# Surge-Resistant Nanocomposite Enameled Wire Using Silica Nanoparticles with Binary Chemical Compositions on the Surface

Authors: Jeseung Yoo; Yongbeom Kim; Suyong Kwon; Joohyun Lee; Young-Soo Seo
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

We developed polyesterimide (PEI) nanocomposite enameled wires using surface-modified silica nanoparticles with binary chemical compositions on the surface. The modification was done using silanes assisted by ultrasound, which facilitated high density modification. Two different trimethoxysilanes were chosen for the modification on the basis of resemblance of chemical compositions on the silica surface to PEI varnish. The surface-modified silica was well dispersed in PEI varnish, which was confirmed by optical observation and viscosity measurement. The glass transition temperature of the silica-PEI nanocomposite increased with the silica content. The silica-dispersed PEI varnish was then used for enameled wire fabrication. The silica-PEI nanocomposite enameled wire exhibited a much longer lifetime compared to that of neat PEI enameled wire in partial discharge conditions.


---

## Body

## 1. Introduction

Enameled wire is composed of conductive copper or aluminum core surrounded by an insulation layer made of polymer. The lifespan of the electric motor is strongly dependent on thermal and electrical properties of the insulation layer. In a high speed switching inverter-fed motor, especially, when instantaneous overlapping voltage called surge voltage is higher than partial discharge inception voltage (PDIV), the insulation layer is degraded by partial discharge (PD), which leads to insulation breakdown [1–4]. For this reason, surge-resistant enameled wire has attracted attention for prolonging the lifespan of various inverter-fed motor installed electric devices such as electric vehicles. For protection from the degradation, nanosized inorganic fillers were incorporated in the insulation layer [5–8] where corona evolved by PD can be trapped on or reflected from the surface of the inorganic filler so that the degradation would be retarded [9–11].Polyesterimide (PEI) was frequently chosen for the insulation layer of high temperature enameled wires because it meets both requirements [12–14] of high thermal index and flexibility sufficient to withstand severe stress while winding. There are many reports regarding the enhanced breakdown time of PEI enameled wire by adding inorganic nanoparticles such as silica, alumina, and clay in the insulation layer. In 2002, Hitachi Cable Ltd. developed silica nanoparticle-PEI nanocomposite enameled wire having breakdown time of 42 min compared to 1 min for one without silica in the PD condition of 2.8 kV and 10 kHz [15]. Since then, surge-resistant properties of nanocomposite enameled wire have been systematically studied [1, 11, 16–18]. As expected, the breakdown time increased with nanoparticle volume fraction on the condition that the nanoparticles are uniformly dispersed.Because it is difficult to disperse nanoparticle in a viscous varnish solution, the sol-gel method, which has a great advantage for dispersion, has attracted attention. In the sol-gel method, nanoparticles are easily dispersed in the insulation layer as soon as they are synthesized from the precursors premixed in the varnish during the wire annealing process accompanied by a coating process [12, 19]. However, serious problems were revealed; for example, the enameled wire production cost increased because the process was too slow and the breakdown strength of the enameled wire was reduced due to impurities remaining from the sol-gel process [20, 21]. In order to avoid such problems, nanoparticles need to be directly dispersed in the varnish and therefore should be properly surface-modified [6, 13].Here we propose a novel surface modification method in which silica nanoparticles are chemically modified using two kinds of silanes, selected based on the fact that their chemical composition on the silica surface matches that of the varnish, resulting in binary chemical compositions forming on the silica surface. Silanes are highly reactive to form chemical bond with silanol group on the silica. During the silanation, ultrasound was applied so that the reaction rate was accelerated and the surface coverage was increased. We found that the surface-modified silica nanoparticles were uniformly dispersed in PEI varnish. The silica nanoparticle dispersed PEI varnish was then applied for the nanocomposite enameled wires fabrication in commercial facilities. Surge resistance properties of the nanocomposite enameled wire were investigated.


