# Synthesis of Metal Oxide Decorated Polycarboxyphenyl Polymer-Grafted Multiwalled Carbon Nanotube Composites by a Chemical Grafting Approach for Supercapacitor Application

Authors: Do-Yeon Kang; Pashupati Pokharel; Yeong-Seok Kim; Sunwoong Choi; Seong-Ho Choi
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

We present grafting of polycarboxyphenyl polymer on the surface of multiwalled carbon nanotube (MWCNT) via a free radical polymerization and subsequent anchoring of the metal oxide nanoparticles for the evaluation of their potential applicability to supercapacitor electrodes. Here, metal oxide nanoparticles, Fe3O4 and Sm2O3, were created after the oxidation of metal precursors Sm(NO3)3 and FeCl2, respectively, and attached on the surface of polycarboxyphenyl-grafted MWCNT (P-CNT) in aqueous medium. This approach shows a potential for enhancing the dispersion of Fe3O4 and Sm2O3 nanoparticles on the wall of P-CNT. The structure and morphological characteristics of the purified MWCNT, P-CNT, and metal oxide-anchored polycarboxyphenyl-grafted MWCNT (MP-CNT) nanocomposites were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). The electrochemical performance of the purified MWCNT electrode, P-CNT electrode, and MP-CNT electrodes was tested by cyclic voltammetry (CV) and galvanostatic charge discharge in a 1.0 M H2SO4 aqueous electrolyte. The results showed that the specific capacitance of the purified MWCNT was 45.3 F/g at the scan rate of 5 mV/s and increased to 54.1 F/g after the modification with polycarboxyphenyl polymer. Further modification of P-CNT with Sm2O3 and Fe3O4 improved the specific capacitance of 65.84 F/g and 173.38 F/g, respectively, at the same scan rate.


