# Efficient One-Pot Synthesis of TiO2/ZrO2/SiO2 Ternary Nanocomposites Using Prunus × Yedoensis Leaf Extract for Enhanced Photocatalytic Dye Degradation

Authors: Velu Manikandan; J. Saranya Packialakshmi; Bandna Bharti; Palaniyappan Jayanthi; Ranjithkumar Dhandapani; Palanivel Velmurugan; Duraisamy Elango; Ragul Paramasivam; Vinayagam Mohanavel; Asad Syed; Abdhallah M. Elgorban; Ali H. Bahkali; Saravanan Muthupandian
Journal: Oxidative Medicine and Cellular Longevity
 (2022)

---

## Abstract

A simple, efficient, and ecofriendly method was employed to synthesize TiO2/ZrO2/SiO2 ternary nanocomposites using Prunus × yedoensis leaf extract (PYLE) that shows improved photocatalytic and antibacterial properties. The characterization of the obtained nanocomposites was done by X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, field-emission scanning electron microscopy (FE-SEM), and energy-dispersive X-ray spectroscopic (EDS) analysis. The synthesized ternary nanocomposites with nanoscale pore diameters were investigated for the elimination of Reactive Red 120 (RR120) dye. The obtained results showed about 96.2% removal of RR120 dye from aqueous solution under sunlight irradiation. Furthermore, it shows promising antibacterial activity against Staphylococcus aureus and Escherichia coli. The improved photocatalytic and antibacterial activity of TiO2/ZrO2/SiO2 may bring unique insights into the production of ternary nanocomposites and their applications in the environment and biomedical field.


---

## Body

## 1. Introduction

The Reactive Red 120 is a cationic dye used in several industries such as paper, leather, cotton, pulp, and wool. This toxic aqueous solution causes various problems including human health issues such as abnormal heartbeat rate, shock, cyanosis, jaundice, tissue death, carcinogenesis, mutagenesis, teratogenesis, respiratory toxicity, kidney failure and malfunctioning, and damage to the major organs like the brain, lung, liver, and sexual organs and causes emphysema [1–3]. The effluents released from the dyeing units are highly toxic, and it is directly discharged into the water bodies, which severely impact the environment. Due to the effluent’s resistance to light, heat, chemicals, and water, these effluents at low-level concentrations do not readily degrade in the environment [4]. The estimated annual production of dye products is 10 million kilograms, out of which up to 2 million kilograms of reactive dyes enter the biosphere [5]. However, over a long period, different methods are employed for treating dyes from aquatic media [6], which include catalytic oxidation, sonocatalytic degradation, ozonation, adsorption [7], electrochemical oxidation [8], and coagulation/flocculation [9]. But these technologies are not suitable to meet the required water quality standards [10]. Recently, semiconductor photocatalysis drags the attention because of its advanced and green technique that provides the potential to degrade the dye in wastewater. It also stands for environmental benignancy, stability, and safety [11].The growing global research needs a fast and environment-friendly technology to remove wastewater pollutants. Recently, nanotechnology has helped researchers enable potential applications in environmental issues. Titanium dioxide (TiO2) nanoparticles have been used as a benchmark photocatalytic material due to their high stability, nontoxicity, low cost, and strong oxidizing agent [12–15]. They have been used in various environmental applications such as high photocatalytic efficiency, optical, dielectrics, and antimicrobial devices [16–18]. TiO2 has a unique series of reactive oxygen functional groups present on the surface, such as carboxylic acid, hydroxyl, and epoxide groups that are beneficial in preparing the TiO2 nanocomposites [19] such as titanium oxide-reduced graphene oxide (TiO2-rGO) [20], SiO2-TiO2/ZrO2 [21], and Zr-TiO2/SiO2 [22]. Overall, titanium reveals a more extensive phi-conjugation system in a two-dimensional planar structure, a higher surface area, and a higher electron conductivity, including reactive oxygen and a carboxyl group which is present in titanium dioxide as a unique functional group would support strengthening the metal and metal oxide particles [23]. Under UV light irradiation [24], TiO2/ZrO2/SiO2 photocatalyst had greater photocatalysis performance than the TiO2/SiO2 and TiO2/ZrO2 systems. Furthermore, TiO2 is a promising material for removing dye from wastewater because of its high electron mobility and flexibility [25].Several investigations are currently being conducted on the heterogeneous photocatalytic degradation of dye exposed to UV-A or visible light [26]. The oxidative technique has decolorized and mineralized the variety of azo dyes on a workbench scale using artificial illumination and solar energy [27]. Wang et al. successfully demonstrated the photocatalytic degradation of eight commercial dyes by using solar energy, including MeO, in the TiO2 mixture [28]. The plant-mediated synthesis of ternary nanocomposites is a safe, ecofriendly, rapid, and more stable approach due to the presence of numerous bioactive compounds such as alkaloids, flavonoids, terpenoids, tannins, saccharides, phenol, vitamins, amino acids, proteins, and various enzymes [29, 30]. Antibiotic resistance of microorganisms poses a serious problem. Thousands of people succumb to the harmful microorganisms and die due to hospital pathogens being resistant to the antibiotics. Hence, there is an ultimate need for novel antimicrobials, and the synthesized ternary nanocomposites exhibit a biocompatible structure which provides great convenience for medical applications. These phytochemicals present in the PYLE extract act as a reducing agent in the bioreduction of ions for the synthesis of TiO2/ZrO2/SiO2 nanocomposites. Controlled pore size distribution, density, compressive strength, and other unique characteristics are important properties of nanocomposites synthesized using the one-pot method. Moreover, the use of solar irradiation, instead of UV light, is another attractive point that fits today’s requests for more intense use of renewable energies. The present study deals with the photocatalytic degradation of RR120 dye obtained by the one-pot solar photoreduction (with the intensity of ~50000 1x) to avoid the high temperature and pressure required for the standard hydrothermal reaction. Additionally, the antibacterial activity of the green synthesized TiO2/ZrO2/SiO2 nanocomposites was also investigated.


## 2. Experimental Sections

### 2.1. Materials

Titanium tetraisopropoxide (C12H28O4Ti assay≥98%, Sigma), zirconium (IV) acetylacetonate (ZrC5H7O24>98%, Sigma), sodium silicate (Na2SiO3·9H2O), and methanol (Daejung Chemicals Reagents, South Korea) were used as precursors to prepare oxide composites. Reactive Red 120 was supplied by SD Fine Chemicals, Mumbai, India. Stock solutions of 1000 mg/L of the dye were prepared, and further concentrations were obtained by diluting the stock solution. Mueller Hinton Agar (MHA) was purchased from MB cell, South Korea. All solutions were prepared using Milli Q water with of conductivity 18 μΩ/m.


