# The Development of an Amperometric Enzyme Biosensor Based on a Polyaniline-Multiwalled Carbon Nanocomposite for the Detection of a Chemotherapeutic Agent in Serum Samples from Patients

Authors: Ahmad Gholami; Fatemeh Farjami; Younes Ghasemi
Journal: Journal of Sensors
 (2021)

---

## Abstract

Polyaniline was electrochemically polymerized onto the platinum electrode modified with a mixture of Nafion and multiwalled carbon nanotube (PANI/MWCNT/Nf/Pt) to detect ammonium ion. The nanobiosensor (ASNase/PANI/MWCNT/Nf/Pt) was then prepared by immobilizing L-asparaginase (L-ASNase) on the PANI/MWCNT/Nf nanocomposite. The prepared nanobiosensor was used for the rapid and sensitive detection of serum concentration of the anticancer agent L-asparagine (L-Asp) during chemotherapy. The nanobiosensor has dynamic ranges of zero to 180μM. The sensitivity of the nanobiosensor was 0.829 μA μM−1 cm−2, and the response time was less than 30 s. The detection limit was 140 nM of L-Asp. The Michaelis–Menten constant (Km) was measured to be 36.2 mM. The nanobiosensor was successfully applied for the determination of L-Asp in the blood samples of leukemia patients.


---

## Body

## 1. Introduction

L-Asparagine (L-Asp) is a nonessential amino acid synthesized by the cells on their own by asparagine synthetase. The cancer cells cannot synthesize L-Asp and rely on the extracellular supply in plasma and tissue. L-Asparaginase (L-ASNase) is a chemotherapeutic agent which can break down L-Asp into aspartic acid and ammonium ion. Due to this process, the cancer cells die as they cannot accomplish their protein synthesis. L-ASNase is extensively used for the treatment of childhood acute lymphoblastic leukemia [1].It is critical to determine and adjust the L-Asp concentration in the patients’ blood during treatment because this chemotherapeutic protein has a narrow therapeutic index. Over the last decades, some efforts have been made to develop methods for determining L-Asp in serum samples. Standard instrumental techniques such as ion-pair chromatography [2], spectrophotometry [3], and colorimetric assay [4] have been used for the determination of L-Asp; however, these methods are often sophisticated, time-consuming, and very expensive.Enzymatic methods for determining amino acid levels are an important route in detecting several biopharmaceuticals [5]. Biosensors containing electrochemical transducers, mostly with potentiometric ones [6], have been developed based on the measurement of ammonium ions produced during the enzymatic destruction of L-Asp. L-ASNase, as a catalytic enzyme, hydrolyzes L-Asp to L-aspartic acid and NH4+ [1, 7]. Analytical studies such as equilibrium dialysis and fluorescence quenching revealed that about one mole of L-aspartic acid and one mole of NH4+ were produced due to hydrolysis of one mole L-asparagine by one mole of L-ASNase, with a dissociation constant on the order of 60-160 μM [8]. However, the significant drawbacks of potentiometric biosensors are the slow response to a steady-state potential value and a high detection limit [9, 10]. In contrast, amperometric biosensors represent better sensitivity, quicker responses, and a lower detection limit [11]. The mentioned properties make them a proper choice for the rapid and reliable tool for determining the L-Asp level in biological samples. Since NH4+ ions are not electroactive, for amperometric determination of this ion, systems with the application of the composite polymers of Nafion with polyaniline (PANI) or polypyrrole were used [12]. PANI is considered a fascinating conductive polymer for designing enzyme biosensors because it has great electrochemical tunability, redox actions, electrocatalytic conduction, good processability, and environmental stability, along with a flexible chemical structure with the ability to be functionalized [13]. Chowdhury et al. showed that PANI nanowires (decorated with gold nanostructures) were successfully used for biopharmaceutical sensing with advantages of low detection limit, excellent sensitivity, and long-term stability [14].One of the most crucial characteristics of conducting polymers is their ability to reversibly alternate between the conducting and insulating electronic states by doping-undoping of ions [15–20]. Anions were shown to be the dopants in polyaniline films [21]. However, polyaniline electrodeposition on Nafion film results in a Nafion-coated polyaniline composite with a cation doping-undoping behavior [22]. Nafion is a cation exchanger conducting polymer. The Nafion-polyaniline composite could effectively sense the ammonium ion; therefore, this composite was used in enzymatic biosensors based on NH4+ detection like urea and L-arginine biosensors [23].Recently, Shu and Tang reviewed the recent advances in photoelectrochemical sensing [24]. They mentioned engineering photoactive materials through photoelectric conversion, which involves kinetics and thermodynamics and conversion efficiency. Semiconductor-carbon heterojunction such as multiwalled carbon nanotubes (MWCNTs) and single-walled carbon nanotubes (SWCNTs) can improve charge separation/transfer in electrochemical biosensors [25, 26]. The introduction of MWCNTs into the PANI matrix [27] and MWCNT into Nafion [28] and their application to construct biosensors were repeatedly reported. Different nanocomposites of Nafion, MWCNT, and polyaniline were constructed [29–31]; however, to the best of our knowledge, they were not used to fabricate amperometric ammonium ion sensors or in the biosensors based on the detection of ammonium ions.In this work, the nanocomposite of PANI/MWCNT/Nafion was prepared. L-ASNase was immobilized directly on the nanocomposite, and a very sensitive L-Asp biosensor was formed. This study may open a new way for effective monitoring of L-Asp in the serum of cancer patients receiving all forms of clinically used L-ASNase, which helps physicians effectively adjust the dose of this chemotherapeutic agent.


