# La Doping of CdS for Enhanced CdS/CdSe Quantum Dot Cosensitized Solar Cells

Authors: Xiaolei Qi; Xiaoping Zou; Sheng He
Journal: Journal of Chemistry
 (2015)

---

## Abstract

CdS/CdSe system of quantum dot cosensitized solar cells (QDCSCs) is one of the most attractive structures for high-efficiency due to its effect of level adjusting. However, the stepwise structure formed between levels of CdS and CdSe has a limitation for enhancing the efficiencies. Metal ions doping in quantum dots have emerged as a common way for changing the Fermi level, band gap, and conductance. Here we report an innovative concept for the rare earth materials La-doped of the CdS layer in the CdS/CdSe QDCSCs by means of the successive ionic layer adsorption and reaction (SILAR). Then we tested that La doped quantum dots can help more electrons accumulate in CdS film, which makes the Fermi level shift up and form a stepped structure. This method leads to enhanced absorption intensity, obviously increasing current density in CdS/CdSe QDCSCs. Our research is a new exploration for improving efficiencies of quantum dot sensitized solar cells.


---

## Body

## 1. Introduction

Emerging new technology of metal ions doping in quantum dots (QDs) has the potential to improve photoelectric conversion efficiency (PCE) of solar cells for the change of Fermi level, band gap, and conductance [1]. Based on this technology, transition metal ion dopant, which has optical activity, such as Mn2+, can change the electronic and optical properties of QDs. Moreover, dopants in the area of middle band gaps of QDs generate electronic states and transform the dynamics of charge separation and recombination. The photoelectric characteristics of semiconductor nanocrystals can also be adjusted by controlling the type and concentration of dopants. In 2008, Lee et al. prepared CdSe and Mg-doped CdSe quantum dots cosensitized solar cells. And compared with the pure CdSe quantum dots sensitized solar cells under the same conditions, the short circuit current of the doped one improved by 47% [2]. In 2013, Lee et al. report on a Hg doping of PbS quantum dots sensitized solar cell with an unprecedentedly high current density of 30 mA/cm2. They also obtained a power conversion efficiency of 5.6% at one sun illumination due to the extremely high current density [3]. Huang et al. of our group studied the properties of Cu-doped-PbS/CdS QDCSCs by changing the doping ratio of Cu2+ and discovered that the ability to capture incident photons of PbS was improved after Cu doping [4]. In contrast to the undoped solar cells, the doped one achieved a high conversion efficiency (2.01%) and a remarkable short circuit current density (21 mA/cm2). Li et al. prepared Cu-doped-CdS/In-doped-CdS quantum dot solar cells by using double doped quantum dot sensitizer, which formed a stepwise structure [5]. The structure was propitious to the electron delivery and collection and led to an improved efficiency. The application of rare earth materials doping in dye sensitized solar cells is a new exploration. Up and down conversion luminescence caused by doping with rare earth ions can enhance the optical trapping and photocurrent in solar cells by expanding the absorption band from visible spectrum to UV infrared region; moreover, the doping effect of rare earth ions raises Fermi level of photoanode, improves photovoltage of cells, and leads to an increased PCE [6–10]. However, up to now, this exploration which has great significance is rare to see. More recently, Wu et al. doped the photoanode of dye sensitized solar cells with rare earth fluoride (YF3 : Eu3+) dopants [11]. This method has significantly increased the PCE of solar cells for dual function of rare earth compounds which includes conversion luminescence and doping effect. In contrast to the undoped system, the PCE of doped solar cells has enhanced 35%.CdS/CdSe system is one of the most popular structures in research field and one of the most efficient QDSCs systems due to the effect of adjusting level. For example, Santra and Kamat employed the CdS/CdSe structure and deposited Mn-doped-CdS/CdSe on mesoporous TiO2 film as the photoanode preparing the QDCSCs, which led to record the standard light intensity short circuit current of 20.7 mA/cm2 and PCE of 5.42% [12]. In the present study, our work was all based on this system. Inspired by the rare earth fluoride doping the photoanode of dye sensitized solar cells, we employed lanthanum (La) doped CdS methodology and assembled the La doping of CdS/CdSe quantum dot cosensitized solar cells which was the first case. Then we analyzed the mechanism about the influences of La dopant on cells by representing photoanode materials and testing performances of solar cells.


