# A Brief Overview of TiO2 Photocatalyst for Organic Dye Remediation: Case Study of Reaction Mechanisms Involved in Ce-TiO2 Photocatalysts System

Authors: Milind Pawar; S. Topcu Sendoğdular; Perena Gouma
Journal: Journal of Nanomaterials
 (2018)

---

## Abstract

The ever-increasing world population and the rapid growth of industrialization globally make necessary the development of clean technologies and affordable materials for remediating environmental pollution from petroleum-based hydrocarbons and dyes, among others. Advanced photocatalytic materials may provide an excellent solution for environmental cleanup without generating toxic byproducts as they allow for the complete oxidation of the pollutants and their conversion to benign species. In this review, the basic principle of photocatalyst operation and the importance of bandgap engineering are discussed. TiO2 has been the default photocatalyst although it has several shortcomings. Doping of TiO2 with Ce has been explored extensively in the literature as a way to enable visible-light-activated photocatalysis and enhanced efficiency. Recent advances in the synthesis of Ce-modified TiO2 photocatalytic materials along with photocatalytic reaction mechanisms are summarized.


---

## Body

## 1. Introduction

The sun is radiating clean energy without any pollutants from billions of years, and it is the most crucial source of energy for life on our planet earth. Amount of solar energy reach on the earth’s surface in a single day can satisfy the energy requirement of mankind for a decade. It is of utmost importance to utilize the abundance of solar energy for a variety of applications such as energy production and environmental cleanup. Wastewater recycling via photocatalyst may pose a solution to the long-standing shortage of fresh water in many countries. A photocatalyst is a material that helps to accelerate and enhance a light-induced reaction without being consumed in the process [1]. Recently, there has been significant interest in the development of novel photocatalytic technology covering an extensive range of environmental applications such as water remediation and environmental cleanup of oil spills and other pollutants. There have also been some energy-related studies, which focus on the use of photocatalysts for fuel production (e.g., H2), specifically through water splitting. Environmental cleanup by using photocatalysts offers many benefits [2]: conversion of pollutants from complex molecules into simple and nontoxic substances and avoidance of secondary treatment, disposal, or use of any expensive oxidizing chemicals by utilization of solar energy. Numerous studies were published on the photocatalytic applications of titania (TiO2) for the decomposition of organic compounds due to the ability of TiO2 to oxidize organic and inorganic substances in water and air through redox processes [3–5]. TiO2 only absorbs ultraviolet (UV) light of broad solar spectrum due to its large bandgap energy (λ < 388 nm), which was comprised of only 3% of the entire solar spectrum. In order to overcome this issue, cerium- (Ce-) doped TiO2 photocatalysts are explored extensively for utilization of visible light to activate TiO2 photocatalyst. This review is focused on Ce-doped TiO2 photocatalysts for advanced oxidation process (AOP) of degradation of organic dyes. Complex reaction mechanisms involved in Ce-doped TiO2 proposed by various researchers in the field are summarized to provide a comprehensive review.


### 1.1. Basic Principle of Oxide-Based Photocatalysts

An ideal photocatalyst should be activated by photons, chemically nonreactive, easily available, nontoxic, and able to utilize a broad solar spectrum [6]. Energy difference of valence band (VB) and conduction band (CB) is known as bandgap (Eg), which determines if the material is a conductor, a semiconductor, or an insulator. Unlike insulators or metals, semiconductors have the bandgap that allows producing electron (e−)/hole (h+) pairs when they absorb a photon with energy equals to their bandgap or higher than that. Semiconducting metal oxides are commonly used as photocatalysts due to their favorable bandgap (Eg) and band edge positions. In semiconductors, the electronic structure plays an important role where the valence band (VB) of the semiconductor is completely filled with electrons and the conduction band (CB) is empty. The bandgap of different semiconductor materials varies as per their electronic structure. Some of the semiconductor oxide materials bandgap is presented in Table 1.Table 1
Bandgap energies of semiconductors as photocatalyst.
Photocatalyst
Bandgap energy (eV)
ZrO2
5.0
ZnS
3.6
TiO2 (anatase)
3.2
TiO2 (rutile)
3.0
WO3
2.8
SnO2
2.5
Fe2O3
2.3
GaP
2.25
V2O5
2.6
CuO
1.7
CdSe
1.7
MnO2
0.25
CeO2
2.94The underlying mechanism of semiconductor photocatalysts (TiO2, ZnO, ZnS, and Fe2O3) is shown in Figure 1. As shown in Figure 1, when a photon with adequate energy (≥bandgap energy of semiconductor) is absorbed by the semiconductor, an electron from valence band (VB) gets excited and jumps to the conduction band (CB), which generates a hole in the valence band. This process of electron-hole pair generation is known as photoexcitation. Photoexcited electrons can be utilized in the reduction of oxygen, and similarly, holes can be utilized in oxidizing water molecules which are adsorbed on photocatalyst surface.Figure 1
Basic mechanism of semiconductor photocatalyst.Photoexcitation: hν ≥ Eg, TiO2 (photocatalyst) + hν (photon) ➔ h+VB (hole in valence band) + e−CB (electron in conduction band).Here, h: Planck’s constant 6.62607004 × 10−34 m2 kg/s; v: frequency of incident light.Following the photoexcitation process, as shown in Figure2, several paths can be followed by the photogenerated electron and hole because of adsorbed species on the photocatalyst surface. Here, electron acceptor species can be reduced by electron (pathway [a]: A + e− ➔ A−); similarly, electron donor species can be oxidized by combining with the hole (pathway [b]: D ➔ D+ + e−). Recombination of electron and hole may occur on the surface of semiconductor particle (pathway [c]: h+ + e− ➔ photocorrosion) or within the volume of the semiconductor particle (pathway [d]) [1]. The process of electron and hole recombination is known as photocorrosion, where electron and hole lose their redox ability by generating thermal energy or a photon.Figure 2
Schematic of charge separation and photogenerated hole and electron (adopted with permission from Linsebigler et al.) [8].Adsorbed water on photocatalyst surface splits into⋅OH and H+ when oxidized. These hydroxyl radicals can easily oxidize organic contaminants. Cationic radicals ⋅RH+ can be produced by direct oxidation of adsorbed organic pollutants (RH) with holes in VB. On the other side, the generation of superoxide radical anions (⋅O2−) occurs due to the reduction of oxygen by the electron. Hydrogen dioxide in conduction band can be produced by the reaction of radical anion and H+. Reactive oxygen species (ROS) that result from chain reaction are as shown in Figure 3 [7].Figure 3
Production of reactive oxygen species by chain reaction (reprinted with permission from Nosaka and Nosaka) [7].


