# A Review on Natural Fiber Reinforced Polymer Composite and Its Applications

Authors: Layth Mohammed; M. N. M. Ansari; Grace Pua; Mohammad Jawaid; M. Saiful Islam
Journal: International Journal of Polymer Science
 (2015)

---

## Abstract

Natural fibers are getting attention from researchers and academician to utilize in polymer composites due to their ecofriendly nature and sustainability. The aim of this review article is to provide a comprehensive review of the foremost appropriate as well as widely used natural fiber reinforced polymer composites (NFPCs) and their applications. In addition, it presents summary of various surface treatments applied to natural fibers and their effect on NFPCs properties. The properties of NFPCs vary with fiber type and fiber source as well as fiber structure. The effects of various chemical treatments on the mechanical and thermal properties of natural fibers reinforcements thermosetting and thermoplastics composites were studied. A number of drawbacks of NFPCs like higher water absorption, inferior fire resistance, and lower mechanical properties limited its applications. Impacts of chemical treatment on the water absorption, tribology, viscoelastic behavior, relaxation behavior, energy absorption flames retardancy, and biodegradability properties of NFPCs were also highlighted. The applications of NFPCs in automobile and construction industry and other applications are demonstrated. It concluded that chemical treatment of the natural fiber improved adhesion between the fiber surface and the polymer matrix which ultimately enhanced physicomechanical and thermochemical properties of the NFPCs.


---

## Body

## 1. Introduction

The increase in environmental consciousness and community interest, the new environmental regulations and unsustainable consumption of petroleum, led to thinking of the use of environmentally friendly materials. Natural fiber is considered one of the environmentally friendly materials which have good properties compared to synthetic fiber [1].A late current industry research identified that the worldwide natural fiber reinforced polymer composites industry sector reached U$2.1 billion in 2010. Current pointers are that interest in NFPCs industry will keep on growing quickly around the world. The utilization of NFPCs has expanded considerably in the shopper merchandise as developing industry sectors throughout the last few years. As indicated by evaluations, over 5 years (2011–2016), the NFPCs industry is estimated to grow 10% worldwide [2].Natural fibers in simple definition are fibers that are not synthetic or manmade. They can be sourced from plants or animals [3]. The use of natural fiber from both resources, renewable and nonrenewable such as oil palm, sisal, flax, and jute to produce composite materials, gained considerable attention in the last decades, so far. The plants, which produce cellulose fibers can be classified into bast fibers (jute, flax, ramie, hemp, and kenaf), seed fibers (cotton, coir, and kapok), leaf fibers (sisal, pineapple, and abaca), grass and reed fibers (rice, corn, and wheat), and core fibers (hemp, kenaf, and jute) as well as all other kinds (wood and roots) [4]. The most common and commercially natural fibers in the world and world production have been shown in Table 1.Table 1
Natural fibers in the world and their world production [4].
Fiber source
World production (10
3 ton)
Bamboo
30.000
Sugar cane bagasse
75.000
Jute
2300
Kenaf
970
Flax
830
Grass
700
Sisal
375
Hemp
214
Coir
100
Ramie
100
Abaca
70Fiber reinforced polymer matrix got considerable attention in numerous applications because of the good properties and superior advantages of natural fiber over synthetic fibers in term of its relatively low weight, low cost, less damage to processing equipment, good relative mechanical properties such as tensile modulus and flexural modulus, improved surface finish of molded parts composite, renewable resources, being abundant [5], flexibility during processing, biodegradability, and minimal health hazards. NFPCs with a high specific stiffness and strength can be produced by adding the tough and light-weight natural fiber into polymer (thermoplastic and thermoset) [6]. On the other hand, natural fibers are not free from problems and they have notable deficits in properties. The natural fibers structure consists of (cellulose, hemicelluloses, lignin, pectin, and waxy substances) and permits moisture absorption from the surroundings which causes weak bindings between the fiber and polymer. Furthermore, the couplings between natural fiber and polymer are considered a challenge because the chemical structures of both fibers and matrix are various. These reasons for ineffectual stress transfer during the interface of the produced composites. Accordingly, natural fiber modifications using specific treatments are certainly necessary. These modifications are generally centered on the utilization of reagent functional groups which have ability for responding of the fiber structures and changing their composition. As a result, fiber modifications cause reduction of moisture absorption of the natural fibers which lead to an excellent enhancement incompatibility between the fiber and polymer matrix [7].The wide applications of NFPCs are growing rapidly in numerous engineering fields. The different kinds of natural fibers reinforced polymer composite have received a great importance in different automotive applications by many automotive companies such as German auto companies (BMW, Audi Group, Ford, Opel, Volkswagen, Daimler Chrysler, and Mercedes), Proton company (Malaysian national carmaker), and Cambridge industry (an auto industry in USA). Beside the auto industry, the applications of natural fiber composites have also been found in building and construction industry, sports, aerospace, and others, for example, panels, window frame, decking, and bicycle frame [8].In a review of chemical treatments of natural fibers, Kabir and coworkers [9] concurred that treatment is an important factor that has to be considered when processing natural fibers. They observed that fibers loose hydroxyl groups due to different chemical treatments, thereby reducing the hydrophilic behavior of the fibers and causing enhancement in mechanical strength as well as dimensional stability of natural fiber reinforced polymer composites. Their general conclusion was that chemical treatment of natural fibers results in a remarkable improvement of the NFPCs.


## 2. Natural Fiber Reinforced Composites (NFPCs)

Natural fiber polymer composites (NFPC) are a composite material consisting of a polymer matrix embedded with high-strength natural fibers, like jute, oil palm, sisal, kenaf, and flax [10]. Usually, polymers can be categorized into two categories, thermoplastics and thermosets. The structure of thermoplastic matrix materials consists of one or two dimensional moleculars, so these polymers have a tendency to make softer at an raised heat range and roll back their properties throughout cooling. On the other hand, thermosets polymer can be defined as highly cross-linked polymers which cured using only heat, or using heat and pressure, and/or light irradiation. This structure gives to thermoset polymer good properties such as high flexibility for tailoring desired ultimate properties, great strength, and modulus [3, 4]. Thermoplastics widely used for biofibers are polyethylene [11], polypropylene (PP) [12], and poly vinyly chloride (PVC); hereas phenolic, polyester, and epoxy resins are mostly utilized thermosetting matrices [10]. Different factors can affect the characteristics and performance of NFPCs. The hydrophilic nature of the natural fiber [5] and the fiber loading also have impacts on the composite properties [13]. Usually, high fiber loading is needed to attain good properties of NFPCs [14]. Generally, notice that the rise in fiber content causes improving in the tensile properties of the composites [8]. Another vital factor that considerably impacts the properties and surface characteristics of the composites is the process parameters utilized. For that reason, appropriate process techniques and parameters should be rigorously chosen in order to get the best characteristics of producing composite [10]. The chemical composition of natural fibers also has a big effect on the characteristics of the composite represented by the percentage of cellulose, hemicellulose, lignin, and waxes. Table 2 shows the chemical composition of some common natural fibers [4].Table 2
Chemical composition of some common natural fibers [4].
Fiber
Cellulose (wt%)
Hemicellulose (wt%)
Ligning (wt%)
Waxes (wt%)
Bagasse
55.2
16.8
25.3
—
Bamboo
26–43
30
21–31
—
Flax
71
18.6–20.6
2.2
1.5
Kenaf
72
20.3
9
—
Jute
61–71
14–20
12-13
0.5
Hemp
68
15
10
0.8
Ramie
68.6–76.2
13–16
0.6–0.7
0.3
Abaca
56–63
20–25
7–9
3
Sisal
65
12
9.9
2
Coir
32–43
0.15–0.25
40–45
Oil palm
65
—
29
—
Pineapple
81
—
12.7
—
Curaua
73.6
9.9
7.5
—
Wheat straw
38–45
15–31
12–20
—
Rice husk
35–45
19–25
20
—
Rice straw
41–57
33
8–19
8–38Many researchers [8, 11, 15–17] have examined and researched the suitability, competitiveness, and capabilities of natural fibers embedded in polymeric matrices. The researchers [4, 18, 19] concentrated on the effect of the fiber surface modifications as well as manufacturing processes in improving fiber/polymer compatibility. On the other hand, some researchers studied and compared between different natural fiber composites and their stability in various applications [20]. Al-Oqla and Sapuan [20] investigated the properties of jute/plastic composites such as crystallinity, fiber modification, thermal stability, weathering resistance, durability, in addition to their suitability to the automotive industry throughout ecodesign components. while Mohanty et al. [21] studied the effects of jute fiber on the mechanical properties of pure biodegradable polymer (Biopol), the mechanical properties of the resulted composites, impact strength, tensile strength, and bending strength, showed an increase when compared with pure Biopol. The tensile strength of jute Biopol was enhanced by 50%, while bending strength and impact strength of the composites were enhanced by 30% and 90% in comparison to pure Biopol.


## 3. General Characteristics of NFPCs

The properties of natural fiber composite are different to each other according to previous studies, because of different kinds of fibers, sources, and moisture conditions. The performance of NFPCs relies on some factors, like mechanical composition, microfibrillar angle [20], structure [10], defects [22], cell dimensions [23], physical properties [4], chemical properties [24], and also the interaction of a fiber with the matrix [25]. Since every product in market has drawbacks, similarly, natural fiber reinforced polymer composites also have drawbacks. The couplings between natural fiber and polymer matrix are problem taken into consideration, as a result of the difference in chemical structure between these two phases. This leads to ineffective stress transfer during the interface of the NFPCs. Thus, the chemical treatments for the natural fiber are necessary to achieve good interface properties. The reagent functional groups in the chemical treatments have ability to react on the fiber structures and alter the fiber composition [9]. Natural fibers include a functional group named as hydroxyl group which makes the fibers hydrophilic. During manufacturing of NFPCs, weaker interfacial bonding occurs between hydrophilic natural fibre and hydrophobic polymer matrices due to hydroxyl group in natural fibres. This could produce NFPCs with weak mechanical and physical properties [8].


