# XPS Depth Study on the Liquid Oxidation of Sn-Bi-Zn-X(Al/P) Alloy and the Effect of Al/P on the Film

Authors: X. J. Wang; N. Liu; S. Shi; Y. X. Chen
Journal: Advances in Materials Science and Engineering
 (2015)

---

## Abstract

X-ray photoelectron spectroscopy (XPS) was used to study the properties of liquid oxidation of Sn-Bi-Zn (SBZ) solder alloys and the effect of Al/P on the oxide film. The results showed that the oxidation film on SBZ surface was in high concentration of both oxygen and zinc. Adding trace amount of Al/P to SBZ alloys (SBZA/ABZP) decreased the ratio of O/M (M could be Sn, Bi, and Al/P) and changed the film compositions. Layers near the free surface of oxidation film mostly contained Zn2+ and Al3+ oxides for SBZA. From the half quantitative analysis result, the aluminum had a surface enrichment behavior in liquid solder, so did phosphorus and zinc. Therefore, the Al/P addition changed their stoichiometry such as the ratio of O/M near film surface.


---

## Body

## 1. Introduction

Due to the step-soldering process in electronic package, solder alloys joining at different temperature ranges have been in demand during manufacturing procedure. Sn-Ag-Cu system, notably, Sn-3.0Ag-0.5Cu, has been becoming the main stream in surface mount technology (SMT) as a middle-temperature Pb-free solder. Accordingly, Sn-Bi alloy, represented by eutectic Sn-58Bi, has been used for thermal module connection in notebook ascribed to the low cost, superior wettability, and almost void-free bonding [1–3]. It can also reduce the damage arising from the mismatch of thermal expansion among various components in electronic assembly [1].But there are still two issues preventing further application of Sn-Bi alloy, that is, lower thermal conductivity and microstructure coarsening with a serious Bi segregation along the interface, which can greatly decrease the reliability of the solder joint [4]. Actually, decreasing Bi-content has been an effective way to adjust the thermal conductivity and melting range. As for the microstructure instability at soldering, temperature can be suppressed by incorporating fine dispersoid particles into Sn-Bi alloy [4, 5].Among the alloying elements, Zn, Al, and P are very cheap and useful. It is reported that minor Zn doped in Pb-free solders can obviously inhibit the growth of intermetallic compounds (IMCs), restrain the growth of Cu3Sn, and suppress the formation of Kirkendall voids during isothermal aging [6, 7]. About 0.5 wt.% Zn addition to Sn-Ag-Cu-Ce solder alloy can restrain the growth of tin whiskers and strengthen the solder joints [8]. Being very active, Zn will worsen the oxidation performance of solder alloy during and after soldering. Element alloying has been an effective way to improve the antioxidant power of Zn-containing solders [9]. Al, Ag, and In addition can improve the liquid oxidation behavior at Sn-Zn alloy [9–12]. Furthermore, Al decreases the oxidation rate while doping in Sn-Zn alloy due to the formation of Al2O3 thin film on the surface, which is much similar to Bi, Ga, and P for Sn-Zn solders [12]. Since Al and P have been paid much attention for the cheapness and effectiveness, Sn-40Bi-2Zn (SBZ) and Sn-40Bi-2Zn-X (X could be Al and P, simplified as SBZA and SBZP, resp.) will be used to investigate the effect of minor Al/P addition on the oxidation performance of SBZ alloy. As regards the testing method, using XPS in the characterization of formed metal alloy surface is not new [13, 14]. Many efforts focusing on oxide formation on iron, steel, and molten tin have been implemented [13–15].


## 2. Experimental Procedures

### 2.1. Preparation of Specimens

SBZ, SBZA, SBZP, and Sn-58Bi alloys (for comparison in oxidation observation by eye) were prepared using pure Sn, Bi, Zn, Al, and P in vacuum oven at 800°C and remelted with stirring at 200°C to obtain a homogenized solder alloy. During the remelting process, an antioxidation agent was used to protect the liquid solder from oxidation. Subsequently, the solder alloys were aged for two weeks in room temperature for a stabilized microstructure.


### 2.2. Surface Observation of Solder Alloy after Oxidation

About 40 g solder alloys were put in graphite crucibles with a diameter of 28 mm and heated up to 170 ± 5°C to observe the oxidation processes during 1 h in air. The first dross should be carefully scraped away from the initial liquid surface to leave a fresh surface for oxidation starting therefrom. The color changes of the liquid solder surface with oxidation time increasing were observed visually and the final appearance of the oxide films was recorded by a digital camera.


