# Preparation and Characterization of Polyhydroxybutyrate/Polycaprolactone Nanocomposites

Authors: Cha Ping Liau; Mansor Bin Ahmad; Kamyar Shameli; Wan Md Zin Wan Yunus; Nor Azowa Ibrahim; Norhazlin Zainuddin; Yoon Yee Then
Journal: The Scientific World Journal
 (2014)

---

## Abstract

Polyhydroxybutyrate (PHB)/polycaprolactone (PCL)/stearate Mg-Al layered double hydroxide (LDH) nanocomposites were prepared via solution casting intercalation method. Coprecipitation method was used to prepare the anionic clay Mg-Al LDH from nitrate salt solution. Modification of nitrate anions by stearate anions between the LDH layers via ion exchange reaction. FTIR spectra showed the presence of carboxylic acid (COOH) group which indicates that stearate anions were successfully intercalated into the Mg-Al LDH. The formation of nanocomposites only involves physical interaction as there are no new functional groups or new bonding formed. X-ray diffraction (XRD) and transmission electron microscopy (TEM) indicated that the mixtures of nanocomposites are intercalated and exfoliated types. XRD results showed increasing of basal spacing from 8.66 to 32.97 Å in modified stearate Mg-Al LDH, and TEM results revealed that the stearate Mg-Al LDH layers are homogeneously distributed in the PHB/PCL polymer blends matrix. Enhancement in 300% elongation at break and 66% tensile strength in the presence of 1.0 wt % of the stearate Mg-Al LDH as compare with PHB/PCL blends. Scanning electron microscopy (SEM) proved that clay improves compatibility between polymer matrix and the best ratio 80PHB/20PCL/1stearate Mg-Al LDH surface is well dispersed and stretched before it breaks.


---

## Body

## 1. Introduction

In the last decades, the production and the use of plastics which are synthetically derived from petroleum with not readily biodegradable have been gradually increased. Meanwhile, the amounts of plastic waste disposal has increased particularly in packaging application. Plastic waste consists of high degree of contamination which requires high energy cost to recycle [1]. The persistence of plastics waste in the environment, dwindling petroleum resources, shortage of landfill space, and the concerns over emissions of poisonous gases during incineration have fuelled efforts to develop biodegradable polymers from renewable resources to reduce the environmental pollution [2]. The term “biodegradable” materials is used to describe those materials which can be degraded and disintegrate by the enzymatic action of living organisms such as bacteria, yeasts, and fungi and the ultimate end-products of the degradation process, these being carbon dioxide, water and biomass under aerobic conditions and hydrocarbons, and methane and biomass under anaerobic conditions [3].Polyhydroxybutyrate (PHB) is natural thermoplastic polyester which is produced by bacterial fermentation [4] and degrades fully in the environment without forming any toxic products. It is biodegradable [5] (after few weeks in soil) and biocompatible, but some of the drawbacks such as brittleness, inherent rigidity, high production cost, and low melt stability limit its applications. A feasible strategy to reduce its brittle character and increase its physical properties such as flexibility and elongation at break is by blending with polycaprolactone (PCL) which is a synthetic thermoplastic polyester produced from ring opening polymerization of ε-caprolactone [6] and chemical synthesis of crude oil. PCL has excellent mechanical properties, is highly flexible, is biodegradable [7] (within 2 years in soil), is biocompatible, and has good water, oil, and solvent resistance. The disadvantages of PCL are low glass transition temperature (Tg) and low melting point leading to thermal instability. Polymer blends constitute a route to combine specific properties from different polymers via blending process that is relatively simple and less expensive compared to synthesis of new materials [8]. The purpose of blending is to achieve intermediate or even superior properties while preserving the major characteristics of the pure components [9]. Much of the attention to polymer/clay nanocomposites has been made to improve the flexibility, compatibility, and mechanical properties of polymer blends with small filler concentration [1, 3]. The final properties of nanocomposites with the filled of nanofiller depended on the filler dispersion and interaction at the polymer-filler interface [9].Inorganic-organic nanocomposite materials with functional organic compounds immobilized into a layered inorganic matrix have potential to offer scientific and technological advantages, since the organized two-dimensional arrays of organic species between the interlayers can result in novel functions that are different to the typical functions of the individual organic species [10–20].Layered double hydroxides (LDHs) are anionic clays with the general formula [M(II)1-XM(III)X(OH)2]X+[AX/nn-·mH2O]X- where M(II) and M(III) are divalent and trivalent cations, respectively, and An- is an exchangeable anion which is intercalated into interlayers to achieve charge neutrality [21]. Meanwhile, LDHs are host guest materials consisting of positively charged metal hydroxide sheets which remain stacked in z-direction with intercalated anions and water molecules [22]. This characteristic makes LDH materials suitable for polymer nanocomposites synthesis is the exchangeable nature of the interlayer anions by suitable oligomeric or polymeric anion [23]. Additionally, it is an advanced additive with the advantages of being environmentally friendly, economic, naturally abundant [24, 25], nontoxic, and room temperature prepared [26]. Naturally, LDHs are of hydrophilic character; in order to prepare high-performance nanocomposites, anion exchange process involves incorporating with long chain organic surfactant anion intercalation to reduce its hydrophilicity [27, 28]. The presence of hydrophobic intercalated anion improves the clay compatibility with being homogeneously dispersed within hydrophobic polymer matrices by strong interfacial adhesion and facilitates penetration of the polymer chains into interlayer spaces [29]. The aim of modification is to enlarge the interlayer distance and make LDH more hydrophobic [30]. The unusual packing of the organic anions in LDH gallery may facilitate their easier incorporation into polymers, leading to better nanocomposites formation [31]. The potential application outcomes could be the development of flame retardant composites, while improving the mechanical reinforcement and thermal stability due to the nanoscale filler dispersion [32] and strength of the polymer/filler interfaces [33].Costa et al. [34] reported the preparation of intercalation of Mg-Al LDH by anionic surfactants revealing increment in interlayer distance of modified Mg-Al LDH depending on the length of the surfactant anions. Furthermore, Sanchez-Garcia et al. [35] carried out solution cast composites preparation due to the fact that the melt instability of PHB will direct melt compounding. Besides, they proved that addition of PCL component led to a finer dispersion of the clay with intercalated morphologies and exhibited improved thermal stability.Recently, lots of researchers were focused on polymer blends and polymer nanocomposites by using biodegradable polymer to improve their use in application and to reduce the environmental pollution. Different biodegradable polymers and clay were used in this research work; the preparation and characterization of PHB/PCL nanocomposites have been described. It is worthwhile to investigate the effects of filler loading on the fracture toughness and the properties of composite materials. Significant improvements in morphology and mechanical properties were observed after the additional modified clay was incorporated into the PHB/PCL blend. Lee et al. [36] proved that the strong hydrogen bonding interaction between biodegradable aliphatic polyester and organoclay will lead to higher degree of intercalation and higher tensile properties caused by formation of nanocomposites with better dispersion.


