# An Expedient SERS Strip Tactic for Rapid On-Site Detection with Long-Time Sensitivity and Repeatability

Authors: Chen Wang; Yueqian Wan; Yong Su; Yafei Cai; Shengjun Xiong; Ding Yuan; Zheng Xia; Jie Zhu
Journal: Advances in Materials Science and Engineering
 (2021)

---

## Abstract

Surface-enhanced Raman spectroscopy (SERS) has attracted lots of interest in academic and industrial fields in recent years. The improvement in long-time sensitivity and repeatability is highly demanded by the on-site applications. Herein, we present an expedient SERS strip tactic with these desired advantages. Specifically, the tactic utilized the outstanding stability of colloidal particles to maintain the SERS materials during the storage. Upon usage, the strip is rapidly prepared on-site, and then the targets were sampled with a dip-coating and heating method, which is designed to standardize the whole detection process with the sensitivity kept. Thanks to the tactic, only one-third of SERS sensitivity decay was observed for rhodamine 6G after half a year. Besides rhodamine 6G, the SERS spectra of different animal blood samples were also investigated with the SERS strip tactic, and a species-based discrimination capability was preliminarily demonstrated.


---

## Body

## 1. Introduction

Raman spectroscopy is a kind of fingerprint spectra resulting from the vibration of chemical bonds, which could be used to identify the molecules and materials [1]. The measurement of Raman spectra is noninvasive, fast, and resistant to water interference. Additionally, the applications of surface-enhanced Raman spectroscopy (SERS) have extended to trace detection fields [1–5], such as the sniffing of explosives [6], drugs [7], pesticide residues [8], prohibited food additions [9], and microorganism identifications [10, 11]. With the development of hand-held Raman spectrometers, the detection method has demonstrated great potential for on-site trace detection and identification, and therefore, the sensing materials with long-term sensitivity, repeatability, and low cost become highly desired [12].The amplification of electromagnetic fields generated by the excitation of localized surface plasma is the source of SERS and roughened surface could enhance the amplification and the adsorption of target molecules [13]. Chemical synthesized colloidal nanoparticles (NPs) of Ag and Au are the major source of SERS materials due to their low cost, long lifetime, and high sensitivity [14]. However, the issues on repeatability and inconvenient operations may still hinder the SERS applications. For example, due to ions, temperature, and organic solvents, the colloidal is easy to aggregate quickly after the samples are transferred in to the colloids, causing low uniformity of the samples and consequential uncertainty of the measurements [15]. Additionally, the use of colloidal NPs requires precise liquid transferring operation in microliter levels. To achieve expedient usage, better sensitivity, and repeatability, the paper-based SERS strips fabricated with printed NPs were explored, and the NPs on the strips were closely stacked on the substrates [16]. Due to the high surface energy and the lack of protection of solvents, the Ostwald ripening of the NPs, and the reaction between NPs with oxygen, humidity and even paper substrates can gradually lower the sensitivity of the conventional SERS strips, leading to a short lifetime in days.To increase the ease of operations, the repeatability of colloidal NPs, and the short lifetime of conventional SERS strips, herein we introduce a hybrid tactic to improve the long-time sensitivity and repeatability of SERS detection with simple operations as shown in Scheme1, which is suitable for rapid on-site applications [17]. In detail, chemically synthesized colloidal AgNPs were prepared and maintained for the low cost and great storage stability. Upon usage, sensing strips were fabricated through the direct dip-coating of colloidal NPs onto the blank paper, followed by rapid heating of a microheater. During target sampling, the as-prepared strip was directly dipped into the sample solution and then heated with the same microheater to accelerate the operation and to avoid the “coffee ring” effect [18, 19]. Therefore, in a single detection, the strip was always freshly fabricated from the stable colloidal NPs to ensure the long-time sensitivity, and the whole process was standardized with dipping and heating operations for better uniformity and repeatability without any liquid transferring operations and unexpected aggregation of NPs. Additionally, the strip fabrication step and target sampling step could be repeated several times to increase the overall sensitivity of the strips. With this SERS strip tactic, the spectra of rhodamine 6G (Rh6G) solution and diluted blood samples from different animals were studied with a hand-held Raman spectrometer to mimic the on-site application scenes. The Raman spectra of Rh6G and blood samples were clearly observed, and the blood samples could be further partially discriminated based on the animal species. This proof-of-concept work may demonstrate a potential application of the SERS technique in forensic and wild animal protection fields [20].Scheme 1
The general detection operations of the SERS strip tactic.


