# Highly Enhanced Vapor Sensing of Multiwalled Carbon Nanotube Network Sensors byn-Butylamine Functionalization

Authors: P. Slobodian; P. Riha; P. Cavallo; C. A. Barbero; R. Benlikaya; U. Cvelbar; D. Petras; P. Saha
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

The sensing of volatile organic compounds by multiwall carbon nanotube networks of randomly entangled pristine nanotubes or the nanotubes functionalized byn-butylamine, which were deposited on polyurethane supporting electrospinned nonwoven membrane, has been investigated. The results show that the sensing of volatile organic compounds by functionalized nanotubes considerably increases with respect to pristine nanotubes. The increase is highly dependent on used vapor polarity. For the case of highly polar methanol, the functionalized MWCNT network exhibits even more than eightfold higher sensitivity in comparison to the network prepared from pristine nanotubes.


---

## Body

## 1. Introduction

Carbon nanotube (CNT) networks many times referred to as buckypapers are able to detect various gases or even different organic vapors [1–3]. The mechanism of detection involves adsorption of analyte molecules on CNT surface by van der Waals forces. The strength of forces and the interaction area between CNTs and gas molecules raise the adsorption and increase the amount of adsorbed molecules. All this leads to the change of electron density on CNTs, the increase of contact resistance between touching nanotubes, and, consequently, the electrical resistance change of whole CNT networks [3].The vapor sensing properties of CNT networks can be improved by a nanotube surface alteration to affect affinity of vapor molecules. Mostly, oxidation [1, 4], plasma treatment [5, 6], or chemical functionalization [3, 7, 8] is used. The modified CNT networks with different selectivity to particular vapors or group of vapors may be assembled into multiple sensory heads sometimes called electronic nose. Comparison of the sensory head data with a library of responses may specify a monitored vapor.The aim of this study is to examine sensing properties ofn-butylamine functionalized multiwall carbon nanotube (MWCNT) networks attached to a supporting polyurethane nonwoven filter to solvent vapors of different polarities defined by total Hildebrand solubility parameter.


