# Effect of NH3 Alkalization and MgO Promotion on the Performance of Ni/SBA-15 Catalyst in Combined Steam and Carbon Dioxide Reforming of Methane

Authors: Phan H. Phuong; Luu C. Loc; Nguyen Tri; Nguyen P. Anh; Ha C. Anh
Journal: Journal of Nanomaterials
 (2021)

---

## Abstract

In this work, 31.4 wt.% Ni/SBA-15 (Ni/SBA-15) nonpromoted and alkalized with ammonia solution and by MgO promoter catalysts were prepared and used for combined steam and CO2 reforming of CH4 (bireforming). Effect of concentration of ammonia solution (NH3(aq)) (10–25 vol.%) and Mg content (3–12 wt.%) on the properties of the Ni/SBA-15 catalysts was investigated by low-angle and powder X-ray diffraction (XRD), N2-BET isothermal adsorption, SEM, TEM, EDS mapping, H2-TPR, and CO2-TPD methods. The performance of the catalysts in bireforming was assessed in the temperature range of 550–800°C. The enhancement of dispersion of NiO particles, reducibility, and basicity of alkalized Ni/SBA-15 catalysts were responsible for improving the catalytic performance of this catalyst. The results revealed that the Ni/SBA-15 treated with 15-25% NH3(aq) solution and promoted with 3-9% Mg exhibited high activity for CH4 conversion. Meanwhile, Ni6Mg/SBA-15 showed the highest CO2 conversion. Among tested catalysts, Ni/SBA-15-20NH3 and Ni9Mg/SBA-15 samples had an almost equal activity with a CH4 conversion of nearly 97% and a CO2 conversion of about 84% at 700°C thanks to its moderate affinity with both CO2 and CH4. However, the H2/CO ratio of the product mixture remained at 2.02 on the Ni/SBA-15-20NH3 catalyst and almost 1 on the Ni9Mg/SBA-15 sample. These results might be related to the fact that the alkalization of the Ni/SBA-15 catalyst by NH3(aq) solution had an advantage over using MgO because side reactions were unlikely to occur.


---

## Body

## 1. Introduction

The rapid increase in emissions of major greenhouse gases such as CO2 and CH4 in the last decade has seriously affected climate change and the living environment in the world. Besides, syngas, the variable mixture of carbon monoxide and hydrogen, is an important intermediate for downstream processes in the chemical industry. Including many benefits for producing syngas from available natural gas reservoirs, along with the consumption of two main greenhouse gases, bireforming of CH4 using CO2 and H2O (reaction (1)) is the most suitable method with extensive application in the chemical industry [1]:
(1)3CH4+CO2+2H2O⟶4CO+8H2,ΔH298=+220kJ/molThe bireforming process (BRM) (reaction (1)) consists of two reactions: dry reforming (DRM) (reaction (2)) and steam reforming (SRM) (reaction (3)):(2)CH4+CO2⇌2CO+2H2,ΔH298=+247.3kJ/mol(3)CH4+H2O⇌CO+3H2,ΔH298=+206.3kJ/molAs can be seen from reactions (1) and (2), the enthalpy at 298 K of DRM is +247.3 kJ/mol, 1.122 times higher than BRM. This means that, as an endothermic reaction, the combined CO2 and steam reforming of methane (Equation (1)) consumes less energy than DRM (Equation (2)). Furthermore, this combination shows the most desirable stoichiometry of H2 and CO, completely suitable for the Fischer-Tropsch synthesis process. By feeding CO2 and steam simultaneously, the products’ ratio can be controlled by adjusting the CH4/CO2/H2O ratio of the feedstock [2]. Moreover, one of the disadvantages of steam reforming methane is the generation of large amounts of CO2 in the side reaction
(4)CO+H2O⇌CO2+H2,ΔH298Ko=‐41kJ/molIn a bireforming reaction, this problem was overcome. In addition, adding H2O to the dry reforming reaction (2), to create a bireforming reaction (1), has limited coke deposition—the biggest disadvantage of CO2 reforming of methane, thanks to reaction (5) [3]:
(5)C+H2O⇌CO+H2,ΔH298Ko=+131.3kJ/molFor these reasons, presently, bireforming is receiving great attention for converting natural gas into synthetic gas.Metals in the VIII B group, especially Ni, Ru, Rh, Pd, Ir, and Pt, have been reported to be highly active in CH4 reforming processes. Despite higher activity and stability, the usage of noble metals is not preferred due to their high cost and less availability. Among other transition metals, Ni possesses high reactivity towards conversion of hydrocarbons [4], photocatalytic water splitting [5], and the hydrogen and the oxygen evolution reaction [6]. In general, supported Ni catalysts are commercially used in steam reforming of CH4 because of the cheap price and good performance compared to the ones with noble metals [7, 8]. However, coke formation and metal sintering have been making this process inapplicable commercially until recently. Hence, metal dispersing and coke resistance improvement of Ni-based catalyst has been attracting attention.In our previous study [9], nanosized NiO/SBA-15 catalysts with NiO crystallite size in the range of 12.9 to 18.3 nm were successfully prepared. In this catalytic system, there are 5–6 nm NiO particles dispersed inside the pores and the NiO particles of 20–50 nm distributed on the surface of SBA-15 when Ni content was 23.5–39.2 wt.%. Dispersion of metallic sites into the pores could prevent Ni from sintering and metal loss during reaction. The high dispersion of NiO in the Ni/SBA-15 catalyst is caused by the unique properties of SBA-15 such as uniform pores with large diameters (5.3–6.0 nm), high porosity, and high specific surface area (613 m2/g). The reduced catalysts have high activity in bireforming reaction, reaching 86% CH4 and 77% CO2 converted at 700°C or 90.5% and 80%, respectively, at 800°C. The catalysts work stably for hundreds of hours due to the presence of weak and strong Lewis basic sites which limit coke formation and increase CO2 adsorption. Similarly, Zhang et al. [10] reported that 12.5% NiO/SBA-15 catalyst had CH4 and CO2 conversion at 800°C of 89% and 85%, respectively, and could remain its activity over 600 hours time-on-stream (TOS) in CO2 methane reforming. As a result, SBA-15 is believed to be potential support for nickel catalyst in the methane bireforming process.Deactivation of Ni/SBA-15 catalyst in dry reforming of CH4 has been addressed to coke deposition rather than sintering of Ni particles [10]. One of the most important factors affecting coke deposition during the reaction is the basicity of catalysts [11]. Coke formation could be reduced or even inhibited when the active metal is dispersed on the metal oxide support with Lewis basic sites. Many studies show that the addition of alkali and alkaline earth metals could change the nature of supports, leading to a reduction of coke formation and an increase of CO2 adsorption [12]. For example, adding a basic Lewis promoter such as alkali metal oxides (Na2O, K2O), alkaline earth (CaO, MgO), or weak base (NH4OH) reduces coke deposition and metal sintering of Ni/Al2O3, Ni/SiO2, and NiO/SBA-15 catalysts [12–14].Danilova et al. [15] suggested that the structural similarity of NiO and MgO led to the formation of a solid solution in the form of a thin layer, surrounding the Ni particles that increased catalyst stability and reduced carbon deposition. Wang et al. [16] demonstrated that in the MgO-modified Ni/SBA-15 catalyst synthesized by the coimpregnation method, the MgO particles covered the walls of channels of SBA-15. Besides, the catalyst basicity increased and the Ni dispersion was improved, leading to an enhancement in chemical adsorption of CO2. As a result, the activity and the coke resistance of the catalyst in the dry reforming reaction were improved. In addition, Alipour et al. [17] reported that adding MgO to the nickel catalyst promoted the catalyst reducibility that enhanced CH4 conversion and coke resistance. NiO-MgO bonding was useful in preventing Ni particle sintering; carbon deposits and these facts have been accepted in many studies [15, 18, 19].Recently, another promoter considered to be examined was NH4OH. Previous researches used NH4OH as a pH controller for some processes [20, 21], but NH4OH could also be used as a promoter thanks to its basicity to enhancing some characteristics of the catalyst. This property was believed to reduce the acidic sites which would improve catalyst activity, limit coke formation, and stabilize catalyst. Modification of SBA-15 by attaching the -NH2 group to its structure improved the structural stability and increased content of amino as well as basic sites [22]. Hao et al. [23] indicated that alkalization increased catalytic activity and coke resistance of the supported Co/Al2O3 catalyst.However, to the best of our knowledge, the impact of treatment with aqueous NH3 step in catalyst preparation or promoting catalysts by MgO on the activity of Ni/SBA-15 catalyst in bireforming has not been carried out so far. In our previous investigation [9], it was reported that NiO/SBA-15 catalyst contained 31.4 mass% Ni (Ni/SBA-15), exhibiting higher activity than other Ni/SBA-15 samples. The conversion of CH4 and CO2 on this catalyst in bireforming (BRM) reached 90% and 76%, respectively, at 700°C. In this study, the effect of NH3 alkalization or promotion by MgO on catalytic activity of Ni/SBA-15 catalyst in BRM reaction was investigated and optimized.


