# Effect of Sodium Aluminate Dosage as a Solid Alkaline Activator on the Properties of Alkali-Activated Slag Paste

Authors: Bin Chen; Jun Wang; Jinyou Zhao
Journal: Advances in Materials Science and Engineering
 (2021)

---

## Abstract

Extensive research into alkali-activated slag as a green gel material to substitute for cement has been done because of the advantages of low-carbon dioxide emissions and recycling of industrial solid waste. Alkali-activated slag usually has good mechanical properties, but the too fast setting time restricted its application and promotion. Changing the composition of alkaline activator could optimize setting time, usually making it by adding sodium carbonate or sodium sulfate but this would cause insufficient hydration reaction power and hinder compressive strength growth. In this paper, the effect of sodium aluminate dosage as an alkaline activator on the setting time, fluidity, compressive strength, hydration products, and microstructures was studied through experiments. It is fair to say that an appropriate amount of sodium aluminate could obtain a suitable setting time and better compressive strength. Sodium aluminate provided enough hydroxyl ions for the paste to promote the hydration reaction process that ensured obtaining high compressive strength and soluble aluminium formed precipitate wrapped on the surface of slag to inhibit the hydration reaction process in the early phase that prolonged setting time. The hydration mechanism research found that sodium aluminate played a key role in the formation of higher cross-linked gel hydration products in the late phase of the process. Preparing an alkali-activated slag with excellent mechanical properties and suitable setting time will significantly contribute to its application and promotion.


---

## Body

## 1. Introduction

Cement as one of the most common commodities has been widely used all over the world [1]. The production of cement consumed a large number of mineral resources and electricity, emitting big quantities of carbon dioxide that account for 5–8% of the total global carbon dioxide emissions, which caused serious damage to the ecological environment [2]. Therefore, it is urgent to find a low-carbon environment-friendly gel material to substitute cement. Alkali-activated slag (AAS) used industrial solid waste slag as raw material, formed to gel material under strong alkali excitation; in this case, it was extreme to be the green ecofriendly substitution of cement [3,4].AAS had the characteristics of low-carbon dioxide emissions and recycling of industrial solid waste, and the advantages of its good early-phase mechanical properties, high-temperature resistance, and strong corrosion resistance had been proved by many studies [5]. However, the disadvantages of AAS were the too fast setting time, cumbersome preparation process, and alkali corrosive damage; these points restricted the AAS application and promotion. Scholars spent lots of effort in solving the AAS too fast setting time and reported that the composition and content of alkaline activator were the effect factors of AAS setting time. Jiao et al. [6] demonstrated that to add Na2CO3 to NaOH as an alkaline activator could extend the setting time obviously, but the compressive strength was seriously lost. Cengiz Duran Atişt et al. [7] found that to use Na2CO3 as an alkaline activator could obtain a longer setting time than NaSiO3 and NaOH by experiment. Longer setting time led to uncompleted hydration reaction which resulted in low compressive strength when Na2CO3 was used as an alkaline activator. Furthermore, the calcite was generated that Na2CO3 was used as an alkaline activator, which was harmful to compressive strength growth. Rashad et al. [8] believed that choosing Na2SO4 as an alkaline activator could earn long setting time and low compressive strength played out at a slow rate. Previous research found that changing the alkaline activator composition by adding Na2CO3 and Na2SO4 could delay setting time but result in low compressive strength which was a key property for AAS. On the other hand, as mentioned by Sakulich et al. [9] and Huang and Han [10], changing the Si/Al ratio of the paste by adding Al2O3 could obtain a suitable setting time, and the problem of low compressive strength also existed. The addition of Al2O3 generated precipitates wrapped on the surface of slag in the early phase and the hydration reaction was inhibited that caused a long setting time [11]. The low concentration of OH− ions in the late phase of hydration reaction was because of the increased of Al3+ ions which consumed a large number of OH− ions in the paste and led to insufficient hydration reaction power and then hard to generate highly cross-linked gel which was the main reason of low growth ratio of AAS compressive strength.Many experts already noted that Na2SiO3 provided more Si4+ and OH− ions for the paste which promoted the hydration reaction progress and obtained better mechanical properties, but the too fast setting time happened against the actual operation. Although adding Na2CO3, Na2SO4, and Al2O3 could avoid too fast setting time, the big consumption or lack of much OH− ions resulted in insufficient hydration power which led to the slow growth ratio of AAS compressive strength. As we all know, the hydration power of AAS mainly relied on the number of OH− ions carried by the alkaline activator. Therefore, we here proposed using NaAlO2 as an alkaline activator and studied the effects on the setting time, fluidity, and mechanical properties of AAS. A large number of OH− ions and more soluble Al3+ ions were provided by the addition of NaAlO2 which ensured better mechanical properties and delayed the hydration reaction rate, respectively. This paper studied the NaAlO2 dosage effects on properties of fresh and hardened Na2SiO3 based AAS paste. Considering the cumbersome preparation process of liquid alkaline activator and the alkali corrosion damage during the preparation and curing, this study proposed to used solid NaAlO2 and Na2SiO3 as a composite alkaline activator. The benefit was that the slag and the solid alkaline activator were dry mixture initially and stored. The way of using was the same as cement by adding water and mixing them directly, which improved the operation convenience and reduced alkali corrosion damage.In this article, the effect of five different NaAlO2 dosages and five different Na2O contents on the setting time, fluidity, and compressive strength of AAS was studied. In addition, XRD, SEM-EDS, and FT-IR were used to analyze the hydration products, microstructures, and the vibration of chemical bonds in order to deeply explore the influence of NaAlO2 on the hydration mechanism.


## 2. Materials and Test Methods

### 2.1. Materials

The chemical components and the photograph of the slag are shown in Table1 and Figure 1, respectively. Blast furnace slag was used with a specific gravity of 2.9 g/cm3 and a specific surface of 435 m2/kg obtained from Minmetals Yingkou Medium Plate (Yingkou, China). According to the GB/T 18046-2017 [12], the slag was classified as S95. The composite solid alkaline activator was made by the mixture of solid NaAlO2 and solid Na2SiO3. NaAlO2 solid (analytical pure) was provided by Dalu Chemical Reagent Factory (Tianjin, China). Na2SiO3 solid (Na2SiO3·9H2O; ratio of Na2O to SiO2 content was 1.03 ± 0.03) was provided by Xilong Scientific Chemical Reagent Factory (Shantou, China). PO 42.5 cement (control group) was provided by Dalian Tianrui Cement Limited Company (Dalian, China).Table 1
Chemical components of blast furnace slag (%).
SiO2Al2O3CaOMgOMnOTiO2SFeOS9532.9314.9840.928.010.550.930.890.79Figure 1
Photograph of blast furnace slag.


### 2.2. Sample Preparation

Alkaline activators preparation, six different NaAlO2 dosages, and five different Na2O contents of 0%, 20%, 40%, 60%, 80%, 100% and 3%, 5%, 7%, 9%, 11%, respectively, were used. The water-to-slag ratio was kept constant at 0.35. The mixture proportions summary is shown in Table 2. For instance, the number “A8S2-5M” represented the alkaline activator with 80% NaAlO2 dosage (NaAlO2-to-Na2SiO3 ratio of 80/20) and 5% Na2O content. For AAS preparation, firstly premix the solid composite alkaline activator (NaAlO2 and Na2SiO3), slag for 2 min, and then add water. The whole mixture was agitated for 4 min, the first 2 min at a slow rate of 200 ± 5 rpm and a fast rate of 400 ± 10 rpm for the other 2 min. The AAS preparation process is shown in Figure 2. The cement test of the control group was used PO 42.5 cement (“C-1”). The water-to-cement ratio remained constant at 0.5.Table 2
Mixture proportions summary.
CodeNaAlO2 dosage (%)Na2O content (%)Slag (g)NaAlO2 (g)Na2SiO3 (g)H2O (g)A0S10-5M0515000344525A2S8-5M205150039.7275.2525A4S6-5M405150079.4206.4525A6S4-5M6051500119137.6525A8S2-5M8051500158.768.8525A10S0-5M10051500198.40525A2S8-3M203150023.8165.1525A2S8-7M207150055.6385.3525A2S8-9M209150071.4495.4525A2S8-11M2011150087.3605.5525Figure 2
The AAS preparation process.


