# Characteristics and Properties of TiO2/EP-PU Composite

Authors: Chen Yufei; Li Zhichao; Tan Junyan; Zhang Qingyu; Han Yang
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

Polymer matrix of EP-PU was prepared by epoxy resin which was polyurethane toughened, and TCA201 coupling agent was used to modify nano-TiO2, and TiO2/EP-PU composite was synthesized using EP, PU, and TCA201-TiO2. The results of SEM and TEM showed that the surface of TiO2 was coated with TCA201 coupling agent through the bonding between the hydroxyl of nano-TiO2 particle and coupling agent molecules, the interaction would be beneficial to improve compatibility of inorganic and organic phases, and TCA201-TiO2 would disperse evenly in composite and improve performance of composite materials. The mechanical properties, thermal stability, dielectric properties, and breakdown strength of composites were investigated by electronic tensile machine, TGA, dielectric spectrum, and CS2674C type voltage tester. The results indicated that appropriate amount of TCA201-TiO2 could improve mechanical properties, the shear strength of 3 wt%-TiO2/EP-PU reached the maximum value at 27.14 MPa, its thermal decomposition temperature was 397.82°C, enhanced 17.48°C more than that of EP-PU matrix, and its dielectric constant (
ε
) and dielectric loss (tan
⁡
δ) showed 4.27 and 0.02, respectively. Its breakdown field strength was 14 kV/mm. Its performance met the requirement of dielectric materials.


---

## Body

## 1. Introduction

Epoxy resin (EP) is one of the most commonly used thermosetting materials in high voltage apparatus as insulation due to its excellent mechanical, electrical properties and chemical stability. EP adhesive with excellent bonding properties is widely used in aerospace, military, electronics, construction, and many other fields [1]. The main purpose of this study was that polyurethane (PU) and inorganic nano-TiO2 are used to increase the mechanical strength, thermal stability and improve the dielectric properties of the composites. Polyurethane (PU) was used as the flexibilizer that reinforced toughness of epoxy resin, and the interfacial theory of composite materials was used to analyze the relationship between material structure and properties of composite [2]. Owing to the poor compatibility existing between the interface of organic matrix and inorganic fillers, some efforts were usually necessary to enhance the compatibility between the inorganic fillers and the polymer matrix during the preparation of hybrid materials [3]. To achieve this objective, TCA201 coupling agent is usually used to modify nano-TiO2 and the surface of modified nano-TiO2 has existed in active group (–OH, –COOH), so the relations of inorganic fillers and polymer matrix should be improved and were beneficial to interfacial energy in the formation of hybrid composites. In this research, EP-PU has existed in “island” structure; this structure is in favor of composites toughness [4]. At the same time, the performance of the composites was tested through mechanical properties, thermal stability, and dielectric properties.


## 2. Experimental

### 2.1. Materials

The chemicals used in this study such as epoxy resin (EP-51) and methyl tetrahydrophthalic anhydride (MTHPA) were industrial products and were purchased from the Lanxing New Chemical Materials Co., Ltd., China. Polyurethane (PU) was industrial products and obtained from Jindao Material Sci & Tech Co., Ltd., Beijing, China, and imidazole was industrial products and purchased from Jinyan Trading Co., Ltd., Guangzhou, China. The density of TiO2 is 0.42 g/cm3, the size of particle is 25 nm, and the melting point of TiO2 is 1830–1850°C and comes from Yicheng Jingrui New Material Co., Ltd., China. Coupling agent of titanate (TCA201) is brought from Jing Tianwei Chemical Co., Ltd., Nanjing, China. The structure of isopropyl tri(dioctylpyrophosphate) titanate (TCA201) was shown in Figure 1.Figure 1
The chemical structure of TCA201.


### 2.2. Modification of Nano-TiO2

TCA201 was dissolving in 17 mL toluene and its concentration was 2.6%. TiO2 was added into above solution until the system was evenly about 2–4 hours under 80°C and then was leached. TiO2 was 10 g.  Washing modified TiO2 solution with toluene 3-4 times and leaching, put it into the oven and let it dry for 10 hours at 80°C and get TCA201-TiO2.


