# Ultrafine Magnetite Nanopowder: Synthesis, Characterization, and Preliminary Use as Filler of Polymethylmethacrylate Nanocomposites

Authors: Pietro Russo; Domenico Acierno; Mariano Palomba; Gianfranco Carotenuto; Roberto Rosa; Antonino Rizzuti; Cristina Leonelli
Journal: Journal of Nanotechnology
 (2012)

---

## Abstract

Magnetite (Fe3O4) nanoparticles prepared by microwave-assisted hydrothermal synthesis have been characterized in terms of morphological and structural features. Electron micrographs collected in both scanning (SEM) and transmission (TEM) modes and evaluations of X-ray powder diffraction (XRD) patterns have indicated the achievement of a monodispersed crystallite structure with particles having an average size around 15–20 nm. Structural investigations by Micro-Raman spectroscopy highlighted the obtainment of magnetite nanocrystals with a partial surface oxidation to maghemite (γ-Fe3O4). Preliminary attention has been also paid to the use of these magnetite nanoparticles as filler for a commercial polymethylmethacrylate resin. Hybrid formulations containing up to 3 wt% of nanoparticles were prepared by melt blending and characterized by calorimetric and thermogravimetric tests. For sake of comparison, same formulations containing commercial Fe3O4 nanoparticles are also reported. Calorimetric characterization indicates an increase of both glass transition temperature and thermal stability of the nanocomposite systems when loaded with the synthesized magnetite nanoparticles rather then loaded with the same amount of commercial Fe3O4. This first observation represents just one aspect of the promising potentiality offered by the novel magnetic nanoparticles when mixed with PMMA.


---

## Body

## 1. Introduction

In the last decades, a considerable amount of research has been devoted to the synthesis and characterization of iron oxides nanoparticles because of their technological potentialities. In particular, nanosized oxide materials such as magnetite (Fe3O4), maghemite (γ-Fe2O3), and hematite (α-Fe2O3) have found wide-ranging applications. Hematite nanoparticles, crystallizing in the rhombohedral system and showing a weak ferromagnetic behavior at room temperature [1], have been extensively used as catalyst [2, 3], pigment [4], gas sensor [5], optical devices [6], and medicine applications [7]. Magnetite and maghemite, instead, crystallizing in the cubic crystal system and with a ferromagnetic behavior at room temperature, have been widely exploited in technological applications including information storage [8], sensors [9], refrigeration [10], and coil cores [11], as well as in contrast agent for magnetic resonance imaging [12, 13], and potential mediator for magnetic hyperthermia [14].Among the chemical routes used so far to synthesize iron oxide based nanomaterials, it is worth to mention hydrothermal synthesis [15, 16], coprecipitation [17], sol-gel method [18], and colloidal chemistry method [19]. These methods usually involve synthesizing an iron-based precursor gel, followed by decomposing the gel or precursor into the designed crystalline iron oxide phase at an elevated temperature. However, the uniformity of the size of the particle of these nanomaterials was rather poor [20–22].Considering that chemical composition and morphology controls for these magnetic nanoparticles appear to be crucial for their applications, a specific interest has been dedicated to control the particle size dispersion [23–26]. Small sizes and uniform morphology are typically required for the applications of magnetic nanoparticles because of the dependence of magnetic properties on the morphologies of nanoparticles. When the size of Fe3O4, nanoparticles is very small, the size of single-magnetic domain is equal to that of each single particle. Fe3O4 nanoparticles usually exhibit superparamagnetic property [27], therefore, their fabrication is attracting a lot of interest.Another well-established approach to control, on one side, the morphology of magnetite nanoparticles during their synthesis and, on the other hand, their dispersion in a polymer matrix is the use of suitable polymeric surfactants [28, 29]. At this regard, given the outstanding interest gained by this class of organic/inorganic materials for applications in many fields, a wide range of resins including polystyrene [30], poly(vinyl alcohol) [31], poly(pyrrole) [32], polyaniline [33, 34], and epoxy resins [35] has been already considered.In this research, ultrafine magnetite nanoparticles were synthesized by an innovative hydrothermal microwave-assisted route and systematically characterized in terms of morphological and structural aspects. Literature references [36, 37] employ iron(III) chloride, FeCl3·6H2O as the metal precursor in the hydrolytic reactions, while in the present work the Fe3O4 precursor was FeCl2·4H2O. This is a main difference that requires to be highlighted since most of the “soft-chemistry” synthetic strategies (both hydrolytic and nonhydrolytic) for the obtainment of magnetite nanoparticles start from iron-(III-)based precursor (see e.g., [38, 39]). Moreover, in the work by Parsons et al. [37] the product obtained at the reaction temperature of 100°C and 125°C was an iron (III) oxyhydroxide chloride, commonly known as akaganeite. An increase in the reaction temperature up to 250°C led to single hematite phase. Thus, the work by Pearsons and coworkers substantially differs from ours in both the precursors used and the synthesised products.As concerns the paper by Wang et al. [36], a further difference (apart from the use of an iron(III) precursor) with respect to our paper is represented by the use of polyethylene glycol (PEG) as surfactant. Indeed, those authors employed such a surfactant in order to obtain nanoparticles of phase pure Fe3O4; however, as they noticed (through FTIR study), the surfactant was adsorbed on the surface of nanoparticles product thus affecting the saturation magnetization.In order to emphasize potential applications of the novel magnetic powder preliminary attention has been devoted to polymer nanocomposites based on an amorphous thermoplastic matrix. In particular, given the relevant interest gained so far by polymer systems containing magnetic particles in many different industrial areas (e.g., radio-absorbing materials, polymer welding, etc. [40, 41], synthesized magnetite was loaded in a polymethylmethacrylate (PMMA) by using a conventional melt-blending process.Compounds with contents equal to 1 and 3% by weight of new magnetite were compared with analogous systems filled with commercial magnetite nanopowder in terms of thermal parameters such as glass transition and thermal stability of the matrix. At this regards, results were discussed taking the neat matrix, processed under the same conditions, as the reference material.


