# Hyaluronic Acid-IR780 Nanoparticles for Photothermal Ablation in Orthotopic Renal Cancer

Authors: Guangxiang Liu; Tingsheng Lin; Qing Zhang; Shengjie Zhang; Changwei Ji; Shiwei Zhang; Hongqian Guo
Journal: Journal of Nanomaterials
 (2020)

---

## Abstract

Renal cancer is one of the most common malignancies in urological tumors; it is necessary to develop a noninvasive and highly targeted thermal ablation method for the treatment of renal tumors. IR780 has been shown to be an effective photothermal agent for tumor thermal ablation. This study was designed to explore the feasibility of applying hyaluronic acid-IR780 nanoparticles (HA-IR780 NPs) for targeted thermal ablation of renal tumors using an in situ renal tumor model. The size of the nanoparticles was172±8.2 nm; it showed a stable spherical nanostructure with good monodispersity. HA-IR780 NPs showed high photothermal efficiency, with the 20 μg/mL HA-IR780 NPs showing a maximum temperature increase of 24.5°C with 6 min of 808 nm laser irradiation. NIR imaging showed that the nanoparticles exhibited targeted accumulation in renal tumor tissues. The treatment efficacy of the HA-IR780 NPs showed that renal tumors treated with the HA-IR780 NPs and laser irradiation were effectively ablated. Our results showed that the HA-IR780 nanoparticles that mediated the photothermal effect could generate tumor-specific heat for the destruction of a renal tumor in a minimally invasive way, which provides a novel strategy for thermal ablation of renal tumors.


---

## Body

## 1. Introduction

Renal cancer is one of the most common malignancies in urology. Radical nephrectomy and nephron-sparing surgery are the major treatments for renal cancer [1–5]. In recent years, radiofrequency ablation (RFA) has been widely used in the treatment of renal tumors, due to its minimally invasive and high treatment efficiency. RFA is a process where needle electrodes are placed in the tumor tissues; the radiofrequency energy was output by the needle to generate heat with a local temperature of 95~100°C and damage the tumor lesions [6–9]. RFA has many advantages when compared with traditional surgery, but it also has many disadvantages: nonuniform heat production in the tumor, tumor dissemination through the RFA catheter, and adjacent organs damaged by high temperature [8, 10]. Therefore, it is necessary to develop a noninvasive and highly targeted thermal ablation method for the treatment of renal tumors.Photothermal therapy (PTT) is an effective method for treating tumors; photosensitizers can generate heat during laser irradiation, efficiently killing tumor cells and resulting in the ablation of tumors [11, 12]. When compared with radiofrequency ablation, photothermal therapy can uniformly generate heat at targeted tumor sites, is noninvasive, and provides a new strategy for thermal ablation of renal cancer [13–16]. Hyaluronic acid (HA) is one of the components in the human body and plays an important role in modulating the immune system and scavenging ROS. HA has good water solubility, biodegradation, low toxicity, and low immunogenicity; it is a good carrier for drug delivery [17–24]. IR780 is a lipophilic, cationic small molecule near-infrared (NIR) photosensitive agent that belongs to the near-infrared heptarchy cyanine dye group and has a molecular weight of 667 Da; it also can generate heat under NIR laser irradiation [25, 26].In this study, we prepared hyaluronic acid-IR780 nanoparticles (HA-IR780 NPs) (shown in Scheme1) using hyaluronic acid as the carrier according to our previous reports [15]. We characterized the HA-IR780 NP nanoparticles by dynamic light scattering (DLS), transmission electron microscope (TEM), and UV-visible spectrophotometer. The NPs were irradiated with an NIR laser to investigate its photothermal properties. The cellular uptake of the NPs in renal cancer cells was performed, and photothermal toxicity of the HA-IR780 NPs in renal cancer cells was also investigated. We established a stable orthotopic renal tumor model, the biodistribution of the NPs was observed by NIR imaging, and the antitumor efficacy of the HA-IR780 NPs in the orthotopic renal tumor model was evaluated.Scheme 1
The synthetic process of HA conjugates.


