# Graphite Oxide under High Pressure: A Raman Spectroscopic Study

Authors: Lianqiang Xu; Li Cheng
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

We present a Raman-based study on the graphite oxide under high pressure. The graphite oxide is stable under hydrostatic high pressure ambient. By carefully fitting the D, G, and D′ bands which are merged at some extent, we successfully retrieve the information of peak position evolution of G band of graphite oxide under pressure, and it is found that the G band pressure coefficient is very close to that of graphene, and the pressure-induced peak position shift is reversible upon releasing the pressure. The Raman-based high pressure investigation indicates that the graphite oxide possesses good mechanical ductility despite the fact that it is oxygenated by functional groups. This study provides useful fundamental understanding of graphite oxide.


---

## Body

## 1. Introduction

In recent years, graphene attracted tremendous scientific and engineering interests owing to its unique electronic properties and tunable electronic band structures [1, 2]. Meanwhile, graphene’s chemical derivatives [3], which are obtained by modifying graphene/graphite structurally or chemically, have been studied extensively because of their giant potential applications [4–6]. To date, most graphene-based practical applications are mainly based on using the graphene-derivative materials, particularly that the graphene oxide (GO) has been already applied successfully in practical applications [7–9]. GO is a flexible material that can exist stably in both structures of powder and transparent film. Though GO is an insulating material, it can be switched to conducting phase by reducing it chemically or physically [3, 10, 11]. Thus it is clearly seen that GO is a multifunctional smart material which can be directly used for various practical applications.The fundamental understanding of GO’s physical and chemical properties has been reported largely in the past few years [3, 12–14], but only very limited studies were published on properties of GO under high pressure. Talyzin et al. discovered that GO is an unusual auxetic material that presents compressibility anomaly [15]. The volume of GO increases with the pressure up to 1.3–1.5 GPa in the water ambient due to the insertion of water into the interlayer space as revealed by detailed X-ray diffraction (XRD) analysis [15]. In addition to XRD-based study, Raman spectroscopy has been proven as one of the most useful and effective methods for probing the physical properties of carbon-based material at high pressure [16, 17], and from viewpoint of instrumental operation, Raman technique is more convenient and safe for probing the basic mechanical properties of carbon-based materials compared to that of XRD. However, despite the fact that GO’s mechanical property has been successfully used for practical applications [18], there have been no reported Raman studies on GO at high pressure. Motivated by this, we present the Raman studies on the GO’s properties at high pressure in this paper.


## 2. Experimental Details

GO samples prepared by traditional modified Hummer’s method were used in the experiment [19]. The microstructure of topography of the GO sample was characterized by JEOL 6700 FEG scanning electron microscope (SEM). The carbon- and oxygen-related chemical species of GO were characterized by XPS using Kratos Axis Ultra DLD (delay line detector) spectrometer equipped with a monochromatic Al Ka X-ray source (1486.6 eV). The X-ray diffraction (XRD) measurement is carried out by using Bruker D8 diffractometer, with a Cu Kα radiation (1.54 Å) in the locked-coupled geometry of the X-ray gun and detector. The high pressure was generated by a diamond anvil cell, in which the mixture of methanol and ethanol with mole ratio of 4 : 1 is used as a pressure medium. The value of pressure is calibrated by the energy shift of the R1 luminescence line of a ruby crystal. The Raman measurement is conducted by Witec CRM200 system with excitation laser wavelength of 532 nm. The laser was focused on the sample by passing through a 50x objective lens, and the Raman signal is finally collected by the same lens in the backscattering geometry. The laser power is controlled below 0.5 mW to avoid laser-induced sample heating effect.


