# The Degradation of Mechanical Properties in Halloysite Nanoclay-Polyester Nanocomposites Exposed in Seawater Environment

Authors: Mohd Shahneel Saharudin; Jiacheng Wei; Islam Shyha; Fawad Inam
Journal: Journal of Nanomaterials
 (2016)

---

## Abstract

Polyester based polymers are extensively used in aggressive marine environments; however, inadequate data is available on the effects of the seawater on the polyester based nanocomposites mechanical properties. This paper reports the effect of seawater absorption on the mechanical properties degradation of halloysite nanoclay-polyester nanocomposites. Results confirmed that the addition of halloysite nanoclay into polyester matrix was found to increase seawater uptake and reduce mechanical properties compared to monolithic polyester. The maximum decreases in microhardness, tensile and flexural properties, and impact toughness were observed in case of 1 wt% nanoclay. The microhardness decreased from 107 HV to 41.7 HV (61% decrease). Young’s modulus decreased from 0.6 GPa to 0.4 GPa (33% decrease). The flexural modulus decreased from 0.6 GPa to 0.34 GPa (43% decrease). The impact toughness dropped from 0.71 kJ/m2 to 0.48 kJ/m2 (32% decrease). Interestingly, the fracture toughness KIC increased with the addition of halloysite nanoclay due to the plasticization effect of the resin matrix. SEM images revealed the significant reduction in mechanical properties in case of 1 wt% reinforcement which is attributed to the degradation of the nanoclay-matrix interface influenced by seawater absorption and agglomeration of halloysite nanoclay.


---

## Body

## 1. Introduction

Thermosetting polymers are used in various industrial applications [1]. In the marine environment, complex conditions such as high salinity, high pressure, high humidity, and alkaline corrosion accelerate the degradation of polymers and greatly reduce their reliability [2]. Bottles, vessels, and pipes are some of the common applications where seawater contact is unavoidable and can lead to the loss of inherent mechanical properties [3]. Unsaturated polyester (UP) resins are widely used in boat components, pipes, tanks, building panels, and automobiles due to their ease in processing, low viscosity, and relatively high chemical and corrosion resistance [4–6]. The formation of a three-dimensional cross-linking structure in UP from free-radical copolymerization between low molar mass that possesses several covalent C=C bonds and the styrene produced localised plastic deformation in front of the crack tip, which leads to brittle failure [7]. So far, many studies have been carried out on thermoset polymers, epoxy, and phenolic and unsaturated polyester in order to improve their mechanical properties and reduce damage severity without losing their strength and stiffness. Numerous synthetic fibres (glass, carbon, Kevlar, etc.) have been increasingly used in producing good mechanical properties composite materials with low cost and light weight [7–13]. The rises of the utilisation of nanoreinforcements (e.g., carbon nanotubes, nano-SiO2, nano-Al2O3 nanocrystalline metals, and nano-TiO2) and nanoclays have navigated the orientation of the literature on polymer nanocomposites to be one of the most popular areas for materials’ improvement [14–16].Halloysite is a clay mineral with the empirical formula Al2Si2O5(OH)4 [17]. Halloysite nanoclay is an unusual and rare natural nanotubular material [15, 16, 18]. Up to now, the superior potential applications have been disappointed by the degradation of the polymer or failure to outperform other incumbent alternatives. Halloysite nanoclay can improve brittle polymers such as polyester at a very low cost [19]. The one-dimensional tubular porous structure on the mesoporous (2–50 nm) and macroporous (>50 nm) scale made halloysite nanoclay superior to many synthetic materials such as CNTs (carbon nanotubes) [20, 21]. The unique properties lead to various applications of the halloysite nanoclay for controlled drug and other active molecules’ release [22]. They also have been used as nanoreactors and adsorbents [23]. The mechanical properties of systems with halloysite nanoclay are not the only improvements that can be observed [24–26]. The incorporation of halloysite nanoclay enhanced the nanocomposites’ thermal stability and flame and corrosion resistance of composites as well [27].Nanoclay as a filler in clay-polymer nanocomposites (CPN) was introduced by Du et al. in 2006 [27]. They have investigated the effect of nanoclay content on the mechanical properties of nanocomposites. In their study, the flexural modulus of the nanocomposites increased from 2711 MPa (neat polypropylene) to 4557 MPa (68% increase). Deng et al. [28] reported the fracture toughness of the nanoclay particle modified epoxies. They have revealed the greatest improvement up to 50% in KIC and 127% in GIC. This remarkable improvement was attributed to the large aspect ratios of halloysite nanoclay [28]. Albdiry and Yousif studied the tensile strength and modulus of unsaturated polyester nanocomposites [29]. The nanocomposites demonstrated an increase in mechanical properties by 7% and 10% in tensile strength and 7% and 12% in tensile modulus, respectively. Tang et al. revealed that the incorporation of small amounts of nanoclay in epoxy matrixes considerably enhanced impact toughness by 78% [30]. In another study by Albdiry et al., 61% fracture toughness enhancement was observed. Quaresimin et al. reported the fracture and interlaminar properties of clay-modified epoxies and their glass reinforced laminates [31]. They reported that 40% improvement in the fracture toughness was observed particularly with Cloisite 30B nanomodified resin [31]. Zappalorto et al. mentioned that the toughness improvements associated with nanomodification are strongly influenced by many factors, such as the filler morphology (size, geometry, and distribution) and, in particular, the applied loading conditions [32].Vahedi and Pasbakhs revealed that 240% improvement of impact toughness can be achieved by incorporating nanoclay into epoxy [33]. Most recently, Bhuvana and Prabakaran reported that the addition of nanoclay significantly increased storage modulus of polyamide up to 36% [34]. An improvement of Young’s modulus up to 26% was reported by Gabr et al. [35] as well. Most of these studies agree that the incorporation of nanoclay into epoxy will increase its mechanical properties. Considering these reports, there are great prospects for nanoclay based materials since they are also becoming the subject of intense global research. Despite the abovementioned literatures on the mechanical properties of polymer nanocomposite, there is a need to investigate the effect of structure morphology and the seawater environmental effect on the mechanical properties of polymer nanocomposites. This is due to the fact that the interaction between the seawater and polyester based nanocomposites is an issue that has not been sufficiently understood and analysed in the literature in a comprehensive manner. In fact, most of the previous studies were focused only on epoxy based polymers and some are rarely discussing the polyester based polymers exposed to seawater environment [3]. As the polyester based polymer is extensively used in aggressive marine environments, the long-term behaviour in such condition is still obscure. Further study is needed for thorough and clear evaluation of the maintenance period and total life time of polyester based polymer used in marine application as the effect of marine environment is complex and clearly depends on the compound used.This study investigates the effect of nanoclay on the mechanical properties of polyester exposed to seawater environment. Figure1 shows the increase in nanoclay research in recent years as the subject of the work is of interest both for the scientific community and for the industry. In many previous studies, it is noted that having uniform dispersion of nanoclay particularly in epoxy nanocomposites has remained a challenge [36]. Therefore, the authors hereby incorporated nanoclay at maximum 1 wt% reinforcement. This is based on a study carried out by Sancaktar and Kuznicki [37], where dispersing at higher weight fraction (more than 1 wt% clays) is difficult and agglomerated clay deteriorates the mechanical properties of the composite materials. Asadi et al. also found that the optimal clay reinforcement should be around 1 wt% for their epoxy-nanotubes nanocomposites samples [38].Figure 1
Number of citations using “halloysite” as keyword searched in title from the Web of Science (by 11/07/2016).


