# Effect of Warm-Mix Agent EC-120 on Performance of Asphalt Binder and Its Microscopic Mechanism

Authors: Tian Xiaoge; Ren Zhang; Yichao Xv; Yantian Chu; Zhen Yang; Shaohua Zhen
Journal: Advances in Civil Engineering
 (2019)

---

## Abstract

In order to figure out the influence of the warm-mix agent EC-120 on the performance of the asphalt binder and its micro mechanism in warm-mixing process, a matrix asphalt, A-70, and SBS-modified asphalt, SBS I-D, were modified with different contents of EC-120, respectively. Then, conventional macromechanic performance tests, dynamic shear rheological (DSR) test at high-temperature, and bending beam rheological (BBR) test at low-temperature were carried out on asphalt binder samples. Meanwhile, they were microscopically analyzed through Fourier transform infrared spectrometer (FTIR) and differential scanning calorimeter (DSC). The results indicated that EC-120 can reduce the viscosity of asphalt binder at high temperature. With the increase of EC-120 content, the high-temperature rutting resistance of two kinds of warm-mix asphalt (WMA) increased, but their crack resistance at low-temperature was reduced. FTIR indicated that this is due to the generation of oxides containing carbonyl functional groups after EC-120 was blended with asphalt binder. The DSC endothermic curves of WMA binders are obviously different from those of base binders, and a strong endothermic peak appears in the interval of 102°C–113°C, indicating that EC-120 will endothermically melt at the temperature of 102°C∼113°C, so it can play the role in reducing the viscosity of asphalt binder at the range of construction temperatures.


---

## Body

## 1. Introduction

Warm-mix asphalt (WMA) refers to the use of certain technical means in the mixing process of asphalt mixture, which can effectively reduce the construction temperatures of the mixture in mixing, spreading, and rolling processes and assure the performance of the mixture not lower than that of hot mix asphalt (HMA) [1–3]. The mixing temperature of WMA is generally 100°C∼120°C, and the paving and compacting temperature is about 80°C∼90°C. Compared with HMA, the construction temperatures are reduced about 30°C, but it has the same workability and performance as HMA [4]. A large number of researches and practices have shown that WMA mixture has the characteristics of good performance, low emission, and low energy consumption compared with HMA mixture [4–6]. As an energy-saving green material, WMA is receiving more and more attention in pavement engineering [7].In the early stage of WMA researches, most of them focused on conventional problems such as construction temperature, gradation design, and pavement performance, which are practical problems in the application of WMA technology [5, 7]. Rodriguez-Alloza et al. comparatively studied the mechanical properties of WMA with different warm-mix agents [8]. Buss et al. [9], Chomicz-Kowalska et al. [10], and Cucalon et al. [11] studied the effect of warm-mix agent on the moisture susceptibility of asphalt mixture. Podolsky et al. studied the rutting resistances of WMAs [12].In recent years, research on WMA has been deepened. Advanced microscopic testing techniques have been used to study the effects of warm-mix agents at a microscopic scale. Menapace et al. studied the surface morphology of WMA at different UV aging stages with optical microscope and atomic force microscope (AFM) [13]. Nazzal et al. examined the moisture susceptibility and healing characteristics of WMA and compared it with those of conventional HMA with the atomic force microscopy (AFM) [14, 15]. Hossain et al. evaluated the effects of two WMA additives on the chemical compositions of asphalt binder with spectroscopy techniques including Fourier transform infrared (FTIR) spectroscopy, nuclear magnetic resonance (NMR), and X-ray photo electron spectroscopy (XPS) [16]. Abd et al. studied nanoscale properties of WMA with atomic force microscopy [17].The object of this paper is to evaluate the effect of warm-mix agent, EC-120, on the performance of WMA, so the DSR tests and BBR tests were adopted to evaluate the effect of EC-120 on the macroperformance of asphalt binder. FTIR and DSC tests were adopted to analyzed its warm-mixing mechanism from a microscopical view.