### 2.3. XPS Procedure

Solder alloys were exposed at 170 ± 5°C for 7 min before cooling down to achieve oxidized surfaces. The solid samples were cut from the top surface of the ingots into about 2-3 mm sheets for XPS tests. For the test is sensitive to pollution, all the samples should be kept carefully away from contaminations.The surface elementary and chemical analyses were carried out via XPS with an achromatic AlKα X-ray source. After the original surface of samples was analyzed, an argon ion beam with 0.2 μA current operating at 3 keV was used to etch away a very thin layer of the solder from the oxidation surface to expose the underlying layer. Subsequently, a second surface analysis of the newer oxide film was performed by XPS with an argon gun attached to. So, repeatedly, an etch rate of about 0.6 nm/s was motivated over a 2 mm × 2 mm area by the manner the same as [16].


### 2.4. XSP Data Analysis

The etching and measurement for each sample were operated about 10 times till the oxygen content test on the surface becomes near to zero. All the spectra were calibrated by carbon adsorbed on the initial surface of the sample during etching.Curve fitting processes for all high-resolution spectra were implemented by the XPS Peak-Fitting Programme-XPSPEAK4.1 to deconvolute and quantify the contribution of each chemical species (element associations) that comprise the spectra.


## 2.1. Preparation of Specimens

SBZ, SBZA, SBZP, and Sn-58Bi alloys (for comparison in oxidation observation by eye) were prepared using pure Sn, Bi, Zn, Al, and P in vacuum oven at 800°C and remelted with stirring at 200°C to obtain a homogenized solder alloy. During the remelting process, an antioxidation agent was used to protect the liquid solder from oxidation. Subsequently, the solder alloys were aged for two weeks in room temperature for a stabilized microstructure.


## 2.2. Surface Observation of Solder Alloy after Oxidation

About 40 g solder alloys were put in graphite crucibles with a diameter of 28 mm and heated up to 170 ± 5°C to observe the oxidation processes during 1 h in air. The first dross should be carefully scraped away from the initial liquid surface to leave a fresh surface for oxidation starting therefrom. The color changes of the liquid solder surface with oxidation time increasing were observed visually and the final appearance of the oxide films was recorded by a digital camera.


## 2.3. XPS Procedure

Solder alloys were exposed at 170 ± 5°C for 7 min before cooling down to achieve oxidized surfaces. The solid samples were cut from the top surface of the ingots into about 2-3 mm sheets for XPS tests. For the test is sensitive to pollution, all the samples should be kept carefully away from contaminations.The surface elementary and chemical analyses were carried out via XPS with an achromatic AlKα X-ray source. After the original surface of samples was analyzed, an argon ion beam with 0.2 μA current operating at 3 keV was used to etch away a very thin layer of the solder from the oxidation surface to expose the underlying layer. Subsequently, a second surface analysis of the newer oxide film was performed by XPS with an argon gun attached to. So, repeatedly, an etch rate of about 0.6 nm/s was motivated over a 2 mm × 2 mm area by the manner the same as [16].


## 2.4. XSP Data Analysis

The etching and measurement for each sample were operated about 10 times till the oxygen content test on the surface becomes near to zero. All the spectra were calibrated by carbon adsorbed on the initial surface of the sample during etching.Curve fitting processes for all high-resolution spectra were implemented by the XPS Peak-Fitting Programme-XPSPEAK4.1 to deconvolute and quantify the contribution of each chemical species (element associations) that comprise the spectra.


## 3. Results and Discussion

### 3.1. Observation of Liquid Solder Alloy

Liquid Sn-58Bi alloy is easily oxidized in atmosphere condition. The freshly displayed surface remained silver-white for about 7 min before a gray white film formed. Then, the color of the liquid solder alloy varies from gray, blue with inhomogeneous purple, and finally dark blue with a light brownish yellow in some areas within 1 h (Figure1(a)). In the same air exposure condition, Zn-containing solder alloy, SBZ loses metallic lustre after about 3 min and keeps in white with a slight blue finally. The solder surface is quite rough due to the Zn oxidation before, during, and after cooling down, as shown in Figure 1(b).Figure 1
Oxidation appearances of (a) Sn-58Bi, (b) Sn-40Bi-2Zn, (c) Sn-40Bi-2Zn-0.005P, and (d) Sn-40Bi-2Zn-0.005Al after exposure in air at 170°C for 1 h.
(a)
(b)
(c)
(d)SBZP and SBZA solder alloys shine with grey or dark grey metallic lustre in liquid state within 1 h of exposure in air. With increasing oxidation time to about 30 min, an oxidation film with a slight grey white is visible on SBZP liquid surface, while the color on SBZA surface shows somewhat blue. After cooling down to room temperature, the surface grows rough on the surface of SBZP solder alloy (Figure1(c)). In comparison, the metal surface of SBZA still keeps smooth in solid state, as shown in Figure 1(d).


