# Valorization of Waste Chicken Feathers: Fabrication and Characterization of Novel Keratin Nanofiber Conduits for Potential Application in Peripheral Nerve Regeneration

Authors: Mduduzi Khumalo; Bruce Sithole; Tamrat Tesfaye; Prabashni Lekha
Journal: Journal of Nanomaterials
 (2022)

---

## Abstract

Flexible, porous, biocompatible, and biodegradable tubular keratin nanofibers were fabricated as nerve regeneration conduits. Keratin was extracted from waste chicken feathers and then blended with polyvinyl alcohol and transformed into nanofiber conduits by electrospinning. The nanofiber conduits had average diameters that ranged from 170 to 234 nm. The nanofibers’ average diameter decreased when the keratin content was increased. In contrast, the range of nanofiber diameter distribution narrowed, suggesting that as nanofibers became thin, their numbers increased, thus reducing the interfacial spaces between them. The analysis confirmed the presence of keratin protein in nanofibers, guaranteeing biocompatibility and biodegradation. TGA showed that keratin improved the thermal stability and hydrophilicity of the nanofibers.


---

## Body

## 1. Introduction

The peripheral nervous system (PNS) is an integral part of the nervous system that enables the body to move muscles and feel normal sensations. Its primary function is to connect the central nervous system (CNS) to tissues and organs [1]. The role of PNS is made possible by central nervous system basic units, called neurons, which are composed of, among others, the bundles of axons that form electric-cable-like peripheral nerves. Unlike CNS protected by the skull and vertebrae, the PNS is exposed to injuries that can either be neuropraxia, axonotmesis, or neurotmesis, where neuropraxia is the least severe, while neurotmesis is the most severe nerve injury [2]. The complicated anatomy of the nerve bundle makes nerve repair difficult, leading to the most unsuccessful treatments. Peripheral nerve injuries remain a challenge for both clinically and basic research despite the advancements that have been made in this field [3]. Current repair methods include end-to-end repair, grafts, and synthetic conduits. While end-to-end suturing, extending, and reconnecting the distal stump to the proximal stump are the simplest and preferred nerve repair method, its success is limited to the gap size and the proximal nerve’s availability stump. Furthermore, it is also limited to the amount of tension induced during stump extension over a nerve gap; if it exceeds the optimal level, the repair process results in partial nerve recovery. The treatment may be done by donating the nerve from the other part of the body, autograft. The autograft is advantageous in eliminating or minimizing immunological rejection and is considered the reference standard for closing the nerve gap [4]. However, the balance of functionality between the donor and recipient tissue or organ must be established. This balance limits the treatment if there is a substantial loss of nervous tissue that may require multiple small grafts. Another form of nerve donation treatment is an allograft, whereby the nerve tissue is harvested from the donor of the same species. Even though this process increases nerve tissue availability, it also introduces the chances of disease transmission and immunological response [1, 5].Therefore, synthetic nerve conduits are favoured for the nerve regeneration process because of their flexibility in mimicking the natural nervous tissue. However, the current commercially available conduits are rigid and inflexible and may cause cell loss due to their lack of physiological properties required during nervous tissue movement [6]. The conduit must be biocompatible, biodegradable, porous, bioresorbable, and mechanically strong [7].Biocompatible synthetic polymers suit most nerve conduits’ fundamental requirements because of their adequate mechanical strength, ductility, and physiochemical compatibility, especially electrospun nanofiber scaffolds [8–10]. Nanofibers have attracted attention for their application as nerve conduits due to their softness, flexibility, high porosity, high surface area to volume ratio, and nanoscale diameter [11, 12]. Research has shown that nanofiber scaffolds support cellular ingrowth due to their ability to mimic the native tissue or organ [13, 14]. Nanofibers can be electrospun into tubular forms that are flexible and soft to allow easy suturing of the distal and proximal stump during nerve repair. Furthermore, their porous nanostructure substrate for cell attachment allows nutrient exchange [5].While biocompatible polymers have been used to fabricate electrospun nanofiber conduits [15], there is still a need for biodegradable polymers derived from natural resources to increase biocompatibility and lower immunological rejection. Among other synthetic polymers, polyvinyl alcohol (PVA) has been used in biomedical applications, including nerve repair treatment, due to its physical and chemical properties. Polyvinyl alcohol is FDA approved for clinical use in humans, and it has good electrospinnability to form nontoxic nanofibers with large pore sizes. However, cell adhesion for cell growth and biocompatibility need improvement [16, 17]. Consequently, keratin has been used with PVA to increase scaffold biocompatibility. As a biodegradable fibrous protein, keratin can act as an extracellular matrix and promote biocompatibility to minimize immunological rejection. This protein has attracted interest from both scientific and industrial communities due to its exceptional properties and abundance. Interest includes investigating keratin application in the biomedical field. Feng et al. [18] developed keratin films to treat the corneal epithelial wound. It was then concluded that the keratin films were promising alternatives to the amniotic membrane for ocular surface reconstruction; the films support proliferation, migration, adhesion, and differentiation of human corneal epithelial cells. The protein can also be used to exfoliate molybdenum disulphide (MoS2) to achieve high-quality dispersion of nanolayered MoS2 with a high yield of about 56%. The produced nanolayered sheet has a long shelf-life and improved electrical conductivity [19]. In another study, the effect of transglutaminase on wool keratin films showed a decrease in elongation at break and an increase in tensile strength, thus improving film stability while conserving drug release rate [20]. Further investigation by Ajay Sharma et al. [21] showed that keratin hydrogels could be used as a scaffold for pulp-dentine regeneration since keratin enhanced odontoblast cell behaviour. Choi et al. [22] developed keratin-based nanofibers with high optical transmittance of 88% at 600 nm with improved mechanical properties. Guo et al. [16] used oxidative hair keratin nanoparticles to coat PVA nanofibers for nerve repair, whereby large pore size enhanced neural cell viability and proliferation. Sierpinski et al. [23] produced a biomedical hair-keratin gel and concluded that it promotes vigorous nerve regeneration response by activating Schwann cells. Keratin inclusion facilitates the treatment result comparable to the gold standard conduit, the autograft. Similar results were observed with the application of hydrogel conduit filled with hair keratin for nerve regeneration, in which results were also comparable to the gold standard for nerve repair [24].Therefore, the current study is aimed at fabricating and characterizing the seamless nanofiber conduit of polyvinyl alcohol and chicken feather keratin to apply in nerve regeneration.


