# Detection Limits of DLS and UV-Vis Spectroscopy in Characterization of Polydisperse Nanoparticles Colloids

Authors: Emilia Tomaszewska; Katarzyna Soliwoda; Kinga Kadziola; Beata Tkacz-Szczesna; Grzegorz Celichowski; Michal Cichomski; Witold Szmaja; Jaroslaw Grobelny
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

Dynamic light scattering is a method that depends on the interaction of light with particles. This method can be used for measurements of narrow particle size distributions especially in the range of 2–500 nm. Sample polydispersity can distort the results, and we could not see the real populations of particles because big particles presented in the sample can screen smaller ones. Although the theory and mathematical basics of DLS technique are already well known, little has been done to determine its limits experimentally. The size and size distribution of artificially prepared polydisperse silver nanoparticles (NPs) colloids were studied using dynamic light scattering (DLS) and ultraviolet-visible (UV-Vis) spectroscopy. Polydisperse colloids were prepared based on the mixture of chemically synthesized monodisperse colloids well characterized by atomic force microscopy (AFM), transmission electron microscopy (TEM), DLS, and UV-Vis spectroscopy. Analysis of the DLS results obtained for polydisperse colloids reveals that several percent of the volume content of bigger NPs could screen completely the presence of smaller ones. The presented results could be extremely important from nanoparticles metrology point of view and should help to understand experimental data especially for the one who works with DLS and/or UV-Vis only.


---

## Body

## 1. Introduction

Nanoparticles (NPs) of noble metals, especially silver (Ag) and gold (Au) NPs, attract much attention in various fields. This is because of the unique properties of nanoscale objects, which are completely different from bulk materials, coatings, and single atoms. Applications or potential applications of NPs are not only diverse but also interdisciplinary and are related to material science, electronics, optics, and biomedicine. Noble metal NPs (in particular Ag NPs) can facilitate important advances in detection, diagnosis, and treatment of human cancers as well as delivery of drug and gene to malignant cells [1, 2]. By exploiting the unique optical and electronic properties of Au NPs, several new methods for ultrasensitive detection of DNA, RNA, and proteins have been developed [3–7].Currently, many applications of silver NPs are related to their versatile antibacterial activity against a broad spectrum of bacteria without releasing toxic biocides. It should be noted that depending on the concentration and size silver nanoparticles can be considered as nontoxic as well as toxic [8–10]. Ag NPs are environmentally friendly antibacterial materials and therefore are used in many cosmetic products and medical applications such as hydrogel dressings [11]. Metal NPs are also promising for surface-enhanced Raman scattering (SERS) applications in detection and analysis of molecules. The enhancement factor can be strong enough that the technique allows detection of a single molecule [12–14].As noble metal NPs are widely used in many applications, it is important to synthesize high-quality materials. In certain applications it is also important to prepare colloids with high concentrations. The size and size distribution are becoming extremely significant when quantum-sized effects are used to control material properties. Therefore, the control and complete analysis of the average particle size and narrow size distribution is essential to use NPs in many applications [15, 16].There are a number of methods for nanoparticles size characterization, for example, scanning/transmission electron microscopy (SEM/TEM), atomic force microscopy (AFM) analytical ultracentrifugation (AUC), dynamic light scattering (DLS), and flow field fractionation (FFF). It is also possible to calculate particles size with the use of X-ray diffraction (XRD) patterns as well as with the shift of the band gap absorption in the UV-Vis spectrum [17, 18]. In case of the above-mentioned method [19–23], the particle size distribution is measured in dispersion or after drying the sample. The detailed description of the above-mentioned methods is beyond the scope of this work and will not be described.There is a range of methods available for the particle size determination, and users should remember that precise characterization of particles requires the usage of few of them. Moreover, it is essential to know about the strengths and weaknesses of applied method for nanoparticles characterization in order to recognize the limits; for example, FFF and AUC methods suffer from artifacts like too small particle diameter because of the particle charge [24]. In case of TEM, it is not always obvious to recognize grain boundaries in aggregates. The main advantage of microscopic techniques is that it is possible to get the information about the morphology and the size of particles at the same time, but the preparation of samples for analysis is crucial (e.g., NPs must be deposited on the well-characterized substrate). Moreover, sample preparation is often time consuming, requires high precision and the use of appropriate reagents [25–27]. Microscopic techniques can also be problematic in case of the polydisperse samples because of possibility of particles aggregation or sample fractionation during drying.Among the techniques of nanoparticles characterization the most commonly used are DLS [23, 28, 29] and UV-Vis spectroscopy [30–33]. The theory and mathematical basics of DLS and UV-Vis techniques are already well known [34, 35]. DLS measures the light scattered from the laser that passes through a colloid. Next, the modulation of the scattered light intensity as a function of time is analyzed, and the hydrodynamic size of particles can be determined [36, 37]. In case of UV-Vis spectroscopy, the intensity of light that is passing through the sample is measured. Nanoparticles have optical properties that are very sensitive on size, shape, agglomeration, and concentration changes. The unique optical properties of metal nanoparticles are a consequence of the collective oscillations of conduction electrons, which excited by electromagnetic radiation are called surface plasmon polariton resonances (SPPR) [35]. Those changes have an influence on the refractive index next to the nanoparticles surface; thus it is possible to characterize nanomaterials using UV-Vis spectroscopy. DLS and UV-Vis spectroscopy are fast and easy to operate techniques for particles characterization, especially for colloidal suspensions [38, 39]. There are several advantages of DLS and UV-Vis techniques: simplicity, sensitivity and selectivity to NPs, short time of measurement, and what is more, the calibration is not required. Therefore, these techniques are increasingly used for NPs characterization in many fields of science and industry [22, 23, 40]. Although the DLS technique is widely used for particles characterization, there are some problems in case of measuring samples with large-size distribution or multimodal distributions [23, 29]. If the measured colloid is monodisperse, the mean diameter of NPs can be determined using DLS technique. In case of polydisperse colloids, there is a risk that during the DLS measurement small objects can be screened by bigger ones and will not even be seen at all. By far, little has been done to determine the detection limits of DLS and UV-Vis techniques experimentally. The main aim of this study was to detect limits of widely used DLS and UV-Vis spectroscopy in characterization of polydisperse nanoparticles, colloids (Ag NPs colloids as mixture of nanoparticles with different sizes, 10 nm, and 55 nm; 10 nm and 80 nm) and to determine the possibilities to observe small objects (10 nm) in the presence of large ones (55 nm and 80 nm).To investigate the detection limits of DLS and UV-Vis techniques colloids with the nanoparticles size about: 10, 55 and 80 nm were used. Selected colloids have nanoparticles sizes below 100 nm which is related to the definition of nanomaterials defined by the European Commission. The selected colloids give the possibility to perform high-quality and reliable measurements (the lower limit of particles size for DLS measurements is about 10 nm). The size of nanoparticles about 55 nm is in the middle of the selected limits (10 nm and 80 nm).DLS and UV-Vis spectroscopy as well as AFM and TEM were used to characterize the monodisperse silver NPs. The colloids were intentionally mixed in appropriate volume ratio, and mixtures (polydisperse colloids) were studied using the DLS and UV-Vis techniques.There are works that compare results from different NPs size measurement techniques [29, 41, 42], but in general the researchers do not apply to polydisperse metallic NPs with the size up to 100 nm. To the authors’ knowledge, the present paper reports the results of such an investigation for the first time.


