# Fundamental Properties of Magnesium Phosphate Cement Mortar for Rapid Repair of Concrete

Authors: Joon Woo Park; Ki Hwan Kim; Ki Yong Ann
Journal: Advances in Materials Science and Engineering
 (2016)

---

## Abstract

Fundamental properties of magnesium phosphate cement (MPC) were investigated in this paper. The setting time and compressive and bond (i.e., flexural and tensile bond) strengths were measured to assess the applicability, and hydration product was detected by the X-ray diffraction. The specimens were manufactured with magnesia and potassium dihydrogen phosphate (K2HPO4) was added to activate hydration process. The Borax (Na2B4O7·10H2O) was used as a retarder to mitigate overwhelming rapid hardening. Mercury intrusion porosimetry was used to examine the pore structure of MPC mortar, and simultaneously rapid chloride penetration test was performed. As a result, the compressive strength of MPC mortar was mostly achieved within 12 hours; in particular, the MPC mortar at 4.0 of M/P ranked the highest value accounting for 30.0 MPa. When it comes to tensile and flexural bond to old substrate in mortar patching, the MPS had the higher tensile and flexural strengths, accounting for 1.9 and 1.7 MPa, respectively, compared to OPC mortar patching. Unlike Portland cement mortar, the MPC mortar contained mainly air void rather than capillary pores in the pore distribution. Presumably due to reduced capillary pore in the MPC, the MPC indicated lower penetrability in the chloride penetration test.


---

## Body

## 1. Introduction

Concrete structure may often suffer from an unexpected deterioration in terms of pop-out arising from physical/chemical delamination and corrosion of steel reinforcement. Moreover, internal cracking has still a potential risk of degradation of concrete properties, subsequently leading to structural failure [1, 2]. Thus, regular repair and rehabilitation would be required to secure a structural safety. However, unlike other civil infrastructures, the traffic restriction during the repair of pavement costs high; only a couple of hours are given for the repair treatment at night to avoid congestion of transportation. Additionally, the conventional repair materials such as ordinary Portland cement and hot-mix asphalt may face early degradation due to a debondment from the existing substrate [3–6].A recent study reported that magnesium phosphate cement (MPC) can rapidly harden to gain the strength in a short duration, ranging about several hours to the level of normal strength of ordinary Portland cement concrete [7, 8]. Typically used MPC was produced by using ammonium phosphate [9, 10]. However, ammonium gas is generated during hydration product and this causes serious odour. Due to its disadvantage, many researchers have effort on finding other phosphate slat. As a result, they found potassium dihydrogen phosphate (KH2PO4) as a replacement. Further studies on MPC using potassium dihydrogen phosphate showed that it has high bond strength [11, 12] and low drying shrinkage [13]. However, limited investigation has been conducted on applying MPC for repair of concrete pavement.In present study, to verify the feasibility of the MPC as a repair mortar to concrete pavement, the setting time was measured by a monitoring of the penetration resistance to fresh mortar, and simultaneously a development of the strength was evaluated. To evaluate its properties with old substrate, bond strength was performed. Additionally the pore structure of MPC mortar was examined by mercury intrusion porosimetry to explain the relation between the porosity and mechanical properties and also explain the relation between pore distribution and ionic permeability.


## 2. Experimental Works

### 2.1. Materials and Specimen Preparation

To assess the mechanical properties of magnesium phosphate cement (MPC) mortar, magnesia was used as a binder, while ordinary Portland cement (OPC) was used for the control. The oxide composition of binders was measured by X-ray fluorescence as given in Table1. The fineness of magnesia and OPC was 5,089 and 3,120 cm2/g, respectively. To activate the hydration process in MPC matrix, potassium dihydrogen phosphate was admixed. The purity of MgO exceeded 88.5% and KH2PO4 exceeded 99.8%. MPC paste specimens were cast for a measurement of X-ray diffraction (XRD) analysis. Mix proportion for MPC paste was varied with MgO/phosphate (M/P) ratio and borax/MgO (B/M) and water/MgO (W/M) was 0.20 (Table 2). To observe the hydration product of MPC, M/P of 4, B/M of 0.08, and W/M of 0.20 were used. MPC mortar specimens were cast for a measurement of mechanical properties (setting time, compressive strength, tensile/flexural bond strength) and pore structures.Table 1
Chemical composition of magnesia and ordinary Portland cement.
Binder type Oxide composition (%) Ignition loss (%) Fineness (cm2/g) CaO SiO2 Al2O3 Fe2O3 MgO SO3 Magnesia (MgO) 4.1 3.3 0.5 2.2 88.5 0.1 — 5089 OPC 60.0 23.0 5.0 2.0 1.0 2.0 2.1 3120Table 2
Mix proportion of MPC paste/mortar.
Binder Activator Type W/M M/P ratio B/M ratio S/(M + P) MgO KH2PO4 Paste 0.2 1.04.08.012.0 Without borax — 0.02 0.04 0.08 0.10  MgO KH2PO4 Mortar 0.2 1.04.08.012.0 Without borax 1.50 0.02 0.04 0.08 0.10


