# Electrochemical Detection of Sequence-Specific DNA with the Amplification of Gold Nanoparticles

Authors: Yuzhong Zhang; Zhen Wang; Yuehong Wang; Lei Huang; Wei Jiang; Mingzhu Wang
Journal: International Journal of Electrochemistry
 (2011)

---

## Abstract

A sensitive electrochemical DNA biosensor was prepared based on mercaptoacetic acid (MAA)/gold nanoparticles (AuNPs) modified electrode. Probe DNA (NH2-DNA) was covalently linked to the carboxyl group of MAA in the presence of 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride (EDC) and N-hydroxyl-succinimide (NHS). Scanning electron microscopy (SEM) and electrochemical impedance spectra (EIS) were used to investigate the film assembly process. The DNA hybridization events were monitored by differential pulse voltammetry (DPV), and adriamycin was used as the electrochemical indicator. Also the factors influencing the performance of the DNA hybridization were investigated in detail. Under the optimal conditions, the signal was linearly changed with target DNA concentration increased from 5.0 × 10−13 to 1.0 × 10−9 M and had a detection limit of 1.7 × 10−13 M (signal/noise ratio of 3). In addition, the DNA biosensor showed good reproducibility and stability during DNA assay.


---

## Body

## 1. Introduction

Nowadays, specific sequences DNA detection has become a most important research field due to its application in disease diagnosis, drug screening, epidemic prevention, and environmental protection [1–3]. Many methods have been used for DNA detection including optics [4, 5], piezoelectricity [6], surface plasmon resonance spectroscopy [7], and electrochemistry [8–11]. Among them, it should be noted that electrochemical DNA sensor is a promising candidate because of its simple, rapid, inexpensive, high sensitivity and selectivity.AuNPs are well-known low-dimensional functional materials with large surface-to-volume ratios and biocompatibility with biosystem. So it is often used for DNA biosensor material. Zhang et al. [12] and Zhang et al. [13, 14] have fabricated some AuNPs-based electrochemical DNA sensors. Wang and his coworkers have invented a DNA biosensor based on amplified voltammetric detection of DNA hybridization via oxidation of ferrocene caps on gold nanoparticle/streptavidin conjugates [15]. Abouzar and his coworkers have developed a label-free electrical detection of DNA hybridization functionalized with AuNPs [16]. Our groups have fabricated several DNA biosensor based on AuNPs amplification [17–19]. Castañeda et al. have a review on electrochemical sensing of DNA using AuNPs [20].In the present paper, we fabricate an electrochemical DNA biosensor for detection of E. coli sequence with the amplification of gold nanoparticles. AuNPs were firstly electrodeposited on the surface of the gold electrode. And the modified AuNPs were used to increase the electrode surface area for more binding amount of MAA so as to enhance the immobilization amount of probe DNA. DPV was used to monitor DNA hybridization event by measurement of the intercalated adriamycin. This DNA biosensor shows a higher sensitivity and selectivity.


## 2. Experiment

### 2.1. Materials

Adriamycin, MAA, sodium dodecyl sulfate (SDS), EDC, and NHS were purchased from Alfa Aesar (Tianjing, China). HAuCl4·4H2O was obtained from Shanghai Chemical Reagent Co., Ltd. Sodium hydroxide and Phosphate were obtained from Nanjing Chemical Reagent (Nanjing, China). Various oligonucleotides were purchased from Shanghai Sangon Bioengineering Technology & Services Co., Ltd. (Shanghai, China). And their sequences are as follows.Probe Sequence
5′-NH2-GAG CGG CGC AAC ATT TCA GGT CGA-3′.Complementary Sequence
5′-TCG ACC TGA AAT GTT GCG CCG CTC-3′.Noncomplementary Sequence
5′-AGC TGG ACT TTA CAA CGC GGC GAG-3′.Single-Base Mismatched Sequence
5′-TCG ACC TGA AAC GTT GCG CCG CTC-3′.Stock solutions of oligonucleotides were prepared with 0.01 M phosphate buffer solution (PBS, pH 7.40) and stored in a freezer. The following buffer solutions were used: hybridization buffer solution (0.1 M NaCl + 0.01 M PBS, pH 7.40) and electrochemical test solution (0.01 M PBS, pH 7.40). All chemicals were of analytical grade and used without further purification. All solutions were prepared with twice-quartz-distilled water.


