# Turn-On Fluorescence Detection of Glutathione Based ono-Phthaldialdehyde-Assisted SiO2 Particles

Authors: Polonca Nedeljko; Matejka Turel; Aleksandra Lobnik
Journal: Journal of Sensors
 (2018)

---

## Abstract

We report about the fluorometric method for the determination of glutathione (GSH) in dietary supplements. The fluorometric assay is based on the use of functionalized silica particles (SiO2-SH) in combination with o-phthaldialdehyde (OPA). The fluorescence excitation and emission wavelengths were located at 340 nm and 430 nm. The relative fluorescence intensity was linear in the concentration range between 1.0 × 10−7 mol/L and 1.0 × 10−5 mol/L (M) with the detection limit of 3.4 × 10−7 M. The fluorescent silica particle-based sensor was successfully employed for the determination of GSH in dietary supplements with excellent recoveries. The proposed sensor may pave a new way for fluorescence sensing of other substances in food samples.


---

## Body

## 1. Introduction

GSH is one of the body’s most powerful antioxidants that detoxifies and which is naturally produced all the time in our body [1–3]. GSH is a natural component and plays significant physiological roles in vivo, such as catching free radicals, catching toxins, and regenerating other antioxidants [1, 4–8]. A healthy adult has about 10 g of GSH circulating in the body tissues. The health benefits of GSH include increased energy, a stronger immune system, healthy liver function, and relief from chronic inflammation. On the other hand, a drop in GSH levels opens a risk for all types of degenerative diseases (Alzheimer’s, Parkinson’s, diabetes, AIDS, cancer, etc.) [2, 5, 7, 9]. A very important factor that influences the reduction of GSH is poor quality food or food that contains too little vital nutrients, such as fibers, vitamins, and minerals. Dairy products, eggs, fats, oils, most beverages, and most cereals have very little GSH [2]. In contrast, fresh fruits, vegetables, and freshly cooked meats have been confirmed to contain a high content of GSH [1, 2, 7]. Daily average GSH intake from foods ranges from 100 to 150 mg and has a major impact on human health [5, 7–9]. Research in humans led to the conclusion that high GSH levels are related to longevity and health [2, 4].Development of a simple, rapid, sensitive, and selective method for the determination of GSH in foods is of great significance for food safety and for the prevention of illness [6, 7]. So far, GSH has been determined in fruit juices, wine, tomato, cucumber, spinach, etc. [6, 7, 9–11]. Previous methods for quantitative detection of GSH include fluorescence [9, 10, 12–15], colorimetry [6–8, 13, 16–18], electrochemistry [11, 19, 20], and high-performance liquid chromatography [21, 22]. Among the various analytical methods, fluorescence sensing is the most appealing due to its generally nondestructive character, high sensitivity, specificity, ease of use, and its wide range of material sources including quantum dots (QDs) [6, 7, 9, 10, 12, 23], Au particles [16, 17, 24, 25], Ag particles [8], MnO2 nanosheets [18], and Co nanomaterials [13].For instance, Chen et al. designed a new-style dual-emission ratiometric fluorescent probe (CdSe@SiO2@CdTe) for visual assay of GSH in real vegetable and fruit samples, which has the advantages of an excellent linear concentration range from 1.0 × 10−7 to 1.0 × 10−5 M with a low detection limit of 4.2 × 10−8 M [6]. Another research based on the use of quantum dots is the work of researchers Jin et al. who developed ZnS hybrid quantum dot system (MPA-Mn:ZnS) for GSH detection. Their system reached a wide linear range of 3.0 × 10−7–2.8 × 10−4 M with a detection limit of 9.7 × 10−8 M. The developed method was applied for the detection of GSH in food, wine, and biological samples [7]. Detsri and Seeharaj reported about a sensitive and selective colorimetric sensing platform for the detection of GSH in dietary supplements by phthalic acid- (PTA-) assisted synthesis of silver nanoparticles (AgNPs). AgNPs stabilized with PTA could cause a strong affinity to GSH. The proposed colorimetric sensor exhibited a linear response in the range of 1.0 × 10−10–1.0 × 10−7 M, with a low detection limit of 0.16 × 10−10 M [8]. Xu et al. reported about a g-CNQDs-Hg2+ system for the selective sensing of GSH in various kinds of food samples. The initial fluorescence from g-CNQDs was quenched by Hg2+ with an electron transfer process. The limit of detection of 3.7 × 10−8 for GSH was achieved with a wide range of 1.6 × 10−7–1.6 × 10−5 M [9]. A fluorescent assay to determine GSH in foods and biological fluids has been successfully used by researchers Wang et al. They provided a broad linear range (1.0 × 10−7–1.0 × 10−4 M) and a detection limit of 7.3 × 10−8 M without any complex modification on CuInS2 QDs [10]. An overview of the previous work based on optical determination of GSH using different nanoparticles is summarized in Table 1.Table 1
Comparison of the analytical performance of the sensing system for the detection of GSH.
Measurement mode
Materials
Indicator
Linear range (M)
LOD (M)
λex/λem (nm)time (min)
Ref.
Fluorescence
CdSe@SiO2@CdTe
-Hg2+
1.0 × 10−7–1.0 × 10−5
4.2 × 10−8
380/61915–20
[6]
Phosphorescence
MPA-Mn:Zn QDs
KMnO4
3.0 × 10−7–2.8 × 10−4
9.7 × 10−8
316/59015–20
[7]
Absorbance
AgNPs
PTA
1.0 × 10−10–1.0 × 10−7
1.6 × 10−10
420/−5
[8]
Fluorescence
g-CNQDs-Hg2+
-Hg2+
1.6 × 10−7–1.6 × 10−5
3.7 × 10−8
365/4655
[9]
Fluorescence
CuInS2 QDs
CuInS2
1.0 × 10−7–1.0 × 10−4
7.3 × 10−8
415/6063–5
[10]
Fluorescence
SiO2-SH-OPA
OPA
1.0 × 10−7–1.0 × 10−5
3.4 × 10−7
340/44120
This studyHerein, we present for the first time a fluorescent probe based ono-phthaldialdehyde-assisted SiO2 particles for GSH determination with a “turn-on” strategy. The advantage of using our system is that our mercaptofunctionalized silica particles are biocompatible and nontoxic [26, 27] and suitable for determining GSH in biological and food samples. Similar nontoxic properties have gold materials [16, 17, 24, 25], but these systems are much more expensive than silica.


