# Synthesis and Characterization of Nickel-Alumina Composites from Recycled Nickel Powder

Authors: V. G. Karayannis; A. K. Moutsatsou
Journal: Advances in Materials Science and Engineering
 (2012)

---

## Abstract

The recycling of metallic waste to create more valuable materials and their valorization into upgraded metal-based composites constitutes an important field of study. The composite industry nowadays considers environmental improvements as important as other properties of the materials. In the present paper, nickel powder was recycled from ferrous scrap, a low-cost and largely available material, by an effective hydrometallurgical recovery process. Then, this recycled powder was successfully used along with particulateα-alumina to prepare oblong nickel-based composite specimens with ceramic reinforcement loadings ranging from 0 to 30 wt.% by applying powder processing manufacturing techniques including cold isostatic pressing (CIP) and sintering. The microstructures obtained were characterized, the specimens were subjected to three-point bend tests, and their fracture behaviour was evaluated. By increasing the % ceramic reinforcement content, density clearly decreases while strengthening is achieved, thus leading to development of lightweight and enhanced oblong nickel-alumina composites. The composite microstructure, and particularly the metal-ceramic interface bonding, has a strong impact on fracture behaviour upon external loading.


---

## Body

## 1. Introduction

The valorization of materials recovered from scrap (metallic waste), a low-price secondary material, into value-added composites, represents a challenge with important technological, economic, and environmental aspects. Metal-ceramic composites, in particular, often exhibit improved properties with respect to their corresponding monolithic counterparts [1–7]. The development of such upgraded composites starting from materials recycled from metallic waste may be of particular interest, because of the possibility to reduce the production cost while also responding to environmental demands that are nowadays imposed by the decrease of ore deposits as well as by problems caused by waste rejection. Furthermore, including recyclates in products can lower carbon footprint and provide a marketing edge. It should be noted that the composite industry prioritizes nowadays environmental improvements as much as other composite properties and several companies are now incorporating recycled materials in composite products.In order to recover high-grade ferrous and nonferrous metal fractions from metallic waste, much attention has been paid to separation processes for the various materials contained in scrap [8–10]. Usually, pyrometallurgical and hydrometallurgical processes are employed for treating solid wastes. High-energy requirement and need of dust collecting and gas cleaning systems are known as the major drawbacks of the pyrometallurgical methods. The hydrometallurgical processes are more environmentally suitable and economic to treat such materials and play an important role in the extraction and recovery of metals from various media. Besides the operational cost, leaching medium also decides what method of acid leaching will be suitable—relatively cheap acetic acid, cheap and available sulphuric acid, or aggressive chloride medium [11–14]. Therefore, an obvious opportunity for hydrometallurgical processing lies in recycling and processing of secondary sources such as ferrous scrap. However, hydrometallurgy has not yet found much application in this area, due to problems such as slow dissolution of the scrap and instability of highly concentrated solutions.In the present study, the recovery of nickel powder from metallic waste (ferrous scrap), a low cost and largely available material, was attained by an attractive hydrometallurgical process [15, 16] that can provide metal and alloy powders, with properties generally similar to typical commercial grades, thus appropriate for the elaboration of nickel-based composites. The cost of the so-produced nickel powder has been estimated as less as 1/3 of that of commercial grades.For investigating the development of metal-based composites, nickel-alumina can be chosen as a model metal-ceramic system. Actually, nickel presents a great interest for various applications. Especially, powder metallurgical nickel-alloy products show improved properties over conventional cast and wrought alloy products. Moreover, nickel-base alloys in the form of superalloys have already proven their usefulness in demanding environments [17–20]. Alumina has low density, electrical resistivity and coefficient of thermal expansion, high hardness, and specific stiffness, and is one of the most stable oxides, providing excellent oxidation and corrosion resistance and good high-temperature mechanical properties. In the form of embedded particles, coatings, or substrates, alumina is now an integral part of novel thermal barrier coating systems proposed for advanced applications [21–24]. Also, the properties of pure materials of this metal-ceramic system are well characterized in a wide temperature range. Indeed, there exists a large mismatch in properties between these two materials that poses a challenge for combining the attractive characteristics of each constitutive phase in a new optimized material with advanced behaviour. Moreover, such metal-ceramic materials, particulate or even functionally graded, can be formed through conventional and economical powder metallurgical routes, although chemical techniques, like in situ reaction processing or sol-gel processing, are also investigated for that purpose [25–30]. In addition, the microstructure stability of this system allows heating at the relatively elevated temperatures required for sintering without formation of undesirable brittle interfacial reaction products, given that nickel does not react with alumina under 1150°C [31]. In consequence, microstructures consisting of nickel and alumina are broadly considered able to satisfy the standards for structural applications in high-temperature demanding environments.The encouraging results of a preliminary research using lower cost nickel powder recycled from ferrous scrap (by the aforementioned hydrometallurgical process) in nickel-alumina pellets fabrication by uniaxial cold pressing, an elemental powder metallurgy technique, lead in the present study to the application of a more effective solid-state powder metallurgy method, comprising cold isostatic pressing (CIP) followed by sintering, in order to elaborate oblong nickel-alumina composites starting from recycled nickel powder and particulateα-alumina, and to evaluate their mechanical and fracture behaviour.


