# Research on the Seismic Performance of Straw Panel-Infilled Concrete Frame by Shaking Table Test

Authors: Jia Zhu; Yuling Bian; Aiping Zhou
Journal: Advances in Civil Engineering
 (2021)

---

## Abstract

Infill wall-frame interaction-induced damage and failure have been found in many previous earthquakes due to the inappropriate estimation of the stiffness of infill walls. It is a common knowledge of design philosophy that properly lowering the lateral stiffness of infill wall may significantly improve the seismic performances of concrete frames. Fabricated straw wall, a sandwich-type structure with tenon and groove, is proposed as a new type of lightweight and environment-friendly infill wall. The lateral stiffness is much lower than that of masonry infill wall. Shaking table tests were carried out for a concrete frame structure with fabricated straw wall, as well as for a frame with masonry infill wall for comparison. Results show that failure modes of them are different. Plastic hinges took place at the ends of beams in the frame with fabricated straw infill wall, different from the frame with masonry infill wall where the plastic hinges emerged at the ends of columns. Numerical analysis was conducted to verify and illustrate the failure mechanism. It indicates that the straw panel-infilled concrete frame well matches the design philosophy and presents better seismic performance.


---

## Body

## 1. Introduction

Masonry infill wall used as partial wall of reinforced concrete frame structures is usually treated as the nonstructural component in design philosophy. However, masonry infill wall exerts a significant effect on the stiffness of frame structures [1–4] and the structural dynamic performances [5]. Design codes [6, 7] take a natural vibration period reduction factor to account for the stiffness contribution of the masonry infill walls; e.g., the factor is specified as 0.6–0.9 by the Chinese code [7].The current design philosophy poses serious problems, as it did in the case of Wenchuan earthquake. On May 12, 2008, an Ms8.0 earthquake struck Wenchuan area where masonry infill wall is extensively adopted. A 3-story building of frame structure in Beichuan is shown in Figure1 [8]. To set street shops for the building, few infill walls were set on the ground floor, while many infill walls were arranged on other floors, making the ground floor much weaker than other layers. Finally, all the bottom columns broke at ends, and the whole building inclined dramatically. The same type of failure is presented in Figure 2 [9]. It is a damaged column of a 6-story building in Dujiangyan city. Its ground floor acted as a garage with no walls. Infill walls on the upper floors made the stiffness vary greatly between the first and second story, so the damage of bottom columns occurred.Figure 1
Damage of a 3-story frame structure [8].Figure 2
Damage of the bottom columns of a 6-story building [9].Witnessing all these damages and failure induced by the interaction between the masonry infill wall and concrete frame [2, 4, 9], the significant role of masonry infill walls in frame structures is gradually realized. Related experiments [10–12] and numerical analyses [13–15] are conducted by different scholars. Some codes [16, 17] recommend struts to represent masonry infill walls in calculations. However, due to the scattered data offered by different experiments, along with the difficulty in modeling brittle materials [18], a widely accepted method to precisely consider the masonry stiffness is still absent.To eliminate the great disparity in lateral stiffness between stories generated by masonry infill walls, arranging masonry infill walls equivalently on each story is a simple way. However, this method is generally not practical, since the main entrances, garage, or stores are often set on the first floor. Due to the need for rational use of space, the layout of masonry infill walls on first floor is quite limited. An effective approach is to lower the stiffness of the masonry infill wall directly. Either decreasing their total number or replacing the masonry with other proper materials would work. By proposing a sandwich-type of fabricated straw panel, the latter method is chosen and studied.


## 2. Fabricated Straw Brick

To properly replace the masonry bricks, a sandwich-type of fabricated straw panel is advanced. With a low elastic modulus [19], straw panels own much lower stiffness compared with masonry bricks [20]. Due to the flexible tenon connection between straw panel and frame, a certain deformation is allowed under horizontal loads and actions. Thus, the interaction between the straw panel infill wall and concrete frame is weak. It also shares the characteristics of sound insulation and self-heat insulation [21–24]. Meanwhile, the straw panels are remarkably fire-resistant considering the compactness [25].The proposed straw panel is a sandwich structure with tenon and groove, consisting of a low-density straw board (ρ≤400 kg/m3) and 2 high-density straw boards (ρ≥700 kg/m3). The low-density board with good thermal insulation and sound insulation performance is used as the lining, of which 2 high-density boards are placed on both sides. The lower end of the low-density lining board is a groove. The high-density outer panel and the low-density lining board are staggered to form a tenon and groove. Considering the requirements of the building modulus and the conditions in the transportation and construction process, the size of the straw panel is decided as shown in Figure 3.Figure 3
Geometrical sizes of a straw brick (unit: mm).Shaking table tests were carried out for a straw panel-infilled frame, as well as for a masonry infilled frame for comparison, to study their seismic performance.


## 3. Experimental Investigation

### 3.1. Experimental Design

#### 3.1.1. Similitude of the Model

Scale models are used in the shaking table tests, which are representative of the prototype structure according to a certain similar relationship. The designed similitude of model is presented in Table1.Table 1
Designed similitude of the model.
TypePhysical propertiesDimensionSimilitudeSimilarity constantMaterial featuresStressFL−2Sσ=SE1Modulus of elasticityFL−2SE1Mass densityFT2L−4Sρ=SE/Sl3Geometrical featuresLengthLSl1/3Dynamic featuresMassFL−2T2Sm=SρSl31/9StiffnessFL−1Sk=SESl1/3AccelerationLT−2Sa=Sl/St21


