# Shape-Controlled Synthesis of Palladium-Copper Nanoalloys with Improved Catalytic Activity for Ethanol Electrooxidation

Authors: Hao Wang; Weihua Yang; Qinhao Zhang; Qingchao Qiu
Journal: International Journal of Electrochemistry
 (2016)

---

## Abstract

A facile solvothermal strategy is developed for the preparation of nanometer sized Pd-Cu alloy. We can control the morphology of these alloys with the use of ethylene glycol (EG) in the presence of KOH. Namely, by increasing the concentration of KOH/EG, the Pd-Cu alloys with different morphologies from near-spherical nanoparticles (NPs) to nanorods and nanowire networks have been prepared. Among all these alloys, near-spherical Pd-Cu NPs-modified electrodes exhibit the highest catalytic activity (11.7 mA/cm2) and stability toward the electrooxidation of ethanol in comparison with commercial Pd/C-modified ones (2.1 mA/cm2).


---

## Body

## 1. Introduction

In recent years, fuel cells based on energy conversion have gathered increasing attraction due to their favorable efficiency, high specific energy density, and low environmental damage [1, 2]. Among various types, direct ethanol fuel cells (DEFCs), especially operating in alkaline media, are more advantageous in practical application. Their energy supplier is the renewable resource of ethanol which is less toxic but possesses a higher theoretical energy density than methanol, and they have less complexity in cell construction [3]. However, the efficiency of DEFC is mostly determined by the catalyst deposited on the anode for ethanol oxidation reaction (EOR). Currently, noble metal nanomaterials (NMs) are widely used as catalysts in fuel cells [4–6]. Among them, Pt and Pd-based catalysts are of central significance for fuel cells [7], especially for DEFCs, owing to their preferable effectiveness for alcohol electrooxidation [8]. Compared with Pt, Pd seems to be more attractive as catalyst, due to its low cost, relatively high abundance, comparable electroactivity, and almost no CO-poisoning effects [7, 9–11].It has been reported that the shape, size and composition of NMs are the key factors to their catalytic activity [7, 12–15]. For instance, PdxCu1-x/C catalysts obtained in a hydrazine hydrate solution were found to be effective in EOR in alkaline medium and Pd0.9Cu0.1/C catalyst showed the best catalytic activity for ethanol oxidation [11]. The Pd-Cu NPs with various shapes from cubic to porous were prepared inl-ascorbic acid solution, equipping the enhanced catalytic activity for methanol oxidation [16]. Zhang and coworkers successfully fabricated the Pd-Cu tripod alloys with different compositions and controllable sizes inl-ascorbic acid system, which exhibited the superior catalytic properties for formic acid oxidation [17]. While successful, most of these Pd-Cu alloys were synthesized in an aqueous solution with the use of additional reductant; the synthesis of them in an anhydrous synthetic system through a wet chemistry technique still remains a great challenge.In this study, we present a facile solvothermal strategy to synthesize shape-controlled bimetallic Pd-Cu alloys. Here, the EG is used as both solvent and reducing agent. To the best of our knowledge, there has been no prior work regarding the morphology-controlled synthesis of Pd-Cu alloys through tuning the concentration of KOH/EG. In order to find out the optimal alloy, the catalytic activity of Pd-Cu alloys was investigated for EOR, using commercial Pd/C catalyst as references.


## 2. Experimental

### 2.1. Materials Synthesis

To synthesize Pd-Cu alloys, 0.5 mL of 48 mM Na2PdCl4/EG and 0.1 mL of 240 mM Cu(CH3COO)2·H2O/EG were mixed together with EG (final volume 10.0 mL), which contained 111 mg polyvinylpyrrolidone (PVP, MW = 30000), 83 mg KI, and a variable concentration (1, 10, or 100 mM) of KOH/EG. The mixed solution was stirred for 30 min at room temperature to obtain a homogeneous suspension. Then the mixture was transferred into a 20 mL Teflon-lined stainless steel autoclave and maintained at 200°C for 6 h in oven. The entire synthesis procedure above should be under anhydrous system. After the autoclave was cooled to room temperature naturally, the final black product was collected by centrifugation, thoroughly washed with ethanol and deionized water to remove the residual PVP and EG, and preserved in ethanol for further characterization.


