# In Vitro Evaluation of a Biomedical-Grade Bilayer Chitosan Porous Skin Regenerating Template as a Potential Dermal Scaffold in Skin Tissue Engineering

Authors: Chin Keong Lim; Ahmad Sukari Halim; Ismail Zainol; Kartini Noorsal
Journal: International Journal of Polymer Science
 (2011)

---

## Abstract

Chitosan is a copolymer ofN-acetylglucosamine and glucosamine. A bilayer chitosan porous skin regenerating template (CPSRT) has been developed for skin tissue engineering. The pore size of the CPSRT was assessed using a scanning electron microscopy (SEM). The in vitro cytocompatibility of the CPSRT was tested on primary human epidermal keratinocyte (pHEK) cultures by measuring lactate dehydrogenase (LDH) levels and skin irritation by western blot analysis of the interleukin-8 (IL-8) and tumor necrosis factor-α (TNF-α) secretions. The ability of the CPSRT to support cell ingrowth was evaluated by seeding primary human dermal fibroblasts (pHDFs) on the scaffold, staining the cells with live/dead stain, and imaging the construct by confocal microscopy (CLSM). The CPSRT with pore sizes ranging from 50 to 150 μm was cytocompatible because it did not provoke the additional production of IL-8 and TNF-α by pHEK cultures. Cultured pHDFs were able to penetrate the CPSRT and had increased in number on day 14. In conclusion, the CPSRT serves as an ideal template for skin tissue engineering.


---

## Body

## 1. Introduction

Biopolymers are naturally synthesized compounds that are produced by living organisms. These materials participate in the natural biological cycle and are eventually degraded and reabsorbed by their environment. Chitin, a biopolymer, can be obtained at relatively low cost from the shells of shellfish (mainly crabs, shrimps, and lobsters), which are a waste product of the seafood processing industry [1]. Chitin and derivatives such as chitosan have a natural basicity that provides properties such as biocompatibility, biodegradability, antibacterial activity, heavy metal ion chelation ability, gel-forming properties, hydrophilicity, and remarkable protein affinity [2].Chitosan is the primary biopolymer derivative ofN-deacetylated chitin and consists of N-acetylglucosamine and glucosamine. Chitosan possesses an abundance of amino and hydroxyl groups that allow it to be chemically modified by processes such as acylation, N-phthaloylation, alkylation, Schiff base formation, reductive alkylation, tosylation, O-carboxymethylation, N-carboxyalkylation, and graft copolymerization [3, 4]. These modifications allow chitosan’s properties to be tailored to a specific application.Tissue regeneration is a complex biological process that involves inward migration and proliferation of cells into a defect area or scaffold, as well as the secretion of an extracellular matrix to support new tissue formation. Biocompatible tissue engineering constructs can provide cues for cell migration and differentiation to promote wound-healing, tissue formation, and vascular network regrowth. Tissue engineering uses polymer scaffolds to promote cell adhesion, proliferation, and differentiationin vitro. Although chitosan has been used in various types of biocompatible wound dressings, such as films, pastes, sheets, and porous templates    [5–8], it also has intrinsic wound-healing abilities [9]. A novel biomedical-grade bilayer chitosan porous skin regenerating template (CPSRT) was developed for use as a dermal scaffold for skin tissue engineering to take advantage of these wound-healing abilities as well as the biocompatible nature of chitosan. The pore size of the CPSRT was assessed using SEM analysis. However, the cytocompatibility and skin irritation of the CPSRT were tested in vitro using pHEK cultures. The in vitro cellular ingrowth into the CPSRT scaffold was evaluated using pHDF and was observed by CLSM.