### 2.2. Apparatus

All electrochemical measurements such as electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), and DPV were performed on a CHI 660A electrochemical workstation (Shanghai Chenhua Instruments Co., China). The three-electrode system was used in the experiment with bare gold electrode or modified electrode as working electrode, a saturated calomel electrode (SCE) as reference electrode and platinum wire as counter electrode. EIS was performed in 0.1 M KCl solution containing 5.0 mM K4Fe(CN)6/K3Fe(CN)6 (pH 7.40) with the frequency range between 0.1 and 100 kHz at the formal potential of 0.115 V. CV and DPV were carried out in a 10 mL electrochemical cell with 5 mL solutions, from which oxygen was removed by purging with high-purity nitrogen for 20 min, and a blanket of nitrogen was maintained over the solution during the measurements. The morphology of AuNPs was obtained by scanning electron microscopy (SEM) using a JEOLJSM-6700F microscope (Hitachi, Japan).


### 2.3. Preparation of ssDNA/MAA/AuNPs Modified Electrode

Prior to modification, the bare gold electrode was firstly polished to a mirror-like surface with gamma alumina suspensions (1.0μm, 0.25 μm and 0.05 μm, resp.). Then it was rinsed with twice-quartz-distilled water and cleaned ultrasonically sequentially in water and 95% ethanol for 3 min. Finally, the electrode was electrochemically cleaned between −0.3 and +1.55 V in 0.5 M H2SO4 until a stable CV was obtained.AuNPs electrochemical deposition was performed in 2.0 × 10−3 M HAuCl4/0.2 M KNO3 solution and electrodeposition time is 50 s at −250 mV (versus SCE). The electrode was denoted as AuNPs/Au. Then the AuNPs/Au electrode was immersed into a 10.0 mM MAA for 4 h to form MAA film through Au–S bond. The obtained electrode was denoted as MAA/AuNPs/Au.After the MAA/AuNPs/Au modified electrode was immersed in a mixture of 5.0 mM EDC and 8.0 mM NHS (pH 7.40) for 45 min, 8μL of 1.0 × 10−5 M probe DNA was dropped on the surface of MAA/AuNPs/Au and kept it for 12 h at the room temperature. Finally, the probe modified electrode was immersed into 0.1% SDS solution for 10 min to remove the unbound probe DNA. Thus the probe DNA modified electrode was prepared, and it was denoted ssDNA/MAA/AuNPs/Au.


### 2.4. Hybridization and Electrochemical Detection

The hybridization experiment was carried out by immersing the probe modified electrode into hybridization buffer solution containing different concentrations of target DNA for 25 min at 37°C. The hybridized electrode was then rinsed with PBS containing 0.1% SDS to remove the unhybridized target DNA. After that, it was incubated in 1.0 × 10−6 M adriamycin for 20 min, followed by rinsing with water and 0.01 M PBS for three times to remove physically absorbed adriamycin.The DNA hybridization was assessed with the DPV peak current of intercalated adriamycin in pH 7.0 PBS, and the concentration of complementary DNA was quantified by peak current of adriamycin (ΔI), which was subtracted from the reduction peak current generated at the ssDNA/MAA/AuNPs modified electrode (ΔI=Ids-DNA-Iss-DNA). DPV parameters were as follows: potential range: −0.45 ~−0.80 V; amplitude: 0.05 V; pulse width: 0.05 s; sample width: 0.0167 s; pulse period: 0.2 s; quiet time: 2 s. The schematic diagram of the DNA biosensor fabrication and electrochemical detection is illustrated in Scheme 1.Scheme 1
The schematic diagram of the procedure available for DNA biosensor fabrication and electrochemical detection.


