# Effect of Rubberwood Content on Biodegradability of Poly(butylene succinate) Biocomposites

Authors: Hemhong Anankaphong; Duanghathai Pentrakoon; Jirawut Junkasem
Journal: International Journal of Polymer Science
 (2015)

---

## Abstract

Poly(butylene succinate) (PBS) biocomposites incorporated with rubberwood powder (RWP) were fabricated with various RWP weight fractions (i.e., 0 to 40% wt) by injection moulding process. The soil burial test was employed to examine the biodegradability of such biocomposites under outdoor environment for 60 days. The physical appearance, percentage weight loss, chemical structure, and mechanical properties before and after the soil burial test were determined. Apparent changes in physical appearance of the biocomposites from optical micrographs were detected in terms of surface morphology and colour. The percentage of crystallinity of PBS/RWP biocomposites was studied by the X-ray diffraction (XRD) technique, and the XRD pattern revealed a decrease in percentage of crystallinity due to enhancing RWP weight fractions. This may be attributed to a presence of rubberwood powders providing more disordered molecular chain arrangement of PBS matrix and also an agglomeration of the rubberwood powder content at greater concentration as seen in SEM micrographs. With increasing RWP weight fractions and burial time, the results exhibited a considerable change in chemical structure (essentially ester linkage due to biodegradation mechanism of PBS), relatively greater percentage weight loss, and a substantial decrease in flexural properties. Consequently, the results indicate that incorporating RWP enhances biodegradability of PBS/RWP biocomposites; that is, the biodegradation rate of biocomposites increases with increasing RWP weight fractions and burial time.


---

## Body

## 1. Introduction

With a considerable emphasis on environmental concerns about an enormous plastic consumption in recent years, the concerns about usage and disposal are diverse, for example, an accumulation of waste in landfills and in natural habitats, the leaching of chemicals from plastic products, and the potential for plastics to transfer chemicals to wildlife and humans [1–3]. Biocomposites (i.e., environmentally friendly composite materials) have received substantial attention from industries and academic circles as evidenced by numerous patents and research publications [4–16].Typically, biocomposites are composite materials comprising one or more phase(s) derived from a biological origin, for example, a composition between nonbiodegradable/biodegradable polymers as matrix and biodegradable natural fibres [8, 17]. As a consequence of environmental issues, the biodegradable polymers have received enormous attention because they provide complete degradation in soil or by composting process and hardly release any harmful elements [7, 10, 18].Amid current commercially available biodegradable polymers, poly(butylene succinate) (PBS) happens to be attractive on account of its excellent biodegradability in nature like in soil, lake sea, and compost, excellent processability, being processible by most of conventional plastics processing machines, good thermal stability and high toughness related to its low glass transition, good thermal and chemical resistance, and being entirely combustible by fire without any toxic gases [8, 10, 15, 19–21]. PBS is an aliphatic polyester, which can be synthesized through the polycondensation reaction of 1,4-butanediol and succinic acid [9]. PBS can degrade under natural environment by bacteria and fungi [1, 12]. This is attributed to PBS chemical structure containing hydrolysable linkage along polymer backbone chain where it is a biodegradable mechanism initiated by hydrolysis mechanism at ester linkage [22]. General mechanism of polymer biodegradation is breaking polymer chain into small molecules (e.g., oligomers, dimers, and monomers) by enzymes or the environmental factors such as temperature, humidity, pH, and sunlight. Then, small molecules are transported inside the microorganism cell to be utilized as carbon and energy sources. The end products of mineralization are CO2, H2O, CH4, and microbial biomass [23]. PBS has been used in many applications replacing conventional plastic such as mulch film, bags, cups, and packaging film [24].Natural biobased filler incorporated biodegradable polymers have attracted a great deal of interest owing to the naturally degradable materials into the soil burial environment [9, 25]. Besides, the natural biobased filler has several advantages over inorganic fillers, such as renewability, low cost, low density, lower CO2 emission, biodegradability, and ecofriendliness [14, 26]. In recent years, there have been many researches with reference to PBS incorporated with lignocellulosic materials as natural filler, such as lignin, coconut, rice husk, bamboo, coir, and wood [14, 14, 27, 28]. Thailand appears to be one of the world’s largest producers of rubberwood products, for example, furniture, toys, and particle boards. During the production, many sawdust wastes are generated and become burden to the manufacturer, for example, environmental pollution, and generating additional operation cost. Hence, some attempts have been made to use rubber sawdust as filler in polymer composites [29–31], however; the biodegradability of a composition between rubber sawdust and nonbiodegradable polymer has barely been studied.In this research, biodegradability of neat PBS and PBS/RWP biocomposites via soil burial test was studied under outdoor environment for 60 days. The physical appearance, percentage weight loss, chemical structure, and mechanical properties before and after the soil burial test were determined. As reported regarding the percentage of crystallinity influencing the biodegradability and mechanical properties [32, 33], hence, the percentage of crystallinity of the neat PBS and PBS/RWP biocomposites was studied by the X-ray diffraction (XRD) technique.