## 2. Experimental

### 2.1. Preparation of La-Doped-CdS/CdSe Cosensitized Mesoporous TiO2 Photoanode

In our experiment, deposition process of CdS : La QDs on nanostructured TiO2 surface used the SILAR method. First, 0.1 M Cd(NO3)2·4H2O was dissolved in ethanol using ultrasonic bath for 45 min. Then, LaCl3 was added to the Cd(NO3)2 ethanol solution with corresponding concentration as cation source. Different doping ratios of La3+ : Cd2+ (1 : 10, 1 : 50, 1 : 100, 1 : 200, and undoped) were chosen to compare with each other. Na2S (0.1 M) was dissolved in methanol as anion source. The FTO glass electrode was precoated with transparent active TiO2 layers, which formed a wide band gap semiconductor TiO2 photoanode. Next, we performed the SILAR cycle procedure. The TiO2 photoanode was firstly dipped into metal cation solution for 5 min, rinsed with ethanol, and dried with N2 and then dipped into sulfide anion solution for 5 min, rinsed again with methanol, and dried with N2. Specifically, the anion source was prepared by dissolving Na2SO3 (0.12 M), Se (0.06 M), and a little permutite in deionized water, then refluxing in aqueous condition at 70°C for about 7 hours, and finally filtering out the unreacted Se and permutite [13]. The SILAR processes of CdSe were similar to those of CdS : La QDs. The TiO2/CdS : La photoanode was successively immersed in metal cation (Cd2+) and anion (Se2+) solutions, then rinsed with corresponding solvent, and dried. Finally, the preparation of La-doped-CdS/CdSe cosensitized mesoporous TiO2 photoanode was finished.


### 2.2. Fabrication of QDCSCs

Na2S (1 M) and S (1 M) were dissolved in deionized water as polysulfide electrolyte. Pt counter electrodes were used in our solar cells. Then the La-doped-CdS/CdSe cosensitized TiO2 photoanode, polysulfide electrolyte, and Pt counter electrode were assembled simply. The packaged solar cells should be put for about 40 min and avoid light processing. Then we can perform the testing.


## 2.1. Preparation of La-Doped-CdS/CdSe Cosensitized Mesoporous TiO2 Photoanode

In our experiment, deposition process of CdS : La QDs on nanostructured TiO2 surface used the SILAR method. First, 0.1 M Cd(NO3)2·4H2O was dissolved in ethanol using ultrasonic bath for 45 min. Then, LaCl3 was added to the Cd(NO3)2 ethanol solution with corresponding concentration as cation source. Different doping ratios of La3+ : Cd2+ (1 : 10, 1 : 50, 1 : 100, 1 : 200, and undoped) were chosen to compare with each other. Na2S (0.1 M) was dissolved in methanol as anion source. The FTO glass electrode was precoated with transparent active TiO2 layers, which formed a wide band gap semiconductor TiO2 photoanode. Next, we performed the SILAR cycle procedure. The TiO2 photoanode was firstly dipped into metal cation solution for 5 min, rinsed with ethanol, and dried with N2 and then dipped into sulfide anion solution for 5 min, rinsed again with methanol, and dried with N2. Specifically, the anion source was prepared by dissolving Na2SO3 (0.12 M), Se (0.06 M), and a little permutite in deionized water, then refluxing in aqueous condition at 70°C for about 7 hours, and finally filtering out the unreacted Se and permutite [13]. The SILAR processes of CdSe were similar to those of CdS : La QDs. The TiO2/CdS : La photoanode was successively immersed in metal cation (Cd2+) and anion (Se2+) solutions, then rinsed with corresponding solvent, and dried. Finally, the preparation of La-doped-CdS/CdSe cosensitized mesoporous TiO2 photoanode was finished.


