# Electrochemical Behavior of TiO2  Nanoparticle Doped WO3 Thin Films

Authors: Suvarna R. Bathe; P. S. Patil
Journal: Journal of Materials
 (2014)

---

## Abstract

Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO) and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101) plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.


---

## Body

## 1. Introduction

The electrochromism is key to green technology as it controls the energy of solar flux entering in building, utilizes solar energy, and increases comfort in buildings. Electrochromic materials are able to sustain reversible and persistent changes of their optical properties under the action of a voltage. The electrochromic phenomenon was discovered in tungsten oxide [1] and this material remains the most promising candidate for large-scale uses of electrochromic devices. Their potential applications include several technological areas, such as smart windows, self-dimming rear mirror, electrochromic display, and antiglare rear view mirrors of automobiles [2]. Among a variety of the transition metal oxides, tungsten oxide (WO3-x) is found to be the most efficient candidate for electrochromic applications. Granqvist [3] explains the theoretical explanation of electrochromic mechanism and reviews about different nanostructured oxides for electrochromic device and describes the mass fabrication by electrochromic foil technology. The electrochromic performance of tungsten oxide, reversible coloration under double injection of ions and electrons, strongly depends on its nature and microstructure. Nanoscale microstructure could improve the electrochromic performances of tungsten oxide thin film because it is easy for ion to intercalate and deintercalate in thin film. Mesoporous tungsten oxides exhibit superior high-rate ion-insertion performance for their short-diffusion length of lithium and hydrogen ions into electrochromic films [4]. Several researchers have attempted to employ the concept of nanotechnology to improve the drawbacks of thin-film-based electrochromic devices (ECDs) such as contrast, cycling life stability, and slow switching time between the colored and bleached states. The researcher developed transition metal oxide nanowires based ECDs that show a great improvement in coloration efficiency, contrast, and durability [5, 6]. These ECDs show promising switching rate, life stability, and contrast. Grätzel [7] used TiO2 nanoparticles and absorbed organic monomers to improve the switching speed. The coloration and bleaching rates of WO3 film increase with the addition of the porous conducting metallic cover layer in a liquid electrolyte cell [8]. Park [9] has studied electrochromic properties of cosputtered Au-WO3 nanocomposite thin films containing high gold concentration (60 mol% Au) and obtained a shorter response time relative to the pure WO3 thin film. The doping of Au nanocrystals in WO3 thin films shows fast coloration time which was ten times shorter as compared with the coloration time of the pure WO3 thin film [10]. Some literature is available on WO3 films doped with Co, Cr, and Ni for electrochromic properties for ECD [11, 12]. He et al. [13] showed that the addition of gold over layer on WO3 thin film formed by physical vapor deposition resulted in a better change of optical density in electrochromic process. Previously our lab studied [14, 15] gold nanoparticles, multiwalled carbon nanotube doped in the WO3 thin films by pulsed spray for improving EC properties. The small doping of Ni (0.3 at %) in WO3 thin films improves electrochromic property, but EC property vanishes due to the limited ion diffusivity for higher concentration [16]. The effects of molybdenum (Mo) doping on the electrochromic behavior of spray pyrolyzed tungsten trioxide [WO3] thin films have been studied [17]. Our earlier work of Ti and Nb doping in WO3 thin films by pulsed spray pyrolysis shows with improved EC properties, but coloration efficiency decreases [18, 19]. Very little literature is available on TiO2 nanoparticle WO3 thin films. The main goal is to increase coloration efficiency by TiO2 nanoparticle doping in WO3 matrix.


