# Uniform Dispersion of Multiwalled Carbon Nanotubes in Copper Matrix Nanocomposites Using Metal Injection Molding Technique

Authors: Ali Samer Muhsan; Faiz Ahmad; Norani M. Mohamed; Puteri Sri Melor Megat Yusoff; Muhammad Rafi Raza
Journal: International Journal of Manufacturing Engineering
 (2013)

---

## Abstract

This work presents a novel fabrication approach of multiwalled carbon nanotubes (MWNTs) reinforced copper (Cu) matrix nanocomposites. A combination of nanoscale dispersion of functionalized MWNTs in low viscose media of dissolved paraffin wax under sonication treatment followed by metal injection molding (MIM) technique was adopted. MWNTs contents were varied from 0 to 10 vol.%. Information about the degree of purification and functionalization processes, evidences on the existence of the functional groups, effect of sonication time on the treated MWNTs, and microstructural analysis of the fabricated Cu/MWNTs nanocomposites were determined using TEM, EDX, FESEM, and Raman spectroscopy analysis. The results showed that the impurities of the pristine MWNTs such as Fe, Ni catalyst, and the amorphous carbon have been significantly removed after purification process. Meanwhile, FESEM and TEM observations showed high stability of MWNTs at elevated temperatures and uniform dispersion of MWNTs in Cu matrix at different volume fractions and sintering temperatures (950, 1000 & 1050°C). The experimentally measured thermal conductivities of Cu/MWNTs nanocomposites showed remarkable increase (11.25% higher than sintered pure Cu) with addition of 1 vol.% MWNTs, and slight decrease below the value of sintered Cu at 5 and 10 vol.% MWNTs.


---

## Body

## 1. Introduction

With continued demand for high-performance electronic devices with low cost, small size and more efficient electronic systems, thermal challenges became a serious concern in electronic packaging design [1]. More transistors means more heat is generated within these systems. High-operating temperature decreases the overall reliability or even permanently damages the entire electronic system [2]. Therefore, a new thermal management solution is required to provide cost-effective means of dissipating heat from next generation microelectronic devices [3]. In response to these critical needs, high-performance heat sink nanocomposite made of copper reinforced by multiwalled carbon nanotubes is proposed.The superior physical, mechanical, and thermal properties of MWNTs have led it to have very high impact on developing new generations of nanocomposite materials with enhanced functionality and wide range of applications [4]. However, incorporation of MWNTs in metal matrix has its own barriers and difficulties that might destroy the desired properties of MWNTs [5].Meanwhile, dispersion of MWNTs in metal matrix nanocomposites is known as the most difficult challenge in fabricating MWNTs based metal matrix nanocomposite. This can be attributed to the following factors: (1) the incompatibility in phases between metal matrix and MWNTs; (2) the large difference in density; (3) bundling and tangling phenomenon of MWNTs that occurs due to the high surface area of MWNTs associated with van der Waal forces between individual MWNTs. Experimentally, most of the previous works showed decrease in the physical properties of MWNTs based nanocomposites mostly due to the MWNTs clustering phenomenon [6–9].Therefore, several techniques have been suggested to improve the dispersion of MWNTs. Unfortunately, most of these techniques were limited to polymer nanocomposites, while only few researchers have focused on improving MWNTs dispersion in metal matrix nanocomposite. Even so, their results did not meet their expectations. For example, Chu et al. [7] studied the effect of incorporating different amounts of MWNTs in Cu matrix using ball milling mixing technique on thermal conductivity. They found that there was no enhancement in the thermal conductivity and they proposed that this behaviour was probably due to the random orientation of MWNTs, the existence of interfacial thermal resistance between MWNTs and copper particles associated with low phase contrast ratio of MWNTs to copper, as well as the poor dispersion of MWNTs in the copper matrix. Similar results were reported by Kim et al. [9] after reinforcing Cu with nickel-coated single-walled carbon nanotubes (SWNTs). They suggested that the existence of grain boundaries and defects in the polycrystals of the composite, resulting in lower thermal conductivity compared to the matrix. Cho et al. [10] used a combination of wet mixing process accelerated by hetroaggregation method using acid-treated MWNTs followed by Spark Plasma Sintering technique. Their results, however, showed no enhancement in thermal conductivity with MWNTs contents higher than 1 vol.%. On the other hand, some researchers have carried out functionalization process on MWNTs to enhance the dispersion of the purified MWNTs and create sidewalls groups such as COOH that have the potential to bind MWNTs to the metal matrix [11–15]. For example, Kim et al. [11] reported the observation of enhanced mechanical properties of MWNT/Cu nanocomposites using a molecular mixing technique. They also observed oxygen atoms at the interface between MWNTs and Cu matrix and proposed that these oxygen molecules had a positive effect on the interfacial strength.Therefore, this study aims to develop a new dispersing technique of multiwalled carbon nanotubes reinforced copper matrix nanocomposites that ensures a homogeneous dispersion of MWNTs in Cu matrix. This technique is basically a multilevel mixing approach of nanoscale dispersion of the functionalized MWNTs in Cu/MWNTs feedstock followed by MIM process.


