# A Novel Micro-Nano Structure Profile Control Agent: Graphene Oxide Dispersion

Authors: Zhong-Bin Ye; Yuan Xu; Hong Chen; Chen Cheng; Li-Juan Han; Lin Xiao
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

Graphite oxide sheet, now referred to as graphene oxide (GO), is the product of chemical exfoliation of graphite and has been known for more than a century. A GO sheet is characterized by two abruptly different length scales; the apparent thickness of the functionalized carbon sheet is approximately 1 nm, but the lateral dimensions can range from a few nanometers to micrometers. In this paper, an improved method for the preparation of graphene oxide within a mild condition is described. We have found that cancelling the high-temperature stage and prolonging the reaction time of mid-temperature can improve the efficiency of oxidation process. We utilized FTIR, XRD, Ultraviolet-visible, TGA, Raman spectrum, and XPS measurements to characterize the successfully synthesized GO. SEM images were employed to reveal the interior microstructure of as-prepared GO dispersion. We also wondrously found that the GO dispersion could be used as profile control agent in the oilfield water-flooding. Flooding experiments showed that the GO dispersion has an ability to adjust water injection profile, reduce permeability ratio, and improve conformance factor. So the GO dispersion would have potential applications in oilfield exploitation.


---

## Body

## 1. Introduction

Recently characterized as “the thinnest material in our universe” [1], graphene, a new class of two-dimensional carbon nanostructure, has stimulated wide interests in both the experimental and theoretical scientific communities due to its extraordinary material properties. In 2004, it was isolated by mechanical exfoliation from graphite crystal and visualized under an optical microscope by Novoselov et al. [2–5]. This has triggered the explosive growth of interest in this new material across many disciplines, which has led to the discovery of many extraordinary properties. For example, graphene was found to have high optical transparency of 97.7%, high electron mobility of up to 200000 cm2 ·V−1·s−1, high thermal conductivity of up to 5000 W·m−1·k−1, high nominal surface area of 2630 m2/g, and high breaking strength of 42 N/m. Therefore, many exciting applications have been envisioned and demonstrated [6]. Graphene can be produced by several methods: micromechanical cleavage of nature graphite, chemical vapor deposition (CVD), plasma enhanced CVD, electric arc discharge, epitaxial growth on electrically insulating surface such as SiC, unzipping of carbon nanotubes, and the oxidation-dispersion-reduction [7–9]. Among these methods, the oxidation-dispersion-reduction process is widely used for it possesses great potential for large-scale synthesis of graphene. Recently, a number of research groups have devoted themselves to applying graphene in a variety of technological applications including methanol oxidation, lithium-ion battery, solar cell, and transparent conducting film.Among the family of derivatized graphene sheets, graphite oxide sheets, now called graphene oxide (GO), have actually been made for over a century [10, 11]. Many graphene-based materials can be conveniently synthesized from graphene oxide, which can be prepared in bulk quantities from graphite with strong oxidizing conditions [12–14]. GO is a layered material featuring a variety of oxygen-containing functionalities with epoxy and hydroxyl groups on the basal plane and carbonyl and carboxyl groups along the edges [15, 16], which provides a platform for rich chemistry to occur both within the intersheet gallery and along sheet edges [17–19] (Figure 1). These oxygen functionalities render graphene oxide layers hydrophilic and water molecules can readily intercalate into the interlayer galleries. Therefore, GO can be also thought of as a graphite-type intercalation compound with both covalently bound oxygen and non-covalently bound water between the carbon layers. GO is hydrophilic and can readily disperse in water to form colloidal suspensions that are stable for at least months at concentrations of 1 mg/mL [20].Chemical structural models of graphene-based sheets. (a) Graphene consists of a single atomic layer of sp2-hybridized carbon atoms which stack together to form graphite. (b) GO consists of a graphene sheet derivitized by phenyl epoxide and hydroxyl groups on the basal plane and carboxylic acid groups on the edges. The edge-COOH groups can ionize resulting in an electrostatic repulsion between the sheets, allowing single layers to form an aqueous colloidal dispersion [6].
(a)
(b)As shown in the previous reports [21], a GO sheet is characterized by two abruptly different length scales. The thickness is of typical molecular dimensions, measured to be about 1 nm by atomic force microscopy (AFM). But its lateral dimensions are of common colloidal particles ranging from nanometers up to microns. Therefore, GO sheets can be characterized as either molecules or particles, depending on which length scale/dimension is of greater interest. This molecule-particle duality should naturally make GO a particularly interesting system for both chemists and material scientists.With the oilfield development, many oil fields have been in medium or high water cut period development stage, comprehensive water cut reached more than 80%, injected water channeling along high permeability layer phenomenon is serious, having the problem of lower water flooding recovery, contradiction of water flooding development is more and more obvious. In order to improve sweep efficiency of oil displacement agent and recovery efficiency, we should adjust profile of fluid absorption. In this paper, we wondrously found that the GO dispersion could be used as profile control agent in the oilfield water-flooding. We successfully synthesized the GO dispersion with the modified Hummer’s method and evaluated the performance of the GO dispersion as profile control agent. With regard to the properties of profile control, the GO dispersion would find potential applications in oilfield exploitation.


