# Enhanced Performance of DSSCs Based on the Insertion Energy Level of CdS Quantum Dots

Authors: Xiaoping Zou; Zhe Sun
Journal: Journal of Chemistry
 (2014)

---

## Abstract

Cadmium sulfide (CdS) quantum dots (QDs) are assembled onto the TiO2 films by chemical bath deposition method (CBD). And the QDs size is controlled by the times of CBD cycles. They are characterized by UV-visible absorption. To avoid the photo corrosion and electrolyte corrosion, CdS and N719 are sequentially assembled onto the nanocrystalline TiO2 films to prepare a CdS/N719 cosensitized photo electrode for the dye-sensitized solar cells. In the structure of TiO2/CdS/N719 electrode, the reorganization of energy levels between CdS and N719 forms a stepwise structure of band-edge levels which is advantageous to the electron injection and hole recovery of CdS and N719 QDs. The open circuit voltage (V
oc), short circuit current density (J
sc), and efficiency are increased.


---

## Body

## 1. Introduction

Due to its renewable and clean-energy characteristics, solar energy is destined to be an important energy source for the next generation. Recently, dye-sensitized solar cells (DSSCs) have attracted lots of attention because of their lower cost compared to the silicon based solar cells. DSSCs are based on photosensitization of mesoporous TiO2 films by absorbed sensitizers. The molecular engineering of porphyrin sensitizers is recently used in DSSCs and energy conversion efficiencies up to 13% have been reported [1]. In addition to organic dyes, semiconductor quantum dots (QDs) which absorb light in the visible spectrum are also good candidates to be a sensitizer of a DSSC cell. And there are some specific advantages of using semiconductor QDs as sensitizers. Due to the quantum confinement effect, the optical property and the band gap of a QD can be adjusted by changing the size of the QDs [2–4]. In addition, the QDs open up a way to utilize hot electrons and to generate multiple electron-hole pairs with a single photon through impact ionization [5, 6]. But there are some disadvantages about the QDs, such that the QDs often undergo photo corrosion and electrolyte corrosion [7, 8]. And we know that certain organic molecules are able to reduce the corrosions [7, 9]. In this work, we make the TiO2 sensitized by both CdS QDs and the N719 in DSSCs to improve the performance of DSSC and also to explore the principles involved.


## 2. Experimental

In our experiment, F-doped tin oxide was used as the substrate. Firstly, FTO glass substrates were ultrasonically soaked in deionized water, acetone, and absolute ethanol subsequently. Then the glass was soaked into the TiCl4 solution with the concentration of 0.04 mol/L for 30 min at 70°C. The TiO2 was coated on the FTO substrates and then sintered at 450°C for 30 min. The thickness of the TiO2 film was 8 μm which was controlled by the times of the screen printing. Here we used chemical bath deposition (CBD) to assemble QDs onto the TiO2 photoelectrode. And the particle size of QDs was controlled by adjusting the dipping time. The TiO2 film was firstly dipped into the Cd(NO3)2 ethanol solution (0.3 M) for 5 min, rinsed with the ethanol, and then dipped for another 5 min in the Na2S ethanol solution (0.1 M) and rinsed again with the ethanol. This is called one cycle, and here we assembled QDs for 2~10 cycles to discuss the effect of the particle size on the light absorbance. For the total dissolution of the solute, the ethanol and the deionized water are mixed as the solvent in which the proportion of the volume is 7 : 3.The TiO2 film with CdS QDs was soaked in the N719 for 44 hours. Then the TiO2 electrodes were incorporated into thin-layer sandwich-type cells with Pt-coated FTO as counter electrode and electrolyte solution. The working area of the sample was 0.25 cm2. The surface morphology of the samples was conducted with the SEM. Optical absorption spectra of the TiO2 electrodes were recorded by a UV/VIS/NIR spectrophotometer. The photocurrent-voltage (I-V) curves were measured by the electrochemical workstation under an illumination of xenon lamp. The irradiance is 100 mW/cm2 which is measured by a radiometer (FZ-A, Photoelectric Instrument Factory of Beijing Normal University).


