# Synthesis and Electrochemical Characterization of Palladium Crystals Enclosed by (100) Facets by Seed-Mediated Fabrication

Authors: Eiji Higuchi; Masashi Kawai; Masanobu Chiku; Hiroshi Inoue
Journal: International Journal of Electrochemistry
 (2018)

---

## Abstract

Pd crystals enclosed by (100) facets were prepared in an aqueous solution containing cetyltrimethylammonium bromide (CTAB) as the capping agent and ascorbic acid as the reducing agent at 30, 40, and 50°C by a modified seed-mediated fabrication technique. Regardless of the reaction temperature, the absorption peak between 300 and 400 nm assigned toPdCl42- decreased with an increase in the reaction time after the addition of ascorbic acid in the PdCl42- aqueous solution containing CTAB because of Pd deposition. The field emission-scanning electron microscopy images showed that the Pd crystals were enclosed by only (100) facets, and their fractions depended on the reaction temperature. The ratios of the peak current at 0.54 and 0.48 V were 0.60, 0.54, and 0.47 for the samples prepared at 30, 40, and 50°C, respectively, suggesting that the proportion of the (100) facet on the Pd surface was higher at lower temperatures.


---

## Body

## 1. Introduction

Polymer electrolyte fuel cells (PEFCs) that use hydrogen as fuel are attracting considerable attention as primary power sources for electric vehicles owing to their high energy conversion efficiency and low emission of pollutants. Pt-based electrocatalysts with high catalytic activity for oxygen reduction reaction (ORR) have been used as cathode catalysts in PEFCs. Pd-based catalysts have also been used for ORR, because Pd is cheaper and more abundant than Pt. The electrocatalytic activity per unit real surface area (specific activity) for ORR on Pd single crystals has been reported to increase in the order of Pd(110) < Pd(111) ≪ Pd(100), which is reverse to that for ORR on Pt single crystals [1]. Moreover, Pd(100) shows higher ORR activity than Pt(110), suggesting that the Pd(100) surface is the most active surface for ORR. Therefore, Pd nanoparticles consisting of only the (100) surface will exhibit a high ORR activity. This necessitates control of structure or shape during the preparation of Pd nanoparticles. Chemical metal deposition methods employing capping agents that preferentially adsorb on a specific facet to suppress crystal growth are often used for this purpose. Recently, many studies on the preparation of shape-controlled nanoparticles have been reported [2–9]. Pd nanocubes and nanobars enclosed by (100) facets were successfully produced with a yield of 80% by solvothermal synthesis at 150°C for 8 h using N,N-dimethylformamide as the reducing agent, palladium(II) acetylacetonate as the Pd precursor, and sodium iodide as the capping agent [2].Seed-mediated growth is another efficient and versatile method to synthesize metal crystals with controlled sizes and shapes. This method is particularly advantageous because it can be used to synthesize metal crystals with controlled shapes by choosing suitable seed nanoparticles and manipulating the crystal growth conditions. The seed-mediated growth method normally consists of two processes: synthesis of seed crystals and their shape-controlled growth in a growth solution containing a metal precursor, reducing agent, and capping reagent. The size of the resultant metal crystal is determined by that of the seed crystal, while its shape is mainly controlled by the difference in the growth rates of the facets. Usually, the shape-controlled growth of seed crystals occurs in the presence of soluble capping agents such as polymers and surfactants, which preferentially adsorb on a specific crystal facet to facilitate growth on other facets, leading to the formation of desired shapes. This facet-blocking strategy is extensively applied in the synthesis of crystals with unique shapes. Until now, the seed-mediated fabrication technique has been mainly performed in nonaqueous solvents at relatively high temperatures (>ca. 80°C). The preparation of shape-controlled Pd crystals in aqueous solutions at lower temperatures is desirable for reducing cost and environmental load. In this study, Pd nanocrystals enclosed by (100) facets were prepared in an aqueous solution containing cetyltrimethylammonium bromide (CTAB) as the capping agent and ascorbic acid as the reducing agent at 30, 40, and 50°C by the seed-mediated fabrication technique. In addition, the surface of the resultant Pd nanocrystals was characterized by Cu-stripping voltammetry.


