# Effect of B2O3 Content on the Sintering Basic Characteristics of Mixed Ore Powder of Vanadium-Titanium Magnetite and Hematite

Authors: Hao Liu; Ke Zhang; Qingfeng Ling; Yuelin Qin
Journal: Journal of Chemistry
 (2020)

---

## Abstract

The sintering basic characteristics of iron ore play a key role in the process of sintering. In this study, the effects of B2O3 on the assimilation characteristics, softening temperature, fluidity of liquid phase, compressive strength of bonding phase, and microstructure of the mixed fine powder of hematite and vanadium-titanium magnetite (H-VTM) are studied. Results show that B2O3 content from 0%–5% (wt%) could improve the assimilation characteristics of the H-VTM and increase the amount of the liquid phase. The liquidity of the bonding phase index (LBPI) of the H-VTM increases from 3.7 to 24.2. When B2O3 content exceeds 2%, the diameter of the pore in the H-VTM sintered samples enlarges. However, the compressive strength gradually decreases. Boron and calcium-magnesium-aluminium elements are abundant in the bonding phase, which can reduce the formation of calcium silicate and perovskite in H-VTM sintered samples.


---

## Body

## 1. Introduction

With the rapid development of the steel industry, the supply of high-quality iron ore is insufficient, so the vanadium-titanium magnetite (VTM) with sufficient reserves is highly needed. The extraction of iron, vanadium, titanium, and other elements in VTM has remarkably progressed, and its industrial-scale production is still dominated by the blast furnace ironmaking process. The primary raw materials for the blast furnace are vanadium-titanium sinter and vanadium-titanium pellets [1, 2].Vanadium-titanium sinter is the raw material for the blast furnace, and there are still many difficulties in the production of vanadium-titanium sinter. As increasing the proportion of VTM in sintering, the amount of the liquid phase and the liquid-phase bonding force both decrease. Resulting in a lower yield and drum strength of vanadium-titanium sinter, the production volume of small size sinter also increases. Low-temperature reduction pulverization index (RDI−3.15) of the vanadium-titanium sinter is significantly higher than the sinter without vanadium-titanium magnetite [3, 4].Zhou et al. [5] revealed that enhancing granulation improved the breathability of the sintering layer, and the increase in oxygen potential could multiply the mass fraction of calcium ferrite in the sinter, including mineral composition, yield, and quality [6]. D. G. Jiang et al. [7] proposed a new idea based on the complementary mineralization of the assimilation characteristics and liquid phase fluidity. They confirmed the feasibility of mineralization based on the sintering basic characteristics of iron ore by optimizing the mineralization method and the sinter pot test. Xu et al. [8] confirmed that the low-temperature reduction pulverization index was improved, and the reduction index was enhanced by 2.6% when the content of iron concentrate rich in boron and magnesium in the vanadium-titanium sintering mixture approached 5%. Chu et al. [9–12] determined that economic indicators such as vertical sintering speed, yield, drum index, sintering cup utilization coefficient, and low-temperature reduction pulverization index initially increased and subsequently decreased with increasing mass ratio of boron ore. Hao [13] found that the low-temperature reduction pulverization index and drum strength of the sintered ore increased, and the reduction index, softening temperature, and softening remain unchanged after boric acid and calcium chloride were added. Zhao et al. [14, 15] observed that adding a certain amount of boron-iron concentrate to the vanadium-titanium sinter could make full use of B2O3, as a result, the liquid phase of the sinter increased, the consolidation process improved, and the metallurgical properties of the sinter also enhanced.Ren et al. [16, 17] researched the influencing pattern of different B2O3 contents on the mineral phase of high-titanium-type VTM and the qualities of sinter; they pronounced that B2O3 was mainly deposited in the 2CaO∙xSiO2∙2/3 (1 − x) B2O3 phase of vanadium-titanium sinter and B2O3 effectively inhibited the precipitation of CaTiO3 and 2CaO∙xSiO2∙2/3 (1 − x) B2O3 and promoted the precipitation of iron-containing mineral phase.In summary, we find that adding boron slime, boric acid, and boron-iron concentrate could improve the strength and the metallurgical performance of sinter and reduce the low-temperature pulverulent ratio, which is conducive to the blast furnace. It is not difficult to find that boron oxide plays a very important role in the sintering process. However, existing researches mainly focus on the effect of boron oxide on the macroperformance of vanadium-titanium sinter. Studies on the influence of B2O3 on the sintering basic characteristics of mixed ore powders using vanadium-titanium fine powder as the main raw material are rarely reported. Especially the researches on the influence mechanism of B2O3 on the sintering basic characteristics of mixed ore powder of vanadium-titanium magnetite and hematite have not been reported so far.Hence, in this work, according to the actual production of mineral types and proportions in southwest China. Experimental samples are mixed with VTM concentrate and Australian hematite powder with a specific mass ratio (8 : 2), and this particular mixture powder is called H-VTM. The effects of B2O3 content on the assimilation characteristics, melting temperature, liquidity of liquid phase, compressive strength, and microstructure changes are studied. The influences of different B2O3 contents on the sintering basic characteristics of H-VTM sintering samples are obtained. The mechanism of B2O3 affecting the sintering process of vanadium-titanium magnetite and hematite is also clarified. Meanwhile, it is possible to find a new method for the recycling of B2O3 in boron-containing solid wastes.


