# Montmorillonite Clay-Based Polyurethane Nanocomposite As Local Triamcinolone Acetonide Delivery System

Authors: Flávia Carmo Horta Pinto; Armando Silva-Cunha; Gerson Antônio Pianetti; Eliane Ayres; Rodrigo Lambert Oréfice; Gisele Rodrigues Da Silva
Journal: Journal of Nanomaterials
 (2011)

---

## Abstract

Biodegradable polyurethane was synthesized by preparing aqueous polyurethane dispersion having poly(caprolactone) and poly(ethylene glycol) as soft segments. Montmorillonite particles were delaminated within the waterborne polyurethane to produce a nanocomposite. The triamcinolone acetonide (TA), an important corticoid drug, was dispersed into the nanocomposite followed by a drying step to produce an implantable drug delivery system. Infrared (FTIR) results demonstrated that the original chemical structure of the TA was preserved after incorporation into the nanocomposite. Wide angle (WAXS) and small angle X-ray scattering (SAXS) results suggested that TA and clay do not dramatically change the morphology phase of the polymer although they can interact with each other. The presence of montmorillonite particles in the nanocomposite reduced the rate of TA release as compared to the pure polyurethane and enhanced the mechanical properties of the polymer. The overall results indicate that montmorillonite clay-based polyurethane nanocomposite could be potentially applied as local TA delivery system.


---

## Body

## 1. Introduction

Nanoparticles derived from expandable clays, such as montmorillonite, have been considered for more than 15 years as a reinforcing agent for polymers [1]. These clays have an interlayer space than can be promptly impregnated by many species including polymers [2]. Exchanging natural cations present in clay by Na+ can allow water to enhance interlayer spacing up to several hundred angstroms [3]. Nonpolar cations can also be used to improve the compatibility between hydrophobic polymers and clays, but these special cations may lead to toxicity when biomedical applications are considered.Nanocomposites composed on polyurethane and montmorillonite particles have been widely investigated [4–6]. They are usually prepared by dispersing the layered silicate particles into the polyurethane matrix. The resulting polymer-layered silicate nanocomposites frequently display advanced properties (such as mechanical properties) due to their high surface area [1, 7]. Many properties, such as mechanical [8], water vapor permeability [5], and water permeability [9, 10] can be improved by incorporating small amounts of delaminated clay to a polyurethane matrix [11]. Montmorillonite clay-based polyurethane nanocomposites have been also explored as implantable drug-delivery systems. In this case, nanocomposites were loaded with therapeutic agents and then implanted in specific organs. They would be able to control the release of a therapeutic agent to a specific target to treat or prevent different types of pathological processes [12–14]. All these studies demonstrated the potential applicability of nanocomposites composed on polyurethane and montmorillonite in different fields.Intercalated and/or exfoliated morphologies can be obtained when clay nanoparticles are included into polymers [2]. An intercalated nanocomposite is obtained when polymer chains impregnate the clay interlayer gap to produce a multilayered structure. The properties of this type of composite are usually similar to polymers containing micrometer particles. In the exfoliated or delaminated structure, clay layers are well dispersed within the polymer matrices, and polymer-clay interactions are dramatically enhanced [15, 16]. Exfoliation of clays within polymer is usually associated with large improvements in properties not always possible to be obtained with micrometer particles are used [17].In the preparation of polyurethane/clay nanocomposites, modifications of montmorillonite by using organic modifiers such as alkylammonium to improve the compatibility between hydrophilic organomontmorillonite and hydrophobic polyurethanes are often employed [3, 6, 18, 19]. These organic chains having positively charged ends can be bonded to the surface of the negatively charged silicate layers resulting in an increase of the interlayer gap [20, 21]. However, these modifications can be potentially toxic when considering biomedical applications of the yielded devices. To avoid this type of potential toxicity, montmorillonite without any modification can be intercalated and/or delaminated using aqueous polyurethane dispersions to produce nanocomposites. In this type of nanocomposite processing technique, water is used to enlarge the space between silicate layers [10, 22, 23].In this study, polyurethane based on poly(caprolactone) and poly(ethylene glycol), as soft segment, and isophorone diisocyanate and hydrazine, as hard segments, was synthesized and dispersed in water. Montmorillonite particles and triamcinolone acetonide were dispersed directly in the waterborne polyurethane. The triamcinolone acetonide-loaded polyurethane nanocomposite implants were obtained by cutting the nanocomposite films into the desired shape (squares of 5 mm of side). The structure of the implantable devices was characterized by analytical techniques to identify not only the intercalation and/or exfoliation of the montmorillonite onto the nanocomposite, but also how the drug interacted and affected its morphology. The effect of the clay particles distribution on the mechanical properties of the polyurethane was also evaluated. The analyzed structure of the implants was useful in understanding thein vitrodrug-controlled release. Additionally, the in vivo release profile of the drug was evaluated through their subcutaneous implantation on the back of mice. Finally, it was revealed the applicability of the montmorillonite clay-based polyurethane nanocomposite loaded with triamcinolone acetonide as local controlled drug-delivery systems.