## 2. Materials and Methods

### 2.1. Synthesis of Monodisperse Silver Nanoparticles

To prepare the polydisperse colloids, it was necessary to synthesize and characterize monodisperse Ag NPs colloids. Ag NPs were obtained in three different sizes: 10 nm, 55 nm, and 80 nm. For the synthesis of NPs [43], the following reagents were used: silver nitrate (AgNO3, purity 99.999%, obtained from Sigma-Aldrich), and sodium citrate (C6H5Na3O7·2H2O, purity 99.0%, obtained from Sigma-Aldrich), tannic acid (C76H52O46, obtained from Fluka), sodium borohydride (NaBH4, purity ≥ 96%, obtained from Sigma-Aldrich). Deionized water was obtained from Deionizer Millipore Simplicity UV system.After the synthesis, the amount of silver ions was determined using flame atomic adsorption spectrometry (AAS, Varian, Spectra 300). The amount of silver ion was less than 0.5 ppm.


#### 2.1.1. Synthesis of 10 nm Ag NPs (Sample 1)

Silver NPs with an average diameter of 10 nm were prepared as follows: into 95.5 g of aqueous silver nitrate solution at the concentration of 0.017%, set on a mechanical stirrer, a mixture of sodium citrate (4.2 g, 4%) and tannic acid (0.63 g, 5%) was added. Immediately after mixing reagents, 0.7 g of solution of sodium borohydride, at the concentration of 2%, was added. After the addition of reductants, the color of the solution changed into brown. The whole mixture was vigorously stirred for 15 min. Final concentration of Ag in colloids was 100 ppm.


#### 2.1.2. Synthesis of 55 nm Ag NPs (Sample 2)

Silver NPs with an average diameter of 55 nm (100 ppm) were prepared by reduction of AgNO3 by sodium citrate and tannic acid. An aqueous solution of AgNO3 (48.85 g, 0.016%) was heated to boil and stirred under reflux. Next the mixture of an aqueous solution of sodium citrate (0.52 g, 4%) and an aqueous solution of tannic acid (0.63 g, 5%) was added. After the addition of the reductants the color of the solution changed into yellow, which indicated the formation of the silver NPs. The solution was vigorously stirred under reflux for additional 15 min, and after that time the suspension was cooled to room temperature. Final concentration of Ag in colloids was 100 ppm.


#### 2.1.3. Synthesis of 80 nm Ag NPs (Sample 3)

Silver NPs with an average diameter of 80 nm were prepared as described above, but with the different amount of silver nitrate (492.7 g, 0.048%), sodium citrate (4.2 g, 15%), and tannic acid (3.15 g, 30%). After synthesis, the solution was dissolved to final concentration of Ag in colloids which was 100 ppm.


### 2.2. Measurement Techniques

The resulting monodisperse NPs of silver colloids (samples 1–3) were examined using the AFM, TEM, DLS, and UV-Vis techniques.


