# Influence of pH and Fluoride Species on the Corrosion Behavior of Ti-xNb-13Zr Alloys in Ringer’s Solution

Authors: A. Robin; O. A. S. Carvalho
Journal: Advances in Materials Science and Engineering
 (2013)

---

## Abstract

Ti-Nb-Zr alloys are interesting materials for implant applications due to the atoxic character of the Nb and Zr alloying elements and to their low elastic modulus when compared to CP-Ti. In this work, the corrosion behaviour of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr alloys was investigated in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and containing 1000 ppm F at 37°C, through open-circuit potential measurements, potentiodynamic polarization, and electrochemical impedance spectroscopy. The four materials showed a passive behavior in Ringer's solution without fluorides for pH ranging from 2 to 7.5 and in Ringer's solution of pH 5 and 7.5 containing 1000 ppm F but presented an active behavior in Ringer's solution of pH 2 containing fluorides. The corrosion resistance of all materials in Ringer's solution decreases with both decrease of pH and addition of fluorides. Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys and, in most conditions, the Ti-Nb-Zr alloys present higher corrosion resistance than CP-Ti.


---

## Body

## 1. Introduction

Commercially pure Ti (CP-Ti) is widely used in restorative surgery as dental and orthopedic implants, due to its high corrosion resistance in physiological media and biocompatibility [1]. Nevertheless, some studies showed that titanium release in the organism can lead from local discoloration of tissue to serious inflammatory reactions [2, 3]. Moreover, the Young modulus of grades 1 to 4 CP-Ti (nearly 100 GPa) is higher than that of bone (30 GPa). Due to this difference in rigidity, there is a poor load sharing between the bone and the implant and bone resorption may occur. These negative aspects of CP-Ti led to the development of more corrosion-resistant, more biocompatible, and more wear-resistant titanium alloys with better biomechanical compatibility.Among these materials, Ti-Nb-Zr ternary alloys are promising since they present a lower Young’s modulus (60–90 GPa) when compared to CP-Ti. The Ti-13Nb-13Zr alloy was the most studied material of this family [4–20]. It was shown to be passive in simulated physiological solutions, such as Ringer’s solution [4, 10, 12, 16], Hank solutions [8, 13–15], artificial saliva [9], and phosphate-buffered saline solution (PBS) [5–7], but active in hydrochloric acid solutions [4]. The corrosion resistance of the Ti-13Nb-13Zr alloy was generally slightly higher than or equal to that of Ti in both saline and acid solutions [4, 8, 14, 15]. The microstructure of the Ti-13Nb-13Zr alloy which is dependent on both heat and mechanical treatments [21] affects its corrosion resistance [4, 10]. Few works are available on the corrosion behavior of other Ti-Nb-Zr ternary alloys [8, 16, 22]. The Ti-5Nb-13Zr and Ti-20Nb-30Zr alloys were shown to be passive in Ringer’s solution and presented higher corrosion resistance than CP-Ti [16]. The Ti-4Nb-15Zr alloy was also passive in Hank’s solution and slightly less corrosion resistant than Ti-13Nb-13Zr [8]. The Ti-22Nb-6Zr alloy was passive in 0.9% NaCl solution and more corrosion resistant than Ti-22Nb [22].It is common that the passive metals undergo localized corrosion (pitting or crevice corrosion) in chloride environment, such as physiological solutions, due to the development of occluded cells. The pH in these occluded cells reaches acidic values which can lead to the chemical dissolution of the protective film. In applications in dental restorations, the implants can be also in contact with fluoride species since the fluoride-based treatments are used to prevent the dental plaque formation and the caries development. The concentration of fluorides varies from nearly 1 ppm in drinking water, 200 ppm in mouth rinses, and 1000–1500 ppm in toothpastes to 10000–20000 ppm in gels, and the pH can range from neutral to acidic values.The objective of this work was to study the influence of pH and fluoride concentration on the corrosion behavior of three Ti-xNb-13Zr alloys (x=5, 13, and 20) in Ringer’s solution at 37°C. The study was based on electrochemical techniques. The results were compared with those obtained for CP-Ti under the same experimental conditions.


