matrix Deposited by ECR-PECVD

Authors: G. Zatryb; A. Podhorodecki; J. Misiewicz; J. Wojcik; P. Mascher
Journal: Journal of Nanotechnology
 (2009)

---

## Abstract

Silicon nanocrystals (Si-nc) embedded in a silicon-rich silicon oxide matrix codoped withEr3+ ions have been fabricated by electron-cyclotron plasma-enhanced chemical vapor deposition. Indirect excitation of erbium photoluminescence via silicon nanocrystals has been obtained within a broad pump wavelength range. The influence of different nanocrystal sizes on the excitation transfer from the Si-nc to Er3+ ions is discussed.


---

## Body

## 1. Introduction

Erbium codoped silicon nanocrystals have become a subject of significant interest due to the wavelength of the radiative transitionI413/2→I415/2 in the 4f shell of the Er3+ ion (1.54 μm) which lies in the spectral region of minimum dispersion and maximum transparency of quartz optical-fiber telecommunication lines. Indirect excitation of erbium ions through electronic states of the silicon oxide host is known to be much more efficient than resonant optical pumping of the 4f electron shell of erbium ion itself [1]. The sensitization process allows one to increase the effective absorption cross-section of erbium by about three orders of magnitude [2]. Additionally, in the presence of silicon nanocrystals (Si-nc) an absorption band covers the wide visible range and thus lanthanide ions can be excited indirectly by white light.Several mechanisms have been proposed to explain the sensitization process of Er3+ PL in systems containing Si-nc. It has been proposed that mainly two energy transfer processes takes place, whose occurrence depends on the ion position with respect to Si-nc and which can work simultaneously [3]. The first process, for the ions very close to the Si-nc surface is fast with transfer time less than 100 ns. In this process an exciton is trapped to a defect state in the band gap and transfers its recombination energy to Er3+ ion by Auger-like process. The second energy transfer process is slower and is considered to be due to the resonant Förster type Coulombic interaction between the free excitons in Si-nc and Er3+. This kind of transfer can occur between nanocrystals and ions that are located at some distance from one another.Another factor that play a role in case of sensitization process is electronic structure of Si-nc. Several features are important here, like for example the spacing of energy levels of Si-nc, tuning of Si-nc and Er3+ electronic states from which energy transfer occurs [4], existence of some interface states like Si=O [5] and passivation of Si-nc surface for instance by nitrogen [6]. Even though there has been much research activity in this field, details of the influence of Si-nc electronic structure on the excitation of Er3+ ions are not yet sufficiently well understood. In particular, there is a shortage of excitation data in the high-absorption spectral region of Si-nc. For instance, available photoluminescence excitation (PLE) results obtained for Si-nc: Er3+ systems focus rather on low-energetic part of the PLE spectrum [7] or does not reach sufficiently deep [8] in the ultra-violet (UV) range where the absorption of Si-nc is very strong. Nevertheless, this kind of results are very valuable since they allowed to establish the occurrence of mediated excitation in this kind of systems. However, it is frequently not enough if one would like to investigate the influence of Si-nc absorption properties on excitation of the Er3+ ions.In this paper, we present results of an investigation of the excitation of erbium photoluminescence in a broad spectral range and its dependence on the erbium concentration and on different silicon concentrations in silicon-rich silicon oxide (SRSO) films grown by electron-cyclotron resonance plasma enhanced chemical vapor deposition (ECR)-PECVD.


## 2. Experimental Details

The Er-codoped SRSO thin films were grown on single crystal Si substrates by ECR-PECVD using SiH4 and O2 source gases diluted in Ar to form the SRSO matrix. Er(TMHD)3 (where TMHD stands for 2,2,6,6-tetramethyl-3,5-heptanedionato) was employed as the rare-earth precursor to achieve high-concentrations of Er codoping. The rare-earth sources were contained in a manifold which can be heated up to 200°C to sublime the precursor inside. Ar carrier gas then transports the rare-earth precursor through a transmission line after which it is introduced in the chamber alongside the SiH4 through the lower dispersion ring. All the films were annealed in a quartz tube furnace under flowing ultrahigh purity N2 for 1 hour. The annealing temperature was in all cases 1100°C. As we have shown in many papers in case of our deposition system this temperature is sufficient to obtain a few nanometers large silicon nanocrystals. This effect has been shown in the  absence of erbium codoping [9] as well as for erbium and different lanthanides codoped samples [10, 11]. The deposition system has been described in more details elsewhere [11]. The composition of the films was measured by Rutherford Backscattering Spectroscopy.The room temperature photoluminescence (PL) and photoluminescence excitation (PLE) of the erbium ions were measured using an InGaAs pin photodiode. As an excitation source, a 450 W Xe arc lamp connected to Triax 180 Jobin Yvon monochromator was used.


