# Study of Ag and Au Nanoparticles Synthesized by Arc

Authors: Der-Chi Tien; Liang-Chia Chen; Nguyen Van Thai; Sana Ashraf
Journal: Journal of Nanomaterials
 (2010)

---

## Abstract

The paper presents a study of Ag and Au nanofluids synthesized by the arc discharge method (ADM) in deionized water. The metallic Ag nanoparticle (Ag0) and ionic Ag (Ag+) have played  an important role in the battle against germs which are becoming more drug-resistant every year. Our study indicates that Ag nanoparticle suspension (SNPS) fabricated by using ADM without added surfactants exclusively contains the metallic Ag nanoparticle and ionic Ag. Besides that, the ADM in deionized water has also been employed for the fabrication process of Au nanoparticles. The experimental results indicate that the prepared Ag nanoparticles can react with the dissolved H2CO3 in deionized water, leading to the formation of Ag2CO3. Significantly different to Ag, the prepared Au nanoparticles with their surfaces bonded by oxygen are suspended in deionized water by the formation of hydrogen bonded with the neighboring water molecules.


---

## Body

## 1. Introduction

Metal nanoparticles have often been studied and used in nanotechnology. Silver has been used to preserve drinking water from germs since the periods of the Egyptian and Roman empires. It even has been used to preserve milk by putting silver coins in milk since the 18th century by immigrants to America. 1% of silver nitrate solution has been employed as eye drops to prevent eye disease in newborn since 1884 [1]. In addition, silver foil has also been used to protect wounds from infection since World War I. To preserve the purity of drinking water on a spacecraft, since the 1970s, the National Aeronautics and Space Administration (NASA) has employed containers made from silver for preserving drinking water. However, since the human being overused too many antibiotics over a long time, thus some of bacteria, such as MRSA (Methicillin Resistant Staphylococcus Aureus) [2] and VRSA (Vancomycin Resistant Staphylococcus Aureus) [3]  have become resistant to antibiotics. To overcome this problem, the physical and chemical properties of silver have been modified by raising the surface-to-volume ratio [4] of metallic Ag nanoparticles [5], which play an increasingly important role in the battle against germs. A new method in synthesizing Ag nanoparticle suspension (SNPS), the arc discharge method (ADM) [6–9], has been successfully developed. From the experimental results and analysis, it was confirmed that this method was fast, simple, and easily adaptable to mass production. The synthesized SNPS contained the ionic Ag components which increase its germ-killing ability [10] and is capable of becoming a major weapon against germs in the postantibiotic era [11].Similarly, Au and Au nanoparticles have been studied aiming at a variety of applications, such as catalysis, bio-labeling, nonlinear optical devices, and optical recording media. Producing Au nanoparticles are usually classified into chemical and physical methods. The chemical method usually involves toxic chemicals to be dangerous to the environment. The physical method includes UV and IR radiation, aerosol technology and lithography [12, 13]. The pure Au nanoparticles is successfully produced by using these methods, however they require using some of stabilizer preventing Au nanoparticles from agglomeration. Especially, these methods may remain quite expensive and potentially dangerous for the environment. To resolve this, a new method is developed to produce Au nanoparticles by direct-current (DC) arc discharge in water. During the arc discharge process, when the temperature between electrodes reaches several thousand °C [14], Au wires are etched in the water medium. The vaporized metal can be condensed more efficiently in the dielectric liquid than in a gas phase. Au vapor condensed in water creates a stable Au aqueous suspension. Well-separated nanosize Au clusters in pure water can be thermodynamically stable for a long time. This study mainly investigates the suspension mechanism of the prepared Au nanoparticles and the Ag nanoparticles.Some of experimental apparatuses, such as conductivity meters, centrifuges, titrators, and atomic absorption spectrophotometers, have been used to identify and measure the proportion of ionic silver. Similarly, a DC arc discharge system which consists of two Au electrodes, a servo control system, a power supply system, and a glass tank has been used to fabricate the Au nanoparticles in deionized water.The rest of the paper is organized in the following order. Section2 describes the experimental method to fabricate Au and Ag nanoparticles. Analysis of the experimental results is presented in Section 3 then followed by conclusions in Section 4.


## 2. Experiments

### 2.1. Materials

In our experimental setup,  silver and Au wires employed as processed materials (Gredmann, 99.99%, 1 mm in diameter) are submerged in deionized water (pH=6.5, conductivity =0.8~0.9 μS) and used as the electrodes in preparing the Ag and Au nanoparticle suspension.