## 2. Experimental Details

### 2.1. Materials

A bacterial crystalline thermoplastic polyhydroxybutyrate powder form was purchased from Sigma-Aldrich Chemic GmbH Company, Germany. Polycaprolactone (CAPA 650) with number-average molecular weight of 50,000 was supplied by Solvay Caprolactone (England). Magnesium nitrate hexahydrate and aluminium nitrate nonahydrate were supplied by HmbG chemicals (Hamburg, Germany). Sodium hydroxide pellets were obtained from Merck (Darmstadt, Germany). Sodium stearate was purchased from R&M chemicals (Essex, UK).


### 2.2. Synthesis of Mg-Al LDH

The Mg-Al LDH was prepared via coprecipitation method. NaOH 1 M solution was added drop by drop into a 250 mL solution of 19.22 g Mg(NO3)2·6H2O (0.2 M) and 9.38 g Al(NO3)3·9H2O (0.067 M) (with the mole ratio of 3 : 1, resp.) until pH 9 was acquired. It was carried out under vigorous stirring and constant flow of nitrogen N2 (g) to exclude carbon dioxide. The resulting suspension was shaken and heated at 70°C in water bath shaker at 100 rpm of speed for about 16 hours. The slurry was filtered, washed methodically with distilled water, and dried in oven at 60°C for 24 hours to obtain the Mg-Al LDH [21].


### 2.3. Preparation of Stearate Mg-Al LDH

Preparation of stearate-Mg3Al LDH via replacement of nitrate ions in the LDH layers with stearate ions from sodium stearate. One gram of the dry powder Mg-Al LDH was mixed with 1.8388 gram of sodium stearate and then dissolved in one liter of distilled water. The mixture was stirred for 24 hours and aged at 70°C of water bath to ensure complete reaction. Then, the white precipitate or slurry was filtered and washed with distilled water twice prior to drying at 60°C. The dried sample was ground and sieved into particles size of less than 100 micrometer.


### 2.4. Preparation of PHB/PCL Blends

PHB/PCL blends were prepared by solution casting method with different PCL contents (10, 20, 30, 40, and 50%). PHB and PCL were weighed, dissolved in 100 mL chloroform, and stirred for one hour, respectively. The two solutions were mixed and stirred for another 1 hour to obtain the homogeneous mixture solution. Besides, the mixture solutions were casted in a glass Petri dish and dried in the solvent atmosphere to obtain sample films.


### 2.5. Preparation of PHB/PCL/Stearate Mg-Al LDH Nanocomposites

From the characterization results of PHB/PCL blends, the optimum ratio of the blend was fixed at 80 : 20. The nanocomposites of PHB/PCL blend with different amounts of stearate Mg-Al LDH (0.25, 0.5, 1, 1.5, and 2%) were carried out by solution casting process. PHB, PCL, and stearate Mg-Al LDH were dissolved and stirred in 100 mL chloroform for one hour, respectively. Then the three solutions were mixed together and stirred for another one hour. Solidification took place to evaporate excess amount of chloroform for 15 minutes. The mixture was poured on Petri dish and left in fume cupboard for solvent evaporation to obtain dried films.


### 2.6. Fourier Transform Infrared (FTIR) Spectroscopy

The functional groups, types of bonding, and identified components in the samples were determined by a Perkin Elmer Spectrum 1000 Series Spectrophotometer equipped with attenuated total reflectance (ATR). The infrared spectra of the samples were recorded in the range of frequency of 400–4000 cm−1.


