# Effects of Zinc Oxide Nanoparticles on the Properties of Pectin/Alginate Edible Films

Authors: Thi Minh Phuong Ngo; Thi Mong Quyen Dang; Thi Xo Tran; Pornchai Rachtanapun
Journal: International Journal of Polymer Science
 (2018)

---

## Abstract

This study aimed at developing the functional packaging properties of pectin/alginate films by adding zinc oxide nanoparticles (ZnO-NPs). The ZnO-NPs were added to the pectin/alginate film at the concentrations of 0.5, 2.5, 5, and 25 g/100 g of blended polymer. The effects of the ZnO-NP incorporation on the mechanical properties, hydration properties, oxygen permeability, ultraviolet transmission, transparency, and antimicrobial activity of the films were investigated. The addition of ZnO-NPs from 0 to 5 g/100 g of blended polymer to the pectin/alginate film increased 191.4% of the tensile strength, 169.8% of elongation at break, and antimicrobial properties (againstAspergillus niger, Colletotrichum gloeosporioides, Escherichia coli, and Saccharomyces cerevisiae). In contrast, it reduced the solubility from 30.38% to 22.49%, water vapor permeability from 1.01 × 10−14 to 0.414 × 10−14 kg·m/m2·Pa·s, moisture absorption, ultraviolet light transmission, and oxygen permeability from 270.86 × 10−19 to 110.79 × 10−19 kg·m/m2·Pa·s. The effects are the highest when the concentration of the ZnO-NPs in the film was 5 g/100 g of blended polymer. Attenuated total reflectance-Fourier transform infrared analysis indicated that some interactions between the ZnO-NPs and pectin/alginate matrices were formed. These results suggest that pectin/alginate/ZnO-NPs films can be used as active packaging for food preservation.


---

## Body

## 1. Introduction

Food packaging materials with proper mechanical strength; barrier properties against water, water vapor, and other gases; thermal stability, recyclability, and biodegradability; and functional properties, such as antimicrobial activities, are highly desirable for food safety and extending the shelf-life of packaged foods [1]. However, biopolymer-based packaging materials have not been widely used in the packaging industry, mainly because of their poor mechanical, barrier, and processing properties. They also have a higher production cost compared to commodity plastic films [2]. Edible films are increasingly used in food preservation, and they are largely produced from nontoxic polysaccharide sources. Among various polysaccharides, pectin and alginate are particularly attractive due to their good film-forming property, moderate mechanical strength, and gas barrier properties with a unique colloidal nature. Recently, zinc oxide nanoparticles (ZnO-NPs) have become well known for their antimicrobial and UV-light barrier properties. The addition of ZnO-NPs to biopolymers has improved the film’s properties and showed strong antimicrobial and UV barrier properties [3]. For these reasons, ZnO-NPs have been applied to food packaging. However, the antimicrobial activity and membrane properties will depend on the amount of ZnO-NPs used. Therefore, the main purpose of this study was to develop pectin/alginate films by mixing ZnO-NPs with different contents and evaluate the effect of them on the properties of the film.


## 2. Materials and Methods

### 2.1. Materials and Sample Preparation

Sodium alginate (AG), with a molecular weight (Mw) of 1.2 × 106 Da, was purchased from Lianyungang Zhongda Seaweed Industrial Co. Ltd. (China). Glycerol and calcium chloride were purchased from Xilong Co. Ltd., China. The BHI medium was purchased from Sigma-Aldrich (St. Louis, USA).The pectin (P) powder and ZnO-NPs were obtained at the LAB of the University of Technology and Education, which belongs to the University of Danang, Vietnam.The pectin powder was extracted from Yanang leaves using a heating method with an optimum temperature of 88°C and time of 75minutes and in a 6.5% citric acid solution. The extracted mixture was precipitated with 96% ethanol. Then, the mixture was centrifuged (4000 rpm for 10 min) and washed three times with 96% ethanol. The pectin precipitate was dried at 60°C, and the dried pectin was ground into a flour. The degree of methyl esterification (DE) measurement value was 48.36, and theMw measurement value was 111,105 Da.The ZnO-NPs were synthesized by the following sol-gel method: First, 1.1 g of Zn(CH3COO)2·2H2O was dissolved with 50 ml diethylene glycol. The mixture was stirred continuously for one hour at 80°C. Then, 50 ml of a 0.1 M LiOH solution was added to the solution. After stirring for 5 minutes at 80°C, the white precipitate formed. The mixture was centrifuged (4000 rpm for 10 minutes) and washed three times with distilled water and then washed three times with 96% ethanol to remove the nonreactive and excess ions. The size of ZnO-NPs was from 20 to 40 nm (Figure 1).Figure 1
(a) SEM photographs of ZnO-NPs at magnification of 25,000x and (b) TEM photographs of ZnO-NPs at magnification of 125,000x.
(a)
(b)The pectin/alginate film-forming aqueous solutions were prepared with 2%w/v at the proportion of pectin : alginate 1 : 1 w/w. Powdered calcium chloride was used at 0.01 g/g polymer and glycerol as a plasticizer at 50% (% w/w of polymer), and both were blended into the pectin-alginate film-solution. The ZnO-NPs were added in the pectin/alginate films with glycerol and fabricated with four levels of ZnO-NPs, namely, 0.5, 2.5, 5, and 25 g/100 g of blended polymer. The mixture was homogenized using a homogenizer at speed of 400 rpm in 15 minutes, and after that, it was stored at 4°C and 90% RH for degassing. To control the film thickness, the volume of each film-forming solution poured into a 15 cm × 15 cm mold was always 60 g. Films were dried at 25°C and at 52 ± 1% relative humidity (RH) for 24 h by using a fan at speed of 1500 rpm.The dried films were removed from the mold and dipped in 5% CaCl2 solution for 20 min to enable cross-linking [4]. Films were dried at 40°C for two hours in the oven (UFE 500, Memmert). Films were stored at 52 ± 1% RH and 25 ± 1°C for 5 days prior to testing.


### 2.2. Thickness

The thickness of the films was measured using a Mitutoyo Dial Thickness Gauge (Model PCM 137, No. 2046S, Japan) with an accuracy of 0.01 mm at 10 random positions for each film. The average standard deviation was about 5% of the average thickness. The tests were repeated three times.


### 2.3. Tensile Property Measurements and % Elongation at Break

The tensile properties and % elongation at break of the samples were measured using an Instron 1141 (Instron Ltd., Canton, USA) with the procedure according to ASTM D882-10 [5]. The samples were prepared as sheets using a gauge length and width of 100 mm and 25 mm, respectively. The initial grip separation was set at 125 mm/min. The elongation at break was calculated by dividing the elongation at the moment of rupture by the initial gauge length and multiplying by 100. The samples were conditioned at 52 ± 1% RH and 25°C for 48 h prior to testing. There were ten sample measurements.


