# The Influences of CuO/ZnO Ratios on the Crystallization Characteristics Electrical and Magnetic Properties ofCuxZn1−xO Powders

Authors: Kuan-Jen Chen; Fei-Yi Hung; Truan-Sheng Lui; Cheng-Hung Chen; Sheng-Po Chang
Journal: Journal of Nanoparticles
 (2013)

---

## Abstract

This study synthesizesCuxZn1−xO powders using an aqueous solution method. The CuxZn1−xO powders with different content ratios of CuO and ZnO (CuO : ZnO = 1 : 2, 1 : 1, and 2 : 1) were formed. The crystalline characteristics and electrical and magnetic properties depended primarily on the mixing effect and oxygenation. The electrical resistance of C0.5Z0.5O (1.5×105Ω/□) powder was lower than that of CuO (5.82×105Ω/□) powder after ZnO mixing in CuO. This reduction was attributed to the substitution of Cu+ ions at Zn2+ sites or the formation of electron trapping defect centers. The concentration ratio of Cu2O phase in CuxZn1−xO powder mainly dominated the electrical resistance. The CuxZn1−xO has a diluted ferromagnetism (DFM) and paramagnetism (PM). The electrical resistance of CuxZn1−xO decreased; the magnetic behavior increased instead. This study also analyzes the chemical binding of Cu0.5Zn0.5O powders to confirm the contribution of Cu+ ions to the electrical and magnetic properties.


---

## Body

## 1. Introduction

Metal oxide nanostructures, such as ZnO [1], CuO [2, 3], SnO2 [4], In2O3 [5], and TiO2 [6], have attracted extensive attention for their optical, electrical and magnetic properties. They are widely applied in various optoelectronic devices, such as photocatalyzers [7], solar cells [8], photodiodes [9], and humidity sensors [10].Recent reports on CuO-ZnO compound and CuO/ZnO heterojunction structures show the need for efficient characteristics [11, 12].  A few Cu dopants (<10 at.%) doped ZnO samples have been investigated [13, 14]. However, the effects of the higher Cu doping contents (>10 at.%) on electrical properties and magnetic behavior of ZnO were rarely reported. Thus, the electrical properties that dominate devices performance and the influences of higher dopant level on the electrical resistance of CuxZn1-xO are topics worthy of further research. In addition, ZnO-diluted magnetic semiconductor (DMS) can enhance its magnetic behavior by Cu doping [15]. The influences of high CuO concentration on magnetic properties of ZnO are not clear.The study uses an aqueous solution method to synthesize CuO andCuxZn1-xO powders. Specifically, this study examines the effects of high ZnO content mixed with CuO on the structural, electrical, and magnetic properties of CuxZn1-xO powders. The relation of electrical resistance and magnetic properties for CuxZn1-xO powders was carried out to understand the influences of CuO mixing effects and clarify the contribution of CuO and Cu2O phase.


## 2.  Experimental Procedures

The experiments in this study synthesized the CuO powder using an aqueous solution. To acquire the CuO powder, 0.25 M copper acetate [Cu(CH3COO)2] was synthesized in deionized water. The precursor solution was uniformly stirred at 80°C for 1 h and then dried at 120°C in an oven to evaporate the solvent. The resulting powder was then analyzed by a differential scanning calorimeter (DSC) and a thermogravimetric analyzer (TGA) to determine the thermal properties of fabricated CuO nanoparticles. The DSC and TGA results indicate that CuO powder could be obtained after thermal annealing in a furnace for 1 h. For CuxZn1-xO powders, the copper acetate and the zinc acetate were mixed with different ratios (CuO : ZnO = 1 : 2, 1 : 1 and 2 : 1) and the molar ratio of zinc acetate to citric acid (C6H8O7) was 2. The CuxZn1-xO powders were then designed according to the concentration ratio of CuO and ZnO as Cu0.3Zn0.67O, Cu0.5Zn0.5O, and Cu0.67Zn0.3O.This study investigates the structural characteristics of powders using X-ray diffraction (XRD, Siemens/D5000) and scanning electron microscopy (SEM, Hitachi/S-4100). To understand the contribution of CuO on the electrical and magnetic characteristics ofCuxZn1-xO powders, a semiconductor parameter analyzer (Agilent/4155-B) and superconducting quantum interference device vibrating sample magnetometer (SQUID VSM) were used, respectively. The composition and chemical bonding of the crystallization were analyzed using an electron spectroscopy for chemical analysis (ESCA, PHI 5000 VersaProbe).