### 2.2. Experimental System Setup

Figure1 shows the DC arc discharge system, consisting of four main parts as follows:(i)
two Ag or Au electrodes(ii)
a servo control system used to maintain the distance between electrodes to be constant(iii)
a power supply system employed to control the DC arc discharge parameters(iv)
a glass tank for containing the deionized water and a Teflon electrode holder used to collect the Ag or Au colloidFigure 1
The DC arc discharge system.The preparation process of the Ag and Au nanoparticle suspension by using ADM mainly bases on some of parameters, such as initial voltage, peak current, on- and off-pulse duration, pressure, the gap between electrodes, temperature and volume of deionized water, and fabrication time, as shown in Table1.Table 1
Some of key parameters for colloidal Ag production.
ParameterValueInitial voltage135 VPeak current6.4 AOn-pulse duration50μsOff-pulse duration50μsTemperature of deionized water25°CFabrication pressure1 atmVolume of deionized water500 mLFabrication time60 s


### 2.3. Identification ofAg+ and Ag0

During the arc discharge, both ionic silver (Ag+) and metallic Ag nanoparticle (Ag0) can be generated. The following apparatuses are used to identify the metallic Ag nanoparticle and ionic Ag(i)
a conductivity meter (JENCO 6307) employed to measure number of ions in the solution and quickly perform qualitative analysis(ii)
a particle sizer (Malvern Instruments ZS-90) used to analyze the distribution of the metallic Ag nanoparticle in suspension: base on this analysis, the velocity and required time can be determined to achieve the optimal conditions for the centrifuge(iii)
a centrifuge (Hettich,  Mikro 22R) used to separate the SNPS into particles and ions: inside the centrifuge, particles are precipitated while ionic Ag  is dissolved in water(iv)
a titrator (METTLER TOLEDO-DL50) used to estimate the concentration of the ionic Ag in the solution(v)
an atomic absorption spectrophotometer (Shimadzu AA-680) used to measure the concentration of ionic Ag below the threshold of 6 ppm and check the accuracy of the estimation made with the above titratorThe conductivity meter was employed to measure the conductivity of the SNPS produced by using ADM and deionized water with a conductivity of 20.1μS/cm and 0.5 μS/cm, respectively. The conductivity of the SNPS was greater than that of deionized water. This indicates that the SNPS contains ions. However, this measure cannot distinguish the type of ions.In an attempt to explore the nature of ions, ions were then separated from the particles by using a centrifuge and evaluated by a qualitative and quantitative analysis. During the separation process, particles were precipitated while ions were not affected. A disadvantage of this method lies in that it could be impossible to complete the separation process in a short period of time if the particles in the suspension were too small (less than a few nanometers).To overcome the above problem, the diameter of the SNPS particles was measured first. Figure2 shows the sizes and size distribution of particles. In the diagram, it can be seen that Ag particles larger than 10 nanometers must be first separated in the centrifuge, in order to remove at least of 96% the metallic Ag nanoparticles.Figure 2
Size distribution of Ag nanoparticles.The centrifuge used to precipitate Ag nanoparticles was set up with some specific parameters as follows: the radius and rotating speed were 7.5 cm and 18,000 rpm, respectively. The relative centrifugal force (RCF) was then calculated by applying.(1)RCF=1.118×10-5×r×N2,
where RCF is the relative centrifugal force (cm/sec2), r is the rotational radius (cm), and N is the rotating speed (revolutions per minute, RPM).The minimum time so that the centrifuge can separate ions was 100 minutes,  which was evaluated by using  using Stokes’ Law:(2)Vs=2×rp2×(ρp-ρf)×RCF9η,
where Vs is the particles' settling velocity (cm/sec), rp is the Stokes radius of particles (cm), ρp is the density of particles (g/cm3), ρf is the density of deionized water (g/cm3), and η is the viscosity of deionized water (dynesec/cm2).Figure3 illustrates the identification process of ionic Ag. First, the ADM was used to fabricate SNPS from deionized water and an Ag rod. A centrifuge (18,000 rpm-100 minutes) was then used to extract the ionic Ag (being contained in the supernatant-Ag+) and the metallic Ag nanoparticles (being contained in the sediment-Ag0). The quantitative analysis of the ionic Ag could be directly carried out on the supernatant (Ag+). However, the quantitative analysis of the metallic Ag nanoparticle requires the addition of an appropriate amount of nitric acid (65%), so that the sediment (Ag0) can be fully dissolved. This mixture is then diluted with deionized water, so that it can be reset to the original volume.Figure 3
Identification process of ionic Ag.