### 2.3. Test Methods

The setting time test was implemented by the Vicat equipment on the basis of GB/T 1346-2011 [13]. Measuring at room temperature, directly the fresh paste was poured into the truncated conical mold (h = 40 mm, dtop = 65 mm, dbottom = 70 mm). The amount of fixed slag for each group was 500 g. The definition of initial setting time was from adding water into slag to the paste permeated 4 ± 1 mm value. The final setting time was defined until the cyclic annular needle printed no mark twice in a row, on the surface of AAS paste.The fluidity test used the truncated conical mold (h = 60 mm, dtop = 36 mm, dbase = 60 mm) under the standard GB/T 8077-2012 [14]. The amount of fixed slag for each group was 300 g. Firstly pour the premixed paste into the mold, and then lift the mold after scraping the surface. The fluidity value was the average value of the two perpendicular directions measurements after 0.5 min.The pastes were poured into the cuboid mold (h = 40 mm, w = 40 mm, l = 160 mm) and then the paste was vibrated by machine for 2 min basing upon GB/T 17671-1999 [15]. After that, the paste was wrapped with plastic to avert evaporation and transferred into the curing room (20 ± 2°C and RH > 50%) for 1d curing time. After samples were demolded, they were kept in the curing room till the test schedule. Compressive strength was tested during 3, 7, and 28 d curing time and loaded at rate of 2.4 kN/s using the CL-automatic compressive strength appliance. The compressive strength value was defined by the mean value of three samples for each curing time.After 3, 7, and 28 days of curing time compressive strength test, the specimens were obtained from the crushed samples and then poured into alcohol for 24 hours to discontinue hydration. Subsequently, the specimens were taken out from the alcohol and dried in a 60°C oven. For purpose of confirming the reaction mechanism and hydration products of AAS, the microtopography and elementary composition of hydration products were used by scanning electron microscopy with energy-dispersive spectrometry (SEM/EDS) and X-ray diffraction (XRD), respectively (JEOL-6360LV, Japan and Empyrean-X, Netherlands). The properties of the bonds of slag and AAS products were surveyed by Fourier transform infrared spectroscopy (FT-IR, PerkinElmer, America).


## 2.1. Materials

The chemical components and the photograph of the slag are shown in Table1 and Figure 1, respectively. Blast furnace slag was used with a specific gravity of 2.9 g/cm3 and a specific surface of 435 m2/kg obtained from Minmetals Yingkou Medium Plate (Yingkou, China). According to the GB/T 18046-2017 [12], the slag was classified as S95. The composite solid alkaline activator was made by the mixture of solid NaAlO2 and solid Na2SiO3. NaAlO2 solid (analytical pure) was provided by Dalu Chemical Reagent Factory (Tianjin, China). Na2SiO3 solid (Na2SiO3·9H2O; ratio of Na2O to SiO2 content was 1.03 ± 0.03) was provided by Xilong Scientific Chemical Reagent Factory (Shantou, China). PO 42.5 cement (control group) was provided by Dalian Tianrui Cement Limited Company (Dalian, China).Table 1
Chemical components of blast furnace slag (%).
SiO2Al2O3CaOMgOMnOTiO2SFeOS9532.9314.9840.928.010.550.930.890.79Figure 1
Photograph of blast furnace slag.


## 2.2. Sample Preparation

Alkaline activators preparation, six different NaAlO2 dosages, and five different Na2O contents of 0%, 20%, 40%, 60%, 80%, 100% and 3%, 5%, 7%, 9%, 11%, respectively, were used. The water-to-slag ratio was kept constant at 0.35. The mixture proportions summary is shown in Table 2. For instance, the number “A8S2-5M” represented the alkaline activator with 80% NaAlO2 dosage (NaAlO2-to-Na2SiO3 ratio of 80/20) and 5% Na2O content. For AAS preparation, firstly premix the solid composite alkaline activator (NaAlO2 and Na2SiO3), slag for 2 min, and then add water. The whole mixture was agitated for 4 min, the first 2 min at a slow rate of 200 ± 5 rpm and a fast rate of 400 ± 10 rpm for the other 2 min. The AAS preparation process is shown in Figure 2. The cement test of the control group was used PO 42.5 cement (“C-1”). The water-to-cement ratio remained constant at 0.5.Table 2
Mixture proportions summary.
CodeNaAlO2 dosage (%)Na2O content (%)Slag (g)NaAlO2 (g)Na2SiO3 (g)H2O (g)A0S10-5M0515000344525A2S8-5M205150039.7275.2525A4S6-5M405150079.4206.4525A6S4-5M6051500119137.6525A8S2-5M8051500158.768.8525A10S0-5M10051500198.40525A2S8-3M203150023.8165.1525A2S8-7M207150055.6385.3525A2S8-9M209150071.4495.4525A2S8-11M2011150087.3605.5525Figure 2
The AAS preparation process.


## 2.3. Test Methods

The setting time test was implemented by the Vicat equipment on the basis of GB/T 1346-2011 [13]. Measuring at room temperature, directly the fresh paste was poured into the truncated conical mold (h = 40 mm, dtop = 65 mm, dbottom = 70 mm). The amount of fixed slag for each group was 500 g. The definition of initial setting time was from adding water into slag to the paste permeated 4 ± 1 mm value. The final setting time was defined until the cyclic annular needle printed no mark twice in a row, on the surface of AAS paste.The fluidity test used the truncated conical mold (h = 60 mm, dtop = 36 mm, dbase = 60 mm) under the standard GB/T 8077-2012 [14]. The amount of fixed slag for each group was 300 g. Firstly pour the premixed paste into the mold, and then lift the mold after scraping the surface. The fluidity value was the average value of the two perpendicular directions measurements after 0.5 min.The pastes were poured into the cuboid mold (h = 40 mm, w = 40 mm, l = 160 mm) and then the paste was vibrated by machine for 2 min basing upon GB/T 17671-1999 [15]. After that, the paste was wrapped with plastic to avert evaporation and transferred into the curing room (20 ± 2°C and RH > 50%) for 1d curing time. After samples were demolded, they were kept in the curing room till the test schedule. Compressive strength was tested during 3, 7, and 28 d curing time and loaded at rate of 2.4 kN/s using the CL-automatic compressive strength appliance. The compressive strength value was defined by the mean value of three samples for each curing time.After 3, 7, and 28 days of curing time compressive strength test, the specimens were obtained from the crushed samples and then poured into alcohol for 24 hours to discontinue hydration. Subsequently, the specimens were taken out from the alcohol and dried in a 60°C oven. For purpose of confirming the reaction mechanism and hydration products of AAS, the microtopography and elementary composition of hydration products were used by scanning electron microscopy with energy-dispersive spectrometry (SEM/EDS) and X-ray diffraction (XRD), respectively (JEOL-6360LV, Japan and Empyrean-X, Netherlands). The properties of the bonds of slag and AAS products were surveyed by Fourier transform infrared spectroscopy (FT-IR, PerkinElmer, America).


