# Antifungal Applications of Ag-Decorated Hydroxyapatite Nanoparticles

Authors: C. A. Zamperini; R. S. André; V. M. Longo; E. G. Mima; C. E. Vergani; A. L. Machado; J. A. Varela; E. Longo
Journal: Journal of Nanomaterials
 (2013)

---

## Abstract

Pure hydroxyapatite (HA) and hydroxyapatite decorated with silver (HA@Ag) nanoparticles were synthesized and characterized. The antifungal effect of HA@Ag nanoparticles in a distilled water solution was evaluated againstCandida albicans. The origin of the antifungal activity of the HA@Ag is also discussed. The results obtained showed that the HA nanorod morphology remained the same with Ag ions decorations on the HA structure which were deposited in the form of nanospheres. Interaction where occurred between the structure and its defect density variation in the interfacial HA@Ag and intrafacial HA region with the fungal medium resulted in antifungal activity. The reaction mechanisms involved oxygen and water adsorption which formed an active complex cluster. The decomposition and desorption of the final products as well as the electron/hole recombination process have an important role in fungicidal effects.


---

## Body

## 1. Introduction

HA, Ca10(PO4)6(OH)2, is the major mineral component of human bone and other calcified tissues [1]. Thus, due to the similarity with bone composition and its ability to bond strongly with human hard tissue, the synthesis of HA (a bioceramic material) is of great interest for several clinical applications in the biomedical field [2, 3]. Synthetic HA is a versatile inorganic material that also exhibits desirable properties such as biocompatibility, bioactivity, and osteoconductivity. In medicine and dentistry, due to its bioactive properties, HA has been successfully used for bone reconstructions and as coatings for dental implants; also, the structure is similar to the human bone mineral component. However, various sources of infections exist in these biomedical interventions, including environment surfaces and surgical equipment as well as microorganisms present in body tissues. Hence, the risk of infectious complications is high and may lead to failures which entail the need for subsequent surgery and medical costs in addition to the pain and suffering of patients. Candida albicans is among the most frequently isolated microorganisms from human infections, mainly in immunocompromised patients [4–6]. Although C. albicans is an eukaryotic commensal microorganism of human mucosal surfaces, when there is impairment of the host immunity, it can cause serious superficial and deep infections [4]. In general, the in vivo colonization of tissues and surfaces by microorganisms is related to biofilm formation. Biofilm-associated C. albicans cells are more resistant to antifungals commonly used compared to cells grown in planktonic form [5]. Therefore, the synthesis of HA with antifungal properties against planktonic and biofilm cells would be an important strategy to inhibit fungal colonization and, consequently, the incidence of surgical infections.Researchers have reported that Ag-based compounds have broad-spectrum activity and a low propensity to induce microbial resistance. Silver nanoparticles (AgNPs) may attach to the cell membrane [3, 7] and cause structural changes, and, consequently, cell death. Additionally, the formation of free radicals [8] and the release of ions by nanoparticles may contribute to the antimicrobial activity of AgNP [9, 10]. These results suggest that the incorporation of an antifungal agent such as AgNP on HA could be a step toward the formulation of new therapeutic agents.Different synthesis methods have been reported in the literature to obtain HA crystals [11–13]. However, these procedures require long processing times as well as high temperatures which creates challenges in the development of a feasible method for the synthesis of HA nanocrystals. In this context, to obtain lower synthesis time and temperature requirements, the microwave-assisted hydrothermal (HTMW) [14, 15] method has been used in recent years and is one of the most promising methods to prepare nanomaterials with controlled size and shape [16]. Nevertheless, the challenge remains to prepare multicomponent or hybrid structures where two or more nanocrystal domains of different materials with individually tailored properties are integrated into one nanostructure.Recently, the synthesis of Ag-doped nanocrystalline HA nanoparticles by a coprecipitation method has been reported and the antibacterial and antifungal activities were evaluated [17–19]. In these investigations, an antimicrobial effect was observed against Gram-negative and Gram-positive bacteria [17, 18] and Candida krusei, a fungal species [19]. In the present study, we report the synthesis of HA nanoparticles decorated with silver through a co-precipitation method with an HTMW treatment using calcium nitrate and ammonium phosphate as precursors. The silver was incorporated into the HA matrix after the synthesis. The HA@Ag powder was structurally characterized by high-resolution transmission electron microscopy (HR-TEM), X-ray diffraction (XRD), FT-Raman spectroscopy, and UV-visible spectroscopy (UV-vis). The potential fungistatic and fungicidal effects of the HA@Ag in solution against C. albicans were evaluated by determining the minimum inhibitory concentration (MIC) and minimum fungicidal concentration (MFC). In addition, the effects of the HA@Ag solution against the biofilm formation of C. albicans were also evaluated. To the authors’ knowledge, such effects of HA@Ag on C. albicans have not been widely evaluated [20].


