# Bulk Behavior of Ball Milled AA2124 Nanostructured Powders Reinforced with TiC

Authors: Hanadi G. Salem; Sherif El-Eskandarany; Amr Kandil; Hassan Abdul Fattah
Journal: Journal of Nanomaterials
 (2009)

---

## Abstract

In the current research work, a top-down approach was employed for the refinement of a micron scale AA2124 alloy powder 40μm in average size using high-energy ball milling up to 60 hours. The produced nanopowders were investigated compared to the micron gas atomized powder both in the monolithic and the reinforced composite states. 1 μm powder of TiC with internal structure <100 nm was used for the reinforcement of the 2124-Al matrices. Milling time of 36 hours produced a <100 nm nanopowders with internal structure size <20 nm. The nanopowder monolithic consolidates exhibited compressive strength of 388 MPa compared to 313 MPa for micronpowder one. Addition of TiC nanostructured powder to the nanopowder consolidated matrix resulted in increase of 130% in compressive strength compared to that produced for the microscale one. Nanopowder of Alalloys produced by mechanical milling reinforced with 10 wt% TiC is recommended for products suitable for high wear and erosion resistance applications. Peak aging increased the hardness and compressive strength of the  as  compacted micronpowder matrices by an average of 188% and 123%, while increased that of the nanopowder matrices by an average of 110% and 117%, respectively.


---

## Body

## 1. Introduction

Composite materials are known  for their multiple functionalities due to the ability of tailoring the composite properties through controlling the type, composition, and morphology of the matrix and reinforcement. Metal Matrix Composite (MMC) has been developed to meet specific properties that cannot be met by a monolithic material regardless of its composition or processing technique (thermomechanical treatment). MMC can be tailored in different methods depending on the type and shape of the reinforcing phase (dispersion, particulate, whiskers, or fiber) and the consolidation technique produced to produce the bulk product [1]. The sintering behavior of metal matrix nanocomposites has been investigated for different matrices such as Ti [2], Cu [3], and Al-matrices [1, 4–9] with various ceramic reinforcements. Ti and Al-powders suffer from the formation of an oxide stable and brittle film, which strongly influences the consolidation behavior of the produced consolidates and hence their mechanical and physical properties [2].Metal matrix composites reinforced with ceramic reinforcements have been extensively studied over the last two decades for their significant use in aerospace aircraft, automobile, and military applications [4–9]. Reinforcement of micron scale ceramic particles used to improve the yield and ultimate strength of the matrix metal on the expense of loosing toughness and ductility.  Al-composites exhibit high specific strength and modulus, low density. AA2024 metallic powders became of great interest as matrices suitable for particulate reinforcement with ceramic powders especially SiC [10–13].Carbides, oxides, and nitrides powder have been used extensively for the reinforcement of Alalloys. In specific, SiC and Al2O3 were the commonly used ceramic reinforcements.  TiC was not investigated enough as a ceramic reinforcement to Alalloys; however, it has been receiving much attention lately for its high melting temperature (3373 K), low thermal coefficient of expansion, extraordinary hardness, excellent wear, and abrasion resistance [14]. The MMC processing parameters have a significant effect on the properties of the produced bulk product. Amongst those parameters, we have type size and shape of both the metallic matrix and the reinforcement particles, as well as the consolidation technique, pressure, temperature, and time. Many studies focused on the effect of the particle size of the matrix relative to the reinforcement within the microscale [4–9]. Other studies focused on the powder consolidation process including hot compaction, Hot and cold isostatic pressing followed by sintering and recently, plasma activated sintering [8, 9].Nanostructured materials exhibit relatively high interfacial energy compared to microstructural materials. The amount of energy stored by the nanostructured materials depends very strongly on the sensitization and processing techniques used for producing Bulk nanostructures material (BNSM). Several techniques have been employed for the synthesis of nanopowders, such as powder atomization and mechanical milling [15–17]. Mechanical milling especially ball milling produces nanopowders with very high stored energy induced by the continuous impact of the powder particles with stainless steel balls. The nature of interaction of the hardened balls and powder particles results in the strain hardening of the particles followed by their fragmentation into finer ones [18]. The amount of stored energy depends on the type of material, the milling time, speed, and temperature.  For Alalloys, grain size of 20nm was reported by Lin et al. [19], which was measured using XRD patterns and observed by TEM.Nanoscale materials have been the subject of major interest in recent years due to the anticipated ultrahigh strength and toughness combination that can be achieved in contrast to materials with conventional meso and microscale structures [1–3]. Reinforcement with nanoscale ceramic powders or the use of nanostructured powders of both the matrix and reinforcement producing nanocomposites derived the attention of the researchers to produce ultrahigh strength/tough MMCs.  The key issue lies in the optimization of the processing parameters suitable for the production of BNSM with superior properties suitable for high and cryogenic temperature applications. It has been reported that extrusion of a cryomilled nanostructured Al-Mg alloy with grain size of 20–30 nm resulted in grain size coarsening up to 90 nm [19]. The degree of grain size coarsening is significantly affected by the alloying elements in the Al alloy, which controls the thermal stability of the powder during the consolidation stages.Consolidation of bulk products starting from nanopowders represents an additional challenge for materials designed with superior properties. BNSM produced from the consolidation of mechanically milled powders could produce products with promising superior properties due to the relatively produced fine high energetic hard powders. On the other hand, the high hardness induced in the milled powder particles retards the particles’ deformation during the compaction stages that is necessary for filling the empty spaces formed in between the particles to enhance consolidation. Accordingly, this research aims for the production of sound BNS consolidates of nanopowders with improved mechanical properties over those of the micron powder of the same material. This involves the fabrication of a nanoscale AA2124 powder by mechanical milling of a microscale as-received powder using high-energy ball milling. Influence of the hot compaction parameters on the consolidation behavior of the milled powders compared to the as-received one is investigated.  Effect of ceramic nanopowders reinforcement additions on the consolidation behavior of both matrices is also investigated.


