# Interconnected CeO2 Nanofibers for Enhanced CO Gas Sensing

Authors: Wenchao Zhang; Nie Zhao; Yongrong Liu; Bo Li
Journal: Journal of Sensors
 (2022)

---

## Abstract

Developing a new type of CO gas sensor with high response, good reproducibility, and short response/recovery time is of great significance in medical fields, especially during anesthesia. During mechanical ventilation, CO gas will be produced by CO2 absorbent. Herein, novel interconnected CeO2 nanofibers with an average diameter of 150 nm are firstly prepared by electrospinning. The results show that the received nanofibers are mainly composed of fluorite-structured CeO2 crystals with oxygen vacancies as well as the adsorbed oxygen species on the fiber surface. It is found that there is no agglomeration and sintering for the nanofibers even after annealing at 1000°C. The interconnected nanofibers exhibit excellent gas sensing performance to CO gas at an optimum operating temperature of 450°C, where the gas sensing response value is 2.82. And the nanofibers also exhibit excellent gas sensing reproducibility, fast response/recovery rate (2 s/4 s), and high response value-concentration correlation toward CO. This study provides a simple approach to interconnected CeO2 nanofibers for potential gas sensor application.


---

## Body

## 1. Introduction

In industry, carbon monoxide (CO) is the basis of monocarbon chemistry, which is mainly used for the production of methanol and phosgene and organic synthesis, and has a very important medical application value [1–3]. However, under normal circumstances, CO is a colorless, tasteless, but highly toxic gas [4]. At a relatively high concentration, people show symptoms of poisoning to varying degrees, which harm the brain, heart, liver, kidney, lung, and other tissues of the human body, and the minimum lethal concentration for human inhalation is 5000 ppm (5 minutes) [5, 6]. According to the ordinances of the National Institute of Occupational Safety and Health, the lethiferous exposure concentration and endurance of CO gas is 35 ppm for endurance of 10 h and 50 ppm for endurance of 8 h [7]. Therefore, it is particularly important to monitor CO leakage in the synthesis and application of CO as fast as possible [8].A semiconductor gas sensor is the most common low-cost gas sensor [9]. A metal oxide semiconductor not only has good chemical and thermal stability but also has excellent gas sensing properties, so it has become a hot research topic all over the world [10, 11]. Among many metal oxides, cerium dioxide (CeO2) is one of the most promising gas sensing materials because of its abundant reserves, low cost, excellent thermal and structural stability, and abundant oxygen vacancies in its crystal structure [12–14]. It is also one of the most promising materials in the field of gas sensing [15]. For example, Wang et al. synthesized silica doped CeO2 nanostructure as NH3 gas sensors, which achieved a 0.5 ppm detection limit and 3244% response to 80 ppm NH3 [16]. But usually, CeO2 nanomaterials are easy to agglomerate, which makes the gas sensing performance of CeO2 nanomaterials decrease rapidly [17]. Compared with nanoparticles, 1D nanofibers have a large aspect ratio, which means that more surface atoms are involved in the surface gas-solid reaction. 1D nanofibers are more stable and do not agglomerate to clumps at high temperatures. Additionally, they provide a simple one-way electron transport and numerous reaction centers compared to higher dimensional nanostructures, thus maintaining a long period of fast response properties [18].In this paper, novel interconnected CeO2 nanofibers are successfully prepared by electrospinning and heat treatment. The interconnected CeO2 nanofibers are connected with each other, which is beneficial to electron transfer. The results show that CeO2 nanofibers have good responsiveness to CO of 10-100 ppm and good reproducibility to the same 100 ppm CO for three times, which indicates that CeO2 nanofibers are a good CO gas sensing material. However, the reported optimal temperature of CeO2 nanofibers is 800°C, and the response/recovery time is long. How to reduce the optimal temperature of CeO2 nanofibers and improve the response/recovery rate is a great challenge.


## 2. Experimental and Characterization

### 2.1. Synthesis of CeO2 Nanofibers

CeO2 nanofibers were prepared by the electrospinning method (Scheme 1). In order to find the proper concentration of the spinning solution, four groups of spinning solutions with different concentrations were designed. Firstly, PVP and Ce(NO3)2·6H2O were dissolved into the DMF to form a uniform and transparent solution, where the weight concentration of Ce(NO3)2·6H2O was 10.50 wt%, 10.0 wt%, 9.5 wt%, and 9.0 wt%, respectively. In electrospinning, the distance between the reeling plate and the needle was controlled at 20 cm, the temperature was approximately 20°C, the humidity was approximately 40%RH, the feed rate was 1 mL/h, and the spinning voltage was 20 kV. When the spinning was stabilized, the white fiber can be seen to be ejected evenly from the needle and distributed in a disc shape on the filament receiving plate. The collected fiber mat was milky white. After that, the white CeO2 nanofibers can be prepared by heating the polymer fiber at 1000°C for 3 h with a ramping rate of 5°C/min.Scheme 1
Synthesis of CeO2 nanofibers from electrospinning.