## 2. Materials and Methods

### 2.1. Chemicals

o-Phthaldialdehyde (OPA, 99%), sodium hydroxide (NaOH, 97%), methanol (MeOH, 99%), 2-propanol (2-PRO, 99.5%), ethanol (EtOH, abs), l-glutathione reduced (GSH, >98%), l-homocysteine (HCY, ≥98%), l-cysteine (CYS, 97%), magnesium nitrate hexahydrate (Mg(NO3)2 × 6H2O, puriss p.a.), calcium carbonate (CaCO3, 98%), citric acid (C6H8O7, 99%), and zinc chloride (ZnCl2, puriss p.a.) were obtained from Sigma-Aldrich. Sodium carbonate (Na2CO3, 99%), sodium bicarbonate (NaHCO3, 99%), monopotassium phosphate (KH2PO4, 99%), potassium chloride (KCl), and ascorbic acid (C6H8O6, 99%) were obtained from Sigma-Aldrich (Riedel-de Haën). Tetraethyl orthosilicate (TEOS, 99%) and 3-mercaptopropyltrimethoxysilane (MPTMS, 95%) were obtained from Sigma-Aldrich. Sodium acetate (C2H3NaO2, 99%) and ammonium hydroxide (NH4OH, 25%) were obtained from Fluka. L-Glutamine (GLU, ≥99%) and glycine (GLY, ≥99%) were from ReagentPlus®. Copper (Cu) was obtained from J.T. Baker and iron (Fe, 99%) was obtained from ACROS Organics. All the reagents and solvents used were of analytical grade and were used without further purification. Dietary supplement L-glutathione was from ZeinPharma through VitalAbo Handels GmbH, and liposomal glutathione Lipolife was from A FORM Lte.


### 2.2. Preparation of Functionalized SiO2 Particles and Conjugation of o-Phthaldialdehyde Indicator Dye (OPA) onto the SiO2-SH Particles

The preparation of functionalized particles and the OPA indicator dye conjugation to functionalized SiO2-SH silica particles was based on a reported method [28]. Briefly, mercaptofunctionalized SiO2 particles (SiO2-SH) were prepared via the Stöber synthesis, which involved the hydrolysis and cocondensation of tetraethoxysilane (TEOS) and 3-mercaptopropyltrimethoxysilane (MPTMS) precursors in an alcoholic mixture consisting of 2-propanol, methanol, and ethanol, according to reactive conditions. The reaction was performed under alkaline conditions in the presence of ammonia as a catalyst. The conjugation of the OPA indicator dye molecules onto the prepared SiO2-SH was prepared according to previous reports [28]. To 10 mg of the prepared SiO2-SH particles were added 4.5 mL of ethanol, 200 μL of preprepared OPA alcohol solutions with concentrations of OPA 7.2 × 10−1 M, and 0.3 mL Na2CO3/NaHCO3 buffer solution (pH = 10); the suspension was then stirred all together for 1 h. After stirring at room temperature, the suspension was centrifuged several times at 6500 rpm for 15 min in order to remove all the unbounded indicator dye.


### 2.3. Preparation of Standard Solutions

Theo-phthaldialdehyde stock solution and buffers of pH 6–10, 12, and 13 were prepared as described previously [29]. The stock standard solution of GSH (1.0 × 10−2 M) was prepared by dissolving salts in deionized water (DW) and was stored at 4 degrees Celsius. Lower GSH concentrations were prepared daily by further dilution with DW. GSH is a protein. It is a tripeptide, which means that it consists of three amino acids, namely, cysteine (CYS), glutamine (GLU), and glycine (GLY) (Figure 1). The solutions of amino acids were prepared in order to exclude these acids as interfering species in the developed assay. The standard stock solutions of GLU, GLY, and CYS were prepared as 1.0 × 10−1 M solutions dissolved in DW. Lower concentrations were prepared by further dilutions with DW.Figure 1
Formation of glutathione.


### 2.4. Preparation of Real Sample Solutions

Two dietary supplements containing GSH, namely glutathione powder (P1) and liposomal glutathione (P2) were provided (Figures2(a) and 2(b)). The preparation of P1 was carried out by taking 2 capsules, each contained 250 mg of GSH. Both capsules were dissolved in 0.25 L of DW, corresponding to concentration of 6.51 × 10−3 M. The preparation of P2 was done by dissolving 5 mL of liposomal GSH in 0.5 L of DW to give a stock solution with a concentration 2.93 × 10−3 M. From the stock solutions of P1 and P2, the working solutions of 1.0 × 10−4 M concentrations were prepared using DW. Compared to P1, P2 did not dissolve completely.Figure 2
Selection of dietary supplements: (a) GSH dietary supplement—capsules (P1), (b) GSH dietary supplement—liposomes (P2), (c) protein—iso mix (Pro1), (d) protein premium whey (Pro2), and (e) protein whey concentrate (Pro3).
(a)
(b)
(c)
(d)
(e)The second set of real sample solutions were prepared from protein dietary supplements, which contained the three amino acids GLU, GLY, and CYS, which are the building blocks of glutathione. Three different proteins were used (iso mix, premium, and concentrate; Figures2(c)–2(e)). Considering that GLU appears in greater proportion in all three proteins, the concentrations of the prepared protein solutions were calculated depending on the GLU content in proteins. Protein Pro1 (iso mix) was prepared by dissolving 30 g of Pro1 in 0.5 L of DW. The quantity of GSH in 30 grams is 7.0 g, which means that the GLU concentration of Pro1 in 0.5 L is 9.58 × 10−2 M. Protein Pro2 (premium whey) was prepared by dissolving 28 g of Pro2 in 0.5 L. The quantity of GSH in 28 grams is 3.1 g, which means that the GLU concentration in 0.5 L is 4.24 × 10−2 M. Protein Pro3 (whey concentrate) was prepared by dissolving 30 g of Pro3 in 0.5 L of DW. The quantity of GSH in 30 grams is 5.58 g, which means that the concentration of the prepared GLU solution is 7.64 × 10−2 M. It should be noted that these are theoretical concentration values that can deviate from real values. This is because even during the preparation of solutions, the proteins did not completely dissolve since fine particles were visible at the bottom of the flasks. All the prepared solutions were filtered through the filter paper MN 640 w · 125 mm (Macherey-Nagel) before preparing other concentrations. From each individually prepared protein solution, a theoretical concentration of 1.0 × 10−2 M was prepared, which was used in further experiments.