#### 3.1.2. Experimental Model Design

The test models of the frame structures are 1/3 scale models of the prototype structure. Two identical reinforced concrete frames are designed for comparison. Each frame is a 1-bay, 3-story structure, filled with masonry bricks or straw panels, respectively. All frame beams, columns, and floor (roof) panels are cast-in-place.In order to ensure the consistency of these 2 concrete frames, synchronous construction and simultaneous pouring are adopted, and each layer of steel and concrete is obtained from the same batch of materials. (For the convenience of description in this article, the frame with masonry bricks is called brick frame, and the frame with straw panels is called straw frame.) The geometrical sizes of models are presented in Tables2 and 3 .Table 2
Geometrical sizes of models (unit: m).
StructureLengthWidthHeightPrototype structure4.54.59Test structures1.51.53Table 3
Geometrical sizes of components (unit: mm).
StructureColumnBeamSlabHcBcHbBbPrototype structure300300300150120Test structures10010010050100According to the Chinese Code for Design of Concrete Structures [26], the component layout and the reinforcement diagrams of components in the test structures are designed and shown in Figures 4–6 . The straw brick is presented in Figures 3 and 7, and the photo of test structures is shown in Figure 8.Figure 4
Front elevation view of test structures (unit: mm).Figure 5
Reinforcement diagram of floor slab (unit: mm).Figure 6
Reinforcement diagrams of columns and beams (unit: mm). (a) Column. (b) Beam.
(a)(b)Figure 7
The straw brick.Figure 8
Test structures on shaking table.


#### 3.1.3. Construction and Installation of Infill Walls

As the brick frame is filled with masonry bricks, its infill wall was constructed in accordance with the requirements of the Chinese current code [27].There are currently no relevant regulations or specifications as references for straw frame, so the installation plan was determined based on the principle of structural stability, the geometrical sizes of straw brick, and the suggestions of the manufacturer’s technicians. Figure9 illustrates the connections between straw components and frame; specific installation steps are as follows:(1)
While the straw bricks with tenon and groove are easy to connect with each other vertically, vertical long straw strips were needed to link the boards horizontally with air nails to enhance the integrity of the straw wall. The straw strips, with the basic geometric size of 120 mm × 18 mm × 900 mm, could be perfectly stuck between two horizontally adjacent straw boards, as shown in Figure9.(2)
Straw strips and frame beams are fixed by embedded parts to avoid slipping and falling off during the vibration. The 10-centimeter-long steel bars in Figure9 acted as the embedded parts whose diameter is 12 mm. Proper holes were reserved at the ends of the straw strips for the embedded parts.(3)
To prevent the straw wall from falling off or tilting out of the frame, steel plates were used to fix the straw wall to the frame. The steel plates were coated with glue to ensure the connection between the straw wall and frame.(4)
In order to guarantee the connections, all straw components were checked before installation, those of which with large deviation in geometrical sizes were screened out.(5)
The installation order from bottom to top and from right to left was followed to ensure that the first straw board at the floor level fits the floor correctly, and that straw boards fits well with the neighboring straw strips.(6)
By conducting the above steps, construction deviation accumulated on the last row of straw boards. Standard straw boards were cut on-site to ensure that the size of the last row and column meets the requirements.(7)
After all installations were complete, the straw strips and straw boards were connected with air nails. 20 mm air nails with an interval of 10 cm were adopted.Figure 9
Connections between straw components and frame.


#### 3.1.4. Experimental Materials

The parameters of experimental materials are shown in Table4.Table 4
Parameters of experimental materials.
MaterialConcreteSteelMasonry brickMortarStraw brickStraw stripElastic modulus (MPa)GradeDensityDensityParameterC25HPB2352400MU10M5559 kg/m3700 kg/m3


### 3.2. Shaking Table Test

#### 3.2.1. Apparatus

This test was carried out on the earthquake simulation shaking table of the Civil Engineering Test Center in Southeast University. The vibration table is an assembled single-degree-of-freedom seismic simulation vibration table, which is mainly composed of a foundation, a table, a dynamic actuator, a controller, an oil source system, and a data acquisition and analysis system.


#### 3.2.2. Spectrum Waves and Load Cases

According to the Chinese current code [7], 3 seismic waves were selected as the input waves in the experiment, namely, the EL Centro wave, the Taft wave, and an artificial wave. In the experiment, the seismic waves are firstly scaled with the acceleration peak value according to the working conditions. And the duration is compressed according to the similar coefficient, which is 23.2 s at last. All of them then work as the excitation input for the test.During the test, the EL Centro wave, Taft wave, and the artificial wave were successively input in one way horizontally. White noise with a peak acceleration of 35 cm/s2 was employed before and after each stage to test the dynamic characteristics of the structures. Ground motions were selected based on the Chinese current code [7] for research. The testing cases are presented in Table 5.Table 5
Testing cases.
StageCase no.Input wavePeak acceleration (cm/s2)StageCase no.Input wavePeak acceleration (cm/s2)Target valueMeasured valueTarget valueMeasured value11White noise3548517White noise35422EL Centro352818EL Centro4004933Taft354919Taft4004054Artificial wave356420Artificial wave40027825White noise3540621White noise35476EL Centro709222EL Centro6205317Taft7010723Taft6205398Artificial wave7014424Artificial wave62053139White noise3545725White noise353910EL Centro14021426EL Centro80053011Taft14021627Taft80056212Artificial wave14020628White noise3559413White noise354329EL Centro110057614EL Centro22028030Taft110071515Taft22041716Artificial wave220348


#### 3.2.3. Measuring Point Layout and Data Collection

After the models had been installed, the measuring points were arranged. 7 magnetic accelerometers (numbered a1–a7) and 7 pull-wire displacement meters (numbered D1–D7) were employed during the tests. An acceleration sensor and a displacement meter were arranged on the ② axis and ④ axis of each floor elevation, roof, and vibration table base of the models, as shown in Figure10.Figure 10
Layout of measuring point.The AdCRAS dynamic data collection system developed by Nanjing Anzheng Software Company was adopted in the test. The system is able to collect the acceleration and displacement response of the model under various working conditions. The sensitivity of acceleration sensor and displacement meter is shown in Table6.Table 6
Sensitivity and measuring range of sensors.
AccelerometerDisplacement meterMeasuring pointSensitivity (mV/m·s2)Measuring pointSensitivity (V/m)Measuring range (mm)a110.02D16.21750a29.92D26.15750a39.90D36.13750a410.16D46.08750a59.92D54.581000a610.38D64.571000a710.22D74.571000


