# Adsorptive Performance of Polypyrrole-Based KOH-Activated Carbon for the Cationic Dye Crystal Violet: Kinetic and Equilibrium Studies

Authors: Abdulaziz Ali Alghamdi; Abdel-Basit Al-Odayni; Naaser A. Y. Abduh; Safiah A. Alramadhan; Mashael T. Aljboar; Waseem Sharaf Saeed
Journal: Adsorption Science & Technology
 (2021)

---

## Abstract

The aim of this work was to investigate the adsorptive performance of the polypyrrole-based KOH-activated carbon (PACK) in the removal of the basic dye crystal violet (CV) using a batch adsorption system. The equilibrium data, obtained at different initial CV concentrations (C0=50–500mg/L) and temperatures (25–45°C), were interpreted using the Langmuir, Freundlich, Temkin, and Dubinin-Radushkevich isotherms, with the Langmuir model providing a better fit (R2≥0.9997) and a maximum adsorption capacity of 497.51 mg/g at 45°C. Under the examined conditions, the values of the thermodynamic parameters free energy, enthalpy, and entropy indicate a spontaneous, endothermic, and physisorption adsorption process. The kinetic data of the adsorption process were very well described by a pseudo-second-order model (R2≥0.9996). However, surface diffusion seems to be the main rate-controlling step. Thus, we concluded that PACK shows commercial potential for the removal of cationic dyes such as CV from industrial effluent.


---

## Body

## 1. Introduction

Water pollution is a major environmental problem worldwide and requires urgent solutions. Industrial discharge is the main source of aquatic pollution [1] and results in the release of various physical, chemical, and biological pollutants, including suspended elements, dissolved gasses, mineral and organic solutes, and microorganisms [2]. The effluents from the paper, textile, leather, food, plastic, pharmaceutical, and printing industries typically contain large quantities of dyes that are used to color their products. Although many of the dyes used are not highly toxic, they cause visual pollution via aesthetic changes to the natural environment. Furthermore, they cause a reduction in light penetration into water, impinging on the photosynthesis of aquatic organisms. Nevertheless, many dyes have long-lasting hazardous and toxic effects on aquatic life, largely due to their high water solubility and nondegradability under natural conditions [3].Crystal violet (CV), also known as gentian violet, is a synthetic cationic dye belonging to the triphenylmethane group. Compared with anionic dyes, cationic dyes are more toxic to mammalian cells due to their ability to interact with negatively charged cell membrane surfaces, which enables them to penetrate into cells and concentrate in the cytoplasm [4]. CV is used in a variety of applications, including textile, plastic, and paper coloring; biological staining; and veterinary and animal medicine. However, researchers have reported that CV is a mutagen and mitotic poison that is toxic to mammalian cells and may exhibit carcinogenic effects [5–8]. Moreover, it can cause irritation to the skin and digestive tract. In extreme cases, CV can cause kidney failure and severe eye irritation leading to permanent blindness [9, 10]. These harmful effects necessitate efficient strategies for the removal of CV (and similar toxic dyes) from water bodies.Numerous methods have been developed for removing dyes from contaminated wastewater, including adsorption-based strategies, membrane filtration, photodegradation, coagulation, chemical oxidation, and biological processes [6, 11–13]. Among these, adsorption is the most common technique due to its numerous advantages, which include its superior performance, ease of operation, cost effectiveness, and the availability of necessary reagents. Furthermore, it has been widely demonstrated that activated carbon is the most effective adsorbent of the various applicable materials, which include natural clays, zeolites, biomasses, polymers, and polymer-based materials [14].Nitrogen-doped polypyrrole-based activated carbons (termed PACK), which is applied here for the removal of CV as a model harmful cationic dye, have been demonstrated to be excellent adsorbents. Various studies have indicated their high capacity in the adsorption of gasses including nitrogen and carbon dioxide, toxic heavy metal ions such as Pb(II), and anionic dyes such as methyl orange [15–18].The objective of the present study was to evaluate the efficiency of PACK in the removal of CV from synthetic wastewater. Its adsorption kinetics, isotherms, and thermodynamic parameters are investigated, discussed, and compared with those of other reported materials.


## 2. Materials and Methods

### 2.1. Materials

Pyrrole (Py, >98%), ammonium persulfate (APS, 98%), potassium hydroxide (KOH, 85%), sodium nitrate (NaNO3, 99%), and sodium hydroxide (NaOH, 98%) were purchased from Alfa Aesar, Karlsruhe, Germany. Hydrochloric acid (HCl, ~36%) and ethanol (EtOH, 99.5%) were obtained from Fisher Chemical, Loughborough, UK. CV (>90%) was provided by BDH Chemicals Ltd., Poole, England, UK, which was dried at 80°C for 2 h before use. All materials were used as received unless otherwise stated.


### 2.2. Adsorbent

PACK was prepared as described in the literature [15–18]. Briefly, HCl-doped polypyrrole (PPy) was prepared using an equimolar quantity (0.08 mol) of the monomer (Py) and the initiator (APS) in cold HCl (1 L, 0.1 M). The obtained material was washed and dried and then calcined under nitrogen at 650°C attained at 3°C/min for 2 h with four times the mass of KOH, the chemical activator, using a Carbolite MTF 12/38/250 tube furnace (Wolf Laboratories, UK). The PACK obtained was sequentially washed with 0.5 M HCl and then water until neutrality and dried.The pH at which the surface net charges of PACK are zero (pHPZC) was determined by a pH drift method described elsewhere [19, 20]. Typically, a solution of 0.1 M NaNO3 was prepared from which batches of 15 mL were adjusted in the pH range 2–11 using 0.1 M HCl or 0.1 M NaOH solution and denoted as pHi. To each sample, 0.015 g PACK was added, and the suspension was shaken intermittently for 24 h at room temperature (25±1°C). Then, the samples were filtered, and the final pH (pHf) of the solutions was measured. The pH of each sample was determined by an Orion 3 Star pH meter (Thermo Scientific, Beverly, MA, USA). pHPZC was determined by plotting pHi vs. pHf. Experiments were performed in duplicate and in parallel with unloaded samples as references. Moreover, a zeta potential of a sample of 1 mg/mL PACK-water dispersion (without pH adjustment) was measured by dynamic light scattering (DLS) (Zetasizer Nano; Malvern Instruments Ltd., London, UK) at room temperature.