## 2. Methodology and Materials

White chicken feathers were collected from the chicken meat processing plant RCL Foods at Hammarsdale, South Africa. Analytical grade sodium bisulphite, sodium hydroxide, sodium dodecyl sulphate, urea, and polyvinyl alcohol were purchased from Sigma-Aldrich, South Africa. The fabrication of seamless nanofiber conduits was done using Nano Spinner NE200 from Inovenso. The main instruments that were used for analysis were Fourier transform infrared spectroscopy (FTIR), Simultaneous Thermographic Analyzer (STA) 6000, and Carbon, Hydrogen, Nitrogen, Sulphur, and Oxygen (CHNS/O) Analyzer (Series II 2400) from PerkinElmer. Experiments, including keratin extraction, fabricating nanofibers and characterizations such as CHNS, were carried in triplicate, while the sample size of diameter measurements of nanofibers was 100.


### 2.1. Pretreatment of Chicken Feathers

Wet chicken feathers were rinsed with water at 60°C to remove excess blood while manually removing other meat by-products and then autoclaved at a temperature of 121°C and pressure 120 kPa for 30 minutes. After that, they were soaked in 0.5%v/vsodium hypochlorite for 24 hours before rinsing with water and dried at 25°C.


### 2.2. Extraction and Analysis of Chicken Feather Keratin

Cleaned-disinfected chicken feathers were ground in a milling machine to increase the dissolution rate during the extraction process. They were then soaked in 99% ethanol for 24 hours to remove fatty materials and rinsed with water before drying at 50°C for three days. Fifteen grams of dry and degreased chicken feathers was deep in a solution of 0.23 M sodium bisulphite, 0.07 M sodium dodecyl sulphate, and 1.5 M urea. The reaction mixture was shaken on a linear platform shaker for homogeneous distribution of all mixture components in a container and then heated in a 90°C oil bath. After cooking, the mixture was centrifuged at 9000 rpm for 15 minutes and filtered to separate the insoluble materials and supernatants. The filtrate obtained was dialyzed in distilled water using cellulose membrane dialysis tubes (MWCO 3.5 kDa) for five days. The keratin solution was lyophilized to obtain keratin powder, sealed, and stored in a cold room at 4°C.


