# Synthesis and Characterization of All Renewable Resources Based Branched Polyester:Poly(2,5-furandicarboxylic acid-co-glycerol)

Authors: Ananda S. Amarasekara; Ashfaqur Razzaq; Paul Bonham
Journal: ISRN Polymer Science
 (2013)

---

## Abstract

Condensation of all renewable resources based monomers 2,5-furandicarboxylic acid and glycerol in the presence of 2 mol% Sb2O3 catalyst at 210°C gives a branched polyester resin in 70% yield.  This resin was characterized by elemental analysis, 1H, 13C NMR, FT-IR, and TGA-DTG.


---

## Body

## 1. Introduction

The growing concern about declining fossil fuel reserves has stimulated recent interests in explorations for renewable resources based fuels as well as platform chemicals for the chemical and polymer industries. Furan compounds derived from renewable carbohydrates are a major class in this new generation of platform chemicals, and 2,5-furandicarboxylic acid (FDCA,1) (Figure 1) is a particularly interesting compound in this group [1–3]. 2,5-Furandicarboxylic acid is the symmetrical diacid resulting from the oxidations of both primary alcohol and aldehyde groups of 5-hydroxymethylfurfural (HMF) [4] to carboxylic acid groups. This is probably the most important derivative of HMF; this symmetrical aromatic diacid has been looked as a potential replacement and the renewable resources based equivalent of terephthalic acid [5], which is a monomer in polyethylene terephthalate (PET) plastics. Furthermore, FDCA is listed in a 2004 US Department of Energy National Renewable Energy Laboratory (NREL) report [6] as one of the twelve building blocks that can be subsequently converted to a number of high-value bio-based chemicals or materials. There are a number of recent reports on the use of FDCA for the preparation of linear polyesters [1, 7] using a variety of polyesterification techniques. The widely used methods involve the use of 2,5-furandicarboxylic acid dichloride, trans-esterification, and interfacial polycondensation [7, 8]. The most commonly studied diol is the ethylene diol [5, 7, 8], but linear polyesters have been prepared by using a number of other diols like 1,3-propane diol [7], 1,4-butane diol [9], 1,6-hexane diol [9], 1,8-octane diol [9], D-isosorbide [10], D-isoidide [10], bis(2,5-hydroxymethyl)-furan [7], bis-(1,4-hydroxymethyl) benzene [7], and hydroquinone [7] as well. The polyester prepared using ethylene diol is probably the most appealing, and Gandini et al. have shown that this renewable resources based equivalent of PET has many properties comparable with PET [5].Figure 1
Synthesis ofpoly(2,5-furandicarboxylic acid-co-glycerol) (3).2,5-Furandicarboxylic acid (1) can be prepared by oxidation of 5-hydroxymethylfurfural (HMF) with some common stoichiometric oxidation reagents [1, 4]. Then, there are a number of reports [1] on catalytic oxidation methods for the conversion of HMF to FDCA, using noble metal catalysts. Excellent yields are reported in the use of Pt-Pb/C catalyst in alkaline aqueous medium, using molecular oxygen as the primary oxidant [11]. Another approach to FDCA is the direct dehydration of mucic acid, under strongly acidic conditions using sulfuric [12] or p-toluenesulfonic acid [13] as the acid catalyst. In our experiments we have prepared FDCA by simple dehydration of mucic acid using 48% aqueous HBr as the catalyst and the solvent.Glycerol (GL,2) (Figure 1) is another renewable resource based platform chemical formed in the saponification of triglycerides in vegetable oils and a byproduct of soap making and biodiesel production. Present interest in the biomass-derived feed stock chemicals has initiated an array of research efforts in converting glycerol to monomers such as propylene glycol, acrolein, and epichlorohydrin that can be used with the existing polymerization technologies. Additionally, there are a number of new reports on the development of novel polymeric materials using glycerol directly as one of the monomers [14–17]. For example, glycerol has been used as a monomer in the polymerizations with adipic and oleic diacid using immobilized Candida antarctica Lipase B (Novozym 435) as a biocatalyst [17]. In another example, Luman et al. reported [18] the preparation of dendritic polymers composed of glycerol and succinic acid for new medical applications. In addition, we have recently shown [19] that glycerol can be directly condensed with another renewable resources based material, levulinic acid, to prepare an oligo-ketal-ester, oligo (levulinic acid-co-glycerol) [19].Our interests [19, 20] in this field of preparation and characterization of novel polymeric materials from renewable feed stocks led us to study the condensation of FDCA with polyols to make branched furanic polyesters. In this communication, we report the first synthesis and characterization of a branched furanic polyester resin by solvent free condensation of FDCA with glycerol.


