# The Development of Biomimetic Spherical Hydroxyapatite/Polyamide 66 Biocomposites as Bone Repair Materials

Authors: Xuesong Zhang; Ming Lu; Yan Wang; Xiaojing Su; Xuelian Zhang
Journal: International Journal of Polymer Science
 (2014)

---

## Abstract

A novel biomedical material composed of spherical hydroxyapatite (s-HA) and polyamide 66 (PA) biocomposite (s-HA/PA) was prepared, and its composition, mechanical properties, and cytocompatibility were characterized and evaluated. The results showed that HA distributed uniformly in the s-HA/PA matrix. Strong molecule interactions and chemical bonds were presented between the s-HA and PA in the composites confirmed by IR and XRD. The composite had excellent compressive strength in the range between 95 and 132 MPa, close to that of natural bone.In vitro experiments showed the s-HA/PA composite could improve cell growth, proliferation, and differentiation. Therefore, the developed s-HA/PA composites in this study might be used for tissue engineering and bone repair.


---

## Body

## 1. Introduction

Hydroxyapatite (HA), with similar composition to natural bone, has been extensively developed for biomedical applications in the past decades because it has good biocompatibility and bioactivity and can bond with host bone directly [1–4]. However, HA ceramics devices, such as filler and porous scaffold, exhibit manifest brittleness, which vastly impedes its clinical applications.In order to obtain a biomaterial with good bioactivity and good mechanical properties, more and more attention focuses on the researches and medical applications of a composite combining hydroxyapatite with a polymer because such composite possesses both good bioactivity (HA) and good ductility (polymer) [4–10]. Those biocomposites are biocompatible and osteoconductive and hence can bond with host bone directly and thus form a uniquely strong biomaterial-bone interface.Previous studies have showed that the properties of HA have manifest effects on the properties of the HA/PA composites [11–16]. For example, HA with atom molar Ca/P ratio of 1.67 is very stable and hence shows poor degradability and bioactivityin vivo while HA with lower atom molar Ca/P ratio (form 1.5 to 1.67) exhibits higher solubility (degradability) and bioactivity. The size of HA also affects the properties of the obtained composite. A nanoscaled HA shows better bioactivity and enhancement effects on polymer and obtains higher mechanical properties compared to the microsized one because the nanosized HA have obvious surface effect and small size effect [17, 18].Recently, nanohydroxyapatite (n-HA)/polyamide 66 biocomposites were developed by Sichuan University [1, 17]. The composites were shown to have good mechanical strength similar to natural bone and good compatibility. Furthermore, cage and vertebral plate developed by those composites have been used for spine repair successfully [19]. However, n-HA preparation process is very complex. Moreover, conglomeration of nanoparticles has been deemed to be one of the main obstacles in the preparation of polymer-based nanobiomaterials [20]. Hence, in this study, we prepared HA/PA composite composed of spherical HA with extrusion method, an industrialized method, and the composition, mechanical properties, and preliminary cell responses to the composites were investigated in order to assess the potential application as bone repair materials.


## 2. Materials and Method

### 2.1. Preparation of s-HA/PA

PA (BASF, A3K) and s-HA (provided by Sichuan University) were mixed proportionally and were processed by extrusion method according to the following parameters: extrusion temperature: 230–275°C; main engine speed: 50 HZ; feed rate: 40 HZ.S-HA/PA composites with 10 w%, 20 w%, 30 w%, and 40 w% s-HA content were prepared and named as 10HA/PA, 20HA/PA, 30HA/PA, and 40HA/PA, respectively.


### 2.2. IR, XRD, and Mechanical Strength

The composition and structure of the 30HA/PA composite were characterized by Fourier transform infrared spectroscopy (170SX FT-IR Spectrometer; Nicolet, Madison, WI) and X-ray diffraction (X’Pert pro-MPD; Philips, Eindhoven, The Netherlands). To observe the S-HA distribution in PA matrices, the 30HA/PA composite was fractured in liquid nitrogen, and a cross-sectional specimen was observed under a scanning electron microscope (Hitachi S-450). In addition, the effects of the amount of s-HA on the compressive strength of the composite were assessed in the composite samples (Φ10×12 mm) containing different amounts of s-HA (0 wt%, 10 wt%, 20 wt%, 30 wt%, and 40 wt%) using a mechanical testing machine (REGER 30–50; Shenzhen Reger Co., Ltd., Shenzhen, China) with 50 kN load cells. The cross-head speed was 5 mm/minute, and the load was applied until the specimens were compressed to about 20% of their original height. Five replicates were carried out for each group, and the results are expressed as the mean ± standard deviation.