## 2.1. Materials

Adriamycin, MAA, sodium dodecyl sulfate (SDS), EDC, and NHS were purchased from Alfa Aesar (Tianjing, China). HAuCl4·4H2O was obtained from Shanghai Chemical Reagent Co., Ltd. Sodium hydroxide and Phosphate were obtained from Nanjing Chemical Reagent (Nanjing, China). Various oligonucleotides were purchased from Shanghai Sangon Bioengineering Technology & Services Co., Ltd. (Shanghai, China). And their sequences are as follows.Probe Sequence
5′-NH2-GAG CGG CGC AAC ATT TCA GGT CGA-3′.Complementary Sequence
5′-TCG ACC TGA AAT GTT GCG CCG CTC-3′.Noncomplementary Sequence
5′-AGC TGG ACT TTA CAA CGC GGC GAG-3′.Single-Base Mismatched Sequence
5′-TCG ACC TGA AAC GTT GCG CCG CTC-3′.Stock solutions of oligonucleotides were prepared with 0.01 M phosphate buffer solution (PBS, pH 7.40) and stored in a freezer. The following buffer solutions were used: hybridization buffer solution (0.1 M NaCl + 0.01 M PBS, pH 7.40) and electrochemical test solution (0.01 M PBS, pH 7.40). All chemicals were of analytical grade and used without further purification. All solutions were prepared with twice-quartz-distilled water.


## 2.2. Apparatus

All electrochemical measurements such as electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), and DPV were performed on a CHI 660A electrochemical workstation (Shanghai Chenhua Instruments Co., China). The three-electrode system was used in the experiment with bare gold electrode or modified electrode as working electrode, a saturated calomel electrode (SCE) as reference electrode and platinum wire as counter electrode. EIS was performed in 0.1 M KCl solution containing 5.0 mM K4Fe(CN)6/K3Fe(CN)6 (pH 7.40) with the frequency range between 0.1 and 100 kHz at the formal potential of 0.115 V. CV and DPV were carried out in a 10 mL electrochemical cell with 5 mL solutions, from which oxygen was removed by purging with high-purity nitrogen for 20 min, and a blanket of nitrogen was maintained over the solution during the measurements. The morphology of AuNPs was obtained by scanning electron microscopy (SEM) using a JEOLJSM-6700F microscope (Hitachi, Japan).


## 2.3. Preparation of ssDNA/MAA/AuNPs Modified Electrode

Prior to modification, the bare gold electrode was firstly polished to a mirror-like surface with gamma alumina suspensions (1.0μm, 0.25 μm and 0.05 μm, resp.). Then it was rinsed with twice-quartz-distilled water and cleaned ultrasonically sequentially in water and 95% ethanol for 3 min. Finally, the electrode was electrochemically cleaned between −0.3 and +1.55 V in 0.5 M H2SO4 until a stable CV was obtained.AuNPs electrochemical deposition was performed in 2.0 × 10−3 M HAuCl4/0.2 M KNO3 solution and electrodeposition time is 50 s at −250 mV (versus SCE). The electrode was denoted as AuNPs/Au. Then the AuNPs/Au electrode was immersed into a 10.0 mM MAA for 4 h to form MAA film through Au–S bond. The obtained electrode was denoted as MAA/AuNPs/Au.After the MAA/AuNPs/Au modified electrode was immersed in a mixture of 5.0 mM EDC and 8.0 mM NHS (pH 7.40) for 45 min, 8μL of 1.0 × 10−5 M probe DNA was dropped on the surface of MAA/AuNPs/Au and kept it for 12 h at the room temperature. Finally, the probe modified electrode was immersed into 0.1% SDS solution for 10 min to remove the unbound probe DNA. Thus the probe DNA modified electrode was prepared, and it was denoted ssDNA/MAA/AuNPs/Au.


## 2.4. Hybridization and Electrochemical Detection

The hybridization experiment was carried out by immersing the probe modified electrode into hybridization buffer solution containing different concentrations of target DNA for 25 min at 37°C. The hybridized electrode was then rinsed with PBS containing 0.1% SDS to remove the unhybridized target DNA. After that, it was incubated in 1.0 × 10−6 M adriamycin for 20 min, followed by rinsing with water and 0.01 M PBS for three times to remove physically absorbed adriamycin.The DNA hybridization was assessed with the DPV peak current of intercalated adriamycin in pH 7.0 PBS, and the concentration of complementary DNA was quantified by peak current of adriamycin (ΔI), which was subtracted from the reduction peak current generated at the ssDNA/MAA/AuNPs modified electrode (ΔI=Ids-DNA-Iss-DNA). DPV parameters were as follows: potential range: −0.45 ~−0.80 V; amplitude: 0.05 V; pulse width: 0.05 s; sample width: 0.0167 s; pulse period: 0.2 s; quiet time: 2 s. The schematic diagram of the DNA biosensor fabrication and electrochemical detection is illustrated in Scheme 1.Scheme 1
The schematic diagram of the procedure available for DNA biosensor fabrication and electrochemical detection.


