# Magnetic and Electrical Properties of Nitrogen-Doped Multiwall Carbon Nanotubes Fabricated by a Modified Chemical Vapor Deposition Method

Authors: María Luisa García-Betancourt; Yadira Itzel Vega-Cantu; Sofía Magdalena Vega-Díaz; Aarón Morelos-Gómez; Mauricio Terrones; Emilio Muñoz-Sandoval
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Chemical vapor deposition (CVD) is a preferential method to fabricate carbon nanotubes (CNTs). Several changes have been proposed to obtain improved CNTs. In this work we have fabricated nitrogen-doped multiwall carbon nanotubes (N-MWCNTs) by means of a CVD which has been slightly modified. Such modification consists in changing the content of the by-product trap. Instead of acetone, we have half-filled the trap with an aqueous solution of NaCl (0–26.82 wt.%). Scanning electron microscope (SEM) characterization showed morphological changes depending upon concentration of NaCl included in the trap. Using high resolution transmission electron microscopy several shape changes on the catalyst nanoparticles were also observed. According to Raman spectroscopy results N-MWCNTs fabricated using pure distillate water exhibit better crystallinity. Resistivity measurements performed on different samples by physical properties measurement Evercool system (PPMS) showed metallic to semiconducting temperature dependent transitions when high content of NaCl is used. Results of magnetic properties show a ferromagnetic response to static magnetic fields and the coercive fields were very similar for all the studied cases. However, saturation magnetization is decreased if aqueous solution of NaCl is used in the trap.


---

## Body

## 1. Introduction

After the discovery, structural identification, and bulk production of carbon nanotubes (CNTs) the interest of researchers about these nanostructures increased exponentially, and the big quest for novel applications started [1–4]. Enormous and exhaustive work, carried out by several important groups, have exhibited their unique thermal, magnetic, mechanical, chemical, and electronic properties [5–7], thus leading to the design of new devices for biosensing, nanoprobing, spintronics, field emission, and other important applications [8–11].One of the most important challenges in nanotube science nowadays is the control of the morphology because this is the route to control the physicochemical properties [10–12]. Depending on the desired applications, modifications in the chemical vapor deposition (CVD) method offer an optional approach to induce some important properties to carbon nanostructures, such as the introduction of water vapor together with the inert gas flow to grow very large carbon nanotubes [13, 14], or the modulation of the shape, size, and crystallinity of catalytic metallic nanoparticles determining the chiral-selective growth of CNTs [15]. In the case of the introduction of contaminants, some authors used alkali chlorides in order to deform the straight carbon nanofibers into helical structure or belts [16, 17]; Lv and coworkers employed Cl as a cleaner of nanoparticles when introduced into the CVD, which evaporates during the process [18, 19]. In other cases it is desirable to have defects in carbon nanotubes such as nonhexagonal rings, dangling bonds, doping, non-sp2, and folding because they are the origin of producing many forms and new carbon architectures [12–21] by adjusting some parameters in the chemical vapor deposition (CVD) method. For example, the introduction of sulfur in the atomizer solution allowed the synthesis of random 3D structures [22]. A two-step CVD was used for the production of three-dimensional networks [23] and long tipped CNTs [24]. Pressure and temperature fluctuations can produce branched junctions [25, 26]. Currently, the versatility of CVD has been exploited widely, allowing modifications in their involved parameters in order to produce highly defective N-MWCNTs. Notwithstanding, research about this method continues increasing because the mechanism of growth of CNT remains unclear.In the present work, following previous research [27, 28] we are proposing a simple modification of the CVD synthesis to alter the morphology and properties of N-MWCNTs, also known as CNx; the modification consists in changing the solution of the by-product trap in the synthesis. We used deionized water and aqueous solutions of NaCl at different weight concentrations, low (1 wt.%), half-saturated (15.84 wt.%), and saturated (26.92 wt.%); instead of acetone which has been normally employed, we used water and aqueous solutions of NaCl at different weight concentrations. We also proposed the growth mechanism of these nanostructures.


