# Radiolytic Synthesis of Vinyl Polymer-Clay Nanocomposite Membranes for Direct Methanol Fuel Cell

Authors: Yoon-Seob Kim; Yun Ok Kang; Seong-Ho Choi
Journal: Journal of Nanomaterials
 (2014)

---

## Abstract

The three-type vinyl polymer-clay nanocomposite membranes with sulfonate (–SO3Na) are prepared by the solvent casting method after radiation-induced copolymerization for application of the direct methanol fuel cell (DMFC) membrane. The three-type vinyl polymers in polymer-clay nanocomposite membranes are included in poly(styrene-co-sodium styrene sulfonate), poly(St-co-NaSS), poly(2-hydroxyethyl methacrylate-co-NaSS), poly(HEMA-co-NaSS), and poly(acrylic acid-co-NaSS), and poly(AAc-co-NaSS). The proton conductivity (S/cm), water uptake (%), and ion-exchange capacity (meq/g) of the poly(St-co-NaSS)-clay nanocomposite membrane are 0.0779, 32.4, 3.63, respectively.  The MeOH permeability of the poly(St-co-NaSS)-clay nanocomposite membrane is exhibited as 7.7
×
10
−
9 mmol
·
cm
−
2
·
s
−
1.  DMFC performance for poly(St-co-NaSS)-clay nanocomposite membrane is also measured in cell voltage and power density verses current density. As results, the poly(St-co-NaSS)-clay nanocomposite membrane can be used as a DMFC membrane on behalf of the commercial Nafion membrane.


---

## Body

## 1. Introduction

Direct methanol fuel cell (DMFC) [1, 2] and polymer electrolyte membranes fuel cell (PEMFC) [3, 4] have recently received much attention due to these power sources presenting a high-energy efficiency and low emission of pollutants. For PEMFC, hydrogen was used as fuel and delivered the power density of 300–500 Wcm−2 at 80–90°C. While there are many problems such as production, storage, and transportation of hydrogen using hydrogen as a fuel, the DMFC has attracted more attention than PEMFC when using liquid methanol as fuel, which is easy to deliver and store. More importantly, methanol fuel can be used at ambient temperature and pressure, which makes the DMFC easy to be applied to portable electronic devices [5]. However, the development of DMFC has faced several serious problems: (i) slow methanol oxidation kinetics [6], (ii) the poisoning of CO intermediate on the Pt surface [7], (iii) the high methanol cross-over through the polymer membrane [8, 9], and (iv) the high costs of the Nafion membrane and Pt catalyst [10, 11].Presently, the perfluorosulfonate ionomer membranes, such as Nafion membrane (Dupont), are the primary polymer membranes used on the DMFC. However, the commercial Nafion polymer membranes showed a serious methanol cross-over problem, which MeOH permeates from the anode to the cathode. The MeOH permeation not only causes a loss of fuel but also a mixed potential being formed at the cathode leading to a lower electrochemical performance of the DMFC. Thus, for the liquid MeOH fuel cell, it is imperative that the most important characteristic properties of a solid polymer membrane on the DMFC must have a lower MeOH permeation of liquid fuel.In order to overcome MeOH crossover in DMFC, polymer-inorganic material composite membranes were prepared from many researchers. Yang and Lee [12] synthesized the PVA/MMT polymer membrane and determined the MeOH permeability at 3-4 × 10−6 cm2 s−1. Lee et al. [13] also prepared the disulfonated poly(arylene ether sulfone)-silica nanocomposites membrane for DMFC and determined the MeOH permeability as 10−6~10−7 cm2 s−1 value at 30°C. Sulfonated poly(ether ether ketone) (SPEEK) membrane-clay composite membrane was also prepared by Jaafar et al. [14] and also determined methanol permeability with a 10−9~10−10 cm2 s−1 value. Karthikeyan et al. [15] also prepared SPEEK-MCM-41 composite membranes with 10−17 m2 s−1 pa−1. Nafion-montmorillonite composite membrane with MeOH permeability of 0.042 mol/L at 1 h for DMFC was also prepared by Jung et al. [16] However, little has been reported for the vinyl polymer-clay nanocomposite membrane with low MeOH permeability.In a previous paper [17], the preparation of poly(St-co-DVB)-clay nanocomposites with a quaternary alkylammonium salt as a intercalating agent by γ-irradiation copolymerization was reported. It was found that the γ-irradiation techniques have many advantages for preparation of vinyl polymer-clay nanocomposites. In particular, they need no radical initiators. During γ-irradiation, free radicals are generated at low temperature. Therefore, the polymer-clay nanocomposites can be simultaneously prepared using the free radicals during γ-irradiation. However, this poly(St-co-DVB)-clay nanocomposite could not be used for DMFC membrane because there are no proton-exchange groups and brittle mechanical properties.In this study, we prepared a three-type vinyl polymer-clay nanocomposite membrane with sulfonate group (–SO3Na) as the cation transfer site by solution casting method after radiation-induced copolymerization of vinyl monomers. The prepared polymer-clay nanocomposite membrane was characterized by FT-IR, TEM, ion-exchange capacity, water-uptake, proton conductivity, and MeOH permeability. Furthermore, in order to know the application of the DMFC membrane, DMFC performance for the poly(St-co-NaSS)-clay nanocomposite membrane was performed.


