# Structural, Thermal, Optical, Electrical, and Adhesive Characteristics of FePdB Thin Films

Authors: Yuan-Tsung Chen
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

To study the structural, thermal, electrical, optical, and adhesive properties of magnetic FePdB thin films, 25–200-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were deposited on a glass substrate by direct current (DC) magnetron sputtering at room temperature (RT). X-ray diffraction (XRD) patterns indicated that the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were amorphous, whereas the 100–200-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were crystalline, with a face-centered cubic (FCC) FePd (111) textured structure. The activation energy of the Fe40Pd40B20 and Fe60Pd20B20 thin films decreased as thickness was increased. The 25-Å-thick Fe40Pd40B20 film exhibited the highest resistivity, whereas the 200-Å-thick Fe60Pd20B20 film exhibited the lowest resistivity. Increasing the thickness and crystallization reduced transmission. The Fe40Pd40B20 thin films exhibited higher surface energy and stronger adhesion than did Fe60Pd20B20 thin films.


---

## Body

## 1. Introduction

FePdB is a new ferromagnetic (FM) material, which can be inserted to magnetic tunnel junction (MTJ) with a free layer or pinned layer in high-density read/write head sensors, spin-valve structures, and magnetoresistance random access memory (MRAM) applications [1–3]. To obtain both high recording density and high tunneling magnetoresistance (TMR), various perpendicular magnetic anisotropy (PMA) materials are used in combination with FM materials such as FePdB, which are known to provide high TMR and MgO tunnel barriers [4, 5]. FePdB alloy metal, a newly developed material, has a huge range of unknown uncertainty that attracted great attention to its characteristics. Transparent ZnO film was also used with FePdB magnetic film to form a bilayer, which can be used in magnetic and photoelectrical applications [6]. It would be of interest to study the relationship between crystalline structural, thermal, optical, electric, and adhesive effects of magnetic FePdB thin films. FePdB alloy is a soft FM material of which investigations are scarce. The research group of Choi et al. reported that FePdB film was placed to CoFeB film as the top and bottom FM layers of MTJs, thus indicating the substantial interest in examining FePdB film [5]. This study investigated the characteristics of crystalline structural, thermal, electric, optical, and adhesive effects of magnetic FePdB thin films.


## 2. Experimental Details

FePdB thin films (25, 50, 75, 100, and 200 Å) were deposited on a glass substrate at room temperature (RT) through direct current (DC) magnetron sputtering. The typical base chamber pressure exceeded 2 × 10−6 Torr, and the Ar working chamber pressure was 5 × 10−3 Torr. The target compositions of the two FePdB alloys were 40 at.% Fe, 40 at.% Pd, and 20 at.% B and 60 at.% Fe, 20 at.% Pd, and 20 at.% B. X-ray diffraction (XRD) with a CuKα1 line (Philips X’pert) was adopted to determine the structures of the alloys. The thermal properties of the FePdB thin films were determined using differential scanning calorimetry (DSC) at heating rates of 10–40 K/min. The electrical properties of the FePdB thin films at RT were studied using a traditional four-point resistance meter. The optical properties of the FePdB thin films were determined using Spectra Smart Analyzer. The surface energy of the FePdB films was calculated based on measurements of the contact angle, using water and diiodomethane as test liquids.


## 3. Results and Discussion

### 3.1. Structure and Thermal Properties

Figures1(a) and 1(b) show the XRD patterns of the Fe40Pd40B20 and Fe60Pd20B20 thin films in 2θ range from 20° to 90° [7]. The XRD results revealed that the thinnest 25 Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were similar to XRD pattern of glass substrate. The thinnest 25 Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were of amorphous structure. Moreover, the thicker 50–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were no apparent crystalline phenomena and the structures were also of amorphous status. An obvious face-centered cubic (FCC) structure and an FePd (111) crystalline peak with an approximately 2θ of 40° were identified in 100–200-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films. According to previous references [8, 9], it can also reasonably be concluded that the diffracted peak is FePd (111). Therefore, the FCC FePd (111) was identified herein. The main crystalline peak of the Fe60Pd20B20 thin film was stronger than that of the Fe40Pd40B20 thin film. This result indicated that the crystallization of the Fe60Pd20B20 thin film was more favorable than that of the Fe40Pd40B20 thin film. Thermal analysis was performed to clarify this result.Figure 1
X-ray diffraction patterns of FePdB thin films. (a) Fe40Pd40B20 and (b) Fe60Pd20B20.
(a)
(b)Figure2 shows the activation energy (Q) of crystallization of the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films [7]. The activation energy was determined using Kissinger fitting as a function of thickness. Because these films were amorphous according to XRD, the activation energy (Q value) of the 25–75-Å-thick Fe40Pd40B20 film decreased from 86.3 to 66.1 kJ/mole, and the Q value of the 25–75-Å-thick Fe60Pd20B20 film decreased from 49.8 to 44.1 kJ/mole. The activation energy of both the Fe40Pd40B20 and Fe60Pd20B20 thin films decreased as the thickness increased, thus lowering the Q value and promoting crystallization. Higher activation energy corresponds to stronger resistance to crystallization. The 75-Å-thick FePdB film exhibited the lowest activation energy. The amorphous state can be easily transformed into a crystalline structure by applying a thermal driving force. In contrast to the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films, both 25-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films exhibited the highest Q value, suggesting that they were difficult to crystallize.Figure 2
Activation energy estimated from Kissinger-fitted plots for amorphous Fe40Pd40B20 and Fe60Pd20B20 thin film with thicknesses of 25–75 Å.


