# Antibacterial Activity of Silver Nanoparticles Synthesized by Bark Extract ofSyzygium cumini

Authors: Ram Prasad; Vyshnava Satyanarayana Swamy
Journal: Journal of Nanoparticles
 (2013)

---

## Abstract

The unique property of the silver nanoparticles having the antimicrobial activity drags the major attention towards the present nanotechnology. The environmentally nontoxic, ecofriendly, and cost-effective method that has been developed for the synthesis of silver nanoparticles using plant extracts creates the major research interest in the field of nanobiotechnology. The synthesized silver nanoparticles have been characterized by the UV-visible spectroscopy, atomic force microscopy (AFM), and scanning electron microscopy (SEM). Further, the antibacterial activity of silver nanoparticles was evaluated by well diffusion method, and it was found that the biogenic silver nanoparticles have antibacterial activity againstEscherichia coli (ATCC 25922), Staphylococcus aureus (ATCC 29213), Pseudomonas aeruginosa (ATCC 27853), Azotobacter chroococcum WR 9, and Bacillus licheniformis (MTCC 9555).


---

## Body

## 1. Introduction

The broad spectrum of nanotechnology is important in the major fields of biology, chemistry, physics, and material sciences. Nanotechnology deals with the study of materials at the nanometers [1, 2]. The day to day development of nanotechnology creates a major interest in the development and fabrications of different dimensioned nanoparticles [3]. The nanomaterials can be synthesized by different methods including chemical, physical, irradiation, and biological methods. The development of new chemical or physical methods has resulted in environmental contaminations, since the chemical procedures involved in the synthesis of nanomaterials generate a large amount of hazardous byproducts [4]. Thus, there is a need for “green nanotechnology” that includes a clean, safe, ecofriendly, and environmentally nontoxic method of nanoparticle synthesis, and in this method there is no need to use high pressure, energy, temperature, and toxic chemicals [5, 6]. The biological methods include synthesis of nanomaterial’s from the extracts of plant, bacterial, fungal species, and so forth. The synthesis of nanoparticles from the plant extracts is considered to be a process [7]. The preparation and maintenance of fungal and bacterial cultures are  time consuming and require aseptic conditions and large manual skills to maintain the cultures [8].Plant extracts include bark, root, leaves, fruit, flowers, rhizoids, and latex and are used to synthesize the nanoparticles. These nanoparticles show different dimensions including the size, shape, and dispersion which have more efficacy than those synthesized from the chemical and physical procedures. Therefore, the use of green plants for similar nanoparticle biosynthesis methodologies is an exciting possibility which has compatibility for pharmaceutical and other biomedical applications, as they do not use toxic chemicals for the synthesis of nanoparticles [9, 10].Nanoparticles had a wide variety of application in the major fields of medicine, electronics, therapeutics, and diagnostic agents. Silver nanoparticles have wide application in biomedical science like treatment of burned patients, antimicrobial activity and used the targeted drug delivery, and so forth [11]. Nowadays the nanoparticles are coated on the medical appliances, food covering sheets, and cans for storing the beverages and food [12–14]. However, there are many problems and toxicity of using metal oxide nanoparticles on the human health. Use of plants for the synthesis of nanoparticles does not require high energy, temperatures, and it is easily scaled up for large scale synthesis, and it is cost effective too [15–17].Syzygium cumini is a medicinal plant available in the tropical forests and is used for treatment of diabetes. The leaves and bark are used for controlling blood pressure and gingivitis [14]. The plant contains a variety of phytochemical compounds such as phenols, tannins, alkaloids, glycosides, amino acids, and flavones, and these molecules are expected to self-assemble and cap the metal nanoparticles formed in their presence and thereby induce some shape control during metal ion reduction [18]. In this study we used the silver nanoparticles synthesized from the bark extract of S. cumini and its antibacterial effect on the bacteria, namely,Escherichia coli(ATCC 25922), Staphylococcus aureus(ATCC 29213), Pseudomonas aeruginosa(ATCC 27853), Azotobacter chroococcumWR 9, andBacillus licheniformis (MTCC 9555).


## 2. Materials and Methods

### 2.1. Chemicals

All analytical reagents and media components were purchased from HiMedia (Mumbai, India) and Sigma Chemicals (St. Louis, MO, USA).


### 2.2. Preparation of Plant Extract

The fresh bark ofSyzygium cumini was collected and kept in hot air oven for drying at 60°C for six hours. The dried bark was chopped into fine pieces with the help of mixer grinder. It was collected, weighed for 2.5 g, and then mixed in 100 mL of double distilled water. This mixture was boiled at 60°C in the water bath for one hour. The solution was cooled at room temperature and filtered by Whatman filter paper No. 1. The filtrate was collected and stored at 4°C for further experiment.