## 2. Materials and Methods

### 2.1. Materials

The following were the materials used: IR780 (Sigma-Aldrich, USA), 1-ethyl-3(3-dimethylaminopropyl) carbodiimide (EDC), N-hydroxysuccinimide (NHS), amino thiophenol (ATP) (J&K Scientific Ltd., China), hyaluronic acid (Mw=10 kDa) (Nanjing Sunlida Biological Technology Co., Ltd., China), cell counting kit-8 (CCK-8) (Dojindo Laboratories, Japan), N,N-dimethylformamide (DMF), and formamide (Shanghai Lingfeng Chemical Reagent Co., Ltd., China). All of the Balb/c mice (male, 6~8 weeks, 18~20 g) were from Yangzhou University Medical Center.


### 2.2. Preparation of the HA-IR780 NPs

For the preparation method of HA-IR780 NPs, refer to our previous report [15]. Briefly, the mixture of 4-aminothiophenol (15 μmol) and IR780 (7.5 μmol) dissolved in DMF was stirred at room temperature overnight to obtain IR780-NH2. Then, NHS (50 μmol), EDC (50 μmol), and HA (5 μmol) were dissolved in formamide solution to get HA-NHS ester. The mixture of HA-NHS ester and IR-780-NH2 (IR780:HA=1mol:1mol) was stirred at room temperature overnight to get amphiphilic HA-IR780 conjugates. The unreacted IR780 was removed by using Sephadex LH-20 (GE Healthcare). Finally, HA-IR780 conjugates were dispersed in PBS to obtain the HA-IR780 nanoparticles. The nanoparticles were purified using an ultrafiltration membrane (molecular weight ~30 kDa) to remove the free small molecules; then, the nanoparticles were filtered through a filter membrane (0.22 μm). Finally, the HA-IR780 NP dispersions were stored at 4°C.


### 2.3. Characterization of the HA-IR780 NPs

TEM (Hitachi H-7650) and DLS (Brookhaven Instruments Corporation, USA) were used to measure the diameter and morphology of the HA-IR780 NPs. The average diameter of HA-IR780 NPs in PBS (pH 7.4, 37°C) at different time points was measured by DLS to investigate its stability. The UV-vis spectra (UV2450, Shimadzu Corporation) of HA-IR780 NPs were also measured. The HA-IR780 NPs (5, 10, and 20μg/mL) were irradiated with the NIR laser (808 nm, 1 W/cm2) to investigate its photothermal properties.


### 2.4. In Vitro Cellular Uptake Behaviour of the HA-IR780 NPs

The renal cell lines (RENCA) were cultured in medium (1640 Gibco medium, 10% foetal bovine serum, 1% streptomycin, and 1% penicillin) in a CO2 incubator at 37°C. To evaluate the cellular uptake of HA-IR780 NPs, the cells were seeded in a 12-well compartment glass (2×104/well). After culturing for 24 h, the medium was replaced with fresh medium containing the HA-IR780 NPs (2 μg/mL). Then, the medium was removed, and cells were washed with PBS after 3 h of coincubation. Subsequently, cells were fixed with 4% paraformaldehyde, and the cell nucleus was stained with DAPI. The fluorescence (DAPI and IR780) in the cells was observed using a confocal laser scanning microscope (CLSM, Leica TCS SP5, Germany; emission: 700~800 nm, excitation: 633 nm).


### 2.5. Photothermal Toxicity of the HA-IR780 NPs In Vitro

To evaluate the photothermal cytotoxicity of the HA-IR780 NPs with NIR laser irradiation, the RENCA cells were seeded in a 96-well compartment glass (1×104/well). After culturing for 24 h, the medium was replaced with fresh medium containing different concentrations of HA-IR780 NPs. Then, the medium was removed after 3 h of coincubation, cells were washed with PBS, and the fresh medium was added. Subsequently, the cells were irradiated with the NIR laser (808 nm, 1 W/cm2) for 2 min. After culturing for 24 h, the CCK-8 assay was performed to evaluate the cell viability.