### 2.2. Testing for Development of MPC

The setting time was determined by the penetration resistance of fresh mortar, measuring periodically its behavior with vicat needles. The initial setting time was determined when penetration depth reached to 25 mm and the final setting time was determined when needle does not mark the specimen surface with a complete circular impression. The size of needle was 50 mm height and 1 mm diameter. The mortar specimen was used in this experiment and the cylinder rubber mould sizedϕ80 × 40 mm was used. Simultaneously the compressive strength of MPC mortar was measured, using a cubic specimen (50 × 50 × 50 mm) at 1-, 3-, 12-, and 24-hour and 28-day curing. The specimen was wrapped to cure at 25°C in a polythene film, immediately after demoulding to avoid leaching-out of ions. The replication of each measurement was 3 and their average value was taken as the value of strength. When it comes to bond strength, tensile and flexural bond strength was simultaneously measured. For the flexural bond strength, the margin of MPC mortar was 50 × 200 × 400 mm, and for the tensile bond strength 50 × 10 × 50 mm, respectively, as given in Figure 1.Figure 1
Schematic for measuring (a) the flexural and (b) tensile bond strength.
(a)
Flexural bond (b)
Tensile bond


### 2.3. Chemistry of MgO Based Cement

The X-ray diffraction (XRD) analysis was used to characterize hydration products in MPC paste. After 28 days of curing, the paste specimen was dried in the oven at 50°C for 48 hours to get rid of the pore water. Then the powder sample was obtained by X-ray diffraction (XRD) analysis, which was conducted by a device D/MAX RINT 2000 with an analyzing range (2θ): 20–70°; scan rate: 4°/min; voltage: 40 kV; current density: 100 mA; tube target: Cu; and wave length: 1.5405 Å (Cu/K-α1), respectively.


### 2.4. Pore Structure

The mercury intrusion porosimetry (MIP) was used to investigate the pore distribution and pore volume of the MPC mortar. A piece of crushed sample was obtained from the middle of the mortar specimen right after the drying process at 50°C for 48 hours. Then the sample was placed in a tube filled with mercury. The obtained sample was initially evacuated to about 50μm mercury and the low pressure was generated up to 0.20 MPa by nitrogen gas. The sample was subsequently imposed by mercury filling pressure ranging from 3.7 × 10−3 to 413 MPa, so that the mercury intrusion volume was recorded at a corresponding pressure. The pore diameter was derived from the pressure using the Washburn equation as given in (1)d=-4γcos⁡θP,where d is the pore diameter (μm); γ is the surface tension (dynes/cm); P is the pressure (MPa); and θ is the contact angle (°) in which the present study took this value as 130°.


### 2.5. Ionic Permeability

The rapid chloride permeability test (RCPT) was used to assess the permeability of MPC concrete compare to that of OPC concrete. This test is based on the standard test method of ASTM C 1202. In this study, however, the mortar specimens were used to minimize the effect of interfacial transition zone (ITZ). A cylinder specimen, 50 mm in thickness and 100 mm in diameter, was connected to two chambers: one was filled with 0.3 M of sodium hydroxide and the other chamber 3.0% of sodium chloride by weight of water to form electrodes. The experimental equipment is shown schematically in Figure2.Figure 2
Setup for rapid chloride ion penetration test.Charged current was calculated by (2) as shown in below, reminding us that if the specimen diameter is other than 95 mm, the charge passed to the established by (3)(2)Q=I0+2·I30+2·I60+2·I90+⋯+2·I300+2·I330+2·I360(3)QS′=QX×95X2,where Q is total charge passed (C), I0 is initial current immediately after voltage is applied (A), and It is current at t min. after voltage applied (A), QS′ is charge passed through specimen diameter of 95 mm (C), QX is charge passed though specimen diameter of X mm (C), and X is diameter of specimens used (mm).