### 2.3. Preparation for Electrospinning Solutions

Solutions of various ratios of 0/100 to 30/70 of keratin/polyvinyl alcohol (K/PVA), at a constant concentration of 12 wt%, were prepared by initially dissolving chicken feather keratin in deionized water, stirred at 50°C while adding about two drops of 1 M NaOH, and then cooled to room temperature. Polyvinyl alcohol was slowly added into the solution while stirring and further stirred for 30 minutes; the temperature increased to 80°C for 2 hours before cooling to room temperature. The conductivity of the solutions was measured using Metrohm 914 pH/conductometer, and the average of three measurements per solution was recorded. The solutions were then ready for electrospinning.


### 2.4. Fabrication of Seamless Nanofiber Conduits

Each electrospinning solution was placed in a 10 ml polyurethane (PU) syringe; the syringe was then connected by a tube to a nanospinner nozzle of 0.8 mm inside diameter. The electrospinning parameters were set to 30 kV, 20 cm nozzle-collector distance, 3 ml/hour feed rate, and a collector rotation speed of 52 cm/s.


### 2.5. Characterization of Nanofiber Conduits

#### 2.5.1. Fourier Transform Infrared Spectroscopy (FTIR)

Functional groups of the keratin, polyvinyl alcohol, and nanofibers were analyzed using Fourier transform infrared spectroscopy (Frontier Universal model, from PerkinElmer) in an attenuated total reflection mode (ATR). Each sample was scanned four times at a wavenumber range of 550–4000 cm-1 with a resolution of 4 cm-1.


#### 2.5.2. CHNS Analysis for Crude Protein Content in Nanofibers

Protein content in nanofibers was done using a CHNS/O analyzer, which determines the content of carbon, hydrogen, nitrogen, and sulphur in the sample. After that, the protein content is calculated by multiplying the nitrogen content by a crude protein conversion factor of 6.25 [25].


#### 2.5.3. Scanning Electron Microscopy (SEM)

Scanning electron microscopy was used to determine morphological properties of nanofiber conduits such as shape, diameter, porosity, smoothness, and beads. Samples were set up on a metal stub using a sticky carbon disc; they were then gold-coated using a sputter coater before being placed in the ZEISS LEO 1450 Scanning Electron Microscope for imaging. Image-Pro Plus software was then used to analyze the diameters of 100 nanofibers.


#### 2.5.4. Thermal Gravimetric Analysis

Thermophysical properties were investigated using a thermal gravimetric analyzer at a heating rate of 30°C/min from 30 to 600°C.


## 2.1. Pretreatment of Chicken Feathers

Wet chicken feathers were rinsed with water at 60°C to remove excess blood while manually removing other meat by-products and then autoclaved at a temperature of 121°C and pressure 120 kPa for 30 minutes. After that, they were soaked in 0.5%v/vsodium hypochlorite for 24 hours before rinsing with water and dried at 25°C.


## 2.2. Extraction and Analysis of Chicken Feather Keratin

Cleaned-disinfected chicken feathers were ground in a milling machine to increase the dissolution rate during the extraction process. They were then soaked in 99% ethanol for 24 hours to remove fatty materials and rinsed with water before drying at 50°C for three days. Fifteen grams of dry and degreased chicken feathers was deep in a solution of 0.23 M sodium bisulphite, 0.07 M sodium dodecyl sulphate, and 1.5 M urea. The reaction mixture was shaken on a linear platform shaker for homogeneous distribution of all mixture components in a container and then heated in a 90°C oil bath. After cooking, the mixture was centrifuged at 9000 rpm for 15 minutes and filtered to separate the insoluble materials and supernatants. The filtrate obtained was dialyzed in distilled water using cellulose membrane dialysis tubes (MWCO 3.5 kDa) for five days. The keratin solution was lyophilized to obtain keratin powder, sealed, and stored in a cold room at 4°C.


## 2.3. Preparation for Electrospinning Solutions

Solutions of various ratios of 0/100 to 30/70 of keratin/polyvinyl alcohol (K/PVA), at a constant concentration of 12 wt%, were prepared by initially dissolving chicken feather keratin in deionized water, stirred at 50°C while adding about two drops of 1 M NaOH, and then cooled to room temperature. Polyvinyl alcohol was slowly added into the solution while stirring and further stirred for 30 minutes; the temperature increased to 80°C for 2 hours before cooling to room temperature. The conductivity of the solutions was measured using Metrohm 914 pH/conductometer, and the average of three measurements per solution was recorded. The solutions were then ready for electrospinning.