## 2. Experimental

### 2.1. Materials

Butylimidazole, styrene methyl chloride, styrene, sodium styrene sulfonate, acrylic acid, 2-hydroxyethyl methacrylate, and 5.0% Nafion solution were obtained from Sigma-Aldrich (Yong-in, Korea). The Na+-montmorillonite (Na+-MMT) was obtained from Southern Clay Products, Inc. (Texas, USA). 80 wt.% PtRu/Vulcan and 80 wt.% Pt/Vulcan catalysts for DMFC performance were obtained Premetek Co. (USA). Solutions for the experiments were prepared with water purified in a Milli-Q plus water purification system (Millipore Co., Ltd., USA, the final resistance of water was 18.2 M Ω cm−1). Other chemicals were of reagent grade.


### 2.2. Preparation of Substituted Imidazolium Salt

1-[(4-ethylphenyl)methyl]-3-butyl-imidazolium chloride represented here as [EPMBIM]+[Cl]− was first prepared by the quaternization reaction of butyl imidazole with styrene methyl chloride at 80°C for 24 h in cyclohexane under refluxing condition. The structure of the prepared imidazolium salt was confirmed by 1H NMR spectra (DMSO-d
6, chemical shift, δ/ppm relative to TMS): 9.34 (s, 1H), 7.88 (t, 1H, and J
=
1.65 Hz), 7.79 (t, 1H, and J
=
1.65 Hz), 4.24 (q, 2H, and J
=
7.26 Hz), 3.89 (s and 3H), and 1.42 (t, 3H, and J
=
7.26 Hz).


### 2.3. Preparation of Organic-Montmorillonite Clay (O-MMT)

Organo-montmorillonite clay (O-MMT) was prepared by the cationic exchange reaction between the sodium cations of MMT clays and the [EPMBIM]+[Cl]−, as intercalating agent in an aqueous solution as shown in Figure 1. The cationic exchange capacity (CEC) of this clay is 98 meq·100−1 g. The suspension solution containing Na+-MMT/[EPMBIM]+[Cl]− = 1/1.1 in CEC was mixed in 250 mL of distilled water. The suspension solution was stirred at 75°C for 24 h to yield white precipitates. The product was filtered, washed with distilled water, and dried in a vacuum oven at 60°C for 12 hrs.Figure 1
Schematic preparation of the three-type vinyl polymer-clay nanocomposite by radiation-induced polymerization.


### 2.4. Preparation of the Vinyl Polymer-Clay Nanocomposite Membrane by the Solvent Casting Method after Radiation-Induced Copolymerization of Vinyl Monomers

Figure1 shows schematic preparation of the three-type vinyl polymer-clay nanocomposite by radiation-induced polymerization and the used vinyl monomer structure. The NaSS was used in order to obtain the sulfonate group (–SO3Na) as the cation-exchange group. The St, HEMA, and AAc were used in order to prepare the membrane. Table 1 exhibits the preparation condition of the three-type vinyl polymer-clay nanocomposites for the DMFC membrane. The suspension solution was bubbled with nitrogen gas to remove oxygen for 30 min and irradiated from a Co-60 source under atmospheric pressure and ambient temperature. A total irradiation dose of 30 kGy (dose rate = 6.48 × 105 h−1) was used. The final products were filtered and then dried in a vacuum oven at 50°C for 6 h.Table 1
Preparation condition of three-type vinyl polymer-clay nanocomposites for DMFC membranea.
Sample
St (g)
HEMA (g)
NaSS (g)
AAc (g)
O-MMT (g)
MeOH (mL)
H2O (mL)
2-Propanol (mL)
Number 1
18.0
—
—
27.0
3.50
200
200
40.0
Number 2
—
18.0
—
27.0
3.50
200
200
40.0
Number 3
—
—
18.0
27.0
3.50
200
200
40.0
aTotal irradiation dose = 30 kGy (dose rate = 6.48 × 105/h).The vinyl polymer-clay nanocomposite membrane was prepared by drying the polymer-clay nanocomposite DMF solution (7.0 wt.-%) in a glass plate at 70°C for 24 hrs.


