# Preparation of Palladium-Impregnated Ceria by Metal Complex Decomposition for Methane Steam Reforming Catalysis

Authors: Worawat Wattanathana; Suttipong Wannapaiboon; Chatchai Veranitisagul; Navadol Laosiripojana; Nattamon Koonsaeng; Apirat Laobuthee
Journal: Advances in Materials Science and Engineering
 (2017)

---

## Abstract

Palladium-impregnated ceria materials were successfully prepared via an integrated procedure between a metal complex decomposition method and a microwave-assisted wetness impregnation. Firstly, ceria (CeO2) powders were synthesized by thermal decomposition of cerium(III) complexes prepared by using cerium(III) nitrate or cerium(III) chloride as a metal source to form a metal complex precursor with triethanolamine or benzoxazine dimer as an organic ligand. Palladium(II) nitrate was consequently introduced to the preformed ceria materials using wetness impregnation while applying microwave irradiation to assist dispersion of the dopant. The palladium-impregnated ceria materials were obtained by calcination under reduced atmosphere of 10% H2 in He stream at 700°C for 2 h. Characterization of the palladium-impregnated ceria materials reveals the influences of the metal complex precursors on the properties of the obtained materials. Interestingly, the palladium-impregnated ceria prepared from the cerium(III)-benzoxazine dimer complex revealed significantly higher BET specific surface area and higher content of the more active Pdδ+ (δ > 2) species than the materials prepared from cerium(III)-triethanolamine complexes. Consequently, it exhibited the most efficient catalytic activity in the methane steam reforming reaction. By optimization of the metal complex precursors, characteristics of the obtained palladium-impregnated ceria catalysts can be modified and hence influence the catalytic activity.


---

## Body

## 1. Introduction

Cerium oxide or so-called ceria (CeO2) naturally contains a high concentration of mobile oxygen vacancy sites, which are created by replacement of a fraction of the Ce4+ occupancies within the ceria lattice by trivalent cerium ions (Ce3+) [1]. These self-generated oxygen vacancy sites act as local sources or sinks for oxygen which take part in the reactions occurring at its surface and therefore enhance the interest in using ceria for a wide range of catalytic applications [2–9]. One of the promising applications of ceria is the use as catalyst support, of which desired characteristics reveal significant influences on the impregnation process of such active catalytic species (e.g,. metal nanoparticles and metal oxide additives), catalytic activity, and stability of the embedded catalysts [10]. Hence, optimizing the preparation procedure of the catalytic support is crucial in order to achieve an effective performance of catalysts.Among various synthetic procedures, thermal decomposition of metal complexes is one of the useful techniques for synthesizing ceramic materials. This method provides many advantages, that is, simple and straightforward procedure, low cost, high availability, and variability of complex formations with miscellaneous cations. Success is highlighted by our achievements within the past decades for preparations of various metal oxides by the thermal decomposition of metal-triethanolamine complexes [11–17]. In particular, ceria and rare-earth-doped ceria materials have been successfully prepared and examined for the applications as solid support catalysts [18–22] and solid electrolytes in solid oxide fuel cells [23, 24].Apart from using cerium(III)-triethanolamine complexes as starting precursors for the thermal decomposition process, the alternative choices of chelating ligands have been investigated. Recently, the use of benzoxazine dimer derivatives as ligand for metal complex precursors has revealed a promising choice for synthesizing ceria through thermal decomposition of metal complex [25]. Therefore, in this work, we extend the state of the art toward the study of the influences of precursor choices used for the metal complex formations on characteristics of the obtained ceria materials and consequently on the catalytic activity after impregnation of palladium catalysts onto the ceria solid support. Specifically, three different combinations of metal sources and organic ligands have been used to prepare metal complex precursors, namely, (a) cerium(III) nitrate hexahydrate (Ce(NO3)3·6H2O) and triethanolamine ligand, (b) cerium(III) chloride heptahydrate (CeCl3·7H2O) and triethanolamine ligand, and (c) cerium(III) nitrate hexahydrate and benzoxazine dimer,N,N-bis(5-methoxy-2-hydroxybenzyl) methyl amine (MeMD), of which the structure was reported previously [25]. Note that the metal complex precursor prepared by combining cerium(III) chloride heptahydrate and benzoxazine dimer MeMD ligand is excluded from this study due to the less stability of this metal complex.Methane steam reforming is selected to be the proof-of-concept reaction for a catalytic activity test. Unlike the conventional homogeneous combustion of methane (known as one of the most powerful greenhouse gases) at high temperature which normally emits CO and NOx as products [26], this reaction provides a useful outcome by conversion of methane to the more valuable fuel, hydrogen gas. Pd-based materials have been well known as an example of the most active catalysts for hydrogen production from natural gases such as by methane steam reformation and partial oxidation. However, the catalytic activity is not stable when directly used in the reactions. Therefore, impregnation and embedding of the Pd-based catalysts in metal oxide support are required to increase the activity and stability of the active Pd-based catalysts [10, 27]. Herein, an attempt to investigate the influences of different precursors used for preparation of ceria materials by thermal decomposition of metal complexes on the function as the catalytic support materials has been accomplished. Palladium catalyst is introduced onto the ceria solid support by employing microwave-assisted wetness impregnation of palladium(II) nitrate dihydrate with the different molar ratios. Calcination under reduced atmosphere was used to generate the catalytic-active palladium-impregnated ceria materials prior to the test of catalytic activity, which is examined by the percentages of methane conversion.


