# Incorporation of Amphipathic Diblock Copolymer in Lipid Bilayer for Improving pH Responsiveness

Authors: Tian Xia; Weiju Hao; Yazhuo Shang; Shouhong Xu; Honglai Liu
Journal: International Journal of Polymer Science
 (2016)

---

## Abstract

Diblock copolymers (mPEG-b-PDPA), which were designed to possess pH-sensitivity as well as amphipathy, were used as an intelligent lock in the liposomal membrane. The so-called pH-sensitive liposomes were prepared by simple mixing of the synthesized mPEG-b-PDPA with phospholipids and cholesterol. Fluorescence polarization at pH 7.4 showed that the membrane stability of the hybrid liposome was significantly increased compared with the pure liposome. Therefore, in the neutral environment, the leakage of doxorubicin (DOX) was inhibited. However, when pH decreased to 6.0, DOX release rate increased by 60% due to the escape of copolymer. The effects of the membrane composition and the PDPA segment length on bilayer membrane functions were investigated. These results revealed that the synthesized copolymers increased the difference in DOX cumulative release between pH 7.4 and 6.0, that is, improved the pH-controllability of the drug release from hybrid liposomes.


---

## Body

## 1. Introduction

There exists a long-term problem that is how to improve the switch effect of drug carriers for the sake of preventing the drug leakage during transport before reaching to the target sites and stimulating the release of drugs at the appropriate time [1, 2]. It is very important to design a kind of intelligent carrier for delivering drugs to the target site accurately and releasing drugs timely in a certain environment with the help of the environmental stimulation. In recent years, researchers have prepared pH-sensitive [3–5], thermosensitive [6–8], and photosensitive [9, 10] vesicle for drug delivery system, in response to the various physiological and pathological environments.For example, triblock copolymers poly(N-vinylcaprolactam)-poly(dimethylsiloxane)-poly(N-vinylcaprolactam) (PVCL-PDMS-PVCL) with temperature sensitivity were synthesized and used to deliver anticancer drugs in physiological temperature range of 37–42°C [11]. Benzoyl peroxide (BPO) had been incorporated into a pH-sensitive mesoporous silica nanocomposite and the enhanced free radical generation induced higher cytotoxicity at pH 6.5 than pH 7.4 [12]. Many pH-responsive copolymers had been designed and synthesized for various applications [13, 14]. For example, Arg-Gly-Asp-polycarboxybetaine methacrylate-poly(2-(diisopropylamino)ethyl methacrylate) (RGD-PCB-PDPA) triblock copolymers were prepared by Huang and coworkers. Theirin vitro andin vivo evaluation findings showed that the multifunctional RGD-PCB-PDPA nanoparticle was a flexible design approach, which indicated a great potential for nanocarriers in tumor-targeted drug delivery.We are interested in designing and preparing liposomes with various stimuli responsibilities. Liposome has attracted much attention in the field of medicine as a drug carrier. Liposome, known as a phospholipid-based vesicle, is composed of a closed vesicle with a structure of bilayer constructed by self-assembly in the aqueous phase [15, 16]. We have synthesized a series pH-sensitive di- and triblock copolymers and inserted it into liposome for pH-controlled releasing [17]. In general, the drug release mechanism of pH-sensitive nanocarriers is often based on the pH-triggered protonation, or hydrolysis, or dissolution/degradation of the polymers [18, 19]. The pH values of extracellular matrix of tumor site, endosome, and lysosome are known to be in weak acid. Then, poly(2-(diisopropylamino) methyl methacrylate) (PDPA), whose triggered pH value (about 6.2) is appropriate for physiological environment, was often selected to be the pH-sensitive segment for various materials [20, 21].We believe a diblock pH-sensitive copolymer might give “lock” effect on lipid membrane fluidity and just need to adjust the block size. In this paper, we synthesized pH-sensitive diblock copolymers with various PDPA lengths. In order to make the diblock copolymers act as a lock, the PDPA lengths were selected to be similar to the thickness of phospholipid bilayer. The synthesized diblock copolymers were inserted into liposome membrane, which was composed of hydrogenated soybean phosphatidylcholine (HSPC), 1,2-dioleoyl-sn-3-phosphocholine (DOPC) [22] and DC-cholesterol. DC-cholesterol was selected for providing positive charge to liposomes so that the liposomes could keep from aggregating. The synthesized polymer is positively charged under neutral environment. At pH 7.4, the interaction between DC-cholesterol and polymer should be electroattraction, while at pH 6.0, the protonated polymers become hydrophilic and escaped from liposomes. The electrorepulsion between PDPA blocks and liposomes should help the escaping behavior. Then, the release behaviors of these hybrid liposomes were comparatively studied under pH 7.4 and pH 6.0. This study confirmed that the DOX-loaded liposome containing pH-responsive diblock copolymers was able to inhibit drug release at pH 7.4 and gave a motivation to release drug at pH 6.0. The synthesized copolymer played a very good role to improve the biofunction of lipid bilayer.


## 2. Experimental

### 2.1. Materials

Methoxypolyethylene glycol (mPEG350), 2-(diisopropylamino) ethyl methacrylate (DPA, 97%), and copper(I) bromide (CuBr; 99.99%) were purchased from Sigma-Aldrich. 1,6-Diphenyl-1,3,5-hexatriene (DPH), doxorubicin hydrochloride (DOX·HCl, 98%) and 2-bromo-2-methylpropionyl bromide (98%) were obtained from J&K Scientific. N,N,N′,N′,N′-Pentamethydieyhylenetriamine (PMDETA, 98%) was provided by TCI. Tetrahydrofuran (anhydrous) (THF, AR) and trichloromethane (AR) were bought from Tianlian Company. Aluminium oxide used for removal of the ATRP copper catalyst was of column chromatography grades 100–200 list order from Tianlian Company. 1-Palmitoyl-2-stearoyl-sn-glycero-3-phosphatidylcholine (HSPC > 98%), 1,2-dioleoyl-sn-glycero-3-phosphocholine (DOPC > 97%), and DC-cholesterol were provided from Lipoid.


### 2.2. Characterizations

#### 2.2.1. Proton Nuclear Magnetic Resonance (1H NMR) and Gel Permeation Chromatography (GPC) Characterization

Molecular weight and polydispersity index (PDI) of mPEG-b-PDPA copolymers were determined by gel permeation chromatography (GPC) using a Waters 1515 instrument at 25°C. THF was used as an eluent with a flow rate of 1.0 mL/min and polystyrene was used as calibration standard. A Bruker 500 MHz NMR spectrometer instrument was used to acquire the1H NMR spectra of mPEG-Br and mPEG-b-PDPA using CDCl3 as solvent. The block copolymer compositions were determined by comparing appropriate integrals assigned to the different comonomers.


#### 2.2.2. Transmission Electron Microscopy (TEM)

Transmission Electron Microscopy (TEM) images were performed on a JEM-1400 electron microscope operated at 100 kv. To prepare TEM samples, the liposome suspension was deposited on a carbon-coated copper grid and negatively stained with the phosphotungstic acid solution. Excess solution was absorbed and the samples were allowed to dry at ambient temperature.


