# Controlled Aspect Ratios of Gold Nanorods in Reduction-Limited Conditions

Authors: Jong-Yeob Kim; Chil Seong Ah; Du-Jeon Jang
Journal: Journal of Nanomaterials
 (2011)

---

## Abstract

Aspect ratios of gold nanorods have been finely modified in reduction-limited conditions via two electrochemical ways: by changing the amount of a growth solution containing small gold clusters in the presence of already prepared gold nanorods as seeds or by changing electrolysis time in the presence or absence of a silver plate. While the atomic molar ratio of gold in the growth solution to gold in the seed solution is critical in the former method, the relative molar ratio of gold ions to silver ions in the electrolytic solution is important in the latter way for the control of the aspect ratios of gold nanorods. The aspect ratios of gold nanorods decrease with an increase of electrolysis time in the absence of a silver plate, but they increase with an increase of electrolysis time in the presence of a silver plate.


---

## Body

## 1. Introduction

The design and controlled fabrication of nanostructured materials with functional properties have been extensively investigated to attract a great deal of attention [1–7]. A great number of inventive techniques involving chemical, electrical, and optical processes have been employed to synthesize monodispersive and anisotropic materials of nanorods (NRs), nanowires, and nanobelts [8–12]. In particular, one-dimensional gold nanostructures have been extensively studied due to their potential in a variety of applications such as biosensing, molecular imaging, and photothermal therapy [13–17]. Gold NRs with diverse aspect ratios have drawn considerable attention because of their optical properties, exhibiting intense longitudinal and transverse plasmon bands in the visible region [18–23].The synthesis of aspect ratio-controlled gold NRs is important because it leads us to explore their properties and to find their applications in sensing and imaging nanoscience. Several approaches such as seeding [22–24], ultrasonic [25], photochemical [20, 26, 27], and electrochemical methods [28–36] have been carried out to control the aspect ratios of gold NRs. We also note that bioreduction techniques [37, 38] have been applied to study faceting and surface reconstruction on gold. The electrochemical synthesis of gold NRs has been proven to have some additional advantages over chemical methods although the growth mechanism of gold NRs during the electrochemical synthesis remains elusive [20]. The aspect ratios of gold NRs have been controlled generally by changing the gold atomic concentration ratio of the growth solution to the seed solution or by varying the amount of silver ions [18–23, 32–35]. The use of silver ions to assist the growth of gold NRs is common in a seed-mediated approach. It has been noted that the addition of a small amount of silver ions is critical for the formation of gold NRs instead of spherical gold nanoparticles [20, 23, 32–35]. However, the roles of silver ions in the determination of the aspect ratios of gold NRs have not been fully understood yet regardless of many reports [18, 23].In this paper, we report that the aspect ratio modification of gold NRs can be approached in two electrochemical ways: by changing the amounts of growth solutions or by changing electrolysis time in the presence or absence of a silver plate. While the gold atomic molar ratio of the growth solution to the seed solution is critical in the former method, the relative atomic molar ratio of gold to silver is found to be important in the latter way to control the aspect ratios of gold NRs.


