# Acidic Tumor pH-Responsive Nanophotomedicine for Targeted Photodynamic Cancer Therapy

Authors: Wooram Park; Sin-jung Park; Heejun Shin; Kun Na
Journal: Journal of Nanomaterials
 (2016)

---

## Abstract

An acidic tumor pH-responsive nanophotomedicine (pH-NanoPM) for targeted photodynamic therapy (PDT) was demonstrated herein. The pH-NanoPM was prepared with a size of ~110 nm by self-assembly of a pH-responsive polymeric photosensitizer (pH-PPS) consisting of pH-cleavable methoxypolyethylene glycol (pH-C-mPEG). Because the pH-C-mPEG can be detached from the nanoparticles by hydrolysis of the benzoic-imine group at the pH of an acidic tumor (~6.5), the particle size and surface charge of the pH-NanoPM were changed along with the environmental pH condition. After detachment of the pH-C-mPEG, the pH-NanoPM particles became positively charged (+18.67±1.95 mV) due to exposure of primary amine groups and decreased to a size of ~40 nm. Fromin vitro cellular experiments with HeLa human cervical cancer cells, the pH-NanoPM exhibited enhanced cellular internalization at acidic tumor pH compared to normal pH, which led to a significant cancer cell killing effect. These results suggest that this system has the potential to be used as a new class of nanophotomedicine for targeted photodynamic cancer therapy.


---

## Body

## 1. Introduction

Over the past several decades, photodynamic therapy (PDT) has been a prospective approach for cancer treatment [1–3]. PDT is based on the administration of a photosensitizer (PS) and irradiation of local tumor site with appropriate light wavelength [4]. Under light irradiation, the excited PS generates cytotoxic reactive oxygen species (ROS), such as singlet oxygen or free radicals, which led to serious cell damage [5]. However, not sufficient therapeutic efficacy and side effect due to nonspecificity of PSs have been major concerns for their clinical application [6–8].Given that reason, various types of nanotechnology-based PSs have been developed to overcome the limitations of existing PSs [9–11]. More recently, stimulus-triggered PSs have emerged to achieve higher targeting efficiency and reduce systemic toxicity [11–13]. Because pH of the tumor extracellular region is slightly more acidic (~pH 6.5) than the pH of normal region (~pH 7.4) [14–16], delivery system based on pH-responsiveness has been actively researched as a promising tumor targeting strategy.Here, we demonstrate an acidic tumor pH-responsive nanophotomedicine (pH-NanoPM) for effective cancer treatment. The pH-NanoPM was prepared by self-assembly of a pH-responsive polymeric PS (pH-PPS, Figure1). The pH-PPS was synthesized via a three-step process (Figure 2(a)). First, pH-cleavable methoxypolyethylene glycol (pH-C-mPEG) was synthesized by incorporation of 4-formylbenzoic acid [17, 18]. Second, the pH-C-mPEG was conjugated with branched polyethylenimine (bPEI). Finally, a PS was introduced by a carbodiimide reaction [19]. The newly synthesized pH-NanoPM was formed as stable micellar nanoparticles at physiological pH (i.e., ~pH 7.4 in normal tissues). However, the particle size and surface charge of the pH-NanoPM particles were changed by cleavage of the pH-C-mPEG molecules in response to acidic environments (e.g., ~pH 6.5 in tumor tissues). Following pH-C-mPEG cleavage, the pH-NanoPM particles became positively charged due to the exposure of the primary amine groups in bPEI. Given the fact that the cellular membranes are negatively charged, the positively charged nature of the pH-Nano PM particles at acidic tumor pH will increase their internalization into cancer cells and therefore enhance their therapeutic effectiveness.Figure 1
Schematic illustration of the acidic tumor pH-responsive nanophotomedicine (pH-NanoPM).Figure 2
Chemical synthesis of the pH-responsive polymeric photosensitizer (pH-PPS). (a) Synthesis of the pH-PPS and (b)1H-NMR analysis of mPEG-benzoic-imine-bPEI in D2O.
(a)
(b)


## 2. Materials and Methods

### 2.1. Materials

Methoxypolyethylene glycol (mPEG, 5 kDa), 4-formylbenzoic acid, dicyclohexyl carbodiimide (DCC), 4-(dimethylamino) pyridine (DMAP),N-hydroxysuccinimide (NHS), methylthiazolyldiphenyl-tetrazolium bromide (MTT), 9,10-dimethylanthracene (DMA), fluorescamine, pyrene, dichloromethane (DCM), andN,N-dimethylformamide (DMF) were purchased from Sigma-Aldrich (Yongin, Republic of Korea). Pheophorbide-a (PPb-a) was obtained from Frontier Scientific (Logan, UT, USA). Branched polyethylenimine (bPEI, 1.8 kDa) was purchased from Alfa Aesar (Ward Hill, MA, USA).