### 2.4. Film Solubility

The films were cut into square 1 cm × 1 cm pieces and dried to a constant weight in a vacuum oven at 60°C for 24 hours to obtain the initial film dry weight (Wd). Each film was then placed in a bottle containing 20 ml distilled water for 24 hours under gentle agitation and controlled temperature at 25°C. The films were then dried under the same conditions to obtain the dry weight of water-leached film (Wws). The tests were performed in triplicate. The film solubility was calculated using
(1)%solubility=Wd−WwsWd×100.


### 2.5. Water Contact Angle

Drop shape analysis (DSA30E, Krüss Co. Ltd., Germany) was used to observe the water contact angle. The samples were prepared as sheets with a dimension of 1 cm × 5 cm. Water was dropped onto the surface of the sheets, and images were taken automatically every 20 s for 2 min. Samples were kept at 25°C and 52 ± 1% RH at least 48 h prior to testing. The measurements were average from three samples for each formulation [6].


### 2.6. Water Vapor Permeability (WVP) and Water Vapor Transmission Rate (WVTR)

The WVP of the films was measured gravimetrically at 25 ± 1°C according to ASTM E96-00 (ASTM, 2000). Film specimens with an approximately 8 cm diameter were mounted on the aluminum cups containing 10 g of silica gel. Paraffin was used to fix the film specimen on the wide rim of an aluminum cup [7]. The sealed cups were then weighed and kept in desiccators with a saturated solution of Mg(NO3)2 salt that provided 52 ± 1% RH at 25 ± 1°C throughout the experiment. The weight gain of the aluminum cups covered with the films was recorded every 10 hours for 5 days [8]. All tests were conducted in triplicate. The WVP and WVTR were calculated using
(2)WVP=w·xt·A·Po·RH1−RH2kg·m/Pa·m2·s,(3)WVTR=wt·Akg/m2·s,where w/t is the permeation rate (g/day) that was calculated by a linear regression of the mass gain versus time (R2>0.99), x is the film average thickness (mm), A is the permeation area (23.76 cm2), Po is the partial water vapor pressure at test temperature (3159 kPa at 25°C), and (RH1 − RH2) is the difference in relative humidity between the two sides of the film [9].


### 2.7. Moisture Sorption Isotherm

The films were cut into a 3 cm × 3 cm squares and dried in a hot air oven at 105°C for 3 h before being placed in desiccators containing dried silica gel for 2 days. The specimens were then placed in several different desiccators containing various kinds of saturated salt solutions to maintain the constant relative humidity at 11.2%, 33.5%, 53.1%, 64.8%, 75.1%, 85.5%, and 93.7%. A cotton wool soaked with 96% ethanol was used as a fungistatic agent in the desiccators containing the salt solutions with a high relative humidity. The specimens were weighed daily until equilibrium was obtained. Equilibrium was achieved when the change in weight did not exceed 0.1% after being weighed for three consecutive times. The equilibrium moisture content (EMC) (g water/100 g dry solid) of the films at each relative humidity was calculated using(4)EMC=WeWiMi+1−1,where We is the equilibrium weight of the film specimen (g), Wi is the initial weight of the film specimen (g), and Mi is the initial moisture content of the film specimen (g water/100 g dry solid) [10, 11]. All measurements were performed in triplicate.


### 2.8. Transparency and Light Transmission of Films

Each film sample was cut into a rectangular piece and directly mounted between two spectrophotometer magnetic cells. The transparency and light transmission of the films were measured at selected wavelengths between 320 and 800 nm using a UV-Vis spectrophotometer (Model 8451A, Hewlett-Packard Co., Santa Clara, CA, USA). The film transparency was calculated with(5)Transparency=−logT600x1/mm,where T600 is the fractional transmittance at 600 nm and x is the film thickness (mm) [12].


### 2.9. Oxygen Permeability and Oxygen Transmission Rate

The oxygen permeability (OP) and oxygen transmission rate (OTR) were measured using a Mocon Instruments tool (OX-TRAN® Model 2/21 Series, Mocon Inc., USA). The measurements were taken using 6 cm × 6 cm film samples at 23 ± 2°C, 75% RH, and 760 mmHg following the standard method [13]. The results are the average over at least three replicate measurements. The OP was calculated by
(6)OP=OTR·lΔPkg·m/Pa·m2·s,where OTR is the value of oxygen transmission rate, l is the thickness of the film, and ΔP is the difference between oxygen partial pressures between the two sides of the film (Pa).


### 2.10. Antimicrobial Action of Film-Forming Solutions

The antimicrobial activities of the film-forming solutions incorporating the ZnO-NPs were evaluated by the well diffusion method in agar againstE. coli, Saccharomyces cerevisiae, Colletotrichum gloeosporioides, and Aspergillus niger. The microorganisms were prepared for the test as follows: E. coli was aseptically inoculated in BHI broth and subsequently incubated at 37°C for 16 h. Saccharomyces cerevisiae, Aspergillus niger, and Colletotrichum gloeosporioides were aseptically inoculated in Sabouraud broth and subsequently incubated at 30°C for 16 h. The evaluation process was as follows: The Sabouraud agar medium was used for S. cerevisiae, Aspergillus niger, and Colletotrichum gloeosporioides, and the BHI agar medium was used for E. coli. All were poured into petri dishes. After solidification, wells at 5 mm in diameter were cut from the agar and 0.1 ml of the film-forming solution was carefully poured inside. Next, a 1 ml suspension containing 106 CFU/ml of each investigated microorganism was spread in the specific agar medium. After incubating for 48 h at 30°C for S. cerevisiae, Aspergillus niger, and Colletotrichum gloeosporioides and 48 h at 37°C for E. coli, all plates were inspected. The diameters of the inhibition zones were measured (in cm) with a ruler on the underside of the petri dish. For example, the image that showed the antibacterial activity of film-forming solution against E. coli is shown in Figure 2. All measurements were performed in triplicate [14, 15].Figure 2
Evaluation image of antibacterial action by the “zone inhibition method.”


### 2.11. Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) Spectroscopy

The reaction between the pectin, alginate, and ZnO-NPs was monitored by ATR-FTIR (Thermo Nicolet 6700, USA). The samples were prepared as thin films (about 60μm). The IR spectra were measured at wavelengths from 500 cm−1 to 4000 cm−1 and with a resolution of 4 cm−1.


### 2.12. Statistical Analysis

Statistics were determined with a completely randomized design with an analysis of variance (ANOVA) using Minitab software (version 16.2.3.0; Minitab Inc., USA). Fisher’s tests were used to compare the difference among the mean values of the film specimens’ properties at the level of 0.05. All experiments were conducted in triplicate.


