# Synthesis and Characterization of Bifunctionalα-Fe2O3-Ag Nanoparticles

Authors: Alvaro Ruíz-Baltazar; Simón Yobanny Reyes-López; Rodrigo Esparza; Miriam Estévez; Ángel Hernández-Martínez; Gerardo Rosas; Ramiro Pérez
Journal: Advances in Condensed Matter Physics
 (2015)

---

## Abstract

The synthesis ofα-Fe2O3-Ag bimetallic nanoparticles using a novel and simplified route is presented in this work. These hybrid nanoparticles were produced using a modification of the chemical reduction method by sodium borohydride (NaBH4). Fe(III) chloride hexahydrate (FeCl3·6H2O) and silver nitrate (AgNO3) as precursors were employed. Particles with semispherical morphology and dumbbell configuration were observed. High-resolution transmission electron microscopy (HRTEM) technique reveals the structure of the dumbbell-like α-Fe2O3-Ag nanoparticles. Some theoretical models further confirm the formation of the α-Fe2O3-Ag structures. Analysis by cyclic voltammetry reveals an interesting catalytic behavior which is associated with the combination of the individual properties of the Ag and α-Fe2O3 nanoparticles.


---

## Body

## 1. Introduction

Bimetallic nanoparticles with dumbbell-like heterostructures have recently attracted increasing attention on these nanoparticles exhibiting different physical and chemical properties and an interesting interfacial interaction between two coexisting materials. This property offers potential applications in the fields of physics, biotechnology, chemistry, materials science, biology, and catalysis [1–3]. In particular, the bimetallic α-Fe2O3-Ag dumbbell-like nanoparticles have enhanced physical-chemical properties, since the Ag nanoparticles present an excellent catalytic activity, antibacterial effect, and a significant biocompatibility [4–7]. On the other hand, α-Fe2O3 possess magnetic properties. In this sense, hybrid α-Fe2O3-Ag nanoparticles represent a nanostructure suitable for drug delivery, phototherapy heterogeneous catalysis, and biosensors among others [8–11]. Consequently, research of new synthesis routes for bimetallic nanoparticles is fundamental in the development of nanotechnology [12–14]. Under this perspective, the possibility to synthesize new nanostructures by mixing noble metals and magnetic nanoparticles offers a wide range of future applications. For this reason, the aim of this research is to present a novel and simplified synthesis route to obtain α-Fe2O3-Ag dumbbell-like nanostructures. This procedure is based on the modification of the chemical reduction method [15], which is carried out at room temperature and the pH of the aqueous solution is not considered. Factors such as the quantities of metallic precursors and the amount of surfactant agent used in the synthesis process are important for determining the growth of the α-Fe2O3-Ag bimetallic nanoparticles [10, 16]. In order to characterize the dumbbell or heterodimers nanostructures, techniques of transmission electron microscopy (TEM), Raman spectroscopy (RMN), and cyclic voltammetry (CV) were employed.


## 2. Materials and Methods

Theα-Fe2O3-Ag dumbbell nanoparticles were produced using a modification of the chemical reduction method [15]. First, the α-Fe2O3 nanoparticles were obtained by the reduction of Fe(III) chloride hexahydrate (0.01 M) with sodium borohydride NaBH4 (0.02 M) and stabilized using polyvinylpyrrolidone (PVP) at constant concentration of 0.5 M. The α-Fe2O3 nanoparticles were stirred magnetically at 600 rpm for 10 minutes. Finally, a solutions of AgNO3 (0.02 M) was added dropwise to the α-Fe2O3 nanoparticles. This process was carried out at room temperature. For the determination of the electrochemical behavior, a PGSTAT Autolab 302 Potentiostat/Galvanostat (Metrohm) was used. In this procedure, 30 μL of α-Fe2O3-Ag nanoparticles in solution was mixed with 5 mg of carbon. Subsequently, ethanol and Nafion were added to the bimetallic nanoparticles. For the structural characterization of α-Fe2O3-Ag dumbbell nanoparticles, a transmission electron microscopy TEM (Phillips Tecnai F-20) was employed to observe the morphology and sizes of iron-silver nanoparticles.