## 3. Results and Discussions

This study uses DSC and TGA analysis to determine the crystallization conditions of CuO precursors (Figure1). The specimens were heated from room temperature to 1000°C at a rate of 10°C/min in air. The TGA data reveals a sharp weight loss in the powder at 270°C because of the evaporation of water and organics [16]. This result is consistent with the DSC curve, which shows an exothermic peak at 280°C. An endothermic peak appears at 480°C and the powder weight (TGA curve) gradually increases and then stabilizes as the temperature exceeds 500°C. The main reason is that the CuO crystallization gradually forms with increasing temperature [17]. Based on these reasons, the CuO powder was annealed at 500°C to estimate the CuO crystallization.Figure 1
DSC-TGA curve of CuO.Figure2(a) shows the XRD patterns of as-grown CuO precursors and CuO powder annealed at 500°C for 1 h. Both samples were polycrystalline and had a monoclinic structure. An additional diffraction peak of (CH3COO)2· Cu appeared in as-grown CuO precursors, indicating that a drying temperature of 120°C was insufficient for its evaporation. After thermal annealing at 500°C, the Cu(CH3COO)2 phase disappeared and the (111) diffraction peak dominated the CuO crystallization. The intensity of the major diffraction peaks increased, indicating that the sufficient thermal energy improved CuO crystallization. Based on the Scherrer formula [16], the grain size of CuO nanoparticles can be estimated from the full width at half-maximum (FWHM) of the (111) diffraction peak. The average grain size of CuO powder increased from 8 nm to 21 nm after thermal annealing at 500°C. This result is associated with the grains growing more easily under the higher temperature [16]. The ZnO powder was also synthesized and compared to CuxZn1-xO powder. XRD analysis of CuxZn1-xO (x=0, 0.33, 0.5, 0.67, and 1) powders were conducted to analyze the effects of ZnO on CuxZn1-xO crystallization (Figure 2(b)). A small amount of ZnO mixing with CuO (CuxZn1-xO, x=0.67), the monoclinic structure of CuO dominated the Cu0.67Zn0.33O crystallization, and ZnO phases existed in the Cu0.67Zn0.33O matrix. With increasing the ZnO concentration in CuxZn1-xO (x value increase from 0.67 to 0.33), the (101) diffraction peak of ZnO was the preferred orientation which indicated that the ZnO phases dominated the CuxZn1-xO crystallization. A comparison of the CuO revealed that the diffraction peak of (111) for Cu0.33Zn0.67O shifted to higher degree. In contrast, the diffraction peak of (101) for Cu0.33Zn0.67O shifted to lower degree comparing with ZnO. These results are associated with compressive strain in the crystallization [4]. In addition, the related (220) diffraction peak of the Cu2O phase was attributed to insufficient oxidation [2]. Notably, the (200) diffraction peak of Cu2O phase did not appear in Cu0.5Zn0.5O crystallization, indicating that the compositional ratio of Cu2O phase was less than other CuxZn1-xO (x = 0.33 and 0.67) powders. This result should affect the electrical properties of CuxZn1-xO powders.XRD patterns of (a) as-grown CuO powder and CuO powder with annealed temperature of 500°C. (b)CuxZn1-xO (x = 0, 0.33, 0.5, 0.67, and 1) powders.
(a)
(b)Figure3 shows SEM images of CuxZn1-xO (x = 0.33, 0.5, and 0.67) powders at an annealing temperature of 500°C. All powders displayed a particle-like structure, and the agglomeration of particles was randomly distributed. The morphology of Cu0.5Zn0.5O powder shows an irregular and its size for the agglomeration of particles is larger than that of Cu0.67Zn0.33O and Cu0.33Zn0.67O powders. The electrical properties of powder might be influenced by the particle size [18], therefore, the electrical resistance were examined.Morphology ofCuxZn1-xO powders: (a) Cu0.33Zn0.67O,  (b) Cu0.5Zn0.5O, and (c) Cu0.67Zn0.33O.
(a)
(b)
(c)Electrical measurements were conducted to determine the resistance value of CuO powder. The CuO powder was pressed to form ingots (Φ 10 mm/~2 mm thick) at a pressure of 30 kg/cm2 for 30 s before measuring their resistivity (Table 1). After annealing at 500°C, the resistivity of the CuO sample decreased from 8.6×1011 Ω/□ to 2.3×106 Ω/□. After CuO mixing with ZnO, the electrical resistance of the Cu0.67Zn0.33O and Cu0.33Zn0.67O samples was higher than that of CuO. This increment of the electrical resistance may be attributed to the substitution of Cu+ ions at Zn2+ sites or the formation of electron trapping defect centers [19]. It is noted that the electrical resistance of Cu0.5Zn0.5O sample (1.5 × 105 Ω/□) decreased instead comparing with CuO sample. This result indicates that the ratio of the CuO phase to Cu2O phase in CuxZn1-xO system decreased [20] and possessed a stable crystallization comparing with Cu0.67Zn0.33O and Cu0.33Zn0.67O samples.Table 1
The relation of electrical resistances and magnetic properties forCuxZn1-xO (x=0, 0.33, 0.5, 0.67, and 1) powders with different CuO/ZnO ratios.
Sample
Resistivity (Ω/□)
Magnetism
Cu
x
Zn
1
-
x
O
Before annealing
