# Enhanced Photocatalytic Activity for Degradation of Methyl Orange over Silica-Titania

Authors: Yaping Guo; Shaogui  Yang; Xuefei Zhou; Chunmian Lin; Yajun Wang; Weifeng Zhang
Journal: Journal of Nanomaterials
 (2011)

---

## Abstract

Silica-modified titania (SMT) powders with different atomic ratios of silica to titanium (Rx) were successfully synthesized by a simple ultrasonic irradiation technique. The prepared samples were characterized by X-ray diffraction (XRD), FT-IR spectroscopy, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and ultraviolet visible spectroscopy. The specific surface area was measured according to BET theory. Results indicate that the addition of silica to titania can suppress the crystalline size growth and the transformation of anatase phase to rutile phase of titania, enlarge specific surface area of the titania particles, and result in a blue shift of absorption edge compared to pure titania. The photocatalytic activity of the SMT samples was evaluated by decolorizing methyl orange aqueous solutions under UV-visible light irradiation. It was found in our study that this activity was affected by silica content, calcination temperature, H2SO4, and oxidants such as KIO4, (NH4)2S2O8 and H2O2. The results reveal that the photocatalytic activity of 0.1-SMT catalyst is the best among all samples calcined at 550°C for 1 h and it is 1.56 times higher than that of Degussa P-25 titania, which is a widely used commercial TiO2 made by Germany Degussa company and has been most widely used in industry as photocatalyst, antiultraviolet product, and thermal stabilizer. The optimal calcination temperature for preparation was 550°C. The photocatalytic activity of SMT samples is significantly enhanced by H2SO4 solution treatment and oxidants.


---

## Body

## 1. Introduction

As a cost-effective, nontoxic, effective photocatalyst, nanosize TiO2 has received much attention during the past three decades. In its practical application, it is very important to improve the efficiency of titania-based photocatalysts because titania usually has a small surface area and pore volume, which leads to its low adsorption of organic pollutants. Therefore, the enlargement of specific surface area and adsorption capability is desirable for titania photocatalyst.Generally speaking, two strategies have been developed to solve the problem. One is the synthesis of malodorous titania with high specific surface area resulting in high adsorbability and photocatalytic activity [1], the other is the combination of titania materials with adsorbent [2]. For the former strategy, titania mostly exists in an amorphous or semicrystalline phase so it has low photocatalytic activity. It has been proven that the later method is relatively easy to prepare. As an adsorbent and stabilizer, silica is the best candidate as it not only possesses a large specific surface area, but also has no absorption in UV region. Titania-silica mixed oxide has attracted considerable attention as attractive materials for photocatalytic applications because of the synergetic function of the photocatalytic activity, adsorbability, and stability.  This may be partially the intimate interaction of titanium dioxide and silica, the new different structural characteristics and physicochemical/reactivity properties of titania-silica complex, such as quantum-sized crystalline, large surface area, high thermal stability, high adsorbability of reactant, or high acidity [3, 4]. Most of studies for titania-silica were concentrated on the structure type of titania supported on silica or titanium silicate series [5–8], the application of waste air purification [9] and wastewater treatment [10]. However, few studies on wastewater treatment with titania-silica have been reported.The purpose of the paper is to explore SMT with high photoactivity for purifying the water. Methyl orange was chosen as a probe for its relatively high reactivity and high stability. We also found that the photocatalytic activity of the prepared SMT could be greatly improved by H2SO4 solution treatment. Explanations are provided based on the influence of sulfuric acid treatment on photocatalytic activity.


## 2. Materials and Methods

### 2.1. Materials

Tetraethylorthosilicate (TEOS), tetrabutylorthotitanate (TBOT), methyl orange, sulfuric acid, KIO4, (NH4)2S2O8, and H2O2 were from Shanghai Chemical Company at analytic purity.


### 2.2. Methods

#### 2.2.1. Preparation of Silica-Modified Titania (SMT) and Surface Acid Treatment

Nanocrystalline Titania powders were prepared by hydrolysis under ultrasonic irradiation [11, 12]. Tetrabutylorthotitanate (TBOT) was used as a titanium source. Tetraethylorthosilicate (TEOS) was used as a precursor of the dopant. The mixture of TBOT (0.1125 mol) and TEOS was directly added dropwise to distilled water (900 mL) under vigorous stirring at room temperature. The atomic ratios of silica to titanium, which hereafter was designated as Rx, were 0, 0.05, 0.1, and 0.2, respectively. The samples were then irradiated with an ultrasonic cleaning bath (KQ3200E, 40 kHz, 150 W) for 1 h, followed by aging in a closed beaker at room temperature for 24 h. After aging, these samples were dried at 100°C for about 8 h in air in order to vaporize water in the gels and then ground to fine powders to obtain dry gel samples. The dried gel samples were calcined at different temperature in air for 1 h.To enhance the photocatalytic activity of the powders, we dipped the SMT in 1 mol·L−1 H2SO4 aqueous solutions at room temperature. After 20 mins, the samples were withdrawn from the H2SO4 solutions. They were carefully rinsed with deionized water and dried at 100°C for 2 h in an oven in air.


#### 2.2.2. Characterization

XRD patterns were made using a X′TRA diffractometer (made in ARL Company in Swiss) with Cu Kα radiation over the scan range 20–60°C for wide angle XRD. The average crystalline size of powders was estimated by the Scherrer formula [13]: D=0.89λ/βcosč (where D is the crystallite size, λ is the wavelength of the X-ray radiation (CuKα=0.15418nm), K is usually taken as 0.89, and β is the line width at half-maximum height, after subtraction of equipment broadening). The FT-IR spectra were recorded by a NEXUS 870 FT-IR, made in U.S. NICOLET  Company in a wavenumber range of 4000–400 cm−1. UV-V is spectroscopic analysis that was performed by using a spectrophotometer (SHIMADZU UV-2401). X-ray photoelectron spectroscopy (XPS) measurements were   done with an ESC ALB MK-II XPS System with a monochromatic Al KR source and a charge neutralizer. Measurement of BET (BET aims to explain the physical adsorption of gas molecules on a solid surface and serves as the basis for an important analysis technique for the measurement of the specific surface area of a material. In 1938, Stephen Brunauer, Paul Hugh Emmett, and Edward Teller published an article about the BET theory in a journal for the first time; “BET” consists of the first initials of their family names [12], surface area was performed using N2 adsorption/desorption isotherms on a Micromeritics ASAP 2020.