### 2.7. X-Ray Diffraction (XRD)

A Shimadzu XRD 6000 Diffractometer with nickel filtered Cu-Kα (λ=0.1542 nm) beam operated at 30 kV and 30 mA was used to determine the interlayer d-spacing of the clay layer in the original Mg-Al LDH, modified stearate Mg-Al LDH, blends, and nanocomposites using Bragg’s equation nλ=2dsinθ. Data were recorded in 2θ range of 2°–30° using the scan rate of 2°/min.


### 2.8. Tensile Properties Measurement

Tensile test was carried out by a Universal Testing Machine, Instron 4302, according to ASTM D638-5. A crosshead speed of 5 mm/min and a load cell of 1 kN were used and the tests were performed at 25°C. The samples films were cut into dumbbell shape using dumbbell cutter (Die BS 6476) and thickness of the samples was measured using a thickness gauge. The results were expressed in terms of tensile strength, tensile modulus, and elongation at break. Seven specimens were tested and the averages of five best measurements were reported.


### 2.9. Scanning Electron Microscopy (SEM)

The scanning electron micrographs of tensile fracture surface of the samples were recorded by a JSM-6400 scanning microscope which is a state-of-the-art high resolution scanning electron microscope with a modern digital image processing system. This SEM Joel operated at 20 kV to investigate the surface morphology of samples. The samples were coated with gold by a Bio-Rad coating system before viewing. The scanning electron micrographs were recorded at the magnification of 2000x.


### 2.10. Transmission Electron Microscopy (TEM)

The transmission electron micrographs of the thin layer of the nanocomposites were recorded by a LEO 912 A Benergy filter transmission electron microscope with an acceleration voltage of 100 keV. The thin layer of samples was prepared using a Reichert Jung Ultracut E microtome equipped with cryosectioning unit. The samples were sliced into thin layer of about 90 nm by a diamond knife cooled at −120°C with liquefied nitrogen.


## 2.1. Materials

A bacterial crystalline thermoplastic polyhydroxybutyrate powder form was purchased from Sigma-Aldrich Chemic GmbH Company, Germany. Polycaprolactone (CAPA 650) with number-average molecular weight of 50,000 was supplied by Solvay Caprolactone (England). Magnesium nitrate hexahydrate and aluminium nitrate nonahydrate were supplied by HmbG chemicals (Hamburg, Germany). Sodium hydroxide pellets were obtained from Merck (Darmstadt, Germany). Sodium stearate was purchased from R&M chemicals (Essex, UK).


## 2.2. Synthesis of Mg-Al LDH

The Mg-Al LDH was prepared via coprecipitation method. NaOH 1 M solution was added drop by drop into a 250 mL solution of 19.22 g Mg(NO3)2·6H2O (0.2 M) and 9.38 g Al(NO3)3·9H2O (0.067 M) (with the mole ratio of 3 : 1, resp.) until pH 9 was acquired. It was carried out under vigorous stirring and constant flow of nitrogen N2 (g) to exclude carbon dioxide. The resulting suspension was shaken and heated at 70°C in water bath shaker at 100 rpm of speed for about 16 hours. The slurry was filtered, washed methodically with distilled water, and dried in oven at 60°C for 24 hours to obtain the Mg-Al LDH [21].


## 2.3. Preparation of Stearate Mg-Al LDH

Preparation of stearate-Mg3Al LDH via replacement of nitrate ions in the LDH layers with stearate ions from sodium stearate. One gram of the dry powder Mg-Al LDH was mixed with 1.8388 gram of sodium stearate and then dissolved in one liter of distilled water. The mixture was stirred for 24 hours and aged at 70°C of water bath to ensure complete reaction. Then, the white precipitate or slurry was filtered and washed with distilled water twice prior to drying at 60°C. The dried sample was ground and sieved into particles size of less than 100 micrometer.


## 2.4. Preparation of PHB/PCL Blends

PHB/PCL blends were prepared by solution casting method with different PCL contents (10, 20, 30, 40, and 50%). PHB and PCL were weighed, dissolved in 100 mL chloroform, and stirred for one hour, respectively. The two solutions were mixed and stirred for another 1 hour to obtain the homogeneous mixture solution. Besides, the mixture solutions were casted in a glass Petri dish and dried in the solvent atmosphere to obtain sample films.


## 2.5. Preparation of PHB/PCL/Stearate Mg-Al LDH Nanocomposites

From the characterization results of PHB/PCL blends, the optimum ratio of the blend was fixed at 80 : 20. The nanocomposites of PHB/PCL blend with different amounts of stearate Mg-Al LDH (0.25, 0.5, 1, 1.5, and 2%) were carried out by solution casting process. PHB, PCL, and stearate Mg-Al LDH were dissolved and stirred in 100 mL chloroform for one hour, respectively. Then the three solutions were mixed together and stirred for another one hour. Solidification took place to evaporate excess amount of chloroform for 15 minutes. The mixture was poured on Petri dish and left in fume cupboard for solvent evaporation to obtain dried films.