## 2. Experimental Methods

### 2.1.  Materials

Commercial Cu powder particles with diameter ranging of 15–20μm were purchased from Sandvik Osprey LTD, UK. Multiwalled carbon nanotubes with diameter of 60–80 nm and 5–15 μm in length were purchased from Shenzhen Nano-Technologies Port Co., Ltd., China. The purity of MWNTs was 95–98% with ash content of ≤ 0.2 wt.%.


### 2.2. Nanoscale Dispersion Process

In this method, MWNTs were first purified and functionalized using concentrated acids with the assist of heating and sonication process. MWNTs were immersed in an acid solution of H2SO4 (98%) and HNO3 (67%) in a ratio of 3 : 1 for different sonication times (0.5, 2.75 and 5 h) under temperature of 70°C. Functionalization has been applied to enhance the dispersion of purified MWNTs and create sidewalls groups that have the potential to bind MWNTs to the Cu matrix.After MWNTs being purified and functionalized in concentrated acids under sonication treatment, MWNTs were washed by distilled water and dried at 120°C for 24 h. MWNTs were mixed again with low viscous liquid media of dissolved paraffin wax (PW) diluted in heptane solvent along with magnetic stirring. This was followed by sonication agitation process to ensure uniform dispersion of MWNTs in PW solution. The dried MWNTs/PW mixture was then mixed with the other components of the binder system (Polyethylene, PE; Stearic Acid, SA) in Z-blade mixer at 160°C. This step provided a high-viscous liquid media with high shear forces that allowed MWNTs to be mixed properly by dispersing the MWNTs clusters with uniform dispersion into the molten binder system. The copper powder was added gradually during the mixing process to form Cu-MWNTs-Binder feedstock as illustrated in Figure1.Figure 1
Nanoscale dispersion process of MWNTs in Paraffin Wax (PW).


### 2.3. Metal Injection Molding Process

Metal injection molding (MIM) technique involves four main stages: feedstock preparation; injection molding of the prepared feedstock; binder removal or debinding process (solvent and thermal debinding) to get a shaped porous metallic part; sintering process in which the debinded samples are condensed to form pure or composite metallic products [6]. In this technique, the prepared feedstock in the previous stage was granulated to small pieces to be plasticized in a heated barrel of injection molding machine, and, then, a controlled volume of the molten feedstock is injected from the plasticator under pressure into a closed mould, with solidification beginning on the mould’s cavity wall to get the desired shape. The injection moulded samples are called green samples. To completely remove the binder from the green samples, two consecutive processes of solvent and thermal debinding were applied. After the binder is being totally removed, sintering process under Argon atmosphere with different sintering temperature of 950, 1000 and 1050°C was carried out as shown in Figure 2.Figure 2
Metal injection process of MWNTs/Cu nanocomposites.


## 2.1.  Materials

Commercial Cu powder particles with diameter ranging of 15–20μm were purchased from Sandvik Osprey LTD, UK. Multiwalled carbon nanotubes with diameter of 60–80 nm and 5–15 μm in length were purchased from Shenzhen Nano-Technologies Port Co., Ltd., China. The purity of MWNTs was 95–98% with ash content of ≤ 0.2 wt.%.


