# Microstructure and Mechanical Properties of Microwave Sintered ZrO2 Bioceramics with TiO2 Addition

Authors: Hsien-Nan Kuo; Jyh-Horng Chou; Tung-Kuan Liu
Journal: Applied Bionics and Biomechanics
 (2016)

---

## Abstract

The microwave sintered zirconia ceramics with 0, 1, 3, and 5 wt% TiO2 addition at a low sintering temperature of 1300°C and a short holding time of 1 hour were investigated. Effect of contents of TiO2 addition on microstructure and mechanical properties of microwave sintered zirconia bioceramics was reported. In the sintered samples, the main phase is monoclinic zirconia (m-ZrO2) phase and minor phase is tetragonal zirconia (t-ZrO2) phase. The grain sizes increased with increasing the TiO2 contents under the sintering temperature of 1300°C. Although the TiO2 phase was not detected in the XRD pattern, Ti and O elements were detected in the EDS analysis. The presence of TiO2 effectively improved grain growth of the ZrO2 ceramics. The Vickers hardness was in the range of 125 to 300 Hv and increased with the increase of TiO2 contents. Sintering temperature dependence on the Vickers hardness was also investigated from 1150°C to 1300°C, showing the increase of Vickers hardness with the increase of the sintering temperature as well as TiO2 addition.


---

## Body

## 1. Introduction

Zirconia (ZrO2) has become one of the most important ceramic materials since 1970s because of the discovery of transformation toughening mechanisms. There are three different polymorphs which existed in pure zirconia, such as monoclinic (m), tetragonal (t), and cubic (c) phases [1, 2]. It is well known that the monoclinic phase existed and is stable at room temperature up to 1170°C; the tetragonal phase is formed and is stable at temperatures above 1170°C up to 2370°C; and the cubic phase is stable above 2370°C [3]. These existent phases depend on the temperature and compositional ranges under equilibrium conditions. Moreover, ZrO2 ceramic shows many special properties, such as high elastic modulus, high fracture toughness, high wear resistance, suitable ionic conductivity, chemical inertness, and high melting temperature [2, 4]. Because of such excellent physical and chemical properties, ZrO2 ceramic is attractive to be a biomaterial and is a popular alternative to alumina as dental bioceramic [5–7].To increase its industrial applicability, it is desired to retain the tetragonal phase at room temperature to provide favorable mechanical properties. Namely, methods for keeping the ZrO2 based solid solution as the tetragonal (t) phase and preventing deleterious t → m phase transformation during cooling after sintering shall be developed [2, 6]. In past, many research efforts reported that a proper percentage of stabilizers such as Y2O3, CeO2, and MgO could be used to hold the tetragonal phase from 1170°C to the room temperature, inhibiting the happening of crack propagation and providing relatively high fracture toughness [2, 6–9]. In addition, the combination of uniform grain size and densification of the ZrO2 based ceramics can in turn improve the mechanical properties [9]. Therefore, the processing of starting powders, composition, and sintering condition such as sintering time and temperature are important parameters to prepare the high quality bioceramics.It is known that, in conventional solid state sintering, the heat is transmitted radiantly to the surface of the material and reaches the internal core of the material by thermal conduction [10]. The sintered piece has approximately 22~25% shrinkage after final sintering. Typically, conventional solid state sintering may not provide uniform heating distribution and requires extended sintering process from 8 to 10 hours for the sintering of ZrO2 dental sample, causing much energy consumption [7].Microwave sintering technology has been used for sintering ceramic materials. In the microwave sintering environment, the suitable material absorbs energy through dielectric heating, and the temperature is more uniformly distributed in the ceramic material [11–14]. Since microwave sintering technology has many attractive features, including uniform heating distribution, rapid volumetric heating, and low cost, it leads to the higher production rates and lower energy consumption. Compared to the conventional sintering technology, it makes the process commercially attractive. Estimates of energy saving are 25% to 95% [14]. However, high purity ZrO2 is a low absorber of microwave energy. Therefore, addition of TiO2 into high purity ZrO2 was provided to improve the microwave coupling at a given temperature [10, 15]. It is expected that microwave sintering would have a lower temperature (below 1400°C) and a shorter process (2 hours) than conventional sintering [16]. The sintering temperature, the heating rate, and the sintering time can affect the grain size, density, and mechanical properties of the sintered ZrO2 ceramic.In this paper, the aim of this study is to investigate the effect of TiO2 content on the microstructure and mechanical properties of the microwave sintered ZrO2 with TiO2 addition at a low sintering temperature and a short holding time. In addition, the relation between the microstructure and mechanical properties is also discussed. Moreover, the dependence of the sintering temperature on the Vickers hardness was also investigated from 1150°C to 1300°C to verify the importance of TiO2 addition.