## 2. Experimental

### 2.1. Chemicals

Cerium(III) nitrate hexahydrate (Ce(NO3)3·6H2O) and cerium(III) chloride heptahydrate (CeCl3·7H2O) were supplied from Acros Organics. Palladium(II) nitrate dihydrate (Pd(NO3)2·2H2O) was purchased from Sigma-Aldrich, while triethanolamine (TEA, N(CH2CH2OH)3) was obtained from CARLO ERBA Reagents. Solvents (ethanol and 1-propanol) were bought from Merck. All chemicals were used without further purification.


### 2.2. Preparation of Cerium Complexes and Ceria

Preparation of cerium-triethanolamine complexes was carried out by the same procedure as our previous literatures [19, 22]. The cerium salt (cerium(III) nitrate hexahydrate or cerium(III) chloride heptahydrate, 150 mmol) was dissolved in 1-propanol in a round bottom flask. The equimolar amount of triethanolamine was then added to the solution of the cerium salt. The mixture was distilled for 5 h to eliminate water, a byproduct from complexation, and 1-propanol solvent. After the reaction completed, pale-yellow precipitates of the complexes were formed. The precipitates were dried using rotary evaporator.One of the derivatives of benzoxazine dimers, so-called MeMD, was used as a ligand to form complex with cerium(III) nitrate. Hereinafter, we call the ligand “benzoxazine dimer.” Cerium(III) nitrate hexahydrate and the benzoxazine dimer with the molar ratio of 1 : 6 were mixed together in ethanol in order to form cerium-benzoxazine dimer complex [25]. The complexation occurred very rapidly, since there was an immediate color change to dark purple after mixing two colorless substances together. The solution was heated and stirred for 30 min to ensure complete reaction.All the obtained complexes were used as precursors for synthesizing ceria powders. According to the thermogravimetric analyses in the previous works [19, 22, 25], the calcination temperature was selected to be 600°C. Therefore, all the prepared cerium complexes were subjected to calcination at 600°C for 2 h under air atmosphere to turn into ceria powders via thermal decomposition. The ceria powders obtained after the heat treatment of the complexes were pale-yellow colored.


### 2.3. Preparation of Palladium-Impregnated Ceria Catalysts

The prepared ceria powders were intended to be used as catalyst support for palladium. The method used for introducing palladium onto the surface of ceria powders was microwave-assisted wetness impregnation, where the ceria support was soaked with palladium salt solution. Prior to impregnation, the obtained ceria powders were ground using mortar and pestle and then sieved with the size of 45μm. Palladium(II) nitrate dihydrate with 1% and 3% by mole was dissolved in deionized water and then added to the prepared ceria. The mixtures were sonicated for 30 min and then heated with domestic microwave to help palladium particles distribute evenly on the surface of the ceria support. After that, the impregnated samples were calcined under 10% H2/He atmosphere at 700°C for 2 h.


