# Multifunctional Epoxy/Nanocomposites Based on Natural Moroccan Clays with High Antimicrobial Activity: Morphological, Thermal and Mechanical Properties

Authors: M. Monsif; A. Zerouale; N. Idrissi Kandri; R. Bertani; A. Bartolozzi; B. M. Bresolin; F. Zorzi; F. Tateo; M. Zappalorto; M. Quaresimin; P. Sgarbossa
Journal: Journal of Nanomaterials
 (2019)

---

## Abstract

In this study, a series of new epoxy/clay nanocomposites (ECN) has been prepared and characterized in order to investigate the properties and compare the effect of the unmodified Moroccan clay on the structure and properties of the composite materials. Five natural clays have been used to reinforce the neat epoxy resin with 1% wt and 5% wt achieving the clay dispersion only through strong milling and mechanical stirring without previous organic modifications of the clays. The quality of clay dispersion in the epoxy matrix and the morphology of nanocomposites have been studied by transmission electron microscopy (TEM), environmental scanning electron microscopy (ESEM), and X-ray diffraction (XRD). The mechanical and thermal properties have also been investigated. The antimicrobial activity of the nanocomposites has been tested againstE. coli and S. aureus in order to evaluate their applicability as advanced antimicrobial materials. The results showed that the epoxy/crude clay nanocomposites exhibited a high inhibition action attending 99% against both bacteria in the case of the clay labeled A5.


---

## Body

## 1. Introduction

In recent years, one of the most intriguing topics concerning polymer nanocomposites is the design and preparation of materials exhibiting improved and/or new properties for a variety of applications [1]. There has been enormous interest from industries for the manufacturing and commercialization of nanocomposites for applications in aerospace [2], automotive [3], packaging [4, 5], electronics [6], and other industrial sectors [7, 8]. These materials also showed a potential use as solution for energy and environmental issues [9]. Nanocomposites are materials based on the combination of a selected matrix and nanodimensional phases. Thus, different materials have been used for their preparation. Among them, polymer nanocomposites containing inorganic nanoscale particles homogeneously dispersed into selected polymer matrices have been extensively investigated and used [10]. The typical nanofiller is clay, but graphite, single- and multiple-wall nanotubes, nanoscale silica [11], and titania [12] have also been investigated. Epoxy resins, extensively used in a wide variety of industrial applications, exhibit weak mechanical properties, thus requiring support through nanoscale blending with other synthetic polymers, fibers, or inorganic materials [13]. However, the improvement of epoxy/clay nanocomposite (ECN) properties depends not only on the concentration of clay but also on its dispersion quality and adhesion in the polymer matrix [14]. Only a few hydrophilic polymers such as poly(ethylene oxide) and poly(vinyl alcohol) can be miscible with clay nanolayers [15]. Therefore, clays are usually organically modified with cationic-organic surfactants [16] in order to make them compatible with organic polymers and to improve their dispersion into the matrix. Clays can be intercalated with several organic and inorganic species [17, 18] including ethylenediamine [19], ammonium [20], or phosphonium ions [21, 22]. Other authors studied different dispersion methods using an ultrasonic mixing procedure or mechanical blending [23–25]. The dispersion of a sufficient quantity of nanoclays can significantly improve the mechanical properties of the material compared to those of the neat epoxy polymers in pristine form [26–28] and increase heat resistance achieving a combination of new optical, electrical, thermal, and biological properties [29].Inorganic materials with antibacterial properties attracted significant attention for application in biomedical devices or in antimicrobial packaging and items in daily use [30]. Therefore, the preparation of epoxy/clay nanocomposites with antimicrobial activity can be of interest [31, 32]. Recently, the antibacterial activity of polymer nanocomposites with different fillers has been studied. For instance, the addition of Na-montmorillonite in some composites, such as chitosan/PVOH films, resulted in 40% growth inhibition of E.coli [33] while epoxy resin nanocomposites with copper-modified clays exhibited antibacterial activity against both Gram-negative and Gram-positive bacteria [34–36]. In general, this activity was found in nanocomposites containing modified clays with cationic systems [37] or metal ions such as copper [35] and silver [38, 39].To our knowledge, even if it was reported that some raw clays have bactericidal activity against bothGram-positive and Gram-negative bacteria [40–44], and against antibiotic-susceptible and antibiotic-resistant bacterial pathogens [45], no publications on the antibacterial activity of epoxy/clay nanocomposites with unmodified clay have been reported.In this study, new epoxy/clay nanocomposites containing 1% wt and 5% wt of natural clay with a sufficient dispersion were prepared, although in the absence of organic modifications and only through strong milling and mechanical stirring.The mechanical and thermal properties of the composites together with the antibacterial activity have been studied in order to evaluate their applicability as advanced antimicrobial materials.


## 2. Material and Methods

This section is aimed at describing the materials used in the experimental program, their preparation, and the methods used for the characterization of their mechanical and antimicrobial properties, which were carried out following the methods used in Ref. [35], where the antibacterial activity of multifunctional Cu2+-montmorillonite/epoxy resin nanocomposites was studied.


### 2.1. Materials

With the aim of the valorization of some local raw materials from Morocco, five clay materials noted asA1, A2, A3, A4, and A5 from different regions and with different compositions were collected to be used as filler in the preparation of epoxy nanocomposites. Before their use, the clays were dried at 60°C, crushed and sieved at 80 μm, and characterized by different techniques [46]. The data concerning the chemical composition are reported in Table 1. A diglycidyl ether of bisphenol A epoxide (DGEBA, Elan-tech EC157) and the mixture of cycloaliphatic amines (Elan-tech W 152LR), both supplied by Elantas, have been used as polymer precursors.Table 1
Mineralogical, chemical composition, and physical properties of the clay samples.
Mineralogical composition
A1
A2
A3
A4
A5
Qz, Kaol, Chl, Il/Musc, Il/Sm, Py, Cal
Qz, Kaol, Chl, Il/Musc, Il/Sm, Py, Cal
Qz, Kaol, Chl, Il/Musc, Py, Cal
Qz, Kaol, Musc, Il, Feld, Cal, Dol
Qz, Kaol, Il, Goe
Chemical composition (% wt)
SiO2
54.50
53.60
53.60
42.60
62.70
TiO2
0.85
0.84
0.87
0.44
0.79
Al2O3
27.4
26.5
26.00
11.00
21.30
Fe2O3
4.89
5.61
5.95
2.32
4.95
MnO
0.07
0.13
0.12
0.04
0.11
MgO
1.76
2.05
2.19
3.29
0.84
CaO
0.31
0.69
1.02
18.80
0.33
Na2O
1.24
1.50
1.68
0.82
0.87
K2O
1.92
2.10
2.06
1.30
1.67
P2O5
0.23
0.18
0.17
0.24
0.06
L.O.I.
6.65
6.58
6.15
18.70
6.12
Qz: quartz; Chl: chlorite; Il/Musc: illite/muscovite; Kaol: kaolinite; Py: pyrophyllite; Fld: feldspars; Cal: calcite; Dol: dolomite; Goe: goethite; Il/Sm: illite/smectite.


