# Simple Cocasting Method to Prepare Magnetic Mesoporous FePt/C Composites and Their Protein Adsorption Property

Authors: Yufang Zhu; Xing He
Journal: Journal of Chemistry
 (2013)

---

## Abstract

A simple cocasting method has been developed to prepare magnetic mesoporous FePt/C composites with superparamagnetic FePt nanoparticles embedded in carbon walls. Furfuryl alcohol, iron(III) acetylacetonate (Fe(acac)3), and platinum(II) acetylacetonate (Pt(acac)2) were used as the carbon and FePt nanoparticle precursors to be simultaneously incorporated into the channels of mesoporous silica SBA-15 template by the incipient wetness impregnation technique. After the polymerization of furfuryl alcohol, the carbonization in argon, and the removal of silica template, magnetic mesoporous FePt/C composites were finally obtained. Magnetic mesoporous FePt/C composites have high surface area of 1244 m2/g and narrow mesopore size distribution peaked at 4.93 nm. FePt nanoparticles were well embedded in mesoporous carbon walls, and mesoporous FePt/C composites exhibit superparamagnetic behavior. Using cytochrome c (Cyt c), myoglobin (Mb), and bovine serum albumin (BSA) as model proteins, the adsorption capacities of Cyt c, Mb, and BSA on magnetic mesoporous FePt/C composites can reach ca. 200, 162, and 121 μg/mg, respectively. These results indicated that mesoporous FePt/C composites have potential as magnetically separable adsorbent for biomolecules separation.


---

## Body

## 1. Introduction

Ordered mesoporous carbon (OMC) materials are of great interest due to their uniform pore structure, high surface area, thermal stability, electrical conductivity, chemical inertness, biocompatibility, and specific surface properties [1, 2]. To date, OMC materials have been widely investigated in various applications, such as adsorption, separation, catalysis, energy storage, and biomedical engineering [3–7]. For example, in medical and food industries, OMC materials could be used as the adsorbents to remove adsorbed proteins from the products solutions; those may give rise to the subsequent adsorption of fibrous proteins leading to adverse biological consequences [8, 9]. However, mesoporous carbons are notoriously difficult to separate from solutions, especially for mesoporous carbons with small particle sizes, which cause some problems in practical applications.Compared to the conventional and complex filtration/centrifugation procedure, magnetic separation as a promising strategy has been widely accepted due to the fact that it can be easily separated under an applied magnetic field [10, 11]. Therefore, many efforts have been made to prepare magnetically separable OMC materials using different approaches recently. One route is the “one-pot” block-copolymer self-assembly strategy associated with a direct carbonization process. For example, Zhai et al. fabricated OMC materials with magnetic frameworks (mesoporous γ-Fe2O3/C composites) by the self-assembly strategy from resol, ferric citrate, and triblock copolymer F127 [12]. Kang et al. reported one-pot simple synthesis of FePt nanoparticles inside order mesoporous aluminosilicate/carbon composites by using polyisoprene-block-poly(ethylene oxide) (PI-b-PEO) as a structure-directing agent [13]. However, it is relatively difficult to obtain OMC materials via a surfactant templating strategy owning to the complexity of the carbon-structure evolution, and only several reports are available until now [14–16].To date, the most effective and popular route to magnetic mesoporous carbon composites is nanocasting strategy by infiltration of an appropriate carbon precursor and metal source into the channels of mesoporous silica, followed by polymerization, carbonization, and subsequent removal of the silica framework [17–22]. For example, Lu et al. prepared cobalt nanoparticles deposited on CMK-3 (Co-OMC) and successfully applied mesoporous carbon to magnetically separable adsorbent and hydrogenation catalyst supports [17]. But the synthetic procedure for Co-OMC is rather complex, which hampers broad application of the magnetic mesoporous carbon composites, despite its many important characteristics. Wang et al. impregnated simultaneously furfuryl alcohol and metal nitrates (carbon and magnetic particle precursors) into mesoporous silica SBA-15, followed by polymerization, carbonization, and the removal of silica framework to obtain magnetic mesoporous FeNi/C composites [18].However, in some as-synthesized magnetic OMC materials, magnetic nanoparticles, for example, Fe3O4, γ-Fe2O3, Ni, are easily subject to oxidation in air or dissolution in acid if no effort has been made to protect magnetic nanoparticles by a carbon-layer coating or embedding in carbon walls. It is well known that FePt nanoparticles have superparamagnetic property and high chemical resistance against acid or oxygen attack [23], which are suitable for adsorption/separation applications. Gupta et al. and Kockrick et al. reported the formation of FePt nanoparticles in mesoporous silica by using the wetness impregnation technique [24, 25]. Our group has developed a nanocasting route to prepare magnetic OMC materials with FePt nanoparticles, involving the polymerization of the impregnated furfuryl alcohol in the channels of mesoporous silica KIT-6, the repeated wetness impregnation of FePt precursors (Fe(acac)3 and Pt(acac)2), the carbonization in argon, and the removal of mesoporous silica templates [26]. Obviously, the repeated wetness impregnation of FePt precursors is a time-consuming process, and it is also difficult to control the uniform distribution of FePt nanoparticles in the whole OMC particles.In this work, we developed a simple cocasting method to simplify the nanocasting procedure for the preparation of magnetic mesoporous FePt/C composites using mesoporous silica SBA-15 as hard template. Furfuryl alcohol, Fe(acac)3, and Pt(acac)2 were simultaneously incorporated into SBA-15 by the wetness impregnation technique, following the polymerization of furfuryl alcohol, the carbonization in argon, and the removal of silica template, magnetic mesoporous FePt/C composites were obtained. This cocasting method makes the procedure simple and saves the preparation time. Furthermore, using Cyt c, Mb, and BSA as model proteins, the adsorption properties of magnetic mesoporous FePt/C composites were also investigated.


