# The Effects of Malonic Acid Derivatives and Acetic Acid Derivatives as Coadsorbents on the Photovoltaic Performance of Dye-Sensitized Solar Cells

Authors: Hiroaki Matsuyoshi; Haruo Tomita; Hitoshi Nishino; Hiroki Sakamoto; Kyohei Manabe
Journal: International Journal of Photoenergy
 (2013)

---

## Abstract

The effects of malonic acid derivatives and acetic acid derivatives as coadsorbents on the photovoltaic performance of D908 dye-sensitized nanocrystalline TiO2 solar cells were investigated. Each of phenylmalonic acid (PMA) and cyclopentylacetic acid (CPEAA) coadsorptions was revealed to improve both the photocurrent and the photovoltage of the solar cells. The improved photocurrent was probably due to the suppression of self-quenching of the excited electrons in the dyes by coadsorption of PMA or CPEAA on the TiO2 that increased in the electron-injection yields from the dye to the TiO2. The improved photovoltage was probably due to suppression of recombination between the injected electrons and I3- ions on the TiO2 surface. ATR-FTIR spectroscopy indicated that PMA or CPEAA coadsorption increased the content of bound dye on the TiO2 surface. This result suggests that PMA or CPEAA coadsorption improved the photocurrent of the solar cells. Electrochemical impedance spectroscopy indicated that PMA or CPEAA coadsorption on the TiO2 surface increased the charge recombination resistance (R2) and decreased the diffusion resistance in the electrolyte (R3). These results suggest that the coadsorption of PMA or CPEAA on the TiO2 may improve its photovoltage and photocurrent.


---

## Body

## 1. Introduction

Dye-sensitized solar cells (DSCs) do not use high-purity silicon, and their manufacturing process is simple and of low cost. DSCs are expected to reduce the manufacturing cost significantly compared with conventional p-n junction solar cells.A great deal of effort has been made to improve the photovoltaic performance of DSCs [1–4].In our previous paper, we studied TiO2 materials [5] and electrolytes [6].The above study was found to be very important to control the interface between TiO2 and dye electrolyte.Dyes are required to be adsorbed on the TiO2 in a monolayer without association or aggregation in order to suppress self-quenching of the excited electrons in the dyes.To reduce association or aggregation of dyes, several carboxylic acid derivatives have been studied. For example, there are several reports using 3-phenylpropionic acid [7], deoxycholic acid [8], chenodeoxycholic acid [9], stearic acid [10], 4-guanidinobutyric acid [11], and hexadecylmalonic acid [12].The coadsorption of dyes on the TiO2 surface is expected to improve both the photocurrent and the photovoltage of DSC cells. The improved photocurrent can be attributed to a positive shift of the conduction band edge of TiO2 [13] or to suppression of self-quenching of the excited electrons in the dyes [14]. The improved photovoltage can be caused by suppression of recombination between the injected electrons and I3- ions [12, 13].In this paper, we report the effects of malonic acid derivatives and acetic acid derivatives as coadsorbents on the photovoltaic performance of DSC cells sensitized by D-908 dye (Figure1).Figure 1
Structure of D908 dye.Especially, dicarboxylic acids such as malonic acid derivatives could be anchored to the surface of  TiO2 more effectively than monocarboxylic acids, and there are few previous papers about dicarboxylic acids as coadsorbents [12]. So, we choose malonic acids derivatives as coadsorbents.


## 2. Materials and Methods

### 2.1. D908 Dye

The molecular structure of D908 dye is shown in Figure1.D908 dye is one of the derivatives of Z907 dye. One of the protons bonded to the carboxylic groups is substituted by benzyltrimethylammonium cation.D908 dye was purchased from Everlight Chemical Industrial Co., and used as supplied without further purification.