## 2. Materials and Experimental Procedure

In the current research, a top-down approach was employed for the refinement of a gas atomized micronpowders of AA2124 alloy with particle size ranging between 5–85μm with an average size of 40 μm.  The as-received AA2124 and TiC powders were supplied by the Aluminum powder Company limited (APC) and Mitsuwa Chemicals Co. LTD, respectively. The chemical composition for the Al 2124 powder and TiC is shown in Table 1. The TiC particle size ranged between 0.85–5 μm with an average size of 1.0 μm. The refinement process was conducted using a FRITCH high-energy ball milling up to 60 hours at 500 rpm in agate jars with ball-to-powder ratio of 30:1. The ball milling investigation intervals were 6, 12, 24, 36, 48, and 60 hours. Density measurement and the effect of the sample aspect ratio h/d (height-to-diameter ratio) were characterized for the compact produced from powders milled for 24 and 36 hours compared to the as-received one. Influence of the matrices powder size and mechanical properties on the TiC ceramic reinforcement distribution was investigated for the 0-hour powders (as-received micronpowder) and powders milled for 24 hours (nanopowders). A turbula mixer was employed for the production of mixtures of 5, 10, and 20 wt% of the 1 μm TiC powder in both matrices.Table 1
Chemical composition (wt%) of the AA2124 metallic matrix and TiC powders.
Matrix PowderCuMgMnSiFeAlAA21243.8–4.01.4–1.60.5–0.70.1max0.1maxBalanceReinforcement PowderTotal CFree CFeN2O2WaxTiTiC19.710.160.200.300.870.15BalanceX-ray diffraction was used to determine the crystallite size of the milled powders compared to the as-received one. The X-Ray diffractometer used is a Diano Co, energized at 45 kV and 10 mA with a dead time of less than10-6 seconds. A step scanning mode using Ni-filter CuKα radiation was used to determine the crystallite size and to trace any structural changes that might have taken place during the refinement of the AA2124 powder during milling. A Leo high resolution filed emission scanning electron microscope (SEM) was employed to characterize the milled powder morphology and the topology of the compact samples.The as-received and milled powders were consolidated into compacts using cold and hot unidirectional pressing at 624 MPa with a pressing holing time of 30 minutes. Tool steel die with an inner diameter of 20 mm was used to consolidate the samples at 480°C (0.75Tm). Height-to-diameter aspect ratios (h/d) of 0.25, 0.5, and 1.0 for the compact samples were investigated for the micron (as-received) and nanoscale (24 hours MT) matrices with and without TiC additions.   A Licka optical microscope was used to investigate the microstructural evolution of the hot compacts (HCs) as a function of the various compaction parameters. Vickers microhardness was used to determine hardness of the consolidates using a Mitutoyo microhardness tester. The VHN measurements was conducted at 200 gm for 15 seconds of dwell time. A minimum of 5 indentations were measured per condition. Compressive strength of the produced consolidates was evaluated using round 20 mm diameter and 5 mm height discs. A 50 tons MTS Universal testing machine was employed for conducting the compression tests at a cross-head speed of 0.5 mm/min. A minimum of 3-samples per condition was tested for compression, the average of which was reported.


## 3. Results and Discussion

In the current work, particle morphology and structure size were characterized for the ball milled as-received AA2124 powder for periods of 6, 12, 24, 36, 48, and 60 hours. Densification of the compact AA2124 powders was characterized for the 0, 24, and 36 hours milling times.


### 3.1. Influence of Mechanical Iteration on the AA2124 Micronpowders

Figure1 shows the SEM images of the milled powders after 0, 6, 12, 24, 36, 48, and 60 hours of milling time. The as-received microscale Al-powder was made of irregular shaped particles with maximum size of 85 μm and about 60 vol.% of the particles with sizes <40 μm (Figure 1(a)). Figure 2 shows the corresponding XRD patterns for the powders as a function of the milling time (MT). After 6 hours of MT, the powder particles were severely deformed and agglomerated into disc-like flaky particles with 6–63 μm in size and 2–12.7 μm in thickness. This was a result of the repeated welding during milling. This agrees with the observations made by Chen et al. who investigated the effect of milling time on Ni-Al alloys [20]. Further milling resulted in increased deformation and strain hardening, and hence the agglomerated discs were disintegrated into fragments of finer cluster ranging between 1–30 μm in size (Figure 1(c)). Milling up to 24 hours produced spherical-shaped clusters of particles ranging between 5–45 μm. Those clusters were made of very fine particles <300 nm in size, which were revealed easily at higher magnifications. Some of the refined powder was also observed separately scattered between the clusters (Figure 1(d)). Increasing the MT up to 36 hours produced ultrafine feathery like-shaped nanoscale powder <100 nm in size that was agglomerated in clusters ranging between 2–30 μm in size (Figure 1(e)). Milling the Al-powder for 48 followed by 60 hours did not result into further reduction of the individual particles’ size below that produced at 36 hours; however, the cluster morphology developed into a more spherical well-defined clusters ranging between 0.3–11 μm in size as shown in Figure  1(f). X-ray diffraction peaks from the (200)Al planes show a significant decrease in intensity as well as broadening with increasing the MT from 0 to 60 hours.AA2124 particle morphology evolution with increasing milling time (a) 0 hour, (b) 6 hours, (c) 12 hours, (d) 24 hours, (e) 36 hours, and (f) 60 hours.
(a)(b)(c)(d)(e)(f)Effect of milling time on (a) X-ray diffraction(200)Al peak and (b) crystallite size.
(a)(b)To determine the powder grain size (D), broadening of X-ray diffraction peaks from the (200)Al planes was employed for substitution in Scherrer’s equation [5, 21]. Figure 2 shows the effect of milling time on the intensity and broadening of the (200)Al peaks at 2θ=44°. Increasing the MT to 6 hours resulted in a significant refinement of the crystallite size from an average of 78-to-32 nm as shown in Figure 2(b). Further milling resulted in a gradual refinement in the crystallite size to a minimum of 15.6 nm at 36 hours of milling time. Increasing the MT above 36 hours did not result into further structural refinement. The observed slight increase in crystallite size up to 17.7 nm although insignificant could be due to the heat generated during the long period of MT up to 60 hours, which may result into coarsening of the nanoscale structure. Milling beyond 60 hours is necessary to trace the structural behavior with increasing MT.