## 2. Experimental Details

The undoped and TiO2 nanoparticle doped WO3 thin films were grown on fluorine doped tin oxide (SnO2 : F, FTO) coated glass and microscopic glass substrates using pulsed spray pyrolysis deposition technique. The precursor solution used for deposition of the films was prepared by dissolving pure WO3 powder in ammonia and distilled water and then heated to 90°C (prior to spray) at which the formation of ammonium tungstate ((NH4)2WO4) is completed. Commercial TiO2 nanoparticle (average particle size ~25 nm) 4 mg is dissolved in 5 mL trioctylphosphine oxide (TOPO) and stirred for 15 minutes; then, ammonium tungstate was added slowly to this solution. Details of the films synthesis are described elsewhere [20]. In brief, the substrate was held at 250°C, while an airflow rate of 15 L/min was maintained during deposition. The solution spraying on and off time interval was kept 5 s (50% duty cycle) for both cases. The thickness of all deposited films was about 200 nm. After deposition, the films were annealed in air at 325°C for 0.5 h.The structural properties were studied using an X-ray diffractometer (XRD) with Cu Kα radiation of wavelength 1.542 Å. X-ray diffraction data were used to identify the phases present in the films and to find out changes in the lattice parameters, if any. The surface morphology of the films was studied using scanning electron microscopy. The optical measurements were carried out at room temperature using a UV-VIS-NIR spectrophotometer. The transmittance of the films was measured in a wavelength range 200–3000 nm. The electrochemical injection or extraction of electrons and H+ ions was carried out using a solution of 0.001 M of H2SO4 electrolyte solution with platinum as a counter electrode and saturated calomel as a reference electrode (SCE). It was confirmed that our data for the undoped films compare very well with the best results reported by other groups [3, 8, 10–12, 21]. This ensures the quality of our films processing conditions and procedures.