---

## Body

## 1. Introduction

With increasing the awareness for pollution control, industry and research centers around the world are searching for the possible alternatives to the development of renewable energy production for the replacement of fossil fuel [1, 2]. In this mission, supercapacitors can be an alternative to fulfill the rising demand of transferable power systems for electronics and automotive applications [3]. The two basic mechanisms for energy storage in supercapacitors are formations of electrical double layer (EDL) capacitance and pseudocapacitance [4]. The first one is a non-Faradic process in which charges are stored electrostatically via reversible ion absorption at the electrode electrolyte interface, while in the second type transformation of Faradic charge takes place at the electrode materials. Furthermore, supercapacitors store the energy in the electric field of the electrochemical double layer (Helmholtz Layer) at the electrode : electrolyte interface [5]. The positive and negative ionic charges within the electrolyte collect at the surface of the solid electrodes and balance for the electronic charge at the electrode surface. The concentration of the electrolyte and the size of the ions determine the thickness of the double layer in the range of 5–10 Å [4].Demand of large supercapacitors with high voltage and improved energy and power density are under discussion for different applications [3]. Because of good thermal and chemical stability, high electrical conductivity, large surface area, porous structures, and long cycling stability of carbon nanomaterials, they are generally used as symmetric electrodes for EDL capacitors [5–7]. Furthermore, the specific surface area and functional groups of carbon nanomaterials impact the electrode performance. The electrode surface area can increase by using porous electrodes with an extremely large internal effective surface [6, 7]. Intercalation of natural graphite and subsequent microwave irradiation can increase the surface area of graphite nanoplatelets [8]. Microwave irradiation of graphite oxide [9, 10] is also an effective way to increase the surface area of graphene sheets and resulting porous material shows high capacitance. Carbon nanomaterials have been also used to improve electrical, thermal, and mechanical properties of polymer nanocomposites [11–15]. Multiwalled CNTs (MWNTs) showed limited specific capacitance, typically ranging from 10 to 100 F/g [4–7]. Certain modification of MWCNT is essential to enhance the specific capacitance and energy density of MWCNT [16, 17]. Conducting polymers (e.g., polypyrrole, polyaniline (PANI), and polythiophene) [18–21] and metal oxides (e.g., RuO2, Fe2O3, Bi2O3, MnO2, and Mn3O4) [22–32] are accepted for pseudocapacitors with relatively high capacitance. During the charge-discharge process in conducting polymers and metal oxide, the generation of positively charged sites on the polymer chains and metal oxides creates structural deterioration with inferior cycling stability which, in turn, lowers the electrical conductivity of electrode [17]. To overcome the abovementioned problems, an appropriate stoichiometric combination of metal oxides or conducting polymers with carbonaceous materials have been used for the development of efficient supercapacitors [18, 21]. Many CNT/metal oxides composites have been reported as the electrochemical electrodes, which showed remarkable capacitance, much higher than those of pure CNT or individual metal oxides due to the prevention of the nanoparticles and CNT agglomeration by the anchored metal oxide nanoparticles on the wall of CNT [25, 28, 29]. Furthermore, the electron transmission across the metal oxides can also be improved by the well conductivity of CNT [25, 28].Generally, an activated carbon electrode shows the rectangular shaped cyclic voltammogram (CV) as an ideal capacitor. RuO2 and IrO2 also have an almost rectangular shaped CV and exhibit good capacitor behavior [24]. However, the shape of the CV is not an outcome of pure double layer charging but of a sequence of redox reactions occurring in the metallic oxide. Zheng and Jow [22] observed a very high specific capacitance of up to 750 F/g for RuO2 prepared at relatively low temperatures. Kim and Park [28] reported the effects of nanosized Fe3O4 on supercapacitive properties of MWCNT. In their study, Fe3O4 nanoparticles were deposited by chemical coprecipitation of Fe2+ and Fe3+ in the presence of MWNTs in alkaline solutions in which a considerably superior specific capacitance of Fe3O4 dispersed MWCNT compared to that of the pure MWNT electrode was observed with retaining 85.1% of its initial capacitance over 1000 cycles. Kotal et al. [18] showed the effects on amidation of carbon nanofiber and, consequently, the grafting of PANI to obtain high capacitance and good cycling stability.The synergistic combination of outstanding conducting properties of carbonaceous materials and high pseudocapacitance of conducting polymers and metal oxide can amalgamate for the development of high-performance supercapacitors. Though supercapacitors of carbon-based materials with conducting polymers are in their growing state [18, 21], there are not any reports that show the electrochemical properties of metal oxide decorated-conjugated polymer-grafted-carbon nanomaterial composites. In this paper, a novel route to produce Fe2O3and Sm2O3 particles-decorated polycarboxyphenyl-grafted MWCNT composite is developed at the first time by the grafting of polycarboxyphenyl group on the wall of MWCNT and subsequent oxidation of metal oxide precursor in an autoclave. Here, grafting of polycarboxyphenyl groups on MWCNT can not only develop long conjugated structure with MWCNT, but also reduce the aggregation of MWCNT. Furthermore, the anchoring of the metal oxide nanoparticles was assisted after grafting the polycarboxyphenyl group on the surface of MWCNT. The polycarboxyphenyl-grafted MWCNT leads to the development of a π-conjugated system and such a type of conducting network may facilitate the effective transfer of the Faradic charge through the MWCNT network. Then, the effect of the covalent functionalization as well as metal oxide decoration was compared for the electrochemical performance of the composites.


## 2. Experimental

### 2.1. Materials

Acetonitrile, azobisisobutyronitrile (AIBN), 4-aminobenzoic acid, sodium nitrite (NaNO2), hydrochloric acid, tetrabutyl ammonium tetrafluoroborate (NBu4BF4), ammonium sulfate, potassium persulfate, samarium nitrate, ferrous chloride, sulfuric acid, and nitric acid were of analytical reagent grade (Sigma-Aldrich) and were used as received. Pristine MWNT (CM-95) was supplied by Hanwha Nanotech Co., Ltd. (Korea). To prepare solutions for the experiments, water was purified in a Milli-Q Plus water purification system (Millipore Co. Ltd., USA).