### 2.6. The Establishment of an Orthotopic Renal Tumor Model in Mice

Balb/c mice were used according to the protocols approved by the Nanjing University Laboratory Animal Center. Briefly, 0.2 mL RENCA cells (1×107) in PBS were injected into the right flank of the mice subcutaneously. After the tumor grew to about 300 mm3, the tumor was removed from the mice and cut into small tumor tissue blocks (∼1 mm3). Then, to establish the orthotopic renal cancer model, mice were anesthetized and fixed on an operating floor. A small left flank incision was made to expose the kidney; one tumor block was seeded into the subcapsular space of the kidney; then, the incision was sutured with 5-0 silk. After few days, the orthotopic renal tumor was confirmed with the naked eye by exposing the kidney directly.


### 2.7. In Vivo Biodistribution of the HA-IR780 NPs

The IR780 fluorescent signal was detected with the IVIS Lumina imaging system (Xenogen Co., USA) to evaluate the distribution of the HA-IR780 NPs in the orthotopic renal tumor model. The mice were intravenously injected with HA-IR780 NPs (2.5 mg/kg) or PBS; NIR imaging (emission spectrum: 780–900 nm, excitation wavelength: 735 nm) was performed at 2 h, 12 h, 24 h, and 48 h after injection. The distribution of the HA-IR780 NPs in the tumor and major organs (liver, lung, kidney, spleen, and heart) was evaluated. The mice were sacrificed 48 h after the injection, and the main organs were isolated; NIR imaging of major organs was performed. IVIS Living Imaging Software was used to analyze the obtained NIR images, and semiquantitative biodistribution analysis was also performed.


### 2.8. Photothermal Therapeutic Efficacy of the HA-IR780 NPs in an Orthotopic Renal Tumor Model

To measure the intratumoral temperature, the HA-IR780 NPs (5 mg/kg IR780) or PBS were intravenously injected into orthotopic renal cancer-bearing mice. 24 hours after injection, mice were anesthetized and the renal tumor was exposed by a small left flank incision; the intratumoral temperature changes under the laser irradiation (808 nm, 1 W/cm2) were recorded. To investigate the treatment efficacy of the NPs, orthotopic renal cancer-bearing mice were divided into four groups (4 mice in each group), including the PBS group, PBS with laser irradiation group, HA-IR780 NP group, and HA-IR780 NPs with laser irradiation group. Mice were intravenously injected with HA-IR780 NPs (5 mg/kg IR780) or PBS. The tumors were irradiated with the NIR laser (808 nm, 1 W/cm2) for 8 min after 24 h injection (day 0). The body weight was measured every two days. The mice were sacrificed at day 12, photographs of kidneys and tumors were taken with a camera, the tumor size was measured, and the kidneys were collected for H&E staining.


### 2.9. Statistical Analysis

A two-sided Studentt-test for two groups and one-way ANOVA for multiple groups were used for statistical analysis. P<0.05 was considered statistically significant.


## 2.1. Materials

The following were the materials used: IR780 (Sigma-Aldrich, USA), 1-ethyl-3(3-dimethylaminopropyl) carbodiimide (EDC), N-hydroxysuccinimide (NHS), amino thiophenol (ATP) (J&K Scientific Ltd., China), hyaluronic acid (Mw=10 kDa) (Nanjing Sunlida Biological Technology Co., Ltd., China), cell counting kit-8 (CCK-8) (Dojindo Laboratories, Japan), N,N-dimethylformamide (DMF), and formamide (Shanghai Lingfeng Chemical Reagent Co., Ltd., China). All of the Balb/c mice (male, 6~8 weeks, 18~20 g) were from Yangzhou University Medical Center.