### 2.3. Cytocompatibility

Culture cells in a humidified atmosphere with 5% CO2, MG63 osteoblast-like cells were cultured in Dulbecco’s Modified Eagle Medium (DMEM) supplemented with 10% FBS plus 100 U/mL penicillin and 100 μg/mL streptomycin sulfate. Cells were incubated in 25 cm2 flasks to reach 80% confluence and then detached for further experiments. For all the cell culture experiments, 30HA/PA composite samples with the size of Ф12×2 mm were used and MAC and tissue culture plate as controls. These samples were sonicated in ethanol and sterilized using ethylene oxide gas.


#### 2.3.1. Cell Proliferation and Morphology

MG-63 osteoblast-like cells were cultured in DMEM supplemented with 10% FBS plus 100 U/mL penicillin and 100μg/mL streptomycin sulfates at 37°C in a humidified 5% CO2 atmosphere. Cells were incubated in 25 cm2 flasks to reach 80% confluence and then detached for further experiments. n-DA/MC composite scaffold samples with the size of Ф6×2 mm were used for all the cell culture experiments, and tissue culture plate (TCP) was used as a control. These samples were sonicated in ethanol and sterilized using ethylene oxide gas.The proliferation of MG-63 cells on the scaffold samples was determined by using MTT (3-{4,5-dimethylthiazol-2yl}-2,5-diphenyl-2H-tetrazolium-bromide) assay. MTT measures changes in absorbance at a specific wavelength and is widely used for measuring cell viability. The production of purple formazan in osteoblast cultures with or without the samples was measured after 1, 3, 5, and 7 days of incubation in 24-well culture plates. For this purpose, 100μL of MTT (MajorBiochem, Shanghai, China) solution (5 mg/mL) was added to each well (containing either cells alone or pellets with adherent cells removed from the original culturing well) and the cells were incubated for 4 hours. Subsequently, the culture medium was aspirated and dimethyl sulfoxide 1000 μL/well was added to dissolve the formazan completely for 10 minutes at 37°C. Then 100 μL of solution was transferred to a 96-well enzyme-linked immunosorbent assay plate and the absorbance was measured at 490 nm using a microplate reader (Multiskan MK3, Thermo Electron Corporation, Waltham, MA). Phase contrast microscopy was used to observe the cell morphology.


#### 2.3.2. ALP Activity

MG-63 cells were seeded on the samples and ALP activity of cells was measured at 1, 3, 5, and 7 days, and the culture medium in 24-well plates was aspirated. 200μL, 1% Nonidet P-40 (NP-40) solution was added to each well at room temperature (RT) and incubated for 1 hour. The cell lysate was obtained and centrifuged. 50 μL supernatant and 50 μL 2 mg/mL p-nitrophenylphosphate (Sangon, Shanghai, China) substrate solution composed of 0.1 mol/L glycine, 1 mmol/L MgCl2·6H2O were added to 96-well plates and incubated for 30 min at 37°C. The reaction was quenched by addition of 100 μL, 0.1 N NaOH; the absorbance of ALP was quantified at the wavelength of 405 nm using a microplate reader (SPECTRAmax 384, Molecular Devices, USA). The total protein content in cell lysate was determined using the bicinchoninic acid (BCA) method in aliquots of the same samples with the Pierce protein assay kit (Pierce Biotechnology Inc., Rockford, IL), read at 560 nm, and calculated according to a series of albumin (BSA) standards. The ALP levels were normalized to the total protein content at the end of the experiment.


## 2.1. Preparation of s-HA/PA

PA (BASF, A3K) and s-HA (provided by Sichuan University) were mixed proportionally and were processed by extrusion method according to the following parameters: extrusion temperature: 230–275°C; main engine speed: 50 HZ; feed rate: 40 HZ.S-HA/PA composites with 10 w%, 20 w%, 30 w%, and 40 w% s-HA content were prepared and named as 10HA/PA, 20HA/PA, 30HA/PA, and 40HA/PA, respectively.