## 2.2. Fabrication of QDCSCs

Na2S (1 M) and S (1 M) were dissolved in deionized water as polysulfide electrolyte. Pt counter electrodes were used in our solar cells. Then the La-doped-CdS/CdSe cosensitized TiO2 photoanode, polysulfide electrolyte, and Pt counter electrode were assembled simply. The packaged solar cells should be put for about 40 min and avoid light processing. Then we can perform the testing.


## 3. Results and Discussion

### 3.1. Influence of Doping Concentration on Solar Cell Performance

We have investigated the effect of diverse doping density on properties of La-doped-CdS/CdSe QDCSCs. The specific experiment parameter and sample calibration used are shown in Table1, among which M-0 represents doping density of La to be zero, namely, undoped, and M-10 represents a 1 : 10 relationship between molarity of La and Cd. And 4+4 represents the total SILAR cycles that four layers of La-doped CdS are deposited firstly, followed by deposition of four layers of CdSe.Table 1
Experiment parameters and sample calibration of different doping concentrations of La doped CdS.
Samples
Doping concentration (La : Cd)
Total SILAR cycles
J
SC (mA/cm2)
V
OC (V)
FF
η (%)
M-0
0
4 + 4
3.88
0.42
0.34
0.54
M-10
1 : 10
4 + 4
5.20
0.43
0.29
0.66
M-50
1 : 50
4 + 4
5.80
0.43
0.27
0.69
M-100
1 : 100
4 + 4
5.79
0.42
0.26
0.66
M-200
1 : 200
4 + 4
5.65
0.40
0.28
0.64Figure1 shows the J-V curves of a range of QDCSCs with samples of diverse doping density from M-0 to M-200. Table 1 shows the specific parameters of solar cells corresponding to Figure 1. In contrast to undoped cell performance, all the doped solar cell parameters are improved a lot, especially the current density. It is easy to get the regularity from Table 1 that current density increases with the reducing La doping ratio then decreases. When La doping ratio is 1 : 50, current density achieves the maximal value (JSC=5.80 mA/cm2); however, open-circuit voltage and fill factor reduce a little. When doping ratio is 1 : 10 or 1 : 50, open-circuit voltage reaches the max (VOC=430 mV). And the fill factor of ratio (1 : 10) is much larger (FF=0.29) than the ratio of 1 : 50. All things considered, when the La doping ratio is 1 : 50, solar cell efficiency reaches the maximum (η=0.69%).Figure 1
TheJ-V curves of different working electrodes based on La-doped CdS. The corresponding parameters are of M-0, M-10, M-50, M-100, and M-200.


### 3.2. Influence of Thickness of Doped CdS on Solar Cell Performance

We have investigated the effect of different SILAR cycles on properties of La-doped-CdS/CdSe QDCSCs based on the optimal doping ratio mentioned in preamble. In this experiment, the doping proportion was chosen as 1 : 50. Furthermore, detailed experiment parameters and sample calibration used are shown in Table2. Then we assembled a range of QDCSCs with samples of different SILAR cycles from S-4 to S-10 and measured the J-V curves and specific parameters of solar cells, respectively (Figure 2 and Table 2). From Table 2, we can find the tendency that, with SILAR cycles of La-doped CdS increasing, current density and fill factor first rise and then decrease. When the SILAR cycles are 6, they all reach the peak value, which are 6.97 mA/cm2 and 0.25. At first, quantum dots increase with the SILAR cycles adding, which can promote generation of photo-induced carriers and consequently lead to current density raising. When the SILAR cycles keep adding, La-CdS layer thickens which makes the transportation path of electrons get longer and increases the electrons loss and finally reduces the current density. However, the open-circuit voltage is ever decreasing, and it achieves the maximal voltage value (0.41 V) as SILAR cycles are 4. On the whole, when the SILAR cycles of La-doped CdS are 6, we attain the highest solar cell efficiency (0.70%).Table 2
Experiment parameters and sample calibration of different SILAR cycles of La doped CdS.
Samples
Doping concentration (La : Cd)
Total SILAR cycles
J
SC (mA/cm2)
V
OC (V)
FF
η (%)
S-4
1 : 50
4 + 4
5.92
0.41
0.21
0.52
S-6
1 : 50
6 + 4
6.97
0.40
0.25
0.70
S-8
1 : 50
8 + 4
6.72
0.37
0.21
0.53
S-10
1 : 50
10 + 4
5.58
0.35
0.18
0.36Figure 2
TheJ-V curves of different working electrodes based on La-doped CdS. The corresponding parameters are of S-4, S-6, S-8, and S-10.Compared with the aforementioned results of different doping concentrations of La-doped CdS, we can find that current density of this experiment enhances slightly, but the open-circuit voltage and fill factor have a greater reduction. As a result, it finally leads to a very small increase in cell efficiency. The voltage reduction is mainly because we have changed the TiO2 slurry and screen used in silk-screen printing in the latter experiments. It results in TiO2 films painted a little thinner than the previous films and a relatively poor uniformity. The fill factor reduction is related to fabrication of Pt counter electrode. Pt slutty painted too little and counter electrode put too long will affect the fill factor.


