# Synthesis and Physicochemical Behaviour of Polyurethane-Multiwalled Carbon Nanotubes Nanocomposites Based on Renewable Castor Oil Polyols

Authors: Alaa Ali; Kamal Yusoh; S. F. Hasany
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

Polyurethanes (PUs) are high performance materials, with vast industrial and engineering applications. In this research, effects of Multiwalled Carbon Nanotubes (MWCNTs) on physicochemical properties of Castor Oil based Polyurethanes (COPUs) were studied. MWCNTs were added in different weight percentages (0% to 1% wt) in a castor oil based polyurethane (COPUs-MWCNTs) nanocomposites. The composition, structure, and morphology of polyurethanes were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), field emission scanning electron microscopy (FESEM), and element detection by energy dispersive spectroscopy (EDX) analysis, respectively. Thermal stability was studied by thermogravimetric analysis (TGA). Barrier properties and surface area studies were investigated by nitrogen permeability machine and BET technique. Mechanical properties were calculated by tensile universal testing machine. Results showed well dispersed MWCNTs in polyurethane matrix at different weight percentages. The best results were obtained with 0.3 wt% of MWCNTs in the composite. Surface area studies revealed presence of very few pores which is in a good agreement with barrier permeability, reduced up to ~68% in 1 wt% and ~70% in 0.5 wt% of MWCNTs in polymer matrix, with respect to pure COPUs samples.


---

## Body

## 1. Introduction

Polyurethanes are versatile polymeric materials with extensive demand due to exceptional physical properties (e.g., high flexibility, high tensile strength, tear and abrasion resistance, solvent resistance, etc.) and high versatility in chemical structures (discussed by Lu and Macosko [1]; reported by Cao et al. [2]; studied by Oprea [3]; discussed by Akintayo et al. [4]). Footwear, machine industry, coatings and paints, rigid insulations, thermoplastic, foams, and medical devices (discussed by Yusoh et al. [5]; reported by Krushna and Nayak [6]; and discussed by Bhuva Bharat [7]) are some important industrial applications. Polyurethanes are generally synthesized by the polyols derived from the petrochemical industry (reported by Kong et al. [8]; discussed by Lligadas et al. [9]; and studied by [10]). The synthesis involves a poly addition polymerization reaction between organic isocyanate and polyol.Due to large consumption of PUs, a huge demand of utilization of renewable resources is always a critical job for researchers, to overcome environmental and price controlling issues related with a petroleum industry (discussed by Fan et al. [11]; reported by Spontón et al. [12]). Chang and Lu [13] depicted novel polyols made from modified castor oil (MCO) that was synthesized using a transesterification process with the glycerol competing with the petroleum polyols to overcome the environmental concerns and rising prices of the mineral oil industry. The commercial utilization of biodegradable polymers has become an active research area during past decades due to potential advantages compared with synthetic petroleum polymers owing to their biodegradable properties (discussed by Xu et al. [14]; studied by Baruah [15]). Yuan [16], in his thesis, presented polyol derived from soybean oil; however, this has some major disadvantages that limited its applications. Polyurethane based on polyols derived from different vegetable oils, like castor (discussed by Yeganeh and Hojati-Talemi [17]; studied by Corcuera et al. [18]), soybean (reported by Ismail et al. [19]; discussed by Yang et al. [20]; studied by Bakhshi et al. [21]), sunflower (discussed by Das et al. [22]), and rapeseed oils (studied by Rojek and Prociak et al. [23]; discussed by Fridrihsone et al. [24]; reported by More et al. [25]) with or without modifications, were being used these days due to their excellent properties derived from the hydrophobic nature of triglycerides.Castor oil possesses a reactive hydroxyl (−OH) functional group contained in its structure that can be used as a polyol and so it is widely used in many chemical industries, especially in the production of polyurethanes by reacting with different diisocyanates, with large availability, nonedibility, renewability, high purity, biodegradability, and low cost (reported by Spontón [12]; discussed by Carme Coll Ferrer et al. [26]). Ivan et al. [27] investigated the properties of environmentally friendly castor oil, based on polyurethane (COPU) hybrid materials with titanium (IV) oxide nanoparticles, as filler, and different types of diisocyanate (toluene diisocyanate and isophorone diisocyanate). Dos Santos et al. [28] presented the preparation and diagnosis of diisocyanate groups from castor oil. Their results exhibited that increasing polyol amount leads to an increase in the strength at rupture of the obtained polymers and a decrease in the polymers elongation, which results into increased modulus. Yeganeh and Hojati-Talemi [17] studied the synthesis of polyurethane networks based on castor oil as a renewable resource of polyol and poly(ethylene glycol) (PEG) through the reaction of epoxy-terminated polyurethane prepolymer (EPUs) with 1,6-hexamethylene diamine, for biomedical majoring. The results found that mechanical properties of the composites were improved by increasing EPUs content, as a result of which surface and bulk properties increase which also increased the hydrolytic degradation rate consequently.Carbon nanotubes (CNTs) represent the ideal, most perfect, and ordered carbon fiber, the structure of which is entirely known at the atomic level and distinctly different from the structure of traditional carbon fibers (discussed by Endo et al. [29]) resulting in the unique properties such as superconductivity, light weight, high stiffness, and axial strength (reported by Kurahatti et al. [30]; discussed by Luo et al. [31]). CNTs, because of their high mechanical strength, are being considered as nanoscale fibers to enhance the performance of polymer nanocomposite materials (studied by Yadav and Cho [32]). Madkour et al. [33] studied the synthesis of thermoplastic polyurethane (TPU), reinforced with multiwalled carbon nanotubes with better thermal stability and improved mechanical performance of thermoplastic polyurethane (TPU). Yadav and Cho [32] illustrated mechanically robust antimicrobial nanocomposites of multiwalled carbon nanotubes nanofillers and hyperbranched polyurethane (HBPU). Yun et al. [34] investigated PU grafted multiwalled carbon nanotubes (PU-g-MWCNTs) to fabricate electroconducting nanocomposites. All of these studies were based on petroleum originated polyols; no study has been reported so far on green and renewable sources of polyols.In this study, the COPUs-MWCNTs polymer nanocomposite has been designed based on green and renewable castor oil as a polyol source, reinforced with purified MWCNTs to investigate the physicochemical behaviour of the synthesized polymer composites. In situ polymerization technique assisted by ultrasonication was adopted with different dispersion times of MWCNTs in the composite matrix to accomplish enhanced dispersion in the reacting mixture.


