# Axial Vascularization of Nano-HA/Collagen/PLA Composites by Arteriovenous Bundle

Authors: Hai Wang; Xiao Chang; Guixing Qiu; Fuzhai Cui; Xisheng Weng; Baozhong Zhang; Bo Yang; Xiaojie Lian; Zhihong Wu
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

In previous studies, nano-hydroxyapatite/collagen/poly(L-lactic acid) (nHAC/PLA) composites have been prepared and confirmed to repair small sized bone defects. However, they are restricted to repair a large defect without sufficient oxygen and nutrition for cell survival. The result of this study confirmed that nHAC/PLA composites could be axially vascularized by being implanted intramuscularly with arteriovenous (AV) bundle (Group A) in the groins of rabbits. The combination with autologous bone marrow (Group B) could not enhance it the vascularization in early phase (2 weeks,P>0.05), but it could enhance in middle and later phases (6 and 10 weeks, P<0.01). It meant that nHAC/PLA could be prefabricated as a vascularized bone substitute for grafting.


---

## Body

## 1. Introduction

Reconstruction of large bone defects poses a major challenge to orthopedists. Despite the development of numerous biological and synthetic bone substitutes, vascularized and nonvascularized autologous bone grafts remain the gold standard for osteogenic bone replacement [1]. The shortcomings and complications of autologous bone grafting including fibula, scapula, or iliac crest restrict its application [2]. Allogenic and xenogenic bone grafts are risk of disease transmission [3]. Tissue engineering and regenerative medicine are promising therapeutic strategies for the repairment or replacement of diseased or injured tissues and organs [4]. Tissue-engineered bone (TEB) represents a promising approach to overcome these problems and is becoming an increasingly popular choice for repairing bone defects. Significant progress has been made toward scaffold materials for structural support with desired osteogenesis and angiogenesis abilities [5]. However, repair of bone defects over 30 mm using tissue-engineering methods is a difficult clinical problem now [6].Vascularization plays a very important role in skeletal development and repair [7]. It is crucial for TEB to establish a vascular network that temporally precedes the formation of new bone [8]. Because blood supply is restricted in its exterior portions without vascularization, cells face the lack of reliable oxygen and nutrient supply. In current surgical practice, tissues that need to be transferred from one part of the body to another as living three-dimensional constructs can be provided with a vasculature by prefabrication techniques [9]. Scaffolds including xenogenic bone mineral [10], poly(DL-lactic-co-glycolic acid) (PLGA) [9], HA/β-TCP granula [2], and processed bovine cancellous bone (PBCB) matrices [11] have been successfully vascularized with surgical angiogenesis skills, allowing transplantation to defect sites.A new type of nano-hydroxyapatite/collagen/poly(L-lactic acid) (nHAC/PLA) composite, similar to the natural bone in main composition and in hierarchical microstructure, has been fabricated before [12–15]. It possesses a porous microstructure with a pore size of about 100–300 μm and a porosity of about 80% like cancellous bone. The cell culture and the implant experiment demonstrated that it was bioactive and could repair some small bone defects. The purpose of this study was to evaluate whether vascularized nHAC/PLA composites could be prefabricated in vivo.


## 2. Materials and Methods

### 2.1. Materials

Synthesis of nHAC/PLA was prepared as previously described [12–15]. Type I collagen (CELLON Company, Strassen, Luxembourg) was diluted in deionized (DI) water at 0.67 g collagen/L and room temperature for 3 hours. Solutions of CaCl2 and H3PO4 (Ca/P = 1.66) were then separately added by drops. The solution was stirred and titrated with sodium hydroxide solution to pH 7.4 at room temperature. The nHAC deposition was harvested by centrifugation and freeze-dried after 48 hours. The nHAC powder was then distributed in the PLA matrix (MW = 1.0 × 105 Da; Shandong Medical Appliance Factory, Liaocheng, China) at a 1 : 1 weight ratio (nHAC/PLA). The mixture was frozen at −20°C overnight and then lyophilized to remove dioxane. After ultrasonication, the material was fabricated into cylindrical slices (Φ=10 mm × 10 mm) with a hole of 1.5 mm diameter in the center.