### 3.1. Mechanical Properties of the NFPCs

There are considerable enhancement and suggestions for the natural fibers that can be implemented in order to enhance their mechanical properties resulting in high strength and structure. Once the base structures are made strong, the polymers can be easily strengthened and improved [26]. There are number of aspects that effects of composite are performance level or activities, of which to name a few are the following;(a)
orientation of fiber [5],
(b)
strength of fibers [8],
(c)
physical properties of fibers [27],
(d)
interfacial adhesion property of fibers [28] and many more.NFPCs are such composites whose mechanical efficiency is dependent upon the interface provided by fiber-matrix along with the stress transfer function in which stress is transferred to fiber from matrix. This has been reported by many investigators in several researches [1, 23, 29]. Characteristic components of natural fibers such as orientation [30], moisture absorption [31], impurities [32], physical properties [33], and volume fraction [34] are such features that play a constitutive role in the determination of NFPCs mechanical properties. Mechanical properties of PLA, epoxy, PP, and polyester matrices can be affected by many types of natural fibers and to show some of them, Figure 1 is included.Figure 1
Some of mechanical properties of natural fiber reinforced polymer composite [5].NFPCs show even better mechanical properties than a pure matrix in cases where jute fibers are added in PLA (polylactic-acid); in this case, 75.8% of PLA’s tensile strength was improved; however, introduction or incorporation of flax fibers showed a negative impact on this addition. The addition of flax fibers resulted in 16% reduced tensile strength of the composites. Conversely, composites of PP were improved with the incorporation of hemp, kenaf, and cotton [5]. By far, maximum improvement is only seen in such composites where jute or polyester has been incorporated where a total of 121% improvement is evident compared to pure polyester [5]. However, due to the rubber phase present in gum compound, a greater range of flexibility is present in such materials which results in reduced stiffness and storage modulus.It is also known that stiffness and stress transfer in composites increases with an increased or excessive addition of fiber which provides a better loss modulus and also a better storage modulus. The loss modulus is also considered to be increased with fiber addition up to 756 MPa at 50 phr fiber loading compared to the loss modulus of gum that is 415 MPa [8].A group of researchers led by Ismail et al. [37] studied the effect of size and filler content on fiber characteristics that cures a wound or any part of the body. Along with this, mechanical properties of Oil Palm Wood Flour (OPWF) was also examined which is reinforced with (ENR) epoxidized natural rubber composites. When the fiber content is increased, torque of the fibers is also increased and with smallest possible particle size of OPWF, highest torque was noticed. However, increasing the factor of OPWF in ENR compounds showed reduced tensile strength and while reaching the break point a considerable elongation is evident. It also evident increase in elongation, tear strength, tensile modulus and hardness due to higher loading of OPWF. A higher tensile strength and tear strength as tensile modulus were identified in composites that were filled with even smallest proportion of OPWF [10]. The fracture behavior of composites is also affected due to the nonlinear mechanical behavior of natural fibers, under the influence of tensile-shear loads [1]. Table 3 shows the mechanical properties for common types of natural fiber in the world [38].Table 3
Physicomechanical properties of natural fibers [38].
Fiber
Density (g/cm3)
Tensile strength (MPa)
Young’s modulus (GPa)
Elongation at break (%)
OPEFB
0.7–1.55
248
3.2
2.5
Flax
1.4
88–1500
60–80
1.2–1.6
Hemp
1.48
550–900
70
1.6
Jute
1.46
400–800
10–30
1.8
Ramie
1.5
500
44
2
Coir
1.25
220
6
15–25
Sisal
1.33
600–700
38
2-3
Abaca
1.5
980
—
—
Cotton
1.51
400
12
3–10
Kenaf (bast)
1.2
295
—
2.7–6.9
Kenaf (core)
0.21
—
—
—
Bagasse
1.2
20–290
19.7–27.1
1.1
Henequen
1.4
430–580
—
3–4.7
pineapple
1.5
170–1672
82
1–3
Banana
1.35
355
33.8
53The bonding strength between fiber and polymer matrix in the composite is consider a major factor in order to get superior fiber reinforcement composites properties. Because of pendant hydroxyl and polar groups in fiber, this leads to extremely high moisture absorption of fiber, resulting in weak interfacial bonding between the fiber and the hydrophobic matrix polymers. To develop composites with good mechanical properties, chemical modification of fibre carried out to reduce the hydrophilic behavior of fibers and the absorption of moisture [15, 39].The different surface treatments of advanced composites applications were reviewed by several researchers [40–42]. The effects of different chemical treatments on cellulosic fibers that were employed as reinforcements for thermoplastics and thermoset were also examined. For the treatments, the different kinds of chemical treatment include silane [43], alkali [44], acrylation [45], benzoylation [46], maleated coupling agents [47], permanganate [48], acrylonitrile and acetylation grafting [49], stearic acid [50], peroxide [51], isocyanate [52], triazine [53], fatty acid derivate (oleoyl chloride), sodium chloride, and fungal [9]. The main purpose of surface treatments of natural fibers to enhanced fibre/matrix interfacial bonding and stress transferability of the composites.The impact of alkaline treatment on surface properties of Iranian cultivated natural fibers was studied by Cordeiroa et al. [54]. The research revealed that alkaline treatment gets rid of some chemical components on the surface of the fibers, comprising uranic acid (hemicellulose), aromatic moieties (extractives), and nonpolar molecules from the partial lignin depolymerisation. There is a stronger effect on chemical components of nonwood fibers. Improving the crystallinity of nonwood fibers, in the softwood fibers result in only a minor increase. Hence, alkaline treatment can result in a remarkable improvement in the specific interaction of the fibers as well as improving the fibers’ wettability.Le Troedec et al. [55] revealed the effects of some chemical treatments, comprising ethylenediaminetetraacetic acid (EDTA), NaOH, polyethylene imine (PEI), CaCl2, and Ca(OH)2. The effects were on the mechanical properties of the composite materials from mixtures of hemp fiber and lime by differential thermal evaluation and tests. The observation was that every treatment had a direct effect on the fiber surface. The treatment was with 6% NaOH and led to cleaning fibers by removing the amorphous compounds, and the increase of the crystallinity index of fiber bundles, while the EDTA treatment led to separates fibers and complex calcium ions related to pectins. In brief, PEI treatment shows all studied properties an intermediate character and lime water treatment depicts calcium ions’ fixation at the surface of fibers in comparison to a calcium chloride treatment which does not.May-Pat et al. [1] reported on the impact of the interphase properties from well controlled surface treatment in the case of natural fibers. The fracture behavior and the mechanical properties of a NFPC depend on the properties of constituents and region of the fiber surface, or interphase, where the stress transfer occurs. Furthermore, the tailoring of the interphase by different kinds of surface treatments and carefully characterizing it provides a better knowledge of the behavior of the NFPCs. Moreover, different fiber surface treatments modify the natural fiber microstructure specifically under high loading rates.Venkateshwaran et al. [35] studied the effect of alkali (NaOH) treatments of various concentrations (0.5%, 1%, 2%, 5%, 10%, 15%, and 20%) on the mechanical properties of banana/epoxy composite. The results reported that as compared to other treated and untreated fiber composites, 1% NaOH treated fiber reinforced composites have a better properties. The alkali concentration on the fiber surfaces results in better mechanical properties of the resulted composite. However, the rising of alkali concentration maybe causes fiber surface damage, leading to a decrease of mechanical properties. The effect of different chemical treatment on the mechanical properties and characteristic of sisal-oil palm hybrid fiber reinforced natural rubber composites have been studied by John et al. [56]. With chemical treatment, the torque values increased which lead to greater crosslinking. Similarly, alkali treatment showed a rise in the composites’ tensile strength in comparison to untreated composites and with 4% NaOH treated fibers, optimum tensile strength was seen for resulted composites. In contrast, for composites treated with 4% NaOH a strong interface is apparent because of a more superior adhesion between rubber and fiber is present which avoids solvent entry and a little swelling occurs.Van de Weyenberg et al. [24] examined the impact of flax processing parameters, and the fiber treatment, on the mechanical properties of flax fiber reinforced epoxy composites. It was discovered that the employment of long flax slivers may not necessarily lead to more superior composite properties. The highest enhancement of the flexural properties of the flax fiber reinforced epoxy composites can be gotten by chemical treatments. There was an increase of transverse strength of up to 250% and transverse modulus, of up to 500%. In addition, the longitudinal properties of the UD composites (both modulus and strength) showed improvements with 40% or more.Some modifications in the chemical and physical properties of the lignocellulosic fibers can be observed after the treatment of the fiber of rubber wood with laccase enzymes. These chemical treatments lead to the amorphous lignin content, changing the hemicellulose content and ultimately the natural crystallinity [57]. The fiber has treatment effect on morphological and single fiber tensile strength of EFB fiber. The EFB fiber treated with boiling water, 2% sodium hydroxide (NaOH), and mixing of boiling water and NaOH was examined by Norul Izani et al. [13]. It was revealed that it changed the properties of the fiber surface topography after the treatment. Compared to untreated EFB fiber, the treated EFB fibers with the two types of treatment were more thermal stability. On the other hand, the tensile strength and Young’s modulus of the treated fiber showed a rise in comparison to untreated fibers. For tensile modulus, the alkaline treatment has enhanced the tensile properties of sugar palm fiber reinforced epoxy composites at better soaking times and concentrations of alkaline. On the other hand, the increase the alkaline concentration may lead to fiber damage [58].Acrylonitrile Butadiene Styrene (ABS) with the coating effect of OPEFB fibers was tested BT. The coated process enhanced the mechanical and physical properties and also improved the fiber performance. The ABS treatment led to reducing the water absorption and also decreased the biodegradation potential of the fiber in contact with soil. With the coating, the tensile strength and elasticity moduli of the OPEFB fibers became better than what they were in the past. The surface area between fiber and soil particles increased by coating fiber, which led to improving the shear strength parameters of the fiber reinforced soils [66].


