# The Effect of Surface Functionalization on the Immobilization of Gold Nanoparticles on Graphene Sheets

Authors: Min Song; Juan Xu; Changzi Wu
Journal: Journal of Nanotechnology
 (2012)

---

## Abstract

In our study, graphene oxide is synthesized by Hummers method. And then, carboxylic acid functionalized graphene (graphene-COOH), thiol-functionalized graphene (graphene-SH), and highly dispersive graphene are prepared by chemical modification of respective groups on the graphene surface. Furthermore, we explore a solution-based approach to prepare three differently functionalized graphene-gold composites by one-step chemical reduction ofAuCl4- ions in respective functionalized graphene suspensions, where the gold nanoparticles are deposited on the functionalized graphene surface during their synthesis process. In addition, we compare the influence of surface functionalization on the growth of gold nanoparticles on graphene surface. Transmission electron morphology (TEM) and ultraviolet-visible (UV-Vis) spectroscopy are employed to study the effect of surface functionalities on AuNPs distribution onto the graphene surface and demonstrate the successful immobilization of AuNPs on graphene surface.


---

## Body

## 1. Introduction

The increasing interest in carbon family materials has opened new ways for producing arrays of novel functional nanomaterials. Among them, graphene, one-atom thick planar sheet of hexagonally arrayed sp2 carbon atoms, has attracted tremendous scientific attention in recent years. Graphite oxide (GO) is prepared from graphite by chemical oxidation, and then converted into a graphene nanosheets in bulk quantity by chemical and thermal reduction in solution to produce graphene [1–4]. Since abundant oxygen functional groups on the both basal plane and edge of GO can be used as anchoring sites for metal nanoparticles, it is possible to use them as a support to produce graphene-nanoparticle hybrids [5]. Furthermore, the covalently attaching oxygen groups, including hydroxyl, epoxy groups on the basal plane and carboxylic groups at the edge of GO surface is also versatile and effective method to prepare graphene-based hybrid materials by the chemical modification of graphene [6].The dispersion of metal nanoparticles on graphene sheets may result in the production of some excellent materials for various potential applications [7–10]. Among noble nanoparticles, AuNPs are one of the most studied nanomaterials, due to their remarkable properties [11–14]. A number of studies show that the hybridization of gold nanoparticles with GO followed by chemical reduction could improve the electrical conductivity and Raman signal [15, 16]. The hybrid materials prepared through the various functionalization strategies show potential applications in many fields such as catalyst, electronics, and biology [17–23]. However, the drawbacks for graphene-based hybrid materials are that the particle diameters of prepared gold nanoparticles are nonuniform, and the interaction between GO and AuNPs are weak.Therefore, we explore a simple approach to prepare three differently functional graphene materials as substrates to fabricate novel nanohybrid materials. The interaction between thiol, carboxyl, and oxygen groups and AuNPs is compared in the paper. The thiol-functionalized graphene (graphene-SH)/Au composites show the best performance compared to the other two hybrid materials due to the strong interaction between –SH and Au, offering an effective way to overcome the drawbacks mentioned above.


## 2. Material and Methods

### 2.1. Preparation of Differently Functionalized Graphene

The natural graphite was bought from Sigma. The graphite oxide (GO) was prepared from purified natural graphite according to Hummeras’s method.Carboxylic acid functionalized graphene (graphene-COOH) produced as follows. GO aqueous suspension (5 mL) was diluted as to give a concentration of 2 mg/mL, and then bath-sonicated for 1 h to give a clear solution. NaOH (1.2 g) and chloroacetic acid (Cl–CH2–COOH) (1.0 g) were added to the GO suspension and bath-sonicated for 1–3 h to convert the –OH groups into –COOH. The resulting GO-COOH solution was neutralized and purified by repeated rinsing and filtrations.Thiol-functionalized graphene (graphene-SH) was produced as follows. The synthesized graphite oxide was suspended in methylene dichloride by sonication for 10 min. And then, (3-mercaptopropyl) trimethoxysilane (MPTMS) was added into 2 mg/mL GO suspension by stirring-reflux method under nitrogen atmosphere. The filtrated solid was washed with tetrahydrofuran and ethanol three times to remove organic matter and dried in a vacuum oven at 60°C for 4 h.Highly dispersive graphene were produced as follows. The synthesized graphite oxide was suspended in water by sonication for 1 h. The suspension was mixed with sodium borohydride and sodium dodecyl benzene sulfonate by refluence at 80°C for 16 h. And then, the product was achieved by centrifugation and washing with water.