### 2.2. Synthesis of Polycarboxyphenyl-Grafted MWCNT (P-CNT)

Purified MWCNT was obtained after the treatment of pristine MWCNT with the mixture of concentrated sulfuric acid and nitric acid (1 : 1) and subsequent washing several times with deionized water. 4-Carboxyphenyl diazonium salt was prepared by diazotization as reported in our previous study [33]. Typically, the grafting of polycarboxyphenyl group on the wall of MWCNT was performed by dispersing 0.2 g of purified MWCNT in 40 mL of acetonitrile with continuous stirring for 4 h, and carboxyphenyl diazonium salt (1.0 g) and AIBN (0.15 g) were added at room temperature. The reaction mixture was stirred for 12 h at 60°C. Next, the reaction mixture was vacuum-filtered, washed with deionized water sufficiently, and finally dried in a vacuum oven at 70°C overnight. Here, the grafting of polycarboxyphenyl group on the MWCNT was controlled by adjusting the amount of diazonium salt in the synthesis medium.


### 2.3. Synthesis of Metal Oxide-Anchored Polycarboxyphenyl-Grafted MWCNT (MP-CNT)

Metal oxide nanoparticles were decorated onto the P-CNT in an autoclave using solution process. The P-CNT (0.2 g) was mixed with the metal oxide precursor (2 g), oxidizing agent (2 g), and an excess of deionized water. The oxidizing agents, (NH4)S2O8 and K2S2O8, were used for the oxidation of metal precursors, Sm(NO3)3 and FeCl2, respectively. The oxidation of metal precursors into metal oxides was performed in an autoclave along with P-CNT at 180°C for 5 h, and the resulting reaction mixture was filtered, washed with deionized water, and then dried in a vacuum oven at 70°C for 24 h.


### 2.4. Characterization of Purified MWCNT, P-CNT, and MP-CNT

An X-ray diffractometer (Rigaku, Japan, with Cu KR (λ
=
1.540 Å) radiation) was used to measure the XRD patterns of purified MWCNT, P-CNT, and MP-CNT. Thermogravimetric analysis of purified MWCNT, P-CNT, and MP-CNT was performed using a sinco TGA N-1000 with a heating rate of 10°C/min under a nitrogen atmosphere. The morphological features of the electrode materials were observed with transmission electron microscopy (TEM, JEM-2100F, JEOL) and scanning electron microscopy (SEM, VEGA II SBH, Tescan). The sample for TEM measurement was prepared by ultrasonication of ~0.01 mg/mL of the electrode materials in deionized water followed by dipping the TEM grid on colloidal suspension. Powder sample without dispersion in any solvent was used for SEM observation.


### 2.5. Electrochemical Measurements

A conventional two-electrode configuration was used to study the electrochemical behavior of the prepared electrode materials (purified MWCNT, P-CNT, and MP-CNT) by cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) measurements. Working electrode (cathode) was prepared by mixing 90% MWCNT, P-CNT, and MP-CNT individually with 10% Nafion solution as a binder. A small amount of isopropyl alcohol was added to obtain a more homogeneous dispersion. Then, the slurry was coated onto highly conductive hydrophobic carbon paper followed by a vacuum dry at 70°C for 24 h. The mass of the as-synthesized electrode materials coated on the electrode was about 1 mg. Activated carbon electrode was used as anode and aqueous H2SO4 solution (1 M) was used as the electrolyte. The applied potential range for CV and GCD was kept in the limits from 0.0 to 1.00 V because the decomposition voltage of 1 M aqueous H2SO4electrolyte is ~1.4 V.


## 2.1. Materials

Acetonitrile, azobisisobutyronitrile (AIBN), 4-aminobenzoic acid, sodium nitrite (NaNO2), hydrochloric acid, tetrabutyl ammonium tetrafluoroborate (NBu4BF4), ammonium sulfate, potassium persulfate, samarium nitrate, ferrous chloride, sulfuric acid, and nitric acid were of analytical reagent grade (Sigma-Aldrich) and were used as received. Pristine MWNT (CM-95) was supplied by Hanwha Nanotech Co., Ltd. (Korea). To prepare solutions for the experiments, water was purified in a Milli-Q Plus water purification system (Millipore Co. Ltd., USA).