## 2. Materials and Method

### 2.1. Materials

Natural graphite powder (purity ≥ 99.85%) was supplied by Shanghai Huayi Group Huayuan chemical CO. Ltd., China. Potassium persulfate, phosphorus pentoxide, concentrated sulfuric acid, sodium nitrate, potassium permanganate, hydrogen peroxide, and hydrochloric acid were purchased from Chengdu Kelong Chemical Reagent Factory, China.


### 2.2. Preparation of Graphene Oxide (GO) Colloid Dispersion

Graphene oxide (GO) was synthesized by the modified Hummer’s method. The details were described as follows.In the pretreatment step to ensure oxidation completely, 10 g of potassium persulfate and 10 g of phosphorus pentoxide were added in 30 mL of concentrated sulfuric acid at 80°C and stirred slowly until the mixture was dissolved to prepare the oxidation solution. 10 g of purified natural graphite powder was added to the aforementioned oxidation solution and stirred at 80°C for 6 hours. Naturally cooling to room temperature, the solution was diluted with 2.5 L of deionized (DI) water; then, the mixture was filtered and washed with plentiful DI water to remove the residual oxidizing agents and dried in a vacuum oven.1 g of preoxidation graphite powder was dispersed in 23 mL of concentrated sulfuric acid under stirring at room temperature; then, 0.5 g of sodium nitrate was added, and the mixture was placed in an ice bath, 3 g of potassium permanganate was added gradually into the graphite slurry to keep the temperature of the slurry lower than 5°C for 2 hours. Successively, the reaction system was heated to 35°C in the water bath and kept at the temperature for 2 hours until the slurry became thick, pasty, and brownish. Next, 46 mL of DI water was added dropwise to the mixture solution, and the temperature was maintained at 35°C in the water bath for another 2 hours. Finally, the mixture was diluted with 92 mL of DI water and treated with 5% (wt.) hydrogen peroxide solution slowly to terminate the reaction until the mixture changed to brilliant yellow which indicated fully oxidized graphite. Afterward, the mixture was filtered and washed with 5% (wt.) hydrochloric acid aqueous solution to remove metal ions followed by repeated washing with DI water until a neutral pH was obtained to remove the excessive acid and inorganic salt. The resulting GO was dried overnight at 60°C to produce GO powder. The as-prepared solid graphene oxide was dispersed again in water (1 mg/mL) by ultrasonication for 2 hours and centrifuged at 8000 rpm for 30 min to remove aggregates.