### 3.3. Mechanism Analysis of La-Doped QDCSCs

First, we performed the materials characterization of La-doped-CdS/CdSe photoanode. Figure3 shows the SEM image of (a) photoanode; we can see the morphology of TiO2 particles about 20 nm size of scale. But it is difficult to observe the morphology of quantum dots by SEM image. Then we performed the characterization of TEM (Figure 4). Figure 3(b) shows the EDS energy spectrum diagram of photoanode. We cannot find La element; it is because the La-doped ratio is 1 : 50 that the amount of dopant La is too little to detect the characteristic X-ray of La element by instrument. So we used the inductively coupled plasma emission spectrometer (ICP-OES) to perform a further qualitative and quantitative analysis of doped elements (shown in Table 3). In this experiment, La doping ratio is 1 : 50; namely, molar concentration of La is 0.02 times molar concentration of Cd2+ in precursor solution (Cd2+ solution). Through the analysis of ICP-OES, we know the actual molar ratio of La : Cd in La-doped-CdS/CdSe photoanode is 1 : 400; namely, the molar concentration of La is 0.0025 times molar concentration of Cd2+ which is only 12.5% of the doping ratio we expected. This result shows that very little of La has doped in CdS.Table 3
ICP-OES quantitative analysis of  La-doped CdS. The doping ratio of La : Cd is 1 : 50 in precursor solution. And the real doping ratio of La : Cd is 1 : 400 which we measured in the table.
Sample
Cd (µg)
La (µg)
La : Cd molar ratio
La-CdS
31.75
0.0982
1 : 400SEM image of photoanode and corresponding EDS energy spectrum diagram: (a) SEM image and (b) EDS energy spectrum.
(a)
(b)The TEM images of La-doped-CdS/CdSe films: (a) low magnification figure and (b) high magnification figure.
(a)
(b)Figure4 shows the TEM micrograph of (a) low magnification figure of photoanode and (b) high magnification figure of rectangular box part which is in (a). We can see nanoparticles about 5–20 nm in Figure 4(a). Observing the high magnification figure we can find that the large particles are TiO2 nanoparticles, and the small particles are La-doped quantum dot sensitizers. The size of small particles is about 5 nm.Figure5 shows the XRD figure of La-doped-CdS/CdSe photoanode. After the deposition of La-doped-CdS and CdSe in photoanode, we can see the diffraction peak of La dopants, in addition to the existing diffraction peak of FTO, TiO2, CdS, and CdSe. When 2θ value is about 47.6°, it is corresponding to the (332) crystal face of La2Se3. Hence, it proves that La dopants really have doped in the photoanode.Figure 5
The XRD patterns of La-doped-CdS/CdSe films.The effect of rare earth materials doping on the optoelectronic properties of the CdS/CdSe is studied by comparing the ultraviolet-visible absorption spectrum of La-doped-CdS(4)/CdSe(4) with that of CdS(4)/CdSe(4) photoanodes, as shown in Figure6. Because the band gap of CdS quantum dot becomes narrow (Figure 10) after doping CdS with La, which can finally enhance the absorption capacity of photoanodes. Compared with the pure CdS(4)/CdSe(4) photoanode, the absorption strength of La-doped-CdS(4)/CdSe(4) photoanode is markedly improved within the wavelength of 350–525 nm; this result is advantageous to improvement of current density of La-doped solar cells.Figure 6
