# Obtaining Hydrophobic Aerogels of Unbleached Cellulose Nanofibers of the SpeciesEucalyptus sp. and Pinus elliottii

Authors: Márcia Zanini; Alessandra Lavoratti; Lídia Kunz Lazzari; Deise Galiotto; Camila Baldasso; Ademir José Zattera
Journal: Journal of Nanomaterials
 (2018)

---

## Abstract

The use of natural fibers from renewable and biodegradable sources in oleophilic sorbents, such as cellulose, has become an interesting alternative due to their excellent properties and sustainability. In addition to that, the low density of the aerogels obtained from cellulose is favorable for their use as sorbents. In this context, the objective of this study is to develop hydrophobic aerogels of unbleached cellulose nanofibers of theEucalyptus sp. and Pinus elliottii. Cellulose samples were submitted to mechanical fibrillation to obtain cellulose nanofiber suspensions, followed by a chemical treatment with methyltrimethoxysilane and dried by freeze-drying to prepare the aerogels. The aerogels presented hydrophobic and oleophilic characteristics, including a water contact angle of 134°, sorption capacities in a heterogeneous medium of above 21.0 g·g−1, and oil removal efficiency greater than 88.5%. The Pinus elliottii nanofiber aerogels showed higher compressive strength when compared to the nanofiber aerogels of Eucalyptus sp.


---

## Body

## 1. Introduction

Water contamination by oil spills causes major environmental impacts. The consequences of these accidents can generate short-, medium-, and long-term impacts to the environment, as well as permanent and irreversible damage to the local ecosystem, affecting the environment and human health [1].The International Tanker Owners Pollution Federation is an organization which has a database of oil spills from oil tankers, transporters, and combined vessels. Accidents with oil spills are generally classified by the amount of oil spilled, such as small (less than 7 tons), medium (7–700 tons), and large (over 700 tons). According to statistics provided by this organization, in 2016 incidents considered small accounted for 81% of the occurrences. A large oil tank spill in the Gulf of Mexico with a cargo of approximately 5500 tons of gasoline and diesel, and four medium-sized spills of various oils, including crude oil, were also recorded. However, the total amount of oil spilled in the marine environment in 2016 was approximately 6000 tons [2].The most used strategies for the treatment of water contaminated with oil are as follows: oil extraction at the surface of the water, dispersion of the oil in the water with the use of chemical dispersants to facilitate natural degradation, and oil burning [3–5]. For the extraction of oil in water, the use of sorbents is considered a promising alternative due to the simplicity of the method. They can be used in the open sea, and the availability of automated systems minimizes workers’ exposure to chemical and toxic substances produced. There is also the possibility of recovering the oil, thus generating less environmental impact [5, 6].Oleophilic sorbents derived from renewable-source fibers, such as cellulose, can be promising alternatives in the treatment of oil-contaminated water. There is an increasing interest in research pertaining to the production of cellulosic oleophilic sorbents, since cellulose is the most abundant biopolymer of the planet from renewable sources. Cellulose is characterized as a linear polysaccharide consisting of D-glucose units linked together alternately, with its repeating unit called cellobiose, which is also present in plants, animals, and some bacteria. Wood is the main source of its production [7–10]. In Brazil, the main sources of cellulose are planted forests of the Pinus sp. and Eucalyptus sp., responsible for more than 98% of the national production [11]. Wood pulp fibers are one of the main source materials in several research areas, because they can be used for a number of applications, including reinforcement in composites, bioenergy feedstocks, source materials for biochemical production, and oleophilic sorbents [12, 13].Cellulose nanofibers (CNFs) are the smallest structures of the plant fibers. They have a nanometric diameter and a micrometric scale length, and a crystalline structure which alternates with amorphous domains [14–16]. CNFs present high stiffness, good tensile strength, and high surface area [17, 18]. These nanofibers are mainly obtained by the mechanical fibrillation of the wood pulp [19], and can be used as constituents of porous materials, such as filters and sorbents [20].Aerogels are solid, highly porous, and low-density materials from a suspension that has undergone a drying process in which the solvent is replaced by a gas without changing its molecular structure. For extraction of the solvent, it is necessary to subject it to a drying process, mainly using freeze-drying or supercritical drying [21]. Aerogels of cellulose nanofibers are highly resistant materials, with a low density, high rate of sorption, and high surface area. They have excellent properties to be used as oleophilic sorbents; however, it is necessary to subject these sorbents to a chemical treatment to obtain a hydrophobic and oleophilic material [22, 23].Many studies report obtaining cellulose aerogels with the addition of chemical solvents, for example, sodium hydroxide solutions, sodium hydroxide/urea solutions, N-methylmorpholine-N-oxide (NMMO), and calcium thiocyanate solutions [21]. Jin et al. [24] prepared aerogels from waste paper without pretreatment, using only 1-allyl-3-methyimidazolium chloride as a solvent to dissolve the material and freeze-drying it.Some studies on obtaining aerogels without the use of solvents have already been published. Korhonen et al. [3] made aerogels from a cellulose nanofiber suspension of homogenized hardwood kraft pulp, followed by freeze-drying and chemical functionalization with titanium dioxide. Zanini et al. [25] reported in their studies the obtainment of aerogels of bleached CNFs of the Eucalyptus sp. species without adding chemical solvents. Lazzari et al. [26] also obtained aerogels of unbleached CNFs of the Pinus elliottii species without the addition of solvents.The novelty of this research is the obtainment and evaluation of the sorption capacities of hydrophobic aerogels from unbleached CNFs ofEucalyptus sp. and Pinus elliottii without the addition of chemical solvents. Moreover, the use of unbleached cellulose waste could be advantageous to the production of these aerogels, since no bleaching process would be required, therefore generating fewer waste. In this study, the aerogels were obtained from mechanically fibrillated CNF suspensions. The contact angle, sorption capacity, and compressive strength were evaluated.


## 2. Materials and Methods

### 2.1. Materials

The following materials were used for the preparation of the aerogels: unbleached cellulose ofEucalyptus sp. (CE), unbleached cellulose of Pinus elliottii (CP) (both CE and CP were supplied by Rio Grande Companhia de Celulose do Sul, RS, Brazil), glacial acetic acid (provided by Neon), and methyltrimethoxysilane (MTMS) (98% purity purchased from Sigma-Aldrich). For the sorption experiments, SAE 20W50 motor oil with a viscosity of 64 cSt and a density of 0.88 g·cm−3 (20–40°C) was provided by Ipiranga Petrochemical (RS, Brazil). This oil was classified as a medium oil, according to ASTM F726-12.