## 3. Results and Discussion

### 3.1. Setting Time

AAS setting time with different NaAlO2 dosages and Na2O contents is displayed in Figure 3. The AAS setting time was related to the NaAlO2 dosage and Na2O content, ranging from 80 to 840 min. The initial and final setting times of 0% NaAlO2 dosage were 80 min and 150 min, respectively. The addition of NaAlO2 was able to prolong the setting time obviously, and the longest setting time was four times that of the shortest. The prolonged setting time was gradually shortened during the NaAlO2 dosage increasing from 20% to 60%; the prolonged setting time was gradually extended when the NaAlO2 dosage increased between 60% and 100%. It noted that the prolonged setting time does not become longer as the amount of NaAlO2 increased, meaning that the increased amount of NaAlO2 dosage does not have an absolutely positive correlation to the prolonged setting time. The different compositions and contents of the alkaline activator have an important influence on the hydration reaction rate. NaAlO2 prolonged setting time significantly, which could be explained by the active Al3+ ions from NaAlO2, NaAlO2 was hydrolyzed and then wrapped on the slag before part of slags dissolved, which caused slag dissolution suppressed. First, the free-stated OH− ions reacted with the active Al3+ wrapped on the surface of slag and the slag could only be further dissolved upon the first step is done, that is why the reaction was slow. Sakulich et al.’s [9] studies found that high concentrations of Al3+ would reduce the hydration reaction rate. However, Aydin and Baradan [16] believed that the prolonged setting time due to the active Al3+ could promote the hydration reaction in the early phase of reaction, but the resulting precipitates had no time to grow up and are hard to form a gel. Another possible reason was that the slag was fully dissolved due to high OH− ions concentration in the early phase of the hydration reaction sourced from the NaAlO2 hydrolysis. The gel generation occurred after the dissolution of slag in the hydration reaction, and most of the slag formed new gels after being dissolved, and it is fair to say that more complete dissolution could lead to longer hydration reaction time.Figure 3
AAS setting time with different NaAlO2 dosages and Na2O contents. (a) Different NaAlO2 dosages and (b) different Na2O contents.
(a)(b)On the other hand, the AAS setting time was significantly getting shorter with the increase of Na2O content. The higher Na2O content in the alkaline activator meant more OH− ions in the slurry, which was the main factor that provided the hydration power to the paste. Therefore, even though the soluble Al3+ in NaAlO2 inhibited the hydration reaction, the higher Na2O content played an important role, which significantly accelerated the hydration reaction rate and shortened the setting time. Bakharev et al. [17] believed that high Na2O content meant higher OH− concentration in the slurry, which caused the decomposition of a large number of cations such as Si4+, Al3+, and Ca2+ in the slag, accelerated the process of depolymerization and polycondensation, and resulted in rapid gel formation, which shorten the setting time. Hence, adding NaAlO2 and reducing Na2O content would prolong the AAS setting time, and the appropriate setting time could be obtained by changing the NaAlO2 dosage and Na2O content.


### 3.2. Fluidity

Figure4 shows AAS fluidity with different NaAlO2 dosages and Na2O contents of alkaline activators. All AAS fluidity was ranged from 60 to 203 mm. The difference between the lowest (for A8S2-5M) and the highest (for A0S10-5M) fluidity was around three times. For all composite solid alkaline activators activated slag, the fluidity decreased by adding NaAlO2. NaAlO2 hydrolyzed to Al3+ and OH- ions that would accelerate the process of hydration reaction [18], and Mehdizadeh and Najafi Kani [19] reported that the fluidity loss was due to the acceleration of slag decomposed and gel generated. Sasaki et al. [20] reported the slump flow values decreased with the Al3+ concentrations increasing. Another reason may be that the greater NaAlO2 dosage caused the weaker hydrolysis capacity of the paste resulting in a low rate of depolymerization of the slag, the final yield stress and apparent viscosity of the paste increased, and the fluidity gradually decreased. Xie et al. [21] believed that the decrease in yield stress would increase the fluidity of the paste. Besides, for all AAS samples, the fluidity declined with increasing Na2O content. High Na2O content resulted in high Na+ and OH− ions concentration, which would generate more Ca2+ ions from the slag. Structural disintegration product numbers were continuously accumulated and the spatial liquid paste content between slag particles was constantly increased. It caused crowded of material particles and fluidity dropped. Puertas et al. [22] discovered that the fluidity decreased with increasing of Na2O content from 3% to 4% and indicated that the higher the yield stress, the lower the fluidity. Hence, the fluidity of AAS has found a strong connection to both NaAlO2 addition and Na2O content.Figure 4
AAS fluidity with different NaAlO2 dosages and Na2O contents. (a) Different NaAlO2 dosages and (b) different Na2O contents.
(a)(b)


### 3.3. Compressive Strength

Figure5 plots the AAS compressive strength with different NaAlO2 dosages and Na2O contents at 3, 7, and 28 d curing time. 20% NaAlO2 dosage could significantly enhance the compressive strength of AAS at 3, 7, and 28 d compared with 0% NaAlO2 dosage; it indicated that NaAlO2 could enhance the AAS compressive strength. The 28 d compressive strength of AAS had a positive correlation with NaAlO2 dosage when its amount increased from 40% to 100%, but not perfect; the 3 d compressive strength of AAS was lower. The lower compressive strength was mainly due to the Al3+ ions from NaAlO2 initially wrapped on the surface of the slag particles in the early phase of hydration reaction, which inhibited the dissolution of the slag. With more NaAlO2 added, the said reaction frequency was more and led to low early compressive strength. The 3 d compressive strength of AAS with the NaAlO2 dosage of 40%, 60%, and 80% was slightly lower than that dosage of 0%. However, the rule was still followed which was the more NaAlO2 dosage caused the higher 3 d compressive strength. It could be indicated that although the cation in the NaAlO2 inhibited the hydration reaction, the higher OH− ions concentration by the addition of NaAlO2 promoted the hydration reaction more significantly. Abdalqader et al. [23] proved the OH− ions were significant to dissolve the slag glass structure and improve the process of hydration reaction.Figure 5
AAS compressive strength with different NaAlO2 dosages and Na2O contents and cement. (a) Different NaAlO2 dosages and cement and (b) different Na2O contents and cement.
(a)(b)It could be seen from the test results that the compressive strength of all AAS samples was constantly increased as the curing time increased, due to the highly gelled coagulation structure formed in the hydration product. Fernandez-Jiménez et al. [24] noticed that it was a highly cross-linked condensed structure formed to enhance AAS compressive strength benefited from the curing time increasing. In addition, the NaAlO2 dosage had a significant impact on the 28 d compressive strength of AAS that higher NaAlO2 dosage led to higher compressive strength. It showed that NaAlO2 could promote the late phase of AAS hydration reaction, made for the formation of gel with higher compressive strength. On the one hand, Al3+ ions promoted the formation of higher cross-linked gel during the late-phase hydration reaction. On the other hand, the hydrolysis of NaAlO2 brought more OH− ions to the reaction solution and promoted the formation of more gels. Garcia et al. [18] found that Al3+ ions could promote the N-A-S-H gel to form C-A-S-H gel in the late hydration reaction and enhanced the compressive strength. Kovtun et al. [25] reported the C-A-S-H gels in AAS products made higher compressive strength of AAS. It is undeniable that when NaAlO2 dosage was 100%, the hydration reaction of the AAS was slow and compressive strength of 3 and 7 d was extremely low, which could also be confirmed by the setting time test results. Shi and Qian [26] believed the hydration reaction was too slow when aluminate was used as an alkaline activator. Too slow hydration reaction rate was not conducive to the application in engineering, which also fully showed that aluminate was not suitable to be used as an alkaline activator alone. Therefore, the Al3+ and OH− ions in NaAlO2 had an impact on certain stages of the AAS hydration reaction, delayed the setting time, and improved the compressive strength of AAS.As shown in Figure5(b), the compressive strength development rules of different Na2O contents at 3, 7, and 28 d curing time were similar. Compressive strength increased by the Na2O content raised from 3% to 5%, but it declined by the Na2O content increased from 7% to 11%. Therefore, the optimum Na2O content was 5%, excessive Na2O content would reduce compressive strength. The OH− ions depolymerized Al3+, Ca2+, and other metal cations from the slag and formed new gels. However, the limited amount of slag led to an increase in the number of OH− ions, but there were not enough cations to combine with them to form a new gel, excessive Na2O content could not enhance the compressive strength of AAS continuously. On the contrary, more free state OH− ions would cause the compressive strength of AAS to weaken. Komnitsas et al. [27] reported that the alkaline activators of 8M KOH and 8% Na2SiO3 were most preferred by the compressive strength and indicated higher content would not be performed better. Jiao et al. [6] reported that among 4%, 6%, and 8% Na2O content of Na2CO3-to-NaOH as an alkaline activator, 6% obtained the best properties of the AAS paste. The compressive strength was obviously affected by the change of Na2O content and there was an optimum content. Hence, the AAS compressive strength was significantly affected by NaAlO2 dosage and Na2O content.For the application of AAS, the comparison with the compressive strength of cement samples was extremely important. The 28 d compressive strength of all AAS samples and the 3 and 7 d compressive strength of most AAS samples were greater than the cement control group, respectively, according to the standard requirements of JGJ/T 439–2018 reaching the 62.5 level standard. Considering the setting time, fluidity and compressive strength, and outstanding advantages of AAS in protecting the environment, AAS could reach the performance requirements of cement and it is important to say AAS performed better in some aspects.


