# Fast Coprecipitation of Calcium Phosphate Nanoparticles inside Gelatin Nanofibers by Tricoaxial Electrospinning

Authors: Silvia Panzavolta; Chiara Gualandi; Andrea Fiorani; Barbara Bracci; Maria Letizia Focarete; Adriana Bigi
Journal: Journal of Nanomaterials
 (2016)

---

## Abstract

We present an effective method for fabricating electrospun gelatin nanofibers containing well-dispersed inorganic nanoparticles. The new method encompasses the use of a special triaxial needle where mixing calcium and phosphate aqueous solutions in an intermediate needle yield calcium phosphate (CaP) nanoparticles that immediately after precipitation are dragged by the outer polymeric solution and incorporated directly in the electrospinning jet, before nanofiber formation. Gelatin electrospun mats containing different amounts of CaP nanoparticles were prepared and characterized by SEM, TEM, TGA, and stress-strain measurements. The results demonstrate that CaP particles having diameter of few tens of nanometers were successfully introduced in the gelatin nanofibers during the electrospinning process and that they were well dispersed throughout the fiber length. In addition, the use of the special triaxial needle enabled modulating the CaP amount in the nanofibers.


---

## Body

## 1. Introduction

In recent years electrospinning technology has attracted increasing interest for applications in the field of bone regeneration [1–3]. This scaffold fabrication technique is cheap and scalable; moreover it offers the possibility to process a great variety of polymers, both synthetic and natural, into continuous fibers having micro- to nanometric diameters with controlled surface texture and orientation. The extracellular matrix of bone is a complex nanocomposite with a multilevel hierarchical structure of its two main components, inorganic hydroxyapatite and collagen fibers [4]. Thus, it is not surprising that most of the scaffolds proposed for bone tissue engineering are biodegradable and bioactive polymer/inorganic composites [5–8]. These systems not only mimic bone extracellular matrix but also combine advantages of both polymers and inorganic materials, thus offering a promising approach to overcome the drawbacks encountered when single-component scaffolds are used [9]. Since the polymeric organic phase is poorly bioactive and is scarcely useful for inducing bone regeneration [5], bioactive inorganic substances, such as bioglasses and calcium phosphates, are introduced in polymer matrices in order to confer bioactivity to the scaffolds.Nonwoven electrospun composite scaffolds for bone tissue engineering are commonly produced by applying two main approaches: (i) direct electrospinning of a dispersion of inorganic particles in a polymeric solution [10] and/or (ii) immersion of the as-spun polymeric scaffolds into calcifying solutions that slowly generate an inorganic coating on the fiber surface (post-mineralization process) [11–14]. In the first approach previously synthesized inorganic particles are added to the polymeric solution to get a homogeneous dispersion, often by using sonication [15–17]. However, this method is not always feasible. To improve the quality and the stability of the suspension some authors increased the hydrophilicity of the polymeric component [18] while others functionalized the inorganic particles at the surface to enhance the compatibility with the polymeric solution [19]. The requirement to maintain the stability of the suspension over the entire duration of the electrospinning process, to guarantee a constant composition and equal dispersion of the inorganic particles in the polymeric fibers throughout the entire mat thickness, is however not easily fulfilled. To gain a more stable suspension another approach was to precipitate the inorganic particles in the presence of the polymeric phase and then dissolve the composite for electrospinning [20–23].On the other hand, the post-mineralization approach requires a post-processing step to introduce the inorganic phase in the electrospun scaffold that complicates and prolongs the scaffold fabrication procedure. In addition, the deposition of the inorganic phase on fiber surface may not be homogeneous throughout the entire scaffold thickness.In this work we developed an alternative approach to fabricate composite electrospun mats that enables the homogeneous dispersion of the inorganic phase in the polymeric fibers thanks to anin situ generation of calcium phosphate (CaP) nanoparticles directly in the electrospinning jet, before nanofiber formation. This was achieved by means of a specifically designed triaxial needle (Figure 1) for the electrospinning process. This particular needle is composed of an inner capillary filled with an aqueous solution containing phosphate ions, an intermediate capillary that brings calcium ions aqueous solution, and an outer needle carrying a polymeric gelatin solution. Gelatin was chosen because it resembles the chemical composition of natural bone ECM, it is highly biocompatible and lowly immunogenic, and furthermore it displays a favorable cellular interaction [14]. The conformation of the inner needle enables extruding the phosphate solution from several holes promoting the mixing with the calcium solution. The three capillaries are mutually positioned, as showed in Figure 1, so that at first the solutions containing calcium (inner needle) and phosphate (intermediate needle) ions come in contact and produce CaP nanoparticles inside the intermediate needle, before coming in contact with the gelatin solution (ejected in the outer needle). Composite electrospun mats of gelatin containing CaP nanoparticles have been produced in this work by using the above described approach. The presence and the distribution of the inorganic particles were investigated by Scanning Electron Microscopy equipped with energy dispersed X-ray spectrometer, Transmission Electron Microscopy, and Thermogravimetric Analysis. The effect of the presence of the inorganic phase on scaffold mechanical properties has been also investigated by tensile stress-strain measurements.Figure 1
Sketch of the triaxial needle configuration and enlargement of the needle internal structure. The feeding solutions were (i) phosphorous-based water solution in the inner needle; (ii) calcium-based water solution in the intermediate needle; (iii) gelatine solution in the outer needle.