## 2. Raw Materials and Test Methods

### 2.1. Raw Materials

#### 2.1.1. Asphalt Binder

Two kinds of asphalt binder, ESSO A-70 matrix asphalt provided by Taihe Asphalt Products Co., Ltd. and a finished SBS modified asphalt, SBS I-D, provided by Zhenjiang Asphalt Co., Ltd. were utilized. The main technical indexes are shown in Tables1 and 2, respectively [18–20].Table 1
Technical indexes of ESSO A-70 matrix asphalt.
Technical indexes
Unit
Results
Specification
Penetration (25°C, 5 s, 100 g)
0.1 mm
67
60–80
Softening point
°C
47.5
≥47
Ductility @15°C
cm
>100
≥100
Relative density @25°C
1.043
Measured
After TFOT
Mass changes
%
0.1
±0.8
Residual penetration ratio (25°C, 5 s, 100 g)
%
65.2
≥63
Residual ductility (5°C, 5 cm/min)
cm
6.8
≥6Table 2
Technical index of SBS I-D modified asphalt.
Technical index
Unit
Results
Specification
Penetration (25°C, 5 s, 100 g)
0.1 mm
53.9
30–60
Softening point
°C
83.4
≥70
Ductility @5°C
cm
35.0
≥25
Relative density @25°C
1.027
Measured
After TFOT
Mass changes
%
−0.422
±1.0
Residual penetration ratio (25°C, 5 s, 100 g)
%
70.1
≥65
Residual ductility (5°C, 5 cm/min)
cm
28.4
≥15


#### 2.1.2. Warm-Mix Agent, EC-120

EC-120 is an organic viscosity reducing asphalt modifier developed by Haichuan Company. It is a long-chain aliphatic polymer. It is in the form of tiny round particles at room temperature. The technical indexes are shown in Table3.Table 3
Technical indexes of EC-120.
Index
Viscosity @135°C (cp)
Penetration @25°C (0.1 mm)
Density @25°C (g/cm3)
Freezing point (°C)
Flash point (°C)
Typical values
12
<1
0.94
100
290


