# Combating Wear of ASTM A36 Steel by Surface Modification Using Thermally Sprayed Cermet Coatings

Authors: Vineet Shibe; Vikas Chawla
Journal: Advances in Materials Science and Engineering
 (2016)

---

## Abstract

Thermal spray coatings can be applied economically on machine parts to enhance their requisite surface properties like wear, corrosion, erosion resistance, and so forth. Detonation gun (D-Gun) thermal spray coatings can be applied on the surface of carbon steels to improve their wear resistance. In the present study, alloy powder cermet coatings WC-12% Co and Cr3C2-25% NiCr have been deposited on ASTM A36 steel with D-Gun thermal spray technique. Sliding wear behavior of uncoated ASTM A36 steel and D-Gun sprayed WC-12% Co and Cr3C2-25% NiCr coatings on base material is observed on a Pin-On-Disc Wear Tester. Sliding wear performance of WC-12% Co coating is found to be better than the Cr3C2-25% NiCr coating. Wear performance of both these cermet coatings is found to be better than uncoated ASTM A36 steel. Thermally sprayed WC-12% Co and Cr3C2-25% NiCr cermet coatings using D-Gun thermal spray technique is found to be very useful in improving the sliding wear resistance of ASTM A36 steel.


---

## Body

## 1. Introduction

Wear controls the service life of machine components. Most of the components fail due to the combination of different types or modes of wear, such as corrosion, adhesion, impact, surface fatigue, abrasion, and erosion. Wear is the removal of material from the surfaces in contact when they slide or roll relative to each other [1]. It is a very slow process, but metal removal takes place steadily and continuously [2]. Wear can be minimized or controlled by using the costly, superior wear resistant materials or by the application of surface modification techniques on the low cost existing, inferior substrate materials [3]. The service life of the machine parts depends upon their surface properties and hence should be considered in design [4]. Surface engineering deals with different techniques that can be applied to achieve desired surface characteristics [5]. Surface engineering improves the performance and service life of machine parts. Its effectiveness on the performance and service life depends upon the material of the surface, alloy, type of service conditions, and the application process used [6].Wear and friction are responsible for many problems and costs more in a modern civilization. Engineers and designers must take these factors into account while designing and constructing different equipment [7]. The economic losses due to friction and wear related issues are about 1 to 2.5% of the gross national product [8]. The estimated costs of losses due to abrasive wear range from 1 to 4% of the gross national product of an industrialized nation [9]. So, it is important to focus on improving wear resistance of machine parts, as it impacts the economy the most.Although wear cannot be eliminated completely, it can be minimized to some extent by using different wear prevention methodologies. Some of the methods used for the prevention of wear are [10] selection of better material, lubrication, temperature control, alignment control, environmental control, contact pressure control, preventive maintenance, and use of surface coatings. Surface coating by thermal spraying is an optimum preventive method which is mostly used in the practical field of application.The desired technical or decorative properties can be enhanced by the application of surface coatings. A suitable coating can be applied on the surface of existing low cost inferior substrate material in the form of a superior layer of material [11]. The purpose of applying coatings to the surface of the substrate or base material is to prevent its surface from different types of wear and to improve the appearance of its surface [12].A number of thermal spray coating techniques are available such as D-Gun, plasma spray, and high velocity oxy-fuel (HVOF) [13]. It is a group of coating techniques in which a superior material to be coated is heated and accelerated towards the base metal to form a surface coating. A large number of materials can be deposited by thermal spraying to produce surface coatings.D-Gun thermal spraying technique finds a variety of applications like in the aircraft industries of the United States and Japan [13]. A D-Gun consists of a long barrel, a powder feeder, and a chamber in which the combustion is initiated and controlled. Gas flows are regulated and controlled with the help of control panels provided in D-Gun [14]. It includes a manipulator to hold and control the movements of the work piece. A measured mixture of oxygen and acetylene gases is fed into the barrel along with the coating powder to be deposited. The gas mixture is ignited with a spark and the combustion produces detonation waves. The detonation waves thus produced heats and accelerated the coating powder to be deposited. Some advantages of D-Gun spray coating process is increase in wear resistance by several times, dense microstructure, lower porosity, smooth surface finish, higher microhardness, lower oxidation of in-flight particles, improved wear and erosion wear resistance, and so forth.


## 2. Materials and Methods

### 2.1. Selection of the Substrate Material

Selection of the base material is made after consultation with Pressure and Process Boilers, Saharanpur (India). Nominal and actual chemical composition (weight % age) of ASTM A36 steel substrate is given in Table1.Table 1
Nominal and actual percentage composition of ASTM A36 steel.
Chemical composition (weight % age) of ASTM A36 steel substrate (IS 2062) % C % Si % Mn % P % S % Al % Cu % Cr % Mo % Ni % Pb % Ti % V % W % Fe Nominal 0.16 0.17 0.46 0.026 0.019 0.007 0.048 0.084 0.018 0.039 0.007 <0.001 0.003 <0.001 98.89 Actual 0.19 0.18 0.92 0.019 0.022 0.01 0.01 0.01 0.002 0.01 — — 0.001 — 98.626


### 2.2. Preparation of Test Specimens from ASTM A36 Steel Substrate Material

Small cylindrical pins of circular cross-section having a diameter of 8 mm and length 30 mm are prepared from ASTM A36 steel material. Manufacturing process such as machining or metal cutting/removal is used for manufacturing cylindrical pins. The pins are machined to required dimensions on lathe machine by using operations like simple turning, facing, and so forth. The end faces of the specimens are ground using emery papers and subsequently polished by polishing papers before the application of surface coating.