### 2.2. Preparation of Epoxy/Clay Nanocomposites

The nanocomposites using the sieved fraction were prepared through mechanical dispersion by mixing the epoxy resin with the unmodified clays. Specifically, epoxy formulations containing 1 and 5% by weight of clay were considered. Initially, a measured amount of unmodified 80μm sieved clays (A1, A2, A3, A4, and A5) was added to the diglycidyl ether of bisphenol A epoxy in a flask. The dispersion process was performed at room temperature under constant magnetic stirring (900 rt/min) for about 18 hrs until the dispersion was homogeneous. Then, the curing agent (the mixture of cycloaliphatic amines) was added under magnetic stirring according to the stoichiometric ratio from the supplier’s datasheet (3 : 1 = epoxide/amine wt/wt). The reacting mixture was degassed for 20 min after the addition of the hardener to remove the air trapped within the blend. Finally, the obtained mixture was casted onto open silicon molds to be cured at room temperature for 24 hours and then in an oven at 60°C for 6 hours. The samples of epoxy clay nanocomposite have been identified as ECP, where E was the epoxy, C referred to the clay, and P was the percentage of used clay.


### 2.3. Characterization and Mechanical Properties of the Nanocomposites

#### 2.3.1. Fourier Transform Infrared Spectroscopy

FTIR spectra of the clay powders were obtained on a Nicolet Avatar 320 spectrophotometer as KBr pellets. For each sample, 32 scans were recorded in the range 4000-400 cm-1 in the transmittance mode with a resolution of 4 cm-1. ATR-FTIR spectra on the polymeric materials were collected with a Nicolet Nexus 5700 instrument at 23°C and 35-45% RH (10 reflections, ZnSe crystal).


#### 2.3.2. X-Ray Diffraction

Powder and nanocomposite XRD analyses were carried out with a PANalytical X’Pert Pro diffractometer equipped with a Co X-ray tube (operating at 40 kV and 40 mA) and a real-time multiple strip (RTMS) detector (X’Celerator). The diffraction profiles were collected over the 2θ range of 2.6–85°, with a virtual 2θ step size of 0.017° and a counting time of 100 s/step.


#### 2.3.3. Environmental Scanning Electron Microscopy

The microanalysis and morphology of the samples have been studied by ESEM (Quanta 200 FEI-XRF embedded). The samples have been observed directly on cross sections obtained by brittle fracture at the temperature of liquid nitrogen.


#### 2.3.4. Transmission Electron Microscopy

The morphology of the nanocomposites was studied by transmission electron microscopy (TEM) with a JEM 2000 EX-II (Jeol, Japan) microscope, at 120 kV. 120 nm thick films were obtained by cutting the samples with a PT-PC Power Tome ultramicrotome at room temperature (RMC Boeckeler Instruments, USA).


#### 2.3.5. Mechanical Properties

Tensile tests on dog-bone (DB) specimens were carried out taking advantage of a MTS809 servo-hydraulic machine equipped with a 2.5 kN load cell using a crosshead speed equal to 2 mm/min and with a MTS 632.29F-30 extensometer. The specimen geometry was chosen according to the ISO 527-2 suggestions [47]. Five specimens were tested for each clay content in order to obtain statistical representative results. In all cases, failure took place in the gauge length of the specimens. Fracture tests were carried out on compact tension (CT) specimens of which the geometry and size comply with ASTM D5045-99 suggestions [48]. According to previously reported procedures [49–51], after demoulding, specimens were precracked by manual tapping, obtaining artificial short cracks. Then 10 mm long cracks were obtained by loading the tapped samples with some zero-to-tension fatigue cycles. For each composite, five specimens were tested. Experimental results were rearranged, and for each test, the value of KIC was determined starting from the crack length and the fracture load, according to ASTM D5045 [48].


#### 2.3.6. Thermogravimetric Analysis

TGA were performed on a TGAQ 5000 thermogravimetric analyser, TA Instruments, under air atmosphere: 15-20 mg of the samples were heated from 25°C to 900°C under air atmosphere with a heating rate of 10°C/min.


#### 2.3.7. Zero Surface Charge Determination

By using the solid addition method [52], the zero surface charge characteristics of the epoxy/clay nanocomposites were determined. In a series of 50 ml of 0.1 M KNO3 solution, the pH0 values were adjusted to 2, 4, 6, 8, and 10 by adding either 0.1 M HCl or 0.1 M NaOH. Then, one gram of crushed specimens was added to each flask. The suspensions were then manually shaken and allowed to equilibrate for 48 h with intermittent manual shaking. The final pH values of the supernatant liquid were noted. The difference between the initial pH (pH0) and the final one (pHf) values (pH=pH0−pHf) was plotted against the pH0. The point of intersection of the resulting curve with abscissa, at which pH=0, gave the pHpzc.


### 2.4. Antimicrobial Activity

#### 2.4.1. Antimicrobial Activity of the Raw Clays

The antimicrobial activity of clays has been determined againstEscherichia coli (E. coli) TCC 8739 and Staphylococcus aureus (S. aureus) ATCC 6538P, selected as examples of Gram-negative and Gram-positive bacteria as recommended by ISO 22196 [53] following the procedure previously reported [35]. Both bacteria were cultured overnight at 35°C onto Tryptic Soy Agar (TSA) before use and diluted in Nutrient Broth (NB) 1 : 500 with distilled water in order to obtain suspensions containing 105-108 cells/ml, suitable for the experiments. Sterilized clays (1 g) were introduced into 800 μl of NB containing the initial pathogen inoculum, and the mixtures were incubated at 35°C for 24 h. Positive controls for growth of bacteria in the absence of clays were carried out together with each series of experiments. In addition, negative controls were performed in order to ensure that the clay samples maintained sterilization during storage. After incubation, the mixtures were subjected to successive 10-fold dilutions in distilled sterilized water and quantitatively cultured in duplicate onto TSA plates to determine the number of viable bacteria. Viable cell counts are expressed as log10cfu per 800 μl.


#### 2.4.2. Antibacterial Activity of the Nanocomposites

The surface biocidal capacity of the nanocomposites has been evaluated againstE. coli ATCC 8739 and S. aureus ATCC 6538P according to ISO 22196 and OECD guidelines [53, 54] and following the procedure previously described [35]. Each strain microbial testing was performed in triplicate: 6 specimens of neat epoxy resins were used as control (3 for t=0 and 3 for t=24hours) and 3 samples of each nanocomposite were tested. The samples were treated with a sterilizing UV irradiation, then an area of 4 cm2 was coated with 50 μl (12.5 μl/cm2) of suspension of diluted bacteria in NB containing 105-107 cells and incubated for 24 hrs at 35°C. The bacteria were recovered by adding 10 ml of soybean casein digest with lecithin and polysorbate neutralizer broth (SCDLP) and 10-fold serial diluted in phosphate-buffered physiological saline solution. Then, 1 ml of each dilution was put into Petri dishes with 15 ml of Molten Plate Count Agar (PCA) and incubated at 35°C for 40 hrs (all the platings were performed in duplicate). Results were expressed as the number of units forming colonies (cfu) per cm2, and the percentage of inhibition was calculated with the equation established in the standard test method ASTM E2149-01 [55] comparing data with reference samples.