### 3.3. Test Results and Discussion

#### 3.3.1. Experimental Observations

In the case of gradually increasing the peak acceleration of seismic waves, the occurrence and specific development of cracks are explained as follows:(1)
Under the Peak Ground Acceleration (PGA) of 35 cm/s2, the horizontal shaking of the models was inconspicuous. No visible cracks appeared on the models.(2)
Under the PGA of 70 cm/s2, cracks appeared at the bottom of the brick frame beams, and tiny cracks took place at the top of the bottom columns.(3)
Under the PGA of 140 cm/s2, previous cracks expanded with low amplitude, and a few horizontal cracks appeared at the top of the bottom column in the brick frame.(4)
Under the PGA of 220 cm/s2, micro cracks on the top of the bottom column in the brick frame began to expand, and cracks appeared in all four columns with a maximum length of 6 cm. Meanwhile, diagonal cracks took place in both ends of the 1st floor beams in the straw frame, as shown in Figure 11.(5)
Under the PGA of 400 cm/s2, top cracks of bottom column in brick frame continued expanding, some of which expanded to the full section. Meanwhile, micro cracks appeared on top of the column in the second story. Cracks in the 1st floor beam of the straw frame expanded, especially in the beams along the shaking direction. During vibration, the gap between straw panels and beams caused by the deformation of the straw frame was observed.(6)
Under the PGA of 620 cm/s2, cracks on the bottom column in the brick frame all extended to the full cross section; the maximum width of which is 2 mm. Cracks in the beams of the 1st and 2nd floor of the straw frame grew, and those of the 1st floor even extended to the full cross section.(7)
Under the PGA of 800 cm/s2, the width of the cracks on the bottom column in the brick frame increased to 3 mm, and cracks appeared at the bottom of some columns. The maximum width of the crack at the beam ends in the straw frame is about 2 mm. The gap between the straw panels and the columns at the top story was between 3 cm and 5 cm.(8)
Under 1100 cm/s2, the bottom columns in the brick frame were twisted, the top of which showed obvious plastic hinge characteristics. The bottom columns in the straw frame twisted in a low amplitude. The local cracks of the brick wall were slightly developed, and the overall performance was good. The straw wall of the top layer of the A axis showed an outward inclining trend. At 1400 cm/s2, the maximum width of cracks in the bottom column in the brick frame is around 5 mm, as shown in Figure 12. The cracks in the brick walls still developed locally and the walls still presented good integrity. The cracks at the beam ends on the 1st floor of the straw frame are about 3 mm, which all extended to the full sections. The straw wall at the top of axis A was about to crumble. At 1800 cm/s2, displacement of the top layer in brick frame became too big. As the bottom column broke, the brick frame overturned as a whole, as shown in Figure 13. Straw frame remained intact.Figure 11
Diagonal cracks in a beam of straw frame.Figure 12
Crack in the bottom column of brick frame.Figure 13
Crumble of the brick frame.


#### 3.3.2. Dynamic Characteristics of Structure

White noise was input on the table before and after the earthquakes at different cases. By performing frequency spectrum analysis on the horizontal acceleration data collected by the acceleration sensor under the action of white noise, the amplitude-frequency curve of the transfer function was acquired. So, the frequencies and damping ratios of the structures were obtained, which are shown in Figures14 and 15 .Figure 14
The frequencies of models in different cases.Figure 15
Damping ratios of models in different cases.Results show that the attenuation law of the first-order frequency of the two models is basically the same, but the main reasons for the stiffness loss of the testing structures are different. It is also deduced from the damping ratios curve that the straw frame consumes more energy than the brick frame. Apparently, the straw frame with flexible connection has strong energy consumption capacity and is safer than brick frame structure under the action of big earthquakes.


#### 3.3.3. Structural Displacement Response

The maximum interstory displacements and story drifts are shown in Table7.Table 7
Maximum interstory displacements and story drifts.
Peak acceleration (cm/s2)Brick frameFloor numberStraw frameFloor numberMax interstory displacement (mm)Max story driftMax interstory displacement (mm)Max story drift350.491/204110.481/20831700.551/181810.761/131612200.721/138910.831/120534000.831/120511.031/97136201.071/93511.851/54118002.391/41812.771/3611Results show that the max inter story displacements in the brick frame are generally smaller than those of the straw frame under the same lateral actions, due to the extra stiffness the masonry wall brings. It is not difficult to explain why the max story displacements occurred in the first story of the brick wall, while max story displacements appeared in the first and third story of the straw frame. Because masonry walls offered extra stiffness, and restricted the deformation of brick frame, this makes the 1st layer much weaker, as no bricks are arranged there. Straw walls, however, brought little extra stiffness to the original structure, hardly affecting the deformation of straw frame.


## 3.1. Experimental Design

### 3.1.1. Similitude of the Model

Scale models are used in the shaking table tests, which are representative of the prototype structure according to a certain similar relationship. The designed similitude of model is presented in Table1.Table 1
Designed similitude of the model.
TypePhysical propertiesDimensionSimilitudeSimilarity constantMaterial featuresStressFL−2Sσ=SE1Modulus of elasticityFL−2SE1Mass densityFT2L−4Sρ=SE/Sl3Geometrical featuresLengthLSl1/3Dynamic featuresMassFL−2T2Sm=SρSl31/9StiffnessFL−1Sk=SESl1/3AccelerationLT−2Sa=Sl/St21


### 3.1.2. Experimental Model Design

The test models of the frame structures are 1/3 scale models of the prototype structure. Two identical reinforced concrete frames are designed for comparison. Each frame is a 1-bay, 3-story structure, filled with masonry bricks or straw panels, respectively. All frame beams, columns, and floor (roof) panels are cast-in-place.In order to ensure the consistency of these 2 concrete frames, synchronous construction and simultaneous pouring are adopted, and each layer of steel and concrete is obtained from the same batch of materials. (For the convenience of description in this article, the frame with masonry bricks is called brick frame, and the frame with straw panels is called straw frame.) The geometrical sizes of models are presented in Tables2 and 3 .Table 2
Geometrical sizes of models (unit: m).
StructureLengthWidthHeightPrototype structure4.54.59Test structures1.51.53Table 3
Geometrical sizes of components (unit: mm).
StructureColumnBeamSlabHcBcHbBbPrototype structure300300300150120Test structures10010010050100According to the Chinese Code for Design of Concrete Structures [26], the component layout and the reinforcement diagrams of components in the test structures are designed and shown in Figures 4–6 . The straw brick is presented in Figures 3 and 7, and the photo of test structures is shown in Figure 8.Figure 4
Front elevation view of test structures (unit: mm).Figure 5
Reinforcement diagram of floor slab (unit: mm).Figure 6
Reinforcement diagrams of columns and beams (unit: mm). (a) Column. (b) Beam.
(a)(b)Figure 7
The straw brick.Figure 8
Test structures on shaking table.