## 2. Materials and Methods

Forests of nitrogen-doped carbon nanotubes (N-MWCNTs) were produced by a slightly modified CVD method using the one-furnace configuration with a by-product trap at the outlet of the quartz tube. The pyrolyzed solution containing 94% of benzylamine (C7H9N, Sigma Aldrich), as a source of carbon and nitrogen, and 6% ferrocene (FeCp2-, Sigma Aldrich) for the catalytic nanoparticles was prepared and placed in a reservoir plugged in to a pulse generator. The reaction was performed during 30 min and using a one-furnace system as is shown in Figure 1. The mixture solution of ferrocene and benzylamine was placed into the atomizer reservoir (see Figure 1). In order to obtain enough material to be characterized a small piece of SiO2/Si was placed inside the quartz tube at the middle of the furnace. In this zone, the temperature is stable (850°C ± 3°C). In a first experiment 200 mL of acetone was put inside the trap. We present some images of such CNT in Supplementary Information (see Figure S1 in Supplementary Material available online at http://dx.doi.org/10.1155/2015/587416). In a second experiment, we half-filled the trap with deionized water (Fermont) instead of acetone. For the following experiments, the density of deionized water was increased by adding NaCl at different weight concentrations (1 wt.%, 15.84 wt.%, and 26.92 wt.%). The obtained samples were called in agreement with the density of the liquid in the trap as CNx-1 for acetone (density 0.79 g/cm2), CNx-2 for deionized water (density 1.00 g/cm2), CNx-3, CNx-4, and CNx-5 for the cases of aqueous solutions of NaCl and densities of 1.01 g/cm2, 1.21 g/cm2, and 1.56 g/cm2, respectively. In all cases the total mixture poured in the trap was 200 mL, which is equivalent to a half-filled trap. For the purpose of having an inert atmosphere inside of the quartz tube (see Figure 1), a constant argon flow rate of 2.5 L/min was established. In all experiments, the temperature was 850°C inside of the furnace where the substrates were situated. The solution mixture was atomized from the solution container by an ultrasonic generator during 30 min. In each case, the substrate was taken out for characterization using scanning electron microscopy (SEM-FEI XL 30 SFEG). In order to prepare the samples for high resolution transmission electron microscopy (HRTEM-FEI TECNAI F30) a small quantity was scraped from the substrates and incorporated into a vial with ethanol, ultrasonicated for 5 minutes and drop-cast on the grids. In the case of X-ray diffraction (RX Advance) characterization the whole substrate was used; the settings follow: 2θ from 10° to 90° and step size of 0.04 during 5 seconds. Raman characterization was performed using a laser of 514 nm in a Raman Renishaw Micro-Raman equipment. Thermogravimetric analysis was achieved using a TGA-Thermo Cahn, model Versa Therm apparatus. The magnetic and resistivity measurements were carried out in a physical properties measurement system (PPMS, Quantum Design). In order to verify the substance effect in the morphology and physical properties of N-MWCNTs we carried out additional experiments as following: (i) the trap was filled with 300 mL of mixture solution of benzylamine and ferrocene (2.5% wt.%); (ii) there was not any substance in the atomizer reservoir; (iii) several clean substrates were placed inside of quartz tube; (iv) the experimental setup was run normally. The resultant sample (substrate and CNT) from this experiment were characterized by SEM (Figure S4 of Supplementary Information) and analyzed in an optical emission spectrophotometer (OES) in order to measure ppm of Na or Cl.Figure 1
Typical CVD setup for carbon nanotubes synthesis using one furnace. Each component used for producing our samples is indicated in the figure. The size of the trap is only representative. The level used in the trap is an important parameter for all our experiments because they are determining the structure and physical properties of resultant N-MWCNTs nanotubes. The substrate is 10 cm long and was placed inside the quartz tube at the middle of the furnace (20 cm).


## 3. Results

Figure2 exhibits SEM images of N-MWCNTs obtained from the different synthesis conditions described above. Figure 2(a) is SEM images of N-MWCNTs fabricated using acetone in the trap (CNx-1 sample); such CNTs are vertically aligned and in general they present bamboo morphology [29, 30] with diameters around 50 nm; sometimes it is possible to observe CNTs with smaller diameters enrolled to the thicker CNTs. In the case when the trap is half-filled with distilled water (CNx-2 sample), the fabricated CNTs have larger diameters and present morphologies which are showed in Figure 2(b); some collapsed structures can be present (see inset). If an aqueous solution of NaCl is used in the trap an additional phenomena could be observed (CNx-3 sample). In this case, sharp morphologies of N-MWCNTs were observed. It seems that such morphologies are formed because the end compartments of the bamboo structure are damaged. Apparently, small nanoparticles play an important role to form sharp CNTs. Another well detectable defect mostly observed in the CNx-4 samples is nanoparticles attached to the external walls of N-MWCNTs known as “nanolumps” [31, 32]. Such nanoparticles may abundantly appear forming “lumpy” nanostructures as is shown in Figure 2(d); Li and coworkers obtained lumpy CNT as a result of air-assisted synthesis [33]. It is probable that these lumps could catalyze thin N-MWCNTs forming the branch morphology [34]. More complex defects were detected in the sample CNx-5. Coalescence of N-MWCNTs and ruptures of thick CNTs with arms or branches were observed (Figure 2(e)). As can be seen at this figure very thin N-MWCNTs with few layers are emerging from such coalesced nanotubes. In Figure 2(f) the catalytic nanoparticles responsible for the growth of CNx-5 are shown. Notice the sharp nail structure as claws. This situation can be one of the main effects of putting saturated NaCl aqueous solution inside the trap.Figure 2
SEM images of the aligned N-MWCNTs grew over Si/SiO2 substrates displaying the different morphologies observed in our samples: (a) typical morphology of N-MWCNTs produced with acetone in the trap (CNx-1); (b) N-MWCNTs fabricated using deionized water in the trap (CNx-2); (c) image showing tip morphology of N-MWCNTs formed when an aqueous solution of NaCl is used (1.0 wt.% case; CNx-3); (d) image of N-MWCNTs in the case of CNx-4 case: here lumps are the main defects detected; (e) image of CNx-5 case (aqueous solution of NaCl 26.92 wt.%): complex structures are observed with very thin CNTs; (f) root part of CNx-5: N-MWCNTs also fabricated with aqueous solution of NaCl 26.92 wt.%, showing dramatic changes in the catalytic nanoparticles. More related SEM figures can be seen in SI (Figure S4).