## 2.4. Fabrication of Seamless Nanofiber Conduits

Each electrospinning solution was placed in a 10 ml polyurethane (PU) syringe; the syringe was then connected by a tube to a nanospinner nozzle of 0.8 mm inside diameter. The electrospinning parameters were set to 30 kV, 20 cm nozzle-collector distance, 3 ml/hour feed rate, and a collector rotation speed of 52 cm/s.


## 2.5. Characterization of Nanofiber Conduits

### 2.5.1. Fourier Transform Infrared Spectroscopy (FTIR)

Functional groups of the keratin, polyvinyl alcohol, and nanofibers were analyzed using Fourier transform infrared spectroscopy (Frontier Universal model, from PerkinElmer) in an attenuated total reflection mode (ATR). Each sample was scanned four times at a wavenumber range of 550–4000 cm-1 with a resolution of 4 cm-1.


### 2.5.2. CHNS Analysis for Crude Protein Content in Nanofibers

Protein content in nanofibers was done using a CHNS/O analyzer, which determines the content of carbon, hydrogen, nitrogen, and sulphur in the sample. After that, the protein content is calculated by multiplying the nitrogen content by a crude protein conversion factor of 6.25 [25].


### 2.5.3. Scanning Electron Microscopy (SEM)

Scanning electron microscopy was used to determine morphological properties of nanofiber conduits such as shape, diameter, porosity, smoothness, and beads. Samples were set up on a metal stub using a sticky carbon disc; they were then gold-coated using a sputter coater before being placed in the ZEISS LEO 1450 Scanning Electron Microscope for imaging. Image-Pro Plus software was then used to analyze the diameters of 100 nanofibers.


### 2.5.4. Thermal Gravimetric Analysis

Thermophysical properties were investigated using a thermal gravimetric analyzer at a heating rate of 30°C/min from 30 to 600°C.


## 2.5.1. Fourier Transform Infrared Spectroscopy (FTIR)

Functional groups of the keratin, polyvinyl alcohol, and nanofibers were analyzed using Fourier transform infrared spectroscopy (Frontier Universal model, from PerkinElmer) in an attenuated total reflection mode (ATR). Each sample was scanned four times at a wavenumber range of 550–4000 cm-1 with a resolution of 4 cm-1.


## 2.5.2. CHNS Analysis for Crude Protein Content in Nanofibers

Protein content in nanofibers was done using a CHNS/O analyzer, which determines the content of carbon, hydrogen, nitrogen, and sulphur in the sample. After that, the protein content is calculated by multiplying the nitrogen content by a crude protein conversion factor of 6.25 [25].


## 2.5.3. Scanning Electron Microscopy (SEM)

Scanning electron microscopy was used to determine morphological properties of nanofiber conduits such as shape, diameter, porosity, smoothness, and beads. Samples were set up on a metal stub using a sticky carbon disc; they were then gold-coated using a sputter coater before being placed in the ZEISS LEO 1450 Scanning Electron Microscope for imaging. Image-Pro Plus software was then used to analyze the diameters of 100 nanofibers.


## 2.5.4. Thermal Gravimetric Analysis

Thermophysical properties were investigated using a thermal gravimetric analyzer at a heating rate of 30°C/min from 30 to 600°C.


## 3. Results and Discussions

### 3.1. Extraction and Characterization of Keratin

White chicken feathers were obtained after pretreatment. The increased whiteness index of feathers was due to removing brown-yellow oil and fats. The index further advanced after degreasing with ethanol. After that, a mixture of an aqueous solution and chicken feather particles was recovered after 4 hours of cooking. The final purification steps resulted in light brown supernatant and keratin powder after filtration and freeze-drying, respectively. Figure1 contains the extracted keratin molecular weight’s sodium dodecyl sulphate polyacrylamide gel electrophoresis (SDS-PAGE) analysis.Figure 1
SDS-PAGE gels of extracted keratin protein: glycine gel (a) and tricine gel (b).It shows that the extracted keratin has molecular weights that range from about 3 kDa to approximately 60 kDa, whereas the broad, intense band between 10 and 15 kDa indicates that multiple monomers have a molecular weight of 10-15 kDa range [26].FTIR’s functional groups’ qualitative analysis confirmed the presence of polypeptide amides, namely, amide A, amide B, amide I, amide II, and amide III represented by the absorbance peaks at 3280.79 mc-1, 2919.88 mc-1, 1633.74 mc-1, 1532.24 mc-1, and 1212.05 mc-1, respectively [27]. Furthermore, the extracted keratin elemental analysis showed that this keratin has 5.02% sulphur, 46.64% carbon, 10.82% nitrogen, 7.72% hydrogen, and 29.74% other elements, including oxygen. The extract is composed of 67.63% protein, calculated from the nitrogen percentage in the hydrolysate.


