# Comparative Assessment of Antimicrobial Efficiency of Ionic Silver, Silver Monoxide, and Metallic Silver Incorporated onto an Aluminum Oxide Nanopowder Carrier

Authors: Agnieszka Maria Jastrzębska; Ewa Karwowska; Andrzej R. Olszyna; Antoni R. Kunicki
Journal: Journal of Nanoscience
 (2013)

---

## Abstract

The present paper provides comparative assessment of antimicrobial efficiency of ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) incorporated onto an aluminum oxide nanopowder carrier (Al2O3). The deposition of Ag+ ions, Ag2O nanoparticles, and Ag nanoparticles on an different phases of aluminum oxide nanopowder carrier was realized using consecutive stages of dry sol-gel method. The Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders were widely characterized qualitatively and quantitatively by SEM, physical nitrogen sorption and XRD analyses. Results indicate that the Al2O3 nanopowders added with Ag+, Ag2O, and Ag, apart from phase composition, were not differing considerably from one another in terms of their morphology and physical properties. However, nanopowders of Al2O3-Ag were more agglomerated than Al2O3-Ag2O and Al2O3-Ag+ nanopowders. The antibacterial activity of the nanopowders was examined by the spread plate method using bacterial strains such as Escherichia coli, Sarcina lutea, and Bacillus subtilis. The best antibacterial properties against Sarcina lutea strain were achieved in the amorphous-Al2O3-Ag+ and Al2O3-Ag2O nanopowders, whereas the worst antimicrobial activity against Bacillus subtilis and Escherichia coli was shown by the Al2O3-Ag+ and Al2O3-Ag nanopowders. The observed increase of the antibacterial activity as the silver content was not however significant for Al2O3-Ag nanopowders. The results obtained in the present experiments show that the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders, possessing good bactericidal properties, can be produced by using consecutive stages of dry sol-gel method, and Al2O3 nanopowder added with Ag2O is considered as the best raw material in the production of antiseptic materials.


---

## Body

## 1. Introduction

At present, there is great demand from the industry for materials that show biocidal properties. That is why, since several years, many research centers all over the world have focused their interest on different forms of silver, mainly metallic silver nanoparticles. Because of their small size, the silver nanoparticles show high-chemical activity dependent on both their sizes and shapes [1]. They have also good antirheumatic [2] and antiinflammatory [3] properties. Results also indicate that the bactericidal effect of the Ag nanoparticles was a synergic action of Reactive Oxygen Species (ROS) and Ag+, not an additive one [4].However, unbound silver particles can easily be removed from the carrier material during exploitation. An additional problem is the natural liability of silver nanoparticles to agglomeration, which results in loss of their biological activity. It is therefore necessary that silver should be built onto the surface of the carrier material. Currently, ionic Ag+ as well as Ag2O and Ag nanoparticles are considered to be an advantageous addition to matrices of various types [5, 6]. Their more important recent applications include dressing materials [7], packaging materials [6] glass-ceramic coatings [8], coatings on implants [9], filtration membranes [10], and antifouling coatings [10]. However, among many known inert carriers, the most promising material is aluminum nanooxide. It is most often used in the form of shaped porous pieces [11], microspheres [12], or nanoneedles [7]. Microbiological investigation results indicate that AgCO3/Al2O3 [7], AgCl/Al2O3, and Ag/Al2O3 [13] exhibit high bactericidal activity at room temperature with no need for any light or electrical power input [13]. In our earlier work, we have used the particles of aluminum oxide as the carrier for silver nano-particles [14]. Our investigation results have also shown that the γ-Al2O3-Ag nanopowders exhibit large specific surface area and good antimicrobial properties [14, 15].However according to above mentioned literature data, there is an evident lack of scientists’ unanimity in the comparison of the antibacterial properties of different forms of silver to pathogenic bacteria. This is due to the fact that they are acquired by using various synthesis procedures and methods, which result in different morphology and physical properties of the resulting material, making the ability of their antimicrobial properties comparison impossible.The present paper provides a comparative assessment of antimicrobial efficiency of ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) incorporated onto an aluminum oxide nanopowder carrier (Al2O3) in the amorphous form or gamma and eta form. To obtain the above-mentioned nanoparticles possessing similar morphology and physical properties, we have decided to use consecutive stages of the dry sol-gel method [16]. According to our best knowledge, this method has been used for the first time for such a purpose. The dry sol-gel method has been also chosen by us because it is considered to be much more “clean” from the chemical point of view, since during this process, apart from carbon dioxide, no other undesired side products appear which could be harmful to the environment [14]. It also enables acquiring ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) deposited on an aluminum oxide nanopowder carrier. This can be easily done by using consecutive stages of this process.


