# Structural Alteration, Hydration Stability, Heavy Metal Removal Efficiency, and Montmorillonite Porosity Fate by Coupling the Soil Solution pH and a Thermal Gradient

Authors: Chadha Mejri; Walid Oueslati; Abdesslem Ben Haj Amara
Journal: Adsorption Science & Technology
 (2022)

---

## Abstract

Clay minerals are considered as a promising material in the context of geological barrier for the confinement of radioactive and industrial waste. Understanding the usefulness of the smectite mineral, in this approach, remains insufficient. The deep investigation about structural response/changes, hydrate stability, cation exchange process, permeability, and heavy metal/radionuclide adsorption/removal efficiency under external constraints is needed. To explore the structural alteration, the hydration stability, and the evolution of montmorillonite porosity under a first order of external applied constraints coupling, a reference Na-rich montmorillonite specimen is used as a starting material, and three exchangeable heavy metal cations (Ba2+, Cu2+, and Co2+) have been selected. The applied constraint coupling is realized at laboratory scale and assured by simultaneously varying of the soil solution pH and the thermal gradient. The evaluation of the mineral fraction response is established by correlation of quantitative XRD analysis results, thermal analysis, and porosity measurements. The quantitative XRD analysis allows rebuilding of the theoretical model describing the interlamellar space (IS) configurations/damages, structural heterogeneity degrees, and hydrous stability. Obtained results show a dominant interstratified hydration character, for all studied complexes, attributed to a new IS organization versus the applied constraint strength. Furthermore, all samples exhibit a heterogeneous hydration behavior traduced by the coexistence of different layers of type population within the crystallite. Additionally, the theoretical XRD profile decomposition allowed us to prove link between the domination of the segregated stacking layers mode against the constraint strength. Thermal analysis allowed us to develop theoretical models describing the decrease of the water molecule amounts as a function of the increase in temperature and soil solution pH. Moreover, a specific hydration footprint response and an interstratification mapping are assigned for each corresponding stress degrees. The evolution of montmorillonite porosity is determined by adsorption measurement, based on Brunauer, Emmett, and Teller (BET) and Barrett-Joyner-Halenda (BJH) pore size distribution analyses which confirms for all samples, the exfoliation process, and the mesopore diameter rise by increasing the constraint intensity.


---

## Body

## 1. Introduction

Montmorillonite is a 2 : 1 phyllosilicate type belonging to the smectite family. The montmorillonite structure consists of a stack of an octahedral (O) sheet (MO4 (OH)2) where (M) can be (Al) or (Mg) ions sandwiched between two tetrahedral (T) sheets (SiO4). This structure is labeled by T-O-T, and the associated layer thickness along the c∗ axis is about 10 Å [1–4]. The montmorillonite differs from the other dioctahedral smectites (beidellite and nontronite) by the existing isomorphous substitutions which occurs in the tetrahedral sheet (i.e., Al3+ substitutes for Si4+) rather than in the octahedral sheet [5]. Indeed, the isomorphic substitutions appearing in the (T) or/and (O) sheets are defined by the localization of different type of cations in the various cavities. These substitutions result in a load deficit that is compensated on the outside of the layer, by compensating cations (CC) [5–7]. The intrinsic montmorillonite properties find a large environmental application domain as depolluant [8–11], ion exchanger [12–16], natural geological barrier for industrial and radioactive waste confinement [17], clay-based nanocomposite for drug delivery [18–27], cosmetic compounds [28–31], medicinal application [32–35], antibacterial properties, and as a topical treatment for skin problems [36–39]. The structural and morphological properties are at the origin of this efficiency and the great exploitability in several fields of application. Indeed, the layer type with its infinite lateral extension (2D), the interlamellar space (IS) allowing the individual layer swelling (then the swelling of the crystallites) with the possibility of solvent insertion (due to the capacity of cation exchange CEC), and the macroporosity associated with the high specific surface (SA) (external and internal) are essential assets favoring the exploitation of such minerals [40, 41]. The montmorillonite layer expansion amount is affected, respectively, by the intrinsic layer charge location, the type/size/charge of exchangeable cation, the abundance/organization of water molecule in the IS, the type/size of organic/inorganic fraction present in the contact solution, the material history (fatigue/stress/strain), and the surrounding environmental/geochemical/mechanical conditions [42–46]. The CC and water molecules are positioned inside the IS, during cation exchange process, following a discreet arrangement allowing a progressive swelling process (hydration process) confirmed by the discretization of the basal spacing distance (d001) fluctuations. The literature proposed basal spacing level defined by [5, 6, 47–49] is as follows: dehydrated 0 W (d001~10 Å), one water layer 1 W (d001~12.4 Å), two water layers 2 W (d001~15.4 Å), three water layers 3 W (d001~18.2 Å), and finally, four water layers 4 W (d001~21 Å).Montmorillonite is widely exploited (in adsorption science) for neutralizing the soil heavy metal dispersion/diffusion [50–52]. The adsorption factor usually depends on the solid/liquid ratio parameters in such kind of application. Usman et al. (2004) [53] demonstrate that low doses of clay (about 4% to 8%) eliminate up to 70% of heavy metals. In addition, the increase in the dose of the clay fraction is accompanied by the increase in the rate of adsorption [54, 55]. Also, the required dose and the remediation force may be affected by the variation in the mineral structural composition [56]. In the other hand, clay plays an essential role in the basic design of deep storage sites for radioactive and industrial waste confinement process [57–60]. The architecture of the sites is achieved by the association of several types of barriers (multibarrier concept). It consists of filler which is the waste in metal packages, incubated by a thick of concrete layer, covered by a clay films buried in well-determined host rock, at a depth of about 500 m below sea level. Several reasons, like the high radioactive element’s adsorption capacity and the low permeability which slows down the radionuclides migration in the host rock, detailed in the work of [61–66] are in favor of the use of clay as a geological coating.The clay adsorption capacity and the clay permeability properties are very sensitive to the variation of the soil solution pH [67–72], the surrounding temperature gradient [56, 67, 68, 72, 73], the kinetic effect during the cation exchange process [74], the surrounding atmospheric pressure variation [75, 76], the surrounding relative humidity (RH) constraint [77–81], the solid-liquid ratio effect during heavy metal removal [41], and the type and nature of the compensating cations [82–85]. Several works [67–72] show that there is a linearly proportional relationship between the pH level fluctuation and the performance of the heavy metal absorber (clay fraction). Es-Sahbany et al. (2019) [72] show that at room temperature, an optimal value of heavy metal adsorption rate was obtained; although at slightly lower or higher temperatures, this result may still be more ideal. Chantawon et al. (2003) [86] and Usman et al. (2004) [53] demonstrate good adsorption results at relatively high temperatures of around 36°C unlike some researchers [87] that observed a decrease in the adsorption rate at temperatures above 30°C. Other authors [88, 89] have proven that chemical adsorption reactions are essentially faster for temperatures that gradually increase with continuous increases in temperature.On the other hand, the experimental approach in the study of the interaction (adsorption, cationic exchange and intercalation) of montmorillonite with heavy metals (and even organic molecules) by XRD analysis has been confirmed by theoretical calculations. Zhang et al. (2018) [90] studied the uranyl ion complexation on montmorillonite edges using a combined first-principle molecular dynamics and surface complexation modeling approach. Obtained results in the case of four selected representative complexing sites show that uranyl ions form hydrolyzed bidentate complexes on these sites. Liu et al. (2021) [91] used the molecular dynamic simulations to explain the sorption behaviors of heavy metal ions (zinc, cadmium, and lead) in the interlayer and nanopore of Wyoming montmorillonite. The calculated diffusion coefficients of the selected three cations in interlayer and nanopore indicated that their diffusion abilities were significantly impaired, implying that montmorillonite adsorbents have a strong ability to fix and retard heavy metal ions. Zhang et al. (2022) [92] investigates by the molecular dynamic simulations of the exchange behavior of radionuclides into montmorillonite. Authors demonstrate that multivalent cations prefer to stay in the mid-plane of interlayer region, and Cs+ and Rb+ cations are located closer to the basal plane via inner-sphere complexation. Furthermore, the orientations of interlayer uranyl ions are nearly perpendicular to basal surface. Density functional theory (DFT) is used to validate XRD data in the case of hydrated Na-hectorite exchanged with Cs-, Ca-, and Sr-cations [93]. Also, the first-principle DFT provides a prediction of the structure, stability, and dynamic properties of organoclays based on montmorillonite (Mt) intercalated with two types of organic cations—tetrabutylammonium (TBA) and tetrabutylphosphonium (TBP) [94]. The Cs adsorption on montmorillonite clay is investigated by 133Cs chemical shift calculations, 133Cs magic-angle-spinning nuclear magnetic resonance (MAS NMR) spectroscopy, X-ray diffraction under controlled relative humidity, and DFT calculations [95]. Obtained results shows that all Cs atoms were positioned around the center of hexagonal cavities in the upper or lower tetrahedral sheets. The calculated 133Cs chemical shifts were highly sensitive to the tetrahedral Al (AlT)-Cs distance and d-spacing, rather than to the Cs coordination number.Work on the linkage of constraints has not been adequately addressed in the literature. Indeed, Meftah et al. (2010) [84] showed that for a well-determined pH value and at a precise temperature clay can permanently change its structure. Thus, Marty et al. (2020) [85] explained that the coupling between the chemistry and hydration of clays shows a specific behavior for most water molecules considering RH and interlamellar space composition. The constraint coupling affecting, respectively, the clay hydration behavior, the absorber performance, and the ion exchanger efficiency is timidly approached during the main works carried out in the last decade focusing the use of clay in the context of multibarrier [41, 79, 96]. Several works [41, 79, 96] have concentrated on the effect of individual parameter and neglecting the coupling and the interaction between existing/surrounding parameters which generally affect the functionality of the material. Very few works are based on this very realist approach [12, 71]. To take full advantage of the huge possibilities of use of these minerals, it is necessary to simulate, at the laboratory scale, what happens during the real use. This approach is realized by respecting a scientific methodology based on five steps. The first is to decipher the nature and intensity of the constraints affecting the mineral (in question), and secondly, to determine the order of the possible couplings constraints and their nature (e.g., first coupling order: coupling of two constraints (e.g., T-%RH, T-pH, T-CEC, S/L ratio-T, …) and second coupling order: coupling of three constraints T-pH-S/L ratio and mechanical stress-T-%RH, …). The third step is to create and implement these constraint coupling types on a laboratory scale. The fourth step is to characterize the material’s response. The last step is the evaluation/optimization based on the eventual results. The tremendous combination of constraints increases the challenges. For this purpose, we will focus on this work only at the first-order coupling between soil solution pH and thermal gradient designated by (T-pH).Essentially, this work focuses the structural alteration, hydration stability, and evolution of montmorillonite porosity by (T-pH) in the case of Na-rich montmorillonite exchanged with heavy metals M2+. This necessarily requires the realization/validation at the laboratory scale of an experimental first-order coupling which consists of the variations of geochemical and thermal stresses strength simultaneously. The structural evaluation is realized by a specific quantitative XRD analysis based on the modeling of the 001 reflections. Thermal analysis is used to develop the model describing interlamellar water molecule amount evolution versus constraint strength. The adsorption specificities and the porosity growth are investigated by BET and BJH pore size distribution analyses.


## 2. Materials and Methods

### 2.1. Baseline Material

A standard dioctahedral smectite SWy-2 extracted from the cretaceous formations of Wyoming (USA) and provided by the clay mineral repository is selected for the present study [1]. The structural formula per half-cell is given by [43]:
(1)Si4+3.96,Al3+0.04Al3+1.53,Fe3+0.18,Fe2+0.045,Mg2+0.26,Ti4+0.01O10OH2Ca2+0.07,K+0.01Na+0.2This bentonite exhibits a low octahedral charge and extremely limited tetrahedral Substitutions. The clay cation exchange capacity (CEC) is 101 meq/100 g [43].


### 2.2. Pretreatment

A pretreatment of the starting material consists of preparing Na-rich montmorillonite suspension (SWy-Na) is realized following a classic protocol detailed by [41] as shown in Figure 1.Figure 1
Experimental protocol for the purification of the starting material. Excess of salt was washed out by 24 h cycles:centrifugation8000rpm+removalofthesupernatant.


### 2.3. Exchangeable Cations

Three heavy metal cations (Ba2+, Cu2+, and Co2+) were the subject of the cation exchange process. The cation preference is explained by the wonderful abundance of the latter in industrial and radioactive waste and the specific characteristics of each one [97].


### 2.4. First-Order Coupling Constraints

First-order stress coupling is based on the association of geochemical (soil solution pH) and the thermal gradients (obtained by varyingT°C) at the laboratory scale. To achieve this goal, an MCl2 solution (where M is the metal cation Ba2+, Cu2+ and Co2+) at a well-determined pH is prepared at a low concentration (0.1 M), followed by the addition of Na-rich montmorillonite powder (SWy-Na). For each constraint pair created (fixed pH and fixed T), an adjustment of the overall volume (200 mL) is made by adding the metal chloride solution and the acid or base additive. Subsequently, and after several mechanical shaking cycle, a cation exchange process will take place at a well-determined temperature for a fixed specified period (24 h) (Figure 2). The soil solution pH variation and temperature values (T°C) are carried out on the same sample. All experimental parameters are summarized in Table 1.Figure 2
Experimental assembly of the 1st order coupling.Table 1
Soil solution pH and temperatures of the coupling of the 1st order of the stresses.
Coupling of the 1st orderSoil solution pHTemperature (°C)Time (h)V (mL)Acid35024560Neutral770200Basic9801190


### 2.5. Cation Exchange Process

A cation exchange process is carried out for each bivalent metal cations Ba2+, Cu2+, and Co2+ brought into contact with the starting sample. The experimental protocol established for each sample consists of applying a mechanical shake throughout 48 h, followed by centrifugation at 4000 rpm. This step is repeated five times to ensure process achievement. After recovery of the solid fraction, a series of washes with distilled water will take place to remove excess of salt from chloride ions. The obtained sample is labeled SWy-M with M that is the metal cation type (e.g., SWy-Ba, SWy-Cu, and SWy-Co). The experimental protocol is summarized in Figure 3.Figure 3
Experimental cation exchange protocol.To be able to analyze the complexes obtained using XRD, oriented sample was prepared by placing the obtained suspensions on a glass slide at air dry for 24 h.


### 2.6. X-Ray Diffraction (XRD)

Structural characterization is carried out using XRD analysis by a Bruker D8 ADVANCE (Bruker AXS GmbH, Karlsruhe, Germany) with CuKα monochromatic radiation (λ=0.15406nm) at 40 kV and 20 mA. The usual scanning parameters were 0.01 (2θ°) as the step size and 6 s as the counting time per step over the explored angular range. Indeed, the XRD profiles were recorded in the 2θ° range from 3.5 to 60 for all specimens. All records are made at room temperature under atmospheric pressure. XRD investigations were directed by the correlation between qualitative and quantitative analyses.


#### 2.6.1. Semiquantitative XRD Analysis

The semiquantitative XRD investigation is carried out by determining, respectively, the observed homogeneity structure based on the 001 reflections shape, the experimentald001 basal spacing value, the calculated full width at the maximum half FWHM, the calculated crystallite size D, and the calculated rationality parameter ξ [98, 99]. This preliminary analysis remains insufficient to deeply identify interlamellar space (IS) contents, layer stacking mode at the crystallite size, the average layer number per stacking, the water molecule abundance and configuration, the saturation of the exchangeable intern and extern site, the hydration heterogeneities, the cause of the observed heterogeneity and the position, and the abundance of the exchangeable cation, and more.