### 2.2. Experiment Methods

To evaluate the effect of EC-120 on macro performance of asphalt binder, different contents of EC-120 (0%, 1%, 2%, 3%, 4%, 5%), were mixed with A-70 and SBS I-D, respectively.Asphalt binders were placed into ovens at different constant temperatures (150°C for A-70 and 170°C for SBS I-D) for 1 hour to melt them. Then they were taken out and weighed for the required binder and mixed with different weights of EC-120. They were mixed with high-speed shear mixer. The mixing speed is 5000 rpm. The temperature was kept at 140°C (A-70) or 160°C degrees (SBS I-D) during mixing. After mixing for 30 minutes, they were put into an oven of 140°C or 160°C for 30 minutes to make them fully swollen.Six groups of warm-mixed A-70 samples and six groups of warm-mixed SBS I-D samples were prepared. The binder with 0% EC-120 is the base binder, and the others are WMA binders. The following macroscopic performance tests and microscopic measurements were then conducted on these samples:(1)
Dynamic shear rheometer (DSR) test [21] at high temperature: MCR301 produced in Germany was adopted. The diameter of plates is 25 mm, and the height of binder samples, the gap between rotating plate and fixed plate, is 1 mm. The value of loading strain was controlled to 12%. The loading frequency was set to 10 rad/s. Test temperatures were set at 52°C, 58°C, 64°C, and 70°C. The rutting factor, G∗/sinδ, calculated through the collected data of complex shear modulus, G∗, and phase angle, δ, was adopted to characterize the high-temperature performance of base binder and WMA binder.(2)
Bending Beam Rheometer (BBR) tests [21] at low-temperature: BBR-TE produced in the United States was adopted. The width of the beam is 12.5 mm, the height is 6.25 mm, and the distance between the supports is 102 mm. Constant load applied is 988 mN. Test temperatures were set at −12°C, −18°C, or −24°C respectively. The stiffness modulus, S, and creep rate, m, were calculated to characterize the low-temperature crack resistance of base binder and WMA binder.(3)
Fourier transform infrared spectroscopy (FTIR): FTIR, as an important way to study the molecular structure of materials, has been widely used in various fields in recent years. By irradiating the sample with infrared light and recording the transmittance of the sample to different wavelengths of infrared light, the corresponding infrared spectrum of the sample can be obtained. The molecular composition of the sample can be determined through comparing the spectrum and the fingerprint area [22]. TENSOR27 infrared spectrometer produced by BRUKER company was used to analyze the changes of molecular composition in the two kinds of asphalt binder, A-70 and SBS I-D, before and after added EC-120, so as to study the warm-mixing mechanism of EC-120 on asphalt binder from the molecular perspective.Asphalt samples were prepared through thin filming method. 1.0 gram of asphalt binder was added into 10 ml of carbon tetrachloride solution, when asphalt binder was completely dissolved, and solution was dropped onto the potassium bromide window sheet and dried under a electric heated lamp. So, a film sample of asphalt binder required for FTIR experiment was prepared.The pressing plate method was used for EC-120 sample preparation because it is a kind of granular solid. EC-120 and potassium bromide powder were mixed at a mass ratio of 1 : 100 and then pressed into a sheet by a hydraulic machine.(4)
Differential scanning calorimetry (DSC): Different materials have different thermal effects, so the thermal effects of materials can be utilized to analyze its composition. The peak and its corresponding temperature in DSC spectrum (heat flow versus temperature) can be used to analyze the thermal stability of materials. The peak temperature represents the temperature at which the state of the substance in the material was changed. Enthalpy change (ΔH) can be calculated through integrating the area of the peak. In general, material is in the multiphase blending state when temperature is in enthalpy change zone. There are great differences in the microcomposition, which will lead to sudden changes in the physical and chemical properties of the material before and after this interval, which has an adverse effect on its thermal stability. So, the peak and enthalpy change ΔH can be adopted to characterize the thermal stability of materials [23].DSC was adopted to evaluate the thermal effects of base binder and WMA binder. And their DSC spectrums were compared to analyze thermal effect of EC-120 on asphalt binder and to clarify the warm-mixing mechanism.Sample prepare method: 0.1 gram of asphalt binder was randomly dipped in the melt asphalt binder with a clean pin and then it was adhered into a flat-bottomed aluminum crucible with a capacity of 40μl and placed in an oven at 160°C for 15 min until its bottom was evenly covered with asphalt binder. After that, it was placed into the refrigerator for about 10 minutes; at last, it was taken out for DSC test.Test method: Test temperature was controlled at 20°C to 500°C, temperature rise rate was 10°C/min, the filling gas was inert gas nitrogen, and gas filling rate was 20 ml/min.According to the DSC spectrum of every sample, three parameters (Tm: peak value of endothermic, Hf: peak area of endothermic, and Te: melting complete temperature) were calculated. And their variations with dosage of EC-120 were studied to analyze the effect of EC-120.


## 2.1. Raw Materials

### 2.1.1. Asphalt Binder

Two kinds of asphalt binder, ESSO A-70 matrix asphalt provided by Taihe Asphalt Products Co., Ltd. and a finished SBS modified asphalt, SBS I-D, provided by Zhenjiang Asphalt Co., Ltd. were utilized. The main technical indexes are shown in Tables1 and 2, respectively [18–20].Table 1
Technical indexes of ESSO A-70 matrix asphalt.
Technical indexes
Unit
Results
Specification
Penetration (25°C, 5 s, 100 g)
0.1 mm
67
60–80
Softening point
°C
47.5
≥47
Ductility @15°C
cm
>100
≥100
Relative density @25°C
1.043
Measured
After TFOT
Mass changes
%
0.1
±0.8
Residual penetration ratio (25°C, 5 s, 100 g)
%
65.2
≥63
Residual ductility (5°C, 5 cm/min)
cm
6.8
≥6Table 2
Technical index of SBS I-D modified asphalt.
Technical index
Unit
Results
Specification
Penetration (25°C, 5 s, 100 g)
0.1 mm
53.9
30–60
Softening point
°C
83.4
≥70
Ductility @5°C
cm
35.0
≥25
Relative density @25°C
1.027
Measured
After TFOT
Mass changes
%
−0.422
±1.0
Residual penetration ratio (25°C, 5 s, 100 g)
%
70.1
≥65
Residual ductility (5°C, 5 cm/min)
cm
28.4
≥15