## 3. Results and Discussion

### 3.1. Electrochemical Impedance Spectroscopy at Different Modified Electrode

Impedance spectroscopy is an effective method for probing the surface features of the modified electrode. In EIS, the semicircle part at higher frequencies corresponds to the electron transfer limited process or the electron transfer resistance (Ret). The linear sect at lower frequencies shows a controlled diffusion process. Figure 1 compares the Nyquist plots of 5.0 mM K4Fe(CN)6/K3Fe(CN)6 at the different modified electrodes. When AuNPs were electrodeposited on the surface of the gold electrode (curve b), the Ret was decreased in contrast to the bare gold electrode (curve a). The results could be rationalized by improved electron transfer kinetics of redox probe on AuNPs modified electrode. The assembly of MAA monolayer on electrode surface induced a larger Ret (curve c) as compared with that of AuNPs electrode due to the electrostatic repulsion between the negative MAA and K4Fe(CN)6/K3Fe(CN)6. When the MAA/AuNPs/Au surface was activated with EDC and NHS, the Ret was evidently decreased because the content of carboxyl group was decreased (curve d). When the probe DNA was covalently immobilized on the electrode surface, the Ret is obviously increased because of the strong electrostatic repulsion between the K4Fe(CN)6/K3Fe(CN)6 molecules and the negative-charged phosphate skeletons of DNA (curve e). After hybridization of the probe DNA with 1.0 × 10−10 M complementary ssDNA, Ret was obviously increased (curve f). Therefore, this impedance change indicated that modification and DNA hybridization successfully occurred on the electrode surface.Figure 1
Nyquist plots obtained at different modified electrode. (a) Bare gold electrode, (b) AuNPs, (c) MAA/AuNPs, (d) activated MAA/AuNPs, (e) ss-DNA/MAA/AuNPs, and (f) ds-DNA/MAA/AuNPs modified electrodes. The supporting electrolyte was 0.1 M KCl solution containing 5.0 mM K4Fe(CN)6/K3Fe(CN)6.


### 3.2. Optimization of DNA Assay Conditions

It is reported that the morphology, magnitude, and distribution of AuNPs could be controlled through controlling deposition time or HAuCl4 concentrations [21]. In order to obtain an optimization for DNA immobilization and hybridization, in this work, magnitude and distribution of AuNPs was performed by changing deposition time and keeping HAuCl4 concentrations a constant. Two different methods (SEM, DPV) were used to investigate the optimization of Au deposition time, respectively.Figure2(A) shows SEM images of AuNPs at different periods of deposition time. It can be observed that morphology and distribution of AuNPs was depended on deposition time. When deposition time was 50 s, AuNPs are about 10 nm and have the same size (b), when the deposition time reached 110 s, a large number of gold clusters were found and lead to a very rough surface (c). Therefore, 50 s was the suitable for AuNPs preparation from the views of uniform size, higher density, and good shape.(A) SEM images of AuNPs at various deposition time. (a) 0, (b) 50 s, (c) 110 s, Deposition potential is −250 mV (versus SCE). (B) DPV responses of adriamycin dependence of deposition time. Electrochemical deposition was performed in 3.0 mM HAuCl4 at various times (t=0,8,16,24,32,40,48,56, and 64 s). DPV measurement was performed in 0.01 M PBS (pH 7.40) containing 1.0 × 10−6 M adriamycin. DPV parameters were as follows: potential range: −0.45 ~−0.80 V; amplitude: 0.05 V; pulse width: 0.05 s; sample width: 0.0167 s; pulse period: 0.2 s; quiet time: 2 s.The characteristic of AuNPs at different deposition time was investigated by DPV using adriamycin as electroactive indicator. Figure2(B) shows the plot of the peak currents of adriamycin dependence of deposition time. It could be observed that peak current increased as deposition time from 0 to 50 s, and the peak current decreased slightly when the deposition time exceeded 50 s. So 50 s was selected as the optimal deposition time.The amount of probe DNA immobilization on the electrode surface is an important factor because the amount of probe DNA directly influences the sensitivity of a DNA biosensor [22]. Figure 3(a) shows the peak current of adriamycin before and after hybridization dependence of probe DNA amount. From Figure 3(a), we can observe the peak current of adriamycin gradually increased with the amount of probe DNA from 3 to 8 μL, and a slight decrease when the amount of probe DNA is over 8 μL. Thus, 8 μL probe DNA was selected in our experiments.(a) Peak current of adriamycin (ΔI) dependence of amounts of probe DNA. The concentration of complementary target DNA is 1.0 × 10−10 M; DPV parameters were the same as in Figure 2(B). (b) Effect of accumulation time on the DPV signals of adriamycin. The concentration of adriamycin is 1.0 × 10−6 M; DPV parameters were the same as in Figure 2(B). (c) DPV signals of adriamycin dependence on DNA hybridization time. The concentration of adriamycin is 1.0 × 10−6 M; the concentration of complementary target DNA is 1.0 × 10−10 M. DPV parameters were the same as in Figure 2(B).
(a)(b)(c)The accumulation time of electrochemical indicator is another factor for sensitivity of DNA biosensor. Figure3(b) shows the reduction peak currents of adriamycin dependence of the accumulation time. It could be seen that the peak current increased significantly with the increasing accumulation time from 5 to 20 min. When the accumulation time is higher than 20 min, the peak current of adriamycin keeps constant relatively. Therefore, 20 min was selected as the optimum accumulation time.Figure3(c) shows the peak current of adriamycin dependence of the hybridization time. From Figure 3(c), it could be seen that the reduction peak currents of adriamycin increased significantly as the hybridization time increased from 5 to 25 min and keep constant after 25 min. This indicated that the hybridization reaction was completed after 25 min. From a view of the sensitivity and assay time, 25 min was generally used for hybridization time.