### 2.3. Preparation of Material Composites

Technological process of composite materials was described as follows. A certain percentage of the EP-51 and PU were mixed at 80°C until they dispersed evenly, and a certain amount of TCA201-TiO2 powder was added into above systems. The solution was dissolving in the ultrasonic condition, cooled to 50°C, and added into MTHPA and imidazole until the system was mixed completely. The mixture was degassed to remove air bubbles and pour into preprepared molds for molding in the oven and curing temperature was 80°C for 2 hr, 120°C, 150°C, and 180°C for 1 hr, respectively.


### 2.4. Measurements

The FT-IR spectra, which were used to study the chemical structure of the polymer matrix, were performed with EQUINOX-55 Fourier transform spectrometer (GER), in the 400–4000 cm−1 range, and 5 scans were averaged for each spectrum. And it could be seen that there existed the characteristic absorption peaks of material.The fracture structures of samples were examined on the Hitachi S-4300 scanning electron microscope (SEM, Japan). Samples were deposited on a sample holder with adhesive carbon foil and sputtered with gold.The state of aggregation and morphology of nano-TiO2 were tested by JEM-2100 transmission electron microscopy (TEM, Japan), the test temperature was 18°C, and voltage was 120 kV.The FT-IR spectra, which were used to study the chemical structure of the polymer matrix, were performed with EQUINOX-55 Fourier transform spectrometer (GER), in the 400–4000 cm−1 range, and it could be seen that there existed the characteristic absorption peaks of material.The shearing strength of the composite materials was determined with CSS-44300 electronic testing machine (China) according to a native standard of GB/T7124-1986. Standard tensile shear experiments were performed at room temperature, under a speed of 5 mm/min. For each sample, at least five measurements were made, and the average value was taken.Thermogravimetric analysis (TGA), which could not only investigate the state of a material and the process of decomposition but also provide useful information about the thermal stability of material, was recorded on a Perkin-Elmer 6 series thermal analysis system. Samples were heated from 200°C to 800°C at a heating rate of 20°C/min in a nitrogen atmosphere and weight of sample was about 10–15 mg.The dielectric constant(
ε
) and dielectric loss (tan
⁡
δ) of composite materials were measured with Agilent-4294A precision impedance analyzer (Japan) in the frequency of 50 Hz at room temperature according to GB/T 1409-89.CS2674C pressure tester (GER) was used to test the breakdown strength of the composites.


## 2.1. Materials

The chemicals used in this study such as epoxy resin (EP-51) and methyl tetrahydrophthalic anhydride (MTHPA) were industrial products and were purchased from the Lanxing New Chemical Materials Co., Ltd., China. Polyurethane (PU) was industrial products and obtained from Jindao Material Sci & Tech Co., Ltd., Beijing, China, and imidazole was industrial products and purchased from Jinyan Trading Co., Ltd., Guangzhou, China. The density of TiO2 is 0.42 g/cm3, the size of particle is 25 nm, and the melting point of TiO2 is 1830–1850°C and comes from Yicheng Jingrui New Material Co., Ltd., China. Coupling agent of titanate (TCA201) is brought from Jing Tianwei Chemical Co., Ltd., Nanjing, China. The structure of isopropyl tri(dioctylpyrophosphate) titanate (TCA201) was shown in Figure 1.Figure 1
The chemical structure of TCA201.


## 2.2. Modification of Nano-TiO2

TCA201 was dissolving in 17 mL toluene and its concentration was 2.6%. TiO2 was added into above solution until the system was evenly about 2–4 hours under 80°C and then was leached. TiO2 was 10 g.  Washing modified TiO2 solution with toluene 3-4 times and leaching, put it into the oven and let it dry for 10 hours at 80°C and get TCA201-TiO2.


