# Synthesis and Characterization of Sodium Bis(2-ethylhexyl)

Authors: D. Venkatesan; D. Deepan; J. Ramkumar; S. Moorthy Babu; R. Dhanasekaran
Journal: Journal of Nanomaterials
 (2012)

---

## Abstract

CdS nanoparticles and thin films are well known for their excellent semiconducting properties. When transition metal ions are doped into the CdS, it exhibits magnetic properties in addition to semiconducting properties and they are termed as dilute magnetic semiconductors (DMSs). In this paper, we discuss the preparation of sodium bis(2-ethylhexyl) sulfonsuccinate (AOT) capped CdS nanoparticles and thin films doped with magnetic impurity Mn. Sodium bis(2-ethulexyl) sulfonsuccinate (AOT), capping agent promotes the uniform formation of nanoparticles. Optical characterizations are made using the UV-Vis spectrometer, PL, and FTIR. XRD shows the hexagonal structure of the CdS. SEM images and EDS measurements were made for the thin films. EPR shows the clear hyperfine lines corresponding to Mn2+ ion in the CdS nanoparticles.


---

## Body

## 1. Introduction

Nanostructured materials, especially II–VI semiconductors, have become a subject of intensive research for their extraordinary properties compared to bulk material [1–3]. Semiconductor nanocrystalline materials which have diameters less than their bulk exciton diameter display size-dependent optical properties due to the quantum confinement. As a result of size quantization, the absorption spectrum gets blue-shifted which indicates the decrease in crystallite size [4]. Manganese-doped CdS nanocrystals have been mainly studied due to their luminescence properties. Synthesis of these doped nanocrystals has become a major interdisciplinary field of research during the past decades. This is due to the fact that the Mn2+ ions provide good traps for the excited electrons, which give rise to their potential use in the fields of nonlinear optics, luminescence, electronics, and optoelectronic devices [5–10]. The localized d orbital electrons of the magnetic dopant ions couple with the electrons in the semiconducting band of the host material. This coupling phenomena lead to number of interesting and peculiar properties such as magnetoelectrical and magneto optical effects.In the present work, we explained the simple attempts made to prepare the sodium bis(2-ethulexyl) sulfonsuccinate (AOT) capped cadmium sulphide nanoparticles and found varying absorption spectra with AOT capping and their stability with variation of capping concentration are reported. The option of AOT was considered since they have better possibilities of improved size control on the formation of CdS nanoparticles. AOT is a double-chain anionic surfactant and a well-known capping agent for semiconductor nanoparticles. Use of AOT creates interesting optical properties of AOT capped CdS nanoparticles which is another motivating factor. Figure1 shows the structure of anionic surfactant AOT [11].Figure 1
Structure of AOT.In the capping process, the organic solvents are absorbed on the surface of the CdS nanoparticles, and this produces the negative charge on the surface of the particles due to polarization. This leads to the repulsive force among the capped nanoparticles. This repulsive force is capable of keeping very small nanoparticles (d<10 nm) to suspend on the solution, where the larger particles settle down at the bottom. Varying the concentration of the capping agent, the particle size can be changed, and, in this work, we have optimized the concentration of capping agent and proceeded with the magnetic dopants in CdS and their magnetic properties are studied.


## 2. Preparation

CdS nanoparticles were prepared by simple chemical process. Following [12], we have adopted a simple method for the synthesis. The general procedure includes 0.01 M of CdCl3, and of 0.01 M of Na2S were dissolved in separate containers containing 20 mL distilled water. 0.1 M dioctyl sodium sulfonsuccinate (AOT) solution in 10 mL hexane was created beforehand. 5 mL of the CdCl2 solution and 5 mL of the Na2S solution were taken into separate beakers. 0.1 M AOT in hexane solutions were mixed into the two solutions and were allowed to stir for 30 minutes using a magnetic stirrer. In order to get the best emulsion, these aqueous solutions were injected into AOT in hexane as rapidly as possible. These respective CdCl2/AOT/hexane and Na2S/AOT/hexane solutions were allowed to stir for 30 min before being mixed together and allowed to stir for an additional 30 min. Both the solutions were mixed together and allowed to stir for another 30 minutes using magnetic stirrer. AOT, capping agent is introduced to constrain the particle size. The particle size depends mainly on the concentration of the capping agent [13]. The initial preparation was done with a concentration of 0.1 M. The similar procedure was adopted, and the concentration of AOT was varied from 0.04 M to 1 M.The samples were characterized by powder X-ray diffraction employing CuKα radiation. The electron paramagnetic resonance spectra were taken using Bruker EMX EPR Spectrometer.


