# Structural Characterization of Emeraldine-Salt Polyaniline/Gold Nanoparticles Complexes

Authors: E. A. Sanches; J. C. Soares; R. M. Iost; V. S. Marangoni; G. Trovati; T. Batista; A. C. Mafud; V. Zucolotto; Y. P. Mascarenhas
Journal: Journal of Nanomaterials
 (2011)

---

## Abstract

Gold nanoparticles (Au NPs) stabilized with polyamidoamine dendrimers (Au-PAMAM) or sodium citrate (Au-CITRATE) were synthesized and complexed with polyaniline emeraldine-salt form (ES-PANI). The complexes were characterized using structural and morphological techniques, including X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Zeta Potential analyses, and Fourier-Transformed Infrared spectroscopy (FTIR). When the Au-CITRATE NPs are added to the polymeric solution, the formation of a precipitate is clearly observed. The precipitate exhibited a different morphology from that found for ES-PANI and Au-CITRATE NPs, suggesting the formation of ES-PANI coating over the surface of Au-CITRATE NPs. On the other hand, when the Au-PAMAM NPs are incorporated into the ES-PANI solution, none interaction was observed, probably due to the repulsive electrostatic interactions, being the organization of the ES-PANI chains unaffected by the presence of the Au-PAMAM NPs.


---

## Body

## 1. Introduction

The discovery and development of new semiconducting polymers have brought a number of technological applications. In general, the ability to combine the electrical properties of semiconductors with the versatility and processability of polymers is the basic concept behind the development of intrinsically conducting polymers (ICPs) [1–5]. Polyaniline (PANI) is one of the most important conducting polymer due to its easy preparation and doping process and environmental stability [6]. The fully reduced leucoemeraldine-base form (LB-PANI, y=1) and the fully oxidized pernigraniline-base form (PB-PANI, y=0) are nonconducting forms of PANI. The partially oxidized emeraldine-base (EB-PANI, y=0.5) is a semiconductor, which becomes the conducting emeraldine-salt form (ES-PANI) after protonation [6–8].Conducting polymer/inorganic nanoparticle composites has attracted attention due to their great potential for applications [9–15] such as nanoelectronics [16], gas sensors [17, 18], biosensors [19–21], capacitors [22], and catalysts [23]. Among the inorganic nanomaterials, gold nanoparticles have received great attention because of their unique electrical and optical properties, as well as their extensive applications in biomedical areas [24]. Composites containing organic polymers and inorganic nanoparticles provide a completely new class of materials with novel properties [25–29].In this study, there was made a structural characterization of hybrid complexes based upon Au NPs and ES-PANI. Two different Au NPs had been used, stabilized with polyamidoamine dendrimers (Au-PAMAM) or sodium citrate (Au-CITRATE). We aimed at investigating the interactions between Au NPs and ES-PANI in solution and their correlation with complex stability.


## 2. Experimental

### 2.1. Synthesis of Au NPs

Au NPs were chemically synthesized using two stabilizers, namely, polyamidoamine dendrimer PAMAM—generation 4, or sodium citrate in order to obtain positively and negatively charged nanoparticles. Au-PAMAM nanohybrids were prepared using 5 mL of KAuCl4 solution (1 mmol·L−1) added to 5 mL of PAMAM (0.07 mmol·L−1) and 5 mL of formic acid (1 mmol·L−1) [30]. Au-CITRATE nanoparticles were prepared using 5 mL of HAuCl4 (2 g·L−1) dissolved in 40 mL of water and 100 mg of sodium citrate (salt form) dissolved in 5 mL of water [31]. Addition of the sodium citrate solution to the gold solution was followed by increasing the temperature to 95°C and continuous stirring for 1 h. A clear red solution was formed during the addition of sodium citrate solution. The final Au NPs solutions were kept in the dark during 4 h before using.