### 2.5. Characterizations

The surface Fourier transform infrared (FT-IR) absorption spectra were obtained with FT-IR spectrum IS10 spectrometer (Thermo scientific Co., USA) in the range of 4000–650 cm−1. The surface morphology of the polymer-clay nanocomposites was determined by FE-TEM (JEOL, JEM-2100F, USA) and FE-SEM (S-4800, Hitachi Science System Co., Japan). Thermal gravimetric analysis (TGA) was conducted on a Scinco TGA S-1000 (Seoul, Korea) under N2 flow from 25°C to 700°C at a heating rate of 20°C min−1. The water uptake (%) was determined as follows:
(1)
Water
uptake
(
%
)
=
[
(
W
w
W
g
)
·
W
g
-
1
]
×
100
,
where W
w and W
g are the weight of the polymer-clay nanocomposite membrane in the wetting and drying condition, respectively. In order to determine ion-exchange capacity of the polymer-clay nanocomposite membrane, the prepared membrane (1.0 cm × 1.0 cm) was placed in 0.5 M HCl solution for 24 hrs and then the membrane with sulfonic acid (–SO3H) was inserted into 1.0 M NaCl solution for 24 hrs. The solution with H+ ions was titrated with 0.01 M NaOH solution. Here, ion-exchange capacity (meq/g) of the polymer-clay nanocomposite membrane was determined by titration method as in the following equation:
(2)
Ion-exchange
capacity
(
meq
/
g
)
=
(
N
NaOH
×
V
NaOH
)
W
g
,
where the N
NaOH and V
NaOH mean the normal concentration and volume for the addition of NaOH solution, respectively. The proton conductivity (S/cm) of the polymer-clay nanocomposite membrane was measured by AC impedance (IM-6ex, Zahner, Germany). The proton conductivity of the polymer-clay nanocomposite membrane was calculated as in the following equation:
(3)
σ
=
L
R
×
A
,
where σ is proton conductivity of the membrane, L and R mean the length between the Pt electrode and the measured value from AC impedance, respectively. A is the area of the polymer-clay nanocomposite membrane.The fuel cell performance was performed via the poly(AAc-co-NaSS)-clay nanocomposite membrane assembly (MEA) as shown Figure 2. The anode catalyst inks were firstly prepared by mixing 2.0 mg of commercial 80 wt.% PtRu/Vulcan catalysts in isopropanol alcohol with 5.0% Nafion solution. The anode electrode was prepared by coating of the anode catalyst ink onto the carbon paper surface. The cathode catalysts inks were also prepared by homogeneous mixing of 2.0 mg commercial Pt/Vulcan. Afterwards, the single-cell MEA was fabricated by hot pressing the two electrodes with the prepared PEM under a pressure of 100 Kg cm−2 at 135°C for 10 min. The single-cell MEA was installed in a fuel-cell test station (PRO200F, Propower Co., Korea). MeOH solution with 1.0 M flowed on rates of 900 mL/min and air flowed on the rates of 2.0 mL·min−1. Measurements of the polarization curves (voltage versus current density) were conducted under various temperatures.Schematic fabrication of MEA using poly(AAc-co-NaSS)-clay nanocomposite membrane for DMFC.
(a)
(b)


## 2.1. Materials

Butylimidazole, styrene methyl chloride, styrene, sodium styrene sulfonate, acrylic acid, 2-hydroxyethyl methacrylate, and 5.0% Nafion solution were obtained from Sigma-Aldrich (Yong-in, Korea). The Na+-montmorillonite (Na+-MMT) was obtained from Southern Clay Products, Inc. (Texas, USA). 80 wt.% PtRu/Vulcan and 80 wt.% Pt/Vulcan catalysts for DMFC performance were obtained Premetek Co. (USA). Solutions for the experiments were prepared with water purified in a Milli-Q plus water purification system (Millipore Co., Ltd., USA, the final resistance of water was 18.2 M Ω cm−1). Other chemicals were of reagent grade.


## 2.2. Preparation of Substituted Imidazolium Salt

1-[(4-ethylphenyl)methyl]-3-butyl-imidazolium chloride represented here as [EPMBIM]+[Cl]− was first prepared by the quaternization reaction of butyl imidazole with styrene methyl chloride at 80°C for 24 h in cyclohexane under refluxing condition. The structure of the prepared imidazolium salt was confirmed by 1H NMR spectra (DMSO-d
6, chemical shift, δ/ppm relative to TMS): 9.34 (s, 1H), 7.88 (t, 1H, and J
=
1.65 Hz), 7.79 (t, 1H, and J
=
1.65 Hz), 4.24 (q, 2H, and J
=
7.26 Hz), 3.89 (s and 3H), and 1.42 (t, 3H, and J
=
7.26 Hz).


## 2.3. Preparation of Organic-Montmorillonite Clay (O-MMT)

Organo-montmorillonite clay (O-MMT) was prepared by the cationic exchange reaction between the sodium cations of MMT clays and the [EPMBIM]+[Cl]−, as intercalating agent in an aqueous solution as shown in Figure 1. The cationic exchange capacity (CEC) of this clay is 98 meq·100−1 g. The suspension solution containing Na+-MMT/[EPMBIM]+[Cl]− = 1/1.1 in CEC was mixed in 250 mL of distilled water. The suspension solution was stirred at 75°C for 24 h to yield white precipitates. The product was filtered, washed with distilled water, and dried in a vacuum oven at 60°C for 12 hrs.Figure 1
Schematic preparation of the three-type vinyl polymer-clay nanocomposite by radiation-induced polymerization.


## 2.4. Preparation of the Vinyl Polymer-Clay Nanocomposite Membrane by the Solvent Casting Method after Radiation-Induced Copolymerization of Vinyl Monomers

