# In Situ Formation of Carbon Nanomaterials on Bulk Metallic Materials

Authors: J. Y. Xu; X. C. Lei; R. Yang; Z. Z. Fan
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

Carbon nanomaterials were synthesized in situ on bulk 316L stainless steel, pure cobalt, and pure nickel by hybrid surface mechanical attrition treatment (SMAT). The microstructures of the treated samples and the resulted carbon nanomaterials were investigated by SEM and TEM characterizations. Different substrates resulted in different morphologies of products. The diameter of carbon nanomaterials is related to the size of the nanograins on the surface layer of substrates. The possible growth mechanism was discussed. Effects of the main parameters of the synthesis, including the carbon source and gas reactant composition, hydrogen, and the reaction temperature, were studied. Using hybrid SMAT is proved to be an effective way to synthesize carbon nanomaterials in situ on surfaces of metallic materials.


---

## Body

## 1. Introduction

Carbon nanofibers (CNFs) and nanotubes (CNTs) have attracted extensive attention in the scientific field because of their remarkable properties [1]. They are being investigated for a wide range of applications, especially for the promising applications in nanoelectronics and field emission devices [2–5]. To meet the requirements of the applications, it is anticipated to produce CNFs/CNTs directly on many substrates.Up to now, several methods have been studied to synthesize CNFs/CNTs on various substrates. In many cases, the hydrocarbons decomposed on dispersed catalytic metal particles on a support [6, 7]. Also the possibility to use the developed CVD methods to synthesize carbon nanomaterials directly on the transition metal surface that is catalytically active exists [8–11]. However, difficulties persist in making effective carbon nanomaterials directly on bulk metal surface using a simple technique with low cost.Surface mechanical attrition treatment (SMAT) has been proved to be an effective way to achieve surface nanocrystallization on various metallic materials [12–16] and can be used to accelerate the chemical reaction of a material surface. Great progress has been achieved in nitriding, chromizing, and synthesizing functional nanoproducts via SMAT [17–23]. Hence, we consider modifying the surface of the metallic materials by SMAT and taking it as the catalyst as well as the substrate for the fabrication of CNFs/CNTs. Carbon nanomaterials were successfully synthesized in situ on bulk titanium by hybrid SMAT process [24]. In this study, the traditional catalytic transition metallic materials (Fe in its alloy forms stainless steel, cobalt, and nickel) were subjected to hybrid SMAT process to synthesize carbon nanomaterials. The morphologies and structures of the obtained carbon nanomaterials were investigated. The possible growth mechanism was discussed. Effects of the main parameters of the synthesis were studied. Hybrid SMAT is proved to be an effective and low-cost way to synthesize carbon nanomaterials in situ on surfaces of metallic materials. It is anticipated to get large-scale carbon nanomaterials/metallic materials composites by using this method to meet the application requirements.


## 2. Materials and Methods

Samples were stainless steel (AISI 316L), pure cobalt (purity 99.9%), and pure nickel (purity 99.9%) plates. The plates were 20 mm in diameter and 1 mm in thickness and were firstly subjected to the SMAT process. Details of SMAT can be found in the previous work [15, 16]. After SMAT, a nanocrystalline surface layer was achieved. During SMAT process, a great amount of repeated and multidirectional impacts induce a severe plastic deformation (SPD) on the sample surface. Accordingly, grains of the surface layer were successfully refined from micrometer into nanometer. In the present work, the SMAT process was performed with a vibration frequency of 20 kHz for 30 min, using the shot with a diameter of 2 mm.Samples treated by SMAT (SMAT samples) were then subjected to a CVD process using a furnace with a quartz tube. The typical parameters were as follows. The reaction was maintained in 550°C for 30 min. The reactant gas composition is C2H2 : H2 = 50 SCCM (mL/min): 100 SCCM in a N2 carrier of 300 SCCM. The main parameters of CVD, including carbon source, gas reactant composition, and temperature, were studied.Transmission electron microscopy (TEM) observations were performed to characterize SMAT samples and the resulted carbon products using a Philips CM30 microscope working under 300 kV accelerated voltage.Scanning electron microscopy (SEM) was also used to investigate the microstructures of the carbon products, using a Sirion, FEI working at 3 kV accelerated voltage.


