# A Clean, Simple, and Efficient Synthesis of 2-Substituted Aryl (Indolyl) Kojic Acid Derivatives by Kaolin/Ag Nanocomposite as a Reusable Catalyst: A Green Protocol

Authors: Bahareh Sadeghi; Mohammad Reza Shahedi
Journal: Journal of Chemistry
 (2013)

---

## Abstract

Kaolin/Ag nanocomposite (kaolin/Ag nanocomposite) was synthesized in a nanoreactor by the calcination of the precursor at high temperature and was shown to efficiently catalyze the one-pot, three-component reaction of an aromatic aldehyde, kojic acid, and indole derivatives under solvent-free conditions to afford the corresponding 2-substituted aryl (indolyl) kojic acid derivatives in high yield.


---

## Body

## 1. Introduction

Nanocomposite is a new class of composites in which the dimensions of the material are in the order of nanometers. Because of this nanometer size characteristic, nanocomposites possess superior properties than the conventional composites such as thermal stability, high surface areas, and mechanical and catalytic properties [1–3]. Up to now, various nanocomposites were synthesized on the basis of Ag nanoparticles with antibacterial and catalytic activities, including silver-hydroxyapatite, dendrimer-silver complexes, hollow Pt/Ag, and silver-silica nanocomposite [4–7]. In this paper, we used the adsorption layer on the surface of kaolin as reactor to prepare Kaolin/Ag nanocomposite material which had a small average grain size and was well distributed. The prepared composite was characterized using Fourier transform infrared (FT-IR), X-ray diffraction (XRD), and scanning electron microscope (SEM) instruments.The 3-substituted indole moieties are included in numerous natural products and they are dominant molecules in medicinal chemistry [8, 9]. On the other hand, kojic acid is also known as an attractive molecule in pharmaceutical chemistry due to its accessibility, potential biological activity, and high reactivity [10, 11]. Due to the vast medicinal utility of kojic acid and 3-substituted indole derivatives, the introduction of a mild, efficient, and selective method to synthesize these compounds is still needed. In continuation of our investigations of the application of solid acids in organic synthesis [12–16], we have investigated the synthesis of Kaolin/Ag nanocomposite as a catalyst and applied for the synthesis of 2-substituted aryl (indolyl) kojic acid derivatives.


## 2. Experimental

### 2.1. General

Melting points were determined with an Electro thermal 9100 apparatus. IR spectra were recorded on a Shimadzu IR-470 spectrometer.1H and 13C NMR spectra were recorded on Bruker DRX-400 Avance Spectrometer for solutions in CDCl3 using TMS as an internal standard. Mass spectra were recorded on a FINNIGAN-MAT 8430 mass spectrometer operating at an ionization potential of 70 eV. Elemental analyses were performed using a Costech ECS 4010 CHNS-O analyzer at the analytical laboratory of Science and Research Unit of Islamic Azad University, Iran. The morphologies of the products were observed using SEM of VEGA/TESCAN microscope with an accelerating voltage of 15 kV. X-ray diffraction (XRD) patterns were taken on a Rigaku D=max-2500 instrument with Cu Ka radiation (40 kV, 100 mA) to analyze crystalline structure. The chemicals for this work were purchased from Fluka (Buchs, Switzerland) and were used without further purification.


### 2.2. General Procedure for the Preparation of Kaolin/Ag Nanocomposite Material

1.5 g Kaolin was dried at 90°C for 2 h and cooled at room temperature. Then, 600 mL of absolute ethyl alcohol was added and well mixed. After 2 h, water (3 mL) and NaOH (0.162 g) were added into the reaction system under stirring and room temperature conditions. After the adsorption equilibrium was attained (24 h), silver nitrate in water (100 mL and 2.28 g) was added at a constant rate, react with NaOH, and reduced by ethanol. After reacting for a definite time, the product was gained by centrifugation and dried at room temperature.


### 2.3. General Procedure for the Preparation of Compounds4a–m

A mixture of aryl aldehyde (1 mmol), kojic acid (1 mmol), and Kaolin/Ag NPs (0.001 g) was stirred at 90°C. After 5–15 min, indole (1 mmol) was added and the reaction was continued for appropriate time. After the completion of the reaction (as monitored by TLC), water was added with reaction mixture (15 mL) and extracted with ethyl acetate (3 × 10 mL). The organic layer was dried over sodium sulfate and concentrated under vacuum. The crude product was chromatographed in silica gel (70 : 30n-hexane/ethyl acetate) and appropriate isolated yield.