### 3.2. The Variation of Atomic Concentration with Etch Time

The variation in chemical composition with etch time of tin, oxygen, bismuth, zinc, and aluminium or phosphorus obtained from the XPS survey scans for the three specimens (SBZ, SBZA, and SBZP) is shown in Figure2. The oxygen content on the outer surface among three specimens decreases by the turn of SBZ, SBZP to SBZA from about 70 at.% to 60 at.% and then 45 at.% (see Figure 2(a)). It indicates that the oxidation film of SBZ is much porous. Moreover, the total thicknesses of the oxide films after oxidation at 170°C for 7 min are about 156 nm for SBZA sample and 216 nm for SBZ and SBZP alloys deduced from oxygen content.Figure 2
XPS depth profiles (at.%) for (a) oxygen, (b) zinc, (c) tin, (d) bismuth, and (e) aluminium and phosphorus recorded for the SBZ, SBZA, and SBZP specimens.
(a)
(b)
(c)
(d)
(e)As observed in Figures2(b) and 2(c), for tin and bismuth as the main elements, their concentrations increase with etch time as expected. The concentrations of zinc, aluminium, and phosphorus oppositely follow an increase sharply and then decrease towards the solder base direction. Among the three alloys, it is worth noting that the Zn concentration on the top of the oxidation film decrease followed by SBZ, SBZP to SBZA in turn corresponding to 40.4 at.%, 36.9 at.%, and 24.6 at.%, respectively. It indicates that a trace amount of Al/P doping in SBZ solder can protect Zn from overoxidation, as shown in Figures 2(d) and 2(e). Furthermore, Zn is somewhat enriched at the area of near surface, also the outer surface compared to the base-alloy composition. Accordingly, the contents of Al and P are thousand times more than additive amount, which suggests that the two elements have strong surface enrichment behavior in liquid solder alloy. Thus, there are three peaks showing Zn, Al, and P at low etching time. It can be ascribed to the following three points. First, element O, especially the absorbed oxidation, makes the other element contents keep lower relatively; second, the chemical O keeps driving Zn and Al/P diffusion from the solder base to react into compounds; finally, the competition between the above two reasons may result in the highest contents emerging at the sublayer of the oxidation films.The ratios of metal element M (M could be metal element in samples) and oxygen on the surface are about 3 : 7, 4 : 6, and 4.5 : 5.5 for SBZ, SBZP, and SBZA, respectively, increasing rapidly to 6 : 4 after etching for 40 s with argon ions for SBZ sample and 10 s for the latter two samples. It indicates the metal elements oxidation in SBZ is much serious compared to the elements in SBZA and SBZP. As for the species of the oxides, it is hard to distinguish them only from the semiquantitative results. And there are two other issues that should also be taken into account in the analysis. Firstly, there are at least four species of elements in the sample alloys which need further high-energy spectra analysis to conform the chemical states of the elements. Secondly, the surface oxygen should conclude both the physical adsorption oxygen and the chemical state oxygen appearing in oxides of metal M. Therefore, the O 1s, Sn 3d, Zn 2p, and so forth spectra should be analysed in detail, respectively, considering that Al addition cannot only protect Zn from oxidation but also reduce the thickness of oxidation film, while trace amount of P doping into SBZ only protects the Zn from overoxidation. Therefore, the XPS spectra of elements in SBZ and SBZA samples have been chosen for further analyses in the following section.