### 2.2. Synthesis of the pH-PPS

The pH-PPS was synthesized via a three-step process as follows. First, pH-C-mPEG was synthesized by a modified version of a previously reported procedure [17, 18]. Typically, 4-formylbenzoic acid (0.6 g, 4 millimolar), DCC (1.7 g, 8 millimolar), and DMAP (1.0 g, 8 millimolar) were added to a solution of mPEG (2 g, 0.4 millimolar) in DMF (20 mL). After stirring for 24 h, the solution was filtered and precipitated in diethyl ether (0.2 L). The product was dried in vacuo at room temperature for 6 h. Second, to synthesize pH-C-mPEG conjugated bPEI, bPEI (0.2 g, 0.33 millimolar) was dissolved in 10 mL of DMF and pH-C-mPEG (1.7 g, 0.11 millimolar) dissolved in 10 mL of DMF was added. The mixture was stirred and heated to 40°C for 4 h and precipitated in cold diethyl ether (0.2 L). The product was dried in vacuo at room temperature for 6 h. The formation of pH-C-mPEG conjugated bPEI was verified by 1H-NMR. The 1H-NMR spectra were measured in D2O at room temperature using a Bruker NMR Spectrometer (Bruker, Germany) at 300 MHz. Finally, to incorporate PS into the pH-C-mPEG conjugated bPEI, a mixture of PPb-a (6.96 mg, 11.59 micromolar), DCC (3.59 mg, 17.39 micromolar), and NHS (2.00 mg, 17.39 micromolar) was dissolved in 5 mL of DMF and stirred for 3 h. Then, the solution was added dropwise into a solution of pH-C-mPEG conjugated bPEI (0.2, 11.59 micromolar) with 5 mL of DMF, and the mixture was stirred for 24 h at room temperature. To purify the conjugates, the reaction solution was poured into 0.2 L of cold diethyl ether. This step was repeated three times and the final product was obtained followed by drying in vacuo at room temperature for 6 h. The PPb-a content of the pH-PPS was measured using UV/Vis spectroscopy [20].


### 2.3. Preparation of the pH-NanoPM

The pH-NanoPM was prepared by a dialysis method. Briefly, the pH-PPS (10 mg) was dissolved in 5 mL of DMSO and dialyzed for 24 h against NaOH/Na2B4O7 buffer using a dialysis membrane (Molecular weight cut-off (MWCO), 1 kDa, Spectrum Laboratories, Rancho Dominguez, CA, USA).


### 2.4. Characterization of the pH-NanoPM

The particle size distribution and zeta-potential of the pH-NanoPM were determined at different pH values (pH 7.4 and 6.5) using DLS (Zetasizer Nano ZS, Malvern Instruments Ltd., UK). All the DLS experiments were performed at 25°C in aqueous solution with 1 mg/mL of concentration.


### 2.5. Measurement of Critical Aggregation Concentration (CAC)

The CAC value of the pH-NanoPM was calculated using pyrene [21, 22]. Briefly, the pyrene was dissolved into acetone with concentration of 6.0 × 10−2M, and then the solution was added to distilled water to yield a pyrene concentration of 12.0 × 10−7M. To remove remaining acetone, the solution was stirred for 6 h at room temperature. Then, the pyrene solution was mixed with solutions of the pH-NanoPM in different concentrations and incubated overnight. The following day, the fluorescence intensities of the mixtures were detected using a fluorescent spectrometer (RF-5301PC, Shimadzu, Japan).


### 2.6. Measurement of Singlet Oxygen Generation (SOG)

The pH-NanoPM (PPb-a, 1.5μg/mL) was dissolved in DMF and mixed with DMA stock solutions (6.0 × 10−2M) to give a final concentration of 20 micromolar DMA. Following stirring for 10 min at room temperature, samples containing the pH-NanoPM and DMA were irradiated with a light intensity of 5 mW/cm2 using a 670 nm laser source (fiber-coupled laser system, LaserLab, Republic of Korea).


### 2.7. Quantitative Measurement of the Exposed Amine Groups in the pH-NanoPM

The pH-NanoPM (1 mg) was dissolved in deionized water (1 mL). The resulting solution (100μL) was mixed with PBS (1 mL, 150 mM) at pH 7.4 and 6.5. This solution was incubated at 37°C for 6 h and then mixed with 20 μL of fluorescamine (2.5 mg/mL) in DMF at room temperature for 30 min. The fluorescence intensity of each solution was measured using a fluorescent spectrometer at excitation wavelength 365 nm and at emission wavelength 465 nm.


### 2.8. Cell Culture and Incubation Conditions

HeLa cells were cultured in Dulbecco’s Modified Eagle Medium (DMEM, 25 mmol/L glucose) equilibrated with 5% CO2 and 95% air at 37°C. The medium was supplemented with 10% fetal calf serum (FCS), 50 mg/L streptomycin, and 75 mg/L penicillin sulfate.


### 2.9.In Vitro Cellular Internalization Test

To confirm the cellular uptake of pH-NanoPM at two different pH values (pH 7.4 and 6.5) [9], HeLa cells were seeded in a 35 mm2 cell culture dish at a density of 1.0 × 106 cells/dish and were cultured for 24 h at 37°C in 5% CO2. The cells were treated with serum free (SF) medium containing the pH-NanoPM (PPb-a, 3.2 × 106 M) for 30 min at pH 7.4 or 6.5. After that, the cells were harvested and redispersed into Dulbecco’s phosphate buffer saline (DPBS, Invitrogen Corp., Carlsbad, CA, USA). The cellular uptake of PPb-a was measured using a flow cytometry (Beckman, San Jose, CA, USA) and analyzed using a CXP analysis program (Beckman).


