# A Study on Contact Fatigue Performance of Nitrided and TiN Coated Gears

Authors: Hongbin Xu; Hui Li; Jianjun Hu; Song Wang
Journal: Advances in Materials Science and Engineering
 (2013)

---

## Abstract

This paper discusses the effects of TiN coating on gear contact fatigue performance through contact fatigue experiment and gear rig test. The results reveal that the deposition on gears with hard coating TiN could provide the subsurface protection and improve the contact fatigue life, and the contact fatigue strength of nitrided+TiN coated 32Cr2MoV is 1557 MPa at survival probability of 99%, 284 MPa higher than that of nitrided 32Cr2MoV. Although TiN coating on the the edge of the meshing zone wore out, there is no obvious pitting at the site and the rest of  meshed zone of TiN coated gear keeps well without pittings and wear grooves, which is opposite to nitrided gears with pittings and peeling off. TiN coating is dense and smooth with lower surface roughness, and it wraps up the gear tooth so that the gear surface no longer contacts with lubricant and prevents the cracks initiation, prolonging the contact fatigue life of gears.


---

## Body

## 1. Introduction

The development in trend of gears, focusing on high-speed, heavy-duty, light weight, and small sizes, makes hardness promotion of gear face through traditional surface treatment and improvement of the bearing capacity of gears by enlarging module faces many limitations. Special work conditions require new type of surface strengthening methods as well as new gear materials with high performance. The hard thin coatings with lower friction and higher wear-resistance, for instance, MoS2 [1], DLC [2], WC/C [3, 4], TiN [5, 6], or the others [5, 7], have been studied for enhancing the surface contact fatigue life. In most cases, the effects of hard coatings on rolling contact fatigue have been mainly investigated by using a roller tester, pin-on-ring tester, three ball-on-rod tester, and so on, which reveals that coatings deposited by PVD could improve the wear resistance and contact fatigue life of substrate. However, it is not always easy to evaluate the tribological properties of tooth surface in meshingly using these fundamental testers [8, 9].Among the common ceramic coatings, the titanium nitride (TiN) is featured by excellent wear-resistance, low friction against metals, and more mature technology, making it widely used in tool and die industry [10, 11]. To confirm the effects of surface engineering on load carrying capacity of gears, this paper dwelled on load carrying capacity of nitrided and TiN deposited gears by means of contact fatigue experiment and gear rig test; additional tooth surface failure was investigated.


## 2. Experiment Details

According to Chinese Standard, 32Cr2MoV whose composition was reported in Table1 was selected to proceed with the experiment, and the geometrical characteristic of gears used in test was presented in Table 2. Heat treatments of samples were as follows: (1) austenitizing at 940°C for 1 h, (2) oil cooling to room temperature, and (3) heating up to 640°C and holding for 1.5 h, then air cooling. After tempering and machining, all samples have been plasma nitrided at 530°C~550°C for 20 hours.Table 1
The composition of 32Cr2MoV (Wt/%).
Material
C
Si
Mn
Cr
Mo
V
32Cr2MoV
0.30~0.34
0.34~0.38
0.48~0.60
2.10~2.23
1.3~1.6
0.24Table 2
Gear specification.
Gear type
Tooth profile
Accuracy
Module/mm
Number of teeth
Pressure angle
Surface hardness
Drive gears
Standard involutes
5
1.75
17
20°
>HRC 58
Driven gears
5
1.75
32
>HRC 58To synthesize the TiN coating by multi-arc ion plating, the work chamber was first vacuumed to pressure of6.67×10-4 Pa, and then Ar gas was introduced into the chamber to clean the workpiece surface by sputtering for 5 minutes. A DC bias voltage 200 V was applied on the Ti target to motivate the ionic Ti coated on the surface for 3 minutes. Then, N2 of 4.0×10-1 Pa work pressure was introduced into the chamber to deposit the TiN film onto the nitrided substrate.Technical specification of samples and fatigue experiment procedure followed the experiment method of metal line contact rolling fatigue (Chinese National Standard GB10622-89). The fatigue experiment conditions were as follows: the four stress levels were 2500 MPa, 2200 MPa, 2000 MPa, and 1800 MPa, slip ratio was 10%, the rotational speed of drive samples was 1400 r/min, temperature of lubricant kept <40°C. The five valid samples were chosen at every stress level to achieve the accurate numbers of cycles.After the contact fatigue strength was obtained by contact fatigue experiment, the load carrying capacity of TiN coated gears has been analyzed by means of gear rig contact test; the conditions were as shown in Table3.Table 3
Operating conditions in gear test.
TorqueT/N·m
Rotational speed R r/min
Normal loadL/N
Contact stressσ/MPa
Timet/h
16.71
2000
1250
1235
84The failure surface of gears was firstly examined by stereomicroscope and microscope, in particular the fracture surfaces prior to being observed by scanning electron microscopy (SEM). Also, the surface roughness of gears was measured.