### 3.3. Amplification of AuNPs

Could the application of the gold nanoparticles enhance the immobilization capacity of probe DNA and amplify signal of DNA hybridization? In this paper, we fabricated two different sensors: one is a sensor containing AuNPs, and another containing no AuNPs. The electrochemical investigation was performed as experiment Section2.4, and the results were shown in Figure 4. It could be observed that the sensor containing AuNPs has a large signal (Figure 4(A): 10.16 × 10−7 A) compared with the sensor containing no AuNPs (Figure 4(B): 2.29 × 10−7 A). These results suggested that the immobilization capacity of probe DNA and hybridization signal improved greatly in the presence of AuNPs.(A) DPV responses obtained for ss-DNA/MAA/AuNPs/Au (a), hybridized with 1.0 × 10−10 M complementary DNA (b). (B) DPV responses obtained for the ss-DNA/MAA/Au (c), hybridized with 1.0 × 10−10 M complementary DNA (d). Experiment condition: accumulation time of adriamycin: 20 min; hybridization time: 25 min. DPV parameters were the same as in Figure 2(B).


### 3.4. Selectivity of the DNA Biosensor

Differentiation of single mismatches is of significant interest for a variety of important applications. In this paper, the selectivity of the DNA biosensor was also evaluated by using single-base mismatch, no complementary and complementary DNA sequences. As is shown in Figure5, it could be observed that the response of single-base mismatch sequence has a significant difference with that of complementary sequence. These results indicated that this DNA biosensor can distinguish single-base mismatch DNA sequence.Figure 5
The histograms of the peak current difference (ΔI) of adriamycin versus different DNA sequences (1.0 × 10−10 M): (A) noncomplementary sequence, (B) single-base mismatch sequence, (C) complementary sequence. Inset: DPV responses of adriamycin recorded at probe modified electrode (a) and after hybridization with 1.0 × 10−10 M noncomplementary sequence (b); 1.0 × 10−10 M single-base mismatch sequence (c); 1.0 × 10−10 M complementary sequence (d). Accumulation time of adriamycin: 20 min; Hybridization time: 25 min. DPV parameters were the same as in Figure 2(B).


