# Structural Construction of Binders Based on Orthophosphoric Acid and Refractory Materials

Authors: R. Liutyi; D. Liuta; I. Petryk
Journal: Advances in Materials Science and Engineering
 (2021)

---

## Abstract

The formation of phosphate binders in systems based on orthophosphoric acid and the most common refractory fillers in foundry technology (quartz dust, zircon ZrSiO4, and kyanite-sillimanite Al2SiO5) has not been previously studied. The phase composition of these inorganic binders was studied, and the formation of silicon SiP2O7 and zirconium ZrP2O7 pyrophosphates was confirmed. The study by differential thermogravimetric analysis in the temperature range of 20–1000°С established the fact that the formed binders are thermally stable and do not emit harmful gaseous substances. The obtained results of the studied binders make it possible to develop new environment-friendly core mixtures of thermal hardening.


---

## Body

## 1. Introduction

The tasks of metallurgy and foundry production are the preparation of alloys and the manufacturing of products from them with a wide range of special properties that are used for both heavy industry [1, 2] and precision casting [3, 4]. This requires the use of materials with high thermal and chemical resistance. Single-layer and double-layer microarc oxide coatings are used as protective heat-resistant coatings on cores and molds [5–8]. During the research of casting processes, it is possible to apply modeling of thermal processes in layered structures, for example, temperature distribution in the mold and casting [9, 10]. For the manufacture of molds and cores, the volume of which is millions of tons per year, we usually use iron phosphate and magnesium phosphate mixtures [4, 11–14], which often contain scarce and substandard components.Also, casting seeks to obtain a high-quality product with low cost and, very important, to meet stringent environmental standards. Conventional foundry binders are responsible for up to 70% of a foundry’s volatile organic compound emissions [15]. The source of unsatisfactory environmental situation is also the spread of sand-resin mixtures [16–18]. New binder technologies are essential for both foundries and the environment.A variety of binder systems have been developed predicated on a foundry’s problems [14, 19–23]. Binders have been solving many problems by addressing the casting quality, productivity, and environmental attributes foundry men receive from their binders. The effects of binder parameters on the properties of ceramic products and their anisotropic shrinkage were investigated [24].The use of phosphorus salts as binders for foundry metal production is poorly researched. The ability to bind and stick by phosphates is associated with the crystalline structure, which is due to the position of phosphorus in the periodic table of elements [25]. Phosphate materials, including binders, have been widely used in many fields of technology [10, 26–28].The research of phosphates is of interest both from the scientific and technological point of view. Н3РО4 and metal oxide, which acts as a hardener, are needed to obtain phosphates [12, 13, 29, 30]. The use of other compounds instead of oxides (silicates, metal salts, etc.) has not yet been considered. In this case, it is noteworthy that the main refractory fillers used in the core mixtures to manufacture complex sand molds for metal casting are oxides of transition and acid elements (SiO2, Al2O3, and ZrO2) [30] or silicates (mAl2O3 · nSiO2, ZrO2 · SiO2, etc.) [12, 13]. Both groups of compounds under normal conditions do not react with Н3РО4, but such an interaction is possible when heated. It is known that the properties of materials, including nonmetallics or composites, are structurally dependent, so studies of phase and mineralogical composition play an important role [31, 32].


## 2. Formulation of Research Problems

Previous studies of new core mixtures, the strengthening of which occurs during heated due to the interaction of Н3РО4 and refractory fillers, gave positive results. In particular, a mixture of 3-4% concentrated (85%) acid and 5–10% quartz dust, the filler of which is quartz sand, after hardening at 300°C, has a compressive strength more than 2.5 MPa with a scattering less than 0.30% [33]. A mixture of 3-4% Н3РО4 and 7-8% zirconium dust, the filler of which is zircon concentrate, after hardening at 350°C, provides a similar level of properties. Mixtures of Н3РО4 and additives of dusty aluminosilicates (pyrophyllite Al2(OН)2[Si4O10] or kyanite-sillimanite Al2O3 · SiO2) after hardening at 300°C provide a compressive strength of 1, 4,…, 3, 2 MPa.These properties make it possible to use these mixtures for the manufacture of foundry cores, which are strengthened by heating. However, there is currently no data on the mineralogical structure of the binder films and their phase composition, so it is not possible to predict the behavior of mixtures when heated in contact with the casting.The aim of the study is to determine the phase and mineralogical composition of binders formed during the interaction of orthophosphoric acid with refractory fillers of different classes and to determine the processes that occur with these binders when heated to 1000°C.