### 1.2. The Bandgap Position

The redox potentials and the bandgap position of a photocatalyst are important factors controlling the photo-induced electron excitation. Semiconductors should allow for different redox reactions under light irradiation. The conduction band of photocatalyst should be at positive potential as compared to the acceptor’s potential in order to transfer an electron to the acceptor. Similarly, the potential level of the valence band is required to be more negative than the donor in order to accept electron [8]. Figure 4 illustrates the valence and conduction band positions for various semiconductors. The bandgap energy determines which semiconductor material can be activated by the light of different wavelengths. TiO2 has been extensively explored because of its photocatalytic activity under ultraviolet and visible light. TiO2 has two primary phases: rutile and anatase. Anatase has higher bandgap with 3.2 eV, which is equivalent to an excitation wavelength of 388 nm, capable of absorbing light near the UV range. Rutile exhibits 3.0 eV with 410 nm wavelength, which absorbs visible light.Figure 4
Band edge position with redox potentials for different semiconductors (adapted from Zhang et al.) [81].The factors affecting the efficiency of photocatalysis are as follows:(i) Intensity of Light Source. The photocatalytic activity of semiconductor oxides depends on the intensity of light absorption. Better photocatalytic efficiency can be achieved with an increase in the intensity of light as it improves charge separation [9].(ii) Nature of the Photocatalyst. Kogo et al. reported that photocatalytic reaction efficiency can be affected by the number of absorbed photons by photocatalysts surface [10]. It implies that photocatalytic reactions take place on the adsorbed surface. Surface morphologies such as particle size and shape are important factors affecting the function of nanomaterials’ photocatalysis process [11]. Different synthesis methods have been developed to exhibit the necessary size, shape, and stability for their applications [12].(iii) pH of the Solution. Surface charge properties can be governed by pH of solution and size of aggregates [13] due to the different charge of the semiconductor surface.(iv) Temperature. When the temperature of the reaction raises, the photocatalytic efficiency decreases due to the enhanced recombination of e−/h+ pairs and enhanced desorption of adsorbed species from the exterior of the photocatalyst.(v) Quantity of the Photocatalyst. It is considered that the photocatalytic activity can be increased with increasing the concentration of the catalyst [14]. However, the level of catalyst concentration has to be determined because the excess catalyst prevents the diffusion of the light into the solution which might result in unfavorable light scattering [15].


### 1.3. TiO2 Photocatalyst

As a photocatalyst, titanium dioxide (TiO2) has attracted substantial attention for a long time and is considered as one of the most promising materials for commercial use due to its outstanding optical and electronic properties, photoactivity, high chemical stability, low cost, nontoxicity, reusability, and eco-friendliness [8, 16, 4]. Much more attention has been focused on the different preparation methods of TiO2 in order to improve its performance compared to commercial TiO2 powders (for example, Degussa P25).The crystallographic structure of TiO2 is shown in Figure 5 [17]. Well-known phases of TiO2 are anatase, rutile, and brookite. Rutile is a tetragonal (a = 4.5937 Å, c = 2.9587 Å), anatase is also a tetragonal (a = 3.7845 Å, c = 9.5143 Å), and brookite is an orthorhombic crystal (a = 5.4558 Å, b = 9.1819 Å, c = 5.1429 Å). C coordinate of anatase is higher than other phases, and c/a ratio of its unit cell is greater than rutile and brookite phases. Among all these phases, anatase is the most active allotropic phase regarding photocatalytic activity when compared to rutile, brookite, and TiO2-B (artificial phase).Figure 5
Common polymorphs of TiO2 (reprinted with permission from Dambournet et al.) [17].Rutile is thermodynamically stable at ambient conditions, whereas anatase is kinetically stable, and it transforms to rutile at higher temperatures [18] depending on the particle size, ambient pressure, and other parameters [19]. Brookite phase is also metastable but difficult to synthesize, hence it is seldom studied [20]. Table 2 represents the oxide polymorphs of TiO2 with experimental condition and method for synthesis as well as particle size. Among the three different crystalline phases of TiO2, anatase shows the highest stability for particle size less than 11 nm. Similarly, rutile shows thermodynamic stability for particle size greater than 35 nm, and for brookite, it is 11–35 nm which are summarized in Table 2 [21].Table 2
Particle size effect on phase stability of TiO2.
Phase
Conditions
Particle size (nm)
Techniques
References
TiO2
Brookite
—
11 to 35
Sol-gel
[21, 73]
Anatase
Room temperature
Below 11
Sol-gel
[21, 73]
Rutile
Above 850°C
Higher than 35
Sol-gel
[21, 73]At room temperature, the rutile phase is thought to be a more stable phase as compared to the anatase in the case of bulk TiO2. However, it was suggested by Zhang and Banfield and independently confirmed by Gouma that anatase becomes a more stable phase due to lower total free energy as compared to rutile if the particle size is smaller than 14 nm [21, 22]. Subsequently, some studies have claimed that rutile and anatase together have higher photocatalytic activity as compared to 100% anatase. For example, the commercial TiO2, Degussa P25, is a mixture of anatase (~75%) and rutile (~25%) phases, and it is the most widely used photocatalyst for environmental applications [23].Anatase can be synthesized at lower temperatures (40°C) to nanoscale size; it shows better photocatalytic properties because nanoscale size increases the number of pores and enhances solid-solid interactions. On the contrary, at higher temperatures (above 300°C) nano-TiO2 has worse photocatalytic activity [24]. The properties of brookite are poorly known because of the difficulties associated with synthesis of pure brookite phase. Tay et al. also shows that the synthesized two phases (anatase/brookite) have higher photocatalytic activity due to the electrons transfer from brookite conduction band (CB) to anatase CB resulting in efficient electron-hole separation [25].