## 3. Results and Discussion

The X-ray diffraction patterns of the undoped and TiO2 nanoparticle doped WO3 thin films deposited on glass substrate are shown in Figure 1. The XRD pattern for undoped WO3 films shows no distinct diffraction peaks, indicating the amorphous nature. The boards hump at diffraction angle ~20–30 degrees is originating from glass substrate. In case of TiO2 nanoparticle doped WO3 films, one peak at d=3.346 Å is observed, which indexed as (101) of anatase phase of TiO2 in accordance with JCPDS-ICDD card number 75-1537.Figure 1
XRD of undoped and TiO2 nanoparticle doped WO3 thin films.The morphology for the undoped and TiO2 nanoparticle doped WO3 films was examined using SEM. Figure 2(a) shows SEM image for undoped WO3 film deposited at 250°C and annealed at 325°C on glass substrate. It clearly shows microfibrous reticulated surface morphology throughout the film. The film appears to be of a multilayered fibrous nature, with mean fiber diameters of about 600 nm. This morphology is helpful for ion intercalation and deintercalation of the film. Figure 2(b) shows the SEM image of TiO2 nanoparticle doped WO3 thin films. TiO2 nanoparticle doping ruptures WO3 fibrous reticulate network and TiO2 nanoparticles were segregated in the surface of the film to form large clusters with particle size ~40 nm.SEM images for (a) undoped and (b) TiO2 nanoparticle doped WO3 thin films.
(a)
(b)Cyclic voltammograms (CV) were recorded for all the undoped and TiO2 nanoparticle doped films with linear potential sweep between −500 and +500 mV at a scan rate of 50 mV/s and shown in Figure 3. The arrow indicates the scan direction. When a negative potential was applied, a blue color was observed, indicating the oxide reduction followed by H+ ions intercalation. After the reversal of the potential, the anodic current started to flow, corresponding to the deintercalation process. There is a well-defined anodic peak for the film, indicating that the H+ insertion-removal process is highly reversible with little hysteresis. The area of the hysteresis curves and the height and position of anodic and cathodic peaks are closely related to the electrochemical processes occurring in the WO3. The decrease in the area of voltammograms and shift of threshold voltage (EΓ) towards positive potential (from −48 to +63 mV) is observed in case of TiO2 nanoparticle doped WO3 films as compared to undoped WO3 films. This can be attributed to decrease in ion mobility of the TiO2 nanoparticle doped WO3 thin films.Figure 3
Cyclic voltammograms (CV) for undoped and TiO2 nanoparticle doped WO3 thin films.The diffusion coefficient (D) of H+ ions during intercalation and deintercalation is calculated by using Randles-Sevcik equation [22]:
(1)D1/2=jp2.72×105×n3/2×A×C0ν1/2,
where jp is the peak current density (anodic peak current density (jpa) and cathodic peak current density (jpc)), n is number of electron, C0 is the concentration of active ions in the solution, ν is the scan rate, andA is the film area. By substituting all the values, the diffusion coefficient at 50 mV/s scan rate is calculated for intercalation and deintercalation processes for the undoped and TiO2 nanoparticle doped films. The diffusion coefficient is 1.86 × 10−9 and 1.38 × 10-11cm2/s for the undoped and TiO2 nanoparticle doped films, respectively. This indicates that the charge insertion of TiO2 nanoparticle doped WO3 films is less than undoped thin film.The amount of H+ ions intercalation and deintercalation with respect to time was carried by using chronocoulometry (CC) studies, which can further be used to estimate reversibility and coloration efficiency. Figure 4 shows charges intercalated/deintercalated versus time transients for the films at ±0.5V for the step of 20 seconds. In the forward scan, the charges are intercalated into the film by diffusion resulting process in coloration due to reduction of W+6 to W+5 states. In the reverse scan, the intercalated charge is removed from the film, resulting in bleaching due to oxidation of W+5 to W+6 states. The reversibility of the films is calculated by the ratio of charge deintercalated (Qdi) from the film into electrolyte to the charge intercalated (Qi) into the film from the electrolyte. The electrochromic reversibility was found to be ~75% for undoped WO3 and 95% for TiO2 nanoparticle doped WO3 films. The electrochromic properties calculated from CV and CC were listed in Table 1.Table 1
The electrochromic properties of undoped and TiO2 nanoparticle doped WO3 films.
Sample ID
Q
i (mC/cm2)
Q
di (mC/cm2)
(ΔOD) (%)
Reversibility (%)
CE (cm2/C) at 630 nm
Diffusion coefficient (cm2/s)
Undoped WO3
9.71
7.12
0.14
75
30
1.86
×
10
-
9
TiO2 nanoparticle doped WO3
10.60
9.98
0.02
95
2
1.38
×
10
-
11Figure 4
Chronocoulometry (CC) for undoped and TiO2 nanoparticle doped WO3 thin films, recorded at potential step ±0.5 V for 20 s.The dependence of optical transmittance on wavelength in the 200–3000 nm for the undoped and TiO2 nanoparticle doped WO3 films in bleached and colored condition for 10 sec is shown in Figure 5. The maximum transmittance observed was ~80% at 860 nm and ~75% at 910 nm for undoped and TiO2 nanoparticle doped WO3 films in bleached state, respectively. All the colored films show similar trend as in bleached films; the only difference is that the maximum transmittance value decreases as compared to the respective bleached films. The undoped and TiO2 nanoparticle doped WO3 films exhibit above ~50% optical transmission in the ~400–1300 nm range and drop abruptly beyond ~1600 nm. The drop in transmission in near infrared (NIR) region can be attributed to an increased reflectance of the films in NIR region [21, 23]. The coloration efficiency (η) at a particular wavelength correlates with the optical contrast, that is, the change in optical density (ΔOD) with charges intercalated per unit electrode area (Qi), and can be expressed as
(2)η=ΔODλQi=log⁡(Tb/Tc)Qi,
where Tb and Tc are the transmittances of the film in the bleached and colored states, respectively. The coloration efficiency decreases in the case of TiO2 nanoparticle doped WO3 films, as expected, indicating that Ti does not take part in the electrochromism mechanism. The values of coloration efficiency at 630 nm for 10 sec are calculated using the above equation for the undoped and TiO2 nanoparticle doped WO3 films and listed in Table 1.Figure 5
Optical transmittance for the bleached (up curve) and the colored (down curve) for undoped (solid line) and TiO2 nanoparticle doped (dotted line) WO3 films.


## 4. Conclusion

In conclusion, TiO2 nanoparticles doping effects on electrochromic WO3 films synthesized using pulsed spray pyrolysis deposition technique have been investigated. The fibrous reticulated morphology is converted into granular structure at TiO2 nanoparticle doping. The TiO2 particulates were segregated on the surface of the film, for doped film. It is seen that TiO2 nanoparticles doping can lead to significant surface morphology changes, which plays an important role in electrochromic properties of WO3 thin films. It was found that the coloration efficiency decreased in case of TiO2 nanoparticles doped films. This indicates that the charge inserted into TiO2 nanoparticle doped WO3 thin film is not sufficient for reducing tungsten species and also observed diffusion coefficient for this film is about ten times less than undoped WO3 films.



---