### 2.10. Confocal Laser Scanning Microscopy (CLSM) Analysis

To observe the cellular localization of pH-NanoPM in HeLa cells [9, 23], HeLa cells (1.0 × 105 cells/well) were cultured on cover slips placed in six-well plates. The following day, the cells were treated with the pH-NanoPM for 30 min at pH 7.4 or 6.5. Then, the cells were washed with DPBS and fixed with a 4% paraformaldehyde solution. To observe the cells under microscope, the cells were mounted using a DAPI containing mounting solution (Fluoroshield™ with DAPI, Sigma-Aldrich, Yongin, Republic of Korea). Then, the cells were visualized using a confocal laser scanning microscope (CLSM, LSM 710 Meta; Carl Zeiss, Germany).


### 2.11.In Vitro Cytotoxicity Study

To confirm the PDT-mediated cancer cell killing effect of the pH-NanoPM, HeLa cells were seeded in black 96-well culture plates at a density of 2.0 × 104 cells per well. After culturing for 24 h, the cells were treated with the SF medium containing the pH-NanoPM (PPb-a, 10 μg/mL) and incubated for 30 min. After that, the cells were washed with DPBS to remove remaining pH-NanoPM in the medium and incubated with fresh complete medium. Then, the cells were irradiated using a 670 nm laser source (3.6 J cm−2, fiber-coupled laser system, LaserLab, Republic of Korea). After 24 h, the cell viability was measured using a MTT assay.


### 2.12. Statistical Analysis

Data are expressed as the mean ± standard deviation (SD). Differences between values were assessed using Student’st-tests.


## 2.1. Materials

Methoxypolyethylene glycol (mPEG, 5 kDa), 4-formylbenzoic acid, dicyclohexyl carbodiimide (DCC), 4-(dimethylamino) pyridine (DMAP),N-hydroxysuccinimide (NHS), methylthiazolyldiphenyl-tetrazolium bromide (MTT), 9,10-dimethylanthracene (DMA), fluorescamine, pyrene, dichloromethane (DCM), andN,N-dimethylformamide (DMF) were purchased from Sigma-Aldrich (Yongin, Republic of Korea). Pheophorbide-a (PPb-a) was obtained from Frontier Scientific (Logan, UT, USA). Branched polyethylenimine (bPEI, 1.8 kDa) was purchased from Alfa Aesar (Ward Hill, MA, USA).


## 2.2. Synthesis of the pH-PPS

The pH-PPS was synthesized via a three-step process as follows. First, pH-C-mPEG was synthesized by a modified version of a previously reported procedure [17, 18]. Typically, 4-formylbenzoic acid (0.6 g, 4 millimolar), DCC (1.7 g, 8 millimolar), and DMAP (1.0 g, 8 millimolar) were added to a solution of mPEG (2 g, 0.4 millimolar) in DMF (20 mL). After stirring for 24 h, the solution was filtered and precipitated in diethyl ether (0.2 L). The product was dried in vacuo at room temperature for 6 h. Second, to synthesize pH-C-mPEG conjugated bPEI, bPEI (0.2 g, 0.33 millimolar) was dissolved in 10 mL of DMF and pH-C-mPEG (1.7 g, 0.11 millimolar) dissolved in 10 mL of DMF was added. The mixture was stirred and heated to 40°C for 4 h and precipitated in cold diethyl ether (0.2 L). The product was dried in vacuo at room temperature for 6 h. The formation of pH-C-mPEG conjugated bPEI was verified by 1H-NMR. The 1H-NMR spectra were measured in D2O at room temperature using a Bruker NMR Spectrometer (Bruker, Germany) at 300 MHz. Finally, to incorporate PS into the pH-C-mPEG conjugated bPEI, a mixture of PPb-a (6.96 mg, 11.59 micromolar), DCC (3.59 mg, 17.39 micromolar), and NHS (2.00 mg, 17.39 micromolar) was dissolved in 5 mL of DMF and stirred for 3 h. Then, the solution was added dropwise into a solution of pH-C-mPEG conjugated bPEI (0.2, 11.59 micromolar) with 5 mL of DMF, and the mixture was stirred for 24 h at room temperature. To purify the conjugates, the reaction solution was poured into 0.2 L of cold diethyl ether. This step was repeated three times and the final product was obtained followed by drying in vacuo at room temperature for 6 h. The PPb-a content of the pH-PPS was measured using UV/Vis spectroscopy [20].


## 2.3. Preparation of the pH-NanoPM

The pH-NanoPM was prepared by a dialysis method. Briefly, the pH-PPS (10 mg) was dissolved in 5 mL of DMSO and dialyzed for 24 h against NaOH/Na2B4O7 buffer using a dialysis membrane (Molecular weight cut-off (MWCO), 1 kDa, Spectrum Laboratories, Rancho Dominguez, CA, USA).


## 2.4. Characterization of the pH-NanoPM

The particle size distribution and zeta-potential of the pH-NanoPM were determined at different pH values (pH 7.4 and 6.5) using DLS (Zetasizer Nano ZS, Malvern Instruments Ltd., UK). All the DLS experiments were performed at 25°C in aqueous solution with 1 mg/mL of concentration.


