# Au-Ag Core-Shell Nanospheres for Surface-Enhanced Raman Scattering Detection of Sudan I and Sudan II in Chili Powder

Authors: Lu Pei; Yiming Ou; Wansong Yu; Yuxia Fan; Yiqun Huang; Keqiang Lai
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Au-Ag core-shell (Au@Ag) bimetallic nanospheres synthesized by a facile seed-growth method are proposed as a substrate for surface-enhanced Raman spectroscopy (SERS) to detect azo-group dyes including Sudan I and Sudan II. Au@Ag nanospheres with a series of particle sizes (diameter: 30–120 nm) and silver shell thicknesses (6–51 nm) were synthesized and compared for their morphological and optical properties to obtain optimum enhancement effect. Normal Raman, SERS, infrared, and ultraviolet-visible were used to investigate the optical absorption properties of Sudan I and Sudan II as well as the enhancement mechanism of Au@Ag substrates. The nanospheres with particle size of 73 ± 6 nm in diameter and silver layer of 27 ± 2 nm resulted in the highest enhancement effect and could be used to detect Sudan I and Sudan II standard solutions at levels as low as 0.4 and 0.1 mg/L, respectively. Moreover, Sudan I and Sudan II in chili powder could be detected at 0.6 and 0.4 mg/kg, respectively. Sudan I and Sudan II with similar structures in complicated food matrices could be distinguished through applying principal component analysis, indicating good selectivity of the SERS method for detection of banned additives in food stuffs at trace levels.


---

## Body

## 1. Introduction

Sudan dyes are a group of synthetic aromatic compounds containing azo-group (-N=N-) as shown in Figure1, which are commonly used in hydrocarbon solvents, oils, waxes, textiles, shoes, and plastics to provide an orange-red appearance. Some of the Sudan dyes, such as Sudan I, was classified as class three carcinogen and can be metabolized by intestinal bacteria to produce carcinogenic compounds [1, 2]. The use of Sudan dyes as coloring agents in foods has been banned in the USA, Australia, Canada, China, and the European Union (EU) since 1995, but the abuse of Sudan dyes in food is not uncommon because of the low cost and wide availability of these dyes [3]. High performance liquid chromatography with the ultraviolet-visible (UV-vis), or diode array detection, or electrochemical detection has been used as the main method for detecting the presence of Sudan dyes in foodstuffs, although rapid methods such as enzyme-linked immunosorbent assay have also been reported [4]. Time-consumption, lack of sensitivity or accuracy, and/or high cost have always been the issues tied to the current analytical methods.Figure 1
The molecular structures of Sudan I and Sudan II.Surface-enhanced Raman scattering or surface-enhanced Raman spectroscopy (SERS) emerges as one of the most potent analytical tools in various fields because of its rapidity, high sensitivity, and selectivity for molecular detection [5, 6]. The most important factor for successful applications of SERS is the use of SERS substrate with proper nanostructured metal surface that allows for effective adsorption of the targeted molecules onto the substrate surface and results in high Raman scattering enhancement and reproducibility [7]. The use of Au@Ag core-shell bimetallic nanoparticles (NPs) as SERS substrate has both the advantages of high enhancement effects of Ag NPs as well as homogeneity and stability of Au NPs [8, 9]. In addition, the core-shell bimetallic structure offers the possibility of a tunable localized surface plasmon resonance (LSPR) that gives rise to SERS by varying the size of the Au core or/and the thickness of the Ag shell, which makes Au@Ag NPs an ideal candidate as substrate for SERS studies [10, 11].The objective of this study was to apply easy-to-prepare Au@Ag substrates with superior SERS performances (high sensitivity, reproducibility, and selectivity) to quickly detect trace levels of Sudan I and Sudan II. To obtain appropriate particle size and thickness of silver shell for high sensitive SERS effect, Au@Ag substrates with a series of particle sizes and Ag shell thicknesses were synthesized and compared for their morphological and optical properties. Four spectroscopic techniques including normal Raman, SERS, infrared (IR), and UV-vis were used to investigate the optical absorption properties of Sudan I and Sudan II as well as the enhancement mechanism of Au@Ag substrates. Principal component analysis (PCA) was used as an exploratory tool to elucidate the spectral differentiation between Sudan I and II.


