# Seismic Behaviour of Exterior Reinforced Concrete Beam-Column Joints in High Performance Concrete Using Metakaolin and Partial Replacement with Quarry Dust

Authors: G. R. Vijay shankar; D. Suji
Journal: ISRN Materials Science
 (2014)

---

## Abstract

Recent earthquakes have demonstrated that most of the reinforced concrete structures were severely damaged; the beam-column joints, being the lateral and vertical load resisting members in reinforced concrete structures, are particularly vulnerable to failures during earthquakes. The existing reinforced concrete beam-column joints are not designed as per code IS13920:1993. Investigation of high performance concrete (HPC) joints with conventional concrete (CC) joints (exterior beam-column) was performed by comparing various reinforcement detailing schemes. Ten specimens were considered in this investigation and the results were compared: four specimens with CC (with and without seismic detailing), four specimens with HPC (with and without seismic detailing), and two specimens with HPC at confinement joint. The test was conducted for lateral load displacement, hysteresis loop, load ratio, percent of initial  stiffness versus displacement curve, total energy dissipation, strain in beam main bars, and crack pattern. The results reveal that HPC with seismic detailing will be better compared with other reinforcements details under cyclic loading and reverse cyclic loading.


---

## Body

## 1. Introduction

Earthquakes present a threat to public safety and welfare in a significant portion everywhere. We cannot stop earthquakes, but we can protect ourselves from them, as “earthquakes do not kill human beings, but the structures do.” The behaviour of reinforced concrete moment resisting frame structures in recent earthquakes all over the world has highlighted the consequences of poor performance of beam-column joints. Beam-column joints in a reinforced concrete moment resisting frame are crucial zones for transfer of loads effectively between the connecting elements (i.e., beams and columns) in the structure. In the analysis of reinforced concrete moment resisting frames, the joints are generally assumed as rigid. In Indian practice, the joint is usually neglected for specific design with attention being restricted to provision of sufficient anchorage for beam longitudinal reinforcement. This may be acceptable when the frame is not subjected to earthquake loads. The poor design practice of beam-column joints is compounded by the high demand imposed by the adjoining flexural members (beams and columns) in the event of mobilizing their inelastic capacities to dissipate seismic energy.For the past three decades, extensive research has been carried out on studying the behaviour of joints under seismic conditions through experimental and analytical studies. Various international codes of practices have been undergoing periodic revisions to incorporate the research findings into practice. This thesis aims to add to that body of knowledge through experimental investigation on the behaviour of beam-column joint under seismic loading.


## 2. Experimental Investigation

### 2.1. Details of Test Specimen

The test specimen was reduced to one-fourth scale to suit the loading arrangement and test facilities. Four numbers of 8  unloaded and beamwas meter bars were used for main bars in column and 3 numbers of 8 mm Diameter were used for top reinforcement and 2 numbers of 8 mm Diameter were used for bottom reinforcement in beams. The dimensions of beam were 110 mm × 90 mm and those of column were 90 × 90 mm. All specimens were cut at midheight of supporting column and at midspan of beams, which were the assumed points of inflection. Figure1 shows a sketch of test specimens with overall dimensions. And Figure 2 shows the various reinforcement detailing schemes.Figure 1
Overall dimensions of test specimens.Figure 2
Various schemes of reinforcement detailing.


### 2.2. Materials

(i)
Cement. Ordinary Portland cement of grade 53 conforming to IS specifications was used to cast the test specimen.
(ii)
Water. Potable water available in the campus was used for mixing and curing of concrete.
(iii)
Fine Aggregate. Fine aggregate used for all the specimens was river sand. The fine aggregate used for casting was sieved through IS 4.75 mm sieve.
(iv)
Coarse Aggregate. To suit the needs of scale of test specimen, small size of coarse aggregate was used. The coarse aggregate used was passed through IS 10 mm sieve.
(v)
Metakaolin. Metakaolin (MK) is produced by heat-treating kaolin, one of the most abundant natural minerals.
(vi)
Quarry Dust. Quarries and aggregate crushers are basic requisites for construction industry and quarry dust is a by-product of rubble crusher units.
(vii)
Super Plasticizer. For processing HPC, the most important chemical admixture is the super plasticizer, which is the high-range water-reducing admixture.


