# Graphene Oxide Reinforced Polylactic Acid/Polyurethane Antibacterial Composites

Authors: Xiaoli An; Haibin Ma; Bin Liu; Jizeng Wang
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

Nanocomposites from PLA/PU containing small concentrations of graphene oxide (GO) were prepared by simple liquid-phase mixing followed by casting. The as-prepared ternary PLA/PU/GO composite films exhibited good antibacterial activity against the gram-positiveStaphylococcus aureus and the gram-negative Escherichia coli, due to the excellent antibacterial property of GO sheets with high specific surface area. The addition of GO inhibited the attachment and proliferation of microbes on the film surfaces, resulting in that the PLA/PU/GO composite films show remarkably improved antibacterial activity compared with PLA/PU composite film. The inhibition efficiency is proportional to the amount of GO. Furthermore, PLA/PU/GO composite fibrous paper was fabricated using electrospinning and exhibited good biocompatibility. The addition of GO does not destroy normal cell’s proliferation and differentiation. PLA/PU/GO composites with good antibacterial activity and biocompatibility make it attractive for the environmental and clinical applications and also provide a candidate for future application of tissue engineering.


---

## Body

## 1. Introduction

Tissue engineering is a field of research in biomedical engineering that applies the principles and methods of engineering and life sciences toward the fundamental understanding of structure/function relationships in normal and pathological mammalian tissues and the development of biological substitutes to restore, maintain, or improve functions [1]. This technique involves processes such as seeding cells onto a scaffold, creating artificial organs and tissues, and triggering or modulating new tissue formation. Currently, synthetic biomaterials (bioceramics and biopolymers) have been widely applied to the tissue engineering fields [2–6]. Also, antimicrobial materials have attracted considerable attention because bacterial infection is a major medical complication associated with the use of implanted medical devices [7–9]. Bacterial infection may result from tissue destruction, premature device failure, and the spread of the infection from other areas [8, 10]. Therefore, much effort has been expended to improve antibacterial activity of synthetic biomaterials [11–13].As thermoplastic synthetic polymers with desirable mechanical property profile, biocompatibility and biodegradability, polylactic acid (PLA) and polyurethane (PU) are two of the most promising biopolymers for tissue engineering territory, such as bone scaffolds, vascular grafts, and heart valves [14, 15]. Moreover, PU exhibits a certain degree of antibacterial efficacy [16, 17]. Compared with scaffolds fabricated from PLA or PU alone [18], it has been known that the composite PLA/PU scaffold exhibits advantageous morphology, mechanics, cell adhesion, and growth-supporting properties. However, dissatisfactory antibacterial activity coming from PU phase in PLA/PU composite limits its practical application in tissue engineering fields.Researchers had excitedly turned to the material to discover graphene’s potential applications, since it was first isolated with the help of Scotch tape in 2004 [19]. Graphene and graphene oxide (GO), with extraordinary mechanical properties (high Young’s modulus and hardness and excellent flexibility) [20], high specific surface area, and low cost, have been considered to be effective reinforcements for high-performance composites [21–24]. On the other hand, GO contains a number of oxygen-containing groups, which makes it relatively easy to be dispersed into some polar solvents and form intercalated composites with polar molecules through the strong interaction [25–30]. Recently, graphene and GO have been proved to exhibit excellent biocompatibility and high antibacterial activity [25, 30–34]. These have motivated us to explore the possibility of GO as an antibacterial reinforcement in biomaterials and study the antiseptic properties and cytotoxicity of GO-containing composites.In this study, PLA/PU/GO composite films were prepared by introducing GO nanosheets into PLA and PU phases through liquid-phase mixing and casting. The as-synthesized composites are characterized by using transmission electron morphology, X-ray diffraction, and field emission scanning electron microscope. Moreover, we investigate the antibacterial activity and biocompatibility of PLA/PU/GO. It showed remarkably improved antibacterial activity compared with PLA/PU composite. The addition of small amounts of GO prevented the attachment and proliferation of microbes on PLA/PU/GO surfaces, including the gram-positiveStaphylococcus aureus (S. aureus)and the gram-negative Escherichia coli (E. coli), as causative organisms of many device-related infections. PLA/PU/GO composites have excellent antibacterial activity and biocompatibility, suggesting their potential application in tissue engineering.


