# An Investigation on the Properties of Palm-Based Polyurethane Solid Polymer Electrolyte

Authors: Farah Nadia Daud; Azizan Ahmad; Khairiah Haji Badri
Journal: International Journal of Polymer Science
 (2014)

---

## Abstract

Palm-based polyurethane electrolyte was prepared via prepolymerization method between palm kernel oil polyol (PKO-p) and 2,4′-diphenylmethane diisocyanate (MDI) in acetone at room temperature with the presence of lithium trifluoromethanesulfonate (LiCF3SO3). The effect of varying the concentration of LiCF3SO3 salt on the ionic conductivity, chemical interaction, and structural and morphological properties of the polyurethane solid polymer electrolyte was investigated. The produced film was analyzed using electrochemical impedance spectroscopy (EIS), attenuated total reflection Fourier transform infrared (ATR-FTIR), X-ray diffraction (XRD), and scanning electron microscopy (SEM). The EIS result showed that the highest ionic conductivity was at 30 wt% LiCF3SO3 with a value of 1.6 × 10−5 S·cm−1. Infrared analysis showed the interaction between lithium ions and amine group (–N–H) at (3600–3100 cm−1), carbonyl group (–C=O) at (1750–1650 cm−1), and ether group (–C–O–C–) at (1150–1000 cm−1) of the polyurethane forming polymer-salt complexes. The XRD result proved that LiCF3SO3 salt completely dissociates within the polyurethane film as no crystalline peaks of LiCF3SO3 were observed. The morphological study revealed that the films prepared have a good homogeneity and compatibility as no phase separation occurred.


---

## Body

## 1. Introduction

Since the discovery of ionic conductivity phenomenon in solid state by Faraday in the 1800s, numerous studies have been conducted on polymer electrolytes pioneered by Peter Wright and Michel Armand who had introduced the first new class of solid ionic conductors in the 1970s [1]. Studies showed that liquid electrolyte has higher ionic conductivity compared to other electrolyte systems. However, it has several disadvantages, namely, leakage, gas formation during operation, and difficulty in handling for portable applications, which has resulted in increasing studies conducted on solid polymer electrolyte given its potential for applications in solid batteries, electrochromic windows, sensors, fuel cell, and others [2].However, most of the current researches focus on the production of petrochemical based polymers such as polyethylene oxide (PEO) compared to polymers based on natural resources. Awareness of the importance of safe and environmental friendly sources of polymer has resulted in the studies replacing the dependence on petrochemical based polymers conductors. Moreover, with the current price hike of petroleum, the use of raw materials based on natural resources for industrial purposes also has increased. Palm oil-based products have become one of the alternatives for the production of polyols for polyurethane products [3].Polyurethane is a copolymer that consists of urethane linkages (–NHCOO) in its molecular structure. It is typically made by the reaction of a polyester or polyether polyol with diisocyanate. As a block copolymer, it has a unique multiphase structure consisting of soft segments and hard segments that are suitable as matrix materials in polymer electrolyte. Studies carried out by Badri et al. [4] described the method of producing monoester polyol (PKO-p) from palm kernel oil (PKO).One of the approaches to produce polyurethanes is through prepolymerization technique in the presence of a solvent. This gives the advantage of lower isocyanate vapor levels and heat reduction of the final reaction compared to a single step polymerization. A single step polymerization of polyurethane gives off heat during formation of the urethane bonds and might cause shrinkage problem. Meanwhile, prepolymerization allows for partial heat dissipation prior to the formation of polyurethane as discussed elsewhere [5–7].In this research, polyurethane was produced via prepolymerization method between PKO-p and 2, 4′-diphenylmethane diisocyanate (MDI) in acetone at room temperature. The effect of different concentrations of LiCF3SO3 salt on the ionic conductivity, chemical interaction, and structural and morphological properties of the polyurethane solid polymer electrolyte was investigated using electrochemical impedance spectroscopy (EIS), attenuated total reflection Fourier transform infrared (ATR-FTIR), X-ray diffraction (XRD), and scanning electron microscopy (SEM).


## 2. Experimental

### 2.1. Materials

Palm kernel oil-based polyol (PKO-p) was prepared as described by Badri et al. [4]. 2,4′-diphenylmethane diisocyanate (MDI) was purchased from Cosmopolyurethane (M) Sdn. Bhd, Port Klang, Malaysia. Acetone was supplied by Systerm Sdn. Bhd., Shah Alam, Malaysia. Polyethylene glycol (PEG) and lithium trifluoromethanesulfonate (LiCF3SO3) were purchased from Sigma-Aldrich Sdn. Bhd., Kuala Lumpur, Malaysia. All materials were used without further purification.