### 2.3. Thermal Spray Powders for Coatings

Two types of cermet coating powders, namely, WC-12% Co and Cr3C2-25% NiCr, are selected for detonation spray deposition on the ASTM A36 steel substrate specimens after the through literature review. Scanning electron microscope (SEM) images and energy-dispersive X-ray spectroscopy (EDS) patterns showing the morphologies, microstructure, and elemental composition of WC-12% Co and Cr3C2-25% NiCr feedstock powders have been shown in Figure 1. The results obtained from EDS confirm that WC-12% Co powder contains C, Co, and W elements and Cr3C2-25% NiCr powder contains C, Ni, and Cr elements.Figure 1
SEM images and EDS patterns showing the morphologies, microstructure, and elemental composition of the (a) WC-12% Co; (b) Cr3C2-25% NiCr feedstock powders.
(a) (b)


### 2.4. Formulation of the Coating

WC-12% Co and Cr3C2-25% NiCr powders are effectively deposited on an ASTM A36 steel substrate by the D-Gun thermal spray coating technique. These coatings are deposited at SVX Powder M Surface Engineering Private Limited, Greater Noida, U.P. (India). Very hard, dense coatings with high bond strength ranging from 70 MPa to 75 MPa are produced by depositing WC-12% Co and Cr3C2-25% NiCr coating powders by D-Gun technique on an ASTM A36 steel substrate. The average bond strength of WC-12% Co and Cr3C2-25% NiCr coating on an ASTM A36 steel substrate is tested using the ASTM standard C633-01 at Metallizing Equipment Company Private Limited, Jodhpur, India. A total of three specimens are tested for WC-12% Co and Cr3C2-25% NiCr coating and the average value of the bond strength is found to be 74 MPa and 71 MPa, respectively. The WC-12% Co powder is supplied by H. C. Starck, Germany, under the product code Amperit 518.074. The powder is agglomerated and sintered having a particle size as 10–45 microns. Cr3C2-25% NiCr powder is supplied by H. C. Starck, Germany, under the product code Amperit 588.074. The powder is agglomerated and sintered having a particle size of 10–45 microns. The parameters used for D-Gun thermal spraying for the two coatings at a spraying distance of 165 mm are shown in Table 2.Table 2
Detonation spray parameters.
WC-12% Co Cr3C2-25% NiCr Gases Flow rate (std. liters per hour) Oxygen 2960 2720 Acetylene 2400 2320 Nitrogen 720 720The front view and top view (macrographs) of uncoated or bare test specimens, WC-12% Co coated pins and Cr3C2-25% NiCr coated pins, have been shown in Figures 2(a), 2(b), and 2(c) respectively.Figure 2
The figure shows the front view and top view (macrographs) of (a) uncoated or bare (ASTM A36) test specimens; (b) WC-12% Co coated pins; (c) Cr3C2-25% NiCr coated pins prepared for the sliding wear testing on pin-on-disc wear tester.
(a) (b) (c)


### 2.5. Measurement of Coating Thickness

Average thickness of WC-12% Co and Cr3C2-25% NiCr coatings on ASTM A36 steel is measured with a thickness gauge Minitest-2000 during D-gun spraying process. Efforts are made to deposit coatings of uniform thickness of 250±10 μm in all the cases of WC-12% Co and Cr3C2-25% NiCr powders for ASTM A36 steel substrate.


### 2.6. Experimental Procedures

Sliding wear tests are conducted on bare and cermet coated ASTM A36 steel samples using a pin-on-disc Tester. The model of the wear and friction monitor tester used is TR-20-PHM-CHM-600 of Ducom make (Ducom Instruments Pvt. Ltd., Bangalore, India) conforming to ASTM G 99 standard. Wear tests are performed on the flat end faces of the pins at room temperature in air having a relative humidity of 51.5%. During wear testing the specimen pin is held stationary against the counter face of a rotating disc at fixed track diameter. Rotating disc is made of an alloy steel (EN-31) which was case hardened (63 to 65 HRC). The composition of EN-31 steel material is given in Table3.Table 3
Chemical composition (weight % age) of the EN-31 steel disc.
Chemical composition (weight % age) of EN31 steel C Si Mn Cr Ni S P 0.90–1.20 0.10–0.35 0.30–0.75 1.00–1.60 1.46 0.04 0.04


