# Enhanced Nanohydroxyapatite Formation Using a Hydrolyzed Gelatin

Authors: Ding Ding; Tengfei Yu; Weijie Zhang; Wei Liu; Yaqin Huang
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Hydroxyapatite (HAP) nanoparticles were synthesized at room temperature using hydrolyzed gelatin (HG) as an additive. The crystallinity of HAP particles can be effectively controlled by adjusting the concentration of HG additive and the pH value of reaction system. The synthesized product was analyzed by Fourier transform infrared (FTIR) spectrometer, energy dispersive spectrometer (EDS), X-ray diffractometry (XRD), and transmission electron microscope (TEM). Meanwhile, it was proved that, with HG additive, HAP can be prepared with the calcium-phosphorus ratio of not only 1.67 but also 1.50. Conventionally, HAP particles need to be synthesized at high temperature with iCa/P = 1.67. Therefore, we believe that this study provides a novel strategy for the preparation of nano-HAP.


---

## Body

## 1. Introduction

Hydroxyapatite (HAP) has attracted much attention recently in the field of bioengineering [1], especially as a bone substitute material due to its biological compatibility and bone conduction. A variety of methods have been developed to synthesize HAP nanoparticles [2–7], such as phase transformation, chemical deposition, hydrothermal, and microemulsion methods. Researchers found that HAP crystal growth depended greatly on the properties of the starting solution, and the morphology of the HAP crystals could be affected by the initial Ca/P ratio (iCa/P). Conventionally, pure HAP particles can be synthesized at the higher temperature with iCa/P = 1.67 [8]. Compared to these artificially synthesized particles, HAP particles obtained from natural bone exhibit better mechanical and biological properties [9]. This biomineralization process involves interactions between organic natural polymer and inorganic matter [10]. The functional groups of organic natural polymer can interact with calcium ions and promote nucleation via molecular recognition. The interaction between functional groups of organic natural polymer and ions in the solution decreases the nucleation activation energy to some extent. Therefore, it is possible to obtain HAP nanoparticles at room temperature. Moreover, the addition of organic natural polymer can also promote the formation of structural organization through polymer-ion interactions. Therefore, we have developed a new strategy in this work to obtain HAP nanoparticles using some principles of biomineralization.Animal bone is an organic/inorganic composite with collagen and HAP. Previous studies reported that collagen promoted the formation of HAP in collagen fibrils scaffold [11]. Collagen is a kind of nature polymer. This inspired us to design a new way to prepare the nano-HAP using the hydrolyzed gelatin (HG) as a multifunctional additive. Our procedure for preparation of the nano-HAP is shown in Scheme 1.Scheme 1
Preparation of the nanohydroxyapatite using hydrolyzed gelatin as an additive.The rationales under our design include the following. (1) HG is the degradation product of collagen. It may enhance the formation of HAP as it has the similar amino acid composition to collagen. (2) HG is soluble in cold water, which facilitates HAP purification. (3) It is expected that the terminal functional groups, such as carboxyl group, hydroxyl oxygen atoms, and oxygen atoms from hydroxyl and carbonyl groups [7, 11], in HG molecules can interact with calcium ions. This kind of interactions may promote the formation of HAP and the mediation of the morphology in nano-HAP particles. (4) This additive may also reduce the aggregation of the particles and induce the formation of certain morphology due to the three-dimensional conformation formed by polypeptide chains in the HG solution. (5) HG is also commercially available and environmentally friendly. This report provides a detailed description of this novel nano-HAP synthesis using HG as a functional additive.