## 3. Results and Discussions

It is found that the absorbance peak is red-shifted when AOT concentration was increased from 0.04 to 1 M. This indicates the increase in particle size with increase in the concentration of capping agent. The band gap of the CdS nanoparticles is a function of the particle size under tight binding approximation (TBA) as well as effective mass approximations (EMA). The experimental data agree well with the effective mass calculations for diameters larger than 4 nm where as TBA fit better for particles with diameters smaller than 4 nm [14]. Murakoshi et al. [15] have reported that the experimental data for the dependence of band gap with particle size agrees well with EMA with a finite potential well, even for smaller sizes. The relationship between the particle size d and band gap Eg is given by(1)Eg=Eg(0)+αdβ,
where Eg(0) is the band gap for bulk CdS (2.42 eV), α and β are constants. The value of β=2 for EMA [16]. The data taken from Lippens and Lannoo [17] for the relationship between band gap and particle size under EMA were solved using the above relation, and the values of α and β were obtained as 13 eV/nm2 and 2, respectively. Thus, greater blue shift was observed at 0.04 M AOT capped CdS nanoparticles, which infers the smaller size compared to higher concentration of AOT. This was confirmed from the UV-VIS measurements taken immediately after preparation.The optical absorption as a function of wavelength for CdS particles with various capping concentrations is shown in Figure2(a). It can be seen from the figure that the absorption edge shifts towards shorter wavelength region as the concentration of AOT is decreased, indicating the formation of CdS particles in the nanometer regime [18]. It can also be seen that, as the AOT concentration is decreased, excitonic peaks appear which is an indication of increase in band gap and decrease in particle size. Haruff and Bunker [19] have reported the appearance of an excitonic peak at around 310–380 nm for AOT capped CdS nanoparticles prepared in different ratio of H2O/AOT. Pileni [20] has also reported the presence of the excitonic peak at the range of 380 nm to 420 nm for AOT protected CdS nanoparticles. From Figure 2(a), for the stabilizer concentration of 0.04 M AOT, excitonic peaks were observed at around 422 nm in the present study, indicating the formation of CdS particles of smaller particle size but may be larger than earlier reported [20]. The excitonic peaks appear at 432 nm and 447 nm for the 0.07 M and 0.1 M AOT indicating the gradually increase in the particle size.(a) Absorption spectra of CdS nanoparticles prepared at different concentrations of AOT. (b) Absorption spectra of pure and doped CdS nanoparticles.
(a)(b)Figure2(b) shows the optical absorption spectra for Mn-doped CdS nanoparticles. The excitonic peak appears at approximately 459 nm, which is red-shifted. This red shift indicates the decrease in band gap and also represents increase in the particle size.Thus, we can conclude that, when the concentration of AOT is smaller, greater blue shift is observed, which refers to smaller particle size. The optimum concentration of the AOT to prepare Mn-doped CdS nanoparticles is 0.04 M.The photoluminescence spectra of CdS have been extensively studied. The role of surface and native defects has been used to explain the behavior of the PL. In PL, a strong and narrow emission peak at 488 nm was observed when the sample was excited at 280 nm light as shown in Figure3(a). The luminescence at 488 nm may be due to a higher level transition in CdS crystallites. It has been reported that this kind of band-edge luminescence arises from the recombination of excitons and/or shallowly fascinated electron-hole pairs. A slight hump is present at 530 nm, which can be ascribed to the surface defect emission of the CdS nanoparticles. In contrast to the above, the PL spectrum of Mn-doped CdS sample shows an additional red-shifted emission featured at 575 nm, due to an internal T41→A61Mn2+ transition [21], indicating huge spectra overlapping between the emission from Mn2+ ions and the emission from surface states. So a capable energy transfer from the excited carriers intent at the surfaces to Mn ions occurs in our CdS : Mn sample [22, 23]. Generally, it is known that the photoluminescence in semiconductors is greatly influenced by the stoichiometric defects at electronic levels. The variation in the intensity of the characteristic peaks shows considerable changes in the stability and size of the nanoparticles. Thus, slight difference is found in the absorption edge as well as the photoluminescence peak positions observed for the pure and the doped samples, which indicates a slight variation in size and stability [24].