## 2.3. Preparation of Material Composites

Technological process of composite materials was described as follows. A certain percentage of the EP-51 and PU were mixed at 80°C until they dispersed evenly, and a certain amount of TCA201-TiO2 powder was added into above systems. The solution was dissolving in the ultrasonic condition, cooled to 50°C, and added into MTHPA and imidazole until the system was mixed completely. The mixture was degassed to remove air bubbles and pour into preprepared molds for molding in the oven and curing temperature was 80°C for 2 hr, 120°C, 150°C, and 180°C for 1 hr, respectively.


## 2.4. Measurements

The FT-IR spectra, which were used to study the chemical structure of the polymer matrix, were performed with EQUINOX-55 Fourier transform spectrometer (GER), in the 400–4000 cm−1 range, and 5 scans were averaged for each spectrum. And it could be seen that there existed the characteristic absorption peaks of material.The fracture structures of samples were examined on the Hitachi S-4300 scanning electron microscope (SEM, Japan). Samples were deposited on a sample holder with adhesive carbon foil and sputtered with gold.The state of aggregation and morphology of nano-TiO2 were tested by JEM-2100 transmission electron microscopy (TEM, Japan), the test temperature was 18°C, and voltage was 120 kV.The FT-IR spectra, which were used to study the chemical structure of the polymer matrix, were performed with EQUINOX-55 Fourier transform spectrometer (GER), in the 400–4000 cm−1 range, and it could be seen that there existed the characteristic absorption peaks of material.The shearing strength of the composite materials was determined with CSS-44300 electronic testing machine (China) according to a native standard of GB/T7124-1986. Standard tensile shear experiments were performed at room temperature, under a speed of 5 mm/min. For each sample, at least five measurements were made, and the average value was taken.Thermogravimetric analysis (TGA), which could not only investigate the state of a material and the process of decomposition but also provide useful information about the thermal stability of material, was recorded on a Perkin-Elmer 6 series thermal analysis system. Samples were heated from 200°C to 800°C at a heating rate of 20°C/min in a nitrogen atmosphere and weight of sample was about 10–15 mg.The dielectric constant(
ε
) and dielectric loss (tan
⁡
δ) of composite materials were measured with Agilent-4294A precision impedance analyzer (Japan) in the frequency of 50 Hz at room temperature according to GB/T 1409-89.CS2674C pressure tester (GER) was used to test the breakdown strength of the composites.


## 3. Results and Discussions

### 3.1. FT-IR Spectral Analysis

FT-IR spectra of nano-TiO2 were presented in Figure 2. The curves ((a) and (b)) were designated as unmodified TiO2 and TCA201-TiO2, respectively.Figure 2
FT-IR spectra of nano-TiO2.It was seen from Figure2 that the curve of TCA201-TiO2 was different from the curve of unmodified TiO2. The peak of curve (b) at 2864 cm−1 and 2934 cm−1 was due to the stretching vibration of C–H in TCA201, and the peak at 1039 cm−1 was the characteristic peak of P–O–P [5]. The peak at 1724 cm−1 was the absorption band of P–O–H, and the peak at 1464 cm−1 was the characteristic peak of P=O. It could prove that TCA201 has been grafted to the surface of TiO2. Chemical interaction of –OCH(CH3)2 in titanate coupling TCA201 and polar group for nano-TiO2 would form organic active monolayer, and this could help to facilitate two-phase action between inorganic and organic phase and improve the properties of composites.