## 2.2. Preparation of the HA-IR780 NPs

For the preparation method of HA-IR780 NPs, refer to our previous report [15]. Briefly, the mixture of 4-aminothiophenol (15 μmol) and IR780 (7.5 μmol) dissolved in DMF was stirred at room temperature overnight to obtain IR780-NH2. Then, NHS (50 μmol), EDC (50 μmol), and HA (5 μmol) were dissolved in formamide solution to get HA-NHS ester. The mixture of HA-NHS ester and IR-780-NH2 (IR780:HA=1mol:1mol) was stirred at room temperature overnight to get amphiphilic HA-IR780 conjugates. The unreacted IR780 was removed by using Sephadex LH-20 (GE Healthcare). Finally, HA-IR780 conjugates were dispersed in PBS to obtain the HA-IR780 nanoparticles. The nanoparticles were purified using an ultrafiltration membrane (molecular weight ~30 kDa) to remove the free small molecules; then, the nanoparticles were filtered through a filter membrane (0.22 μm). Finally, the HA-IR780 NP dispersions were stored at 4°C.


## 2.3. Characterization of the HA-IR780 NPs

TEM (Hitachi H-7650) and DLS (Brookhaven Instruments Corporation, USA) were used to measure the diameter and morphology of the HA-IR780 NPs. The average diameter of HA-IR780 NPs in PBS (pH 7.4, 37°C) at different time points was measured by DLS to investigate its stability. The UV-vis spectra (UV2450, Shimadzu Corporation) of HA-IR780 NPs were also measured. The HA-IR780 NPs (5, 10, and 20μg/mL) were irradiated with the NIR laser (808 nm, 1 W/cm2) to investigate its photothermal properties.


## 2.4. In Vitro Cellular Uptake Behaviour of the HA-IR780 NPs

The renal cell lines (RENCA) were cultured in medium (1640 Gibco medium, 10% foetal bovine serum, 1% streptomycin, and 1% penicillin) in a CO2 incubator at 37°C. To evaluate the cellular uptake of HA-IR780 NPs, the cells were seeded in a 12-well compartment glass (2×104/well). After culturing for 24 h, the medium was replaced with fresh medium containing the HA-IR780 NPs (2 μg/mL). Then, the medium was removed, and cells were washed with PBS after 3 h of coincubation. Subsequently, cells were fixed with 4% paraformaldehyde, and the cell nucleus was stained with DAPI. The fluorescence (DAPI and IR780) in the cells was observed using a confocal laser scanning microscope (CLSM, Leica TCS SP5, Germany; emission: 700~800 nm, excitation: 633 nm).


## 2.5. Photothermal Toxicity of the HA-IR780 NPs In Vitro

To evaluate the photothermal cytotoxicity of the HA-IR780 NPs with NIR laser irradiation, the RENCA cells were seeded in a 96-well compartment glass (1×104/well). After culturing for 24 h, the medium was replaced with fresh medium containing different concentrations of HA-IR780 NPs. Then, the medium was removed after 3 h of coincubation, cells were washed with PBS, and the fresh medium was added. Subsequently, the cells were irradiated with the NIR laser (808 nm, 1 W/cm2) for 2 min. After culturing for 24 h, the CCK-8 assay was performed to evaluate the cell viability.


## 2.6. The Establishment of an Orthotopic Renal Tumor Model in Mice

Balb/c mice were used according to the protocols approved by the Nanjing University Laboratory Animal Center. Briefly, 0.2 mL RENCA cells (1×107) in PBS were injected into the right flank of the mice subcutaneously. After the tumor grew to about 300 mm3, the tumor was removed from the mice and cut into small tumor tissue blocks (∼1 mm3). Then, to establish the orthotopic renal cancer model, mice were anesthetized and fixed on an operating floor. A small left flank incision was made to expose the kidney; one tumor block was seeded into the subcapsular space of the kidney; then, the incision was sutured with 5-0 silk. After few days, the orthotopic renal tumor was confirmed with the naked eye by exposing the kidney directly.


## 2.7. In Vivo Biodistribution of the HA-IR780 NPs

The IR780 fluorescent signal was detected with the IVIS Lumina imaging system (Xenogen Co., USA) to evaluate the distribution of the HA-IR780 NPs in the orthotopic renal tumor model. The mice were intravenously injected with HA-IR780 NPs (2.5 mg/kg) or PBS; NIR imaging (emission spectrum: 780–900 nm, excitation wavelength: 735 nm) was performed at 2 h, 12 h, 24 h, and 48 h after injection. The distribution of the HA-IR780 NPs in the tumor and major organs (liver, lung, kidney, spleen, and heart) was evaluated. The mice were sacrificed 48 h after the injection, and the main organs were isolated; NIR imaging of major organs was performed. IVIS Living Imaging Software was used to analyze the obtained NIR images, and semiquantitative biodistribution analysis was also performed.