## 2. Experimental

### 2.1. Materials and Procedures

The purified MWCNTs of acetylene type were supplied by Sun Nanotech Co. Ltd., China (diameter 10–30 nm, length 1–10μm, purity >90%, and volume resistance 0.12 Ωcm according to supplier). The complete information about the used pristine MWCNT can be found in our previous work [9], where the results of TEM analysis are presented. The diameter of individual nanotubes was determined within the range 10 and 60 nm (100 measurements), the average diameter and standard deviation 15±6 nm, and the length from tenths of micron up to 3 μm. The nanotube wall consists of about 15 to 35 rolled layers of graphene.n-Butylamine (BuNH2), thionyl chloride (SOCl2), and dimethylformamide (DMF) were supplied by Sigma Aldrich and triethylamine by Merck. The functionalization which yields oxidized groups covalently attached onto nanotube surface was performed in mixture of H2SO4 + HNO3 under reflux for 0.5 hours. These groups are binding elements for the amine functional groups. BuNH2 functionalized nanotubes were prepared in a 250 mL round-bottomed flask filled with 0.3 g of MWNTs treated by HNO3 + H2SO4 and 30 mL of SOCl2. The mixture was stirred at 80°C for 24 h and then decanted and the rest of unreacted SOCl2 was removed under vacuum. Afterwards, 10 g of BuNH2 in 15 mL of DMF was added to the mixture and dispersed by sonication in a water bath at 35°C for 30 min. Finally, the reaction proceeded at 65–75°C for 24 h in the presence of triethylamine as a catalyst. The nanotubes were then rinsed by acetone and ethanol to remove any remains of modifiers before network preparation. The amine treated MWCNTs are further on denoted as MWCNT (BuNH2) and the pristine ones as MWCNT (pure).The nanotubes were used for the preparation of aqueous paste: 1.6 g of MWCNTs and ~50 mL of deionized water were mixed with the help of a mortar and pestle. The paste was then diluted in deionized water with sodium dodecyl sulfate (SDS) and 1-pentanol. Consequently, NaOH aqueous solution was added to adjust pH to the value of 10. The final nanotube concentration in the suspension was 0.3 wt. %, and the concentration of SDS and 1-pentanol was 0.1 M and 0.14 M, respectively. The dispersion was homogenized using UZ Sonopuls HD 2070 kit for 30 min at 50% power of the apparatus and in 50% pulse mode under the temperature of about 50°C [1]. The homogenized dispersion of nanotubes was vacuum filtered through the nonwoven polyurethane (PU) membrane. The disk-shaped filtration cake was washed several times by deionized water and methanol in situ. The cake forms an entangled nanotube network which is partially infiltrated into the membrane pores. This interlocked structure of MWCNT network and PU membrane is used as a sensor in sensing experiments.Polyurethane nonwoven porous membrane for MWCNT dispersion filtration was prepared by electrospinning. PU solution in dimethylformamide (DMF) based on 4,4′-methylene-bis(phenyl isocyanate) (MDI), poly(3methyl-1,5-pentanediol)-alt-(adipic, isophthalic acid) (PAIM), and 1,4-butanediol (BD) was synthesized in molar ratio 9 : 1 : 8 (PU 918) at 90°C for 6 hours. Per partes method of synthesis was used starting with preparation of prepolymer from MDI and PAIM and followed by addition of BD and remaining quantity of MDI. The prepared solution was diluted with DMF to reduce the viscosity to 1.3 Pas (PU concentration of 13 wt. %) and to increase the conductivity to 150μS/cm. Nanofibre layers were prepared from PU solution by the commercially available equipment SpinLine 120 (SPUR a.s., Zlin, Czech Republic, http://www.spur-nanotechnologies.cz) using nanofibre forming jets. The experimental conditions were as follows: relative humidity of 34%, temperature of 23°C, electric voltage applied to PU solution of 95 kV, distance between electrodes of 270 mm, and speed of supporting textile collecting nanofibres of 0.2 m/min. Nanofibre layer with area mass of about 2.5 g/m2 and average pore size distribution of about 500 nm was collected on the polypropylene nonwoven textile.


### 2.2. Characterization of Nanotube Networks

MWCNTs (pure) were analyzed via transmission electron microscopy (TEM) using microscope JEOL JEM 2010 at the accelerating voltage of 160 kV. The sample was deposited on 300 mesh copper grid with a carbon film (SPI, USA) from MWCNT dispersion in acetone prepared by ultrasonication and dried.The structure of PU filtering membrane and MWCNT networks were observed with the help of scanning electron microscope (SEM) Vega LMU, produced by Tescan Ltd. The samples were deposited on carbon targets and covered with a thin Au/Pd layer. For the observations, the regime of secondary electrons was chosen.The networks were also analyzed by X-ray photoelectron spectroscopy (XPS) on TFA XPS Physical Electronics instrument at the base pressure in the chamber of about 6 × 10−8 Pa. The samples were excited with X-rays over a 400 μm spot area with a monochromatic Al Kα1,2 radiation at 1486.6 eV. Photoelectrons were detected with a hemispherical analyzer positioned at an angle of 45° with respect to the normal to the sample surface. Survey-scan spectra were made at the pass energy of 187.85 eV, and the energy step was 0.4 eV. Individual high-resolution spectra for C1s were taken at a pass energy of 23.5 eV and 0.1 eV energy step. The concentration of elements was determined from survey spectra by MultiPak v7.3.1 software from Physical Electronics.Fourier transform infrared (FTIR) analyses of MWCNT samples in powder form prepared by KBr were performed using Thermo Scientific Nicolet IS5 spectrometer with ID1 transmission accessory.


