# Cefuroxime-Loaded Hydrogels for Prevention and Treatment of Bacterial Contamination of Open Wounds

Authors: Pavlo Virych; Oksana Nadtoka; Volodymyr Doroschuk; Sergey Lelyushok; Vasyl Chumachenko; Tetiana Bezugla; Nataliya Kutsevol
Journal: International Journal of Polymer Science
 (2021)

---

## Abstract

Dextran/Sulfodextran-graft-polyacrylamide- and polyacrylamide-based hydrogels were synthesized by radical polymerization and loaded with cefuroxime to obtain antimicrobial wound dressings. Antibiotic release from the antibiotic-loaded hydrogels into an aqueous solution was studied by the HPLC-UV method. It is shown that cefuroxime-loaded Dextran/Sulfodextran-graft-polyacrylamide hydrogels release the antibiotic more slowly compared to polyacrylamide hydrogel with the same density of cross-links. Antibacterial activity of the synthesized materials was testedin vitro against wild strains of S. aureus, E. coli, and Klebsiella spp. The possibility of using the obtained antimicrobial hydrogels for the treatment of infected wounds was confirmed in vivo in a rat model.


---

## Body

## 1. Introduction

Among the many antibacterial agents, antibiotics are the most effective and widely used drugs. However, their widespread and often thoughtless use has provoked the emergence and expansion of resistant strains of bacteria. There are two main ways to overcome antibiotic resistance: the synthesis of novel antibiotics and the development of new methods of antibiotic applications. Hydrogels of different chemical nature appear to be promising carriers of antibiotics in biotechnology and medicine. Over the last few decades, various antibiotic-loaded hydrogels have been developed as antibacterial coatings and dressings for the treatment of superficial trauma, burn, or diabetic wounds [1–5]. These materials release antibiotics at the wound site, thus preventing infection and promoting the healing process [6]. Local administration of antibiotics significantly reduces the unwanted side effects that are often observed with systemic use.Hydrogels are three-dimensional cross-linked polymer systems possessing high water swellability. The use of hydrogels as wound dressings or coverings requires some special properties such as biocompatibility, oxygen permeability, sufficient mechanical strength and flexibility, and the ability to be easily applied and removed from wounds [7, 8]. Multiple hydrophilic groups of hydrogels ensure nonadhesion to the wound, which means painless removal of the coating. They also create a moist wound environment that is beneficial for healing [9]. Currently, various hydrogels are extensively studied as drug delivery systems, and some of them have already been used as wound dressings. The researchers highlight the advantages of hydrogels over traditional pharmaceuticals [2, 10].Topical administration of antimicrobials allows formulating the hydrogels that contain high concentrations of antibiotics [9]. It is especially important for the care of infected wounds and burns. Sometimes, antibiotic-loaded hydrogels are tested against both antibiotic-susceptible and antibiotic-resistant bacteria [11, 12].The hydrogels loaded with antibiotics must release the active substance in a sustained manner because successful anti-inflammatory wound treatment is directly dependent on the continuous action of antimicrobial agents. Controlled and prolonged release of the antibiotic in the affected area is the essential requirement for the prevention of biofilm formation [6, 13]. Moreover, sustained delivery of the drug to the application site ensures a significant increase in time intervals needed to change the dressing on the wound. The nature of the polymer and the degree of cross-linking are believed to be the main factors that regulate the ability of hydrogels to deliver drug substances and release them at the target site. Some structure peculiarities of hydrogels can affect these processes too.Our idea was to create polyacrylamide-based antimicrobial hydrogels for the treatment of infected wounds. These hydrogels can be loaded with the desired amount of antibiotics, and their local application for drug release provides overcoming the side effects of a systemic overdose. To vary the structure of the synthesized hydrogels, small amounts of polysaccharides were used in the syntheses as structure-affecting components. The antibiotic-loaded samples were testedin vitro against some painful bacteria and in vivo as antimicrobial dressings.


## 2. Materials and Methods

### 2.1. Reagents

Acrylamide (AA), three samples of Dextran withMw=20000g/mol (D20), Mw=100000g/mol (D100), and Mw=500000g/mol (D500), Sulfodextran with Mw=500000g/mol (SD500), N,N′-methylene-bis-acrylamide (MBA), and cerium (IV) ammonium nitrate (CAN) were supplied by Sigma-Aldrich (USA). Antibiotic cefuroxime and antiseptic miramistin were purchased at a local pharmacy.All reagents were used without further purification. Double-deionized water was used for all syntheses and procedures.