## 2.1. Materials and Specimen Preparation

To assess the mechanical properties of magnesium phosphate cement (MPC) mortar, magnesia was used as a binder, while ordinary Portland cement (OPC) was used for the control. The oxide composition of binders was measured by X-ray fluorescence as given in Table1. The fineness of magnesia and OPC was 5,089 and 3,120 cm2/g, respectively. To activate the hydration process in MPC matrix, potassium dihydrogen phosphate was admixed. The purity of MgO exceeded 88.5% and KH2PO4 exceeded 99.8%. MPC paste specimens were cast for a measurement of X-ray diffraction (XRD) analysis. Mix proportion for MPC paste was varied with MgO/phosphate (M/P) ratio and borax/MgO (B/M) and water/MgO (W/M) was 0.20 (Table 2). To observe the hydration product of MPC, M/P of 4, B/M of 0.08, and W/M of 0.20 were used. MPC mortar specimens were cast for a measurement of mechanical properties (setting time, compressive strength, tensile/flexural bond strength) and pore structures.Table 1
Chemical composition of magnesia and ordinary Portland cement.
Binder type Oxide composition (%) Ignition loss (%) Fineness (cm2/g) CaO SiO2 Al2O3 Fe2O3 MgO SO3 Magnesia (MgO) 4.1 3.3 0.5 2.2 88.5 0.1 — 5089 OPC 60.0 23.0 5.0 2.0 1.0 2.0 2.1 3120Table 2
Mix proportion of MPC paste/mortar.
Binder Activator Type W/M M/P ratio B/M ratio S/(M + P) MgO KH2PO4 Paste 0.2 1.04.08.012.0 Without borax — 0.02 0.04 0.08 0.10  MgO KH2PO4 Mortar 0.2 1.04.08.012.0 Without borax 1.50 0.02 0.04 0.08 0.10


## 2.2. Testing for Development of MPC

The setting time was determined by the penetration resistance of fresh mortar, measuring periodically its behavior with vicat needles. The initial setting time was determined when penetration depth reached to 25 mm and the final setting time was determined when needle does not mark the specimen surface with a complete circular impression. The size of needle was 50 mm height and 1 mm diameter. The mortar specimen was used in this experiment and the cylinder rubber mould sizedϕ80 × 40 mm was used. Simultaneously the compressive strength of MPC mortar was measured, using a cubic specimen (50 × 50 × 50 mm) at 1-, 3-, 12-, and 24-hour and 28-day curing. The specimen was wrapped to cure at 25°C in a polythene film, immediately after demoulding to avoid leaching-out of ions. The replication of each measurement was 3 and their average value was taken as the value of strength. When it comes to bond strength, tensile and flexural bond strength was simultaneously measured. For the flexural bond strength, the margin of MPC mortar was 50 × 200 × 400 mm, and for the tensile bond strength 50 × 10 × 50 mm, respectively, as given in Figure 1.Figure 1
Schematic for measuring (a) the flexural and (b) tensile bond strength.
(a)
Flexural bond (b)
Tensile bond


## 2.3. Chemistry of MgO Based Cement

The X-ray diffraction (XRD) analysis was used to characterize hydration products in MPC paste. After 28 days of curing, the paste specimen was dried in the oven at 50°C for 48 hours to get rid of the pore water. Then the powder sample was obtained by X-ray diffraction (XRD) analysis, which was conducted by a device D/MAX RINT 2000 with an analyzing range (2θ): 20–70°; scan rate: 4°/min; voltage: 40 kV; current density: 100 mA; tube target: Cu; and wave length: 1.5405 Å (Cu/K-α1), respectively.