## 2. Materials

Halloysite nanoclay was used as reinforcement filler and was acquired from Sigma-Aldrich (Figure2(a)). The diameters are in between 30 and 70 nm with lengths between 1 and 4 μm. They possess tube-like morphologies as illustrated in Figure 2(b). The density of nanoclay is 2.53 g/cm3 and surface area is 64 m2/g. It has low electrical and thermal conductivities and strong hydrogen interactions. The tube-like morphology, high aspect ratio, and low percolation make nanoclay ideal reinforcement for polyester and other polymers.Figure 2
SEM images of halloysite nanoclay particles used in experiments as received (a) halloysite nanoclay in clusters and (b) schematic of halloysite nanoclay tubular structure.
(a) (b)The polyester resin (NORSODYNE O 12335 AL) was acquired from East Coast Fibreglass, UK. The resin has density of 1.2 g/cm3. The catalyst (hardener) was methyl ethyl ketone peroxide solution in dimethyl phthalate and was purchased from East Coast Fibreglass, UK. To produce monolithic polyester samples, the resin was mixed with catalyst (Butanox M-50) with a polyester : catalyst ratio of 98 : 2. Following thorough hand mixing for 5 minutes, vacuum degassing was carried out for 5 minutes. The mixture was then poured into moulds and cured at room temperature for 24 h followed by postcuring at 60°C for 2 h according to a process performed by Bonnia et al. [39] and Ratna Prasad and Mohana Rao [40]. Four different weight fractions of nanoclay (0.1 wt%, 0.3 wt%, 0.7 wt%, and 1.0 wt%) were used to reinforce the polyester. Collected seawater from South Shields, United Kingdom, was used to study the environmental effect on the polymer nanocomposites.


