# Synthesis and Characterization of an Amphiphilic Linoleic Acid-g-Quaternary Chitosan with Low Toxicity

Authors: Xiaobin Fang; Yingqi Xu; Jinming Zhang; Xianghong Lu; Yitao Wang; Meiwan Chen
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

A novel amphiphilic derivative of chitosan, namely, a linoleic acid-g-quaternary chitosan (LA-g-QC), was designed and synthesized as low toxic material for biomedical applications in this study. The chemical structure of LA-g-QC was characterized by Fourier transform infrared spectroscopy (FTIR),1H nuclear magnetic resonance (1H-NMR), and elemental analysis. LA-g-QC could form nanosized micelles with self-assembly, which was confirmed by the results of critical micelle concentration (CMC) via fluorescence spectroscopy. The average size of LA-g-QC was 140 nm and its zeta potential was approximately +35.50 mV. CMC value was 31.00 mg/mL. Furthermore, LA-g-QC micelles, at final concentrations between 0.94 μg/mL and 30 μg/mL, did not inhibit the proliferation of HepG2 or SMMC 7721 cell lines. Taken together, LA-g-QC has low cytotoxicity and high potential for the preparation of novel drug-delivery micelles.


---

## Body

## 1. Introduction

Chitosan is a natural polysaccharide withβ-(1-4)-linked D-glucosamine (deacetylated unit) and N-acetyl-D-glucosamine (acetylated unit) [1, 2] and the only kind of natural edible animal fibers containing free amino group alkaline cation, which is composed after the formation of deacetylation under alkaline conditions. Its molecular weight varies from a few hundred thousand to several million, depending upon different preparation conditions and the degree of deacetylation ranging from 60 to 100% [3]. Chitosan has many unique properties such as cell affinity and biocompatibility [4] and is known as the sixth element of life. Thus it can be used for the prevention and treatment of some human diseases [5]. Owing to the special molecular structure and physicochemical properties, chitosan has antimicrobial, anti-inflammatory, hemostatic, wound healing, and other bioactivities, which make it possible to be widely used in food industry, chemicals, agriculture, and bioengineering [6, 7].However, chitosan is soluble neither in water nor in common organic solvents such as dilute sulfuric acid and phosphoric acid; it is only soluble in dilute hydrochloric acid, nitric acid, and most other organic and inorganic acids [8]. In the media where pH is above 6, the amines of chitosan become deprotonated and, therefore, it becomes insoluble. Compared with chitin, chitosan exhibits better dissolution ability significantly contributing to its hydrophilicity and amino functional group [9]. Nevertheless, it can only dissolve in dilute acid solution, which limits its application to a large extent. Therefore, to improve the solubility of chitosan, especially solubility in water, is one of the most important modifications of chitosan [10]. Prepared by chemical modification, a large number of hydroxyl groups and amino groups of the chitosan molecular chains can be introduced into various derivatives which have different functional groups on the repeating units. Thus, the chemical modification of chitosan in chitin chemistry is one of the most active areas of research. For instance, Chen et al. [11] introduced deoxycholic acid into chitosan, which acted as hydrophobic group, to endow chitosan with amphiphilicity.Linoleic acid (LA), as one of the polyunsaturated fatty acids, can be easily inserted into the phospholipid bilayer of cell membrane and disorder the structure and fluidity of cell membrane, thus being rapidly taken up by cells [12]. Furthermore, it can also affect the tumor cell chemosensitivity [13]. Therefore, LA was chosen and used as hydrophobic part to modify chitosan in our research.In this study, with an aim to improve the solubility of chitosan, an amphiphilic LA-g-quaternary chitosan (LA-g-QC) copolymer was designed and synthesized. Having confirmed its structure by1H-NMR, FTIR, and TEM, we fabricated LA-g-QC copolymer into micelles by using the self-assembly method and analyzed its physicochemical properties of LA-g-QC micelles including CMC, particle size, zeta potential, and TEM. Furthermore, thein vitro cytotoxicity of LA-g-QC micelles was evaluated.