## 2. Materials and Methods

### 2.1. Synthesis of Au@Ag Nanoparticles with Different Sizes

Colloidal Au nanospheres with diameter of18
±
2 nm were synthesized as seeds according to the Frens method [12]. As-prepared Au colloid and L-ascorbic acid (1.2 mL, 0.1 mol/L) were added in a glass vial, stirring continuously. AgNO3 solution was added drop-by-drop into this vial and the final mixture was continuously stirred for 5 min to form Au@Ag NPs. The sizes of Au@Ag NPs were controlled by using different amount (0.45, 0.9, 1.5 and 4.5 mL) of Au seeds and varying the concentration (0.5, 1 and 2 mmol/L) of silver nitrate during silver coating process. The color of Au@Ag NPs ranged from orange to cream when the amount of Au seeds used for silver coating decreased or the concentration of silver nitrate increased.The surface morphology of Au@Ag NPs were analyzed with transmission electron microscopy (TEM, JEM-2100F, JEOL Ltd., Tokyo, Japan) and the average particle sizes was calculated based upon the diameters of 100 particles. In addition, the optical absorption of Au NPs and Au@Ag NPs were analyzed with a UV-vis absorbance spectroscopy (UV3000PC, MAPADA Instruments Ltd., Shanghai, China) over a range of 300–800 nm.


### 2.2. Preparation of Standard Solutions

Sudan I and Sudan II purchased from Sigma-Aldrich (≥96%; Sigma-Aldrich Chemicals, St. Louis, MO) were dissolved into acetonitrile (HPLC reagent; Sigma-Aldrich Chemicals, St. Louis, MO) aqueous solution (v/v = 1 : 1) to prepare a series of standard solutions (0.1–1.0 mg/L) for each dye.


### 2.3. Chili Samples Pretreatment

Chili powder was purchased from a local supermarket in Shanghai, China. Sudan I and Sudan II were extracted from chili powder based on an international method released by the Government Chemist of liquid chromatography, and the recovery rate was about 80–110%. Briefly, 1 g of chili powder was vigorously mixed with 10 mL of acetonitrile for 2 min. The mixture was then shaken (280 times/min) in a vibrator for 30 min at room temperature and centrifuged at 5000 rpm for 10 min. The supernatants were combined after a second centrifugation with 10 mL of acetonitrile added and then evaporated to dryness with a rotary evaporator (R206B, Shanghai SENCO Technology Ltd., Shanghai, China) at 40°C. Following this, the residue was reconstituted in 1 mL of acetonitrile and further purified using C18 cartridge for solid phase extraction (500 mg, 3 mL; Supelco, Bellefonte, PA, USA). The extracts were finally filtered through 0.45μm pore size of syringe filters and spiked with Sudan I [0-1 mg/kg] or Sudan II [0-1 mg/kg]. The extracts spiked with Sudan dyes were kept at refrigerator temperature before further use.


### 2.4. Spectral Measurements

Infrared (IR) spectra of Sudan dyes were obtained using a Nicolet 6700 FTIR spectrometer (Thermo Fisher Scientific Inc., Waltham, MA, USA) equipped with a DTGS detector operating at room temperature. Sudan I or Sudan II was ground with KBr powder and pressed into a thin pellet. The spectrum of the pellet was obtained in transmittance mode with spectral resolution of 4 cm−1 and was an average of 32 scans.A Nicolet DXR microscopy Raman spectrometer (Thermo Fisher Scientific Inc., Waltham, MA, USA) with a 633 nm He–Ne laser was employed to acquire Raman and SERS spectra. All spectra were collected at 5 mW, 20x objective (Olympus) with a slit width of 50 cm−1. The accumulation time was 2 s for each of the five scans acquired for a sample.To assemble SERS substrates, Au@Ag NPs were concentrated 3 times and then mixed with standard solution (v/v = 1 : 1) or chili sample extract (v/v = 2 : 1). The mixture (5μL) was pipetted onto a microscope glass slide, and SERS spectra were acquired after evaporation of the solvent. To ensure the reproducibility of a SERS spectrum, the average of a total of 30 spectra collected from 10 different spots at each of the three batches of substrates was used as the final spectrum for a sample.