## 2.1. Materials

With the aim of the valorization of some local raw materials from Morocco, five clay materials noted asA1, A2, A3, A4, and A5 from different regions and with different compositions were collected to be used as filler in the preparation of epoxy nanocomposites. Before their use, the clays were dried at 60°C, crushed and sieved at 80 μm, and characterized by different techniques [46]. The data concerning the chemical composition are reported in Table 1. A diglycidyl ether of bisphenol A epoxide (DGEBA, Elan-tech EC157) and the mixture of cycloaliphatic amines (Elan-tech W 152LR), both supplied by Elantas, have been used as polymer precursors.Table 1
Mineralogical, chemical composition, and physical properties of the clay samples.
Mineralogical composition
A1
A2
A3
A4
A5
Qz, Kaol, Chl, Il/Musc, Il/Sm, Py, Cal
Qz, Kaol, Chl, Il/Musc, Il/Sm, Py, Cal
Qz, Kaol, Chl, Il/Musc, Py, Cal
Qz, Kaol, Musc, Il, Feld, Cal, Dol
Qz, Kaol, Il, Goe
Chemical composition (% wt)
SiO2
54.50
53.60
53.60
42.60
62.70
TiO2
0.85
0.84
0.87
0.44
0.79
Al2O3
27.4
26.5
26.00
11.00
21.30
Fe2O3
4.89
5.61
5.95
2.32
4.95
MnO
0.07
0.13
0.12
0.04
0.11
MgO
1.76
2.05
2.19
3.29
0.84
CaO
0.31
0.69
1.02
18.80
0.33
Na2O
1.24
1.50
1.68
0.82
0.87
K2O
1.92
2.10
2.06
1.30
1.67
P2O5
0.23
0.18
0.17
0.24
0.06
L.O.I.
6.65
6.58
6.15
18.70
6.12
Qz: quartz; Chl: chlorite; Il/Musc: illite/muscovite; Kaol: kaolinite; Py: pyrophyllite; Fld: feldspars; Cal: calcite; Dol: dolomite; Goe: goethite; Il/Sm: illite/smectite.


## 2.2. Preparation of Epoxy/Clay Nanocomposites

The nanocomposites using the sieved fraction were prepared through mechanical dispersion by mixing the epoxy resin with the unmodified clays. Specifically, epoxy formulations containing 1 and 5% by weight of clay were considered. Initially, a measured amount of unmodified 80μm sieved clays (A1, A2, A3, A4, and A5) was added to the diglycidyl ether of bisphenol A epoxy in a flask. The dispersion process was performed at room temperature under constant magnetic stirring (900 rt/min) for about 18 hrs until the dispersion was homogeneous. Then, the curing agent (the mixture of cycloaliphatic amines) was added under magnetic stirring according to the stoichiometric ratio from the supplier’s datasheet (3 : 1 = epoxide/amine wt/wt). The reacting mixture was degassed for 20 min after the addition of the hardener to remove the air trapped within the blend. Finally, the obtained mixture was casted onto open silicon molds to be cured at room temperature for 24 hours and then in an oven at 60°C for 6 hours. The samples of epoxy clay nanocomposite have been identified as ECP, where E was the epoxy, C referred to the clay, and P was the percentage of used clay.


## 2.3. Characterization and Mechanical Properties of the Nanocomposites

### 2.3.1. Fourier Transform Infrared Spectroscopy

FTIR spectra of the clay powders were obtained on a Nicolet Avatar 320 spectrophotometer as KBr pellets. For each sample, 32 scans were recorded in the range 4000-400 cm-1 in the transmittance mode with a resolution of 4 cm-1. ATR-FTIR spectra on the polymeric materials were collected with a Nicolet Nexus 5700 instrument at 23°C and 35-45% RH (10 reflections, ZnSe crystal).


### 2.3.2. X-Ray Diffraction

Powder and nanocomposite XRD analyses were carried out with a PANalytical X’Pert Pro diffractometer equipped with a Co X-ray tube (operating at 40 kV and 40 mA) and a real-time multiple strip (RTMS) detector (X’Celerator). The diffraction profiles were collected over the 2θ range of 2.6–85°, with a virtual 2θ step size of 0.017° and a counting time of 100 s/step.


### 2.3.3. Environmental Scanning Electron Microscopy

The microanalysis and morphology of the samples have been studied by ESEM (Quanta 200 FEI-XRF embedded). The samples have been observed directly on cross sections obtained by brittle fracture at the temperature of liquid nitrogen.


### 2.3.4. Transmission Electron Microscopy

The morphology of the nanocomposites was studied by transmission electron microscopy (TEM) with a JEM 2000 EX-II (Jeol, Japan) microscope, at 120 kV. 120 nm thick films were obtained by cutting the samples with a PT-PC Power Tome ultramicrotome at room temperature (RMC Boeckeler Instruments, USA).


### 2.3.5. Mechanical Properties

Tensile tests on dog-bone (DB) specimens were carried out taking advantage of a MTS809 servo-hydraulic machine equipped with a 2.5 kN load cell using a crosshead speed equal to 2 mm/min and with a MTS 632.29F-30 extensometer. The specimen geometry was chosen according to the ISO 527-2 suggestions [47]. Five specimens were tested for each clay content in order to obtain statistical representative results. In all cases, failure took place in the gauge length of the specimens. Fracture tests were carried out on compact tension (CT) specimens of which the geometry and size comply with ASTM D5045-99 suggestions [48]. According to previously reported procedures [49–51], after demoulding, specimens were precracked by manual tapping, obtaining artificial short cracks. Then 10 mm long cracks were obtained by loading the tapped samples with some zero-to-tension fatigue cycles. For each composite, five specimens were tested. Experimental results were rearranged, and for each test, the value of KIC was determined starting from the crack length and the fracture load, according to ASTM D5045 [48].


### 2.3.6. Thermogravimetric Analysis

TGA were performed on a TGAQ 5000 thermogravimetric analyser, TA Instruments, under air atmosphere: 15-20 mg of the samples were heated from 25°C to 900°C under air atmosphere with a heating rate of 10°C/min.


### 2.3.7. Zero Surface Charge Determination

By using the solid addition method [52], the zero surface charge characteristics of the epoxy/clay nanocomposites were determined. In a series of 50 ml of 0.1 M KNO3 solution, the pH0 values were adjusted to 2, 4, 6, 8, and 10 by adding either 0.1 M HCl or 0.1 M NaOH. Then, one gram of crushed specimens was added to each flask. The suspensions were then manually shaken and allowed to equilibrate for 48 h with intermittent manual shaking. The final pH values of the supernatant liquid were noted. The difference between the initial pH (pH0) and the final one (pHf) values (pH=pH0−pHf) was plotted against the pH0. The point of intersection of the resulting curve with abscissa, at which pH=0, gave the pHpzc.


## 2.3.1. Fourier Transform Infrared Spectroscopy

FTIR spectra of the clay powders were obtained on a Nicolet Avatar 320 spectrophotometer as KBr pellets. For each sample, 32 scans were recorded in the range 4000-400 cm-1 in the transmittance mode with a resolution of 4 cm-1. ATR-FTIR spectra on the polymeric materials were collected with a Nicolet Nexus 5700 instrument at 23°C and 35-45% RH (10 reflections, ZnSe crystal).


## 2.3.2. X-Ray Diffraction

Powder and nanocomposite XRD analyses were carried out with a PANalytical X’Pert Pro diffractometer equipped with a Co X-ray tube (operating at 40 kV and 40 mA) and a real-time multiple strip (RTMS) detector (X’Celerator). The diffraction profiles were collected over the 2θ range of 2.6–85°, with a virtual 2θ step size of 0.017° and a counting time of 100 s/step.


## 2.3.3. Environmental Scanning Electron Microscopy

The microanalysis and morphology of the samples have been studied by ESEM (Quanta 200 FEI-XRF embedded). The samples have been observed directly on cross sections obtained by brittle fracture at the temperature of liquid nitrogen.


## 2.3.4. Transmission Electron Microscopy

The morphology of the nanocomposites was studied by transmission electron microscopy (TEM) with a JEM 2000 EX-II (Jeol, Japan) microscope, at 120 kV. 120 nm thick films were obtained by cutting the samples with a PT-PC Power Tome ultramicrotome at room temperature (RMC Boeckeler Instruments, USA).


