# Electron Transport Characteristics of Wurtzite GaN

Authors: F. M. Abou El-Ela; A. Z. Mohamed
Journal: ISRN Condensed Matter Physics
 (2013)

---

## Abstract

A three-valley Monte Carlo simulation approach was used to investigate electron transport in wurtzite GaN such as the drift velocity, the drift mobility, the average electron energy, energy relaxation time, and momentum relaxation time at high electric fields. The simulation accounted for polar optical phonon, acoustic phonon, piezoelectric, intervalley scattering, and Ridley charged impurity scattering model. For the steady-state transport, the drift velocity against electric field showed a negative differential resistance of a peak value of2.9×105 m/s at a critical electric field strength 180×105 V/m. The electron drift velocity relaxes to the saturation value of 1.5×105 m/s at very high electric fields. The electron velocities against time over wide range of electric fields are reported.


---

## Body

## 1. Introduction

In recent years, nearly all electronic and optoelectronic devices have been realized using alloys of the III–V nitrides, gallium nitride (GaN), aluminum nitride (AlN), and indium nitride (InN) [1, 2]. There has been considerable interest in GaN due to its wide band gap and favorable material properties, such as high electron mobility and very high thermal conductivity [3]; GaN and related compounds with aluminum and indium currently have great potential for applications in optoelectronics devices in the frequency range from microwaves to ultraviolet, quantum dots infrared photodetectors [4–7]. GaN also has large speed electron velocity and can be used for electronics devices [8].The electron transport characteristics of the III–V nitride semiconductor, GaN, have long been recognized. In 1975, Littlejohn et al. [9] were the first to report results obtained from semiclassical Monte Carlo simulations of the steady-state electron transport within bulk wurtzite GaN.In 1993, Gelmont et al. [10] reported on ensemble semi-classical two-valley Monte Carlo simulations of the electron transport within bulk wurtzite GaN; this analysis improvs upon the analysis of Littlejohn et al. [9], by incorporating intervalley scattering into the simulations. In 1995, Mansour et al. [11] reported the use of such an approach in order to determine how the crystal temperature influences the velocity-field characteristic associated with bulk wurtzite GaN. Kolnik et al. [12] reported on employing full-band Monte Carlo simulations of the electron transport within bulk wurtzite GaN and bulk zinc-blende GaN.In 1998, Albrecht et al. [13] reported on employing ensemble semiclassical five-valley Monte Carlo simulations of the electron transport within bulk wurtzite GaN, with the aim of determining elementary analytical expressions for a number of electron transport parameters corresponding to bulk wurtzite GaN. The first known study of transient electron transport within the III–V nitride semiconductors was that carried by Foutz et al. reported in 1997 [14].On the experimental front, in 2000, Wraback et al. [15] reported on the use of a femtosecond optically detected time-of-flight experimental technique in order to experimentally determine the velocity-field characteristic associated with bulk wurtzite GaN.An understanding of the electron transport in GaN is necessary to improve GaN semiconductors based devices. Transport properties of GaN at both steady state and transient state has been discussed extensively over the year; uncertainty in material band parameters remains a key source of ambiguity in analysis of the electron transport properties.


## 2. Monte Carlo Simulation

In order to calculate the electron drift velocity for large electric fields, consideration of conduction band satellite valleys is necessary. A three-valley model of the conduction band using parameters for wurtzite phase GaN is used. The scatterings considered in our calculation are polar optical phonon, acoustic deformation potential, piezoelectric, charged impurity scattering, and intervalley scattering. Our Monte Carlo simulations differ from other monte carlo simulation due to the use of Ridley charged impurity model and including the electron temperature at high electric fields. For more details of these scattering mechanisms, the reader is referred to [16–19].We simulate 10000 electrons and the crystal temperature is set to 300 K. Nonparabolicity is considered in the lowest conduction band valley; this nonparabolicity is treated through the application of the Kane model [17–19].The material parameters used for our simulations are tabulated in Table1. These parameters selections are from [1] and originally from [20] for GaN. The valley parameters selections are presented in Table 2 [1]. These parameters were originally determined from the band structural calculations of [21].Table 1
The material parameters corresponding to wurtzite GaN.
Parameter
Value
Mass density (kg/m3)
6150
Sound velocity (m/s)
6560
Acoustic deformation potential (eV)
8.3
Static dielectric constant
8.9
High-frequency dielectric constant
5.35
Piezoelectric constant,e14 (C/m2)
0.375
Optical phonon energy (eV)
0.0912
Intervalley deformation potentials (eV/m)
1011
Intervalley phonon energies (eV)
0.0912Table 2
The valley parameters corresponding to wurtzite GaN.
Valley
Γ1
Γ2
L-M
Valley degeneracy
1
1
6
Effective mass
0.2me
m
e
m
e
Intervalley energy separation (eV)
—
1.9
2.1
Energy gap (eV)
3.39
5.29
5.49
Nonparabolicity (eV−1)
0.189
0.0
0.0