## 2. Experimental

### 2.1. Materials

Poly(butylene succinate) (PBS, density of 1.26 g/cm3; MFI = 40 g/10 min at load of 21.18 N, 190°C) was supplied by Mitsubishi Chemical (Thailand) Company Limited. Rubberwood powders (RWP) having a particle size of 80 Mesh were supplied by Suppaisarn Thai Wood Powder Company Limited (Bangkok, Thailand).


### 2.2. Biocomposite Preparation

The PBS pellets were dried at 80°C in a vacuum oven for 24 hours prior to mixing. A specified content of PBS/RWP compounds (i.e., 5%, 10%, 20%, 30%, and 40% wt) was mixed with PBS in a LTE-26-44, Labtech twin screw extruder at a screw speed of 30 rpm and temperature profile of extruder from 140°C to 175°C. The extrudate strands were cooled in a water bath and then pelletized.Prior to biocomposite fabrication, the PBS/RWP compound pellets were dried at 60°C in a vacuum oven for 24 hours. Subsequently, the samples were fabricated using an injection moulding machine (HM 65/210s, Battenfeld) at 150 rpm injection speed, 150-bar injection pressure, temperature profile from 135°C to 145°C, and 25-second cooling time.


### 2.3. Characterization

To assess the percentage of crystallinity of the neat PBS and PBS/RWP compounds, X-ray diffraction (XRD) analysis (D8, Bruker AXS) with Cu Ka radiation (0.154 nm) was conducted 1 time/sample. Composites were scanned under diffraction angle2θ in the range of 5 to 40° using fixed time mode with step interval of 0.02°.The chemical structure of biocomposites was characterized by attenuated total reflection mode or FTIR-ATR (NICOLET 6700, Thermo scientific). The FTIR spectra were recorded in a range of 400–4000 cm−1 with a resolution of 4.0 cm−1 and scanning 64 scans. Carbonyl index was calculated by the following [34]:(1)Carbonyl  IndexCI=I1712I1420,where I1712 is the peak intensity at 1712 cm−1 representing C=O stretching of ester linkage and I1420 is the peak intensity at 1420 cm−1 representing a stretching of methyl group, which was chosen as the reference peak.Besides, the morphology of impact fractured surface of the neat PBS and biocomposites was investigated using a Scanning Electron Microscope (JSM-6480LV, JEOL). The specimens were coated with a thin layer of gold before viewing on the SEM. The micrographs at 500x and 3000x magnification with an accelerating voltage of 15 kV were obtained.


### 2.4. Soil Burial Test

The 2.5 × 12.7 × 3.3 mm sample dimension was used for biodegradability test. The samples were buried beneath the farmland soil containing 0.35% nitrogen, 0.10% phosphorous, 1.37% potassium, and pH of 6.69 in the flower pot. The soil burial test procedure in this research was conducted with reference to the previous researches [19, 34, 35]. The samples were positioned at 6 cm depth from the top soil surface and 3 cm above the inner bottom pot. The test was carried out under outdoor environment avoiding ultraviolet (UV) light for 60 days with the following condition: watering 500 mL every 48 hours to control humidity. Ten day interval, five specimens of each formula were collected, cleaned, and dried at 60°C for 6 hours. Subsequently, the physical appearance, percentage weight loss, chemical structure, and flexural properties were determined.