## 2. Experimental

### 2.1. Preparation

A certain amount of HG (2 wt%, 5 wt%, and 10 wt%) was firstly dissolved in Ca(NO3)2 aqueous solution, and then (NH4)2HPO4 aqueous solution was added slowly, until the ratio of n(Ca) to n(P) reached 1.67 (HAP-1, HAP-2, and HAP-3) and 1.50 (HAP-7). The pH (7.5, 8.5, 9.5, and 10.5) of the obtained solution was adjusted by adding varying amounts of NH3·H2O (HAP-4, HAP-5, HAP-6, and HAP-2). After stirring for 10 h at room temperature, the slurry was filtered, washed, and air-dried, and then the resulting white powders were obtained.The influence of the initial pH on HAP morphology was investigated under the condition of a fixed amount of HG (5 wt%) and the ratio of nCa/P (1.67). The effects of HG were studied by fixing the initial pH at 10.5 and the nCa/P ratio at 1.67. Finally, for the experiments designed to investigate the effects of the nCa/P ratio (1.50, 1.67), the initial pH was set at 10.5, and the amount of HG added was 5 wt%. As a comparison, a sample prepared without HG under similar conditions was synthesized. In order to remove hydrolyzed gelatin, HAP-2 was calcined at 700°C as the control sample (HAP-8). Table1 summarizes the experimental parameters for preparing the various HAP samples in this study.Table 1
Experimental parameters for preparing HAP samples.
Sample
HG(wt%)
Ca2+/P3+ (molar ratio)
pH
Calcined at 700°C
HAP-1
2
5 : 3
10.5
No
HAP-2
5
5 : 3
10.5
No
HAP-3
10
5 : 3
10.5
No
HAP-4
5
5 : 3
7.5
No
HAP-5
5
5 : 3
8.5
No
HAP-6
5
5 : 3
9.5
No
HAP-7
5
3 : 2
10.5
No
HAP-8
5
5 : 3
10.5
Yes


### 2.2. Characterization

The samples were characterized using scanning electron microscope (SEM; HITACHI S-4700), transmission electron microscope (TEM; JEM-100CX), X-ray diffractometry (XRD; D/Max2500VB2+/PC; Cu-Ka radiation at 40 kV with an X-ray diffractometer), and Fourier transform infrared spectrometer (FTIR; Nexus 670).


## 2.1. Preparation

A certain amount of HG (2 wt%, 5 wt%, and 10 wt%) was firstly dissolved in Ca(NO3)2 aqueous solution, and then (NH4)2HPO4 aqueous solution was added slowly, until the ratio of n(Ca) to n(P) reached 1.67 (HAP-1, HAP-2, and HAP-3) and 1.50 (HAP-7). The pH (7.5, 8.5, 9.5, and 10.5) of the obtained solution was adjusted by adding varying amounts of NH3·H2O (HAP-4, HAP-5, HAP-6, and HAP-2). After stirring for 10 h at room temperature, the slurry was filtered, washed, and air-dried, and then the resulting white powders were obtained.The influence of the initial pH on HAP morphology was investigated under the condition of a fixed amount of HG (5 wt%) and the ratio of nCa/P (1.67). The effects of HG were studied by fixing the initial pH at 10.5 and the nCa/P ratio at 1.67. Finally, for the experiments designed to investigate the effects of the nCa/P ratio (1.50, 1.67), the initial pH was set at 10.5, and the amount of HG added was 5 wt%. As a comparison, a sample prepared without HG under similar conditions was synthesized. In order to remove hydrolyzed gelatin, HAP-2 was calcined at 700°C as the control sample (HAP-8). Table1 summarizes the experimental parameters for preparing the various HAP samples in this study.Table 1
Experimental parameters for preparing HAP samples.
Sample
HG(wt%)
Ca2+/P3+ (molar ratio)
pH
Calcined at 700°C
HAP-1
2
5 : 3
10.5
No
HAP-2
5
5 : 3
10.5
No
HAP-3
10
5 : 3
10.5
No
HAP-4
5
5 : 3
7.5
No
HAP-5
5
5 : 3
8.5
No
HAP-6
5
5 : 3
9.5
No
HAP-7
5
3 : 2
10.5
No
HAP-8
5
5 : 3
10.5
Yes


## 2.2. Characterization

The samples were characterized using scanning electron microscope (SEM; HITACHI S-4700), transmission electron microscope (TEM; JEM-100CX), X-ray diffractometry (XRD; D/Max2500VB2+/PC; Cu-Ka radiation at 40 kV with an X-ray diffractometer), and Fourier transform infrared spectrometer (FTIR; Nexus 670).