## 2. Materials and Methods

### 2.1. Synthesis of the Aqueous Polyurethane Dispersion (PU)

Aqueous polyurethane dispersion (PU) was prepared by a prepolymer mixing process, using a 250 mL three-neck glass flask equipped with a heating mantel, a mechanical stirrer, and a thermometer. The macrodiol components-polycaprolactone—diol (PCL 1000) (Tone Polyol 2221,M̅n=1000 g·mol−1), polycaprolactone-diol (PCL 2000) (Tone Polyol 0249, M̅n=2000 g·mol−1) (Dow-USA) (Sigma-Aldrich), and poly(ethylene glycol) (PEG, Mn=1500 g·mol−1, Sigma-Aldrich), isophorone diisocyanate (IPDI) (Bayer-Brazil) (NCO/OH ratio of 2.3) and 2,2-bis(hydroxymethyl) propionic acid (DMPA) (98.3%, Fluka) were added to the reactor in the presence of dibutyl tin dilaurate (DBDLT) (Miracema Nuodex-Brazil) and the reaction was carried out at 70°C–75°C in a nitrogen atmosphere for 4 h. The amount of free NCO groups on a percentage basis was determined by the standard di-butyl amine back titration method. After titration, the prepolymer temperature was allowed to drop to 40°C. The carboxylic acid groups were neutralized by the addition of triethylamine (TEA) (98%, Vetec-Brazil). The mixture was stirred for another 40 min to ensure that the reaction had been completed. All samples were dispersed by adding deionized water to the neutralized prepolymer which was stirred vigorously. After the dispersion, the amount of hydrazine (HZ) (solution 64%, Arch Química-Brazil) enough to react with free NCO groups was added to the reactor with a small amount of water, and stirring was continued for another 30 min. This chemical procedure was successful in producing a polyurethane dispersion with a solid content of about 25%. The composition of the polyurethane dispersion is shown in Table 1. Films were produced by casting the dispersion in a Teflon mould and allowing them to dry at room temperature for one week. Afterwards the films were placed in an oven at 60°C for 24 h [24]. A schematic representation of the chemical reactions and processing steps used to produce the polyurethane dispersion and nanocomposites is shown in Figure 1.Table 1
Composition (wt.%) of the aqueous PU dispersion*.
ReagentsConcentration (wt.%)Isophorone diisocyanate (IPDI)8.58Polycaprolactone-diol 1000 (PCL1000)4.85Polycaprolactone-diol 2000 (PCL2000)9.09Polyethylene glycol 1500 (PEG 1500)0.732,2-bis(hydroxymethyl) propionic acid (DMPA)0.97Triethylamine (TEA)0.73Water74.70Hydrazine (HZ)1.08*0.01% of dibutyl tin dilaurate based on the amounts of IPDI, PCL, and DMPA.Figure 1
Schematic representation of the process used to prepare polyurethane containing montmorillonite (MMT-Na+) and triamcinolone acetonide.


### 2.2. Incorporation of Clay Nanoparticles-Cloisite Na+

The montmorillonite clay without any treatment (Cloisite Na+, Southern Clay Products) was dispersed in water (5 wt.%) by stirring it for 24 hours at room temperature. This procedure is useful to reduce the average particle size of the clay particles to yield clay nanoparticles dispersed in water [25]. Clay nanoparticles were incorporated into the polyurethane aqueous dispersion by mixing the polymer with the aqueous dispersion of the clay (Figure 1). The dispersions were mixed in proportions to yield a final nanocomposite containing 5 wt.% of clay in the polyurethane.


### 2.3. Incorporation of Triamcinolone Acetonide and Preparation of the Implants

Triamcinolone acetonide (TA) (Sigma-Aldrich, 99.0%) was incorporated into the polymer by dispersing it in the nanocomposite prior of casting the films to yield materials having 20.5 wt% of the drug (Figure1). The dried films were cut into squares (5 mm in side) to obtain the triamcinolone acetonide-loaded polyurethane nanocomposite implants (TA PU-NC implants) having approximately 1.27 mg each one. Triamcinolone acetonide-loaded polyurethane implants (without clay particles) (TA PU implants) were also prepared.


### 2.4. Characterization

#### 2.4.1. Fourier Transform Infrared

Infrared spectra were collected in a Fourier transform infrared spectrophotometer (FTIR; Perkin Elmer, model Spectrum 1000). Measurements were carried out using the attenuated total reflectance (ATR) technique. Each spectrum was a result of 32 scans with a resolution of 4 cm−1.


#### 2.4.2. Small Angle X-Ray Scattering

The measurements of synchrotron small angle X-ray scattering (SAXS) were performed using the beam line of the national synchrotron light laboratory (LNLS, Campinas, Brazil). The photon beam used in the LNLS SAXS beamline comes from one of the 12 bending magnets of the electron storage ring. The white photon beam is extracted from the ring through a high-vacuum path. After passing through a thin beryllium window, the beam is monochromatized (λ = 1.608 Å) and horizontally focused by a cylindrically bent and asymmetrically cut silicon single crystal. The focus is located at the detection plane. The X-ray scattering intensity, I(q), was experimentally determined as a function of the scattering vector “q” whose modulus is given by q=(4π/λ)sin(θ), where λ is the X-ray wavelength and θ being half the scattering angle. Each SAXS pattern corresponds to a data collection time of 900 s. From the experimental scattering intensity produced by all the studied samples, the parasitic scattering intensity produced by the collimating slits was subtracted. All SAXS patterns were corrected for the nonconstant sensitivity of the PSD, for the time varying intensity of the direct synchrotron beam and for differences in sample thickness. Because of the normalization procedure, the SAXS intensity was determined for all samples in the same arbitrary units so that they can be directly compared.


#### 2.4.3. Wide Angle X-Ray Scattering

Wide angle X-ray scattering (WAXS) was performed by using a synchrotron light beam with a wavelength of 1.608 Å and an exposition time of 300 s. The scattering intensity was recorded by a Pilatus (100 K, 33 mm × 84 mm) detector. The sample to detector distance used was 80 mm.