### 2.5. Physical Appearance and Percentage Weight Loss Observation

The optical microscope (Olympus CX31, E for L) with 20x magnification was employed to examine the physical appearance (e.g., surface morphology and colour) before and after the soil burial test.The percentage weight loss of biocomposites was measured using an electronic balance and calculated by using the following:(2)Weight  loss%=Wi-WfWi×100,where Wi and Wf are the weight (g) of specimen before and after soil burial test, respectively.


### 2.6. Flexural Properties

The flexural properties of the neat PBS and PBS/RWP biocomposites were determined in line with ASTM D790. Lloyd L500 Universal Testing Machine (Fareham, UK) was used with 10 kN load cell and 13 mm/min crosshead speed. A three-point loading system with a total span length of 50 mm was performed at the ambient temperature. At least five specimens for each sample were employed.


## 2.1. Materials

Poly(butylene succinate) (PBS, density of 1.26 g/cm3; MFI = 40 g/10 min at load of 21.18 N, 190°C) was supplied by Mitsubishi Chemical (Thailand) Company Limited. Rubberwood powders (RWP) having a particle size of 80 Mesh were supplied by Suppaisarn Thai Wood Powder Company Limited (Bangkok, Thailand).


## 2.2. Biocomposite Preparation

The PBS pellets were dried at 80°C in a vacuum oven for 24 hours prior to mixing. A specified content of PBS/RWP compounds (i.e., 5%, 10%, 20%, 30%, and 40% wt) was mixed with PBS in a LTE-26-44, Labtech twin screw extruder at a screw speed of 30 rpm and temperature profile of extruder from 140°C to 175°C. The extrudate strands were cooled in a water bath and then pelletized.Prior to biocomposite fabrication, the PBS/RWP compound pellets were dried at 60°C in a vacuum oven for 24 hours. Subsequently, the samples were fabricated using an injection moulding machine (HM 65/210s, Battenfeld) at 150 rpm injection speed, 150-bar injection pressure, temperature profile from 135°C to 145°C, and 25-second cooling time.


## 2.3. Characterization

To assess the percentage of crystallinity of the neat PBS and PBS/RWP compounds, X-ray diffraction (XRD) analysis (D8, Bruker AXS) with Cu Ka radiation (0.154 nm) was conducted 1 time/sample. Composites were scanned under diffraction angle2θ in the range of 5 to 40° using fixed time mode with step interval of 0.02°.The chemical structure of biocomposites was characterized by attenuated total reflection mode or FTIR-ATR (NICOLET 6700, Thermo scientific). The FTIR spectra were recorded in a range of 400–4000 cm−1 with a resolution of 4.0 cm−1 and scanning 64 scans. Carbonyl index was calculated by the following [34]:(1)Carbonyl  IndexCI=I1712I1420,where I1712 is the peak intensity at 1712 cm−1 representing C=O stretching of ester linkage and I1420 is the peak intensity at 1420 cm−1 representing a stretching of methyl group, which was chosen as the reference peak.Besides, the morphology of impact fractured surface of the neat PBS and biocomposites was investigated using a Scanning Electron Microscope (JSM-6480LV, JEOL). The specimens were coated with a thin layer of gold before viewing on the SEM. The micrographs at 500x and 3000x magnification with an accelerating voltage of 15 kV were obtained.


## 2.4. Soil Burial Test

The 2.5 × 12.7 × 3.3 mm sample dimension was used for biodegradability test. The samples were buried beneath the farmland soil containing 0.35% nitrogen, 0.10% phosphorous, 1.37% potassium, and pH of 6.69 in the flower pot. The soil burial test procedure in this research was conducted with reference to the previous researches [19, 34, 35]. The samples were positioned at 6 cm depth from the top soil surface and 3 cm above the inner bottom pot. The test was carried out under outdoor environment avoiding ultraviolet (UV) light for 60 days with the following condition: watering 500 mL every 48 hours to control humidity. Ten day interval, five specimens of each formula were collected, cleaned, and dried at 60°C for 6 hours. Subsequently, the physical appearance, percentage weight loss, chemical structure, and flexural properties were determined.