## 2. Materials and Methods

SBA-15 was prepared by the method described in the work [9]. To prepare SBA-15 alkalized with ammonia solution (SBA-15-NH3), 2 grams of SBA-15 was put into beakers containing 50 ml NH3(aq) solution with various concentrations, 10%, 15%, 20%, and 25% in volume, respectively. These mixtures were then placed in an autoclave at 160°C for 10 h. After that, they were washed with distilled water and dried at 120°C for 2 h.Then, NiO supported on SBA-15-NH3 catalysts were prepared by impregnating Ni(NO3)2 solution on SBA-15-NH3 according to the procedure described in reported work [9]. The Ni content in the catalysts was fixed at 31.4 wt.% (or 40 wt.%NiO). The obtained samples were calcined in air at 800°C for 0.5 h and symbolized as follows, Ni/SBA-15-aNH3, where a represents concentration of ammonia solution used in preparation of alkalized SBA-15 support. Meanwhile, NiO supporting SBA-15 promoted by MgO catalysts were formed by using coimpregnation of Ni(NO3)2(aq) and Mg(NO3)2(aq) solution on support SBA-15. The amount of Mg(NO3)2(aq) solution used is varied to obtain samples with different Mg contents (3–12 wt.%). After that, the samples were calcined at 800°C for 0.5 h and were denoted as NibMg/SBA-15, where b performs Mg content. All the samples were then reduced in situ in 40 mol% H2/N2 gas mixture (3 L/h) at 800°C for 2 h before reaction.The physicochemical properties of the catalysts were studied by several methods such as XRD (Bruker D2 Phaser powder diffractometer), N2-BET isothermal adsorption (Nova Station B, Quantachrome NovaWin Instrument), scan electron microscopy (FE–SEM JEOL 7401 instrument), transmission electron microscopy (TEM on the TEM JEM 1400 of JEOL USA instrument), EDS mapping on JEOL JST-IT 200 instrument, hydrogen temperature-programmed reduction (H2-TPR), and the carbon dioxide temperature-programmed desorption (CO2-TPD). Both H2-TPR and CO2-TPD were carried out on a microreactor with a sample of 50 mg using a Gas Chromatograph GOW-MAC 69-350 with a thermal conductivity detector (TCD). The activity of catalysts for bireforming was tested in a microflow reactor under atmospheric pressure at a temperature of 550–800°C as described in detail in our previous paper [9]. Briefly, a catalyst sample of 0.2 grams, the feed flow rate of 6 L/h, CH4 concentration in feed of 3 mol.%, and the molar ratio of CH4 : CO2 : H2O in feed of 3 : 1.2 : 2.4 was used in the investigation.