### 1.4. Modified TiO2

Two primary factors must be taken into account while designing the systems for conducting photocatalytic reactions. The first one is the efficiency of e− and h+ pair generation when the photocatalyst is illuminated with solar radiation. Second is the efficiency of the e−/h+ pair separation before they lose their redox ability due to recombination. The photocatalytic efficiency can be enhanced significantly by addressing the following primary issues: (i) increase the time of charge separation and recombination, (ii) broaden the solar spectrum range for photocatalyst, and (iii) changing the yield of a particular product [1, 8].Semiconductor photocatalysis system can be designed by considering the stability of the material under the light, product selectivity, and activation wavelength range [8]. TiO2 has been the most widely studied photocatalyst for many years. However, the main barriers of the TiO2 are its activation by ultraviolet light (λ ≤ 400 nm) because of the wide bandgap of TiO2 (~3.2 eV for anatase and ~3.0 eV for rutile), for which it only absorbs UV light (only about 3% of overall solar spectrum) [26]. Another major drawback of TiO2 is photogenerated electron-hole recombination, which deteriorates the photocatalytic activity [27]. Therefore, an apparent goal is the reducing bandgap of TiO2 in order to shift the absorption band to the visible region and to enhance the electron-hole separation process. The modifications of TiO2 have been accomplished by different strategies such as doping, codoping, sensitization, and coupling [28–32]. The coupling of two semiconductors provides different energy levels, which give a chance to improve a more efficient charge separation to enhance the lifetime of charge carriers and to increase interfacial charge transfer [33].Rare-earth elements are ideal dopants because of their 4f electronic configuration and spectroscopic properties [34]. Modification of electronic structure as well as crystal structure of TiO2 can be performed by doping rare-earth elements. Lanthanide ions could act as effective electron scavengers to trap the CB electrons from TiO2. Xu et al. [35] studied doping with rare-earth ions including La3+, Ce3+, Er3+, Pr3+, Gd3+, Nd3+, and Sm3+ in TiO2 which improved photocatalytic activity in the degradation of nitrite. Wang et al. [36, 37] also illustrated doping with lanthanide ions (La3+, Er3+, Pr3+, Nd3+, and Sm3+), which improved the photoelectrochemical properties as well as increased the photocurrent response and the photon current conversion efficiency in the range of 300–400 nm.


### 1.5. Cerium-Modified TiO2 Photocatalyst

Cerium is one of the most reactive rare-earth metals and can be utilized in a broad range of applications in the field of catalysis and photocatalysis. It is also one of the most generous rare-earth elements, making up about 0.0046% of the Earth’s crust by weight (64 ppm), even more abundant than copper (60 ppm) [38]. Cerium has Ce3+/Ce4+ redox couple, which can shift between CeO2 and Ce2O3 under reducing and oxidizing conditions [39, 40]. Furthermore, different electronic structures between Ce3+ (4f15d0) and Ce4+ (4f05d0) electronic configuration would lead to changed optical as well as catalytic properties [41]. The ability of Ce3+ to oxidize to Ce4+ states leads to high oxygen mobility that could result in strong catalytic potential [42], and because of this reason, it commonly applied in heterogeneous catalysis. However, CeO2 does not show good thermostable behavior because of its rapid sintering under influence of elevated temperatures [43, 44].Cerium oxide (ceria), CeO2 has the face-centered cubic (fcc) fluorite structure with eight coordinate cations (oxygen atoms) and four coordinate anions (Figure 6). The complete unit cell, Ce4O8, measures 0.51 nm (5.1 Å) on edge [44]. Ceria being an n-type semiconductor has a bandgap of 2.94 eV. The favorable bandgap of ceria makes it active under UV-Vis range and its utilization as a photocatalyst in advanced oxidation processes.Figure 6
(a) Unit cell of the CeO2 crystal structure; (b–d) (100), (110), and (111) planes of CeO2 structure (reprinted with permission from Wang and Feng) [82].
(a)
(b)
(c)
(d)Ceria is used in numerous catalytic reactions such as photocatalytic reactions and water splitting reactions, to name a few [45]. Recently, ceria has been explored as a dopant in aqueous phase photocatalytic reactions [36, 46].The photocatalytic activity of Ce-TiO2 for degradation of 2-mercaptobenzothiazole was reported by Li et al. [39]. The activity of Ce-TiO2 was higher in comparison with pure TiO2, and this was attributed to the higher surface area and better charge separation of photocatalyst [39]. Optical absorption was shifted to visible range 400–500 nm because of the introduction of Ce 4f level. Formation of 4f level and defect level were considered as a reason for delayed electron-hole recombination and activation of photocatalyst under UV visible light range [39].The phase transformation of anatase to rutile was hindered by Ce ions for low concentrations [47, 48]. Liu et al. produced Ce-TiO2 (3–7 wt % Ce) with sol-gel process and finally calcined at a different temperature. With increasing temperature, anatase phase showed growth for lower temperature domain for both pure TiO2 and Ce-TiO2 systems; however, when the temperature was increased from 600°C to 800°C, the transformation of anatase to rutile phase was inhibited in the Ce–TiO2 oxide. The main importance of this study was to show the shifting of light absorbance to the range of 380–460 nm in Ce–TiO2 [48]. For higher amount of Ce, phase segregation of ceria on the surface of TiO2 and rutile was formed [49].López et al. represented the structure and morphology of the CeO2–TiO2 oxides that were prepared by the sol-gel method as 10 wt % and 90 wt % and then calcined at 473, 673, 873, and 1073 K temperatures [50]. Experimental results showed that better thermal stability for TiO2 can be achieved by doping Ce ions to prevent particle sintering and subsequent pore collapsing [50]. Positive impact on crystallographic characteristic as well as sintering of photocatalyst was achieved by Ce doping. Distribution of cerianite on TiO2 caused substitution of Ti4+ by Ce4+ within the TiO2 anatase structure [50].Cao et al. [51] synthesized 0.2% Ce-TiO2 by the sol-gel method. The photodegradation test of methylene blue (MB) was carried out to assess the photocatalytic activity of Ce-TiO2. Interesting behavior of first rising and then falling the degradation efficiency with an increase of Ce content was found. At low Ce content in the Ce-TiO2, it is very easy for Ce4+ to capture the photogenerated electron and be reduced to Ce3+, which in turn separates the electrons and holes effectively and subsequently improve the photocatalytic activity of TiO2. However, when the Ce content exceeds a certain amount, the TiO2 crystal lattice reduces the crystallinity because of high impurities and defects. This causes shortening of the trapping center distance, increases the chance of recombination of the photogenerated charge carriers in the trapping center, and thus reduces the photocatalytic efficiency in return.Reli et al. [52] prepared novel cerium-doped TiO2 with sol-gel method within surfactant Triton X-114 in cyclohexane and showed that 1.2 wt % Ce gives the maximum photocatalytic activity for the decomposition of ammonia under UV light radiation. Hierarchical CeO2/TiO2 nanofibrous mats were prepared by Cao et al. [53] via electrospinning method. Photocatalysts prepared by electrospinning technique showed better photocatalytic efficiency for CeO2/TiO2 nanocomposite as compared to TiO2 for the degradation of RB dye under UV light irradiation.Eskandarloo et al. [54] represented TiO2/CeO2 hybrid photocatalysts, which were prepared from a powder mixture of titania and ceria. It was found that mixing TiO2 with CeO2 could facilitate efficient charge transfer, which can ease the separation of the photogenerated charge and in return increase photocatalytic efficiency [54]. Apart from here mentioned synthesis methods for Ce-TiO2 photocatalyst, their morphology and particle size are summarized in Table 3.Table 3
Literature review on various preparation methods with process parameters of Ce-TiO2 catalyst.
Materials
Dopant
Dopant concentration
Morphology
Bandgap, eV
Rate of degradation of MB dye (10−3 min−1)
References
TiO2
Ce
3 mol
Nanoparticle
2.46
24
[72]
Fe/Ce
Nanoparticle
2.5
15.4
[74]
Ce
1 wt %
Nanofiber
2.99
15
[75]
Nd
1 wt %
Nanofiber
3.1
13
[75]
Ce
5 wt %mol
Nanoparticle
16.6
[76]
Ce/N
0.6 mol
Nanoparticle
2.52
[77]
Ce
Nanofibrous mats
49.5
[53]
Ce
5 mol %
Microsphere
2.49
1.6
[71]
Ce/Pt
6.6 wt %
Nanoparticle
2.3
[78]
Ce
Thin film
2.6
2.5
[79]
Ce
2 mol
Nanobelt
2.51
34.8
[80]
Degussa P25
3.2
6.3


