# The Intrinsic Room-Temperature Ferromagnetism in ZnO:Co Thin Films Deposited by PLD

Authors: C. C. Wang; B. Y. Man; M. Liu; C. S. Chen; S. Z. Jiang; S. Y. Yang; S. C. Xu; X. G. Gao; B. Hu
Journal: Advances in Condensed Matter Physics
 (2012)

---

## Abstract

c-axis preferential orientated ZnO:Co thin films were synthesized on c-plane sapphire substrates by using pulsed laser deposition (PLD) technique in an oxygen-deficient ambient. X-ray diffraction spectra, scanning electron microscopy, X-ray photoelectron spectroscopy, energy dispersive spectroscopy, UV-vis transmittance spectra, and Raman spectra were used for characterization. Ferromagnetic behavior was clearly observed at room temperature and verified to be the intrinsic property of the material. The presence of second phase was ruled out.


---

## Body

## 1. Introduction

Dilute magnetic semiconductors (DMSs)—semiconductors doped with a few percent of magnetic atoms—have been intensely researched in the past few years due to their promising application in spintronics devices [1]. Based on the theoretical works of Dietl et al. [2], ZnO-based DMS has attracted a considerable amount of interest due to their proposed applications of room-temperature ferromagnetism. Many reports on the observation of ferromagnetism at room temperature have been published, while surprisingly other reports did not evidence any ferromagnetism in the compounds [3–5]. These controversial results suggested that the magnetism is very sensitive to the preparation conditions. There is a continuous debate about the origin of ferromagnetism and it is not clear whether ferromagnetism is originated from secondary phases or it is an intrinsic phenomenon. It is, therefore, important to ascertain whether the ferromagnetism is related to the presence of second phases.In this work, we report the structure and magnetic properties of ZnO:Co thin film with special emphasis on clarifying the origin of magnetic behavior from the perspective of structural characteristics. The Co appears to substitute for tetrahedrally coordinated Zn cations in the lattice and exhibits a +2 oxidation state. For the thin films we are able to identify there is not any impurity phase, indicating an intrinsic origin to the room-temperature ferromagnetism.


## 2. Experiment

c-axis-oriented thin films of Co-doped ZnO have been grown on c plane of sapphire single-crystal substrates using pulsed laser deposition (PLD) technique. The Zn0.95Co0.05O target used was prepared by the conventional solid state reaction technique. ZnO (99.99%) powder and Co2O3 (99.9%) powder as raw materials were mixed for 6 hours using a ball-mill, then uniaxially pressed (200 MPa) into a disk. The corresponding target was continuously sintered at 800°C, 1000°C and 1200°C for 2 hours in air and then quenched to room temperature finally [6]. A pulsed KrF excimer laser with a wavelength of 248 nm, a frequency of 10 Hz, and energy density of 2~3 J/cm2 was used for deposition. The target-to-substrate distance was fixed at 4 cm. The deposition period was 15 min. During the deposition, the substrates were kept at a constant temperature 500°C. After deposition, the samples were slowly cooled down to room temperature. The PLD system was evacuated by a turbomolecular pump to a base pressure of 5 × 10−5 Pa. The oxygen partial pressure for film growth was varied between 10−4 and 10 Pa. The substrates were ultrasonically cleaned in acetone and methanol, then rinsed in deionized water. In any case, Al2O3 substrates have been outgassed at 750°C prior to deposition.The magnetic measurement was carried out using a MicroMag Mode 2900 alternating gradient magnetometer (AGM). The structure of the deposited films was examined using a Rigaku D/max-rB X-ray diffractormeter (XRD) and a Zeiss supra55 field emission scanning electron microscopy (FESEM). The composition of the films was measured using a PHI-5300 X-ray photoelectron spectroscopy (XPS) and an Oxford X-Max energy dispersive spectroscopy (EDS). Optical measurements were made using a U-4000 Hitachi spectrophotometer. Raman spectra were acquired from a Renishaw inVia micro-Raman spectrometer in the backscattering geometry.