### 3.2. Flame Retardant Properties of the NFPCs

Due to eco-friendly and sustainability nature, natural fiber composites prefers as compared to conventional synthetic fibre based composites. They are applied in diversified domains [9, 18, 20, 38, 67] such as building materials [68], aerospace industry, and automotive industry [69]. Natural fibers and polymers are organic materials and are very sensitive to alter any features if flame is introduced to them. Flame retardancy is another aspect that has become greatly significant in order to fulfill safety measures taken while developing natural fiber composites.In the presence of flame, burning of composites takes place in five different steps as shown below:(a)
Heating.
(b)
Decomposition.
(c)
Ignition.
(d)
Combustion.
(e)
Propagation [70].If flame retardancy has been achieved in the aforementioned steps, no matter whether ignition step has been conducted or not, the procedure will be terminated before an actual ignition is set up. There are two forms of products that are obtained upon burning of composites; these two include high cellulose content and high lignin content. High cellulose provides chances of higher flammability whereas higher values of lignin show there is a greater chance of char formation [71]. Thermal resistance is provided by flax fibers [72]; however, silica or ash is another important feature that is helpful in extinguishing fire [73].In order to enhance fire resistance of various NFPCs, different procedures are undertaken. Fire barriers are kind of barriers that can be applied to phenolics, ceramics, intumescents, glass mats, silicone, ablatives, and chemical additives too. Coatings and additives used in the system of intumescent are found to be very promising fire barrier treatments in which these barriers are expanded upon heating resulting in a cellular surface that is charred even. However, with the help of this charred surface, internal or underlying components and protected against flux and heat.One of the well-known or profound flame retardants for reinforced polymers (natural fibers) is used with the combination of char developing cellulose material [74]. The only method of reducing combustion in this scenario is through increasing stability and char formation in the polymer. This will result in reduced flammability, decrease visible smoke, and restrict the volume of products produced due to combustions [72]. Fire retardant coating is another method that helps in enhancement of fire resistance property of composites. This coating is done at the end or finishing stage or impregnation. Due to changes in the fibers and lingo-cellulosic particles, fire resistance is altered during the process of manufacturing [75].The two most widely used metal hydroxide flame retardants are known to be aluminum hydroxide [Al(OH3)] and magnesium hydroxide [Mg(OH)2] which are purposefully added to polymers. The chemical reaction through which these two flame retardants decompose are as follows:(1)
2
Al
OH
3
⟶
Al
2
O
3
+
3
H
2
O
Δ
H
=
20
cal
/
g
(2)
Mg
OH
2
⟶
MgO
+
H
2
O
Δ
H
=
328
cal
/
gOut of these two flame retardants, magnesium hydroxide display better thermal stability as compared to aluminum hydroxide since the temperature range given off by the decomposition of magnesium hydroxide is nearly 300–320 degrees centigrade (°C) which is much higher than the temperature range offered by aluminum hydroxide that is only 200°C. For this reason, aluminum hydroxide is not considered to be thermally stable as it cannot be used for polyamides, polypropylene, or others whereas magnesium hydroxide can be used.It was also shown in a research that the addition of expandable graphite (EG) and ammonium polyphosphate (APP) in composite polymer as a source of flame retardant (FR) helps in enhancing flax fiber reinforced PP composite’s property of fire retardancy. It was also shown that heat release rate (HRR) in a composite additive of 30 wt% of flax fiber and 25 wt% of EG (expandable graphite) was decreased to 35 from 167 kW/m2 [76].Spirocyclic pentaerythritol bisphosphorate disphosphoryl melamine (SPDPM) is a type of intumescent flame retardant for PLA that was studied by Zhan et al. [77]. Char formation that is a result of spirocyclic pentaerythritol bisphosphorate disphosphoryl melamine (SPDPM), an active component of flame retardancy, enhances antidripping performance of PLA and flame retardancy too with an addition of 25 wt%. Flame retardancy is not an easy thing to be imparted and it is only possible if there is an extensive high loading of inorganic filler.Hapuarachchi and Peijs [78] studied the development of fully bio-based natural fiber composite that has enhanced features of fire or flame retardancy. This natural fiber composite was developed with the help of PLA polymers that were derived from crops accompanied with 2 kinds of nanofillers which are able to produce synergy corresponding to flame retardancy. Upon analysis, after incorporating hemp fiber mat in PLA resin, decrease in PHRR (peak heat release) in calorimeter will be shown.


### 3.3. Biodegradability of the NFPCs

High strength composites are resultant products of natural fiber reinforcement in polymers which also provide extra or improved biodegradability, low cost, light weight, and enhanced properties related to mechanical structure [29]. At temperatures as high as 240°C, natural fibers start degrading whereas constituents of fiber, such as hemicelluloses, cellulose, lignin, and others, start degrading at different levels of temperature; for example, at 200°C lignin starts to decompose whereas at temperatures higher than this other constituents will also degrade [9].Since thermal stability of the fibers is dependent on the structural constituents of fibers, it can be improved if the concentration levels or the structural constituents are completely removed, such as lignin and hemicelluloses. This can be achieved with the help of chemical treatments. Development of fibers and materials that provide services are two important aspects which should be considered while degradating natural fibers [9]. Natural fibers have a short lifetime with minimum environmental damage upon degradation whereas synthetic ones affect environment due to pollution caused by degradation. Lignin, hemicelluloses, and cellulose concentrations or composition affect thermal degradation features of lingo-cellulosic materials [13]. More than fifty percent weight of jute or Biopol composite is lost after exactly 1500 days of burial [21].


### 3.4. Energy Absorption of the NFPCs

High strength, energy absorption, and stiffness are obtained by composite materials which are widely used in automotive and motorsport sectors of industry mainly due to the property of mass reduction [79]. Enhanced energy absorption is evident from the increased volume fraction that is only possible in the presence of low speed such as 2.5 m/s [80]. On the other hand, at high speeds, such as 300 m/s, similar performance is shown by flax, jute, and hemp, but jute showed brittleness and low strength of fibers [81]. Potential of NFPCs that is required for application in providing sustainable energy absorption was investigated by Meredith et al. While keeping focus on motorsport [80]. Vacuum Assisted Resin Transfer Molding (VARTM) technique is used to test conical specimens of flax, jute, and hemp for their properties and features. Various values exhibited by different kinds of materials were recorded to analyze specific energy absorption (SEA).


### 3.5. Tribology Properties of NFPCs

Since every material has some wear and friction properties that degrade with respect to time, the tribological loadings are important to consider for an improved mechanical part design [5]. Around 90% failure is obtained due to differences in tribological loading conditions which alters their wear and friction properties [82]. Reinforcement is a method with which fiber’s or polymers tribological properties are altered (either positively or negatively) [83]. Studies on different kinds of tribological analysis have been conducted on fibers including kenaf/epoxy [84], betelnut fiber reinforced polyester [85], sisal/phenolic resin [86], sugarcane fiber reinforced polyester (SCRP) [87], and cotton/polyester [88]. Improvement in wear performance of PLA was evident due to the addition of natural fibers in which wear rate of composites was quite low in comparison to wear rate at higher loads on neat PLA [82].Kenaf fibers reinforced with epoxy composite were used by Chin and Yousif [84] for a kind of bearing application, in which they showed an 85% enhancement of wear performance and normal orientation in composites. Wear and friction features of glass fiber/polyester (GRP) and sugarcane fiber/polyester (SCRP) were studied by El-Tayeb with different parameters including speed, the time taken for test, and load [87]. The research results concluded SCRP as a competitor of GRP composite. The same characteristics were studied by Xin et al. [86] for sisal fiber reinforced resin brake composites which showed sisal fiber can be used instead of asbestos in brake pads [89, 90].Laminated composites were developed with the help of three different natural fibers such as grewia, nettle, optiva, and sisal. This connection of natural fibers was studied by Bajpai et al. in which a hot compression procedure was used to incorporate three different materials in a PLA polymer [82]. Friction and wear features of composites were examined under different situations such as dry contact condition with varying operating parameters. Due to an option of variable operating parameters, applied load was varied in between range of 10 to 30 N with a speed ranging from 1 to 3 m/s and sliding distance of thousand to three thousand meters. The research results showed infusion of natural fiber mats, in PLA matrix, is capable of enhancing wear and frictional behavior of neat polymers. An approximate reduction of 10–44% in the coefficient of friction with a greater reduction of 70% seen in developed composites for specific wear rate is visualized in comparison to neat PLA [82].


### 3.6. Water Absorption Characteristics of the NFPCs

Natural fibers work well as reinforcement in polymers. However, the main weakness of the application of natural fibers is their susceptibility to moisture [91]. Mechanical properties of polymeric composites have a strong dependence on the interface adhesion between the fiber and the polymer matrix [15]. The natural fibers are rich of cellulose, hemicelluloses, lignin, and pectins, all of which are hydroxy 1 groups; that is, they are usually hydrophilic sources and strong polar whilst polymers show considerable hydrophobicity. Thus, there are major challenges of suitability between the matrix and fiber that weakens interface region between matrices and natural fibers [5]. At the composite materials’ outer layers, water absorption happens and decreases gradually into the bulk of the matrix. A generally high water intake by composite materials results in an increased weight of wet profiles, a conceivable decline in their strength, and increment in their deflection, swelling, and causing pressure on nearby structures. These can cause warping, buckling, bigger possibility of their microbial inhabitation, freeze, and unfreeze caused destruction of mechanical characteristics of composite materials [92].Oil palm fiber natural rubber (OPF-NR) composites increased in the water absorption percentage corresponding to an increase in fiber loading because of the fibers’ hydrophilicity. The absorption behavior of NR showed modifications from Fickian to non-Fickian with additional OPF because of the microcracks and the viscoelastic nature of the polymer [8]. In the woven pandanus/banana fabric composites tests, woven pandanus fabric composites increased the water uptake compared to woven banana fabric composites because of higher lignin content and hemicellulose, as well as the presence of defects in the composite system [93]. Furthermore, temperature can affect the percentage of water absorption of the composites. At 65% humidity at 21°C, the equilibrium moisture content of some natural fiber can be observed in Table 4 [4]. It was revealed that the water absorption of OPF-NR composite was less than of OPF-sisal fiber-NR hybrid biocomposite. The incorporation of sisal fiber that contains relatively more holocellulose (23%), which is exceptionally hydrophilic brought on more water intake. Besides, the lignin content material of OPF (19%) was bigger than sisal fiber (9%). Lignin being hydrophobic reduces the water absorption [8].Table 4
The equilibrium moisture content of different natural fiber at 65% relative humidity (RH) and 21°C [4].
Fiber
Equilibrium moisture content (%)
Sisal
11
Hemp
9.0
Jute
12
Flax
7
Abaca
15
Ramie
9
Pineapple
13
Coir
10
Bagasse
8.8
Bamboo
8.9Many researchers [8, 56] showed the effect of coupling agent such as maleic anhydride polyethylene and chemical treatments such as bleaching, acetylation, and alkali treatment on reduction moisture absorption of NFPCs. The surface of the fibers is cleaned during the chemical treatments to ensure there are no impurities which increases the fiber surface roughness and preventing the moisture absorption via the removal of the coat of OH groups of fiber as seen in equation below [5, 9]: (3)
Fiber-OH
+
NaOH
⟶
Fiber-
O
-
Na
+
+
H
2
OSreekala and Thomas [91] investigated the moisture absorption properties of OPEFB fiber in different temperature condition. They also studied the effect of different modification on OPEFB fiber, such as silane treatment, gamma irradiation, latex coating, mercerization, acetylation, peroxide treatment, and isocyanate treatment on moisture absorption properties. They concluded that all the treatment causes the seduction in moisture absorption properties in all temperatures.The mercerization of OPF-sisal fiber-NR hybrid composites led to reducing water adsorption of the composite by improving the adhesive characteristics of fiber surface and also providing a large surface area which causes better mechanical interlocking [94]. Shinoj et al. [8] conducted the effect of chemical treatment for agave fibers on moisture adsorption before blending in a polymer matrix. The chemical treatment is achieved using four types of reagents, acetic anhydride (Ac), maleic anhydride (MA), styrene (S), and acrylic acid (AA). This paper concludes that the chemical treatment causes decrease in the global diffusivity of water and also concludes that the water mobility in the fiber core is more than at the surface.