### 3.4. XRD

Figure6(a) plots the XRD results of different NaAlO2 dosages. The reflected phenomenon at approximately 20–40° of all AAS was the AAS characteristic reflected corresponding to the big quantity of amorphous products. Obviously, AAS main reaction products were C–S–H (I), gismondine and calcite, and little glaucophane. C–S–H (I) was the main paste of all AAS and was reflected phenomenon at around 30° which existed in all specimens. Calcite was found in all paste and the reflected phenomenon of calcite and C–S–H (I) were overlapped; it caused C–S–H (I) to identify difficultly. The formation of calcite may be caused by sample carbonization during preparation and curing time. However, tetranatrolite was also a major product which was found in this research, and the tetranatrolite products amount increased by NaAlO2 dosage elevating. The generated tetranatrolite would cause more C-A-S-H to be generated, which had higher compressive strength. Bae et al. [28] indicated that single or multiple zeolites formation had a strong correlation with the dosage of NaAlO2. Zeolite paste was formed by C-A-S-H gel and indicated that more C-A-S-H structures are generated by elevating NaAlO2 contents, thereby improving the AAS compressive strength. Khalid et al. [29] reported that zeolites ease formed the amorphous aluminosilicate gel. Therefore, an increase in the amount of NaAlO2 would increase the compressive strength of the material. In addition, Bernal et al. [30] suggested that the amount of zeolite Na–P1 formed was obviously dependent on the addition of NaAlO2.Figure 6
XRD images of AAS and raw slag. (a) Different NaAlO2 dosages at 28 d curing time and raw slag; (b) A0S10-5M at 3, 7, and 28 d curing time and raw slag; and (c) A10S0-5M at 3, 7, and 28 d curing time and raw slag.
(a)(b)(c)Figures6(b) and 6(c) show XRD images of different curing times of AAS. The increase in peak intensity could reflect the increased amount of hydration products. A0S10-5M had already produced a large amount of C–S–H gel at 3 d curing time; however, A10S0-5M had no obvious results at 3 and 7 d curing time. The peak intensity by the curing time increased and more products generated by the reactive process continued. Cao et al. [31] declared that the hydration products did not form large numbers of C–S–H (I) gel until 28 d curing time; much tetranatrolite was generated due to the addition of NaAlO2 and the maximum amount were formed at 28 d, which correspond to the higher 28 d compressive strength and the SEM analysis.


### 3.5. SEM/EDS

Figure7 demonstrates SEM micrographs of AAS at 3 d curing time. A0S10-5M and A2S8-5M slags had undergone dissolution and polycondensation reactions, resulting in a certain amount of amorphous gel structure and being bonded to the matrix on the outer surface of slags. Most of A6S4-5M and A8S2-5M slags had begun to dissolve and some amorphous gel structures had been produced. Most of A4S6-5M and A10S0-5M slags had not been dissolved, and only a small amount of amorphous gel structure had been generated. High NaAlO2 content had a certain inhibitory effect on early gel formation. Fernández-Jiménez et al. [32] demonstrated that particles coverage with formed aluminosilicates producing also a substantial slowdown of the reaction, retarding the dissolution of Si4+ and Al3+ required by the formation of gel. Gharzounia et al. [33] suggested that the Al3+ favored the precipitation of secondary reaction products and was negatived to geopolymer network. The microstructure characteristics interpreted compressive strength phenomenon of different NaAlO2 dosages at 3 d curing time, which corresponded to compressive strength analysis.Figure 7
SEM micrographs of AAS at 3 d curing time. (a) A0S10-5M; (b) A2S8-5M; (c) A4S6-5M; (d) A6S4-5M; (e) A8S2-5M; (f) A10S0-5M.Figure8 shows a SEM micrograph of A8S2-5M at 7 d curing time. Plenty of amorphous C–S–H gel structures were produced gradually, whose shape was mainly flaky and rarely fibrous. It shows that the degree of crystallization had increased at this time, but there were still a large number of voids, and the reactants had not been wrapped tightly to form a dense whole. The paste compressive strength was lower at the moment, which was corresponding to the compressive strength test results. Wang et al. [34] found some discontinuous pastes and voids were resulting from a less compact matrix and reduced performance of materials.Figure 8
SEM micrograph of A8S2-5M at 7 d curing time.Figure9 exhibits SEM micrographs of AAS at 28 d curing time. Still, unreacted slags in the specimen can be seen, but they were embedded in the gel to form a more homogeneous whole. A0S10-5M and A4S6-5M were not as enough dense as A8S2-5M, meaning their reaction was incomplete. On the other hand, A8S2-5M had a completed degree of reaction, it formed more homogeneous and smooth gels and enclosed unreactive materials, which was one of the main reasons for the dense structure and improved compressive strength. Composite solid alkaline activator activated slag materials that had better performance in 28 d curing time, and NaAlO2 was the crucial part in improving compressive strength in the reaction late phase. Huang et al. [35] reported that, at the late phase, the formation of larger secondary crystallization and a number of amorphous aluminosilicate minerals was filled in the voids, accelerating product generation. The AAS compressive strength development could be interpreted by the composition and morphology of paste.Figure 9
SEM micrographs of AAS at 28 d curing time. (a) A0S10-5M; (b) A4S6-5M; and (c) A8S2-5M.Figures10 and 11 are SEM/EDS images of A4S6-5M and A2S8-5M at 28 d curing time, respectively. Table 3 shows the EDS conclusions of the atomic ratios. The EDS analysis outcomes proved that the large share was Ca, Si, and Al, and a relatively small share were held by Na and Mg, which mostly contributed to the formation of C-A-S-H and C-S-H. The properties of C-S-H greatly depended on adjusting Ca/Si ratios. Figures 9 and 10 show the Ca/Si ratios of the measuring points were 0.99 and 1.05 which were defined as C-S-H (I), respectively, while the Ca/Si ratios of ordinary Portland cement hydration products were greater than 1.5. Zhang et al. discovered the AAS Ca/Si ratio was about 1.1. The molecular chain Si4+ of C–S–H (I) was easily replaced by part of Al3+ ions in the system, thereby generating C-A-S-H gel. Furthermore, the Ca/Si ratios of A2S8-5M were higher than A4S6-5M, which were 1.05 and 0.99, respectively; thus, the number of Si–O bonds produced by A2S8-5M was higher than A4S6-5M and corresponded to the resulting compressive strength and FT-IR.Figure 10
SEM/EDS photograph of A4S6-5M at 28 d curing time.
(a)(b)Figure 11
SEM/EDS photograph of A2S8-5M at 28 d curing time.
(a)(b)Table 3
A4S6-5M and A2S8-5M conclusions of atomic ratio at 28 d curing time (%).
CodeOCaSiAlMgNaCa/SiA4S6-5M61.087.227.265.714.693.090.99A2S8-5M62.359.69.177.301.363.351.05