#### 2.2.3. Dynamic Light Scattering (DLS)

Dynamic light scattering (DLS) studies were carried out using a Zetasizer Nano ZS Instrument. The influence of pH on zeta-potential of liposomes was investigated in the range of pH 2–9 [17, 20]. The diblock copolymers were firstly dissolved in 0.01 M HCl to prepare stock solution at final a concentration of 0.1 mg/mL. The pH titration was carried out by adding small volume of 0.1 M NaOH solution under stirring. The change of pH values was monitored by using PHS-2C precision acidity meter. The average results were accepted as the final data measured at least three times.


#### 2.2.4. Turbidity

The aggregation behavior of the copolymer was measured in a UV-Vis spectrophotometer (UV-2450, Shimadzu, Japan). The transmittance of the copolymer solution was monitored in a quartz cuvette (1 cm width) under various pH values.


#### 2.2.5. Fluorescence Polarization

The fluorescence polarization (Pol) of liposome was measured by a LS55 fluorimeter (Perkin Elmer) equipped with automated polarizer. Liposome suspensions were prepared: 75μL of liposome suspension and 200 μL of DPH solution were added to the PBS buffer solution to be further diluted to 4 mL. The concentration of DPH was 2 mmol/L and lipid/DPH (w/w) was 800 : 1. In order to make the probes to be incorporated, the samples were shaken overnight at 37°C before measurements. The Pol values were measured at an excitation slit of 10 nm and emission slit of 5 nm and excitation and emission wavelengths of 360 and 425 nm, respectively. Fluorescence polarization was then calculated automatically by [23, 24](1)Pol=Ivv-GIvhIvv+GIvh,where Pol is the fluorescence polarization and Ivv and Ivh are the fluorescence intensities of the emitted light polarized parallel and perpendicular to the exciting light, respectively. G is the grating correction factor, which is equal to Ihv/Ihh, obtained by measuring the vertically and horizontally polarized emission intensities after excitation with horizontally polarized light.


### 2.3. Synthesis of mPEG-Br Macroinitiator

mPEG-Br macroinitiator was synthesized according to the literature method [21, 25]. Typically, mPEG-OH (0.0086 mol) was dropped into 50 mL of dichloromethane. The flask containing the solution was placed in an ice bath, and trimethylamine (TEA) (0.0216 mol) was added to the solution. Then, 2-bromo-2-methylpropionyl bromide (0.0202 mol) was added dropwise to the solution over 1 h under stirring and then the reaction was continued for about 30 h at room temperature. The crude solution was washed with saturated sodium chloride solution and saturated sodium hydrogen carbonate solution for three times followed by extracting with dichloromethane. After that, anhydrous magnesium sulfate was added to the extract liquor and then filtered to remove insoluble impurities and concentrated by evaporation. The product was finally dried under vacuum for about 12 h.


### 2.4. Synthesis of mPEG-b-PDPA Diblock Copolymer

The diblock copolymer was synthesized by ATRP with mPEG-Br as initiator [26, 27]. In a typical ATRP procedure, a Schlenk flask with a magnetic stir bar and a rubber septum was charged with DPA monomer (12.657 mmol), mPEG-Br macroinitiator (0.8438 mmol), PMDETA (0.9282 mmol), and anhydrous tetrahydrofuran (6.0 mL). This mixture was deoxygenated by bubbling N2 for 0.5 h before adding CuIBr catalyst (0.8438 mmol). The reactant mixture was degassed by three freezing-thawing cycles. Afterwards, the polymerization reaction was carried out in an oil bath preheated at 55°C for 12 h. Finally, the reaction solution was diluted by addition of THF and then passed through a neutral alumina column to remove the copper catalysts. The diblock copolymer was then washed by Milli-Q water for at least 3 times and dried under vacuum for 24 h.


### 2.5. Preparation of Liposomes

Liposomes were prepared by a thin lipid film hydration method [28]. In brief, HSPC or DOPC, DC-cholesterol, and different mole ratio of diblock copolymer were dissolved in chloroform in a round bottom flask. Then a film was formed by rotary evaporation of the solvent at the temperature of 45°C and then organic solvent was volatilized completely after 1 h. The lipid film was hydrated with 5 mL of ammonium sulfate solution at 60°C to achieve a final lipid concentration of 1 mg/mL. Following hydration, uniform liposomes were obtained by extrusion at 60°C through 400 nm polycarbonate filter 11 times and then 200 nm filter 7 times by using a LiposoFast.


### 2.6. Drug Loading

The active transport method was used to encapsulate DOX into liposome. The liposome suspension was dialyzed against the 0.9% NaCl solution using dialysis tubes (cutoffMn=14000) to remove the free ammonium sulfate acid. Then, the suspension was placed in a flask. DOX solution (2.5 mg/mL) was mixed with the liposome suspension at the molar ratio of 1 : 10 (DOX : lipids). The unloaded free DOX was removed through a Sephadex G-50 column. The liposomes loaded with DOX were collected and mixed with Triton X-100 for measuring encapsulated amount. The total DOX amount A1 and encapsulated DOX amount A0 were determined by the absorbing intensity at 485 nm (UV-2450, Shimadzu). The encapsulated efficiency (E%) was calculated based on [29](2)E%=A0A1×100%.


### 2.7.In Vitro DOX Release

In vitro DOX release was carried under various pH values (pH 6.0 or 7.4). 1 mL of DOX-loaded liposome suspension was moved to a dialysis tube (cutoff Mn=14000), which was exposed to 25 mL of PBS solution at 37°C. The cumulative release amount of DOX at different time At was measured and the release percentage was calculated:(3)Cumulative  release%=AtA0×100%.


## 2.1. Materials

Methoxypolyethylene glycol (mPEG350), 2-(diisopropylamino) ethyl methacrylate (DPA, 97%), and copper(I) bromide (CuBr; 99.99%) were purchased from Sigma-Aldrich. 1,6-Diphenyl-1,3,5-hexatriene (DPH), doxorubicin hydrochloride (DOX·HCl, 98%) and 2-bromo-2-methylpropionyl bromide (98%) were obtained from J&K Scientific. N,N,N′,N′,N′-Pentamethydieyhylenetriamine (PMDETA, 98%) was provided by TCI. Tetrahydrofuran (anhydrous) (THF, AR) and trichloromethane (AR) were bought from Tianlian Company. Aluminium oxide used for removal of the ATRP copper catalyst was of column chromatography grades 100–200 list order from Tianlian Company. 1-Palmitoyl-2-stearoyl-sn-glycero-3-phosphatidylcholine (HSPC > 98%), 1,2-dioleoyl-sn-glycero-3-phosphocholine (DOPC > 97%), and DC-cholesterol were provided from Lipoid.


## 2.2. Characterizations

### 2.2.1. Proton Nuclear Magnetic Resonance (1H NMR) and Gel Permeation Chromatography (GPC) Characterization

Molecular weight and polydispersity index (PDI) of mPEG-b-PDPA copolymers were determined by gel permeation chromatography (GPC) using a Waters 1515 instrument at 25°C. THF was used as an eluent with a flow rate of 1.0 mL/min and polystyrene was used as calibration standard. A Bruker 500 MHz NMR spectrometer instrument was used to acquire the1H NMR spectra of mPEG-Br and mPEG-b-PDPA using CDCl3 as solvent. The block copolymer compositions were determined by comparing appropriate integrals assigned to the different comonomers.