## 2.4. Pore Structure

The mercury intrusion porosimetry (MIP) was used to investigate the pore distribution and pore volume of the MPC mortar. A piece of crushed sample was obtained from the middle of the mortar specimen right after the drying process at 50°C for 48 hours. Then the sample was placed in a tube filled with mercury. The obtained sample was initially evacuated to about 50μm mercury and the low pressure was generated up to 0.20 MPa by nitrogen gas. The sample was subsequently imposed by mercury filling pressure ranging from 3.7 × 10−3 to 413 MPa, so that the mercury intrusion volume was recorded at a corresponding pressure. The pore diameter was derived from the pressure using the Washburn equation as given in (1)d=-4γcos⁡θP,where d is the pore diameter (μm); γ is the surface tension (dynes/cm); P is the pressure (MPa); and θ is the contact angle (°) in which the present study took this value as 130°.


## 2.5. Ionic Permeability

The rapid chloride permeability test (RCPT) was used to assess the permeability of MPC concrete compare to that of OPC concrete. This test is based on the standard test method of ASTM C 1202. In this study, however, the mortar specimens were used to minimize the effect of interfacial transition zone (ITZ). A cylinder specimen, 50 mm in thickness and 100 mm in diameter, was connected to two chambers: one was filled with 0.3 M of sodium hydroxide and the other chamber 3.0% of sodium chloride by weight of water to form electrodes. The experimental equipment is shown schematically in Figure2.Figure 2
Setup for rapid chloride ion penetration test.Charged current was calculated by (2) as shown in below, reminding us that if the specimen diameter is other than 95 mm, the charge passed to the established by (3)(2)Q=I0+2·I30+2·I60+2·I90+⋯+2·I300+2·I330+2·I360(3)QS′=QX×95X2,where Q is total charge passed (C), I0 is initial current immediately after voltage is applied (A), and It is current at t min. after voltage applied (A), QS′ is charge passed through specimen diameter of 95 mm (C), QX is charge passed though specimen diameter of X mm (C), and X is diameter of specimens used (mm).