x
=
1
8.6 × 1011
—
2.3 × 106
AFM
Annealed at 500°C
x
=
0.67
1.0 × 107
DFM + PM
x
=
0.5
1.5 × 105
DFM + PM
x
=
0.33
8.2 × 108
DFM + PM
x
=
0
9.0 × 108
DMTo understand the contribution of CuO on the magnetic properties, theCuxZn1-xO powders with different ratios of CuO and ZnO were measured. Figure 4 shows the magnetization (M) as a function of magnetic field (H) at the temperature of 10 K for the CuxZn1-xO powders. All samples have a linear-like M-H variation at a magnetic field of ±5000 Oe without measureable hysteresis, which indicates a paramagnetic behavior [21]. The magnetization of Cu0.33Zn0.67O sample was higher than that of Cu0.5Zn0.5O and Cu0.67Zn0.33O samples, which indicated that the Cu0.33Zn0.67O powder contains a better paramagnetism (PM). The increment of antiferromagnetic interaction possibly reduced the PM that resulted from the formation of CuO crystallization [21]. From XRD data (Figure 2(b)), the CuO phase dominated the Cu0.5Zn0.5O, Cu0.67Zn0.33O crystallization and affected their magnetic properties that were consistent with the result of M-H curves. In addition, the lower magnetization of Cu0.5Zn0.5O, Cu0.67Zn0.33O was also attributed to the secondary phase of Cu2O [22]. The low-field region of the hysteresis loops of CuxZn1-xO powders was clearly observed (inset of Figure 4) which indicated that all CuxZn1-xO powders also contained a diluted ferromagnetism (DFM). The FM could be developed by the distortion of ZnO structure by the substitution of remnant Cu2+ ions into ZnO lattice [22, 23]. It is found that the coercivity field of the Cu0.33Zn0.67O, Cu0.5Zn0.5O, and Cu0.67Zn0.33O powders is 75 Oe, 150 Oe, and 78 Oe, respectively. That is to say, the Cu0.5Zn0.5O powder has a good stability for thermal interference [24].Figure 4
Magnetic field dependence of magnetization (M-H) for CuxZn1-xO powders at 10 K. The inset shows the hysteresis loops for lower regions (±500 Oe).The chemical bonding of the Cu0.5Zn0.5O powder was examined by XPS with full region scanning from 0 eV to 1200 eV (Figure 5). In Figure 5(a), all peaks from oxygen, copper, zinc, and a trace of carbon are apparent, meaning that the Cu0.5Zn0.5O powder is substantially covered by Cu2+, Zn2+, and O−2. The high-resolution scanning information provided in Figures 5(b)–5(d) is for the separate analysis of elements: O, Cu, and Zn, respectively. The high-resolution XPS spectrum of the O1s signal (Figure 5(b)) indicates that the binding energy of 530.3 eV can be attributed to oxidized ions in the CuO particles [25]. Multipeak Gaussian fitting shows another O1s peak located at 532.4 eV, indicating that this binding energy was dominated by Zn2+ ion doping [23]. The high-resolution XPS spectrum of the Cu2p3/2 mode (Figure 5(c)) appears at 932.3 eV, indicating the presence of Cu2+ ion [2]. The binding energy of 952.3 eV (Cu2p1/2 mode) can be attributed to Cu+ ions in Cu0.5Zn0.5O that resulted from Cu2O [26, 27]. This result is consistent with the observation of XRD data (Figure 3(b)). Figure 5(d) shows two strong peaks at 1021.5 eV and 1044.7 eV which correspond to Zn2p3/2 and Zn2p1/2, respectively. This is consistent with the Zn2+ ion binding in previous reports [28]. Based on these results, the Zn2+ ions were substituted by Cu+ to form the Cu2O phase that affects the electrical and magnetic properties.XPS spectra of Cu0.5Zn0.5O powder: (a) XPS spectrum of Cu0.5Zn0.5O powder fully scanned from 300 eV to 1200 eV, (b) high-resolution selective spectrum of O, (c) high-resolution selective spectrum of Cu, and (d) high-resolution selective spectrum of Zn.
(a)
(b)
(c)
(d)The correlation of the magnetic properties and resistivity ofCuxZn1-xO powders were summarized in Table 1. The magnetic property of pure CuO powder varied from antiferromagnetism (AFM) to paramagnetism (PM) when ZnO to CuO. The resistivity of CuxZn1-xO powders decreased; the values of the paramagnetic behavior decreased. These results indicate that the paramagnetic behavior in Cu0.33Zn0.67O powder is the highest. The lower carrier concentration may promote paramagnetic ordering in Cu0.33Zn0.67O [29].


## 4. Conclusions

The stability of oxide (CuO or Cu2O) depends primarily on the intensity of oxidation (annealing temperature). When ZnO participated in the CuO system, the crystalline quality of CuO powder deteriorated. The ZnO mixing effect increased the crystallization size and induced a compressive stress in the particle. Although the presence of ZnO phases deteriorated Cu0.5Zn0.5O crystallization, the electrical conductance was improved. A lower Cu2O phase concentration and stable crystallization reduced the electrical resistance of Cu0.5Zn0.5O powder. The electrical resistance of Cu0.5Zn0.5O powder was the lowest and the magnetic behavior was the smallest because CuO and Cu2O contents were higher. XPS analysis reveals that the Zn2+ ions were substituted by Cu2+ and Cu+ ions, forming CuO and Cu2O phases that confirmed the contribution of Cu2O on the electrical and magnetic properties.



---

*Source: 405043-2013-02-24.xml*