## 2. Materials and Methods

### 2.1. Materials

Chitosan (M
w 2.0 × 105, DD (degree of deacetylation) 85%) was obtained from Jinan Haidebei Marine Bioengineering Co., Ltd. (Shandong, China). 2,3-Epoxypropyltrimethylammonium chloride [14] was provided by Dongying Guofeng Fine Chemical Co., Ltd. (Shandong, China). LA was purchased from Aladdin Industrial Corporation (Shanghai, China). All other agents used were of analytical grades.Human hepatoma cell lines HepG2 and SMMC 7721 were supplied by American Type Culture Collection (ATCC, Rockville, MD, USA). Fetal bovine serum (FBS), Dulbecco’s Modified Eagle Medium (DMEM), and 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) were obtained from Sigma-Aldrich.


### 2.2. Preparation of LA-g-QC

The LA-g-QC copolymer was synthesized by two steps as shown in Figure1. The first step is obtaining quaternized chitosan (QCS) by 2,3-Epoxypropyltrimethylammonium chloride [14] under microwave radiation [15]. A certain amount of chitosan was dispersed in isopropyl alcohol, and the suspension was regulated to pH 9 with sodium hydroxide solution. ETA aqueous solution was then added to chitosan suspension drop by drop. The whole reaction mixture was exposed to microwave irradiation at 400 W for 70 min. Subsequently, reaction mixture was precipitated by the cold acetone and washed with phosphate buffer solution for three times. The second step is grafting LA on QCS. QCS, LA, and EDC were dissolved in dimethyl formamide with molar ratio 1 : 1 : 1.5 under stirring for 12 h. The reaction mixture was precipitated and washed by acetone for three times. Finally, LA-g-QC was obtained by lyophilizing.Figure 1
The synthetic route of LA-g-QC copolymer. The first step was the chemical reaction of ETA and the chitosan and finally the obtaining of QCS. The second step was to graft LA on QCS.


### 2.3. Preparation of LA-g-QC Micelles

The LA-g-QC micelles were prepared by the solvent evaporation method. In brief, LA-g-QC copolymer (10 mg) dispersed in the 4% ethanol solution under stirring. After stirring for 2 h, the suspension was filtered with 0.45μm filter membrane to obtain LA-g-QC micelles solution.


### 2.4. Fourier Transform Infrared Spectroscopy (FTIR)

Chitosan and LA-g-QC were mixed with KBr, and the FTIR spectra of which were conducted on a NEXUS 670 FT-IR spectrophotometer (Nicolet, USA) at room temperature at 25°C [16]. The samples were scanned from 400 to 4000 cm−1 with a resolution of 4 cm−1.


### 2.5. Proton Nuclear Magnetic Resonance (1H-NMR)

The1H-NMR spectra of chitosan and LA-g-QC were characterized using liquid nuclear magnetic resonance spectrometer (400 MHz, Bruker, Germany), with CF3COOD/D2O as solvents.


### 2.6. Elemental Analysis

The substitution degree (SD) of QCS and LA-g-QC was determined by elemental analysis using elemental analyzer Vario EL cube (Elementar, Germany). SD was calculated according to the content of C, O, and N.


### 2.7. Transmission Electron Microscopy (TEM)

LA-g-QC micelle solution was placed on a carbon-coated copper grid, observed subsequently, and photographed using high resolution transmission electron microscopy (HRTEM, Tecnai G20, FEI Company, USA) with an operating voltage of 200 kV.


### 2.8. Particle Size and Zeta Potential

Particle size and zeta potential of LA-g-QC micelles were measured using a dynamic light scattering Zetasizer (DLS) at 25°C with Zetasizer Nano ZSP System (Malvern Instruments, Worcestershire, UK).


### 2.9. Critical Micelle Concentration (CMC)

The CMC of LA-g-QC was determined by Fluorescence Spectrometer (LUMINA, Thermo Scientific, USA) with pyrene as a hydrophobic probe. Aliquots of pyrene in acetone (6.0 × 10−6 M, 1 mL) were added to each vial (10 mL). After acetone evaporation was complete, 10 mL of a series of concentrations of LA-g-QC (1.0 × 10−4, 1.0 × 10−3, 2.0 × 10−3, 5.0 × 10−2, 1.0 × 10−1, and 1.0 mg/mL) was added to the above vials. The fluorescence emission spectra were recorded at an excitation wavelength of 339 nm, and the emission wavelength was between 360 and 450 nm.