## 2. Experiment

### 2.1. Reagents

Sodium hydrogen phosphate and sodium dihydrogen phosphate were purchased from Acrose. L-Asparagine and ammonium chloride were bought from Merck. L-Asparaginase was from Kyowa (Japan). Bovine serum albumin (BSA), D-homocysteic acid, 5-sulfosalicylic acid, MWCNT (>90% carbon basis,D×L110‐170nm×5‐9μm), and Nafion were obtained from Sigma-Aldrich.


### 2.2. Apparatus

A scanning electron microscope (MIRA3TESCAN-XMU) was used to characterize the PANI/MWCNT film on the surface of a Pt electrode. FT-IR ATR spectra were recorded by using TENSOR II (Bruker, Germany). The electropolymerization of aniline was performed through a three-electrode system, including a Pt auxiliary electrode, an Ag/AgCl 3 M KCl reference electrode, and a Pt disk (3.0 mm diameter) working electrode. An Autolab electrochemical system (Eco-Chemie, Utrecht, The Netherlands) equipped with Autolab PGSTAT-302N GPES software (Eco-Chemie, Utrecht, The Netherlands) was used for voltammetric experiments.


### 2.3. Pretreatment of MWCNT

A sample of 0.5 g MWCNT was suspended in 240 mL of concentrated nitric acid and sulphuric acid (1 : 3 in volume ratio) and refluxed at 80°C for 4 h. After washing with copious amounts of doubly distilled water until the supernatant attained a pH around seven, the sample was dried in a vacuum oven at 80°C.


### 2.4. Preparation of Electrodes

A 0.5 wt% Nafion solution was prepared by diluting a 5% sample with 90% ethanol/water. A 5μL aliquot of this solution was coated onto a working Pt electrode and dried in air. Then, 5 μL of 0.1 mg/mL MWCNT was placed on the electrode and was dried. The MWCNT/Nf/Pt electrode was immersed in a solution containing 0.2 M aniline in 0.5 M HCl, and electropolymerization was carried out by cyclic voltammetry. The potential was swept from 200 to 1200 mV (vs. the Ag/AgCl reference electrode) with a scan rate of 50 mV s-1. The fabricated electrode (PANI/MWCNT/Nf/Pt) has a distinct light green color. The PANI/Nf/Pt electrode was made in the same way without MWCNT.To prepare the selective membrane, a solution of 200 U/mL L-ASNase, 2% Nafion, and 2% BSA was prepared. 5μL of this solution was drop-cast on the surface of PANI/MWCNT/Nf/Pt and allowed to dry.


### 2.5. Preparation of Real Samples

To study the biosensor application in real sample analysis, we tested blood samples collected from patients hospitalized in Namazi Hospital, located in Shiraz, Iran. The donor was a patient with acute lymphoblastic leukemia (ALL) who was given low doses of L-ASNase (10000 IU per m2 every 3 days). The samples were obtained 24 h before administration of L-ASNase and 72 h after the second dose.


### 2.6. Determination of L-Asp Concentration by the Reference Method

A total of 2 mL blood sample was added to 0.1 mL homocysteic acid solution (100μg/mL) and 0.5 mL sulfosalicylic acid (200 μg/mL). The solution was vortexed and centrifuged at 4000 RPM for 3 min, and the supernatants were stored at -80°C until further analysis.The serum concentration of L-Asp was also determined using high-performance liquid chromatography (HPLC) as the reference method. The column was treated with phthaldialdehyde, and separation was done by isocratic elution with a mobile phase of water-acetonitrile-sodium propionate buffer (82 : 7.5 : 10.5,v/v), delivered at a flow rate of 1.6 mL/min through a Eurospher C18 column (150mm×4.6mm) as the stationary phase. The chromatographic pattern of L-Asp was detected by using a fluorescence detector (Knauer, Berlin, Germany) at the excitation wavelength of 360 nm and an emission cut-off filter of 418 nm. The analysis of chromatograms was done by using EZChrom Elite® software.