### 2.2. Methods

#### 2.2.1. Production of the Aerogels

Cellulose fibrillation was performed by a mechanical process. The pulp was dispersed in distilled water with an initial concentration of 3% (wt%/v%). Grinding was conducted in a Masuko Sangyo stone disc mill, model MKCA6-2J with an adapted recirculation pump, for 5 hours with a rotation speed of 2500 rpm. Figure1(a) illustrates the mechanical grinding.Figure 1
Process for obtaining aerogels: (a) mechanical grinding, (b) chemical treatment, (c) freeze-drying process, and (d) aerogels.In order to obtain the aerogels’ hydrophobic properties, a chemical treatment of the suspensions with the use of the methyltrimethoxysilane (MTMS) was carried out at a concentration of 2% in mass, according to our previous work [25]. The CNF suspension was filtered through a vacuum system. The permeate pH was then adjusted to 3.0 by adding acetic acid under magnetic stirring for 5 min. Subsequently, 2% in mass of MTMS was added to this solution under magnetic stirring. The resulting solutions were slowly added dropwise into the MTMS supernatant filtration. The CNF suspension with MTMS was mechanically stirred at 500 rpm for 1 hour and kept in an oven at 70°C for 2 hours, as shown in Figure 1(b).Triplicates of the samples obtained in the chemical treatment were placed in cylindrical molds and frozen to −80°C for 24 hours. They were then transferred to a vacuum chamber for freeze-drying for 72 hours, as shown in Figure1(c). Finally, Figure 1(d) shows the cellulose aerogels.


#### 2.2.2. Sample Characterization

Cellulose was characterized in relation to itsα-, β-, and γ-cellulose content according to TAPPI T203 standards. Scanning electron microscopy with field emission gun (FEG-SEM — MIRA 3, Tescan) was used for morphological characterization.The determination of the apparent density of the aerogels obtained by freeze-drying and cellulose (as received) was performed by an adaptation of ASTM D3575-14 standards, by measuring the volume and the mass of the obtained aerogels, according to (1). Three samples were measured.
(1)Density=massvolume.The porosity of the aerogels can be obtained by (2), which relates the density of the cellulose to the obtained aerogel. Triplicates were performed.
(2)Porosity=1−densityofaerogeldensityofcellulose.Compressive strength tests were performed in a universal EMIC test equipment, model DL 2000, with a compression speed of 1.3 mm·min−1. The tension required to reduce the thickness of the specimen by up to 50% of its initial thickness was measured, as adapted from ASTM D695-15 standards.The modification on the aerogel surface was investigated by Fourier transform infrared spectroscopy (FTIR) in a Nicolet iS10 Thermo Scientific equipment. Each spectrum was obtained by performing 32 scans by attenuated total reflectance (ATR). The wavenumber analyzed ranged from 400 cm−1 to 4000 cm−1.Fast sorption tests in homogeneous medium were performed, adapted from ASTM F726-12. Samples were weighted and placed in homogeneous media (either water or oil) for 15 ± 0.5 minutes. After that, aerogels were vertically removed from the media, drained for 30 ± 2 seconds, and then weighted. Triplicates were performed. The sorption capacity results were calculated as follows:(3)CA=mf−mimi,where CA is sorption capacity (g·g−1), mi is initial mass (g), and mf is final mass (g).The water contact angle measurement was obtained through the sessile drop method, in distilled water, with an approximate droplet volume of 5μL. Samples were placed on a glass slide at 25 ± 2°C and relative humidity of 60 ± 5%. Three droplets of water were placed on the top of the samples. Pictures were taken every 15 minutes for 30 minutes and the images were analyzed with the SURFTENS software.The quantity of oil previously estimated from homogeneous media tests in oil was added to a Petri dish with 200 mL of distilled water. After that, aerogels were placed in the heterogeneous medium for 15 ± 0.5 minutes. The sorbent was removed from the oil in a vertical orientation with a clip, leaving it to drain for 30 ± 2 seconds and weighted, according to the ASTM F726-12 standard adaptation. Assays were performed with 3 samples and the amount of oil adsorbed is given by (2). This method was adapted from Zhang et al. [4] and Nguyen et al. [27].


## 2.1. Materials

The following materials were used for the preparation of the aerogels: unbleached cellulose ofEucalyptus sp. (CE), unbleached cellulose of Pinus elliottii (CP) (both CE and CP were supplied by Rio Grande Companhia de Celulose do Sul, RS, Brazil), glacial acetic acid (provided by Neon), and methyltrimethoxysilane (MTMS) (98% purity purchased from Sigma-Aldrich). For the sorption experiments, SAE 20W50 motor oil with a viscosity of 64 cSt and a density of 0.88 g·cm−3 (20–40°C) was provided by Ipiranga Petrochemical (RS, Brazil). This oil was classified as a medium oil, according to ASTM F726-12.


## 2.2. Methods

### 2.2.1. Production of the Aerogels

Cellulose fibrillation was performed by a mechanical process. The pulp was dispersed in distilled water with an initial concentration of 3% (wt%/v%). Grinding was conducted in a Masuko Sangyo stone disc mill, model MKCA6-2J with an adapted recirculation pump, for 5 hours with a rotation speed of 2500 rpm. Figure1(a) illustrates the mechanical grinding.Figure 1
Process for obtaining aerogels: (a) mechanical grinding, (b) chemical treatment, (c) freeze-drying process, and (d) aerogels.In order to obtain the aerogels’ hydrophobic properties, a chemical treatment of the suspensions with the use of the methyltrimethoxysilane (MTMS) was carried out at a concentration of 2% in mass, according to our previous work [25]. The CNF suspension was filtered through a vacuum system. The permeate pH was then adjusted to 3.0 by adding acetic acid under magnetic stirring for 5 min. Subsequently, 2% in mass of MTMS was added to this solution under magnetic stirring. The resulting solutions were slowly added dropwise into the MTMS supernatant filtration. The CNF suspension with MTMS was mechanically stirred at 500 rpm for 1 hour and kept in an oven at 70°C for 2 hours, as shown in Figure 1(b).Triplicates of the samples obtained in the chemical treatment were placed in cylindrical molds and frozen to −80°C for 24 hours. They were then transferred to a vacuum chamber for freeze-drying for 72 hours, as shown in Figure1(c). Finally, Figure 1(d) shows the cellulose aerogels.