### 2.5. Principal Component Analysis (PCA)

Multivariate PCA analysis [DeLight 3.2 (DSquared Development Inc., LaGrande, OR, USA)] was used to differentiate spectral data for Sudan I and Sudan II extracts. The results of the data analysis reflect the selectivity of SERS method for different analytes. In order to ensure that the result of PCA was reliable and the spectra were representative, three different concentrations of extracts were used for Sudan I (0.4, 0.5 and 1 mg/kg) and for Sudan II (0.6, 0.8 and 1 mg/kg), respectively.


## 2.1. Synthesis of Au@Ag Nanoparticles with Different Sizes

Colloidal Au nanospheres with diameter of18
±
2 nm were synthesized as seeds according to the Frens method [12]. As-prepared Au colloid and L-ascorbic acid (1.2 mL, 0.1 mol/L) were added in a glass vial, stirring continuously. AgNO3 solution was added drop-by-drop into this vial and the final mixture was continuously stirred for 5 min to form Au@Ag NPs. The sizes of Au@Ag NPs were controlled by using different amount (0.45, 0.9, 1.5 and 4.5 mL) of Au seeds and varying the concentration (0.5, 1 and 2 mmol/L) of silver nitrate during silver coating process. The color of Au@Ag NPs ranged from orange to cream when the amount of Au seeds used for silver coating decreased or the concentration of silver nitrate increased.The surface morphology of Au@Ag NPs were analyzed with transmission electron microscopy (TEM, JEM-2100F, JEOL Ltd., Tokyo, Japan) and the average particle sizes was calculated based upon the diameters of 100 particles. In addition, the optical absorption of Au NPs and Au@Ag NPs were analyzed with a UV-vis absorbance spectroscopy (UV3000PC, MAPADA Instruments Ltd., Shanghai, China) over a range of 300–800 nm.


## 2.2. Preparation of Standard Solutions

Sudan I and Sudan II purchased from Sigma-Aldrich (≥96%; Sigma-Aldrich Chemicals, St. Louis, MO) were dissolved into acetonitrile (HPLC reagent; Sigma-Aldrich Chemicals, St. Louis, MO) aqueous solution (v/v = 1 : 1) to prepare a series of standard solutions (0.1–1.0 mg/L) for each dye.


## 2.3. Chili Samples Pretreatment

Chili powder was purchased from a local supermarket in Shanghai, China. Sudan I and Sudan II were extracted from chili powder based on an international method released by the Government Chemist of liquid chromatography, and the recovery rate was about 80–110%. Briefly, 1 g of chili powder was vigorously mixed with 10 mL of acetonitrile for 2 min. The mixture was then shaken (280 times/min) in a vibrator for 30 min at room temperature and centrifuged at 5000 rpm for 10 min. The supernatants were combined after a second centrifugation with 10 mL of acetonitrile added and then evaporated to dryness with a rotary evaporator (R206B, Shanghai SENCO Technology Ltd., Shanghai, China) at 40°C. Following this, the residue was reconstituted in 1 mL of acetonitrile and further purified using C18 cartridge for solid phase extraction (500 mg, 3 mL; Supelco, Bellefonte, PA, USA). The extracts were finally filtered through 0.45μm pore size of syringe filters and spiked with Sudan I [0-1 mg/kg] or Sudan II [0-1 mg/kg]. The extracts spiked with Sudan dyes were kept at refrigerator temperature before further use.


## 2.4. Spectral Measurements

Infrared (IR) spectra of Sudan dyes were obtained using a Nicolet 6700 FTIR spectrometer (Thermo Fisher Scientific Inc., Waltham, MA, USA) equipped with a DTGS detector operating at room temperature. Sudan I or Sudan II was ground with KBr powder and pressed into a thin pellet. The spectrum of the pellet was obtained in transmittance mode with spectral resolution of 4 cm−1 and was an average of 32 scans.A Nicolet DXR microscopy Raman spectrometer (Thermo Fisher Scientific Inc., Waltham, MA, USA) with a 633 nm He–Ne laser was employed to acquire Raman and SERS spectra. All spectra were collected at 5 mW, 20x objective (Olympus) with a slit width of 50 cm−1. The accumulation time was 2 s for each of the five scans acquired for a sample.To assemble SERS substrates, Au@Ag NPs were concentrated 3 times and then mixed with standard solution (v/v = 1 : 1) or chili sample extract (v/v = 2 : 1). The mixture (5μL) was pipetted onto a microscope glass slide, and SERS spectra were acquired after evaporation of the solvent. To ensure the reproducibility of a SERS spectrum, the average of a total of 30 spectra collected from 10 different spots at each of the three batches of substrates was used as the final spectrum for a sample.