## 2. Experimental

### 2.1. Synthesis of Mesoporous Silica SBA-15

Mesoporous silica SBA-15 was prepared following a previously reported method [27]. 4.0 g of P123 (EO20PO70EO20) was added to a mixture of 30 g of H2O and 120 g of 2 M HCl aqueous solution in a Teflon-lined container, which was stirred at 35°C usually overnight. Then, 8.50 g of TEOS was added into this solution under vigorous stirring. After 5 min of stirring, the mixture was kept under static conditions at 35°C for 20 h, followed by 24 h at 100°C. The solid products were collected by filtration, washed with water, dried, and calcined at 550°C in air.


### 2.2. Preparation of Magnetic Mesoporous FePt/C Composites

Magnetic mesoporous FePt/C composites were prepared using SBA-15 as hard template, furfuryl alcohol as carbon source, Fe(acac)3 (99.9%) and Pt(acac)2 (98%) as FePt sources. Typically, equimolar amounts (0.225 mmol) of Fe(acac)3 and Pt(acac)2 were dissolved in 4 mL of chloroform (CHCl3) to obtain the Fe(acac)3/Pt(acac)2/CHCl3 solution. Subsequently, 1.2 mL of Fe(acac)3/Pt(acac)2/CHCl3 solution, 1.2 mL of furfuryl alcohol, and a small quantity of oxalic acid were dissolved in 4 mL of ethanol under stirring to form a mixed solution. This mixed solution was incorporated into 1 g of SBA-15 by the wetness impregnation technique. After evaporating the ethanol and chloroform and polymerizing furfuryl alcohol at 100°C for 5 h and at 150°C for 2 h, the resulting composites were thermal treated in argon at 700°C to carbonize the polyfurfuryl alcohol and induce the formation of FePt nanoparticles. The silica templates in the composites were removed by twice washing with heated 2 M NaOH solution. The template-free mesoporous FePt/C composites were collected by filtering, washed with water and ethanol, and dried at 100°C.