### 3.2. Electrical Analysis

Figures3(a) and 3(b) show the electrical resistivity (ρ) of the Fe40Pd40B20 and Fe60Pd20B20 thin films with five thicknesses. The electrical resistivity decreased as the thickness of the Fe40Pd40B20 and Fe60Pd20B20 films increased. The resistivity value of the Fe40Pd40B20 films decreased from 23176 to 6828 Ω·cm, and the resistivity value of the Fe60Pd20B20 films decreased from 4710 to 1145 Ω·cm. Thus, the 25-Å-thick Fe40Pd40B20 film exhibited the highest resistivity, whereas the 200-Å-thick Fe60Pd20B20 film exhibited the lowest resistivity. The scattering of electrons from the grain boundaries and surface, as well as greater crystallization, causes thicker films to have higher resistivity [10, 11]. According to the XRD results, the crystallization of the Fe60Pd20B20 thin films was more favorable than that of the Fe40Pd40B20 thin films. The resistivity value of the Fe40Pd40B20 films of any thickness was higher than that of Fe60Pd20B20 films. Comparison to other magnetic Fe2Si thin films reveals that the resistivity value of FePdB films is around 9 times smaller than Fe2Si films [12]. Magnetic FePdB films are typically applied in semiconductor processes, and resistivity is a critical parameter in electrical applications.Figure 3
Electrical resistivity (ρ) as a function of Fe40Pd40B20 and Fe60Pd20B20 thickness. (a) Fe40Pd40B20 and (b) Fe60Pd20B20.
(a)
(b)


### 3.3. Optical Analysis

Figures4(a) and 4(b) show the optical transmission (T%) of the Fe40Pd40B20 and Fe60Pd20B20 thin films with five thicknesses. When the wavelength was 1000 nm for the entire transmittance plot, this indicates that it was the highest transmittance value in the visible light wavelength 1000 nm. As shown in Figure 4(a), when the total wavelength ranged from 400 to 1000 nm, the transmission of the Fe40Pd40B20 thin films gradually increased from approximately 20% to 63%. As the thickness of the Fe40Pd40B20 thin films increased, T% decreased. As shown in Figure 4(b), when the total wavelength ranged from 400 to 1000 nm, the transmission of the Fe60Pd20B20 thin film exhibited two gradually rising curves. The T% of the 25–75-Å-thick Fe60Pd20B20 films increased from 20% to 40%, but the T% of the 100–200-Å-thick Fe60Pd20B20 films increased from 5% to 20%. This phenomenon was inferred based on the crystallization observed using XRD. Large grains either in thicker films are reasonably concluded to inhibit the transfer of the photon signal through the film, causing low transmission [13].Figure 4
The transmission (%) of optical property as a function of Fe40Pd40B20 and Fe60Pd20B20 thin film thickness. (a) Fe40Pd40B20 and (b) Fe60Pd20B20.
(a)
(b)