### 2.2.2. Sample Characterization

Cellulose was characterized in relation to itsα-, β-, and γ-cellulose content according to TAPPI T203 standards. Scanning electron microscopy with field emission gun (FEG-SEM — MIRA 3, Tescan) was used for morphological characterization.The determination of the apparent density of the aerogels obtained by freeze-drying and cellulose (as received) was performed by an adaptation of ASTM D3575-14 standards, by measuring the volume and the mass of the obtained aerogels, according to (1). Three samples were measured.
(1)Density=massvolume.The porosity of the aerogels can be obtained by (2), which relates the density of the cellulose to the obtained aerogel. Triplicates were performed.
(2)Porosity=1−densityofaerogeldensityofcellulose.Compressive strength tests were performed in a universal EMIC test equipment, model DL 2000, with a compression speed of 1.3 mm·min−1. The tension required to reduce the thickness of the specimen by up to 50% of its initial thickness was measured, as adapted from ASTM D695-15 standards.The modification on the aerogel surface was investigated by Fourier transform infrared spectroscopy (FTIR) in a Nicolet iS10 Thermo Scientific equipment. Each spectrum was obtained by performing 32 scans by attenuated total reflectance (ATR). The wavenumber analyzed ranged from 400 cm−1 to 4000 cm−1.Fast sorption tests in homogeneous medium were performed, adapted from ASTM F726-12. Samples were weighted and placed in homogeneous media (either water or oil) for 15 ± 0.5 minutes. After that, aerogels were vertically removed from the media, drained for 30 ± 2 seconds, and then weighted. Triplicates were performed. The sorption capacity results were calculated as follows:(3)CA=mf−mimi,where CA is sorption capacity (g·g−1), mi is initial mass (g), and mf is final mass (g).The water contact angle measurement was obtained through the sessile drop method, in distilled water, with an approximate droplet volume of 5μL. Samples were placed on a glass slide at 25 ± 2°C and relative humidity of 60 ± 5%. Three droplets of water were placed on the top of the samples. Pictures were taken every 15 minutes for 30 minutes and the images were analyzed with the SURFTENS software.The quantity of oil previously estimated from homogeneous media tests in oil was added to a Petri dish with 200 mL of distilled water. After that, aerogels were placed in the heterogeneous medium for 15 ± 0.5 minutes. The sorbent was removed from the oil in a vertical orientation with a clip, leaving it to drain for 30 ± 2 seconds and weighted, according to the ASTM F726-12 standard adaptation. Assays were performed with 3 samples and the amount of oil adsorbed is given by (2). This method was adapted from Zhang et al. [4] and Nguyen et al. [27].


## 2.2.1. Production of the Aerogels

Cellulose fibrillation was performed by a mechanical process. The pulp was dispersed in distilled water with an initial concentration of 3% (wt%/v%). Grinding was conducted in a Masuko Sangyo stone disc mill, model MKCA6-2J with an adapted recirculation pump, for 5 hours with a rotation speed of 2500 rpm. Figure1(a) illustrates the mechanical grinding.Figure 1
Process for obtaining aerogels: (a) mechanical grinding, (b) chemical treatment, (c) freeze-drying process, and (d) aerogels.In order to obtain the aerogels’ hydrophobic properties, a chemical treatment of the suspensions with the use of the methyltrimethoxysilane (MTMS) was carried out at a concentration of 2% in mass, according to our previous work [25]. The CNF suspension was filtered through a vacuum system. The permeate pH was then adjusted to 3.0 by adding acetic acid under magnetic stirring for 5 min. Subsequently, 2% in mass of MTMS was added to this solution under magnetic stirring. The resulting solutions were slowly added dropwise into the MTMS supernatant filtration. The CNF suspension with MTMS was mechanically stirred at 500 rpm for 1 hour and kept in an oven at 70°C for 2 hours, as shown in Figure 1(b).Triplicates of the samples obtained in the chemical treatment were placed in cylindrical molds and frozen to −80°C for 24 hours. They were then transferred to a vacuum chamber for freeze-drying for 72 hours, as shown in Figure1(c). Finally, Figure 1(d) shows the cellulose aerogels.


## 2.2.2. Sample Characterization

Cellulose was characterized in relation to itsα-, β-, and γ-cellulose content according to TAPPI T203 standards. Scanning electron microscopy with field emission gun (FEG-SEM — MIRA 3, Tescan) was used for morphological characterization.The determination of the apparent density of the aerogels obtained by freeze-drying and cellulose (as received) was performed by an adaptation of ASTM D3575-14 standards, by measuring the volume and the mass of the obtained aerogels, according to (1). Three samples were measured.
(1)Density=massvolume.The porosity of the aerogels can be obtained by (2), which relates the density of the cellulose to the obtained aerogel. Triplicates were performed.
(2)Porosity=1−densityofaerogeldensityofcellulose.Compressive strength tests were performed in a universal EMIC test equipment, model DL 2000, with a compression speed of 1.3 mm·min−1. The tension required to reduce the thickness of the specimen by up to 50% of its initial thickness was measured, as adapted from ASTM D695-15 standards.The modification on the aerogel surface was investigated by Fourier transform infrared spectroscopy (FTIR) in a Nicolet iS10 Thermo Scientific equipment. Each spectrum was obtained by performing 32 scans by attenuated total reflectance (ATR). The wavenumber analyzed ranged from 400 cm−1 to 4000 cm−1.Fast sorption tests in homogeneous medium were performed, adapted from ASTM F726-12. Samples were weighted and placed in homogeneous media (either water or oil) for 15 ± 0.5 minutes. After that, aerogels were vertically removed from the media, drained for 30 ± 2 seconds, and then weighted. Triplicates were performed. The sorption capacity results were calculated as follows:(3)CA=mf−mimi,where CA is sorption capacity (g·g−1), mi is initial mass (g), and mf is final mass (g).The water contact angle measurement was obtained through the sessile drop method, in distilled water, with an approximate droplet volume of 5μL. Samples were placed on a glass slide at 25 ± 2°C and relative humidity of 60 ± 5%. Three droplets of water were placed on the top of the samples. Pictures were taken every 15 minutes for 30 minutes and the images were analyzed with the SURFTENS software.The quantity of oil previously estimated from homogeneous media tests in oil was added to a Petri dish with 200 mL of distilled water. After that, aerogels were placed in the heterogeneous medium for 15 ± 0.5 minutes. The sorbent was removed from the oil in a vertical orientation with a clip, leaving it to drain for 30 ± 2 seconds and weighted, according to the ASTM F726-12 standard adaptation. Assays were performed with 3 samples and the amount of oil adsorbed is given by (2). This method was adapted from Zhang et al. [4] and Nguyen et al. [27].