### 3.1.3. Construction and Installation of Infill Walls

As the brick frame is filled with masonry bricks, its infill wall was constructed in accordance with the requirements of the Chinese current code [27].There are currently no relevant regulations or specifications as references for straw frame, so the installation plan was determined based on the principle of structural stability, the geometrical sizes of straw brick, and the suggestions of the manufacturer’s technicians. Figure9 illustrates the connections between straw components and frame; specific installation steps are as follows:(1)
While the straw bricks with tenon and groove are easy to connect with each other vertically, vertical long straw strips were needed to link the boards horizontally with air nails to enhance the integrity of the straw wall. The straw strips, with the basic geometric size of 120 mm × 18 mm × 900 mm, could be perfectly stuck between two horizontally adjacent straw boards, as shown in Figure9.(2)
Straw strips and frame beams are fixed by embedded parts to avoid slipping and falling off during the vibration. The 10-centimeter-long steel bars in Figure9 acted as the embedded parts whose diameter is 12 mm. Proper holes were reserved at the ends of the straw strips for the embedded parts.(3)
To prevent the straw wall from falling off or tilting out of the frame, steel plates were used to fix the straw wall to the frame. The steel plates were coated with glue to ensure the connection between the straw wall and frame.(4)
In order to guarantee the connections, all straw components were checked before installation, those of which with large deviation in geometrical sizes were screened out.(5)
The installation order from bottom to top and from right to left was followed to ensure that the first straw board at the floor level fits the floor correctly, and that straw boards fits well with the neighboring straw strips.(6)
By conducting the above steps, construction deviation accumulated on the last row of straw boards. Standard straw boards were cut on-site to ensure that the size of the last row and column meets the requirements.(7)
After all installations were complete, the straw strips and straw boards were connected with air nails. 20 mm air nails with an interval of 10 cm were adopted.Figure 9
Connections between straw components and frame.


### 3.1.4. Experimental Materials

The parameters of experimental materials are shown in Table4.Table 4
Parameters of experimental materials.
MaterialConcreteSteelMasonry brickMortarStraw brickStraw stripElastic modulus (MPa)GradeDensityDensityParameterC25HPB2352400MU10M5559 kg/m3700 kg/m3


## 3.1.1. Similitude of the Model

Scale models are used in the shaking table tests, which are representative of the prototype structure according to a certain similar relationship. The designed similitude of model is presented in Table1.Table 1
Designed similitude of the model.
TypePhysical propertiesDimensionSimilitudeSimilarity constantMaterial featuresStressFL−2Sσ=SE1Modulus of elasticityFL−2SE1Mass densityFT2L−4Sρ=SE/Sl3Geometrical featuresLengthLSl1/3Dynamic featuresMassFL−2T2Sm=SρSl31/9StiffnessFL−1Sk=SESl1/3AccelerationLT−2Sa=Sl/St21


## 3.1.2. Experimental Model Design

The test models of the frame structures are 1/3 scale models of the prototype structure. Two identical reinforced concrete frames are designed for comparison. Each frame is a 1-bay, 3-story structure, filled with masonry bricks or straw panels, respectively. All frame beams, columns, and floor (roof) panels are cast-in-place.In order to ensure the consistency of these 2 concrete frames, synchronous construction and simultaneous pouring are adopted, and each layer of steel and concrete is obtained from the same batch of materials. (For the convenience of description in this article, the frame with masonry bricks is called brick frame, and the frame with straw panels is called straw frame.) The geometrical sizes of models are presented in Tables2 and 3 .Table 2
Geometrical sizes of models (unit: m).
StructureLengthWidthHeightPrototype structure4.54.59Test structures1.51.53Table 3
Geometrical sizes of components (unit: mm).
StructureColumnBeamSlabHcBcHbBbPrototype structure300300300150120Test structures10010010050100According to the Chinese Code for Design of Concrete Structures [26], the component layout and the reinforcement diagrams of components in the test structures are designed and shown in Figures 4–6 . The straw brick is presented in Figures 3 and 7, and the photo of test structures is shown in Figure 8.Figure 4
Front elevation view of test structures (unit: mm).Figure 5
Reinforcement diagram of floor slab (unit: mm).Figure 6
Reinforcement diagrams of columns and beams (unit: mm). (a) Column. (b) Beam.
(a)(b)Figure 7
The straw brick.Figure 8
Test structures on shaking table.