### 3.3. Analyses for SBZ

Figure3 shows the O 1s spectra of SBZ sample etched at various times along the film depth direction, which are decomposed to one or two symmetric peaks using a Shirley background type of subtraction for fitting the original asymmetric peaks through Gaussian curves.Figure 3
O 1s spectra of SBZ sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 80 s, and (d) 260 s.
(a)
(b)
(c)
(d)The deconvoluted O 1s peaks are located at 530.6 (A) and 532.6 (B) eV for etch time of 0 s, corresponding to the spectral factoring of O chemically bound with metal element M and the adsorbed oxygen, respectively. Peak A might be assigned to the presence of metal oxide (OM oxide) [17]. Peak B has been reported to correspond to presentation of adsorbed oxygen [15]. It is obvious that the amount of adsorbed oxygen is much higher than that of O chemically bound with metal M. After etching for 60 s (Figure 3(b)), the adsorbed oxygen on surface is very low and entirely removed within 80 s, producing a symmetrical and sharp peak pattern shown in Figure 3(c). It is worthwhile to note that the peak A in Figure 3(a) shifts from 530.6 eV to 530.9 eV after 60 s etching, which might be resulting from the stronger covalence of Sn-O bond.The XPS patterns of Sn 3d peaks for SBZ sample at different depths in the oxide film are shown in Figure4. There are two kinds of chemical states of tin: tin oxides and metallic tin. The peak position of metallic tin, Sn0, is located at 484.8 eV, while the peaks standing for tin oxides are showing at 486–487.1 eV. For the difference of peak positions between Sn2+ and Sn4+ is so small that their states cannot be distinguished from each other. With etching time increasing, the proportion of tin oxide decreases and the peak position of Sn 3d5/2 spectrum gradually shifts from 484.5 eV (tin oxides) to 485 eV (metallic tin).Figure 4
Sn 3d5/2 spectra of SBZ sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 140 s, and (d) 260 s.
(a)
(b)
(c)
(d)Figure5(a) displays Zn 2p spectra which possess two peaks corresponding to 1021.6 eV (Zn 2p3/2) and 1048.1 eV (Zn 2p1/2), respectively. One thing to be noted is that there is a small shift of the Zn 2p3/2 peaks to the left after etching for 60 s. This peak shift could be ascribed to the chemical state change of Zn in the oxides, from ZnO to Zn metal according to the data in Table 1.Table 1
XPS binding energy values for solder elements and the oxidative products obtained from literatures (Al, O data from NIST Standard Reference Database 20, V. 3.5).
Sn 3d5/2 (eV)
Zn 2p3/2 (eV)
Bi 4f7/2 (eV)
Al 2p (eV)
O 1s
Sn [15]
484.8
—
SnO [15, 19]
486.6/486
—
530.1
SnO2 [15, 19]
486.4/487.1
531.0
Zn [20]
1021.45
ZnO [20]
1021.7
530.7
Bi [10]
156.8
Bi2O3 [10, 17]
159.5
529.8
Al [21]
73
Al2O3 [18]
76-77
532.6
O [15]
532.5Figure 5
Spectra of (a) Zn 2p and (b) Bi 4f in SBZ sample oxidized at 170°C for 7 min after etching for various time.
(a)
(b)And Bi 4f spectra include a doublet structure generated by the splitting of multiplet (i.e., Bi 4f7/2 and Bi 4f5/2) shown in Figure5(b). Based on the binding energies reported in previous studies in Table 1 and NIST Standard Reference Database, Bi compounds of the film in this study can be classified into two types as Bi metal and Bi2O3 corresponding to the peak binding energies around 157 eV and 158 eV, respectively [10, 17].