### 2.2. Experimental Design

All experiments were approved by the animal ethics committee of Peking Union Medical College Hospital (PUMCH), and the procedures were conducted in accordance with the guidelines for the care and maintenance of animals. Fifteen three-month-old New Zealand rabbits (Experimental Animal Center of PUMCH, Beijing, China) weighing 2.5 to 3.0 kg were used. All operations were performed under sterile conditions by the same surgeon. An nHAC/PLA composite was directly implanted into the intramuscular gap with an arteriovenous (AV) bundle in the left groin (Group A), and another one was implanted into the intramuscular gap with an AV bundle in the right groin (Group B) after being mixed with the autologous bone marrow. Histological examinations were performed at 2, 6, and 10 weeks after implantation.


### 2.3. Surgical Procedures

The animals were anesthetized with an intravenous injection of 3% pentobarbital sodium (1 mL/kg body weight, Sigma, USA). 800,000 IU penicillin sodium (North China Pharmaceutical Group Corporation, China) was injected intramuscularly for preventing infection. Group A was treated as follows. Through a skin incision from the groin midpoint to the left knee, the femoral neurovascular bundle was exposed, and the nerve was protected. The left femoral artery and vein were surgically dissociated and then were transversely cut and ligatured at 2 to 3 cm under the femoral artery furcation for an AV bundle. The AV bundle was placed in the hole of the nHAC/PLA composite and was placed into the intramuscular gap. The femoral muscle and skin were sutured with 3-0 silk sutures. In Group B, the same procedures were performed after another nHAC/PLA composite was mixed with 10 mL autologous bone marrow from its tibia using a self-made device (Figure1). Postoperatively, 800,000 IU penicillin sodium and 0.15 mg buprenorphine (Tianjin Institute of Pharmaceutical Research, China) were separately administered intramuscularly every 12 hours for 3 days.Figure 1
The self-made device for mixing bone marrow with an nHAC/PLA composite.


### 2.4. Histological Examinations

The animals were sacrificed after 2, 6, and 10 weeks (n=5, resp.). The implants were removed and fixed in 10% buffered formalin for 24 hours. After washing, they were decalcified by 14% ethylenediaminetetraacetic acid (EDTA) solution for 6 weeks. Then, they were dehydrated in graded ethanols and embedded in paraffin. Eight cross-sections (5 μm) were obtained from each specimen, perpendicular to the AV bundle in the middle (Figure 2(a)), using a Leica microtome (Leica Microsystems, Wetzlar, Germany). For histomorphometirc analysis, four sections were randomly selected for haematoxylin and eosin (H&E) staining, and microphotographs were taken using a microscope and a digital camera (Leica Microsystems). On each section, four microphotographs of interest in the inner 1/3 radius at 3, 6, 9, and 12 o’clock at 400x magnification were evaluated, and the number of vessels in high power field (HPF) was counted by two independent and blinded pathologists (Figure 2(b)). Microvessel density (MVD) was calculated for each group and each time point. One of the other sections was prepared for CD31 immunofluorescence histochemical staining with rabbit anti-PECAM-1 (primary antibody; Beijing Biosynthesis Biotechnology Corporation, China) and goat anti-rabbit IgG/FITC (second antibody; Beijing Biosynthesis Biotechnology Corporation, China) for qualitative assessment.Figure 2
Schematic drawing demonstrating the approach to histological examinations: (a) 8 cross-sections were obtained perpendicular to the AV bundle in the middle; (b) 4 microphotographs of interest in the inner1/3 radius at 3, 6, 9, and 12 o,clock at 400x   magnification were evaluated for MVD (dark black points).


### 2.5. Statistics Analysis

All results of MVD were given as means ± standard deviation (X ± SD, vessels/HPF). Statistical analysis was performed using the paired samples Student’s t-test with SPSS 16.0. The critical level of statistical significance was set at P<0.05.


## 2.1. Materials

Synthesis of nHAC/PLA was prepared as previously described [12–15]. Type I collagen (CELLON Company, Strassen, Luxembourg) was diluted in deionized (DI) water at 0.67 g collagen/L and room temperature for 3 hours. Solutions of CaCl2 and H3PO4 (Ca/P = 1.66) were then separately added by drops. The solution was stirred and titrated with sodium hydroxide solution to pH 7.4 at room temperature. The nHAC deposition was harvested by centrifugation and freeze-dried after 48 hours. The nHAC powder was then distributed in the PLA matrix (MW = 1.0 × 105 Da; Shandong Medical Appliance Factory, Liaocheng, China) at a 1 : 1 weight ratio (nHAC/PLA). The mixture was frozen at −20°C overnight and then lyophilized to remove dioxane. After ultrasonication, the material was fabricated into cylindrical slices (Φ=10 mm × 10 mm) with a hole of 1.5 mm diameter in the center.