### 2.2. Biological Materials

Staphylococcus aureus and Escherichia coli were collected from the Korean agriculture culture collection (KACC) in Suwon, South Korea. The collected organisms were subcultured in nutrient agar and incubated at 37°C for 24 hours; after incubation, the plates were stored at 4°C until the experiment.


### 2.3.Prunus × Yedoensis Leaf Extracts (PYLE) Preparation

50 grams ofPrunus× yedoensis leaves was collected from the plants in and around the Chonbuk National University, Iksan campus, South Korea. The collected leaves were washed in distilled water to remove the impurities, and then these leaves were sheared into small pieces. After shearing, it was boiled with 200 mL sterile Milli Q water for 30 min in a heating mantle to obtain the decoction. The obtained decoction was subjected to filtration using a Whatman No.42 filter paper. After filtration, it was stored at 4°C until further process.


### 2.4. One-Pot Green Synthesis and Calcination Treatment of TiO2-Coated ZrO2/SiO2 Nanocomposites

100 mL of 0.1 M titanium tetraisopropoxide (C12H28O4Ti assay≥98%, Sigma) solution was added to 300 mL of Prunus × yedoensis leaf extract mixture was vigorously stirred for one hour and ultrasonicated for 15-30 min. Followed by adding 100 mL of 0.1 M Zr(C5H7O2)4 and 100 mL of 0.1 M Na2SiO3·9H2O to the sonicated reaction mixture using a peristaltic pump (flow rate-0.5 mL/hour) at 80°C. Then the reaction mixture was subjected to centrifugation at 12000 rpm, the pellets were collected, and then the pellets were washed subsequently with distilled water and methanol to remove organic material present in the final product. The obtained product was subjected to calcination at 800°C for two hours in a muffle furnace. The final product obtained was designated as TiO2/ZrO2/SiO2 ternary nanocomposites and subjected to characterization and investigation of photocatalytic and antibacterial activities.


### 2.5. Characterization of TiO2/ZrO2/SiO2 Ternary Nanocomposites

The green synthesized TiO2/ZrO2/SiO2 ternary nanocomposites were analyzed by FE-SEM-EDS (SU-8240, Hitachi, Japan) to observe the surface morphology and appearance of the nanocomposite. EDS was used to confirm the element present in the nanocomposite. XRD patterns were obtained using a Rigaku X-ray diffractometer to find out the crystalline nature of the nanocomposite. The scanning was completed in the region of 2θ from 10°-80° at 0.041/min at a constant time of 2S. The functional groups in the prepared nanocomposite were analyzed using a Perkin-Elmer FTIR spectrophotometer (USA) with a range of 4000-400 cm-1. Raman spectroscopy was carried out by XploRA Raman microscope equipped with laser light of wavelength 532 nm. The UV-visible spectroscopy was recorded on UV-1800, Shimadzu, Kyoto, Japan, with the variable wavelength from 300 to 800 nm.


### 2.6. Photocatalytic Activity of TiO2/ZrO2/SiO2 Ternary Nanocomposites under Various Light Sources

The photocatalytic activity of TiO2/ZrO2/SiO2 ternary nanocomposites was conducted by the method proposed by Borthakur et al. [31] with modifications. Briefly, the reaction mixture was prepared by adding 10 mg of synthesized TiO2/ZrO2/SiO2 ternary nanocomposites in 100 mL of RR120 aqueous solution with an initial concentration of 10 ppm, and the suspension was stirred in the dark for 30 min before irradiated in the sunlight to establish the absorption-desorption equilibrium between the photocatalyst and RR120 dye. The sunlight irradiation was carried out between 11:00 a.m. and 2:00 p.m. on consecutive days (summer season) in June and July 2020 (GPS coordination: 35.84682° N, 127.12935° E). The photocatalytic activity of TiO2/ZrO2/SiO2 ternary nanocomposites was estimated by measuring the degradation of RR120 in an aqueous solution under sunlight irradiation using a UV-Vis spectrophotometer. A sample solution of RR120 was withdrawn within the fixed time interval and centrifuged at 12,000 rpm for 20 min during the photocatalytic reaction. After centrifugation, the supernatant was used to measure the amount of RR120 at λmax (515 nm) [26] using a UV-visible spectrophotometer. The following equation determined the percentage of RR120 degraded by the prepared nanocomposite from the photocatalytic activity [32].
(1)Percentageofdegradation=C0−CtC0×100.Here,C0 is the initial concentration of the aqueous RR120 solution (mg/L), and Ct is the concentration of the aqueous solution after irradiation (mg/L). The reaction mixture was also subjected to different pH (4–12), different initial concentrations (C0) of RR120 (10 mg/L to 30 mg/L), and three different dosages of TiO2/ZrO2/SiO2 (from 20 to 60 mg/L). The kinetics study of RR120 was carried out to find the reaction rate constant of as-synthesized TiO2/ZrO2/SiO2 nanocomposites. The degradation of RR120 can be described by the pseudo-first-order equation [33].
(2)lnC0Ct=−kappt,where C0 is the initial concentration of RR120 aqueous solution, Ct is the final concentration of RR120 aqueous solution, kapp is the pseudo-first-order rate constant (min-1), and t is time (min). kapp values were enumerated from the slope lnCt/C0 at a different time plot observed for the sample solution without a catalyst, with the catalyst in a dark chamber, TiO2/SiO2, TiO2/ZrO2, and TiO2/ZrO2/SiO2 photocatalysts. The k-rate constant was derived through the kinetic value.


### 2.7. Antibacterial Activity

The TiO2/ZrO2/SiO2 ternary nanocomposite antibacterial activity was evaluated against the Staphylococcus aureus and Escherichia coli by the well diffusion technique. The bacterial suspension was swabbed on the Muller Hinton agar plate for antibacterial activity, and the different concentrations of nanocomposites (50, 75, and 100 μg/mL) were loaded in the respective well on the agar plates. Then the plates were incubated at 37°C for 24 h. The antibacterial activity of TiO2/ZrO2/SiO2 ternary nanocomposites was identified by the clear zone around the well, which indicates the inhibition of bacteria by the composite.


## 2.1. Materials

Titanium tetraisopropoxide (C12H28O4Ti assay≥98%, Sigma), zirconium (IV) acetylacetonate (ZrC5H7O24>98%, Sigma), sodium silicate (Na2SiO3·9H2O), and methanol (Daejung Chemicals Reagents, South Korea) were used as precursors to prepare oxide composites. Reactive Red 120 was supplied by SD Fine Chemicals, Mumbai, India. Stock solutions of 1000 mg/L of the dye were prepared, and further concentrations were obtained by diluting the stock solution. Mueller Hinton Agar (MHA) was purchased from MB cell, South Korea. All solutions were prepared using Milli Q water with of conductivity 18 μΩ/m.