## 3. Characterisation

DMA (Model 8000, PerkinElmer) was used to determine dynamic storage modulus (E′) and loss modulus (E′′) of the samples. The loss factor tan⁡δ was calculated as the ratio (E′′/E′). Rectangular test specimens of dimensions 20 × 10 × 3 mm were used with a single cantilever clamp. All tests were carried out by temperature sweep method (temperature ramp from 30°C to 130°C at 5°C min−1) at a constant frequency of 1 Hz. The maximum force of DMA was 10 N and was applied during all the DMA test. The glass transition temperature (Tg) was taken as the temperature value at the peak of tan⁡δ curves. Scanning electron microscopy (SEM) analysis using FEI Quanta 200 was carried out on the fractured surfaces of tensile specimens to evaluate the fracture modes in the samples. The fractured portions were cut from the specimens and a layer of gold was applied using Emscope sputter coater model SC500A.Rectangular specimens with dimensions 80 × 10 × 4 mm were immersed into the liquid media at room temperature. The weight was measured after 168 h immersion using 0.001 mg accurate weighing balance. Before weighing a specimen, any retained liquid (seawater) was removed from its surface with an absorbent paper. The samples were kept at room temperature for 168 h and increase in weight was measured every 24 h with respect to initial weight (before immersion). The seawater absorption in the sample was measured as % weight increase in the samples. The following equation was used to calculate the seawater absorption in the specimens:(1)Wc=Wt-Wo×100Wo,where Wt is the weight of specimen at time t (i.e., after immersion in the liquid) and Wo is the initial weight of the sample, that is, before placing in seawater. The specimens have been immersed in seawater and weighed at regular intervals of 24 h over a total time of 168 h.The densification of samples was calculated according to ASTM D792. The densities of polyester, hardener, nanoclay, and water were 1.2, 1.18, 2.53, and 0.9975 g cm−3, respectively. The following equations were used to obtain the experimental density and densification:(2)Experimentaldensity=weightinairweightinair-weightinwater,×densityofwaterDensification%=experimentaldensitytheoreticaldensity×100.Vickers microhardness test was performed using the Buehler Micromet II for the monolithic polyester and its nanocomposites. The load applied was 200 g for 10 seconds. After seawater immersion, the samples were taken out and the liquid was completely wiped out from the specimen surface.Tensile tests were performed using Instron Universal Testing Machine (Model 3382). Five specimens were tested for each composition. The displacement rate was kept at 1 mm/min. Tensile properties were assessed according to ISO 527 (Figure3(a)) with specimen thickness of 3 mm. Three-point bending test was performed according to ISO 178 with dimensions 80 × 10 × 4 mm (Figure 3(b)).Figure 3
The schematic of specimens: (a) tensile, (b) flexural, and (c) Charpy impact toughness and (d) fracture toughness,KIC.
(a) (b) (c) (d)Charpy impact toughness test was performed according to ASTM D6110 (Figure3(c)) using notch samples. A notch of 45° was made in the centre of the samples. The impact toughness was obtained using (3), where m is mass of hammer (kg), g is standard gravity (9.81 m s−2), h is the length of hammer (m), and t is sample thickness (mm). Hence,(3)Impacttoughness=mghcos⁡β-cos⁡αwt.Fracture toughness (KIC) was determined using a single edge notch three-point bending (SEN-TPB) specimen (ASTM D5045) as shown in Figure 3(d). The dimensions were 3 × 6 × 36 mm with a crack length of 3 mm at the middle of the sample. KIC was calculated using linear fracture mechanics by the following relationship:(4)KIC=Pmaxa/wBW1/2,where f(a/w) is the calibration factor for the samples which is given as(5)faw=2+a/w0.0866+4.64a/w2+14.72a/w3-5.6a/w41-a/w3/2.The critical strain energy release rate (GIC) was obtained using (6) where E is Young’s modulus calculated from the tensile tests (MPa) and v is Poisson’s ratio of the polyester, taken to be 0.35. Hence,(6)GIC=KIC2E1-v2.


## 4. Results and Discussion

Seawater absorption analyses are shown in Figure4. In case of 0.3 wt% reinforcement, the seawater absorption was 0.12% higher compared to monolithic polyester after 168 h of immersion. At 1 wt% reinforcement, the seawater absorption was 0.72% more than that of monolithic polyester. Higher nanoclay content contributes to more seawater diffusion by swelling matrix and nanoparticles. The seawater absorption was found to increase as the nanoclay increased. Seawater molecules may enter through polymer chain and microvoids. A study by Dhakal et al. also revealed a similar trend of absorption in polyester nanocomposites [41]. The increased amount of spaces between nanoclay particles created an abundant surface area on which water molecules can adhere. Due to its high surface area, the nanoclay absorbed more seawater than unfilled polyester. On the other hand, several authors revealed that the water absorption of clay-polymers matrix nanocomposites is mainly influenced by two aspects. The first suggests that the clay body is water rich and thus absorbs more liquid than nearly all the polymers used as matrix [42]. The second one states that clay layers dispersed in the nanoscale are able to decrease the mean free path of water molecules to pass through the nanocomposite network compared to monolithic matrix. As a result, this reduces water absorption [33, 34]. This research however is in line with what has been reported by Ollier et al. where the clay absorbed seawater more than unfilled polyester [42].Figure 4
Absorption behaviour of nanoclay-polyester nanocomposites.