## 2. Materials and Methods

### 2.1. Preparation of Colloidal AgNPs

Colloidal AgNPs were prepared following the similar method of previous literature [16]. To increase the concentration of AgNPs, the concentrations of the precursors were tripled compared to the original method. In a typical preparation, 90 mg of AgNO3 was added to 160 ml ultrapure water and then heated in a round-bottom flask with 120°C with vigorous stirring for 10 minutes. Then, 10 ml of a solution containing 100 mg of sodium citrate was added to the flask dropwise within 5 minutes. After half an hour, the solution turned brown grey and was removed from the heating bath to cool down to room temperature.


### 2.2. General Detection Operations of the SERS Strip Tactic

The SERS strip tactic for on-site applications requires a microheater containing a precise closed-loop temperature control plate, blank strips made from Fisherbrand pure cellulose chromatography paper, vials containing the prepared colloidal AgNPs, empty vials for liquid samples, and a hand-held Raman spectrometer. And the general detection operations include three steps. The first step is the fabrication of a test strip. The temperature of the microheater was optimized to 65 °C for strip fabrication. A blank strip (∼4 cm × 0.5 cm) was directly dipped into the colloidal AgNPs vial for 5 seconds and then was quickly pulled out with a following baking for 1 minute with the microheater. The first step could be performed a few times to enhance the detection sensitivity. The second step is the sample preparation and transferring. The target molecule or material should be in a liquid state itself or dissolved in a certain kind of solvent to form a homogeneous state, which is suitable for strip dipping. The insoluble materials should be filtered before sampling to avoid possible interference left on the strip surface. Then, a fabricated strip is dipped to the sample vial for 5 seconds, which contains the solution of target samples. Similar to the first step, the strip is taken out and baked for 1 minute with the microheater, and this process could also be done for multiple times to accumulate the target molecules within the strip. The temperature of the microheater should be optimized for different samples. For Rh6G and blood samples, the temperature was kept as 65°C. The third step is the spectrum measurement. The freshly prepared strip with target molecules is directly measured with a hand-held Raman spectrometer. The central area of a strip is recommended to avoid the edge effect of the strip. All the blood samples were kept in −20°C refrigerator and contained trisodium citrate as the anticoagulant. Before sampling, they were diluted by 10 times with 0.9% NaCl water solution. In the experiments, the strips were dip-coated and heated for three times, and the blood samples were dipped and heated for once.


### 2.3. Morphological and Spectral Characterizations

The Raman spectra were characterized with a hand-held Raman spectrometer (model CR-2000, HT-NOVA Co., Ltd.) in all the experiments. The excitation laser is 785 nm, and the detectable wavelength ranges 200∼3200 cm−1 with the spectral resolution ranging 4∼6 cm−1. Morphological observations were conducted by scanning electron microscopy (SEM, Carl Zeiss, Supra 55) and transmission electron microscope (TEM, FEI, Tecnai F30).


## 2.1. Preparation of Colloidal AgNPs

Colloidal AgNPs were prepared following the similar method of previous literature [16]. To increase the concentration of AgNPs, the concentrations of the precursors were tripled compared to the original method. In a typical preparation, 90 mg of AgNO3 was added to 160 ml ultrapure water and then heated in a round-bottom flask with 120°C with vigorous stirring for 10 minutes. Then, 10 ml of a solution containing 100 mg of sodium citrate was added to the flask dropwise within 5 minutes. After half an hour, the solution turned brown grey and was removed from the heating bath to cool down to room temperature.


## 2.2. General Detection Operations of the SERS Strip Tactic

The SERS strip tactic for on-site applications requires a microheater containing a precise closed-loop temperature control plate, blank strips made from Fisherbrand pure cellulose chromatography paper, vials containing the prepared colloidal AgNPs, empty vials for liquid samples, and a hand-held Raman spectrometer. And the general detection operations include three steps. The first step is the fabrication of a test strip. The temperature of the microheater was optimized to 65 °C for strip fabrication. A blank strip (∼4 cm × 0.5 cm) was directly dipped into the colloidal AgNPs vial for 5 seconds and then was quickly pulled out with a following baking for 1 minute with the microheater. The first step could be performed a few times to enhance the detection sensitivity. The second step is the sample preparation and transferring. The target molecule or material should be in a liquid state itself or dissolved in a certain kind of solvent to form a homogeneous state, which is suitable for strip dipping. The insoluble materials should be filtered before sampling to avoid possible interference left on the strip surface. Then, a fabricated strip is dipped to the sample vial for 5 seconds, which contains the solution of target samples. Similar to the first step, the strip is taken out and baked for 1 minute with the microheater, and this process could also be done for multiple times to accumulate the target molecules within the strip. The temperature of the microheater should be optimized for different samples. For Rh6G and blood samples, the temperature was kept as 65°C. The third step is the spectrum measurement. The freshly prepared strip with target molecules is directly measured with a hand-held Raman spectrometer. The central area of a strip is recommended to avoid the edge effect of the strip. All the blood samples were kept in −20°C refrigerator and contained trisodium citrate as the anticoagulant. Before sampling, they were diluted by 10 times with 0.9% NaCl water solution. In the experiments, the strips were dip-coated and heated for three times, and the blood samples were dipped and heated for once.