## 2. Materials and Methods

### 2.1. Raw Materials

The chemical composition of the sintered raw material is shown in Table1. Based on actual production situation, the mixed mineral powder used in this study composes of hematite powder and vanadium-titanium magnetite powder with a mass ratio of 2 : 8. The particle size of hematite powder and vanadium-titanium magnetite powder is both less than 74 μm. All the other reagents used in the experiments are of analytical grade.Table 1
Chemical composition of ore powder (wt%).
Ore powderTFeSiO2CaOAl2O3MgOTiO2MnOFeOPSVTM55.784.330.693.862.789.080.3630.500.090.54Hematite59.764.320.733.160.140.120.160.800.070.09H-VTM56.584.330.703.722.257.290.3224.560.090.45


### 2.2. Methods

#### 2.2.1. Assimilation Characteristics

The assimilation characteristics experiment is shown in Figure1. H-VTM and CaO are made into a mixed ore powder sample at 6000 N pressure, with a diameter of 8 mm and CaO sample with a diameter of 15 mm. The mixed ore powder sample was placed on top of the CaO sample and then placed into the sintering device to roast at 200°C in a specific heating system. The heating rate is 10° per minute until the end of the assimilation. Afterwards, the samples were naturally cooled and removed from the device. The assimilation characteristics were characterized at the temperature at which the contact angle between the H-VTM sample and the CaO sample began to change. The assimilation characteristics are used to characterize the difficulty of the reaction between iron ore powder and calcium oxide.Figure 1
Diagrammatic chart of the assimilation characteristics experiment.


#### 2.2.2. Melting Temperature

The experiment of melting temperature is shown in Figure2. The chemical composition of the samples ensured the binary basicity R2 of 2.0. A mixed sample (1.00 g) is placed in a 3 mm × 3 mm mould to make into the sample. Then, it is placed on a corundum gasket. The well-made sample is heated with a particular heating system; the melting of the column is observed to determine its melting temperature.Figure 2
Diagrammatic chart of melting temperature experiment.


#### 2.2.3. Compressive Strength of Bonding Phase

The experiment of the compressive strength of the bonding phase is shown in Figure3. The chemical composition of the samples ensured the binary basicity R2 of 2.0. Every mixed sample (3.00 g) is placed in a Φ8 mm  ×  8 mm mould. The samples are placed in the heating furnace under an air atmosphere and heated at 1250°C for 30 min. After heating, the specimens are moved out from the furnace and air-cooled to ambient temperature. Four sintered samples are selected for the compressive strength test. The average compressive strength is used to characterize the bonding phase strength.Figure 3
Diagrammatic chart of compressive strength of bonding phase.


#### 2.2.4. Fluidity of Liquid Phase

The experiment of the fluidity is shown in Figure4. The liquidity of the bonding phase index (LBPI) is calculated according to the equation as follows:(1)LBPI=S∗=S1−S0S0×100%,where S∗ represents the ratio of the increased area of the sample to the original area of the sample after heating and flowing and S0 and S1 are the vertical projection areas before and after flowing.Figure 4
Diagrammatic chart of the fluidity of liquid-phase experiment.The chemical composition of the samples ensured the binary basicityR2 of 2.0. A mixed sample of 1.00 g is placed in a Φ8 mm × 8 mm mould and heated at 1350°C for 30 min. After the samples cooled, every sample is removed and analysed by image software. The fluidity of the bonding phase index of H-VTM samples is calculated according to equation (1).