#### 2.2.1. Atomic Force Microscopy

AFM measurements of NPs were performed with the use of a commercial AFM system (Solver P47, NT-MDT), operating in air under ambient conditions. Images were typically obtained in the tapping mode using a rectangular silicon nitride cantilever (NSC 35/Si3N4/AlBS, MikroMasch). The composition of the 1, 2, and 3 colloids varies. In case of samples 1, 2, and 3, the nanoparticles surface stabilizer is different, so that it was necessary to use a different surface modifier for the more effective adsorption of nanoparticles on the substrate. Hence, different substrates (mica or silicon wafer) for AFM measurements were used. Moreover, the usage of a different modifier has a negligible effect on the measured size of NPs. In order to carry out AFM measurements, colloids of silver NPs were deposited on mica (sample 1) or silicon substrates (samples 2 and 3) using the procedure described in [25].


#### 2.2.2. Transmission Electron Microscopy

The size and shape of Ag NPs (samples 1 and 2) were evaluated by a high resolution transmission electron microscope, JEOL JEM 1200 EX, at an accelerating voltage of 120 kV. TEM samples of the silver NPs (samples 1, 2, and 3) were prepared by placing of the product solution onto the carbon-coated copper grids, allowing the solvent to evaporate in air.


#### 2.2.3. Dynamic Light Scattering

The size and size distribution of particles in the colloids were measured using a Nano ZS zetasizer system (Malvern Instruments). Measurement parameters were as follows: a laser wavelength of 633 nm (He–Ne), a scattering angle of 173° (fixed—without changing possibility), a measurement temperature of 25°C, a medium viscosity of 0.8872 mPa·s and a medium refractive index of 1.330, and material refractive index of 0.200. Before DLS measurement, the colloid was passed through a 0.2μm polyvinylidene fluoride (PVDF) membrane. The sample was loaded into quartz microcuvette, and five measurements were performed, for which the mean result was recorded. DLS studies were carried out in two modes: general purpose mode (with normal resolution) and multiple narrow mode (with high resolution).


#### 2.2.4. UV-Vis Spectroscopy

UV-Vis spectra were recorded using as a light source versatile lamps optimized for the visible-near infrared Vis-NIR (360–2000 nm), Ocean Optics, HL-2000 (tungsten halogen light sources). To collect UV-Vis spectra, the USB2000 + detector (miniature fiber optic spectrometer) was used. Before measurement, the samples were diluted one hundred times. The presented results were obtained by averaging 1000 of single measurements.


### 2.3. Polydisperse Sample Preparation

The prepared and well-characterized monodisperse colloids were mixed together in appropriate volume ratios. To examine the sensitivity/resolution of DLS and UV-Vis techniques, the mixtures of monodisperse colloids with the size of 10, 55, and 80 nm were measured. The list of initial colloids and polydisperse samples prepared by the mixing of appropriate monodisperse colloids is presented in Table1.Table 1
Summary of tested samples. The numbers indicate the percentage of the volume for silver NPs of a particular size.
Sample  number
Percentage volume [%]
Presented  results
10 nm AgNPs
55 nm AgNPs
80 nm AgNPs
1
100
—
—
DLS, AFM, TEM, UV-Vis
2
—
100
—
DLS, AFM, TEM, UV-Vis
3
—
—
100
DLS, AFM, TEM, UV-Vis
4
99
1
—
DLS, UV-Vis
5
98
2
—
DLS, UV-Vis
6
97
3
—
DLS, UV-Vis
7
96
4
—
DLS, UV-Vis
8
95
5
—
DLS, UV-Vis
9
90
10
—
UV-Vis
10
80
20
—
UV-Vis
11
70
30
—
UV-Vis
12
60
40
UV-Vis
13
50
50
—
UV-Vis
14
40
60
—
UV-Vis
15
20
80
—
UV-Vis
16
99
—
1
DLS, UV-Vis
17
98
—
2
DLS, UV-Vis
18
97
—
3
DLS, UV-Vis
19
96
—
4
DLS, UV-Vis
20
95
—
5
DLS, UV-Vis
21
90
—
10
UV-Vis
22
80
—
20
UV-Vis
23
70
—
30
UV-Vis
24
60
—
40
UV-Vis
25
50
—
50
UV-Vis
26
40
—
60
UV-Vis
27
20
—
80
UV-VisThe DLS and UV-Vis characterization was carried out for the samples 4–8 and 16–20. Additional measurements using UV-Vis spectroscopy were performed for the samples 9–15 and 21–27.


## 2.1. Synthesis of Monodisperse Silver Nanoparticles

To prepare the polydisperse colloids, it was necessary to synthesize and characterize monodisperse Ag NPs colloids. Ag NPs were obtained in three different sizes: 10 nm, 55 nm, and 80 nm. For the synthesis of NPs [43], the following reagents were used: silver nitrate (AgNO3, purity 99.999%, obtained from Sigma-Aldrich), and sodium citrate (C6H5Na3O7·2H2O, purity 99.0%, obtained from Sigma-Aldrich), tannic acid (C76H52O46, obtained from Fluka), sodium borohydride (NaBH4, purity ≥ 96%, obtained from Sigma-Aldrich). Deionized water was obtained from Deionizer Millipore Simplicity UV system.After the synthesis, the amount of silver ions was determined using flame atomic adsorption spectrometry (AAS, Varian, Spectra 300). The amount of silver ion was less than 0.5 ppm.