### 3.4. Analyses for SBZA

The O 1s spectra of SBZA sample along the depth of the oxide film are shown in Figure6. The deconvoluted O 1s peaks for original surface are located at 531 (A′) eV and 532.6 (B′) eV. Based on the results in Figure 3, A′ peak can be assigned to metal oxide (OM oxygen), and the latter B′ may relate to the adsorbed oxygen like SBZ alloy and the emerging Al2O3 [18]. However, B′ peak disappears after 20 s of etching. It should be the absorbed oxygen mainly. The binding energy of peak A′ is 0.4 eV higher than the position of peak A in SBZ sample, which may indicate the species changes of oxides in the outmost surface of the film.Figure 6
O 1s spectra of SBZA sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 20 s, and (d) 80 s.
(a)
(b)
(c)
(d)According to the atomic concentration depth profile of SBZA etched for 0 s, it is found that there are mainly Zn and Al in the outer surface of the oxidation film. And considering that O chemically bounded with Zn located at 530.7 eV, O bounded with Al located at 532.6 eV, the OM oxygen should be mainly ZnO and Al2O3 with a little Bi and Sn inside. Peak B which corresponded to adsorbed oxygen (532.5 eV) [17] and Al2O3 [19] that could not be resolved becomes lower and totally disappears after etching for 20 s. That is, the film of SBZA sample is much denser than the surface film of SBZ sample, because the time getting to zero for physical adsorbed oxygen in SBZ sample requires 60 s, 40 s more than SBZA sample.It is noteworthy that peak A′ shifts from 531 eV to higher binding energy, 531.5 eV after 20 s etch time, then 531.7 eV at the etching time of 80 s, which might be also ascribed to the stronger Sn-O bond similar to the SBZ sample.Sn 3d spectra along the film depth are shown in Figure7. Similar to the results for SBZ in Figure 3, the peak position of Sn 3d5/2 of the original outer surface is positioned at 487.03 eV. However, after 80 s of etching, Sn 3d peak shifts slightly to 486.31 eV first and then maintains its position till the tin oxide disappears. Both the binding energy of the outer surface and the subsurface are slightly greater than that of the SBZ oxide film. The possible reason may lie in a strong electron withdrawing group or compounds around the tin atoms, which changed the chemical conditions resulting by the trace amount of Al addition. After removing 36 nm from the surface by etching, no oxide has been detected by XPS. The peak position of metallic tin is located at 484.86 eV as shown in Figure 7(d).Figure 7
Sn 3d5/2 spectra of SBZA sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 20 s, (d) 80 s, (e) 140 s, and (f) 260 s.
(a)
(b)
(c)
(d)
(e)
(f)Figure8 shows the XPS spectra of Al 2p depth profiles of oxide film in SBZA sample. The XPS peak height (Al content can be estimated) on the subsurface of oxidation is higher than that on the outer surface. The detected segregation layer of Al is very thin, distributed over a depth of about 12–48 nm from the outer surface. There is no visible Al peak detected beyond the area. From Figure 8, it is found that an almost invisible peak around 75.1 eV is showing at the outer film surface. After etching for 20 s, a new peak located at 72.2 eV arises corresponding to metal Al. It implies the enrichment behavior of element Al at the subsurface that the atom Al can be kept as a lower chemical state, Al0. While the etching time increases to 80 s, both kinds of peaks shift to higher energy direction. It suggests that there is a new chemical state of Al in the oxide. Based on [18], this peak position for Al 2p approaches that of Al2O3, with 0.9~1.9 eV deviation which might result by Sn and Bi dissolved in the oxidation film. However, further research is necessary to clarify the Al mechanism in the protective oxide film.Figure 8
Al 2p spectra of SBZA sample exposure at 170°C for 7 min after etching for (a) various times from 0 s to 140 s, (b) 0 s (initial surface), (c) 20 s, and (d) 80 s.
(a)
(b)
(c)
(d)Combined with the result of semiquantitative analysis (see Figure2), it is reasonable to propose that there is a triple-layer oxidation film structure. The outer surface should mainly comprise of O in physical status and ZnO with about 6 nm in thickness. The subsurface should be ZnO and Al2O3 doped with Sn4+ and Bi3+ to about 30–84 nm thickness according to Al element getting to almost zero and Sn metal contents almost being the main in all forms of Sn, which could be a protective film to prevent further oxidation of the molten solder alloy in atmosphere condition. And the inner remaining thickness of the film layer should be (Sn, Bi, and Zn) O as a transition layer.


## 3.1. Observation of Liquid Solder Alloy

Liquid Sn-58Bi alloy is easily oxidized in atmosphere condition. The freshly displayed surface remained silver-white for about 7 min before a gray white film formed. Then, the color of the liquid solder alloy varies from gray, blue with inhomogeneous purple, and finally dark blue with a light brownish yellow in some areas within 1 h (Figure1(a)). In the same air exposure condition, Zn-containing solder alloy, SBZ loses metallic lustre after about 3 min and keeps in white with a slight blue finally. The solder surface is quite rough due to the Zn oxidation before, during, and after cooling down, as shown in Figure 1(b).Figure 1
Oxidation appearances of (a) Sn-58Bi, (b) Sn-40Bi-2Zn, (c) Sn-40Bi-2Zn-0.005P, and (d) Sn-40Bi-2Zn-0.005Al after exposure in air at 170°C for 1 h.
(a)
(b)
(c)
(d)SBZP and SBZA solder alloys shine with grey or dark grey metallic lustre in liquid state within 1 h of exposure in air. With increasing oxidation time to about 30 min, an oxidation film with a slight grey white is visible on SBZP liquid surface, while the color on SBZA surface shows somewhat blue. After cooling down to room temperature, the surface grows rough on the surface of SBZP solder alloy (Figure1(c)). In comparison, the metal surface of SBZA still keeps smooth in solid state, as shown in Figure 1(d).