## 2. Experimental Section

### 2.1. Materials and Synthesis

For the synthesis of HA, two aqueous solutions were prepared: a calcium nitrate tetrahydrate solution (Mallinckrodt, 99.9%) and an ammonium phosphate solution (Mallinckrodit 99.4%). The ammonium phosphate solution was then dripped into the calcium solution with constant agitation. The system was kept under flowing N2 throughout the mixing, and the pH solution was maintained at approximately 11 with the addition of ammonium hydroxide. The suspension containing the white solid precipitate was placed in a 100 mL Teflon autoclave which was sealed and loaded into the HTMW system using 2.45 GHz microwave radiation with 800 W of power. The system was heated to 140°C and maintained at this temperature for 1 minute at a heating rate of 140°C/min under constant pressure (approximately 3.0 bar). After treatment, the autoclave was naturally cooled to room temperature. The resultant product was washed with deionized water several times until a neutral pH was obtained and then dried in an oven. HA@Ag was synthesized using the previously prepared HA powder dispersed in distilled water, and the pH was adjusted to 5 with HNO3. The solution was stirred at 60°C, and then 5 mL of AgNO3 solution (1.4 × 10−2 M) was added. The precipitate was washed to pH 7 and then again dried in an oven. The working concentration was 1 mol HA : 1 mol Ag.


### 2.2. Characterization of the HA@Ag

Morphology and size characterizations were performed by transmission electron microscopy (TEM, Tecnai G2TF20, FEI). To confirm the presence of Ag, an energy dispersive X-ray (EDX) measurement was taken in the same apparatus. All measurements were taken at room temperature. HA@Ag samples were characterized by XRD using a Rigaku DMax 2500PC diffractometer at 40 kV and 150 mA with Cu Kα radiation, a graphite monochromator, and a rotary anode. Raman spectra were recorded on a RFS/100/S Bruker Fourier transform Raman (FT-Raman) spectrometer with a 1064 nm excitation wavelength using a Nd:YAG laser in a spectral resolution of 4 cm−1. UV-vis absorption was recorded using a Cary 5G spectrometer in total reflectance mode by the integration cell.