## 2.1. Reagents

Sodium hydrogen phosphate and sodium dihydrogen phosphate were purchased from Acrose. L-Asparagine and ammonium chloride were bought from Merck. L-Asparaginase was from Kyowa (Japan). Bovine serum albumin (BSA), D-homocysteic acid, 5-sulfosalicylic acid, MWCNT (>90% carbon basis,D×L110‐170nm×5‐9μm), and Nafion were obtained from Sigma-Aldrich.


## 2.2. Apparatus

A scanning electron microscope (MIRA3TESCAN-XMU) was used to characterize the PANI/MWCNT film on the surface of a Pt electrode. FT-IR ATR spectra were recorded by using TENSOR II (Bruker, Germany). The electropolymerization of aniline was performed through a three-electrode system, including a Pt auxiliary electrode, an Ag/AgCl 3 M KCl reference electrode, and a Pt disk (3.0 mm diameter) working electrode. An Autolab electrochemical system (Eco-Chemie, Utrecht, The Netherlands) equipped with Autolab PGSTAT-302N GPES software (Eco-Chemie, Utrecht, The Netherlands) was used for voltammetric experiments.


## 2.3. Pretreatment of MWCNT

A sample of 0.5 g MWCNT was suspended in 240 mL of concentrated nitric acid and sulphuric acid (1 : 3 in volume ratio) and refluxed at 80°C for 4 h. After washing with copious amounts of doubly distilled water until the supernatant attained a pH around seven, the sample was dried in a vacuum oven at 80°C.


## 2.4. Preparation of Electrodes

A 0.5 wt% Nafion solution was prepared by diluting a 5% sample with 90% ethanol/water. A 5μL aliquot of this solution was coated onto a working Pt electrode and dried in air. Then, 5 μL of 0.1 mg/mL MWCNT was placed on the electrode and was dried. The MWCNT/Nf/Pt electrode was immersed in a solution containing 0.2 M aniline in 0.5 M HCl, and electropolymerization was carried out by cyclic voltammetry. The potential was swept from 200 to 1200 mV (vs. the Ag/AgCl reference electrode) with a scan rate of 50 mV s-1. The fabricated electrode (PANI/MWCNT/Nf/Pt) has a distinct light green color. The PANI/Nf/Pt electrode was made in the same way without MWCNT.To prepare the selective membrane, a solution of 200 U/mL L-ASNase, 2% Nafion, and 2% BSA was prepared. 5μL of this solution was drop-cast on the surface of PANI/MWCNT/Nf/Pt and allowed to dry.


## 2.5. Preparation of Real Samples

To study the biosensor application in real sample analysis, we tested blood samples collected from patients hospitalized in Namazi Hospital, located in Shiraz, Iran. The donor was a patient with acute lymphoblastic leukemia (ALL) who was given low doses of L-ASNase (10000 IU per m2 every 3 days). The samples were obtained 24 h before administration of L-ASNase and 72 h after the second dose.


## 2.6. Determination of L-Asp Concentration by the Reference Method

A total of 2 mL blood sample was added to 0.1 mL homocysteic acid solution (100μg/mL) and 0.5 mL sulfosalicylic acid (200 μg/mL). The solution was vortexed and centrifuged at 4000 RPM for 3 min, and the supernatants were stored at -80°C until further analysis.The serum concentration of L-Asp was also determined using high-performance liquid chromatography (HPLC) as the reference method. The column was treated with phthaldialdehyde, and separation was done by isocratic elution with a mobile phase of water-acetonitrile-sodium propionate buffer (82 : 7.5 : 10.5,v/v), delivered at a flow rate of 1.6 mL/min through a Eurospher C18 column (150mm×4.6mm) as the stationary phase. The chromatographic pattern of L-Asp was detected by using a fluorescence detector (Knauer, Berlin, Germany) at the excitation wavelength of 360 nm and an emission cut-off filter of 418 nm. The analysis of chromatograms was done by using EZChrom Elite® software.


## 3. Results and Discussion

As the first step for constructing the L-Asp biosensor, an ammonium sensor was developed and optimized because the proposed biosensor determines L-Asp by measuring the ammonium ion concentration produced during enzymatic destruction of L-Asp.


