# Enhanced Mechanical Properties of Mg-6Sn-3Al-1Zn Alloy with Bimodal Grain Size Disturbed in the Microstructure Uniformly through Changing the Rolling Temperature

Authors: Fuan Wei; Jinhui Wang; Ping Li; Bo Shi
Journal: Advances in Materials Science and Engineering
 (2020)

---

## Abstract

The mechanical properties of Mg-6Sn-3Al-1Zn alloy were enhanced with bimodal grain size disturbed in the microstructure uniformly; the Mg-6Sn-3Al-1Zn alloys were rolled with 60% thickness reduction at different rolling temperatures. The results have shown that the Mg-6Sn-3Al-1Zn alloys are composed of Mg2Sn phase and α-Mg matrix phase. When the rolling temperature was less than or equal to 400°C, with the rolling temperature increasing, the average size and volume fraction of Mg2Sn phase and the average grain size of small grains remained unchanged, the average grain size of large grains decreased, the volume fraction of small grains increased, and the yield strength of the alloy increased. When the rolling temperature reached 450°C, the average size and volume fraction of Mg2Sn phase and the average grain size of large grains increased, and the volume fraction of small grains and the yield strength of the alloy decreased. The elongation increased with the rolling temperature increasing, but the change trend of hardness was just opposite. When the alloy was rolled at 400°C, the average sizes of small grains, large grains, and Mg2Sn phases were 3.66 μm, 9.24 μm, and 19.5 μm, respectively. The volume fractions of small grains, large grains, and Mg2Sn phases were 18.6%, 77.6%, and 3.8%, respectively. And the tensile properties reached the optimum; for example, the tensile strength, yield strength, elongation, and Vickers hardness were 361 MPa, 289.5 MPa, 20.5%, and 76.3 HV, respectively.


---

## Body

## 1. Introduction

Magnesium alloys are the lightest metallic structural materials [1–3]. Besides, magnesium alloys have widespread applications in modern aerospace, automobile industries, and electrical appliances, due to their strong specific strength, excellent electrode conductivity, electromagnetic shielding capability, and being easy to reuse [4–8]. In other words, magnesium alloys play an important role in modern industry.Both the strength and ductility of the alloy cannot be enhanced at the same time. How to improve the strength and ductility of the alloy is a hot research topic. The research has found that bimodal microstructures formed in magnesium alloys or Al–Mg alloys could simultaneously improve the strength and ductility [9–13].In recent years, many researchers have executed a mass of works on the study of rolling magnesium alloys, and they have developed many technologies to obtain high mechanical properties magnesium alloy sheets [14–16]. However, the effect of rolling temperature on the microstructure and mechanical properties of Mg-6Sn-3Al-1Zn alloy was seldom studied systematically. Due to being without rare earth elements, Mg-6Sn-3Al-1Zn alloys have low cost. In this paper, the optimum rolling temperature was found out, and the evolution of microstructure and mechanical properties was systematically investigated. Bimodal microstructure of Mg-6Sn-3Al-1Zn alloy was obtained when the rolling temperature was more than or equal to 350°C (the amount of rolling deformation was fixed at 60%). After the Mg-6Sn-3Al-1Zn alloy was rolled at 400°C, large grains and small grains of bimodal microstructure distributed uniformly in the alloy, which leads to simultaneous enhancements of the strength and ductility of Mg-6Sn-3Al-1Zn alloy compared to the casting alloy. The present studies have significant value for the development of high mechanical properties Mg-6Sn-3Al-1Zn alloy, and the guiding function for fabricating high mechanical properties magnesium alloys in the future.


## 2. Experimental

### 2.1. Fabrication of Mg-6Sn-3Al-Zn Alloy

Firstly, the Mg, Sn, Al, and Zn bulks were weighted according to the weight ratio of Mg-6Sn-3Al-Zn alloy. Subsequently, Mg, Al, Zn bulks, refining agent, and molds were put into the resistance furnace for heat preservation at 300°C for 12 h. Due to the low melting point of Sn, then Sn bulk was dried by a dryer. The preheated Mg bulk was put into the smelting furnace and the mix gas (the volume ratio of Ar and SF6 was 1 : 99) was introduced. After setting the temperature of the furnace as 800°C, Mg bulks were heated. When the Mg bulks were melted, the Sn, Zn, and Al bulks were added in order. When the melt temperature reached 730°C, 36 g refining agent was added and then fully agitated and the impurities were removed. The melt temperature was constantly heated to 750°C and kept for 20 min, and then the power supply was shut down for cooling the melt. When the temperature of the melt gradually reduced to 730°C, it was cast in a mold which was preheated to 300°C. After the melt solidification, the Mg-6Sn-3Al-Zn alloy was taken out from the mold.