## 2.2. Nanoscale Dispersion Process

In this method, MWNTs were first purified and functionalized using concentrated acids with the assist of heating and sonication process. MWNTs were immersed in an acid solution of H2SO4 (98%) and HNO3 (67%) in a ratio of 3 : 1 for different sonication times (0.5, 2.75 and 5 h) under temperature of 70°C. Functionalization has been applied to enhance the dispersion of purified MWNTs and create sidewalls groups that have the potential to bind MWNTs to the Cu matrix.After MWNTs being purified and functionalized in concentrated acids under sonication treatment, MWNTs were washed by distilled water and dried at 120°C for 24 h. MWNTs were mixed again with low viscous liquid media of dissolved paraffin wax (PW) diluted in heptane solvent along with magnetic stirring. This was followed by sonication agitation process to ensure uniform dispersion of MWNTs in PW solution. The dried MWNTs/PW mixture was then mixed with the other components of the binder system (Polyethylene, PE; Stearic Acid, SA) in Z-blade mixer at 160°C. This step provided a high-viscous liquid media with high shear forces that allowed MWNTs to be mixed properly by dispersing the MWNTs clusters with uniform dispersion into the molten binder system. The copper powder was added gradually during the mixing process to form Cu-MWNTs-Binder feedstock as illustrated in Figure1.Figure 1
Nanoscale dispersion process of MWNTs in Paraffin Wax (PW).


## 2.3. Metal Injection Molding Process

Metal injection molding (MIM) technique involves four main stages: feedstock preparation; injection molding of the prepared feedstock; binder removal or debinding process (solvent and thermal debinding) to get a shaped porous metallic part; sintering process in which the debinded samples are condensed to form pure or composite metallic products [6]. In this technique, the prepared feedstock in the previous stage was granulated to small pieces to be plasticized in a heated barrel of injection molding machine, and, then, a controlled volume of the molten feedstock is injected from the plasticator under pressure into a closed mould, with solidification beginning on the mould’s cavity wall to get the desired shape. The injection moulded samples are called green samples. To completely remove the binder from the green samples, two consecutive processes of solvent and thermal debinding were applied. After the binder is being totally removed, sintering process under Argon atmosphere with different sintering temperature of 950, 1000 and 1050°C was carried out as shown in Figure 2.Figure 2
Metal injection process of MWNTs/Cu nanocomposites.


## 3. Results and Discussion

### 3.1. TEM and EDX Analysis

Figure3 shows the transmission electron micrograph (TEM) of MWNTs before (a) and after (b) purification process. It can be seen that the impurities of the pristine MWNTs, such as Fe, Ni catalyst, and the amorphous carbon have been successfully removed after the purification and sonication process. These results were further proved by Energy dispersive X-ray spectroscopy (EDX) and Raman microscope inspection. EDX results (Table 1) show that Fe catalyst was completely eliminated and Ni was reduced significantly after acid treatment. However, longer time of sonication treatment may result in aggressive oxidation of the MWNT surface that can degrade the MWNTs. Therefore, in order to test the effect of sonication process on the MWNTs structure, different sonication hours of 0.5, 2.75, and 5 were applied. The results revealed that the sonication time of 2.75 h was recorded as the optimal parameter.Table 1
EDX results of acid treated MWNTs under different Sonication Hours.
Element
Weight%
Atomic%
0.5 h Sonication treatment
C
94.22
96.52
O
4.04
3.11
Fe
0.45
0.10
Ni
1.29
0.27
2.75 h Sonication treatment
C
90.56
93.40
O
7.95
6.16
Fe
—
—
S
0.73
0.28
Ni
0.76
0.16
5 h Sonication treatment
C
88.93
91.82
O
10.25
7.95
Fe
—
—
S
0.32
0.12
Ni
0.50
0.10TEM images of (a) Pristine MWNTs and (b) Purified MWNTs with sonication treatment for 2.75 h.
(a)
(b)