### 1.6. Photocatalytic Degradation Mechanism of Ce-TiO2 System

Various photocatalytic reaction mechanisms have been proposed so far depending upon the morphology and phases present, different mechanisms apply for photocatalytic reactions. Xie and Yuan [55] studied the cerium ion (Ce4+) modified TiO2 sol and nanocrystallites, which were prepared by chemical hydrothermal synthesis methods. Figure 7 illustrates the photosensitized photocatalysis mechanism of dye in the Ce4+-TiO2 sol system. In this reaction mechanism, an excited electron from dye due to visible light transfers to Ce ion. The hole left on dye can extract electrons to form hydroxyl radicals (HO⋅). In this process, the electrons are trapped by Ce4+ ions and are subsequently utilized for the formation of superoxide radicals [56]. The presence of Ce4+ on the surface of nanoparticle could develop the below reactions:Figure 7
Photosensitized photocatalysis of Ce4+-TiO2 sol system (reprinted with permission from Xie and Yuan) [55].Ce4++e−→Ce3+andCe3++O2→Ce4++O⋅2Photocatalytic degradation of dyes through semiconductor materials follows a complex path. Many researchers presented dye sensitization and subsequent charge transfer as a major reaction mechanism. Verma et al. presented photocatalytic reaction mechanism for the presence of ceria at the interface of anatase and rutile. Dependence of the catalyst’s architecture and Ce content was explored by Verma et al. [57]. The unique architecture of Ce-TiO2 system was synthesized via simple sol-gel method with varying Ce content. Doping of Ce inhibited transformation of anatase to stable rutile phase. As it was mentioned earlier that anatase has better photocatalytic activity, Ce doping showed a positive effect on photocatalytic activity which was measured by degradation of MB. Novel architecture material showed enhanced activity under a combination of ultraviolet and visible light. Reason for higher photocatalytic activity was sought to be the presence of CeO2 at the interface of anatase and rutile, which thus facilitates excellent interfacial charge transfer as shown in Figure 8. In such systems, excitation of electron from valence band to conduction band of CeO2 occur due to photoactivation via visible light (Eg = 2.94). However, CB electron of CeO2 is not capable of reduction of O2 due to its unfavorable redox potential position. This electron can transfer to CB of anatase and subsequently to rutile via interfacial charge transfer. An electron in CB of rutile can thermodynamically have accepted by O2 adsorbed on the surface and create highly reactive superoxide anions by reduction reaction. On the contrary, holes can migrate to VB of CeO2 to accept electron from adsorbed water and create ⋅OH− (hydroxyl cation) [57].Figure 8
Interfacial charge transfer mechanism (adopted with permission from Verma et al.) [57].Reaction mechanism can be summarized as follows:(1)
Photoactivation: Ce-TiO2 (system) + hv ➔ e− + h+
(2)
Ce4+ ➔ Ce3+ + e−
(3)
Interfacial charge transfer: e−(CB Ce) ➔ e−(CB anatase) ➔ e−(CB rutile)
(4)
Reduction: O2 + e−(CB rutile) ➔ ⋅O2−
(5)
⋅O2− + organic dye ➔ degradation of dye
(6)
Interfacial charge transfer: h+ (VB rutile) ➔ h+ (VB anatase) ➔ h+ (VB Ce)
(7)
Oxidation: h+ (VB Ce) + H2O ➔ HO⋅ + H+
(8)
HO⋅ + Organic dye ➔ degradation of dye


### 1.7. Photocatalytic Activity Assessment by Methyl Blue Degradation

Some studies suggest that the hydroxyl radicals play a key role as reactants for oxidation of organic substrates in aqueous photocatalysis. Therefore, hydroxyl radicals yield is essential to determine the photocatalytic efficiency and for comparison of different photocatalytic materials. In order to assess the photocatalytic efficiency of a TiO2-based catalyst, an organic and inorganic pollutant can be used as the environment. They can be divided into three categories: azo dyes [58], organic compounds [59], and inorganic gases [60]. Dye degradation is a popular method for assessing the efficiency because of its being fast and easy. Dyes have relatively high extinction coefficients to activate the photocatalyst, and they consequently will absorb a significant amount of the incoming light, which makes it difficult to assess the full photocatalytic activity [61].Methylene blue (MB) is most commonly used as a model dye for the adsorption of organic dyes from aqueous solution [62]. It is a heterocyclic aromatic hydrocarbon with a molecular formula, C16H18N3SCl [63] (molecular weight 319.85 g/mol, maximum absorption wavelength 640). Methylene blue dye is commonly used in the textile, food, and chemical industries [64, 65]. As it is a commonly used dye in numerous industrial sectors, it can mix up with domestic water and pollute it. Therefore, it is crucial to remove this toxic dye from contaminated water by converting it to inorganic benign compounds by adding photocatalyst materials to wastewater [66, 67].C16H18N3SCl + 25.5O2 ➔ 16CO2 + 6H2O + 3HNO3 + H2SO4 + HCl [68, 69].Methylene blue is found to give several environmental and health damages through contamination of water. Toxicity rate of MB is four and acute exposure by intravenous injection causes sweating, dizziness, confusion, vomiting, chest pain, and nausea [70].The structures of the dye molecules directly decide the absorption characteristic of dyes for light. In the electron absorption spectra of dyes, there are several absorption bands, which reflect the state of motion of the electrons. The absorption wavelength, absorption intensity, and the shape of the absorption band are related directly to the structure of dye molecules. Therefore, it is possible to evaluate the structural variation of dyes by investigating the variation of the electron absorption spectra during the process of degradation of the dyes.It has been reported that the photodecomposition of RhB aqueous solution in the presence of TiO2 particles as a photocatalyst has two pathways: (1) the photocatalytic pathway which would occur under UV irradiation. In this pathway, TiO2 would be activated to generate electrons under UV irradiation (λ ≤ 385 nm) to drive the process of photodegradation; (2) the photosensitization pathway which usually occurs under visible light irradiation. The bandgap of anatase TiO2 is 3.2 eV; therefore, the energy of visible light (λ > 400 nm) is not enough to excite TiO2 to produce electrons to drive the process of photodegradation. In the photosensitization pathway, where TiO2 cannot be activated by visible light, dyes will absorb visible light irradiation and can be excited, which will drive the process of photodegradation. However, the existence of TiO2 photocatalyst is a prerequisite and a crucial requirement to ensure electron carriers to contact with electron acceptors adsorbed on the TiO2 surface, which will help in the process of photodecomposition.Xie et al. [71] showed that doping content of Ce microspheres improved photocatalytic activity on the degradation of MB under visible light irradiation. Priyanka et al. [72] studied the photocatalytic activity of TiO2 and Ce-doped TiO2 nanoparticles in solar light, and the degradation of MB was monitored. Within 10 min of sunlight irradiation, the 3 mol % Ce-doped TiO2 sample could degrade about 90% of MB dye and then the degradation was almost complete in 30 min.