### 2.2. Syntheses of Hydrogels

Dextran/Sulfodextran-graft-polyacrylamide (D/SD-g-PAA) hydrogels were synthesized by free-radical polymerization in the presence of MBA as a cross-linker (Figure1) [14, 15]. Being added into the synthesis mixture in very small amounts, Dextran/Sulfodextran affected the structure of the final product.Figure 1
The proposed mechanism of the synthesis of cross-linked D-g-PAA hydrogels.Dextran/Sulfodextran (5×10−4mmol) was dissolved in 24 mL of distilled water at 25°C. The polysaccharide solution was stirred and bubbled with argon for 20 min to remove oxygen. Then, a CAN/HNO3 initiator system (3×10−2mmol CAN in 1 mL of 0.125 N HNO3) was added, and the solution was stirred and bubbled with argon for another 2 min. A monomer AA (50 mmol) and a cross-linking agent MBA (0.4 g per 100 g of AA) were added to the solution. The reaction mixture was kept under argon for 24 h. To remove the unreacted monomer, the obtained hydrogels were thoroughly washed with distilled water. Then, all samples were dried and stored at ambient temperature.Polyacrylamide (PAA) hydrogels were synthesized under the same conditions but without the Dextran/Sulfodextran in the reaction mixture. The samples of cross-linked PAA were dried and stored as the samples of cross-linked D/SD-g-PAA.Further in the text, the synthesized hydrogels are designated as D20-g-PAA-0.4, D100-g-PAA-0.4, D500-g-PAA-0.4, and SD500-g-PAA-0.4 according to a polysaccharide component of the obtained samples and a ratio MBA to AA in the syntheses.


### 2.3. Preparation of Antibiotic-Loaded Hydrogels

The weighed samples of the dried hydrogels were placed in an aqueous solution of cefuroxime (166.6 mg/mL) and incubated at 25°C for 18 hours. The amount of loaded antibiotic in the hydrogel sample was estimated by subtracting the amount of cefuroxime remaining in the solution from the initial content. All concentrations were determined by high-performance liquid chromatography with ultraviolet detection (HPLC-UV). The hydrogels swollen in this solution were used for further studies of their ability to release the antibiotic. Such samples contain an indication of cefuroxime (-Cef) in their names.


### 2.4. Antibiotic Release Study

The swollen samples of the antibiotic-loaded hydrogels were removed from the solution of cefuroxime, wiped with a piece of filter paper, and then placed in 25.0 mL of distilled water. The experiment was performed with gentle stirring at 25°C. To determine the concentration of the antibiotic released into the solution, the aliquots of the solution were taken at regular intervals and analyzed by the HPLC-UV method. The antibiotic release experiment was performed with each antibiotic-loaded hydrogel at least three times.


### 2.5. Thermogravimetric Analysis (TGA)

Thermogravimetric studies of the synthesized hydrogels were performed using a Netzsch TG 209 F1 Libra apparatus (Selb, Germany). The experiments were carried in a nonisothermal mode. Dry samples were heated with the heating rate of 10°C/min and monitored for weight change in the range of 30-900°C. The measurements were carried out under nitrogen protective flow. The weight of the samples under investigation was 10 mg. Al2O3 served as reference material.


### 2.6.In Vitro Tests for Antibacterial Activity

To test the antibacterial hydrogels for their ability to inhibit bacterial growth, wild-type strains ofStaphylococcus aureus, Escherichia coli, and Klebsiella spp. selectively grown on Endo’s or yolk-salt agar media were used. The sensitivity of the microorganisms was evaluated by the disc diffusion method on a Müller–Hinton agar of the following composition (g/L): agar—17, hydrolyzed casein—17.5, hydrolyzed bovine hart—2, and water-soluble starch—1.5; pH=7.3. The dry hydrogels were swollen (24 h) in an aqueous solution of cefuroxime (0.1 and 1 mg/mL). A miramistin solution (0.1 mg/mL) was used for the control experiment. The tested samples were 5 mm in diameter, and their sizes were similar to those of standard disks with antibiotics. The measurement of the growth inhibition zone was carried out using a digital caliper Miol 15-240. The contact of the hydrogel samples with the microorganisms occurred within 24 h before recording the diameter of growth inhibition. Statistical data processing was performed using the Shapiro-Wilk test (p>0.05) and the Scheffe ANOVA test (p<0.05). Each in vitro experiment was repeated three times.