### 2.3. Synthesis of Silver Nanoparticles

Silver nanoparticles (AgNO3) were synthesized by reducing the freshly prepared 1 mM silver nitrate and stored under dark conditions with the bark extract. The reaction mixture was prepared in ratio of 9 : 1 (V/V) of freshly prepared silver nitrate solution and bark extract, respectively. The initial color of the solution was observed.


### 2.4. UV-Visible Spectroscopy

The silver nanoparticles show the plasmon resonance at 400 to 450 nm in the UV-Visible spectrum. The UV-Visible spectrum of synthesized silver nanoparticles was analysed by spectrophotometer (LAB INDIA UV 300+).


### 2.5. Atomic Force Microscopy

Atomic force microscopy is an advanced characterization technique to identify the size, shape, and dispersion of the silver nanoparticles. In order to characterize the silver nanoparticles, the sample was prepared by sonication at room temperature for about 15 minutes in the ultrasonicator. Then the sample solution was dried as a thin layer on mica-based glass slide which was used to view under the AFM Model NT-MDA Solver.


### 2.6. Scanning Electron Microscopy

SEM analysis of the silver nanoparticles provides the information regarding the dimensions including the surface, shape, and size. The sample was prepared by sonicating the sample solution for 15 minutes at room temperature. A small drop of sonicated sample was dried on a glass slide, and it was coated by gold and observed under ZEISS EVO HD SEM.


### 2.7. Antibacterial Property

The antibacterial property of the silver nanoparticles was determined by using the bacterial species including the pathogenic bacteria such asEscherichia coli(ATCC 25922), Staphylococcus aureus(ATCC 29213), Pseudomonas aeruginosa(ATCC 27853), Azotobacter chroococcumWR 9, and Bacillus licheniformis(MTCC 9555), by the well diffusion method [14]. The different concentrations used were at low concentrations (2, 5, 10, and 15 μL) and at higher concentrations (25, 50, 75, and 100 μL) for the identification of antimicrobial activity of the above bacterial species. All the plates were incubated at 37°C for 24 hours, and the zone of inhibition of bacteria was measured.


## 2.1. Chemicals

All analytical reagents and media components were purchased from HiMedia (Mumbai, India) and Sigma Chemicals (St. Louis, MO, USA).


## 2.2. Preparation of Plant Extract

The fresh bark ofSyzygium cumini was collected and kept in hot air oven for drying at 60°C for six hours. The dried bark was chopped into fine pieces with the help of mixer grinder. It was collected, weighed for 2.5 g, and then mixed in 100 mL of double distilled water. This mixture was boiled at 60°C in the water bath for one hour. The solution was cooled at room temperature and filtered by Whatman filter paper No. 1. The filtrate was collected and stored at 4°C for further experiment.


## 2.3. Synthesis of Silver Nanoparticles

Silver nanoparticles (AgNO3) were synthesized by reducing the freshly prepared 1 mM silver nitrate and stored under dark conditions with the bark extract. The reaction mixture was prepared in ratio of 9 : 1 (V/V) of freshly prepared silver nitrate solution and bark extract, respectively. The initial color of the solution was observed.


## 2.4. UV-Visible Spectroscopy

The silver nanoparticles show the plasmon resonance at 400 to 450 nm in the UV-Visible spectrum. The UV-Visible spectrum of synthesized silver nanoparticles was analysed by spectrophotometer (LAB INDIA UV 300+).


## 2.5. Atomic Force Microscopy

Atomic force microscopy is an advanced characterization technique to identify the size, shape, and dispersion of the silver nanoparticles. In order to characterize the silver nanoparticles, the sample was prepared by sonication at room temperature for about 15 minutes in the ultrasonicator. Then the sample solution was dried as a thin layer on mica-based glass slide which was used to view under the AFM Model NT-MDA Solver.


## 2.6. Scanning Electron Microscopy

SEM analysis of the silver nanoparticles provides the information regarding the dimensions including the surface, shape, and size. The sample was prepared by sonicating the sample solution for 15 minutes at room temperature. A small drop of sonicated sample was dried on a glass slide, and it was coated by gold and observed under ZEISS EVO HD SEM.


## 2.7. Antibacterial Property

The antibacterial property of the silver nanoparticles was determined by using the bacterial species including the pathogenic bacteria such asEscherichia coli(ATCC 25922), Staphylococcus aureus(ATCC 29213), Pseudomonas aeruginosa(ATCC 27853), Azotobacter chroococcumWR 9, and Bacillus licheniformis(MTCC 9555), by the well diffusion method [14]. The different concentrations used were at low concentrations (2, 5, 10, and 15 μL) and at higher concentrations (25, 50, 75, and 100 μL) for the identification of antimicrobial activity of the above bacterial species. All the plates were incubated at 37°C for 24 hours, and the zone of inhibition of bacteria was measured.