### 2.10.In Vitro Cytotoxicity Assays

HepG2 and SMMC 7721 cells were cultivated in DMEM medium added with 10% FBS, 100 U/mL penicillin, and 100μg/mL streptomycin at 37°C and 5% CO2. The cytotoxicity of LA-g-QC micelles on these two cells was investigated by MTT assay [17]. The cells were seeded into 96-well plates at 6000 cells per well in 100 μL of culture medium. After 24 h incubation, the medium was removed and replaced with medium containing various concentrations of blank polymer micelles. After the additional 24 h and 48 h incubation at 37°C, respectively, medium without FBS containing MTT dye 5 mg/mL took place of the previous culture medium for another 4 h to form formazan crystals by mitochondrial dehydrogenases. Subsequently, 100 μL of DMSO was supplemented to dissolve the formazan crystals in each well. The absorbance of cells was evaluated at 570 nm with untreated cells as controls. The absorbance ratio of treated cells and control cells was expressed as cell viability to characterize the cytotoxicity of polymers.


## 2.1. Materials

Chitosan (M
w 2.0 × 105, DD (degree of deacetylation) 85%) was obtained from Jinan Haidebei Marine Bioengineering Co., Ltd. (Shandong, China). 2,3-Epoxypropyltrimethylammonium chloride [14] was provided by Dongying Guofeng Fine Chemical Co., Ltd. (Shandong, China). LA was purchased from Aladdin Industrial Corporation (Shanghai, China). All other agents used were of analytical grades.Human hepatoma cell lines HepG2 and SMMC 7721 were supplied by American Type Culture Collection (ATCC, Rockville, MD, USA). Fetal bovine serum (FBS), Dulbecco’s Modified Eagle Medium (DMEM), and 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) were obtained from Sigma-Aldrich.


## 2.2. Preparation of LA-g-QC

The LA-g-QC copolymer was synthesized by two steps as shown in Figure1. The first step is obtaining quaternized chitosan (QCS) by 2,3-Epoxypropyltrimethylammonium chloride [14] under microwave radiation [15]. A certain amount of chitosan was dispersed in isopropyl alcohol, and the suspension was regulated to pH 9 with sodium hydroxide solution. ETA aqueous solution was then added to chitosan suspension drop by drop. The whole reaction mixture was exposed to microwave irradiation at 400 W for 70 min. Subsequently, reaction mixture was precipitated by the cold acetone and washed with phosphate buffer solution for three times. The second step is grafting LA on QCS. QCS, LA, and EDC were dissolved in dimethyl formamide with molar ratio 1 : 1 : 1.5 under stirring for 12 h. The reaction mixture was precipitated and washed by acetone for three times. Finally, LA-g-QC was obtained by lyophilizing.Figure 1
The synthetic route of LA-g-QC copolymer. The first step was the chemical reaction of ETA and the chitosan and finally the obtaining of QCS. The second step was to graft LA on QCS.


## 2.3. Preparation of LA-g-QC Micelles

The LA-g-QC micelles were prepared by the solvent evaporation method. In brief, LA-g-QC copolymer (10 mg) dispersed in the 4% ethanol solution under stirring. After stirring for 2 h, the suspension was filtered with 0.45μm filter membrane to obtain LA-g-QC micelles solution.


## 2.4. Fourier Transform Infrared Spectroscopy (FTIR)

Chitosan and LA-g-QC were mixed with KBr, and the FTIR spectra of which were conducted on a NEXUS 670 FT-IR spectrophotometer (Nicolet, USA) at room temperature at 25°C [16]. The samples were scanned from 400 to 4000 cm−1 with a resolution of 4 cm−1.


## 2.5. Proton Nuclear Magnetic Resonance (1H-NMR)

The1H-NMR spectra of chitosan and LA-g-QC were characterized using liquid nuclear magnetic resonance spectrometer (400 MHz, Bruker, Germany), with CF3COOD/D2O as solvents.


## 2.6. Elemental Analysis

The substitution degree (SD) of QCS and LA-g-QC was determined by elemental analysis using elemental analyzer Vario EL cube (Elementar, Germany). SD was calculated according to the content of C, O, and N.