### 2.2. Preparation of Differently Functionalized Graphene-Gold Composites

The 2 mg graphene-COOH, graphene-SH, and dispersive graphene were, respectively, suspended in 1 wt% HAuCl4 solution (2 mL) by sonication for 5 min to make relative materials dispersed equably. The suspended solution was then diluted to 200 mL with doubly distilled water and heated to boiling while stirring. Afterward, 20 mL sodium citrates were added to the boiling solution which was kept heating for 30 min with magnetic stirring until the color of the solutions did not change. Then, the sample was cooled to room temperature, then separated in the centrifuge and washed with doubly distilled water five times. The resulting products were dried in a vacuum oven at 80°C for 12 h.


### 2.3. Characterization

TEM images were obtained by using JEM2000FX (JEOL). UV-Vis absorption spectroscopy was performed on Hitachi U-4100.


## 2.1. Preparation of Differently Functionalized Graphene

The natural graphite was bought from Sigma. The graphite oxide (GO) was prepared from purified natural graphite according to Hummeras’s method.Carboxylic acid functionalized graphene (graphene-COOH) produced as follows. GO aqueous suspension (5 mL) was diluted as to give a concentration of 2 mg/mL, and then bath-sonicated for 1 h to give a clear solution. NaOH (1.2 g) and chloroacetic acid (Cl–CH2–COOH) (1.0 g) were added to the GO suspension and bath-sonicated for 1–3 h to convert the –OH groups into –COOH. The resulting GO-COOH solution was neutralized and purified by repeated rinsing and filtrations.Thiol-functionalized graphene (graphene-SH) was produced as follows. The synthesized graphite oxide was suspended in methylene dichloride by sonication for 10 min. And then, (3-mercaptopropyl) trimethoxysilane (MPTMS) was added into 2 mg/mL GO suspension by stirring-reflux method under nitrogen atmosphere. The filtrated solid was washed with tetrahydrofuran and ethanol three times to remove organic matter and dried in a vacuum oven at 60°C for 4 h.Highly dispersive graphene were produced as follows. The synthesized graphite oxide was suspended in water by sonication for 1 h. The suspension was mixed with sodium borohydride and sodium dodecyl benzene sulfonate by refluence at 80°C for 16 h. And then, the product was achieved by centrifugation and washing with water.


## 2.2. Preparation of Differently Functionalized Graphene-Gold Composites

The 2 mg graphene-COOH, graphene-SH, and dispersive graphene were, respectively, suspended in 1 wt% HAuCl4 solution (2 mL) by sonication for 5 min to make relative materials dispersed equably. The suspended solution was then diluted to 200 mL with doubly distilled water and heated to boiling while stirring. Afterward, 20 mL sodium citrates were added to the boiling solution which was kept heating for 30 min with magnetic stirring until the color of the solutions did not change. Then, the sample was cooled to room temperature, then separated in the centrifuge and washed with doubly distilled water five times. The resulting products were dried in a vacuum oven at 80°C for 12 h.


## 2.3. Characterization

TEM images were obtained by using JEM2000FX (JEOL). UV-Vis absorption spectroscopy was performed on Hitachi U-4100.