### 2.2. Preparation of the As-Rolled Mg-3Al-6Sn-1Zn Alloy Samples

The cylindrical magnesium alloy was milled to a cuboid form using a milling machine. And the sample was solution-treated at 450°C for 8 h and then was water-quenched. The cubic sample was processed by wire cutting to obtain the magnesium alloy sheets (30 mm (width) × 50 mm (length) × 5 mm (thickness)). We fixed the amount of rolling deformation at 60% and selected 300°C, 350°C, 400°C, and 450°C as the rolling temperature. Before rolling, the mill roller was heated to 200°C, and the sample was held for 15 min at rolling temperature. The rolling reduction of the first rolling pass was 1 mm, and the subsequent rolling reduction was 0.3 mm, and the sample was kept warm in a resistance furnace with 2 min between the two passes.


### 2.3. Microstructure Characterization and Mechanical Properties Test

Firstly, the rolling samples were cut to be sheet samples (12 mm (length) × 6 mm (width)) along the rolling direction. Subsequently, these sheet samples were strictly disposed by the abrasive papers and mechanical polisher. These polishing slices were immediately etched for 25 s using the etch liquid (CH3CH2OH including 4% HNO3). Finally, we observed the microstructure of the samples by using metallographic microscope (OM, DMI3000, Leica, Weztlar, Germany). The phases of magnesium alloy were identified by x-ray diffraction (XRD, BRUKERXD8ADVANCE-A25, Bruker, Karlsruhe, Germany) with a scan range of 20°–90°, a scan step of 0.02°. And the microstructure was observed using scanning electron microscopy (SEM, Merlin Campact, Carl Zeiss Microscopy Ltd., Jena, Germany) with an acceleration voltage of 20 kV and an electric current of 10 μA.The grain size was characterized by Electron Back-Scattered Diffraction (EBSD, Oxford Instruments, Oxford, UK). We cut 5 mm (length) × 3 mm (width) in the center of the sample along the rolling direction, annealed it at 350°C for 5 min to remove stress, and polished it with 400#, 800#, 1200#, 2000#, 3000#, 5000#, and 7000# sandpapers, respectively. And then the samples were electrochemically polished with 7% perchlorate alcohol solution. Before electrochemical polishing, liquid nitrogen was added to the electrolyte solution to ensure the temperature of the electrolyte solution of -25°C. Polishing voltage, current, and time were 20 V, 0.2 μA, and 2 min, respectively. Argon ion polishing was carried out after electropolishing, polished voltage was 3 keV, polished angle was 3°, polished time was 90 min, and then the sample was observed by SEM equipped with EBSD from Oxford instrument, operating voltage and step were 20 kV and 0.21 μm, respectively, and EBSD patterns were indexed by using CHANNEL 5 software from HKL Technology, Oxford Instruments.The dislocation analysis was characterized by transmission electron microscope (TEM, JEM-2010 HR, JEOL Ltd., Tokyo, Japan). Firstly, we used a wire cutting machine to cut a sample of 20 mm (length) × 20 mm (width). Secondly, the sample was thinned by sandpaper until its thickness decreased to 40μm. Thirdly, TEM specimens were prepared by polishing machine (Model 110 Automatic Twin-Jet Electropolisher, E.A. Fischione Instruments, USA) used with an electrolyte solution composed of 4 vol% of HClO4 and 96 vol% of C2H5OH. Fourthly, the sample was further reduced by a precision ion polishing system (PIPS, Gatan II 695, Pleasanton, USA). Lastly, the sample was observed by TEM at an operating voltage of 200 kV and a current of 103 μA.The sheet samples were measured under 0.2 kgf loading force and dwelling 10 s using Vickers hardness tester (WILSON VH1102 type, Buehler, Illinois Tool Works Inc., Lake Bluff, USA). After 5-time measurements, we acquired the average value of Vickers hardness as the final value. Tensile properties were tested on an electronic universal testing machine (AGS-X-50 kN, Shimadzu, Tokyo, Japan) with a cross-head speed of 0.2 mm/min and repeated three times; the average value was as the final value.