## 2. Materials and Methods

### 2.1. Raw Materials—Recycling

In Greece, the market research regarding ferrous scrap leads to the conclusion that only a small percentage of this solid waste is recycled in the steel production industries, covering a 50% of the required raw material, while stainless steel scrap is exported. Unfortunately, the main part of ferrous scrap is rejected raising increasing environmental concerns.In the present study, samples of this secondary raw material in the form of industrial cutting disks from high-speed tools were selected. According to the analyses results presented in Table1, this ferrous scrap can be classified as stainless steel 316, an alloy that is broadly used in various applications, from chemical industry to pipeline and reactor construction.Table 1
Ferrous scrap characterization.
Elements%Fe64.4Cr18.2Ni12.7Mo2.7Mn1.1Si0.5Co0.2Cu0.1C0.03S0.003P0.007TiTracesA hydrometallurgical process was developed, according to which, iron, chromium, nickel, and molybdenum can be recovered from ferrous scrap in powder form, appropriate for powder metallurgy applications. A hydrometallurgical process consists in general of a dissolution stage, a solvent extraction, and the stripping of loaded organic solution stage, and finally the stage of condensation and crystallization of the metal salts. Basic objectives of the recovery process were the following:(i)
extraction of metals of the highest economic value,(ii)
use of simple unitary operations requiring a minimum investment,(iii)
working at low temperature with dilute reagents and at low concentrations,(iv)
the working liquor should be recyclable to minimize costs,(v)
production of a final product in powder form with considerable added value.Dissolution of scrap was performed by leaching with hydrochloric acid loaded with chlorine gas. After evaluation, leaching temperature and time conditions employed were 60°C and 1.5 h, respectively. Versatic 6 (Shell Company Ltd.), a synthetic carboxylic acid, and commercial Kerosene were used for the solvent extraction step. Versatic 6 is a dialkyl alkanoic acid of a molecular weight of 116, empirical formula C6H12O2, and purity 99% (according to the technical bulletin of the company). Due to the utilization of this acidic cation exchanger, it is easy, by changing the solution pH, to achieve selective retention of the metals by forming complexes. Mixing the scrap solution with the organic phase at pH = 2, molybdenum is being bound. After the separation of the phases by adjusting the aqueous phase to pH = 3, iron is separated, and repeating the procedure at pH = 5.3, chromium is drown away. At last, the aqueous solution is enriched in nickel, and then nickel chloride crystals are obtained by evaporation and crystallization. Finally, nickel powder is produced by hydrogen reduction of the nickel chlorides at 300°C for 1.5 h. The flowsheet of the hydrometallurgical process for nickel recovery in powder form is presented in Figure 1, where the optimum proposed experimental conditions are also reported.Figure 1
Flowsheet of the hydrometallurgical method for nickel recovery in powder form, showing the process optimal conditions.The nickel powder so-produced and then used as a raw material for the fabrication of nickel-based composites has a purity of 99.90%, a specific gravity of 8.83 g/cm3, and a specific surface of 3500 cm2/g. Therefore, its properties are similar to these of typical commercially available powders produced by atomization. α-Alumina powder (corundum, 0.9 μm mean particle size, 99% purity) from Aldrich Chemical Company, Inc. was selected as the ceramic constituent. The particle size distribution of nickel and alumina powders used is comparatively depicted in Figure 2. A difference in granulometry between metal and ceramic powders is shown in Figure 2. Such particle size differences have been considered beneficial to more efficient particle packing during powder mixture compression.Figure 2
Particle size distribution of nickel and alumina powders.