### 2.4. Materials Characterization

X-ray diffraction (XRD) analysis was carried out at room temperature on the prepared catalysts using an X-ray diffractometer (X’Pert PRO MPD diffractometer) operating at 40 kV and 30 mA using nickel-filtered Cu Kα radiation. Diffraction patterns were recorded in the 2θ range of 20–90° by step scanning with a step interval of 0.02° and a scanning time of 2 s for each step. The crystallite size (DXRD) of the calcined powders was determined using the Scherrer equation: D=0.9λ/βcos⁡θ, where λ is the wavelength of the X-rays (1.5406 Å), θ is the scattering angle of the main reflection (111), and β is the corrected peak at full width at half maximum (FWHM) intensity. Morphology of the prepared catalysts was studied by scanning electron microscope (SEM, JEOL JSM5410) equipped with an energy dispersive X-ray analyzer (EDX). Prior to the study, the samples were mounted on stubs using carbon tape and then sputtered with Au to avoid particle charging. Moreover, transmission electron microscope (TEM, JEOL JEM-2100) equipped with an EDX unit was used for further investigation of microstructure of the materials. X-ray photoelectron spectroscopy (XPS) was operated to investigate the elemental species and their oxidation states in the obtained materials. The specific surface area (SBET) of the obtained catalysts was measured from nitrogen adsorption isotherm at 77 K using a surface area analyzer (Micromeritics) based on the Brunauer-Emmett-Teller (BET) principle. The mesopore size distribution was further analyzed based on the Barrett-Joyner-Halenda (BJH) method.


### 2.5. Study on Catalytic Activity toward Methane Steam Reforming

Conversion of methane steam reforming reaction was studied in a temperature-programmed microflow reactor operated at ambient pressure. A catalyst with approximately 50 mg was packed in the quartz tube in the reactor. Reagent gases were flowed in the tube containing the catalyst with a flow rate in the range from 20 to 200 cm3 min−1. After the reactions, the exit gas mixture was transferred via trace-heated lines (100°C) to the analysis section, which consists of a Porapak Q column, Shimadzu 14B gas chromatograph (GC). The outlet of the GC column was directly connected to thermal conductivity detector (TCD) and flame ionization detector (FID). In order to satisfactorily separate all elements, the temperature setting inside the GC column was programmed varying with time. In the first 3 min, the column temperature was constant at 60°C; it was then increased steadily by the rate of 15°C min−1 until 120°C and lastly decreased to 60°C.


## 2.1. Chemicals

Cerium(III) nitrate hexahydrate (Ce(NO3)3·6H2O) and cerium(III) chloride heptahydrate (CeCl3·7H2O) were supplied from Acros Organics. Palladium(II) nitrate dihydrate (Pd(NO3)2·2H2O) was purchased from Sigma-Aldrich, while triethanolamine (TEA, N(CH2CH2OH)3) was obtained from CARLO ERBA Reagents. Solvents (ethanol and 1-propanol) were bought from Merck. All chemicals were used without further purification.


## 2.2. Preparation of Cerium Complexes and Ceria

Preparation of cerium-triethanolamine complexes was carried out by the same procedure as our previous literatures [19, 22]. The cerium salt (cerium(III) nitrate hexahydrate or cerium(III) chloride heptahydrate, 150 mmol) was dissolved in 1-propanol in a round bottom flask. The equimolar amount of triethanolamine was then added to the solution of the cerium salt. The mixture was distilled for 5 h to eliminate water, a byproduct from complexation, and 1-propanol solvent. After the reaction completed, pale-yellow precipitates of the complexes were formed. The precipitates were dried using rotary evaporator.One of the derivatives of benzoxazine dimers, so-called MeMD, was used as a ligand to form complex with cerium(III) nitrate. Hereinafter, we call the ligand “benzoxazine dimer.” Cerium(III) nitrate hexahydrate and the benzoxazine dimer with the molar ratio of 1 : 6 were mixed together in ethanol in order to form cerium-benzoxazine dimer complex [25]. The complexation occurred very rapidly, since there was an immediate color change to dark purple after mixing two colorless substances together. The solution was heated and stirred for 30 min to ensure complete reaction.All the obtained complexes were used as precursors for synthesizing ceria powders. According to the thermogravimetric analyses in the previous works [19, 22, 25], the calcination temperature was selected to be 600°C. Therefore, all the prepared cerium complexes were subjected to calcination at 600°C for 2 h under air atmosphere to turn into ceria powders via thermal decomposition. The ceria powders obtained after the heat treatment of the complexes were pale-yellow colored.