## 2.3.5. Mechanical Properties

Tensile tests on dog-bone (DB) specimens were carried out taking advantage of a MTS809 servo-hydraulic machine equipped with a 2.5 kN load cell using a crosshead speed equal to 2 mm/min and with a MTS 632.29F-30 extensometer. The specimen geometry was chosen according to the ISO 527-2 suggestions [47]. Five specimens were tested for each clay content in order to obtain statistical representative results. In all cases, failure took place in the gauge length of the specimens. Fracture tests were carried out on compact tension (CT) specimens of which the geometry and size comply with ASTM D5045-99 suggestions [48]. According to previously reported procedures [49–51], after demoulding, specimens were precracked by manual tapping, obtaining artificial short cracks. Then 10 mm long cracks were obtained by loading the tapped samples with some zero-to-tension fatigue cycles. For each composite, five specimens were tested. Experimental results were rearranged, and for each test, the value of KIC was determined starting from the crack length and the fracture load, according to ASTM D5045 [48].


## 2.3.6. Thermogravimetric Analysis

TGA were performed on a TGAQ 5000 thermogravimetric analyser, TA Instruments, under air atmosphere: 15-20 mg of the samples were heated from 25°C to 900°C under air atmosphere with a heating rate of 10°C/min.


## 2.3.7. Zero Surface Charge Determination

By using the solid addition method [52], the zero surface charge characteristics of the epoxy/clay nanocomposites were determined. In a series of 50 ml of 0.1 M KNO3 solution, the pH0 values were adjusted to 2, 4, 6, 8, and 10 by adding either 0.1 M HCl or 0.1 M NaOH. Then, one gram of crushed specimens was added to each flask. The suspensions were then manually shaken and allowed to equilibrate for 48 h with intermittent manual shaking. The final pH values of the supernatant liquid were noted. The difference between the initial pH (pH0) and the final one (pHf) values (pH=pH0−pHf) was plotted against the pH0. The point of intersection of the resulting curve with abscissa, at which pH=0, gave the pHpzc.


## 2.4. Antimicrobial Activity

### 2.4.1. Antimicrobial Activity of the Raw Clays

The antimicrobial activity of clays has been determined againstEscherichia coli (E. coli) TCC 8739 and Staphylococcus aureus (S. aureus) ATCC 6538P, selected as examples of Gram-negative and Gram-positive bacteria as recommended by ISO 22196 [53] following the procedure previously reported [35]. Both bacteria were cultured overnight at 35°C onto Tryptic Soy Agar (TSA) before use and diluted in Nutrient Broth (NB) 1 : 500 with distilled water in order to obtain suspensions containing 105-108 cells/ml, suitable for the experiments. Sterilized clays (1 g) were introduced into 800 μl of NB containing the initial pathogen inoculum, and the mixtures were incubated at 35°C for 24 h. Positive controls for growth of bacteria in the absence of clays were carried out together with each series of experiments. In addition, negative controls were performed in order to ensure that the clay samples maintained sterilization during storage. After incubation, the mixtures were subjected to successive 10-fold dilutions in distilled sterilized water and quantitatively cultured in duplicate onto TSA plates to determine the number of viable bacteria. Viable cell counts are expressed as log10cfu per 800 μl.


### 2.4.2. Antibacterial Activity of the Nanocomposites

The surface biocidal capacity of the nanocomposites has been evaluated againstE. coli ATCC 8739 and S. aureus ATCC 6538P according to ISO 22196 and OECD guidelines [53, 54] and following the procedure previously described [35]. Each strain microbial testing was performed in triplicate: 6 specimens of neat epoxy resins were used as control (3 for t=0 and 3 for t=24hours) and 3 samples of each nanocomposite were tested. The samples were treated with a sterilizing UV irradiation, then an area of 4 cm2 was coated with 50 μl (12.5 μl/cm2) of suspension of diluted bacteria in NB containing 105-107 cells and incubated for 24 hrs at 35°C. The bacteria were recovered by adding 10 ml of soybean casein digest with lecithin and polysorbate neutralizer broth (SCDLP) and 10-fold serial diluted in phosphate-buffered physiological saline solution. Then, 1 ml of each dilution was put into Petri dishes with 15 ml of Molten Plate Count Agar (PCA) and incubated at 35°C for 40 hrs (all the platings were performed in duplicate). Results were expressed as the number of units forming colonies (cfu) per cm2, and the percentage of inhibition was calculated with the equation established in the standard test method ASTM E2149-01 [55] comparing data with reference samples.


## 2.4.1. Antimicrobial Activity of the Raw Clays

The antimicrobial activity of clays has been determined againstEscherichia coli (E. coli) TCC 8739 and Staphylococcus aureus (S. aureus) ATCC 6538P, selected as examples of Gram-negative and Gram-positive bacteria as recommended by ISO 22196 [53] following the procedure previously reported [35]. Both bacteria were cultured overnight at 35°C onto Tryptic Soy Agar (TSA) before use and diluted in Nutrient Broth (NB) 1 : 500 with distilled water in order to obtain suspensions containing 105-108 cells/ml, suitable for the experiments. Sterilized clays (1 g) were introduced into 800 μl of NB containing the initial pathogen inoculum, and the mixtures were incubated at 35°C for 24 h. Positive controls for growth of bacteria in the absence of clays were carried out together with each series of experiments. In addition, negative controls were performed in order to ensure that the clay samples maintained sterilization during storage. After incubation, the mixtures were subjected to successive 10-fold dilutions in distilled sterilized water and quantitatively cultured in duplicate onto TSA plates to determine the number of viable bacteria. Viable cell counts are expressed as log10cfu per 800 μl.


## 2.4.2. Antibacterial Activity of the Nanocomposites

The surface biocidal capacity of the nanocomposites has been evaluated againstE. coli ATCC 8739 and S. aureus ATCC 6538P according to ISO 22196 and OECD guidelines [53, 54] and following the procedure previously described [35]. Each strain microbial testing was performed in triplicate: 6 specimens of neat epoxy resins were used as control (3 for t=0 and 3 for t=24hours) and 3 samples of each nanocomposite were tested. The samples were treated with a sterilizing UV irradiation, then an area of 4 cm2 was coated with 50 μl (12.5 μl/cm2) of suspension of diluted bacteria in NB containing 105-107 cells and incubated for 24 hrs at 35°C. The bacteria were recovered by adding 10 ml of soybean casein digest with lecithin and polysorbate neutralizer broth (SCDLP) and 10-fold serial diluted in phosphate-buffered physiological saline solution. Then, 1 ml of each dilution was put into Petri dishes with 15 ml of Molten Plate Count Agar (PCA) and incubated at 35°C for 40 hrs (all the platings were performed in duplicate). Results were expressed as the number of units forming colonies (cfu) per cm2, and the percentage of inhibition was calculated with the equation established in the standard test method ASTM E2149-01 [55] comparing data with reference samples.


## 3. Results and Discussion

### 3.1. Natural Clay Characterization

The fractions below 80μm of unmodified clays used as raw material have been firstly characterized to obtain an overview of their characteristics and properties [46]. The results, collected in Table 1, revealed their mineralogical and chemical composition. All the samples contained quartz, kaolinite, micas (mainly illite and/or muscovite), and expansible minerals (such as mixed layers, smectite, or vermiculite) associated with other clays and nonclay minerals. For A1, A2, and A3, chlorite, pyrophyllite, and calcite were also present; A4 contained feldspars, calcite, and dolomite while A5 had goethite. The chemical compositions of the five Moroccan clays showed that the powders had a high content of silica due to the presence of quartz and other silicates, together with alumina. K2O, MgO, and Na2O were present in small quantities, and their amounts were associated with the occurrence of illite, chlorite, feldspars, and mixed layers in agreement with the mineralogical composition. Iron can be incorporated into clays minerals as oxides and hydroxides, as observed for A1, A2, A3, and A5. Only A4 contained an important amount of CaO (18.80% wt) and the highest content of MgO, according to the occurrence of calcite and dolomite. A5 was characterized by the highest content of SiO2 (62.70% wt) and the lowest amount of MgO, which explained the high quartz content and the absence of chlorite. It should be noted that A1 and A4 have been recently used to prepare geopolymers [56].


