# Synthesis, Spectral Characterization, and Antibacterial and Antifungal Studies of PANI/V2O5 Nanocomposites

Authors: Chakradhar Sridhar; Nagesh Gunvanthrao Yernale; M. V. N. Ambika Prasad
Journal: International Journal of Chemical Engineering
 (2016)

---

## Abstract

The present study deals with the synthesis and characterization of nanocrystalline vanadium pentoxide (V2O5) nanoparticles and their antibacterial and antifungal activity onStaphylococcus aureus and Aspergillus niger, respectively, by agar diffusion method. The metal oxide has been synthesized by employing the sol-gel method, polyaniline (PANI) has been synthesized by chemical oxidation, and PANI/V2O5 composites have been synthesized byin situ polymerization method with different ratios (10, 20, 30, 40, and 50 weight%) of V2O5 in PANI. The newly prepared composites were characterized by FTIR and powder X-ray diffraction (P-XRD) techniques and are found to be formed of PANI/V2O5 nanocomposites, and also the compounds showed moderate antibacterial and antifungal activity.


---

## Body

## 1. Introduction

Conducting polymers are unique because they show electrical, biological, and optical property changes when they are chemically treated with oxidizing or reducing agents. After chemical treatment with redox active agents, these polymers can change from an initial insulating state to an electrically conducting state [1]. This transition can be used in such applications as chemical sensors [2, 3], optical sensors [4], and biosensors [5, 6]. The most widely studied conducting polymers include polyaniline, polypyrrole, and polythiophene. Polyaniline is appealing because it is environmentally stable, is easily synthesized, and can react with chemical species at room temperature [7]. The nanoparticles composites materials have unique physical properties that have attracted more and more attention as a cathode in rechargeable ion batteries and selective gas sensors such as ammonia because of their high surface area and redox activity [8, 9]. Biological activity of vanadium pentoxide nanomaterial depends on factors such as the type of the derivative, manner of its administration, dose, length of treatment, and also individual- and species-specific sensitivity to the administered compound [10]. V2O5 nanomaterial is amphoteric in nature. Vanadium is correlated to its degree of oxidation (vanadyl\vanadate ion) and chemical form (organic\inorganic ligand) [11–13]. The existence of the various vanadate species depends on the pH and on the total concentration of vanadium. Their occurrence can be accounted for by protonation and condensation equilibrium; it is evident that only in very dilute solutions are monomeric vanadium ions found, and increases in concentration, particularly if the solution is acidic, lead to polymerization [14–16].In the recent past, the conducting polymer-based nanocomposites have drawn attention to their application as potent biological agents [17–21]. Therefore, PANI-V2O5 composites have been most intensively studied among various composites, because they could combine the merits of PANI and crystalline V2O5 within a single material and are expected to have applications in potent biological agents.


## 2. Experimental

### 2.1. Materials and Methods

The monomer aniline was distilled twice before use; an AR grade ammonium persulfate [(NH4)2S2O8], hydrochloric acid (HCl), and vanadium pentoxide (V2O5) were used for synthesis.


### 2.2. Synthesis of V2O5 Nanoparticles

The sol solution of vanadium nitrate hydrate and citric acid in double distilled water with specific weight percentages was prepared. The resulting mixture was dissolved by constant stirring for about 24 h at 40°C until a clear solution was obtained and was refluxed for about 1 h. During the reflux, the solution turns into a metal-citrate homogeneous complex with a slight color change from milky white to a clear solution. The completion of the reaction gives rise to the formation of the complex and the evaporation of the solvent forms a gel. Further, the gel was kept in hot air oven by slow heating up to 100°C for 3 h; there will be chelation between metal ions and citric acid [22]. This process helps in achieving a proper stoichiometry and control of the particle size without any need of a special atmosphere and also improves uniformity of the distribution of the metal ions in the solution. In the final step of the sol-gel process, the wet gel was fully dried by direct heating on the hot plate at 180–200°C for 5 h. The resulting white powder (V2O5) was obtained.The PANI/V2O5 composites were prepared byin situ polymerization method. To the mixture of double distilled aniline (0.1 mol) and hydrochloric acid (1 M), V2O5 was added in five different weights (10, 20, 30, 40, and 50 weight%) with vigorous stirring to keep V2O5 suspended in the solution. 11.2 g of ammonium persulfate was added slowly with constant stirring at 0–5°C. The reaction mixture was kept for stirring for about 24 h. The greenish precipitate was formed which was recovered by vacuum filtration and washed several times with distilled water. The obtained composite PANI/V2O5 is kept in oven for drying for 24 h to get a constant weight [23].