### 2.1.1. Synthesis of 10 nm Ag NPs (Sample 1)

Silver NPs with an average diameter of 10 nm were prepared as follows: into 95.5 g of aqueous silver nitrate solution at the concentration of 0.017%, set on a mechanical stirrer, a mixture of sodium citrate (4.2 g, 4%) and tannic acid (0.63 g, 5%) was added. Immediately after mixing reagents, 0.7 g of solution of sodium borohydride, at the concentration of 2%, was added. After the addition of reductants, the color of the solution changed into brown. The whole mixture was vigorously stirred for 15 min. Final concentration of Ag in colloids was 100 ppm.


### 2.1.2. Synthesis of 55 nm Ag NPs (Sample 2)

Silver NPs with an average diameter of 55 nm (100 ppm) were prepared by reduction of AgNO3 by sodium citrate and tannic acid. An aqueous solution of AgNO3 (48.85 g, 0.016%) was heated to boil and stirred under reflux. Next the mixture of an aqueous solution of sodium citrate (0.52 g, 4%) and an aqueous solution of tannic acid (0.63 g, 5%) was added. After the addition of the reductants the color of the solution changed into yellow, which indicated the formation of the silver NPs. The solution was vigorously stirred under reflux for additional 15 min, and after that time the suspension was cooled to room temperature. Final concentration of Ag in colloids was 100 ppm.


### 2.1.3. Synthesis of 80 nm Ag NPs (Sample 3)

Silver NPs with an average diameter of 80 nm were prepared as described above, but with the different amount of silver nitrate (492.7 g, 0.048%), sodium citrate (4.2 g, 15%), and tannic acid (3.15 g, 30%). After synthesis, the solution was dissolved to final concentration of Ag in colloids which was 100 ppm.


## 2.1.1. Synthesis of 10 nm Ag NPs (Sample 1)

Silver NPs with an average diameter of 10 nm were prepared as follows: into 95.5 g of aqueous silver nitrate solution at the concentration of 0.017%, set on a mechanical stirrer, a mixture of sodium citrate (4.2 g, 4%) and tannic acid (0.63 g, 5%) was added. Immediately after mixing reagents, 0.7 g of solution of sodium borohydride, at the concentration of 2%, was added. After the addition of reductants, the color of the solution changed into brown. The whole mixture was vigorously stirred for 15 min. Final concentration of Ag in colloids was 100 ppm.


## 2.1.2. Synthesis of 55 nm Ag NPs (Sample 2)

Silver NPs with an average diameter of 55 nm (100 ppm) were prepared by reduction of AgNO3 by sodium citrate and tannic acid. An aqueous solution of AgNO3 (48.85 g, 0.016%) was heated to boil and stirred under reflux. Next the mixture of an aqueous solution of sodium citrate (0.52 g, 4%) and an aqueous solution of tannic acid (0.63 g, 5%) was added. After the addition of the reductants the color of the solution changed into yellow, which indicated the formation of the silver NPs. The solution was vigorously stirred under reflux for additional 15 min, and after that time the suspension was cooled to room temperature. Final concentration of Ag in colloids was 100 ppm.


## 2.1.3. Synthesis of 80 nm Ag NPs (Sample 3)

Silver NPs with an average diameter of 80 nm were prepared as described above, but with the different amount of silver nitrate (492.7 g, 0.048%), sodium citrate (4.2 g, 15%), and tannic acid (3.15 g, 30%). After synthesis, the solution was dissolved to final concentration of Ag in colloids which was 100 ppm.


## 2.2. Measurement Techniques

The resulting monodisperse NPs of silver colloids (samples 1–3) were examined using the AFM, TEM, DLS, and UV-Vis techniques.


### 2.2.1. Atomic Force Microscopy

AFM measurements of NPs were performed with the use of a commercial AFM system (Solver P47, NT-MDT), operating in air under ambient conditions. Images were typically obtained in the tapping mode using a rectangular silicon nitride cantilever (NSC 35/Si3N4/AlBS, MikroMasch). The composition of the 1, 2, and 3 colloids varies. In case of samples 1, 2, and 3, the nanoparticles surface stabilizer is different, so that it was necessary to use a different surface modifier for the more effective adsorption of nanoparticles on the substrate. Hence, different substrates (mica or silicon wafer) for AFM measurements were used. Moreover, the usage of a different modifier has a negligible effect on the measured size of NPs. In order to carry out AFM measurements, colloids of silver NPs were deposited on mica (sample 1) or silicon substrates (samples 2 and 3) using the procedure described in [25].


### 2.2.2. Transmission Electron Microscopy

The size and shape of Ag NPs (samples 1 and 2) were evaluated by a high resolution transmission electron microscope, JEOL JEM 1200 EX, at an accelerating voltage of 120 kV. TEM samples of the silver NPs (samples 1, 2, and 3) were prepared by placing of the product solution onto the carbon-coated copper grids, allowing the solvent to evaporate in air.


### 2.2.3. Dynamic Light Scattering

The size and size distribution of particles in the colloids were measured using a Nano ZS zetasizer system (Malvern Instruments). Measurement parameters were as follows: a laser wavelength of 633 nm (He–Ne), a scattering angle of 173° (fixed—without changing possibility), a measurement temperature of 25°C, a medium viscosity of 0.8872 mPa·s and a medium refractive index of 1.330, and material refractive index of 0.200. Before DLS measurement, the colloid was passed through a 0.2μm polyvinylidene fluoride (PVDF) membrane. The sample was loaded into quartz microcuvette, and five measurements were performed, for which the mean result was recorded. DLS studies were carried out in two modes: general purpose mode (with normal resolution) and multiple narrow mode (with high resolution).