## 2.2. IR, XRD, and Mechanical Strength

The composition and structure of the 30HA/PA composite were characterized by Fourier transform infrared spectroscopy (170SX FT-IR Spectrometer; Nicolet, Madison, WI) and X-ray diffraction (X’Pert pro-MPD; Philips, Eindhoven, The Netherlands). To observe the S-HA distribution in PA matrices, the 30HA/PA composite was fractured in liquid nitrogen, and a cross-sectional specimen was observed under a scanning electron microscope (Hitachi S-450). In addition, the effects of the amount of s-HA on the compressive strength of the composite were assessed in the composite samples (Φ10×12 mm) containing different amounts of s-HA (0 wt%, 10 wt%, 20 wt%, 30 wt%, and 40 wt%) using a mechanical testing machine (REGER 30–50; Shenzhen Reger Co., Ltd., Shenzhen, China) with 50 kN load cells. The cross-head speed was 5 mm/minute, and the load was applied until the specimens were compressed to about 20% of their original height. Five replicates were carried out for each group, and the results are expressed as the mean ± standard deviation.


## 2.3. Cytocompatibility

Culture cells in a humidified atmosphere with 5% CO2, MG63 osteoblast-like cells were cultured in Dulbecco’s Modified Eagle Medium (DMEM) supplemented with 10% FBS plus 100 U/mL penicillin and 100 μg/mL streptomycin sulfate. Cells were incubated in 25 cm2 flasks to reach 80% confluence and then detached for further experiments. For all the cell culture experiments, 30HA/PA composite samples with the size of Ф12×2 mm were used and MAC and tissue culture plate as controls. These samples were sonicated in ethanol and sterilized using ethylene oxide gas.


### 2.3.1. Cell Proliferation and Morphology

MG-63 osteoblast-like cells were cultured in DMEM supplemented with 10% FBS plus 100 U/mL penicillin and 100μg/mL streptomycin sulfates at 37°C in a humidified 5% CO2 atmosphere. Cells were incubated in 25 cm2 flasks to reach 80% confluence and then detached for further experiments. n-DA/MC composite scaffold samples with the size of Ф6×2 mm were used for all the cell culture experiments, and tissue culture plate (TCP) was used as a control. These samples were sonicated in ethanol and sterilized using ethylene oxide gas.The proliferation of MG-63 cells on the scaffold samples was determined by using MTT (3-{4,5-dimethylthiazol-2yl}-2,5-diphenyl-2H-tetrazolium-bromide) assay. MTT measures changes in absorbance at a specific wavelength and is widely used for measuring cell viability. The production of purple formazan in osteoblast cultures with or without the samples was measured after 1, 3, 5, and 7 days of incubation in 24-well culture plates. For this purpose, 100μL of MTT (MajorBiochem, Shanghai, China) solution (5 mg/mL) was added to each well (containing either cells alone or pellets with adherent cells removed from the original culturing well) and the cells were incubated for 4 hours. Subsequently, the culture medium was aspirated and dimethyl sulfoxide 1000 μL/well was added to dissolve the formazan completely for 10 minutes at 37°C. Then 100 μL of solution was transferred to a 96-well enzyme-linked immunosorbent assay plate and the absorbance was measured at 490 nm using a microplate reader (Multiskan MK3, Thermo Electron Corporation, Waltham, MA). Phase contrast microscopy was used to observe the cell morphology.


### 2.3.2. ALP Activity

MG-63 cells were seeded on the samples and ALP activity of cells was measured at 1, 3, 5, and 7 days, and the culture medium in 24-well plates was aspirated. 200μL, 1% Nonidet P-40 (NP-40) solution was added to each well at room temperature (RT) and incubated for 1 hour. The cell lysate was obtained and centrifuged. 50 μL supernatant and 50 μL 2 mg/mL p-nitrophenylphosphate (Sangon, Shanghai, China) substrate solution composed of 0.1 mol/L glycine, 1 mmol/L MgCl2·6H2O were added to 96-well plates and incubated for 30 min at 37°C. The reaction was quenched by addition of 100 μL, 0.1 N NaOH; the absorbance of ALP was quantified at the wavelength of 405 nm using a microplate reader (SPECTRAmax 384, Molecular Devices, USA). The total protein content in cell lysate was determined using the bicinchoninic acid (BCA) method in aliquots of the same samples with the Pierce protein assay kit (Pierce Biotechnology Inc., Rockford, IL), read at 560 nm, and calculated according to a series of albumin (BSA) standards. The ALP levels were normalized to the total protein content at the end of the experiment.