### 3.7. Viscoelastic Behavior of the NFPCs

Dynamic mechanical measurements or the viscoelastic behavior over a range of temperatures provides valuable insight into the structure, morphology, and determination of the interface characteristics of natural fiber composite materials [95]. Storage modulus gives an insight into the load bearing capability and the stiffness behavior of natural fiber composite materials. Storage modulus is a measure of the maximum energy stored in the material during one cycle of oscillation. The mechanical damping coefficient is the ratio of the loss modulus to the storage modulus and is related to the degree of molecular mobility in the polymeric material. On the other hand, loss modulus is proportional to the amount of energy dissipated as heat by the sample [96].The viscoelastic behavior of novel commingled biocomposites based on polypropylene/jute yarns is reported by [96]. By using commingling method, jute yarn reinforced polypropylene commingled composites were prepared. The viscoelastic behavior or dynamic mechanical properties of the result commingled composites were studied according to the fiber content and different kinds of chemical treatments such as potassium permanganate (KMnO4), maleic anhydride modified polypropylene (MAPP), toluene diisocyanate (TDI), and stearic acid (ST). This study concluded that increasing of fiber content leads to increasing the storage and loss modulus of the composite. On the other hand, at all temperatures, the chemical treatment by KMnO4 and MAPP leads to increasing the storage modulus and loss modulus of the respective treated composites than the untreated ones.By using the dynamic mechanical analyzer, Venkateshwaran et al. [35] studied the impact of alkali treatments on the viscoelastic behavior of natural fiber composite. The corresponding viscoelastic properties were determined as a function of temperature and frequency when the measurements were executed in the tensile mode of the used equipment. At the temperature range of 30–140°C at 0.1, 1, and 10 Hz frequencies, respectively, the experiments executed the graphs plotted, as storage modulus (E−) versus temperature and tan
⁡
δ versus temperature, as shown in Figures 2 and 3 [35].Figure 2
tan
⁡
δ versus temperature curves of the alkali treated and untreated composites at 1 Hz frequency [35].Figure 3
tan
⁡
δ versus temperature curves of alkali treated and untreated composites [35].


### 3.8. Relaxation Behavior of the NFPCs

Natural fiber possesses an intrinsic relaxation behavior which has a main function in the stress relaxation of NFPCs. Thus, the tensile stress relaxation of the reinforcing fiber needs to be studied in detail [38]. Sreekala et al. [29], for instance, did such a study focusing on the character of individual OPEFB fiber and, in addition, examined the fiber surface modification effects, ageing, and strain level on the fiber relaxation behavior. The fibers stress relaxation was lessened significantly with surface treatments, like latex modification, and thus decreasing resulting physical interaction between the latex particles and fiber surface. Also, water and thermal ageing reduce the rate of relaxation for the oil palm fiber; the rate of stress relaxation of the OPEFB fiber was optimized at 10% strain level which is shown in Figure 4, while the relaxation modulus values for the fiber show similar trends as in the case of stress relaxation as shown in Figure 5. On the other hand, the stress relaxation rate of OPF-sisal fiber-NR hybrid composites showed a reduction with an increase in fiber percentage [97].Figure 4
Stress relaxation curves of untreated and treated OPEFB fiber at 10% strain [29].Figure 5
Relaxation modulus curves of untreated and treated OPEFB fiber at 10% strain [29].


### 3.9. Thermal Properties of NFPCs

The untreated OPFs are thermally more stable when compared with treated ones, while OPF is considered thermally more stable compared to flax fibers and hemp fibers. Increase of temperatures from 20°C to 150°C causes increase of the heat capability of OPFs particularly from 1.083J
g
-
1
°
C
-
1 to 3.317 J
g
-
1
°
C
-
1 [98]. The thermal diffusivity, thermal conductivity, and specific heat of the flax/HDPE composites lessened with a rise in fiber composition. However, the thermal conductivity and thermal diffusivity showed no significant changes in the range of 170–200°C. The biocomposites’ specific heat showed gradual increase with temperature [4]. By using polycarbonate to generate functional composites, pineapple leaf fiber was the support. The changed pineapple leaf fibers composite, treated with silane, showed the impact strengths and highest tensile. The composites’ thermal stability is lower than the neat polycarbonate resin according to the thermogravimetric examination. Besides that, the thermal stability lessened with a rise in pineapple leaf fiber composition [4].Enzymatic treatment for many natural fibers such as flax and hemp often natural fibers can lead to improvement in surface and thermal properties [56]. Hemicellulose and pectinase are the treatments which can improve the thermal properties of the fibers mentioned. The enzymes possess an attractive state for the improvement of the natural fibers’ surfaces for natural fiber composite application [67].Norul Izani et al. [13] studied the effect of chemical treatment on the morphological and tensile strength of the EFB fiber. The treatments were by the types of treatments, 2% sodium hydroxide (NaOH) and combination of both NaOH and boiling water. The chemical treatment by NaOH led to enhancing the fiber surface topography, thermal stability, and tensile strength of the fiber, while the chemical treatment using NaOH and water boiling caused the higher thermal properties of the EFB fibers compared to untreated fibers.