### 2.7. Sliding Wear Studies

The specifications of the pin-on-disc tester used for wear testing include wear track diameter ranging from 10 to 100 mm, speed ranging from 200 to 2000 rpm, normal load ranging from 5 to 200 N, and sliding velocity ranging from 0.5 to 10 ms−1. Both the disc and the pin are thoroughly cleaned and dried, before conducting the wear tests. The pin is loaded against the rotating disc through a dead weight loading system. The test parameters taken in the present investigation include wear track diameter (D) of 80 mm, speed of rotation of the disc (N) at 477 rpm, and three different normal applied loads of 40 N, 50 N and 60 N. The specimen pins are held at a fixed wear track diameter of 80 mm in order to have a constant sliding velocity (v) of 2 ms−1 throughout the wear testing, as v=(πDN/60) ms−1. Thus, the wear tests are conducted for bare and coated specimens at a constant sliding velocity of 2 ms−1 at three different normal applied loads of 40 N, 50 N, and 60 N. A constant linear sliding velocity of 2 ms−1 is maintained by adjusting the speed of rotation of the disc. Wear tests are conducted for a total sliding distance of 10,800 m for each specimen. Weight losses of all the samples are measured after 5, 5, 10, 10, 20, and 40 minutes to find the wear loss. The weight is measured on a microbalance to an accuracy of 0.001 g. This weight loss data is used to determine the cumulative wear rate (C.W.R). Results of C.W.R. (in Bowden) with the sliding distance (m) are reported in the results and discussion.


## 2.1. Selection of the Substrate Material

Selection of the base material is made after consultation with Pressure and Process Boilers, Saharanpur (India). Nominal and actual chemical composition (weight % age) of ASTM A36 steel substrate is given in Table1.Table 1
Nominal and actual percentage composition of ASTM A36 steel.
Chemical composition (weight % age) of ASTM A36 steel substrate (IS 2062) % C % Si % Mn % P % S % Al % Cu % Cr % Mo % Ni % Pb % Ti % V % W % Fe Nominal 0.16 0.17 0.46 0.026 0.019 0.007 0.048 0.084 0.018 0.039 0.007 <0.001 0.003 <0.001 98.89 Actual 0.19 0.18 0.92 0.019 0.022 0.01 0.01 0.01 0.002 0.01 — — 0.001 — 98.626


## 2.2. Preparation of Test Specimens from ASTM A36 Steel Substrate Material

Small cylindrical pins of circular cross-section having a diameter of 8 mm and length 30 mm are prepared from ASTM A36 steel material. Manufacturing process such as machining or metal cutting/removal is used for manufacturing cylindrical pins. The pins are machined to required dimensions on lathe machine by using operations like simple turning, facing, and so forth. The end faces of the specimens are ground using emery papers and subsequently polished by polishing papers before the application of surface coating.


## 2.3. Thermal Spray Powders for Coatings

Two types of cermet coating powders, namely, WC-12% Co and Cr3C2-25% NiCr, are selected for detonation spray deposition on the ASTM A36 steel substrate specimens after the through literature review. Scanning electron microscope (SEM) images and energy-dispersive X-ray spectroscopy (EDS) patterns showing the morphologies, microstructure, and elemental composition of WC-12% Co and Cr3C2-25% NiCr feedstock powders have been shown in Figure 1. The results obtained from EDS confirm that WC-12% Co powder contains C, Co, and W elements and Cr3C2-25% NiCr powder contains C, Ni, and Cr elements.Figure 1
SEM images and EDS patterns showing the morphologies, microstructure, and elemental composition of the (a) WC-12% Co; (b) Cr3C2-25% NiCr feedstock powders.
(a) (b)


## 2.4. Formulation of the Coating

WC-12% Co and Cr3C2-25% NiCr powders are effectively deposited on an ASTM A36 steel substrate by the D-Gun thermal spray coating technique. These coatings are deposited at SVX Powder M Surface Engineering Private Limited, Greater Noida, U.P. (India). Very hard, dense coatings with high bond strength ranging from 70 MPa to 75 MPa are produced by depositing WC-12% Co and Cr3C2-25% NiCr coating powders by D-Gun technique on an ASTM A36 steel substrate. The average bond strength of WC-12% Co and Cr3C2-25% NiCr coating on an ASTM A36 steel substrate is tested using the ASTM standard C633-01 at Metallizing Equipment Company Private Limited, Jodhpur, India. A total of three specimens are tested for WC-12% Co and Cr3C2-25% NiCr coating and the average value of the bond strength is found to be 74 MPa and 71 MPa, respectively. The WC-12% Co powder is supplied by H. C. Starck, Germany, under the product code Amperit 518.074. The powder is agglomerated and sintered having a particle size as 10–45 microns. Cr3C2-25% NiCr powder is supplied by H. C. Starck, Germany, under the product code Amperit 588.074. The powder is agglomerated and sintered having a particle size of 10–45 microns. The parameters used for D-Gun thermal spraying for the two coatings at a spraying distance of 165 mm are shown in Table 2.Table 2
Detonation spray parameters.
WC-12% Co Cr3C2-25% NiCr Gases Flow rate (std. liters per hour) Oxygen 2960 2720 Acetylene 2400 2320 Nitrogen 720 720The front view and top view (macrographs) of uncoated or bare test specimens, WC-12% Co coated pins and Cr3C2-25% NiCr coated pins, have been shown in Figures 2(a), 2(b), and 2(c) respectively.Figure 2
The figure shows the front view and top view (macrographs) of (a) uncoated or bare (ASTM A36) test specimens; (b) WC-12% Co coated pins; (c) Cr3C2-25% NiCr coated pins prepared for the sliding wear testing on pin-on-disc wear tester.
(a) (b) (c)


## 2.5. Measurement of Coating Thickness

Average thickness of WC-12% Co and Cr3C2-25% NiCr coatings on ASTM A36 steel is measured with a thickness gauge Minitest-2000 during D-gun spraying process. Efforts are made to deposit coatings of uniform thickness of 250±10 μm in all the cases of WC-12% Co and Cr3C2-25% NiCr powders for ASTM A36 steel substrate.