### 2.2. Characterization

X-ray diffraction (XRD) is characterized on a Japanese TTRAX III X-ray diffractometer with the light source of CuKα ray, while the wavelength is 0.15418 nm. The acceleration voltage is set to 20 kV, and the scanning range is set to 10~90°. The data were analyzed using MDI Jade 6.0 software and the Scherrer formula of D=Kλ/βCOSθ (D is the average size of crystal particle, K is the Scherrer coefficient (0.89), β is the peak HWHM, and θ is the diffraction angle); λ is the wavelength of X-ray (0.15406 nm) used to calculate the average size of crystal particles of gas sensing materials. A scanning electron microscope (SEM) was observed and characterized by Hitachi Field Emission SEM of Hitachi Model S-4800.Fourier-transform infrared (FT-IR) spectra of samples in KBr pellets were obtained with a PerkinElmer spectrometer at the measuring range of 400-4000 cm-1. X-ray photoelectron spectroscopy (XPS) was recorded on a Thermo Scientific ESCALAB 250Xi machine with Al Ka as the excitation source.


### 2.3. Gas Sensing Tests

Gas sensing tests were performed on a commercial CGS-8 Gas Sensing Measurement System. The gas sensor was fabricated by pasting a viscous slurry of the obtained sample onto an alumina tube which was positioned with a pair of Au electrodes and four Pt wires on both ends of the tube. The test substrate was prepared by mixing 0.1 g nanofiber sample with 0.1 mL terpineol to form a homogeneous paste, and then, the paste was carefully coated on the side heating alumina ceramic tube electrode. The outer diameter of the alumina ceramic tube was 1.2 mm, and the length was 4 mm. A Ni-Cr heating wire (diameter=0.5 mm, resistance=35 Ω) was inserted into the tube to form an indirect-heated gas sensor. Ra/Rg was usually used to characterize the response value of the gas sensing material when the resistance decreases after contacting the detection gas. Among them, Ra and Rg were the resistance of the sensor in air and after contact with the gas. Response time (tres) and recovery time (trec) were defined as the time required to achieve a 90% change in sensor resistance, respectively.


## 2.1. Synthesis of CeO2 Nanofibers

CeO2 nanofibers were prepared by the electrospinning method (Scheme 1). In order to find the proper concentration of the spinning solution, four groups of spinning solutions with different concentrations were designed. Firstly, PVP and Ce(NO3)2·6H2O were dissolved into the DMF to form a uniform and transparent solution, where the weight concentration of Ce(NO3)2·6H2O was 10.50 wt%, 10.0 wt%, 9.5 wt%, and 9.0 wt%, respectively. In electrospinning, the distance between the reeling plate and the needle was controlled at 20 cm, the temperature was approximately 20°C, the humidity was approximately 40%RH, the feed rate was 1 mL/h, and the spinning voltage was 20 kV. When the spinning was stabilized, the white fiber can be seen to be ejected evenly from the needle and distributed in a disc shape on the filament receiving plate. The collected fiber mat was milky white. After that, the white CeO2 nanofibers can be prepared by heating the polymer fiber at 1000°C for 3 h with a ramping rate of 5°C/min.Scheme 1
Synthesis of CeO2 nanofibers from electrospinning.


## 2.2. Characterization

X-ray diffraction (XRD) is characterized on a Japanese TTRAX III X-ray diffractometer with the light source of CuKα ray, while the wavelength is 0.15418 nm. The acceleration voltage is set to 20 kV, and the scanning range is set to 10~90°. The data were analyzed using MDI Jade 6.0 software and the Scherrer formula of D=Kλ/βCOSθ (D is the average size of crystal particle, K is the Scherrer coefficient (0.89), β is the peak HWHM, and θ is the diffraction angle); λ is the wavelength of X-ray (0.15406 nm) used to calculate the average size of crystal particles of gas sensing materials. A scanning electron microscope (SEM) was observed and characterized by Hitachi Field Emission SEM of Hitachi Model S-4800.Fourier-transform infrared (FT-IR) spectra of samples in KBr pellets were obtained with a PerkinElmer spectrometer at the measuring range of 400-4000 cm-1. X-ray photoelectron spectroscopy (XPS) was recorded on a Thermo Scientific ESCALAB 250Xi machine with Al Ka as the excitation source.