### 3.2. Preparation and Characterization of Keratin/PVA Nanofibers

The prepared electrospinning solutions of various ratios of keratin and PVA, from 00/100 to 30/70, were homogeneous and had a pH of 8 at 24.1°C. The graph in Figure2 shows the effect of keratin content in the electrospinning solution.Figure 2
Conductivity of keratin/PVA solutions of different keratin and polyvinyl alcohol ratios.The conductivity of electrospinning solutions increased with an increase in keratin content. The increase in conductivity may be due to polar amino acids in keratin. The morphology of keratin/PVA nanofibers with different keratin contents from 0% to 30% is shown in Figure3. All nanofibers were cylindrical and became thinner as keratin content was increased. As keratin content increases, the conductivity of the spinning solution increases.Figure 3
SEM images and distributions of nanofiber diameters of the keratin/polyvinyl alcohol system: (a) 0% keratin/100% PVA, (b) 10% K/90% PVA, (c) 20% K/80% PVA, and (d) 30% K/70% PVA.
(a)(b)(c)(d)The increase in conductivity increases the polymer jet’s electrical charge, increases the electric field force, and results in thinner jets and nanofibers and smaller fiber diameters. In addition to greater electric field strength, increasing conductivity decreases the solution’s viscosity, resulting in smaller nanofiber’s average diameters. However, there was no noticeable change in the individual nanofibers’ cross-sectional shape from 100%bPVA to 90% PVA nanofibers, as shown in Figure4.Figure 4
SEM images of keratin nanofibers: (a) tubular structure and (b) the outer and inner surfaces of the tube; (c, d) cross-sections of individual nanofibers, 0% K/100% PVA and 10% K/90% PVA nanofibers, respectively.
(a)(b)(c)(d)Figure3 also shows histograms of nanofiber diameters to indicate the diameter distributions that narrow as keratin content increases. Energy-dispersive X-ray (EDX) results, shown in Figure 5, indicate that keratin/PVA nanofibers are mainly composed of carbon, oxygen, nitrogen, and sulphur.Figure 5
Energy-dispersive X-ray (EDX) results of keratin/PVA nanofiber tubes: (a) EDX spectrum of elements, (b) element mapping, and (c) atomic concentration of nanofibers.
(a)(b)(c)The element mapping of EDX showed that all the atoms were evenly distributed throughout the nanofibers’ materials. The significant amounts of nitrogen and sulphur indicated the presence of keratin proteins. There was a noticeable increase in nitrogen percentage as keratin content increased in nanofibers. The conductivity and average diameters of nanofibers are tabulated in Table1 and shown in Figure 6.Table 1
Conductivity of different keratin/PVA solutions and average diameters of relevant nanofibers.
Keratin/PVAConductivity (mS/cm)Averagediameter±Std.dev (nm)Averageporesize±Std.dev (nm)0%/100%272234±870.3±0.08110%/90%484212±630.09±0.02920%/80%1020196±370.07±0.01230%/70%1198170±500.04±0.004Figure 6
Graph of the effect of keratin content on average diameters of keratin/PVA nanofibers.Furthermore, in Figure5(b), SEM image analysis shows atoms evenly distributed throughout the nanofiber tubes. The average pore sizes decreased from 0.09 to 0.04 pm, decreasing with increased keratin content. This effect can also be attributed to the keratin conductivity effect; high conductivity within the polymer jet causes the jet to split into thinner jets due to the greater repulsive force, resulting in a higher number of fibers per unit area, thus reducing the number of fibers per unit pore size.The FTIR spectra of PVA nanofibers, keratin powder, and keratin/PVA nanofibers are shown in Figure7. Keratin spectrum was used as a reference spectrum for keratin/PVA nanofiber spectra. The keratin spectrum exhibited peaks of different amides of keratin protein. A peak at 3282.56 cm-1 is N-H stretching of amide A and possible Fermi resonance from the overtone of amide I [28], C-N bending of amide B (2919.88 cm-1), CO stretching of amide I (1633.74 cm-1), C-N stretching and N-H bending of amide II (1532.24 cm-1), amide III’s CO stretching (1200 cm-1), C-H bending of amide IV (623 cm-1), and S-O stretching of cysteine-sulphonate (1212.05 cm-1) and disulphide bonds at 550 cm-1 [16, 29]. Some PVA spectrum peaks include -OH stretching peak at 3100 cm-1, -CHO stretching at 2950 cm-1, and CO stretching at 2900 cm-1. The addition of keratin into PVA increased the intensity of amides A and B; this can be attributed to the interaction of the -NH2 group of keratin and -OH group of PVA, resulting in hydrogen bond formation.Figure 7
FTIR spectra of chicken feather keratin, PVA nanofibers, keratin/PVA nanofibers, and a zoomed-in subgraph of new peaks.The increased amount of keratin corresponds with two new peaks related to PVA, at 1642.26 cm-1 and 1547.21 cm-1. These peaks shift to shorter wavelengths as keratin content increases. The changes in the intensities of peaks, forming new ones and shifting to shorter wavelengths, confirm keratin in the nanofibers and suggest the chemical interactions between keratin and PVA. This chemical reaction between the PVA and keratin functional group minimizes the interaction between keratin macromolecules and increases the keratin’s electrospinnability; the amide-carbonyl interaction further prevents phase separation of keratin and PVA in blended spinning solution [30].TG analysis in Figure8 shows the mass-loss curves and their derivatives to indicate polyvinyl alcohol nanofibers’ thermal behaviour, keratin, and keratin-PVA nanofibers. These graphs show three major mass-loss events for nanofibers and keratin. The first event at just below 100°C was attributed to water evaporation. The mass loss, shown in Table 2, resulted in a mass reduction of 2.59% for 100% PVA nanofibers and 2.49% to 3.98% for 10% to 30% keratin nanofibers and keratin.Figure 8
Thermogravimetric analysis and TGA derivative of keratin/PVA nanofibers.Table 2
Quantity of mass loss of keratin/PVA nanofibers at 100°C and 400°C.
Mass loss (%)SampleT100°CT400°C100% PVA2.5980.3910% K/90%P VA2.4970.1120% K/80% PVA3.2771.5130% K/70% PVA3.7770.91Keratin powder3.9868.11The increasing trend of water mass with the increase in PVA keratin content indicates keratin nanofibers’ hydrophilicity. The second and significant mass loss occurred between 190°C and 400°C. This was attributed to the degradation of alpha-helix and peptide bonds of amino acid residues [31].The onset temperature of PVA nanofibers, 190°C, was higher than that of keratin and keratin/PVA nanofibers at 160°C. However, increasing keratin content showed no further effect on the onset temperature of keratin/PVA nanofibers. Nevertheless, PVA nanofibers and keratin showed a high degradation rate, with PVA nanofibers having the highest rate. Both PVA nanofibers and keratin exhibited a high degradation rate than their blend nanofibers. The third mass loss event occurred between 405°C and 490°C; this loss was due to the degradation of the previous mass loss event’s by-products. Keratin had a high amount of residuals than PVA, indicating better stability, while the ash content of keratin/PVA nanofibers fell between keratin and PVA.