## 2.8. Photothermal Therapeutic Efficacy of the HA-IR780 NPs in an Orthotopic Renal Tumor Model

To measure the intratumoral temperature, the HA-IR780 NPs (5 mg/kg IR780) or PBS were intravenously injected into orthotopic renal cancer-bearing mice. 24 hours after injection, mice were anesthetized and the renal tumor was exposed by a small left flank incision; the intratumoral temperature changes under the laser irradiation (808 nm, 1 W/cm2) were recorded. To investigate the treatment efficacy of the NPs, orthotopic renal cancer-bearing mice were divided into four groups (4 mice in each group), including the PBS group, PBS with laser irradiation group, HA-IR780 NP group, and HA-IR780 NPs with laser irradiation group. Mice were intravenously injected with HA-IR780 NPs (5 mg/kg IR780) or PBS. The tumors were irradiated with the NIR laser (808 nm, 1 W/cm2) for 8 min after 24 h injection (day 0). The body weight was measured every two days. The mice were sacrificed at day 12, photographs of kidneys and tumors were taken with a camera, the tumor size was measured, and the kidneys were collected for H&E staining.


## 2.9. Statistical Analysis

A two-sided Studentt-test for two groups and one-way ANOVA for multiple groups were used for statistical analysis. P<0.05 was considered statistically significant.


## 3. Results and Discussions

### 3.1. Preparation and Characterization of the HA-IR780 NPs

The HA-IR780 nanoparticles were prepared according to our previous reports. The HA was chemically conjugated with IR780 to obtain a HA-IR780 conjugate via 4-aminothiophenol. HA-IR780 conjugate is amphiphilic, due to its hydrophobic IR780 segment and hydrophilic HA segment. Therefore, the HA-IR780 conjugates self-assembled into nanoparticles with a hydrophobic core and a hydrophilic shell in aqueous solutions. From Figure1(a), DLS showed that the particle size of the HA-IR780 nanoparticles was evenly distributed between 150 and 180 nm with an average particle size of 172±8.2 nm. TEM revealed that the NPs were spherical in shape with good monodispersity. Figure 1(b) shows that the stability of the HA-IR780 NPs and the size of the NPs remained consistent (~180 nm) at 24 hours. Figure 1(c) shows UV/vis absorption bands between 706 and 836 nm of the HA-IR780 NPs with a maximum wavelength at 796 nm in ethanol. When compared with free IR780, the absorption peak of the HA-IR780 NPs was a 10 nm redshift. This is because the structure of IR780 was changed by chemical modification. Figure 1(d) shows the photothermal efficiency of the HA-IR780 NPs in vitro. When the concentration of HA-IR780 NPs was 5, 10, and 20 μg/mL, the temperature increase was 15.8°C, 20.3°C, and 24.5°C with 6 min of 808 nm laser irradiation (1 W/cm2), respectively. The tumor cells can receive irreversible damage from the NPs with this temperature increase.Figure 1
Characterization of the HA-IR780 NPs: (a) size distribution and TEM image of the HA-IR780 NPs, (b) size stability of the HA-IR780 NPs, (c) UV-vis-NIR absorbance spectrum of the HA-IR780 NPs, and (d) photothermal effect of the HA-IR780 NPs in vitro.
(a)
(b)
(c)
(d)


### 3.2. In Vitro Cellular Uptake Behaviour of the HA-IR780 NPs

The cellular uptake of the HA-IR780 NPs by the RENCA cell lines that was observed by confocal microscopy is shown in Figure2. The cancer cells treated with the HA-IR780 NPs (2 μg/mL) showed a strong red colour in the cytoplasm, and the cancer cells that were treated with PBS showed no red colour in the cytoplasm. This indicated that a large number of the HA-IR780 NPs were taken up by the cancer cells.Figure 2
Cellular uptake of the HA-IR780 NPs. Confocal images of the RENCA cells after 3 h of incubation with the HA-IR780 NPs (blue: DAPI, red: IR780).