## 2. Experimental

### 2.1. Synthesis of PLA/PU/GO Composite Films

Polyurethane (PU) was synthesized in our laboratory according to previous study [35, 36]. GO nanosheets were prepared according to the method described by Hummer with a modification [37, 38]. In brief, powdery GO was dispersed in a 50 mL of DMF and dichloromethane (volume ratio = 2/3) solution by ultrasonification to form a uniform suspension. After that, 12 wt.% PLA (Mw = 26,000) and 3 wt.% PU (mass ratio = 4/1) were dissolved into the suspension with the aid of ultrasonification and stirring. Subsequently, PLA/PU/GO composite film was obtained by casting the suspension onto a clean silicon wafer, evaporating organic solvents, drying at 60°C in vacuum for 24 h, and peeling from the Si wafer. In our system, the PLA/PU/GO composite films with two different GO contents (the weight ratios between GO and polymers were 3 : 100 and 5 : 100) were prepared, which were denoted as PLA/PU/GO (3%) and PLA/PU/GO (5%), respectively. In comparison, PLA/PU film was prepared under the same conditions.


### 2.2. Synthesis of PLA/PU/GO Composite Nanofibers

PLA/PU/GO nanocomposite fibrous membrane was prepared by electrospinning. In brief, the above PLA/PU/GO (5%) suspension was used as the electrospun precursor. In a typical electrospinning process, the precursor suspension was loaded into a plastic syringe equipped with a 23-gauge stainless steel needle. A high voltage of 16 kV was supplied by a direct-current power supply and the feeding rate for the precursor suspension was adjusted to a constant rate of 0.3 mL/h using a syringe pump. A piece of aluminum foil was placed 15 cm below the tip of the needle to collect the as-spun nanofibers. Finally, the PLA/PU/GO fibrous paper was obtained by removing residual solvents at room temperature and peeling from the foil. Also, PLA/PU nanofibrous paper was prepared under the same conditions.


### 2.3. Characterization

Transmission electron microscopy (TEM, JEOL, JEM-2010) was employed to investigate the morphology of as-prepared GO, using an accelerating voltage of 200 kV. XPS measurement of the GO was performed on a Perkin-Elmer PHI-5702 multi-functional X-ray photoelectron spectroscope (Physical Electronics, USA), using Al-Kα radiation (photon energy: 1476.6 eV) as the excitation source and the binding energy of Au (Au 4f7/2: 84.00 eV) as the reference. X-ray diffraction (XRD) patterns were carried out by an X-ray diffraction using CuKα radiation (XRD, Rigaku, D/Max-2400), to investigate the microstructures of the PLA/PU/GO composite samples. Field emission scanning electron microscope (FESEM, JEOL, JSM 6701F) was employed to investigate the cross section of the casted films and the morphology of as-electrospun nanofibers.