## 2.6. Experimental Procedures

Sliding wear tests are conducted on bare and cermet coated ASTM A36 steel samples using a pin-on-disc Tester. The model of the wear and friction monitor tester used is TR-20-PHM-CHM-600 of Ducom make (Ducom Instruments Pvt. Ltd., Bangalore, India) conforming to ASTM G 99 standard. Wear tests are performed on the flat end faces of the pins at room temperature in air having a relative humidity of 51.5%. During wear testing the specimen pin is held stationary against the counter face of a rotating disc at fixed track diameter. Rotating disc is made of an alloy steel (EN-31) which was case hardened (63 to 65 HRC). The composition of EN-31 steel material is given in Table3.Table 3
Chemical composition (weight % age) of the EN-31 steel disc.
Chemical composition (weight % age) of EN31 steel C Si Mn Cr Ni S P 0.90–1.20 0.10–0.35 0.30–0.75 1.00–1.60 1.46 0.04 0.04


## 2.7. Sliding Wear Studies

The specifications of the pin-on-disc tester used for wear testing include wear track diameter ranging from 10 to 100 mm, speed ranging from 200 to 2000 rpm, normal load ranging from 5 to 200 N, and sliding velocity ranging from 0.5 to 10 ms−1. Both the disc and the pin are thoroughly cleaned and dried, before conducting the wear tests. The pin is loaded against the rotating disc through a dead weight loading system. The test parameters taken in the present investigation include wear track diameter (D) of 80 mm, speed of rotation of the disc (N) at 477 rpm, and three different normal applied loads of 40 N, 50 N and 60 N. The specimen pins are held at a fixed wear track diameter of 80 mm in order to have a constant sliding velocity (v) of 2 ms−1 throughout the wear testing, as v=(πDN/60) ms−1. Thus, the wear tests are conducted for bare and coated specimens at a constant sliding velocity of 2 ms−1 at three different normal applied loads of 40 N, 50 N, and 60 N. A constant linear sliding velocity of 2 ms−1 is maintained by adjusting the speed of rotation of the disc. Wear tests are conducted for a total sliding distance of 10,800 m for each specimen. Weight losses of all the samples are measured after 5, 5, 10, 10, 20, and 40 minutes to find the wear loss. The weight is measured on a microbalance to an accuracy of 0.001 g. This weight loss data is used to determine the cumulative wear rate (C.W.R). Results of C.W.R. (in Bowden) with the sliding distance (m) are reported in the results and discussion.


## 3. Results

### 3.1. Microstructure of the Coatings

The Scanning electron microscope (SEM) micrographs for D-Gun sprayed WC-12% Co coating on ASTM A36 is shown in Figure3(a) and for Cr3C2-25% NiCr coating on the same substrate is shown in Figure 3(b). Figure 3(a)(A) depicts the small size splats in case of WC-12% Co coating whereas Figure 3(b)(A) shows the coarse splats in case of Cr3C2-25% NiCr coating. Figures 3(a)(B), 3(a)(C), 3(a)(D), 3(b)(B), 3(b)(C), and 3(b)(D) depict the SEM images of the worn samples of WC-12% Co and Cr3C2-25% NiCr coating after the conduct of wear tests at the normal applied loads of 40 N, 50 N, and 60 N, respectively. It is quite clear from these SEM images of worn samples that, at higher applied load, there is more extensive loss of material.Figure 3
(a) SEM images of D-Gun sprayed WC-12% Co coating showing: (A) Unworn surface; (B) Surface worn under a load of 40 N; (C) Surface worn under a load of 50 N; (D) Surface worn under a load of 60 N. (b) SEM images of D-Gun sprayed Cr3C2-25% NiCr coating showing: (A) Unworn surface; (B) Surface worn under a load of 40 N; (C) Surface worn under a load of 50 N; (D) Surface worn under a load of 60 N.
(a) (b)


### 3.2. X-Ray Diffraction (XRD) Analysis

XRD patterns for D-Gun sprayed WC-12% Co on an ASTM A36 steel substrate is shown in Figure4(a). XRD patterns for D-gun sprayed Cr3C2-25% NiCr coating on an ASTM A36 steel substrate are shown in Figure 4(b). From the XRD patterns for D-Gun sprayed WC-12% Co coating on ASTM A36 steel substrate, it is found that WC-12% Co coated specimen showed the major phases of WC and the minor phases of Co.Figure 4
X-ray diffraction patterns of D-Gun sprayed (a) WC-12% Co; (b) Cr3C2-25% NiCr coating on an ASTM A36 steel substrate.
(a) (b)From the XRD patterns for D-gun sprayed Cr3C2-25% NiCr coating on ASTM A36 steel substrate, it is found that Cr3C2-25% NiCr coated specimen showed the major phases of Cr3C2, Cr7C3, and Ni which are desired phases of this coating.