### 2.4. Fabrication Au Nanoparticles

Au wires were used as the positive and negative electrodes and they would be etched in deionized water if the power supply system provides a stable pulse voltage. To ionize the aqua medium between electrodes and the DC arc discharge with a pulse voltage of around 70–100 V was first provided within 2-3μs. Following this, shown in Figure 4, a pulse voltage of around 20–40 V was employed within 10 μs while the etching current was maintained at 4A.Figure 4
Current and voltage pulses created by the DC arc discharge system during etching of the Au electrodes.The servo control system was based on a close-looped feedback to control the gap between two electrodes (within a few microns). The upper Au electrode was held by the servo control system while the bottom one was fixed by the Teflon ring. The temperature of deionized water in the tank was maintained at the room temperature.The surface layer of Au wires was evaporated and then condensed in water to create the Au suspension. The colloidal Au was then collected. The size distribution, zeta potential, and optical properties of Au particles could be determined through the inspection and analysis of the colloidal Au. A field emission scanning electron microscope (FE-SEM, HITACHI S4700) was applied to determine the size distribution of Au nanoparticles. The Energy Dispersive X-ray (EDX) spectrum was taken to demonstrate the chemical composition of prepared Au particles. A NanoZS90 system (Malvern) was used to measure the zeta potential of the aqueous suspension of the charged Au particles. The measurement of the zeta potential was mainly based on particle velocity in the unit electric field. The double-beam UV-VIS spectrophotometer (9423UVA1002E Helios Alpha) was used to analyze optical properties of Au nanoparticles.


## 2.1. Materials

In our experimental setup,  silver and Au wires employed as processed materials (Gredmann, 99.99%, 1 mm in diameter) are submerged in deionized water (pH=6.5, conductivity =0.8~0.9 μS) and used as the electrodes in preparing the Ag and Au nanoparticle suspension.


## 2.2. Experimental System Setup

Figure1 shows the DC arc discharge system, consisting of four main parts as follows:(i)
two Ag or Au electrodes(ii)
a servo control system used to maintain the distance between electrodes to be constant(iii)
a power supply system employed to control the DC arc discharge parameters(iv)
a glass tank for containing the deionized water and a Teflon electrode holder used to collect the Ag or Au colloidFigure 1
The DC arc discharge system.The preparation process of the Ag and Au nanoparticle suspension by using ADM mainly bases on some of parameters, such as initial voltage, peak current, on- and off-pulse duration, pressure, the gap between electrodes, temperature and volume of deionized water, and fabrication time, as shown in Table1.Table 1
Some of key parameters for colloidal Ag production.
ParameterValueInitial voltage135 VPeak current6.4 AOn-pulse duration50μsOff-pulse duration50μsTemperature of deionized water25°CFabrication pressure1 atmVolume of deionized water500 mLFabrication time60 s