### 4.1. Results and Discussion of the Experiments

The DMA results are shown in Figures5, 6, and 7. The changes in Tg depend on the percentage of filler incorporated. In dry condition, the halloysite nanoclay remarkably increased Tg. In case of monolithic polyester, the mean value of Tg was 80°C. The Tg values were found to steadily increase as nanoclay increased. For instance, in case of 0.7 wt%, an increase of 4.4°C in Tg was recorded. However, in case of 1 wt% reinforcement, the Tg value was slightly lower than nanocomposites of 0.7 wt% reinforcement (3°C increase compared to monolithic polyester). This phenomenon is due to the agglomeration of halloysite nanoclay particles where these particles tend to form clay clusters or platelets as also reported by Liu et al. [43].Figure 5
T g of nanocomposites for dry and immersed samples.Figure 6
Storage modulus of dry (a) and immersed (b) samples.
(a) (b)Figure 7
Loss modulus of nanocomposites in air (a) and after seawater exposure (b).
(a) (b)After seawater immersion, it was observed that theTg values dropped considerably in comparison to dry conditions. The seawater undoubtedly had altered the structural integrity of the nanocomposites. Samples immersed in seawater were found to swell and to be slightly soft compared to samples tested in the dry condition. After seawater immersion, monolithic polyester recorded the highest Tg value of 77°C. The minimum Tg value was observed in case of 1 wt% (74°C) nanoclay reinforcement. The decrease in Tg with nanoclay addition could be attributed to the plasticization effect on the matrix by the organic modifier of the nanoclay. The plasticization may have also been caused by the slipping of nanoclay platelets in the clustered nanoclay [44]. The storage modulus and loss modulus of the polyester and its nanocomposites in dry condition are shown in Figures 6(a) and 7(a). The storage and loss moduli data were taken from the highest peak of tan⁡δ. The storage moduli were higher at initial temperature (30°C) and then decreased when approaching Tg. It can be found that the increase in stiffness and restriction in the movement of polymer chains by halloysite nanoclay caused remarkable improvement in storage modulus of the nanocomposites.Very little increase in storage modulus was recorded in case of 0.1 wt% reinforcement (162% increase). The highest increase of storage modulus was observed in case of 0.7 wt% with a 678% increase. After seawater exposure, different trends were observed. The seawater environment reduced the stiffness of the samples especially for the nanocomposites systems. About 27% storage modulus decrease was observed in case of 0.7 wt%. The maximum decrease of storage modulus was 43% in case of 1 wt% reinforcement.Based on the dynamic mechanical analysis, it is evidently shown that monolithic polyester shows better resistance towards the seawater environment. Loss modulus of the polyester and nanocomposites is shown in Figure7(b). The curves for all nanocomposites systems were found to shift slightly to the left compared to samples tested in the dry condition. Apart from that, it can be seen from the figure that the loss modulus peak values decrease when samples were immersed in seawater.After seawater immersion, monolithic polyester had the highest loss modulus curve followed by 0.1 wt%, 0.3 wt%, 0.7 wt%, and 1 wt% reinforcement. The significant decrease of loss modulus was from 555 MPa to 295 MPa (1 wt% reinforcement). The samples exposed to seawater for longer periods are softer than the dried samples. The water-absorbed samples tend to be less stiff than the dried samples.The densification percentage of nanoclay-polyester nanocomposites is presented in Figure8(a). The large standard deviations in the nanocomposites can be attributed to the porosity in the samples produced. Entrapped air bubbles in the resin restricted the movement of the polymer chains and acted as micropores after curing [45]. Another mechanism for their existence is due to the relative fast curing of polyester resin when mixed with curing agent, where the volatiles could not escape during the exothermic curing process.Figure 8
Mechanical properties of halloysite nanoclay-polyester nanocomposites in dry and wet conditions.
(a) (b) (c) (d) (e) (f)  (g) (h) (i) (j)Surface hardness is normally investigated as one of the most important factors that are related to the abrasion and wear resistance of nanocomposites materials [39, 40]. The Vickers microhardness graph is shown in Figure 8(b) for samples tested in air and after seawater exposure. The incorporation of nanoclay significantly improved the microhardness property, particularly in case of 0.7 wt% reinforcement (44% increase). Minimum microhardness improvement was observed in case of 0.1 wt% with 11.4% increase. After seawater immersion, monolithic polyester showed maximum hardness, while at 1 wt% reinforcement the lowest value of microhardness was recorded (61% reduction).Young’s moduli (tensile moduli) of the monolithic polyester and its composites are shown in Figure8(c). Monolithic polyester recorded the lowest Young modulus of 0.7 GPa. The minimum increase for Young’s modulus was observed in case of 0.1 wt% with 5.4% improvement. The nanoclay also showed the maximum increase of 35% in case of 0.7 wt% reinforcement. Significant Young’s modulus reduction can be seen after seawater immersion. At 1 wt% nanoclay reinforcement, Young’s modulus dropped from 0.6 GPa to 0.4 GPa (33.3% decrease).The UTS (ultimate tensile strength) is presented in Figure8(d). The maximum increase in UTS was from 29.5 MPa to 44.2 MPa (50% increase) in case of 0.7 wt% nanoclay. The nanoclay also showed a minimum increase up to 15.3% in case of 0.1 wt% reinforcement. After seawater exposure, the UTS showed a significant decrease. The maximum decrease of UTS was observed in case of 1.0 wt% reinforcement (22% decrease) compared to monolithic polyester. The nanoclay likewise showed minimum decrease up to 2.4% in case of 0.1 wt% reinforcement.The variation in ultimate tensile strain (%) is shown in Figure8(e). The tensile strain was obtained from the % value of strain corresponding to UTS. In dry conditions, the reinforcement of nanoclay reduced the tensile strain. This is due to the fact that the nanoclay reinforcement improved the stiffness of the nanocomposites materials. In case of 0.7 wt% reinforcement, the ultimate tensile strain was 4.5%. This lower strain value can be attributed to the stiffness of the nanocomposites. After seawater immersion, the ultimate tensile strain values were increased for all nanocomposites as a result of the plasticization effect. About 5.2% of the tensile strain value was observed for monolithic polyester. In contrast, at 1 wt% reinforcement, 9% of the tensile strain was observed. The increase of tensile strain is due to the softening of the polymer matrix which increased the energy required to create a fracture. Reductions in the tensile properties (ultimate tensile strength, Young’s modulus, and ultimate tensile strain) can be associated with the plasticization effect of the resin matrix by seawater, which appears to lower the yield stress and increase the size of the plastic zone ahead of the crack [41, 42, 46]. Apart from that, the weakening of adhesion between halloysite nanoclays and matrix is also the reason of the decrease in tensile properties [47]. As for the flexural modulus (Figure 8(f)), nanocomposites samples tested in air condition showed excellent improvements. Maximum flexural modulus was achieved at 0.7 wt% reinforcement from 0.77 GPa to 1.24 GPa (61% improvement). In wet conditions, the flexural modulus dropped from 0.6 GPa (monolithic polyester) to 0.34 GPa (1 wt% nanoclay). The variations of flexural strength are shown in Figure 8(g). The maximum flexural strength was observed from 55.7 MPa to 80 MPa in case of 0.7 wt% (44% increase). About 2.3% increase was obtained at 0.1 wt% reinforcement. A similar trend was also found in samples exposed to seawater where the flexural strength dropped significantly. In case of 1 wt%, it can be seen that the flexural strength was reduced by about 22%. Monolithic polyester, in contrast, showed the maximum flexural strength value which is 51.4 MPa.The variations of impact toughness results are shown in Figure8(h). Samples tested in dry conditions showed that the Charpy impact toughness remarkably increased and the minimum improvement was observed at 0.1 wt% (54% increase). The impact toughness increased steadily and reached maximum values at 0.7 wt% reinforcement (80% increase). The seawater exposure reduced the impact strength of the nanocomposites. The increase of impact toughness can be attributed to the good interfacial adhesion between nanoclay and the polyester matrix. Good interfacial bonding between nanoclay and polyester requires higher energy absorbing capacity, which as a result produces higher impact strength. This finding is in agreement with Albdiry et al. [48] and Lin et al. [49] who reported maximum improvements in impact toughness of 61% and 300%, respectively. However, after seawater immersion, the impact strength for the nanocomposites was decreased. The impact strength decreased by 9% in case of 0.1 wt% reinforcement. The lowest impact toughness was observed in case of 1 wt%, with 32% decrease.TheKIC and GIC values are presented in Figures 8(i) and 8(j), respectively. It can be observed that KIC and GIC monotonically increased with the increase of halloysite nanoclays addition (from 0.1 wt% to 0.7 wt%). For dry samples, the maximum increase of KIC was obtained in case of 0.7 wt% from 0.26 to 0.4 MPa·m1/2 (54% increase). For the nanocomposites immersed in seawater, KIC also increased with the increase in halloysite nanoclay loading due to liquid absorption which caused plasticization of polymer matrix. The maximum KIC after seawater immersion was obtained in case of 1 wt% reinforcement from 0.59 MPa·m1/2 to 0.79 MPa·m1/2 (34% increase). The maximum GIC recorded for dry samples was observed in case of 0.7 wt% from 70 J/m2 to 108 J/m2 (54.3% increase). After seawater immersion, samples with 1 wt% halloysite nanoclay reinforcement recorded the maximum GIC from 133 J/m2 to 185 J/m2 (39% increase). The seawater uptake caused the polymer matrix to soften and increase the ductility of the samples; as a result, the failure time also increased.