## 1.1. Basic Principle of Oxide-Based Photocatalysts

An ideal photocatalyst should be activated by photons, chemically nonreactive, easily available, nontoxic, and able to utilize a broad solar spectrum [6]. Energy difference of valence band (VB) and conduction band (CB) is known as bandgap (Eg), which determines if the material is a conductor, a semiconductor, or an insulator. Unlike insulators or metals, semiconductors have the bandgap that allows producing electron (e−)/hole (h+) pairs when they absorb a photon with energy equals to their bandgap or higher than that. Semiconducting metal oxides are commonly used as photocatalysts due to their favorable bandgap (Eg) and band edge positions. In semiconductors, the electronic structure plays an important role where the valence band (VB) of the semiconductor is completely filled with electrons and the conduction band (CB) is empty. The bandgap of different semiconductor materials varies as per their electronic structure. Some of the semiconductor oxide materials bandgap is presented in Table 1.Table 1
Bandgap energies of semiconductors as photocatalyst.
Photocatalyst
Bandgap energy (eV)
ZrO2
5.0
ZnS
3.6
TiO2 (anatase)
3.2
TiO2 (rutile)
3.0
WO3
2.8
SnO2
2.5
Fe2O3
2.3
GaP
2.25
V2O5
2.6
CuO
1.7
CdSe
1.7
MnO2
0.25
CeO2
2.94The underlying mechanism of semiconductor photocatalysts (TiO2, ZnO, ZnS, and Fe2O3) is shown in Figure 1. As shown in Figure 1, when a photon with adequate energy (≥bandgap energy of semiconductor) is absorbed by the semiconductor, an electron from valence band (VB) gets excited and jumps to the conduction band (CB), which generates a hole in the valence band. This process of electron-hole pair generation is known as photoexcitation. Photoexcited electrons can be utilized in the reduction of oxygen, and similarly, holes can be utilized in oxidizing water molecules which are adsorbed on photocatalyst surface.Figure 1
Basic mechanism of semiconductor photocatalyst.Photoexcitation: hν ≥ Eg, TiO2 (photocatalyst) + hν (photon) ➔ h+VB (hole in valence band) + e−CB (electron in conduction band).Here, h: Planck’s constant 6.62607004 × 10−34 m2 kg/s; v: frequency of incident light.Following the photoexcitation process, as shown in Figure2, several paths can be followed by the photogenerated electron and hole because of adsorbed species on the photocatalyst surface. Here, electron acceptor species can be reduced by electron (pathway [a]: A + e− ➔ A−); similarly, electron donor species can be oxidized by combining with the hole (pathway [b]: D ➔ D+ + e−). Recombination of electron and hole may occur on the surface of semiconductor particle (pathway [c]: h+ + e− ➔ photocorrosion) or within the volume of the semiconductor particle (pathway [d]) [1]. The process of electron and hole recombination is known as photocorrosion, where electron and hole lose their redox ability by generating thermal energy or a photon.Figure 2
Schematic of charge separation and photogenerated hole and electron (adopted with permission from Linsebigler et al.) [8].Adsorbed water on photocatalyst surface splits into⋅OH and H+ when oxidized. These hydroxyl radicals can easily oxidize organic contaminants. Cationic radicals ⋅RH+ can be produced by direct oxidation of adsorbed organic pollutants (RH) with holes in VB. On the other side, the generation of superoxide radical anions (⋅O2−) occurs due to the reduction of oxygen by the electron. Hydrogen dioxide in conduction band can be produced by the reaction of radical anion and H+. Reactive oxygen species (ROS) that result from chain reaction are as shown in Figure 3 [7].Figure 3
Production of reactive oxygen species by chain reaction (reprinted with permission from Nosaka and Nosaka) [7].


## 1.2. The Bandgap Position

The redox potentials and the bandgap position of a photocatalyst are important factors controlling the photo-induced electron excitation. Semiconductors should allow for different redox reactions under light irradiation. The conduction band of photocatalyst should be at positive potential as compared to the acceptor’s potential in order to transfer an electron to the acceptor. Similarly, the potential level of the valence band is required to be more negative than the donor in order to accept electron [8]. Figure 4 illustrates the valence and conduction band positions for various semiconductors. The bandgap energy determines which semiconductor material can be activated by the light of different wavelengths. TiO2 has been extensively explored because of its photocatalytic activity under ultraviolet and visible light. TiO2 has two primary phases: rutile and anatase. Anatase has higher bandgap with 3.2 eV, which is equivalent to an excitation wavelength of 388 nm, capable of absorbing light near the UV range. Rutile exhibits 3.0 eV with 410 nm wavelength, which absorbs visible light.Figure 4
Band edge position with redox potentials for different semiconductors (adapted from Zhang et al.) [81].The factors affecting the efficiency of photocatalysis are as follows:(i) Intensity of Light Source. The photocatalytic activity of semiconductor oxides depends on the intensity of light absorption. Better photocatalytic efficiency can be achieved with an increase in the intensity of light as it improves charge separation [9].(ii) Nature of the Photocatalyst. Kogo et al. reported that photocatalytic reaction efficiency can be affected by the number of absorbed photons by photocatalysts surface [10]. It implies that photocatalytic reactions take place on the adsorbed surface. Surface morphologies such as particle size and shape are important factors affecting the function of nanomaterials’ photocatalysis process [11]. Different synthesis methods have been developed to exhibit the necessary size, shape, and stability for their applications [12].(iii) pH of the Solution. Surface charge properties can be governed by pH of solution and size of aggregates [13] due to the different charge of the semiconductor surface.(iv) Temperature. When the temperature of the reaction raises, the photocatalytic efficiency decreases due to the enhanced recombination of e−/h+ pairs and enhanced desorption of adsorbed species from the exterior of the photocatalyst.(v) Quantity of the Photocatalyst. It is considered that the photocatalytic activity can be increased with increasing the concentration of the catalyst [14]. However, the level of catalyst concentration has to be determined because the excess catalyst prevents the diffusion of the light into the solution which might result in unfavorable light scattering [15].