## 2. Experimental

Fumed silica was purchased from Sigma-Aldrich, which has an average size of 11 nm with a specific area of255±15 m2/g. Fumed silica nanoparticles were used because they are known as their excellent property for preventing PD-induced breakdown [22]. Silanes also from Sigma-Aldrich were used without further purification. Cresol was a thinner for polyesterimide and polyamideimide varnish with a solid content of 39 wt%, which were supplied by Komec Co., Korea.For surface modification of silica with silanes, 12 g of fumed silica was added into 600 mL of toluene in a 1,000 mL glass bottle. The bottle was sonicated for 30 minutes at 85°C using a bath-type sonicator (60 W, 28 kHz) in order to disperse fumed silica in toluene. The solution temperature was kept for 85°C during the following silanation reaction. Table1 lists silane modified silica from SN1 to SN7. For single silane modification (SN1 and SN6), 10 g of silane was added to the solution and ultrasonication was applied for 3 days. For double silane modification (SN2, SN3, SN5, and SN7), 8 g of first silane was added to the solution and ultrasonication for 3 h. Successively, 2 g of second silane was added and sonicated for 3 days. For triple silane modification (SN4), 8 g of first silane was added to the solution and sonicated for 3 h. 2 g of second silane was added and sonicated for 3 h, and then 1 g of third silane was added and sonicated for 3 days. After the reaction, the solution was mixed with ethanol and then filtered using a glass filter funnel. Gel-like filtrates were washed five times with ethanol to remove unreacted silanes and then dried in an oven at 110°C overnight.Table 1
Single, double, and triple silane modified silica nanoparticles.
(a)
Name
First silane
Second silane
Third silane
SN1
ANMS
—
—
SN2
ANMS
DAMS
—
SN3
ANMS
TMMS
—
SN4
ANMS
DAMS
TMMS
SN5
DAMS
TMMS
—
SN6
TAMS
—
SN7
TAMS
TMMS
—
(b)
ANMS
(3-Anilinopropyl)trimethoxysilane
DAMS
N-(2-Aminoethyl)-3-(trimethoxysilyl)propylamine
TAMS
2-[2-(3-Trimethoxysilylpropylamino)ethylamino]ethylamine
TMMS
TrimethylmethoxysilaneScanning electron microscope (SEM) image was taken using field emission-SEM (FE-SEM, Hitachi, S-4700). Viscosity of the varnish solution was measured using a Brookfield viscometer. Glass transition of the silica-PEI nanocomposites was measured using differential scanning calorimeter (DSC, Mettler-Toledo, DSC1). Surge endurance test was done using a PD tester (SungMin Instrument, Korea).


## 3. Results and Discussion

### 3.1. Surface Modifications

Figure1 shows SEM images of silane modified silica particles. Silane directly reacts with hydroxyl group on the surface of silica, forming a permanent chemical bond. Particle size is indistinguishable from SN1 to SN7, which is still bigger by few nanometers than fumed silica particle, indicating that fumed silica is covered by an organic layer. As previously reported [22], the area occupied by ANMS (92.1 Å2) is 3.6 times bigger than DAMS (25.6 Å2) on the fumed silica surface due to greater steric hindrance of ANMS than DAMS. From SN1 to SN4, in which cases ANMS was treated first, the area occupied by a silane lies in between those two values, which indicates, paradoxically, that the first treatment by ANMS may allow further surface modification using smaller sized silane. This reaction requires high energy provided by cavitation effects generated by ultrasound. The first TAMS treatment cases (SN6 and SN7) are similar to the DAMS case (SN5). It is noted that polymerization reaction between the silanes was minimized during the surface modification.Figure 1
SEM images of fumed silica, modified nanoparticles of SN1 to SN7.


### 3.2. Dispersion in Cresol

The dispersion state of the silane modified silica from SN1 to SN7 was checked. After they were dissolved in cresol with a solid content of 15 wt% assisted by ultrasonication at 85°C, where cresol is a thinner for PEI varnish, they were left at room temperature for a day and checked visually clearness of the solution. Figure2 shows the result of the dispersion. ANMS exhibits better compatibility than the other silanes. Unlike the previous result [22] where ANMS-TMMS dual silane modified silica (here, SN3) was well dissolved in cresol-xylene mixture solvent, ANMS-DAMS silica (SN2) exhibits the best dispersion state in cresol alone. Even though ANMS modified silica (SN1) was also dispersed in cresol, it required a longer sonication time for dispersion and was much more viscous than SN2 in cresol. ANMS-DAMS-TMMS triple silane modified silica (S4) was not dispersed because small TMMS molecules consumed silanol groups on the silica faster than DAMS. SN5, SN6, and SN7, where DAMS or TAMS was used as a first silane for the modification, did not result in good compatibility to cresol, which indicates that these molecules are less compatible to cresol than ANMS.Figure 2
Dispersion test of silane modified silica from SN1 to SN7 in cresol.