### 3.2. Raman Spectroscopy and SEM Characterization Tests of Functionalized MWNTs

Raman spectroscopy revealed necessary information on the evolution of MWNTs after chemical or physical treatment [16]. Figure 4 illustrates the Raman spectra of pristine MWNTs (Raw MWNTs), acid treated MWNTs with sonication time of 0.5, 2.75 and 5 h. The D/G ratio represents the defect density in graphitic structures. As clearly shown in Figure 4, there were two peaks at ~1330 cm−1 (D band) and the other at ~1570 cm−1 (G band). By the comparison of the ID/IG ratios of these spectra, it could be seen that this ratio was varied as sonication time increased. The pristine MWNTs had the lowest ID/IG ratios of 0.838. The ID/IG ratios gradually increased to 0.848, 0.855, and 0.861 of the MWNTs treated under sonication process of 0.5, 2.75, and 5 hours, respectively. The amount of defects apparently increased in MWNTs after functionalization process, especially the one after 5 hours of sonication treatment. These results were further confirmed by FESEM characterization, as shown in Figure 5. This Figure includes four FESEM images which corresponding to (a) the pristine MWNTs, (b) acid treated MWNTs (functionalized MWNTs) with sonication process of 0.5, (c) 2.75, and (d) 5 hours. Although EDX inspection test showed higher impurities removal at 5 h sonication treatment (Table 1), Figure 5(d) revealed that clear damages were occurred on the MWNTs structure after 5 hours of sonication treatment. Therefore, based on these results, the sonication treatment time chosen was 2.75 hours.Figure 4
Raman spectra of raw MWNTs and functionalized MWNTs using a mixture of H2SO4 : NHO3 (3 : 1) under different sonication’s dwell time.FESEM images of raw and functionalized MWNTs. (a) pristine MWNTs, (b) sonication treatment for 0.5 hour, (c) treated for 2.75 hours and (d) treated for 5 hours.
(a)
(b)
(c)
(d)


### 3.3. Microstructural Analysis of Cu/MWNTs Nanocomposites

Figure6 shows the FESEM images of Cu/MWNTs nanocomposites demonstrating the quality of MWNTs dispersion in Cu matrix at different fabrication stages. Figures 6(a) and 6(b) illustrate the FESEM of Cu/MWNTs green (before debinding process) and sintered parts, respectively. These parts were fabricated without utilizing the newly developed technique, and they are presented here for comparison purposes. It clearly showed that MWNTs were agglomerated between the Cu particles and formed porosities rather than enhancing the interfacial bonding. Figures 6(c) and 6(d) represent the green and brown (thermal debinded) Cu/MWNTs parts after applying the new dispersion technique. Figures 6(e), 6(f), and 6(g) show the fractured surfaces of the sintered Cu/MWNTs parts at different sintering temperature (950, 1000, and 1050°C, resp.). Figure 6(h) presents a TEM nanograph, which in turn illustrates the incorporation of the individual MWNT into the Cu particles. It revealed that the mechanical damages in MWNTs structure were very few. It also showed a good interfacial bonding at Cu/MWNTs interface.FESEM micrograph of sintered Cu-10 vol.% MWNTs nanocomposites. (a) and (b) are the FESEM of Cu/MWNTs green and sintered parts, respectively, before applying the new dispersion technique, (c) and (d) represent the green and brown samples of Cu/MWNTs sintered at 950 and 1000°C, respectively, both are after applying the new dispersion technique. Images (e), (f) and (g) show the fractured surfaces of the sintered Cu/MWNTs parts at 950, 1000 and 1050°C, respectively. (h) TEM nano-graph showing good bonding at the interface between functionalized MWNTs and Cu particles.
(a)
(b)
(c)
(d)
(e)
(f)
(g)
(h)In general, we can clearly note that MWNTs dispersion has been significantly improved after utilizing the new technique of nanoscale dispersion. This can be attributed first to the functionalization process that provides COOH groups on the outer surfaces of the MWNTs. In addition, sonication process generates energy in different forms on the MWNTs clusters, these energies are oscillating zones of high temperature with extremely rapid heating and cooling rates; alternating impulses of very high pressure; formation of microbubbles throughout the liquid medium of MWNTs that growth and collapse on the MWNTs surfaces. These energies are sufficient to push the individual MWNT apart and overcome the van der Waal forces between MWNTs, which is considered as the main reason of the MWNTs clustering phenomenon [16–18]. Meanwhile, MIM technique provided high-shear forces from the binder system components during feedstock preparation that disperse and exfoliate the MWNTs clusters into the Cu matrix homogeneously. This indicates that nanoscale dispersion method combined with MIM technique is a very effective method for achieving uniform distribution of MWNTs in metal matrix nanocomposites.