## 2. Materials and Methods

### 2.1. Techniques for Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag Nanopowders Synthesis

Ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) were deposited on an aluminum oxide nanopowder carrier by using consecutive stages of dry sol-gel method. A flow chart of the processes used in the present study is shown in Figure 1 and its detailed description is given below. All the reagents were delivered by the Sigma Aldrich Co. and were used in the delivery state.Figure 1
Flow chart of the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders synthesis process as well as methods of analyzes.Dry sol-gel method consists of a mild reaction between a mixture of a metal-organic aluminum compound (triethylaluminium—Et3Al) and alumoxan (aluminum triisopropoxide (i-PrO)3Al) with oxygen from the air. The reaction was conducted in an organic solvent (hexane). The reagents were added in such amounts that the concentration of the aluminum compounds was 0.1 M. The silver benzoate was then added to reactive mixture so that the silver content in the final product was 0.0, 0.30, 1.35, 2.84, and 12.55 wt%. Subsequently, solvent was removed and resulting powder was dried in air at 25°C, 24 h. This process gave ionic silver deposited on amorphous aluminum nanooxide carrier (Al2O3-Ag+) (1). Precursor was then subjected to thermal decomposition in air at 700°C for 24 h in a muffle furnace. This process gave single-valent silver oxide nanoparticles deposited on aluminum nanooxide carrier (Al2O3-Ag2O) (2). The intermediary product thus obtained was subjected to reduction in a hydrogen atmosphere at 700°C for 2 h, which yielded the final product, that is, the Al2O3-Ag nanopowder (3). The reactions described above are described by the formulae
(1)(i-PrO)3Al+Et3Al→O2,C6H14,C7H5COO-Ag+,dryingAl2O3-C7H5COO-Ag+(2)Al2O3-C7H5COO-Ag+→O2,700°C,24hAl2O3-Ag2O+CO2+H2O(3)Al2O3-Ag2O→H2,700°C,2hAl2O3-Ag+H2O