#### 2.4.4. Scanning Electron Microscopy

Scanning electron microscopy (SEM) was performed using a JEOL microscope (model JSM-6360LV) operating at 15 kV. The TA PU implants were cryofractured and mounted on aluminium stubs using double-sided adhesive tape. Prior to microscopic examination, all the samples were sputter-coated with a gold layer under argon atmosphere using a sputter apparatus (Balzers Union SCD 040 unit, Balzers, Germany). The implants surfaces were viewed at 1000–10000x magnification, and the images were transferred to the computer by means of a digital image transference interface (DITI). The photomicrographs were adjusted using the software Adobe Photoshop 6.0 and Adobe Illustrator 9.01 (Adobe Systems Incorporated, 2000, USA).


#### 2.4.5. Mechanical Tests

Mechanical tensile tests were performed by following information reported in the ASTM D638. Samples were cut from sheets using a dog-bone die and tested using a 1.0 mm/min load rate and a load cell of 200 N.


### 2.5. In Vitro Release of TA from the PU-NC and PU Implants

The United States Pharmacopeia [26] states in the general chapter 〈1092〉 the dissolution procedure: “sink conditions are defined as the volume of medium at least three times that required to form a saturated solution of drug substance. When sink conditions are present, it is more likely that dissolution results will reflect the properties of the dosage form”.Thein vitrorelease of TA was carried out under sink conditions during 8 months. As the aqueous solubility of TA is 21.0 μg/mL at 28°C [27], sink conditions were achieved with at least 181 mL for the evaluated polymeric implants.The TA PU-NC and TA PU implants were placed in different Erlenmeyers containing 181 mL of phosphate buffer solution (PBS pH = 7.4)(n=5). These Erlenmeyers were placed inside an incubator set at 37°C and 30 rpm. At predetermined intervals, 181 mL of the PBS was sampled and the same volume of fresh PBS was added to each tube. The amount of TA released from each PU-NC and PU implants was assayed by high performance liquid chromatographic method described above, and expressed as the cumulative percentage of TA released in the medium. The average of the obtained measurements was calculated and used to plot the release profile curve.The TA released from PU-NC and PU implants was measured by high-performance liquid chromatography (HPLC) by a Hewlett Packard HP 1100 apparatus equipped with an autosampler model HP 1100. An HP 1100 pump was set at a constant flow rate of 1.2 mL/min. A C-18 reversed-phase column (4.6 mm × 250 mm, macropore size of 5μm) (Chromolith RP-18E, Merck KGaA Performance & Life Science Chemicals, Germany) was also used. The mobile phase was a mixture of acetonitrile (EM Science, Merck KGaA, Germany) and ultrafiltrated water obtained from Milli Q Plus, Millipore (USA) (50 : 50). An HP 1100 ultraviolet detector was used at a wavelength of 242 nm. The HPLC method was previously validated, and demonstrated to be specific, linear, precise and accurate as well as simple and reliable.


### 2.6. In Vivo Release of TA from the PU-NC and PU Implants

Six-to-eight-week-old female Swiss mice from the Centro de Bioterismo of the Federal University of Minas Gerais (UFMG) were maintained in individual cages, with food and waterad libitum, and controlled temperature and humidity in the animal house of the School of Pharmacy of the Federal University of São João Del Rei (UFSJ). Experiments were approved by the Ethics Committee in Animal Experimentation at UFSJ.The animals were anesthetized with a mixture of (10 mg kg−1) xylazine and (100 mg kg−1) ketamine hydrochloride (i.p.). Their dorsal hair was shaved and the skin wiped with 70% ethanol. TA PU-NC and TA PU implants were incorporated into the sponge discs, and they were aseptically inserted into a subcutaneous pouch that had been made with curved artery forceps through a 1cm long dorsal mid-line incision. After the implantation procedure, the animals were maintained in individual cages and provided with chow pellets and water ad libitum. The light/dark cycle was 12 : 12 h with lights on at 7:00 am and lights off at 7:00 pm. Postoperatively, the animals were monitored for any signs of infection at the operative site, or upon discomfort or distress; any mice presenting such signs were immediately sacrificed.TA PU-NC and TA PU implants were inserted into a subcutaneous pouch of the mice as described above. At 4, 7, 15, and 30 days after implantation, animals (n=5 for each time) were euthanized, and the TA PU-NC and TA PU implants were carefully removed. The implant was fragmented using a scissor, and the pieces were dissolved in 50 mL of a mixture of acetonitrile and ultrafiltrated water (1:1). The content of TA remaining in the PU-NC and PU implants was measured by HPLC method previously described.


