# Scalable Deposition of Nanomaterial-Based Temperature Sensors for Transparent and Pervasive Electronics

Authors: Andreas Albrecht; Almudena Rivadeneyra; Marco Bobinger; Jacopo Bonaccini Calia; Florin C. Loghin; Jose F. Salmeron; Markus Becherer; Paolo Lugli; Aniello Falco
Journal: Journal of Sensors
 (2018)

---

## Abstract

This work presents a comparative analysis of materials for planar semitransparent thermocouples fabricated by spray deposition on a flexible substrate. Three different materials are employed to build such devices, analyzing also the effect of the spray order in their final performance. The highest Seebeck coefficient (50.4μV/K) is found for a junction made of carbon nanotubes (CNTs) on top of silver nanowires (AgNWs) whereas its efficiency in terms of power is the lowest because of the higher sheet resistance of the CNTs. In this case, the best combination for energy-harvesting purposes would be poly (3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) and AgNWs, with a power factor of 219 fW/K2. These results prove the feasibility of developing large-scale and cost-effective thermocouples that could be used for sensing or energy-harvesting applications.


---

## Body

## 1. Introduction

Thermoelectric (TE) phenomena have been investigated and employed extensively for more than a century, as they relate two fundamental quantities: electricity and thermal transmission. Among the many TE effects which have been studied and exploited, the two which received a broader attention are the Peltier and Seebeck effects, respectively. These two can be seen as counterparts, since the former explains a temperature gradient due to electrical current flow through dissimilar materials while Seebeck is mainly the potential difference due to a temperature gradient [1].The latter can be employed for the realization of “thermocouples,” ideally defined as the series of two lines of different materials, which generate voltages with opposite signs upon the application of a thermal gradient. By applying a temperature gradient between the junction of the two materials and their extremities, it is possible to measure a potential difference between the single ends, which will be the sum of the voltages generated by each “leg” [2]. A first order mathematical expression of the Seebeck effect for each line is the following:
(1)ΔV=αSΔT,with αS being the material-dependent Seebeck coefficient sometimes also referred to as simple “S.”Since (1) shows a linear dependency between temperature change and resulting voltage, this effect is a well-suited indicator for temperature measurement or energy-harvesting applications. For many material combinations, this relationship is linear, leading to an easy-to-read temperature sensor. In addition to this, a steep curve is preferred, as it represents a thermocouple more sensitive to temperature changes and allows a higher possible resolution. Remarkably, the insurgence of a voltage difference can also be employed to drive an electric load or to charge up an energy accumulator. The usage of TCs for thermal energy-harvesting applications has been driven by materials with very high thermoelectric power, such as bismuth telluride (Bi2Te3) [3]. The ability to convert thermal energy in electricity can be effectively summarized by the dimensionless figure of merit (FoM) ZT, defined as
(2)ZT=αS2σTK,where σ is the electrical conductivity and K is the thermal conductivity [4].Together withαS, these transport parameters are intertwined and are affected by other intrinsic properties of the material, such as carrier concentration and band structure [4]. The FoM also gives clear indications of how more efficient thermocouples can be obtained by either maximizing αS and σ or minimizing K.Nevertheless, these strictly thermoelectrical parameters alone do not suffice to define next generation thermocouples. In fact, the research in the field of the Internet of Things and wearable electronics has been leaning towards the realization of flexible or conformal devices [5], seamlessly integrated in the environment [6], objects [7], or even the human body [8]. Furthermore, conventional thermocouples are built of different metals, metal alloys, or doped semiconductors, which present high ZT values as well as high environmental impact. The deposition of pure metals and inorganic semiconductors is extremely energy intensive [9] and difficult to recycle. One approach towards the substitution of such materials is the realization of novel devices, based on polymers or nanostructured materials. Albeit, at the current state, nanomaterials present lower FoM; they still have a wide margin of improvement, and they possess a number of uncommon qualities, which are not to be found in conventional thermoelectric materials. Nanomaterials are potentially low cost [10], can be obtained through nontoxic production processes [9], can be semitransparent [11], and can be easily processed into various shapes [12, 13] on arbitrary substrates [14, 15].For instance, it is possible to increase theZT values of insulating or semiconducting polymers, through the simple addition of one-dimensional fiber structures, such as carbon nanotubes (CNTs) or conducting nanowires. A composite of polymer and fiber would preserve the low thermal conductivity of a polymer, while it would present an enhanced conductivity, due to the low electrical resistivity of the fiber structure, after reaching a percolation threshold [16]. An interesting example for this class of solutions is the work of Yu et al., in which they demonstrated a great increase of the FoM through adding CNTs into polymer [17].In a similar direction, the employment of conductive nanomaterials (e.g., silver nanowires (AgNWs) [18], poly (3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) [19], and CNTs [20]) can improve the performance of the TCs because of very low heat capacity accompanied by Seebeck coefficients of circa 40 μV/°C [21, 22]. As previously stated, the interest in this class of materials is also due to their potential (semi)transparency. Nanotubes, nanowires, and polymers have been previously employed in many applications, which require a semitransparent conductive layer, such as organic photodiodes [23, 24], solar cells [25], organic light-emitting diodes [26], and transparent heaters [27] as well as power-harvesting applications [28–30].In this work, we exploit all the remarkable properties of solution processable nanomaterials such as scalability and roll-to-roll (R2R) processability at ambient conditions to fabricate novel kinds of semitransparent thermocouples by means of spray deposition. Because of the inherit flexibility of this deposition technique, the novel devices we propose can be integrated straightforwardly and seamlessly onto any transparent surface, enabling the fabrication of semitransparent differential temperature sensors for smart homes and integrated cars or even for the smart lenses of the future.


