# Dielectric Behavior of Ceramic (BST)/Epoxy Thick Films

Authors: N. Hadik; A. Outzourhit; A. Elmansouri; A. Abouelaoualim; A. Oueriagli; E. L. Ameziane
Journal: Active and Passive Electronic Components
 (2009)

---

## Abstract

Composite  materials were made by mixing powders ofBa1−xSrxTiO3 (x=0.2 and 0.4) ceramics and epoxy resin with various volume fractions (vol%). Dielectric measurements of these composites were performed as a function of filler ratio in the range 100–360°K at 10 KHz. The dielectric constant of the composite  increased with increasing volume fraction  varies slightly with temperature. The 20 vol% of BST(0.4)-epoxy composite had the highest dielectric constant of 19.4 and dielectric loss tangent of 0.027. Among the dielectric mixing models presented, the model of Lichtenecker shows the best fit to the experimental data for both composites.


---

## Body

## 1. Introduction

Recently, there has been a great interest in a new generation of composite materials exhibiting high dielectric performance with lower cost, size, weight, and easy processability [1–3]. Low dielectric losses and moderate dielectric constants are required for use in microelectronic packaging and principally for decoupling multichip modules (MCMs)  [4, 5].Different elements have been mixed to polymers like carbon, iron, nickel, or conducting polymer [6–9] to tune their electrical properties. On the other hand, ferroelectric ceramic-polymer composite materials are principally used for high density energy storage and for capacitor applications [10–13]. Their properties can be easily adjusted by changing the volume fraction of the ferroelectric material while the matrix integrity was maintained during manufacturing. The grain size of the ceramic powders, the uniformity, the thickness, the interfacial effects, and the porosity of the composites influence the physical properties and the quality of the ferroelectric ceramic/polymer composites [10–13].Previous studies on ceramics-epoxy composites revealed  dielectric constants in the range of 24 and 44 for BaTiO3 and PMN thick films for 40 vol% [14]. A lower value of 23 was noted for Nb2O5 doped TiO2 ceramics-epoxy films prepared by screen printing [15]. Other authors obtained dielectric constants as high as 75 in the case of CaCu3Ti4O12 (CCTO) ceramic-epoxy mixtures for a concentration reaching 64% [16].Different laws have been proposed to fit the experimental dielectric constants for two component mixtures, and to predict the effect of each phase on the dielectric properties [17].  Models such as  the series, parallel, Hashing-Shtrikman, and Lichtenecker models were developed under various assumptions concerning arrangement of inclusions and their shape [18].In this work, ceramic-epoxy composites were fabricated usingBa1-xSrxTiO3 (x=0.2 and 0.4) powders mixed with Bisphenol A epoxy. The dielectric proprieties of composites with ceramic loadings of 5, 10, 15, and 20 vol% were studied as a function  of  temperature.


## 2. Materials and Methods

The powders of BST ceramics were prepared from high purity barium carbonate (BaCO3) (Fluka 98.5%), strontium carbonate (SrTiO3) (Riedel-de Haen 96%), and titanium dioxide (TiO2) (Arcos 98%) precursors. The starting powders corresponding to  Ba0.8Sr0.2TiO3 (BST(0.2)) and  Ba0.6Sr0.4TiO3  (BST(0.4)) were calcined at 1200°C in air for 1 hour and a half. The obtained powders were ground in an agate Mortar and pestle and then mixed with a solution of epoxy (Bispfenol-A-Diglycidylether) and its hardener (Triethylenetetramine) at different volume fractions of 0, 5, 10, 15, and 20 vol%, which were calculated using the weight and density of calcined BST and epoxy. The density of BST(0.2) and BST(0.4) powders is 5.797 and 5.703, respectively, as determined from the measured lattice parameters, while that of the epoxy and its hardener is 1.151 and 1.025, respectively, as given by the manufacturer (Struers). The mixture was blended for 20 minutes and thick film samples, with a thickness of about 100 μm, were cast on ITO/glass substrate by the knife-edge method. Films with volume fractions exceeding 20% were not made as homogeneous mixtures were difficult to make and the obtained thick films have a poor quality.For dielectric measurements, an aluminium electrode was deposed on the samples by vacuum thermal evaporation. The dielectric measurements were performed from 100 to 360°K using a Keithley LCZ 3330 meter in the frequency range of 40 Hz to 100 kHz.The Microstructures of samples were examined by scanning electron microscopy (SEM) using JEOL JSM 5500 SEM equipped an EDAX Falcon EDS analyser. On the other hand, X-ray diffraction analysis was performed using the  Philips X’pert diffractometer.