## 2.3. Morphological and Spectral Characterizations

The Raman spectra were characterized with a hand-held Raman spectrometer (model CR-2000, HT-NOVA Co., Ltd.) in all the experiments. The excitation laser is 785 nm, and the detectable wavelength ranges 200∼3200 cm−1 with the spectral resolution ranging 4∼6 cm−1. Morphological observations were conducted by scanning electron microscopy (SEM, Carl Zeiss, Supra 55) and transmission electron microscope (TEM, FEI, Tecnai F30).


## 3. Results and Discussion

### 3.1. Preparation of Test Strips and Morphological Characterizations

Figure1(a) exhibits the microheater designed for the SERS strip tactic. The heating zone consisted of a closed-loop controlled heater targeting 65°C and a hollow cover to allow the escape of water vapor generated during the baking. The fast evaporation of the solvent could restrain the “coffee ring” effect, which is a common reason for heterogeneity in the wet coating process. The prepared AgNPs had good dispersion in the colloidal solution, ensuring the uniformity of dip-coating of the strips. To begin the detection, the blank test strip was dipped into the vial containing the colloidal AgNPs for 5 seconds, as shown in Figure 1(b). Then, the strip was placed in the microheater to fabricate the test strip rapidly. After the baking, the color of the strip with AgNPs appeared to be light grey. As a control, the blank test strip was also baked following the same procedure, while the color remained white, indicating the color change should be due to the adhesion of AgNPs onto the paper. When the first cycle of dip-coating and heating was done, there is an option to repeat the fabrication to further enrich the AgNPs on the surface. Figure 1(c) displays the strips with different cycles of fabrications ranging from zero to five. Correspondingly, the color of these strips becomes darker and darker, demonstrating the net accumulation of AgNPs on the surface in each fabrication step. When the SERS strips were prepared, they were ready for the target sampling step to contact the liquid sample solutions. Figure 1(d) displays this step for Rh6G water solution, which is quite similar to the strip fabrication step, and this sampling step is also accumulable for better overall sensitivity if necessary.Figure 1
(a) The photo of the microheater, (b) the dip-coating of a test strip into colloidal AgNPs, (c) the prepared test strips with different cycles of dip-coating and heating, and (d) the target sampling of Rh6G solution with a prepared test strip.
(a)(b)(c)(d)To confirm the coherence between the color change of test strips and the accumulation of AgNPs and to further study the AgNPs distribution on the strips, the morphology of colloidal AgNPs and the fabricated strips were characterized with TEM and SEM, respectively. Figure2(a) shows a typical TEM image of AgNPs. The shape of the AgNPs was between spheres and polyhedrons with multiple facets. Their diameters ranged from 35 nm to 50 nm with a narrow distribution. The surface of these AgNPs was clear and sharp. After the fabrication of strips, the central part of the strip was cut for SEM characterization to ensure representativeness. Figures 2(b)∼2(f) show the surface status of the strips with 1∼5 cycles of dip-coating and heating, and Figures S1(a)∼S1(e) also confirm the similar morphological status in larger areas, respectively. After the first cycle, the AgNPs were clearly found on the test strips and formed small clusters containing tens of AgNPs, instead of evenly distributed across the paper interface. Such cluster-like structures may indicate that the interaction between the AgNPs themselves is stronger than the interaction between the AgNPs and paper. So, even with a low amount of AgNPs contact, the aggregation could also be achieved efficiently. After the second cycle, a few small clusters “grew” to tiny islands and more clusters formed, indicating the accumulation was preferred around existing AgNPs with the favourable interaction. Then, in the following cycles, the islands tended to continue growing into large areas, and some clusters started to merge into large islands. After the fifth cycle, the large islands containing a large amount of AgNPs became dominant on the surface of the paper. Therefore, the SEM images may support the positive correlation between the color change and the amount of AgNPs. Additionally, it was clear that, even with once dip-coating and heating, the AgNPs aggregation, or “hot-spots,” efficiently formed and should be capable of offering SERS sensitivity. More fabrication cycles would cause consequent aggregations so that the sensitivity of the strip was also expected to increase.Figure 2
(a) The TEM image of AgNPs and the SEM images of test strips surface after (b) 1 cycle, (c) 2 cycles, (d) 3 cycles, (e) 4 cycles, and (f) 5 cycles of dip-coating and heating. The scale bar of the TEM image is 0.1μm, and the scale bar of the SEM images is 0.5 μm.
(a)(b)(c)(d)(e)(f)