## 2. Materials and Methods

### 2.1. Materials

For the fabrication of the TC, we tested different combinations of materials, in particular, a custom-made solution of PEDOT:PSS (Clevios PH1000) with 1 g of polymer diluted in 4 g of deionized (DI) water, 10 mg of Dynol 604 (Sigma-Aldrich), and 250 mg of Ethylene glycol (EG), which is employed to increase their conductivity [31]. Before adding PEDOT:PSS, the material was filtered with a pore-size filter of 0.45 μm. The solution was always sonicated for 30 s to disperse agglomerates before spray deposition. For AgNWs, we diluted 1 g of AgNW (ECD0X3from Ras Materials) with 14 g isopropyl alcohol and 5 g deionized (DI) water. The mixture thus produced, the solution was always shaken before using it.The CNTs that we have used are commercially available from Sigma-Aldrich (Product number: 773735). The CNT ink consists of DI water, 90% semiconducting single-walled CNTs (SWCNTs), and sodium dodecyl sulfate (SDS, Sigma-Aldrich), which acts as dispersing agent. The base solution was made by dissolving 1 wt % SDS in DI water. 0.03 wt % of CNTs were added to the solution and treated with a horn sonicator (Branson Sonifier S-450D) for 25 min at a power of 50%. The solution was then centrifuged at 15 krpm for 90 min and the top 80% of the supernatant separated, to be used as the CNT ink [32].


### 2.2. Fabrication Process

To manufacture the TCs, the inks were sprayed through a shadow mask onto a 75μm thick Kapton HN foil with an area of 50 × 50 mm2. We selected the polyimide film because of its high thermal stability to avoid influences of the substrate or its destruction during the measurement. In accordance with the process parameters that we previously tailored for the deposition of AgNWs and CNTs [27, 33], the materials were sprayed to conductive films using a fully automated spray robot PVA350 from Werner Wirth (Germany) equipped with a 781S General Purpose spray valve from Nordson (USA) [18]. Every layer was deposited via mesh-like motion, as shown in Figure 1. The nozzle movement had a speed of 250 mm/s, and the nozzle-to-sample distance was set to 50 mm; the mesh line distance was set to 3 mm. All samples were sprayed with a material pressure of 0.02 MPa and an atomizing pressure of 0.05 MPa. The orifice opening of the nozzle can be manually decreased with a valve (nozzle orifice opening value). The maximum diameter of the nozzle orifice is 0.3 mm. The spraying nozzle was changed when spraying with CNT or AgNW/PEDOT:PSS, with its appropriate gun number, which is written manually on its metal frame. The temperature of the hot plate was also varied when spraying the different materials. In particular, the temperature was set to 65°C for AgNWs, 90°C for PEDOT:PSS, and 80°C for SWCNTs. The spray deposition of a solution implies to be in a wet spraying regime.Figure 1
(a) Schematic of the spray setup. (b) Schematic of the trajectory of the gun over the sample while spraying: one deposited layer consists of spraying the sample in line form on x- and on y-direction. The gun remains at the same distance of the sample during the whole process.
(a)
(b)To speed up the drying of the wet droplets arriving at the substrate, the substrates were left lying on the hot plate. This approach allows the formation of dry layers with good thickness control over time, enhancing at the same time reproducibility [32].Four TCs are fabricated in series (see Figure2(a)), fixing the substrate and the shadow mask (see Figure 2(b)) via small magnets (diameter of 1 mm) on the hot plate of the spray machine. Ten layers of each material were spray deposited, each having its own mask.Figure 2
(a) Dimensions of one TC device containing four TC. The TC legs are all identical, 2.5 mm width and 27.5 mm length. The different colors in the drawing are indicating the different materials: in dark grey the material sprayed first, in light grey the material sprayed seconds, in green the contacts, which were made by the overlapping of both sprayed materials, and in yellowish color the substrate. (b) Layout of the laser-cut mask needed to spray the four TC structures. Two such masks are needed to produce one TC. The first mask is oriented as in the picture. The second mask is the same, rotated by 180°, to be placed superimposing the mask ends in alternate manner. This creates the pattern shown in (a).
(a)
(b)


