# Thermal Analysis of NR Composite with MWCNTs Aligned in a Magnetic Field

Authors: Jin Xu; Yan He
Journal: International Journal of Polymer Science
 (2015)

---

## Abstract

We got the aligned carbon tube in the rubber matrix through magnetic field. TEM shows that Fe3O4 is symmetrically coated on the outer surface of MWCNTs. Diffraction peaks corresponding to Fe3O4 cubic crystal also appeared in the X-ray diffraction spectra. Thermal conductivity of composites increases by filling the appropriate content of carbon tube. If the magnetic field is larger and the direction time is longer, a greater thermal conductivity of composites can be obtained.


---

## Body

## 1. Introduction

Carbon nanotubes (CNTs), a kind of typical one-dimensional nanocarbon materials with a seamless nanotube structure which seem to be curled up by a single layer or multilayer graphite flake, show a variety of excellent properties such as electrical, thermal, mechanical, and optical properties and have attracted much attention due to their outstanding properties and significant potential application in so many fields since Iijima’s observations in 1991 [1]. CNTs are becoming a focus and leading edge in the study of science and industry since Ajayan et al. [2] used the carbon nanotubes for reinforcing polymer composite. Therefore, many scholars have conducted a lot of research and exploration and have achieved gratifying results. However, these studies mainly focused on the resin, plastic, and other composite materials. The research on carbon nanotubes reinforced rubber composite mainly focused on mechanics, thermal stability, and conductive and electromagnetic work. The research on the performance of thermal conductivity of carbon nanotube filled rubber was even limited.Rubber is a typical viscoelastic polymer. Its thermal conductivity is very small (about 0.2 W/(m·K)) because of the existence of phonon scattering caused by the lattice defects and its chain segment non-free movement. However, CNTs make heat transfer come true mainly via the vibration of the phonon. So CNTs own a higher thermal conductivity as shown in the related articles; it was reported that the theoretical value of thermal conductivity of carbon nanotube is as high as 6600 W/(m·K) [3], and the experimental value can also achieve 3000 W/(m·K) [4]. Research on thermal conductivity of rubber filled with carbon nanotube has also made some achievements in recent years [5, 6]. But our team [7] found that although carbon nanotube owned excellent thermal conductivity itself, its ability of improving the rubber’s heat conduction was just limited. The reason mainly is that the thermal properties of carbon nanotube based composite material are very closely related to the distribution, structure characteristics of carbon nanotubes in the composite material, microscopic state, and the rule of heat transfer [8–12].Orientation distribution and different existing state have an obvious effect on formation of thermal conductive network chain structure, for carbon nanotubes, special thermal conductive materials, have the particularity of one-dimensional structure, compared with the other thermal conductive filler, which is bound to bring a greater impact on the performance of thermal conductivity of the composite. Marconnet et al. [13] found that the thermal conductivity of epoxy resin composites filled with 17% of orient carbon nanotubes increased by 18%. Park et al. [14] found that if carbon nanotubes in epoxy are oriented by mechanical method, the thermal conductivity of composites rises up to 100 W/(m·K), compared with epoxy resin composites with an arbitrarily arrangement for carbon nanotubes at room temperature, which owned a thermal conductivity of the 55 W/(m·K). Abdalla et al. [15] made carbon nanotubes aligned in the resin in a magnetic field and found that thermal conductivity of resin composites along the direction of carbon nanotubes orientation is much bigger than that in vertical directions. Haggenmueller et al. [16] studied the thermal conductivity of polyethylene composites filled with carbon nanotube and found that thermal conductivity was obviously increasing with the increase of orientation coefficient in the axial orientation.In this paper, magnetic nanocomposites formation of Fe3O4-CNTs is reported firstly, which was prepared by hydrothermal process, with multiwalled carbon nanotubes as the carrier. And the analysis of microstructure, magnetism of Fe3O4-CNTs, and homogeneity of Fe3O4 on CNTs surface are presented. Then, carbon nanotubes were made to be aligned in the nature rubber adopting a method of solution blending in a magnetic field [17], and the rubber was cross-linked at room temperature. Then NR polymer composites are presented; along with that was a study on microstructure of CNTs aligned in nature rubber and the relationship between magnetic field intensity, orientation time, and thermal conductivity of nature rubber composites.