## 2. Experimental

### 2.1. Preparation of Pd Crystals

Reagents PdCl2·2NaCl·3H2O (Wako Pure Chemical Industries, Ltd.), CTAB (Tokyo Chemical Industry Co., Ltd.), and ascorbic acid (Wako Pure Chemical Industries, Ltd.) were used as received.First, 10 mL of 10 mM CTAB aqueous solution was mixed with 2.5 mL of 10 mMPdCl42- aqueous solution, which was prepared by dissolving PdCl2·2NaCl·3H2O in ultrapure water at 50°C in an Ar atmosphere. Then, 250 μL of 100 mM ascorbic acid aqueous solution was added in the mixed solution at 50°C in an Ar atmosphere, followed by stirring at the same temperature for 1 h to form a suspension. The suspension was centrifuged at 14800 rpm and decanted. The black residue was washed 3 times with ultrapure water and redispersed in 0.1 mL of ultrapure water. The resultant suspension is denoted as Pd seed suspension.The growth solution for shape control was prepared by mixing 20 mL of 50 mM CTAB aqueous solution with 1 mL of 10 mMPdCl42- aqueous solution in a glass vial. Next, 0.1 mL of the Pd seed suspension was added in the growth solution at different temperatures of 30, 40, and 50°C in an O2 atmosphere, followed by stirring at the same temperature for 5 min and addition of 500 μL of 100 mM ascorbic acid aqueous solution. The resultant suspension was centrifuged at 14800 rpm and decanted. The black residue obtained was washed 3 times with ultrapure water. After suction filtration, it was dried in vacuum at room temperature for 12 h. The resultant Pd powders prepared at 30, 40, and 50°C are denoted as Pd-30, Pd-40, and Pd-50, respectively. For comparison, Pd nanoparticle-loaded carbon black (Pd/CB) was prepared by our previous method [10].


### 2.2. Characterization of Pd Crystals

The absorption spectra of the growth solution containing Pd seeds before and after addition of ascorbic acid at 30, 40, and 50°C were measured using a UV-Vis spectrophotometer (UV-2100PC, Shimadzu).The crystal structures of Pd-30, Pd-40, and Pd-50 were analyzed by X-ray diffraction (XRD; Shimadzu, XRD-6100) using a Cu Kα source (λ=0.1541 nm, 50 kV, 30 mA, 1° min−1).The mean particle sizes and shapes of the Pd seed crystals were evaluated by Cs-corrected scanning transmission electron microscopy (STEM; HD-2700, Hitachi; 200 kV). The Pd/CB specimen was used to observe the Pd seeds. After the addition of CB (Ketjen Black EC300, Lion) in the Pd seed suspension, the mixture was sonicated for 60 min to prepare Pd/CB. After suction filtration, the Pd/CB was thoroughly washed with ultrapure water. The samples for TEM microscopic measurements were obtained by dropping a dispersion of Pd/CB catalyst in ethanol on a Cu microgrid (Nisshin EM Co.) with a micropipette and air-drying it. The shapes of Pd-30, Pd-40, and Pd-50 were evaluated by field emission-scanning electron microscopy (FE-SEM; Hitachi S-4500). The samples for FE-SEM studies were prepared by casting a drop of each Pd dispersion onto a glassy carbon (GC) electrode.


### 2.3. Electrochemical Measurements of Pd Crystals

To evaluate the electrochemical properties of Pd-30, Pd-40, and Pd-50, the dispersions of Pd-30, Pd-40, and Pd-50 were cast on a GC disk electrode (Pd/GC) with a diameter of 0.50 cm (geometric surface area: 0.20 cm2) according to the previous procedure [10]. The amount of Pd loaded on the GC disk was 20 μg cm−2. A Pt plate and a reversible hydrogen electrode (RHE) were used as the counter and the reference electrodes, respectively. The surfaces of Pd-30, Pd-40, and Pd-50 were characterized by Cu-stripping voltammetry. The Cu monolayer was underpotentially deposited on the Pd crystal surfaces by holding the electrode potential at 0.3 V versus RHE for 3 min in an Ar-saturated 0.5 M H2SO4 solution containing 2 mM CuSO4 at 25°C. It was then oxidized by sweeping the potential from 0.3 to 0.8 V versus RHE at a sweep rate of 10 mV s−1.