The UV-visible absorption spectra of La-doped-CdS(4)/CdSe(4) and CdS(4)/CdSe(4).In Figure6, we just showed the comparison of the absorption spectrum between La-CdS(4)/CdSe(4) and CdS(4)/CdSe(4) photoanodes. To compare the absorption ability definitely, we performed the UV-Vis absorption spectroscopy of La-CdS/CdSe photoanode of different SILAR cycles, which is shown in Figure 7. When SILAR cycles of La-doped CdS layers were added from 4 to 10 on the condition of fixed SILAR cycles of CdSe layers, the absorption capacity of photoanodes were also increased especially in wavelength of 350–500 nm.Figure 7
UV-Vis absorption spectroscopy of La-CdS/CdSe photoanode of different SILAR cycles.To confirm that doped quantum dots can change the energy level of quantum dots, we have performed the ultraviolet photoelectron spectroscopy test to ascertain the top of valence band of quantum dots. Quantum dots band gap can be obtained by utilizing the absorption spectrum function:αhν2=hν-Eg (α is absorption coefficient, Eg is band gap, and hν is photon energy). According to the band gap and top of valence band, we can calculate the bottom of the conduction band of quantum dots. It can be known that the bottom of the conduction band of TiO2 is 4.20 eV from the Figure 1e of the article “Quantum-Dot-Sensitized Solar Cell with Unprecedentedly High Photocurrent” published by Lee et al. [3].Known from the tangent at photon energy axial intercept in Figure8, the band gaps of TiO2/CdS(6) and TiO2/La-CdS(6) are 2.44 eV and 2.35 eV, respectively. Similarly, known from the tangent at photon energy axial intercept in Figure 9, the top of valence band of TiO2/CdS(6) and that of TiO2/La-CdS(6) are 4.24 eV and 4.02 eV, respectively. Consequently, we can calculate their bottoms of the conduction band which are 1.8 eV and 1.67 eV, respectively. Figure 10 shows the corresponding energy level diagram of La-doped CdS. The band gap of CdS quantum dot becomes narrow; meanwhile, its conduction band and valence band shift up. It is propitious to transport charges inside the solar cells and reduce recombination of electrons and holes, which will cause an increase of photocurrent and consequently a rise of PCE. This is consistent with experimental results.Figure 8
The absorption spectrum around doped CdS calculated by usingαhν2=hν-Eg.Figure 9
The ultraviolet photoelectron spectroscopy around doped CdS.Figure 10
The diagram of La doping to the adjustment of CdS energy level.Figure11 shows IPCE curves of La-doped-CdS(6)/CdSe(4) and CdS(8)/CdSe(4) QDCSCs. According to the previous research of our group [14], when the cycles of CdS are 8, the efficiency of CdS/CdSe QDCSCs reach the maximum value. Therefore, we chose La-doped-CdS(6)/CdSe(4) and CdS(8)/CdSe(4) to compare with each other. When the wavelength is in the range of 350–475 nm, the maximal IPCE value is raised to 63% of La-doped solar cells while the undoped value is 55%. In addition, compared with the undoped IPEC value in the wavelength range of 475–550 nm, the La-doped IPCE value is still a little higher. It is consistent with the above corresponding absorption spectrum. We can see a slightly lowered La-doped IPCE value in the wavelength of 550–700 nm. The reason is that the carreries generated in long wavelength do not effectively transfer to the external circuit.Figure 11
IPCE curves of La-doped-CdS(6)/CdSe(4) and CdS(8)/CdSe(4) QDCSCs.