### 3.3. Evaluation of Microhardness

The microhardness of the coatings is measured on the surface and along the cross-section. The cross-sectional analysis reading is taken with reference to the substrate-coating interface at intervals of 50-micron approximate distances. Miniload 2 Microhardness Tester (Leitz, Germany) fitted with a Vicker’s pyramidal diamond indenter is used for measuring the microhardness of the coatings at 200 g load at Central Tool Room, Ludhiana, Govt. of India Society, Ministry of Micro, Small and Medium Enterprises. The critical microhardness values of the substrate are found to be in the range 211–220 HV0.2. The WC-12% Co coating has shown maximum microhardness of the order of 1178–1192 HV0.2. Cr3C2-25% NiCr coating has shown microhardness in the order of 716–726 HV0.2.


### 3.4. Measurement of Porosity

Few pores and voids appear in the D-gun sprayed coatings, as it is an intermittent process during metal spraying. The porosity measurements are made by PMP3 inverted metallurgical microscope with stereographic imaging. The magnification is selected in such a way that the coating microstructure image covers the screen and permits the resolution of the voids that provides remarkably to the total porosity area percentage. The method of choosing the suitable range of light gray contrast spots is accomplished systematically by stereographic imaging to guarantee that only voids are chosen. The analysis using an image processing software decides the pore area size in the sight range by changing over the pore areas into a background color; for example, red despite whatever is left of the microstructure remains in its actual color. The area of one element is mathematically related to the total area of the image, as the program counts the number of one-color-type pixels, for example, red, and sets that as a proportion of the total number of pixels in the image, that is, the total area. Around twenty discrete locations are chosen to prevent the overlap between two locations and decide the area percent porosity [15]. The optical images depicting the porosity in D-Gun sprayed WC-12% Co and Cr3C2-25% NiCr coating on an ASTM A36 steel substrate are shown in Figures 5(a) and 5(b), respectively. The average porosity of WC-12% Co and Cr3C2-25% NiCr coating is found to be 0.28776% and 0.84625%, respectively, on an ASTM A36 steel substrate. Thus, the average porosity of all the as sprayed coatings is found to be less than 1.0%.Figure 5
Optical images showing the porosity in D-Gun sprayed (a) WC-12% Co; (b) Cr3C2-25% NiCr coating on an ASTM A36 steel substrate.
(a) (b)


### 3.5. Measurement of Surface Roughness (Ra) Values

Veeco Optical Profilometer (NT 1100, USA make) is used to measure the surface roughness (Ra values) at IIT, Roorkee. It has the three-dimensional profiling capability with excellent precision and accuracy. The roughness is found to be in the range of 2.96–4.27 μm for WC-12% Co coatings and 3.96–4.64 μm for Cr3C2-25% NiCr, respectively.


### 3.6. Wear Behavior

Wear testing of bare as well as cermet coated specimens is conducted on a Pin-On-Disc wear tester [16] as per the standard procedure conforming to ASTM G99 standard. Variation of C.W.R. (in Bowden) with the sliding distance has been discussed in this section for the different cases under investigation. Variation of the C.W.R. with the sliding distance for bare and WC-12% Co, Cr3C2-25% NiCr coated ASTM A36 steel at a normal applied load of 40 N, 50 N, and 60 N has been plotted in Figures 6(a), 6(b), and 6(c), respectively.Figure 6
Variation of C.W.R. for uncoated and D-Gun spray coated ASTM A36 steel at normal applied load of (a) 40 N; (b) 50 N; (c) 60 N at sliding velocity of 2 ms−1.
(a) (b) (c)It is clear from Figure6 that the WC-12% Co coated samples have shown considerable wear resistance at the three different applied loads of 40 N, 50 N, and 60 N in comparison with Cr3C2-25% NiCr coated and bare samples.Bar charts as shown in Figures7(a), 7(b), and 7(c) clearly depict the C.W.R. for bare and D-Gun spray coated ASTM A36 steel at normal applied load of 40 N, 50 N, and 60 N at a sliding velocity of 2 ms−1, after a sliding distance of 10,800 m.Figure 7
Bar chart showing C.W.R. for uncoated (bare) and D-Gun sprayed coated ASTM A36 steel at normal applied load of (a) 40 N; (b) 50 N; (c) 60 N at a sliding velocity of 2 ms−1, after a sliding distance of 10,800 m.
(a) (b) (c)These plots and bar charts clearly show that the bare ASTM steel specimen has shown much higher C.W.R as compared to cermet coated specimens at all the different applied loads of 40 N, 50 N, and 60 N. Therefore, it can be concluded that at different loads of 40 N, 50 N, and 60 N the D-Gun sprayed WC-12% Co coating has shown considerable wear resistance as compared to the Cr3C2-25% NiCr coated specimens and bare ASTM A36 steel.