Figure1 shows schematic preparation of the three-type vinyl polymer-clay nanocomposite by radiation-induced polymerization and the used vinyl monomer structure. The NaSS was used in order to obtain the sulfonate group (–SO3Na) as the cation-exchange group. The St, HEMA, and AAc were used in order to prepare the membrane. Table 1 exhibits the preparation condition of the three-type vinyl polymer-clay nanocomposites for the DMFC membrane. The suspension solution was bubbled with nitrogen gas to remove oxygen for 30 min and irradiated from a Co-60 source under atmospheric pressure and ambient temperature. A total irradiation dose of 30 kGy (dose rate = 6.48 × 105 h−1) was used. The final products were filtered and then dried in a vacuum oven at 50°C for 6 h.Table 1
Preparation condition of three-type vinyl polymer-clay nanocomposites for DMFC membranea.
Sample
St (g)
HEMA (g)
NaSS (g)
AAc (g)
O-MMT (g)
MeOH (mL)
H2O (mL)
2-Propanol (mL)
Number 1
18.0
—
—
27.0
3.50
200
200
40.0
Number 2
—
18.0
—
27.0
3.50
200
200
40.0
Number 3
—
—
18.0
27.0
3.50
200
200
40.0
aTotal irradiation dose = 30 kGy (dose rate = 6.48 × 105/h).The vinyl polymer-clay nanocomposite membrane was prepared by drying the polymer-clay nanocomposite DMF solution (7.0 wt.-%) in a glass plate at 70°C for 24 hrs.


## 2.5. Characterizations

The surface Fourier transform infrared (FT-IR) absorption spectra were obtained with FT-IR spectrum IS10 spectrometer (Thermo scientific Co., USA) in the range of 4000–650 cm−1. The surface morphology of the polymer-clay nanocomposites was determined by FE-TEM (JEOL, JEM-2100F, USA) and FE-SEM (S-4800, Hitachi Science System Co., Japan). Thermal gravimetric analysis (TGA) was conducted on a Scinco TGA S-1000 (Seoul, Korea) under N2 flow from 25°C to 700°C at a heating rate of 20°C min−1. The water uptake (%) was determined as follows:
(1)
Water
uptake
(
%
)
=
[
(
W
w
W
g
)
·
W
g
-
1
]
×
100
,
where W
w and W
g are the weight of the polymer-clay nanocomposite membrane in the wetting and drying condition, respectively. In order to determine ion-exchange capacity of the polymer-clay nanocomposite membrane, the prepared membrane (1.0 cm × 1.0 cm) was placed in 0.5 M HCl solution for 24 hrs and then the membrane with sulfonic acid (–SO3H) was inserted into 1.0 M NaCl solution for 24 hrs. The solution with H+ ions was titrated with 0.01 M NaOH solution. Here, ion-exchange capacity (meq/g) of the polymer-clay nanocomposite membrane was determined by titration method as in the following equation:
(2)
Ion-exchange
capacity
(
meq
/
g
)
=
(
N
NaOH
×
V
NaOH
)
W
g
,
where the N
NaOH and V
NaOH mean the normal concentration and volume for the addition of NaOH solution, respectively. The proton conductivity (S/cm) of the polymer-clay nanocomposite membrane was measured by AC impedance (IM-6ex, Zahner, Germany). The proton conductivity of the polymer-clay nanocomposite membrane was calculated as in the following equation:
(3)
σ
=
L
R
×
A
,
where σ is proton conductivity of the membrane, L and R mean the length between the Pt electrode and the measured value from AC impedance, respectively. A is the area of the polymer-clay nanocomposite membrane.The fuel cell performance was performed via the poly(AAc-co-NaSS)-clay nanocomposite membrane assembly (MEA) as shown Figure 2. The anode catalyst inks were firstly prepared by mixing 2.0 mg of commercial 80 wt.% PtRu/Vulcan catalysts in isopropanol alcohol with 5.0% Nafion solution. The anode electrode was prepared by coating of the anode catalyst ink onto the carbon paper surface. The cathode catalysts inks were also prepared by homogeneous mixing of 2.0 mg commercial Pt/Vulcan. Afterwards, the single-cell MEA was fabricated by hot pressing the two electrodes with the prepared PEM under a pressure of 100 Kg cm−2 at 135°C for 10 min. The single-cell MEA was installed in a fuel-cell test station (PRO200F, Propower Co., Korea). MeOH solution with 1.0 M flowed on rates of 900 mL/min and air flowed on the rates of 2.0 mL·min−1. Measurements of the polarization curves (voltage versus current density) were conducted under various temperatures.Schematic fabrication of MEA using poly(AAc-co-NaSS)-clay nanocomposite membrane for DMFC.
(a)
(b)