#### 2.2.3. Photocatalytic Activity of Silica-Modified Titania (SMT)

The photocatalytic activity of prepared SMT powders for decomposition of methyl orange was investigated as shown in Figure1. The photocatalytic reactor has an  effective volume of 150 ml. The experiment was performed in the following condition: UV irradiation (a 400 W high-pressure mercury lamp from factory of Beijing light with a maximum wavelength of 365 nm, Io =1.50 mW/cm2), vigorous stirring, no airflow. The initial concentration of methyl orange was 20 mg·L−1 and Rx-SMT powders were kept 1.0 g/L in all cases.Figure 1
Photoreactor system for methyl orange degradation. (1) Cooling water input, (2) water outflow, (3) UV lamp, (4) Quartz sleeve, (5) Stirrer bar, (6) reactant solution, (7) exhaust, and (8) glass reactor.Degussa P25 titania particles (50 m2/g) with crystalline structure of ca. 20% rutile and 80% anatase and primary particle size of ca. 21 nm was taken as a reference to test the photoactivity of the Rx-SMT powders towards the degradation of methyl orange.The concentration of methyl orange was determined using UV-1600 spectroscopy at wavelength ë = 440 nm quantitatively. Total organic carbon (TOC) was determined with Shimadzu TOC-5000 analyzer.


## 2.1. Materials

Tetraethylorthosilicate (TEOS), tetrabutylorthotitanate (TBOT), methyl orange, sulfuric acid, KIO4, (NH4)2S2O8, and H2O2 were from Shanghai Chemical Company at analytic purity.


## 2.2. Methods

### 2.2.1. Preparation of Silica-Modified Titania (SMT) and Surface Acid Treatment

Nanocrystalline Titania powders were prepared by hydrolysis under ultrasonic irradiation [11, 12]. Tetrabutylorthotitanate (TBOT) was used as a titanium source. Tetraethylorthosilicate (TEOS) was used as a precursor of the dopant. The mixture of TBOT (0.1125 mol) and TEOS was directly added dropwise to distilled water (900 mL) under vigorous stirring at room temperature. The atomic ratios of silica to titanium, which hereafter was designated as Rx, were 0, 0.05, 0.1, and 0.2, respectively. The samples were then irradiated with an ultrasonic cleaning bath (KQ3200E, 40 kHz, 150 W) for 1 h, followed by aging in a closed beaker at room temperature for 24 h. After aging, these samples were dried at 100°C for about 8 h in air in order to vaporize water in the gels and then ground to fine powders to obtain dry gel samples. The dried gel samples were calcined at different temperature in air for 1 h.To enhance the photocatalytic activity of the powders, we dipped the SMT in 1 mol·L−1 H2SO4 aqueous solutions at room temperature. After 20 mins, the samples were withdrawn from the H2SO4 solutions. They were carefully rinsed with deionized water and dried at 100°C for 2 h in an oven in air.


### 2.2.2. Characterization

XRD patterns were made using a X′TRA diffractometer (made in ARL Company in Swiss) with Cu Kα radiation over the scan range 20–60°C for wide angle XRD. The average crystalline size of powders was estimated by the Scherrer formula [13]: D=0.89λ/βcosč (where D is the crystallite size, λ is the wavelength of the X-ray radiation (CuKα=0.15418nm), K is usually taken as 0.89, and β is the line width at half-maximum height, after subtraction of equipment broadening). The FT-IR spectra were recorded by a NEXUS 870 FT-IR, made in U.S. NICOLET  Company in a wavenumber range of 4000–400 cm−1. UV-V is spectroscopic analysis that was performed by using a spectrophotometer (SHIMADZU UV-2401). X-ray photoelectron spectroscopy (XPS) measurements were   done with an ESC ALB MK-II XPS System with a monochromatic Al KR source and a charge neutralizer. Measurement of BET (BET aims to explain the physical adsorption of gas molecules on a solid surface and serves as the basis for an important analysis technique for the measurement of the specific surface area of a material. In 1938, Stephen Brunauer, Paul Hugh Emmett, and Edward Teller published an article about the BET theory in a journal for the first time; “BET” consists of the first initials of their family names [12], surface area was performed using N2 adsorption/desorption isotherms on a Micromeritics ASAP 2020.


### 2.2.3. Photocatalytic Activity of Silica-Modified Titania (SMT)

The photocatalytic activity of prepared SMT powders for decomposition of methyl orange was investigated as shown in Figure1. The photocatalytic reactor has an  effective volume of 150 ml. The experiment was performed in the following condition: UV irradiation (a 400 W high-pressure mercury lamp from factory of Beijing light with a maximum wavelength of 365 nm, Io =1.50 mW/cm2), vigorous stirring, no airflow. The initial concentration of methyl orange was 20 mg·L−1 and Rx-SMT powders were kept 1.0 g/L in all cases.Figure 1
Photoreactor system for methyl orange degradation. (1) Cooling water input, (2) water outflow, (3) UV lamp, (4) Quartz sleeve, (5) Stirrer bar, (6) reactant solution, (7) exhaust, and (8) glass reactor.Degussa P25 titania particles (50 m2/g) with crystalline structure of ca. 20% rutile and 80% anatase and primary particle size of ca. 21 nm was taken as a reference to test the photoactivity of the Rx-SMT powders towards the degradation of methyl orange.The concentration of methyl orange was determined using UV-1600 spectroscopy at wavelength ë = 440 nm quantitatively. Total organic carbon (TOC) was determined with Shimadzu TOC-5000 analyzer.


## 2.2.1. Preparation of Silica-Modified Titania (SMT) and Surface Acid Treatment

Nanocrystalline Titania powders were prepared by hydrolysis under ultrasonic irradiation [11, 12]. Tetrabutylorthotitanate (TBOT) was used as a titanium source. Tetraethylorthosilicate (TEOS) was used as a precursor of the dopant. The mixture of TBOT (0.1125 mol) and TEOS was directly added dropwise to distilled water (900 mL) under vigorous stirring at room temperature. The atomic ratios of silica to titanium, which hereafter was designated as Rx, were 0, 0.05, 0.1, and 0.2, respectively. The samples were then irradiated with an ultrasonic cleaning bath (KQ3200E, 40 kHz, 150 W) for 1 h, followed by aging in a closed beaker at room temperature for 24 h. After aging, these samples were dried at 100°C for about 8 h in air in order to vaporize water in the gels and then ground to fine powders to obtain dry gel samples. The dried gel samples were calcined at different temperature in air for 1 h.To enhance the photocatalytic activity of the powders, we dipped the SMT in 1 mol·L−1 H2SO4 aqueous solutions at room temperature. After 20 mins, the samples were withdrawn from the H2SO4 solutions. They were carefully rinsed with deionized water and dried at 100°C for 2 h in an oven in air.