## 2.6. Fourier Transform Infrared (FTIR) Spectroscopy

The functional groups, types of bonding, and identified components in the samples were determined by a Perkin Elmer Spectrum 1000 Series Spectrophotometer equipped with attenuated total reflectance (ATR). The infrared spectra of the samples were recorded in the range of frequency of 400–4000 cm−1.


## 2.7. X-Ray Diffraction (XRD)

A Shimadzu XRD 6000 Diffractometer with nickel filtered Cu-Kα (λ=0.1542 nm) beam operated at 30 kV and 30 mA was used to determine the interlayer d-spacing of the clay layer in the original Mg-Al LDH, modified stearate Mg-Al LDH, blends, and nanocomposites using Bragg’s equation nλ=2dsinθ. Data were recorded in 2θ range of 2°–30° using the scan rate of 2°/min.


## 2.8. Tensile Properties Measurement

Tensile test was carried out by a Universal Testing Machine, Instron 4302, according to ASTM D638-5. A crosshead speed of 5 mm/min and a load cell of 1 kN were used and the tests were performed at 25°C. The samples films were cut into dumbbell shape using dumbbell cutter (Die BS 6476) and thickness of the samples was measured using a thickness gauge. The results were expressed in terms of tensile strength, tensile modulus, and elongation at break. Seven specimens were tested and the averages of five best measurements were reported.


## 2.9. Scanning Electron Microscopy (SEM)

The scanning electron micrographs of tensile fracture surface of the samples were recorded by a JSM-6400 scanning microscope which is a state-of-the-art high resolution scanning electron microscope with a modern digital image processing system. This SEM Joel operated at 20 kV to investigate the surface morphology of samples. The samples were coated with gold by a Bio-Rad coating system before viewing. The scanning electron micrographs were recorded at the magnification of 2000x.


## 2.10. Transmission Electron Microscopy (TEM)

The transmission electron micrographs of the thin layer of the nanocomposites were recorded by a LEO 912 A Benergy filter transmission electron microscope with an acceleration voltage of 100 keV. The thin layer of samples was prepared using a Reichert Jung Ultracut E microtome equipped with cryosectioning unit. The samples were sliced into thin layer of about 90 nm by a diamond knife cooled at −120°C with liquefied nitrogen.


## 3. Results and Discussion

### 3.1. Characterization of Mg-Al LDH and Stearate Mg-Al LDH

Figure1 shows the FTIR spectra of Mg-Al LDH and stearate Mg-Al LDH which have broad adsorption bands at around 3399.51 cm−1 and 3420.04 cm−1, respectively. This is due to the O–H group stretching of both hydroxide layers and interlayer water molecules. Although the samples were calcined for longer time, the absorption bands persist which might be caused by strong bonded internal −OH group. An absorption band observed at 1600–1650 cm−1 is attributed to the H–OH bending vibration of the interlayer water. Absorption bands at below 800 cm−1 region are the lattice vibration bands of J–O and O–J–O (J = Mg or Al). An intense band which is shown in Mg–Al LDH at 1348.42 cm−1 is an asymmetric stretching vibration of nitrate anions [37]. Spectra 1(b) and 1(c) proved that the C–H stretching vibration due to the presence of the –CH3 and –CH2xgroups of long chain stearate anions [38] is observed at 2800–3000 cm−1 which has no peak at the spectrum 1(a). Meanwhile, two strong absorption peaks that located at 1566.73 cm−1 and 1455.02 cm−1 are assigned to carboxylate asymmetric and symmetric stretching [39]. As a conclusion, the stearate anions were successfully replacing the nitrate anions which were intercalated between the layers.Figure 1
FTIR spectra for (a) pristine Mg-Al LDH, (b) stearate Mg-Al LDH, and (c) sodium stearate.Figure2 shows the XRD patterns of Mg-Al LDH, stearate Mg-Al LDH, and sodium stearate in the determination range of 2θ from 2 to 30°. Both Mg-Al LDH and stearate Mg-Al LDH are crystalline solids with well-defined layered structure. From the determination of basal spacing by Bragg’s equation, nλ = 2dsinθ, where n is equal to 1 for <003> peak, λ is the wavelength of Cu-Kα radiation, and θ is the half of the scattering angle. The sodium stearate diffractogram shows a sharp peak at 2θ of 2.22° corresponding to the d-spacing of 39.80 Å which proved that the organic modifier increased clay interlayer distance. The chemical modification process indicates enhancement of d-spacing from 8.66 Å in Mg-Al LDH (corresponding 2θ value is 10.22°) to 32.97 Å in stearate Mg-Al LDH (corresponding 2θ value is 2.68°). This increment means that the stearate anions are successfully intercalated into the Mg-Al LDH interlayer and replace the nitrate anion via the anion exchange method [40]. In other words, long tail of hydrophobic chain of stearate anions will increase the d-spacing by radiating away the hydrophobic side of stearate anion from surface and hydrophilic side resides in the interlayer of LDH [34].Figure 2
XRD patterns of (a) pristine Mg-Al LDH, (b) stearate Mg-Al LDH, and (c) sodium stearate.