## 2. Experimental

### 2.1. Materials and Physical Measurements

Mucic acid, glycerol, antimony (III) oxide (>99%), and 48% HBr were purchased from Aldrich Chemical Co.1H NMR spectra were recorded in DMSO-d6 or CF3COOD on a Varian Mercury plus spectrometer operating at 400 MHz, and chemical shifts are given in ppm downfield from TMS (δ = 0.00). 13C NMR spectra in DMSO-d6 or CF3COOD were recorded on the same spectrometer operating at 100 MHz; chemical shifts were measured relative to DMSO-d6 and converted to δ(TMS) using δ(DMSO) = 39.51 and δ(CF3-) = 116.60 ppm. FT-IR spectra were recorded on a Thermo Nicolet IR 200 spectrometer using KBr pellets. Thermogravimetric analysis was carried out in air on a Perkin Elmer Diamond TG/DTG system at a heating rate 10°C/min. Elemental analysis was performed at QTI laboratories, NJ, USA.


### 2.2. Synthesis of 2,5-Furandicarboxylic Acid (FDCA) (1)

A suspension of mucic acid (5.0 g, 24 mmol) in 35 mL of 48% aq. HBr was refluxed for 18 h. Then the reaction mixture was distilled to remove ~25 mL of aq. HBr. The resulting dark suspension was cooled in an ice bath and basified by careful addition of 4 M aq. sodium hydroxide solution. This basic solution was filtered using a Buchner funnel to remove charred byproducts, and the filtrate was acidified topH=1 by addition of conc. HCl and kept in a refrigerator overnight for crystallization. The solid product formed was collected by suction filtration and dried in air to give pure 2,5-furandicarboxylic acid (FDCA) (1) as white crystals (1.80 g, 48% yield), m.pt. > 300°C. 1H NMR of the product indicated that sample is >99.5% pure.1H NMR (DMSO-d6) δ 3.20–3.90 (b, 2H), 7.27 (s, 2H). 13C NMR (DMSO-d6) δ 118.9, 147.5, 159.4.


### 2.3. Synthesis ofPoly(2,5-furandicarboxylic acid-co-glycerol) (3)

A mixture of 2,5-furandicarboxylic acid (407 mg, 2.61 mmol) and glycerol (160 mg,  1.74 mmol) was dissolved in 1.0 mL ofN,N-dimethyl formamide in a small round bottom flask, then Sb2O3 (15.2 mg, 0.068 mmol, 2 mol%) was added to this solution. The resulting mixture was gradually heated from room temperature (23°C) to 150°C under a nitrogen atmosphere during a period of 1.0 h and held at 150°C for 30 min then the reaction flask was connected to a vacuum (5 mmHg) and heated to 210°C, in 30 min. and held at 210°C for 2 h under vacuum. Flask was cooled, and the solid product was washed with hot methanol in a soxhlet extractor for 16 h then dried under vacuum to yield poly(2,5-furandicarboxylic acid-co-glycerol) as a white sold. The experiment was carried out in triplicate; average product weight: 331 mg, 70% yield.Anal. Calc. for C24H16O15: C, 52.95; H, 2.96. Found: C, 53.31; H, 2.73.1H, 13C NMR, and FT-IR are shown in Figures 2(a), 2(b), and 3, respectively.1H (a) and 13C (b) NMR spectra of poly(2,5-furandicarboxylic acid-co-glycerol) (3) in CF3COOD,  *solvent.
(a)
(b)Figure 3
FT-IR spectrum ofpoly(2,5-furandicarboxylic acid-co-glycerol) (3).Thermal analysis recorded in the 20–800°C temperature range in air using a Pt crucible showed a two step thermogravimetric (TG) analysis curve with 78 and 22% weight losses (Figure4). These weight losses correspond to two peaks at 355 and 590°C in the derivative TG analysis (DTG) plot.Figure 4
TG-DTG Curves ofpoly(2,5-furandicarboxylic acid-co-glycerol) (3).


## 2.1. Materials and Physical Measurements

Mucic acid, glycerol, antimony (III) oxide (>99%), and 48% HBr were purchased from Aldrich Chemical Co.1H NMR spectra were recorded in DMSO-d6 or CF3COOD on a Varian Mercury plus spectrometer operating at 400 MHz, and chemical shifts are given in ppm downfield from TMS (δ = 0.00). 13C NMR spectra in DMSO-d6 or CF3COOD were recorded on the same spectrometer operating at 100 MHz; chemical shifts were measured relative to DMSO-d6 and converted to δ(TMS) using δ(DMSO) = 39.51 and δ(CF3-) = 116.60 ppm. FT-IR spectra were recorded on a Thermo Nicolet IR 200 spectrometer using KBr pellets. Thermogravimetric analysis was carried out in air on a Perkin Elmer Diamond TG/DTG system at a heating rate 10°C/min. Elemental analysis was performed at QTI laboratories, NJ, USA.