## 2.1. Fabrication of Mg-6Sn-3Al-Zn Alloy

Firstly, the Mg, Sn, Al, and Zn bulks were weighted according to the weight ratio of Mg-6Sn-3Al-Zn alloy. Subsequently, Mg, Al, Zn bulks, refining agent, and molds were put into the resistance furnace for heat preservation at 300°C for 12 h. Due to the low melting point of Sn, then Sn bulk was dried by a dryer. The preheated Mg bulk was put into the smelting furnace and the mix gas (the volume ratio of Ar and SF6 was 1 : 99) was introduced. After setting the temperature of the furnace as 800°C, Mg bulks were heated. When the Mg bulks were melted, the Sn, Zn, and Al bulks were added in order. When the melt temperature reached 730°C, 36 g refining agent was added and then fully agitated and the impurities were removed. The melt temperature was constantly heated to 750°C and kept for 20 min, and then the power supply was shut down for cooling the melt. When the temperature of the melt gradually reduced to 730°C, it was cast in a mold which was preheated to 300°C. After the melt solidification, the Mg-6Sn-3Al-Zn alloy was taken out from the mold.


## 2.2. Preparation of the As-Rolled Mg-3Al-6Sn-1Zn Alloy Samples

The cylindrical magnesium alloy was milled to a cuboid form using a milling machine. And the sample was solution-treated at 450°C for 8 h and then was water-quenched. The cubic sample was processed by wire cutting to obtain the magnesium alloy sheets (30 mm (width) × 50 mm (length) × 5 mm (thickness)). We fixed the amount of rolling deformation at 60% and selected 300°C, 350°C, 400°C, and 450°C as the rolling temperature. Before rolling, the mill roller was heated to 200°C, and the sample was held for 15 min at rolling temperature. The rolling reduction of the first rolling pass was 1 mm, and the subsequent rolling reduction was 0.3 mm, and the sample was kept warm in a resistance furnace with 2 min between the two passes.


## 2.3. Microstructure Characterization and Mechanical Properties Test

Firstly, the rolling samples were cut to be sheet samples (12 mm (length) × 6 mm (width)) along the rolling direction. Subsequently, these sheet samples were strictly disposed by the abrasive papers and mechanical polisher. These polishing slices were immediately etched for 25 s using the etch liquid (CH3CH2OH including 4% HNO3). Finally, we observed the microstructure of the samples by using metallographic microscope (OM, DMI3000, Leica, Weztlar, Germany). The phases of magnesium alloy were identified by x-ray diffraction (XRD, BRUKERXD8ADVANCE-A25, Bruker, Karlsruhe, Germany) with a scan range of 20°–90°, a scan step of 0.02°. And the microstructure was observed using scanning electron microscopy (SEM, Merlin Campact, Carl Zeiss Microscopy Ltd., Jena, Germany) with an acceleration voltage of 20 kV and an electric current of 10 μA.The grain size was characterized by Electron Back-Scattered Diffraction (EBSD, Oxford Instruments, Oxford, UK). We cut 5 mm (length) × 3 mm (width) in the center of the sample along the rolling direction, annealed it at 350°C for 5 min to remove stress, and polished it with 400#, 800#, 1200#, 2000#, 3000#, 5000#, and 7000# sandpapers, respectively. And then the samples were electrochemically polished with 7% perchlorate alcohol solution. Before electrochemical polishing, liquid nitrogen was added to the electrolyte solution to ensure the temperature of the electrolyte solution of -25°C. Polishing voltage, current, and time were 20 V, 0.2 μA, and 2 min, respectively. Argon ion polishing was carried out after electropolishing, polished voltage was 3 keV, polished angle was 3°, polished time was 90 min, and then the sample was observed by SEM equipped with EBSD from Oxford instrument, operating voltage and step were 20 kV and 0.21 μm, respectively, and EBSD patterns were indexed by using CHANNEL 5 software from HKL Technology, Oxford Instruments.The dislocation analysis was characterized by transmission electron microscope (TEM, JEM-2010 HR, JEOL Ltd., Tokyo, Japan). Firstly, we used a wire cutting machine to cut a sample of 20 mm (length) × 20 mm (width). Secondly, the sample was thinned by sandpaper until its thickness decreased to 40μm. Thirdly, TEM specimens were prepared by polishing machine (Model 110 Automatic Twin-Jet Electropolisher, E.A. Fischione Instruments, USA) used with an electrolyte solution composed of 4 vol% of HClO4 and 96 vol% of C2H5OH. Fourthly, the sample was further reduced by a precision ion polishing system (PIPS, Gatan II 695, Pleasanton, USA). Lastly, the sample was observed by TEM at an operating voltage of 200 kV and a current of 103 μA.The sheet samples were measured under 0.2 kgf loading force and dwelling 10 s using Vickers hardness tester (WILSON VH1102 type, Buehler, Illinois Tool Works Inc., Lake Bluff, USA). After 5-time measurements, we acquired the average value of Vickers hardness as the final value. Tensile properties were tested on an electronic universal testing machine (AGS-X-50 kN, Shimadzu, Tokyo, Japan) with a cross-head speed of 0.2 mm/min and repeated three times; the average value was as the final value.