## 2.3.1. Cell Proliferation and Morphology

MG-63 osteoblast-like cells were cultured in DMEM supplemented with 10% FBS plus 100 U/mL penicillin and 100μg/mL streptomycin sulfates at 37°C in a humidified 5% CO2 atmosphere. Cells were incubated in 25 cm2 flasks to reach 80% confluence and then detached for further experiments. n-DA/MC composite scaffold samples with the size of Ф6×2 mm were used for all the cell culture experiments, and tissue culture plate (TCP) was used as a control. These samples were sonicated in ethanol and sterilized using ethylene oxide gas.The proliferation of MG-63 cells on the scaffold samples was determined by using MTT (3-{4,5-dimethylthiazol-2yl}-2,5-diphenyl-2H-tetrazolium-bromide) assay. MTT measures changes in absorbance at a specific wavelength and is widely used for measuring cell viability. The production of purple formazan in osteoblast cultures with or without the samples was measured after 1, 3, 5, and 7 days of incubation in 24-well culture plates. For this purpose, 100μL of MTT (MajorBiochem, Shanghai, China) solution (5 mg/mL) was added to each well (containing either cells alone or pellets with adherent cells removed from the original culturing well) and the cells were incubated for 4 hours. Subsequently, the culture medium was aspirated and dimethyl sulfoxide 1000 μL/well was added to dissolve the formazan completely for 10 minutes at 37°C. Then 100 μL of solution was transferred to a 96-well enzyme-linked immunosorbent assay plate and the absorbance was measured at 490 nm using a microplate reader (Multiskan MK3, Thermo Electron Corporation, Waltham, MA). Phase contrast microscopy was used to observe the cell morphology.


## 2.3.2. ALP Activity

MG-63 cells were seeded on the samples and ALP activity of cells was measured at 1, 3, 5, and 7 days, and the culture medium in 24-well plates was aspirated. 200μL, 1% Nonidet P-40 (NP-40) solution was added to each well at room temperature (RT) and incubated for 1 hour. The cell lysate was obtained and centrifuged. 50 μL supernatant and 50 μL 2 mg/mL p-nitrophenylphosphate (Sangon, Shanghai, China) substrate solution composed of 0.1 mol/L glycine, 1 mmol/L MgCl2·6H2O were added to 96-well plates and incubated for 30 min at 37°C. The reaction was quenched by addition of 100 μL, 0.1 N NaOH; the absorbance of ALP was quantified at the wavelength of 405 nm using a microplate reader (SPECTRAmax 384, Molecular Devices, USA). The total protein content in cell lysate was determined using the bicinchoninic acid (BCA) method in aliquots of the same samples with the Pierce protein assay kit (Pierce Biotechnology Inc., Rockford, IL), read at 560 nm, and calculated according to a series of albumin (BSA) standards. The ALP levels were normalized to the total protein content at the end of the experiment.


## 3. Results

### 3.1. IR and XRD

Figure1(a) showed the characteristic peaks of the PA. The –CO–NH– peaks could be observed at about 1556 cm−1, 3307 cm−1 (N–H stretching), and 1642 cm−1 (C=O). Bonds at 2857 and 2925 cm−1 were the characteristic peaks of C–H vibration. In Figure 1(b), the PO43- peaks were found at about 566, 953, 1033, and 1107 cm−1. The OH– peaks were found at about 3569 and 605 cm−1. Figure 1(c) was the spectra of composite. It can be seen that peaks of both s-HA and PA presented in the composite, and the peaks had shown clear shifts. The peaks of PA shifted from 1556, 1642, and 3307 cm−1 to 1552, 1637, and 3301 cm−1. Owing to the existence of hydrogen, it will absorb more energy than before, resulting in the absorption wavelength getting shorter. So, the peaks of HA shifted from 3569 to 3561 cm−1. Those peaks’ shift suggests that hydrogen formed between s-HA and PA.Figure 1
FT-IR spectra of PA (a), s-HA (b), and s-HA/PA composite (c).Figure2 showed the XRD patterns of PA (a), s-HA/PA composite (b), and s-HA (c). Figure 2(c) indicated that the major characteristic peaks of HA appeared around 25.9°, 32°, 33°, 33.9°, and 39.7°, which were corresponding to the peaks of the bone apatite [5]. Two strong peaks at 2θ=19.9°, 23.5° were attributed to PA in Figure 2(a). Because of the interaction of HA and copolymer, the orderliness of PA was seriously disturbed, which is responsible for the decrease of the intensities of PA peaks in Figure 2(b).Figure 2
The XRD patterns of PA (a), s-HA/PA composite (b), and s-HA (c).