### 2.1.2. Warm-Mix Agent, EC-120

EC-120 is an organic viscosity reducing asphalt modifier developed by Haichuan Company. It is a long-chain aliphatic polymer. It is in the form of tiny round particles at room temperature. The technical indexes are shown in Table3.Table 3
Technical indexes of EC-120.
Index
Viscosity @135°C (cp)
Penetration @25°C (0.1 mm)
Density @25°C (g/cm3)
Freezing point (°C)
Flash point (°C)
Typical values
12
<1
0.94
100
290


## 2.1.1. Asphalt Binder

Two kinds of asphalt binder, ESSO A-70 matrix asphalt provided by Taihe Asphalt Products Co., Ltd. and a finished SBS modified asphalt, SBS I-D, provided by Zhenjiang Asphalt Co., Ltd. were utilized. The main technical indexes are shown in Tables1 and 2, respectively [18–20].Table 1
Technical indexes of ESSO A-70 matrix asphalt.
Technical indexes
Unit
Results
Specification
Penetration (25°C, 5 s, 100 g)
0.1 mm
67
60–80
Softening point
°C
47.5
≥47
Ductility @15°C
cm
>100
≥100
Relative density @25°C
1.043
Measured
After TFOT
Mass changes
%
0.1
±0.8
Residual penetration ratio (25°C, 5 s, 100 g)
%
65.2
≥63
Residual ductility (5°C, 5 cm/min)
cm
6.8
≥6Table 2
Technical index of SBS I-D modified asphalt.
Technical index
Unit
Results
Specification
Penetration (25°C, 5 s, 100 g)
0.1 mm
53.9
30–60
Softening point
°C
83.4
≥70
Ductility @5°C
cm
35.0
≥25
Relative density @25°C
1.027
Measured
After TFOT
Mass changes
%
−0.422
±1.0
Residual penetration ratio (25°C, 5 s, 100 g)
%
70.1
≥65
Residual ductility (5°C, 5 cm/min)
cm
28.4
≥15


## 2.1.2. Warm-Mix Agent, EC-120

EC-120 is an organic viscosity reducing asphalt modifier developed by Haichuan Company. It is a long-chain aliphatic polymer. It is in the form of tiny round particles at room temperature. The technical indexes are shown in Table3.Table 3
Technical indexes of EC-120.
Index
Viscosity @135°C (cp)
Penetration @25°C (0.1 mm)
Density @25°C (g/cm3)
Freezing point (°C)
Flash point (°C)
Typical values
12
<1
0.94
100
290