#### 2.6.2. XRD Profile Modeling: Theoretical Diffracted Intensity and Modeing Strategy

The modeling XRD approach is based on a matrix mathematical formalism developed by [42]. The expression of the intensity of the diffracted waves along the c∗ axis is as follows:
(2)I0012θ=LpSpurReϕWI+2∑nM−1M−nnQn,where Re means the real part of the final matrix, Spur is the sum of the diagonal terms of the real matrix, Lp is the Lorentz polarization factor, M is the number of layers per stack, n=1, …, 1–M–1, [Ф], is the matrix of the structural factor, I is the unitary matrix, W is the diagonal matrix of the proportions of the different types of layers, and Q is the matrix representing the interference phenomena between the adjacent layers.The modeling approach allowed us to identify the abundance of different layer types abundances (Wi), the type and the abundance of the mixed layer structure MLS, the stacking mode of different layer types, the average number M of layers per coherent scattering domain (CSD), and the IS water molecule distribution [78]. Within a CSD, layer stacking is described by a set of junction probabilities (Pij). Briefly, the relationship between probabilities and Wi abundance of two different types of layers (i and j) can be summarized as follows: (i) the segregation tendency is given by Wi<Pii and Wj<Pjj, (ii) total demixing is obtained for Pii=Pjj=1, (iii) the regular tendency is obtained if Wi<Pji<1 and Wj<Pij<1, and (iv) finally, the boundary between the last distribution labeled chaotic/or random is obtained when Wi=Pji=Pii and Wj=Pij=Pjj with ΣWi=1 and ΣPij=1 [42, 100].The modeling strategy consists of the theoretical reproduce of the experimental XRD profile initially from a homogeneous structure subsequently improved by adding other supplementary contributions. The existence of two mixed-layer structures (MLS) does not reflect the presence of two populations of particles physically present in the sample [48, 79, 101]. Therefore, layers with the same hydration state present in different MLS contributing to the diffracted intensity are assumed to have identical properties (chemical composition, layer thickness, and z-coordinates of atoms). The details of the XRD modeling approach are explained in detail in previous work of [41, 48, 78, 79, 101]. The atomic coordinates z in the 2 : 1 layer framework (octahedral layer sandwiched between two tetrahedral layers) are shown in Table 2. The z-coordinates of the IS content (exchangeable cation, molecules, etc.) are optimized, during the modeling process [66, 102], to improve the agreement Rwp:
(3)RWP=∑I2θiexp−I2θicalc2∑I2θiexp2×100%,where I2θiexp is the experimental diffracted intensity, and I2θicalc is the calculated ones.Table 2
Thez atomic coordinates within the 2 : 1 layer framework along the c∗ axis [42].
Atom typeO1O2O3O4O5O6OH1OH2Si1Si2AlNumber21221211222Zn (Å)00.202.254.316.266.591.984.280.596.043.43


#### 2.6.3. Modeling Strategy

The search for optimal structural parameters passes necessary through the determination of the shape function called “modulation function.” It is related to the positions of the characteristic XRD reflections, by making the variations of the following parameters: (i) theWi proportions of the different distances and the relative probabilities Pij of succession law between layer type i and layer type j and (ii) the average layer number M per stack.The agreement between theoretical and experimental profile is improved (decrease ofRWP value) by some adjustment attributed to the following parameters: (i) the z position of the layer atom composition along the c∗ axis, (ii) the number and position z of the exchangeable cations, and (iii) the abundance and the configuration (their z positions following the normal at the sheet plane [82, 99, 103, 104] of the interlayer water molecules). A brief modeling strategy summary is reported in Figure 4.Figure 4
The main input structural parameter for the XRD modeling approach.


### 2.7. Thermal Analysis: Thermogravimetry/Differential Thermal Analysis (TG/DTA)

The hydration properties are very sensitive to the amount of water molecule which is identified by TG-DTA thermal analyses coupled with the “Labsys TG” model. All TG-DTA records are realized at variable temperatures from 0 to 500°C at a speed of 5°C/min. The used gas stream is argon. Approximately 10 mg of sample was used in platinum pans in each analysis. The determination of nH2O necessarily depends on the results drawn from the TG-DTA curves followed by a theoretical calculation via modeling. After having optimized the theoretical XRD models, a structural formula per half unit cell can be determined by taking into account the weighting of each MLS and then of each layer population and its specific weighting as well as the average number of layers per crystallite (Table 3). Subsequently, the molar mass of the obtained results is calculated. The number of nH2O (abundance) is estimated according to the following parameters: the initial mass minitial of the sample before analysis, the variation in sample mass Δm, the average number of layers M, and the number of moles n (deduced from masse molar).Table 3
Examples of half-cell structural formulas for raw montmorillonite SWy-2 and exchanged (SWy-2) with sodium and heavy metals at full saturation.
SamplesStructural half-cell formulaSWy-2(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Ca2+0.07, K+0.01, Na+0.2)SWy-Na(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Na+0.28)SWy-Co(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Co2+0.14)SWy-Cu(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Cu2+0.14)SWy-Ba(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Ba2+0.14)


### 2.8. Adsorption Analysis and Porosity Investigation

This study uses BET analysis in order to gain insight in particular surface area (SA) estimation in the case of porous materials, yielding knowledge in the effects of porosity fate and particle size evolution versus constraint strength [41, 105, 106]. This goal is achieved by multilayer nitrogen adsorption isotherm variation (performed at 77 K) versus relative pressure (P/P0~0.95). This task is fully automated manipulating Quantachrome NOVA 2000e series volumetric gas adsorption instrument. BJH analysis is employed to define pore area and specific pore volume by means of adsorption and desorption procedures. Also, the pore size distribution (PSD) was identified assuming several pores shape approximations. The adsorbed nitrogen and oxygen were eliminated under reduced (vacuum) pressure at 100°C for 8 h before measuring SA and PSD [107–110].


## 2.1. Baseline Material

A standard dioctahedral smectite SWy-2 extracted from the cretaceous formations of Wyoming (USA) and provided by the clay mineral repository is selected for the present study [1]. The structural formula per half-cell is given by [43]:
(1)Si4+3.96,Al3+0.04Al3+1.53,Fe3+0.18,Fe2+0.045,Mg2+0.26,Ti4+0.01O10OH2Ca2+0.07,K+0.01Na+0.2This bentonite exhibits a low octahedral charge and extremely limited tetrahedral Substitutions. The clay cation exchange capacity (CEC) is 101 meq/100 g [43].


## 2.2. Pretreatment

A pretreatment of the starting material consists of preparing Na-rich montmorillonite suspension (SWy-Na) is realized following a classic protocol detailed by [41] as shown in Figure 1.Figure 1
Experimental protocol for the purification of the starting material. Excess of salt was washed out by 24 h cycles:centrifugation8000rpm+removalofthesupernatant.


## 2.3. Exchangeable Cations

Three heavy metal cations (Ba2+, Cu2+, and Co2+) were the subject of the cation exchange process. The cation preference is explained by the wonderful abundance of the latter in industrial and radioactive waste and the specific characteristics of each one [97].


## 2.4. First-Order Coupling Constraints

First-order stress coupling is based on the association of geochemical (soil solution pH) and the thermal gradients (obtained by varyingT°C) at the laboratory scale. To achieve this goal, an MCl2 solution (where M is the metal cation Ba2+, Cu2+ and Co2+) at a well-determined pH is prepared at a low concentration (0.1 M), followed by the addition of Na-rich montmorillonite powder (SWy-Na). For each constraint pair created (fixed pH and fixed T), an adjustment of the overall volume (200 mL) is made by adding the metal chloride solution and the acid or base additive. Subsequently, and after several mechanical shaking cycle, a cation exchange process will take place at a well-determined temperature for a fixed specified period (24 h) (Figure 2). The soil solution pH variation and temperature values (T°C) are carried out on the same sample. All experimental parameters are summarized in Table 1.Figure 2
Experimental assembly of the 1st order coupling.Table 1
Soil solution pH and temperatures of the coupling of the 1st order of the stresses.
Coupling of the 1st orderSoil solution pHTemperature (°C)Time (h)V (mL)Acid35024560Neutral770200Basic9801190


## 2.5. Cation Exchange Process

A cation exchange process is carried out for each bivalent metal cations Ba2+, Cu2+, and Co2+ brought into contact with the starting sample. The experimental protocol established for each sample consists of applying a mechanical shake throughout 48 h, followed by centrifugation at 4000 rpm. This step is repeated five times to ensure process achievement. After recovery of the solid fraction, a series of washes with distilled water will take place to remove excess of salt from chloride ions. The obtained sample is labeled SWy-M with M that is the metal cation type (e.g., SWy-Ba, SWy-Cu, and SWy-Co). The experimental protocol is summarized in Figure 3.Figure 3
Experimental cation exchange protocol.To be able to analyze the complexes obtained using XRD, oriented sample was prepared by placing the obtained suspensions on a glass slide at air dry for 24 h.


## 2.6. X-Ray Diffraction (XRD)

Structural characterization is carried out using XRD analysis by a Bruker D8 ADVANCE (Bruker AXS GmbH, Karlsruhe, Germany) with CuKα monochromatic radiation (λ=0.15406nm) at 40 kV and 20 mA. The usual scanning parameters were 0.01 (2θ°) as the step size and 6 s as the counting time per step over the explored angular range. Indeed, the XRD profiles were recorded in the 2θ° range from 3.5 to 60 for all specimens. All records are made at room temperature under atmospheric pressure. XRD investigations were directed by the correlation between qualitative and quantitative analyses.


### 2.6.1. Semiquantitative XRD Analysis

The semiquantitative XRD investigation is carried out by determining, respectively, the observed homogeneity structure based on the 001 reflections shape, the experimentald001 basal spacing value, the calculated full width at the maximum half FWHM, the calculated crystallite size D, and the calculated rationality parameter ξ [98, 99]. This preliminary analysis remains insufficient to deeply identify interlamellar space (IS) contents, layer stacking mode at the crystallite size, the average layer number per stacking, the water molecule abundance and configuration, the saturation of the exchangeable intern and extern site, the hydration heterogeneities, the cause of the observed heterogeneity and the position, and the abundance of the exchangeable cation, and more.


### 2.6.2. XRD Profile Modeling: Theoretical Diffracted Intensity and Modeing Strategy

The modeling XRD approach is based on a matrix mathematical formalism developed by [42]. The expression of the intensity of the diffracted waves along the c∗ axis is as follows:
(2)I0012θ=LpSpurReϕWI+2∑nM−1M−nnQn,where Re means the real part of the final matrix, Spur is the sum of the diagonal terms of the real matrix, Lp is the Lorentz polarization factor, M is the number of layers per stack, n=1, …, 1–M–1, [Ф], is the matrix of the structural factor, I is the unitary matrix, W is the diagonal matrix of the proportions of the different types of layers, and Q is the matrix representing the interference phenomena between the adjacent layers.The modeling approach allowed us to identify the abundance of different layer types abundances (Wi), the type and the abundance of the mixed layer structure MLS, the stacking mode of different layer types, the average number M of layers per coherent scattering domain (CSD), and the IS water molecule distribution [78]. Within a CSD, layer stacking is described by a set of junction probabilities (Pij). Briefly, the relationship between probabilities and Wi abundance of two different types of layers (i and j) can be summarized as follows: (i) the segregation tendency is given by Wi<Pii and Wj<Pjj, (ii) total demixing is obtained for Pii=Pjj=1, (iii) the regular tendency is obtained if Wi<Pji<1 and Wj<Pij<1, and (iv) finally, the boundary between the last distribution labeled chaotic/or random is obtained when Wi=Pji=Pii and Wj=Pij=Pjj with ΣWi=1 and ΣPij=1 [42, 100].The modeling strategy consists of the theoretical reproduce of the experimental XRD profile initially from a homogeneous structure subsequently improved by adding other supplementary contributions. The existence of two mixed-layer structures (MLS) does not reflect the presence of two populations of particles physically present in the sample [48, 79, 101]. Therefore, layers with the same hydration state present in different MLS contributing to the diffracted intensity are assumed to have identical properties (chemical composition, layer thickness, and z-coordinates of atoms). The details of the XRD modeling approach are explained in detail in previous work of [41, 48, 78, 79, 101]. The atomic coordinates z in the 2 : 1 layer framework (octahedral layer sandwiched between two tetrahedral layers) are shown in Table 2. The z-coordinates of the IS content (exchangeable cation, molecules, etc.) are optimized, during the modeling process [66, 102], to improve the agreement Rwp:
(3)RWP=∑I2θiexp−I2θicalc2∑I2θiexp2×100%,where I2θiexp is the experimental diffracted intensity, and I2θicalc is the calculated ones.Table 2
Thez atomic coordinates within the 2 : 1 layer framework along the c∗ axis [42].
Atom typeO1O2O3O4O5O6OH1OH2Si1Si2AlNumber21221211222Zn (Å)00.202.254.316.266.591.984.280.596.043.43


### 2.6.3. Modeling Strategy

The search for optimal structural parameters passes necessary through the determination of the shape function called “modulation function.” It is related to the positions of the characteristic XRD reflections, by making the variations of the following parameters: (i) theWi proportions of the different distances and the relative probabilities Pij of succession law between layer type i and layer type j and (ii) the average layer number M per stack.The agreement between theoretical and experimental profile is improved (decrease ofRWP value) by some adjustment attributed to the following parameters: (i) the z position of the layer atom composition along the c∗ axis, (ii) the number and position z of the exchangeable cations, and (iii) the abundance and the configuration (their z positions following the normal at the sheet plane [82, 99, 103, 104] of the interlayer water molecules). A brief modeling strategy summary is reported in Figure 4.Figure 4
The main input structural parameter for the XRD modeling approach.


## 2.6.1. Semiquantitative XRD Analysis

The semiquantitative XRD investigation is carried out by determining, respectively, the observed homogeneity structure based on the 001 reflections shape, the experimentald001 basal spacing value, the calculated full width at the maximum half FWHM, the calculated crystallite size D, and the calculated rationality parameter ξ [98, 99]. This preliminary analysis remains insufficient to deeply identify interlamellar space (IS) contents, layer stacking mode at the crystallite size, the average layer number per stacking, the water molecule abundance and configuration, the saturation of the exchangeable intern and extern site, the hydration heterogeneities, the cause of the observed heterogeneity and the position, and the abundance of the exchangeable cation, and more.


## 2.6.2. XRD Profile Modeling: Theoretical Diffracted Intensity and Modeing Strategy

The modeling XRD approach is based on a matrix mathematical formalism developed by [42]. The expression of the intensity of the diffracted waves along the c∗ axis is as follows:
(2)I0012θ=LpSpurReϕWI+2∑nM−1M−nnQn,where Re means the real part of the final matrix, Spur is the sum of the diagonal terms of the real matrix, Lp is the Lorentz polarization factor, M is the number of layers per stack, n=1, …, 1–M–1, [Ф], is the matrix of the structural factor, I is the unitary matrix, W is the diagonal matrix of the proportions of the different types of layers, and Q is the matrix representing the interference phenomena between the adjacent layers.The modeling approach allowed us to identify the abundance of different layer types abundances (Wi), the type and the abundance of the mixed layer structure MLS, the stacking mode of different layer types, the average number M of layers per coherent scattering domain (CSD), and the IS water molecule distribution [78]. Within a CSD, layer stacking is described by a set of junction probabilities (Pij). Briefly, the relationship between probabilities and Wi abundance of two different types of layers (i and j) can be summarized as follows: (i) the segregation tendency is given by Wi<Pii and Wj<Pjj, (ii) total demixing is obtained for Pii=Pjj=1, (iii) the regular tendency is obtained if Wi<Pji<1 and Wj<Pij<1, and (iv) finally, the boundary between the last distribution labeled chaotic/or random is obtained when Wi=Pji=Pii and Wj=Pij=Pjj with ΣWi=1 and ΣPij=1 [42, 100].The modeling strategy consists of the theoretical reproduce of the experimental XRD profile initially from a homogeneous structure subsequently improved by adding other supplementary contributions. The existence of two mixed-layer structures (MLS) does not reflect the presence of two populations of particles physically present in the sample [48, 79, 101]. Therefore, layers with the same hydration state present in different MLS contributing to the diffracted intensity are assumed to have identical properties (chemical composition, layer thickness, and z-coordinates of atoms). The details of the XRD modeling approach are explained in detail in previous work of [41, 48, 78, 79, 101]. The atomic coordinates z in the 2 : 1 layer framework (octahedral layer sandwiched between two tetrahedral layers) are shown in Table 2. The z-coordinates of the IS content (exchangeable cation, molecules, etc.) are optimized, during the modeling process [66, 102], to improve the agreement Rwp:
(3)RWP=∑I2θiexp−I2θicalc2∑I2θiexp2×100%,where I2θiexp is the experimental diffracted intensity, and I2θicalc is the calculated ones.Table 2
Thez atomic coordinates within the 2 : 1 layer framework along the c∗ axis [42].
Atom typeO1O2O3O4O5O6OH1OH2Si1Si2AlNumber21221211222Zn (Å)00.202.254.316.266.591.984.280.596.043.43


## 2.6.3. Modeling Strategy

The search for optimal structural parameters passes necessary through the determination of the shape function called “modulation function.” It is related to the positions of the characteristic XRD reflections, by making the variations of the following parameters: (i) theWi proportions of the different distances and the relative probabilities Pij of succession law between layer type i and layer type j and (ii) the average layer number M per stack.The agreement between theoretical and experimental profile is improved (decrease ofRWP value) by some adjustment attributed to the following parameters: (i) the z position of the layer atom composition along the c∗ axis, (ii) the number and position z of the exchangeable cations, and (iii) the abundance and the configuration (their z positions following the normal at the sheet plane [82, 99, 103, 104] of the interlayer water molecules). A brief modeling strategy summary is reported in Figure 4.Figure 4
The main input structural parameter for the XRD modeling approach.