### 3.2. Influence of the Powder Particle Morphology and Its Grain Size on the Green Compact Properties

The effect of particle size on the compaction relative density of the compacts was investigated. Milling times of 0, 24, and 36 were selected for this analysis. Figure3 shows high magnification SEM images for the powders, which reveals the internal structure refinement of the powder as a function of milling time. The as-received powder (Figure 3(a)) shows that the powders have smooth surfaces with orange skin-liked topology, which represents a typical morphology for the gas atomized powders. The average size of the observed internal structures was about 350 nm. Finer particles do not reveal their internal structure which could be due to being much finer than that measured for the coarser particles. Powder milled for 24 hours shows clusters of fine particles with evidence for excessive deformation. Fine grains <88 nm in size were revealed (marked by arrows in Figure 3(b)). Increasing the milling time to 36 hours revealed the formation of much finer clusters heavily deformed and very fine internal structure <40 nm in size (marked by arrows in Figure 3(c)). This agrees to a great extent with the crystallite size measurements produced by EDX analysis (Figure 2(a)).SEM micrographs for the (a) as-received powder, (b) 24 hours MT, and (c) 36 hours MT.
(a)(b)(c)Cold compaction was conducted in a die 20 mm in diameter for powder volumes that produced h/d ratios of 0.25, 0.5, and 1.0 at a constant pressure of 624 MPa for 30 minutes. Effect of particle size on the extent of densification was determined by Archimedes’ principle using three randomly selected samples [22].  Figure 4 shows the effect of milling time on the degree of densification as a function of h/d ratio. Obviously, increasing the MT led to a decrease in the powders’ particle size from an average of 40 μm-to-90 nm produced green compacts with a lower density regardless of the h/d ratio. On comparing the effect of h/d ratio on the percent decrease in density for the 40 μm (24 hours) and 90 nm (36 hours) particle sizes, about 13.4% and 7.5% were measured for h/d ratio of 0.25 and 1.0, respectively. This indicates that smaller h/d ratio not only produced higher green compact densities but also improved the densification of the nanoscale particles compared to the microscale one.Figure 4
Effect of MT on the relative change in density of GC produced at compaction pressures of 624 MPa for 30 minutes and h/d ratios of 0.25, 0.5, and 1.0.Figure5 shows high resolution SEM images at low and high magnifications for the 40 μm (0 hour), 300 nm (24 hours) and 90 nm (36 hours) green compact powder at h/d ratio of 0.25. It is observed that the 0 hour particles formed large porosity at triple points although finer particles were entrapped between the bigger ones. The 36 hours milled powder shows more uniform distribution of the pores in between the fragmented hard fine particles. For the 24-hour milled powders, particle refinement increased the particle-to-particle contact surfaces, which reduced porosity. Higher magnification images revealed clearly the internal structure of the as-received 0 hour powders, which was about 500 nm in average size. On the other hand the milled powders for 24 and 36 hours images did not reveal the internal structure due to the intensity of plastic deformation induced by milling. The nanopowder green compaction behavior can be attributed to the resistance of the strain hardened nanopowders to the imposed pressure compared to that of the micronpowder, which agrees with the observations made by  Srivatsan et al. [23].SEM images at low and high magnifications for the (a) 40μm, (b) 300 nm, and (c) 90 nm green compact powders with 0.25 h/d ratio, respectively.
(a)(b)(c)(d)(e)(f)