## 2.1. Materials and Sample Preparation

Sodium alginate (AG), with a molecular weight (Mw) of 1.2 × 106 Da, was purchased from Lianyungang Zhongda Seaweed Industrial Co. Ltd. (China). Glycerol and calcium chloride were purchased from Xilong Co. Ltd., China. The BHI medium was purchased from Sigma-Aldrich (St. Louis, USA).The pectin (P) powder and ZnO-NPs were obtained at the LAB of the University of Technology and Education, which belongs to the University of Danang, Vietnam.The pectin powder was extracted from Yanang leaves using a heating method with an optimum temperature of 88°C and time of 75minutes and in a 6.5% citric acid solution. The extracted mixture was precipitated with 96% ethanol. Then, the mixture was centrifuged (4000 rpm for 10 min) and washed three times with 96% ethanol. The pectin precipitate was dried at 60°C, and the dried pectin was ground into a flour. The degree of methyl esterification (DE) measurement value was 48.36, and theMw measurement value was 111,105 Da.The ZnO-NPs were synthesized by the following sol-gel method: First, 1.1 g of Zn(CH3COO)2·2H2O was dissolved with 50 ml diethylene glycol. The mixture was stirred continuously for one hour at 80°C. Then, 50 ml of a 0.1 M LiOH solution was added to the solution. After stirring for 5 minutes at 80°C, the white precipitate formed. The mixture was centrifuged (4000 rpm for 10 minutes) and washed three times with distilled water and then washed three times with 96% ethanol to remove the nonreactive and excess ions. The size of ZnO-NPs was from 20 to 40 nm (Figure 1).Figure 1
(a) SEM photographs of ZnO-NPs at magnification of 25,000x and (b) TEM photographs of ZnO-NPs at magnification of 125,000x.
(a)
(b)The pectin/alginate film-forming aqueous solutions were prepared with 2%w/v at the proportion of pectin : alginate 1 : 1 w/w. Powdered calcium chloride was used at 0.01 g/g polymer and glycerol as a plasticizer at 50% (% w/w of polymer), and both were blended into the pectin-alginate film-solution. The ZnO-NPs were added in the pectin/alginate films with glycerol and fabricated with four levels of ZnO-NPs, namely, 0.5, 2.5, 5, and 25 g/100 g of blended polymer. The mixture was homogenized using a homogenizer at speed of 400 rpm in 15 minutes, and after that, it was stored at 4°C and 90% RH for degassing. To control the film thickness, the volume of each film-forming solution poured into a 15 cm × 15 cm mold was always 60 g. Films were dried at 25°C and at 52 ± 1% relative humidity (RH) for 24 h by using a fan at speed of 1500 rpm.The dried films were removed from the mold and dipped in 5% CaCl2 solution for 20 min to enable cross-linking [4]. Films were dried at 40°C for two hours in the oven (UFE 500, Memmert). Films were stored at 52 ± 1% RH and 25 ± 1°C for 5 days prior to testing.


## 2.2. Thickness

The thickness of the films was measured using a Mitutoyo Dial Thickness Gauge (Model PCM 137, No. 2046S, Japan) with an accuracy of 0.01 mm at 10 random positions for each film. The average standard deviation was about 5% of the average thickness. The tests were repeated three times.


## 2.3. Tensile Property Measurements and % Elongation at Break

The tensile properties and % elongation at break of the samples were measured using an Instron 1141 (Instron Ltd., Canton, USA) with the procedure according to ASTM D882-10 [5]. The samples were prepared as sheets using a gauge length and width of 100 mm and 25 mm, respectively. The initial grip separation was set at 125 mm/min. The elongation at break was calculated by dividing the elongation at the moment of rupture by the initial gauge length and multiplying by 100. The samples were conditioned at 52 ± 1% RH and 25°C for 48 h prior to testing. There were ten sample measurements.


## 2.4. Film Solubility

The films were cut into square 1 cm × 1 cm pieces and dried to a constant weight in a vacuum oven at 60°C for 24 hours to obtain the initial film dry weight (Wd). Each film was then placed in a bottle containing 20 ml distilled water for 24 hours under gentle agitation and controlled temperature at 25°C. The films were then dried under the same conditions to obtain the dry weight of water-leached film (Wws). The tests were performed in triplicate. The film solubility was calculated using
(1)%solubility=Wd−WwsWd×100.


## 2.5. Water Contact Angle

Drop shape analysis (DSA30E, Krüss Co. Ltd., Germany) was used to observe the water contact angle. The samples were prepared as sheets with a dimension of 1 cm × 5 cm. Water was dropped onto the surface of the sheets, and images were taken automatically every 20 s for 2 min. Samples were kept at 25°C and 52 ± 1% RH at least 48 h prior to testing. The measurements were average from three samples for each formulation [6].


## 2.6. Water Vapor Permeability (WVP) and Water Vapor Transmission Rate (WVTR)

The WVP of the films was measured gravimetrically at 25 ± 1°C according to ASTM E96-00 (ASTM, 2000). Film specimens with an approximately 8 cm diameter were mounted on the aluminum cups containing 10 g of silica gel. Paraffin was used to fix the film specimen on the wide rim of an aluminum cup [7]. The sealed cups were then weighed and kept in desiccators with a saturated solution of Mg(NO3)2 salt that provided 52 ± 1% RH at 25 ± 1°C throughout the experiment. The weight gain of the aluminum cups covered with the films was recorded every 10 hours for 5 days [8]. All tests were conducted in triplicate. The WVP and WVTR were calculated using
(2)WVP=w·xt·A·Po·RH1−RH2kg·m/Pa·m2·s,(3)WVTR=wt·Akg/m2·s,where w/t is the permeation rate (g/day) that was calculated by a linear regression of the mass gain versus time (R2>0.99), x is the film average thickness (mm), A is the permeation area (23.76 cm2), Po is the partial water vapor pressure at test temperature (3159 kPa at 25°C), and (RH1 − RH2) is the difference in relative humidity between the two sides of the film [9].


## 2.7. Moisture Sorption Isotherm

The films were cut into a 3 cm × 3 cm squares and dried in a hot air oven at 105°C for 3 h before being placed in desiccators containing dried silica gel for 2 days. The specimens were then placed in several different desiccators containing various kinds of saturated salt solutions to maintain the constant relative humidity at 11.2%, 33.5%, 53.1%, 64.8%, 75.1%, 85.5%, and 93.7%. A cotton wool soaked with 96% ethanol was used as a fungistatic agent in the desiccators containing the salt solutions with a high relative humidity. The specimens were weighed daily until equilibrium was obtained. Equilibrium was achieved when the change in weight did not exceed 0.1% after being weighed for three consecutive times. The equilibrium moisture content (EMC) (g water/100 g dry solid) of the films at each relative humidity was calculated using(4)EMC=WeWiMi+1−1,where We is the equilibrium weight of the film specimen (g), Wi is the initial weight of the film specimen (g), and Mi is the initial moisture content of the film specimen (g water/100 g dry solid) [10, 11]. All measurements were performed in triplicate.