## 3. Results and Discussion

### 3.1. Characterization of Cellulose Samples

Theα-cellulose, β-cellulose, γ-cellulose, and lignin contents of the samples are shown in Table 1.Table 1
Percentages ofα-cellulose, β-cellulose, γ-cellulose, and lignin of the cellulose samples.
Samples
α-Cellulose (%)
β-Cellulose (%)
γ-Cellulose (%)
Lignin (%)
CE
57.34 ± 0.18
16.48 ± 0.27
0.74 ± 0.01
14.18 ± 0.02
CP
60.2 ± 0.27
13.33 ± 0.17
0.84 ± 0.01
5.69 ± 0.02The CE sample presented a higher lignin content and lower percentage ofα-cellulose compared to CP. Chen et al. [28] found a 24.4% lignin mass content for Eucalyptus sp. wood. Gomide et al. [29] found α-cellulose contents ranging from 43.9 to 49.7% and lignin contents ranging from 27.5 to 31.7% in Eucalyptus sp. wood used in their studies. Pinus elliotti species presented lignin contents ranging from 32.8 to 35%. According to Klock et al. [30], in long-fiber woods such as Pinus elliotti, the average composition of wood pulp varies from 40 to 44%.The percentages of CE and CP lignin used in this work were lower when compared to the original wood. The percentages ofα-cellulose of the same samples, when compared with the original wood, were higher due to the process used to obtain the samples. During this process, the extractives, husks, and part of the lignin were removed.Figure2 shows the FEG-SEM micrographs of the CE and CP cellulose samples, with magnifications of 150x and 1000x. A set of compact fibers in macro/micrometric scale is observed, as well as long filaments and linear structures coming from intramolecular hydrogen bonds between hydroxyl groups of the same molecules, resulting in a straight and rigid polymer chain [31]. It is also observed that CP cellulose has fibers with seemingly larger diameters than CE cellulose.Figure 2
FEG-SEM micrograph of CE at 150x (a) and 1000x magnification (b). FEG-SEM micrograph of CP at 150x (c) and 1000x magnification (d).
(a)
(b)
(c)
(d)The apparent density values of cellulose samples were 0.198 ± 0.010 g·cm−3 for CE and 0.414 ± 0.011 g·cm−3 for CP. CP has the lowest apparent density, as well as the smallest compaction of fibers when compared to the CP cellulose sample.


### 3.2. Development of Aerogels

The mechanical process promoted the cellulose fibrillation, resulting in homogeneous suspensions, which can be seen in Figure1(a). Differently from chemical processes, this process presents less environmental impact while also allowing the obtainment of CNFs from an aqueous solution suspension of cellulose fibers without the addition of chemical compounds. According to Peng et al. [32], a uniform aqueous suspension of CNFs is formed after fibrillation in which the strong hydrogen bonds between water and cellulose particles allow the system to remain stable. In the mechanical process, the shear forces of disintegration and the high degree of fibrillation provide the obtainment of interconnected fibrils with a diameter of less than 100 nm in width and length in the micrometric scale [33, 34].The final contents of cellulose in the suspension of CE and CP were, respectively, 2.449 ± 0.02% and 2.304 ± 0.05% in cellulose mass. The values found herein were lower than the initial ones (3.0% in mass) due to losses during the grinding process.The aerogels did not present a retraction in relation to the initial volume of the suspensions of CNF, thus acquiring the format of the cylindrical mold used. According to Shi et al. [35], the volume shrinkage of aerogels reflects the efficiency of the drying method. Figure 1(d) shows the aerogels obtained from CE and CP suspensions, showing homogeneity in their structures, and no discoloration. CNF aerogels obtained by Chen et al. [36] also maintained their volumes after freeze-drying, without shrinkage. According to Nguyen et al. [27], cellulose aerogels are formed by hydrogen bonds and by the self-assembly process of the cellulose fibers.


### 3.3. Apparent Density and Porosity

The apparent density values of the aerogels obtained varied from 0.030 g·cm−3 to 0.032 g·cm−3. These values are directly related to the fiber content present, as well as to its production process.Mechanical fibrillation and freeze-drying processes yielded CE and CP aerogels with decreased densities based on the source of the cellulose, that is, from 0.198 ± 0.0125 g·cm−3 to 0.030 ± 0.0011 g·cm−3, and from 0.414 ± 0.0109 g·cm−3 to 0.032 ± 0.0022 g·cm−3, respectively. CP aerogels showed the lowest density due to being derived from lower density cellulose.CP aerogels presented a higher porosity (92.2%), while CE aerogels presented values of 85.3%, due to the CE cellulose having a lower density, being less compacted when compared to CP.Values found in relation to the apparent density and porosity are in agreement with studies already published by other authors. Pääkkö et al. [37] and Korhonen et al. [3] described a nanocellulose aerogel with a density between 0.02 and 0.03 g·cm−3 and a porosity of 98%. Aerogels were obtained from a nanocellulose hydrogel (mechanically homogenized hardwood kraft pulp, dry content about 2%) and subsequently vacuum freeze-dried. In their studies with aerogels of cellulose nanofibers, Zanini et al. [38] found apparent density values of 0.0240 g·cm−3 and a porosity of 97.2%. The authors obtained freeze-dried aerogels derived from a suspension with 2.19% (wt%) of cellulose nanofibres obtained by a mechanical process.


