# Seepage Characteristics of Slurry with Particle Additives in the High-Permeability Sand Layer

Authors: Yuan Wang; Zhikui Wang; Di Feng; Sijin Liu; Shujun Xu; Kun Zhou
Journal: Geofluids
 (2021)

---

## Abstract

In the process of the slurry shield construction, the formation of the filter cake is the key to maintain the stability of the excavation face. In high-permeability formation, ordinary pure bentonite slurry is easy to pass through the formation void. Therefore, it is necessary to study the slurry permeability characteristics of the high-permeability sand layer. For the purpose of researching the permeability characteristics of slurry in sandy formation, this paper studies the influence of slurry viscosity on the formation of the filter cake in high-permeability formation under different pressure gradients by the slurry permeability test. The effect of additive particle size on the film-forming gain was studied by adding additives with different particle sizes into pure bentonite slurries with different viscosities. This paper presents a method to determine the optimum slurry viscosity and particle size for high-permeability formation so as to guide the slurry shield construction in high-permeability formation.


---

## Body

## 1. Introduction

The slurry shield tunnel has been widely used in recent years, especially in the urban subway and river crossing tunnel. However, during the slurry shield construction in the high-permeability stratum, the pure bentonite slurry inrush caused disasters frequently, which seriously affect the stability of the shield construction face. In order to maintain the stability of the slurry shield excavation face during construction, it is necessary to prevent the slurry suspension from penetrating into the soil. To ensure the effective transmission of support pressure to the soil, it is necessary to form a dense low-permeability filter cake on the face of the tunnel [1–7]. For highly permeable soils, pure bentonite suspensions cannot be used anymore, which penetrate the ground, and the required suspension pressure may not be attached. It is necessary to add chemical additives (tackifier, dispersant, etc.) [8] and coarse-grained materials (vermiculite, sand, clay, quartz powder, sawdust, fiber, etc.) [8–14] to improve the slurry properties. When the slurry permeates the formation, it could reduce the formation permeability and form the membrane more quickly and efficiently.For the purpose of researching the effect of slurry particle additives on formation permeability, Fritz [8] considered the influence of additive polymer, sand, and vermiculite on the maximum slurry pressure and determined the composition proportion of the best combination. The slurry pressure that the best combination could bear is more than 10 times higher than that of using ordinary bentonite slurry. Han et al. [9] and Liu et al. [15] compared the effective gap of the formation with the minimum particle size and the maximum particle size of the slurry and divided the formation state of the membrane into three types: filter cake type, permeability zone type, and filter cake and permeability zone type. Liu et al. [15, 16] took light sand as coarse-grained material. By comparing the relationship between the particle size of coarse-grained material and the pore diameter of formation, it was found that the addition of coarse-grained material is more conducive to the formation of the filter cake, and the coarse-grained material with a smaller particle size could produce a good synergistic effect with slurry particles. Min et al. [11, 12] defined the average pore diameter soil through the formation permeability coefficient and pore ratio, compared the average pore diameter with the particle size of representative slurry particles, and divided the seepage phenomenon into three categories.For the purpose of researching the influence of slurry viscosity on formation permeability, Min et al. [12] showed that increasing the content of clay particles was more conducive to the formation of the filter cake, but only the content of clay particles (clay particles less than 0.005 mm) in the slurry could be used as an important index for slurry adjustment. The effect of coarse particles in the slurry was ignored. Wang et al. [17] and Min et al. [18] regarded the slurry as Bingham fluid, tested the slurry performance with a rotary viscometer, and established the relationship between the yield stress which can characterize the viscosity of the slurry and the initial pressure gradient in the process of mud infiltration. The yield stress is positively correlated with the initial pressure gradient. Zhai et al. [19] and Xu and Bezuijen [14] regarded slurry infiltration as a kind of formation silting process and increased slurry viscosity by increasing bentonite content. It is concluded that increasing the viscosity of slurry is more conducive to the formation of the filter cake. In the process of slurry shield circulation, the slurry plays an important role in carrying slag, so the slurry should have good fluidity. Therefore, previous studies were mostly limited to low-viscosity mud (marsh time 30~40s). However, in the high-permeability stratum, the shield machine is in the rest state and does not need to carry slag. At this time, the primary role of slurry is not to carry slag but to form the filter cake. In other words, grouting must be used in the high-permeability stratum to reduce the permeability in front of the excavation face. The use of high-viscosity bentonite slurry has become the first choice [20].Therefore, it is necessary to carry out the influence of slurry viscosity and particle size on the formation of the filter cake in high-permeability formation. The relationship between the slurry viscosity and the pressure gradient of pure bentonite was established by the slurry permeability experiment. The influence of slurry viscosity on the formation of the filter cake in high-permeability formation under different pressure gradients is studied. By adding additives with different particle sizes to pure bentonite slurry with different viscosities, the effect of additive particle size on the gain effect of filter cake formation was studied. In this paper, a method of optimum slurry viscosity and particle size suitable for the high-permeability stratum is proposed to guide slurry shield construction in the high-permeability stratum.


