# Heat Generation by Polypyrrole Coated Glass Fabric

Authors: A. M. Rehan Abbasi; J. Militky; J. Gregr
Journal: Journal of Textiles
 (2013)

---

## Abstract

Vapor deposition technique was employed to coat polypyrrole (PPy) on glass substrate using FeCl3 as oxidant and p-toluenesulfonic acid (−OTs) as doping agent. The Joule heating effect of PPy coated E-glass fabric was studied by supplying various DC electric fields. The coated fabric exhibited reasonable electrical stability, possessed medium electrical conductivity and was effective in heat generation. An increase in temperature of conductive fabric subjected to constant voltage was observed whereas decrease in power consumption was recorded. Thickness of PPy coating on glass fibers was analyzed by Laser confocal microscope and scanning electron microscope.


---

## Body

## 1. Introduction

In the late 1970s, MacDiarmid, Heeger, and Shirakawa discovered how to get polymers conducting electricity [1]. The first material becoming an intrinsically conducting polymer (ICP) was polyacetylene, after a doping with iodine. The announcement of this discovery quickly reverberated around scientific communities, and intensity of the research for other conducting polymers magnified dramatically [1–3]. A new generation of polymers was then developed, exhibiting the electrical and optical properties of metals or semiconductors, at the same time retaining the attractive mechanical properties and processing advantages of polymers. Intrinsically, conducting polymers were immediately seen as a new route to mimic metallic conductivity, besides the well-known approach to insert conductive fillers into an inherently insulating resin, or to coat a plastic substrate with a conductive metal solution [4].Ability to apply conducting polymers to any fiber type and textile structure provides unlimited flexibility in the design of conductive fabrics. Each fiber on the surface of the textile is coated by a thin layer of conducting polymer. As a result of chemical polymerization in the presence of a fabric, a continuous thin film of conducting polymer is formed on the fabric surface. Current will flow through these fabrics without any wiring through them and the heat generated is not affected by holes or cuts in the fabric as the entire surface is electrically conductive.Wide ranging modulation of electrical properties of conducting textiles leads to various other applications. Electrical conductivity is sensitive to external stimuli such as temperature and pressure, suggesting applications in the area of sensors.Kinetics of degradation of conductivity of chemically and electrochemically synthesized polypyrrole at elevated temperatures has been thoroughly investigated. However, only a few brief reports have been published on the aspect of heat generation. In one of these reports, low temperature radiant heating panels were produced by PPy coating, and effect of heat generation was studied, but their applications are still limited due to comparatively low tensile strength of the fabric. The aim of this work is to develop heating panels by coating PPy on glass fabric for commercial and industrial applications, specially suggested for space heating systems at low cost. The reason for choosing glass fiber is its higher tensile strength compared to other fibers of the same price.


## 2. Methodology

### 2.1. Sample Preparation

PPy was coated on E-glass fabric having specifications given in Table1. The glass fabric was first immersed in aqueous solution of −OTs and FeCl3 as an oxidant in molar ratio 1 : 2, respectively, at the temperature of 10°C and squeezed with rubber rollers padding machine with 100% pickup.Table 1
Specification of the E-glass fabric used for experiment.
Properties
Index
Weave
Plain
Fineness (tex)
Warp
1250
Weft
1250
Warp/cm
3.67
Weft/cm
3.5
Cover factor (SI)
Warp
13
Weft
12.4
Areal density (g·m−2)
900
Thickness (mm)
1.1
Fabric porosity (ϕ)
0.678Fabric porosity can be calculated by(1)ϕ=1-(ρfaρf).
Here, ρfa is the density of fabric that can be evaluated through dividing areal density by the thickness, whereas ρf is the known density of fiber.As the amount of PPy depends upon the oxidizing agent present in the system, different specimens were developed by taking different concentrations of FeCl3 as 0.3, 0.4, 0.5, and 0.6 mol/L keeping dopant to oxidizing agent ratio as 1 : 2 constant.If released to air, a vapor pressure of 8.35 mmHg at 25°C indicates pyrrole exists solely as a vapor in the ambient atmosphere. Therefore, fabric was then immediately exposed to vapors of pyrrole monomer for 8 hours. Later, fabric was rinsed with ethanol and distilled water to remove excess of monomer and biproducts. Finally, it was dried in air at25±4°C for 24 hours. The formation of the conductive polymer coating on the textile substrate starts from deposited oligomers, which form islands in the initial stage and finally grow and cover the surface of the substrate completely [5].For evaluation of electrical properties of fabrics, two parameters were selected, namely, the surface and volume resistivity. These parameters can be calculated from the information of surface and bulk resistivity, the dimensions of the electrodes, and/or the thickness of the sample. For this purpose, concentric electrode system was used conforming to DIN EN 1149-1, EN 100 015, EN 61340-5-1, together with Agilent 53131A digital multimeter. Measurements of electrical resistance were performed in the climatic conditionst=20±2°C and φ=40±2%, which is in accordance with the standard ČSN 80 0059.The morphology and thickness of PPy coating on glass fiber was characterized by scanning electron microscope (SEM) Carl Zeiss Ultra plus after gold coating and Laser confocal microscope in the Technical University of Liberec, Czech Republic.