### 2.3. Antifungal Activity

C. albicans (ATCC 90028) was grown in Sabouraud dextrose agar (SDA, Acumedia Manufacturers Inc., Baltimore, MD, USA) containing 5 μg/mL gentamicin for 48 h at 37°C, followed by 21 h at 37°C in an RPMI-1640 culture medium. Cells of the resultant culture were harvested by centrifugation at 4000 g for 5 min, washed twice with a phosphate-buffered saline solution (PBS; pH 7.2), and resuspended in the RPMI-1640 culture medium. The estimation of minimum inhibitory concentration (MIC) and minimum fungicidal concentration (MFC), using a broth microdilution assay [21], was used to evaluate the antifungal activity of the HA@Ag solution. The determination of MIC and MFC was used because it is a standard methodology for antimicrobial tests. C. albicans was incubated on a 96-well microtiter plate for 48 hours at 35°C and exposed to a serial two-fold dilution in the RPMI-1640 culture medium of the HA@Ag solution (from 1000 μg/mL to 3.90 μg/mL). The MIC value was the lowest concentration of the HA@Ag solution which resulted in no visible growth (by visual inspection). Thereafter, aliquots from each well were diluted (10−1, 10−2, 10−3, and 10−4) in PBS and inoculated on SDA (in duplicate) in order to establish the MFC. After 48 h at 37°C, the colony-forming units per milliliter (CFU/mL) were calculated, and a log10 transformation was plotted. The MFC value was defined as the lowest concentration of the HA@Ag solution resulting in 99% reduction of fungal growth (UFC/mL). The assays were performed in triplicate on three separate occasions.Additionally, the effects of the HA@Ag solution against biofilm formation ofC. albicansalso were evaluated. C. albicanssuspensions were spectrophotometrically standardized in an RPMI-1640 culture medium at 1 × 107 CFU/mL. Initially, 200 μL aliquots were placed in each well of the 96-well microtiter plates and maintained for 90 min at 37°C (adhesion phase) in an orbital shaker [5]. Then, the loosely adhered cells were removed by washing twice with 200 μL of PBS. Each one of the wells was filled with 200 μL of fresh RPMI-1640 culture medium containing different concentrations of the HA@Ag solution (from 1000 μg/mL to 3.90 μg/mL), and the plates were incubated at 37°C in an orbital shaker at 75 rpm for 48 h. After biofilm formation, the wells were carefully washed twice with 200 μL of PBS to remove nonadherent cells.The number of viableC. albicans and the total biomass of the biofilms exposed to different concentrations of the HA@Ag solution were evaluated by counting the colonies which formed units (CFU/mL) and measuring the absorbance of the crystal violet staining, respectively. To enumerate the CFU/mL, biofilms were scraped out of the wells of the 96-well microtiter plate and suspended by vigorous vortex mixing (1 min) in PBS. Thereafter, 10−1, 10−2, 10−3, and 10−4 dilutions were performed, and aliquots of 25 μL were inoculated on SDA plates (in duplicate). For the determination of the total biomass, the biofilms were fixed with methanol and stained with 1% violet crystal solution for 5 min. The stain bonded to biofilm was dissolved in acetic acid at 33% and the optical density was measured (570 nm) using a spectrophotometer (Thermo Plate—TP Reader). Data obtained from CFU/mL quantification and total biomass were statistically analyzed by ANOVA and Tukey’s post hoc tests at 5% of significance.The morphological characteristics of the biofilms formed in the presence of the HA@Ag solution also were evaluated using a field emission gun-scanning electron microscopy (FEG-SEM). For this procedure,C. albicans biofilms were cultured and exposed to different concentrations of HA@Ag solution on the bottom of a 24-well plate, as described previously. Following biofilm formation, these products were fixed with 2.5% glutaraldehyde in PBS for 24 hours, dehydrated in increasing concentrations of ethanol (70%, 85%, and 90%) for 5 min each and observed in FEG-SEM (Jeol, JSM 7500 F).


## 2.1. Materials and Synthesis

For the synthesis of HA, two aqueous solutions were prepared: a calcium nitrate tetrahydrate solution (Mallinckrodt, 99.9%) and an ammonium phosphate solution (Mallinckrodit 99.4%). The ammonium phosphate solution was then dripped into the calcium solution with constant agitation. The system was kept under flowing N2 throughout the mixing, and the pH solution was maintained at approximately 11 with the addition of ammonium hydroxide. The suspension containing the white solid precipitate was placed in a 100 mL Teflon autoclave which was sealed and loaded into the HTMW system using 2.45 GHz microwave radiation with 800 W of power. The system was heated to 140°C and maintained at this temperature for 1 minute at a heating rate of 140°C/min under constant pressure (approximately 3.0 bar). After treatment, the autoclave was naturally cooled to room temperature. The resultant product was washed with deionized water several times until a neutral pH was obtained and then dried in an oven. HA@Ag was synthesized using the previously prepared HA powder dispersed in distilled water, and the pH was adjusted to 5 with HNO3. The solution was stirred at 60°C, and then 5 mL of AgNO3 solution (1.4 × 10−2 M) was added. The precipitate was washed to pH 7 and then again dried in an oven. The working concentration was 1 mol HA : 1 mol Ag.


## 2.2. Characterization of the HA@Ag

Morphology and size characterizations were performed by transmission electron microscopy (TEM, Tecnai G2TF20, FEI). To confirm the presence of Ag, an energy dispersive X-ray (EDX) measurement was taken in the same apparatus. All measurements were taken at room temperature. HA@Ag samples were characterized by XRD using a Rigaku DMax 2500PC diffractometer at 40 kV and 150 mA with Cu Kα radiation, a graphite monochromator, and a rotary anode. Raman spectra were recorded on a RFS/100/S Bruker Fourier transform Raman (FT-Raman) spectrometer with a 1064 nm excitation wavelength using a Nd:YAG laser in a spectral resolution of 4 cm−1. UV-vis absorption was recorded using a Cary 5G spectrometer in total reflectance mode by the integration cell.


