# Study on the Retention and Distributions of the Copper-Based Preservative in Standing Tree Chinese Fir (Cunninghamia lanceolata)

Authors: Youhua Fan; Yong Wang; Ninghua Yu; Layun Deng; Zejun Chen
Journal: Advances in Materials Science and Engineering
 (2016)

---

## Abstract

In spite of some studies about the wood permeability and its improving measures, some progress has been made to study the diffusion and transmission of preservative solutions in standing trees. In the present study, copper- (Cu-) based preservative with other reagents is injected into the standing treeChinese fir using sap-flow method. The chemical compositions of the retreated woods are analyzed with Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The samples from different height positions are analyzed with scanning electron microscope (SEM) and atomic absorption spectroscopy (AAS) to obtain microstructures and preservative retention, respectively. The results indicate that the preservative solutions with lower concentrations are more conducive to diffusion and transmission in the wood. Moreover, the preservative retention at different height position has a greater concentration gradient for composite preservative solutions than those of the single preservative solutions. Solidified preservative particles are observed in xylem rays with SEM. The results of the present study provide some useful information for the functional design of the target wood products.


---

## Body

## 1. Introduction

Wood is a complex biomass material constituted mainly of cellulose, hemicelluloses, lignin, and an amount of extractives. It is widely used in building, furniture, paper pulp production, and so forth, for its advantages of high strength-weight ratio, impact resistance, and high process ability and especially for its sustainable and environmentally friendly natural properties [1]. Nevertheless, wood is a type of biological composite material, which is susceptible to outdoor environment. Defects such as decay and worm holes are some of the problems playing a significant role in efficient utilization of wood. Numerous attempts have been made to prolong its service life in previous studies [2–7]. Antiseptic treatment of wood is an effective method to prolong its service life using chromated copper arsenate (CCA) and alkaline copper quaternary (ACQ) [8–11]. However, impregnation modification needs fixed equipment investment, complex processes, high energy consumption, and environmental pollutions [12–14].Chinese fir is one of the most important commercial timber species in China, which accounts for more than 90% of the amount of deforestation. However, defects such as low hardness, low density, and easy decay are unfavorable factors to limit their application outdoors as structural materials. Therefore, antiseptic treatment is essential to prolong the service life and expand the applications scope of the fast-growing woods.Stumpage treatment dates back to the study of Iida et al. in 1990s [15], who firstly dyed the standing tree by using sap-flow method for effective utilization of lesser-used species. Those dyeing woods have been shown to grow comparatively large discoloration in the color. Subsequently, Zhao dyed fifty-eight species of hardwood and three species of softwood using the similar injection method [16]. Despite the deficiency of uneven dyeing, energy consumption is not needed in this method for the flow of the liquid in the tree by transpiration.The staining material can be transported from the bottom of the trunk to the top trunk of the standing tree by transpiration; inspired by the above ideas, copper- (Cu-) based preservatives with other reagents are injected into theChinese fir using the sap-flow method. The aim of our experiment is (i) to investigate the variation of preservative retention with the tree height and (ii) assess the effect of additive on the transmission and diffusion of the preservatives in the living trees.


## 2. Materials and Methods

### 2.1. Materials

Copper carbonate basic Cu2(OH)2·CO3, polyethylene glycol with molecular weight of 400, and ammonia water were obtained from Sinopharm Chemical Reagent Co., China. Double-distilled water was used in the experiments.


### 2.2. Data Collections

The entire data collection process was carried out according to the method of GB/T 23229-2009 [17]. The matureChinese fir trees, 20 years old, used for experiments were located at 28.12 degrees north and 113.06 degrees east. The experimental trees located more than 20 meters away from the watershed. The tree diameters at breast height (the height from the ground 1.4 m) were 20 cm to 24 cm with average of 2250 trees per hectare. The average temperature was 33.6°C during the experimental period from June to September.The copper carbonate basic was dissolved into ammonia water solution. The concentrations of the copper carbonate basic solutions were 2 wt.%, 4 wt.%, and 6 wt.%, respectively. The solutions were divided into two groups: one group was single preservative solution (Cu-NH) and the other was composite preservative solution via adding the additive, namely, polyethylene glycol, with its content of 5 wt.% (Cu-NH-PEG).The stumpage treatment procedures were carried out as follows. Firstly, two holes with diameter of 10 mm were drilled using a drill bit on the symmetric position of the trunk. The holes are 30 cm high above the ground. The holes were supposed to reach the tree pith. And then, the holes were connected with plastic bottles of preservative solutions using a Y type plastic pipe. The plastic bottle was kept above 80–100 cm from the ground. The total injection volume of the preservative solutions was 30 liters within four weeks. The target trees were cut down after 4–8 weeks of the treatment to solidify the preservative solutions. Three parallel experiments were carried out with the same concentration of the preservative solutions. The treatment procedures were shown in Figure1.Figure 1
Illustration of the stumpage modification procedures onChinese fir.