### 2.2. Temperature Measurements

For the purpose of evaluating heat generation by polypyrrole coated glass fabric samples, 5 V, 10 V, 15 V, and 20 V DC electromotive forces by DC voltage supplier NZ-2229.2 from Statron, Czech Republic, were applied via stainless steel clamp type electrodes. Meanwhile DC current passing through the substrate was measured by connecting Agilent 53131A digital multimeter in series. The rise in temperature was determined by the infrared thermal camera by Fluke together with k-type thermocouples in connection with ART data acquisition module. The infrared thermal camera was helpful to figure the homogeneity of the specimen out.


## 2.1. Sample Preparation

PPy was coated on E-glass fabric having specifications given in Table1. The glass fabric was first immersed in aqueous solution of −OTs and FeCl3 as an oxidant in molar ratio 1 : 2, respectively, at the temperature of 10°C and squeezed with rubber rollers padding machine with 100% pickup.Table 1
Specification of the E-glass fabric used for experiment.
Properties
Index
Weave
Plain
Fineness (tex)
Warp
1250
Weft
1250
Warp/cm
3.67
Weft/cm
3.5
Cover factor (SI)
Warp
13
Weft
12.4
Areal density (g·m−2)
900
Thickness (mm)
1.1
Fabric porosity (ϕ)
0.678Fabric porosity can be calculated by(1)ϕ=1-(ρfaρf).
Here, ρfa is the density of fabric that can be evaluated through dividing areal density by the thickness, whereas ρf is the known density of fiber.As the amount of PPy depends upon the oxidizing agent present in the system, different specimens were developed by taking different concentrations of FeCl3 as 0.3, 0.4, 0.5, and 0.6 mol/L keeping dopant to oxidizing agent ratio as 1 : 2 constant.If released to air, a vapor pressure of 8.35 mmHg at 25°C indicates pyrrole exists solely as a vapor in the ambient atmosphere. Therefore, fabric was then immediately exposed to vapors of pyrrole monomer for 8 hours. Later, fabric was rinsed with ethanol and distilled water to remove excess of monomer and biproducts. Finally, it was dried in air at25±4°C for 24 hours. The formation of the conductive polymer coating on the textile substrate starts from deposited oligomers, which form islands in the initial stage and finally grow and cover the surface of the substrate completely [5].For evaluation of electrical properties of fabrics, two parameters were selected, namely, the surface and volume resistivity. These parameters can be calculated from the information of surface and bulk resistivity, the dimensions of the electrodes, and/or the thickness of the sample. For this purpose, concentric electrode system was used conforming to DIN EN 1149-1, EN 100 015, EN 61340-5-1, together with Agilent 53131A digital multimeter. Measurements of electrical resistance were performed in the climatic conditionst=20±2°C and φ=40±2%, which is in accordance with the standard ČSN 80 0059.The morphology and thickness of PPy coating on glass fiber was characterized by scanning electron microscope (SEM) Carl Zeiss Ultra plus after gold coating and Laser confocal microscope in the Technical University of Liberec, Czech Republic.


## 2.2. Temperature Measurements

For the purpose of evaluating heat generation by polypyrrole coated glass fabric samples, 5 V, 10 V, 15 V, and 20 V DC electromotive forces by DC voltage supplier NZ-2229.2 from Statron, Czech Republic, were applied via stainless steel clamp type electrodes. Meanwhile DC current passing through the substrate was measured by connecting Agilent 53131A digital multimeter in series. The rise in temperature was determined by the infrared thermal camera by Fluke together with k-type thermocouples in connection with ART data acquisition module. The infrared thermal camera was helpful to figure the homogeneity of the specimen out.