### 2.2. Synthesis of Emeraldine-Salt Polyaniline (ES-PANI) and Samples Characterization

Aniline (Aldrich) was used after distillation. HCl (aq), acetone, and (NH4)2S2O8 were commercially obtained (Aldrich) and used without further purification. Synthesis of ES-PANI was performed based on the method described by Bhadra et al. [32] with some modifications. Distilled aniline (0.2 M) was dissolved in 500 mL of HCl (1.0 M) at room temperature. A stoichiometric calculated amount of ammonium persulfate (11.5 g) was dissolved in 200 mL of HCl (1.0 M), placed in a burette, and added drop by drop to the above solution for 2 h. The system was kept under constant stirring for 3 h. The dark green precipitate resulting from this reaction (20 mg) was solubilized in 10 mL of distilled water, sonificated for 0.5 h, and filtered. The resulting solution was separated in aliquots of 1.5 mL, in which were added volumes of 50, 100, and 500 mL of Au-PAMAM NPs. The same procedure was repeated for the additions of Au-CITRATE NPs.Transmission Electron Microscopy (TEM) images for Au-PAMAM and Au-CITRATE NPs solutions were obtained on a Philips CM120 electron microscope operating at an acceleration voltage of 120 kV. Samples were ultrasonically dispersed for 1 h and then a drop of each one suspension was placed in a carbon-coated copper grid, which was left to stand for 24 h. Scanning Electron Microscopy (SEM) images were obtained using a Supra 35, Carl Zeiss, 3.0 kV. Powder samples were deposited on a carbon tape and the surface morphology was obtained at room temperature.Charges of the ES-PANI/Au NPs solutions were measured using a Zetasizer Nano ZS (Malvern) and a Titrator MPT-2. XRD patterns were collected with a Rigaku RotaFlex equipped with a graphite monochromator, operating with CuKα  radiation, 50 kV, and 100 mA. The data collection was recorded in the range of 2θ=5–70° with a step of 0.02° and 2 seconds/step. Fourier-Transformed Infrared spectroscopy (FTIR) was performed in the transmission mode on a Nexus 470 FTIR spectrometer. The spectra were obtained over 32 scans.


## 2.1. Synthesis of Au NPs

Au NPs were chemically synthesized using two stabilizers, namely, polyamidoamine dendrimer PAMAM—generation 4, or sodium citrate in order to obtain positively and negatively charged nanoparticles. Au-PAMAM nanohybrids were prepared using 5 mL of KAuCl4 solution (1 mmol·L−1) added to 5 mL of PAMAM (0.07 mmol·L−1) and 5 mL of formic acid (1 mmol·L−1) [30]. Au-CITRATE nanoparticles were prepared using 5 mL of HAuCl4 (2 g·L−1) dissolved in 40 mL of water and 100 mg of sodium citrate (salt form) dissolved in 5 mL of water [31]. Addition of the sodium citrate solution to the gold solution was followed by increasing the temperature to 95°C and continuous stirring for 1 h. A clear red solution was formed during the addition of sodium citrate solution. The final Au NPs solutions were kept in the dark during 4 h before using.


## 2.2. Synthesis of Emeraldine-Salt Polyaniline (ES-PANI) and Samples Characterization

Aniline (Aldrich) was used after distillation. HCl (aq), acetone, and (NH4)2S2O8 were commercially obtained (Aldrich) and used without further purification. Synthesis of ES-PANI was performed based on the method described by Bhadra et al. [32] with some modifications. Distilled aniline (0.2 M) was dissolved in 500 mL of HCl (1.0 M) at room temperature. A stoichiometric calculated amount of ammonium persulfate (11.5 g) was dissolved in 200 mL of HCl (1.0 M), placed in a burette, and added drop by drop to the above solution for 2 h. The system was kept under constant stirring for 3 h. The dark green precipitate resulting from this reaction (20 mg) was solubilized in 10 mL of distilled water, sonificated for 0.5 h, and filtered. The resulting solution was separated in aliquots of 1.5 mL, in which were added volumes of 50, 100, and 500 mL of Au-PAMAM NPs. The same procedure was repeated for the additions of Au-CITRATE NPs.Transmission Electron Microscopy (TEM) images for Au-PAMAM and Au-CITRATE NPs solutions were obtained on a Philips CM120 electron microscope operating at an acceleration voltage of 120 kV. Samples were ultrasonically dispersed for 1 h and then a drop of each one suspension was placed in a carbon-coated copper grid, which was left to stand for 24 h. Scanning Electron Microscopy (SEM) images were obtained using a Supra 35, Carl Zeiss, 3.0 kV. Powder samples were deposited on a carbon tape and the surface morphology was obtained at room temperature.Charges of the ES-PANI/Au NPs solutions were measured using a Zetasizer Nano ZS (Malvern) and a Titrator MPT-2. XRD patterns were collected with a Rigaku RotaFlex equipped with a graphite monochromator, operating with CuKα  radiation, 50 kV, and 100 mA. The data collection was recorded in the range of 2θ=5–70° with a step of 0.02° and 2 seconds/step. Fourier-Transformed Infrared spectroscopy (FTIR) was performed in the transmission mode on a Nexus 470 FTIR spectrometer. The spectra were obtained over 32 scans.