## 2.5. Physical Appearance and Percentage Weight Loss Observation

The optical microscope (Olympus CX31, E for L) with 20x magnification was employed to examine the physical appearance (e.g., surface morphology and colour) before and after the soil burial test.The percentage weight loss of biocomposites was measured using an electronic balance and calculated by using the following:(2)Weight  loss%=Wi-WfWi×100,where Wi and Wf are the weight (g) of specimen before and after soil burial test, respectively.


## 2.6. Flexural Properties

The flexural properties of the neat PBS and PBS/RWP biocomposites were determined in line with ASTM D790. Lloyd L500 Universal Testing Machine (Fareham, UK) was used with 10 kN load cell and 13 mm/min crosshead speed. A three-point loading system with a total span length of 50 mm was performed at the ambient temperature. At least five specimens for each sample were employed.


## 3. Results and Discussion

### 3.1. X-Ray Diffraction Analysis

X-ray diffraction analyses were conducted to investigate the crystallographic nature of the neat PBS and PBS/RWP biocomposites. The X-ray diffractograms of the neat PBS and PBS/RWP biocomposites, presented in Figure1, exhibit a typical peak of semicrystalline structure of PBS, that is, two speculate diffraction peaks located at 2θ = 19.74° and 2θ = 22.56° [36].Figure 1
X-ray diffractograms of PBS and PBS/RWP biocomposites.It can be observed that the intensity peak of PBS/RWP biocomposites decreases and becomes somewhat broader with increasing the rubberwood powder content. This reveals that an increase of rubberwood powder content results in a decrease of the percentage of crystallinity, as displayed in Table1. This may be attributed to the presence of rubberwood powders interrupting the arrangement of the molecular chains of PBS matrix (i.e., providing more disordered arrangement). With increase in the rubberwood powder content, a greater loss of its crystallinity is observed, particularly as rubberwood powder content greater than 20. This may be due to an agglomeration of the rubberwood powders at higher concentration as SEM micrographs result.Table 1
Percentage of crystallinity of the neat PBS and PBS/RWP biocomposites.
PBS
PBS/RWP5
PBS/RWP10
PBS/RWP20
PBS/RWP30
PBS/RWP40
Crystallinity (%)
44.7
39.6
38.9
39.6
36.9
34.5The argument of the agglomeration of the rubberwood powders at higher concentration is supported by the SEM micrographs of the neat PBS and PBS/RWP biocomposites at magnifications 500x and 3000x as shown in Table2. The neat PBS exhibits smooth surface. As increasing the rubberwood powder content, a slightly greater numbers of holes are found, and rough surface is exhibited at high rubberwood powder loading. This is because the PBS matrix may be not enough to encapsulate wood particles and the particle size of wood increases due to the agglomeration of wood particle. It is observable that an average rubberwood particle dimension increases from approximately 50 microns for PBS/RWP5, PBS/RWP10, and PBS/RWP20 biocomposites to around 100 microns for PBS/RWP30 and PBS/RWP40 biocomposites.Table 2
SEM micrographs of the neat PBS and PBS/RWP biocomposites.
Magnification
PBS
PBS/RWP5
PBS/RWP10
PBS/RWP20
PBS/RWP30
PBS/RWP40
500x
3000x