## 2.1. General

Melting points were determined with an Electro thermal 9100 apparatus. IR spectra were recorded on a Shimadzu IR-470 spectrometer.1H and 13C NMR spectra were recorded on Bruker DRX-400 Avance Spectrometer for solutions in CDCl3 using TMS as an internal standard. Mass spectra were recorded on a FINNIGAN-MAT 8430 mass spectrometer operating at an ionization potential of 70 eV. Elemental analyses were performed using a Costech ECS 4010 CHNS-O analyzer at the analytical laboratory of Science and Research Unit of Islamic Azad University, Iran. The morphologies of the products were observed using SEM of VEGA/TESCAN microscope with an accelerating voltage of 15 kV. X-ray diffraction (XRD) patterns were taken on a Rigaku D=max-2500 instrument with Cu Ka radiation (40 kV, 100 mA) to analyze crystalline structure. The chemicals for this work were purchased from Fluka (Buchs, Switzerland) and were used without further purification.


## 2.2. General Procedure for the Preparation of Kaolin/Ag Nanocomposite Material

1.5 g Kaolin was dried at 90°C for 2 h and cooled at room temperature. Then, 600 mL of absolute ethyl alcohol was added and well mixed. After 2 h, water (3 mL) and NaOH (0.162 g) were added into the reaction system under stirring and room temperature conditions. After the adsorption equilibrium was attained (24 h), silver nitrate in water (100 mL and 2.28 g) was added at a constant rate, react with NaOH, and reduced by ethanol. After reacting for a definite time, the product was gained by centrifugation and dried at room temperature.


## 2.3. General Procedure for the Preparation of Compounds4a–m

A mixture of aryl aldehyde (1 mmol), kojic acid (1 mmol), and Kaolin/Ag NPs (0.001 g) was stirred at 90°C. After 5–15 min, indole (1 mmol) was added and the reaction was continued for appropriate time. After the completion of the reaction (as monitored by TLC), water was added with reaction mixture (15 mL) and extracted with ethyl acetate (3 × 10 mL). The organic layer was dried over sodium sulfate and concentrated under vacuum. The crude product was chromatographed in silica gel (70 : 30n-hexane/ethyl acetate) and appropriate isolated yield.