### 2.2. Materials Characterization

A Hitachi H7650 transmission electron microscopy (TEM) was used to observe the nanoparticle shape and distribution. The nanoparticle structures and phase purity were conducted by powder X-ray diffraction (XRD) spectroscopy using a Japan Rigaku D/max-2500 diffractometer equipped with Cu Kα radiation (λ = 1.54056 Å). The ratio of Pd and Cu in the as-prepared Pd-Cu alloys was performed by X-ray energy dispersive spectroscopy (EDS). TEM analysis was operating at 200 kV, and then drops of the suspension were deposited on a copper mesh covered with carbon film for TEM observation.


### 2.3. Electrochemical Measurements

The electrochemical experiments in this study were performed with a conventional three-electrode electrochemical cell on a CHI 660E electrochemical workstation (CH Instruments, Chenhua Company, Shanghai, China). A platinum foil, a saturated calomel electrode (SCE), and a glassy carbon electrode (GCE, 3 mm in diameter) were used as the counter electrode, the reference electrode, and the working electrode, respectively. Aliquots (14μL) of the as-synthesized Pd-Cu alloys solutions were dropped homogeneously on the clean GCE followed by casting Nafion solution (0.05 wt.%, 5 μL) on the electrode surfaces to seal the samples in place and air-dried for 30 min at ambient temperature. Cyclic voltammetry (CV) measurements were collected to examine the electrochemical active surface area (ECSA) and the electrocatalytic activity of Pd-Cu alloy catalysts for EOR. Chronoamperograms (CA) measurements were then employed to study the stability of these catalysts.


## 2.1. Materials Synthesis

To synthesize Pd-Cu alloys, 0.5 mL of 48 mM Na2PdCl4/EG and 0.1 mL of 240 mM Cu(CH3COO)2·H2O/EG were mixed together with EG (final volume 10.0 mL), which contained 111 mg polyvinylpyrrolidone (PVP, MW = 30000), 83 mg KI, and a variable concentration (1, 10, or 100 mM) of KOH/EG. The mixed solution was stirred for 30 min at room temperature to obtain a homogeneous suspension. Then the mixture was transferred into a 20 mL Teflon-lined stainless steel autoclave and maintained at 200°C for 6 h in oven. The entire synthesis procedure above should be under anhydrous system. After the autoclave was cooled to room temperature naturally, the final black product was collected by centrifugation, thoroughly washed with ethanol and deionized water to remove the residual PVP and EG, and preserved in ethanol for further characterization.


## 2.2. Materials Characterization

A Hitachi H7650 transmission electron microscopy (TEM) was used to observe the nanoparticle shape and distribution. The nanoparticle structures and phase purity were conducted by powder X-ray diffraction (XRD) spectroscopy using a Japan Rigaku D/max-2500 diffractometer equipped with Cu Kα radiation (λ = 1.54056 Å). The ratio of Pd and Cu in the as-prepared Pd-Cu alloys was performed by X-ray energy dispersive spectroscopy (EDS). TEM analysis was operating at 200 kV, and then drops of the suspension were deposited on a copper mesh covered with carbon film for TEM observation.


## 2.3. Electrochemical Measurements

The electrochemical experiments in this study were performed with a conventional three-electrode electrochemical cell on a CHI 660E electrochemical workstation (CH Instruments, Chenhua Company, Shanghai, China). A platinum foil, a saturated calomel electrode (SCE), and a glassy carbon electrode (GCE, 3 mm in diameter) were used as the counter electrode, the reference electrode, and the working electrode, respectively. Aliquots (14μL) of the as-synthesized Pd-Cu alloys solutions were dropped homogeneously on the clean GCE followed by casting Nafion solution (0.05 wt.%, 5 μL) on the electrode surfaces to seal the samples in place and air-dried for 30 min at ambient temperature. Cyclic voltammetry (CV) measurements were collected to examine the electrochemical active surface area (ECSA) and the electrocatalytic activity of Pd-Cu alloy catalysts for EOR. Chronoamperograms (CA) measurements were then employed to study the stability of these catalysts.