### 2.4. Antibacterial Activity Test

The antibacterial activity of PLA/PU and PLA/PU/GO nanocomposites againstE. coli ATCC 25922 and S. aureus ATCC 6538 was measured by using plastics-measurement of antibacterial activity on plastics surfaces (ISO 22196, International Standard 22196 : 2007(E)). Before the test, the film samples (PLA/PU, PLA/PU/GO (3%) and PLA/PU/GO (5%)) were cut into 40 mm × 40 mm and washed repeatedly with sterile water, then dried in the air. At the same time, polyethylene films were prepared in 40 mm × 40 mm, sterilized in 75% ethanol, and then washed with sterile water. 1.5 × 105 CFU/mL bacterial suspension was seeded on each film sample and covered with polyethylene film so that the bacterial suspension can spread to the edges. Make sure that bacterial suspension does not leak beyond the edges of the film. 40 mL of phosphate-buffered saline (PBS) was used to wash the sample and polyethylene films in order to get the present bacteria followed by gentle shaking for 1 h, then diluted to 10-, 100-fold with a gradient method, and 1 mL of each dilution was placed into separate sterile Petri dishes. After that, 15 mL of plate count agar was poured into each Petri dish to disperse the bacteria by swirling gently. All plating shall be performed in duplicate. The Petri dishes were inverted and incubated at 37°C for 24 h. After incubation, the number of colonies in the Petri dishes was counted. For each dilution series, record the number of colonies recovered to two significant figures, as well as the dilution factor for the plates used for counting.S. aureus andE. coli were seeded on glass plate and PLA/PU/GO (5%) film and incubated for 24 h. The glass plate and PLA/PU/GO (5%) film seeded with bacteria were rinsed twice with PBS and fixed in 3% glutaraldehyde for 4 h, then rinsed in 0.1 mL of PBS. Thereafter, they were dehydrated with upgrading concentrations of ethanol (30%, 50%, 60%, 70%, 80%, 90%, 95%, and 100%) twice for 15 min each. After final washing with 100% ethanol, the samples were kept in fume hood. Finally, the glass plate and PLA/PU/GO (5%) film were sputter-coated with gold and observed under SEM to examine the morphology of E. coliand S. aureus.


### 2.5. Biocompatibility Test

To study the biocompatibility of the fibrous samples, MC3T3-E1 cells were used in our system, which are commonly used to assess cytotoxicity of materials. MC3T3-E1 cells were maintained at RPMI-l640 medium with 10% fetal bovine serum and 1% antibiotic/antimycotic solution in a 5% CO2 incubator at 37°C, refreshed every 3 days with Trypsin-EDTA solution, and then resuspended in a fresh culture medium. The PLA/PU and PLA/PU/GO (5%) fibrous papers were cut into pieces (1 cm × 1 cm) as scaffolds, soaked in 75% ethanol for 1 h to be sterilized, and then exchanged with PBS for three times (30 min each). The fibrous scaffolds were then washed with RPMI-1640 containing 10% FBS for two times (2 h each). 2 × 105 cell suspension was seeded on each scaffold. The cell-scaffold constructs were cultured in RPMI-l640 supplemented with 10% FBS, 1% antibiotic/antimycotic solution for up to 48 h. Finally, the cells were stained with acridine orange (AO), which was cleaved to yield a green fluorescent product by metabolically active cells. The density of the cells that adhered on each scaffold was observed at 100-fold magnification with a fluorescence microscopy (Olympus BX51).


## 2.1. Synthesis of PLA/PU/GO Composite Films

Polyurethane (PU) was synthesized in our laboratory according to previous study [35, 36]. GO nanosheets were prepared according to the method described by Hummer with a modification [37, 38]. In brief, powdery GO was dispersed in a 50 mL of DMF and dichloromethane (volume ratio = 2/3) solution by ultrasonification to form a uniform suspension. After that, 12 wt.% PLA (Mw = 26,000) and 3 wt.% PU (mass ratio = 4/1) were dissolved into the suspension with the aid of ultrasonification and stirring. Subsequently, PLA/PU/GO composite film was obtained by casting the suspension onto a clean silicon wafer, evaporating organic solvents, drying at 60°C in vacuum for 24 h, and peeling from the Si wafer. In our system, the PLA/PU/GO composite films with two different GO contents (the weight ratios between GO and polymers were 3 : 100 and 5 : 100) were prepared, which were denoted as PLA/PU/GO (3%) and PLA/PU/GO (5%), respectively. In comparison, PLA/PU film was prepared under the same conditions.