(a)
CN
x
-
1
(b)
CN
x
-
2
(c)
CN
x
-
3
(d)
CN
x
-
4
(e)
CN
x
-
5
(f)Figure3 displays representative TEM images of the different fabricated N-MWCNTs. Figure 3(a) contains a micrograph of the case CNx-2 (water), showing N-MWCNTs with diameters as small as 2 nm and as big as 60 nm. Most of N-MWCNTs exhibited bamboo-type morphology, some of them with conical and other with cylindrical compartments. It is difficult to say how nitrogen is incorporated into the N-MWCNTs without X-ray photoelectron spectroscopy (XPS) analysis of the samples. However, there are some studies showing that the shape of compartments can be associated with the type of nitrogen inclusion in the graphitic structure of CNT [35]. Both shapes of compartments are also observed in N-MWCNTs fabricated when acetone is used in the trap (see Figure S1, Supplementary Information). Figure 3(b) also exhibits representative TEM images of N-MWCNTs corresponding to the CNx-2 (water). Here, it is possible to observe a thin CNT with two collapsed sites and a CNT with lumps of different sizes (Figure 3(b)). In the case of aqueous solution with NaCl 1 wt.% (distilled water slightly altered with NaCl) another morphology of N-MWCNTs is observed, namely, broken CNTs with a sharp end where an encapsulated conical-shape nanoparticle is observed (Figure 3(c)); for the case CNx-4 using aqueous solution of NaCl 15.84 wt.% (water with NaCl at half-saturation) the sample shows a lump attached to CNT (Figure 3(d)). The sample CNx-5, when the trap was filled with aqueous solution of NaCl at 26.92 wt.% (saturated water of NaCl), exhibited complex morphologies as displayed in Figures 3(e) and 3(f). Apparently coaxial CNTs with large diameters and ruptures are formed in this case (Figure 3(e)). These CNTs can be coalesced with others to form the structure presented in the right part of Figure 3(e). In addition, it is probable to find multiterminal junctions containing different shapes and sized metallic nanoparticles (Figure 3(f)).Figure 3
TEM images displaying the representative morphologies of fabricated N-MWCNTs over Si/SiO2 substrates using different aqueous solutions of NaCl in the trap, namely, (a) and (b) CNx-2; (c) CNx-3; (d) CNx-4; and (e) and (f) CNx-5.
(a)
CN
x
-
2
(b)
CN
x
-
2
(c)
CN
x
-
3
(d)
CN
x
-
4
(e)
CN
x
-
5
(f)
CN
x
-
5The diameter distribution corresponding to the different obtained N-MWCNTs samples is presented in Figure S5. The diameter distribution has a Gaussian-type shape in the case ofCNx-1, which is the sample produced using a trap with acetone. In the case of CNx-2 and CNx-3 the respective diameter distribution curves exhibit bimodal behaviors. In the cases of CNx-4 and CNx-5 the diameter distributions are also bimodal however with lower pronounced differences. The average diameters for the different cases were 62±2 nm, 47±3 nm, 61±2 nm, 36±2 nm, and 37±2 nm for CNx-1, CNx-2, CNx-3, CNx-4, and CNx-5, respectively.It is probable that the different CNT morphologies found in our samples could be attributed to the catalytic metallic nanoparticles. The final shape of these nanoparticles could give us information about the process involved in the growth of different N-MWCNTs observed. Figure4 depicts TEM images of some encapsulated metallic nanoparticles found in distinct N-MWCNTs samples. Long nanowires with more than 500 nm length (Figure 4(a)) were observed in the samples CNx-2 and CNx-3 (low content of NaCl in the trap). Encapsulated nanoparticles with irregular morphologies distort the CNT structure (Figure 4(b)) or can form junctions (Figure 4(c)). These types of nanoparticles were observed in CNx-4 which were produced with a moderate quantity of aqueous solution NaCl in the trap. Very small encapsulated nanoparticles along the CNTs (internal multiparticles) were detected in N-MWCNTs fabricated with a saturated aqueous solution NaCl in the trap (Figure 4(d)). Also lumps encapsulating nanoparticles with oval morphology or nanoparticles incrusted in the wall could be found in this saturated case (Figures 4(e) and 4(f)). It seems that the inclusion of NaCl in the trap with water produces effects among the nanoparticles. However, it is not possible to be sure about that, unless more sophisticate experiments are performed to elucidate the real growth mechanism.Figure 4
(a) Sharp N-MWCNTs encapsulating a nanowire longer than 500 nm followed by a cylinder nanoparticle at the tip of the CNT; (b) N-MWCNTs with irregular-shaped metallic nanoparticles; (c) oval-shaped nanoparticle followed by two N-MWCNTs forming a junction; (d) two N-MWCNTs with sharp morphology: one of them has multiple encapsulated metallic nanoparticles; (e) oval lump that shows the graphitic carbon shells formed in the compartments; (f) “oval” nanoparticle encapsulated laterally in the walls of the bamboo structure of N-MWCNTs.