## 2.1. Preparation of Pd Crystals

Reagents PdCl2·2NaCl·3H2O (Wako Pure Chemical Industries, Ltd.), CTAB (Tokyo Chemical Industry Co., Ltd.), and ascorbic acid (Wako Pure Chemical Industries, Ltd.) were used as received.First, 10 mL of 10 mM CTAB aqueous solution was mixed with 2.5 mL of 10 mMPdCl42- aqueous solution, which was prepared by dissolving PdCl2·2NaCl·3H2O in ultrapure water at 50°C in an Ar atmosphere. Then, 250 μL of 100 mM ascorbic acid aqueous solution was added in the mixed solution at 50°C in an Ar atmosphere, followed by stirring at the same temperature for 1 h to form a suspension. The suspension was centrifuged at 14800 rpm and decanted. The black residue was washed 3 times with ultrapure water and redispersed in 0.1 mL of ultrapure water. The resultant suspension is denoted as Pd seed suspension.The growth solution for shape control was prepared by mixing 20 mL of 50 mM CTAB aqueous solution with 1 mL of 10 mMPdCl42- aqueous solution in a glass vial. Next, 0.1 mL of the Pd seed suspension was added in the growth solution at different temperatures of 30, 40, and 50°C in an O2 atmosphere, followed by stirring at the same temperature for 5 min and addition of 500 μL of 100 mM ascorbic acid aqueous solution. The resultant suspension was centrifuged at 14800 rpm and decanted. The black residue obtained was washed 3 times with ultrapure water. After suction filtration, it was dried in vacuum at room temperature for 12 h. The resultant Pd powders prepared at 30, 40, and 50°C are denoted as Pd-30, Pd-40, and Pd-50, respectively. For comparison, Pd nanoparticle-loaded carbon black (Pd/CB) was prepared by our previous method [10].


## 2.2. Characterization of Pd Crystals

The absorption spectra of the growth solution containing Pd seeds before and after addition of ascorbic acid at 30, 40, and 50°C were measured using a UV-Vis spectrophotometer (UV-2100PC, Shimadzu).The crystal structures of Pd-30, Pd-40, and Pd-50 were analyzed by X-ray diffraction (XRD; Shimadzu, XRD-6100) using a Cu Kα source (λ=0.1541 nm, 50 kV, 30 mA, 1° min−1).The mean particle sizes and shapes of the Pd seed crystals were evaluated by Cs-corrected scanning transmission electron microscopy (STEM; HD-2700, Hitachi; 200 kV). The Pd/CB specimen was used to observe the Pd seeds. After the addition of CB (Ketjen Black EC300, Lion) in the Pd seed suspension, the mixture was sonicated for 60 min to prepare Pd/CB. After suction filtration, the Pd/CB was thoroughly washed with ultrapure water. The samples for TEM microscopic measurements were obtained by dropping a dispersion of Pd/CB catalyst in ethanol on a Cu microgrid (Nisshin EM Co.) with a micropipette and air-drying it. The shapes of Pd-30, Pd-40, and Pd-50 were evaluated by field emission-scanning electron microscopy (FE-SEM; Hitachi S-4500). The samples for FE-SEM studies were prepared by casting a drop of each Pd dispersion onto a glassy carbon (GC) electrode.