## 2.7. Thermal Analysis: Thermogravimetry/Differential Thermal Analysis (TG/DTA)

The hydration properties are very sensitive to the amount of water molecule which is identified by TG-DTA thermal analyses coupled with the “Labsys TG” model. All TG-DTA records are realized at variable temperatures from 0 to 500°C at a speed of 5°C/min. The used gas stream is argon. Approximately 10 mg of sample was used in platinum pans in each analysis. The determination of nH2O necessarily depends on the results drawn from the TG-DTA curves followed by a theoretical calculation via modeling. After having optimized the theoretical XRD models, a structural formula per half unit cell can be determined by taking into account the weighting of each MLS and then of each layer population and its specific weighting as well as the average number of layers per crystallite (Table 3). Subsequently, the molar mass of the obtained results is calculated. The number of nH2O (abundance) is estimated according to the following parameters: the initial mass minitial of the sample before analysis, the variation in sample mass Δm, the average number of layers M, and the number of moles n (deduced from masse molar).Table 3
Examples of half-cell structural formulas for raw montmorillonite SWy-2 and exchanged (SWy-2) with sodium and heavy metals at full saturation.
SamplesStructural half-cell formulaSWy-2(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Ca2+0.07, K+0.01, Na+0.2)SWy-Na(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Na+0.28)SWy-Co(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Co2+0.14)SWy-Cu(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Cu2+0.14)SWy-Ba(Si4+3.96, Al3+0.04) (Al3+1.53, Fe3+0.18, Fe2+0.045, Mg2+0.26, Ti4+0.01) O10 (OH) 2 (Ba2+0.14)


## 2.8. Adsorption Analysis and Porosity Investigation

This study uses BET analysis in order to gain insight in particular surface area (SA) estimation in the case of porous materials, yielding knowledge in the effects of porosity fate and particle size evolution versus constraint strength [41, 105, 106]. This goal is achieved by multilayer nitrogen adsorption isotherm variation (performed at 77 K) versus relative pressure (P/P0~0.95). This task is fully automated manipulating Quantachrome NOVA 2000e series volumetric gas adsorption instrument. BJH analysis is employed to define pore area and specific pore volume by means of adsorption and desorption procedures. Also, the pore size distribution (PSD) was identified assuming several pores shape approximations. The adsorbed nitrogen and oxygen were eliminated under reduced (vacuum) pressure at 100°C for 8 h before measuring SA and PSD [107–110].


## 3. Results and Discussion

### 3.1. Semiquantitative XRD Investigation of the Baseline Samples

The experimental XRD profile of the starting SWy-Na complex (Figure5) shows three characteristic reflections (n=1, 2, and 4). The first reflection (001) is located at 2θ=7.16° (d001=12.33Å) probably indicating a hydration 1 W state (Table 4). By calculating the FWHM and ξ parameter value, the homogeneous observed character is confirmed [111, 112]. This result is consistent with the results of [48] on the same sample. Na-rich montmorillonite (SWy-Na) has been studied extensively before since it is considered a reference sample [5–7, 41, 48, 78–79, 89, 113]. At this level, our goal is to refine the obtained literature results related to the SWy-Na sample. For the SWy-Cu, SWy-Co, and SWy-Ba samples, qualitative and quantitative XRD results extracted from the same authors earlier works [47, 97] are used (Tables 4 and 5).Figure 5
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Na.∗Halite (NaCl).Table 4
Qualitative XRD investigation in the case of the samples SWy-Na, SWy-Co, SWy-Cu, and SWy-Ba [47, 97].
Sample2θ°d001 (Å)FWHM (2θ°)D (Å)ξ (Å)CharacterSWy-Na7.1612.330.7418.770.062HomogeneousSWy-Co [47]5.8614.880.7119.550.520InterstratifiedSWy-Cu [47]7.1412.360.6122.770.100HomogeneousSWy-Ba [91]5.9114.941.5508.960.970InterstratifiedNotes: 2θ°: Bragg’s angle; d001: basal distance of the 1st reflection; D: average crystalline size; FWHM: full width at half maximum; ξ: rationality deviation parameters.Table 5
Optimum structural parameters used for modeling XRD profiles in the case of baseline samples [47, 97].
Sample% MLSd001nH2OWAPAASMMRWP (%)SWy-Na8010.500.800.85R1−seg102.272012.52SWy-Co [47]1612.41.10.160.30R1−seg84.258415.21.9SWy-Cu [47]9512.41.10.950.05R1−seg83.820515.21.9SWy-Ba [91]6412.41.10.150.15R083.7715.21.93612.41.10.650.77R1−seg15.22.0Notes:d001: interlamellar distance; nH2O: number of water molecules per half-cell; zH2O: position of the molecules along the c∗ axis of the H2O molecule is attached to 9.6 Å for hydration states 1 W. The position of the exchangeable cations per half-cell calculated along the axis c∗ is fixed à 9.6 Å for hydration states 1 W [41]. M: average number of sheets per stack; SM: layer stacking mode; R0: maximum order; R1: random stacking; R1−X, associated stacking (segregation-partial order); C: characters; Ho: homogeneous; He: heterogeneous; RWP: confidence factor.


### 3.2. Modeling of XRD Profiles in the Case of SWy-Na Sample

The mixed layer structure (MLS) used to achieve the best agreement between the experimental and calculated XRD model (Figure5) shows an heterogeneous hydration character that results in the coexistence of two types of layers (0 W and 1 W) with a strong dominance for the 1 W phase at about 80%. This opposes the obtained qualitative description.Indeed, the distribution of IS water molecules has respected the previous work [5, 6, 48, 88, 101] with a water sheet located in the middle of the IS for 1 W phase and the absence of water in the IS for the dehydrated state 0 W. Regardless of the type of hydration state, the exchangeable cations Na (per half-cell unit) are positioned in the center of the IS along the c∗ axis respecting the configuration of the data provided by the literature [5, 48]. The average number of layers per crystallite M is equal to 10. The confidence factor RWP is very low (2.27%), which reflects the high quality of fitting. The structural parameters are summarized in Table 5.


### 3.3. Semiquantitative Description of XRD Analysis after Applying First-Order Coupling Stress

#### 3.3.1. Case of the SWy-Co Sample

The experimental XRD results for the SWy-Co samples obtained are shown in Figure6. For the first three constraint coupling levels (pH=3; T=50°C⟶pH=7; T=70°C), there is an asymmetry for the main 001 reflections located at 6.1 in 2θ° with d001~ 14.5 Å synonymous of a minor 2 W hydration state presence attributed to the Co2+ cation in IS. Also, a shoulder towards the wide angles around in 7.2° in 2θ (d001~ 12.3 Å) attributed to the existence of the sodium residue resulting from the starting sample. Generally, the observed asymmetric 001 reflections indicates the coexistence of several hydration states within the crystallite and/or a partial cation exchange process. The values of the FWHM and ξ parameters confirms this idea (Table 6).Figure 6
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Co.Table 6
Qualitative XRD investigation in the case of the samples SWy-Co SWy-Cu and SWy-Ba.
Samples2θ°d001 (Å)FWHM (2θ°)D (Å)ξ (Å)CharactersSWy-CopH=3; T=50°C06.2214.201.2710.930.563InterstratifiedpH=5; T=60°C06.2414.151.1811.770.653pH=7; T=70°C06.0914.501.0013.890.406pH=9; T=80°C06.0714.551.9307.190.109pH=11; T=90°C∗∗∗∗∗SWy-CupH=3; T=50°C07.1612.340.6122.770.016HomogeneouspH=5; T=60°C07.0312.570.7119.570.096pH=7; T=70°C07.0812.481.7407.980.114InterstratifiedpH=9; T=80°C07.0612.511.9707.050.207pH=11; T=90°C07.0012.622.1406.490.270SWy-BapH=3; T=50°C07.1812.300.7019.850.055HomogeneouspH=5; T=60°C07.1412.371.3010.690.013InterstratifiedpH=7; T=70°C07.2012.270.5525.260.091HomogeneouspH=9; T=80°C07.1812.300.6820.430.216pH=11; T=90°C07.3512.020.5724.380.064Notes:∗absence of the 001 reflection.In Table6, for the rest of the samples, a different hydration behavior was observed. The diffracted intensity ratio I001/I002, I001/I003, and I001/I004 of the complex studied under (pH=9, T=80°C/pH=11, T=90°C) decreases if compared with the three first studied samples. Also, a drastic decrease in the 001-reflection intensity is observed in both samples and which probably indicates a bottom transformation that affected the structure when increasing constraints strength. This strange structural behavior finds an explanation by the effect of the increase in temperature and the basic aspect of the soil solution pH on the cohesion energy between layers and even destruction of the chemical bonds within octahedral and tetrahedral sheet forming the layer. The main structure is affected and an elevated layer’s exfoliation trends within the crystallites favoring a total transformation of the original 2 : 1 phase to a 1 : 1 clay structure that was established. The raised value of the 002-reflection intensity and the absence of the 001 line can be interpreted in this case by the beginning of a great structural transformation. This remains to be proven by quantitative XRD analysis and by studying the porosity evolution of these two samples.


#### 3.3.2. Case of the SWy-Cu Sample

The experimental XRD models, in the case of SWy-Cu, obtained by varying the external constraint strength are summarized in Figure7. For the first two constraints of the coupling value (pH=3; T=50°C and pH=5; T=60°C), the experimental XRD models are almost identical with a low FWHM value (Table 6) indicating probably either the coexistence, within the stacks, of several hydration states [77] or an unfinished (partial) cation exchange, knowing that Cu2+ cation is indistinguishable from the starting sodium by simple XRD analysis at room conditions from the starting sodium cation [47]. All qualitative parameters are summarized in Table 6. For the rest of the complexes (pH=7; T=70°C⟶pH=11; T=90°C), a stack towards the small angles (5.9°⟶15Å) appeared and ascribed to the material response to the applied stress. Indeed, a beginning of 2 W transition, without a real domination, is confirmed by increasing the coupling constraint intensity. It remains to be noted that the higher-order peaks have a relatively low intensity regardless surrounding environment change and from soilsolutionpHvalue=7 and temperature T=70°C, an abrupt structural change is observed.Figure 7
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Cu.


#### 3.3.3. Case of the SWy-Ba Sample

The experimental XRD profiles of SWy-Ba sample are reported in Figure8. An intense 001 reflection situated at 7.2° (2θ) (d001~ 12.3 Å) indicating a 1 W hydration state dominates all sample. This probably reflects the existence of a Na+ residue originating from the starting sample or from added NaOH solution used to balance the pH solution. This opposes the earlier results [41, 97] on cation exchange in the case of Ba2+ which demonstrate a 2 W hydration state behavior.Figure 8
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Ba.ForpH=5/T=60°C, the XRD profile shows a shoulder towards the low angles (5.8°⟶d001=15.23Å) with an increase in the FWHM and ξ parameter value indicating the 2 W hydration state transition beginning. Also, it can be interpreted by the coexistence, within the stacks, of several states of hydration [77] or an unfinished (partial) cation exchange knowing that the barium hydrate baseline to two layers of water 2 W (15 Å). All qualitatively estimated parameters are summarized in Table 6.


### 3.4. XRD Modeling Profiles after Applying First-Order Coupling Stress

#### 3.4.1. Case of the SWy-Co Samples

The qualitative XRD analysis suggested heterogeneous hydration behavior for SWy-Co samples, regardless of the strength of the stresses applied. This interstratification has been approved by the 001 reflection modeling approach which assumes the coexistence of two different hydration states (e.g., 1 W and 2 W). To improve the agreement between the calculated and experimental models (Figure6) and for each constraint strength from pH=5/T=60°C towards pH=11/T=90°C, the proposed MLS is theoretically decomposed into two layer populations type (i.e., 1 W: d001~ 12.2 Å and 2 W: d001~ 15.2 Å) stacked according to specific succession probability laws. The structural parameters associated with this modeling approach are summarized in Table 7. The proposed MLS is obtained by weighted layer populations that are tolerated to have an identical chemical composition, identical layer thickness, and identical z-atoms coordinates [40, 48]. The CEC of the results is partially saturated by the Na+ and Co2+ cations since, under ambient conditions, sodium always has a hydration state of 1 W [41, 48], and cobalt has a hydration state of 2 W.Table 7
Structural parameters of SWy-Co, SWy-Cu, and SWy-Ba.
Samples% MLSxW-echa.catd001nH2OWAPAASMMMtotRWPSWy-CopH=3; T=50°C16.681 W-Na12.20.044211R00593.6183.281 W-Na12.20.03460.400.55R1−seg102 W-Co15.20.02590.0259pH=5; T=60°C16.701 W-Na12.20.032211R00593.7983.301 W-Na12.20.02520.400.55R1−seg102 W-Co15.20.01890.0189pH=7; T=70°C351 W-Na12.20.02300.350.63R1−seg0883.42652 W-Co15.20.03000.0300pH=9; T=80°C401 W-Na12.20.02000.400.40R00777.45602 W-Co15.20.02430.0243pH=11; T=90°C401 W-Na12.20.01010.400.40R00779.12602 W-Co15.20.01130.0113SWy-CupH=3; T=50°C81.231 W-Na12.20.11660.950.95R014123.842 W-Cu15.20.00310.003118.771 W-Na12.20.03330.950.95R0042 W-Cu15.20.00090.0009pH=5; T=60°C84.201 W-Na12.20.07970.850.86R1−seg14123.562 W-Cu15.20.00700.007015.801 W-Na12.20.02280.850.86R1−seg042 W-Cu15.20.00200.0020pH=7; T=70°C751 W-Na12.20.04100.750.90R1−seg10104.92252 W-Cu15.20.00680.0068pH=9; T=80°C701 W-Na12.20.02500.700.87R1−seg0886.04302 W-Cu15.20.01480.0148pH=11; T=90°C701 W-Na12.20.02840.700.87R1−seg0887.73302 W-Cu15.20.00610.0061SWy-BapH=3; T=50°C72.171 W-Na12.20.100111R012105.4127.831 W-Na12.20.04460.900.89R1−p.ord062 W-Ba15.20.00450.0045pH=5; T=60°C841 W-Na12.20.09780.840.91R1−seg10105.96162 W-Ba15.20.00930.0093pH=7; T=70°C951 W-Na12.20.09050.950.97R1−seg12125.22052 W-Ba15.20.00450.0045pH=9; T=80°C65.751 W-Na12.20.061111R013135.3734.251 W-Na12.20.02020.800.85R1−seg132 W-Ba15.20.00250.0025pH=11; T=90°C150 W-Na10.20.00000.850.83R1−p.ord13135.16851 W-Ba12.20.0750Notes: xW-echa.cat: layer type and associated exchangeable cation;d001: interlamellar distance; nH2O: number of water molecules per half-cell; zH2O: position of the molecules along the c∗ axis of the H2O molecule is attached to 9.6 Å and 11.3 Å–13.9 Å for hydration states 1 W and 2 W, respectively. The position of the exchangeable cations per half-cell calculated along the axis c∗ is fixed with 9.60 Å and 12.25 Å for hydration states 1 W and 2 W [41]; n-echa.cat: number of exchangeable cations per half-cell is set to 0.28 (for the cation Na+) and at 0.14 (for bivalent metal cations), indicating complete saturation of cation exchange capacity (CEC); M: average number of sheets per stack; Mtot, total average number of sheets per stack; SM: layer stacking mode; R0: maximum order; R1: random stacking; R1−X: associated stacking (segregation-partial order); C: characters; Ho: homogeneous; He: heterogeneous; RWP: confidence factor.The theoretical decomposition of the SWy-Co sample, (pH=11; T=90°C) which has undergone fundamental changes in its basic structure, can be followed by two major hypotheses:The 1st consists in considering that it is still a T-O-T type structure despite the absence of the main 001 reflection which must be positioned around 6.1° (2θ) (d001~ 14.5 Å) and can be attenuated (is no longer sensitive to X-rays during diffractogram recordings) following the increase in the applied stress strength. In this case, a theoretical model based on the heterogeneous mixed 1 W/2 W structure with a major domination for the phase 2 W was adopted with very low average layer number per crystallite. This hypothesis can be practically verified for the good agreement towards higher diffraction orders.The 2nd considers that the basic clay structure has been strictly modified following the coupled increase in temperature T and the soil solution pH during the cation exchange process. This supposition is justified through the destruction of chemical bonds within the crystallite and/or which give rise to a new structure derived from smectite. This result, despite its originality, agrees with the work of [108, 109] which focuses on the hydrothermal synthesis of zeolite from clay minerals by controlling the pH effect on the synthesis process. Hence, the transition from a T-O-T phyllosilicate type (montmorillonite) to another kaolinite T-O phyllosilicate type is probabilistic, knowing that kaolinite has a dioctahedral structure [114–116]. Its structural half-cell formula is defined by (Si4 Al4 O10 (OH)8), whose basal distance d001 is of the order of 7 Å [117–119] with a closed IS accompanied by the absence of isomorphic substitutions (not CC in the middle of IS). For this hypothesis (Figure 6), we consider that the first reflection (in the 1st hypothesis was considered as 2nd reflection 002) is positioned around 12° (2θ) (d001~ 7 Å) from where the second reflection is necessarily positioned around 24° (2θ) (Table 7). For this hypothesis, we note the presence of a relatively intense reflection around 18° (2θ). A rational reflection position is obtained for the three reflections order (12°⟶18°⟶24°). Also, the exchangeable cation has no place in this configuration, which even calls into question the cation exchange process. Therefore, the first supposition seems more scientifically logical. The 1st hypothesis has been adopted in the rest of the calculations. It remains to be noted that the quality of the fitting is controlled by the RWP parameter.