## 3. Results and Discussion

### 3.1. Characterization of Pd-Cu Alloy Catalysts

Figure1 displays our process and XRD patterns of resulting Pd-Cu alloys. When the concentration of KOH/EG was relatively low (~1 mM), that is, the theoretical pH value of the reaction system was 11, the near-spherical Pd-Cu NPs were obtained (Figure 1(a)). From the XRD patterns (Figure 1(b)), it can be seen that our products are very close to those of pure Pd (JCPDS: 87-0643). We found that the shape of as-prepared products changed from near-spherical to nanorods after increasing the concentration of KOH/EG to 10 mM. The diffraction peaks of the nanorods shift to a higher angle, which are located between those of pure Pd and Cu (JCPDS: 65-9743), confirming the formation of Pd-Cu alloys. When the concentration of KOH/EG was increased to 100 mM, namely, the theoretical pH value of the reaction solution went up to 13, the morphology of as-synthesized alloys changed to nanowire networks, and their characteristic peaks on XRD are shifted toward that of pure Cu. Moreover, the diffraction peaks in the XRD patterns of these Pd-Cu alloys are all shifted toward higher angles with increase of the concentration of KOH/EG, which means that the proportion of Cu increased as more KOH/EG was added to the synthetic system. Or in other words, the KOH/EG with a high concentration has promoted the reduction of Cu2+. In addition, the EDS measurement shows that the corresponding molar ratio of Cu to Pd in the Pd-Cu near-spherical, nanorods, and nanowire networks alloys is approximately 0.27, 0.93, and 1.97, respectively, which exactly agrees with the XRD data.Figure 1
(a) Schematic illustration of the synthetic pathways leading to the formation of Pd-Cu alloys with three different structures and (b) XRD patterns for the corresponding alloys.
(a)
(b)The as-prepared electrocatalysts were characterized using TEM analysis. Figures2(a) and 2(b) show the as-prepared Pd-Cu near-spherical NPs and their average size. We found that the particles are not entirely spherical; instead they had edged features and a relatively small size fluctuation (d = 56.7 ± 5.7 nm) (Figure 2(c)). The XRD pattern of near-spherical NPs (Figure 1(b)) displays that the diffraction peaks appear between the peaks for pure Pd and Cu, and no characteristic peaks of Cu or its oxides are detected, suggesting the formation of Pd-Cu alloys [18]. Furthermore, the amount of Pd is about 3.7 times higher than that of Cu, as strongly determined by EDS data (Figure 2(d)). This may be due to much easier reduction of Pd2+ to Pd (0.92 Vversus RHE) compared to that of Cu2+/Cu (0.34 Vversus RHE); in particular the concentration of KOH/EG is still relatively low.Figure 2
(a, b) Typical TEM images of Pd-Cu near-spherical NPs with different magnifications. (c) Particle size distribution analysis. (d) EDS spectrum of the corresponding NPs.
(a)
(b)
(c)
(d)With an increase of the concentration of KOH/EG, we observed that the shape of as-prepared alloys changed from near-spherical to nanorods structures. Figures3(a) and 3(b) show the typical TEM images of Pd-Cu nanorods. According to the TEM images, it can be seen that the synthetic products consist of most Pd-Cu nanorods (diameter, ~18 nm) with an aspect ratio of ~6 and few irregular Pd-Cu NPs about 10–30 nm in diameter. The EDS spectrum (the inset in Figure 3(a)) shows the existence of both Pd and Cu in each of the nanorods, which can further be proven by the XRD results (Figure 1(b)).Figure 3
(a, b) Typical TEM images of Pd-Cu nanorods with different magnifications. The inset in (a) is the corresponding EDS spectrum.
(a)
(b)In order to explore the effect of KOH/EG on the morphology, we further increased the concentration of KOH/EG while keeping all other synthetic conditions unchanged. Figures4(a) and 4(b) show the typical TEM images of the as-prepared Pd-Cu nanowire networks with different magnifications, revealing that the products consist of uniform nanowire networks with high yield. From the pattern of particle size distribution (Figure 4(c)), we found that the average diameter of the Pd-Cu alloys is about 8.34 ± 0.6 nm, and their length is observed to be several tens of nanometers. From the EDS spectrum (Figure 4(d)) and XRD results (Figure 1(b)), we can conclude that the nanowire network consisted of a Pd-Cu alloy. In addition, the atomic ratio of Pd/Cu is determined to be approximately 1 : 2 from the EDS data (Figure 4(d)). This may be due to the preferential reduction of Cu species in comparison with Pd species when the concentration of KOH/EG is relatively high.Figure 4
(a, b) Typical TEM images of Pd-Cu nanowire networks with different magnifications. (c) Particle size distribution analysis. (d) EDS spectrum of the corresponding alloys.
(a)
(b)
(c)
(d)According to the above results, the morphology of the prepared Pd-Cu alloys can be remarkably changed by varying the concentration of KOH/EG [18]. To explore the limit of KOH/EG, we have further carried out a series of control experiments. Figures 5(a) and 5(b) show that Pd-Cu near-spherical NPs were still obtained under the same conditions but with the lower concentration (0.1 mM) of KOH/EG. Furthermore, as illustrated in Figures 5(c) and 5(d), the products consist of nanowire networks as usual when the concentration of KOH/EG was further increased to 1 M. It can be thus deduced that KOH/EG mainly plays a crucial role of shape controllers in the synthesis of these Pd-Cu alloys [18]. However, further studies are still required to fully understand how KOH/EG with different concentration determines the shape evolution of these Pd-Cu alloys.Figure 5
Typical TEM images of Pd-Cu alloys with different magnifications collected under the same conditions, except the variation in the concentration of KOH/EG: (a, b) 0.1 mM and (c, d) 1 M.
(a)
(b)
(c)
(d)