## 2. Materials and Methods

In this study, starting powders used ZrO2 with purity of 99.9% and TiO2 with purity of 99.85%. Four composite samples were prepared by adding TiO2 content from 0, 1, 3, and 5 wt% into ZrO2, respectively. The powders were mixed by wet ball-milling for 12 h in ethanol, using high purity zirconia balls as medium to achieve a homogeneous mixture. After milling, the mixed powders were dried at 90°C for 10 h. The dried powders were mechanically grounded and added with 10 wt% PVA solution. Five green samples, for each composition, with a diameter of 10 mm and a thickness of 1 mm were formed by uniaxially pressing. The samples were microwave sintered at the sintering temperatures of 1150, 1200, 1250, and 1300°C for a holding time of 1 hour in microwave oven. The heating rate was varied as 100°C/min up to 300°C for 1 h to burn out the binder and 100°C/min up to the final temperature under air atmosphere. The sintered samples were naturally cooled to the room temperature. In the study, the microwave furnace (Therm Wave Mod. III), with a continuously variable power of 2.45 GHz microwaves up to 1.3 kW, was used. To provide indirect heating of the powders, silicon carbide (SiC), having a very strong heating response to 2.45 GHz microwaves, was used as a susceptor. The samples were placed in the center of the susceptor and the sintering temperature was measured by insertion of a thermal couple around the susceptor.After sintering, the diameter and thickness of each sintered sample were measured with a digital caliper to calculate the shrinkage percent. The crystalline phases of the composite specimens were conducted by using X-ray diffraction (XRD, Bruker D8 Advance) analysis with CuKα radiation of λ
=
1.5406 Å using a Ni filter and with a secondary graphite monochromator. A scanning range of 2θ = 20°~60° with a step of 0.03° and 0.4 s as a count time per step was used. The morphology of the sintered samples was examined by scanning electron microscope (SEM, HORIBA EX-200) with the function of energy dispersive spectroscopy (EDS). The average grain size of the microwave sintered samples was obtained by analyzing SEM images using the linear intercept method on the fracture surfaces. The hardness of the sintered samples was conducted at room temperature by a micro-Vickers hardness tester (HM-113, Japan) with an indent load of 5 g held for 6 s on the surface of the microwave sintered samples. The measurement was repeated five times for each sample. With removal of the largest and smallest values during the measurement, the average value was determined to be the measured result.


## 3. Results and Discussion

### 3.1. XRD Analysis

Figure1 shows the XRD patterns of the microwave sintered ZrO2 samples with addition of 0, 1, 3, and 5 wt% TiO2 contents at 1300°C for 1 h. The main diffraction patterns of the tetragonal phase are around 2θ = 30°, 51°, and 60°. In these patterns, it was found that the diffraction patterns with reflections in 2θ = 28° and 31° were related to the main phase of monoclinic zirconia and low diffraction intensity with reflection in 2θ = 50.36° was related to second phase of tetragonal zirconia in the sintered samples for different TiO2 content [2, 6]. As reported in many researches, low-temperature cubic and tetragonal phases are meta-stable and would be converted into the monoclinic phase during cooling. Typically, the addition of stabilizers, such as Y2O3, CeO2, CaO, and MgO, to pure ZrO2 can provide multiphases which coexisted in a material, known as Partially Stabilized Zirconia (PSZ) [1, 2]. In this study, the addition of TiO2 seemed not to prevent t → m phase transformation during cooling. The result might be caused from the sintering temperature of 1300°C and the holding time of 1 hour which were much lower than conventional sintering temperature and time for the stabilizer [8]. However, the intensities of main monoclinic (m) phases with reflections in 2θ = 28° and 31° both slightly decreased with increasing TiO2 content, indicating TiO2 additions into pure ZrO2 still have an effect on the phase transformation.Figure 1
XRD patterns of the microwave sintered ZrO2 samples with addition of 0, 1, 3, and 5 wt% TiO2 contents.