### 3.2. Characterization of PHB/PCL/Stearate Mg-Al LDH Nanocomposites

Stearate Mg-Al LDH was produced by the anion exchange reaction betweenNO3- anion in the interlayer of Mg-Al LDH and stearate anion H3C(CH2)16COO− from organic modifier sodium stearate. The replacement of anion position NO3- with H3C(CH2)16COO− anion enlarges the interlayer d-spacing and reduces hydrophilic surface of Mg-Al LDH. Clay with hydrophobic surface leads to easy intercalation of polymer chain within the clay layer due to the fact that the same polar will increase the dispersion. The stearate Mg-Al LDH produced was the solution casting with PHB/PCL blend with the weight ratio of 80 : 20 to formed PHB/PCL/stearate Mg-Al LDH nanocomposites. The previous investigation shows that 80PHB/20PCL blend had the higher tensile strength and elongation at break, so this weight ratio was chosen as our optimum blend.Figure3 shows the FTIR spectra of pure PHB, pure PCL, 80PHB/20PCL blend, and PHB/PCL/stearate Mg-Al LDH nanocomposites with different stearate Mg-Al LDH contents. The spectra 3(a) and 3(b) have the almost same functional group and peak of spectrum where absorption band is at 3442.37 cm−1 and 3444.95 cm−1, respectively, corresponding to broad O–H stretching. C–H group located at 2933.87 and 2978.11 reflecting lipid nature of PHB such as symmetric-asymmetric stretching band of methyl-methylene. Meanwhile, the peaks which appeared at 2942.37 cm−1 and 2867.18 cm−1 are due to the C–H stretching in spectrum 3(b). Beside, a strongest ester carbonyl absorption band, C=O stretching vibration located at 1719.54 cm−1 and 1722.17 cm−1 respectively. An asymmetrical C–H bending vibration in CH3 group showed an absorption band at 1453.33 cm−1 and 1466.56 cm−1, respectively. C–O–H bond shows a peak at 1378.95 cm−1 and 1365.30 cm−1 respectively. Additionally, FTIR spectra 3(a) and 3(b) present at 1181.48 cm−1 and 1167.31 cm−1 are attributed to C–O stretching. The spectra of PHB/PCL blend 3(c) and PHB/PCL/stearate Mg-Al LDH nanocomposites 3(d), 3(e), 3(f), 3(g), and 3(h) are consistent with the combination of pure PHB and pure PCL spectra. There is no major peak shifting or formation of new peak in the blend and nanocomposites spectra caused by no strong interaction and bonding between PHB, PCL and stearate Mg-Al LDH [29].Figure 3
FTIR spectra of (a) pure PHB, (b) pure PCL, and (c) 80PHB/20PCL blend and PHB/PCL/stearate Mg-Al LDH nanocomposite with (d) 0.25, (e) 0.5, (f) 1, (g) 1.5, and (h) 2 wt% stearate Mg-Al LDH content.Figure4 shows the XRD patterns of pure PHB, pure PCL, optimum ratio of PHB/PCL blend, and PHB/PCL/LDH nanocomposites of various amounts of the stearate Mg-Al LDH contents. The absence of the main diffraction peak at around 2.00° for very low concentrations such as 0.25 and 0.5 wt% stearate Mg-Al LDH nanocomposites shows that the LDH layers are completely exfoliated and randomly dispersed in the PHB/PCL polymer blend matrix [21]. For the nanocomposites that contain 1, 1.5, and 2 wt% stearate Mg-Al LDH nanocomposite there is a very small peak at 2θ of 2.195°, 2.275°, and 2.325° with 40.20 Å, 38.78 Å, and 38.00 Å interlayer spacing, respectively. This increment of d-spacing indicates that polymer chains are intercalated into the clay layers to form intercalated type nanocomposites.Figure 4
XRD patterns of (a) pure PHB, (b) pure PCL, and (c) 80PHB/20PCL and PHB/PCL/stearate Mg-Al LDH nanocomposites with (d) 0.25, (e) 0.5, (f) 1, (g) 1.5, and (h) 2 wt% stearate Mg-Al LDH content.The formation of nanocomposites can be directly observed by TEM. The transmission electron micrographs of optimum 80PHB/20PCL polymer blend and 80PHB/20PCL/1stearate Mg-Al LDH nanocomposites are shown in Figure5. In Figure 5(a), both of the polymers are organic polymers which dispersed well together so that the surfaces look smooth. After the addition of inorganic stearate Mg-Al LDH clay, the dark lines in Figure 5(b) represent the LDH layers in the PHB/PCL polymer matrix. At low clay content (1 wt% stearate Mg-Al LDH), clay is well dispersed in PHB/PCL matrix which also indicated a mixture of intercalated and exfoliated type nanocomposites.Transmission electron micrographs of (a) 80PHB/20PCL blend and (b) 80PHB/20PCL/1 wt% stearate Mg-Al LDH nanocomposites.
(a)
(b)Figures6, 7, and 8 show the tensile strength, modulus, and elongation at break of PHB/PCL/stearate Mg-Al LDH nanocomposites with effect of different stearate Mg-Al LDH contents. The tensile strength of neat PHB is 23.00 MPa and decreases to 17.02 MPa upon the addition of 20PCL. However, addition of 1 wt% of stearate Mg-Al LDH into 80PHB/20PCL blend increases the tensile strength to 28.23 MPa or an enhancement of 66% compared to the unfilled clay PHB/PCL blends. Tensile strength depends on the interaction between filler and polymer matrix; this result indicates that incorporating of stearate Mg-Al LDH increases interfacial adhesion which may play an important role in causing compatibilization at a molecular level [41]. The compatibility of clay improves the stress transfer within nanocomposites leading to increased tensile strength. Further addition of high filler content probably favours the formation of inorganic clusters or agglomerates and therefore reduces the tensile strength. The tensile modulus of PHB/PCL/stearate Mg-Al LDH nanocomposites increases with the increase of stearate Mg-Al LDH content. This increment is probably caused by restriction of the polymer chains from the interaction with the clay surface [42] which make samples stiff and easy to break with low value of elongation at break. Meanwhile, higher modulus is attributed to the good dispersion of nanosize clay primary particles that restrict the mobility of polymer chain under loading and good interfacial adhesion between the clay layers [43].Figure 6
Tensile strength of PHB/PCL/stearate Mg-Al LDH nanocomposites with 0.25, 0.5, 1, 1.5, and 2 wt% stearate Mg-Al LDH content.Figure 7
Modulus of PHB/PCL/stearate Mg-Al LDH nanocomposites with 0.25, 0.5, 1, 1.5, and 2 wt% stearate Mg-Al LDH content.Figure 8
Elongation at break of PHB/PCL/stearate Mg-Al LDH nanocomposites with 0.25, 0.5, 1, 1.5, and 2 wt% stearate Mg-Al LDH content.Nanocomposites with 1 wt% stearate Mg-Al LDH produced higher improvement in elongation at break which is 300% higher as compared with that of 80PHB/20PCL blend. Stearate anions are considered as plasticizer since their long hydrocarbon segments improve the flexibility of polymer matrix [44]. This is observed in the presence of long chain hydrocarbon parts of stearate anions which are intercalated into the LDH layers with increment flexibility and elongation at break of nanocomposites. However, the graph displayed similar trend to tensile strength; further addition of stearate Mg-Al LDH decreases the elongation at break due to extended agglomerates which makes the nanocomposites more brittle [45, 46].Figure9 shows SEM micrographs obtained from the tensile fracture surfaces of PHB/PCL blend and its nanocomposites containing 0.25, 0.5, 1, 1.5, and 2 wt% of stearate Mg-Al LDH. Figure 9(a) shows the fractured surface of optimum PHB/PCL blend with rough surface which reduces the rigidity of the samples. Figures 9(b)–9(e) show rough and well stretched surface before it breaks, indicating that the presence of the stearate Mg-Al LDH improves the compatibility and flexibility in nanocomposites [29]. This reveals that stearate Mg-Al LDH is a good compatibilizer that enhances the mixing and interaction between the components in the nanocomposites. Additionally, this could be the reason why nanocomposites exhibit higher tensile strength and elongation at break compared to unfilled additive blends.Figure 9
Scanning electron micrographs of (a) 80PHB/20PCL blend and PHB/PCL/stearate Mg-Al LDH nanocomposites with (b) 0.25, (c) 0.5, (d) 1, (e) 1.5, and (f) 2 wt% stearate Mg-Al LDH content at 2000x magnification.