### 3.5. Analytical Performance

Under the optimal conditions, the analytical performance of the DNA biosensor was investigated using the immobilized probe DNA to hybridize with the different concentrations of the complementary sequence. Figure6 shows the DPVs records of intercalated adriamycin at various complementary oligonucleotides concentrations. It could be observed that the peak currents of adriamycin increased with increasing the concentration of complementary DNA, and the peak currents difference (ΔI) was linear with the logarithmic value of the concentration of the complementary DNA in the range from 5.0 × 10−13  to 1.0 × 10−9 M. The regression equation was ΔI (10−7 A) = 3.5518 log CDNA + 45.3301 (unit of C is M), and the regression coefficient (R) of the linear curve was 0.9979. The detection limit is 1.7 × 10−13 M (S/N = 3). Compared with reported sensors [23–25], this DNA biosensor showed higher sensitivity.Figure 6
DPV response of the intercalated adriamycin recorded for the probe DNA modified electrode that hybridized with various concentrations of complementary DNA: (a) 0 M; (b) 5.0 × 10−13 M; (c) 1.0 × 10−12 M; (d) 5.0 × 10−12 M; (e) 1.0 × 10−11 M; (f) 1.0 × 10−10 M; (g) 1.0 × 10−9 M. Inset: Peak current (ΔI) of the intercalated adriamycin versus logarithm of concentration of complementary DNA. Error bars show the standard deviations of measurements taken from three independent experiments. Accumulation time of adriamycin: 20 min; hybridization time: 25 min. The DPV parameters were the same as in Figure 2(B).


### 3.6. Reproducibility, Reusability, and Stability of the DNA Biosensor

The reproducibility of biosensor is a very important factor for their application. Four DNA sensors were fabricated independently under the same conditions and used to detect 1.0 × 10−10 M complementary DNA. And the reduction peak currents of adriamycin were 1.217 × 10−6 A, 1.258 × 10−6 A, 1.259 × 10−6 A, and 1.227 × 10−6 A, respectively. The average value was 1.2402×10-6 A, and the relative standard deviation (RSD) was 2.15%.The reusability of the DNA biosensor was investigated by immersing hybridized electrodes in hot water (80°C) for 5–10 min to make ds-DNA into ss-DNA via thermal denaturation. The renew sensor was used to test 1.0 × 10−10 M complementary DNA and found that the fifth regenerated sensor has 84.7% response of the initial sensor (initial: 1.24 × 10−6 A, final: 1.05 × 10−6 A). This result indicated the proposed DNA biosensor had a good reusability.The stability of the biosensor was also examined. The DNA sensor was stored in a freezer at 4°C for two weeks, and no apparent change about the peak current of adriamycin was observed.


## 3.1. Electrochemical Impedance Spectroscopy at Different Modified Electrode

Impedance spectroscopy is an effective method for probing the surface features of the modified electrode. In EIS, the semicircle part at higher frequencies corresponds to the electron transfer limited process or the electron transfer resistance (Ret). The linear sect at lower frequencies shows a controlled diffusion process. Figure 1 compares the Nyquist plots of 5.0 mM K4Fe(CN)6/K3Fe(CN)6 at the different modified electrodes. When AuNPs were electrodeposited on the surface of the gold electrode (curve b), the Ret was decreased in contrast to the bare gold electrode (curve a). The results could be rationalized by improved electron transfer kinetics of redox probe on AuNPs modified electrode. The assembly of MAA monolayer on electrode surface induced a larger Ret (curve c) as compared with that of AuNPs electrode due to the electrostatic repulsion between the negative MAA and K4Fe(CN)6/K3Fe(CN)6. When the MAA/AuNPs/Au surface was activated with EDC and NHS, the Ret was evidently decreased because the content of carboxyl group was decreased (curve d). When the probe DNA was covalently immobilized on the electrode surface, the Ret is obviously increased because of the strong electrostatic repulsion between the K4Fe(CN)6/K3Fe(CN)6 molecules and the negative-charged phosphate skeletons of DNA (curve e). After hybridization of the probe DNA with 1.0 × 10−10 M complementary ssDNA, Ret was obviously increased (curve f). Therefore, this impedance change indicated that modification and DNA hybridization successfully occurred on the electrode surface.Figure 1
Nyquist plots obtained at different modified electrode. (a) Bare gold electrode, (b) AuNPs, (c) MAA/AuNPs, (d) activated MAA/AuNPs, (e) ss-DNA/MAA/AuNPs, and (f) ds-DNA/MAA/AuNPs modified electrodes. The supporting electrolyte was 0.1 M KCl solution containing 5.0 mM K4Fe(CN)6/K3Fe(CN)6.