## 2.2. Experimental Design

All experiments were approved by the animal ethics committee of Peking Union Medical College Hospital (PUMCH), and the procedures were conducted in accordance with the guidelines for the care and maintenance of animals. Fifteen three-month-old New Zealand rabbits (Experimental Animal Center of PUMCH, Beijing, China) weighing 2.5 to 3.0 kg were used. All operations were performed under sterile conditions by the same surgeon. An nHAC/PLA composite was directly implanted into the intramuscular gap with an arteriovenous (AV) bundle in the left groin (Group A), and another one was implanted into the intramuscular gap with an AV bundle in the right groin (Group B) after being mixed with the autologous bone marrow. Histological examinations were performed at 2, 6, and 10 weeks after implantation.


## 2.3. Surgical Procedures

The animals were anesthetized with an intravenous injection of 3% pentobarbital sodium (1 mL/kg body weight, Sigma, USA). 800,000 IU penicillin sodium (North China Pharmaceutical Group Corporation, China) was injected intramuscularly for preventing infection. Group A was treated as follows. Through a skin incision from the groin midpoint to the left knee, the femoral neurovascular bundle was exposed, and the nerve was protected. The left femoral artery and vein were surgically dissociated and then were transversely cut and ligatured at 2 to 3 cm under the femoral artery furcation for an AV bundle. The AV bundle was placed in the hole of the nHAC/PLA composite and was placed into the intramuscular gap. The femoral muscle and skin were sutured with 3-0 silk sutures. In Group B, the same procedures were performed after another nHAC/PLA composite was mixed with 10 mL autologous bone marrow from its tibia using a self-made device (Figure1). Postoperatively, 800,000 IU penicillin sodium and 0.15 mg buprenorphine (Tianjin Institute of Pharmaceutical Research, China) were separately administered intramuscularly every 12 hours for 3 days.Figure 1
The self-made device for mixing bone marrow with an nHAC/PLA composite.


## 2.4. Histological Examinations

The animals were sacrificed after 2, 6, and 10 weeks (n=5, resp.). The implants were removed and fixed in 10% buffered formalin for 24 hours. After washing, they were decalcified by 14% ethylenediaminetetraacetic acid (EDTA) solution for 6 weeks. Then, they were dehydrated in graded ethanols and embedded in paraffin. Eight cross-sections (5 μm) were obtained from each specimen, perpendicular to the AV bundle in the middle (Figure 2(a)), using a Leica microtome (Leica Microsystems, Wetzlar, Germany). For histomorphometirc analysis, four sections were randomly selected for haematoxylin and eosin (H&E) staining, and microphotographs were taken using a microscope and a digital camera (Leica Microsystems). On each section, four microphotographs of interest in the inner 1/3 radius at 3, 6, 9, and 12 o’clock at 400x magnification were evaluated, and the number of vessels in high power field (HPF) was counted by two independent and blinded pathologists (Figure 2(b)). Microvessel density (MVD) was calculated for each group and each time point. One of the other sections was prepared for CD31 immunofluorescence histochemical staining with rabbit anti-PECAM-1 (primary antibody; Beijing Biosynthesis Biotechnology Corporation, China) and goat anti-rabbit IgG/FITC (second antibody; Beijing Biosynthesis Biotechnology Corporation, China) for qualitative assessment.Figure 2
Schematic drawing demonstrating the approach to histological examinations: (a) 8 cross-sections were obtained perpendicular to the AV bundle in the middle; (b) 4 microphotographs of interest in the inner1/3 radius at 3, 6, 9, and 12 o,clock at 400x   magnification were evaluated for MVD (dark black points).


## 2.5. Statistics Analysis

All results of MVD were given as means ± standard deviation (X ± SD, vessels/HPF). Statistical analysis was performed using the paired samples Student’s t-test with SPSS 16.0. The critical level of statistical significance was set at P<0.05.


## 3. Results

### 3.1. Surgery and Macroscopic Appearance

All 15 rabbits tolerated the surgical procedure and survived well. There were no major perioperative complications such as infection, hematomas, or wound dehiscence. No extrusion of the implants occurred over the observation period. The implants were surrounded by neighbouring tissue. At each time point, there was no significant difference of the mass around tissue and the blood supply of the implants between the two groups in the macroscopic appearance.