## 3.2. The Variation of Atomic Concentration with Etch Time

The variation in chemical composition with etch time of tin, oxygen, bismuth, zinc, and aluminium or phosphorus obtained from the XPS survey scans for the three specimens (SBZ, SBZA, and SBZP) is shown in Figure2. The oxygen content on the outer surface among three specimens decreases by the turn of SBZ, SBZP to SBZA from about 70 at.% to 60 at.% and then 45 at.% (see Figure 2(a)). It indicates that the oxidation film of SBZ is much porous. Moreover, the total thicknesses of the oxide films after oxidation at 170°C for 7 min are about 156 nm for SBZA sample and 216 nm for SBZ and SBZP alloys deduced from oxygen content.Figure 2
XPS depth profiles (at.%) for (a) oxygen, (b) zinc, (c) tin, (d) bismuth, and (e) aluminium and phosphorus recorded for the SBZ, SBZA, and SBZP specimens.
(a)
(b)
(c)
(d)
(e)As observed in Figures2(b) and 2(c), for tin and bismuth as the main elements, their concentrations increase with etch time as expected. The concentrations of zinc, aluminium, and phosphorus oppositely follow an increase sharply and then decrease towards the solder base direction. Among the three alloys, it is worth noting that the Zn concentration on the top of the oxidation film decrease followed by SBZ, SBZP to SBZA in turn corresponding to 40.4 at.%, 36.9 at.%, and 24.6 at.%, respectively. It indicates that a trace amount of Al/P doping in SBZ solder can protect Zn from overoxidation, as shown in Figures 2(d) and 2(e). Furthermore, Zn is somewhat enriched at the area of near surface, also the outer surface compared to the base-alloy composition. Accordingly, the contents of Al and P are thousand times more than additive amount, which suggests that the two elements have strong surface enrichment behavior in liquid solder alloy. Thus, there are three peaks showing Zn, Al, and P at low etching time. It can be ascribed to the following three points. First, element O, especially the absorbed oxidation, makes the other element contents keep lower relatively; second, the chemical O keeps driving Zn and Al/P diffusion from the solder base to react into compounds; finally, the competition between the above two reasons may result in the highest contents emerging at the sublayer of the oxidation films.The ratios of metal element M (M could be metal element in samples) and oxygen on the surface are about 3 : 7, 4 : 6, and 4.5 : 5.5 for SBZ, SBZP, and SBZA, respectively, increasing rapidly to 6 : 4 after etching for 40 s with argon ions for SBZ sample and 10 s for the latter two samples. It indicates the metal elements oxidation in SBZ is much serious compared to the elements in SBZA and SBZP. As for the species of the oxides, it is hard to distinguish them only from the semiquantitative results. And there are two other issues that should also be taken into account in the analysis. Firstly, there are at least four species of elements in the sample alloys which need further high-energy spectra analysis to conform the chemical states of the elements. Secondly, the surface oxygen should conclude both the physical adsorption oxygen and the chemical state oxygen appearing in oxides of metal M. Therefore, the O 1s, Sn 3d, Zn 2p, and so forth spectra should be analysed in detail, respectively, considering that Al addition cannot only protect Zn from oxidation but also reduce the thickness of oxidation film, while trace amount of P doping into SBZ only protects the Zn from overoxidation. Therefore, the XPS spectra of elements in SBZ and SBZA samples have been chosen for further analyses in the following section.