### 2.3. Adsorbate

The chemical structure of the adsorbate CV is shown in Figure1. It is a well-known cationic dye with a color index number of C.I. 42555, a λmax of 590 nm, a molar mass of 407.98 g/mol, and solubility in water of 16 g/L at 25°C. A stock solution (1000 ppm) of CV was prepared in deionized water and further diluted to obtain the desired working concentrations. The extinction coefficient of CV (Ɛ=85436M−1·cm−1=0.2094ppm−1·cm−1) was obtained from a standard curve established using CV concentrations of 0.5, 1, 2, 3, and 4 ppm (R2=0.9864), with the dye concentrations measured photometrically using a UV-Vis spectrophotometer (U-2910, Hitachi, Tokyo, Japan) with reference to λmax at room temperature (25±1°C).Figure 1
Chemical structure of CV.


### 2.4. Adsorption Experiments

Adsorption equilibrium experiments were performed using 50 mL Eppendorf tubes at CV concentrations of 50, 100, 200, 300, and 500 ppm and temperatures of 25, 35, and 45°C, using 20 mg of the adsorbent (PACK), agitated at 150 rpm using a GFL 3017 digital shaker (GFL Gesellschaft für Labortechnik mbH, Burgwedel, Germany) for 24 h. Then, the adsorbent was filtered off, and the residual CV concentrations were measured. Kinetic experiments were conducted using 1 L Erlenmeyer flasks under the following conditions: 40 mg PACK, 500 mL CV solutions (15 and 45 ppm), 150 rpm agitation, and 25°C adsorption temperature. The residual dye concentrations were measured at 0, 5, 10, 30, 45, 60, 90, and 120 min, with at least two replicate concentration measurements being performed. All experiments were performed in duplicate without pH adjustment. However, the pH value of, e.g., 50 ppm CV solution analyzed at25±1°C was found to be 6.91±0.19. Regeneration trials were carried out by using solvent mixtures of acetone and 0.25 M of NaOH or HCl. However, a pilot experiment was performed first using single eluents of NaOH, HCl, acetic acid (AA), and acetone (Ac). The results obtained were not satisfied, with less than 24% desorption obtained when NaOH or HCl was used alone. Accordingly, elution systems of 25% acetone and 75% of 0.25 NaOH or HCl were chosen, and the reusability test was performed for three cycles of adsorption-desorption processes.


### 2.5. Theoretical Calculations

The equilibrium adsorption capacity (qe, mg/g) and the removal efficiency (Re, %) of PACK were determined using Equations (1) and (2), respectively:
(1)qe=C0−CeVm,(2)Re%=C0−CeC0100,where C0 and Ce are the adsorbate concentrations (mg/L) in the liquid phase before and after adsorption, V (L) is the solution volume, and m (g) is the dry mass of the adsorbent used.The adsorption mechanism was investigated by employing the pseudo-first-order (PFO), pseudo-second-order (PSO), and intraparticle diffusion (IPD) kinetics models proposed by Lagegren and Svenska [21], Ho and McKay [22], and Weber and Morris [23], respectively. The linear forms of these three models are given by Equations (3), (4), and (5), respectively.
(3)logqe−qt=logqe−k1t2.303,(4)tqt=1k2qe2+tqe,(5)qt=kidt0.5+C,where qt (mg/g) is the adsorption capacity at time t (min); k1 (min-1), k2 (g/(mg·min)), and kid (mg/(g·min0.5)) are the rate constants of the PFO, PSO, and IPD models, respectively; and C (mg/g) is the y-intercept of the IPD model, giving information about the boundary layer thickness, where higher values of C indicate greater boundary layer effects [23, 24]. The initial rate (h) (mg/(g·min)) of the adsorption process is typically given by the reciprocal value of the PSO plot intercept:
(6)h=k2qe2.The adsorption isotherm was modeled with the Langmuir [25, 26], Freundlich [27], Temkin [28], and Dubinin-Radushkevich (D-R) [29] linear form models, as given in Equations (7), (8), (9), and (10), respectively.
(7)Ceqe=Ceqm+1KLqm,(8)lnqe=lnKF+1nlnCe,(9)qe=RTKTlnA+RTKTlnCe=BlnA+BlnCe,(10)lnqe=lnqm−KD‐RƐ2,where qm (mg/g) is the maximum monolayer capacity; KL (L/mg), KF (mg/g)(L/mg)1/n, KT (J/mol), and KD‐R (mol2/kJ2) are, respectively, the Langmuir, Freundlich, Temkin, and D-R isotherm constants; T (K) is the absolute temperature, R (8.314 J/mol·K) is the universal gas constant, and A (L/mg) is the Temkin isotherm equilibrium binding constant. Basically, the Langmuir isotherm (Equation (7)) assumes monolayer adsorbent surface coverage. This can be better understood in terms of the so-called separation factor (RL, dimensionless) given in Equation (11), which describes the isotherm shape and indicates whether the adsorption is favorable or not, as per the following criteria: RL>1, unfavorable adsorption; RL=1, linear; 0<RL<1, favorable; and RL=0, irreversible.
(11)RL=11+KLC0.Conversely, the Freundlich isotherm, Equation (8), assumes multilayer adsorption and a heterogeneous adsorbent surface. The 1/n value indicates the relative distribution of energy and the heterogeneity of the adsorbent sites. Thus, 1/n>1 represents multilayer adsorption, 1/n=1 denotes a linear adsorption and concentration-independent adsorption with indistinguishable energy of all sites, 1/n<0 indicates Langmuir-shaped adsorption, and 0.1<1/n<1.0 represents favorable adsorption conditions where heterogeneity increases as the value approaches zero [30, 31]. The Temkin isotherm, Equation (9), assumes that, at moderate concentration, the intermolecular interactions cause the heats of adsorption of all the molecules to decrease linearly with coverage. KT is the Temkin equilibrium constant related to the maximum binding energy [32]. The D-R isotherm equation (Equation (10)) is an analog of the Langmuir equation. However, it is more general and ordinarily describes the adsorption mechanism assuming a Gaussian energy distribution onto a heterogeneous surface [33–35]. Therefore, it is only suitable for intermediate concentrations. The D-R constant, KD‐R, is the activity coefficient related to the mean sorption energy, while Ɛ (Equation (12)) is the Polanyi potential. The mean adsorption energy, E (kJ/mol), can be calculated using Equation (13). It provides information about the adsorbate free energy required for the transfer of one mole from infinite distance to the adsorbent surface, indicating whether the adsorption mechanism is a chemical ion exchange (9–16 kJ/mol) or physical (less than 8 kJ/mol) [28, 36, 37].
(12)Ɛ=RTln1+1Ce,(13)E=12KD‐R0.5.The effect of heat on the adsorption system was determined using the thermodynamic parameters Gibbs free energy change (ΔG°), enthalpy change (ΔH°), and entropy change (ΔS°), which are expressed by the Van’t Hoff equation [38]:
(14)lnK0=ΔS°R−ΔH°RT=−ΔG°RT,(15)K0=qeCe,where K0 (L/g) is the apparent equilibrium constant.


