# Enhanced Strain-Dependent Electrical Resistance of Polyurethane Composites with Embedded Oxidized Multiwalled Carbon Nanotube Networks

Authors: R. Benlikaya; P. Slobodian; P. Riha
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

The effect of different chemical oxidation of multiwalled carbon nanotubes with H2O2, HNO3, and KMnO4 on the change of electrical resistance of polyurethane composites with embedded oxidized nanotube networks subjected to elongation and bending has been studied. The testing has shown about twenty-fold increase in the electrical resistance for the composite prepared from KMnO4 oxidized nanotubes in comparison to the composites prepared from the pristine and other oxidized nanotubes. The evaluated sensitivity of KMnO4 treated composite in terms of the gauge factor increases with strain to nearly 175 at the strain 11%. This is a substantial increase, which ranks the composite prepared from KMnO4 oxidized nanotubes among materials as strain gauges with the highest electromechanical sensitivity. The observed differences in electromechanical properties of the composites are discussed on basis of their structure which is examined by the measurements of Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and  scanning electron microscope. The possible practical use of the composites is demonstrated by monitoring of elbow joint flexion during two different physical exercises.


---

## Body

## 1. Introduction

In recent years there has been an increase in the studies on the composites composed of thermoplastic polyurethane (TPU) with carbon nanomaterials such as multiwalled carbon nanotubes (MWCNTs) [1], carbon nanofibers [2], and single- or multi-walled carbon nanotube networks (SWCNT-N, MWCNT-N), or buckypaper [3–5]. Thermoplastic polyurethane elastomers exhibit useful properties as abrasion resistance. However, since these polymers are not chemically cross-linked, they exhibit lower recoverability following elongation than cross-linked elastomers [6].The carbon nanotube networks (CNT-Ns) can proportionally transfer their unique properties into composites and bring about substantial improvements in their properties such as the strength, the electrical and thermal conductivity, the electromagnetic interference shielding compared to the polymer composites with CNT particulate filler [7]. Using CNT-Ns as a strain sensor has also potential advantage since the networks have high sensitivity to local distributions of stress and strain as well as the ability to sense stresses and strains in different directions in the host materials [8]. In this respect the strain sensitivities of epoxy [8], poly (methylmethacrylate) [9], and thermoplastic polyurethane composites [5] with MWCNT-Ns or SWCNT-Ns have already been studied. Moreover, there are also some studies on the effect of the functionalization of CNT-Ns with plasma [10, 11] as well as the carboxylic acid and amine groups [5] on the electrical properties [5, 11], thermal properties [5], and mechanical properties [10, 11] of polyurethane [5], polyimide [10] and polycarbonate [11] composites with CNT-Ns. Lima and coworkers stated that the range of property design possibilities of the elastomeric polyurethane composite is possible by tailoring the functional group content and the carbon nanotube load [5]. Nevertheless, according to our knowledge, no study related to examination of the effect of functionalized MWCNT-Ns with various oxidants on the strain sensitivity of TPU/MWCNT-N composites has been published yet. There are some studies showing various properties of CNT-polymer bulk composites to be affected by various oxidation conditions of nanotubes [12]. Rein and coworkers investigated the coupling between the electrical and mechanical properties of the CNT-N films made of SWCNTs and MWCNTs when embedded in several types of epoxies and observed different electromechanical responses [8]. However, this coupling is not affected only by the nanotube type but also by the interaction of the polymer matrix and CNT-N films [13].In this study, the thermoplastic polyester-based polyurethane composite with various MWCNT-Ns, oxidized by three agents as H2O2, HNO3, and KMnO4, is investigated in terms of their electrical resistance change during elongation and bending. The observed differences in electromechanical properties of TPU composites are discussed on basis of their structure which is examined by the Fourier transform infrared spectroscopy (FTIR), the X-ray photoelectron spectroscopy (XPS), and the scanning electron microscope (SEM).


## 2. Experimental

### 2.1. Materials

Purified MWCNTs produced by the chemical vapor deposition of acetylene were supplied by Sun Nanotech Co. Ltd., China, and characterized in our previous studies [4, 7, 14]. The thermoplastic polyurethane elastomer Desmopan DP 2590A was supplied by Bayer Material Science.KMnO4 oxidation: the oxidized MWCNTs were prepared in a glass reactor with a reflux condenser filled with 250 mL of 0.5 M H2SO4, into which 5 g of KMnO4 as oxidizing agent and 2 g of MWCNTs were added. The dispersion was sonicated at 85°C for 15 hours using thermostatic ultrasonic bath (Bandelin Electronic DT 103H). The dispersion was filtered, and then MWCNTs were washed with concentrated HCl to remove MnO2 and then washed with water until pH=7.HNO3 oxidation: 2 g of MWCNTs was added to 250 mL of HNO3 (concentrated) and heated at 140°C for 2 hours. After that the dispersion was cooled and filtered. The sediment was washed by deionized water and dried at 40°C for 24 hours.H2O2 oxidation: 1.5 g of MWCNTs was added to 30 mL of H2O2 and simultaneously stirred at 50 rpm (Heidolph, type MR HEI-standard) and heated for 72 hours at 65°C. Each day 5 mL of fresh hydrogen peroxide was added to original dispersion to refresh the activity of H2O2. In the end the dispersion was filtered and rinsed by water. The resulting product was dried at 40°C for 24 hours.For making an entangled MWCNT network, a porous polyurethane membrane and a vacuum filtration method were used. The homogenized dispersion of MWCNTs was vacuum filtered through the membrane. The formed networked layer had thickness about 35μm. The partial infiltration of MWCNTs into the filter pores creates an effective interlocking of MWCNT network layer with TPU filter which even strengthens when the porous filter is transformed into the polymeric film in the course of compression molding at 175°C. The detailed preparation of TPU membrane, MWCNT networks, and the composite was described in our previous paper [4].The network of pristine MWCNTs is denoted  below as  MWCNT-N, and the ones of oxidized MWCNTs are denoted as MWCNT-N (KMnO4), MWCNT-N (HNO3), MWCNT-N (H2O2). The composites of the size 10×30 mm were melt welded onto the surface of TPU tensile test specimen (dog-bone shaped) for extension and bending tests [4]. The shape and dimension are chosen according to standard EN ISO 3167. The resulting structure of prepared samples sensitive to deformation consists of three-layers structure. There is TPU specimen, TPU/MWCNT composite layer created from melted TPU filtering membrane with interfiltrated nanotubes, and pure MWCNT network originated on filter during filtration.


