# Facile Route to Generate Fuel Oil via Catalytic Pyrolysis of Waste Polypropylene Bags: Towards Waste Management of >20μ

Authors: Neeraj Mishra; Sunil Pandey; Bhushan Patil; Mukeshchand Thukur; Ashmi Mewada; Madhuri Sharon; Maheshwar Sharon
Journal: Journal of Fuels
 (2014)

---

## Abstract

A novel strategy of waste recycling of polypropylene plastics (PP) bags for generation of commercially viable byproducts using nanoforms of nickel as catalyst is presented in this work. After pyrolysis of waste PP bags (>20μm) under continuous argon flow, 90% conversion efficiency to high petroleum oil was observed at 550°C. To assess the physicochemical attributes of formed oil, flash point, pour point, viscosity, specific gravity, heating value, and density were also measured and found to be very close to ideal values of commercial fuel oil. Moreover, GC-MS was used to resolve the range of trace mass hydrocarbon present in the liquefied hydrocarbon. Our robust recycling system can be exploited as economical technique to solve the nuisance of waste plastic hazardous to ecosystem.


---

## Body

## 1. Introduction

Due to the nondegradability of PP plastics, their heavy accumulation in the environment is causing hostile effects on ecosystem including soil erosion [1]. Conventional routes to recycle PP plastics such as mechanical recycling, land filling, incineration, and chemical recycling [2] suffer from many hostile impacts such as landfill waste, clogged waterways, occupational health hazards, energy consumption, animal death, water contamination, foreign oil dependency, toxic pollution, soil degradation, costly production/recycling of plastics, and landscape litter. Additionally, these techniques have following limitations.(1)
Low-conversion efficiency.
(2)
No valuable by products are formed; rather one form of plastic is converted to another, which has no commercial value.
(3)
Requiring high energy and manual efforts.
(4)
Heavy pollutants are generated during the process.Keeping these cardinal issues under consideration, a facile route to convert waste plastics into high-performance fuel oil using high temperature pyrolysis is discussed in this paper. Fuel oil generated by our method was found to have all the characteristics to be used as fuel oil in factories. Since waste plastics like polypropylene (PP) contain 85% the carbon and rest is hydrogen, this makes them extremely suitable for feedstock recycling with the production of valuable hydrocarbon products. This fact can be explained with the difference in the activation energy of two polymers. PP requires lower activation energy to break the C−H bond than polyethylene (PE) because carbon chain of PP polymer contains tertiary carbon atoms which have considerably lower resistance against degradation [3]. There are several products obtained from the catalytic pyrolysis of PP which are carbon nano-materials (CNMs) of different morphologies [4–6], wax [7–9], oil [10–13] and gases [3, 14]. Most of the works, concerned with production of oils from waste PP plastics, and conversion efficiency was found to be <50%.Our main efforts were focused on converting WPP into less nonhazardous forms by ecofriendly method like catalytic pyrolysis. In our previous paper, conversion of PP to MWCNTs was reported [15]. However, during these conversion experiments, traces of liquid hydrocarbons were also noted. Therefore, a systematic study of oil-like liquefied hydrocarbon production was undertaken. This conversion has been demonstrated earlier by a simple thermal process in which polymers are melted and broken down to smaller molecules, at high temperature, into gaseous, liquid, and solid hydrocarbons [16]. Sarker et al. in 2012 [11] have performed thermal degradation of HDPE-2 in a fiber glass reactor system at a reaction temperature between 370 and 420°C and a reaction time of 4 h using HZSM-5 molecular sieves as catalyst to obtain hydrocarbon liquid fuel. Tymoshevskyy et al. in 2009 [17] have used pyrolysis method to convert PP, PE, and polystyrene (PS) waste to fuel with trial of several catalysts. They have separated the product of catalytic cracking used in a distillation column into gas, gasoline, light oil, and heavy oil fractions. Tiwari et al. in 2009 [12] have done the catalytic degradation of Linear Low Density PE (LLDPE) using two commercial cracking catalyst-1 and cracking catalyst-2 containing 20% and 40% US-Y zeolite, respectively, with average particle size in micrometers at temperature of 600°C to produce light hydrocarbon fuel. Catalytic pyrolysis of LDPE was investigated using various fly ash-derived silica-alumina catalysts (FSAs) by Na et al. in 2006 [18]. In the present work, our trials involve simple catalyst preparation as well as cost effective pyrolysis reactor for the synthesis of liquefied hydrocarbons. Catalytic pyrolysis due to combined impact of pyrolysis and catalytic reforming is shown as a more efficient method for processing large amounts of waste plastics [19]. We have made an attempt to utilize WPP as potential precursor for synthesis of liquefied hydrocarbons using catalytic pyrolysis. The synthesis of liquefied hydrocarbons from waste PP plastics using Ni as a catalyst in reactor at pyrolysis temperature of 550°C is reported. It was observed by Na et al. in 2006 [18] and Pandian and Kamalakannan in 2012 [20], that liquefied hydrocarbon synthesized at lower temperature or below 500°C after 1-2 days turns into wax whereas oil prepared above 500°C remains as it is after long period of time. Synthesized liquefied product was characterized by GCMS. Moreover, its flash point, pour point, viscosity, specific gravity, and density were also measured.