## 2.5. Principal Component Analysis (PCA)

Multivariate PCA analysis [DeLight 3.2 (DSquared Development Inc., LaGrande, OR, USA)] was used to differentiate spectral data for Sudan I and Sudan II extracts. The results of the data analysis reflect the selectivity of SERS method for different analytes. In order to ensure that the result of PCA was reliable and the spectra were representative, three different concentrations of extracts were used for Sudan I (0.4, 0.5 and 1 mg/kg) and for Sudan II (0.6, 0.8 and 1 mg/kg), respectively.


## 3. Results and Discussion

### 3.1. Morphological and Optical Characteristics of Au@Ag NPs

Au@Ag nanoparticles were prepared by deposition of Ag through chemical reduction in the presence of Au seeds. By adjusting the amounts of AgNO3 solution and Au seeds used, the thickness of the shell and thus the size of bimetallic particles could be controlled easily. As the amount of Au colloid used was increased from 0.45 mL to 0.9 mL, 1.5 mL, and 4.5 mL, with the use of 1 mmol/L AgNO3 for silver coating, the average diameters of the resulted bimetallic NPs were decreased from 120
±
11 nm to 73
±
6 nm, 61
±
5 nm, and 50
±
4 nm, respectively, while the corresponding Ag shell thickness was about 51 nm, 27 nm, 21 nm, and 16 nm, respectively (Figures 2(a)–2(d)). This is because, with increased numbers of Au seeds, the amounts of Ag precipitated onto each Au nanoparticle would decrease, resulting in smaller Au@Ag nanoparticles [13, 14]. Similarly, the thickness of silver shells could also be controlled by varying the AgNO3 concentration while keeping the amount of Au seeds constant during silver coating process, and a higher AgNO3 concentration led to larger bimetallic NPs (Figures 2(b), 2(e), and 2(f)). However, when the concentration of AgNO3 solution was too high, such as 2 mmol/L, some necklace-like chains were formed due to excessive Ag reduced from Ag+. The excessive Ag was deposited in the gaps between Au@Ag NPs and thus produced adhesion between particles rather than continuously coated on the surface of Ag shells to form larger particle sizes [15].Figure 2
TEM images of Au@Ag nanoparticles synthesized with 1 mmol/L AgNO3 solution and different amounts of Au seeds including (a) 0.45 mL, (b) 0.9 mL, (c) 1.5 mL, and (d) 4.5 mL and synthesized with 0.9 mL Au seeds and different concentrations of AgNO3 solutions including (e) 0.5 mmol/L and (f) 2 mmol/L.
(a)
(b)
(c)
(d)
(e)
(f)The Au core and Ag shell structure of Au@Ag nanoparticles was confirmed with the use of scanning TEM-high angle annular dark field (STEM-HAADF) imaging and energy dispersive spectroscopy (EDS) elemental mapping (Figure3). The relative position of Au and Ag in a NP can be directly observed as a brighter, denser outer shell and a darker, sparser inner region in the STEM-HAADF image due to their different atomic number. The EDS mapping results indicated that the Au is in the center of the particle area as the core (in red), while the Ag is located on the outside as the shell (in green).Figure 3
STEM-HAADF and EDS elemental mapping images for Au L map and Ag L map and an overlay of the Au and Ag maps of Au@Ag NPs (particle sizes about 120 nm). The scale bar in STEM-HAADF applies to all images.The surface plasmon resonance (SPR) peaks for colloidal Au seeds and Au@Ag bimetallic NPs synthesized using different amounts of Au seeds are shown in Figure4. For the colloid of Au seeds, only one SPR peak was observed at 521 nm, which was in the typical range of 517–575 nm for Au NPs. For the colloids of bimetallic NPs, the SPR peaks gradually red-shifted from 423 nm to 432 nm and then 446 nm when the amount of Au seeds used decreased from 4.5 mL to 0.9 mL. The SPR peaks of the 573 nm Au@Ag bimetallic NPs were close to that of the Ag NPs generally within the range of 390–500 nm, indicating that the optical properties of these NPs were dominated by Ag shells [16]. As the particle sizes were further enlarged to about 120 nm, the peak intensity declined because of the reducing concentration of ions in really large-sized Au@Ag sol, and a shoulder peak became visible at 407 nm due to a different electron oscillation pattern from the dipole resonance of the primary peak [17].Figure 4
UV-vis spectra of colloidal Au seeds and Au@Ag NPs synthesized with 1 mmol/L AgNO3 solution and various amounts of Au seeds including (a) 0.45 mL, (b) 0.9 mL, (c) 1.5 mL, and (d) 4.5 mL.