## 2.3. Identification ofAg+ and Ag0

During the arc discharge, both ionic silver (Ag+) and metallic Ag nanoparticle (Ag0) can be generated. The following apparatuses are used to identify the metallic Ag nanoparticle and ionic Ag(i)
a conductivity meter (JENCO 6307) employed to measure number of ions in the solution and quickly perform qualitative analysis(ii)
a particle sizer (Malvern Instruments ZS-90) used to analyze the distribution of the metallic Ag nanoparticle in suspension: base on this analysis, the velocity and required time can be determined to achieve the optimal conditions for the centrifuge(iii)
a centrifuge (Hettich,  Mikro 22R) used to separate the SNPS into particles and ions: inside the centrifuge, particles are precipitated while ionic Ag  is dissolved in water(iv)
a titrator (METTLER TOLEDO-DL50) used to estimate the concentration of the ionic Ag in the solution(v)
an atomic absorption spectrophotometer (Shimadzu AA-680) used to measure the concentration of ionic Ag below the threshold of 6 ppm and check the accuracy of the estimation made with the above titratorThe conductivity meter was employed to measure the conductivity of the SNPS produced by using ADM and deionized water with a conductivity of 20.1μS/cm and 0.5 μS/cm, respectively. The conductivity of the SNPS was greater than that of deionized water. This indicates that the SNPS contains ions. However, this measure cannot distinguish the type of ions.In an attempt to explore the nature of ions, ions were then separated from the particles by using a centrifuge and evaluated by a qualitative and quantitative analysis. During the separation process, particles were precipitated while ions were not affected. A disadvantage of this method lies in that it could be impossible to complete the separation process in a short period of time if the particles in the suspension were too small (less than a few nanometers).To overcome the above problem, the diameter of the SNPS particles was measured first. Figure2 shows the sizes and size distribution of particles. In the diagram, it can be seen that Ag particles larger than 10 nanometers must be first separated in the centrifuge, in order to remove at least of 96% the metallic Ag nanoparticles.Figure 2
Size distribution of Ag nanoparticles.The centrifuge used to precipitate Ag nanoparticles was set up with some specific parameters as follows: the radius and rotating speed were 7.5 cm and 18,000 rpm, respectively. The relative centrifugal force (RCF) was then calculated by applying.(1)RCF=1.118×10-5×r×N2,
where RCF is the relative centrifugal force (cm/sec2), r is the rotational radius (cm), and N is the rotating speed (revolutions per minute, RPM).The minimum time so that the centrifuge can separate ions was 100 minutes,  which was evaluated by using  using Stokes’ Law:(2)Vs=2×rp2×(ρp-ρf)×RCF9η,
where Vs is the particles' settling velocity (cm/sec), rp is the Stokes radius of particles (cm), ρp is the density of particles (g/cm3), ρf is the density of deionized water (g/cm3), and η is the viscosity of deionized water (dynesec/cm2).Figure3 illustrates the identification process of ionic Ag. First, the ADM was used to fabricate SNPS from deionized water and an Ag rod. A centrifuge (18,000 rpm-100 minutes) was then used to extract the ionic Ag (being contained in the supernatant-Ag+) and the metallic Ag nanoparticles (being contained in the sediment-Ag0). The quantitative analysis of the ionic Ag could be directly carried out on the supernatant (Ag+). However, the quantitative analysis of the metallic Ag nanoparticle requires the addition of an appropriate amount of nitric acid (65%), so that the sediment (Ag0) can be fully dissolved. This mixture is then diluted with deionized water, so that it can be reset to the original volume.Figure 3
Identification process of ionic Ag.


## 2.4. Fabrication Au Nanoparticles

Au wires were used as the positive and negative electrodes and they would be etched in deionized water if the power supply system provides a stable pulse voltage. To ionize the aqua medium between electrodes and the DC arc discharge with a pulse voltage of around 70–100 V was first provided within 2-3μs. Following this, shown in Figure 4, a pulse voltage of around 20–40 V was employed within 10 μs while the etching current was maintained at 4A.Figure 4
Current and voltage pulses created by the DC arc discharge system during etching of the Au electrodes.The servo control system was based on a close-looped feedback to control the gap between two electrodes (within a few microns). The upper Au electrode was held by the servo control system while the bottom one was fixed by the Teflon ring. The temperature of deionized water in the tank was maintained at the room temperature.The surface layer of Au wires was evaporated and then condensed in water to create the Au suspension. The colloidal Au was then collected. The size distribution, zeta potential, and optical properties of Au particles could be determined through the inspection and analysis of the colloidal Au. A field emission scanning electron microscope (FE-SEM, HITACHI S4700) was applied to determine the size distribution of Au nanoparticles. The Energy Dispersive X-ray (EDX) spectrum was taken to demonstrate the chemical composition of prepared Au particles. A NanoZS90 system (Malvern) was used to measure the zeta potential of the aqueous suspension of the charged Au particles. The measurement of the zeta potential was mainly based on particle velocity in the unit electric field. The double-beam UV-VIS spectrophotometer (9423UVA1002E Helios Alpha) was used to analyze optical properties of Au nanoparticles.