## 2. Experimental

### 2.1. Materials

The polymeric matrix used in this study was the polymethylmethacrylate (PMMA) Optix CA-51 (MFI 15 g/10 min) supplied by Plaskolite-Continental Acrylics.Commercial magnetite nanopowder (named Fe3O4 (C) in the text and figures) was provided by Sigma Aldrich with an average particle size less than 50 μm and a BET surface area higher than 60 m2/g.Hydrazine hydrate and NaOH (pellets) were purchased from Sigma Aldrich, while FeCl2·4H2O was provided by Merck. All of these precursors for the microwave-assisted hydrothermal synthesis of magnetite nanoparticles were of analytical grade and used without any purification.


### 2.2. Synthesis of Magnetite Nanoparticles (Fe3O4 (S))

The general procedure for the microwave assisted hydrothermal synthesis of Fe3O4 nanoparticles is as follows: 0.5150 g (2.6 mmol) of FeCl2·4H2O were dissolved in 13 mL of deionized water under nitrogen atmosphere, in a Teflon-lined digestion vessel. A previously prepared NaOH/hydrate hydrazine solution (0.2609 g (6.5 mmol) of NaOH in 2.174 mL (70 mmol) of N2H4·H2O) was dropwise added to the iron (II) solution under nitrogen and vigorous magnetic stirring.The sealed reaction vessel was hydrothermally treated using a microwave digestion system ETHOS TC (Milestone) operating at 2.45 GHz frequency, at 100°C for 120 min. with a continuous and accurate computer controlling of reaction time, temperature, pressure, and microwave power. After the reaction the product was naturally cooled to room temperature, and the obtained dark-brown powder was centrifuged (4000 rpm), washed several times with deionized water, and finally dried overnight at 80°C, under vacuum. Surface area was determined to be 81 m2/g.


### 2.3. Preparation of PMMA/Fe3O4 Nanocomposites

The inclusion of nanosized particles of magnetite in the molten PMMA was carried out in a HAAKE Minilab Rheomex microcompounder mod. CTW5 conical double-screw extruder. In this apparatus, an integrated bypass valve enables the recirculation of the melt via a back flow channel. In our case, pellets of PMMA and proper amounts of magnetite were fed to the microcompounder in a maximum time of 2 minutes, allowing a recirculation of the molten compound for 5 minutes before collecting the extruded composite systems.A flat temperature profile of 220°C and a screw speed of 80 rpm were employed operating in corotating mode.