### 3.2. Raman Spectra of Sudan I and Sudan II

The similarity of Sudan I and Sudan II in their molecular structures results in similar Raman spectral features as shown in Figure5. The spectra of two chemicals had two prominent peaks at around 1496 and 1227 cm−1 due to the stretching of double benzene ring and the C-H in-plane bending of phenyl groups [18, 19].Figure 5
IR and Raman spectra for Sudan I and Sudan II; representative SERS spectra of 1 mg/L Sudan II solution adsorbed on Au@Ag substrates synthesized with 1 mmol/L AgNO3 solution and various amounts of Au seeds including (a) 0.45 mL, (b) 0.9 mL, (c) 1.5 mL, and (d) 4.5 mL, as well as with 0.9 mL Au seeds and different concentrations of AgNO3 solutions including (e) 0.5 and (f) 2 mmol/L.Although Sudan I and Sudan II had similar Raman spectral features, each Sudan dye showed spectral singularities because of its unique molecular structure. The relative intensity of the peak at around 1599 cm−1 due to the stretching of N=N bond varied between two Sudan dyes, and the absorption intensity of Sudan II at around 1609 cm−1 was relatively weak compared to Sudan I [19, 20]. In addition, the peaks at around 1390 cm−1 in Sudan I and 1380 cm−1 in Sudan II are attributed to the C-N and C=C stretching in benzene rings [18]. Furthermore, the peaks arising from the C-H, O-H in-plane bending, and benzene rings distortions appear at 1171 cm−1 in Sudan I and 1154 cm−1 in Sudan II, respectively.


### 3.3. Screening SERS Substrates with High Enhancement Effect for Sudan Solutions

Au@Ag NPs with different particle sizes were used as substrates to acquire SERS spectra of Sudan II (1 mg/L), and their SERS enhancement factors (EF) were calculated based upon the following equation [21]:(1)
EF
=
I
SERS
I
n
o
r
m
N
n
o
r
m
N
SERS
,where I
SERS and I
n
o
r
m are the measured intensity of a specific characteristic peak for SERS and normal Raman spectra collected under the same test condition with or without the use of NPs as substrate, respectively; N
n
o
r
m and N
SERS are the corresponding number of Sudan II molecules. Based on the strongest characteristic peak at 1227 cm−1, the EFs for six Au@Ag NPs were estimated to be 2.4 × 104, 4.6 × 104, 3.2 × 104, 1.8 × 104, 2.0 × 104, and 2.6 × 104 corresponding to the particle size of 120
±
11, 73
±
6, 61
±
5, 50
±
4, 30
±
2, and 94
±
5 nm, respectively. The Au@Ag NPs of about 73 nm led to the highest enhancement effect. This is probably because Au@Ag NPs with relatively thinner Ag shell (such as the 61 nm Au@Ag NPs) has less intrinsic SERS activity of Ag NPs which normally can provide stronger electromagnetic enhancement than Au NPs, while Au@Ag NPs with too thick silver shell (such as the 120 nm NPs) are unable to provide proper or enough junctions for Sudan II molecules adsorbed onto the surfaces of Ag shells [22].