### 2.2. Malonic Acid Derivatives and Acetic Acid Derivatives

We chose six malonic acid derivatives including alkyl, cycloalkyl, and phenyl groups shown in Figure2 and six acetic acid derivatives including alkyl, cycloalkyl, and naphthyl groups shown in Figure 3.Figure 2
Structures of malonic acid derivatives.Figure 3
Structures of acetic acid derivatives.Isopropylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.), n-butylmalonic acid (Wako Chemical Co., Ltd.), n-hexadecylmalonic acid (Oakwood Products, Inc.), cyclopentylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.), phenylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.), and benzylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.) were used as supplied.Cyclopropylacetic acid (Wako Chemical Co., Ltd.), cyclopentylacetic acid (Tokyo Kasei Kogyo Co., Ltd.), cyclohexylacetic acid (Tokyo Kasei Kogyo Co., Ltd.), cycloheptylacetic acid (Alfa Aesar), tert-butylacetic acid (Tokyo Kasei Kogyo Co., Ltd.), and 1-naphthylacetic acid (Tokyo Kasei Kogyo Co., Ltd.) were used as supplied.


### 2.3. Preparation of TiO2 Electrodes Sensitized by D908 Dye

TiO2 nanoparticle (ca. 20 nm) pastes were prepared by the method of the previous paper [15]. TiO2 electrodes (apparent area 0.25 cm2; thickness ca 14 μm) were prepared on a glass substrate coated with F-doped SnO2 by screen printing. The electrodes were heated at 550°C for 1 hour. The D908 dye (0.5 mM) and the coadsorbent (0.5 mM) were dissolved in a 50 : 50 (vol.%) solution of acetonitrile and tert-butyl alcohol. The solvents were purchased from Kanto Chemical Co., Inc. and used as supplied without further purification. The TiO2 films were immersed in the dye solutions and kept at 25°C for 20 h.


### 2.4. Preparation of Electrolyte

The electrolyte consisted of 0.06 M iodine, 0.1 M LiI, 0.6 M 1-ethyl-3-methylimidazolium iodide, and 0.5 M 4-tert-butylpyridine in acetonitrile iodine (Wako Pure Chemical Industries, Ltd.), LiI (Kojundo Chemical Laboratory Co., Ltd.), 1-ethyl-3-methylimidazolium iodide (Kanto Chemical Co., Inc.), 4-tert-butylpyridine (Sigma-Aldrich), and acetonitrile (Kanto Chemical Co., Inc.) were used as supplied.


### 2.5. Fabrication of DSC Cells and Photovoltaic Measurement

The DSC cell consisted of the TiO2 electrode, a counter electrode, a polyimide film spacer (35 μm thick), and the electrolyte. The counter electrode was a Pt film sputtered on a TCO-coated glass plate.Photovoltaic measurement employed an AM1.5 solar simulator equipped with a xenon lamp (San-ei Electric Co., Ltd.).


### 2.6. Measurement of the Amount of Dye Adsorbed on TiO2

The areas around the TiO2 films sensitized by D908 dye were wiped with ethanol. Then, the TiO2 films were immersed in a 1.5 : 1.0 (vol.%) solution of ethanol and 0.1 M KOH for 10 minutes. After recognizing the dye desorption, 1.0 mL of the solution was used to measure its specific adsorption (maximum adsorption wavelength: 510 nm) by the spectrophotometer (Shimadzu UV-2550). The amounts of adsorbed dyes were calculated from the absorbance of 510 nm light for 1.0 mL desorbed sample solutions.


### 2.7. Measurement of Attenuated Total Reflection Fourier-Transformed IR (ATR-FTIR) Spectroscopy

The surfaces of TiO2 films sensitized by D908 dye, D908 dye with phenylmalonic acid, and D908 dye with cyclopentylacetic acid were analyzed by ATR-FTIR (Nicolet, iN10MX) with 128 scans at a resolution of 8 cm−1.


### 2.8. Measurement by Raman Spectroscopy

The surfaces of TiO2 films sensitized by D908 dye, D908 dye with phenylmalonic acid, and D908 dye with cyclopentylacetic acid were analyzed with a Raman microscope (Renishaw, inVia) with an exciting light of 532 nm wavelength, an exciting light power of 0.5% (0.35 mW), an objective mirror of 50x magnification, an irradiation time of 3 seconds, 180-degree back scatter, and 5 times of scanning. The wave number was calibrated by silicone.


### 2.9. Measurement by Electrochemical Impedance Spectroscopy (EIS)

The large DSC cells using the TiO2 electrodes (apparent area 5.1 cm2, thickness ca 14 μm) sensitized by D908 dye, D908 dye with phenylmalonic acid, and D908 dye with cyclopentylacetic acid were fabricated and measured with an electrochemical impedance spectroscope (EIS) (Biologic, SP-300) under irradiation of 100 mW/cm2at 25°C.