## 2. Experiment

Waste PP was collected from Brihanmumbai Municipal Corporation (BMC) garbage disposal centre. Immediately after collection, WPP were washed, air-dried, and shredded into small pieces prior to pyrolysis in presence of nano-sized nickel as catalyst. To synthesize Ni catalyst, 10 mL of 5 mM nickel nitrate was mixed with the same volume of ethanol under constant stirring for 2 hrs [21]. One kg of shredded WPP was mixed with 10 mL of nickel (Ni) catalyst and subjected to pyrolysis as displayed in Figure 1.Figure 1
Schematic diagram of unit used for synthesizing liquefied hydrocarbon by catalytic pyrolysis reactor. In this diagram, stainless steel reactor (A), gas inlet, condenser (B), liquid collection tank, valve, pressure gauge, and safety valve have been shown.Pyrolysis of waste plastic under controlled Ar (500 sccm) gas atmosphere at fixed temperature of 550°C (the ramp temperature of 10°C/min was used during this whole reaction process until the required temperature was achieved) with 1 h of dwell time in the presence of Ni as catalyst resulted in production of liquefied hydrocarbon or oil. This liquid was collected after the furnace temperature was allowed to cool down naturally once the reaction time was over in the atmosphere of 100 sccm of Ar gas (Figure1). Due to high temperature, plastics get fragmented into monomers and reacted with catalyst and converted into the form of respective gases form which condense through condenser and are stored in the collection tank (Figure 1).


## 3. Characterisation Technique

Gas chromatography coupled with high resolution mass spectrometer (GC-HRMS) was done by using an Agilent 7890 chromatograph with a (15 mm × 0.25 mm × 0.25μm) glass column packed with 80–100 mesh n-octanes, Porasil C, and with a flame ionization detector (FID). In gas chromatography, helium gas at the flow rate 1.5 mL/min was used as a carrier gas with a head space injection temperature of 250°C. The oven temperature was programmed from 40°C (2 min hold) to 140°C (10 min hold) with heating ramp rate of 8°C/min. Data scan rate of the sample was kept at 0.6 sec/scan with mass scan range of 10 to 425 m/z.Electron energy of mass spectrometer (Jeol, AccuTOF GCV) was 70 eV, and the ion source and coupling temperatures were 230 and 300°C, respectively. The ion mass spectra derived were automatically compared to TLC, MS spectral libraries. Standard solutions were analyzed to verify the identity of the peaks by retention time and provide quantitative analysis.Elemental analysis was carried out by CHNS (O) analyser of Thermo Finnigan (FLASH EA112 series) of IIT Bombay, Mumbai.Density, API gravity, specific gravity, pour point, and flash point—all these tests of liquid hydrocarbon, were characterized by standard methods [20].