## 2. Experimental

The materials used in this work were as-cast grade 1 CP-Ti and the experimental Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr alloys (wt%).The Ti-Nb-Zr alloys were produced from commercially pure Ti, Zr, and Nb sheets by melting in an arc-furnace under argon atmosphere, heat-treated under vacuum at 1000°C for 1 h, water-quenched, cold-swaged (around 90% reduction in area), and afterwards heat-treated at 900°C (temperature above theβ transus temperature) for 30 min under vacuum and again water-quenched. The microstructures of all materials have been presented elsewhere [16]. Ti had a characteristic as-cast microstructure, with nonhomogeneous size distribution of α phase grains and the Ti-Nb-Zr alloys showed a typical martensitic microstructure constituted of α′ hexagonal martensite. The α′′ orthorhombic martensite is also present in Ti-20Nb-13Zr alloy.Cylindrical test specimens (8 mm diameter and 15 mm length) were machined from the four materials and mounted in polytetrafluoroethylene (PTFE) holders. The cross section of the electrodes (0.5 cm2 area) was mechanically ground with emery paper up to 600 grit, rinsed with distilled water, and dried with acetone.The solution was Ringer’s solution [23] with the following composition: 8.6 g NaCl + 0.3 g KCl + 0.33 g CaCl2–2H2O in 1000 mL deionized water. The natural pH of Ringer’s solution was 7.5. The solution was naturally aerated and the experiments were conducted without stirring. The temperature was maintained at 37°C using a thermostatic bath. The counter electrode was a square-shaped platinum sheet of 18 cm2 area. All potentials were referred to the saturated calomel electrode (SCE) potential (= + 0.242 V/SHE—standard hydrogen electrode). The fluoride species were added to Ringer’s solution using NaF P.A. salt. The pH was adjusted to 2 and 5 using dilute HCl solution.Open-circuit potential (OCP), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization measurements were performed using the Electrochemical Interface SOLARTRON model 1287A and the Frequency Response Analyzer SOLARTRON model 1260 A, controlled by the Ecorr/Zplot SOLARTRON model 125587S software. Prior to polarization experiments, the working electrodes were immersed in Ringer’s solution for 3 h, taking the moment of immersion as zero time. Then, impedance measurements at OCP were performed using a sinusoidal signal of 10 mV amplitude and frequencies in the range of 0.1 Hz–100 kHz. Cathodic and anodic polarizations were then carried out potentiodynamically with a sweep rate of 0.16 mV/s. After each run, the samples were reground with emery papers to a 600-grit finish in order to remove any product formed on the metal surface which could affect the following tests, rinsed with distilled water, dried, and transferred quickly in the solution.


## 3. Results and Discussion

### 3.1. Corrosion Behavior in Ringer’s Solution without Fluorides

Figure1 shows the variation of OCP for CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 without fluoride. The OCPs shift in the noble direction, which indicates the formation and growth of passive films on all materials. This is a general trend for Ti and Ti alloys in physiological solutions [4–10, 12–16].Variation of OCP with exposure time for (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
(a)
(b)
(c)
(d)The values of OCP measured after 3 h exposure are reported in Table1. As expected, all these values are found in the stability region of TiO2 of the Ti-H2O Pourbaix diagram [24] (Figure 2). Nevertheless, the Ti-5Nb-13Zr alloy is the less noble material, whereas CP-Ti is the nobler one (Table 1). It is not possible to compare the OCPs measured in this work with published data because the OCP values are highly dependent on the surface finish and heat treatments. For example, values ranging from −0.513 V to −0.064 V/SCE were reported for Ti-13Nb-13Zr alloy in Ringer’s solution [10].Table 1
OCP values (in V/SCE) measured after 3 h exposure in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
CP-Ti
Ti-5Nb-13Zr
Ti-13Nb-13Zr
Ti-20Nb-13Zr
pH 2
0.078
−0.238
−0.067
−0.064
pH 5
−0.019
−0.257
−0.096
−0.121
pH 7.5
−0.085
−0.190
−0.080
−0.123Figure 2
Ranges of OCP values measured after 3 h exposure in Ringer’s solution of pH 2, 5, and 7.5 without fluoride and containing 1000 ppm F at 37°C.Figure3 presents the polarization curves of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 without fluoride. Their shapes are similar which shows that the anodic and cathodic reactions occurring on all materials are the same. As no active-passive transition is observed, it is confirmed that all materials are spontaneously passive in Ringer’s solutions of pH ranging from 2 to 7.5. All materials remain passive at least up to 2.0 V/SCE. In some cases, an anodic peak is observed at nearly 1.7 V/SCE and has been attributed to some phase change in the passivating oxide film [4].Polarization curves of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
(a)
(b)
(c)
(d)The corrosion current densities determined by Tafel extrapolation method and the passive current densities measured at 1.0 V/SCE in the passive region are reported in Figures4(a) and 4(b), respectively. All the corrosion current densities are in the order of 10−7 A cm−2, which depicts the high corrosion resistance of all materials in Ringer’s solutions of pH ranging from 2 to 7.5. The low values of the passive current densities (order of 10−6 A cm−2) indicate the high stability of the passivating films. Comparable values were obtained for CP-Ti and Ti-13Nb-13Zr alloy in Hank’s solution [14, 25]. The Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr, and Ti-20Nb-13Zr alloys in Ringer’s solution without fluorides (Figure 4(a)), which can be related to the lower Nb content of α′ phase in Ti-5Nb-13Zr and the two phases α′ + α′′ microstructure in Ti-20Nb-13Zr [16].(a) Corrosion current densities and (b) passive current densities (measured at 1.0 V/SCE) of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 without fluoride and containing 1000 ppm F at 37°C.
(a)
(b)