## 2.2. Biological Materials

Staphylococcus aureus and Escherichia coli were collected from the Korean agriculture culture collection (KACC) in Suwon, South Korea. The collected organisms were subcultured in nutrient agar and incubated at 37°C for 24 hours; after incubation, the plates were stored at 4°C until the experiment.


## 2.3.Prunus × Yedoensis Leaf Extracts (PYLE) Preparation

50 grams ofPrunus× yedoensis leaves was collected from the plants in and around the Chonbuk National University, Iksan campus, South Korea. The collected leaves were washed in distilled water to remove the impurities, and then these leaves were sheared into small pieces. After shearing, it was boiled with 200 mL sterile Milli Q water for 30 min in a heating mantle to obtain the decoction. The obtained decoction was subjected to filtration using a Whatman No.42 filter paper. After filtration, it was stored at 4°C until further process.


## 2.4. One-Pot Green Synthesis and Calcination Treatment of TiO2-Coated ZrO2/SiO2 Nanocomposites

100 mL of 0.1 M titanium tetraisopropoxide (C12H28O4Ti assay≥98%, Sigma) solution was added to 300 mL of Prunus × yedoensis leaf extract mixture was vigorously stirred for one hour and ultrasonicated for 15-30 min. Followed by adding 100 mL of 0.1 M Zr(C5H7O2)4 and 100 mL of 0.1 M Na2SiO3·9H2O to the sonicated reaction mixture using a peristaltic pump (flow rate-0.5 mL/hour) at 80°C. Then the reaction mixture was subjected to centrifugation at 12000 rpm, the pellets were collected, and then the pellets were washed subsequently with distilled water and methanol to remove organic material present in the final product. The obtained product was subjected to calcination at 800°C for two hours in a muffle furnace. The final product obtained was designated as TiO2/ZrO2/SiO2 ternary nanocomposites and subjected to characterization and investigation of photocatalytic and antibacterial activities.


## 2.5. Characterization of TiO2/ZrO2/SiO2 Ternary Nanocomposites

The green synthesized TiO2/ZrO2/SiO2 ternary nanocomposites were analyzed by FE-SEM-EDS (SU-8240, Hitachi, Japan) to observe the surface morphology and appearance of the nanocomposite. EDS was used to confirm the element present in the nanocomposite. XRD patterns were obtained using a Rigaku X-ray diffractometer to find out the crystalline nature of the nanocomposite. The scanning was completed in the region of 2θ from 10°-80° at 0.041/min at a constant time of 2S. The functional groups in the prepared nanocomposite were analyzed using a Perkin-Elmer FTIR spectrophotometer (USA) with a range of 4000-400 cm-1. Raman spectroscopy was carried out by XploRA Raman microscope equipped with laser light of wavelength 532 nm. The UV-visible spectroscopy was recorded on UV-1800, Shimadzu, Kyoto, Japan, with the variable wavelength from 300 to 800 nm.


## 2.6. Photocatalytic Activity of TiO2/ZrO2/SiO2 Ternary Nanocomposites under Various Light Sources

The photocatalytic activity of TiO2/ZrO2/SiO2 ternary nanocomposites was conducted by the method proposed by Borthakur et al. [31] with modifications. Briefly, the reaction mixture was prepared by adding 10 mg of synthesized TiO2/ZrO2/SiO2 ternary nanocomposites in 100 mL of RR120 aqueous solution with an initial concentration of 10 ppm, and the suspension was stirred in the dark for 30 min before irradiated in the sunlight to establish the absorption-desorption equilibrium between the photocatalyst and RR120 dye. The sunlight irradiation was carried out between 11:00 a.m. and 2:00 p.m. on consecutive days (summer season) in June and July 2020 (GPS coordination: 35.84682° N, 127.12935° E). The photocatalytic activity of TiO2/ZrO2/SiO2 ternary nanocomposites was estimated by measuring the degradation of RR120 in an aqueous solution under sunlight irradiation using a UV-Vis spectrophotometer. A sample solution of RR120 was withdrawn within the fixed time interval and centrifuged at 12,000 rpm for 20 min during the photocatalytic reaction. After centrifugation, the supernatant was used to measure the amount of RR120 at λmax (515 nm) [26] using a UV-visible spectrophotometer. The following equation determined the percentage of RR120 degraded by the prepared nanocomposite from the photocatalytic activity [32].
(1)Percentageofdegradation=C0−CtC0×100.Here,C0 is the initial concentration of the aqueous RR120 solution (mg/L), and Ct is the concentration of the aqueous solution after irradiation (mg/L). The reaction mixture was also subjected to different pH (4–12), different initial concentrations (C0) of RR120 (10 mg/L to 30 mg/L), and three different dosages of TiO2/ZrO2/SiO2 (from 20 to 60 mg/L). The kinetics study of RR120 was carried out to find the reaction rate constant of as-synthesized TiO2/ZrO2/SiO2 nanocomposites. The degradation of RR120 can be described by the pseudo-first-order equation [33].
(2)lnC0Ct=−kappt,where C0 is the initial concentration of RR120 aqueous solution, Ct is the final concentration of RR120 aqueous solution, kapp is the pseudo-first-order rate constant (min-1), and t is time (min). kapp values were enumerated from the slope lnCt/C0 at a different time plot observed for the sample solution without a catalyst, with the catalyst in a dark chamber, TiO2/SiO2, TiO2/ZrO2, and TiO2/ZrO2/SiO2 photocatalysts. The k-rate constant was derived through the kinetic value.


## 2.7. Antibacterial Activity

The TiO2/ZrO2/SiO2 ternary nanocomposite antibacterial activity was evaluated against the Staphylococcus aureus and Escherichia coli by the well diffusion technique. The bacterial suspension was swabbed on the Muller Hinton agar plate for antibacterial activity, and the different concentrations of nanocomposites (50, 75, and 100 μg/mL) were loaded in the respective well on the agar plates. Then the plates were incubated at 37°C for 24 h. The antibacterial activity of TiO2/ZrO2/SiO2 ternary nanocomposites was identified by the clear zone around the well, which indicates the inhibition of bacteria by the composite.


## 3. Results and Discussion

This study prepared the green synthesis of TiO2/ZrO2/SiO2 ternary nanocomposites using PYLE.