### 2.3. Compressive Strength of Concrete

See Table2.


### 2.4. Steel

The main reinforcement used for the specimen was tor steel of diameter of 8 mm. The shear reinforcement was mild steel of diameter of 3.3 mm. Specimens of 300 mm length were cut out and tested in computerized UTM to obtain the tensile strength. The test results of the specimen are shown in Table3.


## 2.1. Details of Test Specimen

The test specimen was reduced to one-fourth scale to suit the loading arrangement and test facilities. Four numbers of 8  unloaded and beamwas meter bars were used for main bars in column and 3 numbers of 8 mm Diameter were used for top reinforcement and 2 numbers of 8 mm Diameter were used for bottom reinforcement in beams. The dimensions of beam were 110 mm × 90 mm and those of column were 90 × 90 mm. All specimens were cut at midheight of supporting column and at midspan of beams, which were the assumed points of inflection. Figure1 shows a sketch of test specimens with overall dimensions. And Figure 2 shows the various reinforcement detailing schemes.Figure 1
Overall dimensions of test specimens.Figure 2
Various schemes of reinforcement detailing.


## 2.2. Materials

(i)
Cement. Ordinary Portland cement of grade 53 conforming to IS specifications was used to cast the test specimen.
(ii)
Water. Potable water available in the campus was used for mixing and curing of concrete.
(iii)
Fine Aggregate. Fine aggregate used for all the specimens was river sand. The fine aggregate used for casting was sieved through IS 4.75 mm sieve.
(iv)
Coarse Aggregate. To suit the needs of scale of test specimen, small size of coarse aggregate was used. The coarse aggregate used was passed through IS 10 mm sieve.
(v)
Metakaolin. Metakaolin (MK) is produced by heat-treating kaolin, one of the most abundant natural minerals.
(vi)
Quarry Dust. Quarries and aggregate crushers are basic requisites for construction industry and quarry dust is a by-product of rubble crusher units.
(vii)
Super Plasticizer. For processing HPC, the most important chemical admixture is the super plasticizer, which is the high-range water-reducing admixture.


## 2.3. Compressive Strength of Concrete

See Table2.


## 2.4. Steel

The main reinforcement used for the specimen was tor steel of diameter of 8 mm. The shear reinforcement was mild steel of diameter of 3.3 mm. Specimens of 300 mm length were cut out and tested in computerized UTM to obtain the tensile strength. The test results of the specimen are shown in Table3.


## 3. Description of the Form Work

To cast the specimen, four wooden moulds were fabricated. The size of the beam was 500 mm × 90 mm × 110 mm and the column size was 800 mm × 90 mm × 90 mm, shown in Figure3. The moulds were nailed to a base plate, in order to keep the alignment accurately.Figure 3
Form work of the test specimens.


### 3.1. Reinforcement Details

#### 3.1.1. Reinforcement Cage of Ordinary Joint

The reinforcement details and reinforcement cage of the ordinary joint are shown in Figure4. The main reinforcement provided in the beam was 8 mm diameter bars, 3 numbers at top and 2 numbers at bottom. The stirrups are 3.3 mm diameter bars at 20 mm c/c for a distance of 2d, that is, 220 mm from the face of the column, and at 40 mm c/c for remaining length of the beam.Figure 4
Reinforcement cage of ordinary joint.


#### 3.1.2. Reinforcement Cage of Seismic Detail Joint

The reinforcement details and reinforcement cage of the test specimen are shown in Figure5. The main reinforcement provided in the beam was 8 mm diameter bars, 3 numbers at top and 2 numbers. at bottom. The stirrups are 3.3 mm diameter bars at 40 mm c/c spacing.Figure 5
Reinforcement cage of seismic detailed joint.