### 3.2. Corrosion Behavior in Ringer’s Solution Containing Fluorides

Figure5 shows the variation of OCP for CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm fluorides. For pH 7.5, the OCPs shift in the noble direction, which indicates the formation and growth of passive films on all materials. The OCP values measured after 3 h exposure under this condition (Table 2) are found in the stability region of TiO2 of the Ti-H2O Pourbaix diagram [24] (Figure 2), which depicts a passive behavior. In Ringer’s solution of pH 2, the OCPs stabilize to very negative values (Table 2) that are found in the stability region of Ti ions of the Ti-H2O Pourbaix diagram [24] (Figure 2), indicating a spontaneous active behavior. For pH 5, although the OCP values are nearly −0.3 to −0.2 V less noble than the values obtained for pH 7.5 (Table 2), they are also found in the stability region of TiO2 (Figure 2), showing the passive behavior of all the materials.Table 2
OCP values (in V/SCE) measured after 3 h exposure in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
CP-Ti
Ti-5Nb-13Zr
Ti-13Nb-13Zr
Ti-20Nb-13Zr
pH 2
−0.964
−0.887
−0.890
−0.881
pH 5
−0.353
−0.537
−0.493
−0.509
pH 7.5
−0.028
−0.308
−0.074
−0.143Variation of OCP with exposure time for (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
(a)
(b)
(c)
(d)Nakagawa et al. [26] show from OCP measurements of Ti-6Al-4V alloy in artificial saliva that there is a well-defined correlation between pH and fluoride concentration that determines the spontaneous (active or passive) behavior of the alloy. The combination of low pH and fluoride presence has been shown to enhance passive film dissolution on CP-Ti, Ti-6Al-4V, and Ti-Ta alloys [26–28].The anodic polarization curves of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 5 and 7.5 containing 1000 ppm fluorides are characteristic of passive materials (Figure6). Nevertheless, the anodic current densities measured for pH 5 present higher values, which is indicative of a lower stability of the passive films. In Ringer’s solution of pH 2, the anodic polarization curves present an active-passive transition, which corroborates the spontaneous active behavior of all materials at OCP under this condition. Similar results were obtained for Ti, Ti-6Al-4V, and Ti-23Ta alloys in artificial saliva containing 1000 ppm fluorides [28].Polarization curves of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
(a)
(b)
(c)
(d)The corrosion current densities and the passive current densities measured at 1.0 V/SCE determined in Ringer’s solution of pH 7.5 are close to the values obtained in solutions without fluorides (Figure4). This indicates that, in neutral solution, the presence of fluoride has little effect on the corrosion resistance and the stability of the passive films.On the contrary, the corrosion current densities and the passive current densities increased nearly 1-2 and 2-3 orders of magnitude in Ringer’s solutions of pH 5 and pH 2, respectively, when compared to the values measured for pH 7.5 (Figure4). Thus, in solutions containing fluorides, the corrosion resistance and the stability of the passive films decrease with decreasing pH. The same trend is observed for all materials.When in the passive state (in Ringer’s solution of pH 5 and 7.5 containing 1000 ppm fluorides), the Ti-13Nb-13Zr alloy is also a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys (Figure4(a)).The higher corrosiveness of low pH aqueous solution containing fluorides has been attributed to the presence ofHF2- or HF species [29]. The concentrations of F−, HF2- and HF are dependent on pH and total fluoride concentration and can be calculated from the equilibria constants and mass conservation equation [30]. Table 3 reports the calculated concentrations of F−, HF2-, and HF for pH 2, 5, and 7.5 and 1000 ppm total fluoride concentration. It is clear that the active behavior of the materials in Ringer’s solution of pH 2 containing 1000 ppm F is related to the high concentration of HF.Table 3
Calculated concentrations of F−, HF2-, and HF for pH 2, 5, and 7.5 and 1000 ppm total fluoride concentration.
pH 2
pH 5
pH 7.5
[F−]/ppm
104
973
988
[
HF
2
-
]/ppm
86
8
0
[HF]/ppm
841
8
0


