# Study of Low Voltage Prebreakdown Sites in Multicrystalline Si Based Cells by the LBIC, EL, and EDS Methods

Authors: V. I. Orlov; E. B. Yakimov; E. P. Magomedbekov; A. B. Danilin
Journal: Advances in Condensed Matter Physics
 (2017)

---

## Abstract

Breakdown sites in multicrystalline Si solar cells have been studied by reverse-bias electroluminescence, electron beam induced current (EBIC) and laser beam induced current (LBIC), and Energy Dispersive X-Ray Spectroscopy methods. In the breakdown sites revealed by EL at small reverse bias (~5 V), the enhanced aluminum and oxygen concentration is revealed. Such breakdowns can be located inside the depletion region because they are not revealed by the EBIC or LBIC methods. Breakdowns revealed by EL at larger bias correlate well with extended defects in the EBIC and LBIC images.


---

## Body

## 1. Introduction

Solar cells made from Si regularly suffer from shunts, which are internal short circuits degrading the parameters of the cells and often even preventing their applicability (see [1–6] and the references therein). Therefore, it is very important to study their nature and to understand the mechanisms of their formation. In spite of numerous studies done by various authors, the cause and occurrence of shunts and electrical breakdown in solar cells are not fully understood yet [6]. The reason for this misunderstanding is determined by the manifold nature of shunts, especially in multicrystalline Si, and by a variety of extended defects and impurities in this material. Among various types of shunts, those associated with local breakdown of solar cells under reverse bias can be mentioned [5–9]. It was shown that such breakdown sites can be revealed by reverse-bias electroluminescence (EL) [5–10] and their classification was carried out [6, 11]. The correlation of EL images with those obtained by the electron beam induced current (EBIC) method sometimes allows finding a link between these sites and extended defects [6, 11]. However, for some breakdown sites (usually revealed at low reverse bias), no correlation with extended defects was revealed [6, 7, 11].In the present study, the breakdown sites in multicrystalline Si based solar cells are revealed by the reverse-bias EL. The EL images obtained at different reverse-bias values are compared with those obtained by the EBIC and light beam induced current (LBIC) methods to correlate them with extended defects. The local composition at the breakdown sites was studied.


## 2. Experimental

Solar cells studied were formed on the multicrystalline Si wafers, 200μm thick and 150 × 150 mm2 in size, cut from bricks grown by casting. The wafer surface was acidic textured. The emitter was produced by POCl3 diffusion. SiNx layer was deposited by PECVD for passivation. Front Ag and rear Al contacts were screen-printed and fired. The samples for investigations with an area of a few cm2 were cut from the solar cells. Most parts of the grain boundaries in these samples, as obtained by Electron Backscatter Diffraction, are of Σ3 and random types and the dislocation density varies in the range from 105 to 106 cm−2 [12].The electroluminescence images were recorded using an optical microscope and a highly sensitive video camera equipped with a silicon charge-coupled device array. The EBIC investigations were carried out with a scanning electron microscope (SEM) JSM 840A (JEOL) at room temperature with beam energy of 35 keV and beam current of 10−10 A. The LBIC measurements were carried out at room temperature with a 980 nm semiconductor laser as an excitation source. Solar cell breakdown is often associated with precipitates or surface contamination [6, 7, 13]; therefore, to study the nature and composition of these precipitates and contamination, the local composition in the breakdown sites was determined by Energy Dispersive X-Ray Spectroscopy (EDS) in the JSM 6490 (JEOL) with INCA 350 system (Oxford Instruments).