### 2.3. Electrical Resistance Measurement

The electrical resistance of sensors (length 15 mm, width 5 mm, and thickness ca 0.3 mm) cut out from the prepared MWCNT network/PU membrane discs was measured along the sensor length by the two-point technique using multimeter Sefram 7338. The sensor was placed on a planar holder with Cu electrodes fixed on both of its sides. The holder with the sensor was placed into the gas chamber set on temperature 40°C; see schematic illustration in Figure1. The air as a gas carrier is pumped (flow rate 1.6 mL/s) through the silica gel into evaporation chamber, with temperature set to 100°C. The analyte (150 μL) was injected into evaporation chamber where it evaporated and its effect on the sensor resistance in gas sensing chamber was measured. The measurement was performed in three repeated 6-minute injection cycles. Experimental VOC used for testing performance of the sensor covered broad range of polarities from nonpolar solvents like hydrocarbons to polar alcohols.Figure 1
Schematic illustration of experimental setup for gas resistive sensors based on CNT/PUR segregated composite to concentration pulse of VOC vapors.


## 2.1. Materials and Procedures

The purified MWCNTs of acetylene type were supplied by Sun Nanotech Co. Ltd., China (diameter 10–30 nm, length 1–10μm, purity >90%, and volume resistance 0.12 Ωcm according to supplier). The complete information about the used pristine MWCNT can be found in our previous work [9], where the results of TEM analysis are presented. The diameter of individual nanotubes was determined within the range 10 and 60 nm (100 measurements), the average diameter and standard deviation 15±6 nm, and the length from tenths of micron up to 3 μm. The nanotube wall consists of about 15 to 35 rolled layers of graphene.n-Butylamine (BuNH2), thionyl chloride (SOCl2), and dimethylformamide (DMF) were supplied by Sigma Aldrich and triethylamine by Merck. The functionalization which yields oxidized groups covalently attached onto nanotube surface was performed in mixture of H2SO4 + HNO3 under reflux for 0.5 hours. These groups are binding elements for the amine functional groups. BuNH2 functionalized nanotubes were prepared in a 250 mL round-bottomed flask filled with 0.3 g of MWNTs treated by HNO3 + H2SO4 and 30 mL of SOCl2. The mixture was stirred at 80°C for 24 h and then decanted and the rest of unreacted SOCl2 was removed under vacuum. Afterwards, 10 g of BuNH2 in 15 mL of DMF was added to the mixture and dispersed by sonication in a water bath at 35°C for 30 min. Finally, the reaction proceeded at 65–75°C for 24 h in the presence of triethylamine as a catalyst. The nanotubes were then rinsed by acetone and ethanol to remove any remains of modifiers before network preparation. The amine treated MWCNTs are further on denoted as MWCNT (BuNH2) and the pristine ones as MWCNT (pure).The nanotubes were used for the preparation of aqueous paste: 1.6 g of MWCNTs and ~50 mL of deionized water were mixed with the help of a mortar and pestle. The paste was then diluted in deionized water with sodium dodecyl sulfate (SDS) and 1-pentanol. Consequently, NaOH aqueous solution was added to adjust pH to the value of 10. The final nanotube concentration in the suspension was 0.3 wt. %, and the concentration of SDS and 1-pentanol was 0.1 M and 0.14 M, respectively. The dispersion was homogenized using UZ Sonopuls HD 2070 kit for 30 min at 50% power of the apparatus and in 50% pulse mode under the temperature of about 50°C [1]. The homogenized dispersion of nanotubes was vacuum filtered through the nonwoven polyurethane (PU) membrane. The disk-shaped filtration cake was washed several times by deionized water and methanol in situ. The cake forms an entangled nanotube network which is partially infiltrated into the membrane pores. This interlocked structure of MWCNT network and PU membrane is used as a sensor in sensing experiments.Polyurethane nonwoven porous membrane for MWCNT dispersion filtration was prepared by electrospinning. PU solution in dimethylformamide (DMF) based on 4,4′-methylene-bis(phenyl isocyanate) (MDI), poly(3methyl-1,5-pentanediol)-alt-(adipic, isophthalic acid) (PAIM), and 1,4-butanediol (BD) was synthesized in molar ratio 9 : 1 : 8 (PU 918) at 90°C for 6 hours. Per partes method of synthesis was used starting with preparation of prepolymer from MDI and PAIM and followed by addition of BD and remaining quantity of MDI. The prepared solution was diluted with DMF to reduce the viscosity to 1.3 Pas (PU concentration of 13 wt. %) and to increase the conductivity to 150μS/cm. Nanofibre layers were prepared from PU solution by the commercially available equipment SpinLine 120 (SPUR a.s., Zlin, Czech Republic, http://www.spur-nanotechnologies.cz) using nanofibre forming jets. The experimental conditions were as follows: relative humidity of 34%, temperature of 23°C, electric voltage applied to PU solution of 95 kV, distance between electrodes of 270 mm, and speed of supporting textile collecting nanofibres of 0.2 m/min. Nanofibre layer with area mass of about 2.5 g/m2 and average pore size distribution of about 500 nm was collected on the polypropylene nonwoven textile.