### 3.6. FT-IR

Figure12 shows determinations of FT-IR for raw slag and AAS at 28 d curing time. The wavenumber of raw slag and AAS at 2000 cm−1 had no virtual diversity, as studies before approved. Raw slag FT-IR showed the wavenumber of 947 cm−1 certified the asymmetric stretching vibration existed which was Si–O–Si bonds or Si–O–Al bonds; those were relying on glass structures of raw slag. Besides, the O–C–O bonds were represented by the wavenumber of 1429 cm−1, indicating that the surface was carbonized.Figure 12
FT-IR spectra of AAS and raw slag. (a) Different NaAlO2 dosages at 28 d curing time; (b) different Na2O contents at 28 d curing time; and (c) A2S8-5M at 3, 7, and 28 d curing time.
(a)(b)(c)AAS FT-IR indicated all AAS established similar bands, so similar products were proved. The same major wavenumbers of 3448, 1629, 1479, 961, 894, and 439 cm−1 were found in all AAS at 28 d curing time. The wavenumber of 3348 cm−1 corresponded to the O–H stretching bands, and 1629 cm−1 related to the H–O–H bending bands. Both of them stood as proof of C-(A)-S-H gel was produced and the hydration process. The wavenumber of 1479 cm−1 was related to the C=O asymmetric bands, which was derived from CO2 in the atmosphere and CO32- generated by carbonization. The results were related to the results of calcite generated by XRD analysis. The wavenumber of 961 cm−1 was the most typical characteristic bands of AAS, which represented the Si–O–Si (Al) asymmetric stretching bands. [AlO4]5− tetrahedron could replace [SiO4]4- tetrahedron on Si–O–Si chain during the reaction. Meanwhile, the alternating polycondensation of Si–O bonds and Al–O bonds occurred and caused microscopic changes in the internal structure. The Si–O–Si (Al) asymmetric stretching bands shifted obviously compared to slag. The wavenumber of 894 cm−1 was related to –OH bending bands, which together with the Si–O–Si (Al) asymmetric stretching bands proved that the alkali-activated reaction occurred. The wavenumber of 439 cm−1 was the bending vibration of the tetrahedron silicate corresponding to the [SiO4]4- tetrahedron bands of O–Si–O and Si–O–Si. The bands were presented in AAS, and its intensity generally changed little, which was correlating to the C–S–H results of XRD.Figure12(b) plots the wavenumber of 610 cm−1 of A0S10-5M was Al–O–Si symmetrical stretching bands, which indicated the part of the [AlO6]9- octahedral structure in the slag was destroyed and transformed into [AlO4]5− tetrahedron. It illustrated that the depolymerization and repolymerization of the aluminosilicate glass body structure occurred. In addition, Figure 12(b) shows the A2S8-5M wave number of 670 cm−1 implying that the wavenumbers of Si–O-T stretching bands were higher than other samples with the same bands. The higher wavenumber of Si–O-T explained that the proportion of Si–O–Si bonds was more than Si–O–Al bonds. And the energy strength of Si–O–Si bonds was stronger than Si–O–Al bonds. Hence, A2S8-5M carried the best compressive strength among all samples, which corresponded to the compressive strength results.Figure12(c) shows that the wavenumbers of Si–O-T stretching bands at 28 d curing time (at 670 cm−1) were higher than the Si–O-T stretching bands at 3 and 7 d curing time (at 610 cm−1). As said above, the proportion of Si–O–Si bonds was more than Si–O–Al bonds as the hydration reaction continued, which was corresponding to the high 28 d compressive strength results.


### 3.7. Analysis of Hydration Mechanism

Based on the macro- and microtest results and analyses, the hydration mechanism of NaAlO2 as a solid alkaline activator was as follows: the raw slag gradually reacted and dissolved under the action of composite solid alkaline activators, and the concentrations of soluble Si4+ and Al3+ ions in slag determined the chemical activity. In the reaction, the Si–O–Si and Si–O–Al bonds were broken and recombined with hydroxyl groups to form the Si(OH)4 and [Al(OH)4]−. The OH− ions as the activator of the reaction provided the environment. Subsequently, Si(OH)4 and [Al(OH)4]− underwent polycondensation and formed a multimer sol. At this time, the monovalent cations may be filled in the ring structure to balance the charge. With concentrations of ions increased, polycondensation reaction occurred between them, reformed the Si–O–Al and Si–O–Si dimer structures, and thereby formed a cyclic polymer with a longer Si–O chain hydrated sodium aluminosilicate gel by polycondensation reaction continuing. The addition of NaAlO2 provided more charged particles and hydrated hydroxyl groups on the surface, which may generate soluble Al3+ and [Al(OH)4]−. In the early phase, active soluble Al3+ wrapped the [SiO4]4− tetrahedron, which stopped the Si4+ reaction. However, in the late phase, active soluble Al3+ easily replaced the bridge [SiO4]4− tetrahedron to play the role of “bridge” and promoted the polycondensation reaction between Si(OH)4 and [Al(OH)4]−. It was noticed from the test results that Al3+ in the NaAlO2 inhibited the hydration reaction progress in the early-phase hydration reaction, but the OH− ions in the NaAlO2 promoted the hydration reaction progress more obviously. In the late hydration reaction, the Al3+ ions and OH- had a dual role which promoted the formation of the highly cross-linked gel. Hence, the bridging oxygen structure in the polymer may be stabilized, formed a higher polymer, and caused the mechanical properties of the materials improved. Figure 13 shows schematic diagram of the main hydration process of fresh and hardened slag based NaAlO2 as an alkaline activator.Figure 13
Schematic diagram of the main hydration process of fresh and hardened slag based NaAlO2 as an alkaline activator.