### 2.4. Characterization Techniques

Nanostructured magnetite morphology was imaged by transmission electron microscopy (TEM, Philips EM2085, 100 kV) and scanning electron microscopy (SEM, Cambridge-S360). In particular, in the preparation of specimens for the TEM investigation, the magnetite powder was dispersed in ethanol by applying ultrasounds (ultrasonic bath, Bandeline RK515CH), and a polymeric surfactant (poly (vinyl pyrrolidone),Mw=10,000 gmol−1) was added in order to achieve a stable colloid. Then, a drop of this colloidal suspension was placed on a TEM copper grid coated by Formvar resin thin film and allowed to dry in air at room temperature. After drying, the copper grid was graphitized by sputtering. The crystallographic structure of magnetite was investigated by large angle X-ray powder diffraction (XRD, X′Pert PRO, PANAlytical, CuKα radiation). The structure of the magnetite powder was also investigated by Micro-Raman spectroscopy (LabRam, Horiba Jobin-Yvon, Longjumeau, France) employing a 632.81 nm wavelength laser which was used on both magnetite powders. In addition, we employed a D1 type filter in order to use 2 mW output laser power, focused onto the sample using a 10x objective lens, in order to avoid any phase transformation of the analyzed powders, as a consequence of laser-induced thermal effects. It is well known that under heat treatment magnetite easily transforms into the oxidized crystal of maghemite at around 200°C to finally complete oxidation to hematite (α-Fe2O3) at around 400°C [42].About PMMA-based nanocomposites, melt-blended products were analysed by differential scanning calorimetry using a DSC (DSC1, Mettler Toledo Instrument). Samples were run by a heating rate of 20°C/min on the temperature range from 25 to 200°C with the aim to verify any influence of magnetite nanoparticles on the glass transition temperature of nanocomposites.Further thermogravimetric tests were carried out by using a Q5000-TA Instrument. Approximately 15 mg of each material were submitted to a temperature ramp from 25 to 600°C at a heating rate of 10°C/min under nitrogen. The influence on magnetite nanoparticles on thermal stability and decomposition behavior of polymer matrix were investigated taking the unfilled PMMA as the reference material.


## 2.1. Materials

The polymeric matrix used in this study was the polymethylmethacrylate (PMMA) Optix CA-51 (MFI 15 g/10 min) supplied by Plaskolite-Continental Acrylics.Commercial magnetite nanopowder (named Fe3O4 (C) in the text and figures) was provided by Sigma Aldrich with an average particle size less than 50 μm and a BET surface area higher than 60 m2/g.Hydrazine hydrate and NaOH (pellets) were purchased from Sigma Aldrich, while FeCl2·4H2O was provided by Merck. All of these precursors for the microwave-assisted hydrothermal synthesis of magnetite nanoparticles were of analytical grade and used without any purification.


## 2.2. Synthesis of Magnetite Nanoparticles (Fe3O4 (S))

The general procedure for the microwave assisted hydrothermal synthesis of Fe3O4 nanoparticles is as follows: 0.5150 g (2.6 mmol) of FeCl2·4H2O were dissolved in 13 mL of deionized water under nitrogen atmosphere, in a Teflon-lined digestion vessel. A previously prepared NaOH/hydrate hydrazine solution (0.2609 g (6.5 mmol) of NaOH in 2.174 mL (70 mmol) of N2H4·H2O) was dropwise added to the iron (II) solution under nitrogen and vigorous magnetic stirring.The sealed reaction vessel was hydrothermally treated using a microwave digestion system ETHOS TC (Milestone) operating at 2.45 GHz frequency, at 100°C for 120 min. with a continuous and accurate computer controlling of reaction time, temperature, pressure, and microwave power. After the reaction the product was naturally cooled to room temperature, and the obtained dark-brown powder was centrifuged (4000 rpm), washed several times with deionized water, and finally dried overnight at 80°C, under vacuum. Surface area was determined to be 81 m2/g.


## 2.3. Preparation of PMMA/Fe3O4 Nanocomposites

The inclusion of nanosized particles of magnetite in the molten PMMA was carried out in a HAAKE Minilab Rheomex microcompounder mod. CTW5 conical double-screw extruder. In this apparatus, an integrated bypass valve enables the recirculation of the melt via a back flow channel. In our case, pellets of PMMA and proper amounts of magnetite were fed to the microcompounder in a maximum time of 2 minutes, allowing a recirculation of the molten compound for 5 minutes before collecting the extruded composite systems.A flat temperature profile of 220°C and a screw speed of 80 rpm were employed operating in corotating mode.