## 2.1. Materials

Pyrrole (Py, >98%), ammonium persulfate (APS, 98%), potassium hydroxide (KOH, 85%), sodium nitrate (NaNO3, 99%), and sodium hydroxide (NaOH, 98%) were purchased from Alfa Aesar, Karlsruhe, Germany. Hydrochloric acid (HCl, ~36%) and ethanol (EtOH, 99.5%) were obtained from Fisher Chemical, Loughborough, UK. CV (>90%) was provided by BDH Chemicals Ltd., Poole, England, UK, which was dried at 80°C for 2 h before use. All materials were used as received unless otherwise stated.


## 2.2. Adsorbent

PACK was prepared as described in the literature [15–18]. Briefly, HCl-doped polypyrrole (PPy) was prepared using an equimolar quantity (0.08 mol) of the monomer (Py) and the initiator (APS) in cold HCl (1 L, 0.1 M). The obtained material was washed and dried and then calcined under nitrogen at 650°C attained at 3°C/min for 2 h with four times the mass of KOH, the chemical activator, using a Carbolite MTF 12/38/250 tube furnace (Wolf Laboratories, UK). The PACK obtained was sequentially washed with 0.5 M HCl and then water until neutrality and dried.The pH at which the surface net charges of PACK are zero (pHPZC) was determined by a pH drift method described elsewhere [19, 20]. Typically, a solution of 0.1 M NaNO3 was prepared from which batches of 15 mL were adjusted in the pH range 2–11 using 0.1 M HCl or 0.1 M NaOH solution and denoted as pHi. To each sample, 0.015 g PACK was added, and the suspension was shaken intermittently for 24 h at room temperature (25±1°C). Then, the samples were filtered, and the final pH (pHf) of the solutions was measured. The pH of each sample was determined by an Orion 3 Star pH meter (Thermo Scientific, Beverly, MA, USA). pHPZC was determined by plotting pHi vs. pHf. Experiments were performed in duplicate and in parallel with unloaded samples as references. Moreover, a zeta potential of a sample of 1 mg/mL PACK-water dispersion (without pH adjustment) was measured by dynamic light scattering (DLS) (Zetasizer Nano; Malvern Instruments Ltd., London, UK) at room temperature.


## 2.3. Adsorbate

The chemical structure of the adsorbate CV is shown in Figure1. It is a well-known cationic dye with a color index number of C.I. 42555, a λmax of 590 nm, a molar mass of 407.98 g/mol, and solubility in water of 16 g/L at 25°C. A stock solution (1000 ppm) of CV was prepared in deionized water and further diluted to obtain the desired working concentrations. The extinction coefficient of CV (Ɛ=85436M−1·cm−1=0.2094ppm−1·cm−1) was obtained from a standard curve established using CV concentrations of 0.5, 1, 2, 3, and 4 ppm (R2=0.9864), with the dye concentrations measured photometrically using a UV-Vis spectrophotometer (U-2910, Hitachi, Tokyo, Japan) with reference to λmax at room temperature (25±1°C).Figure 1
Chemical structure of CV.


## 2.4. Adsorption Experiments

Adsorption equilibrium experiments were performed using 50 mL Eppendorf tubes at CV concentrations of 50, 100, 200, 300, and 500 ppm and temperatures of 25, 35, and 45°C, using 20 mg of the adsorbent (PACK), agitated at 150 rpm using a GFL 3017 digital shaker (GFL Gesellschaft für Labortechnik mbH, Burgwedel, Germany) for 24 h. Then, the adsorbent was filtered off, and the residual CV concentrations were measured. Kinetic experiments were conducted using 1 L Erlenmeyer flasks under the following conditions: 40 mg PACK, 500 mL CV solutions (15 and 45 ppm), 150 rpm agitation, and 25°C adsorption temperature. The residual dye concentrations were measured at 0, 5, 10, 30, 45, 60, 90, and 120 min, with at least two replicate concentration measurements being performed. All experiments were performed in duplicate without pH adjustment. However, the pH value of, e.g., 50 ppm CV solution analyzed at25±1°C was found to be 6.91±0.19. Regeneration trials were carried out by using solvent mixtures of acetone and 0.25 M of NaOH or HCl. However, a pilot experiment was performed first using single eluents of NaOH, HCl, acetic acid (AA), and acetone (Ac). The results obtained were not satisfied, with less than 24% desorption obtained when NaOH or HCl was used alone. Accordingly, elution systems of 25% acetone and 75% of 0.25 NaOH or HCl were chosen, and the reusability test was performed for three cycles of adsorption-desorption processes.