### 2.5. Determination of Glutathione Using Standard Solutions

The procedure for the determination of GSH is as follows: 0.05 mL of aqueous suspension of SiO2-SH-OPA particles (2 mg of SiO2-SH-OPA particles per mL) was diluted in 1 mL of buffer solution (pH 13). In order to obtain the final concentration of GSH in the concentration range between 5.0 × 10−8 M and 1.0 × 10−5 M, various volumes of an aqueous solution of GSH were added. Finally, deionized H2O was added until the final volume of 5 mL was reached. Working solutions were left to incubate for 20 min before measurements. Fluorescence emission of the SiO2-SH-OPA particles in the presence of GSH was recorded at room temperature at the excitation wavelength of 340 nm. The same procedure was used to determine the amino acids.


### 2.6. Determination of Glutathione in Real Samples

In the case of the determination of GSH in dietary supplements (P1), the standard addition method was used. The known constant concentration of dietary supplement P1 solutions (1.0 × 10−5 mol/L) was spiked with a series of different standards of GSH solutions (1.0 × 10−6, 3.0 × 10−6, 5.0 × 10−6, 8.0 × 10−6, and 1.0 × 10−5 M). Theoretically, this means that the concentration of P1 in the final volume (5 mL) was 1.0 × 10−6 M.The aim here was also to determine amino acids (as GSH building blocks) in protein samples. Firstly, a calibration curve was prepared from the standard GLU solutions which serve to read the concentration of GLU in the unknown sample. The protein samples containing theoretical concentrations of GLU (2.0 × 10−7, 1.0 × 10−6, and 1.8 × 10−6 M) were prepared.


### 2.7. Characterization

SiO2-SH particles were prepared according to [26]. The size and morphology of SiO2-SH were characterized with transmission electron microscopy (TEM) and scanning electron microscopy (SEM).Figure3(a) shows SEM images of SiO2 particles and Figure 3(b) shows TEM images of SiO2 particles. Both samples were prepared at the molar ratio between the water and the precursor R=40. From both Figures 3(a) and 3(b), it can be seen that SiO2 particles were monodispersed, spherical in shape, and with a narrow particle size distribution (500 ± 19 nm). No agglomeration of SiO2 particles was observed.Figure 3
The size and morphology of the samples: (a) SEM SiO2 particles, (b) TEM SiO2 particles, and (c) TEM SiO2-SH particles (P=2); R=40.
(a)
(b)
(c)Figure3(c) shows TEM images of SiO2-SH particles. The average particle size of the prepared SiO2-SH samples depends on the concentration of the MPTMS precursor. The optimal molar ratio between TEOS and MPTMS precursors was P=2, while the molar ratio between the water and the precursor was R=40. The prepared SiO2-SH particles were monodispersed and spherical in shape. The specific surface area and porosity (volume, diameter) of SiO2-SH particles were determined using the gas adsorption method (BET). The nitrogen adsorption results showed that SiO2-SH particles (P=2: 1, R=40) had a BET specific surface area of 4.77 m2 g−1 and a pore volume of 0.040 cm3 g−1. No agglomeration of SiO2-SH particles was observed.


## 2.1. Chemicals

o-Phthaldialdehyde (OPA, 99%), sodium hydroxide (NaOH, 97%), methanol (MeOH, 99%), 2-propanol (2-PRO, 99.5%), ethanol (EtOH, abs), l-glutathione reduced (GSH, >98%), l-homocysteine (HCY, ≥98%), l-cysteine (CYS, 97%), magnesium nitrate hexahydrate (Mg(NO3)2 × 6H2O, puriss p.a.), calcium carbonate (CaCO3, 98%), citric acid (C6H8O7, 99%), and zinc chloride (ZnCl2, puriss p.a.) were obtained from Sigma-Aldrich. Sodium carbonate (Na2CO3, 99%), sodium bicarbonate (NaHCO3, 99%), monopotassium phosphate (KH2PO4, 99%), potassium chloride (KCl), and ascorbic acid (C6H8O6, 99%) were obtained from Sigma-Aldrich (Riedel-de Haën). Tetraethyl orthosilicate (TEOS, 99%) and 3-mercaptopropyltrimethoxysilane (MPTMS, 95%) were obtained from Sigma-Aldrich. Sodium acetate (C2H3NaO2, 99%) and ammonium hydroxide (NH4OH, 25%) were obtained from Fluka. L-Glutamine (GLU, ≥99%) and glycine (GLY, ≥99%) were from ReagentPlus®. Copper (Cu) was obtained from J.T. Baker and iron (Fe, 99%) was obtained from ACROS Organics. All the reagents and solvents used were of analytical grade and were used without further purification. Dietary supplement L-glutathione was from ZeinPharma through VitalAbo Handels GmbH, and liposomal glutathione Lipolife was from A FORM Lte.