### 3.1. X-Ray Diffraction Analysis

Figure1(a) illustrates the XRD pattern of TiO2/ZrO2/SiO2 nanocomposites. The diffraction peaks at 25°, 36°, 48°, 54°, 55.5°, 69°, 70°, and 75° were assigned to the corresponding planes (101), (103), (200), (210), (211), (116), (220), and (215), respectively, which indicate the presence of anatase TiO2. Also, it can be evidenced that the moderate low-intensity peaks at 27°, 35.5°, 42°, 56°, and 63° correspond to the planes of (110), (101), (111), (220), and (002), revealing the presence of rutile TiO2. Similar interpretations were made by Chellappa and Vijayalakshmi [34]. The prepared TiO2/ZrO2/SiO2 ternary nanocomposite might exhibit a mixed phase of anatase and rutile TiO2. A low intense peak at 30° indexed to (111) resembles the zirconia phase, which might increase the mechanical strength of the ternary nanocomposites. The diffraction peaks at 38°, 45°, and 65° correspond to (112), (211), and (023), respectively; these planes confirmed the presence of monoclinic ZrO2. This was in good agreement with the study conducted by [35]. The heterojunction of TiO2-coated ZrO2/SiO2 inhibits the conversion of TiO2 anatase to rutile at 800°C. In ZrO2/SiO2, the low intense peak at 20° and 30° reflects the combination pattern of ZrO2/SiO2 into TiO2 coated nanocomposite [36, 37]. In this study, all assigned diffraction peaks in TiO2-coated ZrO2/SiO2 revealed an enhanced photocatalytic activity compared with the pure TiO2 because of the anatase crystalline phase. From the XRD results, it can be assumed that the coated TiO2 nanoparticles might be entered into the channels of the ZrO2/SiO2 binary particle network.Figure 1
(a) XRD spectra, (b) FTIR spectrum, and (c) Raman spectra of TiO2/ZrO2/SiO2 nanocomposite.
(a)(b)(c)


### 3.2. FTIR Analysis

The FTIR spectrum of the nanocomposites is shown in Figure1(b). Several functional groups were present in the prepared nanocomposite within 4000-400 cm-1. The prominent peak at 3384 cm-1 corresponds to the O-H stretching group present on the composite surface. The bank at 1627 cm-1 corresponds to C=C stretching vibrations in aromatic functional groups [38]. It is well known that the surface hydroxyl group plays a significant role in photocatalysis by capturing the holes and generating reactive hydroxyl radicals with high oxidation capacity [36]. The band around 1122 cm-1 is attributed to C-O stretching vibrations from the alcohol group, and the band at 669 cm-1 is assigned to the C-Cl stretching vibrations in the alkyl halide group. However, introducing titanium atoms to SiO2 to form the tetrahedral structure gives a complete structure of adsorbent [39]. The small peak at 515 cm-1 corresponds to the alkyl group in the Ti-O stretching, confirming the metal-oxygen bonding to nanocomposite [40].


### 3.3. Raman Analysis

Raman spectra of TiO2/ZrO2/SiO2 ternary nanocomposites are shown in Figure 1(c). The sharp peaks at 140, 394, 510, and 635 cm-1 were assigned to the anatase phase of TiO2. No characteristic peaks of silica were observed in the spectra. It is well known that zirconia has three polymorphs, namely monoclinic, tetragonal, and cubic; however, no Raman bands were observed for all these polymorphs [21]. Therefore, the Raman results indicate that silica and zirconium oxide are amorphous in the prepared TiO2/ZrO2/SiO2 ternary nanocomposites and are probably present as dispersed surface species.


### 3.4. FE-SEM-EDS

The surface morphology of TiO2/ZrO2/SiO2 nanocomposite was observed under field-emission scanning electron microscopy (FE-SEM). TiO2/ZrO2/SiO2 ternary nanocomposites were almost spherical in shape [41]. The uniform distribution of particles on the nanocomposite surface has been observed. The formation of aggregation in the nanocomposite might be due to the presence of excess H+ ions of H2O molecules on the surface of the nanocomposite [42]. The particle size of the prepared nanocomposite was in the range of 2-20 μm, as shown in Figures 2(a)–2(c), where the prepared particles appeared to have a moderately rough surface [43]. Also, the surface roughness of nanocomposite was slightly increased due to the presence of TiO2 on the surface [44]. The elemental composition of TiO2/ZrO2/SiO2 ternary nanocomposites was determined by energy-dispersive X-ray spectroscopy (EDS), as shown in Figure 2(d). It can be seen that the presence of different elements such as titanium (Ti), zirconium (Zr), and silica (Si) confirmed the configuration of the green synthesized TiO2/ZrO2/SiO2 ternary nanocomposites. Biofabrication of nanocomposites was reduced and capped by polyphenols, which was actively confirmed by EDS [42].Figure 2
(a–c) FE-SEM images of TiO2/ZrO2/SiO2 ternary nanocomposites and (d) EDS spectra of TiO2/ZrO2/SiO2 ternary nanocomposites.
(a)(b)(c)(d)


### 3.5. Elemental Mapping-EDS Analysis

Elemental mapping results of TiO2/ZrO2/SiO2 nanocomposites are shown in Figures 3(a), 3(c), 3(e), and 3(g). The EDS results assessed the homogeneity of the nanocomposites. The distribution of Si, Zr, and Ti in the TiO2/ZrO2/SiO2 nanocomposites is observed in Figures 3(b), 3(d), 3(f), and 3(h). Several earlier studies well coincided with the evenly distributed titanium over the SiO2 spheres, which evidently confirms the active role of titanium in the nanocomposites [45, 46]. EDS measurements confirmed the presence of Ti, Zr, and Si. Furthermore, all other elements like Zr, Si, and O are uniformly dispersed without agglomeration, and similar results were obtained from the study conducted by Choi and Choy [47].Figure 3
(a, c, e, g) Element mapping analysis of TiO2/ZrO2/SiO2 ternary nanocomposites and (b, d, f, h) EDS spectra.
(a)(b)(c)(d)(e)(f)(g)(h)