### 3.4. Analysis of Surface Energy and Adhesion

The surface energy was determined based on the contact angle and some calculations [14–16]. Figure 5 shows the surface energy of the Fe40Pd40B20 and Fe60Pd20B20 thin films with five thicknesses. The surface energy of the Fe40Pd40B20 thin films decreased (65.592 to 64.204 mJ/mm2, black line of Figure 5) as the thickness was increased. The surface energy of Fe60Pd20B20 thin films also decreased (64.304 to 63.554 mJ/mm2, red line of Figure 5) as the thickness was increased. The surface energy of the Fe40Pd40B20 thin films was higher than that of the Fe60Pd20B20 thin films. Low surface energy corresponds to weak adhesion. Thus, the adhesion capability of the Fe40Pd40B20 thin films was higher than that of the Fe60Pd20B20 thin films. Nevertheless, a high degree of crystallization results in low surface energy and weak adhesion [17]. According to the XRD results, the crystallization of the Fe60Pd20B20 thin films was more favorable than that of the Fe40Pd40B20 thin films. This analysis of surface energy and adhesion was consistent with the crystallization results obtained using XRD. Hence, the 25-Å-thick Fe40Pd40B20 film exhibited the lowest crystallization, as well as the highest surface energy and strongest adhesion, and can be used in adhesive applications such as free layers for magnetic tunnel junctions. In summary, the Fe60Pd20B20 thin films exhibited more favorable crystallization, lower resistance, lower transmission, lower surface energy, and weaker adhesion than did the Fe40Pd40B20 films.Figure 5
Surface energy as a function of Fe40Pd40B20 and Fe60Pd20B20 thickness.


## 3.1. Structure and Thermal Properties

Figures1(a) and 1(b) show the XRD patterns of the Fe40Pd40B20 and Fe60Pd20B20 thin films in 2θ range from 20° to 90° [7]. The XRD results revealed that the thinnest 25 Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were similar to XRD pattern of glass substrate. The thinnest 25 Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were of amorphous structure. Moreover, the thicker 50–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were no apparent crystalline phenomena and the structures were also of amorphous status. An obvious face-centered cubic (FCC) structure and an FePd (111) crystalline peak with an approximately 2θ of 40° were identified in 100–200-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films. According to previous references [8, 9], it can also reasonably be concluded that the diffracted peak is FePd (111). Therefore, the FCC FePd (111) was identified herein. The main crystalline peak of the Fe60Pd20B20 thin film was stronger than that of the Fe40Pd40B20 thin film. This result indicated that the crystallization of the Fe60Pd20B20 thin film was more favorable than that of the Fe40Pd40B20 thin film. Thermal analysis was performed to clarify this result.Figure 1
X-ray diffraction patterns of FePdB thin films. (a) Fe40Pd40B20 and (b) Fe60Pd20B20.
(a)
(b)Figure2 shows the activation energy (Q) of crystallization of the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films [7]. The activation energy was determined using Kissinger fitting as a function of thickness. Because these films were amorphous according to XRD, the activation energy (Q value) of the 25–75-Å-thick Fe40Pd40B20 film decreased from 86.3 to 66.1 kJ/mole, and the Q value of the 25–75-Å-thick Fe60Pd20B20 film decreased from 49.8 to 44.1 kJ/mole. The activation energy of both the Fe40Pd40B20 and Fe60Pd20B20 thin films decreased as the thickness increased, thus lowering the Q value and promoting crystallization. Higher activation energy corresponds to stronger resistance to crystallization. The 75-Å-thick FePdB film exhibited the lowest activation energy. The amorphous state can be easily transformed into a crystalline structure by applying a thermal driving force. In contrast to the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films, both 25-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films exhibited the highest Q value, suggesting that they were difficult to crystallize.Figure 2
Activation energy estimated from Kissinger-fitted plots for amorphous Fe40Pd40B20 and Fe60Pd20B20 thin film with thicknesses of 25–75 Å.


## 3.2. Electrical Analysis

Figures3(a) and 3(b) show the electrical resistivity (ρ) of the Fe40Pd40B20 and Fe60Pd20B20 thin films with five thicknesses. The electrical resistivity decreased as the thickness of the Fe40Pd40B20 and Fe60Pd20B20 films increased. The resistivity value of the Fe40Pd40B20 films decreased from 23176 to 6828 Ω·cm, and the resistivity value of the Fe60Pd20B20 films decreased from 4710 to 1145 Ω·cm. Thus, the 25-Å-thick Fe40Pd40B20 film exhibited the highest resistivity, whereas the 200-Å-thick Fe60Pd20B20 film exhibited the lowest resistivity. The scattering of electrons from the grain boundaries and surface, as well as greater crystallization, causes thicker films to have higher resistivity [10, 11]. According to the XRD results, the crystallization of the Fe60Pd20B20 thin films was more favorable than that of the Fe40Pd40B20 thin films. The resistivity value of the Fe40Pd40B20 films of any thickness was higher than that of Fe60Pd20B20 films. Comparison to other magnetic Fe2Si thin films reveals that the resistivity value of FePdB films is around 9 times smaller than Fe2Si films [12]. Magnetic FePdB films are typically applied in semiconductor processes, and resistivity is a critical parameter in electrical applications.Figure 3
Electrical resistivity (ρ) as a function of Fe40Pd40B20 and Fe60Pd20B20 thickness. (a) Fe40Pd40B20 and (b) Fe60Pd20B20.
(a)
(b)