### 4.2. SEM Images

Figures9(a), 9(b), 9(c), 9(d), and 9(e) show the fractured surface of the monolithic polyester and its nanocomposites exposed in seawater environment. The fractured surface layers are short and round ended in monolithic polyester showing minimal plastic deformation. The monolithic polyester samples also showed the roughest surface compared to halloysite nanoclay-polyester nanocomposites. The surface roughness corresponds to the resistance of the material to the propagation of the cracks. It can be observed from the figure that the morphological structures of nanocomposites based on reinforcement polyester resin with halloysite nanoclay particles prepared are uniformly dispersed especially in case of 0.1 wt%, 0.3 wt%, and 0.7 wt%. In case of 1 wt% reinforcement, agglomeration can be seen as shown in Figure 9(e).Figure 9
SEM images showing the details of fracture surfaces of polyester and its nanocomposites; (a) monolithic polyester, (b) 0.1 wt% reinforcement polyester, (c) 0.3 wt% reinforcement, (d) fractured surface of 0.7 wt% reinforcement, and (e) fractured surface of 1 wt% reinforcement.
(a) (b) (c) (d) (e)The fracture mode on halloysite nanoclay-polyester nanocomposites was a smooth, straight path and showed a sign of plastic deformation. When the crack initiates, it propagates with fewer diversions and more likely results in straight fracture paths or river markings. Lower resistance to crack propagation shows more straight and longer fracture paths as shown in Figure9(e).Agglomeration of halloysite nanoclays can be seen in 1 wt% reinforcement also shown in Figure9(e). The halloysite nanoclay clusters were found to be poorly dispersed. This also proves that at high concentration the movement of clay is restricted. The agglomeration of nanoparticles and the plasticization effect are important factors affecting the final properties of the nanocomposites at 1 wt% reinforcement.