### 2.2. Preparation of Prepolymerized Polyurethane (PU)

The method used by Wong and Badri [5] was followed. PKO-p and MDI were separately dissolved in acetone at room temperature to form urethane prepolymer. The amount of LiCF3SO3 salt was varied at 5 to 30 wt%. The LiCF3SO3 salt was dissolved in the PKO-p and stirred via magnetic bar for 30 min. The MDI was then added into the PKO-p drop-wise and the mixture was stirred for another 5 min and casted into a Teflon plate. The solvent was allowed to slowly evaporate in a fume hood at room temperature for 24 h. The films were yellow in color, translucent, and free standing.


### 2.3. Measurements

The ionic conductivity measurements were carried out by EIS using a high frequency resonance analyzer (HFRA; Solartron 1260, Schlumberger) with applied frequency ranging from 0.1 to 106 Hz at a perturbation voltage of 1000 mV. The disc-shaped sample of 16 mm diameter was sandwiched between two stainless steel blocking electrodes. The ATR-IR spectrum was recorded by Perkin Elmer Spectrum 2000 in the range of 4,000 to 650 cm−1 with a scanning resolution of 4 cm−1. The analysis was conducted to study the interaction between LiCF3SO3 salt and the functional groups presence in polyurethane polymeric chain. XRD model D-5000 Siemen was used to determine presence of crystalline or amorphous phase as a function of salt concentration. The data was collected at diffraction angle 2θ of 5° to 60° at the rate of 0.04°·s−1. The morphologies of the cross-sectioned polymer electrolytes were analyzed using SEM Philip model XL30 at 1000x magnifications with 17 kV electron beam. The thickness of the film obtained ranged from 0.11 to 0.17 mm. The whole analysis was conducted at room temperature.


## 2.1. Materials

Palm kernel oil-based polyol (PKO-p) was prepared as described by Badri et al. [4]. 2,4′-diphenylmethane diisocyanate (MDI) was purchased from Cosmopolyurethane (M) Sdn. Bhd, Port Klang, Malaysia. Acetone was supplied by Systerm Sdn. Bhd., Shah Alam, Malaysia. Polyethylene glycol (PEG) and lithium trifluoromethanesulfonate (LiCF3SO3) were purchased from Sigma-Aldrich Sdn. Bhd., Kuala Lumpur, Malaysia. All materials were used without further purification.


## 2.2. Preparation of Prepolymerized Polyurethane (PU)

The method used by Wong and Badri [5] was followed. PKO-p and MDI were separately dissolved in acetone at room temperature to form urethane prepolymer. The amount of LiCF3SO3 salt was varied at 5 to 30 wt%. The LiCF3SO3 salt was dissolved in the PKO-p and stirred via magnetic bar for 30 min. The MDI was then added into the PKO-p drop-wise and the mixture was stirred for another 5 min and casted into a Teflon plate. The solvent was allowed to slowly evaporate in a fume hood at room temperature for 24 h. The films were yellow in color, translucent, and free standing.


## 2.3. Measurements

The ionic conductivity measurements were carried out by EIS using a high frequency resonance analyzer (HFRA; Solartron 1260, Schlumberger) with applied frequency ranging from 0.1 to 106 Hz at a perturbation voltage of 1000 mV. The disc-shaped sample of 16 mm diameter was sandwiched between two stainless steel blocking electrodes. The ATR-IR spectrum was recorded by Perkin Elmer Spectrum 2000 in the range of 4,000 to 650 cm−1 with a scanning resolution of 4 cm−1. The analysis was conducted to study the interaction between LiCF3SO3 salt and the functional groups presence in polyurethane polymeric chain. XRD model D-5000 Siemen was used to determine presence of crystalline or amorphous phase as a function of salt concentration. The data was collected at diffraction angle 2θ of 5° to 60° at the rate of 0.04°·s−1. The morphologies of the cross-sectioned polymer electrolytes were analyzed using SEM Philip model XL30 at 1000x magnifications with 17 kV electron beam. The thickness of the film obtained ranged from 0.11 to 0.17 mm. The whole analysis was conducted at room temperature.