### 2.2. Characterization of MWCNT-N and TPU/MWCNT-N Composite

TEM of CNT material was performed using microscope JEOL JEM 2010 at the accelerating voltage of 160 kV. The sample for TEM was fabricated on 300 mesh copper grid with a carbon film (SPI, USA) from MWCNT dispersion in acetone prepared by ultrasonication, which was deposited on the grid and dried.The structure of MWCNT-Ns on the composites was analyzed by scanning electron microscope (SEM) Vega LMU, produced by Tescan Ltd. The samples were deposited on carbon targets and covered with a thin Au/Pd layer. For the observations the regime of secondary electron was chosen.XPS signals measured from MWCNT-Ns were recorded using a Thermo ScientificK-Alpha XPS system (Thermo Fisher Scientific, UK) equipped with a microfocused, monochromatic Al Kα X-ray source (1486.6 eV). An X-ray beam of 400 μm size was used at 6 mA × 12 kV. The spectra were acquired in the constant analyzer energy mode with pass energy of 200 eV for the survey. Narrow regions were collected using the snapshot acquisition mode (150 eV pass energy) enabling rapid collection of data (5 s per region). The narrow region data was postprocessed using Jansson’s algorithm to remove the analyser point spread function which resulted in improved resolution of the spectra for peak deconvolution [15].The resistance change of the composites was monitored by a two-point technique under different tensile loading. The time-dependent resistance change was measured by means of the Vernier LabQuest Interface System connected to the Differential Voltage Probe and the Wheatstone bridge with sampling frequency 200 Hz.Fourier transform infrared (FTIR) analyses of the MWCNT-Ns and the composite samples were performed on FT-IR spektrometr Nicolet 6700. Transmission accessory was used for the MWCNT-Ns samples in powder form prepared by KBr. FTIR-attenuated total reflectance (ATR) spectra of the interface of TPU/MWCNT composite layer where upper network made of pure CNT was washed out were obtained using Ge plate for ATR and repeated three times. The MWCNT-Ns were used for FTIR-ATR spectra of TPU/MWCNT composites as a background.


## 2.1. Materials

Purified MWCNTs produced by the chemical vapor deposition of acetylene were supplied by Sun Nanotech Co. Ltd., China, and characterized in our previous studies [4, 7, 14]. The thermoplastic polyurethane elastomer Desmopan DP 2590A was supplied by Bayer Material Science.KMnO4 oxidation: the oxidized MWCNTs were prepared in a glass reactor with a reflux condenser filled with 250 mL of 0.5 M H2SO4, into which 5 g of KMnO4 as oxidizing agent and 2 g of MWCNTs were added. The dispersion was sonicated at 85°C for 15 hours using thermostatic ultrasonic bath (Bandelin Electronic DT 103H). The dispersion was filtered, and then MWCNTs were washed with concentrated HCl to remove MnO2 and then washed with water until pH=7.HNO3 oxidation: 2 g of MWCNTs was added to 250 mL of HNO3 (concentrated) and heated at 140°C for 2 hours. After that the dispersion was cooled and filtered. The sediment was washed by deionized water and dried at 40°C for 24 hours.H2O2 oxidation: 1.5 g of MWCNTs was added to 30 mL of H2O2 and simultaneously stirred at 50 rpm (Heidolph, type MR HEI-standard) and heated for 72 hours at 65°C. Each day 5 mL of fresh hydrogen peroxide was added to original dispersion to refresh the activity of H2O2. In the end the dispersion was filtered and rinsed by water. The resulting product was dried at 40°C for 24 hours.For making an entangled MWCNT network, a porous polyurethane membrane and a vacuum filtration method were used. The homogenized dispersion of MWCNTs was vacuum filtered through the membrane. The formed networked layer had thickness about 35μm. The partial infiltration of MWCNTs into the filter pores creates an effective interlocking of MWCNT network layer with TPU filter which even strengthens when the porous filter is transformed into the polymeric film in the course of compression molding at 175°C. The detailed preparation of TPU membrane, MWCNT networks, and the composite was described in our previous paper [4].The network of pristine MWCNTs is denoted  below as  MWCNT-N, and the ones of oxidized MWCNTs are denoted as MWCNT-N (KMnO4), MWCNT-N (HNO3), MWCNT-N (H2O2). The composites of the size 10×30 mm were melt welded onto the surface of TPU tensile test specimen (dog-bone shaped) for extension and bending tests [4]. The shape and dimension are chosen according to standard EN ISO 3167. The resulting structure of prepared samples sensitive to deformation consists of three-layers structure. There is TPU specimen, TPU/MWCNT composite layer created from melted TPU filtering membrane with interfiltrated nanotubes, and pure MWCNT network originated on filter during filtration.