## 3.3. Analyses for SBZ

Figure3 shows the O 1s spectra of SBZ sample etched at various times along the film depth direction, which are decomposed to one or two symmetric peaks using a Shirley background type of subtraction for fitting the original asymmetric peaks through Gaussian curves.Figure 3
O 1s spectra of SBZ sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 80 s, and (d) 260 s.
(a)
(b)
(c)
(d)The deconvoluted O 1s peaks are located at 530.6 (A) and 532.6 (B) eV for etch time of 0 s, corresponding to the spectral factoring of O chemically bound with metal element M and the adsorbed oxygen, respectively. Peak A might be assigned to the presence of metal oxide (OM oxide) [17]. Peak B has been reported to correspond to presentation of adsorbed oxygen [15]. It is obvious that the amount of adsorbed oxygen is much higher than that of O chemically bound with metal M. After etching for 60 s (Figure 3(b)), the adsorbed oxygen on surface is very low and entirely removed within 80 s, producing a symmetrical and sharp peak pattern shown in Figure 3(c). It is worthwhile to note that the peak A in Figure 3(a) shifts from 530.6 eV to 530.9 eV after 60 s etching, which might be resulting from the stronger covalence of Sn-O bond.The XPS patterns of Sn 3d peaks for SBZ sample at different depths in the oxide film are shown in Figure4. There are two kinds of chemical states of tin: tin oxides and metallic tin. The peak position of metallic tin, Sn0, is located at 484.8 eV, while the peaks standing for tin oxides are showing at 486–487.1 eV. For the difference of peak positions between Sn2+ and Sn4+ is so small that their states cannot be distinguished from each other. With etching time increasing, the proportion of tin oxide decreases and the peak position of Sn 3d5/2 spectrum gradually shifts from 484.5 eV (tin oxides) to 485 eV (metallic tin).Figure 4
Sn 3d5/2 spectra of SBZ sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 140 s, and (d) 260 s.
(a)
(b)
(c)
(d)Figure5(a) displays Zn 2p spectra which possess two peaks corresponding to 1021.6 eV (Zn 2p3/2) and 1048.1 eV (Zn 2p1/2), respectively. One thing to be noted is that there is a small shift of the Zn 2p3/2 peaks to the left after etching for 60 s. This peak shift could be ascribed to the chemical state change of Zn in the oxides, from ZnO to Zn metal according to the data in Table 1.Table 1
XPS binding energy values for solder elements and the oxidative products obtained from literatures (Al, O data from NIST Standard Reference Database 20, V. 3.5).
Sn 3d5/2 (eV)
Zn 2p3/2 (eV)
Bi 4f7/2 (eV)
Al 2p (eV)
O 1s
Sn [15]
484.8
—
SnO [15, 19]
486.6/486
—
530.1
SnO2 [15, 19]
486.4/487.1
531.0
Zn [20]
1021.45
ZnO [20]
1021.7
530.7
Bi [10]
156.8
Bi2O3 [10, 17]
159.5
529.8
Al [21]
73
Al2O3 [18]
76-77
532.6
O [15]
532.5Figure 5
Spectra of (a) Zn 2p and (b) Bi 4f in SBZ sample oxidized at 170°C for 7 min after etching for various time.
(a)
(b)And Bi 4f spectra include a doublet structure generated by the splitting of multiplet (i.e., Bi 4f7/2 and Bi 4f5/2) shown in Figure5(b). Based on the binding energies reported in previous studies in Table 1 and NIST Standard Reference Database, Bi compounds of the film in this study can be classified into two types as Bi metal and Bi2O3 corresponding to the peak binding energies around 157 eV and 158 eV, respectively [10, 17].