## 2.8. Transparency and Light Transmission of Films

Each film sample was cut into a rectangular piece and directly mounted between two spectrophotometer magnetic cells. The transparency and light transmission of the films were measured at selected wavelengths between 320 and 800 nm using a UV-Vis spectrophotometer (Model 8451A, Hewlett-Packard Co., Santa Clara, CA, USA). The film transparency was calculated with(5)Transparency=−logT600x1/mm,where T600 is the fractional transmittance at 600 nm and x is the film thickness (mm) [12].


## 2.9. Oxygen Permeability and Oxygen Transmission Rate

The oxygen permeability (OP) and oxygen transmission rate (OTR) were measured using a Mocon Instruments tool (OX-TRAN® Model 2/21 Series, Mocon Inc., USA). The measurements were taken using 6 cm × 6 cm film samples at 23 ± 2°C, 75% RH, and 760 mmHg following the standard method [13]. The results are the average over at least three replicate measurements. The OP was calculated by
(6)OP=OTR·lΔPkg·m/Pa·m2·s,where OTR is the value of oxygen transmission rate, l is the thickness of the film, and ΔP is the difference between oxygen partial pressures between the two sides of the film (Pa).


## 2.10. Antimicrobial Action of Film-Forming Solutions

The antimicrobial activities of the film-forming solutions incorporating the ZnO-NPs were evaluated by the well diffusion method in agar againstE. coli, Saccharomyces cerevisiae, Colletotrichum gloeosporioides, and Aspergillus niger. The microorganisms were prepared for the test as follows: E. coli was aseptically inoculated in BHI broth and subsequently incubated at 37°C for 16 h. Saccharomyces cerevisiae, Aspergillus niger, and Colletotrichum gloeosporioides were aseptically inoculated in Sabouraud broth and subsequently incubated at 30°C for 16 h. The evaluation process was as follows: The Sabouraud agar medium was used for S. cerevisiae, Aspergillus niger, and Colletotrichum gloeosporioides, and the BHI agar medium was used for E. coli. All were poured into petri dishes. After solidification, wells at 5 mm in diameter were cut from the agar and 0.1 ml of the film-forming solution was carefully poured inside. Next, a 1 ml suspension containing 106 CFU/ml of each investigated microorganism was spread in the specific agar medium. After incubating for 48 h at 30°C for S. cerevisiae, Aspergillus niger, and Colletotrichum gloeosporioides and 48 h at 37°C for E. coli, all plates were inspected. The diameters of the inhibition zones were measured (in cm) with a ruler on the underside of the petri dish. For example, the image that showed the antibacterial activity of film-forming solution against E. coli is shown in Figure 2. All measurements were performed in triplicate [14, 15].Figure 2
Evaluation image of antibacterial action by the “zone inhibition method.”


## 2.11. Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) Spectroscopy

The reaction between the pectin, alginate, and ZnO-NPs was monitored by ATR-FTIR (Thermo Nicolet 6700, USA). The samples were prepared as thin films (about 60μm). The IR spectra were measured at wavelengths from 500 cm−1 to 4000 cm−1 and with a resolution of 4 cm−1.


## 2.12. Statistical Analysis

Statistics were determined with a completely randomized design with an analysis of variance (ANOVA) using Minitab software (version 16.2.3.0; Minitab Inc., USA). Fisher’s tests were used to compare the difference among the mean values of the film specimens’ properties at the level of 0.05. All experiments were conducted in triplicate.


## 3. Results and Discussion

### 3.1. Thickness and Mechanical Properties

The thickness and mechanical properties of the P/AG films with various ZnO-NP contents are presented in Table1. The thicknesses of the P/AG films that contain the ZnO-NPs is higher than for the P/AG only film. The increase in ZnO-NP content from 0 to 25 g/100 g of blended polymer led to an increase in the film thickness from 52.4 to 74.6 μm. The increase in the thickness was not only attributed to the higher solid content of nanocomposite films ZnO-NPs but also attributed to their structure. Similar results were reported by Shahmohammadi Jebel and Almasi [16].Table 1
Thickness and mechanical properties (tensile strength = TS; % elongation = %E) of P/AG films with various ZnO-NP contents.
ZnO-NP content (g/100 g of blended polymer)
Thickness (μm)
TS (MPa)
%E (%)
0
43.8 ± 2.11d
21.71 ± 1.23d
0.86 ± 0.04c
0.5
52.4 ± 2.5c
32.59 ± 1.6c
1.89 ± 0.05b
2.5
56.8 ± 2.83b
36.43 ± 0.98b
1.93 ± 0.05b
5
58.1 ± 2.08b
41.56 ± 1.94a
2.32 ± 0.06a
25
74.6 ± 3.25a
12.79 ± 0.58e
0.85 ± 0.04c
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.The tensile strength (TS) and % elongation at break (E) for the films with various ZnO-NP contents equilibrated at 25 ± 1°C and 52 ± 1% RH are shown in Table1. There was an increase in tensile strength from 21.71 to 41.56 MPa when increasing the ZnO-NP content from 0.5 to 5 g/100 g of blended polymer. On the other hand, the increase in the ZnO-NP concentration from 5 to 25 g/100 g of blended polymer reduced the tensile strength from 41.56 to 12.79 MPa. The tensile strength was the highest when the ZnO-NPs were added at a concentration of 5 g/100 g of blended polymer, where it reached 191.4% of the tensile strength for the P/AG film.The change in elongation is similar to that of tensile strength. Changes in tensile strength and elongation values may be due to the formation of hydrogen links between the pectin, alginate’s hydroxyl groups, and oxygen atoms in the ZnO-NPs [17, 18]. Moreover, a low concentration of ZnO-NPs had a negligible effect on the formation of hydrogen bonds between the OH and the COOH groups in the pectin/alginate matrix, as well as the formation of bonds between the Ca2+ and the COO− groups of the pectin and alginate chains. The pectin and alginate chains thereby adopted a structure that resembles an “egg-box” model.The decrease in TS and E of the film with 25 g ZnO-NPs/100 g polymer was probably due to agglomeration of the ZnO-NPs, the nonuniform distribution of the ZnO-NPs, and the recrystallization of the ZnO-NPs in the polymer matrix. These factors caused discontinuous cracks in the polymer matrix and resulted in a sudden decrease in the TS and E. A similar result was observed when adding CuO-NPs and ZnO-NPs into a carrageenan matrix [18].