### 2.7. In Vivo Evaluation of Healing Properties

The effects of synthesized antibacterial hydrogels on infected wound healing were assessed by the rat wound model. Thein vivo tests were performed using white outbred rats, which were kept in standard conditions of a vivarium. All manipulations with animals were carried out according to the Law of Ukraine “On the Protection of Animals from Cruelty” and the European Convention for the Protection of Vertebrate Animals Used for Research and Other Scientific Purposes.Female rats weighing 230-260 g were selected, and general anesthesia was performed with sodium etaminal at the rate of 3.5 mg per 1 kg of live weight. The area of the back between the shoulder blades of the animal was cleared of hair. A section of skin 7-8 mm in diameter was removed with a sharp scalpel. The resulting wound was infected with the mixture of microorganismsS. aureus, E. coli, and Klebsiella spp., which were in physiological solution in the amount of 1·108 CFU/mL. The wound was covered with the synthesized hydrogels loaded with cefuroxime (1 mg/mL) or miramistin (0.1 mg/mL) and the standard fabric material (gauze dressing). The bandage was fixed with a wide Band-Aid. After 24 h, the wound was wiped with a sterile swab, and the wound bacteria were inoculated into the nutrient medium. Yolk-saline agar was used to cultivate gram-positive bacteria, and Endo’s medium was used for gram-negative bacteria.Wound healing of the rats was assessed visually.Skin irritation tests revealed that D/SD-g-PAA hydrogels per se did not cause any irritation, indicating its safety for topical application.


## 2.1. Reagents

Acrylamide (AA), three samples of Dextran withMw=20000g/mol (D20), Mw=100000g/mol (D100), and Mw=500000g/mol (D500), Sulfodextran with Mw=500000g/mol (SD500), N,N′-methylene-bis-acrylamide (MBA), and cerium (IV) ammonium nitrate (CAN) were supplied by Sigma-Aldrich (USA). Antibiotic cefuroxime and antiseptic miramistin were purchased at a local pharmacy.All reagents were used without further purification. Double-deionized water was used for all syntheses and procedures.


## 2.2. Syntheses of Hydrogels

Dextran/Sulfodextran-graft-polyacrylamide (D/SD-g-PAA) hydrogels were synthesized by free-radical polymerization in the presence of MBA as a cross-linker (Figure1) [14, 15]. Being added into the synthesis mixture in very small amounts, Dextran/Sulfodextran affected the structure of the final product.Figure 1
The proposed mechanism of the synthesis of cross-linked D-g-PAA hydrogels.Dextran/Sulfodextran (5×10−4mmol) was dissolved in 24 mL of distilled water at 25°C. The polysaccharide solution was stirred and bubbled with argon for 20 min to remove oxygen. Then, a CAN/HNO3 initiator system (3×10−2mmol CAN in 1 mL of 0.125 N HNO3) was added, and the solution was stirred and bubbled with argon for another 2 min. A monomer AA (50 mmol) and a cross-linking agent MBA (0.4 g per 100 g of AA) were added to the solution. The reaction mixture was kept under argon for 24 h. To remove the unreacted monomer, the obtained hydrogels were thoroughly washed with distilled water. Then, all samples were dried and stored at ambient temperature.Polyacrylamide (PAA) hydrogels were synthesized under the same conditions but without the Dextran/Sulfodextran in the reaction mixture. The samples of cross-linked PAA were dried and stored as the samples of cross-linked D/SD-g-PAA.Further in the text, the synthesized hydrogels are designated as D20-g-PAA-0.4, D100-g-PAA-0.4, D500-g-PAA-0.4, and SD500-g-PAA-0.4 according to a polysaccharide component of the obtained samples and a ratio MBA to AA in the syntheses.


## 2.3. Preparation of Antibiotic-Loaded Hydrogels

The weighed samples of the dried hydrogels were placed in an aqueous solution of cefuroxime (166.6 mg/mL) and incubated at 25°C for 18 hours. The amount of loaded antibiotic in the hydrogel sample was estimated by subtracting the amount of cefuroxime remaining in the solution from the initial content. All concentrations were determined by high-performance liquid chromatography with ultraviolet detection (HPLC-UV). The hydrogels swollen in this solution were used for further studies of their ability to release the antibiotic. Such samples contain an indication of cefuroxime (-Cef) in their names.