## 3.1. Extraction and Characterization of Keratin

White chicken feathers were obtained after pretreatment. The increased whiteness index of feathers was due to removing brown-yellow oil and fats. The index further advanced after degreasing with ethanol. After that, a mixture of an aqueous solution and chicken feather particles was recovered after 4 hours of cooking. The final purification steps resulted in light brown supernatant and keratin powder after filtration and freeze-drying, respectively. Figure1 contains the extracted keratin molecular weight’s sodium dodecyl sulphate polyacrylamide gel electrophoresis (SDS-PAGE) analysis.Figure 1
SDS-PAGE gels of extracted keratin protein: glycine gel (a) and tricine gel (b).It shows that the extracted keratin has molecular weights that range from about 3 kDa to approximately 60 kDa, whereas the broad, intense band between 10 and 15 kDa indicates that multiple monomers have a molecular weight of 10-15 kDa range [26].FTIR’s functional groups’ qualitative analysis confirmed the presence of polypeptide amides, namely, amide A, amide B, amide I, amide II, and amide III represented by the absorbance peaks at 3280.79 mc-1, 2919.88 mc-1, 1633.74 mc-1, 1532.24 mc-1, and 1212.05 mc-1, respectively [27]. Furthermore, the extracted keratin elemental analysis showed that this keratin has 5.02% sulphur, 46.64% carbon, 10.82% nitrogen, 7.72% hydrogen, and 29.74% other elements, including oxygen. The extract is composed of 67.63% protein, calculated from the nitrogen percentage in the hydrolysate.