### 3.2. SERS Effect of Rh6G Based on the Strip Tactic

According to the morphological study, the strip tactic implied great potential on the SERS applications with tunable sensitivity. To quantitatively evaluate the performance of the fabricated strips, several series of SERS spectra of Rh6G water solution were measured. Figure3(a) show the first series of SERS spectra of different concentrations of Rh6G sampled by the test strips with three fabrication cycles. The concentration range of Rh6G was from 2 × 10−4 mM to 0.1 mM, and except for the spectra of 2 × 10−4 mM of Rh6G, the spectra from other concentrations showed clear peaks of Rh6G. In Figure S2, multiple spectra of a 5 × 10−3 mM Rh6G solution from different strips confirmed the good reproducibility of the tactic. And for different concentrations, from the low Raman shift side, the six strongest peaks were also identical, located at 612 cm−1, 771 cm−1, 1183 cm−1, 1312 cm−1, 1364 cm−1, and 1510 cm−1, and they were consistent with previous literature, indicating the heating temperature was suitable for Rh6G [21]. Since the spectra of the Rh6G were similar, the peak intensities (with baseline correction) at 1364 cm−1 were calculated and plotted in Figure 3(b). A clear positive correlation relationship between the concentrations and selected peak intensity was found, indicating the qualitative and quantitative capability of the strip tactic.Figure 3
(a) The SERS spectra and (b) the 1364 cm−1 peak intensity plot of different concentrations of Rh6G sampled by test strips with 3 cycles of fabrication and (c) the SERS spectra and (d) the 1364 cm−1 peak intensity plot of 0.6 mM of Rh6G sampled by test strips with different fabrication cycles.
(a)(b)(c)(d)In the second series, the adjustable sensitivity via the number of fabrication cycles was studied. The strips with fabrication cycles from one to five were prepared to measure the SERS spectra of 0.6 mM of Rh6G solution, as shown in Figure3(c). The results demonstrated that, even with only 1 cycle of fabrication, the strip was sensitive enough to provide the SERS spectrum with a high signal-to-noise ratio, which was consistent with the surface AgNPs clusters found in the morphological study of the strips with one cycle of fabrication. Indeed, with the increase of the fabrication cycles, all the characteristic peaks of Rh6G grew gradually, indicating that more AgNPs could enhance the SERS signals. And this effect was also observed for different concentrations of Rh6G, as shown in Figure S3. According to the peak intensity (with baseline correction) at 1364 cm−1, with the same concentration and measurement configuration of the Raman spectrometer, the intensity tunable range contributed by the fabrication cycles was 4-5 times, as shown in Figure 3(d). It was interesting to note that the enchantment ratio from the 2nd to the 4th cycle was relatively higher than the number from the 1st to the 2nd cycle and from the 4th to the 5th cycle. Considering the morphological study, the stages between the 2nd and the 4th cycles could well correspond to the formation of larger islands of AgNPs on the surface. While in the 1st cycle, only small clusters formed and in the 5th cycle, the net accumulation of islands may be limited by dissolve equilibrium. Additionally, combining the flexible dipping times of the sampling step, the total tunable sensitivity windows of this method were over twenty times. Considering the concentrations of target molecules for on-site measurement are usually unknown and enriching target molecules requires mass of work and additional instruments, such unique sensitivity flexibility may greatly assist in the on-site detections for different targets and applications.


