# Characterization of Solid Oxide Fuel Cells with LSCF-SDC Composite Cathodes

Authors: Gianfranco DiGiuseppe; Venkatesh Boddapati
Journal: Journal of Energy
 (2018)

---

## Abstract

This paper reports the study of an anode-supported SOFC cell containing an LSCF-SDC composite cathode. The SOFC cell was tested at different temperatures and reactant flow rates. After testing, the cell was sectioned and characterized using SEM/EDS. Such analysis indicated that no structural damage and no significant interdiffusion of elements among the layers occurred. The measured electrochemical performance data at different temperatures indicate an Arrhenius behavior or temperature activated processes. The low-porosity anode functional layer appears to be very sensitive to low hydrogen contents. The electrochemical performance is also affected by changing air flow rates.


---

## Body

## 1. Introduction

Solid oxide fuel cells (SOFCs) are electrochemical devices that convert directly the chemical energy of a fuel without the combustion step. It is common knowledge that they are highly efficient, fuel flexible, and modular and have cogeneration capabilities [1–4]. Significant progress in this technology has occurred over the years, including commercialization efforts; however, improvements are still possible. For instance, the oxygen electrode or cathode still limits the performance capabilities of SOFCs especially at lower temperatures [5, 6]. One approach to improve the cathode performance is to use functional layers to improve the oxygen reduction reaction kinetics and mass transfer [7, 8]. A different approach is the use of composite cathodes where an electrolyte phase is mixed with the cathode material [9, 10]. Others have used infiltration techniques to again enhance the oxygen reduction reaction kinetics in the cathode [11, 12]. Regardless of the approach used, chemical compatibility and long-term performance need to be better understood to ensure that SOFC systems can compete with existing technologies. In this work, we report the material and electrochemical characterization of LSCF-SDC composite cathode tested at different temperatures, hydrogen flow rates, and air flow rates. The effects of these parameters on the cell performance are discussed in detail as well as the postmortem characterization of the tested cell.


## 2. Experimental

Commercial anode-supported bilayers were purchased with a diameter of about 25.4 mm. They consist of a highly porous Ni-YSZ bulk support anode where a thin layer of lower porosity acts as a functional layer. A dense YSZ layer acts as the electrolyte. A commercial SDC ink is screen-printed onto the electrolyte and fired at 1240°C for 2 hours. The SDC layer acts as a barrier layer between YSZ and LSCF cathodes to prevent unwanted chemical reactions. A mixture of LSCF-SDC is subsequently screen-printed and fired at 1110°C for 1 hour. Current collectors were applied on both sides with an ink and fired at 850°C for 1 hour. The cell active area is measured to be 2.5 cm2.The SOFC cell was tested in the test rig shown in Figure1. The temperature was varied between 500 and 750°C and closely monitored by placing a thermocouple near the cell. On the anode side, humidified hydrogen was used at room temperature with a flow rate ranging from 0.05 to 1.0 SLPM. At room temperature, the water content is around 3% [1]. On the cathode side, air was used as an oxidant with a flow rate ranging from 0.1 to 1.0 SLPM. Voltage-current density curves as well as impedance measurements were made using a PARSTAT 2273 apparatus coupled with a power booster obtained from AMETEK Princeton Applied Research. Voltage-current density curves were obtained at a scan rate of 3 mV/s between open-circuit voltage down to 0.3 V. Impedance data were obtained at open-circuit voltage. The frequency range was between 0.01 Hz and 1 MHz with AC amplitude of 10 mV and 12 datum points per frequency decade. An analytical Quanta 200 s Environmental Scanning Electron Microscope produced by the Phillips Electron Optics company was used for the postmortem characterization for the high-magnification picture and chemical maps.Figure 1
Schematics of the button cell testing setup used for this work.


