# CdS Nanoparticles with a Thermoresponsive Polymer: Synthesis and Properties

Authors: Aslam Khan
Journal: Journal of Nanomaterials
 (2012)

---

## Abstract

This paper describes the synthesis of thermoresponsive colloidal nanocomposites based on CdS and poly(N-isopropylacrylamide). The CdS nanoparticles were prepared at room temperature from cadmium chloride and sodium sulfide salts in the presence of an organic ligand, 3-mercaptopropionic acid (MPA). The as-prepared MPA-bound CdS nanoparticles were stable for more than 30 days and exhibited good optical properties. The effect of various ratios of MPA/Cd2+ and H2O/DMF (dimethylformamide) on the particle size of the CdS nanoparticles was investigated using UV-vis absorption measurements. Transmission electron microscopy studies showed that the particle sizes were approximately 4 nm in diameter, which is consistent with the size obtained using UV-vis spectroscopy. The CdS nanocomposite showed a temperature-responsive phenomenon as its temperature increased from 20 to 45°C.


---

## Body

## 1. Introduction

Colloidal nanoparticles (NPs) have attracted extensive scientific and industrial interest as a consequence of their highly size-dependent properties and their unique optical and electronic features [1–4]. These properties have led to the potential application of colloidal NPs in light-emitting devices [5], photonic crystals [6], and biological labels [7–10]. CdS nanoparticles represent a material that can be both fabricated and functionalized with biomolecules in a single step. Consequently, much effort has been devoted to the synthesis of these small quantum-sized particles. CdS NPs have been successfully synthesized in a variety of media, such as nonaqueous solvents [11–13], reverse micelles [14, 15], vesicles [16], zeolites [17, 18], and others [19, 20]. Some of the synthetic methods use Cd2+ and H2S in separate phases that are unevenly mixed and result in the uneven formation and aggregation of CdS NPs. Some methods involve mixing Cd2+ with S2− at a rate that is faster than their homogenous mixing rate; the inhomogeneity at early stages of these methods results in a broadening of the size distribution of the products. In addition, the preparation and deoxygenation of fresh H2S aqueous solutions are necessary in these methods to avoid the formation of colloidal sulfur and other species that result from the instability of Na2S as a precursor.Environmentally responsive polymers have been a subject of great interest in the past decade due to their versatile applications [21]. Such polymers are sometimes termed “smart” because their properties allow them to react in a specific way to external stimuli. Hence, such smart materials can respond to various parameters, such as temperature [22, 23], pH [24, 25], ionic strength [26], or magnetic field strength [27]. Applications of these systems include drug delivery [28, 29], biosensing [30], chemical separation [31], biomaterials [32], and catalysis [33–35]. Poly(N-isopropylacrylamide) (pNIPAAm) is the most extensively used thermoresponsive polymer [23]. pNIPAAm exhibits a low critical solution temperature (LCST) (or phase-separation temperature) of approximately 32°C in aqueous solution, below which the polymer is hydrophilic and above which it becomes hydrophobic. It is possible to increase the functionality of polymers by finding the right balance of hydrophilic and hydrophobic comonomers. Polymers can also be tuned to a desired temperature range by polymerization with a more hydrophilic comonomer (which raises the LCST) or a hydrophobic comonomer (which lowers the LCST) [36].In this study, CdS NPs and pNIPAAm composites are prepared and the interaction between the amide group of isopropylacrylamide from the polymer backbone and the carboxyl group from the modified CdS NPs is investigated. The resultant composites based on CdS@pNIPAAm are expected to be thermoresponsive because pNIPAAm is a typical smart polymer that undergoes the coil-to-globules transition in water at its LCST of approximately 32°C. In addition, the optical properties of MPA-coated CdS NPs in DMF are thoroughly investigated.