### 3.1. Electropolymerization of Aniline on the Nf/Pt Electrode

The CVs recorded during electrodeposition of polyaniline on the Nf/Pt electrode are shown in Figure1. The peak positions and their intensities are analogous to those commonly observed in the literature [20]; however, they vary with the conditions of electrodeposition. The polymerization mechanism of aniline in acid medium and the PANI polymer structure is presented in Scheme 1. The CVs show that the electropolymerization processes consist of two or three electrochemical systems. The large peak at 0.9 V that appeared at the first scan is due to the oxidation of aniline monomer to form cation radicals (the first step of Scheme 1). The reverse sweep of the first cycle involves a crossing effect interpreted as the start of the nucleation process of the polymer. New peaks, which are ascribable to the electrochemical response of PANI deposits formed during the oxidation process of aniline, appear after the first cycle.Figure 1
Five successive cyclic voltammograms of the Nf/Pt electrode in 0.2 M aniline in 0.5 M HCl at a scan rate of 50 mV s-1.Scheme 1
The schematic diagram showing the structure and the electropolymerization mechanism of polyaniline.The following cycles indicate a normal growth of the polymeric deposit. In acidic solutions, the second step of polymerization involves an isomeric transformation of cation radicals and the formation of a dimeric intermediate product through deprotonation and rearomatization. The anodic peak around 0.1 V is due to the oxidation of the dimer to dimer cation radicals and then further reacts with monomer cation radicals which is the propagation step of the polymerization (step 3 of Scheme1). Also, the oxidation of leucoemeraldin (a fully reduced form of PANI, x=1) to emeraldine (a half-reduced form of PANI, x=0.5) occurs at this potential. The cathodic peak of this redox pair is related to the reduction of emeraldine to leucoemeraldine. The redox pair around 0.7 V was assigned to emeraldine oxidation to pernigraniline (a fully oxidized form of PANI, x=0) and reverse reduction reaction (step 4 of Scheme 1). The very weak peak at ca. 0.5 V is due to benzoquinone/hydroquinone—the products of PANI hydrolysis [21].As the potential needed for the oxidation of the monomer is always higher than the charging of oligomeric intermediates or the resulting polymer, the two processes of polymer formation and its oxidations (doping) are simultaneously occurring. The anions are doped during electrochemical polymerization, fulfilling the request of electroneutrality. When Nafion, which is a cation exchanger, is used as a substrate, the sulfonate groups attached to the polymer backbone play the role of anions, and upon oxidation, the cationic PA polymer forms within the Nafion matrix with the expulsion of Na+; therefore, the reduction process needs cations.
(1)C++PA+·RSO3−+e−⟶PA·C+·RSO3−.