## 2. Experimental

### 2.1. Materials

MWCNTs used in this study have the following specifications: purity >90%; outer diameter, 30–50 nm; inner diameter 5–10 nm; and length 10–20μm. They were obtained from Chengdu organic chemicals, China. Castor oil was of commercial grade and was purchased from the local market. It was dehydrated at 80°C in a vacuum oven and characterized for hydroxyl value (148), acid value (2), and moisture content (0.379%). Polypropylene glycol (PPG) (Mn = 4000) was supplied by SIGMA-Aldrich Company. Chain extender, 1,4-butanediol, was procured from Himedia, India. The toluene diisocyanate (TDI) and dimethylformamide (DMF) which were used as received were supplied from SIGMA-Aldrich Company.


### 2.2. Purification of MWCNTs

Initially, as provided, MWCNTs were preheated at ~450°C for 30 minutes to remove amorphous carbon (discussed by Manivannan et al. [35]). The MWCNTs were purified via stirring using an acid treatment (50 mL of 95% H2SO4 and 20 mL of 65% HNO3), with a ratio of (3 : 1), at 80°C for 5 hours, and this was followed by filtration (studied by Yun et al. [34]; discussed by Jana et al. [36]; reported by Yudianti et al. [37]). The collected solid was washed out with distilled water till pH neutralized (~7 pH). The filtered solid was then washed with 25 mL of acetone to remove most of the water from the sample and dried at 80°C for 20 hours. The purity of the MWCNTs was confirmed by FTIR spectroscopy.


### 2.3. Synthesis of MWCNTs-Polyurethane (COPUs-MWCNTs) Nanocomposites

Purified MWCNTs reinforced polyurethane nanocomposites were fabricated via in situ polymerization. The synthesis process involved two stages; the initial dispersion is followed by mixing of raw materials as follows. Firstly, different weight percent of the functionalized MWCNTs (0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt%) was dispersed by blending the MWCNTs in a mixture of polypropylene glycol polyol and dehydrated castor oil (15%) at 80°C, followed by ultrasonic bath for up to three hours at 50°C.In the second stage, the mixture was dissolved with 6.5 gm of toluene diisocyanate (TDI) drop-by-drop and vacuum degassed for 3–5 minutes at 85°C to achieve homogenous reaction and to prevent the bubbles formation. Prepolymer obtained was lastly reacted with 0.9 gm of 1,4-butanediol in the presence of 0.25 gm catalyst (DABCO) at 85°C for two minutes; then 50 mL of dimethylformamide (DMF) was added gradually and the temperature was reduced to 70°C. The mixture was continuously stirred until solution reduced up to 40% and became viscous; it was then poured into a mould to obtain a thin film and then cured in an oven at 65°C under vacuum for 24 hours. Obtained film was later postcured for a week at 80°C.