## 2.1. D908 Dye

The molecular structure of D908 dye is shown in Figure1.D908 dye is one of the derivatives of Z907 dye. One of the protons bonded to the carboxylic groups is substituted by benzyltrimethylammonium cation.D908 dye was purchased from Everlight Chemical Industrial Co., and used as supplied without further purification.


## 2.2. Malonic Acid Derivatives and Acetic Acid Derivatives

We chose six malonic acid derivatives including alkyl, cycloalkyl, and phenyl groups shown in Figure2 and six acetic acid derivatives including alkyl, cycloalkyl, and naphthyl groups shown in Figure 3.Figure 2
Structures of malonic acid derivatives.Figure 3
Structures of acetic acid derivatives.Isopropylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.), n-butylmalonic acid (Wako Chemical Co., Ltd.), n-hexadecylmalonic acid (Oakwood Products, Inc.), cyclopentylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.), phenylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.), and benzylmalonic acid (Tokyo Kasei Kogyo Co., Ltd.) were used as supplied.Cyclopropylacetic acid (Wako Chemical Co., Ltd.), cyclopentylacetic acid (Tokyo Kasei Kogyo Co., Ltd.), cyclohexylacetic acid (Tokyo Kasei Kogyo Co., Ltd.), cycloheptylacetic acid (Alfa Aesar), tert-butylacetic acid (Tokyo Kasei Kogyo Co., Ltd.), and 1-naphthylacetic acid (Tokyo Kasei Kogyo Co., Ltd.) were used as supplied.


## 2.3. Preparation of TiO2 Electrodes Sensitized by D908 Dye

TiO2 nanoparticle (ca. 20 nm) pastes were prepared by the method of the previous paper [15]. TiO2 electrodes (apparent area 0.25 cm2; thickness ca 14 μm) were prepared on a glass substrate coated with F-doped SnO2 by screen printing. The electrodes were heated at 550°C for 1 hour. The D908 dye (0.5 mM) and the coadsorbent (0.5 mM) were dissolved in a 50 : 50 (vol.%) solution of acetonitrile and tert-butyl alcohol. The solvents were purchased from Kanto Chemical Co., Inc. and used as supplied without further purification. The TiO2 films were immersed in the dye solutions and kept at 25°C for 20 h.


## 2.4. Preparation of Electrolyte

The electrolyte consisted of 0.06 M iodine, 0.1 M LiI, 0.6 M 1-ethyl-3-methylimidazolium iodide, and 0.5 M 4-tert-butylpyridine in acetonitrile iodine (Wako Pure Chemical Industries, Ltd.), LiI (Kojundo Chemical Laboratory Co., Ltd.), 1-ethyl-3-methylimidazolium iodide (Kanto Chemical Co., Inc.), 4-tert-butylpyridine (Sigma-Aldrich), and acetonitrile (Kanto Chemical Co., Inc.) were used as supplied.


## 2.5. Fabrication of DSC Cells and Photovoltaic Measurement

The DSC cell consisted of the TiO2 electrode, a counter electrode, a polyimide film spacer (35 μm thick), and the electrolyte. The counter electrode was a Pt film sputtered on a TCO-coated glass plate.Photovoltaic measurement employed an AM1.5 solar simulator equipped with a xenon lamp (San-ei Electric Co., Ltd.).


## 2.6. Measurement of the Amount of Dye Adsorbed on TiO2

The areas around the TiO2 films sensitized by D908 dye were wiped with ethanol. Then, the TiO2 films were immersed in a 1.5 : 1.0 (vol.%) solution of ethanol and 0.1 M KOH for 10 minutes. After recognizing the dye desorption, 1.0 mL of the solution was used to measure its specific adsorption (maximum adsorption wavelength: 510 nm) by the spectrophotometer (Shimadzu UV-2550). The amounts of adsorbed dyes were calculated from the absorbance of 510 nm light for 1.0 mL desorbed sample solutions.


## 2.7. Measurement of Attenuated Total Reflection Fourier-Transformed IR (ATR-FTIR) Spectroscopy

The surfaces of TiO2 films sensitized by D908 dye, D908 dye with phenylmalonic acid, and D908 dye with cyclopentylacetic acid were analyzed by ATR-FTIR (Nicolet, iN10MX) with 128 scans at a resolution of 8 cm−1.