## 2.2. Synthesis of PLA/PU/GO Composite Nanofibers

PLA/PU/GO nanocomposite fibrous membrane was prepared by electrospinning. In brief, the above PLA/PU/GO (5%) suspension was used as the electrospun precursor. In a typical electrospinning process, the precursor suspension was loaded into a plastic syringe equipped with a 23-gauge stainless steel needle. A high voltage of 16 kV was supplied by a direct-current power supply and the feeding rate for the precursor suspension was adjusted to a constant rate of 0.3 mL/h using a syringe pump. A piece of aluminum foil was placed 15 cm below the tip of the needle to collect the as-spun nanofibers. Finally, the PLA/PU/GO fibrous paper was obtained by removing residual solvents at room temperature and peeling from the foil. Also, PLA/PU nanofibrous paper was prepared under the same conditions.


## 2.3. Characterization

Transmission electron microscopy (TEM, JEOL, JEM-2010) was employed to investigate the morphology of as-prepared GO, using an accelerating voltage of 200 kV. XPS measurement of the GO was performed on a Perkin-Elmer PHI-5702 multi-functional X-ray photoelectron spectroscope (Physical Electronics, USA), using Al-Kα radiation (photon energy: 1476.6 eV) as the excitation source and the binding energy of Au (Au 4f7/2: 84.00 eV) as the reference. X-ray diffraction (XRD) patterns were carried out by an X-ray diffraction using CuKα radiation (XRD, Rigaku, D/Max-2400), to investigate the microstructures of the PLA/PU/GO composite samples. Field emission scanning electron microscope (FESEM, JEOL, JSM 6701F) was employed to investigate the cross section of the casted films and the morphology of as-electrospun nanofibers.


## 2.4. Antibacterial Activity Test

The antibacterial activity of PLA/PU and PLA/PU/GO nanocomposites againstE. coli ATCC 25922 and S. aureus ATCC 6538 was measured by using plastics-measurement of antibacterial activity on plastics surfaces (ISO 22196, International Standard 22196 : 2007(E)). Before the test, the film samples (PLA/PU, PLA/PU/GO (3%) and PLA/PU/GO (5%)) were cut into 40 mm × 40 mm and washed repeatedly with sterile water, then dried in the air. At the same time, polyethylene films were prepared in 40 mm × 40 mm, sterilized in 75% ethanol, and then washed with sterile water. 1.5 × 105 CFU/mL bacterial suspension was seeded on each film sample and covered with polyethylene film so that the bacterial suspension can spread to the edges. Make sure that bacterial suspension does not leak beyond the edges of the film. 40 mL of phosphate-buffered saline (PBS) was used to wash the sample and polyethylene films in order to get the present bacteria followed by gentle shaking for 1 h, then diluted to 10-, 100-fold with a gradient method, and 1 mL of each dilution was placed into separate sterile Petri dishes. After that, 15 mL of plate count agar was poured into each Petri dish to disperse the bacteria by swirling gently. All plating shall be performed in duplicate. The Petri dishes were inverted and incubated at 37°C for 24 h. After incubation, the number of colonies in the Petri dishes was counted. For each dilution series, record the number of colonies recovered to two significant figures, as well as the dilution factor for the plates used for counting.S. aureus andE. coli were seeded on glass plate and PLA/PU/GO (5%) film and incubated for 24 h. The glass plate and PLA/PU/GO (5%) film seeded with bacteria were rinsed twice with PBS and fixed in 3% glutaraldehyde for 4 h, then rinsed in 0.1 mL of PBS. Thereafter, they were dehydrated with upgrading concentrations of ethanol (30%, 50%, 60%, 70%, 80%, 90%, 95%, and 100%) twice for 15 min each. After final washing with 100% ethanol, the samples were kept in fume hood. Finally, the glass plate and PLA/PU/GO (5%) film were sputter-coated with gold and observed under SEM to examine the morphology of E. coliand S. aureus.