## 3.1.3. Construction and Installation of Infill Walls

As the brick frame is filled with masonry bricks, its infill wall was constructed in accordance with the requirements of the Chinese current code [27].There are currently no relevant regulations or specifications as references for straw frame, so the installation plan was determined based on the principle of structural stability, the geometrical sizes of straw brick, and the suggestions of the manufacturer’s technicians. Figure9 illustrates the connections between straw components and frame; specific installation steps are as follows:(1)
While the straw bricks with tenon and groove are easy to connect with each other vertically, vertical long straw strips were needed to link the boards horizontally with air nails to enhance the integrity of the straw wall. The straw strips, with the basic geometric size of 120 mm × 18 mm × 900 mm, could be perfectly stuck between two horizontally adjacent straw boards, as shown in Figure9.(2)
Straw strips and frame beams are fixed by embedded parts to avoid slipping and falling off during the vibration. The 10-centimeter-long steel bars in Figure9 acted as the embedded parts whose diameter is 12 mm. Proper holes were reserved at the ends of the straw strips for the embedded parts.(3)
To prevent the straw wall from falling off or tilting out of the frame, steel plates were used to fix the straw wall to the frame. The steel plates were coated with glue to ensure the connection between the straw wall and frame.(4)
In order to guarantee the connections, all straw components were checked before installation, those of which with large deviation in geometrical sizes were screened out.(5)
The installation order from bottom to top and from right to left was followed to ensure that the first straw board at the floor level fits the floor correctly, and that straw boards fits well with the neighboring straw strips.(6)
By conducting the above steps, construction deviation accumulated on the last row of straw boards. Standard straw boards were cut on-site to ensure that the size of the last row and column meets the requirements.(7)
After all installations were complete, the straw strips and straw boards were connected with air nails. 20 mm air nails with an interval of 10 cm were adopted.Figure 9
Connections between straw components and frame.


## 3.1.4. Experimental Materials

The parameters of experimental materials are shown in Table4.Table 4
Parameters of experimental materials.
MaterialConcreteSteelMasonry brickMortarStraw brickStraw stripElastic modulus (MPa)GradeDensityDensityParameterC25HPB2352400MU10M5559 kg/m3700 kg/m3


## 3.2. Shaking Table Test

### 3.2.1. Apparatus

This test was carried out on the earthquake simulation shaking table of the Civil Engineering Test Center in Southeast University. The vibration table is an assembled single-degree-of-freedom seismic simulation vibration table, which is mainly composed of a foundation, a table, a dynamic actuator, a controller, an oil source system, and a data acquisition and analysis system.


### 3.2.2. Spectrum Waves and Load Cases

According to the Chinese current code [7], 3 seismic waves were selected as the input waves in the experiment, namely, the EL Centro wave, the Taft wave, and an artificial wave. In the experiment, the seismic waves are firstly scaled with the acceleration peak value according to the working conditions. And the duration is compressed according to the similar coefficient, which is 23.2 s at last. All of them then work as the excitation input for the test.During the test, the EL Centro wave, Taft wave, and the artificial wave were successively input in one way horizontally. White noise with a peak acceleration of 35 cm/s2 was employed before and after each stage to test the dynamic characteristics of the structures. Ground motions were selected based on the Chinese current code [7] for research. The testing cases are presented in Table 5.Table 5
Testing cases.
StageCase no.Input wavePeak acceleration (cm/s2)StageCase no.Input wavePeak acceleration (cm/s2)Target valueMeasured valueTarget valueMeasured value11White noise3548517White noise35422EL Centro352818EL Centro4004933Taft354919Taft4004054Artificial wave356420Artificial wave40027825White noise3540621White noise35476EL Centro709222EL Centro6205317Taft7010723Taft6205398Artificial wave7014424Artificial wave62053139White noise3545725White noise353910EL Centro14021426EL Centro80053011Taft14021627Taft80056212Artificial wave14020628White noise3559413White noise354329EL Centro110057614EL Centro22028030Taft110071515Taft22041716Artificial wave220348


### 3.2.3. Measuring Point Layout and Data Collection

After the models had been installed, the measuring points were arranged. 7 magnetic accelerometers (numbered a1–a7) and 7 pull-wire displacement meters (numbered D1–D7) were employed during the tests. An acceleration sensor and a displacement meter were arranged on the ② axis and ④ axis of each floor elevation, roof, and vibration table base of the models, as shown in Figure10.Figure 10
Layout of measuring point.The AdCRAS dynamic data collection system developed by Nanjing Anzheng Software Company was adopted in the test. The system is able to collect the acceleration and displacement response of the model under various working conditions. The sensitivity of acceleration sensor and displacement meter is shown in Table6.Table 6
Sensitivity and measuring range of sensors.
AccelerometerDisplacement meterMeasuring pointSensitivity (mV/m·s2)Measuring pointSensitivity (V/m)Measuring range (mm)a110.02D16.21750a29.92D26.15750a39.90D36.13750a410.16D46.08750a59.92D54.581000a610.38D64.571000a710.22D74.571000


## 3.2.1. Apparatus

This test was carried out on the earthquake simulation shaking table of the Civil Engineering Test Center in Southeast University. The vibration table is an assembled single-degree-of-freedom seismic simulation vibration table, which is mainly composed of a foundation, a table, a dynamic actuator, a controller, an oil source system, and a data acquisition and analysis system.


## 3.2.2. Spectrum Waves and Load Cases

According to the Chinese current code [7], 3 seismic waves were selected as the input waves in the experiment, namely, the EL Centro wave, the Taft wave, and an artificial wave. In the experiment, the seismic waves are firstly scaled with the acceleration peak value according to the working conditions. And the duration is compressed according to the similar coefficient, which is 23.2 s at last. All of them then work as the excitation input for the test.During the test, the EL Centro wave, Taft wave, and the artificial wave were successively input in one way horizontally. White noise with a peak acceleration of 35 cm/s2 was employed before and after each stage to test the dynamic characteristics of the structures. Ground motions were selected based on the Chinese current code [7] for research. The testing cases are presented in Table 5.Table 5
Testing cases.
StageCase no.Input wavePeak acceleration (cm/s2)StageCase no.Input wavePeak acceleration (cm/s2)Target valueMeasured valueTarget valueMeasured value11White noise3548517White noise35422EL Centro352818EL Centro4004933Taft354919Taft4004054Artificial wave356420Artificial wave40027825White noise3540621White noise35476EL Centro709222EL Centro6205317Taft7010723Taft6205398Artificial wave7014424Artificial wave62053139White noise3545725White noise353910EL Centro14021426EL Centro80053011Taft14021627Taft80056212Artificial wave14020628White noise3559413White noise354329EL Centro110057614EL Centro22028030Taft110071515Taft22041716Artificial wave220348