## 3. Results and Discussion

Figure1(a) shows a bright field TEM image of the nanostructures obtained by chemical reduction. This image shows dispersed heterodimers or dumbbell-like nanostructures. This kind of structures presents a typical configuration which consists of a nanoparticle with known composition and size and which is attached to another particle whose composition is different and its size is generally smaller. In order to probe that two different elements are present in this heterodimers nanostructures, Figure 1(b) reveals the chemical composition of the bimetallic structures obtained by EDS technique. Figure 1(c) present a Z-contrast image obtained by high angle angular dark field (HAADF), which illustrates that the particles with smaller size and higher contrast are associated with the Ag, due to the fact that this element has a higher atomic number (Z) in relation to the iron. Ag nanoparticles show higher contrasts region (lighter). Consequently, darker region corresponds to nanoparticle with low Z (Fe). In this sense, Figure 1(d) shows a bright field TEM image of an individual nanostructure where Ag nanoparticles with higher Z exhibit darker contrast. Also, as will be discussed later by high-resolution transmission electron microscopy HRTEM technique and Raman spectroscopy, the nature of the Fe structure present in the heterodimer will be determined.Figure 1
(a) TEM image ofα-Fe2O3-Ag dumbbell-like nanoparticles, (b) EDS chemical analysis (c) Z-contrast image (HAADF), and (d) bright field TEM image of an individual α-Fe2O3-Ag nanoheterodimers.
(a)
(b)
(c)
(d)To verify the Fe nanostructure present in the HRTEM analysis that was carried out, Figure2(a) reveals the d-spacing related to the heterodimer, in which we can observe distances of 0.235, 0.236, and 0.198 nm corresponding to the planes (
1
-
1
-
1
), (
1
-
11
), and (020) of Ag, respectively (JCPDF #04-0783). Additionally, an interplanar distance of 0.189 nm associated with the α-Fe2O3 (JCPDF #33-0664) was observed. Figure 2(b) illustrates the FFT of the α-Fe2O3-Ag system. Also, Figures 2(c) and 2(d) show in detail the interface of the heterodimer, where the presence of both entities is confirmed. This result suggests that the Fe nanoparticles were oxidized. Some reports indicate that the iron nanoparticles can be oxidized by many factors as pH of aqueous solution and oxidative etching among others [10, 16]. In particular, in this synthesis process, the pH of the aqueous solution was constant; therefore, it can be deduced that oxidative species such as oxygen, Fe(III) in solution, and corrosive ions as chlorides present during the chemical synthesis favor the oxidation process.Figure 2
(a) HREM image of theα-Fe2O3-Ag interface, (b) FFT of the HREM image associated with the α-Fe2O3-Ag bimetallic nanoparticles, and (c) HREM filtered image of dumbbell-like particle.Under this perspective, it is important to establish the structure and crystallinity of the nanoparticles. Ag andα-Fe2O3-Ag nanoparticles have a cubic FCC structures. In this sense, Figure 3(a) describes a simulation model of the dumbbell-like nanostructure. The Ag nanoparticle modelling (Inodecahedron) has an average size of 7 nm according to the experimental Ag nanoparticle observed by TEM and high angle annular dark field (HAADF) images, while α-Fe2O3-Ag structures show an average diameter of 20 nm. In order to verify the structures observed by HRTEM images, a simulated TEM image was constructed from the proposed model (Figure 3(b)). The method to obtain the theoretical images (HRTEM) is based on the multislice approach of electron diffraction dynamical theory [17]. This simulated image presents a close similarity to the experimental HRTEM image. Hence, this model describes accurately the α-Fe2O3-Ag heterodimers formation. The axis zone used to the TEM image simulation was [201]. Figure 3(c) describes in detail the simulated interface of the α-Fe2O3 and Ag structures. This image exhibits a great similarity with the experimental HRTEM image shown in Figure 2(c). Therefore, the proposed models and simulated images confirm and support the characterization carried out by the HRTEM technique, which indicates the presence of α-Fe2O3 and Ag nanostructures.Figure 3
(a) Simulation model of the dumbbell-likeα-Fe2O3-Ag nanostructure, (b) simulated bright field image, and (c) simulated image from the interface of α-Fe2O3-Ag.
(a)
(b)
(c)Nevertheless, the iron species such as the maghemite (γ-Fe2O3) and hematite (α-Fe2O3) are very similar from the point of view of their electronic configuration, lattice parameter, and d-spacing [17–19]. For this reason, it is important to accurately set the kind of iron oxide observed. Some reports indicate that by XRD technique it is possible to establish only the structural differences between two iron oxides [20–22]. In this regard, Raman spectroscopy can provide clear assignment of the iron oxide polymorphs through the observation of the phonon modes. The iron oxides species exhibit distinct Raman signatures; therefore, it is possible to take advantage of the so-called phonon confinement effects to confirm the oxide present in the sample [23]. In order to demonstrate accurately the type of oxide present in the system, a Raman spectrum of dumbbell nanoparticles is presented in Figure 4.Figure 4