### 3.2. Microstructure

Under the microwave sintering temperature of 1300°C and the holding time of 1 hour, the linear shrinkage of the microwave sintered ZrO2 samples with different additions was approximately 16%. With the density measurement, the relative densities of microwave sintered ZrO2 ceramics with TiO2 addition achieved around 88% to 90%. Figure 2 shows SEM results of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents at 1300°C in 1 h. It is clearly observed that the grain sizes increased with increasing TiO2 contents. The grain sizes were 420 nm, 650 nm, 890 nm, and 1060 nm with the addition of TiO2 content with 0, 1, 3, and 5 wt%, respectively. The result indicated that the addition of TiO2 in ZrO2 ceramic could improve the grain growth and enhance the microwave sintering. Since the TiO2 phase was not detected in the XRD pattern, the TiO2 phase might be too small to be detected and TiO2 addition was embedded around the ZrO2 grain and/or within the ZrO2 grain. Although the sintered samples did not achieve the full densification, it shall be noted that even at such a low temperature and a short holding time the ZrO2 grains were eventually coalesced with each other. At the triple junctions of the ZrO2 grains, some micro pores were present. It is known that the appearance of pores would increase the diffusion distance between ZrO2 grains, thus reducing the driving force for pore shrinkage of the sintered ceramics [6].Figure 2
SEM of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents.
(a)
(b)
(c)
(d)Figure3 shows EDS analysis of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents. The EDS results verified that the content of TiO2 increased actually with increasing TiO2 addition. Although the TiO2 phase was not detected in the XRD pattern, Ti and O elements were detected in the EDS analysis. The presence of TiO2 on the grain and/or grain boundaries effectively improved the grain growth of the ZrO2 grains.Figure 3
EDS analysis of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents.
(a)
(b)
(c)
(d)


### 3.3. Mechanical Properties

Figure4 shows the Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents. Despite the errors associated with the measurement, it is found that the Vickers hardness of the ZrO2 ceramic with addition of 0, 1, 3, and 5 wt% TiO2 contents was 125, 150, 250, and 300 Hv, respectively. The hardness values are low if the sintered samples are designed for dental use, since the sintered samples did not achieve the full densification under such a low temperature and a short holding time. Optical microscope of the ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents was shown in Figure 5. It is clearly observed that, under the same indent load, the lengths of the cross-indentation were decreased with increasing TiO2 contents. Thus, the larger length of the Vickers hardness indicated the shorter length of the cross-indentation. Typically, many factors would affect the Vickers hardness of ceramic materials, including the intrinsic deformability of the ceramic and the extrinsic microstructural features such as existent phases, grain size, crystal orientation, porosity, and boundary constitution [6, 8]. Under the microwave sintering temperature of 1300°C and the holding time of 1 hour, the main phase of monoclinic zirconia and second phase of tetragonal zirconia coexisted in the sintered samples with different TiO2 content, and the amount of the main phase was much larger than that of the second phase, as discussed in Figure 1. However, the grain sizes increased and the microwave sintering enhanced with increasing TiO2 contents. Thus, it is suggested that in this study the hardness of ZrO2 was mainly influenced by the enhanced microwave sintering with TiO2 addition.Figure 4
Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents.Figure 5
Optical microscope of the ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents (the scale bar is 20 μm.).
(a)
(b)
(c)
(d)Figure6 shows further the Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents under different sintering temperatures. It is actually found that, with increasing the sintering temperature from 1150°C to 1300°C, the Vickers hardness of the ZrO2 ceramics increased in spite of TiO2 contents. The increase was not obvious from 1150°C to 1200°C and then enhanced after 1200°C. Moreover, for the same sintering temperature, the Vickers hardness of ZrO2 was enlarged by doping with TiO2 in spite of the content. Namely, TiO2 addition into the ZrO2 ceramics actually improved the Vickers hardness of the ZrO2 ceramics under the microwave sintering. Figure 7 shows the optical microscope of the ZrO2 ceramics with addition of 5 wt% TiO2 contents sintered at (a) 1150°C, (b) 1200°C, (c) 1250°C, and (d) 1300°C. It is verified that, with higher sintering temperature, the length of the cross-indentation decreased due to the increase of the Vickers hardness. From the above results, it is summarized that TiO2 content plays an important role in the crystallite phases, microstructures, and mechanical properties of microwave sintered ZrO2 ceramics with TiO2 addition. In the future, the sintering temperature shall be high and/or the sintering holding time shall be also longer to achieve the full densification and enough Vickers hardness of the ZrO2 ceramics for the dental use.Figure 6
Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents under different sintering temperatures.Figure 7
Optical microscope of the ZrO2 ceramics with addition of 5 wt% TiO2 contents sintered at (a) 1150°C, (b) 1200°C, (c) 1250°C, and (d) 1300°C (the scale bar is 20 μm.).
(a)
(b)
(c)
(d)