## 2.2.2. Characterization

XRD patterns were made using a X′TRA diffractometer (made in ARL Company in Swiss) with Cu Kα radiation over the scan range 20–60°C for wide angle XRD. The average crystalline size of powders was estimated by the Scherrer formula [13]: D=0.89λ/βcosč (where D is the crystallite size, λ is the wavelength of the X-ray radiation (CuKα=0.15418nm), K is usually taken as 0.89, and β is the line width at half-maximum height, after subtraction of equipment broadening). The FT-IR spectra were recorded by a NEXUS 870 FT-IR, made in U.S. NICOLET  Company in a wavenumber range of 4000–400 cm−1. UV-V is spectroscopic analysis that was performed by using a spectrophotometer (SHIMADZU UV-2401). X-ray photoelectron spectroscopy (XPS) measurements were   done with an ESC ALB MK-II XPS System with a monochromatic Al KR source and a charge neutralizer. Measurement of BET (BET aims to explain the physical adsorption of gas molecules on a solid surface and serves as the basis for an important analysis technique for the measurement of the specific surface area of a material. In 1938, Stephen Brunauer, Paul Hugh Emmett, and Edward Teller published an article about the BET theory in a journal for the first time; “BET” consists of the first initials of their family names [12], surface area was performed using N2 adsorption/desorption isotherms on a Micromeritics ASAP 2020.


## 2.2.3. Photocatalytic Activity of Silica-Modified Titania (SMT)

The photocatalytic activity of prepared SMT powders for decomposition of methyl orange was investigated as shown in Figure1. The photocatalytic reactor has an  effective volume of 150 ml. The experiment was performed in the following condition: UV irradiation (a 400 W high-pressure mercury lamp from factory of Beijing light with a maximum wavelength of 365 nm, Io =1.50 mW/cm2), vigorous stirring, no airflow. The initial concentration of methyl orange was 20 mg·L−1 and Rx-SMT powders were kept 1.0 g/L in all cases.Figure 1
Photoreactor system for methyl orange degradation. (1) Cooling water input, (2) water outflow, (3) UV lamp, (4) Quartz sleeve, (5) Stirrer bar, (6) reactant solution, (7) exhaust, and (8) glass reactor.Degussa P25 titania particles (50 m2/g) with crystalline structure of ca. 20% rutile and 80% anatase and primary particle size of ca. 21 nm was taken as a reference to test the photoactivity of the Rx-SMT powders towards the degradation of methyl orange.The concentration of methyl orange was determined using UV-1600 spectroscopy at wavelength ë = 440 nm quantitatively. Total organic carbon (TOC) was determined with Shimadzu TOC-5000 analyzer.


## 3. Results and Discussion

### 3.1. Crystal Structure and TEM Photomicrography

XRD was used to investigate the changes of crystalline phase of the SMT gel powders before and after heat treatment. Figure2 shows the effects of silica on phase structures of the TiO2 powders dried at 100°C for 8 h. The anatase phase is dominant in the as-prepared TiO2 sample, but there is a small amount of   brookite in it. The weak peak  at 2č = 30.7° corresponds to the brookite phase of titania. When Rx > 0.1, the intensities of brookite peaks steadily become weaker and finally disappear. This is probably due to the fact that silica suppresses the crystallization of brookite by adsorbing onto the surfaces of TiO2 particles. Similar result has been observed with F ion doping [14].Figure 2
XRD patterns of the Rx-SMT xerogel powders (Rx = 0, 0.05, 0.1, and 0.2) and dried at 100°C for 8 h.Figure3 shows the effects of silica content on the phase structures of Rx-SMT powders calcined at 550°C. For pure titania (Rx = 0), significant peaks of rutile phase are observed obviously. The dominant phase of titania (Rx > 0) is anatase when some portion of silica is embedded into titania particles. Apart from the diffraction peaks corresponding to anatase, there are no other diffraction peaks from 2č = 20–60 degree for all SMT samples (except for pure titania) as shown in Figure 3, indicating that silica exists in an amorphous phase. The average size of anatase titania from Scherrer formula was presented in Table 1. The result shows that the crystallite size decreased sharply with increasing the doping silica content up to 0.05. When the silica content was over 0.05, there was no significant change in the crystallite size of SMT particles. This result confirms that the embedding of some portion of silica into titania particle inhibits the growth of anatase crystal of titania particles [15].Table 1
Textural properties of the Rx-SMT powders prepared at 550°C for 1 h.
SamplesSi/Ti molecular ratio by XPSSurface area (m2·g−1)Average size (nm)0-SMT02050.50.05-SMT0.0531608.90.1-SMT0.0941967.20.1-SMT treated by H2SO4 solution0.0931957.20.2-Silica titania0.2062086.9Figure 3
XRD patterns of  Rx-SMT powders (Rx = 0, 0.05, 0.1, and 0.2) calcined at 550°C for 1 h.Figure4 shows the effects of calcination temperature on phase structures of 0.1-SMT powders. It can be seen that the peak intensities of anatase increase and the width of the (101) plane diffraction peak of anatase (2θ= 25.4°) becomes narrower with increasing calcination temperature (from 100 to 750°C). It has been reported that anatase-type TiO2 changes to rutile-type structure by heat treatment above 635°C from the results of a kinetic study on the anatase-to-rutile phase transformation [13].  At 750°C, anatase is a main phase and a small amount of rutile phase is detected, while the phase of pure titania calcained at 550°C was dominant rutile phase. The resulting SMT powders contain only anatase phase in the calcination temperature range of 100–650°C. Accordingly, SMT samples show high thermal stability and the presence of silica seems to be critical for the stabilization of the anatase phase. The presence of silicon atoms in the anatase matrix retards the change of face-centered cubic arrangement of oxide ion in anatase into hexagonal packing in rutile because this change is associated with the cleavage of a part of Ti-O bonds [9]. The decrease of the surface energy caused by substitution of the surface OH groups with oxide ions also contributes to the thermal stability of the present products [15]. The average sizes at different temperatures were calculated, which corresponded to 1.4, 4.6, 10.1, and 28.8 nm for 100, 450, 650, and 750°C, respectively. At temperatures lower than 650°C, anatase phases are present in relatively small grain sizes. However, at 750°C (Rx = 0.1), anatase and rutile phases are both present and the grains of various phases grow dramatically. This is attributable to the fact that the phase transitions accelerate the process of grain growth by providing the heat of phase transformation [16]. The XRD results revealed that the heat treatment induced the increase of crystalline size and phase transformation.Figure 4
XRD patterns of 0.1-SMT powders calcined at (a) 100, (b) 450, (c) 650, and (d) 700°C for 1 h.Figure5 shows TEM photographs of 0.1-SMT powders calcined at 550°C for 1 h. It can be seen that the dispersion property of the sample is good. Table 1 indicates that specific surface area of the samples increase with the increase of the silica content. This result confirms that the suitable addition of silica into titania matrix helps to suppress the reduction of surface area at high calcination temperature. It is well noted that the specific surface areas of 0.1-SMT (196 m2/g) and 0.1-SMT after H2SO4 solution treatment (195 m2/g) are not significantly different.Figure 5
TEM image of 0.1-SMT prepared by ultrasonic irradiation hydrolysis and claniced at 550°C.