## 3.2. Optimization of DNA Assay Conditions

It is reported that the morphology, magnitude, and distribution of AuNPs could be controlled through controlling deposition time or HAuCl4 concentrations [21]. In order to obtain an optimization for DNA immobilization and hybridization, in this work, magnitude and distribution of AuNPs was performed by changing deposition time and keeping HAuCl4 concentrations a constant. Two different methods (SEM, DPV) were used to investigate the optimization of Au deposition time, respectively.Figure2(A) shows SEM images of AuNPs at different periods of deposition time. It can be observed that morphology and distribution of AuNPs was depended on deposition time. When deposition time was 50 s, AuNPs are about 10 nm and have the same size (b), when the deposition time reached 110 s, a large number of gold clusters were found and lead to a very rough surface (c). Therefore, 50 s was the suitable for AuNPs preparation from the views of uniform size, higher density, and good shape.(A) SEM images of AuNPs at various deposition time. (a) 0, (b) 50 s, (c) 110 s, Deposition potential is −250 mV (versus SCE). (B) DPV responses of adriamycin dependence of deposition time. Electrochemical deposition was performed in 3.0 mM HAuCl4 at various times (t=0,8,16,24,32,40,48,56, and 64 s). DPV measurement was performed in 0.01 M PBS (pH 7.40) containing 1.0 × 10−6 M adriamycin. DPV parameters were as follows: potential range: −0.45 ~−0.80 V; amplitude: 0.05 V; pulse width: 0.05 s; sample width: 0.0167 s; pulse period: 0.2 s; quiet time: 2 s.The characteristic of AuNPs at different deposition time was investigated by DPV using adriamycin as electroactive indicator. Figure2(B) shows the plot of the peak currents of adriamycin dependence of deposition time. It could be observed that peak current increased as deposition time from 0 to 50 s, and the peak current decreased slightly when the deposition time exceeded 50 s. So 50 s was selected as the optimal deposition time.The amount of probe DNA immobilization on the electrode surface is an important factor because the amount of probe DNA directly influences the sensitivity of a DNA biosensor [22]. Figure 3(a) shows the peak current of adriamycin before and after hybridization dependence of probe DNA amount. From Figure 3(a), we can observe the peak current of adriamycin gradually increased with the amount of probe DNA from 3 to 8 μL, and a slight decrease when the amount of probe DNA is over 8 μL. Thus, 8 μL probe DNA was selected in our experiments.(a) Peak current of adriamycin (ΔI) dependence of amounts of probe DNA. The concentration of complementary target DNA is 1.0 × 10−10 M; DPV parameters were the same as in Figure 2(B). (b) Effect of accumulation time on the DPV signals of adriamycin. The concentration of adriamycin is 1.0 × 10−6 M; DPV parameters were the same as in Figure 2(B). (c) DPV signals of adriamycin dependence on DNA hybridization time. The concentration of adriamycin is 1.0 × 10−6 M; the concentration of complementary target DNA is 1.0 × 10−10 M. DPV parameters were the same as in Figure 2(B).
(a)(b)(c)The accumulation time of electrochemical indicator is another factor for sensitivity of DNA biosensor. Figure3(b) shows the reduction peak currents of adriamycin dependence of the accumulation time. It could be seen that the peak current increased significantly with the increasing accumulation time from 5 to 20 min. When the accumulation time is higher than 20 min, the peak current of adriamycin keeps constant relatively. Therefore, 20 min was selected as the optimum accumulation time.Figure3(c) shows the peak current of adriamycin dependence of the hybridization time. From Figure 3(c), it could be seen that the reduction peak currents of adriamycin increased significantly as the hybridization time increased from 5 to 25 min and keep constant after 25 min. This indicated that the hybridization reaction was completed after 25 min. From a view of the sensitivity and assay time, 25 min was generally used for hybridization time.


## 3.3. Amplification of AuNPs

Could the application of the gold nanoparticles enhance the immobilization capacity of probe DNA and amplify signal of DNA hybridization? In this paper, we fabricated two different sensors: one is a sensor containing AuNPs, and another containing no AuNPs. The electrochemical investigation was performed as experiment Section2.4, and the results were shown in Figure 4. It could be observed that the sensor containing AuNPs has a large signal (Figure 4(A): 10.16 × 10−7 A) compared with the sensor containing no AuNPs (Figure 4(B): 2.29 × 10−7 A). These results suggested that the immobilization capacity of probe DNA and hybridization signal improved greatly in the presence of AuNPs.(A) DPV responses obtained for ss-DNA/MAA/AuNPs/Au (a), hybridized with 1.0 × 10−10 M complementary DNA (b). (B) DPV responses obtained for the ss-DNA/MAA/Au (c), hybridized with 1.0 × 10−10 M complementary DNA (d). Experiment condition: accumulation time of adriamycin: 20 min; hybridization time: 25 min. DPV parameters were the same as in Figure 2(B).