## 3. Charged Ionized Impurity Scattering Rate

The scattering rate of electron by charged ionized donor in GaN may be calculated according to Brooks and Herring (B.H) model [22]
(1)ΓBH(k)=2NIe4m*1/28ε2ℏ2qc2(1+2αE)γ1/2(E)[11+(qc/2k)2].Erepresents the electron energy, m* is the effective mass, α is the nonparabolicity factor, and  ε represents  the high frequency dielectric constant, where NI is the density of impurity atoms, while qc is the inverse screening length defined by qc=Ne2/εkBTe, N is the electron concentration, Te is the electron temperature, and γ(E)=E(1+αE).Ridley [16, 19] proposed a model, which becomes convenient to use in the Monte Carlo method [23] since it solves the problem of cutting the impurity scattering at very small electron energy in the B.H model, at the same time it reconciles between the different proposed models used before
(2)ΓR(k)=v(k)a[1-exp(-aΓBH(k)v(k))]ΓR(k), ΓBH(k) represent the Ridley  and the Brooks Herring impurity scattering rates respectively; v(k) is the electron group velocity and a is the average distance apart the impurity center which is given by Ridley [16, 17]
(3)a=(2πNI)-1/3.


## 4. Results and Discussion

Figure1 illustrates the computed scattering rates for phonons in the Γ1 valley; it is clear that piezoelectric scattering rate weakens towards high electron energies. The principle source of scattering is that due to optical type phonons either through polar interaction or through intervalley deformation potential mechanism. It is seen that the acoustic scattering rate is very small compared with polar optical phonon scattering rate.Figure 1
Scattering rates versus electron energy in theΓ1 valley.Figure2 shows a comparison between the Brooks Herring (B.H) model at ionized impurity concentration of 1017 cm−3 and the Ridley model (R), at different impurity concentration. In both models we have assumed the electron temperature equivalence 300 K.  Additionally, the impurity concentration is taken to be equivalent to the free electron concentration. There is a large reduction of the scattering rate in the Ridley (R) model compared to the (B.H) model, especially at small electron energy. Consequently, it is more reasonable to use the Ridley model in the Monte Carlo method, since it solves the problem of cutting the impurity scattering at very small electron energy.Figure 2
Impurity scattering rates versus electron energy in theΓ1 valley.The velocity-field characteristic associated with Wurtzite GaN is presented in Figure3 as function of electric fields for lattice temperature 300 K and ionized impurity concentration equal to 1017cm-3;  results from other group and various available experimental data [24–26] are also included for comparison.Figure 3
The velocity-field characteristic.At applied electric fields less than50×105 V/m, the scattering processes are dominated by acoustic deformation potential, piezoelectric phonon scattering, and impurity scattering. Thus, at low fields, where the electron temperature is less than the polar optical phonon temperature, Polar optical phonon emissions are a rare event and the free carriers remain a majority in the Γ1 valley where their effective mass is weak. Their speed increases with the electric field to reach a maximum value of 2.9×105 m/s for a critical field 180×105 V/m.At the critical field, the electrons gain more and more energy so they are excited and transferred to the upper valleys where they become heavier. The possibility of their collisions increases, which slows them and their steady-state velocity begins to reduce. This is in response to further increases in the applied electric field strength; that is, a region of negative differential mobility is observed. At very high fields, the electron saturation drift velocities are in the order of1.5×105 m/s. Our calculations of steady-state drift velocity curve were in a fair agreement with those given by other groups at low electric field while at high field experimental values are significantly lower. Also due to the scattering mechanisms used and different chosen data parameters there are modest agreement at high fields with other simulation results.The average electron energy as a function of the applied electric field is shown in Figure4, initially, the average electron energy remains low, only slightly higher than the thermal energy 3/2kBT. We see that there is a sudden increase around 150×105 V/m. This increase is due to the fact that the dominant energy loss mechanism for GaN is polar optical phonon scattering. When the applied electric field is less than 100×105 V/m, all of the energy that the electrons gain from the applied electric field is lost through polar optical phonon scattering. The other scattering mechanisms, that is, piezoelectric scattering, impurity scattering, and acoustic deformation potential scattering, do not remove energy from the electron ensemble; they are elastic scattering mechanisms.Figure 4