## 2.3. Electrochemical Measurements of Pd Crystals

To evaluate the electrochemical properties of Pd-30, Pd-40, and Pd-50, the dispersions of Pd-30, Pd-40, and Pd-50 were cast on a GC disk electrode (Pd/GC) with a diameter of 0.50 cm (geometric surface area: 0.20 cm2) according to the previous procedure [10]. The amount of Pd loaded on the GC disk was 20 μg cm−2. A Pt plate and a reversible hydrogen electrode (RHE) were used as the counter and the reference electrodes, respectively. The surfaces of Pd-30, Pd-40, and Pd-50 were characterized by Cu-stripping voltammetry. The Cu monolayer was underpotentially deposited on the Pd crystal surfaces by holding the electrode potential at 0.3 V versus RHE for 3 min in an Ar-saturated 0.5 M H2SO4 solution containing 2 mM CuSO4 at 25°C. It was then oxidized by sweeping the potential from 0.3 to 0.8 V versus RHE at a sweep rate of 10 mV s−1.


## 3. Results and Discussion

### 3.1. Morphologies of Pd-30, Pd-40, and Pd-50

Figure1 shows the UV-Vis absorption spectra of the growth solution containing the Pd seed suspension at 30, 40, and 50°C in an O2 atmosphere before and after the addition of ascorbic acid aqueous solution. In each case, a large absorption peak was observed between 300 and 400 nm before the addition of ascorbic acid aqueous solution. This peak is assigned to metal-centered transition of PdCl42- [11, 12]. After the addition of ascorbic acid aqueous solution, the absorbance of the peak decreased with an increase in the reaction time regardless of the reaction temperature, suggesting that PdCl42- was used for Pd deposition. As can be seen from Figure 1, the time required for the disappearance of the absorption peak is shorter at higher temperatures, which is due to the increase in the reduction rate of PdCl42- to Pd. The absorption peak completely disappeared within 24 h at 30°C, because of the slow reduction rate of PdCl42- to Pd at this temperature. At 50°C, the absorption peak completely disappeared within 1 h.Figure 1
UV-Vis absorption spectra of growth solution containing Pd seeds before and after addition of ascorbic acid at (a) 30°C, (b) 40°C, and (c) 50°C under O2 atmosphere.
(a)
(b)
(c)Figure2 shows the XRD patterns of Pd-30, Pd-40, and Pd-50. In each XRD pattern, three diffraction peaks were observed at 2θ=40.1, 46.7, and 68.1°, which are assigned to (111), (200), and (220) planes of face-centered cubic Pd, respectively; this suggests the formation of metallic Pd. The ratio of peak intensity of the (200) plane to that of the (111) plane for all the samples (Pd-30, Pd-40, and Pd-50) was 0.35, whereas for the Pd/CB [10], in which the Pd nanoparticles were spherical, it was 0.22. This suggests that Pd-30, Pd-40, and Pd-50 have a higher proportion of Pd(100) planes than Pd/CB.Figure 2
XRD patterns of Pd-30, Pd-40, and Pd-50.We investigated the shapes of the Pd seeds by TEM and those of Pd-30, Pd-40, and Pd-50 by SEM; the results are shown in Figure3. Pd nanocrystals with different shapes, such as rectangular bar, cube, truncated polyhedron, and truncated cube, are observed in each image. For each sample, the shapes of more than 200 Pd crystals chosen randomly from several SEM images were examined and classified into two categories: Pd crystals enclosed by only (100) facets and others; and the results are summarized in Table 1. The size of the Pd seed was ca. 8 nm. The size of the Pd crystals increased when the Pd seed suspension was added in the growth solution.Table 1
Shape distribution profiles for Pd-30, Pd-40, and Pd-50.
Pd crystal
Crystals enclosed by (100)/%
Others/%
Pd-30
51
49
Pd-40
25
75
Pd-50
28
72Figure 3
TEM image of Pd seed and SEM images of Pd-30, Pd-40, and Pd-50.
(a)
Pd seed
(b)
Pd-30
(c)
Pd-40
(d)
Pd-50It is known that Br− ions preferentially adsorb on the Pd(100) facet [13], causing preferential deposition of Pd on other facets. In the present growth solution, Br− in CTAB will preferentially adsorb on the (100) facet of the Pd seeds and inhibit the deposition of Pd, leading to Pd crystals enclosed by the (100) facets [13]. Therefore, the adsorbed Br− has to inactivate the (100) facet of this crystal to continue the growth of (111) facet.Xiong et al. have extensively explored the method of oxidative etching for shape-controlled synthesis of metal nanostructures [8]. Oxidative etching, caused by oxygen and chloride, can be used to remove Br− ions from the (100) facet and thus expose sites for addition of Pd atoms. At a sufficiently high concentration, the Br− ions would make it difficult to perform oxidative etching over the facet. However, with the assistance of water, oxidative etching can occur locally on a specific facet of cubic Pd [8]. When sufficient Pd atoms exist on the etched sites, deposition of Pd atoms will be faster than the dissolution of Pd atoms caused by etching. It has been reported that preferential growth at active sites breaks the cubic symmetry of a Pd nanocrystal and leads to the formation of Pd nanorods and nanobars [8]. In the present study, O2 and Cl− (from PdCl42-) were included in the growth solution. Thus, according to Figure 3, the Pd crystals enclosed by only (100) facets exhibit not only cubic but also anisotropic shapes such as rectangular bars.The proportion of Pd crystals enclosed by only the (100) facets in Pd-30 was higher than that in Pd-40 and Pd-50, suggesting that the reaction temperature influences [2] the formation of Pd crystals enclosed by only the (100) facets. The change in the temperature can exponentially influence the reaction rate, which includes dissolution and deposition rates in the present case. When the adsorption energy of Br− in the growth solution is strengthened at low temperatures, the deposition and the dissolution of Pd do not occur easily. On the contrary, the dissolution and the deposition rates are faster at higher temperatures, and the crystal shape changes via cycles of dissolution and reduction. In addition, when the concentration of the Pd precursor is sufficiently high, Pd deposition will be faster than Pd dissolution [8]. The concentration of the Pd precursor in the present growth solution appears to satisfy the condition at which the deposition rate is higher than the dissolution rate at low temperatures.