### 2.3. Characterization

The transmittance spectra were measured from 350 nm to 800 nm using the light from a 300 W Xenon arc lamp from Newport Oriel chopped at 210 Hz, which passes through an Oriel Cornerstone 260 ¼ monochromator and illuminates a calibrated photodiode with a transconductance amplifier connected to an Oriel Merlin digital lock-in amplifier.To quantify the performance of a transparent conducting material, the ratio between the transmission at 550 nm (T10) and the sheet resistance of the film (Rs) is taken. The formula in (3) gives a FoM on conductive films [34].
(3)FoM=T10RS.Sheet resistance was measured at room temperature using a four-point probe head from Jandel connected to a Keysight B2901A source measuring unit.In order to determine the exact thickness of the film, a tactile profilometer measurement is performed with the Bruker’s DektakXT device.A field-emission scanning electron microscope (FESEM) is used for the surface imaging. Therefore, it scans over the surface of the sample with an electron beam exposed to voltages between 1 kV and 30 kV.Infrared images were recorded using a high-resolution calibrated thermal imaging camera (Testo 890, 640 × 480 pixels), which employs bolometric detectors and has a spectral sensitivity window of 7.5–14μm. The emissivity of the thin films was determined by adjusting the temperature measured by the camera to match the temperature on the heated side, which was measured employing a PT100 thermoresistance.A custom-built setup was designed to characterize the flexible transparent TCs. The setup consists of a flat ceramic heater and a Peltier cooler embedded into a low-heat-conductive isolating foam glass. The setup is illustrated in Figure3. The TCs are placed on top of the heater and cooler and pressed down by the top foam glass and a weight. The temperatures at the surface of the TCs are measured by thermoresistors (PT100 from Heraeus M422) mounted at the hot and cold side. Two single-channel programmable power supplies (Keithley 2200) control the heater and cooler. The voltages generated by the TCs are measured by a Keithley 2700 multimeter at an input impedance of 1 MΩ. For all measurements, the temperature was ramped from 27°C to 107°C, corresponding to a maximum temperature difference of 80°C. The setup is automated by LabView 2016.Figure 3
Custom-made setup for the thermoelectrical characterization of the device schematic on the top part, real picture on the bottom. The position of the TC under test is marked in green from (a) side view with lifted top cover and (b) top view without top cover. Reprocessed from original files published in [35].Infrared (IR) images for the thermocouple setup with the heater at a temperature of 300°C are included in the supporting information in FigureS1. Due to the excellent thermal insulation of the foam glass, the generated heat is confined to the heater area. This confinement gives rise to an increase in the temperature gradient and, hence, also an increase in the Seebeck coefficients.


## 2.1. Materials

For the fabrication of the TC, we tested different combinations of materials, in particular, a custom-made solution of PEDOT:PSS (Clevios PH1000) with 1 g of polymer diluted in 4 g of deionized (DI) water, 10 mg of Dynol 604 (Sigma-Aldrich), and 250 mg of Ethylene glycol (EG), which is employed to increase their conductivity [31]. Before adding PEDOT:PSS, the material was filtered with a pore-size filter of 0.45 μm. The solution was always sonicated for 30 s to disperse agglomerates before spray deposition. For AgNWs, we diluted 1 g of AgNW (ECD0X3from Ras Materials) with 14 g isopropyl alcohol and 5 g deionized (DI) water. The mixture thus produced, the solution was always shaken before using it.The CNTs that we have used are commercially available from Sigma-Aldrich (Product number: 773735). The CNT ink consists of DI water, 90% semiconducting single-walled CNTs (SWCNTs), and sodium dodecyl sulfate (SDS, Sigma-Aldrich), which acts as dispersing agent. The base solution was made by dissolving 1 wt % SDS in DI water. 0.03 wt % of CNTs were added to the solution and treated with a horn sonicator (Branson Sonifier S-450D) for 25 min at a power of 50%. The solution was then centrifuged at 15 krpm for 90 min and the top 80% of the supernatant separated, to be used as the CNT ink [32].