## 2.2. Synthesis of Polycarboxyphenyl-Grafted MWCNT (P-CNT)

Purified MWCNT was obtained after the treatment of pristine MWCNT with the mixture of concentrated sulfuric acid and nitric acid (1 : 1) and subsequent washing several times with deionized water. 4-Carboxyphenyl diazonium salt was prepared by diazotization as reported in our previous study [33]. Typically, the grafting of polycarboxyphenyl group on the wall of MWCNT was performed by dispersing 0.2 g of purified MWCNT in 40 mL of acetonitrile with continuous stirring for 4 h, and carboxyphenyl diazonium salt (1.0 g) and AIBN (0.15 g) were added at room temperature. The reaction mixture was stirred for 12 h at 60°C. Next, the reaction mixture was vacuum-filtered, washed with deionized water sufficiently, and finally dried in a vacuum oven at 70°C overnight. Here, the grafting of polycarboxyphenyl group on the MWCNT was controlled by adjusting the amount of diazonium salt in the synthesis medium.


## 2.3. Synthesis of Metal Oxide-Anchored Polycarboxyphenyl-Grafted MWCNT (MP-CNT)

Metal oxide nanoparticles were decorated onto the P-CNT in an autoclave using solution process. The P-CNT (0.2 g) was mixed with the metal oxide precursor (2 g), oxidizing agent (2 g), and an excess of deionized water. The oxidizing agents, (NH4)S2O8 and K2S2O8, were used for the oxidation of metal precursors, Sm(NO3)3 and FeCl2, respectively. The oxidation of metal precursors into metal oxides was performed in an autoclave along with P-CNT at 180°C for 5 h, and the resulting reaction mixture was filtered, washed with deionized water, and then dried in a vacuum oven at 70°C for 24 h.


## 2.4. Characterization of Purified MWCNT, P-CNT, and MP-CNT

An X-ray diffractometer (Rigaku, Japan, with Cu KR (λ
=
1.540 Å) radiation) was used to measure the XRD patterns of purified MWCNT, P-CNT, and MP-CNT. Thermogravimetric analysis of purified MWCNT, P-CNT, and MP-CNT was performed using a sinco TGA N-1000 with a heating rate of 10°C/min under a nitrogen atmosphere. The morphological features of the electrode materials were observed with transmission electron microscopy (TEM, JEM-2100F, JEOL) and scanning electron microscopy (SEM, VEGA II SBH, Tescan). The sample for TEM measurement was prepared by ultrasonication of ~0.01 mg/mL of the electrode materials in deionized water followed by dipping the TEM grid on colloidal suspension. Powder sample without dispersion in any solvent was used for SEM observation.


## 2.5. Electrochemical Measurements

A conventional two-electrode configuration was used to study the electrochemical behavior of the prepared electrode materials (purified MWCNT, P-CNT, and MP-CNT) by cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) measurements. Working electrode (cathode) was prepared by mixing 90% MWCNT, P-CNT, and MP-CNT individually with 10% Nafion solution as a binder. A small amount of isopropyl alcohol was added to obtain a more homogeneous dispersion. Then, the slurry was coated onto highly conductive hydrophobic carbon paper followed by a vacuum dry at 70°C for 24 h. The mass of the as-synthesized electrode materials coated on the electrode was about 1 mg. Activated carbon electrode was used as anode and aqueous H2SO4 solution (1 M) was used as the electrolyte. The applied potential range for CV and GCD was kept in the limits from 0.0 to 1.00 V because the decomposition voltage of 1 M aqueous H2SO4electrolyte is ~1.4 V.