### 3.3. Surface Modification Using Bath- and Horn-Type Sonicator

Unlike a bath-type sonicator, the ultrasound generating horn in a horn-type sonicator directly contacts with reaction solution. Here we used a horn-type sonicator (200 W, 20 kHz, Janosonic, Co., South Korea), which has higher power than the bath-type sonicator (60 W, 28 kHz), for SN2 preparation. For the bath-type sonicator, after ANMS was added to the solution, 3-hour sonication was applied, while for a horn-type sonicator 30 min sonication was applied, followed by DAMS addition, and further sonication was applied. SN2 obtained from both methods was dissolved using the horn-type sonicator for 3 hours in cresol. The solubility of SN2 was checked in terms of total sonication time for the silane reaction as shown in Figure3. The dispersion state of SN2 was easily checked by turning the bottle upside down. Using a bath-type sonicator, 72-hour sonication for silane modification was required for complete dispersion in cresol. On the other hand, 3.5-hour sonication was enough using a horn-type sonicator. Therefore, the horn-type sonicator is much faster than the bath-type sonicator for the complete silane reaction, though considering its higher power compared to the bath-type sonicator. This implies that high sonication power facilitates the effective reaction of DAMS with a silanol group by overcoming the steric hindrance of ANMS.Figure 3
Sonication time for SN2 preparation using bath- and horn-type sonicator. 20 wt% SN2 was dissolved in cresol for checking solubility.


### 3.4. Dispersion in PEI Varnish

SN2-PEI varnish solution was prepared by simply mixing SN2 dissolved in cresol with PEI varnish. The SN2 content is 0, 1, 3, 5, 10, 15, and 20 wt% in PEI varnish. Alternatively, it can be prepared by directly dissolving dry SN2 in PEI varnish assisted by ultrasonication. The former method was faster than the later one, but the results are the same. Each solution was transparent to 20 wt% SN2 as shown in Figure4 inset, indicating that SN2 is well dissolved in PEI varnish.Figure 4
Viscosity of SN2-PEI varnish solution and solution bottles in inset.Solubility of SN2 was also checked by viscosity of the solution, which is important in the enameled wire coating process because it determines coating thickness and flatness. The viscosity of the solution was measured at 25 and 50°C. At 25°C, the viscosity of the PEI varnish was measured to 213 centipoises (cp). It steadily increases as the SN2 concentration increases up to 10 wt% and then steeply increases. At 50°C, on the other hand, which is close to the usual PEI varnish bath temperature in enameled wire fabrication, the varnish viscosity steadily increases as the SN2 concentration increases up to 20 wt%.The organic content of SN2 was obtained after burning it at 600°C for 2 h accompanied by drying at 200°C for 2 h, which was 13.0 wt%. This value lies in between 6.0 wt% for SN3 and 16.3 wt% for SN5. It is certain that both ANMS and DAMS exist on the silica surface in the SN2 sample, even though exact proportion of each silane is unclear. Again, it is confirmed that dual silane modification, that is, ANMS treatment followed by DAMS treatment, has been accomplished assisted by ultrasonic power. Figure5 shows schematic drawing for chemical structure of SN2, cresol, and PEI varnish. SN2 is composed of both the nonpolar benzene ring and the polar amine group on its surface, that is, binary chemical compositions. Cresol and PEI varnish also have both polar and nonpolar characters. Therefore, the surface chemical structure of SN2 is quite similar to cresol as well as PEI varnish as shown in the figure. In this way, we believe that surface character of nanoparticles can be tailored by using two or more kinds of silanes, enhancing compatibility to the matrix environment for the dispersion.Figure 5
Schematic drawing for chemical similarity of silica surface with binary chemical compositions to cresol and PEI varnish.