## 2. Experimental Studies

### 2.1. Materials

Two kinds of materials were used to simulate the formation of the filter cake, which were pure bentonite slurry material formed by bentonite and water and slurry material added with coarse additives. Thepure bentonite was composed of different clay particles; it was mixed material. However, its clay particle size was less than 0.075 mm, which was 1-2 orders of magnitude smaller than that in additives, so it was defined as pure bentonite slurry [8, 21].To investigate the influence of slurry viscosity and particle size of additives on the formation of the high-permeability sand film, four pure bentonite slurry materials [11, 19] were prepared, respectively. After screening, impurities were removed from the bentonite, and bentonite particles with particle sizes less than or equal to 0.075 mm [12] were obtained. Five kinds of coarse-grained additive materials with different particle sizes were prepared [8, 16]. For the integrity and accuracy of the experimental data, three kinds of coarse sand with different particle sizes [11, 16] were also prepared as high-permeability formation materials for slurry permeability. Slurry materials and formation materials would be described in detail below.


#### 2.1.1. Stratum Materials

For the integrity and accuracy of the experimental data, three kinds of high-permeability formations with different permeability coefficients and pore ratios were constructed in the paper. The construction method was to obtain three kinds of uniform sand with particle sizes of 2-3 cm, 3-4 cm, and 4-5 cm through four kinds of standard sieves with diameters of 1 mm, 2 mm, 3 mm, and 4 mm, named S1, S2, and S3, respectively. The basic physical indexes of the experimental formation materials were measured by the standard of the soil conventional parameter test, as shown in Table1.Table 1
Basic physical indexes of the test soils.
Identity of soilS1S2S3Grain size range (mm)2-33-44-5Dry density (g/cm3)1.451.491.53n0.430.400.36K (m/s)1.86×10−23.87×10−24.97×10−2D′¯ (μm) [11]305456544The permeability of soil is affected by its porosity and pore size distribution. It is difficult to accurately measure the pore size of sand, so some conceptual models and empirical equations are used to estimate the pore size of the formation. The average pore size of a formation is equivalent to the pore size of a formation [11, 22–24]. The accuracy of the formula (D′¯=K/31×1.5n) is verified by the experimental comparison between the calculated data of formation average pore size in Min et al.’s paper and the data of the PoreMaster60GT mercury injection instrument. Therefore, this paper selects the formula as the standard for calculating the average pore size D′¯. (D′¯ is the average pore diameter size of soil.)


#### 2.1.2. Slurry Materials

According to the different research emphases, two kinds of slurry materials were prepared. To investigate the influence of the relationship between the viscosity of pure bentonite slurry and the pressure gradient of slurry, the first kind of slurry was prepared as pure bentonite slurry (i.e., the content of particle additives was zero). Thepure bentonite slurry was a mixture of sodium bentonite and CMC (0.04%, a high molecular polymer [11, 25]) and water. In order to reflect the effect of slurry viscosity on formation silting better, we choose the method of increasing bentonite content in this paper. Four kinds of pure Na-bentonite slurries with concentrations of 7.4%, 13.7%, 19.4%, and 24.2% were prepared, which were named SL1-SL4, respectively.To investigate the influence of the silting effect of particle size additives on formation, the average pore sizes of S1, S2, and S3 were 0.305 mm, 0.456 mm, and 0.544 mm, respectively. In this paper, fine sand with a particle size of 0.2 mm~0.6 mm (increment 0.1 mm) and SL3 pure bentonite slurry [15, 16], which were widely used in high-permeability formation engineering, were selected as the second slurry in this paper, named SL32-SL36, respectively. Table 2 shows the slurry material parameters. The fine sand is selected as an additive in this paper.Table 2
Mass of each constituent in slurry.
Type of slurryThe content of bentonite (%)The particle diameter of additivesMarsh time (s)SL17.4No contain22 sSL213.7No contain68 sSL319.40 and 0.2 mm~0.6 mm, namely, SL3 and SL31~SL35, respectively155 sSL424.2No contain210