## 3. Results

The XRD patterns of Mg-6Sn-3Al-Zn alloys without and with rolling at different temperatures are shown in Figure1. As can be seen, the phases include α-Mg matrix and Mg2Sn second phase, indicating that the phase compositions are steady at various rolling temperatures. The (0002) diffraction peak intensity increased after rolling, while the (10-10) and (10-11) diffraction peak intensity decreased. This indicates that the (0002) basal texture was formed in Mg-6Sn-3Al-Zn alloy after rolling at different temperatures.Figure 1
XRD patterns of Mg-6Sn-3Al-Zn alloys without and with rolling at different temperatures.Basal plane (0002), prismatic plane (10-10), and (11-20) pole figures of Mg-6Sn-3Al-Zn alloys rolled at different temperatures are shown in Figure2. After rolling, (0002) basal plane textures are formed, which is consistent with the XRD result. According to the (0002) basal plane pole figure, the maximum pole density points are distributed in the center of the pole figures. Therefore, it is shown that the basal plane of the alloy is parallel to the rolling direction. The texture intensity increases firstly and then remains unchanged with the increasing of the rolling temperature. When the Mg-6Sn-3Al-Zn alloys are rolled at 300°C, 350°C, 400°C, and 450°C, the texture intensities are 9.45, 12.16, 11.41, and 11.62, respectively.Figure 2
Basal plane (0002), prismatic plane (10-10) and (11-20) pole figures of Mg-6Sn-3Al-Zn alloys rolled at different temperatures: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.The OM pictures of the Mg-6Sn-3Al-Zn alloys rolled at different temperature are shown in Figure3. The black rod-like phase is Mg2Sn second phase, and the matrix phase is α-Mg phase. The statistical calculations on the average size and volume fraction of Mg2Sn second phase were performed by Image-Pro Plus 6.0 software, and the variations of them with the rolling temperature are shown in Figure 4. When the rolling temperature was less than or equal to 400°C, the average size and volume fraction of Mg2Sn phase almost did not change with the rolling temperature increasing. When the alloys were rolled at 300°C, 350°C, and 400°C, the average sizes of Mg2Sn phase were 18.6 μm, 17.6 μm, and 18.6 μm, respectively, and the volume fractions of Mg2Sn phase were 3.6%, 3.8%, and 3.8%, respectively. When the rolling temperature reached 450°C, the average size and volume fraction of Mg2Sn phase increased sharply; for example, their values were 39.3 μm and 9.7%, respectively (shown in Table 1).Figure 3
OM pictures of Mg-6Sn-3Al-Zn alloys rolled at different temperatures: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
(a)(b)(c)(d)Figure 4
(a) The average grain size of small grains, big grains, and Mg2Sn phases of the alloys rolled at different temperatures. (b) The volume fraction of small grains, big grains, and Mg2Sn phases of the alloys rolled at different temperatures.
(a)(b)Table 1
The average sizes and volume fractions of Mg2Sn phases, small grains, and big grains of alloys rolled at different temperatures.
Rolling temperature (°C)The average size (μm)The volume fraction (%)Small grainsLarge grainsMg2Sn phasesSmall grainsLarge grainsMg2Sn phases3003.6811.2918.67.289.23.63503.5910.0517.613.183.13.84003.669.2419.518.677.63.84503. 729.6839.316.473.99.7EBSD images of the rolled Mg-6Sn-3Al-1Zn alloys with different rolling temperatures are shown in Figure5. As can be seen from Figure 5, after the alloys were rolled at different temperature, bimodal microstructures were formed, and the grains of the alloy were composed of small grains and large grains.Figure 5
EBSD images of the as-rolled Mg-6Sn-3Al-1Zn alloys at different rolling temperatures: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
(a)(b)(c)(d)Misorientation angle distribution diagrams of the rolled Mg-6Sn-3Al-1Zn alloys with different rolling temperatures are shown in Figure6. As can be seen, a few of {10-12} extension twinning (the angle with parent crystal is 86.1°) and {10-11} contraction twinning (the angle with parent crystal is 56°) exist in deformed alloys.Figure 6
Misorientation angle distribution diagrams of the as-rolled Mg-6Sn-3Al-1Zn alloys at different rolling temperatures: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
(a)(b)(c)(d)Twin and high/low-angle boundary distribution diagrams of the rolled Mg-6Sn-3Al-1Zn alloys with different rolling temperatures are shown in Figure7. As can be seen, the red and blue lines represent the extension twinning boundary and contraction twinning boundary, respectively. The volume fraction of twins is unchanged with the rolling temperature increasing; when the rolling temperatures are 300°C, 350°C, 400°C, and 450°C, the volume fractions of twins are 0.60%, 1.0%, 0.53%, and 0.73%, respectively. Thus, when the rolling temperature is more than or equal to 300°C, the dynamic recrystallization process is completed.Figure 7