## 3.1. Microstructure of the Coatings

The Scanning electron microscope (SEM) micrographs for D-Gun sprayed WC-12% Co coating on ASTM A36 is shown in Figure3(a) and for Cr3C2-25% NiCr coating on the same substrate is shown in Figure 3(b). Figure 3(a)(A) depicts the small size splats in case of WC-12% Co coating whereas Figure 3(b)(A) shows the coarse splats in case of Cr3C2-25% NiCr coating. Figures 3(a)(B), 3(a)(C), 3(a)(D), 3(b)(B), 3(b)(C), and 3(b)(D) depict the SEM images of the worn samples of WC-12% Co and Cr3C2-25% NiCr coating after the conduct of wear tests at the normal applied loads of 40 N, 50 N, and 60 N, respectively. It is quite clear from these SEM images of worn samples that, at higher applied load, there is more extensive loss of material.Figure 3
(a) SEM images of D-Gun sprayed WC-12% Co coating showing: (A) Unworn surface; (B) Surface worn under a load of 40 N; (C) Surface worn under a load of 50 N; (D) Surface worn under a load of 60 N. (b) SEM images of D-Gun sprayed Cr3C2-25% NiCr coating showing: (A) Unworn surface; (B) Surface worn under a load of 40 N; (C) Surface worn under a load of 50 N; (D) Surface worn under a load of 60 N.
(a) (b)


## 3.2. X-Ray Diffraction (XRD) Analysis

XRD patterns for D-Gun sprayed WC-12% Co on an ASTM A36 steel substrate is shown in Figure4(a). XRD patterns for D-gun sprayed Cr3C2-25% NiCr coating on an ASTM A36 steel substrate are shown in Figure 4(b). From the XRD patterns for D-Gun sprayed WC-12% Co coating on ASTM A36 steel substrate, it is found that WC-12% Co coated specimen showed the major phases of WC and the minor phases of Co.Figure 4
X-ray diffraction patterns of D-Gun sprayed (a) WC-12% Co; (b) Cr3C2-25% NiCr coating on an ASTM A36 steel substrate.
(a) (b)From the XRD patterns for D-gun sprayed Cr3C2-25% NiCr coating on ASTM A36 steel substrate, it is found that Cr3C2-25% NiCr coated specimen showed the major phases of Cr3C2, Cr7C3, and Ni which are desired phases of this coating.


## 3.3. Evaluation of Microhardness

The microhardness of the coatings is measured on the surface and along the cross-section. The cross-sectional analysis reading is taken with reference to the substrate-coating interface at intervals of 50-micron approximate distances. Miniload 2 Microhardness Tester (Leitz, Germany) fitted with a Vicker’s pyramidal diamond indenter is used for measuring the microhardness of the coatings at 200 g load at Central Tool Room, Ludhiana, Govt. of India Society, Ministry of Micro, Small and Medium Enterprises. The critical microhardness values of the substrate are found to be in the range 211–220 HV0.2. The WC-12% Co coating has shown maximum microhardness of the order of 1178–1192 HV0.2. Cr3C2-25% NiCr coating has shown microhardness in the order of 716–726 HV0.2.


## 3.4. Measurement of Porosity

Few pores and voids appear in the D-gun sprayed coatings, as it is an intermittent process during metal spraying. The porosity measurements are made by PMP3 inverted metallurgical microscope with stereographic imaging. The magnification is selected in such a way that the coating microstructure image covers the screen and permits the resolution of the voids that provides remarkably to the total porosity area percentage. The method of choosing the suitable range of light gray contrast spots is accomplished systematically by stereographic imaging to guarantee that only voids are chosen. The analysis using an image processing software decides the pore area size in the sight range by changing over the pore areas into a background color; for example, red despite whatever is left of the microstructure remains in its actual color. The area of one element is mathematically related to the total area of the image, as the program counts the number of one-color-type pixels, for example, red, and sets that as a proportion of the total number of pixels in the image, that is, the total area. Around twenty discrete locations are chosen to prevent the overlap between two locations and decide the area percent porosity [15]. The optical images depicting the porosity in D-Gun sprayed WC-12% Co and Cr3C2-25% NiCr coating on an ASTM A36 steel substrate are shown in Figures 5(a) and 5(b), respectively. The average porosity of WC-12% Co and Cr3C2-25% NiCr coating is found to be 0.28776% and 0.84625%, respectively, on an ASTM A36 steel substrate. Thus, the average porosity of all the as sprayed coatings is found to be less than 1.0%.Figure 5
Optical images showing the porosity in D-Gun sprayed (a) WC-12% Co; (b) Cr3C2-25% NiCr coating on an ASTM A36 steel substrate.
(a) (b)


## 3.5. Measurement of Surface Roughness (Ra) Values

Veeco Optical Profilometer (NT 1100, USA make) is used to measure the surface roughness (Ra values) at IIT, Roorkee. It has the three-dimensional profiling capability with excellent precision and accuracy. The roughness is found to be in the range of 2.96–4.27 μm for WC-12% Co coatings and 3.96–4.64 μm for Cr3C2-25% NiCr, respectively.