## 2.3. Antifungal Activity

C. albicans (ATCC 90028) was grown in Sabouraud dextrose agar (SDA, Acumedia Manufacturers Inc., Baltimore, MD, USA) containing 5 μg/mL gentamicin for 48 h at 37°C, followed by 21 h at 37°C in an RPMI-1640 culture medium. Cells of the resultant culture were harvested by centrifugation at 4000 g for 5 min, washed twice with a phosphate-buffered saline solution (PBS; pH 7.2), and resuspended in the RPMI-1640 culture medium. The estimation of minimum inhibitory concentration (MIC) and minimum fungicidal concentration (MFC), using a broth microdilution assay [21], was used to evaluate the antifungal activity of the HA@Ag solution. The determination of MIC and MFC was used because it is a standard methodology for antimicrobial tests. C. albicans was incubated on a 96-well microtiter plate for 48 hours at 35°C and exposed to a serial two-fold dilution in the RPMI-1640 culture medium of the HA@Ag solution (from 1000 μg/mL to 3.90 μg/mL). The MIC value was the lowest concentration of the HA@Ag solution which resulted in no visible growth (by visual inspection). Thereafter, aliquots from each well were diluted (10−1, 10−2, 10−3, and 10−4) in PBS and inoculated on SDA (in duplicate) in order to establish the MFC. After 48 h at 37°C, the colony-forming units per milliliter (CFU/mL) were calculated, and a log10 transformation was plotted. The MFC value was defined as the lowest concentration of the HA@Ag solution resulting in 99% reduction of fungal growth (UFC/mL). The assays were performed in triplicate on three separate occasions.Additionally, the effects of the HA@Ag solution against biofilm formation ofC. albicansalso were evaluated. C. albicanssuspensions were spectrophotometrically standardized in an RPMI-1640 culture medium at 1 × 107 CFU/mL. Initially, 200 μL aliquots were placed in each well of the 96-well microtiter plates and maintained for 90 min at 37°C (adhesion phase) in an orbital shaker [5]. Then, the loosely adhered cells were removed by washing twice with 200 μL of PBS. Each one of the wells was filled with 200 μL of fresh RPMI-1640 culture medium containing different concentrations of the HA@Ag solution (from 1000 μg/mL to 3.90 μg/mL), and the plates were incubated at 37°C in an orbital shaker at 75 rpm for 48 h. After biofilm formation, the wells were carefully washed twice with 200 μL of PBS to remove nonadherent cells.The number of viableC. albicans and the total biomass of the biofilms exposed to different concentrations of the HA@Ag solution were evaluated by counting the colonies which formed units (CFU/mL) and measuring the absorbance of the crystal violet staining, respectively. To enumerate the CFU/mL, biofilms were scraped out of the wells of the 96-well microtiter plate and suspended by vigorous vortex mixing (1 min) in PBS. Thereafter, 10−1, 10−2, 10−3, and 10−4 dilutions were performed, and aliquots of 25 μL were inoculated on SDA plates (in duplicate). For the determination of the total biomass, the biofilms were fixed with methanol and stained with 1% violet crystal solution for 5 min. The stain bonded to biofilm was dissolved in acetic acid at 33% and the optical density was measured (570 nm) using a spectrophotometer (Thermo Plate—TP Reader). Data obtained from CFU/mL quantification and total biomass were statistically analyzed by ANOVA and Tukey’s post hoc tests at 5% of significance.The morphological characteristics of the biofilms formed in the presence of the HA@Ag solution also were evaluated using a field emission gun-scanning electron microscopy (FEG-SEM). For this procedure,C. albicans biofilms were cultured and exposed to different concentrations of HA@Ag solution on the bottom of a 24-well plate, as described previously. Following biofilm formation, these products were fixed with 2.5% glutaraldehyde in PBS for 24 hours, dehydrated in increasing concentrations of ethanol (70%, 85%, and 90%) for 5 min each and observed in FEG-SEM (Jeol, JSM 7500 F).