### 2.3. Characterization

The Fourier transform infrared (FTIR) spectra of graphite and GO were recorded using ThermoFisher Scientific Nicolet 6700 over range from 670 to 4000 cm−1. X-ray diffraction (XRD) measurements were performed directly on the powder sample of graphite and GO using PANalytical XPERT-PRO diffractometer (40 kV, 40 mA) with Cu (λ = 1.54 Å) irradiation at a scanning of 2°/s in the 2θ range of 5–70°. The Ultraviolet-visible absorption spectra of GO aqueous dispersion were recorded on a TU-1901 double-beam spectrophotometer. Thermogravimetric analysis (TGA) was carried out with NETZSCH STA 449F3. The heating rate was 10°C/min. Each time, ~5 mg sample was measured in an aluminum crucible under inert gas atmosphere from 40 to 800°C. Scanning electron microcopy (SEM) measurements were carried out on a field emission scanning electron microanalyzer (FEI Quanta 450) at an accelerating voltage of 20 kV. Raman spectroscopy was performed at room temperature using a HR800 Raman spectrometer at 532.2 nm wavelength incident laser light. X-ray photoelectron spectroscopy (XPS) analysis was performed with Kratos AXIS Ultra DLD using a monochromic Al Kα radiation (hν = 1486.6 eV) at 15 kV and 10 mA.


### 2.4. Evaluation of Core Flooding Experiment

Schematic diagrams of experimental set-up were showed in Figure2. For the flooding experiment of single core, the size of the core was φ2.5 × 7 cm, the permeability was 110 × 10−3
μm2, and the pore volume was 9.9 cm3. The fixed rate of injection was 0.5 mL/min and the concentration of GO was 500 mg/L. We evaluated the flooding property of GO via the pressure of the total injection process.Schematic diagrams of experimental set-up: flooding of single core (a) and flooding of two cores in parallel (b).
(a)
(b)For the flooding experiment of two cores in parallel, the size of the cores was also φ2.5 × 7 cm and the permeability was 58 × 10−3 μm2 and 232 × 10−3 μm2, respectively. The permeability ratio of the cores was 1 : 4. The pore volumes of the cores were 9.5 cm3 and 10.5 cm3, respectively. The fixed rate of injection was 3 mL/min and the concentration of GO was 500 mg/L. We evaluated the shunt rate of low permeability layer and the pressure of the total injection process.


## 2.1. Materials

Natural graphite powder (purity ≥ 99.85%) was supplied by Shanghai Huayi Group Huayuan chemical CO. Ltd., China. Potassium persulfate, phosphorus pentoxide, concentrated sulfuric acid, sodium nitrate, potassium permanganate, hydrogen peroxide, and hydrochloric acid were purchased from Chengdu Kelong Chemical Reagent Factory, China.


## 2.2. Preparation of Graphene Oxide (GO) Colloid Dispersion

Graphene oxide (GO) was synthesized by the modified Hummer’s method. The details were described as follows.In the pretreatment step to ensure oxidation completely, 10 g of potassium persulfate and 10 g of phosphorus pentoxide were added in 30 mL of concentrated sulfuric acid at 80°C and stirred slowly until the mixture was dissolved to prepare the oxidation solution. 10 g of purified natural graphite powder was added to the aforementioned oxidation solution and stirred at 80°C for 6 hours. Naturally cooling to room temperature, the solution was diluted with 2.5 L of deionized (DI) water; then, the mixture was filtered and washed with plentiful DI water to remove the residual oxidizing agents and dried in a vacuum oven.1 g of preoxidation graphite powder was dispersed in 23 mL of concentrated sulfuric acid under stirring at room temperature; then, 0.5 g of sodium nitrate was added, and the mixture was placed in an ice bath, 3 g of potassium permanganate was added gradually into the graphite slurry to keep the temperature of the slurry lower than 5°C for 2 hours. Successively, the reaction system was heated to 35°C in the water bath and kept at the temperature for 2 hours until the slurry became thick, pasty, and brownish. Next, 46 mL of DI water was added dropwise to the mixture solution, and the temperature was maintained at 35°C in the water bath for another 2 hours. Finally, the mixture was diluted with 92 mL of DI water and treated with 5% (wt.) hydrogen peroxide solution slowly to terminate the reaction until the mixture changed to brilliant yellow which indicated fully oxidized graphite. Afterward, the mixture was filtered and washed with 5% (wt.) hydrochloric acid aqueous solution to remove metal ions followed by repeated washing with DI water until a neutral pH was obtained to remove the excessive acid and inorganic salt. The resulting GO was dried overnight at 60°C to produce GO powder. The as-prepared solid graphene oxide was dispersed again in water (1 mg/mL) by ultrasonication for 2 hours and centrifuged at 8000 rpm for 30 min to remove aggregates.