## 2. Materials and Methods

### 2.1. Materials

Cadmium chloride, sodium sulfide, 2,2′-azodiisobutyronitrile (AIBN), and dryN,N-dimethylformamide (DMF) were supplied by Merck (India) and used as received. N-Isopropylacrylamide was obtained from Aldrich, recrystallized in hexane, and dried under vacuum before use. 3-Mercaptopropionic acid (MPA) was purchased from Sigma-Aldrich. The water used in all experiments was purified to a resistance of 10 MΩ (Milli-Q Reagent Water System, Millipore Corporation) and filtered through a 0.2 μm filter to remove any particulate matter.


### 2.2. Synthesis of MPA-Modified CdS Nanoparticles

In the first step, 2.5 mmol of cadmium chloride monohydrate (CdCl2·H2O) was dissolved in 3 mL of deionized water. The cadmium chloride solution was then mixed with 5.0 mmol of MPA in 30 mL of DMF and stirred vigorously for 10 min. In the second step, 3 mL of aqueous sodium sulfide solution (Na2S: 1.67 mmol) was slowly added dropwise to the cadmium chloride solution with stirring. After the solutions were mixed, the resulting solution immediately turned yellow and cloudy. Then the reaction was allowed to continue for an additional 4 h at room temperature, and the yellow solution gradually became transparent. At the end, the product was centrifuged (10,000 rpm), washed several times with DMF, and finally washed with water.


### 2.3. Synthesis of pNIPAAm

pNIPAAm was synthesized using free-radical polymerization at 70°C as follows: 1.18 g (10.4 mmol) ofN-isopropylacrylamide was added to 12 mL of DMF. The reaction medium was carefully degassed and maintained under a nitrogen purge. Then, 9.15×10-6 mol of AIBN was dissolved in the reaction mixture. The solution was degassed by bubbling with nitrogen for 30 min. The reaction mixture was refluxed at 70°C for 7 h under nitrogen. Upon completion of the reflux, the product was precipitated upon the addition of diethyl ether and then dried in vacuum. The number-average molecular weight (Mn) and molecular weight distribution (Mw) of the polymer were measured using GPC and were found to be Mn=25,890 and Mw/Mn=1.08, respectively.


### 2.4. Preparation of CdS@pNIPAAm Nanocomposites

In a typical synthesis, 10 mL of 0.05% polymer solution in water was placed in a 25 mL beaker and stirred for 3 h at room temperature for complete dissolution. To this solution, 500μL of 0.2 mmol/L freshly prepared CdS NPs in water was added. This mixture was stirred for 1 h. This solution was used for further characterization studies.


### 2.5. Characterization

The molecular weight of the polymer was determined using gel permeation chromatography (GPC) (Waters 515, MA, USA) on an instrument that was equipped with a differential refractometer detector (Waters 2410, MA, USA). THF served as the mobile phase with a flow rate of 1 mL/min. Number-average molecular weights and polydispersity indices were calculated from a calibration curve using a series of polystyrene standards (Polymer Laboratories, MA, USA) with molecular weights that ranged from 1350 to 151,700. The UV-vis absorption spectra were detected with a Varian Cary 50 Bio UV-vis spectrophotometer over a wavelength range of 320–650 nm using DMF as a solvent. All of the samples for UV-vis were centrifuged prior to measurement by adding an excess amount of water to remove the impurities and redispersing them in DMF. Transmission electron microscope (TEM) studies of the samples were performed by depositing a drop of sample that was dispersed in DMF onto a carbon-coated copper grid and allowing it to air dry at room temperature. A JEOL JEM-2100 transmission electron microscope operating at an accelerating voltage of 200 kV was used for these measurements. The photoluminescence (PL) spectra were measured at room temperature on an FA-375 luminescence spectrometer (Thermospectronic, USA) operating with a 365 nm laser beam as a light source. The powder X-ray diffraction (XRD) patterns were acquired on a Bruker-AXS D8 ADVANCE X-ray diffractometer at a scanning rate of 0.02 steps/s from 20 to 70° with Cu Kα radiation (λ=0.1542 nm). The Fourier-transform infrared (FTIR) spectra were scanned over the range of 400–4000 cm−1 with a potassium bromide plate on a Perkin-Elmer Spectrum-One spectrophotometer. To measure the LCSTs of the colloidal CdS@pNIPAAm nanocomposite and pNIPAAm, the cloud-point method (turbidimetry) was employed. Briefly, the LCST of aqueous colloidal solutions ((CdS) = 0.20 mmol/L) were measured on a UV-vis spectrophotometer (Lambda 45, Perkin Elmer) at 500 nm using a peltier-thermostattable 9-cell holder; the solution temperature was increased from 20 to 45°C at 1°C intervals. At each temperature, the samples were stabilized for 10 min prior to the measurements. The LCST values of the colloids were determined at the temperature where the sample exhibited an optical transmittance of 50%.


