# Influence of Deposition Rate on the Thermoelectric Properties of Sb2Te3 Thin Films by Thermal Evaporation Method

Authors: Jyun-Min Lin; Ying-Chung Chen; Wei Chen
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Thermoelectric (TE) materials are crucial because they can be used in power generation and cooling devices. Sb2Te3-based compounds are the most favorable TE materials because of their excellent figure of merit at room temperature. In this study, Sb2Te3 thin films were prepared on SiO2/Si substrates through thermal evaporation. The influence of the evaporation current on the microstructures and TE properties of Sb2Te3 thin films were investigated. The crystalline structures and morphologies of the thin films were analyzed using X-ray diffraction and field emission scanning electron microscopy. The Seebeck coefficient, electrical conductivity, and power factor (PF) were measured at room temperature. The experimental results showed that the Seebeck coefficient increased and conductivity decreased with increasing evaporation current. The Seebeck coefficient reached a maximum of 387.58 μV/K at an evaporation current of 80 A. Conversely, a PF of 3.57 µW/cmK2 was obtained at room temperature with evaporation current of 60 A.


---

## Body

## 1. Introduction

As energy shortage and carbon reduction are becoming more crucial challenges, green technology is attracting increasing attention. Thermoelectric (TE) materials are advantageous because of their environmentally friendly and renewable nature. TE characteristics facilitate the conversion of thermal energy and electrical energy, which can directly convert thermal energy to electrical energy through the Seebeck effect and electrical energy to thermal energy through the Peltier effect without entailing mechanical moving parts. TE materials have several high-profile applications in such fields as space flight, military, and medicine [1]. The performance of TE materials depends on their Seebeck coefficient, electrical conductivity, and thermal conductivity. The energy conversion efficiency of TE materials is evaluated using the figure of merit ZT: ZT=(S2σ/κ)T, where S is the Seebeck coefficient (V/K), σ is the electrical conductivity, T is the absolute temperature, κ is the thermal conductivity [1, 2], and S2σ is the power factor (PF). Therefore, an excellent ZT can be obtained by increasing the Seebeck coefficient and electrical conductivity and reducing thermal conductivity. Bismuth telluride- (Bi–Te-) and antimony telluride- (Sb–Te-) based compounds are currently the state-of-the-art TE materials for operations at near room temperature. Furthermore, Bi–Te- and Sb–Te-based TE materials exhibit the highest ZT and are widely used in commercial TE generators and coolers [3]. Generally, commercial TE devices are manufactured from sintered bulks of these materials. However, bulk materials possess low ZT. To increase ZT, low-dimensional materials are used to improve the TE properties because they increase the density of Fermi-level states and enhance phonon scattering [4] on nanostructured materials. In addition, miniaturizing TE devices using a bulk sample is difficult. Therefore, to miniaturize the device and effectively improve TE properties, several techniques have been reported for growing thin films, such as flash evaporation [5], ion-beam sputtering [6, 7], pulse laser deposition [8, 9], sputtering [10–12], electrochemical deposition [13–15], metal-organic chemical vapor deposition [16, 17], and molecular beam epitaxy [18–20]. However, some processes require long duration and expensive facilities. Therefore, in this study, Sb2Te3-based thin films were fabricated through thermal evaporation, which offers such advantages as low fabricating expenses and short processing time. In addition, we evaluated the effects of the thermal evaporation rate on the TE properties of evaporated thin films on a SiO2/Si substrate.


## 2. Experimental

P-type (100) silicon wafers served as the TE thin film substrates. After the RCA cleaning process, a 400-nm SiO2 layer was thermally grown on a SiO2/Si substrate through atmospheric pressure chemical vapor deposition. The p-type Sb2Te3 thin films were then deposited through thermal evaporation. High-purity (99.99%) Sb2Te3 powder with a diameter of 1–10 mm was used as the evaporation source and evaporated from a tungsten boat. The weight of Sb2Te3 powders was fixed for each evaporation process. To evaluate the effects of the thermal evaporation rate on the TE properties of thin films, the thermal evaporation current was varied in the range 50–80 A. The thin films were prepared in an evacuated chamber with a working pressure of less than 3.75×10-5 Torr at room temperature. The thickness of the evaporated Sb2Te3 films was measured from the SEM cross-sectional photographs.The crystalline phases of TE thin films were examined using X-ray diffraction (XRD; Cu-Kα, Bruker D8). The Sb2Te3 thin films were revealed by scanning 2θ from 20° to 60° at the speed of 1 second for each step with an angular gap of 0.05 degree. The surface morphologies of the Sb2Te3 thin films were analyzed using field emission scanning electron microscopy (FE-SEM, JEOL JSM6700). To evaluate the TE properties, Seebeck coefficient (S) and electrical conductivity (σ) were measured at room temperature. The Seebeck coefficient was obtained by measuring the resulting Seebeck voltage as applying a temperature gradient across the sample, in which the data was acquired by a Keithley 2700 system. As measured temperature was changed in a small range, for example, approximately 5°C, the Seebeck coefficient of the device under test (DUT) could be considered as a fixed value. The Seebeck coefficient obtained in this study is averaged from the values of ten measurements. The electrical conductivity of the specimen was measured using a four-point probe method at room temperature with a Keithly 2400 source meter. Subsequently, PF (S2σ) was calculated using S and σ.