## 2.2. Characterization of Nanotube Networks

MWCNTs (pure) were analyzed via transmission electron microscopy (TEM) using microscope JEOL JEM 2010 at the accelerating voltage of 160 kV. The sample was deposited on 300 mesh copper grid with a carbon film (SPI, USA) from MWCNT dispersion in acetone prepared by ultrasonication and dried.The structure of PU filtering membrane and MWCNT networks were observed with the help of scanning electron microscope (SEM) Vega LMU, produced by Tescan Ltd. The samples were deposited on carbon targets and covered with a thin Au/Pd layer. For the observations, the regime of secondary electrons was chosen.The networks were also analyzed by X-ray photoelectron spectroscopy (XPS) on TFA XPS Physical Electronics instrument at the base pressure in the chamber of about 6 × 10−8 Pa. The samples were excited with X-rays over a 400 μm spot area with a monochromatic Al Kα1,2 radiation at 1486.6 eV. Photoelectrons were detected with a hemispherical analyzer positioned at an angle of 45° with respect to the normal to the sample surface. Survey-scan spectra were made at the pass energy of 187.85 eV, and the energy step was 0.4 eV. Individual high-resolution spectra for C1s were taken at a pass energy of 23.5 eV and 0.1 eV energy step. The concentration of elements was determined from survey spectra by MultiPak v7.3.1 software from Physical Electronics.Fourier transform infrared (FTIR) analyses of MWCNT samples in powder form prepared by KBr were performed using Thermo Scientific Nicolet IS5 spectrometer with ID1 transmission accessory.


## 2.3. Electrical Resistance Measurement

The electrical resistance of sensors (length 15 mm, width 5 mm, and thickness ca 0.3 mm) cut out from the prepared MWCNT network/PU membrane discs was measured along the sensor length by the two-point technique using multimeter Sefram 7338. The sensor was placed on a planar holder with Cu electrodes fixed on both of its sides. The holder with the sensor was placed into the gas chamber set on temperature 40°C; see schematic illustration in Figure1. The air as a gas carrier is pumped (flow rate 1.6 mL/s) through the silica gel into evaporation chamber, with temperature set to 100°C. The analyte (150 μL) was injected into evaporation chamber where it evaporated and its effect on the sensor resistance in gas sensing chamber was measured. The measurement was performed in three repeated 6-minute injection cycles. Experimental VOC used for testing performance of the sensor covered broad range of polarities from nonpolar solvents like hydrocarbons to polar alcohols.Figure 1
Schematic illustration of experimental setup for gas resistive sensors based on CNT/PUR segregated composite to concentration pulse of VOC vapors.