## 3. Results and Discussion

The graphene oxide sheet, the oxidation of a graphene sheet, can be easily obtained by chemical conversion of inexpensive graphite oxide. Graphene oxide can be used as substrate for deposition of metal nanoparticles due to their unique advantages. For example, graphene oxide sheets have large surface areas and contain the abundance of functional groups (such as carboxyl, carbonyl, hydroxyl, and epoxide) on the surfaces and edges, which facilitate the synthesis of hybrids. Therefore, we firstly use the graphene oxide sheet as the substrate to synthesize carboxylic acid functionalized graphene (graphene-COOH), thiol-functionalized graphene (graphene-SH), and highly dispersive graphene, respectively. And then, the functional graphenes are immersed in HAuCl4 solution by one step chemical reduction to form the functional graphene-Au hybrids. Figure 1 illustrates the synthetic route for immobilization of Au nanoparticles onto the three differently functional graphene surfaces to obtain novel hybrids.Figure 1
Schematic illustration on the preparation route to immobilize gold nanoparticles onto differently functionalized graphene surface.Morphologies of Au nanoparticles deposited on functional graphene sheets have been characterized by TEM. Figure2 shows the typical TEM images of as-synthesized hybrids. As for dispersive graphene/Au hybrids, gold nanoparticles appear as dark dots with an average particle size of 20 nm. It is clearly seen in Figure 2(a) that the dispersive graphene oxide surface is uniformly decorated by the Au nanoparticles with very few aggregations, indicating a strong interaction between the dispersive graphene oxide and Au nanoparticles. The possible mechanism is that the abundant oxygen functional group on the graphene oxide surface might be used as nucleation sites for growth of Au nanoparticles. Meanwhile, much quantity of small aromatic conjugated domains on graphene oxide sheet will act as an electron-donating source to reduce Au ions and form smaller Au nanoparticles [24–26].TEM images of highly dispersive graphene/Au (a), carboxylic acid functionalized graphene /Au (b), and thiol-functionalized graphene/Au hybrids (c).
(a)
(b)
(c)However, as for the graphene-COOH/Au in Figure2(b), the sizes of the Au nanoparticles (black dots) are in the range of 8–40 nm. And they occupy only a very small portion of the carboxylic group functional graphene sheet surface. This is reasonable because GO is converted into graphene-COOH, much more oxygen containing groups were changed to carboxylic acid groups. Therefore, fewer functional groups will remain as nucleation sites, resulting in the formation of fewer particles.In addition, we prepare thiol group functionalized graphene with a simple and effective method. And then, the thiol groups are surrounded byAuCl4- that turned into small gold nanoparticles when meeting the reduce agents. Simultaneously, thiol groups could strongly bind gold nanoparticles. The success of functionalization reaction could be demonstrated from the TEM image in Figure 2(c). The results illustrate that the size and shape of Au nanoparticles are much more uniform compared to those on the other two hybrids. Au nanoparticles are distributed on the whole surface of thiol group functional graphene sheet. However, there is a little agglomeration on the surface. This is possibly due to that the graphene has more thiol functional groups, which provided stronger driving force for self-assembly of Au nanoparticles (GNPs).In addition, to furthermore demonstrate the success functionalization, we have further investigated the amount of the synthesized gold nanoparticles on the three differently functional graphene by using UV-vis absorption spectroscopy to explore the efficiency of the respective synthesis. As shown in Figure3, the absorption peak of Au nanoparticles are observed at 520 nm. After one step chemical reduction of Au ions in three differently functional graphene, the UV-Vis absorption spectroscopy of respective centrifugal suspensions show no absorption peak at 520 nm. The results indicate that the Au nanoparticles have been coated on the functional graphene surface, therefore, no gold absorption peak is observed. Therefore, the results of our UV-vis absorption spectroscopic studies of gold nanoparticles synthesized and the respective centrifugal suspensions in the presence of functional graphene indicate that more than 99% of the synthesized gold nanoparticles have been coated on the three differently functional graphene surface.UV-vis absorption spectra of colloid gold solution and centrifugal suspension in the presence of highly dispersive graphene/Au (a), carboxylic acid functionalized graphene /Au (b), and thiol-functionalized graphene/Au hybrids (c).
(a)
(b)
(c)


## 4. Conclusion

We prepare three functionalized graphene by a simple and effective method. Further, a straightforward one-step chemical synthesis method of Au nanoparticles on functionalized graphene surfaces is proposed. The results illustrate that the dispersive GO surface are uniformly decorated by the Au nanoparticles with very few aggregations for dispersive graphene/Au hybrids. And, the sizes of the Au nanoparticles show the wide range and occupy only a very small portion of the carboxylic group functional graphene sheet surface for graphene-COOH/Au hybrids. The results illustrate that the size and shape of Au nanoparticles are much more uniform compared to those on the other two hybrids due to the strong interaction between thiol groups and gold nanoparticles.



---