Raman spectrum of theα-Fe2O3-Ag bimetallic system.In these Raman spectra, typical intensities from the hematite structure located at 221 cm−1 (A1g), 241 cm−1 (Eg), 295 cm−1 (Eg), and 504 (A1g) are observed. However, two bands situated at 365 and 551 cm−1 are attributed to maghemite and magnetite, respectively [23]. These bands account for only minority phases, with hematite being the predominant phase, thus confirming the results obtained by HRTEM. Complementarily, the presence of the Ag nanoparticles is demonstrated by the bands situated at 1342 and 1645 cm−1 [20, 21].The formation of this kind of nanostructures can be discussed from the point of view of the solubility, since in general terms these elements are immiscible in the solid state, promoting the dumbbell configuration. In addition, the nucleation rate takes preponderant role in the formation of the Fe2O3-Ag system because Fe nanoparticles, previously formed, offer nucleation sites for forming Ag nanoparticles through a heterogeneous nucleation. Thermodynamically, Ag solution atoms nucleate in regions where the energy barrier is lower, in this case in the α-Fe2O3 nanoparticles. To expand the discussion regarding the factors that involved the growing of these nanostructures, the surface charges associated with the active sites of the nanoparticles should be considered [18]. Based on the fact that the particle size and structure type determine the compensation charge in the nanoparticles surface, it can be deduced that mainly the size of decahedral Ag nanoparticles would influence the charge compensation and hence the formation of Fe2O3 heterostructures [24], due the fact that the decahedral nanoparticles exhibit greater reactivity. In this regard, some studies have reported these structures as a function of the α-Fe2O3 size/size Ag seed ratio [22, 23]. It is important to highlight the synthesis methodology presented in this research since it offers a simple route for obtaining controlled bimetallic nanostructures. This synthesis is carried out at room temperature while some other methodologies involve temperature (~400°C) [22, 24–26].In order to establish a reference parameter regarding the electrochemical behavior of the bimetallic system (α-Fe2O3-Ag) and Ag nanoparticles, Figure 5 shows the cyclic voltammogram corresponding to the bimetallic and monometallic nanoparticles. It can be seen that in the case of bimetallic nanoparticles there is an increase in the current density of the redox processes involved in comparison with the monometallic nanoparticles. Additionally, α-Fe2O3-Ag heterodimers nanostructures present a displacement in the values associated with the potential formation and reduction of metal oxides. Based on this behavior, it can be deduced that the two systems have different electrochemical characteristics. It is important to note that the presence of α-Fe2O3 increases the region where monolayers of oxides are formed. It has been reported that the position of hydrogen adsorption/desorption peak and the oxygen reduction peak is proportional to the nanoparticle size [27]. Nevertheless, the synthesis of monometallic (Ag) and bimetallic (α-Fe2O3-Ag) nanoparticles was carried out analogously under the same conditions, such that very similar particle sizes were obtained. In this sense, the electrochemical comparison of both systems is considerably accurate. Hence, through this technique, it is possible to determine the electrochemical behavior of the monometallic (Ag) nanoparticles and the influence of hematite in the processes of oxidation and reduction.Figure 5
Cyclic voltammograms of theα-Fe2O3-Ag and Ag nanoparticles in acid medium employed a solution of H2SO4 (0.5 M). Scan rate 50 mV s−1 at 25°C in presence of N2.


## 4. Conclusions

The synthesis ofα-Fe2O3-Ag dumbbell-like nanostructures or heterodimers was performed using a novel and simplified route, in which factors as temperature and pH of the aqueous solution were constant. It was observed that the formation of these nanostructures is favored by factors such as compensation charges generated by Ag and α-Fe2O3 particles, which are derived from the structure type and the active sites of these entities. Moreover, structural characterization of the bimetallic system was carried out mainly by TEM techniques, and corroborated by modeling and simulation of HRTEM images. However, the different species of iron oxides have a large number of similarities as lattice parameters, d-spacings, and chemical composition. Thus, an analysis by Raman spectroscopy was conducted, in order to specify the type of iron oxide present in the bimetallic system. This study confirms that the majority phase of this system is hematite. Nevertheless, some traces of maghemite and magnetite were identified. On the other hand, the electrochemical characterization reveals that this kind of bimetallic nanostructure offers potential catalytic applications, given their particular behavior observed in the studies of cyclic voltammetry. It should be noted that the oxidation and reduction potentials are very well defined and hence a significant catalytic activity could be expected.



---

*Source: 320873-2015-12-14.xml*