### 3.4. Scanning Electron Microscopy with Field Emission Gun (FEG-SEM)

Figure3 shows the microscopy images obtained from CE and CP aerogels. In Figures 3(a) and 3(c), the macroscopic structure of the aerogels is observed, and in Figures 3(b) and 3(d) it is possible to visualize the presence of fibers with diameters within the nanoscale range in the samples of the obtained aerogels. In this work, CNFs were obtained with diameters smaller than 71 nm.Figure 3
FEG-SEM micrographs of CE aerogel: lamellar structure (a) and nanofiber detail (b). FEG-SEM micrographs of CP aerogel: lamellar structure (c) and nanofiber detail (d).The morphology and properties of aerogels are theoretically related to sample freezing conditions, cellulose particle size, solid concentration in the suspension, surface loading, and the self-organizing behavior of the cellulose fibers during freeze-drying. In the micrographs of freeze-dried aerogels, the formation of a lamellar structure with fiber alignment was also observed. This was also reported by Pääkkö et al. [37] and Han et al. [39].Freeze-dried aerogels presented a lamellar structure. During the freezing process, the ordered and porous structure is achieved by organizing the growing spaces of the ice crystals. Thus, it is important that this stage is carried out fast for the formation of small crystals, allowing the formation of the chains with cellulose microfibers, thus forming voids after freeze-drying [37].According to Han et al. [39], the arrangements of hydrogen bonds play an important role in the self-organizing properties of the cellulose suspension. At concentrations ranging from 2.2 to 2.6%, the spaces between the microfibers enable the formation of intra- and intermolecular hydrogen bonds, as well as the formation of Van der Walls forces, aligning them longitudinally during the freezing process, thus yielding a lamellar structure.In the micrograph shown in Figure3(c), the presence of fragments of larger fibers is observed in the CP aerogel when compared to microscopy of the CE aerogel (Figure 3(a)), mainly because CP has a longer fiber length. As such, larger fiber fragments may remain even after the fibrillation process, when compared to the aerogels from the CE suspension. Bassa et al. [40] observed the same behavior for Pinus sp. and Eucalyptus sp. fibers. The authors report that Pinus sp. fibrils are longer than Eucalyptus fibers.


### 3.5. Compressive Strength Tests

The compressive strength tests were performed with aerogels with and without chemical treatment. The results obtained from the compressive strength test with 50% deformation have the following values: 60.26 kPa (CE aerogel), 69.35 kPa (CP aerogel), 89.76 kPa (CE aerogel with MTMS), and 128.77 kPa (CP aerogel with MTMS).The chemical treatment with MTMS provided higher compressive strength for the aerogels: an increase of 48.95% for the CE aerogel and an increase of 85.68% for the CP aerogel. Zhang et al. [4], also observed greater compressive strength of CNF sponges after chemical treatment with MTMS. According to the authors, this effect was attributed to the increasing contribution of the polysiloxane layer at the NFC surface. Pääkkö et al. [37] obtained values of 200 kPa for CNF aerogels in the test of resistance to compression, with 70% deformation.Stress-strain curves under compression are shown in Figure4. Linear elastic regions can be observed in the stress-strain curves. Gradual transition from linear to nonlinear, as well as densification behavior, that is, the collapse of empty spaces, was also seen. This behavior is characteristic of porous materials, and it was also observed by Sehaqui et al. [41] and Karadagli et al. [42].Figure 4
Compressive stress-strain curve of aerogels.The graph shows that the aerogels from CP with and without treatment presented higher values of compressive strength when compared to CE aerogels. According to Kim et al. [43], the compression of the fiber network of the CNF aerogel takes place upon the bending of individual fibers or by the breakage of interfiber bonds, as well as by the loss of friction between adjacent fibers and the physical entanglement of the fibers. Also, according to Sehaqui et al. [41], at low strains the stress-strain behavior is linear and elastic in nature. Deformation is expected to be primarily due to elastic cell wall bending at large strains in the densification region, where the cell walls are in close contact to each other and there is a steep rise in stress levels with little further strain. Therefore, it could be suggested that the larger fiber fragments of the fibrils in CP aerogels provide increased compressive strength in comparison with CE aerogels, which possess seemingly smaller and bent fibrils, as seen in the SEM micrographs in Figure 3.


### 3.6. Fourier Transform Infrared Spectroscopy (FTIR)

Figures5(a) and 5(b) show the spectra obtained from the cellulose source and their aerogels before and after chemical treatment. In the samples with chemical treatment, it is possible to observe the appearance of new bands, characteristics of the MTMS silane.Figure 5
FTIR spectra: (a) CE cellulose and CE aerogel with and without MTMS. (b) CP cellulose and CE aerogel with and without MTMS.
(a)
(b)It was not possible to identify chemical changes related to mechanical fibrillation or to the freeze-drying process in these samples. Characteristic bands of the cellulose fibers were observed in the cellulose samples and in their respective aerogels without chemical treatment.The band at 3300 cm−1 is related to the O–H stretching vibration of the hydroxyl groups. The peak at 1596 cm−1 is associated to C=C, C–O stretching, or to the bending vibrations of different groups present in lignin. The peak at 1318 cm−1 is attributed to the bending vibration of the C–H and C–O groups of the aromatic ring in polysaccharides. The band at 1032 cm−1 is characteristic of the C–O vibration of cellulose, and the peak at 896 cm−1 is related to amorphous cellulose vibration, that is, glucose ring stretch [44–49].After chemical treatment with MTMS, the characteristic vibrations of silane were identified at 1265 cm−1 and 1267 cm−1, related to the deformation of the CH bond of the methyl group. The peaks at 890 cm−1 and 893 cm−1 were attributed to the Si–OH bond stretching vibrations, and the peaks at 776 cm−1 and 777 cm−1 were related to the absorption bands of the stretching vibrations of the Si–C bond and/or the stretching vibrations of the Si–O bond [50, 51].


### 3.7. Water Contact Angle Measurement

The contact angle measurement was carried out with aerogels with and without chemical treatment. The hydrophobic character of the aerogels was determined by measuring the contact angle of their surface with water. It was not possible to perform any measurement during the test of aerogels without silane treatment, since the water was sorbed immediately after its addition to the surface. Figure6(a) shows the test performed. The contact angles obtained for the aerogels with MTMS were 135.82° ± 2.31 and 134.81° ± 1.32, for CE and CP, respectively. These results allowed the identification of the hydrophobic character in the aerogels.Figure 6
(a) Contact angle measurements fromt=0 to t=30. (b) Sorption capacity tests from t=0 to t=15 min in heterogeneous medium (oil/water).
(a)
(b)According to Wan et al. [52] and Xiao et al. [48], the modification by silane contributes to the formation of a low-energy surface of the cellulose aerogel due to the replacement of surface hydroxyl groups in the cellulose with hydrophobic groups. Xiao et al. [48] obtained a value of 135° for pine needle nanofiber aerogels obtained by the treatment of trimethylchlorosilane through vapor phase deposition.