## 2.2. Experiment Methods

To evaluate the effect of EC-120 on macro performance of asphalt binder, different contents of EC-120 (0%, 1%, 2%, 3%, 4%, 5%), were mixed with A-70 and SBS I-D, respectively.Asphalt binders were placed into ovens at different constant temperatures (150°C for A-70 and 170°C for SBS I-D) for 1 hour to melt them. Then they were taken out and weighed for the required binder and mixed with different weights of EC-120. They were mixed with high-speed shear mixer. The mixing speed is 5000 rpm. The temperature was kept at 140°C (A-70) or 160°C degrees (SBS I-D) during mixing. After mixing for 30 minutes, they were put into an oven of 140°C or 160°C for 30 minutes to make them fully swollen.Six groups of warm-mixed A-70 samples and six groups of warm-mixed SBS I-D samples were prepared. The binder with 0% EC-120 is the base binder, and the others are WMA binders. The following macroscopic performance tests and microscopic measurements were then conducted on these samples:(1)
Dynamic shear rheometer (DSR) test [21] at high temperature: MCR301 produced in Germany was adopted. The diameter of plates is 25 mm, and the height of binder samples, the gap between rotating plate and fixed plate, is 1 mm. The value of loading strain was controlled to 12%. The loading frequency was set to 10 rad/s. Test temperatures were set at 52°C, 58°C, 64°C, and 70°C. The rutting factor, G∗/sinδ, calculated through the collected data of complex shear modulus, G∗, and phase angle, δ, was adopted to characterize the high-temperature performance of base binder and WMA binder.(2)
Bending Beam Rheometer (BBR) tests [21] at low-temperature: BBR-TE produced in the United States was adopted. The width of the beam is 12.5 mm, the height is 6.25 mm, and the distance between the supports is 102 mm. Constant load applied is 988 mN. Test temperatures were set at −12°C, −18°C, or −24°C respectively. The stiffness modulus, S, and creep rate, m, were calculated to characterize the low-temperature crack resistance of base binder and WMA binder.(3)
Fourier transform infrared spectroscopy (FTIR): FTIR, as an important way to study the molecular structure of materials, has been widely used in various fields in recent years. By irradiating the sample with infrared light and recording the transmittance of the sample to different wavelengths of infrared light, the corresponding infrared spectrum of the sample can be obtained. The molecular composition of the sample can be determined through comparing the spectrum and the fingerprint area [22]. TENSOR27 infrared spectrometer produced by BRUKER company was used to analyze the changes of molecular composition in the two kinds of asphalt binder, A-70 and SBS I-D, before and after added EC-120, so as to study the warm-mixing mechanism of EC-120 on asphalt binder from the molecular perspective.Asphalt samples were prepared through thin filming method. 1.0 gram of asphalt binder was added into 10 ml of carbon tetrachloride solution, when asphalt binder was completely dissolved, and solution was dropped onto the potassium bromide window sheet and dried under a electric heated lamp. So, a film sample of asphalt binder required for FTIR experiment was prepared.The pressing plate method was used for EC-120 sample preparation because it is a kind of granular solid. EC-120 and potassium bromide powder were mixed at a mass ratio of 1 : 100 and then pressed into a sheet by a hydraulic machine.(4)
Differential scanning calorimetry (DSC): Different materials have different thermal effects, so the thermal effects of materials can be utilized to analyze its composition. The peak and its corresponding temperature in DSC spectrum (heat flow versus temperature) can be used to analyze the thermal stability of materials. The peak temperature represents the temperature at which the state of the substance in the material was changed. Enthalpy change (ΔH) can be calculated through integrating the area of the peak. In general, material is in the multiphase blending state when temperature is in enthalpy change zone. There are great differences in the microcomposition, which will lead to sudden changes in the physical and chemical properties of the material before and after this interval, which has an adverse effect on its thermal stability. So, the peak and enthalpy change ΔH can be adopted to characterize the thermal stability of materials [23].DSC was adopted to evaluate the thermal effects of base binder and WMA binder. And their DSC spectrums were compared to analyze thermal effect of EC-120 on asphalt binder and to clarify the warm-mixing mechanism.Sample prepare method: 0.1 gram of asphalt binder was randomly dipped in the melt asphalt binder with a clean pin and then it was adhered into a flat-bottomed aluminum crucible with a capacity of 40μl and placed in an oven at 160°C for 15 min until its bottom was evenly covered with asphalt binder. After that, it was placed into the refrigerator for about 10 minutes; at last, it was taken out for DSC test.Test method: Test temperature was controlled at 20°C to 500°C, temperature rise rate was 10°C/min, the filling gas was inert gas nitrogen, and gas filling rate was 20 ml/min.According to the DSC spectrum of every sample, three parameters (Tm: peak value of endothermic, Hf: peak area of endothermic, and Te: melting complete temperature) were calculated. And their variations with dosage of EC-120 were studied to analyze the effect of EC-120.