## 3. Results

Oxidation of the pyrrole monomer in the presence of the substrate causes polymerization to take place on the fabric surface, resulting in a thin and smooth conductive coating, whilst some of the polymer particles formed on the PPy coating deposited on the surface at prolonged reaction time and at higher monomer concentration, which can be seen as clumps of PPy deposition on the surface and shown as inhomogeneity in the PPy coating, as shown in Figure1. The morphology of the glass surface after coating with PPy shown in Figure 2 explains that each fiber in the fabric structure is covered with PPy depending upon the concentration. The average thickness of coating of PPy on E-glass fiber was measured as 1.165±0.05 μm.SEM micrographs: (a) E-glass control and (b) E-glass coated with PPy using FeCl3 0.6 mol/L.
(a)
(b)The surface morphology of the PPy coating using FeCl3 0.6 mol/L studied by Laser confocal microscope (a) describes the surface morphology and (b) comparison of thickness.
(a)
(b)The average thickness was also measured with the help of Laser confocal microscopy and was found to be around 1.372μm as shown in Figure 2, which also proves the homogeneity and smoothness of PPy coating on glass fibers.The weight gain (Δm) by the glass fabric after coating follows a linear function of concentration of FeCl3 (C) as revealed in Figure 3, and this relation can be expressed mathematically as (2) with coefficient of determination R2=0.962:
(2)Δm=9.0442·C.
The presence of PPy on the E-glass fabric specimen was characterized by Fourier transform infrared spectroscopy (FTIR) as shown in Figure 4. The strong absorbance of control specimen at 958 cm−1 shows the occurrence of Si–O–Si and Si–OH in E-glass structure. The absorption at 1546 and 1452 cm−1 assigned to ring vibration of C=C and C=N as well as at 1168 cm−1 for N–C vibration confirms the presence of pyrrole ring of PPy. Absorptions at 1303 and 1035 cm−1 confirm in-plane vibration of =C–H, whereas absorption at 788 cm−1 shows out-plane vibration of =C–H.Figure 3
The dependence of weight gain by glass fabric after coating by PPy.Figure 4
FTIR absorbance curves of E-glass control and E-glass coated with PPy.Sharp increase in temperature of fabric specimen was observed in first 3 min with the applied voltage which was then stabilized after reaching a plateau, as shown in Figure5, and it shows the ease with which heat could be generated by employing a reasonable DC voltage.Figure 5
Escalation of temperature of E-glass fabric coated by PPy using 0.6 mol/L FeCl3 with increase in DC voltage V and time.Power densityPD (volume specific power) is the amount of power (time rate of energy transfer) per unit volume. It is then also called volume power density which is expressed as (W/m3). Volume power density is sometimes an important consideration where space is constrained. In this study, power density PD is extremely linear function of voltage supplied to the PPy coated glass fabric as illustrated in Figure 6 and expressed as
(3)e˙gen=E˙genvelement=PD=82.58V-245.83.
Here, e˙gen shows the power generated per unit volume, E˙gen the quantity of heat energy, and velement the volume of the heating element which in our case is fabric.Figure 6
Rise in power density and temperature of sample D4 as a function of DC voltageV.However, temperature rise in fabric sample at equilibrium (after 3 min) follows exponential function of voltage withR2=0.9717, that can be written as
(4)T=T0e0.0795V.
Here, T is the temperature in (°C) measured at equilibrium at applied DC V, and T0 is the temperature of fabric at ambient conditions, which was recorded as 22.3°C for this experiment.


## 4. Conclusion

For the specimen the rate of change of temperature has two distinct phases: an initial sharp rise during the first 100 s or so, followed by a leveling off to plateau at approximately 300 to 400 s. During the first phase, the electrical energy input to the samples exceeds the combined thermal energy losses in the forms of convection, radiation, and conduction and hence, the temperature rises. As the temperature rises the heat losses increase until they are balanced with the heat generated and the temperature of the fabric stops rising. This is the stable temperature of the fabric under the applied voltage.The electrical power supplied to the specimen that ultimately converts into thermal power follows a linear dependence on the DC voltage supplied, whereas rise in temperature of the specimen is a power function of supplied voltage.The estimated cost to produce PPy coated E-glass fabric at laboratory scale was roughly calculated as less than Euro 1.15 per m2, and this kind of heat generating industrial textile can find its practical application as heating systems for small and medium spaces as well as for the drying of wet cement in civil works.



---

*Source: 571024-2013-09-24.xml*