## 2. Materials and Methods

### 2.1. Preparation and Microstructure Examination of CPSRT

CPSRT was developed at the Advanced Materials Research Centre (AMREC-SIRIM), Malaysia and in accordance with the methods described by Zainol et al. [10]. Pharmaceutical-grade chitosan powder with molecular weight at 634 kDa and deacetylation degree (DD) at 89% was purchased from Hunza Nutriceuticals Sdn Bhd, Perak, Malaysia. Chitosan was dissolved in 1% (v/v) acetic acid to prepare a 2% (w/v) chitosan solution. About 20% (w/w) glycerol were added as a plasticizer, followed by neutralization with sodium bicarbonate to achieve a pH of 6.2. The chitosan solution was then poured into a polytetrafluoroethylene (PTFE) mold and was casted and left dry at room temperature for the preparation of chitosan film. To create the porous structure of the CPSRT, the chitosan solution was frozen at −20°C and lyophilized for 24 hours. The chitosan bilayer CPSRT was fabricated through the attachment of both chitosan film and chitosan sponge using chitosan solution as the glue. The CPSRT was sterilized using ethylene oxide (EO) according to the International Standards Organization (ISO) guidelines (Part 10993–7:1995: Ethylene Oxide Sterilization Residuals).The microstructure of the CPSRT was then observedvia an SEM system. Briefly, the CPSRT was fixed in 2.5% glutaraldehyde for 1 hour followed by fixation in 2% Osmiumtetroxid for 30 minutes at room temperature. The CPSRT was then washed two times in distilled water, and the dehydration was performed using a graded series of ethanol (25%, 50%, 75%, and 100% ethanol for 5 minutes each).


### 2.2. pHEK and pHDF Cultures

Skin samples were obtained from consenting patients who had undergone elective surgery at Hospital Universiti Sains Malaysia, Kubang Kerian, Kelantan, after being approved by the Human Ethic Committee of Universiti Sains Malaysia.The epidermal layer was lifted from the dermal layer after incubation in a dispase solution (2.4 units/mL). Keratinocytes were released from the epidermal layer using 0.25% trypsin-EDTA for 15 minutes at 37°C. The trypsin was deactivated by adding Dulbecco’s minimal Eagle’s medium (DMEM) supplemented with 10% fetal bovine serum (FBS). The pHEKs were centrifuged for 7 minutes at 200 ×g and were resuspended in CnT-07 (CELLnTEC Advanced cell system) growth medium. pHEK cells were seeded at a density of 2 × 105 viable cells/mL in culture flasks and were incubated at 37°C with 5% CO2.The remaining dermal layer was minced into smaller pieces and digested using collagenase type-I (200 cu/mL of DMEM) for 12 hours at 37°C to extract the pHDFs. The dissociated fibroblasts were washed with DPBS, and the cell pellets were sieved through a 70μm strainer before being centrifuged at 200 ×g for 10 minutes. The pHDFs were seeded at 2 × 105 viable cells/mL in DMEM supplemented with 10% FBS and 1% penicillin-streptomycin.


### 2.3. Cytotoxicity of CPSRT by LDH Assay

The pHEK cultures at passage 3 were seeded at a density of 5 × 104 cells/mL in 24-well plate. CPSRT was sized into 5 × 5 mm2 and was washed twice in the CnT-07 medium. The CPSRTs were then placed on 70% confluent cultures of pHEK in the same manner as a direct-contact test. The experiment was performed for 72 hours on 5 skin samples.At each time point, 100μL of supernatant was removed and added to an optically clear 96-well flat bottom microplate. This was mixed with 100 μL of LDH reaction mixtures (diaphorase/NAD+ + iodotetrazolium chloride and sodium lactate) and incubated for 30 minutes at room temperature, as described in the instruction manual of the LDH Cytotoxicity Detection kit (Roche). The optical density (OD) of the test samples and the controls was measured at 490 nm using an enzyme-linked immunosorbent assay (ELISA) plate reader. The reference wavelength was set to 620 nm. pHEK cultures treated with 1% triton-X solution served as the positive control, whereas pHEKs with only growth medium served as the negative control. Background absorbance was measured using growth medium alone. The cytotoxicity was expressed as a percentage of the positive control, as shown in the following equation:
(1)Cytotoxicity(%)=(ExperimentalOD-Negativecontrol)(Positivecontrol-Negativecontrol)×100%.