### 3.8. Sorption Tests in Homogeneous Medium

Sorption tests in homogeneous medium with water were carried out with the samples with and without chemical treatment. Results obtained for the samples without chemical treatment have values of 29.995 ± 0.078 g·g−1 and 33.920 ± 0.109 g·g−1 for the CE and CP aerogels, respectively. For the samples treated with MTMS, the sorption values found were 0.173 ± 0.003 g·g−1 for the CE aerogel and 0.491 ± 0.005 g·g−1 for the CP aerogel. This shows that the chemical treatment used provided low affinity of the material with water.Sorption tests in homogeneous medium with oil were carried out with the samples with and without chemical treatment. Results obtained for the samples without chemical treatment have values of 20.796 ± 2.80 g·g−1 and 17.518 ± 2.272 g·g−1 for the CE and CP aerogels, respectively. After chemical treatment with MTMS, the aerogels showed an increase in the oil sorption capacity, being 24.32 ± 2.519 g·g−1 for the CE aerogel and 22.829 ± 1.530 g·g−1 for the CP aerogel.The oil sorption process in cellulose aerogels is related to the interiority of the porous structure of the material (large surface area and large number of capillary channels internally), as well as to the hydrophobic characteristic of the surface [53].CE aerogels presented a higher amount of oil sorbed, while having the lowest density. The lower the density of the material, the greater the amount of voids, thus the tendency to sorb more oil. According to Rengasamy et al. [54], the sorption capacity is influenced by the density of the fibers. Lower values of density show lower compaction of aerogels and greater availability of free spaces for the oil to be sorbed into the material.


### 3.9. Sorption Tests in Heterogeneous Medium (Water/Oil)

Sorption capacity in heterogeneous medium of chemically treated aerogels was 21.543 ± 0.126 g·g−1 and 21.303 ± 0.257 g·g−1 for the CE and CP aerogels, respectively. As such, the efficiency in oil removal was between 88.5 and 93.3%. The hydrophobic characteristic on the surface of the aerogels provides the selectivity of the sorbent in the presence of the heterogeneous medium of water and oil. Figure 6(b) shows the performed tests.Jin et al. [24] obtained aerogels from newspaper waste. This residue was composed of 50.1% cellulose and 18.1% lignin. They performed a chemical treatment in the aerogels by vapor deposition of trimethylchlorosilane. The aerogels presented an adsorption capacity ranging from 11 to 22 g·g−1 for motor oil and organic solvents such as chloroform, for example.Zanini et al. [25] obtained aerogels of bleached CNFs of Eucalyptus sp. with a sorption capacity in heterogeneous medium of 16.78 g·g−1 and an oil removal efficiency of 87.9%. The presence of lignin in unbleached cellulose aerogels favored a higher sorption capacity. This was also observed by Payne et al. [55], who verified that the presence of lignin in cellulose fibers resulted in a 10% increase in the sorption of the oil, attributing to the higher affinity of lignin with oil because of its aromatic nature.In their studies, based on different methods of silanization, Lazzari et al. [26] obtained aerogels with 1.5% of unbleached CNFs of Pinus elliottii, with a sorption capacity in heterogeneous medium of 68.42 g·g−1. The present study found lower values in relation to the sorption capacity found by Lazzari et al. [26]. However, it was possible to observe that the silanization process provided greater mechanical resistance to the aerogels obtained.


## 3.1. Characterization of Cellulose Samples

Theα-cellulose, β-cellulose, γ-cellulose, and lignin contents of the samples are shown in Table 1.Table 1
Percentages ofα-cellulose, β-cellulose, γ-cellulose, and lignin of the cellulose samples.
Samples
α-Cellulose (%)
β-Cellulose (%)
γ-Cellulose (%)
Lignin (%)
CE
57.34 ± 0.18
16.48 ± 0.27
0.74 ± 0.01
14.18 ± 0.02
CP
60.2 ± 0.27
13.33 ± 0.17
0.84 ± 0.01
5.69 ± 0.02The CE sample presented a higher lignin content and lower percentage ofα-cellulose compared to CP. Chen et al. [28] found a 24.4% lignin mass content for Eucalyptus sp. wood. Gomide et al. [29] found α-cellulose contents ranging from 43.9 to 49.7% and lignin contents ranging from 27.5 to 31.7% in Eucalyptus sp. wood used in their studies. Pinus elliotti species presented lignin contents ranging from 32.8 to 35%. According to Klock et al. [30], in long-fiber woods such as Pinus elliotti, the average composition of wood pulp varies from 40 to 44%.The percentages of CE and CP lignin used in this work were lower when compared to the original wood. The percentages ofα-cellulose of the same samples, when compared with the original wood, were higher due to the process used to obtain the samples. During this process, the extractives, husks, and part of the lignin were removed.Figure2 shows the FEG-SEM micrographs of the CE and CP cellulose samples, with magnifications of 150x and 1000x. A set of compact fibers in macro/micrometric scale is observed, as well as long filaments and linear structures coming from intramolecular hydrogen bonds between hydroxyl groups of the same molecules, resulting in a straight and rigid polymer chain [31]. It is also observed that CP cellulose has fibers with seemingly larger diameters than CE cellulose.Figure 2
FEG-SEM micrograph of CE at 150x (a) and 1000x magnification (b). FEG-SEM micrograph of CP at 150x (c) and 1000x magnification (d).
(a)
(b)
(c)
(d)The apparent density values of cellulose samples were 0.198 ± 0.010 g·cm−3 for CE and 0.414 ± 0.011 g·cm−3 for CP. CP has the lowest apparent density, as well as the smallest compaction of fibers when compared to the CP cellulose sample.


## 3.2. Development of Aerogels

The mechanical process promoted the cellulose fibrillation, resulting in homogeneous suspensions, which can be seen in Figure1(a). Differently from chemical processes, this process presents less environmental impact while also allowing the obtainment of CNFs from an aqueous solution suspension of cellulose fibers without the addition of chemical compounds. According to Peng et al. [32], a uniform aqueous suspension of CNFs is formed after fibrillation in which the strong hydrogen bonds between water and cellulose particles allow the system to remain stable. In the mechanical process, the shear forces of disintegration and the high degree of fibrillation provide the obtainment of interconnected fibrils with a diameter of less than 100 nm in width and length in the micrometric scale [33, 34].The final contents of cellulose in the suspension of CE and CP were, respectively, 2.449 ± 0.02% and 2.304 ± 0.05% in cellulose mass. The values found herein were lower than the initial ones (3.0% in mass) due to losses during the grinding process.The aerogels did not present a retraction in relation to the initial volume of the suspensions of CNF, thus acquiring the format of the cylindrical mold used. According to Shi et al. [35], the volume shrinkage of aerogels reflects the efficiency of the drying method. Figure 1(d) shows the aerogels obtained from CE and CP suspensions, showing homogeneity in their structures, and no discoloration. CNF aerogels obtained by Chen et al. [36] also maintained their volumes after freeze-drying, without shrinkage. According to Nguyen et al. [27], cellulose aerogels are formed by hydrogen bonds and by the self-assembly process of the cellulose fibers.