(a)
CN
x
-
3
(b)
CN
x
-
4
(c)
CN
x
-
4
(d)
CN
x
-
5
(e)
CN
x
-
5
(f)
CN
x
-
5Figure5 shows the X-ray diffractograms for all the samples obtained from the diverse situations. CNx-1 presents the two typical predominant phases characteristic of N-MWCNTs fabricated with acetone in the trap, namely, C and Fe3C; possibly α-Fe phase is also present. Probably the most intense peak of (110) of α-Fe around 45° is spliced with the plane (103) of Fe3C. The inclusion of distilled water inside of the trap (CNx-2) changes the diffraction patterns and some peaks of Fe3C were relatively increased such as (112), (021), (200), and (120) planes for 2θ: 37.73°, 38.03°, 40.09°, and 41.28°, respectively; the peaks for the planes (140) and (313) at 78.27° and 78.78° present a relative higher intensity as well. Note that the Fe3O4 is clearly present in this case. For CNx-3, which is the case when the aqueous solution contains 1.0 wt.%, the appearance of iron oxides (maghemite γ-Fe2O3 and magnetite Fe3O4) in the samples is clearly seen in Figure 5 (green plot). However, if the percentage of NaCl is increased in the aqueous solution used in the trap, the intensities of peaks corresponding to iron oxides phase are reduced or in some cases they disappear. This situation could be due to the Na+ and Cl− ions saturated in the water molecules, limiting the oxygen reflux entrance to the system. This could be the reason why the X-ray diffractogram of CNx-1 is very similar to the respective CNx-5.Figure 5
X-ray diffractograms for the N-MWCNTs samples synthesized with different liquids in the residual bubbler (trap):CNx-1 (acetone), CNx-2 (water), CNx-3 (low 1 wt.% of NaCl), CNx-4 (half-saturation, 15.84 wt.% of NaCl), and CNx-5 (saturation, 26.92 wt.% of NaCl).In order to analyze the thermal stability and reactivity of our N-MWCNTs we have carried out thermogravimetric analysis (TGA) under oxygen atmosphere. The samples were analyzed using a rate heating of 10 C/min. Figure6 shows the degradation curve for each sample, plotted as loss mass (%) versus temperature. Al curves are similar with some differences related to the samples, such as the degradation temperature, obtained from the maximum value of the first loss mass derivative (see inferior inset at the left), calculated from the degradation plots. The maximum values of first loss mass derivative are plotted for each sample at the top inset at the right. As can be seen, the plot has in general a decreasing behavior as the weight percent of NaCl was increased, showing a maximum value of 458°C for CNx-2 (only water in the trap), revealing that this sample is the least reactive compared to the other cases. It seems that water in the trap produces CNTs more resistant to oxidation with fewer defects or nitrogen atoms in the walls. Possibly this result could be correlated with the fact that the compartments of CNx-2 are longer than the other cases (see Figure 4(b)). The decrease of degradation temperature in the samples CNx-3, CNx-4, and CNx-5 could be attributed to the introduction of additional defects to the graphitic surface of CNTs. The mass loss at lower temperatures could be imputed by the quantity of amorphous carbon in the sample. We observed that CNx-2 contains the higher percentage of amorphous carbon (~1.24%), higher than CNx-1 (~1.04%) and CNx-3, CNx-4, and CNx-4 (0.62%, no observable%, 0.85%, resp.). The residual mass observed at the final degradation temperature corresponds to the iron oxide; the content was also different for each sample. CNx-1 exhibits the lowest residual mass (7.41%), while for CNx-2 and CNx-3 the percentage is very similar (7.94% and 8.08%, resp.) and for CNx-4 and CNx-5 the percentage of residual was increasing (8.44% and 8.72%, resp.). The reason for this increase can be associated with the agglomeration of metallic nanoparticles particles in the later cases, as was observed with the presence of nanolumps which are bigger for these cases.Figure 6
Thermogravimetric profile of N-MWCNTs synthesized using different substances in the trap (acetone, deionized water, and three concentrations by weight of NaCl). The insets correspond to the first derivative of thermogravimetric profile (left) and degradation temperature.For the purpose of studying the microstructure and crystalline order of our carbon nanotubes we performed Raman spectroscopy measurements. We used excitation energy of 514 nm over the samples of N-MWCNTs synthesized with the different liquids in the residual bubbler. The Raman spectra are presented in Figure7(a), plotted between 100 and 3500 cm−1. The typical characteristic bands of carbonaceous materials are indicated in the plot, the D band situated at 1352 cm−1 (defect mode), G band situated at 1580 cm−1 (graphite mode), and G′ located near 2500–2800 cm−1 (second order mode). The peaks appeared in the range 200–500 nm in two of the spectra (CNx-2 and CNx-3, marked with asterisks) which very probably correspond to the