## 2.2. Preparation of Functionalized SiO2 Particles and Conjugation of o-Phthaldialdehyde Indicator Dye (OPA) onto the SiO2-SH Particles

The preparation of functionalized particles and the OPA indicator dye conjugation to functionalized SiO2-SH silica particles was based on a reported method [28]. Briefly, mercaptofunctionalized SiO2 particles (SiO2-SH) were prepared via the Stöber synthesis, which involved the hydrolysis and cocondensation of tetraethoxysilane (TEOS) and 3-mercaptopropyltrimethoxysilane (MPTMS) precursors in an alcoholic mixture consisting of 2-propanol, methanol, and ethanol, according to reactive conditions. The reaction was performed under alkaline conditions in the presence of ammonia as a catalyst. The conjugation of the OPA indicator dye molecules onto the prepared SiO2-SH was prepared according to previous reports [28]. To 10 mg of the prepared SiO2-SH particles were added 4.5 mL of ethanol, 200 μL of preprepared OPA alcohol solutions with concentrations of OPA 7.2 × 10−1 M, and 0.3 mL Na2CO3/NaHCO3 buffer solution (pH = 10); the suspension was then stirred all together for 1 h. After stirring at room temperature, the suspension was centrifuged several times at 6500 rpm for 15 min in order to remove all the unbounded indicator dye.


## 2.3. Preparation of Standard Solutions

Theo-phthaldialdehyde stock solution and buffers of pH 6–10, 12, and 13 were prepared as described previously [29]. The stock standard solution of GSH (1.0 × 10−2 M) was prepared by dissolving salts in deionized water (DW) and was stored at 4 degrees Celsius. Lower GSH concentrations were prepared daily by further dilution with DW. GSH is a protein. It is a tripeptide, which means that it consists of three amino acids, namely, cysteine (CYS), glutamine (GLU), and glycine (GLY) (Figure 1). The solutions of amino acids were prepared in order to exclude these acids as interfering species in the developed assay. The standard stock solutions of GLU, GLY, and CYS were prepared as 1.0 × 10−1 M solutions dissolved in DW. Lower concentrations were prepared by further dilutions with DW.Figure 1
Formation of glutathione.


## 2.4. Preparation of Real Sample Solutions

Two dietary supplements containing GSH, namely glutathione powder (P1) and liposomal glutathione (P2) were provided (Figures2(a) and 2(b)). The preparation of P1 was carried out by taking 2 capsules, each contained 250 mg of GSH. Both capsules were dissolved in 0.25 L of DW, corresponding to concentration of 6.51 × 10−3 M. The preparation of P2 was done by dissolving 5 mL of liposomal GSH in 0.5 L of DW to give a stock solution with a concentration 2.93 × 10−3 M. From the stock solutions of P1 and P2, the working solutions of 1.0 × 10−4 M concentrations were prepared using DW. Compared to P1, P2 did not dissolve completely.Figure 2
Selection of dietary supplements: (a) GSH dietary supplement—capsules (P1), (b) GSH dietary supplement—liposomes (P2), (c) protein—iso mix (Pro1), (d) protein premium whey (Pro2), and (e) protein whey concentrate (Pro3).
(a)
(b)
(c)
(d)
(e)The second set of real sample solutions were prepared from protein dietary supplements, which contained the three amino acids GLU, GLY, and CYS, which are the building blocks of glutathione. Three different proteins were used (iso mix, premium, and concentrate; Figures2(c)–2(e)). Considering that GLU appears in greater proportion in all three proteins, the concentrations of the prepared protein solutions were calculated depending on the GLU content in proteins. Protein Pro1 (iso mix) was prepared by dissolving 30 g of Pro1 in 0.5 L of DW. The quantity of GSH in 30 grams is 7.0 g, which means that the GLU concentration of Pro1 in 0.5 L is 9.58 × 10−2 M. Protein Pro2 (premium whey) was prepared by dissolving 28 g of Pro2 in 0.5 L. The quantity of GSH in 28 grams is 3.1 g, which means that the GLU concentration in 0.5 L is 4.24 × 10−2 M. Protein Pro3 (whey concentrate) was prepared by dissolving 30 g of Pro3 in 0.5 L of DW. The quantity of GSH in 30 grams is 5.58 g, which means that the concentration of the prepared GLU solution is 7.64 × 10−2 M. It should be noted that these are theoretical concentration values that can deviate from real values. This is because even during the preparation of solutions, the proteins did not completely dissolve since fine particles were visible at the bottom of the flasks. All the prepared solutions were filtered through the filter paper MN 640 w · 125 mm (Macherey-Nagel) before preparing other concentrations. From each individually prepared protein solution, a theoretical concentration of 1.0 × 10−2 M was prepared, which was used in further experiments.


## 2.5. Determination of Glutathione Using Standard Solutions

The procedure for the determination of GSH is as follows: 0.05 mL of aqueous suspension of SiO2-SH-OPA particles (2 mg of SiO2-SH-OPA particles per mL) was diluted in 1 mL of buffer solution (pH 13). In order to obtain the final concentration of GSH in the concentration range between 5.0 × 10−8 M and 1.0 × 10−5 M, various volumes of an aqueous solution of GSH were added. Finally, deionized H2O was added until the final volume of 5 mL was reached. Working solutions were left to incubate for 20 min before measurements. Fluorescence emission of the SiO2-SH-OPA particles in the presence of GSH was recorded at room temperature at the excitation wavelength of 340 nm. The same procedure was used to determine the amino acids.


## 2.6. Determination of Glutathione in Real Samples

In the case of the determination of GSH in dietary supplements (P1), the standard addition method was used. The known constant concentration of dietary supplement P1 solutions (1.0 × 10−5 mol/L) was spiked with a series of different standards of GSH solutions (1.0 × 10−6, 3.0 × 10−6, 5.0 × 10−6, 8.0 × 10−6, and 1.0 × 10−5 M). Theoretically, this means that the concentration of P1 in the final volume (5 mL) was 1.0 × 10−6 M.The aim here was also to determine amino acids (as GSH building blocks) in protein samples. Firstly, a calibration curve was prepared from the standard GLU solutions which serve to read the concentration of GLU in the unknown sample. The protein samples containing theoretical concentrations of GLU (2.0 × 10−7, 1.0 × 10−6, and 1.8 × 10−6 M) were prepared.