## 2.7. Transmission Electron Microscopy (TEM)

LA-g-QC micelle solution was placed on a carbon-coated copper grid, observed subsequently, and photographed using high resolution transmission electron microscopy (HRTEM, Tecnai G20, FEI Company, USA) with an operating voltage of 200 kV.


## 2.8. Particle Size and Zeta Potential

Particle size and zeta potential of LA-g-QC micelles were measured using a dynamic light scattering Zetasizer (DLS) at 25°C with Zetasizer Nano ZSP System (Malvern Instruments, Worcestershire, UK).


## 2.9. Critical Micelle Concentration (CMC)

The CMC of LA-g-QC was determined by Fluorescence Spectrometer (LUMINA, Thermo Scientific, USA) with pyrene as a hydrophobic probe. Aliquots of pyrene in acetone (6.0 × 10−6 M, 1 mL) were added to each vial (10 mL). After acetone evaporation was complete, 10 mL of a series of concentrations of LA-g-QC (1.0 × 10−4, 1.0 × 10−3, 2.0 × 10−3, 5.0 × 10−2, 1.0 × 10−1, and 1.0 mg/mL) was added to the above vials. The fluorescence emission spectra were recorded at an excitation wavelength of 339 nm, and the emission wavelength was between 360 and 450 nm.


## 2.10.In Vitro Cytotoxicity Assays

HepG2 and SMMC 7721 cells were cultivated in DMEM medium added with 10% FBS, 100 U/mL penicillin, and 100μg/mL streptomycin at 37°C and 5% CO2. The cytotoxicity of LA-g-QC micelles on these two cells was investigated by MTT assay [17]. The cells were seeded into 96-well plates at 6000 cells per well in 100 μL of culture medium. After 24 h incubation, the medium was removed and replaced with medium containing various concentrations of blank polymer micelles. After the additional 24 h and 48 h incubation at 37°C, respectively, medium without FBS containing MTT dye 5 mg/mL took place of the previous culture medium for another 4 h to form formazan crystals by mitochondrial dehydrogenases. Subsequently, 100 μL of DMSO was supplemented to dissolve the formazan crystals in each well. The absorbance of cells was evaluated at 570 nm with untreated cells as controls. The absorbance ratio of treated cells and control cells was expressed as cell viability to characterize the cytotoxicity of polymers.


## 3. Results and Discussion

### 3.1. Synthesis and Structural Characterization of LA-g-QC

A novel amphiphilic LA-g-QC copolymer was synthesized according to the schemes shown in Figures2 and 3. It can be seen from the FTIR spectra of chitosan that the characteristic peak lying at 1599 cm−1 attributed to NH2 deformation vibration; however, it was weakened or even disappeared in the spectra of QCS and LA-g-QC, and another peak at 1544 cm−1 corresponding to N-H and C-N of amido bond appeared. Additionally, a new peak at 1483 cm−1 emerged due to the methyl groups in the quaternary ammonium salt [15]. Interestingly, the characteristic peaks of primary alcohol and secondary alcohol in QCS samples positioned between 1152 cm−1 and 1030 cm−1 were consistent with the ones in original chitosan. The results indicated that the N-monosubstitution on C2 position of chitosan was modified by introducing the ETA as expected. Moreover, in the spectra of LA-g-QC, another new peak at 1750 cm−1 appeared due to the ester groups, proving that the LA was successfully grafted into the quaternary chitosan. In order to confirm the successful synthesis of LA-g-QC, 1H-NMR spectra of LA-g-QC are shown in Figure 3. Besides the typical signals for chitosan, including δ = 2.87~3.15 ppm for CH groups and δ = 3.23 ppm for CH2, it can be observed at δ = 2.61, 3.44 ppm for CH2 groups, δ = 3.35 ppm for CH3 groups, and δ = 3.97 ppm for CH groups of quaternary ammonium salt. Last but not least, the signals were detected at δ = 4.35 ppm and δ = 0.87~1.98 ppm for LA. These results suggested that quaternary ammonium salt and LA were successfully grafted onto chitosan.Figure 2
FTIR spectra of chitosan, QCS, and LA-g-QC.Figure 3
1H-NMR spectra of LA-g-QC in D2O.