### 2.3. Characterization

The wide angle X-ray diffraction (WAXRD) patterns were obtained on a Stoe Stadi P powder diffractometer equipped with a curved germanium (111) monochromator and linear PSD using Cu Kα1 radiation (1.5405 Å) in transmission geometry. The small angle X-ray diffraction (SAXRD) patterns were measured on a Bruker AXS Nanostar using CuKα1 radiation (1.5405 Å) and 105 cm of sample to detector distance. Scanning electron microscopy (SEM) was carried out with a Zeiss DMS 982 Gemini field emission scanning electron microscope. Transmission electron microscopy (TEM) was performed using a JEM-2000FX electron microscope operated at an acceleration voltage of 200 kV. N2 adsorption-desorption isotherms were obtained on a Nova 2000 pore analyzer at 77 K under continuous adsorption conditions. BET and BJH analyses were used to determine the surface area, pore size, and pore volume. UV/Vis adsorption measurements were recorded using a Shimadzu UV-2450 spectrophotometer. Magnetic measurement was carried out on a superconducting quantum interference device (SQUID) magnetometer at room temperature.


### 2.4. Adsorption of Proteins on Magnetic Mesoporous FePt/C Composites

A series of protein solutions (Cyt c, Mb, and BSA) with concentrations ranging from 0.05 mg/mL to 2 mg/mL were prepared by dissolving each protein in buffer solutions with different pH values (pH3.6~10.8). In a typical adsorption experiment, 20 mg of magnetic mesoporous FePt/C composites was suspended in 10 mL of protein solution in a closed vial, and the resulting mixture was shaken at 4°C and 120 rpm for 72 h to reach the equilibration of protein adsorption. The amount of protein adsorbed was calculated by subtracting the amount found in the supernatant liquid after adsorption from the amount of protein present before the addition of the adsorbent by UV analysis at a certain wavelength (Cyt c at 407 nm, Mb at 409 nm, and BSA at 279 nm, resp.). Calibration experiments were done separately before each set of measurements with protein solutions of different concentrations buffered at the same pH as the isotherm. Magnetic separation prior to the analysis was used to avoid potential interference from the suspended scattering particles in the UV-Vis analysis.


## 2.1. Synthesis of Mesoporous Silica SBA-15

Mesoporous silica SBA-15 was prepared following a previously reported method [27]. 4.0 g of P123 (EO20PO70EO20) was added to a mixture of 30 g of H2O and 120 g of 2 M HCl aqueous solution in a Teflon-lined container, which was stirred at 35°C usually overnight. Then, 8.50 g of TEOS was added into this solution under vigorous stirring. After 5 min of stirring, the mixture was kept under static conditions at 35°C for 20 h, followed by 24 h at 100°C. The solid products were collected by filtration, washed with water, dried, and calcined at 550°C in air.


## 2.2. Preparation of Magnetic Mesoporous FePt/C Composites

Magnetic mesoporous FePt/C composites were prepared using SBA-15 as hard template, furfuryl alcohol as carbon source, Fe(acac)3 (99.9%) and Pt(acac)2 (98%) as FePt sources. Typically, equimolar amounts (0.225 mmol) of Fe(acac)3 and Pt(acac)2 were dissolved in 4 mL of chloroform (CHCl3) to obtain the Fe(acac)3/Pt(acac)2/CHCl3 solution. Subsequently, 1.2 mL of Fe(acac)3/Pt(acac)2/CHCl3 solution, 1.2 mL of furfuryl alcohol, and a small quantity of oxalic acid were dissolved in 4 mL of ethanol under stirring to form a mixed solution. This mixed solution was incorporated into 1 g of SBA-15 by the wetness impregnation technique. After evaporating the ethanol and chloroform and polymerizing furfuryl alcohol at 100°C for 5 h and at 150°C for 2 h, the resulting composites were thermal treated in argon at 700°C to carbonize the polyfurfuryl alcohol and induce the formation of FePt nanoparticles. The silica templates in the composites were removed by twice washing with heated 2 M NaOH solution. The template-free mesoporous FePt/C composites were collected by filtering, washed with water and ethanol, and dried at 100°C.