## 2.1. Synthesis of the Aqueous Polyurethane Dispersion (PU)

Aqueous polyurethane dispersion (PU) was prepared by a prepolymer mixing process, using a 250 mL three-neck glass flask equipped with a heating mantel, a mechanical stirrer, and a thermometer. The macrodiol components-polycaprolactone—diol (PCL 1000) (Tone Polyol 2221,M̅n=1000 g·mol−1), polycaprolactone-diol (PCL 2000) (Tone Polyol 0249, M̅n=2000 g·mol−1) (Dow-USA) (Sigma-Aldrich), and poly(ethylene glycol) (PEG, Mn=1500 g·mol−1, Sigma-Aldrich), isophorone diisocyanate (IPDI) (Bayer-Brazil) (NCO/OH ratio of 2.3) and 2,2-bis(hydroxymethyl) propionic acid (DMPA) (98.3%, Fluka) were added to the reactor in the presence of dibutyl tin dilaurate (DBDLT) (Miracema Nuodex-Brazil) and the reaction was carried out at 70°C–75°C in a nitrogen atmosphere for 4 h. The amount of free NCO groups on a percentage basis was determined by the standard di-butyl amine back titration method. After titration, the prepolymer temperature was allowed to drop to 40°C. The carboxylic acid groups were neutralized by the addition of triethylamine (TEA) (98%, Vetec-Brazil). The mixture was stirred for another 40 min to ensure that the reaction had been completed. All samples were dispersed by adding deionized water to the neutralized prepolymer which was stirred vigorously. After the dispersion, the amount of hydrazine (HZ) (solution 64%, Arch Química-Brazil) enough to react with free NCO groups was added to the reactor with a small amount of water, and stirring was continued for another 30 min. This chemical procedure was successful in producing a polyurethane dispersion with a solid content of about 25%. The composition of the polyurethane dispersion is shown in Table 1. Films were produced by casting the dispersion in a Teflon mould and allowing them to dry at room temperature for one week. Afterwards the films were placed in an oven at 60°C for 24 h [24]. A schematic representation of the chemical reactions and processing steps used to produce the polyurethane dispersion and nanocomposites is shown in Figure 1.Table 1
Composition (wt.%) of the aqueous PU dispersion*.
ReagentsConcentration (wt.%)Isophorone diisocyanate (IPDI)8.58Polycaprolactone-diol 1000 (PCL1000)4.85Polycaprolactone-diol 2000 (PCL2000)9.09Polyethylene glycol 1500 (PEG 1500)0.732,2-bis(hydroxymethyl) propionic acid (DMPA)0.97Triethylamine (TEA)0.73Water74.70Hydrazine (HZ)1.08*0.01% of dibutyl tin dilaurate based on the amounts of IPDI, PCL, and DMPA.Figure 1
Schematic representation of the process used to prepare polyurethane containing montmorillonite (MMT-Na+) and triamcinolone acetonide.


## 2.2. Incorporation of Clay Nanoparticles-Cloisite Na+

The montmorillonite clay without any treatment (Cloisite Na+, Southern Clay Products) was dispersed in water (5 wt.%) by stirring it for 24 hours at room temperature. This procedure is useful to reduce the average particle size of the clay particles to yield clay nanoparticles dispersed in water [25]. Clay nanoparticles were incorporated into the polyurethane aqueous dispersion by mixing the polymer with the aqueous dispersion of the clay (Figure 1). The dispersions were mixed in proportions to yield a final nanocomposite containing 5 wt.% of clay in the polyurethane.


## 2.3. Incorporation of Triamcinolone Acetonide and Preparation of the Implants

Triamcinolone acetonide (TA) (Sigma-Aldrich, 99.0%) was incorporated into the polymer by dispersing it in the nanocomposite prior of casting the films to yield materials having 20.5 wt% of the drug (Figure1). The dried films were cut into squares (5 mm in side) to obtain the triamcinolone acetonide-loaded polyurethane nanocomposite implants (TA PU-NC implants) having approximately 1.27 mg each one. Triamcinolone acetonide-loaded polyurethane implants (without clay particles) (TA PU implants) were also prepared.


## 2.4. Characterization

### 2.4.1. Fourier Transform Infrared

Infrared spectra were collected in a Fourier transform infrared spectrophotometer (FTIR; Perkin Elmer, model Spectrum 1000). Measurements were carried out using the attenuated total reflectance (ATR) technique. Each spectrum was a result of 32 scans with a resolution of 4 cm−1.


### 2.4.2. Small Angle X-Ray Scattering

The measurements of synchrotron small angle X-ray scattering (SAXS) were performed using the beam line of the national synchrotron light laboratory (LNLS, Campinas, Brazil). The photon beam used in the LNLS SAXS beamline comes from one of the 12 bending magnets of the electron storage ring. The white photon beam is extracted from the ring through a high-vacuum path. After passing through a thin beryllium window, the beam is monochromatized (λ = 1.608 Å) and horizontally focused by a cylindrically bent and asymmetrically cut silicon single crystal. The focus is located at the detection plane. The X-ray scattering intensity, I(q), was experimentally determined as a function of the scattering vector “q” whose modulus is given by q=(4π/λ)sin(θ), where λ is the X-ray wavelength and θ being half the scattering angle. Each SAXS pattern corresponds to a data collection time of 900 s. From the experimental scattering intensity produced by all the studied samples, the parasitic scattering intensity produced by the collimating slits was subtracted. All SAXS patterns were corrected for the nonconstant sensitivity of the PSD, for the time varying intensity of the direct synchrotron beam and for differences in sample thickness. Because of the normalization procedure, the SAXS intensity was determined for all samples in the same arbitrary units so that they can be directly compared.


### 2.4.3. Wide Angle X-Ray Scattering

Wide angle X-ray scattering (WAXS) was performed by using a synchrotron light beam with a wavelength of 1.608 Å and an exposition time of 300 s. The scattering intensity was recorded by a Pilatus (100 K, 33 mm × 84 mm) detector. The sample to detector distance used was 80 mm.


### 2.4.4. Scanning Electron Microscopy

Scanning electron microscopy (SEM) was performed using a JEOL microscope (model JSM-6360LV) operating at 15 kV. The TA PU implants were cryofractured and mounted on aluminium stubs using double-sided adhesive tape. Prior to microscopic examination, all the samples were sputter-coated with a gold layer under argon atmosphere using a sputter apparatus (Balzers Union SCD 040 unit, Balzers, Germany). The implants surfaces were viewed at 1000–10000x magnification, and the images were transferred to the computer by means of a digital image transference interface (DITI). The photomicrographs were adjusted using the software Adobe Photoshop 6.0 and Adobe Illustrator 9.01 (Adobe Systems Incorporated, 2000, USA).


### 2.4.5. Mechanical Tests

Mechanical tensile tests were performed by following information reported in the ASTM D638. Samples were cut from sheets using a dog-bone die and tested using a 1.0 mm/min load rate and a load cell of 200 N.