### 3.6. Photocatalytic Degradation of RR120 in the Presence of TiO2/ZrO2/SiO2 Ternary Nanocomposites

The prepared TiO2/ZrO2, TiO2/SiO2, and TiO2/ZrO2/SiO2 nanocomposites were tested for their photocatalytic activity. The photocatalytic degradation of the RR120 dye experiment was standardized with the pH, catalyst dose, concentration of RR120 dye, and time interval under the sunlight irradiation. We have identified that at pH of 5, a catalyst dose of 10 mg/L, the concentration of RR120 dyes with 30 mg/L, and initially at 15 minutes, steadily increasing the steady time of 75 minutes showed better photocatalytic activity. The RR120 dye absorption peak at 515 nm showed that the amount of dye is drastically decreased without shifting the peak position to the baseline, indicating the complete decomposition in the aqueous solution. Moreover, these bioreduced TiO2/ZrO2/SiO2 nanocomposites toward RR120 exhibited a promising photocatalytic efficiency with a 96.2% removal rate within 75 min. The absorbance spectra of the treated dye in the aqueous solution with the prepared composites were measured using a UV-visible spectrophotometer (Figures 4(a)–4(c)). The variations in the relative RR120 dye concentration (Ct/C0) are presented in Figure 4(d), which shows the comparison of the photodegradation rate of RR120 dye in the presence of TiO2/ZrO2, TiO2/SiO2, and TiO2/ZrO2/SiO2 nanocomposites, respectively. The variation in RR120 dye removal is influenced by sunlight sources irradiation time [48].Figure 4
UV-Vis spectra of RR120 removal at different time intervals: (a) TiO2/ZrO2, (b) TiO2/SiO2, and (c) TiO2/ZrO2/SiO2 ternary nanocomposites and (d) RR120 removal rate at different photocatalytic systems.
(a)(b)(c)(d)The obtained results clearly show that the RR120 removal efficiency of aqueous solutions without catalyst, with the catalyst in the dark, TiO2/ZrO2, and TiO2/SiO2 were less than that of the heterogeneous TiO2/ZrO2/SiO2 ternary nanocomposites. The plant-based nanocomposite preparation is the most attractive approach for mass production at a minimal price that is safe for the ecosystem and human life. This nanocomposite might be an excellent potential photocatalyst for degrading pollutants utilizing sunlight [49].The fact that the nanocomposites were synthesized by the sol-gel method could describe the photocatalytic improvement under natural sunlight with TiO2/ZrO2/SiO2 ternary nanocomposites. In this case, nanocomposites with a large specific area would include more active surface sites for adsorbing water molecules and forming aggressive •OH and HOO• radicals by capturing the photogenerated holes [50]. The photocatalytic interactions are fueled by these active free radicals, resulting in the degradation of various pollutants from the aqueous medium [51]. However, the larger surface area still enables the dye molecule diminishment on the TiO2/ZrO2/SiO2 photocatalyst surface. According to Abroushan et al. [52], the phosphate molecules are adsorbed on the surface of nanocomposite and generate electrons when exposed to sunlight [52]. In the present study, these electrons are attracted by the surface adsorbed O2 molecules, resulting in the formation of O2•– and HO• radicals, which have a higher chance of contacting RR120 dyes due to a quicker reaction speed, and the RR120 dye may be mineralized over time by superoxide radical ions [53]. As an outcome, the relatively smaller crystalline size of TiO2/ZrO2/SiO2 ternary nanocomposite is advantageous for reducing O2 and oxidation of H2O molecules by capturing the electron, and the hole pair enhances the photocatalytic performance when exposed to sunlight [54]. According to the results, TiO2/ZrO2/SiO2 ternary nanocomposites as active photocatalyst have an excellent photocatalytic potential to discharge the RR120 dye in the aqueous solution. The results obtained were compared with the other green synthesized nanocomposites, as shown in Table 1. From the results, the TiO2/ZrO2/SiO2 photocatalyst has a unique adsorption capability for RR120 in an aqueous solution. This enhancement could be attributed to a synergistic effect on a unique adsorption property and effective electron detachment at the photocatalyst functionality of nanocomposites. Moreover, no photocatalyst based on TiO2/ZrO2/SiO2 ternary nanocomposites for the breakdown of RR120 dye contaminant has been reported until now.Table 1
Comparison of photocatalytic activity of TiO2/ZrO2/SiO2 nanocomposites with similar kinds of studies.
S. NoCatalyst% removalCatalyst (mg/L)Irradiation timeReferences1Fe2O3/Ag nanocomposites88.2%60140 min[64] Saranya et al. [64]2TiO2 nanocomposites94%100150 min[65] Khade et al. [65]3TiO2–SiO2–Ag nanocomposites80%504 h[66] Liu et al. [66]4Catechin@ZIF-L nanocomposites92%50 mg150 min[67] Raju et al. [67]5TiO2/ZrO2/SiO2 nanocomposites96.2%10 mg75 minOur study


### 3.7. Kinetic Study of the TiO2/ZrO2/SiO2 Ternary Nanocomposite Catalysts

Figure5(a) illustrates the reaction kinetics of photodegradation of RR120 dye by various nanocomposites. The k value for a sample with catalyst in a dark chamber, without a catalyst, TiO2/ZrO2, TiO2/SiO2, and TiO2/ZrO2/SiO2 ternary nanocomposite was estimated to be R2=0.7902,0.9503,0.9833.0.9859,and0.9824, respectively. Each of the plot lines shows a linear correlation with a high correlation coefficient of 0.9824, indicating the degradation of RR120 dye by green synthesized ternary nanocomposite using sunlight follows pseudo-first-order reaction kinetics. The higher k value proves that the TiO2/ZrO2/SiO2 ternary nanocomposite has an excellent photocatalytic activity. This statement was in agreement with the previous report conducted by Zhang et al. [55].Figure 5
(a) Pseudo-first-order reaction kinetics of photodegradation of RR120 over various samples and (b) reusability of the prepared TiO2/ZrO2/SiO2 ternary nanocomposites.
(a)(b)


### 3.8. Reusability Study

For assessing the reusability of TiO2/ZrO2/SiO2 ternary nanocomposites, photodegradation was checked by repeating the four cycles as shown in Figure 5(b). The photocatalytic experiments (300 min) were repeated in four cycles, with the same nanocomposites retained after each cycle [56]. At the end of each photocatalytic experiment, samples were recovered and washed with deionized water and then used to analyze their stability. The amount of photocatalytic reduction by the nanocomposites showed the best performance, and similar interpretations were observed in the study conducted by Hinojosa–Reyes et al. [57]). These results depicted the photocatalytic activity of the biogenic fabricated TiO2/ZrO2/SiO2 ternary nanocomposites with renewed management. It can be considered that the distinction in the degradation efficiency might be due to the various surface features, crystalline nature, and the optical properties of nanocomposites [58]. After recycling four times, there were no significant variations in the degradation efficiency. This clearly states that the synthesized TiO2/ZrO2/SiO2 ternary nanocomposites are reusable enough for industrial and environmental applications.