### 3.2. FT-IR Spectroscopy

FT-IR spectra of Rx-SMT calcined at 550°C for 1 h are presented in Figure6. The peak around 1090 cm−1 attributed to the asymmetric stretching vibrations of Si–O–Si band [17], and the Ti–O–Si linkage stretching band appears at about 962 cm−1 [18]. When the ratio of silicon to titanium was over 0.1, the distinct band for Ti–O–Si vibration (962 cm−1) was observed. The existence of Si–O–Ti bond in FT-IR analysis may be attributed to the existence of covalent bond between amorphous SiO2 and crystalline TiO2. The band for the asymmetric Si–O–Si stretching vibration was observed for all composite samples, and its intensity was increased with increasing the silicon content. The presence of Si–O–Si bond in FT-IR is caused by the formation of SiO2 in the samples, which is in agreement with the reported result [19]. Besides, Ti–O–Ti bond may be present in the range of 400 to 600 cm−1 [20] for all samples. From these results of FT-IR, it is clear that the silica exists as segregated amorphous phase in the anatase titania powders and some metal–O–metal bonding of Ti–O–Si, which result from formation of a new ternary amorphous SixTiyOz phase as there is no match in the XRD analysis and/or existence of covalent bond between amorphous SiO2 and crystalline TiO2.Figure 6
FT-IR spectra of Rx-SMT powders calcined at 550°C for 1 h.The peak around 1650 cm−1 is due to the bending vibration of O–H bond, which is assigned to the chemisorbed water, and the peak around 3460 cm−1 is assigned to the stretching mode of O–H bond and related to free water [21]. This water band was increased with increasing the ratio of silica to titanium. This is due to the fact that silica has the capability to absorb water in air [22]. In addition, when titania was embedded with silica, crystallite growth was suppressed and the surface area was kept larger (as shown in Table 1), and in this case, the capability to hold absorbed water became larger.FT-IR spectra of Rx-SMT after H2SO4 treatment were presented in Figure 7. The peak corresponding to 1244 cm−1 is the stretching frequency of S=O, and the peaks corresponding to 1159 and 1078 cm−1 are the characteristic frequencies of SO42-, which indicated the chelatometric coordinated adsorption of SO42- on SMT. The sulfate ion, both in surface and bulk, creates high surface acidity to improve the photocatalytic activity [23].Figure 7
FTIR spectra of Rx-SMT powders treated by 1M H2SO4 solution. Rx = 0.05, 0.1, and 0.2.


### 3.3. XPS Studies

Figure8 shows the XPS spectrum of 0.1-SMT powders  heat-treated at 550°C for 1 h and 0.1-SMT treated by 1 M H2SO4 solution. XPS peaks show that the 0.1-SMT powders contain nly Ti, O, Si, and a trace amount of carbon. The following binding energies are used in our quantitative measurements: Ti 2p at 460.10 eV, O 1 s at 531.35 eV, Si 2p at 103.8 eV, and  C 1 s at 286.20 eV. The atomic ratio of Ti : O : Si is about 1 : 2.13 : 0.13, which is higher than the nominal atomic composition of TiO2, indicating that silica atoms are partially concentrated on the surface region of the titania particles [7]. The C element is ascribed to the residual carbon from precursor solution and the adventitious hydrocarbon from the XPS instrument itself. It is easily observed that 0.1-SMT treated by 1 M H2SO4 solution contains Ti, O, Si, S, and a trace amount of carbon. The binding energies of Ti 2p, O 1 s, Si, S, and C 1 s are 460.70, 531.9, 105, 171.1, and 286.45 eV, respectively. It is easily noted from the figure that the binding energy of Ti2p in 0.1-SMT after H2SO4 treatment is higher than that of 0.1-SMT before H2SO4 treatment; the higher binding energy is helpful to improve its photocatalytic activity.Figure 8
XPS spectra of 0.1-SMT calcined at 550°C for 1 h and 0.1-SMT treated by H2SO4 solution.


### 3.4. UV-Vis Spectra

As a photocatalyst, the wavelength distribution of the absorbed light is one of the important properties regardless of the quantum yield. Figure9 shows the UV-Vis diffuse reflectance spectra (UV/Vis DRS) of prepared powders with the different silica content. Absorption edge of rutile (Rx = 0) is found to be at the shorter wavelength than that of anatase. Compared Rx-SMT samples with pure titania sample, the absorption spectrum of the Rx-SMT samples show a stronger absorption in the UV-visible range and a blue shift in the band gap absorption edge was observed in all SMT samples. The blue shift of absorption of a photocatalyst means that the photocatalyst has a greater oxidation-reduction potential and enhance the absorption, which will improve its photocatalytic activity [24].Figure 9
UV-Vis spectra of Rx-SMT with different Si/Ti ratios. Rx = 0, 0.05, 0.1, and 0.2.The energy band gap of prepared samples could be estimated from a plot of (αhγ) 1/2 versus photon energy (hγ). The intercept of the tangent to the plot will give a good estimation of the band gap energy for indirect band gap materials such as TiO2  [25, 26]. The absorption coefficient α can be calculated from the measured absorbance (A) using the following equation:
(1)α=2.303ρ103lcMA,
where the densityρ=3.9g cm−3, molecular weight M=79.9 g mol−1, c is the molar concentration of TiO2, and l is the optical path length.The calculated band gap energies of all silica-modified samples with different Rx values (0, 0.05, 0.1, and 0.2) are about 2.97 eV, 3.29, 3.31, and 3.34 eV, respectively. The above results imply that the absorption edge was clearly shifted toward shorter wavelengths for all SMT samples.


### 3.5. Photocatalytic Activity

As the photocatalytic mechanism suggests, both photocatalysts and a light source are necessary for the photo-oxidation reaction to occur [6]. A control experiment was conducted on three different conditions: (i) in the dark in presence of 0.1-SMT, (ii) only UV irradiation without photocatalyst, and (iii) under UV illumination in presence of 0.1-SMT. In all above conditions, the initial concentration of Methyl orange is 20 mg/L.  In Figure 1, the concentration of MO is plotted as a function of reaction time.As can be seen in Figure10, in the dark, 0.9% of the initial substrate disappeared after 1 h of continuous stirring due to the adsorption phenomena. Over this time, abatement of 5.4% after 1.5 h was detected. In direct photolysis, about 8% disappearing efficiency was observed during the 1 h irradiation; and 17% of the initial methyl orange disappeared after 1.5 h. When aqueous 0.1-SMT suspension was exposed to UV light, the concentration of MO decrease markedly. About 68–82% of methyl orange was bleached within 40–60 mins of time experiment, respectively. It can be clearly seen from Figure 10 that 93.5% of methyl orange in aqueous solution was photocatalytically degraded, and its corresponding mineralization efficiency was only 33%. It indicated that the complete mineralization of Methyl orange took more time than degradation.Figure 10
The variation of MO and TOC concentrations by photocatalytic technology with 0.1-SMT; (a) MO-dark experiment; (b) MO-direct photolysis; (c) TOC-photocatalysis; (d) MO-photocatalysis.The photocatalytic activity of Rx-SMT powders is affected by various factors, such as the doping silica content, calcined temperature, and sulfuric acid treatment.