### 3.4. Relative Density

Figure7 shows the effect of sintering temperature on the relative density of MWNTs/Cu nanocomposites at different dwell time and MWNTs vol.%. At 1050°C sintering temperature and dwell time of 60 min, the measured relative densities were about 94.8%, 93.5%, 90.6%, and 89% for pure copper, 1, 5, and 10 vol.% MWNTs, respectively. In general, the relative densities of MWNTs/Cu nanocomposites were lower than the pure Cu matrix due to accumulation of MWNTs at the grain boundaries of the Cu matrix, which is the basis of the pores creation. These accumulations increased by increase the MWNTs volume fraction. Similar behaviour was observed at 90 min and 120 min dwell times. However, it can also be noted that there is an increasing in all relative densities results as the dwell time increased regardless at which sintering temperature were they fabricated.Figure 7
Relative densities of MWNTs/Cu nanocomposites.


### 3.5. Thermal Conductivity Measurement

Thermal conductivities of MWCNTs/Cu composites were measured using NETZSCH model LFA 447 NanoFlash  apparatus (LFA447, Netzsch, Germany). Figure8 demonstrates the thermal conductivities of MWNTs/Cu nanocomposites as a function of MWNTs volume fraction with two different measuring temperatures (25 and 125°C). The MWNTs/Cu thermal conductivities were measured in direction perpendicular to the injection molding axis and it showed varied values as MWNTs content increased. The highest value was recorded at Cu-1 vol.% MWNTs (366.516 W/mK) sintered at 1050°C for 120 minutes. This value corresponds to an increase of ~32 W/mK (11.25%) over that of the sintered copper (Cu matrix). It is worth mentioning that the sintered copper powder with polycystic structure has lower thermal conductivity (330 W/mK) than the monocrystal copper (401 W/mK), and this most probably is due to the existence of grain boundary and defects in polycrystals [19]. It can also be seen that thermal conductivities of sintered copper and Cu-1 vol.% MWNTs were slightly decreased by increasing the measuring temperature from 25 to 125°C due to the free electrons that dissipate their kinetic energy to atoms as a result of increased collision [20]. Reversely, at high MWNTs content (higher than 1 vol.% MWNTs), thermal conductivities showed an increase as the measuring temperature increased. Whereas, thermal conductivity of Cu-5 vol.% MWNTs was relatively increased from 239.1 to 271.7 W/mK by increasing the measuring temperature from 25 to 125°C, respectively. Similar conduct was noted at Cu/10 vol. MWNTs. This can be attributed to the consistency of high MWNTs thermal conductivity at elevated temperature. However, by increasing MWNTs content more than 1 vol.%, the measured thermal conductivities of the composites showed deviation compared to the estimated values which were obtained by the rule of mixture (RM), and became even lower than that of the sintered copper. Some researchers have reported similar behavior showing that thermal conductivity of Cu/CNTs nanocomposite increased with low CNTs content and then decreased as CNTs content increased [21–24]. For instance, Chu and coworkers [22] have fabricated Cu/CNTs nanocomposites using a novel particles compositing method followed by spark plasma sintering. They reported that the addition of CNTs showed no enhancement in the overall thermal conductivity of the fabricated nanocomposites. They suggested that the presence of an interfacial thermal resistance is believed to be the main reason of why the measured thermal conductivities are being degraded (322 W/mK). They also attributed these unexpected results to the following factors: low wettability between CNTs and Cu matrix, nonhomogeneity or bundling of CNTs, porosity and incomplete consolidation processing. Likewise, Kim et al. [23] have reported same underperformance thermal conductivity of Nick-coated SWCNTs/Cu (150 W/mK). Yamanaka et al. [24] proposed that the decrease in thermal conductivity is mostly due to the difficulty in dispersing clustered CNTs with an increase in CNTs content. Other similar results were published by Cho and coworker [25]. They used a combination of a wet mixing process accelerated by hetroaggregation method using acid-treated CNTs followed by SPS consolidation technique. They noted that the highest record thermal conductivity was at 1 vol.% CNTs (359.2 W/mK). Their results, however, showed no enhancement in thermal conductivity with CNTs contents higher than 1 vol.% CNTs. Therefore, our novel technique of using functionalized CNTs associate with ultrasonication process followed by MIM method perhaps is the ultimate technology in fabrication of CNTs/MM nanocomposites. This is due to its ability in combining two or more ingredient materials that are not compatible at molten state and difficult to be fabricated via conventional techniques. It also ensures a good dispersion of CNTs in metal matrices by providing high shear forces during mixing process (feedstock preparation).Figure 8
Thermal conductivities of MWNTs/Cu composites as a function of MWNTs volume fraction with two different measuring temperatures (25 and 125°C).