## 2.3. Characterization

The wide angle X-ray diffraction (WAXRD) patterns were obtained on a Stoe Stadi P powder diffractometer equipped with a curved germanium (111) monochromator and linear PSD using Cu Kα1 radiation (1.5405 Å) in transmission geometry. The small angle X-ray diffraction (SAXRD) patterns were measured on a Bruker AXS Nanostar using CuKα1 radiation (1.5405 Å) and 105 cm of sample to detector distance. Scanning electron microscopy (SEM) was carried out with a Zeiss DMS 982 Gemini field emission scanning electron microscope. Transmission electron microscopy (TEM) was performed using a JEM-2000FX electron microscope operated at an acceleration voltage of 200 kV. N2 adsorption-desorption isotherms were obtained on a Nova 2000 pore analyzer at 77 K under continuous adsorption conditions. BET and BJH analyses were used to determine the surface area, pore size, and pore volume. UV/Vis adsorption measurements were recorded using a Shimadzu UV-2450 spectrophotometer. Magnetic measurement was carried out on a superconducting quantum interference device (SQUID) magnetometer at room temperature.


## 2.4. Adsorption of Proteins on Magnetic Mesoporous FePt/C Composites

A series of protein solutions (Cyt c, Mb, and BSA) with concentrations ranging from 0.05 mg/mL to 2 mg/mL were prepared by dissolving each protein in buffer solutions with different pH values (pH3.6~10.8). In a typical adsorption experiment, 20 mg of magnetic mesoporous FePt/C composites was suspended in 10 mL of protein solution in a closed vial, and the resulting mixture was shaken at 4°C and 120 rpm for 72 h to reach the equilibration of protein adsorption. The amount of protein adsorbed was calculated by subtracting the amount found in the supernatant liquid after adsorption from the amount of protein present before the addition of the adsorbent by UV analysis at a certain wavelength (Cyt c at 407 nm, Mb at 409 nm, and BSA at 279 nm, resp.). Calibration experiments were done separately before each set of measurements with protein solutions of different concentrations buffered at the same pH as the isotherm. Magnetic separation prior to the analysis was used to avoid potential interference from the suspended scattering particles in the UV-Vis analysis.