### 3.2. Epoxy/Clay Nanocomposite Characterization

A few publications described the preparation of epoxy/clay nanocomposites with the incorporation of unmodified clay [57] or minerals [58]. Herein, we studied the dispersion of some natural clays in the absence of organic modification within the epoxy resin matrix and described the chemical and physical characterization of the nanocomposites.The FTIR spectra (FigureSI.1) resulted in being slightly modified with respect to the spectrum of the pristine epoxy resin (the strong absorptions of νCCaromatic, νCCOC, νCN, and νCOC ethers and νCOC oxirane were present at 1508, 1239, 1104, 1032, and 827 cm-1, respectively) along with an increased broad band at 3392 cm-1 of the OH stretching of Si-OH and Al-OH and of the hydroxyl groups present in the epoxy matrix [35, 36]. Only in the case of EA4 was a broadening of the signal at 1450 cm-1 observed due to the presence of a strong and broad signal in A4 at 1430 cm-1 of calcite.In Figure1, selected XRD spectra (Figure SI.2) of the nanocomposites have been reported. The spectra exhibited the signals corresponding to the crystalline phases of the original clay. No clear evidence of the presence of intercalated systems could be observed, reasonably due to the use of raw clays, without previous pretreatment with organic components.Figure 1
XRD spectra of claysA2 and A4 and of the corresponding nanocomposites EA25% and EA45%. chl: chlorite; mica: illite and/or muscovite; pyr: pyrophyllite; ka: kaolinite; mix-l: mixed layers.ESEM analyses of the fracture surfaces (Figure2) revealed a homogeneous distribution of the clay in all epoxy resin nanocomposites even with 5% wt of clay content with some agglomeration of the particles, which were distributed along the brittle fracture surface up to a size of few microns, particularly in the EA2 and EA4 samples. Micrographs showed the silicate layer penetration in between the epoxy network, as well as the different paths of the crack, particularly for EA3 where the higher amount of phyllosilicates [46] could lead to a better intercalation in the composite. The clay particles reasonably acted as obstacles causing the crack. Liu et al. [59] reported that more than one toughening mechanism usually occurs in the epoxy/clay system such as shear yielding of the matrix, crack deflection (evidenced in the EA1, EA2, EA4, and EA5 samples), micro voiding, and debonding between the clay and epoxy (as observed for EA3) [60].Figure 2
ESEM images of the fracture surfaces of epoxy/clay nanocomposite specimens with 5% wt clay content (scale bar 50μm).TEM analyses (Figure3) showed some exfoliated and intercalated structures (in particular for the samples bearing 5% of clay) together with a bigger stack of platelets dispersed inside the epoxy matrix. Composite EA35% displays the smallest clay agglomerates with exfoliated fragments compared with the other samples, in agreement with the suggested effect of the higher phyllosilicate content on the intercalation.Figure 3
TEM images of selected nanocomposites containing 1% wt and 5% wt of clay loading.


### 3.3. Thermal Stability of the Nanocomposites

In Figure4, the thermograms of the nanocomposites have been shown, and in Table 2, the onset temperature of thermal degradation and the percentage of residue after thermal degradation have been reported. It could be observed that the incorporation of unmodified clays decreased to some degrees (from 319°C to about 315°C) the thermal degradation onset in the presence of 1% of clay and about one degree more in the presence of 5% wt for A1-A4. In the case of A5, an increase up to 325°C was observed for 1% of clay, but a decrease to 310°C for 5%. This behavior could be in principle explained by the low level of intercalation within the nanocomposite and by a catalytic effect on the thermal degradation of the epoxy matrix of the metal oxides (in particular iron oxide) in the clays [61].Figure 4
TGA of neat epoxy and epoxy/clay nanocomposites with (a) 1% wt and (b) 5% wt of clay loading.
(a)
(b)Table 2
Residue of neat epoxy and epoxy/clay nanocomposites after thermal treatment until 900°C.
Sample
Neat epoxy resin
EA11%
EA15%
EA21%
EA25%
EA31%
EA35%
EA41%
EA45%
EA51%
EA55%
Onset of thermal degradation (°C)
319.36
315.24
314.25
314.19
313.85
315.13
315.44
316.60
315.01
325.24
310.80
Initial weight (mg)
17.73
21.06
17.66
23.29
16.81
20.14
17.03
21.52
22.72
17.67
21.13
Residue (mg)
0.076
0.275
1.200
0.349
0.826
0.073
0.491
0.131
0.903
0.773
0.771
Residue (% wt)
0.48
1.31
6.80
1.50
4.91
0.36
2.89
0.61
3.98
3.38
4.65


### 3.4. Mechanical Properties of the Nanocomposites

The effect of the weight content of nanoclay on the nanocomposite strain to failure (εR), tensile strength (σR), and Young’s modulus (E) is shown in Figure 5. In particular, it was evident from Figure 5(a) that the addition of 1% wt of nanoclays to the epoxy resin always resulted in an increase of the strain to failure. Such an increase was limited, in the case of A2 and A3, whereas it was pronounced for A1, A4, and A5. A reverse trend could be noted, instead, in the case of 5% wt clay nanocomposites, which exhibited a strain to failure almost equal or lower than that of the neat polymer. Similar to the results for the strain to failure, as reported in Figure 5(b), the incorporation of a low amount of unmodified clay (1% wt) allowed the tensile strength σR to be considerably improved (from 59.99 to 68.77, 67.60, 70.51, and 76.10 MPa in the case of EA11%, EA21%, EA41%, and EA51%, respectively, when compared to neat epoxy resin). The increase of the weight content (from 1% to 5% wt) gave a decrease of σR for A1, A2, and A3, whilst nanocomposites EA45% and EA55% still preserved an enhanced tensile strength. The decrease of the tensile properties while increasing the clay loading (5%) was in agreement with the results previously reported for epoxy resins in the literature [35, 36, 49–51]. The obtained results showing that a small amount of unmodified clay (1%wt) allowed the improvement of strain to failure and tensile strength of the nanocomposites indicated a good dispersion of the clays, in particular in the case of A5. This effect could be attributed to the large interfacial interaction between the matrix and the clay, the aspect ratio of the dispersed clay particle, and the nanometer scale clay particle dimension. It is noteworthy that here an improvement of mechanical properties was observed at a lower value (1% wt) of clay content with respect to the amount often considered necessary for a reinforcement of the nanocomposite (3%) [61, 62]. It should be noted that comparable results have been reported for the epoxy/clay nanocomposite bearing an interpenetrating PEO network, where the best mechanical properties have been obtained with 1% wt clay (MMT) content [63].Figure 5
Strain to failure (a), tensile strength (b), and Young’s modulus (c) of neat epoxy and epoxy/clay nanocomposites with 1% wt and 5% wt loading ofA1, A2, A3, A4, and A5 clays.
(a)
(b)
(c)As evident from Figure5(c), the addition of unmodified clays had a detrimental effect on the elastic modulus, E, except for EA41%.