### 3.9. Antibacterial Activity

The bactericidal activity of TiO2/ZrO2/SiO2 against S. aureus and E. coli is displayed in Figure 6. The antibacterial activity was carried out by a well diffusion method, and a zone of inhibition was observed for different concentrations (50, 75, and 100 μg/mL) of a nanocomposite (20 mg in 0.5 mL) [59]. While increasing the concentration of the nanocomposites, the zone of inhibition in the well plate also increases. The highest inhibition rate was observed in S. aureus at the concentration of 100 μg/mL, compared to E. coli (Table 2). The enhanced antibacterial activity of TiO2/ZrO2/SiO2 ternary nanocomposites has been familiar to the generation of reactive oxygen species (ROS), which could disrupt the DNA, proteins, and lipids, and leads to the death of the bacteria [60]. Nanoparticles can easily penetrate through the cell membrane; consequently, accumulation inside bacterial cells damages membrane integrity and ultimately destroys the bacteria [61]. While the nanocomposite was in contact with the cell membrane of the bacteria, Ti2+ was released and bound to the outer membrane; because the bacterial cell membrane was negatively charged [60]. Therefore, Ti2+ positively charged might mutually attract negatively charged cell membrane and cause damage to the cell membrane, which undoubtedly leads to bacterial death [62].Figure 6
Variable numbers of colonies in agar plates (a)Staphylococcus aureus and (b) Escherichia coli exposed to different concentrations of TiO2/ZrO2/SiO2 nanocomposites.
(a)(b)Table 2
Antibacterial activity (zone of inhibition) of TiO2/ZrO2/SiO2 nanocomposites against Gram-positive and Gram-negative bacteria.
Zone of inhibition (ZOI) in mmS. NoSamplesBacterial strainsS. aureusE. coli50μg75μg100μg50μg75μg100μg1.PYLE——————2.TiO2/ZrO2—1±0.62±0.2—1±0.82±0.43.TiO2/SiO2—1±0.21±0.9—1±0.52±0.34.TiO2/ZrO2/SiO2 nanocomposites8 ± 0.611±0.912±0.96±0.48±0.310±0.65.Chloramphenicol10 ± 0.712±0.715±0.312±0.415±0.316±0.6


### 3.10. Photocatalytic Mechanism

Figure7 illustrates the proposed mechanism of RR120 degradation by TiO2/ZrO2/SiO2 nanocomposites. The photocatalytic process consists of the photogenerated electron and hole and their transfer to the surface of the nanocomposites and creates active oxygen species. Under the irradiation of artificial sunlight, each oxide’s conduction and valence band contain the photogenerated hole and electron. According to the diagram, the position of the valence band of TiO2 is higher than that of ZrO2 and SiO2. Therefore, the photogenerated hole transfer can take place from the valance band of TiO2 to the valance band of ZrO2 and SiO2 [63]. However, in the case of photogenerated electrons, transfer takes place from the conduction band of SiO2 to ZrO2 and then to TiO2. Such photogeneration effectively reduces the recombination of electron-hole pairs. Hence, during the photocatalytic reaction, the electron can be captured by O2 to create a superoxide radical anion [55]. The hole can react with the hydroxyl group to generate hydroxyl radicals responsible for the degradation of RR120. It can be clear from the diagram that the hole and electron are effectively separated from each other at the surface of the TiO2/ZrO2/SiO2 nanocomposite.Figure 7
The proposed mechanism of RR120 degradation by TiO2/ZrO2/SiO2 ternary nanocomposites.


## 3.1. X-Ray Diffraction Analysis

Figure1(a) illustrates the XRD pattern of TiO2/ZrO2/SiO2 nanocomposites. The diffraction peaks at 25°, 36°, 48°, 54°, 55.5°, 69°, 70°, and 75° were assigned to the corresponding planes (101), (103), (200), (210), (211), (116), (220), and (215), respectively, which indicate the presence of anatase TiO2. Also, it can be evidenced that the moderate low-intensity peaks at 27°, 35.5°, 42°, 56°, and 63° correspond to the planes of (110), (101), (111), (220), and (002), revealing the presence of rutile TiO2. Similar interpretations were made by Chellappa and Vijayalakshmi [34]. The prepared TiO2/ZrO2/SiO2 ternary nanocomposite might exhibit a mixed phase of anatase and rutile TiO2. A low intense peak at 30° indexed to (111) resembles the zirconia phase, which might increase the mechanical strength of the ternary nanocomposites. The diffraction peaks at 38°, 45°, and 65° correspond to (112), (211), and (023), respectively; these planes confirmed the presence of monoclinic ZrO2. This was in good agreement with the study conducted by [35]. The heterojunction of TiO2-coated ZrO2/SiO2 inhibits the conversion of TiO2 anatase to rutile at 800°C. In ZrO2/SiO2, the low intense peak at 20° and 30° reflects the combination pattern of ZrO2/SiO2 into TiO2 coated nanocomposite [36, 37]. In this study, all assigned diffraction peaks in TiO2-coated ZrO2/SiO2 revealed an enhanced photocatalytic activity compared with the pure TiO2 because of the anatase crystalline phase. From the XRD results, it can be assumed that the coated TiO2 nanoparticles might be entered into the channels of the ZrO2/SiO2 binary particle network.Figure 1
(a) XRD spectra, (b) FTIR spectrum, and (c) Raman spectra of TiO2/ZrO2/SiO2 nanocomposite.
(a)(b)(c)


## 3.2. FTIR Analysis

The FTIR spectrum of the nanocomposites is shown in Figure1(b). Several functional groups were present in the prepared nanocomposite within 4000-400 cm-1. The prominent peak at 3384 cm-1 corresponds to the O-H stretching group present on the composite surface. The bank at 1627 cm-1 corresponds to C=C stretching vibrations in aromatic functional groups [38]. It is well known that the surface hydroxyl group plays a significant role in photocatalysis by capturing the holes and generating reactive hydroxyl radicals with high oxidation capacity [36]. The band around 1122 cm-1 is attributed to C-O stretching vibrations from the alcohol group, and the band at 669 cm-1 is assigned to the C-Cl stretching vibrations in the alkyl halide group. However, introducing titanium atoms to SiO2 to form the tetrahedral structure gives a complete structure of adsorbent [39]. The small peak at 515 cm-1 corresponds to the alkyl group in the Ti-O stretching, confirming the metal-oxygen bonding to nanocomposite [40].


## 3.3. Raman Analysis

Raman spectra of TiO2/ZrO2/SiO2 ternary nanocomposites are shown in Figure 1(c). The sharp peaks at 140, 394, 510, and 635 cm-1 were assigned to the anatase phase of TiO2. No characteristic peaks of silica were observed in the spectra. It is well known that zirconia has three polymorphs, namely monoclinic, tetragonal, and cubic; however, no Raman bands were observed for all these polymorphs [21]. Therefore, the Raman results indicate that silica and zirconium oxide are amorphous in the prepared TiO2/ZrO2/SiO2 ternary nanocomposites and are probably present as dispersed surface species.