## 3.1. TEM and EDX Analysis

Figure3 shows the transmission electron micrograph (TEM) of MWNTs before (a) and after (b) purification process. It can be seen that the impurities of the pristine MWNTs, such as Fe, Ni catalyst, and the amorphous carbon have been successfully removed after the purification and sonication process. These results were further proved by Energy dispersive X-ray spectroscopy (EDX) and Raman microscope inspection. EDX results (Table 1) show that Fe catalyst was completely eliminated and Ni was reduced significantly after acid treatment. However, longer time of sonication treatment may result in aggressive oxidation of the MWNT surface that can degrade the MWNTs. Therefore, in order to test the effect of sonication process on the MWNTs structure, different sonication hours of 0.5, 2.75, and 5 were applied. The results revealed that the sonication time of 2.75 h was recorded as the optimal parameter.Table 1
EDX results of acid treated MWNTs under different Sonication Hours.
Element
Weight%
Atomic%
0.5 h Sonication treatment
C
94.22
96.52
O
4.04
3.11
Fe
0.45
0.10
Ni
1.29
0.27
2.75 h Sonication treatment
C
90.56
93.40
O
7.95
6.16
Fe
—
—
S
0.73
0.28
Ni
0.76
0.16
5 h Sonication treatment
C
88.93
91.82
O
10.25
7.95
Fe
—
—
S
0.32
0.12
Ni
0.50
0.10TEM images of (a) Pristine MWNTs and (b) Purified MWNTs with sonication treatment for 2.75 h.
(a)
(b)


## 3.2. Raman Spectroscopy and SEM Characterization Tests of Functionalized MWNTs

Raman spectroscopy revealed necessary information on the evolution of MWNTs after chemical or physical treatment [16]. Figure 4 illustrates the Raman spectra of pristine MWNTs (Raw MWNTs), acid treated MWNTs with sonication time of 0.5, 2.75 and 5 h. The D/G ratio represents the defect density in graphitic structures. As clearly shown in Figure 4, there were two peaks at ~1330 cm−1 (D band) and the other at ~1570 cm−1 (G band). By the comparison of the ID/IG ratios of these spectra, it could be seen that this ratio was varied as sonication time increased. The pristine MWNTs had the lowest ID/IG ratios of 0.838. The ID/IG ratios gradually increased to 0.848, 0.855, and 0.861 of the MWNTs treated under sonication process of 0.5, 2.75, and 5 hours, respectively. The amount of defects apparently increased in MWNTs after functionalization process, especially the one after 5 hours of sonication treatment. These results were further confirmed by FESEM characterization, as shown in Figure 5. This Figure includes four FESEM images which corresponding to (a) the pristine MWNTs, (b) acid treated MWNTs (functionalized MWNTs) with sonication process of 0.5, (c) 2.75, and (d) 5 hours. Although EDX inspection test showed higher impurities removal at 5 h sonication treatment (Table 1), Figure 5(d) revealed that clear damages were occurred on the MWNTs structure after 5 hours of sonication treatment. Therefore, based on these results, the sonication treatment time chosen was 2.75 hours.Figure 4
Raman spectra of raw MWNTs and functionalized MWNTs using a mixture of H2SO4 : NHO3 (3 : 1) under different sonication’s dwell time.FESEM images of raw and functionalized MWNTs. (a) pristine MWNTs, (b) sonication treatment for 0.5 hour, (c) treated for 2.75 hours and (d) treated for 5 hours.
(a)
(b)
(c)
(d)