## 2.4.1. Fourier Transform Infrared

Infrared spectra were collected in a Fourier transform infrared spectrophotometer (FTIR; Perkin Elmer, model Spectrum 1000). Measurements were carried out using the attenuated total reflectance (ATR) technique. Each spectrum was a result of 32 scans with a resolution of 4 cm−1.


## 2.4.2. Small Angle X-Ray Scattering

The measurements of synchrotron small angle X-ray scattering (SAXS) were performed using the beam line of the national synchrotron light laboratory (LNLS, Campinas, Brazil). The photon beam used in the LNLS SAXS beamline comes from one of the 12 bending magnets of the electron storage ring. The white photon beam is extracted from the ring through a high-vacuum path. After passing through a thin beryllium window, the beam is monochromatized (λ = 1.608 Å) and horizontally focused by a cylindrically bent and asymmetrically cut silicon single crystal. The focus is located at the detection plane. The X-ray scattering intensity, I(q), was experimentally determined as a function of the scattering vector “q” whose modulus is given by q=(4π/λ)sin(θ), where λ is the X-ray wavelength and θ being half the scattering angle. Each SAXS pattern corresponds to a data collection time of 900 s. From the experimental scattering intensity produced by all the studied samples, the parasitic scattering intensity produced by the collimating slits was subtracted. All SAXS patterns were corrected for the nonconstant sensitivity of the PSD, for the time varying intensity of the direct synchrotron beam and for differences in sample thickness. Because of the normalization procedure, the SAXS intensity was determined for all samples in the same arbitrary units so that they can be directly compared.


## 2.4.3. Wide Angle X-Ray Scattering

Wide angle X-ray scattering (WAXS) was performed by using a synchrotron light beam with a wavelength of 1.608 Å and an exposition time of 300 s. The scattering intensity was recorded by a Pilatus (100 K, 33 mm × 84 mm) detector. The sample to detector distance used was 80 mm.


## 2.4.4. Scanning Electron Microscopy

Scanning electron microscopy (SEM) was performed using a JEOL microscope (model JSM-6360LV) operating at 15 kV. The TA PU implants were cryofractured and mounted on aluminium stubs using double-sided adhesive tape. Prior to microscopic examination, all the samples were sputter-coated with a gold layer under argon atmosphere using a sputter apparatus (Balzers Union SCD 040 unit, Balzers, Germany). The implants surfaces were viewed at 1000–10000x magnification, and the images were transferred to the computer by means of a digital image transference interface (DITI). The photomicrographs were adjusted using the software Adobe Photoshop 6.0 and Adobe Illustrator 9.01 (Adobe Systems Incorporated, 2000, USA).


## 2.4.5. Mechanical Tests

Mechanical tensile tests were performed by following information reported in the ASTM D638. Samples were cut from sheets using a dog-bone die and tested using a 1.0 mm/min load rate and a load cell of 200 N.


## 2.5. In Vitro Release of TA from the PU-NC and PU Implants

The United States Pharmacopeia [26] states in the general chapter 〈1092〉 the dissolution procedure: “sink conditions are defined as the volume of medium at least three times that required to form a saturated solution of drug substance. When sink conditions are present, it is more likely that dissolution results will reflect the properties of the dosage form”.Thein vitrorelease of TA was carried out under sink conditions during 8 months. As the aqueous solubility of TA is 21.0 μg/mL at 28°C [27], sink conditions were achieved with at least 181 mL for the evaluated polymeric implants.The TA PU-NC and TA PU implants were placed in different Erlenmeyers containing 181 mL of phosphate buffer solution (PBS pH = 7.4)(n=5). These Erlenmeyers were placed inside an incubator set at 37°C and 30 rpm. At predetermined intervals, 181 mL of the PBS was sampled and the same volume of fresh PBS was added to each tube. The amount of TA released from each PU-NC and PU implants was assayed by high performance liquid chromatographic method described above, and expressed as the cumulative percentage of TA released in the medium. The average of the obtained measurements was calculated and used to plot the release profile curve.The TA released from PU-NC and PU implants was measured by high-performance liquid chromatography (HPLC) by a Hewlett Packard HP 1100 apparatus equipped with an autosampler model HP 1100. An HP 1100 pump was set at a constant flow rate of 1.2 mL/min. A C-18 reversed-phase column (4.6 mm × 250 mm, macropore size of 5μm) (Chromolith RP-18E, Merck KGaA Performance & Life Science Chemicals, Germany) was also used. The mobile phase was a mixture of acetonitrile (EM Science, Merck KGaA, Germany) and ultrafiltrated water obtained from Milli Q Plus, Millipore (USA) (50 : 50). An HP 1100 ultraviolet detector was used at a wavelength of 242 nm. The HPLC method was previously validated, and demonstrated to be specific, linear, precise and accurate as well as simple and reliable.