### 3.2. Electrochemical Behavior of Pd-Cu Alloy Catalysts

Figure6 plots the CV curves of commercial Pd/C and Pd-Cu alloy catalysts in 0.5 M KOH at a scan rate of 50 mV/s. All the specific current density (j) was normalized to the ECSA, which was estimated from the charges associated with the reduction peak of PdO using CV data, assuming 405 μC/cm2 for the reduction of a PdO monolayer [19]. Figure 7(a) shows the electrocatalytic activity of these catalysts toward ethanol oxidation, which was investigated in 0.5 M KOH containing 1.0 M ethanol. It is clear that Pd-Cu near-spherical NPs display the highest specific activity among these catalysts. The peak current density of ethanol electrooxidation in the positive potential scan of Pd-Cu near-spherical NPs is approximately 11.7 mA/cm2, which is nearly 5.5 times higher than that (2.1 mA/cm2) of the commercial Pd/C. It is well known that the noble metal catalyst such as Pd usually shows superior activity at edges and corners [13, 18]. In this case, the synthesis of Pd-based nanoparticles with edges/frame structure is extremely desired. Meanwhile, here in our experiments, the highest activity for Pd-Cu near-spherical NPs with edges truncation is in good agreement with this [18].Figure 6
CV curves of modified electrodes for commercial Pd/C, near-spherical Pd-Cu NPs, nanorods Pd-Cu alloys, and nanowire networks Pd-Cu alloys in 0.5 M KOH at a scan rate of 50 mV s−1.Figure 7
(a) CV curves and (b) CA curves (at −0.25 Vversus SCE) of modified electrodes for commercial Pd/C, near-spherical Pd-Cu NPs, nanorods Pd-Cu alloys, and nanowire networks Pd-Cu alloys in 0.5 M KOH containing 1.0 M ethanol at a scan rate of 50 mV s−1.
(a)
(b)To further evaluate the stability on ethanol electrooxidation of Pd-Cu alloy catalysts and commercial Pd/C catalyst, we recorded CA curves for 600 s at −0.25 V (versus SCE) in the solution of 0.5 M KOH containing 1.0 M ethanol (shown in Figure 7(b)). CA curves indicate that the Pd-Cu near-spherical NPs possess the higher stability for the entire time course, which further verifies that Pd-Cu near-spherical NPs exhibit better electrocatalytic performance in the EOR.