### 3.3. Stability of the SERS Strip Tactic

As a practical tactic for on-site detection, besides the sensitivity and ease of use, the long-term stability on performance is essential, especially for quantitative or semiquantitative applications. According to previous literature, the colloid system is relatively stable if stored in a controlled environment, while the paper-based predeposited strips meet the fast decay of sensitivity [16]. This fact is one of the motivations of the tactic that the NPs are stored in the colloidal state and then freshly are prepared into strips on the field with a rapid and controllable microheater. To prove the advantage of this approach, a series of long-time tests of Rh6G spectra with predeposited strips and on-site fabricated strips were conducted with the same batch of colloidal AgNPs. Half of the NPs were used to fabricate strips at the beginning of the experiments with the dip-coating and heating method. These strips were counted as the predeposited strips and immediately packed with an aluminium film plastic bag under vacuum. And the other half of the colloidal AgNPs was kept in vials for the SERS strip tactic. All the strips and colloids were kept at 4°C temperature and in dark. Then, in every 2 days, 0.5 mM of Rh6G water solution was measured with the sealed predeposited strips and the freshly fabricated strips with the stored colloidal AgNPs. After ten days, the measured spectra were compared in Figure 4(a). It was clear that the sensitivity of the predeposited strips decreased significantly though they were carefully sealed, while the sensitivity of the strips fabricated the tactic was almost kept based on the 1364 cm−1 peak intensity plot, as shown in Figure 4(b). Then, in the subsequent experiments, the predeposited strips could barely detect Rh6G solution after one month, while with the strip tactic, the peak intensity of Rh6G spectra only suffers about one-third loss after six months, compared to the initial intensity. Consequently, such on-site fabrication tactic was confirmed to help prevent the sensitivity decay with little sacrifice on strip fabrication time. The advantage on long-term stability, in addition to the tunable sensitivity, could provide a convenient tool for on-site applications.Figure 4
(a) The Raman spectra of 0.5 mM of Rh6G sampled by sealed predeposited strips (up) and strips fabricated with the tactic (down) and (b) the 1364 cm−1 peak intensity plot of these spectra in ten days.
(a)(b)


### 3.4. Detection and Discrimination of Animal Blood Samples

With the confirmation of the sensitivity, long-term stability, and repeatability, the SERS strip tactic was applied to study a series of blood samples, since rapid blood identification is usually desired in forensic and wild animal protection fields, and some previous literature has reported that Raman spectra could be used for the detection and discrimination of blood [22–24]. Although heating would change the biological activity of blood samples, the heating temperature was still set to 65°C because the Raman spectroscopy mainly reveals the information of primary chemical bonds, instead of the folding structures of biomacromolecules. The blood samples from seven species of animals were measured following the general operations for 30 times per species, and all the spectra are demonstrated in Figure S4. The high similarity of the spectra from a certain species indicated the good reproducibility of the strip tactic. Figure 5 shows the average Raman spectra, and compared to the blank test strips, the blood samples showed several specific peaks, such as the peaks at 480 cm−1, 660 cm−1, 1128 cm−1, 1221 cm−1, 1315 cm−1, 1439 cm−1, and 1578 cm−1, which were also observed in other literature [25, 26]. Specifically, 660 cm−1 and 1221 cm−1 are related to haemoglobin in the blood; 1128 cm−1 and 1315 cm−1 may be from the spermine phosphate hexahydrate; and 1439 cm−1 closely matches the Raman bands of serum albumin [27, 28].Figure 5
The average Raman spectra of blood samples from seven species of animals.However, the blood components of large animals are complex, so the characteristic peaks based interpretation into chemical bonds and molecules may be complicated. The identification goal is not only the chemical components but also the species information. Therefore, in a lot of cases, the classification algorithms towards final labels, instead of matching the characteristic peaks, were more frequently applied. Such algorithms mainly require good reproducibility and consistency between the labelled samples and the detected unknown samples and are relatively less influenced by the poetical chemical or physical change during the tests if the same change happens in both the labelled samples and the detected unknown samples. Herein, we applied the principle component analysis (PCA), which was frequently applied for the classification goals [29], to these spectra to attempt to cluster the spectra based on species. Overall, the first two components covered over 95% of the information of the original spectra, indicating the feasibility of the PCA method to these spectra. Figure 6 shows the PCA clustering analysis with a 95% confident range of each cluster. From the overlaps of different species, the SERS signals from the strips could fully discriminate 5 species from each other, such as kangaroo, dog, golden monkey, and sika deer. On the other hand, a part of the spectra of cat blood samples overlapped with the blank strips, which may be caused by relatively weak signals of these spectra. The confident ellipses of cattle and red-crowned crane SERS spectra shared about one-third of samples, which may cause less accurate prediction regarding these two animals. To further verify the classification potential, the third principle component, which carried about 1.5% of the information, was also considered. Under this condition, the spectra from the cat could successfully separate from the blank strips under 95% confidence while cattle and red-crowned crane still cannot be fully distinguished with the SERS strips and the hand-held Raman spectrometer. In summary, in the preliminary experiments, the animal species could be probably discriminated via the Raman spectra of blood under 95% confidence. If the goal is only yes/no binary classification towards a certain kind of species, the true positive rate should be higher.Figure 6
The PCA results of the Raman spectra of seven species of animal blood samples with 95% confident ranges.