### 3.2. Analysis of SEM Patterns

SEM was always used to analyze microscopic structure of the composite material, and the microstructures of nano-TiO2 and composites were shown in Figure 3.Figure 3
SEM photos of TiO2 and TCA201-TiO2/EP-PU composite.
(a)
(b)
(c)
(d)Figures3(a) and 3(b) show microtopography of unmodified nano-TiO2, TCA201-TiO2 and Figures 3(c) and 3(d) show fracture SEM picture of 3 wt% (TCA201-TiO2)/EP-PU and 7 wt% (TCA201-TiO2)/EP-PU, respectively. Unmodified TiO2 particles had an irregular shape but uniformly disperse. TiO2 particles were of nanoscale and the white area was relatively big, so the clusters phenomenon existed (see Figure 4(a)). The surface that TCA201-TiO2 was uniformly coated by coupling agent had relatively flat, smooth, and small spherical particles, and white areas were more dispersed in Figure 3(b). Agglomeration tendency was weakened; the interaction between the particles was reduced and uniformly dispersed. It also indicated that particle size decreased, and the surface area increased [6–8]. Figures 3(c) and 3(d) showed that the relatively flat area was EP matrix, which was continuous phase, and PU molecule had uniformly formed “island structure” in EP matrix. Inorganic particles were dispersing phase and were evenly dispersed in EP-PU matrix, and the interaction of inorganic components and PU matrix was very strong and they were distributed in PU matrix “island structure” in Figures 3(c) and 3(d), and the inorganic particles in “island structure” were of nanoscale. Nanoparticles had a larger surface area [9], and the surface of modified nanoparticles had active groups and compatibility with organic phase, to promote the mutual penetration of the two-phase interface; the interpenetration could help to improve the mechanical properties.Figure 4
TEM patterns of TCA201-TiO2.
(a)
(b)


### 3.3. Analysis of TEM Patterns

The morphology of TCA201-TiO2 was investigated by TEM in order to observe the effect of modification and verified the result of FT-IR in Figure 4.Figure4 shows the TEM images of TCA201-TiO2;  Figures 4(a) and 4(b) were magnified to 4 × 104 times and 8 × 104 times,  respectively. In the picture, it would be seen that TCA201-TiO2 dispersed evenly, and the particle size was in the nanosized and modified nano-TiO2 uniformly connected at both ends of the coupling agent, which demonstrated that the interaction of the active group in TiO2 molecular and the active group in TCA201 was existing. The interaction could be intermolecular cross-linking, inhibit reuniting of TiO2, and improve the interaction of two phases, titanate made the epoxy resin and nano-TiO2 surface connection strengthen, and organic functional groups of titanate and the epoxy resin should produce chemical bonding, so the nano-TiO2 well dispersed in an epoxy resin and TCA201-TiO2 could greatly improve and enhance their overall performance. Transmission electron microscopy showed how nano-TiO2 and TCA201 connected.


### 3.4. Mechanical Properties

The diagram of the shear strength of TCA201-TiO2/EP-PU composite was shown in Figure 5.Figure 5
Shear strength curve of TCA201-TiO2/EP-PU.With the increase of TCA201-TiO2 filler, the shear strength of the composites gradually increased and then declined. The shear strength of 3 wt% TCA201-TiO2/EP-PU composite was the maximum value for 27.14 MPa. The content of TCA201-TiO2 was more than 3 wt% and the shear strength of composite materials decreased but still was higher than that of pure polymer matrix EP-PU.Generally, TCA201-TiO2 modified by coupling agent was not simply physically blending with polymer matrix. TCA201-TiO2 and polymer matrix could form chemical bonds through coupling agent; as the surface of TCA201-TiO2 has existed in much active groups, these groups could improve fracture energy and adhesive strength of the composites [10]. The structure of coupling agent had two kinds of functional group; one was active group and the other was nonactive group; this structure would play the role of a bridge which associated with the nano-TiO2 and the epoxy matrix. The function enhanced the interfacial adhesion and consumed more energy; thereby mechanical properties of composites were improved [11].Nanoparticles had large specific surface area and high superficial energy; it could help to improve interactions with epoxy matrix. When the content of nanoparticles was more excessive, the interactions of inorganic particles could be enhanced, but the interactions of polymer matrix and inorganic component would weaken, and inorganic TiO2 would be reunion and the dispersion of two phases would be much difficult. The phenomenon of agglomeration occurred, which resulted in stress concentration point, and the mechanical properties of composites could decrease, but the shear strength of composites was still higher than that of pure epoxy resin matrix [12, 13].