## 4.1. Results and Discussion of the Experiments

The DMA results are shown in Figures5, 6, and 7. The changes in Tg depend on the percentage of filler incorporated. In dry condition, the halloysite nanoclay remarkably increased Tg. In case of monolithic polyester, the mean value of Tg was 80°C. The Tg values were found to steadily increase as nanoclay increased. For instance, in case of 0.7 wt%, an increase of 4.4°C in Tg was recorded. However, in case of 1 wt% reinforcement, the Tg value was slightly lower than nanocomposites of 0.7 wt% reinforcement (3°C increase compared to monolithic polyester). This phenomenon is due to the agglomeration of halloysite nanoclay particles where these particles tend to form clay clusters or platelets as also reported by Liu et al. [43].Figure 5
T g of nanocomposites for dry and immersed samples.Figure 6
Storage modulus of dry (a) and immersed (b) samples.
(a) (b)Figure 7
Loss modulus of nanocomposites in air (a) and after seawater exposure (b).
(a) (b)After seawater immersion, it was observed that theTg values dropped considerably in comparison to dry conditions. The seawater undoubtedly had altered the structural integrity of the nanocomposites. Samples immersed in seawater were found to swell and to be slightly soft compared to samples tested in the dry condition. After seawater immersion, monolithic polyester recorded the highest Tg value of 77°C. The minimum Tg value was observed in case of 1 wt% (74°C) nanoclay reinforcement. The decrease in Tg with nanoclay addition could be attributed to the plasticization effect on the matrix by the organic modifier of the nanoclay. The plasticization may have also been caused by the slipping of nanoclay platelets in the clustered nanoclay [44]. The storage modulus and loss modulus of the polyester and its nanocomposites in dry condition are shown in Figures 6(a) and 7(a). The storage and loss moduli data were taken from the highest peak of tan⁡δ. The storage moduli were higher at initial temperature (30°C) and then decreased when approaching Tg. It can be found that the increase in stiffness and restriction in the movement of polymer chains by halloysite nanoclay caused remarkable improvement in storage modulus of the nanocomposites.Very little increase in storage modulus was recorded in case of 0.1 wt% reinforcement (162% increase). The highest increase of storage modulus was observed in case of 0.7 wt% with a 678% increase. After seawater exposure, different trends were observed. The seawater environment reduced the stiffness of the samples especially for the nanocomposites systems. About 27% storage modulus decrease was observed in case of 0.7 wt%. The maximum decrease of storage modulus was 43% in case of 1 wt% reinforcement.Based on the dynamic mechanical analysis, it is evidently shown that monolithic polyester shows better resistance towards the seawater environment. Loss modulus of the polyester and nanocomposites is shown in Figure7(b). The curves for all nanocomposites systems were found to shift slightly to the left compared to samples tested in the dry condition. Apart from that, it can be seen from the figure that the loss modulus peak values decrease when samples were immersed in seawater.After seawater immersion, monolithic polyester had the highest loss modulus curve followed by 0.1 wt%, 0.3 wt%, 0.7 wt%, and 1 wt% reinforcement. The significant decrease of loss modulus was from 555 MPa to 295 MPa (1 wt% reinforcement). The samples exposed to seawater for longer periods are softer than the dried samples. The water-absorbed samples tend to be less stiff than the dried samples.The densification percentage of nanoclay-polyester nanocomposites is presented in Figure8(a). The large standard deviations in the nanocomposites can be attributed to the porosity in the samples produced. Entrapped air bubbles in the resin restricted the movement of the polymer chains and acted as micropores after curing [45]. Another mechanism for their existence is due to the relative fast curing of polyester resin when mixed with curing agent, where the volatiles could not escape during the exothermic curing process.Figure 8
Mechanical properties of halloysite nanoclay-polyester nanocomposites in dry and wet conditions.
(a) (b) (c) (d) (e) (f)  (g) (h) (i) (j)Surface hardness is normally investigated as one of the most important factors that are related to the abrasion and wear resistance of nanocomposites materials [39, 40]. The Vickers microhardness graph is shown in Figure 8(b) for samples tested in air and after seawater exposure. The incorporation of nanoclay significantly improved the microhardness property, particularly in case of 0.7 wt% reinforcement (44% increase). Minimum microhardness improvement was observed in case of 0.1 wt% with 11.4% increase. After seawater immersion, monolithic polyester showed maximum hardness, while at 1 wt% reinforcement the lowest value of microhardness was recorded (61% reduction).Young’s moduli (tensile moduli) of the monolithic polyester and its composites are shown in Figure8(c). Monolithic polyester recorded the lowest Young modulus of 0.7 GPa. The minimum increase for Young’s modulus was observed in case