## 3. Results and Discussion

TEM characterizations indicate the microstructural features of the very top surface of SMAT transition metallic materials, as can be seen in Figure1.Bright-field (a, c, e) and dark-field (b, d, f) TEM images showing typical microstructures of the top surface layer in (a, b) SMAT 316L stainless steel; (c, d) SMAT Co; and (e, f) SMAT Ni. The insets are the corresponding SAED patterns.
(a)
(b)
(c)
(d)
(e)
(f)Although the mechanisms of the nanocrystallization of three metallic materials are not the same [16], there is no evident difference from the surface layer except for the grain size. After SMAT under the same parameters, cobalt exhibits the smallest average grain size (about 30 nm), followed in order by 316L stainless steel (about 70 nm) and nickel (about 110 nm) according to the TEM images. In spite of the grain size, the nanocrystalline surface layers of the SMAT metals exhibit similar appearance. On the very top surface, there are equiaxed nanograins with random crystallographic orientations, as shown by the inserted SAED patterns. Between this layer and the matrix, a transition layer with grain sizes increasing gradually is presented.After CVD process, thin black films were fabricated on SMAT 316L stainless steel and SMAT Co, while soft black products with a certain thickness were synthesized on SMAT Ni. No product was found in the untreated zone of samples. The carbon deposit yields were measured experimentally. SMAT Ni has the largest carbon deposit yield, up to 62.29 mg/cm2, followed in order by SMAT Co (16.4 mg/cm2) and SMAT 316L stainless steel (9.26 mg/cm2).We compared the morphologies of the carbon nanomaterials synthesized on different SMAT metals. Figure2 shows SEM images of carbon nanomaterials in connection with various substrates at different magnifications. The lower magnification pictures are used to convey the relative density and uniformity of nanofiber growth. The higher magnification pictures convey the relative morphology of the CNFs. It can be clearly seen that the morphologies and structures of the substrate-synthesized carbon nanostructures significantly depend on the type of substrate. CNFs synthesized on SMAT Co possess a fairly uniform size distribution of about 25 nm. In contrast to this, SMAT 316L stainless steel and SMAT Ni result in large diameter CNFs (more than 100 nm).Figure 2
Comparison of the morphology of carbon products synthesized on different SMAT metals: (a) on SMAT 316L, ×5 K; (b) on 316L, ×20 K; (c) on 316L, ×90 K; (d) on SMAT Co, ×5 K; (e) on SMAT Co, ×20 K; (f) on SMAT Co, ×90 K; (g) on SMAT Ni, ×5 K; (h) on SMAT Ni, ×20 K; and (i) on SMAT Ni, ×90 K.Besides the dimension, the morphologies are totally different. CNFs synthesized on SMAT 316L stainless steel are neither uniform nor dense, distributed among the metal clusters, with a broad diameter distribution ranging from tens of nanometers to several micrometers. Some of them appear to undergo a further partial and simultaneous change in shape, rotating on an axis perpendicular to the direction of fiber growth, and thus forcing the filament to a helical form (Figure2(c)). CNFs synthesized on SMAT Ni are straighter, longer, and even thicker than those grown on SMAT 316L stainless steel, tangled with microspheres (Figure 2(g)). The medium magnification (Figure 2(h)) reveals that the microspheres are composed of thin curly entangled fibers, twisted among the thick fibers. High magnification image revealed that the thick fibers synthesized on SMAT Ni are comprised of stacked graphene segments (Figure 2(i)). Unlike SMAT 316L stainless steel or SMAT Ni, SMAT Co results in quite uniform CNFs that entangle with each other, giving the appearance like dense grass in low magnification (Figure 2(d)). Twists are characteristic of the CNFs and no straight regions are observed (Figures 2(e) and 2(f)). In contrast to SMAT 316L stainless steel, occurrences of inactive metal articles appearing as isolated particles or clusters are rarely observed on SMAT Co and SMAT Ni.TEM characterizations were performed to establish the nature of the fibers observed in SEM. Figure3 shows the TEM images, which represent typical examples of the products synthesized on SMAT 316L stainless steel, SMAT Co, and SMAT Ni.Figure 3
TEM images of the CNFs synthesized on different SMAT metals (a) on SMAT 316L stainless steel; (c) on SMAT Co; (e) on SMAT Ni and the related HREM images of the CNFs synthesized (b) on SMAT 316L stainless steel; (d) on SMAT Co; (f) on SMAT Ni.As shown in Figure3(a), on the SMAT 316L stainless steel, a mixture of amorphous carbon and encapsulated particles is observed. Nanofibers are found stretched out from the mixture. Many metallic particles are still inactive toward nanofiber catalysis, becoming embedded. The catalysts are quasi-spherical metal particles with an average diameter of 60~70 nm, which is in accord with the results obtained by the TEM of the substrates (Figure 1(a)). As for SMAT Co, a significantly wide distribution in diameter and a greater variation in morphology are observed (Figure 3(c)). The fiber-like products are thin CNFs with an average diameter of about 25 nm. These CNFs are much thinner and