## 4. Result and Discussion

During the catalytic degradation of WPP, the following cardinal steps decided the efficiency of conversion.(1)
Size monodispersity of the catalyst.
(2)
Ratio of WPP and catalyst.
(3)
Temperature gradient between site of pyrolysis (Figure1(A)) and site of collection (Figure 1(B)).As displayed in Figure2, size of Ni catalyst was found to be ranging between 5 and 10 nm. At nanoscale, enhanced catalytic activity of Ni involved in cracking and hydrogenation leads to efficient conversion of WPP to oil [22, 23]. Additionally, efficient diffusion of Ni during the process of pyrolysis helps to accelerate the entire reaction [24].SEM and EDEX of Ni nanoparticles.
(a)
(b)Ratio of WPP and catalyst (1% w/w) was also found to be vital parameter due to quantity-dependent reaction mechanism of Ni catalyst. At higher quantities, Ni influences conversion of PP to higher aromatic compounds which leads to amorphous carbon, thus decreasing the yield of oil. This is also due to self-pyrolytic properties of aromatic compounds which get converted to amorphous carbon [25]. Conversion of WPP to oil mainly depends upon the vaporization followed by prompt condensation of vapours with the help of condenser. Due to unique design of our furnace, vaporisation of PP was initiated at 350°C followed by complete process at 550°C. Till the vapours reach to condenser for the formation oil, there was sharp maintenance of temperature to avoid loss of higher carbon numbers (which may decrease the yield). This gradient in the temperature of the reaction vessel (550°C) and condenser (150°C) was possible due to kink (Figure 1(B)) separating the vapours at high as well as low temperatures.Most preliminary analysis of the oil was its visual inspection of the colour obtained after catalytic pyrolysis of WPP. The appearance of oil was transparent and yellowish red in colour. The oil obtained from the pyrolysis was fractionated by distillation and the fuel properties were studied. Elemental composition of fuel oil is found to be C (83%), H (14%), and O (1%) which confirmed hydrocarbon nature of oil (Figure3). A comparative analysis of sulfur content, pour point, viscosity, and distillation recovery of oil synthesized using various methods is presented in Table 1. Pour point of the sample was found to be less than 10°C, which is in accordance with the standard values of fuel oil [26]. Flash points, density, acidity of fuel oil were found to be ~40°C, 0.7930 g/mL, and 0.76, respectively. All the above values were found to be standard values of fuel oil [11, 27].Table 1
Comparative study of physical properties of fuel oil obtained by WPP with other waste plastic products.
SR. no.
Test
Method of testing
Result
Waste LDPE[20]
Waste mixed plastic[12]
Waste HDPE[27]
Gulf fuel oil [28]
1
Density @ 15∘C
ASTM D 4052:2002
0.7930 g/mL
0.8760 g/mL
NA
0.7828 g/mL
NA
2
Acidity (mg KOH/g)
ASTM D 974:2002
0.76
Nil
NA
NA
Nil
3
API gravity @ 60∘F
ASTM D 1298:1999
46.67
NA
60.65
NA
31.4
4
Flash point COC
ASTM D 92-05a
<40∘C
45∘C
22
Plus 1∘C
NA
5
Kinematic viscosity @ 40∘C
ASTM D 445:2005
2.149 mm2/s
1.47 mm2/s
NA
1.63 mm2/s
5.69
6
Colour
ASTM D 1500:2004a
D 8 (light yellowish- red clear)
NA
Pale yellow
Dark brownish clear
Orange
7
Conradson carbon residue
ASTM D 189:2005
0.010% (wt%)
NA
NA
0.01%
NA
8
Asphaltene content
ASTM D 3279:2001
0.21 (wt%)
NA
NA
NA
NA
9
Ash content
ASTM D 482:2003
<0.01% (wt)
0.02%
NA
NA
NA
10
Calculated carbon aromatic index
ISO 8217:1996
763.4
NA
NA
NA
NA
11
Pour point
ASTM D 97-05a
Minus 10∘C
NA
<−20∘C
Minus 15∘C
1.6∘C
12
Sediment by extraction
ASTM D 473:2002
0.012 (wt)
0.001
NA
NA
NA
13
Specific gravity @ 15∘C
ASTM D 4052:2002
0.7932
NA
0.7365
0.7835
0.8690
14
Sulphur content
ASTM D 4094:2003
0.0025%
0.083%
0.002%
0.019%
0.09%
15
Water by distillation
ASTM D 95-05el
<0.05%
0.01%
NA
NA
0.05%
16
Calorific value
ASTM D 240 cal/g
10,000
10,810
10,498
10,244
10,460
17
Distillation range
ASTM D 86:04b
Initial boiling range
71∘C
82
5%  recovery
110∘C
10% recovery
141∘C
126
20%
185∘C
30%
226∘C
188
40%
261∘C
50%
291∘C
226
60%
319∘C
70%
343∘C
278
80%
365∘C
85%
380∘C
90%
390∘C
320
100%
400∘C
85.3%
352
99.6%
Total recovery
90%
95%
*NA: not available.Figure 3