### 2.3. Sample Analysis and Characterization

In the experimental tree, sawdust was collected using sampling cone every two meters. Counting from the tree roots, the samples were identified as the first, second, third, and fourth part. At the same saw plane, four samples were collected for analysis of the preservative retention. The preservative retention (expressed as CuO) was analyzed according to the method of GB/T 23229-2009 [17]. The sampling schematic diagram for detecting preservative retention was shown in Figure 2.Figure 2
The sampling schematic diagram for detecting modifier retention.Sawdust was smashed by high speed mill, 100-mesh beads were used for X-ray diffraction (XRD) analysis by Rigaku D/max-2000PC, XRD scans operating with a Cu anode at 40 kV and 50 mA in the range of2
θ value between 10° and 70° with a speed of 8°/min. The chemical compositions of the resulting samples were investigated by Nicolet 6700 Fourier transform infrared spectrometer (FTIR) spectroscopy (Thermo Scientific). The surface compositions of the samples were determined by X-ray photoelectron spectroscopy (XPS). The XPS measurements were performed using an EscaLab 250Xi XPS spectrometer (Thermo-VG Scientific) with an Al Ka X-ray source (15 kV, 10 mA) and an analytical chamber with a base pressure of 10−6 Pa. All binding energies (Bes) were referred to the C 1s peak (284.6 eV) arising from surface hydrocarbons (or adventitious hydrocarbon). The samples used for SEM analysis were prepared by slip-propelled slicer from the experimental tree trunk every two meters. The morphologies were examined by TM 3000 scanning electron microscope (HITACHI), using an accelerating voltage of 15 kV.


## 2.1. Materials

Copper carbonate basic Cu2(OH)2·CO3, polyethylene glycol with molecular weight of 400, and ammonia water were obtained from Sinopharm Chemical Reagent Co., China. Double-distilled water was used in the experiments.


## 2.2. Data Collections

The entire data collection process was carried out according to the method of GB/T 23229-2009 [17]. The matureChinese fir trees, 20 years old, used for experiments were located at 28.12 degrees north and 113.06 degrees east. The experimental trees located more than 20 meters away from the watershed. The tree diameters at breast height (the height from the ground 1.4 m) were 20 cm to 24 cm with average of 2250 trees per hectare. The average temperature was 33.6°C during the experimental period from June to September.The copper carbonate basic was dissolved into ammonia water solution. The concentrations of the copper carbonate basic solutions were 2 wt.%, 4 wt.%, and 6 wt.%, respectively. The solutions were divided into two groups: one group was single preservative solution (Cu-NH) and the other was composite preservative solution via adding the additive, namely, polyethylene glycol, with its content of 5 wt.% (Cu-NH-PEG).The stumpage treatment procedures were carried out as follows. Firstly, two holes with diameter of 10 mm were drilled using a drill bit on the symmetric position of the trunk. The holes are 30 cm high above the ground. The holes were supposed to reach the tree pith. And then, the holes were connected with plastic bottles of preservative solutions using a Y type plastic pipe. The plastic bottle was kept above 80–100 cm from the ground. The total injection volume of the preservative solutions was 30 liters within four weeks. The target trees were cut down after 4–8 weeks of the treatment to solidify the preservative solutions. Three parallel experiments were carried out with the same concentration of the preservative solutions. The treatment procedures were shown in Figure1.Figure 1
Illustration of the stumpage modification procedures onChinese fir.