## 2.2. Characterization of MWCNT-N and TPU/MWCNT-N Composite

TEM of CNT material was performed using microscope JEOL JEM 2010 at the accelerating voltage of 160 kV. The sample for TEM was fabricated on 300 mesh copper grid with a carbon film (SPI, USA) from MWCNT dispersion in acetone prepared by ultrasonication, which was deposited on the grid and dried.The structure of MWCNT-Ns on the composites was analyzed by scanning electron microscope (SEM) Vega LMU, produced by Tescan Ltd. The samples were deposited on carbon targets and covered with a thin Au/Pd layer. For the observations the regime of secondary electron was chosen.XPS signals measured from MWCNT-Ns were recorded using a Thermo ScientificK-Alpha XPS system (Thermo Fisher Scientific, UK) equipped with a microfocused, monochromatic Al Kα X-ray source (1486.6 eV). An X-ray beam of 400 μm size was used at 6 mA × 12 kV. The spectra were acquired in the constant analyzer energy mode with pass energy of 200 eV for the survey. Narrow regions were collected using the snapshot acquisition mode (150 eV pass energy) enabling rapid collection of data (5 s per region). The narrow region data was postprocessed using Jansson’s algorithm to remove the analyser point spread function which resulted in improved resolution of the spectra for peak deconvolution [15].The resistance change of the composites was monitored by a two-point technique under different tensile loading. The time-dependent resistance change was measured by means of the Vernier LabQuest Interface System connected to the Differential Voltage Probe and the Wheatstone bridge with sampling frequency 200 Hz.Fourier transform infrared (FTIR) analyses of the MWCNT-Ns and the composite samples were performed on FT-IR spektrometr Nicolet 6700. Transmission accessory was used for the MWCNT-Ns samples in powder form prepared by KBr. FTIR-attenuated total reflectance (ATR) spectra of the interface of TPU/MWCNT composite layer where upper network made of pure CNT was washed out were obtained using Ge plate for ATR and repeated three times. The MWCNT-Ns were used for FTIR-ATR spectra of TPU/MWCNT composites as a background.


## 3. Results

### 3.1. FTIR Measurements

Table1 summarizes the frequencies of some functional groups in FTIR spectra of MWCNT-Ns. The OH stretch is shifted to lower wavelength for only MWCNT-N (H2O2) which could show the increase in the amount of hydrogen bonded hydroxyl groups. On the other hand, C–H stretching of MWCNTs is shifted to lower wavelength for all oxidation treatments.Table 1
Summary of FTIR measurements for the pristine and oxidized MWCNT-Ns.
Possible assignments
Wavenumber (cm−1)
MWCNT-N
MWCNT-N(H2O2)
MWCNT-N(HNO3)
MWCNT-N(KMnO4)
OH stretch
3435
3459
3428
3427
C–H stretch (CH2, CH3)
2908, 2840
2977, 2888
2980, 2880
2978, 2888
C=O stretch (carboxyl or ketone)
1705
1718
1726
1710
Intermediate oxidized products—quinone groups
1652
1637
1661, 1635
1641
C=C stretch
1559
1565
1580
1569
CH2/CH3 bending
1460
1443
1437
1440
Skeletal C–C tangential  motions + C–O stretch
1222
1219, 1167
1184
1190
C–O stretch
1082
1083, 1052
1084, 1049
1087, 1046A weak C=O peak at 1705 cm−1 was observed in pristine MWCNT-N, which shows that there is carbonyl or carboxylic group in its surface. The reason why pristine MWCNT-N has carbonyl and OH groups could be partial oxidation of the surfaces of MWCNTs during purification by the manufacturer [16]. The higher shift in the carbonyl stretching mode is seen for MWCNT-N (HNO3) than for other oxidized MWCNT-Ns. The reason may be a kind of C=O group or other groups that interacts with the C=O group. Zhang and coworkers found that even if the acid mixture and dilute nitric acid produce carboxylic group on the surface of SWCNTs, the strength vibration peaks are not at the same location due to possible different hydrogen bonding interactions [17]. The results summarized in Table 1 also show that there are probably no anhydride/lactone groups on the surfaces of MWCNTs since these groups are usually observed at around 1750 cm−1 or more high wavenumber [18–20].The peak assigned to quinone group at 1652 cm−1 in pristine MWCNT-N is usually shifted to higher wavelength in oxidized MWCNT-Ns. Coupling effects (i.e., both of intermolecular and inner molecular hydrogen bonding with hydroxyl groups) also might be responsible for the downshift in the C=O stretching mode, besides the production of surface-bound quinone groups with extended conjugation [21].The up-shift in the C=C stretching mode of MWCNT-Ns was observed for all oxidized MWCNT-Ns. The highest shift was observed for MWCNT-N (HNO3) compared to other MWCNT-N. This treatment may suggest a change in the structure of the MWCNT-N [17].The C–H (CH2/CH3) bending at 1460 cm−1 and the peak at 1222 cm−1 for MWCNT-N are shifted to higher wavelength for all oxidized MWCNT-Ns. The peak at around 1170 cm−1 assigned to C–OH group was also observed on MWCNT after H2O2 oxidation in another study [22]. A new band around 1050 cm−1 in FTIR spectra of oxidized MWCNT-Ns was also observed, which could be assigned to alcoholic C–O stretching vibration [22]. Overall, the observed changes in FTIR spectra of oxidized MWCNT-Ns confirm the efficiency of the oxidizing process and formation of the new oxygen-containing functional groups on the surface of carbon nanotubes.


### 3.2. XPS Data

The X-ray photoelectron spectroscopy was performed on the MWCNT-N specimens to get information on the functional groups attached onto the nanotube surface. The surface composition (in atomic %) was determined by considering the integrated peak areas of C1 and the respective sensitivity factors. The fractional concentration of a particular elementA was computed using
(1)%A=(IA/sA)Σ(In/sn)×100%,
where IA denotes the signal intensity of element A, In integrated peak areas, and  sA and sn the Scofield sensitivity factors corrected for the analyzer transmission.The main binding energy peak (284.5 eV) in XPS spectra of MWCNT-Ns was assigned to the C1s-sp2, while the other ones were assigned to C–O (286.2 eV), C=O (287.1 eV), O–C=O (288.6–289 eV), and C1s-π-π* (291.1–291.5 eV). XPS data in Figure 1 show that all MWCNT-Ns have C–OH, C=O, and O–C=O groups on their surface and that MWCNT-N (KMnO4), MWCNT-N (HNO3),  and MWCNT-N (H2O2) have maximum percentage of O–C=O, C=O, and C–OH, respectively. FTIR data of these MWCNT-Ns also confirm the presence of these functional groups on the surface. It was also stated in an other study that MWCNTs treated with (NH4)2S2O8, H2O2, and O3 have higher concentrations of carbonyl and hydroxyl functional groups, while more aggressive oxidants (e.g., HNO3, KMnO4) form higher fractional concentrations of carboxyl groups [23]. The acidic potassium permanganate (KMnO4) is a strong oxidizing agent and produces more surface acidic groups than nitric acid [24].Figure 1
Oxygen content (at %) on MWCNT-Ns oxidized by different reagents.The study of Fang and coworkers shows that XPS analysis is a useful and simple method for evaluating the content variation of amorphous carbon in SWNT samples by analyzing the sp3/sp2 carbon ratio [25]. According to our XPS results of MWCNT-Ns the carbon ratios are 2.50, 2.71, 3.50, and 1.69 for MWCNT-N, MWCNT-N (H2O2), MWCNT-N (HNO3), and MWCNT-N (KMnO4), respectively. The reason why the total oxygen amount for MWCNT-N (KMnO4) is less than that in case of other oxidants could be due to removing away more amount of the oxygen species originated from amorphous carbon structures during the acidified KMnO4 oxidation process.