## 2. Materials and Methods

The synthesis of a seed solution was conducted using a simple electrochemical cell [28]. A gold plate (3 × 1 × 0.05 cm3) and a platinum plate (3 × 1 × 0.05 cm3) were used as the anode and the cathode, respectively. Spacing between the anode plate and the cathode plate was kept at 0.25 cm. Both electrodes were immersed in 6 mL of an electrolytic solution containing 80 mM hexadecyltrimethylammonium bromide (CTAB) as a hydrophilic cationic surfactant and 8.0 mM tetraoctylammonium bromide as a hydrophobic cationic cosurfactant [18, 28]. Immediately prior to electrolysis, 0.13 mL of acetone and 0.09 mL of cyclohexane were added into the electrolytic solution. While current was typically set at 5 mA, temperature was maintained roughly at 38°C throughout electrolysis. A silver metal plate (3 × 1 × 0.05 cm3) was immersed into the electrolytic solution. 6 mL of an aqueous solution containing gold clusters (<1 nm in diameter) was prepared for a growth solution using the above-mentioned electrochemical method. The color of the solution was pale blue when the electrolysis was over. Gold clusters of the growth solution were too small for their sizes to be measured using transmission electron microscopy (TEM). Growth solutions were used within 5 min after being prepared to prevent spontaneous nucleation into gold NRs. Aspect ratios of gold NRs were controlled by adding various amounts of gold cluster solutions as growth solutions to fixed amounts (0.1 mL) of gold NR solutions as seed solutions to make the gold atomic molar ratios (w0) of growth solutions to seed solutions be 0, 1.5, 1.75, 2, and 3. To modify the aspect ratios of gold NRs by changing electrolysis time, a silver plate was inserted in the electrolytic solution of the above mentioned simple electrochemical cell having a gold plate as the anode and a platinum plate as the cathode. Firstly, we applied electric current for 10 min to the electrolytic solutions having a silver plate. Secondly, in one experiment, the silver plate was removed from the electrolytic solution, and then electric current was additionally applied for 5, 10, or 15 min with a typical current setting of 5 mA. In the other experiment, electrolysis was continuously operated with the silver plate for up to 25 min. A comparative study with and without a silver plate was carried out to understand the effect of silver ions on the surface-plasmon resonances and the aspect ratios of gold NRs.The absorption spectra of the aqueous colloidal solutions of gold NRs contained in quartz cells having a path length of 2 mm were taken using a UV/vis spectrophotometer (Scinco, UVS2040). A drop of a gold colloidal solution was placed on a carbon-coated copper grid for the TEM measurement using a microscope (JEOL, JEM2000).