### 3.5. Fracture Tests

As far as fracture tests are concerned, 5 CT specimens were used for each material configuration and the results forKIC in terms of average values are reported in Figure 6. It is noteworthy that, different from tensile properties, the mode I fracture toughness presented a monotonic increase with the filler content increase (except for the A5 nanoclay), in agreement with the behavior reported in the literature [64]. Based on the experimental results, the most effective toughening clay was A3, which allowed the epoxy resin fracture toughness to be increased from 0.96 MPa m0.5 (neat polymer) to about 1.22 for filler content of 1% and up to about 1.35 MPa m0.5 with a weight fraction of 5% of nanoclays.Figure 6
Effect of the nanomodification of the epoxy resin on the fracture toughness. The mean value and the scatter band of the values for neat epoxy is given by the black solid and dashed lines, respectively.


### 3.6. Point of Zero Charge (pHpzc)

The point of zero charge is a very important characteristic that allows to determine the pH at which the material has net electrical neutrality. In Figure7, the plots of ΔpH (pH0–pHf) vs. pH0 are reported. The point of zero charge for neat epoxy was found to be 6.2 and that of epoxy/clay nanocomposites prepared with 1% of A1 (EA11%), A4 (EA41%), and A5 (EA51%) were 6.9, 7, and 6.7, respectively, whereas those of EA21% and EA31% had approximately the same pHpzc of neat epoxy. By increasing the concentration of clay particles from 1 to 5% wt, the pHpzc remains in the same order with a variation of ≈0.1 units. It was observed that pHpzc of neat epoxy was lower than that of EA4 nanocomposites, and it was higher than that of EA1 nanocomposites. This variation in pHpzc could be related to the difference in the surface functional groups of the materials, in particular OH and NH on the epoxy resin. They can interact in different ways and extent with the complex mixture of metals present in the raw clay materials, thus depending on their composition. It should be noted that in the case of EA4 composites, bearing a higher carbonate content, pHpzc resulted in an increase in comparison with the neat epoxy resin.Figure 7
Determination of the point of zero charge of (a) the nanocomposites prepared with 1% and (b) the nanocomposites prepared with 5% of clay by the solid addition method.
(a)
(b)


### 3.7. Antimicrobial Activity of Clays and Nanocomposites

The emergence of an increasing number of antibiotic-resistant strains of bacteria has significantly boosted the research for new antibacterial materials. In particular, some intriguing studies have been recently reported concerning natural clays [38–44]. As for natural clays A1-A5, the data concerning their activity against E. coli and S. aureus have been collected in Figure 8. We observed that all clays under investigation did not show bacteriostatic or biocidal activity against E. coli, while a biocidal activity corresponding to a reduction of 22% of units forming colonies was observed in the case of A1 and A3 and 24% for A2 against S. aureus. The activity resulted in being lower (7%) in the case of A4, while for A5, the reduction was significantly higher (42%).Figure 8
Biological activity of the natural claysA1–A5 against E. coli and S. aureus.
(a)
(b)The antibacterial activity of the epoxy polymer loading natural clays has been established by measuring the growth inhibition of selected bacteria in comparison with the controls. The results have been collected in Table3. The presence of clays A1, A2, and A3 in the epoxy clay nanocomposites did not induce any bacteriostatic activity against E. coli either at 1% wt or 5% wt compared to neat epoxy resin; on the contrary, a moderate antibacterial activity could be observed against S. aureus in the case of A2 and A3. EA4 showed an antibacterial activity against either E. coli or S. aureus depending on the clay amount: the killing percentage of EA45% against S. aureus was 99.88%. The highest antibacterial activity against E. coli was observed for EA51% and EA55%, whereas against S. aureus, EA45%, EA51%, and EA55% registered the highest effects (killing percentage of EA55% against E. coli and S. aureus raised up 99.86% and 99.99%, respectively).Table 3
Antibacterial activity of epoxy/clay nanocomposites againstE. coli and S. aureus.
Ech.
Control
EA1
EA2
EA3
EA4
EA5
1%
5%
1%
5%
1%
5%
1%
5%
1%
5%
E. coli
cfu/50μl
1.6∗105
5.5∗106
5.8∗106
1.5∗106
2∗107
1.8∗107
6.7∗106
1.9∗104
1.1∗104
<10
2.24∗102
cfu/cm2
4∗104
1.4∗106
1.5∗106
3.8∗105
5∗106
4.5∗106
1.7∗106
4.75∗103
2.7∗103
<10
56
% kill
—
—
—
—
—
—
—
88.12
93.12
99.99
99.86
S. aureus
cfu/50μl
1.9∗106
1.5∗106
105∗106
2.9∗105
7.3∗105
3.1∗105
3.1∗105
8.9∗105
2.28∗103
1.9∗102
1.9∗102
cfu/cm2
4.8∗105
3.8∗105
3.8∗105
7.3∗104
1.8∗105
7.8∗104
7.8∗104
2.24∗105
5.7∗102
47.5
47.5
% kill
—
20.83
20.83
84.79
62.5
83.75
83.75
87.78
99.88
99.99
99.99For nanocomposites loaded withA1, A2, and A3, our hypothesis is that the presence of chlorite and a high amount of Al2O3 and Na2O could cause the antibacterial activity in particular against S. aureus, which has a much less complicated cell wall structure than Gram-negative bacteria and lower dimension than E. coli [65], thus being more sensible to biocidal systems (reported diameter of S. aureus 0.5-1 μm; length of E. coli 1.5-2 μm). As for the biocidal activity of nanocomposites containing A4 and A5, it could be explained with the high content of calcium (for A4) and iron (for A5), in agreement with the data reported in the literature [41, 66]. The occurrence of low-ordered iron mineral phases (goethite) in A5 enhances the solubility of iron compared to silicates and crystalline oxides. The improvement of the activity of nanocomposites with respect to the free clays could be explained with the availability of a support for bacteria adhesion which could improve the contact with bactericidal clays and the surface. The EA5 surface had also the farthest pH value with respect to the nutrient broth (6.8), enhancing possible electrical interaction with the negative cell wall of bacteria, whereas for EA4, the nutrient medium sustained carbonate dissolution and then Ca, Mg (possibly also Fe2+) solubilisation. The results are in agreement with some observations previously reported concerning nanocomposites exhibiting antimicrobial activity for which two mechanisms are proposed: activity of surfactant release from the clay and the action of the solid surface [67, 68].It is noteworthy that the biocidal activity of the nanocomposites described here is comparable with the data reported for nanocomposites loading silver ions, which are the most used bactericidal agents [69, 70]. As an example, TiO2/Ag+ exchanged montmorillonite in polyacrylic latex coatings produced an antibacterial effect at 1% wt content [69], and a similar effect was reported for silver-embedded epoxy/clay nanocomposites at 2.5% wt content [38].


## 3.1. Natural Clay Characterization

The fractions below 80μm of unmodified clays used as raw material have been firstly characterized to obtain an overview of their characteristics and properties [46]. The results, collected in Table 1, revealed their mineralogical and chemical composition. All the samples contained quartz, kaolinite, micas (mainly illite and/or muscovite), and expansible minerals (such as mixed layers, smectite, or vermiculite) associated with other clays and nonclay minerals. For A1, A2, and A3, chlorite, pyrophyllite, and calcite were also present; A4 contained feldspars, calcite, and dolomite while A5 had goethite. The chemical compositions of the five Moroccan clays showed that the powders had a high content of silica due to the presence of quartz and other silicates, together with alumina. K2O, MgO, and Na2O were present in small quantities, and their amounts were associated with the occurrence of illite, chlorite, feldspars, and mixed layers in agreement with the mineralogical composition. Iron can be incorporated into clays minerals as oxides and hydroxides, as observed for A1, A2, A3, and A5. Only A4 contained an important amount of CaO (18.80% wt) and the highest content of MgO, according to the occurrence of calcite and dolomite. A5 was characterized by the highest content of SiO2 (62.70% wt) and the lowest amount of MgO, which explained the high quartz content and the absence of chlorite. It should be noted that A1 and A4 have been recently used to prepare geopolymers [56].