## 3.1. Characterization of Pd-Cu Alloy Catalysts

Figure1 displays our process and XRD patterns of resulting Pd-Cu alloys. When the concentration of KOH/EG was relatively low (~1 mM), that is, the theoretical pH value of the reaction system was 11, the near-spherical Pd-Cu NPs were obtained (Figure 1(a)). From the XRD patterns (Figure 1(b)), it can be seen that our products are very close to those of pure Pd (JCPDS: 87-0643). We found that the shape of as-prepared products changed from near-spherical to nanorods after increasing the concentration of KOH/EG to 10 mM. The diffraction peaks of the nanorods shift to a higher angle, which are located between those of pure Pd and Cu (JCPDS: 65-9743), confirming the formation of Pd-Cu alloys. When the concentration of KOH/EG was increased to 100 mM, namely, the theoretical pH value of the reaction solution went up to 13, the morphology of as-synthesized alloys changed to nanowire networks, and their characteristic peaks on XRD are shifted toward that of pure Cu. Moreover, the diffraction peaks in the XRD patterns of these Pd-Cu alloys are all shifted toward higher angles with increase of the concentration of KOH/EG, which means that the proportion of Cu increased as more KOH/EG was added to the synthetic system. Or in other words, the KOH/EG with a high concentration has promoted the reduction of Cu2+. In addition, the EDS measurement shows that the corresponding molar ratio of Cu to Pd in the Pd-Cu near-spherical, nanorods, and nanowire networks alloys is approximately 0.27, 0.93, and 1.97, respectively, which exactly agrees with the XRD data.Figure 1
(a) Schematic illustration of the synthetic pathways leading to the formation of Pd-Cu alloys with three different structures and (b) XRD patterns for the corresponding alloys.
(a)
(b)The as-prepared electrocatalysts were characterized using TEM analysis. Figures2(a) and 2(b) show the as-prepared Pd-Cu near-spherical NPs and their average size. We found that the particles are not entirely spherical; instead they had edged features and a relatively small size fluctuation (d = 56.7 ± 5.7 nm) (Figure 2(c)). The XRD pattern of near-spherical NPs (Figure 1(b)) displays that the diffraction peaks appear between the peaks for pure Pd and Cu, and no characteristic peaks of Cu or its oxides are detected, suggesting the formation of Pd-Cu alloys [18]. Furthermore, the amount of Pd is about 3.7 times higher than that of Cu, as strongly determined by EDS data (Figure 2(d)). This may be due to much easier reduction of Pd2+ to Pd (0.92 Vversus RHE) compared to that of Cu2+/Cu (0.34 Vversus RHE); in particular the concentration of KOH/EG is still relatively low.Figure 2
(a, b) Typical TEM images of Pd-Cu near-spherical NPs with different magnifications. (c) Particle size distribution analysis. (d) EDS spectrum of the corresponding NPs.
(a)
(b)
(c)
(d)With an increase of the concentration of KOH/EG, we observed that the shape of as-prepared alloys changed from near-spherical to nanorods structures. Figures3(a) and 3(b) show the typical TEM images of Pd-Cu nanorods. According to the TEM images, it can be seen that the synthetic products consist of most Pd-Cu nanorods (diameter, ~18 nm) with an aspect ratio of ~6 and few irregular Pd-Cu NPs about 10–30 nm in diameter. The EDS spectrum (the inset in Figure 3(a)) shows the existence of both Pd and Cu in each of the nanorods, which can further be proven by the XRD results (Figure 1(b)).Figure 3
(a, b) Typical TEM images of Pd-Cu nanorods with different magnifications. The inset in (a) is the corresponding EDS spectrum.
(a)
(b)In order to explore the effect of KOH/EG on the morphology, we further increased the concentration of KOH/EG while keeping all other synthetic conditions unchanged. Figures4(a) and 4(b) show the typical TEM images of the as-prepared Pd-Cu nanowire networks with different magnifications, revealing that the products consist of uniform nanowire networks with high yield. From the pattern of particle size distribution (Figure 4(c)), we found that the average diameter of the Pd-Cu alloys is about 8.34 ± 0.6 nm, and their length is observed to be several tens of nanometers. From the EDS spectrum (Figure 4(d)) and XRD results (Figure 1(b)), we can conclude that the nanowire network consisted of a Pd-Cu alloy. In addition, the atomic ratio of Pd/Cu is determined to be approximately 1 : 2 from the EDS data (Figure 4(d)). This may be due to the preferential reduction of Cu species in comparison with Pd species when the concentration of KOH/EG is relatively high.Figure 4
(a, b) Typical TEM images of Pd-Cu nanowire networks with different magnifications. (c) Particle size distribution analysis. (d) EDS spectrum of the corresponding alloys.
(a)
(b)
(c)
(d)According to the above results, the morphology of the prepared Pd-Cu alloys can be remarkably changed by varying the concentration of KOH/EG [18]. To explore the limit of KOH/EG, we have further carried out a series of control experiments. Figures 5(a) and 5(b) show that Pd-Cu near-spherical NPs were still obtained under the same conditions but with the lower concentration (0.1 mM) of KOH/EG. Furthermore, as illustrated in Figures 5(c) and 5(d), the products consist of nanowire networks as usual when the concentration of KOH/EG was further increased to 1 M. It can be thus deduced that KOH/EG mainly plays a crucial role of shape controllers in the synthesis of these Pd-Cu alloys [18]. However, further studies are still required to fully understand how KOH/EG with different concentration determines the shape evolution of these Pd-Cu alloys.Figure 5
Typical TEM images of Pd-Cu alloys with different magnifications collected under the same conditions, except the variation in the concentration of KOH/EG: (a, b) 0.1 mM and (c, d) 1 M.
(a)
(b)
(c)
(d)