## 2.3. Sample Analysis and Characterization

In the experimental tree, sawdust was collected using sampling cone every two meters. Counting from the tree roots, the samples were identified as the first, second, third, and fourth part. At the same saw plane, four samples were collected for analysis of the preservative retention. The preservative retention (expressed as CuO) was analyzed according to the method of GB/T 23229-2009 [17]. The sampling schematic diagram for detecting preservative retention was shown in Figure 2.Figure 2
The sampling schematic diagram for detecting modifier retention.Sawdust was smashed by high speed mill, 100-mesh beads were used for X-ray diffraction (XRD) analysis by Rigaku D/max-2000PC, XRD scans operating with a Cu anode at 40 kV and 50 mA in the range of2
θ value between 10° and 70° with a speed of 8°/min. The chemical compositions of the resulting samples were investigated by Nicolet 6700 Fourier transform infrared spectrometer (FTIR) spectroscopy (Thermo Scientific). The surface compositions of the samples were determined by X-ray photoelectron spectroscopy (XPS). The XPS measurements were performed using an EscaLab 250Xi XPS spectrometer (Thermo-VG Scientific) with an Al Ka X-ray source (15 kV, 10 mA) and an analytical chamber with a base pressure of 10−6 Pa. All binding energies (Bes) were referred to the C 1s peak (284.6 eV) arising from surface hydrocarbons (or adventitious hydrocarbon). The samples used for SEM analysis were prepared by slip-propelled slicer from the experimental tree trunk every two meters. The morphologies were examined by TM 3000 scanning electron microscope (HITACHI), using an accelerating voltage of 15 kV.


## 3. Results and Discussion

### 3.1. XRD Analysis

XRD analysis is used to investigate the phase evolution of the preservative treated samples. The XRD pattern of the pureChinese fir powder is shown in Figure 3(a). The diffraction peaks observed at 16.1° and 22.5° are the characteristic diffraction peaks of the I type of wood cellulose (101) and (002) crystal plane in the structure cell. For the treated samples, the same diffraction peaks also appear in the corresponding position, which show that the addition of the modified agent does not destroy the crystalline form of the cellulose.Figure 3
XRD patterns of (a)Chinese firpowder; (b) the first part; (c) the second part; (d) the third part; (e) the fourth part of the 2% Cu-NH treatedChinese fir.


### 3.2. FTIR Studies

The chemical compositions of theChinese fir treated under different preservative solutions are studied by using Fourier transform infrared spectroscopy (FTIR). The obtained spectra are shown in Figure 4. Several characteristic absorption peaks are observed in the range of 2000–500 cm−1. The band at 1743 cm−1 is identified to the carboxyl stretching vibration in carboxylic acid groups in hemicellulose (Figure 4(a)). The band at 1510 cm−1 is assigned to aromatic skeletal vibration in lignin [18]. The bands at 1427 and 896 cm−1 are assigned to the absorption of the beta bonds stretching the cellulose. For the treated samples, the band density at 1743 cm−1 has a slight reduction. The reduction of the band is attributed to the reactions between copper and carboxylic groups that have taken place, while the cellulose acts as a stabilizer of the Cu-NH complex in solution [19–23]. Based on an analysis of the references, the groups of -COOH, -OH, -CHO, and so forth are the reactive groups to fix the metal ions. It can be seen from Figures 4(e)–4(g) that the densities of the wide band at 1100–980 cm−1 increase obviously due to the asymmetric stretching vibration absorption of the -CH2-O-CH2- of the PEG additive. Other characteristic peaks have not changed significantly. From these data, it is concluded that the preservatives solutions have not changed the chemical compositions of treated wood.Figure 4
FTIR spectra ofChinese fir treated under different conditions. (a)Chinese fir; (b) 2 wt.% Cu-NH treatedChinese fir; (c) 4 wt.% Cu-NH treatedChinese fir; (d) 6 wt.% Cu-NH treatedChinese fir; (e) 2 wt.% Cu-NH-PEG treatedChinese fir; (f) 4 wt.% Cu-NH-PEG treatedChinese fir; (g) 6 wt.% Cu-NH-PEG treatedChinese fir.