### 3.3. From Tubes to Strain Sensing Element

Figures2(a)–2(e) summarize pathway of CNT application for strain sensing element. Part (a) represents TEM analyses of one individual MWCNT tube which typically consists of about 15–35 rolled layers of graphene. The SEM micrograph of the upper surfaces of MWCNT-N network created from entangled tubes is presented in part (b). Comparing results for each principal material it was found that the structures of networks slightly differ from each to other. MWCNT-N (KMnO4) seems to have smoother surface than others with more densely packed nanotubes and smaller diameters of pores. On the other hand, the most porous structure belongs to MWCNT-N (HNO3). The composite cross-section after the compression molding is shown in Figure 2(c) (upper black layer represents both pure MWCNT network and TPU/MWCNT composite interlayer while lower part is body of TPU specimen). Moreover, the melted polymer apparently encloses MWCNTs from MWCNT network surface in the course of molding at 175°C, making firm connection between the polymer and layer of entangled nanotubes. MWCNT network and TPU filtering membrane can be easily melt welded onto the surface of TPU tensile test specimen (dog-bone shaped) for extension and resistance tests, Figure 2(d). As an example of practical use of TPU/MWCNT composite as a strain sensing element, a strip of TPU/MWCNT-N composite was fixed on the elastic bandage to monitor human elbow flexion.Figure 2
(a) TEM micrograph of nanotube structure; (b) SEM micrograph of the surface of entangled MWCNT network; (c) the composite cross-section after the compression molding; (d) photograph of TPU dog-bone shaped specimen; (e) and  (a) position of measuring strip of TPU/MWCNT network composite on the elastic elbow bandage.


### 3.4. Tensile Deformation and Gauge Factor of MWCNT-N/PU Composites

The relative electrical resistance change, defined asΔR/R0=(R-R0)/R0, where R0 is the electrical resistance of the measured sample before the first elongation and R is the resistance while elongating, versus the percentage of mechanical strain is presented in Figure 3. The composite specimens are deformed by the tensile stress with increasing value in each cycle 0.43, 0.73, 1.07, 1.37, 1.71, 2.09, and 2.47 MPa. The increasing stress obviously enhances composite plastic deformation. Consequently, the residual strain increases in the off-load state with increasing number of cycles. The similar residual increase of the resistance is also observed except the resistance of TPU/MWCNT-N (KMnO4) composite which is reversible. Thus the nanotube oxidation by KMnO4 has a stabilizing effect on the cyclic resistance change. The testing has shown also the sixteen-fold increase in the resistance for the composite prepared from KMnO4 oxidized nanotubes in comparison to the composites prepared from the pristine and other oxidized nanotubes.Response of the relative resistance change and strain of the TPU composites versus the step increase of tensile strength (a) TPU/MWCNT-N, (b) TPU/MWCNT-N (H2O2), (c) TPU/MWCNT-N (HNO3), and (d) TPU/MWCNT-N (KMnO4).
(a)
TPU/MWCNT-N
(b)
TPU/MWCNT-N (H2O2)
(c)
TPU/MWCNT-N (HNO3)
(d)
TPU/MWCNT-N (KMnO4)Figure4 shows fast resistance change of the strips of composites anchored tightly on one side to bending deformation induced by the tip deflection of free ending. The oxidation treatment evidently causes the increase in the resistance change which is highest for TPU/MWCNT-N (KMnO4) composite.Figure 4
Time-dependent response of the strips of the TPU composites anchored tightly on one side to the initial deflection of free ending.The sensitivity of electrically conductive materials is usually evaluated by a gauge factor GF which is defined as the relative resistance change divided by the applied strainε, GF=(ΔR/R0)/ε  [26]. The gauge factors of the composites given in Figure 5 were calculated by using maximum values of resistance change and strain for each cycle in Figure 3. The gauge factor of CNT thin film was found to be 65 under room temperature for very low strain up to 0.05% [27]. Wang and coworkers found the Gauge factors of iodine-doped and iodine-undoped carbon nanotubes as 125 and 65, respectively [28].Figure 5
Gauge factors of the TPU composites.The calculated gauge factors of our composites increase with the strain up of  the maximum measured gauge factor which is for TPU/MWCNT-N, TPU/MWCNT-N (H2O2), TPU/MWCNT-N (HNO3), and TPU/MWCNT-N (KMnO4) about 8, 10, 12, and 175 for the strains 11, 9.1, 8.6 and 10.9%, respectively.