## 2.5. Theoretical Calculations

The equilibrium adsorption capacity (qe, mg/g) and the removal efficiency (Re, %) of PACK were determined using Equations (1) and (2), respectively:
(1)qe=C0−CeVm,(2)Re%=C0−CeC0100,where C0 and Ce are the adsorbate concentrations (mg/L) in the liquid phase before and after adsorption, V (L) is the solution volume, and m (g) is the dry mass of the adsorbent used.The adsorption mechanism was investigated by employing the pseudo-first-order (PFO), pseudo-second-order (PSO), and intraparticle diffusion (IPD) kinetics models proposed by Lagegren and Svenska [21], Ho and McKay [22], and Weber and Morris [23], respectively. The linear forms of these three models are given by Equations (3), (4), and (5), respectively.
(3)logqe−qt=logqe−k1t2.303,(4)tqt=1k2qe2+tqe,(5)qt=kidt0.5+C,where qt (mg/g) is the adsorption capacity at time t (min); k1 (min-1), k2 (g/(mg·min)), and kid (mg/(g·min0.5)) are the rate constants of the PFO, PSO, and IPD models, respectively; and C (mg/g) is the y-intercept of the IPD model, giving information about the boundary layer thickness, where higher values of C indicate greater boundary layer effects [23, 24]. The initial rate (h) (mg/(g·min)) of the adsorption process is typically given by the reciprocal value of the PSO plot intercept:
(6)h=k2qe2.The adsorption isotherm was modeled with the Langmuir [25, 26], Freundlich [27], Temkin [28], and Dubinin-Radushkevich (D-R) [29] linear form models, as given in Equations (7), (8), (9), and (10), respectively.
(7)Ceqe=Ceqm+1KLqm,(8)lnqe=lnKF+1nlnCe,(9)qe=RTKTlnA+RTKTlnCe=BlnA+BlnCe,(10)lnqe=lnqm−KD‐RƐ2,where qm (mg/g) is the maximum monolayer capacity; KL (L/mg), KF (mg/g)(L/mg)1/n, KT (J/mol), and KD‐R (mol2/kJ2) are, respectively, the Langmuir, Freundlich, Temkin, and D-R isotherm constants; T (K) is the absolute temperature, R (8.314 J/mol·K) is the universal gas constant, and A (L/mg) is the Temkin isotherm equilibrium binding constant. Basically, the Langmuir isotherm (Equation (7)) assumes monolayer adsorbent surface coverage. This can be better understood in terms of the so-called separation factor (RL, dimensionless) given in Equation (11), which describes the isotherm shape and indicates whether the adsorption is favorable or not, as per the following criteria: RL>1, unfavorable adsorption; RL=1, linear; 0<RL<1, favorable; and RL=0, irreversible.
(11)RL=11+KLC0.Conversely, the Freundlich isotherm, Equation (8), assumes multilayer adsorption and a heterogeneous adsorbent surface. The 1/n value indicates the relative distribution of energy and the heterogeneity of the adsorbent sites. Thus, 1/n>1 represents multilayer adsorption, 1/n=1 denotes a linear adsorption and concentration-independent adsorption with indistinguishable energy of all sites, 1/n<0 indicates Langmuir-shaped adsorption, and 0.1<1/n<1.0 represents favorable adsorption conditions where heterogeneity increases as the value approaches zero [30, 31]. The Temkin isotherm, Equation (9), assumes that, at moderate concentration, the intermolecular interactions cause the heats of adsorption of all the molecules to decrease linearly with coverage. KT is the Temkin equilibrium constant related to the maximum binding energy [32]. The D-R isotherm equation (Equation (10)) is an analog of the Langmuir equation. However, it is more general and ordinarily describes the adsorption mechanism assuming a Gaussian energy distribution onto a heterogeneous surface [33–35]. Therefore, it is only suitable for intermediate concentrations. The D-R constant, KD‐R, is the activity coefficient related to the mean sorption energy, while Ɛ (Equation (12)) is the Polanyi potential. The mean adsorption energy, E (kJ/mol), can be calculated using Equation (13). It provides information about the adsorbate free energy required for the transfer of one mole from infinite distance to the adsorbent surface, indicating whether the adsorption mechanism is a chemical ion exchange (9–16 kJ/mol) or physical (less than 8 kJ/mol) [28, 36, 37].
(12)Ɛ=RTln1+1Ce,(13)E=12KD‐R0.5.The effect of heat on the adsorption system was determined using the thermodynamic parameters Gibbs free energy change (ΔG°), enthalpy change (ΔH°), and entropy change (ΔS°), which are expressed by the Van’t Hoff equation [38]:
(14)lnK0=ΔS°R−ΔH°RT=−ΔG°RT,(15)K0=qeCe,where K0 (L/g) is the apparent equilibrium constant.


## 3. Results and Discussion

### 3.1. Characterization

The essential features of the adsorbent PACK, including its structural and surface properties as well as its efficacies as an adsorbent of gasses, heavy metal ions, and anionic dyes represented by carbon dioxide (CO2), lead ions (Pb2+), and methyl orange (MO), respectively, have been reported by Alghamdi et al. [15–17] and Sevilla et al. [18] (Table 1). Furthermore, to obtain insight into the surface charge, the pH at which the net surface charge is zero (pHPZC) was estimated and found to be 6.35 (Figure 2). Thus, the surface is positively charged below pH 6.35 and negatively charged above pH 6.35. Moreover, the zeta potential at neutral pH (-30.6 mV, see Figure S1) indicated a negative surface which further supports the pHPZC result.Table 1
Properties of PACK.
Chemical composition (wt%)BETAdsorption capacity (mg/g)CHNOKClSA (m2/g)APD (nm)CO2Pb2+MO73.170.864.7020.370.400.5028712.35050521BET: Brunauer–Emmett–Teller; SA: surface area; APD: average pore diameter; MO: methyl orange.Figure 2
Point of zero charge for PACK adsorbent.