### 2.2.4. UV-Vis Spectroscopy

UV-Vis spectra were recorded using as a light source versatile lamps optimized for the visible-near infrared Vis-NIR (360–2000 nm), Ocean Optics, HL-2000 (tungsten halogen light sources). To collect UV-Vis spectra, the USB2000 + detector (miniature fiber optic spectrometer) was used. Before measurement, the samples were diluted one hundred times. The presented results were obtained by averaging 1000 of single measurements.


## 2.2.1. Atomic Force Microscopy

AFM measurements of NPs were performed with the use of a commercial AFM system (Solver P47, NT-MDT), operating in air under ambient conditions. Images were typically obtained in the tapping mode using a rectangular silicon nitride cantilever (NSC 35/Si3N4/AlBS, MikroMasch). The composition of the 1, 2, and 3 colloids varies. In case of samples 1, 2, and 3, the nanoparticles surface stabilizer is different, so that it was necessary to use a different surface modifier for the more effective adsorption of nanoparticles on the substrate. Hence, different substrates (mica or silicon wafer) for AFM measurements were used. Moreover, the usage of a different modifier has a negligible effect on the measured size of NPs. In order to carry out AFM measurements, colloids of silver NPs were deposited on mica (sample 1) or silicon substrates (samples 2 and 3) using the procedure described in [25].


## 2.2.2. Transmission Electron Microscopy

The size and shape of Ag NPs (samples 1 and 2) were evaluated by a high resolution transmission electron microscope, JEOL JEM 1200 EX, at an accelerating voltage of 120 kV. TEM samples of the silver NPs (samples 1, 2, and 3) were prepared by placing of the product solution onto the carbon-coated copper grids, allowing the solvent to evaporate in air.


## 2.2.3. Dynamic Light Scattering

The size and size distribution of particles in the colloids were measured using a Nano ZS zetasizer system (Malvern Instruments). Measurement parameters were as follows: a laser wavelength of 633 nm (He–Ne), a scattering angle of 173° (fixed—without changing possibility), a measurement temperature of 25°C, a medium viscosity of 0.8872 mPa·s and a medium refractive index of 1.330, and material refractive index of 0.200. Before DLS measurement, the colloid was passed through a 0.2μm polyvinylidene fluoride (PVDF) membrane. The sample was loaded into quartz microcuvette, and five measurements were performed, for which the mean result was recorded. DLS studies were carried out in two modes: general purpose mode (with normal resolution) and multiple narrow mode (with high resolution).


## 2.2.4. UV-Vis Spectroscopy

UV-Vis spectra were recorded using as a light source versatile lamps optimized for the visible-near infrared Vis-NIR (360–2000 nm), Ocean Optics, HL-2000 (tungsten halogen light sources). To collect UV-Vis spectra, the USB2000 + detector (miniature fiber optic spectrometer) was used. Before measurement, the samples were diluted one hundred times. The presented results were obtained by averaging 1000 of single measurements.


## 2.3. Polydisperse Sample Preparation

The prepared and well-characterized monodisperse colloids were mixed together in appropriate volume ratios. To examine the sensitivity/resolution of DLS and UV-Vis techniques, the mixtures of monodisperse colloids with the size of 10, 55, and 80 nm were measured. The list of initial colloids and polydisperse samples prepared by the mixing of appropriate monodisperse colloids is presented in Table1.Table 1
Summary of tested samples. The numbers indicate the percentage of the volume for silver NPs of a particular size.
Sample  number
Percentage volume [%]
Presented  results
10 nm AgNPs
55 nm AgNPs
80 nm AgNPs
1
100
—
—
DLS, AFM, TEM, UV-Vis
2
—
100
—
DLS, AFM, TEM, UV-Vis
3
—
—
100
DLS, AFM, TEM, UV-Vis
4
99
1
—
DLS, UV-Vis
5
98
2
—
DLS, UV-Vis
6
97
3
—
DLS, UV-Vis
7
96
4
—
DLS, UV-Vis
8
95
5
—
DLS, UV-Vis
9
90
10
—
UV-Vis
10
80
20
—
UV-Vis
11
70
30
—
UV-Vis
12
60
40
UV-Vis
13
50
50
—
UV-Vis
14
40
60
—
UV-Vis
15
20
80
—
UV-Vis
16
99
—
1
DLS, UV-Vis
17
98
—
2
DLS, UV-Vis
18
97
—
3
DLS, UV-Vis
19
96
—
4
DLS, UV-Vis
20
95
—
5
DLS, UV-Vis
21
90
—
10
UV-Vis
22
80
—
20
UV-Vis
23
70
—
30
UV-Vis
24
60
—
40
UV-Vis
25
50
—
50
UV-Vis
26
40
—
60
UV-Vis
27
20
—
80
UV-VisThe DLS and UV-Vis characterization was carried out for the samples 4–8 and 16–20. Additional measurements using UV-Vis spectroscopy were performed for the samples 9–15 and 21–27.