## 3.1. Characterization of Mg-Al LDH and Stearate Mg-Al LDH

Figure1 shows the FTIR spectra of Mg-Al LDH and stearate Mg-Al LDH which have broad adsorption bands at around 3399.51 cm−1 and 3420.04 cm−1, respectively. This is due to the O–H group stretching of both hydroxide layers and interlayer water molecules. Although the samples were calcined for longer time, the absorption bands persist which might be caused by strong bonded internal −OH group. An absorption band observed at 1600–1650 cm−1 is attributed to the H–OH bending vibration of the interlayer water. Absorption bands at below 800 cm−1 region are the lattice vibration bands of J–O and O–J–O (J = Mg or Al). An intense band which is shown in Mg–Al LDH at 1348.42 cm−1 is an asymmetric stretching vibration of nitrate anions [37]. Spectra 1(b) and 1(c) proved that the C–H stretching vibration due to the presence of the –CH3 and –CH2xgroups of long chain stearate anions [38] is observed at 2800–3000 cm−1 which has no peak at the spectrum 1(a). Meanwhile, two strong absorption peaks that located at 1566.73 cm−1 and 1455.02 cm−1 are assigned to carboxylate asymmetric and symmetric stretching [39]. As a conclusion, the stearate anions were successfully replacing the nitrate anions which were intercalated between the layers.Figure 1
FTIR spectra for (a) pristine Mg-Al LDH, (b) stearate Mg-Al LDH, and (c) sodium stearate.Figure2 shows the XRD patterns of Mg-Al LDH, stearate Mg-Al LDH, and sodium stearate in the determination range of 2θ from 2 to 30°. Both Mg-Al LDH and stearate Mg-Al LDH are crystalline solids with well-defined layered structure. From the determination of basal spacing by Bragg’s equation, nλ = 2dsinθ, where n is equal to 1 for <003> peak, λ is the wavelength of Cu-Kα radiation, and θ is the half of the scattering angle. The sodium stearate diffractogram shows a sharp peak at 2θ of 2.22° corresponding to the d-spacing of 39.80 Å which proved that the organic modifier increased clay interlayer distance. The chemical modification process indicates enhancement of d-spacing from 8.66 Å in Mg-Al LDH (corresponding 2θ value is 10.22°) to 32.97 Å in stearate Mg-Al LDH (corresponding 2θ value is 2.68°). This increment means that the stearate anions are successfully intercalated into the Mg-Al LDH interlayer and replace the nitrate anion via the anion exchange method [40]. In other words, long tail of hydrophobic chain of stearate anions will increase the d-spacing by radiating away the hydrophobic side of stearate anion from surface and hydrophilic side resides in the interlayer of LDH [34].Figure 2
XRD patterns of (a) pristine Mg-Al LDH, (b) stearate Mg-Al LDH, and (c) sodium stearate.