### 2.2. Experimental Procedure

The phase composition of the nanopowders was examined with an X-ray diffractometer (XRD-Philips 1830) using a copper lamp radiation (CuKα). A qualitative phase analysis was based on the data recorded within the 2θ angle range from 20° to 120° at a 2θ increment of 0.05° and a counting time of 3 s.The morphology of the nanopowders was examined in a scanning electron microscope (SEM-LEO 1530, Zeiss) operated at an accelerating voltage of 2.0 kV. The test nanopowder samples were prepared according to the following procedure. After preparing a mixture of the nanopowder in propan-2-ol using an ultrasonic homogenizer for 1 min, a drop of it was placed, with a pipette, on a polished thin monolithic silicon plates. Then, the surface of each of the plates was dried, and the deposited nanopowders were coated with a thin carbon layer using a BAL-TEC SCD 005 duster equipped with a CEA 035 unit.The microscopic examinations were also aimed at characterising quantitatively the nanopowders by the so-called stereological analysis using a MicroMeter v.086b computer program designed for analysing and processing the images of microstructures. The stereological analysis of the nanopowders also utilized the SEM images. The stereological parameters were measured on the individual cross sections of the nanopowder particles and then; the average value of a given parameterd2 was calculated. The calculated value of the average size d2¯ of a particle or agglomerate, also called the equivalent diameter, is defined as the diameter of a circle with the surface area equal to that of the analyzed particle or agglomerate. The analysis also took into account the coefficient of variation CV (d2) of the measured values with a parameter n=327 for particles and n=121 for agglomerates statistical analysis.The specific surface area of the nanopowders was examined based on the isotherms of the physical nitrogen adsorption measured experimentally, using a Quadrasorb-SI device (Quantachrome Co). Before the measurements, the samples were degassed at a temperature of 350°C for 48 h. The adsorption and desorption of nitrogen on the surface of the nanoparticles were measured at a temperature of −195.8°C, within the entire range of the relative pressure. The specific surface areaSBET was determined using the Brunauer, Emmett, Teller, method and the BET equation, which permit determining the specific surface area within the range of the relative pressure PP0-1 from 0.05 to 0.35.The total volume of the pores present in the nanopowders,VBJH, was determined by the Barret, Joyner, and Halenda method and using the BJH equation based on the isotherms of the physical desorption of nitrogen. The assumption underlying this method is that during the capillary condensation at the relative pressure below 0.4, the only effect which occurs with a further increase of the pressure is the thickening of the mono-layer of the adsorbate formed on the surface of the pore walls. The distributions of the pore sizes determined by the BJH method were used for estimating the average pore size DBJH.Finally, the bactericidal activity of the Al2O3-Ag powders was examined by the spread plate method. The microorganisms examined in the present experiments came from the private collection of Biology Department, Faculty of Environmental Engineering, Warsaw University of Technology, and included bacteria strains such as Escherichia coli, Sarcina lutea,andBacillus subtilis. The bacteria strains were inoculated on a nutrient agar medium (delivered by the MERCK), appropriately prepared and sterilized, which was deposited in Petri plates. The inoculation was performed using a sterile glass rod. The bacteria were spread on the surface of the nutrient medium, where an appropriate powder was then deposited. The growth inhibition zone of each bacterial strain was determined after incubation at a temperature of 37°C (Escherichia coli) or 26°C (other bacterial cultures) for 72 h. Subsequently, photographic documentation of the Petri plates was performed. Because the nanopowders were not regularly distributed (the area occupied by each of the nanopowders was not 6.35 mm standardized width according to Kirby-Bauer method) [17], antimicrobial efficiencies of nanopowders were assessed by means of the Kirby-Bauer method, adjusted to the analysis of the nanopowders. The relative bacterial inhibition zone DK-B was determined by using equation
(4)DK-B=6,35·D1D2,
where 6,35 is a standardized width of a Kirby-Bauer paper disc (mm), D1 is the width of a bacterial inhibition zone (mm) and D1=(D1a+D1b+···+D1h)/8, D2 is the width of a zone occupied by the nanopowder (mm) and D2=(D2a+D2b+···+D2h)/8.Method for determiningD1 and D2 parameters is also presented in Figure 2. The D1 parameter represents the inhibition zone (a dark area around a nanopowder) in which the growth of a bacterium susceptible to the powder is inhibited. The size (width) of this zone is proportional to how sensitive the particular microorganism is. The D2 parameter represents the width of a zone occupied by the particular nanopowder. It should be however noted that the width of the bacterial inhibition zone is always the same, no matter what amount of zone the particular nanopowder will occupy. Thus, it can be assumed that the width of a bacterial inhibition zone depends only on its antibacterial properties and the concentration of the powder at different measured areas is not significant.Figure 2
Method for determiningD1 and D2 parameters for modified Kirby-Bauer method.Measurement of each of the parameter was repeated eight times around a circle (Figure2) and performed by using NIS Elements 3.22.11 (Nikon) computer program designed for photodocumentation analysis and processing. The results were presented in Figure 7 as mean ± standard deviation.


## 2.1. Techniques for Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag Nanopowders Synthesis

Ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) were deposited on an aluminum oxide nanopowder carrier by using consecutive stages of dry sol-gel method. A flow chart of the processes used in the present study is shown in Figure 1 and its detailed description is given below. All the reagents were delivered by the Sigma Aldrich Co. and were used in the delivery state.Figure 1
Flow chart of the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders synthesis process as well as methods of analyzes.Dry sol-gel method consists of a mild reaction between a mixture of a metal-organic aluminum compound (triethylaluminium—Et3Al) and alumoxan (aluminum triisopropoxide (i-PrO)3Al) with oxygen from the air. The reaction was conducted in an organic solvent (hexane). The reagents were added in such amounts that the concentration of the aluminum compounds was 0.1 M. The silver benzoate was then added to reactive mixture so that the silver content in the final product was 0.0, 0.30, 1.35, 2.84, and 12.55 wt%. Subsequently, solvent was removed and resulting powder was dried in air at 25°C, 24 h. This process gave ionic silver deposited on amorphous aluminum nanooxide carrier (Al2O3-Ag+) (1). Precursor was then subjected to thermal decomposition in air at 700°C for 24 h in a muffle furnace. This process gave single-valent silver oxide nanoparticles deposited on aluminum nanooxide carrier (Al2O3-Ag2O) (2). The intermediary product thus obtained was subjected to reduction in a hydrogen atmosphere at 700°C for 2 h, which yielded the final product, that is, the Al2O3-Ag nanopowder (3). The reactions described above are described by the formulae
(1)(i-PrO)3Al+Et3Al→O2,C6H14,C7H5COO-Ag+,dryingAl2O3-C7H5COO-Ag+(2)Al2O3-C7H5COO-Ag+→O2,700°C,24hAl2O3-Ag2O+CO2+H2O(3)Al2O3-Ag2O→H2,700°C,2hAl2O3-Ag+H2O