## 2.1. Materials

MWCNTs used in this study have the following specifications: purity >90%; outer diameter, 30–50 nm; inner diameter 5–10 nm; and length 10–20μm. They were obtained from Chengdu organic chemicals, China. Castor oil was of commercial grade and was purchased from the local market. It was dehydrated at 80°C in a vacuum oven and characterized for hydroxyl value (148), acid value (2), and moisture content (0.379%). Polypropylene glycol (PPG) (Mn = 4000) was supplied by SIGMA-Aldrich Company. Chain extender, 1,4-butanediol, was procured from Himedia, India. The toluene diisocyanate (TDI) and dimethylformamide (DMF) which were used as received were supplied from SIGMA-Aldrich Company.


## 2.2. Purification of MWCNTs

Initially, as provided, MWCNTs were preheated at ~450°C for 30 minutes to remove amorphous carbon (discussed by Manivannan et al. [35]). The MWCNTs were purified via stirring using an acid treatment (50 mL of 95% H2SO4 and 20 mL of 65% HNO3), with a ratio of (3 : 1), at 80°C for 5 hours, and this was followed by filtration (studied by Yun et al. [34]; discussed by Jana et al. [36]; reported by Yudianti et al. [37]). The collected solid was washed out with distilled water till pH neutralized (~7 pH). The filtered solid was then washed with 25 mL of acetone to remove most of the water from the sample and dried at 80°C for 20 hours. The purity of the MWCNTs was confirmed by FTIR spectroscopy.


## 2.3. Synthesis of MWCNTs-Polyurethane (COPUs-MWCNTs) Nanocomposites

Purified MWCNTs reinforced polyurethane nanocomposites were fabricated via in situ polymerization. The synthesis process involved two stages; the initial dispersion is followed by mixing of raw materials as follows. Firstly, different weight percent of the functionalized MWCNTs (0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt%) was dispersed by blending the MWCNTs in a mixture of polypropylene glycol polyol and dehydrated castor oil (15%) at 80°C, followed by ultrasonic bath for up to three hours at 50°C.In the second stage, the mixture was dissolved with 6.5 gm of toluene diisocyanate (TDI) drop-by-drop and vacuum degassed for 3–5 minutes at 85°C to achieve homogenous reaction and to prevent the bubbles formation. Prepolymer obtained was lastly reacted with 0.9 gm of 1,4-butanediol in the presence of 0.25 gm catalyst (DABCO) at 85°C for two minutes; then 50 mL of dimethylformamide (DMF) was added gradually and the temperature was reduced to 70°C. The mixture was continuously stirred until solution reduced up to 40% and became viscous; it was then poured into a mould to obtain a thin film and then cured in an oven at 65°C under vacuum for 24 hours. Obtained film was later postcured for a week at 80°C.


## 3. Characterization

The crystal structure of the COPUs-MWCNTs nanocomposites was analysed by X-ray diffraction (XRD), using an X-ray diffractometer (Rigaku Miniflex II, Japan) employing a graphite monochromator and CuKα radiation (l nm). Fourier transform infrared spectroscopy (FTIR) analysis of COPUs-MWCNTs nanocomposites was done using a FTIR spectrometer (Nicolet 5DX FT-IR, USA). The morphology of the hybrids was examined by field emission scanning electron microscopy (FE-SEM; JEOL EVO-50, Japan) and scanning electron microscopy (SEM; JEOL 6300F, Japan). Element detection EDX was performed with the attached equipment in FESEM spectroscopy. Thermal stability of polyurethane nanocomposites was determined using a thermogravimetric analyzer (TGA) type Universal V4.5A, TA instruments were under nitrogen atmosphere. Tensile testing was carried out on an Instron model 4505 universal testing machine at 25°C, with a load cell of 5 KN and following ASTM D 638. The crosshead speed was set to 2 mm/min. Samples were cut in a dumbbell shape with an ASTM D 638 (type V). Surface area properties were studied by BET Micromeritics surface area analyzer and gas permeability test was done by nitrogen permeable machine setup.