### 3.2. Solubility and Water Contact Angle

The water contact angle (θ) is the most common parameter used to describe the hydrophilicity of film surfaces. Hydrophilic membranes possess a contact angle of 0° < θ < 90°, while hydrophobic membranes have a contact angle of 90° < θ < 180° [19]. Table 2 shows the solubility and water contact angle for the film specimens.Table 2
Effect of ZnO-NP contents on the solubility and water contact angle of P/AG films.
ZnO-NP contents (g/100 g of blended polymer)
Contact angle (°)
Solubility (%)
0
73.85 ± 6.4a
30.38 ± 1.3a
0.5
72.9 ± 4.5a
27.34 ± 1.8ab
2.5
72.5 ± 2.9a
23.16 ± 2.1b
5
70.73 ± 4.1a
22.49 ± 3.1b
25
54.07 ± 7.4b
26.1 ± 1.5ab
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.Results showed that adding ZnO-NPs to the P/AG film at the amount of 0.5 to 5 g/100 g of blended polymer did not significantly change the water contact angle. However, the water contact angle for the film-incorporated ZnO-NPs with 25 g/100 g of blended polymer was lower than the other films. Reducing the water contact angle may be due to an increase in surface roughness at high ZnO-NP concentrations.The solubility values for the specimens trended to the decrease with increasing ZnO-NP content, except for the ZnO-NP content of 25 g/100 g of blended polymer. These results indicate that the addition of the ZnO-NPs reduced the number of hydroxyl groups and charged groups (−COO−). Moreover, the length of the polymer increased due to the formation of links between the ZnO-NPs, pectin, and alginate. Consequently, the solubility of the films was reduced. The ZnO-NP content in the 25 g/100 g of blended polymer was more than necessary for creating hydrogen bonds such that it probably had a negative effect on the cross-linking between the Ca2+ ion, the pectin, and the alginate carboxyl groups. This increased the solubility value. Thus, the film solubility trended to increase when the ZnO-NP content was 25 g/100 g of blended polymer.


### 3.3. WVP and WVTR of P/AG Films

Table3 shows WVP and WVTR of film specimens. The WVP values of the specimens decreased from 1.01 to 0.414 kg·m/m2·Pa·s (59%), and WVTR values decreased from 4.226 to 1.486 kg/m2·s (64.8%), when increasing the ZnO-NP content from 0 to 5 g/100 g of blended polymer. This may be due to the formation of the hydrogen bonds between the pectin, alginate matrix, and oxygen atoms in the ZnO-NPs, which increases the adhesion of the biopolymer matrix and can reduce the diffusion of the water molecules in the material. A similar result was reported by Almasi et al. [20]. On the other hand, the even distribution of the ZnO-NPs with smaller sizes and filling of the microvoids should reduce the length of a free path for water uptake. Similar results were reported for the effect of ZnO-NPs on the WVP of biopolymer-based nanocomposites [3, 21]. There was no significant change in the WVP and WVTR values of the sample when increasing the content of the ZnO-NPs from 5 to 25 g/100 g of blended polymer, which may be due to the maximum reduction of the hydrophilic groups, such as OH and COOH in the polymer.Table 3
WVP and WVTR of P/AG films with various ZnO-NP contents.
ZnO-NP contents (g/100 g of blended polymer)
WVP × 10−14 (kg·m/m2·Pa ·s)
WVRT × 10−7 (kg/m2·s)
0
1.01 ± 0.029a
4.226 ± 0.121a
0.5
0.576 ± 0.018b
2.148 ± 0.069b
2.5
0.447 ± 0.008c
1.949 ± 0.035b
5
0.414 ± 0.02cd
1.486 ± 0.069c
25
0.381 ± 0.019d
1.437 ± 0.069c
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.


### 3.4. Moisture Sorption Isotherm

The moisture absorption of the P/AG film was higher than that of P/AG films with the ZnO-NPs in the range of water activity between 0.86 and 0.93 (Figure3). A similar result was reported by Galus and Lenart [22]. The film’s moisture absorption decreased as the ZnO-NP content increased. However, there was no significant change in the moisture absorption between the P/AG films and the P/AG films with the ZnO-NPs in the water activity range of 0 to 0.75. Based on the results obtained for the solubility, WVP, mechanical properties, and moisture sorption isotherm, it is recognized that these trends are due to the formation of hydrogen bonding between the OH groups of the pectin, alginate, and oxygen atoms of the ZnO-NPs. The reduction in moisture absorption may be due to the reduction of the free OH groups in the membrane. On the other hand, a uniform dispersion of smaller ZnO-NPs and filling of microvoids produces a decrease in the length of the free path for water uptake.Figure 3
Moisture sorption isotherms of P/AG films incorporated with various ZnO-NP contents at 25 ± 1°C.


### 3.5. Transparency and Light Transmission of Films

Figure4 shows the light transmission of film specimens. Light transmission decreases in the wavelength range of 320 to 350 nm (UV light) and reaches the lowest value at 350 nm. The light transmittance of films containing ZnO-NPs is always lower than that of films without the ZnO-NPs. The higher the ZnO concentration in the film, the lower the light transmission at the wavelength range of 320 to 350 nm. This result shows that ZnO-NPs in the film have absorbed ultraviolet light. This result is consistent with that of Khodaiyana et al. [23] who observed that the UV absorbance of the nanocomposite polymers increased as the ZnO-NP content increased. They also observed that a ZnO-Np content greater than 1% was necessary to induce UV filtration in a kefiran biopolymer. There is no significant difference in light transmittance between films containing ZnO-NPs and P/AG films in the wavelength range of 500 to 800 nm, except for P/AG films with a ZnO-NP content of 25 g/100 g of blended polymer.Figure 4
Light transmission of the films.Table4 shows the transparency of the films with various ZnO-NP contents. The transparency for the films containing 0.5 to 5 g/100 g blended polymer of ZnO-NPs was not significantly different from the P/AG film. However, the addition of ZnO-NPs with 25 g/100 g of blended polymer into the films decreased the transparency value. The reduction of transparency of the films with a concentration of 25 g ZnO-NPs/100 g polymer may be due to the over-distribution of the ZnO-NPs in the pectin/alginate network.Table 4
Transparency of P/AG films with various ZnO-NP contents.
ZnO-NP contents (g/100 g of blended polymer)
0
0.5
2.5
5
25
Transparency values (1/mm)
3.24 ± 0.02b
3.26 ± 0.01b
3.25 ± 0.03b
3.17 ± 0.02ab
3.01 ± 0.02a
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.