## 3. Results and Discussions

A large area EL image of solar cell obtained at reverse bias of 10 V is shown in Figure1 (i.e., in the regime, in which the breakdown sites can be associated with decorated extended defects [6, 11]). A lot of inhomogeneously distributed breakdown defects of different forms can be seen as bright points. It should be mentioned that large enough areas are free from breakdown defects. The images of a cell fragment containing breakdown defects were obtained at different reverse-bias values. Such images with higher magnification are shown in Figure 2. It is seen that at small bias only a few breakdown sites can be revealed as bright spots (shown with white arrows). Typical breakdown sites revealed at small bias (so-called type 1 breakdown [6, 11, 14]) are shown in Figures 2(b) and 2(c) as two bright spots with brightness increasing with reverse bias. In Figure 2(c) obtained at 19 V reverse bias, some additional bright points appear (line of bright points between two bright defects). An analysis of EBIC and LBIC images of the same region shows that the bright spots revealed at larger reverse voltage correlate well with some random grain boundaries (compare Figures 2(c) and 3). This is in good agreement with the previously observed results for breakdowns of type II [6, 11] that allows associating these breakdown sites with decorated grain boundaries. As seen in Figure 2(c), the EL images of such breakdowns are not continuous lines but instead consist, as in [11], of bright point sets. Moreover, not all electrically active grain boundaries introduce breakdown sites. It should be noted that, in the EBIC images of grain boundary producing the line breakdown sites (Figure 3(a)), some dark points and lines can be also seen. That is, precipitates decorating this grain boundary can be revealed in the EBIC mode. However, our EDS investigations do not reveal any compositional changes in such breakdown sites. Of course, it should be taken into account that the sensitivity of EDS method in the scanning electron microscope due to rather large excitation volume is rather low and this method cannot detect small precipitates. Thus, it can be stated that, in the cells studied, the precipitates formed on grain boundaries and other extended defects are the reason for type II breakdown in accordance with previous investigations [6, 11]; however, the composition of these precipitates was not established. It only could be mentioned that direct evidence was previously obtained (see [6] and the references therein) that FeSi2 precipitates are responsible for type II breakdown and probably this is the case in the studied cells also. It should be also mentioned that most Σ3 grain boundaries cannot be revealed in the EBIC or LBIC modes due to their low recombination activity [15]. An absence of line breakdown defects, which cannot be associated with the defects in EBIC and LBIC images, may indicate that Σ3 grain boundaries do not cause breakdown. It should be also noted that while at such bias type III avalanche breakdown is usually observed [6], in the samples studied, probably type II breakdown regime is still realized because all additional breakdown sites can be associated with grain boundaries; however, this point was not studied in detail here.Figure 1
EL image of a large area fragment of structure under study obtained at 10 V reverse bias. The distance between contact strips is 2.3 mm.Figure 2
EL images of a solar cell fragment obtained at reverse biasUb = 0 V (а), 5 V (b), and 19 V (c). Type I breakdown sites are shown with white arrows.
(a)
(b)
(c)Figure 3
EBIC (a) and LBIC (b) images of the same region as in Figure2.
(a)
(b)Further, we will focus on the breakdown sites shown in Figure2(b). A comparison of EL images with EBIC and LBIC images of the same region (Figure 3) does not reveal any electrically active extended defects in these sites that correlate with previous investigations [6, 11]. Therefore, it could be assumed that the corresponding defects are located in the depletion region or in highly doped n+-layer, where they do not produce the EBIC or LBIC contrast. In the secondary electron image surface stains were observed at some breakdown sites (Figures 4 and 5) similar to those observed in [7] but at other sites no surface defects were revealed at the positions of type I breakdowns. EDS mapping reveals the enhanced aluminum and oxygen concentrations at these sites (Figures 4 and 6) that well correlate with the results obtained in [2, 7], where it was concluded that these breakdowns arise due to contamination of the wafer with aluminium particles before and during processing. It should be noted that, as shown in [16], Al spikes indeed can be formed and in n-Si they can produce short circuits in solar cells. Here, p-Si is used; therefore, Al exhibiting precipitate behavior can be different from that in [16]. Nevertheless, the results presented confirm the effect of Al containing precipitates on the low voltage solar cell breakdown in accordance with [7]. It should be also noted that Al contacts were made on the back surface while the Al precipitates are revealed on the front one. Al can come from Ag paste used for top contact formation, in which Al sometimes is added, although the breakdown sites studied are located far enough from the contact grid. (EL cannot reveal breakdown sites under contacts.) It should be mentioned that the composition of some breakdown sites (e.g., right one in Figure 2(b)) is more complex. Besides aluminum and a small amount of oxygen, the enhanced concentration of carbon and sodium is also revealed (Figure 6). As assumed in [17, 18], SiC filaments can be a reason for some shunts. Therefore, for these particular defects, an additional possible reason for breakdown could be considered (i.e., Al spikes may be also formed on the SiC filaments).Figure 4
SE image and EDS maps of aluminum and oxygen distribution for the left breakdown site in Figure2(b).Figure 5
SE image of the right breakdown site in Figure2(b).Figure 6
EDS maps for the right breakdown site in Figure2(b).In order to determine the spectral distribution of the luminescence arising from the type I breakdowns spectrally resolved EL measurements were performed at different reverse voltages for a few of them. Typical EL spectra obtained from the breakdowns of type I are presented in Figure7. It is seen that the spectra are practically independent of the applied reverse bias. They exhibit a broad band ranging from 400 nm beyond 750 nm. These spectra are similar to those observed in [7]; however, they have a maximum at about 570 nm; that is, they are blue-shifted according to 715 nm observed in [7].Figure 7
EL spectra of breakdowns measured at reverse bias of 5 V (1), 6 V (2), and 9 V (3). The spectrum of breakdown free region measure at 9 V is also shown (4).


## 4. Conclusion

Breakdown sites in multicrystalline Si solar cells have been studied by reverse-bias EL, EBIC, LBIC, and EDS methods. It is shown that the breakdown sites revealed by EL at small reverse bias in breakdown regime 1 can be associated with Al spikes located inside the depletion region. Breakdowns revealed by EL at larger bias in accordance with previous investigations correlate well with extended defects in the EBIC and LBIC images and can be associated with small precipitates formed on the random grain boundaries.



---