### 2.3. Antibacterial and Antifungal Activity

The antibacterial and antifungal activity of PANI, V2O5, and PANI/V2O5 nanocomposites were performed by the agar diffusion method [24, 25]. The antibacterial activity of the test compounds is tested against Gram-positive bacteria,Staphylococcus aureus(MTCC 3160), and antifungal activity againstAspergillus niger (MTCC 1881) in accordance with the international recommendation provided by the Clinical and Laboratory Standard Institute (CLSI). The above organisms were obtained from the Department of Microbiology and Biotechnology, Gulbarga University, Kalaburagi, Karnataka, India, which are previously procured from Institute of Microbial Technology Chandigarh, India. The stock solutions of each test compound (1 mg mL−1) were prepared by dissolving 10 mg of the each test compound in 10 mL of freshly distilled DMSO. Further, the various concentrations of the test compounds (25, 50, 100, 250, 500, and 1000 μg) were prepared by diluting the stock solutions with the required volume of freshly distilled DMSO.


#### 2.3.1. Antibacterial Activity

The media were prepared by dissolving peptone 10 g, NaCl 10 g, yeast extract 5 g, and agar 20 g in 1000 mL of distilled water. Initially, the stock cultures of bacteria were revived by inoculating in broth media and grown at 37°C for 18 h. The agar plates were prepared and wells were made in the plate. Further, each plate was inoculated with 18 h old cultures (100μL, 10−4 cfu) and spread evenly on the plate. After 20 min, the wells were filled with newly prepared compounds and standard antibiotic, Ciprofloxacin, at different concentrations (25, 50, 100, 250, 500, and 1000 μg). All the plates were incubated at 37°C for 24 h and the diameter of inhibition zone was measured. The experiment was done in triplicate and the average values were calculated for antibacterial activity.


#### 2.3.2. Antifungal Activity

The media were prepared by using Czapek-Dox Agar (composition (g/L): sucrose 30.0; sodium nitrate 2.0; K2HPO4 1.0, MgSO4. 7H2O 0.5; KCl 0.5; FeSO4 0.01; agar 20). Initially, the stock cultures were revived by inoculating in broth media and grown at 27°C for 48 h. The agar plates of the above media were prepared and wells were made in the plate. Each plate was inoculated with 48 h old cultures (100 μL 104 CFU) and spread evenly on the plate. After 20 min, the wells were filled with different concentrations (25, 50, 100, 250, 500, and 1000 μg) of samples and antibiotic, Fluconazole. All the plates were incubated at 27°C for 96 h and the diameter of inhibition zone was noted. The experiment was done in triplicate and the average values were calculated for antibacterial activity.The minimum concentration of each test compound with no visible growth of test bacteria/fungi was reported as MIC for their respective strains. Blank tests have shown that DMSO in the preparation of the test solution does not affect the test organisms.


### 2.4. Physical Measurement

The FTIR spectra were recorded on a Perkin Elmer 1600 spectrophotometer in KBr and powder X-ray diffraction studies were performed by Philips X-ray diffractometer with Cu Kα as a radiation source.


## 2.1. Materials and Methods

The monomer aniline was distilled twice before use; an AR grade ammonium persulfate [(NH4)2S2O8], hydrochloric acid (HCl), and vanadium pentoxide (V2O5) were used for synthesis.


## 2.2. Synthesis of V2O5 Nanoparticles

The sol solution of vanadium nitrate hydrate and citric acid in double distilled water with specific weight percentages was prepared. The resulting mixture was dissolved by constant stirring for about 24 h at 40°C until a clear solution was obtained and was refluxed for about 1 h. During the reflux, the solution turns into a metal-citrate homogeneous complex with a slight color change from milky white to a clear solution. The completion of the reaction gives rise to the formation of the complex and the evaporation of the solvent forms a gel. Further, the gel was kept in hot air oven by slow heating up to 100°C for 3 h; there will be chelation between metal ions and citric acid [22]. This process helps in achieving a proper stoichiometry and control of the particle size without any need of a special atmosphere and also improves uniformity of the distribution of the metal ions in the solution. In the final step of the sol-gel process, the wet gel was fully dried by direct heating on the hot plate at 180–200°C for 5 h. The resulting white powder (V2O5) was obtained.The PANI/V2O5 composites were prepared byin situ polymerization method. To the mixture of double distilled aniline (0.1 mol) and hydrochloric acid (1 M), V2O5 was added in five different weights (10, 20, 30, 40, and 50 weight%) with vigorous stirring to keep V2O5 suspended in the solution. 11.2 g of ammonium persulfate was added slowly with constant stirring at 0–5°C. The reaction mixture was kept for stirring for about 24 h. The greenish precipitate was formed which was recovered by vacuum filtration and washed several times with distilled water. The obtained composite PANI/V2O5 is kept in oven for drying for 24 h to get a constant weight [23].