(a) Photoluminescence of the system excited at 280 nm (λex=280 nm), (b) system excited at 300 nm (λex=300 nm).
(a)(b)Figure3(b) shows a distinct peak at 488 nm, when excited at 300 nm light. This is the characteristic peak. An additional red-shifted peak at 545 nm is also present which represents the defect emission peak. The intensity of the surface defect emission increases as the Mn dopant percentage increases. The Mn (2%) doped sample shows a broad peak compared to the others; this can be attributed to large surface defects present. The peak at 600 nm is due to the excitation itself.FTIR spectra of AOT, pure and AOT capped CdS nanoparticles are shown in the Figure4. The CH stretching band is characterized by four peaks (2861, 2874, 2932, and 2960 cm−1) due to the symmetric and antisymmetric stretching vibrations of CH2 and CH3 groups of the AOT alkyl chains [25]. The absorption peak around 1047 cm−1 is due to the CH2 twist [26]. With the overall observations, it can be concluded that the AOT has formed a coating over the cadmium sulfide nanoparticles, which in turn supports their influence on size reduction. There was no formation of sulphate compounds. The obtained results are tabulated in Table 1.Table 1
FT-IR spectra of CdS system.
S. no.Wave number cm−1Bonding(1)2960νas(CH3)(2)2932νas(CH2)(3)2874νs(CH3)(4)2861νs(CH2)(5)1643ν(CO) of AOTFigure 4
FT-IR spectra of the CdS system.The pure and doped CdS nanoparticle solutions are deposited on glass substrate heated at 80°C. The XRD pattern of the deposited film is shown in Figure5. From the JCPDS (file no. 10-0454) cards, the peaks of the pure CdS are marked. The planes corresponding to CdS are marked. The peaks at angle 2θ = 25.96°, 29.98°, 35.44°, and 43.58° correspond to the planes [002] [101], [102], and [110], respectively, which confirms that the CdS thin films are having the hexagonal crystalline structure. CdS exhibits both hexagonal and cubic crystalline structures. The planes [002] and [101] represent the hexagonal structure of CdS. The intensity of the peaks was found to be very weak which refers the poor crystallinity of the materials that is being deposited. Since the CdS nanoparticles are being capped with AOT, the X-ray beam falls on the amorphous AOT and reduces the intensity of the peaks of the CdS nanostructured thin films. Since the AOT is a polymer compound and being amorphous, they do not show sharp peaks as like the crystalline materials. And no peaks of the secondary phase NaCl were found, and it is very clear from the EDX data which confirms the absence of the chlorine in the entire system.Figure 5
XRD patterns of the pure and Mn : CdS thin films.Moreover, the as-deposited samples usually lack in the crystallinity, and similar results were reported [27, 28]. When thin films are annealed, the crystallinity of the thin films may increase.Figure6(a) shows SEM images of pure CdS nanoparticles deposited on a glass plate. We can observe more surface irregularities like ridges from the SEM images but are not visible cracks. The CdS nanoparticles, embedded in the AOT matrix, indicate that the sample is mixed with large number of well dispersed with irregular shape and size. Figure 6(b) shows the cluster of nanoparticles at higher resolution. But most of the particles appear to be spherical in shape.SEM images of pure CdS thin films: (a) lower magnification, (b) higher magnification.