### 3.3. Distribution of the Preservative Solutions

During the stumpage treatment procedures, the preservative solutions flow with the longitudinal tracheids along the truck from root to top of the canopy by the driving force of transpiration. The complicated capillary structure of wood has an uncertain influence on the permeability of the preservative solutions [24]. Therefore, it is necessary to analyze the vertical concentration distribution of the preservative in different height positions.Figure5 shows the copper-based compounds concentration, identified as copper oxidation, changing with the longitudinal height of the trunk. It can be seen that lower concentration of preservative is easier to diffuse into the wood. Moreover, the preservative retention reduces with the increase of longitudinal height of the trunk. However, high concentration of preservative forms large retention gradient due to the preservative enrichment and solidifying at the bottom of the trunk, which influences the homogenous distribution of the preservative in the trunk [25, 26]. As seen from Figure 5(a), the preservative retention at the first part is 2.24 kg/m3, 4.24 kg/m3, and 6.25 kg/m3, respectively. At the fourth part of treated trees, the values are 0.97 kg/m3, 1.98 kg/m3, and 3.14 kg/m3, respectively. For the composite preservative solutions (Figure 5(b)), the preservative retention at the first part is 2.04 kg/m3, 3.94 kg/m3, and 5.57 kg/m3, respectively. At the fourth part, the values are 0.87 kg/m3, 1.62 kg/m3, and 2.69 kg/m3, respectively. From these data, it is concluded that the preservative retention for the composite preservative solutions is lower than that of the single preservative solution.Figure 5
The preservative retention in different height positions in the treatedChinese fir by (a) the Cu-NH preservative solutions; (b) the Cu-NH-PEG preservative solutions.
(a)
(b)Liquid movement from the roots to the atmosphere is controlled by the conductivity of the water pathway components [27]. Conductivities affecting liquid flow in the plant are hydraulic and diffusive [28]. In the course of the experiments, the effect of pressure on the fluid diffusion is constant. The effect of pressure is not considered. On a theoretical basis, modification of the tracheids size may potentially cause unfavorable effect on the transport of water in the xylem [27–29]. In other words, changing the shape of the tracheids or filling the tracheids space will also affect the diffusion of liquid in the xylem [30]. For the composite preservative solutions, higher relative molecular mass of PEG will fill the tracheids or pits or xylem rays, which will block the diffusion of the composite preservative solutions in the wood. Therefore, the retention of the preservatives in the woods is lower than that of the single preservative solutions [31, 32].


### 3.4. Morphology of the Samples

The morphologies of the samples are examined by SEM. The nontreated sample is tested as a reference. The porous structure of wood is clearly visible and nothing is filled in the tracheids and pits (Figure6(a)). As shown in Figure 6(b) to Figure 8, the morphologies of the resulting samples are different from the nontreated sample. Longitudinal tracheids are the main diffusion channels of coniferous wood and their main functions are to transport water and support the tree. Water migration between the tracheids depends mainly on the pits of the tracheids walls. Tens or hundreds of pairs of pits connect the adjacent tracheids. Xylem rays are main diffusion channels of the axial direction for coniferous wood. Then, the main materials circulation systems consisting of the longitudinal tracheids, pits, and xylem rays are constructed for coniferous wood. During the transpiration, the preservative diffuses along the longitudinal direction from the root of the trunk pipe to the crown. Simultaneously, the preservatives diffuse in wood through the pits and the xylem ray. The preservatives are more inclined to solidify into particles during the diffusion along with the xylem rays. Therefore, the solid particles appear in the xylem rays, which are shown in Figure 6(b). In the root of the trunk, large numbers of solidified particles appear due to its local higher concentration. During the process of transmission from the root to the crown, the solidified preservative particles gradually reduce with the decrease of the concentration of preservative solution. To the fourth-part sample, the solidified particles appear in a few xylem rays. For 2 wt.%, 4 wt.%, and 6 wt.%, three different concentrations of the preservative solutions, diffusion processions of the preservative solutions have similar variations, which are reflected in Figures 6, 7, and 8, respectively. Moreover, EDS spectrum of the solidified particles is given in Figure 6(f). The presence of Cu coming from the solidified particles is confirmed.Figure 6
SEM of (a) theChinese fir; (b) the first part; (c) the second part; (d) the third part; (e) the fourth part of 2% Cu-NH solution treatedChinese fir; (f) EDS spectrum of the solidified particle.Figure 7
SEM of (a) theChinese fir; (b) the first part; (c) the second part; (d) the third part; (d) the fourth part of 4 wt.% Cu-NH solution treatedChinese fir.Figure 8
SEM of (a) the first part; (b) the second part; (c) the third part; (d) the fourth part of 6 wt.% Cu-NH solution treated Chinese fir.In comparison with the single preservative solution Cu-NH, it is more difficult for the composite preservative solution Cu-NH-PEG to diffuse in the wood due to the increase of solution viscosity. Therefore, the preservative mainly solidifies in the root of the trunk. Concentration also has some influence on the diffusion of the preservative in wood. It can be seen from Figures9–11 that low concentrations of preservative solutions are more conducive to diffusion and transport in wood, and then more solidifying particles appear in the xylem rays. Those results are consistent with the results shown in Figure 5. In the process of diffusion, the preservative can react with the active groups of the cellulose, such as hydroxyl, carbonyl, and aldehyde group, which will enhance the properties of wood. Physical filling solidified preservative in xylem rays can also effectively improve the mechanical properties of wood [33, 34].Figure 9
SEM of (a) theChinese fir; (b) the second part; (c) the third part; (d) the fourth part of 2 wt.% Cu-NH-PEG composite solution treatedChinese fir.Figure 10
SEM of (a) theChinese fir; (b) the second part; (c) the third part; (d) the fourth part of 4 wt.% Cu-NH-PEG composite solution treatedChinese fir.Figure 11
SEM of (a) the first part; (b) the second part; (c) the third part; (d) the fourth part of 6 wt.% Cu-NH-PEG composite solution treatedChinese fir.