## 3. Results and Discussion

Figure1 illustrates the schematic procedure used in this work for the synthesis of magnetic mesoporous FePt/C composites. Firstly, after the calcination to remove the surfactant template from SBA-15, furfuryl alcohol, Fe(acac)3, Pt(acac)2, and a small quantity of oxalic acid were introduced into the mesoporous channels of SBA-15 by wetness impregnation technique. Subsequently, furfuryl alcohol was polymerized under the catalysis by oxalic acid to form polyfurfuryl alcohol. During polymerization of furfuryl alcohol, Fe(acac)3 and Pt(acac)2 were embedded in the framework of polyfurfuryl alcohol. Then, polyfurfuryl alcohol was carbonized under Ar atmosphere at 700°C to convert into compact carbon, and Fe(acac)3 and Pt(acac)2 were decomposed and in situ carbothermally reduced to magnetic alloy FePt nanoparticles accompanying the carbonization process. Finally, magnetic mesoporous FePt/C composites were obtained after the removal of silica template by hot 2 M NaOH aqueous solution.Figure 1
Schematic procedures for the synthesis of magnetic mesoporous FePt/C composites.Figure2 shows XRD patterns of magnetic mesoporous FePt/C composites. Magnetic mesoporous FePt/C composites exhibit three well-resolved reflections in the 2θ range between 1 and 2.5°, which can be indexed as (100), (110), and (200) reflections associated with hexagonal symmetry and confirmed the ordered mesoporous structure. The wide-angle XRD pattern of magnetic mesoporous FePt/C composites (in the inset of Figure 2) can be easily indexed to amorphous carbon and cubic FePt (JCPDS 29-0717) according to the reflection peak positions and relative intensities, suggesting that FePt has been formed by using carbonization of polyfurfuryl alcohol/SBA-15 containing Fe(acac)3 and Pt(acac)2. Furthermore, the weak and broad FePt characteristic diffraction peaks indicate that the nanoscale FePt particles were formed in the carbon matrix.Figure 2
Small-angle XRD pattern of magnetic mesoporous FePt/C composites, and the inset is wide-angle XRD pattern of magnetic mesoporous FePt/C composites.Figure3 shows the representative SEM and TEM images of magnetic mesoporous FePt/C composites. From SEM image (Figure 3(a)), magnetic mesoporous FePt/C composites are rod-like with the length of ca. 1.0 μm, which is similar with the morphology of SBA-15 template (not shown). TEM was used to directly observe pore structure and the distribution of FePt nanoparticles in magnetic mesoporous FePt/C composites. In TEM image (Figure 3(b)), ordered stripe-like and hexagonally arranged pattern was clearly observed, further confirming the ordered mesostructure of FePt/C composites. It can also be seen that a lot of small black points (FePt nanoparticles) are uniformly distributed in the entire particles. Furthermore, most of FePt nanoparticles are distributed in the carbon walls, and the sizes are similar to the diameters of carbon walls, which suggest these FePt nanoparticles are embedded in the carbon walls. It can be understood that polyfurfuryl alcohol was confined in the channels of SBA-15 template, and Fe and Pt precursors were highly dispersed within the polyfurfuryl alcohol framework. During carbonization process, the cross-linked polyfurfuryl alcohol converted into compact carbon and fully filled in the channels of SBA-15 template, resulting into no space between silica wall and carbon rod for the growth of FePt nanoparticles. As a result, FePt nanoparticles only can grow in the carbon framework.(a) SEM and (b) TEM images of magnetic mesoporous FePt/C composites (scale bar in (a): 500 nm; scale bar in (b): 50 nm).
(a)
(b)Figure4 shows the nitrogen adsorption-desorption isotherm and the corresponding pore size distribution of magnetic mesoporous FePt/C composites. The isotherm curve is of type IV with a marked leap in the adsorption branch between relative pressures P/P0 of 0.42 and 0.7, which is typical for mesoporous materials. It suggests that the ordered mesoporous structure has been kept after the embedding of FePt nanoparticles. The specific surface area is 1244 m2/g calculated from the linear part of the BET (Brunauer-Emmett-Teller) plot, and the single point adsorption total volume at P/P0=0.90 and micropore volume calculated from t-plot method are 1.396 and 0.553 cm3/g, respectively. The corresponding pore size distribution curve calculated from adsorption branch by the BJH (Barrett-Joyner-Halenda) method shows a narrow pore size distribution peaked at 4.93 nm (inset of Figure 4), allowing small biomolecules to adsorb into the channels of magnetic mesoporous FePt/C composites.Figure 4
Nitrogen adsorption-desorption isotherm of magnetic mesoporous FePt/C composites and the corresponding pore size distribution calculated from the desorption branche.Figure5 shows the magnetization curve of mesoporous FePt/C composites measured at room temperature. The magnetization strength of mesoporous FePt/C composites is 1.14 emu/g at 20 K Oe, and almost no hysteresis loop can be observed in the magnetization curve, which suggests that mesoporous FePt/C composites have superparamagnetic property. This may be due to that most of FePt nanoparticles are embedded in the carbon walls and their particle sizes are small enough to exhibit the superparamagnetic behavior. Therefore, these magnetic mesoporous FePt/C composites could be used as magnetically separable adsorbents.Figure 5