## 3. Results and Discussion

Figure1 shows the X-ray diffraction patterns of BST (x=0.2 and x=0.4) powders at room temperature. The results reveal that the ceramics have a single perovskite-type phase after calcination at 1200°C. No peaks corresponding to secondary phases or unreacted precursors were observed. The lattice parameters of the two compositions are, respectively, 0.3974 nm and 0.3960 nm. The SEM micrographs  of BST (x=0.2 and x=0.4) ceramics powders, shown in Figures 2(a) and 2(b),  reveal a distribution of  grain size being in the range of 0.5–2 μm, with an average size of 1 μm.Figure 1
X-ray diffraction pattern of BST(0.2) and BST(0.4) ceramics powders.Micrographs of BST ceramic powders ((a) and (b)) and composites ((c) and (d)): (a)x=0.2, (b) x=0.4, (c) BST(x=0.2)-epoxy 10 vol%, and  (d) BST(x=0.4)-epoxy 15  vol%.
(a)(b)(c)(d)Figures2(c) and 2(d) depict the microstructure of the BST-epoxy composite thick films with 10% and 15% volume fractions, respectively. A uniform dispersion of ceramic fillers in the epoxy matrix is obtained as revealed by the SEM micrographs. In addition, no pores were observed in these thick films.


## 4. Dielectric Measurements

The dielectric properties of sintered ceramics at 1400°C for 75 minutes  measured at 10 KHz are shown in Figure3. The Curie temperature which corresponds to the ferroelectric to paraelectric transition is 353 and 280 K, respectively, for BST(0.2) and BST(0.4), respectively. The loss tangent did not exceed 0.065 and 0.024 and the maximum dielectric constants at 10 KHz are 1665, 1880, respectively, for the two compositions.Figure 3
Temperature dependence of the dielectric constant of the sintered BST(0.2) and BST(0.4) ceramics.Figure4 shows the dielectric constant of pure epoxy, BST(0.2)-epoxy and BST(0.4)-epoxy composites thick films, with ceramics loadings of 5, 10, 15, and 20 vol% as a function of temperature. The dielectric constant of pure epoxy remained practically constant, and it slightly increases from its value of 6.3 at 300 K above 320 K. For both compositions, as the figure shows, the dielectric constant of the ferroelectric-epoxy thick films increases with increasing ceramics loading. All the samples exhibited a similar behaviour with temperature. At 300 K the dielectric constant values for 5, 10, 15, and 20 vol% loading were 8.3, 11.3, 13.3, 17.7, and 8.8, 12.1, 15, 19.3, respectively, for composites with BST(0.2) and BST(0.4) ceramics, at 10 KHz. Theses values remain lower than those of pure BST(0.2) and BST(0.4) ceramics (Figure 2).Dielectric constant for BST-epoxy composites as function of temperature for different volume fraction at 10 KHz.
(a)(b)For all the ceramic-epoxy composite samples, the dielectric constant increases slightly when the temperature rises. This increase becomes more significant when the temperature rises above 320°K. The low dielectric constant value of both composites is due the low contents of the high-dielectric constant ceramic dispersed in the epoxy.  In this case, the dielectric response mainly results from the continuous low dielectric constant epoxy matrix.There are three competing mechanisms in the dielectric response of the ceramic-epoxy composites [19].(1)
The segmental mobility of polymer which increases with increasing temperature; this mechanism should increase the dielectric constant.(2)
The disruption of contacts between filler particles caused by the thermal expansion of resin and ceramic; this mechanism should decrease dielectric constant.(3)