## 3.2. Electrochemical Behavior of Pd-Cu Alloy Catalysts

Figure6 plots the CV curves of commercial Pd/C and Pd-Cu alloy catalysts in 0.5 M KOH at a scan rate of 50 mV/s. All the specific current density (j) was normalized to the ECSA, which was estimated from the charges associated with the reduction peak of PdO using CV data, assuming 405 μC/cm2 for the reduction of a PdO monolayer [19]. Figure 7(a) shows the electrocatalytic activity of these catalysts toward ethanol oxidation, which was investigated in 0.5 M KOH containing 1.0 M ethanol. It is clear that Pd-Cu near-spherical NPs display the highest specific activity among these catalysts. The peak current density of ethanol electrooxidation in the positive potential scan of Pd-Cu near-spherical NPs is approximately 11.7 mA/cm2, which is nearly 5.5 times higher than that (2.1 mA/cm2) of the commercial Pd/C. It is well known that the noble metal catalyst such as Pd usually shows superior activity at edges and corners [13, 18]. In this case, the synthesis of Pd-based nanoparticles with edges/frame structure is extremely desired. Meanwhile, here in our experiments, the highest activity for Pd-Cu near-spherical NPs with edges truncation is in good agreement with this [18].Figure 6
CV curves of modified electrodes for commercial Pd/C, near-spherical Pd-Cu NPs, nanorods Pd-Cu alloys, and nanowire networks Pd-Cu alloys in 0.5 M KOH at a scan rate of 50 mV s−1.Figure 7
(a) CV curves and (b) CA curves (at −0.25 Vversus SCE) of modified electrodes for commercial Pd/C, near-spherical Pd-Cu NPs, nanorods Pd-Cu alloys, and nanowire networks Pd-Cu alloys in 0.5 M KOH containing 1.0 M ethanol at a scan rate of 50 mV s−1.
(a)
(b)To further evaluate the stability on ethanol electrooxidation of Pd-Cu alloy catalysts and commercial Pd/C catalyst, we recorded CA curves for 600 s at −0.25 V (versus SCE) in the solution of 0.5 M KOH containing 1.0 M ethanol (shown in Figure 7(b)). CA curves indicate that the Pd-Cu near-spherical NPs possess the higher stability for the entire time course, which further verifies that Pd-Cu near-spherical NPs exhibit better electrocatalytic performance in the EOR.


## 4. Conclusions

In this study, a simplified one-pot synthetic strategy has been developed to prepare Pd-Cu alloys with various morphologies from near-spherical to nanorods and nanowire networks structures. The use of KOH/EG with different concentration was demonstrated to play a critical role in the shape evolution of Pd-Cu alloys. Among these alloys, the near-spherical Pd-Cu catalyst shows the highest specific activity and stability toward the electrooxidation of ethanol in comparison with commercial Pd/C catalyst, mainly due to the advantages of more edge truncation, a greater number of active sites, and bimetallic synergistic effects. Having the excellent electrocatalytic activity, optimal stability, and cost effectiveness, the near-spherical Pd-Cu NPs exhibit great potential as an efficient anode catalyst for DEFCs.



---

*Source: 4261012-2016-02-04.xml*