## 3. Results

Figure1(a) shows the TEM images of the Au-PAMAM NPs. It is possible to observe that the particles are distributed in a spherical shape. The corresponding histogram (Figure 1(b)) indicates a broad distribution ranging from 10 to 40 nm. The largest percentage corresponds to particles between 15 and 20 nm, representing 53%. Figure 2(a) shows the TEM images of the Au-CITRATE NPs. The corresponding histogram (Figure 2(b)) indicates a small nanoparticles sizes variation, showing that they are distributed, in similar percentage (50%) between 10 and 20 nm.(a) TEM images of the Au-PAMAM NPs and (b) Histogram of the Au size distribution.
(a)(b)(a) TEM images of the Au-CITRATE NPs and (b) Histogram of the Au size distribution.
(a)(b)The as-synthesized ES-PANI powder (Figure3) seems to have nanofibers morphology and showed a branched geometry. Figure 4 shows the Au-PAMAM NPs dispersed on the polymer chains, suggesting that the Au-PAMAM NPs, as expected, did not interact with the ES-PANI, preserving its chain conformation. Further, as shown in Figure 5, the composite formed by the interaction between ES-PANI and Au-CITRATE NPs presents different morphology as compared to the pure ES-PANI (Figure 3) and Au-CITRATE NPs (Figure 2(a)). The composite particles are larger than ES-PANI and Au-CITRATE NPs, suggesting that the polymer coated the Au-CITRATE NPs. While the exact formation mechanism of such nanostructures is not completely understood, SEM images show that the interaction between these materials promotes a formation of new composites.Figure 3
SEM images of as-synthesized ES-PANI powder.Figure 4
SEM images of the Au-PAMAM NPs dispersed on the ES-PANI chains.Figure 5
SEM images of the complex formed by the interaction between ES-PANI and Au-CITRATE NPs.Crystalline or semicrystalline polymers are two phase systems. The phase in which the polymer chains are ordered in close packed array is the crystalline region. The crystalline domains are connected to the amorphous regions. In the XRD patterns of Au NPs, Pham et al. (2011) found peaks at 38.21°, 44.33°, 64.58°, and 75.25°, which are assigned to face-centered cubic bulk gold [33]. ES-PANI powder showed broad peaks at 2θ=6, 9, 11, 15, 20, 25, 27, 29, 33, 36, and 52°, which indicate some degree of crystallinity (Figure 6(a)). When the Au-PAMAM NPs were added to the ES-PANI solution, the diffractogram did not present any variation regarding the crystallinity of the polymer semicrystalline phase (Figure 6(b)). XRD pattern of the complex containing ES-PANI and Au-CITRATE NPS is shown in Figure 6(c). It was observed that the addition of Au-CITRATE NPs changed the ES-PANI structure, making it more amorphous after the interaction. ES-PANI showed two broad peaks centered at 2θ=11.9 and 23.4°, which also are characteristic of the polyaniline [34]. Additional peaks at approximately 2θ=38, 44, and 65° represent, respectively, Bragg’s reflections from Au NPs [33] observed in addition to the peaks of ES-PANI. A suggested formation of the complexes is depicted in Figure 7.XRD patterns of (a) pure ES-PANI, (b) ES-PANI + Au-PAMAM NPs, and (c) complex containing ES-PANI + Au-CITRATE NPs.
(a)(b)(c)Figure 7
Representative structure of the complexes formation between the polymer chains and the Au-CITRATE NPs.The Zeta potentials are depicted in Table1. This measurement indicates the surface potential of the particles and was analyzed as a function of nanoparticles concentration. ES-PANI and Au-PAMAM show positive Zeta potential and Au-CITRATE shows negative zeta potential. After addition of Au-PAMAM to ES-PANI solution, there was observed an increase of the Zeta potential, suggesting no interactions due to the electrostatic repulsion. On the other hand, after adding 50 μL of Au-CITRATE to ES-PANI solution, the Zeta potential decreased from 42.0 to 32.2 mV, and after adding 500 μL, the values decreased to 11.4 mV, suggesting that the ES-PANI can form a coating on the surface of the Au-CITRATE NPs due to the attractive electrostatic interaction between the opposite charges.Table 1