## 3.4. FE-SEM-EDS

The surface morphology of TiO2/ZrO2/SiO2 nanocomposite was observed under field-emission scanning electron microscopy (FE-SEM). TiO2/ZrO2/SiO2 ternary nanocomposites were almost spherical in shape [41]. The uniform distribution of particles on the nanocomposite surface has been observed. The formation of aggregation in the nanocomposite might be due to the presence of excess H+ ions of H2O molecules on the surface of the nanocomposite [42]. The particle size of the prepared nanocomposite was in the range of 2-20 μm, as shown in Figures 2(a)–2(c), where the prepared particles appeared to have a moderately rough surface [43]. Also, the surface roughness of nanocomposite was slightly increased due to the presence of TiO2 on the surface [44]. The elemental composition of TiO2/ZrO2/SiO2 ternary nanocomposites was determined by energy-dispersive X-ray spectroscopy (EDS), as shown in Figure 2(d). It can be seen that the presence of different elements such as titanium (Ti), zirconium (Zr), and silica (Si) confirmed the configuration of the green synthesized TiO2/ZrO2/SiO2 ternary nanocomposites. Biofabrication of nanocomposites was reduced and capped by polyphenols, which was actively confirmed by EDS [42].Figure 2
(a–c) FE-SEM images of TiO2/ZrO2/SiO2 ternary nanocomposites and (d) EDS spectra of TiO2/ZrO2/SiO2 ternary nanocomposites.
(a)(b)(c)(d)


## 3.5. Elemental Mapping-EDS Analysis

Elemental mapping results of TiO2/ZrO2/SiO2 nanocomposites are shown in Figures 3(a), 3(c), 3(e), and 3(g). The EDS results assessed the homogeneity of the nanocomposites. The distribution of Si, Zr, and Ti in the TiO2/ZrO2/SiO2 nanocomposites is observed in Figures 3(b), 3(d), 3(f), and 3(h). Several earlier studies well coincided with the evenly distributed titanium over the SiO2 spheres, which evidently confirms the active role of titanium in the nanocomposites [45, 46]. EDS measurements confirmed the presence of Ti, Zr, and Si. Furthermore, all other elements like Zr, Si, and O are uniformly dispersed without agglomeration, and similar results were obtained from the study conducted by Choi and Choy [47].Figure 3
(a, c, e, g) Element mapping analysis of TiO2/ZrO2/SiO2 ternary nanocomposites and (b, d, f, h) EDS spectra.
(a)(b)(c)(d)(e)(f)(g)(h)


## 3.6. Photocatalytic Degradation of RR120 in the Presence of TiO2/ZrO2/SiO2 Ternary Nanocomposites

The prepared TiO2/ZrO2, TiO2/SiO2, and TiO2/ZrO2/SiO2 nanocomposites were tested for their photocatalytic activity. The photocatalytic degradation of the RR120 dye experiment was standardized with the pH, catalyst dose, concentration of RR120 dye, and time interval under the sunlight irradiation. We have identified that at pH of 5, a catalyst dose of 10 mg/L, the concentration of RR120 dyes with 30 mg/L, and initially at 15 minutes, steadily increasing the steady time of 75 minutes showed better photocatalytic activity. The RR120 dye absorption peak at 515 nm showed that the amount of dye is drastically decreased without shifting the peak position to the baseline, indicating the complete decomposition in the aqueous solution. Moreover, these bioreduced TiO2/ZrO2/SiO2 nanocomposites toward RR120 exhibited a promising photocatalytic efficiency with a 96.2% removal rate within 75 min. The absorbance spectra of the treated dye in the aqueous solution with the prepared composites were measured using a UV-visible spectrophotometer (Figures 4(a)–4(c)). The variations in the relative RR120 dye concentration (Ct/C0) are presented in Figure 4(d), which shows the comparison of the photodegradation rate of RR120 dye in the presence of TiO2/ZrO2, TiO2/SiO2, and TiO2/ZrO2/SiO2 nanocomposites, respectively. The variation in RR120 dye removal is influenced by sunlight sources irradiation time [48].Figure 4
UV-Vis spectra of RR120 removal at different time intervals: (a) TiO2/ZrO2, (b) TiO2/SiO2, and (c) TiO2/ZrO2/SiO2 ternary nanocomposites and (d) RR120 removal rate at different photocatalytic systems.
(a)(b)(c)(d)The obtained results clearly show that the RR120 removal efficiency of aqueous solutions without catalyst, with the catalyst in the dark, TiO2/ZrO2, and TiO2/SiO2 were less than that of the heterogeneous TiO2/ZrO2/SiO2 ternary nanocomposites. The plant-based nanocomposite preparation is the most attractive approach for mass production at a minimal price that is safe for the ecosystem and human life. This nanocomposite might be an excellent potential photocatalyst for degrading pollutants utilizing sunlight [49].The fact that the nanocomposites were synthesized by the sol-gel method could describe the photocatalytic improvement under natural sunlight with TiO2/ZrO2/SiO2 ternary nanocomposites. In this case, nanocomposites with a large specific area would include more active surface sites for adsorbing water molecules and forming aggressive •OH and HOO• radicals by capturing the photogenerated holes [50]. The photocatalytic interactions are fueled by these active free radicals, resulting in the degradation of various pollutants from the aqueous medium [51]. However, the larger surface area still enables the dye molecule diminishment on the TiO2/ZrO2/SiO2 photocatalyst surface. According to Abroushan et al. [52], the phosphate molecules are adsorbed on the surface of nanocomposite and generate electrons when exposed to sunlight [52]. In the present study, these electrons are attracted by the surface adsorbed O2 molecules, resulting in the formation of O2•– and HO• radicals, which have a higher chance of contacting RR120 dyes due to a quicker reaction speed, and the RR120 dye may be mineralized over time by superoxide radical ions [53]. As an outcome, the relatively smaller crystalline size of TiO2/ZrO2/SiO2 ternary nanocomposite is advantageous for reducing O2 and oxidation of H2O molecules by capturing the electron, and the hole pair enhances the photocatalytic performance when exposed to sunlight [54]. According to the results, TiO2/ZrO2/SiO2 ternary nanocomposites as active photocatalyst have an excellent photocatalytic potential to discharge the RR120 dye in the aqueous solution. The results obtained were compared with the other green synthesized nanocomposites, as shown in Table 1. From the results, the TiO2/ZrO2/SiO2 photocatalyst has a unique adsorption capability for RR120 in an aqueous solution. This enhancement could be attributed to a synergistic effect on a unique adsorption property and effective electron detachment at the photocatalyst functionality of nanocomposites. Moreover, no photocatalyst based on TiO2/ZrO2/SiO2 ternary nanocomposites for the breakdown of RR120 dye contaminant has been reported until now.Table 1
Comparison of photocatalytic activity of TiO2/ZrO2/SiO2 nanocomposites with similar kinds of studies.
S. NoCatalyst% removalCatalyst (mg/L)Irradiation timeReferences1Fe2O3/Ag nanocomposites88.2%60140 min[64] Saranya et al. [64]2TiO2 nanocomposites94%100150 min[65] Khade et al. [65]3TiO2–SiO2–Ag nanocomposites80%504 h[66] Liu et al. [66]4Catechin@ZIF-L nanocomposites92%50 mg150 min[67] Raju et al. [67]5TiO2/ZrO2/SiO2 nanocomposites96.2%10 mg75 minOur study