### 3.3. Photothermal Toxicity of the HA-IR780 NPs In Vitro

The photothermal therapy effect of the HA-IR780 NPs in the RENCA cells was evaluated. Figure3 shows the remarkable cytotoxicity of the HA-IR780 NPs when the cells were exposed to 808 nm laser irradiation; especially at IR780 concentrations of 4 μg/mL, the survival rate of the RENCA cells was only 3.1%. Without laser irradiation, the control group showed low cytotoxicity of the HA-IR780 NPs on the RENCA cells. The results suggested that the HA-IR780 NPs can effectively kill cancer cells via the photothermal effect.Figure 3
In vitro photothermal therapy of the HA-IR780 NPs. The cytotoxicity of the HA-IR780 NPs in the RENCA cells with or without laser irradiation (808 nm, 1 W/cm2) for 2 min.


### 3.4. In Vivo Biodistribution of the HA-IR780 NPs

We established the orthotopic renal tumor model in Balb/c mice. The distribution of the HA-IR780 NPs in orthotopic renal tumor-bearing mice was evaluated with the IVIS Lumina imaging system. Figure4 shows the NIR fluorescence of the HA-IR780 NPs that was detected in the tumor region (left kidney) at 2 h postinjection. The HA-IR780 NPs tended to accumulate in the tumor region over time, with remarkable accumulation in the tumor region after 24 h and 48 h injection. The distribution of the HA-IR780 NPs in the tumor and major organs (liver, lung, kidney, spleen, and heart) was evaluated at 48 h after the injection. The results showed that the tumors had a stronger NIR fluorescence signal, which confirmed the accumulation of the HA-IR780 NPs in the tumor. The results indicated excellent tumor-targeting property of the HA-IR780 NPs. This excellent tumor-targeting property of the NPs is probably due to the EPR effect on the tumor of the NPs.Figure 4
In vivo biodistribution of HA-IR780 NPs in orthotopic renal tumor-bearing mice: (a) NIR imaging of orthotopic renal tumor-bearing mice injected with HA-IR780 NPs; (b) fluorescence images of the major organs and renal tumor at 48 h after injection of the NPs; (c) semiquantitative biodistribution analysis of the HA-IR780 NPs in mice.
(a)
(b)
(c)


### 3.5. Photothermal Therapeutic Efficacy of the HA-IR780 NPs in an Orthotopic Renal Tumor Model

Next, we measured the intratumoral temperature under the laser irradiation (808 nm, 1 W/cm2) at 24 h after the intravenous injection of the NPs (Figure 5(b)). Temperature changes in the tumor area were measured during 8 min laser irradiation. The temperature of the tumor area was significantly increased in the HA-IR780 NP groups within 8 min laser irradiation, and the tumor area had a maximum temperature of 49.8±1.69°C. However, the temperature of the tumor area was not significantly changed in the PBS groups.Figure 5
Photothermal therapy for orthotopic renal tumor-bearing mice: (a) tumor volume of mice pretreatment; (b) temperature changes in the tumor area under laser irradiation (808 nm, 1 W/cm2, 8 min) after mice were injected with HA-IR780 NPs; (c) tumor volume at 12 days after different treatments; (d) body weight of mice after different treatments.
(a)
(b)
(c)
(d)At day 0, the tumor volume was66.8±38.42 mm3, 54.795±14.76 mm3, 59.43±10.10 mm3, and 68.1±27.28 mm3 in the PBS group, PBS with laser irradiation group, HA-IR780 NP, group and HA-IR780 NPs with laser irradiation group, respectively (Figure 5(a)). At day 12, the tumor size was 926.9±211.82 mm3, 950.1±151.22 mm3, 849.7±132.07 mm3, and 28.7±18.02 mm3 in the PBS group, PBS with laser irradiation group, HA-IR780 NP group, and HA-IR780 NPs with laser irradiation group, respectively (Figure 5(c)). The clear visual images of pre-/posttreatment orthotopic renal cancer are shown in Figure 6. All renal tumors were sliced and stained with H&E; the PBS, PBS with laser, and HA-IR780 NPs without laser groups showed large tumors located in the kidneys. However, in the HA-IR780 NPs with laser irradiation group, only very small residual tumors were located in the kidneys. In addition, there was no significant difference in body weight after the various treatments (Figure 5(d)). The results indicated the excellent photothermal effect on renal tumor ablation.Figure 6
Representative images of orthotopic renal cancer at pretreatment and posttreatment and the corresponding H&E-stained renal tumor sections.