### 3.2. Characterization of the Ammonium Sensor

Figure2 shows the linear sweep voltammograms of the PANI/Nf/Pt electrode in the buffer solution pH 7 containing different concentrations of NH4+. An increased cathodic current at about -0.2 V was observed. The transient current responses of various electrodes to successive addition of 2.5 μM NH4+ in chronoamperometric experiments at a constant potential of -0.2 V are displayed in Figure 3. No cathodic current was seen under ammonium addition at the Nf/Pt and PANI/Pt electrodes (amperograms a and b). However, at the PANI/Nf/Pt (amperogram c) electrode, a transient reduction current was observed, proportional to the concentration of ammonium ion in the solution.Figure 2
Linear sweep voltammograms of PANI/CNT/Nf/Pt recorded before (a) and after successive addition of 0.5 mM NH4Cl (b–e) (PBS pH 7, scan rate 50 mV·s−1).Figure 3
The response current-time curves of various modified electrodes Nf/Pt (a), PANI/Pt (b), PANI/Nf/Pt (c), and PANI/MWCNT/Nf/Pt (d) at successive addition of 2.5μM NH4+ in PBS (0.05 M, pH 7).The effect of incorporation of MWCNT in the PANI-Nf film was also investigated. A comparison of amperograms c and d confirms the higher sensitivity of the PANI/CNT/Nf nanocomposite than the PANI/Nf film. As described by other authors in the literature [32, 33], the functional group on the MWCNT surface in pH 7 is deprotonated to form the negative surface charge. This deprotonization may cause an increase in diffusing and movement of cations in the nanocomposite film and, therefore, enhance the current.Different parameters were optimized by chronoamperometry to obtain the best sensitivity for ammonium ion detection. As shown in Figure4(a), the sensitivity depends on the number of cycles used for electrodeposition of the PANI film because PANI is indeed the transducer of the sensor. The sensitivity increased up to five cycles, but the responses diminished at higher cycles, probably due to increased film thickness.Figure 4
The current of the ammonium sensor vs. the concentration ofNH4+ at (a) different electrodeposition cycles and (b) different constant potentials.
(a)(b)Applied working potentials were changed in the range of −0.1 to −0.3 V to determine the optimal polarization voltage for amperometric detection of ammonium ion with the current maximum found at −0.2 V (Figure4(b)).The SEM technique was used to characterize the morphology of the nanocomposite electrodeposited on the surface of the Pt electrode. A typical SEM image is shown in Figure5. It was evident that after the electrodeposition of the PANI film on the MWCNT-modified electrode, the majority of MWCNTs have been entrapped in the PANI film.Figure 5
SEM image of the PANI/MWCNT/Nafion nanocomposite.Figure6 shows a typical FT-IR ATR spectrum of pure polyaniline and the nanocomposite on the surface of a platinum electrode. The spectra of activated MWCNT and Nafion were also presented. The infrared bands are in agreement with those given in the literature for PANI [24, 25]. The two vibrations of pure polyaniline at 1288 and 1244 cm-1 are assigned to the stretching of the C–N bonds of the aromatic amine. The band at 1139 cm-1 is due to a vibrational mode of benzenoid-NH+=quinoid [26], which shows that the polyaniline films formed by electropolymerization are in the emeraldine form. The bands at 1566 and 1491 cm-1 are assignable to the ring stretching vibration of quinoid and benzenoid. It is observed in the FTIR spectra of the nanocomposite that polyaniline interacts with MWCNTs and causes redshift of the bands of polyaniline. This effect was previously reported [27]. The band at 1710 cm−1 in MWCNT spectra is due to the C=O stretching frequency, indicating the presence of the carboxylic group created during the activation of MWCNTs. This band also appears in the nanocomposite spectrum at 1700 cm-1 because the polyaniline peaks are absent in this region. In Nafion spectra, the band at 1056 cm-1 and 1154 cm-1 is attributed to S=O and CF2 stretching vibrations [28], respectively. But these bands are not observed in the nanocomposite spectra because they are masked by stronger PANI peaks.Figure 6
FT-IR ATR spectra of Nafion, MWCNT, polyaniline, and the nanocomposite.


### 3.3. Electrochemical Performances of the L-Asp Nanobiosensor

The L-Asp nanobiosensor (ASNase/PANI/MWCNT/Nf/Pt) was prepared by immobilization of L-ASNase on the PANI/MWCNT/Nf/Pt electrode. The influence of pH on the performance of the nanobiosensor was studied, and the results are shown in Figure7(a). The highest current was found at pH 7.0, and it was employed throughout the study.Figure 7
(a) Response current-time curves of the ASNase/PANI/MWCNT/Nf/Pt biosensor at successive addition of 5μM NH4+ in different phosphate buffer solutions, (b) amperometric response curve of the L-Asp biosensor in 0.05 M PBS to successive additions of L-Asp at an applied potential of -0.2, and (c) a plot of current vs. the concentrations of L-Asp in the range of 0 to 180 μM.
(a)(b)(c)Figure7(b) displays the amperometric response of the ASNase/PANI/MWCNT/Nf/Pt nanobiosensor to the sequential increment of L-Asp concentration at a constant potential of -0.2 V.A plot of the current versus the concentration of L-Asp is shown in Figure7(c). A dynamic concentration range was observed from 0 to 180 μM. The current intensity of the biosensor toward L-Asp increased linearly over the concentration range of 0 to 15 μM. The equation for the calibration line was IμA=0.0586CμM+0.0393 with R2=0.990, where C in the above equation is the L-Asp concentration in μM and I is the current in μA. The sensitivity of the biosensor was 0.829 μA μM−1 cm−2, and the limit of detection at a signal-to-noise ratio of 3 was estimated as 0.14 μM. Stepwise growth of reduction current was observed with increasing amounts of L-Asp in PBS, and the current reached a steady-state level of less than 30 s (response time). The reproducibility (RSD) of this sensor was 2.9% (n=5) to determine 10 μM L-Asp. The performance of the proposed nanobiosensor was compared with other L-Asp biosensors in Table 1. Its response time and detection limit are lower than other electrochemical biosensors that have ever been reported [34].Table 1
Characteristic of electrochemical L-Asp biosensors reported.
MethodDynamic range (M)Response timeDetection limit (μM)ReferencesPotentionmetric7×10−5–10−210 min60[30]Potentionmetric1.6×10−5–1.5×10−35 min[31]Amperometric2‐20×10−6——[29]Amperometric1‐180×10−630 s0.14This workThe apparent Michaelis–Menten constant (Kmapp) indicates the enzyme-substrate affinity for the biosensors. The electrochemical version of the Lineweaver–Burk equation can be applied to calculate Kmapp:
(2)1iss=1imax+Kmappimaxc,where iss is the steady-state current after adding substrate, C is the bulk concentration of the substrate, and imax is the maximum current measured under saturated substrate condition [35]. The calculated Kmapp of the L-Asp biosensor is 36.2 mM.