## 3. Results and Discussion

Figure2 reports SEM pictures of the SOFC cell after the completion of all testing. The anode support layer is very porous with a thin, less porous, functional layer with a thickness of around 8 micrometers. The highly dense YSZ layer is also around 8 micrometers thick. The SDC layer is around 4 micrometers and is somewhat a dense layer. The LSCF-SDC composite cathode is highly porous and is around 20 micrometers in thickness. The SEM images show that the cell is intact and well preserved as no discernible damage or delamination of layers can be observed.Figure 2
SEM cross section images of the tested SOFC cell.In addition to the cell structural integrity, interdiffusion of elements among all layers needs to be avoided. EDS was performed on the cross section shown in Figure2 to obtain chemical maps. Figure 3 illustrates the chemical elements that comprise the cathode, namely, La, Sr, Co, and Fe. La is uniformly distributed in the cathode, and the sharp line near the SDC layer would indicate negligible diffusion into the barrier layer. La is one of the most abundant elements in the cathode, Fe being the other one. The SEM was not able to detect Sr in meaningful quantities. This was mostly because X-ray lines overlap between Sr and Y. In addition, the amount of Sr in the cathode is not very large and, in general, SEM machines do not have a very high resolution. Co is also present in small amounts, and it is reasonably well distributed within the cathode. Again, within the SEM resolution, Co did not move into the barrier layer either. Lastly, Fe is uniformly distributed in the cathode; however, small amounts are present in the SDC layer. Iron is used as a sintering aid to obtain dense ceria layers, and some commercial suppliers will add small amounts of iron oxide in the SDC ink [13]. Because of this, it is hard to distinguish if iron has migrated from the cathode to the SDC layer as some of it is already there.Figure 3
EDS chemical maps for La, Sr, Co, and Fe elements.Figure4 shows the chemical maps for Sm and Ce. Both elements are uniformly distributed within the SDC layer, and as expected it extends uniformly into the composite cathode. Neither element has migrated into the YSZ electrolyte as sharp edges can be clearly observed. Noticeable is some background noise in the Sm map, but none is observed with the Ce map. Figure 5 reports the chemical maps for Y, Zr, and Ni. Y and Zr are uniformly observed in the electrolyte layer. The sharp edge near the SDC layer indicates no interdiffusion with the barrier layer. Y and Zr are, however, not uniformly distributed in the anode. The anode functional contains more Y and Zr than the bulk anode in order to increase the three-phase boundary, thereby increasing the electrochemical reactions in the fuel side [14]. Ni is uniformly distributed in bulk anode in order to increase electrical conductivity, but less Ni is present in the anode functional layer where a mixed conductivity is desired [15].Figure 4
EDS chemical maps for Sm and Ce elements.Figure 5
EDS chemical maps for Y, Zr, and Ni elements.Interdiffusion between SDC and YSZ layer has been recently reported for SOFC cells fired at 1400°C and occurs at firing temperatures above 1200°C [16]. Similar behavior has been reported for a ceria barrier layer doped with gadolinium as well [17]. For SDC/YSZ bilayers where the SDC layer is deposited, using a Pulsed Laser Deposition technique avoids the high temperature firing step, and the interdiffusion between the two layers has not been observed [18]. Additional studies report that the dissolution of Sm into the YSZ phase can also result in decreased ionic conductivity in the electrolyte [19, 20]. The reason that interdiffusion between SDC and YSZ layer is not observed in the tested cell is likely due to the low firing temperature of the SDC layer (1240°C). Though interdiffusion may have not been completely prevented, the effects are very small and cannot be detected using conventional SEM/EDS techniques.Figure6 presents the voltage-current density characteristics of the tested cell measured from 500 to 750°C at 50°C intervals. The cell power density increases with temperature and reaches a maximum of about 1.2 W/cm2. The cell open-circuit voltage at 750°C is around 1.1 V which is slightly lower than the Nernst voltage of 1.110 V at the same temperature [15]. This slight difference is due to minor leakages through the seal in the setup. As it can be seen, the cell performance at 750°C is quite good but becomes irrelevant as the temperature reaches 500°C. At high current densities, the voltage does not drop rapidly which suggests that diffusion losses are not very large at all temperatures.Figure 6