of 0.1 wt% with 5.4% improvement. The nanoclay also showed the maximum increase of 35% in case of 0.7 wt% reinforcement. Significant Young’s modulus reduction can be seen after seawater immersion. At 1 wt% nanoclay reinforcement, Young’s modulus dropped from 0.6 GPa to 0.4 GPa (33.3% decrease).The UTS (ultimate tensile strength) is presented in Figure8(d). The maximum increase in UTS was from 29.5 MPa to 44.2 MPa (50% increase) in case of 0.7 wt% nanoclay. The nanoclay also showed a minimum increase up to 15.3% in case of 0.1 wt% reinforcement. After seawater exposure, the UTS showed a significant decrease. The maximum decrease of UTS was observed in case of 1.0 wt% reinforcement (22% decrease) compared to monolithic polyester. The nanoclay likewise showed minimum decrease up to 2.4% in case of 0.1 wt% reinforcement.The variation in ultimate tensile strain (%) is shown in Figure8(e). The tensile strain was obtained from the % value of strain corresponding to UTS. In dry conditions, the reinforcement of nanoclay reduced the tensile strain. This is due to the fact that the nanoclay reinforcement improved the stiffness of the nanocomposites materials. In case of 0.7 wt% reinforcement, the ultimate tensile strain was 4.5%. This lower strain value can be attributed to the stiffness of the nanocomposites. After seawater immersion, the ultimate tensile strain values were increased for all nanocomposites as a result of the plasticization effect. About 5.2% of the tensile strain value was observed for monolithic polyester. In contrast, at 1 wt% reinforcement, 9% of the tensile strain was observed. The increase of tensile strain is due to the softening of the polymer matrix which increased the energy required to create a fracture. Reductions in the tensile properties (ultimate tensile strength, Young’s modulus, and ultimate tensile strain) can be associated with the plasticization effect of the resin matrix by seawater, which appears to lower the yield stress and increase the size of the plastic zone ahead of the crack [41, 42, 46]. Apart from that, the weakening of adhesion between halloysite nanoclays and matrix is also the reason of the decrease in tensile properties [47]. As for the flexural modulus (Figure 8(f)), nanocomposites samples tested in air condition showed excellent improvements. Maximum flexural modulus was achieved at 0.7 wt% reinforcement from 0.77 GPa to 1.24 GPa (61% improvement). In wet conditions, the flexural modulus dropped from 0.6 GPa (monolithic polyester) to 0.34 GPa (1 wt% nanoclay). The variations of flexural strength are shown in Figure 8(g). The maximum flexural strength was observed from 55.7 MPa to 80 MPa in case of 0.7 wt% (44% increase). About 2.3% increase was obtained at 0.1 wt% reinforcement. A similar trend was also found in samples exposed to seawater where the flexural strength dropped significantly. In case of 1 wt%, it can be seen that the flexural strength was reduced by about 22%. Monolithic polyester, in contrast, showed the maximum flexural strength value which is 51.4 MPa.The variations of impact toughness results are shown in Figure8(h). Samples tested in dry conditions showed that the Charpy impact toughness remarkably increased and the minimum improvement was observed at 0.1 wt% (54% increase). The impact toughness increased steadily and reached maximum values at 0.7 wt% reinforcement (80% increase). The seawater exposure reduced the impact strength of the nanocomposites. The increase of impact toughness can be attributed to the good interfacial adhesion between nanoclay and the polyester matrix. Good interfacial bonding between nanoclay and polyester requires higher energy absorbing capacity, which as a result produces higher impact strength. This finding is in agreement with Albdiry et al. [48] and Lin et al. [49] who reported maximum improvements in impact toughness of 61% and 300%, respectively. However, after seawater immersion, the impact strength for the nanocomposites was decreased. The impact strength decreased by 9% in case of 0.1 wt% reinforcement. The lowest impact toughness was observed in case of 1 wt%, with 32% decrease.TheKIC and GIC values are presented in Figures 8(i) and 8(j), respectively. It can be observed that KIC and GIC monotonically increased with the increase of halloysite nanoclays addition (from 0.1 wt% to 0.7 wt%). For dry samples, the maximum increase of KIC was obtained in case of 0.7 wt% from 0.26 to 0.4 MPa·m1/2 (54% increase). For the nanocomposites immersed in seawater, KIC also increased with the increase in halloysite nanoclay loading due to liquid absorption which caused plasticization of polymer matrix. The maximum KIC after seawater immersion was obtained in case of 1 wt% reinforcement from 0.59 MPa·m1/2 to 0.79 MPa·m1/2 (34% increase). The maximum GIC recorded for dry samples was observed in case of 0.7 wt% from 70 J/m2 to 108 J/m2 (54.3% increase). After seawater immersion, samples with 1 wt% halloysite nanoclay reinforcement recorded the maximum GIC from 133 J/m2 to 185 J/m2 (39% increase). The seawater uptake caused the polymer matrix to soften and increase the ductility of the samples; as a result, the failure time also increased.