## 2.3. Gas Sensing Tests

Gas sensing tests were performed on a commercial CGS-8 Gas Sensing Measurement System. The gas sensor was fabricated by pasting a viscous slurry of the obtained sample onto an alumina tube which was positioned with a pair of Au electrodes and four Pt wires on both ends of the tube. The test substrate was prepared by mixing 0.1 g nanofiber sample with 0.1 mL terpineol to form a homogeneous paste, and then, the paste was carefully coated on the side heating alumina ceramic tube electrode. The outer diameter of the alumina ceramic tube was 1.2 mm, and the length was 4 mm. A Ni-Cr heating wire (diameter=0.5 mm, resistance=35 Ω) was inserted into the tube to form an indirect-heated gas sensor. Ra/Rg was usually used to characterize the response value of the gas sensing material when the resistance decreases after contacting the detection gas. Among them, Ra and Rg were the resistance of the sensor in air and after contact with the gas. Response time (tres) and recovery time (trec) were defined as the time required to achieve a 90% change in sensor resistance, respectively.


## 3. Results and Discussion

A SEM photograph of the interconnected CeO2 nanofiber samples is shown in Figure 1. It can be found that the nanofiber can keep good morphology after annealing at 1000°C for 3 hours in air atmosphere, and the nanofiber has a high aspect ratio. The average diameter of the received CeO2 nanofibers was 150 nm, and the diameter was uniform. From the surface morphology of nanofibers, it can be seen that the fibers are composed of many nanoparticles with a relatively small particle size between 20 and 40 nm. This may have resulted from the long annealing time for 3 h at 1000°C, so that the CeO2 crystal size of nanofibers grows up. However, such large grains in the nanofibers can also effectively reduce the carrier loss due to the fewer grain boundaries.Figure 1
SEM images of the interconnected CeO2 nanofibers: (a) low magnification; (b) large magnification.
(a)(b)The interconnected CeO2 nanofibers were analyzed by FT-IR, and the results are shown in Figure 2. The absorption peak near 3400 cm-1 in the FT-IR spectrum is the absorption peak of -OH in air, while the peak near 547 cm-1 is the characteristic absorption peak of Ce-O stretch vibration [19]. This has supported the presence of CeO2, which consisted in the nanofibers.Figure 2
FT-IR spectrum of the interconnected CeO2 nanofibers.The composition and surface states of CeO2 nanofibers were further characterized by XPS. Figure 3(a) is the full XPS spectrum of interconnected nanofibers. It can be seen that there are obvious spectrum lines of Ce3d, Ce4s, Ce4p, Ce4d, and O1s in the sample, indicating that there are only Ce and O elements in the fiber and no other impurities. The presence of the Ce element is analyzed by peaking the Ce3d spectra, as shown in Figure 3(b). The characteristic peaks of 916.7, 907.6, 900.8, 898.4, 888.9, and 882.7 eV obtained by dividing the peak of Ce3d spectra are all typical peaks of the Ce (IV) oxidation state [20]. Among them, the peaks at the binding energy of 916.7, 907.6, and 900.8 eV are the characteristic peaks of Ce element 3d3/2 orbitals, and the peaks at 898.4, 888.9, and 882.7 eV are characteristic peaks of Ce element 3d5/2 orbitals, indicating the Ce (III) oxidation state synthesized with Ce (IV) oxidation state in the samples. This demonstrates that oxygen vacancies existed in the CeO2 nanofibers [19, 21].Figure 3
The XPS spectrum of the interconnected CeO2 nanofibers: (a) survey spectrum; (b) Ce3d spectra.
(a)(b)Figure4 is an O1s splitting pattern of CeO2 nanofibers. For O1s, three main peaks at the binding energy of 532.3, 530.9, and 529.6 eV were obtained. The OL peak at 529.6 eV was the diffraction peak of lattice oxygen in the CeO2 phase, while the OC peak at 532.3 eV was mainly chemically adsorbed oxygen species (O2-, O2-, and O-) [22]. The OV peaks at 530.9 eV were corresponding to oxygen vacancies in the CeO2 crystals, which were likely to cause the encouraging gas sensing by the oxygen vacancy defects [21, 23]. Therefore, according to XPS analysis, the pure CeO2 nanofibers were composed of CeO2 crystals, oxygen vacancies, and adsorbed oxygen species.Figure 4
The O1s splitting pattern of CeO2 nanofibers.The effect of working temperature on the gas sensing performance of interconnected CeO2 nanofibers toward 500 ppm CO was investigated. The results are shown in Figure 5. It was found that the response of CeO2 nanofibers to CO gas increases first and then decreases with the increase of working temperature. The optimum working temperature was 450°C, and the maximum response value of the sensor was 2.82. This is because the sensing material was in low activity at the low working temperature [24]. At the higher temperature, the gas sensing material was more active. However, when the temperature was too high (500°C), the thermal motion of the gas is intense; thus, the gas desorption tendency was stronger. Therefore, only when the gas adsorption and desorption reach the dynamic equilibrium, the response can achieve the highest, and the dynamic equilibrium temperature (approximately 450°C) was the best working temperature for CO gas sensing.Figure 5