### 3.2. Physical Appearance and Percentage Weight Loss Analysis after Soil Burial Testing

Optical micrographs of the neat PBS and PBS/RWP biocomposites surface before and after soil burial test for 60 days at 20x magnification are illustrated in Table3. Prior to the soil burial test, the neat PBS shows a relatively smooth surface whereas the PBS/RWP biocomposites surface appears to show more impurities with increase in the rubberwood powder content. This may be ascribed to an inadequate compatibility between the hydrophilic RWP and the hydrophobic PBS [37, 38].Table 3
Optical micrographs of the neat PBS and PBS/RWP biocomposites.
Burial time
PBS
PBS/RWP5
PBS/RWP10
PBS/RWP20
PBS/RWP30
PBS/RWP40
0 days
10 days
20 days
30 days
40 days
50 days
60 daysFollowing 60-day soil burial test, an insignificant change in physical appearance was observed for the neat PBS, PBS/RWP5, PBS/RWP10, and PBS/RWP20 biocomposites. Meanwhile, for PBS/RWP30 and PBS/RWP40 biocomposites revealed more obvious changes, such as rougher surface and more cavities and cracks spreading on the sample surface. The presence of cavities on the fractured surfaces of PBS/RWP biocomposites resulted from an elimination of some rubberwood powder phase. This indicates that the biodegradability of these biocomposites primarily originated from the rubberwood powder phase, which is a hydrophilic nature and a hydrobiodegradable characteristic of PBS via hydrolysis mechanism [22, 39].Additionally, to observe the change of the neat PBS and PBS/RWP biocomposites after soil burial test for 60 days, the percentage weight loss of all samples was measured and shown in Figure2.Figure 2
Percentage weight loss of the neat PBS and PBS/RWP biocomposites.An apparent increase in percent weight loss was noticed for the PBS/RWP30 and PBS/RWP40 biocomposites after soil burial test from 20 days onward. These results are associated with the crystallinity values obtained by X-ray diffraction analysis, that is, greater weight loss as fewer the crystallinity value. This denotes that the percentage of crystallinity appears to be one of the crucial parameters influencing the biodegradation processes since the molecules in the amorphous region are loosely packed, thus making it more vulnerable to degradation [40, 41]. Moreover, the rate of hydrolysis is also affected by crystallinity due to the easy diffusion of water molecules into amorphous region [42]. This essentially corresponds to the previous research discoveries, which are the plastic chemical and physical properties having important roles in the biodegradation, for example, the surface conditions (surface area, hydrophilic and hydrophobic properties), the first-order structures (chemical structure, molecular weight, and molecular weight distribution), and the high order structures (glass transition temperature, melting temperature, modulus of elasticity, crystallinity, and crystal structure) of polymers processes [40].Furthermore, it can be observed that the surface color of PBS/RWP biocomposites faded after biodegradability test. This is owing to an elimination of hydrophilic extractive components, which are low molecular weight organic compounds contributing to colour and odor of woods [43].


### 3.3. Fourier Transform Infrared (FTIR) Analysis after Soil Burial Testing

The FTIR technique can be used to investigate a performance of hydrolysis of ester linkage in PBS phase via the carbonyl index value. Figure3 shows the FTIR-ATR spectra of the neat PBS at different soil burial time, presenting distinct peaks at around 1711 cm−1 indicating C=O stretching of ester linkage, 1220–1265 cm−1 indicating C-C-O stretching for the functional groups in the ester linkage of PBS, 1045–1149 cm−1 indicating O-C-C stretching vibration for the PBS, and 917 cm−1 for -C-OH bending in carboxylic acid groups [44, 45]. Following the soil burial test, a considerably reduced absorption intensity of C-C-O, O-C-C, and C=O stretching was observed.Figure 3
FTIR-ATR spectra of the neat PBS at different soil burial time.The carbonyl index values of the neat PBS are shown in Table4. It can be seen that the carbonyl index values decreased as the burial time increased. These results confirm that the chemical structures of PBS were changed after the compost burial test, mainly due to hydrolysis of the ester bonds, C-C-O and O-C-C, in the main chain [45].Table 4
The carbonyl index values of the neat PBS and the PBS/RWP biocomposites.
Carbonyl index (CI) at various burial times
0 days
10 days
20 days
30 days
40 days
50 days
60 days
PBS
3.70
3.47
3.21
3.18
3.16
2.95
3.04
PBS/RWP5
3.82
3.47
3.39
3.29
3.17
2.48
2.45
PBS/RWP10
3.97
3.29
2.89
2.72
2.75
2.48
2.31
PBS/RWP20
3.31
3.03
2.80
2.61
2.68
2.57
2.56
PBS/RWP30
3.41
2.87
2.65
2.55
2.56
2.35
2.24
PBS/RWP40
3.07
2.71
2.34
2.34
2.22
2.27
2.21Besides, it can be noticed that the carbonyl index values decreased due to enhancing rubberwood powder contents. This once more indicates a change in chemical structures as incorporating rubberwood powders. A similar behavior, that is, decreased as the burial time increased, was observed for the PBS/RWP biocomposites compared with the neat PBS. An example of FTIR-ATR spectra for the PBS/RWP biocomposites is shown in Figure4.Figure 4
FTIR-ATR spectra of the PBS/RWP40 biocomposites at different soil burial time.The spectra of PBS show peaks at 917 cm−1 for -C-OH bending in carboxylic acid groups, 1045 cm−1 for -O-C-C stretching vibration, 1144–1264 cm−1 for O-C-C stretching in ester linkages, 1330 cm−1 for symmetric deformational vibrations of -CH2- groups, 1710–1713 cm−1 for C=O stretching vibration of ester groups, and 2945 cm−1 for asymmetric deformational vibration of -CH2- groups [46]. Following the soil burial test, a considerably reduced absorption intensity of -CH2- groups (at 1324 cm−1) and O-C-C (at 1045 cm−1) was observed. This results from amorphous and crystalline cellulose degradation by bacteria and fungi in soil [45].