## 2.3. Preparation of Palladium-Impregnated Ceria Catalysts

The prepared ceria powders were intended to be used as catalyst support for palladium. The method used for introducing palladium onto the surface of ceria powders was microwave-assisted wetness impregnation, where the ceria support was soaked with palladium salt solution. Prior to impregnation, the obtained ceria powders were ground using mortar and pestle and then sieved with the size of 45μm. Palladium(II) nitrate dihydrate with 1% and 3% by mole was dissolved in deionized water and then added to the prepared ceria. The mixtures were sonicated for 30 min and then heated with domestic microwave to help palladium particles distribute evenly on the surface of the ceria support. After that, the impregnated samples were calcined under 10% H2/He atmosphere at 700°C for 2 h.


## 2.4. Materials Characterization

X-ray diffraction (XRD) analysis was carried out at room temperature on the prepared catalysts using an X-ray diffractometer (X’Pert PRO MPD diffractometer) operating at 40 kV and 30 mA using nickel-filtered Cu Kα radiation. Diffraction patterns were recorded in the 2θ range of 20–90° by step scanning with a step interval of 0.02° and a scanning time of 2 s for each step. The crystallite size (DXRD) of the calcined powders was determined using the Scherrer equation: D=0.9λ/βcos⁡θ, where λ is the wavelength of the X-rays (1.5406 Å), θ is the scattering angle of the main reflection (111), and β is the corrected peak at full width at half maximum (FWHM) intensity. Morphology of the prepared catalysts was studied by scanning electron microscope (SEM, JEOL JSM5410) equipped with an energy dispersive X-ray analyzer (EDX). Prior to the study, the samples were mounted on stubs using carbon tape and then sputtered with Au to avoid particle charging. Moreover, transmission electron microscope (TEM, JEOL JEM-2100) equipped with an EDX unit was used for further investigation of microstructure of the materials. X-ray photoelectron spectroscopy (XPS) was operated to investigate the elemental species and their oxidation states in the obtained materials. The specific surface area (SBET) of the obtained catalysts was measured from nitrogen adsorption isotherm at 77 K using a surface area analyzer (Micromeritics) based on the Brunauer-Emmett-Teller (BET) principle. The mesopore size distribution was further analyzed based on the Barrett-Joyner-Halenda (BJH) method.


## 2.5. Study on Catalytic Activity toward Methane Steam Reforming

Conversion of methane steam reforming reaction was studied in a temperature-programmed microflow reactor operated at ambient pressure. A catalyst with approximately 50 mg was packed in the quartz tube in the reactor. Reagent gases were flowed in the tube containing the catalyst with a flow rate in the range from 20 to 200 cm3 min−1. After the reactions, the exit gas mixture was transferred via trace-heated lines (100°C) to the analysis section, which consists of a Porapak Q column, Shimadzu 14B gas chromatograph (GC). The outlet of the GC column was directly connected to thermal conductivity detector (TCD) and flame ionization detector (FID). In order to satisfactorily separate all elements, the temperature setting inside the GC column was programmed varying with time. In the first 3 min, the column temperature was constant at 60°C; it was then increased steadily by the rate of 15°C min−1 until 120°C and lastly decreased to 60°C.