## 1.3. TiO2 Photocatalyst

As a photocatalyst, titanium dioxide (TiO2) has attracted substantial attention for a long time and is considered as one of the most promising materials for commercial use due to its outstanding optical and electronic properties, photoactivity, high chemical stability, low cost, nontoxicity, reusability, and eco-friendliness [8, 16, 4]. Much more attention has been focused on the different preparation methods of TiO2 in order to improve its performance compared to commercial TiO2 powders (for example, Degussa P25).The crystallographic structure of TiO2 is shown in Figure 5 [17]. Well-known phases of TiO2 are anatase, rutile, and brookite. Rutile is a tetragonal (a = 4.5937 Å, c = 2.9587 Å), anatase is also a tetragonal (a = 3.7845 Å, c = 9.5143 Å), and brookite is an orthorhombic crystal (a = 5.4558 Å, b = 9.1819 Å, c = 5.1429 Å). C coordinate of anatase is higher than other phases, and c/a ratio of its unit cell is greater than rutile and brookite phases. Among all these phases, anatase is the most active allotropic phase regarding photocatalytic activity when compared to rutile, brookite, and TiO2-B (artificial phase).Figure 5
Common polymorphs of TiO2 (reprinted with permission from Dambournet et al.) [17].Rutile is thermodynamically stable at ambient conditions, whereas anatase is kinetically stable, and it transforms to rutile at higher temperatures [18] depending on the particle size, ambient pressure, and other parameters [19]. Brookite phase is also metastable but difficult to synthesize, hence it is seldom studied [20]. Table 2 represents the oxide polymorphs of TiO2 with experimental condition and method for synthesis as well as particle size. Among the three different crystalline phases of TiO2, anatase shows the highest stability for particle size less than 11 nm. Similarly, rutile shows thermodynamic stability for particle size greater than 35 nm, and for brookite, it is 11–35 nm which are summarized in Table 2 [21].Table 2
Particle size effect on phase stability of TiO2.
Phase
Conditions
Particle size (nm)
Techniques
References
TiO2
Brookite
—
11 to 35
Sol-gel
[21, 73]
Anatase
Room temperature
Below 11
Sol-gel
[21, 73]
Rutile
Above 850°C
Higher than 35
Sol-gel
[21, 73]At room temperature, the rutile phase is thought to be a more stable phase as compared to the anatase in the case of bulk TiO2. However, it was suggested by Zhang and Banfield and independently confirmed by Gouma that anatase becomes a more stable phase due to lower total free energy as compared to rutile if the particle size is smaller than 14 nm [21, 22]. Subsequently, some studies have claimed that rutile and anatase together have higher photocatalytic activity as compared to 100% anatase. For example, the commercial TiO2, Degussa P25, is a mixture of anatase (~75%) and rutile (~25%) phases, and it is the most widely used photocatalyst for environmental applications [23].Anatase can be synthesized at lower temperatures (40°C) to nanoscale size; it shows better photocatalytic properties because nanoscale size increases the number of pores and enhances solid-solid interactions. On the contrary, at higher temperatures (above 300°C) nano-TiO2 has worse photocatalytic activity [24]. The properties of brookite are poorly known because of the difficulties associated with synthesis of pure brookite phase. Tay et al. also shows that the synthesized two phases (anatase/brookite) have higher photocatalytic activity due to the electrons transfer from brookite conduction band (CB) to anatase CB resulting in efficient electron-hole separation [25].


## 1.4. Modified TiO2

Two primary factors must be taken into account while designing the systems for conducting photocatalytic reactions. The first one is the efficiency of e− and h+ pair generation when the photocatalyst is illuminated with solar radiation. Second is the efficiency of the e−/h+ pair separation before they lose their redox ability due to recombination. The photocatalytic efficiency can be enhanced significantly by addressing the following primary issues: (i) increase the time of charge separation and recombination, (ii) broaden the solar spectrum range for photocatalyst, and (iii) changing the yield of a particular product [1, 8].Semiconductor photocatalysis system can be designed by considering the stability of the material under the light, product selectivity, and activation wavelength range [8]. TiO2 has been the most widely studied photocatalyst for many years. However, the main barriers of the TiO2 are its activation by ultraviolet light (λ ≤ 400 nm) because of the wide bandgap of TiO2 (~3.2 eV for anatase and ~3.0 eV for rutile), for which it only absorbs UV light (only about 3% of overall solar spectrum) [26]. Another major drawback of TiO2 is photogenerated electron-hole recombination, which deteriorates the photocatalytic activity [27]. Therefore, an apparent goal is the reducing bandgap of TiO2 in order to shift the absorption band to the visible region and to enhance the electron-hole separation process. The modifications of TiO2 have been accomplished by different strategies such as doping, codoping, sensitization, and coupling [28–32]. The coupling of two semiconductors provides different energy levels, which give a chance to improve a more efficient charge separation to enhance the lifetime of charge carriers and to increase interfacial charge transfer [33].Rare-earth elements are ideal dopants because of their 4f electronic configuration and spectroscopic properties [34]. Modification of electronic structure as well as crystal structure of TiO2 can be performed by doping rare-earth elements. Lanthanide ions could act as effective electron scavengers to trap the CB electrons from TiO2. Xu et al. [35] studied doping with rare-earth ions including La3+, Ce3+, Er3+, Pr3+, Gd3+, Nd3+, and Sm3+ in TiO2 which improved photocatalytic activity in the degradation of nitrite. Wang et al. [36, 37] also illustrated doping with lanthanide ions (La3+, Er3+, Pr3+, Nd3+, and Sm3+), which improved the photoelectrochemical properties as well as increased the photocurrent response and the photon current conversion efficiency in the range of 300–400 nm.