## 3. Results and Discussion

### 3.1. Characterization of Vinyl Polymer-Clay Nanocomposite Membrane

Figure3 presents the FT-IR spectra of Na+-MMT (a) O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1 in the wavenumber 650 to 4000 cm−1. In the pristine Na+-MMT (Figure 3(a)), a clear broad band in the region 3300–3700 cm−1 was observed which corresponds to the –OH stretching vibration. The band has two features at 3620 cm−1 and 3440 cm−1 that can be attributed to the presence of two types of O–H groups: isolated O–H groups and those involved in hydrogen bonding. The peak observed at 1630 cm−1 is related to the bending vibration mode of hydrated water molecules and weakly bonded water molecules [18]. The strong broad band in the region of 990–1160 cm−1 is likely due to siloxane (Si–O–Si) bond. The nanocomposite prepared by intercalation of imidazolium salt within the interlayer spacing of MMT shows different features in the FT-IR spectra compared to those of pure constituents. In the O-MMT system (Figure 3(b)), it is clear that the intercalation of imidazolium cation has a significant impact upon the structure of MMT. The typical bans of 3620 and 3440 cm−1 in MMT were changed to a new intense band centered at 3620 cm−1 in O-MMT, which corresponds to the increase of isolated hydroxyl groups and the decrease of hydrogen bonding –OH groups. The peak at 1630 cm−1 corresponding to hydrated water molecules in O-MMT is disappeared. This is possibly due to the effect of organophilic transformation of the MMT surfaces caused by [EPMBIM]+[Cl]−. Moreover, imidazolium cation moieties in the interlayer spacing MMT are determined by the existence of small peaks around 1570 and 1467 cm−1 corresponding to stretching vibration bands of the imidazole ring.Figure 3
FR-IR spectra of Na+-MMT (a), O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1.The vinyl group of the O-MMT can be inserted in functional vinyl polymers by radiation-induced copolymerization of the functional vinyl monomers such as sodium styrene sulfonate (NaSS). As results, the O-MMT was well dispersed onto functional vinyl polymers. In the poly(St-co-NaSS)-clay nanocomposite membrane (Figure 3(c)), the characteristic absorption bands were observed at 1490 and 1598 cm−1 related to the C=C stretching of the aromatic ring, respectively. The sharp bands at 692 and 754 cm−1 correspond to the C–H bending vibration of 1,4-disubstituted benzene. The characteristic –SO
2
- stretching appeared at 1412 cm−1 due to the sulfonate site of the poly(NaSS) in nanocomposite membrane. In poly(HEMA-co-NaSS)- and poly(AAc-co-NaSS)-clay composite, the characteristic >C=O stretching peaks at approximately 1750 cm−1 due to poly(HEMA) and poly(AAc) in the nanocomposite membrane was shown and the characteristic –SO
2
- stretching appeared at 1412 cm−1 due to the sulfonate site of poly(NaSS) in the nanocomposite membrane. As results, vinyl polymer-clay nanocomposite membranes were successfully synthesized.Figure4 shows TGA curves of Na+-MMT (a), O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1. In Na+-MMT of Figure 4(a), the first weight loss was observed below 110°C due to moisture. In Figure 4(b) (O-MMT), a small amount of the first weight loss around 100°C due to moisture existed on the imidazolium site of O-MMT, and second weigh loss appeared from 300°C to 500°C due to [EPMBIM] onto O-MMT. The graft yield (%) of [EPMBIM] onto O-MMT was calculated about 25% from TGA curve data. As results, the O-MMT was successfully prepared by the ion-exchange reaction. In the poly(St-co-NaSS)-clay nanocomposite membrane (Figure 4(c)), the small amount of the first weights (%) at 100°C due to moisture onto the sulfonate site of poly(St-co-NaSS) and second weight loss at 450°C due to main chain degradation of copolymer matrix was observed. The residue weight (%) of poly(St-co-NaSS) was to be 75% because of carbonation of the copolymer matrix. In Figure 4(d), a small amount of first weight loss (%) was also observed around ~100°C due to moisture, and second weighs loss at 400°C due to degradation of the copolymer matrix. Similar degradation patterns were also observed in the poly(AAc-co-NaSS)-clay nanocomposite membrane; see Figure 4(e). From these results, the vinyl polymer-clay nanocomposite membranes were successfully prepared by the solvent casting method after radiation-induced copolymerization of feed with the functional vinyl monomers as one-step preparation.Figure 4
TGA curves of Na+-MMT (a), O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1.The microstructures of TEM images of Na+-MMT, O-MMT, and vinyl polymer-clay nanocomposites membrane observed by TEM are shown in Figure 5. The sheets of clay are about 200–300 nm. Individual clay layers are observed looks like line structure onto copolymer. The well-exfoliated clay sheets are indeed observed to be disorderly dispersed in the copolymer matrix (Figure 5, numbers 1, 2, and 3). As a result, the polymer-clay nanocomposite membranes are successfully prepared by radiation-initiated copolymerization of feed with functional vinyl monomers in the presence of O-MMT with the active vinyl group.TEM images of Na+-MMT, O-MMT, and vinyl polymer-clay nanocomposites in Table 1.
(a)
(b)
(c)
(d)
(e)Figure6 exhibits surface SEM and cross-section images of the poly(AAc-co-NaSS)-clay nanocomposite membrane (number 3 in Table 1). In the cross-section image of the membrane, the layer structure appeared due to the clay layer. From these results, we expect to decrease MeOH permeability since the clay layer protects against MeOH permeation.SEM images of the poly(St-co-NaSS)-clay nanocomposite membrane (number 1 in Table 1).
(a)
(b)Figure7 shows ion-exchange capacity (IEC) of vinyl polymer-clay nanocomposite membranes at 25°C. In order to compare ion-exchange capacity, the commercial Nafion 117 membrane was also measured and denoted in Figure 7. The IEC provides an indication of the ion exchangeable groups presenting in a polymer matrix. The IEC of the vinyl polymer-clay nanocomposite membrane with the sulfonate group was higher than that of the commercial Nafion 117 membrane. We expect the high IEC for poly(AAc-co-NaSS)-clay membrane compared to that of the poly(St-co-NaSS)-clay membrane and poly(HEMA-co-NaSS)-clay membrane because of the presence of carboxylic acid and the sulfonate group. However, the highest IEC could be obtained by the poly(St-co-NaSS)-clay nanocomposite membrane because of hydrophilic/hydrophobic interface of the polymer structure. As a result, the higher IEC of poly(St-co-NaSS)-clay nanocomposite membrane can be expected to have higher power density in DMFC.Figure 7
Ion-exchange capacity of vinyl polymer-clay nanocomposite membranes at 25°C.Figure8 exhibits the proton conductivity of vinyl polymer-clay nanocomposite membranes and commercial Nafion 117 membrane at 25°C. The proton conductivity of the poly(St-co-NaSS)-clay nanocomposites was higher than that of the commercial Nafion 117 membrane. We expected the higher conductivity to be poly(AAc-co-NaSS)-clay nanocomposite because the charged anions of –COO− and –S(=O)O−. However, the lower proton conductivity of the poly(AAc-co-NaSS)-clay nanocomposite membrane was obtained because of hydrogen bonds between carboxylic acid and sulfonic acid in the polymer structure. Many researchers [19, 20] reported that the proton can transport through the hydrophilic channels at the hydrophilic/hydrophobic interface of the polymer microstructure.Figure 8
Proton conductivity of vinyl polymer-clay nanocomposite membranes at 25°C.Figure9 shows water uptake (%) of vinyl polymer-clay nanocomposite membranes at 25°C. Adequate water uptake and successful possession of water molecules are required for effective proton transport across the membrane. However, the water swelling ratio should also be carefully considered because excessive swelling reduces dimensional stability and affects the mechanical properties of the polymer electrolyte membranes. Despite the high water uptake of the poly(AAc-co-NaSS)-clay nanocomposite membrane, the swelling ratio is high, but the poly(St-co-NaSS)-clay nanocomposite membrane possessed the high water uptake and no swelling effects. As a result, the poly(St-co-NaSS)-clay nanocomposite membrane can be successfully used in DMFC membrane.Figure 9
Water uptake of vinyl polymer-clay nanocomposite membranes at 25°C.Table2 summarized the physical and electrochemical properties of the vinyl polymer-clay nanocomposites membrane prepared by radiation-induced copolymerization of feed with functional vinyl monomers for DMFC. In addition, the physical and electrochemical properties of the commercial Nafion-117 membrane were listed in order to compare properties. The MeOH permeability for the vinyl polymer-clay nanocomposite membrane was lower than that of the commercial Nafion-117 membrane. From these results, the poly(St-co-NaSS)-clay nanocomposites membrane with hydrophilic/hydrophobic interface in polymer nanostructure can be used in the DMFC membrane.Table 2
Physical and electrochemical properties of vinyl polymer-clay nanocomposites membrane for DMFC.
Membrane
Thickness (μm)a
Proton conductivity (S/cm)b
Water uptake (%)c
Ion-exchange capacity (meq/g)d
MeOH permeability (mmol·cm−2·s−1)e
Number 1
40.0
0.0779
32.4
3.63
7.7 × 10−9
Number 2
50.0
0.425
22.2
2.83
ND
Number 3
50.0
0.0524
50.4
3.04
4.4
×
10
-
6
Nafion 117
180
0.0721
5.26
0.90
2.2 × 10−10
aDetermined by venier calipers. bDetermined by a AC impedance. cDetermined by dropping test. dDetermined by titration method. eDetermined by GC-FID. ND: not determined.