## 2.2. Experimental Procedure

The phase composition of the nanopowders was examined with an X-ray diffractometer (XRD-Philips 1830) using a copper lamp radiation (CuKα). A qualitative phase analysis was based on the data recorded within the 2θ angle range from 20° to 120° at a 2θ increment of 0.05° and a counting time of 3 s.The morphology of the nanopowders was examined in a scanning electron microscope (SEM-LEO 1530, Zeiss) operated at an accelerating voltage of 2.0 kV. The test nanopowder samples were prepared according to the following procedure. After preparing a mixture of the nanopowder in propan-2-ol using an ultrasonic homogenizer for 1 min, a drop of it was placed, with a pipette, on a polished thin monolithic silicon plates. Then, the surface of each of the plates was dried, and the deposited nanopowders were coated with a thin carbon layer using a BAL-TEC SCD 005 duster equipped with a CEA 035 unit.The microscopic examinations were also aimed at characterising quantitatively the nanopowders by the so-called stereological analysis using a MicroMeter v.086b computer program designed for analysing and processing the images of microstructures. The stereological analysis of the nanopowders also utilized the SEM images. The stereological parameters were measured on the individual cross sections of the nanopowder particles and then; the average value of a given parameterd2 was calculated. The calculated value of the average size d2¯ of a particle or agglomerate, also called the equivalent diameter, is defined as the diameter of a circle with the surface area equal to that of the analyzed particle or agglomerate. The analysis also took into account the coefficient of variation CV (d2) of the measured values with a parameter n=327 for particles and n=121 for agglomerates statistical analysis.The specific surface area of the nanopowders was examined based on the isotherms of the physical nitrogen adsorption measured experimentally, using a Quadrasorb-SI device (Quantachrome Co). Before the measurements, the samples were degassed at a temperature of 350°C for 48 h. The adsorption and desorption of nitrogen on the surface of the nanoparticles were measured at a temperature of −195.8°C, within the entire range of the relative pressure. The specific surface areaSBET was determined using the Brunauer, Emmett, Teller, method and the BET equation, which permit determining the specific surface area within the range of the relative pressure PP0-1 from 0.05 to 0.35.The total volume of the pores present in the nanopowders,VBJH, was determined by the Barret, Joyner, and Halenda method and using the BJH equation based on the isotherms of the physical desorption of nitrogen. The assumption underlying this method is that during the capillary condensation at the relative pressure below 0.4, the only effect which occurs with a further increase of the pressure is the thickening of the mono-layer of the adsorbate formed on the surface of the pore walls. The distributions of the pore sizes determined by the BJH method were used for estimating the average pore size DBJH.Finally, the bactericidal activity of the Al2O3-Ag powders was examined by the spread plate method. The microorganisms examined in the present experiments came from the private collection of Biology Department, Faculty of Environmental Engineering, Warsaw University of Technology, and included bacteria strains such as Escherichia coli, Sarcina lutea,andBacillus subtilis. The bacteria strains were inoculated on a nutrient agar medium (delivered by the MERCK), appropriately prepared and sterilized, which was deposited in Petri plates. The inoculation was performed using a sterile glass rod. The bacteria were spread on the surface of the nutrient medium, where an appropriate powder was then deposited. The growth inhibition zone of each bacterial strain was determined after incubation at a temperature of 37°C (Escherichia coli) or 26°C (other bacterial cultures) for 72 h. Subsequently, photographic documentation of the Petri plates was performed. Because the nanopowders were not regularly distributed (the area occupied by each of the nanopowders was not 6.35 mm standardized width according to Kirby-Bauer method) [17], antimicrobial efficiencies of nanopowders were assessed by means of the Kirby-Bauer method, adjusted to the analysis of the nanopowders. The relative bacterial inhibition zone DK-B was determined by using equation
(4)DK-B=6,35·D1D2,
where 6,35 is a standardized width of a Kirby-Bauer paper disc (mm), D1 is the width of a bacterial inhibition zone (mm) and D1=(D1a+D1b+···+D1h)/8, D2 is the width of a zone occupied by the nanopowder (mm) and D2=(D2a+D2b+···+D2h)/8.Method for determiningD1 and D2 parameters is also presented in Figure 2. The D1 parameter represents the inhibition zone (a dark area around a nanopowder) in which the growth of a bacterium susceptible to the powder is inhibited. The size (width) of this zone is proportional to how sensitive the particular microorganism is. The D2 parameter represents the width of a zone occupied by the particular nanopowder. It should be however noted that the width of the bacterial inhibition zone is always the same, no matter what amount of zone the particular nanopowder will occupy. Thus, it can be assumed that the width of a bacterial inhibition zone depends only on its antibacterial properties and the concentration of the powder at different measured areas is not significant.Figure 2
Method for determiningD1 and D2 parameters for modified Kirby-Bauer method.Measurement of each of the parameter was repeated eight times around a circle (Figure2) and performed by using NIS Elements 3.22.11 (Nikon) computer program designed for photodocumentation analysis and processing. The results were presented in Figure 7 as mean ± standard deviation.