### 3.5. XPS Measurements

The chemical compositions of theChinese fir and the 2 wt.% Cu-NH solution treatedChinese fir are determined using XPS, which are shown in Figure 12. As seen from the treatedChinese fir specimen, the peak located at 934.17 eV is attributed to the Cu 2p region of the copper-based preservative compared with theChinese firspecimen [35, 36]. The result shows that the copper-based preservative is solidified in the wood, which is consistent with the EDS result.Figure 12
XPS spectra of (a) theChinese fir; (b) the first part of 2 wt.% Cu-NH solution treatedChinese fir.


## 3.1. XRD Analysis

XRD analysis is used to investigate the phase evolution of the preservative treated samples. The XRD pattern of the pureChinese fir powder is shown in Figure 3(a). The diffraction peaks observed at 16.1° and 22.5° are the characteristic diffraction peaks of the I type of wood cellulose (101) and (002) crystal plane in the structure cell. For the treated samples, the same diffraction peaks also appear in the corresponding position, which show that the addition of the modified agent does not destroy the crystalline form of the cellulose.Figure 3
XRD patterns of (a)Chinese firpowder; (b) the first part; (c) the second part; (d) the third part; (e) the fourth part of the 2% Cu-NH treatedChinese fir.


## 3.2. FTIR Studies

The chemical compositions of theChinese fir treated under different preservative solutions are studied by using Fourier transform infrared spectroscopy (FTIR). The obtained spectra are shown in Figure 4. Several characteristic absorption peaks are observed in the range of 2000–500 cm−1. The band at 1743 cm−1 is identified to the carboxyl stretching vibration in carboxylic acid groups in hemicellulose (Figure 4(a)). The band at 1510 cm−1 is assigned to aromatic skeletal vibration in lignin [18]. The bands at 1427 and 896 cm−1 are assigned to the absorption of the beta bonds stretching the cellulose. For the treated samples, the band density at 1743 cm−1 has a slight reduction. The reduction of the band is attributed to the reactions between copper and carboxylic groups that have taken place, while the cellulose acts as a stabilizer of the Cu-NH complex in solution [19–23]. Based on an analysis of the references, the groups of -COOH, -OH, -CHO, and so forth are the reactive groups to fix the metal ions. It can be seen from Figures 4(e)–4(g) that the densities of the wide band at 1100–980 cm−1 increase obviously due to the asymmetric stretching vibration absorption of the -CH2-O-CH2- of the PEG additive. Other characteristic peaks have not changed significantly. From these data, it is concluded that the preservatives solutions have not changed the chemical compositions of treated wood.Figure 4
FTIR spectra ofChinese fir treated under different conditions. (a)Chinese fir; (b) 2 wt.% Cu-NH treatedChinese fir; (c) 4 wt.% Cu-NH treatedChinese fir; (d) 6 wt.% Cu-NH treatedChinese fir; (e) 2 wt.% Cu-NH-PEG treatedChinese fir; (f) 4 wt.% Cu-NH-PEG treatedChinese fir; (g) 6 wt.% Cu-NH-PEG treatedChinese fir.