### 3.4. Real Sample Analysis

The biosensor was also tested for the L-Asp quantification in serum samples of the patient with leukemia before and after treatment with L-ASNase using the standard addition method. The presence of endogenous ammonium in the samples interferes with these determinations since the response measured corresponds to the sum of the ammonium generated enzymatically and present in the sample. Therefore, the latter was additionally measured in serum samples with the MWCNT/PANI/Nf/Pt electrode, and the concentration of L-Asp was calculated as a difference between the signals of PANI/MWCNT/Nf/Pt- and ASNase/PANI/MWCNT/Nf/Pt-based sensors (Table2). The results of a reference method (explained in the experimental part) are also given in Table 2. The t-test was applied to compare the results of the two methods. As seen from Table 2, the proposed biosensor results agree well with those obtained using a reference method.Table 2
The concentration of L-Asp in the blood sample of a patient with acute lymphoblastic leukemia.
SampleL-Asp (μM) concentration measured by the biosensor (n=3)L-Asp (μM) concentration measured by the reference method (n=3)atexpaFexpBefore L-ASNase injection64.53±3.8161.97±1.031.1113.6After L-ASNase injection7.96±0.478.33±0.0991.3222.5atexp and Fexp show the experimental Student t and experimental F values, respectively (t0.05 -2.78 and F0.052,2 -39.25).


## 3.1. Electropolymerization of Aniline on the Nf/Pt Electrode

The CVs recorded during electrodeposition of polyaniline on the Nf/Pt electrode are shown in Figure1. The peak positions and their intensities are analogous to those commonly observed in the literature [20]; however, they vary with the conditions of electrodeposition. The polymerization mechanism of aniline in acid medium and the PANI polymer structure is presented in Scheme 1. The CVs show that the electropolymerization processes consist of two or three electrochemical systems. The large peak at 0.9 V that appeared at the first scan is due to the oxidation of aniline monomer to form cation radicals (the first step of Scheme 1). The reverse sweep of the first cycle involves a crossing effect interpreted as the start of the nucleation process of the polymer. New peaks, which are ascribable to the electrochemical response of PANI deposits formed during the oxidation process of aniline, appear after the first cycle.Figure 1
Five successive cyclic voltammograms of the Nf/Pt electrode in 0.2 M aniline in 0.5 M HCl at a scan rate of 50 mV s-1.Scheme 1
The schematic diagram showing the structure and the electropolymerization mechanism of polyaniline.The following cycles indicate a normal growth of the polymeric deposit. In acidic solutions, the second step of polymerization involves an isomeric transformation of cation radicals and the formation of a dimeric intermediate product through deprotonation and rearomatization. The anodic peak around 0.1 V is due to the oxidation of the dimer to dimer cation radicals and then further reacts with monomer cation radicals which is the propagation step of the polymerization (step 3 of Scheme1). Also, the oxidation of leucoemeraldin (a fully reduced form of PANI, x=1) to emeraldine (a half-reduced form of PANI, x=0.5) occurs at this potential. The cathodic peak of this redox pair is related to the reduction of emeraldine to leucoemeraldine. The redox pair around 0.7 V was assigned to emeraldine oxidation to pernigraniline (a fully oxidized form of PANI, x=0) and reverse reduction reaction (step 4 of Scheme 1). The very weak peak at ca. 0.5 V is due to benzoquinone/hydroquinone—the products of PANI hydrolysis [21].As the potential needed for the oxidation of the monomer is always higher than the charging of oligomeric intermediates or the resulting polymer, the two processes of polymer formation and its oxidations (doping) are simultaneously occurring. The anions are doped during electrochemical polymerization, fulfilling the request of electroneutrality. When Nafion, which is a cation exchanger, is used as a substrate, the sulfonate groups attached to the polymer backbone play the role of anions, and upon oxidation, the cationic PA polymer forms within the Nafion matrix with the expulsion of Na+; therefore, the reduction process needs cations.
(1)C++PA+·RSO3−+e−⟶PA·C+·RSO3−.