## 3. Results and Discussion

Crystalline structures of HAP nanoparticles with various HG contents were confirmed by XRD measurements as shown in Figure1. The sample without HG exhibits different diffraction pattern from the standardized HAP. Poorly crystalline HAP phases formed as the HG content in the solution was greater than 5 wt%. The X-ray diffraction pattern of HAP-2 evidenced a much higher intensity for the (211), (310), and (231) peaks than the intensity of the HAP-1 peaks characteristic of HAP. This result can be attributed to a preferential growth of the HAP crystals in the (211), (310), and (231) directions due to the HG influence. However, with the increase of HG content, the formation of a large number of nuclei sufficiently depletes the concentration of calcium ions that are available for growth such that the crystals cannot grow very large. The preferred orientations of planes (002) and (310) were maintained in the sample series until HAP-2 and then fell precipitously as the HG content was increased to 10 wt%. The formation and growth of HAP crystals were greatly influenced by the excess amount of HG. At the same time, it has also been found that the intensity of the peaks at 2θ≈28° presents a rising tendency with the increase of HG content. It is well known that HAP contains two polymorphs: hexagonal and monoclinic. The hexagonal prism is related to the plane (102) (2θ≈28°) [12]. The result shows that HG can work well as a functional additive to promote the transformation of polymorphs. Therefore we speculate that when increasing the contents of HG, the monoclinic HAP polymorph would transform into the hexagonal one. These results indicate that the addition of HG is necessary for the synthesis of HAP.Figure 1
XRD patterns of (a) HAP-1, (b) HAP-2, (c) HAP-3, and (d) sample synthesized without HG.The effect of pH changes on and crystallization behavior of HAP was evaluated using X-ray diffraction analysis (Figure2). The characteristic peaks at 25.8°, 31.8°, 33.9°, and 39.8° correspond to the (002), (211), (202), and (310) diffractions of the standard HAP crystallites, respectively. At the pH of 7.5, the HAP phase is directly observed on XRD pattern by adding HG. The increased XRD peak intensity implies that the crystallinity of HAP increases with the increase of the pH value. And the intensity of peaks at 2θ≈28° presents decline tendency with the increase of the pH value. It shows that the polymorphs and the crystallinity of HAP can be changed by controlling the pH of the initial reaction, which results in altering the morphology and size of HAP.Figure 2
XRD patterns of the HAP with varying pH: (a) 7.5, (b) 8.5, (c) 9.5, and (d) 10.5.We also synthesized pure HAP nanoparticles using an initial Ca/P ratio of 1.50. The XRD patterns (Figure3) show the characteristic peaks similar to those of HAP-2. Normally, without HG as an additive, HAP could not be synthesized with the Ca/P ratio of 1.50. The amorphous calcium phosphate (TCP) precursor could be prepared by conventional chemical precipitation methods without HG with the ratio of 1.50 (HAP-7). In this work, we found that the HG was able to promote the formation of HAP with initial Ca/P molar ratio of 1.50. The impurity phases were inhibited by adding HG, demonstrating HG’s promotion of HAP formation. We speculate that HG can work well as a functional additive to reduce the transition enthalpy from TCP to HAP.Figure 3