## 2.7. Characterization

SiO2-SH particles were prepared according to [26]. The size and morphology of SiO2-SH were characterized with transmission electron microscopy (TEM) and scanning electron microscopy (SEM).Figure3(a) shows SEM images of SiO2 particles and Figure 3(b) shows TEM images of SiO2 particles. Both samples were prepared at the molar ratio between the water and the precursor R=40. From both Figures 3(a) and 3(b), it can be seen that SiO2 particles were monodispersed, spherical in shape, and with a narrow particle size distribution (500 ± 19 nm). No agglomeration of SiO2 particles was observed.Figure 3
The size and morphology of the samples: (a) SEM SiO2 particles, (b) TEM SiO2 particles, and (c) TEM SiO2-SH particles (P=2); R=40.
(a)
(b)
(c)Figure3(c) shows TEM images of SiO2-SH particles. The average particle size of the prepared SiO2-SH samples depends on the concentration of the MPTMS precursor. The optimal molar ratio between TEOS and MPTMS precursors was P=2, while the molar ratio between the water and the precursor was R=40. The prepared SiO2-SH particles were monodispersed and spherical in shape. The specific surface area and porosity (volume, diameter) of SiO2-SH particles were determined using the gas adsorption method (BET). The nitrogen adsorption results showed that SiO2-SH particles (P=2: 1, R=40) had a BET specific surface area of 4.77 m2 g−1 and a pore volume of 0.040 cm3 g−1. No agglomeration of SiO2-SH particles was observed.


## 3. Results and Discussion

### 3.1. Optimization of the Sensing Conditions of SiO2-SH-OPA Particles in the Presence of GSH

In order to achieve the superior performance of the SiO2-SH-OPA probe, a series of tests was carried out, including spectral properties, effect of pH, quantity of particles, response time, sensitivity, and standard addition method. The basic principle for the determination of GSH is that the SiO2-SH-OPA particles, which are nonfluorescent, form a fluorescent product when binding to glutathione; the reaction is formed between the OPA carboxyl group and the thiol group of GSH. However, in our case, the SiO2-SH-OPA particles themselves do show some small starting fluorescent signal—their own fluorescence. After the addition of higher concentrations of GSH, the fluorescence emission of the formed product SiO2-SH-OPA-GSH increases proportionally, which can be seen from Figure 4(a). The emission spectra of the SiO2-SH-OPA-GSH fluorescent product (FP) were measured at a maximum emission peak of 430 nm, while the excitation wavelength was 340 nm. The emission intensity was measured after 20 minutes, at pH 13 and at room temperature. The concentration range for the determination of the response of SiO2-SH-OPA particles in the presence of GSH was from 5.0 × 10−8 to 1.0 × 10−5 M. The influence of pH on the fluorescence intensity of SiO2-SH-OPA-GSH FP was investigated with constant GSH concentration (1.0 × 10−3 M). Figure 4(b) shows the curves obtained at different pH values varying from 4 to 13. From the figure, it can be seen that the system does not react at the acidic pH. It is slightly responsive in the neutral range, while in the alkaline range the steepness of the fluorescence signal rises to pH 13. When the pH is low, GSH is protonated (thiol form) and thus not nucleophilic enough to compete with the much more abundant water molecules. At high pH conditions, GSH is almost entirely present in its highly nucleophilic thiolate form (GS−) and attacks the C=O group of the quinone (OPA) by nucleophilic addition, whereby a rigid structure is formed, which is fluorescent. pH 13 was finally selected for the optimum pH for further determination of GSH. The fluorescence intensity of the SiO2-SH-OPA-GSH FP is influenced by the quantity of OPA-conjugated particles (Figure 4(c)). The concentration of the added GSH was constant (1.0 × 10−3 M), but the added volumes of the prepared SiO2-SH-OPA particles were changed (20 μL, 50 μL, 80 μL, and 100 μL). It turned out that the florescence intensity of SiO2-SH-OPA-GSH FP is greatest when 50 qL of particles are used. For this reason, 50 μL of particles were used throughout the study. The case wherein a larger quantity of SiO2-SH-OPA particles (>50 qL) was added resulted in a cloudy sample and in a decrease in the emission intensity.Figure 4
(a) Emission spectra of SiO2-SH-OPA particles in the absence (blank) and presence of GSH. (b) Influence of pH on SiO2-SH-OPA FP. (c) Influence of the quantity of SiO2-SH-OPA particles. (d) Response time. Experimental conditions: (GSH) = 5.0 × 10−8–1.0 × 10−5 mol/L; λex/λem=340/431nm.
(a)
(b)
(c)
(d)In addition to the abovementioned factors (pH influence, particle size, and higher concentration of GSH), the fluorescence intensity also depends on the reaction time at which the SiO2-SH-OPA-GSH FP reaches the maximum emission peak (Figure 4(d)). The response time of the FP formation was recorded at different time intervals (immediately and after 5, 10, 15, and 20 minutes). The concentration of the added GSH was constant (1.0 × 10−3 M). It was discovered that 50% of the fluorescence intensity increase is developed within the first 5 minutes, whereas the other 50% is developed between 5 and 20 min. Finally, 20 min of incubation time was chosen as the optimal for the GSH determination.