## 3.4. Analyses for SBZA

The O 1s spectra of SBZA sample along the depth of the oxide film are shown in Figure6. The deconvoluted O 1s peaks for original surface are located at 531 (A′) eV and 532.6 (B′) eV. Based on the results in Figure 3, A′ peak can be assigned to metal oxide (OM oxygen), and the latter B′ may relate to the adsorbed oxygen like SBZ alloy and the emerging Al2O3 [18]. However, B′ peak disappears after 20 s of etching. It should be the absorbed oxygen mainly. The binding energy of peak A′ is 0.4 eV higher than the position of peak A in SBZ sample, which may indicate the species changes of oxides in the outmost surface of the film.Figure 6
O 1s spectra of SBZA sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 20 s, and (d) 80 s.
(a)
(b)
(c)
(d)According to the atomic concentration depth profile of SBZA etched for 0 s, it is found that there are mainly Zn and Al in the outer surface of the oxidation film. And considering that O chemically bounded with Zn located at 530.7 eV, O bounded with Al located at 532.6 eV, the OM oxygen should be mainly ZnO and Al2O3 with a little Bi and Sn inside. Peak B which corresponded to adsorbed oxygen (532.5 eV) [17] and Al2O3 [19] that could not be resolved becomes lower and totally disappears after etching for 20 s. That is, the film of SBZA sample is much denser than the surface film of SBZ sample, because the time getting to zero for physical adsorbed oxygen in SBZ sample requires 60 s, 40 s more than SBZA sample.It is noteworthy that peak A′ shifts from 531 eV to higher binding energy, 531.5 eV after 20 s etch time, then 531.7 eV at the etching time of 80 s, which might be also ascribed to the stronger Sn-O bond similar to the SBZ sample.Sn 3d spectra along the film depth are shown in Figure7. Similar to the results for SBZ in Figure 3, the peak position of Sn 3d5/2 of the original outer surface is positioned at 487.03 eV. However, after 80 s of etching, Sn 3d peak shifts slightly to 486.31 eV first and then maintains its position till the tin oxide disappears. Both the binding energy of the outer surface and the subsurface are slightly greater than that of the SBZ oxide film. The possible reason may lie in a strong electron withdrawing group or compounds around the tin atoms, which changed the chemical conditions resulting by the trace amount of Al addition. After removing 36 nm from the surface by etching, no oxide has been detected by XPS. The peak position of metallic tin is located at 484.86 eV as shown in Figure 7(d).Figure 7
Sn 3d5/2 spectra of SBZA sample exposure at 170°C for 7 min after etching for (a) 0 s (initial surface), (b) 10 s, (c) 20 s, (d) 80 s, (e) 140 s, and (f) 260 s.
(a)
(b)
(c)
(d)
(e)
(f)Figure8 shows the XPS spectra of Al 2p depth profiles of oxide film in SBZA sample. The XPS peak height (Al content can be estimated) on the subsurface of oxidation is higher than that on the outer surface. The detected segregation layer of Al is very thin, distributed over a depth of about 12–48 nm from the outer surface. There is no visible Al peak detected beyond the area. From Figure 8, it is found that an almost invisible peak around 75.1 eV is showing at the outer film surface. After etching for 20 s, a new peak located at 72.2 eV arises corresponding to metal Al. It implies the enrichment behavior of element Al at the subsurface that the atom Al can be kept as a lower chemical state, Al0. While the etching time increases to 80 s, both kinds of peaks shift to higher energy direction. It suggests that there is a new chemical state of Al in the oxide. Based on [18], this peak position for Al 2p approaches that of Al2O3, with 0.9~1.9 eV deviation which might result by Sn and Bi dissolved in the oxidation film. However, further research is necessary to clarify the Al mechanism in the protective oxide film.Figure 8
Al 2p spectra of SBZA sample exposure at 170°C for 7 min after etching for (a) various times from 0 s to 140 s, (b) 0 s (initial surface), (c) 20 s, and (d) 80 s.
(a)
(b)
(c)
(d)Combined with the result of semiquantitative analysis (see Figure2), it is reasonable to propose that there is a triple-layer oxidation film structure. The outer surface should mainly comprise of O in physical status and ZnO with about 6 nm in thickness. The subsurface should be ZnO and Al2O3 doped with Sn4+ and Bi3+ to about 30–84 nm thickness according to Al element getting to almost zero and Sn metal contents almost being the main in all forms of Sn, which could be a protective film to prevent further oxidation of the molten solder alloy in atmosphere condition. And the inner remaining thickness of the film layer should be (Sn, Bi, and Zn) O as a transition layer.


## 4. Conclusion

The properties of the oxide film that forms on liquid SBZ solder and the effect of Al/P addition on the film properties were investigated by XPS depth profiling at 170°C for 7 min:(1)
It was found that the thickness of the SBZ oxide was approximately 216 nm. Further XPS analysis revealed that the oxide film close to the substrate mainly composed of Sn2+ oxides which consisted mostly of Zn2+ oxides near the free surface. The amount of Sn4+ and Bi3+ oxides generated near the film surface was found to be similar to the three types of samples.(2)
With 0.005 wt.% Al addition to SBZ creating a SBZA alloy, a triple-layer oxidation film structure can be observed. The outer surface should mainly comprise of physical absorbed O and ZnO. Oxides of Zn and Al are mainly responsible for the formation of the subsurface of SBZA alloy. The oxides of Sn and Bi forming the innermost layer also contribute a little to the film formation. Considerable Al segregation occurs towards the surface principally as Al2O3.(3)
A trace amount of P doped to SBZ could not decrease the thickness of the oxidation film. But the Zn content in the outer surface of oxidation was decreased. This supports the idea that a minus P can protect Zn from excess oxidation.(4)
This work suggests that the solders with Zn can be considered as a potential alternative with trace amount of Al addition for low melting point solders, especially when the oxidation of the liquid solder is a concern.



---

*Source: 257231-2015-07-08.xml*