### 2.4. Western Blot Analysis of IL-8 and TNF-α Skin Proinflammatory Cytokines

This experiment was performed according to the western blotting protocols described by Millipore and Coufal et al. [11] with minor modifications. Cultured pHEKs in direct contact with CPSRTs were removed from the 6-well plates at 24 and 72 hours using Accutase.Protein was extracted from 5 × 106 pelleted cells (n=3) in 1 mL of RIPA buffer with salt (0.4 M sodium chloride, 50 mM Tris-HCl at pH 7.4, 1% NP-40, 0.1% sodium dodecyl sulphate (SDS), 1% Na-deoxycholate, 1 mM EDTA and 1 mM phenylmethanesulphonyl fluoride) at 4°C on a shaker for 5 hours. The lysed cells were then centrifuged at 15,700 ×g for 20 minutes at 4°C.A 10% resolving gel (monomer solution acrylamide, 4X running gel buffer pH 8.8, 10% ammonium persulphate (APS), 10% SDS, TEMED and ddH2O) was precast for 15 minutes before adding a layer of 7.5% stacking gel on top (monomer solution acrylamide, 4X stacking gel buffer at pH 6.8, 10% APS, 10% SDS, TEMED, and ddH2O). Ten microliters of sample (at 1 μg/μL total protein concentration) was mixed with 10 μL of 2X protein sample loading buffer. Protein samples were heated for 5 minutes at 96°C and loaded into wells, followed by the addition of 5 μL of prestained protein ladder in a different well. SDS polyacrylamide gel electrophoresis was performed at 150 V for 45 minutes. Transblotting was conducted at a constant 13 V for 90 minutes.The transblotted polyvinylidene fluoride membrane was blocked with blocking buffer (5% w/v nonfat milk, 1X Tris buffered saline (TBS) and 0.05% Tween-20) for 1 hour, followed by washing buffer (1X TBS and 0.05% Tween-20) for 10 minutes. The membranes were then incubated with the following primary antibodies: mouse monoclonal antihuman IL-8 (dilution 1 : 1000) (Abcam), TNF-α (dilution 1 : 1000) (Abcam), and loading control alpha-tubulin (dilution 1 : 5000) (Abcam) for 120 minutes each. Goat antimouse HRP-conjugated secondary antibody (dilution at 1 : 2000) (Sigma-Aldrich) was added and incubated for 1 hour at room temperature. The membrane was then incubated with chemiluminescent horseradish peroxidase substrate for 3 minutes at room temperature before visualization and quantification of band intensity using a ChemiImager 4040 image analyzer. Protein band intensity was scored in arbitrary intensity units (AIUs) and was normalized to the alpha-tubulin loading control. Each experiment was repeated in three skin samples. Cultured pHEK in direct contact with low-density polyethylene (LDPE) served as negative control whereas the organotin-polyvinylchloride (PVC) as positive control.


### 2.5. Growth of pHDF within CPSRT Observed via CLSM Microscopy

pHDF cultures at passage 3 were dislodged from culture flasks and seeded at 2 × 106 viable cells/mL onto CPSRTs in 96-well plates. After 24 hours, the CPSRTs were transferred to 12-well plates. Growth medium was changed every day to mitigate nutrient depletion. Cultures were evaluated at days 5 and 14.Briefly, CPSRTs were transferred back to 96-well plates and washed twice with Dulbecco’s phosphate buffered saline (DPBS) before live/dead cell staining. One hundred microliters of live/dead cell reagents (Molecular Probe, Invitrogen) containing calcein (2μM) and ethidium homodimer-1 (4 μM) was added to each CPSRT and incubated for 45 minutes at room temperature. CPSRTs were imaged both in cross-section and on the construct surface under a CLSM with excitation/emission wavelengths at 495 nm/515 nm for calcein and 495 nm/635 nm for ethidium-homodimer-1. CPSRTs incubated in growth medium without cultured cells served as the negative control.


### 2.6. Statistical Analyses

The results are expressed as mean ± standard deviation (SD). The Wilcoxon signed-rank test was used to assess significance among the different experimental conditions. Differences were regarded as significant atP≤0.05.