Twins and high/low-angle boundary distribution diagrams of the as-rolled Mg-6Sn-3Al-1Zn alloys at different rolling temperatures: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
(a)(b)(c)(d)Kernel Average Misorientation (KAM) maps of the rolled Mg-6Sn-3Al-1Zn alloys with different rolling temperatures are shown in Figure8. As can be seen, the KAM value is almost constant. When the alloys were rolled with 300°C, 350°C, 400°C, and 450°C, the KAM value was 4.98, 4.97, 4.96, and 4.94, indicating that the dynamic recrystallization process is completed as the rolling temperature is more than or equal to 300°C.Figure 8
Kernel Average Misorientation maps of the as-rolled Mg-6Sn-3Al-1Zn alloys at different rolling temperatures: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
(a)(b)(c)(d)The statistical calculations on the average sizes and volume fractions of Mg2Sn second phase, small grains, and big grains were performed by Image-Pro Plus 6.0 software. And the variations of them with the increasing of the rolling temperature are shown in Figure 4. The average grain size of small grains of the alloy almost does not change with the rolling temperature increasing. And when the alloys are rolled at 300°C, 350°C, 400°C, and 450°C, the average grain sizes of small grains are 3.68 μm, 3.59 μm, 3.66 μm, and 3.72 μm, respectively. When the rolling temperature is less than or equal to 400°C, the average grain size of large grains of alloy decreases with the rolling temperature increasing. For the alloys rolled at 300°C, 350°C, and 400°C, the average grain sizes of large grains are 11.29 μm, 10.05 μm, and 9.24 μm, respectively. When the rolling temperature reaches 450°C, the average grain size of large grains increases to 9.68 μm. When the rolling temperature is less than or equal to 400°C, the volume fraction of small grains of the alloy increases with the rolling temperature increasing. For the alloys rolled at 300°C, 350°C, and 400°C, the volume fractions of small grains are 7.2%, 13.1%, and 18.6%, respectively. When the rolling temperature reaches 450°C, the volume fraction of small grains decreases to 16.4%. The volume fraction of large grains of the alloy decreases with the increasing of the rolling temperature; after the alloy is rolled at 300°C, 350°C, 400°C, and 450°C, the volume fractions of large grains are 89.2%, 83.1%, 77.6%, and 73.9%, respectively, which are shown in Table 1.The grain size distributions of the alloys rolled at different temperatures which are determined from EBSD images are shown in Figure9. As can be seen, when the rolling temperature is less than or equal to 400°C, the number of recrystallized grains increases and the average grain size decreases with the rolling temperature increasing. For the alloy rolled at 300°C, 350°C, and 400°C, the average grain sizes are 7.50 μm, 5.66 μm, and 5.42 μm, respectively. When the rolling temperature reaches 450°C, the average grain size increases to 6.16 μm.Figure 9
Grain size distributions of the alloys rolled at different temperatures which were determined from EBSD images: (a) 300°C, (b) 350°C, (c) 400°C, (d) 450°C.
(a)(b)(c)(d)The grain area distributions of the alloys rolled at different temperatures which are determined from EBSD images and the results are shown in Figure10. When the rolling temperature is more than or equal to 350°C, the bimodal microstructure is clearly formed. With the rolling temperature increasing, the area ranges of big grains firstly decrease and then increase, but the area range of small grains shows a trend of first decreasing and then unchanging. For the alloy rolled at 350°C, the area range of small grains is 0-1250 μm2, and the area range of big grains is 1450-3550 μm2. For the alloy rolled at 400°C, the area range of small grains narrows to 0-650 μm2, while the area ranges of big grains narrow to 1250-1950 μm2. For the alloy rolled at 450°C, the area ranges of small grains almost do not change compared to that of the alloy rolled at 400°C, but the volume fraction of small grains decreases, and the area ranges of big grains increase to 1050-3650 μm2.Figure 10
Grain area distributions of the alloys rolled at different temperatures which were determined from EBSD images: (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