### 3.5. Heat Resistance Properties

Thermal degradation behaviors of composites were evaluated by thermogravimetric analysis (TGA). TGA curves of composite materials were shown in Figure6. The results demonstrated that T
d of TCA201-TiO2/EP-PU was firstly increased and then decreased with the increase of TCA201-TiO2 doping. When the amount of TCA201-TiO2 was 3 wt%, T
d that reached up to 397.82°C was higher 17.48°C than that of pure materials. The main reasons were that firstly heat resistance of inorganic TCA201-TiO2 was stronger and to increase its content in the polymer matrix was bound to enhancing the heat resistance of the composite. Secondly, there were active groups in the TCA201-TiO2 particles structure, and there were a large number of hydroxyl groups in the organic phase; the two kinds of active groups could have contact with cross-linking agent and exist in strong interactions. This interaction enhanced fracture energy of composites and became beneficial to the heat resistant properties of composite [14, 15]. Thirdly, inorganic TCA201-TiO2 particles possessed a large specific surface area, contacting area of organic matrix was larger, and there were nanoeffects. So the thermal stability of composites is enhanced. Fourthly, when the content of inorganic component was excessive, the interaction forces of inorganic particles would be enhanced and dispersion of two phases weakened and easily led to agglomeration in the epoxy resin.Figure 6
TG curve of TCA201-TiO2/EP-PU.Figure7 shows SEM patterns for the breakdown point of 7 wt% TCA201-TiO2/EP-PU. Figures 7(a), 7(b), and 7(c) show back breakdown point of composite and Figure 7(d) shows face breakdown point of composite.Figure 7
SEM of TCA201-TiO2/EP-PU breakdown point.
(a)
(b)
(c)
(d)It was seen that a large number of inorganic components were separated (in Figures7(a), 7(b), and 7(c)). This was because electrical energy would transform into heat energy in the breakdown processing; the heat energy caused epoxy resin matrix to decompose and inorganic component of composite was separated [16, 17]. And the heat energy of back breakdown could not spread rapidly; therefore, it would produce thermal loss. The produced heat energy during face breakdown of composite radiated its heat away into space and could not make two-phase inorganic and organic component separate in Figure 7(d).


### 3.6. Dielectric Properties

Figure8 shows the dielectric constant and dielectric loss curve of TCA201-TiO2/EP-PU composites. It was noted that dielectric constant of TCA201-TiO2/EP-PU increased with the increasing of amount of TCA201-TiO2. As polar functional groups increased, it would result in the degree of polarization of the composite material to enhance and led to the increase of the dielectric constant eventually. At the same time, because nano-TiO2 particles in epoxy resin had a good surface effect, other polarization also could occur in the two-phase interface of composite and led to increasing the degree of polarization of the composite [18].Figure 8
Dielectric constant and dielectric loss curves of TCA201-TiO2/EP-PU.Dielectric loss(
tan
⁡
δ
) curve in Figure 8 displayed that tan
⁡
δ increased, too, with the increase of TCA201-TiO2 filler. There could be two reasons; one was electrical conductivity loss of polar functional groups and the other was the relaxation loss of the polar functional groups. From the above analysis, conclusions were obtained that the polar functional groups of the composite materials were driven by electric field strength to generate strong polarization. And the content of TCA201-TiO2 in composite increased and the number of the conductive carriers increased, too. Under the influence of an external electric field, it made the carrier bring about the directional movement phenomenon of the heat loss of dielectric material, ultimately.