## 3. Results and Discussion

Figure1 shows the absorption spectra of gold NRs prepared at different w0 values. The absorption spectrum of gold NRs prepared in the absence of the growth solution has the longitudinal plasmon maximum at 748 nm (Figure  1(a)). As the w0 value increased gradually from 0 to 3, the wavelength at the absorption maximum of the longitudinal plasmon mode (λL) shifts to the blue continuously and largely. Table 1 indicates that λL at w0=3 is shorter by 95 nm than λL at w0=0. However, the wavelength at the absorption maximum of the transverse plasmon mode (λT) shifts gradually and very slightly to the red with an increase of the w0 value. The extreme shift of λL to the blue and the slight shift of λT to the red indicate that the aspect ratios of gold NRs decrease extensively and continuously with an increase of w0 value. Thus, this suggests that we can control the aspect ratios of gold NRs by adjusting the w0 value.Table 1
Wavelengths at longitudinal absorption peaks (λL), average lengths (l), average diameters (d), and average aspect ratios (AR) for the gold NRs of the samples described in Figures 1 and 2.
Figuresw0aλL (nm)l (nm)d (nm)ARFigures1(a) and 2(a)0.0074836.610.43.6Figures1(b) and 2(b)1.5071436.411.73.2Figures1(c) and 2(c)1.7569937.912.93.0Figures1(d) and 2(d)2.0068737.813.22.9Figures1(e) and 2(e)3.0065336.914.82.5aGold atomic molar ratio of the growth solution to the seed solution.Figure 1
Absorption spectra for gold NR solutions prepared by being set aside for 2 days at variousw0 values of 0 (a), 1.5 (b), 1.75 (c), 2 (d), and 3 (e).The TEM images of Figure2 clearly show that the mean diameter of gold NRs increased continuously with an increase of the w0 value. However, the mean length of gold NRs remained almost invariant regardless of the variation of the w0 value. These imply that the aspect ratios of gold NRs decreased as the w0 value increased (Table 1). From these observations it can be inferred that the gold seeds were grown more easily on the side of gold NRs than on the ends of gold NRs. It is known that the rarely observed {110} facets of gold NRs has higher energy than the {111} and {100} facets of gold NRs do [30, 33, 39–42]. In previous other seeding methods, which employed small nanoparticles as seeds, the aspect ratios of gold NRs were reported to increase with an increase of the w0 value because the growth of gold NRs was assisted by the aqueous micellar template of CTAB [18, 22, 24]. However, if gold NRs were used as seeds, the diameters grew faster than the lengths did. As the w0 value increased from 0 to 2, the average length of gold NRs increased only 3.3% whereas the average diameter of gold NRs increased by 27% (Table 1). So the use of already prepared gold NRs as seeds is considered to be important for the fine modification of the aspect ratios of gold NRs.TEM images of gold NRs prepared by being set aside for 2 days at variousw0 values of 0 (a), 1.5 (b), 1.75 (c), 2 (d), and 3 (e). Each scale bar indicates 25 nm.
(a)(b)(c)(d)(e)On one hand, Figure3(a) shows that the wavelength at the longitudinal absorption maximum of gold NRs dispersed in water decreased linearly with an increase of the w0 value. This implies that the optical properties of gold NRs can be tuned finely to cover a wide spectral range of 748–653 nm by adjusting the w0 value, as described with Figure 1. On the other hand, Figure 3(b) reveals that the average aspect ratio of gold NRs decreased linearly from 3.6 to 2.5 as the w0 value increased from 0 to 3. As discussed with Figure 2, this suggests that the aspect ratios of gold NRs can be modified finely by adjusting the w0 value.λL (a) and AR (b) of gold NRs versus w0 for the samples described in Figures 1 and 2.
(a)(b)To modify the aspect ratios of gold NRs by changing electrolysis time, a silver plate was inserted to a simple electrochemical cell having a gold plate as the anode and a platinum plate as the cathode. Figure4(a) shows the absorption spectrum of gold NRs prepared by applying the electric current to the electrolytic solution for 10 min in the presence of a silver plate. Then, the silver plate was removed from the electrolytic solution, and the electric current was applied additionally to the electrolytic solution for 5 (Figure  4(b)), 10 (Figure  4(c)), or 15 min (Figure  4(d)). Table 2 indicates that λL at 5 min was shifted largely (by 66 nm) to the long wavelength compared with λL at 0 min. However, λL at 10 min and λL at 15 min were shifted gradually to the short wavelength compared with λL at 0 min. Table 2 indicates that λL at 10 min and λL at 15 min were shifted to the blue by 19 nm and 44 nm, respectively, compared with λL at 0 min. Thus, this suggests that we can control the aspect ratios of gold NRs by adjusting electrolysis time after removing the silver plate. In contrary to the obvious shift of λL, λT was relatively unchanged to be present at 520 nm.Table 2
Wavelengths at longitudinal absorption peaks (λL), average lengths (l), average diameters (d), and average aspect ratios (AR) for the gold NRs of the samples described in Figures 4 and 5.
FiguresTime (min)aλL (nm)l (nm)d (nm)ARFigures4(a) and 5(a)067436.713.72.7Figures4(b) and 5(b)574061.718.93.3Figures4(c) and 5(c)1065558.924.52.4Figures4(d) and 5(d)1563050.123.92.1aAdditional electrolysis period after removing the silver plate.Figure 4