### 3.4. Mechanical Properties after Soil Burial Testing

The flexural properties (flexural strength, flexural modulus, and elongation at maximum load) of the neat PBS and PBS/RWP biocomposites before and after soil burial test for 60 days are shown in Figures5–7.Figure 5
Flexural strength of the neat PBS and PBS/RWP biocomposites as a function of burial time.Figure 6
Flexural modulus of the neat PBS and PBS/RWP biocomposites as a function of burial time.Figure 7
Elongation at maximum load of the neat PBS and PBS/RWP biocomposites as a function of burial time.As seen from Figures5–7, the flexural properties of the neat PBS barely changed with increase in the burial time, despite the fact that the carbonyl index reduced (i.e., indicating an occurrence of the hydrolysis of ester linkage in PBS phase). However, a significant drop in flexural strength and flexural modulus was observed for all of the PBS/RWP biocomposites as the soil burial time increased. These may be attributed to a presence of cavities on the fractured surfaces of PBS/RWP biocomposites as a result of the elimination of some rubberwood powder phase and hydrolysis mechanism of PBS phase, which were more apparent as the soil burial time increased from 20 days onward. This can also be supporting the results from the weight loss analysis (as shown in Figure 2). These results indicate two stages of PBS biodegradable mechanism, which are initially random cleavage of ester linkage leading to a decrease in molecular weight (probably a combination of rubberwood powder elimination and hydrolysis of ester linkage in PBS phase) that affects mechanical properties and then microorganism degradation.


## 3.1. X-Ray Diffraction Analysis

X-ray diffraction analyses were conducted to investigate the crystallographic nature of the neat PBS and PBS/RWP biocomposites. The X-ray diffractograms of the neat PBS and PBS/RWP biocomposites, presented in Figure1, exhibit a typical peak of semicrystalline structure of PBS, that is, two speculate diffraction peaks located at 2θ = 19.74° and 2θ = 22.56° [36].Figure 1
X-ray diffractograms of PBS and PBS/RWP biocomposites.It can be observed that the intensity peak of PBS/RWP biocomposites decreases and becomes somewhat broader with increasing the rubberwood powder content. This reveals that an increase of rubberwood powder content results in a decrease of the percentage of crystallinity, as displayed in Table1. This may be attributed to the presence of rubberwood powders interrupting the arrangement of the molecular chains of PBS matrix (i.e., providing more disordered arrangement). With increase in the rubberwood powder content, a greater loss of its crystallinity is observed, particularly as rubberwood powder content greater than 20. This may be due to an agglomeration of the rubberwood powders at higher concentration as SEM micrographs result.Table 1
Percentage of crystallinity of the neat PBS and PBS/RWP biocomposites.
PBS
PBS/RWP5
PBS/RWP10
PBS/RWP20
PBS/RWP30
PBS/RWP40
Crystallinity (%)
44.7
39.6
38.9
39.6
36.9
34.5The argument of the agglomeration of the rubberwood powders at higher concentration is supported by the SEM micrographs of the neat PBS and PBS/RWP biocomposites at magnifications 500x and 3000x as shown in Table2. The neat PBS exhibits smooth surface. As increasing the rubberwood powder content, a slightly greater numbers of holes are found, and rough surface is exhibited at high rubberwood powder loading. This is because the PBS matrix may be not enough to encapsulate wood particles and the particle size of wood increases due to the agglomeration of wood particle. It is observable that an average rubberwood particle dimension increases from approximately 50 microns for PBS/RWP5, PBS/RWP10, and PBS/RWP20 biocomposites to around 100 microns for PBS/RWP30 and PBS/RWP40 biocomposites.Table 2
SEM micrographs of the neat PBS and PBS/RWP biocomposites.
Magnification
PBS
PBS/RWP5
PBS/RWP10
PBS/RWP20
PBS/RWP30
PBS/RWP40
500x
3000x


