# Biosynthesis of Anisotropic Silver Nanoparticles byBhargavaea indica and Their Synergistic Effect with Antibiotics against Pathogenic Microorganisms

Authors: Priyanka Singh; Yeon Ju Kim; Hina Singh; Ramya Mathiyalagan; Chao Wang; Deok Chun Yang
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

The strainBhargavaea indica DC1 isolated from four-year-old P. ginseng rhizospheric soil was used to perform rapid and extracellular biosynthesis of anisotropic silver nanoparticles. The ultraviolet-visible (UV-vis) spectra of the reaction mixture containing silver nanoparticles showed a peak at 460 nm, corresponding to the surface plasmon absorbance of silver nanoparticles. Field-emission transmission electron microscopy (FE-TEM) structural characterization revealed the nanobar, pentagon, spherical, icosahedron, hexagonal, truncated triangle, and triangular nanoparticles, with the size range from 30 to 100 nm. The energy-dispersive X-ray (EDX) analysis and elemental mapping results also confirmed that the silver was the predominant component of isolated nanoparticles. The X-ray diffraction (XRD) results correspond to the purity of silver nanoparticles and dynamic light scattering (DLS) result indicated that the average diameter of particles was 111.6 nm. In addition, enhancement in antimicrobial activity of commercial antibiotics was observed against various pathogenic microorganisms such as Vibrio parahaemolyticus, Salmonella enterica, Staphylococcus aureus, Bacillus anthracis, Bacillus cereus, Escherichia coli, and Candida albicans.


---

## Body

## 1. Introduction

Nanomaterials have been studied intensively and have received considerable attention in various scientific fields due to unique properties including ultra-small size, high surface-area-to-mass ratio, and high reactivity [1]. Chemical and physical methods for the synthesis of metal nanoparticles are well known, but the methodologies are expensive and not environmentally friendly, thus limiting the applications of metal nanoparticles in biological and medical platforms [2]. To overcome the limitation of physiochemical methodologies, the simple, low-cost, and eco-friendly technologies are needed whereby these nanoparticles can be synthesized while avoiding the use of toxic chemicals and solvents. The green synthesis is a feasible alternative, and various biological species have been well studied for this purpose, including bacteria, yeast, fungi, and plant extracts [2–6]. Such research has led to new product developments and applications of biological species in different fields [7].Among the many metal nanoparticles, silver nanoparticles are one of the most studied and prominent nanoproducts. Silver nanoparticles are well known for their inhibitory and bactericidal effects and have a broad range of applications in many fields [8, 9]. The reduction of Ag+ ions by some biological species and products causes the synthesis of silver nanoparticles with enhancing properties due to an increase in the surface plasmon resonance and large effective scattering cross section of individual nanoparticles [10]. Moreover, the activity of metal nanoparticles at nanostructure level can be easily tuned by varying specific characteristics [11]. These unique properties of nanoparticles make them a superior and indispensable choice in many areas of biological activity [12].Anisotropic particles provide greater versatility and options in many cases and applications. Studies suggest that shape of particles is one of the important factors, as most of the intrinsic properties depend on it. Nonspherical nanoparticles such as pentagons, cubes, nanospheres, icosahedrons, hexagons, truncated triangles, triangular prisms, and other more exotic structures of metal nanoparticles exhibit unique and fine-tuned properties which strongly differ and are more pronounced from those of spherical nanoparticles. Their unusual physiochemical property makes them ideal structures and valuable choice to be used for biomedical labelling, optical sensing and imaging, photonics, electronics, catalysis, and electronic devices among others. Furthermore, anisotropic particles provide templates for further synthesis of novel nanomaterials [9, 14]. Anisotropic silver and gold nanoparticles synthesized by chemical, physical, and biological system have been studied and demonstrated for their importance and applications in medical field [15–17].The antibiotic resistance mechanism in microorganisms has become a major concern and has received considerable attention in the medical field [18]. Silver nanoparticles can play a major role in this area, as they have been found to be active against many multidrug resistant pathogenic microorganisms [19] and in addition, most of the microorganisms are less likely to develop defense mechanisms against metals as compared to antibiotics. Thus, here we report the biosynthesis of anisotropic silver nanoparticles by bacterial strain isolated from four-year-oldPanax ginseng rhizospheric soil.P. ginseng is a slow-growing, perennial, and herbal medicinal plant. The rhizospheric soil microflora of theP. ginseng have been well studied and explored for various applications such as the bioconversion of ginsenosides [20], plant growth promoting activity [21], and antimicrobial activity [22]. In the present study, a bacterial strain isolated fromP. ginseng rhizospheric soil is demonstrated to be useful for an application in the field of nanotechnology, that is, for the synthesis of anisotropic silver nanoparticles. The biosynthesised anisotropic silver nanoparticles were characterized by UV-vis, FE-TEM, EDX, elemental mapping, XRD, and DLS. In addition, nanoparticles were tested for their antimicrobial properties against pathogenic microorganisms includingBacillus anthracis,Vibrio parahaemolyticus,Salmonella enterica,Staphylococcus aureus,Escherichia coli,Bacillus cereus, andCandida albicans. Furthermore, the silver nanoparticles have been tested in combination with commercial antibiotics including lincomycin, oleandomycin, novobiocin, vancomycin, penicillin G, rifampicin, and cycloheximide, for their ability to enhance the antibiotics’ antimicrobial effects against pathogenic microorganisms.


## 2. Experimental

### 2.1. Media, Chemicals, and Microorganism

All media used were purchased from Difco, MB cell, Seoul, Korea. Analytical-grade silver nitrate (AgNO3) and cycloheximide were purchased from Sigma-Aldrich Chemicals, USA. All antibiotics used were purchased from Oxoid Ltd., England: vancomycin (VA30) 30 μg/disk, rifampicin (RD5) 5 μg/disk, oleandomycin (OL15) 15 μg/disk, penicillin G (P10) 10 μg/disk, novobiocin (NV30) 30 μg/disk, and lincomycin (MY15) 15 μg/disk.The pathogenic bacterial strains usedBacillus anthracis [NCTC 10340],Vibrio parahaemolyticus [ATCC 33844],Salmonella enterica [ATCC 13076],Staphylococcus aureus [ATCC 6538],Escherichia coli [ATCC 10798],Bacillus cereus [ATCC 14579], andCandida albicans [KACC 30062]. The bacterial strains were cultured on nutrient agar media at 37°C and preserved at −70°C in glycerol stock vials for further study.C. albicans was cultured on Sabouraud dextrose agar at 28°C and preserved at −70°C in glucose yeast peptone broth (GYP) glycerol stocks vials.