### 2.2. Experimental Apparatus and Test Method

In this paper, the self-developed filter cake airtightness test device was used as the test device (as shown in Figure1). The device consists of the main body of the permeation column, a pressure relief valve maintaining stable air pressure, and an air compressor providing air pressure. The inner diameter of the plexiglass cylinder is 75 mm, 10 mm thin, and 40 mm high. It could withstand a maximum pressure of about 1 MPa. An air compressor was used to provide osmotic pressure. The initial slurry pressure is 50 kPa, with 50 kPa as an order of magnitude, and it is continuously increased to the maximum 300 kPa. In order to control and measure the pressure in the column, a pressure relief valve is used to stabilize the air pressure with a stability accuracy of 1 kPa. The main body of the permeation column is composed of the plexiglass cylinder. The air compressor could pressurize the experimental slurry in the column through the intake valve on the column. After the slurry penetrates through the formation, the rate loss of the slurry could be measured by connecting the measuring cylinder with the drainage outlet.Figure 1
Filter cake airtightness test apparatus.Before adding 5 cm of the cushion layer, the test was carried out at the bottom of the layer. In order to make the formation distribute evenly, the formation material was added three times. Add about 7 mm each time, and then hammer 10 times each time to keep the void ratio stable. Secondly, tap water was used to saturate the formation materials. Then, 500 mL of slurry was introduced into the top of the formation to form a slurry layer in the upper part of the formation. Finally, an air compressor was used to apply different air pressures on the upper part of the mud layer to simulate the slurry infiltration. The downward seepage that flowed through the test soil layer was recorded by using the slurry pressure method. When the pressure was applied each time, the flow rate was stable; record the corresponding slurry pressure and discharge volume. At the same time, the formation of the filter cake was observed. When the cake was formed, the test pressure ends.


## 2.1. Materials

Two kinds of materials were used to simulate the formation of the filter cake, which were pure bentonite slurry material formed by bentonite and water and slurry material added with coarse additives. Thepure bentonite was composed of different clay particles; it was mixed material. However, its clay particle size was less than 0.075 mm, which was 1-2 orders of magnitude smaller than that in additives, so it was defined as pure bentonite slurry [8, 21].To investigate the influence of slurry viscosity and particle size of additives on the formation of the high-permeability sand film, four pure bentonite slurry materials [11, 19] were prepared, respectively. After screening, impurities were removed from the bentonite, and bentonite particles with particle sizes less than or equal to 0.075 mm [12] were obtained. Five kinds of coarse-grained additive materials with different particle sizes were prepared [8, 16]. For the integrity and accuracy of the experimental data, three kinds of coarse sand with different particle sizes [11, 16] were also prepared as high-permeability formation materials for slurry permeability. Slurry materials and formation materials would be described in detail below.


### 2.1.1. Stratum Materials

For the integrity and accuracy of the experimental data, three kinds of high-permeability formations with different permeability coefficients and pore ratios were constructed in the paper. The construction method was to obtain three kinds of uniform sand with particle sizes of 2-3 cm, 3-4 cm, and 4-5 cm through four kinds of standard sieves with diameters of 1 mm, 2 mm, 3 mm, and 4 mm, named S1, S2, and S3, respectively. The basic physical indexes of the experimental formation materials were measured by the standard of the soil conventional parameter test, as shown in Table1.Table 1
Basic physical indexes of the test soils.
Identity of soilS1S2S3Grain size range (mm)2-33-44-5Dry density (g/cm3)1.451.491.53n0.430.400.36K (m/s)1.86×10−23.87×10−24.97×10−2D′¯ (μm) [11]305456544The permeability of soil is affected by its porosity and pore size distribution. It is difficult to accurately measure the pore size of sand, so some conceptual models and empirical equations are used to estimate the pore size of the formation. The average pore size of a formation is equivalent to the pore size of a formation [11, 22–24]. The accuracy of the formula (D′¯=K/31×1.5n) is verified by the experimental comparison between the calculated data of formation average pore size in Min et al.’s paper and the data of the PoreMaster60GT mercury injection instrument. Therefore, this paper selects the formula as the standard for calculating the average pore size D′¯. (D′¯ is the average pore diameter size of soil.)


### 2.1.2. Slurry Materials

According to the different research emphases, two kinds of slurry materials were prepared. To investigate the influence of the relationship between the viscosity of pure bentonite slurry and the pressure gradient of slurry, the first kind of slurry was prepared as pure bentonite slurry (i.e., the content of particle additives was zero). Thepure bentonite slurry was a mixture of sodium bentonite and CMC (0.04%, a high molecular polymer [11, 25]) and water. In order to reflect the effect of slurry viscosity on formation silting better, we choose the method of increasing bentonite content in this paper. Four kinds of pure Na-bentonite slurries with concentrations of 7.4%, 13.7%, 19.4%, and 24.2% were prepared, which were named SL1-SL4, respectively.To investigate the influence of the silting effect of particle size additives on formation, the average pore sizes of S1, S2, and S3 were 0.305 mm, 0.456 mm, and 0.544 mm, respectively. In this paper, fine sand with a particle size of 0.2 mm~0.6 mm (increment 0.1 mm) and SL3 pure bentonite slurry [15, 16], which were widely used in high-permeability formation engineering, were selected as the second slurry in this paper, named SL32-SL36, respectively. Table 2 shows the slurry material parameters. The fine sand is selected as an additive in this paper.Table 2
Mass of each constituent in slurry.
Type of slurryThe content of bentonite (%)The particle diameter of additivesMarsh time (s)SL17.4No contain22 sSL213.7No contain68 sSL319.40 and 0.2 mm~0.6 mm, namely, SL3 and SL31~SL35, respectively155 sSL424.2No contain210