## 3.1. Mechanical Properties of the NFPCs

There are considerable enhancement and suggestions for the natural fibers that can be implemented in order to enhance their mechanical properties resulting in high strength and structure. Once the base structures are made strong, the polymers can be easily strengthened and improved [26]. There are number of aspects that effects of composite are performance level or activities, of which to name a few are the following;(a)
orientation of fiber [5],
(b)
strength of fibers [8],
(c)
physical properties of fibers [27],
(d)
interfacial adhesion property of fibers [28] and many more.NFPCs are such composites whose mechanical efficiency is dependent upon the interface provided by fiber-matrix along with the stress transfer function in which stress is transferred to fiber from matrix. This has been reported by many investigators in several researches [1, 23, 29]. Characteristic components of natural fibers such as orientation [30], moisture absorption [31], impurities [32], physical properties [33], and volume fraction [34] are such features that play a constitutive role in the determination of NFPCs mechanical properties. Mechanical properties of PLA, epoxy, PP, and polyester matrices can be affected by many types of natural fibers and to show some of them, Figure 1 is included.Figure 1
Some of mechanical properties of natural fiber reinforced polymer composite [5].NFPCs show even better mechanical properties than a pure matrix in cases where jute fibers are added in PLA (polylactic-acid); in this case, 75.8% of PLA’s tensile strength was improved; however, introduction or incorporation of flax fibers showed a negative impact on this addition. The addition of flax fibers resulted in 16% reduced tensile strength of the composites. Conversely, composites of PP were improved with the incorporation of hemp, kenaf, and cotton [5]. By far, maximum improvement is only seen in such composites where jute or polyester has been incorporated where a total of 121% improvement is evident compared to pure polyester [5]. However, due to the rubber phase present in gum compound, a greater range of flexibility is present in such materials which results in reduced stiffness and storage modulus.It is also known that stiffness and stress transfer in composites increases with an increased or excessive addition of fiber which provides a better loss modulus and also a better storage modulus. The loss modulus is also considered to be increased with fiber addition up to 756 MPa at 50 phr fiber loading compared to the loss modulus of gum that is 415 MPa [8].A group of researchers led by Ismail et al. [37] studied the effect of size and filler content on fiber characteristics that cures a wound or any part of the body. Along with this, mechanical properties of Oil Palm Wood Flour (OPWF) was also examined which is reinforced with (ENR) epoxidized natural rubber composites. When the fiber content is increased, torque of the fibers is also increased and with smallest possible particle size of OPWF, highest torque was noticed. However, increasing the factor of OPWF in ENR compounds showed reduced tensile strength and while reaching the break point a considerable elongation is evident. It also evident increase in elongation, tear strength, tensile modulus and hardness due to higher loading of OPWF. A higher tensile strength and tear strength as tensile modulus were identified in composites that were filled with even smallest proportion of OPWF [10]. The fracture behavior of composites is also affected due to the nonlinear mechanical behavior of natural fibers, under the influence of tensile-shear loads [1]. Table 3 shows the mechanical properties for common types of natural fiber in the world [38].Table 3
Physicomechanical properties of natural fibers [38].
Fiber
Density (g/cm3)
Tensile strength (MPa)
Young’s modulus (GPa)
Elongation at break (%)
OPEFB
0.7–1.55
248
3.2
2.5
Flax
1.4
88–1500
60–80
1.2–1.6
Hemp
1.48
550–900
70
1.6
Jute
1.46
400–800
10–30
1.8
Ramie
1.5
500
44
2
Coir
1.25
220
6
15–25
Sisal
1.33
600–700
38
2-3
Abaca
1.5
980
—
—
Cotton
1.51
400
12
3–10
Kenaf (bast)
1.2
295
—
2.7–6.9
Kenaf (core)
0.21
—
—
—
Bagasse
1.2
20–290
19.7–27.1
1.1
Henequen
1.4
430–580
—
3–4.7
pineapple
1.5
170–1672
82
1–3
Banana
1.35
355
33.8
53The bonding strength between fiber and polymer matrix in the composite is consider a major factor in order to get superior fiber reinforcement composites properties. Because of pendant hydroxyl and polar groups in fiber, this leads to extremely high moisture absorption of fiber, resulting in weak interfacial bonding between the fiber and the hydrophobic matrix polymers. To develop composites with good mechanical properties, chemical modification of fibre carried out to reduce the hydrophilic behavior of fibers and the absorption of moisture [15, 39].The different surface treatments of advanced composites applications were reviewed by several researchers [40–42]. The effects of different chemical treatments on cellulosic fibers that were employed as reinforcements for thermoplastics and thermoset were also examined. For the treatments, the different kinds of chemical treatment include silane [43], alkali [44], acrylation [45], benzoylation [46], maleated coupling agents [47], permanganate [48], acrylonitrile and acetylation grafting [49], stearic acid [50], peroxide [51], isocyanate [52], triazine [53], fatty acid derivate (oleoyl chloride), sodium chloride, and fungal [9]. The main purpose of surface treatments of natural fibers to enhanced fibre/matrix interfacial bonding and stress transferability of the composites.The impact of alkaline treatment on surface properties of Iranian cultivated natural fibers was studied by Cordeiroa et al. [54]. The research revealed that alkaline treatment gets rid of some chemical components on the surface of the fibers, comprising uranic acid (hemicellulose), aromatic moieties (extractives), and nonpolar molecules from the partial lignin depolymerisation. There is a stronger effect on chemical components of nonwood fibers. Improving the crystallinity of nonwood fibers, in the softwood fibers result in only a minor increase. Hence, alkaline treatment can result in a remarkable improvement in the specific interaction of the fibers as well as improving the fibers’ wettability.Le Troedec et al. [55] revealed the effects of some chemical treatments, comprising ethylenediaminetetraacetic acid (EDTA), NaOH, polyethylene imine (PEI), CaCl2, and Ca(OH)2. The effects were on the mechanical properties of the composite materials from mixtures of hemp fiber and lime by differential thermal evaluation and tests. The observation was that every treatment had a direct effect on the fiber surface. The treatment was with 6% NaOH and led to cleaning fibers by removing the amorphous compounds, and the increase of the crystallinity index of fiber bundles, while the EDTA treatment led to separates fibers and complex calcium ions related to pectins. In brief, PEI treatment shows all studied properties an intermediate character and lime water treatment depicts calcium ions’ fixation at the surface of fibers in comparison to a calcium chloride treatment which does not.May-Pat et al. [1] reported on the impact of the interphase properties from well controlled surface treatment in the case of natural fibers. The fracture behavior and the mechanical properties of a NFPC depend on the properties of constituents and region of the fiber surface, or interphase, where the stress transfer occurs. Furthermore, the tailoring of the interphase by different kinds of surface treatments and carefully characterizing it provides a better knowledge of the behavior of the NFPCs. Moreover, different fiber surface treatments modify the natural fiber microstructure specifically under high loading rates.Venkateshwaran et al. [35] studied the effect of alkali (NaOH) treatments of various concentrations (0.5%, 1%, 2%, 5%, 10%, 15%, and 20%) on the mechanical properties of banana/epoxy composite. The results reported that as compared to other treated and untreated fiber composites, 1% NaOH treated fiber reinforced composites have a better properties. The alkali concentration on the fiber surfaces results in better mechanical properties of the resulted composite. However, the rising of alkali concentration maybe causes fiber surface damage, leading to a decrease of mechanical properties. The effect of different chemical treatment on the mechanical properties and characteristic of sisal-oil palm hybrid fiber reinforced natural rubber composites have been studied by John et al. [56]. With chemical treatment, the torque values increased which lead to greater crosslinking. Similarly, alkali treatment showed a rise in the composites’ tensile strength in comparison to untreated composites and with 4% NaOH treated fibers, optimum tensile strength was seen for resulted composites. In contrast, for composites treated with 4% NaOH a strong interface is apparent because of a more superior adhesion between rubber and fiber is present which avoids solvent entry and a little swelling occurs.Van de Weyenberg et al. [24] examined the impact of flax processing parameters, and the fiber treatment, on the mechanical properties of flax fiber reinforced epoxy composites. It was discovered that the employment of long flax slivers may not necessarily lead to more superior composite properties. The highest enhancement of the flexural properties of the flax fiber reinforced epoxy composites can be gotten by chemical treatments. There was an increase of transverse strength of up to 250% and transverse modulus, of up to 500%. In addition, the longitudinal properties of the UD composites (both modulus and strength) showed improvements with 40% or more.Some modifications in the chemical and physical properties of the lignocellulosic fibers can be observed after the treatment of the fiber of rubber wood with laccase enzymes. These chemical treatments lead to the amorphous lignin content, changing the hemicellulose content and ultimately the natural crystallinity [57]. The fiber has treatment effect on morphological and single fiber tensile strength of EFB fiber. The EFB fiber treated with boiling water, 2% sodium hydroxide (NaOH), and mixing of boiling water and NaOH was examined by Norul Izani et al. [13]. It was revealed that it changed the properties of the fiber surface topography after the treatment. Compared to untreated EFB fiber, the treated EFB fibers with the two types of treatment were more thermal stability. On the other hand, the tensile strength and Young’s modulus of the treated fiber showed a rise in comparison to untreated fibers. For tensile modulus, the alkaline treatment has enhanced the tensile properties of sugar palm fiber reinforced epoxy composites at better soaking times and concentrations of alkaline. On the other hand, the increase the alkaline concentration may lead to fiber damage [58].Acrylonitrile Butadiene Styrene (ABS) with the coating effect of OPEFB fibers was tested BT. The coated process enhanced the mechanical and physical properties and also improved the fiber performance. The ABS treatment led to reducing the water absorption and also decreased the biodegradation potential of the fiber in contact with soil. With the coating, the tensile strength and elasticity moduli of the OPEFB fibers became better than what they were in the past. The surface area between fiber and soil particles increased by coating fiber, which led to improving the shear strength parameters of the fiber reinforced soils [66].


## 3.2. Flame Retardant Properties of the NFPCs

Due to eco-friendly and sustainability nature, natural fiber composites prefers as compared to conventional synthetic fibre based composites. They are applied in diversified domains [9, 18, 20, 38, 67] such as building materials [68], aerospace industry, and automotive industry [69]. Natural fibers and polymers are organic materials and are very sensitive to alter any features if flame is introduced to them. Flame retardancy is another aspect that has become greatly significant in order to fulfill safety measures taken while developing natural fiber composites.In the presence of flame, burning of composites takes place in five different steps as shown below:(a)
Heating.
(b)
Decomposition.
(c)
Ignition.
(d)
Combustion.
(e)
Propagation [70].If flame retardancy has been achieved in the aforementioned steps, no matter whether ignition step has been conducted or not, the procedure will be terminated before an actual ignition is set up. There are two forms of products that are obtained upon burning of composites; these two include high cellulose content and high lignin content. High cellulose provides chances of higher flammability whereas higher values of lignin show there is a greater chance of char formation [71]. Thermal resistance is provided by flax fibers [72]; however, silica or ash is another important feature that is helpful in extinguishing fire [73].In order to enhance fire resistance of various NFPCs, different procedures are undertaken. Fire barriers are kind of barriers that can be applied to phenolics, ceramics, intumescents, glass mats, silicone, ablatives, and chemical additives too. Coatings and additives used in the system of intumescent are found to be very promising fire barrier treatments in which these barriers are expanded upon heating resulting in a cellular surface that is charred even. However, with the help of this charred surface, internal or underlying components and protected against flux and heat.One of the well-known or profound flame retardants for reinforced polymers (natural fibers) is used with the combination of char developing cellulose material [74]. The only method of reducing combustion in this scenario is through increasing stability and char formation in the polymer. This will result in reduced flammability, decrease visible smoke, and restrict the volume of products produced due to combustions [72]. Fire retardant coating is another method that helps in enhancement of fire resistance property of composites. This coating is done at the end or finishing stage or impregnation. Due to changes in the fibers and lingo-cellulosic particles, fire resistance is altered during the process of manufacturing [75].The two most widely used metal hydroxide flame retardants are known to be aluminum hydroxide [Al(OH3)] and magnesium hydroxide [Mg(OH)2] which are purposefully added to polymers. The chemical reaction through which these two flame retardants decompose are as follows:(1)
2
Al
OH
3
⟶
Al
2
O
3
+
3
H
2
O
Δ
H
=
20
cal
/
g
(2)
Mg
OH
2
⟶
MgO
+
H
2
O
Δ
H
=
328
cal
/
gOut of these two flame retardants, magnesium hydroxide display better thermal stability as compared to aluminum hydroxide since the temperature range given off by the decomposition of magnesium hydroxide is nearly 300–320 degrees centigrade (°C) which is much higher than the temperature range offered by aluminum hydroxide that is only 200°C. For this reason, aluminum hydroxide is not considered to be thermally stable as it cannot be used for polyamides, polypropylene, or others whereas magnesium hydroxide can be used.It was also shown in a research that the addition of expandable graphite (EG) and ammonium polyphosphate (APP) in composite polymer as a source of flame retardant (FR) helps in enhancing flax fiber reinforced PP composite’s property of fire retardancy. It was also shown that heat release rate (HRR) in a composite additive of 30 wt% of flax fiber and 25 wt% of EG (expandable graphite) was decreased to 35 from 167 kW/m2 [76].Spirocyclic pentaerythritol bisphosphorate disphosphoryl melamine (SPDPM) is a type of intumescent flame retardant for PLA that was studied by Zhan et al. [77]. Char formation that is a result of spirocyclic pentaerythritol bisphosphorate disphosphoryl melamine (SPDPM), an active component of flame retardancy, enhances antidripping performance of PLA and flame retardancy too with an addition of 25 wt%. Flame retardancy is not an easy thing to be imparted and it is only possible if there is an extensive high loading of inorganic filler.Hapuarachchi and Peijs [78] studied the development of fully bio-based natural fiber composite that has enhanced features of fire or flame retardancy. This natural fiber composite was developed with the help of PLA polymers that were derived from crops accompanied with 2 kinds of nanofillers which are able to produce synergy corresponding to flame retardancy. Upon analysis, after incorporating hemp fiber mat in PLA resin, decrease in PHRR (peak heat release) in calorimeter will be shown.