## 3.2. Characterization of the Ammonium Sensor

Figure2 shows the linear sweep voltammograms of the PANI/Nf/Pt electrode in the buffer solution pH 7 containing different concentrations of NH4+. An increased cathodic current at about -0.2 V was observed. The transient current responses of various electrodes to successive addition of 2.5 μM NH4+ in chronoamperometric experiments at a constant potential of -0.2 V are displayed in Figure 3. No cathodic current was seen under ammonium addition at the Nf/Pt and PANI/Pt electrodes (amperograms a and b). However, at the PANI/Nf/Pt (amperogram c) electrode, a transient reduction current was observed, proportional to the concentration of ammonium ion in the solution.Figure 2
Linear sweep voltammograms of PANI/CNT/Nf/Pt recorded before (a) and after successive addition of 0.5 mM NH4Cl (b–e) (PBS pH 7, scan rate 50 mV·s−1).Figure 3
The response current-time curves of various modified electrodes Nf/Pt (a), PANI/Pt (b), PANI/Nf/Pt (c), and PANI/MWCNT/Nf/Pt (d) at successive addition of 2.5μM NH4+ in PBS (0.05 M, pH 7).The effect of incorporation of MWCNT in the PANI-Nf film was also investigated. A comparison of amperograms c and d confirms the higher sensitivity of the PANI/CNT/Nf nanocomposite than the PANI/Nf film. As described by other authors in the literature [32, 33], the functional group on the MWCNT surface in pH 7 is deprotonated to form the negative surface charge. This deprotonization may cause an increase in diffusing and movement of cations in the nanocomposite film and, therefore, enhance the current.Different parameters were optimized by chronoamperometry to obtain the best sensitivity for ammonium ion detection. As shown in Figure4(a), the sensitivity depends on the number of cycles used for electrodeposition of the PANI film because PANI is indeed the transducer of the sensor. The sensitivity increased up to five cycles, but the responses diminished at higher cycles, probably due to increased film thickness.Figure 4
The current of the ammonium sensor vs. the concentration ofNH4+ at (a) different electrodeposition cycles and (b) different constant potentials.
(a)(b)Applied working potentials were changed in the range of −0.1 to −0.3 V to determine the optimal polarization voltage for amperometric detection of ammonium ion with the current maximum found at −0.2 V (Figure4(b)).The SEM technique was used to characterize the morphology of the nanocomposite electrodeposited on the surface of the Pt electrode. A typical SEM image is shown in Figure5. It was evident that after the electrodeposition of the PANI film on the MWCNT-modified electrode, the majority of MWCNTs have been entrapped in the PANI film.Figure 5
SEM image of the PANI/MWCNT/Nafion nanocomposite.Figure6 shows a typical FT-IR ATR spectrum of pure polyaniline and the nanocomposite on the surface of a platinum electrode. The spectra of activated MWCNT and Nafion were also presented. The infrared bands are in agreement with those given in the literature for PANI [24, 25]. The two vibrations of pure polyaniline at 1288 and 1244 cm-1 are assigned to the stretching of the C–N bonds of the aromatic amine. The band at 1139 cm-1 is due to a vibrational mode of benzenoid-NH+=quinoid [26], which shows that the polyaniline films formed by electropolymerization are in the emeraldine form. The bands at 1566 and 1491 cm-1 are assignable to the ring stretching vibration of quinoid and benzenoid. It is observed in the FTIR spectra of the nanocomposite that polyaniline interacts with MWCNTs and causes redshift of the bands of polyaniline. This effect was previously reported [27]. The band at 1710 cm−1 in MWCNT spectra is due to the C=O stretching frequency, indicating the presence of the carboxylic group created during the activation of MWCNTs. This band also appears in the nanocomposite spectrum at 1700 cm-1 because the polyaniline peaks are absent in this region. In Nafion spectra, the band at 1056 cm-1 and 1154 cm-1 is attributed to S=O and CF2 stretching vibrations [28], respectively. But these bands are not observed in the nanocomposite spectra because they are masked by stronger PANI peaks.Figure 6
FT-IR ATR spectra of Nafion, MWCNT, polyaniline, and the nanocomposite.