## 3. Results and Discussion

The green synthesis of silver nanoparticles usingS. cumini bark extract was successfully carried out, as the change in the color of the solution from yellowish brown to dark brown color exhibits the reduction of the silver nitrate in aqueous solution due to excitation of surface plasmon vibrations in silver nanoparticles [19]. During this reaction process the pH of the solution changes from 5.93 to 5.72, which implies that the reaction occurs under acidic condition.This complete reaction occurs in seven hours. The brown to dark brown color change of the reaction mixture indicated the formation of silver nanoparticles (Figure 1).Syzygium cumini bark extract sample. Change in the color of the solution from brown to dark brown. (a) Silver nitrate solution, (b) reaction mixture, and (c) change in the color of the solution.
(a)
(b)
(c)The formation of silver nanoparticles was confirmed through measurement of UV-Visible spectrum of the reaction mixture. The UV-Visible spectrophotometric analysis of colloidal reaction mixture of silver nanoparticles synthesized usingS. cumini bark showed sharp peak at 427 nm in the spectrum, and broadening of peak indicated that the particles are polydispersed [20] (Figure 2). The efficiency of this method was tested for stability also. The reaction mixture was stored for 45 days, and no precipitation in the solution was observed. It was also checked through UV-Vis absorption on regular interval.Figure 2
UV-visible spectrum of silver nanoparticles.The atomic force microscopy (AFM) results display the surface morphology of the monodispersed silver nanoparticles usingS. cumini bark extract. The particle size of the silver nanoparticles that ranges from 20 to 60 nm was observed. The topographical image of silver nanoparticles indicated that they are agglomerated and formed distinct nanoparticles (Figures 3(a) and 3(b)). The bright spots on the micrograph indicated that the nanoparticles are spherical in shape.Atomic force microscopy. (a) Image of synthesized silver nanoparticles and (b) its histogram.
(a)
(b)The biosynthesized silver nanoparticles were characterized by scanning electron microscopy for their morphology and size. The SEM micrograph reveals that the synthesized silver nanoparticles have spherical morphology with size range from 20 to 60 nm and also indicated that the particles are well separated showing no agglomeration (Figure4).Figure 4
SEM images of silver nanoparticles synthesized byS. cumini bark extract.The different species of bacteria show zone of inhibition in the well diffusion method of antimicrobial activity. The different patterns of the zone of inhibitions are observed in Figure5. Synthesized silver nanoparticles showed antibacterial activity against both Gram positive and negative bacteria (Figure 6). The highest zone of inhibition was observed for Bacillus licheniformiseven at lower concentration. The exact mechanism of the inhibition of the bacteria is still unknown, but some hypothetical mechanisms show that the inhibition is due to ionic binding of the silver nanoparticles on the surface of the bacteria which creates a great intensity of the proton motive force, and the one hypothesis from the research states that the silver nanoparticles invade the bacterial cell and bind to the vital enzymes containing thiol groups [12, 21, 22]. Also, the findings of Sereemaspun et al. (2008) [23] suggested the inhibition of oxidation-based biological process by penetration of metallic nanosized particles across the microsomal membrane [23, 24]. The molecular basis for the biosynthesis of these silver crystals speculated that the organic matrix contains silver binding properties that provide amino acid moieties that serve as the nucleation sites [25, 26].Antibacterial effects varying the concentrations of silver nanoparticles samples, (a) lower concentrations (2, 5, 10, and 15μL) and (b) Higher concentrations (25, 50, 75, and 100 μL).
(a)
(b)Figure 6
Antibacterial activity ofSyzygium cumini,with different concentrations ranging from 2, 5, 10, 15, 25, 50, 75, and 100 μL.


## 4. Conclusions

The biological synthesis of the silver nanoparticles is rapid, ecofriendly, cost-effective, and simple method of synthesis. In the present study-silver nanoparticles are synthesized at room temperature within a less span of time. The synthesized silver nanoparticles were characterized by UV-visible spectrometer, AFM, and SEM analysis. The size of the nanoparticles ranges from 20 to 60 nm with spherical shape. AFM and SEM reveal that the synthesized silver nanoparticles are well dispersed showing no agglomeration. These nanoparticles showed a broad spectrum antimicrobial activity against both Gram positive and Gram negative bacteria. Investigation on the antibacterial activity of synthesized silver nanoparticles usingcumini extract against Staphylococcus aureus and Bacillus licheniformis reveals high potential as antimicrobial agent in pharmaceutical, food, and cosmetic industries.



---

*Source: 431218-2013-04-30.xml*