## 2.8. Measurement by Raman Spectroscopy

The surfaces of TiO2 films sensitized by D908 dye, D908 dye with phenylmalonic acid, and D908 dye with cyclopentylacetic acid were analyzed with a Raman microscope (Renishaw, inVia) with an exciting light of 532 nm wavelength, an exciting light power of 0.5% (0.35 mW), an objective mirror of 50x magnification, an irradiation time of 3 seconds, 180-degree back scatter, and 5 times of scanning. The wave number was calibrated by silicone.


## 2.9. Measurement by Electrochemical Impedance Spectroscopy (EIS)

The large DSC cells using the TiO2 electrodes (apparent area 5.1 cm2, thickness ca 14 μm) sensitized by D908 dye, D908 dye with phenylmalonic acid, and D908 dye with cyclopentylacetic acid were fabricated and measured with an electrochemical impedance spectroscope (EIS) (Biologic, SP-300) under irradiation of 100 mW/cm2at 25°C.


## 3. Results and Discussion

### 3.1. Photovoltaic Performance

Table1 shows the amount of D908 dyes adsorption and the photovoltaic parameters of DSC devices without coadsorbent (control) and with isopropylmalonic acid (IPMA), n-butylmalonic acid (BMA), n-hexadecylmalonic acid (HDMA), cyclopentylmalonic acid (CPMA), phenylmalonic acid (PMA), and benzylmalonic acid (BZMA).Table 1
Photovoltaic parameters of DSC devices with malonic acid derivatives.
Coadsorbent
The amount of dye adsorption
J
sc
V
oc
FF
η
10−8 mol/cm2
(mA/cm2)
(V)
(%)
Control
19.4
16.4
0.64
0.66
6.9
Isopropylmalonic acid
13.9
16.3
0.64
0.69
7.2
n-Butylmalonic acid
14.1
15.8
0.64
0.69
7.0
n-Hexadecylmalonic acid
11.9
14.8
0.64
0.70
6.6
Cyclopentylmalonic acid
14.8
16.7
0.64
0.68
7.3
Phenylmalonic acid
18.1
17.4
0.66
0.68
7.8
Benzylmalonic acid
12.6
16.4
0.63
0.68
7.0As shown in Table1, all the adsorbed amounts of the D908 dyes decreased when the six types of malonic acid derivatives were used as coadsorbents. These results indicate that malonic acid derivatives were adsorbed on the TiO2 and suppressed D908 dye adsorption.For the DSC device with HDMA, the amounts of the adsorbed D908 dyes dramatically decreased to 11.9 × 10−8 mol/cm2 relative to the control device (19.4 × 10−8 mol/cm2). This result suggests that HDMA significantly suppressed D908 dye adsorption by its bulky steric effects. As a result of decreased dye adsorption, the value of Jsc decreased from 16.4 to 14.8 mA/cm2, and the value of conversion efficiency also decreased from 6.9% to 6.6%.The other five DSC devices improved their conversion efficiencies. In particular, the DSC device with PMA showed the highest value of conversion efficiency (7.8%) among all the seven DSC devices. The amount of the adsorbed D908 dye decreased to 18.1 × 10−8 mol/cm2 relative to the control device (19.4 × 10−8 mol/cm2), but the device showed a 6% improvement in the value of Jsc (17.4 mA/cm2) relative to that of the control device (16.4 mA/cm2). This result suggests that the coadsorption of PMA on the TiO2 suppressed the aggregation of the dyes and the self-quenching of the excited electrons in the dyes by its steric effect. The effect is described in Section 3.2 ATR-FTIR spectroscopy and Section 3.4 electrochemical impedance spectroscopy. Therefore, the coadsorption of PMA increased in electron-injection yields from the dye to the TiO2.The device also showed a 3% improvement inVoc(0.66 V) relative to the control device (0.64 V). This result suggests that the coadsorption of PMA on the TiO2 suppressed the recombination between the injected electrons and I3- ions. The effect is also described in Section 3.4 electrochemical impedance spectroscopy.Table2 shows the amounts of the adsorbed D908 dyes and the photovoltaic parameters of DSC devices with cyclopropylacetic acid (CPRAA), cyclopentylacetic acid (CPEAA), cyclohexylacetic acid (CHEAA), cycloheptylacetic acid (CHPAA), tert-butylacetic acid (TBAA) and naphthylacetic acid (NPAA). As shown in Table 2, all the amounts of the adsorbed D908 dyes decreased when the six types of acetic acid derivatives were used as coadsorbents. These results suggest that acetic acid derivatives were adsorbed on the TiO2 and suppressed D908 dye adsorption. Three DSC devices with CPEAA, CHEAA, or TBAA improved their conversion efficiencies. In particular, the device with CPEAA showed the highest value of conversion efficiency (7.6%) among seven devices. The amount of adsorbed D908 dye decreased to 17.2 × 10−8 mol/cm2 relative to the control device (19.4 × 10−8 mol/cm2), but the device showed a 4% improvement in Jsc (17.0 mA/cm2) relative to the control device (16.4 mA/cm2). The device also showed a 3% improvement in Voc (0.66 V) relative to the control device (0.64 V). These results suggest that the coadsorption of CPEAA on the TiO2 has an effect similar to that of PMA. The effect is also described in Section 3.2 ATR-FTIR spectroscopy and Section 3.4 Electrochemical impedance spectroscopy.Table 2
Photovoltaic parameters of DSC devices with acetic acid derivatives.
Coadsorbent
The amount of dye adsorption
J
sc
V
oc
FF
η
10−8 mol/cm2
(mA/cm2)
(V)
(%)
Control
19.4
16.4
0.64
0.66
6.9
Cyclopropylacetic acid
17.1
16.6
0.62
0.67
6.9
Cyclopentylacetic acid
17.2
17.0
0.66
0.68
7.6
Cyclohexylacetic acid
18.2
17.0
0.64
0.67
7.3
Cycloheptylacetic acid
17.3
16.5
0.62
0.67
6.9
tert-Butylacetic acid
18.7
16.6
0.63
0.68
7.1
1-Naphthylacetic acid
18.0
16.3
0.61
0.68
6.8