### 3.2. DMFC Performance for Poly(AAc-co-NaSS)-Clay Nanocomposite Membrane

In order to know membrane ability, the DMFC performance was performed using MEA with the commercial catalysts. Figure10 shows DMFC performance of the poly(St-co-NaSS)-clay nanocomposite membrane (a) and poly(AAc-co-NaSS)-clay nanocomposite membrane (b) at 60°C. The operating condition of the cathode and anode electrode was fixed in two DMFC performances except for the membrane. As you can see, power density on DMFC performance with the poly(St-co-NaSS)-clay nanocomposite membrane being higher than that of the poly(AAc-co-NaSS)-clay nanocomposite membrane. From these results, the poly(St-co-NaSS)-clay nanocomposite membrane prepared by radiation-initiated copolymerization of the functional vinyl monomers can be used as a separator in a direct methanol fuel cell.DMFC performance of the poly(St-co-NaSS)-clay nanocomposite membrane (a) and poly(AAc-co-NaSS)-clay nanocomposite membrane (b) at 60°C.
(a)
(b)


## 3.1. Characterization of Vinyl Polymer-Clay Nanocomposite Membrane

Figure3 presents the FT-IR spectra of Na+-MMT (a) O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1 in the wavenumber 650 to 4000 cm−1. In the pristine Na+-MMT (Figure 3(a)), a clear broad band in the region 3300–3700 cm−1 was observed which corresponds to the –OH stretching vibration. The band has two features at 3620 cm−1 and 3440 cm−1 that can be attributed to the presence of two types of O–H groups: isolated O–H groups and those involved in hydrogen bonding. The peak observed at 1630 cm−1 is related to the bending vibration mode of hydrated water molecules and weakly bonded water molecules [18]. The strong broad band in the region of 990–1160 cm−1 is likely due to siloxane (Si–O–Si) bond. The nanocomposite prepared by intercalation of imidazolium salt within the interlayer spacing of MMT shows different features in the FT-IR spectra compared to those of pure constituents. In the O-MMT system (Figure 3(b)), it is clear that the intercalation of imidazolium cation has a significant impact upon the structure of MMT. The typical bans of 3620 and 3440 cm−1 in MMT were changed to a new intense band centered at 3620 cm−1 in O-MMT, which corresponds to the increase of isolated hydroxyl groups and the decrease of hydrogen bonding –OH groups. The peak at 1630 cm−1 corresponding to hydrated water molecules in O-MMT is disappeared. This is possibly due to the effect of organophilic transformation of the MMT surfaces caused by [EPMBIM]+[Cl]−. Moreover, imidazolium cation moieties in the interlayer spacing MMT are determined by the existence of small peaks around 1570 and 1467 cm−1 corresponding to stretching vibration bands of the imidazole ring.Figure 3
FR-IR spectra of Na+-MMT (a), O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1.The vinyl group of the O-MMT can be inserted in functional vinyl polymers by radiation-induced copolymerization of the functional vinyl monomers such as sodium styrene sulfonate (NaSS). As results, the O-MMT was well dispersed onto functional vinyl polymers. In the poly(St-co-NaSS)-clay nanocomposite membrane (Figure 3(c)), the characteristic absorption bands were observed at 1490 and 1598 cm−1 related to the C=C stretching of the aromatic ring, respectively. The sharp bands at 692 and 754 cm−1 correspond to the C–H bending vibration of 1,4-disubstituted benzene. The characteristic –SO
2
- stretching appeared at 1412 cm−1 due to the sulfonate site of the poly(NaSS) in nanocomposite membrane. In poly(HEMA-co-NaSS)- and poly(AAc-co-NaSS)-clay composite, the characteristic >C=O stretching peaks at approximately 1750 cm−1 due to poly(HEMA) and poly(AAc) in the nanocomposite membrane was shown and the characteristic –SO
2
- stretching appeared at 1412 cm−1 due to the sulfonate site of poly(NaSS) in the nanocomposite membrane. As results, vinyl polymer-clay nanocomposite membranes were successfully synthesized.Figure4 shows TGA curves of Na+-MMT (a), O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1. In Na+-MMT of Figure 4(a), the first weight loss was observed below 110°C due to moisture. In Figure 4(b) (O-MMT), a small amount of the first weight loss around 100°C due to moisture existed on the imidazolium site of O-MMT, and second weigh loss appeared from 300°C to 500°C due to [EPMBIM] onto O-MMT. The graft yield (%) of [EPMBIM] onto O-MMT was calculated about 25% from TGA curve data. As results, the O-MMT was successfully prepared by the ion-exchange reaction. In the poly(St-co-NaSS)-clay nanocomposite membrane (Figure 4(c)), the small amount of the first weights (%) at 100°C due to moisture onto the sulfonate site of poly(St-co-NaSS) and second weight loss at 450°C due to main chain degradation of copolymer matrix was observed. The residue weight (%) of poly(St-co-NaSS) was to be 75% because of carbonation of the copolymer matrix. In Figure 4(d), a small amount of first weight loss (%) was also observed around ~100°C due to moisture, and second weighs loss at 400°C due to degradation of the copolymer matrix. Similar degradation patterns were also observed in the poly(AAc-co-NaSS)-clay nanocomposite membrane; see Figure 4(e). From these results, the vinyl polymer-clay nanocomposite membranes were successfully prepared by the solvent casting method after radiation-induced copolymerization of feed with the functional vinyl monomers as one-step preparation.Figure 4