## 2.1.1. Stratum Materials

For the integrity and accuracy of the experimental data, three kinds of high-permeability formations with different permeability coefficients and pore ratios were constructed in the paper. The construction method was to obtain three kinds of uniform sand with particle sizes of 2-3 cm, 3-4 cm, and 4-5 cm through four kinds of standard sieves with diameters of 1 mm, 2 mm, 3 mm, and 4 mm, named S1, S2, and S3, respectively. The basic physical indexes of the experimental formation materials were measured by the standard of the soil conventional parameter test, as shown in Table1.Table 1
Basic physical indexes of the test soils.
Identity of soilS1S2S3Grain size range (mm)2-33-44-5Dry density (g/cm3)1.451.491.53n0.430.400.36K (m/s)1.86×10−23.87×10−24.97×10−2D′¯ (μm) [11]305456544The permeability of soil is affected by its porosity and pore size distribution. It is difficult to accurately measure the pore size of sand, so some conceptual models and empirical equations are used to estimate the pore size of the formation. The average pore size of a formation is equivalent to the pore size of a formation [11, 22–24]. The accuracy of the formula (D′¯=K/31×1.5n) is verified by the experimental comparison between the calculated data of formation average pore size in Min et al.’s paper and the data of the PoreMaster60GT mercury injection instrument. Therefore, this paper selects the formula as the standard for calculating the average pore size D′¯. (D′¯ is the average pore diameter size of soil.)


## 2.1.2. Slurry Materials

According to the different research emphases, two kinds of slurry materials were prepared. To investigate the influence of the relationship between the viscosity of pure bentonite slurry and the pressure gradient of slurry, the first kind of slurry was prepared as pure bentonite slurry (i.e., the content of particle additives was zero). Thepure bentonite slurry was a mixture of sodium bentonite and CMC (0.04%, a high molecular polymer [11, 25]) and water. In order to reflect the effect of slurry viscosity on formation silting better, we choose the method of increasing bentonite content in this paper. Four kinds of pure Na-bentonite slurries with concentrations of 7.4%, 13.7%, 19.4%, and 24.2% were prepared, which were named SL1-SL4, respectively.To investigate the influence of the silting effect of particle size additives on formation, the average pore sizes of S1, S2, and S3 were 0.305 mm, 0.456 mm, and 0.544 mm, respectively. In this paper, fine sand with a particle size of 0.2 mm~0.6 mm (increment 0.1 mm) and SL3 pure bentonite slurry [15, 16], which were widely used in high-permeability formation engineering, were selected as the second slurry in this paper, named SL32-SL36, respectively. Table 2 shows the slurry material parameters. The fine sand is selected as an additive in this paper.Table 2
Mass of each constituent in slurry.
Type of slurryThe content of bentonite (%)The particle diameter of additivesMarsh time (s)SL17.4No contain22 sSL213.7No contain68 sSL319.40 and 0.2 mm~0.6 mm, namely, SL3 and SL31~SL35, respectively155 sSL424.2No contain210


## 2.2. Experimental Apparatus and Test Method

In this paper, the self-developed filter cake airtightness test device was used as the test device (as shown in Figure1). The device consists of the main body of the permeation column, a pressure relief valve maintaining stable air pressure, and an air compressor providing air pressure. The inner diameter of the plexiglass cylinder is 75 mm, 10 mm thin, and 40 mm high. It could withstand a maximum pressure of about 1 MPa. An air compressor was used to provide osmotic pressure. The initial slurry pressure is 50 kPa, with 50 kPa as an order of magnitude, and it is continuously increased to the maximum 300 kPa. In order to control and measure the pressure in the column, a pressure relief valve is used to stabilize the air pressure with a stability accuracy of 1 kPa. The main body of the permeation column is composed of the plexiglass cylinder. The air compressor could pressurize the experimental slurry in the column through the intake valve on the column. After the slurry penetrates through the formation, the rate loss of the slurry could be measured by connecting the measuring cylinder with the drainage outlet.Figure 1
Filter cake airtightness test apparatus.Before adding 5 cm of the cushion layer, the test was carried out at the bottom of the layer. In order to make the formation distribute evenly, the formation material was added three times. Add about 7 mm each time, and then hammer 10 times each time to keep the void ratio stable. Secondly, tap water was used to saturate the formation materials. Then, 500 mL of slurry was introduced into the top of the formation to form a slurry layer in the upper part of the formation. Finally, an air compressor was used to apply different air pressures on the upper part of the mud layer to simulate the slurry infiltration. The downward seepage that flowed through the test soil layer was recorded by using the slurry pressure method. When the pressure was applied each time, the flow rate was stable; record the corresponding slurry pressure and discharge volume. At the same time, the formation of the filter cake was observed. When the cake was formed, the test pressure ends.