## 2.1. Preparation and Microstructure Examination of CPSRT

CPSRT was developed at the Advanced Materials Research Centre (AMREC-SIRIM), Malaysia and in accordance with the methods described by Zainol et al. [10]. Pharmaceutical-grade chitosan powder with molecular weight at 634 kDa and deacetylation degree (DD) at 89% was purchased from Hunza Nutriceuticals Sdn Bhd, Perak, Malaysia. Chitosan was dissolved in 1% (v/v) acetic acid to prepare a 2% (w/v) chitosan solution. About 20% (w/w) glycerol were added as a plasticizer, followed by neutralization with sodium bicarbonate to achieve a pH of 6.2. The chitosan solution was then poured into a polytetrafluoroethylene (PTFE) mold and was casted and left dry at room temperature for the preparation of chitosan film. To create the porous structure of the CPSRT, the chitosan solution was frozen at −20°C and lyophilized for 24 hours. The chitosan bilayer CPSRT was fabricated through the attachment of both chitosan film and chitosan sponge using chitosan solution as the glue. The CPSRT was sterilized using ethylene oxide (EO) according to the International Standards Organization (ISO) guidelines (Part 10993–7:1995: Ethylene Oxide Sterilization Residuals).The microstructure of the CPSRT was then observedvia an SEM system. Briefly, the CPSRT was fixed in 2.5% glutaraldehyde for 1 hour followed by fixation in 2% Osmiumtetroxid for 30 minutes at room temperature. The CPSRT was then washed two times in distilled water, and the dehydration was performed using a graded series of ethanol (25%, 50%, 75%, and 100% ethanol for 5 minutes each).


## 2.2. pHEK and pHDF Cultures

Skin samples were obtained from consenting patients who had undergone elective surgery at Hospital Universiti Sains Malaysia, Kubang Kerian, Kelantan, after being approved by the Human Ethic Committee of Universiti Sains Malaysia.The epidermal layer was lifted from the dermal layer after incubation in a dispase solution (2.4 units/mL). Keratinocytes were released from the epidermal layer using 0.25% trypsin-EDTA for 15 minutes at 37°C. The trypsin was deactivated by adding Dulbecco’s minimal Eagle’s medium (DMEM) supplemented with 10% fetal bovine serum (FBS). The pHEKs were centrifuged for 7 minutes at 200 ×g and were resuspended in CnT-07 (CELLnTEC Advanced cell system) growth medium. pHEK cells were seeded at a density of 2 × 105 viable cells/mL in culture flasks and were incubated at 37°C with 5% CO2.The remaining dermal layer was minced into smaller pieces and digested using collagenase type-I (200 cu/mL of DMEM) for 12 hours at 37°C to extract the pHDFs. The dissociated fibroblasts were washed with DPBS, and the cell pellets were sieved through a 70μm strainer before being centrifuged at 200 ×g for 10 minutes. The pHDFs were seeded at 2 × 105 viable cells/mL in DMEM supplemented with 10% FBS and 1% penicillin-streptomycin.


## 2.3. Cytotoxicity of CPSRT by LDH Assay

The pHEK cultures at passage 3 were seeded at a density of 5 × 104 cells/mL in 24-well plate. CPSRT was sized into 5 × 5 mm2 and was washed twice in the CnT-07 medium. The CPSRTs were then placed on 70% confluent cultures of pHEK in the same manner as a direct-contact test. The experiment was performed for 72 hours on 5 skin samples.At each time point, 100μL of supernatant was removed and added to an optically clear 96-well flat bottom microplate. This was mixed with 100 μL of LDH reaction mixtures (diaphorase/NAD+ + iodotetrazolium chloride and sodium lactate) and incubated for 30 minutes at room temperature, as described in the instruction manual of the LDH Cytotoxicity Detection kit (Roche). The optical density (OD) of the test samples and the controls was measured at 490 nm using an enzyme-linked immunosorbent assay (ELISA) plate reader. The reference wavelength was set to 620 nm. pHEK cultures treated with 1% triton-X solution served as the positive control, whereas pHEKs with only growth medium served as the negative control. Background absorbance was measured using growth medium alone. The cytotoxicity was expressed as a percentage of the positive control, as shown in the following equation:
(1)Cytotoxicity(%)=(ExperimentalOD-Negativecontrol)(Positivecontrol-Negativecontrol)×100%.