## 4.2. SEM Images

Figures9(a), 9(b), 9(c), 9(d), and 9(e) show the fractured surface of the monolithic polyester and its nanocomposites exposed in seawater environment. The fractured surface layers are short and round ended in monolithic polyester showing minimal plastic deformation. The monolithic polyester samples also showed the roughest surface compared to halloysite nanoclay-polyester nanocomposites. The surface roughness corresponds to the resistance of the material to the propagation of the cracks. It can be observed from the figure that the morphological structures of nanocomposites based on reinforcement polyester resin with halloysite nanoclay particles prepared are uniformly dispersed especially in case of 0.1 wt%, 0.3 wt%, and 0.7 wt%. In case of 1 wt% reinforcement, agglomeration can be seen as shown in Figure 9(e).Figure 9
SEM images showing the details of fracture surfaces of polyester and its nanocomposites; (a) monolithic polyester, (b) 0.1 wt% reinforcement polyester, (c) 0.3 wt% reinforcement, (d) fractured surface of 0.7 wt% reinforcement, and (e) fractured surface of 1 wt% reinforcement.
(a) (b) (c) (d) (e)The fracture mode on halloysite nanoclay-polyester nanocomposites was a smooth, straight path and showed a sign of plastic deformation. When the crack initiates, it propagates with fewer diversions and more likely results in straight fracture paths or river markings. Lower resistance to crack propagation shows more straight and longer fracture paths as shown in Figure9(e).Agglomeration of halloysite nanoclays can be seen in 1 wt% reinforcement also shown in Figure9(e). The halloysite nanoclay clusters were found to be poorly dispersed. This also proves that at high concentration the movement of clay is restricted. The agglomeration of nanoparticles and the plasticization effect are important factors affecting the final properties of the nanocomposites at 1 wt% reinforcement.


## 5. Conclusions

The results showed that small amounts of nanoclay considerably improved the microhardness, tensile properties, flexural properties, impact toughness, and fracture toughness of the nanocomposites. In dry conditions, the optimal limit of nanoclay was found in case of 0.7 wt%. The microhardness was improved by 44% compared to monolithic polyester. Young’s modulus increased from 0.7 GPa to 1 GPa (43% increase) and the flexural modulus increased from 0.77 GPa to 1.24 GPa (61% increase). The fracture toughness improved from 0.26 MPa·m1/2 to 0.4 MPa·m1/2 (54% increase).The seawater exposure, however, has significantly reduced the mechanical properties of the nanocomposites. The microhardness decreased from 107 HV to 42 HV (61% decrease) compared to monolithic polyester. Young’s modulus exhibited a decrease of 33%, and flexural modulus exhibited a decrease of 43%. The maximumKIC after seawater immersion was obtained in case of 1 wt% reinforcement from 0.59 MPa·m1/2 to 0.79 MPa·m1/2 (34% increase). Maximum GIC was obtained from 133 J/m2 to 185 J/m2 (39% increase). The seawater uptake caused the polymer matrix to soften and increase the ductility of the samples; as a result, the failure time also increased.During the water immersion tests of the nanocomposites, the interface alone or possibly both the interface and the nanoparticles were damaged and caused degradation of nanocomposites properties. This can be attributed to poor interfacial adhesion between the nanoclay and polymer matrix. On the other hand, the seawater diffusion in nanocomposites depends on several issues such as the volume of the fillers as well as the viscosity of the matrix. The halloysite nanoclay increased the viscosity and is likely to produce voids in the nanocomposites. Voids allow seawater to diffuse easily. The interfacial region in nanoclay-polyester nanocomposites is more susceptible to damage due to seawater absorption. Microhardness, tensile properties, flexural properties, and impact toughness were significantly negatively affected by seawater immersion after 168 h.



---

*Source: 2604631-2016-12-04.xml*