## 4. Results and Discussion

### 4.1. Structure and Morphology of PU Nanocomposites

FTIR spectrum indicates a peak at ranges from 1715 to 1725 cm−1, which refers to carbonyl hydrogen bonding present in nanocomposites, with different intensities (discussed by Jana et al. [36]); the COPUs peak is much sharper and intense while in the case of both of the COPU nanocomposites the peak became broad with lower intensity, predicting a reduction in carbonyl hydrogen bonding due to purified MWCNTs intercalation in COPU matrix. From Figure 1, one characteristic peak of MWCNTs and two characteristic peaks of COPUs were observed at near 3500 cm−1 (reported by Yudianti et al. [37]), 3340 cm−1 (discussed by Yadav et al. [38]), and 1718 cm−1 (reported by Gu et al. [39]) due to the stretching vibration of -
OH, -
NH, and −C=O groups in purified MWCNTs and COPUs, respectively. It was clearly seen that the OH peak intensity at 3500 cm−1, which shows the strongest peak in the MWCNTs, vanishes with the addition of MWCNTs in polymer; Sahoo et al. [40] signified that MWCNTs were successfully covalently encapsulated by two layers of polymer. In this study, the MWCNTs used in the composite preparation were an acid-treated carbon nanotube which contains carboxylic acid groups. The carboxylic acid groups may have reacted with OH groups of the polymer to form ester groups (discussed by Wang et al. [41]).Figure 1
FT-IR spectra of pure COPUs and COPUs-MWCNTs nanocomposites, with virgin 0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt% MWCNTs loadings.Figure2 depicts the diffraction peaks of the pure COPUs and the COPUs-MWCNTs nanocomposites at 2
θ
=
20.2°, 20.1°, and 20° of the reflection plane with interchain (d) spacing of 4.445, 4.451, and 4.501 A°, respectively, which is related to the existence of short range regular ordered structure of both the hard and the soft domains along with disordered structure of amorphous phase of the polyurethane matrix. Peaks become broadened with reduced intensity, with the addition of MWCNTs, which inferred that the MWCNTs considerably affect the well short-range microstructural phases of both soft and hard segments of the COPUs matrix (reported by Aruna and Deba [42]; discussed by Kuan et al. [43]). This may be due to the presence of strong interfacial interactions between MWCNTs and COPUs matrix. In addition, the individual or bundled nanotubes also influence the resulting steric hindrance effect of the soft and the hard phases of COPUs matrix (discussed by Jana et al. [36]). Peak assigned to the (100) plane of the MWCNTs was found at 2θ value ~40° (100) Bragg reflection planes. The peaks are attributed to the ordered regular arrangement of the concentric cylinders of the graphitic carbon atoms in nanotubes (studied by Zhou et al. [44]).Figure 2
Powder X-ray diffraction patterns of pure COPUs and COPUs-MWCNTs nanocomposites, with virgin 0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt% MWCNTs loadings.Surface morphology of the pure COPUs and MWCNTs reinforced COPUs nanocomposites at ×50,000 and ×200,000 magnifications is shown in Figure3 and is studied by FESEM microscopy. The bright dots and tread-like structures in the images are attributed to the MWCNTs. The dispersion of MWCNTs in the COPUs matrix at lower loading (0.3 wt%) as shown in Figure 3(b), is found to be homogeneously dispersed throughout the COPUs matrix without any agglomeration. But agglomeration is seen at higher (0.5 and1 wt%) loadings depicted in Figures 3(c) and 3(d), respectively. In 0.3 wt% MWCNTs loading micrographs, well-dispersed nanotubes throughout the entire surface could be attributed to the induced Van der Waals force between polymer and MWCNTs, which exceeds the existing intertube forces during sonication (discussed by Ma et al. [45]).FESEM images of fractured surface of (a) 0% MWCNTs, (b) 0.3% MWCNTs, (c) 0.5% MWCNTs, and (d) 1% MWCNTs in COPUs matrix.
(a)
(b)
(c)
(d)The result is in good agreement with the thermogravimetric (TGA) results, where 0.3 wt% MWCNTs showed higher stability than other percentages. In micrographs (0.5 and 1 wt%), high agglomeration of MWCNTs is seen, which may be due to self-aggregation of MWCNTs by Van der Waals bonding and also due to lack of interfacial adhesion between MWCNTs and COPUs matrix (reported by Aruna and Deba [42]; investigated by Nayak et al. [46]).Figure4 shows SEM images of the fractured surfaces of pure and COPUs-MWCNTs nanocomposites in different weight percentages. The homogeneous dispersion of MWCNTs in the polymer matrix is one of the conditions needed for a composite to display good mechanical strength reinforcement because inhomogeneities can lead to structural defects in the composite material (investigated by Yoo et al. [47]). The bright dots and thread-like structures in the images are attributed to the MWCNTs in composite Figures 4(a), 4(b), 4(c), 4(d), 4(e), and 4(f), where some microaggregates inside the film are present which might be the result of DMF evaporation which decreases the total solubility of solution and increases the difference of the solubility of the solution and the nanotubes (discussed by Wongtimnoi et al. [48]).SEM images of pure COPUs and COPUs-MWNTs composites: (a) COPUs, (b) COPUs-MWNTs 0.1%, (c) COPUs-MWNTs 0.2%, (d) COPUs-MWNTs 0.3%, (e) COPUs-MWNTs 0.4%, and (f) COPUs-MWNTs 0.5%.
(a)
(b)
(c)
(d)
(e)
(f)The dispersion of MWCNTs in the COPUs matrix up to 0.3 wt% MWCNTs, as shown in Figure4(d), is found to be homogeneously dispersed throughout the COPUs matrix with no or very little agglomeration, which is quiet prominent at higher (0.4, and 0.5 wt%) loadings as depicted in Figures 4(e) and 4(f), respectively. In 0.3 wt% MWCNTs loading micrographs, well-dispersed nanotubes throughout the entire surface could be attributed to the induced Van der Waals force between polymer matrix and MWCNTs, which surpasses the standing intertube forces during sonication (discussed by Ma et al. [45]). The better dispersion of the MWCNTs results in more effective transfer of load imposed on the COPUs-MWCNTs nanocomposite and higher effective filling volume, which can be contributed more likely to the improvement of mechanical properties (reported by Gu et al. [39]).