### 3.6. Doping Silica Content

The photocatalytic activity of the prepared SMT powders for the decomposition of methyl orange was investigated as a function of silica content. The photocatalytic degradation follows pseudo first-order kinetics. The results are presented in Figure11 and Table 2. It is clearly seen that the photocatalytic degradation rate of methyl orange firstly increased with increasing the silica content when the range of silica content was from 0 to 0.1, it may be due to the decrease of average sizes as shown in the XRD analysis in Figure 3 and the increase of surface hydroxyl group as shown in the analysis of FT-IR in Figure 4. However, higher silica content (>0.1) did not favor the further enhancement of the photoactivity of SMT powders because the crystallinity of anatase decreased in spite of the larger specific surface area (Table 2), and SiO2 did not exhibit photocatalytic activity. It should be noted that the photocatalytic activity of 0.1-SMT is the best among all the samples and it was about 1.56 times of that of Degussa P25 titania, which is recognized as an excellent photocatalyst [27]. The difference in both of specific surface area and anatase crystallites is responsible for this discrepancy of Rx-SMT photoactivity and the surface area of Rx-SMT samples were presented in Table 1. Moreover, another reason on enhancement of SMT is ultrasonic irradiation in the preparation of samples; ultrasonic irradiation enhances hydrolysis of titanium and silicon alkoxide, and crystallization of the gel, because ultrasonic cavitation creates a unique environment for hydrolysis of titanium and silicon alkoxide. The similar result has been observed in formaldehyde degradation in silica titania system, which was reported [9].Table 2
The kinetics constants and regression coefficients of methyl orange photocatalysis on Rx-SMT and Degussa P-25 titania.
PhotocatalystKinetic constant (min−1)r2Ratio ofK to KP25Rx = 0K0=0.00150.93980.0789Rx = 0.05K1=0.02340.99491.2316Rx = 0.1K2=0.02960.99521.5579Rx = 0.2K3=0.01490.99560.7842Degussa P-25 titaniaKP25=0.0190.99771Figure 11
Concentration changes of methyl orange versus UV irradiation time with Rx-SMT photocatalysts calcined at 550°C for 1 h.It can be seen from Figure11 and Table 2 that pure titania (Rx = 0) shows very poor photocatalytic activity, compared to other samples. This can be easily explained that the sample was mainly composed of rutile phase with poor photocatalytic activity and has low specific surface area.


### 3.7. Calcined Temperature

It is well known that calcination is a common treatment that can be used to enhance the photoactivity of nanosized photocatalysts [27]. The photocatalytic activity of the prepared 0.1-SMT powders for the decomposition of methyl orange was investigated as a function of calcination temperature and the result was shown in Figure 12. The 0.1-SMT sample calcined at 100°C shows good photocatalytic activity with a reaction rate constant of 7.9 × 10−3 min−1. The reaction rate constant increases with increasing calcination temperature. Enhancing the photocatalytic activity at elevated temperatures can be ascribed to an obvious improvement in the crystallinity of anatase (as shown in Figure 4). At 550°C, the reaction rate constant k reaches the highest value of 2.96 ×10−2 min−1 and it is obviously higher than that of Degussa P-25 titania  (k=1.9×10-2 min−1). The high photocatalytic activity of the sample calcined 550°C is partially due to its large surface area and small crystallite size. Moreover, both of the intense absorption in the UV-visible range and a blue shift in the band gap transition of the SMT samples indicate that more powerful photogenerated holes and electrons can participate in the photocatalytic reactions. Calcination temperatures well above 550°C are not desirable. Samples calcined at 750°C display relatively poor photocatalytic activity.Figure 12
Concentration changes of methyl orange versus UV irradiation time with 0.1-SMT powders calcined at 100, 450, 550, 650, and 750°C.


### 3.8. H2SO4 Treatment

The photocatalytic activity of the prepared Rx-SMT powders treated by H2SO4 solution was also investigated in the paper. The results are shown in Figure 13 and Table 3. By comparing Figure 13 with Figure 11, it is noted from that the photocatalytic activity of all the catalysts is improved after H2SO4 treatment. The reaction rate constants of Rx-SMT (Rx = 0, 0.05, 0.1, and 0.2) after sulfuric acid treatment are 0.0094, 0.0295, 0.0405, and 0.0194 min−1, respectively. The photocatalytic degradation rate of methyl orange over 0.1-SMT after sulfuric acid treatment was 2 times of that of Degussa P-25 titania and 1.37 times of that 0.1-SMT without sulfuric  acid treatment. FTIR results (Figure 7) showed that all samples after H2SO4 treatment demonstrate enhanced acidity on their surface. It was reported that the enhancement in surface acidity improves the activity of a photocatalytic system [28]. Therefore the photocatalytic activity of all samples after H2SO4 solution treatment was higher than that of the samples without H2SO4 solution.Table 3
The kinetics constants and regression coefficients of methyl orange photocatalysis on Rx-SMT treated by H2SO4 solution.
PhotocatalystKinetic constant (min−1)r2Ratio ofK to KP25Rx = 0, acid0.00940.96270.4947Rx = 0.05, acid0.02950.97631.5526Rx = 0.1, acid0.04050.98762.0558Rx = 0.2, acid0.01940.98731.0210Figure 13
Concentration changes of methyl orange versus UV irradiation time with different photocatalysts.


### 3.9. Oxidants Affecting the Photodegradation of MO over 1%-FST(Rx = 10%)

The effect of different oxidants such as in aqueous solutions on the photodegradation efficiency of MO in aqueous 1%-FST(Rx = 10%) suspensions was investigated here, the addition concentration of the oxidants all was 0.01 M and reaction time all was 60 mins. When these oxidants were separately added into reaction solutions, the photodegradation efficiencies corresponding to KIO4, (NH4)2S2O8, H2O2, and control were 95.1%, 87.5%, 93.2%, and 82%, respectively, which indicated that these oxidants enhance the photodegradation of MO. The higher degree of degradation with the oxidants may be ascribed to formation of highly reactive radical intermediates and the electron capture by these oxidants in the following equations [28]. 								(2)IO4∙-+hv⟶IO3∙+O∙-(3)O∙-+H+⟶∙OH(4)S2O82-+hv⟶2SO4∙-(5)SO4∙-+H2O⟶∙OH+SO42-+H+(6)S2O82-+eCB-⟶SO4∙-+SO42-(7)H2O2+hv⟶∙OH
It was well documented that the  electron reduction potentials of different species such as E(O2/O2∙-), E(H2O2/∙OH) and E(S2O82-/SO42-) are −115 mV, 1150 mV, and 1100 mV, respectively. It showed that all added oxidants should be more efficient electron acceptors than molecular oxygen to inhibit the electron-hole recombination.