XRD patterns of products with varying Ca/P molar ratio: (a) 1.50 (HAP-7) and (b) 1.67 (HAP-2).Figure4(a) shows the FTIR spectra of the sample HAP-2 synthesized with HG. In order to further understand the structure of the components and formation process of HAP, the FTIR spectra of the HG (Figure 4(b)) and HAP-8 (Figure 4(c)) are also shown as comparison. Both HAP-2 and HAP-8 have the absorption bands at 1036 cm−1, 565 cm−1, and 603 cm−1, confirming the presence of a phosphate group. Moreover, typical absorption bands for hydroxyl vibrational modes at 3572 cm−1 were also identified for both samples. It is noted that HAP-2 has the absorption band at 1638 cm−1, which is due to the presence of C=O in HG and a broad absorption band at 3572 cm−1 which represents overlapping peaks of amido and hydroxyl groups. Furthermore, the bands at 1421 cm−1 and 1456 cm−1 can be attributed to the existence of carboxylate, confirming the chemical bonding between HG and calcium ions. Compared to HAP-2, there are no absorption bands of C=O and carboxylate in HAP-8, which is the result of the removal of HG after calcination. Comparing with HAP-2 and HAP-8, the red shift of 1640 cm−1 band in HG was used to confirm the chemical bond formation between carboxyl ions in HG and HAP. It is believed that the red shift in the HAP-2 system is encouraged by the wagging vibration through the covalent bond formation with Ca2+ ions of HAP nanocrystals. Overall, the FTIR results are consistent with the XRD results.Figure 4
FTIR spectra of (a) HAP-2, (b) HG, and (c) HAP-8.The elemental composition and microstructure of HAP-2 and HAP-8 were investigated using EDS and TEM (Figure5). From the EDS analysis, we can easily identify the existence of oxygen, carbon, calcium, and phosphorus atoms in both HAP-2 (Figure 5(a)) and HAP-8 (Figure 5(b)). The relative ratio of calcium to phosphorus (Ca/P) is approximately 1.62, which is close to the initial set value of 1.67. The calcium deficiency may be due to the EDS measurement error or caused by the imperfect crystal lattice and the presence of additional phases. TEM images show that HAP-2 (Figure 5(c)) nanoparticles are generally spherical and the particles size is approximately 40–60 nm in diameter. Compared to HAP-2 (Figure 5(c)), the particle size of HAP-8 (about 30–100 nm, see Figure 5(d)) increased after the removal of HG on the surface, suggesting that HG also played an important role in the particle size control during the synthesis of HAP.Figure 5
EDS and TEM images of (a, c) HAP-2 and (b, d) HAP-8.
(a)
(b)
(c)
(d)Our findings may be explained by the molecular structure of the added gelatin. The molecular chain of hydrolyzed gelatin is composed of a series of amino acids and their telopeptides consist of many functional groups, such as carboxyl group, hydroxyl oxygen atom, and oxygen atoms from hydroxyl and carbonyl groups. Scheme2 shows the schematic representation of HAP microcrystal formation via terminal carboxyl group. As the calcium ions accumulate near the terminal carboxyl group and interact with it, thus, terminal carboxyl group must gain an overall positive charge. These positively charged areas may be attracted to negatively charged phosphate ions (PO4)3-, initiating the nucleation of HAP particles on the terminal of hydrolyzed gelatin chain [11, 13, 14]. The HG solution can provide more terminal carboxyl group for the selective attraction of calcium ions, which facilitates the nuclei formation of HAP. Moreover, HG can serve as a good dispersant to inhibit the conglomeration of HAP [15].Scheme 2
Possible mechanisms of HAP formation facilitated by hydrolyzed gelatin as an additive.


## 4. Conclusion

In contrast to conventional high temperature synthesis, we developed a synthesis protocol of the nanohydroxyapatite at room temperature using a hydrolyzed gelatin as an additive. The results demonstrated that the HG can promote the formation of HAP, even in the calcium-deficient case (Ca/P molar ratio of 1.50), and act as a dispersant and structure modifier as well. The amount of HG and the initial pH of the precursor reactants greatly influenced the nucleation and growth of HA nanocrystals. The as-synthesized HAP has uniformly spherical structure and an average particle size of about 40–60 nm. We believe the method described in this study is an efficient and facile strategy for the synthesis of well-dispersed nano-HAP.



---