### 2.2. Isolation of Bacteria

A bacterial strain DC1 was isolated from four-year-oldP. ginseng rhizospheric soil (Sodang, Republic of Korea) on tryptic soy agar (TSA) and incubated at 30°C for 24 h. Its genomic DNA was extracted using a commercial genomic DNA extraction kit (Core Bio System). The 16S rRNA gene was amplified from the chromosomal DNA of the isolated strain using the universal bacterial primer set 27F, 518F, 800R, and 1512R [23, 24]. The purified PCR products were sequenced by Genotech (Daejeon, Korea). The 16S rRNA gene sequences of related taxa were obtained from the GenBank database and EzTaxon-e server [25].


### 2.3. Extracellular Synthesis of Silver Nanoparticles

The biological synthesis of silver nanoparticles was carried out as reported [11] with slight modification. Briefly, the bacteria were grown in tryptic soy broth (TSB) and kept in incubation for 24 h in a shaker held at 37°C and 120 rpm. The culture was then centrifuged at 8000 rpm for 5 min and the supernatant was used for the synthesis of silver nanoparticles. AgNO3 was added to the culture supernatant to reach the concentration of 1 mM, and this reaction mixture was incubated in the orbital shaker at 200 rpm and 25°C. The extracellular synthesis of silver nanoparticles was monitored by visual inspection for a change in the color of the culture medium. After incubation was complete, the reaction mixture was first centrifuged at 2000 rpm for 5 min to remove any medium components, and then the biosynthesised silver nanoparticles were collected by high-speed centrifugation at 16000 rpm for 20 min. The product obtained was washed several times by centrifugation and redispersion in water to remove the unconverted silver ions and any medium components. Finally, the silver nanoparticles were collected in the form of a pellet and used for characterization.


### 2.4. Characterization of Silver Nanoparticles

UV-vis, FE-TEM, EDX, elemental mapping (quantitation method: Cliff-Lorimer ratio), and DLS were used to characterize the size, shape, composition, and other properties of the silver nanoparticles. The bioreduction was monitored by using a UV-vis spectrophotometer (Ultrospec 2100 pro); this was carried out by scanning the absorbance spectra of the reaction mixture over the wavelength range of 300–700 nm. TEM, EDX, and elemental mapping were performed by using a FE-TEM (JEM-2100F, JEOL) operated at 200 kV. Samples for FE-TEM, EDX, and elemental mapping were prepared by dropping the unstained silver nanoparticles pellet solution onto a carbon-coated copper grid and drying in an oven at 60°C. FE-TEM was used for structural characterization of nanoparticles. EDX and elemental mapping were used to study the distribution of elements. The X-ray diffraction (XRD) analyses were performed on X-ray diffractometer, D8 Advance, Bruker, Germany, operated at 40 kv, 40 mA, with CuKα radiation, at a scanning rate of 6°/min, step size 0.02, over the 2θ range of 20–80°. The silver nanoparticles have been collected by centrifugation and washing several times with sterile water. Then, the particles were finally recovered by air drying and obtained in powder form.DLS (particles size analyzer, Photal, Otsuka Electronics, Japan) was used to monitor size distribution profile of biologically synthesized silver nanoparticles. The hydrodynamic diameters and polydispersity index (PDI) were analysed at 25°C. As a reference dispersive medium pure water with refractive index 1.3328, viscosity 0.8878, and dielectric constant 78.3 was used.The stability of silver nanoparticles was observed by keeping the anisotropic silver nanoparticles reaction mixture for different time interval at room temperature. In addition, the effect of change in pH on the stability of the silver nanoparticles was studied. The sodium hydroxide solution was added in the range of 4–10 pH and then the solution has been scanned by UV-vis spectrophotometer to observe the absorbance.


### 2.5. Analysis of Antimicrobial Activity of Silver Nanoparticles

Antimicrobial activity of the silver nanoparticles against pathogenic microorganisms,S. aureus,B. anthracis,V. parahaemolyticus,S. enterica,E. coli,B. cereus, andC. albicans, was tested by the well diffusion method, carried out using Muller-Hinton agar (MHA) plates. An overnight log-phase culture of each strain was spread evenly on an MHA plate by using a glass spreader. Wells were made on the MHA plates by using a gel puncture. 50 μL of the biosynthesised silver nanoparticles reaction mixture was added into each of four wells and the plates were incubated at 37°C for 24 h.Simultaneously, the synergistic effects of different commercial antibiotics with silver nanoparticles were also tested by the disk diffusion method. Similarly, an overnight log-phase culture of each strain was spread evenly on an MHA plate. Then, antibiotic disk of each of the commercial antibiotics was placed on the plate, and 30μL of a 100 ppm solution of silver nanoparticles was added over each disk (10 μL, 3 times). Antibiotic disks without silver nanoparticles were used as negative control. The plates were allowed to dry and then incubated at 37°C for 24 h. After incubation, the susceptibility pattern of the test organisms was determined by measuring the diameter of the zone of inhibition for both the well diffusion and disk diffusion methods. Similarly, cycloheximide antimicrobial activity againstC. albicans was evaluated and compared with addition of silver nanoparticles with same concentration.


## 2.1. Media, Chemicals, and Microorganism

All media used were purchased from Difco, MB cell, Seoul, Korea. Analytical-grade silver nitrate (AgNO3) and cycloheximide were purchased from Sigma-Aldrich Chemicals, USA. All antibiotics used were purchased from Oxoid Ltd., England: vancomycin (VA30) 30 μg/disk, rifampicin (RD5) 5 μg/disk, oleandomycin (OL15) 15 μg/disk, penicillin G (P10) 10 μg/disk, novobiocin (NV30) 30 μg/disk, and lincomycin (MY15) 15 μg/disk.The pathogenic bacterial strains usedBacillus anthracis [NCTC 10340],Vibrio parahaemolyticus [ATCC 33844],Salmonella enterica [ATCC 13076],Staphylococcus aureus [ATCC 6538],Escherichia coli [ATCC 10798],Bacillus cereus [ATCC 14579], andCandida albicans [KACC 30062]. The bacterial strains were cultured on nutrient agar media at 37°C and preserved at −70°C in glycerol stock vials for further study.C. albicans was cultured on Sabouraud dextrose agar at 28°C and preserved at −70°C in glucose yeast peptone broth (GYP) glycerol stocks vials.