## 3.3. Apparent Density and Porosity

The apparent density values of the aerogels obtained varied from 0.030 g·cm−3 to 0.032 g·cm−3. These values are directly related to the fiber content present, as well as to its production process.Mechanical fibrillation and freeze-drying processes yielded CE and CP aerogels with decreased densities based on the source of the cellulose, that is, from 0.198 ± 0.0125 g·cm−3 to 0.030 ± 0.0011 g·cm−3, and from 0.414 ± 0.0109 g·cm−3 to 0.032 ± 0.0022 g·cm−3, respectively. CP aerogels showed the lowest density due to being derived from lower density cellulose.CP aerogels presented a higher porosity (92.2%), while CE aerogels presented values of 85.3%, due to the CE cellulose having a lower density, being less compacted when compared to CP.Values found in relation to the apparent density and porosity are in agreement with studies already published by other authors. Pääkkö et al. [37] and Korhonen et al. [3] described a nanocellulose aerogel with a density between 0.02 and 0.03 g·cm−3 and a porosity of 98%. Aerogels were obtained from a nanocellulose hydrogel (mechanically homogenized hardwood kraft pulp, dry content about 2%) and subsequently vacuum freeze-dried. In their studies with aerogels of cellulose nanofibers, Zanini et al. [38] found apparent density values of 0.0240 g·cm−3 and a porosity of 97.2%. The authors obtained freeze-dried aerogels derived from a suspension with 2.19% (wt%) of cellulose nanofibres obtained by a mechanical process.


## 3.4. Scanning Electron Microscopy with Field Emission Gun (FEG-SEM)

Figure3 shows the microscopy images obtained from CE and CP aerogels. In Figures 3(a) and 3(c), the macroscopic structure of the aerogels is observed, and in Figures 3(b) and 3(d) it is possible to visualize the presence of fibers with diameters within the nanoscale range in the samples of the obtained aerogels. In this work, CNFs were obtained with diameters smaller than 71 nm.Figure 3
FEG-SEM micrographs of CE aerogel: lamellar structure (a) and nanofiber detail (b). FEG-SEM micrographs of CP aerogel: lamellar structure (c) and nanofiber detail (d).The morphology and properties of aerogels are theoretically related to sample freezing conditions, cellulose particle size, solid concentration in the suspension, surface loading, and the self-organizing behavior of the cellulose fibers during freeze-drying. In the micrographs of freeze-dried aerogels, the formation of a lamellar structure with fiber alignment was also observed. This was also reported by Pääkkö et al. [37] and Han et al. [39].Freeze-dried aerogels presented a lamellar structure. During the freezing process, the ordered and porous structure is achieved by organizing the growing spaces of the ice crystals. Thus, it is important that this stage is carried out fast for the formation of small crystals, allowing the formation of the chains with cellulose microfibers, thus forming voids after freeze-drying [37].According to Han et al. [39], the arrangements of hydrogen bonds play an important role in the self-organizing properties of the cellulose suspension. At concentrations ranging from 2.2 to 2.6%, the spaces between the microfibers enable the formation of intra- and intermolecular hydrogen bonds, as well as the formation of Van der Walls forces, aligning them longitudinally during the freezing process, thus yielding a lamellar structure.In the micrograph shown in Figure3(c), the presence of fragments of larger fibers is observed in the CP aerogel when compared to microscopy of the CE aerogel (Figure 3(a)), mainly because CP has a longer fiber length. As such, larger fiber fragments may remain even after the fibrillation process, when compared to the aerogels from the CE suspension. Bassa et al. [40] observed the same behavior for Pinus sp. and Eucalyptus sp. fibers. The authors report that Pinus sp. fibrils are longer than Eucalyptus fibers.


## 3.5. Compressive Strength Tests

The compressive strength tests were performed with aerogels with and without chemical treatment. The results obtained from the compressive strength test with 50% deformation have the following values: 60.26 kPa (CE aerogel), 69.35 kPa (CP aerogel), 89.76 kPa (CE aerogel with MTMS), and 128.77 kPa (CP aerogel with MTMS).The chemical treatment with MTMS provided higher compressive strength for the aerogels: an increase of 48.95% for the CE aerogel and an increase of 85.68% for the CP aerogel. Zhang et al. [4], also observed greater compressive strength of CNF sponges after chemical treatment with MTMS. According to the authors, this effect was attributed to the increasing contribution of the polysiloxane layer at the NFC surface. Pääkkö et al. [37] obtained values of 200 kPa for CNF aerogels in the test of resistance to compression, with 70% deformation.Stress-strain curves under compression are shown in Figure4. Linear elastic regions can be observed in the stress-strain curves. Gradual transition from linear to nonlinear, as well as densification behavior, that is, the collapse of empty spaces, was also seen. This behavior is characteristic of porous materials, and it was also observed by Sehaqui et al. [41] and Karadagli et al. [42].Figure 4
Compressive stress-strain curve of aerogels.The graph shows that the aerogels from CP with and without treatment presented higher values of compressive strength when compared to CE aerogels. According to Kim et al. [43], the compression of the fiber network of the CNF aerogel takes place upon the bending of individual fibers or by the breakage of interfiber bonds, as well as by the loss of friction between adjacent fibers and the physical entanglement of the fibers. Also, according to Sehaqui et al. [41], at low strains the stress-strain behavior is linear and elastic in nature. Deformation is expected to be primarily due to elastic cell wall bending at large strains in the densification region, where the cell walls are in close contact to each other and there is a steep rise in stress levels with little further strain. Therefore, it could be suggested that the larger fiber fragments of the fibrils in CP aerogels provide increased compressive strength in comparison with CE aerogels, which possess seemingly smaller and bent fibrils, as seen in the SEM micrographs in Figure 3.