## 2. Experimental

### 2.1. Materials

Materials are as follows: nature rubber (the total solids content of 61.5); multiwalled carbon nanotube (diameter: 20–40 nm; length: 5–15μm; specific surface area: 90–120 m2/g; Shenzhen port of nano Co., Ltd.); sodium dodecyl sulfate (SDS); FeCl3·6H2O; FeSO4·7H2O; toluene; potassium ethyl xanthate; zinc diethyl dithiocarbamate (ZDC); other rubber curing auxiliaries.


### 2.2. Fabrication of Fe3O4-CNTs

The pretreatment of the MWCNTs: the CNTs used in the experiment were prepared by chemical vapor deposition (CVD); a mixture of nanocarbon materials can be obtained from it, which contains large amounts of catalyst particles, amorphous carbon, nanocarbon particles, and other impurities. These impurities seriously affect the performance of carbon nanotubes and limit the application of carbon nanotubes. Therefore, raw carbon nanotubes need to be purified. Moreover, due to CNTs’ smooth surface, there is no bonded or noncovalent interactions between CNTs and Fe3O4. So it is quite necessary to make CNTs surface with enough charge groups. Now, 10 g original CNTs to 500 mL of concentrated sulfuric acid and nitric acid mixture (volume ratio 1 : 1) are added, and it was purified for 6 h at 60°C under ultrasonic processing, and then it is filtered and washed with deionized water again and again until neutral. And then it got dried in vacuum under 80°C.Preparation of magnetic nanocomposites CNTs-Fe3O4 [16]: 0.004 mol FeCl3·6H2O and 0.002 mol FeSO4·7H2O were added to 400 mL deionized water, as well as 1 g of purified CNTs, and then dispersed by ultrasound for 0.5 h at room temperature. Firstly, the mixture solution was stirred under nitrogen protection at 50°C for 0.5 h. Secondly, 6 mol/L NaOH solution was added to adjust the PH of mixture solution was alkaline at 65°C. After reacting for 1 h, 0.25 g sodium dodecyl sulfate (SDS) was added to the mixture solution at 85°C. Finally, the mixture solution was cooled to room temperature under stirring and then filtered to get sediment. The sediment was washed to neutral with deionized water. Fe3O4-CNTs magnetic composite materials were separated out using a magnet, dried in a vacuum oven, and then ground.


### 2.3. Fabrication of Fe3O4-CNTs/NR Composite

The formulation of NR composites used in experiments is shown in Table1. NR was dissolved in toluene solution, stirred and dispersed for 1 h. At the same time, Fe3O4/MWNTs were dispersed in toluene solution using ultrasonic dispersion machine for 1 h. In order to obtain well-mixed mixture, we mixed the two kinds of solution above for 2 h. The mixed solution of rubber additives was added to the mixed solution of NR and Fe3O4/MWNTs. Then we put the mixture in a culture dish and removed bubbles for 0.5 h under vacuum condition. Put the dish in a magnetic field for a certain period of time to make Fe3O4/MWNTs oriented (Figure 1).Table 1
Formula of Fe3O4-CNTs/NR composite.
Raw material
Mass fraction phr/g
NR
100
S
3
ZnO
3
ZDC
1
SA
2
RD
1
Potassium ethyl xanthate
1
Fe3O4-CNTs
VariableFigure 1
The orientation of MWNTs in NR in magnetic field.


## 2.1. Materials

Materials are as follows: nature rubber (the total solids content of 61.5); multiwalled carbon nanotube (diameter: 20–40 nm; length: 5–15μm; specific surface area: 90–120 m2/g; Shenzhen port of nano Co., Ltd.); sodium dodecyl sulfate (SDS); FeCl3·6H2O; FeSO4·7H2O; toluene; potassium ethyl xanthate; zinc diethyl dithiocarbamate (ZDC); other rubber curing auxiliaries.