## 3.6. Wear Behavior

Wear testing of bare as well as cermet coated specimens is conducted on a Pin-On-Disc wear tester [16] as per the standard procedure conforming to ASTM G99 standard. Variation of C.W.R. (in Bowden) with the sliding distance has been discussed in this section for the different cases under investigation. Variation of the C.W.R. with the sliding distance for bare and WC-12% Co, Cr3C2-25% NiCr coated ASTM A36 steel at a normal applied load of 40 N, 50 N, and 60 N has been plotted in Figures 6(a), 6(b), and 6(c), respectively.Figure 6
Variation of C.W.R. for uncoated and D-Gun spray coated ASTM A36 steel at normal applied load of (a) 40 N; (b) 50 N; (c) 60 N at sliding velocity of 2 ms−1.
(a) (b) (c)It is clear from Figure6 that the WC-12% Co coated samples have shown considerable wear resistance at the three different applied loads of 40 N, 50 N, and 60 N in comparison with Cr3C2-25% NiCr coated and bare samples.Bar charts as shown in Figures7(a), 7(b), and 7(c) clearly depict the C.W.R. for bare and D-Gun spray coated ASTM A36 steel at normal applied load of 40 N, 50 N, and 60 N at a sliding velocity of 2 ms−1, after a sliding distance of 10,800 m.Figure 7
Bar chart showing C.W.R. for uncoated (bare) and D-Gun sprayed coated ASTM A36 steel at normal applied load of (a) 40 N; (b) 50 N; (c) 60 N at a sliding velocity of 2 ms−1, after a sliding distance of 10,800 m.
(a) (b) (c)These plots and bar charts clearly show that the bare ASTM steel specimen has shown much higher C.W.R as compared to cermet coated specimens at all the different applied loads of 40 N, 50 N, and 60 N. Therefore, it can be concluded that at different loads of 40 N, 50 N, and 60 N the D-Gun sprayed WC-12% Co coating has shown considerable wear resistance as compared to the Cr3C2-25% NiCr coated specimens and bare ASTM A36 steel.


## 4. Discussion

### 4.1. Microstructure of the Coatings

The WC-12% Co coating has small size splats whereas the splats are coarse for Cr3C2-25% NiCr. From the SEM images as shown in Figures 3(a)(B), 3(a)(C), 3(a)(D), 3(b)(B), 3(b)(C), and 3(b)(D) it is clear that, at higher applied load, there is more extensive loss of material. There is no subsurface cracking in the case of the coated specimens. WC-12% Co coated samples were found to be more wear resistant at three different applied loads of 40 N, 50 N, and 60 N than Cr3C2-25% NiCr. In the present investigation, superior wear resistance of WC-12% Co coating is found which may be due to the presence of W on its surface. Similar results and microstructure are obtained by Chivavibul et al. [17] for WC-Co coatings. The microstructure obtained for Cr3C2-25% NiCr coatings are similar to the findings of Kamal et al. [18].


### 4.2. X-Ray Diffraction (XRD) Analysis

The number of peaks corresponding to different phases of WC-12% Co and Cr3C2-25% NiCr coatings on ASTM A36 material can be seen from diffraction patterns as shown in Figures 4(a) and 4(b), respectively. Theses identified phases for WC-Co coatings are in agreement with those observed by Suresh Babu et al. [19]. XRD phases identified for Cr3C2-25% NiCr coatings are in agreement with the findings of Mohanty et al. [20].


### 4.3. Evaluation of Microhardness

The higher microhardness values of WC-12% Co and Cr3C2-25% NiCr cermet coatings may be one of the reasons of high wear resistance of these coatings, which is in agreement with those observed by Sahraoui et al. [21].


### 4.4. Measurement of Porosity

The lower porosity of WC-12% Co and Cr3C2-25% NiCr cermet coatings may be one of the reasons of high wear resistance of these coatings, which is also supported by the findings of Sahraoui et al. [21].


### 4.5. Surface Roughness (Ra) Values

Coatings are differentiated on the basis of their properties like porosity, microhardness, microstructure, surface roughness and residual stresses. The surface of the coating is rough due to the due to the presence of fully melted and partially melted particles.


### 4.6. Wear Behavior

From the plots showing the variation of the C.W.R. with the sliding distance for bare and WC-12% Co, Cr3C2-25% NiCr coated ASTM A36 steel at a normal applied load of 40 N, 50 N, and 60 N, it is evident that the WC-12% Co and Cr3C2-25% NiCr cermet coated samples have shown lower C.W.R than uncoated ASTM A36 steel samples at all these three different applied loads.From the bar charts showing C.W.R. for uncoated and D-Gun sprayed coated ASTM A36 steel at normal applied load of 40 N, 50 N, and 60 N at a constant sliding velocity of 2 ms−1, after a sliding distance of 10,800 m, it is clear that the bare ASTM steel specimen has shown much higher C.W.R as compared to cermet coated specimens at all these three different applied loads. D-Gun sprayed WC-12% Co coating has shown considerable wear resistance as compared to the Cr3C2-25% NiCr coated specimens and bare ASTM A36 steel at all these three different applied loads. Also, it is found that the C.W.R for WC-12% Co and Cr3C2-25% NiCr cermet coated samples and bare ASTM A36 steel samples increases with an increase in the applied normal load.D-Gun sprayed coatings are more wear resistant than bare or uncoated material which is in agreement with what was observed by Murthy et al. [22], Sundararajan et al. [23], and Wang et al. [24]. The wear rate is observed to increase with increase in applied load which is in agreement with what was observed by Qureshi and Sheikh [25]. Glaeser [26] opinioned that the wear rate is proportional to load and sliding distance during wear testing which fully supports the test results. Identical to the findings of the wear tests in the present study, enhancement of wear resistance of steel substrates is also observed after the deposition of coatings by Kulu and Phil [27]. The improvement of wear resistance after the deposition of coatings is also supported by the findings of Sahraoui et al. [21].