## 2.6. In Vivo Release of TA from the PU-NC and PU Implants

Six-to-eight-week-old female Swiss mice from the Centro de Bioterismo of the Federal University of Minas Gerais (UFMG) were maintained in individual cages, with food and waterad libitum, and controlled temperature and humidity in the animal house of the School of Pharmacy of the Federal University of São João Del Rei (UFSJ). Experiments were approved by the Ethics Committee in Animal Experimentation at UFSJ.The animals were anesthetized with a mixture of (10 mg kg−1) xylazine and (100 mg kg−1) ketamine hydrochloride (i.p.). Their dorsal hair was shaved and the skin wiped with 70% ethanol. TA PU-NC and TA PU implants were incorporated into the sponge discs, and they were aseptically inserted into a subcutaneous pouch that had been made with curved artery forceps through a 1cm long dorsal mid-line incision. After the implantation procedure, the animals were maintained in individual cages and provided with chow pellets and water ad libitum. The light/dark cycle was 12 : 12 h with lights on at 7:00 am and lights off at 7:00 pm. Postoperatively, the animals were monitored for any signs of infection at the operative site, or upon discomfort or distress; any mice presenting such signs were immediately sacrificed.TA PU-NC and TA PU implants were inserted into a subcutaneous pouch of the mice as described above. At 4, 7, 15, and 30 days after implantation, animals (n=5 for each time) were euthanized, and the TA PU-NC and TA PU implants were carefully removed. The implant was fragmented using a scissor, and the pieces were dissolved in 50 mL of a mixture of acetonitrile and ultrafiltrated water (1:1). The content of TA remaining in the PU-NC and PU implants was measured by HPLC method previously described.