### 2.1. Research Objectives

(1)
X-ray phase analysis of binders formed during the interaction of orthophosphoric acid with quartz, zircon, and aluminosilicates(2)
Investigation of the processes that take place in the newly formed binders during heating, polymorphic and other transformations, and general thermal stability(3)
Development of recommendations for the use of the investigated binders in the composition of foundry core mixtures, which are strengthened by heating


## 2.1. Research Objectives

(1)
X-ray phase analysis of binders formed during the interaction of orthophosphoric acid with quartz, zircon, and aluminosilicates(2)
Investigation of the processes that take place in the newly formed binders during heating, polymorphic and other transformations, and general thermal stability(3)
Development of recommendations for the use of the investigated binders in the composition of foundry core mixtures, which are strengthened by heating


## 3. Experimental Data

A multifunctional diffractometer Rigaku Ultima IV was used to determine the phase composition of binders, which performed qualitative and quantitative analysis. The processes that occur during heating were determined using curves of differential thermogravimetric analyses taken from the STA 449 C Jupiter.As we have previously established, the mixture based on quartz sand with 1–4% of orthophosphoric acid is strengthened when heated to 300–320°C. The strength depends on the particle size characteristics of the sand. 2.5–10.0% of the quartz dust in the mixture stabilizes the strength and reduces the flakeability of the mixtures [34, 35]. Based on the analysis of the information presented above, it can be stated unequivocally that the strengthening of the mixtures is due to the formation of binders in them when heated. The binders are the product of the interaction of Н3РО4 and silicon particles since there are no other impurities in the mixture. To ensure the purity of the experiment and eliminate the influence of the impurities, which inevitably are in the filler, the sample of new binders was synthesized from 85%-Н3РО4 and silicon dust. These components are mixed and withstood for 1 hour in a laboratory oven at 300°С. The sample has become fully solid. After cooling, it was ground to the dust.X-ray analysis of the sample showed the presence of it completely new to the molding and core mixtures of the compounds (Figure1). It is silicon pyrophosphate SiР2О7, whose lines are marked on the diffraction pattern. In addition to the SiР2О7 lines, there are SiO2 lines available. Quantitative analysis showed 19% pyrophosphate and 81% oxide of silicon. Thus, the formation mechanism of the binders in the silicon system with Н3РО4 is disclosed.Figure 1
X-ray analysis of the composition of dust silicon (5 mass units) and orthophosphoric acid (3 mass units), strengthened at 300°С.Of particular note, the salts of pyrophosphoric acid Н4Р2О7 are formed, but orthophosphoric acid Н3РО4 was added to the mixture. This fact is explained by the polymorphic transformation of the acid, which occurs at approximately 215°С [11, 25–27]. Probably, the transformation is also the reason for the long process of strengthening the mixture (1-2 hours). As a result, for the first time, pyrophosphate is the binder in foundries. In addition, for the first time, it was received directly from a part of the refractory filler.The differential thermal analysis of the sample was performed in an alundum crucible in air with a heating rate of 20–30°С/min in the interval of 20–1000°С (Figure2). The binders are not subjected to thermal decomposition or other transformations. The endothermic effect at 570°С attributes to the conversion of α-quartz to β-quartz (since approximately 81% SiO2 is present in the sample).Figure 2
Differential thermoanalyses of the composition of dust silicon (5 mass units) and orthophosphoric acid (3 mass units).The advantages of the investigated binding system also include the absence of gas emission, as evidenced by the stability of the mass (Figure2) at high temperature.Zircon filler is also widely used in core mixtures. It is zirconium silicate (ZrO2·SiO2 or ZrSiO4). We have found that the addition of Н3РО4 makes it possible to strengthen the mixture with such fillers at 330–360°С. Zircon and Н3РО4 also form binders, the composition and structure of which need to be researched.The composition of 5 mass units of dust zircon and 3 mass units of 85%-Н3РО4 was mixed and withstood for 1 hour at 350°С in the laboratory oven. Exposure has strengthened the composition throughout the volume. Two crystalline phases were interpreted on the diffraction pattern (Figure 3): zircon (its number is 77.6%) and zirconium pyrophosphate ZrР2О7 (22.4%). The formation of zirconium pyrophosphate is the cause of strengthening the sample, so these are binders.Figure 3
X-ray analysis of the composition of dust zircon (5 mass units) and H3PO4 (3 mass units), strengthened at 300°С.Differential thermoanalysis of this composition (Figure4) makes it possible to conclude that the thermal stability is high. First, there are no polymorphic transformations when heated to 1000°С. Secondly, there are no any physicochemical processes in the sample. Thirdly, the mass varies slightly. Thus, these binders are promising for the core mixtures.Figure 4
Differential thermoanalysis of the composition of dust zircon (5 mass units) and H3PO4 (3 mass units).Strengthening of mixtures of orthophosphoric acid and kyanite-sillimanite (Al2O3 · SiO2 or Al2SiO5) occurs in the temperature interval of 250–300°С. But the phase composition is not so clear. The diffraction pattern of the mixture of 7 mass units of dust kyanite-sillimanite and 3 mass units of 85% orthophosphoric acid Н3РО4, strengthened at 300°С, does not allow to establish its complete mineralogical structure (Figure 5).Figure 5