### 2.2. Fabrication of Nickel-Alumina Composites

Powder processing techniques were applied in order to prepare nickel-alumina composite samples with alumina loadings ranging between 0–30 wt.%. First, nickel and alumina powders were dry mixed, and the mixtures were pressed to form a series of oblong cylindrical composite bars, appropriate for mechanical testing, by using cold isostatic pressing (CIP, 2000 bar). Compaction difficulties with regard to composite specimen integrity and strength, especially in the specimens with the higher % alumina amount, were observed. To overcome these hindrances, polypropylene carbonate (PPC) was incorporated in all mixtures as a binder. Then, the sintering procedure was carried out within a temperature/atmosphere controlled furnace for the consolidation of the composite bars. The following sintering conditions were selected after optimization: all compacts were first preheated at 400°C for 1 h for the additive decomposition, then sintered at 1200°C for 4 h in inert atmosphere, and finally gradually cooled to room temperature in the furnace, also in inert atmosphere, to minimize oxidation and quenching.


### 2.3. Characterization and Mechanical Testing

Phase identification of the sintered specimens was conducted by X-ray diffraction (XRD) measurements (Siemens, Diffractometer D-5000). The microstructural characterization of the samples was realised by light optical microscopy (Olympus, BX60M) as well as by Scanning Electron Microscopy (SEM) (Jeol, JSM-6400) coupled with Energy Dispersive X-ray Spectroscopy (EDX) analysis. Apparent density after sintering was measured by using a specific apparatus (Shimadzu, SMK401-AUW220V) according to the water immersion (Archimedes’) method. Then, relative densities were calculated using theoretical densities of the individual constituents. Modulus of elasticity and fracture strength were determined from three-point bending tests carried out on rectangular bars—machined from the fabricated cylindrical ones and then ground and polished on the tensile surface—in a load frame (Instron), with a crosshead speed of 0.1 mm/min. The initial portion of the loading curve was used for the Young’s modulus determination. All samples were loaded to failure, except for the 100% nickel ones for which the plastic deformation exceeded 2%. Finally, fracture surfaces were studied.