## 3. Results and Discussion

### 3.1. Physicochemical Characteristics of Catalysts

The properties of bare SBA-15 support are showed detailed in our previous paper [9]. Briefly, three intensive main diffraction peaks at 2θ of 0.90°, 1.60°, and 1.84°, indexed as the (100), (110), and (200) reflections, respectively, appearing in the low-angle XRD pattern (Figure 1(a)), prove that two-dimensional, ordered hexagonal mesostructure SBA-15 was successfully prepared [24]. The SEM image (Figure 1(b)) showed that SBA-15 was prepared in a porous cocoon diameter of hundred nm. N2 adsorption-desorption profiles of the synthesized SBA-15 are presented in Figure 1(c). According to the IUPAC classification, the profile of the sample belonged to the IV type isotherm curve with the H1 hysteresis loop in a P/P0 range of 0.45–0.7, which was a characteristic of mesoporous materials. Hysteresis was observed for reasonably large pores (d≥4 nm), and these pores showed capillary condensation and evaporation at values for P/P0>0.45 [25]. The H1 type hysteresis of obtained SBA-15 indicated the well-organized materials, associating with the presence of cylindrical pores. Moreover, the small inclination of hysteresis indicated that the obtained pores were uniform. This result was further confirmed by the TEM image of synthesized SBA-15 reported in our previous paper [26]. The diameter of the channels of SBA-15, determined from the N2 adsorption isotherms (Figure 1(d)) and TEM analysis [26], was approximately 6.08 nm. The specific surface area and pore volume of the synthesized SBA-15, determined from the N2 adsorption isotherm, were 639.1 m2·g-1 and 0.65 cm3·g-1, respectively. Therefore, NiO were easily dispersed into the channel system of SBA-15, as indicated in Figure 2(a’).Figure 1
The narrow-angle XRD pattern (a) [9] and physicochemical properties of synthesized SBA-15 support: SEM image (b), N2 isotherm (c), pore distribution (d), H2-TPR profiles (e), and CO2-TPD pattern (f).
(a)(b)(c)(d)(e)(f)Figure 2
SEM images (a–e) and TEM images (a’–e’) of the catalysts.The reducibility of supports was characterized by the H2-TPR method. It was found from Figure 1(e) that there were no reduction peaks for SBA-15 and NH3-treated SBA-15 supports in the temperature range from 100 up to 900°C. The basicity of supports and catalysts was evaluated via CO2-TPD characterization. It was reported that there were three CO2-TPD peaks observed in the temperature ranges of 100–200, 300–400, and 600–800°C, attributed to weak, moderate, and strong basic sites, respectively [27]. The two CO2-TPD peaks of SBA-15 and SBA-15-NH3 at 100–200°C and 500–700°C were attributed to weak and strong basic sites, respectively. The same result was reported by Zhang et al. [27]. The presence of weak basic sites (100–200°C) and strong basic sites (600–700°C) on SBA-15 was explained as follows. At the heating temperature of 550°C for 2 hours, there still existed H2O and Cl- ions in the structure of SBA-15, which were Lewis bases. The CO2-TPD pattern of the ammonia-treated support, SBA-15-NH3, was similar, including the characteristic peaks for weak and strong basic sites. Heating ammonia in glass tubes at various temperatures, Perman and Atkinson found that decomposition began under the most favourable circumstances at 500°C [28]. Then, on the alkalized support, there existed NH3, which almost did not dissociate to N2 and H2 at drying temperature 120°C for 2 hours, providing additional Lewis basic sites.The wide-angle XRD patterns of the obtained catalysts are indicated in Figure3. The spreading peak located at about 20-25° was accredited to the silica frameworks belonging to SBA-15 support for all catalysts [29]. The XRD patterns of NH3-modified SBA-15 supported NiO (Figure 3(a)), and MgO-promoted NiO/SBA-15 catalysts (Figure 3(b)) showed that all catalysts exhibited diffraction peaks with high intensity at 2θ=37.3°, 43.2°, 62.9°, 76°, and 79.3° corresponding to (101), (200), (220), (311), and (222) plans of a face-center cubic crystalline NiO structure in all catalysts [30]. Moreover, all of the peaks were highly apparent at high intensity. This meant that NiO appeared as a high-crystalline state. Besides, the peaks for the NiO phase in alkalized catalysts were more intense than that of the bare catalyst, Ni/SBA-15. It was proposed that NiO particles were not dispersed homogeneously over the mesopores of SBA-15 for alkalized samples [31]. Based on XRD patterns, the average crystallite size of NiO (dcry) could be calculated through the Scherrer equation [32] at 2θ=43.2°, which is shown in Table 1. As seen, the size of NiO crystals increased from 18.4 nm in nonpromoted catalyst to 18.5-21 nm in the MgO-promoted ones and to 30–40 nm in ammonia-alkalized samples (Table 1). In particular, no characteristic peaks of MgO crystallites were detected in all samples containing 3–12% Mg. This fact suggested a high dispersion of Mg oxides on mesoporous silica or a formation of Ni-Mg-O solid solution [33].Figure 3
XRD patterns of NiO/SBA-15 catalysts alkalized with NH3(aq) (a) and NiO/SBA-15 catalysts promoted by MgO (b).
(a)(b)Table 1
The structural properties of the catalysts.
CatalystsSBETa (m2/g)dporea (nm)Vporea (cm3/g)dcryb (nm)Tmaxc (°C)mNioc (a.u.)mCO2d (a.u.)Ni/SBA-15232.66.080.2918.35369, 450, and 62011Ni/SBA-15-15NH3————3401.81.2Ni/SBA-15-20NH324.892.500.0240.83311.81Ni/SBA-15-25NH327.422.540.0230.03301.91.2Ni3Mg/SBA-15————392, 7880.891Ni6Mg/SBA-1536.52.140.0221.0385, 7600.732Ni9Mg/SBA-1527.51.640.0118.5360, 440, and 5861.074aBET surface (SBET), average pore diameter (dpore), and total pore volume (Vpore) were obtained from N2 adsorption isotherm analysis. bNiO crystal size (dcry) was obtained from XRD patterns at 2θ=43.2°. cThe maximal reduction temperature (Tmax) and the number of reduced NiomNio, based on H2 consumption, were obtained from H2-TPR results. dThe desorbed CO2 amount (mCO2) was obtained from the results of CO2-TPD results of activated samples.On the SEM image of the nonmodified sample Ni/SBA-15 catalyst (Figure2(a)), the SBA-15 cocoon diameter of 200-400 nm and spherical particle size of ten nm sticking on the cocoon surface were found. The highly ordered hexagonal structure of the SBA-15 was clearly observed on the TEM image of this catalyst (Figure 2(a’)). In addition, the nanosized NiO particles in the channels of SBA-15 and some large clusters on the outer surfaces were shown in the TEM image of the Ni/SBA-15 sample (Figure 2(a’)). This meant that the size of inside NiO particles was around 6 nm and of outside NiO bulk was almost ten nm.The cocoon shape of SBA-15 was still observed on SEM images of all alkalized samples (Figures2(b)–2(e)). It could be seen from Figures 2(b) and 2(c) that, for NH3-alkalized Ni/SBA-15 samples, cocoons had smaller size and are less porous than nonmodified Ni/SBA-15 and some particles had been broken down. The SEM image of the MgO-promoted samples (Figures 2(d) and 2(e)) was characterized by many bright spherical particles with size of 10-50 nm appearing on the surface of SBA-15 cocoons. In addition, the ordered mesostructure was still observed on the TEM images (Figures 2(d’) and 2(e’)) of these samples. On the TEM image of the MgO-promoted samples, besides the dark particles being similar to those of the Ni/SBA-15 sample (Figure 2(a’)), the light-colored particles were also observed. Both types of particles appeared both in the structural channel and on the outer surface of SBA-15 support. This proved the existence of particles with different compositions on the NiMg/SBA-15 catalyst. Specifically, dark-colored particles could be assigned to NiO while light-colored particles were responsible for the MgO or the NiO-MgO mixture. Meanwhile, as depicted in Figures 2(b’) and 2(c’), the ordered mesoporous structure was not observed on TEM images of NH3-alkalized Ni/SBA-15 samples. This was possibly due to the damage of thin pore walls of SBA-15 support in ammonia solution. On the TEM image of the NH3-modified samples (Figures 2(b’) and 2(c’)), the light-colored particles, assigned to NiO particles distributed in the porous structure of the material and the dark color thin layer, which might be derived from NH3, could be seen.EDS mapping of catalysts (Figure4) indicated an evenly and highly dispersed form of all species on all catalysts. The elemental composition indicated in the EDS mapping to some extent was matched with