## 2.2. Fabrication Process

To manufacture the TCs, the inks were sprayed through a shadow mask onto a 75μm thick Kapton HN foil with an area of 50 × 50 mm2. We selected the polyimide film because of its high thermal stability to avoid influences of the substrate or its destruction during the measurement. In accordance with the process parameters that we previously tailored for the deposition of AgNWs and CNTs [27, 33], the materials were sprayed to conductive films using a fully automated spray robot PVA350 from Werner Wirth (Germany) equipped with a 781S General Purpose spray valve from Nordson (USA) [18]. Every layer was deposited via mesh-like motion, as shown in Figure 1. The nozzle movement had a speed of 250 mm/s, and the nozzle-to-sample distance was set to 50 mm; the mesh line distance was set to 3 mm. All samples were sprayed with a material pressure of 0.02 MPa and an atomizing pressure of 0.05 MPa. The orifice opening of the nozzle can be manually decreased with a valve (nozzle orifice opening value). The maximum diameter of the nozzle orifice is 0.3 mm. The spraying nozzle was changed when spraying with CNT or AgNW/PEDOT:PSS, with its appropriate gun number, which is written manually on its metal frame. The temperature of the hot plate was also varied when spraying the different materials. In particular, the temperature was set to 65°C for AgNWs, 90°C for PEDOT:PSS, and 80°C for SWCNTs. The spray deposition of a solution implies to be in a wet spraying regime.Figure 1
(a) Schematic of the spray setup. (b) Schematic of the trajectory of the gun over the sample while spraying: one deposited layer consists of spraying the sample in line form on x- and on y-direction. The gun remains at the same distance of the sample during the whole process.
(a)
(b)To speed up the drying of the wet droplets arriving at the substrate, the substrates were left lying on the hot plate. This approach allows the formation of dry layers with good thickness control over time, enhancing at the same time reproducibility [32].Four TCs are fabricated in series (see Figure2(a)), fixing the substrate and the shadow mask (see Figure 2(b)) via small magnets (diameter of 1 mm) on the hot plate of the spray machine. Ten layers of each material were spray deposited, each having its own mask.Figure 2
(a) Dimensions of one TC device containing four TC. The TC legs are all identical, 2.5 mm width and 27.5 mm length. The different colors in the drawing are indicating the different materials: in dark grey the material sprayed first, in light grey the material sprayed seconds, in green the contacts, which were made by the overlapping of both sprayed materials, and in yellowish color the substrate. (b) Layout of the laser-cut mask needed to spray the four TC structures. Two such masks are needed to produce one TC. The first mask is oriented as in the picture. The second mask is the same, rotated by 180°, to be placed superimposing the mask ends in alternate manner. This creates the pattern shown in (a).
(a)
(b)


## 2.3. Characterization

The transmittance spectra were measured from 350 nm to 800 nm using the light from a 300 W Xenon arc lamp from Newport Oriel chopped at 210 Hz, which passes through an Oriel Cornerstone 260 ¼ monochromator and illuminates a calibrated photodiode with a transconductance amplifier connected to an Oriel Merlin digital lock-in amplifier.To quantify the performance of a transparent conducting material, the ratio between the transmission at 550 nm (T10) and the sheet resistance of the film (Rs) is taken. The formula in (3) gives a FoM on conductive films [34].
(3)FoM=T10RS.Sheet resistance was measured at room temperature using a four-point probe head from Jandel connected to a Keysight B2901A source measuring unit.In order to determine the exact thickness of the film, a tactile profilometer measurement is performed with the Bruker’s DektakXT device.A field-emission scanning electron microscope (FESEM) is used for the surface imaging. Therefore, it scans over the surface of the sample with an electron beam exposed to voltages between 1 kV and 30 kV.Infrared images were recorded using a high-resolution calibrated thermal imaging camera (Testo 890, 640 × 480 pixels), which employs bolometric detectors and has a spectral sensitivity window of 7.5–14μm. The emissivity of the thin films was determined by adjusting the temperature measured by the camera to match the temperature on the heated side, which was measured employing a PT100 thermoresistance.A custom-built setup was designed to characterize the flexible transparent TCs. The setup consists of a flat ceramic heater and a Peltier cooler embedded into a low-heat-conductive isolating foam glass. The setup is illustrated in Figure3. The TCs are placed on top of the heater and cooler and pressed down by the top foam glass and a weight. The temperatures at the surface of the TCs are measured by thermoresistors (PT100 from Heraeus M422) mounted at the hot and cold side. Two single-channel programmable power supplies (Keithley 2200) control the heater and cooler. The voltages generated by the TCs are measured by a Keithley 2700 multimeter at an input impedance of 1 MΩ. For all measurements, the temperature was ramped from 27°C to 107°C, corresponding to a maximum temperature difference of 80°C. The setup is automated by LabView 2016.Figure 3
Custom-made setup for the thermoelectrical characterization of the device schematic on the top part, real picture on the bottom. The position of the TC under test is marked in green from (a) side view with lifted top cover and (b) top view without top cover. Reprocessed from original files published in [35].Infrared (IR) images for the thermocouple setup with the heater at a temperature of 300°C are included in the supporting information in FigureS1. Due to the excellent thermal insulation of the foam glass, the generated heat is confined to the heater area. This confinement gives rise to an increase in the temperature gradient and, hence, also an increase in the Seebeck coefficients.