### 3.3. Effect of  TiC-Wt% Reinforcement Additions on the Micro and Nanopowder AA2124 Matrices

The consolidation behavior of the as-received gas atomized micronpowder (40 nm particle size with 78 nm crystallite size) and the 24-hour milled nanopowders (300 nm particle size with 20 nm crystallite size) were mixed with 0, 5, 10, and 20 TiC wt% nanostructured powders. Figure6 shows SEM micrographs at low and high magnifications for the TiC powder. The TiC particles are random in shape and range between 140 nm-5 μm in size.Figure 6
SEM images for (a) as-received microcrystalline micronpowder, (b) Nanocrystalline nanopowders milled 24 hours, (c) TiC powder, and (d) compaction conditions of the produced mixtures.Characterization of the consolidation behavior of the produced nanocomposites was conducted for the green and hot compacts. After mixing of the powders, a compaction load of 624 MPa for 30 minutes and 0.25 h/d ratio were used for cold compaction. Figure7 shows the effect of adding TiC nanostructured powder on the degree of densification of the AA2124 micro and nanopowders after cold compaction. It is clear that the observed decrease in density with the refinement of the powder from the micron to the nanoscale level of the bare matrix (Figure 4) was carried over to the produced densities of the reinforced condition for both the green and hot compacts. Hot compaction of the unreinforced matrices, however, resulted in a significant increase in density of both powders, especially for the nanoscale one. A 7% versus 2.4% increase in relative density was measured for the nano and microscale powders by hot compaction, respectively. It is suggested that powder milling for 24 hours resulted in the strain hardening of the produced powders, which hindered the deformation of the powder particles under the applied load used during cold compaction which resulted in the measured low density (92%). Conversely, the as-received micronpowder produced by gas atomization is expected to be relatively soft, which facilitated the deformation and hence resulted in filling of the empty spaces between the individual powder particles. This could be sustained by the observations made in Figures 5(a) and 5(b). Heating of the nanopowders under pressure allowed for the sliding of fine individual nanoparticles and the small clusters to slide in between the coarser clusters, which enhances the densification of the produced hot compacts.Figure 7
Effect of TiC addition on the density variation of the micro and nanopowder matrices green and hot compacts.5 wt% addition of TiC did not result in a noticeable change in the densification degree for both types of hot compact matrices. However, increasing the TiC content resulted in a significant decrease in relative density as shown in the figure. Further addition of TiC to both matrices resulted in deterioration in density of the produced compacts; although, hot compactions resulted in a significant enhancement in density. 9% and 7.4% increase in density was achieved by hot compaction of the nano and microscale reinforced matrices with 20 wt% TiC, respectively.Figure8 shows the SEM micrographs for the microscale and nanoscale Al matrix green compacts reinforced with 0, 5, 10, and 20 wt% TiC.   It was observed that reinforcement of the AA2124 matrices with 5 wt% TiC resulted in the formation of isolated large voids especially in the microscale particles, which explains the significant decrease in density. It is clear that local diffusion between the micronparticles without reinforcement (Figures 8(a)–8(d)) was reduced significantly due to the accumulation of the TiC fine particles on the surface of the Al matrix particles. The difference in particle size of the TiC particles compared to the Al matrix particles promoted the lack of uniform distribution of the reinforcement within the matrix and hence resulted in the observed drop in density that was observed in Figure 7. Conversely, the nanoscale Al matrix did not suffer a significant drop in density by adding TiC particles compared to the unreinforced condition (Figure 8(e)) due to the size compatibility with the matrix fine agglomerates, which can be observed at higher magnification images shown in Figures 8(f)–8(h).High magnification SEM micrographs for the micro (a)–(d) and nanoscale (e)–(h) green matrices reinforced with 0, 5, 10, and 20 wt% TiC, respectively. Arrows point at TiC particles.
(a)(b)(c)(d)(e)(f)(g)(h)In the microscale matrix composite green compacts (Figures8(b) and 8(c)) the observed pores were formed between the individual particles, while in the nanopowder matrix two types of pores were observed (a) large interagglomerate pores and (b) small pores between the individual nanoparticles (Figures 8(f) and 8(g)). It is clear that localization of the reinforcement is occurring between the particles of the nanoparticles and the agglomerates of the nanopowder clusters. This agrees with the findings of Srivatsan et al. [23].  Previous investigations revealed that a green compact densification can increase if the applied pressure during compaction breaks down the agglomerates, which produces homogeneous small interparticle pore distribution. This in turn will improve the consolidate properties. Breaking down of the agglomerated cluster depends on the powder fabrication method, which controls the degree by which the agglomerated clusters resist deformation [23].The observed decrease in density with addition of TiC to the nanopowder matrix disagrees with the produced increase in density observed by El-Eskandarany, who investigated the effect of adding SiC to Al matrix [8]. This could be explained by the difference in processing of the nanocomposites in both cases. El-Eskandarany produced the nanoscale composite through the simultaneous ball milling of SiC reinforcing particles with the Al matrix and produced Al/SiC nanocomposite particles made out of uniformly distributed nanoparticles of the reinforcement phase encapsulated within Al matrix. Hence the densification process is expected to be different from that used in the current research, where the Al matrix was first refined via ball milling into the nanopowder matrix followed by mixing it with the TiC particles. This could have resulted in the segregation of the reinforcing particulates along the boundaries between the Al matrix nanoparticles. As a result a lack of diffusion between the particles occurred and hence increased the void volume fraction. This was confirmed through investigation of the green compact specimens using SEM.In order to investigate the mechanical behavior of HC micronpowder versus the nanopowder with and without TiC reinforcement, microhardness testing was conducted. Note, the microhardness testing investigates the particle-to-particle bond strength regardless of the densification degree, since the performed indentations were conducted only in dense consolidated regions on the surface of the specimen. Figure9 shows the effect of TiC additions on the VHN-values produced for both the micro and nanoscale hot compacts matrices.Figure 9
A graph showing the Effect of TiC addition on the microhardness for the as-received micron and nanopowder consolidated HC.It is observed that the hardness of the monolithic nanopowder HC is higher than that of the micron one by 343%. Similar observations were made by Chen et al., on nanocrystalline NiAl milled powders [20].  Addition of 5 wt% TiC to the nanopowder HC resulted in a 124% increase in hardness of the monolithic one compared to an increase of 132% for the micronpowder HC. Increasing the TiC-content beyond 5 wt% did not result in a noticeable increase in hardness, especially for the nanopowder compacts, while a gradual increase in hardness was observed for the micronpowder matrix reinforced with up to 20 wt%.The compressive strength measured for the AA2124/TiC composite materials obtained by hot compaction for the micro and nanopowder compact matrices with and without TiC reinforcement is displayed in Table2 and Figure 10.  It is observed that refinement of the micronpowder to the nanoscale level by ball milling produced hot compact discs not only with significantly enhanced hardness values, but also with enhanced compressive strength. The nanopowder monolithic consolidates exhibited compressive strength of 388 MPa compared to 313 MPa for micronpowder one, which represents a 123% improved compressive strength. Addition of TiC nanostructured powder up to 20 wt% to the nanopowder consolidated matrix resulted in an average increase of 130% in compressive strength compared to that produced for the microscale one. From the diagram it is obvious that 10 wt% TiC produced the highest compressive strength for both matrices, which decreased with increasing the content up to 20 wt%.Table 2
Effect of TiC additions to the micron and nanopowder matrices.
TiC wt%Compressive strength (MPa)  (micronpowder matrices)Compressive strength (MPa)        (nanopowder matrices)0313.663895357.84493.2310415.55538.5720373.65507.47Figure 10
Compressive strength of HC micro and nanopowder consolidates as a function of TiC additions.Investigation of the hot compacts microstructure at low and high magnification (Figure11) explained the difference in VHN-values for both matrices. The consolidated micronpowder particle size was measured to be <50 μm (Figure 11(a)) for the grain size 2 μm in average size (Figure 11(b)). On the other hand, the ultrafine structure size produced by hot compaction of the nanopowders was not revealed by optical microscopy as shown in Figures 11(c), 11(d).  This suggests the possibility of retaining the nanoscale internal structure but as well as the nanoscale refined powder produced by 24 hours of MT. High strain hardening and stored energy in the nanostructure induced by the prior high-energy ball milling explain the observed improvement in hardness and compressive strength over the micronpowder consolidates. Additional investigations using transmission electron microcopy (TEM) is essential for the observation of the produced nanoscale structure along with the dislocation density after sintering.Optical micrographs at low and high magnifications showing the microstructure of the hot compact discs produced for the monolithic (a), (b) micronpowder and (c), (d) nanopowder HC AA2124.
(a)(b)(c)(d)Figure12 shows the microstructural evolution as a function of TiC additions at magnifications images for the micron and nanopowder matrices, respectively. TiC-content increase within the micronpowder matrices above 5 wt% shows an increase in the voids size and volume fraction as shown in the low magnification images (Figures 12(c)-12(d)).  For the nanopowder HC matrices, TiC addition even with 5 wt% resulted in the formation of isolated voids which coalesced into larger voids and cavities when TiC content increased to 10% and 20% as shown in Figures 12(e)-12(f). Cavity and void formation was persistent in both matrices, especially for the AA2124/20%TiC composite. It is suggested that the difference in thermal coefficient of expansion between the AA2124 matrices and the TiC resulted in the observed voiding during the cooling stage after HC.OM micrographs showing low magnification images for the (a)–(d) micronpowder 0, 5, 10, and 20%, and (e)–(h) nanopowder 0, 5, 10, and 20% consolidated HC matrices, respectively.
(a)(b)(c)(d)(e)(f)(g)(h)Figure13 shows that higher magnification images show an increase in preferential clustering of the reinforcement phase along the matrix particles’ boundaries and triple points with the increase in TiC-content as shown in Figures 13(a)–13(d). Reinforcement segregation between the interstices of the relatively coarse micronpowder matrix particles during the compaction stage resulted in the formation of the reinforcement network particles along the matrix boundaries. The relative particle size (RPS) ratio of the matrix-to-reinforcement could be the cause of the observed segregation. Similar conclusions were depicted by Prasad et al. who investigated the effect of the RPS ratio of AA2124-to-SiC [6]. Their studies showed that lower RPS ratio results in enhanced distribution of the reinforcement phase within the matrix and hence results into higher densification and improved mechanical properties.OM micrographs showing high magnification images for the (a)–(d) micronpowder 0, 5, 10, and 20%, and (e)–(h) nanopowder 0, 5, 10, and 20% consolidated HC matrices, respectively.
(a)(b)(c)(d)(e)(f)(g)(h)Comparing the reinforced nanopowder HC matrices (Figures13(e)–13(h)) with that of the micronpowder one (Figures 13(a)–13(d)), it is clear that the TiC particles were uniformly distributed within the nanopowder matrix with no signs of clustering along the matrix boundaries or triple points. An extremely strained matrix kinking around the TiC particles is shown at higher magnifications in the areas free from voids and cavities. It is worth noting that RPS ratios of 45:1 and 8:1 were measured for the micronpowder and nanopowder HC matrices, respectively, compared to those of the TiC reinforcement. Many studies were conducted on the effect of RPS ratio on Al-base alloys reinforced with ceramic particles [6, 24, 25].The observed intense matrix deformation around the TiC particles in addition to the strain hardening effect induced by ball milling of the matrix powder explains the exhibited increase in VHN values and compressive strength measured for the Nanopowder consolidated matrices compared to the micronpowder one. AA2124 is a precipitation-hardenable alloy that contains different kind of second phase particles most important of which is the Cu-rich phases which are responsible for the strengthening of the alloy on aging [1]. It is suggested that the diffusion mean free path of the Cu element is strongly affected by the reinforcement distribution within the matrix. The higher the RPS ratio, the higher the diffusion mean free path of Cu within the matrix which results in the segregation of the Cu rich phase within the reinforcement clusters and hence poor properties.Further investigation is required to understand the consolidation behavior and deformation mechanism of the nanopowder matrix compared to the micropowder one with and without reinforcement. One of the major causes that might have contributed to the formed cavities is the problem of entrapped air pockets within the individual particles and agglomerates. The powder compaction stage was done in open air without the use of vacuum or inert gas. A much improved consolidation behavior is expected under controlled atmosphere. Moreover, metal forming after cold or hot compaction will without doubt increase density and hence enhance the mechanical behavior of the consolidated bulk specimens.Investigation of the effect of aging time at 175°C was also investigated for the micron and nanopowder matrices in the monolithic and reinforced conditions. Table3 shows the peak aging time for each condition as well as the exhibited VHN-values and compressive strength.Table 3
Effect of aging at 175°C on peak aging time, hardness, and compressive strength.
TiC (wt.%)Micronpowder matricesNanopowder matricesPeak aging time (min)VHNσComp (MPa)Peak aging time (min)VHNσComp   (MPa)056019037753030545854301954533603655401030022050827037563620190242464180425624From Table3, it is clear that increasing content of TiC to both matrices resulted in decreasing the peak aging duration from about 9 to 3 hours for the matrices reinforced with 0 up to 20 wt% TiC, respectively. On the other hand, the peak aging time recorded for the micron and nanopowder matrices was almost the same for all conditions. Peak aging increased the hardness of the as compressed micronpowder matrices (Figure 9) by an average of 188%, while increased that of the nanopowder matrices by an average of 110%. In addition, peak aging resulted in increasing the compressive strength of the micron and nanopowder matrices was 123% and 117% in average, respectively. This indicates that solution heat treatment at 500°C for 1 hour followed by peak aging at 175°C for hours did not result in the loss of the mechanical properties of the milled powders, but rather enhanced the mechanical properties. In order to explain the nanopowder mechanical behavior post solutionizing and aging structural evolution compared to that of the micronpowder matrices with and without reinforcement microstructural investigation is currently under investigation.Comparing the continuously cast and rolled sheets of AA2124-T851 properties with those produced for the investigated 24 hours milled powder consolidates in the T6 temper condition, it is found that a hardness of 146 HV versus 309 HV is produced, respectively. In addition, the hot compact nanopowders reinforced with only 10 wt% TiC displayed compressive strength that is higher (636 MPa) than MMC of AA2124 micronpowder (75μm particle size) reinforced with either 10% BN or 15% Al2O3  processed by a combined cold uniaxial compaction followed by conventional extrusion at 480°C with an extrusion ratio of 3.25:1  [26]. This indicates a significant improvement in the load bearing capacity and durability of the fabricated Al-based nanocomposites, especially for applications that requires high performance at relatively high operating  temperatures.