## 2.2. Fabrication of Fe3O4-CNTs

The pretreatment of the MWCNTs: the CNTs used in the experiment were prepared by chemical vapor deposition (CVD); a mixture of nanocarbon materials can be obtained from it, which contains large amounts of catalyst particles, amorphous carbon, nanocarbon particles, and other impurities. These impurities seriously affect the performance of carbon nanotubes and limit the application of carbon nanotubes. Therefore, raw carbon nanotubes need to be purified. Moreover, due to CNTs’ smooth surface, there is no bonded or noncovalent interactions between CNTs and Fe3O4. So it is quite necessary to make CNTs surface with enough charge groups. Now, 10 g original CNTs to 500 mL of concentrated sulfuric acid and nitric acid mixture (volume ratio 1 : 1) are added, and it was purified for 6 h at 60°C under ultrasonic processing, and then it is filtered and washed with deionized water again and again until neutral. And then it got dried in vacuum under 80°C.Preparation of magnetic nanocomposites CNTs-Fe3O4 [16]: 0.004 mol FeCl3·6H2O and 0.002 mol FeSO4·7H2O were added to 400 mL deionized water, as well as 1 g of purified CNTs, and then dispersed by ultrasound for 0.5 h at room temperature. Firstly, the mixture solution was stirred under nitrogen protection at 50°C for 0.5 h. Secondly, 6 mol/L NaOH solution was added to adjust the PH of mixture solution was alkaline at 65°C. After reacting for 1 h, 0.25 g sodium dodecyl sulfate (SDS) was added to the mixture solution at 85°C. Finally, the mixture solution was cooled to room temperature under stirring and then filtered to get sediment. The sediment was washed to neutral with deionized water. Fe3O4-CNTs magnetic composite materials were separated out using a magnet, dried in a vacuum oven, and then ground.


## 2.3. Fabrication of Fe3O4-CNTs/NR Composite

The formulation of NR composites used in experiments is shown in Table1. NR was dissolved in toluene solution, stirred and dispersed for 1 h. At the same time, Fe3O4/MWNTs were dispersed in toluene solution using ultrasonic dispersion machine for 1 h. In order to obtain well-mixed mixture, we mixed the two kinds of solution above for 2 h. The mixed solution of rubber additives was added to the mixed solution of NR and Fe3O4/MWNTs. Then we put the mixture in a culture dish and removed bubbles for 0.5 h under vacuum condition. Put the dish in a magnetic field for a certain period of time to make Fe3O4/MWNTs oriented (Figure 1).Table 1
Formula of Fe3O4-CNTs/NR composite.
Raw material
Mass fraction phr/g
NR
100
S
3
ZnO
3
ZDC
1
SA
2
RD
1
Potassium ethyl xanthate
1
Fe3O4-CNTs
VariableFigure 1
The orientation of MWNTs in NR in magnetic field.


## 3. Results and Discussion

### 3.1. TEM Analysis of Fe3O4/MWNTs Composite Particles

Figure2 is O-MWNTs under optimum acidification condition and Fe3O4/MWNTs nanomagnetic composite particles prepared by chemical coprecipitation. Figure 2(a) shows that MWNTs were cut shorter, with their end caps open, while MWNTs’ surface became cleaner for amorphous carbon generated during their preparation and nanocarbon particles and other impurities have been cleared after the acid treatment. Those variations all provide skeleton for Fe3O4. The TEM image shows MWNTs being coated by Fe3O4 magnetic particles. It is clear that a large number of black particles of size about 20 nm are symmetrically coated on the outer surface of MWNTs. In the preparation and washing process, Fe3O4 particles are still relatively evenly adsorbed on the MWNTs surface without falling after a relatively long period of ultrasonic oscillation and mixing treatment. This indicates that a negative charge was produced on their surface by purified MWNTs, so that a certain degree of electrostatic attraction makes Fe3O4 particles firmly adsorbed on the surface of MWNTs.Figure 2
TEM images of O-MWNTs and Fe3O4/MWNTs: (a) O-MWNTs and (b) Fe3O4/MWNTs.
(a)
(b)


### 3.2. X-Ray Diffraction Spectra of MWNTs Coated by Fe3O4

Figure3 shows that the O-MWNTs are treated by mixed acid (a) and MWNTs coated with Fe3O4. Typical Bragg peaks appear at 2θ = 26.018° in curve (a), which also appear at curve (b) in the same position. But its strength is significantly less than O-MWNTs curve for the weaken role. Contrast JCPDS card (number 88-315) in 30.258°, 35.519°, 43.213°, 53.517°, 57.101°, and 62.770° at diffraction peaks corresponds to Fe3O4 cubic crystal (220), (311), (400), (422), (511), and (440), six crystal faces.Figure 3
X-ray diffraction spectra of O-MWNTs and Fe3O4/MWNTs.