## 3. Results and Discussion

### 3.1. Ionic Conductivity

In the complex impedance plot, the real quantityZ′ (x-axis) was plotted againstZ′′ (y-axis) which displayed the polymer electrolytes characteristics as an arc followed by linear spike that was a straight line inclined to the real axis. The bulk resistance (R
b) of the electrolyte system was determined from an impedance plot where the ionic conductivity (σ) was calculated fromR
b that was obtained from the intercept on the real axis (Z′), the film thickness (l), and the contact area of the thin film (A
=
π
r
2
=
π
(
0.80
cm
)
2
=
2.01
cm
2) according to the equation σ = [l/(AR
b)] [8, 9]. Table 1 shows the conductivity of PU-LiCF3SO3 electrolyte at varying concentration of LiCF3SO3 salt conducted at room temperature. The ionic conductivity increased with increasing concentration of LiCF3SO3 salt. The ionic conductivity increased three magnitudes compared to pristine PU, with the addition of only 5 wt% LiCF3SO3 (1.8 × 10−8 S·cm−1). The highest conductivity was recorded at 30 wt% LiCF3SO3 with conductivity of 1.6 × 10−5 S·cm−1. This increment was contributed by the number of conducting species in the electrolyte caused by ion dissociation of LiCF3SO3. This occurred due to the presence of coordinating atoms in the polymer host [10, 11]. The conducting species or free mobile ions present in the polymer may increase the amorphous structure of the polymer host through favorable free volume; thus, it eases the ion migration [12, 13]. The ion transport phenomenon was further discussed in the IR spectroscopy analysis.Table 1
The effect of LiCF3SO3salt on the ionic conductivity of the polymer electrolyte.
LiCF3SO3, (wt%)
Ionic conductivity (σ), (S·cm−1)
0
~10−12
5
1.8
×
10
-
8
10
1.3
×
10
-
7
15
6.6
×
10
-
7
20
4.0
×
10
-
6
25
4.5
×
10
-
6
30
1.6
×
10
-
5


### 3.2. IR Spectroscopy Analysis

Previous studies [14–17] have reported the presence of strong hydrogen-bonding interaction in poly(ether-urethane) that leads to changes in PU microstructure consisting of soft and hard segments. The nature of the interaction and coordination of Li+ and CF3SO
3
- ions transport within the PU chains was analyzed by mean of the IR spectrum [18]. In the hard segment, the urethane groups have electrostatic charges at hydrogen, oxygen, and nitrogen atoms forming dipoles which attract another atom of opposite charge. The main functional groups in the regions such as 3600–3100 cm−1 (the hydrogen bonded N–H stretching mode and the free N–H stretch), 1750–1650 cm−1 (the carbonyl symmetric stretching vibration or amide band) (–C=O), and 1150–1000 cm−1 (the –C–O–C– stretch) were identified to discern the effect of LiCF3SO3 on the chemical interaction of the PU electrolyte. Figure 1 exhibited that the N-H peak of PU at 3290 cm−1 shifted to a higher wave number as the concentration of the lithium salt increased, indicating that free N-H was generated and there was less hard-hard segment hydrogen bonds left [19, 20].Figure 1
The N-H peak of PU at 3290 cm−1 shifted to the right as the concentration of the lithium salt increased.Peak of ether group (–C–O–C–) at 1017–1029 cm−1 (Figure 2) became intense while peak at 1105 cm−1 became almost a plateau due to overlapping peaks contributed by the Li+ bonded ether group, free bonded ether, and hydrogen ether.Figure 2
Peak of ether group (–C–O–C–) at 1017–1029 cm−1and 1105 cm−1 for the free bonded ether and hydrogen ether.However, Figure3 indicated a reduction in intensity of the hydrogen bonded carbonyl group at 1707 cm−1 as the concentration of salt increased. Meanwhile, peak of the nonhydrogen bonded carbonyl urethane group at 1720 cm−1 shifted to a lower frequency due to the interaction with lithium ions. From the observation conducted on the ATR-IR spectroscopy analysis, it can be deduced that lithium salts had interacted with both the hard segments which were the N–H and C=O and also the soft segment which was –C–O–C– of polyurethane and affected the crystallinity of polyurethane as observed in the XRD analysis [19].Figure 3
The hydrogen-bonded carbonyl group at 1707 cm−1 and the nonhydrogen bonded carbonyl urethane group at 1720 cm−1.