## 2.5. Biocompatibility Test

To study the biocompatibility of the fibrous samples, MC3T3-E1 cells were used in our system, which are commonly used to assess cytotoxicity of materials. MC3T3-E1 cells were maintained at RPMI-l640 medium with 10% fetal bovine serum and 1% antibiotic/antimycotic solution in a 5% CO2 incubator at 37°C, refreshed every 3 days with Trypsin-EDTA solution, and then resuspended in a fresh culture medium. The PLA/PU and PLA/PU/GO (5%) fibrous papers were cut into pieces (1 cm × 1 cm) as scaffolds, soaked in 75% ethanol for 1 h to be sterilized, and then exchanged with PBS for three times (30 min each). The fibrous scaffolds were then washed with RPMI-1640 containing 10% FBS for two times (2 h each). 2 × 105 cell suspension was seeded on each scaffold. The cell-scaffold constructs were cultured in RPMI-l640 supplemented with 10% FBS, 1% antibiotic/antimycotic solution for up to 48 h. Finally, the cells were stained with acridine orange (AO), which was cleaved to yield a green fluorescent product by metabolically active cells. The density of the cells that adhered on each scaffold was observed at 100-fold magnification with a fluorescence microscopy (Olympus BX51).


## 3. Results and Discussions

As shown in Figure1(a), as-prepared GO sheets are nearly transparent under electron irradiation, indicating that the GO sheets are quite thin. As shown in Figure 1(b), the C1s XPS spectrum of GO indicates the presence of four components: the C in C=C bonds (284.5 eV), the C in C-O bonds (286.6 eV), the C in C=O bonds (287.7 eV), and the C in O–C=O bonds (288.7 eV). It indicates the considerable degree of the oxidation existing in GO material [39, 40]. GO sheets are a chemically modified graphene with suspended hydroxyl, epoxyl, and carboxyl functional groups [41], which result in the hydrophilic nature of GO.Characterization of GO sheets: (a) TEM image and (b) C1s XPS spectrum. The scale is 100 nm.
(a)
(b)As we know, fully exfoliated GO nanosheets can be dispersed in a polar organic solvent N,N-dimethylformamide (NMF) without any assistance of chemical treatment [42]. In our system, PLA/PU/GO composite films were prepared by a simple liquid-phase mixing followed by casting. Figure 2 shows the SEM images of the fracture surfaces of the PLA/PU and PLA/PU/GO (5%) films.Cross section SEM images of PLA/PU film ((a) and (b)) and PLA/PU/GO (5%) film ((c) and (d)) with different magnifications.
(a)
(b)
(c)
(d)As low-magnification images show (Figures2(a) and 2(c)), two fracture surfaces exhibit the same morphology: the PU particles are randomly distributed within the PLA polymer matrix without obvious agglomeration. However, high-magnification images (Figures 2(b) and 2(d)) show that their fracture surfaces are totally different. For the fracture of the PLA/PU film, the surface of the individual PU particle is relatively smooth. In comparison with the fracture of the PLA/PU/GO (0.5%) film, the surface of the individual PU particle is wrapped by layer-stacked GO sheets. Our fabrication process is presented to explain the combination of GO sheets and PU particles in PLA polymer matrix. As we know, PU molecule chains contain plenty of N-H groups and GO sheets contain many oxygen-containing groups. After they are mixed by ultrasonication and high speed stirring, PU particles and GO sheets will preferentially stick together due to the strong interactions, as a result that PU particles are wrapped by GO sheets.Figure3 shows the XRD patterns of PLA/PU and PLA/PU/GO (5%) films as well as the XRD pattern of powdery GO. The XRD pattern of the GO powders exhibits a characteristic diffraction peak at 11.6° (the shoulder centered at 20° is attributed to the glass plate, which is used as the substrate of supporting powdery sample for XRD measurement). The XRD patterns obtained from the PLA/PU/GO (5%) film is similar to those of the PLA/PU film apart from the existence of a weak peak ascribed to the GO phase. Therefore, the XRD result further confirms the successful addition of GO sheets into PLA/PU film, which is consistent with the result coming from SEM investigations. The weakening of GO peak is due to two aspects: one is the relatively low content of GO and the other is the good dispersion of GO within the PLA/PU matrix.Figure 3