Magnetization curve of magnetic mesoporous FePt/C composites measured at room temperature.In order to evaluate the ability of magnetic mesoporous FePt/C composites to adsorb biomolecules, we investigated the protein adsorption on magnetic mesoporous FePt/C composites. Three different globular proteins, cytochrome c (Cyt c), myoglobin (Mb), and bovine serum albumin (BSA) were used as model proteins to study the adsorption capacities on magnetic mesoporous FePt/C composites. Figure6(a) shows the adsorption capacities of Cyt c, Mb, and BSA on magnetic mesoporous FePt/C composites with different solution pH ranging from 3.6 to 10.8 at protein concentration of 1.0 mg/mL. It can be observed that magnetic mesoporous FePt/C composites have the highest adsorption capacity for Cyt c and the lowest adsorption capacity for BSA, respectively. It has been accepted that the relative size of the protein molecules with respect to the channel diameter of mesoporous materials influences directly the protein adsorption capacity [28]. In this work, the peak pore size of magnetic mesoporous FePt/C composites (Dp) is 4.93 nm, but the proteins have different molecular sizes. The dimensions of Cyt c, Mb, and BSA are around 2.6×3.2×3.0 nm, 2.9×3.6×6.4 nm, and 5.5×5.6×12.0 nm, respectively. As a result, the smallest Cyt c proteins could be adsorbed in the channels of magnetic mesoporous FePt/C composites more than the larger Mb and BSA proteins. On the other hand, the highest adsorption capacity for each protein can be found at a pH equal to the isoelectric point (pI) of each protein (pI=9.8 for Cyt c, pI=7.2 for Mb, and pI=4.8 for BSA). The adsorption of proteins is typically determined by electrostatic and hydrophobic interactions, and the cohesive attraction and repulsion of the amino acids present in the protein molecules [29]. Near the pI, the net charge of proteins is around zero, and thus the hydrophobic interactions between the protein molecules and magnetic mesoporous FePt/C composites (carbon rods are hydrophobic) dominate the protein adsorption ability on magnetic mesoporous FePt/C composites. Furthermore, there is no repulsion between amino acid residues on the surface of adsorbed protein molecules near the pI [29], resulting into that the protein molecules are more densely packed on the surface of magnetic mesoporous FePt/C composites. Therefore, the adsorption capacities of Cyt c, Mb, and BSA are highest near the pI of each protein, respectively. The adsorption capacities of Cyt c, Mb, and BSA are reduced below and above the pI, which could be ascribed to the expansion of the effective molecular diameter of each protein since strong repulsive forces between the amino acid residues of the molecule are present below and above the pI, and more space is needed for the expanded protein molecules.(a) the adsorption capacities of Cyt c, Mb, and BSA on magnetic mesoporous FePt/C composites with different solution pH ranging from 3.6 to 10.8 at protein concentration of 1.0 mg/mL; (b) the adsorption curves of Cyt c, Mb, and BSA on magnetic mesoporous FePt/C composites with the solution at a pH equal to the pI of each protein (pI=9.8 for Cyt c, pI=7.2 for Mb, and pI=4.8 for BSA).
(a)
(b)Figure6(a) shows the adsorption curves of Cyt c, Mb, and BSA on magnetic mesoporous FePt/C composites with the solution at a pH equal to the pI of each protein. Each adsorption curve shows a sharp initial rise and a following steady stage, suggesting a high affinity between the protein molecules and the surface of mesoporous FePt/C composites at the initial stage. The saturation adsorption capacities on magnetic mesoporous FePt/C composites for Cyt c, Mb, and BSA are around 200, 162, and 121 μg/mg, respectively, indicating that magnetic mesoporous FePt/C composites exhibit superior protein adsorption ability. The saturation adsorption for each protein can be reached at concentrations above 0.5 mg/mL, which confirmed that the adsorption capacities of each protein on magnetic mesoporous FePt/C composites in Figure 6(a) reached the saturation adsorption. Therefore, magnetic mesoporous FePt/C composites have potential as magnetically separable adsorbent for biomolecules separation.


## 4. Conclusion

Magnetic mesoporous FePt/C composites with FePt nanoparticles embedded in carbon walls were successfully prepared using a simple cocasting method. Furfuryl alcohol, Fe(acac)3, and Pt(acac)2that were simultaneously incorporated into the channels of SBA-15 template made the Fe and Pt precursors be highly dispersed within the polyfurfuryl alcohol framework after polymerization process. During carbonization process, the cross-linked polyfurfuryl alcohol is converted into compact carbon and fully filled in the channels of SBA-15 template, resulting into the embedding of FePt nanoparticles in carbon walls. This cocasting method made the preparation procedure simpler and saved the preparation time. The results indicated that FePt/C composites have ordered mesoporous structure with high surface area of 1244 m2/g, narrow mesopore size distribution peaked at 4.93 nm, and superparamagnetic behavior (Ms=1.14 emu/g). By using Cyt c, Mb, and BSA as model proteins, the adsorption capacities of mesoporous FePt/C composites can reach ca. 200, 162, and 121 μg/mg, respectively. Therefore, these magnetic mesoporous FePt/C composites have potential as magnetically separable adsorbents for biomolecules separation.



---

*Source: 530143-2012-10-04.xml*