### 3.2. Histological Examinations

The newly formed tissue was composed predominantly of inflammatory cells, fibroblasts, blood vessels, and vascular sprouts in both groups (Figure3). There was less tissue occupying the pores of nHAC/PLA in Group A than in Group B. Along with the time extension, there were fewer inflammatory cells and more fibroblasts and vessels. At 2 weeks later, MVD of the implants in both groups is similar (9.35 ± 1.58 versus 9.08 ± 2.18, P=0.712>0.05, Figure 4).  At 6 weeks later, MVD of the implants in Group A was significantly less than in Group B (15.60 ± 3.20 versus 19.08 ± 3.18, P<0.01, Figure 4). When explanting after 10 weeks, MVD of the implants in Group A was also significantly less than in Group B (18.19 ± 3.17 versus 20.67 ± 3.78, P<0.01, Figure 4). There was a trend towards an increase in MVD in each group over time. The new vessels of the implants could be verified by using CD31 immunofluorescence histochemical staining (Figure 5). The vascular walls and red blood cells showed remarkable light green fluorescence. By 10 weeks, more new vessels were observed in Group B than Group A.Hematoxylin and eosin (H&E) staining of specimens (magnification×200): (a~c) 2, 6, and 10 weeks separately after implantation from Group A; (d~f) 2, 6, and 10  weeks separately after implantation from Group B. Black arrows showed vessels.
(a)
(b)
(c)
(d)
(e)
(f)Figure 4
Quantification of microvessel density (MVD) between Group A and Group B. 2 weeks: no significant difference (P>0.05); 6 and 10 weeks: significant difference (P<0.01).CD31 immunofluorescence histochemical staining of specimens 10 weeks after implantation (magnification×100): the vascular walls and red blood cells display remarkable light green fluorescence: (a) from Group A, (b) from Group B. Red arrows showed vessels.
(a)
(b)


## 3.1. Surgery and Macroscopic Appearance

All 15 rabbits tolerated the surgical procedure and survived well. There were no major perioperative complications such as infection, hematomas, or wound dehiscence. No extrusion of the implants occurred over the observation period. The implants were surrounded by neighbouring tissue. At each time point, there was no significant difference of the mass around tissue and the blood supply of the implants between the two groups in the macroscopic appearance.


## 3.2. Histological Examinations

The newly formed tissue was composed predominantly of inflammatory cells, fibroblasts, blood vessels, and vascular sprouts in both groups (Figure3). There was less tissue occupying the pores of nHAC/PLA in Group A than in Group B. Along with the time extension, there were fewer inflammatory cells and more fibroblasts and vessels. At 2 weeks later, MVD of the implants in both groups is similar (9.35 ± 1.58 versus 9.08 ± 2.18, P=0.712>0.05, Figure 4).  At 6 weeks later, MVD of the implants in Group A was significantly less than in Group B (15.60 ± 3.20 versus 19.08 ± 3.18, P<0.01, Figure 4). When explanting after 10 weeks, MVD of the implants in Group A was also significantly less than in Group B (18.19 ± 3.17 versus 20.67 ± 3.78, P<0.01, Figure 4). There was a trend towards an increase in MVD in each group over time. The new vessels of the implants could be verified by using CD31 immunofluorescence histochemical staining (Figure 5). The vascular walls and red blood cells showed remarkable light green fluorescence. By 10 weeks, more new vessels were observed in Group B than Group A.Hematoxylin and eosin (H&E) staining of specimens (magnification×200): (a~c) 2, 6, and 10 weeks separately after implantation from Group A; (d~f) 2, 6, and 10  weeks separately after implantation from Group B. Black arrows showed vessels.
(a)
(b)
(c)
(d)
(e)
(f)Figure 4
Quantification of microvessel density (MVD) between Group A and Group B. 2 weeks: no significant difference (P>0.05); 6 and 10 weeks: significant difference (P<0.01).CD31 immunofluorescence histochemical staining of specimens 10 weeks after implantation (magnification×100): the vascular walls and red blood cells display remarkable light green fluorescence: (a) from Group A, (b) from Group B. Red arrows showed vessels.
(a)
(b)