## 3.1. XRD Analysis

Figure1 shows the XRD patterns of the microwave sintered ZrO2 samples with addition of 0, 1, 3, and 5 wt% TiO2 contents at 1300°C for 1 h. The main diffraction patterns of the tetragonal phase are around 2θ = 30°, 51°, and 60°. In these patterns, it was found that the diffraction patterns with reflections in 2θ = 28° and 31° were related to the main phase of monoclinic zirconia and low diffraction intensity with reflection in 2θ = 50.36° was related to second phase of tetragonal zirconia in the sintered samples for different TiO2 content [2, 6]. As reported in many researches, low-temperature cubic and tetragonal phases are meta-stable and would be converted into the monoclinic phase during cooling. Typically, the addition of stabilizers, such as Y2O3, CeO2, CaO, and MgO, to pure ZrO2 can provide multiphases which coexisted in a material, known as Partially Stabilized Zirconia (PSZ) [1, 2]. In this study, the addition of TiO2 seemed not to prevent t → m phase transformation during cooling. The result might be caused from the sintering temperature of 1300°C and the holding time of 1 hour which were much lower than conventional sintering temperature and time for the stabilizer [8]. However, the intensities of main monoclinic (m) phases with reflections in 2θ = 28° and 31° both slightly decreased with increasing TiO2 content, indicating TiO2 additions into pure ZrO2 still have an effect on the phase transformation.Figure 1
XRD patterns of the microwave sintered ZrO2 samples with addition of 0, 1, 3, and 5 wt% TiO2 contents.


## 3.2. Microstructure

Under the microwave sintering temperature of 1300°C and the holding time of 1 hour, the linear shrinkage of the microwave sintered ZrO2 samples with different additions was approximately 16%. With the density measurement, the relative densities of microwave sintered ZrO2 ceramics with TiO2 addition achieved around 88% to 90%. Figure 2 shows SEM results of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents at 1300°C in 1 h. It is clearly observed that the grain sizes increased with increasing TiO2 contents. The grain sizes were 420 nm, 650 nm, 890 nm, and 1060 nm with the addition of TiO2 content with 0, 1, 3, and 5 wt%, respectively. The result indicated that the addition of TiO2 in ZrO2 ceramic could improve the grain growth and enhance the microwave sintering. Since the TiO2 phase was not detected in the XRD pattern, the TiO2 phase might be too small to be detected and TiO2 addition was embedded around the ZrO2 grain and/or within the ZrO2 grain. Although the sintered samples did not achieve the full densification, it shall be noted that even at such a low temperature and a short holding time the ZrO2 grains were eventually coalesced with each other. At the triple junctions of the ZrO2 grains, some micro pores were present. It is known that the appearance of pores would increase the diffusion distance between ZrO2 grains, thus reducing the driving force for pore shrinkage of the sintered ceramics [6].Figure 2
SEM of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents.
(a)
(b)
(c)
(d)Figure3 shows EDS analysis of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents. The EDS results verified that the content of TiO2 increased actually with increasing TiO2 addition. Although the TiO2 phase was not detected in the XRD pattern, Ti and O elements were detected in the EDS analysis. The presence of TiO2 on the grain and/or grain boundaries effectively improved the grain growth of the ZrO2 grains.Figure 3
EDS analysis of the microwave sintered ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents.
(a)
(b)
(c)
(d)