## 3. Results and Discussion

### 3.1. Monodisperse Silver Nanoparticles

The colloids prepared as monodisperse silver NPs were measured using DLS. The size measured in DLS technique is the hydrodynamic diameter of the theoretical sphere that diffuses with the same speed as the measured nanoparticle. This size is not only connected with the metallic core of the nanoparticles (like it is in case of microscopic techniques when measuring the size of nanoparticles) but it is also influenced with all substances adsorbed on the surface of the nanoparticles (e.g., stabilizers) and the thickness of the electrical double layer (solvation shell), moving along with the particle. The thickness of the electrical double layer and its influence on the measured size of nanoparticles depend on the substances present in the colloid and on the surface of nanoparticles. As a consequence, the size measured in DLS technique is bigger in comparison with macroscopic techniques. The results obtained for the samples 1–3 are shown in Figure1. Analyses of obtained results indicate that in the investigated colloids monodisperse NPs with size (10 ± 5) nm (Figure 1(a)), (55 ± 9) nm (Figure 1(b)), and (80 ± 20) nm (Figure 1(c)) are present. In all cases, measurements uncertainties were calculated as the standard deviation. Measurements parameters were as follows: dispersant RI = 1,330; viscosity = 0,8872 cP; temperature = 25,0°C; attenuator was set up automatically and ranged from 6 to 9. In case of all monodisperse AgNPs, the count rate was between 160 and 400 kcps. Polydispersity index (PdI) for monodisperse silver nanoparticles was smaller than 0,140.Size distribution of Ag NPs measured by the DLS technique for (a) sample 1, (b) sample 2, and (c) sample 3.
(a)
(b)
(c)Figure2 shows AFM images of Ag NPs (samples 1–3) homogeneously distributed on the different surfaces. Analysis of these images confirms that the silver NPs are monodisperse. The diameters of the obtained NPs were (8 ± 3) nm, (38 ± 6) nm and (55 ± 9) nm for the samples 1, 2, and 3, respectively. The average sizes of NPs were determined by measuring at least one hundred objects and creating a histogram. AFM images show that the investigated objects are monodisperse, without aggregates or agglomerates. The particles are characterized by a narrow size distribution around the mean value.AFM images of monodisperse silver NPs for (a) sample 1 deposited on mica substrate, (b) sample 2 deposited on silicon substrate, and (c) sample 3 deposited on silicon substrate.
(a)
(b)
(c)Additionally, TEM was also used to determine the average size of silver NPs. TEM images of sample 1 (Figure3(a)), sample 2 (Figure 3(b)), and sample 3 (Figure 3(c)) were recorded in order to verify the presence of monodisperse NPs. The diameters of nanoparticles were measured using Motic Plus 2.0 software. The population of analyzed nanoparticles was about 100 for AFM and TEM measurements. Next, the size distribution histogram was created, and for each data set, the mean size and standard deviation were calculated. The study allowed determining the average sizes of NPs to be (10 ± 2) nm, (41 ± 5) nm, and (61 ± 11) nm for the samples 1, 2, and 3, respectively. Agglomerated nanoparticles seen on TEM images are connected with the sample preparation for measurements. In case of sample preparation for TEM measurements, it is not possible to modify the substrate surface (copper grid with a thin carbon coating). As a consequence, it may happen that some accumulated nanoparticles can be seen. However, AFM and DLS measurements revealed that colloids (sample 1, 2, and 3) are monodisperse.TEM images of monodisperse Ag NPs for (a) sample 1, (b) sample 2, and (c) sample 3.
(a)
(b)
(c)For monodisperse colloids, measurements with the use of UV-Vis spectroscopy were also performed. The absorption peaks are located at wavelengths of 407 nm, 427 nm, and 439 nm for the samples 1, 2, and 3, respectively.It should be noted that differences in the size of NPs were determined by the use of different techniques. This is not caused by measurement error, but in fact by the specificity of each technique. TEM and AFM measure the geometric size of the NPs deposited on the surface, so the results from these two techniques are similar. In case of the DLS technique, the hydrodynamic size is measured. This size is characterized for the ball model, which has the same diffusion coefficient as a measured NP. As a result, the size of measured NPs can differ from that determined by the AFM/TEM techniques. In general, each presented measurement method shows that only monodisperse particles are present in the investigated colloids.