## 3.7. Kinetic Study of the TiO2/ZrO2/SiO2 Ternary Nanocomposite Catalysts

Figure5(a) illustrates the reaction kinetics of photodegradation of RR120 dye by various nanocomposites. The k value for a sample with catalyst in a dark chamber, without a catalyst, TiO2/ZrO2, TiO2/SiO2, and TiO2/ZrO2/SiO2 ternary nanocomposite was estimated to be R2=0.7902,0.9503,0.9833.0.9859,and0.9824, respectively. Each of the plot lines shows a linear correlation with a high correlation coefficient of 0.9824, indicating the degradation of RR120 dye by green synthesized ternary nanocomposite using sunlight follows pseudo-first-order reaction kinetics. The higher k value proves that the TiO2/ZrO2/SiO2 ternary nanocomposite has an excellent photocatalytic activity. This statement was in agreement with the previous report conducted by Zhang et al. [55].Figure 5
(a) Pseudo-first-order reaction kinetics of photodegradation of RR120 over various samples and (b) reusability of the prepared TiO2/ZrO2/SiO2 ternary nanocomposites.
(a)(b)


## 3.8. Reusability Study

For assessing the reusability of TiO2/ZrO2/SiO2 ternary nanocomposites, photodegradation was checked by repeating the four cycles as shown in Figure 5(b). The photocatalytic experiments (300 min) were repeated in four cycles, with the same nanocomposites retained after each cycle [56]. At the end of each photocatalytic experiment, samples were recovered and washed with deionized water and then used to analyze their stability. The amount of photocatalytic reduction by the nanocomposites showed the best performance, and similar interpretations were observed in the study conducted by Hinojosa–Reyes et al. [57]). These results depicted the photocatalytic activity of the biogenic fabricated TiO2/ZrO2/SiO2 ternary nanocomposites with renewed management. It can be considered that the distinction in the degradation efficiency might be due to the various surface features, crystalline nature, and the optical properties of nanocomposites [58]. After recycling four times, there were no significant variations in the degradation efficiency. This clearly states that the synthesized TiO2/ZrO2/SiO2 ternary nanocomposites are reusable enough for industrial and environmental applications.


## 3.9. Antibacterial Activity

The bactericidal activity of TiO2/ZrO2/SiO2 against S. aureus and E. coli is displayed in Figure 6. The antibacterial activity was carried out by a well diffusion method, and a zone of inhibition was observed for different concentrations (50, 75, and 100 μg/mL) of a nanocomposite (20 mg in 0.5 mL) [59]. While increasing the concentration of the nanocomposites, the zone of inhibition in the well plate also increases. The highest inhibition rate was observed in S. aureus at the concentration of 100 μg/mL, compared to E. coli (Table 2). The enhanced antibacterial activity of TiO2/ZrO2/SiO2 ternary nanocomposites has been familiar to the generation of reactive oxygen species (ROS), which could disrupt the DNA, proteins, and lipids, and leads to the death of the bacteria [60]. Nanoparticles can easily penetrate through the cell membrane; consequently, accumulation inside bacterial cells damages membrane integrity and ultimately destroys the bacteria [61]. While the nanocomposite was in contact with the cell membrane of the bacteria, Ti2+ was released and bound to the outer membrane; because the bacterial cell membrane was negatively charged [60]. Therefore, Ti2+ positively charged might mutually attract negatively charged cell membrane and cause damage to the cell membrane, which undoubtedly leads to bacterial death [62].Figure 6
Variable numbers of colonies in agar plates (a)Staphylococcus aureus and (b) Escherichia coli exposed to different concentrations of TiO2/ZrO2/SiO2 nanocomposites.
(a)(b)Table 2
Antibacterial activity (zone of inhibition) of TiO2/ZrO2/SiO2 nanocomposites against Gram-positive and Gram-negative bacteria.
Zone of inhibition (ZOI) in mmS. NoSamplesBacterial strainsS. aureusE. coli50μg75μg100μg50μg75μg100μg1.PYLE——————2.TiO2/ZrO2—1±0.62±0.2—1±0.82±0.43.TiO2/SiO2—1±0.21±0.9—1±0.52±0.34.TiO2/ZrO2/SiO2 nanocomposites8 ± 0.611±0.912±0.96±0.48±0.310±0.65.Chloramphenicol10 ± 0.712±0.715±0.312±0.415±0.316±0.6


## 3.10. Photocatalytic Mechanism

Figure7 illustrates the proposed mechanism of RR120 degradation by TiO2/ZrO2/SiO2 nanocomposites. The photocatalytic process consists of the photogenerated electron and hole and their transfer to the surface of the nanocomposites and creates active oxygen species. Under the irradiation of artificial sunlight, each oxide’s conduction and valence band contain the photogenerated hole and electron. According to the diagram, the position of the valence band of TiO2 is higher than that of ZrO2 and SiO2. Therefore, the photogenerated hole transfer can take place from the valance band of TiO2 to the valance band of ZrO2 and SiO2 [63]. However, in the case of photogenerated electrons, transfer takes place from the conduction band of SiO2 to ZrO2 and then to TiO2. Such photogeneration effectively reduces the recombination of electron-hole pairs. Hence, during the photocatalytic reaction, the electron can be captured by O2 to create a superoxide radical anion [55]. The hole can react with the hydroxyl group to generate hydroxyl radicals responsible for the degradation of RR120. It can be clear from the diagram that the hole and electron are effectively separated from each other at the surface of the TiO2/ZrO2/SiO2 nanocomposite.Figure 7
The proposed mechanism of RR120 degradation by TiO2/ZrO2/SiO2 ternary nanocomposites.


## 4. Conclusions

TiO2/ZrO2/SiO2 ternary nanocomposites were successfully synthesized by a simple, efficient, and ecofriendly method. The obtained results showed that TiO2/ZrO2/SiO2 ternary nanocomposites have an excellent photodegradation activity and a promising bactericidal activity against the Staphylococcus aureus and E. coli. The high photocatalytic performance of TiO2/ZrO2/SiO2 was achieved based on the electron transfer between TiO2 NPs and ZrO2-SiO2. Also, the XRD pattern revealed the presence of monoclinic and tetragonal ZrO2 and anatase TiO2. The ternary nanocomposites decreased the recombination rate of electron and hole pairs; therefore, the superoxide anion, hydroxyl radical, and hydroxyl group play important role in the photodegrading and antibacterial activities. In nutshell, the one-pot green synthesized TiO2/ZrO2/SiO2 ternary nanocomposite act as a promising photocatalyst to remove the recalcitrant dye/pollutant in environmental applications and can be used for other industrial and medical applications.



---