## 3.3. Microstructural Analysis of Cu/MWNTs Nanocomposites

Figure6 shows the FESEM images of Cu/MWNTs nanocomposites demonstrating the quality of MWNTs dispersion in Cu matrix at different fabrication stages. Figures 6(a) and 6(b) illustrate the FESEM of Cu/MWNTs green (before debinding process) and sintered parts, respectively. These parts were fabricated without utilizing the newly developed technique, and they are presented here for comparison purposes. It clearly showed that MWNTs were agglomerated between the Cu particles and formed porosities rather than enhancing the interfacial bonding. Figures 6(c) and 6(d) represent the green and brown (thermal debinded) Cu/MWNTs parts after applying the new dispersion technique. Figures 6(e), 6(f), and 6(g) show the fractured surfaces of the sintered Cu/MWNTs parts at different sintering temperature (950, 1000, and 1050°C, resp.). Figure 6(h) presents a TEM nanograph, which in turn illustrates the incorporation of the individual MWNT into the Cu particles. It revealed that the mechanical damages in MWNTs structure were very few. It also showed a good interfacial bonding at Cu/MWNTs interface.FESEM micrograph of sintered Cu-10 vol.% MWNTs nanocomposites. (a) and (b) are the FESEM of Cu/MWNTs green and sintered parts, respectively, before applying the new dispersion technique, (c) and (d) represent the green and brown samples of Cu/MWNTs sintered at 950 and 1000°C, respectively, both are after applying the new dispersion technique. Images (e), (f) and (g) show the fractured surfaces of the sintered Cu/MWNTs parts at 950, 1000 and 1050°C, respectively. (h) TEM nano-graph showing good bonding at the interface between functionalized MWNTs and Cu particles.
(a)
(b)
(c)
(d)
(e)
(f)
(g)
(h)In general, we can clearly note that MWNTs dispersion has been significantly improved after utilizing the new technique of nanoscale dispersion. This can be attributed first to the functionalization process that provides COOH groups on the outer surfaces of the MWNTs. In addition, sonication process generates energy in different forms on the MWNTs clusters, these energies are oscillating zones of high temperature with extremely rapid heating and cooling rates; alternating impulses of very high pressure; formation of microbubbles throughout the liquid medium of MWNTs that growth and collapse on the MWNTs surfaces. These energies are sufficient to push the individual MWNT apart and overcome the van der Waal forces between MWNTs, which is considered as the main reason of the MWNTs clustering phenomenon [16–18]. Meanwhile, MIM technique provided high-shear forces from the binder system components during feedstock preparation that disperse and exfoliate the MWNTs clusters into the Cu matrix homogeneously. This indicates that nanoscale dispersion method combined with MIM technique is a very effective method for achieving uniform distribution of MWNTs in metal matrix nanocomposites.


## 3.4. Relative Density

Figure7 shows the effect of sintering temperature on the relative density of MWNTs/Cu nanocomposites at different dwell time and MWNTs vol.%. At 1050°C sintering temperature and dwell time of 60 min, the measured relative densities were about 94.8%, 93.5%, 90.6%, and 89% for pure copper, 1, 5, and 10 vol.% MWNTs, respectively. In general, the relative densities of MWNTs/Cu nanocomposites were lower than the pure Cu matrix due to accumulation of MWNTs at the grain boundaries of the Cu matrix, which is the basis of the pores creation. These accumulations increased by increase the MWNTs volume fraction. Similar behaviour was observed at 90 min and 120 min dwell times. However, it can also be noted that there is an increasing in all relative densities results as the dwell time increased regardless at which sintering temperature were they fabricated.Figure 7
Relative densities of MWNTs/Cu nanocomposites.