## 2.1. Materials

Cadmium chloride, sodium sulfide, 2,2′-azodiisobutyronitrile (AIBN), and dryN,N-dimethylformamide (DMF) were supplied by Merck (India) and used as received. N-Isopropylacrylamide was obtained from Aldrich, recrystallized in hexane, and dried under vacuum before use. 3-Mercaptopropionic acid (MPA) was purchased from Sigma-Aldrich. The water used in all experiments was purified to a resistance of 10 MΩ (Milli-Q Reagent Water System, Millipore Corporation) and filtered through a 0.2 μm filter to remove any particulate matter.


## 2.2. Synthesis of MPA-Modified CdS Nanoparticles

In the first step, 2.5 mmol of cadmium chloride monohydrate (CdCl2·H2O) was dissolved in 3 mL of deionized water. The cadmium chloride solution was then mixed with 5.0 mmol of MPA in 30 mL of DMF and stirred vigorously for 10 min. In the second step, 3 mL of aqueous sodium sulfide solution (Na2S: 1.67 mmol) was slowly added dropwise to the cadmium chloride solution with stirring. After the solutions were mixed, the resulting solution immediately turned yellow and cloudy. Then the reaction was allowed to continue for an additional 4 h at room temperature, and the yellow solution gradually became transparent. At the end, the product was centrifuged (10,000 rpm), washed several times with DMF, and finally washed with water.


## 2.3. Synthesis of pNIPAAm

pNIPAAm was synthesized using free-radical polymerization at 70°C as follows: 1.18 g (10.4 mmol) ofN-isopropylacrylamide was added to 12 mL of DMF. The reaction medium was carefully degassed and maintained under a nitrogen purge. Then, 9.15×10-6 mol of AIBN was dissolved in the reaction mixture. The solution was degassed by bubbling with nitrogen for 30 min. The reaction mixture was refluxed at 70°C for 7 h under nitrogen. Upon completion of the reflux, the product was precipitated upon the addition of diethyl ether and then dried in vacuum. The number-average molecular weight (Mn) and molecular weight distribution (Mw) of the polymer were measured using GPC and were found to be Mn=25,890 and Mw/Mn=1.08, respectively.


## 2.4. Preparation of CdS@pNIPAAm Nanocomposites

In a typical synthesis, 10 mL of 0.05% polymer solution in water was placed in a 25 mL beaker and stirred for 3 h at room temperature for complete dissolution. To this solution, 500μL of 0.2 mmol/L freshly prepared CdS NPs in water was added. This mixture was stirred for 1 h. This solution was used for further characterization studies.