presence of iron oxides compounds [36–38], as X-ray diffraction analysis results have shown in such samples. The D band, G band, and G′ shifts are within the intervals of 1353 cm−1 to 1359 cm−1, 1587 cm−1 to 1590 cm−1, and 1795 cm−1 to 1712 cm−1, respectively. We can observe a small shifting towards lower frequencies for the samples synthesized using deionized water or aqueous solution with NaCl with respect to the as-produced with acetone in the residual bubbler, but specifically the G shifting to lower frequencies indicates a reduction of N doping for CNx-2 (produced with water). This situation is concomitant with the observation in TGA, where a less reactive sample was observed. We studied the sample from the rates in intensities ID/IG and IG′/IG; such values are plotted in Figures 7(b) and 7(c) as a function of the sample. In each sample, the D band intensity is lower than G band intensity. At the same time G′ band intensity increases as the weight concentration of NaCl increases. The sample with high degree of disorder or with nongraphitic carbon is the CNx-2 (matches with TGA analysis), followed by CNx-3 whose values are 0.83 and 0.75, respectively. The most crystalline sample resulted in the CNx-4 with a rate ID/IG value of 0.38. The rate IG′/IG increases with the increment of density in the liquid, probably indicating that we have quite crystalline samples when substances other than acetone are used in the trap. The G′ band is a particular mark of carbonaceous materials; it is higher in pure materials, such as nondoped CNT and graphene.Figure 7
(a) Raman spectra of N-MWCNTs synthesized using different substances in the residual bubbler: acetone (C3H6O), water (H2O), and aqueous solution of NaCl at three weight concentrations (1%, 15.48%, and 26.92%). The RBM: D, G, and G′ modes are listed in each spectrum. The asterisks indicate that some peaks related to the signals come from Si/SiO2 substrates. Rates (b) ID/IG and (c) IG′/IG plotted as a function of the sample.
(a)
(b)
(c)Figures8(a)–8(f) exhibit the hysteresis loops measured in the interval ±1 T for 2 K, 100 K, and 300 K for the N-MWCNTs samples synthesized with different substances in the trap. For each plot, we have included the corresponding SEM images of N-MWCNTs forest grown on Si/SiO2 (Figures 8(f)–8(j)). In addition, we have drawn the encapsulated nanoparticles observed by TEM to each case. In each group of nanoparticles, their intervals of dimensions (D-diameter and L-length) and aspect ratio (AR) obtained from each sample are listed. In general the magnetic measurements confirm the ferromagnetic nature of the samples. CNx-1 exhibits a hysteresis loop shown in Figure 8(a); the forest is aligned perpendicularly to the substrate, clean and free of amorphous carbon material on its surface. The nanoparticles of this sample have a conical morphology that is usually located at the tip of the N-MWCNTs. As an example, see the SEM image in the blue square for acetone, where you can see the top of the forest of N-MWCNTs. The contrast of the image allows appreciating the conical nanoparticles with maximum aspect ratio of 5. Their diameters and lengths are within the ranges 20–60 nm and 90–276 nm, respectively. The inset drawing represents the morphology which can take the nanoparticle when encapsulated by N-MWCNTs. The inserted HRTEM image shows the morphology with conical shape in N-MWCNTs [39]. Hysteresis loops of samples synthesized with the other substances are similar to acetone (see Figures 8(b)–8(e)), but properties are quite different. The respective forests show that CNTs are also aligned with some defects and amorphous material on the surface (Figures 8(g)–8(j)). The morphologies of the nanoparticles is totally different from each other (see drawings in each case); we can say that nanoparticles shape is dependent on the type of substance used in the trap. For the cases of CNx-2 (H2O) and CNx-3 (1 wt.% NaCl) nanoparticles have very similar morphologies, including nanowires with aspect ratios greater than 5. The diameters and lengths of the nanoparticles for CNx-2 are in the ranges 3–78 nm and 23–479 nm, respectively, while for CNx-3 the diameters and lengths are within the ranges of 8–60 nm and 11–348 nm, respectively. The aspect ratios are 16 and 25 for CNx-2 and CNx-3, respectively, and the nanoparticles lengths in CNx-3 can be more than 1 micron. When increasing the NaCl weight concentration the dimensions of nanoparticles take smaller dimensions. This fact is confirmed by the data reported in each case. CNx-4 (half-saturation of NaCl) shows faceted nanoparticle morphologies, with diameter and length within the ranges of 8–60 nm and 11–348 nm, respectively, and aspect ratio of 10. CNx-5 (saturated aqueous solution of NaCl) has nanoparticles with diameters within the range of 5–22 nm and length of 7–118 nm, with lower aspect ratio of 10.Figure 8