The effect of working temperature on the gas sensing response of CeO2 nanofibers.The response/recovery time is an important index to measure the gas sensing performance. The response/recovery times of interconnected CeO2 nanofibers toward 500 ppm CO gas at 350°C and 450°C are shown in Figure 6. Define the response time (tres) and recovery time (trec) as 90% of the resistance value of the gas sensing material at the time of injection and release of the gas. tres/trec of CeO2 nanofibers at 350°C and 450°C are 4 s/5 s and 2 s/4 s, respectively. That is, tres/trec decreases with the increasing working temperature from 350°C to 450°C. This may be ascribed to the relatively higher working temperature which can facilitate the thermal diffusion of the gas and increase the activity of gas sensing materials.Figure 6
The response/recovery time of interconnected CeO2 nanofibers to 500 ppm CO gas: (a) 350°C and (b) 450°C.
(a)(b)Sensing reproducibility reflects the stability of sensing materials to gas. Thus, it is an important index of gas sensing performance. As shown in Figure7, the interconnected CeO2 nanofibers were tested for gas sensing cycling reproducibility on 500 ppm CO at the optimum operating temperature 450°C. The results revealed that the response value of CeO2 nanofibers remained unchanged after 5 cycles, which indicated that the interconnected CeO2 nanofibers had good gas sensing reproducibility.Figure 7
The gas sensing cycling reproducibility of interconnected CeO2 nanofibers.Furthermore, the strong linear relationship between the sensing response and the gas concentration is very important for the gas sensors to recognize the gas concentration. Figure8(a) shows the gas sensing response values of interconnected CeO2 nanofibers to 20, 50, 100, 200, 300, 400, and 500 ppm CO, respectively. It can be seen that the response of the sensor increases gradually with the increasing CO concentration. The sensing response-gas concentration curve is shown in Figure 8(b), where the sensing response was fitted linearly. The correlation coefficient between the sensing responses of CeO2 nanofibers to CO concentration was 0.954, which demonstrated that the sensing response was linearly correlated with the gas concentration.Figure 8
(a) The gas sensing response values of interconnected CeO2 nanofibers toward various CO concentrations and (b) the linear fitting of sensing responses to gas concentrations.
(a)(b)We also compared our sensing performance with previous works on the CO sensor. As shown in Table1, the CeO2 nanofibers exhibit a relatively high response to CO. Particularly, the sensors based on CeO2 nanofibers show an ultrafast response/recovery time, which is better than most of the reported CO sensors [25–29]. According to the great reproducibility, quick response/recovery, and ideally linear fitting ability, the synthesized CeO2 nanofibers in this study showed excellent potential application in CO gas sensing.Table 1
Comparison of recent reported CO sensing performance based on metal oxide gas sensors.
MaterialsCO concentration (ppm)ResponseResponse time (s)Recovery time (s)Ref.ZnO nanoparticles800.78782125Au/CeO2 nanoparticles300.439726TiO2 nanofibers152.68610927Co3O4 nanofibers52.40143628CuO/TiO2 nanoparticles501.7726555429CeO2 nanofibers5002.8224This work


## 4. Conclusions

In this paper, novel interconnected CeO2 nanofibers were simply fabricated via the electrospinning method. The average diameter of interconnected CeO2 nanofibers was only 150 nm, and the nanofibers were mainly composed of fluorite CeO2 crystals, oxygen vacancies, and adsorbed oxygen species in the fibers. The received interconnected CeO2 nanofibers showed an excellent gas sensing performance toward CO. The response of CO was first increasing and followed by decreasing as the increasing of working temperature, due to the dynamic equilibrium of gas adsorption and desorption. The optimum working temperature of the nanofibers was approximately 450°C, and the sensing response value could reach 2.82. Furthermore, the nanofiber samples revealed quick response/recovery ability, and the best response time 2 s and recovery time 4 s were tested at 450°C. The interconnected CeO2 nanofibers also exhibit good gas sensing reproducibility among 5 cycles. In addition, the CeO2 nanofiber exhibited a linear response-gas concentration relationship toward CO from 20 ppm to 500 ppm. This demonstrated that the CeO2 nanofibers in this research could be a great candidate for CO sensors. And CeO2 nanofibers may sensor the CO in the mechanical ventilation.



---