## 3.3. Biodegradability of the NFPCs

High strength composites are resultant products of natural fiber reinforcement in polymers which also provide extra or improved biodegradability, low cost, light weight, and enhanced properties related to mechanical structure [29]. At temperatures as high as 240°C, natural fibers start degrading whereas constituents of fiber, such as hemicelluloses, cellulose, lignin, and others, start degrading at different levels of temperature; for example, at 200°C lignin starts to decompose whereas at temperatures higher than this other constituents will also degrade [9].Since thermal stability of the fibers is dependent on the structural constituents of fibers, it can be improved if the concentration levels or the structural constituents are completely removed, such as lignin and hemicelluloses. This can be achieved with the help of chemical treatments. Development of fibers and materials that provide services are two important aspects which should be considered while degradating natural fibers [9]. Natural fibers have a short lifetime with minimum environmental damage upon degradation whereas synthetic ones affect environment due to pollution caused by degradation. Lignin, hemicelluloses, and cellulose concentrations or composition affect thermal degradation features of lingo-cellulosic materials [13]. More than fifty percent weight of jute or Biopol composite is lost after exactly 1500 days of burial [21].


## 3.4. Energy Absorption of the NFPCs

High strength, energy absorption, and stiffness are obtained by composite materials which are widely used in automotive and motorsport sectors of industry mainly due to the property of mass reduction [79]. Enhanced energy absorption is evident from the increased volume fraction that is only possible in the presence of low speed such as 2.5 m/s [80]. On the other hand, at high speeds, such as 300 m/s, similar performance is shown by flax, jute, and hemp, but jute showed brittleness and low strength of fibers [81]. Potential of NFPCs that is required for application in providing sustainable energy absorption was investigated by Meredith et al. While keeping focus on motorsport [80]. Vacuum Assisted Resin Transfer Molding (VARTM) technique is used to test conical specimens of flax, jute, and hemp for their properties and features. Various values exhibited by different kinds of materials were recorded to analyze specific energy absorption (SEA).


## 3.5. Tribology Properties of NFPCs

Since every material has some wear and friction properties that degrade with respect to time, the tribological loadings are important to consider for an improved mechanical part design [5]. Around 90% failure is obtained due to differences in tribological loading conditions which alters their wear and friction properties [82]. Reinforcement is a method with which fiber’s or polymers tribological properties are altered (either positively or negatively) [83]. Studies on different kinds of tribological analysis have been conducted on fibers including kenaf/epoxy [84], betelnut fiber reinforced polyester [85], sisal/phenolic resin [86], sugarcane fiber reinforced polyester (SCRP) [87], and cotton/polyester [88]. Improvement in wear performance of PLA was evident due to the addition of natural fibers in which wear rate of composites was quite low in comparison to wear rate at higher loads on neat PLA [82].Kenaf fibers reinforced with epoxy composite were used by Chin and Yousif [84] for a kind of bearing application, in which they showed an 85% enhancement of wear performance and normal orientation in composites. Wear and friction features of glass fiber/polyester (GRP) and sugarcane fiber/polyester (SCRP) were studied by El-Tayeb with different parameters including speed, the time taken for test, and load [87]. The research results concluded SCRP as a competitor of GRP composite. The same characteristics were studied by Xin et al. [86] for sisal fiber reinforced resin brake composites which showed sisal fiber can be used instead of asbestos in brake pads [89, 90].Laminated composites were developed with the help of three different natural fibers such as grewia, nettle, optiva, and sisal. This connection of natural fibers was studied by Bajpai et al. in which a hot compression procedure was used to incorporate three different materials in a PLA polymer [82]. Friction and wear features of composites were examined under different situations such as dry contact condition with varying operating parameters. Due to an option of variable operating parameters, applied load was varied in between range of 10 to 30 N with a speed ranging from 1 to 3 m/s and sliding distance of thousand to three thousand meters. The research results showed infusion of natural fiber mats, in PLA matrix, is capable of enhancing wear and frictional behavior of neat polymers. An approximate reduction of 10–44% in the coefficient of friction with a greater reduction of 70% seen in developed composites for specific wear rate is visualized in comparison to neat PLA [82].


## 3.6. Water Absorption Characteristics of the NFPCs

Natural fibers work well as reinforcement in polymers. However, the main weakness of the application of natural fibers is their susceptibility to moisture [91]. Mechanical properties of polymeric composites have a strong dependence on the interface adhesion between the fiber and the polymer matrix [15]. The natural fibers are rich of cellulose, hemicelluloses, lignin, and pectins, all of which are hydroxy 1 groups; that is, they are usually hydrophilic sources and strong polar whilst polymers show considerable hydrophobicity. Thus, there are major challenges of suitability between the matrix and fiber that weakens interface region between matrices and natural fibers [5]. At the composite materials’ outer layers, water absorption happens and decreases gradually into the bulk of the matrix. A generally high water intake by composite materials results in an increased weight of wet profiles, a conceivable decline in their strength, and increment in their deflection, swelling, and causing pressure on nearby structures. These can cause warping, buckling, bigger possibility of their microbial inhabitation, freeze, and unfreeze caused destruction of mechanical characteristics of composite materials [92].Oil palm fiber natural rubber (OPF-NR) composites increased in the water absorption percentage corresponding to an increase in fiber loading because of the fibers’ hydrophilicity. The absorption behavior of NR showed modifications from Fickian to non-Fickian with additional OPF because of the microcracks and the viscoelastic nature of the polymer [8]. In the woven pandanus/banana fabric composites tests, woven pandanus fabric composites increased the water uptake compared to woven banana fabric composites because of higher lignin content and hemicellulose, as well as the presence of defects in the composite system [93]. Furthermore, temperature can affect the percentage of water absorption of the composites. At 65% humidity at 21°C, the equilibrium moisture content of some natural fiber can be observed in Table 4 [4]. It was revealed that the water absorption of OPF-NR composite was less than of OPF-sisal fiber-NR hybrid biocomposite. The incorporation of sisal fiber that contains relatively more holocellulose (23%), which is exceptionally hydrophilic brought on more water intake. Besides, the lignin content material of OPF (19%) was bigger than sisal fiber (9%). Lignin being hydrophobic reduces the water absorption [8].Table 4
The equilibrium moisture content of different natural fiber at 65% relative humidity (RH) and 21°C [4].
Fiber
Equilibrium moisture content (%)
Sisal
11
Hemp
9.0
Jute
12
Flax
7
Abaca
15
Ramie
9
Pineapple
13
Coir
10
Bagasse
8.8
Bamboo
8.9Many researchers [8, 56] showed the effect of coupling agent such as maleic anhydride polyethylene and chemical treatments such as bleaching, acetylation, and alkali treatment on reduction moisture absorption of NFPCs. The surface of the fibers is cleaned during the chemical treatments to ensure there are no impurities which increases the fiber surface roughness and preventing the moisture absorption via the removal of the coat of OH groups of fiber as seen in equation below [5, 9]: (3)
Fiber-OH
+
NaOH
⟶
Fiber-
O
-
Na
+
+
H
2
OSreekala and Thomas [91] investigated the moisture absorption properties of OPEFB fiber in different temperature condition. They also studied the effect of different modification on OPEFB fiber, such as silane treatment, gamma irradiation, latex coating, mercerization, acetylation, peroxide treatment, and isocyanate treatment on moisture absorption properties. They concluded that all the treatment causes the seduction in moisture absorption properties in all temperatures.The mercerization of OPF-sisal fiber-NR hybrid composites led to reducing water adsorption of the composite by improving the adhesive characteristics of fiber surface and also providing a large surface area which causes better mechanical interlocking [94]. Shinoj et al. [8] conducted the effect of chemical treatment for agave fibers on moisture adsorption before blending in a polymer matrix. The chemical treatment is achieved using four types of reagents, acetic anhydride (Ac), maleic anhydride (MA), styrene (S), and acrylic acid (AA). This paper concludes that the chemical treatment causes decrease in the global diffusivity of water and also concludes that the water mobility in the fiber core is more than at the surface.


## 3.7. Viscoelastic Behavior of the NFPCs

Dynamic mechanical measurements or the viscoelastic behavior over a range of temperatures provides valuable insight into the structure, morphology, and determination of the interface characteristics of natural fiber composite materials [95]. Storage modulus gives an insight into the load bearing capability and the stiffness behavior of natural fiber composite materials. Storage modulus is a measure of the maximum energy stored in the material during one cycle of oscillation. The mechanical damping coefficient is the ratio of the loss modulus to the storage modulus and is related to the degree of molecular mobility in the polymeric material. On the other hand, loss modulus is proportional to the amount of energy dissipated as heat by the sample [96].The viscoelastic behavior of novel commingled biocomposites based on polypropylene/jute yarns is reported by [96]. By using commingling method, jute yarn reinforced polypropylene commingled composites were prepared. The viscoelastic behavior or dynamic mechanical properties of the result commingled composites were studied according to the fiber content and different kinds of chemical treatments such as potassium permanganate (KMnO4), maleic anhydride modified polypropylene (MAPP), toluene diisocyanate (TDI), and stearic acid (ST). This study concluded that increasing of fiber content leads to increasing the storage and loss modulus of the composite. On the other hand, at all temperatures, the chemical treatment by KMnO4 and MAPP leads to increasing the storage modulus and loss modulus of the respective treated composites than the untreated ones.By using the dynamic mechanical analyzer, Venkateshwaran et al. [35] studied the impact of alkali treatments on the viscoelastic behavior of natural fiber composite. The corresponding viscoelastic properties were determined as a function of temperature and frequency when the measurements were executed in the tensile mode of the used equipment. At the temperature range of 30–140°C at 0.1, 1, and 10 Hz frequencies, respectively, the experiments executed the graphs plotted, as storage modulus (E−) versus temperature and tan
⁡
δ versus temperature, as shown in Figures 2 and 3 [35].Figure 2
tan
⁡
δ versus temperature curves of the alkali treated and untreated composites at 1 Hz frequency [35].Figure 3
tan
⁡
δ versus temperature curves of alkali treated and untreated composites [35].


## 3.8. Relaxation Behavior of the NFPCs

Natural fiber possesses an intrinsic relaxation behavior which has a main function in the stress relaxation of NFPCs. Thus, the tensile stress relaxation of the reinforcing fiber needs to be studied in detail [38]. Sreekala et al. [29], for instance, did such a study focusing on the character of individual OPEFB fiber and, in addition, examined the fiber surface modification effects, ageing, and strain level on the fiber relaxation behavior. The fibers stress relaxation was lessened significantly with surface treatments, like latex modification, and thus decreasing resulting physical interaction between the latex particles and fiber surface. Also, water and thermal ageing reduce the rate of relaxation for the oil palm fiber; the rate of stress relaxation of the OPEFB fiber was optimized at 10% strain level which is shown in Figure 4, while the relaxation modulus values for the fiber show similar trends as in the case of stress relaxation as shown in Figure 5. On the other hand, the stress relaxation rate of OPF-sisal fiber-NR hybrid composites showed a reduction with an increase in fiber percentage [97].Figure 4
Stress relaxation curves of untreated and treated OPEFB fiber at 10% strain [29].Figure 5
Relaxation modulus curves of untreated and treated OPEFB fiber at 10% strain [29].