## 1.5. Cerium-Modified TiO2 Photocatalyst

Cerium is one of the most reactive rare-earth metals and can be utilized in a broad range of applications in the field of catalysis and photocatalysis. It is also one of the most generous rare-earth elements, making up about 0.0046% of the Earth’s crust by weight (64 ppm), even more abundant than copper (60 ppm) [38]. Cerium has Ce3+/Ce4+ redox couple, which can shift between CeO2 and Ce2O3 under reducing and oxidizing conditions [39, 40]. Furthermore, different electronic structures between Ce3+ (4f15d0) and Ce4+ (4f05d0) electronic configuration would lead to changed optical as well as catalytic properties [41]. The ability of Ce3+ to oxidize to Ce4+ states leads to high oxygen mobility that could result in strong catalytic potential [42], and because of this reason, it commonly applied in heterogeneous catalysis. However, CeO2 does not show good thermostable behavior because of its rapid sintering under influence of elevated temperatures [43, 44].Cerium oxide (ceria), CeO2 has the face-centered cubic (fcc) fluorite structure with eight coordinate cations (oxygen atoms) and four coordinate anions (Figure 6). The complete unit cell, Ce4O8, measures 0.51 nm (5.1 Å) on edge [44]. Ceria being an n-type semiconductor has a bandgap of 2.94 eV. The favorable bandgap of ceria makes it active under UV-Vis range and its utilization as a photocatalyst in advanced oxidation processes.Figure 6
(a) Unit cell of the CeO2 crystal structure; (b–d) (100), (110), and (111) planes of CeO2 structure (reprinted with permission from Wang and Feng) [82].
(a)
(b)
(c)
(d)Ceria is used in numerous catalytic reactions such as photocatalytic reactions and water splitting reactions, to name a few [45]. Recently, ceria has been explored as a dopant in aqueous phase photocatalytic reactions [36, 46].The photocatalytic activity of Ce-TiO2 for degradation of 2-mercaptobenzothiazole was reported by Li et al. [39]. The activity of Ce-TiO2 was higher in comparison with pure TiO2, and this was attributed to the higher surface area and better charge separation of photocatalyst [39]. Optical absorption was shifted to visible range 400–500 nm because of the introduction of Ce 4f level. Formation of 4f level and defect level were considered as a reason for delayed electron-hole recombination and activation of photocatalyst under UV visible light range [39].The phase transformation of anatase to rutile was hindered by Ce ions for low concentrations [47, 48]. Liu et al. produced Ce-TiO2 (3–7 wt % Ce) with sol-gel process and finally calcined at a different temperature. With increasing temperature, anatase phase showed growth for lower temperature domain for both pure TiO2 and Ce-TiO2 systems; however, when the temperature was increased from 600°C to 800°C, the transformation of anatase to rutile phase was inhibited in the Ce–TiO2 oxide. The main importance of this study was to show the shifting of light absorbance to the range of 380–460 nm in Ce–TiO2 [48]. For higher amount of Ce, phase segregation of ceria on the surface of TiO2 and rutile was formed [49].López et al. represented the structure and morphology of the CeO2–TiO2 oxides that were prepared by the sol-gel method as 10 wt % and 90 wt % and then calcined at 473, 673, 873, and 1073 K temperatures [50]. Experimental results showed that better thermal stability for TiO2 can be achieved by doping Ce ions to prevent particle sintering and subsequent pore collapsing [50]. Positive impact on crystallographic characteristic as well as sintering of photocatalyst was achieved by Ce doping. Distribution of cerianite on TiO2 caused substitution of Ti4+ by Ce4+ within the TiO2 anatase structure [50].Cao et al. [51] synthesized 0.2% Ce-TiO2 by the sol-gel method. The photodegradation test of methylene blue (MB) was carried out to assess the photocatalytic activity of Ce-TiO2. Interesting behavior of first rising and then falling the degradation efficiency with an increase of Ce content was found. At low Ce content in the Ce-TiO2, it is very easy for Ce4+ to capture the photogenerated electron and be reduced to Ce3+, which in turn separates the electrons and holes effectively and subsequently improve the photocatalytic activity of TiO2. However, when the Ce content exceeds a certain amount, the TiO2 crystal lattice reduces the crystallinity because of high impurities and defects. This causes shortening of the trapping center distance, increases the chance of recombination of the photogenerated charge carriers in the trapping center, and thus reduces the photocatalytic efficiency in return.Reli et al. [52] prepared novel cerium-doped TiO2 with sol-gel method within surfactant Triton X-114 in cyclohexane and showed that 1.2 wt % Ce gives the maximum photocatalytic activity for the decomposition of ammonia under UV light radiation. Hierarchical CeO2/TiO2 nanofibrous mats were prepared by Cao et al. [53] via electrospinning method. Photocatalysts prepared by electrospinning technique showed better photocatalytic efficiency for CeO2/TiO2 nanocomposite as compared to TiO2 for the degradation of RB dye under UV light irradiation.Eskandarloo et al. [54] represented TiO2/CeO2 hybrid photocatalysts, which were prepared from a powder mixture of titania and ceria. It was found that mixing TiO2 with CeO2 could facilitate efficient charge transfer, which can ease the separation of the photogenerated charge and in return increase photocatalytic efficiency [54]. Apart from here mentioned synthesis methods for Ce-TiO2 photocatalyst, their morphology and particle size are summarized in Table 3.Table 3
Literature review on various preparation methods with process parameters of Ce-TiO2 catalyst.
Materials
Dopant
Dopant concentration
Morphology
Bandgap, eV
Rate of degradation of MB dye (10−3 min−1)
References
TiO2
Ce
3 mol
Nanoparticle
2.46
24
[72]
Fe/Ce
Nanoparticle
2.5
15.4
[74]
Ce
1 wt %
Nanofiber
2.99
15
[75]
Nd
1 wt %
Nanofiber
3.1
13
[75]
Ce
5 wt %mol
Nanoparticle
16.6
[76]
Ce/N
0.6 mol
Nanoparticle
2.52
[77]
Ce
Nanofibrous mats
49.5
[53]
Ce
5 mol %
Microsphere
2.49
1.6
[71]
Ce/Pt
6.6 wt %
Nanoparticle
2.3
[78]
Ce
Thin film
2.6
2.5
[79]
Ce
2 mol
Nanobelt
2.51
34.8
[80]
Degussa P25
3.2
6.3