## 3.  Results and Discussion

Figure1 shows TEM morphologies of pure HA and the HA@Ag synthesized under the same conditions, respectively. Figure 1 shows that there was very little difference between the two samples in particle size and morphologies. The pure HA (see Figure 1(a)) has a nanorod structure with a diameter varying from 12 to 27 nm. A closer look at a comparatively thin rod plate which provides sufficient transparency of electrons for high resolution is provided in Figure 2; a layered structure is apparent.(a) TEM image of pure HA and (b) TEM image of HA@Ag.
(a)
(b)Figure 2
(a) An EDX measurement of HA@Ag nanoparticles; (b) HRTEM image of Ag nanospheres; and (c) a zoom of a nanoparticle with (111) interplanar distance.However, silver is observed in the nanospherical morphology with an interplanar distance of 0.276 nm which corresponds to the Ag (1 1 1) plane (the preferential growth plane) (see Figure2(c)) according to the JCPDS 65–2871. The EDX spectrum of HA@Ag confirms calcium (Ca), phosphor (P), oxygen (O), and silver (Ag) in the samples (see Figure 2(a)). The presence of copper (Cu) and silicon (Si) was attributed to the sample grid support.The characterization in a long-range order of the pure HA and HA@Ag samples was performed by XRD (see Figures3(a) and 3(b), resp.). The HA single phase formation has a hexagonal structure with a P 63/m space group even with Ag. No planes related to the Ag phase were located. Secondary phases such as calcium carbonate, CaCO3, were not found in XRD results.Figure 3
XRD patterns for (a) pure HA and (b) HA@Ag sample.The HA@Ag structure in a short-range order was performed by FT-Raman analyses as a complementary structural study for XRD data. Raman spectra at room temperature in the frequency range of 400 to 1200 cm−1 for the HA@Ag powder processed in the HTMW system during 1 min are displayed in Figure 4. According to Penel et al. [22], all Raman modes are related to the HA phase. From Raman studies on carbonated apatite, two distinct wavenumbers of the ν1 carbonate mode have been suggested according to OH− or PO43- site substitution at 1108 and 1070 cm−1, respectively. Variable numbers of bands in the v1PO43- domain were also detected by the authors [22]. Since none of these characteristics were found in the Raman spectrum (see Figure 4), we conclude that the HA@Ag obtained does not present the concurrent calcium carbonate phase as a second phase which agrees with XRD results that indicate the HA single phase formation.Figure 4
FT-Raman spectra for (a) pure HA and (b) HA@Ag.A UV-vis analysis was conducted (see Figures5(a) and 5(b)) to determine the electronic structure of HA@Ag. Moreover, the GAP energy was calculated by using the Wood and Tauc method from the UV-spectra for pure HA and HA@Ag. The values obtained were 4.7 eV for pure HA and 3.6 eV for HA@Ag. There is a significant difference between band gap values for both samples. The exponential optical absorption edge and the optical band gap energy are controlled by the degree of structural disorder in the lattice. The decrease in the band gap can be attributed to defects, local bond distortion, and intrinsic surface and/or interface states (HA and Ag) which yield localized electronic levels in the forbidden band gap.UV-vis absorbance spectra for (a) pure HA and (b) HA@Ag samples.
(a)
(b)We believe that this significant difference is attributed to Ag surface defects and (HA@Ag) interface defects [23] (see Figure 6).Figure 6
Illustration of the system with the formation of a complex cluster[Ag4]d.MIC and MFC values were 62.5μg/mL and 250 μg/mL, respectively (Figure 7). These results demonstrate that the HA@Ag solution has fungistatic and fungicidal effects against the microorganism tested and thus indicate that it may be a potential candidate for developing new antimicrobial agents with multiple applications in the biomedical field. Although these MIC and MFC values against C. albicans are higher than those values obtained with commonly used antifungal agents [5] and different nanoparticles [24–26], other important aspects should be considered. First, when composites are used, the concentrations of individual nanoparticles can be decreased as well as the cytotoxicity to eukaryotic human cells [27]. Moreover, in this study, the amount of AgNO3 used was 7.10−5 mol with a Ag/HA ratio of 1. Hence, the combination of different nanoparticles could have a positive impact in avoiding the development of microbial resistance [27].Figure 7