the loading value, proving that the method of catalysts’ preparation was suitable. On the Ni/SBA-15 catalyst, the elemental content of Si (28.4%) was approximate to the loading value (28.0%) while the oxygen content was slightly higher (46.8% vs. 40%) and of Ni was slightly lower (24.8 vs. 31.4%). This might be related to the formation of some large clusters on the outer surfaces of the catalyst, as seen in the TEM image, reducing the Ni content. Meanwhile, the Ni content of the two alkalinized catalysts was higher than the calculated value, demonstrating the positive effect of the alkalization on Ni dispersion. The highest Ni content was achieved on the MgO-modified catalyst (Ni6Mg/SBA-15), reaching 40.6% (compared to 31.4% calculated value). This fact showed that Mg was a highly effective additive for improving Ni dispersion. In this sample, the Mg content was approximate to the expected value (5.3% vs. 6.0%) although MgO was not detected on the XRD pattern (Figure 3(b)). This fact proved that highly dispersed MgO was successfully introduced into SBA-15. Meanwhile, the content of Si and O in this sample was lower than the calculated values, respectively, 20.1 vs. 26.7% and 34.0% vs. 39.3%. This might be related to the highest density of active metal particles on the SBA-15 surface as found on the TEM image of sample Ni6Mg/SBA-15 (Figure 2(d)). On the NH3(aq)-treated catalyst (Ni/SBA-15-20NH3), the elemental composition of the EDS mapping was the most matched with the calculated values. Specifically, the components of Si, O, and Ni are 25.1% vs. 28%, 39.9% vs. 40.6%, and 32.3% vs. 31.4%, respectively. In particular, the content of N in this sample was determined to be 2.7%, proving that N was included in the Ni/SBA-15 catalyst. This was explained as follows. Although NH3 was almost completely dissociated to N2 and H2 at 650°C on supported nickel catalysts [34], a small residual of ammonia was found even at 700°C and 800°C in calcination [35].Figure 4
EDS mapping of catalysts: Ni/SBA-15 (a), Ni/SBA-15-20NH3 (b), and Ni6Mg/SBA-15 (c).
(a)(b)(c)The alkalization of Ni/SBA-15 with NH3 and with MgO promoter led to a sharp decrease in pore diameter, pore volume, and specific surface area. In particular, the specific surface area value dropped from 232.6 m2/g of Ni/SBA-15 to 25–37 m2/g, the pore diameter decreased from 6 nm to 2 nm, and the pore volume fell from 0.29 to 0.01–0.02 cm3/g (Table 1). A sharp decrease in pore diameter and pore volume might be related to coverage of the channel walls of SBA-15 by MgO particles [16] and attachment of NH3 residual to the structural channel of support as seen on TEM images. Consequently, the specific surface area of the catalysts was drastically reduced. However, the pore diameter of the alkalized catalysts was still being favourable for the diffusion of CH4 and CO2 into the pores, as their kinetic diameter was 0.38 and 0.44 nm, respectively. Besides, as seen from SEM images, Ni6Mg/SBA-15 showed the smallest size. Consequently, this sample had the highest specific surface area among the alkalized catalysts.H2-TPR profiles of the Ni/SBA-15 catalysts modified by NH3(aq) or MgO are depicted in Figure 5. The H2-TPR pattern of the Ni/SBA-15 catalyst showed three reduction peaks. The former strongest peak is at Tmax,1=372°C, assigned to the reduction of free, bulky NiO [36, 37]. The second very weak reduction peak is at Tmax,2=450°C, representing the reduction of the weak interacted NiO-support species, and the third one is at Tmax,3=620°C, being attributed to the reduction of some forms of Ni2+ ions strongly interacting with support [27] and/or reduction of small clusters of Ni2+ in pores [38]. Compared to the Ni/SBA-15 catalyst, the NH3-modified samples presented the shifting of the first reduction peak towards lower temperature, Tmax,1=330‐355°C, while the other two reduction peaks almost disappeared. This was consistent with the fact that only one type of active phase particle was observed on the TEM image (Figures 2(b’) and 2(c’)). Besides, the higher the concentration of NH3 solution, the more shift of reduction peaks towards the lower temperature was observed. Moreover, the area of the lower temperature reduction peak increased about doubles when nonmodified and modified catalysts were compared. That means the alkalization of SBA-15 with NH3(aq) solution led to an enhancement of reducibility of the Ni/SBA-15 catalyst, whereby the catalytic activity should be improved.Figure 5
H2-TPR profiles of NiO/SBA-15 catalysts alkalized with NH3(aq) (a) and NiO/SBA-15 catalysts promoted by MgO (b).
(a)(b)The characteristics of the H2-TPR pattern of NiMg/SBA-15 catalysts (Figure 5(b)) were dependent on the MgO loading content. When the low-Mg content (3–6%) was added, the H2-TPR profiles of NiMg/SBA-15 catalysts showed two reduction peaks. The shifting of the first reduction peak towards higher temperature (Tmax,1=392 and 385°C) compared to the Ni/SBA-15 sample demonstrated an enhancement on the metal-support interactions [39]. The second peak in the H2-TPR profile, at 760–788°C, was attributed to the reduction of some forms of Ni2+ ions deeply located in the MgO lattice which exhibited a strong interaction [27]. The area ratio of the second reduction peak to the first reduction peak rose with the increase of MgO loading content. This indicated that the more MgO added to the catalyst, the more the number of interacted NiO-MgO species formed. Meanwhile, the H2-TPR pattern of the Ni9Mg/SBA-15 sample consists of three reduction peaks centered at 360, 440, and 586°C. There was no reduction peak above 700°C while a reduction peak at around 600°C appeared on the TPR profile of the Ni9Mg/SBA-15 catalyst. This new reduction peak could be assigned to the strong interaction of NiO with bare MgO [13], which formed when the loading MgO was in excess. The catalysts alkalized with NH3 solution showed a higher number of reduced Nio as compared to the catalysts modified by the MgO additive. This might be related to the fact that the catalysts alkalized with NH3 solution had a homogeneous dispersion of the elements throughout the catalyst since the elemental composition from EDS data was well matched with the calculated value.The profiles of CO2-TPD of modified Ni/SBA-15 catalysts are illustrated in Figure 6. Compared with the support (Figure 1(f)), the intensity of the CO2 desorption peak (Figure 5), corresponding to strong basic sites, was much lower. This could be explained by the high calcination temperature of the catalyst (800°C) while the heating temperature of the SBA-15 support was 550°C and the drying temperature of the NH3-treated SBA-15 was 120°C. The intense dehydration and Cl- ion evaporation at the calcination temperature of 800°C resulted in a decrease in the number of Lewis basic sites in the Ni/SBA-15 and NiMg/SBA-15 catalysts. As previously reported, NH3 was almost completely dissociated from hydrogen and nitrogen at 700°C [35] or 1100°C [40]. Furthermore, the dissociation of NH3 to N2 and H2 was strongly promoted by the Ni catalyst. For example, on the Ni/TiO2 catalyst, 30% NH3 was dissociated at 550°C, and almost 100% NH3 was decomposed at 650°C [34]. These processes led to lowering the basicity of the NH3-treated catalyst as compared to the corresponding support.Figure 6
CO2-TPD pattern of NiO/SBA-15 catalysts alkalized with NH3(aq) (a) and NiO/SBA-15 catalysts promoted by MgO (b).
(a)(b)There were two CO2 desorption peaks in the temperature range of 100–350°C and 400–700°C in all Ni/SBA-15 catalysts. The first peak could be assigned to weak and moderate basic sites while the second one was addressed to strong basic sites. It could be seen that, unlike the support, the majority of basic sites in these catalysts were weak and moderate. Treating NiO/SBA-15 catalysts with NH3(aq) as well as promoting with MgO favoured the presence of weak and moderate basic sites. It followed from Table 1 that the alkalization led to an increase in basic site density. The basicity of the NH3(aq)-treated samples on the one hand does not change much when the concentration of NH3(aq) solution changes on the other hand; it is lower than that of the NiMg/SBA-15 catalyst. This may be related to the fact that most of ammonia was dissociated into hydrogen and nitrogen at calcination temperature, and there remained only a small amount of NH3 residue in the catalysts, as seen in EDS mapping data.