## 3.1. Influence of Mechanical Iteration on the AA2124 Micronpowders

Figure1 shows the SEM images of the milled powders after 0, 6, 12, 24, 36, 48, and 60 hours of milling time. The as-received microscale Al-powder was made of irregular shaped particles with maximum size of 85 μm and about 60 vol.% of the particles with sizes <40 μm (Figure 1(a)). Figure 2 shows the corresponding XRD patterns for the powders as a function of the milling time (MT). After 6 hours of MT, the powder particles were severely deformed and agglomerated into disc-like flaky particles with 6–63 μm in size and 2–12.7 μm in thickness. This was a result of the repeated welding during milling. This agrees with the observations made by Chen et al. who investigated the effect of milling time on Ni-Al alloys [20]. Further milling resulted in increased deformation and strain hardening, and hence the agglomerated discs were disintegrated into fragments of finer cluster ranging between 1–30 μm in size (Figure 1(c)). Milling up to 24 hours produced spherical-shaped clusters of particles ranging between 5–45 μm. Those clusters were made of very fine particles <300 nm in size, which were revealed easily at higher magnifications. Some of the refined powder was also observed separately scattered between the clusters (Figure 1(d)). Increasing the MT up to 36 hours produced ultrafine feathery like-shaped nanoscale powder <100 nm in size that was agglomerated in clusters ranging between 2–30 μm in size (Figure 1(e)). Milling the Al-powder for 48 followed by 60 hours did not result into further reduction of the individual particles’ size below that produced at 36 hours; however, the cluster morphology developed into a more spherical well-defined clusters ranging between 0.3–11 μm in size as shown in Figure  1(f). X-ray diffraction peaks from the (200)Al planes show a significant decrease in intensity as well as broadening with increasing the MT from 0 to 60 hours.AA2124 particle morphology evolution with increasing milling time (a) 0 hour, (b) 6 hours, (c) 12 hours, (d) 24 hours, (e) 36 hours, and (f) 60 hours.
(a)(b)(c)(d)(e)(f)Effect of milling time on (a) X-ray diffraction(200)Al peak and (b) crystallite size.
(a)(b)To determine the powder grain size (D), broadening of X-ray diffraction peaks from the (200)Al planes was employed for substitution in Scherrer’s equation [5, 21]. Figure 2 shows the effect of milling time on the intensity and broadening of the (200)Al peaks at 2θ=44°. Increasing the MT to 6 hours resulted in a significant refinement of the crystallite size from an average of 78-to-32 nm as shown in Figure 2(b). Further milling resulted in a gradual refinement in the crystallite size to a minimum of 15.6 nm at 36 hours of milling time. Increasing the MT above 36 hours did not result into further structural refinement. The observed slight increase in crystallite size up to 17.7 nm although insignificant could be due to the heat generated during the long period of MT up to 60 hours, which may result into coarsening of the nanoscale structure. Milling beyond 60 hours is necessary to trace the structural behavior with increasing MT.