## 3.4. Selectivity of the DNA Biosensor

Differentiation of single mismatches is of significant interest for a variety of important applications. In this paper, the selectivity of the DNA biosensor was also evaluated by using single-base mismatch, no complementary and complementary DNA sequences. As is shown in Figure5, it could be observed that the response of single-base mismatch sequence has a significant difference with that of complementary sequence. These results indicated that this DNA biosensor can distinguish single-base mismatch DNA sequence.Figure 5
The histograms of the peak current difference (ΔI) of adriamycin versus different DNA sequences (1.0 × 10−10 M): (A) noncomplementary sequence, (B) single-base mismatch sequence, (C) complementary sequence. Inset: DPV responses of adriamycin recorded at probe modified electrode (a) and after hybridization with 1.0 × 10−10 M noncomplementary sequence (b); 1.0 × 10−10 M single-base mismatch sequence (c); 1.0 × 10−10 M complementary sequence (d). Accumulation time of adriamycin: 20 min; Hybridization time: 25 min. DPV parameters were the same as in Figure 2(B).


## 3.5. Analytical Performance

Under the optimal conditions, the analytical performance of the DNA biosensor was investigated using the immobilized probe DNA to hybridize with the different concentrations of the complementary sequence. Figure6 shows the DPVs records of intercalated adriamycin at various complementary oligonucleotides concentrations. It could be observed that the peak currents of adriamycin increased with increasing the concentration of complementary DNA, and the peak currents difference (ΔI) was linear with the logarithmic value of the concentration of the complementary DNA in the range from 5.0 × 10−13  to 1.0 × 10−9 M. The regression equation was ΔI (10−7 A) = 3.5518 log CDNA + 45.3301 (unit of C is M), and the regression coefficient (R) of the linear curve was 0.9979. The detection limit is 1.7 × 10−13 M (S/N = 3). Compared with reported sensors [23–25], this DNA biosensor showed higher sensitivity.Figure 6
DPV response of the intercalated adriamycin recorded for the probe DNA modified electrode that hybridized with various concentrations of complementary DNA: (a) 0 M; (b) 5.0 × 10−13 M; (c) 1.0 × 10−12 M; (d) 5.0 × 10−12 M; (e) 1.0 × 10−11 M; (f) 1.0 × 10−10 M; (g) 1.0 × 10−9 M. Inset: Peak current (ΔI) of the intercalated adriamycin versus logarithm of concentration of complementary DNA. Error bars show the standard deviations of measurements taken from three independent experiments. Accumulation time of adriamycin: 20 min; hybridization time: 25 min. The DPV parameters were the same as in Figure 2(B).


## 3.6. Reproducibility, Reusability, and Stability of the DNA Biosensor

The reproducibility of biosensor is a very important factor for their application. Four DNA sensors were fabricated independently under the same conditions and used to detect 1.0 × 10−10 M complementary DNA. And the reduction peak currents of adriamycin were 1.217 × 10−6 A, 1.258 × 10−6 A, 1.259 × 10−6 A, and 1.227 × 10−6 A, respectively. The average value was 1.2402×10-6 A, and the relative standard deviation (RSD) was 2.15%.The reusability of the DNA biosensor was investigated by immersing hybridized electrodes in hot water (80°C) for 5–10 min to make ds-DNA into ss-DNA via thermal denaturation. The renew sensor was used to test 1.0 × 10−10 M complementary DNA and found that the fifth regenerated sensor has 84.7% response of the initial sensor (initial: 1.24 × 10−6 A, final: 1.05 × 10−6 A). This result indicated the proposed DNA biosensor had a good reusability.The stability of the biosensor was also examined. The DNA sensor was stored in a freezer at 4°C for two weeks, and no apparent change about the peak current of adriamycin was observed.


## 4. Conclusions

A simple and sensitive electrochemical DNA biosensor based on ss-DNA/MAA/AuNPs modified electrode was fabricated. AuNPs could enhance the immobilization capacity of probe DNA and amplify electrochemical signal. This DNA biosensor exhibited excellent selectivity and stability.



---

*Source: 619782-2011-05-29.xml*