### 3.2. Validation of the Method

The concentration range for the fluorescent determination of GSH was from 5.0 × 10−8 M to 1.0 × 10−5 M. As can be seen from Figure 5, the fluorescence intensity of SiO2-SH-OPA-GSH FP increased linearly with the addition of increasing GSH concentrations from 1.0 × 10−7 M to 1.0 × 10−5 M.Figure 5
Experimental conditions: (GSH) = 5.0 × 10−8–1.0 × 10−5 M; λex/λem=340/431nm, pH = 13, 20 min, n=3.In Figure5, the linear regression equation of the calibration curve is expressed as y=1.41+891204.55x, with a correlation coefficient (R2) of 0.9954. The LOD for GSH detection was found to be 3.4 × 10−7 M. Compared with other reported research works [6–10] for optical GSH determination, the present fluorescent method shows a comparable response.Under optimized conditions, the accuracy and precision of the presented fluorescent assay were evaluated. Table2 summarized the mean values, recovery, relative standard deviation (RSD), and accuracy of the proposed method. The repeatability was assessed using three replicates for each working samples’ concentrations in a single day. Different amounts of standard GSH solutions (1.0 × 10−6, 3.0 × 10−6, 5.0 × 10−6, 8.0 × 10−6, and 1.0 × 10−5 M) were added. The percent recoveries of GSH in diluted samples of pure standard GSH solution, were between 94.0% and 107.0%, satisfying the quantitative analysis in the solution samples. The data presented in Table 2 show satisfactory validation parameters.Table 2
Determination of GSH (standard) by the reported fluorescence method.
Sample
Added (μM)
Founda (μM)
Recovery (%,n=3)
RSDb (%, n=3)
Accuracyc (%, n=3)
GSH standard solution
1.0
1.05 ± 0.06
105.0
6.13
5.00
3.0
3.21 ± 0.12
107.0
3.74
7.00
5.0
5.40 ± 0.26
108.0
4.88
8.00
8.0
7.52 ± 0.28
94.0
3.69
−6.00
10.0
9.69 ± 0.28
96.9
2.88
−3.10
aMean ± standard deviation (n=3). bRSD (%) was calculated from standarddeviation/mean×100. cAccuracy was calculated from foundconcentration–knownconcentration/knownconcentration×100.In comparison to other developed optical probes for the determination of GSH in food samples (Table1), we can conclude that the SiO2-SH-OPA probe shows a comparable concentration range of GSH determination, except in the case of AgNPs. With AgNPs, the linear range and the limit of GSH detection are lower by about three orders of magnitude. However, the LOD is a little higher in the case of SiO2-SH-OPA than that determined by other probes. The time needed for the analysis is comparable. The advantage of the silica particles developed within this study is that these particles are biocompatible and nontoxic and more affordable than gold nanoparticles.


### 3.3. Selectivity of SiO2-SH-OPA

The selectivity of the proposed method for the optical detection of GSH was evaluated using interfering agents, including common amino acids (GLU, GLY, CYS, and HCYS), dietary supplements (P1 and P2), and cations and acids, commonly found in foods (Na+, K+, Mg2+, Ca2+, Cu2+, Fe3+, Zn2+, ascorbic acid, and citric acid). The monitored amino acids were taken because three of them (GLU, GLY, and CYS) represent the basic elements of GSH. In addition to the amino acids, homocysteine was also chosen because it contains a thiol group such as GSH itself. The results shown in Figure 6 show that a marked change in the fluorescence intensity appear in the presence of the standard GSH solution. The second highest fluorescent response was developed in the presence of the dietary supplement P1, while a much lower fluorescence intensity was recorded in the presence of P2. Similarly, a low fluorescence intensity is given by amino acids (GLU, GLY, CYS, and HCYS). Cations and acids, commonly found in foods, were not influenced by the determination of GSH. Compared to the standard GSH solution, the fluorescence intensity of P1 is lower for about 36.7%, while the fluorescence intensity of P2 is lower for about 74.4%. Based on these findings, we continued research with the dietary supplement P1. The proposed method is suitable for determining GSH and it shows good selectivity towards amino acids.Figure 6
Fluorescence intensity of SiO2-SH-OPA particles in the presence of GSH species: standard solution (GSH), dietary supplements (P1), dietary supplements (P2), glutamine (GLU), glycine (GLY), cysteine (CYS), homocysteine (HCYS), and cations and acids, commonly found in foods (Na+, K+, Mg2+, Ca2+, ascorbic acid, and citric acid). Experimental conditions: (GSH, P1, P2, Glu, Gly, Cys, Hcys, Na+, K+, Mg2+, Ca2+, ascorbic acid, citric acid) = 1.0 × 10−5 M; λex/λem=340/431nm, pH 13, 20 min.


### 3.4. Determination of GSH in Dietary Supplements

Preparation of the dietary supplement solution was carried out according to the procedure (standard addition method) described in Section2.3. As already mentioned, it turned out that the response of the SiO2-SH-OPA particles in the presence of P1 is higher than in the case of P2. The lower response of P2 is attributed to the fact that P2 was less soluble during the preparation of its basic solutions, and it did not also dissolve completely. To further validate the fluorescent determination of GSH, a standard addition method with P1 was carried out. Furthermore, we conducted a recovery test by spiking a series of different standard GSH solutions (1.0 × 10−6, 3.0 × 10−6, 5.0 × 10−6, 8.0 × 10−6, and 1.0 × 10−5 M) to ensure the accuracy of the sample test. Recoveries of the known spiked amounts of GSH in dietary supplement P1 were between 85.5% and 97.3% with RSD between 0.55% and 4.78% (Table 3).Table 3
Analytical results for the determination of GSH in dietary supplement P1 using the proposed fluorescent method.
Found in sample P1 (μM)
Standard added GSH (μM)
Total founda (μM)
Recovery (%,n=3)
RSDb (%, n=3)
Accuracyc (%)
1.2
1.0
1.88 ± 0.09
85.5
4.78
−14.5
3.0
3.89 ± 0.15
92.6
3.76
−7.4
5.0
5.91 ± 0.06
95.3
1.01
−4.7
8.0
8.92 ± 0.15
96.9
1.68
−3.1
10.0
10.9 ± 0.06
97.3
0.55
−2.7
aMean ± standard deviation (n=3). bRSD (%) was calculated from standard deviation/mean × 100, cAccuracy was calculated from [(found concentration – known concentration)/known concentration] × 100.As an additional confirmation of the stability of the SiO2-SH-OPA particles for the GSH determination and selectivity against amino acids, a time drive experiment was conducted and the results are shown in Figure 7.Figure 7
Fluorescence intensity versus time of SiO2-SH-OPA particles in the presence of standard GSH solution, dietary supplement P1, and amino acid standard solutions (GLU, CYS, and GLY). Experimental conditions: (GSH, P1, GLU, CYS, and GLY) = 8.0 × 10−6 M; λex/λem=340/431nm, pH 13.It is evident from Figure7 that the fluorescence signal of SiO2-SH-OPA is increasing in the presence of the GSH analyte (present in standard solutions and in P1) whereas the fluorescence intensity in the presence of GLU, GLY, and CYS remains constant over time. OPA-assisted SiO2 particles (SiO2-SH-OPA) have shown high selectivity toward GSH and P1 and could be used as a selective fluorometric method.