### 3.2. Cu-Stripping Voltammograms of Pd-30, Pd-40, and Pd-50

The surfaces of Pd-30, Pd-40, and Pd-50 were characterized by Cu-stripping voltammetry in an Ar-saturated (0.5 M H2SO4 + 2 mM CuSO4) aqueous solution. Figure 4 shows the Cu-stripping voltammograms from 0.3 to 0.8 V versus RHE for Pd-30, Pd-40, and Pd-50 and Pd/CB for reference. The stripping peaks of the underpotentially deposited Cu monolayer are sensitive to crystallographic orientations of the surface Pd atoms [14–16]. Cuesta et al. found that the stripping peaks of Cu adatoms on the Pd(111) and the Pd(100) single crystals are observed at approximately 0.49 and 0.54 V versus RHE, respectively, whereas on Pd(110), the two stripping peaks are observed at approximately 0.37 and 0.53 V versus RHE. In the Cu-stripping voltammogram of Pd/CB, a large Cu-stripping peak (30 μA) corresponding to Pd(111) and a small peak (6.3 μA) corresponding to Pd(110) are observed, but the peak corresponding to Pd(100) is not observed. On the other hand, Cu-stripping peaks corresponding to Pd(110), (111), and (100) are observed at approximately 0.36, 0.48, and 0.54 V versus RHE, respectively, in Pd-30, Pd-40, and Pd-50, suggesting that all the Pd surfaces had these facets. As shown in Figure 4, the Cu-stripping currents at 0.36 V for all the samples (Pd-30, Pd-40, and Pd-50) are similar. The ratios of the peak current at 0.54 and 0.48 V were 0.60, 0.54, and 0.47 for Pd-30, Pd-40, and Pd-50, respectively, suggesting that the proportion of the (100) facet on the Pd surface was higher at lower temperatures.Figure 4
Cu-stripping voltammograms for Pd-30, Pd-40, and Pd-50 in an Ar-saturated (0.5 M H2SO4 + 2 mM CuSO4) aqueous solution.