## 2.4. Antibiotic Release Study

The swollen samples of the antibiotic-loaded hydrogels were removed from the solution of cefuroxime, wiped with a piece of filter paper, and then placed in 25.0 mL of distilled water. The experiment was performed with gentle stirring at 25°C. To determine the concentration of the antibiotic released into the solution, the aliquots of the solution were taken at regular intervals and analyzed by the HPLC-UV method. The antibiotic release experiment was performed with each antibiotic-loaded hydrogel at least three times.


## 2.5. Thermogravimetric Analysis (TGA)

Thermogravimetric studies of the synthesized hydrogels were performed using a Netzsch TG 209 F1 Libra apparatus (Selb, Germany). The experiments were carried in a nonisothermal mode. Dry samples were heated with the heating rate of 10°C/min and monitored for weight change in the range of 30-900°C. The measurements were carried out under nitrogen protective flow. The weight of the samples under investigation was 10 mg. Al2O3 served as reference material.


## 2.6.In Vitro Tests for Antibacterial Activity

To test the antibacterial hydrogels for their ability to inhibit bacterial growth, wild-type strains ofStaphylococcus aureus, Escherichia coli, and Klebsiella spp. selectively grown on Endo’s or yolk-salt agar media were used. The sensitivity of the microorganisms was evaluated by the disc diffusion method on a Müller–Hinton agar of the following composition (g/L): agar—17, hydrolyzed casein—17.5, hydrolyzed bovine hart—2, and water-soluble starch—1.5; pH=7.3. The dry hydrogels were swollen (24 h) in an aqueous solution of cefuroxime (0.1 and 1 mg/mL). A miramistin solution (0.1 mg/mL) was used for the control experiment. The tested samples were 5 mm in diameter, and their sizes were similar to those of standard disks with antibiotics. The measurement of the growth inhibition zone was carried out using a digital caliper Miol 15-240. The contact of the hydrogel samples with the microorganisms occurred within 24 h before recording the diameter of growth inhibition. Statistical data processing was performed using the Shapiro-Wilk test (p>0.05) and the Scheffe ANOVA test (p<0.05). Each in vitro experiment was repeated three times.


## 2.7. In Vivo Evaluation of Healing Properties

The effects of synthesized antibacterial hydrogels on infected wound healing were assessed by the rat wound model. Thein vivo tests were performed using white outbred rats, which were kept in standard conditions of a vivarium. All manipulations with animals were carried out according to the Law of Ukraine “On the Protection of Animals from Cruelty” and the European Convention for the Protection of Vertebrate Animals Used for Research and Other Scientific Purposes.Female rats weighing 230-260 g were selected, and general anesthesia was performed with sodium etaminal at the rate of 3.5 mg per 1 kg of live weight. The area of the back between the shoulder blades of the animal was cleared of hair. A section of skin 7-8 mm in diameter was removed with a sharp scalpel. The resulting wound was infected with the mixture of microorganismsS. aureus, E. coli, and Klebsiella spp., which were in physiological solution in the amount of 1·108 CFU/mL. The wound was covered with the synthesized hydrogels loaded with cefuroxime (1 mg/mL) or miramistin (0.1 mg/mL) and the standard fabric material (gauze dressing). The bandage was fixed with a wide Band-Aid. After 24 h, the wound was wiped with a sterile swab, and the wound bacteria were inoculated into the nutrient medium. Yolk-saline agar was used to cultivate gram-positive bacteria, and Endo’s medium was used for gram-negative bacteria.Wound healing of the rats was assessed visually.Skin irritation tests revealed that D/SD-g-PAA hydrogels per se did not cause any irritation, indicating its safety for topical application.