### 3.2. Effect of Contact Time and Kinetic Studies

Figure3 shows the time profile of CV adsorption onto PACK for two different initial concentrations (15 and 45 ppm). Figure 4 shows a histogram representing the values of the adsorption efficiency (Re, %) as well as the capacities at the first adsorption phase (q5t, 5 min) and at equilibrium (qe, 60 min). Clearly, the adsorption is initially fast (~5 min), indicating an abundance of readily available active sites on the adsorbent surface. Thereafter, the adsorption rate slows dramatically as the active sites are gradually saturated by the adsorbate molecules, reaching equilibrium after ~60 min. Moreover, the data indicate that more than 80% of the adsorbent sites are occupied in the first 5 min (Figure 3). It is also observed that as the initial dye concentration increases, the adsorption capacity (qe) increases while the efficiency (Re) decreases. The initial rapid adsorption (i.e., in the first 5 min) indicates a chemisorption process. However, for the second phase, the profile suggests a physisorption mechanism, which is possibly governed by a diffusion mechanism [39].Figure 3
Effect of contact time on the adsorption of CV onto PACK.Figure 4
Graphical illustration of the adsorption of CV (C0=15 and 45 ppm) on PACK after 5 min (q5t, the initial adsorption phase) and at equilibrium (qe), along with efficiency (%) values. Conditions: adsorbatevolume=500mL; temperature=25°C; adsorbentmass=0.04g; agitation=150rpm; apparentequilibriumtime=90min.The mechanism involved in this adsorption system was investigated using PFO, PSO, and IPD kinetic models (Figures5, 6, and 7), as described by Equations (3), (4), and (5), respectively. The corresponding kinetic parameters and correlation coefficients are presented in Table 2. As can be seen, the relatively higher value of the correlation coefficient, which is an important criterion in the determination of good fit, for the PSO model (R2≥0.9996) compared to those of the PFO (R2≤0.8392) and IPD (R2≤0.8143) models as well as the very close similarity of the experimental and PSO model adsorption capacity (qe) values indicates that the adsorption mechanism is best described by the PSO model. The poor fit of the IPD (R2≤0.8143) model reveals the negligible effect of intraparticle diffusion on the rate-controlling step. Moreover, the intercept deviation from the origin indicates the involvement of a film-diffusion mechanism. The high value of the intercept C, which is the measure of the film boundary thickness, reflects the significant effect of external film resistance on the adsorption mechanism. Moreover, the IPD plot indicates the presence of more than one single mechanism. Generally, the fast adsorption rate in the first few minutes is not recognized as a rate-limiting step and can be explained by the abundance of CV dye molecules and PACK active sites in the adsorption system. However, the two-stage IPD plot for the adsorption process at a CV concentration of 45 ppm (Figure 7) may indicate a gradual adsorption controlled by a boundary layer (stage 1) followed by a slow adsorption controlled by intraparticle diffusion and equilibrium processes (stage 2); data of the two-stage IPD model are given in the supporting information, Table S1.Figure 5
PFO kinetic plot for the adsorption of CV onto PACK. Conditions:C0=15, 45 ppm; adsorbatevolume=500mL; temperature=25°C; adsorbent=0.04g; agitation=150rpm; time=90min.Figure 6
PSO kinetic plot for the adsorption of CV onto PACK.Figure 7
Webber-Morris intraparticle diffusion plot for the adsorption of CV onto PACK (see Figure4 for conditions).Table 2
Kinetic parameters for the adsorption of CV onto PACK.
C0 (mg/L)qe‐exp (mg/g)PFOPSOIPDqe (mg/g)k1 (1/min)R2qe (mg/g)k2 (g/(mg·min))R2h (mg/(g·min))kid (mg/(g·min0.5))C (mg/g)R21575.7722.530.0490.829175.990.0130.999776.452.03158.920.814345168.1969.070.0800.8392168.350.00690.9996145.392.910142.960.7450


### 3.3. Adsorption Isotherms

Adsorption isotherms generally describe the way in which an adsorbate interacts with an adsorbent when equilibrium is attained at a certain temperature. In this study, the adsorption system was evaluated at 25, 35, and 45°C, and the experimental data were fitted into four models expressed by Equations (7)–(10) (Figure 8), and the calculated parameters are presented in Table 3. The goodness of fit for the experimental data was found to be in the order LangmuirR2≥0.9997>TemkinR2≤0.9853>FreundlichR2≤0.9688>D‐RR2≤0.9382. The maximum adsorption capacity (the monolayer surface coverage) (qm, mg/g), for the initial CV concentration range 50–500 ppm, was increased from 380.2 to 497.5 mg/g as the temperature increases from 298 to 318 K. Over the same temperature range, the values of the heterogeneity factor 1/n (0.156–0.183) and separation factor (RL) (0.016–0.002) indicate favorable adsorption. The decrease in the values of the Temkin equilibrium binding constant (A) with temperature increase indicates favorable adsorption process at high temperatures. According to the D-R model, the values of the mean adsorption energy, E (kJ/mol), over the tested temperatures are in the range 8.174–8.357 kJ/mol, indicating a predominantly physisorption process (i.e., Echemical>9; Ephysical<8) [28, 36]. As the values of the E are in the boundary between the two mechanisms, the involvement of the ion exchange adsorption mechanism cannot be ruled out. Such electrostatic interaction is expected between the positively charged CV particles and negative sites on PACK.Figure 8
Langmuir, Freundlich, Temkin, and D-R isotherm plots for CV adsorption onto PACK.Table 3
Langmuir, Freundlich, Temkin, and D-R isotherm parameters for CV adsorption onto PACK.
(a)Temp. (K)LangmuirFreundlichqm (mg/g)KL (L/mg)RL (C0mg/L=50–500)R2KF (mg/g) (L/mg)1/n1/nnR2298380.231.130.0172–0.00180.9999194.230.1566.410.9535308421.941.230.0159–0.00160.9999211.850.1656.060.9534318497.511.260.0157–0.00160.9997237.750.1835.480.9688(b)T (K)TemkinDubinin-Radushkevich (D-R)A (L/mg)KT (J/mol)BR2KD‐R (mol2/J2)qm (mg/g)E (kJ/mol)R22983693.9686.5028.6430.98537.48×10−9308.938.1740.93823083271.6380.4031.8510.97197.18×10−9326.248.3450.92853182031.8569.0438.2940.96907.16×10−9348.398.3570.9071


### 3.4. Adsorption Thermodynamics

The values of Gibbs free energy (ΔG°), enthalpy (ΔH°), and entropy (ΔS°) changes obtained for CV concentrations of 50, 100, 200, 300, and 500 ppm are given in Table 4. The negative values of ΔG° indicate the spontaneity and feasibility of the adsorption, whereas the positive values of ΔH° and ΔS° indicate the endothermic nature and increase in randomness of the process, respectively [40]. According to the data obtained under the applied conditions, the adsorption process is more favored at low concentrations and at high temperatures (Table 4). It is known that the value of ΔG° for chemisorption (−80 to −400 kJ/mol) is higher than that of physical adsorption (from 0 to −20 kJ/mol). Moreover, a value of ΔH° less than 40 kJ/mol suggests a physical process [41]. Here, the ranges of ΔG° and ΔH° values indicate a physical adsorption mechanism, supporting our earlier conclusion.Table 4
Thermodynamic parameters for the adsorption of CV onto PACK.
C0 (mg/L)T (K)lnK0ΔG° (kJ/mol)ΔH° (kJ/mol)ΔS° (J/mol·K)R25029810.1725−5.747214.0845131.9420.984430810.3957−5.995631810.5292−6.22401002988.7861−5.384218.5563135.4380.98803089.0738−5.64743189.2561−5.88332002984.4129−3.678032.5018145.2140.92603084.6391−3.80153185.2423−4.38023002982.7850−2.537656.9083214.3780.99423083.6251−3.29793184.2276−3.81155002980.65371.053234.8243121.8230.94963080.93570.17023181.5416−1.1443Figure9 is a schematic presentation for the adsorption mechanism in which π-π and ionic interactions are dominant. This is in line with the results predicted by the adsorption models discussed above. Thus, the physisorption mechanism is practically superior; however, chemical interaction involving strong ionic bonds and ion exchange cannot be ignored, a case that is evinced by the results of isotherms and thermodynamic parameter values, which are generally in the region of the physical process but closer to chemical limits. Moreover, the effect of the diffusion process in the adsorption mechanism is also expected at least in the last stage of adsorption.Figure 9
Schematic presentation of the adsorption mechanism of the cationic dye crystal violet by PACK adsorbent.