#### 3.4.2. Case of the SWy-Cu Samples

The best agreement between theoretical and experimental XRD patterns (Figure7) of the SWy-Cu samples is obtained using an interstratified structure of two MLS comprising various relative layers proportions with different hydration states (Table 7). This variability confirms the heterogeneous hydration character and the intermediate 1 W-2 W hydration phase observed regardless of the intensity of the applied constraints. In detail, a minor contribution of the 2 W phase increases from 5% to 30% by increasing the intensity of the external applied stress (pH=3; T=50°C⟶pH=11; T=90°C). Indeed, the 2 W hydration phase implemented in the theoretical model is necessarily attributed to the layer fraction whose CEC is saturated by Cu2+. This weighting fluctuation is evidence of an incomplete cation exchange process (d001<15Å). On the other hand, the dominance of 1 W layer hydration phase is interpreted by the existence of a fraction (quite large) regardless of the applied constraints applied. This contribution is attributed to the sodium residues from the starting sample (SWy-Na).The agreements obtained between the experimental and theoretical profiles (RWP~3% to 8%) are generally acceptable (< 10%), despite the misfit observed after widening the peaks around 14° and 28° (2θ). In fact, this disagreement can be broken down into a good reflection position agreement and a disagreement of diffracted intensity related to the input fluctuation of the distribution and abundance of water molecules in the IS. This disagreement led us to explore wide-angle areas, later to establish a possible link between CEC saturation and the degree of hydration heterogeneity.The logical increase of theRWP factor in the case of SWy-Cu sample reflects the increase in the heterogeneity’s degree defined, respectively, by an asymmetry of the first 001 reflections, the high FWHM value, and the ξ rationality parameter. Theoretically, this result is related to the variability of possible MLS configurations allowing a good fit of the 001 reflection. The exploitation of the WA, PAA, M, and RWP values allowed us to characterize a specific distribution of the n normalized layers within the crystallites according to the generated stacking modes and the contribution of each phase. This statistical representation of the layer can help to understand the CEC sensitivity fluctuation (of the starting sample) following the variation in the temperature T and pH during the cation exchange process.


#### 3.4.3. Case of the SWy-Ba Samples

For SWy-Ba samples, the best agreements between theoretical and experimental models are shown in Figure8. The main structural parameters used to achieve a good fit are summarized in Table 7. For each model, several types of layers with variable stacking mode are used to improve the agreement obtained between the experimental and calculated models. This MLS is composed by several layers of type populations depending on the hydration state (0 W, 1 W, and 2 W) whose basal distance d001 is equal to 10.2 Å, 12.2 Å, and 15.2 Å, respectively. This variability confirms the heterogeneous hydration character observed by qualitative XRD analysis for the entire SWy-Ba series (pH=3; T=50°C⟶pH=11; T=90°C) with a major dominance for the 1 W hydration phase saturated by Na+ cation assigned to the starting sample. In addition, the 2 W phases are assigned to the fraction whose CEC is saturated by Ba2+ cation [41]. More specifically, for the first four samples from pH=3/T=50°C towards pH=9/T=80°C, an omnipresent minor contribution of the 2 W phase which does not exceed 16% is noted and which is evidence of the incomplete cation exchange process. In addition, the quite important dominance of the 1 W hydration phase (about 90%) is noted. The last sample (pH=11; T=90°C) has another intermediate phase 0 W/1 W which explain the observed decrease in basal distance probably resulting in the shrinkage of IS as a result of the temperature increase. The quality agreements obtained between the theoretical and experimental profiles are in average of ~5% which is generally acceptable.


### 3.5. Evolution of the Water Molecule Abundances versus Coupling Constraint Strength

#### 3.5.1. Evolution of the nH2O Amounts versus Constraint Strength

The delicate theoretical determination of nH2O amounts for each studied sample is deduced from the results of thermogravimetry/differential thermal analysis (TG/DTA) (Figure S1) and summarized in Table 8.Table 8
Results from TG/DTA analyses in the case of samples SWy-Co, SWy-Cu, and SWy-Ba.
Samplesminitial (mg)Δm (mg)SWy-CopH=3; T=50°C15.9009.974pH=5; T=60°C16.6013.387pH=7; T=70°C06.8001.820pH=9; T=80°C17.1011.074pH=11; T=90°C12.3008.605SWy-CupH=3; T=50°C17.5012.975pH=5; T=60°C17.4014.246pH=7; T=70°C15.7012.836pH=9; T=80°C11.3006.972pH=11; T=90°C14.0010.848SWy-BapH=3; T=50°C15.0006.773pH=5; T=60°C23.6019.570pH=7; T=70°C15.0006.731pH=9; T=80°C15.4003.501pH=11; T=90°C19.1012.462Notes:minitial: initial mass of the samples before analysis; Δm: change in mass during analysis.Regardless of the sample type, the hydration state is governed by the cationic nature, the layer charge value, and the layer charge location [5–7, 107, 108, 120–122]. All samples studied belongs to the Wyoming montmorillonite specimen characterized by the same layer charge and the charge location value. The nature of the exchangeable cations and the external stresses applied to the cation exchange process (first-order coupling constraint) is at the origin of these specific water molecule amounts fluctuations. The water affinity of the exchangeable cation is related to the ionic potential which is defined by the ratio of the valence of the cation to its ionic radius [110] (Table 9). As this potential increases, the cation’s affinity for water also increases. Indeed, bivalent cations such as cobalt (Co2+), copper (Cu2+), and barium (Ba2+) have a high affinity of water translated by a 2 W hydration state [6, 7]. Unlike monovalent cations like sodium (Na+), having a low affinity for water mainly generates monohydrated states 1 W.Table 9
Radius and ionic potential of some cations [110].
CationsIonic potential (eV)Ionic radius (Å)Na+1.050.95Ba2+1.481.35Cu2+2.740.73Co2+3.080.65Based on the quantitative XRD analysis, a discretization of the content of the IS is carried out. Indeed, the evolution of nH2O molecules per half-cell, relative to the constraint strength, is described by Table 10 and represented in Figure 9. For all series, a decrease in the water molecules amounts as a function of the increase in temperature and soil solution pH.Table 10
Evolution of the nH2O amounts versus constraint strength for samples SWy-Co, SWy-Cu, and SWy-Ba.
SamplesPhasesSaturationmmolar (g/mol)MnH2O% Na+% M2+SWy-CopH=3; T=50°CPhase 11000370.864050.0442Phase 216.6883.28379.250100.0865pH=5; T=60°CPhase 11000370.864050.0322Phase 216.7083.30379.248100.0630pH=7; T=70°CØ3565377.406080.0833pH=9; T=80°CØ3070377.909070.0686pH=11; T=90°CØ3070377.909070.0327SWy-CupH=3; T=50°CPhase 19505371.432140.1228Phase 29505371.432040.0351pH=5; T=60°CPhase 18515372.568140.0937Phase 28515372.568040.0268pH=7; T=70°CØ7525373.703100.0546pH=9; T=80°CØ7030374.271080.0358pH=11; T=90°CØ7030374.271080.0406SWy-BapH=3; T=50°CPhase 110000370.864120.1001Phase 29000374.066060.0496pH=5; T=60°CØ8416375.988100.1164pH=7; T=70°CØ9505372.465120.0995pH=9; T=80°CPhase 110000370.864130.0611Phase 28020377.267130.0252pH=11; T=90°CØ1585398.076130.0750Notes: phases: modeling phase of each sample; Ø: absence of phases;mmolar: molar mass of the sample related to each phase; 4: average number of layers per stack; nH2O: number of water molecules per half-cell bound to each phase.Figure 9
nH2O abundance fluctuation as a function of stress strength for SWy-Co, SWy-Cu, and SWy-Ba samples (black scatter). Red scatter: the used linear and Lorentz fit function, respectively.In the case of SWy-Co sample (Figure9), there is an overall linear decrease in the number of water molecules as a function of the increase applied stresses intensity (pH=3; T=50°C⟶pH=11; T=90°C). Using a linear regression approach, a mathematical equation was developed. The behavior and evolution of the nH2O abundance fluctuation re described by the following function:
(4)y=0.14888−0.02226.x,where y is the nH2O abundance fluctuation, and x is the applied stress intensity.In the case of SWy-Cu and SWy-Ba samples (Figure9), there is a nonlinear water molecule amount decrease unlike SWy-Co as a function of the increase in external stresses applied. So, a regression approach based on the Lorentz equation was adopted to fit this evolution. This variation is described by function below:
(5)y=y0+2Aп×w4x−xc2w2,where y0 is the baseline offset, xc is the center of the peak, w equals the width of the peak at half height, and A is the area under the peak. The parameters of the used Lorentz function are presented in Figure 9.This decrease trends on the water molecule amount (nH2O) versus constraint strength are predictable when increasing temperature which automatically affects the IS closing and subsequently, it affects the cation exchange capacity of the mineral.


#### 3.5.2. Individual Evolution of the 0 W, 1 W, and 2 W Abundances versus Constraint Strength

The “water footprint” schematized on FigureS2 shows the coexistence within the particle of several phases with different weights. The variation of the cation exchange process makes it possible to better understand the structural response of the starting material (such as fluctuations in basal distance d001, FWHM, crystalline size, rationality ξ, average number of layers M, and mode of stacking layers). Understanding the CEC functioning mode is closely related to the discretization of hydration states [48].For SWy-Co samples, a decrease in the 1 W monohydrate state, accompanied by an increase in fluctuation for the 2 W hydration state, represents the main hydration behavior. This can be interpreted by an easy intercalation of the compensating cations (Co2+) in IS more and more, replacing the sodium cations (Na+) that will leave the structure partially according to the applied stress variation. This hypothesis is confirmed by the global incomplete exchange process despite the exchange equilibrium time provided and remains to be noted that abundances in the aqueous phase are normalized to 100%. For SWy-Cu samples, the same behavior of the previous sample (SWy-Co) is observed. A slight fluctuation for the 1 W hydration state followed by a slow increase of 2 W is noted. For the latest SWy-Ba samples, the water behavior is almost different. There is a slow decrease in the 1 W state. This fluctuation is accompanied by a slight increase of 2 W phases. This is not valid for the complex pH=11 and T=90°C (extreme case) which has a minority anhydrate state of 0 W (15%) and a majority hydration state of 1 W (85%). The abundance of individual layer type deduced from the optimized theoretical MLS used to reproduce experimental XRD profiles was shown in Figure S3. Indeed, the 2 W hydration state is the most dominant phase in the entire SWy-Co series. Unlike the two complexes SWy-Cu and SWy-Ba, the 1 W hydration state is the most dominant phases.


### 3.6. Evolution of the Average Number of Layers versus Constraint Strength

The average number of layers (M) is a very important parameter in the crystal structure clay response when studied by XRD analysis. It has a direct influence on the 001 reflections of the theoretical and experimental models. For the low M value, the reflections 001 will be very wide with elevated value of FMWH and vice versa. The evolution of M parameter for all SWy-Co, SWy-Cu, and SWy-Ba samples is shown in Figure 10.Figure 10
Average number of layersM evolution versus constraint strength in the case of SWy-Co, SWy-Cu, and SWy-Ba samples (black scatter). Red scatter: the used Boltzmann fit.The SWy-Ba sample is the exception and exhibits growth ofM when increasing intensity constraint. The M evolution as a function of the applied stress applied is fitted for each sample and shown in Figure 10.The evolution ofM for all complexes following a Boltzmann function is shown below:
(6)y=A2+A1−A21+ex−x0/dx,where A1 is the initial value, A2 is the final value, x0 is the center, and dx is a time constant.All functions parameters are summarized in Figure10.