## 3.2. Physical Appearance and Percentage Weight Loss Analysis after Soil Burial Testing

Optical micrographs of the neat PBS and PBS/RWP biocomposites surface before and after soil burial test for 60 days at 20x magnification are illustrated in Table3. Prior to the soil burial test, the neat PBS shows a relatively smooth surface whereas the PBS/RWP biocomposites surface appears to show more impurities with increase in the rubberwood powder content. This may be ascribed to an inadequate compatibility between the hydrophilic RWP and the hydrophobic PBS [37, 38].Table 3
Optical micrographs of the neat PBS and PBS/RWP biocomposites.
Burial time
PBS
PBS/RWP5
PBS/RWP10
PBS/RWP20
PBS/RWP30
PBS/RWP40
0 days
10 days
20 days
30 days
40 days
50 days
60 daysFollowing 60-day soil burial test, an insignificant change in physical appearance was observed for the neat PBS, PBS/RWP5, PBS/RWP10, and PBS/RWP20 biocomposites. Meanwhile, for PBS/RWP30 and PBS/RWP40 biocomposites revealed more obvious changes, such as rougher surface and more cavities and cracks spreading on the sample surface. The presence of cavities on the fractured surfaces of PBS/RWP biocomposites resulted from an elimination of some rubberwood powder phase. This indicates that the biodegradability of these biocomposites primarily originated from the rubberwood powder phase, which is a hydrophilic nature and a hydrobiodegradable characteristic of PBS via hydrolysis mechanism [22, 39].Additionally, to observe the change of the neat PBS and PBS/RWP biocomposites after soil burial test for 60 days, the percentage weight loss of all samples was measured and shown in Figure2.Figure 2
Percentage weight loss of the neat PBS and PBS/RWP biocomposites.An apparent increase in percent weight loss was noticed for the PBS/RWP30 and PBS/RWP40 biocomposites after soil burial test from 20 days onward. These results are associated with the crystallinity values obtained by X-ray diffraction analysis, that is, greater weight loss as fewer the crystallinity value. This denotes that the percentage of crystallinity appears to be one of the crucial parameters influencing the biodegradation processes since the molecules in the amorphous region are loosely packed, thus making it more vulnerable to degradation [40, 41]. Moreover, the rate of hydrolysis is also affected by crystallinity due to the easy diffusion of water molecules into amorphous region [42]. This essentially corresponds to the previous research discoveries, which are the plastic chemical and physical properties having important roles in the biodegradation, for example, the surface conditions (surface area, hydrophilic and hydrophobic properties), the first-order structures (chemical structure, molecular weight, and molecular weight distribution), and the high order structures (glass transition temperature, melting temperature, modulus of elasticity, crystallinity, and crystal structure) of polymers processes [40].Furthermore, it can be observed that the surface color of PBS/RWP biocomposites faded after biodegradability test. This is owing to an elimination of hydrophilic extractive components, which are low molecular weight organic compounds contributing to colour and odor of woods [43].