## 1.6. Photocatalytic Degradation Mechanism of Ce-TiO2 System

Various photocatalytic reaction mechanisms have been proposed so far depending upon the morphology and phases present, different mechanisms apply for photocatalytic reactions. Xie and Yuan [55] studied the cerium ion (Ce4+) modified TiO2 sol and nanocrystallites, which were prepared by chemical hydrothermal synthesis methods. Figure 7 illustrates the photosensitized photocatalysis mechanism of dye in the Ce4+-TiO2 sol system. In this reaction mechanism, an excited electron from dye due to visible light transfers to Ce ion. The hole left on dye can extract electrons to form hydroxyl radicals (HO⋅). In this process, the electrons are trapped by Ce4+ ions and are subsequently utilized for the formation of superoxide radicals [56]. The presence of Ce4+ on the surface of nanoparticle could develop the below reactions:Figure 7
Photosensitized photocatalysis of Ce4+-TiO2 sol system (reprinted with permission from Xie and Yuan) [55].Ce4++e−→Ce3+andCe3++O2→Ce4++O⋅2Photocatalytic degradation of dyes through semiconductor materials follows a complex path. Many researchers presented dye sensitization and subsequent charge transfer as a major reaction mechanism. Verma et al. presented photocatalytic reaction mechanism for the presence of ceria at the interface of anatase and rutile. Dependence of the catalyst’s architecture and Ce content was explored by Verma et al. [57]. The unique architecture of Ce-TiO2 system was synthesized via simple sol-gel method with varying Ce content. Doping of Ce inhibited transformation of anatase to stable rutile phase. As it was mentioned earlier that anatase has better photocatalytic activity, Ce doping showed a positive effect on photocatalytic activity which was measured by degradation of MB. Novel architecture material showed enhanced activity under a combination of ultraviolet and visible light. Reason for higher photocatalytic activity was sought to be the presence of CeO2 at the interface of anatase and rutile, which thus facilitates excellent interfacial charge transfer as shown in Figure 8. In such systems, excitation of electron from valence band to conduction band of CeO2 occur due to photoactivation via visible light (Eg = 2.94). However, CB electron of CeO2 is not capable of reduction of O2 due to its unfavorable redox potential position. This electron can transfer to CB of anatase and subsequently to rutile via interfacial charge transfer. An electron in CB of rutile can thermodynamically have accepted by O2 adsorbed on the surface and create highly reactive superoxide anions by reduction reaction. On the contrary, holes can migrate to VB of CeO2 to accept electron from adsorbed water and create ⋅OH− (hydroxyl cation) [57].Figure 8
Interfacial charge transfer mechanism (adopted with permission from Verma et al.) [57].Reaction mechanism can be summarized as follows:(1)
Photoactivation: Ce-TiO2 (system) + hv ➔ e− + h+
(2)
Ce4+ ➔ Ce3+ + e−
(3)
Interfacial charge transfer: e−(CB Ce) ➔ e−(CB anatase) ➔ e−(CB rutile)
(4)
Reduction: O2 + e−(CB rutile) ➔ ⋅O2−
(5)
⋅O2− + organic dye ➔ degradation of dye
(6)
Interfacial charge transfer: h+ (VB rutile) ➔ h+ (VB anatase) ➔ h+ (VB Ce)
(7)
Oxidation: h+ (VB Ce) + H2O ➔ HO⋅ + H+
(8)
HO⋅ + Organic dye ➔ degradation of dye


## 1.7. Photocatalytic Activity Assessment by Methyl Blue Degradation

Some studies suggest that the hydroxyl radicals play a key role as reactants for oxidation of organic substrates in aqueous photocatalysis. Therefore, hydroxyl radicals yield is essential to determine the photocatalytic efficiency and for comparison of different photocatalytic materials. In order to assess the photocatalytic efficiency of a TiO2-based catalyst, an organic and inorganic pollutant can be used as the environment. They can be divided into three categories: azo dyes [58], organic compounds [59], and inorganic gases [60]. Dye degradation is a popular method for assessing the efficiency because of its being fast and easy. Dyes have relatively high extinction coefficients to activate the photocatalyst, and they consequently will absorb a significant amount of the incoming light, which makes it difficult to assess the full photocatalytic activity [61].Methylene blue (MB) is most commonly used as a model dye for the adsorption of organic dyes from aqueous solution [62]. It is a heterocyclic aromatic hydrocarbon with a molecular formula, C16H18N3SCl [63] (molecular weight 319.85 g/mol, maximum absorption wavelength 640). Methylene blue dye is commonly used in the textile, food, and chemical industries [64, 65]. As it is a commonly used dye in numerous industrial sectors, it can mix up with domestic water and pollute it. Therefore, it is crucial to remove this toxic dye from contaminated water by converting it to inorganic benign compounds by adding photocatalyst materials to wastewater [66, 67].C16H18N3SCl + 25.5O2 ➔ 16CO2 + 6H2O + 3HNO3 + H2SO4 + HCl [68, 69].Methylene blue is found to give several environmental and health damages through contamination of water. Toxicity rate of MB is four and acute exposure by intravenous injection causes sweating, dizziness, confusion, vomiting, chest pain, and nausea [70].The structures of the dye molecules directly decide the absorption characteristic of dyes for light. In the electron absorption spectra of dyes, there are several absorption bands, which reflect the state of motion of the electrons. The absorption wavelength, absorption intensity, and the shape of the absorption band are related directly to the structure of dye molecules. Therefore, it is possible to evaluate the structural variation of dyes by investigating the variation of the electron absorption spectra during the process of degradation of the dyes.It has been reported that the photodecomposition of RhB aqueous solution in the presence of TiO2 particles as a photocatalyst has two pathways: (1) the photocatalytic pathway which would occur under UV irradiation. In this pathway, TiO2 would be activated to generate electrons under UV irradiation (λ ≤ 385 nm) to drive the process of photodegradation; (2) the photosensitization pathway which usually occurs under visible light irradiation. The bandgap of anatase TiO2 is 3.2 eV; therefore, the energy of visible light (λ > 400 nm) is not enough to excite TiO2 to produce electrons to drive the process of photodegradation. In the photosensitization pathway, where TiO2 cannot be activated by visible light, dyes will absorb visible light irradiation and can be excited, which will drive the process of photodegradation. However, the existence of TiO2 photocatalyst is a prerequisite and a crucial requirement to ensure electron carriers to contact with electron acceptors adsorbed on the TiO2 surface, which will help in the process of photodecomposition.Xie et al. [71] showed that doping content of Ce microspheres improved photocatalytic activity on the degradation of MB under visible light irradiation. Priyanka et al. [72] studied the photocatalytic activity of TiO2 and Ce-doped TiO2 nanoparticles in solar light, and the degradation of MB was monitored. Within 10 min of sunlight irradiation, the 3 mol % Ce-doped TiO2 sample could degrade about 90% of MB dye and then the degradation was almost complete in 30 min.


## 2. Conclusion

TiO2 being extensively used as a photocatalyst for degradation of organic dyes, modification of it by Ce doping for visible light activation has been presented in this review. Various synthesis processes along with different morphologies of Ce-doped TiO2 are also summarized. Complex reaction mechanisms involved with Ce-doped TiO2 with important aspects were discussed. Even though the above-mentioned reaction mechanisms occurred simultaneously, it is very difficult to conclude which mechanism is more dominating during photocatalytic degradation of dye. It would be a mere oversimplification of complex reaction mechanism to present with any one of above-mentioned reaction mechanism alone. Photocatalytic reaction mechanisms for brookite and complex systems require more elaboration. When contributions from surface area, bandgap, presence of phases, concentration of Ce, and morphology of nanomaterial are included, the complex yet complete reaction mechanism of Ce-doped TiO2 system can be modeled. Such reaction mechanism provides the ground basis for designing better material for utilization of visible light for novel applications of visible light active photocatalysts. It is expected that this review will provide a fundamental understanding of remedies to overcome bare TiO2 limitations.



---