## 2.1. Raw Materials

The chemical composition of the sintered raw material is shown in Table1. Based on actual production situation, the mixed mineral powder used in this study composes of hematite powder and vanadium-titanium magnetite powder with a mass ratio of 2 : 8. The particle size of hematite powder and vanadium-titanium magnetite powder is both less than 74 μm. All the other reagents used in the experiments are of analytical grade.Table 1
Chemical composition of ore powder (wt%).
Ore powderTFeSiO2CaOAl2O3MgOTiO2MnOFeOPSVTM55.784.330.693.862.789.080.3630.500.090.54Hematite59.764.320.733.160.140.120.160.800.070.09H-VTM56.584.330.703.722.257.290.3224.560.090.45


## 2.2. Methods

### 2.2.1. Assimilation Characteristics

The assimilation characteristics experiment is shown in Figure1. H-VTM and CaO are made into a mixed ore powder sample at 6000 N pressure, with a diameter of 8 mm and CaO sample with a diameter of 15 mm. The mixed ore powder sample was placed on top of the CaO sample and then placed into the sintering device to roast at 200°C in a specific heating system. The heating rate is 10° per minute until the end of the assimilation. Afterwards, the samples were naturally cooled and removed from the device. The assimilation characteristics were characterized at the temperature at which the contact angle between the H-VTM sample and the CaO sample began to change. The assimilation characteristics are used to characterize the difficulty of the reaction between iron ore powder and calcium oxide.Figure 1
Diagrammatic chart of the assimilation characteristics experiment.


### 2.2.2. Melting Temperature

The experiment of melting temperature is shown in Figure2. The chemical composition of the samples ensured the binary basicity R2 of 2.0. A mixed sample (1.00 g) is placed in a 3 mm × 3 mm mould to make into the sample. Then, it is placed on a corundum gasket. The well-made sample is heated with a particular heating system; the melting of the column is observed to determine its melting temperature.Figure 2
Diagrammatic chart of melting temperature experiment.


### 2.2.3. Compressive Strength of Bonding Phase

The experiment of the compressive strength of the bonding phase is shown in Figure3. The chemical composition of the samples ensured the binary basicity R2 of 2.0. Every mixed sample (3.00 g) is placed in a Φ8 mm  ×  8 mm mould. The samples are placed in the heating furnace under an air atmosphere and heated at 1250°C for 30 min. After heating, the specimens are moved out from the furnace and air-cooled to ambient temperature. Four sintered samples are selected for the compressive strength test. The average compressive strength is used to characterize the bonding phase strength.Figure 3
Diagrammatic chart of compressive strength of bonding phase.


### 2.2.4. Fluidity of Liquid Phase

The experiment of the fluidity is shown in Figure4. The liquidity of the bonding phase index (LBPI) is calculated according to the equation as follows:(1)LBPI=S∗=S1−S0S0×100%,where S∗ represents the ratio of the increased area of the sample to the original area of the sample after heating and flowing and S0 and S1 are the vertical projection areas before and after flowing.Figure 4
Diagrammatic chart of the fluidity of liquid-phase experiment.The chemical composition of the samples ensured the binary basicityR2 of 2.0. A mixed sample of 1.00 g is placed in a Φ8 mm × 8 mm mould and heated at 1350°C for 30 min. After the samples cooled, every sample is removed and analysed by image software. The fluidity of the bonding phase index of H-VTM samples is calculated according to equation (1).


## 2.2.1. Assimilation Characteristics

The assimilation characteristics experiment is shown in Figure1. H-VTM and CaO are made into a mixed ore powder sample at 6000 N pressure, with a diameter of 8 mm and CaO sample with a diameter of 15 mm. The mixed ore powder sample was placed on top of the CaO sample and then placed into the sintering device to roast at 200°C in a specific heating system. The heating rate is 10° per minute until the end of the assimilation. Afterwards, the samples were naturally cooled and removed from the device. The assimilation characteristics were characterized at the temperature at which the contact angle between the H-VTM sample and the CaO sample began to change. The assimilation characteristics are used to characterize the difficulty of the reaction between iron ore powder and calcium oxide.Figure 1
Diagrammatic chart of the assimilation characteristics experiment.