## 4.1. Microstructure of the Coatings

The WC-12% Co coating has small size splats whereas the splats are coarse for Cr3C2-25% NiCr. From the SEM images as shown in Figures 3(a)(B), 3(a)(C), 3(a)(D), 3(b)(B), 3(b)(C), and 3(b)(D) it is clear that, at higher applied load, there is more extensive loss of material. There is no subsurface cracking in the case of the coated specimens. WC-12% Co coated samples were found to be more wear resistant at three different applied loads of 40 N, 50 N, and 60 N than Cr3C2-25% NiCr. In the present investigation, superior wear resistance of WC-12% Co coating is found which may be due to the presence of W on its surface. Similar results and microstructure are obtained by Chivavibul et al. [17] for WC-Co coatings. The microstructure obtained for Cr3C2-25% NiCr coatings are similar to the findings of Kamal et al. [18].


## 4.2. X-Ray Diffraction (XRD) Analysis

The number of peaks corresponding to different phases of WC-12% Co and Cr3C2-25% NiCr coatings on ASTM A36 material can be seen from diffraction patterns as shown in Figures 4(a) and 4(b), respectively. Theses identified phases for WC-Co coatings are in agreement with those observed by Suresh Babu et al. [19]. XRD phases identified for Cr3C2-25% NiCr coatings are in agreement with the findings of Mohanty et al. [20].


## 4.3. Evaluation of Microhardness

The higher microhardness values of WC-12% Co and Cr3C2-25% NiCr cermet coatings may be one of the reasons of high wear resistance of these coatings, which is in agreement with those observed by Sahraoui et al. [21].


## 4.4. Measurement of Porosity

The lower porosity of WC-12% Co and Cr3C2-25% NiCr cermet coatings may be one of the reasons of high wear resistance of these coatings, which is also supported by the findings of Sahraoui et al. [21].


## 4.5. Surface Roughness (Ra) Values

Coatings are differentiated on the basis of their properties like porosity, microhardness, microstructure, surface roughness and residual stresses. The surface of the coating is rough due to the due to the presence of fully melted and partially melted particles.


## 4.6. Wear Behavior

From the plots showing the variation of the C.W.R. with the sliding distance for bare and WC-12% Co, Cr3C2-25% NiCr coated ASTM A36 steel at a normal applied load of 40 N, 50 N, and 60 N, it is evident that the WC-12% Co and Cr3C2-25% NiCr cermet coated samples have shown lower C.W.R than uncoated ASTM A36 steel samples at all these three different applied loads.From the bar charts showing C.W.R. for uncoated and D-Gun sprayed coated ASTM A36 steel at normal applied load of 40 N, 50 N, and 60 N at a constant sliding velocity of 2 ms−1, after a sliding distance of 10,800 m, it is clear that the bare ASTM steel specimen has shown much higher C.W.R as compared to cermet coated specimens at all these three different applied loads. D-Gun sprayed WC-12% Co coating has shown considerable wear resistance as compared to the Cr3C2-25% NiCr coated specimens and bare ASTM A36 steel at all these three different applied loads. Also, it is found that the C.W.R for WC-12% Co and Cr3C2-25% NiCr cermet coated samples and bare ASTM A36 steel samples increases with an increase in the applied normal load.D-Gun sprayed coatings are more wear resistant than bare or uncoated material which is in agreement with what was observed by Murthy et al. [22], Sundararajan et al. [23], and Wang et al. [24]. The wear rate is observed to increase with increase in applied load which is in agreement with what was observed by Qureshi and Sheikh [25]. Glaeser [26] opinioned that the wear rate is proportional to load and sliding distance during wear testing which fully supports the test results. Identical to the findings of the wear tests in the present study, enhancement of wear resistance of steel substrates is also observed after the deposition of coatings by Kulu and Phil [27]. The improvement of wear resistance after the deposition of coatings is also supported by the findings of Sahraoui et al. [21].


## 5. Conclusions

In the present investigation, the main conclusions on the basis of the results obtained are as follows:(1)
WC-12% Co and Cr3C2-25% NiCr cermet coatings have successfully been deposited on ASTM A36 steel substrate.(2)
WC-12% Co and Cr3C2-25% NiCr cermet coated samples have shown lower C.W.R than uncoated ASTM A36 steel samples.(3)
Enhancement in sliding wear resistance of ASTM A36 steel is observed after the deposition of WC-12% Co and Cr3C2-25% NiCr cermet coatings.(4)
C.W.R for cermet coated specimens and uncoated specimens increases with an increase in the applied normal load.(5)
Minimum C.W.R is observed for WC-12% Co coated specimens. WC-12% Co is found to be the best coating to be deposited on an ASTM A36 steel substrate in the present study.(6)
Sliding wear resistance of WC-12% Co coating is found to be better than Cr3C2-25% NiCr coating.(7)
Sliding wear resistance for all the investigated cases followed the trend as given below:the trend is WC-12% Co coated ASTM A36 steel > Cr3C2-25% NiCr coated ASTM A36 steel > Bare ASTM A36 steel,therefore, out of these combinations WC-12% Co–ASTM A36 coating-substrate combination is found to be the best combination.



---