## 2.3. Characterization

The Fourier transform infrared (FTIR) spectra of graphite and GO were recorded using ThermoFisher Scientific Nicolet 6700 over range from 670 to 4000 cm−1. X-ray diffraction (XRD) measurements were performed directly on the powder sample of graphite and GO using PANalytical XPERT-PRO diffractometer (40 kV, 40 mA) with Cu (λ = 1.54 Å) irradiation at a scanning of 2°/s in the 2θ range of 5–70°. The Ultraviolet-visible absorption spectra of GO aqueous dispersion were recorded on a TU-1901 double-beam spectrophotometer. Thermogravimetric analysis (TGA) was carried out with NETZSCH STA 449F3. The heating rate was 10°C/min. Each time, ~5 mg sample was measured in an aluminum crucible under inert gas atmosphere from 40 to 800°C. Scanning electron microcopy (SEM) measurements were carried out on a field emission scanning electron microanalyzer (FEI Quanta 450) at an accelerating voltage of 20 kV. Raman spectroscopy was performed at room temperature using a HR800 Raman spectrometer at 532.2 nm wavelength incident laser light. X-ray photoelectron spectroscopy (XPS) analysis was performed with Kratos AXIS Ultra DLD using a monochromic Al Kα radiation (hν = 1486.6 eV) at 15 kV and 10 mA.


## 2.4. Evaluation of Core Flooding Experiment

Schematic diagrams of experimental set-up were showed in Figure2. For the flooding experiment of single core, the size of the core was φ2.5 × 7 cm, the permeability was 110 × 10−3
μm2, and the pore volume was 9.9 cm3. The fixed rate of injection was 0.5 mL/min and the concentration of GO was 500 mg/L. We evaluated the flooding property of GO via the pressure of the total injection process.Schematic diagrams of experimental set-up: flooding of single core (a) and flooding of two cores in parallel (b).
(a)
(b)For the flooding experiment of two cores in parallel, the size of the cores was also φ2.5 × 7 cm and the permeability was 58 × 10−3 μm2 and 232 × 10−3 μm2, respectively. The permeability ratio of the cores was 1 : 4. The pore volumes of the cores were 9.5 cm3 and 10.5 cm3, respectively. The fixed rate of injection was 3 mL/min and the concentration of GO was 500 mg/L. We evaluated the shunt rate of low permeability layer and the pressure of the total injection process.