## 2.2.2. Melting Temperature

The experiment of melting temperature is shown in Figure2. The chemical composition of the samples ensured the binary basicity R2 of 2.0. A mixed sample (1.00 g) is placed in a 3 mm × 3 mm mould to make into the sample. Then, it is placed on a corundum gasket. The well-made sample is heated with a particular heating system; the melting of the column is observed to determine its melting temperature.Figure 2
Diagrammatic chart of melting temperature experiment.


## 2.2.3. Compressive Strength of Bonding Phase

The experiment of the compressive strength of the bonding phase is shown in Figure3. The chemical composition of the samples ensured the binary basicity R2 of 2.0. Every mixed sample (3.00 g) is placed in a Φ8 mm  ×  8 mm mould. The samples are placed in the heating furnace under an air atmosphere and heated at 1250°C for 30 min. After heating, the specimens are moved out from the furnace and air-cooled to ambient temperature. Four sintered samples are selected for the compressive strength test. The average compressive strength is used to characterize the bonding phase strength.Figure 3
Diagrammatic chart of compressive strength of bonding phase.


## 2.2.4. Fluidity of Liquid Phase

The experiment of the fluidity is shown in Figure4. The liquidity of the bonding phase index (LBPI) is calculated according to the equation as follows:(1)LBPI=S∗=S1−S0S0×100%,where S∗ represents the ratio of the increased area of the sample to the original area of the sample after heating and flowing and S0 and S1 are the vertical projection areas before and after flowing.Figure 4
Diagrammatic chart of the fluidity of liquid-phase experiment.The chemical composition of the samples ensured the binary basicityR2 of 2.0. A mixed sample of 1.00 g is placed in a Φ8 mm × 8 mm mould and heated at 1350°C for 30 min. After the samples cooled, every sample is removed and analysed by image software. The fluidity of the bonding phase index of H-VTM samples is calculated according to equation (1).


## 3. Results and Discussion

### 3.1. Sintering Basic Characteristics of H-VTM with Different B2O3 Contents

In Figure5, the sample without B2O3 began to assimilate at 1359°C, but the assimilation temperature decreased to 1205°C when the B2O3 was 5.00% (wt%). This result indicated that adding B2O3 could improve the assimilation characteristics of H-VTM. B2O3 has a low melting point (450°C), which could form a low-melting-point chemical compound and promote the formation of the liquid phase. For instance, the reaction of B2O3 with CaO and SiO2 can form 2CaO·B2O3·SiO2 whose melting point is 901°C. This reaction could effectively inhibit the formation of calcium orthosilicate (2CaO·SiO2). B3+ is quickly diffused into the crystals of calcium orthosilicate (2CaO·SiO2) and inhibits multiphase transformation of calcium orthosilicate. This reaction is described in the subsequent microstructure analysis.Figure 5
Sintering basic characteristics of the H-VTM sintered sample with different B2O3 contents.As is shown in Figure5, when the mass ratio of B2O3 increased from 0.00% to 5.00%, the melting temperature decreased from 1504°C to 1453°C. When increasing the amount of B2O3, the melting temperature of H-VTM decreased obviously. In the whole process, adding B2O3 was conducive to the improvement of the capacity of the liquid phase inside the sintered samples. The LBPI of the H-VTM increased significantly from 3.70 to 24.2. This trend was consistent with the results which were calculated using the reaction module and the equilibrium module of FactSage 7.1 software. The calculation conditions were based on R2 at 2.0 and carbon mass ratio at 3.5% under standard atmospheric pressure and air atmosphere. The chemical composition of the H-VTM was introduced in the reaction and the equilibrium module as input data. The amount of B2O3 was increased from 0.00% to 5.00% with a step size of 1.00%. The temperature was increased from 1000°C to 1600°C in a step of 50°C.The average compressive strength of H-VTM fluctuated significantly with the rise of B2O3. The compressive strength was 531 N/P without B2O3. The compressive strength grew significantly with the increase of B2O3 content, peaking at 857 N/P with B2O3 content at 2.00%. As the B2O3 ratio further increases, the compressive strength dropped sharply, reaching its lowest point at 356 N/P with B2O3 ratio at 5.00%.In Figure6, at the same mass ratio of B2O3, the amount of liquid phase in sintering continuously increased with the increase of temperature, especially when the temperature exceeded 1210°C. At the same temperature, the amount of liquid phase of the sample with a high percentage of boron oxide was significantly more than the sample with lower ones. When the ratios of B2O3 were 0.00%, 1.00%, 2.00%, 3.00%, 4.00%, and 5.00%, the ratios of the liquid phase were 15.74%, 25.32%, 32.43%, 39.42%, 44.73%, and 51.36%, respectively. B2O3 could react with CaO, SiO2, MgO, and Al2O3 to form mineral phases with a low melting point. Besides, the melting point of B2O3 is low (450°C). Therefore, B2O3 initially transformed into the liquid phase. Overheating reduced the liquid viscosity and quickly form a certain amount of liquid phase, which was beneficial for diffusion during sintering. As a result, the amount of liquid phase of H-VTM improved with the increase of the ratio of B2O3.Figure 6
The volume of liquid phase with different B2O3 contents.