(a–e) Hysteresis loops measured at 2, 200, and 300 K for encapsulated metallic nanoparticles inCNx synthesized using different substances inside the trap. (f–j) SEM images of CNx forests grown over silicon substrates and drawings of the encapsulated nanoparticles in CNx. *Courtesy and permission from [39].The analysis of hysteresis curves (saturation, coercive field, and remanence versus temperature) is presented in Figure9. The saturation as a function of temperature is exhibited in Figure 9(a) where we can see that it is easier to saturate the ferromagnetic material contained in CNx-2 (water) and CNx-3, CNx-4, and CNx-5 (with aqueous solutions of NaCl) than CNx-1 (acetone). Figure 9(b) presents the plot of coercive field as a function of temperature for the five samples. The coercive field decreases when increasing temperature in all samples, but the values decrease for CNx-2, CNx-4, and CNx-5. The sample CNx-3 is very similar to CNx-1. The remanence, shown in Figure 9(c), has a decreasing trend as a function of temperature for each sample. However, the remanence decreases for the cases of nanoparticles synthesized N-MWCNTs contained in different substances into the trap, with lower values for CNx-5.Figure 9
(a) Saturation, (b) coercivity, and (c) remanence values as a function of temperature for encapsulated metallic nanoparticles inCNx synthesized in acetone (CNx-1), water (CNx-2), and various concentrations by weight NaCl in water (CNx-3, CNx-4, and CNx-5).
(a)
(b)
(c)According to Figure9 the most notable changes observed in the magnetic properties are related to the magnetization saturation. Since the iron carbide and α-Fe phases are present in all cases, these changes could be associated with the presence of iron oxides phases (see X-ray diffractograms of Figure 5) or due to the morphological changes of magnetic nanoparticles inside or attached to CNT [40, 41]. For example, CNx-1, which is the control sample, presents mostly the typical Fe3C with a high saturation magnetization. Although some other important peaks were not observed, it is very probable that α-Fe phase is also present (the peak with the maximum intensity is located around 45 degrees). The shape of magnetic nanoparticles in this case is conical with an aspect ratio around 3. Even though the majority of the magnetic phase is also Fe3C in CNx-2 samples, the saturation magnetization is reduced when water is used in the trap (see Figure 8(b)). One of the probable explanations to this behavior is the morphology changes in the nanoparticles. A statistical analysis was performed to 60 TEM images of CNx-2 case, which showed that 34% of the nanoparticles have a spherical shape (first drawing) and the other 66% presented other kinds of morphologies (see right drawings of Figure 8(g)). The reduction of the saturation magnetization in this case is around 33.3%, which is approximately the percentage of nanoparticles which are spherical in type. However, there is another source that could contribute to the reduction of saturation magnetization, namely, the magnetite phase present in this sample. The peak at around 35 degrees shows the existence of that phase in sample CNx-2 (see CNx-2 diffractogram in Figure 5). Note that it was not possible to observe the peak having the second strongest value, which is around 62 degrees. Magnetite in bulk phase has a saturation magnetization of around 85–100 emu/g, which is around 50% lower than the respective saturation magnetizations of Fe3C (169 emu/g for bulk) phase [42–45]. Therefore, a combination of such effects could be the cause of the observed changes. In the case of CNx-3 the statistical analysis yielded the fact that only 6.8% of the magnetic nanoparticles have a spherical shape. Therefore, the effect of morphology changes of magnetic nanoparticles may not be important. However, now the γ-Fe2O3 phase is present in this sample and could be one of the cause of the reduction of saturation magnetization. If the CNx-2 and CNx-3 X-ray diffractograms of Figure 5 are compared, it is possible to observe that in the CNx-3 case two additional diffraction peaks are present. These peaks are around 34 and 54 degrees and might be associated with (311) and (422) planes of the maghemite (γ-Fe2O3) phase, which has around 90 emu/g of saturation magnetization in the case of bulk phase. The presence of γ-Fe2O3 and Fe3O4 phases could be causing the saturation magnetization to reduce by more than 50% (see Figure 9(a)). An interesting situation is observed in the X-ray diffractogram of case CNx-4. The diffraction peaks corresponding to (311) and (422) planes of the maghemite phase are not present anymore and the structure corresponding to the Fe3C phase is drastically modified (see Figure 5CNx-4 case). Also, the diffraction peak at 35 degrees related to the Fe3O4 magnetite phase is notably reduced. In addition, three new diffraction peaks are present, namely, at around 29, 56, and 77 degrees. The first two peaks correspond to (220) and (551) planes of