### 3.2. Compressive Strength of s-HA/PA Composite

The compressive strength of composite with different s-HA is shown in Table1. It can be seen that the compressive strength increased from 67 MPa to 132 MPa with the increase of s-HA from 0 to 40% in composite.Table 1
Compressive strength of s-HA/PA composite.
Samples
Compression strength (MPa)mean ± SD
PA
67
±
7
10HA/PA
95
±
15
20HA/PA
108
±
9
30HA/PA
126
±
8
40HA/PA
132
±
11


### 3.3. SEM Analysis

The SEM photographs of s-HA and s-HA/PA composite are shown in Figure3. The s-HA was about 20–60 μm (Figure 3(a)) and uniformly distributed in PA matrix (Figure 3(b)). In addition, no cracks between s-HA and PA were observed.The morphology of s-HA (a) and s-HA/PA (b).
(a)
(b)


### 3.4. Cytocompatibility

#### 3.4.1. Cell Proliferation

The optical density (OD) values can provide an indicator of cell viability on biomaterials; thus the proliferation of MG63 cells on 30HA/PA composite was evaluated using MTT. As shown in Figure4, the OD values of the composite and the controls (tissue culture plate, TCP) increased with time, suggesting that MG63 cells were viable on these samples, showing positive cellular responses. No significant difference for OD values was found between the composite and controls at 1, 3, and 5 days. However, the OD value of the composite was higher than those of control at 7 days, indicating that the 30HA/PA composite could promote cell proliferation at 7 days.Figure 4
Viability of MG63 cells on s-HA/PA composite by MTT assay, TCP as controls,*P<0.05.


#### 3.4.2. ALP Activity

ALP activity of MG63 cells cultured on the 30HA/PA composite was determined at 1, 3, 5, and 7 days. The results are shown in Figure5. The ALP activity increased with time for both the composite and TCP. No significant difference between the composite and TCP was found at 1 and 3 days. However, the level of ALP activity of cells on the HA/PA composite was obviously higher than those of MAC and tissue culture plate at 5 and 7 days.Figure 5
ALP activity of MG63 cells cultured on s-HA/PA composite, TCP as controls,*P<0.05.


#### 3.4.3. Cell Morphology

The phase contrast microscopy images of MG63 cells cultured with the HA/PA composite scaffolds are shown in Figure6. It can be seen that, after 1 day of culture, the cells had a sheet shape and there were large intercellular spaces. After 3 days, the population of the cells increased and the intercellular spaces reduced manifestly. The cells kept increasing and the gap between cells disappeared after 5 and 7 days, indicating that the HA/PA composite scaffolds had no negative effects on cells growth and maintain normal cell morphology.Phase contrast microscopy images of MG63 cells cultured on the s-HA/PA composite for 1 day (a), 3 days (b), 5 days (c), and 7 days (d).
(a)
(b)
(c)
(d)


## 3.1. IR and XRD

Figure1(a) showed the characteristic peaks of the PA. The –CO–NH– peaks could be observed at about 1556 cm−1, 3307 cm−1 (N–H stretching), and 1642 cm−1 (C=O). Bonds at 2857 and 2925 cm−1 were the characteristic peaks of C–H vibration. In Figure 1(b), the PO43- peaks were found at about 566, 953, 1033, and 1107 cm−1. The OH– peaks were found at about 3569 and 605 cm−1. Figure 1(c) was the spectra of composite. It can be seen that peaks of both s-HA and PA presented in the composite, and the peaks had shown clear shifts. The peaks of PA shifted from 1556, 1642, and 3307 cm−1 to 1552, 1637, and 3301 cm−1. Owing to the existence of hydrogen, it will absorb more energy than before, resulting in the absorption wavelength getting shorter. So, the peaks of HA shifted from 3569 to 3561 cm−1. Those peaks’ shift suggests that hydrogen formed between s-HA and PA.Figure 1
FT-IR spectra of PA (a), s-HA (b), and s-HA/PA composite (c).Figure2 showed the XRD patterns of PA (a), s-HA/PA composite (b), and s-HA (c). Figure 2(c) indicated that the major characteristic peaks of HA appeared around 25.9°, 32°, 33°, 33.9°, and 39.7°, which were corresponding to the peaks of the bone apatite [5]. Two strong peaks at 2θ=19.9°, 23.5° were attributed to PA in Figure 2(a). Because of the interaction of HA and copolymer, the orderliness of PA was seriously disturbed, which is responsible for the decrease of the intensities of PA peaks in Figure 2(b).Figure 2
The XRD patterns of PA (a), s-HA/PA composite (b), and s-HA (c).