### 3.2. ATR-FTIR Spectroscopy

Figure4 shows the attenuated total reflection Fourier-transformed IR (ATR-FTIR) spectra of TiO2 films sensitized by D908 alone, D908 with PMA, and D908 with CPEAA in the range of 1200–1800 cm−1. The assignments of the peaks were prepared by the previous papers [10, 16].Figure 4
ATR-FTIR spectra of TiO2 films sensitized with D908 alone, D908 with PMA, and D908 with CPEAA.The peak at 1381 cm−1 was assigned to the carboxylate groups (–COO−) anchored to the surface of the TiO2, and the peak at 1720 cm−1 was assigned to the free carboxylic acid (–COOH) of the D908 dye. The intensity at 1381 cm−1 relative to that at 1720 cm−1 (I1381/I1720) was calculated, and the values were 11.2 (D908 alone, control), 21.3 (D908 with PMA), and 17.2 (D908 with CPEAA), respectively.Therefore, the amounts of D908 dyes anchored to the surface of TiO2 were in the following order: D908 with PMA > D908 with CPEAA > control. This result provides an explanation for improved Jsc value for the DSC device with PMA or CPEAA, even though the amounts of dye were less.


### 3.3. Raman Spectroscopy

Figure5 shows the Raman spectra of TiO2 films sensitized by D908 alone, D908 with PMA, and D908 with CPEAA in the range of 400–1800 cm−1. The assignments of the peaks were prepared by the previous paper [17].Figure 5
Raman spectra of the TiO2 films sensitized with D908 alone, D908 with PMA, and D908 with CPEAA.The peak at 640 cm−1 was assigned to the TiO2, and the peak at 1610 cm−1 was assigned to the D908 dye. The intensity at 1610 cm−1 relative to that at 640 cm−1 (I1610/I640) was calculated, and the values were 4.26 (D908 alone, control), 3.26 (D908 with PMA), and 2.03 (D908 with CPEAA), respectively.Therefore, the amounts of D908 dye adsorbed on the surface of TiO2 were in the following order: control > D908 with PMA > D908 with CPEAA. This result coincides with the order of the amounts of D908 dyes measured by the spectrophotometer as referred to in Section 2.7, and suggests that Raman spectra can be used for the evaluation of the amount of dye more conveniently.