## 3. Results and Discussion

The numbers of cycles in different contact stress levels for the nitrided and nitrided+TiN coated samples were presented in Table4, which illustrated that the numbers of cycles of nitrided+TiN coated samples were larger than those of nitrided samples under the same failure criterion and experimental condition.Table 4
Contact fatigue life of gears under different contact stress levels.
Contact stressσ/MPa
Contact fatigue lifeN/×105
Nitreded and TiN coated 32Cr2MoV
Nitrided 32Cr2MoV
2500
1.45
1.74
9.56
1.51
1.17
1.23
1.34
1.01
1.31
1.06
2200
4.94
4.66
5.44
5.18
4.65
3.88
3.31
3.97
3.92
3.10
2000
13.85
11.46
16.01
15.72
14.22
6.92
5.77
7.51
7.23
7.04
1800
49.75
53.85
50.72
47.86
43.75
19.91
22.63
21.73
17.86
16.40By analyzing numbers of cycles with Fixed Emitting Point Method-An Accelerated Test Program [12], fatigue curves of different survival ratio from the test gears have been drawn and fatigue limit was acquired, as shown in Figure 1. The P-S-N curve indicated that the fatigue life and the increment of fatigue lives of nitrided+TiN coated samples were higher than those of the nitrided samples with the descending of stress levels. It was obvious that TiN coating could provide the subsurface protection and that properties of high cycle fatigue of nitrided samples could be improved by deposition of TiN. The contact fatigue strength of nitrided+TiN 32Cr2MoV is 284 MPa higher than that of nitrided 32Cr2MoV.99% survival probability P-S-N curves.
(a)
Nitrided 32Cr2MoV
(b)
Nitrided+TiN coated 32Cr2MoVFigure2 was the photograph of gear surface before gear rig contact test at contact stress 1235 Mpa. Both tooth faces with different surface treatment showed the uniform state without the scratches and defects.Tooth surface before gear rig contact test.
(a)
Nitrided+TiN coated 32Cr2MoV
(b)
Nitrided 32Cr2MoVAfter long time running test, there was significant comparison between the two kinds of tooth faces, which was demonstrated by Figure3. It could be seen that the fatigue load obviously damaged the nitrided gears surfaces, and base metal is exposed with deep scratches, grooves, and spallings on tooth surface. As a distinction, nitrided+TiN coated gears were in good conditions relatively with less Horizontal grooves than the nitrided gears, few scratches and grooves were observed on nitrided+TiN coated driven gears, but it could be found that TiN coatings of driving gears on the edge of meshed zone were peeling off. There were some indentations on the nitrided+TiN coated driven gears but meshing zone kept original color and luster without the TiN coating peeling off. Marco-observation of tooth surface showed that TiN coating could increase the wear-resistance and resistance to contact fatigue.The macrophotograph of tooth surface after running test.
(a)
Nitrided driving gears
(b)
Nitrided driven gears
(c)
Nitrided+TiN coated driving gears
(d)
Nitrided+TiN coated driven gearsThe results of gears surfaces magnified 50 times were shown in Figure4. Long time running caused serious fatigue wear on nitrided gear surface which emerged in forms of pitting and grooves. However, few pitting were observed on the nitrided+TiN coated gears, and wear of gear surface was too slight to exhaust the TiN coatings. According the gear status without TiN peeling off in Figure 4(d), The circle concave should not be pittings, which revealed that wear of TiN was uniform during the gear test.The photograph of tooth surface after running test magnified 50 times.
(a)
Nitrided driving gears
(b)
Nitrided driven gears
(c)
Nitrided+TiN coated driving gears
(d)
Nitrided+TiN coated driven gearsThe area of pitch line and edge of meshed zone of nitrided gears were investigated by SEM, as shown in Figure5. All of the gears at the pitch line have the serious superficial injury, whose characteristics were also the fine pits and scratches with direction along the flank profiles (Figures 5(a) and 5(c)), while on the edge of the meshing zone there were obviously large areas of peeling off (Figures 5(b) and 5(d)). The SEM micrograph and EDS results of nitrided+TiN gears are shown in Figure 6. The peeling off of TiN coated gears was less than that of nitrided gears, and TiN coatings on pitch line still existed and were covered on the tooth surface. However substrate exposed on the edge of meshed zone, which revealed that TiN coatings have peeling off. an explanation for this phenomenon was contact interference of gear shape between driven gears and drive gears [8, 13]. Furthermore, the residual TiN coatings of all nitrided+TiN gears maintained a uniform state and color, without the wear scar and plowing grooves along the tooth profile, which sharply contrasted with the nitrided gears. The EDS results of coated