## 2. Materials and Methods

### 2.1. Materials

Type A Gelatin (280 Bloom, Italgelatine SpA) from pig skin was used. Acetic acid (AcOH) was purchased from Sigma-Aldrich and used without further purification. Calcium chloride dihydrate (CaCl2·2H2O) and sodium phosphate monobasic dodecahydrate (Na3PO4·12H2O) were purchased from Carlo Erba and used without further purification.


### 2.2. Preparation of Electrospun Scaffolds

The in-house built electrospinning apparatus is composed of a high voltage power supply (Spellman SL 50 P 10/CE/230), two syringe pumps (KD Scientific 200 series), a glass syringe, a stainless steel triaxial needle connected to the power supply electrode, and a grounded aluminum collector (10 cm× 10 cm). The triaxial needle used in the present work (Figure 1) is constituted by an inner needle (OD = 0.9 mm; ID = 0.6 mm), positioned concentrically to the intermediate needle (OD = 1.5 mm; ID = 1.2 mm), and an outer needle (OD = 2.2 mm; ID = 1.8 mm). The tip of the outer needle protrudes 2 cm below that of the intermediate one which in turn protrudes 2 cm below the tip of the inner needle. In addition, the tip of the inner needle presents twenty little holes regularly distributed along the wall for a length of 1 cm. The solutions were dispensed at a controlled flow rate (as specified below) by using the syringe pumps through a Teflon tube to the needles.Gelatin was dissolved in AcOH : H2O (60 : 40 v/v) at a concentration of 30% w/v to prepare the shell solution. The inner needle was fed by a solution containing different amount of CaCl2·2H2O, in Double Distilled Water (DDW) (Ca solution), while the intermediate needle contained a solution obtained by dissolving Na3PO4·12H2O in DDW (P solution): different concentrations were tested (by keeping Ca/P molar ratio equal to 1) in order to obtain scaffolds with different inorganic phase contents. The scaffolds were labeled GCaP50, GCaP250, and GCaP375, accordingly to the concentrations of Ca and P solutions, that is, 50, 250, and 375 mM, respectively. The flow rate of the shell solution was set at 0.3 mL/h while those of the inner and intermediate solutions were 0.12 mL/h. The triaxial needle was placed vertical to the collecting plate at a distance of 20 cm and the applied voltage was set at 18 kV. Mats of pure gelatin (G), used as reference sample, were produced by feeding the inner and intermediate needle with MilliQ water and by using the same electrospinning parameters. Electrospun mats were kept under vacuum over P2O5 at room temperature (RT) overnight in order to remove residual solvents.


### 2.3. Instrumental Techniques

The inorganic phase obtained by electrospraying Ca and P solutions was collected on a Titanium disc and characterized by means of X-ray diffraction (XRD). XRD measurements were performed using a PANalytical X’Celerator powder diffractometer. CuKα radiation was used (40 mA, 40 kV). The 2θ range was from 20° to 40° with a step size of 0.05° and time/step of 20 s. Morphological observations were carried out using a Philips XL-20 Scanning Electron Microscope (SEM) equipped with energy dispersed X-ray spectrometer (EDS) by applying an accelerating voltage of 15 kV. Samples were sputter-coated with gold prior SEM analysis. Fiber diameter distributions were determined by using image analysis software (EDAX Genesis) through the measurement of about 150 fibers. Thermogravimetric analysis (TGA) was performed with a TA Instruments TGA2950 thermogravimetric analyzer from RT to 800°C (heating rate 10°C min−1, purge gas air). Electrospun fibers supported on conventional copper microgrids were observed by using a Philips CM 100 Transmission Electron Microscope (TEM) operating at 80 kV. Tensile stress-strain measurements were performed by using a Dynamic Mechanical Thermal Analyzer (DMTA, TA Instruments Q800 series) equipped with tension-film clamps. All the analyses were performed on rectangular strips cut from electrospun mats (width = 5 mm; gauge length about 10 mm; thickness = 0.040 ÷ 0.090 mm, measured by a microcaliper) by applying a preload force of 0.008 N and using a cross-head speed of 0.5 mm/min. Eight replicate specimens were run for each sample and mechanical data, tensile elastic modulus (E), stress at break (σb), and deformation at break (εb), were given as the average value ± standard deviation.