## 3. Results and Discussion

### 3.1. Mechanical Properties of MPC

The time to set measured by the penetration resistance is given in Figure3, depending on M/P ratio and B/M ratio. It is evident that an increase in the M/P ratio resulted in an increase in the setting time, irrespective of whether or not borax is admixed. For example, the final setting time at M/P ratio of 1 was 15.38 min, M/P of 4 was 16.97 min, M/P of 8 was 18.10 min, and M/P of 16 was 22.61 min, when borax was not admixed. Xu et al. [12] studied properties of MPC mortar and found that the M/P ratio had a crucial impact to the rate of hydration; the lower M/P ratio leads to higher hydration heat and this help to have higher chemical reactivity. Thus, the setting time would be presumably related to the purity of magnesia. In the present study, the setting time for the magnesia, of which the purity accounted for 88.5%, ranged within 15–22 mins, while the setting time was significantly reduced by the higher purity of magnesia (i.e., 94%) in a previous study [14].Figure 3
Time to final set for MPC mortar depending on the M/P and admixing the borax as a retarder.It is clearly seen that the borax increased the setting time at 0.02–0.08 of B/M ratio. Surprisingly, the MPC mortar at 0.10 of B/M had the lowest setting time. When the ratio of M/P is set to 4, for example, the time to set at 0.02 of B/M was 18.12 min, at 0.04 was 20.51 min, at 0.08 was 23.14 min, and at 0.10 was 17.13 min, respectively. MPC mortar at other M/P had the similar results. To increase the setting time, partial replacement with fly ash, ground granulated blast-furnace slag, or aluminate cement would be alternative to chemical admixture [15–19]. Notwithstanding, the time to set seems still very short, ranging from 16.74 to 34.12 min. In in situ testing, it takes usually 2 to 3 hours to cast and patch immediately after mixing, delivering, pumping and other procedures. Thus, the setting time must be further obtained to be reasonable in in situ testing or other techniques; for example, spraying or rolling must be developed.The compressive strength of MPC mortar was measured at 1, 3, 12, 24, and 672 hours, as given in Figure4. It is seen that an increase in the curing age resulted in an increase in the compressive strength of MPC and control mortar. The compressive strength of MPC is higher than control until 28 days. This is due to high crystallinity of MgKPO4(H2O)6. This is a main hydration product of MPC mortar. The hydration mechanism will be treated in Section 3.2. A development of the compressive strength for MPC specimens was dependent on the M/P ratio. For example, the compressive strength of MPC was 5.47 MPa at 1.0 of M/P ratio and 22.8 MPa at 4.0, the highest strength. Then, the strength was reduced by an increase in the M/P. It may be attributed to the fact that the lower M/P ratio leads to having higher hydration heat and this help to have higher chemical reactivity [12].Figure 4
Development of compressive strength for MPC and control mortar specimens depending on the M/P ratio and curing age without borax.At 4.0 of M/P, the effect of borax on the compressive strength for MPC mortar was examined after 24 hours curing. Simultaneously, the setting time for borax was measured, as given in Figure5. It is clearly seen that an increase in the B/M ratio resulted in a decrease in the compressive strength. For example, the compressive strength of MPC with no borax was 33.00 MPa, 32.67 MPa at 0.02 of B/M, 31.11 MPa at 0.04 of B/M, 29.18 MPa at 0.08 of B/M, and 25.46 MPa at 0.10 of B/M, respectively. However, the borax did not always reduce the rate of hardening process. Until 0.08 of B/M, the setting time was increased, but beyond this level of borax, the setting time was adversely reduced. Thus, a cautious care must be taken in using the borax to increase the setting time.Figure 5
Development of compressive strength and final setting time for MPC mortar admixed with/without borax (B/M of ranging 0 to 0.10) at M/P of 4 and age of 24 hours.The flexural and tensile bond strength measured at 28 days is given in Figure6. The MPC mortar always had higher bond strength both tensile and flexural strength, compared to control mortar patching. For tensile bond, the MPC mortar produced about 1.9 MPa while control mortar achieved 1.5 MPa. The higher level of flexural bon strength was also observed in MPC mortar. The flexural bond strength of MPC was 1.7 MPa while control mortar achieved only 1.2 MPa. Li et al. [17] also investigated the tensile and flexural bond strength found using other type of phosphate such as diammonium phosphate ((NH4)2HPO4) and disodium hydrogen phosphate (Na2HPO4·12H2O) and had almost doubled the higher strength in flexural strength when diammonium phosphate was used, which does not, however, seem suitable due to its environmental issues.Figure 6
Tensile and flexural bond strength of MPC mortar to old substrate, compared to control mortar patching.


### 3.2. Hydration Products

The XRD curve of representative MPC paste (M/P was 4.0 with no borax) after 28 days of curing was obtained as given in Figure7. According to the diffraction peaks, there is a main phase of crystal product that was found in XRD pattern. MgKPO4·6H2O is the main hydration product of MPC paste. Another phase was unreacted magnesia (MgO), which would subsequently react further and could have increased strength. In mechanism of hydration of MPC, the presence of struvite of potassium would be key factor in the reaction products, as struvite can be present in both crystalline and amorphous form. The reaction process is given by following equations [20]: (4)KH2PO4⟶K++H2PO4-KH2PO4⟶K++HPO42-+H+KH2PO4⟶K++PO43-+2H+MgO+H2O⟶MgOH++OH-MgOH++2H2O⟶MgOH2+H3O+MgOH2⟶Mg2++2OH-Mg2++6H2O⟶MgH2O62+K++MgH2O62++PO43-⟶MgKPO4·6H2OFinal  hydration  formFigure 7
X-ray diffraction patterns of MPC paste without borax at M/P ratio of 4 and age of 28 days.