## 2.4. Western Blot Analysis of IL-8 and TNF-α Skin Proinflammatory Cytokines

This experiment was performed according to the western blotting protocols described by Millipore and Coufal et al. [11] with minor modifications. Cultured pHEKs in direct contact with CPSRTs were removed from the 6-well plates at 24 and 72 hours using Accutase.Protein was extracted from 5 × 106 pelleted cells (n=3) in 1 mL of RIPA buffer with salt (0.4 M sodium chloride, 50 mM Tris-HCl at pH 7.4, 1% NP-40, 0.1% sodium dodecyl sulphate (SDS), 1% Na-deoxycholate, 1 mM EDTA and 1 mM phenylmethanesulphonyl fluoride) at 4°C on a shaker for 5 hours. The lysed cells were then centrifuged at 15,700 ×g for 20 minutes at 4°C.A 10% resolving gel (monomer solution acrylamide, 4X running gel buffer pH 8.8, 10% ammonium persulphate (APS), 10% SDS, TEMED and ddH2O) was precast for 15 minutes before adding a layer of 7.5% stacking gel on top (monomer solution acrylamide, 4X stacking gel buffer at pH 6.8, 10% APS, 10% SDS, TEMED, and ddH2O). Ten microliters of sample (at 1 μg/μL total protein concentration) was mixed with 10 μL of 2X protein sample loading buffer. Protein samples were heated for 5 minutes at 96°C and loaded into wells, followed by the addition of 5 μL of prestained protein ladder in a different well. SDS polyacrylamide gel electrophoresis was performed at 150 V for 45 minutes. Transblotting was conducted at a constant 13 V for 90 minutes.The transblotted polyvinylidene fluoride membrane was blocked with blocking buffer (5% w/v nonfat milk, 1X Tris buffered saline (TBS) and 0.05% Tween-20) for 1 hour, followed by washing buffer (1X TBS and 0.05% Tween-20) for 10 minutes. The membranes were then incubated with the following primary antibodies: mouse monoclonal antihuman IL-8 (dilution 1 : 1000) (Abcam), TNF-α (dilution 1 : 1000) (Abcam), and loading control alpha-tubulin (dilution 1 : 5000) (Abcam) for 120 minutes each. Goat antimouse HRP-conjugated secondary antibody (dilution at 1 : 2000) (Sigma-Aldrich) was added and incubated for 1 hour at room temperature. The membrane was then incubated with chemiluminescent horseradish peroxidase substrate for 3 minutes at room temperature before visualization and quantification of band intensity using a ChemiImager 4040 image analyzer. Protein band intensity was scored in arbitrary intensity units (AIUs) and was normalized to the alpha-tubulin loading control. Each experiment was repeated in three skin samples. Cultured pHEK in direct contact with low-density polyethylene (LDPE) served as negative control whereas the organotin-polyvinylchloride (PVC) as positive control.


## 2.5. Growth of pHDF within CPSRT Observed via CLSM Microscopy

pHDF cultures at passage 3 were dislodged from culture flasks and seeded at 2 × 106 viable cells/mL onto CPSRTs in 96-well plates. After 24 hours, the CPSRTs were transferred to 12-well plates. Growth medium was changed every day to mitigate nutrient depletion. Cultures were evaluated at days 5 and 14.Briefly, CPSRTs were transferred back to 96-well plates and washed twice with Dulbecco’s phosphate buffered saline (DPBS) before live/dead cell staining. One hundred microliters of live/dead cell reagents (Molecular Probe, Invitrogen) containing calcein (2μM) and ethidium homodimer-1 (4 μM) was added to each CPSRT and incubated for 45 minutes at room temperature. CPSRTs were imaged both in cross-section and on the construct surface under a CLSM with excitation/emission wavelengths at 495 nm/515 nm for calcein and 495 nm/635 nm for ethidium-homodimer-1. CPSRTs incubated in growth medium without cultured cells served as the negative control.


## 2.6. Statistical Analyses

The results are expressed as mean ± standard deviation (SD). The Wilcoxon signed-rank test was used to assess significance among the different experimental conditions. Differences were regarded as significant atP≤0.05.