The change in the dielectric response of the filler particles with temperature.The dielectric constant of two composites  ceramic polymer with the 20 vol% ceramics filler exhibits the highest increase as a function of temperature. In addition, the composite containing BST(0.4) has a higher dielectric constant than that based on BST(0.2). The former composite is therefore suitable for applications requiring moderately high dielectric constant.Dielectric losses are low and vary between 0.026 and 0.033 for all the samples (Figure5). For BST(0.4)-epoxy composites, the losses first increase when the volume fraction increases and then decrease with a maximum of 0.033 for 10 vol%. A similar trend is exhibited by the composites based on BST(0.2)-epoxy for   loading  less than 10 vol%. This behaviour is due to the fact that the dielectric properties of these composites are dominated by the main continuous phase of the polymer matrix at these loading rations [20]. According to the simple mixing rules, the dielectric losses are expected to increase monotonically with increasing filler ratio. In our case a maximum at 10% for BST(x=0.4)-epoxy and fluctuations in the case of the BST(0.2)-epoxy were observed. This behaviour was also reported in other BST-polymer composites and was attributed to BST-epoxy interfacial phenomena that strongly influence the dielectric properties [21] of the composites. Further and detailed investigations of this peculiar behaviour are underway.Figure 5
Loss tangent of BST-epoxy composites at 10 KHz as function of volume fraction.As shown in Figure6, the dielectric constant of the composites decreases with increasing frequency. This behaviour can be attributed to a decrease in the dipolar polarisation in the matrix.  Ramajo et al. [19] reported that this behaviour is more important at elevated temperature and low frequency for epoxy-barium titanate composite materials. In addition, owing to the heterogeneity of the composites, the contribution of the interfacial or Maxwell-Wagner-Sillars (MWS) polarisation [22] can also be responsible for this behaviour. In parallel, the displacement or orientation of bound charge carriers responsible of other types of polarisations (atomic, electronic, dipolar) [23] may also play a role in this dispersion.Figure 6
Dielectric constant of BST-epoxy sample with 20 vol% loading as a function of frequency.Different mixture laws were proposed to fit the experimental results such as the Series, Parallel, Hashing-Shtrikman’s, Looyenga, and  Lichtenecker models.Figure7 shows that the Lichtenecker model fits better the experimental results of both composites. In the case of BST(0.4) epoxy composite we notice a small deviation from the Lichtenecker model. This is probably due to the fact that this model assumes that the composite is a random mixture of spherical inclusions in the matrix [17]. The dielectric constant used in this formula is 6.3 for pure epoxy and 1246 and 1676 for sintered ceramics BST(0.2) and BST(0.4),  respectively.Theoretical mixture models and experimental result for BST-epoxy as function of volume fraction at  10 KHz.
(a)(b)


## 5. Conclusion

Composites BST-epoxy thick films were prepared by the knife-edge method from mixed ceramics powders and epoxy resin.The dielectric constant of the composite thick films increased with increasing ceramic loading and slightly with temperature. The composite thick film with 20 vol% of BST(0.4) ceramic presented the highest dielectric constant. At these loading ratios the dielectric properties of these composites originate mainly from the contribution of the polymer matrix.The dielectric losses for both composite did not exceed 0.033. On the other hand, the dielectric constant decreases with increasing frequency. This dispersion may be caused by the Maxwell-Wagner-Sillars (MWS) polarisation, or by a displacement or orientation of bound charge carriers. Among dielectric mixing models, the Lichtenecker model accounts better for the experimental results for the both composites.



---

*Source: 437130-2009-11-12.xml*