## 3.1. Influence of Doping Concentration on Solar Cell Performance

We have investigated the effect of diverse doping density on properties of La-doped-CdS/CdSe QDCSCs. The specific experiment parameter and sample calibration used are shown in Table1, among which M-0 represents doping density of La to be zero, namely, undoped, and M-10 represents a 1 : 10 relationship between molarity of La and Cd. And 4+4 represents the total SILAR cycles that four layers of La-doped CdS are deposited firstly, followed by deposition of four layers of CdSe.Table 1
Experiment parameters and sample calibration of different doping concentrations of La doped CdS.
Samples
Doping concentration (La : Cd)
Total SILAR cycles
J
SC (mA/cm2)
V
OC (V)
FF
η (%)
M-0
0
4 + 4
3.88
0.42
0.34
0.54
M-10
1 : 10
4 + 4
5.20
0.43
0.29
0.66
M-50
1 : 50
4 + 4
5.80
0.43
0.27
0.69
M-100
1 : 100
4 + 4
5.79
0.42
0.26
0.66
M-200
1 : 200
4 + 4
5.65
0.40
0.28
0.64Figure1 shows the J-V curves of a range of QDCSCs with samples of diverse doping density from M-0 to M-200. Table 1 shows the specific parameters of solar cells corresponding to Figure 1. In contrast to undoped cell performance, all the doped solar cell parameters are improved a lot, especially the current density. It is easy to get the regularity from Table 1 that current density increases with the reducing La doping ratio then decreases. When La doping ratio is 1 : 50, current density achieves the maximal value (JSC=5.80 mA/cm2); however, open-circuit voltage and fill factor reduce a little. When doping ratio is 1 : 10 or 1 : 50, open-circuit voltage reaches the max (VOC=430 mV). And the fill factor of ratio (1 : 10) is much larger (FF=0.29) than the ratio of 1 : 50. All things considered, when the La doping ratio is 1 : 50, solar cell efficiency reaches the maximum (η=0.69%).Figure 1
TheJ-V curves of different working electrodes based on La-doped CdS. The corresponding parameters are of M-0, M-10, M-50, M-100, and M-200.


## 3.2. Influence of Thickness of Doped CdS on Solar Cell Performance

We have investigated the effect of different SILAR cycles on properties of La-doped-CdS/CdSe QDCSCs based on the optimal doping ratio mentioned in preamble. In this experiment, the doping proportion was chosen as 1 : 50. Furthermore, detailed experiment parameters and sample calibration used are shown in Table2. Then we assembled a range of QDCSCs with samples of different SILAR cycles from S-4 to S-10 and measured the J-V curves and specific parameters of solar cells, respectively (Figure 2 and Table 2). From Table 2, we can find the tendency that, with SILAR cycles of La-doped CdS increasing, current density and fill factor first rise and then decrease. When the SILAR cycles are 6, they all reach the peak value, which are 6.97 mA/cm2 and 0.25. At first, quantum dots increase with the SILAR cycles adding, which can promote generation of photo-induced carriers and consequently lead to current density raising. When the SILAR cycles keep adding, La-CdS layer thickens which makes the transportation path of electrons get longer and increases the electrons loss and finally reduces the current density. However, the open-circuit voltage is ever decreasing, and it achieves the maximal voltage value (0.41 V) as SILAR cycles are 4. On the whole, when the SILAR cycles of La-doped CdS are 6, we attain the highest solar cell efficiency (0.70%).Table 2
Experiment parameters and sample calibration of different SILAR cycles of La doped CdS.
Samples
Doping concentration (La : Cd)
Total SILAR cycles
J
SC (mA/cm2)
V
OC (V)
FF
η (%)
S-4
1 : 50
4 + 4
5.92
0.41
0.21
0.52
S-6
1 : 50
6 + 4
6.97
0.40
0.25
0.70
S-8
1 : 50
8 + 4
6.72
0.37
0.21
0.53
S-10
1 : 50
10 + 4
5.58
0.35
0.18
0.36Figure 2
TheJ-V curves of different working electrodes based on La-doped CdS. The corresponding parameters are of S-4, S-6, S-8, and S-10.Compared with the aforementioned results of different doping concentrations of La-doped CdS, we can find that current density of this experiment enhances slightly, but the open-circuit voltage and fill factor have a greater reduction. As a result, it finally leads to a very small increase in cell efficiency. The voltage reduction is mainly because we have changed the TiO2 slurry and screen used in silk-screen printing in the latter experiments. It results in TiO2 films painted a little thinner than the previous films and a relatively poor uniformity. The fill factor reduction is related to fabrication of Pt counter electrode. Pt slutty painted too little and counter electrode put too long will affect the fill factor.