## 3. Results and Discussion

Herein, we attempted to synthesize Kaolin/Ag nanocomposite in a nanoreactor, which was shown to efficiently catalyse the synthesis of 2-substituted aryl (indolyl) kojic acid derivatives, by the three-component condensation of an aromatic aldehyde1, kojic acid 2, and indole derivatives 3 (Scheme 1).Scheme 1
Synthesis of 2-substituted aryl (indolyl) kojic acid derivatives in the presence of Kaolin/Ag nanocomposite as catalyst.The stable catalyst is easily prepared and used for preparation of 2-substituted aryl (indolyl) kojic acid derivatives. The Kaolin/Ag nanocomposite is made using nanotechnique and the mechanism of adsorption. Silver ion is reduced by methanol in an alkaline solution while the temperature was fixed to 25°C during the reaction. These are the differences and advantages of this method compared with previous article [17].In the experiment, we first studied IR spectra of Kaolin and Kaolin/Ag nanocomposite (Figure1). In both of them, OH stretching bond is observed at ~3621 cm−1. Comparison of the infrared spectra of Kaolin and Kaolin/Ag show that, in both of them, the asymmetric stretching vibrations for Al2O3 and SiO2 appeared at ~914 cm−1 and ~1114 cm−1, respectively. Also, the symmetric stretching vibrations for Al2O3 and SiO2 appeared at ~694 cm−1 and ~789 cm−1, respectively. In Kaolin/Ag spectrum, the absorption of nitrate is observed at 1369 and 1444 cm−1. It is detected that Ag nanoparticles are distributed over the surface of Kaolin in the form of massive agglomeration.Figure 1
FT-IR spectrum of (a) Kaolin and (b) Kaolin/Ag nanocomposite.The results of XRD are shown in Figure2. In both XRD patterns, peaks that appeared at 2θ=10 and 25° are quartz crystals. The pattern of Kaolin (a) shows that at 2θ=30–40° no characteristic peaks come out, but pattern of Kaolin/Ag nanocomposite (b) shows that at 2θ=30–40° intensities of peaks increase, which demonstrates that Kaolin/Ag nanocomposite is produced.Figure 2
XRD patterns of (a) Kaolin and (b) Kaolin/Ag nanocomposite.As reported in the article for silver nanoparticle/kaolinite composites [17], silver is placed in the space between the layers of kaolinite and that explains why the XRD of kaolinite and silver nanoparticle/kaolinite composites are identical.The dimensions of nanoparticles were observed with SEM. The size of commercial Kaolin/Ag nanocomposite is about 36–53 nm, and SEM images of Kaolin/Ag nanocomposite showed that the Ag nanoparticles were homogeneously dispersed in Kaolin matrices (Figure3).SEM images of Kaolin/Ag nanocomposite.
(a)
(b)It is clearly seen on the TEM images of Kaolin that the crystals’ size is 170–400 nm, but TEM images of Kaolin/Ag nanocomposite show crystals’ size decrease of 50 nm, and it is detected that Ag nanoparticles are distributed over the surface of Kaolin in the form of massive agglomeration (Figures4 and 5).TEM images of (a) Kaolin 400 nm and (b) Kaolin 170 nm.
(a)
(b)Figure 5
TEM image of Kaolin/Ag NPs 50 nm.BET results are given in Table1. This information includes the measurement of surface area, total pore volume, and the average pore diameter of Kaolin/Ag nanocomposite and Kaolin. According to the obtained data, weight, surface area, and the average pore diameter of Kaolin/Ag nanocomposite were increased than those of Kaolin and the total pore volume was decreased.Table 1
Study of BET tests of Kaolin and Kaolin/Ag nanocomposite.
Entry
Type of measurement
Kaolin
Silver/kaolin
1
Sample weight (g)
0.1527
0.2412
2
Temperature (k)
77
77
3
Saturated vapor pressure (KPa)
89.013
89.009
4
Mean pore diameter (nm)
41.65
54.70
5
Total pore volume (cm3·g−1)
0.1064
0.1013
6
As, BET (m2·g−1)
1.02
7.41To optimize the reaction conditions, the reaction of benzaldehyde, kojic acid, and indole was used as a model reaction. In order to establish the better catalytic activity of Kaolin/Ag nanocomposite, we have compared the reaction using other catalysts at solvent-free conditions and for 75 min. The results are listed in Table2. The problems in the reported protocols such as prolonged reaction time and poor yields prompted us to develop a new rapid method affording excellent yield for the synthesis of 2-substituted aryl (indolyl) kojic acid derivatives.Table 2
Evaluation of the activity of different catalysts for the synthesis of4a.
Entry
Catalyst
Yield
a/%
1
KAl(SO4)2·12H2O
60
2
Kaolin
83
3
Silver NPs
92
4
Kaolin/Ag nanocomposite
98
aReaction conditions: 60 min at 90°C in solvent-free conditions.In order to determine the optimum quantity of Kaolin/Ag nanocomposite, the reaction of benzaldehyde, kojic acid, and indole was carried out at solvent-free conditions using different quantities of Kaolin/Ag nanocomposite (Table3). Kaolin/Ag nanocomposite of 0.001 g gave an excellent yield in 75 min (Table 3, entry 4).Table 3