magnetite and the last peak corresponds to (140) plane of cementite. Note how the intensity of the peak at around 43 degrees is greatly increased in comparison with the other Fe3C diffraction peaks. This peak can also be associated with the (400) plane of magnetite. Apparently, the magnetic behavior in this case is due to different causes than the previous situations. It is probable that the magnetic magnetite, cementite, and α-Fe phases are those that determine the behavior of the saturation magnetization. Note also that the phase of maghemite was not well observed. Figure S8 (Supplementary Information) shows that, in elongated nanoparticles, mostly α-Fe and cementite phases are contained. In this case, in order to explain the increase of saturation of magnetization, additional information that we need to consider is the morphological changes experienced by magnetic nanoparticles. The drawings on the left side of Figure 8(i) show complex structures of the encapsulated nanoparticles in CNx-4. According to a statistical analysis, it was found that only 8.6% of them have spherical shape and the rest present an elongated structure. It is noteworthy that some nanoparticles have square-type morphology (see Figure S7 in Supplementary Information). Finally, the X-ray diffractogram of CNx-5 does not show any Fe-oxides phases. Only defined diffraction peaks of Fe3C and α-Fe planes were observed. It seems that, in this case, the morphology changes are the only ones responsible for the observed decrease of saturation magnetization (more than 50%). Figure S9 shows several HRTEM images of such nanoparticles. These particles take different shapes such as spherical (13%), cylindrical (28%), deformed (23%), seed (28%), oval (5%), and arrow (3%) [27]. It is well known that if the morphologies of the ferromagnetic nanoparticles are different, it is very probable that the process of magnetization will be strongly dependent upon their shape and size and also on the applied magnetic field direction [39, 41]. The irregular shapes of ferromagnetic nanoparticles in this CNx-5 case could have reduced the saturation magnetization due to surface or finite size effects [46, 47]. Note that the coercivity values follow the trend in aspect ratio where CNx-3 with an aspect ratio of 25 had the highest values and the samples with the lowest aspect ratio of 10 (CNx-4 and CNx-5) exhibited the lowest coercivity (see drawings of Figure 8).The resistance of the N-MWCNTs was measured by the four-probe method as a function of the temperature in the range 2–395 K (Figure10). The resistance of CNx-2 is an order of magnitude higher than CNx-1 and CNx-3 (Figure 10(a)), but the three resistance curves have similar behavior. However the resistance of CNx-4 and CNx-5 (Figure 10(b)) is two orders of magnitude lower than CNx-1 with a different curve behavior. All samples showed two kinds of behaviors of electronic transport. The samples CNx-1, CNx-2, and CNx-3 showed semiconducting electronic transport with very large values of resistivity at low temperatures (2 K). The samples CNx-4 and CNx-5: (i) at very low temperatures (below 20 K) the slope of the resistance increases when temperature decreases; (ii) between 20 K and 300 K, the resistance increases with the increment of temperature showing metallic behavior. It is not possible to associate these two last behaviors with the N-MWCNTs themselves. However, it is very probable that some Na contamination of the substrates during the synthesis occurred. Results from OES characterization of samples (substrates and N-MWCNTs) obtained by the additional experiments, which were performed to verify the effect of trap substance over morphology and physical properties, showed that when the trap is filled with aqueous solution of NaCl (15.84 wt.% case) a gram of N-MWCNTs contains 0.204 mg of Na and in each gram of Si substrate there is 0.00835 mg of Na. This could explain the metallic transport at temperatures above 20 K. Similar kind of effect has been observed by p-doping with the intercalation of I, K, and Br within SWNT bundles, with a metallic-like behavior at high temperatures (>50 K) and semiconducting behavior at lower temperatures (<50 K) [48, 49]. However the mechanism is not yet well understood and we encourage more research regarding this effect.Figure 10
Resistance behavior ofCNx synthesized with different substances in the residual bubbler of CVD setup. (a) Black line corresponds to CNx-1 (acetone), red line to CNx-2 (water), and blue line to CNx-3 (aqueous solution of 1 wt.% of NaCl) and (b) red line corresponds to CNx-4 (aqueous solution of 15.48 wt.% of NaCl) and orange line to CNx-5 (aqueous solution of 26.92 wt.% of NaCl). Resistances of CNx-1, CNx-2, and CNx-3 have typical semiconducting behavior. At the same time, the samples prepared with aqueous solution NaCl in the residual bubbler show metallic response above 20 K and semiconducting behavior at very low temperature.