The average electron energy as a function of the applied electric field.However, beyond certain critical applied electric field strength, the polar optical phonon scattering mechanism can no longer remove all of the energy gained from the applied electric field. Other scattering mechanisms must start to play a role if the electron ensemble is to remain in equilibrium. The average electron energy increases until intervalley scattering begins and an energy balance is reestablished.Figure5 illustrates the fractional electron number as a function of the applied electric field. As the applied electric field is increased beyond 150×105 V/m, the average electron energy increases until a substantial fraction of the electrons have acquired enough energy in order to transfer into the upper valleys of the conduction band. As the effective mass of the electrons in the upper valleys is greater than that in the lowest valley, the electrons in the upper valleys will be slower. Finally, at high applied electric fields, the number of electrons in each valley saturates. At this point, the electron drift velocity stops decreasing and achieves saturation.Figure 5
The fractional electron number as a function of the applied electric field.The spreading of the distribution function (D.F.) as a function of energy in theΓ1 valley of GaN is shown in Figure 6, where the electric field varies from 50 × 105 V/m to 300×105 V/m. The kink in the energy distribution appears at electron energy equivalent to the phonon energy, that is, ħω. There is another kink when the electron energy reaches 2ħω, represents iterative emission of two phonons, which is possible only at lattice temperature of 300 K.Figure 6
The number of distribution functions against electron energy in theΓ1 valley.In Figure7, the average electron drift mobility has its maximum value at very low values of the electric field due to the smallest effective mass for the electrons in the central valley. The negative differential mobility NDM is observed by increasing the electric field due to intervalley mechanism. Linear low-field electrons drift velocity dependence on the applied electric field, vd=μF in this regime. At high electric field, the average electron drift mobility reaches low values due to the increase of electron effective mass in higher valleys.Figure 7
The average drifts mobility as a function of electric field.The effective momentum relaxation timeτm and the effective energy relaxation time τe at steady state are given respectively, by Foutz et al. [20]:
(4)τm=m*VdqF,τe=E-E0qVdF,
where E0=3/2KBTL, TL is the lattice temperature, and KB is Boltzmann constant. The energy-dependent effective mass m* is an average of the effective mass (m*=m0*(1+2αE)) over the ensemble.Figures8 and 9 show the momentum relaxation time and the energy relaxation time versus electric fields in GaN. The momentum relaxation time decreases as electric field increases at applied electric fields corresponding to a field higher than 100×105 V/m, which is a negative differential resistance (NDR) region due to intervalley scattering to higher Γ2 and M-L valleys. On the contrary, the energy relaxation time increases for the same reasons which were already mentioned.Figure 8
The momentum relaxation time as a function of the electric field.Figure 9
The Energy relaxation time as a function of the electric field.We examine transient electron transport in bulk wurtzite GaN for a variety of applied field strengths. Figure10 illustrates the time dependence of the electron drift velocity and the electron energy for electric field ranging between (50–300)×105 V/m. Below the critical field (170×105 V/m), the electron drift velocity reaches steady state very quickly with no velocity overshoot. For applied electric field strengths above the critical value, the electrons gain a greater energy in the Γ1 valley where the electron effective mass is lowest. They are getting a great acceleration which enables them to reach the electron peak velocity; that is, an overshoot occurs. Then the electrons transfer to the upper valleys where they become heavier and their velocity decreases toward its steady-state value.The time dependence of (a) the electron drift velocity and (b) the electron energy.
(a)
(b)


## 5. Conclusions

Electron transport in wurtzite GaN at room temperature has been simulated by the ensemble Monte Carlo method. The main feature of our calculated results, due to the scattering mechanisms, is an ohmic region at low fields lower than the threshold field, where all electrons occupy theΓ1 valley, followed by a negative differential resistance, which occurs as a consequence of the intervalley electron transfer mainly from the Γ1 to the Γ2 valley at fields larger than the threshold field, since a significant number of electrons can have energies in excess of the Γ1-Γ2 difference and it is possible for them to be scattered in the Γ2 valley by short wave length phonons. An electron in the Γ2 valley has an effective mass much larger than its value in the Γ1 valley. Consequently, the average velocity becomes less than the ohmic value as the field strength increases. The transfer to the Γ2 minimum is sufficiently rapid as the field strength increases; thus, the intervalley transfer mechanism could lead to a negative differential mobility. Finally, the velocity overshoot occurs only over very small distances for electrons injected at higher energies.



---

*Source: 654752-2013-09-09.xml*