### 2.2.2. Transmission Electron Microscopy (TEM)

Transmission Electron Microscopy (TEM) images were performed on a JEM-1400 electron microscope operated at 100 kv. To prepare TEM samples, the liposome suspension was deposited on a carbon-coated copper grid and negatively stained with the phosphotungstic acid solution. Excess solution was absorbed and the samples were allowed to dry at ambient temperature.


### 2.2.3. Dynamic Light Scattering (DLS)

Dynamic light scattering (DLS) studies were carried out using a Zetasizer Nano ZS Instrument. The influence of pH on zeta-potential of liposomes was investigated in the range of pH 2–9 [17, 20]. The diblock copolymers were firstly dissolved in 0.01 M HCl to prepare stock solution at final a concentration of 0.1 mg/mL. The pH titration was carried out by adding small volume of 0.1 M NaOH solution under stirring. The change of pH values was monitored by using PHS-2C precision acidity meter. The average results were accepted as the final data measured at least three times.


### 2.2.4. Turbidity

The aggregation behavior of the copolymer was measured in a UV-Vis spectrophotometer (UV-2450, Shimadzu, Japan). The transmittance of the copolymer solution was monitored in a quartz cuvette (1 cm width) under various pH values.


### 2.2.5. Fluorescence Polarization

The fluorescence polarization (Pol) of liposome was measured by a LS55 fluorimeter (Perkin Elmer) equipped with automated polarizer. Liposome suspensions were prepared: 75μL of liposome suspension and 200 μL of DPH solution were added to the PBS buffer solution to be further diluted to 4 mL. The concentration of DPH was 2 mmol/L and lipid/DPH (w/w) was 800 : 1. In order to make the probes to be incorporated, the samples were shaken overnight at 37°C before measurements. The Pol values were measured at an excitation slit of 10 nm and emission slit of 5 nm and excitation and emission wavelengths of 360 and 425 nm, respectively. Fluorescence polarization was then calculated automatically by [23, 24](1)Pol=Ivv-GIvhIvv+GIvh,where Pol is the fluorescence polarization and Ivv and Ivh are the fluorescence intensities of the emitted light polarized parallel and perpendicular to the exciting light, respectively. G is the grating correction factor, which is equal to Ihv/Ihh, obtained by measuring the vertically and horizontally polarized emission intensities after excitation with horizontally polarized light.


## 2.2.1. Proton Nuclear Magnetic Resonance (1H NMR) and Gel Permeation Chromatography (GPC) Characterization

Molecular weight and polydispersity index (PDI) of mPEG-b-PDPA copolymers were determined by gel permeation chromatography (GPC) using a Waters 1515 instrument at 25°C. THF was used as an eluent with a flow rate of 1.0 mL/min and polystyrene was used as calibration standard. A Bruker 500 MHz NMR spectrometer instrument was used to acquire the1H NMR spectra of mPEG-Br and mPEG-b-PDPA using CDCl3 as solvent. The block copolymer compositions were determined by comparing appropriate integrals assigned to the different comonomers.


## 2.2.2. Transmission Electron Microscopy (TEM)

Transmission Electron Microscopy (TEM) images were performed on a JEM-1400 electron microscope operated at 100 kv. To prepare TEM samples, the liposome suspension was deposited on a carbon-coated copper grid and negatively stained with the phosphotungstic acid solution. Excess solution was absorbed and the samples were allowed to dry at ambient temperature.


## 2.2.3. Dynamic Light Scattering (DLS)

Dynamic light scattering (DLS) studies were carried out using a Zetasizer Nano ZS Instrument. The influence of pH on zeta-potential of liposomes was investigated in the range of pH 2–9 [17, 20]. The diblock copolymers were firstly dissolved in 0.01 M HCl to prepare stock solution at final a concentration of 0.1 mg/mL. The pH titration was carried out by adding small volume of 0.1 M NaOH solution under stirring. The change of pH values was monitored by using PHS-2C precision acidity meter. The average results were accepted as the final data measured at least three times.


## 2.2.4. Turbidity

The aggregation behavior of the copolymer was measured in a UV-Vis spectrophotometer (UV-2450, Shimadzu, Japan). The transmittance of the copolymer solution was monitored in a quartz cuvette (1 cm width) under various pH values.


## 2.2.5. Fluorescence Polarization

The fluorescence polarization (Pol) of liposome was measured by a LS55 fluorimeter (Perkin Elmer) equipped with automated polarizer. Liposome suspensions were prepared: 75μL of liposome suspension and 200 μL of DPH solution were added to the PBS buffer solution to be further diluted to 4 mL. The concentration of DPH was 2 mmol/L and lipid/DPH (w/w) was 800 : 1. In order to make the probes to be incorporated, the samples were shaken overnight at 37°C before measurements. The Pol values were measured at an excitation slit of 10 nm and emission slit of 5 nm and excitation and emission wavelengths of 360 and 425 nm, respectively. Fluorescence polarization was then calculated automatically by [23, 24](1)Pol=Ivv-GIvhIvv+GIvh,where Pol is the fluorescence polarization and Ivv and Ivh are the fluorescence intensities of the emitted light polarized parallel and perpendicular to the exciting light, respectively. G is the grating correction factor, which is equal to Ihv/Ihh, obtained by measuring the vertically and horizontally polarized emission intensities after excitation with horizontally polarized light.


## 2.3. Synthesis of mPEG-Br Macroinitiator

mPEG-Br macroinitiator was synthesized according to the literature method [21, 25]. Typically, mPEG-OH (0.0086 mol) was dropped into 50 mL of dichloromethane. The flask containing the solution was placed in an ice bath, and trimethylamine (TEA) (0.0216 mol) was added to the solution. Then, 2-bromo-2-methylpropionyl bromide (0.0202 mol) was added dropwise to the solution over 1 h under stirring and then the reaction was continued for about 30 h at room temperature. The crude solution was washed with saturated sodium chloride solution and saturated sodium hydrogen carbonate solution for three times followed by extracting with dichloromethane. After that, anhydrous magnesium sulfate was added to the extract liquor and then filtered to remove insoluble impurities and concentrated by evaporation. The product was finally dried under vacuum for about 12 h.


## 2.4. Synthesis of mPEG-b-PDPA Diblock Copolymer

The diblock copolymer was synthesized by ATRP with mPEG-Br as initiator [26, 27]. In a typical ATRP procedure, a Schlenk flask with a magnetic stir bar and a rubber septum was charged with DPA monomer (12.657 mmol), mPEG-Br macroinitiator (0.8438 mmol), PMDETA (0.9282 mmol), and anhydrous tetrahydrofuran (6.0 mL). This mixture was deoxygenated by bubbling N2 for 0.5 h before adding CuIBr catalyst (0.8438 mmol). The reactant mixture was degassed by three freezing-thawing cycles. Afterwards, the polymerization reaction was carried out in an oil bath preheated at 55°C for 12 h. Finally, the reaction solution was diluted by addition of THF and then passed through a neutral alumina column to remove the copper catalysts. The diblock copolymer was then washed by Milli-Q water for at least 3 times and dried under vacuum for 24 h.