## 3. Results

The phase composition of the nanopowders was examined by X-ray diffractometry. The presence of amorphous aluminium, aluminum oxide, silver monoxide, and metallic silver in the nanopowders was confirmed by XRD examinations. The diffractogram obtained for the Al2O3-Ag+ revealed the presence of the amorphous aluminium oxide phase (Figure 3(a)). There was no evidence for any silver phase. It should be however noted that the XRD method is not able to detect organic phases. Thus, the acquired result however confirms the presence of Ag+ in the nanopowder. The intermediate product of the synthesis process, obtained after the thermal decomposition process (Al2O3-Ag2O), contained gamma and eta aluminium oxide phases and the 1-valent silver oxide phase (Figure 3(b)) which then, during the reduction process, was entirely transformed into metallic silver (Figure 3(c)). The final product, that is, the Al2O3-Ag (2.84 wt%) nanopowder, did not contain the eta phase of aluminum oxide, since it had been entirely transformed into the more stable gamma phase.XRD diffractograms obtained for the Al2O3-Ag+ nanopowder (a), intermediary product after the thermal decomposition conducted at a temperature of 700°C for 24 h (Al2O3-Ag2O) (b), and the final product after the reduction process conducted at a temperature of 700°C for 2 h in H2 (Al2O3-Ag) (c). The final product contained 2.84 wt% of silver.
(a)
(b)
(c)However, the silver additive affected the morphology and liability to agglomeration of the resulting nanopowders was analyzed in a scanning electron microscope. By way of example, Figure4 shows SEM images obtained for the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders. We can see that they contain both agglomerates and single particles. Images also show that, at higher Ag+, Ag2O, and Ag contents, nanopowders that have more significant liability to agglomeration and nanopowders added with Ag are much more agglomerated than those, added with Ag+ and Ag2O.Figure 4
SEM images obtained for the nanopowders such as Al2O3-Ag+ (a), Al2O3-Ag2O (b), and Al2O3-Ag (c) produced by using consecutive stages of the dry sol-gel method. The silver content in the final product was 0.0 wt% (samples marked with 0), 0.30 wt% (samples marked with 1), 1.35 wt% (samples marked with 2), 2.84 wt% (samples marked with 3), and 12.55 wt% (samples marked with 4).The SEM images were also used in the stereological analysis. The results are given in Figure5 and in Tables 1 and 2. Results of the particle stereological analysis (Table 1) show that the average particle sizes of the nanopowders added with Ag+, Ag2O, and Ag does not differ much from each other (Figures 5(a), 5(b) and 5(c)). The range of particle sizes of nanopowders added with Ag+ and Ag is similar to that of pure Al2O3. However, Al2O3-Ag2O particle stereological analysis shows that the range of particle sizes of these nanopowders is smaller in comparison with that of pure Al2O3 (Figure 5(b)). Results of the agglomerate stereological analysis (Table 2) show that at higher Ag+ and Ag2O contents (Figures 5(a) and 5(b)), the average agglomerate size does not differ much from that observed in the pure Al2O3 nanopowder (312 nm, coefficient of variation = 54 nm). It was only with the Al2O3-Ag nanopowders when the concentration of Ag becomes highly disadvantageous: the particle size increases from 310 nm (sample 2) to 505 nm and 962 nm (samples 3, and 4, resp.) (Figure 5(c)). Others results also confirm that morphology of the particles plays an important role in silver particles antimicrobial activity. Pal et al. [18] showed that triangular-shaped silver nanoplates displayed the strongest biocidal action against E. coli, compared with spherical and rod-shaped nanoparticles and with Ag+ ions (in the form of AgNO3).Table 1