## 3. Results and Discussion

From the SEM image shown in Figure1(a), the GO shows obvious exfoliated structure as compared to that of its precursor graphite powder. The XPS data further confirms that the GO is heavily oxidized as the atomic ratio between O and C is ~1 : 2. XRD data shows that the graphite (002) peak at 2θ=26.5° (d002=3.35 Å) is fully quenched, and instead, an obvious peak at 2θ=8.71° (d002=10.14 Å) is clearly observed. This is the evidence that shows that the interlayer space of graphite is enlarged dramatically after the intercalation of chemical functional groups and water molecules due to the oxidization process [20, 21].(a) SEM image of GO surface. (b) XPS result of GO. (c) XRD pattern of GO.
(a)
(b)
(c)Before the high pressure is applied to GO, the typical Raman spectrum measured in ambient air is shown in Figure2(a). There are two strong active Raman peaks located at ~1350 and 1600 cm−1 [3, 13]. The former peak is called D band, which is activated once the defects are introduced into sp2 hybridized carbon networks [22], and the intensity of D band is proportional to the defects concentration [23]. Thus the strong D band intensity indicates the existence of large amount of defects in sp2-carbon-based materials. The later peak is the G band, arising from the E2g vibrational mode of sp2-carbon network. It is worth mentioning that the presentation of strong D band at ~1350 cm−1 must accompany the presentation of another defects-assisted Raman band, the D′ band, located at ~1620 cm−1. The same as the case of D band, the intensity of D′ band is also proportional to the concentration of defects. Furthermore, containing the large amount of defects would give rise to the broadening effect of Raman bands. Thus the normally considered broad “G band” of GO is actually consisting of both G and D′ bands despite the fact that it looks like a single band due to the merge effect after broadening. In addition to the intense D, G, and D′ bands observed obviously, there are three weak Raman active bands at high wavenumber region (>2500 cm−1), which are 2D, D+G, and 2D′ bands. The 2D and 2D′ bands are second-order bands of D and D′ bands, respectively. Interestingly, the intensity of both 2D and 2D′ bands is inversely proportional to the concentration of defects because both of them are activated by two-phonon (with opposite momentum) assisted double resonant processes. Thus the pristine graphene with perfect sp2 carbon network presents very strong 2D and 2D′ bands, but the intensity decreases dramatically with breaking the sp2-hybridized structure through physical and chemical methods, such as irradiation of plasma/e-beam, oxidization, hydrogenation, and fluorination. The D+G band is a combination band which is also reflecting the concentration of defect. It can be obviously observed only when the concentration of defects is high. The shapes of D and G bands do not show obvious change and even the GO is heavily reduced (it is worth noting that the conductivity of reduced GO is normally presenting 4–6 orders higher than those of GO) [3, 10, 13], but the intensity ratio between 2D and D+G (I2D/ID+G) bands increases obviously due to the restoration of sp2-hybridized structure [13]. Thus these two Raman active bands are also very important for characterizing GO and RGO. However, for the GO under high pressure, the relatively weak intensities of 2D, D+G, and 2D′ bands overlap partially with the strong second-order Raman peak from diamond anvils, and hence the peak positions of relatively weak 2D, D+G, and 2D′ bands are difficult to be exactly determined under pressure. Furthermore, the diamond presents a very strong peak at ~1333 cm−1, which strongly influenced our observation for the peak information of D band. In our experiment, we will focus on the investigation of the peak position evolution of G and D′ bands under high pressure.(a) Raman spectrum of GO excited by 532 nm laser. (b) The enlarged region of 1000–2000 cm−1, and the five dashed lines are the five deconvoluted Raman peaks.
(a)