## 2.5. Measurement of Critical Aggregation Concentration (CAC)

The CAC value of the pH-NanoPM was calculated using pyrene [21, 22]. Briefly, the pyrene was dissolved into acetone with concentration of 6.0 × 10−2M, and then the solution was added to distilled water to yield a pyrene concentration of 12.0 × 10−7M. To remove remaining acetone, the solution was stirred for 6 h at room temperature. Then, the pyrene solution was mixed with solutions of the pH-NanoPM in different concentrations and incubated overnight. The following day, the fluorescence intensities of the mixtures were detected using a fluorescent spectrometer (RF-5301PC, Shimadzu, Japan).


## 2.6. Measurement of Singlet Oxygen Generation (SOG)

The pH-NanoPM (PPb-a, 1.5μg/mL) was dissolved in DMF and mixed with DMA stock solutions (6.0 × 10−2M) to give a final concentration of 20 micromolar DMA. Following stirring for 10 min at room temperature, samples containing the pH-NanoPM and DMA were irradiated with a light intensity of 5 mW/cm2 using a 670 nm laser source (fiber-coupled laser system, LaserLab, Republic of Korea).


## 2.7. Quantitative Measurement of the Exposed Amine Groups in the pH-NanoPM

The pH-NanoPM (1 mg) was dissolved in deionized water (1 mL). The resulting solution (100μL) was mixed with PBS (1 mL, 150 mM) at pH 7.4 and 6.5. This solution was incubated at 37°C for 6 h and then mixed with 20 μL of fluorescamine (2.5 mg/mL) in DMF at room temperature for 30 min. The fluorescence intensity of each solution was measured using a fluorescent spectrometer at excitation wavelength 365 nm and at emission wavelength 465 nm.


## 2.8. Cell Culture and Incubation Conditions

HeLa cells were cultured in Dulbecco’s Modified Eagle Medium (DMEM, 25 mmol/L glucose) equilibrated with 5% CO2 and 95% air at 37°C. The medium was supplemented with 10% fetal calf serum (FCS), 50 mg/L streptomycin, and 75 mg/L penicillin sulfate.


## 2.9.In Vitro Cellular Internalization Test

To confirm the cellular uptake of pH-NanoPM at two different pH values (pH 7.4 and 6.5) [9], HeLa cells were seeded in a 35 mm2 cell culture dish at a density of 1.0 × 106 cells/dish and were cultured for 24 h at 37°C in 5% CO2. The cells were treated with serum free (SF) medium containing the pH-NanoPM (PPb-a, 3.2 × 106 M) for 30 min at pH 7.4 or 6.5. After that, the cells were harvested and redispersed into Dulbecco’s phosphate buffer saline (DPBS, Invitrogen Corp., Carlsbad, CA, USA). The cellular uptake of PPb-a was measured using a flow cytometry (Beckman, San Jose, CA, USA) and analyzed using a CXP analysis program (Beckman).


## 2.10. Confocal Laser Scanning Microscopy (CLSM) Analysis

To observe the cellular localization of pH-NanoPM in HeLa cells [9, 23], HeLa cells (1.0 × 105 cells/well) were cultured on cover slips placed in six-well plates. The following day, the cells were treated with the pH-NanoPM for 30 min at pH 7.4 or 6.5. Then, the cells were washed with DPBS and fixed with a 4% paraformaldehyde solution. To observe the cells under microscope, the cells were mounted using a DAPI containing mounting solution (Fluoroshield™ with DAPI, Sigma-Aldrich, Yongin, Republic of Korea). Then, the cells were visualized using a confocal laser scanning microscope (CLSM, LSM 710 Meta; Carl Zeiss, Germany).


## 2.11.In Vitro Cytotoxicity Study

To confirm the PDT-mediated cancer cell killing effect of the pH-NanoPM, HeLa cells were seeded in black 96-well culture plates at a density of 2.0 × 104 cells per well. After culturing for 24 h, the cells were treated with the SF medium containing the pH-NanoPM (PPb-a, 10 μg/mL) and incubated for 30 min. After that, the cells were washed with DPBS to remove remaining pH-NanoPM in the medium and incubated with fresh complete medium. Then, the cells were irradiated using a 670 nm laser source (3.6 J cm−2, fiber-coupled laser system, LaserLab, Republic of Korea). After 24 h, the cell viability was measured using a MTT assay.


## 2.12. Statistical Analysis

Data are expressed as the mean ± standard deviation (SD). Differences between values were assessed using Student’st-tests.


## 3. Results and Discussion

### 3.1. Synthesis and Preparation of the pH-NanoPM

In this study, a novel pH-responsive polymeric photosensitizer (pH-PPS) was designed and synthesized as shown in Figure2(a). First, pH-cleavable methoxypolyethylene glycol (pH-C-mPEG) was synthesized by incorporation of 4-formylbenzoic acid, which formed a benzoic-imine linkage with primary amine groups. The hydrolysis kinetics and hydrolysis bonding equilibrium of an imine bond are significantly influenced by the environmental pH [17, 18, 24]. According to previous reports [17, 18], the benzoic-imine bond was stable at pH 7.4, while rapid hydrolysis was observed in acidic pH environments. As-synthesized pH-C-mPEG was then linked with bPEI via the benzoic-imine linkage. The successful synthesis of pH-C-mPEG conjugated bPEI was confirmed by using 1H-NMR analysis (Figure 2(b)). Finally, the PS, pheophorbide-a (PPb-a), was conjugated with the primary amine group of the pH-C-mPEG and bPEI conjugates through carbodiimide coupling chemistry [20].