## 3.3. Distribution of the Preservative Solutions

During the stumpage treatment procedures, the preservative solutions flow with the longitudinal tracheids along the truck from root to top of the canopy by the driving force of transpiration. The complicated capillary structure of wood has an uncertain influence on the permeability of the preservative solutions [24]. Therefore, it is necessary to analyze the vertical concentration distribution of the preservative in different height positions.Figure5 shows the copper-based compounds concentration, identified as copper oxidation, changing with the longitudinal height of the trunk. It can be seen that lower concentration of preservative is easier to diffuse into the wood. Moreover, the preservative retention reduces with the increase of longitudinal height of the trunk. However, high concentration of preservative forms large retention gradient due to the preservative enrichment and solidifying at the bottom of the trunk, which influences the homogenous distribution of the preservative in the trunk [25, 26]. As seen from Figure 5(a), the preservative retention at the first part is 2.24 kg/m3, 4.24 kg/m3, and 6.25 kg/m3, respectively. At the fourth part of treated trees, the values are 0.97 kg/m3, 1.98 kg/m3, and 3.14 kg/m3, respectively. For the composite preservative solutions (Figure 5(b)), the preservative retention at the first part is 2.04 kg/m3, 3.94 kg/m3, and 5.57 kg/m3, respectively. At the fourth part, the values are 0.87 kg/m3, 1.62 kg/m3, and 2.69 kg/m3, respectively. From these data, it is concluded that the preservative retention for the composite preservative solutions is lower than that of the single preservative solution.Figure 5
The preservative retention in different height positions in the treatedChinese fir by (a) the Cu-NH preservative solutions; (b) the Cu-NH-PEG preservative solutions.
(a)
(b)Liquid movement from the roots to the atmosphere is controlled by the conductivity of the water pathway components [27]. Conductivities affecting liquid flow in the plant are hydraulic and diffusive [28]. In the course of the experiments, the effect of pressure on the fluid diffusion is constant. The effect of pressure is not considered. On a theoretical basis, modification of the tracheids size may potentially cause unfavorable effect on the transport of water in the xylem [27–29]. In other words, changing the shape of the tracheids or filling the tracheids space will also affect the diffusion of liquid in the xylem [30]. For the composite preservative solutions, higher relative molecular mass of PEG will fill the tracheids or pits or xylem rays, which will block the diffusion of the composite preservative solutions in the wood. Therefore, the retention of the preservatives in the woods is lower than that of the single preservative solutions [31, 32].