## 3. Results and Discussion

GO was synthesized by the traditional Hummer’s method including three steps which were low-temperature (0°C), mid-temperature (35°C), and high-temperature (98°C) with concentrated sulfuric acid and potassium permanganate as oxidant. In this paper, we called off the step of high-temperature, which was replaced with prolonging the reaction time of mid-temperature to improve the extent of oxidation of graphite and avoid the damage of eruption in the high-temperature reaction. We could manufacture the GO with a secure and stable condition. The mechanism of the preparation of graphene oxide was described as follows.In the stage of low-temperature, the mixture presented the color of black because that the oxidizability of concentrated sulfuric acid could not provide the condition of intercalation. Adding potassium permanganate, the edge of graphite begun to be oxidized, which resulted in sulfate ion and strong-polarity vitriol were adsorbed in the edge of graphite with electrostatic attraction. The carbon grid plane of graphite was transformed to positively charged macromolecule plane gradually along with adding of strong oxidation and proceeding of oxidation reaction; thus, negative changed bisulfate ion and strong-polarity vitriol were adsorbed and intercalated into interlayer of graphite to form vitriol-graphite intercalated compound with attractive interaction between charges and electrostatic attraction of strong-polarity vitriol (reaction equation (1)) [22]:
(1)
6
n
H
2
SO
4
+
2
n
graphite
+
n
[
O
]
=
n
H
2
O
+
2
n
graphite
+
·
HSO
4
-
·
2
H
2
SO
4
n
In the stage of mid-temperature, the vitriol-graphite intercalated compound was oxidized deeply with strong oxidizability of potassium permanganate, while the oxygen atom and the carbon atom were combined with covalent bond; the partial C=C of six-member ring were fractured to form the structure similar with alcohol (reaction equation (2)) [22]:
(2)
MnO
4
-
+
2
H
+
+
SO
4
2
-
+
[
graphite
+
·
HSO
4
-
·
2
H
2
SO
4
]
⟶
MnO
2
↓
+
SO
x
+
H
2
O
+
GO
y
The mixture was diluted with water after the mid-temperature stage, the vitriol-graphite intercalated compound was hydrolyzed and while vitriol was pushed aside with plenty of water, hydrogen sulfate ions were exchanged with the hydroxide in the water. In this process, if the temperature was excessive, the vitriol-graphite intercalated compound will be thermally decomposed, and the structure of graphite will be restored rapidly, resulting in that GO could not be formed on account of that the hydroxide and water could not enter into interlamination of graphite. Thus, during the above-mentioned stage, the thermal decomposition reaction would reduce the oxidation degree of graphite because of the excessive temperature. The GO synthesized by the traditional Hummer’s method (T-GO) and the modified Hummer’s method (M-GO) were shown in Figure 3. M-GO was oxidized more adequately than T-GO with a brighter color. So in our study, we canceled the high-temperature reaction and maintained 35°C to carry out the last step reaction after adding the water dropwise to the mixture solution.The GO synthesized by the modified Hummer’s method (a) and the traditional Hummer’s method (b).
(a)
(b)FTIR spectra of pristine graphite and GO were presented in Figure4. For the graphite spectrum, no vibration peak was observed. The FTIR spectra of GO was tested for confirming the successful synthesis of GO. The intense band at 3365 cm−1 and the broad band at 3200 cm−1 to 3700 cm−1 were attributed to stretching of the O–H bond of CO–H and residual water molecules, which confirmed that the GO could not be dried thoroughly. The band at 1729 cm−1 was associated with stretching of the C=O bond of carbonyl or carboxyl groups. The bands present at 1623 and 1223 cm−1 were attributed to deformations of the O–H bond in water and CO–H groups, respectively. Deformation of the C–O bond was observed as the intense band present at 1047 cm−1. The bands at 874 and 826 cm−1 were attributed to characteristic absorption band of the C–O–C.Figure 4
FTIR spectra of graphite and GO.XRD provided a conclusive proof for the degree of oxidation as the layer distances of pristine graphite and GO was highly different which was showed in Figure5. For the pristine graphite, the (002) diffraction peak appears at 2θ = 26.5°, indicating an interlayer spacing of 0.34 nm between graphene platelets, obtained by Bragg’s equation. After oxidization-induced expansion, the (002) diffraction peak shifted to 2θ = 10.6°, with no reflections at 26.5°, suggesting that the interlayer distance increased to 0.834 nm due to oxidation and completely eliminated the 0.34 nm graphite interlayer spacing. This suggested that the graphite was efficiently oxidized. Increase in the interlayer spacing was attributed to the introduction of oxygenic functional groups and the presence of water molecules between the graphite layers or other structural defects [23].Figure 5