### 3.2. Characterization of the pH-NanoPM

The synthesized pH-PPS was further analyzed using a UV-Vis spectrophotometry. As shown in Figure3(a), the UV-Vis spectra of the pH-PPS presented dominant absorption bands at 400 and 670 nm, which originate from the PPb-a. These results indicate that the PPb-a molecules were successfully incorporated into the polymeric conjugates. The pH-NanoPM was a self-assembled form of nanomicellar aggregates in aqueous solution, assembled by their amphiphilicity. To confirm the critical aggregation concentration (CAC), the fluorescence emission spectrum of pyrene was measured in different concentrations of pH-PPS. Because the fluorescence of pyrene is influenced by environmental polarity changes, pyrene has been used to determine CAC values of amphiphilic polymers [22]. The fluorescent emission peaks of pyrene at 373 and 383 nm were denoted as I1 and I3, respectively. The I1/I3 ratio was used to measure the concentration at which the conjugates can self-assemble as nanoparticular structures. As shown in Figure 3(b), the CAC of the pH-NanoPM was found to be 0.01 mg/mL at pH 7.4, indicating that the stable nanoparticular structure remains above this concentration. Additionally, it is worth noting that the pH-NanoPM exhibited good drug loading efficiency (drug loading contents (wt%): 3.9 ± 0.5% doxorubicin). This result indicates that the developed pH-Nano PM can be used not only as a photomedicine but also as a drug-delivery carrier. To assess the photo-activity of the pH-NanoPM, singlet oxygen generation ability was monitored using DMA, the fluorescent intensity of which is highly quenched upon selective reaction with singlet oxygen [25]. The pH-NanoPM dissolved in DMF solution was irradiated using a 670 nm laser for different lengths of time and then the amount of singlet oxygen generated was determined by the amount of DMA fluorescence quenched. As shown in Figure 3(c), the relative fluorescence intensity of DMA from the pH-PPS solution gradually decreased with increasing exposure time with a reduction level of ~40% after 3 min exposure. No significant differences in DMA reduction levels were observed between the pH-PPS and free PPb-a, suggesting that the pH-PPS retains the singlet oxygen generation ability after conjugation with the polymer. To determine the effect of pH on the pH-cleavable linker benzoic-imine, particle size distribution changes were monitored under different pH conditions. The pH-NanoPM particles were found to have a size of ~110 nm with a narrow size distribution at pH 7.4, the physiological pH of the bloodstream. The pH-NanoPM particles were found to be smaller (~40 nm) at pH 6.5, the acidic tumor pH. This indicates that the PEG molecules on the surface of pH-NanoPM were successfully detached due to the cleavage of the benzoic-imine linker at acidic pH.Figure 3
Physicochemical characterization of the pH-NanoPM. (a) UV-Vis absorption spectra of free pheophorbide-a (PPb-a) and pH-PPS. (b) Analysis of the critical aggregate concentration (CAC) of pH-PPS (Inset: fluorescent emission spectra of pyrene in polymer dissolved water). (c) Measurement of singlet oxygen generation of free PPb-a and pH-PPS in DMF with laser irradiation. (d) Particle size distribution of pH-NanoPM particles at different pH values (pH 7.4 and 6.5).
(a)
(b)
(c)
(d)


### 3.3. pH-Responsive Physical Property Changes of the pH-NanoPM

As discussed previously, the pH-NanoPM was designed to enable detachment of the PEG shell and conversion of surface charge from negative to positive at the tumor site for efficient cellular internalization. To confirm the surface charge conversion ability of the pH-NanoPM, the zeta-potential of the particles was observed under different pH conditions. As shown in Figure4(a), the pH-NanoPM had a slightly negatively charged surface at physiological pH (zeta-potential value = −1.89±3.20 mV). In general, negatively charged nanoparticles are stable and tend not to undesirably aggregate with serum proteins in the bloodstream [9]. The surface charge of the pH-NanoPM increased to +18.67±1.95 mV at pH 6.5. To further investigate the chemical cleavage of the pH-cleavable linker, primary amine groups in the pH-NanoPM were quantitatively measured at different pH values using fluorescamine which is an amine-specific fluorescent probe. The fluorescamine results (Figure 4(b)) showed that the pH-NanoPM contains ~50% free amine groups at pH 7.4. The primary amine contents of pH-NanoPM increased significantly to ~90% at pH 6.5, suggesting that the free primary amines in the pH-NanoPM are exposed by successful cleavage of the pH-responsive benzoic-imine linker. These results demonstrate that the PEG shells are successfully detached from the pH-NanoPM by the cleavage of the pH-responsive cleavable linker at acidic pH and that physical properties might lead to a microenvironment-specific delivery.Figure 4
pH-responsive physical property changes of the pH-NanoPM. (a) Zeta-potential measurement of the pH-NanoPM at different pH values (pH 7.4 and 6.5). (b) Quantitative measurement of exposed amine groups in different pH values as determined by fluorescamine assay (pH 7.4 and 6.5).
(a)
(b)