## 3. Results

Oxidation of MWCNTs by HNO3 + H2SO4 leads to formation of carboxyl, quinone, and hydroxyl groups on the surface of nanotubes with the following result: the concentration of carboxyl group is higher than other groups [10]. The possible mechanism of MWCNT oxidation by HNO3 + H2SO4 and subsequent functionalization by BuNH2 is illustrated in Figure 2. The first step of oxidation by HNO3 + H2SO4 mixture increases the content of carboxylic groups covalently bonded to nanotube surface. Then the carboxylic groups are converted to acyl chloride groups using SOCl2. Finally, butyl amine molecules are bonded to MWCNTs to produce amide groups (–CONH). FTIR and XPS measurements were used to observe the changes in the structure of pristine MWCNTs after the amidation. FTIR spectra of BuNH2, pure MWCNT, and MWCNT (BuNH2) are given in Figure 3. The peaks of BuNH2 at 1602 and 1463 cm−1 can be attributed to –NH2 and –CH2/CH3 groups. In the FTIR spectrum of pure MWCNTs, the peaks at 1731, 1580, and 1460 cm−1 can belong to ester group, C=C stretching mode, and –CH2/CH3 groups, respectively [11]. The peak assigned to quinone group at 1646 cm−1 [12] in FTIR spectrum of pure MWCNTs shifts to 1642 cm−1 after the amidation. The disappearance of the peak at 1731 cm−1 and the appearance of the peak at 1710 cm−1 show the hydrolysis of the ester groups to carboxylic acid in the acid mixture and the presence of unreacted carboxyl groups in the structure of MWCNT (BuNH2), respectively. The peaks about 1460 cm−1 show –CH2/CH3 groups on both MWCNTs.Figure 2
Possible reaction route for MWCNT functionalization by BuNH2.Figure 3
FTIR spectra of BuNH2, pure MWCNTs, and MWCNT (BuNH2).Surface composition (at %) of pristine MWCNTs changes after treatment from 85.8% (C) and 14.2% (O) to 87.5% (C), 8.9% (O), and 3.5% (N) for MWCNT (BuNH2). Figure 4(a) shows the typical peaks of XPS survey spectra for C1s positioned at 284.78 eV, O1s at 527.7 eV, and N1s at 399.2 eV. The N1s peak at 399.2 eV originating on MWCNT (BuNH2) confirms the presence of amide functional groups on the MWCNT (BuNH2) samples [12]. Figure 4(b) shows a broaden peak at 284.79 eV with 60.2% of the total C–C bond (1s, sp2) area on the surface of pristine MWCNTs. Other peaks at 285.78 eV (18.8%), 287.06 eV (15.5%), 289.41 eV (2.6%), and 290.46 eV (2.8%) can be attributed to sp3 hybridized C–C bonds present at defective locations and tubular structure asymmetry [13, 14], C–O, C=O, and O–C=O groups, and π-π electronic transition in pristine MWCNTs, respectively. The shifting of the peak from 287.06 to 286.99 eV as seen in Figure 4(c) could be reason for the formation of amide groups in the structure of MWCNT (BuNH2). The increase in the area % of sp3 hybridized C–C bonds could arise from the additional alkyl groups of BuNH2. The reason of the fact that the peak of O–C=O group shifts from 289.41 to 288.41 eV [15] can be the hydrolysis of the ester groups on pure MWCNTs to the carboxylic groups on MWCNT (BuNH2), which is confirmed by their FTIR spectra. However, the presence of the peak at 288.41 eV after modification shows that there are still unreacted carboxyl groups with BuNH2 on its surface. It is clear that the findings of XPS and FTIR measurements compromise with each other and confirm expected modification. It was seen in the previous study [3] that the peaks of –NH2 and C=C vibrations were coupled with each other in the case of the alkyl diamine treated MWCNTs. In our case, the increase in the intensity of the peak at 1580 cm−1 could arise from the residue of unreactedn-butylamine in the structure of the MWCNTs because of the observation of two different peaks in the deconvoluted N1s spectra; see Figure 4(d). In another study, the atoms of nitrogen with a bonding energy of 400.0 eV and 401.0 eV were assigned to the bonds involving primary amines (–CH2–NH2) and amide carbonyl groups (–N–C=O), respectively [14], which supports the presence of the amine and amide groups on MWCNT (BuNH2). XPS and FTIR data show us that there are also physically adsorbed n-butyl amine molecules on MWCNTs as well as chemically reacted ones.(a) XPS survey spectra of pure and BuNH2 treated MWCNTs. (b) Deconvoluted high resolution XPS peak C1s with functional groups for pure MWCNTs. (c) Deconvoluted high resolution XPS peak C1s with functional groups for MWCNT (BuNH2). (d) High resolution XPS spectra obtained in the N1s bonding energy region for MWCNT (BuNH2).