### 3.5. Analysis of SN2/Polyesterimide Nanocomposites

SN2/polyesterimide nanocomposite sample was prepared by thermal curing in the following procedure. SN2 dispersed PEI varnish was transferred into a 40μL aluminum pan used for differential scanning calorimeter (DSC) measurement. Then, the pan was placed in an oven successively at 120°C for 30 min, at 170°C for 45 min, and at 230°C for 2 h.The surface of thermally cured neat PEI as well as SN2-PEI composites was flat according to the FE-SEM images as shown in Figure6. There is no indication of large sized aggregate on the surface. Dispersion of SN2 in the nanocomposite can be checked by dipping it into 49% hydrofluoric acid solution to dissolve silica particles existing in the close vicinity of the surface. After the treatment, the neat PEI sample exhibited a flat surface without any holes. On the other hand, on the 10 wt% SN2-PEI composite, holes appear, and their size is somewhat irregular, spanning 5 to 20 nm, which might be dependent on the embedding depth of the silica. Most of holes are round, however, indicating a single silica particle. This implies that silica is well dispersed in the PEI matrix. 20 wt% SN2-PEI composite also exhibits good dispersion even though ellipsoidal shaped holes occasionally appear, which may result from aggregate 2-3 particles. Consequently, it is found that aggregation of between silica particles in PEI is minimized by dual silane surface modification.Figure 6
SEM images of thermally cured SN2-PEI nanocomposite before and after HF treatments.The thermal property of the cured sample was investigated by DSC. Figure7 shows DSC thermograms where the SN2 content varied from 0 to 20 wt%, where the glass transition temperature (Tg) is indicated by vertical bars. Tg of each sample is displayed in terms of SN2 content in inset. Tg of neat PEI steeply increases from 90 to 107°C by adding up to 5 wt% SN2. Above 5 wt%  Tg increment is retarded and reaches 113°C for 20 wt%. The increase in Tg is attributed to a strong interaction between SN2 and the polymer matrix, which causes restricted motion of the polymer chains on the surface of the silica nanoparticles. A similar result was previously reported in which Tg of polyetherimide increased with an increase in inorganic nanofiller concentration as a result of good dispersion [23].Figure 7
Thermograms of PEI nanocomposite measured by DSC with 0, 1, 3, 5, 10, 15, and 20 wt% SN2 from the top. Inset shows glass transition temperature (Tg) in terms of SN2 content obtained from the thermograms. Thermograms are moved down for clarity.


### 3.6. Fabrication of SN2-PEI Nanocomposite Enameled Wire and Surge Endurance Test

Fabrication of the SN2-PEI nanocomposite enameled wire has been done in a commercial coating facility. Both SN2 synthesis and dispersion in PEI varnish were done using a horn-type sonicator installed 3-liter reaction chamber with a water circulating jacket. Singly and doubly coated enameled wires were fabricated, which are PEI enameled wire and polyamideimide (PAI) covered PEI enameled wire as shown in Figure8. PEI enameled wires including 0, 5, and 10 wt% SN2 coated on copper wire with diameter of 0.56±0.01 mm were prepared. Coating thickness for each wire which was 29.5±0.5 μm for PEI without SN2, 30.0±0.5 μm for 5 wt%, and 30.8±0.5 μm for 10 wt% SN2 in PEI was obtained after repetitive coating 8 times, where the thickness slightly increases as the silica content increases because of increased viscosity of the varnish solution. PAI covered PEI enameled wire consists of an inner PEI layer and an outer self-lubricating PAI layer, which is a popular form of heat resistant enameled wire. The 30 μm PEI layer from 8 coats of PEI varnish followed by 10 μm PAI layer from 3 coats of PAI varnish was formed on the 1.0 mm copper wire in diameter, where the 5 wt% SN2 was dispersed only in the PEI varnish.Figure 8
Applied voltage versus breakdown time of (a) PEI nanocomposite enameled wire and (b) PAI covered PEI nanocomposite enameled wire at 10 kHz. In inset, structure of both enameled wires and twisted wires for the test before and after voltage applied is displayed.
(a)
(b)A surge endurance test was done using twisted wires as shown in Figure8. Voltage with square wave ranged from 3,000 to 4,500 V with 10 kHz applied at room temperature, in which conditions PD was generated on the surface of the twisted wire. The breakdown time was measured when the insulation breaks down. In Figure 8(a), PEI enameled wire was broken down after 4 min at 4.5 kV. But by adding 5 wt% SN2, it endured longer times of 8 min and further addition of SN2 to 10 wt% leads the breakdown time to increase to 28 min. This indicates that the embedded silica particles are well dispersed and effectively protect PEI layer from corrosion induced by PD. As the applied voltage decreases to 4.0 and 3.5 kV, the breakdown time difference between neat PEI and nanocomposite wire increases. It also increases exponentially with the increase in SN2 content. Similar results have been obtained for PAI covered PEI enameled wire as shown in Figure 8(b).