## 2.2. Isolation of Bacteria

A bacterial strain DC1 was isolated from four-year-oldP. ginseng rhizospheric soil (Sodang, Republic of Korea) on tryptic soy agar (TSA) and incubated at 30°C for 24 h. Its genomic DNA was extracted using a commercial genomic DNA extraction kit (Core Bio System). The 16S rRNA gene was amplified from the chromosomal DNA of the isolated strain using the universal bacterial primer set 27F, 518F, 800R, and 1512R [23, 24]. The purified PCR products were sequenced by Genotech (Daejeon, Korea). The 16S rRNA gene sequences of related taxa were obtained from the GenBank database and EzTaxon-e server [25].


## 2.3. Extracellular Synthesis of Silver Nanoparticles

The biological synthesis of silver nanoparticles was carried out as reported [11] with slight modification. Briefly, the bacteria were grown in tryptic soy broth (TSB) and kept in incubation for 24 h in a shaker held at 37°C and 120 rpm. The culture was then centrifuged at 8000 rpm for 5 min and the supernatant was used for the synthesis of silver nanoparticles. AgNO3 was added to the culture supernatant to reach the concentration of 1 mM, and this reaction mixture was incubated in the orbital shaker at 200 rpm and 25°C. The extracellular synthesis of silver nanoparticles was monitored by visual inspection for a change in the color of the culture medium. After incubation was complete, the reaction mixture was first centrifuged at 2000 rpm for 5 min to remove any medium components, and then the biosynthesised silver nanoparticles were collected by high-speed centrifugation at 16000 rpm for 20 min. The product obtained was washed several times by centrifugation and redispersion in water to remove the unconverted silver ions and any medium components. Finally, the silver nanoparticles were collected in the form of a pellet and used for characterization.


## 2.4. Characterization of Silver Nanoparticles

UV-vis, FE-TEM, EDX, elemental mapping (quantitation method: Cliff-Lorimer ratio), and DLS were used to characterize the size, shape, composition, and other properties of the silver nanoparticles. The bioreduction was monitored by using a UV-vis spectrophotometer (Ultrospec 2100 pro); this was carried out by scanning the absorbance spectra of the reaction mixture over the wavelength range of 300–700 nm. TEM, EDX, and elemental mapping were performed by using a FE-TEM (JEM-2100F, JEOL) operated at 200 kV. Samples for FE-TEM, EDX, and elemental mapping were prepared by dropping the unstained silver nanoparticles pellet solution onto a carbon-coated copper grid and drying in an oven at 60°C. FE-TEM was used for structural characterization of nanoparticles. EDX and elemental mapping were used to study the distribution of elements. The X-ray diffraction (XRD) analyses were performed on X-ray diffractometer, D8 Advance, Bruker, Germany, operated at 40 kv, 40 mA, with CuKα radiation, at a scanning rate of 6°/min, step size 0.02, over the 2θ range of 20–80°. The silver nanoparticles have been collected by centrifugation and washing several times with sterile water. Then, the particles were finally recovered by air drying and obtained in powder form.DLS (particles size analyzer, Photal, Otsuka Electronics, Japan) was used to monitor size distribution profile of biologically synthesized silver nanoparticles. The hydrodynamic diameters and polydispersity index (PDI) were analysed at 25°C. As a reference dispersive medium pure water with refractive index 1.3328, viscosity 0.8878, and dielectric constant 78.3 was used.The stability of silver nanoparticles was observed by keeping the anisotropic silver nanoparticles reaction mixture for different time interval at room temperature. In addition, the effect of change in pH on the stability of the silver nanoparticles was studied. The sodium hydroxide solution was added in the range of 4–10 pH and then the solution has been scanned by UV-vis spectrophotometer to observe the absorbance.


## 2.5. Analysis of Antimicrobial Activity of Silver Nanoparticles

Antimicrobial activity of the silver nanoparticles against pathogenic microorganisms,S. aureus,B. anthracis,V. parahaemolyticus,S. enterica,E. coli,B. cereus, andC. albicans, was tested by the well diffusion method, carried out using Muller-Hinton agar (MHA) plates. An overnight log-phase culture of each strain was spread evenly on an MHA plate by using a glass spreader. Wells were made on the MHA plates by using a gel puncture. 50 μL of the biosynthesised silver nanoparticles reaction mixture was added into each of four wells and the plates were incubated at 37°C for 24 h.Simultaneously, the synergistic effects of different commercial antibiotics with silver nanoparticles were also tested by the disk diffusion method. Similarly, an overnight log-phase culture of each strain was spread evenly on an MHA plate. Then, antibiotic disk of each of the commercial antibiotics was placed on the plate, and 30μL of a 100 ppm solution of silver nanoparticles was added over each disk (10 μL, 3 times). Antibiotic disks without silver nanoparticles were used as negative control. The plates were allowed to dry and then incubated at 37°C for 24 h. After incubation, the susceptibility pattern of the test organisms was determined by measuring the diameter of the zone of inhibition for both the well diffusion and disk diffusion methods. Similarly, cycloheximide antimicrobial activity againstC. albicans was evaluated and compared with addition of silver nanoparticles with same concentration.


## 3. Results and Discussion

### 3.1. Isolation and Identification of Bacteria

The bacterial strain DC1 used herein to carry out the extracellular biosynthesis of silver nanoparticles was isolated from four-year-oldP. ginseng rhizospheric soil and showed 99.79% similarity withBhargavaea indica [26]. The strainBhargavaea indica DC1 16S rRNA sequence has been submitted to NCBI with accession number KM819013. The strain has been deposited to KCTC culture collection (KCTC 33595).