## 3.1. Preparation of Test Strips and Morphological Characterizations

Figure1(a) exhibits the microheater designed for the SERS strip tactic. The heating zone consisted of a closed-loop controlled heater targeting 65°C and a hollow cover to allow the escape of water vapor generated during the baking. The fast evaporation of the solvent could restrain the “coffee ring” effect, which is a common reason for heterogeneity in the wet coating process. The prepared AgNPs had good dispersion in the colloidal solution, ensuring the uniformity of dip-coating of the strips. To begin the detection, the blank test strip was dipped into the vial containing the colloidal AgNPs for 5 seconds, as shown in Figure 1(b). Then, the strip was placed in the microheater to fabricate the test strip rapidly. After the baking, the color of the strip with AgNPs appeared to be light grey. As a control, the blank test strip was also baked following the same procedure, while the color remained white, indicating the color change should be due to the adhesion of AgNPs onto the paper. When the first cycle of dip-coating and heating was done, there is an option to repeat the fabrication to further enrich the AgNPs on the surface. Figure 1(c) displays the strips with different cycles of fabrications ranging from zero to five. Correspondingly, the color of these strips becomes darker and darker, demonstrating the net accumulation of AgNPs on the surface in each fabrication step. When the SERS strips were prepared, they were ready for the target sampling step to contact the liquid sample solutions. Figure 1(d) displays this step for Rh6G water solution, which is quite similar to the strip fabrication step, and this sampling step is also accumulable for better overall sensitivity if necessary.Figure 1
(a) The photo of the microheater, (b) the dip-coating of a test strip into colloidal AgNPs, (c) the prepared test strips with different cycles of dip-coating and heating, and (d) the target sampling of Rh6G solution with a prepared test strip.
(a)(b)(c)(d)To confirm the coherence between the color change of test strips and the accumulation of AgNPs and to further study the AgNPs distribution on the strips, the morphology of colloidal AgNPs and the fabricated strips were characterized with TEM and SEM, respectively. Figure2(a) shows a typical TEM image of AgNPs. The shape of the AgNPs was between spheres and polyhedrons with multiple facets. Their diameters ranged from 35 nm to 50 nm with a narrow distribution. The surface of these AgNPs was clear and sharp. After the fabrication of strips, the central part of the strip was cut for SEM characterization to ensure representativeness. Figures 2(b)∼2(f) show the surface status of the strips with 1∼5 cycles of dip-coating and heating, and Figures S1(a)∼S1(e) also confirm the similar morphological status in larger areas, respectively. After the first cycle, the AgNPs were clearly found on the test strips and formed small clusters containing tens of AgNPs, instead of evenly distributed across the paper interface. Such cluster-like structures may indicate that the interaction between the AgNPs themselves is stronger than the interaction between the AgNPs and paper. So, even with a low amount of AgNPs contact, the aggregation could also be achieved efficiently. After the second cycle, a few small clusters “grew” to tiny islands and more clusters formed, indicating the accumulation was preferred around existing AgNPs with the favourable interaction. Then, in the following cycles, the islands tended to continue growing into large areas, and some clusters started to merge into large islands. After the fifth cycle, the large islands containing a large amount of AgNPs became dominant on the surface of the paper. Therefore, the SEM images may support the positive correlation between the color change and the amount of AgNPs. Additionally, it was clear that, even with once dip-coating and heating, the AgNPs aggregation, or “hot-spots,” efficiently formed and should be capable of offering SERS sensitivity. More fabrication cycles would cause consequent aggregations so that the sensitivity of the strip was also expected to increase.Figure 2
(a) The TEM image of AgNPs and the SEM images of test strips surface after (b) 1 cycle, (c) 2 cycles, (d) 3 cycles, (e) 4 cycles, and (f) 5 cycles of dip-coating and heating. The scale bar of the TEM image is 0.1μm, and the scale bar of the SEM images is 0.5 μm.
(a)(b)(c)(d)(e)(f)