(a)(b)Figure7(a) shows SEM images of Mn (1 mol %) doped CdS thin films. It is observed that the films are not uniform throughout the regions, but the films are without any void, pinhole, or cracks and they cover the substrates well. Figure 7(b) shows the structure of nanoparticles at higher magnification. We can infer that the clusters like patterns are formed due to the agglomeration of constituent particles. The images show presence of larger cluster.SEM images of Mn (1 mol %) doped CdS thin films: (a) lower magnification, (b) higher magnification.
(a)(b)Figure8(a) shows images of Mn (2 mol %) doped CdS thin films. There we clearly observe the small-nanosized grains engaged in a fibrous-like structure, which clearly indicates the nanocrystalline nature along with some agglomerated phase of CdS thin films. The fibrous-like structure is due to the presence of the capping agent which continued to remain even after the heating process. From these images, grain sizes of the films are not uniform. Therefore, we estimated the grain sizes from 70 to 500 nm. Figure 8(b) shows images of Mn (3 mol %) doped CdS thin films.SEM images of (a) Mn 2 mol %, (b) Mn 3 mol % doped CdS thin films.
(a)(b)The EDX report shows the purity of the sample. There is no impurity available in the sample as there is no element except the Cd, S, Mn, C, and Na in the EDX spectrum. The orbital states of Cd, S, Mn, C, and Na are seen in the EDX spectrum. It should be noted here that the contribution of the S atoms in EDX spectrum comes from both S atoms present in the AOT molecules and from those in the CdS nanoparticles. Figure9 shows the EDX measurement for the thin films.EDX spectra of (a) pure, (b) 1 mol %, (c) 2 mol %, (d) 3 mol % Mn-doped CdS thin films.
(a)(b)(c)(d)The amount of dopants present in the Mn : CdS thin films reveals that the Mn concentration increases with increase in the dopants increase. From the figure, the energy levels at 0.650 KeV, 0.762 KeV, 5.898 KeV, 6.489 KeV, and 6.536 KeV correspond to theLIαβ, LIIαβ, Kα, Kβ, and Kαβ (Table 2).Table 2
Concentration of Mn in doped thin films.
S. no.SystemAt % of the dopant(1)1 mol % Mn0.16(2)2 mol % Mn0.30(3)3 mol % Mn0.55Figure10 shows the EPR spectra of the Mn-doped CdS nanoparticles solution in hexane. We can find the fully resolved hyperfine structure for typical Mn2+ (d5 configuration) at hexagonal lattice sites in CdS, and the electronic ground state is S5/26. As the spin of the Mn2+ is S=5/2, and the hyperfine splitting term is (2S+1). Hence EPR signal for Mn2+ in material will have six resonant lines. This configuration is due to the localized trapping of Mn2+ electron which is a substitutional dopant [29]. The intensity of the peaks in 2 mol% Mn-doped ZnO is less. The reason may be due to the nonuniform distribution of Mn2+ [30] ions. The six hyperfine splitting refers to 5/2↔3/2, 3/2↔1/2, 1/2↔-1/2, -1/2↔-3/2, and -3/2↔5/2 [31].Figure 10
EPR spectra of Mn-doped CdS nanoparticles in hexane.


## 4. Conclusion

The following conclusions can be drawn from the results of the study on the effect of stabilizer concentration on the formation and stability of AOT-capped CdS nanoparticles and thin films. The amount of capping agent was varied for preparing the nanomaterials. It was found the smaller the concentration of AOT, greater the blue shift which infers that the particles size reduces. Absorption peak for pure and doped CdS nanoparticles is found in visible region. And red shift is found on the addition of dopants, and excitonic feature is greatly suppressed. In PL, emission is found near 488 nm at both the excitation wavelength (λex=280 nm and 300 nm) corresponds to the surface defects in the CdS system. The emission peak at 575 nm refers to transition of Mn2+ ion from excited state to ground state. FTIR reveals the stretching of the functional group present in the system. CdS absorption peak is found near 2361 cm−1. The nanoparticles are then deposited on glass substrate at 80°C. XRD pattern reveals the lower crystallinity of the thin films, and small shifts are observed on addition of dopants. SEM images report the surface features, and the uniform distribution of the particles and EDX shows the concentration of Mn in the case of Mn : CdS thin films. Six hyperfine splitting are found in EPR spectra. Since the splitting is clear, this preparation method can be used in preparing Mn-doped CdS thin films using any other sophisticated instrument.



---