## 3. Results and Discussion

The thickness of the evaporated Sb2Te3 films under various evaporation currents was measured to be about 400 nm from the SEM cross-sectional photographs. The results also show that the deposition rate of thin films is approximately linearly increased with the increased evaporation current, as shown in Figure 1.Figure 1
The relationship between deposition rate and evaporation current for the deposition of Sb2Te3 thin films.The X-ray diffraction patterns of the Sb2Te3 alloy powder are presented in Figure 2. The peaks agree with the powder diffraction pattern for Sb2Te3 material (JCPDS #71-0393). All diffraction peaks of the Sb2Te3 powder coincided with those of JCPDS data, indicating the formation of a single phase Sb2Te3. For the Sb2Te3 powder, the diffraction angles at 28.24°, 38.29°, and 42.35° corresponded to the (0 1 5), (1 0 10), and (1 1 0) crystalline phases, respectively.Figure 2
XRD patterns of the Sb2Te3 powder.Figure3 shows the XRD patterns of the Sb2Te3 thin films deposited at various evaporation currents. The results show that the diffraction peaks corresponding to the (0 1 5), (1 0 10), and (1 1 0) crystalline phases were not obvious. Because these thin films were deposited on an unheated substrate, the atoms did not have sufficient energy to facilitate crystal growth at room temperature. Figure 4 presents the SEM images of the thin films deposited at various evaporation currents at room temperature. The as-deposited thin films had a continuous and smooth surface with a fine grain size and uniformly distributed structure.Figure 3
XRD patterns of Sb2Te3 thin films deposited on SiO2/Si substrates at various evaporation currents: (a) JCPDS, (b) 50 A, (c) 60 A, (d) 70 A, and (e) 80 A.Figure 4
FE-SEM top-viewed photographs of the Sb2Te3 thin films under various evaporation currents: (a) 50 A, (b) 60 A, (c) 70 A, and (d) 80 A.
(a)
(b)
(c)
(d)The effect of the evaporation current on the Seebeck coefficient is illustrated in Figure5. The Seebeck coefficient of the as-deposited thin films was positive, confirming that Sb2Te3 thin films are p-type semiconductors. The Seebeck coefficient increased with increasing evaporation current. The maximum value of 387.58 μV/K was obtained at 80 A. On the other hand, the effect of the evaporation current on electrical conductivity is shown in Figure 6. Electrical conductivity decreased with increasing evaporation current. The sample deposited at 50 A existed as maximum electrical conductivity of 592.70 S·cm−1. The trend of conductivity may be due to the fact that as the evaporation current increases, the structure of thin film becomes less dense, which results in increased resistivity and decreased conductivity. The trend of Seebeck coefficient is inverse with that of conductivity [21].Figure 5
Variations of Seebeck coefficient for Sb2Te3 thin films deposited at different evaporation current.Figure 6
Variations of electrical conductivity for Sb2Te3 thin films deposited at different evaporation current.Power factor, PF, is a crucial TE parameter and can be calculated from the Seebeck coefficient and electrical conductivity. Figure7 presents the PFs obtained for the Sb2Te3 films deposited at various evaporation currents. The highest PF of 3.57 μW/cmK2 was obtained at an evaporation current of 60 A. The TE properties of the Sb2Te3 thin films deposited at various evaporation currents are summarized in Table 1. The maximum Seebeck coefficient and PF of p-type Sb2Te3 thin films were approximately 387.58 μV/K and 3.59 μW/cmK2, respectively.Table 1
Thermoelectric properties of Sb2Te3 films deposited at different evaporation current.
Evaporation current (A)
50
60
70
80
Seebeck coefficient (μV/K)
28
129.3
242.4
387.58
Electrical conductivity (S⋅cm−1)
592.7
214.75
0.11
0.11
Power factor (μW/cmK2)
0.46
3.57
0.017
0.028Figure 7
Variations of power factor for Sb2Te3 thin films deposited at different evaporation current.


## 4. Conclusion

In this study, the thermal evaporation method was successfully utilized for the preparation of the Sb2Te3 thermoelectric thin films on SiO2/Si substrates with low cost. The effects of evaporation current on the thermoelectric properties and microstructures of the Sb2Te3 thin films have been investigated at the evaporation current of 50–80 A. The electrical conductivity decreased from 592.7 S/cm to 0.11 S/cm, whereas the Seebeck coefficient increased from 28 μV/K to 387.58 μV/K as the evaporation current varied from 50 A to 80 A. The optimized power factor of 3.57 μW/cm·K2 was obtained for Sb2Te3 thin film deposited at evaporation current of 60 A.



---

*Source: 564954-2015-07-07.xml*