## 3. Results and Discussion

Ceria powders were synthesized by thermal decomposition at 600°C for 2 h of three different cerium(III) complexes formed by using different precursor sources as follows: (a) cerium(III) chloride heptahydrate as a metal source and triethanolamine as a ligand (coined as CeO2-T-Cl), (b) cerium(III) nitrate hexahydrate and triethanolamine ligand (CeO2-T-N), and (c) cerium(III) nitrate hexahydrate and benzoxazine dimer derivative ligand (CeO2-B-N). Note that structural characteristics of the three metal complex precursors have been thoroughly investigated and reported in our previous works [22, 25] and are not discussed further in this recent work. The obtained ceria powders exhibit high crystallinity indexed to be the face-centered cubic CeO2 (JCPDS number 34-0394) and no crystalline impurity is observed in the XRD patterns (as demonstrated in Figure 1(a) in both red and blue curves).Figure 1
XRD patterns of the obtained products of (a) ceria after the thermal decomposition of the metal complex at 600°C for 2 h, further used as a catalytic support; (b) ceria support after microwave-assisted wetness impregnation of palladium(II) nitrate (3% mole); (c) Pd-impregnated ceria catalyst after calcination under reduced atmosphere of 10% H2 in He stream at 700°C for 2 h, denoted as 3Pd-CeO2-T-N (red curves) and 3Pd-CeO2-B-N (blue curves) with regard to the use of cerium(III) nitrate to prepare metal complexes with triethanolamine and benzoxazine dimer ligand, respectively.These obtained ceria powders were further used as catalytic support to impregnate palladium catalyst by using microwave-assisted wetness impregnation of palladium(II) nitrate dihydrate for 1% and 3% mole. For notation of the synthesized Pd-impregnated ceria catalysts reported herein, we coin the termxPd-CeO2-a-b, wherex denotes percentages ofPd impregnating amount (1 for 1% and3 for 3% mole),a denotes type of organic ligand used for preparation of metal complex (T for triethanolamine andB for benzoxazine dimer), andb denotes type of cerium salts used for preparation of metal complex (Cl for cerium(III) chloride andN for cerium(III) nitrate). The materials were characterized by XRD after the wetness impregnation process, and there is no significant change of the XRD patterns (or crystallinity) of the ceria support before and after the impregnation (Figure 1(b)). In order to activate the Pd-impregnated ceria catalyst, the materials were further treated by calcination at 700°C for 2 h under reduced atmosphere of 10% H2 in He stream. XRD patterns of the obtained Pd-impregnated ceria catalysts show no significant change from the crystallinity of the ceria support materials before impregnation (Figure 1(c)). Moreover, there are no additional diffraction peaks related to crystalline Pd-based materials, indicating the rather small particles as well as the lack of long-range crystallite ordering of the Pd-based species in the materials.With closer inspection on the XRD patterns of the Pd-impregnated ceria catalysts derived from different metal complex precursors (Figure2), it is noteworthy that a variation of metal complex precursors influences the crystallinity of the obtained materials. Specifically, crystallinity of ceria support is highest when using cerium(III) chloride and triethanolamine for preparing metal complex precursor (Figure 2, black curves), followed by the cases of using cerium(III) nitrate and triethanolamine (Figure 2, red curves), and the lowest crystallinity is in the cases of using cerium(III) nitrate and benzoxazine dimer (Figure 2, blue curves). Crystallite sizes calculated by Scherrer equation according to the XRD patterns are shown in Table 1, highlighting dependence on the metal complex precursors. The use of benzoxazine dimer as ligand for cerium complex formation notably reduces the crystallite size of the ceria product.Table 1
Crystallite size calculated by Scherrer equation according to the XRD patterns, percentage of different chemical states of the Pd-based species according to the Pd 3d XPS spectra, and specific surface area derived from BET calculation of N2 adsorption isotherm at 77 K (SBET) of the obtained Pd-impregnated ceria catalysts.
Pd-impregnated ceria catalysts
FWHM
Crystallite size (nm)
% of Pd-based species
S
B
E
T
(degree)
Pd2+
P
d
δ
+ (δ>2)
(m2/g)
1Pd-CeO2-T-Cl
0.28328
30.20
—
—
17.22
3Pd-CeO2-T-Cl
0.28363
30.16
76.6
23.4
17.70
1Pd-CeO2-T-N
0.49834
17.17
—
—
14.30
3Pd-CeO2-T-N
0.39466
21.68
75.7
24.3
11.42
1Pd-CeO2-B-N
0.77191
11.10
—
—
62.89
3Pd-CeO2-B-N
0.70906
12.07
70.0
30.0
57.01Figure 2