### 4.2. Element Detection Analysis

The purity and elemental composition of the synthesized polyurethane-MWCNTs nanocomposites were confirmed by the EDX measurement as shown in Figure5. EDX analysis confirms that only Oxygen (O), Carbon (C), and Nitrogen (N) elements are present in the nanocomposites, which is in good agreement with the stoichiometric composition of polyurethane-MWCNTs nanocomposites. O, C, and N are the main elements of polyurethane-MWCNTs nanocomposites and carbon peak belongs to both of COPUs and MWCNT. The EDX elemental microanalysis (mass percentage) of nanohybrid is listed in Table 1.Table 1
EDX studies of different weight% of MWCNTs in COPU matrix with elemental weight and atomic percentages.
MWCNTs wt%
Element
Weight percentage
Atomic percentage
0.5
C
59.85
65.73
N
9.85
9.28
O
30.3
24.99
0.3
C
59.80
65.25
N
9.84
9.3
O
30.9
24.45
0.1
C
59.78
65.05
N
9.82
9.35
O
30.4
25.6Figure 5
EDX analysis of COPUs-MWCNTs nanocomposites.


### 4.3. Thermogravimetric Analysis (TGA)

Thermogravimetric behavior is a good evidence of the interactions within the COPUs-MWCNTs nanocomposites. In this study thermogravimetric stability was calculated on different percentages of MWCNTs (0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt%) as shown in Figure6 within the COPU matrix, which was previously compared with the neat polyurethane. The samples are heated from room temperature to 550°C at a rate of 10°C/min under inert atmosphere. The temperature of pure polyurethane is ~341.2°C (discussed by Kuan et al. [43]). The better result is obtained with 0.3 wt% of MWCNTs in the COPU matrix. In the COPUs-MWCNTs nanocomposites, decomposition temperature of polyurethane part is observed at ~410°C with a weight loss of ~89%. The decomposition temperature is increased up to ~50°C with the addition of MWCNTs, which may be ascribed to the combined effect of excellent thermal stability of MWCNTs and their strong interfacial interactions within the layers of polymer matrix (investigated by Guo et al. [49]). This also provides the quantitative evidence of 11% in weight of MWCNTs present in the sample of polymer matrix.Figure 6
TGA spectrum of pure COPUs and COPUs-MWCNTs nanocomposite with varying MWCNTs wt%.


### 4.4. Mechanical Properties of PU Nanocomposites Film

A comparative stress-strain study of pure COPUs and COPUs-MWCNTs nanocomposites with 0.3 wt% MWCNTs depicts an improvement of ~5% in tensile strength and ~128% in modulus in COPUs-MWCNTs nanocomposites as shown in Figures7 and 8. The dispersion of MWCNTs into the COPUs matrix increases the resistance of the polymer to deformation. This is due to well-dispersed and polymer-filler interaction in the nanocomposites (discussed by Jana et al. [36]). The main reason for this improvement can be ascribed to COPUs-MWCNTs hitching and hydrogen bonding between MWCNTs particles and the polymer (reported by Krushna and Nayak [6]). It may be also because of carboxylic groups located onto the MWCNTs surface which form covalent bonds with the COPUs resulting in significantly enhanced interfacial adhesion (investigated by Sahoo et al. [50]).Figure 7
Stress-strain curves of pure COPUs and COPU-MWCNTs 0.3 wt% composites.Figure 8
Tensile strength of COPUs and COPUs-MWCNTs nanocomposites with pure and 0.3 wt% MWCNTs.


### 4.5. Gas-Barrier Properties

The inclusion of MWCNTs into the COPUs matrix has a huge impact on the gas diffusion mechanism due to different permeability properties of the matrix and the MWCNTs nanofiller (discussed by Maji et al. [51]). A reduction in permeability of nitrogen is observed with an increase in MWCNTs concentration (Figure 9). Samples up to 0.5 wt% of MWCNTs show permeability reduction, which is ~70% over the pure COPU, but beyond that, the decrease is insignificant (for 1 wt% loading, the reduction is ~68%). The increase in gas barrier property for polymer-MWCNTs nanocomposite may be due to the exfoliation, compatibilization, orientation, and reaggregation of purified MWCNTs in to the polymer matrix, as shown in Figure 10 (studied by Joshi et al. [52]).Figure 9
Nitrogen permeability rate in different MWCNTs weight percentages.Figure 10
Schematic model describing the path of the diffusing N2 gas through the COPU-MWCNTs nanocomposite. (d) is the actual distance travelled in the absence of fillers and (d
′) is tortuous path length in the presence of fillers.