### 3.2. Catalytic Performance for Bireforming

Figures7(a) and 7(b) show the activity of Ni/SBA-15 catalysts treated with different NH3(aq) solutions in CH4 bireforming. It could be seen that both CH4 and CO2 conversion increased when raising the reaction temperature. This was evident because bireforming (1) is a strongly endothermic reaction. In general, catalysts showed higher CH4 conversion than CO2 conversion. It may be related to the occurrence of the Water Gas Shift (WGS) reaction (4) in methane reforming conditions, producing additional CO2 [41].Figure 7
The conversion of CH4 (a) and CO2 (b) of NiO/SBA-15 catalysts treated with NH3(aq) at different reaction temperatures.
(a)(b)As it was followed from Figures7 and 8, conversion of CH4 on modified Ni/SBA-15 catalysts was higher than that on the nonpromoted one over the range of reaction temperature. This might be related to the alkalization of SBA-15 resulting in an increase in NiO dispersion, reducibility, and density of basic sites, as seen in Table 1. Besides, it has been found that the CH4 conversion of NH3-modified catalysts was higher than that of the MgO-modified samples. This result could be explained by the higher number of reduced Ni0mNio in the NH3-modified catalysts when two groups of modified catalysts were compared. From the data in Figure 8, it could be seen that by increasing the content of MgO additive from 0 to 9%, the CH4 conversion increased, reaching the maximum value of 96.4% at the content of 9% Mg. However, when Mg content was continually raised to 12%, the conversion of CH4 slightly decreased.Figure 8
The conversion of CH4 (a) and CO2 (b) of NiO/SBA-15 catalysts promoted by MgO at different reaction temperatures.
(a)(b)The magnitude order of the amount of reduced Ni0, based on H2-TPR (Table 1), was in the following order:
(6)Ni/SBA‐15‐25NH3>Ni/SBA‐15‐20NH3≈Ni/SBA‐15‐15NH3>Ni9Mg/SBA‐15>Ni/SBA‐15>Ni3Mg/SBA‐15>Ni6Mg/SBA‐15From order (6), it could be seen that four catalysts with the highest number of reduced Ni0 (Ni/SBA-15-25 NH3, Ni/SBA-15-20 NH3, Ni/SBA-15-15 NH3, and Ni9Mg/SBA-15) were also the samples with the highest CH4 conversion (Figure 9). The catalysts treated with 15-25% NH3 had approximately the same and highest value of CH4 conversion among the catalysts, reaching 98-99% at 700°C because the number of reduced Nio of these three catalysts is approximate and the highest. Similarly, in the MgO-promoted catalyst group, the highest CH4 conversion of the Ni9Mg/SBA-15 sample was due to its highest reducibility. This implied that CH4 was activated by reduced Nio sites, having the higher reducibility catalyst; the higher activity in CH4 oxidation is reached.Figure 9
The conversion of CH4 and CO2 and the mole ratio H2/CO at reaction temperatures of 700°C over the catalysts.From the obtained results in Table1, it is possible to order the catalysts based on their basicity as follows:
(7)Ni9Mg/SBA‐15>Ni6Mg/SBA‐15>Ni/SBA‐15‐25NH3>Ni/SBA‐15‐15NH3≈Ni/SBA‐15‐20NH3≈Ni3Mg/SBA‐15≈Ni/SBA‐15Among the samples, 9% Mg-promoted catalyst showed the highest density of basic sites, and ranked second is the catalyst with 6% Mg, based on the peak area of the TPD pattern. These samples are also the two catalysts with the highest activity in CO2 conversion. The enhanced basicity was advantageous as CO2 adsorption affinity could be improved, which in turn affected the CO2 conversion and stability [42]. However, the dependence of CO2 conversion on alkalized catalysts with different NH3(aq) solutions was complex (Figure 7(b)). Specifically, CO2 conversion on the two catalysts alkalized with 15% and 20% NH3(aq) solution was higher than that on the nonalkalized one. In contrast, the catalysts were alkalized with the most dilute (10%) or most concentrated (25%) NH3(aq) solution, exhibiting a lower CO2 conversion compared to the nonalkalized one. In addition, it should be noted that the catalysts alkalized with 10% and 25% NH3(aq) solution possessed the highest CH4 conversion and the lowest CO2 conversion (Figure 7). However, at 700°C and higher, CH4 conversion was almost the same on the three NH3-promoted catalysts, reaching over 98%.It could be observed from Figure9 that, in most cases, the H2/CO molar ratio of the product mixture was higher than the theoretical value (which was 2) because of the WGS reaction (4), consuming CO and generating an additional amount of H2. It was worth noting that when the NH3(aq) concentration or the MgO loading content increased, the H2/CO ratio decreased and might become less than 2. In addition to the main reaction (1), several side reactions might be involved in the process. The contribution of side reactions in the composition of reaction products was dependent on feed composition and conversion [43] as well as the using catalyst. Some side reactions such as Reverse Water Gas Shift (RWGS) and methane dry reforming (2) reduced the H2/CO ratio. Alkalization of Ni/SBA-15 catalyst could be able to increase the CO2 adsorption that would lead to an enhancement of these reactions.In particular, the Ni/SBA-15-25NH3 sample has a very low CO2 conversion although it also has high basicity. The highest CH4 conversion and the lowest CO2 conversion obtained on this sample might be related to its highest reducibility, promoting the CH4 reforming by steam according to Equation (6), with the result of CO2 additional generation:
(8)CH4+2H2O⇌CO2+4H2,ΔH298=+690kJ/molFurther, although possessing higher basicity than Ni6Mg/SBA-15, the Ni9Mg/SBA-15 sample exhibits a slightly lower CO2 conversion. Additionally, two samples with the highest basicity of the two alkalized catalyst groups (Ni/SBA-15-25NH3 and Ni9Mg/SBA-15) also expressed the lowest value of mol ratio H2/CO among the studied catalysts. This is explained as follows. When the samples are treated with a too high loading alkalizing agent, they possess high base properties that enhanced CO2 adsorption, promoting dry reforming (2), generating more CO. CO in turn activates the WGS reaction (4), which in result reduces the H2/CO ratio on the one hand and on the other hand reduces CO2 conversion. The value of the H2/CO ratio and the CO2 conversion depends on the catalyst properties. On the Ni/SBA-15-25NH3 sample, the WGS reaction (4) was stronger, so the CO2 conversion was lower, and the H2:COratio>1. Conversely, on the Ni9Mg/SBA-15 catalyst, the dry reforming (2) is relatively stronger than WGS reaction (4), so the CO2 conversion remains quite high, while the ratio H2/CO~1. In general, excessive alkalization can also lead to disadvantages for the catalysts. Besides, the previous report [44] indicated that excessive basicity of the catalyst itself is detrimental to catalytic activity as it will stimulate a higher extent of the CO2 dissociation (CO2→C+O2) and thereupon deactivate the catalyst.Hence, in order to obtain the highest yield of synthetic gas, it was necessary to select a catalyst with optimal adsorption capacity for these two reactants. Comparison of the two highly active catalysts, Ni/SBA-15-20NH3 and Ni9Mg/SBA-15, showed that they had an equally high activity with a CH4 conversion of nearly 97% and a CO2 conversion of almost 84% at 700°C. However, the H2/CO ratio obtained remained at 2.02 on the Ni/SBA-15-20NH3 catalyst and almost 1 on the Ni9Mg/SBA-15 sample. These facts proved that the alkalization of the Ni/SBA-15 catalyst by NH3(aq) solution had an advantage over using MgO because side reactions were unlikely to occur.As shown in Table2, there are three main groups of Ni-based catalysts for the BRM reaction based on three supports including Al2O3 [14, 49–52, 56], CeO2 [45, 50, 51], and SBA-15 [9, 42, 52]. In general, the highest value of CH4 conversion reached on all three groups is approximately the same, ranging from 86 to 92% at 700°C. Meanwhile, the CO2 conversion under the same reaction conditions is lower (64-77%). In particular, two groups of Ni catalysts supported on Al2O3 and CeO2 show low CO2 conversion and do not exceed 67% at 700°C [46, 50], while this value reached 77% on the Ni/SBA-15 catalyst [9]. Furthermore, the promotion of the Ni/Al2O3 catalyst by alkali metal additives [13, 47–49] or CeO2 [48, 49] or Zr [48] did not significantly improve the activity, and the CO2 conversion did not exceed 78% at 700°C [47]. Meanwhile, for the Ni/CeO2 catalyst, vanadium additive shows its promoting role, since the conversion of CH4 and CO2 at 700°C was raised from 89% to 96% and from 67% to 75%, respectively [51], as 0.3%V was added to the Ni/CeO2 catalyst. The special feature of the Ni/SBA-15 [9] compared with Ni/Al2O3 [46] and Ni/CeO2 [50] catalysts is that it has high conversion of both CH4 and CO2. These values reach 86% and 77% at 700°C, respectively [9]. In comparison with other Ni-based catalysts, Ni/SBA-15-20NH3 and Ni9Mg/SBA-15 catalysts in this study showed outstanding activity in bireforming of CH4. Typically, CH4 conversion on these two samples was almost 97% at 700°C, and CO2 conversion was nearly 84%, much higher than this value on others.Table 2
Comparison of the CH4 and CO2 conversion in CSCRM: reaction temperature (T), CH4 conversion (XCH4), and CO2 conversion (XCO2).
CatalystsT (°C)XCH4 (%)XCO2 (%)Refs.5Ni/Al2O390058—[45]5Ni/CeO273—6.67Ni/α-Al2O37009264[46]6.67Ni/(MgO-Al2O3) (1 : 2)80010067[47]6.67Ni/(BaO-Al2O3) (1 : 2)100786.67Ni/(CaO-Al2O3) (1 : 2)10058Ni/MgO–Al2O380093—[13]700837115Ni/MgAl2O48507435[48]15Ni/CeO2–ZrO2/MgAl2O4804115Ni–CeO2–ZrO2/MgAl2O48144Ni–Ce/θ-Al2O38508047[49]Ni/MgAl2O4 (MgO/Al2O3=3/7)8547Ni–Ce/MgAl2O4(3)86587.87Ni/CeO2-NR7008967[50]80096727.87Ni0.3V/CeO2-NR7009675[51]31.4Ni/SBA-157008677[9]80090.58010Ni/SBA-158509885[42]10Ni3MgO/SBA-15928510Ni/Ce-SBA-158007860[52]31.4Ni/SBA-15-20NH37009784This work31.4Ni9Mg/SBA-159685