## 3. Results and Discussion

The incorporation of clay nanoparticles into the polymer matrix affected the mechanical properties of the polymer as initially predicted. Clay nanoparticles improved the elastic modulus of the polymer approximately two and a half times when compared to the pure polymer, as indicated in Table2. Therefore, clay particles could be used to tune the stiffness of the PU, avoiding the necessity of changing some of the parameters of the PU synthesis, such as the ratio between soft and hard segments. The adjustment of the stiffness of the nanocomposite is an attractive characteristic for designing biomedical scaffolds and implantable solid systems [13], since stiff needle-shaped implants can be easily inserted through soft tissues without the need of a special incision. The reduction in both the strength and strain failure rates is a consequence of the interactions between the clay and polymer chains that restrict chain mobility.Table 2
Mechanical properties of PU and PU-NC films.
Elastic modulus (MPa)Strength (MPa)Strain at failure (%)PU12533944PU-NC33325503Figure2 shows the infrared spectra of pure PU (Figure 2(a)), PU-NC (containing clay) (Figure 2(b)), TA PU implants (Figure 2(c)), TA PU-NC implants (Figure 2(d)), pure TA (Figure 2(e)), and pure montmorillonite (Figure 2(f)). Characteristic infrared bands observed in pure PU include 2945–2866 cm−1 related to the stretching vibration of –CH2 groups and 1723–1600 cm−1 equivalent to the stretching vibration of free and hydrogen-bonded carbonyl in the urethane, urea, and ester bonds in the poly(caprolactone) segments. The hydrogen bonded carbonyl in the urethane and urea (in the hard segment) and ester bonds in poly(caprolactone) (in the soft segment) could interact not only with the polar surface of the clay nanoparticles to yield a higher degree of hydrogen bonded species, but also with the primary amine present in the molecular structure of the polyurethane. The absorption band that resulted from stretching vibrations of bonded primary amine was observed in 3333 cm−1, confirming the existence of interaction between the hydrogen of the primary amine and carbonyl in the urethane, urea, and ester groups. However, an absorption infrared band at 1531 cm−1 was also identified corresponding to bending vibrations of nonbonded primary amine. An absorption band around 2270 cm−1 was not observed in spectra, which indicated the absence of nonreactive NCO groups [28]. If this type of chemical group was present, the occurrence of side reactions which leads to the formation of allophanate or biuret linkages would be possible [29]. The same infrared bands observed in pure PU were identified in spectra of PU-NC (Figure 2(b)), TA PU implants (Figure 2(c)) and TA PU-NC implants (Figure 2(d)).Figure 2
FTIR spectra of pure PU (a), PU-NC (containing clay) (b), TA PU implants (c), TA PU-NC implants (d), pure TA, (e) and pure montmorillonite (f).The infrared spectra of pure clay (Figure2(f)) revealed a weak infrared band at 3600 cm−1 due to the –OH band stretch in Al-OH and Si-OH, and an intense absorption band at approximately 1040 cm−1 due to Si-O stretching (out-of-plane) and Si-O stretching (in-plane) vibration in layered silicates [30, 31]. The infrared band corresponding to Si-O bonds is also observed in the spectra of PU-NC and TA PU-NC implants (Figures 2(b) and 2(d)), but the intensity is lower than that present in the spectra of pure clay. It is suggested that the intensity change in the Si-O stretching vibration band is related to the low concentration of clay in polyurethane, the weakening of interactions between interlayer water molecules and surface oxygen [32], and also due to the intercalation of the polyurethane and/or TA between clay lamellas.Typical absorption bands observed in pure TA (Figure2(e)) can be visualized in the spectra of TA PU (Figure 2(c)) and TA PU-NC implants (Figure 2(d)), such as 3392 cm−1 corresponding to the hydroxyl groups, between 3000–2900 cm−1 related to C–H stretching of sp3 and sp2 carbons, 1700–1730 cm−1 and 1662 cm−1 due to carbonyl groups of aliphatic ester and ketone. The obtained FTIR results corroborated with those previously reported [33]. The maintenance of the characteristic infrared bands of the PU, PU-NC, and TA, as well as the absence of new bands, demonstrated that there was no detectable chemical interaction between the polymer and drug during the manufacture process of the implants and indicated that the drug was successfully incorporated into the polyurethane-nanocomposite.Figure3 shows wide-angle x-ray scattering (WAXS) of pure PU (Figure 3(a)), PU-NC (containing clay) (Figure 3(b)), TA PU implants (Figure 3(c)), TA PU-NC implants (Figure 3(d)), and pure TA (Figure 3(e)). The WAXS curve of the pure PU (Figure 3(a)) revealed that no defined scattering peaks can be noted as a consequence of the presence of a highly amorphous structure. Crystallization of poly(caprolactone) segments is restricted, having low molar mass (<2000 g/mol) in polyurethanes, since low molar mass oligomers are confined between hard domains that do not allow them to have regular conformations that can lead to crystallization [34]. The WAXS curve recorded for PU containing clay nanoparticles (Figure 3(b)) revealed also an amorphous pattern of the nanocomposite. According to Kiersnowski et al. [35], the WAXS curve of montmorillonite reveals diffraction peaks related to the crystalline structure of this clay. By contrast, WAXS data obtained for PU-NC did not show diffraction peaks, suggesting the disruption of the regular layered structure of the montmorillonite are due to the delamination of the clay incorporated into the polymer. The presence of poly(ethylene glycol) segments within the polyurethane macromolecular architecture was useful in promoting complete exfoliation of the clay structure, since the hydrophilic poly(ethylene glycol) possibly interacted efficiently with the polar clay surface to restrict clay nanoparticles to pack again during drying of the aqueous dispersion [36]. Typical scattering peaks observed in pure TA (Figure 3(e)) can be visualized in the WAXS curves of TA PU (Figure 3(c)) and TA PU-NC implants (Figure 3(d)), demonstrating the preserved crystalline pattern of the drug. However, the incorporation of clay nanoparticles and drug into the polyurethane led to a small shift of the diffraction peaks of TA to lower angles. This shift in q values suggested interactions between drug and clay nanoparticles due to the diffusion of the TA into the clay sheets and crystallization within the clay lamella, leading to the enlargement of the distance between crystalline planes of the drug. The interactions between silicate layers and guest molecules, such as nonionic TA, are weak interaction bonds represented by hydrogen bonding and hydrophobic interactions (Van der Walls). Complexes with montmorillonite and anionic or other nonionic drugs also exhibited bonding via absorption due to the establishment of weak interaction bonds [37]. On the other hand, McGinity and Lach [38] confirmed that basic molecules bonded strongly with montmorillonite, since clay minerals are naturally inorganic cationic exchangers and they may undergo ion exchange with basic drugs.Figure 3
WAXS curves of pure PU (a), PU-NC (containing clay) (b), TA PU implants (c), TA PU-NC implants (d), and pure TA (e).Small angle X-ray scattering (SAXS) has been used to characterize the morphology of nanoscaled phase-separated materials, such as polymer nanocomposites, block copolymers, and segmented polymers, since this technique records electron density fluctuations throughout the material in a nanometer range [39, 40]. SAXS provides useful data to study segmental polymers such as polyurethanes, since this type of polymer often phase separate in hard and soft domains that have enough electronic contrast to affect X-ray scattering at low angles. Nanocomposites containing clay has also been investigated by SAXS [41, 42] to show the degree of clay delamination and nanoparticle orientation within the polymer.Figure4 shows SAXS data for PU-based materials that comprise nanoparticles derived from clay and TA. SAXS data in Figure 4 was reformatted using the Lorentz correction (I(q)q2), that is, useful to enhance the resolution of small SAXS peaks. No scattering peak can be clearly seen in SAXS curve associated with the pure PU (Figure 4(a)) even after the Lorentz correction, indicating the low electron difference between segments of the polyurethane. Considering the fact that this polyurethane is based on poly(caprolactone) and poly(ethylene glycol), as soft segments, and urethane hard segments, the hydrophilic domains were able to chemically interact by means of hydrogen bonds, producing a more homogeneous structure with possibly very small domains with no major differences in electron density. The incorporation of TA into the polymer did not lead to major changes in the scattering profile (Figure 4(c)). Therefore, the presence of TA did not alter the original structure of pure PU. Otherwise, an increase in scattering (mainly for lower values of q) was observed when clay nanoparticles were introduced into PU (Figure 4(b)) as an evidence of the presence of these nanoentities that have a higher electron density than the pure polymer. It was demonstrated previously [43] that clay nanoparticles can interact with hard segments of polyurethane through the formation of hydrogen bonds to change the course of the phase separation process. Additionally, the polar clay surface can also interact with the poly(ethylene glycol)-based soft segments of the polymer, changing the morphology of the polyurethane. The level of scattering was even more enhanced when TA was also incorporated into PU together with clay nanoparticles (Figure 4(d)). This result may indicate that interactions between the drug and clay may have created a larger number of scattering sites within the polymer. The interactions between silicate layers and TA, accommodated in their gallery spaces, might be hydrophobic interactions (Van der Walls) and hydrogen bonding, since the drug was absorbed in the clay mainly in the neutral form [37].Figure 4
Lorentz corrected SAXS scattering data of pure PU (a), PU-NC (containing clay) (b), TA PU implants (c), TA PU-NC implants (d), and pure TA (e).Scanning electron microscopy (SEM) was used for examination of the fractured surfaces of pure PU (Figure5(a)), PU-NC (containing clay) (Figure 5(b)), TA PU implants (Figure 5(c)), and TA PU-NC implants (Figure 5(d)). The cross-sectional area of the pure PU was smooth and dense, with no evidence of pores or channels. On the other hand, the PU-NC surface was completely rough due to the homogeneous distribution of the clay nanoparticles in the polymer surface. This could be attributed to the chemical interactions between the polar clay surface and polar urethane bonds and/or poly(ethylene glycol) present in the segments of the polyurethane. The cross-sectional area of the TA PU-NC implants was also rough due to the presence of the clay nanoparticles and TA crystals not only in the PU matrix, but also on the clay sheets. Since no large clay and TA aggregates could be observed on the fractured surface of the samples, it can be suggested that the manufacture procedure of the implants yielded a high-quality polyurethane nanocomposite loaded with small crystals of the drug.SEM images of pure PU (a), PU-NC (containing clay) (b), TA PU implants (c), and TA PU-NC implants (d).
(a)(b)(c)(d)Figure6 shows the percentage of the cumulative TA release profile from PU implants (Figure 6(a)) and PU-NC implants (Figure 6(b)). The TA leached from the implantable devices was quantified by HPLC method. Neither any peak for a degradation product nor any alteration of the chromatographic pattern of TA was observed, indicating that the preparation technique of the PU and PU-NC implants and the conditions of the in vitro release of the drug did not affect the stability of the drug. TA PU and TA PU-NC implants led to a controlled release of the drug which followed a bimodal pattern: during the first 15 days, a faster dissolution and diffusion of the drug was released corresponding to a minimal burst effect. Over this period, approximately 16% and 24% of TA was released from PU-NC and PU implants, respectively, corresponding to the leaching of TA crystals deposited in the implant surfaces. In the second stage, approximately 93% and 85% of TA was released from the PU and PU-NC implants. It suggests that this phase was characterized by the diffusion of the drug and the degradation of the polymeric matrix. The presence of poly(ethylene glycol) in the soft segments of the polyurethane increased hydrophilicity and aqueous permeability in the polymer backbone, promoting hydrolytic cleavage of ester bonds of the poly(caprolactone) also present in the soft segments of the polyurethane. Furthermore, the scission of the poly(caprolactone) increased the porosity and surface area for drug diffusion [44]. In terms of the bonds present in poly(ester urethanes), the most susceptible to hydrolysis are ester bonds. However, the hydrolysis of ester bonds of urethane groups in one order of magnitude is slower relative to ester bonds of the soft segment. Therefore, the soft segment bonds hydrolyze at a greater rate than hard segment bonds and govern the degradation rate of the poly(ester urethanes) [45].Figure 6
Cumulative TA release profile from PU implants (a) and PU-NC implants (b). Results represent mean ± standard deviation (n=5 for each time and each sample).The incorporation of montmorillonite particles into the polymeric matrix loaded with the drug reduced the rate of TA release over the time. This may be due to the establishment of different types of host-guest interactions between clay nanoparticles and TA intercalated into montmorillonite (as detected by WAXS and SAXS). Besides the interactions between them being weak interaction bonds, they contributed to a more extensive release of the drug from the PU-NC implants.Figure7 shows the percentage of the cumulative TA release profile from PU implants (Figure 7(a)) and PU-NC implants (Figure 7(b)). The TA-loaded PU and PU-NC implants maintained a sustained release of the drug for at least 30 days within the subcutaneous tissue of the mice. The PU and PU-NC implants showed an initial burst release of the drug over the first 7 days. Over this period, approximately 36% and 27% of TA was released from PU and PU-NC implants, indicating faster dissolution of the drug deposited on the surface of the polymeric implants. In a second stage that occurred between the 8th and the 30th days of the test, the PU and PU-NC implants released 80% and 73% of TA, respectively, providing controlled and sustained TA release within the subcutaneous tissue of the mice. During this period, the dissolution and diffusion of the drug and the degradation of the polymeric matrix might modulate the TA release rate. It was previously described that the in vivodegradation of polyurethanes involves the hydrolysis of ester linkages in polyester soft segments, and the enzymatic hydrolysis by the presence of esterases, since those enzymes are able to recognize and act upon unnatural substrates such as polyurethanes [46]. Additionally, the overall rate of TA released from the PU-NC implants was lower than that obtained for the PU implants. Therefore, the intercalation capability offered by the montmorillonite particles was applied to decrease the release of the TA, providing a prolonged delivery of the drug over the time in comparison with the free polymer. This can be relevant for long-term treatment of chronic inflammatory pathologies.Figure 7
Cumulative TA release profile from PU (a) and PU-NC (b) subcutaneous implants in mice. Sustained release of TA was observed up to day 30 after implantation. Results represent mean ± standard deviation (n=5 for each time and each sample).It was observed that approximately 31% of TA was released from PU-NC implantsin vitro and 73% of drug was delivered by PU-NC implants in vivo during 30 days. The differences between the physiological environment (in vivotest) and the simulated physiological conditions (in vitrotest) explain the lack of correlation between the in vivoand in vitroprofile release of TA from PU-NC implants.