Results of the particle stereological analysis of the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders produced by thermal decomposition at 700°C for 24 h followed by reduction in H2 conducted at 700°C for 2 h.
Sample numbers(Ag concentration)
Al2O3-Ag+ particle
Al2O3-Ag2O particle
Al2O3-Ag particle
d
2
¯/nm
CV (d2)/[%]
d
2
¯/nm
CV (d2)/[%]
d
2
¯/nm
CV (d2)/[%]
0  (0.00 wt%)
65
18
65
20
—
—
1 (0.30 wt%)
55
20
35
28
49
28
2 (1.35 wt%)
54
23
39
23
45
34
3 (2.84 wt%)
51
26
37
27
41
36
4 (12.55 wt%)
48
32
38
30
59
30Table 2
Results of the agglomerate stereological analysis of the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders produced by thermal decomposition at 700°C for 24 h followed by reduction in H2 conducted at 700°C for 2 h.
Sample numbers(Ag concentration)
Al2O3-Ag+agglomerate
Al2O3-Ag2O agglomerate
Al2O3-Ag agglomerate
d
2
¯/nm
CV (d2)/[%]
d
2
¯/nm
CV (d2)/[%]
d
2
¯/nm
CV (d2)/[%]
0  (0.00 wt%)
312
54
312
54
—
—
1 (0.30 wt%)
270
54
291
53
388
73
2 (1.35 wt%)
226
51
302
50
310
43
3 (2.84 wt%)
344
40
370
57
505
44
4 (12.55 wt%)
336
62
356
54
962
63Particle and agglomerate size distributions of the nanopowders produced by using consecutive stages of the dry sol-gel method such as Al2O3-Ag+ after hexane evaporation at 25°C, 24 h, air atmosphere (a); Al2O3-Ag2O after thermal decomposition at 700°C, 24 h, air atmosphere (b); and Al2O3-Ag after reduction at 700°C, 2 h, H2 atmosphere (c). The silver content in the final product was 0.0 wt% (samples marked with 0), 0.30 wt% (samples marked with 1), 1.35 wt% (samples marked with 2), 2.84 wt% (samples marked with 3), and 12.55 wt% (samples marked with 4).
(a)
(b)
(c)The specific surface area of the Al2O2-Ag nanopowders and their open porosity which characterizes the structure of the nanopowder agglomerates were examined based on the isotherms of nitrogen physical sorption determined experimentally. The results including the specific surface area, the total volume of the pores, and the average pore diameter are given in Table 3. We can see that the specific surface area of the sample 2 added with Ag2O and Ag exceeds 200 m2g−1, with the total pore volume above 1.1×10-3 m3g−1 and the average pore diameter exceeding 20 nm. The lower specific surface area, below 180 m2g−1, was found in the other samples (0, 1, 3 and 4) added with Ag2O and Ag with the total pore volume below 1×103 m3g−1. For example, high specific surface area of the Al2O3 nanopowder (above 250 m2g−1) indicates that this nanopowder is highly amorphous and that the possible agglomerates have a very loose structure. Our results can be compared with those of Buckley et al. [7] suggesting that the antibacterial performance (against Staphylococcus aureus and Pseudomonas aeruginosastrains) of alumina-supported materials exhibits a striking increase with bacteria inhibition zone size and is directly proportional to the carbonate surface area.Table 3
Physical properties of the Al2O3-Ag+, Al2O3-Ag2O, and Al2O3-Ag nanopowders produced by the thermal decomposition (700°C, 24 h) followed by reduction (H2, 700°C, 2 h).
Sample numbers(Ag concentration)
Al2O3-Ag+
Al2O3-Ag2O
Al2O3-Ag
S
BET/m2g−1
V
BJH × 10−3/m3g−1
D
BJH/nm
S
BET/m2g−1
V
BJH × 10−3/m3g−1
D
BJH/nm
S
BET/m2g−1
V
BJH × 10−3/m3g−1
D
BJH/nm
0  (0.00 wt%)
252,60
0,835
4
169,60
0,758
8
—
—
—
1 (0.30 wt%)
118,50
0,506
25
161,80
0,632
6
148,50
0,616
11
2 (1.35 wt%)
198,60
0,808
2
228,10
1,346
22
208,00
1,199
11
3 (2.84 wt%)
151,30
0,490
5
175,80
0,619
8
157,60
0,642
7
4 (12.55 wt%)
228,00
0,518
4
178,60
0,539
6
172,90
0,456
