# Magnetization Reversal in Ferromagnetic Nanorings of Fourfold Symmetries

Authors: Andrea Ehrmann; Tomasz Blachowicz
Journal: Advances in Materials Science and Engineering
 (2017)

---

## Abstract

Magnetic nanoparticles offer a broad spectrum of magnetization reversal processes and respective magnetic states, such as onion, horseshoe, or vortex states as well as various states including domain walls. These states can be correlated with stable intermediate states at remanence, enabling new quaternary memory devices storing two bits in one particle. The stability of these intermediated states was tested with respect to shape modifications, variations in the anisotropy axes, and rotations and fluctuations of the external magnetic field. In our micromagnetic simulations, 6 different stable intermediate states were observed at vanishing magnetic field in addition to the remanence state. The angular region of approx. 5°–12° between nanoring and external magnetic field was identified as being most stable with respect to all modifications, with an onion state as technologically best accessible intermediate state to create quaternary memory devices.


---

## Body

## 1. Introduction

Magnetic nanoparticles have gained the interest of several research groups due to their unique magnetic properties, enabling their possible application in magnetic storage media, sensors, MRAMs, spin valves, and so on [1–6]. In magnetic nanoparticles, shape anisotropy is significantly stronger than magnetocrystalline and magnetoelastic anisotropy so that the magnetic properties can be changed by modifications of the particle shape [7]. This is why magnetic nanodots and nanorings were shown to enable formation of a broad variety of magnetic states, such as onion or horseshoe, flux-closed vortex states, and domain wall states [8–15].Particularly “square rings” of different shapes and materials have shown interesting magnetic properties. In several situations, hysteresis loops with steps on both sides occur in theoretical and experimental investigations, allowing creating “quaternary” memory systems with four stable states at vanishing external magnetic field and thus the possibility of storing two bits in one position [16]. On the other hand, experimental investigation of these structures has revealed undesired modifications of the original rings’ shapes in the lithography process, resulting in modified magnetization reversal processes [17, 18]. This experience underlines the necessity of examining the influence of such shape modifications to allow creation of nanorings with reliable magnetic properties.In this paper, phase diagrams of magnetic states are presented for “ideal” and “real” square rings, varying the magnetocrystalline anisotropy axes between a random state, as in a typical sputtered sample, and two epitaxial states, as they could be gained by molecular beam epitaxy (MBE) [19] or self-assembly [20], for a complete in-plane rotation of the nanoring with respect to the external field.


## 2. Materials and Methods

For modelling, the micromagnetic simulator OOMMF (Object Oriented Micromagnetic Framework) [21] was used which is based on finite differences (discretizing space into small cuboids) and the Landau-Lifshitz-Gilbert (LLG) equation of motion [22].Nanostructures of two different geometries were chosen for simulation (Figure1): one square ring with “ideal” square corner cuts which has shown to result in intermediate stable states at remanence [16] and one ring with “realistic” diagonal corner cuts which was gained in former lithographic processes [17, 18]. Lateral dimensions were chosen as 200 nm diameter and 5 nm height, similar to real nanorings under experimental investigation [17, 18].Figure 1
Ring shapes used for simulations with square (a) and diagonal corner cuts (b).
(a) (b)As material, iron (Fe) was chosen which showed ideal properties to reach the aforementioned intermediates states [23]. The chosen parameters were as follows: saturation magnetization MS=1700·103 A/m, exchange constant A=21·10-12 J/m, anisotropy constant K1=48·103 J/m3, Gilbert damping constant α=0.1, and mesh diameterd = 5 nm. These values are consistent with typical literature values [24]. The damping constant is slightly increased, compared with values measured in Fe nanostructures [25], to avoid oscillations which would not occur in real experiments with relatively slow field sweeps.To avoid statistical variations which would superpose the effects due to interactions between the neighboring nanorings, the influence of thermal fluctuations of temperatures above zero was ignored. It can be assumed that any temperature above zero will further decrease the field regions in which all nanorings show the same behavior.The anisotropy was on the one hand assumed to be uniform on the macroscale, that is, having randomly distributed axes in each cell, to create a sputtered nanoring with polycrystalline structure. In other simulations, the anisotropy axes were fixed at 0°/90° as well as at ±45° to create both extremal cases of epitaxially grown nanorings.The external magnetic field was applied parallel to the sample plane. The sample orientation was varied between 0° (external magnetic field parallel to thex-axis of the sample/to one side of the nanoring) and 45° in steps of 5°. Maximum external fields between ±0.2 T and ±0.3 T were used, depending on the angle, to ensure reaching magnetization saturation. Additionally, minor loops were simulated to investigate the possibility of creating additional stable magnetic states at vanishing external magnetic field.