### 3.2. Microstructure of H-VTM with Different B2O3 Contents

The X-ray diffraction (XRD) is used to investigate the phases changes of the sintered samples. As is shown in Figure7, after heating samples at 1250°C for 30 min, by contrast, the diffraction peaks of Fe3O4 and CaO·Fe2O3 increased as the B2O3 mass ratio increased.Figure 7
XRD patterns of H-VTM-sintered samples with different B2O3 contents. 1: Fe2O3; 2: Fe3O4; 3: CaO·Fe2O3; 4: 2CaO·SiO2.The addition of B2O3 could inhibit the formation of 2CaO·SiO2 and promote the formation of CaO·Fe2O3. This scene is shown in Figure 8. Before 1100oC, the 2CaO·SiO2 content grew continuously with the increase of the B2O3 mass ratio. It reached its highest value when the addition amount of B2O3 is 5.00% at 1100°C.Figure 8
2CaO·SiO2 contents in the samples with different B2O3 contents.The microstructures of the samples with different content of B2O3 were observed using a scanning electron microscope (SEM) equipped with an energy-dispersive X-ray spectroscope (EDS). In Figure 9, as the amount of B2O3 increased, the bonding phase (the bright white part) in the H-VTM-sintered sample was more evenly distributed in the microstructure. When the mass ratio of B2O3 was 2.00%, the number of pores in the sintered sample decreased significantly, but larger diameter pore began to appear because the increasing B2O3 could promote the formation of liquid phase in H-VTM. The liquid phase started to shrink during the cooling process and then came the pore structure. This phenomenon also could explain the inflexion point of the compressive strength of H-VTM and the increase of the number of internal pores, resulting in the formation of H-VTM microstructure and the decrease of compressive strength.Figure 9
SEM of H-VTM with different B2O3 contents.
(a)(b)(c)(d)(e)(f)The scanning results of the sintered sample with 5.00% B2O3 are shown in Figure 10. Hematite was mainly distributed in a fish-bone shape. Silicon, calcium, and aluminium were combined and distributed in the bright white area and formed a bonding phase. Titanium and iron were concentrated, producing the main iron base phase.Figure 10
Surface scanning of the H-VTM sample with 5% B2O3.SEM-EDS was carried out on the cooled sample with 5.00% B2O3, as is shown in Figure 11. The EDS analysis results from point A to C with 5.00% B2O3 are shown in Table 2. The main element at point A is Fe, which accounts for 67.29%. O, Si, Ca, and other elements were almost nonexistent, which indicates that the main object is hematite or magnetite. The main elements at point B are O and Fe, and the contents of Si, Ca, and B are 6.14%, 14.35%, and 7.73%, respectively. Therefore, the primary material of the point B is ferrite, silicate, or borate, forming a bonding phase. Boron is abundant in the bonding material phase. As the B2O3 mass ratio increased, the perovskite phase decreased and calcium ferrite and calcium borate gradually increased, while calcium silicate gradually decreased. These results indicated that B2O3 worked together with CaO and SiO2 to form the low-melting-point substance CaO·2B2O3 (melting point of 989°C), CaO·B2O3·2SiO2 (melting point of 957°C), and 2CaO·B2O3·SiO2 (melting point of 901°C). Thus, the production of calcium silicate decreases, and this result is consistent with XRD.Figure 11
SEM-EDS of the sample with 5% B2O3.Table 2
SEM-EDS analysis of the sample with 5.00% B2O3 (wt%).
PointBOFeSiCaTiMgAlA1.0124.2967.290.120.451.981.000.37B7.7337.6123.836.1414.351.131.642.66C6.2536.4128.715.7713.341.231.822.56