### 3.3. Magnetic Analysis of Fe3O4/MWNTs

The left photo of Figure4 shows that magnetic nanocomposite particles Fe3O4/MWNTs are added to the water by ultrasonic vibration and evenly are dispersed. Then the right photo of Figure 4 is obtained by putting mixed solution in a magnetic field. It is found that Fe3O4/MWNTs composite particles quickly settled toward one side of beaker wall, which shows that MWNTs coated with Fe3O4 enhance magnetic itself.Figure 4
Photos of Fe3O4/MWNTs under a magnetic field.


### 3.4. SEM Analysis of NR Composites Filled with Aligned Fe3O4/MWNTs

As can be seen from Figure5, the probability of contact between Fe3O4 and MWNTs increases with the increasing filling fraction of particles and also promoted a more perfect thermal network chain. Fe3O4 particles in contact with each other on the surface of carbon tube serve as a bridge between MWNTs. The longer the time for orientation or the larger the magnetic field strength is, the greater the degree of orientation of Fe3O4/MWNTs can be obtained. The particles are arranged in parallel in the orientation direction which reduces thermal resistance. So the thermal conductivity of composites increases with directional time and magnetic field intensity (Figure 5).Figure 5
SEM images of NR composites: (a) 6% 0 B 0 h; (b) 10% 1 B 0 h; (c) 10% 1 B 2.5 h; (d) 10% 2 B 2.5 h.
(a)
(b)
(c)
(d)


### 3.5. Thermal Performance Analysis of NR Composites Filled with Fe3O4/MWNTs

The degree of orientation of Fe3O4/MWNTs in NR matrix increases, which is likely to lead to anisotropy of NR composites along the direction of magnetic field. NR composites obtain higher thermal conductivity and growth rate along orientation direction in strong magnetic field (B1 = 400 mT andB2 = 600 mT). Strong magnetic field works are done on Fe3O4/MWNTs, which is attributed to high anisotropic degree of NR composites (Figure 6).Figure 6
Effect of orientation time and magnetic intensity on thermal conductivity of composite (volume fraction = 6%, at 80°C test temperature).We get curves of thermal conductivity of NR composite under different magnetic field intensity at 1.5 hours. With the increase of Fe3O4/MWNTs filling fraction, thermal conductivity of NR composites increases gradually and strong magnetic field (B2) has greater effect on improving thermal conductivity. Thermal conductivity of composites is better inB2 because of higher orientation degree of Fe3O4/MWNTs (Figure 7).Figure 7
Impact of volume fraction on thermal conductivity of Fe3O4/MWNTs/NR composite (at 80°C test temperature).


## 3.1. TEM Analysis of Fe3O4/MWNTs Composite Particles

Figure2 is O-MWNTs under optimum acidification condition and Fe3O4/MWNTs nanomagnetic composite particles prepared by chemical coprecipitation. Figure 2(a) shows that MWNTs were cut shorter, with their end caps open, while MWNTs’ surface became cleaner for amorphous carbon generated during their preparation and nanocarbon particles and other impurities have been cleared after the acid treatment. Those variations all provide skeleton for Fe3O4. The TEM image shows MWNTs being coated by Fe3O4 magnetic particles. It is clear that a large number of black particles of size about 20 nm are symmetrically coated on the outer surface of MWNTs. In the preparation and washing process, Fe3O4 particles are still relatively evenly adsorbed on the MWNTs surface without falling after a relatively long period of ultrasonic oscillation and mixing treatment. This indicates that a negative charge was produced on their surface by purified MWNTs, so that a certain degree of electrostatic attraction makes Fe3O4 particles firmly adsorbed on the surface of MWNTs.Figure 2
TEM images of O-MWNTs and Fe3O4/MWNTs: (a) O-MWNTs and (b) Fe3O4/MWNTs.
(a)
(b)