TGA curves of Na+-MMT (a), O-MMT (b), number 1 (c), number 2 (d), and number 3 (e) in Table 1.The microstructures of TEM images of Na+-MMT, O-MMT, and vinyl polymer-clay nanocomposites membrane observed by TEM are shown in Figure 5. The sheets of clay are about 200–300 nm. Individual clay layers are observed looks like line structure onto copolymer. The well-exfoliated clay sheets are indeed observed to be disorderly dispersed in the copolymer matrix (Figure 5, numbers 1, 2, and 3). As a result, the polymer-clay nanocomposite membranes are successfully prepared by radiation-initiated copolymerization of feed with functional vinyl monomers in the presence of O-MMT with the active vinyl group.TEM images of Na+-MMT, O-MMT, and vinyl polymer-clay nanocomposites in Table 1.
(a)
(b)
(c)
(d)
(e)Figure6 exhibits surface SEM and cross-section images of the poly(AAc-co-NaSS)-clay nanocomposite membrane (number 3 in Table 1). In the cross-section image of the membrane, the layer structure appeared due to the clay layer. From these results, we expect to decrease MeOH permeability since the clay layer protects against MeOH permeation.SEM images of the poly(St-co-NaSS)-clay nanocomposite membrane (number 1 in Table 1).
(a)
(b)Figure7 shows ion-exchange capacity (IEC) of vinyl polymer-clay nanocomposite membranes at 25°C. In order to compare ion-exchange capacity, the commercial Nafion 117 membrane was also measured and denoted in Figure 7. The IEC provides an indication of the ion exchangeable groups presenting in a polymer matrix. The IEC of the vinyl polymer-clay nanocomposite membrane with the sulfonate group was higher than that of the commercial Nafion 117 membrane. We expect the high IEC for poly(AAc-co-NaSS)-clay membrane compared to that of the poly(St-co-NaSS)-clay membrane and poly(HEMA-co-NaSS)-clay membrane because of the presence of carboxylic acid and the sulfonate group. However, the highest IEC could be obtained by the poly(St-co-NaSS)-clay nanocomposite membrane because of hydrophilic/hydrophobic interface of the polymer structure. As a result, the higher IEC of poly(St-co-NaSS)-clay nanocomposite membrane can be expected to have higher power density in DMFC.Figure 7
Ion-exchange capacity of vinyl polymer-clay nanocomposite membranes at 25°C.Figure8 exhibits the proton conductivity of vinyl polymer-clay nanocomposite membranes and commercial Nafion 117 membrane at 25°C. The proton conductivity of the poly(St-co-NaSS)-clay nanocomposites was higher than that of the commercial Nafion 117 membrane. We expected the higher conductivity to be poly(AAc-co-NaSS)-clay nanocomposite because the charged anions of –COO− and –S(=O)O−. However, the lower proton conductivity of the poly(AAc-co-NaSS)-clay nanocomposite membrane was obtained because of hydrogen bonds between carboxylic acid and sulfonic acid in the polymer structure. Many researchers [19, 20] reported that the proton can transport through the hydrophilic channels at the hydrophilic/hydrophobic interface of the polymer microstructure.Figure 8
Proton conductivity of vinyl polymer-clay nanocomposite membranes at 25°C.Figure9 shows water uptake (%) of vinyl polymer-clay nanocomposite membranes at 25°C. Adequate water uptake and successful possession of water molecules are required for effective proton transport across the membrane. However, the water swelling ratio should also be carefully considered because excessive swelling reduces dimensional stability and affects the mechanical properties of the polymer electrolyte membranes. Despite the high water uptake of the poly(AAc-co-NaSS)-clay nanocomposite membrane, the swelling ratio is high, but the poly(St-co-NaSS)-clay nanocomposite membrane possessed the high water uptake and no swelling effects. As a result, the poly(St-co-NaSS)-clay nanocomposite membrane can be successfully used in DMFC membrane.Figure 9
Water uptake of vinyl polymer-clay nanocomposite membranes at 25°C.Table2 summarized the physical and electrochemical properties of the vinyl polymer-clay nanocomposites membrane prepared by radiation-induced copolymerization of feed with functional vinyl monomers for DMFC. In addition, the physical and electrochemical properties of the commercial Nafion-117 membrane were listed in order to compare properties. The MeOH permeability for the vinyl polymer-clay nanocomposite membrane was lower than that of the commercial Nafion-117 membrane. From these results, the poly(St-co-NaSS)-clay nanocomposites membrane with hydrophilic/hydrophobic interface in polymer nanostructure can be used in the DMFC membrane.Table 2
Physical and electrochemical properties of vinyl polymer-clay nanocomposites membrane for DMFC.
Membrane
Thickness (μm)a
Proton conductivity (S/cm)b
Water uptake (%)c
Ion-exchange capacity (meq/g)d
MeOH permeability (mmol·cm−2·s−1)e
Number 1
40.0
0.0779
32.4
3.63
7.7 × 10−9
Number 2
50.0
0.425
22.2
2.83
ND
Number 3
50.0
0.0524
50.4
3.04
4.4
×
10
-
6
Nafion 117
180
0.0721
5.26
0.90
2.2 × 10−10
aDetermined by venier calipers. bDetermined by a AC impedance. cDetermined by dropping test. dDetermined by titration method. eDetermined by GC-FID. ND: not determined.