### 3.2. Synthesis and Characterization of Silver Nanoparticles

In this study, silver nanoparticles were successfully synthesised extracellularly in the culture supernatant ofB. indica DC1.The first indication of silver nanoparticles synthesis was that, upon addition of 1 mM silver nitrate into the flask containing a 24 h culture supernatant of the strain, the medium gradually turned brown, whereas no color change was observed in the control without bacteria. This brown color could be due to the excitation of surface plasmon vibrations, which would arise from the formation of silver nanoparticles in the reaction mixture [11]. Interestingly, the culture supernatant incubated with 1 mM silver nitrate mediated the biosynthesis of silver nanoparticles within 48 h. The 1 mM concentration for the synthesis of silver nanoparticles was selected based on the silver nitrate tolerating capacity of the isolateB. indica DC1. The strain showed optimum growth at 1 mM concentration. Moreover, the concentration of precursor (0.1–1 mM) for the synthesis of nanoparticles does not show any effect on the end product of reaction; thus the shape and size of nanoparticles were not affected by the precursor concentration ranging.UV-vis is the most established method for structural characterization of metal nanoparticles. The reduction of silver ions during exposure to the supernatant of the strain DC1 was easily monitored by UV-vis. After the incubation period, the reaction mixture was scanned in the range of 300–700 nm, showing a major absorbance peak at 460 nm (Figure1(a)). The broad peak is due to the anisotropic nature of the particles. It has been reported that the band in this region corresponds to the surface plasmon resonance of silver nanoparticles [27]. Thus, the reaction mixture indicates the formation of silver nanoparticles. The nanoparticles synthesize extracellularly, avoiding the downstream processing needed for intracellular synthesis.Figure 1
UV-vis spectra of culture supernatant ofBhargavaea indica DC1 treated with (1 mM) AgNO3 (a). Transmission electron micrograph of anisotropic silver nanoparticles synthesised byBhargavaea indica DC1, 100 and 200 nm (b).
(a)
(b)
(c)Various researchers have reported evidence of the extracellular biosynthesis of silver nanoparticles, including TEM structural characterizations [28]. The anisotropic silver nanoparticles synthesised were successfully characterized by FE-TEM and revealed that the particles ranged in size from 30 to 100 nm and were of various shapes including nanobar, pentagon, spherical, icosahedron, hexagonal, truncated triangle, and triangular shapes (Figure 1(b)). Although the monodispersity is the main issue associated with the nanoparticles synthesis, the biosynthesised anisotropic silver nanoparticles are of great advantage in biological platforms, since the silver nanoparticles undergo shape-dependent interactions with microorganisms [9]. Reports suggest that the biosynthesised silver nanoparticles of different shapes can be separated by centrifugation, as the nanoparticles show shape-dependent sedimentation behaviour [29]. The biological synthesis of anisotropic gold and silver nanoparticles byAspergillus niger has been reported previously. The syntheses of anisotropic silver nanoparticles byMorganella psychrotolerans [30] and anisotropic gold nanoparticles by the fungal strainRhizopus oryzae [31] have been studied. To our knowledge, this is the first report of the ability ofB. indica DC1 to synthesise silver nanoparticles of various shapes and sizes. The exact mechanism behind the synthesis remains to be elucidated, but based on reports, the enzyme and proteins synthesised extracellularly by bacterial strain in the reaction mixture help in reducing the silver nitrate to silver nanoparticles. Moreover, the particles synthesised without any additional stabilizing and capping agent thus eliminating the main step of chemical synthesis and overcome the limitations. The cell-free supernatant containing extracellular enzymes and proteins functions as a reducing, shape-directing, and stabilizing agent [2, 31].The purity of the biosynthesised silver nanoparticles was examined by EDX (Figure2(a)); the EDX spectrum displayed an optical absorption band peak at 3 keV, which is the characteristic peak of nanosized metallic silver, corresponding to surface plasmon resonance [32]. Carbon and copper signals originating in the low-energy part of the spectrum arose from the use of the carbon-coated copper TEM grid. Similar results have been observed in the study of biosynthesised silver nanoparticles byStreptomyces hygroscopicus [33] and mangroveStreptomyces sp. BDUKAS10 [6].Figure 2
EDX spectra of the whole scan area showing major peak of anisotropic silver nanoparticles at 3 keV (a) and TEM micrograph of anisotropic silver nanoparticles pellet solution and silver nanoparticles; 55.95% (b), respectively.
(a)
(b)
(c)Figure2(b) shows an elemental mapping result for the biosynthesised silver nanoparticles, showing the relative locations of elements in the TEM cross section. Results clearly demonstrate that the maximum deposition corresponds to silver nanoparticles, 55.95%. Other elements observed included carbon, 12.65%, and copper, 28.68%; these two elements were observed due to the carbon-coated copper grid used for TEM structural analysis. Chlorine was also observed in a very low amount, 2.71%, in the cross sections of the nanoparticles themselves. The distribution of silver element was clearly visible in elemental maps and was the predominant element. Thus, the EDX spectrum and elemental mapping gave confirmation that the nanoparticles consisted of silver only [6]. Figure 3 showed the X-ray diffraction pattern of silver nanoparticles and exhibited intense peaks in the whole spectrum of 2θ value ranging from 20 to 80 and this pattern was similar to Bragg’s reflection of silver nanocrystals.Figure 3
X-ray diffraction patterns of anisotropic silver nanoparticles obtained byBhargavaea indica DC1.The DLS measurements of number, intensity, and volume distribution of nanoparticles show the size range from 50 to 150 nm with an average diameter of 111 nm and PDI 0.233 (Figures4(a)–4(c)) which is different from the size measured by TEM, that is, 30–100 nm. Reports suggest that the size difference between the particles size analyses by DLS and TEM measurement has difference due to the fact that TEM visualizes the metallic core of the particles, whereas DLS measures the hydrodynamic diameter of the particles [34]. Thus,B. indica DC1 was demonstrated to be suitable for the simple, green, nonhazardous, economical, and eco-friendly synthesis of antimicrobial anisotropic silver nanoparticles without any additional reducing and stabilizing agent.Figure 4
Particles size distribution of anisotropic silver nanoparticles according to number (a), intensity (b), and volume (c), respectively.
(a)
(b)
(c)Based on the incubation of reaction mixture for different time interval at room temperature, the stability of the nanoparticles was observed and was found that there was no observable variation in the UV-vis spectrum, which directed the stable nature of the anisotropic silver nanoparticles. In addition, the silver nanoparticles solution was observed before and after the addition of sodium hydroxide. In results, no major change in the wavelength was observed, which further confirmed the stability.