## 3.1. Setting Time

AAS setting time with different NaAlO2 dosages and Na2O contents is displayed in Figure 3. The AAS setting time was related to the NaAlO2 dosage and Na2O content, ranging from 80 to 840 min. The initial and final setting times of 0% NaAlO2 dosage were 80 min and 150 min, respectively. The addition of NaAlO2 was able to prolong the setting time obviously, and the longest setting time was four times that of the shortest. The prolonged setting time was gradually shortened during the NaAlO2 dosage increasing from 20% to 60%; the prolonged setting time was gradually extended when the NaAlO2 dosage increased between 60% and 100%. It noted that the prolonged setting time does not become longer as the amount of NaAlO2 increased, meaning that the increased amount of NaAlO2 dosage does not have an absolutely positive correlation to the prolonged setting time. The different compositions and contents of the alkaline activator have an important influence on the hydration reaction rate. NaAlO2 prolonged setting time significantly, which could be explained by the active Al3+ ions from NaAlO2, NaAlO2 was hydrolyzed and then wrapped on the slag before part of slags dissolved, which caused slag dissolution suppressed. First, the free-stated OH− ions reacted with the active Al3+ wrapped on the surface of slag and the slag could only be further dissolved upon the first step is done, that is why the reaction was slow. Sakulich et al.’s [9] studies found that high concentrations of Al3+ would reduce the hydration reaction rate. However, Aydin and Baradan [16] believed that the prolonged setting time due to the active Al3+ could promote the hydration reaction in the early phase of reaction, but the resulting precipitates had no time to grow up and are hard to form a gel. Another possible reason was that the slag was fully dissolved due to high OH− ions concentration in the early phase of the hydration reaction sourced from the NaAlO2 hydrolysis. The gel generation occurred after the dissolution of slag in the hydration reaction, and most of the slag formed new gels after being dissolved, and it is fair to say that more complete dissolution could lead to longer hydration reaction time.Figure 3
AAS setting time with different NaAlO2 dosages and Na2O contents. (a) Different NaAlO2 dosages and (b) different Na2O contents.
(a)(b)On the other hand, the AAS setting time was significantly getting shorter with the increase of Na2O content. The higher Na2O content in the alkaline activator meant more OH− ions in the slurry, which was the main factor that provided the hydration power to the paste. Therefore, even though the soluble Al3+ in NaAlO2 inhibited the hydration reaction, the higher Na2O content played an important role, which significantly accelerated the hydration reaction rate and shortened the setting time. Bakharev et al. [17] believed that high Na2O content meant higher OH− concentration in the slurry, which caused the decomposition of a large number of cations such as Si4+, Al3+, and Ca2+ in the slag, accelerated the process of depolymerization and polycondensation, and resulted in rapid gel formation, which shorten the setting time. Hence, adding NaAlO2 and reducing Na2O content would prolong the AAS setting time, and the appropriate setting time could be obtained by changing the NaAlO2 dosage and Na2O content.


## 3.2. Fluidity

Figure4 shows AAS fluidity with different NaAlO2 dosages and Na2O contents of alkaline activators. All AAS fluidity was ranged from 60 to 203 mm. The difference between the lowest (for A8S2-5M) and the highest (for A0S10-5M) fluidity was around three times. For all composite solid alkaline activators activated slag, the fluidity decreased by adding NaAlO2. NaAlO2 hydrolyzed to Al3+ and OH- ions that would accelerate the process of hydration reaction [18], and Mehdizadeh and Najafi Kani [19] reported that the fluidity loss was due to the acceleration of slag decomposed and gel generated. Sasaki et al. [20] reported the slump flow values decreased with the Al3+ concentrations increasing. Another reason may be that the greater NaAlO2 dosage caused the weaker hydrolysis capacity of the paste resulting in a low rate of depolymerization of the slag, the final yield stress and apparent viscosity of the paste increased, and the fluidity gradually decreased. Xie et al. [21] believed that the decrease in yield stress would increase the fluidity of the paste. Besides, for all AAS samples, the fluidity declined with increasing Na2O content. High Na2O content resulted in high Na+ and OH− ions concentration, which would generate more Ca2+ ions from the slag. Structural disintegration product numbers were continuously accumulated and the spatial liquid paste content between slag particles was constantly increased. It caused crowded of material particles and fluidity dropped. Puertas et al. [22] discovered that the fluidity decreased with increasing of Na2O content from 3% to 4% and indicated that the higher the yield stress, the lower the fluidity. Hence, the fluidity of AAS has found a strong connection to both NaAlO2 addition and Na2O content.Figure 4
AAS fluidity with different NaAlO2 dosages and Na2O contents. (a) Different NaAlO2 dosages and (b) different Na2O contents.
(a)(b)


## 3.3. Compressive Strength

Figure5 plots the AAS compressive strength with different NaAlO2 dosages and Na2O contents at 3, 7, and 28 d curing time. 20% NaAlO2 dosage could significantly enhance the compressive strength of AAS at 3, 7, and 28 d compared with 0% NaAlO2 dosage; it indicated that NaAlO2 could enhance the AAS compressive strength. The 28 d compressive strength of AAS had a positive correlation with NaAlO2 dosage when its amount increased from 40% to 100%, but not perfect; the 3 d compressive strength of AAS was lower. The lower compressive strength was mainly due to the Al3+ ions from NaAlO2 initially wrapped on the surface of the slag particles in the early phase of hydration reaction, which inhibited the dissolution of the slag. With more NaAlO2 added, the said reaction frequency was more and led to low early compressive strength. The 3 d compressive strength of AAS with the NaAlO2 dosage of 40%, 60%, and 80% was slightly lower than that dosage of 0%. However, the rule was still followed which was the more NaAlO2 dosage caused the higher 3 d compressive strength. It could be indicated that although the cation in the NaAlO2 inhibited the hydration reaction, the higher OH− ions concentration by the addition of NaAlO2 promoted the hydration reaction more significantly. Abdalqader et al. [23] proved the OH− ions were significant to dissolve the slag glass structure and improve the process of hydration reaction.Figure 5
AAS compressive strength with different NaAlO2 dosages and Na2O contents and cement. (a) Different NaAlO2 dosages and cement and (b) different Na2O contents and cement.
(a)(b)It could be seen from the test results that the compressive strength of all AAS samples was constantly increased as the curing time increased, due to the highly gelled coagulation structure formed in the hydration product. Fernandez-Jiménez et al. [24] noticed that it was a highly cross-linked condensed structure formed to enhance AAS compressive strength benefited from the curing time increasing. In addition, the NaAlO2 dosage had a significant impact on the 28 d compressive strength of AAS that higher NaAlO2 dosage led to higher compressive strength. It showed that NaAlO2 could promote the late phase of AAS hydration reaction, made for the formation of gel with higher compressive strength. On the one hand, Al3+ ions promoted the formation of higher cross-linked gel during the late-phase hydration reaction. On the other hand, the hydrolysis of NaAlO2 brought more OH− ions to the reaction solution and promoted the formation of more gels. Garcia et al. [18] found that Al3+ ions could promote the N-A-S-H gel to form C-A-S-H gel in the late hydration reaction and enhanced the compressive strength. Kovtun et al. [25] reported the C-A-S-H gels in AAS products made higher compressive strength of AAS. It is undeniable that when NaAlO2 dosage was 100%, the hydration reaction of the AAS was slow and compressive strength of 3 and 7 d was extremely low, which could also be confirmed by the setting time test results. Shi and Qian [26] believed the hydration reaction was too slow when aluminate was used as an alkaline activator. Too slow hydration reaction rate was not conducive to the application in engineering, which also fully showed that aluminate was not suitable to be used as an alkaline activator alone. Therefore, the Al3+ and OH− ions in NaAlO2 had an impact on certain stages of the AAS hydration reaction, delayed the setting time, and improved the compressive strength of AAS.As shown in Figure5(b), the compressive strength development rules of different Na2O contents at 3, 7, and 28 d curing time were similar. Compressive strength increased by the Na2O content raised from 3% to 5%, but it declined by the Na2O content increased from 7% to 11%. Therefore, the optimum Na2O content was 5%, excessive Na2O content would reduce compressive strength. The OH− ions depolymerized Al3+, Ca2+, and other metal cations from the slag and formed new gels. However, the limited amount of slag led to an increase in the number of OH− ions, but there were not enough cations to combine with them to form a new gel, excessive Na2O content could not enhance the compressive strength of AAS continuously. On the contrary, more free state OH− ions would cause the compressive strength of AAS to weaken. Komnitsas et al. [27] reported that the alkaline activators of 8M KOH and 8% Na2SiO3 were most preferred by the compressive strength and indicated higher content would not be performed better. Jiao et al. [6] reported that among 4%, 6%, and 8% Na2O content of Na2CO3-to-NaOH as an alkaline activator, 6% obtained the best properties of the AAS paste. The compressive strength was obviously affected by the change of Na2O content and there was an optimum content. Hence, the AAS compressive strength was significantly affected by NaAlO2 dosage and Na2O content.For the application of AAS, the comparison with the compressive strength of cement samples was extremely important. The 28 d compressive strength of all AAS samples and the 3 and 7 d compressive strength of most AAS samples were greater than the cement control group, respectively, according to the standard requirements of JGJ/T 439–2018 reaching the 62.5 level standard. Considering the setting time, fluidity and compressive strength, and outstanding advantages of AAS in protecting the environment, AAS could reach the performance requirements of cement and it is important to say AAS performed better in some aspects.