## 3.2. DMFC Performance for Poly(AAc-co-NaSS)-Clay Nanocomposite Membrane

In order to know membrane ability, the DMFC performance was performed using MEA with the commercial catalysts. Figure10 shows DMFC performance of the poly(St-co-NaSS)-clay nanocomposite membrane (a) and poly(AAc-co-NaSS)-clay nanocomposite membrane (b) at 60°C. The operating condition of the cathode and anode electrode was fixed in two DMFC performances except for the membrane. As you can see, power density on DMFC performance with the poly(St-co-NaSS)-clay nanocomposite membrane being higher than that of the poly(AAc-co-NaSS)-clay nanocomposite membrane. From these results, the poly(St-co-NaSS)-clay nanocomposite membrane prepared by radiation-initiated copolymerization of the functional vinyl monomers can be used as a separator in a direct methanol fuel cell.DMFC performance of the poly(St-co-NaSS)-clay nanocomposite membrane (a) and poly(AAc-co-NaSS)-clay nanocomposite membrane (b) at 60°C.
(a)
(b)


## 4. Conclusion

Vinyl polymer-clay nanocomposite membranes were synthesized by radiation-induced copolymerization of the functional monomers as a one-step reaction. Polymers were included in poly(St-co-NaSS), poly(HEMA-co-NaSS), and poly(AAc-co-NaSS), respectively. The physical and electrochemical properties of the vinyl polymer-clay nanocomposites membrane were evaluated in order to be applied in the DMFC membrane. Among them, the poly(St-co-NaSS)-clay nanocomposite membrane with hydrophilic/hydrophobic interface in the polymer nanostructure exhibited good physical and chemical properties and high power density. The poly(St-co-NaSS)-clay nanocomposite membrane prepared by radiation-initiated copolymerization of the functional vinyl monomers can be used as a separator in DMFC on behalf of the commercial Nafion-117 membrane.



---