### 3.5. Reusability

As the reusability of the adsorbent is of crucial importance in the economic development, efficient protocols for adsorbate recovery and adsorbent regeneration have to be established; however, common adsorbents vary greatly in their stability and applicability to be regenerated. Figure10 illustrates the chemical regeneration efficiency calculated according to [5]
(16)Desorption%=DesorbedmassAdsorbedmass100.Figure 10
Desorption percentage of CV from PACK after three cycles using solvent mixtures (NaOH/acetone or HCl/acetone) or single solvent (NaOH or HCl; only cycle one presented).The low desorption efficiency of a single solvent elution system (NaOH, HCl) may be due to ion competition, indicating high comparative affinity of CV dye toward PACK (Figure10; only cycle 1 is presented). However, NaOH shows better desorption performance of CV than HCl, possibly due to electrostatic repulsion at pH above pHPZC [5].When acetone was added to the above single solvents, the regeneration efficiency was enhanced. As shown in Figure10, the desorption efficiency reduced about 4 and 11% when the binary eluents NaOH/Ac and HCl/Ac were used, respectively. The results generally indicate a total mass recovery of CV of about 72% after three cycles of the adsorption-desorption process. The reduced efficiency (28%) could be due to incomplete desorption of CV [42]. The results indicate the reusability of the adsorbent with possible regeneration enhancement; however, it necessitates further optimization of the regeneration conditions including solvents types, concentrations, solution pH, etc.


### 3.6. Relative Performance of PACK

For comparative purposes, the values of adsorption capacity,qm (mg/g), of several adsorbents reported in the literature are provided in Table 5. Furthermore, information on the adsorbent source, reusability, and adsorption conditions has also been tabulated. As can be seen, the qm of PACK for CV is 497.51 mg/g, which is well positioned with respect to the listed materials. The differences in the adsorption capacities are due to the variety in the chemical and morphological properties of the adsorbents, including their functional groups, surface areas, and porosities. However, the suitability of a potential adsorbent is generally assessed in terms of efficiency, availability, reusability, and cost-effectiveness. The naturally available and the agricultural and industrial wastes may be inexpensive adsorbents, but they are less efficient. In many cases, modification of such materials has increased their adsorption efficiencies. Conversely, the synthetic adsorbents, including activated carbon, exhibit better performances in the removal of water pollutants ([16, 43]). However, the source of the carbonaceous materials, processing, and activation conditions are important factors in the final properties of the carbon. The excellent adsorptive performance of PACK can be ascribed to the properties discussed above.Table 5
Comparison of the CV adsorption capacities of various reported adsorbents.
Adsorbentqm (mg/L)Adsorption conditionsRef.Source typeCo (mg/L)pHT (°C)Adsorbent dosage (g/L)NaOH-modified rice husk (NMRH)44.88508201.0[44]AgricultureGranulated-activated carbon90.915-1511401.0[5]CommercialNatural zeolite177.7520-20010252.0[45]Natural clayMerck-activated carbon84.1130-807251.0[45]CommercialZnCl2-activated carbon (ZCAC)142.8520-908251.0[19]AgricultureJute fiber carbon27.9920-1108301.0[46]AgriculturePhosphoric acid-activated carbon (PAAC)60.3810-406RT3.0[10]AgricultureSulfuric acid-activated carbon (SAAC)85.6810-406RT2.0[10]AgricultureF. orientalis L.-activated carbon769.23200-800—250.8[47]AgricultureBiochar from palm kernel shell (BC-PKS)24.4550-50072516.7[48]BiomassPalm kernel fiber78.920-1807.2252.0[49]AgricultureTomato waste nanoporous carbon (TWNC)64.5220-3508402.0[50]BiomassPACK497.5150-5006.9450.8This workSynthetic


## 3.1. Characterization

The essential features of the adsorbent PACK, including its structural and surface properties as well as its efficacies as an adsorbent of gasses, heavy metal ions, and anionic dyes represented by carbon dioxide (CO2), lead ions (Pb2+), and methyl orange (MO), respectively, have been reported by Alghamdi et al. [15–17] and Sevilla et al. [18] (Table 1). Furthermore, to obtain insight into the surface charge, the pH at which the net surface charge is zero (pHPZC) was estimated and found to be 6.35 (Figure 2). Thus, the surface is positively charged below pH 6.35 and negatively charged above pH 6.35. Moreover, the zeta potential at neutral pH (-30.6 mV, see Figure S1) indicated a negative surface which further supports the pHPZC result.Table 1
Properties of PACK.
Chemical composition (wt%)BETAdsorption capacity (mg/g)CHNOKClSA (m2/g)APD (nm)CO2Pb2+MO73.170.864.7020.370.400.5028712.35050521BET: Brunauer–Emmett–Teller; SA: surface area; APD: average pore diameter; MO: methyl orange.Figure 2
Point of zero charge for PACK adsorbent.