### 3.4. Electrochemical Impedance Spectroscopy (EIS)

Electrochemical impedance spectroscopy (EIS) was performed to investigate the interface in the DSC devices by the method of the previous papers [18, 19].Figure6 shows the Nyquist plots of DSC devices using the TiO2 films sensitized by D908 alone, D908 with PMA, and D908 with CPEAA. The plots were fitted by the equivalent circuit of DSC shown in Figure 7, and Rs, R1, R2, and R3 values were calculated.Figure 6
Nyquist plots for the DSC devices using TiO2 films sensitized with D908 alone, D908 with PMA, and D908 with CPEAA.Figure 7
Equivalent circuit of DSC.Rs means the series resistance such as that of F-doped SnO2 and interconnection.R1 (Pt) means the resistance of charge transfer between Pt and electrolyte. R2 (TiO2) means the charge recombination resistance from TiO2 to I3- ions. R3 (I) means the diffusion resistance in electrolyte. These parameters are shown in Table 3.Table 3
Impedance parameters of DSC devices with PMA or CPEAA.
Coadsorbent
Rs
R1 (Pt)
R2 (TiO2)
R3 (I)
Control
5.5
1.2
3.8
3.6
Phenylmalonic acid
5.5
1.2
4.0
3.4
Cyclopentylacetic acid
5.5
1.2
4.0
3.4The values of R2 in the DSC devices with PMA or CPEAA were larger than that of the control device. This result suggests that the coadsorption of PMA or CPEAA on the TiO2 suppressed the recombination between the injected electrons and I3- ions; therefore, PMA or CPEAA coadsorption improved the Voc of the DSC devices.The values of R3 in the DSC devices with PMA or CPEAA were smaller than that of the control device. This result suggests that the coadsorption of PMA or CPEAA on the TiO2 suppressed the aggregation of the dyes and I- ions were able to access the dyes more smoothly; thus PMA or CPEAA coadsorption improved the Jsc of the DSC devices.