## 3.3. Optical Analysis

Figures4(a) and 4(b) show the optical transmission (T%) of the Fe40Pd40B20 and Fe60Pd20B20 thin films with five thicknesses. When the wavelength was 1000 nm for the entire transmittance plot, this indicates that it was the highest transmittance value in the visible light wavelength 1000 nm. As shown in Figure 4(a), when the total wavelength ranged from 400 to 1000 nm, the transmission of the Fe40Pd40B20 thin films gradually increased from approximately 20% to 63%. As the thickness of the Fe40Pd40B20 thin films increased, T% decreased. As shown in Figure 4(b), when the total wavelength ranged from 400 to 1000 nm, the transmission of the Fe60Pd20B20 thin film exhibited two gradually rising curves. The T% of the 25–75-Å-thick Fe60Pd20B20 films increased from 20% to 40%, but the T% of the 100–200-Å-thick Fe60Pd20B20 films increased from 5% to 20%. This phenomenon was inferred based on the crystallization observed using XRD. Large grains either in thicker films are reasonably concluded to inhibit the transfer of the photon signal through the film, causing low transmission [13].Figure 4
The transmission (%) of optical property as a function of Fe40Pd40B20 and Fe60Pd20B20 thin film thickness. (a) Fe40Pd40B20 and (b) Fe60Pd20B20.
(a)
(b)


## 3.4. Analysis of Surface Energy and Adhesion

The surface energy was determined based on the contact angle and some calculations [14–16]. Figure 5 shows the surface energy of the Fe40Pd40B20 and Fe60Pd20B20 thin films with five thicknesses. The surface energy of the Fe40Pd40B20 thin films decreased (65.592 to 64.204 mJ/mm2, black line of Figure 5) as the thickness was increased. The surface energy of Fe60Pd20B20 thin films also decreased (64.304 to 63.554 mJ/mm2, red line of Figure 5) as the thickness was increased. The surface energy of the Fe40Pd40B20 thin films was higher than that of the Fe60Pd20B20 thin films. Low surface energy corresponds to weak adhesion. Thus, the adhesion capability of the Fe40Pd40B20 thin films was higher than that of the Fe60Pd20B20 thin films. Nevertheless, a high degree of crystallization results in low surface energy and weak adhesion [17]. According to the XRD results, the crystallization of the Fe60Pd20B20 thin films was more favorable than that of the Fe40Pd40B20 thin films. This analysis of surface energy and adhesion was consistent with the crystallization results obtained using XRD. Hence, the 25-Å-thick Fe40Pd40B20 film exhibited the lowest crystallization, as well as the highest surface energy and strongest adhesion, and can be used in adhesive applications such as free layers for magnetic tunnel junctions. In summary, the Fe60Pd20B20 thin films exhibited more favorable crystallization, lower resistance, lower transmission, lower surface energy, and weaker adhesion than did the Fe40Pd40B20 films.Figure 5
Surface energy as a function of Fe40Pd40B20 and Fe60Pd20B20 thickness.


## 4. Conclusions

The XRD patterns indicated that the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were amorphous, whereas the 100–200-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films were crystalline, with an FCC FePd (111) textured structure at approximately 2θ = 40°. Because of their amorphous structure, the 25–75-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films exhibited decreasing activation energy as the thickness was increased. The 75-Å-thick FePdB film exhibited the lowest activation energy. The 25-Å-thick Fe40Pd40B20 and Fe60Pd20B20 films exhibited the highest Q value, suggesting that they are difficult to crystallize. The 25-Å-thick Fe40Pd40B20 film exhibited the highest resistivity, whereas the 200-Å-thick Fe60Pd20B20 film exhibited the lowest resistivity. Transmission decreased when both thickness and crystallization increased. The Fe40Pd40B20 thin films exhibited higher surface energy and stronger adhesion than did the Fe60Pd20B20 thin films. The Fe40Pd40B20 thin films exhibited less favorable crystallization, higher resistance, higher transmission, higher surface energy, and stronger adhesion than did the Fe60Pd20B20 thin films.



---

*Source: 216495-2015-08-23.xml*