## 3.1. Surface Modifications

Figure1 shows SEM images of silane modified silica particles. Silane directly reacts with hydroxyl group on the surface of silica, forming a permanent chemical bond. Particle size is indistinguishable from SN1 to SN7, which is still bigger by few nanometers than fumed silica particle, indicating that fumed silica is covered by an organic layer. As previously reported [22], the area occupied by ANMS (92.1 Å2) is 3.6 times bigger than DAMS (25.6 Å2) on the fumed silica surface due to greater steric hindrance of ANMS than DAMS. From SN1 to SN4, in which cases ANMS was treated first, the area occupied by a silane lies in between those two values, which indicates, paradoxically, that the first treatment by ANMS may allow further surface modification using smaller sized silane. This reaction requires high energy provided by cavitation effects generated by ultrasound. The first TAMS treatment cases (SN6 and SN7) are similar to the DAMS case (SN5). It is noted that polymerization reaction between the silanes was minimized during the surface modification.Figure 1
SEM images of fumed silica, modified nanoparticles of SN1 to SN7.


## 3.2. Dispersion in Cresol

The dispersion state of the silane modified silica from SN1 to SN7 was checked. After they were dissolved in cresol with a solid content of 15 wt% assisted by ultrasonication at 85°C, where cresol is a thinner for PEI varnish, they were left at room temperature for a day and checked visually clearness of the solution. Figure2 shows the result of the dispersion. ANMS exhibits better compatibility than the other silanes. Unlike the previous result [22] where ANMS-TMMS dual silane modified silica (here, SN3) was well dissolved in cresol-xylene mixture solvent, ANMS-DAMS silica (SN2) exhibits the best dispersion state in cresol alone. Even though ANMS modified silica (SN1) was also dispersed in cresol, it required a longer sonication time for dispersion and was much more viscous than SN2 in cresol. ANMS-DAMS-TMMS triple silane modified silica (S4) was not dispersed because small TMMS molecules consumed silanol groups on the silica faster than DAMS. SN5, SN6, and SN7, where DAMS or TAMS was used as a first silane for the modification, did not result in good compatibility to cresol, which indicates that these molecules are less compatible to cresol than ANMS.Figure 2
Dispersion test of silane modified silica from SN1 to SN7 in cresol.


## 3.3. Surface Modification Using Bath- and Horn-Type Sonicator

Unlike a bath-type sonicator, the ultrasound generating horn in a horn-type sonicator directly contacts with reaction solution. Here we used a horn-type sonicator (200 W, 20 kHz, Janosonic, Co., South Korea), which has higher power than the bath-type sonicator (60 W, 28 kHz), for SN2 preparation. For the bath-type sonicator, after ANMS was added to the solution, 3-hour sonication was applied, while for a horn-type sonicator 30 min sonication was applied, followed by DAMS addition, and further sonication was applied. SN2 obtained from both methods was dissolved using the horn-type sonicator for 3 hours in cresol. The solubility of SN2 was checked in terms of total sonication time for the silane reaction as shown in Figure3. The dispersion state of SN2 was easily checked by turning the bottle upside down. Using a bath-type sonicator, 72-hour sonication for silane modification was required for complete dispersion in cresol. On the other hand, 3.5-hour sonication was enough using a horn-type sonicator. Therefore, the horn-type sonicator is much faster than the bath-type sonicator for the complete silane reaction, though considering its higher power compared to the bath-type sonicator. This implies that high sonication power facilitates the effective reaction of DAMS with a silanol group by overcoming the steric hindrance of ANMS.Figure 3
Sonication time for SN2 preparation using bath- and horn-type sonicator. 20 wt% SN2 was dissolved in cresol for checking solubility.