### 3.7. Breakdown Field Strength

Breakdown strength of insulating material generally generates thermal breakdown and electrical breakdown at the breakdown point, and simultaneously electric energy was changed to thermal energy, so breakdown phenomenon would happen and the composite is destroyed. Though the modified nanoparticles and the organic polymer could be compatible well, and there were certain defects between the inorganic phase and the organic phase interface. It was seen in Figure9 that the breakdown field strength of TCA201-TiO2/EP-PU composite was reduced with the content of TCA201-TiO2. Because insulating materials might release heat and convert part of the electrical energy into heat under an external electric field, the dielectric loss happened and the energy was lost. Therefore, the increase of dielectric loss gave the media issue more heat and enhanced temperature, which would break the balance of heating and cooling. In addition, TiO2 had the semiconductor, so the conductivity of composites improved rapidly with the increase of temperature. This resulted in the decline of material breakdown strength [19].Figure 9
Breakdown strength curve of TCA201-TiO2/EP-PU.It would aggravate the second reunion of nanoparticles in the composite curing process, which caused deformities of the electric field and made the temperature at test point of the local area slightly higher than the others. And this part of heat could not be well distributed out and make the thermal breakdown occur in this region. Secondly, there were some compatibility issues between the two-phase interfaces when inorganic particles and the epoxy matrix were mixed, at which some tiny bubbles and trap appeared in composite materials, and the defects also increased with the increase of TiO2. These factors brought about the decline of breakdown field strength of composite material. Breakdown field strength of 3 wt%-TCA201-TiO2/EP-PU composite was 14 kV/mm; it met the requirement of insulating material.


## 3.1. FT-IR Spectral Analysis

FT-IR spectra of nano-TiO2 were presented in Figure 2. The curves ((a) and (b)) were designated as unmodified TiO2 and TCA201-TiO2, respectively.Figure 2
FT-IR spectra of nano-TiO2.It was seen from Figure2 that the curve of TCA201-TiO2 was different from the curve of unmodified TiO2. The peak of curve (b) at 2864 cm−1 and 2934 cm−1 was due to the stretching vibration of C–H in TCA201, and the peak at 1039 cm−1 was the characteristic peak of P–O–P [5]. The peak at 1724 cm−1 was the absorption band of P–O–H, and the peak at 1464 cm−1 was the characteristic peak of P=O. It could prove that TCA201 has been grafted to the surface of TiO2. Chemical interaction of –OCH(CH3)2 in titanate coupling TCA201 and polar group for nano-TiO2 would form organic active monolayer, and this could help to facilitate two-phase action between inorganic and organic phase and improve the properties of composites.


## 3.2. Analysis of SEM Patterns

SEM was always used to analyze microscopic structure of the composite material, and the microstructures of nano-TiO2 and composites were shown in Figure 3.Figure 3
SEM photos of TiO2 and TCA201-TiO2/EP-PU composite.
(a)
(b)
(c)
(d)Figures3(a) and 3(b) show microtopography of unmodified nano-TiO2, TCA201-TiO2 and Figures 3(c) and 3(d) show fracture SEM picture of 3 wt% (TCA201-TiO2)/EP-PU and 7 wt% (TCA201-TiO2)/EP-PU, respectively. Unmodified TiO2 particles had an irregular shape but uniformly disperse. TiO2 particles were of nanoscale and the white area was relatively big, so the clusters phenomenon existed (see Figure 4(a)). The surface that TCA201-TiO2 was uniformly coated by coupling agent had relatively flat, smooth, and small spherical particles, and white areas were more dispersed in Figure 3(b). Agglomeration tendency was weakened; the interaction between the particles was reduced and uniformly dispersed. It also indicated that particle size decreased, and the surface area increased [6–8]. Figures 3(c) and 3(d) showed that the relatively flat area was EP matrix, which was continuous phase, and PU molecule had uniformly formed “island structure” in EP matrix. Inorganic particles were dispersing phase and were evenly dispersed in EP-PU matrix, and the interaction of inorganic components and PU matrix was very strong and they were distributed in PU matrix “island structure” in Figures 3(c) and 3(d), and the inorganic particles in “island structure” were of nanoscale. Nanoparticles had a larger surface area [9], and the surface of modified nanoparticles had active groups and compatibility with organic phase, to promote the mutual penetration of the two-phase interface; the interpenetration could help to improve the mechanical properties.Figure 4
TEM patterns of TCA201-TiO2.
(a)
(b)