### 3.2. Elemental Analysis

The substitution degree (SD) of quaternary ammonium salt and LA was important parameter for LA-g-QC. According to the elemental analysis, the substitution degree was calculated based on the C and N molar ratios. It can be seen from Table1 that the standard deviation of the prepared polymers QCS and LA-g-QC was between 2.3% and 1.6%, respectively. The substitution degree (SD) of quaternary ammonium salt and LA was 42.6% and 27.4%, respectively.Table 1
Chemical compositions and properties of polymer micelles (n
=
3).
Sample
N(C)/N(O)
Standard deviation (%)
Degree of quaternization (%)
Degree of substitution (%)
CS
1.13
0.3
—
—
QCS
1.41
2.3
42.6
—
LA-g-QC
2.05
1.6
—
27.4
Note. N(C)/N(O): the rate of the number of carbon elements to the number of oxygen elements in polymer. The table showed the degree of quaternization of the QCS and the degree of substitution of LA-g-QC through the elemental analysis.


### 3.3. Particle Size and Zeta Potential

The particle size and zeta potential of LA-g-QC were analyzed, respectively. Figure4(a) showed that LA-g-QC had a narrow distribution (PDI = 0.201, <0.5 = with an average size of 136.5 nm). Figure 4(b) indicated that the zeta potential was approximately +17.4 mV. Both results proved that LA-g-QC exhibited good properties as micelles. As reported, small nanocarriers (<200 nm) with positive charge can easily prevent the reticuloendothelial cell systems from uptake while tending to combine with the negative charge in cellular membrane. Therefore, the bioavailability of bioactive drugs can be enhanced after encapsulation into LA-g-QC.Figure 4
(a) The average particle size of LA-g-QC micelles was 136.5 nm with a narrow distribution. (b) The zeta potential of LA-g-QC micelles. It showed that the zeta potential was about +17.4 mV. (c) and (d) The TEM images of LA-g-QC micelles. It showed that the micelles had a spherical shape and the size of the micelles was slightly smaller than that determined by the DLS.
(a)
(b)
(c)
(d)


### 3.4. Transmission Electron Microscopy (TEM)

The TEM images of LA-g-QC micelles were shown in Figure4(c), illustrating that the micelles had homogeneous spherical shapes and smooth surfaces without cracks. Micelles size viewed from TEM seemed to be slightly smaller compared with those obtained from DLS determination, indicating that the hydrophilic backbone in the micelles might shrink while drying the TEM samples.


### 3.5. Critical Micelle Concentration (CMC)

As CMC is an important characteristic to evaluate the aggregation properties of LA-g-QC, it was determined by using the probe fluorescence technique. Pyrene was applied as the fluorescence probe, which hardly solubilized in water but had a considerably high solubility in the hydrophobic region of the micelles such as LA-g-QC solution with a series of concentrations from 1.0 × 10−4 to 1.0 mg/mL. The results demonstrated that the fluorescence intensity rose as the concentration of LA-g-QC increased. The fluorescence of pyrene in water is negligible because of the extremely low solubility. However, when the concentration was above CMC, the solubility of pyrene would increase because the micelle core was formed as a subsequence, as a result of increased solution fluorescence. The fluorescence intensity ratio of pyrene I
3
/
I
1 (383 nm/372 nm) was analyzed as a logarithm function of the LA-g-QC concentration (Figure 5). A Boltzmann function was used to fit the scatters. By using the mathematical method, the value of CMC was calculated and shown as low as approximately 3.5 mg/L. These results indicated that LA-g-QC was rational material for forming self-organized liposomes and might retain the integrity even upon strong dilution during systematic circulation.Figure 5
LA-g-QC micellar solution at different concentrations. The value of CMC was calculated as low as approximately 3.5 mg/L.