XRD patterns of GO, PLA/PU, and PLA/PU/GO (5%).Figure4 exhibits considerable antibacterial activities when the bacteria are attached to PLA/PU/GO (3% GO and 5% GO) for 24 h. The incorporation of 5% GO into PLA/PU composite reduced E. coli andS. aureus growth up to 100%. Moreover, the incorporation of 3% GO reducedE. coli growth up to 100% and reduces S. aureusgrowth up to 99%, at 24 h. As the control group, PLA/PU composite showed the ability to inhibit bacterial growth, but not more effective than experimental groups. Such a release profile is consistent with SEM studies in Figure 4. The introduction of GO nanoparticles may reduce the probability that the bacteria will colonize on implant surface [23].Photographs of (a)S. aureus and (b) E. coli grown on PLA/PU, PLA/PU/GO (3%), and PLA/PU/GO (5%) for 24 h, respectively.
(a)
(b)After 4 h incubation with PLA/PU/GO nanocomposites of (3% GO, 5% GO) at 37°C, the antibacterial activity forE. coli decreased to 54% and 91% (Figure 5(a)), suggesting the strong inhibition ability of PLA/PU/GO nanocomposites to E. coli. We also employed a classic-colony counting method to measure the microbial viability of S. aureusfor 4 h. We found that viability significantly lose up to 54% and 89%, respectively (Figure 5(b)). These results further confirmed that GO contents were responsible for the observed strong antibacterial effect.Photographs of (a)S. aureus and (b) E. coli grown on PLA/PU/GO (3%) and PLA/PU/GO (5%) for 4 h, respectively.
(a)
(b)Figure6 shows that the morphology of S. aureusand E. coli when seeded on glass plates and PLA/PU/GO nanocomposites for 4 h at 37°C. The control group (seeded on glass plates) displays a normal bacterial appearance of S. aureus and E. coli (Figures 6(a) and 6(c)). The SEM studies (Figures 6(b) and 6(d)) reveal that S. aureusandE. coli largely lost their original appearance; such irreversible changes might arise from the effects of either oxidative stress or physical disruption that have been related to carbon nanomaterial [24, 28].SEM images ofS. aureus attached to (a) glass plate and (b) PLA/PU/GO (5%) for 4 h incubation at 37°; SEM images of E. coli attached on (c) glass plate and (d) PLA/PU/GO (5%) for 4 h incubation at 37°C.
(a)
(b)
(c)
(d)Figure7 shows the SEM micrographs of the PLA/PU and PLA/PU/GO nanofibers. It is clearly seen that ultrafine fibers have been successfully fabricated via electrospinning and all the fibers present loose three-dimensional (3D) frameworks. Also, the integration of 3D frameworks that mimic the natural extra-cellular matrix (ECM) structure is beneficial for cell adhesion and growth [30].SEM images of (a) electrospun PLA/PU nanofibers and (b) electrospun PLA/PU/GO (5%) nanofibers.
(a)
(b)Figure8 shows the fluorescence microscopy result after the cells were seeded directly on PLA/PU/GO fibrous scaffolds and incubated for 24 h. The PLA/PU/GO nanocomposite appeared to enhance the cell adhesion and proliferation. It can be definitely attributed to the excellent intrinsic biocompatibility and the hydrophilic nature of GO materials, which can greatly promote the cell-material interaction. The soluble and nonsoluble degradation products were found to be nontoxic to bovine AF cells grown in vitro.Figure 8
Fluorescence microscopy image of MC3T3-E1 cells grown on the electrospun PLA/PU/GO (5%) nanofibers for 48 h at 37°C. The magnification is 100x.


## 4. Conclusion

PLA/PU/GO nanocomposites passess strong antimicrobial activities and exhibit excellent biocompatibility, suggesting that such nanocomposite could be a good candidate material applied in tissue engineering territory, while simultaneously reducing the threat of bacterial colonization and subsequent chronic infection of surrounding tissue.



---

*Source: 373414-2013-09-11.xml*