## 3.4. XRD

Figure6(a) plots the XRD results of different NaAlO2 dosages. The reflected phenomenon at approximately 20–40° of all AAS was the AAS characteristic reflected corresponding to the big quantity of amorphous products. Obviously, AAS main reaction products were C–S–H (I), gismondine and calcite, and little glaucophane. C–S–H (I) was the main paste of all AAS and was reflected phenomenon at around 30° which existed in all specimens. Calcite was found in all paste and the reflected phenomenon of calcite and C–S–H (I) were overlapped; it caused C–S–H (I) to identify difficultly. The formation of calcite may be caused by sample carbonization during preparation and curing time. However, tetranatrolite was also a major product which was found in this research, and the tetranatrolite products amount increased by NaAlO2 dosage elevating. The generated tetranatrolite would cause more C-A-S-H to be generated, which had higher compressive strength. Bae et al. [28] indicated that single or multiple zeolites formation had a strong correlation with the dosage of NaAlO2. Zeolite paste was formed by C-A-S-H gel and indicated that more C-A-S-H structures are generated by elevating NaAlO2 contents, thereby improving the AAS compressive strength. Khalid et al. [29] reported that zeolites ease formed the amorphous aluminosilicate gel. Therefore, an increase in the amount of NaAlO2 would increase the compressive strength of the material. In addition, Bernal et al. [30] suggested that the amount of zeolite Na–P1 formed was obviously dependent on the addition of NaAlO2.Figure 6
XRD images of AAS and raw slag. (a) Different NaAlO2 dosages at 28 d curing time and raw slag; (b) A0S10-5M at 3, 7, and 28 d curing time and raw slag; and (c) A10S0-5M at 3, 7, and 28 d curing time and raw slag.
(a)(b)(c)Figures6(b) and 6(c) show XRD images of different curing times of AAS. The increase in peak intensity could reflect the increased amount of hydration products. A0S10-5M had already produced a large amount of C–S–H gel at 3 d curing time; however, A10S0-5M had no obvious results at 3 and 7 d curing time. The peak intensity by the curing time increased and more products generated by the reactive process continued. Cao et al. [31] declared that the hydration products did not form large numbers of C–S–H (I) gel until 28 d curing time; much tetranatrolite was generated due to the addition of NaAlO2 and the maximum amount were formed at 28 d, which correspond to the higher 28 d compressive strength and the SEM analysis.


## 3.5. SEM/EDS

Figure7 demonstrates SEM micrographs of AAS at 3 d curing time. A0S10-5M and A2S8-5M slags had undergone dissolution and polycondensation reactions, resulting in a certain amount of amorphous gel structure and being bonded to the matrix on the outer surface of slags. Most of A6S4-5M and A8S2-5M slags had begun to dissolve and some amorphous gel structures had been produced. Most of A4S6-5M and A10S0-5M slags had not been dissolved, and only a small amount of amorphous gel structure had been generated. High NaAlO2 content had a certain inhibitory effect on early gel formation. Fernández-Jiménez et al. [32] demonstrated that particles coverage with formed aluminosilicates producing also a substantial slowdown of the reaction, retarding the dissolution of Si4+ and Al3+ required by the formation of gel. Gharzounia et al. [33] suggested that the Al3+ favored the precipitation of secondary reaction products and was negatived to geopolymer network. The microstructure characteristics interpreted compressive strength phenomenon of different NaAlO2 dosages at 3 d curing time, which corresponded to compressive strength analysis.Figure 7
SEM micrographs of AAS at 3 d curing time. (a) A0S10-5M; (b) A2S8-5M; (c) A4S6-5M; (d) A6S4-5M; (e) A8S2-5M; (f) A10S0-5M.Figure8 shows a SEM micrograph of A8S2-5M at 7 d curing time. Plenty of amorphous C–S–H gel structures were produced gradually, whose shape was mainly flaky and rarely fibrous. It shows that the degree of crystallization had increased at this time, but there were still a large number of voids, and the reactants had not been wrapped tightly to form a dense whole. The paste compressive strength was lower at the moment, which was corresponding to the compressive strength test results. Wang et al. [34] found some discontinuous pastes and voids were resulting from a less compact matrix and reduced performance of materials.Figure 8
SEM micrograph of A8S2-5M at 7 d curing time.Figure9 exhibits SEM micrographs of AAS at 28 d curing time. Still, unreacted slags in the specimen can be seen, but they were embedded in the gel to form a more homogeneous whole. A0S10-5M and A4S6-5M were not as enough dense as A8S2-5M, meaning their reaction was incomplete. On the other hand, A8S2-5M had a completed degree of reaction, it formed more homogeneous and smooth gels and enclosed unreactive materials, which was one of the main reasons for the dense structure and improved compressive strength. Composite solid alkaline activator activated slag materials that had better performance in 28 d curing time, and NaAlO2 was the crucial part in improving compressive strength in the reaction late phase. Huang et al. [35] reported that, at the late phase, the formation of larger secondary crystallization and a number of amorphous aluminosilicate minerals was filled in the voids, accelerating product generation. The AAS compressive strength development could be interpreted by the composition and morphology of paste.Figure 9
SEM micrographs of AAS at 28 d curing time. (a) A0S10-5M; (b) A4S6-5M; and (c) A8S2-5M.Figures10 and 11 are SEM/EDS images of A4S6-5M and A2S8-5M at 28 d curing time, respectively. Table 3 shows the EDS conclusions of the atomic ratios. The EDS analysis outcomes proved that the large share was Ca, Si, and Al, and a relatively small share were held by Na and Mg, which mostly contributed to the formation of C-A-S-H and C-S-H. The properties of C-S-H greatly depended on adjusting Ca/Si ratios. Figures 9 and 10 show the Ca/Si ratios of the measuring points were 0.99 and 1.05 which were defined as C-S-H (I), respectively, while the Ca/Si ratios of ordinary Portland cement hydration products were greater than 1.5. Zhang et al. discovered the AAS Ca/Si ratio was about 1.1. The molecular chain Si4+ of C–S–H (I) was easily replaced by part of Al3+ ions in the system, thereby generating C-A-S-H gel. Furthermore, the Ca/Si ratios of A2S8-5M were higher than A4S6-5M, which were 1.05 and 0.99, respectively; thus, the number of Si–O bonds produced by A2S8-5M was higher than A4S6-5M and corresponded to the resulting compressive strength and FT-IR.Figure 10
SEM/EDS photograph of A4S6-5M at 28 d curing time.
(a)(b)Figure 11
SEM/EDS photograph of A2S8-5M at 28 d curing time.
(a)(b)Table 3
A4S6-5M and A2S8-5M conclusions of atomic ratio at 28 d curing time (%).
CodeOCaSiAlMgNaCa/SiA4S6-5M61.087.227.265.714.693.090.99A2S8-5M62.359.69.177.301.363.351.05