Elemental analysis of fuel oil.American Petroleum Institute (API) gravity of liquefied hydrocarbon prepared from waste plastics was found to be 46.67. There is an inverse relationship between API gravity and density; that is, the higher the density, the lower the API gravity. Light crude is generally that with API gravity over 40 [20]. Therefore, liquefied hydrocarbon produced from our pyrolysis system was found to be light.Specific gravity of liquefied hydrocarbon prepared from pyrolysis of waste PP was estimated to be 0.7932 at 15°C which is similar to specific gravity of petroleum (density compared to water), that is, 0.8 [20, 29].Liquefied hydrocarbon synthesized from pyrolysis of WPP has 25 ppm (0.0025%) of sulfur content which is very less compared to standard fuel oil. Fuel oil is normally described as sweet (low sulfur) or sour (high sulfur) depending on their sulfur content. Sweet fuel oil has sulfur content less than 0.5%, and anything more than that is sour. Sweet oil is more preferable than the sour due to its applicability to produce most of the refined products [18, 27]. Another important attribute was found to be kinematic viscosity of liquefied hydrocarbon synthesized from waste plastic that was estimated to be 2.149 mm2/s at 40°C. As per the standard kinematic viscosities of fuel oil (3.5–9.7 mm2/s), oil formed by our method was found to be less viscous [20, 30, 31].Calorific value of oil synthesized from pyrolysis of waste plastic was recorded to be 10,000 cal/g (41.86 MJ/kg), whereas Calorific values of various fuel oils, for example, diesel, gasoline, petrol and petroleum fuel are 44.8, 47.3, 48 and 43 MJ/Kg respectively [20, 30, 31]. Hence, it can be said that this liquefied hydrocarbon obtained from waste plastic can be used for fuel.From the distillation report of the liquefied hydrocarbon, it was found that boiling range of the oil is 71–390°C, which suggests the presence of a mixture of different fractions such as gasoline, kerosene, and diesel [17, 20, 30–32].A typical GC chromatogram diagram for the liquid fraction taken from plastics pyrolysis is illustrated in Figure4. It is clear that chromatogram obtained in high efficient column contains two dominant products which are alk-1-enes and n-alkanes in the range C6–C23, with only a small proportion of cyclic and alcoholic substances. Besides these main mixed plastics decomposition products, chromatogram is fully occupied by several hundred small peaks of other compounds including broad peak of many unresolved compounds which is characteristic for multicomponent hydrocarbon mixtures. This is due to low pyrolysis temperature. Furthermore, a detailed list of all hydrocarbons detected in the liquid fraction of pyrolysis of waste products based on high-density polyethylene (HDPE) and low-density polyethylene (LDPE) was well explained by Achilias et al. in 2007 [8]. It was observed that pyrolysis of the plastic bag made from PE and PP leads to a fraction mainly in the region of C7–C12, which is in the gasoline region. Also, the main components were alkanes and alkenes. A mass spectrum indicates that the fragment of polymers contains only one carbon atom; this is due to the fragmentation at interval of –CH2 break from long chain. Mass spectra at different time intervals show that oil contained alkanes, alkenes, some cycloalkanes, and alcohol. Mass spectra at 3.9 min show that oil might contain cycloalkane and alkenes like cyclodecane and 1-decene, respectively (Figure 5). There are some aliphatic alkanes found to be present at time interval of 4 min having m/z ratio of 142 corresponds to decane (C10H22) (Figure 6). It is seen from Figure 7 that there are some higher alcoholic groups like n-pentadecanol (C15H32O). Figure 8 indicates higher alkanes, present at interval time of 29.4 minutes; they are nonacosane (C29H60) and triacontane (C30H62). It is concluded from the GC-MS data that oil contain alkanes, alkenes, cyclic alkanes, and some alcoholic groups.Figure 4
Total ion chromatogram of liquefied hydrocarbon obtained from the pyrolysis of waste PP at 550°C in the presence of Ni as catalyst for a duration of 1 hr in atmosphere of Ar.Figure 5
Mass spectra of peaks at 3.9 min.Figure 6
Mass spectra of peaks at 4 min.Figure 7
Mass spectra of peaks at 11 min.Figure 8
Mass spectra of peaks at 29.4 min.