## 3. Results

### 3.1. Structure of CPSRT

The microstructure of the sponge layer and the cross-sectional view bilayer CPSRT was observed under an SEM (Figure1). The pore sizes of CPSRT are ranging from 50 to 150 μm (Figure 1(a)). The chitosan film layer was intact to the chitosan porous layer, making up a bilayer structure (Figure 1(b)).SEM images of CPSRT. (a) Surface of sponge layer. (b) Cross-sectional view of CPSRT that indicates a chitosan film combining a chitosan porous layer.
(a)(b)


### 3.2. Cytotoxicity of CPSRT In Vitro

Cytotoxicityin vitro was assessed by measuring the amount of LDH released into the supernatant from damaged pHEKs after 72 hours of incubation with CPSRTs, as a percentage of the LDH values in positive controls. The LDH assay indicated that the CPSRTs displayed no measurable cytotoxic behavior when compared with positive controls at all time points (Figure 2). However, cytotoxicity was noticeably elevated after 48 hours of treatment with CPSRTs compared to the 6-hour CPSRT treatment. The CPSRT cytotoxicity was significantly reduced at 72 hours (P<0.05).Figure 2
Cytotoxicity of CPSRT as determined by the release of LDH from the damaged cells.n=5, *for P≤0.05.


### 3.3. Proinflammatory Cytokine Expression of CPSRT

IL-8 and TNF-α proteins were expressed by pHEKs at all time points (Figures 3 and 4). pHEKs treated with organotin-PVC produced the most IL-8 and TNF-α at 24 hours, and both proteins were noticeably increased at 72 hours (P<0.05). No significant difference in IL-8 expression was observed between pHEKs treated with CPSRT and LDPE at both time points. However, TNF-α expression remained unchanged in the treatment with CPSRTs at both time points and had the lowest value out of all three groups (CPSRT, organotin-PVC, LDPE). Although pHEKs treated with LDPE expressed higher TNF-α compared with CPSRT at 24 hours, LDPE-induced TNF-α levels declined at 72 hours.Figure 3
Western blot analysis of IL-8 in pHEK cultures. pHEK cultures were treated for 24 hours ((i) CPSRT, (ii) LDPE, and (iii) organotin-PVC) and 72 hours ((iv) CPSRT, (v) LDPE, and (vi) organotin-PVC) (n=3). *For P≤0.05 compared with both CPSRT and LDPE.Figure 4
TNF-α protein expression in western blot analysis. pHEK cultures were treated for 24 hours [(i) CPSRT, (ii) LDPE and (iii) organotin-PVC] and 72 hours [(iv) CPSRT, (v) LDPE and (vi) organotin-PVC] (n=3). *For P≤0.05 compared with CPSRT.


### 3.4. Ingrowths of pHDF on CPSRT

The ingrowth of pHDF cells was observable at day 5 by CLSM (Figure5). The viable cultured cells propagated in small groups within the CPSRT pores, as shown by the green fluorescence (Figure 5(a)). No significant quantity of dead or apoptosis cells was seen, indicated by the lack of red fluorescence emission. At fourteen days postseeding, the groups of pHDF cells had proliferated enough to fuse into a larger cell mass that covered the top surface of CPSRT (Figure 5(b)). Furthermore, pHDF cells had also infiltrated and proliferated into the porous structure of CPSRT, as visualized in the cross-sectional view (Figure 5(c)).Live/dead cell staining of pHDF cultures seeded on CPSRTs. (a) Three-dimensional (3D) surfaces were scanned using a CLSM at day 5. (b) Viable pHDFs (green) were confluent at day 14. (c) Cross-sectional view of a CPSRT seeded with pHDFs at day 14.
(a)(b)(c)


## 3.1. Structure of CPSRT

The microstructure of the sponge layer and the cross-sectional view bilayer CPSRT was observed under an SEM (Figure1). The pore sizes of CPSRT are ranging from 50 to 150 μm (Figure 1(a)). The chitosan film layer was intact to the chitosan porous layer, making up a bilayer structure (Figure 1(b)).SEM images of CPSRT. (a) Surface of sponge layer. (b) Cross-sectional view of CPSRT that indicates a chitosan film combining a chitosan porous layer.
(a)(b)


## 3.2. Cytotoxicity of CPSRT In Vitro

Cytotoxicityin vitro was assessed by measuring the amount of LDH released into the supernatant from damaged pHEKs after 72 hours of incubation with CPSRTs, as a percentage of the LDH values in positive controls. The LDH assay indicated that the CPSRTs displayed no measurable cytotoxic behavior when compared with positive controls at all time points (Figure 2). However, cytotoxicity was noticeably elevated after 48 hours of treatment with CPSRTs compared to the 6-hour CPSRT treatment. The CPSRT cytotoxicity was significantly reduced at 72 hours (P<0.05).Figure 2
Cytotoxicity of CPSRT as determined by the release of LDH from the damaged cells.n=5, *for P≤0.05.