## 2.5. Preparation of Liposomes

Liposomes were prepared by a thin lipid film hydration method [28]. In brief, HSPC or DOPC, DC-cholesterol, and different mole ratio of diblock copolymer were dissolved in chloroform in a round bottom flask. Then a film was formed by rotary evaporation of the solvent at the temperature of 45°C and then organic solvent was volatilized completely after 1 h. The lipid film was hydrated with 5 mL of ammonium sulfate solution at 60°C to achieve a final lipid concentration of 1 mg/mL. Following hydration, uniform liposomes were obtained by extrusion at 60°C through 400 nm polycarbonate filter 11 times and then 200 nm filter 7 times by using a LiposoFast.


## 2.6. Drug Loading

The active transport method was used to encapsulate DOX into liposome. The liposome suspension was dialyzed against the 0.9% NaCl solution using dialysis tubes (cutoffMn=14000) to remove the free ammonium sulfate acid. Then, the suspension was placed in a flask. DOX solution (2.5 mg/mL) was mixed with the liposome suspension at the molar ratio of 1 : 10 (DOX : lipids). The unloaded free DOX was removed through a Sephadex G-50 column. The liposomes loaded with DOX were collected and mixed with Triton X-100 for measuring encapsulated amount. The total DOX amount A1 and encapsulated DOX amount A0 were determined by the absorbing intensity at 485 nm (UV-2450, Shimadzu). The encapsulated efficiency (E%) was calculated based on [29](2)E%=A0A1×100%.


## 2.7.In Vitro DOX Release

In vitro DOX release was carried under various pH values (pH 6.0 or 7.4). 1 mL of DOX-loaded liposome suspension was moved to a dialysis tube (cutoff Mn=14000), which was exposed to 25 mL of PBS solution at 37°C. The cumulative release amount of DOX at different time At was measured and the release percentage was calculated:(3)Cumulative  release%=AtA0×100%.


## 3. Results and Discussions

### 3.1. Synthesis of mPEG-PDPA

The mPEG-b-PDPA diblock copolymers with different block lengths were synthesized [30]. Considering the thickness of the lipid bilayer, not very long chains were selected for PDPA (n=10, 15, and 22). The properties of the copolymers, determined by GPC and 1H NMR, were shown in Table 1 and Figure 1. These diblock copolymers had a small polydispersity index (PDI), showing that the distributions of mPEG-b-PDPA were narrow, uniform, and well controlled. Various degrees of polymerization of the copolymers can be obtained by changing the feed ratio of raw materials. GPC curves (not shown) revealed that unimodal peak and no tailing in the low molecular weight were observed. 1H NMR spectra of mPEG-Br and mPEG-b-PDPA with the relevant peaks were illustrated in Figure 1. As shown in Figure 1(A), the peaks at δ3.60 and δ3.33 ppm were assigned to protons of -CH2-CH2 and -OCH3 groups of the mPEG-Br, respectively. The peak at δ1.96 ppm belonged to -C(CH3)2- groups. Compared with the 1H NMR spectrum of mPEG-Br (Figure 1(A)), the characteristic peaks at δ0.97 and δ2.60 ppm appeared in the spectrum of mPEG-b-PDPA (Figure 1(B)), which were assigned to -CH-(CH3)2- and O-CH2-CH2-N- groups, indicating the presence of PDPA. According to these results, the copolymers of the desired structures were successfully synthesized.Table 1
GPC,1H NMR, and triggering pH values of mPEG-b-PDPA diblock copolymers.
Copolymer
Composition
M
n
,
N
M
R (gmol−1)
M
n
,
G
P
C (gmol−1)
PDI (Mw/Mn)
Triggering pH
1
mPEG8-b-PDPA10
2632
4171
1.37
6.36
2
mPEG8-b-PDPA15
3699
4037
1.22
6.47
3
mPEG8-b-PDPA22
5192
7227
1.19
6.54Figure 1
1H NMR spectra (CDCl3) of mPEG-Br (A) and mPEG-b-PDPA (B).


### 3.2. pH-Sensitivity of mPEG-b-PDPA Diblock Copolymers

The diblock copolymers responded to the change of environmental pH. In order to obtain a better understanding of the pH-sensitive mPEG-b-PDPA copolymers, the properties of copolymers in a certain pH range had been investigated. Figure2(a) shows the zeta-potential of the copolymers under different pH values. At low pH, the tertiary amine groups of PDPA block were protonated, which provided high positive zeta-potential. With increasing pH, the tertiary amine groups of PDPA block were deprotonated gradually, which induced a transition in charges from positive to negative values. As shown in Figure 2(a), the isoelectric points (IEP) of these copolymers were in a range of pH 6.5–7.0. Thus, it clearly revealed that the property of the diblock copolymers was significantly affected by pH of the solution. The transmittances of copolymer solutions at different pH values were measured and shown in Figure 2(b). The triggering pH values of the diblock copolymers, which could be determined at a certain pH value when the solution suddenly became turbid, were listed in Table 1. It could be seen that the triggering pH values increased slightly with the increase of PDPA length. This might be due to the fact that more tertiary amine groups need to be deprotonated when the PDPA lengths increased.Figure 2
The pH-sensitivity of diblock copolymers. Zeta-potential (a) and transmittance (b) of copolymers measured as a function of pH (concentration of copolymer: 0.1 mg/mL).
(a)
(b)