## 2.1. Raw Materials—Recycling

In Greece, the market research regarding ferrous scrap leads to the conclusion that only a small percentage of this solid waste is recycled in the steel production industries, covering a 50% of the required raw material, while stainless steel scrap is exported. Unfortunately, the main part of ferrous scrap is rejected raising increasing environmental concerns.In the present study, samples of this secondary raw material in the form of industrial cutting disks from high-speed tools were selected. According to the analyses results presented in Table1, this ferrous scrap can be classified as stainless steel 316, an alloy that is broadly used in various applications, from chemical industry to pipeline and reactor construction.Table 1
Ferrous scrap characterization.
Elements%Fe64.4Cr18.2Ni12.7Mo2.7Mn1.1Si0.5Co0.2Cu0.1C0.03S0.003P0.007TiTracesA hydrometallurgical process was developed, according to which, iron, chromium, nickel, and molybdenum can be recovered from ferrous scrap in powder form, appropriate for powder metallurgy applications. A hydrometallurgical process consists in general of a dissolution stage, a solvent extraction, and the stripping of loaded organic solution stage, and finally the stage of condensation and crystallization of the metal salts. Basic objectives of the recovery process were the following:(i)
extraction of metals of the highest economic value,(ii)
use of simple unitary operations requiring a minimum investment,(iii)
working at low temperature with dilute reagents and at low concentrations,(iv)
the working liquor should be recyclable to minimize costs,(v)
production of a final product in powder form with considerable added value.Dissolution of scrap was performed by leaching with hydrochloric acid loaded with chlorine gas. After evaluation, leaching temperature and time conditions employed were 60°C and 1.5 h, respectively. Versatic 6 (Shell Company Ltd.), a synthetic carboxylic acid, and commercial Kerosene were used for the solvent extraction step. Versatic 6 is a dialkyl alkanoic acid of a molecular weight of 116, empirical formula C6H12O2, and purity 99% (according to the technical bulletin of the company). Due to the utilization of this acidic cation exchanger, it is easy, by changing the solution pH, to achieve selective retention of the metals by forming complexes. Mixing the scrap solution with the organic phase at pH = 2, molybdenum is being bound. After the separation of the phases by adjusting the aqueous phase to pH = 3, iron is separated, and repeating the procedure at pH = 5.3, chromium is drown away. At last, the aqueous solution is enriched in nickel, and then nickel chloride crystals are obtained by evaporation and crystallization. Finally, nickel powder is produced by hydrogen reduction of the nickel chlorides at 300°C for 1.5 h. The flowsheet of the hydrometallurgical process for nickel recovery in powder form is presented in Figure 1, where the optimum proposed experimental conditions are also reported.Figure 1
Flowsheet of the hydrometallurgical method for nickel recovery in powder form, showing the process optimal conditions.The nickel powder so-produced and then used as a raw material for the fabrication of nickel-based composites has a purity of 99.90%, a specific gravity of 8.83 g/cm3, and a specific surface of 3500 cm2/g. Therefore, its properties are similar to these of typical commercially available powders produced by atomization. α-Alumina powder (corundum, 0.9 μm mean particle size, 99% purity) from Aldrich Chemical Company, Inc. was selected as the ceramic constituent. The particle size distribution of nickel and alumina powders used is comparatively depicted in Figure 2. A difference in granulometry between metal and ceramic powders is shown in Figure 2. Such particle size differences have been considered beneficial to more efficient particle packing during powder mixture compression.Figure 2
Particle size distribution of nickel and alumina powders.


## 2.2. Fabrication of Nickel-Alumina Composites

Powder processing techniques were applied in order to prepare nickel-alumina composite samples with alumina loadings ranging between 0–30 wt.%. First, nickel and alumina powders were dry mixed, and the mixtures were pressed to form a series of oblong cylindrical composite bars, appropriate for mechanical testing, by using cold isostatic pressing (CIP, 2000 bar). Compaction difficulties with regard to composite specimen integrity and strength, especially in the specimens with the higher % alumina amount, were observed. To overcome these hindrances, polypropylene carbonate (PPC) was incorporated in all mixtures as a binder. Then, the sintering procedure was carried out within a temperature/atmosphere controlled furnace for the consolidation of the composite bars. The following sintering conditions were selected after optimization: all compacts were first preheated at 400°C for 1 h for the additive decomposition, then sintered at 1200°C for 4 h in inert atmosphere, and finally gradually cooled to room temperature in the furnace, also in inert atmosphere, to minimize oxidation and quenching.