### 3.3. Pore Structure and Ionic Permeability

The pore volume of MPC mortar measured by the mercury intrusion porosimetry is illustrated in Figure8. It is seen that total cumulative pore volume in the MPC mortar was varied with M/P ratio. In fact, an increase in the M/P ratio resulted in an increase in the pore volume. For example, the total cumulative pore volume of MPC at 1.0 of M/P was 0.0759 mL/g, 0.0831 mL/g at 4.0, 0.1107 mL/g at 8.0, and 0.1382 mL/g at 12.0, corresponding to 13.9, 15.5, 20.5, and 25.5% in volume, respectively. The influence of M/P on the porosity may be attributed to pore formation in the process of hydration. In fact, an increase in M/P (i.e., increased magnesia) accompanied an increase in the capillary pore, leading to the entire porosity.Figure 8
Cumulative intrusion of MPC mortar depends on the M/P ratio.The pore volume and distribution of MPC and control mortar measured by the mercury intrusion porosimetry are illustrated in Figure9. It is seen that total pore volume in the MPC mortar accounted for 0.074 mL/g, corresponding to 15.5% in porosity. In fact, this level of porosity is slightly smaller than for OPC mortar ranging within 17–21%. Due to its smaller porosity, MPC mortar gained higher compressive strength in present study. This may be due to high crystalline structure of MgKPO4·6H2O compared to hydration product such as C-S-H in OPC matrix. It can be said that the pore structure of the MPC benefits in raising the durability against degrading environments. For example, the peak intensity at pore diameter for MPC mortar was in the range of 200 to 4,000 nm, entrained air void, imposing the higher resistance to freeze and thaw. Entrained air void buffers the expansion of freezing in pore water to reduce internal stress. In OPC mortar, the peak intensity at pore diameter was in the range of 0.04 to 2 nm, as being equivalent to capillary pore which is related to the ionic transport properties. Moreover, the capillary pores can make internetwork for ionic transport.Figure 9
The cumulative and incremental intrusion of MPC at M/P of 4 and control mortar at 24 days.The current passed through the MPC and OPC cells is plotted with time in Figure10, together with charges passed for the duration. The ionic permeability of the OPC concrete specimen had the higher current and charge, accounting for 4112.0 C, while MPC concrete specimen was 3238.4 C. The MPC concrete produced the higher resistance to ionic transport. A low charge passed in MPC concrete may result from the pore distribution. In OPC mortar, capillary pores mostly occupy the pore constitute, which could form an internetwork for ionic transport. However, in MPC, entrained air void is mainly constituted in the pore structure. According to the guided values for the ionic penetration, both concrete specimens were marked in moderate range as shown in Table 3, presumably due to absence of grave in mix.Table 3
Chloride ion penetrability based on charge passed for concrete specimen (ASTM C 1202-91).
Charge passed (Coulombs) Chloride ion penetrability >4000 High 2000–4000 Moderate 1000–2000 Low 100–1000 Very low <100 NegligibleFigure 10
Charged current with time depending on binder type.