Mean values of log10 (CFU/mL) of planktonic cultures of C. albicans exposed to HA@Ag solution. Errors bars: standard deviation. *: significant differences compared with control (0 μg/mL).Bearing in mind the biofilm architecture and its role on resistance against antimicrobial agents, it was considered important to evaluate the possible effects of the HA@Ag solution against cells and extracellular polymeric matrix. The results demonstrated that, when theC. albicans biofilms were exposed to different concentrations of the HA@Ag solution, a significant reduction in the number of CFU/mL was observed only at a concentration of 1000 μg/mL (see Figure 8). This result can be attributed to the higher resistance of C. albicans cells grown in biofilms [5, 24–26]. Although mechanisms of biofilm drug resistance are not fully understood, factors such as decreased growth rate, expression of resistance genes, and an extracellular polymeric matrix can contribute to increased tolerance of cells in biofilms [28].The biofilm matrix acts as a barrier, protecting the deep layers of cells. Recently, Ciobanu et al. [19] evaluated the effect of nanosized particles of Ag-doped HA on the first step of bacterial adherence to the inert substratum and on a 24 h preformed biofilm. These authors also observed that the inhibitory effect against biofilm formation was dependent on the concentration of the nanoparticles evaluated. Other recent studies that evaluated the effect of silver nanoparticles against C. albicans biofilms also observed a high tolerance of this fungal specie grown in biofilms when compared to planktonic cells [24–26].Figure 8
Mean values of log10 (CFU/mL) of C. albicans biofilm exposed to HA@Ag solution. Errors bars: standard deviation. *: significant difference compared with control (0 μg/mL).The results obtained after crystal violet staining showed significant decreases of the total biomass values whenC. albicans biofilms were exposed to HA@Ag solution at concentrations of 1000 μg/mL, 500 μg/mL, and 250 μg/mL (see Figure 9), showing clearly that the HA@Ag solution affected the extracellular matrix production. This result is important because biofilm formation is one of the major virulence factors of C. albicans, and its reduction makes the microorganisms more susceptible to antifungal agents and more vulnerable to host defense mechanisms. Although the biofilms matrix was reduced by the HA@Ag solution, this effect was not observed in the terms of CFU/mL. This finding suggests that the cells exhibit recovery ability after the plating, and thus, the HA@Ag solution can have a temporary and reversible effect against C. albicans biofilms. These results are in agreement with those observed in a recent study in which Ag nanoparticles were effective in reducing biofilm biomass when applied to biofilms of C. albicansandC. glabrata. However, the effect of Ag nanoparticles in the number of viable biofilm cells of C. albicans was less evident [26].Figure 9
Total biomass ofC. albicans biofilms exposed to HA@Ag solution. Errors bars: standard deviation. *: significant differences compared with control (0 μg/mL).Moreover, the results obtained also demonstrated that the total biomass values ofC. albicans biofilms exposed to concentrations of 7.82 and 3.91 μg/mL of the HA@Ag solution were significantly higher as compared with the control (0 μg/mL). It has been reported that subinhibitory concentrations of antimicrobial agents could up regulate genes related to virulence factors, such as enzyme production [29] and biofilm formation [30].FEG-SEM images confirm the quantitative outcomes obtained with biofilms (see Figure10) since alterations in cell morphology (“shriveled” cells appearance) were observed proportional to the concentration of HA@Ag nanoparticles. However, as can be seen in Figure 10, some intact cells remain even in the presence of high concentrations of nanoparticles. Micrographs with none (control) or low HA@Ag content showed more cell aggregates and higher quantity of hyphal cells. C. albicans is able to change its morphology between yeast and filamentous (hyphae and pseudohyphae) forms in a process called polymorphism. Hyphal cells are responsible for infection in the host and are able to invade tissues. These findings show that the HA@Ag solution exhibited an antifungal property against C. albicans biofilms.FEG-SEM ofC. albicans biofilms with different concentrations of the HA@Ag solution: (a) 1000, (b) 500, (c) 250, (d) 125, (e) 62.5, and (f, control) 0 μg/mL. N: HA@Ag nanoparticles, S: “shriveled” cells appearance, H: Hyphae.
(a)
(b)
(c)
(d)
(e)
(f)The performance of HA and silver is primarily dictated not only by physicochemical and mechanical properties, but also by biological activity [31]. HA is known as a biocompatible ceramic, and Ag has long been studied as an antimicrobial agent which has been successfully used in biomedical prosthesis and surgical instruments [31–35]. The antimicrobial activity of Ag can be explained in many ways. It has been reported that Ag ions can damage the bacterial outer membrane which causes cell death [34–36]. A similar mechanism seems to occur for C. albicans. Kim et al. [37] reported a potent antifungal effect of Ag nanoparticles against C. albicans with MIC values similar to amphotericin B. In this study [37], several methodologies such as flow cytometry