### 3.4. SERS Analysis of Sudan I and Sudan II with Optimal Au@Ag Substrates

The Au@Ag NPs with particles sizes of about 73 nm were selected as SERS substrate for analysis of a series standard solutions of Sudan I (0.4, 0.6, 0.8, and 1 mg/L) and Sudan II (0.1, 0.2, 0.5, and 1 mg/L) as well as for Sudan dyes in chili extracts. As shown in Figure6, the flat signal of blank substrates indicates that the background of substrates did not interfere with the SERS spectral features of Sudan dyes, and the intensity of the characteristic peaks decreased as the concentration of Sudan I and Sudan II decreased. The strong and medium-strong peaks at around 1229, 1390, 1496, and 1599 cm−1 were discernible at the concentration as low as 0.4 mg/L for Sudan I and 1227, 1380, and 1486 cm−1 at 0.1 mg/L for Sudan II standards.Figure 6
Representative SERS spectra of Sudan I and Sudan II standard solutions with Au@Ag NPs of about 73 nm as substrate.Figure7 presents SERS spectra of chili extracts spiked with Sudan I [0 (blank), 0.6, 0.8, 1, and 5 mg/kg] and Sudan II [0 (blank), 0.4, 0.5, 1, and 5 mg/kg], using Au@Ag NPs of about 73 nm as SERS substrates. No discernible SERS signals from nontargeted compounds could be found, and the major peaks in the SERS spectra of chili extracts spiked with Sudan I or Sudan II were consistent with those of their standard solutions. However, interference from chili matrices did exist since the SERS signals for chili extracts spiked with Sudan dyes were weaker than those for standard solutions with the same levels of Sudan dyes. The minimum concentration for Sudan I and Sudan II in chili extracts with major characteristic peaks discernible was 0.6 mg/kg and 0.4 mg/kg, respectively, higher than their standard counterparts.Figure 7
Representative SERS spectra of chili extracts spiked with Sudan I and Sudan II, using Au@Ag NPs of about 73 nm as substrate.Figure8 shows the plot of PCA (n
=
36) scores for the first two principal components that accounted for 76.9% of the spectral variation. The chili extracts spiked with Sudan I and Sudan II could be distinguished clearly, indicating the possibility of analyzing chili powder contaminated with different types and different levels of Sudan dyes.Figure 8
Plot of PCA score for SERS spectra of chili extracts spiked with Sudan I (0.6–1 mg/kg) and Sudan II (0.4–1 mg/kg), using Au@Ag NPs of about 73 nm as substrate.


## 3.1. Morphological and Optical Characteristics of Au@Ag NPs

Au@Ag nanoparticles were prepared by deposition of Ag through chemical reduction in the presence of Au seeds. By adjusting the amounts of AgNO3 solution and Au seeds used, the thickness of the shell and thus the size of bimetallic particles could be controlled easily. As the amount of Au colloid used was increased from 0.45 mL to 0.9 mL, 1.5 mL, and 4.5 mL, with the use of 1 mmol/L AgNO3 for silver coating, the average diameters of the resulted bimetallic NPs were decreased from 120
±
11 nm to 73
±
6 nm, 61
±
5 nm, and 50
±
4 nm, respectively, while the corresponding Ag shell thickness was about 51 nm, 27 nm, 21 nm, and 16 nm, respectively (Figures 2(a)–2(d)). This is because, with increased numbers of Au seeds, the amounts of Ag precipitated onto each Au nanoparticle would decrease, resulting in smaller Au@Ag nanoparticles [13, 14]. Similarly, the thickness of silver shells could also be controlled by varying the AgNO3 concentration while keeping the amount of Au seeds constant during silver coating process, and a higher AgNO3 concentration led to larger bimetallic NPs (Figures 2(b), 2(e), and 2(f)). However, when the concentration of AgNO3 solution was too high, such as 2 mmol/L, some necklace-like chains were formed due to excessive Ag reduced from Ag+. The excessive Ag was deposited in the gaps between Au@Ag NPs and thus produced adhesion between particles rather than continuously coated on the surface of Ag shells to form larger particle sizes [15].Figure 2
TEM images of Au@Ag nanoparticles synthesized with 1 mmol/L AgNO3 solution and different amounts of Au seeds including (a) 0.45 mL, (b) 0.9 mL, (c) 1.5 mL, and (d) 4.5 mL and synthesized with 0.9 mL Au seeds and different concentrations of AgNO3 solutions including (e) 0.5 mmol/L and (f) 2 mmol/L.
(a)
(b)
(c)
(d)
(e)
(f)The Au core and Ag shell structure of Au@Ag nanoparticles was confirmed with the use of scanning TEM-high angle annular dark field (STEM-HAADF) imaging and energy dispersive spectroscopy (EDS) elemental mapping (Figure3). The relative position of Au and Ag in a NP can be directly observed as a brighter, denser outer shell and a darker, sparser inner region in the STEM-HAADF image due to their different atomic number. The EDS mapping results indicated that the Au is in the center of the particle area as the core (in red), while the Ag is located on the outside as the shell (in green).Figure 3
STEM-HAADF and EDS elemental mapping images for Au L map and Ag L map and an overlay of the Au and Ag maps of Au@Ag NPs (particle sizes about 120 nm). The scale bar in STEM-HAADF applies to all images.The surface plasmon resonance (SPR) peaks for colloidal Au seeds and Au@Ag bimetallic NPs synthesized using different amounts of Au seeds are shown in Figure4. For the colloid of Au seeds, only one SPR peak was observed at 521 nm, which was in the typical range of 517–575 nm for Au NPs. For the colloids of bimetallic NPs, the SPR peaks gradually red-shifted from 423 nm to 432 nm and then 446 nm when the amount of Au seeds used decreased from 4.5 mL to 0.9 mL. The SPR peaks of the 573 nm Au@Ag bimetallic NPs were close to that of the Ag NPs generally within the range of 390–500 nm, indicating that the optical properties of these NPs were dominated by Ag shells [16]. As the particle sizes were further enlarged to about 120 nm, the peak intensity declined because of the reducing concentration of ions in really large-sized Au@Ag sol, and a shoulder peak became visible at 407 nm due to a different electron oscillation pattern from the dipole resonance of the primary peak [17].Figure 4
UV-vis spectra of colloidal Au seeds and Au@Ag NPs synthesized with 1 mmol/L AgNO3 solution and various amounts of Au seeds including (a) 0.45 mL, (b) 0.9 mL, (c) 1.5 mL, and (d) 4.5 mL.