### 3.5. FTIR Spectra of the Composite Interfaces

As shown above, the type of MWCNTs significantly affects the resulting sensitivity of composites to strain. Rein and coworkers suggested in their study [8] that the source of the large difference in sensitivity between carbon nanotube network types in epoxy resins is the interaction between the polymer and MWCNTs [13]. The difference in the maximum strain values of the investigated composites could arise from the interactions in MWCNT-Ns and/or between TPU and MWCNT-Ns. At first FTIR spectra for the interface of the composites were measured using the MWCNT-Ns as a background.In the polyester-based polyurethane, the NH groups as proton donor and the oxygens in carbonyl groups of urethane and ester groups as proton acceptors behave in formation of hydrogen bonding. When MWCNT-Ns have hydroxyl, carboxyl, ketone, and ether groups on their surface, these groups can also play a part in forming hydrogen bonding between the polymer and MWCNT-Ns. Possible interactions between TPU and MWCNT-Ns are shown in Figure6 by considering FTIR and XPS data of MWCNT-Ns.Figure 6
The possible interactions between TPU and MWCNT-Ns. The distances among the functional groups are drawn randomly. They give no information about the strength of hydrogen bonding. Two headed arrows and dashed lines show repulsion forces and intermolecular hydrogen bonding, respectively.Some changes observed in FTIR spectra of TPU/MWCNT composites compared with that of pure TPU are given in Figure7 and Table 2. The broad -NH absorption between 3230 and 3430 cm−1 has been removed in TPU/MWCNT-N composites which could show that all NH groups are hydrogen bonded with some groups on the MWNTs. The CH bands (CH2/CH3) seen at 2957 and 2873 cm−1 in TPU are divided in the composites into three parts such as around 2960, 2917, and 2850 cm−1 due to the interaction with MWCNT-Ns.Table 2
Some peaks in FTIR spectra of TPU and TPU/MWCNT-Ns composites.
Possible assignments
Wavenumber (cm−1)
TPU
TPU/MWCNT-N
TPU/MWCNT-N(H2O2)
TPU/MWCNT-N(HNO3)
TPU/MWCNT-N(KMnO4)
C=O stretch
—
1759, 1744
1748
1759, 1743
1759
Free C=O stretch
1728
1726
1715
1723
1725
C=O stretch for hydrogenbonded urethane group
1706
1710, 1690
1700, 1683
1708, 1689
1707, 1688
C=O stretch for hydrogenbonded ester group
1662
1665
1652
1664
1662
NH bending + C=C stretch
1597
1574
1573
1574
1577
C–N stretch + N–H bending
1531
1535
1538
1539
1539Figure 7
FTIR spectra of TPU and the composites between 2400 and 3600 cm−1.The observed changes in three different carbonyl peaks of TPU can be seen in Table2. When the ones at 1728 and 1706 cm−1 split into two or three parts in the composites due to some interactions shown in Figure 6, some of three carbonyl peaks remained unchanged or shifted to higher/lower wavelengths for different composites. The more shifting to higher wavelength for all carbonyl peaks was observed for TPU/MWCNT-N (H2O2) due to probable hydrogen bonding between the C=O groups on TPU and –OH groups on the MWCNT-N.


### 3.6. FTIR Spectra of the Composite Interfaces Subjected to Strain

FTIR spectra related to the composite interfaces reveal some differences among the amounts of functional groups on the MWCNT-Ns. Hence FTIR spectra of TPU and the interfaces of TPU composites subjected to 7 various strains were examined. The values of strain could not be calculated properly due to the pressure of the ATR tip on the samples. Important differences among them are given in Figures8 and 9.Figure 8
Comparison of FTIR spectra of TPU/MWCNT-N (KMnO4) and TPU/MWCNT-N (HNO3) for various elongations.Figure 9
FTIR spectra of TPU/MWCNT-N for various elongation.Some peaks in the C=O stretch region of TPU/MWCNT-N (HNO3) which could interact with the -OH/-COOH groups on the MWCNT-N disappeared or shifted to lower wavenumber in the 2nd and 3rd elongations as follows from Figure 8, owing to new interactions of carbonyl groups on TPU with the functional groups on MWCNT-N (HNO3). On the other hand, the peaks in the C=O stretch region of TPU/MWCNT-N (KMnO4) remained unchanged. Figure 9 shows that hydrogen bond between NH group in TPU and C=O/-OH/-COOH group in the pristine MWCNT-N, schematically illustrated in Figure 6, was damaged in the 4th elongation. Such a situation was not observed for other TPU composites. The reason seems to be that there are less oxygenated groups on the pristine MWCNT-N in comparison with oxidized nanotube networks (Figure 1). The disappeared/changed interactions at interfaces of the composites with strain may influence the stress transfer between TPU and MWCNT networks. Hence, the observation may also give information about why TPU/MWCNT-N (HNO3) and TPU/MWCNT-N have lower resistance change with strain than TPU/MWCNT-N (KMnO4) when the interactions between MWCNTs may be affected due to the difference in the amount of functional groups on their surfaces.


### 3.7. Practical Use of TPU/MWCNT-N (KMnO4) Composite

The possible practical use of TPU/MWCNT-N (KMnO4) composite is demonstrated by monitoring of elbow joint flexion during two different physical exercises, namely, bodyweight dips and cable-based arm curls (Figure 10). The strip of the composite was adhered to an elastic bandage (83% of polyamide and 17% of elastolan) by means of dimethyl formamide/methyl isobutyl ketone (1 : 3) solution. The electrical contacts were fixed to the strip by a silver-colloid electroconductive paint Dotite D-550 (SPI Supplies), and the resistance was measured lengthwise by the two-point technique using multimeter Sefram 7338.Measurement of elbow joint flexion during (a) the bodyweight dips and (b) the cable-based arm curls.
(a)
(b)Figures11(a) and 11(b) show waveforms of the test performed by the volunteer with the bandage. The data are reversible and sensitive so that the composite can be used, for example, for the similar measurements in orthopedics and rehabilitation.Time-dependent resistance change of TPU/MWNCT-N (KMnO4) composite strain sensor during (a) the bodyweight dips and (b) the cable-based arm curls.
(a)
(b)