## 3.1. Crystal Structure and TEM Photomicrography

XRD was used to investigate the changes of crystalline phase of the SMT gel powders before and after heat treatment. Figure2 shows the effects of silica on phase structures of the TiO2 powders dried at 100°C for 8 h. The anatase phase is dominant in the as-prepared TiO2 sample, but there is a small amount of   brookite in it. The weak peak  at 2č = 30.7° corresponds to the brookite phase of titania. When Rx > 0.1, the intensities of brookite peaks steadily become weaker and finally disappear. This is probably due to the fact that silica suppresses the crystallization of brookite by adsorbing onto the surfaces of TiO2 particles. Similar result has been observed with F ion doping [14].Figure 2
XRD patterns of the Rx-SMT xerogel powders (Rx = 0, 0.05, 0.1, and 0.2) and dried at 100°C for 8 h.Figure3 shows the effects of silica content on the phase structures of Rx-SMT powders calcined at 550°C. For pure titania (Rx = 0), significant peaks of rutile phase are observed obviously. The dominant phase of titania (Rx > 0) is anatase when some portion of silica is embedded into titania particles. Apart from the diffraction peaks corresponding to anatase, there are no other diffraction peaks from 2č = 20–60 degree for all SMT samples (except for pure titania) as shown in Figure 3, indicating that silica exists in an amorphous phase. The average size of anatase titania from Scherrer formula was presented in Table 1. The result shows that the crystallite size decreased sharply with increasing the doping silica content up to 0.05. When the silica content was over 0.05, there was no significant change in the crystallite size of SMT particles. This result confirms that the embedding of some portion of silica into titania particle inhibits the growth of anatase crystal of titania particles [15].Table 1
Textural properties of the Rx-SMT powders prepared at 550°C for 1 h.
SamplesSi/Ti molecular ratio by XPSSurface area (m2·g−1)Average size (nm)0-SMT02050.50.05-SMT0.0531608.90.1-SMT0.0941967.20.1-SMT treated by H2SO4 solution0.0931957.20.2-Silica titania0.2062086.9Figure 3
XRD patterns of  Rx-SMT powders (Rx = 0, 0.05, 0.1, and 0.2) calcined at 550°C for 1 h.Figure4 shows the effects of calcination temperature on phase structures of 0.1-SMT powders. It can be seen that the peak intensities of anatase increase and the width of the (101) plane diffraction peak of anatase (2θ= 25.4°) becomes narrower with increasing calcination temperature (from 100 to 750°C). It has been reported that anatase-type TiO2 changes to rutile-type structure by heat treatment above 635°C from the results of a kinetic study on the anatase-to-rutile phase transformation [13].  At 750°C, anatase is a main phase and a small amount of rutile phase is detected, while the phase of pure titania calcained at 550°C was dominant rutile phase. The resulting SMT powders contain only anatase phase in the calcination temperature range of 100–650°C. Accordingly, SMT samples show high thermal stability and the presence of silica seems to be critical for the stabilization of the anatase phase. The presence of silicon atoms in the anatase matrix retards the change of face-centered cubic arrangement of oxide ion in anatase into hexagonal packing in rutile because this change is associated with the cleavage of a part of Ti-O bonds [9]. The decrease of the surface energy caused by substitution of the surface OH groups with oxide ions also contributes to the thermal stability of the present products [15]. The average sizes at different temperatures were calculated, which corresponded to 1.4, 4.6, 10.1, and 28.8 nm for 100, 450, 650, and 750°C, respectively. At temperatures lower than 650°C, anatase phases are present in relatively small grain sizes. However, at 750°C (Rx = 0.1), anatase and rutile phases are both present and the grains of various phases grow dramatically. This is attributable to the fact that the phase transitions accelerate the process of grain growth by providing the heat of phase transformation [16]. The XRD results revealed that the heat treatment induced the increase of crystalline size and phase transformation.Figure 4
XRD patterns of 0.1-SMT powders calcined at (a) 100, (b) 450, (c) 650, and (d) 700°C for 1 h.Figure5 shows TEM photographs of 0.1-SMT powders calcined at 550°C for 1 h. It can be seen that the dispersion property of the sample is good. Table 1 indicates that specific surface area of the samples increase with the increase of the silica content. This result confirms that the suitable addition of silica into titania matrix helps to suppress the reduction of surface area at high calcination temperature. It is well noted that the specific surface areas of 0.1-SMT (196 m2/g) and 0.1-SMT after H2SO4 solution treatment (195 m2/g) are not significantly different.Figure 5
TEM image of 0.1-SMT prepared by ultrasonic irradiation hydrolysis and claniced at 550°C.


## 3.2. FT-IR Spectroscopy

FT-IR spectra of Rx-SMT calcined at 550°C for 1 h are presented in Figure6. The peak around 1090 cm−1 attributed to the asymmetric stretching vibrations of Si–O–Si band [17], and the Ti–O–Si linkage stretching band appears at about 962 cm−1 [18]. When the ratio of silicon to titanium was over 0.1, the distinct band for Ti–O–Si vibration (962 cm−1) was observed. The existence of Si–O–Ti bond in FT-IR analysis may be attributed to the existence of covalent bond between amorphous SiO2 and crystalline TiO2. The band for the asymmetric Si–O–Si stretching vibration was observed for all composite samples, and its intensity was increased with increasing the silicon content. The presence of Si–O–Si bond in FT-IR is caused by the formation of SiO2 in the samples, which is in agreement with the reported result [19]. Besides, Ti–O–Ti bond may be present in the range of 400 to 600 cm−1 [20] for all samples. From these results of FT-IR, it is clear that the silica exists as segregated amorphous phase in the anatase titania powders and some metal–O–metal bonding of Ti–O–Si, which result from formation of a new ternary amorphous SixTiyOz phase as there is no match in the XRD analysis and/or existence of covalent bond between amorphous SiO2 and crystalline TiO2.Figure 6
FT-IR spectra of Rx-SMT powders calcined at 550°C for 1 h.The peak around 1650 cm−1 is due to the bending vibration of O–H bond, which is assigned to the chemisorbed water, and the peak around 3460 cm−1 is assigned to the stretching mode of O–H bond and related to free water [21]. This water band was increased with increasing the ratio of silica to titanium. This is due to the fact that silica has the capability to absorb water in air [22]. In addition, when titania was embedded with silica, crystallite growth was suppressed and the surface area was kept larger (as shown in Table 1), and in this case, the capability to hold absorbed water became larger.FT-IR spectra of Rx-SMT after H2SO4 treatment were presented in Figure 7. The peak corresponding to 1244 cm−1 is the stretching frequency of S=O, and the peaks corresponding to 1159 and 1078 cm−1 are the characteristic frequencies of SO42-, which indicated the chelatometric coordinated adsorption of SO42- on SMT. The sulfate ion, both in surface and bulk, creates high surface acidity to improve the photocatalytic activity [23].Figure 7
FTIR spectra of Rx-SMT powders treated by 1M H2SO4 solution. Rx = 0.05, 0.1, and 0.2.