## 3. Results and Discussion

### 3.1. Physical Characterization

Figure4 presents a photograph of a manufactured series of four thermocouples made with PEDOT:PSS sprayed on top of AgNWs. The blueish color of PEDOT:PSS appears dark whereas the AgNW is less pronounced. The definition of the patterns is reproducible, and the error in the alignment is almost negligible (less than 1 mm in the worst case) in comparison with the junction area.Figure 4
Picture of thermocouples made of PEDOT:PSS (dark grey) sprayed on top of AgNW (light grey). AgNWs form a milky-white or silver layer and the blue/grey PEDOT:PSS layer overlaps at the contact regions. The hot area is on the right side and the cold area is on the left side similar to the schematic.Thickness was measured against a reference level, the glass substrate itself, obtained by scratching with a thin scalpel a straight line on the film and using the scratch bottom as reference value for the zero-height value. The average thicknesses of the sprayed layers for all nanomaterials were below 300 nm, corresponding to very little material usage. Thickness measurements are not well suited for nanowire and nanotube networks as they possess a low density and only peaks are visible. Scanning electron microscopy (SEM) is more suitable to evaluate the uniformity of the spray deposition. SEM was used to image different parts of the sample and verify the complete coverage of the sample. Figure5 shows illustrative images for each material, emphasising the different sizes of the nanostructures: AgNWs are up to tens of micron long and very stiff; CNTs are shorter than one micron, with a flexible and easy to adapt shape, while PEDOT:PSS constitutes a uniform soft layer.Figure 5
FESEM pictures of (a) AgNWs, (b) CNTs, and (c) PEDOT:PSS spray-deposited films.
(a)
(b)
(c)


### 3.2. Optical Characterization

The transmittance over the visible spectrum (350 nm to 750 nm) are shown in Figure6(a). Here, we see similar transmittance values for CNT and AgNWs, which become more transparent for longer wavelengths. PEDOT:PSS shows the lowest transmittance, and it is characterized by a strong absorption in the red part of the spectrum. As per previous protocols defined in literature, the transmittance value in the maximum sensitivity of the human eye in the green range (550 nm) of the spectrum is considered as reference transmittance, indicating transmittance values of 87%, 90%, and 78% for AgNWs, CNTs, and PEDOT:PSS, respectively. Figure 6(b) illustrates the decrease in the transmittance with the increase in the number of spray-deposited layers. As the purpose of this work is to achieve semitransparent thermocouples, we have to look for a trade-off between sheet resistance and transmittance for each material. Both transmittance and sheet resistance vary according to the thickness. The thicker the layers are, the lower the sheet-resistance result and the lower the transmittances obtained. Therefore, in order to not lose transmittance, the number of layer used to fabricate the thermocouples was set to 10.Figure 6
Transmittance of reference films for the materials used. CNT and AgNW have similar transparency. PEDOT transparency decreases at increasing wavelengths.


### 3.3. Electrical Characterization

The resistivity of AgNW, PEDOT:PSS, and CNT deposited film is presented in Table1. Due to the very high resistivity of CNT compared to the other two films, the resistivity of a full TC is determined by the CNT, when this is part of it.Table 1
Electrical and optical properties of single material thin-film.
Material
T (%) at 550 nm
RS [Ω/sq.]
FoM (%)
AgNW
85
52
45
PEDOT:PSS
76
100
0.650
CNT
89
3.4·104
0.003The measured sheet resistance of 10-layer single material thin films is also included in Table1, showing how this parameter for PEDOT:PSS is two orders of magnitude lower than CNTs and one higher than AgNWs. Combining these numerical value, it is easy to estimate the FoM, equal to 45, 0.56, and 0.003 for AgNWs, PEDOT:PSS, and CNTs, respectively.