## 3.2. Epoxy/Clay Nanocomposite Characterization

A few publications described the preparation of epoxy/clay nanocomposites with the incorporation of unmodified clay [57] or minerals [58]. Herein, we studied the dispersion of some natural clays in the absence of organic modification within the epoxy resin matrix and described the chemical and physical characterization of the nanocomposites.The FTIR spectra (FigureSI.1) resulted in being slightly modified with respect to the spectrum of the pristine epoxy resin (the strong absorptions of νCCaromatic, νCCOC, νCN, and νCOC ethers and νCOC oxirane were present at 1508, 1239, 1104, 1032, and 827 cm-1, respectively) along with an increased broad band at 3392 cm-1 of the OH stretching of Si-OH and Al-OH and of the hydroxyl groups present in the epoxy matrix [35, 36]. Only in the case of EA4 was a broadening of the signal at 1450 cm-1 observed due to the presence of a strong and broad signal in A4 at 1430 cm-1 of calcite.In Figure1, selected XRD spectra (Figure SI.2) of the nanocomposites have been reported. The spectra exhibited the signals corresponding to the crystalline phases of the original clay. No clear evidence of the presence of intercalated systems could be observed, reasonably due to the use of raw clays, without previous pretreatment with organic components.Figure 1
XRD spectra of claysA2 and A4 and of the corresponding nanocomposites EA25% and EA45%. chl: chlorite; mica: illite and/or muscovite; pyr: pyrophyllite; ka: kaolinite; mix-l: mixed layers.ESEM analyses of the fracture surfaces (Figure2) revealed a homogeneous distribution of the clay in all epoxy resin nanocomposites even with 5% wt of clay content with some agglomeration of the particles, which were distributed along the brittle fracture surface up to a size of few microns, particularly in the EA2 and EA4 samples. Micrographs showed the silicate layer penetration in between the epoxy network, as well as the different paths of the crack, particularly for EA3 where the higher amount of phyllosilicates [46] could lead to a better intercalation in the composite. The clay particles reasonably acted as obstacles causing the crack. Liu et al. [59] reported that more than one toughening mechanism usually occurs in the epoxy/clay system such as shear yielding of the matrix, crack deflection (evidenced in the EA1, EA2, EA4, and EA5 samples), micro voiding, and debonding between the clay and epoxy (as observed for EA3) [60].Figure 2
ESEM images of the fracture surfaces of epoxy/clay nanocomposite specimens with 5% wt clay content (scale bar 50μm).TEM analyses (Figure3) showed some exfoliated and intercalated structures (in particular for the samples bearing 5% of clay) together with a bigger stack of platelets dispersed inside the epoxy matrix. Composite EA35% displays the smallest clay agglomerates with exfoliated fragments compared with the other samples, in agreement with the suggested effect of the higher phyllosilicate content on the intercalation.Figure 3
TEM images of selected nanocomposites containing 1% wt and 5% wt of clay loading.


## 3.3. Thermal Stability of the Nanocomposites

In Figure4, the thermograms of the nanocomposites have been shown, and in Table 2, the onset temperature of thermal degradation and the percentage of residue after thermal degradation have been reported. It could be observed that the incorporation of unmodified clays decreased to some degrees (from 319°C to about 315°C) the thermal degradation onset in the presence of 1% of clay and about one degree more in the presence of 5% wt for A1-A4. In the case of A5, an increase up to 325°C was observed for 1% of clay, but a decrease to 310°C for 5%. This behavior could be in principle explained by the low level of intercalation within the nanocomposite and by a catalytic effect on the thermal degradation of the epoxy matrix of the metal oxides (in particular iron oxide) in the clays [61].Figure 4
TGA of neat epoxy and epoxy/clay nanocomposites with (a) 1% wt and (b) 5% wt of clay loading.
(a)
(b)Table 2
Residue of neat epoxy and epoxy/clay nanocomposites after thermal treatment until 900°C.
Sample
Neat epoxy resin
EA11%
EA15%
EA21%
EA25%
EA31%
EA35%
EA41%
EA45%
EA51%
EA55%
Onset of thermal degradation (°C)
319.36
315.24
314.25
314.19
313.85
315.13
315.44
316.60
315.01
325.24
310.80
Initial weight (mg)
17.73
21.06
17.66
23.29
16.81
20.14
17.03
21.52
22.72
17.67
21.13
Residue (mg)
0.076
0.275
1.200
0.349
0.826
0.073
0.491
0.131
0.903
0.773
0.771
Residue (% wt)
0.48
1.31
6.80
1.50
4.91
0.36
2.89
0.61
3.98
3.38
4.65


## 3.4. Mechanical Properties of the Nanocomposites

The effect of the weight content of nanoclay on the nanocomposite strain to failure (εR), tensile strength (σR), and Young’s modulus (E) is shown in Figure 5. In particular, it was evident from Figure 5(a) that the addition of 1% wt of nanoclays to the epoxy resin always resulted in an increase of the strain to failure. Such an increase was limited, in the case of A2 and A3, whereas it was pronounced for A1, A4, and A5. A reverse trend could be noted, instead, in the case of 5% wt clay nanocomposites, which exhibited a strain to failure almost equal or lower than that of the neat polymer. Similar to the results for the strain to failure, as reported in Figure 5(b), the incorporation of a low amount of unmodified clay (1% wt) allowed the tensile strength σR to be considerably improved (from 59.99 to 68.77, 67.60, 70.51, and 76.10 MPa in the case of EA11%, EA21%, EA41%, and EA51%, respectively, when compared to neat epoxy resin). The increase of the weight content (from 1% to 5% wt) gave a decrease of σR for A1, A2, and A3, whilst nanocomposites EA45% and EA55% still preserved an enhanced tensile strength. The decrease of the tensile properties while increasing the clay loading (5%) was in agreement with the results previously reported for epoxy resins in the literature [35, 36, 49–51]. The obtained results showing that a small amount of unmodified clay (1%wt) allowed the improvement of strain to failure and tensile strength of the nanocomposites indicated a good dispersion of the clays, in particular in the case of A5. This effect could be attributed to the large interfacial interaction between the matrix and the clay, the aspect ratio of the dispersed clay particle, and the nanometer scale clay particle dimension. It is noteworthy that here an improvement of mechanical properties was observed at a lower value (1% wt) of clay content with respect to the amount often considered necessary for a reinforcement of the nanocomposite (3%) [61, 62]. It should be noted that comparable results have been reported for the epoxy/clay nanocomposite bearing an interpenetrating PEO network, where the best mechanical properties have been obtained with 1% wt clay (MMT) content [63].Figure 5
Strain to failure (a), tensile strength (b), and Young’s modulus (c) of neat epoxy and epoxy/clay nanocomposites with 1% wt and 5% wt loading ofA1, A2, A3, A4, and A5 clays.
(a)
(b)
(c)As evident from Figure5(c), the addition of unmodified clays had a detrimental effect on the elastic modulus, E, except for EA41%.