## 3.2. Characterization of PHB/PCL/Stearate Mg-Al LDH Nanocomposites

Stearate Mg-Al LDH was produced by the anion exchange reaction betweenNO3- anion in the interlayer of Mg-Al LDH and stearate anion H3C(CH2)16COO− from organic modifier sodium stearate. The replacement of anion position NO3- with H3C(CH2)16COO− anion enlarges the interlayer d-spacing and reduces hydrophilic surface of Mg-Al LDH. Clay with hydrophobic surface leads to easy intercalation of polymer chain within the clay layer due to the fact that the same polar will increase the dispersion. The stearate Mg-Al LDH produced was the solution casting with PHB/PCL blend with the weight ratio of 80 : 20 to formed PHB/PCL/stearate Mg-Al LDH nanocomposites. The previous investigation shows that 80PHB/20PCL blend had the higher tensile strength and elongation at break, so this weight ratio was chosen as our optimum blend.Figure3 shows the FTIR spectra of pure PHB, pure PCL, 80PHB/20PCL blend, and PHB/PCL/stearate Mg-Al LDH nanocomposites with different stearate Mg-Al LDH contents. The spectra 3(a) and 3(b) have the almost same functional group and peak of spectrum where absorption band is at 3442.37 cm−1 and 3444.95 cm−1, respectively, corresponding to broad O–H stretching. C–H group located at 2933.87 and 2978.11 reflecting lipid nature of PHB such as symmetric-asymmetric stretching band of methyl-methylene. Meanwhile, the peaks which appeared at 2942.37 cm−1 and 2867.18 cm−1 are due to the C–H stretching in spectrum 3(b). Beside, a strongest ester carbonyl absorption band, C=O stretching vibration located at 1719.54 cm−1 and 1722.17 cm−1 respectively. An asymmetrical C–H bending vibration in CH3 group showed an absorption band at 1453.33 cm−1 and 1466.56 cm−1, respectively. C–O–H bond shows a peak at 1378.95 cm−1 and 1365.30 cm−1 respectively. Additionally, FTIR spectra 3(a) and 3(b) present at 1181.48 cm−1 and 1167.31 cm−1 are attributed to C–O stretching. The spectra of PHB/PCL blend 3(c) and PHB/PCL/stearate Mg-Al LDH nanocomposites 3(d), 3(e), 3(f), 3(g), and 3(h) are consistent with the combination of pure PHB and pure PCL spectra. There is no major peak shifting or formation of new peak in the blend and nanocomposites spectra caused by no strong interaction and bonding between PHB, PCL and stearate Mg-Al LDH [29].Figure 3
FTIR spectra of (a) pure PHB, (b) pure PCL, and (c) 80PHB/20PCL blend and PHB/PCL/stearate Mg-Al LDH nanocomposite with (d) 0.25, (e) 0.5, (f) 1, (g) 1.5, and (h) 2 wt% stearate Mg-Al LDH content.Figure4 shows the XRD patterns of pure PHB, pure PCL, optimum ratio of PHB/PCL blend, and PHB/PCL/LDH nanocomposites of various amounts of the stearate Mg-Al LDH contents. The absence of the main diffraction peak at around 2.00° for very low concentrations such as 0.25 and 0.5 wt% stearate Mg-Al LDH nanocomposites shows that the LDH layers are completely exfoliated and randomly dispersed in the PHB/PCL polymer blend matrix [21]. For the nanocomposites that contain 1, 1.5, and 2 wt% stearate Mg-Al LDH nanocomposite there is a very small peak at 2θ of 2.195°, 2.275°, and 2.325° with 40.20 Å, 38.78 Å, and 38.00 Å interlayer spacing, respectively. This increment of d-spacing indicates that polymer chains are intercalated into the clay layers to form intercalated type nanocomposites.Figure 4
XRD patterns of (a) pure PHB, (b) pure PCL, and (c) 80PHB/20PCL and PHB/PCL/stearate Mg-Al LDH nanocomposites with (d) 0.25, (e) 0.5, (f) 1, (g) 1.5, and (h) 2 wt% stearate Mg-Al LDH content.The formation of nanocomposites can be directly observed by TEM. The transmission electron micrographs of optimum 80PHB/20PCL polymer blend and 80PHB/20PCL/1stearate Mg-Al LDH nanocomposites are shown in Figure5. In Figure 5(a), both of the polymers are organic polymers which dispersed well together so that the surfaces look smooth. After the addition of inorganic stearate Mg-Al LDH clay, the dark lines in Figure 5(b) represent the LDH layers in the PHB/PCL polymer matrix. At low clay content (1 wt% stearate Mg-Al LDH), clay is well dispersed in PHB/PCL matrix which also indicated a mixture of intercalated and exfoliated type nanocomposites.Transmission electron micrographs of (a) 80PHB/20PCL blend and (b) 80PHB/20PCL/1 wt% stearate Mg-Al LDH nanocomposites.
(a)