## 3.2.3. Measuring Point Layout and Data Collection

After the models had been installed, the measuring points were arranged. 7 magnetic accelerometers (numbered a1–a7) and 7 pull-wire displacement meters (numbered D1–D7) were employed during the tests. An acceleration sensor and a displacement meter were arranged on the ② axis and ④ axis of each floor elevation, roof, and vibration table base of the models, as shown in Figure10.Figure 10
Layout of measuring point.The AdCRAS dynamic data collection system developed by Nanjing Anzheng Software Company was adopted in the test. The system is able to collect the acceleration and displacement response of the model under various working conditions. The sensitivity of acceleration sensor and displacement meter is shown in Table6.Table 6
Sensitivity and measuring range of sensors.
AccelerometerDisplacement meterMeasuring pointSensitivity (mV/m·s2)Measuring pointSensitivity (V/m)Measuring range (mm)a110.02D16.21750a29.92D26.15750a39.90D36.13750a410.16D46.08750a59.92D54.581000a610.38D64.571000a710.22D74.571000


## 3.3. Test Results and Discussion

### 3.3.1. Experimental Observations

In the case of gradually increasing the peak acceleration of seismic waves, the occurrence and specific development of cracks are explained as follows:(1)
Under the Peak Ground Acceleration (PGA) of 35 cm/s2, the horizontal shaking of the models was inconspicuous. No visible cracks appeared on the models.(2)
Under the PGA of 70 cm/s2, cracks appeared at the bottom of the brick frame beams, and tiny cracks took place at the top of the bottom columns.(3)
Under the PGA of 140 cm/s2, previous cracks expanded with low amplitude, and a few horizontal cracks appeared at the top of the bottom column in the brick frame.(4)
Under the PGA of 220 cm/s2, micro cracks on the top of the bottom column in the brick frame began to expand, and cracks appeared in all four columns with a maximum length of 6 cm. Meanwhile, diagonal cracks took place in both ends of the 1st floor beams in the straw frame, as shown in Figure 11.(5)
Under the PGA of 400 cm/s2, top cracks of bottom column in brick frame continued expanding, some of which expanded to the full section. Meanwhile, micro cracks appeared on top of the column in the second story. Cracks in the 1st floor beam of the straw frame expanded, especially in the beams along the shaking direction. During vibration, the gap between straw panels and beams caused by the deformation of the straw frame was observed.(6)
Under the PGA of 620 cm/s2, cracks on the bottom column in the brick frame all extended to the full cross section; the maximum width of which is 2 mm. Cracks in the beams of the 1st and 2nd floor of the straw frame grew, and those of the 1st floor even extended to the full cross section.(7)
Under the PGA of 800 cm/s2, the width of the cracks on the bottom column in the brick frame increased to 3 mm, and cracks appeared at the bottom of some columns. The maximum width of the crack at the beam ends in the straw frame is about 2 mm. The gap between the straw panels and the columns at the top story was between 3 cm and 5 cm.(8)
Under 1100 cm/s2, the bottom columns in the brick frame were twisted, the top of which showed obvious plastic hinge characteristics. The bottom columns in the straw frame twisted in a low amplitude. The local cracks of the brick wall were slightly developed, and the overall performance was good. The straw wall of the top layer of the A axis showed an outward inclining trend. At 1400 cm/s2, the maximum width of cracks in the bottom column in the brick frame is around 5 mm, as shown in Figure 12. The cracks in the brick walls still developed locally and the walls still presented good integrity. The cracks at the beam ends on the 1st floor of the straw frame are about 3 mm, which all extended to the full sections. The straw wall at the top of axis A was about to crumble. At 1800 cm/s2, displacement of the top layer in brick frame became too big. As the bottom column broke, the brick frame overturned as a whole, as shown in Figure 13. Straw frame remained intact.Figure 11
Diagonal cracks in a beam of straw frame.Figure 12
Crack in the bottom column of brick frame.Figure 13
Crumble of the brick frame.


### 3.3.2. Dynamic Characteristics of Structure

White noise was input on the table before and after the earthquakes at different cases. By performing frequency spectrum analysis on the horizontal acceleration data collected by the acceleration sensor under the action of white noise, the amplitude-frequency curve of the transfer function was acquired. So, the frequencies and damping ratios of the structures were obtained, which are shown in Figures14 and 15 .Figure 14
The frequencies of models in different cases.Figure 15
Damping ratios of models in different cases.Results show that the attenuation law of the first-order frequency of the two models is basically the same, but the main reasons for the stiffness loss of the testing structures are different. It is also deduced from the damping ratios curve that the straw frame consumes more energy than the brick frame. Apparently, the straw frame with flexible connection has strong energy consumption capacity and is safer than brick frame structure under the action of big earthquakes.


### 3.3.3. Structural Displacement Response

The maximum interstory displacements and story drifts are shown in Table7.Table 7
Maximum interstory displacements and story drifts.
Peak acceleration (cm/s2)Brick frameFloor numberStraw frameFloor numberMax interstory displacement (mm)Max story driftMax interstory displacement (mm)Max story drift350.491/204110.481/20831700.551/181810.761/131612200.721/138910.831/120534000.831/120511.031/97136201.071/93511.851/54118002.391/41812.771/3611Results show that the max inter story displacements in the brick frame are generally smaller than those of the straw frame under the same lateral actions, due to the extra stiffness the masonry wall brings. It is not difficult to explain why the max story displacements occurred in the first story of the brick wall, while max story displacements appeared in the first and third story of the straw frame. Because masonry walls offered extra stiffness, and restricted the deformation of brick frame, this makes the 1st layer much weaker, as no bricks are arranged there. Straw walls, however, brought little extra stiffness to the original structure, hardly affecting the deformation of straw frame.