## 3.2. SERS Effect of Rh6G Based on the Strip Tactic

According to the morphological study, the strip tactic implied great potential on the SERS applications with tunable sensitivity. To quantitatively evaluate the performance of the fabricated strips, several series of SERS spectra of Rh6G water solution were measured. Figure3(a) show the first series of SERS spectra of different concentrations of Rh6G sampled by the test strips with three fabrication cycles. The concentration range of Rh6G was from 2 × 10−4 mM to 0.1 mM, and except for the spectra of 2 × 10−4 mM of Rh6G, the spectra from other concentrations showed clear peaks of Rh6G. In Figure S2, multiple spectra of a 5 × 10−3 mM Rh6G solution from different strips confirmed the good reproducibility of the tactic. And for different concentrations, from the low Raman shift side, the six strongest peaks were also identical, located at 612 cm−1, 771 cm−1, 1183 cm−1, 1312 cm−1, 1364 cm−1, and 1510 cm−1, and they were consistent with previous literature, indicating the heating temperature was suitable for Rh6G [21]. Since the spectra of the Rh6G were similar, the peak intensities (with baseline correction) at 1364 cm−1 were calculated and plotted in Figure 3(b). A clear positive correlation relationship between the concentrations and selected peak intensity was found, indicating the qualitative and quantitative capability of the strip tactic.Figure 3
(a) The SERS spectra and (b) the 1364 cm−1 peak intensity plot of different concentrations of Rh6G sampled by test strips with 3 cycles of fabrication and (c) the SERS spectra and (d) the 1364 cm−1 peak intensity plot of 0.6 mM of Rh6G sampled by test strips with different fabrication cycles.
(a)(b)(c)(d)In the second series, the adjustable sensitivity via the number of fabrication cycles was studied. The strips with fabrication cycles from one to five were prepared to measure the SERS spectra of 0.6 mM of Rh6G solution, as shown in Figure3(c). The results demonstrated that, even with only 1 cycle of fabrication, the strip was sensitive enough to provide the SERS spectrum with a high signal-to-noise ratio, which was consistent with the surface AgNPs clusters found in the morphological study of the strips with one cycle of fabrication. Indeed, with the increase of the fabrication cycles, all the characteristic peaks of Rh6G grew gradually, indicating that more AgNPs could enhance the SERS signals. And this effect was also observed for different concentrations of Rh6G, as shown in Figure S3. According to the peak intensity (with baseline correction) at 1364 cm−1, with the same concentration and measurement configuration of the Raman spectrometer, the intensity tunable range contributed by the fabrication cycles was 4-5 times, as shown in Figure 3(d). It was interesting to note that the enchantment ratio from the 2nd to the 4th cycle was relatively higher than the number from the 1st to the 2nd cycle and from the 4th to the 5th cycle. Considering the morphological study, the stages between the 2nd and the 4th cycles could well correspond to the formation of larger islands of AgNPs on the surface. While in the 1st cycle, only small clusters formed and in the 5th cycle, the net accumulation of islands may be limited by dissolve equilibrium. Additionally, combining the flexible dipping times of the sampling step, the total tunable sensitivity windows of this method were over twenty times. Considering the concentrations of target molecules for on-site measurement are usually unknown and enriching target molecules requires mass of work and additional instruments, such unique sensitivity flexibility may greatly assist in the on-site detections for different targets and applications.


## 3.3. Stability of the SERS Strip Tactic

As a practical tactic for on-site detection, besides the sensitivity and ease of use, the long-term stability on performance is essential, especially for quantitative or semiquantitative applications. According to previous literature, the colloid system is relatively stable if stored in a controlled environment, while the paper-based predeposited strips meet the fast decay of sensitivity [16]. This fact is one of the motivations of the tactic that the NPs are stored in the colloidal state and then freshly are prepared into strips on the field with a rapid and controllable microheater. To prove the advantage of this approach, a series of long-time tests of Rh6G spectra with predeposited strips and on-site fabricated strips were conducted with the same batch of colloidal AgNPs. Half of the NPs were used to fabricate strips at the beginning of the experiments with the dip-coating and heating method. These strips were counted as the predeposited strips and immediately packed with an aluminium film plastic bag under vacuum. And the other half of the colloidal AgNPs was kept in vials for the SERS strip tactic. All the strips and colloids were kept at 4°C temperature and in dark. Then, in every 2 days, 0.5 mM of Rh6G water solution was measured with the sealed predeposited strips and the freshly fabricated strips with the stored colloidal AgNPs. After ten days, the measured spectra were compared in Figure 4(a). It was clear that the sensitivity of the predeposited strips decreased significantly though they were carefully sealed, while the sensitivity of the strips fabricated the tactic was almost kept based on the 1364 cm−1 peak intensity plot, as shown in Figure 4(b). Then, in the subsequent experiments, the predeposited strips could barely detect Rh6G solution after one month, while with the strip tactic, the peak intensity of Rh6G spectra only suffers about one-third loss after six months, compared to the initial intensity. Consequently, such on-site fabrication tactic was confirmed to help prevent the sensitivity decay with little sacrifice on strip fabrication time. The advantage on long-term stability, in addition to the tunable sensitivity, could provide a convenient tool for on-site applications.Figure 4
(a) The Raman spectra of 0.5 mM of Rh6G sampled by sealed predeposited strips (up) and strips fabricated with the tactic (down) and (b) the 1364 cm−1 peak intensity plot of these spectra in ten days.
(a)(b)