## 3.9. Thermal Properties of NFPCs

The untreated OPFs are thermally more stable when compared with treated ones, while OPF is considered thermally more stable compared to flax fibers and hemp fibers. Increase of temperatures from 20°C to 150°C causes increase of the heat capability of OPFs particularly from 1.083J
g
-
1
°
C
-
1 to 3.317 J
g
-
1
°
C
-
1 [98]. The thermal diffusivity, thermal conductivity, and specific heat of the flax/HDPE composites lessened with a rise in fiber composition. However, the thermal conductivity and thermal diffusivity showed no significant changes in the range of 170–200°C. The biocomposites’ specific heat showed gradual increase with temperature [4]. By using polycarbonate to generate functional composites, pineapple leaf fiber was the support. The changed pineapple leaf fibers composite, treated with silane, showed the impact strengths and highest tensile. The composites’ thermal stability is lower than the neat polycarbonate resin according to the thermogravimetric examination. Besides that, the thermal stability lessened with a rise in pineapple leaf fiber composition [4].Enzymatic treatment for many natural fibers such as flax and hemp often natural fibers can lead to improvement in surface and thermal properties [56]. Hemicellulose and pectinase are the treatments which can improve the thermal properties of the fibers mentioned. The enzymes possess an attractive state for the improvement of the natural fibers’ surfaces for natural fiber composite application [67].Norul Izani et al. [13] studied the effect of chemical treatment on the morphological and tensile strength of the EFB fiber. The treatments were by the types of treatments, 2% sodium hydroxide (NaOH) and combination of both NaOH and boiling water. The chemical treatment by NaOH led to enhancing the fiber surface topography, thermal stability, and tensile strength of the fiber, while the chemical treatment using NaOH and water boiling caused the higher thermal properties of the EFB fibers compared to untreated fibers.


## 4. Natural Fiber Polymer Composites Application

The applications of NFPCs are growing rapidly in numerous engineering fields. The different kinds of natural fibers such as jute, hemp, kenaf, oil palm, and bamboo reinforced polymer composite have received a great importance in different automotive applications, structural components, packing, and construction [5, 99]. NFPCs are finding in electrical and electronic industries, aerospace, sports, recreation equipment, boats, machinery office products, and so forth. The widespread application of NFPCs in polymer composites due to its low specific weight, relatively high strength, relatively low production cost, resistance to corrosion and fatigue, totally biodegradable, improving the surface finish of molded part composites, relatively good mechanical properties, available and renewable sources as compared to synthetic fibers [5, 98]. On the other hand, there is a physical disadvantage of the NFPCs such as moisture absorption, restricted processing temperature, and variable quality and this disadvantage led to limiting their performance [73].


### 4.1. Natural Fiber Composites Applications in the Interior Car

Most of the car companies in the world have done a lot of investigation in order to insert the NFPCs in their products. The car manufacture in Europe has done various researches to increase the applications of NFPCs in automotive industry, especially in car interior such as seat backs, parcel shelves, boot linens, front and rear door linens, truck linens, and door-trim panels [89]. Beside the use for car interior parts in automobile industry, natural fiber embedded in polymers has been used for high requirement applications for exterior auto body components, such as the middle section between the headlights above the fender of a passenger bus [18].German auto companies (BMW, Audi Group, Ford, Opel, Volkswagen, Daimler Chrysler, and Mercedes) utilize the cellulose fibers composites in various automobile part, shown in Figure6, such as using coco nut fibers rubber latex composites for the seats of the Mercedes Benz A-class model and using fax-sisal fiber mat reinforced epoxy door panels of Mercedes Benz E-class model [8]. Audi company uses flax/sisal mat reinforced polyurethane composite with a mix to make door trim panels [60]. Ford is using kenaf fibers imported from Bangladesh in their “Mondeo” model and the door panels of the Mondeo are manufactured from kenaf reinforced PP composites while using flax in floor trays [61]. Kenaf and flax mixture has gone into package trays and door panel inserts for Opel Vectras. Volkswagen company used cellulose fiber to make Seatback, door panel, boot-lid finish panel, boot-liner in Passat Variant, Golf, A4, and Bora model.Figure 6
Automobile components made of natural fiber composites [36].BMW Group has a lot of NFPCs into its automobiles. BMW Group used about 10 000 tonnes of natural fiber in 2004 [100]. Each BMW 7 series car boats 24 kg of renewable raw materials, with flax and sisal in the interior door lining panels. Also use cotton in the soundproofing, wool in the upholstery, and wood fiber in the seat back. Daimler-Benz in Germany is also working with a range of natural fibers ± sisal, jute, coconut, European hemp, and flax ± as reinforcing fibers in high-quality polypropylene components in order to replace glass fibers. Daimler-Benz has developed the dashboards and center armrest consoles along with seat shells and paneling on seat backs. Moreover, it increased the utilization of NFPCs in some automobiles by approximately 98% over earlier models by utilizing natural fibers, for example, abaca and flax. On the other hand, the Cambridge industry made rear shelf trim panels of the 2000 model Chevrolet Impala using flax fiber polypropylene composite [8, 101]. Toyota, Proton, Volvo, and other automobile companies used cellulose fiber to make car parts as shown in Table 5.Table 5
The application of natural fiber composites in automotive industry [59–62].
Manufacturer
Model
Application
Rover
2000 and others
Rear storage shelf/panel, and insulations
Opel
Vectra, Astra, Zafira
Door panels, pillar cover panel, head-liner panel, and instrumental panel
Volkswagen
Passat Variant, Golf, A4, Bora
Seat back, door panel, boot-lid finish panel, and boot-liner
Audi
A2, A3, A4, A4 Avant, A6, A8, Roadstar, Coupe
Boot-liner, spare tire-lining, side and back door panel, seat back, and hat rack
Daimler Chrysler
A, C, E, and S class, EvoBus (exterior)
Pillar cover panel, door panels, car windshield/car dashboard, and business table
BMW
3, 5 and 7 series and other Pilot
Seat back, headliner panel, boot-lining, door panels, noise insulation panels, and moulded foot well linings
Peugeot
406
Front and rear door panels, seat backs, and parcel shelf
Fiat
Punto, Brava, Marea, Alfa Romeo 146, 156, 159
Door panel
General Motors
Cadillac De Ville, Chevrolet Trail Blazer
Seat backs, cargo area floor mat
Toyota
ES3
Pillar garnish and other interior parts
Saturn
L300
Package trays and door panel
Volvo
V70, C70
Seat padding, natural foams, and cargo floor tray
Ford
Mondeo CD 162, Focus
Floor trays, door inserts, door panels, B-pillar, and boot-liner
Saab
9S
Door panels
Renault
Clio, Twingo
Rear parcel shelf
Toyota
Raum, Brevis, Harrier, Celsior,
Floor mats, spare tire cover, door panels, and seat backs
Mitsubishi
Cargo area floor, door panels, and instrumental panel
Mercedes Benz
C, S, E, and A classes
Door panels (flax/sisal/wood fibers with epoxy resin/UP matrix), glove box (cotton fibers/wood molded, flax/sisal), instrument panel support, insulation (cotton fiber), molding rod/apertures, seat backrest panel (cotton fiber), trunk panel (cotton with PP/PET fibers), and seat surface/backrest (coconut fiber/natural rubber)
Trucks
Internal engine cover, engine insulation, sun visor, interior insulation, bumper, wheel box, and roof cover
Citroen
C5
Interior door panelling
Lotus
Eco Elise (July 2008)
Body panels, spoiler, seats, and interior carpets
Rover
2000 and others
Insulation, rear storage shelf/panel
VAUXHALL
Corsa, Astra, Vectra, Zafira
Headliner panel, interior door panels, pillar cover panel, and instrument panel


### 4.2. The Natural Fiber Applications in the Industry

Other than the car industry, the applications of NFPCs are found in building and construction, aerospace, sports, and more, such as partition boards, ceilings, boats, office products, and machinery. The most applications of NFPCs are concentrated on nonload bearing indoor components in civil engineering because of their vulnerability to environmental attack [72]. Green buildings are wanted to be ecologically mindful, suitable, and healthy place to live and work. Biocomposites is consider one of the major materials utilized as a part of green materials at this time. It could be categorized, with regard to their application in the building market, into two principle products: firstly, structural biocomposites, which include bridge as well as roof structure, and secondly, nonstructural biocomposites which include window, exterior construction, composites panels, and door frame [2].The wide advantages of natural fibers reinforced composites such as high stiffness to weight ratio, lightweight, and biodegradability give them suitability in different application in building industries [102]. Van de Weyenberg et al. [24] have shown that good properties of thin walled elements such as high strength in tension and compression, made of sisal fiber reinforced composite, give it a wide area of application, for instance, structural building members, permanent formwork, tanks, facades, long span roofing elements, and pipes strengthening of existing structures. On the other hand, bamboo fiber can be used in structural concrete elements as reinforcement, while sisal fiber and coir fiber composites have been used in roofing components in order to replace asbestos [15]. Natural fiber reinforced concretes products in construction applications like sheets (both plain and corrugated) and boards are light in weight and are ideal for use in roofing, ceiling, and walling for the construction of low cost houses [103]. Table 6 shows the various applications of cellulose fiber in industry, construction, and other industries.Table 6
Natural fiber composite applications in industry [3, 63–65].
Fiber
Application in building, construction, and others
Hemp fiber
Construction products, textiles, cordage, geotextiles, paper & packaging, furniture, electrical, manufacture bank notes, and manufacture of pipes
Oil palm fiber
Building materials such as windows, door frames, structural insulated panel building systems, siding, fencing, roofing, decking, and other building materials [14]
Wood fiber
Window frame, panels, door shutters, decking, railing systems, and fencing
Flax fiber
Window frame, panels, decking, railing systems, fencing, tennis racket, bicycle frame, fork, seat post, snowboarding, and laptop cases
Rice husk fiber
Building materials such as building panels, bricks, window frame, panels, decking, railing systems, and fencing
Bagasse fiber
Window frame, panels, decking, railing systems, and fencing
Sisal fiber
In construction industry such as panels, doors, shutting plate, and roofing sheets; also, manufacturing of paper and pulp
Stalk fiber
Building panel, furniture panels, bricks, and constructing drains and pipelines
Kenaf fiber
Packing material, mobile cases, bags, insulations, clothing-grade cloth, soilless potting mixes, animal bedding,  and material that absorbs oil and liquids
Cotton fiber
Furniture industry, textile and yarn, goods, and cordage
Coir fibers
Building panels, flush door shutters, roofing sheets, storage tank, packing material, helmets and postboxes, mirror casing, paper weights, projector cover, voltage stabilizer cover, a filling material for the seat upholstery, brushes and brooms, ropes and yarns for nets, bags, and mats, as well as padding for mattresses, seat cushions
Ramie fiber
Use in products as industrial sewing thread, packing materials, fishing nets, and filter cloths. It is also made into fabrics for household furnishings (upholstery, canvas) and clothing, paper manufacture.
Jute fiber
Building panels, roofing sheets, door frames, door shutters, transport, packaging, geotextiles, and chip boards.