## 2.3. Characterization and Mechanical Testing

Phase identification of the sintered specimens was conducted by X-ray diffraction (XRD) measurements (Siemens, Diffractometer D-5000). The microstructural characterization of the samples was realised by light optical microscopy (Olympus, BX60M) as well as by Scanning Electron Microscopy (SEM) (Jeol, JSM-6400) coupled with Energy Dispersive X-ray Spectroscopy (EDX) analysis. Apparent density after sintering was measured by using a specific apparatus (Shimadzu, SMK401-AUW220V) according to the water immersion (Archimedes’) method. Then, relative densities were calculated using theoretical densities of the individual constituents. Modulus of elasticity and fracture strength were determined from three-point bending tests carried out on rectangular bars—machined from the fabricated cylindrical ones and then ground and polished on the tensile surface—in a load frame (Instron), with a crosshead speed of 0.1 mm/min. The initial portion of the loading curve was used for the Young’s modulus determination. All samples were loaded to failure, except for the 100% nickel ones for which the plastic deformation exceeded 2%. Finally, fracture surfaces were studied.


## 3. Results and Discussion

After sintering, densified nickel-alumina oblong composite specimens were successfully developed (Figure3).Figure 3
Photograph of a sintered 30 wt.% ceramic content nickel-alumina composite.The high purity and the relatively small particle size (providing an increased specific surface energy) of the used nickel powder recycled from metallic waste should contribute to an acceptable consolidation degree obtained at the relatively moderate sintering temperatures applied in the present work, as it can be deduced from the optical micrographs of sintered 20 and 30 wt.% ceramic loading nickel-alumina composites shown in Figure4. In these micrographs, lighter phase represents the metal and darker the ceramic constituent.Micrographs of sintered 20 wt.% (a) and 30 wt.% (b) ceramic content nickel-alumina composites.
(a)(b)At the sintering temperatures selected, densification occurs by coalescence of nickel particles by atomic diffusion that forms typical solid-state sintering necks binding the metal-ceramic composites, while poorer connectivity can be suggested in the ceramic phase. At lower % ceramic addition (Figure4(a)), the volume part of nickel phase containing interconnected metal particles apparently prevails over the ceramic part, thus a microstructure of a nickel matrix reinforced with alumina is obtained. However, when increasing the % ceramic constituent (Figure 4(b)), metal contiguity is decreased and the volume of sintered metal parts isolated between the ceramic additions is more pronounced.Metal (nickel) and ceramic (alumina) phases remain separate in Figure4, an indication of limited interdiffusion. A recent study attempted to elucidate the microscopic nature of metal-ceramic bonding and the influence of oxygen vacancies on adhesion at such metal/ceramic interfaces, and particularly at nickel/zirconia nickel-iron/zirconia interfaces, concluding that bonding mechanisms can involve two types of interactions, namely, the nickel-zirconium hybridization and nickel-oxygen ionic bonding [32].From Figure4, agglomerates of 5–25 μm are revealed in the ceramic phase. The particle size difference between metal and ceramic powders used (see Figure 2), although being considered beneficial to consolidation degree, may, at least partly, be responsible for the formation of such ceramic clusters when using powder compaction procedures.Alumina discrete particles or agglomerates, not always uniformly distributed in the nickel matrix, are located in Figure5 that provides SEM micrographs of a sintered 20 wt.% ceramic loading nickel-alumina composite, at two magnifications (the darker phase represents nickel and the lighter alumina, according to EDX analysis results). Also, an interfacial porosity is clearly revealed. These results lead to the conclusion that the necessary compression additive occupied a significant volume in these materials, thus creating pores after its removal during the green compacts thermal treatment. A bulk porosity ranging from 13.7% to 35.9% when increasing the % ceramic loading from 0 to 30 wt.% was determined in the sintered specimens. For this variation in consolidation degree, matrix volume contiguity limitations with the increasing % alumina addition should be taken into consideration.Micrographs of a sintered 20 wt.% ceramic content nickel-alumina composite, at two magnifications.