### 3.4. Thermoelectric Characterization

The measurement of the open-circuit voltage (Figure7) gave a clearly linear relationship (R2>0.995) to temperature difference between hot and cold junction, for the temperature range used in the tests. As such, the Seebeck coefficient has been estimated as the slope of the curve, neglecting any second-order effect. The transparent TCs presented Seebeck coefficients of 50.4 ± 5.68 μV/K, 26.9 ± 2.87 μV/K, and 14.8 ± 0.83 μV/K for AgNWs-CNTs, CNTs-PEDOT, and AgNWs-PEDOT, respectively. These results are in line with previous literature for nontransparent nanomaterial-based thermocouples and, hence, represent a significant advancement towards the obtainment of transparent electronics. Nevertheless, not only the value is different among different material couples but also the same material couple, when sprayed in a different order results in different thermovoltages. This is particularly true for TC, in which one of the two materials is CNTs. For instance, when AgNWs are sprayed on top of CNTs, the Seebeck coefficient of the TC exhibits a drop of nearly 30%, with respect to the reverse spraying order. An opposite to this phenomenon can be appreciated for the combination PEDOT:PSS and CNTs, in which the TCs with a CNT bottom layer outperform the dual combination. The reasons behind the two behaviours are most likely related to a better electrochemical interface in the most performing combination, due to the sequence of process steps. In the former case, i.e., CNTs on AgNWs, the appropriate interface is guaranteed by the ductility and conformability of the CNTs, which can well entangle the AgNWs. Vice versa, the stiff AgNWs would not be able to conform to the rough surface of the CNTs, leading to poor electrical contact. In the latter case, i.e., PEDOT:PSS on CNTs, the motivation can be found in the solubility of PEDOT:PSS in water. After the deposition of CNTs on top of the polymeric layer, they need to be placed in a water bath to remove the dispersing matrix. By doing so, the CNTs become conductive, while part of the PEDOT:PSS is delaminated because of the contact with water. Finally, in the case of PEDOT:PSS and AgNW thermocouples, there is no difference in the deposition order, although this TC combination presents the lowest VOC (about 15.5 μV/K).Figure 7
Linearity of open-circuit voltage over the temperature difference for thermocouple pairs made with (a) AgNW-CNTs, (b) CNTs-PEDOT:PSS, and (c) AgNW-PEDOT:PSS. The order of mentioning in the legend indicates the spraying order with the second material sprayed after the first one.
(a)
(b)
(c)Table2 presents the average voltage Si¯. The spraying order is indicated in each column, mentioning first the material deposited as bottom layer. We also analyzed the potential of these thermocouples as energy harvesters. For this purpose, we measured resistance values of the series of four thermocouples (also included in Table 2). PEDOT:PSS in combination with AgNWs shows lower resistance. Actually, the higher values obtained by the other TCs are associated to the high sheet-resistance value of the sprayed CNTs. The power factor was estimated as the square of the half of the Seebeck coefficient divided by the resistance (4). These values are included in Table 2. Errors have been calculated as the standard deviation.
(4)PFseries=Sseries/22Rseries=14Sseries2Rseries.Table 2
Series Seebeck coefficient of the four legs of the TCs inμV/K for the three material combinations and the two spraying orders and the mean value of the individual junctions (Si¯). The material mentioned first was sprayed first. The resistance and the resulting power over the four thermocouples are also displayed.
Type
AgNW-CNT
CNT-AgNW
CNT-PEDOT:PSS
PEDOT:PSS-CNT
AgNW-PEDOT:PSS
PEDOT:PSS-AgNW
Si¯ (μV/K)Sseries (μV/K)
50.4 ± 5.68201.7
37.5 ± 1.40149.9
26.9 ± 2.87107.4
13.8 ± 5.5155.1
14.8 ± 0.8358.9
14.3 ± 0.6457.2
Rseries (kΩ)
92.2
90.2
179
222
5.38
3.73
PFseries (fW/K2)
110
62.3
16.1
3.42
161
219It can be seen that the lower output power values are found in those thermocouples with CNTs. This very low values are caused by the high resistance of CNT layers (sheet resistance in the order of tens of kΩ/sq). In contrast with this, the higher output power is achieved by the AgNWs-PEDOT:PSS combination where the sheet resistance is in all cases below 100Ω/sq.Table3 summarizes the Seebeck coefficients obtained in other planar thermocouples reported in literature. As the combination of materials is similar, the Seebeck coefficients do not vary significantly; they are, however, manufactured with high-throughput, large area methods. Albeit remarkable, this result, by itself, does not allow the employability of these printed TCs as energy harvesters because of the high leg-resistance.Table 3
Comparison among planar thermocouples.
Reference
Thermocouple type
Seebeck coefficient (μV/K)
Temperature range (K)
Yu et al. [17]
Doped multiwalled CNT (MWCNT) bundles with metal contact [17]
22
110–300
Penza et al. [22]
CNT bundles with Cr-Al electrodes
40.7
293–343
Miao et al. [38]
Isolated MWCNTs with Pt-electrodes
~35
260–420
This work
AgNWs-SWCNTsSWCNTs-PEDOT:PSSAgNWs-PEDOT:PSS
50.426.914.8
293–273In order to enhance the performance of the CNT-based thermocouples as thermal harvesters, a drastic reduction of the sheet resistance would be necessary. To achieve this, it would be needed to spray more layers with the consequential loss of transparency [36] or by using a third material to improve the junction [37].