gears were consistent with previous analysis. Normally, the element Fe could not be detected by EDS after TiN coatings have been deposited onto surface, which misfits the result of Figure 6 and demonstrates that wear of TiN coating has occurred during the gear running. The content of Ti and Fe in the different area revealed that wear of TiN on the edge of meshed zone was more severe than that on the pitch line zone. After running test some round spots and strip pits, the size of which was larger than that of the liquid-drop spots within 10 μm found in the TiN surface by different PVD technology were observed on the TiN coated driven gears (Figures 3(d) and 4(d)). However, morphology of spots and strip pits was quite different from the warp or bulge of film and similar to the indentation, showing that the TiN coating has good toughness and deformation capacity. The indentation illustrated that the driven gear surface was deformed during the repeated sliding and rolling, and the deformed material will rapture if the accumulated strain exceeds the critical value of plastic strain [14]. The failure characteristic of TiN coated gears was consistent with contact fatigue of traditional hardened gears, but TiN could improve the contact fatigue performance.The SEM micrograph of nitrided gears after running test.
(a)
Pitch line of driving gear
(b)
Edge of meshed zone of driving gear
(c)
Pitch line of driven gear
(d)
Edge of meshed zone of driven gearFigure 6
The SEM micrograph of nitrided+TiN gears after running test; (a) pitch line of driving gear, (b) edge of meshed zone of driving gear, (c) pitch line of driven gear, and (d) edge of meshed zone of driven gear.The observation of nitrided gears is consistent with gear failure rules: pittings usually occur on the site near tooth root and below the pitch line, and it is easier for generating pittings on the driving gears than driven gears; additionally heavy load may cause spalling [15, 16]. Compared with the severe tooth damage of all nitrided gears, the TiN coated gears show an excellent resistance of pitting and spalling. TiN coatings within thickness 3 μm still remain on the most of gear surface, which demonstrated wear of TiN coated gears is slighter. On the basis of the contact fatigue model, main failure type of hardened gears is pitting owing to its shallower nitride case and important role of surface cracks. Micro cracks caused by surface machining and repeated plastic deformation interact with lubricant and result in nucleation and propagation of fatigue cracks [8, 14, 15]. Deposition with TiN coating wrapped up the gear tooth so that the gear surface no longer contacts with lubricant and prevents the cracks initiation; furthermore, brittle TiN coating combined with hard case may weaken the surface plastic deformation, prolonging the contact fatigue life of gears. After the TiN coating wore out, the conditions of nitrided+TiN gears are the same as nitrided gears, and pitting process is similar to nitrided gears.The changes in surface roughness also reflected the wear of gears, as shown in Figure7. The surface roughness of nitrided gears increased to about ΔRa 0.6~0.7 μm, which indicated that pitting destroyed the smoothness of nitrided gears. Reversely, surface roughness Ra of TiN coated gears decreased, making tooth surface smoother, and helping reduce the friction and wear, and improving and inhibiting pitting of gears.Figure 7
Surface roughness of gears.


## 4. Conclusions

From the previous discussion, the conclusion can be summarized as follows.(1)
The deposition on gears by hard coating TiN can provide subsurface protection and improve the contact fatigue life. The contact fatigue strength of nitrided+TiN coated 32Cr2MoV is 1557 Mpa at survival probability of 99%, and it is 284 MPa higher than that of nitrided 32Cr2MoV.(2)
Due to the protection of TiN coatings with good toughness and deformation capacity, feature of gear surface fatigue exhibit indentation instead of pittings, which is different from the pittings and liquid-drop spots within 10μm found in the TiN deposition. The meshing zone of coated TiN gear face keeps well basically without pittings and wear grooves, which is opposite to nitrided gears with pittings and peeling off. Even on the edge of the meshing zone TiN coatings have been worn out, the gear face kept well without pittings. The surface of the TiN coating is dense and smooth with lower surface roughness, and it wraps up the gear tooth so that the gear surface no longer contacts with lubricant and prevents the cracks initiation. During the running test, surface roughness of TiN coated gears decreased, making tooth surface smoother and helping reduce the friction and wear, improving contact fatigue properties.



---