## 3.1. Sintering Basic Characteristics of H-VTM with Different B2O3 Contents

In Figure5, the sample without B2O3 began to assimilate at 1359°C, but the assimilation temperature decreased to 1205°C when the B2O3 was 5.00% (wt%). This result indicated that adding B2O3 could improve the assimilation characteristics of H-VTM. B2O3 has a low melting point (450°C), which could form a low-melting-point chemical compound and promote the formation of the liquid phase. For instance, the reaction of B2O3 with CaO and SiO2 can form 2CaO·B2O3·SiO2 whose melting point is 901°C. This reaction could effectively inhibit the formation of calcium orthosilicate (2CaO·SiO2). B3+ is quickly diffused into the crystals of calcium orthosilicate (2CaO·SiO2) and inhibits multiphase transformation of calcium orthosilicate. This reaction is described in the subsequent microstructure analysis.Figure 5
Sintering basic characteristics of the H-VTM sintered sample with different B2O3 contents.As is shown in Figure5, when the mass ratio of B2O3 increased from 0.00% to 5.00%, the melting temperature decreased from 1504°C to 1453°C. When increasing the amount of B2O3, the melting temperature of H-VTM decreased obviously. In the whole process, adding B2O3 was conducive to the improvement of the capacity of the liquid phase inside the sintered samples. The LBPI of the H-VTM increased significantly from 3.70 to 24.2. This trend was consistent with the results which were calculated using the reaction module and the equilibrium module of FactSage 7.1 software. The calculation conditions were based on R2 at 2.0 and carbon mass ratio at 3.5% under standard atmospheric pressure and air atmosphere. The chemical composition of the H-VTM was introduced in the reaction and the equilibrium module as input data. The amount of B2O3 was increased from 0.00% to 5.00% with a step size of 1.00%. The temperature was increased from 1000°C to 1600°C in a step of 50°C.The average compressive strength of H-VTM fluctuated significantly with the rise of B2O3. The compressive strength was 531 N/P without B2O3. The compressive strength grew significantly with the increase of B2O3 content, peaking at 857 N/P with B2O3 content at 2.00%. As the B2O3 ratio further increases, the compressive strength dropped sharply, reaching its lowest point at 356 N/P with B2O3 ratio at 5.00%.In Figure6, at the same mass ratio of B2O3, the amount of liquid phase in sintering continuously increased with the increase of temperature, especially when the temperature exceeded 1210°C. At the same temperature, the amount of liquid phase of the sample with a high percentage of boron oxide was significantly more than the sample with lower ones. When the ratios of B2O3 were 0.00%, 1.00%, 2.00%, 3.00%, 4.00%, and 5.00%, the ratios of the liquid phase were 15.74%, 25.32%, 32.43%, 39.42%, 44.73%, and 51.36%, respectively. B2O3 could react with CaO, SiO2, MgO, and Al2O3 to form mineral phases with a low melting point. Besides, the melting point of B2O3 is low (450°C). Therefore, B2O3 initially transformed into the liquid phase. Overheating reduced the liquid viscosity and quickly form a certain amount of liquid phase, which was beneficial for diffusion during sintering. As a result, the amount of liquid phase of H-VTM improved with the increase of the ratio of B2O3.Figure 6
The volume of liquid phase with different B2O3 contents.