### 3.3. EIS Results

The Bode diagrams obtained at OCP in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and of pH 7.5 containing 1000 ppm fluorides present a linear relation (slope close to −1) between log|Impedance| and log (Frequency) and a phase angle near −90° from the low to intermediate frequencies (Figures 7 and 8). For CP-Ti, this is limited to a narrower frequency range, which is indicative of a lower stability of the oxide film formed on CP-Ti (Figures 7(a) and 8(a)). All these results depict a predominantly capacitive behavior of the metal/solution interface, characteristic of passive materials. In Ringer’s solution of pH 5 containing fluorides, although the four materials are passive, the oxide layers are less capacitive, which can be related to their lower stability. Bode diagrams of the same shape and impedance values of the same order of magnitude were obtained for many other Ti alloys in physiological solutions [11, 31, 32].Bode diagrams of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr obtained at OCP in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
(a)
(b)
(c)
(d)Bode diagrams of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr obtained at OCP in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
(a)
(b)
(c)
(d)Very low impedance values were measured in Ringer’s solution of pH 2 containing 1000 ppm fluorides, which confirms the active state of all materials under these conditions. Impedance values of few tens of Ω cm2 were also measured for Ti-23Ta alloy in artificial saliva of pH2 containing 1000 ppm fluorides [33] and for Ti and Ti-6Al-4V alloy in artificial saliva of pH3 containing 0.01 M NaF [34].For comparison, the corrosion resistance of the materials can be estimated by the values of impedance modulus at low frequencies (Table4). The impedance results confirm that the Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys. In most conditions, the Ti-Nb-Zr alloys presented higher corrosion resistance than CP-Ti.Table 4
Impedance modulus (inΩ cm2) at low frequency (= 0.1 Hz) in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and containing 1000 ppm F at 37°C.
CP-Ti
Ti-5Nb-13Zr
Ti-13Nb-13Zr
Ti-20Nb-13Zr
0 ppm F
pH 2
21227
33371
76491
40350
pH 5
30543
52854
110420
57979
pH 7.5
33725
69234
110647
62797
1000 ppm F
pH 2
18
15
14
12
pH 5
7010
2054
2525
1926
pH 7.5
24495
53785
64752
45122


## 3.1. Corrosion Behavior in Ringer’s Solution without Fluorides

Figure1 shows the variation of OCP for CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 without fluoride. The OCPs shift in the noble direction, which indicates the formation and growth of passive films on all materials. This is a general trend for Ti and Ti alloys in physiological solutions [4–10, 12–16].Variation of OCP with exposure time for (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
(a)
(b)
(c)
(d)The values of OCP measured after 3 h exposure are reported in Table1. As expected, all these values are found in the stability region of TiO2 of the Ti-H2O Pourbaix diagram [24] (Figure 2). Nevertheless, the Ti-5Nb-13Zr alloy is the less noble material, whereas CP-Ti is the nobler one (Table 1). It is not possible to compare the OCPs measured in this work with published data because the OCP values are highly dependent on the surface finish and heat treatments. For example, values ranging from −0.513 V to −0.064 V/SCE were reported for Ti-13Nb-13Zr alloy in Ringer’s solution [10].Table 1
OCP values (in V/SCE) measured after 3 h exposure in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
CP-Ti
Ti-5Nb-13Zr
Ti-13Nb-13Zr
Ti-20Nb-13Zr
pH 2
0.078
−0.238
−0.067
−0.064
pH 5
−0.019
−0.257
−0.096
−0.121
pH 7.5
−0.085
−0.190
−0.080
−0.123Figure 2
Ranges of OCP values measured after 3 h exposure in Ringer’s solution of pH 2, 5, and 7.5 without fluoride and containing 1000 ppm F at 37°C.Figure3 presents the polarization curves of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 without fluoride. Their shapes are similar which shows that the anodic and cathodic reactions occurring on all materials are the same. As no active-passive transition is observed, it is confirmed that all materials are spontaneously passive in Ringer’s solutions of pH ranging from 2 to 7.5. All materials remain passive at least up to 2.0 V/SCE. In some cases, an anodic peak is observed at nearly 1.7 V/SCE and has been attributed to some phase change in the passivating oxide film [4].Polarization curves of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
(a)
(b)
(c)
(d)The corrosion current densities determined by Tafel extrapolation method and the passive current densities measured at 1.0 V/SCE in the passive region are reported in Figures4(a) and 4(b), respectively. All the corrosion current densities are in the order of 10−7 A cm−2, which depicts the high corrosion resistance of all materials in Ringer’s solutions of pH ranging from 2 to 7.5. The low values of the passive current densities (order of 10−6 A cm−2) indicate the high stability of the passivating films. Comparable values were obtained for CP-Ti and Ti-13Nb-13Zr alloy in Hank’s solution [14, 25]. The Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr, and Ti-20Nb-13Zr alloys in Ringer’s solution without fluorides (Figure 4(a)), which can be related to the lower Nb content of α′ phase in Ti-5Nb-13Zr and the two phases α′ + α′′ microstructure in Ti-20Nb-13Zr [16].(a) Corrosion current densities and (b) passive current densities (measured at 1.0 V/SCE) of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 without fluoride and containing 1000 ppm F at 37°C.
(a)
(b)