### 3.3. X-Ray Diffraction Analysis (XRD)

The X-ray diffraction analysis is used to determine the structure, complexation, and crystallization of the polymer matrix. The effect of complexation of PU-LiCF3SO3 system was investigated by performing XRD analysis where the appearance of the amorphous region or the reduction of the crystalline region would result in high ionic conductivity compared to the crystalline and semicrystalline region as reported by Su’ait et al. [21]. The measurement was conducted in the range of 5°–60° at diffraction angle of 2θ. Figure 4 shows the XRD pattern of pristine PU and the PU-LiCF3SO3 to study the change of crystalline structure upon addition of different weight percentages (10%, 20%, and 30%) of LiCF3SO3. From the diffractogram, we can observe that the pristine PU film was a semicrystalline polymer with a broad hump at 20° and crystalline peaks at 31°, 52°, and 53°. As the salt addition increased, the crystalline peaks decreased and disappeared as 30 wt% of LiCF3SO3 was added into PU. The hump becomes broader and flatter proving that the PU became more amorphous upon the salt addition [22]. In amorphous state, greater ionic diffusivity can occur as ions can move in the amorphous phase freely because of low energy barrier. Besides, the amorphous polymer exhibits more flexible backbone which can increase local chain mobility. Hence, the segmental motions of the polymer will also increase. This will then improve the transportation property of the electrolyte system [9].Figure 4
XRD patterns of PU1 with varying amount of LiCF3SO3.


### 3.4. Scanning Electron Microscopy (SEM)

Figure5 shows the SEM micrograph of the pristine PU film. It exhibited a clear and smooth surface. However, the presence of LiCF3SO3 in the PU film was obviously shown upon drying of the sample. Higher loading of the LiCF3SO3 gave more distribution of the LiCF3SO3 salt on the PU film. This was strongly supported by the XRD analysis where there was a reduction in the crystallinity of the sample. Thus, higher conductivity was observed. The micrographs of the PU electrolytes at 10, 20, and 30 wt% showed the uniformly distributed spherical grains in the electrolyte system (Figures 6, 7, and 8). The more the appearance of the LiCF3SO3 salt on the PU film, the higher the conductivity increase.Figure 5
SEM micrograph of pristine polyurethane.Figure 6
SEM micrograph of the PU film containing 10 wt% LiCF3SO3.Figure 7
SEM micrograph of the PU film containing 20 wt% LiCF3SO3.Figure 8
SEM micrograph of the PU film containing 30 wt% LiCF3SO3.


## 3.1. Ionic Conductivity

In the complex impedance plot, the real quantityZ′ (x-axis) was plotted againstZ′′ (y-axis) which displayed the polymer electrolytes characteristics as an arc followed by linear spike that was a straight line inclined to the real axis. The bulk resistance (R
b) of the electrolyte system was determined from an impedance plot where the ionic conductivity (σ) was calculated fromR
b that was obtained from the intercept on the real axis (Z′), the film thickness (l), and the contact area of the thin film (A
=
π
r
2
=
π
(
0.80
cm
)
2
=
2.01
cm
2) according to the equation σ = [l/(AR
b)] [8, 9]. Table 1 shows the conductivity of PU-LiCF3SO3 electrolyte at varying concentration of LiCF3SO3 salt conducted at room temperature. The ionic conductivity increased with increasing concentration of LiCF3SO3 salt. The ionic conductivity increased three magnitudes compared to pristine PU, with the addition of only 5 wt% LiCF3SO3 (1.8 × 10−8 S·cm−1). The highest conductivity was recorded at 30 wt% LiCF3SO3 with conductivity of 1.6 × 10−5 S·cm−1. This increment was contributed by the number of conducting species in the electrolyte caused by ion dissociation of LiCF3SO3. This occurred due to the presence of coordinating atoms in the polymer host [10, 11]. The conducting species or free mobile ions present in the polymer may increase the amorphous structure of the polymer host through favorable free volume; thus, it eases the ion migration [12, 13]. The ion transport phenomenon was further discussed in the IR spectroscopy analysis.Table 1
The effect of LiCF3SO3salt on the ionic conductivity of the polymer electrolyte.
LiCF3SO3, (wt%)
Ionic conductivity (σ), (S·cm−1)
0
~10−12
5
1.8
×
10
-
8
10
1.3
×
10
-
7
15
6.6
×
10
-
7
20
4.0
×
10
-
6
25
4.5
×
10
-
6
30
1.6
×
10
-
5