## 3.3.1. Experimental Observations

In the case of gradually increasing the peak acceleration of seismic waves, the occurrence and specific development of cracks are explained as follows:(1)
Under the Peak Ground Acceleration (PGA) of 35 cm/s2, the horizontal shaking of the models was inconspicuous. No visible cracks appeared on the models.(2)
Under the PGA of 70 cm/s2, cracks appeared at the bottom of the brick frame beams, and tiny cracks took place at the top of the bottom columns.(3)
Under the PGA of 140 cm/s2, previous cracks expanded with low amplitude, and a few horizontal cracks appeared at the top of the bottom column in the brick frame.(4)
Under the PGA of 220 cm/s2, micro cracks on the top of the bottom column in the brick frame began to expand, and cracks appeared in all four columns with a maximum length of 6 cm. Meanwhile, diagonal cracks took place in both ends of the 1st floor beams in the straw frame, as shown in Figure 11.(5)
Under the PGA of 400 cm/s2, top cracks of bottom column in brick frame continued expanding, some of which expanded to the full section. Meanwhile, micro cracks appeared on top of the column in the second story. Cracks in the 1st floor beam of the straw frame expanded, especially in the beams along the shaking direction. During vibration, the gap between straw panels and beams caused by the deformation of the straw frame was observed.(6)
Under the PGA of 620 cm/s2, cracks on the bottom column in the brick frame all extended to the full cross section; the maximum width of which is 2 mm. Cracks in the beams of the 1st and 2nd floor of the straw frame grew, and those of the 1st floor even extended to the full cross section.(7)
Under the PGA of 800 cm/s2, the width of the cracks on the bottom column in the brick frame increased to 3 mm, and cracks appeared at the bottom of some columns. The maximum width of the crack at the beam ends in the straw frame is about 2 mm. The gap between the straw panels and the columns at the top story was between 3 cm and 5 cm.(8)
Under 1100 cm/s2, the bottom columns in the brick frame were twisted, the top of which showed obvious plastic hinge characteristics. The bottom columns in the straw frame twisted in a low amplitude. The local cracks of the brick wall were slightly developed, and the overall performance was good. The straw wall of the top layer of the A axis showed an outward inclining trend. At 1400 cm/s2, the maximum width of cracks in the bottom column in the brick frame is around 5 mm, as shown in Figure 12. The cracks in the brick walls still developed locally and the walls still presented good integrity. The cracks at the beam ends on the 1st floor of the straw frame are about 3 mm, which all extended to the full sections. The straw wall at the top of axis A was about to crumble. At 1800 cm/s2, displacement of the top layer in brick frame became too big. As the bottom column broke, the brick frame overturned as a whole, as shown in Figure 13. Straw frame remained intact.Figure 11
Diagonal cracks in a beam of straw frame.Figure 12
Crack in the bottom column of brick frame.Figure 13
Crumble of the brick frame.


## 3.3.2. Dynamic Characteristics of Structure

White noise was input on the table before and after the earthquakes at different cases. By performing frequency spectrum analysis on the horizontal acceleration data collected by the acceleration sensor under the action of white noise, the amplitude-frequency curve of the transfer function was acquired. So, the frequencies and damping ratios of the structures were obtained, which are shown in Figures14 and 15 .Figure 14
The frequencies of models in different cases.Figure 15
Damping ratios of models in different cases.Results show that the attenuation law of the first-order frequency of the two models is basically the same, but the main reasons for the stiffness loss of the testing structures are different. It is also deduced from the damping ratios curve that the straw frame consumes more energy than the brick frame. Apparently, the straw frame with flexible connection has strong energy consumption capacity and is safer than brick frame structure under the action of big earthquakes.


## 3.3.3. Structural Displacement Response

The maximum interstory displacements and story drifts are shown in Table7.Table 7
Maximum interstory displacements and story drifts.
Peak acceleration (cm/s2)Brick frameFloor numberStraw frameFloor numberMax interstory displacement (mm)Max story driftMax interstory displacement (mm)Max story drift350.491/204110.481/20831700.551/181810.761/131612200.721/138910.831/120534000.831/120511.031/97136201.071/93511.851/54118002.391/41812.771/3611Results show that the max inter story displacements in the brick frame are generally smaller than those of the straw frame under the same lateral actions, due to the extra stiffness the masonry wall brings. It is not difficult to explain why the max story displacements occurred in the first story of the brick wall, while max story displacements appeared in the first and third story of the straw frame. Because masonry walls offered extra stiffness, and restricted the deformation of brick frame, this makes the 1st layer much weaker, as no bricks are arranged there. Straw walls, however, brought little extra stiffness to the original structure, hardly affecting the deformation of straw frame.


## 4. Numerical Analysis

The objective of this section is to verify and illustrate the failure mechanism of test structures.


### 4.1. FEM Models

By using SAP2000 (version 22.1.0), numerical analysis models of frameworks were built based on experimental structures. The only difference of FEM models was the way that those infill walls were considered. Compression struts, with no mass, were adopted to represent the stiffness contribution of masonry walls, as code ASCE/SEI 41-06 [17] proposed. The width of strut was the same with the thickness of masonry infill walls, namely, 40 mm. And the depth of strut was calculated based on (equation (7)) [17], which was 148 mm. With low elastic modulus and flexible connection, however, straw wall was treated as nonstructure component, whose stiffness was ignored. Both the self-weight of masonry bricks and straw panels were considered as vertical linear loads on beams.To study the failure mechanism, plastic hinges were defined at both ends of all columns and beams. Pushover analysis was conducted, with gradient horizontal loads being imposed on each floor. The FEM models of brick framework and straw framework are shown in Figures16 and 17 . “H” in the figures represents plastic hinge; dimensionless values of the horizontal loads merely illustrate the ratio of acting pushover loads.Figure 16
FEM model of straw framework.Figure 17
FEM model of brick framework.