## 3.4. Dispersion in PEI Varnish

SN2-PEI varnish solution was prepared by simply mixing SN2 dissolved in cresol with PEI varnish. The SN2 content is 0, 1, 3, 5, 10, 15, and 20 wt% in PEI varnish. Alternatively, it can be prepared by directly dissolving dry SN2 in PEI varnish assisted by ultrasonication. The former method was faster than the later one, but the results are the same. Each solution was transparent to 20 wt% SN2 as shown in Figure4 inset, indicating that SN2 is well dissolved in PEI varnish.Figure 4
Viscosity of SN2-PEI varnish solution and solution bottles in inset.Solubility of SN2 was also checked by viscosity of the solution, which is important in the enameled wire coating process because it determines coating thickness and flatness. The viscosity of the solution was measured at 25 and 50°C. At 25°C, the viscosity of the PEI varnish was measured to 213 centipoises (cp). It steadily increases as the SN2 concentration increases up to 10 wt% and then steeply increases. At 50°C, on the other hand, which is close to the usual PEI varnish bath temperature in enameled wire fabrication, the varnish viscosity steadily increases as the SN2 concentration increases up to 20 wt%.The organic content of SN2 was obtained after burning it at 600°C for 2 h accompanied by drying at 200°C for 2 h, which was 13.0 wt%. This value lies in between 6.0 wt% for SN3 and 16.3 wt% for SN5. It is certain that both ANMS and DAMS exist on the silica surface in the SN2 sample, even though exact proportion of each silane is unclear. Again, it is confirmed that dual silane modification, that is, ANMS treatment followed by DAMS treatment, has been accomplished assisted by ultrasonic power. Figure5 shows schematic drawing for chemical structure of SN2, cresol, and PEI varnish. SN2 is composed of both the nonpolar benzene ring and the polar amine group on its surface, that is, binary chemical compositions. Cresol and PEI varnish also have both polar and nonpolar characters. Therefore, the surface chemical structure of SN2 is quite similar to cresol as well as PEI varnish as shown in the figure. In this way, we believe that surface character of nanoparticles can be tailored by using two or more kinds of silanes, enhancing compatibility to the matrix environment for the dispersion.Figure 5
Schematic drawing for chemical similarity of silica surface with binary chemical compositions to cresol and PEI varnish.


## 3.5. Analysis of SN2/Polyesterimide Nanocomposites

SN2/polyesterimide nanocomposite sample was prepared by thermal curing in the following procedure. SN2 dispersed PEI varnish was transferred into a 40μL aluminum pan used for differential scanning calorimeter (DSC) measurement. Then, the pan was placed in an oven successively at 120°C for 30 min, at 170°C for 45 min, and at 230°C for 2 h.The surface of thermally cured neat PEI as well as SN2-PEI composites was flat according to the FE-SEM images as shown in Figure6. There is no indication of large sized aggregate on the surface. Dispersion of SN2 in the nanocomposite can be checked by dipping it into 49% hydrofluoric acid solution to dissolve silica particles existing in the close vicinity of the surface. After the treatment, the neat PEI sample exhibited a flat surface without any holes. On the other hand, on the 10 wt% SN2-PEI composite, holes appear, and their size is somewhat irregular, spanning 5 to 20 nm, which might be dependent on the embedding depth of the silica. Most of holes are round, however, indicating a single silica particle. This implies that silica is well dispersed in the PEI matrix. 20 wt% SN2-PEI composite also exhibits good dispersion even though ellipsoidal shaped holes occasionally appear, which may result from aggregate 2-3 particles. Consequently, it is found that aggregation of between silica particles in PEI is minimized by dual silane surface modification.Figure 6
SEM images of thermally cured SN2-PEI nanocomposite before and after HF treatments.The thermal property of the cured sample was investigated by DSC. Figure7 shows DSC thermograms where the SN2 content varied from 0 to 20 wt%, where the glass transition temperature (Tg) is indicated by vertical bars. Tg of each sample is displayed in terms of SN2 content in inset. Tg of neat PEI steeply increases from 90 to 107°C by adding up to 5 wt% SN2. Above 5 wt%  Tg increment is retarded and reaches 113°C for 20 wt%. The increase in Tg is attributed to a strong interaction between SN2 and the polymer matrix, which causes restricted motion of the polymer chains on the surface of the silica nanoparticles. A similar result was previously reported in which Tg of polyetherimide increased with an increase in inorganic nanofiller concentration as a result of good dispersion [23].Figure 7
Thermograms of PEI nanocomposite measured by DSC with 0, 1, 3, 5, 10, 15, and 20 wt% SN2 from the top. Inset shows glass transition temperature (Tg) in terms of SN2 content obtained from the thermograms. Thermograms are moved down for clarity.