## 2.3. Antibacterial and Antifungal Activity

The antibacterial and antifungal activity of PANI, V2O5, and PANI/V2O5 nanocomposites were performed by the agar diffusion method [24, 25]. The antibacterial activity of the test compounds is tested against Gram-positive bacteria,Staphylococcus aureus(MTCC 3160), and antifungal activity againstAspergillus niger (MTCC 1881) in accordance with the international recommendation provided by the Clinical and Laboratory Standard Institute (CLSI). The above organisms were obtained from the Department of Microbiology and Biotechnology, Gulbarga University, Kalaburagi, Karnataka, India, which are previously procured from Institute of Microbial Technology Chandigarh, India. The stock solutions of each test compound (1 mg mL−1) were prepared by dissolving 10 mg of the each test compound in 10 mL of freshly distilled DMSO. Further, the various concentrations of the test compounds (25, 50, 100, 250, 500, and 1000 μg) were prepared by diluting the stock solutions with the required volume of freshly distilled DMSO.


### 2.3.1. Antibacterial Activity

The media were prepared by dissolving peptone 10 g, NaCl 10 g, yeast extract 5 g, and agar 20 g in 1000 mL of distilled water. Initially, the stock cultures of bacteria were revived by inoculating in broth media and grown at 37°C for 18 h. The agar plates were prepared and wells were made in the plate. Further, each plate was inoculated with 18 h old cultures (100μL, 10−4 cfu) and spread evenly on the plate. After 20 min, the wells were filled with newly prepared compounds and standard antibiotic, Ciprofloxacin, at different concentrations (25, 50, 100, 250, 500, and 1000 μg). All the plates were incubated at 37°C for 24 h and the diameter of inhibition zone was measured. The experiment was done in triplicate and the average values were calculated for antibacterial activity.


### 2.3.2. Antifungal Activity

The media were prepared by using Czapek-Dox Agar (composition (g/L): sucrose 30.0; sodium nitrate 2.0; K2HPO4 1.0, MgSO4. 7H2O 0.5; KCl 0.5; FeSO4 0.01; agar 20). Initially, the stock cultures were revived by inoculating in broth media and grown at 27°C for 48 h. The agar plates of the above media were prepared and wells were made in the plate. Each plate was inoculated with 48 h old cultures (100 μL 104 CFU) and spread evenly on the plate. After 20 min, the wells were filled with different concentrations (25, 50, 100, 250, 500, and 1000 μg) of samples and antibiotic, Fluconazole. All the plates were incubated at 27°C for 96 h and the diameter of inhibition zone was noted. The experiment was done in triplicate and the average values were calculated for antibacterial activity.The minimum concentration of each test compound with no visible growth of test bacteria/fungi was reported as MIC for their respective strains. Blank tests have shown that DMSO in the preparation of the test solution does not affect the test organisms.


## 2.3.1. Antibacterial Activity

The media were prepared by dissolving peptone 10 g, NaCl 10 g, yeast extract 5 g, and agar 20 g in 1000 mL of distilled water. Initially, the stock cultures of bacteria were revived by inoculating in broth media and grown at 37°C for 18 h. The agar plates were prepared and wells were made in the plate. Further, each plate was inoculated with 18 h old cultures (100μL, 10−4 cfu) and spread evenly on the plate. After 20 min, the wells were filled with newly prepared compounds and standard antibiotic, Ciprofloxacin, at different concentrations (25, 50, 100, 250, 500, and 1000 μg). All the plates were incubated at 37°C for 24 h and the diameter of inhibition zone was measured. The experiment was done in triplicate and the average values were calculated for antibacterial activity.