## 3.3. Fourier Transform Infrared (FTIR) Analysis after Soil Burial Testing

The FTIR technique can be used to investigate a performance of hydrolysis of ester linkage in PBS phase via the carbonyl index value. Figure3 shows the FTIR-ATR spectra of the neat PBS at different soil burial time, presenting distinct peaks at around 1711 cm−1 indicating C=O stretching of ester linkage, 1220–1265 cm−1 indicating C-C-O stretching for the functional groups in the ester linkage of PBS, 1045–1149 cm−1 indicating O-C-C stretching vibration for the PBS, and 917 cm−1 for -C-OH bending in carboxylic acid groups [44, 45]. Following the soil burial test, a considerably reduced absorption intensity of C-C-O, O-C-C, and C=O stretching was observed.Figure 3
FTIR-ATR spectra of the neat PBS at different soil burial time.The carbonyl index values of the neat PBS are shown in Table4. It can be seen that the carbonyl index values decreased as the burial time increased. These results confirm that the chemical structures of PBS were changed after the compost burial test, mainly due to hydrolysis of the ester bonds, C-C-O and O-C-C, in the main chain [45].Table 4
The carbonyl index values of the neat PBS and the PBS/RWP biocomposites.
Carbonyl index (CI) at various burial times
0 days
10 days
20 days
30 days
40 days
50 days
60 days
PBS
3.70
3.47
3.21
3.18
3.16
2.95
3.04
PBS/RWP5
3.82
3.47
3.39
3.29
3.17
2.48
2.45
PBS/RWP10
3.97
3.29
2.89
2.72
2.75
2.48
2.31
PBS/RWP20
3.31
3.03
2.80
2.61
2.68
2.57
2.56
PBS/RWP30
3.41
2.87
2.65
2.55
2.56
2.35
2.24
PBS/RWP40
3.07
2.71
2.34
2.34
2.22
2.27
2.21Besides, it can be noticed that the carbonyl index values decreased due to enhancing rubberwood powder contents. This once more indicates a change in chemical structures as incorporating rubberwood powders. A similar behavior, that is, decreased as the burial time increased, was observed for the PBS/RWP biocomposites compared with the neat PBS. An example of FTIR-ATR spectra for the PBS/RWP biocomposites is shown in Figure4.Figure 4
FTIR-ATR spectra of the PBS/RWP40 biocomposites at different soil burial time.The spectra of PBS show peaks at 917 cm−1 for -C-OH bending in carboxylic acid groups, 1045 cm−1 for -O-C-C stretching vibration, 1144–1264 cm−1 for O-C-C stretching in ester linkages, 1330 cm−1 for symmetric deformational vibrations of -CH2- groups, 1710–1713 cm−1 for C=O stretching vibration of ester groups, and 2945 cm−1 for asymmetric deformational vibration of -CH2- groups [46]. Following the soil burial test, a considerably reduced absorption intensity of -CH2- groups (at 1324 cm−1) and O-C-C (at 1045 cm−1) was observed. This results from amorphous and crystalline cellulose degradation by bacteria and fungi in soil [45].


## 3.4. Mechanical Properties after Soil Burial Testing

The flexural properties (flexural strength, flexural modulus, and elongation at maximum load) of the neat PBS and PBS/RWP biocomposites before and after soil burial test for 60 days are shown in Figures5–7.Figure 5
Flexural strength of the neat PBS and PBS/RWP biocomposites as a function of burial time.Figure 6
Flexural modulus of the neat PBS and PBS/RWP biocomposites as a function of burial time.Figure 7
Elongation at maximum load of the neat PBS and PBS/RWP biocomposites as a function of burial time.As seen from Figures5–7, the flexural properties of the neat PBS barely changed with increase in the burial time, despite the fact that the carbonyl index reduced (i.e., indicating an occurrence of the hydrolysis of ester linkage in PBS phase). However, a significant drop in flexural strength and flexural modulus was observed for all of the PBS/RWP biocomposites as the soil burial time increased. These may be attributed to a presence of cavities on the fractured surfaces of PBS/RWP biocomposites as a result of the elimination of some rubberwood powder phase and hydrolysis mechanism of PBS phase, which were more apparent as the soil burial time increased from 20 days onward. This can also be supporting the results from the weight loss analysis (as shown in Figure 2). These results indicate two stages of PBS biodegradable mechanism, which are initially random cleavage of ester linkage leading to a decrease in molecular weight (probably a combination of rubberwood powder elimination and hydrolysis of ester linkage in PBS phase) that affects mechanical properties and then microorganism degradation.


## 4. Conclusions

Biodegradability of the PBS can be enhanced by the incorporation of rubberwood powder as supported by the SEM and optical micrographs illustrating greater cavities on the fractured surfaces of PBS/RWP and higher weight loss, a decline in crystallinity as seen in the X-ray diffractograms, and a more pronounced drop in carbonyl index values. This reveals the presence of rubberwood powders providing more disordered molecular chain arrangement of PBS matrix. This can also be confirmed by deteriorating of flexural properties with increase in soil burial test for 60 days in comparison with the neat PBS. Consequently, it can be concluded that the presence of rubberwood powder promotes the biodegradation rate of PBS matrix.



---

*Source: 368341-2015-10-26.xml*