## 3. Analysis of Test Results

### 3.1. Effect of EC-120 on High-Temperature Performance of Asphalt Binder

DSR tests were carried out on binders with different EC-120 contents at four different high-temperatures, 52°C, 58°C, 64°C, and 70°C. The rutting factor,G∗/sinδ, of WMAs with different EC-120 contents at different temperatures is shown in Figure 1.Figure 1
Relationship betweenG∗/sinδ and EC-120 dosage of WMAs. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)It can be seen from Figure1 that at the same temperature, the rutting factors of the two types of WMA increased with the increase of EC-120 content, indicating that the addition of EC-120 can improve the rutting resistance of binders. When EC-120 content exceeds 4%, the increase rate of G∗/sinδ of the two types of WMA is significantly reduced. It can be speculated that a stable grid structure can be formed in asphalt binder when the content of EC-120 is about 4%. The improvement effect of increasing EC-120 content on the high-temperature performance of asphalt is limited when the content of EC-120 is greater than 4%.


### 3.2. Effect of EC-120 on Low-Temperature Performance of Asphalt Binder

BBR tests were carried out on base binder and different WMA binder samples at different low temperatures of −12°C, −18°C, and −24°C. The creep stiffness modulus,S, and creep rate, m, were obtained and showed in Figures 2 and 3.Figure 2
Relationships between S of WMA binders and EC-120 content. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)Figure 3
Relationships betweenm of WMA binders and EC-120 content. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)It can be seen from Figures2 and 3 that with the increase of EC-120 content, the low-temperature stiffness modulus S of the two kinds of WMAs increased and the creep rate m value continuously decreased, indicating that EC-120 has a negative effect on the low-temperature performance of asphalt binder.


## 3.1. Effect of EC-120 on High-Temperature Performance of Asphalt Binder

DSR tests were carried out on binders with different EC-120 contents at four different high-temperatures, 52°C, 58°C, 64°C, and 70°C. The rutting factor,G∗/sinδ, of WMAs with different EC-120 contents at different temperatures is shown in Figure 1.Figure 1
Relationship betweenG∗/sinδ and EC-120 dosage of WMAs. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)It can be seen from Figure1 that at the same temperature, the rutting factors of the two types of WMA increased with the increase of EC-120 content, indicating that the addition of EC-120 can improve the rutting resistance of binders. When EC-120 content exceeds 4%, the increase rate of G∗/sinδ of the two types of WMA is significantly reduced. It can be speculated that a stable grid structure can be formed in asphalt binder when the content of EC-120 is about 4%. The improvement effect of increasing EC-120 content on the high-temperature performance of asphalt is limited when the content of EC-120 is greater than 4%.


## 3.2. Effect of EC-120 on Low-Temperature Performance of Asphalt Binder

BBR tests were carried out on base binder and different WMA binder samples at different low temperatures of −12°C, −18°C, and −24°C. The creep stiffness modulus,S, and creep rate, m, were obtained and showed in Figures 2 and 3.Figure 2
Relationships between S of WMA binders and EC-120 content. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)Figure 3
Relationships betweenm of WMA binders and EC-120 content. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)It can be seen from Figures2 and 3 that with the increase of EC-120 content, the low-temperature stiffness modulus S of the two kinds of WMAs increased and the creep rate m value continuously decreased, indicating that EC-120 has a negative effect on the low-temperature performance of asphalt binder.