(a)(b)(c)(d)The TEM bright field image, selected area electron diffraction (which comes from the blue circle of TEM bright field image and the yellow circle of TEM bright field image), and dark field image (which comes from the white circle of the selected area electron diffraction) of the alloy rolled at 400°C are shown in Figure11. Dislocation analysis by the invisibility criterion (g·b = 0) reveals that the TEM foil contains <a> dislocations and <c+a> dislocations. <c + a> dislocations are visible under both g = (01-10) and g = (0002), while <a> dislocations are invisible under g = (0002). Hence, these findings agree with the literature (Sabat et al., 2018) [17]. By comparing Figure 11(a) with Figure 11(d), we find that the volume fraction of <a> dislocation is more than that of <c + a> dislocation. Accordingly, these TEM works suggest that the pyramidal plane <a> slip is easier to start than the pyramidal plane <c + a> slip in the process of rolling, and the SF (stacking fault) energy of pyramidal <a> slip is higher than that of pyramidal <c + a> slip, which can be attributed to the more difficult nucleation of <c + a> dislocations than that of <a> dislocations. As can be seen from Figure 11(a), the rod-like Mg2Sn phases, presented in Figure 12, are distributed in the microstructure; the dislocations pile up near the Mg2Sn phase, indicating that the Mg2Sn phases could hinder the dislocation motions and then improve alloy strength.Figure 11
The TEM bright field image (a), selected area electron diffraction (b, c), and the TEM dark field image (d) of the alloy rolled at 400°C. <c + a> dislocations were identified in a grain based on the invisibility criterion; <a> dislocations were also found in their vicinity. Two-beam dark-field images were taken along the [2-1-10] zone axis under g = (01-10) and g = (0002), respectively.
(a)(b)(c)(d)Figure 12
The EDS mapping of the alloy with a rolling temperature of 400°C. (a) Selected region from TEM bright field image, (b) Mg element, (c) Al element, (d) Zn element, and (e) Sn element.
(a)(b)(c)(d)(e)The EDS (Energy Dispersive Spectrometer) mappings of the alloy rolled at 400°C are shown in Figure12. As can be seen from Figure 12(a), a few of rod-like phases are distributed in the TEM bright field image. We select a rectangular region for EDS mapping. As can be seen from Figure 12(e), the Sn element is rich and shows rod-like pattern, indicating that the rod-like phases in TEM bright field image are Mg2Sn phase, and this result is consistent with XRD result. Moreover, as can be seen, the Mg, Al, and Zn elements are distributed uniformly in the microstructure.The tensile stress-strain curves of the alloys rolled at different temperatures, the changes of tensile mechanical properties, and Vickers hardness of the alloys with rolling temperature are shown in Figure13 and summarized in Table 2. When the rolling temperature is less than or equal to 400°C, yield strength of the alloy increases from 267.8 MPa for the alloy rolled at 300°C to 289.5 MPa for the alloy rolled at 400°C. When the rolling temperature reaches 450°C, yield strength of the alloy decreases to 235.3 MPa. When the alloy is rolled at 350°C, the tensile strength of the alloy almost does not change compared to the alloy rolled at 300°C. For the alloy rolled at 400°C, its tensile strength increases to 361.1 MPa. When the rolling temperature reaches 450°C, tensile strength of the alloy decreases to 318.9 MPa. The elongation of the alloy increases with the rolling temperature increasing. For the alloys rolled at 300°C, 350°C, 400°C, and 450°C, their elongations are 11.2%, 19.3%, 20.5%, and 21.1%, respectively. The Vickers hardness of the alloy decreases with the rolling temperature increasing. For the alloys rolled at 300°C, 350°C, 400°C, and 450°C, their hardness values are 80.9 HV, 79.1 HV, 76.3 HV, and 66.3 HV, respectively. Importantly, for the alloy rolled at 400°C, the tensile strength and plasticity reach the best combination.Figure 13
The tensile stress-strain curves of the alloys rolled at different temperatures (a), the changes of tensile mechanical properties (b), and Vickers hardness (c) of the alloys with rolling temperatures.
(a)(b)(c)Table 2
Mechanical properties of alloy rolled at different temperatures.
Rolling temperature (°C)Tensile strength (MPa) (mean ± SD)Yield strength (MPa) (mean ± SD)Elongation (%) (mean ± SD)Vickers hardness (HV) (mean ± SD)300347.9 ± 6.2267.8 ± 2.311.2 ± 0.380.9 ± 1.3350341.8 ± 6.3277.3 ± 4.319.3 ± 0.279.1 ± 1.3400361.1 ± 0.6289.5 ± 4.120.5 ± 0.476.3 ± 0.7450318.9 ± 9.0235.3 ± 4.521.1 ± 0.266.3 ± 1.0