## 3.1. Physicochemical Characteristics of Catalysts

The properties of bare SBA-15 support are showed detailed in our previous paper [9]. Briefly, three intensive main diffraction peaks at 2θ of 0.90°, 1.60°, and 1.84°, indexed as the (100), (110), and (200) reflections, respectively, appearing in the low-angle XRD pattern (Figure 1(a)), prove that two-dimensional, ordered hexagonal mesostructure SBA-15 was successfully prepared [24]. The SEM image (Figure 1(b)) showed that SBA-15 was prepared in a porous cocoon diameter of hundred nm. N2 adsorption-desorption profiles of the synthesized SBA-15 are presented in Figure 1(c). According to the IUPAC classification, the profile of the sample belonged to the IV type isotherm curve with the H1 hysteresis loop in a P/P0 range of 0.45–0.7, which was a characteristic of mesoporous materials. Hysteresis was observed for reasonably large pores (d≥4 nm), and these pores showed capillary condensation and evaporation at values for P/P0>0.45 [25]. The H1 type hysteresis of obtained SBA-15 indicated the well-organized materials, associating with the presence of cylindrical pores. Moreover, the small inclination of hysteresis indicated that the obtained pores were uniform. This result was further confirmed by the TEM image of synthesized SBA-15 reported in our previous paper [26]. The diameter of the channels of SBA-15, determined from the N2 adsorption isotherms (Figure 1(d)) and TEM analysis [26], was approximately 6.08 nm. The specific surface area and pore volume of the synthesized SBA-15, determined from the N2 adsorption isotherm, were 639.1 m2·g-1 and 0.65 cm3·g-1, respectively. Therefore, NiO were easily dispersed into the channel system of SBA-15, as indicated in Figure 2(a’).Figure 1
The narrow-angle XRD pattern (a) [9] and physicochemical properties of synthesized SBA-15 support: SEM image (b), N2 isotherm (c), pore distribution (d), H2-TPR profiles (e), and CO2-TPD pattern (f).
(a)(b)(c)(d)(e)(f)Figure 2
SEM images (a–e) and TEM images (a’–e’) of the catalysts.The reducibility of supports was characterized by the H2-TPR method. It was found from Figure 1(e) that there were no reduction peaks for SBA-15 and NH3-treated SBA-15 supports in the temperature range from 100 up to 900°C. The basicity of supports and catalysts was evaluated via CO2-TPD characterization. It was reported that there were three CO2-TPD peaks observed in the temperature ranges of 100–200, 300–400, and 600–800°C, attributed to weak, moderate, and strong basic sites, respectively [27]. The two CO2-TPD peaks of SBA-15 and SBA-15-NH3 at 100–200°C and 500–700°C were attributed to weak and strong basic sites, respectively. The same result was reported by Zhang et al. [27]. The presence of weak basic sites (100–200°C) and strong basic sites (600–700°C) on SBA-15 was explained as follows. At the heating temperature of 550°C for 2 hours, there still existed H2O and Cl- ions in the structure of SBA-15, which were Lewis bases. The CO2-TPD pattern of the ammonia-treated support, SBA-15-NH3, was similar, including the characteristic peaks for weak and strong basic sites. Heating ammonia in glass tubes at various temperatures, Perman and Atkinson found that decomposition began under the most favourable circumstances at 500°C [28]. Then, on the alkalized support, there existed NH3, which almost did not dissociate to N2 and H2 at drying temperature 120°C for 2 hours, providing additional Lewis basic sites.The wide-angle XRD patterns of the obtained catalysts are indicated in Figure3. The spreading peak located at about 20-25° was accredited to the silica frameworks belonging to SBA-15 support for all catalysts [29]. The XRD patterns of NH3-modified SBA-15 supported NiO (Figure 3(a)), and MgO-promoted NiO/SBA-15 catalysts (Figure 3(b)) showed that all catalysts exhibited diffraction peaks with high intensity at 2θ=37.3°, 43.2°, 62.9°, 76°, and 79.3° corresponding to (101), (200), (220), (311), and (222) plans of a face-center cubic crystalline NiO structure in all catalysts [30]. Moreover, all of the peaks were highly apparent at high intensity. This meant that NiO appeared as a high-crystalline state. Besides, the peaks for the NiO phase in alkalized catalysts were more intense than that of the bare catalyst, Ni/SBA-15. It was proposed that NiO particles were not dispersed homogeneously over the mesopores of SBA-15 for alkalized samples [31]. Based on XRD patterns, the average crystallite size of NiO (dcry) could be calculated through the Scherrer equation [32] at 2θ=43.2°, which is shown in Table 1. As seen, the size of NiO crystals increased from 18.4 nm in nonpromoted catalyst to 18.5-21 nm in the MgO-promoted ones and to 30–40 nm in ammonia-alkalized samples (Table 1). In particular, no characteristic peaks of MgO crystallites were detected in all samples containing 3–12% Mg. This fact suggested a high dispersion of Mg oxides on mesoporous silica or a formation of Ni-Mg-O solid solution [33].Figure 3
XRD patterns of NiO/SBA-15 catalysts alkalized with NH3(aq) (a) and NiO/SBA-15 catalysts promoted by MgO (b).
(a)(b)Table 1
The structural properties of the catalysts.
CatalystsSBETa (m2/g)dporea (nm)Vporea (cm3/g)dcryb (nm)Tmaxc (°C)mNioc (a.u.)mCO2d (a.u.)Ni/SBA-15232.66.080.2918.35369, 450, and 62011Ni/SBA-15-15NH3————3401.81.2Ni/SBA-15-20NH324.892.500.0240.83311.81Ni/SBA-15-25NH327.422.540.0230.03301.91.2Ni3Mg/SBA-15————392, 7880.891Ni6Mg/SBA-1536.52.140.0221.0385, 7600.732Ni9Mg/SBA-1527.51.640.0118.5360, 440, and 5861.074aBET surface (SBET), average pore diameter (dpore), and total pore volume (Vpore) were obtained from N2 adsorption isotherm analysis. bNiO crystal size (dcry) was obtained from XRD patterns at 2θ=43.2°. cThe maximal reduction temperature (Tmax) and the number of reduced NiomNio, based on H2 consumption, were obtained from H2-TPR results. dThe desorbed CO2 amount (mCO2) was obtained from the results of CO2-TPD results of activated samples.On the SEM image of the nonmodified sample Ni/SBA-15 catalyst (Figure2(a)), the SBA-15 cocoon diameter of 200-400 nm and spherical particle size of ten nm sticking on the cocoon surface were found. The highly ordered hexagonal structure of the SBA-15 was clearly observed on the TEM image of this catalyst (Figure 2(a’)). In addition, the nanosized NiO particles in the channels of SBA-15 and some large clusters on the outer surfaces were shown in the TEM image of the Ni/SBA-15 sample (Figure 2(a’)). This meant that the size of inside NiO particles was around 6 nm and of outside NiO bulk was almost ten nm.The cocoon shape of SBA-15 was still observed on SEM images of all alkalized samples (Figures2(b)–2(e)). It could be seen from Figures 2(b) and 2(c) that, for NH3-alkalized Ni/SBA-15 samples, cocoons had smaller size and are less porous than nonmodified Ni/SBA-15 and some particles had been broken down. The SEM image of the MgO-promoted samples (Figures 2(d) and 2(e)) was characterized by many bright spherical particles with size of 10-50 nm appearing on the surface of SBA-15 cocoons. In addition, the ordered mesostructure was still observed on the TEM images (Figures 2(d’) and 2(e’)) of these samples. On the TEM image of the MgO-promoted samples, besides the dark particles being similar to those of the Ni/SBA-15 sample (Figure 2(a’)), the light-colored particles were also observed. Both types of particles appeared both in the structural channel and on the outer surface of SBA-15 support. This proved the existence of particles with different compositions on the NiMg/SBA-15 catalyst. Specifically, dark-colored particles could be assigned to NiO while light-colored particles were responsible for the MgO or the NiO-MgO mixture. Meanwhile, as depicted in Figures 2(b’) and 2(c’), the ordered mesoporous structure was not observed on TEM images of NH3-alkalized Ni/SBA-15 samples. This was possibly due to the damage of thin pore walls of SBA-15 support in ammonia solution. On the TEM image of the NH3-modified samples (Figures 2(b’) and 2(c’)), the light-colored particles, assigned to NiO particles distributed in the porous structure of the material and the dark color thin layer, which might be derived from NH3, could be seen.EDS mapping of catalysts (Figure4) indicated an evenly and highly dispersed form of all species on all catalysts. The elemental composition indicated in the EDS mapping to some extent was matched with the loading