## 3.5. Thermal Conductivity Measurement

Thermal conductivities of MWCNTs/Cu composites were measured using NETZSCH model LFA 447 NanoFlash  apparatus (LFA447, Netzsch, Germany). Figure8 demonstrates the thermal conductivities of MWNTs/Cu nanocomposites as a function of MWNTs volume fraction with two different measuring temperatures (25 and 125°C). The MWNTs/Cu thermal conductivities were measured in direction perpendicular to the injection molding axis and it showed varied values as MWNTs content increased. The highest value was recorded at Cu-1 vol.% MWNTs (366.516 W/mK) sintered at 1050°C for 120 minutes. This value corresponds to an increase of ~32 W/mK (11.25%) over that of the sintered copper (Cu matrix). It is worth mentioning that the sintered copper powder with polycystic structure has lower thermal conductivity (330 W/mK) than the monocrystal copper (401 W/mK), and this most probably is due to the existence of grain boundary and defects in polycrystals [19]. It can also be seen that thermal conductivities of sintered copper and Cu-1 vol.% MWNTs were slightly decreased by increasing the measuring temperature from 25 to 125°C due to the free electrons that dissipate their kinetic energy to atoms as a result of increased collision [20]. Reversely, at high MWNTs content (higher than 1 vol.% MWNTs), thermal conductivities showed an increase as the measuring temperature increased. Whereas, thermal conductivity of Cu-5 vol.% MWNTs was relatively increased from 239.1 to 271.7 W/mK by increasing the measuring temperature from 25 to 125°C, respectively. Similar conduct was noted at Cu/10 vol. MWNTs. This can be attributed to the consistency of high MWNTs thermal conductivity at elevated temperature. However, by increasing MWNTs content more than 1 vol.%, the measured thermal conductivities of the composites showed deviation compared to the estimated values which were obtained by the rule of mixture (RM), and became even lower than that of the sintered copper. Some researchers have reported similar behavior showing that thermal conductivity of Cu/CNTs nanocomposite increased with low CNTs content and then decreased as CNTs content increased [21–24]. For instance, Chu and coworkers [22] have fabricated Cu/CNTs nanocomposites using a novel particles compositing method followed by spark plasma sintering. They reported that the addition of CNTs showed no enhancement in the overall thermal conductivity of the fabricated nanocomposites. They suggested that the presence of an interfacial thermal resistance is believed to be the main reason of why the measured thermal conductivities are being degraded (322 W/mK). They also attributed these unexpected results to the following factors: low wettability between CNTs and Cu matrix, nonhomogeneity or bundling of CNTs, porosity and incomplete consolidation processing. Likewise, Kim et al. [23] have reported same underperformance thermal conductivity of Nick-coated SWCNTs/Cu (150 W/mK). Yamanaka et al. [24] proposed that the decrease in thermal conductivity is mostly due to the difficulty in dispersing clustered CNTs with an increase in CNTs content. Other similar results were published by Cho and coworker [25]. They used a combination of a wet mixing process accelerated by hetroaggregation method using acid-treated CNTs followed by SPS consolidation technique. They noted that the highest record thermal conductivity was at 1 vol.% CNTs (359.2 W/mK). Their results, however, showed no enhancement in thermal conductivity with CNTs contents higher than 1 vol.% CNTs. Therefore, our novel technique of using functionalized CNTs associate with ultrasonication process followed by MIM method perhaps is the ultimate technology in fabrication of CNTs/MM nanocomposites. This is due to its ability in combining two or more ingredient materials that are not compatible at molten state and difficult to be fabricated via conventional techniques. It also ensures a good dispersion of CNTs in metal matrices by providing high shear forces during mixing process (feedstock preparation).Figure 8
Thermal conductivities of MWNTs/Cu composites as a function of MWNTs volume fraction with two different measuring temperatures (25 and 125°C).


## 4. Conclusions

For the first time, uniform dispersion of multiwalled carbon nanotube reinforced copper matrix nanocomposites was successfully achieved. The newly developed approach of nanoscale dispersion followed by MIM fabrication technique was proved to be effective in exfoliating the MWNTs clusters and homogeneously distribute the individual MWNT in Cu matrix. Nanoscale dispersion process provided a functional group on the top surface of MWNTs, which significantly enhanced the solubility of MWNTs in the liquid media of dissolved paraffin wax. These results were verified using EDX, TEM, FESEM, and Raman spectroscope analysis method. EDX and Raman Spectroscope provided sufficient information on the quality of the purification and functionalization process. In addition, it explained the effects of sonication treatment on the MWNTs structure. TEM and FESEM images showed high stability of MWNTs in Cu matrix at high sintering temperature. It also demonstrated a good adherence between dispersed MWNTs and Cu particles. The measured thermal conductivities showed remarkable increase of 11% with addition of 1 vol.% MWNTs, and slight decrease at 5 and 10 vol.% MWNTs compared to the value of pure sintered Cu. Therefore, MIM is considered to be the most promising technique for forming and fabricating high performance heat sink nanocomposites with high precision in shape, high volume production and cost much lower than the traditional methods.



---

*Source: 386141-2013-10-02.xml*