## 4. Discussion

### 4.1. Effect of Rolling Temperature on Bimodal Microstructure

When the rolling temperature is less than or equal to 400°C, with the rolling temperature increasing, the average grain size of large grains of alloy decreases, and the volume fraction of small grains of alloy increases. It is because the rolling temperature is higher than the recrystallization temperature. High rolling temperature and large rolling deformation sufficiently promote the recrystallization process of alloys. Hence, the higher the rolling temperature, the smaller the grains formed after rolling. When the rolling temperature reaches 450°C, the average grain size of large grains increases, and the volume fraction of small grains decreases. This is because the rolling temperature is too high, resulting in grain size growth.


### 4.2. Effect of Rolling Temperature on Mg2Sn Phase

Low rolling temperature will separate out Mg2Sn phase from matrix. However, the rolling period is very short. Therefore, when the rolling temperature is less than or equal to 400°C, the volume fraction of Mg2Sn phase almost does not change with the rolling temperature increasing. When the rolling temperature reaches 450°C, the average size and volume fraction of Mg2Sn phase increase sharply. This is owing to the phenomenon that high rolling temperature will lead to Mg2Sn phase separated out from the solid solution. However, the average size of Mg2Sn phase almost does not change with the rolling temperature increasing. It is because the Mg2Sn phase belongs to the hard brittle phase, and in this work, the amount of rolling deformation is 60%; the force for breaking resistance of Mg2Sn phase is the same.


### 4.3. Effect of Rolling Temperature on Mechanical Properties

When the rolling temperature is less than or equal to 400°C, with the rolling temperature increasing, the yield strength of the alloy increases, which can be attributed to the grain size of large grains decreasing and the volume fraction increasing; then, the fine grain strengthening effect is obvious. When the rolling temperature reaches 450°C, the yield strength of the alloy decreases, because the grain size clearly increases. Otherwise, although the volume fraction of Mg2Sn phase increases, the average size of Mg2Sn phase is large; thus, the dispersion strengthening effect is weakened.When the alloy was rolled at 350°C, a bimodal microstructure was clearly formed. This leads to the elongation increasing sharply. Otherwise, due to the high rolling temperature, the pyramidal plane <a> slip and <c + a> slip started in the process of rolling. The higher the rolling temperature of alloy, the easier to start the dislocation motion. This showed that the elongation of the alloy increases with the rolling temperature increasing. When the alloy was rolled at 450°C, the area ranges of large grains increased, which led to the elongation further increasing.