## 3.3. Mechanical Properties

Figure4 shows the Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents. Despite the errors associated with the measurement, it is found that the Vickers hardness of the ZrO2 ceramic with addition of 0, 1, 3, and 5 wt% TiO2 contents was 125, 150, 250, and 300 Hv, respectively. The hardness values are low if the sintered samples are designed for dental use, since the sintered samples did not achieve the full densification under such a low temperature and a short holding time. Optical microscope of the ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents was shown in Figure 5. It is clearly observed that, under the same indent load, the lengths of the cross-indentation were decreased with increasing TiO2 contents. Thus, the larger length of the Vickers hardness indicated the shorter length of the cross-indentation. Typically, many factors would affect the Vickers hardness of ceramic materials, including the intrinsic deformability of the ceramic and the extrinsic microstructural features such as existent phases, grain size, crystal orientation, porosity, and boundary constitution [6, 8]. Under the microwave sintering temperature of 1300°C and the holding time of 1 hour, the main phase of monoclinic zirconia and second phase of tetragonal zirconia coexisted in the sintered samples with different TiO2 content, and the amount of the main phase was much larger than that of the second phase, as discussed in Figure 1. However, the grain sizes increased and the microwave sintering enhanced with increasing TiO2 contents. Thus, it is suggested that in this study the hardness of ZrO2 was mainly influenced by the enhanced microwave sintering with TiO2 addition.Figure 4
Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents.Figure 5
Optical microscope of the ZrO2 ceramics with addition of (a) 0, (b) 1, (c) 3, and (d) 5 wt% TiO2 contents (the scale bar is 20 μm.).
(a)
(b)
(c)
(d)Figure6 shows further the Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents under different sintering temperatures. It is actually found that, with increasing the sintering temperature from 1150°C to 1300°C, the Vickers hardness of the ZrO2 ceramics increased in spite of TiO2 contents. The increase was not obvious from 1150°C to 1200°C and then enhanced after 1200°C. Moreover, for the same sintering temperature, the Vickers hardness of ZrO2 was enlarged by doping with TiO2 in spite of the content. Namely, TiO2 addition into the ZrO2 ceramics actually improved the Vickers hardness of the ZrO2 ceramics under the microwave sintering. Figure 7 shows the optical microscope of the ZrO2 ceramics with addition of 5 wt% TiO2 contents sintered at (a) 1150°C, (b) 1200°C, (c) 1250°C, and (d) 1300°C. It is verified that, with higher sintering temperature, the length of the cross-indentation decreased due to the increase of the Vickers hardness. From the above results, it is summarized that TiO2 content plays an important role in the crystallite phases, microstructures, and mechanical properties of microwave sintered ZrO2 ceramics with TiO2 addition. In the future, the sintering temperature shall be high and/or the sintering holding time shall be also longer to achieve the full densification and enough Vickers hardness of the ZrO2 ceramics for the dental use.Figure 6
Vickers hardness of the ZrO2 ceramics with addition of 0, 1, 3, and 5 wt% TiO2 contents under different sintering temperatures.Figure 7
Optical microscope of the ZrO2 ceramics with addition of 5 wt% TiO2 contents sintered at (a) 1150°C, (b) 1200°C, (c) 1250°C, and (d) 1300°C (the scale bar is 20 μm.).
(a)
(b)
(c)
(d)


## 4. Conclusions

This paper investigated the effect of contents of TiO2 addition on microstructure and mechanical properties of microwave sintered zirconia bioceramics for the dental use. The zirconia ceramics with 1, 3, and 5 wt% TiO2 addition were sintered using the microwave energy at the sintering temperature of 1300°C. For different TiO2 content, the main phase was the monoclinic zirconia (m-ZrO2) phase and second phase was tetragonal zirconia (t-ZrO2) phase. For all sintered samples, the grain growth was nearly completed. The grain sizes increased with increasing TiO2 contents, indicating that TiO2 addition effectively improved the grain growth of the ZrO2 grains. The Vickers hardness increased with TiO2 contents in the range from 125 to 300 Hv. Moreover, the Vickers hardness of ZrO2 was enlarged by doping with TiO2 in spite of the content under the same sintering temperature from 1150°C to 1300°C. Based on the study results, the microwave sintering is verified to be used to sinter ZrO2 bioceramics with a low sintering temperature, and TiO2 addition plays an important role in the crystallite phases, microstructures, and mechanical properties of microwave sintered ZrO2 ceramics.



---