## 3.2. X-Ray Diffraction Spectra of MWNTs Coated by Fe3O4

Figure3 shows that the O-MWNTs are treated by mixed acid (a) and MWNTs coated with Fe3O4. Typical Bragg peaks appear at 2θ = 26.018° in curve (a), which also appear at curve (b) in the same position. But its strength is significantly less than O-MWNTs curve for the weaken role. Contrast JCPDS card (number 88-315) in 30.258°, 35.519°, 43.213°, 53.517°, 57.101°, and 62.770° at diffraction peaks corresponds to Fe3O4 cubic crystal (220), (311), (400), (422), (511), and (440), six crystal faces.Figure 3
X-ray diffraction spectra of O-MWNTs and Fe3O4/MWNTs.


## 3.3. Magnetic Analysis of Fe3O4/MWNTs

The left photo of Figure4 shows that magnetic nanocomposite particles Fe3O4/MWNTs are added to the water by ultrasonic vibration and evenly are dispersed. Then the right photo of Figure 4 is obtained by putting mixed solution in a magnetic field. It is found that Fe3O4/MWNTs composite particles quickly settled toward one side of beaker wall, which shows that MWNTs coated with Fe3O4 enhance magnetic itself.Figure 4
Photos of Fe3O4/MWNTs under a magnetic field.


## 3.4. SEM Analysis of NR Composites Filled with Aligned Fe3O4/MWNTs

As can be seen from Figure5, the probability of contact between Fe3O4 and MWNTs increases with the increasing filling fraction of particles and also promoted a more perfect thermal network chain. Fe3O4 particles in contact with each other on the surface of carbon tube serve as a bridge between MWNTs. The longer the time for orientation or the larger the magnetic field strength is, the greater the degree of orientation of Fe3O4/MWNTs can be obtained. The particles are arranged in parallel in the orientation direction which reduces thermal resistance. So the thermal conductivity of composites increases with directional time and magnetic field intensity (Figure 5).Figure 5
SEM images of NR composites: (a) 6% 0 B 0 h; (b) 10% 1 B 0 h; (c) 10% 1 B 2.5 h; (d) 10% 2 B 2.5 h.
(a)
(b)
(c)
(d)


## 3.5. Thermal Performance Analysis of NR Composites Filled with Fe3O4/MWNTs

The degree of orientation of Fe3O4/MWNTs in NR matrix increases, which is likely to lead to anisotropy of NR composites along the direction of magnetic field. NR composites obtain higher thermal conductivity and growth rate along orientation direction in strong magnetic field (B1 = 400 mT andB2 = 600 mT). Strong magnetic field works are done on Fe3O4/MWNTs, which is attributed to high anisotropic degree of NR composites (Figure 6).Figure 6
Effect of orientation time and magnetic intensity on thermal conductivity of composite (volume fraction = 6%, at 80°C test temperature).We get curves of thermal conductivity of NR composite under different magnetic field intensity at 1.5 hours. With the increase of Fe3O4/MWNTs filling fraction, thermal conductivity of NR composites increases gradually and strong magnetic field (B2) has greater effect on improving thermal conductivity. Thermal conductivity of composites is better inB2 because of higher orientation degree of Fe3O4/MWNTs (Figure 7).Figure 7
Impact of volume fraction on thermal conductivity of Fe3O4/MWNTs/NR composite (at 80°C test temperature).


## 4. Conclusions

(1)
TEM shows that Fe3O4 is uniformly coated on the outer surface of MWNTs. Diffraction peaks corresponding to Fe3O4 cubic crystal also appeared in the X-ray diffraction spectra.
(2)
In the absence of magnetic field, thermal conductivity of composites with different Fe3O4/MWNTs content increases, followed with test temperature. As the amount of fillers increases, the formation of heat transfer network chain becomes more and more perfect, in which attribute composites have higher thermal conductivity.
(3)
Thermal conductivity of composites increases by filling the appropriate modification of carbon tube. If the magnetic field is larger and the direction time is longer, the thermal conductivity of composites is greater.



---