## 4.1. Effect of Rolling Temperature on Bimodal Microstructure

When the rolling temperature is less than or equal to 400°C, with the rolling temperature increasing, the average grain size of large grains of alloy decreases, and the volume fraction of small grains of alloy increases. It is because the rolling temperature is higher than the recrystallization temperature. High rolling temperature and large rolling deformation sufficiently promote the recrystallization process of alloys. Hence, the higher the rolling temperature, the smaller the grains formed after rolling. When the rolling temperature reaches 450°C, the average grain size of large grains increases, and the volume fraction of small grains decreases. This is because the rolling temperature is too high, resulting in grain size growth.


## 4.2. Effect of Rolling Temperature on Mg2Sn Phase

Low rolling temperature will separate out Mg2Sn phase from matrix. However, the rolling period is very short. Therefore, when the rolling temperature is less than or equal to 400°C, the volume fraction of Mg2Sn phase almost does not change with the rolling temperature increasing. When the rolling temperature reaches 450°C, the average size and volume fraction of Mg2Sn phase increase sharply. This is owing to the phenomenon that high rolling temperature will lead to Mg2Sn phase separated out from the solid solution. However, the average size of Mg2Sn phase almost does not change with the rolling temperature increasing. It is because the Mg2Sn phase belongs to the hard brittle phase, and in this work, the amount of rolling deformation is 60%; the force for breaking resistance of Mg2Sn phase is the same.


## 4.3. Effect of Rolling Temperature on Mechanical Properties

When the rolling temperature is less than or equal to 400°C, with the rolling temperature increasing, the yield strength of the alloy increases, which can be attributed to the grain size of large grains decreasing and the volume fraction increasing; then, the fine grain strengthening effect is obvious. When the rolling temperature reaches 450°C, the yield strength of the alloy decreases, because the grain size clearly increases. Otherwise, although the volume fraction of Mg2Sn phase increases, the average size of Mg2Sn phase is large; thus, the dispersion strengthening effect is weakened.When the alloy was rolled at 350°C, a bimodal microstructure was clearly formed. This leads to the elongation increasing sharply. Otherwise, due to the high rolling temperature, the pyramidal plane <a> slip and <c + a> slip started in the process of rolling. The higher the rolling temperature of alloy, the easier to start the dislocation motion. This showed that the elongation of the alloy increases with the rolling temperature increasing. When the alloy was rolled at 450°C, the area ranges of large grains increased, which led to the elongation further increasing.


## 5. Conclusions

The Mg-6Sn-3Al-1Zn alloys are composed of Mg2Sn phase and α-Mg matrix phase. When the rolling temperature was less than or equal to 400°C, with the rolling temperature increasing, the average size and volume fraction of Mg2Sn second phase and the average grain size of small grains remain unchanged. Due to the dynamic recrystallization during the rolling process, the average grain size of large grains decreased, and the volume fraction of small grains increased, which led to the yield strength of the alloy increasing. When the rolling temperature reached 450°C, due to the high rolling temperature, the average grain size of large grains increased, the volume fraction of small grains decreased, and the average size and volume fraction of Mg2Sn phase and the yield strength of the alloy decreased. With the rolling temperature increasing, the elongation increased, but the hardness change had an opposite trend. When the rolling temperature reached 400°C, the average size of small grains, large grains, and Mg2Sn phase was 3.66 μm, 9.24 μm, and 19.5 μm, and the volume fraction of small grains, large grains, and Mg2Sn phase was 18.6%, 77.6%, and 3.8%, respectively. Accordingly, the tensile properties reached the optimum; i.e., the tensile strength, yield strength, elongation, and Vickers hardness were 361.1 MPa, 289.5 MPa, 20.5%, and 76.3 HV, respectively.



---

*Source: 6635507-2020-12-24.xml*