## 3.2. Corrosion Behavior in Ringer’s Solution Containing Fluorides

Figure5 shows the variation of OCP for CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm fluorides. For pH 7.5, the OCPs shift in the noble direction, which indicates the formation and growth of passive films on all materials. The OCP values measured after 3 h exposure under this condition (Table 2) are found in the stability region of TiO2 of the Ti-H2O Pourbaix diagram [24] (Figure 2), which depicts a passive behavior. In Ringer’s solution of pH 2, the OCPs stabilize to very negative values (Table 2) that are found in the stability region of Ti ions of the Ti-H2O Pourbaix diagram [24] (Figure 2), indicating a spontaneous active behavior. For pH 5, although the OCP values are nearly −0.3 to −0.2 V less noble than the values obtained for pH 7.5 (Table 2), they are also found in the stability region of TiO2 (Figure 2), showing the passive behavior of all the materials.Table 2
OCP values (in V/SCE) measured after 3 h exposure in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
CP-Ti
Ti-5Nb-13Zr
Ti-13Nb-13Zr
Ti-20Nb-13Zr
pH 2
−0.964
−0.887
−0.890
−0.881
pH 5
−0.353
−0.537
−0.493
−0.509
pH 7.5
−0.028
−0.308
−0.074
−0.143Variation of OCP with exposure time for (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
(a)
(b)
(c)
(d)Nakagawa et al. [26] show from OCP measurements of Ti-6Al-4V alloy in artificial saliva that there is a well-defined correlation between pH and fluoride concentration that determines the spontaneous (active or passive) behavior of the alloy. The combination of low pH and fluoride presence has been shown to enhance passive film dissolution on CP-Ti, Ti-6Al-4V, and Ti-Ta alloys [26–28].The anodic polarization curves of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr in Ringer’s solution of pH 5 and 7.5 containing 1000 ppm fluorides are characteristic of passive materials (Figure6). Nevertheless, the anodic current densities measured for pH 5 present higher values, which is indicative of a lower stability of the passive films. In Ringer’s solution of pH 2, the anodic polarization curves present an active-passive transition, which corroborates the spontaneous active behavior of all materials at OCP under this condition. Similar results were obtained for Ti, Ti-6Al-4V, and Ti-23Ta alloys in artificial saliva containing 1000 ppm fluorides [28].Polarization curves of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
(a)
(b)
(c)
(d)The corrosion current densities and the passive current densities measured at 1.0 V/SCE determined in Ringer’s solution of pH 7.5 are close to the values obtained in solutions without fluorides (Figure4). This indicates that, in neutral solution, the presence of fluoride has little effect on the corrosion resistance and the stability of the passive films.On the contrary, the corrosion current densities and the passive current densities increased nearly 1-2 and 2-3 orders of magnitude in Ringer’s solutions of pH 5 and pH 2, respectively, when compared to the values measured for pH 7.5 (Figure4). Thus, in solutions containing fluorides, the corrosion resistance and the stability of the passive films decrease with decreasing pH. The same trend is observed for all materials.When in the passive state (in Ringer’s solution of pH 5 and 7.5 containing 1000 ppm fluorides), the Ti-13Nb-13Zr alloy is also a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys (Figure4(a)).The higher corrosiveness of low pH aqueous solution containing fluorides has been attributed to the presence ofHF2- or HF species [29]. The concentrations of F−, HF2- and HF are dependent on pH and total fluoride concentration and can be calculated from the equilibria constants and mass conservation equation [30]. Table 3 reports the calculated concentrations of F−, HF2-, and HF for pH 2, 5, and 7.5 and 1000 ppm total fluoride concentration. It is clear that the active behavior of the materials in Ringer’s solution of pH 2 containing 1000 ppm F is related to the high concentration of HF.Table 3
Calculated concentrations of F−, HF2-, and HF for pH 2, 5, and 7.5 and 1000 ppm total fluoride concentration.
pH 2
pH 5
pH 7.5
[F−]/ppm
104
973
988
[
HF
2
-
]/ppm
86
8
0
[HF]/ppm
841
8
0