X-ray analysis of the composition of kyanite-sillimanite (7 mass units) and orthophosphoric acid (3 mass units), strengthened at 300°С.Three crystalline phases were interpreted on the diffraction pattern: kyanite (or disthene), sillimanite, and quartz. The phase composition of the sample is almost identical to the composition of kyanite-sillimanite. But binders in this sample were uniquely formed because it was strengthened. Analyzing the distribution of the peaks and their intensities on the diffraction pattern, we conclude that binders in the strengthened state should be attributed to amorphous aluminum hydrophosphates or to their crystal hydrate forms.As a result of the analysis, we assume that binders were formed by the chemical reaction:(1)Al2SiO5+6H3PO4⟶2AlH2PO43⋅2H2O+SiO2+H2OBy mass ratio, this reaction is fully completed under the condition of 162 mass units of kyanite-sillimanite and 588 mass units of Н3РО4. Our sample, taking into account the acid concentration, contained 980 mass units of kyanite-sillimanite and 500 mass units of Н3РО4. In this case, only 138 mass units of kyanite-sillimanite reacted, and 980–138 = 842 mass units remained. Chemical equation (1) should form 51 mass units of quartz.The calculated composition of the crystalline phases in the sample is 94.3% of kyanite-sillimanite and 5.7% of quartz. Phase analysis revealed exactly the same composition, so the assumptions about chemical processes are generally correct. However, nothing is still known about binders, which is in an amorphous state.In the range of 100–200°С, aluminum dihydrogen phosphate gradually separates Н2О molecules. According to chemical equation (1), the initial amount of this hydrophosphate is 648 mass units. In this case, the amount of Н2О is 62 mass units. It is equal to 4.0% of the total mass of the sample (842 + 51 + 648). According to the DTGA graph (Figure 6), weight loss is close to this and equals 3.6%. Therefore, binders exist in the form of Al(H2PO4)3. Its residual amount is 648–62 = 586 mass units.Figure 6
Differential thermoanalysis of the composition of kyanite-sillimanite (7 mass units) and orthophosphoric acid (3 mass units).At a temperature of 417.9°С, an endothermic effect was recorded, which was accompanied by an insignificant sudden decrease in mass. At this temperature, hydrophosphates can lose constitutional water, and this process is not very simple. It is expressed by the following chemical reactions(2)AlH2PO43⟶AlPO4+2H3PO4(3)Al2SiO5+2H3PO4⟶2AlPO4+3H2O+SiO2According to chemical reaction (2), monosubstituted hydrogen phosphate is converted to trisubstituted orthophosphate. This releases a certain amount of active substance Н3РО4. 345 mass units of hydrogen phosphate give 122 mass units of orthophosphate and 196 mass units of Н3РО4. Our sample included 586 mass units of hydrogen phosphate, so 207 mass units of orthophosphate and 333 mass units of Н3РО4 were formed. If free kyanite-sillimanite is present in the sample, then it immediately reacts with Н3РО4. In addition, aluminum orthophosphate is formed.According to chemical reaction (3) 162 mass units of kyanite-sillimanite react with 196 mass units of Н3РО4 and give 244 mass units of orthophosphate, 54 mass units of water, and 60 mass units of quartz. In our case, 275 mass units of kyanite-sillimanite will react with 333 mass units of Н3РО4, so 415 mass units of orthophosphate, 92 mass units of water, and 102 mass units of quartz are formed.After these transformations, the sample consists of 842–275 = 567 mass units of kyanite-sillimanite (42%), 51 + 102 = 153 mass units of quartz (12%), and 207 + 415 = 622 mass units of aluminum orthophosphate (46%). The amount of released Н2О from the total mass of the sample is 6.4%. According to the graph (Figure 6), the weight loss is 6.5%, which exactly coincides with the calculation.The total smooth heat release in the range of 200–500°С is the result of the transition of aluminum phosphate from amorphous to crystalline form. Heating above 500°С does not show any thermal effect, i.e., aluminum orthophosphate (as well as quartz and kyanite-sillimanite) is remained unchanged up to 1000°С.The obtained data coincide with the results of other researchers [11, 26] who have studied the compositions of aluminosilicates (kaolinite and pyrophyllite) with Н3РО4 and also the thermal transformations of widespread aluminophosphate binders. The considered binding composition of kyanite-sillimanite and orthophosphoric acid is suitable for the core mixture.


## 4. Conclusions

The phase composition of binders obtained from the interaction of orthophosphoric acid and refractory fillers, such as dust silicon, zircon, and kyanite-sillimanite, was first investigated.It is found that the formed binders are Si and Zr pyrophosphates and also amorphous Al phosphates. The formation of pyrophosphates is related to the temperature interval of the strengthened mixtures (250–350°С), in which orthophosphoric acid is turned into pyrophosphoric acid.The new binders are thermally stable. This is particularly true for SiP2O7 and ZrP2O7, which are characterized by the absence of transformations when heated. Heating of binders formed from kyanite-sillimanite and H3PO4, causes the crystallization of amorphous phosphates, as well as the transformation of acidic aluminum phosphates to the normal state. This is not detrimental to the characteristics of the core mixture.



---

*Source: 6667769-2021-02-25.xml*