## 2.3.2. Antifungal Activity

The media were prepared by using Czapek-Dox Agar (composition (g/L): sucrose 30.0; sodium nitrate 2.0; K2HPO4 1.0, MgSO4. 7H2O 0.5; KCl 0.5; FeSO4 0.01; agar 20). Initially, the stock cultures were revived by inoculating in broth media and grown at 27°C for 48 h. The agar plates of the above media were prepared and wells were made in the plate. Each plate was inoculated with 48 h old cultures (100 μL 104 CFU) and spread evenly on the plate. After 20 min, the wells were filled with different concentrations (25, 50, 100, 250, 500, and 1000 μg) of samples and antibiotic, Fluconazole. All the plates were incubated at 27°C for 96 h and the diameter of inhibition zone was noted. The experiment was done in triplicate and the average values were calculated for antibacterial activity.The minimum concentration of each test compound with no visible growth of test bacteria/fungi was reported as MIC for their respective strains. Blank tests have shown that DMSO in the preparation of the test solution does not affect the test organisms.


## 2.4. Physical Measurement

The FTIR spectra were recorded on a Perkin Elmer 1600 spectrophotometer in KBr and powder X-ray diffraction studies were performed by Philips X-ray diffractometer with Cu Kα as a radiation source.


## 3. Results and Discussions

### 3.1. FTIR Spectral Data

The prominent peak (Figure1(a)) observed at 2924 cm−1 is due to CH2 asymmetric stretching, peak at 1603 cm−1 confirms the formation of PANI, and peaks at 1574 cm−1 and 1494 cm−1 may be attributed to the presence of quinoid (N=Q=N) and benzenoid (N=B=N) ring stretching. Also, the peaks observed at 1303 cm−1, 1146 cm−1, 734 cm−1, and 502 cm−1 are due to N-H deformation, C-O-C stretching of excess oxidant, and C-H vibration of p-coupling benzenoid ring and aromatic ring, respectively [26].Figure 1
(a) FTIR spectrum of PANI. (b) FTIR spectrum of V2O5 nanoparticle. (c) FTIR spectrum of 50 weight% of V2O5 in PANI (V2O5/PANI nanocomposite).
(a)
Pure PANI
(b)
Pure V2O5
(c)
V2O5 50 wt% in PANIThe FTIR spectrum of V2O5 nanoparticles (Figure 1(b)) shows absorption bands at 1022 cm−1, and 817 cm−1 and 580 cm−1 are assigned to V=O stretching band and V-O-V deformation modes, respectively [27].Also, the FTIR spectrum (Figure1(c)) of mixture of PANI/V2O5 nanoparticles with 50 weight% displayed the absorption bands at 3431 cm−1, 2920 cm−1, 1600 cm−1, 1572 cm−1, 1492 cm−1, 1301 cm−1, 1145 cm−1, 1020 cm−1, 810 cm−1, and 578 cm−1, confirming the presence of V2O5 in PANI. When comparing the FTIR spectra of PANI and V2O5 nanoparticles (Figures 1(a) and 1(b)), it is clearly observed that some of the absorption frequencies are slightly shifted towards lower side, which is due to the weak Vander Waals force and confirms the formation of nanocomposite.


### 3.2. Powder X-Ray Diffraction

The powder X-ray analysis data (Figure2(a)) shows the amorphous nature of the PANI with the appearance of a broad peak centered at 2θ ≈ 25.53°, which corresponds toh k l values of (2 0 0) diffraction planes PANI [28].Figure 2
(a) Powder X-ray diffraction pattern of PANI. (b) Powder X-ray diffraction pattern of V2O5 nanoparticle. (c) Powder X-ray diffraction pattern of 50 weight% of V2O5 in PANI (V2O5/PANI nanocomposite).
(a)
Pure PANI
(b)
Pure V2O5
(c)
50 wt% of V2O5 in PANIThe powder X-ray diffraction pattern of V2O5 nanoparticle (Figure 2(b)) shows thegood crystallinity nature. The formations of nanoparticles are confirmed by the existence of sharp peaks. The crystallite size of the synthesized V2O5 nanoparticle was calculated using Scherer’s formula: D
=
0.9
λ
/
β
cos
⁡
θ.The average crystallite size of V2O5 nanoparticles is found to be ~11 nm. In the XRD spectra (Figure 2(b)), it was observed that the different peaks are attributed to theh k l values of (2 0 0), (0 0 1), (1 1 0), (4 0 0), (0 1 1), (3 1 0), (0 0 2), (4 1 1), (6 0 0), (6 0 1), (1 2 1), (4 2 0), and (7 1 0) planes which are in good agreement with the data of V2O5 powder file (JCPDS number 09-0387) which corresponds to the orthorhombic crystalline structure. The XRD spectrum exhibits an intense (0 0 1) peak indicating preferential orientation in the 0
0
1 direction. This result reveals that the structure is such that the crystallographic c-axis is perpendicular to the substrate surface and the crystalline orientation is favored [29].In the powder X-ray diffraction pattern (Figure2(c)) of PANI/V2O5 nanocomposite with 50 weight% of V2O5 nanoparticles in PANI, the various sharp peaks are attributed to theh k l values of (2 0 0), (0 0 1), (1 1 0), (4 0 0), (0 1 1), (3 1 0), (0 0 2), and (3 1 0) planes. In comparison (Figures 2(a) and 2(b)), it is clearly revealed that V2O5 nanoparticle has retained its structure even though it is dispersed in PANI during the process of polymerization.