### 3.3. Antimicrobial Activity of Silver Nanoparticles against Test Microorganisms

The biosynthesised silver nanoparticles displayed antimicrobial activity against a range of pathogenic microorganisms such asC. albicans,V. parahaemolyticus,S. aureus,B. anthracis,B. cereus,S. enterica, andE. coli (Figure 5). The mean diameter of the zone of inhibition of all the four wells was determined for each microorganism, showing that the silver nanoparticles had the greatest antimicrobial activity againstC. albicans, followed byV. parahaemolyticus,S. aureus,B. anthracis,B. cereus,S. enterica, and thenE. coli. The study has been done in duplicate and average results were interpreted in Table 1. The results clearly indicate that silver nanoparticles exert antimicrobial activity against tested microorganisms. Many studies have reported the antimicrobial activity of silver nanoparticles against pathogenic microorganisms [7, 11]. However, the mechanism of the metal nanoparticles’ inhibitory action is still not clearly understood. There are reports suggesting that (i) the electrostatic attraction between the negatively charged bacterial cell and the positively charged nanoparticles leads to accumulation of nanoparticles on the bacterial membrane, resulting in an increase in cell permeability, (ii) the association of silver with oxygen and its reaction with sulfhydryl (S-H) groups on the cell wall forms R-S-S-R bonds, thereby blocking respiration, (iii) the silver nanoparticles interact with bacterial proteins, which finally leads to cell death, and (iv) the nanoparticles release silver ion which provide additional bactericidal effect [35].Table 1
Diameter of zone of inhibition (mm) of reaction mixture (50μL) containing anisotropic silver nanoparticles against pathogenic microorganisms.
Number
Pathogenic microorganism
Zone of inhibition (mm)†
1
Candida albicans[KACC 30062]
23 ± 0.5
2
Vibrio parahaemolyticus[ATCC 33844]
22 ± 1
3
Staphylococcus aureus[ATCC 6538]
18 ± 0.8
4
Bacillus anthracis[NCTC 10340]
16 ± 0.6
5
Bacillus cereus[ATCC 14579]
15 ± 0.4
6
Salmonella enterica[ATCC 13076]
14 ± 1
7
Escherichia coli[ATCC 10798]
10 ± 1
†Mean diameter of four wells, 50 μL reaction mixture containing anisotropic silver nanoparticles.Figure 5
Zones of inhibition of 50μL of reaction mixture containing anisotropic silver nanoparticles against pathogenic strains includingCandida albicans,Vibrio parahaemolyticus,Staphylococcus aureus,Bacillus anthracis,Bacillus cereus,Salmonella enterica, andEscherichia coli, respectively.The combination of silver nanoparticles with different commercial antibiotics was evaluated to determine its activity against six pathogenic bacteria using the disk diffusion method. Figure6(a) represents the antimicrobial activity of partially purified silver nanoparticles and standard antibiotics antimicrobial activity againstS. enterica,E. coli,V. parahaemolyticus,B. anthracis,B. cereus, andS. aureus, respectively. The synergistic effect of antibiotics (lincomycin, oleandomycin, novobiocin, vancomycin, penicillin G, and rifampicin) with biosynthesised silver nanoparticles increased the susceptibility of the tested microorganisms (Figure 6(b)). The disk diffusion tests clearly indicated that the strains ofS. enterica,E. coli, andV. parahaemolyticuswere completely resistant to the antibiotics, whereas the bacterial strains showed sensitivity to the disks when anisotropic silver nanoparticle solution was added and results in the formation of a zone of inhibition forS. enterica,E. coli, andV. parahaemolyticus. The average increase in sensitivity patter of antibiotics was calculated by average increase in fold area [35]. The average increase in fold area of the antibiotics against antibiotics resistant microorganisms was greatest for novobiocin, followed by rifampicin, lincomycin, and oleandomycin and then vancomycin and penicillin G. Similar results regarding increase in fold area have been observed against multidrug resistantE. coli [16]. The other pathogenic stains showed susceptibility to antibiotics disks alone,B. anthracis,B. cereus, andS. aureus,and showed increased susceptibility when the disks were combined with anisotropic silver nanoparticle solution, observed as increases in the diameter of the zone of inhibition forB. anthracis,B. cereus, andS. aureus. This clearly indicated the effect of biosynthesised anisotropic silver nanoparticles in enhancing the antimicrobial action of antibiotics. The average increase in fold area against antibiotic sensitive microorganism, when anisotropic silver nanoparticles were added, was greatest for penicillin G, followed by vancomycin, rifampicin, oleandomycin, novobiocin, and lincomycin. In addition, in case of cycloheximide, the similar pattern of action was found againstC. albicans. On the addition of silver nanoparticles with cycloheximide, the activity of cycloheximide increases. The study has been done in duplicate and average results were interpreted in Table 2. The present study shows results similar to those of a line of studies that presented increased efficacies of commercial antibiotics against pathogenic microorganisms [13, 16, 28]. It indicates that biosynthesised anisotropic silver nanoparticles show antimicrobial activity against pathogenic microorganisms. Moreover, the nanoparticles were shown to enhance the effect of commercial antibiotics against multidrug resistant bacteria. Thus, the biosynthesised anisotropic silver nanoparticles are ready for applications in the clinical field against pathogenic microorganisms, although the exact mechanism of their action remains to be elucidated.Table 2
Individual and combined efficacy of commercial antibiotics with biosynthesised anisotropic silver nanoparticles against pathogenic microorganisms.
Pathogenic strain
MY15
MY15 + AgNPs
FA‡
OL15
OL15 + AgNPs
FA‡
NV30
NV30 + AgNPs
FA‡
(a)
(b)
(a)
(b)
(a)
(b)
S. enterica
0†
12 ± 0.5
3
0†
12 ± 0.2
3
0†
14 ± 0.9
4.44
E. coli
0†
13 ± 0.3
3.69
0†
13 ± 0.6
3.69
0†
14 ± 1
4.44
V. parahaemolyticus
0†
15 ± 0.4
5.25
0†
15 ± 0.3
5.25
0†
17 ± 0.6
7.02
Average
3.98
3.98
5.3
B. anthracis
14 ± 0.1
16 ± 0.1
0.31
15 ± 0.4
18 ± 0.2
0.44
19 ± 0.2
22 ± 0.3
0.34
B. cereus
16 ± 0.2
18 ± 0.6
0.26
22 ± 0.3
24 ± 0.5
0.19
22 ± 0.1
25 ± 0.4
0.29
S. aureus
25 ± 0.1
28 ± 0.5
0.25
22 ± 0.2
25 ± 0.7
0.29
30 ± 0.3
34 ± 1
0.28
Average
0.27
0.31
0.30
Pathogenic strain
VA30
VA30 + AgNPs
FA‡
P10
P10  + AgNPs
FA‡
RD5
RD5 + AgNPs
FA‡
(a)
(b)
(a)
(b)
(a)
(b)
S. enterica
0†
12 ± 0.3
3
0†
12 ± 1
3
0†
13 ± 0.5
3.69
E. coli
0†
13 ± 0.4
3.69
0†
13 ± 1.2
3.69
0†
13 ± 0.2
3.69
V. parahaemolyticus
0†
14 ± 0.2
4.44
0†
14 ± 1.5
4.44
0†
15 ± 0.3
5.25
Average
3.71
3.71
4.21
B. anthracis
15 ± 0.5
19 ± 0.7
0.6
0†
15 ± 0.5
5.25
12 ± 0.2
16 ± 0.7
0.78
B. cereus
17 ± 0.2
20 ± 0.6
0.38
8 ± 0.3
16 ± 0.8
3
13 ± 0.3
15 ± 0.4
0.33
S. aureus
16 ± 0.4
20 ± 0.2
0.56
36 ± 0.5
40 ± 0.8
0.23
27 ± 0.4
29 ± 0.6
0.15
Average
0.52
2.83
0.42
Pathogenic strain
CHX
CHX  +  AgNPs
FA‡
C. albicans
0†
13 ± 0.5
3.69
Notes.†In the absence of bacterial growth inhibition zones, the disc’s diameter (6 mm) was used to calculate the fold increases [13].
‡Increase in fold area (FA) = (b2-a2)/a2.
MY15: lincomycin 15μg/disk, OL15: oleandomycin 15 μg/disk, VA30: vancomycin 30 μg/disk,  NV30: novobiocin 30 μg/disk, P10: penicillin G 10 μg/disk, and RD5: rifampicin 5 μg/disk; CHX: cycloheximide, 10 μg/disk; AgNPs: biosynthesised anisotropic silver nanoparticles, 30 μL (100 ppm).Figure 6
Zones of inhibition of partially purified silver nanoparticles pellet solution 30μL (100 ppm) and standard antibiotics as control, againstSalmonella enterica,Escherichia coli,Vibrio parahaemolyticus,Bacillus anthracis,Bacillus cereus, andStaphylococcus aureus, respectively (a). Zones of inhibition of standard antibiotics disks with anisotropic silver nanoparticles againstSalmonella enterica,Escherichia coli,Vibrio parahaemolyticus,Bacillus anthracis,Bacillus cereus,Staphylococcus aureus, andCandida albicans (b), respectively.Note. (1) Lincomycin (MY15) 15 µg/disk, (2) oleandomycin (OL15) 15 µg/disk, (3) novobiocin (NV30) 30 µg/disk, (4) vancomycin (VA30) 30 µg/disk, (5) penicillin G (P10) 10 µg/disk, and (6) rifampicin (RD5) 5 µg/disk; cycloheximide (CHX) 10 µg/disk and anisotropic silver nanoparticles (AgNPs) 30 µL (100 ppm).
(a)
(b)