## 4. Conclusion

In the present work, the montmorillonite without any treatment could be intercalated within the polymer chains due to the use of aqueous polyurethane dispersion to produce the nanocomposite. The triamcinolone acetonide, an important corticoid, was incorporated into the nanocomposite by dispersing it in the waterborne polyurethane. Triamcinolone acetonide-loaded polyurethane nanocomposite implants were successfully designed. The incorporation of nanocomposite into the polymer chains modulated the mechanical properties of the polymer system that became more attractive not only for designing implantable solid systems but also for biomedical scaffolds. FTIR and WAXS data showed that the incorporation of the drug into the nanocomposite did not severely change the chemical and crystallographic aspects of the drug respectively. SAXS data demonstrated that the introduction of the clay nanoparticles into the polyurethane provided no major modifications of the morphology of the polymer. However, this technique provided some evidences that clay can interact with the drug.In vitro and in vivotriamcinolone acetonide release studies showed that the drug was released slower from the nanocomposite compared to the pure polyurethane, as a result of the interaction between the montmorillonite and the drug present in the interlayer spacing of the host clay. Therefore, the incorporation of montmorillonite nanoparticles into the biodegradable polyurethane chains was useful not only to tune the mechanical properties of the polymer but also to provide controlled long-term delivery of the drug over the time. The treatment of chronic inflammatory diseases by montmorillonite clay-based polyurethane implants seems feasible.



---

*Source: 528628-2011-10-04.xml*