## 3.6. Fabrication of SN2-PEI Nanocomposite Enameled Wire and Surge Endurance Test

Fabrication of the SN2-PEI nanocomposite enameled wire has been done in a commercial coating facility. Both SN2 synthesis and dispersion in PEI varnish were done using a horn-type sonicator installed 3-liter reaction chamber with a water circulating jacket. Singly and doubly coated enameled wires were fabricated, which are PEI enameled wire and polyamideimide (PAI) covered PEI enameled wire as shown in Figure8. PEI enameled wires including 0, 5, and 10 wt% SN2 coated on copper wire with diameter of 0.56±0.01 mm were prepared. Coating thickness for each wire which was 29.5±0.5 μm for PEI without SN2, 30.0±0.5 μm for 5 wt%, and 30.8±0.5 μm for 10 wt% SN2 in PEI was obtained after repetitive coating 8 times, where the thickness slightly increases as the silica content increases because of increased viscosity of the varnish solution. PAI covered PEI enameled wire consists of an inner PEI layer and an outer self-lubricating PAI layer, which is a popular form of heat resistant enameled wire. The 30 μm PEI layer from 8 coats of PEI varnish followed by 10 μm PAI layer from 3 coats of PAI varnish was formed on the 1.0 mm copper wire in diameter, where the 5 wt% SN2 was dispersed only in the PEI varnish.Figure 8
Applied voltage versus breakdown time of (a) PEI nanocomposite enameled wire and (b) PAI covered PEI nanocomposite enameled wire at 10 kHz. In inset, structure of both enameled wires and twisted wires for the test before and after voltage applied is displayed.
(a)
(b)A surge endurance test was done using twisted wires as shown in Figure8. Voltage with square wave ranged from 3,000 to 4,500 V with 10 kHz applied at room temperature, in which conditions PD was generated on the surface of the twisted wire. The breakdown time was measured when the insulation breaks down. In Figure 8(a), PEI enameled wire was broken down after 4 min at 4.5 kV. But by adding 5 wt% SN2, it endured longer times of 8 min and further addition of SN2 to 10 wt% leads the breakdown time to increase to 28 min. This indicates that the embedded silica particles are well dispersed and effectively protect PEI layer from corrosion induced by PD. As the applied voltage decreases to 4.0 and 3.5 kV, the breakdown time difference between neat PEI and nanocomposite wire increases. It also increases exponentially with the increase in SN2 content. Similar results have been obtained for PAI covered PEI enameled wire as shown in Figure 8(b).


## 4. Conclusions

In this study, surge-resistant silica nanoparticle-PEI nanocomposite enameled wires were fabricated. For uniform dispersion of the silica nanoparticle in PEI varnish, its surface character was tailored by chemical modifications using two kinds of silanes so that the surface chemical composition would become similar to the varnish. The modification reaction was accelerated by ultrasound using a horn-type sonicator. After the modification, the nanoparticle with content of 20 wt% was well dispersed in both cresol and PEI varnish. Glass transition temperature of the silica-PEI nanocomposite was improved from 90 to 113°C by increasing the silica content up to 20 wt%. The nanoparticle dispersed varnish was then applied for fabrication of the nanocomposite coated enameled wires in commercial facilities. The silica-PEI nanocomposite enameled wire exhibited enhanced surge resistance wherein the breakdown time increased by 7-8 times compared to that of neat PEI enameled wire. This surface modification method can be extended to nanoparticles for enhancing compatibility to various matrix environments.



---