## 3.2. Influence of the Powder Particle Morphology and Its Grain Size on the Green Compact Properties

The effect of particle size on the compaction relative density of the compacts was investigated. Milling times of 0, 24, and 36 were selected for this analysis. Figure3 shows high magnification SEM images for the powders, which reveals the internal structure refinement of the powder as a function of milling time. The as-received powder (Figure 3(a)) shows that the powders have smooth surfaces with orange skin-liked topology, which represents a typical morphology for the gas atomized powders. The average size of the observed internal structures was about 350 nm. Finer particles do not reveal their internal structure which could be due to being much finer than that measured for the coarser particles. Powder milled for 24 hours shows clusters of fine particles with evidence for excessive deformation. Fine grains <88 nm in size were revealed (marked by arrows in Figure 3(b)). Increasing the milling time to 36 hours revealed the formation of much finer clusters heavily deformed and very fine internal structure <40 nm in size (marked by arrows in Figure 3(c)). This agrees to a great extent with the crystallite size measurements produced by EDX analysis (Figure 2(a)).SEM micrographs for the (a) as-received powder, (b) 24 hours MT, and (c) 36 hours MT.
(a)(b)(c)Cold compaction was conducted in a die 20 mm in diameter for powder volumes that produced h/d ratios of 0.25, 0.5, and 1.0 at a constant pressure of 624 MPa for 30 minutes. Effect of particle size on the extent of densification was determined by Archimedes’ principle using three randomly selected samples [22].  Figure 4 shows the effect of milling time on the degree of densification as a function of h/d ratio. Obviously, increasing the MT led to a decrease in the powders’ particle size from an average of 40 μm-to-90 nm produced green compacts with a lower density regardless of the h/d ratio. On comparing the effect of h/d ratio on the percent decrease in density for the 40 μm (24 hours) and 90 nm (36 hours) particle sizes, about 13.4% and 7.5% were measured for h/d ratio of 0.25 and 1.0, respectively. This indicates that smaller h/d ratio not only produced higher green compact densities but also improved the densification of the nanoscale particles compared to the microscale one.Figure 4
Effect of MT on the relative change in density of GC produced at compaction pressures of 624 MPa for 30 minutes and h/d ratios of 0.25, 0.5, and 1.0.Figure5 shows high resolution SEM images at low and high magnifications for the 40 μm (0 hour), 300 nm (24 hours) and 90 nm (36 hours) green compact powder at h/d ratio of 0.25. It is observed that the 0 hour particles formed large porosity at triple points although finer particles were entrapped between the bigger ones. The 36 hours milled powder shows more uniform distribution of the pores in between the fragmented hard fine particles. For the 24-hour milled powders, particle refinement increased the particle-to-particle contact surfaces, which reduced porosity. Higher magnification images revealed clearly the internal structure of the as-received 0 hour powders, which was about 500 nm in average size. On the other hand the milled powders for 24 and 36 hours images did not reveal the internal structure due to the intensity of plastic deformation induced by milling. The nanopowder green compaction behavior can be attributed to the resistance of the strain hardened nanopowders to the imposed pressure compared to that of the micronpowder, which agrees with the observations made by  Srivatsan et al. [23].SEM images at low and high magnifications for the (a) 40μm, (b) 300 nm, and (c) 90 nm green compact powders with 0.25 h/d ratio, respectively.
(a)(b)(c)(d)(e)(f)