### 3.6. Oxygen Permeability and Oxygen Transmission Rate

The OP and OTR of P/AG and P/AG films with various ZnO-NP contents are presented in Table5.Table 5
OP and OTR of P/AG films with various ZnO-NP contents.
ZnO-NP contents (g/100 g of blended polymer)
OP × 10−19 (kg·m/m2·Pa·s)
OTR × 10−11 (kg/m2·s)
0
270.86 ± 9.79a
158.65 ± 16.17a
0.5
253.85 ± 15.35a
137.51 ± 6.95b
2.5
191.87 ± 12.44b
89.82 ± 3.68c
5
110.79 ± 7.74d
51.87 ± 3.98d
25
132.92 ± 7.45c
48.84 ± 3.55dThe addition of ZnO-NP to the P/AG films led to a reduced oxygen permeability. The lowest reduction occurred when the ZnO-NP concentration reached 5 g/100 g of polymer. The OP values decreased by 59%, and OTR values decreased by 67.3% with the addition of 5 g ZnO-NPs/100 g of blended polymer. The permeability coefficient of a substance is determined by the formulaP=D×S, in which D is the diffusion coefficient and S is the solubility coefficient [24]. The reduction of OP and OTR can be attributed to the distribution of the ZnO nanoparticles in the film matrix, which led to a reduced oxygen diffusion. The increase in OP when the concentration of ZnO-NPs was 25 g/100 g of blended polymer was probably due to reducing the hydrogen bonds in the pectin/alginate matrix and reducing the interaction between P/AG and ZnO-NPs, due to structural changes in the polymer matrix. Therefore, the diffusion coefficient increased leading to an increase in the oxygen permeability of these films. This result shows the possibility of using P/AG membranes with ZnO-NPs in food preservation to inhibit oxidation.


### 3.7. Antimicrobial Action of Film-Forming Solutions

The antimicrobial activities of the P/AG ZnO-NPs films againstEscherichia coli, Saccharomyces cerevisiae, Colletotrichum gloeosporioides, and Aspergillus niger are shown in Figure 5.Figure 5
Antimicrobial activities of P/AG films with various ZnO-NP contents.The inhibition zone increased with the increase of the ZnO-NP concentration in the range of 0.5 to 5 g/100 g of polymer. However, when increasing the concentration from 5 g to 25 g/100 g of polymer, the inhibitory zone did not increase. This may be related to the decrease of the diffusion ability of the ZnO-NPs in the agar at high concentrations. The antimicrobial effect was due to the ZnO-NPs because the pure P/AG film that did not contain ZnO-NPs was not antibacterial. The inhibitory effect of the ZnO-NPs againstAspergillus niger and Colletotrichum gloeosporioides was greater than that against E. coli and Saccharomyces cerevisiae. It is believed that the antimicrobial activity of ZnO-NPs is mainly dependent on the cell wall structure of the microorganisms. In almost mold, the hyphal cell wall consists of a single, 80 to 150 nm layer composed of chitin and β-glucan. In contrast, the 200 to 600 nm thick yeast cell wall has three layers [25]. The cell wall of E. coli (Gram-negative bacteria) is composed of a complex structure with thin peptidoglycan layer surrounded by an outer membrane [26, 27]. The antimicrobial activity of the P/AG films with ZnO-NPs was the highest when the ZnO-NP concentration was 5 g/100 g of blended polymer. The results of the study on the antimicrobial properties of P/AG films with ZnO-NPs support the use of this material to preserve food products, especially products that are susceptible to mold damage. Moreover, ZnO-NPs have a negligible negative effect on human cells according to Reddy et al. [28].


### 3.8. FTIR Spectra of P/AG Films with ZnO-NPs

The ATR-FTIR analysis demonstrates the interaction between the ZnO-NPs, pectin, and alginate. The results are shown in Figure6.Figure 6
FTIR spectra of P/AG films incorporated with various ZnO-NP contents.The results show that the spectra for all films have characteristic peaks at 4000–500 cm−1. The P/AG films exhibited the major band at 1630 cm−1, which is the characteristic peak of C=O stretching/hydrogen bonding coupled with a COO− group of pectin and alginate [25]. The absorption peaks at 1400 and 1440 cm−1 are related to the stretching bands of the COO− groups, and the peak at 3410 cm−1 was induced by the OH groups. The ATR-FTIR spectra of P/AG/ZnO-NPs films show that the peaks at 3410, 2890, 1630, and 1420 cm−1 were shifted to 3300–3200, 2920–2910, 1597, and 1410 cm−1, respectively. Shifting of the adsorption peaks indicates that hydrogen bonds between the oxygen atoms of ZnO-NPs and the OH, the COOH, and the CH3 (hexane) groups of pectin/alginate matrix occurred. These results confirm that the addition of ZnO-NPs can improve the water resistance, oxygen resistance, and mechanical properties of the P/AG films. The reason could be that the OH and the COOH groups of the pectin/alginate matrix are able to form hydrogen bonds with oxygen groups in the ZnO-NPs.


## 3.1. Thickness and Mechanical Properties

The thickness and mechanical properties of the P/AG films with various ZnO-NP contents are presented in Table1. The thicknesses of the P/AG films that contain the ZnO-NPs is higher than for the P/AG only film. The increase in ZnO-NP content from 0 to 25 g/100 g of blended polymer led to an increase in the film thickness from 52.4 to 74.6 μm. The increase in the thickness was not only attributed to the higher solid content of nanocomposite films ZnO-NPs but also attributed to their structure. Similar results were reported by Shahmohammadi Jebel and Almasi [16].Table 1
Thickness and mechanical properties (tensile strength = TS; % elongation = %E) of P/AG films with various ZnO-NP contents.
ZnO-NP content (g/100 g of blended polymer)
Thickness (μm)
TS (MPa)
%E (%)
0
43.8 ± 2.11d
21.71 ± 1.23d
0.86 ± 0.04c
0.5
52.4 ± 2.5c
32.59 ± 1.6c
1.89 ± 0.05b
2.5
56.8 ± 2.83b
36.43 ± 0.98b
1.93 ± 0.05b
5
58.1 ± 2.08b
41.56 ± 1.94a
2.32 ± 0.06a
25
74.6 ± 3.25a
12.79 ± 0.58e
0.85 ± 0.04c
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.The tensile strength (TS) and % elongation at break (E) for the films with various ZnO-NP contents equilibrated at 25 ± 1°C and 52 ± 1% RH are shown in Table1. There was an increase in tensile strength from 21.71 to 41.56 MPa when increasing the ZnO-NP content from 0.5 to 5 g/100 g of blended polymer. On the other hand, the increase in the ZnO-NP concentration from 5 to 25 g/100 g of blended polymer reduced the tensile strength from 41.56 to 12.79 MPa. The tensile strength was the highest when the ZnO-NPs were added at a concentration of 5 g/100 g of blended polymer, where it reached 191.4% of the tensile strength for the P/AG film.The change in elongation is similar to that of tensile strength. Changes in tensile strength and elongation values may be due to the formation of hydrogen links between the pectin, alginate’s hydroxyl groups, and oxygen atoms in the ZnO-NPs [17, 18]. Moreover, a low concentration of ZnO-NPs had a negligible effect on the formation of hydrogen bonds between the OH and the COOH groups in the pectin/alginate matrix, as well as the formation of bonds between the Ca2+ and the COO− groups of the pectin and alginate chains. The pectin and alginate chains thereby adopted a structure that resembles an “egg-box” model.The decrease in TS and E of the film with 25 g ZnO-NPs/100 g polymer was probably due to agglomeration of the ZnO-NPs, the nonuniform distribution of the ZnO-NPs, and the recrystallization of the ZnO-NPs in the polymer matrix. These factors caused discontinuous cracks in the polymer matrix and resulted in a sudden decrease in the TS and E. A similar result was observed when adding CuO-NPs and ZnO-NPs into a carrageenan matrix [18].