### 4.2. Numerical Results and Discussion

As pushover analysis proceeded, plastic hinges took place. Figures18 and 19 show records of the pushover steps, where first hinges that reached C stage [16] appeared. In the straw framework, the first failure hinge emerged at the beam end of the 1st floor, while 7 other hinges appeared in other beams and columns. In the brick framework, first failure hinges took place only at the column ends of the 1st floor. Table 8 lists the displacements, story displacements, and story drifts at the time.Figure 18
Hinges distribution of straw framework.Figure 19
Hinges distribution of brick framework.Table 8
Displacements and story drifts of numerical models when the first failure hinges appeared.
FrameworkDisplacement (mm)Interstory displacement (mm)Story drift1st floor2nd floor3rd floor1st floor2nd floor3rd floor1st floor2nd floor3rd floorStraw frame20.4040.6445.7420.4020.245.101/491/501/196Brick frame26.0327.0627.4926.031.030.431/391/9711/2326Results show that before the failure of structure, the straw frame withstands greater lateral deformation than brick frame does under the same lateral action mode. From bottom to top, the story drifts of brick frame decrease dramatically than those of straw frame, which indicates that the masonry infill walls stupendously enhance the lateral stiffness of upper floors. However, when it comes to the story drifts of first stories, the brick frame apparently owns a bigger value. Above all, masonry infill walls on upper floors result in the localized increase of stiffness, leading to the redistribution of stress generated by lateral actions. This was presented in the form of a weaker first story, eventually a weaker frame than a straw frame or a bare one.With the difference of these structures produced by unequal stiffness, the failure modes differ. Numerical analyses show that the first failure hinge took place at the end of the 1st floor beam in the straw frame, while the first failure hinges appeared at the ends of the bottom columns in the brick frame, which accords with the experimental observations above. Failure of beams undoubtedly brings about local damage, while it sometimes in turn protects the structures by absorbing and dissipating part of the seismic energy. However, as vertical load bearing members, the failure of columns would lead to the collapse of the whole structure. This is the reason why the Chinese code [7] recommends the notion of strong column and weak beam, making sure columns fail after beams to protect the living at its best in seldomly occurred earthquakes. In a word, straw frame presents better seismic performance than brick frame.


## 4.1. FEM Models

By using SAP2000 (version 22.1.0), numerical analysis models of frameworks were built based on experimental structures. The only difference of FEM models was the way that those infill walls were considered. Compression struts, with no mass, were adopted to represent the stiffness contribution of masonry walls, as code ASCE/SEI 41-06 [17] proposed. The width of strut was the same with the thickness of masonry infill walls, namely, 40 mm. And the depth of strut was calculated based on (equation (7)) [17], which was 148 mm. With low elastic modulus and flexible connection, however, straw wall was treated as nonstructure component, whose stiffness was ignored. Both the self-weight of masonry bricks and straw panels were considered as vertical linear loads on beams.To study the failure mechanism, plastic hinges were defined at both ends of all columns and beams. Pushover analysis was conducted, with gradient horizontal loads being imposed on each floor. The FEM models of brick framework and straw framework are shown in Figures16 and 17 . “H” in the figures represents plastic hinge; dimensionless values of the horizontal loads merely illustrate the ratio of acting pushover loads.Figure 16
FEM model of straw framework.Figure 17
FEM model of brick framework.


## 4.2. Numerical Results and Discussion

As pushover analysis proceeded, plastic hinges took place. Figures18 and 19 show records of the pushover steps, where first hinges that reached C stage [16] appeared. In the straw framework, the first failure hinge emerged at the beam end of the 1st floor, while 7 other hinges appeared in other beams and columns. In the brick framework, first failure hinges took place only at the column ends of the 1st floor. Table 8 lists the displacements, story displacements, and story drifts at the time.Figure 18
Hinges distribution of straw framework.Figure 19
Hinges distribution of brick framework.Table 8
Displacements and story drifts of numerical models when the first failure hinges appeared.
FrameworkDisplacement (mm)Interstory displacement (mm)Story drift1st floor2nd floor3rd floor1st floor2nd floor3rd floor1st floor2nd floor3rd floorStraw frame20.4040.6445.7420.4020.245.101/491/501/196Brick frame26.0327.0627.4926.031.030.431/391/9711/2326Results show that before the failure of structure, the straw frame withstands greater lateral deformation than brick frame does under the same lateral action mode. From bottom to top, the story drifts of brick frame decrease dramatically than those of straw frame, which indicates that the masonry infill walls stupendously enhance the lateral stiffness of upper floors. However, when it comes to the story drifts of first stories, the brick frame apparently owns a bigger value. Above all, masonry infill walls on upper floors result in the localized increase of stiffness, leading to the redistribution of stress generated by lateral actions. This was presented in the form of a weaker first story, eventually a weaker frame than a straw frame or a bare one.With the difference of these structures produced by unequal stiffness, the failure modes differ. Numerical analyses show that the first failure hinge took place at the end of the 1st floor beam in the straw frame, while the first failure hinges appeared at the ends of the bottom columns in the brick frame, which accords with the experimental observations above. Failure of beams undoubtedly brings about local damage, while it sometimes in turn protects the structures by absorbing and dissipating part of the seismic energy. However, as vertical load bearing members, the failure of columns would lead to the collapse of the whole structure. This is the reason why the Chinese code [7] recommends the notion of strong column and weak beam, making sure columns fail after beams to protect the living at its best in seldomly occurred earthquakes. In a word, straw frame presents better seismic performance than brick frame.


## 5. Conclusion

After the shaking table tests are conducted to study the seismic performance of a 1/3-scale straw panel-infilled frame in comparison with masonry infilled frame, along with the numerical analysis, the following conclusions are drawn:(1)
As the story drifts of brick frame are generally smaller than those of straw frame under the same load cases, the masonry walls greatly affect the stiffness of original frame. Consequently, ignoring the stiffness contribution of masonry infill walls in seismic design process is inappropriate and dangerous.(2)
According to the outcome of test results and numerical analysis, inconsistent layout of masonry infill walls along the vertical direction results in the disparity of lateral stiffness for successive stories, leading to the redistribution of stress generated by lateral actions. Eventually, the failure mode shifts to a brittle type, as the stress concentration firstly harms the columns in weak stories.(3)
The proposed straw panels, with lightweight and flexible connections, bring less mass and little extra stiffness to bare frames. Thus, great disparity of lateral stiffness along vertical direction will not be achieved. Consequently, the failure mode is consistent with that of the bare frame, in which the beams damage firstly and consume part of the seismic energy to ensure the whole structure resisting the seismic actions better. The damping ratios’ curve also showed that the straw frame consumes more energy than the brick frame. With proper design, the straw panel-infilled frame is a good system combined with safety and flexibility in building space layout.



---