Voltage and power density curves versus current density at different temperatures.Impedance data at OCV were collected at the same temperatures, and the Nyquist plots are shown in Figure7. The data show that the performance decline is mostly due to electrode polarization because the low frequency intercept becomes larger and larger as temperature decreases. In other words, the cathode electrochemical activity or capability is severely diminished with lowering temperatures. The ohmic portion of the cell can be found from the high frequency intercept. The ohmic contribution to the lowered cell performance is smaller than the electrode polarization; however, a significant increase in ohmic resistance is still present. See inset in Figure 7. To further demonstrate the above, Table 1 reports the ohmic resistance and total electrodes polarization estimated from the impedance data shown in Figure 7. At each temperature, the percentage ohmic contribution to the total resistance is much smaller. Also noticeable is that both resistances are temperature activated processes, and they follow an Arrhenius behavior. This is shown in Figure 8 where the logarithm of both resistances is plotted against the inverse of temperature. The observed linear behavior of the data confirms the Arrhenius behavior.Table 1
Ohmic resistance and electrodes polarization estimated from the impedance data shown in Figure7.
T (°C) Ohmic Resistance (ohm cm2) Electrodes Polarization (ohm cm2) Percent Ohmic Percent Polarization 500 1.5 17 8% 92% 550 1.0 6.5 13% 87% 600 0.6 3.1 16% 84% 650 0.4 1.9 17% 83% 700 0.2 1.2 14% 86% 750 0.1 0.8 11% 89%Figure 7
Impedance curves at different temperatures.Figure 8
Logarithm of resistances as a function of the inverse temperature.To further characterize the cell performance, the hydrogen flow rate was varied from 0.05 to 1.0 standard liters per minute at 750°C. The voltage-current density characteristics are shown in Figure9. The cell performance is not affected at large flow rates or between 1 and 0.5 SLPM. At 0.25 SLPM, the cell performance starts to be affected at high current densities. Some small data oscillation is also observed for this set of data. Further decrease in the hydrogen flow rate affects the performance sooner and sooner (or at lower current densities). The data oscillation also becomes more evident and significant. To the authors’ knowledge, this behavior has not been reported in the literature. However, this could be a significant finding as it indicates that the low-porosity anode functional layer may affect how fast hydrogen may diffuse (or water diffuses out) through the three-phase boundary especially at lower hydrogen concentrations. This behavior could be a concern in a stack operating at high fuel utilization in locations where the hydrogen concentration becomes low and the water concentration becomes high. For this set of tests, the impedance data collected at OCV are shown in Figure 10. The ohmic portion or high frequency intercepts do not change with changing hydrogen flow rate as expected. Except for the lowest two flow rates, the low frequency intercepts are reasonably the same. This behavior indicates that the circles at low frequency are related to diffusion processes.Figure 9
Voltage and power density curves versus current density at different hydrogen flow rates at 750°C.Figure 10
Impedance curves at different hydrogen flow rates at 750°C.Finally, the dependence on air flow rate was also studied. Figure11 presents the voltage-current density characteristics for an air flow rate between 0.1 and 1.0 SLPM at 750°C. The curves are affected at all flow rates, though the loss of performance is larger at the lowest flow rates. For this set of tests, the impedance data collected at OCV are shown in Figure 12. Again, the ohmic portion does not change with changing flow rates. However, the low frequency circles do not seem to increase significantly and do not capture very well what is observed with the voltage-current density curves.Figure 11
Voltage and power density curves versus current density at different air flow rates at 750°C.Figure 12
Impedance curves at different air flow rates at 750°C.


## 4. Conclusion

In this work, an anode-supported SOFC cell has been tested and characterized at different temperatures and reactant flow rates. SEM/EDS analysis indicates no significant interdiffusion of the elements has occurred. In addition, the tested cell preserved its structural integrity and shows no damage or delamination. Voltage-current density and impedance data at different temperatures indicate an Arrhenius behavior or temperature activated processes. Variation in hydrogen flow rates indicates concerns with the low-porosity anode functional layer especially at low hydrogen contents. Variation in air flow rates also lowers the cell performance.



---

*Source: 4041960-2018-06-03.xml*