(a)
(b)In the CVD experiment we are proposing the use of different liquids other than acetone. We have used water and aqueous solutions of NaCl at three weight concentrations (1%; 15.48%, half-saturation; and 26.92%, saturation). In all cases we consider that a reflux evaporation of water molecules and some atoms of Na or Cl are entering to the hot zone of the furnace and participating in the catalysis of N-MWCNTs. The feedstock that contains the C, Fe, and N is carried by the argon gas. However, it seems that the reflux evaporation is also present in the process of synthesis. For example, in the case of water the oxygen directly affects the catalytic particles, keeping the catalyst alive [13, 14]. This effect could be responsible for the different nanoparticle shapes that catalyze N-MWCNTs in different morphologies, sizes, and diameters. In the case of H, this can be associated with C forming hydrocarbons which probably could be cleaned by the gas. In the case of the presence of NaCl the steps are similar, but the water evaporation is different because NaCl was solubilized in water, where the water molecules are attracted by the Na+ and Cl− ions. The water is attracted by the crystal structure in the individual ions encircling and dissolving slowly the NaCl. The water molecules alignment depends on the ion kind (Na+ or Cl−). The negative part of water molecule (O) surrounds the Na+ ion, while the positive side (H) surrounds the Cl− ion. Taking into account this limitation to water, we may consider the fact that less water vapor is refluxing to the hot zone as well as some Na+ or Cl− are entering by the water evaporation. In the case of saturated NaCl there are not available water molecules due to the fact all of them are associated with ions. First, water molecules and ions surrounded by water molecules are contaminating the feedstock deposited in the substrate. CNT has started growing but encapsulating small nanoparticles, at different sites in the hollow structure. The effects of the water molecules have an effect similar to the previous case, but in this case the Na or Cl ions are also participating in the catalysis, probably reducing the sizes of nanoparticles. In order to alternatively test how the Na or Cl could be affecting the growing of carbon nanotubes a specific experiment was performed. Instead of introducing aqueous solution of NaCl (case 15.84 wt.%) inside the trap, a more complicated CVD setup was used to fabricate the carbon nanotubes (see Figure S5 in Supplementary Information). In this case two sprayers were used, one with the typical solution containing benzylamine and ferrocene and the other with an aqueous solution of NaCl. Both systems were switched on at same time with different sprayer conditions of frequency and power to tray to obtain similar results to the original experiment with the trap. A total of 335 mg of powder was obtained from the quartz tube. Figure S6 (Supplementary Information) shows the fabricated N-MWCNTs selected from different part of the sample, which show different lengths but similar aspect at the magnification showed (see Supplementary Information) [50]. From these images it was possible to observe the dramatic damages due to the NaCl vapor introduced in the synthesis. More research using this bi-sprayer system is in progress.


## 4. Summary

The CVD configuration was modified to synthesize controlled morphologies in nitrogen-doped carbon nanotubes by increasing the density of the liquid trap used in the bubbler. The SEM and HRTEM images revealed the fact that the morphology of N-MWCNTs was modified substantially exploding the versatility of CVD. We studied the present morphologies in the sample by observing the hollow core morphology, which resulted in the fact that the bamboo structure not only was observed, but also collapsed, MWCNT, and different junctions. When increasing the density of the liquid in the residual bubbler it affected not only the tube morphology, but also the metallic nanoparticles morphology. X-Ray diffraction showed the presence of different phases of iron such as oxides (magnetite and maghemite) and most of the planes were observed in N-MWCNTs synthesized with water (CNx-2) and low concentration of NaCl + H2O (CNx-3) in the bubbler. The peaks of planes of iron oxides are not usually observed in samples of N-MWCNTs synthesized with acetone in the bubbler. Raman and thermogravimetric analysis exhibited the fact that water produces a noncrystalline sample that could be attributed to the high degree of disorder in the sample or high level of amorphous carbon. Yet, the presence of NaCl in water showed samples with higher crystalline structure and more reactivity. Magnetic measurements lower coercive fields, remanence, and saturation for the increment of NaCl. Resistivity plots revealed the semiconducting nature of the N-MWCNTs synthesized with water and low NaCl, similar to acetone, but with different orders of magnitude. The samples synthesized with aqueous solution of NaCl showed metallic behavior due to the fact that the resistances were increased with the increment of temperature. More sophisticated experiments can be designed to tune the morphological and chemical and physical properties of N-MWCNTs.



---