6Investigations of the antimicrobial properties of the pure Al2O3 nanopowder as well as added with Ag+, Ag2O and Ag were performed using the classical culture method. The results of the examination of the antiseptic properties of the nanopowders by means of the culture method as well as relative bacterial growth inhibition zone analysis are shown in Figures 6 and 7. They indicate that the inhibitory effect against the individual bacterial strains varied greatly depending on the composition of the nanopowder and it was enhanced with increasing silver content. Figure 6 shows exemplary photographs of the Petri plates covered with pure Al2O3 and Al2O3-Ag+, Ag2O, and Ag nanopowders. Dark areas (inhibition zones) visible around the examined nanopowders are evidence that they inhibit the growth of bacteria such as Escherichia coli, Sarcina lutea, and Bacillus subtilis. Results indicate that the bacterial growth inhibition zones only occur on the Petri plates covered with silver-added Al2O3 nanopowders. No such rings are observed on the surfaces of the Petri plates covered with pure Al2O3 nanopowder (no silver addition-samples: Ag-0, Ag-cal-0 and Ag-red-0) which itself has evidently no biocidal properties.Photographs of the selected parts of Petri plates covered with nanopowders such as Al2O3-Ag+ (a), Al2O3-Ag2O (b), and Al2O3-Ag (c) produced by using consecutive stages of the dry sol-gel method after 72 h incubation. The silver content in the final product was 0.0 wt% (samples marked with 0), 0.30 wt% (samples marked with 1), 1.35 wt% (samples marked with 2), 2.84 wt% (samples marked with 3), and 12.55 wt% (samples marked with 4).
(a)
(b)
(c)Quantitative results of a growth test method of the bacterial strains such asBacillus subtilis (a), Escherichia coli (b) and Sarcina lutea (c). The silver content in the final product was 0.0 wt% (samples marked with 0), 0.30 wt% (samples marked with 1), 1.35 wt% (samples marked with 2), 2.84 wt% (samples marked with 3), and 12.55 wt% (samples marked with 4).
(a)
(b)
(c)Quantitative results of an growth test indicate that the relative bacterial growth inhibition zone does not exceed 12 mm for nanopowders added with Ag+ and Ag for all examined bacteria (Figure 7). The best antibacterial properties against Sarcina lutea strain were achieved in the Al2O3 nanopowders added with Ag+ and Ag2O, whereas the lowest effect was observed for Bacillus subtilis and Escherichia coli in case of the Al2O3-Ag+ and Al2O3-Ag nanopowders. The relative growth inhibition zone for Al2O3-Ag+ nanopowders exceeded 16.5 mm, showing that the bacteria inhibition was about 100% better in comparison with Al2O3 nanopowder. The observed increase of the bactericidal activity, as the silver content was increased, was not however significant for Al2O3-Ag nanopowders. With the nanopowder containing Ag+, no substantial enhancement of the inhibitory effect was observed for Escherichia coli. Further Ag+ increase did not improve appreciably the antibacterial effectiveness of the nanopowders. Also Choi et al. [19] based on a prolonged microtiter assay demonstrated that at about 4.2 μM Ag, the inhibitions on the growth of Escherichia coli by Ag nanoparticles, Ag+ ions, and AgCl colloids were about 55%, 100%, and 66%, respectively. Similar results were obtained by Chang et al. [13]. They investigated the catalytic inactivation of E. coli(E. coli) in water by Al2O3-Ag and Al2O3-AgCl particles. Their results showed that Al2O3-Ag (at 50 mg/L) with the larger amount of eluted Ag+ actually exhibited stronger bactericidal activity than Al2O3-AgCl, which implied that Ag+ may play an important role in the bactericidal process. Our results can be also compared with those of Buckley et al. [7] who investigated the antimicrobial activity of the Ag/meso-Al2O3 by zone plate inhibition method against Staphylococcus aureus and Pseudomonas aeruginosastrains. The normalised zone of inhibition of the supported Ag2CO3 nanoparticles far exceeded that of bulk AgO, Ag2CO3, and Ag2O. Our investigation results have also shown that the γ-Al2O3-Ag nanopowders exhibit large specific surface area and good antimicrobial properties [14, 15].