### 3.6.In Vitro Cytotoxicity Assays

Highly biological safety should be the most important criterion for medical application. To figure out whether micelles constituted by LA-g-QC copolymer have potential as drug carriers or probes, MTT assay has been applied to evaluate its cytotoxicity. HepG2 and SMMC 7721 cells were chosen to incubate with various concentrations of LA-g-QC micelles for 24 h and 48 h, respectively. As shown in Figure6, blank micelles did not significantly inhibit the cell proliferation, ranging from 0.94 to 30 μg/mL copolymer concentrations. After 24 h incubation, cell viability kept above 90%. Even after incubation for 48 h, low cytotoxicity of LA-g-QC copolymer was shownin vitro (Cell viability > 85%). This result was consistent with the reported cytotoxicity of chitosan-based polymeric micelles, which showed that treatment with 15.6 μg/mL of hydrophobically modified sulfated chitosan for 48 h made approximately 90% of HepG2 cells survive [18]. This result would provide evidences for the low biological toxicity and application potential of LA-g-QC micelles in biomedical field.Figure 6
Cytotoxicity of LA-g-QC micelles against HepG2 and SMMC 7721 cells after 24 h (a) and 48 h (b) incubation.
(a)
(b)


## 3.1. Synthesis and Structural Characterization of LA-g-QC

A novel amphiphilic LA-g-QC copolymer was synthesized according to the schemes shown in Figures2 and 3. It can be seen from the FTIR spectra of chitosan that the characteristic peak lying at 1599 cm−1 attributed to NH2 deformation vibration; however, it was weakened or even disappeared in the spectra of QCS and LA-g-QC, and another peak at 1544 cm−1 corresponding to N-H and C-N of amido bond appeared. Additionally, a new peak at 1483 cm−1 emerged due to the methyl groups in the quaternary ammonium salt [15]. Interestingly, the characteristic peaks of primary alcohol and secondary alcohol in QCS samples positioned between 1152 cm−1 and 1030 cm−1 were consistent with the ones in original chitosan. The results indicated that the N-monosubstitution on C2 position of chitosan was modified by introducing the ETA as expected. Moreover, in the spectra of LA-g-QC, another new peak at 1750 cm−1 appeared due to the ester groups, proving that the LA was successfully grafted into the quaternary chitosan. In order to confirm the successful synthesis of LA-g-QC, 1H-NMR spectra of LA-g-QC are shown in Figure 3. Besides the typical signals for chitosan, including δ = 2.87~3.15 ppm for CH groups and δ = 3.23 ppm for CH2, it can be observed at δ = 2.61, 3.44 ppm for CH2 groups, δ = 3.35 ppm for CH3 groups, and δ = 3.97 ppm for CH groups of quaternary ammonium salt. Last but not least, the signals were detected at δ = 4.35 ppm and δ = 0.87~1.98 ppm for LA. These results suggested that quaternary ammonium salt and LA were successfully grafted onto chitosan.Figure 2
FTIR spectra of chitosan, QCS, and LA-g-QC.Figure 3
1H-NMR spectra of LA-g-QC in D2O.


## 3.2. Elemental Analysis

The substitution degree (SD) of quaternary ammonium salt and LA was important parameter for LA-g-QC. According to the elemental analysis, the substitution degree was calculated based on the C and N molar ratios. It can be seen from Table1 that the standard deviation of the prepared polymers QCS and LA-g-QC was between 2.3% and 1.6%, respectively. The substitution degree (SD) of quaternary ammonium salt and LA was 42.6% and 27.4%, respectively.Table 1
Chemical compositions and properties of polymer micelles (n
=
3).
Sample
N(C)/N(O)
Standard deviation (%)
Degree of quaternization (%)
Degree of substitution (%)
CS
1.13
0.3
—
—
QCS
1.41
2.3
42.6
—
LA-g-QC
2.05
1.6
—
27.4
Note. N(C)/N(O): the rate of the number of carbon elements to the number of oxygen elements in polymer. The table showed the degree of quaternization of the QCS and the degree of substitution of LA-g-QC through the elemental analysis.