## 3.3. Mechanism Analysis of La-Doped QDCSCs

First, we performed the materials characterization of La-doped-CdS/CdSe photoanode. Figure3 shows the SEM image of (a) photoanode; we can see the morphology of TiO2 particles about 20 nm size of scale. But it is difficult to observe the morphology of quantum dots by SEM image. Then we performed the characterization of TEM (Figure 4). Figure 3(b) shows the EDS energy spectrum diagram of photoanode. We cannot find La element; it is because the La-doped ratio is 1 : 50 that the amount of dopant La is too little to detect the characteristic X-ray of La element by instrument. So we used the inductively coupled plasma emission spectrometer (ICP-OES) to perform a further qualitative and quantitative analysis of doped elements (shown in Table 3). In this experiment, La doping ratio is 1 : 50; namely, molar concentration of La is 0.02 times molar concentration of Cd2+ in precursor solution (Cd2+ solution). Through the analysis of ICP-OES, we know the actual molar ratio of La : Cd in La-doped-CdS/CdSe photoanode is 1 : 400; namely, the molar concentration of La is 0.0025 times molar concentration of Cd2+ which is only 12.5% of the doping ratio we expected. This result shows that very little of La has doped in CdS.Table 3
ICP-OES quantitative analysis of  La-doped CdS. The doping ratio of La : Cd is 1 : 50 in precursor solution. And the real doping ratio of La : Cd is 1 : 400 which we measured in the table.
Sample
Cd (µg)
La (µg)
La : Cd molar ratio
La-CdS
31.75
0.0982
1 : 400SEM image of photoanode and corresponding EDS energy spectrum diagram: (a) SEM image and (b) EDS energy spectrum.
(a)
(b)The TEM images of La-doped-CdS/CdSe films: (a) low magnification figure and (b) high magnification figure.
(a)
(b)Figure4 shows the TEM micrograph of (a) low magnification figure of photoanode and (b) high magnification figure of rectangular box part which is in (a). We can see nanoparticles about 5–20 nm in Figure 4(a). Observing the high magnification figure we can find that the large particles are TiO2 nanoparticles, and the small particles are La-doped quantum dot sensitizers. The size of small particles is about 5 nm.Figure5 shows the XRD figure of La-doped-CdS/CdSe photoanode. After the deposition of La-doped-CdS and CdSe in photoanode, we can see the diffraction peak of La dopants, in addition to the existing diffraction peak of FTO, TiO2, CdS, and CdSe. When 2θ value is about 47.6°, it is corresponding to the (332) crystal face of La2Se3. Hence, it proves that La dopants really have doped in the photoanode.Figure 5
The XRD patterns of La-doped-CdS/CdSe films.The effect of rare earth materials doping on the optoelectronic properties of the CdS/CdSe is studied by comparing the ultraviolet-visible absorption spectrum of La-doped-CdS(4)/CdSe(4) with that of CdS(4)/CdSe(4) photoanodes, as shown in Figure6. Because the band gap of CdS quantum dot becomes narrow (Figure 10) after doping CdS with La, which can finally enhance the absorption capacity of photoanodes. Compared with the pure CdS(4)/CdSe(4) photoanode, the absorption strength of La-doped-CdS(4)/CdSe(4) photoanode is markedly improved within the wavelength of 350–525 nm; this result is advantageous to improvement of current density of La-doped solar cells.Figure 6
The UV-visible absorption spectra of La-doped-CdS(4)/CdSe(4) and CdS(4)/CdSe(4).In Figure6, we just showed the comparison of the absorption spectrum between La-CdS(4)/CdSe(4) and CdS(4)/CdSe(4) photoanodes. To compare the absorption ability definitely, we performed the UV-Vis absorption spectroscopy of La-CdS/CdSe photoanode of different SILAR cycles, which is shown in Figure 7. When SILAR cycles of La-doped CdS layers were added from 4 to 10 on the condition of fixed SILAR cycles of CdSe layers, the absorption capacity of photoanodes were also increased especially in wavelength of 350–500 nm.Figure 7