### 3.4. pH-Responsive Cellular Internalization of the pH-NanoPM

Having demonstrated that the PEG shell on the surface of the pH-NanoPM is capable of detachment at weak acidic pH and the subsequent exposure of the cationic amine groups of bPEI, the cellular internalization of the pH-NanoPM was monitored in a cancer cell line. HeLa, a cervical cancer cell line, was used in this study. The HeLa cells were incubated with the pH-NanoPM particles at pH 7.4 or 6.5, and the cellular uptake and subcellular localization of particles were determined using flow cytometry and confocal laser scanning microscopy (CLSM), respectively. According to our previous reports [9, 12], the pH change of cell media does not influence the cellular uptake behavior of nanoparticles itself. In this study, a noncleavable linker containing group was not included because their uptake behavior has already been reported [17, 18]: the noncleavable PEG containing micelles showed low cellular internalization behavior regardless of pH value change. PEG, a hydrophilic polymer, is well known to be biocompatible and nonimmunogenic and to improve pharmacokinetics [26, 27]. For those reasons, PEG has been used to impart a steric barrier on delivery carriers resulting in reduced reticuloendothelial system (RES) uptake and enhanced blood circulation time. However, it has been reported that the physical properties of PEG also reduce tumor cell uptake. As shown in Figure 5(a), fewer than 6% of pH-NanoPM particles were internalized at pH 7.4, indicating that the PEG shell of the nanoparticles hinders their cellular uptake capacity. Under acidic tumor pH (pH 6.5), much greater cellular uptake was observed (>95%) compared to cells incubated with the particles at pH 7.4. This result is consistent with previous reports [17, 18] and suggests that the detachment of the PEG shell from the pH-NanoPM particles at pH 6.5 led to enhanced cellular internalization of the nanoparticles for targeted cancer therapy. In addition to the uptake properties, the cellular localization of the pH-NanoPM particles was observed by CLSM. As shown in Figure 5(b), the pH-NanoPM particles were located mainly within the cytoplasm. The signals from the PPb-a of the pH-NanoPM and the DAPI-stained nuclei are depicted in cyan and blue, respectively. Furthermore, Figure 5(b) clearly shows that a few pH-NanoPM particles were delivered to nuclei as well, which is desirable for an efficient anticancer therapeutic effect.Figure 5
In vitro cellular internalization of the pH-NanoPM. (a) Flow cytometry quantification of the cellular internalization of the pH-NanoPM at different pH values (pH 7.4 and 6.5). (b) Confocal microscopy image of HeLa cells treated with the pH-NanoPM (Scale bars: 50 μm).
(a)
(b)


### 3.5.In Vitro Cytotoxicity of pH-NanoPM at Different pH

After we confirmed the differential intracellular uptake of the pH-NanoPM under different pH conditions, we determined the photo-mediated anticancer therapeutic effect. HeLa cells were treated with the pH-NanoPM at pH 7.4 or 6.5 and were irradiated with a 670 nm laser (3.6 J/cm−2, n=4). Cell viabilities at different pH values were measured using an MTT assay. The quantified cell viability results showed that there is a significant cell killing effect with pH-NanoPM treatment at weak acidic pH. As shown in Figure 6, under no laser irradiation, the pH-NanoPM showed no cytotoxicity at pH 7.4, suggesting the biocompatibility of the synthesized polymer. The cells treated with the particles at pH 6.5 showed a slightly reduced level of viability, which might be due to the surface charge change of the pH-NanoPM from negative to positive by the deshielding of the PEG layer. It is well known that positively charged nanoparticles have cytotoxicity due to their cationic charge inducing membrane damage [28, 29]. Under laser irradiation, the pH-NanoPM at pH 7.4 showed faint cancer treatment efficiency with a viability of 90.12±4.44%, which correlates with the reduced uptake at physiological pH, while the cells treated with the pH-NanoPM at pH 6.5 and irradiation had a viability of 29.42±11.82%. These results clearly demonstrate that the pH-mediated detachment of PEG layer of the pH-NanoPM leads to enhanced internalization and ultimately successful photo-mediated cancer treatment.Figure 6
In vitro cytotoxicity test of the pH-NanoPM at different pH values: HeLa cells treated with the pH-NanoPM at pH 7.4 and 6.5 (dose of PPb-a: 1.6 × 10−5M, and laser power: 3.6 J/cm−2, n=4, p∗<0.001).


## 3.1. Synthesis and Preparation of the pH-NanoPM

In this study, a novel pH-responsive polymeric photosensitizer (pH-PPS) was designed and synthesized as shown in Figure2(a). First, pH-cleavable methoxypolyethylene glycol (pH-C-mPEG) was synthesized by incorporation of 4-formylbenzoic acid, which formed a benzoic-imine linkage with primary amine groups. The hydrolysis kinetics and hydrolysis bonding equilibrium of an imine bond are significantly influenced by the environmental pH [17, 18, 24]. According to previous reports [17, 18], the benzoic-imine bond was stable at pH 7.4, while rapid hydrolysis was observed in acidic pH environments. As-synthesized pH-C-mPEG was then linked with bPEI via the benzoic-imine linkage. The successful synthesis of pH-C-mPEG conjugated bPEI was confirmed by using 1H-NMR analysis (Figure 2(b)). Finally, the PS, pheophorbide-a (PPb-a), was conjugated with the primary amine group of the pH-C-mPEG and bPEI conjugates through carbodiimide coupling chemistry [20].