### 3.7. Evolution of the Layer Stacking Modes

A mapping representation of the hydration state in the case of SWy-Co, SWy-Cu, and SWy-Ba samples via XRD modeling profile approach is summarized in Figure11. The light brown, caramel, and dark brown colors represent the 0 W, 1 W, and 2 W layer type, respectively. Each line thus represents a layer with its intrinsic hydration state. The configuration considered here is an optimal configuration (best agreement obtained) extracted from the best agreements obtained between theoretical and experimental XRD profile. For SWy-Co complexes, the correlation between partial and total segregation stacking is observed. Thus, for SWy-Cu samples, we notice that the total segregation aspect is present regardless of the applied constraint applied. On the other hand, the SWy-Ba series shows the existence of two modes of stacking, segregation accompanied by partial order, with blatant dominance for segregated stacking.Figure 11
Mapping representation of the hydration state in the case of SWy-Co (a), SWy-Cu (b), and SWy-Ba (c) samples via XRD modeling approach.
(a)(b)(c)


### 3.8. BET and BJH Pore Size Distribution Analysis

The exploitation of the results obtained from the structural analysis by XRD modeling approach demonstrates a variability, in term of population, within the same crystallite. This directly influences the internal and external layers surfaces, which subsequently affects the adsorption properties and the sample porosity. Our objective is to evaluate the effect of the applied coupling disturbance (pH andT°C) on these properties. Indeed, we are looking for a link between structural damage, the intrinsic properties of the sample, and the saturation of the CEC. For that, a study based on BET adsorption measurement and BJH pore size distribution analysis is directed. Both the single-point and multipoint BET methods based on the surface area (SA) purpose from nitrogen isotherms were approved to evaluate external layer surface perturbation [41, 123–131] (Figure 12). Average pore diameter is determined using the BJH method (Figure 13). Whatever the nature of the exchangeable cation, an increase in the SA values is shown as a function of the constraint intensity up to a pH=9 and a T=80°C. After this limit value, a behavior divergence is shown. In fact, for the two samples saturated, respectively, by Co and Cu cations, a decrease in the SA values is observed against the continuous growth in the case of the Ba cation.Figure 12
SABET single and multipoint BET evolution versus constraint strength for (a) SWy-Co, (b) SWy-Cu, and (c) SWy-Ba samples.
(a)(b)(c)Figure 13
BJH method average pore diameter evolution versus constraint strength.The average pore diameter evolution versus constraint strength (Figure13) can provide a preliminary explanation for the observed SA fluctuations.For all samples, the limit of mesoporosity domain is respected (where pores whose maximum diameter is between 2 and 50 nm). Indeed, the SWy-Ba sample practically keeps the same average pore diameters values up topH=11 and T=90°C. However, the other two samples are marked by a considerable increase in the average pore diameter, which probably indicates a transformation that affected the internal configuration of the clay particle. This agrees with the results obtained from XRD analysis focusing the evolution of the average number of layers versus constraint strength.Obtained nitrogen adsorption (ADS)-desorption (DES) isotherms curves shape (Figure14) shows a very closer type II isotherm classification [127–131]. This allocation confirms the supremacy of the mesoporous texture despite the fluctuations observed and the nature of the exchangeable cation. The relative large pore size obtained in the case of stressed SWy-Ba sample is explained by the coupling of three essential parameters, respectively, the acidic or basic nature of the soil solution, the intrinsic hydration property, and the nature of the exchangeable cation. The Ba2+ ions exchange promotes the exfoliation process and thereafter increases the porosity degree.Figure 14
Nitrogen adsorption (ads)-desorption (des)-isotherms in the case of SWy-Co, SWy-Cu, and SWy-Ba.To overcome the limits of SA analysis (i.e., nitrogen can only cover external surfaces and does not interact with internal surfaces), since it cannot access the information in the volume of the sample and subsequently, it does not provide information on the IS configurations/changes, a pore size distribution (PSD) analysis imposes itself. The application of PSD analysis requires technical approaches such as (i) the volumes of micropores, mesopores, and macropores including nanopores in one gram solid labeled, respectively,VMi, VMe, and VMa (all in mL/g) and (ii) the effects related to macroporosity are neglected assuming that they do not affect the properties of adsorption and the specific micromesopore volumes (V=VMi+VMe) that is determined using the desorption data (at the relative equilibrium pressure P/P0). Fundamental approximations used for the PSD analysis target the shape and characteristics of the pores. Indeed, cylindrical shape (with radius (r) approximately half of its width) is adopted. Also, cylindrical mesopores are characterized by r radii which correspond to V values (calculated from the corrected Kelvin equation using P/P0 values).The PSD plots provide information on the variation of the cumulative pore volume versus pore radius (V-r) (Figure 15). Although they have the same trend, the V-r curves relating to each sample present specificities showing the effect of the applied stress on the evolution of the porosity. In the case of SWy-Co sample and from a diameter of 4 nm, an evolution divergence appears with a “gap” in favor of high pH and T°C value which reaches 0.086 mL/g (Figure 15). The V-r variation divergence proves, initially, the achievement of the cation exchange process which is confirmed by an individual comportment of the V-r curves despite having the same appearance. In addition, a direct effect of the increase of the applied stresses appears as an increase in the V-r “gap.” For SWy-Ba, the maximum cumulative pore volume is 0.062 mL/g attained at pH=9 and T=80°C. The major remark concerns the last two values of pH and T. Indeed, although they present a very similar appearance to the other V-r characteristic curves, there is a jump (“gap”) of 0.015 mL/g attributed to the acid-base transformation. In the case of SWy-Cu, the V-r curves have respected the same shape as for the other samples, but the maximum value did not exceed 0.069 mL/g. The common behavior for the three samples lies in the existence of a cumulative pore volume “gap” observed during the acid-base transformation. The value of this gap is practically very similar and close for all samples, and it averages around 0.016 mL/g. This variation is consistent with the XRD modeling profile which predicts layer exfoliation and presence of highly hydrated rate.Figure 15
The pore size distribution (PSD) curve for the different studied samples (V-r) in the case of SWy-Co, SWy-Cu, and SWy-Ba.The derivative pore size distribution curve (Figure16) confirms the prevailing mesoporosity with a pore diameter concentration varying between 2.20 and 9.89 nm. A concentration of large pore populations related to the saturated Co2+ sample (at pH=11 and T=90°C) is observed. This agrees with the obtained SA results and XRD analysis. The V-r curve radius derivative for all samples is given in Figure 16. For the rest of the studied samples, an almost similar variation is observed except for SWy-Ba (pH=11/T=90) which presents an extremum around 4.01 nm with a small extent.Figure 16
The derivative pore size distribution curve.


## 3.1. Semiquantitative XRD Investigation of the Baseline Samples

The experimental XRD profile of the starting SWy-Na complex (Figure5) shows three characteristic reflections (n=1, 2, and 4). The first reflection (001) is located at 2θ=7.16° (d001=12.33Å) probably indicating a hydration 1 W state (Table 4). By calculating the FWHM and ξ parameter value, the homogeneous observed character is confirmed [111, 112]. This result is consistent with the results of [48] on the same sample. Na-rich montmorillonite (SWy-Na) has been studied extensively before since it is considered a reference sample [5–7, 41, 48, 78–79, 89, 113]. At this level, our goal is to refine the obtained literature results related to the SWy-Na sample. For the SWy-Cu, SWy-Co, and SWy-Ba samples, qualitative and quantitative XRD results extracted from the same authors earlier works [47, 97] are used (Tables 4 and 5).Figure 5
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Na.∗Halite (NaCl).Table 4
Qualitative XRD investigation in the case of the samples SWy-Na, SWy-Co, SWy-Cu, and SWy-Ba [47, 97].
Sample2θ°d001 (Å)FWHM (2θ°)D (Å)ξ (Å)CharacterSWy-Na7.1612.330.7418.770.062HomogeneousSWy-Co [47]5.8614.880.7119.550.520InterstratifiedSWy-Cu [47]7.1412.360.6122.770.100HomogeneousSWy-Ba [91]5.9114.941.5508.960.970InterstratifiedNotes: 2θ°: Bragg’s angle; d001: basal distance of the 1st reflection; D: average crystalline size; FWHM: full width at half maximum; ξ: rationality deviation parameters.Table 5
Optimum structural parameters used for modeling XRD profiles in the case of baseline samples [47, 97].
Sample% MLSd001nH2OWAPAASMMRWP (%)SWy-Na8010.500.800.85R1−seg102.272012.52SWy-Co [47]1612.41.10.160.30R1−seg84.258415.21.9SWy-Cu [47]9512.41.10.950.05R1−seg83.820515.21.9SWy-Ba [91]6412.41.10.150.15R083.7715.21.93612.41.10.650.77R1−seg15.22.0Notes:d001: interlamellar distance; nH2O: number of water molecules per half-cell; zH2O: position of the molecules along the c∗ axis of the H2O molecule is attached to 9.6 Å for hydration states 1 W. The position of the exchangeable cations per half-cell calculated along the axis c∗ is fixed à 9.6 Å for hydration states 1 W [41]. M: average number of sheets per stack; SM: layer stacking mode; R0: maximum order; R1: random stacking; R1−X, associated stacking (segregation-partial order); C: characters; Ho: homogeneous; He: heterogeneous; RWP: confidence factor.


## 3.2. Modeling of XRD Profiles in the Case of SWy-Na Sample

The mixed layer structure (MLS) used to achieve the best agreement between the experimental and calculated XRD model (Figure5) shows an heterogeneous hydration character that results in the coexistence of two types of layers (0 W and 1 W) with a strong dominance for the 1 W phase at about 80%. This opposes the obtained qualitative description.Indeed, the distribution of IS water molecules has respected the previous work [5, 6, 48, 88, 101] with a water sheet located in the middle of the IS for 1 W phase and the absence of water in the IS for the dehydrated state 0 W. Regardless of the type of hydration state, the exchangeable cations Na (per half-cell unit) are positioned in the center of the IS along the c∗ axis respecting the configuration of the data provided by the literature [5, 48]. The average number of layers per crystallite M is equal to 10. The confidence factor RWP is very low (2.27%), which reflects the high quality of fitting. The structural parameters are summarized in Table 5.


## 3.3. Semiquantitative Description of XRD Analysis after Applying First-Order Coupling Stress

### 3.3.1. Case of the SWy-Co Sample

The experimental XRD results for the SWy-Co samples obtained are shown in Figure6. For the first three constraint coupling levels (pH=3; T=50°C⟶pH=7; T=70°C), there is an asymmetry for the main 001 reflections located at 6.1 in 2θ° with d001~ 14.5 Å synonymous of a minor 2 W hydration state presence attributed to the Co2+ cation in IS. Also, a shoulder towards the wide angles around in 7.2° in 2θ (d001~ 12.3 Å) attributed to the existence of the sodium residue resulting from the starting sample. Generally, the observed asymmetric 001 reflections indicates the coexistence of several hydration states within the crystallite and/or a partial cation exchange process. The values of the FWHM and ξ parameters confirms this idea (Table 6).Figure 6
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Co.Table 6
Qualitative XRD investigation in the case of the samples SWy-Co SWy-Cu and SWy-Ba.
Samples2θ°d001 (Å)FWHM (2θ°)D (Å)ξ (Å)CharactersSWy-CopH=3; T=50°C06.2214.201.2710.930.563InterstratifiedpH=5; T=60°C06.2414.151.1811.770.653pH=7; T=70°C06.0914.501.0013.890.406pH=9; T=80°C06.0714.551.9307.190.109pH=11; T=90°C∗∗∗∗∗SWy-CupH=3; T=50°C07.1612.340.6122.770.016HomogeneouspH=5; T=60°C07.0312.570.7119.570.096pH=7; T=70°C07.0812.481.7407.980.114InterstratifiedpH=9; T=80°C07.0612.511.9707.050.207pH=11; T=90°C07.0012.622.1406.490.270SWy-BapH=3; T=50°C07.1812.300.7019.850.055HomogeneouspH=5; T=60°C07.1412.371.3010.690.013InterstratifiedpH=7; T=70°C07.2012.270.5525.260.091HomogeneouspH=9; T=80°C07.1812.300.6820.430.216pH=11; T=90°C07.3512.020.5724.380.064Notes:∗absence of the 001 reflection.In Table6, for the rest of the samples, a different hydration behavior was observed. The diffracted intensity ratio I001/I002, I001/I003, and I001/I004 of the complex studied under (pH=9, T=80°C/pH=11, T=90°C) decreases if compared with the three first studied samples. Also, a drastic decrease in the 001-reflection intensity is observed in both samples and which probably indicates a bottom transformation that affected the structure when increasing constraints strength. This strange structural behavior finds an explanation by the effect of the increase in temperature and the basic aspect of the soil solution pH on the cohesion energy between layers and even destruction of the chemical bonds within octahedral and tetrahedral sheet forming the layer. The main structure is affected and an elevated layer’s exfoliation trends within the crystallites favoring a total transformation of the original 2 : 1 phase to a 1 : 1 clay structure that was established. The raised value of the 002-reflection intensity and the absence of the 001 line can be interpreted in this case by the beginning of a great structural transformation. This remains to be proven by quantitative XRD analysis and by studying the porosity evolution of these two samples.


### 3.3.2. Case of the SWy-Cu Sample

The experimental XRD models, in the case of SWy-Cu, obtained by varying the external constraint strength are summarized in Figure7. For the first two constraints of the coupling value (pH=3; T=50°C and pH=5; T=60°C), the experimental XRD models are almost identical with a low FWHM value (Table 6) indicating probably either the coexistence, within the stacks, of several hydration states [77] or an unfinished (partial) cation exchange, knowing that Cu2+ cation is indistinguishable from the starting sodium by simple XRD analysis at room conditions from the starting sodium cation [47]. All qualitative parameters are summarized in Table 6. For the rest of the complexes (pH=7; T=70°C⟶pH=11; T=90°C), a stack towards the small angles (5.9°⟶15Å) appeared and ascribed to the material response to the applied stress. Indeed, a beginning of 2 W transition, without a real domination, is confirmed by increasing the coupling constraint intensity. It remains to be noted that the higher-order peaks have a relatively low intensity regardless surrounding environment change and from soilsolutionpHvalue=7 and temperature T=70°C, an abrupt structural change is observed.Figure 7
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Cu.


### 3.3.3. Case of the SWy-Ba Sample

The experimental XRD profiles of SWy-Ba sample are reported in Figure8. An intense 001 reflection situated at 7.2° (2θ) (d001~ 12.3 Å) indicating a 1 W hydration state dominates all sample. This probably reflects the existence of a Na+ residue originating from the starting sample or from added NaOH solution used to balance the pH solution. This opposes the earlier results [41, 97] on cation exchange in the case of Ba2+ which demonstrate a 2 W hydration state behavior.Figure 8
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Ba.ForpH=5/T=60°C, the XRD profile shows a shoulder towards the low angles (5.8°⟶d001=15.23Å) with an increase in the FWHM and ξ parameter value indicating the 2 W hydration state transition beginning. Also, it can be interpreted by the coexistence, within the stacks, of several states of hydration [77] or an unfinished (partial) cation exchange knowing that the barium hydrate baseline to two layers of water 2 W (15 Å). All qualitatively estimated parameters are summarized in Table 6.


## 3.3.1. Case of the SWy-Co Sample

The experimental XRD results for the SWy-Co samples obtained are shown in Figure6. For the first three constraint coupling levels (pH=3; T=50°C⟶pH=7; T=70°C), there is an asymmetry for the main 001 reflections located at 6.1 in 2θ° with d001~ 14.5 Å synonymous of a minor 2 W hydration state presence attributed to the Co2+ cation in IS. Also, a shoulder towards the wide angles around in 7.2° in 2θ (d001~ 12.3 Å) attributed to the existence of the sodium residue resulting from the starting sample. Generally, the observed asymmetric 001 reflections indicates the coexistence of several hydration states within the crystallite and/or a partial cation exchange process. The values of the FWHM and ξ parameters confirms this idea (Table 6).Figure 6
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Co.Table 6
Qualitative XRD investigation in the case of the samples SWy-Co SWy-Cu and SWy-Ba.
Samples2θ°d001 (Å)FWHM (2θ°)D (Å)ξ (Å)CharactersSWy-CopH=3; T=50°C06.2214.201.2710.930.563InterstratifiedpH=5; T=60°C06.2414.151.1811.770.653pH=7; T=70°C06.0914.501.0013.890.406pH=9; T=80°C06.0714.551.9307.190.109pH=11; T=90°C∗∗∗∗∗SWy-CupH=3; T=50°C07.1612.340.6122.770.016HomogeneouspH=5; T=60°C07.0312.570.7119.570.096pH=7; T=70°C07.0812.481.7407.980.114InterstratifiedpH=9; T=80°C07.0612.511.9707.050.207pH=11; T=90°C07.0012.622.1406.490.270SWy-BapH=3; T=50°C07.1812.300.7019.850.055HomogeneouspH=5; T=60°C07.1412.371.3010.690.013InterstratifiedpH=7; T=70°C07.2012.270.5525.260.091HomogeneouspH=9; T=80°C07.1812.300.6820.430.216pH=11; T=90°C07.3512.020.5724.380.064Notes:∗absence of the 001 reflection.In Table6, for the rest of the samples, a different hydration behavior was observed. The diffracted intensity ratio I001/I002, I001/I003, and I001/I004 of the complex studied under (pH=9, T=80°C/pH=11, T=90°C) decreases if compared with the three first studied samples. Also, a drastic decrease in the 001-reflection intensity is observed in both samples and which probably indicates a bottom transformation that affected the structure when increasing constraints strength. This strange structural behavior finds an explanation by the effect of the increase in temperature and the basic aspect of the soil solution pH on the cohesion energy between layers and even destruction of the chemical bonds within octahedral and tetrahedral sheet forming the layer. The main structure is affected and an elevated layer’s exfoliation trends within the crystallites favoring a total transformation of the original 2 : 1 phase to a 1 : 1 clay structure that was established. The raised value of the 002-reflection intensity and the absence of the 001 line can be interpreted in this case by the beginning of a great structural transformation. This remains to be proven by quantitative XRD analysis and by studying the porosity evolution of these two samples.