## 3.1. Reinforcement Details

### 3.1.1. Reinforcement Cage of Ordinary Joint

The reinforcement details and reinforcement cage of the ordinary joint are shown in Figure4. The main reinforcement provided in the beam was 8 mm diameter bars, 3 numbers at top and 2 numbers at bottom. The stirrups are 3.3 mm diameter bars at 20 mm c/c for a distance of 2d, that is, 220 mm from the face of the column, and at 40 mm c/c for remaining length of the beam.Figure 4
Reinforcement cage of ordinary joint.


### 3.1.2. Reinforcement Cage of Seismic Detail Joint

The reinforcement details and reinforcement cage of the test specimen are shown in Figure5. The main reinforcement provided in the beam was 8 mm diameter bars, 3 numbers at top and 2 numbers. at bottom. The stirrups are 3.3 mm diameter bars at 40 mm c/c spacing.Figure 5
Reinforcement cage of seismic detailed joint.


## 3.1.1. Reinforcement Cage of Ordinary Joint

The reinforcement details and reinforcement cage of the ordinary joint are shown in Figure4. The main reinforcement provided in the beam was 8 mm diameter bars, 3 numbers at top and 2 numbers at bottom. The stirrups are 3.3 mm diameter bars at 20 mm c/c for a distance of 2d, that is, 220 mm from the face of the column, and at 40 mm c/c for remaining length of the beam.Figure 4
Reinforcement cage of ordinary joint.


## 3.1.2. Reinforcement Cage of Seismic Detail Joint

The reinforcement details and reinforcement cage of the test specimen are shown in Figure5. The main reinforcement provided in the beam was 8 mm diameter bars, 3 numbers at top and 2 numbers. at bottom. The stirrups are 3.3 mm diameter bars at 40 mm c/c spacing.Figure 5
Reinforcement cage of seismic detailed joint.


## 4. Casting and Curing

The moulds are arranged properly and placed over a smooth surface. The sides of the mould exposed to concrete were oiled well to prevent the side walls of the mould from absorbing water from concrete and to facilitate easy removal of the specimen. The reinforcement cages were placed in the moulds and cover between cage and form provided was 10 mm. Cement mortar block pieces were used as cover blocks. The concrete contents such as cement, sand, aggregate, metakaolin, quarry dust, super plasticizer, and water were weighed accurately and mixed. The mixing was done till uniform mix was obtained. The concrete was placed into the mould immediately after mixing and was well compacted. It is shown in Figures6 and 7. The test specimens were demoulded at the end of 24 hours of casting (Table 1). They were marked identifications. They were cured in water for 28 days. After 28 days of curing the specimen was dried in air and whitewashed.Table 1
Details of test specimens.
Sl. number
Specimens ID
Description of test specimens
% of metakaolin and quarry dust
1
O1 & O2
Conventional concrete(without seismic detailing)
—
2
SS1 & SS2
Conventional concrete(with seismic detailing)
—
3
E11 & E12
High performance concrete(without seismic detailing)
Normal concrete + 10% metakaolin + 30% quarry dust
4
E21 & E22
High performance concrete(with seismic detailing)
Normal concrete + 10% metakaolin + 30% quarry dust
5
E31 & E32
High performance concrete(with seismic detailing) (confinement joint)
Normal concrete + 10% metakaolin + 30% quarry dustTable 2
Cube compressive strength details.
Type
Compressive strength of cube (N/mm2)
Conventional  concrete M40
45.67
High performance concrete (M40) with 10% metakaolin + 30% quarry dust mix
51.34Table 3
Properties of reinforcements.
Sl. number
Description
Yield load (kN)
Ultimate load (kN)
Ultimate stress (N/mm2)
Yield stress (N/mm2)
1
8 mm bar
21
26.9
353.09
417.73
2
3.3 mm bar
1.42
2.9
341.36
166Figure 6
Confinement joint concrete.Figure 7
Curing the specimens.