## 2.1. Materials

Type A Gelatin (280 Bloom, Italgelatine SpA) from pig skin was used. Acetic acid (AcOH) was purchased from Sigma-Aldrich and used without further purification. Calcium chloride dihydrate (CaCl2·2H2O) and sodium phosphate monobasic dodecahydrate (Na3PO4·12H2O) were purchased from Carlo Erba and used without further purification.


## 2.2. Preparation of Electrospun Scaffolds

The in-house built electrospinning apparatus is composed of a high voltage power supply (Spellman SL 50 P 10/CE/230), two syringe pumps (KD Scientific 200 series), a glass syringe, a stainless steel triaxial needle connected to the power supply electrode, and a grounded aluminum collector (10 cm× 10 cm). The triaxial needle used in the present work (Figure 1) is constituted by an inner needle (OD = 0.9 mm; ID = 0.6 mm), positioned concentrically to the intermediate needle (OD = 1.5 mm; ID = 1.2 mm), and an outer needle (OD = 2.2 mm; ID = 1.8 mm). The tip of the outer needle protrudes 2 cm below that of the intermediate one which in turn protrudes 2 cm below the tip of the inner needle. In addition, the tip of the inner needle presents twenty little holes regularly distributed along the wall for a length of 1 cm. The solutions were dispensed at a controlled flow rate (as specified below) by using the syringe pumps through a Teflon tube to the needles.Gelatin was dissolved in AcOH : H2O (60 : 40 v/v) at a concentration of 30% w/v to prepare the shell solution. The inner needle was fed by a solution containing different amount of CaCl2·2H2O, in Double Distilled Water (DDW) (Ca solution), while the intermediate needle contained a solution obtained by dissolving Na3PO4·12H2O in DDW (P solution): different concentrations were tested (by keeping Ca/P molar ratio equal to 1) in order to obtain scaffolds with different inorganic phase contents. The scaffolds were labeled GCaP50, GCaP250, and GCaP375, accordingly to the concentrations of Ca and P solutions, that is, 50, 250, and 375 mM, respectively. The flow rate of the shell solution was set at 0.3 mL/h while those of the inner and intermediate solutions were 0.12 mL/h. The triaxial needle was placed vertical to the collecting plate at a distance of 20 cm and the applied voltage was set at 18 kV. Mats of pure gelatin (G), used as reference sample, were produced by feeding the inner and intermediate needle with MilliQ water and by using the same electrospinning parameters. Electrospun mats were kept under vacuum over P2O5 at room temperature (RT) overnight in order to remove residual solvents.


## 2.3. Instrumental Techniques

The inorganic phase obtained by electrospraying Ca and P solutions was collected on a Titanium disc and characterized by means of X-ray diffraction (XRD). XRD measurements were performed using a PANalytical X’Celerator powder diffractometer. CuKα radiation was used (40 mA, 40 kV). The 2θ range was from 20° to 40° with a step size of 0.05° and time/step of 20 s. Morphological observations were carried out using a Philips XL-20 Scanning Electron Microscope (SEM) equipped with energy dispersed X-ray spectrometer (EDS) by applying an accelerating voltage of 15 kV. Samples were sputter-coated with gold prior SEM analysis. Fiber diameter distributions were determined by using image analysis software (EDAX Genesis) through the measurement of about 150 fibers. Thermogravimetric analysis (TGA) was performed with a TA Instruments TGA2950 thermogravimetric analyzer from RT to 800°C (heating rate 10°C min−1, purge gas air). Electrospun fibers supported on conventional copper microgrids were observed by using a Philips CM 100 Transmission Electron Microscope (TEM) operating at 80 kV. Tensile stress-strain measurements were performed by using a Dynamic Mechanical Thermal Analyzer (DMTA, TA Instruments Q800 series) equipped with tension-film clamps. All the analyses were performed on rectangular strips cut from electrospun mats (width = 5 mm; gauge length about 10 mm; thickness = 0.040 ÷ 0.090 mm, measured by a microcaliper) by applying a preload force of 0.008 N and using a cross-head speed of 0.5 mm/min. Eight replicate specimens were run for each sample and mechanical data, tensile elastic modulus (E), stress at break (σb), and deformation at break (εb), were given as the average value ± standard deviation.