## 2.2. Synthesis of 2,5-Furandicarboxylic Acid (FDCA) (1)

A suspension of mucic acid (5.0 g, 24 mmol) in 35 mL of 48% aq. HBr was refluxed for 18 h. Then the reaction mixture was distilled to remove ~25 mL of aq. HBr. The resulting dark suspension was cooled in an ice bath and basified by careful addition of 4 M aq. sodium hydroxide solution. This basic solution was filtered using a Buchner funnel to remove charred byproducts, and the filtrate was acidified topH=1 by addition of conc. HCl and kept in a refrigerator overnight for crystallization. The solid product formed was collected by suction filtration and dried in air to give pure 2,5-furandicarboxylic acid (FDCA) (1) as white crystals (1.80 g, 48% yield), m.pt. > 300°C. 1H NMR of the product indicated that sample is >99.5% pure.1H NMR (DMSO-d6) δ 3.20–3.90 (b, 2H), 7.27 (s, 2H). 13C NMR (DMSO-d6) δ 118.9, 147.5, 159.4.


## 2.3. Synthesis ofPoly(2,5-furandicarboxylic acid-co-glycerol) (3)

A mixture of 2,5-furandicarboxylic acid (407 mg, 2.61 mmol) and glycerol (160 mg,  1.74 mmol) was dissolved in 1.0 mL ofN,N-dimethyl formamide in a small round bottom flask, then Sb2O3 (15.2 mg, 0.068 mmol, 2 mol%) was added to this solution. The resulting mixture was gradually heated from room temperature (23°C) to 150°C under a nitrogen atmosphere during a period of 1.0 h and held at 150°C for 30 min then the reaction flask was connected to a vacuum (5 mmHg) and heated to 210°C, in 30 min. and held at 210°C for 2 h under vacuum. Flask was cooled, and the solid product was washed with hot methanol in a soxhlet extractor for 16 h then dried under vacuum to yield poly(2,5-furandicarboxylic acid-co-glycerol) as a white sold. The experiment was carried out in triplicate; average product weight: 331 mg, 70% yield.Anal. Calc. for C24H16O15: C, 52.95; H, 2.96. Found: C, 53.31; H, 2.73.1H, 13C NMR, and FT-IR are shown in Figures 2(a), 2(b), and 3, respectively.1H (a) and 13C (b) NMR spectra of poly(2,5-furandicarboxylic acid-co-glycerol) (3) in CF3COOD,  *solvent.
(a)
(b)Figure 3
FT-IR spectrum ofpoly(2,5-furandicarboxylic acid-co-glycerol) (3).Thermal analysis recorded in the 20–800°C temperature range in air using a Pt crucible showed a two step thermogravimetric (TG) analysis curve with 78 and 22% weight losses (Figure4). These weight losses correspond to two peaks at 355 and 590°C in the derivative TG analysis (DTG) plot.Figure 4
TG-DTG Curves ofpoly(2,5-furandicarboxylic acid-co-glycerol) (3).


## 3. Results and Discussion

### 3.1. Synthesis and Characterization of 2,5-Furandicarboxylic Acid (FDCA) (1)

2,5-Furandicarboxylic acid used for the polymer synthesis was prepared by dehydration of mucic acid by refluxing in 48% HBr for 18 h. We have observed that shorter reaction periods give lower yields, whereas reaction periods longer than 18 h produce excessive charring of the reaction mixture. Furthermore, we have found that it is essential to convert the product to its disodium salt form before the removal of the charred byproducts by filtration. This method provides a simple direct route to FDCA, when compared to the conventional methods [1, 4] of oxidation of 5-hydroxymethylfurfural. The 1H and 13C NMR spectra of the product are in agreement with the reported data [13] for FDCA.