### 3.3. The pH-Sensitivity of Hybrid Liposomes

The pH-sensitive hybrid liposomes were prepared by incorporating diblock copolymers into the liposome bilayer membranes with different molar ratios. The physicochemical properties of the liposomes were summarized in Table2. In this work, the molar ratio between phospholipids and cholesterol was always 5 : 1.Table 2
Compositions and properties of the liposomes (pH 7.4).
Liposome
Composition of liposomea
Copolymer percentage
Diameter (nm)
PDI
Zeta-potential (mV)
Lp1
HSPC
0
139.3 ± 4.0
0.151
10.3 ± 0.8
Lp2
HSPC : polymer(mPEG8-b-PDPA10)
5%
173.2 ± 8.0
0.229
13.6 ± 1.4
Lp3
HSPC : polymer(mPEG8-b-PDPA15)
5%
183.7 ± 8.0
0.246
15.8 ± 1.4
Lp4
HSPC : polymer(mPEG8-b-PDPA22)
2%
179.9 ± 8.0
0.219
15.7 ± 1.4
Lp5
HSPC : polymer(mPEG8-b-PDPA22)
5%
198.8 ± 8.0
0.250
16.9 ± 1.4
Lp6
HSPC : polymer(mPEG8-b-PDPA22)
10%
206.2 ± 8.0
0.334
18.7 ± 1.4
Lp7
HSPC : DOPC (1 : 1)
0
146.0 ± 4.0
0.178
11.6 ± 1.4
Lp8
HSPC : DOPC (1 : 1) : polymer(mPEG8-b-PDPA10)
5%
163.5 ± 8.0
0.207
17.2 ± 1.4
Lp9
HSPC : DOPC (1 : 1) : polymer(mPEG8-b-PDPA15)
5%
175.1 ± 8.0
0.210
16.1 ± 1.4
Lp10
HSPC : DOPC (1 : 1) : polymer(mPEG8-b-PDPA22)
5%
187.3 ± 8.0
0.207
17.2 ± 1.4
aCholesterol was contained in all liposomes and the molar ratio between lipid and cholesterol was 5 : 1.As shown in Table2, pH-sensitive hybrid liposomes appeared to be larger than the pure liposome (Lp1) under pH 7.4, which may be due to the stretching PEG chains from the bilayer. It could be seen that the sizes of Lp2, Lp3, and Lp5 were somewhat increased, which was thought to depend on the increase of PDPA lengths. The sizes of hybrid liposomes were found not to change when pH decreased from 7.4 to 6.0 as shown in Figure 3. Their zeta-potentials under pH 7.4 were also shown in Table 2, which were found to be the same as their values under pH 6.0. The results revealed that the vesicle structures of hybrid liposomes were not destroyed by the stimulation of pH, which should relate to their positive zeta-potentials and the PEG extending on the surface. The morphology of liposome was examined by TEM (Figure 2, inset). The TEM images showed round-shaped vesicles whose sizes were found consistent with the diameters obtained by DLS. TEM images also revealed that the vesicle structures of liposomes still exist when the condition changed from neutral to weak acid.Figure 3
Size distributions and TEM images (inset, bar: 200 nm) of Lp1 (a) and Lp5 (b) under pH 6.0 and pH 7.4, separately. The concentration of the liposome suspension was 1.0 mg/mL.
(a)
(b)Then, Pol measurements were performed. DPH was used as a fluorescence probe to investigate the membrane fluidity of the liposomes [31, 32]. The behavior of fluorescence probe in liposomal membranes was deemed to reflect the behavior of lipids. The lower the value of the Pol, the higher the fluidity (i.e., lower stability) of the liposomal membrane. The Pol values of the liposome bilayer membrane were found almost constant over time under pH 7.4. As shown in Figure 4(a), the Pol values increased obviously when 5% of diblock copolymers were incorporated (Lp3 and Lp5), compared with pure liposome (Lp1). Except for Lp2, its Pol value had a slight decrease, which may be due to the short length of PDPA chain. A shorter PDPA (PDPA10) had a length similar to the thickness of liposomal single-layer. Therefore, copolymer1(mPEG8-b-PDPA10) could not reach the second layer of the liposome and could not act as a lock to fix the bilayer. The insertion of copolymer1, on the contrary, led to a slight decrease in membrane stability. The Pol values of Lp3 and Lp5 significantly increased, suggesting that the copolymers with longer PDPA could go across the whole lipid bilayer and enhanced the membrane stability.Figure 4
(a) Polarization of pure and hybrid liposomes at pH 7.4; (b) polarization of liposomes at pH 6.0 measured as a function of time. The molar ratio of copolymers was 5%.
(a)
(b)Figure4(b) reveals the Pol values of various liposomes measured as a function of time under pH 6.0. For pure liposome (Lp1), when pH decreased from 7.4 to 6.0, the Pol values were found not to change over the whole time period, indicating pH did not affect its membrane fluidity. However, Pol values of Lp3 and Lp5 decreased obviously at pH 6.0. This was thought to result from the escape of the copolymers from liposomes. The copolymers became completely hydrophilic and then could not stay in the lipid bilayer when the PDPA block protonated. After about 18 h, their Pol values became close to that of Lp1, suggesting a pure liposome state came back again. Certainly, the Pol value of Lp2 also tended to approach that of pure liposome.


### 3.4. Effect of PDPA Length on Release

In order to assess the drug loading and releasing of the liposomes, DOX was used as a model drug. DOX is a water-soluble anticancer drug in its hydrochloride salt form. Herein, DOX was encapsulated into liposomes using an active loading method and the drug loading efficiency was over 80%. Experiment of DOX release from liposome was performed in PBS solution with different pH values (pH 6.0 and pH 7.4) at 37°C. Copolymers with different lengths had been synthesized in this work to study the effect of PDPA segment size on the release behavior. The compositions and properties of the corresponding liposomes (Lp2, Lp3, and Lp5) were summarized in Table2. Their DOX release profiles were investigated and shown in Figure 5.Figure 5
Cumulative release profiles of DOX from pure liposome and hybrid liposomes inserted by copolymers with different PDPA segment sizes. Solid symbol: pH 6.0. Open symbol: pH 7.4. The molar ratio of copolymers was 5%.For the pure liposome, no significant differences (about 26.5% and 24.4%) were observed in the drug release profiles under both pH values, suggesting that pH itself did not affect the membrane permeability. However, for liposomes incorporated with diblock copolymers, the drug release profiles showed different behaviors depending on pH. Under pH 7.4, the drug release from the hybrid liposomes (except for Lp2) decreased to be 18.1% (Lp3) and 15.1% (Lp5) compared with that of Lp1, indicating that drug leakage was inhibited. And under pH 6.0, the drug releases of the three hybrid liposomes obviously increased, which were 39.1% (Lp2), 43.3% (Lp3), and 53.2% (Lp5). For Lp5, the difference in cumulative release percentage between the two pH values increased by about 40%, which was most remarkable. The results highlighted that copolymers with proper length of PDPA played an important role, that is, acted as an intelligent lock in lipid bilayer to inhibit the drug leakage under neutral environment and enhance the release under weak acidic condition. The enhanced release occurring at pH 6.0 was thought to result from the escaping of copolymers from the liposomes [17]. From the results of polarization (Figure 4), the PDPA block of copolymer was protonated gradually under pH 6.0. It could be thought that a polymer began to escape from liposomes when the protonation is completed and at that time the quick release could begin. From Figure 4(b), the first 6 h was mainly a protonation process and after that it was an escaping process. Comparing this with the behaviors of drug release shown in Figure 5, it could be easy to understand that the improvement in release rate of hybrid liposomes is not very significant during the first 5-6 h comparing with that of pure liposome. A quick release step was found to continue till the copolymers have left completely. Copolymers with longer PDPA should require more time to complete the protonation and seemed to give the lipid bilayer more long-time disturbance. The copolymer mPEG8-b-PDPA22 was considered a candidate incorporated into liposomes for the next studies.


### 3.5. Effect of Insertion Ratio on Release

The drug release profiles of liposomes with 0 (Lp1), 2% (Lp4), 5% (Lp5), and 10% (Lp6) copolymer3 and their liposomal fluorescence polarization were shown in Figure 6. As shown in Figure 6(a), compared with that of Lp1, the Pol values of Lp4–Lp6 increased, where the Lp5 improved most obviously. The PDPA block of the copolymer3 was thought to be long enough to go across the whole lipid bilayer and then acted as locks in the fluid membrane (as illustrated in Figure 6(b)). Their release profiles were obtained under both pH values as shown in Figure 6(c). With incorporating copolymers, the drug release rate of hybrid liposomes decreased at pH 7.4 and increased at pH 6.0, compared with pure liposome. The results suggested that the insertion of the copolymer significantly enhanced the stability of liposome in neutral condition, while the DOX release was stimulated when exposed to weak acidic environment. For Lp5, it had the most remarkable differences between the two pH values, and the cumulative release percentage improved from 15.1% to 53.2% when pH decreased from 7.4 to 6.0. However, beyond our expectation, the Lp6, incorporating much more copolymer, did not have the most significant pH-controlled effect on release. Its accumulated release percentages were 18.5% and 54.7%, respectively. It was thought that too much copolymers inserted into liposomes could impact the spatial structure of vesicle. Here, the DOX leakage at pH 7.4 had somewhat increased, which was consistent with the results of Pol. It was well demonstrated that proper amount of diblock copolymers incorporated into liposome was able to effectively decrease the drug leakage at pH 7.4 and promote the drug release under pH 6.0.Figure 6
(a) The Pol values of hybrid liposomes incorporated with various copolymer contents at pH 7.4 measured immediately after preparation; (b) scheme of copolymers inserting into lipid bilayer as locks; (c) cumulative release profiles of DOX from liposomes inserted by various ratios of mPEG8-b-PDPA22 under pH 6.0 and pH 7.4 at 37°C.
(a)
(b)
(c)