more uniform than those synthesized on SMAT 316L stainless steel. Figure 2(d) also shows that the metal particles locate at the top ends of the nanofibers. Most of the pyrolysis products are thick CNFs showing either curved or straight shapes. Figure 3(e) shows the TEM views of typical CNFs synthesized on SMAT Ni, indicating thick CNFs of over 100 nm in diameter. The HREM image (Figure 3(f)) reveals that the nanofibers have a “herringbone” structure that consists of graphite sheet oriented at a specific angle to the fiber axis with an interlayer space of 0.34 nm. In addition to thick CNFs, thin CNTs are also observed in the products synthesized on SMAT Ni. It can be clearly seen from Figure 4(a) that thick fiber is twisted by uniform thin fibers, which is similar to the products reported by Ding et al., and so forth. using a Ni-Ni3P as a catalyst [25].Figure 4
TEM images of carbon products synthesized on SMAT Ni (a) image at low magnification showing CNTs as well as CNFs; (b) image at high magnification showing details of CNTs; and (c) image showing the presence of the catalyst particles as well as CNFs.The curly fibers are entangled with each other. The inset image is the corresponding SAED pattern. The higher magnification (Figure4(b)) revealed that those thin fibers are thin MWNTs with a diameter of about 10 nm and without any catalyst particle embedded at the tip. Thin CNTs are also observed stretched out from catalyst clusters, as can be seen from Figure 4(c). The observed metal particles are much bigger than the size of the carbon nanotubes. Therefore, it can be deduced that those thin CNTs are catalyzed by the thick CNFs rather than the Ni nanoparticles. Hollow thick CNFs are also found (Figure 3(e)).Corresponding to the grain size distributions of SMAT transition metals, the diameter distributions of CNFs are illustrated in Figure5. It is noted that the variation tendency of the CNFs sizes is similar to the variation of grain size of SMAT transition metals. However, in the cases of SMAT 316L stainless steel and SMAT Ni, the CNFs sizes are larger than the nanocrystalline grains.Figure 5
Average grain size of different SMAT metals and the average diameters of corresponding CNFs.Here we discuss a possible mechanism of the CNFs growth on the surface of SMAT metallic materials. The catalyst particles wrapped with graphite (Figure3(a)) and encapsulated in a CNF (Figure 3(d)) have been found through TEM observations. The experimental observations lead to the proposal that the CNFs growth follows the mechanism presented by Baker et al. [26]. It is supposed that when the hydrocarbon meets the front-exposed metal particle surface, it decomposes and releases active hydrogen and carbon atoms. The carbon atoms dissolve and diffuse through the metal particles and precipitate on the rear face to form the carbon filament. The catalytic ability of the transition metallic materials to form carbon nanomaterials is related to a combination of factors that include the catalytic activity for the decomposition of unstable carbon compounds such as hydrocarbon, the formation of metastable carbides, and the diffusion of carbon through the metal particles [27]. It is known that a large number of grain boundaries and other defects in nanocrystalline materials may serve as fast atomic diffusion channels for the diffusion. In the previous work [17–23], it was found that the high chemical reactivity of the nanocrystalline that attributes to numerous grain boundaries and a large excess energy in the form of nonequilibrium defects such as dislocations and subgrain boundaries that are induced by plastic deformation arouse a considerable driving force which is stored on the surface of SMAT metallic materials. At the same time, the high concentration of the nonequilibrium defects may decrease the activation energy of diffusion. Experiments have also proved that when the grain size is reduced to nanoscale and defects are induced by SPD, the chemical reaction kinetics will be enhanced severely during mechanical attrition of metals [28, 29]. As a result, the atomic diffusivities were greatly enhanced after SMAT. When carbon atoms diffuse into the surface layer of SMAT metallic materials, the nanocrystalline grains act as catalyst particles, providing nuclei for the carbon nanomaterials.Using hybrid SMAT is proved to be an effective way to synthesize carbon nanomaterials in situ on surfaces of metallic materials. However, the whole process and mechanism are rather complicated. Further studies are needed for understanding the principles so that we could control the diameter and the morphology of the CNFs by changing the parameters of hybrid SMAT process.Effects of the main parameters of the synthesis, including the carbon source, gas reactant composition, hydrogen, and the reaction temperature, were studied using SMAT Co. Similar phenomena were found in SMAT Ni and SMAT 316L stainless steel.Carbon source is considered to contribute to the special structure and the yield. A series of experiments has been done on SMAT Co using CH4 and C2H2 as carbon source.When using CH4 as carbon source, no evidence for the formation of filamentous carbon was observed upon SMAT Co