## 3.3. XPS Studies

Figure8 shows the XPS spectrum of 0.1-SMT powders  heat-treated at 550°C for 1 h and 0.1-SMT treated by 1 M H2SO4 solution. XPS peaks show that the 0.1-SMT powders contain nly Ti, O, Si, and a trace amount of carbon. The following binding energies are used in our quantitative measurements: Ti 2p at 460.10 eV, O 1 s at 531.35 eV, Si 2p at 103.8 eV, and  C 1 s at 286.20 eV. The atomic ratio of Ti : O : Si is about 1 : 2.13 : 0.13, which is higher than the nominal atomic composition of TiO2, indicating that silica atoms are partially concentrated on the surface region of the titania particles [7]. The C element is ascribed to the residual carbon from precursor solution and the adventitious hydrocarbon from the XPS instrument itself. It is easily observed that 0.1-SMT treated by 1 M H2SO4 solution contains Ti, O, Si, S, and a trace amount of carbon. The binding energies of Ti 2p, O 1 s, Si, S, and C 1 s are 460.70, 531.9, 105, 171.1, and 286.45 eV, respectively. It is easily noted from the figure that the binding energy of Ti2p in 0.1-SMT after H2SO4 treatment is higher than that of 0.1-SMT before H2SO4 treatment; the higher binding energy is helpful to improve its photocatalytic activity.Figure 8
XPS spectra of 0.1-SMT calcined at 550°C for 1 h and 0.1-SMT treated by H2SO4 solution.


## 3.4. UV-Vis Spectra

As a photocatalyst, the wavelength distribution of the absorbed light is one of the important properties regardless of the quantum yield. Figure9 shows the UV-Vis diffuse reflectance spectra (UV/Vis DRS) of prepared powders with the different silica content. Absorption edge of rutile (Rx = 0) is found to be at the shorter wavelength than that of anatase. Compared Rx-SMT samples with pure titania sample, the absorption spectrum of the Rx-SMT samples show a stronger absorption in the UV-visible range and a blue shift in the band gap absorption edge was observed in all SMT samples. The blue shift of absorption of a photocatalyst means that the photocatalyst has a greater oxidation-reduction potential and enhance the absorption, which will improve its photocatalytic activity [24].Figure 9
UV-Vis spectra of Rx-SMT with different Si/Ti ratios. Rx = 0, 0.05, 0.1, and 0.2.The energy band gap of prepared samples could be estimated from a plot of (αhγ) 1/2 versus photon energy (hγ). The intercept of the tangent to the plot will give a good estimation of the band gap energy for indirect band gap materials such as TiO2  [25, 26]. The absorption coefficient α can be calculated from the measured absorbance (A) using the following equation:
(1)α=2.303ρ103lcMA,
where the densityρ=3.9g cm−3, molecular weight M=79.9 g mol−1, c is the molar concentration of TiO2, and l is the optical path length.The calculated band gap energies of all silica-modified samples with different Rx values (0, 0.05, 0.1, and 0.2) are about 2.97 eV, 3.29, 3.31, and 3.34 eV, respectively. The above results imply that the absorption edge was clearly shifted toward shorter wavelengths for all SMT samples.


## 3.5. Photocatalytic Activity

As the photocatalytic mechanism suggests, both photocatalysts and a light source are necessary for the photo-oxidation reaction to occur [6]. A control experiment was conducted on three different conditions: (i) in the dark in presence of 0.1-SMT, (ii) only UV irradiation without photocatalyst, and (iii) under UV illumination in presence of 0.1-SMT. In all above conditions, the initial concentration of Methyl orange is 20 mg/L.  In Figure 1, the concentration of MO is plotted as a function of reaction time.As can be seen in Figure10, in the dark, 0.9% of the initial substrate disappeared after 1 h of continuous stirring due to the adsorption phenomena. Over this time, abatement of 5.4% after 1.5 h was detected. In direct photolysis, about 8% disappearing efficiency was observed during the 1 h irradiation; and 17% of the initial methyl orange disappeared after 1.5 h. When aqueous 0.1-SMT suspension was exposed to UV light, the concentration of MO decrease markedly. About 68–82% of methyl orange was bleached within 40–60 mins of time experiment, respectively. It can be clearly seen from Figure 10 that 93.5% of methyl orange in aqueous solution was photocatalytically degraded, and its corresponding mineralization efficiency was only 33%. It indicated that the complete mineralization of Methyl orange took more time than degradation.Figure 10
The variation of MO and TOC concentrations by photocatalytic technology with 0.1-SMT; (a) MO-dark experiment; (b) MO-direct photolysis; (c) TOC-photocatalysis; (d) MO-photocatalysis.The photocatalytic activity of Rx-SMT powders is affected by various factors, such as the doping silica content, calcined temperature, and sulfuric acid treatment.


## 3.6. Doping Silica Content

The photocatalytic activity of the prepared SMT powders for the decomposition of methyl orange was investigated as a function of silica content. The photocatalytic degradation follows pseudo first-order kinetics. The results are presented in Figure11 and Table 2. It is clearly seen that the photocatalytic degradation rate of methyl orange firstly increased with increasing the silica content when the range of silica content was from 0 to 0.1, it may be due to the decrease of average sizes as shown in the XRD analysis in Figure 3 and the increase of surface hydroxyl group as shown in the analysis of FT-IR in Figure 4. However, higher silica content (>0.1) did not favor the further enhancement of the photoactivity of SMT powders because the crystallinity of anatase decreased in spite of the larger specific surface area (Table 2), and SiO2 did not exhibit photocatalytic activity. It should be noted that the photocatalytic activity of 0.1-SMT is the best among all the samples and it was about 1.56 times of that of Degussa P25 titania, which is recognized as an excellent photocatalyst [27]. The difference in both of specific surface area and anatase crystallites is responsible for this discrepancy of Rx-SMT photoactivity and the surface area of Rx-SMT samples were presented in Table 1. Moreover, another reason on enhancement of SMT is ultrasonic irradiation in the preparation of samples; ultrasonic irradiation enhances hydrolysis of titanium and silicon alkoxide, and crystallization of the gel, because ultrasonic cavitation creates a unique environment for hydrolysis of titanium and silicon alkoxide. The similar result has been observed in formaldehyde degradation in silica titania system, which was reported [9].Table 2
The kinetics constants and regression coefficients of methyl orange photocatalysis on Rx-SMT and Degussa P-25 titania.
PhotocatalystKinetic constant (min−1)r2Ratio ofK to KP25Rx = 0K0=0.00150.93980.0789Rx = 0.05K1=0.02340.99491.2316Rx = 0.1K2=0.02960.99521.5579Rx = 0.2K3=0.01490.99560.7842Degussa P-25 titaniaKP25=0.0190.99771Figure 11
Concentration changes of methyl orange versus UV irradiation time with Rx-SMT photocatalysts calcined at 550°C for 1 h.It can be seen from Figure11 and Table 2 that pure titania (Rx = 0) shows very poor photocatalytic activity, compared to other samples. This can be easily explained that the sample was mainly composed of rutile phase with poor photocatalytic activity and has low specific surface area.