## 5. Test Setup and Instrumentation

All the specimens were tested in a reaction frame of 50 tons of capacity. The test setup is shown in Figures8 and 9; hydraulic jack was used to apply the load at the free end of the beam in both upward and downward directions individually. To record the load precisely a proving ring was used. The load is applied in cyclic and reverse cyclic manners and measured for every 5 mm deflection. The deflection of the beam at the point of loading during test was measured as 5 mm, −5 mm, 10 mm, −10 mm, and 15 mm, respectively. Reversal loading is noted for every decrease in deflection.Figure 8
Test setup for cyclic load.Figure 9
Test setup for reverse cyclic load.


### 5.1. Measurement of Joint Distortion

Dial gauge D6 was fixed diagonally in the opposite direction in the joint region. It is used to measure the joint distortion.


### 5.2. Measurement of Strains

Mechanical and digital strain gauges were used to measure strain in reinforcement bars. Gauge length of mechanical strain is 100 mm. Demec points were fixed in position for the measurement of strains.


## 5.1. Measurement of Joint Distortion

Dial gauge D6 was fixed diagonally in the opposite direction in the joint region. It is used to measure the joint distortion.


## 5.2. Measurement of Strains

Mechanical and digital strain gauges were used to measure strain in reinforcement bars. Gauge length of mechanical strain is 100 mm. Demec points were fixed in position for the measurement of strains.


## 6. Loading History

The exterior beam-column joint specimen was subjected to cyclic loading and reverse cyclic loading simulating earthquake loads. The displacement sequence consists of 5 mm, −5 mm, 10 mm, −10 mm, 15 mm, −15 mm, 45 mm, and −45 mm. Each displacement level is indicated in dial gauge and corresponding loads are noted from the proving ring. In the first cycle, beam was loaded gradually up to 5 mm deflection and then unloaded. The beam was loaded gradually up to −5 mm deflection and then unloaded the second cycle, beam was loaded gradually up to 10 mm and then unloaded and beam was loaded gradually up to −10 mm and then unloaded similarly each cycle of load is applied.


## 7. Load versus Displacement Cycle

The load versus displacement cycle is drawn for every specimen (Figure18); the load is noted for 5 mm displacement, for each cyclic and reverse cyclic loading. The reversal of loading is noted from the proving ring. Figures 10 to 14 show the hysteresis loop for all the specimens.Figure 10
Load versus displacement cycle for O1 and O2.


## 8. Load versus Displacement

Cycle for O1 and O2. See Figure 10.Cycle for SS1 and SS2. See Figure 11.Figure 11
Load versus displacement cycle for SS1 and SS2.Cycle for E11 and E12. See Figure 12.Figure 12
Load versus displacement cycle for E11 and E12.Cycle for E21 and E22. See Figure 13.Figure 13
Load versus displacement cycle for E21 and E22.Figure 14
Load versus displacement cycle for E31 and E32.Cycle for E31 and E32. See Figure 14.Figures10 to 14 show the variation of load versus displacement cycle for various beam-column joints with various combinations at beam end displacement. The area for each hysteresis loop was calculated using these figures. From Figure 13 it is inferred that specimens E21 and E22 have a load carrying capacity (23 kN) higher than the ordinary beam-column joint.


## 9. Energy Dissipation

Energy Dissipation versus Deflection. Figure 15 shows the energy dissipated at each cycle for various specimens. The energy dissipation capacity is calculated using the enclosed area of the load deformation curve during each cycle of loading (i.e., area of each hysteresis loop). From this figure it is inferred that energy dissipation for E21 and E22 (10% metakaolin + 30% quarry dust) is more than other specimens.Figure 15
Energy dissipation versus displacement.