## 3.1. Mechanical Properties of MPC

The time to set measured by the penetration resistance is given in Figure3, depending on M/P ratio and B/M ratio. It is evident that an increase in the M/P ratio resulted in an increase in the setting time, irrespective of whether or not borax is admixed. For example, the final setting time at M/P ratio of 1 was 15.38 min, M/P of 4 was 16.97 min, M/P of 8 was 18.10 min, and M/P of 16 was 22.61 min, when borax was not admixed. Xu et al. [12] studied properties of MPC mortar and found that the M/P ratio had a crucial impact to the rate of hydration; the lower M/P ratio leads to higher hydration heat and this help to have higher chemical reactivity. Thus, the setting time would be presumably related to the purity of magnesia. In the present study, the setting time for the magnesia, of which the purity accounted for 88.5%, ranged within 15–22 mins, while the setting time was significantly reduced by the higher purity of magnesia (i.e., 94%) in a previous study [14].Figure 3
Time to final set for MPC mortar depending on the M/P and admixing the borax as a retarder.It is clearly seen that the borax increased the setting time at 0.02–0.08 of B/M ratio. Surprisingly, the MPC mortar at 0.10 of B/M had the lowest setting time. When the ratio of M/P is set to 4, for example, the time to set at 0.02 of B/M was 18.12 min, at 0.04 was 20.51 min, at 0.08 was 23.14 min, and at 0.10 was 17.13 min, respectively. MPC mortar at other M/P had the similar results. To increase the setting time, partial replacement with fly ash, ground granulated blast-furnace slag, or aluminate cement would be alternative to chemical admixture [15–19]. Notwithstanding, the time to set seems still very short, ranging from 16.74 to 34.12 min. In in situ testing, it takes usually 2 to 3 hours to cast and patch immediately after mixing, delivering, pumping and other procedures. Thus, the setting time must be further obtained to be reasonable in in situ testing or other techniques; for example, spraying or rolling must be developed.The compressive strength of MPC mortar was measured at 1, 3, 12, 24, and 672 hours, as given in Figure4. It is seen that an increase in the curing age resulted in an increase in the compressive strength of MPC and control mortar. The compressive strength of MPC is higher than control until 28 days. This is due to high crystallinity of MgKPO4(H2O)6. This is a main hydration product of MPC mortar. The hydration mechanism will be treated in Section 3.2. A development of the compressive strength for MPC specimens was dependent on the M/P ratio. For example, the compressive strength of MPC was 5.47 MPa at 1.0 of M/P ratio and 22.8 MPa at 4.0, the highest strength. Then, the strength was reduced by an increase in the M/P. It may be attributed to the fact that the lower M/P ratio leads to having higher hydration heat and this help to have higher chemical reactivity [12].Figure 4
Development of compressive strength for MPC and control mortar specimens depending on the M/P ratio and curing age without borax.At 4.0 of M/P, the effect of borax on the compressive strength for MPC mortar was examined after 24 hours curing. Simultaneously, the setting time for borax was measured, as given in Figure5. It is clearly seen that an increase in the B/M ratio resulted in a decrease in the compressive strength. For example, the compressive strength of MPC with no borax was 33.00 MPa, 32.67 MPa at 0.02 of B/M, 31.11 MPa at 0.04 of B/M, 29.18 MPa at 0.08 of B/M, and 25.46 MPa at 0.10 of B/M, respectively. However, the borax did not always reduce the rate of hardening process. Until 0.08 of B/M, the setting time was increased, but beyond this level of borax, the setting time was adversely reduced. Thus, a cautious care must be taken in using the borax to increase the setting time.Figure 5
Development of compressive strength and final setting time for MPC mortar admixed with/without borax (B/M of ranging 0 to 0.10) at M/P of 4 and age of 24 hours.The flexural and tensile bond strength measured at 28 days is given in Figure6. The MPC mortar always had higher bond strength both tensile and flexural strength, compared to control mortar patching. For tensile bond, the MPC mortar produced about 1.9 MPa while control mortar achieved 1.5 MPa. The higher level of flexural bon strength was also observed in MPC mortar. The flexural bond strength of MPC was 1.7 MPa while control mortar achieved only 1.2 MPa. Li et al. [17] also investigated the tensile and flexural bond strength found using other type of phosphate such as diammonium phosphate ((NH4)2HPO4) and disodium hydrogen phosphate (Na2HPO4·12H2O) and had almost doubled the higher strength in flexural strength when diammonium phosphate was used, which does not, however, seem suitable due to its environmental issues.Figure 6
Tensile and flexural bond strength of MPC mortar to old substrate, compared to control mortar patching.


## 3.2. Hydration Products

The XRD curve of representative MPC paste (M/P was 4.0 with no borax) after 28 days of curing was obtained as given in Figure7. According to the diffraction peaks, there is a main phase of crystal product that was found in XRD pattern. MgKPO4·6H2O is the main hydration product of MPC paste. Another phase was unreacted magnesia (MgO), which would subsequently react further and could have increased strength. In mechanism of hydration of MPC, the presence of struvite of potassium would be key factor in the reaction products, as struvite can be present in both crystalline and amorphous form. The reaction process is given by following equations [20]: (4)KH2PO4⟶K++H2PO4-KH2PO4⟶K++HPO42-+H+KH2PO4⟶K++PO43-+2H+MgO+H2O⟶MgOH++OH-MgOH++2H2O⟶MgOH2+H3O+MgOH2⟶Mg2++2OH-Mg2++6H2O⟶MgH2O62+K++MgH2O62++PO43-⟶MgKPO4·6H2OFinal  hydration  formFigure 7
X-ray diffraction patterns of MPC paste without borax at M/P ratio of 4 and age of 28 days.