## 3.1. Photovoltaic Performance

Table1 shows the amount of D908 dyes adsorption and the photovoltaic parameters of DSC devices without coadsorbent (control) and with isopropylmalonic acid (IPMA), n-butylmalonic acid (BMA), n-hexadecylmalonic acid (HDMA), cyclopentylmalonic acid (CPMA), phenylmalonic acid (PMA), and benzylmalonic acid (BZMA).Table 1
Photovoltaic parameters of DSC devices with malonic acid derivatives.
Coadsorbent
The amount of dye adsorption
J
sc
V
oc
FF
η
10−8 mol/cm2
(mA/cm2)
(V)
(%)
Control
19.4
16.4
0.64
0.66
6.9
Isopropylmalonic acid
13.9
16.3
0.64
0.69
7.2
n-Butylmalonic acid
14.1
15.8
0.64
0.69
7.0
n-Hexadecylmalonic acid
11.9
14.8
0.64
0.70
6.6
Cyclopentylmalonic acid
14.8
16.7
0.64
0.68
7.3
Phenylmalonic acid
18.1
17.4
0.66
0.68
7.8
Benzylmalonic acid
12.6
16.4
0.63
0.68
7.0As shown in Table1, all the adsorbed amounts of the D908 dyes decreased when the six types of malonic acid derivatives were used as coadsorbents. These results indicate that malonic acid derivatives were adsorbed on the TiO2 and suppressed D908 dye adsorption.For the DSC device with HDMA, the amounts of the adsorbed D908 dyes dramatically decreased to 11.9 × 10−8 mol/cm2 relative to the control device (19.4 × 10−8 mol/cm2). This result suggests that HDMA significantly suppressed D908 dye adsorption by its bulky steric effects. As a result of decreased dye adsorption, the value of Jsc decreased from 16.4 to 14.8 mA/cm2, and the value of conversion efficiency also decreased from 6.9% to 6.6%.The other five DSC devices improved their conversion efficiencies. In particular, the DSC device with PMA showed the highest value of conversion efficiency (7.8%) among all the seven DSC devices. The amount of the adsorbed D908 dye decreased to 18.1 × 10−8 mol/cm2 relative to the control device (19.4 × 10−8 mol/cm2), but the device showed a 6% improvement in the value of Jsc (17.4 mA/cm2) relative to that of the control device (16.4 mA/cm2). This result suggests that the coadsorption of PMA on the TiO2 suppressed the aggregation of the dyes and the self-quenching of the excited electrons in the dyes by its steric effect. The effect is described in Section 3.2 ATR-FTIR spectroscopy and Section 3.4 electrochemical impedance spectroscopy. Therefore, the coadsorption of PMA increased in electron-injection yields from the dye to the TiO2.The device also showed a 3% improvement inVoc(0.66 V) relative to the control device (0.64 V). This result suggests that the coadsorption of PMA on the TiO2 suppressed the recombination between the injected electrons and I3- ions. The effect is also described in Section 3.4 electrochemical impedance spectroscopy.Table2 shows the amounts of the adsorbed D908 dyes and the photovoltaic parameters of DSC devices with cyclopropylacetic acid (CPRAA), cyclopentylacetic acid (CPEAA), cyclohexylacetic acid (CHEAA), cycloheptylacetic acid (CHPAA), tert-butylacetic acid (TBAA) and naphthylacetic acid (NPAA). As shown in Table 2, all the amounts of the adsorbed D908 dyes decreased when the six types of acetic acid derivatives were used as coadsorbents. These results suggest that acetic acid derivatives were adsorbed on the TiO2 and suppressed D908 dye adsorption. Three DSC devices with CPEAA, CHEAA, or TBAA improved their conversion efficiencies. In particular, the device with CPEAA showed the highest value of conversion efficiency (7.6%) among seven devices. The amount of adsorbed D908 dye decreased to 17.2 × 10−8 mol/cm2 relative to the control device (19.4 × 10−8 mol/cm2), but the device showed a 4% improvement in Jsc (17.0 mA/cm2) relative to the control device (16.4 mA/cm2). The device also showed a 3% improvement in Voc (0.66 V) relative to the control device (0.64 V). These results suggest that the coadsorption of CPEAA on the TiO2 has an effect similar to that of PMA. The effect is also described in Section 3.2 ATR-FTIR spectroscopy and Section 3.4 Electrochemical impedance spectroscopy.Table 2
Photovoltaic parameters of DSC devices with acetic acid derivatives.
Coadsorbent
The amount of dye adsorption
J
sc
V
oc
FF
η
10−8 mol/cm2
(mA/cm2)
(V)
(%)
Control
19.4
16.4
0.64
0.66
6.9
Cyclopropylacetic acid
17.1
16.6
0.62
0.67
6.9
Cyclopentylacetic acid
17.2
17.0
0.66
0.68
7.6
Cyclohexylacetic acid
18.2
17.0
0.64
0.67
7.3
Cycloheptylacetic acid
17.3
16.5
0.62
0.67
6.9
tert-Butylacetic acid
18.7
16.6
0.63
0.68
7.1
1-Naphthylacetic acid
18.0
16.3
0.61
0.68
6.8


## 3.2. ATR-FTIR Spectroscopy

Figure4 shows the attenuated total reflection Fourier-transformed IR (ATR-FTIR) spectra of TiO2 films sensitized by D908 alone, D908 with PMA, and D908 with CPEAA in the range of 1200–1800 cm−1. The assignments of the peaks were prepared by the previous papers [10, 16].Figure 4
ATR-FTIR spectra of TiO2 films sensitized with D908 alone, D908 with PMA, and D908 with CPEAA.The peak at 1381 cm−1 was assigned to the carboxylate groups (–COO−) anchored to the surface of the TiO2, and the peak at 1720 cm−1 was assigned to the free carboxylic acid (–COOH) of the D908 dye. The intensity at 1381 cm−1 relative to that at 1720 cm−1 (I1381/I1720) was calculated, and the values were 11.2 (D908 alone, control), 21.3 (D908 with PMA), and 17.2 (D908 with CPEAA), respectively.Therefore, the amounts of D908 dyes anchored to the surface of TiO2 were in the following order: D908 with PMA > D908 with CPEAA > control. This result provides an explanation for improved Jsc value for the DSC device with PMA or CPEAA, even though the amounts of dye were less.