## 3.1. Physical Characterization

Figure4 presents a photograph of a manufactured series of four thermocouples made with PEDOT:PSS sprayed on top of AgNWs. The blueish color of PEDOT:PSS appears dark whereas the AgNW is less pronounced. The definition of the patterns is reproducible, and the error in the alignment is almost negligible (less than 1 mm in the worst case) in comparison with the junction area.Figure 4
Picture of thermocouples made of PEDOT:PSS (dark grey) sprayed on top of AgNW (light grey). AgNWs form a milky-white or silver layer and the blue/grey PEDOT:PSS layer overlaps at the contact regions. The hot area is on the right side and the cold area is on the left side similar to the schematic.Thickness was measured against a reference level, the glass substrate itself, obtained by scratching with a thin scalpel a straight line on the film and using the scratch bottom as reference value for the zero-height value. The average thicknesses of the sprayed layers for all nanomaterials were below 300 nm, corresponding to very little material usage. Thickness measurements are not well suited for nanowire and nanotube networks as they possess a low density and only peaks are visible. Scanning electron microscopy (SEM) is more suitable to evaluate the uniformity of the spray deposition. SEM was used to image different parts of the sample and verify the complete coverage of the sample. Figure5 shows illustrative images for each material, emphasising the different sizes of the nanostructures: AgNWs are up to tens of micron long and very stiff; CNTs are shorter than one micron, with a flexible and easy to adapt shape, while PEDOT:PSS constitutes a uniform soft layer.Figure 5
FESEM pictures of (a) AgNWs, (b) CNTs, and (c) PEDOT:PSS spray-deposited films.
(a)
(b)
(c)


## 3.2. Optical Characterization

The transmittance over the visible spectrum (350 nm to 750 nm) are shown in Figure6(a). Here, we see similar transmittance values for CNT and AgNWs, which become more transparent for longer wavelengths. PEDOT:PSS shows the lowest transmittance, and it is characterized by a strong absorption in the red part of the spectrum. As per previous protocols defined in literature, the transmittance value in the maximum sensitivity of the human eye in the green range (550 nm) of the spectrum is considered as reference transmittance, indicating transmittance values of 87%, 90%, and 78% for AgNWs, CNTs, and PEDOT:PSS, respectively. Figure 6(b) illustrates the decrease in the transmittance with the increase in the number of spray-deposited layers. As the purpose of this work is to achieve semitransparent thermocouples, we have to look for a trade-off between sheet resistance and transmittance for each material. Both transmittance and sheet resistance vary according to the thickness. The thicker the layers are, the lower the sheet-resistance result and the lower the transmittances obtained. Therefore, in order to not lose transmittance, the number of layer used to fabricate the thermocouples was set to 10.Figure 6
Transmittance of reference films for the materials used. CNT and AgNW have similar transparency. PEDOT transparency decreases at increasing wavelengths.


## 3.3. Electrical Characterization

The resistivity of AgNW, PEDOT:PSS, and CNT deposited film is presented in Table1. Due to the very high resistivity of CNT compared to the other two films, the resistivity of a full TC is determined by the CNT, when this is part of it.Table 1
Electrical and optical properties of single material thin-film.
Material
T (%) at 550 nm
RS [Ω/sq.]
FoM (%)
AgNW
85
52
45
PEDOT:PSS
76
100
0.650
CNT
89
3.4·104
0.003The measured sheet resistance of 10-layer single material thin films is also included in Table1, showing how this parameter for PEDOT:PSS is two orders of magnitude lower than CNTs and one higher than AgNWs. Combining these numerical value, it is easy to estimate the FoM, equal to 45, 0.56, and 0.003 for AgNWs, PEDOT:PSS, and CNTs, respectively.