## 3.3. EIS Results

The Bode diagrams obtained at OCP in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and of pH 7.5 containing 1000 ppm fluorides present a linear relation (slope close to −1) between log|Impedance| and log (Frequency) and a phase angle near −90° from the low to intermediate frequencies (Figures 7 and 8). For CP-Ti, this is limited to a narrower frequency range, which is indicative of a lower stability of the oxide film formed on CP-Ti (Figures 7(a) and 8(a)). All these results depict a predominantly capacitive behavior of the metal/solution interface, characteristic of passive materials. In Ringer’s solution of pH 5 containing fluorides, although the four materials are passive, the oxide layers are less capacitive, which can be related to their lower stability. Bode diagrams of the same shape and impedance values of the same order of magnitude were obtained for many other Ti alloys in physiological solutions [11, 31, 32].Bode diagrams of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr obtained at OCP in Ringer’s solution of pH 2, 5, and 7.5 at 37°C.
(a)
(b)
(c)
(d)Bode diagrams of (a) CP-Ti, (b) Ti-5Nb-13Zr, (c) Ti-13Nb-13Zr, and (d) Ti-20Nb-13Zr obtained at OCP in Ringer’s solution of pH 2, 5, and 7.5 containing 1000 ppm F at 37°C.
(a)
(b)
(c)
(d)Very low impedance values were measured in Ringer’s solution of pH 2 containing 1000 ppm fluorides, which confirms the active state of all materials under these conditions. Impedance values of few tens of Ω cm2 were also measured for Ti-23Ta alloy in artificial saliva of pH2 containing 1000 ppm fluorides [33] and for Ti and Ti-6Al-4V alloy in artificial saliva of pH3 containing 0.01 M NaF [34].For comparison, the corrosion resistance of the materials can be estimated by the values of impedance modulus at low frequencies (Table4). The impedance results confirm that the Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys. In most conditions, the Ti-Nb-Zr alloys presented higher corrosion resistance than CP-Ti.Table 4
Impedance modulus (inΩ cm2) at low frequency (= 0.1 Hz) in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and containing 1000 ppm F at 37°C.
CP-Ti
Ti-5Nb-13Zr
Ti-13Nb-13Zr
Ti-20Nb-13Zr
0 ppm F
pH 2
21227
33371
76491
40350
pH 5
30543
52854
110420
57979
pH 7.5
33725
69234
110647
62797
1000 ppm F
pH 2
18
15
14
12
pH 5
7010
2054
2525
1926
pH 7.5
24495
53785
64752
45122


## 4. Conclusions

The corrosion behaviour of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr alloys was investigated in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and containing 1000 ppm F at 37°C. The results showed the following.(i)
All materials present a passive behavior in Ringer’s solution without fluorides independently on the pH values.(ii)
All materials present a passive behavior in Ringer’s solution of pH 5 and 7.5 containing fluorides.(iii)
All materials present an active behavior in Ringer’s solution of pH 2 containing 1000 ppm fluorides, which was attributed to the presence of HF species.(iv)
The corrosion resistance of all materials in Ringer’s solution decreases with both decrease of pH and addition of fluorides.(v)
Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys and, in most conditions, the Ti-Nb-Zr alloys present higher corrosion resistance than CP-Ti.



---

*Source: 434975-2013-12-28.xml*