## 2.5. Characterization

The molecular weight of the polymer was determined using gel permeation chromatography (GPC) (Waters 515, MA, USA) on an instrument that was equipped with a differential refractometer detector (Waters 2410, MA, USA). THF served as the mobile phase with a flow rate of 1 mL/min. Number-average molecular weights and polydispersity indices were calculated from a calibration curve using a series of polystyrene standards (Polymer Laboratories, MA, USA) with molecular weights that ranged from 1350 to 151,700. The UV-vis absorption spectra were detected with a Varian Cary 50 Bio UV-vis spectrophotometer over a wavelength range of 320–650 nm using DMF as a solvent. All of the samples for UV-vis were centrifuged prior to measurement by adding an excess amount of water to remove the impurities and redispersing them in DMF. Transmission electron microscope (TEM) studies of the samples were performed by depositing a drop of sample that was dispersed in DMF onto a carbon-coated copper grid and allowing it to air dry at room temperature. A JEOL JEM-2100 transmission electron microscope operating at an accelerating voltage of 200 kV was used for these measurements. The photoluminescence (PL) spectra were measured at room temperature on an FA-375 luminescence spectrometer (Thermospectronic, USA) operating with a 365 nm laser beam as a light source. The powder X-ray diffraction (XRD) patterns were acquired on a Bruker-AXS D8 ADVANCE X-ray diffractometer at a scanning rate of 0.02 steps/s from 20 to 70° with Cu Kα radiation (λ=0.1542 nm). The Fourier-transform infrared (FTIR) spectra were scanned over the range of 400–4000 cm−1 with a potassium bromide plate on a Perkin-Elmer Spectrum-One spectrophotometer. To measure the LCSTs of the colloidal CdS@pNIPAAm nanocomposite and pNIPAAm, the cloud-point method (turbidimetry) was employed. Briefly, the LCST of aqueous colloidal solutions ((CdS) = 0.20 mmol/L) were measured on a UV-vis spectrophotometer (Lambda 45, Perkin Elmer) at 500 nm using a peltier-thermostattable 9-cell holder; the solution temperature was increased from 20 to 45°C at 1°C intervals. At each temperature, the samples were stabilized for 10 min prior to the measurements. The LCST values of the colloids were determined at the temperature where the sample exhibited an optical transmittance of 50%.