## 3.3. Proinflammatory Cytokine Expression of CPSRT

IL-8 and TNF-α proteins were expressed by pHEKs at all time points (Figures 3 and 4). pHEKs treated with organotin-PVC produced the most IL-8 and TNF-α at 24 hours, and both proteins were noticeably increased at 72 hours (P<0.05). No significant difference in IL-8 expression was observed between pHEKs treated with CPSRT and LDPE at both time points. However, TNF-α expression remained unchanged in the treatment with CPSRTs at both time points and had the lowest value out of all three groups (CPSRT, organotin-PVC, LDPE). Although pHEKs treated with LDPE expressed higher TNF-α compared with CPSRT at 24 hours, LDPE-induced TNF-α levels declined at 72 hours.Figure 3
Western blot analysis of IL-8 in pHEK cultures. pHEK cultures were treated for 24 hours ((i) CPSRT, (ii) LDPE, and (iii) organotin-PVC) and 72 hours ((iv) CPSRT, (v) LDPE, and (vi) organotin-PVC) (n=3). *For P≤0.05 compared with both CPSRT and LDPE.Figure 4
TNF-α protein expression in western blot analysis. pHEK cultures were treated for 24 hours [(i) CPSRT, (ii) LDPE and (iii) organotin-PVC] and 72 hours [(iv) CPSRT, (v) LDPE and (vi) organotin-PVC] (n=3). *For P≤0.05 compared with CPSRT.


## 3.4. Ingrowths of pHDF on CPSRT

The ingrowth of pHDF cells was observable at day 5 by CLSM (Figure5). The viable cultured cells propagated in small groups within the CPSRT pores, as shown by the green fluorescence (Figure 5(a)). No significant quantity of dead or apoptosis cells was seen, indicated by the lack of red fluorescence emission. At fourteen days postseeding, the groups of pHDF cells had proliferated enough to fuse into a larger cell mass that covered the top surface of CPSRT (Figure 5(b)). Furthermore, pHDF cells had also infiltrated and proliferated into the porous structure of CPSRT, as visualized in the cross-sectional view (Figure 5(c)).Live/dead cell staining of pHDF cultures seeded on CPSRTs. (a) Three-dimensional (3D) surfaces were scanned using a CLSM at day 5. (b) Viable pHDFs (green) were confluent at day 14. (c) Cross-sectional view of a CPSRT seeded with pHDFs at day 14.
(a)(b)(c)