## 3. Results and Discussion

Figure2 depicts a typical hysteresis loop, simulated in the angular region of 1°–15°. While the (positive) saturated state is an onion state, magnetization reversal occurs via a horseshoe state, another anion, and a second horseshoe until finally the next onion state is reached which is the (negative) saturated state. These magnetization states are shown in Figure 3. While the intermediate onion state occurs nearly always in this angular region, the horseshoe states may vanish, depending on the angle, geometry, and anisotropy (epitaxial or sputtered) of the nanoring.Figure 2
Sample hysteresis loop with the main magnetization states identified as onion and horseshoe states. Lilac marks depict the coercive fieldHCoerc as well as the fields defined as HConnect and HMinor.Figure 3
Possible magnetic states for not-too-large angles: horseshoe 1 (a), onion (b), and horseshoe 2 (c).
(a) (b) (c)While these states are also visible in the “realistic” shape with diagonal corner cuts, other states occur exclusively in the “ideal” nanorings with square corner cuts with randomly distributed anisotropy axes, that is, in a “sputtered” nanoring. These states are depicted in Figure4. In all these states, domain walls block the formation of a vortex state.Figure 4
Possible magnetic states for larger angles, simulated in a nanoring with square corner cuts and randomly distributed anisotropy axes: one 360° domain wall (a), one 360° domain wall (b), and two 360° domain walls (c).
(a) (b) (c)In Figure5, phase diagrams of the minor loops via onion states are shown. At first glance, both situations, square or diagonal corner cuts, look similar. Between 1° and approx. 17°, minor loops via onion states are possible for which the connection fields HConnect and the minor coercive fields HMinor are given. For small angles, the field distances between HCoerc and HConnect are relatively large, allowing for switching into the intermediate onion state by stopping the field sweep within a large field area to go back to zero magnetic field. This is helpful for technical applications in storage devices, and so on. Nevertheless, there is also a significant difference in the angular area around 30° visible where the coercive fields of the nanorings with square corner cuts show a maximum while those of the nanorings with diagonal corner cuts increase continuously.Figure 5
Phase diagrams of minor loops via onion states, simulated for nanorings with square corner cuts (a) and diagonal corner cuts (b). The fieldsHCoerc,HConnect, and HMinor are explained in Figure 2.
(a) (b)To evaluate the reason for this difference as well as the occurrence of other possible magnetic states, Figure6 depicts the complete phase diagrams for the nanorings with square corner cuts, separated with respect to the three anisotropy situations. For both epitaxial nanorings, only onion states are visible; additional steps in the hysteresis loop are correlated with instable modifications of the magnetization distribution in corners which are reversed by small field changes.Figure 6
Phase diagrams simulated for nanorings with square corner cuts, assuming epitaxial anisotropy orientation along 0° (a), 45° (c), and random anisotropy axes (b). The colors of the texts correspond to those in Figure5.
(a) (b) (c)In case of a random distribution of the anisotropy axes, that is, a sputtered sample, most of the smaller angles up to approx. 17° reverse magnetization in the aforementioned steps, that is, from positive saturated onion via first horseshoe, intermediate onion, and second horseshoe to negative saturated onion. Nevertheless, for some angles this process works without horseshoe states. In this special nanoring, additional domain wall states may occur for larger angles (cf. Figure4). While the state with two 360° domain walls is only assumed for 45°, for angles between 17° and 43° one of the states with one 360° domain wall may be taken. While this happens more often in some angles and less often in others, the influence of arbitrary anisotropy axes distribution can change this behavior at any time.It should be mentioned that the sputtered sample shows more deviations from a clear correlation between sample angle and coercive fields due to the arbitrary distribution of anisotropy axes. This effect results in small variations of the simulated values for repeated simulations.In Figure7, the phase diagrams of the nanorings with diagonal corner cuts are shown. Firstly it is visible that no domain wall states occur. On the other hand, in all three anisotropy geometries, the phase diagrams look similar, with the angular region below approx. 20° reversing magnetization via the above describe route, that is, from positive saturated onion via first horseshoe, intermediate onion, and second horseshoe to negative saturated onion, while there are no intermediate states available for higher angles.Figure 7
Phase diagrams simulated for nanorings with diagonal corner cuts, assuming epitaxial anisotropy orientation along 0° (a), 45° (c), and random anisotropy axes (b). The colors of the texts correspond to those in Figure5; dot colors are identical with those in Figure 6.
(a) (b) (c)In general, it can be stated that the nanoring with diagonal corner cuts shows a more reliable, less arbitrary spectrum of magnetization reversal mechanisms. Due to their statistic character, the domain wall states in the “sputtered” sample with square corner cuts are only of academic interest. From the technical point of view, those angular regions are best suited which(i)
avoid instabilities, for example, arising from symmetry axes, such as 0°, or from changes in the magnetization reversal processes, such as around 17°–20°;(ii)
are similar for patent shape and diagonal corner cuts;(iii)
are similar for sputtered and both epitaxial samples;(iv)
are similar for neighboring angles;(v)
have large differences betweenHCoerc and HConnect, since in this way they can simply be reached and are thus well reproducible;(vi)
have large differences betweenHCoerc and HMinor, since in this way they are robust against small field deviations due to crosstalk from neighboring nanorings.This means that a sputtered sample in an orientation around 5°–10° should be preferred in technological applications, such as quaternary magnetic storage devices.


## 4. Conclusions

To conclude, we have given an overview of different magnetization reversal processes and magnetic states occurring in square nanorings grown by sputtering or epitaxially from iron. Using micromagnetic simulations, we have shown the variety of magnetic states which can be reached in such nanostructures, depending on the exact shape, anisotropy orientation, and external magnetic field direction. While some processes exhibited a statistical nature and could not be repeated, an angular region around 5°–10° between external field and nanoring side has proven to reverse magnetization via a stable intermediate onion state which can be used for technological purposes, for example, in storage devices or MRAM applications.



---

*Source: 3149682-2017-10-16.xml*