## 3. Experimental Results and Discussions

The experimental results in the fabrication of Ag nanoparticles are shown in Table2. The difference between the conductivity of SNPS (20.1 mS/cm) and supernatant (Ag+) (19.0 mS/cm) is insignificant. This suggests that SNPS contains the ions which develop into Ag atoms in the centrifuge and slightly reduce the conductivity of supernatant (Ag+).Table 2
Experimental results obtained from fabricating Ag nanoparticles.
#SampleConductivityTitratorAA(μS/cm)(ppm)(ppm)1Deionized water0.5002Colloidal Ag20.119.926.43Supernatant (Ag+)19.018.619.24Sediment (Ag0) dissolved by HNO3n/a*11.211.4*Using HNO3 in order to void the conductivity measurement.Shown in Table2, using the titrator and AA, the concentration of the ionic Ag in SNPS was found at 19.9 and 26.4 ppm, respectively. These results prove that ions in SNPS are ionic Ag. The measurement result taken with AA is greater than the one by the titrator since AA is sensitive to both ionic Ag and metallic Ag nanoparticles, whereas the titrator is solely sensitive to ionic Ag.Because ionic Ag only dissolves in the supernatant, the titrator and AA could be also used to measure the concentration of Ag ions in SNPS. The concentration was identified to be 18.6 and 19.2 ppm by both of the instruments, respectively. There is a slight difference in these measurement results due to the fact that the supernatant (Ag+) contains less than 10 nanometers of the metallic Ag nanoparticles.Similarly, the titrator and AA were used to measure the concentration of the sediment (Ag0) which was fully dissolved in nitric acid, in which concentration was identified to be 11.2 and 11.4 ppm, respectively. These results suggest that the concentration of suspended metallic Ag nanoparticle in SNPS was approximately 11 ppm.In the fabrication process of SNPS, ionic Ag was produced as a by-product of the synthesis process of the metallic Ag nanoparticles. The spark discharge occurs as shown in Figure5. Four individual effects simultaneously interact in the discharge process as follows:(i)
a strong electric field(ii)
a high plasma temperature(iii)
active Ag atoms being imparted from the Ag rod(iv)
hydrogen and oxygen atoms being imparted from water moleculesFigure 5
Plasma and electrical discharge.The Ag-ion-like compound dissolved in deionized water was formed when the reaction between the active atoms developed. Furthermore, during the bombardment of spark discharge, due to the hydrogen bond, the atomic oxygen can adhere to the surface of charged Ag nanoparticles (marked by the dash line in Figure5). A steady colloid was formed due to the bond between water molecules and oxygen atoms on the surface of Ag nanoparticles.Figures6 and 7 illustrate the SEM images of Ag and Au nanoparticles, respectively. Several drops of Ag (or Au) colloid were deposited on a conductive silicon wafer, in which the sample was then gently heated on a heating plate. The SEM image of the secondary electrons was then taken.Figure 6
SEM image of prepared Ag nanoparticles.Figure 7
SEM image of prepared Au nanoparticles.Figures8 and 9 show the size distribution of Ag and Au nanoparticles which were calculated from the SEM image, respectively. The number of Ag particles with the size of  20nm ± 15nm is dominant, while the number of Au particles with the size of 25nm±15nm is principal.Figure 8
Size distribution of prepared Ag nanoparticles.Figure 9
Size distribution of prepared Au nanoparticles.The EDX spectrum shown in Figures10 and 11 was obtained from the same sample of Ag and Au colloid, respectively. The EDX spectrum of Ag nanoparticles demonstrates the distinct presence of Ag peaks at 2.984  (Ag-Lα1), 3.151 (Ag-Lβ1), 3.348 (Ag-Lβ2), 3.52 keV (Ag-Lg1) and 2.644 keV (Ag-L1), while the EDX spectrum of Au nanoparticles demonstrates the distinct presence of Au peaks at 1.87, 2.1213  (Au-Mα), 2.149  (Au-Kβ1) and 2.205 keV (Au-Mβ). Some differences exist between the EDX spectra of Ag and Au nanoparticles as a layer of Au was coated on the SEM sample before performing the SEM analysis followed by the EDX spectrum test. In addition, the Si peak at 1.7398 keV (Si-Kα) can be also found due to the presence of the silicon wafer which was used as a support for Ag and Au nanoparticles.Figure 10
EDX spectrum of Ag nanoparticles deposited.Figure 11
EDX spectrum of Au nanoparticles deposited.The maximum Zeta potential of the aqueous Ag and Au colloid was found reaching at approximately –45 mV and –35 mV, respectively. Figures12 and 13 demonstrate the negatively charged Ag and Au nanoparticles in water, respectively. The Ag (or Au) particles dispersed in water were negatively charged due to their ionic characteristics of Ag (or Au) micelles. The repulsive electrostatic forces existing between Ag (or Au) nanoparticles protect them against the agglomeration and sedimentation in water suspension.Figure 12
Zeta potential of the aqueous Ag colloid.Figure 13