analysis, glucose and trehalose release, plasma membrane fluorescence anisotropy, and transmission electron microscopy (TEM) were used to elucidate the mechanism of antifungal action. Membrane depolarization, the arrest of the fungal cell cycle by flow cytometry, the release of intracellular glucose and trehalose, a decrease in plasma membrane fluorescence with increasing concentrations of Ag nanoparticles, pits in the cell wall, and pores in the plasma membrane on the TEM images were observed. These findings demonstrate that Ag nanoparticles destruct the fungal membrane integrity and inhibit the normal budding process.Disorders in surfaces and interfaces occur in HA@Ag synthesized by the HTMW method and create disordered sites [38]. This fact induces restructuring at the intermediate range which results in structural and electronic alterations to both the surface and interface. Disordered sites yield a local lattice distortion that is propagated along the overall material which pushes the surrounding clusters away from their ideal positions. Thus, complex clusters (disordered clusters) must move for these properties to occur which changes the electronic distribution along the network of these polar clusters [39]. This electronic structure may dictate the biological activity and plays a major role in determining the reactivity and stability of the cluster.The mechanism of cluster complex [Ag4]• activity with oxygen essentially depends on the complex cluster with the formation of a superoxide and/or a hydroxyl radical. [Ag4]d• and [Ag4]d′ can create hydroxyl radicals (OH*) and superoxide anions (O2H*) by electron/hole reactions which can facilitate protein inactivation and eventual cell apoptosis where d = disorder and O = order.Moreover, an effective charge separation requires an electric field between the sample bulk and surface. Consequently, the effect of surface properties on electron/hole reaction performance should be considered in terms of the following:(1)[Ag4]0x+[Ag4]dx⟶[Ag4]d′+[Ag4]d•The reactivity of molecular oxygen with a complex cluster[Ag4]d• on the surface of silver oxide results in a chemisorbed species and subsequent oxygen incorporation into the lattice:
(2)[Ag4]d•+O2⟶[Ag4]d•⋯O2(ads)(3)[Ag4]d•⋯O2(ads)+[Ag4]0′⟶[Ag4]d•⋯O2(ads)′+[Ag4]0xThe clusters formed by the complex silver oxide also interact with water and split into hydroxyl radicals and hydrogen ions according to the following reactions:(4)[Ag4]•+H2O⟶[Ag4]•⋯H2O(ads)(5)[Ag4]•⋯H2O(ads)⟶[Ag4]•⋯OH*(ads)+H•Products of the partial oxidation reaction between water and a complex cluster[Ag4]d• are hydroxyl radicals, OH*, and hydrogen ions. These radicals exhibit high oxidation power which produces a microorganism mineralization in water (anodic oxidation) (5).Primary reaction (cathodic) is the formation of a superoxide species[Ag4]d•⋯O2′ (2) and (3). These species then react with H• (5) and produce the formation of hydrogen peroxide radicals (HO2*) according to the following reactions:
(6)[Ag4]d•⋯O2(ads)′+H•⟶[Ag4]d•⋯O2H(ads)*The radicals OH* and O2H* may react with the fungal cells which ultimately results in their oxidation.The nature of the superoxide or hydroxyl radicals can be described using a complex cluster model where the electron transfer from the surface to the adsorbed molecular oxygen occurs [40–42].These reaction mechanisms involve oxygen and water adsorptions that form an active complex cluster. Its decomposition, desorption of the final products, and the electron hole recombination process may have an important role in fungicidal effects.Therefore, HA@Ag was successfully obtained by maintaining the structure of HA nanorods overlapped by nanosphere Ag as confirmed by TEM images. The HA@Ag obtained shows efficient antifungal action. The results of antifungal tests can be explained by the interaction between the structure and the defect density variation in the interfacial (HA@Ag) and intrafacial (HA) region with the fungal medium which results in antifungal activity.


## 4. Conclusions

HA@Ag was successfully obtained by maintaining the HA nanorods structure overlapped by nanosphere Ag through a co-precipitation method with HTMW. The HA@Ag solution showed fungistatic and fungicidal effects againstC. albicans planktonic cells with MIC and MFC values of 62.5 μg/mL and 250 μg/mL, respectively. Additionally, the HA@Ag solution at concentrations of 1000 μg/mL, 500 μg/mL, and 250 μg/mL also exhibited antibiofilm activity, affecting mainly the extracellular matrix production. The morphological characteristics of cells were altered, and the density of hyphal cells was less noticeable in presence of the HA@Ag solution at higher concentrations. A mechanism was proposed to justify the antifungal activity by the interaction between the structure and the defect density variation in the interfacial (HA@Ag) and intrafacial (HA) region with the fungal medium.



---

*Source: 174398-2013-07-15.xml*