## 3. Results and Discussion

The magnetic measurement results for the sample deposited under1.3×10-3 Pa oxygen partial pressure at 500°C are shown in Figure 1. Inset (a) shows the ferromagnetic signal of the ZnO:Co film before subtracting the linear diamagnetic background signal arising from the substrate. The hysteresis loops of the sample clearly indicate that the as-grown ZnO:Co thin film is ferromagnetism with Curie temperature (Tc) above room temperature. The coercive field of the sample is about 70 Oe. Oxides of cobalt (CoO TN=291 K, Co3O4  TN=30 K) are well known to be antiferromagnetism with the Néel temperature below room temperature. Hence, the observed ferromagnetic behaviors might not be explained in terms of the formation of oxides of cobalt.Figure 1
Magnetization curve for film deposited under 1.3 × 10−3 Pa oxygen partial pressure at room temperature. Inset (a) shows magnetization curve before subtracting the diamagnetic contribution from the substrate. Inset (b) shows the magnified portion of the magnetization curve near origin.The film is highly crystallized as seen from the sharp diffraction peaks shown in Figure2 and the full width at half-maximum (FWHM) of the rocking curve is close to 0.33°. The two diffraction peaks observed around 34.4° and 72.7° are characteristic of the hexagonal ZnO wurtzite with the c-axis perpendicular to the substrate plane. The c-axis lattice constant, estimated from the peak position of the (002) line, is 0.5217 nm, as compared to the c-axis lattice value of 0.5206 nm recorded for ZnO powder. The average grain size, inferred from the line broadening of (002) peak using the Scherrer formula, is found to be in the 25 nanometer range. In addition, within the detection limits of XRD, we do not find any evidence of second phase.Figure 2
XRD pattern of the ZnO:Co grown under 1.3 × 10−3 Pa oxygen partial pressure. The inset depicts the rocking curve of (002) reflection of the film.The surface and cross-sectional morphology were analyzed using a FESEM. Figure3 shows the typical surface and cross-sectional images of the as-deposited film. We could see clearly that the as-deposited film consists of dense and uniformly sized grains and has a smooth surface without any voids and cracks. The existence of these small grains indicates that the nucleation density is rather high and the growth proceeds in a three-dimensional fashion. The cross-sectional SEM also obviously shows the 3D columnar growth [7] mode.Figure 3
SEM and cross-sectional SEM images of the as-grown film under 1.3 × 10−3 Pa oxygen partial pressure.XPS was also used to characterize the charge state of Co ions in the film. Figure4 shows XPS spectrum for the as-grown film. The C peak in the as-grown spectrum is presumably due to the adsorption of adventitious hydrocarbons during sample was transferred through air. The inset shows the Co 2p spectrum of the sample. The spectrum shows four peaks, the 2p3/2 and 2p1/2 doublet and shake-up resonance transitions (satellite) of these two peaks at higher binding energies. The Co 2p3/2 core levels for Co-O bonding is 781.4 eV, and the energy difference between Co 2p3/2 and Co 2p1/2 is 15.4 eV, which matches that of standard CoO, indicating the presence of a high-spin divalent state of Co in these samples [8, 9]. Thus, within the detection limits of the spectrometer, we can rule out metallic Co as the source of the observed ferromagnetism.Figure 4
The full-range XPS spectra of the ZnO:Co thin film, revealing only Zn, Co, O, and C peaks. The inset shows the Co 2p spectrum of the sample.EDS is used to measure the percentage of cobalt in the ZnO:Co film. The EDS data taken at a number of locations throughout the specimen reveal a uniform distribution of Co dissolved in ZnO lattices. The cobalt content of the film deposited under 1.3 × 10−3 Pa oxygen partial pressure is 6.6%, that is, the dopant concentration in the film is higher than in the target. Similar results of the transition metal enrichment in doped ZnO films grown by PLD have been reported [10–12]. The reasons have been analyzed by the higher sputter yield of the Zn atoms than Co atoms from the thin film surface, which caused by the high energy ions (several hundred eV [13]) in the laser ablation plasma plume. The preferential sputtering from the film surface was caused by two factors: surface binding effects and mass difference effects [11]. For ZnO:Co alloy film, sputtering from the surface is strongly determined by the surface binding energy (BE) of the metal atoms and to a lesser extent by their atomic mass [13]. Thus, the sputter yield is higher for Zn because it has the lower surface energy (the surface BE for Zn of ZnO is 3.04 eV, while the surface BE for Co of Co3O4 is 6.05 eV [13]), resulting in a higher cobalt concentration in the film than in the target.Evidence for Co substitution in the ZnO lattice for our film can be inferred from optical absorption measurements. Figure5 shows the optical transmission for ZnO:Co film. An undoped ZnO film is included as reference. Three absorption peaks are observed in the doped film and labelled as 1, 2, and 3. The absorption peaks at approximately 566, 611, and 655 nm can be identified as the d-d transitions from the A42(E) ground state toward A21(G), T14(P), and E2(G) excited states of Zn substituted Co2+ ions in ZnO [14, 15]. This shows the presence of cobalt in a tetrahedral crystal field in the +2 state. The Co doping also leads to bandgap narrowing, which is typically interpreted as due to the sp-d exchange interactions between the band electrons and the localized d electrons of Co ions [16]. Based on the above experiment results, we can find that the Co cations have successfully entered into the hexagonal wurtzite structure and substituted for Zn cations sites in the ZnO lattice.Figure 5