## 3.2. Effect of Contact Time and Kinetic Studies

Figure3 shows the time profile of CV adsorption onto PACK for two different initial concentrations (15 and 45 ppm). Figure 4 shows a histogram representing the values of the adsorption efficiency (Re, %) as well as the capacities at the first adsorption phase (q5t, 5 min) and at equilibrium (qe, 60 min). Clearly, the adsorption is initially fast (~5 min), indicating an abundance of readily available active sites on the adsorbent surface. Thereafter, the adsorption rate slows dramatically as the active sites are gradually saturated by the adsorbate molecules, reaching equilibrium after ~60 min. Moreover, the data indicate that more than 80% of the adsorbent sites are occupied in the first 5 min (Figure 3). It is also observed that as the initial dye concentration increases, the adsorption capacity (qe) increases while the efficiency (Re) decreases. The initial rapid adsorption (i.e., in the first 5 min) indicates a chemisorption process. However, for the second phase, the profile suggests a physisorption mechanism, which is possibly governed by a diffusion mechanism [39].Figure 3
Effect of contact time on the adsorption of CV onto PACK.Figure 4
Graphical illustration of the adsorption of CV (C0=15 and 45 ppm) on PACK after 5 min (q5t, the initial adsorption phase) and at equilibrium (qe), along with efficiency (%) values. Conditions: adsorbatevolume=500mL; temperature=25°C; adsorbentmass=0.04g; agitation=150rpm; apparentequilibriumtime=90min.The mechanism involved in this adsorption system was investigated using PFO, PSO, and IPD kinetic models (Figures5, 6, and 7), as described by Equations (3), (4), and (5), respectively. The corresponding kinetic parameters and correlation coefficients are presented in Table 2. As can be seen, the relatively higher value of the correlation coefficient, which is an important criterion in the determination of good fit, for the PSO model (R2≥0.9996) compared to those of the PFO (R2≤0.8392) and IPD (R2≤0.8143) models as well as the very close similarity of the experimental and PSO model adsorption capacity (qe) values indicates that the adsorption mechanism is best described by the PSO model. The poor fit of the IPD (R2≤0.8143) model reveals the negligible effect of intraparticle diffusion on the rate-controlling step. Moreover, the intercept deviation from the origin indicates the involvement of a film-diffusion mechanism. The high value of the intercept C, which is the measure of the film boundary thickness, reflects the significant effect of external film resistance on the adsorption mechanism. Moreover, the IPD plot indicates the presence of more than one single mechanism. Generally, the fast adsorption rate in the first few minutes is not recognized as a rate-limiting step and can be explained by the abundance of CV dye molecules and PACK active sites in the adsorption system. However, the two-stage IPD plot for the adsorption process at a CV concentration of 45 ppm (Figure 7) may indicate a gradual adsorption controlled by a boundary layer (stage 1) followed by a slow adsorption controlled by intraparticle diffusion and equilibrium processes (stage 2); data of the two-stage IPD model are given in the supporting information, Table S1.Figure 5
PFO kinetic plot for the adsorption of CV onto PACK. Conditions:C0=15, 45 ppm; adsorbatevolume=500mL; temperature=25°C; adsorbent=0.04g; agitation=150rpm; time=90min.Figure 6
PSO kinetic plot for the adsorption of CV onto PACK.Figure 7
Webber-Morris intraparticle diffusion plot for the adsorption of CV onto PACK (see Figure4 for conditions).Table 2
Kinetic parameters for the adsorption of CV onto PACK.
C0 (mg/L)qe‐exp (mg/g)PFOPSOIPDqe (mg/g)k1 (1/min)R2qe (mg/g)k2 (g/(mg·min))R2h (mg/(g·min))kid (mg/(g·min0.5))C (mg/g)R21575.7722.530.0490.829175.990.0130.999776.452.03158.920.814345168.1969.070.0800.8392168.350.00690.9996145.392.910142.960.7450


## 3.3. Adsorption Isotherms

Adsorption isotherms generally describe the way in which an adsorbate interacts with an adsorbent when equilibrium is attained at a certain temperature. In this study, the adsorption system was evaluated at 25, 35, and 45°C, and the experimental data were fitted into four models expressed by Equations (7)–(10) (Figure 8), and the calculated parameters are presented in Table 3. The goodness of fit for the experimental data was found to be in the order LangmuirR2≥0.9997>TemkinR2≤0.9853>FreundlichR2≤0.9688>D‐RR2≤0.9382. The maximum adsorption capacity (the monolayer surface coverage) (qm, mg/g), for the initial CV concentration range 50–500 ppm, was increased from 380.2 to 497.5 mg/g as the temperature increases from 298 to 318 K. Over the same temperature range, the values of the heterogeneity factor 1/n (0.156–0.183) and separation factor (RL) (0.016–0.002) indicate favorable adsorption. The decrease in the values of the Temkin equilibrium binding constant (A) with temperature increase indicates favorable adsorption process at high temperatures. According to the D-R model, the values of the mean adsorption energy, E (kJ/mol), over the tested temperatures are in the range 8.174–8.357 kJ/mol, indicating a predominantly physisorption process (i.e., Echemical>9; Ephysical<8) [28, 36]. As the values of the E are in the boundary between the two mechanisms, the involvement of the ion exchange adsorption mechanism cannot be ruled out. Such electrostatic interaction is expected between the positively charged CV particles and negative sites on PACK.Figure 8
Langmuir, Freundlich, Temkin, and D-R isotherm plots for CV adsorption onto PACK.Table 3
Langmuir, Freundlich, Temkin, and D-R isotherm parameters for CV adsorption onto PACK.
(a)Temp. (K)LangmuirFreundlichqm (mg/g)KL (L/mg)RL (C0mg/L=50–500)R2KF (mg/g) (L/mg)1/n1/nnR2298380.231.130.0172–0.00180.9999194.230.1566.410.9535308421.941.230.0159–0.00160.9999211.850.1656.060.9534318497.511.260.0157–0.00160.9997237.750.1835.480.9688(b)T (K)TemkinDubinin-Radushkevich (D-R)A (L/mg)KT (J/mol)BR2KD‐R (mol2/J2)qm (mg/g)E (kJ/mol)R22983693.9686.5028.6430.98537.48×10−9308.938.1740.93823083271.6380.4031.8510.97197.18×10−9326.248.3450.92853182031.8569.0438.2940.96907.16×10−9348.398.3570.9071