## 3.1. Isolation and Identification of Bacteria

The bacterial strain DC1 used herein to carry out the extracellular biosynthesis of silver nanoparticles was isolated from four-year-oldP. ginseng rhizospheric soil and showed 99.79% similarity withBhargavaea indica [26]. The strainBhargavaea indica DC1 16S rRNA sequence has been submitted to NCBI with accession number KM819013. The strain has been deposited to KCTC culture collection (KCTC 33595).


## 3.2. Synthesis and Characterization of Silver Nanoparticles

In this study, silver nanoparticles were successfully synthesised extracellularly in the culture supernatant ofB. indica DC1.The first indication of silver nanoparticles synthesis was that, upon addition of 1 mM silver nitrate into the flask containing a 24 h culture supernatant of the strain, the medium gradually turned brown, whereas no color change was observed in the control without bacteria. This brown color could be due to the excitation of surface plasmon vibrations, which would arise from the formation of silver nanoparticles in the reaction mixture [11]. Interestingly, the culture supernatant incubated with 1 mM silver nitrate mediated the biosynthesis of silver nanoparticles within 48 h. The 1 mM concentration for the synthesis of silver nanoparticles was selected based on the silver nitrate tolerating capacity of the isolateB. indica DC1. The strain showed optimum growth at 1 mM concentration. Moreover, the concentration of precursor (0.1–1 mM) for the synthesis of nanoparticles does not show any effect on the end product of reaction; thus the shape and size of nanoparticles were not affected by the precursor concentration ranging.UV-vis is the most established method for structural characterization of metal nanoparticles. The reduction of silver ions during exposure to the supernatant of the strain DC1 was easily monitored by UV-vis. After the incubation period, the reaction mixture was scanned in the range of 300–700 nm, showing a major absorbance peak at 460 nm (Figure1(a)). The broad peak is due to the anisotropic nature of the particles. It has been reported that the band in this region corresponds to the surface plasmon resonance of silver nanoparticles [27]. Thus, the reaction mixture indicates the formation of silver nanoparticles. The nanoparticles synthesize extracellularly, avoiding the downstream processing needed for intracellular synthesis.Figure 1
UV-vis spectra of culture supernatant ofBhargavaea indica DC1 treated with (1 mM) AgNO3 (a). Transmission electron micrograph of anisotropic silver nanoparticles synthesised byBhargavaea indica DC1, 100 and 200 nm (b).
(a)
(b)
(c)Various researchers have reported evidence of the extracellular biosynthesis of silver nanoparticles, including TEM structural characterizations [28]. The anisotropic silver nanoparticles synthesised were successfully characterized by FE-TEM and revealed that the particles ranged in size from 30 to 100 nm and were of various shapes including nanobar, pentagon, spherical, icosahedron, hexagonal, truncated triangle, and triangular shapes (Figure 1(b)). Although the monodispersity is the main issue associated with the nanoparticles synthesis, the biosynthesised anisotropic silver nanoparticles are of great advantage in biological platforms, since the silver nanoparticles undergo shape-dependent interactions with microorganisms [9]. Reports suggest that the biosynthesised silver nanoparticles of different shapes can be separated by centrifugation, as the nanoparticles show shape-dependent sedimentation behaviour [29]. The biological synthesis of anisotropic gold and silver nanoparticles byAspergillus niger has been reported previously. The syntheses of anisotropic silver nanoparticles byMorganella psychrotolerans [30] and anisotropic gold nanoparticles by the fungal strainRhizopus oryzae [31] have been studied. To our knowledge, this is the first report of the ability ofB. indica DC1 to synthesise silver nanoparticles of various shapes and sizes. The exact mechanism behind the synthesis remains to be elucidated, but based on reports, the enzyme and proteins synthesised extracellularly by bacterial strain in the reaction mixture help in reducing the silver nitrate to silver nanoparticles. Moreover, the particles synthesised without any additional stabilizing and capping agent thus eliminating the main step of chemical synthesis and overcome the limitations. The cell-free supernatant containing extracellular enzymes and proteins functions as a reducing, shape-directing, and stabilizing agent [2, 31].The purity of the biosynthesised silver nanoparticles was examined by EDX (Figure2(a)); the EDX spectrum displayed an optical absorption band peak at 3 keV, which is the characteristic peak of nanosized metallic silver, corresponding to surface plasmon resonance [32]. Carbon and copper signals originating in the low-energy part of the spectrum arose from the use of the carbon-coated copper TEM grid. Similar results have been observed in the study of biosynthesised silver nanoparticles byStreptomyces hygroscopicus [33] and mangroveStreptomyces sp. BDUKAS10 [6].Figure 2
EDX spectra of the whole scan area showing major peak of anisotropic silver nanoparticles at 3 keV (a) and TEM micrograph of anisotropic silver nanoparticles pellet solution and silver nanoparticles; 55.95% (b), respectively.
(a)
(b)
(c)Figure2(b) shows an elemental mapping result for the biosynthesised silver nanoparticles, showing the relative locations of elements in the TEM cross section. Results clearly demonstrate that the maximum deposition corresponds to silver nanoparticles, 55.95%. Other elements observed included carbon, 12.65%, and copper, 28.68%; these two elements were observed due to the carbon-coated copper grid used for TEM structural analysis. Chlorine was also observed in a very low amount, 2.71%, in the cross sections of the nanoparticles themselves. The distribution of silver element was clearly visible in elemental maps and was the predominant element. Thus, the EDX spectrum and elemental mapping gave confirmation that the nanoparticles consisted of silver only [6]. Figure 3 showed the X-ray diffraction pattern of silver nanoparticles and exhibited intense peaks in the whole spectrum of 2θ value ranging from 20 to 80 and this pattern was similar to Bragg’s reflection of silver nanocrystals.Figure 3
X-ray diffraction patterns of anisotropic silver nanoparticles obtained byBhargavaea indica DC1.The DLS measurements of number, intensity, and volume distribution of nanoparticles show the size range from 50 to 150 nm with an average diameter of 111 nm and PDI 0.233 (Figures4(a)–4(c)) which is different from the size measured by TEM, that is, 30–100 nm. Reports suggest that the size difference between the particles size analyses by DLS and TEM measurement has difference due to the fact that TEM visualizes the metallic core of the particles, whereas DLS measures the hydrodynamic diameter of the particles [34]. Thus,B. indica DC1 was demonstrated to be suitable for the simple, green, nonhazardous, economical, and eco-friendly synthesis of antimicrobial anisotropic silver nanoparticles without any additional reducing and stabilizing agent.Figure 4
Particles size distribution of anisotropic silver nanoparticles according to number (a), intensity (b), and volume (c), respectively.
(a)
(b)
(c)Based on the incubation of reaction mixture for different time interval at room temperature, the stability of the nanoparticles was observed and was found that there was no observable variation in the UV-vis spectrum, which directed the stable nature of the anisotropic silver nanoparticles. In addition, the silver nanoparticles solution was observed before and after the addition of sodium hydroxide. In results, no major change in the wavelength was observed, which further confirmed the stability.