## 3.2. Preparation and Characterization of Keratin/PVA Nanofibers

The prepared electrospinning solutions of various ratios of keratin and PVA, from 00/100 to 30/70, were homogeneous and had a pH of 8 at 24.1°C. The graph in Figure2 shows the effect of keratin content in the electrospinning solution.Figure 2
Conductivity of keratin/PVA solutions of different keratin and polyvinyl alcohol ratios.The conductivity of electrospinning solutions increased with an increase in keratin content. The increase in conductivity may be due to polar amino acids in keratin. The morphology of keratin/PVA nanofibers with different keratin contents from 0% to 30% is shown in Figure3. All nanofibers were cylindrical and became thinner as keratin content was increased. As keratin content increases, the conductivity of the spinning solution increases.Figure 3
SEM images and distributions of nanofiber diameters of the keratin/polyvinyl alcohol system: (a) 0% keratin/100% PVA, (b) 10% K/90% PVA, (c) 20% K/80% PVA, and (d) 30% K/70% PVA.
(a)(b)(c)(d)The increase in conductivity increases the polymer jet’s electrical charge, increases the electric field force, and results in thinner jets and nanofibers and smaller fiber diameters. In addition to greater electric field strength, increasing conductivity decreases the solution’s viscosity, resulting in smaller nanofiber’s average diameters. However, there was no noticeable change in the individual nanofibers’ cross-sectional shape from 100%bPVA to 90% PVA nanofibers, as shown in Figure4.Figure 4
SEM images of keratin nanofibers: (a) tubular structure and (b) the outer and inner surfaces of the tube; (c, d) cross-sections of individual nanofibers, 0% K/100% PVA and 10% K/90% PVA nanofibers, respectively.
(a)(b)(c)(d)Figure3 also shows histograms of nanofiber diameters to indicate the diameter distributions that narrow as keratin content increases. Energy-dispersive X-ray (EDX) results, shown in Figure 5, indicate that keratin/PVA nanofibers are mainly composed of carbon, oxygen, nitrogen, and sulphur.Figure 5
Energy-dispersive X-ray (EDX) results of keratin/PVA nanofiber tubes: (a) EDX spectrum of elements, (b) element mapping, and (c) atomic concentration of nanofibers.
(a)(b)(c)The element mapping of EDX showed that all the atoms were evenly distributed throughout the nanofibers’ materials. The significant amounts of nitrogen and sulphur indicated the presence of keratin proteins. There was a noticeable increase in nitrogen percentage as keratin content increased in nanofibers. The conductivity and average diameters of nanofibers are tabulated in Table1 and shown in Figure 6.Table 1
Conductivity of different keratin/PVA solutions and average diameters of relevant nanofibers.
Keratin/PVAConductivity (mS/cm)Averagediameter±Std.dev (nm)Averageporesize±Std.dev (nm)0%/100%272234±870.3±0.08110%/90%484212±630.09±0.02920%/80%1020196±370.07±0.01230%/70%1198170±500.04±0.004Figure 6
Graph of the effect of keratin content on average diameters of keratin/PVA nanofibers.Furthermore, in Figure5(b), SEM image analysis shows atoms evenly distributed throughout the nanofiber tubes. The average pore sizes decreased from 0.09 to 0.04 pm, decreasing with increased keratin content. This effect can also be attributed to the keratin conductivity effect; high conductivity within the polymer jet causes the jet to split into thinner jets due to the greater repulsive force, resulting in a higher number of fibers per unit area, thus reducing the number of fibers per unit pore size.The FTIR spectra of PVA nanofibers, keratin powder, and keratin/PVA nanofibers are shown in Figure7. Keratin spectrum was used as a reference spectrum for keratin/PVA nanofiber spectra. The keratin spectrum exhibited peaks of different amides of keratin protein. A peak at 3282.56 cm-1 is N-H stretching of amide A and possible Fermi resonance from the overtone of amide I [28], C-N bending of amide B (2919.88 cm-1), CO stretching of amide I (1633.74 cm-1), C-N stretching and N-H bending of amide II (1532.24 cm-1), amide III’s CO stretching (1200 cm-1), C-H bending of amide IV (623 cm-1), and S-O stretching of cysteine-sulphonate (1212.05 cm-1) and disulphide bonds at 550 cm-1 [16, 29]. Some PVA spectrum peaks include -OH stretching peak at 3100 cm-1, -CHO stretching at 2950 cm-1, and CO stretching at 2900 cm-1. The addition of keratin into PVA increased the intensity of amides A and B; this can be attributed to the interaction of the -NH2 group of keratin and -OH group of PVA, resulting in hydrogen bond formation.Figure 7