## 3. Results and Discussion

Figure1 shows PL spectra in the infrared region obtained for Er3+ codoped SixOy films at 488 nm excitation wavelength. The Si concentration in the films was 37 and 39 at. %, with Er3+ dopant concentrations of 0.15, 0.30 and 0.45 at. %. For all samples, emission at 1534 nm was observed, which is related to I413/2→I415/2 transition of Er3+ ions. The complex structure of the emission band likely originates from different environments of the Er3+ ions. This results in slightly shifted energy levels of the emitting ions, which are differently split by the local crystal field.Figure 1
PL spectra of Er3+ codoped SixOy films with different at. % of Si and Er obtained at 488 nm excitation wavelength.Moreover, Figure1 shows that the PL intensity increases strongly with the increase in erbium concentration and reaches a maximum for 0.45 at. %. Overall, the strongest emission was obtained for the sample with 39 at. % Si. The observed changes of the PL intensity with different Si and Er concentrations are consistent with our previous results [12] and are discussed there.It is well known that increasing the Si concentration in SRSO results in the formation of larger nanocrystals with smaller band gap [13, 14]. Thus, by changing the nanocrystal size, it is possible to tune the energy levels and to obtain more efficient excitation of the lanthanide ions either by a resonant or by a nonresonant excitation transfer. To verify this scenario we performed PLE experiments of Er3+ ions, comparing the properties of samples with 37 and 39 at. % Si, respectively. The obtained results are shown in Figure 2, in the form of normalized PLE intensities. The normalization was done separately for samples with 37 and 39 at. % Si  relative to samples with the 0.45 at. % of erbium ions.Figure 2
Normalized PLE spectra of Er3+ codoped SixOy films with different at. % of Si and Er measured at 1534 nm.The appearance of Er3+ related emission at excitation wavelengths far from resonance with erbium energy levels clearly indicates an efficient excitation transfer from silicon nanocrystals to lanthanide ions. From Figure 2, it is also evident that the maximum of the PLE peak shifts significantly towards smaller energies when the Si content increases, namely from 4.25 eV (for 37 at. % Si) to 3.52 eV (for 39 at. % Si). At the same time any significant shift in the PLE spectrum for different erbium concentrations is observed. The latter can be related to the small erbium concentrations while the former is related to quantum confinement effects (QCE), since changes in Si concentration reflect changes in Si-nc sizes [13].Moreover, the shape of the PLE spectra for samples with 39 at. % Si is much more Gaussian than in the case of 37 at. % Si. From fitting the PLE curves with a Gaussian function, we obtain a FWHM (full width at half maximum) of about ~167 nm for samples with 37 at. % Si and ~210 nm for samples with 39 at. % Si. It is well known that during the PECVD process the crystals’ mean radius increases with the silicon concentration of the films. Larger mean radii are also associated with a wider size distribution of Si nanocrystals. For example, Iacona et al. [13] have demonstrated that for nanocrystals deposited by PECVD with 37 at. % Si the radius is r=1.1 nm with standard deviation σ = 0.2 nm, for 39 at. % Si, r=1.5 and σ = 0.3, and for 42 at. % Si, r = 1.7 with σ = 0.5. These changes in size distribution should also be reflected in their absorption spectra [15]. Thus, the changes of the PLE spectra observed in our experiment may be associated with a widening of the nanocrystal size distribution and changes of the distribution mean value (QCE) [15].It should be pointed out that in general, the PLE signal is not simply an absorption spectrum of silicon nor the erbium ions. This is due to the fact that emission from the lanthanide ion depends on the absorption efficiency of Si-nc, the emission efficiency of the erbium ions, but also on the efficiency of the excitation transfer from the nanocrystal to the ion. This last factor can be dependent on the kind of the excitation transfer mechanism that takes place (Förster-Dexter energy transfer or charge transfer) and the matching of the energy levels of the nanocrystal and ion. Assuming constant erbium-related emission efficiency, our experimental results support the notion that the absorption properties of Si nanocrystals themselves play a dominant role in the excitation of Er3+ ions since the excitation spectra of the ions depend on the Si-nc size and size distribution in the same way as it should be expected for the Si-nc alone [16–18]. Unfortunately, the strong excitation transfer weakens the PL related to Si nanocrystals dramatically and we were not able to detect the PLE originating from Si-nc in our case.It is also worth of noticing, that shift of energy value of the PLE maximum for only a 2 at. % change in Si concentration is very strong (around 0.7 eV). It should not be however surprising when one takes into account that even a small change in Si concentration may lead to a significant change in the Si-nc sizes. As we have shown previously [9], the change of Si-nc diameter is smaller for larger annealing temperatures but is still very well recognizable for Ta = 1100°C and for instance 3 at. % difference in Si concentration may lead to 1-2 nm change of Si-nc size.Moreover, these