## 3. Results and Discussion

The thickness of bare TiO2 film prepared using TiO2 powders of P25 was about 5 μm. Figure 1 shows the SEM of TiO2 with different amount of CdS, and (a) was TiO2 with CdS after 4 CBD cycles and (b) was 10 CBD cycles. From these images we can see that, with the increase cycles of the CdS, the interspaces of the TiO2 particles are becoming smaller and smaller; this result indicates that the CdS was assembled onto the surface of TiO2 particles, and the amount of the CdS QDs is increased with increasing CBD cycles. Figures 1(a) and 1(b) are SEM of TiO2 with different amount of CdS; Figures 1(c) to 1(e) are typical XRD patterns and TEM images of the photo anode.SEM of TiO2 with different amount of CdS, (a) 4 CBD cycles of CdS, (b) 10 CBD cycles of CdS, (c) typical XRD patterns, and (d) and (e) typical TEM images of the photo anode.
(a)
(b)
(c)
(d)
(e)Figure2 shows the absorbance spectra of CdS/TiO2 films in the visible region. From this figure we can see that, with the increase of the cycles of CdS, the absorbance intensities are becoming stronger and stronger, and this suggests the increased number of CdS QDs. The extrapolations at the absorption edges show a red shift in the spectra. The shift suggests a growth in QD size with increasing CBD cycles. And this can be explained by the decrease in band gap energy arising from the increasing particle size in the quantum size regime.Figure 2
The absorbance spectra of CdS/TiO2 films in the visible region.The parameters of QDSSCs were tabulated in Table1, and the corresponding trend of the parameters with increasing CBD cycles was shown in Figure 3.Table 1
The parameters of QDSSCs with CBD cycles of 2~10.
Cycles of CBD
J
sc (mA/cm2)
V
oc (V)
FF
Efficiencies (%)
2
1.592
0.433
0.41
0.285
4
2.816
0.442
0.47
0.586
6
3.91
0.483
0.39
0.745
8
3.765
0.408
0.39
0.596
10
3.672
0.403
0.30
0.438Trend of theJ
sc, V
oc, FF, and efficiency with different CBD cycles.
(a)
(b)
(c)
(d)From Table1 and Figure 3 we can see that with the increasing cycles of CBD, the short circuit current (J
sc), open circuit voltage (V
oc), and the efficiency are improved before the CBD cycle is 6 and fill factor (FF) before 4, but these parameters are decreased with the continuing increase of CBD cycles. This suggests, with the increasing CBD cycles (before the cycles of 6), the size of the QDs is becoming larger and the energy level has been adjusted. This makes the V
oc increase with the increase of the CBD cycles. This is according to the absorbance spectra of CdS/TiO2 films. And also the more CBD cycles are, the bigger J
sc is becoming, and this suggests the additional amount of CdS QDs. So is the efficiency. But when the CBD cycles are 8 or more, the J
sc, V
oc, FF, and efficiency are decreased. This may be because the spaces between the TiO2 particles are becoming blocked, and the electrolyte getting into the spaces is becoming harder, and this makes the hole and electron recombination easier, so the J
sc decreases. This also causes the FF to decrease and so does the efficiency. So we can get the best efficiency with the CdS sensitized TiO2, which is 0.745% with the CBD cycle of 6. But we can see that the efficiency is still low, and the QDs also undergo photo corrosion and electrolyte corrosion. So here we make the cosensitized DSSC.Plots of photocurrent density against voltage of the cosensitized DSSC are shown in Figure4. And the corresponding readings are tabulated in Table 2. When the TiO2 was sensitized both by CdS and N719, the efficiency increases as shown in Table 2. We can see that, with the assembly of CdS QDs, the efficiency first increases from 4.39% to 5.37%, but with the CBD cycle of 4 it decreases to 2.74% and when the cycle is 10, the efficiency decreases to 0.24%.Table 2
Parameters of DSSCs constructed with different sensitization conditions.
Sensitization architecture
J
sc (mA/cm2)
V
oc (V)
FF
Efficiencies
N719 (No QD)
8.421
0.709
0.73
4.39%
2
10.024
0.729
0.73
5.37%
4
6.451
0.690
0.63
2.79%
6
3.710
0.644
0.10
0.24%Figure 4
J-V curves of N719-sensitized DSSC and N719 and CdS cosensitized DSSCs.The trend of the parameters of the DSSC is shown in Figure5. From this figure we can see that when the CBD cycle is 2, the J
sc, V
oc, FF, and efficiency are the best, and when the cycles increase these parameters become smaller.Trend of theJ
sc, V
oc, FF, and efficiency with different CBD cycles of cosensitized solar cell.
(a)
(b)
(c)
(d)The phenomena observed above can be explained as follows [9–13]: with the assembly of the CdS QDs, an energy level is inserted between the conduction band of TiO2 and N719 as shown in Figure 6. When the CBD cycle is 2, the conduction band of the CdS is becoming closer to the conduction band of TiO2. Then the electron transition is becoming easier, so the J
sc increases. But with the increase of the CBD cycles (such as 4), the spaces between the TiO2 particles are becoming blocked, and the electrolyte getting into the spaces is becoming harder. What is more is that the electrons can transfer between the TiO2 particles, so the recombination between the electron and hole is becoming easier, so the J
sc decreases. This also causes the FF to decrease and so does the efficiency. So we can see that when CBD cycle is 2, the best efficiency can be obtained. The performance to other related cosensitized DSSCs is compared in Table 3.Table 3
The comparisons of the performance to other related cosensitized DSSCs.
Number
Quantum dot
Dye
Photo anode
Efficiencies (%) (noncosensitizing)
Efficiencies (%) (cosensitizing)
Increment of efficiencies (%)
References
0
CdS
N719
TiO2
4.39
5.37
22.3
This work
1
CdS
N719
TiO2
1.67
2.36
41.3
[9]
2
CdS
N719
ZnO/ZnS
1.16
1.59
37.1
[10]
3
PbS
N719
TiO2
5.95
6.35
6.7
[11]
4
Ag2S/CdS
N3
TiO2
0.98
1.66
69.4
[12]
5
Ag2S
N3
TiO2 nanotube
3.64
4.40
20.9
[13]Figure 6
Representation of energy level diagram in a cosensitized DSSC by N719 and CdS.


## 4. Conclusions

The CdS QDs alone can sensitize TiO2 films. In order to avoid photo corrosion and electrolyte corrosion, the TiO2 films are cosensitized by CdS and N719. The band gap of CdS QDs was tuned by CBD cycles. With the inserting energy level of CdS, the V
oc and J
sc were increased and so was the efficiency. The efficiency was improved from 4.39% to 5.37% when the CBD cycle was 2.



---

*Source: 219704-2014-05-22.xml*