## 3.4. Thermoelectric Characterization

The measurement of the open-circuit voltage (Figure7) gave a clearly linear relationship (R2>0.995) to temperature difference between hot and cold junction, for the temperature range used in the tests. As such, the Seebeck coefficient has been estimated as the slope of the curve, neglecting any second-order effect. The transparent TCs presented Seebeck coefficients of 50.4 ± 5.68 μV/K, 26.9 ± 2.87 μV/K, and 14.8 ± 0.83 μV/K for AgNWs-CNTs, CNTs-PEDOT, and AgNWs-PEDOT, respectively. These results are in line with previous literature for nontransparent nanomaterial-based thermocouples and, hence, represent a significant advancement towards the obtainment of transparent electronics. Nevertheless, not only the value is different among different material couples but also the same material couple, when sprayed in a different order results in different thermovoltages. This is particularly true for TC, in which one of the two materials is CNTs. For instance, when AgNWs are sprayed on top of CNTs, the Seebeck coefficient of the TC exhibits a drop of nearly 30%, with respect to the reverse spraying order. An opposite to this phenomenon can be appreciated for the combination PEDOT:PSS and CNTs, in which the TCs with a CNT bottom layer outperform the dual combination. The reasons behind the two behaviours are most likely related to a better electrochemical interface in the most performing combination, due to the sequence of process steps. In the former case, i.e., CNTs on AgNWs, the appropriate interface is guaranteed by the ductility and conformability of the CNTs, which can well entangle the AgNWs. Vice versa, the stiff AgNWs would not be able to conform to the rough surface of the CNTs, leading to poor electrical contact. In the latter case, i.e., PEDOT:PSS on CNTs, the motivation can be found in the solubility of PEDOT:PSS in water. After the deposition of CNTs on top of the polymeric layer, they need to be placed in a water bath to remove the dispersing matrix. By doing so, the CNTs become conductive, while part of the PEDOT:PSS is delaminated because of the contact with water. Finally, in the case of PEDOT:PSS and AgNW thermocouples, there is no difference in the deposition order, although this TC combination presents the lowest VOC (about 15.5 μV/K).Figure 7
Linearity of open-circuit voltage over the temperature difference for thermocouple pairs made with (a) AgNW-CNTs, (b) CNTs-PEDOT:PSS, and (c) AgNW-PEDOT:PSS. The order of mentioning in the legend indicates the spraying order with the second material sprayed after the first one.
(a)
(b)
(c)Table2 presents the average voltage Si¯. The spraying order is indicated in each column, mentioning first the material deposited as bottom layer. We also analyzed the potential of these thermocouples as energy harvesters. For this purpose, we measured resistance values of the series of four thermocouples (also included in Table 2). PEDOT:PSS in combination with AgNWs shows lower resistance. Actually, the higher values obtained by the other TCs are associated to the high sheet-resistance value of the sprayed CNTs. The power factor was estimated as the square of the half of the Seebeck coefficient divided by the resistance (4). These values are included in Table 2. Errors have been calculated as the standard deviation.
(4)PFseries=Sseries/22Rseries=14Sseries2Rseries.Table 2
Series Seebeck coefficient of the four legs of the TCs inμV/K for the three material combinations and the two spraying orders and the mean value of the individual junctions (Si¯). The material mentioned first was sprayed first. The resistance and the resulting power over the four thermocouples are also displayed.
Type
AgNW-CNT
CNT-AgNW
CNT-PEDOT:PSS
PEDOT:PSS-CNT
AgNW-PEDOT:PSS
PEDOT:PSS-AgNW
Si¯ (μV/K)Sseries (μV/K)
50.4 ± 5.68201.7
37.5 ± 1.40149.9
26.9 ± 2.87107.4
13.8 ± 5.5155.1
14.8 ± 0.8358.9
14.3 ± 0.6457.2
Rseries (kΩ)
92.2
90.2
179
222
5.38
3.73
PFseries (fW/K2)
110
62.3
16.1
3.42
161
219It can be seen that the lower output power values are found in those thermocouples with CNTs. This very low values are caused by the high resistance of CNT layers (sheet resistance in the order of tens of kΩ/sq). In contrast with this, the higher output power is achieved by the AgNWs-PEDOT:PSS combination where the sheet resistance is in all cases below 100Ω/sq.Table3 summarizes the Seebeck coefficients obtained in other planar thermocouples reported in literature. As the combination of materials is similar, the Seebeck coefficients do not vary significantly; they are, however, manufactured with high-throughput, large area methods. Albeit remarkable, this result, by itself, does not allow the employability of these printed TCs as energy harvesters because of the high leg-resistance.Table 3
Comparison among planar thermocouples.
Reference
Thermocouple type
Seebeck coefficient (μV/K)
Temperature range (K)
Yu et al. [17]
Doped multiwalled CNT (MWCNT) bundles with metal contact [17]
22
110–300
Penza et al. [22]
CNT bundles with Cr-Al electrodes
40.7
293–343
Miao et al. [38]
Isolated MWCNTs with Pt-electrodes
~35
260–420
This work
AgNWs-SWCNTsSWCNTs-PEDOT:PSSAgNWs-PEDOT:PSS
50.426.914.8
293–273In order to enhance the performance of the CNT-based thermocouples as thermal harvesters, a drastic reduction of the sheet resistance would be necessary. To achieve this, it would be needed to spray more layers with the consequential loss of transparency [36] or by using a third material to improve the junction [37].


## 4. Conclusions

We have demonstrated the feasibility of producing spray-deposited, large-scale, and semitransparent thermocouples on flexible substrates. These thermocouples show Seebeck coefficients of up to 54μV/K and a very linear response, being a perfect candidate for autonomous temperature sensing. The best combination in terms of Seebeck coefficient was found for the junction made of AgNWs and CNTs, depositing them in the mentioned order. The achievement of such semitransparent devices, easy to integrate into other systems with means of conventional solution-processing methods, is a first step towards transparent electronic devices, seamlessly integrated into windows or windshields. Finally, although further work is still necessary to overcome the current limitations, such as the high resistance, which hinders the use as energy harvesters, the methods we describe in this work, coupled with a choice of materials more tailored to the applications, can be generalised and employed for the realization of thermally sensitive electronics, where transparency, cost effectiveness, and ease of process are required.



---

*Source: 7102069-2018-10-31.xml*