## 3.3. Effect of  TiC-Wt% Reinforcement Additions on the Micro and Nanopowder AA2124 Matrices

The consolidation behavior of the as-received gas atomized micronpowder (40 nm particle size with 78 nm crystallite size) and the 24-hour milled nanopowders (300 nm particle size with 20 nm crystallite size) were mixed with 0, 5, 10, and 20 TiC wt% nanostructured powders. Figure6 shows SEM micrographs at low and high magnifications for the TiC powder. The TiC particles are random in shape and range between 140 nm-5 μm in size.Figure 6
SEM images for (a) as-received microcrystalline micronpowder, (b) Nanocrystalline nanopowders milled 24 hours, (c) TiC powder, and (d) compaction conditions of the produced mixtures.Characterization of the consolidation behavior of the produced nanocomposites was conducted for the green and hot compacts. After mixing of the powders, a compaction load of 624 MPa for 30 minutes and 0.25 h/d ratio were used for cold compaction. Figure7 shows the effect of adding TiC nanostructured powder on the degree of densification of the AA2124 micro and nanopowders after cold compaction. It is clear that the observed decrease in density with the refinement of the powder from the micron to the nanoscale level of the bare matrix (Figure 4) was carried over to the produced densities of the reinforced condition for both the green and hot compacts. Hot compaction of the unreinforced matrices, however, resulted in a significant increase in density of both powders, especially for the nanoscale one. A 7% versus 2.4% increase in relative density was measured for the nano and microscale powders by hot compaction, respectively. It is suggested that powder milling for 24 hours resulted in the strain hardening of the produced powders, which hindered the deformation of the powder particles under the applied load used during cold compaction which resulted in the measured low density (92%). Conversely, the as-received micronpowder produced by gas atomization is expected to be relatively soft, which facilitated the deformation and hence resulted in filling of the empty spaces between the individual powder particles. This could be sustained by the observations made in Figures 5(a) and 5(b). Heating of the nanopowders under pressure allowed for the sliding of fine individual nanoparticles and the small clusters to slide in between the coarser clusters, which enhances the densification of the produced hot compacts.Figure 7
Effect of TiC addition on the density variation of the micro and nanopowder matrices green and hot compacts.5 wt% addition of TiC did not result in a noticeable change in the densification degree for both types of hot compact matrices. However, increasing the TiC content resulted in a significant decrease in relative density as shown in the figure. Further addition of TiC to both matrices resulted in deterioration in density of the produced compacts; although, hot compactions resulted in a significant enhancement in density. 9% and 7.4% increase in density was achieved by hot compaction of the nano and microscale reinforced matrices with 20 wt% TiC, respectively.Figure8 shows the SEM micrographs for the microscale and nanoscale Al matrix green compacts reinforced with 0, 5, 10, and 20 wt% TiC.   It was observed that reinforcement of the AA2124 matrices with 5 wt% TiC resulted in the formation of isolated large voids especially in the microscale particles, which explains the significant decrease in density. It is clear that local diffusion between the micronparticles without reinforcement (Figures 8(a)–8(d)) was reduced significantly due to the accumulation of the TiC fine particles on the surface of the Al matrix particles. The difference in particle size of the TiC particles compared to the Al matrix particles promoted the lack of uniform distribution of the reinforcement within the matrix and hence resulted in the observed drop in density that was observed in Figure 7. Conversely, the nanoscale Al matrix did not suffer a significant drop in density by adding TiC particles compared to the unreinforced condition (Figure 8(e)) due to the size compatibility with the matrix fine agglomerates, which can be observed at higher magnification images shown in Figures 8(f)–8(h).High magnification SEM micrographs for the micro (a)–(d) and nanoscale (e)–(h) green matrices reinforced with 0, 5, 10, and 20 wt% TiC, respectively. Arrows point at TiC particles.
(a)(b)(c)(d)(e)(f)(g)(h)In the microscale matrix composite green compacts (Figures8(b) and 8(c)) the observed pores were formed between the individual particles, while in the nanopowder matrix two types of pores were observed (a) large interagglomerate pores and (b) small pores between the individual nanoparticles (Figures 8(f) and 8(g)). It is clear that localization of the reinforcement is occurring between the particles of the nanoparticles and the agglomerates of the nanopowder clusters. This agrees with the findings of Srivatsan et al. [23].  Previous investigations revealed that a green compact densification can increase if the applied pressure during compaction breaks down the agglomerates, which produces homogeneous small interparticle pore distribution. This in turn will improve the consolidate properties. Breaking down of the agglomerated cluster depends on the powder fabrication method, which controls the degree by which the agglomerated clusters resist deformation [23].The observed decrease in density with addition of TiC to the nanopowder matrix disagrees with the produced increase in density observed by El-Eskandarany, who investigated the effect of adding SiC to Al matrix [8]. This could be explained by the difference in processing of the nanocomposites in both cases. El-Eskandarany produced the nanoscale composite through the simultaneous ball milling of SiC reinforcing particles with the Al matrix and produced Al/SiC nanocomposite particles made out of uniformly distributed nanoparticles of the reinforcement phase encapsulated within Al matrix. Hence the densification process is expected to be different from that used in the current research, where the Al matrix was first refined via ball milling into the nanopowder matrix followed by mixing it with the TiC particles. This could have resulted in the segregation of the reinforcing particulates along the boundaries between the Al matrix nanoparticles. As a result a lack of diffusion between the particles occurred and hence increased the void volume fraction. This was confirmed through investigation of the green compact specimens using SEM.In order to investigate the mechanical behavior of HC micronpowder versus the nanopowder with and without TiC reinforcement, microhardness testing was conducted. Note, the microhardness testing investigates the particle-to-particle bond strength regardless of the densification degree, since the performed indentations were conducted only in dense consolidated regions on the surface of the specimen. Figure9 shows the effect of TiC additions on the VHN-values produced for both the micro and nanoscale hot compacts matrices.Figure 9
A graph showing the Effect of TiC addition on the microhardness for the as-received micron and nanopowder consolidated HC.It is observed that the hardness of the monolithic nanopowder HC is higher than that of the micron one by 343%. Similar observations were made by Chen et al., on nanocrystalline NiAl milled powders [20].  Addition of 5 wt% TiC to the nanopowder HC resulted in a 124% increase in hardness of the monolithic one compared to an increase of 132% for the micronpowder HC. Increasing the TiC-content beyond 5 wt% did not result in a noticeable increase in hardness, especially for the nanopowder compacts, while a gradual increase in hardness was observed for the micronpowder matrix reinforced with up to 20 wt%.The compressive strength measured for the AA2124/TiC composite materials obtained by hot compaction for the micro and nanopowder compact matrices with and without TiC reinforcement is displayed in Table2 and Figure 10.  It is observed that refinement of the micronpowder to the nanoscale level by ball milling produced hot compact discs not only with significantly enhanced hardness values, but also with enhanced compressive strength. The nanopowder monolithic consolidates exhibited compressive strength of 388 MPa compared to 313 MPa for micronpowder one, which represents a 123% improved compressive strength. Addition of TiC nanostructured powder up to 20 wt% to the nanopowder consolidated matrix resulted in an average increase of 130% in compressive strength compared to that produced for the microscale one. From the diagram it is obvious that 10 wt% TiC produced the highest compressive strength for both matrices, which decreased with increasing the content up to 20 wt%.Table 2
Effect of TiC additions to the micron and nanopowder matrices.
TiC wt%Compressive strength (MPa)  (micronpowder matrices)Compressive strength (MPa)        (nanopowder matrices)0313.663895357.84493.2310415.55538.5720373.65507.47Figure 10
Compressive strength of HC micro and nanopowder consolidates as a function of TiC additions.Investigation of the hot compacts microstructure at low and high magnification (Figure11) explained the difference in VHN-values for both matrices. The consolidated micronpowder particle size was measured to be <50 μm (Figure 11(a)) for the grain size 2 μm in average size (Figure 11(b)). On the other hand, the ultrafine structure size produced by hot compaction of the nanopowders was not revealed by optical microscopy as shown in Figures 11(c), 11(d).  This suggests the possibility of retaining the nanoscale internal structure but as well as the nanoscale refined powder produced by 24 hours of MT. High strain hardening and stored energy in the nanostructure induced by the prior high-energy ball milling explain the observed improvement in hardness and compressive strength over the micronpowder consolidates. Additional investigations using transmission electron microcopy (TEM) is essential for the observation of the produced nanoscale structure along with the dislocation density after sintering.Optical micrographs at low and high magnifications showing the microstructure of the hot compact discs produced for the monolithic (a), (b) micronpowder and (c), (d) nanopowder HC AA2124.
(a)(b)(c)(d)Figure12 shows the microstructural evolution as a function of TiC additions at magnifications images for the micron and nanopowder matrices, respectively. TiC-content increase within the micronpowder matrices above 5 wt% shows an increase in the voids size and volume fraction as shown in the low magnification images (Figures 12(c)-12(d)).  For the nanopowder HC matrices, TiC addition even with 5 wt% resulted in the formation of isolated voids which coalesced into larger voids and cavities when TiC content increased to 10% and 20% as shown in Figures 12(e)-12(f). Cavity and void formation was persistent in both matrices, especially for the AA2124/20%TiC composite. It is suggested that the difference in thermal coefficient of expansion between the AA2124 matrices and the TiC resulted in the observed voiding during the cooling stage after HC.OM micrographs showing low magnification images for the (a)–(d) micronpowder 0, 5, 10, and 20%, and (e)–(h) nanopowder 0, 5, 10, and 20% consolidated HC matrices, respectively.
(a)(b)(c)(d)(e)(f)(g)(h)Figure13 shows that higher magnification images show an increase in preferential clustering of the reinforcement phase along the matrix particles’ boundaries and triple points with the increase in TiC-content as shown in Figures 13(a)–13(d). Reinforcement segregation between the interstices of the relatively coarse micronpowder matrix particles during the compaction stage resulted in the formation of the reinforcement network particles along the matrix boundaries. The relative particle size (RPS) ratio of the matrix-to-reinforcement could be the cause of the observed segregation. Similar conclusions were depicted by Prasad et al. who investigated the effect of the RPS ratio of AA2124-to-SiC [6]. Their studies showed that lower RPS ratio results in enhanced distribution of the reinforcement phase within the matrix and hence results into higher densification and improved mechanical properties.OM micrographs showing high magnification images for the (a)–(d) micronpowder 0, 5, 10, and 20%, and (e)–(h) nanopowder 0, 5, 10, and 20% consolidated HC matrices, respectively.
(a)(b)(c)(d)(e)(f)(g)(h)Comparing the reinforced nanopowder HC matrices (Figures13(e)–13(h)) with that of the micronpowder one (Figures 13(a)–13(d)), it is clear that the TiC particles were uniformly distributed within the nanopowder matrix with no signs of clustering along the matrix boundaries or triple points. An extremely strained matrix kinking around the TiC particles is shown at higher magnifications in the areas free from voids and cavities. It is worth noting that RPS ratios of 45:1 and 8:1 were measured for the micronpowder and nanopowder HC matrices, respectively, compared to those of the TiC reinforcement. Many studies were conducted on the effect of RPS ratio on Al-base alloys reinforced with ceramic particles [6, 24, 25].The observed intense matrix deformation around the TiC particles in addition to the strain hardening effect induced by ball milling of the matrix powder explains the exhibited increase in VHN values and compressive strength measured for the Nanopowder consolidated matrices compared to the micronpowder one. AA2124 is a precipitation-hardenable alloy that contains different kind of second phase particles most important of which is the Cu-rich phases which are responsible for the strengthening of the alloy on aging [1]. It is suggested that the diffusion mean free path of the Cu element is strongly affected by the reinforcement distribution within the matrix. The higher the RPS ratio, the higher the diffusion mean free path of Cu within the matrix which results in the segregation of the Cu rich phase within the reinforcement clusters and hence poor properties.Further investigation is required to understand the consolidation behavior and deformation mechanism of the nanopowder matrix compared to the micropowder one with and without reinforcement. One of the major causes that might have contributed to the formed cavities is the problem of entrapped air pockets within the individual particles and agglomerates. The powder compaction stage was done in open air without the use of vacuum or inert gas. A much improved consolidation behavior is expected under controlled atmosphere. Moreover, metal forming after cold or hot compaction will without doubt increase density and hence enhance the mechanical behavior of the consolidated bulk specimens.Investigation of the effect of aging time at 175°C was also investigated for the micron and nanopowder matrices in the monolithic and reinforced conditions. Table3 shows the peak aging time for each condition as well as the exhibited VHN-values and compressive strength.Table 3
Effect of aging at 175°C on peak aging time, hardness, and compressive strength.
TiC (wt.%)Micronpowder matricesNanopowder matricesPeak aging time (min)VHNσComp (MPa)Peak aging time (min)VHNσComp   (MPa)056019037753030545854301954533603655401030022050827037563620190242464180425624From Table3, it is clear that increasing content of TiC to both matrices resulted in decreasing the peak aging duration from about 9 to 3 hours for the matrices reinforced with 0 up to 20 wt% TiC, respectively. On the other hand, the peak aging time recorded for the micron and nanopowder matrices was almost the same for all conditions. Peak aging increased the hardness of the as compressed micronpowder matrices (Figure 9) by an average of 188%, while increased that of the nanopowder matrices by an average of 110%. In addition, peak aging resulted in increasing the compressive strength of the micron and nanopowder matrices was 123% and 117% in average, respectively. This indicates that solution heat treatment at 500°C for 1 hour followed by peak aging at 175°C for hours did not result in the loss of the mechanical properties of the milled powders, but rather enhanced the mechanical properties. In order to explain the nanopowder mechanical behavior post solutionizing and aging structural evolution compared to that of the micronpowder matrices with and without reinforcement microstructural investigation is currently under investigation.Comparing the continuously cast and rolled sheets of AA2124-T851 properties with those produced for the investigated 24 hours milled powder consolidates in the T6 temper condition, it is found that a hardness of 146 HV versus 309 HV is produced, respectively. In addition, the hot compact nanopowders reinforced with only 10 wt% TiC displayed compressive strength that is higher (636 MPa) than MMC of AA2124 micronpowder (75μm particle size) reinforced with either 10% BN or 15% Al2O3  processed by a combined cold uniaxial compaction followed by conventional extrusion at 480°C with an extrusion ratio of 3.25:1  [26]. This indicates a significant improvement in the load bearing capacity and durability of the fabricated Al-based nanocomposites, especially for applications that requires high performance at relatively high operating  temperatures.