## 3.3. Analysis of TEM Patterns

The morphology of TCA201-TiO2 was investigated by TEM in order to observe the effect of modification and verified the result of FT-IR in Figure 4.Figure4 shows the TEM images of TCA201-TiO2;  Figures 4(a) and 4(b) were magnified to 4 × 104 times and 8 × 104 times,  respectively. In the picture, it would be seen that TCA201-TiO2 dispersed evenly, and the particle size was in the nanosized and modified nano-TiO2 uniformly connected at both ends of the coupling agent, which demonstrated that the interaction of the active group in TiO2 molecular and the active group in TCA201 was existing. The interaction could be intermolecular cross-linking, inhibit reuniting of TiO2, and improve the interaction of two phases, titanate made the epoxy resin and nano-TiO2 surface connection strengthen, and organic functional groups of titanate and the epoxy resin should produce chemical bonding, so the nano-TiO2 well dispersed in an epoxy resin and TCA201-TiO2 could greatly improve and enhance their overall performance. Transmission electron microscopy showed how nano-TiO2 and TCA201 connected.


## 3.4. Mechanical Properties

The diagram of the shear strength of TCA201-TiO2/EP-PU composite was shown in Figure 5.Figure 5
Shear strength curve of TCA201-TiO2/EP-PU.With the increase of TCA201-TiO2 filler, the shear strength of the composites gradually increased and then declined. The shear strength of 3 wt% TCA201-TiO2/EP-PU composite was the maximum value for 27.14 MPa. The content of TCA201-TiO2 was more than 3 wt% and the shear strength of composite materials decreased but still was higher than that of pure polymer matrix EP-PU.Generally, TCA201-TiO2 modified by coupling agent was not simply physically blending with polymer matrix. TCA201-TiO2 and polymer matrix could form chemical bonds through coupling agent; as the surface of TCA201-TiO2 has existed in much active groups, these groups could improve fracture energy and adhesive strength of the composites [10]. The structure of coupling agent had two kinds of functional group; one was active group and the other was nonactive group; this structure would play the role of a bridge which associated with the nano-TiO2 and the epoxy matrix. The function enhanced the interfacial adhesion and consumed more energy; thereby mechanical properties of composites were improved [11].Nanoparticles had large specific surface area and high superficial energy; it could help to improve interactions with epoxy matrix. When the content of nanoparticles was more excessive, the interactions of inorganic particles could be enhanced, but the interactions of polymer matrix and inorganic component would weaken, and inorganic TiO2 would be reunion and the dispersion of two phases would be much difficult. The phenomenon of agglomeration occurred, which resulted in stress concentration point, and the mechanical properties of composites could decrease, but the shear strength of composites was still higher than that of pure epoxy resin matrix [12, 13].


## 3.5. Heat Resistance Properties

Thermal degradation behaviors of composites were evaluated by thermogravimetric analysis (TGA). TGA curves of composite materials were shown in Figure6. The results demonstrated that T
d of TCA201-TiO2/EP-PU was firstly increased and then decreased with the increase of TCA201-TiO2 doping. When the amount of TCA201-TiO2 was 3 wt%, T
d that reached up to 397.82°C was higher 17.48°C than that of pure materials. The main reasons were that firstly heat resistance of inorganic TCA201-TiO2 was stronger and to increase its content in the polymer matrix was bound to enhancing the heat resistance of the composite. Secondly, there were active groups in the TCA201-TiO2 particles structure, and there were a large number of hydroxyl groups in the organic phase; the two kinds of active groups could have contact with cross-linking agent and exist in strong interactions. This interaction enhanced fracture energy of composites and became beneficial to the heat resistant properties of composite [14, 15]. Thirdly, inorganic TCA201-TiO2 particles possessed a large specific surface area, contacting area of organic matrix was larger, and there were nanoeffects. So the thermal stability of composites is enhanced. Fourthly, when the content of inorganic component was excessive, the interaction forces of inorganic particles would be enhanced and dispersion of two phases weakened and easily led to agglomeration in the epoxy resin.Figure 6
TG curve of TCA201-TiO2/EP-PU.Figure7 shows SEM patterns for the breakdown point of 7 wt% TCA201-TiO2/EP-PU. Figures 7(a), 7(b), and 7(c) show back breakdown point of composite and Figure 7(d) shows face breakdown point of composite.Figure 7
SEM of TCA201-TiO2/EP-PU breakdown point.
(a)
(b)
(c)
(d)It was seen that a large number of inorganic components were separated (in Figures7(a), 7(b), and 7(c)). This was because electrical energy would transform into heat energy in the breakdown processing; the heat energy caused epoxy resin matrix to decompose and inorganic component of composite was separated [16, 17]. And the heat energy of back breakdown could not spread rapidly; therefore, it would produce thermal loss. The produced heat energy during face breakdown of composite radiated its heat away into space and could not make two-phase inorganic and organic component separate in Figure 7(d).