## 3.3.2. Case of the SWy-Cu Sample

The experimental XRD models, in the case of SWy-Cu, obtained by varying the external constraint strength are summarized in Figure7. For the first two constraints of the coupling value (pH=3; T=50°C and pH=5; T=60°C), the experimental XRD models are almost identical with a low FWHM value (Table 6) indicating probably either the coexistence, within the stacks, of several hydration states [77] or an unfinished (partial) cation exchange, knowing that Cu2+ cation is indistinguishable from the starting sodium by simple XRD analysis at room conditions from the starting sodium cation [47]. All qualitative parameters are summarized in Table 6. For the rest of the complexes (pH=7; T=70°C⟶pH=11; T=90°C), a stack towards the small angles (5.9°⟶15Å) appeared and ascribed to the material response to the applied stress. Indeed, a beginning of 2 W transition, without a real domination, is confirmed by increasing the coupling constraint intensity. It remains to be noted that the higher-order peaks have a relatively low intensity regardless surrounding environment change and from soilsolutionpHvalue=7 and temperature T=70°C, an abrupt structural change is observed.Figure 7
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Cu.


## 3.3.3. Case of the SWy-Ba Sample

The experimental XRD profiles of SWy-Ba sample are reported in Figure8. An intense 001 reflection situated at 7.2° (2θ) (d001~ 12.3 Å) indicating a 1 W hydration state dominates all sample. This probably reflects the existence of a Na+ residue originating from the starting sample or from added NaOH solution used to balance the pH solution. This opposes the earlier results [41, 97] on cation exchange in the case of Ba2+ which demonstrate a 2 W hydration state behavior.Figure 8
Best agreement between theoretical and experimental XRD profiles obtained in the case of SWy-Ba.ForpH=5/T=60°C, the XRD profile shows a shoulder towards the low angles (5.8°⟶d001=15.23Å) with an increase in the FWHM and ξ parameter value indicating the 2 W hydration state transition beginning. Also, it can be interpreted by the coexistence, within the stacks, of several states of hydration [77] or an unfinished (partial) cation exchange knowing that the barium hydrate baseline to two layers of water 2 W (15 Å). All qualitatively estimated parameters are summarized in Table 6.


## 3.4. XRD Modeling Profiles after Applying First-Order Coupling Stress

### 3.4.1. Case of the SWy-Co Samples

The qualitative XRD analysis suggested heterogeneous hydration behavior for SWy-Co samples, regardless of the strength of the stresses applied. This interstratification has been approved by the 001 reflection modeling approach which assumes the coexistence of two different hydration states (e.g., 1 W and 2 W). To improve the agreement between the calculated and experimental models (Figure6) and for each constraint strength from pH=5/T=60°C towards pH=11/T=90°C, the proposed MLS is theoretically decomposed into two layer populations type (i.e., 1 W: d001~ 12.2 Å and 2 W: d001~ 15.2 Å) stacked according to specific succession probability laws. The structural parameters associated with this modeling approach are summarized in Table 7. The proposed MLS is obtained by weighted layer populations that are tolerated to have an identical chemical composition, identical layer thickness, and identical z-atoms coordinates [40, 48]. The CEC of the results is partially saturated by the Na+ and Co2+ cations since, under ambient conditions, sodium always has a hydration state of 1 W [41, 48], and cobalt has a hydration state of 2 W.Table 7
Structural parameters of SWy-Co, SWy-Cu, and SWy-Ba.
Samples% MLSxW-echa.catd001nH2OWAPAASMMMtotRWPSWy-CopH=3; T=50°C16.681 W-Na12.20.044211R00593.6183.281 W-Na12.20.03460.400.55R1−seg102 W-Co15.20.02590.0259pH=5; T=60°C16.701 W-Na12.20.032211R00593.7983.301 W-Na12.20.02520.400.55R1−seg102 W-Co15.20.01890.0189pH=7; T=70°C351 W-Na12.20.02300.350.63R1−seg0883.42652 W-Co15.20.03000.0300pH=9; T=80°C401 W-Na12.20.02000.400.40R00777.45602 W-Co15.20.02430.0243pH=11; T=90°C401 W-Na12.20.01010.400.40R00779.12602 W-Co15.20.01130.0113SWy-CupH=3; T=50°C81.231 W-Na12.20.11660.950.95R014123.842 W-Cu15.20.00310.003118.771 W-Na12.20.03330.950.95R0042 W-Cu15.20.00090.0009pH=5; T=60°C84.201 W-Na12.20.07970.850.86R1−seg14123.562 W-Cu15.20.00700.007015.801 W-Na12.20.02280.850.86R1−seg042 W-Cu15.20.00200.0020pH=7; T=70°C751 W-Na12.20.04100.750.90R1−seg10104.92252 W-Cu15.20.00680.0068pH=9; T=80°C701 W-Na12.20.02500.700.87R1−seg0886.04302 W-Cu15.20.01480.0148pH=11; T=90°C701 W-Na12.20.02840.700.87R1−seg0887.73302 W-Cu15.20.00610.0061SWy-BapH=3; T=50°C72.171 W-Na12.20.100111R012105.4127.831 W-Na12.20.04460.900.89R1−p.ord062 W-Ba15.20.00450.0045pH=5; T=60°C841 W-Na12.20.09780.840.91R1−seg10105.96162 W-Ba15.20.00930.0093pH=7; T=70°C951 W-Na12.20.09050.950.97R1−seg12125.22052 W-Ba15.20.00450.0045pH=9; T=80°C65.751 W-Na12.20.061111R013135.3734.251 W-Na12.20.02020.800.85R1−seg132 W-Ba15.20.00250.0025pH=11; T=90°C150 W-Na10.20.00000.850.83R1−p.ord13135.16851 W-Ba12.20.0750Notes: xW-echa.cat: layer type and associated exchangeable cation;d001: interlamellar distance; nH2O: number of water molecules per half-cell; zH2O: position of the molecules along the c∗ axis of the H2O molecule is attached to 9.6 Å and 11.3 Å–13.9 Å for hydration states 1 W and 2 W, respectively. The position of the exchangeable cations per half-cell calculated along the axis c∗ is fixed with 9.60 Å and 12.25 Å for hydration states 1 W and 2 W [41]; n-echa.cat: number of exchangeable cations per half-cell is set to 0.28 (for the cation Na+) and at 0.14 (for bivalent metal cations), indicating complete saturation of cation exchange capacity (CEC); M: average number of sheets per stack; Mtot, total average number of sheets per stack; SM: layer stacking mode; R0: maximum order; R1: random stacking; R1−X: associated stacking (segregation-partial order); C: characters; Ho: homogeneous; He: heterogeneous; RWP: confidence factor.The theoretical decomposition of the SWy-Co sample, (pH=11; T=90°C) which has undergone fundamental changes in its basic structure, can be followed by two major hypotheses:The 1st consists in considering that it is still a T-O-T type structure despite the absence of the main 001 reflection which must be positioned around 6.1° (2θ) (d001~ 14.5 Å) and can be attenuated (is no longer sensitive to X-rays during diffractogram recordings) following the increase in the applied stress strength. In this case, a theoretical model based on the heterogeneous mixed 1 W/2 W structure with a major domination for the phase 2 W was adopted with very low average layer number per crystallite. This hypothesis can be practically verified for the good agreement towards higher diffraction orders.The 2nd considers that the basic clay structure has been strictly modified following the coupled increase in temperature T and the soil solution pH during the cation exchange process. This supposition is justified through the destruction of chemical bonds within the crystallite and/or which give rise to a new structure derived from smectite. This result, despite its originality, agrees with the work of [108, 109] which focuses on the hydrothermal synthesis of zeolite from clay minerals by controlling the pH effect on the synthesis process. Hence, the transition from a T-O-T phyllosilicate type (montmorillonite) to another kaolinite T-O phyllosilicate type is probabilistic, knowing that kaolinite has a dioctahedral structure [114–116]. Its structural half-cell formula is defined by (Si4 Al4 O10 (OH)8), whose basal distance d001 is of the order of 7 Å [117–119] with a closed IS accompanied by the absence of isomorphic substitutions (not CC in the middle of IS). For this hypothesis (Figure 6), we consider that the first reflection (in the 1st hypothesis was considered as 2nd reflection 002) is positioned around 12° (2θ) (d001~ 7 Å) from where the second reflection is necessarily positioned around 24° (2θ) (Table 7). For this hypothesis, we note the presence of a relatively intense reflection around 18° (2θ). A rational reflection position is obtained for the three reflections order (12°⟶18°⟶24°). Also, the exchangeable cation has no place in this configuration, which even calls into question the cation exchange process. Therefore, the first supposition seems more scientifically logical. The 1st hypothesis has been adopted in the rest of the calculations. It remains to be noted that the quality of the fitting is controlled by the RWP parameter.


### 3.4.2. Case of the SWy-Cu Samples

The best agreement between theoretical and experimental XRD patterns (Figure7) of the SWy-Cu samples is obtained using an interstratified structure of two MLS comprising various relative layers proportions with different hydration states (Table 7). This variability confirms the heterogeneous hydration character and the intermediate 1 W-2 W hydration phase observed regardless of the intensity of the applied constraints. In detail, a minor contribution of the 2 W phase increases from 5% to 30% by increasing the intensity of the external applied stress (pH=3; T=50°C⟶pH=11; T=90°C). Indeed, the 2 W hydration phase implemented in the theoretical model is necessarily attributed to the layer fraction whose CEC is saturated by Cu2+. This weighting fluctuation is evidence of an incomplete cation exchange process (d001<15Å). On the other hand, the dominance of 1 W layer hydration phase is interpreted by the existence of a fraction (quite large) regardless of the applied constraints applied. This contribution is attributed to the sodium residues from the starting sample (SWy-Na).The agreements obtained between the experimental and theoretical profiles (RWP~3% to 8%) are generally acceptable (< 10%), despite the misfit observed after widening the peaks around 14° and 28° (2θ). In fact, this disagreement can be broken down into a good reflection position agreement and a disagreement of diffracted intensity related to the input fluctuation of the distribution and abundance of water molecules in the IS. This disagreement led us to explore wide-angle areas, later to establish a possible link between CEC saturation and the degree of hydration heterogeneity.The logical increase of theRWP factor in the case of SWy-Cu sample reflects the increase in the heterogeneity’s degree defined, respectively, by an asymmetry of the first 001 reflections, the high FWHM value, and the ξ rationality parameter. Theoretically, this result is related to the variability of possible MLS configurations allowing a good fit of the 001 reflection. The exploitation of the WA, PAA, M, and RWP values allowed us to characterize a specific distribution of the n normalized layers within the crystallites according to the generated stacking modes and the contribution of each phase. This statistical representation of the layer can help to understand the CEC sensitivity fluctuation (of the starting sample) following the variation in the temperature T and pH during the cation exchange process.


### 3.4.3. Case of the SWy-Ba Samples

For SWy-Ba samples, the best agreements between theoretical and experimental models are shown in Figure8. The main structural parameters used to achieve a good fit are summarized in Table 7. For each model, several types of layers with variable stacking mode are used to improve the agreement obtained between the experimental and calculated models. This MLS is composed by several layers of type populations depending on the hydration state (0 W, 1 W, and 2 W) whose basal distance d001 is equal to 10.2 Å, 12.2 Å, and 15.2 Å, respectively. This variability confirms the heterogeneous hydration character observed by qualitative XRD analysis for the entire SWy-Ba series (pH=3; T=50°C⟶pH=11; T=90°C) with a major dominance for the 1 W hydration phase saturated by Na+ cation assigned to the starting sample. In addition, the 2 W phases are assigned to the fraction whose CEC is saturated by Ba2+ cation [41]. More specifically, for the first four samples from pH=3/T=50°C towards pH=9/T=80°C, an omnipresent minor contribution of the 2 W phase which does not exceed 16% is noted and which is evidence of the incomplete cation exchange process. In addition, the quite important dominance of the 1 W hydration phase (about 90%) is noted. The last sample (pH=11; T=90°C) has another intermediate phase 0 W/1 W which explain the observed decrease in basal distance probably resulting in the shrinkage of IS as a result of the temperature increase. The quality agreements obtained between the theoretical and experimental profiles are in average of ~5% which is generally acceptable.


## 3.4.1. Case of the SWy-Co Samples

The qualitative XRD analysis suggested heterogeneous hydration behavior for SWy-Co samples, regardless of the strength of the stresses applied. This interstratification has been approved by the 001 reflection modeling approach which assumes the coexistence of two different hydration states (e.g., 1 W and 2 W). To improve the agreement between the calculated and experimental models (Figure6) and for each constraint strength from pH=5/T=60°C towards pH=11/T=90°C, the proposed MLS is theoretically decomposed into two layer populations type (i.e., 1 W: d001~ 12.2 Å and 2 W: d001~ 15.2 Å) stacked according to specific succession probability laws. The structural parameters associated with this modeling approach are summarized in Table 7. The proposed MLS is obtained by weighted layer populations that are tolerated to have an identical chemical composition, identical layer thickness, and identical z-atoms coordinates [40, 48]. The CEC of the results is partially saturated by the Na+ and Co2+ cations since, under ambient conditions, sodium always has a hydration state of 1 W [41, 48], and cobalt has a hydration state of 2 W.Table 7
Structural parameters of SWy-Co, SWy-Cu, and SWy-Ba.
Samples% MLSxW-echa.catd001nH2OWAPAASMMMtotRWPSWy-CopH=3; T=50°C16.681 W-Na12.20.044211R00593.6183.281 W-Na12.20.03460.400.55R1−seg102 W-Co15.20.02590.0259pH=5; T=60°C16.701 W-Na12.20.032211R00593.7983.301 W-Na12.20.02520.400.55R1−seg102 W-Co15.20.01890.0189pH=7; T=70°C351 W-Na12.20.02300.350.63R1−seg0883.42652 W-Co15.20.03000.0300pH=9; T=80°C401 W-Na12.20.02000.400.40R00777.45602 W-Co15.20.02430.0243pH=11; T=90°C401 W-Na12.20.01010.400.40R00779.12602 W-Co15.20.01130.0113SWy-CupH=3; T=50°C81.231 W-Na12.20.11660.950.95R014123.842 W-Cu15.20.00310.003118.771 W-Na12.20.03330.950.95R0042 W-Cu15.20.00090.0009pH=5; T=60°C84.201 W-Na12.20.07970.850.86R1−seg14123.562 W-Cu15.20.00700.007015.801 W-Na12.20.02280.850.86R1−seg042 W-Cu15.20.00200.0020pH=7; T=70°C751 W-Na12.20.04100.750.90R1−seg10104.92252 W-Cu15.20.00680.0068pH=9; T=80°C701 W-Na12.20.02500.700.87R1−seg0886.04302 W-Cu15.20.01480.0148pH=11; T=90°C701 W-Na12.20.02840.700.87R1−seg0887.73302 W-Cu15.20.00610.0061SWy-BapH=3; T=50°C72.171 W-Na12.20.100111R012105.4127.831 W-Na12.20.04460.900.89R1−p.ord062 W-Ba15.20.00450.0045pH=5; T=60°C841 W-Na12.20.09780.840.91R1−seg10105.96162 W-Ba15.20.00930.0093pH=7; T=70°C951 W-Na12.20.09050.950.97R1−seg12125.22052 W-Ba15.20.00450.0045pH=9; T=80°C65.751 W-Na12.20.061111R013135.3734.251 W-Na12.20.02020.800.85R1−seg132 W-Ba15.20.00250.0025pH=11; T=90°C150 W-Na10.20.00000.850.83R1−p.ord13135.16851 W-Ba12.20.0750Notes: xW-echa.cat: layer type and associated exchangeable cation;d001: interlamellar distance; nH2O: number of water molecules per half-cell; zH2O: position of the molecules along the c∗ axis of the H2O molecule is attached to 9.6 Å and 11.3 Å–13.9 Å for hydration states 1 W and 2 W, respectively. The position of the exchangeable cations per half-cell calculated along the axis c∗ is fixed with 9.60 Å and 12.25 Å for hydration states 1 W and 2 W [41]; n-echa.cat: number of exchangeable cations per half-cell is set to 0.28 (for the cation Na+) and at 0.14 (for bivalent metal cations), indicating complete saturation of cation exchange capacity (CEC); M: average number of sheets per stack; Mtot, total average number of sheets per stack; SM: layer stacking mode; R0: maximum order; R1: random stacking; R1−X: associated stacking (segregation-partial order); C: characters; Ho: homogeneous; He: heterogeneous; RWP: confidence factor.The theoretical decomposition of the SWy-Co sample, (pH=11; T=90°C) which has undergone fundamental changes in its basic structure, can be followed by two major hypotheses:The 1st consists in considering that it is still a T-O-T type structure despite the absence of the main 001 reflection which must be positioned around 6.1° (2θ) (d001~ 14.5 Å) and can be attenuated (is no longer sensitive to X-rays during diffractogram recordings) following the increase in the applied stress strength. In this case, a theoretical model based on the heterogeneous mixed 1 W/2 W structure with a major domination for the phase 2 W was adopted with very low average layer number per crystallite. This hypothesis can be practically verified for the good agreement towards higher diffraction orders.The 2nd considers that the basic clay structure has been strictly modified following the coupled increase in temperature T and the soil solution pH during the cation exchange process. This supposition is justified through the destruction of chemical bonds within the crystallite and/or which give rise to a new structure derived from smectite. This result, despite its originality, agrees with the work of [108, 109] which focuses on the hydrothermal synthesis of zeolite from clay minerals by controlling the pH effect on the synthesis process. Hence, the transition from a T-O-T phyllosilicate type (montmorillonite) to another kaolinite T-O phyllosilicate type is probabilistic, knowing that kaolinite has a dioctahedral structure [114–116]. Its structural half-cell formula is defined by (Si4 Al4 O10 (OH)8), whose basal distance d001 is of the order of 7 Å [117–119] with a closed IS accompanied by the absence of isomorphic substitutions (not CC in the middle of IS). For this hypothesis (Figure 6), we consider that the first reflection (in the 1st hypothesis was considered as 2nd reflection 002) is positioned around 12° (2θ) (d001~ 7 Å) from where the second reflection is necessarily positioned around 24° (2θ) (Table 7). For this hypothesis, we note the presence of a relatively intense reflection around 18° (2θ). A rational reflection position is obtained for the three reflections order (12°⟶18°⟶24°). Also, the exchangeable cation has no place in this configuration, which even calls into question the cation exchange process. Therefore, the first supposition seems more scientifically logical. The 1st hypothesis has been adopted in the rest of the calculations. It remains to be noted that the quality of the fitting is controlled by the RWP parameter.