## 3. Results and Discussion

Our approach covers the grafting of 4-carboxyphenyl diazonium salt on the wall of purified MWCNT to give carboxyphenyl-grafted MWCNT. The reaction of diazonium salt with the carboxyphenyl-grafted MWCNT and AIBN by free radical polymerization ultimately generated polycarboxyphenyl-grafted MWCNT (P-CNT). The carboxyl group on the diazonium salt also assisted in the polymerization, leading to the development of aπ-conjugated system in P-CNT. Then, the P-CNT was subsequently reacted with the excess of metal precursors separately to produce a complex derivative on its surface, followed by oxidation of the metal precursor in the presence of oxidizing agent to form a MP-CNT composite (Figure 1).Figure 1
Schematic diagrams for the grafting of conjugated polycarboxyphenyl polymer on the wall of MWCNT and subsequent decoration with metal oxide nanoparticles.The morphologies of the surfaces, defects, and surface irregularities of purified MWCNT, P-CNT, and MP-CNT are the most important factors for evaluating the electrochemical properties. In this study, TEM and SEM were used to provide reliable and visual measurements about the surface morphologies of the electrode materials. Figure2 shows the TEM images of the (a) purified MWCNT, (b) P-CNT, (c) P-CNT with Sm(NO3)3, (d) Sm2O3/P-CNT, (e) P-CNT with FeCl2, and (f) Fe2O3/P-CNT. The sp2 hybridization state of carbon in MWCNT was not changed due to the grafting of conjugated polycarboxyphenyl polymer. Obviously, the diameter of P-CNT was observed greater in Figure 2(b) than the purified MWCNT in Figure 2(a) as a proof of the grafting of polycarboxyphenyl polymer. In our previous study, we have already reported the mechanism of the formation of polycarboxyphenyl-grafted MWCNT with plausible structures by the grafting of diazonium compound for the development of enzyme-free biosensors [33]. The morphological feature of the P-CNT with metal precursor was changed after the treatment with oxidizing agent. Here, the fine distribution of Fe2O3 nanoparticles was observed compared to Sm2O3 nanoparticles on the surface of P-CNT.Figure 2
TEM images of (a) purified MWCNT, (b) P-CNT, (c) P-CNT with Sm(NO3)3, (d) Sm2O3 nanoparticle decorated P-CNT, (e) P-CNT with FeCl2, and (f) Fe2O3 particle decorated P-CNT.
(a)
(b)
(c)
(d)
(e)
(f)Figure3 displays the SEM images of (a) purified MWCNT, (b) P-CNT, (c) P-CNT with Sm(NO3)3, (d) Sm2O3/P-CNT, (e) P-CNT with FeCl2, and (f) Fe2O3/P-CNT. Similar to TEM images, grafting of polycarboxyphenyl polymer on MWCNT increased the diameter of MWCNT. Relatively, dense decoration of metal oxide nanoparticles on P-CNT was observed in Sm2O3/P-CNT compared to Fe2O3/P-CNT composite. Energy dispersive X-ray (EDX) analysis in Figure 4 confirms that only carbon and oxygen are present in the analysis of (a) purified MWCNT and (b) P-CNT. After the reaction with metal precursors, Fe and Sm were also observed in Figures 4(c) and 4(e), respectively. The calculated atomic ratios of Sm to O in Figure 4(d) and Fe to O in Figure 4(f) are close to 2 : 3, which agree well with the stoichiometric ratio of Fe2O3 and Sm2O3. Figure 5(a) presents the X-ray diffraction patterns of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with Sm(NO3)3, and (D) Sm2O3/P-CNT. The diffraction peak of MWCNT at 2
θ
=
26.1° and 43.3° was observed corresponding to the 002 and 100, respectively. The Sm2O3/P-CNT shows diffraction peaks at 222, 321, 024, 332, 422, 125, and 400 as the indication of the formation of Sm2O3 nanoparticle [34] on the surface of MWCNT. Figure 5(b) shows X-ray diffraction patterns of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with FeCl2, and (D) Fe2O3 nanoparticles decorated P-CNT. Except for the characteristic diffraction peak of MWCNT, we could not observe any additional peak in P-CNT with FeCl2, but P-CNT with Sm(NO3)3 showed sharp diffraction peak at 102. Probably, the difference in the interaction of different metal precursors (Sm(NO3)3 and FeCl2) with P-CNT was responsible for showing such type of variation on the X-ray diffraction peaks. Furthermore, Fe2O3/P-CNT composite shows the diffraction peaks of Fe2O3 at 220, 311, 222, and 400 [35]. Here, the broader size of the diffractive peaks of Fe2O3 indicates that the crystalline size of Fe2O3 particles is quite small.Figure 3