Comparison of XRD patterns of the Pd-impregnated ceria catalysts prepared by using ceria support derived from different metal complex precursors and impregnating Pd with two different concentrations: (a) 1Pd-CeO2-T-Cl, (b) 3Pd-CeO2-T-Cl, (c) 1Pd-CeO2-T-N, (d) 3Pd-CeO2-T-N, (e) 1Pd-CeO2-B-N, and (f) 3Pd-CeO2-B-N.Scanning electron microscopic (SEM) images of the six different Pd-impregnated ceria catalysts are illustrated in Figure3. According to the overview of SEM images, the Pd-impregnated ceria materials are observed as aggregation of nanometer-sized particles, which cannot easily distinguish the influences of the different metal complex precursors and the impregnating concentrations on the particle size and morphology. However, the corresponding energy dispersive X-ray (EDX) spectrum and the EDX elemental mapping (shown in Figure 4 as an example) indicate that cerium, oxygen, and palladium are well distributed within the material matrix. This evidence reveals preliminary success of impregnation of Pd-based catalysts onto the ceria support.Figure 3
SEM images of the Pd-impregnated ceria catalysts. (a) 1Pd-CeO2-T-Cl, (b) 3Pd-CeO2-T-Cl, (c) 1Pd-CeO2-T-N, (d) 3Pd-CeO2-T-N, (e) 1Pd-CeO2-B-N, and (f) 3Pd-CeO2-B-N. Scale bar represents 10μm.Figure 4
EDX mapping of cerium, oxygen, and palladium within 1Pd-CeO2-B-N showing a good distribution of the three elements within the material matrix and its corresponding EDX spectrum based on SEM image.To get insight into microstructures of the Pd-impregnated ceria catalysts, TEM is further used for microscopic characterization. According to the TEM images (Figure5), the effect of different metal complex precursors on the particle size of Pd-impregnated ceria catalysts is clearly observed. Specifically, Pd-impregnated ceria prepared by cerium(III)-benzoxazine dimer complex shows significantly smaller particle size (approximately 10 nm) than the ones prepared from cerium(III)-triethanolamine complexes. High-resolution TEM image of the 3Pd-CeO2-B-N catalyst (Figure 5(d)) clearly indicates the crystallite planes (111) and (200) of CeO2 with the crystallite plane size of 0.319 and 0.285 nm, respectively. Note that it is rather complicated to distinguish presence of Pd-based species by TEM due to a low content of Pd doping amount. However, EDX spectrum (Figure 5(e)) indicates the presence of Pd-based species with a better signal of Pd content than the EDX spectra observed in the bulk materials according to SEM measurements (Figure 4).Figure 5
TEM images of the Pd-impregnated ceria catalysts. (a) 3Pd-CeO2-T-Cl, (b) 3Pd-CeO2-T-N, and (c) 3Pd-CeO2-B-N. (d) High-resolution TEM image of the 3Pd-CeO2-B-N catalyst indicating the crystallite planes of CeO2; (e) the corresponding EDX spectrum of the 3Pd-CeO2-B-N catalyst based on TEM image in (c).
(a)
(b)
(c)
(d)
(e)To clearly elucidate the presence of Pd species impregnated in the materials, XPS spectra of the Pd-impregnated ceria catalysts are recorded (Figure6). The XPS results of Pd 3d5/2 could be decomposed into two components at a binding energy of 337.0 and 339.0 eV, which could be assigned to oxidized Pd species of Pd2+ and Pdδ+ (δ > 2), respectively. Moreover, the XPS results of Pd 3d3/2 could be also decomposed into two components of oxidized Pd species of Pd2+ and Pdδ+ (δ > 2). Interestingly, the Pd-impregnated ceria prepared by cerium(III)-benzoxazine dimer complex exhibits the highest content of the high-oxidative Pdδ+ (30.0%, see Table 1). Herein, we confirm successful impregnation of oxidized Pd-based catalyst on the CeO2 support.Figure 6
Pd 3d XPS profiles of the Pd-impregnated ceria catalysts. (a) 3Pd-CeO2-T-Cl, (b) 3Pd-CeO2-T-N, and (c) 3Pd-CeO2-B-N. The green and blue lines represent the decomposed spectra which could be assigned to the oxidized Pd species of Pd2+ and Pdδ+ (δ > 2), respectively. The red line represents the combination of all decomposed spectra of Pd 3d.
(a)
(b)