## 3.4.2. Case of the SWy-Cu Samples

The best agreement between theoretical and experimental XRD patterns (Figure7) of the SWy-Cu samples is obtained using an interstratified structure of two MLS comprising various relative layers proportions with different hydration states (Table 7). This variability confirms the heterogeneous hydration character and the intermediate 1 W-2 W hydration phase observed regardless of the intensity of the applied constraints. In detail, a minor contribution of the 2 W phase increases from 5% to 30% by increasing the intensity of the external applied stress (pH=3; T=50°C⟶pH=11; T=90°C). Indeed, the 2 W hydration phase implemented in the theoretical model is necessarily attributed to the layer fraction whose CEC is saturated by Cu2+. This weighting fluctuation is evidence of an incomplete cation exchange process (d001<15Å). On the other hand, the dominance of 1 W layer hydration phase is interpreted by the existence of a fraction (quite large) regardless of the applied constraints applied. This contribution is attributed to the sodium residues from the starting sample (SWy-Na).The agreements obtained between the experimental and theoretical profiles (RWP~3% to 8%) are generally acceptable (< 10%), despite the misfit observed after widening the peaks around 14° and 28° (2θ). In fact, this disagreement can be broken down into a good reflection position agreement and a disagreement of diffracted intensity related to the input fluctuation of the distribution and abundance of water molecules in the IS. This disagreement led us to explore wide-angle areas, later to establish a possible link between CEC saturation and the degree of hydration heterogeneity.The logical increase of theRWP factor in the case of SWy-Cu sample reflects the increase in the heterogeneity’s degree defined, respectively, by an asymmetry of the first 001 reflections, the high FWHM value, and the ξ rationality parameter. Theoretically, this result is related to the variability of possible MLS configurations allowing a good fit of the 001 reflection. The exploitation of the WA, PAA, M, and RWP values allowed us to characterize a specific distribution of the n normalized layers within the crystallites according to the generated stacking modes and the contribution of each phase. This statistical representation of the layer can help to understand the CEC sensitivity fluctuation (of the starting sample) following the variation in the temperature T and pH during the cation exchange process.


## 3.4.3. Case of the SWy-Ba Samples

For SWy-Ba samples, the best agreements between theoretical and experimental models are shown in Figure8. The main structural parameters used to achieve a good fit are summarized in Table 7. For each model, several types of layers with variable stacking mode are used to improve the agreement obtained between the experimental and calculated models. This MLS is composed by several layers of type populations depending on the hydration state (0 W, 1 W, and 2 W) whose basal distance d001 is equal to 10.2 Å, 12.2 Å, and 15.2 Å, respectively. This variability confirms the heterogeneous hydration character observed by qualitative XRD analysis for the entire SWy-Ba series (pH=3; T=50°C⟶pH=11; T=90°C) with a major dominance for the 1 W hydration phase saturated by Na+ cation assigned to the starting sample. In addition, the 2 W phases are assigned to the fraction whose CEC is saturated by Ba2+ cation [41]. More specifically, for the first four samples from pH=3/T=50°C towards pH=9/T=80°C, an omnipresent minor contribution of the 2 W phase which does not exceed 16% is noted and which is evidence of the incomplete cation exchange process. In addition, the quite important dominance of the 1 W hydration phase (about 90%) is noted. The last sample (pH=11; T=90°C) has another intermediate phase 0 W/1 W which explain the observed decrease in basal distance probably resulting in the shrinkage of IS as a result of the temperature increase. The quality agreements obtained between the theoretical and experimental profiles are in average of ~5% which is generally acceptable.


## 3.5. Evolution of the Water Molecule Abundances versus Coupling Constraint Strength

### 3.5.1. Evolution of the nH2O Amounts versus Constraint Strength

The delicate theoretical determination of nH2O amounts for each studied sample is deduced from the results of thermogravimetry/differential thermal analysis (TG/DTA) (Figure S1) and summarized in Table 8.Table 8
Results from TG/DTA analyses in the case of samples SWy-Co, SWy-Cu, and SWy-Ba.
Samplesminitial (mg)Δm (mg)SWy-CopH=3; T=50°C15.9009.974pH=5; T=60°C16.6013.387pH=7; T=70°C06.8001.820pH=9; T=80°C17.1011.074pH=11; T=90°C12.3008.605SWy-CupH=3; T=50°C17.5012.975pH=5; T=60°C17.4014.246pH=7; T=70°C15.7012.836pH=9; T=80°C11.3006.972pH=11; T=90°C14.0010.848SWy-BapH=3; T=50°C15.0006.773pH=5; T=60°C23.6019.570pH=7; T=70°C15.0006.731pH=9; T=80°C15.4003.501pH=11; T=90°C19.1012.462Notes:minitial: initial mass of the samples before analysis; Δm: change in mass during analysis.Regardless of the sample type, the hydration state is governed by the cationic nature, the layer charge value, and the layer charge location [5–7, 107, 108, 120–122]. All samples studied belongs to the Wyoming montmorillonite specimen characterized by the same layer charge and the charge location value. The nature of the exchangeable cations and the external stresses applied to the cation exchange process (first-order coupling constraint) is at the origin of these specific water molecule amounts fluctuations. The water affinity of the exchangeable cation is related to the ionic potential which is defined by the ratio of the valence of the cation to its ionic radius [110] (Table 9). As this potential increases, the cation’s affinity for water also increases. Indeed, bivalent cations such as cobalt (Co2+), copper (Cu2+), and barium (Ba2+) have a high affinity of water translated by a 2 W hydration state [6, 7]. Unlike monovalent cations like sodium (Na+), having a low affinity for water mainly generates monohydrated states 1 W.Table 9
Radius and ionic potential of some cations [110].
CationsIonic potential (eV)Ionic radius (Å)Na+1.050.95Ba2+1.481.35Cu2+2.740.73Co2+3.080.65Based on the quantitative XRD analysis, a discretization of the content of the IS is carried out. Indeed, the evolution of nH2O molecules per half-cell, relative to the constraint strength, is described by Table 10 and represented in Figure 9. For all series, a decrease in the water molecules amounts as a function of the increase in temperature and soil solution pH.Table 10
Evolution of the nH2O amounts versus constraint strength for samples SWy-Co, SWy-Cu, and SWy-Ba.
SamplesPhasesSaturationmmolar (g/mol)MnH2O% Na+% M2+SWy-CopH=3; T=50°CPhase 11000370.864050.0442Phase 216.6883.28379.250100.0865pH=5; T=60°CPhase 11000370.864050.0322Phase 216.7083.30379.248100.0630pH=7; T=70°CØ3565377.406080.0833pH=9; T=80°CØ3070377.909070.0686pH=11; T=90°CØ3070377.909070.0327SWy-CupH=3; T=50°CPhase 19505371.432140.1228Phase 29505371.432040.0351pH=5; T=60°CPhase 18515372.568140.0937Phase 28515372.568040.0268pH=7; T=70°CØ7525373.703100.0546pH=9; T=80°CØ7030374.271080.0358pH=11; T=90°CØ7030374.271080.0406SWy-BapH=3; T=50°CPhase 110000370.864120.1001Phase 29000374.066060.0496pH=5; T=60°CØ8416375.988100.1164pH=7; T=70°CØ9505372.465120.0995pH=9; T=80°CPhase 110000370.864130.0611Phase 28020377.267130.0252pH=11; T=90°CØ1585398.076130.0750Notes: phases: modeling phase of each sample; Ø: absence of phases;mmolar: molar mass of the sample related to each phase; 4: average number of layers per stack; nH2O: number of water molecules per half-cell bound to each phase.Figure 9
nH2O abundance fluctuation as a function of stress strength for SWy-Co, SWy-Cu, and SWy-Ba samples (black scatter). Red scatter: the used linear and Lorentz fit function, respectively.In the case of SWy-Co sample (Figure9), there is an overall linear decrease in the number of water molecules as a function of the increase applied stresses intensity (pH=3; T=50°C⟶pH=11; T=90°C). Using a linear regression approach, a mathematical equation was developed. The behavior and evolution of the nH2O abundance fluctuation re described by the following function:
(4)y=0.14888−0.02226.x,where y is the nH2O abundance fluctuation, and x is the applied stress intensity.In the case of SWy-Cu and SWy-Ba samples (Figure9), there is a nonlinear water molecule amount decrease unlike SWy-Co as a function of the increase in external stresses applied. So, a regression approach based on the Lorentz equation was adopted to fit this evolution. This variation is described by function below:
(5)y=y0+2Aп×w4x−xc2w2,where y0 is the baseline offset, xc is the center of the peak, w equals the width of the peak at half height, and A is the area under the peak. The parameters of the used Lorentz function are presented in Figure 9.This decrease trends on the water molecule amount (nH2O) versus constraint strength are predictable when increasing temperature which automatically affects the IS closing and subsequently, it affects the cation exchange capacity of the mineral.


### 3.5.2. Individual Evolution of the 0 W, 1 W, and 2 W Abundances versus Constraint Strength

The “water footprint” schematized on FigureS2 shows the coexistence within the particle of several phases with different weights. The variation of the cation exchange process makes it possible to better understand the structural response of the starting material (such as fluctuations in basal distance d001, FWHM, crystalline size, rationality ξ, average number of layers M, and mode of stacking layers). Understanding the CEC functioning mode is closely related to the discretization of hydration states [48].For SWy-Co samples, a decrease in the 1 W monohydrate state, accompanied by an increase in fluctuation for the 2 W hydration state, represents the main hydration behavior. This can be interpreted by an easy intercalation of the compensating cations (Co2+) in IS more and more, replacing the sodium cations (Na+) that will leave the structure partially according to the applied stress variation. This hypothesis is confirmed by the global incomplete exchange process despite the exchange equilibrium time provided and remains to be noted that abundances in the aqueous phase are normalized to 100%. For SWy-Cu samples, the same behavior of the previous sample (SWy-Co) is observed. A slight fluctuation for the 1 W hydration state followed by a slow increase of 2 W is noted. For the latest SWy-Ba samples, the water behavior is almost different. There is a slow decrease in the 1 W state. This fluctuation is accompanied by a slight increase of 2 W phases. This is not valid for the complex pH=11 and T=90°C (extreme case) which has a minority anhydrate state of 0 W (15%) and a majority hydration state of 1 W (85%). The abundance of individual layer type deduced from the optimized theoretical MLS used to reproduce experimental XRD profiles was shown in Figure S3. Indeed, the 2 W hydration state is the most dominant phase in the entire SWy-Co series. Unlike the two complexes SWy-Cu and SWy-Ba, the 1 W hydration state is the most dominant phases.