value, proving that the method of catalysts’ preparation was suitable. On the Ni/SBA-15 catalyst, the elemental content of Si (28.4%) was approximate to the loading value (28.0%) while the oxygen content was slightly higher (46.8% vs. 40%) and of Ni was slightly lower (24.8 vs. 31.4%). This might be related to the formation of some large clusters on the outer surfaces of the catalyst, as seen in the TEM image, reducing the Ni content. Meanwhile, the Ni content of the two alkalinized catalysts was higher than the calculated value, demonstrating the positive effect of the alkalization on Ni dispersion. The highest Ni content was achieved on the MgO-modified catalyst (Ni6Mg/SBA-15), reaching 40.6% (compared to 31.4% calculated value). This fact showed that Mg was a highly effective additive for improving Ni dispersion. In this sample, the Mg content was approximate to the expected value (5.3% vs. 6.0%) although MgO was not detected on the XRD pattern (Figure 3(b)). This fact proved that highly dispersed MgO was successfully introduced into SBA-15. Meanwhile, the content of Si and O in this sample was lower than the calculated values, respectively, 20.1 vs. 26.7% and 34.0% vs. 39.3%. This might be related to the highest density of active metal particles on the SBA-15 surface as found on the TEM image of sample Ni6Mg/SBA-15 (Figure 2(d)). On the NH3(aq)-treated catalyst (Ni/SBA-15-20NH3), the elemental composition of the EDS mapping was the most matched with the calculated values. Specifically, the components of Si, O, and Ni are 25.1% vs. 28%, 39.9% vs. 40.6%, and 32.3% vs. 31.4%, respectively. In particular, the content of N in this sample was determined to be 2.7%, proving that N was included in the Ni/SBA-15 catalyst. This was explained as follows. Although NH3 was almost completely dissociated to N2 and H2 at 650°C on supported nickel catalysts [34], a small residual of ammonia was found even at 700°C and 800°C in calcination [35].Figure 4
EDS mapping of catalysts: Ni/SBA-15 (a), Ni/SBA-15-20NH3 (b), and Ni6Mg/SBA-15 (c).
(a)(b)(c)The alkalization of Ni/SBA-15 with NH3 and with MgO promoter led to a sharp decrease in pore diameter, pore volume, and specific surface area. In particular, the specific surface area value dropped from 232.6 m2/g of Ni/SBA-15 to 25–37 m2/g, the pore diameter decreased from 6 nm to 2 nm, and the pore volume fell from 0.29 to 0.01–0.02 cm3/g (Table 1). A sharp decrease in pore diameter and pore volume might be related to coverage of the channel walls of SBA-15 by MgO particles [16] and attachment of NH3 residual to the structural channel of support as seen on TEM images. Consequently, the specific surface area of the catalysts was drastically reduced. However, the pore diameter of the alkalized catalysts was still being favourable for the diffusion of CH4 and CO2 into the pores, as their kinetic diameter was 0.38 and 0.44 nm, respectively. Besides, as seen from SEM images, Ni6Mg/SBA-15 showed the smallest size. Consequently, this sample had the highest specific surface area among the alkalized catalysts.H2-TPR profiles of the Ni/SBA-15 catalysts modified by NH3(aq) or MgO are depicted in Figure 5. The H2-TPR pattern of the Ni/SBA-15 catalyst showed three reduction peaks. The former strongest peak is at Tmax,1=372°C, assigned to the reduction of free, bulky NiO [36, 37]. The second very weak reduction peak is at Tmax,2=450°C, representing the reduction of the weak interacted NiO-support species, and the third one is at Tmax,3=620°C, being attributed to the reduction of some forms of Ni2+ ions strongly interacting with support [27] and/or reduction of small clusters of Ni2+ in pores [38]. Compared to the Ni/SBA-15 catalyst, the NH3-modified samples presented the shifting of the first reduction peak towards lower temperature, Tmax,1=330‐355°C, while the other two reduction peaks almost disappeared. This was consistent with the fact that only one type of active phase particle was observed on the TEM image (Figures 2(b’) and 2(c’)). Besides, the higher the concentration of NH3 solution, the more shift of reduction peaks towards the lower temperature was observed. Moreover, the area of the lower temperature reduction peak increased about doubles when nonmodified and modified catalysts were compared. That means the alkalization of SBA-15 with NH3(aq) solution led to an enhancement of reducibility of the Ni/SBA-15 catalyst, whereby the catalytic activity should be improved.Figure 5
H2-TPR profiles of NiO/SBA-15 catalysts alkalized with NH3(aq) (a) and NiO/SBA-15 catalysts promoted by MgO (b).
(a)(b)The characteristics of the H2-TPR pattern of NiMg/SBA-15 catalysts (Figure 5(b)) were dependent on the MgO loading content. When the low-Mg content (3–6%) was added, the H2-TPR profiles of NiMg/SBA-15 catalysts showed two reduction peaks. The shifting of the first reduction peak towards higher temperature (Tmax,1=392 and 385°C) compared to the Ni/SBA-15 sample demonstrated an enhancement on the metal-support interactions [39]. The second peak in the H2-TPR profile, at 760–788°C, was attributed to the reduction of some forms of Ni2+ ions deeply located in the MgO lattice which exhibited a strong interaction [27]. The area ratio of the second reduction peak to the first reduction peak rose with the increase of MgO loading content. This indicated that the more MgO added to the catalyst, the more the number of interacted NiO-MgO species formed. Meanwhile, the H2-TPR pattern of the Ni9Mg/SBA-15 sample consists of three reduction peaks centered at 360, 440, and 586°C. There was no reduction peak above 700°C while a reduction peak at around 600°C appeared on the TPR profile of the Ni9Mg/SBA-15 catalyst. This new reduction peak could be assigned to the strong interaction of NiO with bare MgO [13], which formed when the loading MgO was in excess. The catalysts alkalized with NH3 solution showed a higher number of reduced Nio as compared to the catalysts modified by the MgO additive. This might be related to the fact that the catalysts alkalized with NH3 solution had a homogeneous dispersion of the elements throughout the catalyst since the elemental composition from EDS data was well matched with the calculated value.The profiles of CO2-TPD of modified Ni/SBA-15 catalysts are illustrated in Figure 6. Compared with the support (Figure 1(f)), the intensity of the CO2 desorption peak (Figure 5), corresponding to strong basic sites, was much lower. This could be explained by the high calcination temperature of the catalyst (800°C) while the heating temperature of the SBA-15 support was 550°C and the drying temperature of the NH3-treated SBA-15 was 120°C. The intense dehydration and Cl- ion evaporation at the calcination temperature of 800°C resulted in a decrease in the number of Lewis basic sites in the Ni/SBA-15 and NiMg/SBA-15 catalysts. As previously reported, NH3 was almost completely dissociated from hydrogen and nitrogen at 700°C [35] or 1100°C [40]. Furthermore, the dissociation of NH3 to N2 and H2 was strongly promoted by the Ni catalyst. For example, on the Ni/TiO2 catalyst, 30% NH3 was dissociated at 550°C, and almost 100% NH3 was decomposed at 650°C [34]. These processes led to lowering the basicity of the NH3-treated catalyst as compared to the corresponding support.Figure 6
CO2-TPD pattern of NiO/SBA-15 catalysts alkalized with NH3(aq) (a) and NiO/SBA-15 catalysts promoted by MgO (b).
(a)(b)There were two CO2 desorption peaks in the temperature range of 100–350°C and 400–700°C in all Ni/SBA-15 catalysts. The first peak could be assigned to weak and moderate basic sites while the second one was addressed to strong basic sites. It could be seen that, unlike the support, the majority of basic sites in these catalysts were weak and moderate. Treating NiO/SBA-15 catalysts with NH3(aq) as well as promoting with MgO favoured the presence of weak and moderate basic sites. It followed from Table 1 that the alkalization led to an increase in basic site density. The basicity of the NH3(aq)-treated samples on the one hand does not change much when the concentration of NH3(aq) solution changes on the other hand; it is lower than that of the NiMg/SBA-15 catalyst. This may be related to the fact that most of ammonia was dissociated into hydrogen and nitrogen at calcination temperature, and there remained only a small amount of NH3 residue in the catalysts, as seen in EDS mapping data.