## 3.1. FTIR Measurements

Table1 summarizes the frequencies of some functional groups in FTIR spectra of MWCNT-Ns. The OH stretch is shifted to lower wavelength for only MWCNT-N (H2O2) which could show the increase in the amount of hydrogen bonded hydroxyl groups. On the other hand, C–H stretching of MWCNTs is shifted to lower wavelength for all oxidation treatments.Table 1
Summary of FTIR measurements for the pristine and oxidized MWCNT-Ns.
Possible assignments
Wavenumber (cm−1)
MWCNT-N
MWCNT-N(H2O2)
MWCNT-N(HNO3)
MWCNT-N(KMnO4)
OH stretch
3435
3459
3428
3427
C–H stretch (CH2, CH3)
2908, 2840
2977, 2888
2980, 2880
2978, 2888
C=O stretch (carboxyl or ketone)
1705
1718
1726
1710
Intermediate oxidized products—quinone groups
1652
1637
1661, 1635
1641
C=C stretch
1559
1565
1580
1569
CH2/CH3 bending
1460
1443
1437
1440
Skeletal C–C tangential  motions + C–O stretch
1222
1219, 1167
1184
1190
C–O stretch
1082
1083, 1052
1084, 1049
1087, 1046A weak C=O peak at 1705 cm−1 was observed in pristine MWCNT-N, which shows that there is carbonyl or carboxylic group in its surface. The reason why pristine MWCNT-N has carbonyl and OH groups could be partial oxidation of the surfaces of MWCNTs during purification by the manufacturer [16]. The higher shift in the carbonyl stretching mode is seen for MWCNT-N (HNO3) than for other oxidized MWCNT-Ns. The reason may be a kind of C=O group or other groups that interacts with the C=O group. Zhang and coworkers found that even if the acid mixture and dilute nitric acid produce carboxylic group on the surface of SWCNTs, the strength vibration peaks are not at the same location due to possible different hydrogen bonding interactions [17]. The results summarized in Table 1 also show that there are probably no anhydride/lactone groups on the surfaces of MWCNTs since these groups are usually observed at around 1750 cm−1 or more high wavenumber [18–20].The peak assigned to quinone group at 1652 cm−1 in pristine MWCNT-N is usually shifted to higher wavelength in oxidized MWCNT-Ns. Coupling effects (i.e., both of intermolecular and inner molecular hydrogen bonding with hydroxyl groups) also might be responsible for the downshift in the C=O stretching mode, besides the production of surface-bound quinone groups with extended conjugation [21].The up-shift in the C=C stretching mode of MWCNT-Ns was observed for all oxidized MWCNT-Ns. The highest shift was observed for MWCNT-N (HNO3) compared to other MWCNT-N. This treatment may suggest a change in the structure of the MWCNT-N [17].The C–H (CH2/CH3) bending at 1460 cm−1 and the peak at 1222 cm−1 for MWCNT-N are shifted to higher wavelength for all oxidized MWCNT-Ns. The peak at around 1170 cm−1 assigned to C–OH group was also observed on MWCNT after H2O2 oxidation in another study [22]. A new band around 1050 cm−1 in FTIR spectra of oxidized MWCNT-Ns was also observed, which could be assigned to alcoholic C–O stretching vibration [22]. Overall, the observed changes in FTIR spectra of oxidized MWCNT-Ns confirm the efficiency of the oxidizing process and formation of the new oxygen-containing functional groups on the surface of carbon nanotubes.


## 3.2. XPS Data

The X-ray photoelectron spectroscopy was performed on the MWCNT-N specimens to get information on the functional groups attached onto the nanotube surface. The surface composition (in atomic %) was determined by considering the integrated peak areas of C1 and the respective sensitivity factors. The fractional concentration of a particular elementA was computed using
(1)%A=(IA/sA)Σ(In/sn)×100%,
where IA denotes the signal intensity of element A, In integrated peak areas, and  sA and sn the Scofield sensitivity factors corrected for the analyzer transmission.The main binding energy peak (284.5 eV) in XPS spectra of MWCNT-Ns was assigned to the C1s-sp2, while the other ones were assigned to C–O (286.2 eV), C=O (287.1 eV), O–C=O (288.6–289 eV), and C1s-π-π* (291.1–291.5 eV). XPS data in Figure 1 show that all MWCNT-Ns have C–OH, C=O, and O–C=O groups on their surface and that MWCNT-N (KMnO4), MWCNT-N (HNO3),  and MWCNT-N (H2O2) have maximum percentage of O–C=O, C=O, and C–OH, respectively. FTIR data of these MWCNT-Ns also confirm the presence of these functional groups on the surface. It was also stated in an other study that MWCNTs treated with (NH4)2S2O8, H2O2, and O3 have higher concentrations of carbonyl and hydroxyl functional groups, while more aggressive oxidants (e.g., HNO3, KMnO4) form higher fractional concentrations of carboxyl groups [23]. The acidic potassium permanganate (KMnO4) is a strong oxidizing agent and produces more surface acidic groups than nitric acid [24].Figure 1
Oxygen content (at %) on MWCNT-Ns oxidized by different reagents.The study of Fang and coworkers shows that XPS analysis is a useful and simple method for evaluating the content variation of amorphous carbon in SWNT samples by analyzing the sp3/sp2 carbon ratio [25]. According to our XPS results of MWCNT-Ns the carbon ratios are 2.50, 2.71, 3.50, and 1.69 for MWCNT-N, MWCNT-N (H2O2), MWCNT-N (HNO3), and MWCNT-N (KMnO4), respectively. The reason why the total oxygen amount for MWCNT-N (KMnO4) is less than that in case of other oxidants could be due to removing away more amount of the oxygen species originated from amorphous carbon structures during the acidified KMnO4 oxidation process.