## 3.2. Raman Spectra of Sudan I and Sudan II

The similarity of Sudan I and Sudan II in their molecular structures results in similar Raman spectral features as shown in Figure5. The spectra of two chemicals had two prominent peaks at around 1496 and 1227 cm−1 due to the stretching of double benzene ring and the C-H in-plane bending of phenyl groups [18, 19].Figure 5
IR and Raman spectra for Sudan I and Sudan II; representative SERS spectra of 1 mg/L Sudan II solution adsorbed on Au@Ag substrates synthesized with 1 mmol/L AgNO3 solution and various amounts of Au seeds including (a) 0.45 mL, (b) 0.9 mL, (c) 1.5 mL, and (d) 4.5 mL, as well as with 0.9 mL Au seeds and different concentrations of AgNO3 solutions including (e) 0.5 and (f) 2 mmol/L.Although Sudan I and Sudan II had similar Raman spectral features, each Sudan dye showed spectral singularities because of its unique molecular structure. The relative intensity of the peak at around 1599 cm−1 due to the stretching of N=N bond varied between two Sudan dyes, and the absorption intensity of Sudan II at around 1609 cm−1 was relatively weak compared to Sudan I [19, 20]. In addition, the peaks at around 1390 cm−1 in Sudan I and 1380 cm−1 in Sudan II are attributed to the C-N and C=C stretching in benzene rings [18]. Furthermore, the peaks arising from the C-H, O-H in-plane bending, and benzene rings distortions appear at 1171 cm−1 in Sudan I and 1154 cm−1 in Sudan II, respectively.


## 3.3. Screening SERS Substrates with High Enhancement Effect for Sudan Solutions

Au@Ag NPs with different particle sizes were used as substrates to acquire SERS spectra of Sudan II (1 mg/L), and their SERS enhancement factors (EF) were calculated based upon the following equation [21]:(1)
EF
=
I
SERS
I
n
o
r
m
N
n
o
r
m
N
SERS
,where I
SERS and I
n
o
r
m are the measured intensity of a specific characteristic peak for SERS and normal Raman spectra collected under the same test condition with or without the use of NPs as substrate, respectively; N
n
o
r
m and N
SERS are the corresponding number of Sudan II molecules. Based on the strongest characteristic peak at 1227 cm−1, the EFs for six Au@Ag NPs were estimated to be 2.4 × 104, 4.6 × 104, 3.2 × 104, 1.8 × 104, 2.0 × 104, and 2.6 × 104 corresponding to the particle size of 120
±
11, 73
±
6, 61
±
5, 50
±
4, 30
±
2, and 94
±
5 nm, respectively. The Au@Ag NPs of about 73 nm led to the highest enhancement effect. This is probably because Au@Ag NPs with relatively thinner Ag shell (such as the 61 nm Au@Ag NPs) has less intrinsic SERS activity of Ag NPs which normally can provide stronger electromagnetic enhancement than Au NPs, while Au@Ag NPs with too thick silver shell (such as the 120 nm NPs) are unable to provide proper or enough junctions for Sudan II molecules adsorbed onto the surfaces of Ag shells [22].