### 3.6. Effect of Lipid Composition on Release

To our knowledge, the composition of liposome plays an important role in the functions of liposome membrane, such as fluidity or permeability [33]. The above results demonstrated that the maximum release amount of DOX could only reach as high as 55% even at pH 6.0. To improve the DOX release efficiency, DOPC, a kind of phospholipids with unsaturated bond, was added to liposome bilayer for adjusting membrane fluidity. Here, HSPC to DOPC at molar ratio of 1 : 1 was selected.The effect of liposome composition on DOX release was also investigated and shown in Figure7(a). As shown in Figure 7(a) with increase of PDPA length, the values of accumulated release amount were increased from 63.6% to 73.8%, 81.9%, and 93.4% at pH 6.0. The cumulative release amount of liposomes with DOPC significantly improved, in comparison with those of liposomes without DOPC (see Figure 5). In addition, it was easy to find that the drug release profiles of pure liposome with DOPC (Lp7) did almost the same behavior under pH 6.0 and pH 7.4. Like the results of Lp1 (Figure 5), the accumulated release amounts were almost the same, 66.7% and 63.6%, respectively. Among hybrid liposomes, Lp10 showed the best pH-controlled effect on DOX release, and the difference in release percentage between pH 6.0 and pH 7.4 was about 60%. The maximum amount of DOX release meant almost all cargos had been released into solution at pH 6.0.Figure 7
(a) Cumulative release profiles of DOX from liposomes containing DOPC and (b) their polarization measured as a function of time under pH 7.4 and pH 6.0 at 37°C. Solid symbol: pH 6.0. Open symbol: pH 7.4.
(a)
(b)It was known that the insertion of DOPC could increase the fluidity of lipid bilayer [22]. Then, the polarization of Lp7 and Lp10 was measured under two pH values as a function of time. Firstly, as shown in Figure 7(b), the Pol values of Lp7 and Lp10 were lower than those of liposomes without DOPC (as shown in Figure 6(a)). Secondly, the Pol values of Lp7 were almost constant under both pH values, which was similar to Lp1. For Lp10, its Pol value under pH 7.4 was found to be higher than that of Lp7 and almost did not change over time. When pH decreased to 6.0, the Pol values of Lp10 reduced rapidly and almost reached the values of Lp7 after 13 h. The Pol results of liposomes seemed to be consistent with the results of DOX release. Compared to the Pol of liposomes with and without DOPC, we could find that the time needed for the recovery of the polarization value to that of pure liposome was not the same, which was 13 h and 20 h, respectively. It was thought that when the copolymers escaped from liposome, the micropores left on the lipid bilayer and induced a rapid release. The higher fluidity membrane of the liposomes containing DOPC seemed to make the micropores disappear more quickly. This induced different release behaviors of Lp5 and Lp10.From these results, the DOX release profile could be separated into two steps: rapid and gradual release steps. It was thought that the rapid drug release was dependent on both permeation and diffusion through micropores left by the escaping copolymers. After the copolymers escaped completely, the micropores disappeared due to the fluidity of lipid bilayer. Then, the release began to rely on the membrane permeability resulting in a slow release process. The results showed that the rapid release step of Lp5 and Lp10 needed about 20 h and 13 h, respectively.


## 3.1. Synthesis of mPEG-PDPA

The mPEG-b-PDPA diblock copolymers with different block lengths were synthesized [30]. Considering the thickness of the lipid bilayer, not very long chains were selected for PDPA (n=10, 15, and 22). The properties of the copolymers, determined by GPC and 1H NMR, were shown in Table 1 and Figure 1. These diblock copolymers had a small polydispersity index (PDI), showing that the distributions of mPEG-b-PDPA were narrow, uniform, and well controlled. Various degrees of polymerization of the copolymers can be obtained by changing the feed ratio of raw materials. GPC curves (not shown) revealed that unimodal peak and no tailing in the low molecular weight were observed. 1H NMR spectra of mPEG-Br and mPEG-b-PDPA with the relevant peaks were illustrated in Figure 1. As shown in Figure 1(A), the peaks at δ3.60 and δ3.33 ppm were assigned to protons of -CH2-CH2 and -OCH3 groups of the mPEG-Br, respectively. The peak at δ1.96 ppm belonged to -C(CH3)2- groups. Compared with the 1H NMR spectrum of mPEG-Br (Figure 1(A)), the characteristic peaks at δ0.97 and δ2.60 ppm appeared in the spectrum of mPEG-b-PDPA (Figure 1(B)), which were assigned to -CH-(CH3)2- and O-CH2-CH2-N- groups, indicating the presence of PDPA. According to these results, the copolymers of the desired structures were successfully synthesized.Table 1
GPC,1H NMR, and triggering pH values of mPEG-b-PDPA diblock copolymers.
Copolymer
Composition
M
n
,
N
M
R (gmol−1)
M
n
,
G
P
C (gmol−1)
PDI (Mw/Mn)
Triggering pH
1
mPEG8-b-PDPA10
2632
4171
1.37
6.36
2
mPEG8-b-PDPA15
3699
4037
1.22
6.47
3
mPEG8-b-PDPA22
5192
7227
1.19
6.54Figure 1
1H NMR spectra (CDCl3) of mPEG-Br (A) and mPEG-b-PDPA (B).


## 3.2. pH-Sensitivity of mPEG-b-PDPA Diblock Copolymers

The diblock copolymers responded to the change of environmental pH. In order to obtain a better understanding of the pH-sensitive mPEG-b-PDPA copolymers, the properties of copolymers in a certain pH range had been investigated. Figure2(a) shows the zeta-potential of the copolymers under different pH values. At low pH, the tertiary amine groups of PDPA block were protonated, which provided high positive zeta-potential. With increasing pH, the tertiary amine groups of PDPA block were deprotonated gradually, which induced a transition in charges from positive to negative values. As shown in Figure 2(a), the isoelectric points (IEP) of these copolymers were in a range of pH 6.5–7.0. Thus, it clearly revealed that the property of the diblock copolymers was significantly affected by pH of the solution. The transmittances of copolymer solutions at different pH values were measured and shown in Figure 2(b). The triggering pH values of the diblock copolymers, which could be determined at a certain pH value when the solution suddenly became turbid, were listed in Table 1. It could be seen that the triggering pH values increased slightly with the increase of PDPA length. This might be due to the fact that more tertiary amine groups need to be deprotonated when the PDPA lengths increased.Figure 2
The pH-sensitivity of diblock copolymers. Zeta-potential (a) and transmittance (b) of copolymers measured as a function of pH (concentration of copolymer: 0.1 mg/mL).
(a)
(b)