FTIR spectra of chicken feather keratin, PVA nanofibers, keratin/PVA nanofibers, and a zoomed-in subgraph of new peaks.The increased amount of keratin corresponds with two new peaks related to PVA, at 1642.26 cm-1 and 1547.21 cm-1. These peaks shift to shorter wavelengths as keratin content increases. The changes in the intensities of peaks, forming new ones and shifting to shorter wavelengths, confirm keratin in the nanofibers and suggest the chemical interactions between keratin and PVA. This chemical reaction between the PVA and keratin functional group minimizes the interaction between keratin macromolecules and increases the keratin’s electrospinnability; the amide-carbonyl interaction further prevents phase separation of keratin and PVA in blended spinning solution [30].TG analysis in Figure8 shows the mass-loss curves and their derivatives to indicate polyvinyl alcohol nanofibers’ thermal behaviour, keratin, and keratin-PVA nanofibers. These graphs show three major mass-loss events for nanofibers and keratin. The first event at just below 100°C was attributed to water evaporation. The mass loss, shown in Table 2, resulted in a mass reduction of 2.59% for 100% PVA nanofibers and 2.49% to 3.98% for 10% to 30% keratin nanofibers and keratin.Figure 8
Thermogravimetric analysis and TGA derivative of keratin/PVA nanofibers.Table 2
Quantity of mass loss of keratin/PVA nanofibers at 100°C and 400°C.
Mass loss (%)SampleT100°CT400°C100% PVA2.5980.3910% K/90%P VA2.4970.1120% K/80% PVA3.2771.5130% K/70% PVA3.7770.91Keratin powder3.9868.11The increasing trend of water mass with the increase in PVA keratin content indicates keratin nanofibers’ hydrophilicity. The second and significant mass loss occurred between 190°C and 400°C. This was attributed to the degradation of alpha-helix and peptide bonds of amino acid residues [31].The onset temperature of PVA nanofibers, 190°C, was higher than that of keratin and keratin/PVA nanofibers at 160°C. However, increasing keratin content showed no further effect on the onset temperature of keratin/PVA nanofibers. Nevertheless, PVA nanofibers and keratin showed a high degradation rate, with PVA nanofibers having the highest rate. Both PVA nanofibers and keratin exhibited a high degradation rate than their blend nanofibers. The third mass loss event occurred between 405°C and 490°C; this loss was due to the degradation of the previous mass loss event’s by-products. Keratin had a high amount of residuals than PVA, indicating better stability, while the ash content of keratin/PVA nanofibers fell between keratin and PVA.


## 4. Conclusion

Keratin/PVA nanofiber tubes were successfully fabricated without longitudinal seams. The addition of polyvinyl alcohol improved keratin’s electrospinnability by interrupting keratin macromolecules’ interaction and forming hydrogen bonds. On the other hand, keratin advanced the thermal stability of PVA nanofibers. Keratin nanofibers have a smaller diameter than keratin-free PVA nanofibers, increasing their surface area. The diameter of the nanofibers decreases when keratin content increases, suggesting the limit in electrospinnability of PVA/keratin blend due to keratin content. When used as nerve conduits, these permeable tubes will provide transportation of nutrients and metabolic waste; they will serve as a barrier that prevents other tissues into the regeneration area. Small diameters increase cell proliferation, cell spreading, and differentiation of neural stem cells while decreasing cell aggregation levels. The keratin-based nanofiber tubes are potential nerve regeneration frames as they mimic the extracellular matrix of the natural fibrous structure of neural tissue. They enhance electrophysiological recovery and axon density. Future investigations on the keratin/PVA nanofiber tubes will include in vitro and in vivo experiments.



---