in the temperature range 550–900°C, regardless of the CH4/H2/N2 ratio. This phenomenon can be explained; that is, CH4 is a most kinetically stable hydrocarbon and is hard to pyrolyze. CH4 does not decompose at lower temperature (e.g., 550°C), while at higher temperature (e.g., 900°C), the nanocrystalline grains on the SMAT metal surface grow up and exhibit no catalytic activity. On the other hand, C2H2 is much easier to decompose at lower temperature and therefore can be regarded as good carbon source in this work.Synthesis of carbon nanostructures is dependent on the reactant gas composition. The effect of the reactant composition on the carbon product is listed in Table1. Best results were obtained with flow rates of C2H2 and H2 of 50 SCCM and 100 SCCM, respectively, in a N2 carrier of 300 SCCM. The relative yield and purity of these nanofibers are highly dependent upon the relative C2H2 to H2 ratio and absolute C2H2 concentration. Gas mixture with lower C2H2 concentration is less active towards CNFs synthesis. Higher C2H2 results in higher yield of nanofibers, yet further increasing in the C2H2 concentration, led to deactivation of the catalyst nanoparticles.Table 1
Carbon products related to different gas composition.
Gas composition (C2H2 : H2 : N2, SCCM)
Related products
30 : 100 : 300
Medium yield of CNFs
50 : 100 : 300
Abundant CNFs
50 : 50 : 300
CNFs with amorphous carbon
100 : 100 : 300
CNFs with encapsulated metal particles
300 : 300 : 300
Encapsulated metal particles with few CNFsHydrogen is also proved to be critical in creating CNFs/CNTs. The influence of absence of H2 is evident. Without H2, the growth becomes sparse and irregular structures are prominent. However, extra H2 is proved similarly detrimental towards CNFs/CNTs growth. Figure 6 shows the SEM images of SMAT Co after CVD process with and without hydrogen. It is clearly shown that the presence of hydrogen obviously affects CNFs growth. There were sintered metal clusters when using 50 SCCM C2H2 and 300 SCCM N2 without any hydrogen but lots of uniform CNFs when 50 SCCM C2H2, 100 SCCM H2 and 300 SCCM N2 were supplied.Figure 6
SEM images of the carbon products synthesized on SMAT Co after CVD process (a) without hydrogen and (b) with hydrogen.As indicated in the literature [30], hydrogen serves several purposes within this growth process. Firstly, hydrogen can be regard as the promoter of the catalyst. It not only forms sufficient concentrations of hydrocarbons, but also satisfies unfilled carbon valencies at the precipitating rear facets of the metal catalyst. Thus, hydrogen can act to etch or remove surface-adsorbed carbon from the catalyst particle rather than accelerating soot formation [31]. Without this surface cleaning process, the catalyst tended to be easily covered by amorphous carbon and would be poisoned and lead to catalyst deactivation. It is particularly important where the rate of carbon deposition exceeds that of solvation. With hydrogen being supplied, the catalyst keeps active so that the decomposition, diffusion, and precipitation of carbon atoms work smoothly. Secondly, hydrogen has been postulated to be necessary to terminate dangling bonds located on edge-plane carbon atoms.The reaction temperature is proved to be a crucial parameter for the synthesis of CNFs/CNTs by CVD method. Since the temperature affects the activity of the catalytic metallic materials and the decomposition of the carbon source gases, the microstructure and the yield of CNFs/CNTs vary with the growth temperature [32]. A series of experiments has been done at temperature from 300°C to 900°C in order to examine the influences of reaction temperature. It is observed that the optimum conditions for reaction are realized at 550°C. The carbon yield at 550°C is 16.4 mg/cm2. If the temperature changes either above or below this point, this is a dramatically drop in the yield of the product. No product has been observed below 350°C or over 850°C. The reason is that C2H2 does not decompose at the temperature below 350°C, while high temperature results in the growth of the nanograins on the surface layer, leading to catalytic deactivation.


## 4. Conclusions

Carbon nanomaterials have been successfully synthesized in situ on various bulk metallic materials by hybrid SMAT. CNFs were formed on SMAT 316L stainless steel and SMAT Co while CNFs and CNTs were formed on SMAT Ni. SMAT Ni is the most active one compared with SMAT Co and SMAT 316L stainless steel and has the largest carbon deposit yield. Different SMAT metals resulted in different morphologies of products. The diameter of CNFs is related to the size of the nanograins on the surface layer of SMAT metals. The possible growth mechanism was discussed. The atomic diffusivities were greatly enhanced after SMAT and the nanocrystalline grains act as catalyst particles, being nuclei for the carbon nanomaterials. Effects of the main parameters including the carbon sources, gas reactant compositions, hydrogen, and reactant temperature were also investigated. The optimized gas reactant composition is C2H2 : H2 : N2 = 50 SCCM : 100 SCCM : 300 SCCM. The appropriate reaction temperature is 550°C.



---

*Source: 690630-2014-03-11.xml*