(b)Figures6, 7, and 8 show the tensile strength, modulus, and elongation at break of PHB/PCL/stearate Mg-Al LDH nanocomposites with effect of different stearate Mg-Al LDH contents. The tensile strength of neat PHB is 23.00 MPa and decreases to 17.02 MPa upon the addition of 20PCL. However, addition of 1 wt% of stearate Mg-Al LDH into 80PHB/20PCL blend increases the tensile strength to 28.23 MPa or an enhancement of 66% compared to the unfilled clay PHB/PCL blends. Tensile strength depends on the interaction between filler and polymer matrix; this result indicates that incorporating of stearate Mg-Al LDH increases interfacial adhesion which may play an important role in causing compatibilization at a molecular level [41]. The compatibility of clay improves the stress transfer within nanocomposites leading to increased tensile strength. Further addition of high filler content probably favours the formation of inorganic clusters or agglomerates and therefore reduces the tensile strength. The tensile modulus of PHB/PCL/stearate Mg-Al LDH nanocomposites increases with the increase of stearate Mg-Al LDH content. This increment is probably caused by restriction of the polymer chains from the interaction with the clay surface [42] which make samples stiff and easy to break with low value of elongation at break. Meanwhile, higher modulus is attributed to the good dispersion of nanosize clay primary particles that restrict the mobility of polymer chain under loading and good interfacial adhesion between the clay layers [43].Figure 6
Tensile strength of PHB/PCL/stearate Mg-Al LDH nanocomposites with 0.25, 0.5, 1, 1.5, and 2 wt% stearate Mg-Al LDH content.Figure 7
Modulus of PHB/PCL/stearate Mg-Al LDH nanocomposites with 0.25, 0.5, 1, 1.5, and 2 wt% stearate Mg-Al LDH content.Figure 8
Elongation at break of PHB/PCL/stearate Mg-Al LDH nanocomposites with 0.25, 0.5, 1, 1.5, and 2 wt% stearate Mg-Al LDH content.Nanocomposites with 1 wt% stearate Mg-Al LDH produced higher improvement in elongation at break which is 300% higher as compared with that of 80PHB/20PCL blend. Stearate anions are considered as plasticizer since their long hydrocarbon segments improve the flexibility of polymer matrix [44]. This is observed in the presence of long chain hydrocarbon parts of stearate anions which are intercalated into the LDH layers with increment flexibility and elongation at break of nanocomposites. However, the graph displayed similar trend to tensile strength; further addition of stearate Mg-Al LDH decreases the elongation at break due to extended agglomerates which makes the nanocomposites more brittle [45, 46].Figure9 shows SEM micrographs obtained from the tensile fracture surfaces of PHB/PCL blend and its nanocomposites containing 0.25, 0.5, 1, 1.5, and 2 wt% of stearate Mg-Al LDH. Figure 9(a) shows the fractured surface of optimum PHB/PCL blend with rough surface which reduces the rigidity of the samples. Figures 9(b)–9(e) show rough and well stretched surface before it breaks, indicating that the presence of the stearate Mg-Al LDH improves the compatibility and flexibility in nanocomposites [29]. This reveals that stearate Mg-Al LDH is a good compatibilizer that enhances the mixing and interaction between the components in the nanocomposites. Additionally, this could be the reason why nanocomposites exhibit higher tensile strength and elongation at break compared to unfilled additive blends.Figure 9
Scanning electron micrographs of (a) 80PHB/20PCL blend and PHB/PCL/stearate Mg-Al LDH nanocomposites with (b) 0.25, (c) 0.5, (d) 1, (e) 1.5, and (f) 2 wt% stearate Mg-Al LDH content at 2000x magnification.


## 4. Conclusion

Modification of stearate Mg-Al LDH was successfully prepared by coprecipitation and ion exchange reaction. Besides, PHB/PCL/stearate Mg-Al LDH nanocomposites were prepared via solution casting method by using chloroform as organic solvent. XRD analysis reveals that low filler concentration produced exfoliated nanocomposites. The presence of 1 wt% of stearate Mg-Al LDH content shows that higher interlayer spacing and intercalated nanocomposites were produced by addition of high filler content. Moreover, there is no major peak shifting and no formation of new peak in FTIR spectrum indicated no strong interaction among PHB, PCL, and stearate Mg-Al LDH. Mechanical analyses showed that an 80PHB/20PCL/1stearate Mg-Al LDH nanocomposite was drastically enhanced by about 66% and 300% for its tensile strength and elongation at break. These improvements have been exhibited by SEM where the incorporation of stearate Mg-Al LDH clay gradually increases the flexibility and compatibility of nanocomposites.



---

*Source: 572726-2014-01-29.xml*