## 3. Results and Discussion

The syntheses of the cross-linked Dextran (Sulfodextran)-graft-polyacrylamide hydrogels include two stages: (1) the preparation of polysaccharide macroradicals as a result of Dextran/Sulfodextran interaction with CAN/HNO3 oxidative system [16, 17] and (2) the growth of PAA chains from active centers on the polysaccharide and their simultaneous cross-linking by the MBA cross-linking agent (Figure 1). Since the concentration of the cross-linking agent MBA is the same in all syntheses, it is assumed that the density of cross-links in all hydrogels is the same.As shown earlier [18], the number of grafted polyacrylamide chains in the synthesized D(SD)-g-PAA copolymers is determined by the molar ratio of the polysaccharide and the CAN initiator. Formed under the action of the initiator, the active centers on the polysaccharide macromolecule trigger the growth of polyacrylamide chains. According to the molar ratio of Dextran (Sulfodextran) to CAN used in the syntheses of hydrogels described above, approximately 60 points of growth can appear on the polysaccharide macromolecule. Near the grafting point, the growing polyacrylamide chains have a conformation that essentially differs from those for PAA macromolecules in solution [16, 19]. An increase in the molecular weight of Dextran molecules, as well as the appearance of a charge on the polymer chain of Sulfodextran, has a significant effect on the conformation of the growing polyacrylamide chain in the nearest vicinity of the polysaccharide. Thus, the internal structure of the cross-linked D/SD-g-PAA hydrogels and their properties may differ from the structure and properties of cross-linked PAA with the same number of cross-links.According to thermogravimetric data, all synthesized hydrogels are very hydrophilic and contain water even when dried. The first weight loss step is registered in the range of 40-190°C with a maximum of about 100°C indicating water desorption (Figure2). In addition, in this interval at higher temperatures, the elimination of NH3 and CO can occur as a result of chemical reactions between some neighboring functional groups of the polyacrylamide chains [20]. The second distinct weight loss step is observed at 300-485°C with a rather lower maximum on the derivative weight loss curve. It corresponds to the decomposition of the polymer matrix itself, which consists mainly of polyacrylamide fragments. The destruction of the polymer matrix of D/SD-g-PAA-0.4 samples begins at a higher temperature compared to PAA-0.4. The increase in this temperature is 15-50°C, depending on the internal structure of the hydrogels (Table 1).Figure 2
Derivative weight loss curve vs. temperature: (1) PAA-0.4, (2) D20-g-PAA-0.4, (3) D100-g-PAA-0.4, (4) D500-g-PAA-0.4, and (5) DS500-g-PAA-0.4 hydrogels.Table 1
Temperature intervals of weight loss on heating, obtained by the DTA method.
SamplePeak 1Peak 21D20-g-PAA-0.435-190315-4852D100-g-PAA-0.445-160320-4503D500-g-PAA-0.430-180330-4504DS500-g-PAA-0.430-185350-4805PAA-0.435-190300-470To prepare the antibiotic-loaded hydrogels for drug release studies, the samples of the dry hydrogels were swollen in an aqueous solution of cefuroxime for 18 h. As shown in Table2, the content of cefuroxime is the greatest for the hydrogels that were synthesized using Dextrans as a structure-affecting component.Table 2
Content of cefuroxime in the synthesized hydrogels (g of antibiotic per g of dried hydrogel).
SampleContent (g/g)1D20-g-PAA-0.4-Cef3.522D100-g-PAA-0.4-Cef3.403D500-g-PAA-0.4-Cef3.344DS500-g-PAA-0.4-Cef3.315PAA-0.4-Cef1.64The contact of the synthesized antibiotic-loaded hydrogels with water leads to the desorption of drug molecules into the solution. A typical antibiotic release profile is shown in Figure3. For all samples, the initial burst of release is followed by desorption at a slower rate. After 3 hours, only a slight increase in the concentration of cefuroxime in the solution can be registered. The sample PAA-0.4-Cef was found to have the highest release rate; the content of cefuroxime in this hydrogel decreased by 55% after 6 h of contact with water (Table 3). The behavior of D-g-PAA-0.4-Cef hydrogels in this process is somewhat different. Being initially more loaded with cefuroxime, these samples release the drug into solution more slowly than PAA-0.4-Cef.Figure 3
Cefuroxime concentration in water solution vs. time of contact with DS500-g-PAA-0.4-Cef hydrogel.Table 3
Release of cefuroxime (in %) from the antibiotic-loaded hydrogels into water.