## 5. Mechanism of Catalytic Degradation of Plastics

The presence of a small amount of Ni catalyst could efficiently promote the dehydrogenation of PP into light hydrocarbons. It was because that the Ni catalyst attacked PP surface to form cationic active sites and promoted the formation of more molecules with a lower carbon number by a cationic mechanism [14, 15]. Catalysts such as metal oxides have appeared to be used mainly for enhancement of monomer recovery [32]. Degradation of PP on nickel oxide solution yield more oils than that on solid acids, and time required to complete degradation on nickel oxide is lower than on solid acids. The composition of oil on metal oxide (NiO) is reported to be rich in 1-olefins and is poor in aromatics and branched isomers. In our case, plastics reacted with catalyst and were converted into smaller fragments or monomers. As the temperature increases these fragments are converted into vapour state which condense to give fuel oil. Octane number is expected to be low for the oils produced on solid bases, since the oils mainly consisted of straight chain hydrocarbons: n-paraffins, and 1-olefins. From an economic point of view, reducing the cost even further will make this process an even more attractive option. This option can be optimized by reuse of catalysts and the use of effective catalysts in smaller quantities [28, 33]. This method seems to be the most promising to be developed into a cost-effective commercial plastic waste recycling process to solve the keen environmental problem of plastic waste disposal.


## 6. Conclusion

Catalytic degradation of waste plastics in the presence of Ni catalyst for duration of 1 h in presence of Ar atmosphere leads to following concluding remarks.(1)
Conversion efficiency of Ni catalysed pyrolysis of WPP was found to be more than 90% yield. The catalytic degradation process produces much less residue content than that from thermal degradation.
(2)
Physicochemical properties of obtained fuel oil can be exploited to make highly efficient fuel or furnace oil after blending with other petroleum products.
(3)
The knowledge of design and process of the semiscale plant will be helpful for developing a commercial scale plant in the future. From this result, it can be concluded that the fuel properties of the catalytic pyrolysis oil match the properties of petroleum fuels.


## Highlights

(i)
Ecofriendly method for waste management of polypropylene plastics.
(ii)
Use of nano-sized catalyst to enhance the rate of conversion of waste plastics to fuel oil.
(iii)
Ideal properties of fuel oil for efficient commercial usage.
(iv)
Unique design of the furnace to facilitate efficient conversion.



---