## 3.1. Optimization of the Sensing Conditions of SiO2-SH-OPA Particles in the Presence of GSH

In order to achieve the superior performance of the SiO2-SH-OPA probe, a series of tests was carried out, including spectral properties, effect of pH, quantity of particles, response time, sensitivity, and standard addition method. The basic principle for the determination of GSH is that the SiO2-SH-OPA particles, which are nonfluorescent, form a fluorescent product when binding to glutathione; the reaction is formed between the OPA carboxyl group and the thiol group of GSH. However, in our case, the SiO2-SH-OPA particles themselves do show some small starting fluorescent signal—their own fluorescence. After the addition of higher concentrations of GSH, the fluorescence emission of the formed product SiO2-SH-OPA-GSH increases proportionally, which can be seen from Figure 4(a). The emission spectra of the SiO2-SH-OPA-GSH fluorescent product (FP) were measured at a maximum emission peak of 430 nm, while the excitation wavelength was 340 nm. The emission intensity was measured after 20 minutes, at pH 13 and at room temperature. The concentration range for the determination of the response of SiO2-SH-OPA particles in the presence of GSH was from 5.0 × 10−8 to 1.0 × 10−5 M. The influence of pH on the fluorescence intensity of SiO2-SH-OPA-GSH FP was investigated with constant GSH concentration (1.0 × 10−3 M). Figure 4(b) shows the curves obtained at different pH values varying from 4 to 13. From the figure, it can be seen that the system does not react at the acidic pH. It is slightly responsive in the neutral range, while in the alkaline range the steepness of the fluorescence signal rises to pH 13. When the pH is low, GSH is protonated (thiol form) and thus not nucleophilic enough to compete with the much more abundant water molecules. At high pH conditions, GSH is almost entirely present in its highly nucleophilic thiolate form (GS−) and attacks the C=O group of the quinone (OPA) by nucleophilic addition, whereby a rigid structure is formed, which is fluorescent. pH 13 was finally selected for the optimum pH for further determination of GSH. The fluorescence intensity of the SiO2-SH-OPA-GSH FP is influenced by the quantity of OPA-conjugated particles (Figure 4(c)). The concentration of the added GSH was constant (1.0 × 10−3 M), but the added volumes of the prepared SiO2-SH-OPA particles were changed (20 μL, 50 μL, 80 μL, and 100 μL). It turned out that the florescence intensity of SiO2-SH-OPA-GSH FP is greatest when 50 qL of particles are used. For this reason, 50 μL of particles were used throughout the study. The case wherein a larger quantity of SiO2-SH-OPA particles (>50 qL) was added resulted in a cloudy sample and in a decrease in the emission intensity.Figure 4
(a) Emission spectra of SiO2-SH-OPA particles in the absence (blank) and presence of GSH. (b) Influence of pH on SiO2-SH-OPA FP. (c) Influence of the quantity of SiO2-SH-OPA particles. (d) Response time. Experimental conditions: (GSH) = 5.0 × 10−8–1.0 × 10−5 mol/L; λex/λem=340/431nm.
(a)
(b)
(c)
(d)In addition to the abovementioned factors (pH influence, particle size, and higher concentration of GSH), the fluorescence intensity also depends on the reaction time at which the SiO2-SH-OPA-GSH FP reaches the maximum emission peak (Figure 4(d)). The response time of the FP formation was recorded at different time intervals (immediately and after 5, 10, 15, and 20 minutes). The concentration of the added GSH was constant (1.0 × 10−3 M). It was discovered that 50% of the fluorescence intensity increase is developed within the first 5 minutes, whereas the other 50% is developed between 5 and 20 min. Finally, 20 min of incubation time was chosen as the optimal for the GSH determination.


## 3.2. Validation of the Method

The concentration range for the fluorescent determination of GSH was from 5.0 × 10−8 M to 1.0 × 10−5 M. As can be seen from Figure 5, the fluorescence intensity of SiO2-SH-OPA-GSH FP increased linearly with the addition of increasing GSH concentrations from 1.0 × 10−7 M to 1.0 × 10−5 M.Figure 5
Experimental conditions: (GSH) = 5.0 × 10−8–1.0 × 10−5 M; λex/λem=340/431nm, pH = 13, 20 min, n=3.In Figure5, the linear regression equation of the calibration curve is expressed as y=1.41+891204.55x, with a correlation coefficient (R2) of 0.9954. The LOD for GSH detection was found to be 3.4 × 10−7 M. Compared with other reported research works [6–10] for optical GSH determination, the present fluorescent method shows a comparable response.Under optimized conditions, the accuracy and precision of the presented fluorescent assay were evaluated. Table2 summarized the mean values, recovery, relative standard deviation (RSD), and accuracy of the proposed method. The repeatability was assessed using three replicates for each working samples’ concentrations in a single day. Different amounts of standard GSH solutions (1.0 × 10−6, 3.0 × 10−6, 5.0 × 10−6, 8.0 × 10−6, and 1.0 × 10−5 M) were added. The percent recoveries of GSH in diluted samples of pure standard GSH solution, were between 94.0% and 107.0%, satisfying the quantitative analysis in the solution samples. The data presented in Table 2 show satisfactory validation parameters.Table 2
Determination of GSH (standard) by the reported fluorescence method.
Sample
Added (μM)
Founda (μM)
Recovery (%,n=3)
RSDb (%, n=3)
Accuracyc (%, n=3)
GSH standard solution
1.0
1.05 ± 0.06
105.0
6.13
5.00
3.0
3.21 ± 0.12
107.0
3.74
7.00
5.0
5.40 ± 0.26
108.0
4.88
8.00
8.0
7.52 ± 0.28
94.0
3.69
−6.00
10.0
9.69 ± 0.28
96.9
2.88
−3.10
aMean ± standard deviation (n=3). bRSD (%) was calculated from standarddeviation/mean×100. cAccuracy was calculated from foundconcentration–knownconcentration/knownconcentration×100.In comparison to other developed optical probes for the determination of GSH in food samples (Table1), we can conclude that the SiO2-SH-OPA probe shows a comparable concentration range of GSH determination, except in the case of AgNPs. With AgNPs, the linear range and the limit of GSH detection are lower by about three orders of magnitude. However, the LOD is a little higher in the case of SiO2-SH-OPA than that determined by other probes. The time needed for the analysis is comparable. The advantage of the silica particles developed within this study is that these particles are biocompatible and nontoxic and more affordable than gold nanoparticles.