## 4. Microscopic Warm-Mixing Mechanism of EC-120

### 4.1. FTIR Spectroscopy Analysis

FTIR spectroscopy was conducted on EC-120, ESSO A-70 matrix asphalt, SBS I-D modified asphalt, and WMAs; the content of EC-120 were 4% for both ESSO A-70 and SBS I-D. The samples of asphalt binders were prepared through the thin filming method, and the samples of EC-120 were produced through pressing plate method.The infrared spectrum of EC-120 is shown in Figure4.Figure 4
Infrared spectrum of EC-120.It can be seen from Figure4 that the peak of EC-120 is between 3250 cm−1 and 3700 cm−1, and there is a particularly prominent peak at 3500 cm−1. This interval is the stretching vibration regions of N-H and O-H. In addition, there are also peaks at 719 cm−1 and 1473 cm−1, which is caused by -(CH)n-, and the value of n is greater than 4 due to the presence of a peak at 719 cm−1. By comparing with the infrared spectrum, the molecular structure of EC-120 is similar to that of polyethylene wax, so it is a kind of PE wax.The infrared spectra of ESSO A-70 and SBS I-D before and after the addition of EC-120 are shown in Table4 and Figure 5.Table 4
Transmittances of base binder and warm-mixed binder (%).
Wave number (cm−1)
Binders
A-70
Warm-mixed A-70
SBS I-D
Warm-mixed SBS I-D
1000
84.55
94.45
78.98
96.72
1500
82.53
94.82
76.22
94.58
2000
88.69
106.01
87.92
107.73
2500
87.92
103.83
86.11
105.15
3000
78.73
83.54
66.51
81.46
3500
88.48
103.73
86.91
107.08
4000
88.03
104.05
85.66
105.89Figure 5
Infrared spectrums of base binder and warm-mixed binder. (a) A-70 and warm-mixed A-70. (b) SBS I-D and warm-mixed SBS I-D.
(a)
(b)It can be seen from Table4 and Figure 5 that due to the addition of EC-120, a new peak presented at 1700 cm−1 in the Infrared spectrums of WMA binders, while the other peaks do not change significantly. The peak at 1700 cm−1 is a carbonyl group, and the compounds include ketones, aldehydes, carboxylic acids, amides, and acid chlorides. Generally, carbonyl content is very few or nonexistent in unaged asphalt. The aging of asphalt can produce a large number of carbonyl compounds. Therefore, EC-120 chemically reacts with asphalt binder to produce a large amount of oxides containing carbonyl functional groups after blended with original asphalt, which leads to deterioration of its physical properties; this is the reason that WMA binders have better rutting resistance than that of base binder.


### 4.2. Thermal Effect Analysis of EC-120

Differential scanning calorimetry (DSC) tests [24] were conducted on base binder and WMA binder with different EC-120 contents. The test temperature was 60°C to 200°C. The DSC curves of base binders and WMA binders with different EC-120 contents are shown in Figures 6(a) and 6(b), respectively.Figure 6
DSC endothermic curve of base binders and WMA binders. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)It can be seen from Figure6 that(1)
The DSC endothermic curves of base binders without EC-120 are smooth and flat; there are no endothermic peaks, indicating that their thermal stabilities are good.(2)
A strong endothermic peak appears in the interval of 102°C∼113°C when EC-120 was added, indicating that the composition has changed in this temperature range. Since the melting point of EC-120 is also about 110°C, it can be concluded that the appearance of endothermic peak is due to the melting of EC-120 after absorbing heat.(3)
With the increase of EC-120 contents, the endothermic peak is getting higher and higher, and the areas of them are gradually increased. Since the endothermic peak is caused by the melting of the EC-120, an increase in EC-120 content tends to result in an increase in the endothermic peak area.