## 3. Results and Discussion

It is well known that the optical and electronic properties of NPs are dominated by carrier confinement (electron/hole), which results in a size dependence of their optical properties, including light absorption, photoluminescence (PL), electroluminescence (EL), and cathodoluminescence (CL) [37]. Here, the typical synthesis of COOH-modified CdS NPs involves the reaction between cadmium and sulfur ions in the presence of organic ligands containing mercapto groups (Scheme 1). The electron-deficient cadmium atoms on the surfaces of semiconductors serve as binding sites to anchor organic ligands and to hinder the further growth of crystal grains. These effects result in the formation of nanosized crystals. Winter et al. [38] reported using MPA to prepare CdS NPs from cadmium chloride and sodium sulfide. However, the reaction had to be performed at high pH for approximately 4 h. In the present method, CdS NPs were prepared at neutral pH to improve their dispersibility in water.Scheme 1
Synthesis of MPA-bound CdS NPs and CdS/polymer nanocomposite hybrids.Figure1 shows a typical transmittance versus temperature curve of a CdS@pNIPAAm nanocomposite sample and pNIPAAm alone. The CdS@pNIPAAm composites are thermoresponsive in water, as are pNIPAAm. The phase-transition temperature or LCST was observed at approximately 30.7°C for the CdS@pNIPAAm composite. Below the phase-transition temperature or LCST, the pNIPAAm is hydrophilic (due to the formation of individual random-coil chains) and the colloidal dispersion of the CdS@pNIPAAm composite is transparent, as shown in inset photograph A in Figure 1. Above the LCST, the pNIPAAm gradually becomes hydrophobic (due to the formation of a single-chain globule or multichain aggregation) and collapses onto the surface of the CdS nanoparticles [23, 39, 40]; the colloidal dispersion becomes turbid during this process, as shown in inset photograph B in Figure 1. When the colloidal dispersion of CdS@pNIPAAm composite solutions were kept at room temperature (~25°C), that is, below the LCST value, for overnight after the phase-transition experiments, precipitation started, and the obtained solid was difficult to redisperse. The LCST value of the CdS/pNIPAAm composite decreases to 30.7°C compared to LCST values of approximately 32.0°C for the pure pNIPAAm (Figure 1) and approximately 32.6°C for the MPA-pNIPAAm mixture without CdS (data not shown). When the MPA-bound CdS@pNIPAAm composite is dispersed in aqueous solution, several interactions between the polymer and the MPA-bound CdS NPs can occur. These interactions can be either van der Waals or H-bonding interactions (inter- or intra-molecular H-bonding) [39]. The polymer itself can form H-bonds between its own –CONH groups and water molecules. Similarly, the –COOH groups of the MPA could form H-bonds with water as well as with the polymer below the LCST. Above the LCST, the polymer shrinks to a form where water molecules are expelled from the network, and when MPA-bound CdS NPs are part of the polymer structures, the H-bonding would primarily occur between the –COOH groups of the MPA-bound CdS NPs and those (along with amide groups) of the polymer. The decrease in the LCST values of the MPA-bound CdS@pNIPAAm composite may be influenced by the unbinding or loss of MPA from the composite. It is known that the bond between a metal and sulfide is not very stable at high temperatures [41]. Thus, parts of the MPA-bound CdS@pNIPAAm chains possibly disengage from the CdS NPs when the colloidal dispersion is heated above the LCST, which results in a decrease of the LCST value of the composite.Figure 1
Plot of transmittance of a colloidal solution of CdS@pNIPAAm and pNIPAAm (pure polymer) dispersed in water as a function of temperature at a wavelength of 500 nm; concentration ofCdS=0.2 mmol/L. Insets: photographs of the colloidal solution of CdS@pNIPAAm in water at (A) 25°C and (B) 40°C.To investigate the effects of ligand concentration on the particle sizes of CdS NPs, the absorbance of CdS nanoparticles prepared with different molar ratios of ligand to Cd2+ was measured using UV-vis spectrophotometry. As shown in Figure 2, a weak blue shift in the maximum absorption band from 422 to 406 nm occurs as the concentration of organic ligand increases. The absorption peaks of three samples of different molar ratios of ligand to Cd2+ are centered at 406, 415, and 422 nm, respectively. The blue shift is consistent with the quantum confinement effect due to decreasing particle size because the higher concentration of ligand is unfavorable to the nucleation and growth of CdS NPs. The electron-deficient atoms of cadmium on the surface of semiconductors