## 3.6. Dielectric Properties

Figure8 shows the dielectric constant and dielectric loss curve of TCA201-TiO2/EP-PU composites. It was noted that dielectric constant of TCA201-TiO2/EP-PU increased with the increasing of amount of TCA201-TiO2. As polar functional groups increased, it would result in the degree of polarization of the composite material to enhance and led to the increase of the dielectric constant eventually. At the same time, because nano-TiO2 particles in epoxy resin had a good surface effect, other polarization also could occur in the two-phase interface of composite and led to increasing the degree of polarization of the composite [18].Figure 8
Dielectric constant and dielectric loss curves of TCA201-TiO2/EP-PU.Dielectric loss(
tan
⁡
δ
) curve in Figure 8 displayed that tan
⁡
δ increased, too, with the increase of TCA201-TiO2 filler. There could be two reasons; one was electrical conductivity loss of polar functional groups and the other was the relaxation loss of the polar functional groups. From the above analysis, conclusions were obtained that the polar functional groups of the composite materials were driven by electric field strength to generate strong polarization. And the content of TCA201-TiO2 in composite increased and the number of the conductive carriers increased, too. Under the influence of an external electric field, it made the carrier bring about the directional movement phenomenon of the heat loss of dielectric material, ultimately.


## 3.7. Breakdown Field Strength

Breakdown strength of insulating material generally generates thermal breakdown and electrical breakdown at the breakdown point, and simultaneously electric energy was changed to thermal energy, so breakdown phenomenon would happen and the composite is destroyed. Though the modified nanoparticles and the organic polymer could be compatible well, and there were certain defects between the inorganic phase and the organic phase interface. It was seen in Figure9 that the breakdown field strength of TCA201-TiO2/EP-PU composite was reduced with the content of TCA201-TiO2. Because insulating materials might release heat and convert part of the electrical energy into heat under an external electric field, the dielectric loss happened and the energy was lost. Therefore, the increase of dielectric loss gave the media issue more heat and enhanced temperature, which would break the balance of heating and cooling. In addition, TiO2 had the semiconductor, so the conductivity of composites improved rapidly with the increase of temperature. This resulted in the decline of material breakdown strength [19].Figure 9
Breakdown strength curve of TCA201-TiO2/EP-PU.It would aggravate the second reunion of nanoparticles in the composite curing process, which caused deformities of the electric field and made the temperature at test point of the local area slightly higher than the others. And this part of heat could not be well distributed out and make the thermal breakdown occur in this region. Secondly, there were some compatibility issues between the two-phase interfaces when inorganic particles and the epoxy matrix were mixed, at which some tiny bubbles and trap appeared in composite materials, and the defects also increased with the increase of TiO2. These factors brought about the decline of breakdown field strength of composite material. Breakdown field strength of 3 wt%-TCA201-TiO2/EP-PU composite was 14 kV/mm; it met the requirement of insulating material.


## 4. Conclusions

The results of FT-IR, TEM, and SEM demonstrated that TCA201 coupling agent had connected with TiO2 particle through chemical cross-linking, and TCA201-TiO2 could disperse well in EP-PU matrix. This would improve the properties of composite. When the amount of TCA201-TiO2 was 3 wt%, shear strength gained maximum value for 27.14 MPa, the thermal decomposition temperature reached up to 397.82°C, which was higher 17.48°C than pure polymer matrix, breakdown field strength of composite was 14 kV/mm, and the performances could meet the requirement of insulating material.



---