## 3.1. Preparation and Characterization of the HA-IR780 NPs

The HA-IR780 nanoparticles were prepared according to our previous reports. The HA was chemically conjugated with IR780 to obtain a HA-IR780 conjugate via 4-aminothiophenol. HA-IR780 conjugate is amphiphilic, due to its hydrophobic IR780 segment and hydrophilic HA segment. Therefore, the HA-IR780 conjugates self-assembled into nanoparticles with a hydrophobic core and a hydrophilic shell in aqueous solutions. From Figure1(a), DLS showed that the particle size of the HA-IR780 nanoparticles was evenly distributed between 150 and 180 nm with an average particle size of 172±8.2 nm. TEM revealed that the NPs were spherical in shape with good monodispersity. Figure 1(b) shows that the stability of the HA-IR780 NPs and the size of the NPs remained consistent (~180 nm) at 24 hours. Figure 1(c) shows UV/vis absorption bands between 706 and 836 nm of the HA-IR780 NPs with a maximum wavelength at 796 nm in ethanol. When compared with free IR780, the absorption peak of the HA-IR780 NPs was a 10 nm redshift. This is because the structure of IR780 was changed by chemical modification. Figure 1(d) shows the photothermal efficiency of the HA-IR780 NPs in vitro. When the concentration of HA-IR780 NPs was 5, 10, and 20 μg/mL, the temperature increase was 15.8°C, 20.3°C, and 24.5°C with 6 min of 808 nm laser irradiation (1 W/cm2), respectively. The tumor cells can receive irreversible damage from the NPs with this temperature increase.Figure 1
Characterization of the HA-IR780 NPs: (a) size distribution and TEM image of the HA-IR780 NPs, (b) size stability of the HA-IR780 NPs, (c) UV-vis-NIR absorbance spectrum of the HA-IR780 NPs, and (d) photothermal effect of the HA-IR780 NPs in vitro.
(a)
(b)
(c)
(d)


## 3.2. In Vitro Cellular Uptake Behaviour of the HA-IR780 NPs

The cellular uptake of the HA-IR780 NPs by the RENCA cell lines that was observed by confocal microscopy is shown in Figure2. The cancer cells treated with the HA-IR780 NPs (2 μg/mL) showed a strong red colour in the cytoplasm, and the cancer cells that were treated with PBS showed no red colour in the cytoplasm. This indicated that a large number of the HA-IR780 NPs were taken up by the cancer cells.Figure 2
Cellular uptake of the HA-IR780 NPs. Confocal images of the RENCA cells after 3 h of incubation with the HA-IR780 NPs (blue: DAPI, red: IR780).


## 3.3. Photothermal Toxicity of the HA-IR780 NPs In Vitro

The photothermal therapy effect of the HA-IR780 NPs in the RENCA cells was evaluated. Figure3 shows the remarkable cytotoxicity of the HA-IR780 NPs when the cells were exposed to 808 nm laser irradiation; especially at IR780 concentrations of 4 μg/mL, the survival rate of the RENCA cells was only 3.1%. Without laser irradiation, the control group showed low cytotoxicity of the HA-IR780 NPs on the RENCA cells. The results suggested that the HA-IR780 NPs can effectively kill cancer cells via the photothermal effect.Figure 3
In vitro photothermal therapy of the HA-IR780 NPs. The cytotoxicity of the HA-IR780 NPs in the RENCA cells with or without laser irradiation (808 nm, 1 W/cm2) for 2 min.