## 3.7. Calcined Temperature

It is well known that calcination is a common treatment that can be used to enhance the photoactivity of nanosized photocatalysts [27]. The photocatalytic activity of the prepared 0.1-SMT powders for the decomposition of methyl orange was investigated as a function of calcination temperature and the result was shown in Figure 12. The 0.1-SMT sample calcined at 100°C shows good photocatalytic activity with a reaction rate constant of 7.9 × 10−3 min−1. The reaction rate constant increases with increasing calcination temperature. Enhancing the photocatalytic activity at elevated temperatures can be ascribed to an obvious improvement in the crystallinity of anatase (as shown in Figure 4). At 550°C, the reaction rate constant k reaches the highest value of 2.96 ×10−2 min−1 and it is obviously higher than that of Degussa P-25 titania  (k=1.9×10-2 min−1). The high photocatalytic activity of the sample calcined 550°C is partially due to its large surface area and small crystallite size. Moreover, both of the intense absorption in the UV-visible range and a blue shift in the band gap transition of the SMT samples indicate that more powerful photogenerated holes and electrons can participate in the photocatalytic reactions. Calcination temperatures well above 550°C are not desirable. Samples calcined at 750°C display relatively poor photocatalytic activity.Figure 12
Concentration changes of methyl orange versus UV irradiation time with 0.1-SMT powders calcined at 100, 450, 550, 650, and 750°C.


## 3.8. H2SO4 Treatment

The photocatalytic activity of the prepared Rx-SMT powders treated by H2SO4 solution was also investigated in the paper. The results are shown in Figure 13 and Table 3. By comparing Figure 13 with Figure 11, it is noted from that the photocatalytic activity of all the catalysts is improved after H2SO4 treatment. The reaction rate constants of Rx-SMT (Rx = 0, 0.05, 0.1, and 0.2) after sulfuric acid treatment are 0.0094, 0.0295, 0.0405, and 0.0194 min−1, respectively. The photocatalytic degradation rate of methyl orange over 0.1-SMT after sulfuric acid treatment was 2 times of that of Degussa P-25 titania and 1.37 times of that 0.1-SMT without sulfuric  acid treatment. FTIR results (Figure 7) showed that all samples after H2SO4 treatment demonstrate enhanced acidity on their surface. It was reported that the enhancement in surface acidity improves the activity of a photocatalytic system [28]. Therefore the photocatalytic activity of all samples after H2SO4 solution treatment was higher than that of the samples without H2SO4 solution.Table 3
The kinetics constants and regression coefficients of methyl orange photocatalysis on Rx-SMT treated by H2SO4 solution.
PhotocatalystKinetic constant (min−1)r2Ratio ofK to KP25Rx = 0, acid0.00940.96270.4947Rx = 0.05, acid0.02950.97631.5526Rx = 0.1, acid0.04050.98762.0558Rx = 0.2, acid0.01940.98731.0210Figure 13
Concentration changes of methyl orange versus UV irradiation time with different photocatalysts.


## 3.9. Oxidants Affecting the Photodegradation of MO over 1%-FST(Rx = 10%)

The effect of different oxidants such as in aqueous solutions on the photodegradation efficiency of MO in aqueous 1%-FST(Rx = 10%) suspensions was investigated here, the addition concentration of the oxidants all was 0.01 M and reaction time all was 60 mins. When these oxidants were separately added into reaction solutions, the photodegradation efficiencies corresponding to KIO4, (NH4)2S2O8, H2O2, and control were 95.1%, 87.5%, 93.2%, and 82%, respectively, which indicated that these oxidants enhance the photodegradation of MO. The higher degree of degradation with the oxidants may be ascribed to formation of highly reactive radical intermediates and the electron capture by these oxidants in the following equations [28]. 								(2)IO4∙-+hv⟶IO3∙+O∙-(3)O∙-+H+⟶∙OH(4)S2O82-+hv⟶2SO4∙-(5)SO4∙-+H2O⟶∙OH+SO42-+H+(6)S2O82-+eCB-⟶SO4∙-+SO42-(7)H2O2+hv⟶∙OH
It was well documented that the  electron reduction potentials of different species such as E(O2/O2∙-), E(H2O2/∙OH) and E(S2O82-/SO42-) are −115 mV, 1150 mV, and 1100 mV, respectively. It showed that all added oxidants should be more efficient electron acceptors than molecular oxygen to inhibit the electron-hole recombination.


## 4. Conclusion

The Rx-SMT powders calcined at 550°C had pure anatase phase without other phases, except that pure titania showed pure rutile phase. XRD and FT-IR results showed that the silicon formed segregated amorphous silica and embedded into anatase titania matrix. BET results indicated that specific surface area increased with increasing the ratio of silica to titanium. Embedding silica into titania matrix increases the thermal stability by suppressing the increase of anatase crystallites and makes it possible to calcine the prepared Rx-SMT powders at high temperature without reducing surface area.The photocatalytic activity of Rx-SMT powders for the degradation of methyl orange increased with increasing the ratio of silica/titanium up to 0.1. The highest photocatalytic activity was obtained at 0.1-SMT and 1.5 times greater than that of Degussa P-25 titania. It can be confirmed that the quantization of particle size and large surface area by embedding silica into anatase titania matrix are beneficial to improve the photocatalytic activity of samples. The optimum ratio of silica to titania was 0.1. The photocatalytic degradation of methyl orange was affected by calcination temperatures. The rate constant at 550°C was higher than that at other temperature. This may be ascribed to higher specific surface area, small crystallite size, and improvement in the crystallinity of anatase.Sulfuric acid treatment can enhance photocatalytic activity of SMT powders. The photocatalytic activity of 0.1-SMT after treatment by H2SO4 solution was improved 37%. This increase in activity can be ascribed to high acidity. These oxidants such as KIO4, (NH4)2S2O8 H2O2 enhance the photodegradation of MO.


## Conflict of Interests

The authors declare that there is no conflict of interests.



---