## 3.3. Pore Structure and Ionic Permeability

The pore volume of MPC mortar measured by the mercury intrusion porosimetry is illustrated in Figure8. It is seen that total cumulative pore volume in the MPC mortar was varied with M/P ratio. In fact, an increase in the M/P ratio resulted in an increase in the pore volume. For example, the total cumulative pore volume of MPC at 1.0 of M/P was 0.0759 mL/g, 0.0831 mL/g at 4.0, 0.1107 mL/g at 8.0, and 0.1382 mL/g at 12.0, corresponding to 13.9, 15.5, 20.5, and 25.5% in volume, respectively. The influence of M/P on the porosity may be attributed to pore formation in the process of hydration. In fact, an increase in M/P (i.e., increased magnesia) accompanied an increase in the capillary pore, leading to the entire porosity.Figure 8
Cumulative intrusion of MPC mortar depends on the M/P ratio.The pore volume and distribution of MPC and control mortar measured by the mercury intrusion porosimetry are illustrated in Figure9. It is seen that total pore volume in the MPC mortar accounted for 0.074 mL/g, corresponding to 15.5% in porosity. In fact, this level of porosity is slightly smaller than for OPC mortar ranging within 17–21%. Due to its smaller porosity, MPC mortar gained higher compressive strength in present study. This may be due to high crystalline structure of MgKPO4·6H2O compared to hydration product such as C-S-H in OPC matrix. It can be said that the pore structure of the MPC benefits in raising the durability against degrading environments. For example, the peak intensity at pore diameter for MPC mortar was in the range of 200 to 4,000 nm, entrained air void, imposing the higher resistance to freeze and thaw. Entrained air void buffers the expansion of freezing in pore water to reduce internal stress. In OPC mortar, the peak intensity at pore diameter was in the range of 0.04 to 2 nm, as being equivalent to capillary pore which is related to the ionic transport properties. Moreover, the capillary pores can make internetwork for ionic transport.Figure 9
The cumulative and incremental intrusion of MPC at M/P of 4 and control mortar at 24 days.The current passed through the MPC and OPC cells is plotted with time in Figure10, together with charges passed for the duration. The ionic permeability of the OPC concrete specimen had the higher current and charge, accounting for 4112.0 C, while MPC concrete specimen was 3238.4 C. The MPC concrete produced the higher resistance to ionic transport. A low charge passed in MPC concrete may result from the pore distribution. In OPC mortar, capillary pores mostly occupy the pore constitute, which could form an internetwork for ionic transport. However, in MPC, entrained air void is mainly constituted in the pore structure. According to the guided values for the ionic penetration, both concrete specimens were marked in moderate range as shown in Table 3, presumably due to absence of grave in mix.Table 3
Chloride ion penetrability based on charge passed for concrete specimen (ASTM C 1202-91).
Charge passed (Coulombs) Chloride ion penetrability >4000 High 2000–4000 Moderate 1000–2000 Low 100–1000 Very low <100 NegligibleFigure 10
Charged current with time depending on binder type.


## 4. Conclusion

In this study, the possibility of MPC mortar for patching in the pavement was assessed by mechanical properties and chemical analysis. The test covers the compressive strength, bond strength to old substrate, and setting time. Simultaneously, its hydration product and ionic transport were examined. To verify the ratio of M/P, the variation in the M/P was considered. The conclusions derived from the experimental works are as follows:(1)
The setting time measured by the penetration resistance using vicat needles to fresh mortar ranged from 15.4 to 34.1 min, depending on the M/P ratio and B/M ratio. An increase in the M/P ratio resulted in an increase in the setting time. For borax, the setting time could be increased up to at 0.08 of B/M, but the setting time was adversely reduced at exceeding this level.(2)
A very rapid development of the compressive strength was achieved within several hours. The strength exceeded 22.8 MPa after 1 hour, 28.0 MPa after 3 hours, and 33.0 MPa after 24 hours at 4.0 of the M/P ratio. However, the compressive strength for MPC mortar was lowered by addition of borax.(3)
The tensile and flexural bond strength to old substrate accounted for 1.9 and 1.7 MPa, respectively, while the bond of OPC mortar patching was about 1.5 and 1.2 MPa, respectively.(4)
The porosity of MPC measured by the mercury intrusion porosimetry was in the range of 13.9 to 25.5%, depending on the M/P ratio. An increase in the M/P ratio resulted in an increase in the porosity, presumably due to hydration degree of magnesia. In particular, the entrained air void was mostly occupied the pore range of the MPC.



---

*Source: 7179403-2016-09-26.xml*