## 3.1. Morphologies of Pd-30, Pd-40, and Pd-50

Figure1 shows the UV-Vis absorption spectra of the growth solution containing the Pd seed suspension at 30, 40, and 50°C in an O2 atmosphere before and after the addition of ascorbic acid aqueous solution. In each case, a large absorption peak was observed between 300 and 400 nm before the addition of ascorbic acid aqueous solution. This peak is assigned to metal-centered transition of PdCl42- [11, 12]. After the addition of ascorbic acid aqueous solution, the absorbance of the peak decreased with an increase in the reaction time regardless of the reaction temperature, suggesting that PdCl42- was used for Pd deposition. As can be seen from Figure 1, the time required for the disappearance of the absorption peak is shorter at higher temperatures, which is due to the increase in the reduction rate of PdCl42- to Pd. The absorption peak completely disappeared within 24 h at 30°C, because of the slow reduction rate of PdCl42- to Pd at this temperature. At 50°C, the absorption peak completely disappeared within 1 h.Figure 1
UV-Vis absorption spectra of growth solution containing Pd seeds before and after addition of ascorbic acid at (a) 30°C, (b) 40°C, and (c) 50°C under O2 atmosphere.
(a)
(b)
(c)Figure2 shows the XRD patterns of Pd-30, Pd-40, and Pd-50. In each XRD pattern, three diffraction peaks were observed at 2θ=40.1, 46.7, and 68.1°, which are assigned to (111), (200), and (220) planes of face-centered cubic Pd, respectively; this suggests the formation of metallic Pd. The ratio of peak intensity of the (200) plane to that of the (111) plane for all the samples (Pd-30, Pd-40, and Pd-50) was 0.35, whereas for the Pd/CB [10], in which the Pd nanoparticles were spherical, it was 0.22. This suggests that Pd-30, Pd-40, and Pd-50 have a higher proportion of Pd(100) planes than Pd/CB.Figure 2
XRD patterns of Pd-30, Pd-40, and Pd-50.We investigated the shapes of the Pd seeds by TEM and those of Pd-30, Pd-40, and Pd-50 by SEM; the results are shown in Figure3. Pd nanocrystals with different shapes, such as rectangular bar, cube, truncated polyhedron, and truncated cube, are observed in each image. For each sample, the shapes of more than 200 Pd crystals chosen randomly from several SEM images were examined and classified into two categories: Pd crystals enclosed by only (100) facets and others; and the results are summarized in Table 1. The size of the Pd seed was ca. 8 nm. The size of the Pd crystals increased when the Pd seed suspension was added in the growth solution.Table 1
Shape distribution profiles for Pd-30, Pd-40, and Pd-50.
Pd crystal
Crystals enclosed by (100)/%
Others/%
Pd-30
51
49
Pd-40
25
75
Pd-50
28
72Figure 3
TEM image of Pd seed and SEM images of Pd-30, Pd-40, and Pd-50.
(a)
Pd seed
(b)
Pd-30
(c)
Pd-40
(d)
Pd-50It is known that Br− ions preferentially adsorb on the Pd(100) facet [13], causing preferential deposition of Pd on other facets. In the present growth solution, Br− in CTAB will preferentially adsorb on the (100) facet of the Pd seeds and inhibit the deposition of Pd, leading to Pd crystals enclosed by the (100) facets [13]. Therefore, the adsorbed Br− has to inactivate the (100) facet of this crystal to continue the growth of (111) facet.Xiong et al. have extensively explored the method of oxidative etching for shape-controlled synthesis of metal nanostructures [8]. Oxidative etching, caused by oxygen and chloride, can be used to remove Br− ions from the (100) facet and thus expose sites for addition of Pd atoms. At a sufficiently high concentration, the Br− ions would make it difficult to perform oxidative etching over the facet. However, with the assistance of water, oxidative etching can occur locally on a specific facet of cubic Pd [8]. When sufficient Pd atoms exist on the etched sites, deposition of Pd atoms will be faster than the dissolution of Pd atoms caused by etching. It has been reported that preferential growth at active sites breaks the cubic symmetry of a Pd nanocrystal and leads to the formation of Pd nanorods and nanobars [8]. In the present study, O2 and Cl− (from PdCl42-) were included in the growth solution. Thus, according to Figure 3, the Pd crystals enclosed by only (100) facets exhibit not only cubic but also anisotropic shapes such as rectangular bars.The proportion of Pd crystals enclosed by only the (100) facets in Pd-30 was higher than that in Pd-40 and Pd-50, suggesting that the reaction temperature influences [2] the formation of Pd crystals enclosed by only the (100) facets. The change in the temperature can exponentially influence the reaction rate, which includes dissolution and deposition rates in the present case. When the adsorption energy of Br− in the growth solution is strengthened at low temperatures, the deposition and the dissolution of Pd do not occur easily. On the contrary, the dissolution and the deposition rates are faster at higher temperatures, and the crystal shape changes via cycles of dissolution and reduction. In addition, when the concentration of the Pd precursor is sufficiently high, Pd deposition will be faster than Pd dissolution [8]. The concentration of the Pd precursor in the present growth solution appears to satisfy the condition at which the deposition rate is higher than the dissolution rate at low temperatures.