(a)(b)Apparent density of the sintered samples decreases from 7.6 g/cm3 to 4.1 g/cm3 when increasing the % amount of alumina introduced in the composites from 0 to 30 wt.%, due to the lower density of the ceramic versus the metallic constituent. The obtained results are even lower than the density values theoretically expected according to the rule of mixtures, because of residual porosity, thus confirming the microstructural observation results.Fracture behaviour of the specimens is illustrated in Figure6 that shows fracture surfaces of sintered nickel-based composite specimens after mechanical testing. In these micrographs, lighter phase depicts alumina and darker nickel matrix.Micrographs of fracture surfaces of sintered nickel-alumina composites after mechanical testing.
(a)(b)(c)(d)(e)(f)Deflection of catastrophic cracks from their initial propagation front in the nickel matrix, which is observed in Figures6(a), 6(b), and 6(c) and is believed to have beneficial effects on mechanical performance, can be associated with dislocations that are generated in the composites more ductile parts and can move during external loading to allow matrix plastic deformation, thus resulting in this effective mechanism of crack deflection. Such dislocations are due to residual thermal tensile stresses generated along the nickel-alumina interface during the composites cooling from the sintering temperature, because of a large thermal expansion coefficient mismatch between the constituents. In fact, in the ductile areas of the composites exhibiting strong interfacial bonds, relative interfacial movement of metal and ceramic materials as a result of these stresses is impeded, and therefore a matrix is locally deformed along the interface by the creation of high dislocation density. It should be emphasized here that this deflection of cracks preexisting or developed during external loading, by preventing an easy and continuous propagation due to the insertion of stiffer particulate reinforcement such as alumina, is precisely one of the main reasons to incorporate ceramic particles in a metal matrix. Crack propagation deflection in the matrix would possibly be even more intense if an interconnected ceramic network was also formed that could lead to stronger interfacial bonding. Frequent crack propagation through the ductile metal phase, such as this revealed in Figures 6(a), 6(b), and 6(c), must be responsible for some roughness the fracture surfaces exhibit, as a result of a certain degree of plastic deformation of nickel grains with necking before fracture occurs.On the other hand, a weak interface in composites brittle areas—where a limited plasticity exists and strain distribution is mainly controlled by relative thermal expansion coefficient and modulus of the constituents—allows some interfacial sliding as a result of residual thermal stresses. However, such interfacial movement is nonuniformly restricted by reinforcement network, thus leading in greater plastic deformation in some areas, and possibly even in the development of microcracks, mainly at the interface. These phenomena could be even more pronounced if higher fabrication temperatures were applied resulting in more intense thermal stresses in the bulk of the materials. Actually, the experimental evidence showed (Figure6(d)) that, in case of such a weak interface, plastic deformation during loading is followed by microcrack deflection along the metal-ceramic interface with its partial debonding that leads to a rather irregular crack propagation path. Such deflection, indicative of nonelastic actions taking place at the interface, as a result of the weak in this case interfacial bonding, is not able to act as a reinforcement mechanism, hence load transfer from matrix to ceramic reinforcement is decreased, thus degrading the composites strength. Naturally, crack deflection along the interface is preferable than crack propagation by ceramic particle cleavage or separation of contiguous particles in ceramic clusters. Such microdamages may develop during external loading or even originate from cooling. Microdamage accumulation can cause voids generation in the bulk of the materials, thus finally leading composites to failure. Actually, such brittle fracture of ceramic particles or clusters has also been located in some areas of these materials (Figures 6(e) and 6(f)). So, it can be concluded that fracture of a rather mixed intergranular and transgranular type is obtained.Crack initiation, propagation, and growth are not only influenced by metal-ceramic interfacial bonding and microdamage accumulation, but also by residual porosity. In particular, the interfacial porosity present in these materials causes matrix-ceramic particles decohesion under lower stresses and decreases the ability of load transfer to the reinforcement, and therefore it is detrimental to strength. Matrix porosity also affects the composites mechanical performance, as it decreases the composites load bearing area. In consequence, fracture occurs sooner after strain localization begins. Pore size distribution, pore shape, and flaws also count.Lack of homogeneity of the reinforcement distribution in the nickel matrix may also have an impact on strength. Particle clusters observed in the ceramic phase can be considered as sites of