### 3.3. Antibacterial and Antifungal Activity Results

The antibacterial and antifungal activities of newly prepared compounds were examined for their effect onS. aureus andA. niger, respectively, by minimum inhibitory concentration (MIC) method. The minimum concentration of each test compound with no visible growth of test bacteria/fungi was reported as MIC for their respective strains [30, 31]. The compound V2O5 and PANI/V2O5 showed the moderate antibacterial activity at 100 μg concentration. Further, the compound V2O5 showed moderate antifungal activity at 50 μg concentration. The obtained results were compared with that of Ciprofloxacin, a broad-spectrum antibiotic for bacterial strains, and Fluconazole for fungal strains as positive control and results are presented in Tables 1 and 2 respectively.Table 1
Antibacterial activity results, zone of inhibition in mm(S. aureus).
Samples
25µg
50µg
100µg
250µg
500µg
1000µg
MICµg
PANI
0
0
0
8
12
15
250
V2O5
0
0
7
10
15
19
100
PANI/V2O5
0
0
9
11
15
22
100
Ciproflaxacin
∗
∗
∗
∗
∗
∗
∗
∗Inhibitions zones were too big to measure.Table 2
Antifungal activity results, zone of inhibition in mm(A. niger).
Sample
25µg
50µg
100µg
250µg
500µg
1000µg
MICµg
PANI
0
0
0
6
10
19
250
V2O5
0
7
13
19
22
20
50
PANI/V2O5
0
0
5
9
14
21
100
Fluconazole
5
14
22
∗
∗
∗
25
∗Inhibitions zones were too big to measure.


## 3.1. FTIR Spectral Data

The prominent peak (Figure1(a)) observed at 2924 cm−1 is due to CH2 asymmetric stretching, peak at 1603 cm−1 confirms the formation of PANI, and peaks at 1574 cm−1 and 1494 cm−1 may be attributed to the presence of quinoid (N=Q=N) and benzenoid (N=B=N) ring stretching. Also, the peaks observed at 1303 cm−1, 1146 cm−1, 734 cm−1, and 502 cm−1 are due to N-H deformation, C-O-C stretching of excess oxidant, and C-H vibration of p-coupling benzenoid ring and aromatic ring, respectively [26].Figure 1
(a) FTIR spectrum of PANI. (b) FTIR spectrum of V2O5 nanoparticle. (c) FTIR spectrum of 50 weight% of V2O5 in PANI (V2O5/PANI nanocomposite).
(a)
Pure PANI
(b)
Pure V2O5
(c)
V2O5 50 wt% in PANIThe FTIR spectrum of V2O5 nanoparticles (Figure 1(b)) shows absorption bands at 1022 cm−1, and 817 cm−1 and 580 cm−1 are assigned to V=O stretching band and V-O-V deformation modes, respectively [27].Also, the FTIR spectrum (Figure1(c)) of mixture of PANI/V2O5 nanoparticles with 50 weight% displayed the absorption bands at 3431 cm−1, 2920 cm−1, 1600 cm−1, 1572 cm−1, 1492 cm−1, 1301 cm−1, 1145 cm−1, 1020 cm−1, 810 cm−1, and 578 cm−1, confirming the presence of V2O5 in PANI. When comparing the FTIR spectra of PANI and V2O5 nanoparticles (Figures 1(a) and 1(b)), it is clearly observed that some of the absorption frequencies are slightly shifted towards lower side, which is due to the weak Vander Waals force and confirms the formation of nanocomposite.