## 3.3. Selectivity of SiO2-SH-OPA

The selectivity of the proposed method for the optical detection of GSH was evaluated using interfering agents, including common amino acids (GLU, GLY, CYS, and HCYS), dietary supplements (P1 and P2), and cations and acids, commonly found in foods (Na+, K+, Mg2+, Ca2+, Cu2+, Fe3+, Zn2+, ascorbic acid, and citric acid). The monitored amino acids were taken because three of them (GLU, GLY, and CYS) represent the basic elements of GSH. In addition to the amino acids, homocysteine was also chosen because it contains a thiol group such as GSH itself. The results shown in Figure 6 show that a marked change in the fluorescence intensity appear in the presence of the standard GSH solution. The second highest fluorescent response was developed in the presence of the dietary supplement P1, while a much lower fluorescence intensity was recorded in the presence of P2. Similarly, a low fluorescence intensity is given by amino acids (GLU, GLY, CYS, and HCYS). Cations and acids, commonly found in foods, were not influenced by the determination of GSH. Compared to the standard GSH solution, the fluorescence intensity of P1 is lower for about 36.7%, while the fluorescence intensity of P2 is lower for about 74.4%. Based on these findings, we continued research with the dietary supplement P1. The proposed method is suitable for determining GSH and it shows good selectivity towards amino acids.Figure 6
Fluorescence intensity of SiO2-SH-OPA particles in the presence of GSH species: standard solution (GSH), dietary supplements (P1), dietary supplements (P2), glutamine (GLU), glycine (GLY), cysteine (CYS), homocysteine (HCYS), and cations and acids, commonly found in foods (Na+, K+, Mg2+, Ca2+, ascorbic acid, and citric acid). Experimental conditions: (GSH, P1, P2, Glu, Gly, Cys, Hcys, Na+, K+, Mg2+, Ca2+, ascorbic acid, citric acid) = 1.0 × 10−5 M; λex/λem=340/431nm, pH 13, 20 min.


## 3.4. Determination of GSH in Dietary Supplements

Preparation of the dietary supplement solution was carried out according to the procedure (standard addition method) described in Section2.3. As already mentioned, it turned out that the response of the SiO2-SH-OPA particles in the presence of P1 is higher than in the case of P2. The lower response of P2 is attributed to the fact that P2 was less soluble during the preparation of its basic solutions, and it did not also dissolve completely. To further validate the fluorescent determination of GSH, a standard addition method with P1 was carried out. Furthermore, we conducted a recovery test by spiking a series of different standard GSH solutions (1.0 × 10−6, 3.0 × 10−6, 5.0 × 10−6, 8.0 × 10−6, and 1.0 × 10−5 M) to ensure the accuracy of the sample test. Recoveries of the known spiked amounts of GSH in dietary supplement P1 were between 85.5% and 97.3% with RSD between 0.55% and 4.78% (Table 3).Table 3
Analytical results for the determination of GSH in dietary supplement P1 using the proposed fluorescent method.
Found in sample P1 (μM)
Standard added GSH (μM)
Total founda (μM)
Recovery (%,n=3)
RSDb (%, n=3)
Accuracyc (%)
1.2
1.0
1.88 ± 0.09
85.5
4.78
−14.5
3.0
3.89 ± 0.15
92.6
3.76
−7.4
5.0
5.91 ± 0.06
95.3
1.01
−4.7
8.0
8.92 ± 0.15
96.9
1.68
−3.1
10.0
10.9 ± 0.06
97.3
0.55
−2.7
aMean ± standard deviation (n=3). bRSD (%) was calculated from standard deviation/mean × 100, cAccuracy was calculated from [(found concentration – known concentration)/known concentration] × 100.As an additional confirmation of the stability of the SiO2-SH-OPA particles for the GSH determination and selectivity against amino acids, a time drive experiment was conducted and the results are shown in Figure 7.Figure 7
Fluorescence intensity versus time of SiO2-SH-OPA particles in the presence of standard GSH solution, dietary supplement P1, and amino acid standard solutions (GLU, CYS, and GLY). Experimental conditions: (GSH, P1, GLU, CYS, and GLY) = 8.0 × 10−6 M; λex/λem=340/431nm, pH 13.It is evident from Figure7 that the fluorescence signal of SiO2-SH-OPA is increasing in the presence of the GSH analyte (present in standard solutions and in P1) whereas the fluorescence intensity in the presence of GLU, GLY, and CYS remains constant over time. OPA-assisted SiO2 particles (SiO2-SH-OPA) have shown high selectivity toward GSH and P1 and could be used as a selective fluorometric method.


## 4. Conclusions

In summary, we have successfully developed and optimized the SiO2-SH-OPA particles for the determination of GSH in dietary supplements. Such a system based on the use of silica particles has been proposed here for the first time. It shows a similar working range when compared to other developed particle-based probes, except when compared to Ag+-based nanoparticles [8]. This new type of “turn-on” fluorescence sensor for GSH based on o-phthaldialdehyde-assisted SiO2 particles has several advantages, such as easy preparation, low cost, high catalytic activity, and repeatability. However, it requires high alkaline media for optimized working conditions. Nevertheless, due to silica biocompatibility properties, the proposed sensing probe could be a promising material of use in other biological samples.



---