## 3. Results and Analysis

### 3.1. Filter Cake Formation of Pure Na-Bentonite Slurry

In order to obtain the permeability law of slurry with different viscosities in high-permeability formation, the permeability of four kinds of pure bentonite slurry in three kinds of formation was analyzed by experiment device 1. The test pressure is in the order of 50 kPa, which was continuously increased to the maximum 250 kPa. By recording the leakage under different pressures, the formation of the filter cake in the three formations was observed (it should be noted that the leakage amount here represents the water after the free water in the slurry was not fully combined with the slurry particles and penetrates through the formation under the action of consolidation) [9, 11]. The test pressure gradient and permeability curve were established here, as shown in Figure 2. In the figure, the abscissa was the pressure action time, the left ordinate is the pressure gradient, and the right ordinate was the leakage amount.Figure 2
Pressure gradient and infiltration curve of the test.
(a)
S1 (D1′¯=305μm)(b)
S2 (D2′¯=456μm)(c)
S3 (D3′¯=544μm)It could be seen from Figure2 that the filter cake of SL3 and SL4 formed in S1 and S2 formations. SL1 and SL2 did not form the filter cake. It showed that with the increase of slurry viscosity, the formation of the filter cake was easier. When the filter cake was formed, the filtering water was less, which indicated that the quality of the filter cake is better. In S3 formation, the filter cake was formed in SL4 and not in SL1-3. Although SL4 formed the filter cake, the quality was poor. When the slurry pressurized to 100 kPa, the filter cake was broken down, and the filtration volume increased rapidly. Only increasing the content of bentonite has a limited effect on the quality of the filter cake.


### 3.2. Filter Cake Formation of Na-Bentonite Slurry with Coarse-Grained Materials

To investigate the influence of slurry viscosity and particle size of additives on the formation of the filter cake in high-permeability formation, five kinds of bentonite slurries SL31~SL35 containing coarse-grained materials were selected to analyze their permeability in three formations. The effect of pure bentonite slurry and particle additives on the formation of the high-permeability formation filter cake was studied under different pressures. The specific experimental operation was consistent with the test operation in Section3.2. The typical curve of the relationship between the filtration rate and the film-forming time is shown in Figure 3. In the figure, the abscissa is the pressure action time, the left ordinate is the pressure gradient, and the right ordinate is the leakage amount.Figure 3
Pressure gradient and infiltration curve of the test.
(a)
S1 (D1′¯=305μm)(b)
S2 (D2′¯=456μm)(c)
S3 (D3′¯=544μm)It could be seen from Figure3 that the initial pressure of slurry leakage was increasing after adding coarse-grained materials to SL3 pure bentonite slurry. The increase of coarse particles in the slurry had a significant effect on the increase of initial mud pressure, which made it easier to form the filter cake than pure bentonite slurry.In general, for S1 formation, the leakage tended to be stable under various pressures, and there was no trend of rapid increase. It was proved that the filter cake could be formed by adding coarse particles in the formation. Since S1 formation could form the filter cake under various pressures, S2 formation and S3 formation were mainly analyzed. For S2 formation, when the vertical pressure was greater than 150 kPa, the leakage of SL31 slurry would increase rapidly. It was proved that the filter cake could not be formed at this time. When the pressure of SL32 and SL35 slurries was higher than 200 kPa, the leakage of SL32 and SL35 slurries increased rapidly, and the filter cake could not be formed. SL33 and SL34 slurries could not form the filter cake when the pressure was greater than 250 kPa. For S3 formation, when the slurry pressure was greater than 100 kPa, the leakage of SL31 slurry increased rapidly. When the vertical pressure of SL32 and SL35 slurries was greater than 150 kPa, the leakage of SL32 and SL35 slurries would increase rapidly, and the filter cake could not be formed. When the initial pressure gradient of SL33 and SL34 was greater than 200 kPa, filter cake could not be formed.