## 4.1. FTIR Spectroscopy Analysis

FTIR spectroscopy was conducted on EC-120, ESSO A-70 matrix asphalt, SBS I-D modified asphalt, and WMAs; the content of EC-120 were 4% for both ESSO A-70 and SBS I-D. The samples of asphalt binders were prepared through the thin filming method, and the samples of EC-120 were produced through pressing plate method.The infrared spectrum of EC-120 is shown in Figure4.Figure 4
Infrared spectrum of EC-120.It can be seen from Figure4 that the peak of EC-120 is between 3250 cm−1 and 3700 cm−1, and there is a particularly prominent peak at 3500 cm−1. This interval is the stretching vibration regions of N-H and O-H. In addition, there are also peaks at 719 cm−1 and 1473 cm−1, which is caused by -(CH)n-, and the value of n is greater than 4 due to the presence of a peak at 719 cm−1. By comparing with the infrared spectrum, the molecular structure of EC-120 is similar to that of polyethylene wax, so it is a kind of PE wax.The infrared spectra of ESSO A-70 and SBS I-D before and after the addition of EC-120 are shown in Table4 and Figure 5.Table 4
Transmittances of base binder and warm-mixed binder (%).
Wave number (cm−1)
Binders
A-70
Warm-mixed A-70
SBS I-D
Warm-mixed SBS I-D
1000
84.55
94.45
78.98
96.72
1500
82.53
94.82
76.22
94.58
2000
88.69
106.01
87.92
107.73
2500
87.92
103.83
86.11
105.15
3000
78.73
83.54
66.51
81.46
3500
88.48
103.73
86.91
107.08
4000
88.03
104.05
85.66
105.89Figure 5
Infrared spectrums of base binder and warm-mixed binder. (a) A-70 and warm-mixed A-70. (b) SBS I-D and warm-mixed SBS I-D.
(a)
(b)It can be seen from Table4 and Figure 5 that due to the addition of EC-120, a new peak presented at 1700 cm−1 in the Infrared spectrums of WMA binders, while the other peaks do not change significantly. The peak at 1700 cm−1 is a carbonyl group, and the compounds include ketones, aldehydes, carboxylic acids, amides, and acid chlorides. Generally, carbonyl content is very few or nonexistent in unaged asphalt. The aging of asphalt can produce a large number of carbonyl compounds. Therefore, EC-120 chemically reacts with asphalt binder to produce a large amount of oxides containing carbonyl functional groups after blended with original asphalt, which leads to deterioration of its physical properties; this is the reason that WMA binders have better rutting resistance than that of base binder.


## 4.2. Thermal Effect Analysis of EC-120

Differential scanning calorimetry (DSC) tests [24] were conducted on base binder and WMA binder with different EC-120 contents. The test temperature was 60°C to 200°C. The DSC curves of base binders and WMA binders with different EC-120 contents are shown in Figures 6(a) and 6(b), respectively.Figure 6
DSC endothermic curve of base binders and WMA binders. (a) Warm-mixed matrix asphalt A-70. (b) Warm-mixed SBS I-D.
(a)
(b)It can be seen from Figure6 that(1)
The DSC endothermic curves of base binders without EC-120 are smooth and flat; there are no endothermic peaks, indicating that their thermal stabilities are good.(2)
A strong endothermic peak appears in the interval of 102°C∼113°C when EC-120 was added, indicating that the composition has changed in this temperature range. Since the melting point of EC-120 is also about 110°C, it can be concluded that the appearance of endothermic peak is due to the melting of EC-120 after absorbing heat.(3)
With the increase of EC-120 contents, the endothermic peak is getting higher and higher, and the areas of them are gradually increased. Since the endothermic peak is caused by the melting of the EC-120, an increase in EC-120 content tends to result in an increase in the endothermic peak area.


## 5. Conclusions

The following conclusions were obtained through macroperformance tests (DSR tests and BBR tests) and microscopic tests (FTIR and DSC) on base asphalt binders, A-70 and SBS I-D, and their warm-mixed asphalt binders with different contents of EC-120.(1)
The addition of EC-120 will enhance the high-temperature rutting resistance of asphalt binder and decrease its low-temperature performance. The impacts increase with the contents of EC-120. The results of FTIR revealed that this is due to the generation of oxides containing carbonyl functional groups after EC-120 was added into asphalt binder.(2)
Comparing the FTIR spectra of asphalt binders before and after adding EC-120, we can find that there is an obvious new peak presented at 1700 cm−1, which is a carbonyl group chemically produced between EC-120 and asphalt binder.(3)
DSC curves of base asphalts and corresponding WMA binders are quite different. A strong endothermic peak appears in the interval of 102°C–113°C in the DSC curves of WMA binders. The endothermic peaks and their areas are gradually increased with the increase of EC-120 contents.(4)
DSC tests showed that EC-120 will endothermically melt at the temperature of 102°C∼113°C and then play the role in reducing the viscosity of asphalt binder. The greater the dose of EC-120, the greater the enthalpy and the more obvious the effect of reducing viscosity. This is the mechanism that EC-120 can be used to reduce the mixing temperature of asphalt binder.



---