(c)Specific surface area (SBET in Table 1) of the obtained Pd-impregnated ceria catalysts is derived from BET calculation of N2 adsorption isotherm at 77 K (Figures 7(a) and 7(b)). The results clearly indicate that the use of benzoxazine dimer ligand leads to the formation of ceria materials with observably higher specific surface area (approximately 60 m2/g) than the cases of using triethanolamine ligand (approximately 15 m2/g). This observation may be explained by referring to the particles sizes of ceria materials observed by TEM (Figure 5). The aggregation of these smaller particles creates a higher surface area of the ceria support (higher SBET value), which is expected to distribute the Pd-impregnated nanoparticles on the ceria support in a better fashion. So the Pd-impregnated ceria catalyst derived from the use of cerium(III)-benzoxazine dimer complex as precursors shows the highest specific surface area among the other cases. Moreover, the Pd-impregnated ceria materials exhibit a hysteresis in the N2 sorption isotherm curves, indicating the characteristics of mesopore within the materials. Their corresponding mesopore size distributions are calculated based on BJH method and illustrated in Figures 7(c) and 7(d). Again, the Pd-impregnated ceria prepared by the cerium(III)-benzoxazine dimer complex shows a relative smaller mesopore size distribution which is significantly different from the materials synthesized from cerium(III)-triethanolamine complexes, highlighting the influence of precursor choices on the characteristics of the obtained materials.Figure 7
Nitrogen adsorption isotherms at 77 K of the (a) 1% and (b) 3% Pd-impregnated ceria catalysts; ((c) and (d)) their corresponding pore size distribution based on BJH method of the 1% and 3% Pd-impregnated ceria catalysts, respectively.
(a)
(b)
(c)
(d)Catalytic activity of the Pd-impregnated ceria catalysts prepared by using ceria support derived from different metal complex precursors was tested in the methane steam reforming reaction operated at ambient pressure in a microflow reactor. Percentages of methane conversion as a function of reaction time using each Pd-impregnated ceria catalyst are shown in Figure8. In each precursor type, it is clearly observed that the higher amount of Pd particles impregnated onto the ceria support is, the higher catalytic reactivity for the conversion of methane steam reforming is (the 3% Pd impregnation shows higher reactivity than the 1% Pd case with respect to the same metal complex precursors). Interestingly, a difference of catalytic activity as dependence of the metal complex precursors is notably observed. The use of Pd-impregnated ceria catalysts derived from the use of cerium(III) nitrate-benzoxazine dimer complex (blue curves) shows the highest percentage of methane conversion of 75% after 1 h of reaction time, whereas the catalytic reactivity is gradually increased as a function of reaction time when using the Pd-impregnated ceria catalysts derived from the cerium(III) chloride-triethanolamine complex precursors (black curves), reaching 70% conversion after 8 h reaction time.Figure 8
Catalytic activity of the obtained Pd-impregnated ceria catalysts according to percentages of methane conversion during the methane steam reforming reaction for hydrogen gas production.Referring to the XPS spectra and BET surface area analysis, the Pd-impregnated ceria catalysts derived from the use of cerium(III) nitrate-benzoxazine dimer complex contain higher amount of Pdδ+ (δ > 2) species and higher BET surface area than the other cases. The Pdδ+ species reveal that more electrons transfer to the oxide support and are more oxidatively active than the metallic Pd and the Pd2+ species [28–32]. The higher oxidation state Pdδ+ should accelerate the C-H bond activation of the CH4 molecule on the coordinatively unsaturated (CUS) Pd and consequently enhances the catalytic activity [31, 32]. Hence, it reveals a consequence of the higher catalytic activity of the Pd-impregnated ceria by means of the higher BET specific surface area and the higher content of the more active Pdδ+ (δ > 2) species, which can be modified by the choice of metal complex precursors used for synthesis of the ceria support by the thermal decomposition method.


## 4. Conclusions

Characteristics of ceria support materials are strongly influenced by the choice of metal complex precursors used for the thermal decomposition process. Optimizing the metal complex precursors leads to a systematic control of particles sizes and consequently specific surface area of the obtained ceria support. The higher surface area of ceria support, achieved by the use of cerium(III)-benzoxazine dimer complex as the thermal decomposition precursor, enhances the quality of impregnation of the catalytically active Pd-based species onto the ceria support. Moreover, the higher content of the more active Pdδ+ (δ > 2) species within the Pd-impregnated ceria catalysts derived from the cerium(III)-benzoxazine dimer complex creates a higher catalytic performance for the methane steam reforming reaction. By optimization of the metal complex precursors, characteristics and catalytic activity of the obtained Pd-impregnated ceria catalysts can be diligently modified and enhanced.



---