Zeta Potential of ES-PANI solution as a function of volume of Au-PAMAM and Au-CITRATE NPs.
SamplesZeta Potential (mV)ES-PANI42.0Au-PAMAM NPs4.0ES-PANI + 50μL Au-PAMAM48.9ES-PANI + 100μL Au-PAMAM57.7ES-PANI + 500μL Au-PAMAM75.5Au-CITRATE NPs−31.7ES-PANI + 50μL Au-CITRATE32.2ES-PANI + 100μL Au-CITRATE27.8ES-PANI + 500μL Au-CITRATE11.4Figure8 shows the FTIR spectra of ES-PANI, Au-CITRATE, and ES-PANI with 50, 100, and 500 μL of Au-CITRATE and the formed complex. The vibrational bands observed for the ES-PANI at 1583 and 1493 cm−1 are assignable to the ring stretching vibration of quinoid and benzenoid, respectively [35, 36]. A 1299 cm−1 band was assignable to the C–N stretching of a secondary aromatic amine [37] and a 825 cm−1 band to an aromatic C–H out-of-plane-bending [38]. The 1130 cm−1 band is a vibrational mode of B–NH+=Q or B–NH+–B, which is formed in doping reactions [39]. When the concentration of Au-CITRATE was increased, there was noted the appearance of bands located at 1401 and 1584 cm−1 related, respectively, to the symmetric and antisimmetric stretching of COO−, which were not so clearly alike in pure Au-CITRATE [40]. With respect to the curve of the precipitate, it shows that there were interactions between the ES-PANI and Au-CITRATE NPs, suggesting that the formed material is a complex. These results suggest that C–N bonds within the polymer are directly influenced by the Au NPs, which are consistent with the donation of electron density from the metal to the C–N bond that are strongly perturbed by the presence of the Au NPs [41, 42].Figure 8
FTIR spectra of ES-PANI, Au-CITRATE, and ES-PANI with 50, 100, and 500μL of Au-CITRATE and the formed complex.Similarly, Figure9 shows the FTIR spectra for ES-PANI, Au-PAMAM, and ES-PANI with 50, 100, and 500 μL of Au-PAMAM. When the concentration of Au-PAMAM was increased, there was observed the appearance of bands located at 3275 cm−1 and 3072 cm−1 related to the presence of terminal primary amino groups [43]. The bands located at 2819 and 2945 cm−1 are related, respectively, to the symmetric and antisimmetric vibrations of CH2. The peaks at 1647 and 1562 cm−1 are assigned to the stretching vibration of amide I mainly C=O stretching vibrations and amide II due to the coupling of bending vibrate of N–H and stretching vibrate of C–N bands, respectively [44]. The spectra showed no structural change when different concentrations of Au-PAMAM are present in ES-PANI; so there was no precipitate.Figure 9
FTIR Spectra for ES-PANI, Au-PAMAM, and ES-PANI with 50, 100, and 500μL of Au-PAMAM.


## 4. Conclusions

We investigated the formation of hybrid composites containing polyaniline and Au NPs. As revealed by the decrease in zeta potential of the ES-PANI/Au-CITRATE, the polyaniline molecules were able to coat the Au-CITRATE NPs, due to the attractive electrostatic interaction between the opposite charges. The same argument applied to ES-PANI/Au-PAMAM indicates that the repulsive electrostatic interaction should avoid the formation of complexes. According to these results the interactions between ES-PANI and Au-CITRATE led to differences in their morphologies observed by SEM as well as the XRD pattern of the precipitate containing ES-PANI and Au-CITRATE NPs. The Au-CITRATE caused a structural change on ES-PANI chains, making them less crystalline, but did not affect the crystallinity of ES-PANI/Au-PAMAM.



---