## 3.4. Morphology of the Samples

The morphologies of the samples are examined by SEM. The nontreated sample is tested as a reference. The porous structure of wood is clearly visible and nothing is filled in the tracheids and pits (Figure6(a)). As shown in Figure 6(b) to Figure 8, the morphologies of the resulting samples are different from the nontreated sample. Longitudinal tracheids are the main diffusion channels of coniferous wood and their main functions are to transport water and support the tree. Water migration between the tracheids depends mainly on the pits of the tracheids walls. Tens or hundreds of pairs of pits connect the adjacent tracheids. Xylem rays are main diffusion channels of the axial direction for coniferous wood. Then, the main materials circulation systems consisting of the longitudinal tracheids, pits, and xylem rays are constructed for coniferous wood. During the transpiration, the preservative diffuses along the longitudinal direction from the root of the trunk pipe to the crown. Simultaneously, the preservatives diffuse in wood through the pits and the xylem ray. The preservatives are more inclined to solidify into particles during the diffusion along with the xylem rays. Therefore, the solid particles appear in the xylem rays, which are shown in Figure 6(b). In the root of the trunk, large numbers of solidified particles appear due to its local higher concentration. During the process of transmission from the root to the crown, the solidified preservative particles gradually reduce with the decrease of the concentration of preservative solution. To the fourth-part sample, the solidified particles appear in a few xylem rays. For 2 wt.%, 4 wt.%, and 6 wt.%, three different concentrations of the preservative solutions, diffusion processions of the preservative solutions have similar variations, which are reflected in Figures 6, 7, and 8, respectively. Moreover, EDS spectrum of the solidified particles is given in Figure 6(f). The presence of Cu coming from the solidified particles is confirmed.Figure 6
SEM of (a) theChinese fir; (b) the first part; (c) the second part; (d) the third part; (e) the fourth part of 2% Cu-NH solution treatedChinese fir; (f) EDS spectrum of the solidified particle.Figure 7
SEM of (a) theChinese fir; (b) the first part; (c) the second part; (d) the third part; (d) the fourth part of 4 wt.% Cu-NH solution treatedChinese fir.Figure 8
SEM of (a) the first part; (b) the second part; (c) the third part; (d) the fourth part of 6 wt.% Cu-NH solution treated Chinese fir.In comparison with the single preservative solution Cu-NH, it is more difficult for the composite preservative solution Cu-NH-PEG to diffuse in the wood due to the increase of solution viscosity. Therefore, the preservative mainly solidifies in the root of the trunk. Concentration also has some influence on the diffusion of the preservative in wood. It can be seen from Figures9–11 that low concentrations of preservative solutions are more conducive to diffusion and transport in wood, and then more solidifying particles appear in the xylem rays. Those results are consistent with the results shown in Figure 5. In the process of diffusion, the preservative can react with the active groups of the cellulose, such as hydroxyl, carbonyl, and aldehyde group, which will enhance the properties of wood. Physical filling solidified preservative in xylem rays can also effectively improve the mechanical properties of wood [33, 34].Figure 9
SEM of (a) theChinese fir; (b) the second part; (c) the third part; (d) the fourth part of 2 wt.% Cu-NH-PEG composite solution treatedChinese fir.Figure 10
SEM of (a) theChinese fir; (b) the second part; (c) the third part; (d) the fourth part of 4 wt.% Cu-NH-PEG composite solution treatedChinese fir.Figure 11
SEM of (a) the first part; (b) the second part; (c) the third part; (d) the fourth part of 6 wt.% Cu-NH-PEG composite solution treatedChinese fir.


## 3.5. XPS Measurements

The chemical compositions of theChinese fir and the 2 wt.% Cu-NH solution treatedChinese fir are determined using XPS, which are shown in Figure 12. As seen from the treatedChinese fir specimen, the peak located at 934.17 eV is attributed to the Cu 2p region of the copper-based preservative compared with theChinese firspecimen [35, 36]. The result shows that the copper-based preservative is solidified in the wood, which is consistent with the EDS result.Figure 12
XPS spectra of (a) theChinese fir; (b) the first part of 2 wt.% Cu-NH solution treatedChinese fir.


## 4. Conclusions

Copper- (Cu-) based preservative with other reagents is successfully injected into the standing treeChinese fir by using sap-flow method. It is more difficult for the composite preservative solution to diffuse in the tree compared with the single preservative solution. For the single preservative solution, the preservative retention at the first part is 2.24 kg/m3, 4.24 kg/m3, and 6.25 kg/m3, respectively. At the fourth part of treated trees, the values are 0.97 kg/m3, 1.98 kg/m3, and 3.14 kg/m3, respectively. For the composite preservative solutions, the preservative retention at the first part is 2.04 kg/m3, 3.94 kg/m3, and 5.57 kg/m3, respectively. At the fourth part, the values are 0.87 kg/m3, 1.62 kg/m3, and 2.69 kg/m3, respectively. The results are consistent with the SEM results. During the diffusion and transportation of the preservative solution, the preservatives are more easily solidified in the xylem rays. In further research, the mechanical properties and dimensional stability combined with anticorrosion resistance of the resulting wood will be carried out to better understand the application value of this sap-flow method and provide technical support for the function design of the target wood products.



---