(b)For the Raman spectrum of as-received GO, we carefully fitted the peaks in the range between 1000 and 2000 cm−1. In Figure 2(b), the G and D′ bands are merged together. It is worth noting that, for the highly destroyed sp2-structure, only D, G, and D′ bands are not enough to perfectly fit all the Raman signals; thus additional f1 and f2 bands (peak position is between D and G bands as shown in Figure 2(b)) are considered for assisting the fitting result [24]. With introducing the two f bands, it is clearly seen that the five individual Raman bands of GO at wavenumber range between 1000 and 2000 cm−1 are well fitted (Figure 2(b)).Although the interlayer space is intercalated by oxygenated functional groups and H2O, the layered structure of GO still remains [20], which is similar to that of graphite except the fluctuation in layers. Thus the in-plane vibrational G and D′ bands deserved to be independently analyzed. For the Raman spectra of GO sample at pressures, it can be seen in Figure 3 that the Raman intensity ratio between GO (D, G, and D′ bands) and diamond (sp3) decreases with increasing pressure from 0 to 7.77 GPa, and the intensity ratio further decreases when the pressure is released from 7.77 to 0 GPa. The peak positions of G and D′ bands for unpressured GO are located at ~1587 and ~1615 cm−1, respectively. It is worth noting that the peak position of G band of GO is slightly larger than pristine graphite/graphene (~1580 cm−1) due to chemical-functional-group-induced hole doping effect. When pressure increases, both G and D′ bands linearly shift to higher wavenumber, and the peak positions blueshift to ~1621 and ~1649 cm−1 at the maximum pressure (7.78 GPa) for G and D′ bands, respectively. The linearly blueshift of both G and D′ bands indicates that the pressure compresses the GO which gives rise to the hardening effect of phonons vibration. For the pressure releasing process, the peak positions of both G and D′ bands decrease, and they reach the original values once the pressure is fully released. It indicates that the high pressure (up to ~8 GPa) induced compression of lattice is reversible. The evolution of peak positions of both G and D′ bands with pressure changes can be clearly seen in Figure 4. There are two phenomena deserved to be mentioned. (a) The slopes of both positions of G and D′ bands vary with pressure are almost the same. (b) The peak positions of both G and D′ bands are reversible upon decreasing the pressure. As shown in Figure 4, the pressure coefficient for G and D′ bands can be easily calculated, which are ~3.8 cm−1/GPa for both bands. The pressure coefficient value for G band of GO is smaller than that of both pure graphite [25, 26] and pristine grapheme [16]. As the interlayer space of GO is filled out of oxygenated functional groups and water molecules, the adjacent layer-layer coupling is suppressed dramatically due to the enlarged distance (reflected by XRD result as shown in Figure 1(c)), and furthermore, the functional groups (such as hydroxyl, carbonyl, and carboxyl groups) chemically bound to the in-plane surface of GO result in the increase of elastic coefficient, which gives rise to the reduction of pressure coefficient. This is also in agreement with the reported result that the effective Young’s modulus of single-layer graphene oxide is lower than that of grapheme [27]. It indicates that though the GO is a kind of derivative of graphite with maintained layered structure, its elastic property shows obvious difference compared to that of graphite.Figure 3
The Raman spectra of GO under various pressures. The first stage shows the evolution of spectra with increasing pressure from 0 to 7.77 GPa gradually, and the second stage shows the evolution of spectra with releasing pressure from 7.77 to 0 GPa.Figure 4
The evolution of peak positions of Raman G (blue) and D′ (red) bands at high pressures. The solid blue squares and red circles represent the pressure increasing stage, and the opened blue squares and red circles represent the pressure releasing stage.


## 4. Conclusions

In summary, Raman spectroscopy has been carried out on GO under hydrostatic pressure up to~8 GPa. By proper fitting the G and D′ bands of GO at various pressures, the evolution of pressure-induced G band shift is clearly revealed, and it is found that the pressure coefficient of G band for GO is smaller than that of graphite and graphene. It is because of the fact that the intercalation of both oxygenated functional groups and water molecules suppresses the adjacent layer-layer coupling, and the chemically bonded functional groups at the in-plane surface of GO result in the increase of elastic coefficient. The reversibility of Raman peak positions with respect to the hydrostatic pressure indicates that the GO is a good mechanical ductile material though its elastic property shows some difference compared to graphite. The Raman study of GO’s properties at high pressure reveals some fundamental understanding and may be useful for guiding GO-based mechanical applications.



---