## 4. Conclusions

In the current paper, we have what follows.(1)
Nanocrystalline-nanopowders<100 nm in particle size and 20 nm internal structural size were fabricated successfully by high-energy ball milling from a 40 μm particle  sized AA2124 powder with internal structure ranging between 53–300 nm in average size.(2)
The consolidation behavior of the micro and nano consolidated matrices was characterized in the monolithic condition and with addition of TiC ceramic nanostructured particles.(3)
The green compact densities of the nanoscale powder decreased to 92% compared to 97% for the micronpowder as-received powder.  This was due to the resistance of the strain hardened agglomerates to the applied pressure used for compaction.(4)
The degree by which the density decreased with the addition of 5 wt% TiC to the matrix was much lower for the nanoscale consolidated matrix compared to the micronpowder consolidated one due to the low RPS ratio between the matrix and the reinforcement, which promoted uniform distribution of the TiC particles within the matrix agglomerates.(5)
Increasing TiC content up to 10 wt% results in the formation of large voids and cavities, which reduces the compressive strength of the produced compacts, although hardness increases with TiC addition regardless of the content.(6)
Hardness and compressive strength increased by peak aging at 175°C for monolithic and composite consolidated nanostructured AA2124, which qualifies them for high performance load bearing light weight applications.(7)
Based on the current research nanopowder of Alalloys produced by 24 hours mechanical milling of gas atomized micronpowders reinforced with  10 wt%. TiC is recommended for products suitable for high wear and erosion resistance applications.(8)
Further investigation is required using TEM for microstructural analysis on the nanoscale level. In addition, investigation of the compressive strength of the produced compacts with and without heat treatment is also planned.



---