few nanometers changes in Si-nc diameter should be considered as very large if one takes into account that we are dealing with the strong quantum confinement regime, where Si-nc size is comparable to the exciton Bohr radius of bulk Si. In this case even a fractional change of Si-nc size may results in a strong change of the nanocrystal band gap. Wolkin et al. have shown [19] that when the nanocrystal size increases from 1 up to about 1.6 nm the energy gap can decrease from approximately 4.25 down to 3.1 eV, respectively. It should be however pointed out that in our case this strong change should be visible rather in the absorption than emission properties of Si-nc, because as we have shown previously [12] we are dealing with recombination via the trapped excitons. Therefore the quantum confinement effect should manifest itself in the PLE results whereas PL spectra of nanocrystals may not even be affected by the Si-nc size due to surface states related emission.In the regime of small nanocrystal diameters, taking into account the empirical formula given by Meier et al. [15] the oscillator strength  increases strongly when nanocrystal diameters is reduced. Therefore, the Si-nc absorption cross-section is expected to be much higher in the case of 37 at. % Si samples, what should be reflected in more efficient Er3+ emission. Indeed, taking into account PLE intensities before normalization, among three Er concentrations that were used, we obtained the strongest Er3+ emission intensity for samples containing 37 at. % Si and 0.45 at. % Er, about 4 times stronger than in the case of 39 at. % Si and the same Er content. This result is in agreement with the above given interpretation. On the other hand, the HOMO-LUMO gap of Si-nc and the 4I13/2 level of erbium ions are even less well tuned to resonance in the case of smaller Si-nc, due to QCE. This should decrease the I413/2→I415/2 emission because multistep relaxation or multiphonon processes are needed to reach the emitting state. Nevertheless, we do not observe weakening of the emission for 37 at. % samples in comparison to 39 at. % samples. This result allows us to conclude, that in investigated case the Si-nc absorption cross-section is the most important factor that influences Er emission intensity.In Figure2, we also show a few higher Er3+energy levels, since some of them are in resonance with the excitation wavelengths used during the PLE experiment and a weak resonant excitation may also appear. However, we did not observe any evidence of this excitation mechanism in our case. This is mostly because the concentration of the lanthanide ions is very low in the investigated samples, which, together with a very low excitation cross-section of erbium ions (~10-20cm2), should not give any significant contribution to the absorption. Thus, it can be concluded that the erbium excitation is dominated by the optical properties of the silicon nanocrystals.To analyze the obtained data in more detail, the correlation between the obtained absorption edge and the size of the Si-nc has been estimated based on the formula given by Niquet et al [20]. Assuming the mean diameters of Si-nc taken from Iacona et al [13] for 37 at. % Si and 39 at. % Si as 2.2 and 3 nm, respectively, values of 2.28 eV and 1.87 eV were obtained, which correspond to HOMO-LUMO gap of silicon nanocrystals. To compare these results with our experimental data, the low energy part of the PLE spectra, corresponding to the lowest absorption transitions, was analyzed assuming that the absorption coefficient in this range is well described by the Tauc formula taken for indirect interband transitions of the bulk materials. The absorption edge values obtained in this way are Eg = 2.1 eV for samples with 37 at. % Si, and Eg = 1.7 eV for samples with 39 at. %. Any deviation in the calculated values for samples that vary in erbium concentration was within experimental error limit. Obtained band gaps are in good agreement with our theoretical estimations and other published experimental results [21]. However, despite the good agreement with the theoretical predictions it must be pointed out that it is only an estimation due to fact that in the case of purely zero-dimensional structures, k-space does not exist (thus, formally, indirect transitions also do not exist) and the density of states is a delta-like function, strongly different from the Tauc assumption of a square-like function for a bulk material.


## 4. Conclusions

The excitation spectra of Er photoluminescence in ECR-PECVD deposited SRSO: Er thin films have been measured. It has been shown that in all investigated samples a strong indirect excitation mechanism of Er3+ ions occurs. Moreover, a significant shift of the PLE spectra has been observed and ascribed to the quantum confinement effect. This feature together with considerable broadening of the PLE spectra for wider Si-nc size distribution indicate that the efficiency of indirect excitation of erbium ions is based mostly on the absorption properties of silicon nanocrystals. Thus, increase of Si-nc related absorption results in more efficient 4I13/2→4I15/2 emission, even though the HOMO-LUMO gap of Si-nc and the 4I13/2 level of erbium ions are less and less well tuned when decreasing the nanocrystal size so that a multistep relaxation or multiphonon processes are needed to reach the emitting state.



---