## 3.6. Fourier Transform Infrared Spectroscopy (FTIR)

Figures5(a) and 5(b) show the spectra obtained from the cellulose source and their aerogels before and after chemical treatment. In the samples with chemical treatment, it is possible to observe the appearance of new bands, characteristics of the MTMS silane.Figure 5
FTIR spectra: (a) CE cellulose and CE aerogel with and without MTMS. (b) CP cellulose and CE aerogel with and without MTMS.
(a)
(b)It was not possible to identify chemical changes related to mechanical fibrillation or to the freeze-drying process in these samples. Characteristic bands of the cellulose fibers were observed in the cellulose samples and in their respective aerogels without chemical treatment.The band at 3300 cm−1 is related to the O–H stretching vibration of the hydroxyl groups. The peak at 1596 cm−1 is associated to C=C, C–O stretching, or to the bending vibrations of different groups present in lignin. The peak at 1318 cm−1 is attributed to the bending vibration of the C–H and C–O groups of the aromatic ring in polysaccharides. The band at 1032 cm−1 is characteristic of the C–O vibration of cellulose, and the peak at 896 cm−1 is related to amorphous cellulose vibration, that is, glucose ring stretch [44–49].After chemical treatment with MTMS, the characteristic vibrations of silane were identified at 1265 cm−1 and 1267 cm−1, related to the deformation of the CH bond of the methyl group. The peaks at 890 cm−1 and 893 cm−1 were attributed to the Si–OH bond stretching vibrations, and the peaks at 776 cm−1 and 777 cm−1 were related to the absorption bands of the stretching vibrations of the Si–C bond and/or the stretching vibrations of the Si–O bond [50, 51].


## 3.7. Water Contact Angle Measurement

The contact angle measurement was carried out with aerogels with and without chemical treatment. The hydrophobic character of the aerogels was determined by measuring the contact angle of their surface with water. It was not possible to perform any measurement during the test of aerogels without silane treatment, since the water was sorbed immediately after its addition to the surface. Figure6(a) shows the test performed. The contact angles obtained for the aerogels with MTMS were 135.82° ± 2.31 and 134.81° ± 1.32, for CE and CP, respectively. These results allowed the identification of the hydrophobic character in the aerogels.Figure 6
(a) Contact angle measurements fromt=0 to t=30. (b) Sorption capacity tests from t=0 to t=15 min in heterogeneous medium (oil/water).
(a)
(b)According to Wan et al. [52] and Xiao et al. [48], the modification by silane contributes to the formation of a low-energy surface of the cellulose aerogel due to the replacement of surface hydroxyl groups in the cellulose with hydrophobic groups. Xiao et al. [48] obtained a value of 135° for pine needle nanofiber aerogels obtained by the treatment of trimethylchlorosilane through vapor phase deposition.


## 3.8. Sorption Tests in Homogeneous Medium

Sorption tests in homogeneous medium with water were carried out with the samples with and without chemical treatment. Results obtained for the samples without chemical treatment have values of 29.995 ± 0.078 g·g−1 and 33.920 ± 0.109 g·g−1 for the CE and CP aerogels, respectively. For the samples treated with MTMS, the sorption values found were 0.173 ± 0.003 g·g−1 for the CE aerogel and 0.491 ± 0.005 g·g−1 for the CP aerogel. This shows that the chemical treatment used provided low affinity of the material with water.Sorption tests in homogeneous medium with oil were carried out with the samples with and without chemical treatment. Results obtained for the samples without chemical treatment have values of 20.796 ± 2.80 g·g−1 and 17.518 ± 2.272 g·g−1 for the CE and CP aerogels, respectively. After chemical treatment with MTMS, the aerogels showed an increase in the oil sorption capacity, being 24.32 ± 2.519 g·g−1 for the CE aerogel and 22.829 ± 1.530 g·g−1 for the CP aerogel.The oil sorption process in cellulose aerogels is related to the interiority of the porous structure of the material (large surface area and large number of capillary channels internally), as well as to the hydrophobic characteristic of the surface [53].CE aerogels presented a higher amount of oil sorbed, while having the lowest density. The lower the density of the material, the greater the amount of voids, thus the tendency to sorb more oil. According to Rengasamy et al. [54], the sorption capacity is influenced by the density of the fibers. Lower values of density show lower compaction of aerogels and greater availability of free spaces for the oil to be sorbed into the material.


## 3.9. Sorption Tests in Heterogeneous Medium (Water/Oil)

Sorption capacity in heterogeneous medium of chemically treated aerogels was 21.543 ± 0.126 g·g−1 and 21.303 ± 0.257 g·g−1 for the CE and CP aerogels, respectively. As such, the efficiency in oil removal was between 88.5 and 93.3%. The hydrophobic characteristic on the surface of the aerogels provides the selectivity of the sorbent in the presence of the heterogeneous medium of water and oil. Figure 6(b) shows the performed tests.Jin et al. [24] obtained aerogels from newspaper waste. This residue was composed of 50.1% cellulose and 18.1% lignin. They performed a chemical treatment in the aerogels by vapor deposition of trimethylchlorosilane. The aerogels presented an adsorption capacity ranging from 11 to 22 g·g−1 for motor oil and organic solvents such as chloroform, for example.Zanini et al. [25] obtained aerogels of bleached CNFs of Eucalyptus sp. with a sorption capacity in heterogeneous medium of 16.78 g·g−1 and an oil removal efficiency of 87.9%. The presence of lignin in unbleached cellulose aerogels favored a higher sorption capacity. This was also observed by Payne et al. [55], who verified that the presence of lignin in cellulose fibers resulted in a 10% increase in the sorption of the oil, attributing to the higher affinity of lignin with oil because of its aromatic nature.In their studies, based on different methods of silanization, Lazzari et al. [26] obtained aerogels with 1.5% of unbleached CNFs of Pinus elliottii, with a sorption capacity in heterogeneous medium of 68.42 g·g−1. The present study found lower values in relation to the sorption capacity found by Lazzari et al. [26]. However, it was possible to observe that the silanization process provided greater mechanical resistance to the aerogels obtained.


## 4. Conclusions

Fibrillation was an efficient process for obtaining CNFs from the two cellulose sources used. When compared to chemical processes, it does not generate hazardous chemical residues.The presence of lignin in the unbleached samples did not alter the overall properties of the aerogels obtained, thus allowing the use of a raw material of lower cost and lower environmental impact for the production of aerogels. The chemical treatment of the aerogels was efficient, which provided the oil selectivity of the material in heterogeneous medium, as well as a greater compressive strength when compared to their neat counterparts. The CP aerogel presented the highest compressive strength, while the CE aerogel presented the highest sorption capacity. In conclusion, unbleached cellulose fibers are a viable alternative for use as oil sorbents in aqueous media.



---