## 3.3. From Tubes to Strain Sensing Element

Figures2(a)–2(e) summarize pathway of CNT application for strain sensing element. Part (a) represents TEM analyses of one individual MWCNT tube which typically consists of about 15–35 rolled layers of graphene. The SEM micrograph of the upper surfaces of MWCNT-N network created from entangled tubes is presented in part (b). Comparing results for each principal material it was found that the structures of networks slightly differ from each to other. MWCNT-N (KMnO4) seems to have smoother surface than others with more densely packed nanotubes and smaller diameters of pores. On the other hand, the most porous structure belongs to MWCNT-N (HNO3). The composite cross-section after the compression molding is shown in Figure 2(c) (upper black layer represents both pure MWCNT network and TPU/MWCNT composite interlayer while lower part is body of TPU specimen). Moreover, the melted polymer apparently encloses MWCNTs from MWCNT network surface in the course of molding at 175°C, making firm connection between the polymer and layer of entangled nanotubes. MWCNT network and TPU filtering membrane can be easily melt welded onto the surface of TPU tensile test specimen (dog-bone shaped) for extension and resistance tests, Figure 2(d). As an example of practical use of TPU/MWCNT composite as a strain sensing element, a strip of TPU/MWCNT-N composite was fixed on the elastic bandage to monitor human elbow flexion.Figure 2
(a) TEM micrograph of nanotube structure; (b) SEM micrograph of the surface of entangled MWCNT network; (c) the composite cross-section after the compression molding; (d) photograph of TPU dog-bone shaped specimen; (e) and  (a) position of measuring strip of TPU/MWCNT network composite on the elastic elbow bandage.


## 3.4. Tensile Deformation and Gauge Factor of MWCNT-N/PU Composites

The relative electrical resistance change, defined asΔR/R0=(R-R0)/R0, where R0 is the electrical resistance of the measured sample before the first elongation and R is the resistance while elongating, versus the percentage of mechanical strain is presented in Figure 3. The composite specimens are deformed by the tensile stress with increasing value in each cycle 0.43, 0.73, 1.07, 1.37, 1.71, 2.09, and 2.47 MPa. The increasing stress obviously enhances composite plastic deformation. Consequently, the residual strain increases in the off-load state with increasing number of cycles. The similar residual increase of the resistance is also observed except the resistance of TPU/MWCNT-N (KMnO4) composite which is reversible. Thus the nanotube oxidation by KMnO4 has a stabilizing effect on the cyclic resistance change. The testing has shown also the sixteen-fold increase in the resistance for the composite prepared from KMnO4 oxidized nanotubes in comparison to the composites prepared from the pristine and other oxidized nanotubes.Response of the relative resistance change and strain of the TPU composites versus the step increase of tensile strength (a) TPU/MWCNT-N, (b) TPU/MWCNT-N (H2O2), (c) TPU/MWCNT-N (HNO3), and (d) TPU/MWCNT-N (KMnO4).
(a)
TPU/MWCNT-N
(b)
TPU/MWCNT-N (H2O2)
(c)
TPU/MWCNT-N (HNO3)
(d)
TPU/MWCNT-N (KMnO4)Figure4 shows fast resistance change of the strips of composites anchored tightly on one side to bending deformation induced by the tip deflection of free ending. The oxidation treatment evidently causes the increase in the resistance change which is highest for TPU/MWCNT-N (KMnO4) composite.Figure 4
Time-dependent response of the strips of the TPU composites anchored tightly on one side to the initial deflection of free ending.The sensitivity of electrically conductive materials is usually evaluated by a gauge factor GF which is defined as the relative resistance change divided by the applied strainε, GF=(ΔR/R0)/ε  [26]. The gauge factors of the composites given in Figure 5 were calculated by using maximum values of resistance change and strain for each cycle in Figure 3. The gauge factor of CNT thin film was found to be 65 under room temperature for very low strain up to 0.05% [27]. Wang and coworkers found the Gauge factors of iodine-doped and iodine-undoped carbon nanotubes as 125 and 65, respectively [28].Figure 5
Gauge factors of the TPU composites.The calculated gauge factors of our composites increase with the strain up of  the maximum measured gauge factor which is for TPU/MWCNT-N, TPU/MWCNT-N (H2O2), TPU/MWCNT-N (HNO3), and TPU/MWCNT-N (KMnO4) about 8, 10, 12, and 175 for the strains 11, 9.1, 8.6 and 10.9%, respectively.


## 3.5. FTIR Spectra of the Composite Interfaces

As shown above, the type of MWCNTs significantly affects the resulting sensitivity of composites to strain. Rein and coworkers suggested in their study [8] that the source of the large difference in sensitivity between carbon nanotube network types in epoxy resins is the interaction between the polymer and MWCNTs [13]. The difference in the maximum strain values of the investigated composites could arise from the interactions in MWCNT-Ns and/or between TPU and MWCNT-Ns. At first FTIR spectra for the interface of the composites were measured using the MWCNT-Ns as a background.In the polyester-based polyurethane, the NH groups as proton donor and the oxygens in carbonyl groups of urethane and ester groups as proton acceptors behave in formation of hydrogen bonding. When MWCNT-Ns have hydroxyl, carboxyl, ketone, and ether groups on their surface, these groups can also play a part in forming hydrogen bonding between the polymer and MWCNT-Ns. Possible interactions between TPU and MWCNT-Ns are shown in Figure6 by considering FTIR and XPS data of MWCNT-Ns.Figure 6
The possible interactions between TPU and MWCNT-Ns. The distances among the functional groups are drawn randomly. They give no information about the strength of hydrogen bonding. Two headed arrows and dashed lines show repulsion forces and intermolecular hydrogen bonding, respectively.Some changes observed in FTIR spectra of TPU/MWCNT composites compared with that of pure TPU are given in Figure7 and Table 2. The broad -NH absorption between 3230 and 3430 cm−1 has been removed in TPU/MWCNT-N composites which could show that all NH groups are hydrogen bonded with some groups on the MWNTs. The CH bands (CH2/CH3) seen at 2957 and 2873 cm−1 in TPU are divided in the composites into three parts such as around 2960, 2917, and 2850 cm−1 due to the interaction with MWCNT-Ns.Table 2
Some peaks in FTIR spectra of TPU and TPU/MWCNT-Ns composites.
Possible assignments
Wavenumber (cm−1)
TPU
TPU/MWCNT-N
TPU/MWCNT-N(H2O2)
TPU/MWCNT-N(HNO3)
TPU/MWCNT-N(KMnO4)
C=O stretch
—
1759, 1744
1748
1759, 1743
1759
Free C=O stretch
1728
1726
1715
1723
1725
C=O stretch for hydrogenbonded urethane group
1706
1710, 1690
1700, 1683
1708, 1689
1707, 1688
C=O stretch for hydrogenbonded ester group
1662
1665
1652
1664
1662
NH bending + C=C stretch
1597
1574
1573
1574
1577
C–N stretch + N–H bending
1531
1535
1538
1539
1539Figure 7
FTIR spectra of TPU and the composites between 2400 and 3600 cm−1.The observed changes in three different carbonyl peaks of TPU can be seen in Table2. When the ones at 1728 and 1706 cm−1 split into two or three parts in the composites due to some interactions shown in Figure 6, some of three carbonyl peaks remained unchanged or shifted to higher/lower wavelengths for different composites. The more shifting to higher wavelength for all carbonyl peaks was observed for TPU/MWCNT-N (H2O2) due to probable hydrogen bonding between the C=O groups on TPU and –OH groups on the MWCNT-N.