## 2.4. Characterization Techniques

Nanostructured magnetite morphology was imaged by transmission electron microscopy (TEM, Philips EM2085, 100 kV) and scanning electron microscopy (SEM, Cambridge-S360). In particular, in the preparation of specimens for the TEM investigation, the magnetite powder was dispersed in ethanol by applying ultrasounds (ultrasonic bath, Bandeline RK515CH), and a polymeric surfactant (poly (vinyl pyrrolidone),Mw=10,000 gmol−1) was added in order to achieve a stable colloid. Then, a drop of this colloidal suspension was placed on a TEM copper grid coated by Formvar resin thin film and allowed to dry in air at room temperature. After drying, the copper grid was graphitized by sputtering. The crystallographic structure of magnetite was investigated by large angle X-ray powder diffraction (XRD, X′Pert PRO, PANAlytical, CuKα radiation). The structure of the magnetite powder was also investigated by Micro-Raman spectroscopy (LabRam, Horiba Jobin-Yvon, Longjumeau, France) employing a 632.81 nm wavelength laser which was used on both magnetite powders. In addition, we employed a D1 type filter in order to use 2 mW output laser power, focused onto the sample using a 10x objective lens, in order to avoid any phase transformation of the analyzed powders, as a consequence of laser-induced thermal effects. It is well known that under heat treatment magnetite easily transforms into the oxidized crystal of maghemite at around 200°C to finally complete oxidation to hematite (α-Fe2O3) at around 400°C [42].About PMMA-based nanocomposites, melt-blended products were analysed by differential scanning calorimetry using a DSC (DSC1, Mettler Toledo Instrument). Samples were run by a heating rate of 20°C/min on the temperature range from 25 to 200°C with the aim to verify any influence of magnetite nanoparticles on the glass transition temperature of nanocomposites.Further thermogravimetric tests were carried out by using a Q5000-TA Instrument. Approximately 15 mg of each material were submitted to a temperature ramp from 25 to 600°C at a heating rate of 10°C/min under nitrogen. The influence on magnetite nanoparticles on thermal stability and decomposition behavior of polymer matrix were investigated taking the unfilled PMMA as the reference material.