## 3.1. Filter Cake Formation of Pure Na-Bentonite Slurry

In order to obtain the permeability law of slurry with different viscosities in high-permeability formation, the permeability of four kinds of pure bentonite slurry in three kinds of formation was analyzed by experiment device 1. The test pressure is in the order of 50 kPa, which was continuously increased to the maximum 250 kPa. By recording the leakage under different pressures, the formation of the filter cake in the three formations was observed (it should be noted that the leakage amount here represents the water after the free water in the slurry was not fully combined with the slurry particles and penetrates through the formation under the action of consolidation) [9, 11]. The test pressure gradient and permeability curve were established here, as shown in Figure 2. In the figure, the abscissa was the pressure action time, the left ordinate is the pressure gradient, and the right ordinate was the leakage amount.Figure 2
Pressure gradient and infiltration curve of the test.
(a)
S1 (D1′¯=305μm)(b)
S2 (D2′¯=456μm)(c)
S3 (D3′¯=544μm)It could be seen from Figure2 that the filter cake of SL3 and SL4 formed in S1 and S2 formations. SL1 and SL2 did not form the filter cake. It showed that with the increase of slurry viscosity, the formation of the filter cake was easier. When the filter cake was formed, the filtering water was less, which indicated that the quality of the filter cake is better. In S3 formation, the filter cake was formed in SL4 and not in SL1-3. Although SL4 formed the filter cake, the quality was poor. When the slurry pressurized to 100 kPa, the filter cake was broken down, and the filtration volume increased rapidly. Only increasing the content of bentonite has a limited effect on the quality of the filter cake.


## 3.2. Filter Cake Formation of Na-Bentonite Slurry with Coarse-Grained Materials

To investigate the influence of slurry viscosity and particle size of additives on the formation of the filter cake in high-permeability formation, five kinds of bentonite slurries SL31~SL35 containing coarse-grained materials were selected to analyze their permeability in three formations. The effect of pure bentonite slurry and particle additives on the formation of the high-permeability formation filter cake was studied under different pressures. The specific experimental operation was consistent with the test operation in Section3.2. The typical curve of the relationship between the filtration rate and the film-forming time is shown in Figure 3. In the figure, the abscissa is the pressure action time, the left ordinate is the pressure gradient, and the right ordinate is the leakage amount.Figure 3
Pressure gradient and infiltration curve of the test.
(a)
S1 (D1′¯=305μm)(b)
S2 (D2′¯=456μm)(c)
S3 (D3′¯=544μm)It could be seen from Figure3 that the initial pressure of slurry leakage was increasing after adding coarse-grained materials to SL3 pure bentonite slurry. The increase of coarse particles in the slurry had a significant effect on the increase of initial mud pressure, which made it easier to form the filter cake than pure bentonite slurry.In general, for S1 formation, the leakage tended to be stable under various pressures, and there was no trend of rapid increase. It was proved that the filter cake could be formed by adding coarse particles in the formation. Since S1 formation could form the filter cake under various pressures, S2 formation and S3 formation were mainly analyzed. For S2 formation, when the vertical pressure was greater than 150 kPa, the leakage of SL31 slurry would increase rapidly. It was proved that the filter cake could not be formed at this time. When the pressure of SL32 and SL35 slurries was higher than 200 kPa, the leakage of SL32 and SL35 slurries increased rapidly, and the filter cake could not be formed. SL33 and SL34 slurries could not form the filter cake when the pressure was greater than 250 kPa. For S3 formation, when the slurry pressure was greater than 100 kPa, the leakage of SL31 slurry increased rapidly. When the vertical pressure of SL32 and SL35 slurries was greater than 150 kPa, the leakage of SL32 and SL35 slurries would increase rapidly, and the filter cake could not be formed. When the initial pressure gradient of SL33 and SL34 was greater than 200 kPa, filter cake could not be formed.


## 4. Discussion

### 4.1. Effect of Coarse-Grained Additives on Filter Cake Formation

Figure4 shows the maximum pressure that five different slurry materials could bear when forming the filter cake in S2 formation and S3 formation, respectively. It could be seen from Figure 4 that with the increase of the average pore size of the formation, the maximum pressure that the same slurry could bear to form the filter cake becomes smaller. Moreover, the increase of coarse particles in the slurry had a significant effect on the increase of initial slurry pressure. The smaller size of the coarse-grained materials could reduce the filtration rate and shorten the film-forming time. However, with the increase of the particle size of coarse-grained materials, the gain effect was gradually weakened. The results showed that the gain effect of coarse-grained material on the filter cake was limited. The results showed that both the filtration loss and the formation time of the filter cake decreased at first and then increased with the increase of particle size in additives, which was similar to Gaussian distribution, as shown in Figure 4.Figure 4
Distribution of the maximum vertical pressure during mud film formation.
(a)
S2 (D2′¯=456μm)(b)
S3 (D3′¯=544μm)In Figure3, SL32 and SL35 and SL33 and SL34 intersect in S2 and S3 formations, indicating that SL33 was more stable than SL34 and that SL32 was more stable than SL35 before the intersection. The reason may be that fine sand particles with too large particle size could not form a good synergistic effect with slurry. In addition, the fine sand with the same content had a larger particle size and fewer particles, which led to the formation of an uneven thin filter cake and easy-to-cause local damage. The selection of the particle size of coarse-grained materials was the most important factor affecting the film-forming effect. The experimental results were consistent with the experimental results of Liu et al. (2015) and also verified the reliability of the experimental results.