## 3.4. SERS Analysis of Sudan I and Sudan II with Optimal Au@Ag Substrates

The Au@Ag NPs with particles sizes of about 73 nm were selected as SERS substrate for analysis of a series standard solutions of Sudan I (0.4, 0.6, 0.8, and 1 mg/L) and Sudan II (0.1, 0.2, 0.5, and 1 mg/L) as well as for Sudan dyes in chili extracts. As shown in Figure6, the flat signal of blank substrates indicates that the background of substrates did not interfere with the SERS spectral features of Sudan dyes, and the intensity of the characteristic peaks decreased as the concentration of Sudan I and Sudan II decreased. The strong and medium-strong peaks at around 1229, 1390, 1496, and 1599 cm−1 were discernible at the concentration as low as 0.4 mg/L for Sudan I and 1227, 1380, and 1486 cm−1 at 0.1 mg/L for Sudan II standards.Figure 6
Representative SERS spectra of Sudan I and Sudan II standard solutions with Au@Ag NPs of about 73 nm as substrate.Figure7 presents SERS spectra of chili extracts spiked with Sudan I [0 (blank), 0.6, 0.8, 1, and 5 mg/kg] and Sudan II [0 (blank), 0.4, 0.5, 1, and 5 mg/kg], using Au@Ag NPs of about 73 nm as SERS substrates. No discernible SERS signals from nontargeted compounds could be found, and the major peaks in the SERS spectra of chili extracts spiked with Sudan I or Sudan II were consistent with those of their standard solutions. However, interference from chili matrices did exist since the SERS signals for chili extracts spiked with Sudan dyes were weaker than those for standard solutions with the same levels of Sudan dyes. The minimum concentration for Sudan I and Sudan II in chili extracts with major characteristic peaks discernible was 0.6 mg/kg and 0.4 mg/kg, respectively, higher than their standard counterparts.Figure 7
Representative SERS spectra of chili extracts spiked with Sudan I and Sudan II, using Au@Ag NPs of about 73 nm as substrate.Figure8 shows the plot of PCA (n
=
36) scores for the first two principal components that accounted for 76.9% of the spectral variation. The chili extracts spiked with Sudan I and Sudan II could be distinguished clearly, indicating the possibility of analyzing chili powder contaminated with different types and different levels of Sudan dyes.Figure 8
Plot of PCA score for SERS spectra of chili extracts spiked with Sudan I (0.6–1 mg/kg) and Sudan II (0.4–1 mg/kg), using Au@Ag NPs of about 73 nm as substrate.


## 4. Conclusions

A series of sizes of Au@Ag nanospheres (diameter: 30–120 nm) with good uniformity were successfully obtained without using surfactant that may hinder the effective adsorption of the analyte molecules onto the substrate surfaces. In addition, the study showed that the use of core-shell Au@Ag NPs with proper particle size (diameter:73
±
6 nm) and shell thickness (27
±
2 nm) as SERS substrate can greatly enhance the Raman intensities of Sudan dyes. The concentration of Sudan I and Sudan II standard solutions could be detected at levels as low as 0.4 mg/L and 0.1 mg/L, respectively. In spite of some interference from the matrices extracted from chili powder, Sudan I and Sudan II in chili powder could be detected at trace levels of 0.6 and 0.4 mg/kg, respectively. Finally, Sudan I and Sudan II with similar structures in complicated food matrices could be distinguished through applying PCA for analyzing SERS spectral data, indicating good selectivity of the SERS method with Au@Ag nanospheres as substrate for detection of banned additives in food stuffs at trace levels.



---