Absorption spectra of aqueous gold NR solutions, electrolyzed at 5 mA for 10 min with a silver plate and then for 0 min (a), 5 min (b), 10 min (c), and 15 min (d) additionally after removing the silver plate.The TEM images of gold NRs in Figure5 support the phenomena observed with the absorption spectra of Figure 4. When the electric current was applied additionally for 5 min after removing the silver plate, aspect ratios as well as diameters and lengths increased, indicating that gold NRs were still growing. However, when the electric current was applied additionally for 10 min and 15 min after removing the silver plate, the aspect ratios of gold NRs decreased although both of the lengths and the diameters increased apparently compared with the respective ones at 0 min. These suggest that the aspect ratios of gold NRs can be regulated by adjusting the amount of silver ions present in the reaction system. This indicates that the average aspect ratio of gold NRs increased in the beginning and then decreased when the electric current was applied in the absence of a silver plate. It is known that the aspect ratios of gold NRs increase with the concentration increase of silver ions [20, 23, 32, 33]. The aspect ratios of gold NRs increased for 5 min and then decreased for further electrolysis time in the absence of a silver plate (Table 2). The mean aspect ratio of gold NRs increased for 5 min because silver deposition on the {110} facets took place to inhibit growth on the sides of gold NRs. Thus, gold grew on the low-energy {100} facets to elongate gold NRs for the early time after removing the silver plate. However, the average aspect ratio of gold NRs decreased for further electrolysis time in the absence of a silver plate because silver deposition occurred no longer to inhibit gold deposition on the high-energy {110} facets.TEM images of modified gold NRs, electrolyzed at 5 mA for 10 min with a silver plate and then for 0 min (a), 5 min (b), 10 min (c), and 15 min (d) additionally after removing the silver plate. Each scale bar indicates 25 nm.
(a)(b)(c)(d)The visible absorption spectra of aqueous gold NR solutions in Figure6 reveal that the aspect ratios of gold NRs can be controlled finely by adjusting electrolysis time in the presence of a silver plate. When the molar ratio of gold ions to silver ions remained invariant during the electrolysis, both λL and AR increased largely and monotonically with electrolysis time (Figure 6 and Table 3). λL at 25 min is larger by 149 nm than λL at 10 min while AR at 25 min is greater by 1.8 than AR at 10 min. Together with Figure 4, Figure 6 indicates that the presence of silver ions in the electrolytic solution is critically vital for the elongation of gold NRs. It has been reported [32] that the aspect ratios of gold NRs increase with the total area of an immersed silver plate. Thus, the amount and the release speed of silver ions can be adjusted to control the aspect ratios of gold NRs finely. It would be fundamentally important to explore how the presence or absence of a silver plate could control the aspect ratios of gold NRs in our process. The report on silver underpotential deposition (UPD) on growing gold nanoparticles by Guyot-Sionnest has provided some useful insight into the role of silver ions and a possible rationale for excess silver ions in a solution [40–42]. Gold NRs grown using CTAB-protected gold seeds in the presence of Ag+ ions were reported [32–35] to bear {110} facets on the sides of gold NRs and {100} facets on the ends of gold NRs. Silver UPD is the reduction of Ag+ to Ag0 at a metal substrate with a surface potential less than the standard reduction potential of Ag+. A great positive shift in potential for silver UPD on gold surfaces was observed on {110} surfaces compared to the {100} or {111} facets [40–42]. The deposition of silver on the sides of gold NRs becomes faster than that on the ends of gold NRs [33, 40–42]. Fast silver deposition followed by strong CTAB binding inhibits growth on the sides of gold NRs and leads to preferential growth at the ends of gold NRs. Presenting the crystalline structure of gold NRs, two recent papers [43, 44] have provided new insights in the growth mechanisms of gold NRs having a wide range of morphologies on the nanoscale.Table 3
Wavelengths at longitudinal absorption peaks (λL) and average aspect ratios (AR) for the gold NRs of the samples described in Figure 6.
FigureTime (min)aλL (nm)ARFigure6(a)106742.7Figure6(b)157453.4Figure6(c)207834.0Figure6(d)258234.5aElectrolysis time in the presence of a silver plate.Figure 6
Absorption spectra of aqueous gold NR colloidal solutions electrolyzed at 5 mA with a silver plate for 10 min (a), 15 min (b), 20 min (c), and 25 min (d).


## 4. Conclusion

The aspect ratios of gold NRs have been controlled in two electrochemical ways. Firstly, they have been finely modified by changing the amount of a growth solution containing small gold clusters in the presence of already prepared gold NRs as seeds. Secondly, they could be controlled well by adjusting electrolysis time in the presence or absence of a silver plate. While the gold concentration ratio of the growth solution to the seed solution was critical in the former method for the control of the aspect ratios of gold NRs, the relative molar ratio of gold ions to silver ions was important in the latter way. The aspect ratios of gold nanorods decreased with an increase of electrolysis time in the absence of a silver plate, but they increased with an increase of electrolysis time in the presence of a silver plate. This indicates that the presence of silver ions in the electrolytic solution is critically vital for the elongation of gold NRs.



---