Zeta potential of the aqueous Au colloid.The UV-VIS absorption spectra of Ag and Au nanoparticles suspension are shown in Figures14 and 15, respectively. A maximum absorbance in the region of approximately 396 nm (for Ag) and 525 nm (for Au), respectively, can be also found in other references [15–17] and [18, 19], respectively.Figure 14
UV-VIS absorption spectra of the aqueous Ag colloid.Figure 15
UV-VIS absorption spectra of the aqueous Au colloid.The process of water decomposition (electrolysis) can be also observed during the production of Ag or Au nanoparticles by arc discharge. Gaseous hydrogen and oxygen appeared in water with a form of small bubbles. They were then partly dissolved in water. After that, hydrogen and oxygen started interacting with Ag (or Au) nanoparticles which was newly prepared. Since hydrogen (with a form of molecular or atomic) cannot continue to be adsorbed on the Au surface at room temperature [20–22], it was ultimately removed from the water suspension and became the gas phase. Meanwhile, at room temperature, oxygen can be absorbed on the Au surface [23–25]. The negatively charged surface of Ag (or Au) nanoparticles which have been injected with electrons by the cathode during arc discharge was saturated by the atomic oxygen which can create hydrogen bonds with water particles in water environment.Consequently, the negatively charged Ag (or Au) nanoparticle micelles can be created in the water medium. The model of Ag and Au nanoparticle micelles is shown in Figures16 and 17, respectively. The water molecules can bond with Ag (or Au) nanoparticles due to hydrogen bonds which are represented by the dash lines. It is importantly noted that the negatively charged Ag (or Au) nanoparticles which are surrounded by water molecules can create a stable suspension without adding any stabilizers and surfactants.Figure 16
Model of Ag nanoparticle micelles.Figure 17
Model of Au nanoparticle micelles.Meanwhile, during the arc discharge, the water molecules can dissociate into hydrogen, oxygen, and free radical hydroxides (OH), during which the oxygen atoms are absorbed by the nano-Au surface. Therefore, this leads to the formation of hydrogen bond with the neighboring water molecules and supports, Au nanoparticles to be suspended in water, preventing agglomeration and sedimentation of the Au particles. Since Au is a noble metal, oxygen does not chemically react with Au. However, the bonding strength of oxygen adsorption on the prepared Au is only slightly lower than that of the energy of covalent bonding. In contrast to Au, the nature of Ag is different from Au as Ag is of a subnoble metal. Although Ag is not easily oxidized, in the presence of a strong electric field, the dissolvedH2CO3 (Dihydrogen Carbonate) in water can react with Ag and lead to the formation of Ag2CO3 (Ag Carbonate), which is a partially soluble compound. During the process, the dissociated CO3 near the Ag surface can lead to the dissolution of micro-nano Ag in the water solution.When the concentration of Ag+ ions is over 10 ppm as shown in Figure18, the absorption peak of the AgNPs can maintain its value indefinitely without change. This suggests that the concentration of Ag2CO3  is thus demonstrated to be linked to the suspensivity of AgNPs. When the concentration of Ag+ ions is higher than the threshold value,  AgNPs can maintain a steady level of suspensivity.Figure 18
Tracking the absorption peak of CS samples with varying Ag+ ion concentrations.One of the most promising applications of AgNPs is its bacteriacidal effect against Staphylococcus aureus.The results from the antimicrobial susceptibility tests suggest that a linear relationship exists between the concentration of silver ions and the diameter of the hollow region which depends on the attacking potency of the anibiotic. That is, the antibacterial potency of a solution is directly related to its level of silver ion concentration, as shown in Figure19, and not to the AgNps which was assumed prior to the research. Extrapolating from this linear relationship, we can predict that the critical concentration of silver ions for producing an inhibitory effect is 18.5 ppm.Figure 19
Concentration of silver ions and inhibitory effect.


## 4. Conclusions

(1)
The DC arc discharge method has been successfully developed for the production of Ag and Au nanoparticles.(2)
Ag and Au nanoparticles in water are characterized as a stable colloid without adding any stabilizers, as the concentration ofAg+ ions is over 10 ppm, AgNPs can maintain its value indefinitely without change.(3)
The experimental result indicates that the prepared Au nanoparticles with their surfaces bonded by oxygen atoms are supported by the formation of hydrogen bond with the neighboring water molecules. This well explains that Au nanoparticles can suspend in water without agglomeration. The bonding strength of oxygen adsorption on the prepared Au is only slightly lower than that of the energy of covalent bonding.(4)
The prepared Ag nanoparticles react with the dissolvedH2CO3 in water, leading to the formation of Ag2CO3 (Ag Carbonate). The dissociated CO3 near the Ag surface can lead to the dissolution of Ag nanoparticles in the water solution.



---