## 3.3. Particle Size and Zeta Potential

The particle size and zeta potential of LA-g-QC were analyzed, respectively. Figure4(a) showed that LA-g-QC had a narrow distribution (PDI = 0.201, <0.5 = with an average size of 136.5 nm). Figure 4(b) indicated that the zeta potential was approximately +17.4 mV. Both results proved that LA-g-QC exhibited good properties as micelles. As reported, small nanocarriers (<200 nm) with positive charge can easily prevent the reticuloendothelial cell systems from uptake while tending to combine with the negative charge in cellular membrane. Therefore, the bioavailability of bioactive drugs can be enhanced after encapsulation into LA-g-QC.Figure 4
(a) The average particle size of LA-g-QC micelles was 136.5 nm with a narrow distribution. (b) The zeta potential of LA-g-QC micelles. It showed that the zeta potential was about +17.4 mV. (c) and (d) The TEM images of LA-g-QC micelles. It showed that the micelles had a spherical shape and the size of the micelles was slightly smaller than that determined by the DLS.
(a)
(b)
(c)
(d)


## 3.4. Transmission Electron Microscopy (TEM)

The TEM images of LA-g-QC micelles were shown in Figure4(c), illustrating that the micelles had homogeneous spherical shapes and smooth surfaces without cracks. Micelles size viewed from TEM seemed to be slightly smaller compared with those obtained from DLS determination, indicating that the hydrophilic backbone in the micelles might shrink while drying the TEM samples.


## 3.5. Critical Micelle Concentration (CMC)

As CMC is an important characteristic to evaluate the aggregation properties of LA-g-QC, it was determined by using the probe fluorescence technique. Pyrene was applied as the fluorescence probe, which hardly solubilized in water but had a considerably high solubility in the hydrophobic region of the micelles such as LA-g-QC solution with a series of concentrations from 1.0 × 10−4 to 1.0 mg/mL. The results demonstrated that the fluorescence intensity rose as the concentration of LA-g-QC increased. The fluorescence of pyrene in water is negligible because of the extremely low solubility. However, when the concentration was above CMC, the solubility of pyrene would increase because the micelle core was formed as a subsequence, as a result of increased solution fluorescence. The fluorescence intensity ratio of pyrene I
3
/
I
1 (383 nm/372 nm) was analyzed as a logarithm function of the LA-g-QC concentration (Figure 5). A Boltzmann function was used to fit the scatters. By using the mathematical method, the value of CMC was calculated and shown as low as approximately 3.5 mg/L. These results indicated that LA-g-QC was rational material for forming self-organized liposomes and might retain the integrity even upon strong dilution during systematic circulation.Figure 5
LA-g-QC micellar solution at different concentrations. The value of CMC was calculated as low as approximately 3.5 mg/L.


## 3.6.In Vitro Cytotoxicity Assays

Highly biological safety should be the most important criterion for medical application. To figure out whether micelles constituted by LA-g-QC copolymer have potential as drug carriers or probes, MTT assay has been applied to evaluate its cytotoxicity. HepG2 and SMMC 7721 cells were chosen to incubate with various concentrations of LA-g-QC micelles for 24 h and 48 h, respectively. As shown in Figure6, blank micelles did not significantly inhibit the cell proliferation, ranging from 0.94 to 30 μg/mL copolymer concentrations. After 24 h incubation, cell viability kept above 90%. Even after incubation for 48 h, low cytotoxicity of LA-g-QC copolymer was shownin vitro (Cell viability > 85%). This result was consistent with the reported cytotoxicity of chitosan-based polymeric micelles, which showed that treatment with 15.6 μg/mL of hydrophobically modified sulfated chitosan for 48 h made approximately 90% of HepG2 cells survive [18]. This result would provide evidences for the low biological toxicity and application potential of LA-g-QC micelles in biomedical field.Figure 6
Cytotoxicity of LA-g-QC micelles against HepG2 and SMMC 7721 cells after 24 h (a) and 48 h (b) incubation.
(a)
(b)


## 4. Conclusion

In this study, a novel amphiphilic chitosan derivative, LA-g-QC copolymer, has been synthesized and characterized. The micelles are spheroids with a narrow size distribution of approximately 136.5 nm. With a merit of low CMC comparing to other similar CMCs-based micelle systems, LA-g-QC has a high potential to form self-organized liposomes.In vitro study further indicated that the cytotoxicity of LA-g-QC copolymer was low, presenting a possibility in advancing the application of LA-g-QC copolymer. Collectively, the findings of our study suggest that LA-g-QC exhibits good properties as micelles.



---

*Source: 568925-2015-08-31.xml*