## 3.3. The pH-Sensitivity of Hybrid Liposomes

The pH-sensitive hybrid liposomes were prepared by incorporating diblock copolymers into the liposome bilayer membranes with different molar ratios. The physicochemical properties of the liposomes were summarized in Table2. In this work, the molar ratio between phospholipids and cholesterol was always 5 : 1.Table 2
Compositions and properties of the liposomes (pH 7.4).
Liposome
Composition of liposomea
Copolymer percentage
Diameter (nm)
PDI
Zeta-potential (mV)
Lp1
HSPC
0
139.3 ± 4.0
0.151
10.3 ± 0.8
Lp2
HSPC : polymer(mPEG8-b-PDPA10)
5%
173.2 ± 8.0
0.229
13.6 ± 1.4
Lp3
HSPC : polymer(mPEG8-b-PDPA15)
5%
183.7 ± 8.0
0.246
15.8 ± 1.4
Lp4
HSPC : polymer(mPEG8-b-PDPA22)
2%
179.9 ± 8.0
0.219
15.7 ± 1.4
Lp5
HSPC : polymer(mPEG8-b-PDPA22)
5%
198.8 ± 8.0
0.250
16.9 ± 1.4
Lp6
HSPC : polymer(mPEG8-b-PDPA22)
10%
206.2 ± 8.0
0.334
18.7 ± 1.4
Lp7
HSPC : DOPC (1 : 1)
0
146.0 ± 4.0
0.178
11.6 ± 1.4
Lp8
HSPC : DOPC (1 : 1) : polymer(mPEG8-b-PDPA10)
5%
163.5 ± 8.0
0.207
17.2 ± 1.4
Lp9
HSPC : DOPC (1 : 1) : polymer(mPEG8-b-PDPA15)
5%
175.1 ± 8.0
0.210
16.1 ± 1.4
Lp10
HSPC : DOPC (1 : 1) : polymer(mPEG8-b-PDPA22)
5%
187.3 ± 8.0
0.207
17.2 ± 1.4
aCholesterol was contained in all liposomes and the molar ratio between lipid and cholesterol was 5 : 1.As shown in Table2, pH-sensitive hybrid liposomes appeared to be larger than the pure liposome (Lp1) under pH 7.4, which may be due to the stretching PEG chains from the bilayer. It could be seen that the sizes of Lp2, Lp3, and Lp5 were somewhat increased, which was thought to depend on the increase of PDPA lengths. The sizes of hybrid liposomes were found not to change when pH decreased from 7.4 to 6.0 as shown in Figure 3. Their zeta-potentials under pH 7.4 were also shown in Table 2, which were found to be the same as their values under pH 6.0. The results revealed that the vesicle structures of hybrid liposomes were not destroyed by the stimulation of pH, which should relate to their positive zeta-potentials and the PEG extending on the surface. The morphology of liposome was examined by TEM (Figure 2, inset). The TEM images showed round-shaped vesicles whose sizes were found consistent with the diameters obtained by DLS. TEM images also revealed that the vesicle structures of liposomes still exist when the condition changed from neutral to weak acid.Figure 3
Size distributions and TEM images (inset, bar: 200 nm) of Lp1 (a) and Lp5 (b) under pH 6.0 and pH 7.4, separately. The concentration of the liposome suspension was 1.0 mg/mL.
(a)
(b)Then, Pol measurements were performed. DPH was used as a fluorescence probe to investigate the membrane fluidity of the liposomes [31, 32]. The behavior of fluorescence probe in liposomal membranes was deemed to reflect the behavior of lipids. The lower the value of the Pol, the higher the fluidity (i.e., lower stability) of the liposomal membrane. The Pol values of the liposome bilayer membrane were found almost constant over time under pH 7.4. As shown in Figure 4(a), the Pol values increased obviously when 5% of diblock copolymers were incorporated (Lp3 and Lp5), compared with pure liposome (Lp1). Except for Lp2, its Pol value had a slight decrease, which may be due to the short length of PDPA chain. A shorter PDPA (PDPA10) had a length similar to the thickness of liposomal single-layer. Therefore, copolymer1(mPEG8-b-PDPA10) could not reach the second layer of the liposome and could not act as a lock to fix the bilayer. The insertion of copolymer1, on the contrary, led to a slight decrease in membrane stability. The Pol values of Lp3 and Lp5 significantly increased, suggesting that the copolymers with longer PDPA could go across the whole lipid bilayer and enhanced the membrane stability.Figure 4
(a) Polarization of pure and hybrid liposomes at pH 7.4; (b) polarization of liposomes at pH 6.0 measured as a function of time. The molar ratio of copolymers was 5%.
(a)
(b)Figure4(b) reveals the Pol values of various liposomes measured as a function of time under pH 6.0. For pure liposome (Lp1), when pH decreased from 7.4 to 6.0, the Pol values were found not to change over the whole time period, indicating pH did not affect its membrane fluidity. However, Pol values of Lp3 and Lp5 decreased obviously at pH 6.0. This was thought to result from the escape of the copolymers from liposomes. The copolymers became completely hydrophilic and then could not stay in the lipid bilayer when the PDPA block protonated. After about 18 h, their Pol values became close to that of Lp1, suggesting a pure liposome state came back again. Certainly, the Pol value of Lp2 also tended to approach that of pure liposome.


## 3.4. Effect of PDPA Length on Release

In order to assess the drug loading and releasing of the liposomes, DOX was used as a model drug. DOX is a water-soluble anticancer drug in its hydrochloride salt form. Herein, DOX was encapsulated into liposomes using an active loading method and the drug loading efficiency was over 80%. Experiment of DOX release from liposome was performed in PBS solution with different pH values (pH 6.0 and pH 7.4) at 37°C. Copolymers with different lengths had been synthesized in this work to study the effect of PDPA segment size on the release behavior. The compositions and properties of the corresponding liposomes (Lp2, Lp3, and Lp5) were summarized in Table2. Their DOX release profiles were investigated and shown in Figure 5.Figure 5
Cumulative release profiles of DOX from pure liposome and hybrid liposomes inserted by copolymers with different PDPA segment sizes. Solid symbol: pH 6.0. Open symbol: pH 7.4. The molar ratio of copolymers was 5%.For the pure liposome, no significant differences (about 26.5% and 24.4%) were observed in the drug release profiles under both pH values, suggesting that pH itself did not affect the membrane permeability. However, for liposomes incorporated with diblock copolymers, the drug release profiles showed different behaviors depending on pH. Under pH 7.4, the drug release from the hybrid liposomes (except for Lp2) decreased to be 18.1% (Lp3) and 15.1% (Lp5) compared with that of Lp1, indicating that drug leakage was inhibited. And under pH 6.0, the drug releases of the three hybrid liposomes obviously increased, which were 39.1% (Lp2), 43.3% (Lp3), and 53.2% (Lp5). For Lp5, the difference in cumulative release percentage between the two pH values increased by about 40%, which was most remarkable. The results highlighted that copolymers with proper length of PDPA played an important role, that is, acted as an intelligent lock in lipid bilayer to inhibit the drug leakage under neutral environment and enhance the release under weak acidic condition. The enhanced release occurring at pH 6.0 was thought to result from the escaping of copolymers from the liposomes [17]. From the results of polarization (Figure 4), the PDPA block of copolymer was protonated gradually under pH 6.0. It could be thought that a polymer began to escape from liposomes when the protonation is completed and at that time the quick release could begin. From Figure 4(b), the first 6 h was mainly a protonation process and after that it was an escaping process. Comparing this with the behaviors of drug release shown in Figure 5, it could be easy to understand that the improvement in release rate of hybrid liposomes is not very significant during the first 5-6 h comparing with that of pure liposome. A quick release step was found to continue till the copolymers have left completely. Copolymers with longer PDPA should require more time to complete the protonation and seemed to give the lipid bilayer more long-time disturbance. The copolymer mPEG8-b-PDPA22 was considered a candidate incorporated into liposomes for the next studies.