## 3.2. IR Spectroscopy Analysis

Previous studies [14–17] have reported the presence of strong hydrogen-bonding interaction in poly(ether-urethane) that leads to changes in PU microstructure consisting of soft and hard segments. The nature of the interaction and coordination of Li+ and CF3SO
3
- ions transport within the PU chains was analyzed by mean of the IR spectrum [18]. In the hard segment, the urethane groups have electrostatic charges at hydrogen, oxygen, and nitrogen atoms forming dipoles which attract another atom of opposite charge. The main functional groups in the regions such as 3600–3100 cm−1 (the hydrogen bonded N–H stretching mode and the free N–H stretch), 1750–1650 cm−1 (the carbonyl symmetric stretching vibration or amide band) (–C=O), and 1150–1000 cm−1 (the –C–O–C– stretch) were identified to discern the effect of LiCF3SO3 on the chemical interaction of the PU electrolyte. Figure 1 exhibited that the N-H peak of PU at 3290 cm−1 shifted to a higher wave number as the concentration of the lithium salt increased, indicating that free N-H was generated and there was less hard-hard segment hydrogen bonds left [19, 20].Figure 1
The N-H peak of PU at 3290 cm−1 shifted to the right as the concentration of the lithium salt increased.Peak of ether group (–C–O–C–) at 1017–1029 cm−1 (Figure 2) became intense while peak at 1105 cm−1 became almost a plateau due to overlapping peaks contributed by the Li+ bonded ether group, free bonded ether, and hydrogen ether.Figure 2
Peak of ether group (–C–O–C–) at 1017–1029 cm−1and 1105 cm−1 for the free bonded ether and hydrogen ether.However, Figure3 indicated a reduction in intensity of the hydrogen bonded carbonyl group at 1707 cm−1 as the concentration of salt increased. Meanwhile, peak of the nonhydrogen bonded carbonyl urethane group at 1720 cm−1 shifted to a lower frequency due to the interaction with lithium ions. From the observation conducted on the ATR-IR spectroscopy analysis, it can be deduced that lithium salts had interacted with both the hard segments which were the N–H and C=O and also the soft segment which was –C–O–C– of polyurethane and affected the crystallinity of polyurethane as observed in the XRD analysis [19].Figure 3
The hydrogen-bonded carbonyl group at 1707 cm−1 and the nonhydrogen bonded carbonyl urethane group at 1720 cm−1.


## 3.3. X-Ray Diffraction Analysis (XRD)

The X-ray diffraction analysis is used to determine the structure, complexation, and crystallization of the polymer matrix. The effect of complexation of PU-LiCF3SO3 system was investigated by performing XRD analysis where the appearance of the amorphous region or the reduction of the crystalline region would result in high ionic conductivity compared to the crystalline and semicrystalline region as reported by Su’ait et al. [21]. The measurement was conducted in the range of 5°–60° at diffraction angle of 2θ. Figure 4 shows the XRD pattern of pristine PU and the PU-LiCF3SO3 to study the change of crystalline structure upon addition of different weight percentages (10%, 20%, and 30%) of LiCF3SO3. From the diffractogram, we can observe that the pristine PU film was a semicrystalline polymer with a broad hump at 20° and crystalline peaks at 31°, 52°, and 53°. As the salt addition increased, the crystalline peaks decreased and disappeared as 30 wt% of LiCF3SO3 was added into PU. The hump becomes broader and flatter proving that the PU became more amorphous upon the salt addition [22]. In amorphous state, greater ionic diffusivity can occur as ions can move in the amorphous phase freely because of low energy barrier. Besides, the amorphous polymer exhibits more flexible backbone which can increase local chain mobility. Hence, the segmental motions of the polymer will also increase. This will then improve the transportation property of the electrolyte system [9].Figure 4
XRD patterns of PU1 with varying amount of LiCF3SO3.


## 3.4. Scanning Electron Microscopy (SEM)

Figure5 shows the SEM micrograph of the pristine PU film. It exhibited a clear and smooth surface. However, the presence of LiCF3SO3 in the PU film was obviously shown upon drying of the sample. Higher loading of the LiCF3SO3 gave more distribution of the LiCF3SO3 salt on the PU film. This was strongly supported by the XRD analysis where there was a reduction in the crystallinity of the sample. Thus, higher conductivity was observed. The micrographs of the PU electrolytes at 10, 20, and 30 wt% showed the uniformly distributed spherical grains in the electrolyte system (Figures 6, 7, and 8). The more the appearance of the LiCF3SO3 salt on the PU film, the higher the conductivity increase.Figure 5
SEM micrograph of pristine polyurethane.Figure 6
SEM micrograph of the PU film containing 10 wt% LiCF3SO3.Figure 7
SEM micrograph of the PU film containing 20 wt% LiCF3SO3.Figure 8
SEM micrograph of the PU film containing 30 wt% LiCF3SO3.


## 4. Conclusion

In this study, palm-based polyurethane solid polymer electrolyte was successfully prepared via prepolymerization method. The highest conductivity obtained was 1.6 × 10−5 S·cm−1 at 30 wt% of LiCF3SO3. FTIR spectroscopy analysis confirmed that there was possible interaction that occurred between PU and lithium ions in the amine, ether, and carbonyl group. The structural analysis recorded by XRD showed the reduction of the PU crystalline phase at the highest conductivity.



---

*Source: 326716-2014-03-30.xml*