Room-temperature optical transmittance spectrum for ZnO:Co and ZnO thin films.The Raman measurements were performed in the backscattering geometry at room temperature with a 514.5 nm (2.4 eV) Ar+ laser as an excitation source. The Raman spectra of the Zn0.95Co0.05O target (inset of Figure 6) are dominated by five broad peaks. The peaks at 198, 322, and 429 cm−1 can be attributed to the 2E2L; 2TA, E2H-E2L, and E2H modes, respectively [17]. The vibrations at around 230 and 530 cm−1are assigned to the acoustic-phonon branch at the zone boundary and shallow donor defects bound on the Co sites, respectively [18]. Figure 6 shows the spectra of Co-doped ZnO deposited under 1.3 × 10−3 Pa oxygen partial pressure. In addition to the phonon modes from the sapphire substrate (the peaks labelled with “s”) and the peaks which also can be observed in the target, additional modes are observed. It also shows that the E2H peak substantially reduced in the film compared with that in the target. The Zn0.95Co0.05O target is polycrystalline ceramics, thereby the intensity of E2H peak is high and FWHM is also large. However, the ZnO:Co thin film is single crystal. The pronounced weakening of E2H peak is the consequence of the structural defect formation and local lattice distortions induced by doping [8, 18, 19]. The peaks at 380, 407, 576 and 670 cm−1 can be attributed to the A1(TO), E1(TO), A1(LO) and TA + LO modes, respectively [17]. The mode of 644 cm−1 which is also revealed in Fe, Sb, Al, N, and (Mn, Co) doped ZnO may correlate with Zn interstitials or oxygen vacancies by the impurity doping [20, 21]. The mode of 694 cm−1 is still uncertain. Sudakar et al. tentatively assigned the mode observed in ZnO:Co samples at about 690 cm−1 to the Zn-O-Co local vibration [22]. The peak at 134 cm−1 due to scattering on E2g phonon of hcp-Co [23] and the peaks at about 146 and 300 cm−1 related to CoO magnons [24, 25] were absent in our sample. Thus, for the thin film we are able to identify no mode of impurity phases. This provides further evidence for the observed ferromagnetism in the samples is not induced by phase segregation.Figure 6
Room-temperature Raman spectrum of ZnO:Co thin film. Peaks attributed to the substrate are labelled with “s”. The inset shows the Raman spectrum of the Zn0.95Co0.05O target.The samples are carefully characterized using XRD, XPS, UV-Vis, and Raman and we are able to make a convincing case that there are no impurity phases present, at least within the limitations of these characterization techniques. Having ruled out the possibility of the presence of second phase through our structural and optical investigations, we infer that the presence of second phase could not be the cause of the observed room-temperature ferromagnetism. Hence, we conclude that the observed room-temperature ferromagnetism is an inherent property of the material. There are several mechanisms proposed in the literature regarding the origin of ferromagnetism in DMSs [26]. The exact mechanism of intrinsic ferromagnetism in TM-doped oxides is still under debate. The Ruderman-Kittel-Kasuya-Yosida (RKKY) interaction is based on free electrons, but ZnO cannot transform into a metal at such a low doping. Direct interactions such as double-exchange or super-exchange cannot be responsible for the ferromagnetism because the magnetic cations are dilute in our samples. Coey et al. proposed that ferromagnetic exchange in dilute ferromagnetic oxides is mediated by shallow donor electrons that form bound magnetic polarons, which overlap to create a spin-split impurity band [27]. However, a carrier-mediated interpretation for the room-temperature ferromagnetism has also been proposed [28]. Co dopant states were successfully identified and positioned in the host ZnO bands [29]. An observable carrier density on the order of less than 0.1 electron per Co ion could stabilize the ferromagnetic coupling against the ambient conditions according to the band-coupling model was demonstrated [30, 31]. The origin of the room-temperature ferromagnetism in the ZnO:Co films will be a study emphasis in our further research.


## 4. Conclusions

In conclusion, we have grown ZnO:Co thin films on Al2O3 (0001) substrates by PLD. Ferromagnetic behaviour was clearly observed at room temperature for the ZnO:Co films. The XRD, XPS, EDS, UV-Vis, and Raman analysis demonstrated that cobalt can be uniformly incorporated into the wurtzite structure and substitute for Zn cations sites in ZnO lattice without phase segregation. There is no evidence for the formation of either metallic Co or CoOx particles in the thin film, indicating an intrinsic origin to the ferromagnetism. The growth of these ferromagnetic films opens the route for the fabrication of spin-based electronics.



---

*Source: 363981-2012-03-21.xml*