## 4.1. Natural Fiber Composites Applications in the Interior Car

Most of the car companies in the world have done a lot of investigation in order to insert the NFPCs in their products. The car manufacture in Europe has done various researches to increase the applications of NFPCs in automotive industry, especially in car interior such as seat backs, parcel shelves, boot linens, front and rear door linens, truck linens, and door-trim panels [89]. Beside the use for car interior parts in automobile industry, natural fiber embedded in polymers has been used for high requirement applications for exterior auto body components, such as the middle section between the headlights above the fender of a passenger bus [18].German auto companies (BMW, Audi Group, Ford, Opel, Volkswagen, Daimler Chrysler, and Mercedes) utilize the cellulose fibers composites in various automobile part, shown in Figure6, such as using coco nut fibers rubber latex composites for the seats of the Mercedes Benz A-class model and using fax-sisal fiber mat reinforced epoxy door panels of Mercedes Benz E-class model [8]. Audi company uses flax/sisal mat reinforced polyurethane composite with a mix to make door trim panels [60]. Ford is using kenaf fibers imported from Bangladesh in their “Mondeo” model and the door panels of the Mondeo are manufactured from kenaf reinforced PP composites while using flax in floor trays [61]. Kenaf and flax mixture has gone into package trays and door panel inserts for Opel Vectras. Volkswagen company used cellulose fiber to make Seatback, door panel, boot-lid finish panel, boot-liner in Passat Variant, Golf, A4, and Bora model.Figure 6
Automobile components made of natural fiber composites [36].BMW Group has a lot of NFPCs into its automobiles. BMW Group used about 10 000 tonnes of natural fiber in 2004 [100]. Each BMW 7 series car boats 24 kg of renewable raw materials, with flax and sisal in the interior door lining panels. Also use cotton in the soundproofing, wool in the upholstery, and wood fiber in the seat back. Daimler-Benz in Germany is also working with a range of natural fibers ± sisal, jute, coconut, European hemp, and flax ± as reinforcing fibers in high-quality polypropylene components in order to replace glass fibers. Daimler-Benz has developed the dashboards and center armrest consoles along with seat shells and paneling on seat backs. Moreover, it increased the utilization of NFPCs in some automobiles by approximately 98% over earlier models by utilizing natural fibers, for example, abaca and flax. On the other hand, the Cambridge industry made rear shelf trim panels of the 2000 model Chevrolet Impala using flax fiber polypropylene composite [8, 101]. Toyota, Proton, Volvo, and other automobile companies used cellulose fiber to make car parts as shown in Table 5.Table 5
The application of natural fiber composites in automotive industry [59–62].
Manufacturer
Model
Application
Rover
2000 and others
Rear storage shelf/panel, and insulations
Opel
Vectra, Astra, Zafira
Door panels, pillar cover panel, head-liner panel, and instrumental panel
Volkswagen
Passat Variant, Golf, A4, Bora
Seat back, door panel, boot-lid finish panel, and boot-liner
Audi
A2, A3, A4, A4 Avant, A6, A8, Roadstar, Coupe
Boot-liner, spare tire-lining, side and back door panel, seat back, and hat rack
Daimler Chrysler
A, C, E, and S class, EvoBus (exterior)
Pillar cover panel, door panels, car windshield/car dashboard, and business table
BMW
3, 5 and 7 series and other Pilot
Seat back, headliner panel, boot-lining, door panels, noise insulation panels, and moulded foot well linings
Peugeot
406
Front and rear door panels, seat backs, and parcel shelf
Fiat
Punto, Brava, Marea, Alfa Romeo 146, 156, 159
Door panel
General Motors
Cadillac De Ville, Chevrolet Trail Blazer
Seat backs, cargo area floor mat
Toyota
ES3
Pillar garnish and other interior parts
Saturn
L300
Package trays and door panel
Volvo
V70, C70
Seat padding, natural foams, and cargo floor tray
Ford
Mondeo CD 162, Focus
Floor trays, door inserts, door panels, B-pillar, and boot-liner
Saab
9S
Door panels
Renault
Clio, Twingo
Rear parcel shelf
Toyota
Raum, Brevis, Harrier, Celsior,
Floor mats, spare tire cover, door panels, and seat backs
Mitsubishi
Cargo area floor, door panels, and instrumental panel
Mercedes Benz
C, S, E, and A classes
Door panels (flax/sisal/wood fibers with epoxy resin/UP matrix), glove box (cotton fibers/wood molded, flax/sisal), instrument panel support, insulation (cotton fiber), molding rod/apertures, seat backrest panel (cotton fiber), trunk panel (cotton with PP/PET fibers), and seat surface/backrest (coconut fiber/natural rubber)
Trucks
Internal engine cover, engine insulation, sun visor, interior insulation, bumper, wheel box, and roof cover
Citroen
C5
Interior door panelling
Lotus
Eco Elise (July 2008)
Body panels, spoiler, seats, and interior carpets
Rover
2000 and others
Insulation, rear storage shelf/panel
VAUXHALL
Corsa, Astra, Vectra, Zafira
Headliner panel, interior door panels, pillar cover panel, and instrument panel


## 4.2. The Natural Fiber Applications in the Industry

Other than the car industry, the applications of NFPCs are found in building and construction, aerospace, sports, and more, such as partition boards, ceilings, boats, office products, and machinery. The most applications of NFPCs are concentrated on nonload bearing indoor components in civil engineering because of their vulnerability to environmental attack [72]. Green buildings are wanted to be ecologically mindful, suitable, and healthy place to live and work. Biocomposites is consider one of the major materials utilized as a part of green materials at this time. It could be categorized, with regard to their application in the building market, into two principle products: firstly, structural biocomposites, which include bridge as well as roof structure, and secondly, nonstructural biocomposites which include window, exterior construction, composites panels, and door frame [2].The wide advantages of natural fibers reinforced composites such as high stiffness to weight ratio, lightweight, and biodegradability give them suitability in different application in building industries [102]. Van de Weyenberg et al. [24] have shown that good properties of thin walled elements such as high strength in tension and compression, made of sisal fiber reinforced composite, give it a wide area of application, for instance, structural building members, permanent formwork, tanks, facades, long span roofing elements, and pipes strengthening of existing structures. On the other hand, bamboo fiber can be used in structural concrete elements as reinforcement, while sisal fiber and coir fiber composites have been used in roofing components in order to replace asbestos [15]. Natural fiber reinforced concretes products in construction applications like sheets (both plain and corrugated) and boards are light in weight and are ideal for use in roofing, ceiling, and walling for the construction of low cost houses [103]. Table 6 shows the various applications of cellulose fiber in industry, construction, and other industries.Table 6
Natural fiber composite applications in industry [3, 63–65].
Fiber
Application in building, construction, and others
Hemp fiber
Construction products, textiles, cordage, geotextiles, paper & packaging, furniture, electrical, manufacture bank notes, and manufacture of pipes
Oil palm fiber
Building materials such as windows, door frames, structural insulated panel building systems, siding, fencing, roofing, decking, and other building materials [14]
Wood fiber
Window frame, panels, door shutters, decking, railing systems, and fencing
Flax fiber
Window frame, panels, decking, railing systems, fencing, tennis racket, bicycle frame, fork, seat post, snowboarding, and laptop cases
Rice husk fiber
Building materials such as building panels, bricks, window frame, panels, decking, railing systems, and fencing
Bagasse fiber
Window frame, panels, decking, railing systems, and fencing
Sisal fiber
In construction industry such as panels, doors, shutting plate, and roofing sheets; also, manufacturing of paper and pulp
Stalk fiber
Building panel, furniture panels, bricks, and constructing drains and pipelines
Kenaf fiber
Packing material, mobile cases, bags, insulations, clothing-grade cloth, soilless potting mixes, animal bedding,  and material that absorbs oil and liquids
Cotton fiber
Furniture industry, textile and yarn, goods, and cordage
Coir fibers
Building panels, flush door shutters, roofing sheets, storage tank, packing material, helmets and postboxes, mirror casing, paper weights, projector cover, voltage stabilizer cover, a filling material for the seat upholstery, brushes and brooms, ropes and yarns for nets, bags, and mats, as well as padding for mattresses, seat cushions
Ramie fiber
Use in products as industrial sewing thread, packing materials, fishing nets, and filter cloths. It is also made into fabrics for household furnishings (upholstery, canvas) and clothing, paper manufacture.
Jute fiber
Building panels, roofing sheets, door frames, door shutters, transport, packaging, geotextiles, and chip boards.


## 5. Conclusions

Natural fiber reinforced polymer composites have beneficial properties such as low density, less expensive, and reduced solidity when compared to synthetic composite products, thus providing advantages for utilization in commercial applications (automotive industry, buildings, and constructions). Using natural fibers as reinforcement for polymeric composites introduces positive effect on the mechanical behavior of polymers. This paper evaluates the characteristics and properties of natural fiber reinforced polymer composites: mechanical, thermal, energy absorption, moisture absorption, biodegradability, flame retardancy, tribology properties. Viscoelastic behavior and relaxation behavior of NFPCs are researched. Also the application of NFPCs in automobile and industry is reported. The effects of chemical treatment of the natural fiber properties were also addressed. The physical and mechanical properties of these NFPCs can be further enhanced through the chemical treatment, while moisture absorption of the NFPCs can be reduced through surface modification of fibers such as alkalization and addition of coupling agents.



---