## 3. Result and Discussion

The as-synthesized magnetite (Fe3O4) was made of a very fine dark-brown powder, which exhibited a good magnetic behavior (Figure 1). As reported in a previous work [43], magnetism of the probe was measured by means of MPMSR-5S-SQUID magnetometer of Quantum-Design. In the ZFC/FC curves the Verwey transition at 120 K was observed. This transition justified the nanoparticle core constituted by stoichiometric magnetite [44]. Magnetization-temperature curves show a saturation magnetization of about 64 emu/g which therefore much lower than the bulk value of magnetite 92 emu/g, observing additional remanence and coercivity. The decrease of the saturation magnetization is, probably, due to the maghemite shell surrounding the nanoparticles.TEM micrograph showing the characteristic dendritic structure generated by the magnetite nanoparticles (left-marker: 1000 nm), and detail of the microscopic structure (right).
(a)
(b)According to the morphological investigation using transmission electron microscope (TEM), the as-prepared powder consisted of monodispersed nanoparticles with a size of ca. 15–20 nm. As visible in the TEM micrograph given in Figure1 (left side, magnification 25000x), these particles produced very large branched or dendritic structures. Details observed at high magnification (180000x) confirmed that the sample is constituted by pseudospherical nanoparticles with a monomodal particle size distribution.Fe3O4 (s) sample was characterized also by scanning electron microscopy (SEM), and according to Figure 2 the nanoparticles appearasaggregates in densely packed secondary particles. Moreover, at higher enlargements (Figure 2(a)-right) these secondary particles appear as powder grains made of closely packed spherical nanoparticles partially sintered together.SEM micrograph of the as-synthesized powder ((a)-left), and detail of the single grain ((a)-right) and of the commercial powder at low ((b)-left) and high ((a)-right) enlargements.
(a)
(b)Microstructure of commercial iron oxide powders has been also characterized by means of scanning electron microscopy. Backscattered electron (BSE) image is reported in Figure2(b). The average grain size is in the 0.8–2.5 μm size. Differently from Fe3O4 hydrothermal powder the commercial one does not present an enhanced nanostructure.As visible in Figure3, X-ray diffractogram (XRD) of the as synthesized samples showed a diffraction pattern characteristic of magnetite (Fe3O4). In particular, the peaks at 2θ equal to 30.1°, 35.4°, 43.1°, 53.4°, 57.1°, and 62.6° can be indexed as (220), (311), (400), (511), and (440) lattice planes of cubic magnetite, respectively (JCPDS 19-629). The average Fe3O4 crystallite size was calculated by applying the Debye-Scherrer equation (Dhkl=0.9λ/βcosθ, in which β stands for the half-width of the XRD diffraction line, θ is the peak position in angles, and λ is the CuKα radiation wavelength, that is 1.54056 Å) to the reflection peak (311) and it resulted approximately of 10 nm. Such crystallite size approximately corresponds to the TEM (Figure 1, right) average size of particles, which indicates a monocrystalline nature of the particles.Figure 3
XRD pattern of the as-prepared magnetite nanoparticles.The presence of hematite, beside to the major magnetite phase, has been confirmed by X-ray diffraction analysis on the commercial iron oxide nanopowders (Figure4).Figure 4
XRD pattern of the commercial magnetite nanostructured particles.To evaluate the purity of crystalline phases in the two magnetite powders, a specific characterization procedure was set up.The XRD patterns of magnetite (Fe3O4) and maghemite (γ-Fe2O3) differ only for the presence of a few diffraction peaks with intensity lower than 5%. Thus, the absence of these low-intensity peaks, from the X-ray diffractogram of Figure 4, can not be considered a proof of the obtainment of pure magnetite phase during the microwave assisted hydrothermal synthesis [40]. An alternative technique has been envisaged in Raman spectroscopy that is considered to be a powerful tool to distinguish the different structural phases of iron oxides [43].Raman spectra of both commercial and synthetic iron oxide nanopowders are reported in Figure5 (please notice that the y-axis is not the same for both spectra).Raman spectra of as-prepared magnetite nanoparticles (a) and the commercial magnetite nanostructured particles (b).
(a)
(b)The presence of nanostructured crystalline powders in the sample of hydrothermally prepared magnetite is clearly visible from the broadness of the peaks in Figure5(a). Magnetite phase is easily discernible by its main band centred at around 667 cm−1. Thus, magnetite can be assumed to be present in both commercial and synthetic iron oxide nanopowders. In the Raman spectrum of as-prepared magnetite nanoparticles, typical maghemite band (720 cm−1 [44, 45]) is clearly evident, thus confirming the obtainment of magnetite nanocrystals with the surface partially oxidised to maghemite. Accordingly to [46] maghemite phase should show an additional band at 511 cm−1, which could be either the one centred at 460 cm−1 or could be identified as the minor peak at its right.On the other hand, commercial iron oxide nanoparticles consist of a complex mixture of magnetite, maghemite, and hematite phases. The latter can be easily individualised by the bands situated at 227, 247, 294, 412, and 613 cm−1, according to literature [44, 45]. The presence of hematite phase has been also confirmed by X-ray diffraction analysis on the commercial iron oxide nanopowders (Figure 4).Regarding thermal properties of melt-blended nanocomposite systems based on polymethylmethacrylate, PMMA, in Figure6, the comparison of thermograms collected by calorimetric tests is depicted. In particular, a clear shift of the inflection point usually associated with the glass-rubber transition is observed for all hybrid formulations.Figure 6