## 3.2. Compressive Strength of s-HA/PA Composite

The compressive strength of composite with different s-HA is shown in Table1. It can be seen that the compressive strength increased from 67 MPa to 132 MPa with the increase of s-HA from 0 to 40% in composite.Table 1
Compressive strength of s-HA/PA composite.
Samples
Compression strength (MPa)mean ± SD
PA
67
±
7
10HA/PA
95
±
15
20HA/PA
108
±
9
30HA/PA
126
±
8
40HA/PA
132
±
11


## 3.3. SEM Analysis

The SEM photographs of s-HA and s-HA/PA composite are shown in Figure3. The s-HA was about 20–60 μm (Figure 3(a)) and uniformly distributed in PA matrix (Figure 3(b)). In addition, no cracks between s-HA and PA were observed.The morphology of s-HA (a) and s-HA/PA (b).
(a)
(b)


## 3.4. Cytocompatibility

### 3.4.1. Cell Proliferation

The optical density (OD) values can provide an indicator of cell viability on biomaterials; thus the proliferation of MG63 cells on 30HA/PA composite was evaluated using MTT. As shown in Figure4, the OD values of the composite and the controls (tissue culture plate, TCP) increased with time, suggesting that MG63 cells were viable on these samples, showing positive cellular responses. No significant difference for OD values was found between the composite and controls at 1, 3, and 5 days. However, the OD value of the composite was higher than those of control at 7 days, indicating that the 30HA/PA composite could promote cell proliferation at 7 days.Figure 4
Viability of MG63 cells on s-HA/PA composite by MTT assay, TCP as controls,*P<0.05.


### 3.4.2. ALP Activity

ALP activity of MG63 cells cultured on the 30HA/PA composite was determined at 1, 3, 5, and 7 days. The results are shown in Figure5. The ALP activity increased with time for both the composite and TCP. No significant difference between the composite and TCP was found at 1 and 3 days. However, the level of ALP activity of cells on the HA/PA composite was obviously higher than those of MAC and tissue culture plate at 5 and 7 days.Figure 5
ALP activity of MG63 cells cultured on s-HA/PA composite, TCP as controls,*P<0.05.


### 3.4.3. Cell Morphology

The phase contrast microscopy images of MG63 cells cultured with the HA/PA composite scaffolds are shown in Figure6. It can be seen that, after 1 day of culture, the cells had a sheet shape and there were large intercellular spaces. After 3 days, the population of the cells increased and the intercellular spaces reduced manifestly. The cells kept increasing and the gap between cells disappeared after 5 and 7 days, indicating that the HA/PA composite scaffolds had no negative effects on cells growth and maintain normal cell morphology.Phase contrast microscopy images of MG63 cells cultured on the s-HA/PA composite for 1 day (a), 3 days (b), 5 days (c), and 7 days (d).
(a)
(b)
(c)
(d)


## 3.4.1. Cell Proliferation

The optical density (OD) values can provide an indicator of cell viability on biomaterials; thus the proliferation of MG63 cells on 30HA/PA composite was evaluated using MTT. As shown in Figure4, the OD values of the composite and the controls (tissue culture plate, TCP) increased with time, suggesting that MG63 cells were viable on these samples, showing positive cellular responses. No significant difference for OD values was found between the composite and controls at 1, 3, and 5 days. However, the OD value of the composite was higher than those of control at 7 days, indicating that the 30HA/PA composite could promote cell proliferation at 7 days.Figure 4
Viability of MG63 cells on s-HA/PA composite by MTT assay, TCP as controls,*P<0.05.