### 3.2. Synthesis and Characterization ofPoly(2,5-furandicarboxylic acid-co-glycerol) (3)

Poly(2,5-furandicarboxylic acid-co-glycerol) (3) was prepared using FDCA : GL 3 : 2 molar ratio as shown in Figure 1. The polymer resin 3 is insoluble in water and all the common organic solvents, including DMF, DMSO, and only slightly soluble in trifluoroacetic acid. These solubility properties are similar to the FDCA-ethylene glycol linear polyester reported in the literature [5].Proton NMR of the polymer resin3, recorded in CF3COOD, is shown in Figure 2(a). This spectrum showed a complex multiplet in the 4.40–5.22 ppm region for the glycerol unit hydrogens and a broad singlet at 7.92 ppm for C-3,4 furan ring hydrogens. 13C NMR (Figure 2(b)) spectrum was recorded in CF3COOD using a 5 s relaxation delay, and this spectrum showed glycerol unit carbons at 68.0 and 75.8 ppm. The 13C peak at 121.2 ppm was assigned to C-3,4 carbons, whereas 146.9 ppm was assigned to C-2,5 carbons of the furan ring. These values are comparable to the corresponding 13C resonances reported [5] for poly(ethylene 2,5-furandicarboxylate) at 121.1 and 147.1 ppm.  The two resonances at 159.2 and 160.7 ppm were assigned to two types of ester carbonyls in the polymer, resulting from esterification at primary and secondary –OH groups of glycerol. Furthermore, these ester carbonyl peaks are comparable to single ester carbonyl resonance reported at 161.0 ppm for poly(ethylene 2,5-furandicarboxylate) [5].FT-IR spectrum of the polymer resin3 recorded in KBr disk (Figure 3) showed characteristic ester bands at 1730 cm−1 for C=O, 1290 cm−1 for C–O–C, and similar absorptions are known for furanic polyesters reported in the literature [7]. Additionally the sharp IR absorption at 768 cm−1 can be assigned to the furan ring, further supporting the proposed structure 3 in Figure 1. Thermogravimetric-derivative thermogravimetric (TG-DTG) analysis curves of the polymer resin 3 showed that new material is stable up to about 275°C in air. Furthermore, polymer was found to degrade in two steps of 78 and 22% weight losses corresponding to peaks at 355 and 590°C in the DTG curve as shown in Figure 4.


## 3.1. Synthesis and Characterization of 2,5-Furandicarboxylic Acid (FDCA) (1)

2,5-Furandicarboxylic acid used for the polymer synthesis was prepared by dehydration of mucic acid by refluxing in 48% HBr for 18 h. We have observed that shorter reaction periods give lower yields, whereas reaction periods longer than 18 h produce excessive charring of the reaction mixture. Furthermore, we have found that it is essential to convert the product to its disodium salt form before the removal of the charred byproducts by filtration. This method provides a simple direct route to FDCA, when compared to the conventional methods [1, 4] of oxidation of 5-hydroxymethylfurfural. The 1H and 13C NMR spectra of the product are in agreement with the reported data [13] for FDCA.


## 3.2. Synthesis and Characterization ofPoly(2,5-furandicarboxylic acid-co-glycerol) (3)

Poly(2,5-furandicarboxylic acid-co-glycerol) (3) was prepared using FDCA : GL 3 : 2 molar ratio as shown in Figure 1. The polymer resin 3 is insoluble in water and all the common organic solvents, including DMF, DMSO, and only slightly soluble in trifluoroacetic acid. These solubility properties are similar to the FDCA-ethylene glycol linear polyester reported in the literature [5].Proton NMR of the polymer resin3, recorded in CF3COOD, is shown in Figure 2(a). This spectrum showed a complex multiplet in the 4.40–5.22 ppm region for the glycerol unit hydrogens and a broad singlet at 7.92 ppm for C-3,4 furan ring hydrogens. 13C NMR (Figure 2(b)) spectrum was recorded in CF3COOD using a 5 s relaxation delay, and this spectrum showed glycerol unit carbons at 68.0 and 75.8 ppm. The 13C peak at 121.2 ppm was assigned to C-3,4 carbons, whereas 146.9 ppm was assigned to C-2,5 carbons of the furan ring. These values are comparable to the corresponding 13C resonances reported [5] for poly(ethylene 2,5-furandicarboxylate) at 121.1 and 147.1 ppm.  The two resonances at 159.2 and 160.7 ppm were assigned to two types of ester carbonyls in the polymer, resulting from esterification at primary and secondary –OH groups of glycerol. Furthermore, these ester carbonyl peaks are comparable to single ester carbonyl resonance reported at 161.0 ppm for poly(ethylene 2,5-furandicarboxylate) [5].FT-IR spectrum of the polymer resin3 recorded in KBr disk (Figure 3) showed characteristic ester bands at 1730 cm−1 for C=O, 1290 cm−1 for C–O–C, and similar absorptions are known for furanic polyesters reported in the literature [7]. Additionally the sharp IR absorption at 768 cm−1 can be assigned to the furan ring, further supporting the proposed structure 3 in Figure 1. Thermogravimetric-derivative thermogravimetric (TG-DTG) analysis curves of the polymer resin 3 showed that new material is stable up to about 275°C in air. Furthermore, polymer was found to degrade in two steps of 78 and 22% weight losses corresponding to peaks at 355 and 590°C in the DTG curve as shown in Figure 4.


## 4. Conclusion

We have shown that condensation of all renewable resources based monomers 2,5-furandicarboxylic acid and glycerol in the presence of 2 mol% Sb2O3 catalyst at 210°C gives a branched polyester resin in 70% yield. This hard resin is insoluble in all common organic solvents and only slightly soluble in trifluoroacetic acid. 2,5-Furandicarboxylic acid monomer used in the polymer synthesis can be prepared in 48% yield in a single step by dehydration of mucic acid with 48% HBr.



---

*Source: 645169-2013-07-21.xml*