SampleTime of contact0.5 h1 h6 h1PAA-0.4-Cef28.2±1.541.6±3.155.1±2.72D20-g-PAA-0.4-Cef24.4±2.329.6±2.141.9±1.63D100-g-PAA-0.4-Cef22.1±2.327.0±2.238.1±2.44D500-g-PAA-0.4-Cef18.6±2.733.9±2.139.5±2.75DS500-g-PAA-0.4-Cef27.9±2.537.2±2.050.6±2.7Thus, D/DS-g-PAA-0.4-Cef hydrogels have some advantages over other hydrogels under investigation. They are assumed to be promising biomaterials for topical application as antimicrobial dressings with prolonged action.To compare the antimicrobial activity of the antibiotic-loaded hydrogels with different internal structures, the dry samples were swollen in an aqueous solution of cefuroxime (0.1 or 1 mg/mL) for 24 h. Miramistin was used as cargo for control experiments. All synthesized cefuroxime-loaded hydrogels demonstrate high activity against test bacterial strains ofS. aureus, E. coli, and Klebsiella spp. The diameter of the growth inhibition zone is 25-30 mm for S. aureus and 20-23 mm for E. coli and Klebsiella spp. when using the hydrogel samples prepared by swelling in a solution of cefuroxime with a concentration of 1 mg/mL (Table 4).Table 4
Antimicrobial activity of cefuroxime-loaded hydrogels swollen in 1 mg/mL antibiotic solution.
SampleDiameter of the growth inhibition zone (mm)S. aureusE. coliKlebsiella sp.1PAA-0.4-Cef27.1±1.523.2±2.820.1±2.42D20-g-PAA-0.4-Cef26.0±2.421.1±3.020.3±2.43D100-g-PAA-0.4-Cef29.8±2.121.8±2.720.2±2.54D500-g-PAA-0.4-Cef25.2±2.522.1±2.822.7±2.45DS500-g-PAA-0.4-Cef29.1±2.521.3±2.722.0±2.8The antimicrobial activity is dose-dependent, but even at a low dose, antibiotic-loaded hydrogels demonstrate high efficacy against harmful microorganisms (Figure4).Figure 4
Activity of the antimicrobial hydrogels (1) PAA-0.4-Cef, (2) D20-g-PAA-0.4-Cef, (3) D100-g-PAA-0.4-Cef, (4) D500-g-PAA-0.4-Cef, and (5) DS500-g-PAA-0.4-Cef againstS. aureus (black—miramistin 0.1 mg/mL; blue—cefuroxime 0.1 mg/mL; red—cefuroxime 1 mg/mL).Thein vivo study of the activity of the synthesized antibiotic-loaded hydrogels against infections was carried out on a rat wound model. Rat models are widely used to investigate various treatments for living organisms [21, 22]. To evaluate the possibility of using antibiotic-loaded D/SD-g-PAA hydrogels in wound protecting and healing, two hydrogels D500-g-PAA-0.4 and SD500-g-PAA-0.4 were swollen in cefuroxime solution (1 mg/mL), and then, they were used to cover the infected wounds of rats. After 24 hours, the bandage was removed from the infected wound, and the surface material of the wound was scraped off. Inoculation of scraping microorganisms on a nutrient medium shows the complete absence of gram-negative bacteria (Figures 5(a) and 5(b), left) and very few colonies of gram-positive colonies (Figures 5(a) and 5(b), right) after 24 h of their growth. According to obtained data, the studied cefuroxime-loaded hydrogel samples demonstrate a higher effectiveness against bacteria compared to the miramistin-loaded hydrogels (Figures 5(c) and 5(d)) and especially to classic gauze dressings (Figures 5(f) and 5(g)).Figure 5
Cultivation of bacteria using Endo (left) and yolk-salt (right) agar media after removal of (a, b) cefuroxime-loaded hydrogels from infected wound; (c, d) miramistin-loaded hydrogels; (f, g) gauze dressings.The cefuroxime-loaded D/SD-g-PAA hydrogels demonstrated their efficacy against a mixture of pathogenic bacteria, so they can be used topically as antimicrobial dressings. Thein vivo experiments show that these antimicrobial hydrogels substantially inhibit the growth of microorganisms on an infected wound surface. The appearance of the rat wounds after removing the bandage confirms the promising use of antibiotic-loaded hydrogels as biomaterials that provide good healing of superficial wounds (Figure 6).Figure 6
Rat wounds after removal of bandages (24 h): (a) classic gauze dressing (the wound was opened after the animal’s motor activity); (b) miramistin-loaded D500-g-PAA-0.4 hydrogel; (c) cefuroxime-loaded D500-g-PAA-0.4 hydrogel.
(a)(b)(c)


## 4. Conclusions

D/SD-g-PAA-based hydrogels are promising materials for the development of antimicrobial dressings for the protection and treatment of superficial wounds. As shown, the structure of hydrogels can be controlled at the stage of synthesis. These hydrogels can be loaded with the desired amount of antibiotics, ensuring that the drug is delivered to the desired site without systemic overdose. The synthesized antimicrobial hydrogels can be prepared in the shape and size required for the wound. It has been shown that the release of the antibiotic is slower for antibiotic-loaded D/SD-g-PAA hydrogels compared to PAA-based hydrogel with the same number of cross-links, which is beneficial for wound healing. Testing of cefuroxime-loaded hydrogels on infected rat wounds has shown rapid clearance and healing of the infected wounds.



---