## 3.2. Solubility and Water Contact Angle

The water contact angle (θ) is the most common parameter used to describe the hydrophilicity of film surfaces. Hydrophilic membranes possess a contact angle of 0° < θ < 90°, while hydrophobic membranes have a contact angle of 90° < θ < 180° [19]. Table 2 shows the solubility and water contact angle for the film specimens.Table 2
Effect of ZnO-NP contents on the solubility and water contact angle of P/AG films.
ZnO-NP contents (g/100 g of blended polymer)
Contact angle (°)
Solubility (%)
0
73.85 ± 6.4a
30.38 ± 1.3a
0.5
72.9 ± 4.5a
27.34 ± 1.8ab
2.5
72.5 ± 2.9a
23.16 ± 2.1b
5
70.73 ± 4.1a
22.49 ± 3.1b
25
54.07 ± 7.4b
26.1 ± 1.5ab
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.Results showed that adding ZnO-NPs to the P/AG film at the amount of 0.5 to 5 g/100 g of blended polymer did not significantly change the water contact angle. However, the water contact angle for the film-incorporated ZnO-NPs with 25 g/100 g of blended polymer was lower than the other films. Reducing the water contact angle may be due to an increase in surface roughness at high ZnO-NP concentrations.The solubility values for the specimens trended to the decrease with increasing ZnO-NP content, except for the ZnO-NP content of 25 g/100 g of blended polymer. These results indicate that the addition of the ZnO-NPs reduced the number of hydroxyl groups and charged groups (−COO−). Moreover, the length of the polymer increased due to the formation of links between the ZnO-NPs, pectin, and alginate. Consequently, the solubility of the films was reduced. The ZnO-NP content in the 25 g/100 g of blended polymer was more than necessary for creating hydrogen bonds such that it probably had a negative effect on the cross-linking between the Ca2+ ion, the pectin, and the alginate carboxyl groups. This increased the solubility value. Thus, the film solubility trended to increase when the ZnO-NP content was 25 g/100 g of blended polymer.


## 3.3. WVP and WVTR of P/AG Films

Table3 shows WVP and WVTR of film specimens. The WVP values of the specimens decreased from 1.01 to 0.414 kg·m/m2·Pa·s (59%), and WVTR values decreased from 4.226 to 1.486 kg/m2·s (64.8%), when increasing the ZnO-NP content from 0 to 5 g/100 g of blended polymer. This may be due to the formation of the hydrogen bonds between the pectin, alginate matrix, and oxygen atoms in the ZnO-NPs, which increases the adhesion of the biopolymer matrix and can reduce the diffusion of the water molecules in the material. A similar result was reported by Almasi et al. [20]. On the other hand, the even distribution of the ZnO-NPs with smaller sizes and filling of the microvoids should reduce the length of a free path for water uptake. Similar results were reported for the effect of ZnO-NPs on the WVP of biopolymer-based nanocomposites [3, 21]. There was no significant change in the WVP and WVTR values of the sample when increasing the content of the ZnO-NPs from 5 to 25 g/100 g of blended polymer, which may be due to the maximum reduction of the hydrophilic groups, such as OH and COOH in the polymer.Table 3
WVP and WVTR of P/AG films with various ZnO-NP contents.
ZnO-NP contents (g/100 g of blended polymer)
WVP × 10−14 (kg·m/m2·Pa ·s)
WVRT × 10−7 (kg/m2·s)
0
1.01 ± 0.029a
4.226 ± 0.121a
0.5
0.576 ± 0.018b
2.148 ± 0.069b
2.5
0.447 ± 0.008c
1.949 ± 0.035b
5
0.414 ± 0.02cd
1.486 ± 0.069c
25
0.381 ± 0.019d
1.437 ± 0.069c
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.


## 3.4. Moisture Sorption Isotherm

The moisture absorption of the P/AG film was higher than that of P/AG films with the ZnO-NPs in the range of water activity between 0.86 and 0.93 (Figure3). A similar result was reported by Galus and Lenart [22]. The film’s moisture absorption decreased as the ZnO-NP content increased. However, there was no significant change in the moisture absorption between the P/AG films and the P/AG films with the ZnO-NPs in the water activity range of 0 to 0.75. Based on the results obtained for the solubility, WVP, mechanical properties, and moisture sorption isotherm, it is recognized that these trends are due to the formation of hydrogen bonding between the OH groups of the pectin, alginate, and oxygen atoms of the ZnO-NPs. The reduction in moisture absorption may be due to the reduction of the free OH groups in the membrane. On the other hand, a uniform dispersion of smaller ZnO-NPs and filling of microvoids produces a decrease in the length of the free path for water uptake.Figure 3
Moisture sorption isotherms of P/AG films incorporated with various ZnO-NP contents at 25 ± 1°C.


## 3.5. Transparency and Light Transmission of Films

Figure4 shows the light transmission of film specimens. Light transmission decreases in the wavelength range of 320 to 350 nm (UV light) and reaches the lowest value at 350 nm. The light transmittance of films containing ZnO-NPs is always lower than that of films without the ZnO-NPs. The higher the ZnO concentration in the film, the lower the light transmission at the wavelength range of 320 to 350 nm. This result shows that ZnO-NPs in the film have absorbed ultraviolet light. This result is consistent with that of Khodaiyana et al. [23] who observed that the UV absorbance of the nanocomposite polymers increased as the ZnO-NP content increased. They also observed that a ZnO-Np content greater than 1% was necessary to induce UV filtration in a kefiran biopolymer. There is no significant difference in light transmittance between films containing ZnO-NPs and P/AG films in the wavelength range of 500 to 800 nm, except for P/AG films with a ZnO-NP content of 25 g/100 g of blended polymer.Figure 4
Light transmission of the films.Table4 shows the transparency of the films with various ZnO-NP contents. The transparency for the films containing 0.5 to 5 g/100 g blended polymer of ZnO-NPs was not significantly different from the P/AG film. However, the addition of ZnO-NPs with 25 g/100 g of blended polymer into the films decreased the transparency value. The reduction of transparency of the films with a concentration of 25 g ZnO-NPs/100 g polymer may be due to the over-distribution of the ZnO-NPs in the pectin/alginate network.Table 4
Transparency of P/AG films with various ZnO-NP contents.
ZnO-NP contents (g/100 g of blended polymer)
0
0.5
2.5
5
25
Transparency values (1/mm)
3.24 ± 0.02b
3.26 ± 0.01b
3.25 ± 0.03b
3.17 ± 0.02ab
3.01 ± 0.02a
Alphabets in a column indicate a significant difference atP<0.05 by Duncan’s multiple.