### 3.2. Polydisperse Colloids of Silver Nanoparticles

The DLS results of the polydisperse colloids obtained by mixing monodisperse 10 nm and 55 nm Ag NPs (samples 4–8) are shown in Figure4. Similar studies using DLS have been carried out for the polydisperse colloids obtained by mixing 10 nm with 80 nm Ag NPs (samples 16–20), and the obtained results are presented in Figure 5. It can be observed that when the volume of bigger particles increases the signal from small particles decreases. This is a consequence of the fact that the ability of a particle to scatter light is proportional to its diameter to the sixth power [41]. The peak coming from 10 nm Ag NPs disappears completely at the 95% of the content of these particles in the colloid (Figure 4(e)). In the considered case, the intensity of light scattered by larger particles (55 nm or 80 nm Ag NPs) totally conceals the signal from smaller ones (10 nm Ag NPs). And as a consequence, such a result can wrongly suggest that only monodisperse particles 55 nm (or 80 nm) in size are present in the colloid.Size distribution of silver NPs measured by the DLS technique for mixtures of monodisperse 10 nm and 55 nm Ag NPs for (a) sample 4, (b) sample 5, (c) sample 6, (d) sample 7, and (e) sample 8. The numbers close to the histogram bars indicate the percentage of the volume for Ag NPs of a particular size in the analyzed mixture.
(a)
(b)
(c)
(d)
(e)Size distribution of silver NPs measured by the DLS technique for mixtures of monodisperse 10 nm and 80 nm Ag NPs for (a) sample 16, (b) sample 17, (c) sample 18, (d) sample 19, and (e) sample 20. The numbers close to the histogram bars indicate the percentage of the volume for Ag NPs of a particular size in the analyzed mixture.
(a)
(b)
(c)
(d)
(e)The characterization results of the optical properties of the polydisperse silver colloids obtained by mixing monodisperse 10 nm and 55 nm (10 nm and 80 nm) Ag NPs in the appropriate volume ratio are shown in Figure6(a) (Figure 6(b)).Evolution of the absorption spectra for mixtures of (a) 10 nm and 55 nm Ag NPs, (b) 10 nm and 80 nm Ag NPs.
(a)
(b)It can be seen that the maximum absorption wavelength increases with the increasing of larger size Ag NPs percentage volume. Finally the maximum absorption peak is shifted to a wavelength of 427 nm (439 nm) when only particles with the size of 55 nm (80 nm) are present in the solution. Such a red-shift is characteristic for an increased NPs size [43, 44]. The position of absorption maximum of polydisperse colloid does not give information about the size of nanoparticles, because it is not possible to observe peaks separation form specific populations in these colloids.


## 3.1. Monodisperse Silver Nanoparticles

The colloids prepared as monodisperse silver NPs were measured using DLS. The size measured in DLS technique is the hydrodynamic diameter of the theoretical sphere that diffuses with the same speed as the measured nanoparticle. This size is not only connected with the metallic core of the nanoparticles (like it is in case of microscopic techniques when measuring the size of nanoparticles) but it is also influenced with all substances adsorbed on the surface of the nanoparticles (e.g., stabilizers) and the thickness of the electrical double layer (solvation shell), moving along with the particle. The thickness of the electrical double layer and its influence on the measured size of nanoparticles depend on the substances present in the colloid and on the surface of nanoparticles. As a consequence, the size measured in DLS technique is bigger in comparison with macroscopic techniques. The results obtained for the samples 1–3 are shown in Figure1. Analyses of obtained results indicate that in the investigated colloids monodisperse NPs with size (10 ± 5) nm (Figure 1(a)), (55 ± 9) nm (Figure 1(b)), and (80 ± 20) nm (Figure 1(c)) are present. In all cases, measurements uncertainties were calculated as the standard deviation. Measurements parameters were as follows: dispersant RI = 1,330; viscosity = 0,8872 cP; temperature = 25,0°C; attenuator was set up automatically and ranged from 6 to 9. In case of all monodisperse AgNPs, the count rate was between 160 and 400 kcps. Polydispersity index (PdI) for monodisperse silver nanoparticles was smaller than 0,140.Size distribution of Ag NPs measured by the DLS technique for (a) sample 1, (b) sample 2, and (c) sample 3.
(a)
(b)
(c)Figure2 shows AFM images of Ag NPs (samples 1–3) homogeneously distributed on the different surfaces. Analysis of these images confirms that the silver NPs are monodisperse. The diameters of the obtained NPs were (8 ± 3) nm, (38 ± 6) nm and (55 ± 9) nm for the samples 1, 2, and 3, respectively. The average sizes of NPs were determined by measuring at least one hundred objects and creating a histogram. AFM images show that the investigated objects are monodisperse, without aggregates or agglomerates. The particles are characterized by a narrow size distribution around the mean value.AFM images of monodisperse silver NPs for (a) sample 1 deposited on mica substrate, (b) sample 2 deposited on silicon substrate, and (c) sample 3 deposited on silicon substrate.
(a)
(b)
(c)Additionally, TEM was also used to determine the average size of silver NPs. TEM images of sample 1 (Figure3(a)), sample 2 (Figure 3(b)), and sample 3 (Figure 3(c)) were recorded in order to verify the presence of monodisperse NPs. The diameters of nanoparticles were measured using Motic Plus 2.0 software. The population of analyzed nanoparticles was about 100 for AFM and TEM measurements. Next, the size distribution histogram was created, and for each data set, the mean size and standard deviation were calculated. The study allowed determining the average sizes of NPs to be (10 ± 2) nm, (41 ± 5) nm, and (61 ± 11) nm for the samples 1, 2, and 3, respectively. Agglomerated nanoparticles seen on TEM images are connected with the sample preparation for measurements. In case of sample preparation for TEM measurements, it is not possible to modify the substrate surface (copper grid with a thin carbon coating). As a consequence, it may happen that some accumulated nanoparticles can be seen. However, AFM and DLS measurements revealed that colloids (sample 1, 2, and 3) are monodisperse.TEM images of monodisperse Ag NPs for (a) sample 1, (b) sample 2, and (c) sample 3.
(a)
(b)
(c)For monodisperse colloids, measurements with the use of UV-Vis spectroscopy were also performed. The absorption peaks are located at wavelengths of 407 nm, 427 nm, and 439 nm for the samples 1, 2, and 3, respectively.It should be noted that differences in the size of NPs were determined by the use of different techniques. This is not caused by measurement error, but in fact by the specificity of each technique. TEM and AFM measure the geometric size of the NPs deposited on the surface, so the results from these two techniques are similar. In case of the DLS technique, the hydrodynamic size is measured. This size is characterized for the ball model, which has the same diffusion coefficient as a measured NP. As a result, the size of measured NPs can differ from that determined by the AFM/TEM techniques. In general, each presented measurement method shows that only monodisperse particles are present in the investigated colloids.