## 3.4. Detection and Discrimination of Animal Blood Samples

With the confirmation of the sensitivity, long-term stability, and repeatability, the SERS strip tactic was applied to study a series of blood samples, since rapid blood identification is usually desired in forensic and wild animal protection fields, and some previous literature has reported that Raman spectra could be used for the detection and discrimination of blood [22–24]. Although heating would change the biological activity of blood samples, the heating temperature was still set to 65°C because the Raman spectroscopy mainly reveals the information of primary chemical bonds, instead of the folding structures of biomacromolecules. The blood samples from seven species of animals were measured following the general operations for 30 times per species, and all the spectra are demonstrated in Figure S4. The high similarity of the spectra from a certain species indicated the good reproducibility of the strip tactic. Figure 5 shows the average Raman spectra, and compared to the blank test strips, the blood samples showed several specific peaks, such as the peaks at 480 cm−1, 660 cm−1, 1128 cm−1, 1221 cm−1, 1315 cm−1, 1439 cm−1, and 1578 cm−1, which were also observed in other literature [25, 26]. Specifically, 660 cm−1 and 1221 cm−1 are related to haemoglobin in the blood; 1128 cm−1 and 1315 cm−1 may be from the spermine phosphate hexahydrate; and 1439 cm−1 closely matches the Raman bands of serum albumin [27, 28].Figure 5
The average Raman spectra of blood samples from seven species of animals.However, the blood components of large animals are complex, so the characteristic peaks based interpretation into chemical bonds and molecules may be complicated. The identification goal is not only the chemical components but also the species information. Therefore, in a lot of cases, the classification algorithms towards final labels, instead of matching the characteristic peaks, were more frequently applied. Such algorithms mainly require good reproducibility and consistency between the labelled samples and the detected unknown samples and are relatively less influenced by the poetical chemical or physical change during the tests if the same change happens in both the labelled samples and the detected unknown samples. Herein, we applied the principle component analysis (PCA), which was frequently applied for the classification goals [29], to these spectra to attempt to cluster the spectra based on species. Overall, the first two components covered over 95% of the information of the original spectra, indicating the feasibility of the PCA method to these spectra. Figure 6 shows the PCA clustering analysis with a 95% confident range of each cluster. From the overlaps of different species, the SERS signals from the strips could fully discriminate 5 species from each other, such as kangaroo, dog, golden monkey, and sika deer. On the other hand, a part of the spectra of cat blood samples overlapped with the blank strips, which may be caused by relatively weak signals of these spectra. The confident ellipses of cattle and red-crowned crane SERS spectra shared about one-third of samples, which may cause less accurate prediction regarding these two animals. To further verify the classification potential, the third principle component, which carried about 1.5% of the information, was also considered. Under this condition, the spectra from the cat could successfully separate from the blank strips under 95% confidence while cattle and red-crowned crane still cannot be fully distinguished with the SERS strips and the hand-held Raman spectrometer. In summary, in the preliminary experiments, the animal species could be probably discriminated via the Raman spectra of blood under 95% confidence. If the goal is only yes/no binary classification towards a certain kind of species, the true positive rate should be higher.Figure 6
The PCA results of the Raman spectra of seven species of animal blood samples with 95% confident ranges.


## 4. Conclusions

In this article, we present a SERS strip tactic which has great potential for on-site measurement with long-term sensitivity and repeatability. With a dedicated microheater, the SERS strips could be fabricated easily and efficiently on the field. In addition, the dip-coating and rapid heating combination method could also be applied to the target sampling process, which not only increases the uniformity and detection efficiency but also enables the tunable window of the sensitivity of the strip tactic about twenty times. Such flexibility may provide great help for the real-world detection when the concentration of the target is unknown or out of the default range. To further demonstrate the practical potential of the strip tactic, the blood samples from different animal species were measured with the SERS strip tactic following the general operations. With the SERS strips, the Raman spectra from all the samples were observed, and by applying the PCA algorithm to those spectra, the spectra were partially discriminated. Such promising results indicated the SERS strip tactic may contribute to forensic, wild animal protection and many other fields, where the on-site expedient detection and screening solutions are desired.



---

*Source: 5560513-2021-04-20.xml*