Comparison of DSC curves of the nanocomposites based on PMMA taking the neat matrix as reference material.The analysis showed an increase of the glass transition temperatureTg, evaluated as the temperature at the inflection point of the thermograms. This parameter appeared to increase with the filler content especially in presence of synthesized magnetite nanoparticles (denoted as S sample), with respect to commercial powders (denoted as C samples).This behavior is usually ascribed to restrictions of the polymer chains mobility by the inclusion of rigid nanoparticles. Moreover, islands of nanoparticles may adsorb portion of adjacent chains, especially if longer than the average size of macromolecules constituting the matrix and, thus, having the highest relaxation times, enhancing this effect.Appreciating the evaluations shown in Figure5 in the light of the range of experimental error evaluated on at least 5 tests for each material and approximately equal to 2%, it can be stated that the commercial magnetite does not significantly alter the glass transition temperature of the matrix, at least on the interval compositions examined so far. On the contrary, the Tg is changed from 100.1°C for the neat matrix to 104.6 and 108.8°C for nanocomposites containing 1 and 3 wt%, respectively, of microwave hydrothermally synthesized magnetite. On the basis of the above considerations, these benefits can be explained by assuming the establishment of specific chemical-physical interactions at the filler-matrix interface such as to improve the thermal performance of the amorphous matrix.Finally, Figures7 and 8 report thermogravimetric (TG) mass loss curves and their first derivative, respectively, for all PMMA nanocomposites.Figure 7
TG mass loss curves of all investigated materials under N2. (Heating rate 10°/min).Figure 8
Derivative TG curves of all investigated materials under N2. (Heating rate 10°/min).In more details, looking to the data, averaged on at least 3 tests for each material and summarized in Table1, the following considerations may be drawn.Table 1
Thermal parameters of PMMA-based materials (Hmax: DTG peak height; FWMH: full width at medium height of DTG peak).
Material
T
-
5
% (°C)
T
peak DTG (°C)
H
max
FWMH (°C)
Neat extruded PMMA
355.2
±
0.5
379.1
±
0.7
45
42
PMMA/1 wt% Fe3O4 (C)
357.8
±
1.2
397.4
±
0.9
38
46
PMMA/3 wt% Fe3O4 (C)
358.8
±
0.7
393.8
±
0.6
41
45
PMMA/1 wt% Fe3O4 (S)
358.1
±
0.8
395.1
±
0.3
38
47
PMMA/3 wt% Fe3O4 (S)
359.4
±
0.7
395.5
±
0.4
38
48Assuming the temperature at which a 5% of weight loss is achieved (T-5%) as the thermal stability of the material, a slight increase of this parameter can be observed for all nanocomposite systems with respect to the neat matrix. This effect can be ascribed to the restrictions of the polymer chains mobility already invoked to explain the increase of the glass transition temperature as well as to the absorption of polymer on the oxide surface by methoxycarbonyl groups (–C(O)OCH3) [47].Moreover, in all cases, the residue at 600°C is comparable with the amount of magnetite nanoparticles, initially included in the PMMA.The comparison of derivative signals in Figure8, instead, has allowed to assess any effect related to the presence of magnetite nanoparticles on the thermal behaviour of investigated materials. Starting from the evidence showing the existence of a single decomposition signal for both unfilled matrix and nanocomposite systems, additions of magnetite always induced a shift of the maximum decomposition signal (Tpeak DTG) to higher temperature with respect to the reference neat matrix (see Table 1). In addition, the hybrid formulations showed a reduction in the height of the decomposition signal.This behavior appeared to be influenced by the type of magnetite used. In particular, for samples containing 1% by weight of nanoparticles a reduction in the height of the signal equal to about 15% compared to the reference material was shown regardless of the type of included magnetite: as shown in Table1, the height of the decomposition signal goes from 45 to 38°C. But further increase of the content of filler implied an inversion of the trend for systems containing commercial magnetite (Fe3O4 (C)), with a reduction in the lowering of the signal compared to the reference value equal to approximately 9% (from the reference value 45 to 41°C). Instead, no further effects were observed in presence of synthesized filler (Fe3O4 (S)).Finally, a slight widening of the decomposition signal was observed for all hybrid formulations with respect to unfilled PMMA and evaluated in terms of full width at medium height (FWMH) (see Table1).These phenomena, probably related to the influence of filler on involved combustion processes, are still under investigation.


## 4. Conclusions

The microwave hydrothermally prepared nanoparticles of magnetite are compared to the commercial ones in terms of effects on the thermal properties of PMMA nanocomposites. The smaller particles size of the synthesized nanoparticles with respect to the commercial ones and the absence of agglomeration allows a better dispersion in the polymeric matrix via extrusion process.The effects of nanoparticles dispersion in the PMMA have been measured in terms of glass transition temperature and thermal stability of melt-blended systems compared with the unfilled matrix.The experimental results showed an increase of both of these parameters especially in the case of new nanoparticles. This effect, attributed to specific filler-matrix interactions, probably more efficient for the greater uniformity of size distribution of synthesized magnetites with respect to the commercial ones, highlights their interesting potentialities of use.Finally, being aware that a magnetic characterization of the nanocomposite systems is as important as the morphological and thermal ones, authors are also expecting better magnetic properties in the Fe3O4-synthetic_PMMA samples.



---

*Source: 728326-2012-08-28.xml*