## 4. Discussion

In this study, a skin-like bilayer porous chitosan scaffold mimicking the thickness of natural skin was created for skin tissue engineering. For skin tissue engineering, pore size for a scaffold is recommended to be within the range between 100 to 200μm [12]. Nevertheless, significant cell proliferation and differentiation were reported for the scaffolds with small pore sizes. Chitosan-gelatin-hydroxyapatite scaffold with pore sizes at the top (65–80 μm) and bottom (10–20 μm), resulted in proliferation of fibroblasts and keratinocytes [13]. Similarly, lyophilized chitosan scaffold coated with collagen (40–100 μm pore sizes) was shown to have interconnected structure, which enhanced cell proliferation and wound-healing without inflammation [14].However, although chitosan is biocompatible, to ensure the CPSRT fabrication process did not alter its natural biocompatibility,in vitro models of cytotoxicity were used to evaluate the construct. In vitro cytotoxicity models are often used to screen for potential harmful effects of chemical compounds because they have good reproducibility and sensitivity, while also minimizing the use of animals. Moreover, cellular cytotoxicity systems are better predictive tools for human toxicity than are whole organism models    [5, 6, 15, 16].By using primary human cell cultures, in this case pHEKs, these results should also better reflect the cytotoxicity outcomes expected in humans, compared with results from transformed cell lines, fibroblasts, or animal cell lines    [6, 7, 17, 18]. LDH is a stable cytoplasmic enzyme present in most cells that is released when the plasma membrane is damaged or ruptured. Therefore, measuring LDH levels is a highly sensitive and accurate measure of cytotoxicity [19]. The CPSRTs in this study did not cause significant cytotoxicity compared with the positive control. However, the reduction in LDH observed at 72 hours may be attributed to chitosan-induced proliferation and cell growth, which is corroborated by the findings of Cho et al. [20]. Chitosan’s oligomers N-acetylglucosamine and glucosamine have been implicated in enhancing cell growth. Glucosamine has been reported to be important for detoxification in the liver and kidneys, as well as in anti-inflammatory, hepatoprotective, antireactive, and antihypoxic activities [21, 22]. N-acetylglucosamine is a major component of dermal tissue that is essential for repairing scar tissue and is present in large quantity in the early phase of wound-healing. It has been effective in modulating keratinocyte cellular adhesion, proliferation, and differentiation, leading to the normalization of stratum corneum exfoliation [23]. Therefore, it is possible that CPSRTs could promote the proliferation of keratinocytes by functioning as a controlled delivery source for N-acetylglucosamine and glucosamine to the in vitro wound-like model in this study.Because the CPSRT is intended to be a scaffold for skin transplantation, it should avoid irritating epidermal transplantation sites to avoid failure of the bioengineered skin graft. Keratinocytes are the primary cell type in the epidermis and serve as a major contributor of epidermal cytokines, particularly pro-inflammatory cytokines, that act as the first line of defense to protect the body from invaders [24]. Many of the currently identified cytokines, such as IL-6, IL-7, IL-8, and TNF-α, are produced by keratinocytes, either constitutively or upon induction by various stimuli    [7, 25]. The findings of this study corroborate the cytokine expression profiles of keratinocytes. The pro-inflammatory cytokines IL-8 and TNF-α were expressed in the negative control cultures, suggesting that these cytokines are constitutively expressed. However, the expression of both cytokines was significantly higher in the positive control, indicating that higher levels of both IL-8 and TNF-α could indicate skin irritation in vitro. High expression of TNF-α has been found in patients with keratinocyte lesions, rendering it important role in inflammatory process [26]. Elevated levels of TNF-α expression could indicate activation of cytokine pathways associated with inflammation and disease progression [6]. CPSRTs did not induce increased production of either IL-8 or TNF-α, but maintained levels similar to those in the negative control, suggesting that these scaffolds did not provoke an irritation response in vitro.Combining cells with natural or synthetic scaffolds is a fundamental approach in tissue engineering. The scaffolds help maintain a three-dimensional (3D) space for cells in order to facilitate cellular proliferation and differentiation and to eventually guide cellular organization into a defined architecture for tissue regeneration. Natural biopolymers have been the focus as they are biocompatible, biodegradable and come from renewable resources. Chitosan has structural characteristics similar to glycosaminoglycans, which can be useful for developing a skin replacement. Therefore, the CPSRT was produced in a skin-like format with a 3D porous structure to provide space for cellular ingrowth. Porous chitosan structures can be formed by freezing and lyophilizing chitosan salt solutions in suitable molds. During the freezing process, ice crystals nucleate along thermal gradients and generate a porous structure when removed by lyophilization.Cultured pHDF cells adapted to the 3D environment by adhering to the 3D structure of the CPSRT at day 5, as verified by live/dead staining and imaging by CLSM. This CPSRT supports cell attachment, as in agreement with Zhu et al. [27] and Fakhry et al. [28]. Cultured pHDFs grew rapidly and achieved confluence within the CPSRT at fourteen days post-seeding. This growth is likely due to the initial adaptation of cells to the 3D environment by adhering to the chitosan motifs in the construct. In addition, degraded chitosan oligomers have been effective at inducing cell migration and proliferation [29].


## 5. Conclusion

A naturally derived, bilayer porous biopolymer scaffold, termed a CPSRT, has been developed for skin tissue engineering with pore sizes ranging from 50 to 150μm. It has been shown to be biocompatible, as it neither induced significant cytotoxic response in the LDH assay nor an irritation response in vitro. This biocompatibility is further supported by the observed ingrowth of pHDFs into the CPSRT.



---

*Source: 645820-2011-09-07.xml*