## 3.2. Characterization of the pH-NanoPM

The synthesized pH-PPS was further analyzed using a UV-Vis spectrophotometry. As shown in Figure3(a), the UV-Vis spectra of the pH-PPS presented dominant absorption bands at 400 and 670 nm, which originate from the PPb-a. These results indicate that the PPb-a molecules were successfully incorporated into the polymeric conjugates. The pH-NanoPM was a self-assembled form of nanomicellar aggregates in aqueous solution, assembled by their amphiphilicity. To confirm the critical aggregation concentration (CAC), the fluorescence emission spectrum of pyrene was measured in different concentrations of pH-PPS. Because the fluorescence of pyrene is influenced by environmental polarity changes, pyrene has been used to determine CAC values of amphiphilic polymers [22]. The fluorescent emission peaks of pyrene at 373 and 383 nm were denoted as I1 and I3, respectively. The I1/I3 ratio was used to measure the concentration at which the conjugates can self-assemble as nanoparticular structures. As shown in Figure 3(b), the CAC of the pH-NanoPM was found to be 0.01 mg/mL at pH 7.4, indicating that the stable nanoparticular structure remains above this concentration. Additionally, it is worth noting that the pH-NanoPM exhibited good drug loading efficiency (drug loading contents (wt%): 3.9 ± 0.5% doxorubicin). This result indicates that the developed pH-Nano PM can be used not only as a photomedicine but also as a drug-delivery carrier. To assess the photo-activity of the pH-NanoPM, singlet oxygen generation ability was monitored using DMA, the fluorescent intensity of which is highly quenched upon selective reaction with singlet oxygen [25]. The pH-NanoPM dissolved in DMF solution was irradiated using a 670 nm laser for different lengths of time and then the amount of singlet oxygen generated was determined by the amount of DMA fluorescence quenched. As shown in Figure 3(c), the relative fluorescence intensity of DMA from the pH-PPS solution gradually decreased with increasing exposure time with a reduction level of ~40% after 3 min exposure. No significant differences in DMA reduction levels were observed between the pH-PPS and free PPb-a, suggesting that the pH-PPS retains the singlet oxygen generation ability after conjugation with the polymer. To determine the effect of pH on the pH-cleavable linker benzoic-imine, particle size distribution changes were monitored under different pH conditions. The pH-NanoPM particles were found to have a size of ~110 nm with a narrow size distribution at pH 7.4, the physiological pH of the bloodstream. The pH-NanoPM particles were found to be smaller (~40 nm) at pH 6.5, the acidic tumor pH. This indicates that the PEG molecules on the surface of pH-NanoPM were successfully detached due to the cleavage of the benzoic-imine linker at acidic pH.Figure 3
Physicochemical characterization of the pH-NanoPM. (a) UV-Vis absorption spectra of free pheophorbide-a (PPb-a) and pH-PPS. (b) Analysis of the critical aggregate concentration (CAC) of pH-PPS (Inset: fluorescent emission spectra of pyrene in polymer dissolved water). (c) Measurement of singlet oxygen generation of free PPb-a and pH-PPS in DMF with laser irradiation. (d) Particle size distribution of pH-NanoPM particles at different pH values (pH 7.4 and 6.5).
(a)
(b)
(c)
(d)


## 3.3. pH-Responsive Physical Property Changes of the pH-NanoPM

As discussed previously, the pH-NanoPM was designed to enable detachment of the PEG shell and conversion of surface charge from negative to positive at the tumor site for efficient cellular internalization. To confirm the surface charge conversion ability of the pH-NanoPM, the zeta-potential of the particles was observed under different pH conditions. As shown in Figure4(a), the pH-NanoPM had a slightly negatively charged surface at physiological pH (zeta-potential value = −1.89±3.20 mV). In general, negatively charged nanoparticles are stable and tend not to undesirably aggregate with serum proteins in the bloodstream [9]. The surface charge of the pH-NanoPM increased to +18.67±1.95 mV at pH 6.5. To further investigate the chemical cleavage of the pH-cleavable linker, primary amine groups in the pH-NanoPM were quantitatively measured at different pH values using fluorescamine which is an amine-specific fluorescent probe. The fluorescamine results (Figure 4(b)) showed that the pH-NanoPM contains ~50% free amine groups at pH 7.4. The primary amine contents of pH-NanoPM increased significantly to ~90% at pH 6.5, suggesting that the free primary amines in the pH-NanoPM are exposed by successful cleavage of the pH-responsive benzoic-imine linker. These results demonstrate that the PEG shells are successfully detached from the pH-NanoPM by the cleavage of the pH-responsive cleavable linker at acidic pH and that physical properties might lead to a microenvironment-specific delivery.Figure 4
pH-responsive physical property changes of the pH-NanoPM. (a) Zeta-potential measurement of the pH-NanoPM at different pH values (pH 7.4 and 6.5). (b) Quantitative measurement of exposed amine groups in different pH values as determined by fluorescamine assay (pH 7.4 and 6.5).
(a)
(b)