### 4.6. BET Surface Analysis

BET surface area analysis is investigated on 0.5 wt% COPUs-MWCNTs (Figure11) nanocomposites by nitrogen adsorption/desorption isotherms measured at 77 K and data are treated according to the Brunauer-Emmett-Teller (BET) theory investigated by Brunauer et al. [53]. The surface area is determined by a multipoint BET method using the adsorption data in the relative pressure (P/P
0) range of 0.05–0.3. The BET surface area, obtained for sample, is 0.3845 m2 g−1. This value is considerably low, which is in a good agreement with the barrier properties indicating presence of very low or no pores in the surface resulting in low permeability that may be due to the exfoliation, compatibilization, orientation, and reaggregation of purified MWCNTs in to the polymer matrix.Figure 11
Nitrogen adsorption-desorption isotherms of 0.5 wt% COPU-MWCNTs.


## 4.1. Structure and Morphology of PU Nanocomposites

FTIR spectrum indicates a peak at ranges from 1715 to 1725 cm−1, which refers to carbonyl hydrogen bonding present in nanocomposites, with different intensities (discussed by Jana et al. [36]); the COPUs peak is much sharper and intense while in the case of both of the COPU nanocomposites the peak became broad with lower intensity, predicting a reduction in carbonyl hydrogen bonding due to purified MWCNTs intercalation in COPU matrix. From Figure 1, one characteristic peak of MWCNTs and two characteristic peaks of COPUs were observed at near 3500 cm−1 (reported by Yudianti et al. [37]), 3340 cm−1 (discussed by Yadav et al. [38]), and 1718 cm−1 (reported by Gu et al. [39]) due to the stretching vibration of -
OH, -
NH, and −C=O groups in purified MWCNTs and COPUs, respectively. It was clearly seen that the OH peak intensity at 3500 cm−1, which shows the strongest peak in the MWCNTs, vanishes with the addition of MWCNTs in polymer; Sahoo et al. [40] signified that MWCNTs were successfully covalently encapsulated by two layers of polymer. In this study, the MWCNTs used in the composite preparation were an acid-treated carbon nanotube which contains carboxylic acid groups. The carboxylic acid groups may have reacted with OH groups of the polymer to form ester groups (discussed by Wang et al. [41]).Figure 1
FT-IR spectra of pure COPUs and COPUs-MWCNTs nanocomposites, with virgin 0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt% MWCNTs loadings.Figure2 depicts the diffraction peaks of the pure COPUs and the COPUs-MWCNTs nanocomposites at 2
θ
=
20.2°, 20.1°, and 20° of the reflection plane with interchain (d) spacing of 4.445, 4.451, and 4.501 A°, respectively, which is related to the existence of short range regular ordered structure of both the hard and the soft domains along with disordered structure of amorphous phase of the polyurethane matrix. Peaks become broadened with reduced intensity, with the addition of MWCNTs, which inferred that the MWCNTs considerably affect the well short-range microstructural phases of both soft and hard segments of the COPUs matrix (reported by Aruna and Deba [42]; discussed by Kuan et al. [43]). This may be due to the presence of strong interfacial interactions between MWCNTs and COPUs matrix. In addition, the individual or bundled nanotubes also influence the resulting steric hindrance effect of the soft and the hard phases of COPUs matrix (discussed by Jana et al. [36]). Peak assigned to the (100) plane of the MWCNTs was found at 2θ value ~40° (100) Bragg reflection planes. The peaks are attributed to the ordered regular arrangement of the concentric cylinders of the graphitic carbon atoms in nanotubes (studied by Zhou et al. [44]).Figure 2
Powder X-ray diffraction patterns of pure COPUs and COPUs-MWCNTs nanocomposites, with virgin 0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt% MWCNTs loadings.Surface morphology of the pure COPUs and MWCNTs reinforced COPUs nanocomposites at ×50,000 and ×200,000 magnifications is shown in Figure3 and is studied by FESEM microscopy. The bright dots and tread-like structures in the images are attributed to the MWCNTs. The dispersion of MWCNTs in the COPUs matrix at lower loading (0.3 wt%) as shown in Figure 3(b), is found to be homogeneously dispersed throughout the COPUs matrix without any agglomeration. But agglomeration is seen at higher (0.5 and1 wt%) loadings depicted in Figures 3(c) and 3(d), respectively. In 0.3 wt% MWCNTs loading micrographs, well-dispersed nanotubes throughout the entire surface could be attributed to the induced Van der Waals force between polymer and MWCNTs, which exceeds the existing intertube forces during sonication (discussed by Ma et al. [45]).FESEM images of fractured surface of (a) 0% MWCNTs, (b) 0.3% MWCNTs, (c) 0.5% MWCNTs, and (d) 1% MWCNTs in COPUs matrix.
(a)
(b)
(c)
(d)The result is in good agreement with the thermogravimetric (TGA) results, where 0.3 wt% MWCNTs showed higher stability than other percentages. In micrographs (0.5 and 1 wt%), high agglomeration of MWCNTs is seen, which may be due to self-aggregation of MWCNTs by Van der Waals bonding and also due to lack of interfacial adhesion between MWCNTs and COPUs matrix (reported by Aruna and Deba [42]; investigated by Nayak et al. [46]).Figure4 shows SEM images of the fractured surfaces of pure and COPUs-MWCNTs nanocomposites in different weight percentages. The homogeneous dispersion of MWCNTs in the polymer matrix is one of the conditions needed for a composite to display good mechanical strength reinforcement because inhomogeneities can lead to structural defects in the composite material (investigated by Yoo et al. [47]). The bright dots and thread-like structures in the images are attributed to the MWCNTs in composite Figures 4(a), 4(b), 4(c), 4(d), 4(e), and 4(f), where some microaggregates inside the film are present which might be the result of DMF evaporation which decreases the total solubility of solution and increases the difference of the solubility of the solution and the nanotubes (discussed by Wongtimnoi et al. [48]).SEM images of pure COPUs and COPUs-MWNTs composites: (a) COPUs, (b) COPUs-MWNTs 0.1%, (c) COPUs-MWNTs 0.2%, (d) COPUs-MWNTs 0.3%, (e) COPUs-MWNTs 0.4%, and (f) COPUs-MWNTs 0.5%.
(a)
(b)
(c)
(d)
(e)
(f)The dispersion of MWCNTs in the COPUs matrix up to 0.3 wt% MWCNTs, as shown in Figure4(d), is found to be homogeneously dispersed throughout the COPUs matrix with no or very little agglomeration, which is quiet prominent at higher (0.4, and 0.5 wt%) loadings as depicted in Figures 4(e) and 4(f), respectively. In 0.3 wt% MWCNTs loading micrographs, well-dispersed nanotubes throughout the entire surface could be attributed to the induced Van der Waals force between polymer matrix and MWCNTs, which surpasses the standing intertube forces during sonication (discussed by Ma et al. [45]). The better dispersion of the MWCNTs results in more effective transfer of load imposed on the COPUs-MWCNTs nanocomposite and higher effective filling volume, which can be contributed more likely to the improvement of mechanical properties (reported by Gu et al. [39]).