## 4. Discussion

Vascularization plays an important role in the process of osteogenesis, both in development and during repair. Osteogenesis is characterized by invasion of capillaries into the mesenchymal zone and the differentiation of mesenchymal cells into mature osteoblasts, which deposit bone matrix and lead to the formation of bone [16]. Diffusion limits oxygen and nutrition supply to a maximum range of 200 μm into a given matrix [17]. Cells cannot survive in the large constructs without vascularization after they are transferred in vivo environment.TEB, an alternative to autologous bone, allogenic and xenogenic bone grafts may overcome their shortcomings such as limited availability for harvest, donor-site morbidity, and disease transmission [2, 3]. It has become technically feasible to repair small sized bone defects in clinical practice, but it still remains challenging for reconstruction of large volume defects [18].The nHAC/PLA composite fabricated before, as one of TEBs, has been demonstrated that it was similar to the natural bone in main composition and in hierarchical microstructure [12].  Previous studies showed that it was bioactive and could repair some small bone defects [15]. However, there was no experiment about its ability of vascularization for repairing large defects so far. In this study, we first demonstrated that the nHAC/PLA composite could be vascularized in vivo.At present, there are three methods to achieve the vascularization of tissue: incorporation of angioinductive growth factors, endothelial cells coculture, and surgical techniques [7]. The vessels of a construct by incorporating endothelial cells are not mature and stable [19]. Delivery of angiogenic factors can only enhance the formation of new vessels [20, 21]. Recently, surgical angiogenesis, utilizing preexisting blood vessels as a vascular carrier and to incorporate artificial materials and cells into them to regenerate nutrient vessels, has become a promising method to establish a functional vascular network.The extrinsic vascular pathway, originating from the periphery of the construct by implanting into a site of high vascularization potential (subcutaneous [22], intramuscular [23], and intraperitoneal [24]), has become the most frequent method of vascularization in tissue engineering and has been available for clinical practice [25]. The disadvantage of this pathway is that the vascular network is random and will be destroyed while transferring to distant implantation sites. For this reason, axial vascularization (the intrinsic vascular pathway), originating from implanted vessels, has been proposed by reconstructive surgeons [18].The methods of axial vascularization included AV shunt loop, distal ligation type AV bundle, and flow-through type AV bundle. After comparing them, although the AV shunt loop showed a greater potential for producing new tissue and capillaries, the distal ligation type AV bundle was thought to be more effective and feasible as a vascular carrier [26]. Up to now, AV bundle has been applied clinically [27], but no application of AV shunt loops has been reported. The AV bundle is simpler to be constructed operatively than the AV shunt loop, does not present problems with thrombus formation, and provides stable blood flow [26]. Hence, distal ligation type AV bundle was chosen as axial vessels in this study. The results of this study showed that AV bundle could induce axial vascularization of nHAC/PLA composites. An nHAC/PLA composite after prefabrication in vivo could be transplanted as a free flap or a pedicle flap to a bone defect.In the past decade, researchers have gained important insights into the role of bone marrow derived cells in adult neovascularization. A subset of bone marrow derived cells, called endothelial progenitor cells, has been of particular interest, as these cells were suggested to home to sites of neovascularization and neoendothelialization and differentiate into endothelial cells in situ, a process referred to as postnatal vasculogenesis [28]. In this study, it was confirmed that the vascularization of nHAC/PLA composites with AV bundle could be significantly enhanced by autologous bone marrow in the middle and later phases. Meanwhile, there was no risk of rejection by autografting. So it was an ideal method to prefabricate a vascularized nHAC/PLA composite with the combination of AV bundle and autologous bone marrow.In conclusion, nHAC/PLA composites, implanted intramuscularly with AV bundles, had been shown to generate new vascular networks for prefabrication of large bone substitutes. The vascularization was better in combination with autologous bone marrow than without it and was more suitable for the microsurgery transplanting. Osteoinduction of microstructured calcium phosphate materials and multiwalled carbon nanotubes (MWNTs) has been shown in soft tissues by concentrating more proteins to differentiate inducible cells to osteogenic cells [29–31]. In the future, the osteoinduction of nHAC/PLA composites in soft tissues should be investigated to decide the possibility of ectopic fabrication of large volume vascularized TEB in combination with recombinant human bone morphogenetic protein-2 (rhBMP-2) or osteogenic protein-1 (OP-1).



---

*Source: 391832-2013-07-17.xml*