## 3.4. pH-Responsive Cellular Internalization of the pH-NanoPM

Having demonstrated that the PEG shell on the surface of the pH-NanoPM is capable of detachment at weak acidic pH and the subsequent exposure of the cationic amine groups of bPEI, the cellular internalization of the pH-NanoPM was monitored in a cancer cell line. HeLa, a cervical cancer cell line, was used in this study. The HeLa cells were incubated with the pH-NanoPM particles at pH 7.4 or 6.5, and the cellular uptake and subcellular localization of particles were determined using flow cytometry and confocal laser scanning microscopy (CLSM), respectively. According to our previous reports [9, 12], the pH change of cell media does not influence the cellular uptake behavior of nanoparticles itself. In this study, a noncleavable linker containing group was not included because their uptake behavior has already been reported [17, 18]: the noncleavable PEG containing micelles showed low cellular internalization behavior regardless of pH value change. PEG, a hydrophilic polymer, is well known to be biocompatible and nonimmunogenic and to improve pharmacokinetics [26, 27]. For those reasons, PEG has been used to impart a steric barrier on delivery carriers resulting in reduced reticuloendothelial system (RES) uptake and enhanced blood circulation time. However, it has been reported that the physical properties of PEG also reduce tumor cell uptake. As shown in Figure 5(a), fewer than 6% of pH-NanoPM particles were internalized at pH 7.4, indicating that the PEG shell of the nanoparticles hinders their cellular uptake capacity. Under acidic tumor pH (pH 6.5), much greater cellular uptake was observed (>95%) compared to cells incubated with the particles at pH 7.4. This result is consistent with previous reports [17, 18] and suggests that the detachment of the PEG shell from the pH-NanoPM particles at pH 6.5 led to enhanced cellular internalization of the nanoparticles for targeted cancer therapy. In addition to the uptake properties, the cellular localization of the pH-NanoPM particles was observed by CLSM. As shown in Figure 5(b), the pH-NanoPM particles were located mainly within the cytoplasm. The signals from the PPb-a of the pH-NanoPM and the DAPI-stained nuclei are depicted in cyan and blue, respectively. Furthermore, Figure 5(b) clearly shows that a few pH-NanoPM particles were delivered to nuclei as well, which is desirable for an efficient anticancer therapeutic effect.Figure 5
In vitro cellular internalization of the pH-NanoPM. (a) Flow cytometry quantification of the cellular internalization of the pH-NanoPM at different pH values (pH 7.4 and 6.5). (b) Confocal microscopy image of HeLa cells treated with the pH-NanoPM (Scale bars: 50 μm).
(a)
(b)


## 3.5.In Vitro Cytotoxicity of pH-NanoPM at Different pH

After we confirmed the differential intracellular uptake of the pH-NanoPM under different pH conditions, we determined the photo-mediated anticancer therapeutic effect. HeLa cells were treated with the pH-NanoPM at pH 7.4 or 6.5 and were irradiated with a 670 nm laser (3.6 J/cm−2, n=4). Cell viabilities at different pH values were measured using an MTT assay. The quantified cell viability results showed that there is a significant cell killing effect with pH-NanoPM treatment at weak acidic pH. As shown in Figure 6, under no laser irradiation, the pH-NanoPM showed no cytotoxicity at pH 7.4, suggesting the biocompatibility of the synthesized polymer. The cells treated with the particles at pH 6.5 showed a slightly reduced level of viability, which might be due to the surface charge change of the pH-NanoPM from negative to positive by the deshielding of the PEG layer. It is well known that positively charged nanoparticles have cytotoxicity due to their cationic charge inducing membrane damage [28, 29]. Under laser irradiation, the pH-NanoPM at pH 7.4 showed faint cancer treatment efficiency with a viability of 90.12±4.44%, which correlates with the reduced uptake at physiological pH, while the cells treated with the pH-NanoPM at pH 6.5 and irradiation had a viability of 29.42±11.82%. These results clearly demonstrate that the pH-mediated detachment of PEG layer of the pH-NanoPM leads to enhanced internalization and ultimately successful photo-mediated cancer treatment.Figure 6
In vitro cytotoxicity test of the pH-NanoPM at different pH values: HeLa cells treated with the pH-NanoPM at pH 7.4 and 6.5 (dose of PPb-a: 1.6 × 10−5M, and laser power: 3.6 J/cm−2, n=4, p∗<0.001).


## 4. Conclusions

The pH-NanoPM presented herein was designed to respond to an acidic tumor extracellular pH to accomplish a targeted photodynamic cancer therapy. At weak acidic pH, the successful cleavage of the pH-responsive linker (i.e., benzoic-imine) was confirmed by chemical analysis. Consequently, the hydrophilic PEG shell that physically hinders cellular internalization was detached from the nanoparticles, which led to a switch in the charge of the particles from negative to positive and a decrease in the size of the pH-NanoPM particles. With these desirable properties, the pH-NanoPM exhibited enhanced cellular internalization at acidic tumor pH compared to that at normal pH, resulting in a significant cancer cell killing effect. These results suggest that this system has the potential to be used as a new class of nanophotomedicine for targeted photodynamic cancer therapy. Given the promising results of these initialin vitro studies, further demonstration is now expected to examine their therapeutic effectivenessin vivo.



---

*Source: 3739723-2016-03-29.xml*