UV-Vis absorption spectroscopy of La-CdS/CdSe photoanode of different SILAR cycles.To confirm that doped quantum dots can change the energy level of quantum dots, we have performed the ultraviolet photoelectron spectroscopy test to ascertain the top of valence band of quantum dots. Quantum dots band gap can be obtained by utilizing the absorption spectrum function:αhν2=hν-Eg (α is absorption coefficient, Eg is band gap, and hν is photon energy). According to the band gap and top of valence band, we can calculate the bottom of the conduction band of quantum dots. It can be known that the bottom of the conduction band of TiO2 is 4.20 eV from the Figure 1e of the article “Quantum-Dot-Sensitized Solar Cell with Unprecedentedly High Photocurrent” published by Lee et al. [3].Known from the tangent at photon energy axial intercept in Figure8, the band gaps of TiO2/CdS(6) and TiO2/La-CdS(6) are 2.44 eV and 2.35 eV, respectively. Similarly, known from the tangent at photon energy axial intercept in Figure 9, the top of valence band of TiO2/CdS(6) and that of TiO2/La-CdS(6) are 4.24 eV and 4.02 eV, respectively. Consequently, we can calculate their bottoms of the conduction band which are 1.8 eV and 1.67 eV, respectively. Figure 10 shows the corresponding energy level diagram of La-doped CdS. The band gap of CdS quantum dot becomes narrow; meanwhile, its conduction band and valence band shift up. It is propitious to transport charges inside the solar cells and reduce recombination of electrons and holes, which will cause an increase of photocurrent and consequently a rise of PCE. This is consistent with experimental results.Figure 8
The absorption spectrum around doped CdS calculated by usingαhν2=hν-Eg.Figure 9
The ultraviolet photoelectron spectroscopy around doped CdS.Figure 10
The diagram of La doping to the adjustment of CdS energy level.Figure11 shows IPCE curves of La-doped-CdS(6)/CdSe(4) and CdS(8)/CdSe(4) QDCSCs. According to the previous research of our group [14], when the cycles of CdS are 8, the efficiency of CdS/CdSe QDCSCs reach the maximum value. Therefore, we chose La-doped-CdS(6)/CdSe(4) and CdS(8)/CdSe(4) to compare with each other. When the wavelength is in the range of 350–475 nm, the maximal IPCE value is raised to 63% of La-doped solar cells while the undoped value is 55%. In addition, compared with the undoped IPEC value in the wavelength range of 475–550 nm, the La-doped IPCE value is still a little higher. It is consistent with the above corresponding absorption spectrum. We can see a slightly lowered La-doped IPCE value in the wavelength of 550–700 nm. The reason is that the carreries generated in long wavelength do not effectively transfer to the external circuit.Figure 11
IPCE curves of La-doped-CdS(6)/CdSe(4) and CdS(8)/CdSe(4) QDCSCs.


## 4. Conclusion

In summary, the rare earth materials La-doped-CdS/CdSe QDCSCs were prepared for the first time using SILAR method. The dopants La in solar cells can help to increase the short circuit current. When La doping ratio was 1 : 50, the efficiency of La-doped-CdS(6)/CdSe(4) solar cells reached the maximum value (η=0.70%). In the end, we systematically analyzed the influence of doped quantum dots sensitizer on the performance of CdS/CdSe QDCSCs and the charge transport mechanism inside solar cells. Namely, after La doping of quantum dots, its band gap become narrow, and conduction band and valence band shift up. It was conducive to the transmission of charges inside solar cells, increase of photocurrent, and consequently improvement of PCE. Our work offers a new direction for improving efficiencies of quantum dot sensitized solar cells.



---