## 3.6. FTIR Spectra of the Composite Interfaces Subjected to Strain

FTIR spectra related to the composite interfaces reveal some differences among the amounts of functional groups on the MWCNT-Ns. Hence FTIR spectra of TPU and the interfaces of TPU composites subjected to 7 various strains were examined. The values of strain could not be calculated properly due to the pressure of the ATR tip on the samples. Important differences among them are given in Figures8 and 9.Figure 8
Comparison of FTIR spectra of TPU/MWCNT-N (KMnO4) and TPU/MWCNT-N (HNO3) for various elongations.Figure 9
FTIR spectra of TPU/MWCNT-N for various elongation.Some peaks in the C=O stretch region of TPU/MWCNT-N (HNO3) which could interact with the -OH/-COOH groups on the MWCNT-N disappeared or shifted to lower wavenumber in the 2nd and 3rd elongations as follows from Figure 8, owing to new interactions of carbonyl groups on TPU with the functional groups on MWCNT-N (HNO3). On the other hand, the peaks in the C=O stretch region of TPU/MWCNT-N (KMnO4) remained unchanged. Figure 9 shows that hydrogen bond between NH group in TPU and C=O/-OH/-COOH group in the pristine MWCNT-N, schematically illustrated in Figure 6, was damaged in the 4th elongation. Such a situation was not observed for other TPU composites. The reason seems to be that there are less oxygenated groups on the pristine MWCNT-N in comparison with oxidized nanotube networks (Figure 1). The disappeared/changed interactions at interfaces of the composites with strain may influence the stress transfer between TPU and MWCNT networks. Hence, the observation may also give information about why TPU/MWCNT-N (HNO3) and TPU/MWCNT-N have lower resistance change with strain than TPU/MWCNT-N (KMnO4) when the interactions between MWCNTs may be affected due to the difference in the amount of functional groups on their surfaces.


## 3.7. Practical Use of TPU/MWCNT-N (KMnO4) Composite

The possible practical use of TPU/MWCNT-N (KMnO4) composite is demonstrated by monitoring of elbow joint flexion during two different physical exercises, namely, bodyweight dips and cable-based arm curls (Figure 10). The strip of the composite was adhered to an elastic bandage (83% of polyamide and 17% of elastolan) by means of dimethyl formamide/methyl isobutyl ketone (1 : 3) solution. The electrical contacts were fixed to the strip by a silver-colloid electroconductive paint Dotite D-550 (SPI Supplies), and the resistance was measured lengthwise by the two-point technique using multimeter Sefram 7338.Measurement of elbow joint flexion during (a) the bodyweight dips and (b) the cable-based arm curls.
(a)
(b)Figures11(a) and 11(b) show waveforms of the test performed by the volunteer with the bandage. The data are reversible and sensitive so that the composite can be used, for example, for the similar measurements in orthopedics and rehabilitation.Time-dependent resistance change of TPU/MWNCT-N (KMnO4) composite strain sensor during (a) the bodyweight dips and (b) the cable-based arm curls.
(a)
(b)


## 4. Conclusions

Multi-walled carbon nanotubes were used in their pure and oxidized forms to prepare entangled networks as a part of TPU/MWCNT-N composites. The response of composites to deformation was measured by their electrical resistance change in the course of extension/relaxation cycles and bending. The results show that the composite with KMnO4 oxidized nanotube network has an enhanced electrical resistance with loading in comparison with the network prepared from the pristine and other oxidized nanotubes. The evaluated sensitivity of TPU/MWCNT-N (KMnO4) composite in terms of the gauge factor increases with strain from values around 5 at the start of deformation to 175 at the strain 11%. This is a substantial increase, which ranks the composite among the materials with the highest electromechanical sensitivity.The distinct resistance and sensitivity increase with elongation and bending may come probably from the different porous structure of MWCNT (KMnO4) network, the interaction between TPU and MWCNT-N (KMnO4) and the increased number of carboxyl groups detached on MWCNT-N (KMnO4) surface. The short oxidized nanotubes, forming densely packed network with small pores, probably lose mechanical contacts with other ones more easily in the course of composite elongation than the longer pristine nanotubes. The unchanged interactions between TPU and MWCNT-N (KMnO4) at the composite interface during the elongation, discussed in details in Section 3.6, may ensure stress transfer from the elastic TPU to the network and its extensive rearrangement and loss of nanotube contacts. Similarly, the increased presence of carboxyl groups on the surface of MWCNT-N (KMnO4) in comparison with other investigated networks (Figure 1) enhances interaction of nanotubes via two interaction points (carbonyl and hydroxyl groups). Thus during elongation more chemical links between nanotubes fade which results also in  loss of conductive points, and consequently, the resistance rise.



---

*Source: 327597-2013-10-08.xml*