## 3.6. Oxygen Permeability and Oxygen Transmission Rate

The OP and OTR of P/AG and P/AG films with various ZnO-NP contents are presented in Table5.Table 5
OP and OTR of P/AG films with various ZnO-NP contents.
ZnO-NP contents (g/100 g of blended polymer)
OP × 10−19 (kg·m/m2·Pa·s)
OTR × 10−11 (kg/m2·s)
0
270.86 ± 9.79a
158.65 ± 16.17a
0.5
253.85 ± 15.35a
137.51 ± 6.95b
2.5
191.87 ± 12.44b
89.82 ± 3.68c
5
110.79 ± 7.74d
51.87 ± 3.98d
25
132.92 ± 7.45c
48.84 ± 3.55dThe addition of ZnO-NP to the P/AG films led to a reduced oxygen permeability. The lowest reduction occurred when the ZnO-NP concentration reached 5 g/100 g of polymer. The OP values decreased by 59%, and OTR values decreased by 67.3% with the addition of 5 g ZnO-NPs/100 g of blended polymer. The permeability coefficient of a substance is determined by the formulaP=D×S, in which D is the diffusion coefficient and S is the solubility coefficient [24]. The reduction of OP and OTR can be attributed to the distribution of the ZnO nanoparticles in the film matrix, which led to a reduced oxygen diffusion. The increase in OP when the concentration of ZnO-NPs was 25 g/100 g of blended polymer was probably due to reducing the hydrogen bonds in the pectin/alginate matrix and reducing the interaction between P/AG and ZnO-NPs, due to structural changes in the polymer matrix. Therefore, the diffusion coefficient increased leading to an increase in the oxygen permeability of these films. This result shows the possibility of using P/AG membranes with ZnO-NPs in food preservation to inhibit oxidation.


## 3.7. Antimicrobial Action of Film-Forming Solutions

The antimicrobial activities of the P/AG ZnO-NPs films againstEscherichia coli, Saccharomyces cerevisiae, Colletotrichum gloeosporioides, and Aspergillus niger are shown in Figure 5.Figure 5
Antimicrobial activities of P/AG films with various ZnO-NP contents.The inhibition zone increased with the increase of the ZnO-NP concentration in the range of 0.5 to 5 g/100 g of polymer. However, when increasing the concentration from 5 g to 25 g/100 g of polymer, the inhibitory zone did not increase. This may be related to the decrease of the diffusion ability of the ZnO-NPs in the agar at high concentrations. The antimicrobial effect was due to the ZnO-NPs because the pure P/AG film that did not contain ZnO-NPs was not antibacterial. The inhibitory effect of the ZnO-NPs againstAspergillus niger and Colletotrichum gloeosporioides was greater than that against E. coli and Saccharomyces cerevisiae. It is believed that the antimicrobial activity of ZnO-NPs is mainly dependent on the cell wall structure of the microorganisms. In almost mold, the hyphal cell wall consists of a single, 80 to 150 nm layer composed of chitin and β-glucan. In contrast, the 200 to 600 nm thick yeast cell wall has three layers [25]. The cell wall of E. coli (Gram-negative bacteria) is composed of a complex structure with thin peptidoglycan layer surrounded by an outer membrane [26, 27]. The antimicrobial activity of the P/AG films with ZnO-NPs was the highest when the ZnO-NP concentration was 5 g/100 g of blended polymer. The results of the study on the antimicrobial properties of P/AG films with ZnO-NPs support the use of this material to preserve food products, especially products that are susceptible to mold damage. Moreover, ZnO-NPs have a negligible negative effect on human cells according to Reddy et al. [28].


## 3.8. FTIR Spectra of P/AG Films with ZnO-NPs

The ATR-FTIR analysis demonstrates the interaction between the ZnO-NPs, pectin, and alginate. The results are shown in Figure6.Figure 6
FTIR spectra of P/AG films incorporated with various ZnO-NP contents.The results show that the spectra for all films have characteristic peaks at 4000–500 cm−1. The P/AG films exhibited the major band at 1630 cm−1, which is the characteristic peak of C=O stretching/hydrogen bonding coupled with a COO− group of pectin and alginate [25]. The absorption peaks at 1400 and 1440 cm−1 are related to the stretching bands of the COO− groups, and the peak at 3410 cm−1 was induced by the OH groups. The ATR-FTIR spectra of P/AG/ZnO-NPs films show that the peaks at 3410, 2890, 1630, and 1420 cm−1 were shifted to 3300–3200, 2920–2910, 1597, and 1410 cm−1, respectively. Shifting of the adsorption peaks indicates that hydrogen bonds between the oxygen atoms of ZnO-NPs and the OH, the COOH, and the CH3 (hexane) groups of pectin/alginate matrix occurred. These results confirm that the addition of ZnO-NPs can improve the water resistance, oxygen resistance, and mechanical properties of the P/AG films. The reason could be that the OH and the COOH groups of the pectin/alginate matrix are able to form hydrogen bonds with oxygen groups in the ZnO-NPs.


## 4. Conclusions

The addition of ZnO-NPs to pectin and alginate films changed some physicochemical properties of films compared to films without the ZnO-NPs. There was a decrease in the solubility, moisture absorption, UV light transmission, WVP, WVTR, OP, and the OTR of the P/AG films with ZnO-NPs compared to the films without them. In contrast, there was an increase in tensile strength, elongation at break, and antimicrobial properties of the P/AG films with ZnO-NPs compared to the films without them. In this work, the change was the highest when the ZnO-NP content in the film was 5 g/100 g of blended polymer. The ATR-FTIR analysis indicated that hydrogen bonds between the ZnO-NPs and pectin/alginate matrices were formed. These results suggest the possibility of using P/AG/ZnO-NPs film in food preservation and that they may be better than pectin/alginate films.



---

*Source: 5645797-2018-10-22.xml*