serve as binding sites to anchor organic ligands and to hinder the further growth of crystal grains; these combined effects result in the formation of nanosized crystals. The as-prepared MPA-bound CdS NPs are stable at room temperature, and we did not observe any precipitation over a period of more than 30 d. In the control experiment without MPA as the organic ligand, CdS particles were prepared in the polymer solution and we observed yellow sediments immediately after the addition of Na2S. The stability of MPA-bound CdS composite nanoparticles over long storage periods again confirms that the nanoparticles are immobilized by the pNIPAAm molecules. It is reasonable to expect that the complexation between MPA-bound CdS nanoparticles and pNIPAAm chains contributes to the stabilization of CdS nanoparticles within the polymer shell. This point will be discussed in more detail below.Figure 2
UV-vis absorption spectra of CdS NPs prepared at H2O/DMF; 0.2/1.0 w/w and different molar ratios of MPA/Cd2+; reaction time 3 h at 25°C.According to Brus, [42] the excitation energy of NPs is inversely proportional to their particle size. The higher energy makes the position of the maximum absorption peak in a NC’s UV-vis spectrum shift toward the blue region. The calculated particle size of the CdS NPs prepared with 1/1 molar ratio of MPA/Cd2+ is 3.89 nm according to Siu et al. [40], whereas the particle sizes in the other two samples are 3.58 nm (MPA/Cd2+ = 0.5/1 mol/mol) and 4.14 nm (MPA/Cd2+ = 2/1 mol/mol). These values are similar to the particle size observed directly from the TEM image and selected-area electron diffraction (SAED) pattern with crystal structure shown in Figure 3, which demonstrates that the mean size of the CdS NPs is approximately 4 nm and that the particles are thoroughly dispersed in the DMF solution. The results also show that the as-prepared CdS NPs behave as quantum dots.Figure 3
Typical transmission electron microscopy image of CdS NPs dispersed in DMF. Scale bar represents 50 nm. Inset: SAED pattern of the same CdS nanoparticles.DMF is used as an organic solvent to enhance the solubility of CdS NPs because they are unavailable in aqueous solution without the addition of DMF. The weight ratio of H2O to DMF in the solution also affects the particle size, which can be easily observed through the transparency of the solution. Precipitation of CdS is observed when the weight ratio (H2O/DMF) exceeds 1.5. The UV-vis absorption spectra of CdS NPs prepared with weight ratios of H2O/DMF ranging from 0.2/1.0 to 0.9/1.0 are presented in Figure 4. With the same reagent concentrations (Cd2+/S2− = 1/0.67 mol/mol), the absorption peaks of H2O/DMF in weight ratios of 0.2/1.0, 0.5/1.0, and 0.9/1.0 (Figure 4(a)) center at 406, 425, and 428 nm, respectively. The corresponding particle diameters of CdS NPs, calculated according to the method of Yu et al. [43], are 3.58, 4.25, and 4.37 nm, respectively. At higher concentrations of DMF, the absorption band is blue-shifted, which indicates that the DMF concentration affects the size of the CdS NPs. A slight blue shift (up to 22 nm) is caused by the change in the dielectric constant of the environment that surrounds the CdS NPs. As previously reported [44–46], the blue shift in the excitonic absorbance spectrum of nanometer-sized semiconductor particles is a phenomenon that is normally attributed to the quantum size effect on band-gap properties and the changing dielectric constant of the surrounding medium.(a) UV-vis absorption spectra of CdS NPs of different weight ratios of H2O/DMF (MPA/Cd2+ = 2.0/1.0 mmol); reaction time 3 h. (b) UV-vis absorption spectra of polymer, polymer-CdS composites, and CdS NPs diluted in DMF at 25°C.
(a)
(b)To confirm that the CdS NPs are well dispersed and bound to the polymer matrix, the UV-vis absorption spectra of polymer-CdS composites with various concentrations of CdS NPs were measured and compared with the spectrum of the pure polymer. Figure4(b) shows the UV-vis absorption spectra of the pure polymer, polymer-CdS composites (CdS = 2 and 5 wt%), and CdS NPs diluted with DMF. As shown in Figure 4(b), no absorption peak is evident for the pure polymer, whereas an absorption peak can be observed in the polymer-CdS composites and pure CdS NPs at 400 nm; this result indicates that the size of the CdS NPs in the composites does not change and is maintained at approximately 4 nm. In addition, the strength of the absorption peak is enhanced with increased CdS concentration.As a typical semiconductor, CdS NPs exhibit interesting optical properties. Figure5 shows the fluorescence emission spectra of the ligand-modified, COOH-coated CdS NC suspension and a polymer composite with