SEM images of (a) purified MWCNT, (b) P-CNT, (c) P-CNT with Sm(NO3)3, (d) Sm2O3 nanoparticle decorated P-CNT, (e) P-CNT with FeCl2, and (f) Fe2O3 particle decorated P-CNT.
(a)
(b)
(c)
(d)
(e)
(f)Figure 4
EDX spectra of (a) purified MWCNT, (b) P-CNT, (c) P-CNT with Sm(NO3)3, (d) Sm2O3 nanoparticle decorated P-CNT, (e) P-CNT with FeCl2, and (f) Fe2O3 particle decorated P-CNT.
(a)
(b)
(c)
(d)
(e)
(f)Figure 5
(a) The XRD patterns of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with Sm(NO3)3, and (D) Sm2O3 nanoparticles decorated P-CNT. (b) The XRD patterns of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with FeCl2, and (D) Fe2O3 nanoparticles decorated P-CNT.
(a)
(b)Figure6(a) shows TGA thermograms of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with Sm(NO3)3, and (D) Sm2O3/P-CNT. Except for ~3% mass loss below 60°C, purified MWCNT did not lose major mass before ~500°C, whereas P-CNT lost 16.3% mass in the two steps between 110 and 400°C and underwent a major mass loss (~65 wt%) at ~500°C. The mass loss of P-CNT below 400°C occurred due to the degradation of grafted polymer in MWCNT. Probably, the degradation of carboxyl group happened at the earlier stage and conjugated benzene rings at the later stage. Here, lower thermal stability of P-CNT than purified MWCNT was due to the grafting of long polymer chain on the wall of nanotube. Figure 6(b) presents TGA thermograms of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with FeCl2, and (D) Fe2O3/P-CNT. When we compared the TGA thermograms of MWCNT with metal precursor and metal oxide nanoparticles in Figures 6(a) and 6(b), obviously thermal stability of the metal oxide particle decorated P-CNT was higher than P-CNT with metal precursor. Interestingly, the residue after TGA of Sm2O3/P-CNT and Fe2O3/P-CNT was observed to be ~40% and ~12%, respectively. The dense decoration of Sm2O3 nanoparticles than Fe2O3 on P-CNT was responsible for obtaining different nature of the TGA thermograms of Sm2O3/P-CNT and Fe2O3/P-CNT and that was also supported by the FESEM images in Figures 3(d) and 3(f).Figure 6
(a) TGA thermograms of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with Sm(NO3)3, and (D) Sm2O3 nanoparticles decorated P-CNT. (b) TGA thermograms of (A) purified MWCNT, (B) P-CNT, (C) P-CNT with FeCl2, and (D) Fe2O3 nanoparticles decorated P-CNT.
(a)
(b)The electrochemical performances of the purified MWCNT, P-CNT, Sm2O3/P-CNT, and Fe2O3/P-CNT were analyzed using CV and GCD measurements. Figure 7(a) shows CV curves obtained in two-electrode cell for (A) purified MWCNT, (B) P-CNT, (C) Sm2O3/P-CNT, and (D) Fe2O3/P-CNT electrodes at a voltage scan rate of 5 mV/s in 1.0 M H2SO4 electrolyte in potential ranges of 0.0 to 1.0 V. From the above CV curves, the difference in the electrochemical surface activity of all electrode materials can easily be identified. It is noted that the area of the CV curves of P-CNT is larger than that of purified MWCNT, indicating a better capacitive response of P-CNT. The grafting of conjugated polycarboxyphenyl group on MWCNT was useful for enhancing the capacitance performance. Significant synergistic effect of polycarboxyphenyl polymer and metal oxide was observed in metal oxide decorated P-CNT. Interestingly, Fe2O3 decorated P-CNT showed the largest capacity among all of the electrode materials without changing the shape of the CV profiles. Furthermore, P-CNT exhibited a much lower area of the CV curve than that of Fe2O3 and Sm2O3decorated P-CNT, indicating the better capacitance performance of the metal decorated P-CNT nanocomposite. Moreover, the intimate interaction or strong charge coupling of Fe2O3 with P-CNT arising from the chemical grafting provides a synergistic effect and results in enhanced accessibility of the electrolyte by every Fe2O3 nanoparticle, leading to improving capacitance