## 3.2. Catalytic Performance for Bireforming

Figures7(a) and 7(b) show the activity of Ni/SBA-15 catalysts treated with different NH3(aq) solutions in CH4 bireforming. It could be seen that both CH4 and CO2 conversion increased when raising the reaction temperature. This was evident because bireforming (1) is a strongly endothermic reaction. In general, catalysts showed higher CH4 conversion than CO2 conversion. It may be related to the occurrence of the Water Gas Shift (WGS) reaction (4) in methane reforming conditions, producing additional CO2 [41].Figure 7
The conversion of CH4 (a) and CO2 (b) of NiO/SBA-15 catalysts treated with NH3(aq) at different reaction temperatures.
(a)(b)As it was followed from Figures7 and 8, conversion of CH4 on modified Ni/SBA-15 catalysts was higher than that on the nonpromoted one over the range of reaction temperature. This might be related to the alkalization of SBA-15 resulting in an increase in NiO dispersion, reducibility, and density of basic sites, as seen in Table 1. Besides, it has been found that the CH4 conversion of NH3-modified catalysts was higher than that of the MgO-modified samples. This result could be explained by the higher number of reduced Ni0mNio in the NH3-modified catalysts when two groups of modified catalysts were compared. From the data in Figure 8, it could be seen that by increasing the content of MgO additive from 0 to 9%, the CH4 conversion increased, reaching the maximum value of 96.4% at the content of 9% Mg. However, when Mg content was continually raised to 12%, the conversion of CH4 slightly decreased.Figure 8
The conversion of CH4 (a) and CO2 (b) of NiO/SBA-15 catalysts promoted by MgO at different reaction temperatures.
(a)(b)The magnitude order of the amount of reduced Ni0, based on H2-TPR (Table 1), was in the following order:
(6)Ni/SBA‐15‐25NH3>Ni/SBA‐15‐20NH3≈Ni/SBA‐15‐15NH3>Ni9Mg/SBA‐15>Ni/SBA‐15>Ni3Mg/SBA‐15>Ni6Mg/SBA‐15From order (6), it could be seen that four catalysts with the highest number of reduced Ni0 (Ni/SBA-15-25 NH3, Ni/SBA-15-20 NH3, Ni/SBA-15-15 NH3, and Ni9Mg/SBA-15) were also the samples with the highest CH4 conversion (Figure 9). The catalysts treated with 15-25% NH3 had approximately the same and highest value of CH4 conversion among the catalysts, reaching 98-99% at 700°C because the number of reduced Nio of these three catalysts is approximate and the highest. Similarly, in the MgO-promoted catalyst group, the highest CH4 conversion of the Ni9Mg/SBA-15 sample was due to its highest reducibility. This implied that CH4 was activated by reduced Nio sites, having the higher reducibility catalyst; the higher activity in CH4 oxidation is reached.Figure 9
The conversion of CH4 and CO2 and the mole ratio H2/CO at reaction temperatures of 700°C over the catalysts.From the obtained results in Table1, it is possible to order the catalysts based on their basicity as follows:
(7)Ni9Mg/SBA‐15>Ni6Mg/SBA‐15>Ni/SBA‐15‐25NH3>Ni/SBA‐15‐15NH3≈Ni/SBA‐15‐20NH3≈Ni3Mg/SBA‐15≈Ni/SBA‐15Among the samples, 9% Mg-promoted catalyst showed the highest density of basic sites, and ranked second is the catalyst with 6% Mg, based on the peak area of the TPD pattern. These samples are also the two catalysts with the highest activity in CO2 conversion. The enhanced basicity was advantageous as CO2 adsorption affinity could be improved, which in turn affected the CO2 conversion and stability [42]. However, the dependence of CO2 conversion on alkalized catalysts with different NH3(aq) solutions was complex (Figure 7(b)). Specifically, CO2 conversion on the two catalysts alkalized with 15% and 20% NH3(aq) solution was higher than that on the nonalkalized one. In contrast, the catalysts were alkalized with the most dilute (10%) or most concentrated (25%) NH3(aq) solution, exhibiting a lower CO2 conversion compared to the nonalkalized one. In addition, it should be noted that the catalysts alkalized with 10% and 25% NH3(aq) solution possessed the highest CH4 conversion and the lowest CO2 conversion (Figure 7). However, at 700°C and higher, CH4 conversion was almost the same on the three NH3-promoted catalysts, reaching over 98%.It could be observed from Figure9 that, in most cases, the H2/CO molar ratio of the product mixture was higher than the theoretical value (which was 2) because of the WGS reaction (4), consuming CO and generating an additional amount of H2. It was worth noting that when the NH3(aq) concentration or the MgO loading content increased, the H2/CO ratio decreased and might become less than 2. In addition to the main reaction (1), several side reactions might be involved in the process. The contribution of side reactions in the composition of reaction products was dependent on feed composition and conversion [43] as well as the using catalyst. Some side reactions such as Reverse Water Gas Shift (RWGS) and methane dry reforming (2) reduced the H2/CO ratio. Alkalization of Ni/SBA-15 catalyst could be able to increase the CO2 adsorption that would lead to an enhancement of these reactions.In particular, the Ni/SBA-15-25NH3 sample has a very low CO2 conversion although it also has high basicity. The highest CH4 conversion and the lowest CO2 conversion obtained on this sample might be related to its highest reducibility, promoting the CH4 reforming by steam according to Equation (6), with the result of CO2 additional generation:
(8)CH4+2H2O⇌CO2+4H2,ΔH298=+690kJ/molFurther, although possessing higher basicity than Ni6Mg/SBA-15, the Ni9Mg/SBA-15 sample exhibits a slightly lower CO2 conversion. Additionally, two samples with the highest basicity of the two alkalized catalyst groups (Ni/SBA-15-25NH3 and Ni9Mg/SBA-15) also expressed the lowest value of mol ratio H2/CO among the studied catalysts. This is explained as follows. When the samples are treated with a too high loading alkalizing agent, they possess high base properties that enhanced CO2 adsorption, promoting dry reforming (2), generating more CO. CO in turn activates the WGS reaction (4), which in result reduces the H2/CO ratio on the one hand and on the other hand reduces CO2 conversion. The value of the H2/CO ratio and the CO2 conversion depends on the catalyst properties. On the Ni/SBA-15-25NH3 sample, the WGS reaction (4) was stronger, so the CO2 conversion was lower, and the H2:COratio>1. Conversely, on the Ni9Mg/SBA-15 catalyst, the dry reforming (2) is relatively stronger than WGS reaction (4), so the CO2 conversion remains quite high, while the ratio H2/CO~1. In general, excessive alkalization can also lead to disadvantages for the catalysts. Besides, the previous report [44] indicated that excessive basicity of the catalyst itself is detrimental to catalytic activity as it will stimulate a higher extent of the CO2 dissociation (CO2→C+O2) and thereupon deactivate the catalyst.Hence, in order to obtain the highest yield of synthetic gas, it was necessary to select a catalyst with optimal adsorption capacity for these two reactants. Comparison of the two highly active catalysts, Ni/SBA-15-20NH3 and Ni9Mg/SBA-15, showed that they had an equally high activity with a CH4 conversion of nearly 97% and a CO2 conversion of almost 84% at 700°C. However, the H2/CO ratio obtained remained at 2.02 on the Ni/SBA-15-20NH3 catalyst and almost 1 on the Ni9Mg/SBA-15 sample. These facts proved that the alkalization of the Ni/SBA-15 catalyst by NH3(aq) solution had an advantage over using MgO because side reactions were unlikely to occur.As shown in Table2, there are three main groups of Ni-based catalysts for the BRM reaction based on three supports including Al2O3 [14, 49–52, 56], CeO2 [45, 50, 51], and SBA-15 [9, 42, 52]. In general, the highest value of CH4 conversion reached on all three groups is approximately the same, ranging from 86 to 92% at 700°C. Meanwhile, the CO2 conversion under the same reaction conditions is lower (64-77%). In particular, two groups of Ni catalysts supported on Al2O3 and CeO2 show low CO2 conversion and do not exceed 67% at 700°C [46, 50], while this value reached 77% on the Ni/SBA-15 catalyst [9]. Furthermore, the promotion of the Ni/Al2O3 catalyst by alkali metal additives [13, 47–49] or CeO2 [48, 49] or Zr [48] did not significantly improve the activity, and the CO2 conversion did not exceed 78% at 700°C [47]. Meanwhile, for the Ni/CeO2 catalyst, vanadium additive shows its promoting role, since the conversion of CH4 and CO2 at 700°C was raised from 89% to 96% and from 67% to 75%, respectively [51], as 0.3%V was added to the Ni/CeO2 catalyst. The special feature of the Ni/SBA-15 [9] compared with Ni/Al2O3 [46] and Ni/CeO2 [50] catalysts is that it has high conversion of both CH4 and CO2. These values reach 86% and 77% at 700°C, respectively [9]. In comparison with other Ni-based catalysts, Ni/SBA-15-20NH3 and Ni9Mg/SBA-15 catalysts in this study showed outstanding activity in bireforming of CH4. Typically, CH4 conversion on these two samples was almost 97% at 700°C, and CO2 conversion was nearly 84%, much higher than this value on others.Table 2
Comparison of the CH4 and CO2 conversion in CSCRM: reaction temperature (T), CH4 conversion (XCH4), and CO2 conversion (XCO2).
CatalystsT (°C)XCH4 (%)XCO2 (%)Refs.5Ni/Al2O390058—[45]5Ni/CeO273—6.67Ni/α-Al2O37009264[46]6.67Ni/(MgO-Al2O3) (1 : 2)80010067[47]6.67Ni/(BaO-Al2O3) (1 : 2)100786.67Ni/(CaO-Al2O3) (1 : 2)10058Ni/MgO–Al2O380093—[13]700837115Ni/MgAl2O48507435[48]15Ni/CeO2–ZrO2/MgAl2O4804115Ni–CeO2–ZrO2/MgAl2O48144Ni–Ce/θ-Al2O38508047[49]Ni/MgAl2O4 (MgO/Al2O3=3/7)8547Ni–Ce/MgAl2O4(3)86587.87Ni/CeO2-NR7008967[50]80096727.87Ni0.3V/CeO2-NR7009675[51]31.4Ni/SBA-157008677[9]80090.58010Ni/SBA-158509885[42]10Ni3MgO/SBA-15928510Ni/Ce-SBA-158007860[52]31.4Ni/SBA-15-20NH37009784This work31.4Ni9Mg/SBA-159685


## 4. Conclusion

On the one hand, the alkalization of Ni/SBA-15 by NH3 solution and with MgO promoter led to a sharp decrease in pore diameter, pore volume, and specific surface area, but on the other hand, this modification significantly enhanced the dispersion of NiO particles, reducibility, and basicity of catalysts. As a result, performance of alkalized Ni/SBA-15 catalysts in methane reforming was improved. MgO acted as a highly effective additive for improving the Ni dispersion and enhancing the metal-support parent and the basicity, but it had slight effect on reducibility. Therefore, the Ni/SBA-15 catalyst promoted by MgO exhibited high activity in CO2 conversion. Meanwhile, the NH3 treatment led to a homogeneous dispersion of the elements throughout the catalyst. So, the catalyst reducibility as well as CH4 conversion was improved strongly. However, the excessive alkalization of the catalyst was not favourable in BRM due to strong adsorption of CO2 and stimulation of side reactions that reduced the H2/CO ratio. The results revealed that the Ni/SBA-15 treated with 15-25% NH3(aq) solution and promoted with 3-9% Mg exhibited high activity for CH4 conversion while Ni6Mg/SBA-15 showed the highest CO2 conversion. Among tested catalysts, Ni/SBA-15-20NH3 and Ni9Mg/SBA-15 samples showed better catalytic activity. At 700°C, conversion of CH4 and CO2 reached 97% and 84%, respectively, on these catalysts, which were higher than the values on the others. However, the Ni/SBA-15-20NH3 sample showed an advantage in limiting side reactions since the H2/CO ratio was obtained at a theoretical value.



---