## 3.2. Cu-Stripping Voltammograms of Pd-30, Pd-40, and Pd-50

The surfaces of Pd-30, Pd-40, and Pd-50 were characterized by Cu-stripping voltammetry in an Ar-saturated (0.5 M H2SO4 + 2 mM CuSO4) aqueous solution. Figure 4 shows the Cu-stripping voltammograms from 0.3 to 0.8 V versus RHE for Pd-30, Pd-40, and Pd-50 and Pd/CB for reference. The stripping peaks of the underpotentially deposited Cu monolayer are sensitive to crystallographic orientations of the surface Pd atoms [14–16]. Cuesta et al. found that the stripping peaks of Cu adatoms on the Pd(111) and the Pd(100) single crystals are observed at approximately 0.49 and 0.54 V versus RHE, respectively, whereas on Pd(110), the two stripping peaks are observed at approximately 0.37 and 0.53 V versus RHE. In the Cu-stripping voltammogram of Pd/CB, a large Cu-stripping peak (30 μA) corresponding to Pd(111) and a small peak (6.3 μA) corresponding to Pd(110) are observed, but the peak corresponding to Pd(100) is not observed. On the other hand, Cu-stripping peaks corresponding to Pd(110), (111), and (100) are observed at approximately 0.36, 0.48, and 0.54 V versus RHE, respectively, in Pd-30, Pd-40, and Pd-50, suggesting that all the Pd surfaces had these facets. As shown in Figure 4, the Cu-stripping currents at 0.36 V for all the samples (Pd-30, Pd-40, and Pd-50) are similar. The ratios of the peak current at 0.54 and 0.48 V were 0.60, 0.54, and 0.47 for Pd-30, Pd-40, and Pd-50, respectively, suggesting that the proportion of the (100) facet on the Pd surface was higher at lower temperatures.Figure 4
Cu-stripping voltammograms for Pd-30, Pd-40, and Pd-50 in an Ar-saturated (0.5 M H2SO4 + 2 mM CuSO4) aqueous solution.


## 4. Conclusions

Pd crystals enclosed by (100) facets were synthesized by the seed-mediated fabrication technique at 30, 40, and 50°C. Before the addition of ascorbic acid aqueous solution, a large absorption peak corresponding to metal-centered transition ofPdCl42- was observed between 300 and 400 nm. After the addition of ascorbic acid aqueous solution, the absorbance of the peak decreased with an increase in the reaction time, suggesting that PdCl42- was used for the Pd deposition. From the XRD studies, the ratios of the peak intensity of (111) and (200) planes for Pd-30, Pd-40, and Pd-50 were higher than that of spherical Pd/CB. The SEM results showed that the proportion of Pd crystals enclosed by only the (100) facets increased with a decrease in the temperature. The Cu-stripping currents at 0.36 V for Pd-30, Pd-40, and Pd-50 were similar, whereas the ratio of the peak current at 0.54 and 0.48 V increased with a decrease in the temperature, suggesting that the proportion of Pd crystals enclosed by (100) was higher at lower temperatures.



---

*Source: 7138638-2018-01-21.xml*