## 3.3. Antimicrobial Activity of Silver Nanoparticles against Test Microorganisms

The biosynthesised silver nanoparticles displayed antimicrobial activity against a range of pathogenic microorganisms such asC. albicans,V. parahaemolyticus,S. aureus,B. anthracis,B. cereus,S. enterica, andE. coli (Figure 5). The mean diameter of the zone of inhibition of all the four wells was determined for each microorganism, showing that the silver nanoparticles had the greatest antimicrobial activity againstC. albicans, followed byV. parahaemolyticus,S. aureus,B. anthracis,B. cereus,S. enterica, and thenE. coli. The study has been done in duplicate and average results were interpreted in Table 1. The results clearly indicate that silver nanoparticles exert antimicrobial activity against tested microorganisms. Many studies have reported the antimicrobial activity of silver nanoparticles against pathogenic microorganisms [7, 11]. However, the mechanism of the metal nanoparticles’ inhibitory action is still not clearly understood. There are reports suggesting that (i) the electrostatic attraction between the negatively charged bacterial cell and the positively charged nanoparticles leads to accumulation of nanoparticles on the bacterial membrane, resulting in an increase in cell permeability, (ii) the association of silver with oxygen and its reaction with sulfhydryl (S-H) groups on the cell wall forms R-S-S-R bonds, thereby blocking respiration, (iii) the silver nanoparticles interact with bacterial proteins, which finally leads to cell death, and (iv) the nanoparticles release silver ion which provide additional bactericidal effect [35].Table 1
Diameter of zone of inhibition (mm) of reaction mixture (50μL) containing anisotropic silver nanoparticles against pathogenic microorganisms.
Number
Pathogenic microorganism
Zone of inhibition (mm)†
1
Candida albicans[KACC 30062]
23 ± 0.5
2
Vibrio parahaemolyticus[ATCC 33844]
22 ± 1
3
Staphylococcus aureus[ATCC 6538]
18 ± 0.8
4
Bacillus anthracis[NCTC 10340]
16 ± 0.6
5
Bacillus cereus[ATCC 14579]
15 ± 0.4
6
Salmonella enterica[ATCC 13076]
14 ± 1
7
Escherichia coli[ATCC 10798]
10 ± 1
†Mean diameter of four wells, 50 μL reaction mixture containing anisotropic silver nanoparticles.Figure 5
Zones of inhibition of 50μL of reaction mixture containing anisotropic silver nanoparticles against pathogenic strains includingCandida albicans,Vibrio parahaemolyticus,Staphylococcus aureus,Bacillus anthracis,Bacillus cereus,Salmonella enterica, andEscherichia coli, respectively.The combination of silver nanoparticles with different commercial antibiotics was evaluated to determine its activity against six pathogenic bacteria using the disk diffusion method. Figure6(a) represents the antimicrobial activity of partially purified silver nanoparticles and standard antibiotics antimicrobial activity againstS. enterica,E. coli,V. parahaemolyticus,B. anthracis,B. cereus, andS. aureus, respectively. The synergistic effect of antibiotics (lincomycin, oleandomycin, novobiocin, vancomycin, penicillin G, and rifampicin) with biosynthesised silver nanoparticles increased the susceptibility of the tested microorganisms (Figure 6(b)). The disk diffusion tests clearly indicated that the strains ofS. enterica,E. coli, andV. parahaemolyticuswere completely resistant to the antibiotics, whereas the bacterial strains showed sensitivity to the disks when anisotropic silver nanoparticle solution was added and results in the formation of a zone of inhibition forS. enterica,E. coli, andV. parahaemolyticus. The average increase in sensitivity patter of antibiotics was calculated by average increase in fold area [35]. The average increase in fold area of the antibiotics against antibiotics resistant microorganisms was greatest for novobiocin, followed by rifampicin, lincomycin, and oleandomycin and then vancomycin and penicillin G. Similar results regarding increase in fold area have been observed against multidrug resistantE. coli [16]. The other pathogenic stains showed susceptibility to antibiotics disks alone,B. anthracis,B. cereus, andS. aureus,and showed increased susceptibility when the disks were combined with anisotropic silver nanoparticle solution, observed as increases in the diameter of the zone of inhibition forB. anthracis,B. cereus, andS. aureus. This clearly indicated the effect of biosynthesised anisotropic silver nanoparticles in enhancing the antimicrobial action of antibiotics. The average increase in fold area against antibiotic sensitive microorganism, when anisotropic silver nanoparticles were added, was greatest for penicillin G, followed by vancomycin, rifampicin, oleandomycin, novobiocin, and lincomycin. In addition, in case of cycloheximide, the similar pattern of action was found againstC. albicans. On the addition of silver nanoparticles with cycloheximide, the activity of cycloheximide