## 10. Beam and Column Reinforcement Strain

To measure the beam and column strain, (Figures16 and 17) Demec strain gauge was placed in the beam bottom reinforcement and in the column top outer face reinforcement. The gauge length of 100 mm was maintained for all the specimens to fix the strain gauge. For specimens O2, SS2, E12, and E32 the yield strain occurs at 5 mm (1st cycle) and ultimate strain at −30 mm (4th cycle). In specimen E22, yield strain occurs at 5 mm (1st cycle) and ultimate strain at 45 mm (5th cycle). Demec strain gauge was used to measure the strain in column top outer reinforcement. For specimens O2 and E22 the yield strain occurs at 10 mm (2nd cycle) and ultimate strain at 30 mm (4th cycle). In specimens E12 and E32 yield strain occurs at 5 mm (1st cycle) and ultimate strain at −30 mm (4th cycle). In specimen SS2 yield strain occurs at −5 mm (1st cycle) and ultimate strain at 30 mm (4th cycle).Figure 16
Beam bottom reinforcement strain versus cycle number.Figure 17
Column top reinforcement strain versus cycle number.Figure 18
Load versus displacement curve.


## 11. Ductility

Ductility is an important characteristic of any structural element. It is described as the capacity of a structural element to undergo deformation beyond yield without losing much of the load carrying capacity. Any type of brittle failure should be avoided, as it does not show warning before failure. If the structure posses sufficient ductile behaviour, it will be able to experience large deformation near ultimate loads. The amount of this inelastic deformation is proportional to the amount of ductility of the member. Ductility has generally been measured by a ratio called ductility factor. It is usually expressed as a ratio of deflection (Δ) at failure to the corresponding property at yield, as shown below:displacement ductility factorμ
Δ
=
Δ
u
/
Δ
y, where Δ
u is ultimate displacement and Δ
y is yield displacement.Increase in deformations after reaching ultimate load condition was not considered during experimentation. Hence the deformations at ultimate load have only been considered. The values of displacement ductility factor are calculated from experimental readings and listed in Table4.Table 4
Displacement ductility factor.
Sl. number
Specimen ID
Displacement
YieldΔ
y  (mm)
UltimateΔ
u (mm)
Ductility factorµ
Δ
1
O1
17.0
40
2.35
2
O2
16.0
39
2.43
3
SS1
15.0
45
3.00
4
SS2
14.5
45
3.10
5
E11
13.0
45
3.46
6
E12
12.0
45
3.75
7
E21
11.0
42
3.81
8
E22
11.5
43
3.64
9
E31
12.5
44
3.26
10
E32
13.5
42
3.34The ductility for the various proportions was calculated and presented in Table4. It is observed that the ductility property for the beam-column joint with mix is more comparing to other specimens. The exterior beam-column joint E21 and E22 with more ductility factor compared to the all other specimens.