## 3.5. Fracture Tests

As far as fracture tests are concerned, 5 CT specimens were used for each material configuration and the results forKIC in terms of average values are reported in Figure 6. It is noteworthy that, different from tensile properties, the mode I fracture toughness presented a monotonic increase with the filler content increase (except for the A5 nanoclay), in agreement with the behavior reported in the literature [64]. Based on the experimental results, the most effective toughening clay was A3, which allowed the epoxy resin fracture toughness to be increased from 0.96 MPa m0.5 (neat polymer) to about 1.22 for filler content of 1% and up to about 1.35 MPa m0.5 with a weight fraction of 5% of nanoclays.Figure 6
Effect of the nanomodification of the epoxy resin on the fracture toughness. The mean value and the scatter band of the values for neat epoxy is given by the black solid and dashed lines, respectively.


## 3.6. Point of Zero Charge (pHpzc)

The point of zero charge is a very important characteristic that allows to determine the pH at which the material has net electrical neutrality. In Figure7, the plots of ΔpH (pH0–pHf) vs. pH0 are reported. The point of zero charge for neat epoxy was found to be 6.2 and that of epoxy/clay nanocomposites prepared with 1% of A1 (EA11%), A4 (EA41%), and A5 (EA51%) were 6.9, 7, and 6.7, respectively, whereas those of EA21% and EA31% had approximately the same pHpzc of neat epoxy. By increasing the concentration of clay particles from 1 to 5% wt, the pHpzc remains in the same order with a variation of ≈0.1 units. It was observed that pHpzc of neat epoxy was lower than that of EA4 nanocomposites, and it was higher than that of EA1 nanocomposites. This variation in pHpzc could be related to the difference in the surface functional groups of the materials, in particular OH and NH on the epoxy resin. They can interact in different ways and extent with the complex mixture of metals present in the raw clay materials, thus depending on their composition. It should be noted that in the case of EA4 composites, bearing a higher carbonate content, pHpzc resulted in an increase in comparison with the neat epoxy resin.Figure 7
Determination of the point of zero charge of (a) the nanocomposites prepared with 1% and (b) the nanocomposites prepared with 5% of clay by the solid addition method.
(a)
(b)


## 3.7. Antimicrobial Activity of Clays and Nanocomposites

The emergence of an increasing number of antibiotic-resistant strains of bacteria has significantly boosted the research for new antibacterial materials. In particular, some intriguing studies have been recently reported concerning natural clays [38–44]. As for natural clays A1-A5, the data concerning their activity against E. coli and S. aureus have been collected in Figure 8. We observed that all clays under investigation did not show bacteriostatic or biocidal activity against E. coli, while a biocidal activity corresponding to a reduction of 22% of units forming colonies was observed in the case of A1 and A3 and 24% for A2 against S. aureus. The activity resulted in being lower (7%) in the case of A4, while for A5, the reduction was significantly higher (42%).Figure 8
Biological activity of the natural claysA1–A5 against E. coli and S. aureus.
(a)
(b)The antibacterial activity of the epoxy polymer loading natural clays has been established by measuring the growth inhibition of selected bacteria in comparison with the controls. The results have been collected in Table3. The presence of clays A1, A2, and A3 in the epoxy clay nanocomposites did not induce any bacteriostatic activity against E. coli either at 1% wt or 5% wt compared to neat epoxy resin; on the contrary, a moderate antibacterial activity could be observed against S. aureus in the case of A2 and A3. EA4 showed an antibacterial activity against either E. coli or S. aureus depending on the clay amount: the killing percentage of EA45% against S. aureus was 99.88%. The highest antibacterial activity against E. coli was observed for EA51% and EA55%, whereas against S. aureus, EA45%, EA51%, and EA55% registered the highest effects (killing percentage of EA55% against E. coli and S. aureus raised up 99.86% and 99.99%, respectively).Table 3
Antibacterial activity of epoxy/clay nanocomposites againstE. coli and S. aureus.
Ech.
Control
EA1
EA2
EA3
EA4
EA5
1%
5%
1%
5%
1%
5%
1%
5%
1%
5%
E. coli
cfu/50μl
1.6∗105
5.5∗106
5.8∗106
1.5∗106
2∗107
1.8∗107
6.7∗106
1.9∗104
1.1∗104
<10
2.24∗102
cfu/cm2
4∗104
1.4∗106
1.5∗106
3.8∗105
5∗106
4.5∗106
1.7∗106
4.75∗103
2.7∗103
<10
56
% kill
—
—
—
—
—
—
—
88.12
93.12
99.99
99.86
S. aureus
cfu/50μl
1.9∗106
1.5∗106
105∗106
2.9∗105
7.3∗105
3.1∗105
3.1∗105
8.9∗105
2.28∗103
1.9∗102
1.9∗102
cfu/cm2
4.8∗105
3.8∗105
3.8∗105
7.3∗104
1.8∗105
7.8∗104
7.8∗104
2.24∗105
5.7∗102
47.5
47.5
% kill
—
20.83
20.83
84.79
62.5
83.75
83.75
87.78
99.88
99.99
99.99For nanocomposites loaded withA1, A2, and A3, our hypothesis is that the presence of chlorite and a high amount of Al2O3 and Na2O could cause the antibacterial activity in particular against S. aureus, which has a much less complicated cell wall structure than Gram-negative bacteria and lower dimension than E. coli [65], thus being more sensible to biocidal systems (reported diameter of S. aureus 0.5-1 μm; length of E. coli 1.5-2 μm). As for the biocidal activity of nanocomposites containing A4 and A5, it could be explained with the high content of calcium (for A4) and iron (for A5), in agreement with the data reported in the literature [41, 66]. The occurrence of low-ordered iron mineral phases (goethite) in A5 enhances the solubility of iron compared to silicates and crystalline oxides. The improvement of the activity of nanocomposites with respect to the free clays could be explained with the availability of a support for bacteria adhesion which could improve the contact with bactericidal clays and the surface. The EA5 surface had also the farthest pH value with respect to the nutrient broth (6.8), enhancing possible electrical interaction with the negative cell wall of bacteria, whereas for EA4, the nutrient medium sustained carbonate dissolution and then Ca, Mg (possibly also Fe2+) solubilisation. The results are in agreement with some observations previously reported concerning nanocomposites exhibiting antimicrobial activity for which two mechanisms are proposed: activity of surfactant release from the clay and the action of the solid surface [67, 68].It is noteworthy that the biocidal activity of the nanocomposites described here is comparable with the data reported for nanocomposites loading silver ions, which are the most used bactericidal agents [69, 70]. As an example, TiO2/Ag+ exchanged montmorillonite in polyacrylic latex coatings produced an antibacterial effect at 1% wt content [69], and a similar effect was reported for silver-embedded epoxy/clay nanocomposites at 2.5% wt content [38].


## 4. Conclusion

The data described here showed that it is possible to obtain epoxy resin nanocomposites even when using suitable unmodified natural clays, if strongly milled and using exclusively the thinner fraction. TEM analysis indicated that partially intercalated systems could be achieved. The most intriguing results have been represented by the improvement of the mechanical properties in the presence of 1% wt of clay and of the onset temperature of thermal degradation in the case of 1% wt ofA5.Furthermore, biocidal activity againstS. aureus was observed for all the nanocomposites, and in the presence of A4 and A5, the antimicrobial action was evidenced also against E. coli even in the presence of a low amount of clays.These results suggest further investigating the direct influence of the single components of the natural clays on the thermal, mechanical, and biocidal properties of the composite, in order to analyse the metal ion release kinetics and verify the antimicrobial effect at a longer term with the aim to modulate the characteristics of the nanocomposites for practical and industrial application, paying particular attention to the preparation of new antimicrobial materials, providing an alternative to surface modification or coating technologies.



---

*Source: 2810901-2019-11-22.xml*