## 3.6. FT-IR

Figure12 shows determinations of FT-IR for raw slag and AAS at 28 d curing time. The wavenumber of raw slag and AAS at 2000 cm−1 had no virtual diversity, as studies before approved. Raw slag FT-IR showed the wavenumber of 947 cm−1 certified the asymmetric stretching vibration existed which was Si–O–Si bonds or Si–O–Al bonds; those were relying on glass structures of raw slag. Besides, the O–C–O bonds were represented by the wavenumber of 1429 cm−1, indicating that the surface was carbonized.Figure 12
FT-IR spectra of AAS and raw slag. (a) Different NaAlO2 dosages at 28 d curing time; (b) different Na2O contents at 28 d curing time; and (c) A2S8-5M at 3, 7, and 28 d curing time.
(a)(b)(c)AAS FT-IR indicated all AAS established similar bands, so similar products were proved. The same major wavenumbers of 3448, 1629, 1479, 961, 894, and 439 cm−1 were found in all AAS at 28 d curing time. The wavenumber of 3348 cm−1 corresponded to the O–H stretching bands, and 1629 cm−1 related to the H–O–H bending bands. Both of them stood as proof of C-(A)-S-H gel was produced and the hydration process. The wavenumber of 1479 cm−1 was related to the C=O asymmetric bands, which was derived from CO2 in the atmosphere and CO32- generated by carbonization. The results were related to the results of calcite generated by XRD analysis. The wavenumber of 961 cm−1 was the most typical characteristic bands of AAS, which represented the Si–O–Si (Al) asymmetric stretching bands. [AlO4]5− tetrahedron could replace [SiO4]4- tetrahedron on Si–O–Si chain during the reaction. Meanwhile, the alternating polycondensation of Si–O bonds and Al–O bonds occurred and caused microscopic changes in the internal structure. The Si–O–Si (Al) asymmetric stretching bands shifted obviously compared to slag. The wavenumber of 894 cm−1 was related to –OH bending bands, which together with the Si–O–Si (Al) asymmetric stretching bands proved that the alkali-activated reaction occurred. The wavenumber of 439 cm−1 was the bending vibration of the tetrahedron silicate corresponding to the [SiO4]4- tetrahedron bands of O–Si–O and Si–O–Si. The bands were presented in AAS, and its intensity generally changed little, which was correlating to the C–S–H results of XRD.Figure12(b) plots the wavenumber of 610 cm−1 of A0S10-5M was Al–O–Si symmetrical stretching bands, which indicated the part of the [AlO6]9- octahedral structure in the slag was destroyed and transformed into [AlO4]5− tetrahedron. It illustrated that the depolymerization and repolymerization of the aluminosilicate glass body structure occurred. In addition, Figure 12(b) shows the A2S8-5M wave number of 670 cm−1 implying that the wavenumbers of Si–O-T stretching bands were higher than other samples with the same bands. The higher wavenumber of Si–O-T explained that the proportion of Si–O–Si bonds was more than Si–O–Al bonds. And the energy strength of Si–O–Si bonds was stronger than Si–O–Al bonds. Hence, A2S8-5M carried the best compressive strength among all samples, which corresponded to the compressive strength results.Figure12(c) shows that the wavenumbers of Si–O-T stretching bands at 28 d curing time (at 670 cm−1) were higher than the Si–O-T stretching bands at 3 and 7 d curing time (at 610 cm−1). As said above, the proportion of Si–O–Si bonds was more than Si–O–Al bonds as the hydration reaction continued, which was corresponding to the high 28 d compressive strength results.


## 3.7. Analysis of Hydration Mechanism

Based on the macro- and microtest results and analyses, the hydration mechanism of NaAlO2 as a solid alkaline activator was as follows: the raw slag gradually reacted and dissolved under the action of composite solid alkaline activators, and the concentrations of soluble Si4+ and Al3+ ions in slag determined the chemical activity. In the reaction, the Si–O–Si and Si–O–Al bonds were broken and recombined with hydroxyl groups to form the Si(OH)4 and [Al(OH)4]−. The OH− ions as the activator of the reaction provided the environment. Subsequently, Si(OH)4 and [Al(OH)4]− underwent polycondensation and formed a multimer sol. At this time, the monovalent cations may be filled in the ring structure to balance the charge. With concentrations of ions increased, polycondensation reaction occurred between them, reformed the Si–O–Al and Si–O–Si dimer structures, and thereby formed a cyclic polymer with a longer Si–O chain hydrated sodium aluminosilicate gel by polycondensation reaction continuing. The addition of NaAlO2 provided more charged particles and hydrated hydroxyl groups on the surface, which may generate soluble Al3+ and [Al(OH)4]−. In the early phase, active soluble Al3+ wrapped the [SiO4]4− tetrahedron, which stopped the Si4+ reaction. However, in the late phase, active soluble Al3+ easily replaced the bridge [SiO4]4− tetrahedron to play the role of “bridge” and promoted the polycondensation reaction between Si(OH)4 and [Al(OH)4]−. It was noticed from the test results that Al3+ in the NaAlO2 inhibited the hydration reaction progress in the early-phase hydration reaction, but the OH− ions in the NaAlO2 promoted the hydration reaction progress more obviously. In the late hydration reaction, the Al3+ ions and OH- had a dual role which promoted the formation of the highly cross-linked gel. Hence, the bridging oxygen structure in the polymer may be stabilized, formed a higher polymer, and caused the mechanical properties of the materials improved. Figure 13 shows schematic diagram of the main hydration process of fresh and hardened slag based NaAlO2 as an alkaline activator.Figure 13
Schematic diagram of the main hydration process of fresh and hardened slag based NaAlO2 as an alkaline activator.


## 4. Conclusions

The effects of NaAlO2 dosage and Na2O content on the setting time, fluidity, compressive strength, and microstructures of AAS paste were studied. The solid alkaline activator was convenient for experimental operation. The main conclusions of the article were as follows.(1)
Both NaAlO2 dosage and Na2O content were critical points of the AAS paste properties.(2)
The setting time could be increased by adding NaAlO2 and decreasing the Na2O content.(3)
The addition of NaAlO2 had a great contribution to the late phase of the hydration reaction process that resulted in higher compressive strength.(4)
With adding NaAlO2, the AAS microstructure became denser and the pore decreased in the late phase of hydration reaction. The main reaction products were C–S–H (I), gismondine, calcite, and tetranatrolite; the amount of tetranatrolite products increased by NaAlO2 elevating.(5)
NaAlO2 hydration produced Al3+ and OH− ions; the coating of the Al3+ ions on the surface of slag particles inhibited the early-phase hydration reaction, prolonged the setting time, and promoted the formation of high cross-linked gels in the late phase of hydration reaction resulting in improving the compressive strength. However, the OH− ions provided sufficient hydration power which ensured that AAS could obtain better mechanical properties in both the early phase and later phase of hydration reaction.



---