(a)
(b)
(c)
(d)Figure5 shows results of TEM analyses of pristine MWCNTs. The micrograph of the cluster of nanotubes is shown in Figure 5(a) and detailed view of one individual nanotube is in Figure 5(b). The partial infiltration of MWCNTs into the membrane pores links MWCNT entangled layer with PU membrane.TEM micrographs of the pristine nanotubes.
(a)
(b)SEM micrographs of the upper surfaces of prepared two principal nanotube networks are presented in Figures6(A) and 6(B). The micrographs show some differences in the porosity of the networks. BuNH2 treated nanotubes seem to form a network with higher porosity than pristine nanotubes. At the same time the functionalization of CNT network by BuNH2 may cause the increase in the surface area of MWCNT (BuNH2) network [3]. So the believed increase in porosity and the surface area of MWCNT (BuNH2) network may be behind the improvement of adsorption properties of this network [16]. Figure 6(C) presents SEM analyses of the used PU filtering membrane prepared by electrospinning as described above. The membrane has a porous structure. The pore size is in the range 50–500 μm; the PU fiber diameter is about 120 nm. In the course of filtration, the membrane pores were filled at first by nanotubes and then a filtration cake forms.Figure 6
SEM micrographs of the surfaces of (A) pristine MWCNT and (B) MWCNT (BuNH2) networks and (C) PU membrane.The adsorption of solvent molecules by the network increases its electrical resistance and thus the network resistance measurement is a simple and convenient method to register MWCNT response to vapor action. The network sensor responseS may be defined as
(1)S=100(R-R0)R0=100ΔRR0,
where R0 denotes the initial sensor resistance when, in the gas sensing chamber, it is exposed only to flow of pure air and R denotes the sensor resistance during measurement when exposed to a mixture of volatile organic compounds (VOC) with air. To compare the sensitivity of both tested composites, that is, MWCNT(pure) and MWCNT(BuNH2) networks on PU membrane to VOC vapors, the sensor response ratio was calculated: (S2-S1)/S1; see Table 1. S1 denotes the sensor response of MWCNT(pure)/PU composite and S2 the sensor response of MWCNT(BuNH2)/PU network.Table 1
Sensor responsesS1 and S2 of sensors with pristine and functionalized MWCNT, respectively, to concentration pulses of different VOC in air from a broad range of polarities defined by Hansen solubility parameters δd, δp, and δh and total Hildebrand solubility parameter, δt.
Solvent
δ
d  [MPa1/2]
δ
p  [MPa1/2]
δ
h  [MPa1/2]
δ
t  [MPa1/2]
S
1  [%]
S
2 [%]
(
S
2
/
S
1
-
1
)
×
100  [%]
n-Pentane
14.5
0
0
14.5
8.0
10
25.0
n-Heptane
15.3
0
0
15.3
6.5
8.0
23.1
Diisopropyl ether
13.8
2.8
4.6
14.8
8.4
12.3
46.4
Diethyl ether
15.5
2.9
4.6
16.4
8.5
17.0
100.0
Ethyl acetate
15.8
5.3
7.2
18.2
9.3
22.0
136.6
2-Butanone
16.0
9.0
5.1
19.1
8.2
26.3
220.7
Chloroform
15.3
18.0
6.1
24.4
4.6
20.5
345.7
1-Pentanol
16.0
6.8
17.4
24.6
5.0
28.0
460.0
Methanol
15.1
12.3
22.3
29.6
3.8
35.8
842.1The sensor response to VOC vapors was tested during adsorption/desorption cycles induced by VOC injection to flow of air. The chosen solvents cover a broad range of Hansen solubility parameters, as shown in Table1. The parameters are defined by
(2)δt2=δd2+δp2+δh2,