## 4.2. Element Detection Analysis

The purity and elemental composition of the synthesized polyurethane-MWCNTs nanocomposites were confirmed by the EDX measurement as shown in Figure5. EDX analysis confirms that only Oxygen (O), Carbon (C), and Nitrogen (N) elements are present in the nanocomposites, which is in good agreement with the stoichiometric composition of polyurethane-MWCNTs nanocomposites. O, C, and N are the main elements of polyurethane-MWCNTs nanocomposites and carbon peak belongs to both of COPUs and MWCNT. The EDX elemental microanalysis (mass percentage) of nanohybrid is listed in Table 1.Table 1
EDX studies of different weight% of MWCNTs in COPU matrix with elemental weight and atomic percentages.
MWCNTs wt%
Element
Weight percentage
Atomic percentage
0.5
C
59.85
65.73
N
9.85
9.28
O
30.3
24.99
0.3
C
59.80
65.25
N
9.84
9.3
O
30.9
24.45
0.1
C
59.78
65.05
N
9.82
9.35
O
30.4
25.6Figure 5
EDX analysis of COPUs-MWCNTs nanocomposites.


## 4.3. Thermogravimetric Analysis (TGA)

Thermogravimetric behavior is a good evidence of the interactions within the COPUs-MWCNTs nanocomposites. In this study thermogravimetric stability was calculated on different percentages of MWCNTs (0.1, 0.2, 0.3, 0.4, 0.5, and 1 wt%) as shown in Figure6 within the COPU matrix, which was previously compared with the neat polyurethane. The samples are heated from room temperature to 550°C at a rate of 10°C/min under inert atmosphere. The temperature of pure polyurethane is ~341.2°C (discussed by Kuan et al. [43]). The better result is obtained with 0.3 wt% of MWCNTs in the COPU matrix. In the COPUs-MWCNTs nanocomposites, decomposition temperature of polyurethane part is observed at ~410°C with a weight loss of ~89%. The decomposition temperature is increased up to ~50°C with the addition of MWCNTs, which may be ascribed to the combined effect of excellent thermal stability of MWCNTs and their strong interfacial interactions within the layers of polymer matrix (investigated by Guo et al. [49]). This also provides the quantitative evidence of 11% in weight of MWCNTs present in the sample of polymer matrix.Figure 6
TGA spectrum of pure COPUs and COPUs-MWCNTs nanocomposite with varying MWCNTs wt%.