increases. The study has been done in duplicate and average results were interpreted in Table 2. The present study shows results similar to those of a line of studies that presented increased efficacies of commercial antibiotics against pathogenic microorganisms [13, 16, 28]. It indicates that biosynthesised anisotropic silver nanoparticles show antimicrobial activity against pathogenic microorganisms. Moreover, the nanoparticles were shown to enhance the effect of commercial antibiotics against multidrug resistant bacteria. Thus, the biosynthesised anisotropic silver nanoparticles are ready for applications in the clinical field against pathogenic microorganisms, although the exact mechanism of their action remains to be elucidated.Table 2
Individual and combined efficacy of commercial antibiotics with biosynthesised anisotropic silver nanoparticles against pathogenic microorganisms.
Pathogenic strain
MY15
MY15 + AgNPs
FA‡
OL15
OL15 + AgNPs
FA‡
NV30
NV30 + AgNPs
FA‡
(a)
(b)
(a)
(b)
(a)
(b)
S. enterica
0†
12 ± 0.5
3
0†
12 ± 0.2
3
0†
14 ± 0.9
4.44
E. coli
0†
13 ± 0.3
3.69
0†
13 ± 0.6
3.69
0†
14 ± 1
4.44
V. parahaemolyticus
0†
15 ± 0.4
5.25
0†
15 ± 0.3
5.25
0†
17 ± 0.6
7.02
Average
3.98
3.98
5.3
B. anthracis
14 ± 0.1
16 ± 0.1
0.31
15 ± 0.4
18 ± 0.2
0.44
19 ± 0.2
22 ± 0.3
0.34
B. cereus
16 ± 0.2
18 ± 0.6
0.26
22 ± 0.3
24 ± 0.5
0.19
22 ± 0.1
25 ± 0.4
0.29
S. aureus
25 ± 0.1
28 ± 0.5
0.25
22 ± 0.2
25 ± 0.7
0.29
30 ± 0.3
34 ± 1
0.28
Average
0.27
0.31
0.30
Pathogenic strain
VA30
VA30 + AgNPs
FA‡
P10
P10  + AgNPs
FA‡
RD5
RD5 + AgNPs
FA‡
(a)
(b)
(a)
(b)
(a)
(b)
S. enterica
0†
12 ± 0.3
3
0†
12 ± 1
3
0†
13 ± 0.5
3.69
E. coli
0†
13 ± 0.4
3.69
0†
13 ± 1.2
3.69
0†
13 ± 0.2
3.69
V. parahaemolyticus
0†
14 ± 0.2
4.44
0†
14 ± 1.5
4.44
0†
15 ± 0.3
5.25
Average
3.71
3.71
4.21
B. anthracis
15 ± 0.5
19 ± 0.7
0.6
0†
15 ± 0.5
5.25
12 ± 0.2
16 ± 0.7
0.78
B. cereus
17 ± 0.2
20 ± 0.6
0.38
8 ± 0.3
16 ± 0.8
3
13 ± 0.3
15 ± 0.4
0.33
S. aureus
16 ± 0.4
20 ± 0.2
0.56
36 ± 0.5
40 ± 0.8
0.23
27 ± 0.4
29 ± 0.6
0.15
Average
0.52
2.83
0.42
Pathogenic strain
CHX
CHX  +  AgNPs
FA‡
C. albicans
0†
13 ± 0.5
3.69
Notes.†In the absence of bacterial growth inhibition zones, the disc’s diameter (6 mm) was used to calculate the fold increases [13].
‡Increase in fold area (FA) = (b2-a2)/a2.
MY15: lincomycin 15μg/disk, OL15: oleandomycin 15 μg/disk, VA30: vancomycin 30 μg/disk,  NV30: novobiocin 30 μg/disk, P10: penicillin G 10 μg/disk, and RD5: rifampicin 5 μg/disk; CHX: cycloheximide, 10 μg/disk; AgNPs: biosynthesised anisotropic silver nanoparticles, 30 μL (100 ppm).Figure 6
Zones of inhibition of partially purified silver nanoparticles pellet solution 30μL (100 ppm) and standard antibiotics as control, againstSalmonella enterica,Escherichia coli,Vibrio parahaemolyticus,Bacillus anthracis,Bacillus cereus, andStaphylococcus aureus, respectively (a). Zones of inhibition of standard antibiotics disks with anisotropic silver nanoparticles againstSalmonella enterica,Escherichia coli,Vibrio parahaemolyticus,Bacillus anthracis,Bacillus cereus,Staphylococcus aureus, andCandida albicans (b), respectively.Note. (1) Lincomycin (MY15) 15 µg/disk, (2) oleandomycin (OL15) 15 µg/disk, (3) novobiocin (NV30) 30 µg/disk, (4) vancomycin (VA30) 30 µg/disk, (5) penicillin G (P10) 10 µg/disk, and (6) rifampicin (RD5) 5 µg/disk; cycloheximide (CHX) 10 µg/disk and anisotropic silver nanoparticles (AgNPs) 30 µL (100 ppm).
(a)
(b)


## 4. Conclusions

The most important advantage of this approach includes the possibility to obtain anisotropic silver nanoparticles of nanobar, pentagon, spherical, icosahedron, hexagonal, truncated triangle, and triangular shapes byBhargavaea indica DC1. The anisotropic silver nanoparticles were synthesized by eco-friendly and economical manner and eliminating the hazardous effects of physiochemical synthesis. Moreover, the particles were synthesized extracellularly, without any extra reducing and capping agent, thus excluding the extra step in physiochemical synthesis. Furthermore, the methodology has greater advantage of easy bulk synthesis which can be exploited for large scale industrial scale-up production due to easy downstream processing.The outcomes of study also indicated that the biosynthesised anisotropic silver nanoparticles had inherent antimicrobial activity and also enhanced the antimicrobial activity of commercial antibiotics against pathogenic microorganisms. The biosynthesized silver nanoparticles may have potential to be used as multifunctional nanoparticles for different applications on medical, clinical, and biological background such as targeting, diagnosis, drug delivery, and photoimaging. Further studies in order to understand the mechanism of action, surface engineering, specific targeting, and conjugation may be useful to develop novel nanoparticles for different applications.



---

*Source: 234741-2015-05-18.xml*