## 3. Results and Discussion

The use of supersaturated calcifying solutions to obtain precipitation of poorly crystalline calcium phosphate phases with different stoichiometry is well known in literature [24–26]. The Ca and P solutions employed in this work have a simplified composition with respect to those previously published [27] which are used to cover metallic substrates with an apatitic coating. In fact, in this study, in order to obtain a fast precipitation of nanoparticles inside the electrospinning needles, the previously used buffered solution containing carbonate ions [28] was substituted with a simple aqueous solution. The triaxial needle with the peculiar configuration shown in Figure 1 was specifically designed to produce calcium phosphate nanoparticles inside the gelatin nanofibers. In brief, the inner capillary is loaded with the P solution that comes in contact with the Ca solution flowing in the intermediate capillary. The two solutions have the same molar concentrations of calcium and phosphate ions and they are delivered at the same flow rate. Moreover, the appositely perforated inner needle enables mixing of Ca and P solutions inside the intermediate capillary to give the precipitation of a calcium phosphate phase. Nanoparticles of CaP, which are expected to precipitate, can be dragged out by the gelatin solution and incorporated inside the polymeric nanofibers. The solutions mixing time can be controlled by regulating the protrusion of the internal needle with respect to the external one.In order to investigate the composition of the inorganic phase, we electrosprayed the Ca and P solutions, in absence of gelatin, on a Titanium (Ti) disk collector. The CaP coated disk was accurately rinsed with distilled water before submitting it to XRD analysis, to remove soluble salts (i.e., NaCl) formed in the precipitation reaction. The XRD pattern reported in Figure2(b) shows the presence of a broad peak at about 25,9° of 2θ and a more intense and broader peak centered at about 32° of 2θ, confirming the effective formation of a poorly crystalline apatitic phase. The concentrations of the Ca and P solutions were such to yield a Ca/P molar ratio of 1.0. The precipitation of an apatitic phase is in agreement with the pH of the mixed Ca-P solution, which was 6.8. At this pH value, hydroxyapatite is the more stable phase [29].Figure 2
Powder X-ray diffraction patterns of (a) Ti collector; (b) inorganic phase deposited on the Ti collector.Electrospun samples containing different amounts of calcium and phosphate were fabricated by changing the initial concentration of the Ca and P starting solutions, while keeping constant all other parameters. Figure3 reports SEM images of gelatin mats enriched with different amounts of CaP nanoparticles. All samples showed bead-free nanofibers with similar morphology and diameters in the range 100–300 nm, indicating that the inclusion of CaP had no evident effect on the nanofiber diameter, as previously found by other authors using different types of inorganic phase [16, 17, 19]. Nanofibers from different samples had a smooth surface and no appreciable presence of nanoparticles at fibers surface, as also confirmed by the images at higher magnification of GCaP250 and GCaP375 in Figures 3(e) and 3(f), respectively. The presence of dispersed nanoparticles was appreciated by TEM analysis, especially for sample GCaP375, as it can be seen in Figures 4(b)–4(d): the inorganic phase was well distributed along the nanofibers in the form of nanoparticles with diameters of few tens of nanometers. On the other hand, in sample GCaP50 very few aggregates were visible and they were not homogeneously distributed along all the fibers (Figure 4(a)).Figure 3
SEM micrographs of G (a), GCaP50 (b), GCaP250 ((c), (e)), and GCaP375 ((d), (f)). Scale bar: 2µm ((a)–(d)); 1 µm ((e), (f)).
(a) (b) (c) (d) (e) (f)Figure 4
TEM images of GCaP50 (a) and of GCaP375 ((b)–(d)) samples. Scale bars: 1µm ((a), (b)); 100 nm ((c), (d)).
(a) (b) (c) (d)TGA analysis reported in Figure5 shows that the weight residue at 700°C, after the complete degradation of the polymeric organic phase, increased with the increasing of the starting solutions concentration, demonstrating that the amount of inorganic phase inside the nanofibers can be modulated during the mat fabrication process. In particular, the residual weight percentage was 0%, 2,5%, 5%, and 8% for G, GCaP50, GCaP250, and GCaP375, respectively. The results fit with the theoretical ones, calculated, taking into account all the ionic species present in the electrospinning solutions.Figure 5