## 3.2. Polydisperse Colloids of Silver Nanoparticles

The DLS results of the polydisperse colloids obtained by mixing monodisperse 10 nm and 55 nm Ag NPs (samples 4–8) are shown in Figure4. Similar studies using DLS have been carried out for the polydisperse colloids obtained by mixing 10 nm with 80 nm Ag NPs (samples 16–20), and the obtained results are presented in Figure 5. It can be observed that when the volume of bigger particles increases the signal from small particles decreases. This is a consequence of the fact that the ability of a particle to scatter light is proportional to its diameter to the sixth power [41]. The peak coming from 10 nm Ag NPs disappears completely at the 95% of the content of these particles in the colloid (Figure 4(e)). In the considered case, the intensity of light scattered by larger particles (55 nm or 80 nm Ag NPs) totally conceals the signal from smaller ones (10 nm Ag NPs). And as a consequence, such a result can wrongly suggest that only monodisperse particles 55 nm (or 80 nm) in size are present in the colloid.Size distribution of silver NPs measured by the DLS technique for mixtures of monodisperse 10 nm and 55 nm Ag NPs for (a) sample 4, (b) sample 5, (c) sample 6, (d) sample 7, and (e) sample 8. The numbers close to the histogram bars indicate the percentage of the volume for Ag NPs of a particular size in the analyzed mixture.
(a)
(b)
(c)
(d)
(e)Size distribution of silver NPs measured by the DLS technique for mixtures of monodisperse 10 nm and 80 nm Ag NPs for (a) sample 16, (b) sample 17, (c) sample 18, (d) sample 19, and (e) sample 20. The numbers close to the histogram bars indicate the percentage of the volume for Ag NPs of a particular size in the analyzed mixture.
(a)
(b)
(c)
(d)
(e)The characterization results of the optical properties of the polydisperse silver colloids obtained by mixing monodisperse 10 nm and 55 nm (10 nm and 80 nm) Ag NPs in the appropriate volume ratio are shown in Figure6(a) (Figure 6(b)).Evolution of the absorption spectra for mixtures of (a) 10 nm and 55 nm Ag NPs, (b) 10 nm and 80 nm Ag NPs.
(a)
(b)It can be seen that the maximum absorption wavelength increases with the increasing of larger size Ag NPs percentage volume. Finally the maximum absorption peak is shifted to a wavelength of 427 nm (439 nm) when only particles with the size of 55 nm (80 nm) are present in the solution. Such a red-shift is characteristic for an increased NPs size [43, 44]. The position of absorption maximum of polydisperse colloid does not give information about the size of nanoparticles, because it is not possible to observe peaks separation form specific populations in these colloids.


## 4. Conclusions

Measurements of the artificially prepared polydisperse colloids were performed using the DLS and UV-Vis spectroscopy techniques. Based on the DLS results, it can be concluded that the detection of smaller NPs in the presence of several percent of bigger ones (mixed together as polydisperse colloids) seems to be in fact very difficult.Simple calculations show that the number of particles with the size of 10 nm in the tested mixtures could be even three orders of magnitude larger than that of 55 nm particles and four orders of magnitude larger than that of 80 nm particles (under the same silver mass concentration per volume unit). However, the light scatter from bigger AgNPs is so intense that the scatter light coming from smaller AgNPs is concealed. Consequently it is not possible to detect the signal coming from 95% of smaller AgNPs in the presence of 5% bigger AuNPs. Depending on the combination of monodisperse colloids applied to prepare artificial polydisperse colloid, the detection limits of DLS and UV-Vis techniques can vary. In case of UV-Vis spectroscopy the separation of peaks for NPs of different sizes was not observed. Measurements of polydisperse colloids showed only the shift of the peak maximum compared with monodisperse samples. Hence, UV-Vis should not be used as a routine method to quantitatively examine particle size but there are a lot of researches where only UV-Vis is used to quantitatively examine particle size [45, 46].There are other measurement techniques where using a lot more complicated equipment is possible to observe specific populations of nanoparticles in polydisperse colloids [47]. However, the main advantage of DLS and UV-Vis is that these techniques are easy to perform as well as quick and cheap. Nevertheless, the present paper clearly shows that while carrying out the synthesis of NPs, one should be very careful while interpreting the results obtained with the mentioned techniques. The obtained results are not unambiguous and an inexperienced investigator may be misled. One has to be aware that in the case of DLS or UV-Vis spectroscopy investigation of polydisperse NPs, it is necessary to make also study by much more reliable techniques such as AFM or TEM/SEM.



---

*Source: 313081-2013-07-14.xml*