XRD patterns of graphite and GO.The Ultraviolet-visible absorption spectra of GO aqueous dispersion were showed in Figure6. The absorption peak at 230 nm of GO corresponded to π
→
π
* transitions of aromatic C=C bonds and the absorption peak at 300 nm corresponded to transitions of C=O bonds.Figure 6
UV-Vis absorption spectra recorded in aqueous dispersion at 0.05 mg/mL of GO.The thermal stability of the GO in comparison with pristine graphite, characterized by TGA, was showed in Figure7. The TGA curve of GO displayed two prominent mass losses at about 100°C and 200°C. The TGA curve of GO showed about 11 wt% mass loss at 100°C, which could be attributed to the evaporation of water trapped between hydrophilic GO sheet. It further demonstrated that GO could not be dried thoroughly in accordance with the result of FTIR. And the main mass loss occurred from 150°C to 250°C due to the thermal decomposition of oxygen-containing functional groups from the graphene oxide surface such as hydroxyl, epoxy, and carbonyl groups which verified that the graphite had been oxidized successfully. The GO loss was approximately 62 wt% at 800°C. However, the TGA curve of the pristine graphite indicated approximately 3 wt% mass loss at 800°C and nearly no mass loss under 100°C which testified that the graphite was super-hydrophobic and had a thermodynamic stability.Figure 7
TGA curves of graphite and GO.Raman spectroscopy was a powerful approach to characterize the graphite degree of carbon-based materials. The significant structural changes occurred during the chemical processing from pristine graphite to GO, was also reflected in their Raman spectra. Figure8 showed the Raman spectra of natural graphite and GO. It was well recognized that the D band resulted from a breathing mode of κ-point photons of A1g symmetry, while the G band was due to the first order scattering of the E2g phonon of sp2 C atoms [24]. The D band of natural graphite was located at 1355 cm−1. The G band of natural graphite was located at 1583 cm−1 and resulted from the in-phase vibration of the graphite lattice. After oxidizing, the intensity of the D band was increased, and the D band of GO was located at 1347 cm−1, which resulted from the decrease in the size of the in-phase sp2 domains due to the extensive oxidation. The G band of GO became much broader and shifted to 1596 cm−1 owing to the present of isolated double bonds that resonated at the higher frequencies than the G band of graphite [25].Figure 8
Raman spectra of graphite and GO excited at 532.2 nm.XPS measurement was applied to investigate the chemical bonds formed on the surface of GO. The survey XPS data was showed in Figure9(a). There were two obvious peaks which attributable to carbon and oxygen, respectively. The C1s XPS spectra of GO were depicted in Figure 9(b). It was clear that four different types of carbon with chemical environments were obvious in GO: carbon sp2 (C=C, 284.6 eV), epoxy/hydroxyl (C–O, 286.5 eV), carbonyl (C=O, 287.8 eV), and carboxyl (O–C=O, 288.7 eV), respectively. This could be attributed to the fact that a large amount of surface oxide groups were chemically attached to the defect or edge sites of the basal planes [26].XPS spectra of GO (a) and high resolution scans of C 1s region of GO (b).
(a)
(b)The microstructure of graphite was composed of numerous graphite sheets which were clearly showed in Figures10(a)–10(d). The interior microstructure of as-prepared GO dispersion was imaged by SEM of its lyophiled samples. According to SEM images (Figures 10(e)–10(h)), the GO aqueous dispersion had an obvious 3D porous network structure. The pore diameters ranged from submicrometer to several micrometers and the pore walls consisted of very thin layers of stacked GO sheets [27]. Therefore, it was reasonable to conclude that a loose dynamic GO network existed in the original dispersion of GO sheets owing to a force balance between electrostatic repulsion and binding interactions (hydrogen bonding, π-stacking, hydrophobic effect, etc.) [28].SEM images with different magnifications of graphite (a–d) and GO dispersion (e–h) interior microstructures.