excitation at 365 nm. As shown in Figure 5, the characteristic emission of CdS NPs occurs at approximately 410, 445, and 620 nm. The emission at 620 nm is assigned to electron-hole recombinations at surface traps, whereas the higher-energy emission at 410 and 445 nm are attributed to recombination from the free excitons state in the interior of the crystallites [41, 47, 48]. Spectrum 5(ii) shows that an increase in the emission peak strength and bandwidth occurs in the CdS-polymer composite. Usually, the energy and bandwidth of CdS photoluminescence bands relate to the size and nature of carrier-trap states that are located at the surfaces of NPs. The effect of band broadening may be explained by the surface structure of CdS NPs and the change in their particle sizes when the CdS NPs are bound to the polymer backbone via H-bonds.Figure 5
Fluorescence emission spectra of (i) a suspension of MPA-modified CdS NPs, and (ii) CdS = 4.0 wt% polymer composite withλex=365 nm at 25°C.To investigate the effect of MPA ligands on the structure of CdS NPs, the samples containing MPA ligands and control samples were characterized using XRD (Figure6). The XRD patterns of CdS (JCPDS 10-454) with different concentrations of MPA and without MPA ligands exhibit characteristic peaks at scattering angles (2θ°) of 26.40, 43.90, and 51.90, which correspond to scattering from the (111), (220), and (311) planes, respectively. The XRD peaks of CdS samples containing MPA broaden, which indicates that the particle sizes of CdS crystals prepared with MPA ligand become smaller. However, the presence of the organic MPA ligand in the preparation of CdS cannot change the structure of the CdS crystals. According to the Scherrer equation [49], the average sizes of the NPs are approximately 3.5, 3.8, and 3.8 nm based on calculations using the width of the (220) peak for MPA/Cd2+ = 2/1 mol/mol, 1/1 mol/mol, and 0.5/1 mol/mol, respectively.Figure 6
XRD patterns of CdS NC powders fabricated with different MPA concentrations (i) MPA/Cd2+ = 2.0/1.0 mol/mol, (ii) MPA/Cd2+ = 1.0/1.0 mol/mol, and (iii) MPA/Cd2+ = 0.5/1.0 mol/mol; solvent H2O/DMF = 0.2/1.0 w/w, reaction time 3 h. Inset shows the XRD pattern of CdS NC powder without addition of MPA.The FTIR spectra of the CdS NPs, pure polymer, and CdS@pNIPAAm nanocomposites are shown in Figure7. From the FTIR spectrum of CdS NPs (Figure 7(i)), the peak at 1713 cm−1 represents the C=O double-bond stretching vibration in the carboxylic acid groups bound to the CdS particles. The peaks at 1655 and 1553 cm−1 represent the amide I and amide II peaks of pure pNIPAAm, respectively. However, in the spectra of the composites, shifts in the N–H deformation peak of the pNIPAAm network and in the C=O stretching peak of the CdS-COOH-modified composite were observed. The wavenumber of the N–H peak decreases from 1655 to 1651 cm−1 and from 1553 to 1549 cm−1 for amide I and II, respectively. The shifts for both peaks are approximately four units to the lower wavenumber. The equipment error is within one unit. The wavenumber of the C=O peak in the CdS-COOH-modified sample shifts from 1713 to 1724 cm−1 in the case of the CdS-polymer composite. This result indicates that there is an interaction between the carboxylic groups of –COOH and the amide groups of pNIPAAm [49]. Also, the widths of the peaks in the composites increased relative to the CdS-COOH modified NPs.Figure 7
FTIR spectra of MPA-modified CdS NPs (i); polymer-CdS composite (ii); polymer (iii).


## 4. Conclusion

Nanocomposites of CdS@pNIPAAm with well-tailored optical properties have been prepared via MPA-bound CdS NPs and pNIPAAm. The CdS NPs were obtained using the reaction between cadmium chloride and sodium sulfide in the presence of MPA as the organic ligand. The COOH-terminated alkyl group attached to the surfaces of the CdS NPs enhances their dispersibility in the solvent, thereby allowing control of the particle size of the NPs. The effect of concentration of the reactants and solvents on the particle size of as-prepared CdS NPs has been thoroughly investigated. The size of CdS NPs characterized with TEM is approximately 4 nm, in good agreement with the calculated data from UV-vis absorption spectra. In addition, the UV-vis absorption band is blue-shifted for the higher concentrations of MPA ligand and DMF, thus indicating that their concentrations are a key factor for the particle size of CdS. The FTIR characterization indicates the formation of a robust bonding between the CdS NPs and the organic ligand. The as-prepared CdS@pNIPAAm particles exhibit a temperature-responsive behavior and their phase-transition temperature is approximately 30.7°C.



---

*Source: 451506-2012-06-14.xml*