## 3.2. Microstructure of H-VTM with Different B2O3 Contents

The X-ray diffraction (XRD) is used to investigate the phases changes of the sintered samples. As is shown in Figure7, after heating samples at 1250°C for 30 min, by contrast, the diffraction peaks of Fe3O4 and CaO·Fe2O3 increased as the B2O3 mass ratio increased.Figure 7
XRD patterns of H-VTM-sintered samples with different B2O3 contents. 1: Fe2O3; 2: Fe3O4; 3: CaO·Fe2O3; 4: 2CaO·SiO2.The addition of B2O3 could inhibit the formation of 2CaO·SiO2 and promote the formation of CaO·Fe2O3. This scene is shown in Figure 8. Before 1100oC, the 2CaO·SiO2 content grew continuously with the increase of the B2O3 mass ratio. It reached its highest value when the addition amount of B2O3 is 5.00% at 1100°C.Figure 8
2CaO·SiO2 contents in the samples with different B2O3 contents.The microstructures of the samples with different content of B2O3 were observed using a scanning electron microscope (SEM) equipped with an energy-dispersive X-ray spectroscope (EDS). In Figure 9, as the amount of B2O3 increased, the bonding phase (the bright white part) in the H-VTM-sintered sample was more evenly distributed in the microstructure. When the mass ratio of B2O3 was 2.00%, the number of pores in the sintered sample decreased significantly, but larger diameter pore began to appear because the increasing B2O3 could promote the formation of liquid phase in H-VTM. The liquid phase started to shrink during the cooling process and then came the pore structure. This phenomenon also could explain the inflexion point of the compressive strength of H-VTM and the increase of the number of internal pores, resulting in the formation of H-VTM microstructure and the decrease of compressive strength.Figure 9
SEM of H-VTM with different B2O3 contents.
(a)(b)(c)(d)(e)(f)The scanning results of the sintered sample with 5.00% B2O3 are shown in Figure 10. Hematite was mainly distributed in a fish-bone shape. Silicon, calcium, and aluminium were combined and distributed in the bright white area and formed a bonding phase. Titanium and iron were concentrated, producing the main iron base phase.Figure 10
Surface scanning of the H-VTM sample with 5% B2O3.SEM-EDS was carried out on the cooled sample with 5.00% B2O3, as is shown in Figure 11. The EDS analysis results from point A to C with 5.00% B2O3 are shown in Table 2. The main element at point A is Fe, which accounts for 67.29%. O, Si, Ca, and other elements were almost nonexistent, which indicates that the main object is hematite or magnetite. The main elements at point B are O and Fe, and the contents of Si, Ca, and B are 6.14%, 14.35%, and 7.73%, respectively. Therefore, the primary material of the point B is ferrite, silicate, or borate, forming a bonding phase. Boron is abundant in the bonding material phase. As the B2O3 mass ratio increased, the perovskite phase decreased and calcium ferrite and calcium borate gradually increased, while calcium silicate gradually decreased. These results indicated that B2O3 worked together with CaO and SiO2 to form the low-melting-point substance CaO·2B2O3 (melting point of 989°C), CaO·B2O3·2SiO2 (melting point of 957°C), and 2CaO·B2O3·SiO2 (melting point of 901°C). Thus, the production of calcium silicate decreases, and this result is consistent with XRD.Figure 11
SEM-EDS of the sample with 5% B2O3.Table 2
SEM-EDS analysis of the sample with 5.00% B2O3 (wt%).
PointBOFeSiCaTiMgAlA1.0124.2967.290.120.451.981.000.37B7.7337.6123.836.1414.351.131.642.66C6.2536.4128.715.7713.341.231.822.56


## 4. Conclusions

The assimilation characteristics, melting temperature, fluidity of the liquid phase, compressive strength of the bonding phase, and microstructure of H-VTM with different B2O3 were studied through different methods:B2O3 reduces the assimilation temperature of H-VTM and enhances its assimilation characteristics. As the amount of B2O3 increases, the melting temperature of H-VTM decreases, as well as LBPI. The addition of B2O3 can increase the amount of liquid phase and enhance the fluidity of the liquid phase.B2O3 (<2.00%) improves the bonding phase strength of sintering samples, but the diameter of the pore in H-VTM enlarges when the amount of B2O3 is over 2.00% and the number of the pore increase. Thus, the H-VTM microstructure becomes more porous, and its compressive strength decreases.Boron and calcium-magnesium-aluminium concentrated in the bonding phase can reduce the formation of calcium silicate and perovskite in the mixed samples of vanadium-titanium and hematite.



---