Optimization amount of Kaolin/Ag nanocomposite catalyst for the synthesis of4a.
Entry
Catalyst
Yield
a (%)
1
—
—
2
0.0005
57
3
0.0008
83
4
0.001
98
aReaction conditions: 60 min at 90°C in solvent-free conditions.The above reaction was also examined in various solvents (Table4). The results indicated that different solvents affected the efficiency of the reaction. Most of these solvents required a longer time and gave moderate yields, and the best results were obtained when solvent-free was used (Table 4, entry 6).Table 4
Effect of the solvent on the synthesis of4a by Kaolin/Ag nanocomposite catalyst.
Entry
Solvent
Yield
a (%)
1
EtOH
60
2
THF
20
3
H2O
45
4
n-Hexane
10
5
Toluene
50
6
Solvent-freeb
98
a60 min at reflux temperature in 10 mL solvent.
b60 min at 90°C.To study the scope of the reaction, a series of aromatic aldehydes, indoles, and kojic acid catalysed by Kaolin/Ag nanocomposite as catalyst were examined. The results are shown in Table5. In all cases, aromatic aldehyde substituted with either electron-donating or electron-withdrawing groups underwent the reaction smoothly and gave products in good yields.Table 5
Condensation of aromatic aldehyde, kojic acid, and indole derivatives in the presence of Kaolin/Ag nanocomposite catalyst.
Entry
Aldehyde
Indole
Product
a
Time(min)
Yield(%)b
M.p. (°C) [Ref.]
1
4a
60
98
79–81 [18]
2
4b
65
83
96–98 [18]
3
4c
55
87
89-90 [18]
4
4d
60
92
86–88 [18]
5
4e
75
82
96–98 [18]
6
4f
70
90
96–98 [18]
7
4g
60
92
87–89
8
4h
65
90
Oil
9
4i
75
82
87–89
10
4j
90
85
169–171
11
4k
80
80
172–174
12
4l
87
82
167–169
13
4m
90
85
170–172
aAll the products were identified by 1H NMR and 13C NMR spectra and also by comparing of melting point and 1H NMR spectra with those of authentic samples reported in the literature.
bYields refer to isolated products.The compounds4a–f were characterized by their 1H-NMR and IR spectroscopy and elemental analyses. Spectral data were compared with the literature data [18].Compounds4g–m was new and their structures were deduced by elemental and spectral analyses. The mass spectrum of compound 4h showed the molecular ion peak at 361. The 1H NMR spectrum of 4h exhibits three sharp lines at δ=5.65, 6.29, and 6.63 ppm for the proton of methine and olefinic protons, respectively. The 1H-NMR spectrum of compound 4h exhibited protons of methylene at 4.21 ppm and protons of methyl group at δ=2.32. Three single signals are observed at 10.19, 7.43, and 5.92 ppm that disappeared after the addition of a few drops of D2O to CDCl3 solution of compound 4h. These signals are related to OH and NH protons. Multiplets are observed between 6.70 and 7.35 ppm which are related to aromatic protons. The 13C-NMR spectrum of compound 4h showed 20 signals in agreement with the proposed structure. The IR spectrum of compound 4h also supported the suggested structure.An interesting feature of this method is that the reagent can be regenerated at the end of the reaction and can be used several times without losing its activity. To recover the catalyst, after completion of the reaction, the mixture was filtered, catalyst (Kaolin/Ag nanocomposite) was washed with CHCl3, and then the solid residue was dried. This process repeated for three cycles, and the yield of product 4a did not change significantly (Table 6).Table 6
Recycling studies of reaction between benzaldehyde, kojic acid, and indole in the presence of Kaolin/Ag nanocomposite to give product4a.
Entry
Cycle
Time (min)
Yield %a
1
Fresh
60
98
2
1
60
92
3
2
60
89
4
3
60
85
aYields refer to isolated products.A mechanistic route is suggested for the generation of 2-substituted aryl (indolyl) kojic acid derivatives from the reaction of an aromatic aldehyde, kojic acid, and indole derivatives in the presence of Kaolin/Ag nanocomposite and role of Kaolin/Ag nanocomposite shown as the catalyst in this proposed mechanism (Scheme2). The initiation step of this chain process begins with the interaction of aldehyde and Kaolin/Ag nanocomposite. The subsequent reaction between the activated aldehyde and kojic acid takes place with the formation of the enone. The resulting enone may undergo Michael’s addition with indole to give the desired product as depicted in Scheme 2.Scheme 2
Proposed mechanism for 2-substituted aryl (indolyl) kojic acid synthesis.


## 4. Conclusion

In summary, by adsorption phase nanoreactor technique, Kaolin/Ag nanocomposite material is synthesized and has shown that it has advantages in the preparation of 2-substituted aryl (indolyl) kojic acid derivatives such as shorter reaction times and simple workup and affords excellent yield. The present method does not involve any hazardous organic solvent. Therefore, this procedure could be classified as green chemistry.



---