## 3.3. Electrochemical Performances of the L-Asp Nanobiosensor

The L-Asp nanobiosensor (ASNase/PANI/MWCNT/Nf/Pt) was prepared by immobilization of L-ASNase on the PANI/MWCNT/Nf/Pt electrode. The influence of pH on the performance of the nanobiosensor was studied, and the results are shown in Figure7(a). The highest current was found at pH 7.0, and it was employed throughout the study.Figure 7
(a) Response current-time curves of the ASNase/PANI/MWCNT/Nf/Pt biosensor at successive addition of 5μM NH4+ in different phosphate buffer solutions, (b) amperometric response curve of the L-Asp biosensor in 0.05 M PBS to successive additions of L-Asp at an applied potential of -0.2, and (c) a plot of current vs. the concentrations of L-Asp in the range of 0 to 180 μM.
(a)(b)(c)Figure7(b) displays the amperometric response of the ASNase/PANI/MWCNT/Nf/Pt nanobiosensor to the sequential increment of L-Asp concentration at a constant potential of -0.2 V.A plot of the current versus the concentration of L-Asp is shown in Figure7(c). A dynamic concentration range was observed from 0 to 180 μM. The current intensity of the biosensor toward L-Asp increased linearly over the concentration range of 0 to 15 μM. The equation for the calibration line was IμA=0.0586CμM+0.0393 with R2=0.990, where C in the above equation is the L-Asp concentration in μM and I is the current in μA. The sensitivity of the biosensor was 0.829 μA μM−1 cm−2, and the limit of detection at a signal-to-noise ratio of 3 was estimated as 0.14 μM. Stepwise growth of reduction current was observed with increasing amounts of L-Asp in PBS, and the current reached a steady-state level of less than 30 s (response time). The reproducibility (RSD) of this sensor was 2.9% (n=5) to determine 10 μM L-Asp. The performance of the proposed nanobiosensor was compared with other L-Asp biosensors in Table 1. Its response time and detection limit are lower than other electrochemical biosensors that have ever been reported [34].Table 1
Characteristic of electrochemical L-Asp biosensors reported.
MethodDynamic range (M)Response timeDetection limit (μM)ReferencesPotentionmetric7×10−5–10−210 min60[30]Potentionmetric1.6×10−5–1.5×10−35 min[31]Amperometric2‐20×10−6——[29]Amperometric1‐180×10−630 s0.14This workThe apparent Michaelis–Menten constant (Kmapp) indicates the enzyme-substrate affinity for the biosensors. The electrochemical version of the Lineweaver–Burk equation can be applied to calculate Kmapp:
(2)1iss=1imax+Kmappimaxc,where iss is the steady-state current after adding substrate, C is the bulk concentration of the substrate, and imax is the maximum current measured under saturated substrate condition [35]. The calculated Kmapp of the L-Asp biosensor is 36.2 mM.


## 3.4. Real Sample Analysis

The biosensor was also tested for the L-Asp quantification in serum samples of the patient with leukemia before and after treatment with L-ASNase using the standard addition method. The presence of endogenous ammonium in the samples interferes with these determinations since the response measured corresponds to the sum of the ammonium generated enzymatically and present in the sample. Therefore, the latter was additionally measured in serum samples with the MWCNT/PANI/Nf/Pt electrode, and the concentration of L-Asp was calculated as a difference between the signals of PANI/MWCNT/Nf/Pt- and ASNase/PANI/MWCNT/Nf/Pt-based sensors (Table2). The results of a reference method (explained in the experimental part) are also given in Table 2. The t-test was applied to compare the results of the two methods. As seen from Table 2, the proposed biosensor results agree well with those obtained using a reference method.Table 2
The concentration of L-Asp in the blood sample of a patient with acute lymphoblastic leukemia.
SampleL-Asp (μM) concentration measured by the biosensor (n=3)L-Asp (μM) concentration measured by the reference method (n=3)atexpaFexpBefore L-ASNase injection64.53±3.8161.97±1.031.1113.6After L-ASNase injection7.96±0.478.33±0.0991.3222.5atexp and Fexp show the experimental Student t and experimental F values, respectively (t0.05 -2.78 and F0.052,2 -39.25).


## 4. Conclusion

The MWCNT/PANI/Nf nanocomposite was utilized to fabricate a new amperometric L-Asp nanobiosensor that exhibited high sensitivity and selectivity. The nanobiosensor was specifically and successfully used to monitor L-Asp in the patient’s blood with acute lymphoblastic leukemia. One can expect that the proposed biosensor has the potential to be used as a point-of-care testing device. However, it will be the subject of further investigation in the future. The proposed nanocomposite might be considered for a wide range of biosensors based on the detection of ammonium ions. This novel nanobiosensor is a rapid, accurate, well-handled, portable vessel for in situ detection of the serum concentration anticancer agent L-asparaginase in human blood during chemotherapy. This approach helps make sure that the patient receives the optimal dose of the drug with the minimum side effect.



---

*Source: 5515728-2021-07-14.xml*