(a)
(b)
(c)
(d)
(e)
(f)
(g)
(h)The core flooding experiments were carried out to evaluate the ability of profile control of GO dispersion. Resistance factor and residual resistance factor were the important indicators that characterize abilities of liquid fluidity control and the permeability descent. Resistance factor was a measure of the relative mobility of profile control system, the greater resistance factor was the stronger the profile control system reduced the flow ability of fluid in porous media. And residual resistance factor was a measurement of the permeability reduction of profile control system permanently. The GO dispersion would produce two important effects after being injected into core: one is that it would increase the aqueous phase injection pressure; the other one is that GO’s adsorption retention would cause the reduction of reservoir permeability. Those two effects led to the significant reduction of displacing phase fluidity in the oil reservoir. Therefore, the GO dispersion injection would reduce total fluidity of water in flooding layer with high permeability, lessen the gap of waterline advancement speed between the layers with higher and lower permeability, adjust water injection profile, and improve conformance factor. The pressure curve of single core flooding was showed in Figure11. According to the results of injection pressure, resistance factor, and residual resistance factor of GO dispersion were calculated with
(3)
F
R
=
Δ
P
p
Δ
P
wi
,
F
RR
=
Δ
P
wa
Δ
P
wi
,
where F
R was resistance factor, F
RR was residual resistance factor, Δ
P
wi was stable pressure of precious water flooding (MPa), Δ
P
p was stable pressure of GO dispersion flooding (MPa), Δ
P
wa was stable pressure of subsequent water flooding (MPa). The resistance factor of GO dispersion was 4.6 and the residual resistance factor was 14.3, respectively, which indicated that GO dispersion had an ability to adjust the profile of fluid absorption.Figure 11
Pressure curve of flooding of GO dispersion with single core.The result of flooding experiment of two cores in parallel was showed in Figure12 and the shunt rate of low permeability was 20% approximately in water flooding stage, which was in accord with the permeability ratio of the cores (1 : 4). In GO dispersion flooding stage, the GO dispersion, which had an obvious 3D porous network structure (according to SEM images), flowed into high permeability layer preferentially. Graphene oxide nanosheets could absorb on surface of the core (Figure 13) and cause a certain extent physical plugging effect. GO dispersion plugged the high permeability layer and caused an increase of injection pressure, but the high permeability layer was not been plugged completely, the penetrability of high permeability layer was reduced but the reservoir had a certain extent connectivity because of the porous structure of GO dispersion. The shunt rate of low permeability increased from 20% to 40% around in the subsequent water flooding. So we demonstrated that the GO dispersion has an ability to adjust water injection profile, reduce permeability ratio, and improve conformance factor.Figure 12
Shunt rate and pressure of flooding of GO dispersion with two cores in parallel.Figure 13
Profile image of the core before and after flooding.


## 4. Conclusions

In conclusion, a simple chemical route has been developed for the preparation of water dispersed nanosized graphene oxide, which cancelled high-temperature stage and prolonged the reaction time of mid-temperature to improve the extent of oxidation of graphite and avoid the damage of eruption in high-temperature reaction. The method developed here is simple, scalable, and environmental friendly. FTIR, XRD, Ultraviolet-visible, TGA, Raman spectrum, and XPS measurements indicate that the GO has been synthesized successfully. GO is essentially a single atomic sheet, while its lateral dimension extends to the size of colloidal particles. SEM images have showed the microcosmic structure of the GO dispersion that GO sheets with lateral dimensions of several micrometers are able to contact with each other to form a loose network in solution. Flooding experiments show that the GO dispersion has an ability to adjust water injection profile, reduce permeability ratio, and improve conformance factor, and could be used as profile control agent in the oilfield water-flooding. Our work may lay a foundation for further industrial applications of GO in oilfield exploitation.



---