of the Fe2O3/P-CNT composites. On the contrary, dense decoration of Sm2O3 on the P-CNT results in agglomeration of metal particles and also decreases the effective surface area of Sm2O3/P-CNT nanocomposite. As a result, the Sm2O3/P-CNT nanocomposite was the low specific capacitance. In this study, we could not observe any redox peaks in P-CNT and MP-CNT probably due to the sequence of redox reactions occurring in the conjugated polymer and metallic oxide decorated MWCNT nanocomposite [3, 25]. The area of the CV curves of Sm2O3/P-CNT and Fe2O3/P-CNT nanocomposites increased with increasing the scan rate from 5 mV/s to 15 mV/s as shown in Figures 7(b) and 7(c). Table 1 shows the specific capacitance of the purified MWCNT, P-CNT, Sm2O3/P-CNT, and Fe2O3/P-CNT electrodes from cyclic voltammograms at a scan rate of 5 mV/s. A Fe2O3 decorated P-CNT composite electrode exhibited the highest specific capacitance (173.3 F g−1), almost 2.8 times higher than that of purified MWCNT electrode and 2.2 times higher than that of P-CNT electrode, indicating a significant synergistic effect of conjugated polymer and Fe2O3. The specific capacitance of the Fe2O3/P-CNT composites was superior to that of Sm2O3/P-CNT, probably due to the different nature of metal oxides and their different interaction properties with P-CNT.Table 1
Specific capacitance (F/g) of the purified MWNT, P-CNT, Sm2O3/P-CNT, and Fe2O3/P-CNT electrodes from cyclic voltammograms at the scan rate of 5 mV s−1 in 1.0 M H2SO4 electrolyte.
Purified MWNT
P-CNT
Sm2O3/P-CNT
Fe2O3/P-CNT
Specific capacitance(F g−1)
45.36
54.1
65.84
173.38Figure 7
(a) Cyclic voltammograms of (A) purified MWNT, (B) P-CNT, (C) Sm2O3/P-CNT, and (D) Fe2O3/P-CNT electrodes at a scan rate of 5 mV s−1 in 1.0 M H2SO4 electrolyte. (b) Cyclic voltammograms of Sm2O3/P-CNT electrodes measured in 1.0 M H2SO4 electrolyte at the scan rates of (A) 5 mV s−1, (B) 10 mV s−1, and (C) 15 mV s−1. (c) Cyclic voltammograms of Fe2O3/P-CNT electrodes measured in 1.0 M H2SO4 electrolyte at the scan rates of (A) 5 mV s−1, (B) 10 mV s−1, and (C) 15 mV s−1.
(a)
(b)
(c)Figure8 shows the GCD plots of (a) purified MWCNT, (b) P-CNT, (c) Sm2O3/P-CNT, and (d) Fe2O3/P-CNT electrodes at an applied constant current of 0.3 mA. It can be seen that the charge-discharge curves of the purified MWNTs were very symmetrical and had a triangular shape as shown in Figure 8(a). This implies that the purified MWNT electrodes clearly had electrochemical double layer capacitive behavior [4, 16]. The P-CNT, Sm2O3/P-CNT, and Fe3O4/P-CNT composite electrodes also showed reversible charge-discharge process of the electrode. Compared to the other electrode materials, Fe3O4/P-CNT composite electrode showed the longest discharge time ascribed to the correct quantity of Fe2O3 contributing reversible redox transitions relating the exchange of protons and/or cations with the electrolyte.Figure 8
Galvanostatic charge discharge of (a) MWNT, (b) P-CNT (b), (c) Sm2O3/P-CNT, and (d) Fe2O3/MWNT at an applied constant current of 0.3 mA in 1.0 M H2SO4 aqueous electrolyte.
(a)
(b)
(c)
(d)


## 4. Conclusions

The grafting of polycarboxyphenyl group on MWCNT and decoration with Fe2O3 and Sm2O3 nanoparticles separately presented herein offer a promising and facile approach to prepare a new class of electrode materials. The TEM, SEM, EDX, TGA, and X-ray diffraction of electrode materials provide the evidences for the grafting of polycarboxyphenyl group on the wall of MWCNT and subsequent metal oxide nanoparticles decoration. Electrochemical test of the purified MWCNT, P-CNT, Sm2O3/P-CNT, and Fe2O3/P-CNT electrodes from cyclic voltammograms at a scan rate of 5 mV/s shows specific capacitance of 45.3 F/g, 54.1 F/g, 65.84 F/g, and 173.3 F/g, respectively. The remarkably highest specific capacitance of Fe2O3/P-CNT composite electrode compared to other electrodes is due to the grafting of the conjugated polycarboxyphenyl polymer on MWCNTs in the development of a π-conjugated structure and proper decoration of P-CNT by Fe2O3 nanoparticles for the charge transfer facilitation.



---