TGA curves of G (a), GCaP50 (b), GCaP250 (c), and GCaP375 (d).Figure6 reports EDS spectra of GCaP50 and GCaP375 samples in the range 0–6 keV (no peaks were observed at energies higher than 6 keV). As expected, Ca and P were detected together with Cl and Na, which acted as counterions in the starting solutions. It is evident that peak intensities increase with the increasing of ionic concentrations in the starting solutions. It is pointed out that EDS analysis cannot distinguish the ions of the apatitic phase from those present in ionic form, if any: thus a quantitative measure of the apatitic phase is not reliable.Figure 6
EDS spectra of GCaP50 and GCaP375.Tensile stress-strain analysis of the composite samples was carried out and compared with that of pure gelatin sample (mechanical data are reported in Table1 and representative curves are reported in Figure 7). Mats display a typical elastoplastic behavior where the stress-to-strain ratio was constant for low strain values (corresponding to the elastic modulus) followed by a plastic deformation at higher strain up to failure. Mechanical properties were affected by the presence of the inorganic phase. In particular, with respect to the mats of pure gelatin, the addition of a small amount of CaP provoked a decrease of the value of the elastic modulus, E, of about 50% (compare G and GCaP50 samples). At higher CaP contents the value of the elastic modulus increased up to a value similar to that of pure gelatin in GCaP250 sample and an even greater value in GCaP375 sample. The stress at break values followed a similar trend while the strain at break followed an almost opposite trend. It is pointed out that, in general, the addition of inorganic particles to a polymeric phase is known to enhance the mechanical strength and elastic modulus when the inorganic particles are fine and evenly dispersed. In the case of electrospun fibers, this is typically observed for very low amounts of filler, while at higher nanoparticles concentrations the mechanical properties get weaker as a consequence of nanoparticles agglomeration [17, 19, 30]. However, some authors found improvement of mat mechanical properties also at very high concentrations of inorganic additive (up to 40 wt%) [15, 22]. In our case, the worsening of the mechanical properties of the GCaP50 sample with respect to G mat might be ascribed to the fact that, at low CaP concentrations, the inorganic phase is not homogeneously distributed along all polymer nanofibers and generates discontinuity zones acting as weak points (see Figure 4(a)). On the contrary, at higher nanoparticle loadings the well-distributed inorganic phase (see Figures 4(b)–4(d)) can act as reinforcement.Table 1
Mechanical properties of G, GCaP50, GCaP250, and GCaP375: tensile modulus (E), stress at break (σb), and strain at break (εb).
Sample E (MPa) σ b (MPa) ε b (%) G 90 ± 6 3.5 ± 0.4 18 ± 1 GCaP50 38 ± 8 2.8 ± 0.3 25 ± 3 GCaP250 90 ± 30 4 ± 1 15 ± 6 GCaP375 150 ± 10 5.4 ± 0.5 15 ± 3Figure 7
Stress-strain curves of G, GCaP50, GCaP250, and GCaP375.


## 4. Conclusions

In this work we electrospun gelatin nanofibers loaded with calcium phosphate nanoparticles by means of an innovative triaxial needle that was proved to be effective in electrospinning a polymer solution with the concomitant fast coprecipitation of inorganic nanoparticles from calcium and phosphate aqueous solutions. XRD analysis confirmed that the nanoparticles generated inside the nanofibers were a poorly crystalline apatitic phase and TEM images showed that nanoparticles were homogenously dispersed in the gelatin nanofibers, thus overcoming some drawbacks of other commonly employed methods for fabricating nanocomposite electrospun scaffolds. Furthermore, by using the special triaxial needle we were able to modulate the amount of inorganic phase added inside the nanofibers that in turn conditioned the mechanical properties of mats. The innovative method proposed in this work, besides ensuring a homogenous dispersion of the inorganic phase within polymeric fibers, prospectively is suitable for fabricating electrospun scaffolds with graded composition, by simply controlling the flow rate of the different solutions involved in the process.



---

*Source: 4235235-2016-10-31.xml*