### 4.2. Mechanism Analysis of Coarse-Grained Additives and Slurry Viscosity on Filter Cake Formation

This section evaluated the film-forming effect of pure bentonite slurry and granular slurry. Figure5(a) shows the final result of SL3 pure bentonite slurry forming the filter cake in S3 formation. It could be seen from the figure that the change of stratum properties could be divided into two parts: the upper part is the filter cake, and the lower part is the permeable zone. Because the clay particle size of pure bentonite slurry was less than 0.075 mm, far less than the average pore diameter of S3 formation of 0.544 mm, a part of clay particles penetrated into the sand layer under the action of seepage force, and most of the clay particles formed the polymer chain structure under the action of polymer CMC and formed the filter cake on the surface of the formation, as shown in Figure 5(a).Figure 5
The permeability effect of slurry in S3 formation.
(a)
Pure bentonite(b)
Bentonite slurry with coarse-grained materialsThe interaction mechanism between polymer chains and clay particles is shown in Figure6(a). In addition to bentonite, the polymer was also mixed into the slurry. The polymer with long strings forms a “net” over the pores causing a rapid clogging almost without respect to any filter law. Figure 6(a) tries to visualize this special situation. The soil-bentonite slurry would penetrate relatively deep into the pores if there were no polymer strings in the slurry mixture. The pure bentonite slurry must overcome the shear force caused by soil action before it could penetrate into the pores of the formation. When the viscosity of the slurry is high, the shear force is larger. The slurry that does not penetrate into the formation will accumulate at the excavation face, which is another way to form a filter cake.Figure 6
Filter cake formation mechanism analysis.
(a)
Pure bentonite(b)
Bentonite slurry with coarse-grained materialsFigure5(b) shows the final effect of SL33 slurry (with a particle size of 0.4 mm) forming the filter cake in S3 formation. It could be seen from the figure that the permeability state of slurry in the formation was obviously divided into three parts: the upper part is the filter cake, the middle part is the particle clogging area, and the bottom part is the permeability zone. Due to the blocking effect of the formation voids, fine sand particles added in the slurry would be silted up after being penetrated a certain distance in front of the excavation face. It could be seen from Figure 3 that under the same level of pressure load, the filtration capacity of SL33 was about half less than that of SL3. SL33 could bear more mud pressure. Finally, the infiltration area and filter cake formation area were dried, sieved, and weighed. The 0.3 mm particle additive accounted for 95% of the original addition. Considering the loss of additive particles in the experiment, most of the particles were blocked in the infiltration area and filter cake. It could be seen from this that the coarse-grained materials will first be silted up in the formation pores, reducing the average pore size of the original formation and forming new pores with a smaller average pore size. The clay particles in the subsequent bentonite slurry were more likely to be silted in the average pore space of the new formation. Thus, the formed sludge membrane has lower filtration capacity and stronger antipermeability damage ability. The interaction mechanism of the polymer chain, clay, and coarse-grained materials after adding coarse-grained materials is shown in Figure 6(b) [25].


## 4.1. Effect of Coarse-Grained Additives on Filter Cake Formation

Figure4 shows the maximum pressure that five different slurry materials could bear when forming the filter cake in S2 formation and S3 formation, respectively. It could be seen from Figure 4 that with the increase of the average pore size of the formation, the maximum pressure that the same slurry could bear to form the filter cake becomes smaller. Moreover, the increase of coarse particles in the slurry had a significant effect on the increase of initial slurry pressure. The smaller size of the coarse-grained materials could reduce the filtration rate and shorten the film-forming time. However, with the increase of the particle size of coarse-grained materials, the gain effect was gradually weakened. The results showed that the gain effect of coarse-grained material on the filter cake was limited. The results showed that both the filtration loss and the formation time of the filter cake decreased at first and then increased with the increase of particle size in additives, which was similar to Gaussian distribution, as shown in Figure 4.Figure 4
Distribution of the maximum vertical pressure during mud film formation.
(a)
S2 (D2′¯=456μm)(b)
S3 (D3′¯=544μm)In Figure3, SL32 and SL35 and SL33 and SL34 intersect in S2 and S3 formations, indicating that SL33 was more stable than SL34 and that SL32 was more stable than SL35 before the intersection. The reason may be that fine sand particles with too large particle size could not form a good synergistic effect with slurry. In addition, the fine sand with the same content had a larger particle size and fewer particles, which led to the formation of an uneven thin filter cake and easy-to-cause local damage. The selection of the particle size of coarse-grained materials was the most important factor affecting the film-forming effect. The experimental results were consistent with the experimental results of Liu et al. (2015) and also verified the reliability of the experimental results.