## 4. Conclusions

Ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) were incorporated onto an aluminum oxide nanopowder carrier by using subsequent stages of dry sol-gel method. The Al2O3 nanopowders added with Ag+, Ag2O and Ag differed considerably from one another in terms of their morphology, physical, and biocidal properties. Since the work of Xiu et al. [20], it has been generally accepted that the catalytically bactericidal effect of silver nanoparticles comes from a synergic action of reactive oxygen species as a result of Ag+ ions release, not however from single Ag nanoparticles. Thus, it is strongly recommended that the morphostructural aspects of the synthesized nanopowders should be discussed with respect to the possible enhancement of the Ag+ ions release. Also other scientific groups results suggest that that silver nanoparticles could undergo a shape-dependent interaction with bacteria. For example, the presence of a {111} plane in crystalline lattice combine to promote Ag nanoparticles biocidal property due to the enhancement of Ag+ ions release [18].To our knowledge, this is the first comparative study on the bactericidal properties of ionic silver (Ag+), silver monoxide (Ag2O), and metallic silver (Ag) incorporated onto an aluminum oxide nanopowder carrier characterized by different morphostructural properties and agglomeration tendency. Nanopowders of Al2O3-Ag+ were not much less agglomerated with the average agglomerate sizes below 340 nm. The Al2O3 nanopowder also had very large specific surface area (above 250 m2g−1) which was evidence that it was highly amorphous and that the possible agglomerates had a very loose structure. This could probably enable better ability of Ag+ ions release ability. The Al2O3 nanopowders added with Ag2O were not also much agglomerated with average particles below 38 nm and agglomerates below 370 nm. It was only with the Al2O3-Ag nanopowders when the Ag effect (higher Ag nanoparticles addition) becomes highly disadvantageous: the particle size increased from 310 nm to 962 nm with increasing Ag content from 0.30 to 12.55 wt%.The best antibacterial properties againstSarcina lutea strain were achieved in the Al2O3 nanopowders added with Ag+ and Ag2O probably due to the fact that these samples were less agglomerated in comparison with Al2O3-Ag, and their morphostructure could enhance Ag+ ions release. Surprisingly, the observed increase of the bactericidal activity as the silver content was increased from 2.84 to 12.55 wt% was not however significant for all of the synthesized nanopowders. Also Choi et al. [19] described ionic form of silver as being much more effective in bacteria killing in comparison with silver nanoparticles. Their work was not however devoted to investigations of nanoparticles agglomeration tendency.Our results demonstrate that the worst effect againstEscherichia coli and Sarcina lutea was shown by the Al2O3-Ag+ and Al2O3-Ag nanopowders, respectively. Moreover, the increase in bactericidal activity was not significant with increasing Ag content from 0.30 to 12.55 wt%.The results obtained in the present experiments show that the Al2O3 nanopowder added with Ag2O produced by the sol-gel method is considered as the best raw material for the production of biocidal materials. It is, however, worth noting that the dry sol-gel method is much more “clean” from the chemical point of view, since during this process, apart from carbon dioxide, no other undesired side products appear which could be harmful to the environment.



---