## 3.5. Effect of Insertion Ratio on Release

The drug release profiles of liposomes with 0 (Lp1), 2% (Lp4), 5% (Lp5), and 10% (Lp6) copolymer3 and their liposomal fluorescence polarization were shown in Figure 6. As shown in Figure 6(a), compared with that of Lp1, the Pol values of Lp4–Lp6 increased, where the Lp5 improved most obviously. The PDPA block of the copolymer3 was thought to be long enough to go across the whole lipid bilayer and then acted as locks in the fluid membrane (as illustrated in Figure 6(b)). Their release profiles were obtained under both pH values as shown in Figure 6(c). With incorporating copolymers, the drug release rate of hybrid liposomes decreased at pH 7.4 and increased at pH 6.0, compared with pure liposome. The results suggested that the insertion of the copolymer significantly enhanced the stability of liposome in neutral condition, while the DOX release was stimulated when exposed to weak acidic environment. For Lp5, it had the most remarkable differences between the two pH values, and the cumulative release percentage improved from 15.1% to 53.2% when pH decreased from 7.4 to 6.0. However, beyond our expectation, the Lp6, incorporating much more copolymer, did not have the most significant pH-controlled effect on release. Its accumulated release percentages were 18.5% and 54.7%, respectively. It was thought that too much copolymers inserted into liposomes could impact the spatial structure of vesicle. Here, the DOX leakage at pH 7.4 had somewhat increased, which was consistent with the results of Pol. It was well demonstrated that proper amount of diblock copolymers incorporated into liposome was able to effectively decrease the drug leakage at pH 7.4 and promote the drug release under pH 6.0.Figure 6
(a) The Pol values of hybrid liposomes incorporated with various copolymer contents at pH 7.4 measured immediately after preparation; (b) scheme of copolymers inserting into lipid bilayer as locks; (c) cumulative release profiles of DOX from liposomes inserted by various ratios of mPEG8-b-PDPA22 under pH 6.0 and pH 7.4 at 37°C.
(a)
(b)
(c)


## 3.6. Effect of Lipid Composition on Release

To our knowledge, the composition of liposome plays an important role in the functions of liposome membrane, such as fluidity or permeability [33]. The above results demonstrated that the maximum release amount of DOX could only reach as high as 55% even at pH 6.0. To improve the DOX release efficiency, DOPC, a kind of phospholipids with unsaturated bond, was added to liposome bilayer for adjusting membrane fluidity. Here, HSPC to DOPC at molar ratio of 1 : 1 was selected.The effect of liposome composition on DOX release was also investigated and shown in Figure7(a). As shown in Figure 7(a) with increase of PDPA length, the values of accumulated release amount were increased from 63.6% to 73.8%, 81.9%, and 93.4% at pH 6.0. The cumulative release amount of liposomes with DOPC significantly improved, in comparison with those of liposomes without DOPC (see Figure 5). In addition, it was easy to find that the drug release profiles of pure liposome with DOPC (Lp7) did almost the same behavior under pH 6.0 and pH 7.4. Like the results of Lp1 (Figure 5), the accumulated release amounts were almost the same, 66.7% and 63.6%, respectively. Among hybrid liposomes, Lp10 showed the best pH-controlled effect on DOX release, and the difference in release percentage between pH 6.0 and pH 7.4 was about 60%. The maximum amount of DOX release meant almost all cargos had been released into solution at pH 6.0.Figure 7
(a) Cumulative release profiles of DOX from liposomes containing DOPC and (b) their polarization measured as a function of time under pH 7.4 and pH 6.0 at 37°C. Solid symbol: pH 6.0. Open symbol: pH 7.4.
(a)
(b)It was known that the insertion of DOPC could increase the fluidity of lipid bilayer [22]. Then, the polarization of Lp7 and Lp10 was measured under two pH values as a function of time. Firstly, as shown in Figure 7(b), the Pol values of Lp7 and Lp10 were lower than those of liposomes without DOPC (as shown in Figure 6(a)). Secondly, the Pol values of Lp7 were almost constant under both pH values, which was similar to Lp1. For Lp10, its Pol value under pH 7.4 was found to be higher than that of Lp7 and almost did not change over time. When pH decreased to 6.0, the Pol values of Lp10 reduced rapidly and almost reached the values of Lp7 after 13 h. The Pol results of liposomes seemed to be consistent with the results of DOX release. Compared to the Pol of liposomes with and without DOPC, we could find that the time needed for the recovery of the polarization value to that of pure liposome was not the same, which was 13 h and 20 h, respectively. It was thought that when the copolymers escaped from liposome, the micropores left on the lipid bilayer and induced a rapid release. The higher fluidity membrane of the liposomes containing DOPC seemed to make the micropores disappear more quickly. This induced different release behaviors of Lp5 and Lp10.From these results, the DOX release profile could be separated into two steps: rapid and gradual release steps. It was thought that the rapid drug release was dependent on both permeation and diffusion through micropores left by the escaping copolymers. After the copolymers escaped completely, the micropores disappeared due to the fluidity of lipid bilayer. Then, the release began to rely on the membrane permeability resulting in a slow release process. The results showed that the rapid release step of Lp5 and Lp10 needed about 20 h and 13 h, respectively.


## 4. Conclusion

In summary, diblock copolymers with pH-sensitive PDPA segments synthesized here had a pH triggering point at about 6.5. The pH-sensitive liposomes were prepared by inserting the copolymers into general liposomes. Diblock copolymers with different chain lengths and molar ratios had different effects on the stability of liposomes. The PDPA segment should be long enough to reach the second layer of the liposome and could act as a lock to fix the bilayer. At pH 7.4, the bilayer fluidity of pH-sensitive liposomes decreased due to the incorporation of copolymers with longer PDPA. Thus, the liposomes inhibited the leakage of DOX in comparison with that of pure liposome. When pH decreased to 6.0, the release efficiency of DOX had been improved because of copolymer escaping. The membrane property was found to give great impact on the pH-controllability. When DOPC improved membrane fluidity of the liposome, the maximum release amount reached over 90% and the difference in release amount under two pH environments increased to be 60%. The optimization of the lipid compositions provided a superior controlled drug release behavior. These results suggest that liposomes containing pH-sensitive diblock copolymer possess a promising potential application in drug delivery system.



---