## 3.3. Raman Spectroscopy

Figure5 shows the Raman spectra of TiO2 films sensitized by D908 alone, D908 with PMA, and D908 with CPEAA in the range of 400–1800 cm−1. The assignments of the peaks were prepared by the previous paper [17].Figure 5
Raman spectra of the TiO2 films sensitized with D908 alone, D908 with PMA, and D908 with CPEAA.The peak at 640 cm−1 was assigned to the TiO2, and the peak at 1610 cm−1 was assigned to the D908 dye. The intensity at 1610 cm−1 relative to that at 640 cm−1 (I1610/I640) was calculated, and the values were 4.26 (D908 alone, control), 3.26 (D908 with PMA), and 2.03 (D908 with CPEAA), respectively.Therefore, the amounts of D908 dye adsorbed on the surface of TiO2 were in the following order: control > D908 with PMA > D908 with CPEAA. This result coincides with the order of the amounts of D908 dyes measured by the spectrophotometer as referred to in Section 2.7, and suggests that Raman spectra can be used for the evaluation of the amount of dye more conveniently.


## 3.4. Electrochemical Impedance Spectroscopy (EIS)

Electrochemical impedance spectroscopy (EIS) was performed to investigate the interface in the DSC devices by the method of the previous papers [18, 19].Figure6 shows the Nyquist plots of DSC devices using the TiO2 films sensitized by D908 alone, D908 with PMA, and D908 with CPEAA. The plots were fitted by the equivalent circuit of DSC shown in Figure 7, and Rs, R1, R2, and R3 values were calculated.Figure 6
Nyquist plots for the DSC devices using TiO2 films sensitized with D908 alone, D908 with PMA, and D908 with CPEAA.Figure 7
Equivalent circuit of DSC.Rs means the series resistance such as that of F-doped SnO2 and interconnection.R1 (Pt) means the resistance of charge transfer between Pt and electrolyte. R2 (TiO2) means the charge recombination resistance from TiO2 to I3- ions. R3 (I) means the diffusion resistance in electrolyte. These parameters are shown in Table 3.Table 3
Impedance parameters of DSC devices with PMA or CPEAA.
Coadsorbent
Rs
R1 (Pt)
R2 (TiO2)
R3 (I)
Control
5.5
1.2
3.8
3.6
Phenylmalonic acid
5.5
1.2
4.0
3.4
Cyclopentylacetic acid
5.5
1.2
4.0
3.4The values of R2 in the DSC devices with PMA or CPEAA were larger than that of the control device. This result suggests that the coadsorption of PMA or CPEAA on the TiO2 suppressed the recombination between the injected electrons and I3- ions; therefore, PMA or CPEAA coadsorption improved the Voc of the DSC devices.The values of R3 in the DSC devices with PMA or CPEAA were smaller than that of the control device. This result suggests that the coadsorption of PMA or CPEAA on the TiO2 suppressed the aggregation of the dyes and I- ions were able to access the dyes more smoothly; thus PMA or CPEAA coadsorption improved the Jsc of the DSC devices.


## 4. Conclusions

Coadsorption of PMA or CPEAA improved both theJsc and the Voc values for DSC devices sensitized by D908 dye even though coadsorption decreased the amount of dye adsorbed on the TiO2 electrode. The conversion efficiency increased from 6.9% to 7.8% for PMA and from 6.9% to 7.6% for CPEAA.ATR-FTIR spectra suggested that coadsorption of PMA or CPEAA increased the amount of D908 dye anchored to the surface of TiO2. This result provides an explanation for the improved Jsc values.Raman spectra suggested that coadsorption of PMA or CPEAA decreased the amount of D908 dye adsorbed on the surface of TiO2. This result coincides with the amount of D908 dye measured by the spectrophotometer and suggests that Raman spectra can be used for the evaluation of the amount of dye more conveniently.Electrochemical impedance spectroscopy suggested that the values of R2 in the DSC devices with PMA or CPEAA were larger than that of the control device. This result suggests that the coadsorption of PMA or CPEAA on the TiO2 suppressed the recombination between the injected electrons and I3- ions, PMA or CPEAA coadsorption improving the Voc of the DSC devices. The values of R3 in the DSC devices with PMA or CPEAA were smaller than that of the control device. This result suggests that the coadsorption of PMA or CPEAA on the TiO2 suppressed the aggregation of the dyes and I- ions were able to access the dyes more smoothly. Consequently, PMA or CPEAA coadsorption improved the Jsc of the DSC devices.



---