## 12. Crack Pattern

In the beam-column joints, compression and tension developed in joint region during cyclic loading and the bond between concrete and reinforcement was reduced consequently. The first crack occurred near the beam-column joint and with further increase in loading the cracks propagated and initial cracks started widening. The crack pattern of the specimens will be discussed below.Figure19 shows the crack pattern for ordinary joint. In this the first crack occurred vertically at 7 mm deflection in the second cyclic loading, when load was applied at the bottom of the beam. The second crack occurred at −10 mm deflection at the third reverse cycle of loading. The third crack occurred diagonally at beam-column joint at 25 mm deflection at the fourth cycle of loading. The major crack occurred at joint region at 40 mm deflection at the fifth cycle of loading.Figure 19
Crack pattern for ordinary joint (O1 and O2).Figure20 shows the crack pattern for the seismic detailed joint. In this joint, while applying the second cycle loading, the first crack occurred vertically at 5 mm deflection in the second cyclic loading. The second crack occurred at −15 mm deflection at the third reverse cycle of loading. The third crack occurred diagonally at beam-column joint in 30 mm deflection at the fourth cycle of loading. The major crack occurred at joint region in 45 mm deflection at the fifth cycle of loading. In this joint the crack width is small compared to ordinary joint, so it behaves better than ordinary joint.Figure 20
Crack pattern for seismic joint (SS1 and SS2).By comparing Figures19, 20, 21, and 22, we can observe that the width of the crack is reduced and the ductility is increased as showed in Table 4. From Figures 19 and 22 the second, third, and fourth cracks were only hair cracks. In the metakaolin + quarry dust specimens closely spaced finer cracks were developed and width of such cracks was smaller than that developed in conventional reinforced concrete joint. It was observed that the use of metakaolin and quarry reinforced specimens concrete in the joint core could increase the joint stiffness and minimise damage to the concrete.Figure 21
Crack pattern for joint with 10% metakaolin + 30% quarry dust (E11 and E12).Figure 22
Crack pattern for joint with 10% metakaolin + 30% quarry dust (E21 and E22).By comparing Figures19 to 23, we can observe that in ordinary specimens wide cracks were developed at the joint and the crack width was more concentrated at the joint. But in metakaolin and quarrydust reinforced specimens in Confiement joint concrete confined exhibts finer cracks were developed and width of such cracks was smaller than those developed in conventional reinforced concrete joint.Figure 23
Crack pattern for joint with 10% metakaolin + 30% quarry dust (E31 and E32).


## 13. Joint Distortion

The dial gauge was used for measuring joint distortion in beam-column joint while applying cyclic load. The joint distortion is calculated from the formula(1)
Joint distortion
=
(
(
(
e
1
+
e
2
)
2
)
×
(
D
(
h
×
b
)
)
)
,
where e
1, and e
2 are changes in length of the diagonal joint region in mm, D is initial diagonal length in mm, H is depth of the joint region in mm, and B is breadth of the joint region in mm.Model Calculation
Changes in length of the diagonal joint region:(
e
1
)
=
138
mm.
Changes in length of the diagonal joint region:(
e
2
)
=
145
mm.
Initial diagonal length:D
=
148
mm.
Depth of the joint region:h
=
110
mm.So joint distortion = 0.2115 mm.Table5 shows the joint shear stress versus joint distortion. In this while comparing the values of joint distortion, the beam-column joints made with 10% metakaolin + 30% quarry dust have less joint distortion compared to the beam-column joints made with ordinary concrete and concrete with seismic detailing.Table 5
Joint distortion.
S. number
Specimen
Joint distortion (mm)
1
O1
0.2107
2
O2
0.2122
3
SS1
0.2113
4
SS2
0.2143
5
E11
0.2115
6
E12
0.2008
7
E21
0.2093
8
E22
0.2034
9
E31
0.2117
10
E32
0.2119


## 14. Conclusion

Based on the experimental study, the following conclusions have been drawn. The exterior beam-column joint E21 and E22 with 10% metakaolin + 30% quarry dust performs better than the beam-column joint with normal concrete as stated below:(i)
10% higher load carrying capacity,
(ii)
15% more energy dissipation.The exterior beam-column joint E31 and E32 (confinement joint) with 10% metakaolin + 30% quarry dust performs better than the beam-column joint with conventional concrete as stated below:(i)
very less joint distortion joint,
(ii)
more ductility factor.The metakaolin and quarry dust concrete specimens exhibited very little or no spalling of the concrete, whereas conventional concrete specimen showed extensive spalling of the concrete.Metakaolin and quarry dust concrete increase the ultimate shear strength when compared to conventional reinforced concrete.Metakaolin bridges the cracks in the concrete and restrains the crack propagation.By using metakaolin, the spacing of hoops provided in the core of beam-column joint can be increased while maintaining ductile behavior. The practical difficulties in placing and compaction of the concrete in beam-column region can be avoided.Thus metakaolin and quarry dust concrete can be seen as an appealing alternative to conventional confining reinforcement in all aspects.



---

*Source: 361962-2014-04-07.xml*