## 3.4. In Vivo Biodistribution of the HA-IR780 NPs

We established the orthotopic renal tumor model in Balb/c mice. The distribution of the HA-IR780 NPs in orthotopic renal tumor-bearing mice was evaluated with the IVIS Lumina imaging system. Figure4 shows the NIR fluorescence of the HA-IR780 NPs that was detected in the tumor region (left kidney) at 2 h postinjection. The HA-IR780 NPs tended to accumulate in the tumor region over time, with remarkable accumulation in the tumor region after 24 h and 48 h injection. The distribution of the HA-IR780 NPs in the tumor and major organs (liver, lung, kidney, spleen, and heart) was evaluated at 48 h after the injection. The results showed that the tumors had a stronger NIR fluorescence signal, which confirmed the accumulation of the HA-IR780 NPs in the tumor. The results indicated excellent tumor-targeting property of the HA-IR780 NPs. This excellent tumor-targeting property of the NPs is probably due to the EPR effect on the tumor of the NPs.Figure 4
In vivo biodistribution of HA-IR780 NPs in orthotopic renal tumor-bearing mice: (a) NIR imaging of orthotopic renal tumor-bearing mice injected with HA-IR780 NPs; (b) fluorescence images of the major organs and renal tumor at 48 h after injection of the NPs; (c) semiquantitative biodistribution analysis of the HA-IR780 NPs in mice.
(a)
(b)
(c)


## 3.5. Photothermal Therapeutic Efficacy of the HA-IR780 NPs in an Orthotopic Renal Tumor Model

Next, we measured the intratumoral temperature under the laser irradiation (808 nm, 1 W/cm2) at 24 h after the intravenous injection of the NPs (Figure 5(b)). Temperature changes in the tumor area were measured during 8 min laser irradiation. The temperature of the tumor area was significantly increased in the HA-IR780 NP groups within 8 min laser irradiation, and the tumor area had a maximum temperature of 49.8±1.69°C. However, the temperature of the tumor area was not significantly changed in the PBS groups.Figure 5
Photothermal therapy for orthotopic renal tumor-bearing mice: (a) tumor volume of mice pretreatment; (b) temperature changes in the tumor area under laser irradiation (808 nm, 1 W/cm2, 8 min) after mice were injected with HA-IR780 NPs; (c) tumor volume at 12 days after different treatments; (d) body weight of mice after different treatments.
(a)
(b)
(c)
(d)At day 0, the tumor volume was66.8±38.42 mm3, 54.795±14.76 mm3, 59.43±10.10 mm3, and 68.1±27.28 mm3 in the PBS group, PBS with laser irradiation group, HA-IR780 NP, group and HA-IR780 NPs with laser irradiation group, respectively (Figure 5(a)). At day 12, the tumor size was 926.9±211.82 mm3, 950.1±151.22 mm3, 849.7±132.07 mm3, and 28.7±18.02 mm3 in the PBS group, PBS with laser irradiation group, HA-IR780 NP group, and HA-IR780 NPs with laser irradiation group, respectively (Figure 5(c)). The clear visual images of pre-/posttreatment orthotopic renal cancer are shown in Figure 6. All renal tumors were sliced and stained with H&E; the PBS, PBS with laser, and HA-IR780 NPs without laser groups showed large tumors located in the kidneys. However, in the HA-IR780 NPs with laser irradiation group, only very small residual tumors were located in the kidneys. In addition, there was no significant difference in body weight after the various treatments (Figure 5(d)). The results indicated the excellent photothermal effect on renal tumor ablation.Figure 6
Representative images of orthotopic renal cancer at pretreatment and posttreatment and the corresponding H&E-stained renal tumor sections.


## 4. Conclusion

We designed the HA-IR780 conjugates, which could self-assemble in water to form HA-IR780 nanoparticles for photothermal ablation of renal tumors. We established a stable orthotopic renal tumor model; the HA-IR780 nanoparticles demonstrated good-tumor targeting property and excellent photothermal effect for renal cancer treatment in the orthotopic renal tumor model.



---

*Source: 2421971-2020-04-16.xml*