## 4.4. Mechanical Properties of PU Nanocomposites Film

A comparative stress-strain study of pure COPUs and COPUs-MWCNTs nanocomposites with 0.3 wt% MWCNTs depicts an improvement of ~5% in tensile strength and ~128% in modulus in COPUs-MWCNTs nanocomposites as shown in Figures7 and 8. The dispersion of MWCNTs into the COPUs matrix increases the resistance of the polymer to deformation. This is due to well-dispersed and polymer-filler interaction in the nanocomposites (discussed by Jana et al. [36]). The main reason for this improvement can be ascribed to COPUs-MWCNTs hitching and hydrogen bonding between MWCNTs particles and the polymer (reported by Krushna and Nayak [6]). It may be also because of carboxylic groups located onto the MWCNTs surface which form covalent bonds with the COPUs resulting in significantly enhanced interfacial adhesion (investigated by Sahoo et al. [50]).Figure 7
Stress-strain curves of pure COPUs and COPU-MWCNTs 0.3 wt% composites.Figure 8
Tensile strength of COPUs and COPUs-MWCNTs nanocomposites with pure and 0.3 wt% MWCNTs.


## 4.5. Gas-Barrier Properties

The inclusion of MWCNTs into the COPUs matrix has a huge impact on the gas diffusion mechanism due to different permeability properties of the matrix and the MWCNTs nanofiller (discussed by Maji et al. [51]). A reduction in permeability of nitrogen is observed with an increase in MWCNTs concentration (Figure 9). Samples up to 0.5 wt% of MWCNTs show permeability reduction, which is ~70% over the pure COPU, but beyond that, the decrease is insignificant (for 1 wt% loading, the reduction is ~68%). The increase in gas barrier property for polymer-MWCNTs nanocomposite may be due to the exfoliation, compatibilization, orientation, and reaggregation of purified MWCNTs in to the polymer matrix, as shown in Figure 10 (studied by Joshi et al. [52]).Figure 9
Nitrogen permeability rate in different MWCNTs weight percentages.Figure 10
Schematic model describing the path of the diffusing N2 gas through the COPU-MWCNTs nanocomposite. (d) is the actual distance travelled in the absence of fillers and (d
′) is tortuous path length in the presence of fillers.


## 4.6. BET Surface Analysis

BET surface area analysis is investigated on 0.5 wt% COPUs-MWCNTs (Figure11) nanocomposites by nitrogen adsorption/desorption isotherms measured at 77 K and data are treated according to the Brunauer-Emmett-Teller (BET) theory investigated by Brunauer et al. [53]. The surface area is determined by a multipoint BET method using the adsorption data in the relative pressure (P/P
0) range of 0.05–0.3. The BET surface area, obtained for sample, is 0.3845 m2 g−1. This value is considerably low, which is in a good agreement with the barrier properties indicating presence of very low or no pores in the surface resulting in low permeability that may be due to the exfoliation, compatibilization, orientation, and reaggregation of purified MWCNTs in to the polymer matrix.Figure 11
Nitrogen adsorption-desorption isotherms of 0.5 wt% COPU-MWCNTs.


## 5. Conclusions

In the conclusion, castor oil based polyurethanes nanocomposites (COPUs-MWCNTs) are synthesized with different weight percentages of MWCNTs. The thermal and mechanical properties of the COPUs matrix are significantly enhanced by the incorporation of MWNTs. FTIR, of the nanocomposites, shows broad peaks with higher intensity, with the increase in MWCNTs weight percentage in the polymer. It indicates a good physical entanglement between the constituents. XRD results revealed broad peaks with lower intensity in relation with pure COPUs, which inferred that the MWCNTs considerably affect the well short-range microstructural phases of both the soft and the hard segments of the COPUs matrix, resulting in strong interfacial interactions between MWCNTs and COPUs matrix. FESEM showed well dispersed MWCNTs in the COPUs matrix up to 0.3 wt%, but agglomeration is seen at higher (0.5 and 1 wt%) loadings. Thermogravimetric analysis depicts that the 0.3 wt% of MWCNTs in the polymer has best thermal stability in relation with other percentages and neat polyurethane, which is in total agreement with FESEM results. SEM monographs displayed good dispersion up to 0.3 wt% loaded MWCNTs in the polymer matrix, which is in good relation with FESEM and TGA results. EDX analysis showed presence of only carbon, nitrogen, and oxygen in different weight and atomic percentages. The barrier properties show improvement with increasing MWCNTs in the polymer matrix up to 5%, which was found compatible with low surface area calculated by BET surface analysis.



---