## 4.2. Mechanism Analysis of Coarse-Grained Additives and Slurry Viscosity on Filter Cake Formation

This section evaluated the film-forming effect of pure bentonite slurry and granular slurry. Figure5(a) shows the final result of SL3 pure bentonite slurry forming the filter cake in S3 formation. It could be seen from the figure that the change of stratum properties could be divided into two parts: the upper part is the filter cake, and the lower part is the permeable zone. Because the clay particle size of pure bentonite slurry was less than 0.075 mm, far less than the average pore diameter of S3 formation of 0.544 mm, a part of clay particles penetrated into the sand layer under the action of seepage force, and most of the clay particles formed the polymer chain structure under the action of polymer CMC and formed the filter cake on the surface of the formation, as shown in Figure 5(a).Figure 5
The permeability effect of slurry in S3 formation.
(a)
Pure bentonite(b)
Bentonite slurry with coarse-grained materialsThe interaction mechanism between polymer chains and clay particles is shown in Figure6(a). In addition to bentonite, the polymer was also mixed into the slurry. The polymer with long strings forms a “net” over the pores causing a rapid clogging almost without respect to any filter law. Figure 6(a) tries to visualize this special situation. The soil-bentonite slurry would penetrate relatively deep into the pores if there were no polymer strings in the slurry mixture. The pure bentonite slurry must overcome the shear force caused by soil action before it could penetrate into the pores of the formation. When the viscosity of the slurry is high, the shear force is larger. The slurry that does not penetrate into the formation will accumulate at the excavation face, which is another way to form a filter cake.Figure 6
Filter cake formation mechanism analysis.
(a)
Pure bentonite(b)
Bentonite slurry with coarse-grained materialsFigure5(b) shows the final effect of SL33 slurry (with a particle size of 0.4 mm) forming the filter cake in S3 formation. It could be seen from the figure that the permeability state of slurry in the formation was obviously divided into three parts: the upper part is the filter cake, the middle part is the particle clogging area, and the bottom part is the permeability zone. Due to the blocking effect of the formation voids, fine sand particles added in the slurry would be silted up after being penetrated a certain distance in front of the excavation face. It could be seen from Figure 3 that under the same level of pressure load, the filtration capacity of SL33 was about half less than that of SL3. SL33 could bear more mud pressure. Finally, the infiltration area and filter cake formation area were dried, sieved, and weighed. The 0.3 mm particle additive accounted for 95% of the original addition. Considering the loss of additive particles in the experiment, most of the particles were blocked in the infiltration area and filter cake. It could be seen from this that the coarse-grained materials will first be silted up in the formation pores, reducing the average pore size of the original formation and forming new pores with a smaller average pore size. The clay particles in the subsequent bentonite slurry were more likely to be silted in the average pore space of the new formation. Thus, the formed sludge membrane has lower filtration capacity and stronger antipermeability damage ability. The interaction mechanism of the polymer chain, clay, and coarse-grained materials after adding coarse-grained materials is shown in Figure 6(b) [25].


## 5. Conclusion

In view of the problem of how to form a low-permeability filter cake in high-permeability strata, this paper investigates the influence of slurry viscosity and particle size on the formation of the filter cake through the slurry permeability experiment. Some new understandings and conclusions are obtained:(1)
In high-permeability formation, increasing the content of bentonite and increasing the viscosity of slurry are reliable methods to form the filter cake quickly and maintain the support pressure of the excavation face. The formation of the polymer chain between clay particles and CMC in bentonite slurry is the reason for the rapid film formation of pure bentonite slurry(2)
Adding coarse-grained materials to slurry could effectively improve the film-forming effect. A good synergistic effect can be achieved by adding granular materials slightly lower than the average pore size of the formation and pure bentonite mud. The amount of leakage is small, and the slurry is denser. It also provides a new idea for the selection of particle size distribution in slurry. The filter cake with better quality can be formed by adding coarse particles slightly smaller than the average pore size of the formation. But the premise is to select the correct way to calculate the average pore size of the formation(3)
There are two kinds of filter cake formed by bentonite slurry in high-permeability formation: one is the filter cake with the permeable zone, and the other is the filter cake with the permeable zone and particle clogging area. The latter kind of filter cake could be formed by adding coarse additives suitable for the average pore size of the formation(4)
There are many reasons that affect the viscosity of slurry. The paper only considers the influence of bentonite content on the viscosity of slurry. The follow-up research could supplement the effect of other additives such as CMC content and a new type ofHengDunNi material on the film-forming effect



---

*Source: 5546932-2021-04-09.xml*