## 3.4.2. ALP Activity

ALP activity of MG63 cells cultured on the 30HA/PA composite was determined at 1, 3, 5, and 7 days. The results are shown in Figure5. The ALP activity increased with time for both the composite and TCP. No significant difference between the composite and TCP was found at 1 and 3 days. However, the level of ALP activity of cells on the HA/PA composite was obviously higher than those of MAC and tissue culture plate at 5 and 7 days.Figure 5
ALP activity of MG63 cells cultured on s-HA/PA composite, TCP as controls,*P<0.05.


## 3.4.3. Cell Morphology

The phase contrast microscopy images of MG63 cells cultured with the HA/PA composite scaffolds are shown in Figure6. It can be seen that, after 1 day of culture, the cells had a sheet shape and there were large intercellular spaces. After 3 days, the population of the cells increased and the intercellular spaces reduced manifestly. The cells kept increasing and the gap between cells disappeared after 5 and 7 days, indicating that the HA/PA composite scaffolds had no negative effects on cells growth and maintain normal cell morphology.Phase contrast microscopy images of MG63 cells cultured on the s-HA/PA composite for 1 day (a), 3 days (b), 5 days (c), and 7 days (d).
(a)
(b)
(c)
(d)


## 4. Discussion

HA has an inorganic component similar to that in human hard tissue. It has a good biocompatibility and can bond to bone tissue in body [1, 21]. The outstanding biological performance of HA biomaterial has been widely proved in the forms of bone filler, coating on titanium alloy, and recently as scaffolds for cell carrier in bone tissue engineering [1, 5, 9, 11]. So, HA is a good candidate for the preparation of ceramic/polymer composites. Previous studies have reported many performances of HA; for example, size and Ca/P ratio exhibited manifest effects on the properties of the resultant composite [22]. Hence, in this study, the spherical HA was used as inorganic phase to enhance polyamide 66 to obtain novel composites, and their properties were characterized. It was shown by IR and XRD that chemical bond was formed between s-HA and PA, which was considered to be a strong interface bond. So when the s-HA are imposed with external pressure, the pressure could be transferred into PA via chemical bond, thus improving the whole mechanical strength. The interface interactions between the polymer and inorganic mineral have been proved to have positive effects on the mechanical properties and the distribution of inorganic particles into the composites [23–25].In this study, the prepared s-HA/PA composite has a good homogeneity (Figure3). Furthermore, no obvious interface debonding could be observed in the fracture surface of composite, suggesting that there was a good interface between s-HA and PA, which was consistent with the results of IR and XRD.The compressive strength of the composites with 10–40 w% s-HA content ranged between 95 and 132 MPa, which was close to that of the natural bone, between 50 and 140 MPa [26]. It has been reported that n-HA/PA composite showed good mechanical strength and could meet the fundamental requirements for supporting after implantation [1]. Compared to that, s-HA/PA composites showed higher compressive strength. Therefore, s-HA/PA should have enough compressive strength for the support requirementsin vivo.To evaluate thein vitro biocompatibility of biomaterials, the cell culture experiments are useful approaches [27, 28]. In this study, the MG63 cells were used to test the cytocompatibility of the s-HA/PA composite. The results showed that the MG63 cells could proliferate better on the composites, as was demonstrated by the MTT assay, suggesting positive cellular responses to this material. After 7-day culture, the OD values of the composites were significantly higher than those of TCP, indicating that the composites could promote the cell proliferation better and had higher cytocompatibility than TCP. The phase contrast microscopy results exhibited that cells population increased with high speed and the spaces among the cells disappeared at 5 days and that the cells maintain normal morphology, suggesting that the s-HA/PA composites had no negative effect on the cell attachment and proliferation. Furthermore, the ALP activity has been used as an early marker for functionality and differentiation of osteoblasts duringin vitro experiments [29–33]. The results showed that the ALP of the MG63 cells cultured on the s-HA/PA composites exhibited significantly higher levels of expression than that of the cells cultured on TCP at 5 and 7 days, indicating that the composite could induce better the differentiation of the cell into osteogenic cells.


## 5. Conclusion

Novel s-HA/PA biocomposites were prepared by extrusion method in this study. The s-HA was homogenously distributed into HA/PA matrix and chemical bond was formed at the interface between organic phase and inorganic phase. The compressive strength of composite was close to that of natural bone. Furthermore, the s-HA/PA composites could not only promote cell proliferation but also induce the differentiation of the cell into osteogenic cells. The results indicated that the s-HA/PA biocomposite might be a candidate for bone repair material.



---

*Source: 579252-2014-07-06.xml*