where δt is the total Hildebrand solubility parameter and δd, δp, and δh denote dispersion, polar, and hydrogen bonding component, respectively.The typical MWCNT network responses to VOC concentration pulses are presented in Figure7. There are sharp increases in sensitivity value caused by adsorption of VOC molecules on CNT surface. Adsorbed molecules change contact resistance in CNT junction leading further to increase in macroscopic CNT layer resistance. Desorption of molecules leads to reversible decrease in macroscopic resistance. It seems that adsorption is faster than desorption process.Figure 7
MWCNT/PU composite responses onto three concentration pulses of VOC vapours like heptane, diisopropyl ether, 2-butanone, and methanol.The interaction forces between MWCNT (BuNH2) network and the VOC molecules are induced dipole-induced dipole, induced dipole-dipole, dipole-dipole, and hydrogen bonding as well as the interactions of coronene subunits on pure nanotubes. First and second group interactions are between alkyl groups (–CH2/CH3) of VOC molecules and –C4H9 groups on MWCNT (BuNH2) network and between the pair of alkyl groups (–CH2/CH3) of VOC molecules and the polar groups (carboxyl and amide) on the network or the pair of polar groups of VOC molecules and the alkyl groups on the network, respectively. These interactions can provide the adsorption of n-heptane and n-pentane on MWCNT (BuNH2) network, which are the weakest interactions between the network and VOCs in this study. The interactions of carboxyl and amide groups on MWCNT (BuNH2) with polar groups of VOC molecules are involved in third and fourth group interactions based on the functional groups of VOC. The hydrogen bonding can have more important role for adsorption of methanol, n-pentanol, and chloroform on MWCNT (BuNH2) network, which is the strongest interaction among them. The network has top three sensor responses to them. The reason of high sensor response of the network to methanol could be that methanol has the highest value of the sum of δh and δd among the VOCs. First, second, and third group interactions include the interactions of other VOCs with the network. Which interactions are more dominant on the adsorption changes with the solubility parameter values of VOCs as shown in Table 1. Second and third group interactions become prominent by the increase in the sum of δh and δd of VOCs. This usually causes the increase of sensor response of MWCNT (BuNH2) network as seen in Figure 8.Figure 8
The ratioS2/S1-1 calculated as the increase in MWCNT (BuNH2) sensitivity with respect to sensitivity of pure MWCNT in trend of increased VOC polarity defined by total Hildebrand solubility parameter.


## 4. Conclusions

Multiwalled carbon nanotubes (MWCNT) were used in their pure and functionalized form byn-butylamine to prepare layered composites of entangled networks deposited on polyurethane supporting nonwoven membrane. The response of composite sensors to organic solvent vapors in a broad range of polarities (defined by Hansen solubility parameters) was measured by the change of electrical resistance as a response to physisorption and desorption of vapors. In case of highly polar methanol, the functionalized network response was more than eightfold higher in comparison to the network prepared from pristine nanotubes.The mechanism of the resistance change may be explained by formation of nonconducting layers between nanotubes owing to exposure to solvent vapors. The functionalization considerably increases the resistance of composite sensor in comparison to the sensor with pristine nanotubes. It suggests that there is a relation between the strength of the van der Waals forces and the sensor response of MWCNT (BuNH2) network. Stronger interactions between the VOCs and the network can induce the higher sensing response of the network. The sum of δh and δd of VOCs can have effect on the sensor responses based on dipole-dipole and hydrogen bonding interactions between the network and the VOCs.



---