## 3.2. Powder X-Ray Diffraction

The powder X-ray analysis data (Figure2(a)) shows the amorphous nature of the PANI with the appearance of a broad peak centered at 2θ ≈ 25.53°, which corresponds toh k l values of (2 0 0) diffraction planes PANI [28].Figure 2
(a) Powder X-ray diffraction pattern of PANI. (b) Powder X-ray diffraction pattern of V2O5 nanoparticle. (c) Powder X-ray diffraction pattern of 50 weight% of V2O5 in PANI (V2O5/PANI nanocomposite).
(a)
Pure PANI
(b)
Pure V2O5
(c)
50 wt% of V2O5 in PANIThe powder X-ray diffraction pattern of V2O5 nanoparticle (Figure 2(b)) shows thegood crystallinity nature. The formations of nanoparticles are confirmed by the existence of sharp peaks. The crystallite size of the synthesized V2O5 nanoparticle was calculated using Scherer’s formula: D
=
0.9
λ
/
β
cos
⁡
θ.The average crystallite size of V2O5 nanoparticles is found to be ~11 nm. In the XRD spectra (Figure 2(b)), it was observed that the different peaks are attributed to theh k l values of (2 0 0), (0 0 1), (1 1 0), (4 0 0), (0 1 1), (3 1 0), (0 0 2), (4 1 1), (6 0 0), (6 0 1), (1 2 1), (4 2 0), and (7 1 0) planes which are in good agreement with the data of V2O5 powder file (JCPDS number 09-0387) which corresponds to the orthorhombic crystalline structure. The XRD spectrum exhibits an intense (0 0 1) peak indicating preferential orientation in the 0
0
1 direction. This result reveals that the structure is such that the crystallographic c-axis is perpendicular to the substrate surface and the crystalline orientation is favored [29].In the powder X-ray diffraction pattern (Figure2(c)) of PANI/V2O5 nanocomposite with 50 weight% of V2O5 nanoparticles in PANI, the various sharp peaks are attributed to theh k l values of (2 0 0), (0 0 1), (1 1 0), (4 0 0), (0 1 1), (3 1 0), (0 0 2), and (3 1 0) planes. In comparison (Figures 2(a) and 2(b)), it is clearly revealed that V2O5 nanoparticle has retained its structure even though it is dispersed in PANI during the process of polymerization.


## 3.3. Antibacterial and Antifungal Activity Results

The antibacterial and antifungal activities of newly prepared compounds were examined for their effect onS. aureus andA. niger, respectively, by minimum inhibitory concentration (MIC) method. The minimum concentration of each test compound with no visible growth of test bacteria/fungi was reported as MIC for their respective strains [30, 31]. The compound V2O5 and PANI/V2O5 showed the moderate antibacterial activity at 100 μg concentration. Further, the compound V2O5 showed moderate antifungal activity at 50 μg concentration. The obtained results were compared with that of Ciprofloxacin, a broad-spectrum antibiotic for bacterial strains, and Fluconazole for fungal strains as positive control and results are presented in Tables 1 and 2 respectively.Table 1
Antibacterial activity results, zone of inhibition in mm(S. aureus).
Samples
25µg
50µg
100µg
250µg
500µg
1000µg
MICµg
PANI
0
0
0
8
12
15
250
V2O5
0
0
7
10
15
19
100
PANI/V2O5
0
0
9
11
15
22
100
Ciproflaxacin
∗
∗
∗
∗
∗
∗
∗
∗Inhibitions zones were too big to measure.Table 2
Antifungal activity results, zone of inhibition in mm(A. niger).
Sample
25µg
50µg
100µg
250µg
500µg
1000µg
MICµg
PANI
0
0
0
6
10
19
250
V2O5
0
7
13
19
22
20
50
PANI/V2O5
0
0
5
9
14
21
100
Fluconazole
5
14
22
∗
∗
∗
25
∗Inhibitions zones were too big to measure.


## 4. Conclusions

The PANI and V2O5 nanoparticles and PANI/V2O5 nanocomposites have been successfully synthesized by chemical oxidation, sol-gel, andin situ polymerization methods, respectively. The prepared samples were well characterized and their formation was confirmed by FTIR and powder X-ray diffraction techniques. These data suggest the formation of composites. Further, the prepared compounds behaved as antibacterial and antifungal agents. Hence, from all these extensive observations, it was concluded that the prepared compounds give the remarkable, versatile, and valuable information to materials chemistry and also they may be used as good biological agents with reduced toxicity and higher efficiency.



---