inherent potential microdamage, as they are not able to support the same amount of stress as nonclustered particles, because matrix areas surrounding them are subjected to higher stresses. Therefore, stress concentration regions are introduced in the matrix, hindering its plastic flow. Hence, matrix strengthening is restricted, as the development and accumulation of internal microdamages during testing is more likely to occur at lower applied stresses.All damages existing in the bulk of the materials, in the form of either debonding between metal and ceramic phases or poor sintering between contiguous ceramic particles or particle fracture, have even been treated in other studies on nickel-alumina composites as porosity deteriorating mechanical performance [33].The mechanical properties values of the nickel-based composites versus the alumina content (wt.%) are plotted in Figure7.Young’s modulus (a) and fracture strength (b) of nickel-alumina composites as a function of ceramic content (wt.%).
(a)(b)Young’s modulus and flexural strength of the composites increase progressively when increasing the addition of stiffer alumina particles. It can be suggested that this strengthening was achieved by two types of mechanisms: firstly, strain-induced load transfer from nickel matrix to reinforcement, given the relatively high % particulate ceramic loading, although matrix strength maintains an important role; secondly, strengthening mechanisms from the ceramic particles effect on the nickel matrix deformation by the inhibition of dislocations motion, already discussed. The restriction of matrix grain growth due to reinforcement particles presence in the matrix, and even due to residual porosity, must also be taken into account. Moreover, the small particle size of the alumina used in the present study is considered beneficial to this reduction of matrix grain (by limiting the motion of grain boundaries) and even to the restriction of microdamages accumulation during mechanical testing. The relatively moderate sintering conditions selected after optimization also contributed to prevent an exceeding matrix grain growth and permitted avoiding formation of brittle interfacial reaction products, which, otherwise, could lead to a weaker interface bond.This increase in mechanical properties (Figure7) combined with the aforementioned clear decrease in density leads to improvement of specific modulus and strength, which is broadly considered as one of the main advantages of metal-ceramic composites of this category. However, this improvement of mechanical performance is relatively limited, mainly because of the residual porosity revealed in these materials and the other microstructural features already discussed. Actually, porosity has a significant impact on mechanical behaviour, and a number of relationships have been proposed that relate the porosity level to mechanical properties. The empirical formulation (1) presented by Coble and Kingery has been used [25, 33] to correlate the elastic modulus, E, of nickel-alumina composites to the amount of porosity present in the composite, as follows:(1)E=E0(1-1.9ρ+0.9ρ2),
where ρ is the porosity and E0 is the Young’s modulus at full density.Bending ductility, in terms of minimum bend radius, the smallest radius around which a specimen can be bent without cracks being observed in the outer tension surface, varies slightly with the increasing ceramic loading. Naturally, it is clearly degraded compared to this of unreinforced nickel.


## 4. Conclusions

Nickel was recycled in powder form from metallic waste (ferrous scrap) by an effective hydrometallurgical process and successfully used into nickel-based composites with particulate alumina reinforcement ranging from 0 to 30 wt.%. The high purity and the relatively small particle size of this nickel powder seems contribute to an acceptable consolidation degree at the relatively moderate sintering temperatures applied, rendering the production of oblong nickel-alumina composites feasible.Mechanical behaviour depends on the % reinforcement content. When increasing the % addition of stiffer ceramic particles, apparent density clearly decreases while strengthening is progressively achieved. The composite microstructure has a strong impact on fracture behaviour upon external loading. Particularly, microcrack initiation, propagation, and growth are influenced by metal-ceramic interfacial bonding as well as by microdamage accumulation originated from cooling or developed during loading. Microcrack propagation deflection in the nickel matrix, indicative of a strong interface, is frequently observed in the composite ductile areas. Thus, lightweight nickel-based composites with improved specific modulus and fracture strength are obtained, which may be important for several applications. The energy savings that can be attained by such reduction of weight must be emphasized from the environmental point of view.



---