## 3.4. Adsorption Thermodynamics

The values of Gibbs free energy (ΔG°), enthalpy (ΔH°), and entropy (ΔS°) changes obtained for CV concentrations of 50, 100, 200, 300, and 500 ppm are given in Table 4. The negative values of ΔG° indicate the spontaneity and feasibility of the adsorption, whereas the positive values of ΔH° and ΔS° indicate the endothermic nature and increase in randomness of the process, respectively [40]. According to the data obtained under the applied conditions, the adsorption process is more favored at low concentrations and at high temperatures (Table 4). It is known that the value of ΔG° for chemisorption (−80 to −400 kJ/mol) is higher than that of physical adsorption (from 0 to −20 kJ/mol). Moreover, a value of ΔH° less than 40 kJ/mol suggests a physical process [41]. Here, the ranges of ΔG° and ΔH° values indicate a physical adsorption mechanism, supporting our earlier conclusion.Table 4
Thermodynamic parameters for the adsorption of CV onto PACK.
C0 (mg/L)T (K)lnK0ΔG° (kJ/mol)ΔH° (kJ/mol)ΔS° (J/mol·K)R25029810.1725−5.747214.0845131.9420.984430810.3957−5.995631810.5292−6.22401002988.7861−5.384218.5563135.4380.98803089.0738−5.64743189.2561−5.88332002984.4129−3.678032.5018145.2140.92603084.6391−3.80153185.2423−4.38023002982.7850−2.537656.9083214.3780.99423083.6251−3.29793184.2276−3.81155002980.65371.053234.8243121.8230.94963080.93570.17023181.5416−1.1443Figure9 is a schematic presentation for the adsorption mechanism in which π-π and ionic interactions are dominant. This is in line with the results predicted by the adsorption models discussed above. Thus, the physisorption mechanism is practically superior; however, chemical interaction involving strong ionic bonds and ion exchange cannot be ignored, a case that is evinced by the results of isotherms and thermodynamic parameter values, which are generally in the region of the physical process but closer to chemical limits. Moreover, the effect of the diffusion process in the adsorption mechanism is also expected at least in the last stage of adsorption.Figure 9
Schematic presentation of the adsorption mechanism of the cationic dye crystal violet by PACK adsorbent.


## 3.5. Reusability

As the reusability of the adsorbent is of crucial importance in the economic development, efficient protocols for adsorbate recovery and adsorbent regeneration have to be established; however, common adsorbents vary greatly in their stability and applicability to be regenerated. Figure10 illustrates the chemical regeneration efficiency calculated according to [5]
(16)Desorption%=DesorbedmassAdsorbedmass100.Figure 10
Desorption percentage of CV from PACK after three cycles using solvent mixtures (NaOH/acetone or HCl/acetone) or single solvent (NaOH or HCl; only cycle one presented).The low desorption efficiency of a single solvent elution system (NaOH, HCl) may be due to ion competition, indicating high comparative affinity of CV dye toward PACK (Figure10; only cycle 1 is presented). However, NaOH shows better desorption performance of CV than HCl, possibly due to electrostatic repulsion at pH above pHPZC [5].When acetone was added to the above single solvents, the regeneration efficiency was enhanced. As shown in Figure10, the desorption efficiency reduced about 4 and 11% when the binary eluents NaOH/Ac and HCl/Ac were used, respectively. The results generally indicate a total mass recovery of CV of about 72% after three cycles of the adsorption-desorption process. The reduced efficiency (28%) could be due to incomplete desorption of CV [42]. The results indicate the reusability of the adsorbent with possible regeneration enhancement; however, it necessitates further optimization of the regeneration conditions including solvents types, concentrations, solution pH, etc.


## 3.6. Relative Performance of PACK

For comparative purposes, the values of adsorption capacity,qm (mg/g), of several adsorbents reported in the literature are provided in Table 5. Furthermore, information on the adsorbent source, reusability, and adsorption conditions has also been tabulated. As can be seen, the qm of PACK for CV is 497.51 mg/g, which is well positioned with respect to the listed materials. The differences in the adsorption capacities are due to the variety in the chemical and morphological properties of the adsorbents, including their functional groups, surface areas, and porosities. However, the suitability of a potential adsorbent is generally assessed in terms of efficiency, availability, reusability, and cost-effectiveness. The naturally available and the agricultural and industrial wastes may be inexpensive adsorbents, but they are less efficient. In many cases, modification of such materials has increased their adsorption efficiencies. Conversely, the synthetic adsorbents, including activated carbon, exhibit better performances in the removal of water pollutants ([16, 43]). However, the source of the carbonaceous materials, processing, and activation conditions are important factors in the final properties of the carbon. The excellent adsorptive performance of PACK can be ascribed to the properties discussed above.Table 5
Comparison of the CV adsorption capacities of various reported adsorbents.
Adsorbentqm (mg/L)Adsorption conditionsRef.Source typeCo (mg/L)pHT (°C)Adsorbent dosage (g/L)NaOH-modified rice husk (NMRH)44.88508201.0[44]AgricultureGranulated-activated carbon90.915-1511401.0[5]CommercialNatural zeolite177.7520-20010252.0[45]Natural clayMerck-activated carbon84.1130-807251.0[45]CommercialZnCl2-activated carbon (ZCAC)142.8520-908251.0[19]AgricultureJute fiber carbon27.9920-1108301.0[46]AgriculturePhosphoric acid-activated carbon (PAAC)60.3810-406RT3.0[10]AgricultureSulfuric acid-activated carbon (SAAC)85.6810-406RT2.0[10]AgricultureF. orientalis L.-activated carbon769.23200-800—250.8[47]AgricultureBiochar from palm kernel shell (BC-PKS)24.4550-50072516.7[48]BiomassPalm kernel fiber78.920-1807.2252.0[49]AgricultureTomato waste nanoporous carbon (TWNC)64.5220-3508402.0[50]BiomassPACK497.5150-5006.9450.8This workSynthetic


## 4. Conclusions

Here, the adsorption efficiency of PACK for the removal of CV from aqueous solutions was investigated. Batch adsorption processes were performed to investigate the effects of contact time (0–120 min, and up to 24 h), initial CV concentration (50–500 mg/L), and temperature (25–45°C). The adsorption kinetics, evaluated using PFO, PSO, and IPD models, revealed that the PSO model provided a better fit (R2≥0.9996). Also, the result indicates an adsorption rate-limiting step dominantly controlled by film diffusion. The equilibrium data, fitted to Langmuir, Freundlich, Temkin, and D-R isotherms, were found to be best expressed by the Langmuir model with a maximum monolayer capacity, qm, of 497.51 mg/g. The thermodynamic studies indicated a spontaneous and endothermic adsorption system in which the spontaneity slightly increases with temperature and decreases with initial CV concentration. The values of ΔG° and ΔH° are clearly positioned in the range indicating a physisorption mechanism, i.e., 0>ΔG°≥−20kJ/mol and ΔH°<40kJ/mol. Overall, these results show that the PACK is a promising adsorbent for the removal of CV and potentially other cationic dyes, from industrial effluent.



---