## 3.5.1. Evolution of the nH2O Amounts versus Constraint Strength

The delicate theoretical determination of nH2O amounts for each studied sample is deduced from the results of thermogravimetry/differential thermal analysis (TG/DTA) (Figure S1) and summarized in Table 8.Table 8
Results from TG/DTA analyses in the case of samples SWy-Co, SWy-Cu, and SWy-Ba.
Samplesminitial (mg)Δm (mg)SWy-CopH=3; T=50°C15.9009.974pH=5; T=60°C16.6013.387pH=7; T=70°C06.8001.820pH=9; T=80°C17.1011.074pH=11; T=90°C12.3008.605SWy-CupH=3; T=50°C17.5012.975pH=5; T=60°C17.4014.246pH=7; T=70°C15.7012.836pH=9; T=80°C11.3006.972pH=11; T=90°C14.0010.848SWy-BapH=3; T=50°C15.0006.773pH=5; T=60°C23.6019.570pH=7; T=70°C15.0006.731pH=9; T=80°C15.4003.501pH=11; T=90°C19.1012.462Notes:minitial: initial mass of the samples before analysis; Δm: change in mass during analysis.Regardless of the sample type, the hydration state is governed by the cationic nature, the layer charge value, and the layer charge location [5–7, 107, 108, 120–122]. All samples studied belongs to the Wyoming montmorillonite specimen characterized by the same layer charge and the charge location value. The nature of the exchangeable cations and the external stresses applied to the cation exchange process (first-order coupling constraint) is at the origin of these specific water molecule amounts fluctuations. The water affinity of the exchangeable cation is related to the ionic potential which is defined by the ratio of the valence of the cation to its ionic radius [110] (Table 9). As this potential increases, the cation’s affinity for water also increases. Indeed, bivalent cations such as cobalt (Co2+), copper (Cu2+), and barium (Ba2+) have a high affinity of water translated by a 2 W hydration state [6, 7]. Unlike monovalent cations like sodium (Na+), having a low affinity for water mainly generates monohydrated states 1 W.Table 9
Radius and ionic potential of some cations [110].
CationsIonic potential (eV)Ionic radius (Å)Na+1.050.95Ba2+1.481.35Cu2+2.740.73Co2+3.080.65Based on the quantitative XRD analysis, a discretization of the content of the IS is carried out. Indeed, the evolution of nH2O molecules per half-cell, relative to the constraint strength, is described by Table 10 and represented in Figure 9. For all series, a decrease in the water molecules amounts as a function of the increase in temperature and soil solution pH.Table 10
Evolution of the nH2O amounts versus constraint strength for samples SWy-Co, SWy-Cu, and SWy-Ba.
SamplesPhasesSaturationmmolar (g/mol)MnH2O% Na+% M2+SWy-CopH=3; T=50°CPhase 11000370.864050.0442Phase 216.6883.28379.250100.0865pH=5; T=60°CPhase 11000370.864050.0322Phase 216.7083.30379.248100.0630pH=7; T=70°CØ3565377.406080.0833pH=9; T=80°CØ3070377.909070.0686pH=11; T=90°CØ3070377.909070.0327SWy-CupH=3; T=50°CPhase 19505371.432140.1228Phase 29505371.432040.0351pH=5; T=60°CPhase 18515372.568140.0937Phase 28515372.568040.0268pH=7; T=70°CØ7525373.703100.0546pH=9; T=80°CØ7030374.271080.0358pH=11; T=90°CØ7030374.271080.0406SWy-BapH=3; T=50°CPhase 110000370.864120.1001Phase 29000374.066060.0496pH=5; T=60°CØ8416375.988100.1164pH=7; T=70°CØ9505372.465120.0995pH=9; T=80°CPhase 110000370.864130.0611Phase 28020377.267130.0252pH=11; T=90°CØ1585398.076130.0750Notes: phases: modeling phase of each sample; Ø: absence of phases;mmolar: molar mass of the sample related to each phase; 4: average number of layers per stack; nH2O: number of water molecules per half-cell bound to each phase.Figure 9
nH2O abundance fluctuation as a function of stress strength for SWy-Co, SWy-Cu, and SWy-Ba samples (black scatter). Red scatter: the used linear and Lorentz fit function, respectively.In the case of SWy-Co sample (Figure9), there is an overall linear decrease in the number of water molecules as a function of the increase applied stresses intensity (pH=3; T=50°C⟶pH=11; T=90°C). Using a linear regression approach, a mathematical equation was developed. The behavior and evolution of the nH2O abundance fluctuation re described by the following function:
(4)y=0.14888−0.02226.x,where y is the nH2O abundance fluctuation, and x is the applied stress intensity.In the case of SWy-Cu and SWy-Ba samples (Figure9), there is a nonlinear water molecule amount decrease unlike SWy-Co as a function of the increase in external stresses applied. So, a regression approach based on the Lorentz equation was adopted to fit this evolution. This variation is described by function below:
(5)y=y0+2Aп×w4x−xc2w2,where y0 is the baseline offset, xc is the center of the peak, w equals the width of the peak at half height, and A is the area under the peak. The parameters of the used Lorentz function are presented in Figure 9.This decrease trends on the water molecule amount (nH2O) versus constraint strength are predictable when increasing temperature which automatically affects the IS closing and subsequently, it affects the cation exchange capacity of the mineral.


## 3.5.2. Individual Evolution of the 0 W, 1 W, and 2 W Abundances versus Constraint Strength

The “water footprint” schematized on FigureS2 shows the coexistence within the particle of several phases with different weights. The variation of the cation exchange process makes it possible to better understand the structural response of the starting material (such as fluctuations in basal distance d001, FWHM, crystalline size, rationality ξ, average number of layers M, and mode of stacking layers). Understanding the CEC functioning mode is closely related to the discretization of hydration states [48].For SWy-Co samples, a decrease in the 1 W monohydrate state, accompanied by an increase in fluctuation for the 2 W hydration state, represents the main hydration behavior. This can be interpreted by an easy intercalation of the compensating cations (Co2+) in IS more and more, replacing the sodium cations (Na+) that will leave the structure partially according to the applied stress variation. This hypothesis is confirmed by the global incomplete exchange process despite the exchange equilibrium time provided and remains to be noted that abundances in the aqueous phase are normalized to 100%. For SWy-Cu samples, the same behavior of the previous sample (SWy-Co) is observed. A slight fluctuation for the 1 W hydration state followed by a slow increase of 2 W is noted. For the latest SWy-Ba samples, the water behavior is almost different. There is a slow decrease in the 1 W state. This fluctuation is accompanied by a slight increase of 2 W phases. This is not valid for the complex pH=11 and T=90°C (extreme case) which has a minority anhydrate state of 0 W (15%) and a majority hydration state of 1 W (85%). The abundance of individual layer type deduced from the optimized theoretical MLS used to reproduce experimental XRD profiles was shown in Figure S3. Indeed, the 2 W hydration state is the most dominant phase in the entire SWy-Co series. Unlike the two complexes SWy-Cu and SWy-Ba, the 1 W hydration state is the most dominant phases.


## 3.6. Evolution of the Average Number of Layers versus Constraint Strength

The average number of layers (M) is a very important parameter in the crystal structure clay response when studied by XRD analysis. It has a direct influence on the 001 reflections of the theoretical and experimental models. For the low M value, the reflections 001 will be very wide with elevated value of FMWH and vice versa. The evolution of M parameter for all SWy-Co, SWy-Cu, and SWy-Ba samples is shown in Figure 10.Figure 10
Average number of layersM evolution versus constraint strength in the case of SWy-Co, SWy-Cu, and SWy-Ba samples (black scatter). Red scatter: the used Boltzmann fit.The SWy-Ba sample is the exception and exhibits growth ofM when increasing intensity constraint. The M evolution as a function of the applied stress applied is fitted for each sample and shown in Figure 10.The evolution ofM for all complexes following a Boltzmann function is shown below:
(6)y=A2+A1−A21+ex−x0/dx,where A1 is the initial value, A2 is the final value, x0 is the center, and dx is a time constant.All functions parameters are summarized in Figure10.


## 3.7. Evolution of the Layer Stacking Modes

A mapping representation of the hydration state in the case of SWy-Co, SWy-Cu, and SWy-Ba samples via XRD modeling profile approach is summarized in Figure11. The light brown, caramel, and dark brown colors represent the 0 W, 1 W, and 2 W layer type, respectively. Each line thus represents a layer with its intrinsic hydration state. The configuration considered here is an optimal configuration (best agreement obtained) extracted from the best agreements obtained between theoretical and experimental XRD profile. For SWy-Co complexes, the correlation between partial and total segregation stacking is observed. Thus, for SWy-Cu samples, we notice that the total segregation aspect is present regardless of the applied constraint applied. On the other hand, the SWy-Ba series shows the existence of two modes of stacking, segregation accompanied by partial order, with blatant dominance for segregated stacking.Figure 11
Mapping representation of the hydration state in the case of SWy-Co (a), SWy-Cu (b), and SWy-Ba (c) samples via XRD modeling approach.
(a)(b)(c)


## 3.8. BET and BJH Pore Size Distribution Analysis

The exploitation of the results obtained from the structural analysis by XRD modeling approach demonstrates a variability, in term of population, within the same crystallite. This directly influences the internal and external layers surfaces, which subsequently affects the adsorption properties and the sample porosity. Our objective is to evaluate the effect of the applied coupling disturbance (pH andT°C) on these properties. Indeed, we are looking for a link between structural damage, the intrinsic properties of the sample, and the saturation of the CEC. For that, a study based on BET adsorption measurement and BJH pore size distribution analysis is directed. Both the single-point and multipoint BET methods based on the surface area (SA) purpose from nitrogen isotherms were approved to evaluate external layer surface perturbation [41, 123–131] (Figure 12). Average pore diameter is determined using the BJH method (Figure 13). Whatever the nature of the exchangeable cation, an increase in the SA values is shown as a function of the constraint intensity up to a pH=9 and a T=80°C. After this limit value, a behavior divergence is shown. In fact, for the two samples saturated, respectively, by Co and Cu cations, a decrease in the SA values is observed against the continuous growth in the case of the Ba cation.Figure 12
SABET single and multipoint BET evolution versus constraint strength for (a) SWy-Co, (b) SWy-Cu, and (c) SWy-Ba samples.
(a)(b)(c)Figure 13
BJH method average pore diameter evolution versus constraint strength.The average pore diameter evolution versus constraint strength (Figure13) can provide a preliminary explanation for the observed SA fluctuations.For all samples, the limit of mesoporosity domain is respected (where pores whose maximum diameter is between 2 and 50 nm). Indeed, the SWy-Ba sample practically keeps the same average pore diameters values up topH=11 and T=90°C. However, the other two samples are marked by a considerable increase in the average pore diameter, which probably indicates a transformation that affected the internal configuration of the clay particle. This agrees with the results obtained from XRD analysis focusing the evolution of the average number of layers versus constraint strength.Obtained nitrogen adsorption (ADS)-desorption (DES) isotherms curves shape (Figure14) shows a very closer type II isotherm classification [127–131]. This allocation confirms the supremacy of the mesoporous texture despite the fluctuations observed and the nature of the exchangeable cation. The relative large pore size obtained in the case of stressed SWy-Ba sample is explained by the coupling of three essential parameters, respectively, the acidic or basic nature of the soil solution, the intrinsic hydration property, and the nature of the exchangeable cation. The Ba2+ ions exchange promotes the exfoliation process and thereafter increases the porosity degree.Figure 14
Nitrogen adsorption (ads)-desorption (des)-isotherms in the case of SWy-Co, SWy-Cu, and SWy-Ba.To overcome the limits of SA analysis (i.e., nitrogen can only cover external surfaces and does not interact with internal surfaces), since it cannot access the information in the volume of the sample and subsequently, it does not provide information on the IS configurations/changes, a pore size distribution (PSD) analysis imposes itself. The application of PSD analysis requires technical approaches such as (i) the volumes of micropores, mesopores, and macropores including nanopores in one gram solid labeled, respectively,VMi, VMe, and VMa (all in mL/g) and (ii) the effects related to macroporosity are neglected assuming that they do not affect the properties of adsorption and the specific micromesopore volumes (V=VMi+VMe) that is determined using the desorption data (at the relative equilibrium pressure P/P0). Fundamental approximations used for the PSD analysis target the shape and characteristics of the pores. Indeed, cylindrical shape (with radius (r) approximately half of its width) is adopted. Also, cylindrical mesopores are characterized by r radii which correspond to V values (calculated from the corrected Kelvin equation using P/P0 values).The PSD plots provide information on the variation of the cumulative pore volume versus pore radius (V-r) (Figure 15). Although they have the same trend, the V-r curves relating to each sample present specificities showing the effect of the applied stress on the evolution of the porosity. In the case of SWy-Co sample and from a diameter of 4 nm, an evolution divergence appears with a “gap” in favor of high pH and T°C value which reaches 0.086 mL/g (Figure 15). The V-r variation divergence proves, initially, the achievement of the cation exchange process which is confirmed by an individual comportment of the V-r curves despite having the same appearance. In addition, a direct effect of the increase of the applied stresses appears as an increase in the V-r “gap.” For SWy-Ba, the maximum cumulative pore volume is 0.062 mL/g attained at pH=9 and T=80°C. The major remark concerns the last two values of pH and T. Indeed, although they present a very similar appearance to the other V-r characteristic curves, there is a jump (“gap”) of 0.015 mL/g attributed to the acid-base transformation. In the case of SWy-Cu, the V-r curves have respected the same shape as for the other samples, but the maximum value did not exceed 0.069 mL/g. The common behavior for the three samples lies in the existence of a cumulative pore volume “gap” observed during the acid-base transformation. The value of this gap is practically very similar and close for all samples, and it averages around 0.016 mL/g. This variation is consistent with the XRD modeling profile which predicts layer exfoliation and presence of highly hydrated rate.Figure 15
The pore size distribution (PSD) curve for the different studied samples (V-r) in the case of SWy-Co, SWy-Cu, and SWy-Ba.The derivative pore size distribution curve (Figure16) confirms the prevailing mesoporosity with a pore diameter concentration varying between 2.20 and 9.89 nm. A concentration of large pore populations related to the saturated Co2+ sample (at pH=11 and T=90°C) is observed. This agrees with the obtained SA results and XRD analysis. The V-r curve radius derivative for all samples is given in Figure 16. For the rest of the studied samples, an almost similar variation is observed except for SWy-Ba (pH=11/T=90) which presents an extremum around 4.01 nm with a small extent.Figure 16
The derivative pore size distribution curve.


## 4. Conclusion

This work studied the Wyoming montmorillonite response to a first-order coupling constraint obtained at the laboratory scale by combining soil solution pH variation with temperature gradient. The eventual mineral response to such disturbance was approached from a structural, hydrological (IS perturbation), cation exchange (CEC), and porosity point of view.The quantitative investigation of the 001 reflections obtained from the XRD patterns via the modeling approach makes it possible to develop a deep theoretical calculation which allows us to build a global idea about the mechanisms accompanying these changes. Indeed, IS configuration and evolution are decrypted according to the applied constraint. Several parameters like nature, abundance, relative probability, size, position, arrangement of atoms/ions in the IS, the quantity of nH2O, the average number of sheets, and the stacking modes in crystallites are precisely identified.These goals are achieved by combining results from XRD profile modeling approach, TG/DTA analysis, and the adsorption measurement outcomes.The starting SWy-Na complexes studied at room condition exhibit a heterogeneous hydration state characterized by a mixture between 0 W and 1 W phases contrary to the qualitative analysis which shows a homogeneous character. A correlation between XRD profile modeling approach consolidated by TG/DTA analysis and the adsorption measurement outcomes shows the following:The case of the Co2+ cation is as follows:
(i)
Heterogeneous hydration behavior induced by the coexistence of two type of layer populations (i.e., 1 W and 2 W phases within the crystallite), whatever the stress force(ii)
The theoretical decomposition of the experimental XRD profiles allowed us to identify all the different populations of existing layers and their stacking mode(iii)
A dominance of the segregated layer stacking mode(iv)
The CEC increases simultaneously with the applied stress intensity increases(v)
A linear regression approach describes the water molecule amount decrease, determined from TG/DTA analysis, as the temperature increases(vi)
The total structure change may appear (2:1⟶1:1) by exceeding the limit of the applied stress (pH 11 and T>150°C)(vii)
The BJH method shows an increase on the porosity rate traduced by an evolution divergence appearing with a “gap” in favor of high pH andT°C value. The pore diameter concentration is varying between 2.20 and 9.89 nmThe case of the Cu2+ cation is as follows:
(i)
An interstratification explains the coexistence of two hydration states (1 W and 2 W) regardless of the stress strength(ii)
The coexistence within the crystallite of different types of layer populations stacked according to a specific set of junction probabilities(iii)
“Total segregation” stacking mode dominated the entire series(iv)
CEC growth by increasing the applied stress(v)
A nonlinear water molecules amount decrease unlike SWy-Co sample as a function of the increase in external applied stresses (from TG/DTA analysis) is fitted with a regression approach based on the Lorentz model(vi)
Adsorption outcomes demonstrate that the sample seems undamaged by the applied stress intensity fluctuationsThe case of the Ba2+ cation is as follows:
(i)
A heterogeneous hydration state proven by the presence of several layers 0 W, 1 W, and 2 W, regardless of the applied stress(ii)
The coexistence of several types of compensating cation (Ba2+ and Na+) indicating the formation of a real physical mixture between populations of different layer types(iii)
Partial CEC saturation and domination of segregated layer stacking aspect(iv)
Results from TG/DTA analysis show a nonlinear evolution governed by a Lorentz function which lies between the observed evolution in the case of Co2+ and Cu2+ cations(v)
The intrinsic sample porosity is affected by the acid-base transformation with a 0.015 mL/g “gap.” The maximum cumulative pore volume is 0.062 mL/g attained atpH=9 and T=80°CIn addition, the XRD modeling approach allowed us to assign a structural response of the water footprint of the samples and to map the interstratification of the different layer type populations.The presence of each cation induces specific structural characteristics and a variable exchanged sample response to external excitation. The observed structural transition, for the Co2+ cation from a pH=8 and T=80°, accompanied by a concentration of large pore populations (at pH=11 and T=90°C) indicates the strong exfoliation phenomena affecting even the elementary tetrahedral or octahedral sheets and subsequently reducing the metal removal efficiency.The evolution of the average number of layers (M) confirms the consolidation of the crystallite thickness in the case of Ba2+ cation despite the acid-base transition and the strong thermal gradient. This is in favor of an irreversible cation exchange process supporting the Barium removal efficiency.



---